A method for manufacturing a field effect transistor

Abstract: In a method for manufacturing a field effect transistor, an inorganic material film is formed such that the film thickness of a resist pattern as a dummy gate or a refractory gate electrode in a gate region on a semiconductor substrate which faces a planned drain region is larger than the film thickness of a side wall facing a planned source region, and a impurities are doped into the semiconductor substrate at a high concentration using the resist pattern or the refractory gate electrode and the inorganic material film on the side walls thereof as the mask. As a result, the FET manufactured by the above process has a interval between the drain region and the gate electrode is larger than a interval between the source region and the gate electrode.

Description: The present invention relates to a method for manufacturing a field effect transistor (FET), and more particularly to a method for manufacturing a Schottky gate field effect transistor (MESFET). (Related Background Art) In a MESFET, it has been proposed to make an interval between a drain n⁺ layer and a gate electrode larger than an interval between a source n⁺ layer and the gate electrode so that a drain break-down voltage is raised while a serial resistance is kept low to attain a low drain conductance. As a manufacturing method for such an asymmetric structure MESFET, a method which uses a multi-layer dummy gate has been known. JP-A-61-194781 shows one manufacturing method therefor, in which a bi-layer dummy gate is formed, a metal film such as aluminum (Al) is deposited on the surface of the dummy gate except a side wall facing the drain and a vicinity thereof, the lower layer of the dummy gate facing the drain is etched using the metal film as a mask to form an asymmetric T-shaped dummy gate structure, and the asymmetric structure MESFET is manufactured by using the asymmetric dummy gate. In the related art, the dummy gate must be of multilayer structure and it must be asymmetric T-shaped dummy gate structure. In order to form the asymmetric T-shaped dummy gate, a complex process including partial vapor deposition of the Al metal film, etching of only one side of the side walls of the lower layer of the dummy gate, and removal of the Al metal film is required. EP-A-O 224 614 discloses a process of fabricating a fully self-aligned field effect transistor, in which a dummy gate is also used to define the topology of the transistor while the dummy gate is replaced by a Schottky gate after ohmic contact metal deposition. Furthermore, EP-A-O 152 615 discloses a method for manufacturing a field effect transistor, in which a gate electrode consisting of first and second metal portions is formed in a gate region. The gate electrode is covered by an insulation layer which subsequently is subjected to an anisotropical etching process until only a portion of the insulation layer is left along the side surfaces of the first and second metal layers. Then, the gate electrode and the insulative portion are covered by a further insulation layer which is subjected to an anisotropical etching process so that insulative portions are formed on both sides of the gate electrode and the insulative portion. Thereafter, impurities are doped into the semiconductor substrate using the gate electrode and the insulative portions as a mask to form source and drain regions in which source and drain electrodes are provided. That means, the above mentioned method provides different insulation layer thicknesses on the sidewalls of the gate electrode by two anisotropical etching processes. It is the main object of the present invention to provide a method for manufacturing the field effect transistor which enables a FET having an interval between a drain region and a gate electrode larger than an interval between a source region and the gate electrode to be manufactured at a high yield. This object is solved by the features of claims 1 and 3, respectively. Particular embodiments of the invention are set out in the dependent claims 2 and 4. In principle, the present invention provides a method for manufacturing a field effect transistor comprising steps of forming a relatively thin inorganic material film on a side wall of a dummy gate or refractory metal gate electrode facing a source, forming a relatively thick inorganic material film on the other side wall facing a drain, and implanting impurity ions at the high concentration using the dummy gate or refractory metal gate electrode and the inorganic material film on the sides thereof as a mask. The present invention will now be described by way of example with reference to the accompanying drawings, in which: Figs. 1A-1H show a process sectional view of one embodiment of the present invention, Fig. 2 shows a sectional view of an ECR plasma CVD apparatus used in the embodiment, and Figs. 3A-3E show a process sectional view of another embodiment of the present invention. Figs. 1A-1H show process sectional views in accordance with one embodiment of the present invention which manufacture an asymmetric MESFET having a LDD (lightly doped drain) structure. The LDD structure serves to relieve a high electric field created in a drain region by miniturization of devices. It refers to a structure in which impurity regions of a relatively low concentration are formed in highly doped source and drain regions (contact regions) facing the gate. A gallium arsenide (GaAs) substrate is first prepared as a semiconductor substrate 1, and n-type and p-type impurity ions are sequentially doped into areas where the FET is to be formed, through a photo-resist mask to form an n-type active layer 2 and a p-type buried layer 8 (see Fig. 1A) Then, resist is applied by a known spin coating method and a resist pattern 9 shown in Fig. 1B is formed by a known photolithography technique. The portion of the resist pattern 9 which is in the gate region is replaced by the gate electrode in a later step, and it acts as a dummy gate. A silicon nitride (SiN x ) film 10 is formed by using an electron cyclotron resonance plasma chemical vapor deposition method (ECR plasma CVD method). Fig. 2 shows a basic structure of an ECR plasma CVD apparatus for depositing the SiN x film 10 in the present embodiment. The ECR plasma CVD apparatus comprises a plasma chamber 41 and a deposition chamber 42. A magnetic coil 43 is disposed around the plasma chamber 41 and a microwave rectangular wave guide 44 is disposed above the plasma chamber 41 with a microwave transparent isolation plate being interposed therebetween. A sample table 45 on which the semiconductor substrate 1 is mounted is arranged in the deposition chamber 42 at an angle of 45° relative to a flow direction 46 of plasma flow. The sample table 45 is rotatable around an axis 50 which extends centrally and which is normal to the surface of the sample table 45. Numeral 47 denotes a coolant pipe, numeral 48 denotes a plasma generation gas inlet pipe, and numeral 49 denotes a reaction gas inlet pipe. In this ECR plasma CVD apparatus, N₂, NH₃, O₂ or Ar gas or mixture thereof is supplied through the plasma generation gas inlet pipe 48 into the plasma chamber 41 in which the ECR condition has been set by the microwave and the magnetic field, and the plasmanized gas is guided by the diverging magnetic field into the deposition chamber 42. On the other hand, insulative film forming gas such as SiH₄, Si₂H₆ or Si₃H₈ is supplied into the deposition chamber 42 through the reaction gas inlet piper 49 and it is excited and activated by the plasma and reacts so that reaction product is deposited on the substrate. A SiN x film is presently formed as the inorganic material film (insulator film) formed by the ECR plasma CVD method, and silicon oxide (SiO₂) or silicon nitride oxide (SiO x N y ) film may also be formed. The ECR plasma CVD method is disclosed in Japanese Journal of Applied Physics Letter, Vol. 22, No. 4, ppL210-L212, 1983. In the present embodiment, the silicon nitride is deposited while the sample table 45 of the ECR plasma CVD apparatus is fixed at a predetermined position. Since the plasma flow 46 of the ECR plasma CVD has a high directivity, the silicon nitride is deposited to the surface of the semiconductor substrate 1 from the oblique above thereof at an angle of 45° and the SiN x film 10 is formed except on one side wall of the resist pattern 9 and a shade area thereof (see Fig. 1B). Thereafter, the silicon nitride is deposited while the sample table 45 is rotated around the axis 50 so that the deposition is done uniformly over the entire surface of the semiconductor substrate 1. Thus, the silicon nitride is deposited on the deposition of the silicon nitride made in the previous stage and the deposition is also made on the other side of the resist pattern 9 and the shade area thereof to which no deposition of the silicon nitride was made in the previous stage. As a result, the silicon nitride (SiN x ) film 10 as shown in Fig. 1C, that is, the SiN x film 10 having different film thicknesses at the right and left side walls of the dummy gate is formed. In order to attain the LDD structure, it is necessary to leave the SiN x film 10 on the sides of the resist pattern 9 as spacers 10 a and 10 b . To this end, a certain degree of fineness is required for the SiN x film 10. This is well satisfied by using the ECR plasma CVD method. Since the ECR plasma CVD method allows the process at a low temperature, the resist pattern is not modified and the lifting-off in a later step is facilitated. The SiN x film 10 formed as shown in Fig. 1C is etched from the above thereof by a reactive ion etching (RIE) method. When the SiN x film 10 on the top of the semiconductor substrate 1 and on the top of the resist pattern 9 is removed, the SiN x film is left on the sides of the gate region resist pattern 9 as the spacers 10 a and 10 b . The spacer 10 a facing the source is thinner than the spacer 10 b facing the drain. Then, high concentration impurities are doped as shown by arrows in Fig. 1D to form n⁺⁺ regions which serve as the source region 6 and the drain region 7. The n⁺⁺ region is not formed in an area where the resist pattern 9 or spacer 10a or 10b exists. Then, the SiN x films of the spacers 10a and 10b are removed by buffered hydrofluoric acid, and n-type impurities are doped as shown by arrows in Fig. 1E. As a result, n⁺ impurity regions 4 having a lower concentration than the n⁺⁺ regions are formed at end areas of the source region 6 and the drain region 7 facing the gate region. In this manner, the LDD structure is attained. This step of forming n⁺ impurity regions 4 may be eliminated for a manufacture of a MESFET having no LDD structure. Then, SiN x films 11 are formed by the ECR plasma CVD method, as shown in Fig. 1F. Because the plasma has a high directivity, the SiN x film 11 is not formed on the sides of the resist pattern 9 when the semiconductor substrate 1 is kept perpendicular to the ECR plasma. Accordingly, a structure shown in Fig. 1G is easily attained by the lift-off process by acetone. The SiN x reversal pattern which is exact reversal to the substitutional resist pattern 9 is obtained. By annealing it in an AsH₃ atmosphere at approximately 800°C, the impurity doped areas are activated. Openings are then formed in the SiN x films 11 and ohmic electrodes 12 and 13 are formed. A Schottky metal is deposited on the entire surface including the gate region, and the gate electrode 3 is formed by the lift-off process. Thus, an FET having the gate electrode 3 formed by the self-alignment process is formed (see Fig. 1H). In this FET, since the spacer 10b is thicker than the spacer 10a, the interval between the drain region 7 and the gate electrode 3 is larger than the interval between the source region 6 and the gate electrode 3 depending on the difference between the film thicknesses. As a result, a drain breakdown voltage is improved over an FET which has the spacers 10a and 10b of equal thickness. In the present embodiment, since the gate electrode 3 is formed after the annealing, the Schottky metal may be Ti/Pt/Au or La B₆ instead of a refractory metal. Since the gate electrode 3 is not subjected to a high temperature process, the Schottky characteristic is not deteriorated. Specific examples of the method for manufacturing the field effect transistor of the present invention are now explained, although the present invention is not limited to those examples. EXAMPLES A field effect transistor was formed on a substrate in accordance with the process of the present invention shown in Figs. 1A-1H, in the manner described below. First, a GaAs substrate was prepared as the semiconductor substrate 1 , and a photo-resist (Az-1400) was applied over the entire surface thereof. After a predetermined pattern was exposed, it was developed to form the resist pattern. Then, ²⁹Si⁺ was lightly doped at an acceleration voltage of 30-70 kilovolt (KV) using the resist formed on the substrate as a mask, to form the n-type active layer 2. Also,Be⁺ was doped at an acceleration voltage of 50-100KV using the resist as a mask, to form the p-type buried layer 8. Then, the resist pattern was removed, and a photo-resist film (AZ-1400) was again applied over the entire surface of the substrate. Another predetermined pattern was exposed thereto and it was developed to form the resist pattern (substitution pattern, the dummy gate) as shown in Fig. 1B. Then, the Si₃ N₄ film 10 as shown in Fig. 1B was formed to the thickness of approximately 1000 Å by using gas mixture of SiH₄, NH₃ and N₂ while the rotation of the sample table 45 of the ECR plasma CVD apparatus shown in Fig. 2 was stopped at an appropriate position. Then, the ECR plasma CVD was continued while the sample table 45 was rotated to form the Si₃ N₄ film 10 as shown in Fig. 1C. Through the two-stage film formation process, the film thickness of the side wall of the dummy gate facing the source was approximately 1000 Å, and the film thickness of the side wall facing the drain was approximately 2000 Å. Then, the Si₃ N₄ film in the flat area was removed by the RIE method to leave the Si₃ N₄ films only on the side walls of the resist pattern as the spacers 10a and 10b, as shown in Fig. 1D. Under this condition, ²⁸Si⁺ was implanted at an acceleration voltage of 80-200 KV to form the n⁺⁺ source region 6 and drain region 7 having a doping concentration of approximately 3x10¹³/cm², as shown in Fig. 1D. Then, the spacers 10a and 10b on the side walls of the resist pattern 9 were removed as shown in Fig. 1E by slight etching by using buffered hydrofluoric acid. Under this condition, ²⁸Si⁺ was implanted at an acceleration voltage of approximately 100KV to form the n⁺ region 4 of in the order of 10¹²/cm² in order to attain the LDD structure. Then, the Si₃ N₄ film 11 was formed by the ECR plasma CVD method perpendicularly to the substrate (Fig. 1F), and the Si₃ N₄ film 11 on the resist pattern was removed by the lift-off process in which the resist pattern was removed by acetone, to form the Si₃ N₄ film (reversal pattern) having the openings as shown in Fig. 1G. The substrate was then annealed for 30 minutes in the AsH₃ atmosphere at approximately 800°C. The annealing was done in the AsH₃ atmosphere in order to prevent As from evaporating from the GaAs substrate. Where the anneal protection film is formed over the entire surface of the substrate, the annealing may be done in an inert atmosphere such as N₂. A resist pattern having openings which align to the openings in the Si₃ N₄ film 11 and which are larger than the openings of the Si₃ N₄ film 11 was formed on the substrate. The source electrode 12 and the drain electrode 13 were formed in the source region and the drain region by a known method. Then, a Ti/Pt/Au electrode material was vapor-deposited on the entire surface thereof, and the resist pattern was removed and the self-alignment gate electrode 3 was formed by the lift-off process to form the MESFET shown in Fig. 1H. In the present example, the low concentration region 4 for the LDD structure was formed after the source/drain regions 6 and 7 had been formed. Alternatively, n-type impurities may be ion-implanted using the dummy gate as the mask immediately after the formation of the dummy gate to form the low concentration impurity region 4. Figs. 3A-3E shows a process sectional view of another embodiment of the present invention. The present embodiment is similar to the embodiment of Figs. 1A-1H in that it manufactures a MESFET of the LDD structure but it differs in that it uses a refractory metal for the gate electrode. A GaAs substrate is prepared as the semiconductor substrate 1, and n-type and p-type impurity ions are sequentially implanted through the photo-resist mask to form the n-type active layer 2 and the p-type buried layer 8, as they are done in the embodiment of Figs. 1A-1H (see Fig. 3A). Then, as a refractory metal tungsten silicide (WSi) is sputtered to the surface of the semiconductor substrate 1, and a gate electrode 30 is formed on the active layer 2 as shown in Fig. 3A by CF₄ gas plasma etching. Then, n-type impurities are implanted using the gate electrode 30 as a mask to form the n⁺ low concentration impurity region 35 for the LDD structure. Then, a silicon nitride (SiN x ) film 31 which is an inorganic material film is formed by the ECR plasma CVD method. The deposition of the silicon nitride in this step is done first while the sample table 45 is fixed at a predetermined position and then it is done while the sample table 45 is rotated, as it is in the embodiment of Fig. 1. As a result, the silicon nitride film 31 is first formed except on the side wall of the gate electrode 30 facing the source and the substrate surface in the vicinity thereof as shown in Fig. 3B, and then it is deposited on the side wall of the gate electrode 30 facing the source and the substrate surface in the vicinity thereof. The film thickness of the side wall of the gate electrode facing the drain is thicker than the film thickness of the side wall facing the source. The silicon nitride film 31 thus formed is etched from the above thereof by the RIE method so that the spacers 31a and 31b are left on the both side walls of the gate electrode 30. Then, a photo-resist is applied and it is patterned to form a resist pattern 32. High concentration impurities are implanted as shown by arrows in Fig. 3D using the resist pattern 32, the gate electrode 30 and the spacers 31a and 31b as a mask to form the n⁺⁺ regions which serve as the source region 6 and the drain region 7. The n⁺⁺ region is not formed in the area where the resist pattern 32, the gate electrode 30 or the spacer 31a or 31b exists. Since the film thickness of the spacer 31b is larger than the film thickness of the spacer 31a, the interval between the drain region 7 and the gate electrode 30 is larger than the interval between the source region 6 and the gate electrode 30. The resist pattern 32 is then removed by acetone and the substrate is annealed in the AsH₃ atmosphere at approximately 800°C so that the impurity doped areas are activated. Then, ohmic electrodes are formed in the source region 6 and the drain region 7 to form the source electrode 33 and the drain electrode 34 of the MESFET shown in Fig. 3E. In this MESFET, since the interval between the drain region 7 and the gate electrode 30 is larger than the interval between the source region 6 and the gate electrode 30, a drain breakdown voltage is high and a drain conductance is low. The both embodiments described herein relate to the manufacture of the MESFET of the LDD structure, but they may be applied to the manufacture of the MESFET having no LDD structure by eliminating the step of forming the low concentration impurity region 4 or 35.

Claims: A method for manufacturing a field effect transistor, said method comprising the steps of: (A) forming a resist pattern (9) corresponding to a gate region on a semiconductor substrate (1); (B) depositing an inorganic material on a surface of the substrate (1) by directing the inorganic material from above the substrate (1) onto the substrate surface in a direction oblique to the substrate surface by the use of an electron cyclotron resonance plasma CVD method, said depositing step including a first step of depositing the inorganic material as the substrate (1) is held in a fixed position, such that the inorganic material is deposited on the side wall of the resist pattern (9) facing the planned drain region (7), and a second step of further depositing the inorganic material while the substrate (1) is rotated about an axis normal to the surface thereof; (C) etching to remove the inorganic material from a predetermined region to form inorganic material films (10a, 10b) so that the film thickness of the inorganic material on the side wall of the resist pattern (9) facing the planned drain region (7) is thicker than the film thickness of the inorganic film on the side wall of the resist pattern (9) facing the planned source region (6); (D) doping the semiconductor substrate (1) with impurities to a high impurity concentration while using the resist pattern (9) and the inorganic material films (10, 10a, 10b) on the side walls thereof as a mask to provide a source region (6) and a drain region (7); (E) removing the remaining inorganic material films (10, 10a, 10b) from the substrate (1); (F) providing a reversal pattern on the semiconductor substrate (1) by forming an insulative film (11) on the substrate (1) and thereafter removing the resist pattern (9); (G) forming a self-alignment gate electrode (3) on the semiconductor substrate (1) in the gate region by using the reversal pattern as a mask; (H) forming a drain electrode (13) in the drain region (7); and (I) forming a source electrode (12) in the source region (6). A method for manufacturing a field effect transistor according to claim 1, wherein after step (A) or step (D), said method comprises a step of doping the semiconductor substrate (1) using the resist pattern (9) as a mask to form an impurity region (4) having a lower concentration than the source/drain regions (6, 7). A method for manufacturing a field effect transistor, said method comprising the steps of: (A) forming a gate electrode (30) made of a refractory metal in a gate region of a semiconductor substrate (1); (B) depositing an inorganic material on a surface of the substrate (1) by directing the inorganic material from above the substrate (1) onto the substrate surface in a direction oblique to the substrate surface by the use of an electron cyclotron resonance plasma CVD method, said depositing step including a first step of depositing the inorganic material as the substrate (1) is held in a fixed position such that the inorganic material is deposited on the side wall of the gate electrode (30) facing the planned drain region (7), and a second step of further depositing the inorganic material while the substrate (1) is rotated about an axis normal to the surface thereof; (C) etching deposited inorganic material to remove the inorganic material from a predetermined region and thereby form inorganic material films (31a, 31b) so that the film thickness of the inorganic material on the side wall of the gate electrode (30) facing the planned drain region (7) is thicker than the film thickness of the inorganic material on the side wall of the gate electrode (30) facing the planned source region (6); (D) doping the semiconductor substrate with impurities to a high impurity concentration while using the gate electrode (30) and the inorganic material films (31a, 31b) on the side walls thereof as a mask to provide a source region (6) and a drain region (7); (E) removing the remaining inorganic material films (31a, 31b) from the substrate (1); (F) forming a drain electrode (34) in the drain region (7), and (G) forming a source electrode (33) in the source region (6). A method for manufacturing a field effect transistor according to claim 3, wherein after step (A), said method comprises a step of doping the semiconductor substrate while using the gate electrode (30) as a mask to form an impurity region (35) having a lower concentration than the source/drain regions (6, 7).

Inventors: SHIKATA SIN-ICHI C O YOKOHAMA, SHIKATA, SIN-ICHI C/O YOKOHAMA WORKS OF
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1989
Main classification: H01L21
IPC codes: H01L21, H01L29