Method of forming stable dispersions of particulate matter

Abstract: The present invention discloses an improved method for forming stable dispersions of particulate matter. In particular, the present invention relates to a method of forming stable dispersions of particulate matter in both organic and silicone-based fluids.

Description: Field of the Invention The present invention relates to a method for forming stable dispersions of particulate matter. In particular, the present invention relates to a method of forming stable dispersions of particulate matter in both organic and silicone-based fluids. Background of the Invention The dispersion of particulate matter in various liquid media to yield stable suspensions represents a process of considerable technological importance in such fields as printing inks and paints. It is generally preferred that, consistent with acceptable rheological characteristics, the resulting suspension should have a high level of stability against sedimentation, or settling, of the suspended particulate matter. Alternatively, if settling does occur, the sediment should be redispersible without great difficulty. Several factors are known to affect the stability of suspensions including size, shape, polarity, charge and density of the particulate matter. Among these the role of size is generally considered to be most important as predicted by Stokes law of sedimentation (or levitation). For practical purposes, if less than about 0.1 µm in size, particles will stay in suspension for many months provided they remain singly dispersed. In fact, a primary objective of most suspension processes is to reduce the size of the particles of the material to be suspended as much as is feasible by mechanical means, such as milling, in the dry state and/or in the suspended state. Milling is often done in the presence of grinding aids or suspension aids to facilitate the generation and/or stabilization of fine particles. Experience has taught that the prevention of agglomeration of primary particles is frequently very difficult. Three main types of interaction between suspended particles have been defined: (a) electrical (repulsive between like charges); (b) van der Waals; and (c) colloid protection. Broadly speaking, these are influenced by electrical charge, polarity of the medium, and added macromolecules, respectively. The theory of suspension stability is well substantiated for aqueous systems but for non-aqueous systems agreement between theory and practice is less well established. The conventional approach to achieve improved suspension stability is the addition of "suspension aids". These can be of several different varieties but all seek to render the dispersed particles more compatible with the continuous phase of the dispersion and/or prevent their substantial settling. Conventionally used suspension aids are surfactants and amphiphilic polymers which act by adsorption at the particle/liquid interface. Sometimes a second liquid is added, and usually in appreciable amount, in an attempt to match the polarity of the continuous phase and the particles. Lastly, non-specific thickening of the liquid medium by addition of a suitable polymer is sometimes employed to reduce particle agglomeration and/or settling. Existing literature teaches that, in contradiction to the present invention, contacting the particulate matter with a second liquid can often have a detrimental effect on suspension stability. The best known case of this is the presence of water in a pigment, such as titanium dioxide, which is dispersed in an organic low polarity liquid. The presence of the water can lead to the formation of rapidly settling agglomerates of the pigment. Pre-addition of a relatively large amount of a secondary liquid prior to mixing with the primary liquid, or continuous phase, is generally not employed. Belgian Pat. 655,167 discloses a process to improve paint covering power and luster, which involves pretreatment of the pigment with about 40% by weight of water and then with 1% by weight of a surface modifying ingredient, e.g. acetylacetone, followed by heating of the resulting slurry to dryness. Thereafter, this dried, treated powder is dispersed in the dispersed phase. It has now been found that a process, in which the addition of a suitable secondary liquid to a finely divided powder prior to its blending with the continuous phase is carried out, can materially improve the suspension suitability even though the final concentration of secondary liquid may be so small as to have insignificant influence on the polarity of the continuous phase overall. GB-A-207 275 discloses a process for preparing finely divided pigments which comprises (a) wetting a dry finely divided pigment with an organic solvent, the solvent being partially or entirely miscible with an oil (b) removing substantially the whole of the solvent by heating and (c) incorporating the pigment with oil. According to the working examples this process requires a heating step to remove the treatment agent. It is known from US-A-3 311 477 to pretreat particulate matter with certain liquids. This document, however, requires (a) a pretreatment liquid mixture of water and a volatile organic liquid miscible with water and (b) drying the wetted solid to remove the wetting liquid. Summary of the Invention The present invention involves an improved method for forming stable dispersions of particulate matter in organic and/or silicone-based fluids through pretreatment of the particulate matter with an effective amount of a liquid selected from the group of lower molecular weight alcohols, chloroform, acetone and heptane, prior to introduction of the particulate matter into the continuous phase of the dispersion. The present invention is directed to a process for forming stable dispersions of particulate matter as described in claim 1. Further embodiments of the invention are set forth in dependent claims 2 to 8. Description of the Invention This invention is based on the discovery that in certain instances of making dispersions of particulate matter in organic and/or silicone-based fluids, pre-addition of a suitable liquid to the particulate matter can markedly improve the stability of the resulting dispersion. In the practice of the present invention, the continuous phase of the dispersions to be formed can be organic fluids, silicone based fluids and mixtures thereof. Preferred as the continuous phase in the formation of dispersions within the scope of the present invention are mineral oils, polyorganosiloxane fluids and polyalkylene glycols. Particularly preferred is the use of (a) polyorganosiloxanes of the formula wherein R, which may be the same or different, is an alkyl group having from 1 to 12 carbon atoms and x has a value from 5 to 50,000 and (b) polyalkylene glycols wherein the alkylene group contains from 2 to 3 carbon atoms. While the selection of particulate matter is not narrowly critical in the practice of the present invention, it must not be soluble in the continuous phase. Preferred in the practice of the present invention is the use as particulate matter of magnesium stearate, calcium stearate, barium stearate and silica. The particulate matter may be present in amounts ranging from 0.01 to 20% by weight, based upon the weight of the continuous phase. Preferably, the particulate matter is present in amounts ranging from 0.1 to 5.0%, on the same basis. Prior to the addition of the particulate matter to the continuous phase, the particulate matter is pretreated through contact with a liquid selected from the group consisting of lower molecular weight alcohols, chloroform, acetone and heptane. Preferred lower molecular weight alcohols include ethanol, isopropanol, n-butanol, t-butanol and n-amyl alcohol. The amount of liquid used in pretreatment of the particulate matter ranges from 1 to in excess of 100% by weight, based upon the weight of the particulate matter. Preferably, from 5 to 50% by weight, on the same basis, of liquid is used in the pretreatment of the particulate matter. Most preferably, from 25 to 35% by weight, on the same basis, is employed. The wet particulate matter pretreated with the liquid may be added to the continuous phase to form the desired dispersion. Drying of the pretreated particulate matter is not required nor is it desired. Due to the relatively small amount of the pretreatment liquid relative to the continuous phase present in the resulting dispersion, the pretreatment liquid does not unduly influence the character of the continuous phase. Surprisingly, as exemplified herein, the addition of the pretreatment liquid along with untreated particulate matter directly to the continuous phase results in no increase in the stability of the resulting dispersion. Indeed, in some instances, an adverse effect on the exhibited properties is found. While not wishing to be bound by the following theory, it is speculated that the interactions which occur between the particulate matter when introduced into the continuous phase is affected by the presence of the pretreatment liquid on the particles. These interactions in turn govern the eventual state of the dispersion and agglomeration of the particulate matter and are thus critical to the stability of the dispersion. It must be stated that, despite the obvious utility of the present invention, the systems which can benefit from its teachings are not readily predictable and must be determined empirically. Indeed, different samples of nominally the same particulate matter have been found to act differently in response to a particular added pretreatment liquid in sedimentation tests. The following examples are given to further illustrate the invention . All percentages set forth hereinafter are by weight unless otherwise noted. EXAMPLE I 2 parts of powdered magnesium stearate were mixed with 1 part of isopropanol (IPA) to form a paste. A 4% solid suspension was prepared by adding an appropriate amount of a blend of polyamylsilicone and polydimethylsilicone oils to the paste and mixing to homogeneity by a roll mill. The resulting homogeneous dispersion was poured into a 100ml graduated glass cylinder for measurement of the settling rate. The above procedures was repeated by replacing IPA with t-butanol, chloroform, heptane and, as a comparative liquid, a blend of polydimethylsilicone oil and polyamylsilicone. A control sample was also prepared by mixing four grams of the magnesium stearate with ninety-six grams of the above blends of silicone fluids. The settling rate of each dispersion was monitored over a period of 3 days. The % settling data is set forth in Table I and refers to the clear top fraction after the particulate matter settled. Pretreatment Liquid 1 day 2 days 3 days None (Control) 20 42 47 Silicone fluid 2 13 25 IPA 1 2 8 t-butanol 3 5 9 chloroform 2 4 14 heptane 1 2 6 Improvement in the stability of the dispersion by pre-addition of a pretreatment liquid is apparent. The extent of improvement, however, varies with liquids. Pre-addition of the silicone fluid blend as a control experiment also showed improvement in suspension stability. However, this level of improvement may be due to the mechanical work introduced during mixing. The extent of improvement is much less than that obtained on pre-addition of the 4 liquids within the scope of the present invention. EXAMPLE II 1 part of magnesium stearate was mixed with 2 parts of IPA and allowed to evaporate at room temperature until pastes containing the desired level of IPA were obtained. Thus, pastes containing 5%, 10%, 30% and 50% IPA were prepared. Appropriate amounts of the silicone fluid blend of Example I were then added to the pastes to prepare dispersions containing 4% solids. No mechanical mixing was employed. The dispersions were then poured into 100 ml graduated glass cylinders and the settling rates were measured. A control sample was also prepared by mixing 4 grams of the magnesium stearate with 96 grams of the silicone fluid blend. Sample 1 day 2 days 3 days None (Control) 20 42 47 5% IPA 12 26 41 10% IPA 2 11 24 30% IPA 2 4 10 50% IPA 6 21 26 The effect of pre-addition of a second liquid is detectable at levels of 5% to 50%. EXAMPLE III (Comparative) Appropriate amounts of IPA were mixed with the silicone fluid blend of Example I so that the fluids would contain 0.1%, 0.3%, 0.5%, 1%, and 2% IPA. 4 grams of magnesium stearate were then introduced into 96 grams of the individual fluids. The suspensions were then poured into 100 ml graduated glass cylinders and the settling rates were monitored. The settling rates of all the suspensions were essentially the same, thereby showing that pre-addition of an equivalent amount of a pretreatment liquid to the continuous phase does not affect the stability of the dispersion. EXAMPLE IV 2 parts of magnesium stearate were mixed with one part of IPA, then diluted with an appropriate amount of 10 centistoke dimethylsilicone oil to a 6% solid dispersion. The process was repeated with heptane instead of IPA and the settling rates were then measured. A control was also prepared by mixing 6 grams of Mg stearate with 94 grams of the 10 centistoke oil. Sample 1 day 2 days 3 days Control 6 24 30 Pre-addition of IPA 2 3 9 Pre-addition of heptane 2 11 16 The effect of pre-addition of the pretreatment liquid on the stability of a dispersion with a different solid level in dimethylsilicone oil was demonstrated. EXAMPLE V 2 parts of each of calcium stearate, zinc stearate and Chemical barium stearate were mixed with one part of IPA, then diluted with an appropriate amount of 10 centistoke dimethyl silicone oil to form 4% solid dispersions. The process was repeated with heptane instead of IPA. The respective control was also prepared without the pre-addition of IPA or heptane. The settling rates of the suspensions were monitored in 100 ml graduated glass cylinders. Sample Control Pre-addition of IPA Pre-addition of heptane Ca stearate 30 10 12 Zn stearate 30 20 8 Ba stearate 62 43 32 EXAMPLE VI 2 parts of magnesium stearate were mixed with 1 part of IPA, then diluted with appropriate amount of white mineral oil (65-75 SUS) to form a 4% solid suspension. The process was repeated with heptane instead of IPA. A control was prepared without pre-addition of IPA or heptane. Sample 1 day 2 days 3 days Control 11 24 -- Pre-addition of IPA 5 -- 16 Pre-addition of heptane 6 -- 11 EXAMPLE VII 2 parts of zinc stearate were mixed with 1 part of IPA, then diluted with an appropriate amount of a polypropylene glycol, marketed by Union Carbide as UCON R LB-65 to a 4% solid suspension. The process was repeated with heptane instead of IPA. A control was prepared without pre-addition of IPA or heptane. Sample Control 58 Pre-addition of IPA 45 Pre-addition of heptane 32 EXAMPLE VIII 1 part of TULLANOX® 500 hydrophobized silica was mixed with 2 parts of heptane, then diluted with 10 centistoke dimethyl silicone oil to form a 1% solid suspension. A control was prepared without pre-addition of heptane. Unlike the suspension of the metallic stearate, this suspension is nearly transparent due to the similarity of the refractive indexes of silica and silicone. However, after settling with time, the accumulation of silica can be detected at the bottom of the glass cylinders. The % volume settled at the bottom is used for the determination of the settling rate. % volume settled in dimethyl silicone oil Sample 1 day 2 days 3 days Control 16 18 17 Pre-addition of heptane 11 12 12 The material accumulation at the bottom apparently goes through different packing structures. This is shown in the case of the control suspension which accumulates 18% in 2 days, but settles to 17% in 5 days.

Claims: A process for forming stable dispersions of particulate matter wherein organic and/or silicone-based fluids are the continuous phase of the dispersion comprising pretreating the particulate matter with a pretreatment liquid selected from lower molecular weight alcohols, chloroform, acetone and heptane, prior to introduction of the particulate matter into the continuous phase of the dispersion, adding the wet matter pretreated with the liquid to the continuous phase, whereby the pretreated particulate matter is not dried. The process of Claim 1 wherein the continuous phase of the dispersion comprises mineral oils, polyorganosiloxane fluids and polyalkylene glycols. The process of Claim 2 wherein the polyorganosiloxane fluids are of the formula wherein R, which may be the same or different, is an alkyl group having from 1 to 12 carbon atoms and x has a value from 5 to 50,000. The process of Claim 2 wherein the polyalkylene glycols contain from 2 or 3 carbon atoms. The process of claims 1 to 4 wherein the lower weight molecular alcohols comprise ethanol, isopropanol, n-butanol, t-butanol and n-amyl alcohol. The process for claims 1 to 5 wherein the particulate matter is selected from magnesium stearate, zinc stearate, calcium stearate, barium stearate and silica. The process of claims 1 to 6 wherein the particulate matter is present in the dispersion in amounts ranging from 0.01 to 20 %, preferably 0.1 to 5 % by weight, based upon the weight of the continuous phase. The process of claims 1 to 7 wherein the particulate matter is pretreated with pretreatment liquid ranging from 1 to in excess of 100 %, preferably 5 to 50 %, especially 25 to 35 % by weight, based upon the weight of the particulate matter.

Inventors: GODDARD ERROL DESMOND, LEUNG PAK SANG, YAN SUE LEIN, GODDARD, ERROL DESMOND, LEUNG, PAK SANG, YAN, SUE LEIN
Applicants: OSI SPECIALTIES INC, OSI SPECIALTIES, INC.
Application year: 1989
Main classification: C09D17
IPC codes: C09K8, C09C1, C09D17