Apparatus and method for shaping fiber reinforced resin matrix materials and product thereof

Abstract: A method of shaping elongated composite structures of a resin matrix reinforced with randomly broken fibers oriented in transverse and non-transverse directions with respect to the longitudinal axis of the structure is implemented by a computer aided apparatus for forming the structure. The apparatus is provided with a heated fixed forming tool (56), a means (32, 34) for stretching the structure from each end and means (44-48) associated with the forming tool for separately holding each formed component length of the structure in place against the forming tool. The formed structure is characterized by the particular orientation of the fibers in the transverse and non-transverse direction after the structure is formed.

Description: Background of the Invention This invention relates to an apparatus and a method for shaping fiber reinforced resin matrix materials. More particularly, the invention relates to an apparatus and method used to shape the material while substantially maintaining the orientation of the fibers in the material relative to each other and the product thereof. It is known that many thermoplastic resin materials can be shaped by means of various metal forming techniques, such as deep drawing, stretch forming, stamping, binding, etc. It is also known to reinforce the resin material with fibers such as glass, carbon, aramids and the like to provide higher strength, impact resistance and dimensional stability. However, the shaping processes of the prior art when applied to resin material structures that have fibers oriented in multiple directions suffer from the inability to maintain the orientation of the fibers relative to each other during the shaping of the structure. In many cases this leads to lower mechanical strength. One way to overcome this problem has been to hand lay-up the shaped structure from discrete segments of the fiber reinforced resin material, then consolidate the hand layed-up material into final form and in this manner control fiber orientation. This process is very labour intensive, time consuming and costly. EP-A-0123225 discloses a method for making high-strength composite structures of thermosetting or thermoplastic resin with reinforcements therein. A continuous longitudinally extending wet charge of resin and reinforcement is formed as an endless source and maintained under a given tension while it is advanced toward a mold cavity. A plurality of reinforcement elements is continuously placed at predetermined positions within the cross-sectional area of the wet charge and with the longitudinal reinforcements being continuously parallel to one another. The resin and the reinforcements form a composite matrix whose angular reinforcement orientation may vary ± 90° with respect to the longitudinal axis of the wet charge and the ultimate product. The reinforcements also may change directions or orientations at different levels within the cross-section area. The composite matrix is advanced into the mold cavity where it is compression molded and cured within a heated tool under low pressure without flowing of the matrix. US-A-3816044 discloses an automatic hot press for forming contoured laminated bench seats utilizing an overhead pivotable heated die to form the inside of the bench against three lower heated dies which form the outside surface of the bench. The central lower heated die is positioned against the sharply curving portion of the bench between the seat and back portions before the other lower dies so as to ensure proper forming and prevent cracking of the bench. The entire operation of the press is automatically sequenced with a pressurized air system. Summary of the Invention According to the present invention, a method has been developed which facilitates the shaping of fiber reinforced resin matrix structures from a straight stock shape and provides a method of controlling orientation of the fibers in the structure without the need to hand lay-up the structure. More specifically, the method of shaping into a predefined path a composite structure of resin matrix reinforced with fibers, said composite structure having a longitudinal axis, is one which comprises: a) defining said path as a plurality of adjoining component lengths; b) stretching said structure from each of its ends by applying a force to each end along its longitudinal axis away from said ends to shape the structure into at least one formed component length defined by said path; c) heating said structure intermediate of its ends while stretching the structure according to step (b); d) holding said one formed component length of the structure in place while stretching said structure as in step (b) to shape the structure into formed component lengths adjoining said one formed length; e) repeating step (d) to complete the formation of said structure into a predefined path; and f) cooling the structure. When the predefined path includes one or more curvilinear portions, each portion is defined as a plurality of component lengths given as dependent variables S, x, y and independent variables L, R and ϑ; where x, y are coordinates of points that generate the cam track path of the apparatus for forming the shaped structure L is the length of the unformed material S is the intermediate arc length of one of component sections R is the radius of curvature of the arc S D is the offset distance of the x,y coordinates from a line tangent to the arc S at its end point T Θ is the angular location of the coordinate of the tangent point T a) expressing x and y as a function of the independent variables L, R, D and Θ such that when S = R (90-Θ) (π/180) , then x = R cos (Θ) + (L - S) sin (Θ) + D cos (Θ) y = R sin (Θ) - (L - S) cos (Θ) + D sin (Θ) b) deriving x and y; and c) shaping said composite from a straight length fiber reinforced resin matrix material by stretching said straight length in a path defined by said x,y coordinates. Preferably the fibers are randomly broken and are oriented in transverse and non-transverse directions with respect to the longitudinal axis of the structure. The hold step (b) maintains the orientation of the fibers relative to one another within about ± 5 degrees of their orientation to the longitudinal axis of the shaped structure. In a preferred embodiment, the shapes are enclosed within thin aluminum sheeting, preferably in the range of 1/32 to 1/8 inch thick depending on the size and geometry of the part to be formed. The purpose of the aluminum sheeting covering the composite material is to maintain the integrity of the softened thermoplastic material during forming. Other materials may be used when the process conditions, such as time, temperature or pressure require them. After the part is formed, then the aluminum or other material is removed. The product is defined as an elongated composite structure shaped into a predefined path, said path having curvilinear portions, each portion being defined by a radius of curvature about a center, said structure comprising: a resin matrix reinforced with fibers, said fibers being oriented with respect to the longitudinal axis of said structure in substantially transverse and non-transverse directions, said fibers oriented in the non-transverse directions of a curvilinear portion being curved with respect to the center for the radius of that curvilinear portion, said fibers oriented in the transverse direction of a curvilinear portion being directed toward the center for the radius of curvature of that curvilinear portion. The product may involve a number of different cross sectional shapes that may be classified by the number of laminate surfaces and junctions of those surfaces. For example, an L, C, O, Z or hat section may be considered to have two laminate surfaces and no junctions, while a T or J section may be considered to have three laminate surfaces with one junction. An I or H section has four laminate surfaces with two junctions. The apparatus of this invention is defined as a computer-aided system that includes a fixed forming tool having a surface defined by the predefined path into which the fiber reinforced structure is to be formed, a means for heating the forming tool, a means for stretching the structure from each of its ends into successive component lengths of the predefined path by applying a force to each end of the structure along its longitudinal axis away from the ends as the structure is formed, and means associated with the forming tool for separately holding each formed component length of the structure in place against the forming tool. Suitable thermoplastic resinous materials which may be used as a resin matrix include, but are not limited to amorphous polyamides, polyether ketone ketones, polyether ether ketones, and amorphous or crystalline polyesters. The resin of choice is reinforced with fibers as, for example, carbon fibers, glass fibers, thermoplastic fibers and aramid fibers. In order to form certain cross sections, the interior portion of the cross sectional shape needs to be supported by a formable member that is flexible in the forming or longitudinal direction while being rigid in the supporting directions which are substantially perpendicular to the longitudinal direction and can withstand process conditions. In the preferred embodiment, this formable member is a stack of steel strips. Brief Description of the Drawings Fig. 1 is a schematic of an apparatus useful in shaping fiber reinforced resin material according to the invention. Fig. 2 is a schematic illustration of a format for calculating the cam track path of the apparatus shown in Fig. 1. Fig. 3 is a schematic block diagram of the computer controlled system for regulating the operation of the apparatus for shaping the fiber reinforced resin matrix structures of this invention. Fig. 4 is the logic flow diagram of the computer program for the operation of the apparatus. Figs. 5-12 are schematic illustrations of the steps of the operation of the apparatus of Fig. 1 in shaping a structure of the invention. Fig. 13 is a perspective view, partially broken away to show the individual plies of a straight stock structure prior to shaping. Figs. 14-17 are schematic plan views of the individual plies in Fig. 13 showing fiber orientation. Fig. 18 is a perspective view, partially broken away to show individual plies, of a shaped structure made according to the invention. Figs. 19-22 are schematic illustrations of fiber orientation in various plies of the shaped article of Fig. 18. Figs. 23-27 are enlarged cross sectional views taken along line A-A of Fig. 1 representing the forming of T, H, C, J and O or hollow shaped cross sectioned parts respectively. Fig. 24a is a broken away enlarged plan view of Fig. 24 designed to show the structure of the support member used. Description of the Preferred Embodiment The preferred embodiment of this invention provides a method for shaping a fiber reinforced resin matrix structure and, as shown in Fig. 1, the apparatus useful in performing the method generally includes: a frame 30, a pair of end clamps 32, 34 in opposed locations on the frame, two pair of cam tracks positioned at the opposed locations, only one pair 36, 38 shown, a pair of hydraulic cylinders 40, 42 pivotally connected between the frame and the clamps, a plurality of holding tools 44-48 (47, 48 now shown) attached to the frame. Each holding tool being configured to form a component length of the shaped structure. A plurality of hydraulic cylinders 50-54 are attached to the top surface of the holding tools 44-48. A forming die comprising a base tool 56 heated by electric cartridge heaters 85 (Fig. 5) (Watlow Electric Manufacturing Co., Firerod cartridge heater J10A62), fixed to the frame 30 and a cap tool 58 connected to hydraulic cylinder 60, which is fixed to frame 30, for movement toward and away from the base tool is located between end clamps 32, 34. A stock length 62 is clamped at each of its ends in clamps 32, 34 and is positioned between holding tools 44-48 and base tool 56. As best shown in Fig. 2, the path of the cam tracks 36, 38 is generated from the geometry of the final curvilinear shape desired as defined by the lower edge 62a of the final shaped component length. More particularly, when forming a shaped article in a predefined path of a plurality of component lengths, each component length being determined by dependent variables S, x, y and independent variables L, R, D and Θ wherein x,y are coordinates of points that generate the cam track path 36, 38, L is the length of the unformed material, S represents the intermediate arc length of one of the component lengths, R is the radius of curvature of the arc S, D is the offset distance of the x,y coordinates from a line tangent to the arc S at its end point T, and Θ is the angular location of the coordinate of the tangent point T. The remaining portion of the straight length is equal to L minus S. In order to properly determine the shape of the cam tracks, it is necessary to define arc length S as having zero stretch spaced a uniform distance A from the lower edge 62a. The x,y coordinates are expressed as a function of the independent variables L, R, D and Θ such that when S = R (90-Θ) (π/180) then: x = R cos (Θ) + (L - S) sin (Θ) + D cos (Θ) y = R sin (Θ) - (L - S) cos (Θ) + D sin (Θ) Referring now to Fig. 3, computer 82 (Allen Bradley programmable logic controller, Series 515, Model 1785-LT) is connected at its output terminals to a hydraulic controller 80 and a heater controller 84. The hydraulic controller 80 in turn is connected to cylinders 40, 42, 50-54 and 60. The heater controller 84 is connected to electric cartridge heater 85 located in base tool 56. Inputs to the computer include position sensors 86, 88 located on end clamps 32, 34 for the purpose of signalling when the hydraulic cylinders 40, 42 have stretched the stock length 62 to the intermediate positions corresponding to the tangent points of the individual component lengths. Additional inputs to the computer consist of pressure transducers 90-93 for the purpose of determining when sufficient holding and consolidation pressure has been achieved. Thermocouple 98 in base 56 is inputted to the heater controller 84 for the purpose of sensing the temperature and signalling the controller. The logic flow diagram (Fig. 4) illustrates the operation of the apparatus as follows: upon placement of the stock length 62, clamped into end clamps 32, 34, the sequence of operation is started. In step 100, heat is applied to the electric cartridge heaters 85 through the heater controller 84. Thermocouple 98 senses the level of the temperature and signals when the operating temperature is reached. The computer signals the hydraulic controller 80 to start the stretching operation (step 102) and clamps 32, 34 are moved in tracks 36, 38 via hydraulic cylinders 40, 42 which are attached to the respective clamps to form a first component length. When the first component length position is reached, as sensed by sensors 86, 88 signals are fed to computer 82 (step 104) which in turn signals controller 80 to actuate cylinder 52 which moves holding tool 46 against the stock length 62 to hold the formed component length in place as indicated in step 106. In the next step in the program, the computer signals hydraulic controller 80 to continue stretching until the two adjacent component lengths are formed (step 108). When the two adjacent component lengths are formed at the second stretching position as sensed again by sensors 86, 88 (step 110), signals are fed to the computer 82 which in turn signals controller 80 to actuate cylinders 51, 53 which move their respective holding tools against the stock length to hold these formed component lengths in place (step 112). In the next step in the program, the computer signals hydraulic controller 80 to continue stretching until the two final component lengths are formed (step 114). When the two final component lengths reach their final position as sensed again by sensors 86, 88 (step 116), signals are fed to the computer 82 which in turn signals controller 80 to actuate cylinders 50, 54 which move their respective holding tools against the stock length to hold the formed component lengths in place (step 118). At the actuation of the final holding cylinders, the computer signals the hydraulic controller to actuate the cap tool cylinder 60 to consolidate the final part, turns the heaters 85 off and circulates cooling fluid (in a manner not shown) through the base tool 56 as indicated by steps 120, 122 and 124. The forming steps are best shown in Figs. 5-12. Fig. 5 illustrates the initial set-up with the stock length 62 located in the forming apparatus with no force applied. The stock length 62 is clamped in position and then heat is applied via base 56. When the stock length 62 reaches the process temperature for the particular resin employed, the stock part is stretched to form the center component length (Fig. 6) by extending cylinders 40, 42 until the straight length is tangent to the arc at the end of the center component length. Once this center component is formed, the holding tool cylinder 52 is extended to move holding tool 46 to hold the component length in place (Fig. 7) while the adjacent component lengths are formed (Fig. 8) and held (Fig. 9). The final stretching occurs for the remaining component lengths (Fig. 10) and then the formed part is consolidated by the remaining holding tools 44, 48 (Fig. 11) and the cap tool 58 (Fig. 12). The stock length 62 is best described by Figs. 13-17 and is seen to consist of a cap portion 64, web portion 66 and a filler 68. This particular product as referred to above may be considered to have three laminate surfaces with one junction and one filler 68. More particularly, the three laminate portions are 66a, 66b and 64. The filler 68 is enclosed by the junction 68a. While we have described this specifically for the T section, the same descriptive arrangements apply for laminate surfaces, junctions and fillers of the other shaped structures mentioned above such as the L, C, O, Z, J, I and hat shaped sections. The plies that form the web also form the lower portion of the cap. The upper portion of the cap is formed by additional plies. The cap portion and the web portion are composed of a plurality of plies with each ply consisting of fiber reinforced resin matrix material wherein the fibers in each ply are oriented with respect to the longitudinal axis in transverse and non-transverse directions. The fibers in the non-transverse direction are randomly broken while the fibers in the transverse direction may be continuous or randomly broken. More particularly, the fibers 71 in ply 70 are oriented at 45° to the longitudinal axis, the fibers 73 in ply 72 are oriented at -45° to the longitudinal axis, the fibers 75 in ply 74 are oriented at 0° to the longitudinal axis and the fibers 77 in ply 76 are oriented at 90° to the longitudinal axis. Thus the fibers in plies 70, 72 and 74 are oriented in substantially non-transverse directions while the fibers in ply 76 are transverse to the longitudinal axis. This can more clearly be seen by referring to Figs. 14-17. Referring back to Fig. 13, a filler 68 consisting of fibers oriented at 0° direction to the longitudinal axis in a resin matrix material, is used to fill the void formed where the web intersects the cap. Referring now to Figs. 18-21, a stretch formed length is shown where in plies 70, 72, 74 the fibers 71, 73, 75 oriented in the non-transverse directions are curved with respect to the center for the radius for that particular portion of the composite structure while the fibers 77 oriented in the transverse direction in ply 76 are directed toward the center for the radius for that particular portion. It should be noted that fibers in Figs. 19-22 after shaping remain oriented with respect to each other and the longitudinal axis of the structure and thus insure the fibers are in the predicted location to provide the optimum strength for the particular application. While the preferred embodiment has been described as a composite structure in the form of a T, it is to be understood that this method may be used to an advantage to form parts that have other structural shapes. Referring to Figs. 23-27, alternate shaped cross section parts are shown along with the support members where needed. More particularly, in Fig. 23 there is shown a T-shaped cross section covered with aluminum sheeting 63 and held in place by holding tool 46 and base tool 56. Similarly in Fig. 24, an H-shaped composite structure 61 covered with aluminum sheeting 63 is held in place by holding tool 46 and base tool 56. With this particular configuration, the support members 55 are positioned in the interior portions of the H-shaped cross section. The support members comprise a plurality of stacked steel strips 57 as shown in Fig. 24a. The steel strips 57 are free to move in the longitudinal direction one with respect to the other. The support member structure is the same for Figs. 25, 26 and 27 which show C-shaped, J-shaped and hollow O-shaped configurations held in place by holding tool 46 and base tool 56. It is to be understood that support members 55 are not clamped at its ends in clamps 32 and 34 as is the stock lengths 61, 62, 65, 67 and 69. In the preferred embodiment the support 55 is disclosed as a stack of steel strips. It is to be understood that while the steel strips are preferred because they are flexible in the forming or longitudinal direction while being rigid in the supporting directions which are normally perpendicular to the longitudinal direction, any other support member which would meet these criteria would also be suitable for this purpose.

Claims: A method of shaping a composite structure (62) of a resin matrix reinforced with fibers into a predefined path, said composite structure having a longitudinal axis, said method comprising: a) defining said path as a plurality of adjoining component lengths; b) stretching said structure from each of its ends by applying a force to each end along its longitudinal axis away from said ends to shape the structure into at least one formed component length defined by said path; c) heating said structure intermediate of its ends while stretching the structure according to step (b); d) holding said one formed component length of the structure in place while stretching said structure as in step (b) to shape the structure into formed component lengths adjoining said one formed length; e) repeating step (d) to complete the formation of said structure into a predefined path; and f) cooling the structure. The method of claim 1 wherein said predefined path is curvilinear. The method of claim 1 or claim 2 wherein said force is generated by clamping each of said ends in end clamps (32, 34) and moving each end clamp along an associated cam track path (36, 38). The method of claim 3 wherein said component lengths are given as dependent variables S, x, y and independent variables L, R, D and ϑ; where: x, y are coordinates of points that generate the cam track path for forming the shaped structure L is the length of the unformed elongated composite material S is the intermediate arc length in degrees of one of the component lengths R is the radius of curvature of the arc S D is the offset distance of the x, y coordinates form a line tangent to the arc S at its end point T ϑ is the angular location of the coordinate of the tangent point T (a) expressing x and y as a function of the independent variables L, R, D and ϑ, such that when S = R (90-ϑ) (π/180) then x = R cos (ϑ) + (L - S) sin (ϑ) + D cos (ϑ) y = R sin (ϑ) + (L - S) cos (ϑ) + D sin (ϑ) (b) deriving x and y; and (c) shaping said composite from a straight length fiber reinforced resin matrix material by stretching said straight length in a path defined by said x, y coordinates. The method as defined in any one of claims 1 to 4 wherein said straight length has from two to four laminate surfaces (64, 66) and up to two junctions. The method as defined in claim 1, 2, 3 or 4 wherein said fibers (71, 73, 75, 77) are randomly broken and have a relative orientation in transverse and non-transverse directions with respect to the longitudinal axis of said structure of from 0° to 90°. The method as defined in claim 6 wherein the holding step maintains the relative orientation of the fibers during shaping. The method of claim 7 wherein the relative orientation of said fibers is maintained within ± 5 degrees. A method of shaping an elongated composite structure of a resin matrix reinforced with fibers into a predefined path according to claim 1, said composite structure having an interior portion, said structure and said interior portion having substantially parallel longitudinal axes, the method including: supporting said structure in directions substantially perpendicular to the longitudinal axis of said interior portion with a support member (55) positioned in said interior portion while performing said first stretching. A method of shaping an elongated composite structure of a resin matrix reinforced with fibers into a predefined path according to claim 1, said composite structure having an enclosed interior portion, said structure and said interior portion having coextensive longitudinal axes, the method including: supporting said structure in directions substantially perpendicular to the longitudinal axis of said interior portion with a support member (55) positioned in said interior portion while performing said stretching; holding more than one of said formed component lengths of the structure in place while performing said second stretching. The method of claim 9 or 10 wherein said support member (55) is an elongated stack of steel strips (57), said stack being flexible in the longitudinal direction while being rigid in the directions perpendicular to the longitudinal direction. A system for shaping an elongated composite structure of a resin matrix reinforced with fibers into a predefined path of successive component lengths comprising: a) a fixed forming tool having a surface defined by said predefined path in contact with said structure; b) means (85) for heating said forming tool; c) means (32, 34) for stretching said structure from each of ends into successive component lengths by applying a force to each of said ends along the longitudinal axis of the structure away from said ends as the structure is formed; and d) means (44-48) associated with said forming tool for separately holding each formed component length of the structure in place against said forming tool. The system as defined in claim 12 wherein the means for holding, the means for heating and the means for stretching are operated with aid of a computer (82). An elongation composite structure (62) shaped into a predefined path, said path having curvilinear portions, each portion being defined by a radius of curvature about a center, said structure comprising: a resin matrix reinforced with fibers (71, 73, 75, 77), said fibers being oriented with respect to the longitudinal axis of said structure in substantially transverse and non-transverse directions, said fibers oriented in the non-transverse directions of a curvilinear portion being curved with respect to the center for the radius of that curvilinear portion, said fibers oriented in the transverse direction of a curvilinear portion being directed toward the center for the radius of curvature of that curvilinear portion. The elongated composite structure of claim 14 wherein the structure is a T-shaped cross-section (64, 66). The elongated composite structure of claim 14 or 15 wherein said resin matrix is a thermoplastic resin and said fibers are randomly broken. The elongated composite structure of claim 14, 15 or 16 wherein said fibers are carbon fibers. The elongated composite structure of claim 14 wherein the structure has an unenclosed interior portion. The elongated composite structure of claim 18 wherein the said unenclosed interior portion faces away from the center of curvature of the predefined path. The elongated composite structure of claim 14 wherein the structure has a C-shaped cross-section. The elongated composite structure of claim 14 wherein the structure has a H-shaped cross-section. The elongated composite structure of claim 14 wherein the structure has a J-shaped cross-section. The elongated composite structure of claim 14 wherein the structure has an enclosed hollow cross-section. The elongated composite structure of claim 23 wherein the enclosed hollow cross-section is rounded. The elongated composite structure of claim 14 wherein the structure has from two to four laminate surfaces and up to two junctions.

Inventors: MEDWIN STEVEN JAY, MEDWIN, STEVEN JAY
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1989
Main classification: B29C53
IPC codes: B32B5, B29C51, B29C53, B29C70, B32B37, B29C43, B29K105