Process for the preparation of zeolitic catalysts

Abstract: Process for the preparation of a zeolitic catalyst which comprises treating a zeolite of the Y-type having an alkali metal oxide/aluminium oxide molar ratio of at most 0.13 with a solution of a multi-valent metal salt having a cationic radius between 0.6 and 1.0 Å and combining the ion-exchanged zeolite without a calcination step with a hydrogenation component of a Group 8 and/or Group 6b metal.

Description: The present invention relates to a process for the preparation of zeolitic catalysts, and their use in hydrocracking processes. The use of zeolites as catalysts and/or catalyst carriers has long been recognized and many methods to improve zeolitic base materials haven been reported in the art. In zeolite research and development much attention has been devoted to physically changing the nature and possibly the properties of zeolitic base materials, e.g. by calcining, calcining under so-called selfsteaming conditions or by wet calcination. Also treatment with ammonium ions in various stages of the zeolite preparation procedures has been reported. It has also been reported that zeolites can be modified by treating them with certain metal salt solutions in combination with various pre- and after-treatments to ensure that the zeolites are produced in the most active form. In this respect reference is made to US-A-4,415,519, describing a zeolite modification in which a sodium-type Y zeolite is exchanged with an ammonium salt solution, the ammonium exchanged zeolite is calcined, e.g. in a self-steaming condition, and the calcined product is reacted with an acidic aluminium salt solution. Subsequently, the aluminium-exchanged zeolite is again subjected to ammonium-exchange. It has now been found that zeolitic catalysts with interesting properties can be produced by ion-exchange of low alkali metal oxide-containing zeolites with certain metal salts, and subsequently, without a calcination treatment, combining the ion-exchanged zeolites with a hydrogenation component of a Group 8 metal and/or a Group 6b metal. The catalysts thus prepared are of importance as hydrocracking catalysts. The present invention therefore provides a process for the preparation of a zeolitic catalyst, which comprises treating a zeolite of the Y-type having an alkali metal oxide/aluminium oxide molar ratio of at most 0.05 with a solution of a multi-valent metal salt comprising as cation Ag²⁺, Bi³⁺, Bi⁵⁺, Ca²⁺, Cd²⁺, Co²⁺, Co³⁺, Cr²⁺, Cr³⁺, Cu²⁺, Fe²⁺, Fe³⁺, Ga³⁺, In³⁺, Ir⁴⁺, Mg²⁺, Mn²⁺, Mn³⁺, Mn⁴⁺, Mo⁴⁺, Pb⁴⁺, Pd²⁺, Pd⁴⁺, Pt²⁺, Pt⁴⁺, Re⁴⁺, Rh³⁺, Ru⁴⁺, Sn²⁺, Sn⁴⁺, Ta⁵⁺, Ti²⁺, Ti³⁺, Ti⁴⁺, Tl³⁺, V³⁺, V⁴⁺, W⁴⁺, W⁶⁺, or Zn²⁺ and combining the ion-exchanged zeolite without a calcination step with a hydrogenation component of a Group 8 and/or Group 6b metal. Zeolites of the Y-type having an alkali metal oxide/aluminium oxide molar ratio of at most 0.05 and in particular a sodium oxide content of at most 2% by weight can suitably be obtained from high alkali metal oxide-containing Y-zeolites by treatment in one or several stages with an ammonium salt solution to reduce the amount of alkali metal to the desired level. Commercially available zeolites, such as Na-Y can be suitably applied as starting materials. Normally, Na-Y zeolites can contain up to about 13.5% by weight of sodium oxide. From for instance FR-A-2,371,231 a process is known wherein Na-Y zeolites containing high amounts of sodium oxide are directly subjected to an ion-exchange treatment. The treatment(s) with an ammonium salt such as ammonium chloride or ammonium sulphate are well known to those skilled in the art. It should be noted that the process according to the present invention provides a method for directly preparing a zeolitic catalyst from a low alkali metal oxide-containing zeolite Y essentially without lowering the unit cell size of the zeolite by calcination after the ion-exchange with a solution of a multi-valent metal salt having a cationic radius between 0.06 and 0.1 nm (0.6 and 1.0 Å). Numerical values of the radii of ions may slightly vary, depending on how they were measured. The values used for this specification have been taken from CRC Handbook of Chemistry and Physics, Cleveland, Ohio, 56th ed, 1975-1976, pages F-209 and F-210. Preference is given to the use of metal salts having cationic radii between 0.06 and 0.08 nm (0.60 and 0.80 Å), in particular to the appropriate salts of gallium, iron, copper, magnesium, cobalt and nickel. Good results have been obtained using gallium and nickel salts. Salts which can be suitably applied comprise inorganic salts such as nitrates and sulphates as well as the appropriate halides. Preference is given to the use of nitrates and chlorides and in particular to nitrates because of their water solubility which facilitates handling of the materials concerned. It is also possible to use (slightly) soluble salts of organic acids such as formates, acetates and propionates. If desired, mixtures of two or more metal salts can be used in the process according to the present invention. The amount of metal salts to be used can be varied between wide ranges, depending to some extent on the nature of the metal applied. Normally, solutions containing between 0.005 and 2 moles of metal salt per litre water can be suitably applied, preference being given to concentrations between 0.01 and 1 mole per litre. The starting zeolite Y material contains at most an alkali metal oxide/aluminium oxide molar ratio of 0.05 (which may have been obtained by an ion-exchange treatment of a zeolite Y containing a higher amount of alkali metal oxide). The starting material is subjected to an ion-exchange with a solution containing the appropriate metal salt(s). The ion-exchange may be carried out by any technique known in the art. If desired the ion-exchange may be repeated a number of times. The ion-exchange is normally carried out at a relatively low temperature, e.g. at temperatures between 10 and 95 °C. Good results have been obtained by carrying out the ion-exchange at a temperature between 20 and 95 °C. It will normally be carried out during a time between 15 minutes and 24 hours. Preference is given to a treatment time between 30 minutes and 6 hours. In the process according to the present invention zeolites having a unit cell size between 2.419 and 2.465 nm (24.19 and 24.65 Å) can be suitably employed. Preferably, zeolites as described in EP-A-0 247 678 and EP-A-0 247 679, are used. After the ion-exchange with the appropriate metal-ion salt solution, the zeolites thus treated with be normally subjected to drying before being combined with a hydrogenation component. Drying is normally achieved by gentle heating of the material concerned at a temperature ranging from ambient to about 200 °C. The drying procedure may be carried out in air or by using an inert gas such as nitrogen. Partial drying is also possible. In contrast, a calcination is normally performed at temperatures between 350 and 800 °C, and usually between 500 and 750 °C, optionally in the presence of steam. The duration of a calcination may vary between wide ranges, from less than 30 minutes to up to 24 hours, depending predominantly on the properties of the zeolite Y as envisaged. The zeolites as produced by the ion-exchange with the metal salt solution, and optionally after drying, are not subjected to the above calcination. Suitable hydroconversion catalysts comprise, apart from one or more zeolites and hydrogenation components, a binder. Binders such as silica, alumina, silica-alumina, clays, zirconia, silica-zirconia, titania, silica-boria and mixtures thereof can be suitable applied. Alumina is a preferred binder. Suitably 10-95 %w of binder can be used. Preferably, 15-75 %w of binder is used. The ion-exchanged zeolite is combined with a hydrogenation component of a Group 8 and/or Group 6b metal. This combining can be carried out by any method known in the art. Preferably this combining is carried out by impregnation and in particular co-mulling. In co-mulling the ion-exchanged zeolite is mixed with the hydrogenating component(s), and optionally a binder, in the presence of water, so that an extrudable paste is obtained. A description of co-mulling can be found in US-A-3,853,747. Preferably, the combining of the ion-exchanged zeolite with the hydrogenation component(s) is carried out by co-mulling the ion-exchanged zeolite, hydrogenation component(s) and binder. Another preferred embodiment of the present invention is to combine the ion-exchanged zeolite with a mixture of refractory oxides, in particular with a mixture of silica-alumina and alumina. The silica-alumina present will then not only serve as binder but also as amorphous hydroconversion (hydrocracking) component. The weight percentage of zeolite in the combination zeolite/silica-alumina is preferably from 5-80, the weight percentage of silica-alumina in this combination is preferably from 5-80, the balance being alumina. The present invention further relates to a hydrocracking process in which a hydrocarbonaceous feedstock is contacted in the presence of hydrogen and under hydrocracking conditions with a hydrocracking catalyst comprising a zeolite of the Y-type having an alkali metal oxide/aluminium oxide of at most 0.13 and multivalent cations with a cationic radius between 0.06 and 0.10 nm (0.6 and 1.0 Å) at ion-exchangeable positions, and at least one hydrogenation component of a Group 8 metal and/or of a Group 6b metal. Suitably, the hydrocracking catalyst comprises one or more components of nickel and/or cobalt and one or more components of molybdenum and/or tungsten or one or more components of platinum and/or palladium. The amount(s) of hydrogenation component(s) in the catalyst suitably range(s) between 0.05 and 10 parts by weight (pbw) of Group 8 metal component(s) and between 2 and 40 pbw of Group 8 metal component(s), calculated as metal(s) per 100 pbw of total catalyst. The hydrogenation components in the catalyst may be in the oxidic and/or the sulphidic form. If a combination of at least a Group 6 and a Group 8 metal component is present as (mixed) oxides, it will be normally subjected to a sulphiding treatment prior to proper use in hydrocracking. As indicated above, the catalysts preferably comprise further a binder. Feedstocks which can be suitably subjected to a hydroconversion process using catalysts in accordance with the present invention comprise gas oils, deasphalted oils, coker gas oils and other thermally cracked gas oils and syncrudes, optionally originating from tar sands, shale oils, residue upgrading processes or biomass. Combinations of various feedstocks can also be applied. It may be desirable to subject part or all of the feedstock to one or more (hydro)treatment steps prior to its use in the hydroconversion process. It is often found convenient to subject the feedstock to a (partial) hydrotreatment. When rather heavy feedstocks are to be processed it may be advantageous to subject such feedstocks to a (hydro)demetallization treatment. Suitable process conditions for the hydroconversion process comprise temperatures in the range from 250 to 500 °C, pressures of up to 300 bar and space velocities between 0.1 and 10 kg feed per litre of catalyst per hour (kg/l.h). Gas/feed ratios of 100 to 5000 Nl/kg feed can suitably be used. Preferably, the hydroconversion process is carried out at a temperature between 300 and 470 °C, a pressure between 25 and 200 bar and a space velocity between 0.2 and 5 kg feed per litre of catalyst per hour. Preferably, gas/feed ratios between 250 and 2000 Nl/kg are applied. The present invention will now be illustrated by means of the following Examples. EXAMPLE 1 A crystalline zeolite Y as described in EP-A-0 247 679, having a typical sodium oxide content of 0.1 %wt, a sodium oxide/aluminium oxide molar ratio of about 0.011 and a unit cell size of 2.433 nm (24.33 Å) was subjected to an ion-exchange treatment with a solution (10 ml per gramme of crystalline alumino-silicate) of 0.2 M gallium nitrate (Ga³⁺ radius: 0.062 nm (0.62 Å)). The ion-exchange treatment was carried out for one hour under reflux conditions. After filtration, the product obtained was washed and subjected to a drying procedure at 120 °C during 16 hours. The dried zeolite was mixed with hydrated aluminium oxide (boehmite), a solution of nickel nitrate (4.75 g) and ammonium metatungstate (18.82 g calculated as WO₃). The resulting mixture was co-mulled for 0.45 hours, and subsequently extruded to produce extrudates. The extrudates were dried for 2 hours at 120 °C and finally calcined for 2 hours at 500 °C. The calcined extrudates contained 6.7 %wt Ga, 2.6 %wt Ni and 8.2 %wt W, calculated as metals on total catalyst. The weight ratio of zeolite Y and alumina binder was 4:1. EXAMPLE 2 A similar procedure as described in Example 1 was carried out using the same type of zeolite Y but a nickel nitrate solution in an amount of 10 ml of 1 M nickel nitrate solution per gram of zeolite (Ni²⁺ radius 0.069 nm (0.69 Å)). After drying of the ion-exchanged zeolite the Ni-containing zeolite (1.3 %wt Ni) was subjected to the same treatment as described for the Ga-containing zeolite in Example 1, yielding a calcined product containing 3.7 %wt Ni and 8.2 %wt W, calculated as metals on total catalyst. The weight ratio of zeolite Y and alumina binder was 4:1. COMPARATIVE EXPERIMENT A similar procedure as described in Examples 1 and 2 was carried out using an aluminium nitrate solution in an amount of 10 ml 1 M aluminium nitrate solution per gram of zeolite. The cationic radius of Al³⁺ is 0.051 nm (0.51 Å). The resulting catalyst contained 2.6 %wt Ni and 8.2 %wt W. EXAMPLE 3 This example shows the advantages of the zeolitic catalysts according to the invention in a hydrocracking process. The catalysts of Examples 1 and 2 (catalysts 1 and 2, respectively) were compared with the catalyst of the Comparative Experiment, catalyst 3, and a catalyst 4 according to EP-A-0 247 679, i.e. using the same type of zeolite Y, but prepared without the relevant ion-exchange step and prepared by impregnation of calcined compositions of zeolite Y and alumina. Catalyst 4 contained 2.6 %wt Ni and 8.2 %wt W, based on total catalyst. The weight ratio of the zeolite Y and the alumina binder was 4:1. The catalyst was tested in a hydrocracking experiment using a hydrocarbon feedstock having the following characteristics: C (%wt) 86.2 H (%wt) 13.8 d (70/4) 0.826 viscosity (100 °C) 487 cm²/s (4.87 cS)(ASTM-D-445) viscosity ( 60 °C) 1243 cm²/s (12.43 cS)(ASTM-D-445) RCT (%wt) 0.05 (ASTM-D-542) I.B.P. 205 °C 10/20 332/370 30/40 392/410 50/60 428/448 70/80 467/492 90 525 F.B.P. 598 The catalyst was diluted with 0.2 mm SiC particles on a 1:1 volume ratio. The catalyst was then presulphided. The subsequent hydrocracking was carried out under the following operation conditions: WHSV 1.1 kg.l⁻¹.h⁻¹ H₂S partial pressure 1.4 bar total pressure 130 bar gas/feed ratio 1,000 Nlkg⁻¹. The experiment was carried out in once-through operation. The catalyst performance is expressed as the temperature required to achieve 70% by weight conversion of 300 °C⁺ material. The results are indicated in TABLE 1: Experiment No. 1 2 3 4 Catalyst No. 1 2 3 4 Temperature required (70 %wt conversion), °C 330 325 325 325 Distribution of 300 °C⁻ product, %wt C 1-4 5.8 4.2 6.1 6.1 C₅-130 °C 40.0 41.7 44.4 44.0 130 °C -300 °C 53.2 47.1 49.5 49.9 From the results it is apparent that the catalysts according to the invention produce less gaseous products (C₁₋₄) than the catalysts 3 and 4, whereby catalyst 1 gives an increased middle distillate yield and catalyst 2 gives an enhanced naphtha yield. From comparison between catalysts 3 and 4 it is apparent that when the ion-exchange is carried out with the Al³⁺ ion, having a too small ionic radius, the performance of the resulting catalyst hardly changes in comparison with a catalyst prepared without the present ion-exchange step. EXAMPLE 4 A Ni-containing zeolite Y obtained after ion-exchange and drying as in Example 2, was mixed with silica-alumina (weight ratio SiO₂:Al₂O₃=3:1), alumina and nickel nitrate solution and molybdenum trioxide. After co-mulling, extrusion, drying and calcination a catalyst was obtained comprising 12.9 %wt Mo and 8.2 %wt Ni, whereby the weight ratio zeolite Y/silica-alumina/alumina was 30:40:30. EXAMPLE 5 Catalyst 5 was compared with a catalyst 6 prepared according to EP-A-0 247 678, i.e. by mixing a zeolite Y with silica-alumina (weight ratio SiO₂:Al₂O₃=3:1) and alumina, extruding the mixture to yield extrudates, drying and calcining the extrudates and depositing Ni and Mo upon the extrudates by impregnation. Catalyst 6 contained 7.8 %wt Ni, 12.9 %wt Mo and the weight ratio zeolite Y/silica-alumina/alumina was 30:40:30. The catalysts were subjected to a hydrocracking process in which the following feedstocks were employed. Feedstock I Feedstock II C (%wt) 86.4 C (%wt) 86.4 H (%wt) 13.6 H (%wt) 13.6 N (ppmw) 4 N (ppmw) 12 Boiling characteristics, °C Boiling characteristics, °C 2/10 290/328 2/10 287/353 20/30 368/396 20/30 384/407 40/50 420/440 40/50 426/444 60/70 460/482 60/70 460/481 80/90 508/542 80/90 505/539 540⁺ °C, (%wt) 10.5 540⁺ °C, (%wt) 9.8 The temperature required to get a 56 %wt conversion was determined as well as the produce distribution. After having run for 125 hours on feedstock I, the feedstock was changed and feedstock II was used. The produce distribution and the temperature required to get a 56 %wt conversion after having run for 200 hours on feedstock II was determined, too. The process conditions were a total pressure of 125 bar, a H₂S partial pressure of 2.4 bar, a space velocity of 0.75 kg/l.hr and a gas/feedstock ratio of 1500 Nl/kg. The results are shown in Table II. Experiment No. 5 6 Catalyst No. 5 6 Feedstock I T required, °C 323 312 Product distribution, %wt C 1-14 4 6 C₅-130 °C 32 31 130-300 °C 64 63 Feedstock II T required, °C 325 326 Product distirbution, %wt C 1-4 4 4 C₅-130 °C 27 32 130-300 °C 69 64 From the above results it is apparent that at low nitrogen content the selectivity of the catalyst 5 to C₁₋₄ hydrocarbons is smaller than that of the prior art catalyst. Further the nitrogen sensitivity, as defined as the temperature difference required to obtain a 56 %wt conversion at 4 and at 12 ppmw N, is for catalyst 6 significant, whereas the N sensitivity of catalyst 5 is small.

Claims: Hydrocracking process in which a hydrocarbonaceous feedstock is contacted in the presence of hydrogen and under hydrocracking conditions with a hydrocracking catalyst comprising a zeolite of the Y type having an alkali metal oxide/aluminium oxide molar ratio of at most 0.13 and multivalent cations with a cationic radius between 0.06 and 0.10 nm (0.6 and 1.0 Å) at ion-exchangeable positions, and at least one hydrogenation component of a Group 8 and/or Group 6b metal. Hydrocracking process according to claim 1, wherein the hydrogenation components having been selected from nickel, cobalt, tungsten, molybdenum, platinum and palladium components. Hydrocracking process according to claim 1 or 2, in which the hydrocracking catalyst further comprises a binder. Hydrocracking process according to any one of claims 1-3, in which the temperature is from 250 to 500 °C, the hydrogen pressure is up to 300 bar, the space velocity is from 0.1 to 10 kg/l.h and the H₂/feedstock ratio is from 100 to 5000 Nl/kg. Process for the preparation of a zeolitic catalyst which comprises treating a zeolite of the Y-type having an alkali metal oxide/aluminium oxide molar ratio of at most 0.05 with a solution of a multi-valent metal salt comprising as cation Ag²⁺, Bi³⁺, Bi⁵⁺, Ca²⁺, Cd²⁺, Co²⁺, Co³⁺, Cr²⁺, Cr³⁺, Cu²⁺, Fe²⁺, Fe³⁺, Ga³⁺, In³⁺, Ir⁴⁺, Mg²⁺, Mn²⁺, Mn³⁺, Mn⁴⁺, Mo⁴⁺, Pb⁴⁺, Pd²⁺, Pd⁴⁺, Pt²⁺, Pt⁴⁺, Ir⁴⁺, Mg²⁺, Mn²⁺, Mn³⁺, Mn⁴⁺, Mo⁴⁺, Pb⁴⁺, Pd²⁺, Pd⁴⁺, Pt²⁺, Pt⁴⁺, Re⁴⁺, Rh³⁺, Ru⁴⁺, Sn²⁺, Sn⁴⁺, Ta⁵⁺, Ti²⁺, Ti³⁺, Ti⁴⁺, Tl³⁺, V³⁺, v⁴⁺, W⁴⁺, W⁶⁺ or Zn²⁺ and combining the ion-exchanged zeolite without a calcination step with a hydrogenation component of a Group 8 and/or Group 6b metal. Process according to claim 5 wherein a starting Y zeolite is used which has been obtained by subjecting a high sodium oxide containing Y zeolite to a treatment with an ammonium compound. Process according to claim 5 or 6 wherein a solution of a multi-valent metal ion is used having a cationic radius between 0.060 and 0.080 nm (0.60 and 0.80 Å). Process according to claim 7 wherein use is made of one ore more salts of gallium, iron, copper, magnesium and cobalt. Process according to claim 8 wherein use is made of a gallium salt. Process according to any one of claims 5-9 wherein use is made of a nitrate or a chloride of a multivalent metal. Process according to any one of claims 5-10 wherein use is made of a solution of a multi-valent metal salt having a molarity between 0.005 and 2. Process according to claim 11 wherein use is made of a solution of a multi-valent metal salt having a molarity between 0.01 and 1. Process according to any one of claims 5-12 wherein the treatment with the multi-valent metal salt solution is carried out at a temperature between 10 and 95 °C. Process according to any one of claims 5-13 wherein the ion-exchanged zeolite is subjected to a drying treatment at a temperature up to 200 °C. Process according to any one of claims 5-14 wherein the ion-exchanged zeolite is combined with the hydrogenation component(s) by impregnation, or, in particular, co-mulling. Process according to claim 15, in which the ion-exchanged zeolite is combined with the hydrogenation component(s) by co-mulling the ion-exchanged zeolite and hydrogenation component(s) together with a binder. Process according to claim 16, in which the binder is selected from the group of refractory oxides consisting of silica, alumina, silica-alumina, clays, zirconia, silica-zirconia, titania, silica-boria and mixtures thereof. Process according to claim 17, in which the binder is a mixture of silica-alumina and alumina.

Inventors: HOEK AREND, HUIZINGA TOM, KLAZINGA AAN HENDRIK, SCHAPER HENNIE, HOEK, AREND, HUIZINGA, TOM, KLAZINGA, AAN HENDRIK, SCHAPER, HENNIE
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1989
Main classification: B01J29
IPC codes: C10G47, B01J29, B01J37