Thickening agents for aqueous systems

Abstract: Thickening agents for aqueous systems are prepared by converting aliphatic alcohols containing 8 to 22 carbon atoms with an ethylene oxide/propylene oxide mixture, and then converting the resulting polyether with statistic distribution with 5 to 20 moles of ethylene oxide, and combining the resulting alkoxylation product provided with a block of ethylene oxide with a di-epoxide, with 0,5 to 3 moles of alkylation product being used in the combination reaction per mole of di-epoxide. The thickening agents may be blended with low-molecular weight alcohol ethoxylates, and are especially suitable for hydraulic fluids.

Description: The invention relates to liquid thickening agents for aqueous systems which are prepared by the alkoxylation of higher aliphatic alcohols with ethylene oxide and propylene oxide to alcohol alkoxylates capped with ethylene oxide and the reaction of the alkoxylated alcohols with diepoxides, a process for the preparation thereof, and the use of same in aqueous systems. It is known to alkoxylate higher alcohols having 8 - 22 carbon atoms with ethylene oxide or propylene oxide or with mixtures of the two alkylene oxides and subsequently to convert the resulting alkoxylated product with diepoxides. Using such products it is possible to prepare aqueous solutions of a high viscosity, as is described, e.g., in DE 3 134 494. The preparation of such products and their suitability as thickening agents is also disclosed in, e.g., US-PS 3 538 033 and 4 102 795. The reaction of alcohols with ethylene oxide/propylene oxide mixtures leads to polyethers with different reactive terminal OH groups, with the ratio of primary OH groups to secondary OH groups being dependent on the reaction conditions. Since the composition of the later products formed by reaction of the alkoxylates with diepoxides is basically dependent on the type of hydroxyl terminal group of the alkoxylates, and variations in reaction conditions (e.g., temperature, EO/PO ratio) are unavoidable when preparing alkoxylates, it is difficult to prepare products of reproducible composition and quality. Highly effective polyether-based thickening agents display in, e.g., water a great dependence of viscosity on temperature, which within the field of application of non-flammable hydraulic fluids presents a major drawback. Therefore, there is still need for the preparation of a thickening agent that has reproducible properties, is universally suited to be used for the thickening of different water-based systems, and displays little viscosity-temperature dependence. This problem is solved by a process for the preparation of thickening agents for aqueous systems by the conversion of higher aliphatic alcohols with 8 - 22 carbon atoms with ethylene oxide and propylene oxide and the reaction of the alkoxylated alcohols with diepoxides, characterized in that aliphatic alcohols with 8 - 22 carbon atoms are converted with a mixture of ethylene oxide/propylene oxide containing more than 15% by weight of propylene oxide in a molar ratio of alcohol to the alkylene oxide mixture of 1:40 - 1:150, and the resulting polyether with statistic distribution of the ethylene oxide and propylene oxide is then converted with 5 - 20 moles of ethylene oxide and the resulting alkoxylation product provided with a block of ethylene oxide units is reacted with a diepoxide, with 0,5 - 3 moles of alkoxylation product being used in the reaction per mole of diepoxide. It is of advantage to make use of a mixture with 20 - 30 wt.% of propylene oxide in the first alkoxylation step. In a particularly advantageous embodiment of the process according to the invention there are mixed with the thickening agent after reaction with the diepoxide 0,1 - 5 parts of a low-molecular weight alcohol ethoxylate per part of thickener. The admixed low-molecular weight alcohol ethoxylates should preferably have a share of 30 - 70% by weight in the thickening agent/alkoxylate mixture. Subject matter of the invention also includes thickening agents as a result of the processes described hereinbefore. Subject matter of the invention further includes mixtures of thickening agents as they can be obtained by the processes described hereinbefore. Subject matter of the invention is also the use of the thickening agents in aqueous systems, more particularly in aqueous hydraulic fluids, metalworking fluids, emulsions, dispersions, more particularly latex dispersions, aqueous tenside systems, acids, and bases. It is of advantage to use the thickening agents as mixtures. The preparation of the thickening agent according to the invention may be carried out as follows. A higher aliphatic alcohol or a corresponding mixture, such as C12/14 H25/29 OH = lauryl myristyl alcohol or C16/C18 H 33/37 OH = tallow alcohol is converted at an elevated temperature of, say, about 140° - 180°C with an ethylene oxide/propylene oxide mixture containing at least 15% by weight of propylene oxide. In this process about 40 to 150, more particularly 60 - 100 moles of alkylene oxide are brought to reaction per mole of alcohol. After the alkoxylated product with statistical distribution of the alkylene oxide has been obtained, alkoxylation takes place again in a second reaction, this time, however, using pure ethylene oxide under otherwise identical reaction conditions. Thus is formed an alkoxylated product which exhibits a range with statistical distribution of the EO/PO units, to which is linked a block of ethylene oxide units. This alkoxylated product is subsequently crosslinked with a diepoxide, such as vinyl cyclohexene dioxide or 1,2,7,8-diepoxy octane. In addition, other diepoxides such as limonene dioxide and diglycidyl ethers such as butane diol diglycidyl ether may be employed. In the process according to the invention products are formed which are liquid at room temperature, can therefore be pumped and easily fed, and can be worked into water at room temperature without being melted down (see Example 2). When a thickening agent is used in aqueous systems, it is of great advantage that no solid thickener residues are formed when the water is evaporated, so that there is no incrustation in the equipment or formation of solid deposits. This means that valves, pumps, pipes, and the like are protected and, consequently, costly servicing is not required. The thickening agent is highly economical, since it is possible to set the desired viscosities already with comparatively small amounts (see Tables 2 and 3). The thickening agents are very hydrolytically stable, so that even at elevated temperatures and longer operating periods there will not be a detrimental decomposition of the polyether, which means that the period of use of the thickening agent can be increased, so that especially in hydraulic plants it will be possible to increase the service life considerably. The cloud point of aqueous systems containing the thickeners prepared according to the invention is high, so that no problems arise at temperature variations. As is known, thickener systems become inactive above the cloud point. The thickening agents have a low foam content in aqueous systems, so that the addition of foam removers is largely superfluous. The thickening agents are extremely stable to shear, which enables the thickening agent to be used especially in hydraulic fluids. Especially advantageous according to the invention are thickening agents consisting of mixtures of at least two thickening agents with different alkyl terminal groups. Such may, e.g., be obtained as follows: first, in separate synthesis steps each time a thickening agent is prepared as described hereinbefore from an alcohol such as lauryl myristyl alcohol or tallow alcohol. The alcohols used each time as starter alcohol are distinguished in the alkyl group by four CH₂ groups. It is of advantage when in the preparation of such mixtures use is made of thickening agents in which the alkyl groups are distinguished by at least four CH₂ groups. The thickening agents prepared in this manner are subsequently mixed (see Examples 3 and 5). However, it is also possible to present directly a mixture of the alcohols in question and prepare the thickening agent mixture directly in the synthesis. It is more advantageous, however, to prepare the individal thickening agents separately first, since in this way there is greater variability in preparing the mixtures. In this way it is possible to prepare thickening agents with custom-made property profiles which meet the most diversified requirements in the art. It was particularly surprising to find that the viscosity-temperature profile of the thickening agents prepared according to the invention and of their mixtures can be changed by the addition of low-molecular weight alkoxylates, e.g. alcohol ethoxylates. As a rule, the viscosity of a thickened aqueous system decreases as the temperature increases. By adding alkoxylates it is possible to reduce considerably the decrease in the viscosity curve as a function of temperature, and within some ranges it is even possible to obtain a positive dependence, i.e. the viscosities increase as the temperature rises, which is especially significant for some fields of application. It is even possible to prepare mixtures in which, over a wide range, the viscosity is not dependent on temperature (see Table 5). The thickening agents can be dissolved in aqueous systems at room temperature within a short period of time; a completely homogeneous system is already obtained after a few minutes' stirring (Examples 2 and 4), whereas for known thickening agents stirring periods of up to 1 hour are required before a homogeneous solution is attained. The intrinsic viscosity of the thickening agents prepared according to the invention can be lowered by the addition of the alkoxylates mentioned hereinbefore, which has a favourable effect on the dosage of the thickening agents (see Table 4). The invention will be further illustrated in the following examples: Examples 1A and 1B Preparation of the thickening agent according to the invention The amounts used in Examples A and B and other product data can be found in Table 1. First, the alcohol in the liquid state was mixed with KOH powder in an autoclave and dehydrated for 60 minutes at 100° - 120°C and a pressure of 13·3 - 20 mBar [10 - 15 Torr (mm Hg)]. Next, the vacuum was disconnected with nitrogen to a starting pressure of 0,4 bar. Then the ethylene oxide/propylene oxide mixture was fed in continuously at 150° - 160°C and 5 bar. After the ethylene oxide/propylene oxide mixture's reaction had been brought to completion, ethylene oxide was added at 150° - 160°C and 5 bar. After completion of the feeding of the ethylene oxide and following after-reaction the product was cooled and decanted. Subsequently, the obtained liquid alkoxylate was charged into a dry three-neck flask flushed with nitrogen and fitted with a stirrer, a reflux condenser, a contact thermometer, a dropping funnel, a vacuum connection, and a nitrogen connection, and mixed with KOH powder. Then dehydration was carried out for 30 minutes at 120°C and 13·3 - 20 mBar [10 - 15 Torr], whereupon the vacuum was disconnected with nitrogen. At 120°C followed the addition of the diepoxide within 30 minutes. After having been stirred for 30 minutes at 120°C, the product was then cooled and decanted. Example 2 Prepared from the thickeners A and B according to Examples 1A and 1B were several concentrated aqueous solutions. The preparation was carried out by adding the liquid thickener to water and subsequent magnetic stirring. At room temperature the stirring time was between 0,5 and 5 minutes, depending on the thickener and the concentration. The viscosity of the solutions was determined in an Ubbelohde viscometer at 20°C and at 40°C. The results can be found in Table 2. Example 3 From the thickeners A and B according to Examples 1A and 1B were prepared several mixtures in different ratios by simple stirring with a glass rod at room temperature. These thickener mixtures were used according to Example 2 for the preparation of thickened aqueous solutions. The viscosities of these solutions at 20°C and at 40°C are to be found in Table 2. Example 4 With the thickeners A and B according to Examples 1A and 1B was thickened in different amounts an ethylene glycol/water 1:1 mixture. The thickened solutions were prepared by the liquid thickener simply being stirred magnetically into the ethylene glycol/water mixture. At room temperature the stirring time was 0,5 - 1 minute, depending on the amount and the thickener. The viscosity of the solutions was measured in an Ubbelohde viscometer at 20°C and at 40°C. The results can be found in Table 3. Example 5 From the thickeners A and B according to Examples 1A and 1B were prepared several mixtures in different ratios by simple stirring with a glass rod. With these thickener mixtures was thickened according to Example 4 an ethylene glycol/water 1:1 mixture. The viscosities of these solutions are to be found in Table 3. Example 6 From the thickeners A and B according to 1A and 1B a premix containing an alcohol with a low degree of ethoxylation was prepared. The premix was prepared by simple stirring with a glass rod at room temperature. The intrinsic viscosity of the resulting premix is considerably lower than the viscosity of the pure thickener (see Table 4). Example 7 Using the thickener/alkoxylate mixtures prepared according to Example 6 several concentrated aqueous solutions were prepared. The thickened solutions were prepared by the premix simply being stirred magnetically into water. At room temperature the stirring time was 0,5 - 3 minutes. The viscosity of the solutions was measured in an Ubbelohde viscometer at 20°C and 40°C. The results have been compiled in Table 5.

Claims: A process for the preparation of thickening agents for aqueous systems by the conversion of higher aliphatic alcohols having 8 - 22 carbon atoms with ethylene oxide and propylene oxide and the reaction of the alkoxylated alcohols with diepoxides, characterized in that aliphatic alcohols with 8 - 22 carbon atoms are converted with a mixture of ethylene oxide/propylene oxide containing more than 15% by weight of propylene oxide in a molar ratio of alcohol to the alkylene oxide mixture of 1:40 - 1:150, and the resulting polyether with statistical distribution of the ethylene oxide and propylene oxide units is then converted with 5 - 20 moles of ethylene oxide and the resulting alkoxylation product provided with a block of ethylene oxide units is reacted with a diepoxide, with 0,5 - 3 moles of alkoxylation product being used in the reaction per mole of diepoxide. A process according to claim 1, characterized in that use is made of 1 - 1,5 moles of alkoxylation product per mole of diepoxide. A process according to claim 1 or claim 2, characterized in that the diepoxide used is vinyl cyclohexene dioxide. A process according to claim 1 or claim 2, characterized in that the diepoxide used is 1,2,7,8-diepoxy octane. A process according to any one of claims 1 - 4, characterized in that for the first alkoxylation use is made of an ethylene oxide/propylene oxide mixture in a proportion of 20 - 30% by weight of propylene oxide. A process according to any one of the claims 1 - 5, characterized in that after the reaction with diepoxide there are mixed with the product 0,1 - 5 parts of low-molecular weight alcohol ethoxylate per part of thickener. A thickening agent that can be obtained by any one of the processes according to claims 1 - 6. Use of the thickening agents according to any one of the claims 1 - 6 for the thickening of aqueous systems. Use according to claim 8 for the thickening of aqueous hydraulic fluids.

Inventors: FITZEK DORIS, VAN DE BERG ALBERT, FITZEK, DORIS, VAN DE BERG, ALBERT
Applicants: AKZO NOBEL NV, AKZO NOBEL N.V.
Application year: 1989
Main classification: C08G65
IPC codes: C10M173, C08G65, C08L63, C09K3