Flux spreading thin film magnetic devices

Abstract: One aspect of the invention is a method of flux conduction comprising providing a structure with anisotropy not purely in the transverse in-plane direction such that flux spreading into the transverse in-plane direction can occur by rotation. Another aspect includes a method for producing a thin film magnetic device capable of conducting signal flux along a first axis, having at least two active magnetic layers for at least one pole, a first of the active magnetic layers having domains which are oriented in a first direction at rest and a second of the active magnetic layers has domains which are oriented in a second direction at rest. The layers are coupled to each other such that signal flux can flow therebetween. In another aspect, a thin film magnetic device having at least one set of magnetic domains is capable of conducting signal flux along a first axis, having at least one set of magnetic domains, a first of the magnetic domains is capable of conducting flux in a first direction at an angle to the first axis, a second of said magnetic domains is capable of conducting flux in a second direction other than the first direction, the domains coupled to each other such that signal flux can flow along the first axis. In yet another aspect, each of the domains of the set is capable of conducting signal flux in a first and a second in-plane direction. Apparatus includes a thin film magnetic recording device having at least one pole with two magnetic layers and capable of conducting signal flux, a first of the magnetic layers having domains oriented in a first direction, a second of said magnetic layers having domains oriented in a second distinct direction, the layers coupled to each other such that signal flux can flow therebetween. The layers may be at right angles to each other, one layer parallel to the axis of signal flux conduction, or may be canted at other angles in symmetry with the axis of signal flux conduction. Another apparatus includes a magnetic conduction path defined by a series of domains, some domains at least capable of rotation into a first low reluctance path, some domains at least capable of rotation into a second low reluctance path.

Description: Background of the Invention The present invention relates to rotational flux conduction in thin film magnetic devices. Magnetic devices, such as thin film recording heads, whether read, read/write, or write, are designed to have particular magnetic orientations, or domains, within the active regions of the device material. The static state of each of these domains can be oriented along a given axis, known as the easy axis (or axis of anisotropy), as desired, by control of the manufacturing process. Performance is critically linked to domain formation, and, therefore, control can be exerted over device performance by controlling domain formation. Conduction of flux, such as in a thin film recording head, is achieved by two mechanisms: domain wall motion and domain rotation. Domain wall motion results in flux being transmitted through a thin film head along the walls of a domain, or domains, the flux spreading out along the domain walls as the flux seeks to return to equilibrium. However, while domain wall motion facilitates conduction of flux at low frequencies, it is a poor vehicle for conduction of flux at high frequencies. Furthermore, defects in the material in a magnetic head can be the source of Barkhausen noise during conduction of flux by wall motion as the flux is perturbed by these defects. Such noise can result in erroneous readings of recorded data. A conventional prior art pole of a magnetic recording head is shown in Fig. 1(a), where medium M will be seen as inserting signal flux into a first transversely oriented domain d1 of a series of transversely oriented domains d1-dn. The rest state flux of the domains is in the X-axis (transverse direction), which leaves a rotational option of flowing into the Y axis (longitudinal direction) or Z axis (vertical direction) in reaction to the signal flux from the medium. The Z-axis is out of plane and is a high reluctance path. Hence the flux will rotate into the Y-axis, as indicated by the rotated arrows of each of domains d1-dn. In view of the foregoing, it will be understood that conduction of flux by domain rotation may be achieved by configuring a series of neighboring transverse domains axially aligned along parallel axes, where signal flux impinged upon the first domain at a given angle will cause the magnetization of that domain to rotate from its static orientation by that angle radially into and impinging upon the neighboring domain. Such rotation can be transmitted in a like manner along an axis of flux transmission by each neighboring domain of the series. Hence, flux can be conducted in the pole and through the yoke of a thin film head in a series of domain rotations. The yoke enables conduction of flux through a transducer which produces electrical signals proportional to flux levels or the rate of flux change. The transducer might be an induction coil or other flux sensing device. An induction coil is shown schematically in Fig. 1(a) as it might overlie the bottom pole of a two pole structure. Further discussion of the flux conduction mechanisms will be found in co-pending patent application entitled: "Perpendicular Anisotropy In Thin Film Devices", EP-0 353 885. The aforementioned document provides a discussion of thin film devices using magnetic anisotropy perpendicular to the plane of the device. In US-4295173 there is described a thin film inductive transducer head in which a pole tip having width equal to, or slightly less than the width of track on the associated magnetic medium, widens toward the back gap region. Resolution is enhanced by thin pole tips and saturation of the yoke structure is avoided by increasing the cross-sectional area of the yoke structure away from the pole tip region. The domain structures are oriented such that the magnetization is perpendicular to the flux path. In Japanese Journal of Applied Physics, Vol 11, No 12, December 1972, p1783-1787; Morio Masuda et al: "Magnetic Coupling between Two Ni-Fe Layers Separated by SiO Intermediate Layer", magnetic coupling energy between two non-magnetostrictive NiFe layers separated by an SiO layer and having mutually orthogonal easy axes is discussed as a function of the thickness of the separation layer. EP-0 281 931, cited under Article 54(3) and (4), discloses a composite magnetic head for efficiently recording and reproducing high frequency signals in a magnetic tape based video recording system. Summary of the Invention The present invention relates to a method and device according to independent claims 1 and 14. Preferred embodiments are defined in the dependent claims. Description of the Preferred Embodiments We first briefly describe the drawings. Fig. 1(a) is a schematic view of the top layer of a prior art pole; Fig. 1(b) is a cross-sectional view of a two layer configuration of the prior art pole of Fig. 1(a). Fig. 2 is a schematic of a two layer pole of a preferred embodiment of the present invention. Fig. 3 is a schematic of the top layer of the pole of Fig. 2. Fig. 4 is a schematic of the bottom layer of the pole of Fig. 2. Fig. 5 is a schematic in two views of a unidirectional anisotropy prior art head. Fig. 6 is a schematic in three views of an alternative embodiment of the present invention showing a flux beam comprised of angular and rotational components. Fig. 7 is a schematic of an alternative laminated embodiment of the present invention having two layers, each layer having a parallel sublayer. Fig. 8 is a conventional laminated two pole geometry. Fig. 9 is a schematic of an alternative embodiment of the present invention where poles P1 and P2 are in the same horizontal plane. Fig. 10 is a schematic of another alternative embodiment of the present invention where poles P1 and P2 are stacked. It is desirable that signal flux be efficiently conducted from the pole tip through the yoke of a magnetic conduction device. Thus a low reluctance flux conduction mechanism is desired. The present invention enables low reluctance flux conduction by magnetization rotation at high frequencies. This is achieved by provision of a structure allowing both longitudinal and lateral rotational conductivity. Such multi-dimensional conductivity obviates the need for domain wall propagation, thus avoiding low response at high frequencies and Barkhausen noise. The invention is applicable to a wide variety of devices relying upon magnetic conduction, including transformers, magnetic field sensors, bubble memory magnetic structures, thin film magnetic memory elements, magnetic shields, and recording heads, and may be embodied in both single and multi-layered devices. Fig. 1(b) shows in cross-section a two-layer configuration of a prior art pole. Here, layers L1 and L2 are separated by a very narrow gap g to enable coupling between layers L1, L2 of rest state domain flux (i.e., D.C. flux of the domains at rest). The anisotropy directions of layers L1, L2 are parallel to each other and transverse to the pole, as indicated by the horizontal arrows a, b in layers L1, L2, respectively. Also, the thicknesses of L1 and L2 are by design equal. Turning to the schematic drawing of Fig. 2, a preferred embodiment of the present invention is shown from a magnetic recording medium looking into the tip of a pole 10 of a magnetic recording head having two active layers, L1, L2, one with in-plane anisotropy (i.e., rest state domain orientation) transversely oriented, and the other layer longitudinally oriented. These layers are separated by a gap layer g. The gap layer is thick enough such that the domain state of each layer will remain independent from each other, but yet is thin enough such that signal flux can transmit readily between the two layers of the pole. In present thin film configurations, perhaps a range of 30-200 nanometres (three hundred to two thousand angstroms) would be a reasonable target for gap size. In a typical two pole recording head, each pole could have a like configuration. Layers L1 and L2 are preferably configured where L1 thickness t1 does not equal L2 thickness t2. These layers are preferably configured with t1 greater than t2. A top view of pole 10 of Fig 2 is shown in Fig. 3, where the first layer L1 of pole 10 has a preferred easy axis transverse to the longitudinal axis of the pole. The domain structure is configured to have relatively large and uniform central domains 12 with adjacent relatively small edge domains 16 in the region of pole tip 20, and with extended edge domains 22 in the yoke region 24. In this configuration, flux from the medium will be read at the first domain dl at pole tip 20. As a result, flux will be conducted by rotation, serially propagating down adjacent domains 12, as it heads toward yoke section 24. This conducting mechanism may be referred to as a flux pipe or flux beam, and is schematically indicated by the parallel vertical dotted lines running up the pole from the tip and through the yoke. A top view of layer L2 of Fig. 2 is shown in Fig. 4. Layer L2 has a longitudinal easy axis, parallel to the longitudinal axis of the pole and transverse to the easy axis of layer L1. The domain structure is substantially longitudinal in orientation. As a result it will conduct flux transversely by rotation. In Figs. 3 and 4, the yoke section 24 is shown to increase in width as it extends away from pole tip 20. If the yoke section were not spread, the boundaries of the flux beam would be defined as shown in dotted lines and the high reluctance effect mentioned above would degrade operation. However, by having this region spread out, the flux beam will somewhat spread out, thus adding to the area within the dotted lines by including at least a portion of the regions indicated by the hash marks 23. This effectively results in a lower reluctance path of conduction through the yoke. It should be appreciated, however, that mere broadening of the yoke alone is not sufficient to accomplish substantial flux spreading in this embodiment. Rather, it is the cooperation between differently oriented layers L₁, L₂ of pole piece 10, which facilitates substantial flux spreading, and the yoke is broadened therefore to facilitate interaction of these layers. A more detailed description of the flux spreading mechanism as applied to the embodiment of Figs. 2, 3 and 4 follows. Flux will be introduced from the magnetic medium into the first transverse domain dl domain at pole tip 20 perpendicular to the easy axis of the transversely magnetized layer L1. The flux will be propagated longitudinally by rotation down that layer, domain 12 to domain 12, for as long as a low path of reluctance is experienced by the flux. As path length and thus reluctance accumulates, a portion of the flux crosses the gap g and propagates into the longitudinally oriented domain L2, thus lowering the reluctance of the system. The flux will propagate transversely in layer L2 until it accumulates reluctance as will cause it to seek a path of lower reluctance and to jump the gap to re-enter into the transverse layer L1. Once in the transverse layer, the flux propagates longitudinally until accumulated reluctance again causes the flux to seek a lower path of reluctance in the longitudinal active layer on the other side of the gap. This process will continue until the flux has propagated through the yoke, but by the virtue of the process of adding a transverse rotational component to flux flow, the flux will have spread out within the widened yoke region, thus reducing total system reluctance. Thin film heads are being used at higher bit densities. One way to achieve this higher bit density is by reduction of track width. Hence, it is desirable to produce a thin film head having a narrow track width but which also operates at high frequencies. Conduction by rotation can enable such achievements. A narrow track should have a high anisotropy field. This high anisotropy field will act to keep the flux path open by keeping edge domains relatively small. As a result, the rotational mechanism may be kept alive even where the structural magnetic reluctance is lowered in the yoke section according to the present invention, although the high anisotropy field will reduce permeability of the structure. In the design of a narrow track, laminated films often are used to eliminate edge domains and 180° walls. Therefore, these laminated films will not spread flux well in conventional configurations. Referring to Fig. 5 (A and B), which includes schematic complementary views of a unidirectional anisotropy prior art head not having the cooperating layers of the present invention, it will be seen that the flux imposed at an angle phi (or 180° minus phi) from the medium upon the transversely oriented magnetization will cause a rotation of the magnetization by such angle. In all other aspects a uniform beam will be conducted back through the pole into and through the yoke, except that it will be canted by one half of phi. As a result, a high magnetic impedance will be experienced at the yoke because the flux beam does not widen significantly. The present invention, in an alternative preferred embodiment, achieves flux spreading by orienting the easy axes of the top and bottom layers of laminated poles at plus and minus angles, theta, relative to the transverse magnetic direction. As a result, the flux will then spread out in a wedge angle of twice the value of theta, plus the additional angular component phi caused by the flux rotation. The wedge-creating embodiment of the present invention is shown conceptually in Fig. 6 (A, B and C), where in 6A the first active layer L1 has been imparted a static angular displacement of its magnetic orientation at an angle theta measured from the transverse axis. The second active layer L2 is shown in 6B having a complementary magnetic orientation at rest at an angle 180° minus theta. When flux is impinged upon the L1 and L2 layers normal to the transverse axis, then the resulting flux beam will be spread equivalent to twice theta plus the rotational component phi for each layer (i.e., one-half phi plus one-half phi). Thus, the flux beam will be the summation of the two angularly and rotationally displaced flux beams of each layer, amounting to two theta plus phi, as shown in 6C. It is preferred in this configuration that the gap between the two layers is small enough to pass rest state domain flux. In operation, flux from the magnetic medium will enter the pole tip and be conducted back to the yoke juncture by rotation in both layers. As the flux enters the yoke juncture, the top layer directs a flux beam off at an angle theta relative to the axis of symmetry of the pole, and the bottom layer directs the flux beam off at an angle 180° minus theta. Conduction of flux between the layers allows the top layer to insert flux into the bottom one in positive theta regions and vice versa. In other embodiments of the invention utilizing laminating films, two or more active magnetic layers can be employed. In a particular embodiment, one pole of which is illustrated in Fig. 7, four active magnetic layers (A, B, C and D) comprise two pairs (AB and CD) of layers. The layers A and B are oriented in the same direction and the gap between A and B is small enough to couple rest state domain flux between them. The layers C and D are similarly configured but their orientation is at a different angle. The gap from B to C is large enough to not conduct rest state domain flux but small enough to conduct signal flux. For example, A and B could be longitudinally oriented while C and D are transversely oriented. Alternatively, A and B could be oriented at plus theta to the transverse direction while C and D are at 180° minus theta. An alternative configuration of the embodiment of Fig. 7 is provided having three active layers (A, B and C), A and B are paired as described above and are transversely oriented. The gap from B to C is large enough to block rest state domain flux but small enough to conduct signal flux. Layer C is oriented longitudinally. The pair A and B conducts flux longitudinally even for narrow track widths. The layer C spreads the flux laterally thus to avoid the high impedance flux beam effect. Alternatively, A and B could be oriented longitudinally and C could be oriented transversely. Fig. 8 shows a conventional two pole yoke geometry where the top and bottom halves of the yoke are symmetrical, and the tips are centered about gap g. The foregoing configurations of the invention can be applied to this geometry. By doing so, flux spreading by rotation will be achieved while preserving flux conduction by rotation in the longitudinal direction. Each pole is shown to have been laminated into two active magnetic layers E,F and E1,F1. These above-described configurations of the invention can also be applied to the geometries shown in Figs. 9 and 10. Here, the invention not only aids in flux spreading by rotation, but also facilitates transverse flux conduction by rotation. For example, in the configuration shown in Fig. 9, poles P1 and P2 are horizontal. Their first layer L1 is longitudinally oriented. Layer L2 is transversely oriented. Flux entering the right hand pole tip near the gap in region RP is initially conducted to the right in the top longitudinally oriented layer. When the flux reaches the juncture with the right hand leg in region RJ, it will transfer to the bottom layer and be conducted toward the back of that pole in that transversely oriented layer. When the flux reaches the back section of the yoke, it must jump back into the top layer in order to travel leftward by rotation. The flux travels in a complementary manner to complete the flux path back to the left hand pole tip. In Fig. 10, poles P1 and P2 are stacked. The first layer L1 extends over each pole and is longitudinally oriented. Layer L2 is transversely oriented and extends over each pole. Vias are provided in the yoke to assure coupling between respective portions of each layer. In this embodiment, the same process occurs as in the embodiment of Fig. 9, but the turns on the path are not abrupt. Also, the pole tips are stacked. It will be appreciated that a transducer must be associated with the yoke in order to generate electrical signals from the signal flux in the device. Various transducer configurations would be operable with practice of the present invention. Manufacturing : In a dry vacuum deposition approach, the transversely oriented layer can be deposited on a wafer substrate by placing the wafer in a transversely oriented magnetic field during deposition. (Alternately, this can be accomplished by growing the film with a crystal orientation that places a crystallographically oriented axis in the transverse direction.) The transversely oriented magnetic field can be supplied by coils or by the magnetron target magnets of a sputtering machine, for example. Also, the deposition can be made at angles normal or other than normal to the surface, where the incident direction establishes the preferred axis. For example, one layer might have a field direction at plus theta to the transverse direction, and the other layer might be oriented at minus theta. During subsequent heat treatment, exclusion of all fields would allow the two layers to self bias. Furthermore, in a configuration where an external transverse field is needed to be present to orient other head layers, then the easy axis in both layers could be established at some angle greater than theta, such that after anneal they would relax to angle theta. After the first layer is laid down, then a buffer layer (non-magnetic) can be deposited. For dry deposition, it is convenient to use a ceramic which can be made thinner than a metal and will stop exchange coupling between the first and the next layer. In orthogonal configurations, for example, the second magnetic layer will be deposited either with the wafer rotated 90° to the first deposition position, or the magnetic field rotated 90°. After these layers are deposited, the yoke may be formed by means of a masked ion milling process. Where it is believed advantageous to sub-laminate each of the oriented layers, orientation direction of magnetization in the sublayers paired together preferably would be in the same direction. It may be found that dry deposition is more suited to this type of heavily laminated structure. For wet processing, each layer is deposited through a plating mask in a bias field to establish appropriate magnetic domain orientation. The non-magnetic layer can be plated if it is a metal, for example Ni-P, Au, Cu, etc. If a ceramic is used for the buffer layer, then this must be sputtered after the mask has been removed. The structure is now ready to receive the next magnetic layer, whereupon a seed layer and mask will be laid down, and the layer will be plated thereon. A problem with the technology described above resides in that any exposure to very high temperatures (for example, greater than 200°C for greater than half an hour for NiFe poles) will degrade the induced anisotropy obtained by depositing in a field. This sensitivity can be overcome by using the angle of incidence approach to inducing anisotropy as discussed above in regard to dry deposition. In particular, it is possible to deposit the first layer of the bottom of the yoke in a longitudinally oriented field. This layer can be annealed in the field at a temperature that is much higher than the process temperatures used in the rest of the process. Next, the top layer of the bottom of the yoke and the bottom layer of the top of the yoke may be deposited in a transverse field, which field is maintained during high temperature processing. Thereafter the top layer of the top yoke may be deposited in a longitudinal field and which is not annealed. Only the bottom layer then has experienced an anisotropy-lowering anneal, and it will retain only some of its orientation. Nevertheless, orientation of this lowest layer, while important for yoke conductivity, is not critical for pole tip conductivity, and therefore such conductivity can be diminished. Other embodiments are within the following claims. Pole materials which may be used in the above processes include alloys of nickel, iron and cobalt, and magnetic garnet and ferrite crystals, to name a few alternatives.

Claims: Claims for the following Contracting States : AT, BE, CH, ES, GR, IT, LI, LU, NL, SE A magnetic device for conducting signal flux therethrough, said magnetic device having an arrangement of at least a first and a second layer of magnetically anistropic material, the first and second layer including magnetic domains oriented to conduct said signal flux by rotation through said layers; characterised in that the respective magnetic anistropies of the first and second layer are non-parallel to each other and in that the first and second layer are separated by a gap so that said first domains and said second domains are coupled to each other to cause said signal flux to pass therebetween. The magnetic device of claim 1 including first magnetic domains in said first layer which forms a first region (L1) for conducting said signal flux in a first direction, said first magnetic domains (12) being oriented transversely to said first direction to cause said signal flux to conduct by rotation in said first direction, and including second magnetic domains in said second layer which forms a second region (L2) for conducting said signal flux in a second direction, said second magnetic domains being oriented transversely to said second direction to cause said signal flux to conduct by rotation in said second direction. The device of claim 2, in which said layers (L1,L2) are separated from each other to avoid flux conduction between said first plurality of magnetic domains (12) and said second plurality of magnetic domains when said signal flux is absent. The device of claim 2, in which said layers (L1,L2) are coupled together to allow flux conduction between said first plurality of magnetic domains (12) and said second plurality of magnetic domains when said signal flux is absent. The device of claim 3 or claim 4, wherein said first layer (L1) or said second layer (L2) comprise two parallel magnetic layers (A,B). The device of claim 2, claim 3 or claim 4 wherein said first plurality of said magnetic domains (12) and said second plurality of said magnetic domains are oriented perpendicularly to each other. The device of claim 2, claim 3 or claim 4 wherein said first plurality of said magnetic domains (12) and said second plurality of said magnetic domains are oriented obliquely to each other. The device of claim 2 constructed as a magnetic transducer having a pair of magnetic poles (P1,P2) for conducting said signal flux from a storage medium to a yoke section of said transducer, each one of said poles including said first region (L1) and said second region (L2), said magnetic poles being coupled together in said yoke section and having tips that are stacked one upon the other, separated by a gap, and arranged to be disposed adjacent to said storage medium. The device of claim 2 constructed as a bubble memory magnetic field structure, wherein said first region (L1) and said second region (L2) are arranged to provide at least one laminated memory element thereof. The device of claim 2 wherein said first magnetic layer has a thickness (t1) that is greater than a thickness (t2) of said second magnetic layer. The device of claim 1 wherein said two magnetic layers (L1,L2) form a pole (P1). The device of claim 11, further comprising a second magnetic pole (P2), said poles (P1,P2) being stacked one on top of the other. The device of claim 11, further comprising a second pole (P2) where said poles (P1,P2) lie adjacent to each other in one plane. A method for making a magnetic conduction device for conducting signal flux therethrough by providing an arrangement of at least a first and a second layer of magnetically anistropic material wherein the respective magnetic anistropies of the first and second layer are orientated non-parallel to each other and wherein a gap is provided between the first and second layer so that the magnetic domains in the first and second layer are coupled to each other to cause signal flux to pass therebetween. The method of claim 14, further comprising separating said first and second layers (L1,L2) from each other by said gap to avoid flux conduction between said magnetic domains of said first and second layers when said signal flux is absent. The method of claim 14, further comprising performing said coupling by said gap so that said layers (L1,L2) are coupled together to allow flux conduction between said magnetic domains of said layers when said signal flux is absent. The method of claim 14, including the steps of configuring a plurality of parallel magnetic sub-layers (A,B;E,F) in said first layer (L1), and coupling said sub-layers together to allow flux conduction between magnetic domains of said sub-layers when said signal flux is absent. The method of claim 14 or claim 17, including the steps of configuring a plurality of parallel magnetic sub-layers (C,D;E1,F1) in said second layer, and coupling said sub-layers together to allow flux conduction between said magnetic domains of said sub-layers when said signal flux is absent. The method of claim 14 wherein said first plurality of said respective magnetic anistropies are oriented perpendicularly to each other. The method of claim 14, wherein said first and second layers (L1,L2) comprises a pole (P1) of a magnetic head disposed along a first axis, and further including orienting said respective magnetic anistropies to provide a first anistropic direction along said first axis and a second anistropic direction perpendicular to said first axis. The method of claim 14 wherein said first plurality of said respective magnetic anistropies are oriented obliquely to each other. Claims for the following Contracting States : DE, FR, GB A thin film magnetic device for conducting signal flux therethrough, said thin film magnetic device having an arrangement of at least a first and a second layer of magnetically anistropic material, the first and second layer including magnetic domains oriented to conduct said signal flux by rotation through said layers; characterised in that the respective magnetic anistropies of the first and second layer are non-parallel to each other and in that the first and second layer are separated by a gap so that said first domains and said second domains are coupled to each other to cause said signal flux to pass therebetween. The magnetic device of claim 1 including first magnetic domains in said first layer which forms a first region (Ll) for conducting said signal flux in a first direction, said first magnetic domains (12) being oriented transversely to said first direction to cause said signal flux to conduct by rotation in said first direction, and including second magnetic domains in said second layer which forms a second region (L2) for conducting said signal flux in a second direction, said second magnetic domains being oriented transversely to said second direction to cause said signal flux to conduct by rotation in said second direction. The device of claim 2, in which said layers (L1,L2) are separated from each other to avoid flux conduction between said first plurality of magnetic domains (12) and said second plurality of magnetic domains when said signal flux is absent. The device of claim 2, in which said layers (L1,L2) are coupled together to allow flux conduction between said first plurality of magnetic domains (12) and said second plurality of magnetic domains when said signal flux is absent. The device of claim 3 or claim 4, wherein said first layer (L1) or said second layer (L2) comprise two parallel magnetic layers (A,B). The device of claim 2, claim 3 or claim 4 wherein said first plurality of said magnetic domains (12) and said second plurality of said magnetic domains are oriented perpendicularly to each other. The device of claim 2, claim 3 or claim 4 wherein said first plurality of said magnetic domains (12) and said second plurality of said magnetic domains are oriented obliquely to each other. The device of claim 2 constructed as a thin film magnetic transducer having a pair of magnetic poles (P1,P2) for conducting said signal flux from a storage medium to a yoke section of said transducer, each one of said poles including said first region (L1) and said second region (L2), said magnetic poles being coupled together in said yoke section and having tips that are stacked one upon the other, separated by a gap, and arranged to be disposed adjacent to said storage medium. The device of claim 2 constructed as a bubble memory magnetic field structure, wherein said first region (L1) and said second region (L2) are arranged to provide at least one laminated memory element thereof. The device of claim 2 wherein said first magnetic layer has a thickness (t1) that is greater than a thickness (t2) of said second magnetic layer. The device of claim 1 wherein said two magnetic layers (L1,L2) form a pole (P1). The device of claim 11, further comprising a second thin film magnetic pole (P2), said poles (P1,P2) being stacked one on top of the other. The device of claim 11, further comprising a second thin film magnetic pole (P2) where said poles (P1,P2) lie adjacent to each other in one plane. A method for making a thin film magnetic conduction device for conducting signal flux therethrough by providing an arrangement of at least a first and a second layer of magnetically anistropic material wherein the respective magnetic anistropies of the first and second layer are orientated non-parallel to each other and wherein a gap is provided between the first and second layer so that the magnetic domains in the first and second layer are coupled to each other to cause signal flux to pass therebetween. The method of claim 14, further comprising separating said first and second layers (L1,L2) from each other by said gap to avoid flux conduction between said magnetic domains of said first and second layers when said signal flux is absent. The method of claim 14, further comprising performing said coupling by said gap so that said layers (L1,L2) are coupled together to allow flux conduction between said magnetic domains of said layers when said signal flux is absent. The method of claim 14, including the steps of configuring a plurality of parallel magnetic sub-layers (A,B;E,F) in said first layer (L1), and coupling said sub-layers together to allow flux conduction between magnetic domains of said sub-layers when said signal flux is absent. The method of claim 14 or claim 17, including the steps of configuring a plurality of parallel magnetic sub-layers (C,D;E1,F1) in said second layer, and coupling said sub-layers together to allow flux conduction between said magnetic domains of said sub-layers when said signal flux is absent. The method of claim 14 wherein said first plurality of said respective magnetic anistropies are oriented perpendicularly to each other. The method of claim 14, wherein said first and second layers (L1,L2) comprises a thin film magentic pole (P1) of a thin film magnetic head disposed along a first axis, and further including orienting said respective magnetic anistropies to provide a first anistropic direction along said first axis and a second anistropic direction perpendicular to said first axis. The method of claim 14 wherein said first plurality of said respective magnetic anistropies are oriented obliquely to each other.

Inventors: MALLARY MICHAEL, SHUKOVSKY HAROLD B, MALLARY, MICHAEL, SHUKOVSKY, HAROLD B.
Applicants: QUANTUM CORP, QUANTUM CORPORATION
Application year: 1989
Main classification: G11B5
IPC codes: H01F3, H01F41, G11B5, H01F10, G01R33, H05K9, G11C11