A device for transferring and fixing electrophotographic toner powder containing thermoplastic resin on to a receiving material

Abstract: A device for fixing or transferring and fixing a powder containing thermoplastic resin on to a receiving material under the influence of pressure and heat, in which device the fixing member in pressure con­ tact with the powder during the fixing of the powder image is provided with an outer covering consisting mainly of silicone rubber. The silicone rubber is the reaction product of polyorganosiloxane bearing Si-H groups and polyorganosiloxane which bears Si-(CH=CH₂) groups and which on average contains between 40 and 1000 monomeric units per polymer chain, bears 1.5-4 terminal vinyl groups, bears at most one non-terminal vinyl group per 80 monomeric units and contains at most 2% Si atoms in the form of SiO3/2 or SiO4/2 units. The thickness of the silicone rubber covering is preferably less than 500 micrometers.

Description: The invention relates to a device for transferring and fixing an image formed with an electrophotographic toner powder containing a thermoplastic resin on to a receiving material under the influence of pressure and heat, comprising cooperating fixing members which form a pressure zone in which the powder image formed by pressure transfer on the surface of one of said fixing members, is pressed against the receiving material, heating means for heating the powder image bearing fixing member, at least the image bearing fixing member being provided with an outer covering of silicone rubber which has an average thickness of 500 micrometres maximum and consists mainly of a specific silicone rubber. In many modern reproduction and printing techniques, e.g. electrophotography, electrostatography and magnetography, a powder image is formed on a re-usable image registration medium, by means of toner powder containing thermoplastic resin, and this powder image is then transferred and fixed on a receiving material, such as ordinary paper. The transfer of the powder image to the receiving material can be effected by bringing the powder image bearing image registration medium into pressure contact with a fixing member, the surface of which consists of silicone rubber having a low affinity for the softened powder. The powder image transferred on the fixing member as a result of the pressure exerted is then transferred to the receiving material, again by pressure, in a pressure zone where the image bearing fixing member cooperates with a second fixing member. Before and/or during passage through the pressure zone, the powder being softened by heating, so that it becomes so viscous that it forms a cohesive layer in response to the pressure exerted, such layer penetrating at least partially into the receiving material. After cooling, the image is permanently bonded to the image receiving material. Heating of the powder image is effected by heating the fixing member, which functions as a temporary receiving support for the powder image, and possibly the receiving material itself. Image transfer processes of this kind are described, inter alia, in US Patents 3 554 836, 3 893 761 and UK Patent 1 279 687. RTV or HTV silicone rubbers are used as outer covering for fixing members. They are obtained by cross-linking into an elastomeric composition polyorganosiloxane mixtures which bear reactive groups, under the influence of a suitable catalyst, at room temperature or at elevated temperature. The silicone rubber covering may also contain additives to improve its properties such as mechanical strength, thermal conductivity and antistatic behaviour. Typical additives are fillers such as silica, titanium dioxide, calcium carbonate, iron oxide, teflon and carbon. The amount of additive in the covering may be 60% by weight or even more and is often between 40 and 50% by weight. Typical rubber compositions for forming a covering for fixing members which can be used as a temporary support for a powder image are described in UK patent No. 1 279 687 and Example 1 of European patent application No. 146 980. British Patent Application No. 2 081 646 describes a device with an intermediate transfer member which has a thin surface layer composed of a silicone rubber obtained by reacting a polyorganosiloxane having Si-H groups with polyorganosiloxane having vinyl groups, which predominantly are non-terminal vinyl groups and having in its molecular structure at most 2-11 monomeric units. The Si-H groups are present in excess with respect to the Si-vinyl groups. European Patent Application No. 62 408 describes a heat fixing roller having an outer layer of silicone rubber derived from polyorganosiloxane bearing vinyl groups and polyorganosiloxane bearing Si-H groups, wherein the Si-H groups are in excess with respect to the vinyl groups, and which layer contains siliceous filler and optionally a triorganosiloxy endblocked polydiorganosiloxane. In addition to good mechanical strength required for long life, the rubber coverings present on fixing members should have a wide working range, i.e. there should be a wide temperature range within which the softened toner powder does not stick to the silicone rubber covering on leaving the pressure zone in which the powder image is fixed on the receiving material. This working range must also be situated at a temperature level at which sufficient fixing of the toner powder on the receiving material is obtained in the pressure zone. The working range of the silicone rubber coverings gradually reduces during operation of the fixing devices, the top limit of the working range in particular falling. A situation is gradually reached in which there is no longer any practical working range and the fixing member has to be replaced. The development of ever-faster copying machines and the continual search for components having a longer life mean that there is a continuous demand for improved covering materials for fixing members. Although it has been possible considerably to lengthen the life of the silicone rubber covering by continuously providing the covering with a thin layer of silicone oil at the fixing device in use, the disadvantage of this solution is that silicone oil is transferred to the receiving material so that its writability deteriorates. In image-forming processes in which a powder image is transferred by pressure from an image registration element to the silicone rubber covering of a fixing member, the application of silicone oil cannot be carried out because then the image registration element would be soiled by the oil and would become unsuitable for further use. According to the invention, a device for transferring and fixing an electrophotographic toner powder according to claim 1 is provided. The fixing members of the device according to the invention provided with a silicone rubber covering are used in image-forming processes in which a powder image is transferred to the fixing member by pressure and is then transferred to and fixed on a receiving material under pressure and heat. The fixing members according to the invention are distinguished from the prior art fixing members in that the top limit of the working range is at a significantly higher temperature and remains substantially constant for a long time (expressed as the number of copies). Thus a longer life is obtained for the fixing members. The silicone rubber used according to the invention is an addition-hardening RTV rubber derived from polyorganosiloxane bearing Si-(CH=CH 2 ) groups (hereinafter referred to as the V-component), and having the above-defined characteristics. V-components not satisfying the demands by themselves, can still be used by mixing them with another V-component, in such a manner that the mixture of V-components does satisfy upon the demands as defined before for the average. Very suitable according to the invention are V-components containing no SiO3/2 or SiO4/2 groups and satisfying the above general formula, where R denotes an alkyl, phenyl, or trifluoroalkyl group, and X is an integer between between 250 and 350. Polyorganosilixanes according to the above general formula are linear products which can be prepared easily and reproducibly. The component bearing reactive Si-H groups (hereinafter referred to as the H-component) is selected from the H-components known for the RTV rubber preparation. Preferably, an H-component is used which contains between 6000 and 11000 m.mol/kg reactive hydrogen groups. Linear H-components, more particularly those in accordance with the following general formula, are very attractive because they can be obtained easily and reproducibly. In this formula, R denotes the organic radical conventional in polyorganosiloxanes, as described hereinbefore, more particularly a methyl group, and the total m + n is between 5 and 40 while the ratio m:n is between 1.5 - 2.5 : 1. The silicone rubber covering is obtained by mixing the V-component with the H-component in the presence of a suitable reaction catalyst, such as a platinum catalyst known for this purpose, and applying the homogeneous mixture in the required layer thickness to a suitable support or substrate. The ratio between the in and H components is so selected that there is an excess of reactive Si-H groups with respect to Si-(CH=CH 2 )-groups. Upon using the fixing member in image forming proccesses in which the fixing member itself acts as a temporary receiving support for a powder image, the silicone rubber outer covering is preferably formed from a mixture of V and H components in which the Si-H groups are present in an excess of 40 to 60%. In other circumstances the excess of Si-H groups may even amount to 400%. In the fixing members according to the invention, the silicone rubber covering may consist completely of the silicone rubber described hereinbefore, but it can also contain the additives known for such coverings, e.g. fillers, silicone resins and antistatic substances, the total of such additives however being at most 20% by weight and preferably not more than 10% by weight. Also, the covering liquid from which the layer is formed may contain a reaction inhibitor in order to bring to the required level the time during which the liquid can be processed. According to the invention, the thickness of the silicone rubber covering on the fixing members is preferably between 10 and 250 micrometers. The silicone rubber covering is preferably applied on a rubber substrate which may also consists of silicone rubber and may have a thickness ranging from a few hundred micrometers to some millimeters. The choice of the rubber composition for the substrate is not critical. Of course a rubber composition should be selected in which the top layer adheres rigidly and which is also strong enough to withstand the pressure applied. Suitable substrates are, for example, silicone rubbers as described in the patents referred to hereinbefore. The silicone rubbers used according to the invention as outer covering for fixing members acting as a temporary receiving support for a powder image may have a hardness of between 20 and 30° Shore A measured with a commercial Shore Durometer according to DIN 53505. They therefore are much softer than the silicone rubbers previously used in practice for this purpose and which have a hardness of between 40 and 55° Shore A. Despite the smaller hardness, the fixing members according to the invention - provided that the surface layer is not too thick (< 500 micrometers) - have a good mechanical strength, comparable to that of the fixing members used heretofore. The invention will now be explained in detail with reference to some examples. Example 1 A fabric belt woven from polyester yarn was provided with an approximately 500 micrometer thick layer of silicone rubber of type RTV 200/201 made by Messrs Possehl, West Germany. An approximately 70 micrometer thick silicone rubber layer was applied over this rubber layer by coating with a liquid of the following composition: 100 g of the V-component described hereinafter 1.9 g of the H-component described hereinafter 5 ppm of a conventional platinum catalyst 40 ppm of 1-ethynyl-1-cyclohexanol (inhibitor) The resulting layer was hardened by holding the belt at a temperature of about 120°C for about 20 hours. The resulting fixing member was used in a copying machine of the Océ 1950 type, in which a powder image was formed on a photoconductive image registration element, the powder image was transferred to the rubber surface of the heated fixing member by pressure, and the softened image was finally transferred to a sheet of paper pressed against the fixing member in a pressure zone. The working range of the fixing member was 103-142°C. After 300 000 copies (A4 size) the working range was still unchanged. Using a fixing member with a top layer as described in Example 8 of UK patent 1 279 687, the working range was 101-128°C, while after 100 000 copies that working range had dropped to 101-112°C. Preparation of H-component A mixture of: was cooled to a temperature of about 0°C with continuous agitation. While the mixture temperature was kept below 20°C 64 g of concentrated sulphuric acid were added to the mixture dropwise. After all the sulphuric acid had been added, the reaction mixture was agitated for another hour and a half at a temperature between 10°C and 20°C and then poured into a mixture of 2000 ml of water and 2000 ml of methylene chloride. The methylene chloride phase was separated and washed with water until the washing water was neutral. After being dried over magnesium sulphate for about 15 hours, the methylene chloride phase was filtered and subjected to vacuum distillation, the undesired fractions distilling over at 70° to 100°C and 14 mm mercury. The residue was an H-component having the average formula: [(CH 3 ) 3 SiO1/2]-[(CH 3 ) 2 SiO2/2] 9.5 -[H(CH 3 )SiO2/2] 19 -[(CH 3 ) 3 SiO1/2] The amount of reactive Si-H groups in the resulting product was 9500 m.mol/kg. Preparation of V-component A mixture of: 532 g of octamethyl cyclotetrasiloxane and 5.1 g of divinyl tetramethyl-disiloxane was heated to ± 85°C with agitation, and then 0.1 g of tetramethyl ammonium hydroxide was added. The reaction mixture was agitated at ± 85°C until there was no further increase in viscosity. This situation was obtained after about 1½ hours. The reaction mixture was then held at 150°C for one hour with agitation and then heated to 170°C. It was then distilled in vacuo until all the volatile constituents had been eliminated from the reaction mixture. The residue was then filtered. The resulting V-component had the average formula: [(CH 3 ) 2 (CH=CH 2 )SiO1/2]-[(CH 3 ) 2 SiO2/2] 180 -[(CH 3 ) 2 (CH=CH 2 )SiO1/2] The quantity of Si-(CH=CH 2 ) groups in the product was 120 m.mol/kg. Example 2 A fixing member was made in the manner described in Example 1, the silicone rubber outer covering being formed by means of a liquid of the following composition: 100 g of V-component in accordance with Example 1 1.6 g of H-component of the formula [SiO4/2] 10 -[SiO1/2(CH 3 ) 2 H] 22 5 ppm of platinum catalyst 40 ppm of 1-ethynyl-1-cyclohexanol 5 g of carbon The outer covering had a thickness of 120 micrometers. The working range of the fixing member in an Océ 1950 copying machine was 102 to 135°C. After 250 000 copies (A4 size) the working range was 103 - 134°C. The H-component used was prepared by adding 36.3 ml concentrated hydrochloric acid dropwise at a temperature of between 5 and 30°C to a solution of 51.3 g of tetraethoxy-silane and 50 g of dimethyl chlorohydrosilane in 250 ml of methylene chloride. The reaction mixture was then agitated for 3 hours at the same temperature and then poured in water. The remaining processing was as described in Example 1. The H-component contained 10400 m.mol/kg reactive Si-H groups. Example 3 Two fixing members were made in accordance with Example 1, the following being used respectively in the composition for forming the silicone rubber outer covering: 1.63 g of H-component of the formula [(CH 3 ) 3 SiO1/2]-[(CH 3 )HSiO2/2] 25 -[(CH 3 ] 2 SiO2/2] 10 -[(CH 3 ) 3 SiO1/2], and 2.52 g of H-component of the formula [(CH 3 ) 3 SiO1/2]-[(CH 3 )HSiO2/2] 4.5 -[(CH 3 ) 2 SiO2/2] 3 -[(CH 3 ) 3 SiO1/2]. In an Océ 1950 copying machine both fixing members had a substantially identical working range which remained substantially constant for 300 000 copies at 102 to 141°C. Both H-components were prepared in the manner described in Example 1, the first H-component being based on 871.5 g of tetramethyl tetrahydro-cyclotetrasiloxane, 444.6 g of octamethyl cyclotetrasiloxane, 81.1 g of hexamethyl disiloxane and 65.1 g of concentrated sulphuric acid. This H-component contained 10400 m.mol/kg reactive Si-H groups. For the preparation of the second H-component the same starting products were used, but now in the following quantities respectively: 510.3 g, 371.1 g, 486.6 g and 63.6 g. This H-component contained 6900 m.mol/kg reactive Si-H groups. Example 4 In a copying machine of the Océ 1950 type, the fixing member receiving the powder image from the photoconductive image registration element, was made as described in Example 1. The second fixing member, pressing against the rearside of the image receiving material in the pressure zone where the powder image is transferred to and fixed on to the image receiving material, was constructed as a belt, of which the support and the first rubber layer were composed as described in Example 1. The silicone rubber outer covering of this belt had a thickness of 150 micrometers and was made by means of the following composition: In the copying machine 200 000 copies were made, about half of which consisted of double sided copies. At the end of the test both fixing members still had a wide working range.

Claims: A device for transferring and fixing an image formed with an electrophotographic toner powder containing a thermoplastic resin, on to a receiving material under the influence of pressure and heat, comprising co-operating fixing members which form a pressure zone in which the powder image formed by pressure transfer on the surface of one of said fixing members, is pressed against the receiving material, heating means for heating the image bearing fixing members, at least the powder image bearing fixing member being provided with an outer covering of silicone rubber which has an average thickness of 500 micrometres maximum, and said covering contains at least 80% by weight of a silicone rubber obtained by reaction of polyorganosiloxane bearing Si-H groups with polyorganosiloxane which bears Si-(CH=CH 2 ) groups, said Si-H groups being in excess with respect to said Si-(CH=CH 2 ) groups, characterised in that said polyorganosiloxane bearing Si-(CH=CH 2 ) groups on average is of the general formula wherein R denotes an alkyl, phenyl or trifluoralkyl group, and X is an integer between 100 and 450 bears 1.5 - 4 terminal vinyl groups, bears at most one non-terminal vinyl group per 80 monomeric units and contains at most 2% Si atoms in the form of SiO 3/2 or SiO 4/2 units. A device according to claim 1 characterised in that X denotes an integer between 250 and 450. A device according to one or more of the preceding claims, characterised in that said polyorganosiloxane bearing Si-H groups contains between 6000 and 11000 m.mol/kg reactive Si-H groups. A device according to claim 3, characterised in that said polyorganosiloxane bearing Si-H groups has the general formula: where R denotes an alkyl, phenyl or trifluoroalkyl group, more particularly a methyl group, the total m + n is between 5 and 40 and the ratio m : n is between 1.5 - 2.5 : 1. A device according to claim 1, characterised in that the fixing member bears a silicone rubber outer covering obtained by reacting the polyorganosiloxane bearing Si-H groups which are present in an excess of 40 to 60% with respect to the Si(CH=CH 2 )groups of the polyorganosiloxane bearing vinyl groups.

Inventors: KUIPER JOHANNES HENDRICUS ANTO, SCHOUSTRA BAUKE, KUIPER, JOHANNES HENDRICUS ANTONIUS, SCHOUSTRA, BAUKE
Applicants: OCE NEDERLAND BV, OCE-NEDERLAND B.V.
Application year: 1989
Main classification: G03G15
IPC codes: E02F9, G03G15, C08L83, B32B7