Components and catalysts for the polymerization of olefins

Abstract: Solid catalyst components for the polymerization of olefins modified with electron-donor compounds, comprising a titanium halide supported on a magnesium dihalide in active form and containing as an electron-donor compound a di- or polyether having specific reactivity characteristics towards MgCl₂ and TiCl₄.

Description: The present invention relates to solid components of catalysts for the polymerization of olefins and the catalysts obtained therefrom. The catalysts including titanium compounds supported on magnesium halides in active form are well known in the art. Catalysts of this type are described for the first time in the USA patent No. 4,298,718. Said catalysts are formed on titanium tetrahalides supported on halides of magnesium in active form. Although the catalysts have high activity in the polymerization of ethylene as well as alpha olefins like propylene and butene-1, they are not very stereospecific. Improvements to stereospecificity have been made by adding electron-donor compounds to the solid catalyst component (U.S. patent No. 4,544,717). Substantial improvements were made using, in addition to the electron-donor present in the solid component, an electron-donor added to the Al-alkyl co-catalyst component (U.S. patent No. 4,107,414). The catalysts modified in this manner although they are highly stereospecific (isotactic index about 94-95) still do not show sufficiently high levels of activity. Significant improvements in activity and stereospecificity were obtained by preparing the solid catalytic component according to the technique described in U.S. patent No. 4,226,741. High level performance in catalyst activity as well as stereospecificity have been obtained with the catalysts described in European patent No. 045977. Said catalysts have as a solid catalyst component, a magnesium halide in active form on which is supported a titanium halide preferably TiCl₄ and an electron-donor compound selected from specific classes of carboxylic acid esters, of which the phthalates are typical examples, and, as a co-catalyst component, a system formed of an Al-trialkyl compound and a silicon compound containing at least one Si-OR bond (R hydrocarbyl radical). After the appearance of the above mentioned patents which mark the fundamental step for the development of the coordination catalysts supported on magnesium halides, many patents have been filed with the purpose of modifying and/or improving the performance of the above mentioned catalysts. In the prolific patent and scientific literature available, however, there is no description of catalysts endowed with both high activity and stereospecificity in which the electron-donor of the solid catalyst component is the only donor present in the catalyst system. The catalysts known up to now that have both high activity and stereospecificity always include the use of an electron-donor in the solid catalyst component and in the co-catalyst component. Surprisingly, it has now been found that it is possible to prepare highly active and stereospecific catalysts where the only donor used is present in the solid catalyst component. An object of the present invention is a solid catalyst component for the polymerization of olefins having the features defined in claim 1; specific embodiments are defined in the claims dependent on claim 1. The donors used in the catalyst components of this invention are ethers which satisfy particular requisites of reactivity towards anhydrous magnesium dichloride and titanium tetrachloride. The ethers of the invention form complexes with anhydrous magnesium dichloride but in a quantity of less than 60 mmoles per 100 g of MgCl₂; with TiCl₄ the ethers do not undergo at all substitution reactions or they react this way for less than 50 % in moles. Preferably the ethers form complexes with anhydrous magnesium dichloride in quantities comprised between 20 and 50 mmoles, and react with TiCl₄ for less than 30%. The procedures for the tests of activated anhydrous magnesium dichloride complexing and reaction with TiCl₄ are reported below. Examples of suitable ethers which satisfy the reactivity criterion sset forth above are 1,3-diethers of formula: where R, R₁ and R₂ independently are linear or branched alkyl, cycloaliphatic, aryl, alkylaryl or arylalkyl radicals with 1-18 carbon atoms, and R₁ or R₂ may also be hydrogen. In particular R is an alkyl radical with 1-6 carbon atoms, and more specifically it is methyl. In this case, when R₁ is methyl, ethyl, propyl or isopropyl, R₂ may be ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, 2-ethylhexyl, cyclohexyl, methyl cyclohexyl, phenyl, or benzyl; when R₁ is hydrogen R₂ can be ethyl, butyl, sec.butyl, t-butyl, 2-ethylhexyl, cyclohexylethyl, diphenylmethyl, p-chloropenhyl, 1-naphthyl, 1-decahydronaphthyl; R₁ and R₂ can be the same and be ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, neopentyl, isopentyl, phenyl, benzyl, cyclopentyl or cyclohexyl. Examples of representative ethers that are included in the above formula are: 2-(2-ethylhexyl) 1,3-dimethoxypropane, 2-isopropyl- 1,3-dimethoxypropane, 2-butyl-1,3-dimethoxypropane, 2-sec-butyl-1,3-dimethoxypropane, 2-cyclohexyl-1,3-dimethoxypropane, 2-phebyl-1,3-diethoxypropane, 2-cumyl-1,3-diethoxypropane, 2-(2-pnehylethyl)-1,3-dimethoxypropane, 2-(2-cyclohexylethyl)1,3-dimethoxypropane, 2-(p-chlorophenyl)1,3-dimethoxypropane, 2-(diphenylmethyl)-1,3-dimethoxypropane,2-(1-naphthyl)1,3-dimethoxy propane, 2,2-fluorophenyl)-1,3-dimethoxypropane, 2-(1-decahydronaphthyl)-1,3-dimethoxypropane, 2-(p-t-butylphenyl)-1,3-dimethoxypropane, 2,2-dicyclohexyl-1,3-dimethoxypropane, 2,2-diethyl-1,3-dimethoxypropane, 2,2-dipropyl-1,3-dimethoxypropane, 2,2-dibutyl-1,3-dimethoxypropane, 2-methyl-2-propyl-1,3-dimethoxypropane, 2-methyl-2-benzyl-1,3-dimethoxypropane, 2-methyl-2-ethyl-1,3-dimethoxypropane, 2-methyl-2-propyl-1,3-dimethoxypropane, 2-methyl-2-phenyl-1,3-dimethoxypropane, 2-methyl-2-cyclohexyl-1,3-dimethoxypropane, 2,2-bis(p-chlorophenyl)-1,3-dimethoxypropane, 2,2-bis(2-cyclohexylethyl)-1,3-dimethoxypropane, 2-methyl-2-isobutyl-1,3-dimethoxypropane, 2-methyl-2-(2-ethylhexyl)-1,3-dimethoxy propane, 2-methyl-2-isopropyl-1,3-dimethoxypropane, 2,2-diisobutyl-1,3-dimethoxypropane, 2,2-diphenyl-1,3-dimethoxypropane, 2,2-dibenzyl-1,3-dimethoxy-propane, 2,2-bis(cyclohexylmethyl)-1,3-dimethoxypropane, 2,2-diisobutyl-1,3-diethoxypropane, 2,2-diisobutyl-1,3-dibutoxypropane, 2-isobutyl-2-isopropy1-1,3-dimethoxypropane, 2,2-di-sec-butyl-1,3-dimethoxypropane, 2,2-di-tertbutyl-1,3-dimethoxypropane, 2,2-di-neopentyl-1,3-dimethoxypropane, 2-isopropyl-2-isopentyl-1,3-dimethoxypropane, 2-phenyl-2-ebnzyl-1,3-dimethoxypropane, 2-cyclohexyl-2-cyclohexylmethyl-1,3-dimethoxypropane, 2-isopropyl-2-3,7-dimethyloctyl-1,3-dimethoxypropane, 2,2-diisopropyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexylmethyl-1,3-dimethoxypropane, 2,2-diisopentyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclopentyl-1,3-dimethoxypropane, 2,2-dicylopentyl-1,3-dimethoxypropane, 2-heptyl-2-pentyl-1,3-dimethoxypropane. Other suitable ethers are: 2,3-diphenyl-1,4-diethoxybutane, 2,3-dicyclohexyl-1,4-diethoxybutane, 2,2-dibenzyl-1,4-diethoxybutane, 2,3-dibenzyl-1,4-diemethoxybutane, 2,3-dicyclohexyl-1,4-dimethoxybutane, 2,3-diisopropyl-1,4-diethoxybutane, 2,2-bis(p-methylphenyl)1,4-dimethoxybutane, 2,3-bis(p-chlorophenyl)1,4-dimethoxybutane, 2,3-bis(p-fluorophenyl)1,4-dimethoxybutane, 2,4-diphenyl-1,5-dimethoxypentane, 2,3-diphenyl-1,5-dimethoxypentane, 2,4-diisopropyl-1,5-dimethoxypentano, 3-methoxymethyltetrahydrofuran, 3-methoxymethyldioxane, 1,1-dimethoxymethyl-decahydronaphthalene, 1,1-dimethoxymethylindane, 2,2-dimethoxymethylindane, 1.1-dimethoxymethyl-2-isopropyl-5-methylcyclohexane, 1,3-diisoamyloxypropane, 1,2-diisobutoxypropane, 1,2-diisobutoxyethane, 1,3-diisoamyloxypropane, 1,2-diisoamuloxyethane, 1,3-dineopentoxypropane, 2,2-tetramethylene-1,3-dimethoxypropane, 1,2-dineopentoxyethane, 2,2-tetramethylene-1,3-dimethoxypropane, 2,2-pentamethylene-1,3-dimethoxypropane, 2,2-pentamethylene-1,3-dimethoxypropane, 2,2-hexamethylene-1,3-dimethoxypropane, 1,2-bis(methoxymethyl)cyclohexane, 2,8-dioxaspiro[5,5]undecane, 3,7-dioxabicyclo[3,3,1]nonane, 3,7-dioxabicyclo[3,3,0]octane, 3,3-diisobutyl-1,5-dioxononane, 6,6-diisobutyldioxyepane, 1,1-dimethoxymethylcyclopropane, 1,1-bis[dimethoxymethyl] cyclohexane, 1,1-bis[methoxymethyl]bicyclo[2,2,1]heptane, 1,1-dimethoxymethyl cyclopentane, 2-methyl-2-methoxymethyl-1,3-dimethoxypropane. The ethers preferred are the 1,3-diethers belonging to the general formula indicated above and in particular those where R is methyl and R₁ and R₂, independently, are isopropyl, isobutyl, t-butyl, cyclohexyl, isopentyl, cyclohexylethyl. Ethers particularly preferred are 2,2-diisobutyl-1,3-dimethoxypropane; 2-isopropyl 2-isopentyl-1,3-dimethoxypropane; 2,2-bis(cyclohexylmethyl)-1,3-dimethoxypropane, 2-isopropyl-2-3,7-dimethyloctyl-1,3-dimethoxypropane, 2,2-diisopropyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexylmethyl-1,3-dimethoxypropane, 2,2-diisopentyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclopentyl-1,3-dimethoxypropane, 2,2-dicyclopentyl-1,3-dimethoxypropane, 2-heptyl-2-pentyl-1,3-dimethoxypropane, 2,2-dicyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-isobutyl-1,3-dimethoxypropane, 2,2-dipropyl-1,3-dimethoxypropane. The above ethers can be prepared according to the methods disclosed in published European patent application EP-A-0361493, of the same Applicant and filed on the same date as the present application with the title "Diethers Usable In The Preparation of Ziegler-Natta Catalysts". Said EP-A-0 361 493 discloses diethers of general formula R VII O-C(R III )(R II )-C(R I )(R)-C(R IV )(R V )-OR VI where R to R V , same or different, are H or hydrocarbon radicals, provided that R and R I are not both H or methyl or are not methyl and propyl, and R VI and R VII are the same or different and are hydrocarbon radicals; two or more of R to R VII may be bonded to form a cyclic structure. Said diethers, used in the preparation of Ziegler-Natta catalysts, are prepared by reaction of diols corresponding to the above diethers with alkylant agent. A way of synthesis of said diols consists in the reduction of the corresponding oxidized compounds such as diketones, ketoaldehydes, dicarboxylic acids. The ether complexing test with MgCl₂ is conducted as follows. In a 100 ml glass flush with fixed blades glass mechanical agitator are introduced in a nitrogen atmosphere, in order: 70 ml anhydrous n-heptane 12 mmoles anhydrous MgCl₂ activated as described below 2 mmoles ether. The ingredients are heated at 60°C for 4 hours (stirring speed 400 rpm), then filtered and washed at room temperature with 100 ml n-heptane and dried with mechanical pump. The quantity of ether complexed is determined, after treatment of the solid with 100 ml of ethanol, by quantitative gaschromatographic analysis. The data relative to the complexing test are shown in Table 1. The test for reactivity with TaCl₄ is conducted as follows. In a 25 ml test tube with a magnetic agitator are introduced, in a nitrigen atmosphere, in order: 10 ml anhydrous n-heptane 5 mmoles TiCl₄ 1 mmole ether donor The ingredients are heated at 70° for 30 min then cooled at 25°C and decomposed with 90 ml of ethanol. The solution obtained is analyzed gas chromatographically with a Carlo Erba HRGC 5300 Mega Series gas chromatograph with a 25 meters Chrompack CP-SIL 5 CB capillary column. The data relative to the reactivity tests are shown in Table 1. The magnesium dichloride used in the complexing test with the ethers is prepared as follows. In a 1 l container of a vibrating mill (Siebtechnik Vibratrom) containing 1.8 kg of steel spheres 16 mm in diameter, are introduced under a nitrogen atmosphere, 50 g anhydrous MgCl₂ and 6.8 ml 1,2 dichloroethane (DCE). The mixture is milled at room temperature for 96 hours, after which the solid obtained is dried at 50°C for 16 hours under vacuum of a mechanical pump. Solid characterization. In the X-ray powder spectrum: half peak breadth of D110 reflection = 1.15 cm; presence of a halo with maximum intensity at angle 2 = 32.1°; Surface area (B.E.T.) = 125 m²/g; Residual DCE = 2.5% by weight. The preparation of the solid catalyst component including the ethers of the invention is carried out according to various methods. For example, the magnesium dihalide (used in anhydrous state containing less than 1% of water), the titanium compound and the di or polyether are ground together under conditions where activation of the magnesium dihalide occurs. The milled product is then treated one or more times with TiCl₄ in excess at temperatures between 80 and 135°C and then washed repeatedly with a hydrocarbon i.e. hexane until all chlorine ions disappear. According to another method, the anhydrous magnesium dihalide is preactivated according to known methods in the prior art and then reacted with an excess of TiCl₄ which contains the ether compound in solution, at temperatures between 80 and 135°C. The treatment with TiCl₄ is repeated and the solid is then washed with hexane to eliminate all traces of unreacted TiCl₄. According to another method, an MgCl₂ nROH adduct (particularly in form of spheroidal particles) in which n is a number from 1 to 3, and ROH is ethanol, butanol, or isobutanol, is treated with an excess of TiCl₄ containing the ether compound in solution at a temperature generally between 80 and 120°C. After the reaction, the solid is treated once more with TiCl₄, then separated and washed with a hydrocarbon until the chlorine ions are removed. According to another method, carboxylates or halocarboxylates of magnesium or alcoholates or chloroalcoholates of magnesium, the chloroalcoholates prepared according to U.S. patent No. 4,220,554 are treated with TiCl₄ in excess containing the ether compound in solution, under reaction conditions described above. According to another method complexes of magnesium halide with titanium alcoholates for example the complex MgCl₂ 2Ti(OC₄H₉)₄ are treated, in a hydrocarbon solution, with TiCl₄ in excess containing the ether compound in solution. The solid product is separated and further treated with an excess of TiCl₄ and then separated and washed with hexane. The reaction with TiCl₄ is conducted at temperatures between 80 and 120°C. According to a variant of the above method, the complex between MgCl₂ and the titanium alcoholate is reacted in hydrocarbon solution with hydropolyxyloxane. The separated solid product is reacted at 50°C with silicon tetrachloride containing the ether compound in solution and the solid is treated with TiCl₄ in excess operating at 80-100°C. It is possible to react with TiCl₄, in excess, containing the ether compound in solution, porous styrene-divinylbenzene resins in spherical particle form, impregnated with solutions of compounds or complexes of Mg soluble in organic solvents. The resins and their method of impregnation are described in EP-A-344 755. The reaction with TiCl₄ is carried out at 80-100°C and after separating the TiCl₄ excess, the reaction is repeated and the solid is then washed with a hydrocarbon. The molar ratio MgCl₂/ether compound used in the reactions indicated above is generally between 4:1 and 12:1. The ether compound is present in the magnesium halide containing component in quantities generally between 5 and 20% mole with respect to the magnesium dihalide. However, in the case of components supported on resins, the molar ratio between fixed ether compound and the magnesium present in generally between 0.3 and 0.8. In the catalyst components of the invention the ratio Mg/Ti is generally between 30:1 and 4:1; in the components supported on resins the ratio is lower, generally from 2:1 to 3:1. The titanium compounds that can be used for the preparation of catalytic components are the halides and halogen alcoholates. Titanium tetrachloride is the preferred compound. Satisfactory results are obtained also with trihalides, particularly TiCl₃ HR, TiCl₃ ARA, and with haloalcoholates, such as TiCl₃OR, wehere R is a phenyl radical. The above mentioned reactions result in the formation of magnesium dihalide in active form. In addition to these reactions, other reactions that result in the formation of magnesium dihalide in active form starting with magnesium compounds different from halides are well known in literature. The active magnesium dihalides present in the solid catalyst components of the invention show in the X-ray powder spectrum of the catalyst component the replacement of the most intense diffraction present in the powder spectrum of the non-activated magnesium halides having a surface area of less than 3 m²/g by a halo with the maximum intensity peak shifted with respect to the position of the most intense diffraction line, or a half peak breadth of the most intense diffraction line at least 30% greater than the half peak breadth of the corresponding line of the non-activated magnesium halide. The most active forms are those where in the X-ray powder spectrum of the catalyst component a halo appears. Among the magnesium dihalides, the magnesium dichloride is the preferred compound. In the case of the most active forms of magnesium dichloride the halo appears in place of the diffraction line that is present in the spectrum of the non-active magnesium chloride at an interplanar distance of 2.56 Å. The solid catalyst component of the invention forms, by reaction with Al-alkyl compounds, catalysts for the polymerization of olefins CH₂=CHR, where R is hydrogen, alkyl radical with 1-6C, or aryl radical, or mixtures of said olefins mixed with each other with or without diolefins. Therefore another object of the present invention is a catalyst for the polymerization of olefins having the features defined in independent claim 14; specific embodiments of said catalysts are defined in the claims depending on claim 14. The Al-alkyl compounds include Al-trialkyl such as Al-triethyl, Al-triisobutyl, Al-tri-n-butyl. Linear or cyclic Al-alkyl compounds containing two or more Al atoms linked to each other by O, N or S atoms may be used. Examples of these compounds are: (C₂H₅)₂Al-O-Al(C₂H₅)₂ where n is a number between 1 and 20. Also one can use AlR₂OR′ compounds, where R′ is an aryl radical substituted in position 2 and/or 6 and R is an alkyl radical with 1-6 carbon atoms, or AlR₂H compounds. The Al-alkyl compound is used in Al/Ti ratios generally between 1 and 1000. The trialkyl compounds may be used in mixtures with Al-alkyl halides, such as AlEt₂Cl. The polymerization of olefins is carried out according to known methods in a liquid phase of the monomer(s) or a solution of monomer(s) in an aliphatic or aromatic hydrocarbon solvent, or in gas phase, or with techniques using a combination of liquid phase and gas phase. The (co)polymerization temperature is generally between 0° and 150°C, preferably between 60° and 100°C, while operating at atmospheric pressure or at a higher pressure. The catalysts may be precontacted with small quantities of olefins (prepolymerization). The prepolymerization improves the catalyst performance as well as the polymer morphology. The prepolymerization is carried out by maintaining the catalyst in suspension in a hydrocarbon solvent (hexane, heptane, etc.) while contacting small amounts of the monomer with the catalyst and polymeriizing at a temperature between room temperature and 60°C producing quantities of polymer included between 0.5 and 3 times the weight of the catalyst component. It may also be carried out in liquid or gaseous monomer, under the temperature conditions above, to produce quantities of polymer up to 1000 g per g of the catalyst component. In case of stereoregular polymerization of olefins, in particular of propylene, sometimes it is convenient to use together with the Al-alkyl compound an electron-donor selected from 2,2,6,6,-tetramethylpiperidine and silicon compounds containing at least one Si-OR bond wherein R is a hydrocarbyl radical. Preferably the silicon compounds have the formula R I R II Si(OR III ) (OR IV ) where R I and R II independently, are branched alkyl, cycloaliphatic or aryls radicals with 1-12 carbon atoms; R III and R IV independently are alkyl radicals with 1-6 carbon atoms. Examples of such compounds are: (t-butyl)₂ Si(OC₃)₂; (cyclohexyl)₂ Si(OCH₃)₂; (isopropyl)₂ Si(OCH₃)₂; (sec-butyl)₂ Si(OCH₃)₂. The molar ratio between Al-alkyl compound and electron-donor is usually between 5:1 and 100:1. As indicated above, the catalysts find particular application in the polymerization of CH₂=CHR olefins where R is an alkyl radical with 1-6 carbon atoms or an aryl radical. They are also particularly suited for the polymerization of ethylene and its mixtures with smaller proportions of alpha-olefins, such as butene-1, hexene-1 and octene-1 to form LLDPE, because the catalysts produce polymers with narrow molecular weight distribution. In the copolymerization of ethylene with propylene, or other alpha-olefins or mixtures thereof to form elastomeric products copolymers are obtained having low crystallinity suitable therefore for the production of elastomers with highly valued qualities. The following examples illustrate the invention. In the examples, unless otherwise indicated, the percentages are by weight. The solubility in xylene is determined by thermo solubilizing the polymer (130°C), cooling and then filtering it. The solubility is determined by the fraction soluble at 25°C. The insoluble residue substantially corresponds to the isotacticity index determined by extraction with boiling n-heptane (4 hours). Melt index E and F for polyethylene and L for polypropylene are determined according to ASTM D1238. Melt index E and F are measured at 190°C with respective weights of 2.15 and 21.6 Kg. The one for polypropylene is measured at 230°C with a weight of 2.16 Kg. The intrinsic viscosity is determined in tetralin at 135°C. Unless otherwise indicated, the isotacticity index (I.I.) has been determined by extraction with boiling n-heptane (4 hours). Polymerization Procedure A In liquid monomer Procedure A.1. In a 4 l stainless steel autoclave equipped with an anchor agitator and previously purged with nitrogen flux at 70°C for 1 hour, were introduced, under propylene flow at 30°C, 80 ml anhydrous n-hexane containing an adequate quantity of solid catalyst component and 6.9 mmoles of Al(Et)₃. The autoclave was closed and 120 ml of hydrogen was introduced. The agitator was inserted and 1.2 Kg of liquid propylene, or other alpha-olefin monomer capable of being polymerized in liquid phase, was charged. The temperature was brought to 70°C in 5 minutes and the polymerization was carried out for 2 hours. At the end of the test the unreacted propylene is removed, the polymer recovered and dried in an oven at 70°C under nitrogen flow for 3 hours, and then characterized. Procedure A.1.1. The procedure of A.1 above were followed except that added to the hexane was an oppropriate quantity of an electron-donor together with Al(Et)₃ corresponding to a molar ratio Al/donor = 20. The composition of the solid catalyst components and the ethers used, the polymerization yields and the properties of the polymers obtained are described in tables 2 and 3. In table 3 the donor used together with Al(Et)₃ is indicated in parenthesis. B In solvent. Procedure B.2. A 2.5 l stainless steel autoclave, equipped with a thermostat and magnetic agitator, which was previously purged with nitrogen flux at 70°C for 1 hour and washed 4 times successively with propylene, was heated to 45°C and, under a light nitrogen flow, 870 ml of anhydrous hexane was charged. The catalyst suspension (catalyst component and Al-alkyl premixed immediately before the test in 130 ml solvent) was then added. The autoclave was closed and 120 ml of hydrogen was fed from a calibrated cylinder. The agitator was inserted and the temperature was rapidly brought to 75°C (in about 5 minutes). Gaseous propylene or other alpha-olefin monomer was then introduced up to a total pressure of 8 atm. This condition was maintained for 4 hours continuously feeding propylene or other monomers to reintegrate the monomer polymerized. At the end of the polymerization the autoclave was rapidly degassed and cooled to 25-30°C. The polymer suspension was then filtered, the solid part was dried in an oven at 70° C in nitrogen for 4 hours and then weighed and analyzed. The filtrate was evaporated and the dry residue consisting of amorphous polymer was recovered and weighed. This was taken into consideration in calculating the total yield and the total isotactic index. Procedure B.2.1 In a 2000 ml stainless steel autoclave, equipped with an anchor agitator, was introduced under a propylene flow at 25°C 1000 ml n-heptane, 2.5 mmoles of Al(C₂H₅)₃ and an adequate quantity of the solid catalyst component. The autoclave was closed and the pressure brought to 1 atm. while feeding propylene, and an overpressure of hydrogen equal to 0.2 atm was introduced. The reaction mixture was heated to 70°C and the pressure brought to a total of 7 atm, by feeding propylene, and polymerized for 2 hours while continuing to feed the monomer to maintain the pressure at 7 atm. The polymer obtained was isolated by filtration and dried; the polymer remaining in the filtrate was precipitated in methanol, vacuum dried and considered in determining the total insoluble residue of the extraction with n-heptane. The composition of the solid catalyst components and ethers used and the polymerization yields and the properties of the polymers obtained are described in tables 2 and 3. Procedure B.2.2. The polymerization methods described in procedure B.2.1. were followed except using 5 mmoles of Al(C₂H₅)₃ together with an adequate quantity of electron donor such that the molar ratio Al/donor=20. The composition of the solid catalyst components, ether and electron donor (with the Al-alkyl compound) used and the polymerization yields and the properties of the polymers obtained are described in tables 2 and 3. In table 3 the donor used together with Al(C₂H₅)₃ is indicated in parenthesis. Example 1 In a 1 l flask equipped with condenser, mechanical agitator and thermometer was introduced 625 ml TiCl₄ under nitrogen environment. 25 g of spherical MgCl₂.2.1C₂H₅OH support, obtained according to the procedures and ingredients of example 1 of U.S. patent 4 469 648, was fed at 0°C with agitation and heated to 100°C over 1 hour. When the temperature reached 40°C, 4.1 ml of 2,2-diisobutyl-1,3-dimethoxypropane was introduced, and the contents maintained at 100°C for 2 hours, left to to settle and the supernatant siphoned off. 550 ml of TiCl₄ was added to the solid and heated at 120°C for 1 hour with agitation. The agitation was stopped, the solid was allowed to settle and the supernatant was removed by siphon. The residual solid was then washed 6 timed with 200 ml portions of anhydrous hexane at 60°C and 3 times at room temperature and dried under vacuum. The catalyst solid component contained 3.45% Ti and 12.6% 2,2-diisobutyl-1,3-dimethoxypropane. Propylene was polymerized according to procedure A.1 above for the liquid monomer using 0,76 g of Al(C₂H₅)₃, 0.09 ml of hexane suspension containing 7.25 mg of solid catalyst component and 1000 ml hydrogen. 460 g of polymer was obtained. The polymer yield was 63.4 Kg/g of catalyst component. The polymer has a 95.3% insoluble residue in xylene at 25°C, a melt index of 10.0 g/10′ and a tamped bulk density of 0.48 g/ml. Example 2 In a 500 ml glass flask equipped with condenser, mechanical agitator and thermometer, was introduced, in an anhydrous nitrogen environment at 20°C, 285 ml of TiCl₄ and 20 g of C₂H₅OMgCl support prepared according to the precedure of U.S. patent n. 4,220,554. While agitating the contents were heated to 70°C in 30 minutes and then 4.7 ml 2,2-diisobutyl-1,3-dimethoxypropane was added and heated to 120°C in 30 minutes. The temperature was maintained at 120°C for 1 hour. The reaction mixture was allowed to settle and supernatant removed by siphon. Then another 285 ml TiCl₄ were added and heated at 120°C for 1 hour. The reaction mixture was allowed to settle and the supernatant removed by siphon. The residual solids were washed 5 times with 150 ml portions of anhydrous heptane at 80°C, and again at room temperature with 150 ml portions of anhydrous hexane until there were no chlorine ions in the wash liquid. The analysis of the vacuum dried solid catlyst component showed a content of 2,2% Ti and 12.2% 2,2-diisobutyl-1,3-dimethoxypropane. Propylene was polymerized according to the Procedure A.1 above using 0.76 g Al(C₂H₅)₃, 0.12 ml hexane suspension containing 13 mg of solid catalyst component and 1000 ml hydrogen. 240 g of polymer was obtained with a polymer yield of 18.4 Kg/g catalyst component, a 95.2% insoluble residue in xylene, at 25°C, a melt index of 10.6 g/10′ and a tamped bulk density of 0.50 g/ml. Example 3 In a 350 ml procelain jar containing 4 porcelain spheres, was introduced, under an anydrous nitrogen environment, 9.2 g of commercial anhydrous MgCl₂ and 3.3 ml of 2,2-diisobutyl-1,3-dimethoxypropane. The jar is placed in a centrifugal mill operated at 350 rpm for 15 hours. In a 250 ml glass flask fitted with a condenser, mechanical agitator and thermometer, under an anhydrous nitrogen environment at room temperature, were introduced 8 g of the above milled product and 115 ml of TiCl₄. The contents were heated to 120°C in 20 minutes and maintained at 120°C for 2 hours. The solids were allowed to settle and supernatant was siphoned off. Another 115 ml of TiCl₄ was introduced, heated at 120°C for 2 hour. The solids were allowed to settle and the supernatant removed by siphone. The solid residue was washed repeatedly at 60°C and at 40°C with 100 ml portions of anhydrous hexane, until there were no chlorine ions in the wash liquid. The solid residue, obtained by vacuum drying, contained 2.15% Ti and 10.2% 2,2-diisobutyl-1,3-dimethoxypropane. The polymerization was carried out according to procedure B.2, using 0.57 g Al(C₂H₅)₃ and 0.25 ml hexane suspension containing 15.0 mg of solid catalyst component. 284 g of polymer was obtained with a polymer yield of 18.9 Kg/g catalyst, a 96.1% residue insoluble in xylene at 25°C, a melt index of 4.2 g/10′ and a tamped bulk density of 0.35 g/ml. Example 4 In a 350 ml porcelain jar containing 4 porcelain spheres was introduced, under an anhydrous nitrogen environment, 7.65 of anhydrous MgCl₂, 2.76 ml 2,2-diisobutyl-1,3-dimethoxypropane, and 1.17 ml TiCl₄. The jar was placed in a centrifugal mill operated at 350 rpm for 20 hours. In a 350 ml glass reactor, equipped with porous disk for filtration, condenser, mechanical agitator and thermometer, was introduced at room temperature under an anhydrous nitrogen environment, 8 g of the above milled product and 32 ml 1,2-dichloroethane. The contents were heated at 83°C for 2 hours, then filtered and the solid residue washed 3 timed with 50 ml portions of anhydrous hexane. The solid residue obtained by vacuum drying contained 1.5% Ti and 18.4% 2,2-diisobutyl-1,3-dimethoxypropane. Propylene was polymerized according to procedure B.2 using 0.57 g Al(C₂H₅)₃ and 0.5 ml hexane suspension containing 81 mg solid catalyst component. 188 g of polymer was obtained with polymer yield of 2.3 Kg/g catalyst component, a 94.7% residue insoluble in xylene, at 25°C a melt index of 8.4 g/10′, and tamped bulk density of 0.29 g/ml. Example 5 In a 500 ml glass flask equipped with a condenser, mechanical agitator and thermometer, was introduced, at room temperature under anhydrous nitrogen atmosphere, 250 ml of TiCl₄ and 25 g of support in spherical particles comprising a styrene-divinylbenzene copolymer impregnated with the MgCl₂ 2Ti(OC₄H₉)₄ complex, prepared according to procedure of example 1 of U.S. patent application SN 07/359,234. While agitating, the contents were heated to 100°C. When the temperature reaches 40°C, 1.52 ml of 2,2-diisobutyl-1,3-dimethoxypropane was introduced. The temperature maintained at 100°C for 1 hour, the solid allowed to settle and the supernatant was removed by siphon. An additional 250 ml TiCl₄ was fed and heated at 120°C for 2 hours. After settlement of the solids and siphoning of the supernatant, the solid residue was washed 5 times with 150 ml portions of anhydrous heptane at 85°C, then 3 times with anhydrous hexane at room temperature, until no chlorine ions were formed in the wash liquid. After vacuum drying, the solid catalytic component contained 0.77% Ti and 3.9% 2,2-diisobutyl-1,3-dimethoxypropane. Propylene was polymerized according to procedure A.1 using 0.79 g Al(C₂H₅)₃, 1.4 ml hexane suspension containing 49.5 mg solid catalyst component and 1300 ml hydrogen. 400 g of polymer was obtained with a polymer yield of 8.1 kg/g catalyst component, a 95.1% insoluble residue in xylene, at 25°C, a melt index of 11.2 g/10′ and a tamped bulk density of 0.42 g/ml. Example 6 In a 500 ml glass flask equipped with condenser, mechanical agitator and thermometer was introduced 156.9 ml Ti(OC₄H₉)₄ and 20 g anhydrous MgCl₂. While agitating, the contents were heated to 140°C for 3 hours, cooled to 40°C and the resulting solution diluted with 157 ml anhydrous heptane. Then 31.5 ml polymethylhydroxyloxane was added (d=0.99 g/ml, Mw=2256). After allowing the solvents to settle and siphoning off the supernatant, the solid was washed 3 times with 150 ml portions of anhydrous heptane. At 50°C, 18.4 ml of SiCl₄ was added over a 15 minutes period, then treated with 2.7 ml 2,2-diisobutyl-1,3-dimethoxypropane and maintained at 50°C for 2 hours. The solids were allowed to settle and the supernatant removed by siphon and washed 4 times with 120 ml portions of anhydrous hexane. The residue was treated with 52.3 ml of TiCl₄ and then heated at 90°C for 2 hours. The liquid was removed by siphon after the solids were allowed to settle, the solid residue was washed repeatedly with anhydrous heptane at 60°C and then 5 times at room temperature, until there were no chlorine ions in the wash liquid. After vacuum drying, the solid solid catalyst component contained 1.65% Ti and 14.9% 2,2-diisobutyl-1,3-dimethoxypropane. Propylene was polymerized according to procedure B.2 using 0.57 g Al(C₂H₅)₃ and 0.4 ml hexane suspension containing 7.9 mg solid catalyst component. 229 g of polymer was obtained with a polymer yield of 29 kg per g; of catalyst component 96.2% insoluble residue in xylene at 25°C and a tamped bulk density 10 AD of 0.42 g/cc. Example 7 Into a 1 l glass flask equipped with condenser, mechanical agitator and thermometer, under anhydrous nitrogen atmosphere, was introduced 572 ml solution containing 11.4 g Al(C₂H₅)₃ for each 100 ml hexane. While agitating at 5°C, 40 g spherical MgCl₂.2.6C₂H₅OH support, prepared according to method of example 1 in U.S. patent No. 4,469,648 was added over 90 minutes, then heated to 60°C for 3.5 hours, the solids were allowed to settle and the supernatant removed by siphon. The solid residue was washed 10 times with 200 ml portions of anhydrous heptane. To the product obtained, which was diluted to 100 ml with anhydrous heptane, was added over 2 hours at 80°C, 2.7 ml n-C₄H₉OH diluted with 1.5 ml anhydrous heptane. The solid were allowed to settle and the liquid siphoned off. The solid was washed repeatedly with 150 ml portions anhydrous hexane. After vacuum drying the solid showed a Mg content of 20.9% and C₂H₅OH of 3.6%. In a 500 ml glass flask was introduced, under an anhydrous nitrogen environment, 362 ml TiCl₄, then while agitating at 0°C, 14.5 g of the solid catalyst component obtained above were added. Over a 1 hour period the contents were heated to 100°C. When the temperature reached 40°C, 4.8 ml 2,2-diisobutyl-1,3-dimethoxypropane was added. The contents were heated at 100°C for 2 hours. The solids allowed to settle and the liquid was siphoned off To the solid residue 319 ml of TiCl₄ was added, heated to 120°C for 1 hour, and then the liquid was removed by siphoning after settling. The solid was washed repeatedly with 150 ml portions anhydrous hexane first at 60°C and then at room temperature. After vacuum drying the catalytic solid contains 2.45% Ti and 6.3% 2,2-diisobutyl-1,3-dimethoxypropane. Propylene was polymerized according to procedure A.1 using 0.76 g Al(C₂H₅)₃, 0.09 ml hexane solution containing 8.9 mg solid catalyst component and 1000 ml hydrogen. 430 g of polymer was obtained with a polymer yield of 51.8 Kg/g catalyst component, 90.4% insoluble residue in xylene at 25°C, a melt index of 8.9 g/10′ and a tamped bulk density of 0.49 g/ml. Examples 8-18 and comparative examples 1-3 Into a 500 ml reactor equipped with filtering disk 225 ml TiCl₄ was introduced at 0°C. While agitating 10.1 g (54 mmoles) microspheroidal MgCl₂.2C₂H₅OH, obtained according to the method of example 1 of U.S. patent 4,469,648, was added. Upon completing the addition, the temperature was brought to 40°C and 9 mmoles ether was introduced. The temperature was raised to 100°C over one hour period and allowed to react for 2 hours after which the unreacted TiCl₄ was removed by filtration. Another 200 ml TiCl₄ was added and allowed to react at 120°C for 1 hour, filtered and washed with n-heptane at 60°C until the chlorine ions disappeared from the filtrate. The ethers used and the analytical data relative to the solid catalyst component obtained in this manner are reported in table 2. Examples 19-36 and comparative examples 4-6 The polymerization data with the catalysts obtained from the solid catalyst components prepared according to examples 8-18 and comparative examples 1-3 are reported in table 3. Example 37 A 1.4 stainless steel autoclave, equipped with a thermostat and mechanical agitator, was purged with gaseous propylene at room temperature for 1 hour. Then, while agitating, 66 g of butadiene, 230 g of liquid propylene and 300 ml of hydrogen were fed. Under propylene pressure a catalytic suspension of 0.6 Al(Et₃)₃ TEAL and 0.048 g solid catalyst component of example 1. The temperature was rapidly brought to 70°C (in 5 min) and the resulting pressure was 24.6 atm. These conditions were maintained for 4 hours reintegrating feeding propylene continuously to reintegrate the portion polymerized. The autoclave was then degassed and cooled at room temperature. 64 g polymer, dried in an over under nitrogen at 60°C for 4 hours, was recovered, with a yield of 1333 g polymer per g catalyst. When analyzed, using standard methods, the polymer showed the following characteristics: [η] in tetrahydronapththalene at 135°C = 1.8 dl/g. MIL = 4 g/10′ Soluble in xylene at 25°C = 24.1% (weight). Butadiene content (determined via IR): raw polymer = 0.6% 1,2; 3.7% 1,4 trans insoluble in xylene = 0.5% 1,2; 1.6% 1,4 trans soluble in xylene = < 0.25% 1,2; 8.2 1,4 trans. Example 38 The autoclave and procedure of example 37 was used to polymerize propylene with the solid catalyst component of example 1, but using instead of Al-triethyl, a mixture of 3.3 mmoles Al-triethyl and 3.3 mmoles Al-diethylmonochloride and 0.018 g solid catalyst component. 380 g of a polymer with a polymer yield of 35.2 kg/g of catalyst component, a 94.1% insoluble residue in xylene at 25°C, and a melt index of 7.3 g/10′. Example 39 In the same autoclave used in example 1 was charged at 30°C and without agitation, a catalyst suspension of 0.9 g Al-triethyl and 0.09 g of the solid catalyst component of example 37 in about 18 ml hexane. Then 800 g propane was introduced with agitation. The temperature was rapidly brought to 75°C, and then 2 atm hydrogen, 200 g butene-1 where introduced. Ethylene was then introduced until the pressure reached 33 atm. These conditions were maintained for 2 hours maintaining constant pressure by continuously feeding with a mixture of ethylene and butene-1 in a weight ratio of 10/1. The autoclave was degassed and cooled at room temperature. The amount of polymer, obtained after drying at 70°C under nitrogen for 4 hours, was 280 g, which corresponded to a yield of 31.1 kg per g of catalyst component. Analyzed using standard methods, the product showed the following characteristics: MIE = 0.23 g/10′ (F/E = 26.7) MIF = 6.16 g/10′ Butene (determined via IR) = 6% (weight) Density = 0.9211 g/cm³ Soluble in xylene at 25°C = 6.3% (weight) Example 40 In the same autoclave used in example 3 purged as described therein but using ethylene instead of propylene, was introduced at 45°C under hydrogen flow, a 900 ml solution of 0.5 g/l of Al-triisobutyl in anhydrous hexane and immediately after 0.015 g of solid catalyst component of example 1 suspended in 100 ml of the above mentioned solution. The contents were rapidly heated to a temperature of 75°C, then hydrogen was fed until the pressure reached 4.5 atm. These conditions were maintained for 3 hours continuously replacing the ethylene polymerized. The autoclave was rapidly degassed and cooled at room temperature. The polymeric suspension was filtered and the solid was dried at 60°C under nitrogen for 8 hours. 300 g of polymer was obtained (corresponding to a yield of 20 kg/g of catalyst component) which had the following characteristics (determined by standard methods): MIE = 1.74 g/10' (MIF/MIE = 26.5) MIF = 46 g/10' [η] 135°C THN = 1.78 dl/g tamped bulk density = 0.362 g/ml Other features, advantages and embodiments of the invention disclosed herein will be readily apparent to those exercising ordinary skill after reading the foregoing disclosures. In this regard, while specific embodiments of the invention have been described in considerable detail, variations and modifications of these embodiments can be effected without departing from the spirit and scope of the invention as described and claimed. Examples 41-51 Catalyst components are prepared according to the procedure of examples 8-18 by using different ethers. The ethers used and the analytical data relative to the solid catalyst component obtained in this matter are reported in Table 4. Examples 52-62 The polymerization data with the catalyst obtained from the solid catalyst components prepared according to examples 41-51 are reported in Table 5.

Claims: A solid catalyst component for the polymerization of olefins comprising a magnesium dihalide in active form and supported thereon a titanium compound containing at least one Ti-halogen bond and an electron-donor compound selected from ethers containing two or more ether groups, said ethers being capable of forming complexes with activated anhydrous magnesium dichloride at less than 60 mmoles per 100 g of activated anhydrous magnesium dichloride and of entering into substitution reactions with TiCl₄ at less than 50 % by moles; the ether complexing test with MgCl₂ being conducted as follows: in a 100 ml glass flask with fixed blades glass mechanical agitator are introduced in a nitrogen atmosphere, in order: 70 ml anhydrous n-heptane 12 mmoles activated anhydrous MgCl₂ 2 mmoles ether; the ingredients are heated at 60°C for 4 hours (stirring speed 400 rpm), then filtered and washed at room temperature with 100 ml n-heptane and dried with mechanical pump; the quantity of ether complexed is determined, after treatment of the solid with 100 ml of ethanol by quantitative gaschromatographic analysis; and the test for reactivity of the ethers with TiCl₄ being conducted as follows: in a 25 ml test tube with a magnetic agitator are introduced, in a nitrogen atmosphere, in order: 10 ml anhydrous n-heptane 5 mmoles TiCl₄ 1 mmole ether donor; the ingredients are heated at 70°C for 30 min, then cooled at 25°C and decomposed with 90 ml of ethanol; the solution obtained is analyzed gas chromatographically with a Carlo Erba HRGC 5300 Mega Series gas chromatograph with a 25 meters Chrompack CP-SIL 5 CB capillary column. The solid catalyst component of claim 1 where the ethers are characterized by the formation of complexes with activated anhydrous magnesium dichloride in quantities between 20 and 50 mmoles per 100 g of activated magnesium dichloride. The solid catalyst component of claim 1 wherein the ethers are selected from diethers having the following general formula: where R, R₁ and R₂, independently, are linear or branched alkyl, cycloaliphatic, aryl, alkylaryl or arylalkyl radicals with 1-18 carbon atoms and R₁ or R₂ may also be hydrogen. The solid catalyst component of claim 3 wherein R is methyl, and when R₁ is methyl, ethyl, propyl or isopropyl, R₂ is ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, 2-ethylhexyl, cyclohexyl, methylcyclohexyl, phenyl or benzyl, and when R₁ and R₂ are the same, they are ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, neopentyl, isopentyl, phenyl, benzyl, cyclopentylor cyclohexyl. The solid catalyst component of claim 3 wherein R is methyl and R₁ and R₂ are different and are isopropyl, isobutyl, t-butyl, cycloexyl, isopentyl or cyclohexylethyl. The solid catalyst component of claim 3 where the ethers are 2,2-diisobutyl-1,3-dimethoxypropane, 2-isopropyl-2-isopentyl-1,3-dimethoxypropane, 2,2-bis(cyclohexyl-methyl)-1,3-dimethoxypropane, 2-isopropyl-2-3,7-dimethyloctyl-1,3-dimethoxypropane, 2,2-diisopropyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexylmethyl-1,3-dimethoxypropane, 2,2-dicyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-isobutyl-1,3-dimethoxypropane, 2,2-diisopentyl-1,3-dimethoxypropane, 2,2-dipropyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclopentyl-1,3-dimethoxypropane, 2,2-dicyclopentyl-1,3-dimethoxypropane, 2-heptyl-2-pentyl-1,3-dimethoxypropane. The solid catalyst component of one or more of the preceding claims wherein the titanium compound is selected from the group consisting of the halo alcoholates and the halides of titanium and the magnesium dihalide is magnesium dichloride. The solid catalytic component of claim 7 wherein the titanium compound is titanium tetrachloride. The solid catalytic component of claim 7 wherein the magnesium dichloride is present in active form characterized in that in the X-ray powder spectrum of the catalyst component a halo appears instead of the most intense diffraction line which appears at an interplanar distance of 2.56 Å in the non-activated magnesium dichloride and the maximum intensity of the halo is shifted with respect to said interplanar distance. The solid catalyst component of one or more of the preceding claims wherein the ether is present in an amount between 5 and 20% mmoles with respect to the magnesium dihalide. The solid catalyst component of one or more of the preceding claims wherein the Mg/Ti ratio is between 30:1 and 4:1. The solid catalyst component of one or more of the preceding claims wherein the magnesium dichloride in active form is obtained from MgCl₂ complexes with alcohols or titanium alcoholates, or from alcoholates and chloroalcoholates of magnesium. The solid catalyst component of one or more of the preceding claims wherein the magnesium dichloride and the titanium compound are supported on resins and the Mg/Ti ratio is from 2:1 to 3:1. A catalyst for the polymerization of olefins CH₂=CHR, wherein R is H, an alkyl radical with 1-6 carbon atoms or an aryl, or mixtures thereof with or without a diolefin, comprising the product obtained by reaction of a solid catalyst component of claim 3 with an Al-alkyl compound. The catalyst of claim 14 wherein the Al-alkyl compound is an Al-trialkyl. The catalyst of claim 15 for the polymerization of olefins CH₂=CHR wherein R is an alkyl radical with 1-6 carbon atoms, further comprising, in addition to the Al-trialkyl compound 2,2,6,6-tetramethylpiperidine or a silicon electron donor compound containing at least one Si-OR bond wherein R is a hydrocarbon radical.

Inventors: ALBIZZATI ENRICO, BARBE PIER CAMILLO, BARINO LUISA, GIANNINI UMBERTO, MORINI GIAMPIERO, NORISTI LUCIANO, SCORDAMAGLIA RAIMONDO, ALBIZZATI, ENRICO, BARBE', PIER CAMILLO, BARINO, LUISA, GIANNINI, UMBERTO, MORINI, GIAMPIERO, NORISTI, LUCIANO, SCORDAMAGLIA, RAIMONDO
Applicants: MONTELL NORTH AMERICA INC, MONTELL NORTH AMERICA INC.
Application year: 1989
Main classification: C08F4
IPC codes: C08F4, C08F110, C08F10