A SYNTHETIC CRYSTALLINE ALUMINOPHOSPHATE COMPOSITION AND A METHOD OF ITS SYNTHESIS

Abstract: A crystalline aluminophosphate composition comprising crystals exhibiting the characteristic X-ray diffraction pattern (I) is synthesized from a reaction mixture containing a C5-C7 alkyldiamine as directing agent.

Description: A SYNTHETIC CRYSTALLINE ALUMINOPHOSIΗATE COMPOSITION AND A METHOD OF ITS SYNTHESIS This invention relates to a synthetic crystalline aluminophosphate composition and to a method of its synthesis. Zeolitic materials, both natural and synthetic, have been demonstrated in the past to have catalytic properties for various types of hydrocarbon conversion. Certain zeolitic materials are ordered, porous crystalline aluminosilicates having a definite crystalline structure as determined by X-ray diffraction, within which there are a large number of smaller cavities which may be interconnected by a number of still smaller channels or pores. These cavities and pores are uniform in size within a specific zeolitic material. Since the dimensions of these pores are such as to accept for adsorption molecules of certain dimensions while rejecting those of larger dimensions, these materials have come to be known as 'toolecular sieves" and are utilized in a variety of ways to take advantage of these properties. Such molecular sieves, both natural and synthetic, include a wide variety of positive ion-containing crystalline aluminosilicates. These aluminosilicates can be described as rigid three-dimensional frameworks of SiO. and A10. in which the tetrahedra are cross-linked by the sharing of oxygen atoms whereby the ratio of the total aluminum and silicon atoms to oxygen atoms is 1:2. The electrovalence of the tetrahedra containing aluminum is balanced by the inclusion in the crystal of a cation, for example an alkali metal or an alkaline earth metal cation. This can be expressed wherein the ratio of aluminum to the number of various cations, such as Ca/2, Sr/2, Na, K or Li, is equal to unity. One type of cation may be exchanged either entirely or partially with another type of cation utilizing ion exchange techniques in a conventional manner. Ey means of such cation exchange, it has been possible to vary the properties of a given aluminosilicate by suitable selection of the cation. Prior art techniques have resulted in the formation of a great variety of synthetic zeolites. The zeolites have come to be designated by letter or other convenient symbols, as illustrated by zeolite A (U.S. Patent 2,882,243), zeolite X (U.S. Patent 2,882,244), zeolite Y (U.S. Patent 3,130,007), zeolite Z -5 (U.S. Patent 3,247,195), zeolite ZK-4 (U.S. Patent 3,314,752), zeolite ZSM-5 (U.S. Patent 3,702,886), zeolite ZSM-11 (U.S. Patent 3,709,979), zeolite ZSM-12 (U.S. Patent 3,832,449), zeolite ZSM-20 (.U.S. Patent 3,972,983), zeolite ZSM-35 (U.S. Patent 4,016,245), 0 zeolite ZSM-38 (U.S. Patent 4,046,859), and zeolite ZSM-23 (U.S. Patent 4,076,842). Molecular sieve materials composed of a variety of crystalline aluminophosphate structures, and their synthesis from certain organic directing agents are also known (see U.S. Patent 5 No. 4,310,440). The present invention provides a novel aluminosphophate structure useful as a catalyst and its synthesis from a specific organic directing agent. Accordingly the invention resides in one aspect in a • 0 crystalline aluminophosphate composition comprising crystals exhibiting a characteristic X-ray diffraction pattern as shown in Table 1. In a further aspect the invention resides in a method for synthesizing a crystalline aluminophosphate composition having ' crystals exhibiting a characteristic X-ray diffraction pattern as shown in Table 1 of the specification, which comprises (i) ■ preparing a mixture comprising sources of an oxide of aluminum, an oxide of phosphorus, water and a directing agent (R), and having a composition, in terms of mole ratios, within the following ranges: to P 2 0 5 /Al 2 θ3 0.01 to 20 H2O/AI2O3 2 to 400 H AI2O3 0.01 to 30 R/A1 2 0 3 0.02 to 20 wherein R is a C -C- alkyldiamine, (ii) maintaining said mixture under conditions to produce said aluminophosphate and (iii) recovering said crystalline aluminophosphate from step (ii). Thus the crystalline aluminophosphate of the invention is distinguished from other aluminophosphate structures by the X-ray diffraction pattern having the characteristic lines listed in Table 1 below: Table 1 Interplanar d -Spacing (A) Relative Intensity (I/I 0 ) 13.721 + 0.1 w-m 9.449 + 0.1 vs 7.5257 0.1 w 6.688 + 0.05 w 5 5..992Z77 ++ 00..0055 w 5.204 T 0.05 w These X-ray diffraction data were collected with a Scintag diffraction s stem, equipped with a graphite diffracted beam monochromator and scintillation counter, using copper K-alpha radiation. The K-alpha 2 component of the K-alpha 1-K-alpha 2 doublet was removed with a computer stripping program. The effective X-ray wavelength for the tabulated data is. therefore the K-alpha 1 value of 1.5405 Angstroms. The diffraction data were recorded by step-scanning at 0.02 degrees of two-theta, where theta is the Bragg angle, and a counting time of 1 second for each step. The interplanar spacings, d's, were calculated in Angstrom units (A), and the relative intensities of the lines, I/I 0? where I is one-hundredth of the intensity of the strongest line, above background, were derived with the use of a profile fitting routine (or second derivative algorithm). The intensities are uncorrected for Lorentz and polarization effects. The relative intensities are given in terms of the symbols vs - very strong (75-100), s = strong (50-74), m = medium (25-49) and w - ** weak (0-24). It should be understood that diffraction data listed for this sample as single lines may consist of multiple overlapping lines which under certain conditions, such as differences in crystallite sizes or very high experimental resolution or crystallographic changes, may appear as resolved or partially resolved lines. Typically, crystallographic changes can include minor changes in unit cell parameters and/or a change in crystal symmetry, .without a change in topology of the structure. These minor effects, including changes in relative intensities, can also occur as a result of differences in cation content, framework composition, nature and degree of pore filling, and thermal and/or hydrothermal history. Normally the aluminophosphate of the invention has a composition which obeys the following formula, in terms of mole ratios of oxides: * * * ^ * C*^ __y * £^ _-_ ■ " • •< _« wherein v is the number of moles of A, occluded organic material resulting from organic directing agent used in synthesis of and filling microporous voids of the product crystals, which material may be removed upon calcination, w is moles of H_0, e.g» from 0 to about 5, M represents cations of valence m, N represents anions of valence n, and x and y are numbers which satisfy the following: 0.0K X4 1 0.01 < y-c 1 χ +y < l With the organic material and water removed from the presently synthesized composition, it will have the formula: • & !tΛ _-.r *CP --I_x !, ft_ The crystalline aluminophosphate of the invention is prepared from a reaction mixture hydrogel containing sources of aluminum oxide, phosphorus oxide, directing agent, and water and having a composition, in terms of mole ratios, within the following ranges: Broad Preferrred Most Preferred P2O5/AI2O3 0.01 to 20 0.2 to 5 0.5 to 2 H _i7O/A--I_22O-3 2 to 400 5 to 200 10 to 100 HVAI2Q3 0.01 to 30 0.5 to 20 1 to 10 0 R/AI2O3 0.02 to 20 0.1 to 10 0.5 to 5 where R is an organic directing agent and maintaining the mixture until crystals of the desired crystalline material are formed. The directing agent is a Cr- alkyldiamine, such as, for example, 5 pentanediamine, e.g. 1,5-pentanediamine, and heptanedia ine, e.g. 1 ,7-heptanediamine. The above reaction mixture can be prepared utilizing any materials which supply the appropriate oxide. The useful sources of aluminum oxide include, as non-limiting examples, any known form 0 of aluminum oxide or hydroxide, organic or inorganic salt or compound, e.g. alumina and aluminates. The useful sources of phosphorus oxide include, as non-limiting examples, any known form of phosphorus acids or phosphorus oxides, phosphates and phosphites, and organic derivatives of phosphorus. * ' Reaction conditions normally require heating the foregoing reaction mixture to a temperature of 80°C to 300°C for a period of time of 5 hours to 20 days. A more preferred temperature range is from 100°C to 200°C for 24 hours to 10 days. The reaction of the gel particles is carried out until 0 crystals form. The solid product comprising the desired aluminophosphate is then recovered from the reaction medium, such as by cooling the whole to room temperature, filtering and water washing. The above synthesis method is facilitated when the reaction mixture comprises at least 0.01%, preferably at least 0.10%, and even more preferably about 1% seed crystals such as those having the structure of the product crystals, based on total weight of crystalline material in the reaction mixture. While the aluminophosphate composition of the present invention may be used as a catalyst component in a wide variety of organic compound, e.g. hydrocarbon compound, conversion reactions, it is notably useful in the processes of cracking, hydrocracking, isomerization and reforming. Other conversion processes for which the present composition may be utilized as a catalyst component include, for example, dewaxing. The crystalline aluminophosphate composition prepared in accordance herewith can be used either in the as-synthesized form, the hydrogen form or another univalent or multivalent cationic form. It can also be used in intimate combination with a hydrogenating component such as tungsten, vanadium, molybdenum, rhenium, nickel, cobalt, chromium, manganese, or a noble metal such as platinum or palladium where a hydrogenation-dehydrogenaton function is to be performed. Such components can be exchanged into the composition, impregnated therein or physically intimately admixed therewith. For example, where the hydrogenation component is platinum, the material can be treated with a platinum metal-containing ion, such as chloroplatinic acid, platinous chloride or a compound containing the platinum amine complex. The present composition, when employed either as an adsorbent or as a catalyst in a hydrocarbon conversion process, should be dehydrated at least partially. This can be done by heating to a temperature in the range of from 65°C to 315°C in an inert atmosphere, such as air, nitrogen, etc. and at atmospheric or subatmospheric pressures for between 1 and 48 hours. Dehydration can be performed at lower temperature merely by placing the zeolite in a vacuum, but a longer time is required to obtain a particular degree of dehydration. The thermal decomposition product of the newly synthesized composition can be prepared by heating same at a temperature of from 200°C to 550°C for from 1 hour to 48 hours. As mentioned above, synthetic aluminophosphate prepared in accordance herewith can have the original cations associated therewith replaced by a wide variety of other cations according to techniques well known in the art. Typical replacing cations include hydrogen, ammonium and metal cations including mixtures thereof. Of the replacing metallic cations, particular preference is given to cations of metals such as rare earths and metals from Groups IIA, IIIA, IVA, IB, IIB, IIIB, IVB, VIB AND VIII of the Periodic Table of Elements, especially M , Ca, Mjg, Zn, Cd, Pd, Ni, Cu, Ti, Al, Sn, Fe and Co. When used as a catalyst, it may be desirable to incorporate the aluminophosphate of the invention with another material resistant to the temperatures and other conditions employed in certain organic conversion processes. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as incorganic materials such as clays, silica and/or metal oxides, e.g. alumina. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the present aluminophosphate, i.e. combined therewith, which is active, may enhance the conversion and/or selectivity of the catalyst in certain organic conversion processes. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate or reaction. Frequently, crystalline catalytic materials have been incorporated into naturally occurring clays, e.g. bentonite and kaolin. These materials, i.e. clays, oxides, etc., function, in part, as binders for the catalyst. It is desirable to provide a catalyst having good crush strength, because in- a petroleum refinery the catalyst is often subjected to rough handling, which tends to break the catalyst down into powder-like materials which cause problems in processing. Naturally occurring clays which can be composited with the hereby synthesized aluminophosphate include the montmorillonite and kaolin families which include the subbentonites , and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays , or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials , the crystals hereby synthesized can be composited with a porous matrix material such as silica -alumina, silica -magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania, as well as ternary compositions such as silic -alumina-thoria, silica -alumina - zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel . A mixture of these components could also be used. The relative proportions of aluminophosphate material and matrix may vary widelv with the crystalline material content ranging from 1 to 90 percent by weight, and more usually in the range of 2 to 50 percent by weight of the composite. -Employing a catalyst comprising the composition of this invention containing a hydrogenation component , reforming stocks can be reformed employing a temperature between 450°C and 550°C. The pressure can be between 445 and 3550 kPa (50 and 500 psig) , but is preferably between 790 and 2170 kPa (100 and 300 psig). The liquid hourly space velocity is generally between 0.1 and 10 hr " , preferably between 1 and 4 hr" and the hydrogen to hydrocarbon mole ratio is generally between 1 and 10, preferably between 3 and 5. A catalyst comprising the, present composition can also be used for hydroisomerization of normal paraffins, when provided with a hydrogenation component, e.g. platinum. Hydroisomerization is - carried out at a temperature between 250°C to 450°C, preferably 300°C to 425°C, with a liquid hourly space velocity between 0.1 and 10 hr" , preferably between 0.5 and 4 hr" , employing hydrogen such that the hydrogen to hydrocarbon mole ratio is between 1 and 10. Additionally, the catalyst can be used for olefin or aromatics iso erization employing temperatures between 0°C and 550°C. A catalyst comprising the aluminophosphate of this invention can also be used for reducing the pour point of gas oils. This process is carried out at a liquid hourly space velocity between 0.1 and 5 hr " and a temperature between 300°C and 425°C. Other reactions which can be accomplished employing a catalyst comprising the composition of this invention containing a metal, e.g. platinum, include hydrogenation-dehydrogenation reactions and desulfurization reactions, olefin polymerization (oligo.nerization), and other organic compound conversions such as the conversion of alcohols (e.g. methanol) to hydrocarbons. In order to more fully illustrate the nature of the invention and the manner of practicing same, the following examples are presented. Example 1 A 56.78 g quantity of 86% H 3 P0 4 was diluted with 167.76 g H 2 0, followed by the mixing of 25.5 g alpha-alumina monohydrate (i .e. Catapal SB) into the dilute phosphoric acid solution. This slurry was mixed , with stirring , at 25 °C for 10 minutes . To the resulting homogeneous suspension was added 25.5 g of 1 ,5-pentanediamine as directing agent . The reaction mixture prepared had the following composition, in mole ratios: with R being the 1 ,5-pentanediamine. The mixture was then transferred to a 300 ml stainless steel autoclave. The sealed autoclave was heated to 180 °C and stirred (400 rpm) at this temperature and autogenous pressure for 3 days. The crystalline product composition was separated from the final liquids by filtration, water washed , and then dried at 110 °C. The dried product crystals were analyzed by X-ray diffraction, proving it to be the present aluminophosphate composition comprising crystals having large pore windows . Table 2 lists the X-ray diffraction pattern of the dried, as-synthesized, product of this example. l H N I— I i— I I— l rs| ) t-H l— I i— i r-i-H l—l f-H i-H i— l l— . I— I l— . I— I I— l O H _ |r)" N u * . Example 2 A quantity of the product composition of Example 1 was analyzed for chemical composition, the results being as follows: Component Wt.% C 13.76 N 6.18 Na 0.077 Al 11.51 P 16.64 Si 0.41 Ash 61.45

Claims: CLAIMS: 1 . A crystalline aluminophosphate composition comprising crystals exhibiting a characteristic X-ray diffraction pattern as shown in Table 1. 2. The composition of claim 1 exhibiting an X-ray diffraction pattern as shown in Table 2. 3. A method for synthesizing a crystalline aluminophosphate composition having crystals exhibiting a characteristic X-ray diffraction pattern as shown in Table 1 of the specification, which comprises (i ) preparing a mixture comprising sources of an oxide of aluminum, an oxide of phosphorus , water and a directing agent (R) , and having a composition , in terms of mole ratios , within the following ranges : wherein R is a Cr-C alkyldiamine, (ii ) maintaining said mixture under conditions to produce said aluminophosphate and (iii ) recovering the crystalline aluminophosphate from step (ii ). 4. "The method of claim 3 wherein said mixture has the following composition ranges: _ 5. The method of claim 3 wherein said directing agent R is pentanediamine. * _ ■ » ■ 4 ■* 6. The method of claim 3 wherein the conditions include a temperature of 80 to 300°C for 5 hours to 20 days. 7. The method of claim 3 wherein said crystalline aluminophosphate composition exhibits an X-ray diffraction pattern as shown in Table 2. 8. The method of claim 3 comprising replacing cations of the crystalline aluminophosphate recovered in step (iii), at least in part, with a cation or a mixture of cations selected from the group consisting of hydrogen and hydrogen precursors, rare earth metals, and metals from Groups IIA, IIIA, IVA, IB, HE, IIIB, IVB, VIB and VIII of the Periodic Table of Elements.

Inventors: VALYOCSIK ERNEST WILLIAM, VALYOCSIK, ERNEST, WILLIAM
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1989
Main classification: C01B25
IPC codes: B01J29, C01B25, C01B37, C07B61, C07C1, C07C2, C07C5, C10G2, C10G45