Curable polymer composition

Abstract: A curable polymer composition comprising: (A) 100 parts by weight of an oxyalkylene base polymer having at least one silicon-containing group to the silicon atom of which a hydroxy group and/or a hydrolyzable group is bonded and which is cross linkable through formation of a siloxane bond, (B) 0.1 to 20 parts by weight of at least one compound selected from the group consisting of a compound having one silanol group in a molecule and a compound which, when reacted with moisture, generates a compound having one silanol group in a molecule, (C) 0.1 to 20 parts by weight of a compound having a silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded and an amino group, and (D) 0.01 to 5 parts by weight of a compound having a silicon-containing group to the silicon atom of which three hydrolyzable groups are bonded and an amino group, which composition provides a cured material having low modulus, good bond strength and improved weather resistance of bond strength.

Description: The present invention relates to a curable polymer composition. More particularly, the present invention relates to a curable polymer composition which comprises an oxyalkylene base polymer having at least one silicon-containing group to the silicon atom of which a hydroxy group and/or a hydrolyzable group is bonded and which is cross likable through formation of a siloxane bond (hereinafter referred to as a "silicon-containing reactive group"). Oxyalkylene base polymers having the silicon-containing reactive groups are disclosed in U.S.-A-3,971,751, and one typical example of such polymers is a polymer of the formula: wherein X'' is a hydrolyzable group such as a methoxy group. The oxyalkylene base polymers having the silicon-containing reactive groups are cured through formation of siloxane bonds (Si-O-Si) between the polymer chains by the function of moisture in the air at room temperature to provide a rubbery cured material in the similar way to room temperature curable silicone rubbers. Since the cured material has good elongation properties, strength and adhesivity, it is used as a sealant, an adhesive and the like. When the rubbery cured material is used as the sealant, it should satisfy various requirements, among which, the tensile properties and adhesivity to a substrate are important. The tensile properties include modulus, elongation, strength at break, and often the rubbery cured material is required to have low modulus and large elongation, which are both characteristic properties of the rubber. The adhesivity includes bond strength and weather resistance of bond strength. The rubbery cured material is required to have large bond strength and good weather resistance of bond strength. Particularly when the rubbery cured material is used as a building sealant, it is often applied on a transparent material such as glass. Therefore, the weather resistance of bond strength, particularly the weather resistance under light illumination is important. As a curable polymer composition which comprises the oxyalkylene base polymer having the silicon-containing reactive group and provides a cured material having low modulus, U.S.-A-4,788,254 discloses a curable polymer composition comprising said oxyalkylene base polymer, a compound having one silanol group in a molecule and/or a compound which generates a compound having one silanol group in a molecule when reacted with moisture (hereinafter referred to as "monovalent silanol compound" collectively). To improve adhesivity of the cured material of the oxyalkylene base polymer having the silicon-containing reactive group, Japanese Patent Kokai Publication No. 182350/1982 discloses the use of a compound having a silicon atom to which a hydrolyzable group is bonded and an amino group such as γ-aminopropyltrimethoxysilane [H₂NCH₂CH₂CH₂Si(OCH₃)₃] or γ-aminopropylmethyldimethoxysilane [H₂NCH₂CH₂CH₂Si(CH₃)(OCH₃)₂]. However, the composition comprising the silicon-containing compound having three hydrolyzable groups such as γ-aminopropyltrimethoxysilane provides a cured material having large modulus. Even when such silicon-containing compound is used in combination with the monovalent silanol compound, the former deteriorates the effects of the latter. The composition comprising the silicon-containing compound having two hydrolyzable groups such as γ-aminopropylmethyldimethoxysilane does not increase modulus of a cured material but the cured material has inferior weather resistance of bond strength. An object of the present invention is to provide a curable polymer composition which can provide a cured material having low modulus, good bond strength against a substrate and weather resistance of bond strength. Accordingly, the present invention provides a curable polymer composition comprising: (A) 100 parts by weight of an oxyalkylene base polymer having at least one silicon-containing group to the silicon atom of which a hydroxy group and/or a hydrolyzable group is bonded and which is crosslinkable through formation of a siloxane bond, wherein the silicon-containing group is a group represented by the formula: wherein R² is a substituted or unsubstituted C₁-C₄₀ organic group; X is a hydroxyl group or a hydrolyzable group; a is 0, 1 or 2; b is 0, 1, 2 or 3; and m is an integer of 0 to 19, provided that when two or more R² groups are present, they may be the same or different, that when two or more X substituents are present, they may be the same or different, that the sum of a and b is not less than 2 (two), that when m is not less than 2, the kinds of the repeating units in the brackets may be the same or different, (B) 0.5 to 10 parts by weight of at least one compound selected from the group consisting of a compound having one silanol group in a molecule and a compound which, when reacted with moisture, generates a compound having one silanol group in a molecule, wherein the compound having one silanol group is a compound represented by the formula (R³)₃SiOH wherein R³ is the same or different and a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms. (C) 0.5 to 10 parts by weight of a non-polymeric compound having a silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded and an amino group, and (D) 0.05 to 3 parts by weight of a non-polymeric compound having a silicon-containing group to the silicon atom of which three hydrolyzable groups are bonded and an amino group, the weight ratio of (B) to (C) being 1:0.01 to 1:5 and of (B) to (D) being 1:0.01 to 1:0.75. The oxyalkylene base polymer having the silicon-containing reactive group (hereinafter referred to as "oxyalkylene base polymer (A)") are disclosed in U.S.-A-3,971,751, 3,979,384 and 4,323,488, Japanese Patent Publication Nos. 36319/1970, 12154/1971 and 32673/1974, and Japanese Patent Kokai Publication Nos. 156599/1975, 73561/1976, 6096/1979, 82123/1980, 123620/1980, 125121/1980, 131022/1980, 135135/1980 and 137129/1980. The backbone of the oxyalkylene base polymer (A) generally comprises repeating units of the formula: -R¹-O- wherein R¹ is a substituted or unsubstituted divalent hydrocarbon group having 1 to 12 carbon atoms, preferably 1 to 8 carbon atoms. Although the backbone of the oxyalkylene base polymer (A) may consist of the repeating units of the formula: -R¹-O-, it may comprise other repeating units. When the other repeating units are contained, the content of the repeating units -R¹-O- is at least 60 % by weight, preferably at least 80 % by weight. Preferably, R¹ is a substituted or unsubstituted divalent alkylene group having 2 to 5 carbon atoms, particularly 3 or 4 carbon atoms. Specific examples of R¹ is -CH(CH₃)-CH₂-, -CH(C₂H₅)-CH₂-, -C(CH₃)₂-CH₂-, -(CH₂)₄-, etc. Among them, -CH(CH₃)-CH₂- is particularly preferable. The backbone of the oxyalkylene base polymer (A) may consists of only one kind of the repeating unit, although it may consists of two or more kinds of the repeating units. The silicon-containing reactive group bonded to the backbone of the polymer (A) is represented by the formula: wherein R² is a substituted or unsubstituted C₁-C₄₀ organic group; X is a hydroxyl group or a hydrolyzable group; a is 0, 1 or 2; b is 0, 1, 2 or 3; and m is an integer of 0 to 19, provided that when two or more R² groups are present, they may be the same or different, that when two or more X' substituents are present, they may be the same or different, that the sum of a and b is not less than 1 (one), that when m is not less than 2, the kinds of the repeating units in the brackets may be the same or different. Among the silicon-containing reactive groups (I), a group of the formula: wherein R² is the same as defined above and ℓ is 1, 2 or 3 is preferred. Specific examples of the hydrolyzable group X in the formula (I) are halogen atoms (e.g. chlorine), a hydrogen atom, alkoxy groups (e.g. a methoxy group and an ethoxy group), acyloxy groups (e.g. an acetoxy group), ketoximate groups, (e.g. a dimethylketoximate group), amino groups (e.g. a dimethylamino group), amide groups (e.g. an N-methylacetamide group), aminoxy groups (e.g. a dimethylaminoxy group), mercapto groups (e.g. a thiophenoxy group) and alkenyloxy groups (e.g. an isopropenyloxy group). Among them, the alkoxy groups such as the methoxy group and the ethoxy group are preferred in view of their mild hydrolyzability. An example of the R² group in the formula (I) is a substituted or unsubstituted C₁-C₄₀, preferably C₁-C₂₀ hydrocarbon group or a triorganosiloxy group. Specific examples of the R² group are substituted or unsubstituted alkyl groups (e.g. a methyl group, an ethyl group and a chloromethyl group), cycloalkyl groups (e.g. a cyclohexyl group), alkenyl groups (e.g. a vinyl group), substituted or unsubstituted aryl groups (e.g. a phenyl group, a tolyl group and a chlorophenyl group) and aralkyl groups (e.g. a benzyl group), and further a triorganosiloxy group of the formula: (R′)₃SiO- wherein R′ groups are the same or different and each a substituted or unsubstituted monovalent organic group having 1 to 20 carbon atoms such as a methyl group and a phenyl group. Among these groups, the methyl group is preferable as the R² group. The oxyalkylene base polymer (A) may have at least one silicon-containing reactive group in a molecule. In view of preferable curing properties, the polymer (A) has 1.1, preferably 1.5 to 4 silicon-containing reactive groups on the average in a molecule. Preferably, the silicon-containing reactive group is bonded to the molecule end of the oxyalkylene base polymer (A). The oxyalkylene base polymer (A) preferably has a number average molecular weight of 3,000 to 30,000, more preferably 5,000 to 15,000. The oxyalkylene base polymers (A) may be used independently or a mixture of two or more of them. The oxyalkylene base polymer (A) may be prepared by various methods. For example, the oxyalkylene base polymer having a first functional group Y is reacted with a compound having the silicon-containing reactive group and a second functional group Y′ which reacts with the first functional group Y, whereby the silicon-containing reactive group is introduced in the oxyalkylene base polymer. Specific manners for such reaction are as follows: (1) The oxyalkylene base polymer having unsaturated groups is reacted with a hydrosilane compound having the hydrolyzable group such as HSi(OCH₃)₃ in the presence of a catalyst such as a compound of a metal of the VIII group of the periodic table (hydrosilylation). Example of the hydrosilylation reaction (2) The oxyalkylene base polymer having unsaturated groups is addition reacted with a compound having the silicon-containing reactive group and a mercapto group such as HS(CH₂)₃Si(OCH₃)₃. (3) The oxyalkylene base polymer having isocyanate groups with a compound having the silicon-containing reactive group and an active hydrogen-containing group such as H₂N(CH₂)₃Si(OCH₃)₃. Example of the reaction (4) The oxyalkylene base polymer having hydroxy groups is reacted with a compound having the silicon-containing reactive group and the isocyanate groups such as OCN(CH₂)₃Si(CH₃)₃. Among these methods, the reaction of the oxyalkylene base polymer having the unsaturated groups with the hydrosilane compound is often used. The oxyalkylene base polymer having the unsaturated groups may be prepared by introducing the unsaturated groups with the use of hydroxy groups of the oxyalkylene base polymer having the hydroxy groups (cf. Japanese Patent Kokai Publication No. 6097/1979). The oxyalkylene base polymer (A) to be used in the present invention is not limited to those prepared by the above described methods, and those prepared by any other methods can be used. The oxyalkylene base polymer (A) further includes an oxyalkylene base polymer the backbone of which is modified. Examples of such polymer are a polymer obtainable by polymerizing a polymerizable monomer in the presence of the oxyalkylene base polymer (A) and a polymer obtainable by introducing the silicon-containing reactive group in a polymer obtained by polymerizing a polymerizable monomer in the presence of the oxyalkylene base polymer having the hydroxy groups. The curable polymer composition of the present invention contains at least one monovalent silanol compound selected from the group consisting of the compound having one silanol group in a molecule and the compound which generates a compound having one silanol group in a molecule when reacted with moisture. By the use of the monovalent silanol compound, the modulus of the cured material of the oxyalkylene base polymer (A) can be decreased. The monovalent silanol compound is easily available and achieves such effect by simply adding it to the curable composition of the oxyalkylene base polymer (A). As the compound having one silanol group in a molecule, any compound having one group of the formula: ≡SiOH can be used. Specific examples of such compound are compounds of the formula: (R³)₃SiOH wherein R³ are the same or different and a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms such as (CH₃)₃SiOH, (CH₃CH₂)₃SiOH, (CH₃CH₂CH₂)₃SiOH, (C₆H₅)₃SiOH, (CH₃)(C₆H₅)₂SiOH and (CH₃)₂(C₆H₅)SiOH; cyclic polysiloxanes such as linear polysiloxanes of the formula: wherein R³ is the same as defined above and n is an integer of 0 to 40. Among them, those having the high content of the ≡SiOH groups have the larger effect when the amounts of the compounds to be added are the same. From this view point, (CH₃)₃SiOH and (CH₃CH₂)₃SiOH are preferred. (C₆H₅)₃SiOH is also preferred due to its easy handling and stability in the air. As the compound which generates a compound having one silanol group in a molecule when reacted with moisture, exemplified are derivatives of the compounds of the formula: (R³)₃SiOH wherein R³ is the same as defined above. Specific examples of such the derivatives are those knows as silylating agents such as (CH₃)₃SiNHSi(CH₃)₃, (CH₃)₃SiN(CH₃)₂, (CH₃)₃Si-NH-CO-NH-Si(CH₃)₃, and CF₃-SO₂-OSi(CH₃)₃. Among them, (CH₃)₃SiNHSi(CH₃)₃ is preferred due to the large content of the ≡SiOH groups of the hydrolyzed compound. These monovalent silanol compounds improve the tensile properties of the cured material, that is, they decrease the modulus and increase the elongation of the cured material of the polymer composition of the present invention. This is because the monovalent silanol compound reacts with the silicon-containing reactive group of the oxyalkylene base polymer (A) to cap said group, whereby the number of the cross-linking sites in the cured polymer decreases and in turn an average molecular weight between the adjacent cross linked points decreases. This results in the decrease of modulus and increase of elongation. The amount of the monovalent silanol compound (B) to be added to the composition is from 0.5 to 10 parts by weight per 100 parts by weight of the oxyalkylene base polymer (A), although it is possible to determine the amount of the monovalent silanol compound from the calculation of the silanol group equivalent based on the amount of the silicon-containing reactive group in the oxyalkylene base polymer (A). Usually, the monovalent silanol compound is added in such an amount that the silanol group equivalent is 0.1 to 0.9 time the silicon-containing reactive group. It is preferred that not all the silicon-containing reactive groups are capped with the monovalent silanol compound and at least one silicon-containing reactive group per molecule of the oxyalkylene base polymer (A) remains uncapped. The monovalent silanol compound may be used in an amount more than 0.9 time the silanol group equivalent, but use of the monovalent silanol compound in such the large amount is not economical. In the compound (C) having the silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded and the amino group (hereinafter referred to as "difunctional aminosilane"), a typical example of the silicon-containing group to the silicon atom of which the hydrolyzable groups are bonded is represented by the formula: wherein R² is the same as defined above and X' is a hydrolyzable group. Specific examples of the hydrolyzable group are halogen atoms (e.g. chlorine), a hydrogen atom, alkoxy groups (e.g. a methoxy group and an ethoxy group), acyloxy groups (e.g. an acetoxy group), ketoximate groups, (e.g. a dimethylketoximate group), amino groups (e.g. a dimethylamino group), amide groups (e.g. an N-methylacetamide group), aminoxy groups (e.g. a dimethylaminoxy group), mercapto groups (e.g. a thiophenoxy group) and alkenyloxy groups (e.g. an isopropenyloxy group). Among them, the alkoxy groups such as the methoxy group and the ethoxy group are preferred in view of their mild hydrolyzability. As the amino group, a substituted or unsubstituted amino group can be used. A typical example of the amino group is represented by the formula: -NR⁴₂ wherein R⁴ is a hydrogen atom or a substituted or unsubstituted hydrocarbon group, preferably an alkyl group, having 1 to 30 carbon atoms. Specific examples of the difunctional aminosilane are as follows: H₂NCH₂CH₂CH₂Si(CH₃)(OCH₃)₂ H₂NCH₂CH₂NHCH₂CH₂CH₂Si(CH₃)(OCH₃)₂ (CH₃)NHCH₂CH₂CH₂Si(CH₃)(OCH₃)₂ (C₂H₅)NHCH₂CH₂NHCH₂CH₂CH₂Si(CH₃)(OCH₃)₂ H₂NCH₂CH₂CH₂Si(CH₃)(OCOCH₃)₂ H₂NCH₂CH₂CH₂Si(CH₃)[ON=C(CH₃)(C₂H₅)]₂ H₂NCH₂CH₂CH₂Si(CH₃)[OC(CH₃)=CH₂]₂. The amount of the difunctional aminosilane (C) to be added to the polymer composition is from 0.5 to 10 parts by weight per 100 parts by weight of the oxyalkylene base polymer (A). The weight ratio of the monovalent silanol compound (B) to the difunctional aminosilane (C) is from 1:0.01 to 1:5, more preferably from 1:0.05 to 1:2. Desirably, the amount of the difunctional aminosilane does not exceed that of the monovalent silanol compound. In the compound (D) having the silicon-containing group to the silicon atom of which three hydrolyzable groups are bonded and an amino group (hereinafter referred to as "trifunctional aminosilane"), a typical example of the silicon-containing group to the silicon atom of which the hydrolyzable groups are bonded is represented by the formula: SiX'₃ wherein X' is the same as defined above. The amino group may be the same as exemplified in connection with the difunctional aminosilane. Specific examples of the trifunctional aminosilane are as follows: H₂NCH₂CH₂CH₂Si(OCH₃)₃ H₂NCH₂CH₂NHCH₂CH₂CH₂Si(OCH₃)₃ (CH₃)NHCH₂CH₂CH₂Si(OCH₃)₃ (C₂H₅)NHCH₂CH₂NHCH₂CH₂CH₂Si(OCH₃)₃ H₂NCH₂CH₂CH₂Si(OCOCH₃)₃ H₂NCH₂CH₂CH₂Si[ON=C(CH₃)(C₂H₅)]₃ H₂NCH₂CH₂CH₂Si[OC(CH₃)=CH₂]₃. The amount of the trifunctional aminosilane to be added to the polymer composition is from 0.05 to 3 parts by weight per 100 parts by weight of the oxyalkylene base polymer (A). The weight ratio of the monovalent silanol compound (B) to the trifunctional aminosilanol (D) is from 1:0.01 to 1:0.75, more preferably from 1:0.02 to 1:0.5, since the modulus of the cured material becomes too high if the amount of the trifunctional aminosilane is too large. The curable polymer composition of the present invention may contain conventional additives such as a curing accelerator, a plasticizer, and a filler. As the curing accelerator, organic tin compounds, acid phosphates, reaction products of acid phosphates and amines, saturated or unsaturated polybasic carboxylic acids and their anhydrides and organic titanates can be used. Specific examples of the organic tin compounds are dibutyltin dilaurate, dibutyltin dimaleate, dibutyltin phthalate, tin octylate and dibutyltin methoxide. The acid phosphates are phosphates having a residue of the formula: and include an organic acid phosphate of the formula: wherein R⁵ is an organic group and d is 1 or 2. Specific examples of the organic acid phosphate are (CH₃O)₂POOH, CH₃OPO(OH)₂, (C₂H₅O)₂POOH, C₂H₅OPO(OH)₂, [(CH₃)₂CHO]₂POOH, (CH₃)₂CHOPO(OH)₂, (C₄H₉O)₂POOH, C₄H₉OPO(OH)₂, (C₈H₁₇O)₂POOH, C₈H₁₇OPO(OH)₂, (C₁₀H₂₁O)₂POOH, C₁₀H₂₁OPO(OH)₂, (C₁₃H₂₇O)₂POOH, C₁₃H₂₇OPO(OH)₂, (HO-C₈H₁₆O)₂POOH, HO-C₈H₁₆OPO(OH)₂, (HO-C₆H₁₂O)₂POOH, HO-C₆H₁₂OPO(OH)₂, [CH₂(OH)CH(OH)O]₂POOH, CH₂(OH)CH(OH)OPO(OH)₂, [CH₂(OH)CH(OH)C₂H₄O]₂POOH, and CH₂(OH)CH(OH)C₂H₄OPO(OH)₂. Specific examples of the organic titanate compound are titanates such as tetrabutyl titanate, tetrapropyl titanate, tetraisopropyl titanate and triethanolamine titanate. When the curing accelerator is used, it is used in an amount of 0.1 to 10 parts by weight by weight per 100 parts by weight of the oxyalkylene base polymer (A). As the plasticizer, any of low molecular weight plasticizers such as dioctyl phthalate, high molecular weight plasticizers and viscous plasticizers may be used. Specific examples of the plasticizer are phthalates (e.g. dibutyl phthalate, diheptyl phthalate, di(2-ethylhexyl) phthalate, butylbenzyl phthalate, butylphthalylbutyl glycolate), esters of non-aromatic dibasic acids (e.g. dioctyl adipate, dioctyl sebacate), esters of polyalkylene glycols (e.g. diethyleneglycol dibenzoate, triethyleneglycol dibenzoate), phosphates (e.g. tricresyl diphosphate, tributyl phosphate), hydrocarbon base oil (e.g. chlorinated paraffins, alkyl diphenyl, partially hydrogenated terphenyl) and mixtures thereof. The plasticizer may be added during the preparation of the polymer. When the plasticizer is used, it is used in an amount of 1 to 150 parts by weight, preferably 10 to 120 parts by weight, more preferably 20 to 100 parts by weight per 100 parts by weight of the oxyalkylene base polymer (A). The filler may be any of the conventionally used ones, and includes silica such as silica fine powder, calcium carbonate (e.g. heavy or light calcium carbonate, precipitated calcium carbonated), kaolin, talc, silica, titanium oxide, aluminum silicate, magnesium oxide, zinc oxide and carbon black. Other additives are anti-sagging agents such as hydrogenated castor oil and organic bentonite, colorants and anti-aging agents. The curable polymer composition of the present invention may be used as a sealing agent, a templating material, a castable rubber material, a foaming material, an adhesive, a coating or a water-proofing material. For example, when the curable composition of the present invention is used as the building sealant, 10 to 300 parts by weight of the inorganic filler such as calcium carbonate, talc or kaolin and optionally the pigments such as titanium oxide and carbon black or the anti-aging agents such as a UV light absorber and an inhibitor of radical chain transfer are added to the composition, well kneaded with a kneader or a paint roll mill and then applied to have the composition exposed to moisture in the air whereby the composition is cured to give the rubbery material having good properties. The present invention will be illustrated by following Examples. Preparation Example In an autoclave equipped with a stirrer, polyoxypropylene base polymer 97 % of the molecular ends of which had allyl ether groups (average molecular weight, 8,000) (800 g) was charged and then metyldimethoxysilane (19 g) was added. To this mixture, 0.34 ml of a solution of chloroplatinic acid (H₂PtCl₆.6H₂O) (8.9 g) in a mixture of isopropanol (18 ml) and tetrahydrofuran (160 ml) was added, and the reaction was effected at 80°C for 6 hours to obtain polyoxypropylene base polymer having 1.7 groups of the formula: per molecule on the average according to the quantitative analysis of the silicon-containing groups by the NMR analysis. The reaction mixture contained little silicon hydride groups according to the analysis of the amount of residual silicon hydride residues therein by IR spectroscopy. Examples 1-3 and Comparative Examples 1-6 To the polymer prepared in Preparation Example (100 g), calcium carbonate (CCR, the trade name of Shiraishi Industry, Co., Ltd.) (120 g), titanium dioxide (R 820, the trade name of Ishihara Industries, Co., Ltd.) (20 g), diacetylacetonatodibutyltin (U-220, the trade name of Nitto Chemical Co., Ltd.) (2 g) as the curing accelerator, a terminal allyl ether type oxypropylene polymer having M n of 5,200 and M w /M n of 1.6 (50 g) in Examples 1 and 2 and Comparative Examples 1-6 or (2-ethylhexyl) phthalate (50 g) in Example 3, the monovalent silanol compound show in Table 1 (2 g), N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane [H₂NCH₂CH₂NHCH₂CH₂CH₂Si(OCH₃)₃] in an amount shown in Table 1 as the trifunctional aminosilane and N-(β-aminoethyl)-γ-aminopropylmethyldimethoxysilane [H₂NCH₂CH₂NHCH₂CH₂CH₂Si(CH₃)(OCH₃)₂] in an amount shown in Table 1 as the difunctional aminosilane were added and well mixed with a three roll mill. Then, an H-shaped test specimen was prepared from the mixture according to JIS A 5758 and tested on its tensile properties, bond strength and weather resistance of the bond strength under illumination (weathering bond strength) in the following manners: Tensile properties The H-shaped test specimen prepared according to JIS A 5758 with the use of an anodized aluminum plate as a substrate is aged at 23°C, 64 %RH for 14 days and further at 30°C for 14 days. Then, tensile test is done at a pulling rate of 30 mm/min. Bond strength The breaking state of the test specimen in the tensile property test is observed. When the cured material itself is broken (cohesive failure), the bond strength between the cured composition and the substrate is strong. When the cured material is peeled off at the interface between the cured material and the substrate (adhesive failure), the bond strength is weak. Weathering bond strength After accelerated weathering of the H-shaped test specimen prepared according to JIS A 5758 with the use of a glass plate as a substrate for 480 hours by means of the Sunshine weatherometer (manufactured by Suga Testing Machine Co., Ltd), the test specimen is subjected to the tensile test by means of the autographic recording machine (IS-5000 manufactured by Shimadzu) The results are shown in Table 1. The overall evaluation of the materials in Examples 1-3 and Comparative Examples 1-6 is shown in Table 2, in which "A" stands for good and "B" stands for poor. Exam. No. Monovalent silanol compound Trifunctional aminosilane/difunctional aminosilane Modulus Bond strength Weatherring bond strength 1 Yes 0.1/2.0 A A A 2 Yes 0.5/2.0 A A A 3 Yes 0.5/2.0 A A A C. 1 No 0.5/2.0 B A A C. 2 Yes 2.0/0 B A A C. 3 Yes 0/2.0 A A B C. 4 Yes 0/0 - B B C. 5 No 0/2.0 B A B C. 6 No 2.0/0 B A A

Claims: Claims for the following Contracting States : BE, CH, LI, DE, FR, GB, IT, NL, SE A curable polymer composition comprising: (A) 100 parts by weight of an oxyalkylene base polymer having at least one silicon-containing group to the silicon atom of which a hydroxy group and/or a hydrolyzable group is bonded and which is crosslinkable through formation of a siloxane bond, wherein the silicon-containing group is a group represented by the formula: wherein R² is a substituted or unsubstituted C₁-C₄₀ organic group; X is a hydroxyl group or a hydrolyzable group; a is 0, 1 or 2; b is 0, 1, 2 or 3; and m is an integer of 0 to 19, provided that when two or more R² groups are present, they may be the same or different, that when two or more X substituents are present, they may be the same or different, that the sum of a and b is not less than 2 (two), that when m is not less than 2, the kinds of the repeating units in the brackets may be the same or different, (B) 0.5 to 10 parts by weight of at least one compound selected from the group consisting of a compound having one silanol group in a molecule and a compound which, when reacted with moisture, generates a compound having one silanol group in a molecule, wherein the compound having one silanol group is a compound represented by the formula (R³)₃SiOH wherein R³ is the same or different and a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms. (C) 0.5 to 10 parts by weight of a non-polymeric compound having a silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded and an amino group, and (D) 0.05 to 3 parts by weight of a non-polymeric compound having a silicon-containing group to the silicon atom of which three hydrolyzable groups are bonded and an amino group, the weight ratio of (B) to (C) being 1:0.01 to 1:5 and of (B) to (D) being 1:0.01 to 1:0.75. The curable polymer composition according to claim 1, wherein the backbone of the oxyalkylene base polymer (A) comprises repeating units of the formula: -R¹-O- wherein R¹ is a substituted or unsubstituted divalent hydrocarbon group having 1 to 12 carbon atoms. The curable polymer composition according to claim 2, wherein R¹ is -CH(CH₃)-CH₂-. The curable polymer composition according to claim 1, wherein X in the formula (I) is a hydrogen atom, a halogen atom, a hydroxyl group, an alkoxy group, an acyloxy group, a ketoximate group, an amino group, an amido group, an aminoxy group, a mercapto group or an alkenyloxy group, and when two or more X groups are present, they may be the same or different. The curable polymer composition according to claim 4, wherein X in the formula (I) is the alkoxy group. The curable polymer composition according to claim 5, wherein X is a methoxy group. The curable polymer composition according to claim 1, the silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded in the compound (C) is a group of the formula: wherein R² is the same as defined above and X' is a hydrolyzable group. The curable polymer composition according to claim 1, wherein the amino group in the compound (C) is -NH₂. The curable polymer composition according to claim 1, wherein the silicon-containing group to the silicon atom of which the hydrolyzable groups are bonded in the compound (D) is a group of the formula: SiX'₃ wherein X' is a hydrolyzable group. The curable polymer composition according to claim 1, wherein the amino group in the compound (D) is -NH₂. Claims for the following Contracting State : ES A method for preparing a curable polymer composition comprising the step of mixing: (A) 100 parts by weight of an oxyalkylene base polymer having at least one silicon-containing group to the silicon atom of which a hydroxy group and/or a hydrolyzable group is bonded and which is crosslinkable through formation of a siloxane bond, wherein the silicon-containing group is a group represented by the formula: wherein R² is a substituted or unsubstituted C₁-C₄₀ organic group; X is a hydroxyl group or a hydrolyzable group; a is 0, 1 or 2; b is 0, 1, 2 or 3; and m is an integer of 0 to 19, provided that when two or more R² groups are present, they may be the same or different, that when two or more X substituents are present, they may be the same or different, that the sum of a and b is not less than 2 (two), that when m is not less than 2, the kinds of the repeating units in the brackets may be the same or different; (B) 0.5 to 10 parts by weight of at least one compound selected from the group consisting of a compound having one silanol group in a molecule and a compound which, when reacted with moisture, generates a compound having one silanol group in a molecule, wherein the compound having one silanol group is a compound represented by the formula (R³)₃SiOH wherein R³ is the same or different and a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms; (C) 0.5 to 10 parts by weight of a non-polymeric compound having a silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded and an amino group; and (D) 0.05 to 3 parts by weight of a non-polymeric compound having a silicon-containing group to the silicon atom of which three hydrolyzable groups are bonded and an amino group, the weight ratio of (B) to (C) being 1:0.01 to 1:5 and of (B) to (D) being 1:0.01 to 1:0.75. A method according to claim 1, wherein the backbone of the oxyalkylene base polymer (A) comprises repeating units of the formula: -R¹-O- wherein R¹ is a substituted or unsubstituted divalent hydrocarbon group having 1 to 12 carbon atoms. A method according to claim 2, wherein R¹ is -CH(CH₃)-CH₂-. A method according to claim 1, wherein X in the formula (I) is a hydrogen atom, a halogen atom, a hydroxyl group, an alkoxy group, an acyloxy group, a ketoximate group, an amino group, an amido group, an aminoxy group, a mercapto group or an alkenyloxy group, and when two or more X groups are present, they may be the same or different. A method according to claim 4, wherein X in the formula (I) is the alkoxy group. A method according to claim 5, wherein X is a methoxy group. A method according to claim 1, the silicon-containing group to the silicon atom of which two hydrolyzable groups are bonded in the compound (C) is a group of the formula: wherein R² is the same as defined above and X' is a hydrolyzable group. A method according to claim 1, wherein the amino group in the compound (C) is -NH₂. A method according to claim 1, wherein the silicon-containing group to the silicon atom of which the hydrolyzable groups are bonded in the compound (D) is a group of the formula: SiX'₃ wherein X' is a hydrolyzable group. A method according to claim 1, wherein the amino group in the compound (D) is -NH₂.

Inventors: HIROSE TOSHIFUMI, ISAYAMA KATSUHIKO, WAKABAYASHI HIROSHI, YUKIMOTO SADAO, HIROSE, TOSHIFUMI, ISAYAMA, KATSUHIKO, WAKABAYASHI, HIROSHI, YUKIMOTO, SADAO
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI CHEMICAL INDUSTRY CO., LTD.
Application year: 1989
Main classification: C08L71
IPC codes: C08K5, C08L71, C08G65