ALUMINA HYDRATE-CONTAINING TOOTHPASTE

Abstract: This invention relates to toothpaste containing an alumina hydrate abrasive and a source of fluoride. According to the invention, there is provided a toothpaste containing a source of fluoride ions and unmilled, precipitated alumina trihydrate as an abrasive, wherein the alumina trihydrate particles have a median particle size of at least 3 micrometres. The median particle size of the alumina trihydrate is preferably below 30 micrometres, more preferably from 5 to 20 micrometres, and most preferably 8 to 12 micrometres. It has been found that the use of an unmilled alumina trihydrate, obtained by precipitation, substantially reduces the loss of available fluoride on storage whereas the use of a milled alumina trihydrate causes significant loss of available fluoride.

Description: This invention relates to toothpaste containing an alumina hydrate abrasive and a source of fluoride ions. Toothpastes containing available fluoride, that is a source of fluoride ions which are available for protecting the user's teeth against caries, are in general use. A common constituent used as an available fluoride source is sodium monofluorophosphate. Other sources are sodium fluoride and stannous fluoride. Periodontal reagents to prevent plaque, and anti-bacteriological reagents may also be present. Toothpaste also contains a particulate abrasive such as alumina trihydrate, calcium carbonate, silica or dicalcium phosphate. The median particle size of the abrasive is generally not more than about 30 micrometres because particles having a larger size, e.g. 50 micrometres, tend to be perceived as "gritty" in texture which is undesirable in a toothpaste. As the particle size is reduced a "smoother" texture is obtained but the cleaning power of such particles becomes less. A good abrasive effect is generally not achieved with particles below about 3 micrometres. When alumina trihydrate is used as the abrasive, particles in this desired size range are generally produced by attrition milling of coarser material before it is incorporated into the toothpaste. Examples of such known toothpastes are given in GB-A-1277585, GB-A-1491211, GB-A-1537823, GB-A-1475252, GB-A-1587608, US-A-4122164, GB-A-1188353, US-A-3957968, GB-B-2009596, GB-A-1310374, GB-A-1373001, GB-A-1442395, US-A-4046872, US-A-4098878, GB-A-1560913, GB-B-2061727, and GB-A-633845. Toothpaste is often stored in its container for a period of months, or even for years before use and it has been found that the content of available fluoride in the toothpaste tends to fall on storage, particularly at elevated temperatures. It is believed that this fall is due to reaction of the fluoride source with the abrasive, whereby some of the fluoride ions are rendered inactive. This fall on storage may render the available fluoride content of a given pack of toothpaste uncertain, and to achieve the minimum desired content of available fluoride the amount of fluoride source added to the toothpaste on manufacture has to be increased. This increases the cost of the product, and addition of fluoride source beyond a certain limit may be undesirable for other reasons. It has now been found that the use of an unmilled alumina trihydrate, obtained by precipitation, substantially reduces the loss of available fluoride on storage, whereas the use of a milled alumina trihydrate causes significant loss of available fluoride. The reasons for this difference in behaviour are not fully understood but it is believed that fracture of the alumina trihydrate particles during milling produces an increased number of chemically and/or physically active sites on the particles' surfaces which appear to be responsible, at least in part, for the perceived reduction in the amount of available fluoride in toothpaste, particularly after storage. According to the present invention there is provided a toothpaste containing a source of fluoride ions and unmilled, precipitated alumina trihydrate as an abrasive, wherein the alumina trihydrate particles have a median particle size of at least 3 micrometres. The median particle size of the alumina trihydrate is preferably below 30 micrometres, more preferably from 5 to 20 micrometres, and most preferably from 8 to 12 micrometres. The content of alumina trihydrate particles may be within the range normally used for abrasives in toothpaste, generally from 20 to 60% by weight. When the abrasive particles have a relatively narrow particle size distribution a relatively low abrasive content, e.g. 20 to 50% by weight, can be used to achieve the desired toothpaste viscosity. The content of the source of fluoride ions may be within the range normally used in toothpaste, generally from 0.1 to 1% by weight. When sodium monofluorophosphate is used as the source of available fluoride it may be present in an amount of about 0.8% of the weight of the toothpaste. The toothpaste may contain other constituents which are conventionally used. A typical formulation is about 50% by weight of alumina trihydrate as abrasive, about 27% by weight of 70% w/w sorbitol syrup, about 1% by weight of sodium carboxymethyl cellulose, about 0.2% by weight of sodium saccharin, about 0.2% by weight of benzoic acid, about 1% by weight of flavour, about 1.5% by weight of a surfactant such as sodium lauryl sulphate and about 0.8% of sodium monofluorophosphate as a source of fluoride, with the remainder water. Peridontal reagents such as Hibitane (supplied by ICI plc) may also be present. The toothpaste may be made by a conventional method in which the constituents other than the surfactant and flavour are mixed in a high-speed disperser. The paste is then transferred to a slow speed mixer where the surfactant and flavour are added and the product is de-aerated. The toothpaste is then sealed in containers, such as tubes. It has been found that an alumina trihydrate having a narrow particle size distribution can be added at a lower addition level than normal milled products to achieve a paste of the correct viscosity. This gives benefits of lower paste density and improved cost effectiveness. It is also known that total and soluble soda contents of alumina trihydrate affect the retained available fluoride in toothpaste. In general the lower the total and soluble soda the higher the retained available fluoride. Thus a reduction in the amount of aluminium trihydrate content is beneficial. Preferably the particle size distribution for the alumina trihydrate particles, as defined by the ratio (d₁₀-d₉₀)/d₅₀, is less than 1.3, and desirably less than 1.0, wherein d₁₀, d₅₀ and d₉₀ are the sizes for which 10%, 50% and 90%, respectively, of the particles are larger than that size. Toothpastes according to the invention will be described by way of illustration in the following Examples. In the Examples the toothpaste formulations used are as set out in Table I. EXAMPLE 1 Samples of toothpaste were prepared by a standard method using a variety of milled and precipitated alumina trihydrate sources. The toothpaste samples were stored for 3 months at a constant temperature of 37°C and the available fluoride content, expressed as the percentage of the original fluoride content, was then measured as follows: A 10 ± 0.1 g sample of the paste was placed in a dry 150 ml beaker. Water, 40 g, was added and the mixture was stirred for 10 minutes so that no solid matter remained undispersed. The slurry was then centrifuged for 20 minutes with a force of 2,500 g. An aliquot, 5 ml, of the supernatant was transferred to a distillation flask fitted for steam distillation. Sulphuric acid (1: 1), 50 mls, was added and the flask was heated. The temperature of the solution was regulated at 160°C ± 2°C. Distillation was continued until 500 mls of distillate had been collected. A 25 ml aliquot of the distillate was transferred to a 50 ml graduated flask and was then diluted to volume with lanthanum alizarin blue. The solution was allowed to stand for 30 minutes and then the absorbance at 622 nm was measured. Total soluble fluoride was determined by reference to a calibration chart prepared using sodium fluoride standards. The results obtained are presented in Table 2. It will be seen that the fluoride retention performance of the precipitated alumina trihydrates is superior to that of the milled alumina trihydrates. EXAMPLE 2 Samples of toothpaste were prepared by a standard method using a milled and a variety of precipitated alumina trihydrate sources. The toothpaste samples were stored for 9 weeks at a constant temperature of 49°C and the available fluoride content, expressed as the percentage of the original fluoride content, was then measured as follows: The total soluble fluoride content of the paste was determined by a technique described by Cropper and Puttnam (Journal of the Society of Cosmetic Chemistry, Vol. 21, (1970), pp. 533-540). The method is based on direct conversion in acid conditions, which also effects hydrolysis of monofluorophosphate, of the fluoride into its fluorosilane derivative. This derivative is extracted into benzene, containing pentane as an internal standard, and the resultant solution analysed by gas chromatography. The results obtained are presented in Table 3. It will be seen that the fluoride retention performance of the precipitated alumina trihydrates is superior to that of the milled alumina trihydrate. It will also be noted that storage at higher temperatures leads to higher loss of available fluoride. For trihydrate sample A the loss at 37°C was 17% (Example 1), but at 49°C was 27% (Example 2), although it will be noted that the analysis methods used in the two Examples were not the same. EXAMPLE 3 Samples of toothpaste were prepared by a standard method using milled and precipitated alumina trihydrate sources. The toothpaste samples were stored for 9 weeks at a constant temperature of 49°C and the available fluoride contents, expressed as the percentage of the original fluoride content, were measured as in Example 2. The results obtained are presented in Table 4. It will be seen that the fluoride retention performance of the precipitated alumina trihydrate is superior to that of the milled alumina trihydrate. EXAMPLE 4 Samples of toothpaste were prepared by a standard method from precipitated alumina trihydrates having the particle size distributions referred to in Table 5. To achieve the same toothpaste viscosity, it was found that the loadings of alumina trihydrate were 52% for sample F and 45% for sample L. As can be seen from the results of Table 5 the alumina trihydrate having the narrower particle-size distribution as defined by the ratio (d₁₀-d₉₀)/d₅₀ gave the benefit of a lower alumina trihydrate loading and consequently a lower toothpaste density. Milled alumina trihydrates of 5 to 30 micrometres are normally manufactured from coarse precipitated material of about 60 micrometres using a fluid energy mill, see British Patent 1,537,823. Commercially available milled alumina trihydrates include those sold by BA Chemicals Ltd. under the trade mark BACO AF. Various methods can be used to prepare precipitated alumina trihydrates. For example, J. Scott (′Effect of Seed and Temperature on the Particle Size of Bayer Hydrate′, paper presented at the International Symposium on the Extractive Metallurgy of Aluminium, New York, February (1962) reported that a 10.5 micrometres precipitated alumina trihydrate can be produced by the following method: a. alumina trihydrate seed (4.1 micrometres) is obtained by wet sieving and elutriation of coarse Bayer alumina trihydrate. b. The seed at a concentration of 40 g per litre is added to sodium aluminate liquor (130 g/l Na₂O, 130 g/l Al₂O₃). c. The solution is then decomposed at 50°C. A precipitated alumina trihydrate having a median particle size of 9 micrometres is also available commercially from Nippon Light Metal Company of Japan. Although heretofore the disclosed precipitated alumina trihydrate has been described as the sole abrasive in the toothpaste composition, it can be supplemented by one or more other abrasives such as calcium carbonate. Furthermore the disclosed precipitated alumina trihydrate can be blended with milled alumina trihydrate if desired. Because of the viscosity considerations referred to previously it is desirable that any other abrasive material which is used to supplement the precipitated alumina trihydrate has a particle size and a particle size distribution within the ranges preferred for the precipitated alumina trihydrate.

Claims: 1. A toothpaste containing (i) a source of fluoride ions and (ii) unmilled, precipitated alumina trihydrate as an abrasive, wherein the alumina trihydrate particles have a median particle size of at least 3 micrometres. 2. A toothpaste according to claim 1, in which the median particle size of the alumina trihydrate is below 30 micrometres. 3. A toothpaste according to claim 2, in which the median particle size of the alumina trihydrate is from 5 to 20 micrometres. 4. A toothpaste according to claim 3, in which the median particle size of the alumina trihydrate is from 8 to 12 micrometres. 5. A toothpaste according to any one of the preceding claims having a content of alumina trihydrate particles of from 20 to 60% by weight. 6. A toothpaste according to claim 5 having a content of alumina trihydrate particles of from 20 to 50% by weight and a particle size distribution for the alumina trihydrate particles as defined by the ratio (d₁₀-d₉₀)/d₅₀ of less than 1.3. 7. A toothpaste according to claim 6 wherein the particle size distribution for the alumina trihydrate particles as defined by the ratio (d₁₀-d₉₀)/d₅₀ is less than 1.0. 8. A toothpaste according to any one of the preceding claims in which the source of fluoride ions is present in an amount of from 0.1 to 1% by weight.

Inventors: EMERY, ANTHONY ROLAND, EVANS, KENNETH ARTHUR, WILLS, KEVIN JOHN
Applicants: ALCAN INTERNATIONAL LIMITED
Application year: 1989
Main classification: A61K7
IPC codes: A61K8, A61Q11