Ruthenium-phosphine complexes

Abstract: A ruthenium-phosphine complex is of formula [RUX ℓ (L) m (R-BINAP)]Y n (I) wherein R-BINAP represents a tertiary phosphine represented by wherein R represents a hydrogen atom or a methyl group; X represents a halogen atom; L represents substituted or unsubstituted benzene or acetonitrile; Y represents a halogen atom, ClO₄, PF₆, BPh₄ (wherein Ph represents a phenyl group) or BF₄; when L is substituted or unsubstituted benzene, ℓ represents 1, m represents 1, and n represents 1; and when L is acetonitrile, when ℓ is 1, then m represents 2, and n represents 1, and when ℓ is 0, then m represents 4, and n represents 2. 27 specific complexes are shown. Synthesis is by (a) RuCl₂(Ar) + BINAP in a solvent at 25 to 50°C; (b) [RuCl₂ (Ar)]₂ + Br or I salt of Li, Na or K, in water or in a mixture of water and methylene chloride and in pre­ sence of a quaternary ammonium or phosphonium halide; (c) [RuCl(Ar) BINAP]Cl + a Na, K, Li, Mg or Ag salt (MY); of ClO₄, PF₆ BPh₄ or BF ₄ , in an organic solvent; or (d) [RuCl(Ar) BINAP]Cl in an organic solvent, optionally with MY is heated at 25°C-50°C for 10-24 hours. The complex is used as catalyst in asymmetric hydrogenation, e.g. of methyl acetoacetate, and exhibits excellent catalytic activity to provide a product of high optical purity.

Description: This invention relates to a ruthenium-phosphine complex useful as a catalyst for various organic syntheses, particularly asymmetric hydrogenation. Various organic synthetic reactions using transition metal complexes as a catalyst have hitherto been developed and utilized for many purposes. In particular, there are a number of reports on asymmetric catalysts to be used in asymmetric syntheses, i.e., asymmetric isomerization, asymmetric hydrogenation, and the like. Of the reported asymmetric catalysts, metal complexes formed between metallic rhodium and an optically active tertiary phosphine are especially well known as catalysts for asymmetric hydrogenation. Such complexes typically include a rhodium-phosphine complex using 2,2′-bis(diphenylphosphino)-1,1′-binaphthyl (hereinafter abbreviated as BINAP) as a ligand as disclosed in JP-A-55-61937 (the term "JP-A" as used herein means an "unexamined published Japanese patent application"). Further, Inoue et al. report in Chemistry Letters , pp. 1007-1008 (1985) that citronellol can be obtained in an optical yield of 66% by asymmetric hydrogenation of geraniol or nerol using various rhodium-phosphine complexes. On the other hand, known ruthenium complexes, though there are not so many reports as compared with rhodium complexes, include those having BINAP or 2,2′-bis(di-p-tolylphosphino)-1,1′-binaphthyl (hereinafter abbreviated as T-BINAP) as a ligand, e.g., Ru₂Cl₄(BINAP)₂NEt₃ (wherein Et represents an ethyl group, hereinafter the same) and Ru₂Cl₄(T-BINAP)₂NEt₃ as reported in Ikariya et al., J. Chem. Soc. Chem. Commun. , p. 922 (1985), Ru(O₂CR)₂(BINAP) and Ru(O₂CR)₂(T-BINAP) (wherein R represents a lower alkyl group, a lower alkyl-substituted phenyl group, etc.) as disclosed in EP-A-245,959(JP-A-62-265293), and [RuH ℓ (R-BINAP) m ]X n (wherein R represents a hydrogen atom or a methyl group; X represents ClO₄, BF₄ or PF₆; when ℓ is 0, then m is 1, and n is 2; and when ℓ is 1, then m is 2, n is 1) as disclosed in EP-A-256,634(JP-A-63-41487). However, these conventional ruthenium complexes require complicated processes for the preparation thereof or the yields and stability of the preparation have not been satisfactory. Besides, the catalytic activity as well as duration of the activity of these complexes are still insufficient. Although metallic rhodium provides excellent complex catalysts, it is expensive due to limitations in the places and quantity of its production. When used as a catalyst component, it forms a large proportion in cost of the catalyst, ultimately resulting in an increase in cost of the final commercial products. While metallic ruthenium is cheaper than metallic rhodium and appears promising as a catalyst component for advantageous industrial application, it still has problems in achievement of precise reactions and its range of application. Therefore, it has been much desired to develop a catalyst which can be prepared easily at low cost, has high activity and durability, and catalyzes asymmetric reactions to attain high optical yields, i.e., to produce reaction products having high optical purity. As a result of extensive investigations with the purpose of meeting the above-described industrial demand, the inventors have discovered a novel ruthenium complex having high catalytic activity which can be obtained in good yield through simple operations, and which is usable either for general syntheses when the ligand thereof is optically inactive or for asymmetric syntheses when the ligand thereof is optically active. The present invention has been completed based on this finding. The present invention relates to a ruthenium-phosphine complex represented by formula (I) [RuX ℓ (L) m (R-BINAP)]Y n (I) wherein R-BINAP represents a tertiary phosphine represented by formula (II): wherein R represents a hydrogen atom or a methyl group; X represents a halogen atom; L represents substituted or unsubstituted benzene or acetonitrile; Y represents a halogen atom, ClO₄, PF₆, BPh₄ (wherein Ph represents a phenyl group) or BF₄; when L is substituted or unsubstituted benzene, ℓ represents 1, m represents 1, and n represents 1; and when L is acetonitrile, when ℓ is 1, then m represents 2, and n represents 1, and when ℓ is 0, then m represents 4, and n represents 2. In formula (I), the substituted or unsubstituted benzene ( hereinafter referred to as Ar)as represented by L is benzene which may be substituted with a C1-4 alkyl group, a C1-4 alkoxyl group, a carboalkoxyl group, a halogen atom, etc., e.g., benzene, toluene, xylene, trimethylbenzene, hexamethylbenzene, ethylbenzene, t-butylbenzene, p -cymene, cumene, methyl benzoate, methyl methylbenzoate, methyl chlorobenzoate, anisole, methylanisole, chlorobenzene, dichlorobenzene, trichlorobenzene, bromobenzene or fluorobenzene. The compound of formula (I) according to the present invention wherein L is a substituted or unsubstituted benzene nucleus can be prepared as follows. The compound wherein X and Y both represent a halogen atom (taking a chlorine atom, for instance, i.e., [RuCl(Ar)(BINAP)]Cl can be quantitatively synthesized by reacting [RuCl₂(Ar)]₂ with BINAP in a solvent, e.g., methanol, ethanol, benzene or methylene chloride or a mixture thereof, at a temperature of from 25°C to 50°C for a period of from 30 minutes to 3 hours and removing the solvent from the reaction mixture by distillation under reduced pressure. The starting compound [RuCl₂(Ar)]₂ can be prepared by the processes disclosed in, e.g., G. Wikhaus, J. Org. Chem. , Vol. 7, p. 487 (1976) or R.A. Zelonka, Can. J. Chem. , Vol. 50, p. 3643 (1972). The compound wherein X and Y both represent a bromine atom or an iodine atom, i.e., [RuBr(Ar)(BINAP)]Br or [RuI(Ar)(BINAP)]I, can be quantitatively synthesized by (i) reacting [RuCl₂(Ar)]₂ with a salt represented by formula (III): M¹Z (III) wherein M¹ represents Li, Na or K; and Z represents Br or I, in water as a solvent to obtain [RuZ₂(AR)]₂, or (ii) reacting [RuCl₂(Ar)]₂ with M¹Z in a mixed solvent of water and methylene chloride in the presence of a quaternary ammonium or phosphonium salt represented by formula (IV): R¹R²R³R⁴QX′ (IV) wherein R¹, R², R³, and R⁴ each represents an alkyl group having from 1 to 16 carbon atoms, a phenyl group or a benzyl group; Q represents a nitrogen atom or a phosphorus atom; and X′ represents a halogen atom, as a phase transfer catalyst by stirring at room temperature to obtain [RuZ₂(Ar)]₂, and then reacting the resulting [RuZ₂(Ar)]₂ with BINAP in a solvent, e.g., methanol, ethanol, benzene, methylene chloride, etc., or a mixture thereof at a temperature of from 25°C to 50°C for a period of from 30 minutes to 3 hours, followed by removing the solvent by distillation under reduced pressure. The phase transfer catalyst of formula (IV) which can be used includes those described in W.P. Weber and G.W. Gokel (translated by Iwao Tabushi and Takako Nishitani), Sokan Ido Shokubai , 1st Ed., Kagaku Dojin K.K., (Sept. 5, 1978). The compound wherein X is a halogen atom (a chlorine atom being taken as an instance), and Y represents ClO₄, PF₆, BPh₄ or BF₄ can be quantitatively obtained by, for example, adding a salt represented by formula: MY wherein M represents Na, K, Li, Mg or Ag; and Y represents ClO₄, PF₆, BPh₄ or BF₄, to a solution of [(RuCl(Ar)(BINAP)]Cl in a solvent, e.g., methanol, ethanol, acetone or methylene chloride, followed by stirring, separating the small amount of insoluble matters, and concentrating the filtrate to dryness. The compound wherein L represents an acetonitrile, and X and Y both represent a halogen atom (a chlorine atom being taken as an instance), i.e., [RuCl(acetonitrile)₂(BINAP)]Cl, can be obtained, for example, as follows. An [RuCl(Ar)(BINAP)]Cl complex is dissolved in acetonitrile, the solution is heated at from 25°C to 50°C for 10 to 24 hours, and excess of acetonitrile is removed by distillation, followed by drying to solid to obtain a crude complex, which is then recrystallized from methylene chloride to obtain the desired compound in a yield of 90% or more. Alternatively, [Ru(acetonitrile)₄(BINAP)]Y₂ can be obtained in a yield of 90% or more by dissolving a [RuCl(Ar)(BINAP)]Cl complex, for example, in a mixed solvent of acetonitrile and methanol, ethanol, acetone or methylene chloride, adding MY to the solution, heating the solution at 25°C to 50°C for 10 to 24 hours, removing the solvent by distillation, and recrystallizing the residue from methylene chloride. In the preparation of the complexes of the present invention according to any of the above-described processes, the solvent used in the synthesis reaction or recrystallization of the crude product is sometimes incorporated into finally obtained crystals. For example, the complex obtained in Example 1 hereinafter described contained double the molar quantity of ethanol used as a solvent for synthesis; and the complex obtained in Example 4 hereinafter described contained half the molar quantity of methylene chloride used for recrystallization. In other cases, for example, in Example 2 hereinafter described, the solvent used was not incorporated into the product at all. Notwithstanding, the incorporation of the solvent into the product does not give rise to any problem in the synthesis of the complex and for use as a catalyst of asymmetric hydrogenation. The ruthenium-phosphine complex thus obtained was confirmed to be a pure complex by analyses, such as spectral analysis. The complex according to the present invention is a stable compound and, when used in asymmetric hydrogenation, exhibits very high catalytic activity. In more detail, asymmetric hydrogenation rapidly proceeds by using the complex at a molar concentration of from 1/100 to 1/10000 based on a substrate to produce a desired hydrogenation product having high purity and optical purity. For example, asymmetric hydrogenation of methyl acetoacetate as a substrate in the presence of the catalyst gives methyl 3-hydroxybutyrate having a purity of 100% and an optical purity of from 97 to 99%. Thus, the ruthenium-phosphine complex according to the present invention produces very excellent results as an industrial catalyst. The present invention will now be illustrated in greater detail with reference to Examples and Use Examples, wherein percentages are by weight unless otherwise indicated. EXAMPLE 1 Synthesis of [RuCl(benzene)(S)-BINAP)]Cl (Chloro-π-benzene-[2,2′-bis(diphenylphosphino)-1,1′-binaphthyl]ruthenium Chloride) In 10 ml of 90% ethanol were dissolved 2.6 g (10 mmole) of RuCl₃·3H₂O and 10 ml (105 mmole) of 1,3-cyclohexadiene, followed by heating at 35°C for 5 hours. The precipitated crystals were collected by filtration, washed with methanol, and dried to obtain 1.87 g (yield: 75%) of [Ru(benzene)Cl₂]₂ (µ-dichloro-π-benzene-ruthenium as a reddish brown solid. In a Schlenk's tube were charged 0.33 g (0.66 mmole) of [Ru(benzene)Cl₂]₂ and 0.82 g (1.31 mmole) of (S)-BINAP. After displacing the atmosphere with argon, 150 ml of ethanol and 20 ml of benzene were added thereto, followed by heating at 50°C for 45 minutes. The reaction solution was filtered through Celite filter aid, and the filtrate was concentrated to dryness to obtain 1.14 g (yield: 90%) of [RuCl(benzene)(S)-BINAP)]Cl as a yellow solid. Melting Point: 114 to 125°C (with decomposition) Elemental Analysis for C₅₀H₃₈Cl₂P₂Ru: Calcd. (%): C 67.21, H 5.22 Found (%): C 66.48, H 4.90 The ³¹P nuclear magnetic resonance spectrum (³¹P-NMR) was determined using "JNM-GX400" manufactured by JEOL Ltd. Chemical shifts were determined using 85% H₃PO₄ as an external standard. ³¹P NMR(CDCl₃) δ ppm: 30.3 (d, J=64.6 Hz), 38.3 (d, J=64.6 Hz) EXAMPLE 2 Synthesis of [RuCl(benzene)((S)-T-BINAP)]BF₄ (Chloro-π-benzene-[2,2′-bis(di-p-tolylphosphino)-1,1′-binaphthyl]ruthenium Tetrafluorobroate) In 20 ml of methylene chloride was dissolved 0.03 g (0.15 mmole) of AgBF₄, and 0.13 g (0.14 mmole) of [RuCl(benzene)((S)-T-BINAP)]Cl prepared in the same manner as in Example 1 and 20 ml of methylene chloride were added thereto, followed by stirring for 1 hour. The reaction solution was filtered through Celite, and the filtrate was concentrated to dryness to obtain 0.13 g (yield: 95%) of [RuCl(benzene)((S)-T-BINAP)]BF₄ as a yellowish brown solid. Elemental Analysis for C₅₄H₄₆BClF₄P₂Ru: Calcd. (%): C 66.17; H 4.73 Found (%): C 65.73; H 4.48 ³¹P-NMR(CDCl₃) δ ppm: 28.4 (d, J=64.5 Hz), 36.2 (d, J=64.5 Hz) EXAMPLE 3 Synthesis of [RuCl(p-cymene)((S)-BINAP)]Cl (Chloro-π-p-cymene-[2,2′-bis(diphenylphosphino)-1,1′-binaphthyl]ruthenium Chloride) One gram of RuCl₃·3H₂O, 30 ml of 90% ethanol, and 5 ml (31 mmole) of p-mentha-1,5-diene were stirred at 45 to 50°C for 5 hours. The precipitated crystals were collected by filtration, washed with methanol, and dried to obtain 0.79 g (yield: 54%) of [Ru(p-cymene)Cl₂]₂ as an orange solid. The resulting [Ru(p-cymene)Cl₂]₂ (0.26 g, 0.43 mmole), 0.53 g (0.85 mmole) of (S)-BINAP, and 60 ml of ethanol were stirred at 50°C for 1 hour. The reaction solution was filtered through Celite, and the filtrate was concentrated to dryness to obtain 0.77 g (yield: 97%) of [RuCl(p-cymene)((S)-BINAP)]Cl as a yellowish brown solid. Elemental Analysis for C₅₄H₄₆Cl₂P₂Ru: Calcd. (%): C 69.83; H 4.99 Found (%): C 70.47; H 5.29 ³¹P-NMR(CDCl₃) δ ppm: 24.5 (d, J=62.6 Hz), 41.2 (d, J=62.6 Hz) EXAMPLE 4 Synthesis of [RuCl(acetonitrile)₂((S)-BINAP)]Cl (Chloro-bisacetonitrile-[2,2′-bis(diphenylphosphino)-1,1′-binaphthyl]ruthenium Chloride) In a 80 ml-volume Schlenk's tube was charged 0.1 g (0.11 mmole) of [RuCl(benzene)(S)-BINAP)]Cl obtained in Example 1, and 20 ml of acetonitrile was added thereto, followed by heating at 50°C for 24 hours while stirring to obtain a yellow clear solution. The solvent was removed under reduced pressure to obtain a yellow solid, which was then recrystallized from methylene chloride-diethyl ether to obtain 0.09 g (yield: 80%) of [RuCl(acetonitrile)₂((S)-BINAP)]Cl as a yellow solid. Elemental Analysis for C₄₈H₃₈N₂Cl₂P₂Ru: Calcd. (%): C 65.76; H 4.33; N 3.19 Found (%): C 65.53; H 4.69; N 3.32 ³¹P-NMR(CDCl₃) δ ppm: 51.3 (d, J=35.2 Hz), 54.4 (d, J=35.2 Hz) EXAMPLE 5 Synthesis of [RuCl(acetonitrile)₄((S)-BINAP)](BF₄)₂ (Tetraacetonitrile-[2,2′-bis(diphenylphosphino)-1,1′-binaphthyl]ruthenium-ditetrafluoroborate) In 20 ml of methylene chloride were dissolved 0.15 g (0.17 mmole) of [RuCl(benzene)(S)-BINAP)]Cl as obtained in Example 1 and 20 ml of acetonitrile, and 0.07 g (0.36 mmole) of AgBF₄ was added thereto, followed by heating at 50°C for 12 hours. The solvent was removed by distillation, and the residue was extracted with methylene chloride. The solvent was removed from the extract by distillation to obtain 0.15 g (yield: 88%) of [RuCl(acetonitrile)₄((S)-BINAP)](BF₄)₂. Elemental Analysis for C₅₂H₄₄N₄B₂F₈P₂Ru: Calcd. (%): C 58.83; H 4.18; N 5.28 Found (%): C 58.96; H 4.25; N 5.53 ³¹P-NMR(CDCl₃) δ ppm: 45.7 EXAMPLE 6 Synthesis of [RuI(p-cymene)((R)-BINAP)]I (Iodo-π-p-cymene-[2,2′-bis(diphenylphosphino)-1,1′-binaphthyl]ruthenium Iodide) In 87 ml of methylene chloride were dissolved 3.5 g (0.11 mmole) of [Ru(p-cymene)Cl₂]₂ as synthesized in Example 3 and 120 mg of tetramethylammonium iodide, and a solution of 18.3 g (110 mmole) of potassium iodide in 87 ml of water was added dropwise thereto, followed by stirring at room temperature for 16 hours. The organic layer separated was washed three times with 120 ml portions of water, and the solvent was removed by distillation, followed by drying to obtain 4.9 g (yield: 89%) of [Ru(p-cymene)I₂]₂ (µ-diiodo-π-p-cymene-rhutenium) as a deep purple solid. In a mixture of 45 ml of ethanol and 23 ml of methylene chloride were dissolved 0.25 g (0.26 mmole) of the resulting [Ru(p-cymene)I₂]₂ and 0.35 g (0.56 mmole) of (R)-BINAP, and the solution was stirred at 50°C for 1 hour. The reaction solution was filtered through Celite, and the filtrate was concentrated to dryness to obtain 0.58 g (yield: 100%) of [RuI(p-cymene)((R)-BINAP)] as a brown solid. Elemental Analysis for C₅₄H₄₆I₂P₂Ru: Calcd. (%): C 58.34; H 4.17 Found (%): C 57.96; H 3.73 ³¹P-NMR (CDCl₃) δ ppm: 24.8 (J=60.2 Hz), 41.6 (J=60.0 Hz) EXAMPLES 7 TO 25 Ruthenium-phosphine complexes of Table 1 below were synthesized in the same manner as in Examples 1 to 6, except for varying the starting materials. Analytical values of the resulting complexes are shown in Table 1. The elemental analytical values shown in Table 1 are for the products from which any solvent, if present due to incorporation during the preparation, has been removed. USE EXAMPLE 1 In a 50 ml-volume autoclave were charged 0.96 g (8.3 mmole) of methyl acetoacetate and 8 ml of methanol, and 2.4 ml (2.8x10⁻³ mmole) of [RuCl(benzene)((S)-BINAP)]Cl as obtained in Example 1 was added thereto under an argon stream, and a hydrogenation reaction was conducted at 20°C and at a hydrogen pressure of 100 kg/cm² for 50 hours. After the solvent was removed by distillation, the residue was subjected to distillation to obtain 0.7 g (yield: 73%) of methyl 3-hydroxybutyrate as a fraction having a boiling point of 63°C/10 mmHg. The resulting product was reacted with (R)-(+)-α-methoxy-α-trifluoromethyl-phenylacetyl chloride to synthesize an ester. The ester was separated into diastereomers and analyzed by high performance liquid chromatography using a column "Nuclosil® 100-3" produced by Chemco Co. (4.6 mm in diameter x 300 mm in height), a 8:2 (by volume) mixture of hexane-diethyl ether as an eluent (flow rate: 1 ml/min), and a UV detector (detection wavelength: 254 nm). As a result, the starting alcohol was found to be a mixture of 98.8% of methyl (S)-(+)-3-hydroxybutyrate and 1.2% of methyl (R)-(-)-3-hydroxybutyrate, and the optical yield was thus found to be 97.6% ee. USE EXAMPLES 2 TO 25 Methyl 3-hydroxybutyrate was prepared by conducting asymmetric hydrogenation of methyl aceto-acetate in the same manner as in Use Example 1, except for using each of the ruthenium-phosphine complexes obtained in Examples 2 to 25 as a catalyst. The results obtained are shown in Table 2 below. The present invention provides a novel ruthenium-phosphine complex exhibiting excellent performance properties as a catalyst for various organic syntheses, and particularly asymmetric hydrogenation. For example, it shows industrially superior results in selective hydrogenation of olefins as well as in catalytic activity. Further, the complex according to the present invention can be produced at lower cost as compared with the conventional rhodium catalysts, making a contribution to reduction of product price and, thus, has a high industrial value.

Claims: A ruthenium-phosphine complex represented by formula (I) [RuX ℓ (L) m (R-BINAP)]Y n (I) wherein R-BINAP represents a tertiary phosphine represented by formula (II): wherein R represents a hydrogen atom or a methyl group; X represents a halogen atom; L represents substituted or unsubstituted benzene or acetonitrile; Y represents a halogen atom, ClO₄, PF₆, BPh₄, wherein Ph represents a phenyl group, or BF₄; when L is substituted or unsubstituted benzene, ℓ represents 1, m represents 1, and n represents 1; and when L is acetonitrile, when ℓ is 1, then m represents 2, and n represents 1, and when ℓ is 0, then m represents 4, and n represents 2. A ruthenium-phosphine complex as in claim 1, wherein L represents benzene or benzene substituted with a C1-4 alkyl group, a C1-4 alkoxy group, a carboalkoxy group, or a halogen atom. A method of asymmetric hydrogenation wherein a complex as claimed in Claim 1 or 2 is used as a catalyst. A method as claimed in Claim 3, wherein methyl acetoacetate is hydrogenated to methyl 3-hydroxy-butyrate.

Inventors: KUMOBAYASHI HIDENORI, MASHIMA KAZUSHI, SAYO NOBORU, TAKAYA HIDEMASA, KUMOBAYASHI, HIDENORI, MASHIMA, KAZUSHI, SAYO, NOBORU, TAKAYA, HIDEMASA
Applicants: TAKASAGO PERFUMERY CO LTD, TAKASAGO INTERNATIONAL CORPORATION
Application year: 1989
Main classification: C07F15
IPC codes: C07C51, C07B61, C07C69, C07F15, C07C67, B01J31