Temporary wet strength resins and paper products containing same

Abstract: Temporary wet strength resins having a molecular weight of from about 40,000 to about 400,000, most preferably from about 120,000 to about 210,000, having the formula: wherein: A is - H or --X-(R)-H and X is -O-, -NH-, or -NCH₃-, and R is a substituted or unsubstituted aliphatic group; Y₁ and Y₂ are independently -H, -CH₃, or a halogen; W is a nonnucleophilic, aliphatic amide; Q is a cationic monomeric unit. The mole percent of "a" ranges from about 1% to about 70%; the mole percent of "b" ranges from about 10% to about 90%; and the mole percent of "c" ranges from about 1% to about 40%.

Description: TECHNICAL FIELD This invention relates to wet strength resins which can impart temporary wet strength to paper products, and to paper products having temporary wet strength. BACKGROUND OF THE INVENTION Wet strength is a desirable attribute of many disposable paper products, such as napkins, paper towels, household tissues, disposable hospital wear, etc. which come into contact with water in use. However, an untreated cellulose fiber assemblage will typically lose 95% to 97% of its strength when saturated with water. To improve the wet strength paper manufacturers in the past have added wet strength resins during the paper making process. These wet strength additives have typically resulted in paper products with permanent wet strength, i.e., paper which when placed in an aqueous medium retains a substantial portion of its initial wet strength over time. Permanent wet strength in paper products is often an unnecessary and undesirable property. Paper products such as toilet tissues, etc., are generally disposed of after brief periods of use into septic systems and the like. Clogging of these systems can result if the paper product permanently retains its hydrolysis-resistant strength properties. More recently, manufacturers have added temporary wet strength additives to paper products for which wet strength is sufficient for the intended use, but which then decays upon soaking in water. Decay of the wet strength facilitates flow of the paper product through septic systems. As recognized in the pertinent literature relating to wet strength of paper products, such as Stannet, "Mechanisms of Wet Strength Development in Paper," Surface Coatings Related Paper Wood symposium, pp. 289-299 (1967) and Westfelt, "Chemistry of Paper Wet Strength. I. A survey of "Mechanisms of Wet Strength Development," Cellulose and Chemistry and Technology, Vol. 13, pp. 813-825 (1979), paper products develop dry strength in part due to interfiber hydrogen bonding. When the paper product is wetted, water disrupts the hydrogen bonds and, as a consequence, lowers the strength of the paper product. Historically, wet strength of paper products has been increased primarily by two approaches. One approach is to prevent water from reaching and disrupting the hydrogen bonds, for example, by coating the paper product. Another approach is to incorporate additives in the paper product which contribute toward the formation of interfiber bonds which are not broken or, for temporary wet strength, which resist being broken, by water. The second approach is the technique of choice, especially for tissue products. In this latter approach, a water soluble wet strength resin is added to the pulp, generally, before the paper product is formed (wet-end addition). The resin generally contains cationic functionalities, so that it can be easily retained by the cellulose fibers, which are naturally anionic. A number of resins have been used or disclosed as being particularly useful for providing wet strength to paper products. These include urea-formaldehyde and melamine-formaldehyde resins. Such resins have limited wet strength decay. Polyamide-epichlorahydrin resins have also been used in paper products. However, they also provide little wet strength decay. Numerous approaches for providing paper products claimed as having good initial wet strength which decays significantly over time have been reported. Resins formed by reacting glyoxal (CHOCHO) with water-soluble vinylamide polymers are suggested as possessing temporary wet strength in U.S. Patent No. 3,556,932, Coscia et al., issued January 19, 1971. However, wet strength decay is reported only at alkaline pH levels - conditions not necessarily present in septic systems. Also, papers incorporating such resins lose only about half their wet strength upon exposure to water. Greater degrees of wet strength decay are desirable. U.S. Patent No. 3,740,391, Williams et al., issued June 19, 1973, describes a water-soluble thermosetting wet strength agent for paper which is prepared by reacting an amidated ionic glucopyranosyl compound with glyoxal. Paper products containing this wet strength agent lose about one half their original wet strength after soaking in water for 24 hours. Such wet strength decay is not sufficiently rapid since the paper products in which the resin is used, such as toilet paper, are generally disposed of within a few minutes use. U.S.Patent 4,605,702, Guerro et al., issued August 12, 1986, discloses temporary wet strength resin made by reacting a vinylamide polymer with glyoxal, and then subjecting the polymer to an aqueous base treatment. The product is said to provide tissue paper which loses a part of its wet strength when soaked in water at neutral pH. U.S. Patent 4,603,176, Bjorkquist and Schmidt, issued July 29, 1986, discloses temporary wet strength resins made by reacting glyoxal with a cationic vinylamide copolymer. The cationic vinylamide copolymer is prepared from a nonnucleophilic, water-soluble monomer, such as dimethylacrylamide, an acrylamide nucleophilic monomer, and monomer containing a quaternary nitrogen. Subsequent to the reaction of glyoxal with the nucleophilic amide, the final product has from about 3% to about 65%, mole percent basis, of monomeric units with nucleophilic amide functionalities and about 1% to about 20%, mole percent basis, of monomeric units with glyoxal-substituted amide functionalities. US Patent 4,122,071, Moriya et. al, issued October 24 1978 represents another disclosure of a cationic vinyl amide copolymer reacted with glyoxal to form a temporary wet strength resin. The novel water soluble thermosetting resins of this disclosure are stated to have the property of nearly constant wet and dry strength over a range of pH values. Although paper incorporating these wet strength resins is asserted to be easily repulped, there is no recognition of the requirements for decay of the wet strength under conditions of low mechanical energy input such as septic sewage treatment systems. Modified starch temporary wet strength agents are marketed by the National Starch and Chemical Corporation (New York, New York). This type of wet strength agent can be made by reacting dimethoxyethyl-N-methyl-α-chloracetamide with cationic starch polymers. Modified starch wet strength agents are also described in U.S. Patent 4,675,394, Solarek, et al., issued June 23, 1987. Unfortunately, such wet strength agents typically deliver relatively high dry strength in conjunction with the level of wet strength provided. This is undesirable for products, such as tissue paper, for which softness is important because increased dry strength generally is accompanied by decreased softness. U.S. Patent 3,410,828, Kekish, issued November 12, 1968 and its parent, U.S. Patent 3,317,370, Kekish, issued May 2, 1967, disclose wet strength resins which comprise water soluble copolymers of an aldehyde monomer, such as acrolein, and a nitrogen heterocyclic monomer containing an ethylenically unsaturated group capable of polymerization with aldehydes. The advantages of these copolymers, as set forth in their respective patent disclosures, is that retention aids (such as aluminum salts), are not needed because the copolymers have no anionic character. Optionally, the copolymers can be made cationic by reacting a water soluble amine or quaternary amine with the copolymers. The disclosures of these patents generally link increased molecular weight with increased effectiveness without consideration of the particular properties and characteristics desirable for temporary, as opposed to permanent, wet strength. US Patent 3,819,555, Kaufman, issued June 25 1974 discloses wet strength polymers comprising a major proportion of vinylamide linkages intended to enhance dry strength properties of paper made therewith. The relationship of dry strength to wet strength and the importance of rapid decay of wet strength from an initially high value are not recognised by this disclosure. In spite of the technology described above, there exists a continuing need to provide temporary wet strength resins having increased wet strength decay rates. U.S. Patent No. 3,096,228, Day et al., issued July 2, 1983, describes paper products wherein a solution of glyoxal is applied to a paper web. Upon exposure to water, this paper described as being is able to resist a rupture for only about a minute and as disintegrating within about 3 minutes. While this approach using glyoxal monomers provides rapid wet strength decay, it does not provide paper products with sufficient initial wet strength or sufficient retention of wet strength over the period of intended use. It is an object of this invention to provide improved temporary wet strength resins that can provide high levels of initial wet strength and which retain sufficient strength during the period of intended use, but which also facilitate wet strength decay such that very low strength levels are attained subsequent to the period of intended use. SUMMARY Of THE INVENTION The temporary wet strength resins of the present invention comprise water-soluble, cationic polymers which have molecular weights of from 40,000 to 400,000, preferably from 70,000 to 250,000, more preferably from 100,000 to 210,000, most preferably from 120,000 to 210,000, and are of the formula: wherein: A is and X is -O-, -NH-, or -NCH₃-, and R is a substituted or unsubstituted aliphatic group; Y₁ and Y₂ are independently -H, -CH₃, or a halogen; W is a non-nucleophilic, aliphatic amide; and Q is a cationic monomeric unit. The mole percent of "a" ranges from 1% to 70%, preferably from 10% to 50%, more preferably from 20% to 40%; the mole percent of "b" ranges from 10% to 90%, preferably from 30% to 85%, more preferably from 52% to 80%; and the mole percent of "c" ranges from 1% to 40%, preferably from 2% to 20%, more preferably from 2% to 8%. The present invention also encompasses paper products containing the above-described resins. The resins as above defined in accordance with the present invention are further characterized by the substantially complete absence of nucleophilic functionalities attached to the polymer backbone that can react to form crosslink bonds with aldehydes. As used herein, the term "substantially complete absence" shall mean that the polymer contains less than 3 mole percent of monomer units having nucleophilic functionalities attached thereto. Preferably, the polymer contains less than 1 mole percent of such monomer units; and more preferably, essentially zero mole percent of such monomer units. As defined herein, the term "nonnucleophilic functionality" shall mean functional groups which do not form stable, covalent bonds with electrophilic functionalities (e.g., aldehydes) under chemical and physical conditions conventionally experienced during papermaking or during storage or use of paper products containing the resins of the present invention. Unless otherwise specified, all molecular weight values herein refer to the weight average molecular weight. Unless otherwise expressly specified, values for a, b, and c shall be mole percentage values based upon the average number of monomer units in the polymer chain. The monomeric units containing A and W, and the monomeric unit, Q, are randomly distributed throughout the polymer in ratios corresponding to the mole percentage ranges described herein. The cationic monomer unit Q can be derived from any polymerizable monomer which imparts a positive charge to the resin subsequent to polymerization. Cationic monomers suitable for use for the present invention are those which carry a positive electrostatic charge when dissolved in water. The counterion can be chloride, fluoride, bromide, iodide, sulphate, methylsulfate, phosphate and the like. Preferably, Q is hydrophilic and is an amine. Preferred cationic monomers include (p-vinylphenyl)trimethyl ammonium chloride, 2-(dimethylamino)ethyl acrylate, trimethyl(p-vinylbenzyl)ammonium chloride, p-dimethylaminoethylstyrene, dimethylaminopropyl acrylamide, 2-methylacryloxyethyltrimethylammoniummethylsulfate, and 3-(methacryloylamino)propyltrimethyl ammonium chloride. There is preferably between 1 mole % and 40 mole % of the cationic monomer unit present in the resin backbone. More preferably, there is between 2 mole % and 20 mole % of the cationic monomer unit present, most preferably between 2 mole % and 8 mole %. The non-nucleophilic functionality W can be incorporated into the polymer by polymerization with any monomer of the formula: wherein W and Y₂ are as defined above, with Y₂ preferably being -H. Preferably, W is hydrophilic, or at least does not make the polymer hydrophobic. Preferred non-nucleophilic monomers are those where W is: The non-nucleophilic functionality W is more preferably selected from a monomer having the formula: and most preferably is: There should be at least 10 mole percent and up to 90% mole percent of the non-nucleophilic monomer unit present in the resin polymer backbone. Preferably, the polymer contains from 30 mole percent to 85 mole percent of this component, more preferably from 52 mole percent to 80 mole percent. The crosslinking component of the polymers of the present invention, i.e., the monomer units having A attached thereto in Formula I, can be derived from the monomer: wherein Y₁ and A are as defined above. If A is: R can be a branched or straight chain aliphatic group. The aliphatic group preferably comprises a methylene or a C₂-C₇ chain, more preferably, a methylene or a C₂ chain. R can be substituted or unsubstituted. Preferably, if R is substituted, the substituent(s) will include an electron withdrawing functionality at the alpha-methylene position relative to the aldehyde group. Suitable electron withdrawing functionalities include: halogens, such as chlorine, fluorine, and bromine; amides, such as -NHCOR' wherein each R' can independently be lower chain (C₁-C₁₂) aliphatic groups, hydroxy groups; alkoxy groups, preferably with short chain (C₁-C₈) alkyl chains; cyano groups, e.g., -C≡N; and nitro groups, e.g., -NO₂. The aldehyde functionality can optionally be chemically protected during polymerization by techniques well-known in the art. Suitable specific examples of monomers for use include acrolein, methacrolein, 3,3-dimethyoxypropyl acrylamide, 3,3 diethoxypropyl acrylamide, 3,3-dimethoxypropyl methacrylamide, 2,2 dimethoxy-1-methylethyl acrylate,3,3-dimethoxypropyl methacrylate, 3-(methacryloylamino)propanal dimethylacetal, 2-(acryloylamino)-ethanal dimethylacetal, 2-(methacryloylamino)propanal dimethyl acetal, 5-(acryloylamino)pentanal dimethylacetal, and 8-(acryloylamino)octanal dimethylacetal. Acrolein is most preferred. Other suitable monomers are disclosed in U.S. Patent No. 3,410,828, Kekish issued November 12, 1986 and U.S. Patent No. 3,317,370, Kekish, issued May 2, 1967. The polymers of the present invention can be made by a wide variety of techniques, including bulk, solution, emulsion, or suspension polymerization. Preferably, the polymers are made by free radical terpolymerization. Suitable free radical initiators include, but are not limited to, thermal initiators, redox couples, and photochemical initiators. Such initiators are described generally in Kirk-Othmer Encyclopedia of Chemical Technology , 3rd edition, John Wiley & Sons (New York), Vol. 13, pp. 355-373 (1981) . Methods and techniques for polymerization are described generally in Encyclopedia of Polymer Science and Technology , Interscience Publishers (New York), Vol. 7, pp. 361-431 (1967), and Kirk-Othmer Encyclopedia of Chemical Technology , 3rd edition, Vol 18, pp. 740-744, John Wiley & Sons (New York), 1982 . The reaction is preferably carried out at temperatures less than 60°C. Typical water soluble initiators that can provide radicals at such temperatures include thermal initiators, including persulfates, such as potassium persulfate, and 2,2'-azobis (2-amidinopropane) dihydrochloride, redox couples, including persulfate and silver salt couples such as potassium persulfate and silver nitrate, and photochemical initiators. In one preferred method, water soluble starting monomers are terpolymerized in an aqueous solution polymerization process. See, for example, Sorenson, W. P. and Campbell, T. W., Preparative Methods of Polymer Chemistry , 2nd edition, Interscience Publishers (New York), 1986, pp. 248-251. Generally, as the molecular weight of the polymer decreases, initial wet strength will become smaller and wet strength decay will become faster. The temporary wet strength resins of the present invention have a molecular weight of at least 40,000, preferably at least 70,000, more preferably at least 100,000, and most preferably at least 120,000. The upper limit for molecular weight will be limited by a combination of the ability of the resin to impart the desired level of strength decay, discussed further below, and practical considerations such as sufficiently low viscosity for application to pulp slurries or pulp sheets and technical and economic concerns related to formation of such high molecular weight resins. The molecular weight is not more than 400,000, preferably less than 250,000, and more preferably less than 210,000. Molecular weight can be controlled by such methods that are known to those skilled in the art, such as varying reaction temperature (increased temperature typically results in reduced molecular weight), varying free radical initiator concentration, and utilization of chain transfer agents. Suitable chain transfer agents include β-mercaptoethanol, thioglycolic acid, glycerol, acetone, and isopropanol. Other suitable chain transfer agents are disclosed in Polymer Handbook , 2nd edition, J. Brandrup and E. H. Immergut, editors, Wiley Interscience (1975), pp. II-57 through II-104. The temporary wet strength resins of the present invention are useful for a wide variety of paper and paper products. As used herein, the terms "paper" and "paper products" include sheet-like masses and molded products containing fibrous cellulosic materials which may be derived from natural sources, such as wood pulp fibers, as well as other fibrous material characterized by having hydroxyl groups attached to the polymer backbone. These include glass fibers and synthetic fibers modified with hydroxyl groups. Cellulosic fibers are preferred. In addition, the present invention encompasses papers made from combinations of cellulosic fibers, or other fibers having hydroxyl-substituted polymer chains, and other fibrous or nonfibrous materials known in the art. The paper products of the present invention preferably contain at least 70%, more preferably at least 85%, by weight (dry product basis), cellulosic fibers. Suitable nonfibrous additions are described in Young, "Fiber Preparation and Approach Flow" Pulp and Paper Chemistry and Chemical Technology , Vol. 2, pp. 881-882. The resins of the present invention are particularly useful for nonwoven tissue paper products containing cellulosic fibers such as toilet paper, facial tissue, and paper towels. These products will typically have basis weights of between 8g/m² and 65g/m², and densities of between 0.05g/cm³ and 0.60g/cm³. They can be made according to any of the techniques known to the art. In forming paper and paper products, the temporary wet strength resins of the present invention are preferably added as dilute aqueous solutions at any point in the papermaking process where wet strength resins are customarily added. The temporary wet strength resins typically are readily absorbed by the cellulose fibers in an aqueous environment at pH values within the range of from 3.5 to 8.0. The polymer can develop wet strength in paper products both at room temperature and at temperatures at which paper is normally dried (85°C-125°C). A substantial amount of initial wet strength is generally imparted to the paper product when from 0.005% to 5% of the temporary wet strength resin by weight of the fiber is added. Typically, acceptable results, i.e., 35% of wet tensile decay at 15 minutes and at least 65% at 90 minutes after saturation, are achieved when from 0.25% to 2.0% of the resin by weight of the fiber is added. Preferably from 30 mole percent to 85 mole percent of the non-nucleophilic unit is present in the resin polymer as, when lower levels of this unit are added, there is an less than desirable amount of wet tensile decay over time and when greater than 85% of the non-nucleophilic unit is present, the paper products typically will not have good initial wet strength. The temporary wet strength resins of the present invention can be used in any type of tissue paper construction. These include: pattern densified tissue paper such as, but limited to, that disclosed in U.S. Patent 3,301,746, Sanford and Sisson, issued January 31, 1987, U.S. Patent 3,974,025, Ayres, issued August 10, 1976, U.S. Patent 4,191,609, Trokhan, issued March 4, 1980, U.S. Patent 3,821,068, Shaw, issued June 28, 1974, U.S. Patent 3,573,164, Friedberg et al., issued March 30, 1971, and U.S. Patent 3,994,771, Morgan et al., issued November 30, 1976; uncompacted, nonpattern-densified tissue paper such as, but not limited to, that disclosed in U.S. Patent 3,812,000, Salvucci et al., issued May 21, 1974 and U.S. Patent 4,208,459, Becker et al., issued June 17, 1980; and conventional tissue paper well known in the art, typically made by pressing a wet web at elevated temperatures to dewater and dry said web. With respect to tissue paper products, and with particular reference to products such as toilet paper, wherein high levels of softness are desired in addition to good initial wet strength with wet strength decay after the period of usage to low strength levels, it is highly preferred for the paper to have an initial wet strength/dry strength ratio (WT i /DT) of at least 10%, preferably at least 12%. Lower rates are less desirable since the amount of resin that will be added to develop sufficient wet strength will impart undesirably high amounts of dry strength, which reduces toilet softness of the dry paper product. Additionally, it is desirable for tissue paper products to exhibit a wet strength decay rate after 90 minutes of soaking in neutral pH water of at least 70%, preferably at least 80%, as defined according to the following equation: wherein: WT i = Initial wet tensile strength of paper with temporary wet strength resin; WT R = Wet tensile strength of paper with resin after 90 minutes soaking in neutral pH water; and WT O = Wet tensile strength of paper without temporary wet strength resin after soaking 90 minutes in neutral pH water. The tensile strength for the above equation is determined according to the procedure described in the Experimental section below. EXPERIMENTAL The following procedures are useful for preparing and testing paper products handsheets containing the resins of the present invention. Handsheets Handsheets can be formed from 100% unrefined Northern Softwood Kraft (NSK), or from other fibers as desired. After dispersing the NSK, or other fibers, in distilled water, the temporary wet strength resin is added to the disintegrated pulp and the slurry is agitated for a fixed period of time ranging from 1 to 60 minutes. Handsheets are made essentially according to TAPPI standard T205 with the following modifications: (1) tap water, adjusted to a desired pH, generally between 5.5 and 6.5, with HCl and/or NaOH is used; (2) the sheet is formed on a polyester wire and dewatered by suction instead of pressing; (3) the embryonic web is transferred by vacuum to a polyester papermaking fabric; (4) the sheet is then dried by steam on a rotary drum drier. The handsheets are aged a minimum of 24 hours in a conditioned room where the temperature is 73°F ⁺ 4F° (about 22.8°C⁺ 2.2C° and the relative humidity is 50% ⁺ 10%. Strength Test 1. Dry Tensile Strength This test is performed on one inch by five inch (about 2.5 cm X 12.7 cm) strips of paper (including handsheets as described above, as well as other paper sheets) in a conditioned room where the temperature is 73°F + 4F° about (228°C ± 2.2°C) and the relative humidity is 50 + 10%. An electronic tensile tester (Model 1122 (Instron Corp., Canton, MA) operated at a crosshead speed of 0.5 inches per minute (about 1.3 cm per min.) and a gauge length of 4.0 inches (about 10.2 cm). 2. Wet Tensile An electronic tensile tester (Model 1122, Instron Corp.) is operated at a crosshead speed of 0.5 inch (about 1.3 cm) per minute and a gauge length of 1.0 inch (about 2.5 cm), using the same size strips as for dry tensile. The strip is soaked in an aqueous solution containing approximately 23 parts per million (ppm) calcium ion (provided as calcium chloride), 7 ppm magnesium ion (provided as magnesium chloride), and 67 ppm sodium bicarbonate (provided as sodium bicarbonate) for the desired soak time, and then measured for tensile strength. As defined herein, initial wet tensile strength is measured when the paper has been saturated for about 5 seconds. It has been found that the resins in the present invention can provide paper products, such as tissue paper products, which have high WT i /DT ratios (10%, preferably 12% and higher) while also providing decay rates in excess of 80%. It is not, however intended to limit the scope of the invention to such tissue paper products. The following examples are provided to illustrate the present invention. The scope of the invention is to be determined by the claims which follow. EXAMPLE I This example exemplifies a process useful for the preparation of a temporary wet strength resin from acrolein, N,N-dimethylacrylamide, and a suitable ammonium chloride compound, having the formula: N,N-dimethylacrylamide (2.77 g, 27.9mmoles), acrolein (0.56 g, 9.99mmoles), [3-(methacryloylamino)propyl]trimethylammonium chloride (0.48 g, 0.0022mmoles), 2,2'-azobis(2-amidinopropane) dihydrochloride (V-50™, available from Wako Chemical USA, Inc., Dallas, Texas) (0.22 g, 0.0008 moles), β-mercaptoethanol (0.0625 g, 0.0008 moles), and water (8.0 ml) are added to a polymerization tube, which is sealed under argon after three successive freeze-pump-thaw cycles. The sealed tube is heated for four hours at 60°C and the contents are then transferred to dialysis bags (molecular weight cut-off at 3,500). Dialysis against water is conducted for 16 hours, and the contents of the bags are freeze-dried. A white solid material should be obtained. Molecular weight can be expected to be between 40,000 and 45,000; "a", between 65% and 70%; "b", between 26% and 31%; and "c", between 2% and 6%. The values for "a" and "b" can be determined by infra-red analysis according to techniques known in the art. The value for "c" can be determined by chloride titration, as described in Fundamentals of Analystical Chemistry , D. A. Skoog and D. M. West, Holt, Rinehart, and Winston (1963), p. 253. Resins with similar composition but different molecular weight can be prepared by varying the level of initiator (V-50) and/or the amount of chain transfer agent (e.g., β-mercaptoethanol), or by other techniques that will be known to those skilled in the art. EXAMPLE II This example exemplifies a process similar to that of Example I, except that smaller amounts of initiator and chain transfer agent and a longer reaction period are implemented. N,N-dimethylacrylamide (2.77 g, 27.9mmoles), acrolein (0.56 g, 9.99mmoles), [3-(methacryloylamino)propyl]trimethylammonium chloride (3.48 g, 2.18mmoles), 2,2'-azobis(2-amidinopropane) dihydrochloride (V-50™, available from Wako Chemical USA, Inc., Dallas, Texas) (0.022 g, 0.081mmoles), β-mercaptoethanol (0.0334 g, 0.428mmoles), and water (9.5 ml) are added to a polymerization tube, which is sealed under argon after three successive freeze-pump-thaw cycles. The sealed tube is heated for six hours at 60°C and the contents are then transferred to dialysis bags (molecular weight cut-off at 3,500). Dialysis against water is conducted for 16 hours, and the contents of the bags are freeze-dried. A white solid material should be obtained. Molecular weight can be expected to be between 135,000 and 140,000; "a", between 62% and 67%; "b", between 3096 and 35%; and "c", between 2% and 5%. EXAMPLE III A temporary wet strength resin is prepared by mixing [3-(methacryloylamino) propyl] trimethylammonium chloride (3726 g, 37.5 moles) with water (7.5 liters) in a 22 liter 3-neck round bottom flask fitted with an overhead stirrer and condenser. The solution is purged with argon for 45 minutes. Next, N,N-dimethylacrylamide (3738 g, 37.7 moles) and acrolein (753 g, 13.4 moles) are added to the flask. V-50 initiator (110 g, 0.4 moles) is dissolved in 740 ml water in a separate container. The initiator solution is then added to the 3-neck round bottom flask all at once to initiate the polymerization reaction. The contents are then heated from room temperature (about 25°C) to 50°C with constant stirring, at which point the reaction becomes exothermic. The reaction temperature is maintained between about 55°C and about 65°C by successively allowing the temperature to increase to no more than 65°C, and cooling the temperature to about 55°C. After the reaction is no longer exothermic (about 5 hours), the flask's contents are stirred an additional 19 hours at 55°C. The resin product can be collected from the reaction solution as described in Example I. The resin product will have the same composition as the product in Example I, except that molecular weight will typically be in the range of 200,000 to 210,000, "a" will typically be from 70% to 75%, "b" will typically be from 18% to 23%, and "c" will typically be from 4% to 8%. EXAMPLE IV This example shows a process for the preparation of a temporary wet strength resin of the present invention having the formula: wherein a is typically from 65% to 70%, b is typically from 26% to 31%, c is typically from 2% to 6%, and the molecular weight is from 40,000 to 45,000. A reaction solution containing N,N-dimethylacrylamide (2.48 g 25.0mmoles), acrolein (0.56 g, 9.99mmoles), 2,2'-azobis(2-amidinopropane)dihydrochloride (0.22 g, 0.81mmoles), β-mercaptoethanol (0.0625 g, 0.80mmoles) and water (9.5 ml) is prepared and added to a polymerization tube and sealed under argon after three sequential freeze-pump-thaw cycles. The contents are heated for four hours at 60°C and transferred to dialysis bags (molecular weight cut-off of 3,500). After 16 hours of dialysis against water, the reaction solution is freeze dried. The above polymer is then recoverable, in the form of a white, solid material. EXAMPLE V This example shows a process for the preparation of a temporary wet strength resin of the formula: A reaction solution containing N-N-dimethylacrylamide (1.99 g, 20.0mmoles), 3-(acryloylamino)propanal dimethylacetal (0.53 g, 3.07mmoles), diallyldimethylammonium chloride (0.52 g, 3.42mmoles), azobisisobutrylnitrile (0.03 g, (0.18mmoles), and ethanol (4.90 ml) is prepared, placed in a polymerization tube, and sealed under argon after three sequential freeze-pump-thaw cycles. The reaction solution is heated for four hours at 70°C and then transferred to dialysis bags (molecular weight cut-off of 3,500). After dialysis against ethanol for 16 hours, the polymer product can be isolated by removing residual solvent under reduced pressure. This polymer will have an acetal protecting group, which can be removed by dissolving the polymer in 0.020 N aqueous HCl (1.0 g of polymer per 40 ml of solution) and heating under an inert atmosphere for four hours at 40°C, to provide the final product. Molecular weight will typically be 40,000 and a, b, and c will typically be between 80% and 85%, between 10% and 15%, and between 2% and 5%, respectively. EXAMPLE VI Paper is made according to the teachings of Sanford and Sisson, U.S. Patent No. 3,301,746, issued January 31, 1967, and U.S. Patent No. 3,994,771, Morgan and Rich, issued November 30, 1976. The papermachine uses a single headbox with internal partitions ("leaves") which create a discretely layered three-layer paper sheet. The headbox is of the fixed roof former type. The center layer of the sheet is comprised of Northern Softwood Kraft pulp (Grande Prairie, Procter & Gamble Cellulose). This center layer comprises thirty percent (30%) of the total weight of the sheet, and the temporary wet strength resin of this invention is added into this layer at a rate of 1g/kg of the pulp (dry fiber basis). The outside two layers are identical, and each is approximately 35% of the total sheet weight, dry fiber basis. These layers are comprised of northern Aspen bleached sulfite pulp. The headbox dilution water is natural water which is acidified with HCl to an approximate pH of from 5.5 to 5.9. The discretely layered sheets are formed on a polyester 84M. This wire is an "84M"; that is, the weave was (84X76 filaments per inch) wire woven in a five-shed pattern to form an embryonic web. The embryonic paper web is transferred to a 36X32 five-shed fabric. These patterns and their use are described in Trokhan, U.S. Patent No. 4,191,609, and Trokhan, U.S. Patent No. 4,239,065. The embryonic paper sheet is first dried with hot air in a flow-through dryer to a moisture level of 35% by weight of the sheet. Such a hot air dryer Is well known to those skilled in the art. The final drying is accomplished on the surface of a Yankee dryer (to which the web has been adhered with polyvinyl alcohol). The paper is dried to approximately 3% moisture, and then creped from the Yankee with a doctor blade zone and reeled to provide an ultimate residual crepe of 20%.

Claims: A water soluble, temporary wet strength resin characterized by the substantially complete absence of nucleophilic functionalities, said resin having the formula: wherein: A is and X is -O-, -NH-, or -NCH₃-, and R is a substituted or unsubstituted aliphatic group; Y₁ and Y₂ are independently -H, -CH₃ or a halogen; W is a nonnucleophilic, aliphatic amide; Q is a cationic monomeric unit; the mole percent of a is from 1% to 70%; the mole percent of b is from 10% to 90%; and the mole percent of c is from 1% to 40%; said resin having an average molecular weight of between 40,000 and 400,000. A temporary wet strength resin according to Claim 1 wherein the mole percent of a is from 10% to 50% the mole percent of b is from 30% to 85% the mole percent of c is from 2% to 20% and the resin has a molecular weight of between 70,000 and 250,000. A temporary wet strength resin according to either one of Claims 1 and 2 and wherein a is from 20% to 40%, b is from 52% to 80%, and c is from 2% to 8%, and said average molecular weight is from 100,000 to 210,000, preferably from 120,000 to 210,000. A temporary wet strength resin according to any one of Claims 1-3 wherein A is -CHO, or wherein R comprises a methylene or a C₂-C₇ aliphatic chain. A temporary wet strength resin according to any one of Claims 1-4 characterised in that W is: A temporary wet strength resin according to Claim 5 wherein W is: and A is -CHO. A temporary wet strength resin according to any one of Claims 1-6 characterized in that the resin comprises less than 3 mole %, preferably less than 1 mole %, more preferably 0 mole %, of monomeric units having a nucleophilic functionality. A paper product comprising a sheet of fibrous materials, characterized in that it further comprises a temporary wet strength resin according to any one of the preceding Claims in an amount from 0.005% to 5% by weight of the fibrous materials said product having an initial wet tensile strength/dry tensile strength ratio of at least 10%, and a wet tensile decay rate after 90 minutes soaking in neutral pH water of at least 70%. A paper product according to Claim 8 wherein the initial wet tensile strength/dry tensile strength ratio is at least 12% and the wet tensile decay rate after 90 minutes soaking in neutral pH water is at least 80%.

Inventors: BJORKQUIST DAVID WILLIAM, BJORKQUIST, DAVID WILLIAM
Applicants: PROCTER & GAMBLE, THE PROCTER & GAMBLE COMPANY
Application year: 1989
Main classification: C08F220
IPC codes: C08F20, C08F216, A61L15, D21H17, C08F220, D21H21, C08F246, C08F16