Direct positive image forming method

Abstract: A direct positive image forming method compris­ ing development processing an imagewise exposed direct positive photographic light-sensitive material which comprises a support having thereon at least one layer containing internal latent image type silver halide grains not having been previously fogged after fogging treatment or while fogging treatment, wherein the fogging treatment is conducted in the presence of a compound represented by the following general formula (I): wherein A₁ and A₂ both represent a hydrogen atom or one of A₁ and A₂ represents a hydrogen atom and the other represents a sulfonyl group or an acyl group; G₁ represents a carbonyl group, a sulfonyl group, a sulfoxy group, or an iminomethylene group; L₁ represents a divalent linkage group; X₁ represents -O- or (wherein R₄ represents a hydrogen atom, an alkyl group or an aryl group); Y₁ represents and R₂ each represents an aliphatic group, an aromatic group, a heterocyclic group, OR₅ or -NR₅R₆ (wherein R₅ represents an aliphatic group, an aromatic group or a heterocyclic group; and R₆ represents a hydrogen atom, an aliphatic group, an aromatic group or a heterocyclic group); and R₃ represents a hydrogen atom, an alkyl group, an aryl group, an alkoxy group, an aralkyl group, an aryloxy group or an amino group. In accordance with the method of the present invention direct positive images having a high maximum image density and a low minimum image density and being stable even when preserved under high temperature and high humidity conditions.

Description: The present invention relates to a direct positive image forming method comprising development processing a direct positive photographic light-sensitive material which comprises a support having thereon at least one layer containing internal latent image type silver halide grains not have been previously fogged after fogging treatment or while fogging treatment, and more particularly to a direct positive image forming method which can provide a sufficiently hign D max even upon development processing at a low pH. It is well known that an internal latent image type silver halide emulsion not having been previously fogged is imagewise exposed to light and then subjected to surface development either after fogging treatment or while fogging treatment to obtain a direct positive image. The term "internal latent image type silver halide photographic emulsion" used herein means a silver halide photographic emulsion of the type in which sensitivity specks are predominantly present in the interior of silver halide grains and a latent image is predominantly formed in the interior of the grains by exposure to light. Various techniques in this field of technology, such as those described, for example, in U.S. Patents 2,592,250, 2,466,957, 2,497,875, 2,588,982, 3,317,322, 3,61,266, 3,761,275, and 3,796,577, British Patents 1,151,363, 1,150,553, and 1,011,062 are known. According to these conventional techniques, photographic light-sensitive materials providing a direct positive image with relatively high sensitivity can be produced. For the details of the direct positive image formation mechanism, reference can be made to, for example, T.H. James, The Theory of the Photographic Process , 4th. Ed., Ch. 7, pp. 182 to 193 and U.S. Patent 3,761,276. It is believed that a direct positive image is formed through the following mechanism: First, imagewise exposure results in the formation of an internal latent image in the interior of silver halide grains, which leads to the formation of fog centers selectively on the surface of the unexposed silver halide grains by surface desensitization based on the internal latent image, and subsequent conventional surface development processing results in formation of a photographic image (a direct positive image) on the unexposed area. Selective formation of fog centers described above can be generally effected by a "light fogging method" in which the entire surface of a light-sensitive layer is secondarily exposed to light as described, for example, in British Patent 1,151,363 or a "chemical fogging method" using a nucleating agent as described, for example, in Research Disclosure , Vol. 151, No. 15162 (November, 1976), pp. 76 to 78. Hydrazine compounds are well known as nucleating agents which are employed in the above-described "chemical fogging method". As another type of nucleating agents, heterocyclic quaternary ammonium salts are known and described, for example, in U.S. Patents 3,615,615, 3,719,494, 3,734,738, 3,759,901, 3,854,956, 4,094,683 and 4,306,016, British Patent 1,283,835, JP-A-52-3426, and JP-A-52 69613 (the term "JP-A" as used herein means an "unexamined published Japanese patent application"). In general, the above described hydrazine type nucleating agents are most excellent in view of discrimination since they provide a large difference between maximum density (Dmax) and minimum density (Dmin). However, they are disadvantageous because they require processing at a high pH (pH>12). As nucleating agents which function in processing at a low pH (pH≦12), heterocyclic quaternary ammonium salts as described above are known. Particularly, propargyl- or butynyl-substituted heterocyclic quaternary ammonium salt compounds as described in U.S. Patent 4,115,122 are excellent nucleating agents in view of discrimination when used in direct positive silver halide emulsions. However, in silver halide emulsions, sensitizing dyes are employed for the purpose of spectral sensitization. In such cases, competitive adsorption of the sensitizing dyes and the heterocyclic quaternary ammonium type nucleating agents onto silver halide grains takes place, and thus, it is necessary to add a large amount of the quaternary ammonium salt type nucleating agents which are of low adsorptivity. In particular, in the case of multilayer color photographic light-sensitive materials, unevenness of density and destroy of color balance may undesirably occur. Therefore, these compounds are still insufficient. Further, these tendencies become more remarkable upon preservation of the photographic material under high temperature and high humidity conditions. In order to solve the above described problems, quaternary salt type nucleating agents having an AgX adsorption accelerating thioamido group are disclosed in U.S. Patent 4,471,044. Although the amount to be added which is necessary to obtain a sufficiently high Dmax is reduced and the decrease in Dmax during preservation at high temperature is controlled by introduction of the adsorptive group, these effects still do not achieve a fully satisfactory level. It is, therefore, the object of the present invention to provide a direct positive image forming method and a direct positive photographic light-sensitive material which provides a high maximum image density and a low minimum image density and which forms stable direct positive images even when they are preserved under high temperature and/or high humidity conditions. This object of the present invention is accomplished with a direct positive image forming method comprising development processing an imagewise exposed direct positive photographic light-sensitive material which comprises a support having thereon at least one layer containing internal latent image type silver halide grains not having been previously fogged after fogging treatment or while fogging treatment, wherein the fogging treatment is conducted in the presence of a compound represented by the following general formula (I): wherein A₁ and A₂ both represent a hydrogen atom or one of A₁ and A₂ represents a hydrogen atom and the other represents a sulfonyl group or an acyl group; G₁ represents a carbonyl group, a sulfonyl group, a sulfoxy group, or an iminomethylene group; L₁ represents a divalent linkage group; X₁ represents -O- or (wherein R₄ represents a hydrogen atom, an alkyl group or an aryl group); Y₁ represents R₁ and R₂ each represents an aliphatic group, an aromatic group, a heterocyclic group, -OR₅ or -NR₅R₆ (wherein R₅ represents an aliphatic group, an aromatic group or a heterocyclic group; and R₆ represents a hydrogen atom, an aliphatic group, an aromatic group or a heterocyclic group); and R₃ represents a hydrogen atom, an alkyl group, an aryl group, an alkoxy group, an aralkyl group, an aryloxy group or an amino group which groups may be substituted. The present invention also provides a direct positive photographic light-sensitive material comprising a support having thereon at least one internal latent image type silver halide emulsion layer not having been previously fogged wherein the photographic light-sensitive materia contains at least one compound represented by the above general formula (I). The present invention is based on the fact that highly active hydrazines which can not be expected from the information hitherto known are obtained by introducing the -Y₁-X₁- group into their molecules as described in the general formula (I). Now, the compound represented by the general formula (I) is described in detail below. In the general formula (I), A₁ and A₂ both represent a hydrogen atom or one of them represents a hydrogen atom and the other represents an alkylsulfonyl group having not more than 20 carbon atoms, an arylsulfonyl group having not more than 20 carbon atoms (preferably a phenylsulfonyl group or a phenylsulfonyl group substituted so that the sum of the Hammett's substituent constants becomes at least -0.5), or an acyl group having not more than 20 carbon atoms (preferably a benzoyl group, a substituted benzoyl group so that the sum of the Hammett's substituent constants becomes at least -0.5), or a straight chain, branched chain or cyclic, unsubstituted or substituted aliphatic acyl group (wherein the substituent can be selected from, for example, a halogen atom, an ether group, a sulfonamido group, a carbonamido group, a hydroxyl group, a carboxyl and a sulfonic acid group). Most preferably, both A₁ and A₂ represent simultaneously hydrogen atoms. The aliphatic group represented by R1 or R₂ includes a straight chain, branched chain or cyclic alkyl group, alkenyl group or alkynyl group and each containing preferably from 1 to 30 carbon atoms, particularly from 1 to 20 carbon atoms. The branched chain alkyl group may contain one or more hetero atoms therein to form a saturated hetero ring. Specific examples of the aliphatic group include a methyl group, a tert-butyl group, an n-octyl group, a tert-octyl group, a cyclohexyl group, a hexenyl group, a pyrrolidyl group, a tetrahydrofuryl group and an n-dodecyl group. The aromatic group represented by R₁ or R₂ includes a monocyclic or dicyclic aryl group, for example, a phenyl group or a naphthyl group. The heterocyclic group represented by R₁ or R₂ includes a 3-membered to 10-membered saturated or unsaturated heterocyclic group containing at least one of a nitrogen atom, an oxygen atom or a sulfur atom which may be a monocyclic ring or form a condensed ring together with an aromatic ring or a heterocyclic ring. A 5-membered or 6-membered aromatic heterocyclic group is preferred. Specific examples of the heterocyclic group include a pyridyl group, an imidazolyl group, a quinolinyl group, a benzimidazolyl group, a pyrimidyl group, a pyrazolyl group, an isoquinolinyl group, a benzothiazolyl group and a thiazolyl group. The aliphatic group, aromatic group and heterocyclic group represented by R₅ or R₆ in OR₅ or NR₅R₆ are the same as those described for R₁ or R₂ respectively. The group represented by R₁, R₂, R₅ and R₆ may be substituted with one or more substituents. Suitable examples of the substituent include an alkyl group, an aralkyl group, an alkoxy group, an aryl group, a substituted amino group, an acylamino group, a sulfonylamino group, a ureido group, a urethane group, an aryloxy group, a sulfamoyl group, a carbamoyl group, an alkylthio group, an arylthio group, a sulfonyl group, a sulfinyl group, a hydroxyl group, a halogen atom, a cyano group, a sulfo group and a carboxy group. These groups may be further substituted. Also, these groups may combine with each other to form a ring. R₁ or R₂ may combine with L₁ to form a ring. Further, R₁ and R₂ may combine with each other to form a ring including a hetero ring which contains one or more hetero atoms (for example, an oxygen atom, a sulfur atom or a nitrogen atom). The divalent linkage group represented by L₁ is an atom or an atomic group including at least one of a carbon atom, a nitrogen atom, a sulfur atom and an oxygen atom. More specifically, it includes an alkylene group, an alkenylene group, an alkynylene group, an arylene group, a heteroarylene group (these groups may be substituted), singly or as a combination thereof. Among them, an arylene group is preferred. The arylene group includes a phenylene group and a naphthylene group and these groups may be substituted. Suitable examples of the substituent include an alkyl group, an aralkyl group, an alkoxy group, an aryl group, an aryloxy group, an alkenyl group, an alkylthio group, an arylthio group, a sulfonyl group, a sulfinyl group, a halogen atom, a cyano group, an acyl group, a nitro group and When G₁ is a carbonyl group, R₃ is preferably a hydrogen atom, an alkyl group (for example, methyl, trifluoromethyl, 3-hydroxypropyl or 3-methanesulfonamidopropyl), an aralkyl group (for example, o-hydroxybenzyl), or an aryl group (for example, phenyl, 3,5-dichlorophenyl, o-methanesulfonamidophenyl or 4-methanesulfonylphenyl). When G₁ is a sulfonyl group, R₃ is preferably an alkyl group (for example, methyl), an aralkyl group (for example, o-hydroxyphenylmethyl), an aryl group (for example, phenyl), or a substituted amino group (for example, dimethylamino). When G₁ is a sulfoxy group, R₃ is preferably a cyanobenzyl group or a methylthiobenzyl group. When G₁ is R₃ is preferably a methoxy group, an ethoxy group, a butoxy group, a phenoxy group or a phenyl group. When G₁ is an N-substituted or unsubstituted iminomethylene group, R₃ is preferably a methyl group, an ethyl group or a substituted or unsubstituted phenyl group. Suitable examples of the substituent for R₃ include an alkyl group, an aralkyl group, an alkoxy group, an aryl group, a substituted amino group, an acylamino group, a sulfonylamino group, a ureido group, a urethane group, an aryloxy group, a sulfamoyl group, a carbamoyl group, an alkylthio group, an arylthio group, a sulfonyl group, a sulfinyl group, a hydroxyl group, a halogen atom, a cyano group, a sulfo group, a carboxy group, an acyloxy group, an acyl group, an alkyloxycarbonyl group, an aryloxycarbonyl group, an alkenyl group, an alkynyl group and a nitro group. These groups may be further substituted. Also, these groups may combine with each other to form a ring. G₁ is most preferably a carbonyl group, and R₃ is preferably a hydrogen atom or a group represented by the following general formula (a): -L₂-Z₁ (a) wherein Z₁ represents a group capable of cleaving the G₁-L₂-Z₁ moiety from the remainder molecule upon a nucleophilic attack on G₁; and L₂ is a divalent organic group capable of forming a G₁, L₂ and Z₁ cyclic structure upon the nucleophilic attack of Z₁ on G₁. In more detail, Z₁ is a group capable of easily making a nucleophilic attack on G₁ to cleave a group from G₁, when the hydrazine compound represented by the general formula (I) is changed to form upon oxidation. Specifically, Z₁ may be a functional group which directly reacts with G₁, for example, -OH, -SH, -NHR₇ (wherein R₇ represents a hydrogen atom, an alkyl group, an aryl group, a heterocyclic group, -COR₈ or -SO₂R₈; and R₈ represents a hydrogen atom, an alkyl group, an aryl group or a heterocyclic group) or -COOH (these groups may be temporarily protected so as to form these groups upon hydrolysis by an alkali), or a functional group which becomes possible to react with G₁ upon a reaction with a nucleophilic agent such as a hydroxy ion or a sulfite ion, for example, (wherein R₉ and R₁₀ each represents a hydrogen atom, an alkyl group, an alkenyl group, an aryl group or a heterocyclic group). The divalent organic group represented by L₂ is an atom or an atomic group including at least one of a carbon atom, a nitrogen atom, a sulfur atom and an oxygen atom. More specifically, it includes an alkylene group, an alkenylene group, an alkynylene group, an arylene group, a heteroarylene group (these groups may be substituted), -O-, -S-, (wherein R₁₁ represents a hydrogen atom, an alkyl group or an aryl group), -N=, -CO-, -SO₂-, singly or as a combination thereof. Preferably, the ring formed with G₁ , Z₁ and L₂ is a 5-membered or 6-membered ring. Of the groups represented by the general formula (a), those represented by the general formula (b) or (c) described below are preferred. wherein R b ¹, R b ², R b ³ and R b ⁴, which may be the same or different, each represents a hydrogen atom, an alkyl group (preferably having from 1 to 12 carbon atoms), an alkenyl group (preferably having from 2 to 12 carbon atoms) or an aryl group (preferably having from 6 to 12 carbon atoms); B represents an atomic group necessary to form a 5-membered or 6-membered ring which may be substituted; m and n each represents 0 or 1, when Z₁ is -COOH, n+m is 0 or 1, and when Z₁ is -OH, -SH or -NHR₄, n+m is 1 or 2: and Z₁ has the same meaning as defined in the general formula (a). Specific examples of the 5-membered or 6-membered ring formed with B include a cyclohexene ring, a benzene ring, a naphthalene ring, a pyridine ring, and a quinoline ring. In the general formula (b), it is preferred that m is 0 and n is 1 and it is particularly preferred that the ring formed with B is a benzene ring. wherein Rc¹ and Rc², which may be the same or different, each represents a hydrogen atom, an alkyl group, an alkenyl group, an aryl group or a halogen atom; Rc³ represents a hydrogen atom, an alkyl group, an alkenyl group or an aryl group; p represents 0 or 1; q represents 1, 2, 3 or 4; and Z₁ has the same meaning as defined in the general formula (a), or Rc¹, Rc² and Rc³ may combine with each other to form a ring as far as the resulting structure makes possible an intramolecular nucleophilic attack of Z₁ on G₁; and when q represents 2 or 3, two or three CRc¹Rc²'s may be the same or different. In the general formula (c), Rc¹ and Rc² each preferably represents a hydrogen atom, a halogen atom or an alkyl group, Rc³ preferably represents an alkyl group or an aryl group, and g preferably represents 1, 2 or 3, and when q is 1, p is 0 or 1, when q is 2, p is 0 or 1, and when q is 3, p is 0 or 1. X₁ in the general formula (I) represents -O- or -NR₄- (wherein R₄ represents a hydrogen atom, an alkyl group (for example, methyl, ethyl, or methoxyethyl), or an aryl group (for example, phenyl). X₁ is preferably -NR₄-, and R₄ is preferably a hydrogen atom. Y₁ in the general formula (I) represents or Y₁ is preferably It is preferred that R₁, R₂, L₁ or R₃, particularly R₁ or R₂ contains a diffusion resistant group, i.e., a so called ballast group, used for couplers. Such a ballast group has eight or more carbon atoms and comprises an alkyl group, a phenyl group, an ether group, an amido group, a ureido group, a urethane group, a sulfonamido group, a thioether group or a combination thereof. It is also preferred that the compound represented by the general formula (I) has an adsorption accelerating group represented by the formula described below on the surface of silver halide in R₁, R₂, L₁ or R₃. Y₂(L₃ wherein Y₂ represents an adsorption accelerating group for silver halide; L₃ represents a divalent linkage group; and ℓ represents 0 or 1. Preferred examples of the adsorption accelerating group for silver halide represented by Y₂ include a thioamido group, a mercapto group, a group having a disulfido bond, or a 5-membered or 6-membered nitrogen-containing heterocyclic group. The thioamido adsorption accelerating group represented by Y₂ is a divalent group represented by which may be a part of a ring structure or an acylic thioamido group. Useful thioamido adsorption accelerating groups are described, for example, in U.S. Patents 4,030,925, 4,031,127, 4,080,207, 4,245,037, 4,255,511, 4,266,013 and 4,276,364, Research Disclosure , Vol. 151, No. 15162 (November, 1976) and ibid. , Vol. 176, No. 17626 (December, 1978). Specific examples of the acyclic thioamido group include a thioureido group, a thiourethane group, and a dithiocarbamic acid ester group. Specific examples of the cyclic thioamido group include 4-thiazoline-2-thione, 4-imidazoline-2-thione, 2-thiohydantoin, rhodanine, thiocarbituric acid, tetrazoline-5-thione, 1,2,4-triazoline-3-thione, 1,3,4-thiadiazoline-2-thione, 1,3,4-oxadiazoline-2-thione, benzimidazoline-2-thione, benzoxazoline-2-thione, and benzothiazoline-2-thione. They may be further substituted. As the mercapto group represented by Y₂, there are an aliphatic mercapto group, an aromatic mercapto group, and a heterocyclic mercapto group (when the atom adjacent to the carbon atom bonded to -SH group is a nitrogen atom, the mercapto group has the same meaning as a cyclic thioamido group which is in a tautomeric relation therewith and specific examples thereof are same as illustrated above). As the 5-membered or 6-membered nitrogen-containing heterocyclic group represented by Y₂, there are 5-membered or 6-membered nitrogen-containing heterocyclic rings comprising a combination of nitrogen, oxygen, sulfur, and carbon. Preferred examples thereof are benzotriazole, triazole, tetrazole, indazole, benzimidazole, imidazole, benzothiazole, thiazole, benzoxazole, oxazole, thiadiazole, oxadiazole, and triazine. They may be further substituted with an appropriate substituent. The substituents can be selected from those described for R₁ or R₂. Y₂ is preferably a cyclic thioamido group (for example, a mercapto-substituted nitrogen-containing heterocyclic ring, such as a 2-mercaptothiadiazole group, a 3-mercapto-1,2,4-triazole group, a 5-mercaptotetrazole group, a 2-mercapto-1,3,4-oxadiazole group, or a 2-mercaptobenzoxazole group) or a nitrogen-containing heterocyclic group (for example, a benzotriazole group, a benzimidazole group, or an indazole group). Two or more Y₂(L₃ groups may present in the compound and they may be the same or different. The divalent linkage group represented by L₃ is an atom or an atomic group including at least one of a carbon atom, a nitrogen atom, a sulfur atom and an oxygen atom. More specifically, it includes an alkylene group, an alkenylene group, an alkynylene group, an arylene group, -O-, -S-, -NH-, -N=, -CO-, -SO₂- (these groups may be substituted), singly or as a combination thereof. Specific examples of the divalent linkage group are set forth below. -CONH-, -NHCONH-, -SO₂NH-, -COO-, NHCOO-, -CH₂-, (CH₂ , (CH₂ , -NHCONHCH₂CH₂CONH-, -CH₂CH₂SO₂NH-, -CH₂CH₂CONH-, -PO₂NH-. These groups may be substituted with an appropriate substituent. The substituents can be selected from those described for R₁ or R₂. Of the compounds represented by the general formula (I), those preferred are represented by the following general formula (Ia): wherein R₁₂ has the same meaning as R₁ or R₂ in the general formula (I); k represents 0, 1 or 2; and R₁, R₂, R₃, R₄, A₁, A₂ and G₁ each has the same meaning as defined in the general formula (I). The group is preferably present at the o- or p-position to the hydrazino group. Specific examples of the compound represented by the general formula (I) are illustrated below: The compounds represented by the general formula (I) can be synthesized according to the methods as described, for example, in Gendai Yuki Gosei Series No. 5, Yuki Rin Kagobutsu (Organic Phosphorus Compounds) edited by Shadanhojin Yuki Gosei Kagaku Kyokai, P. Brigl, H. Muller, Ber. , Vol. 72, p. 2121 (1939), V.V. Katyshkina, M. Ya. Kraft, Zh. Obshch. Vol. 26, p. 3060 (1956), C. A. , Vol. 51, p. 8028a (1957), H.D. Orloff, C.J. Worrel, F.X. Markley, J. Am. Chem. Soc. , Vol. 80, p. 727 (1958), G. Jacobsen, Ber. , Vol. 8, p. 1519 (1875), M. Rapp, Ann. , Vol. 224, p. 156 (1884), R. Heim, Ber. , Vol. 16, p. 1763 (1883), Org. Synth. Coll. , Vol. 2, p. 110 (1943), A.E. Arbuzov, K.V. Nikonorov, Zh. Obshch. Khim. , Vol. 17, p. 2140 (1947), C. A. , Vol. 42, p. 4246b (1948), Org. Synth. , Vol. 46, p. 42 (1965), R.M. Isham, U.S. Patent 2,662,095 (1948), C. A. , Vol. 48, p. 13709f (1954), G.A. Saul, K.L. Godfrey, British Patent 744,484 (1953), C. A. , Vol. 50, p. 16825c (1956), and H. Normant, Angew. Chem. , Vol. 79, p. 1029 (1967). Representative synthesis examples of the compounds represented by the general formula (I) are set forth below. SYNTHESIS EXAMPLE 1 Synthesis of Compound I-2 7.6 g (0.05 mole) of 2-(4 aminophenyl)-1-formylhydrazine was dissolved in 25 ml of dimethylformamide and to the solution was added 10.4 ml (0.05 mole) of diphenylphosphorochloridate with thoroughly stirring in a nitrogen gas atmosphere. The mixture was cooled to reaction temperature of 10°C or below, and 5.7 ml of methylmorpholine was gradually added dropwise thereto. After the completion of the addition, the reaction temperature was raised to about 20°C and the mixture was stirred for 30 minutes. The reaction solution was poured into 400 ml of water, and extracted with ethyl acetate. The extract was dried with sodium sulfate and the ethyl acetate was distilled off. The residual oily product was isolated and purified by silica gel column chromatography (using dichloromethane/methanol=10/1) to obtain 8.9 g (yield: 46.6%) of Compound I-2 as an oily product. SYNTHESIS EXAMPLE 2 Synthesis of Compound I-1 6.0 g (0.04 mole) of 2-(4-aminophenyl)-1-formylhydrazine was dissolved in 20 ml of acetonitrile and to the solution was added 5.8 ml (0.04 mole) of diethylphosphorochloridate with thoroughly stirring in a nitrogen gas atmosphere. The mixture was cooled to reaction temperature of 10°C or below and 4.6 ml (0.04 mole) of methylmorpholine was gradually added dropwise thereto. After the completion of the addition, the reaction temperature was raised to about 20°C and the mixture was stirred for one hour. The reaction solution was filtered, the filtrate was concentrated under a reduced pressure. The residual oily product was isolated and purified by silica gel column chromatography (using ethyl acetate/methanol=4/1) to obtain 6.2 g (yield: 55.0%) of Compound I-1 as zn oily product. The nucleating agent used in the present invention can be incorporated into the photographic light-sensitive material or into a processing solution for the photographic light-sensitive material, and preferably is incorporated into the photographic light-sensitive material. When the nucleating agent used in the present invention is incorporated into the photographic light-sensitive material, although it is preferably that it is added to an internal latent image type silver halide emulsion layer, it can be added to other layers such as an intermediate layer, a subbing layer or a backing layer so long as the nucleating agent diffuses during coating or processing to be adsorbed onto silver halide. When the nucleating agent is added to a processing solution, it can be added to a developing solution or a prebath having a low pH as described in JP-A-58-178350. When the nucleating agent is incorporated into the photographic light-sensitive material, preferably the amount thereof is from 10⁻⁸ to 10⁻² mol, more preferably from 10⁻⁷ to 10⁻³, per mol of silver halide contained in an emulsion layer. When the nucleating agents is added to the processing solution, preferably the amount of the nucleating agents is from 10⁻⁵ to 10⁻¹ mol, more preferably from 10⁻⁴ to 10⁻² mol, per liter thereof. The internal latent image type silver halide emulsion not having been previously fogged which can be used in the present invention includes an emulsion containing silver halide grains whose surfaces have not been previously fogged, and which form latent images predominantly internally. More specifically, suitable emulsions have the characteristic that when coated on a transparent support in a predetermined amount ranging from 0.5 g/m² to 3 g/m² in terms of silver, exposed for a fixed time between 0.01 and 10 seconds, then developed at 18°C for 5 minutes in the following developing solution A (internal developer), a resulting maximum density (measured by a conventional photographic density measuring method) is at least about 5 times, more preferably at least about 10 times, as much as that obtained by coating and exposing the emulsion in the same manner as described above, but developing at 20°C for 6 minutes in the following developing solution B (surface developer): Internal developer A Metol 2 g Sodium sulfite (anhydrous) 90 g Hydroquinone 8 g Sodium carbonate (monohydrate) 52.5 g KBr 5 g KI 0.5 g Water to make 1 liter Surface developer B Metol 2.5 g ℓ-Ascorbic acid 10 g NaBO₂·4H₂O 35 g KBr 1 g Water to make 1 liter Specific examples of the internal latent image type emulsions include conversion type silver halide emulsions as described, for example, in U.S. Patent 2,592,250, and core/shell type silver halide emulsions as described, for example, in U.S. Patents 3,761,276, 3,850,637, 3,923,513, 4,035,185, 4,395,478 and 4,504,570, JP-A-,2-156614, JP-A-55-127549, JP-A-53-60222, JP-A-56-22681, JP-A-59-208540, JP-A-60-107641, JP-A-61-3137, Japanese Patent Application No. 61-32462 (corresponding to JP-A-62-215272) and the patents cited in Research Disclosure , No. 23510 (November, 1983), p. 236. The silver halide grains used in the present invention may be regular crystals such as cubic, octahedral, dodecahedral or tetradecahedral crystals, irregular crystals such as spherical crystals, or tabular grains whose length/thickness ratio is 5 or more. A composite form of these crystal forms may be used, and an emulsion made up of a mixture of these crystals may also be used. The composition of the silver halide includes silver chloride, silver bromide or a mixed silver halide, and the silver halide preferably used in the present invention is either free from silver iodide, or if it contains silver iodide, it is silver chloro(iodo)bromide, silver (iodo)chloride or silver (iodo)bromide containing 3 mol% or less of silver iodide. The average grain size of the silver halide grains is preferably from 0.1 µm up to 2 µm, more preferably from 0.15 µm to 1 µm. Although the distribution of the grain size may be wide or narrow, in order to improve graininess and sharpness, it is preferred in the present invention to use a so-called "monodisperse" silver halide emulsion having a narrow grain size distribution such that 90% or more of all the grains fall within the average grain size of ±40%, preferably ±20%, in terms of grain number or weight. In order to satisfy the gradation required for the photographic light-sensitive material, in emulsion layers having substantially the same color sensitivity, two or more monodisperse silver halide emulsions different in grain size or a plurality of grains of the same size but different in sensitivity are mixed in the same layer or are applied as different layers that are superposed. Further, two or more polydisperse silver halide emulsions or a monodisperse silver halide emulsion and a polydisperse silver halide emulsion can be used in the form of a mixture or in superposed layers. In the silver halide emulsion used in the present invention, the interior or the surface of the grains may be chemically sensitized by sulfur sensitization, selenium sensitization, reduction sensitization or noble metal sensitization, that can be used alone or in combination. Specific examples of useful chemical sensitization are described, for example, in the patents cited in Research Disclosure , No. 17643, Item III (December, 1978), page 23. The photographic emulsion used in the present invention is spectrally sensitized with a photographic sensitizing dye in a conventional manner. Particularly useful dyes are cyanine dyes, merocyanine dyes and complex merocyanine dyes, which may be used alone or in combination, and can also be used in combination with supersensitizers. Specific examples thereof are described, for example, in the patents cited in Research Disclosure , No. 17643, Item IV (December, 1978), pages 23 to 24. The photographic emulsions used in the present invention can contain an antifoggant or a stabilizer for the purpose of stabilizing the photographic performance, or of preventing formation of fog during the production, storage or photographic processing of the photographic light-sensitive material. Specific examples of anti-foggants and stabilizers are described, for example, in Research disclosure , No. 17643, Item IV (December, 1978), and E.J Birr, Stabilization of Photographic Silver Halide Emulsion , 1974 (Focal Press). In order to form direct positive color images according to the present invention, various color couplers can be employed. Useful color couplers are compounds that can undergo a coupling reaction with an oxidation product of an aromatic primary amine type color developing agent to produce or release a dye substantially non-diffusible and that themselves are preferably substantially non-diffusible. Typical examples of useful color couplers include naphtholic or phenolic compounds, pyrazolone or pyrazoloazole compounds and open chain or heterocyclic ketomethylene compounds. Specific examples of these cyan, magenta and yellow couplers which can be used in the present invention are compounds as described, for example, in Research Disclosure , No. 17643 (December, 1978), page 25, Item VII-D; ibid ., No. 18717 (November, 1979) and Japanese Patent Application No. 61-32462 (corresponding to JP-A-62-215272), and compounds described in the patents cited therein. Colored couplers for correcting undesired absorption in the short wavelength range of produced dyes; couplers capable of forming dyes with appropriate diffusibility; colorless compound forming couplers; DIR couplers that can release a development inhibitor as a result of the coupling reaction; and polymerized couplers can also be used. As binders or protective colloids which can be used in emulsion layers and intermediate layers of the photographic light-sensitive material of the present invention, it is advantageous to use gelatin, but other hydrophilic colloids than gelatin can also be used. The photographic light-sensitive material in accordance with the present invention may contain a color fog preventing agent or color stain preventing agent. Representative examples of these compounds are described in JP-A-62-215272, pages 185 to 193. In the present invention, a color formation reinforcing agent can be employed for the purpose of increasing a color forming property of coupler. Representative examples of such compounds are described in JP-A-62-215272, pages 121 to 125. The photographic light-sensitive material of the present invention can contain dyes for preventing irradiation or halation, ultraviolet light absorbing agents, plasticizers, brightening agents, matting agents, aerial fog preventing agents, coating aids, hardening agents, antistatic agents, lubricants, etc. Typical examples of these additives are described in Research Disclosure , No. 17643, Items VIII to XIII (December, 1978), pages 25 to 27, ibid ., No. 18716 (November, 1979), pages 647 to 651. The present invention can be applied to multilayer multicolor photographic materials having at least two layers having different spectral sensitivities on a support. Generally, a multilayer natural color photographic material has at least one red-sensitive emulsion layer, at least one green-sensitive emulsion layer and at least one blue-sensitive emulsion layer on a support. The order of these layers is appropriately selected as desired. In a preferred order of the layers, a red-sensitive emulsion layer, a green-sensitive emulsion layer and a blue-sensitive emulsion layer are coated in that order on a support or a green-sensitive emulsion layer, a red-sensitive emulsion layer and a blue-sensitive emulsion layer are coated in that order on a support. Each of these emulsion layers may consist of two or more emulsion layers different in sensitivity, or may consist of two or more emulsion layers having the same sensitivity with a light-insensitive layer between them. Generally, the red-sensitive emulsion layer contains a cyan forming coupler, the green-sensitive emulsion layer contains a magenta forming coupler and the blue-sensitive emulsion layer contains a yellow forming coupler, but in some cases the combination can be changed. It is preferable that the photographic light-sensitive material according to the present invention is provided with suitable auxiliary layers such as a protective layer, an intermediate layer, a filter layer, an antihalation layer, a backing layer and a white reflective layer, in addition to the silver halide emulsion layers. In the photographic light-sensitive materials of the present invention, the photographic emulsion layers and other layers are applied on a support as described in Research Disclosure , No. 17643, Item XVII (December, 1978), page 28, European Patent 0,102,253, and JP-A-61-97655. The coating methods as described in Research Disclosure , No. 17643, Item XV, pages 28 to 29 can be employed. The present invention may be applied to various types of color photographic light-sensitive materials. For instance, color reversal films for slides and television, color reversal papers, instant color films, etc. are typical examples. In addition, the present invention may be applied to color hard copies for preserving images of full color copiers or CRT. The present invention is also applicable to black-and-white photographic light-sensitive materials utilizing mixing of three color couplers, as described, for example, in Research Disclosure , No. 17123 (July, 1978). Furthermore, the present invention can be applied to black-and-white photographic light-sensitive materials. Examples of the black-and-white (B/W) photographic light-sensitive materials to which can be applied the present invention include B/W direct positive photographic light-sensitive materials (for example, photographic materials for X-ray, for duplication, for micrography, for photocomposing, and for printing) as described, for example, in JP-A-59-208540 and JP-A-60-260039. It is preferred to employ a nucleation accelerating agent together with the above described nucleating agent in the present invention. The term "nucleation accelerating agent" as used herein means a substance which does not substantially act as the nucleating agent but, rather, acts to accelerate the action of the nucleating agent to increase the maximum density of direct positive images and/or reduce the development time required to provide a predetermined direct positive image density. As the nucleation accelerating agent, a compound represented by the general formula (II) or (III) described below, is preferably employed. wherein Q represents an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring to which a carbocyclic aromatic ring or a heterocyclic aromatic ring may further be condensed; L represents a divalent linkage group comprising an atom or atomic group selected from the group consisting of a hydrogen atom, a carbon atom, a nitrogen atom, an oxygen atom, and a sulfur atom; R₁₈ represents an organic group containing at least one of a thioether group, an amino group, an ammonium group, an ether group, or a heterocyclic group; n represents 0 or 1; m represents 0, 1 or 2; and M represents a hydrogen atom, an alkali metal atom, an ammonium group or a group capable of being cleaved under an alkaline condition, wherein Q′ represents an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring which is capable of forming imino silver; L, R₁₈, n and M each has the same meaning as defined in the general formula (II) above; and m represents 1 or 2. [(L R₁₈] m also has the same meaning as defined in the general formula (II) above. Now, the compound represented by the general formula (II) or (III) will be explained in detail. In the general formula (II), Q preferably represents an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring comprising at least one atom selected from the group consisting of a carbon atom, a nitrogen atom, an oxygen atom, a sulfur atom and a selenium atom. The heterocyclic ring may be condensed with a carbocyclic aromatic ring or heterocyclic aromatic ring. Examples of the heterocyclic ring include a tetrazole, a triazole, an imidazole, a thiadiazole, an oxadiazole, a selenadiazole, an oxazole, a thiazole, a benzoxazole, a benzothiazole, a benzimidazole, and a pyrimidine. M represents a hydrogen atom, an alkali metal atom (for example, sodium, or potassium), an ammonium group (for example, trimethylammonium, or dimethylbenzylammonium) or a group which undergoes cleavage under an alkaline condition to become a hydrogen atom or an alkali metal atom for M (for example, acetyl, cyanoethyl, or methanesulfonylethyl). The above described heterocyclic ring may be substituted with a nitro group, a halogen atom (for example, chlorine, or bromine), a mercapto group, a cyano group, a substituted or unsubstituted alkyl group for example, methyl, ethyl, propyl, tert-butyl, cyanoethyl), a substituted or unsubstituted aryl group (for example, phenyl, 4-methanesulfonamidophenyl, 4-methylphenyl, 3,4-dichlorophenyl, naphthyl), a substituted or unsubstituted alkenyl group (for example, allyl), a substituted or unsubstituted aralkyl group (for example, benzyl, 4-methylbenzyl, phenethyl), a sulfonyl group (for example, methanesulfonyl, ethanesulfonyl, p-toluenesulfonyl), a carbamoyl group (for example, unsubstituted carbamoyl, methylcarbamoyl, phenylcarbamoyl), a sulfamoyl group (for example, un substituted sulfamoyl, methylsulfamoyl, phenylsulfamoyl), a carbonamido group (for example, acetamido, benzamido), a sulfonamido group (for example, methanesulfonamido, benzenesulfonamido, p-toluenesulfonamido), an acyloxy group (for example, acetyloxy, benzoyloxy), a sulfonyloxy group (for example, methanesulfonyloxy), a ureido group (for example, unsubstituted ureido, methylureido, methylureido, phenylureido), a thioureido group (for example, unsubstituted thioureido, methylthioureido), an acyl group (for example, acetyl, benzoyl), an oxycarbonyl group (for example, methoxycarbonyl, phenoxycarbonyl), an oxycarbonylamino group (for example, methoxycarbonylamino, phenoxycarbonylamino, 2-ethylhexyloxycarbonylamino), a carboxylic acid or a salt thereof, a sulfonic acid or a salt thereof, or a hydroxy group. However, the heterocyclic ring preferably is not substituted with a carboxylic acid or a salt thereof, a sulfonic acid or a salt thereof, or a hydroxy group in view of the effect of accelerating nucleation. Preferred examples of the heterocyclic ring represented by Q include a tetrazole, a triazole, an imidazole, a thiadiazole, and an oxadiazole. L represents a divalent linkage group comprising an atom or atomic group selected from the group consisting of a hydrogen atom, a carbon atom, a nitrogen atom, an oxygen atom and a sulfur atom. Suitable examples of the divalent linkage group include -S-, -O-, In the above formulae, R₁₉, R₂₀, R₂₁, R₂₂, R₂₃, R₂₄, R₂₅, R₂₆, R₂₇ and R₂₈ each represents a hydrogen atom, a substituted or unsubstituted alkyl group (for example, methyl, ethyl, propyl, n-butyl), a substituted or unsubstituted aryl group (for example, phenyl, 2-methylphenyl), a substituted or unsubstituted alkenyl group (for example, propenyl, 1-methylvinyl), or a substituted or unsubstituted aralkyl group (for example, benzyl, phenethyl). These linkage groups may be connected through a straight chain or branched chain alkylene group (for example, methylene, ethylene, propylene, butylene, hexylene, 1-methylethylene) or a substituted or unsubstituted arylene group (for example, phenylene, naphthylene) to a heterocyclic ring described below. R₁₈ in the general formula (II) or (III) represents an organic group containing at least one of a thioether group, an amino group (including a salt thereof), an ammonium group, an ether group or a heterocyclic group (including a salt thereof). Suitable examples of the organic group include groups obtained by combining a group selected from a substituted or unsubstituted alkyl group a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aralkyl group, and a substituted or unsubstituted aryl group with a thioether group, an amino group, an ammonium group, an ether group, or a heterocyclic group above. Combinations of such organic groups may be used. Specific examples of such organic groups include a dimethylaminoethyl group, an aminoethyl group, a diethylaminoethyl group, a dibutylaminoethyl group, a dimethylaminopropyl hydrochloride group, a dimethylaminoethylthioethyl group, a 4-dimethylaminophenyl group, a 4-dimethylaminobenzyl group, a methylthioethyl group, an ethylthiopropyl group, a 4-methylthio-3-cyanophenyl group, a methylthiomethyl group, a trimethylammonioethyl group, a methoxyethyl group, a methoxyethoxyethoxyethyl group, a methoxyethylthioethyl group, a 3,4-dimethoxyphenyl group, a 3-chloro-4 methoxyphenyl group, a morpholinoethyl group, a 1-imidazolylethyl group, a morpholinoethylthioethyl group, a pyrrolidinoethyl group, a piperidinopropyl group, a 2-pyridylmethyl group, a 2-(1-imidazolyl)ethylthioethyl group, a pyrazolylethyl group, a triazolylethyl group, and a methoxyethoxyethoxyethoxycarbonylaminoethyl group. In the general formula (II), n represents 0 or 1, and m represents 0, 1 or 2. In the general formula (III), L, R₁₈, n and M each has the same meaning as defined in the general formula (II); m represents 1 or 2; and Q′ represents an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring which is capable of forming imino silver, preferably an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring comprising at least one atom selected from the group consisting of a carbon atom, a nitrogen atom, an oxygen atom, a sulfur atom and a selenium atom. The heterocyclic ring may be condensed with a carbocyclic aromatic ring or heterocyclic aromatic ring. Suitble examples of the heterocyclic ring formed by Q′ include an indazole, a benzimidazole, a benzotriazole, a benzoxazole, a benzothiazole, an imidazole, a thiazole, an oxazole, a triazole, a tetrazole, a tetraazaindene, a triazaindene, a diazaindene, a pyrazole, and an indole. Of the compounds represented by the general formula (II), those represented by the general formula (IV), (V), (VI), or (VII) described below are preferably employed. wherein M, R₁₈, L and n each has the same meaning as defined in the general formula (II); and X represents an oxygen atom, a sulfur atom or a selenium atom, preferably a sulfur atom, wherein R₂₉ represents a hydrogen atom, a halogen atom (for example, chlorine, bromine), a nitro group, a mercapto group, an unsubstituted amino group, a substituted or unsubstituted alkyl group (for example, methyl, ethyl), a substituted or unsubstituted alkenyl group (for example, propenyl, 1-methylvinyl), a substituted or unsubstituted aralkyl group (for example, benzyl, phenethyl), a substituted or unsubstituted aryl group (for example, phenyl, 2-methylphenyl) or (L R₁₈; R₃₀ represents a hydrogen atom, an unsubstituted amino group or (L R₁₈, when both R₂₉ and R₃₀ represent (L R₁₈, they may be the same or different, provided that at least one of R₂₉ and R₃₀ represents (L R₁₈; and M, R₁₈, L and n each has the same meaning as defined in the general formula (II), wherein R₃₁ represents (L R₁₈; and M, R₁₈, L and n each has the same meaning as defined in the general formula (II), wherein R₃₂ and R₃₃, which may be the same or different, each represents a hydrogen atom, a halogen atom, a substituted or unsubstituted amino group, a nitro group, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aralkyl group or a substituted or unsubstituted aryl group; M and R₃₁ each has the same meaning as defined in the general formula (VI). Specific examples of the compound represented by the general formulae (III) to (VII) will be set forth hereinafter. The nucleation acclerating agent described above used in the present invention is incorporated into the photographic light-sensitive material or a processing solution, and preferably incorporated into an internal latent image type silver halide emulsion layer or other hydrophilic colloid layer (for example, an intermediate layer or a protective layer). Particularly preferably, the nucleation accelerating agent is incorporated into a silver halide emulsion layer or an adjacent layer thereto. The amount of the nucleation accelerating agent added is preferably from 10⁻⁶ to 10⁻² mol, more preferably from 10⁻⁵ to 10⁻² mol per mol of silver halide. When the nucleation accelerating agent is added to the processing solution, specifically a developing solution or a prebath thereof, the amount added is preferably from 10⁻⁸ to 10⁻³ mol, more preferably from 10⁻⁷ to 10⁻⁴ mol, per liter thereof. A color developing solution which can be used in development processing of the photographic light-sensitive material according to the present invention is an alkaline aqueous solution containing preferably an aromatic primary amine type color developing agent as a main component. As the color developing agent, while an aminophenol type compound is useful, a p-phenylenediamine type compound is preferably employed. Typical examples of the p-phenylenediamine type compounds include 3-methyl-4-amino-N,N-diethylaniline, 3-methyl-4-amino-N-ethyl-N-β-hydroxyethylaniline, 3-methyl-4-amino-N-ethyl-N-β-methanesulfonamidoethylaniline, 3-methyl-4-amino-N-ethyl-N-β-methoxyethylaniline, or sulfate, hydrochloride, p-toluenesulfonate thereof. Two or more kinds of color developing agents may be employed in a combination thereof, depending on the purpose. The pH of the color developing solution used is ordinarily in a range from 9.0 to 12.0, preferably in a range from 9.5 to 11.5, most preferably in a range from 9.8 to 11.0. After color development, the photographic emulsion layers are usually subjected to a bleach processing. The bleach processing can be performed simultaneously with a fix processing (bleach-fix processing), or it can be performed independently from the fix processing. Further, for the purpose of performing a rapid processing, a processing method wherein after a bleach processing a bleach-fix processing is conducted may be employed. Moreover, it may be appropriately practiced depending on the purpose to process using a continuous two tank bleach-fixing bath, to carry out fix processing before bleach-fix processing, or to conduct bleach processing after bleach-fix processing. After a desilvering step, the silver halide color photographic material according to the present invention is generally subjected to a water washing step and/or a stabilizing step. An amount of water required for the water washing step may be set in a wide range depending on characteristics of photographic light-sensitive materials (due to elements used therein, for example, couplers), uses thereof, temperature of washing water, a number of water washing tanks (stages), a replenishment system such as countercurrent or orderly current, or other various conditions. A relationship between a number of water washing tanks and an amount of water in a multi-stage countercurrent system can be determined based on the method as described in Journal of the Society of Motion Picture and Television Engineers , Vol. 64, pages 248 to 253 (May, 1955). For the purpose of simplification and acceleration of processing, a color developing agent may be incorporated into the silver halide color photographic material according to the present invention. In order to incorporate the color developing agent, it is preferred to employ various precursors of color developing agents. In order to develop the black-and-white photographic light-sensitive material, known various developing agents can be employed in the present invention. For instance, polyhydroxybenzenes, for example, hydroquinone, 2-chlorohydroquinone, 2-methylhydroquinone, catechol, and pyrogallol; aminophenols, for example, p-aminophenol, N-methyl-p-aminophenol, and 2,4-diaminophenol; 3-pyrazolidones, for example, 1-phenyl-3-pyrazolidone, 1-phenyl-4,4′-dimethyl-3-pyrazolidone, 1-phenyl-4-methyl-4-hydroxymethyl-3-pyrazolidone, and 5,5-dimethyl-1-phenyl-3-pyrazolidone; and ascorbic acids; are employed individually or in a combination. Further, a developing solution as described in JP-A-58-55928 may be employed. Such developing agents may be incorporated into an alkaline processing composition (processing element) or an appropriate layer of a light-sensitive element. The developing solution may contain sodium sulfite, potassium sulfite, ascorbic acid, or a reductone (for example, piperidinohexose reductone) as a preservative. The photographic light-sensitive material according to the present invention can provide direct positive images upon development using a surface developing solution. The surface developing solution has a property in that its development process is substantially invited by a latent image or a fog center positioned on the surface of silver halide grain. Although it is preferred that the surface developing solution does not contain a silver halide solvent, the surface developing solution may contain a silver halide solvent such as sulfite, as far as an internal latent image does not substantially contribute until the development due to the development center positioned on the surface of silver halide grain is completed. The developing solution may contain sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, trisodium phosphate, or sodium metaborate, as an alkali agent or a buffering agent. The amount of these agents is selected so that the pH of the developing solution is adjusted to a range from 9.0 to 12.0, preferably from 9.5 to 11.5. It is advantageous that the developing solution may further contain a compound which is usually employed as an antifoggant, for example, a benzimidazole such as 5-nitrobenzimidazole, a benzotriazole such as benzotriazole, or 5-methylbenzotriazole, in order to reduce a minimum density of direct positive image. Specific examples and methods for use of developing agents, preservatives, buffering agents and methods of development with respect to black-and-white photographic light-sensitive materials are described, for example, in Research Disclosure , No. 17643 (December, 1978), Items XIX to XXI. In accordance with the present invention, positive images having a high maximum image density and a low minimum image density can be formed by processing a direct positive photographic light-sensitive material. In any magenta, cyan and yellow color images, high maximum image densities and low minimum image densities are obtained. This effect is obtained in a case of developing processing at a pH of 11.5 or below. Still higher maximum image density is obtained by coexisting with a nucleation accelerating agent in such a case. Further, the formation of image can be stably performed according to the image forming method of the present invention even if direct positive photographic light-sensitive materials are preserved under high temperature and high humidity conditions. The present invention is now illustrated in greater detail with reference to the following examples. EXAMPLE 1 The following First layer to Fourteenth layer were coated on the front side of a paper support (having a thickness of 100 µm), both surfaces of which were laminated with polyethylene, and the following Fifteenth layer to Sixteenth layer were coated on the back side of the paper support to prepare a color photographic light-sensitive material. The polyethylene laminated on the First layer side of the support contained titanium dioxide as a white pigment and a slight amount of ultramarine as a bluish dye (chromaticity of the surface of the support was 88.0, -0.20 and -0.75 in an L*, a* and b* system). Construction of Layers The composition of each layer is shown below. The coating amounts of the components are described in the unit of g/m². With respect to silver halide, the coating amount is indicated in terms of a silver coating amount. The emulsion used in each layer was prepared according to the method for preparation of Emulsion EM1. The emulsion used in the Fourteenth layer was a Lippmann emulsion not being chemically sensitized on the surfaces of grains. First Layer: Antihalation Layer Black colloidal silver 0.10 Gelatin 0.70 Second Layer: Intermediate Layer Gelatin 0.70 Third Layer: Low-Sensitive Red-Sensitive Layer Fourth Layer: High-Sensitive Red-Sensitive Layer Fifth Layer: Intermediate Layer Six Layer: Low-sensitive Green-Sensitive Layer Seventh Layer: high-Sensitive Green-Sensitive Layer Eighth Layer: Intermediate Layer Same as Fifth Layer Ninth Layer: Yellow Filter Layer Tenth Layer: Intermediate Layer Same as Fifth Layer Eleventh Layer: Low-Sensitive Blue-Sensitive Layer Twelfth Layer: High-Sensitive Blu-Sensitive Layer Thirteenth Layer: Ultraviolet Light Absorbing Layer Fourteenth Layer: Protective Layer Fifteenth Layer: Black Layer Sixteenth Layer: Back Protective Layer Preparation of Emulsion EM-1 An aqueous solution of potassium bromide (0.12N, 900 ml) and an aqueous solution of silver nitrate 0.12N, 830 ml) were added simultaneously to an aqueous gelatin solution (3%, 700 ml) at 75°C over a period of 15 minutes while vigorously stirring, to obtain an octahedral silver bromide emulsion having an average grain diameter of 0.40 µm. 0.3 g of 3,4-dimethyl-1,3-thiazoline-2-thione, 6 mg of sodium thiosulfate and 7 mg of chloroauric acid (tetrahydrate) were added to the emulsion per mol of silver in order and the emulsion was heated to 75°C for 80 minutes to be chemically sensitized. The thus-prepared silver bromide grains were used as cores and were further grown under the same precipitation conditions as above to obtain finally a monodisperse octahedral core/shell type silver bromide emulsion having an average grain diameter of 0.7 µm. The coefficient of variation of the grain size was about 10%. 1.5 mg of sodium thiosulfate and 1.5 mg of chloroauric acid (tetrahydrate) were added to the emulsion per mol of silver, and the emulsion was heated to 60°C for 60 minutes to be chemically sensitized, thus an internal latent image type silver halide emulsion was obtained. To each light-sensitive layer, a nucleating agent was added as shown in Table 1 below. Also, to each layer, as emulsifying dispersing aids, sodium alkylnaphthalenesulfonate and sodium alkylbenzenesulfonate, and as coating aids, succinic acid ester and were added. Furthermore, to the layers containing silver halide or colloidal silver, Stabilizers (Cpd-23, 24, 25) were added. The compounds used in this example are illustrated below. Solv-1 Di(2-ethylhexyl) sebacate Solv-2 Trinonyl phosphate Solv-3 Di(3-methylhexyl) phthalate Solv-4 Tricresyl phosphate Solv-5 Dibutyl phthalate Solv-6 Trioctyl phosphate Solv-7 Di(2-ethylhexyl) phthalate H-1 1,2-Bis(vinylsulfonylacetamido)ethane H-2 4,6-Dichloro-2-hydroxy-1,3,5-triazine sodium salt The color photographic light-sensitive materials thus prepared were exposed to light through a wedge (3200°K, 1/10″, 100 CMS) and then subjected to Processing Step A described below. Density of magenta color image formed was measured. The results are shown in Table 1 below. Comparative Compound A: From the results shown in Table 1, it is apparent that Sample Nos. 1 to 7 containing the nucleating agents according to the present invention are preferred since they exhibit high Dma x in comparison with Sample No. 8 for comparison. Further, the similar results were obtained with respect to cyan and yellow color image densities. Processing Step A: The composition of the processing solutions used was as follows. Washing Water (both tank solution and replenisher) City water was passed through a mixed bed type column filled with an H type strong acidic cation exchange resin (Amberlite IR-120B manufactured by Rohm & Haas Co.) and an OH type anion exchange resin (Amberlite IR-400 manufactured by Rohm & Haas Co.) to prepare water containing not more than 3 mg/liter of calcium ion and magnesium ion. To the water thus-treated were added sodium dichloroisocyanurate in an amount of 20 mg/liter and sodium sulfate in an amount of 1.5 g/liter. The pH of the solution was in a range from 6.5 to 7.5. EXAMPLE 2 Color photographic light sensitive materials were prepared in the same manner as described in Example 1 except that a nucleating agent and a nucleation accelerating agent were added to each emulsion layer as shown in Table 2 below. Then, exposure to light and processing were conducted in the same manner as described in Example 1 except for changing the time for color development to 100 seconds. Density of cyan color image formed was measured. The results are shown in Table 2 below. From the results shown in Table 2, it is apparent that Sample Nos. 1 to 6 containing the nucleating agents according to the present invention are preferred since they exhibit high D max in comparison with Sample Nos. 7 to 9 for comparison. EXAMPLE 3 Preparation of Emulsion X An aqueous solution of silver nitrate (0.9N, 111 ml, containing silver nitrate in an amount corresponding to about 1/8 of the total molar quantity of silver nitrate to be used) and an aqueous solution of potassium bromide (0.9N, 120 ml) were simultaneously added at constant addition rate to an aqueous gelatin solution (3%, 500 ml, pH: 5.5) of 75°C containing 20 mg per liter of thioether (1,8-dihydroxy-3,6-dithiaoctane) under thoroughly stirring for 5 minutes while maintaining a silver electrode potential constantly to obtain a spherical monodisperse silver bromide emulsion having an average grain diameter of about 0.14 µm. 20 mg of sodium thiosulfate and 20 mg of chloroauric acid (4 hydrate) were added to the emulsion per mol of silver halide and the pH was adjusted at 7.5, followed by heating at 75°C for 80 minutes with thoroughly stirring to effect chemical sensitization. The thus obtained silver bromide grains were used as cores, an aqueous solution of silver nitrate (1.2N, 583 ml, containing silver nitrate in an amount corresponding to about 7/8 of the total molar quantity of silver nitrate to be used) and an aqueous solution of potassium bromide (1.3N, 583 ml) were added simultaneously under thoroughly stirring at the same temperature as above over a period of 40 minutes while maintaining a silver electrode potential for growing regular octahedral grains in order to allow for the growth of shell thereby a cubic monodisperse core/shell type silver bromide emulsion having an average grain diameter of about 0.3 µm was obtained. The pH of the emulsion was adjusted at 6.5 and 5 mg of sodium thiosulfate and 5 mg of chloroauric acid (4 hydrate) were added thereto per mol of silver halide, followed by ripening at 75°C for 60 minutes to effect chemical sensitization of the surface of shell to finally obtain an internal latent image type octahedral monodisperse core/shell silver bromide emulsion (Emulsion X). As a result of measurement on grain size distribution of the emulsion using electron microscopic photographs, it was found that an average grain diameter was 0.30 µm and a coefficient of variation (percent of a value obtained by dividing a statistical standard deviation with the above-described average grain diameter) was 10%. To Emulsion X described above was added, as a panchromatic sensitizing dye, 5 mg of 3,3′-diethyl-9-methylthiacarbocyanine per mol of silver halide, and then were added the nucleating agent as shown in Table 3 below and 5.6×10⁻⁴ mol of Nucleation accelerating agent A-6 per mol of silver halide, respectively. The coating solution thus-prepared was coated on a polyethylene terephthalate film support so as to be a silver coating amount of 2.8 g/m² simultaneously with a protective layer composed of gelatin and a hardening agent. Thus, direct positive photographic light-sensitive material Samples No. 1 to No. 5 each being sensitive up to red light were prepared. These samples were exposed through a step wedge using a sensitometer equipped with a tungsten lamp of 1 KW (color temperature: 2,854°K) for 0.1 second. Thereafter, each sample was developed at 38°C for 18 seconds by an automatic developing machine (Kodak Proster I Processor) using Kodak Proster Plus processing solution (developing solution: pH of 10.7), followed by washing with water, fixing and washing with water step by the same processor and dried. The maximum density (D max ) and the minimum density (D min ) of direct positive image thus-formed in each sample were measured. The results thus-obtained are shown in Table 3 below. As is apparent from the results shown in Table 3, Sample Nos. 1 to 3 containing the nucleating agent according to the present invention are preferred since they provide high D max and low D min as compared with Sample No. 4 for comparison. EXAMPLE 4 Preparation of Core/shell Type Direct Positive Emulsion (EM-1) An aqueous solution of potassium bromide (0.52N, 500 ml) and an aqueous solution of silver nitrate (0.50N, 500 ml) were simultaneously added at 75°C over a period of about 60 minutes with vigorous stirring to an aqueous gelatin solution (3%, 600 ml) to obtain a silver bromide emulsion. Before the precipitation, 80 mg of 3,4-dimethyl-1,3-thiazoline-2-thione per mole of silver and 6 g of benzimidazole per mol of silver were added to the precipitation vessel. After the completion of the precipitation, silver bromide crystals having an average grain diameter of about 1.1 µm were formed. Then 5.4 mg of sodium thiosulfate per mol of silver and 3.9 mg of potassium chloroaurate per mol of silver were added to the silver bromide emulsion and the emulsion was heated at 75°C for 35 minutes to be chemically sensitized. The thus chemically sensitized silver bromide grains were used as cores and to the emulsion were added simultaneously an aqueous solution of potassium bromide (1.2N, 750 ml) and an aqueous solution of silver nitrate (1.0N, 750 ml) over a period of 40 minutes in the same manner as the first step described above to prepare a core/shell emulsion. The final average grain diameter of the emulsion was 1.5 µm. To the core/shell type emulsion were added 0.50 mg of sodium thiosulfate per mol of silver and 57 mg of poly(N-vinylpyrrolidone) per mol of silver and the emulsion was heated at 60°C for 45 minutes to be chemically sensitized on the surface of grains, whereby Emulsion (EM-1) was prepared. Preparation of Light-Sensitive Sheet A On a polyethylene terephthalate transparent film support, Layer 1 to Layer 6 were coated according to the, layer structure shown below to prepare Light-Sensitive Sheet A. Layer 6: Protective layer containing gelatin Layer 5: Red-sensitive core/shell type direct positive emulsion layer Layer 4: Layer containing a cyan DRR compound Layer 3: Light shielding layer Layer 2: White reflective layer Layer 1: Mordanting layer Support Layer 1 : Mordanting layer containing a copolymer having the repeating unit described below in the ratio described below: x:y=50:50 which is described in U.S. Patent 3,898,088 (3.0 g/m²) and gelatin (3.0 mg/m²) Layer 2 : White reflective layer containing titanium oxide (20 g/m²) and gelatin (2.0 g/m²) Layer 3 : Light-shielding layer containing carbon black (2.0 g/m²) and gelatin (1.5 g/m²) Layer 4 : Layer containing a cyan DRR compound described below (0.44 g/m²), tricyclohexyl phosphate (0.09 g/m²) and gelatin (0.8 g/m²) Layer 5 : Red-sensitive core/shell type direct positive silver bromide emulsion layer containing Emulsion (EM-1) described above (0.81 g/m² as silver), a red-sensitizing dye (the aforementioned ExS-1, 2, 3), the nucleating agent and the nucleation accelerating agent as shown in Table 4 below, 4-hydroxy-6-methyl-1,3,3a,7-tetraazaindene (4.3 mg/m²) and sodium 5-pentadecylhydroquinone-2-sulfonate (0.11 g/m²) Layer 6 : Protective layer containing gelatin (1.0 g/m²) Processing Solution: 0.8 g portions of the processing solution having the above-described composition were retained in "pressure-rupturable containers". Cover Sheet: On a polyethylene terephthalate transparent film support, Layer 1′ to Layer 3′ described below were coated in this order to prepare a cover sheet. Layer 1′ : Neutralizing layer containing a copolymer of acrylic acid and butyl acrylate (weight ratio: 80/20) (22 g/m²) and 1,4-bis(2,3-epoxypropoxy)butane (0.44 g/m²) Layer 2′ : Layer containing acetyl cellulose (as modified by hydrolysis of 100 g acetyl cellulose to form 39.4 g of acetyl group) (3.8 g/m²), a copolymer of styrene and maleic anhydride (weight ratio: 60/40, molecular weight: about 50,000) (0.2 g/m²) and 5-(β-cyanoethylthio)-1-phenyltetrazole (0.115 g/m²) Layer 3′ : Layer containing a copolymer latex of vinylidene chloride, methyl acrylate and acrylic acid (weight ratio: 85/12/3) (2.5 g/m²) and polymethyl methacrylate latex (particle size: 1 to 3 µm) (0.05 g/m²) Exposure to Light and Development Processing The above-described cover sheet was superposed on each of the above-described light-sensitive sheets, and image exposure was conducted through a continuous gradation wedge from the cover sheet side. Then, the above-described processing solution was spread in a thickness of 75 µm between these two sheets using pressure-applying rollers. The spread processing was conducted at 25°C. 100 Seconds after the processing, cyan color density of the image transferred on the mordanting layer (image-receiving layer) was measured through the transparent support of the light-sensitive sheet by a reflective densitometer. The results thus-obtained are shown in Table 4 below. As is apparent from the results shown in Table 4, Sample Nos. 1 to 6 containing the nucleating agent according to the present invention are preferred since they provide high D max as compared with Sample Nos. 7 to 9 for comparison.

Claims: A direct positive image forming method comprising development processing an imagewise exposed direct positive photographic light-sensitive material which comprises a support having thereon at least one layer containing internal latent image type silver halide grains not having been previously fogged after fogging treatment or while fogging treatment, wherein the fogging treatment is conducted in the presence of a compound represented by the following general formula (I): wherein A₁ and A₂ both represent a hydrogen atom or one of A1 and A₂ represent a hydrogen atom and the other represents an alkylsulfonyl group, an arylsulfonyl group or an acyl group; G₁ represents a carbonyl group, a sulfonyl group, a sulfoxy group, or an iminomethylene group; L₁ represents a divalent linkage group; X₁ represents -0- or (wherein R₄ represents a hydrogen atom, an alkyl group or an aryl group); Y₁ represents R₁ and R₂ each represents an aliphatic group, an aromatic group, a heterocyclic group, -OR₅ or -NR₅R₆ (wherein R₅ represents an aliphatic group, an aromatic group or a heterocyclic group; and R₆ represents a hydrogen atom, an aliphatic group, an aromatic group or a heterocyclic group); and R₃ represents a hydrogen atom, an alkyl group, an aryl group, an alkoxy group, an aralkyl group, an aryloxy group or an amino group which groups may be substituted. The direct positive image forming method of claim 1, wherein the alkylsulfonyl or arylsulfonyl group or acyl group represented by A₁ or A₂ has up to 20 carbon atoms. The direct positive image forming method of claim 1, wherein both A₁ and A₂ are a hydrogen atom. The direct positive image forming method of claim 1, wherein the aliphatic group represented by R₁, R₂, R₅ or R₆ is a straight chain, branched chain or cyclic alkyl group, alkenyl group or alkynyl group each containing up to 30 carbon atoms, and the branched chain alkyl group may contain one or more hetero atoms therein to form a saturated hetero ring. The direct positive image forming method of claim 1, wherein the aromatic group represented by R₁, R₂, R₅ and R₆ is a monocyclic or dicyclic aryl group. The direct positive image forming method of claim 1, wherein the heterocyclic group represented by R₁, R₂, R₅ or R₆ is a 3-membered to 10-membered saturated or unsaturated heterocyclic group containing at least one of a nitrogen atom,an oxygen atom or a sulfur atom which may be a monocyclic ring or form a condensed ring together with an aromatic ring or a heterocyclic ring. The direct positive image forming method of claim 1, wherein a substituent for the aliphatic group, aromatic group or heterocyclic group represented by R₁, R₂, R₅ or R₆ is selected from an alkyl group, an aralkyl group, an alkoxy group, an aryl group, a substituted amino group, an acylamino group, a sulfonylamino group, a ureido group, a urethane group, an aryloxy group, a sulfamoyl group, a carbamoyl group, an alkylthio group, an arylthio group, a sulfonyl group, a sulfinyl group, a hydroxyl group, a halogen atom, a cyano group, a sulfo group and a carboxy group. The direct positive image forming method of claim 1, wherein R₁ or R₂ may combine with L₁ to form a ring, or R₁ and R₂ may combine with each other to form a ring. The direct positive image forming method of claim 1, wherein the divalent linkage group represented by L₁ is an atom or an atomic group including at least one of a carbon atom, a nitrogen atom, a sulfur atom and an oxygen atom. The direct positive image forming method of claim 9, wherein the divalent linkage group represented by L₁ is an arylene group. The direct positive image forming method of claim 9, wherein a substituent for the divalent linkage group represented by L₁ is selected from an alkyl group, an aralkyl group, an alkoxy group, an aryl group, an aryloxy group, an alkenyl group, an alkylthio group, an arylthio group, a sulfonyl group, a sulfinyl group, a halogen atom, a cyano group, an acyl group, a nitro group and The direct positive image forming method of claim 1, wherein G₁ represents a carbonyl group, and R₃ represents a hydrogen atom, an alkyl group, an aralkyl group or an aryl group. The direct positive image forming method of claim 1, wherein G₁ represents a sulfonyl group, and R₃ represents an alkyl group, an aralkyl group, an aryl group or a substiuted amino group. The direct positive image forming method of claim 1, wherein G₁ represents a sulfoxy group, and R₃ represents a cyanobenzyl group or a methylthiobenzyl group. The direct positive image forming method of claim 1, wherein G₁ represents and R₃ represents a methoxy group, an ethoxy group, a butoxy group, a phenoxy group or a phenyl group. The direct positive image forming method of claim 1, wherein G₁ represents an N-substituted or unsubstituted iminomethylene group, and R₃ represents a methyl group, an ethyl group or a substituted or unsubstituted phenyl group. The direct positive image forming method of claim 1, wherein a substituent from the group represented by R₃ is selected from an alkyl group, an aralkyl group, an alkoxy group, an aryl group, a substituted amino group, an acylamino group, a sulfonylamino group, a ureido group, a urethane group, an aryloxy group, a sulfamoyl group, a carbamoyl group, an alkylthio group, an arylthio group, a sulfonyl group, a sulfinyl group, a hydroxyl group, a halogen atom, a cyano group, a sulfo group, a carboxy group, an acyloxy group, an acyl group, an alkyloxycarbonyl group, an aryloxycarbonyl group, an alkenyl group, an alkynyl group and a nitro group, which groups may be further substituted. The direct positive image forming method of claim 1, wherein G₁ represents a carbonyl group, and R₃ represents a hydrogen atom or a group represented by the following general formula (a): -L₂-Z₁ (a) wherein Z₁ represents a group capable of cleaving the G₁-L₂-Z₁ moiety from the remainder molecule upon a nucleophilic attack on G₁; and L₂ is a divalent organic group capable of forming a G₁, L₂ and Z₁ cyclic structure upon the nucleophilic attack of Z₁ on G₁. The direct positive image forming method of claim 18, wherein the group represented by Z₁ is a functional group selected from -OH, -SH, NHR₇ (wherein R₇ represents a hydrogen atom, an alkyl group, an aryl group, a heterocyclic group, COR₈ or -SO₂R₈; and R₈ represents a hydrogen atom, an alkyl group, an aryl group or a heterocyclic group) or -COOH, or a functional group selected from (wherein R₉ and R₁₀ each represents a hydrogen atom, an alkyl group, an alkenyl group, an aryl group or a heterocyclic group). The direct positive image forming method of claim 18, wherein the divalent organic group represented by L₂ is an atom or an atomic group including at least one of a carbon atom, a nitrogen atom, a sulfur atom and an oxygen atom. The direct positive image forming method of claim 18, wherein the group represented by the general formula (a) is a group represented by the following general formula (b): wherein R b ¹, R b ², R b ³ and R b ⁴, which may be the same or different, each represents a hydrogen atom, an alkyl group, an alkenyl group or an aryl group; B represents an atomic group necessary to form a 5-membered or 6-membered ring which may be substituted; m and n each represents 0 or 1, when Z₁ is -COOH, n+m is 0 or 1, and when Z₁ is -OH, -SH or -NHR₄, n+m is 1 or 2; and Z₁ has the same meaning as defined in the general formula (a). The direct positive image forming method of claim 21, wherein m is 0 and n is 1. The direct positive image forming method of claim 21, wherein the ring formed with B is a benzene ring. The direct positive image forming method of claim 18, wherein the group represented by the general formula (a) is a group represented by the following general formula (c): wherein Rc¹ and Rc², which may be the same or different, each represents a hydrogen atom, an alkyl group, an alkenyl group, an aryl group or a halogen atom; Rc³ represents a hydrogen atom, an alkyl group, an alkenyl group or an aryl group; p represents 0 or 1; q represents 1, 2, 3 or 4; and Z₁ has the same meaning as defined in the general formula (a), or Rc¹, Rc² and Rc³ may combine with each other to form a ring as far as the resulting structure makes possible an intramolecular nucleophilic attack of Z₁ on G₁; and when q represents 2 or 3, two or three CRc¹Rc²'s may be the same or different. The direct positive image forming method of claim 24, wherein Rc¹ and Rc² each represents a hydrogen atom, a halogen atom or an alkyl group, Rc³ represents an alkyl group or an aryl group, and when q is 1, p is 0 or 1, when q is 2, p is 0 or 1, and when q is 3, p is 0 or 1. The direct positive image forming method of claim 1, wherein X₁ represents -NR₄- wherein R₄ represents a hydrogen atom. The direct positive image forming method of claim 1, wherein Y₁ represents The direct positive image forming method of claim 1, wherein R₁ or R₂ contains a ballast group. The direct positive image forming method of claim 1, wherein R₁, R₂, L₁ or R₃ contains an adsorption accelerating group on the surface of the silver halide represented by the following formula: Y₂(L₃ wherein Y₂ represents an adsorption accelerating group for silver halide; L₃ represents a divalent linkage group; and ℓ represents 0 or 1. The direct positive image forming method of claim 29, wherein the adsorption accelerating group represented by Y₂ is a thioamido group, a mercapto group, a group having a disulfido bond, or a 5-membered or 6-membered nitrogen-containing heterocyclic group. The direct positive image forming method of claim 30, wherein the thioamido adsorption accelerating group represented by Y₂ is a divalent group represented by which may be part of a ring structure or an acylic thioamido group. The direct positive image forming method of claim 29, wherein Y₂ is a cyclic thioamido group or a nitrogen-containing heterocyclic group. The direct positive image forming method of claim 29, wherein the divalent linkage group represented by L₃ is an atom or an atomic group including at least one of a carbon atom, a nitrogen atom, a sulfur atom and an oxygen atom. The direct positive image forming method of claim 1, wherein the compound is represented by the following general formula (Ia): wherein R₁₂ has the same meaning as R₁ or R₂ in the general formula (I); k represents 0, 1 or 2; and R₁, R₂, R₃, R₄, A₁, A₂ and G₁ each has the same meaning as defined in the general formula (I). The direct positive image forming method of claim 34, wherein the group is present at the o- or p-position to the hydrazino group. The direct positive image forming method of claim 1, wherein the compound represented by the general formula (I) is present in the direct positive photographic light-sensitive material. The direct positive image forming method of claim 1, wherein the pH of the color developing solution is used in the development process is in a range from 9.0 to 12.0. The direct positive image forming method of claim 37, wherein the pH is in a range from 9.5 to 11.5. The direct positive image forming method of claim 38, wherein the pH is in a range from 9.8 to 11.0. A direct positive photographic light-sensitive material comprising a support having thereon at least one internal latent image type silver halide emulsion layer not having been previously fogged, wherein the photographic light-sensitive material contains at least one compound represented by the following general formula (I): wherein A₁ and A₂ both represent a hydrogen atom or one of A₁ and A₂ represents a hydrogen atom and the other represents an alkylsulfonyl group, an arylsulfonyl group or an acyl group; G₁ represents a carbonyl group, a sulfonyl group, a sulfoxy group, or an iminomethylene group; L₁ represents a divalent linkage group; X₁ represents -O- or (wherein R₄ represents a hydrogen atom, an alkyl group or an aryl group); Y₁ represents or R₁ and R₂ each represents an aliphatic group, an aromatic group, a heterocyclic group, -OR₅ or -NR₅R₆ (wherein R₅ represents an aliphatic group, an aromatic group or a heterocyclic group; and R₆ represents a hydrogen atom, an aliphatic group, an aromatic group or a heterocyclic group); and R₃ represents a hydrogen atom, an alkyl group, an aryl group, an alkoxy group, an aralkyl group, an aryloxy group or an amino group which groups may be substituted. The direct positive photographic light-sensitive material of claim 40, wherein the compound represented by the general formula (I) is present in an internal latent image type silver halide emulsion layer, an intermediate layer, a subbing layer or a backing layer. The direct positive photographic light-sensitive material of claim 42, wherein the compound is present in an internal latent image type silver halide emulsion layer. The direct positive photographic light-sensitive material of claim 41, wherein the internal latent image type silver halide emulsion layer is a monodisperse silver halide emulsion layer. The direct positive photographic light-sensitive material of claim 41, wherein the photographic light-sensitive material further contains a color coupler. The direct positive photographic light-sensitive material of claim 44, wherein the color coupler is selected from a naphtholic or phenolic cyan coupler, a pyrazolone or pyrazoloazole magenta coupler and an open chain or heterocyclic ketomethylene yellow coupler. The direct positive photographic light-sensitive material of claim 41, wherein the photographic light-sensitive material comprises at least one red-sensitive silver halide emulsion layer containing at least one cyan forming coupler, at least one green-sensitive silver halide emulsion layer containing at least one magenta forming coupler and at least one blue-sensitive silver halide emulsion layer containing at least one yellow forming coupler. The direct positive photographic light-sensitive material of claim 41, wherein the photographic light-sensitive material further contains a nucleation accelerating agent. The direct positive photographic light-sensitive material of claim 47, wherein the nucleation accelerating agent is a compound represented by the following general formula (II) or (III): wherein Q represents an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring to which a carbocyclic aromatic ring or a heterocyclic aromatic ring may further be condensed; L represents a divalent linkage group comprising an atom or atomic group selected from the group consisting of a hydrogen atom, a carbon atom, a nitrogen atom, an oxygen atom, and a sulfur atom; R₁₈ represents an organic group containing at least one of a thioether group, an amino group, an ammonium group, an ether group, or a heterocyclic group; n represents 0 or 1; m represents 0, 1 or 2; and M represents a hydrogen atom, an alkali metal atom, an ammonium group or a group capable of being cleaved under an alkaline condition; wherein Q′ represents an atomic group necessary to form a 5-membered or 6-membered heterocyclic ring which is capable of forming imino silver; L, R₁₈, n and M each has the same meaning as defined in the general formula (II) above; and m represents 1 or 2. The direct positive photographic light-sensitive material of claim 48, wherein the heterocyclic ring completed with Q is substituted with a substituent selected from a nitro group, a halogen atom, a mercapto group, a cyano group, a substituted or unsubstituted alkyl group, a substituted or unsubstituted aryl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aralkyl group, a sulfonyl group, a carbamoyl group, a sulfamoyl group, a carbonamido group, a sulfonamido group, an acyloxy group, a sulfonyloxy group, a ureido group, a thioureido group, an acyl group, an oxycarbonyl group, and an oxycarbonylamino group. The direct positive photographic light-sensitive material of claim 48, wherein the heterocyclic ring completed with Q is a tetrazole, a triazole, an imidazole, a thiadiazole or an oxadiazole. The direct positive photographic light-sensitive material of claim 48, wherein the heterocyclic ring represented by Q' is an indazole, a benzimidazole, a benzotriazole, a benzoxazole, a benzothiazole, an imidoazole, a thiazole, an oxazole, a triazole, a tetrazole, a tetraazaindene, a triazaindene, a diazaindene, a pyrazole or an indole. The direct positive photographic light-sensitive material of claim 48, wherein the nucleation accelerating agent is a compound represented by the following general formula (IV), (V), (VI) or (VII): wherein M, R₁₈, L and n each has the same meaning as defined in the general formula (II); and X represents an oxygen atom, a sulfur atom or a selenium atom; wherein R₂₉ represents a hydrogen atom, a halogen atom, a nitro group, a mercapto group, an unsubstituted amino group, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted aryl group or (L R₁₈; R₃₀ represents a hydrogen atom, an unsubstituted amino group or (L -R₁₈, when both R₂₉ and R₃₀ represent (L R₁₈, they may be the same or different, provided that at least one or R₂₉ and R₃₀ represents (L R₁₈, L and n each has the same meaning as defined in the general formula (II); wherein R₃₁ represents (L R₁₈ ; and M, R₁₈, L and n each has the same meaning as defined in the general formula (II); wherein R₃₂ and R₃₃, whch may be the same or different, each represents a hydrogen atom, a halogen atom, a substituted or unsubstituted amino group, a nitro group, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aralkyl group or a substituted or unsubstituted aryl group; M and R₃₁ each has the same meaning as defined in the general formula (VI). The direct positive photographic light-sensitive material of claim 47, wherein the nucleation accelerating agent is present in an internal latent image type silver halide emulsion layer or a hydrophilic colloid layer.

Inventors: INOUE NORIYUKI FUJI PHOTO FILM, YAGIHARA MORIO FUJI PHOTO FILM, INOUE, NORIYUKI FUJI PHOTO FILM CO., LTD., YAGIHARA, MORIO FUJI PHOTO FILM CO., LTD.
Applicants: FUJI PHOTO FILM CO LTD, FUJI PHOTO FILM CO., LTD.
Application year: 1989
Main classification: G03C1
IPC codes: G03C1, G03C7