CERAMIC CUTTING MATERIAL REINFORCED BY WHISKERS

Abstract: The present invention relates to a ceramic cutting insert comprising whiskers for chip forming machining of steel and having improved mechanical, thermal and wear properties. The insert comprises besides the oxide based matrix 5-50 % by volume, preferably 10-40 % by volume, of homogeneously dispersed whiskers of a solid solution of nitride and oxide of aluminium preferably of the cubic aluminium oxynitride spinel (AlON). A part of the whiskers may be replaced by whiskers of silicon carbide. The properties of the composite material can be further modified by coating the whisker material with thin layers. The whisker reinforced cutting material shows an improved toughness behaviour.

Description: The present invention relates to ceramic cutting tool materials and, in particular, to such cutting materials in which monocrystalline whiskers (hair crystals) based upon aluminium are homogenously distributed in an oxide based ceramic matrix which leads to an improved strength and toughness without having a negative influence on the wear resistance to any appreciable extent. Ceramic cutting tools have now been available for several decades but not until the last ten years they have got a commercial importance for use in chip forming machining. The main reason for the limited use of ceramic cutting tools has been sudden and unexpected cutting insert failures because of inadequate strength and toughness. During the last ten years the properties of ceramic cutting materials have been improved in many respects why they have increased their relative market share in cutting of cast iron and (nickel-base) alloys with high heat resistance. In cutting of steel, which is the completely dominating operation, the share of the cutting inserts being ceramic is still very modest because said workpiece material makes extreme simultaneous demands upon strength, toughness and wear resistance which have not been possible to fulfil by today known ceramic cutting tool materials. Aluminium oxide based cutting tools are very sensitive to thermal cracking as aluminium oxide in itself has a relatively low thermal conductivity. This fact leads to a very short life in steel cutting, particularly under conditions having short engagement times and varying cutting depths. To a certain extent the thermal properties have been improved by an addition of titanium carbide and/or titanium nitride which improves the thermal conductivity of the composite material. The addition of titanium carbide/nitride also increases the hardness of the material. In comparison with pure aluminium oxide materials an increased life is therefore obtained in cutting of hard workpiece materials and in operations demanding resistance to thermal shocks. This type of material has, however, too poor a toughness behaviour for a general use in cutting of steel. Another, later step of development includes addition of homogenously dispersed fine-grained zirconium oxide particles in a matrix of aluminium oxide. Transformation of the "metastable" zirconium oxide particles at the use increases both strength and toughness and will, thus, lead to a more predictable life. The thermal properties of said kind of material are, however, insignificantly better than those of pure aluminium oxide materials why initiation and growth of thermally induced cracks still are great problems in practical cutting operations generating high cutting edge temperatures such as machining of steel. It has recently been shown, e.g US 4,543,345 and EP-A-194 811, that alloying with SiC-whiskers, monocrystalline hair crystals, in a matrix of aluminium oxide leads to a greatly improved fracture toughness and strength. Ceramic cutting materials based upon this concept have proved very good performance in cutting of materials with high heat strength but in cutting of steel they have shown surprisingly short tool lives because of preferential attacks of the SiC-crystals leading to a weakening of the surface zone with accompanying high wear and risks of initiation of fractures. EP-A- 279 673 discloses aluminium oxide or aluminium nitride whiskers in a composite powder of alumina. DE 34 45 766 and DE 35 18 844 disclose alumina whiskers in a ceramic matrix. EP-A-283 454 discloses the use of whiskers of nitrides carbides and/or borides of Ti and/or Zr in an oxide based matrix. The matrix may consist of oxides only (white ceramics) or it may additionally contain hard particles of carbides or nitrides (black ceramics). For compounds with extended homogeneity range, such as TiC, the disclosure is not restricted to only compounds with stoichiometric composition. EP-A-296 133 discloses the use of platelike "whiskers" (platelets) in a ceramic matrix and EP-A-295 228 the use of a mixture of thin whiskers, thick whiskers and/or platelets in a ceramic matrix. It is a purpose of the invention to obtain a ceramic material for chip forming machining of steel, in particular, where the above mentioned weaknesses of the known aluminium oxide based cutting materials have been eliminated. In materials according to the invention there is, thus, a unique combination of strength, toughness, thermal shock resistance and wear resistance, which has not been possible to obtain by earlier known oxide based cutting materials. The primary aim of the present invention is to make oxide based ceramic cutting materials reinforced by whiskers having a low solubility in steel resulting in that the cutting material obtains an improved and more predictable toughness, strength and thermal shock resistance without appreciably deteriorating the wear resistance in cutting of steel, in particular, which has not been possible by earlier known material compositions. The ceramic cutting material according to the present invention comprises an oxide based, preferably aluminium oxide based, matrix with 5-50, preferably 10-40, especially 25-35 % by volume homogeneously dispersed whiskers based upon a solid solution of nitride and oxide of aluminium preferably the cubic aluminium oxynitride spinel (AlON). Said whiskers consist of mono- crystals with a diameter of 0.5-10µm and a length of 2.5-100µm characterised thereof that the length/diameter ratio preferably is 5-10. Alternatively the whiskers may consist of monocrystalline platelets with a thickness of 0.5 - 8µm and a diameter of 10 - 50µm. The grain size of the oxide matrix shall be < 10µm, preferably < 4µm. The oxide matrix shall consist of essentially ceramic oxides or of ceramic oxides mixed with hard carbides and/or nitrides and/or borides and/or binder metal. Preferably, the ceramic matrix shall contain < 20 % by vol ZrO₂. A part of, less than 50 %, the above mentioned whiskers may be replaced by silicon carbide whiskers which have a favourable influence on the thermal shock resistance without notably reducing the wear resistance when machining steel at moderate cutting speeds under the condition that the total amount of SiC whiskers does not exceed 15 % by volume. The cutting material in question is made by wet milling and mixing of oxide based powder and monocrystalline whisker crystals together with suitable sintering aids. After drying the mixture is compacted to desired geometrical form and sintered without pressure to near theoretical density. After the sintering the possible remaining closed porosity can be removed by a hot isostatic pressing. If it is not possible by sintering to obtain a closed porosity the material can be pressure sintered in a suitable graphite tool or after encapsulating be hot isostatically pressed to desired density. The sintering method is depending upon the whisker material and is chosen so that the material reaches a density which exceeds 99 % of the theoretical density. In the preferred embodiment the whisker material consists of aluminiumoxinitride (AlON) and the matrix is aluminium oxide based, which allows pressureless sintering of up to 40 % by volume of whiskers. Use of whisker reinforcement in the aluminium oxide based matrix leads to a significant increase of the fracture strength. The mechanisms which cause said increase can be load transfer between whisker and matrix, crack deflection and whisker pull out. These mechanisms utilise and are dependent upon the crack propagation taking place along a sufficiently weak boundary surface between whisker and matrix. The bonding strength between whisker and matrix is therefore an important parameter which can be influenced by coating of the whisker material with thin layers of a material decreasing the bonding strength in order to further improve the fracture toughness. Alumina whiskers give a significant increase of the fracture toughness but even better properties seem to be obtained if nitrogen is incorporated in the lattice to form solid solutions in the AlN-Al₂O₃ quasibinary system. It is well known that nitrogen additions to Al₂O₃ can produce an aluminiumoxinitride (AlON) of a cubic structure closely related to the gamma-Al₂O₃-structure. The better properties of composites made from aluminiumoxinitride whiskers seem to be related to different bonding properties between whisker and matrix. For machining, however, oxinitride whiskers are to be preferred due to their greater chemical stability which leads to less wear. Example 1 30 % by volume of aluminiumoxinitride and -oxide whiskers resp. were wet-mixed with 70 % by volume of a mixture of 95.5 % Al₂O₃, 4.2 % ZrO₂ and 0.3 % MgO (all by weight). After drying in vacuum the mixture was dry-mixed and pressed to blanks. The blanks were sintered at 1550°C to 99 % of theoretical density. The fracture toughness (K IC ) is measured by means of the so called indentation method. An impression is made with the aid of a pyramid shaped diamond indenter and K IC is calculated from the length of the cracks which are induced from the corners of the indenter. A reference of Al₂O₃ + 4.2 % by weight ZrO₂ + 0.3 % by weight MgO was used at the measurement. The result of the K IC determination is shown in table 1. It is obvious from the table that incorporation of AlON-whiskers gives a significant increase of the fracture toughness. The fracture toughness is a parameter which shows the ability of a material to resist mechanical stresses without catastrophic failure. In the case of chip forming machining it means that higher feeds can be allowed, i.e. the rate of the material removal can be increased for a given cutting speed. For machining of iron based workpieces composites with AlON-whiskers are preferred because they show the best combination of wear and toughness.

Claims: Oxide based ceramic cutting insert for chip forming machining of steel characterised in that said insert besides the oxide based matrix comprises 5-50 % by volume, preferably 10-40 % by volume, of homogeneously dispersed whiskers of a solid solution of nitride and oxide of aluminium preferably of the cubic aluminium oxynitride spinel (AlON). Cutting insert according to the preceding claim characterised in, that the matrix comprises ceramic oxides or ceramic oxides mixed with one or more hard carbides and/or nitrides and/or borides and/or binder metal. Cutting insert according to any of the preceding claims, characterised in, that the matrix is based upon aluminium oxide and < 20 % by volume of ZrO₂. Cutting insert according to any of the preceding claims, characterised in, that up to 50 % of the whiskers is replaced by SiC whiskers, the total amount of SiC whiskers being < 15 % by volume.

Inventors: BRANDT, GUNNAR
Applicants: SANDVIK AKTIEBOLAG
Application year: 1989
Main classification: C04B35
IPC codes: C04B35