SKID RAIL

Abstract: A skid rail (1A) for use in furnaces, particularly furnaces for heating steel pieces for hot processing, comprising a central water-cooled skid pipe (2) with a coating of refractory insulator (5), through which project skid members (4A) mounted on saddles (3A) welded to the pipe (2). To achieve high resistance to heat-deformation, shock, and abrasion the skid rail uses, as the material of the skid members (4A) thereof, an oxide-dispersion reinforced type super alloy which comprises specified proportions of Cr, Fe, Al and Ti, and optionally a certain amount of Co, the balance being Ni, and contains fine particles of a high melting point metal oxide such as Y₂O₃, ZrO₂ and Al₂O₃ dispersed in the austenitic matrix of the alloy.

Description: The present invention relates to skid rails for furnaces, such as are used in, for example, the steel industry for heating steel pieces. As the material for preparing skid rails of heating furnaces such as walking beam furnaces or pusher furnaces, heat-resistant casting alloys have been used. In the soaking zone of a furnace, the skid rails are subjected to such a high temperature as 1200 - 1350°C, and suffer from heat strain and abrasion, and therefore, the lives of the skid rails are short. It has been proposed to use ceramics having high heat-resistance and anti-abrasion properties as the material of the skid rails or skid buttons (for example, Japanese Utility Model Publication No. 35326/1980), and the assignee has made efforts in improving the material (for example, Japanese Patent Disclosure No. 89516/1985). So-called fine ceramics materials such as SiC and Si₃N₄ preferable from the view point of high shock-resistance thereof, which is one of the properties requested to the skid rails, are easily damaged by oxidation when used in a strongly oxidative atmosphere. On the other hand, research has been made since few years ago on the super alloys of oxide-dispersion reinforced type, i.e., Ni-based super alloys in which fine particles of an oxide having a high melting point such as Y₂O₃ are dispersed, and application thereof to gas-turbines and jet-engines has been tried (for example, Japanese Patent Publication No. 38665/1981). As to high temperature furnace it has been proposed to use an oxide-dispersion reinforced type super alloy of the composition consisting of 12.5 - 20 % Cr, up to 1% Al, up to 0.1 % C and up to 0.5 % (volume) Y₂O₃, the balance being Ni, as a material for mesh belts (Japanese Patent Publication No. 9610/1984). The task of the present invention is to provide skid rails for heating furnaces having not only high temperature deformation resistance, anti-abrasion property and shock resistance, but also a good oxidation resistance It has been found that this can be done advantageously by using the technology of reinforcing heat-resistant super alloys with dispersed fine oxide particles, and the solution according to the invention is set out broadly in the claims. Specific embodiments of the invention are described by way of example with reference to the drawings, in which: Fig. 1 to Fig. 3 illustrate a typical embodiment of a skid rail according to the invention: Fig. 1 being a plan view; Fig. 2, a side elevation view; and Fig. 3, a cross-sectional view. Fig. 4 and Fig. 5 illustrate another embodiment of a skid rail according to the invention: Fig. 4 being a plan view corresponding to Fig. 1; and Fig. 5, a side elevation view corresponding to Fig. 2. A typical embodiment of the skid rail according to the invention is, as shown in Fig. 1 to Fig. 3, a skid rail 1A made by welding metal saddles 3A on a water-cooled skid pipe 2, attaching a skid member 4A to each saddle and covering all the members except for the skid members with refractory insulator 5, which is characterized in that, as the material of the skid member, an oxide-dispersion reinforced type super alloy comprising 18 - 40 % of Cr, each up to 5 % of Fe, Al and Ti and the balance of Ni, and containing 0.1 - 2 % of fine particles of a high melting point metal oxide or oxide dispersed in the austenite matrix. Preferable range of Cr-content is 20 - 40 %, and more preferable range is 25 - 35 %. The high melting point metal oxide may be one or more selected from Y₂O₃, ZrO₂ and Al₂O₃. The super alloy may further contain up to 5 % of Co. Another embodiment of the skid rail according to the invention is the skid rail 1B shown in Fig. 4 and Fig. 5, which uses cylindrical saddles 3B, to which button shaped skid members 4B are attached. In order to produce the above mentioned oxide dispersion reinforced type super alloy, so-called mechanical alloying technology developed by INCO (The International Nickel Co., Inc.) is useful. The technology comprises finely grinding and mixing powders of metal components and fine crystals of a high melting point metal oxide in a high kinetic energy type ball mill so as to produce an intimate and uniform mixture of very fine particles of the components. The mixture prepared by the mechanical alloying is then compacted and sintered by hot extrusion or hot interstatic pressing and, if necessary, machined to the shape of the skid member. In general, oxide-dispersion reinforced type super alloys are stable even at a high temperature, and the above mentioned known alloys have alloy compositions suitable for uses such as turbine blades (Japanese Patent Publication No. 56-38665) or mesh belts (Japanese Patent Publication No. 59-9610) and contain suitable amounts of oxide particles. However, the known alloys are not useful as the material for a skid rail. By using the above described oxide-dispersion reinforced type super alloy according to the present invention, it is possible to achieve a high compression creep strength, as shown in the working examples described later, in addition to the heat-resistance and oxidation-resistance which meet using conditions in heating furnaces, and thus, durable skid rails are provided. The reasons for selecting the compositions of the present super alloy are as follows: Cr: 18 - 40 % If the content of Cr is less than the lower limit, the desired heat-resistance is not obtained. On the other hand, if it exceeds the upper limit, it becomes difficult to maintain the austenite structure. Preferable range of Cr content is 20 - 40 %, particularly, 25 - 35 %. Fe: up to 5 % Content of Fe should be limited preferably to 1 % or less. However, the super alloy of a higher Fe content up to 5 % can be used as the material for the present skid rail. Therefore, return scrap may be used as the raw material of the super alloy. Al: up to 5 %, Ti: up to 5 % For usual skid rails contents of these components in the super alloy may be 1 % or less. If, however, it is desired to enhance the anti-oxidation property, for example, for the skid rail to be used in heating furnaces with atmosphere of relatively large O₂ quantity (up to several %), further addition of those components up to 5 % will give improved results. Addition of higher amounts will cause increase of harmful large inclusions. Co: up to 5 % Addition of Co in an amount up to 5 % is useful for increasing hot strength of the alloy. The effect will saturate at around 5 %. High melting point metal oxide: 0.1 - 2 % The most preferable metal oxide is Y₂O₃. For the skid rail used in heating furnaces of relatively low temperature (up to about 1200°C) whole or a portion of Y₂O₃ may be replaced with ZrO₂ or Al₂O₃. Of course, combined use of two or three of Y₂O₃, ZrO₂ and Al₂O₃ is possible. Contents of the high melting point metal oxide should be 0.1 % or more. Otherwise, the effect of stabilizing the super alloy at a high temperature will not be satisfactory. As the content increases, the effect slows down at about 1% and saturates at 2 %, and therefore, a suitable content in this range should be chosen. EXAMPLES Oxide-dispersion reinforced type super alloys of INCONEL ALLOY MA758 group and having the compositions as shown in Table 1 (weight %, the balance being Ni) were prepared by the above noted mechanical alloying process, and the alloys were hot extruded and machined to give testing materials. The above obtained materials and a conventional skid rail material "TH101" (0.1C-32Cr-21Ni-23Co-2.5W-Zr) were subjected to compression test at a very high temperature for determining the durability as the material for the skid rail. Deformation (%) of the materials at various testing conditions are as shown in Table 2. From reference to the case of alloy No.1, 1300°C, stress 0.4 kg/mm² and 30 hours, it is seen that deformation of the conventional material reached 6.14 % and, in contrast, that the deformation of the material according to the present invention was so small as 0.28 %, thus the good results were ascertained. In practical use in soaking zones of steel heating furnaces, life of a skid rail embodying the present invention was more than 10 times of that of the conventional products. In the case of alloys No.3 and No.4 where a portion of Y₂O₃ was replaced with ZrO₂ or Al₂O₃, when compared with the case of Y₂O₃ alone the extent of deformation is even smaller at longer testing periods, and the performance is much higher than that of the conventional material. Further, it is expected that, even if all of the Y₂O₃ is replaced with ZrO₂, Al₂O₃ or combination thereof, the resulting oxide-dispersion reinforced super alloy can be used at a relatively low heating furnace temperature around 1200°C. Skid rails embodying the present invention may exhibit, when used in various furnaces such as heating furnaces for hot processing of steel, excellent properties of anti-hot deformation, anti-oxidation, anti-abrasion and thermal shock resistance, and therefore can be used for a long period. This will decrease maintenance labor of the heating furnaces and facilitates continuous operation thereof, thus decreased costs for energy and maintenance result in the costdown of hot processing of steel.

Claims: 1. A skid rail made by welding metal saddles on a water-cooled skid pipe, attaching skid members to the saddles and covering all the members except for the skid members with refractory insulator, characterized in that an oxide-dispersion reinforced type super alloy comprising 18 - 40 % (by weight) Cr, up to 5 % Fe, up to 5 % Al, up to 5 % Co and up to 5 % Ti, and the balance of Ni, and containing fine particles of 0.1 - 2 % high melting point metal oxide dispersed in the austenite matrix is used as the material of the skid members. 2. A skid rail of claim 1, wherein the high melting point metal oxide is Y₂O₃. 3. A skid rail made by welding metal saddles on a water-cooled skid pipe, attaching skid members to the saddles and covering all the members except for the skid members with refractory insulator, characterized in that an oxide-dispersion reinforced type super alloy comprising 20 - 40 % Cr, up to 1 % Fe, up to 1 % Al and up to 1 % Ti, and the balance of Ni, and containing fine particles of 0.1 - 2 % high melting point metal oxide dispersed in the austenite matrix is used as the material of the skid members. 4. A skid rail of claim 3, wherein the high melting point metal oxide is Y₂O₃. 5. A skid rail comprising a coolable skid pipe (2) having a covering (5) of refractory insulator material though which skid members (4) project outwardly, characterized in that the projecting skid members (4) are made from an oxide-dispersion-type super alloy comprising by weight: 18-40% Cr, 0.05% to 5% Fe, 0.05% to 5% Al, up to 5% Co, up to 5% Ti, 0.1-2% fine particulate high melting-point metal oxide, and Ni to 100%, the metal oxide being dispersed in the austenite matrix.

Inventors: INOUE, HISAO, ISOBE, SUSUMU 122-1, TAKIKAWACHO, KOBAYASHI, HIROSHI, TERAI, KAZUTO, TSUKUDA, KENJI
Applicants: DAIDO TOKUSHUKO KABUSHIKI KAISHA, INCO ALLOYS INTERNATIONAL, INC.
Application year: 1989
Main classification: F27D3
IPC codes: C21D1, C22C19, F27D1, F27D3