PIPE FOR RELINING UNDERGROUND PIPELINES

Abstract: Pipe for relining underground pipelines, which is of the composite type having an annularly rigid corrugated outside wall (10) of polymer material, which is connected to the outside surface of a smooth inside wall (11) which consists of a thermoplastic elastomer so that it can be stretched and compressed. According to the invention there is provided on the inside of the smooth inside wall (11) a thin layer (13) of thermoplastic having a lower frictional coefficient and/or greater wear-resistance than the material of the inside wall.

Description: PIPE FOR RELINING UNDERGROUND PIPELINES The invention relates to a pipe for relining underground pipelines, which is of the composite type with an annularly rigid corrugated outside wall of polymer material, which is attached to the outside surface of a smooth inside wall, which consists of a thermoplastic elastomer so that it can be stretched and compressed. Pipes of this type are described in the European patent application with publication number 0 213 674. When an underground pipeline is to be relined by using pipes of this type the pipe is drawn from ground level through a well or manhole into the pipeline, and due to the fact that the inside wall consists of a thermoplastic elastomer the pipe then can be abruptly angled - at an angle of 90 if necessary - when it passes from the well or the manhole into the pipeline, and the pipe can adjust to existing constrictions and direction changes in the underground pipeline more easily than in case of a rigid inside wall. In order to use such relining pipes having a rigid inside wall it is usually necessary to take up wide manholes which allow the pipe to be drawn from ground level into the underground pipeline via the manhole along a rather flat trajectory. Pipes of the type referred to herein are not without problems, however, in other respects than those relating to the procedure of drawing the pipe into the underground pipeline. In the first place problems arise in the manufacture of the pipe. The pipe is manufactured by coextruding the inside wall and the outside wall, said latter wall at the same time in connection with the extrusion being corrugated by forming and cooling the wall against chains of chilled molds and the smooth inside wall being calibrated and cooled by sliding over a cooling mandrel. The problem involved in the technique of manufacturing the pipe is that the inside wall of a thermoplastic elastomer tends to stick to the cooling mandrel involving the risk of the wall being torn to rags. In the second place there is a problem with respect to the wear resistance of the smooth inside wall of thermoplastic elastomer. This wall must be made substantially thinner than the wall of corre¬ sponding smooth, rigid polyethylene or PVC pipes for waste conduits in order that it can be stretched and compressed as is necessary at abrupt direction changes when the pipe is drawn into the underground pipeline, which means that the wear resistance will be a criti¬ cal factor in this connection. At the same time it can be questioned if a wall of a thermoplastic elastomer can be on a level with a wall of polyethylene or PVC as far as the long term wear resistance is concerned. The present invention provides a possibility to meet these problems, viz. by the relining pipe of the type referred to herein being constructed in the man¬ ner defined in the characterizing clause of claim 1. In order to explain the invention in more detail reference is made to the accompanying drawing which discloses a fragmentary axial cross-sectional view of a relining pipe according to the invention in one em¬ bodiment thereof. The pipe shown in the drawing is of a prior art embodiment as far as it comprises a corrugated outside wall 10 and an inside wall 11 which is smooth on the inside as well as the outside thereof, the inside peaks of the outside wall being connected to the smooth outside of the inside wall at 12. The pipe pre¬ ferably is manufactured by coextruding the outside and the inside walls, the outside wall being corrugated in connection with the extrusion by being formed and cooled against chains of chilled molds. The inside wall is calibrated and cooled in connection with the extrusion by means of a cooled inside mandrel. Suit¬ able materials for the outside wall are polyethylene, polypropylene, and PVC, while suitable materials for the inside wall are e.g. EPDM mixed with polyethylene (synthetic rubber) , thermoplastic defines, e.g. VISTAFLEX (registered trademark) , SANTOPRENE (registered trademark) , and ALCRYN (registered trade¬ mark) , ethylenevinylacetate polymers, e.g. ESCORENE (registered trademark) , and mixtures of styrene, ethylene, and butane, e.g. ELEXAR (registered trade¬ mark) . On the inside surface of the inside pipe 11 a thin layer 13 of thermoplastic, e.g. polyethylene, crosslinked polyethylene or PVC, is provided, the pur¬ pose of which is to form anantifriction layer between the mandrel and the thermoplastic elastomer and to provide improved wear-resistance of the inside pipe. If the inside wall consists of a thermoplastic elas¬ tomer which is compatible with an outside wall of polyethylene or polypropylene, then polyethylene is chosen when priority is given to the reduction of the friction, and crosslinked polyethylene is chosen when priority is given to the wear-resistance. PVC is used in the layer 13 in case the inside wall consists of a thermoplastic elastomer which is compatible with an outside wall of PVC, e.g. ALCRYN (registered trade¬ mark) . The layer 13 can have a thickness of 0.05 to 0.30 mm on an inside wall of a thermoplastic elastomer which has a thickness of about 1 mm in case of a pipe having an outside diameter of about 200 mm. More generally the thickness of the layer 13 should measure 2-30% of the total thickness of the inside pipe 11 and the layer 13. Crosslinked polyethylene preferably is of the silan crosslinked type which can crosslink automatically under the influence of humidity after the manufacturing step proper. A further advantage of the pipe described is that the layer 13 can be used for providing a colour code which makes possible to distinguish a normal double- wall pipe (wherein the outside wall as well as the in¬ side wall is rigid) from a double-wall pipe having an inside wall of thermoplastic elastomer. It is import¬ ant to be able to distinguish easily between these two types of pipes in handling material (handling scrap) in the factory.

Claims: CLAIMS 1. Pipe for relining underground pipelines, which is of the composite type with an annular rigid corrugated outside wall (10) of polymer material, which is connected to the outside surface of a smooth inside wall (11) which consists of a thermoplastic elastomer so that it can be stretched and compressed, c h a r a c t e r i z e d in that there is provided on the inside of the smooth inside wall (11) a thin layer (13) of thermoplastic having lower frictional coefficient and/or greater wear-resistance than the material of the inside wall. 2. Pipe as in claim 1 wherein the layer (13) con¬ sists of polyethylene. 3. Pipe as in claim 1 wherein the layer (13) consists of crosslinked polyethylene. 4. Pipe as in claim 3 wherein the layer of crosslinked polyethylene is of the silan crosslinked type. 5. Pipe as in claim 1 wherein the layer (13) consists of PVC. 6. Pipe as in any of claims 1 to 3 wherein the thickness of the layer (13) is of the order of 2 to 30% of the total thickness of the inside pipe (11) and the layer (13) .

Inventors: AAGREN LENNART, HOELSOE EINO, AAGREN, LENNART, HOELSOE, EINO
Applicants: UPONOR NV, UPONOR N.V.
Application year: 1989
Main classification: F16L55
IPC codes: B32B1, F16L1, F16L11, F16L55