Pump impeller

Abstract: A water pump impeller is shown in Figure 1 which is cast directly onto the shaft by first making a foam pattern of the impeller on the shaft, and then using that pattern to foam a mould cavity in which the foam is contained, and casting the molten metal into the cavity to destroy the foam and form the impeller.

Description: This invention relates to water pumps and more especially the impellers thereof, as used in internal combustion engines. Such an impeller comprises a disc or cage extending from a hub and carrying a plurality of impeller blades Modern I.C. engines utilise pressurised coolant systems, so that although the coolant may be water, the temperature can be above 100 deg.C. However, the impeller is necessarily fast with a drive shaft which is in heat conducting contact with engine parts which may be at substantially higher temperatures, and this creates problems in the design which are only solved at present by relatively expensive manufacturing techniques both for the impeller per se and its securement on the drive shaft therefor. Prior Patent GB 798 810-A describes a cast impeller for a centrifugal blower or a pump, having an impeller disc and vanes which are made of a light metal casting made in the usual sand cavity with a tubular hub sleeve of a material described as being of higher rigidity than the light metal (which may mean higher melting point) located in the cavity so that the casting forms about it. The object of the invention is to provide improvements which can avoid the need for expensive machining operations and allow more economical production. According to the invention, a method of making a water pump impeller having a hub and a vaned disc, comprises the steps described in claim 1. Lost foam casting is described for example in FR 1 201 101A, but the preferred technique of the present invention is more particularly described hereinafter in this specification. The foam may be made by filling the die with polystyrene beads and injecting steam. The shape may then be coated by dipping into a ceramic slurry which is allowed to dry. Preferably the metal is iron. The former may be a die insert which may be of stainless steel in the form of a short tube with radial outwardly extending flanges at one or both ends and with one or more peripheral and external ribs or other projections. This forms a central hole in the foam and acts as a support for the same during transfer from the die and location in the mould. The iron then casts onto the insert and the impeller becomes axially keyed to the insert by the ribs or contained by the flanges. The insert may be dimensioned so that in use it, with the impeller formed thereon, is a drive or interference fit on the shaft. Alternatively, the shaft itself may be used as the former on which the foam is formed, so that the impeller is later cast direct onto the shaft. This avoids the use of any intermediary between the shaft and the impeller. The invention is now described with reference to the accompanying drawings wherein :- Figure 1 is a sectional elevation showing an impeller with a first kind of insert; Figure 2 is a similar view with a second kind of insert; Figure 3 shows the same kind of impeller but cast direct to a shaft; and Figure 4 is a view on the line 4 4 of Figure 3. All of the impellers shown in the drawings comprise a tubular hub portion 10 which is integral with a disc 12 carrying a set of curved impeller vanes 14. The shape and contours of the hub, disc and vanes form no part of this invention. In Figure 1 the hub is mounted on a stainless steel tube 16 made integral with end flange 18 and with keying ribs 20. In Figure 2 there are two flanges 18 and 22. In Figures 3 and 4 the impeller is cast direct on the shaft 24. In manufacture according to the invention, a female die 30 Figure 1 has a cavity complementary to the impeller including co-axial stubs 32 to receive locate and position the insert 16. The die may be in two parts which are diametrically split or axially separable. When closed, and with insert in position, material is injected to fill the cavity with foam and take the required shape of the impeller, and this is allowed or caused to cure. The material may be injected for example through a port 34. The foam pattern of the impeller is coated with suitable material to provide a required surface finish and is then used to make a so-called sand casting for example though it could alternatively be used as a pattern for a shell mould, which in either case will generally assume the position and shape of the die 30 in Figure 1. Iron (for example) is cast into the cavity formed by the mould, sand or sand equivalent, and thus cause destruction of the foam which becomes replaced by the iron. The method for Figure 2 differs only in the nature of the insert. In the case of Figure 3, the die is adapted to support and locate the shaft 24 so that as well as Figure 1 representing the impeller made of cast iron, it may equally well represent the foam pattern made thereon prior to the casting step. The subject mould making step is the same for Figure 3 as for Figure 1. The impeller of the present invention does not need machining and is effectively ready for use when cast.

Claims: A method of making a water pump impeller having a hub (10) and a vaned disc (12,14) comprising the steps of creating a casting die cavity corresponding in shape to the impeller, locating a tubular former (16) having radial projections (20) in said cavity, and casting molten metal in said cavity to surround the former and harden and solidify thereon characterised in that said former is a stainless steel tube with a radial outwardly extending flange (18,22) at least at one end, said former is supported in a forming die complimentary in shape to the required impeller shape, the cavity in said die is filled with material to form a foam pattern which is allowed or caused to cure, the cured foam pattern supported on the former is used to make the casting die cavity and said pattern is destroyed by the molten metal as said cavity is filled. The method of Claim 1 wherein the former has radial outwardly projecting flanges at both ends. The method of Claim 1 wherein the former is a drive shaft (24) for the impeller used as an insert in the die forming the foam, and the impeller is then cast onto the shaft.

Inventors: FREEMAN RICHARD ROBERT, FREEMAN, RICHARD ROBERT
Applicants: CONCENTRIC PUMPS LTD, CONCENTRIC PUMPS LIMITED
Application year: 1989
Main classification: F04D29
IPC codes: B22D19, F04D29