Silane coupling agent and glass fiber product for laminates

Abstract: The present invention is directed to a glass fiber product for laminates having excellent epoxy resin impreg­ nation properties and solvent resistance, high soldering heat resistance, good heat shock resistance and low water absorption properties, and it is also directed to a silane coupling agent for providing such a glass fiber product. That is, the present invention is connected with a silane coupling agent prepared by reacting 2.3 to 4.0 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to which 4 active hydrogen atoms are bound, a silane coupling agent prepared by reaction 1.3 to 3.0 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to which 3 active hydrogen atoms are bound and to which one alkylsilyl group is bound, or a silane coupling agent prepared by reacting 0.3 to 2.0 mols of a haloalkylalkoxy­ silane with 1 mol of a diamine having N atoms to which 2 active hydrogen atoms are bound and to which 2 alkylsilyl groups are bound. In addition, the present invention is also connected with a silane coupling agent prepared by reacting the diamine with a haloalkylalkoxysilane and a halomethylstyrene. Moreover, the present invention is also connected with a glass fiber product for laminates treated with the above-mentioned silane coupling agent.

Description: The present invention relates to a novel silane coupling agent and a glass fibler product for laminates treated with the silane coupling agent. In general, a silane coupling agent has the structure in which a silicon atom simultaneously has an alkoxy group capable of reacting with the surface of an inorganic material and an organic functional group which is reactive or compatible with an organic material, and therefore the silane coupling agent is used as an adhesion improver between the organic and inorganic materials. For example, the silane coupling agents are widely utilized with the intention of improving mechanical strength, electrical characteristics, water resistance, heat resistance, adhesive properties and the like in the fields of the surface treatment of glass fibers and various inorganic fillers as well as the modification of reinforced plastics, sealants, adhesives and coating materials by adding the silane coupling agent itself to their matrix resins. Above all, the application of the silane coupling agent to the surface treatment of glass fibers for glass epoxy laminates and the like is one of applications in which some effects of the silane coupling agent can be most exerted. Examples of conventional surface treating agents suitable for the glass fibers, particularly the glass fibers for glass epoxy laminates include silane compounds such as 3-aminopropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane and 3-(N-styrylmethyl-2-aminoethylamino)propyltrimethoxysilane hydrochloride. In recent years, technical innovation makes rapid progress in the field of glass fibers, particularly glass epoxy laminates, and needless to say, these laminates are required to be excellent in epoxy resin impregnation properties and solvent resistance. Particularly, in the case that the glass epoxy laminates are used as print-circuit boards, it is demanded that they have higher heat resistance and lower water absorption properties, with the advance of soldering technique in a print-circuit board-manufacturing process and a manufacturing technique in a malti-layer print-circuit board-manufacturing process. In these days, however, the conventional silane coupling agents scarcely satisfy these requirements, and another silane coupling agent having more excellent functions is desired. On the other hand, most of the silane coupling agents presently used are high-boiling single compounds manufactured by isolation and purification. SUMMARY OF THE INVENTION An object of the present invention is to provide a glass fiber product for laminates having excellent epoxy resin impregnation properties and solvent resistance, high soldering heat resistance, good heat shock resistance and low water absorption properties. Another object of the present case is to provide a silane coupling agent used to manufacture such a glass fiber product. Inventors of the present application have intensively conducted researches to solve the above-mentioned problems, and as a result, they have found that an aminosilane compound formed by subjecting a diamine compound and a haloalkylalkoxysilane, which are raw materials, to condensation reaction in a limited ratio or another aminosilane compound formed by the addition reaction of halomethylstyrene to the condensation reaction product can be directly used in the form of various mixtures without undergoing any particular operations of isolation and purification, and that the employment of the above-mentioned aminosilane compound can solve these problems. The present invention has been achieved on the basis of this knowledge. That is, the present invention is directed to - (1) a silane coupling agent obtainable by reacting 1.4 to 2.5 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to one of which one alkylenesilyl group substituted by methoxy or ethoxy groups and optionally methyl groups is bound and to the residual bonds of which 3 active hydrogen atoms are bound. (2) a silane coupling agent obtainable by reacting a halomethylstyrene with a reaction product obtainable by reacting 1.4 to 2.5 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to one of which one alkylenesilyl group substituted by methoxy or ethoxy groups and optionally methyl groups is bound and to the residual bonds of which 3 active hydrogen atoms are bound, the amount of said halomethylstyrene being not more than 80 mol% of mol amounts given by subtracting the mols of said used haloalkylalkoxysilane from the mols of said active hydrogen of said used diamine. (3) a process for preparing a silane coupling agent described in either of the previous paragraphs (1) or (2) which comprises the step of reacting a haloalkylalkoxysilane with a diamine having N atoms to which active hydrogen atoms are bound, while a secondarily produced hydrogen halide is removed by the use of a basic material which is inert to the raw materials and the reaction product. (4) a glass fiber product for laminates treated with the silane coupling agent described in either of the previous paragraphs (1) or (2). DETAILED DESCRIPTION OF THE INVENTION A haloalkylalkoxysilane which can be used in the practice of the present invention is preferably a compound represented by the formula wherein each of R 1 and R 2 is independently a substituted or unsubstituted alkyl group, an aryl group or an alkenyl group each of said groups having 1 to 6 carbon atoms, R 3 is a straight-chain or branched alkylene group having 1 to 6 carbon atoms, n is 1, 2 or 3, and X is a halogen atom. Examples of such a haloalkylalkoxysilane compound include 3-chloropropyltrimethoxysilane, 3-chloropropyltriethoxysilane, 3-bromopropyltrimethoxysilane, 3-bromopropyltriethoxysilane, 4-chlorobutyltrimethoxysilane, 4-chlorobutyltriethoxysilane, 3-chloropropylmethyldimethoxysilane, 3-chloropropylmethyldiethoxysilane, 3-bromopropylmethyldimethoxysilane, 3-bromopropylmethyldiethoxysilane, 3-chloropropyldimethylmethoxysilane, 3-chloropropyldimethylethoxysilane, 3-bromopropyldimethylmethoxysilane and 3-bromopropyldimethylethoxysilane. Examples of the diamine mentioned above include N-2-aminoethylaminopropylmethyldimethoxysilane, N-2-aminoethylaminopropylmethyldiethoxysilane, N-2-aminoethylaminopropyltrimethoxysilane, N-2-aminoethylaminopropyltriethoxysilane, N-2-aminoethylaminopropyldimethylmethoxysilane, N-2-aminoethylaminopropyldimethylethoxysilane, N-trimethoxysilylpropyldiaminopropane, N-trimethoxysilylpropyldiaminohexane, N-trimethoxysilylpropylphenylenediamine, N-trimethoxysilylpropyldiaminobiphenyl, N-trimethoxysilylpropyldiaminodiphenylmethane and (aminoethylaminomethyl)phenethyltrimethoxysilane. Examples of the halomethylstyrene used in the present invention include chloromethylstyrene, bromomethylstyrene and iodomethylstyrene, but practically methylstyrene chloride is convenient. The reaction is carried out in a dried organic solvent which is inert to the raw materials. Examples of the solvent include lower alcohols such as methanol and ethanol, ethers such as tetrahydrofuran and dioxane, and aromatic hydrocarbons such as toluene and xylene. These solvents are preferably used in a dry state. If a large amount of moisture is contained in the solvent, the alkoxy group of the raw materials and product undergoes hydrolysis in order to form a condensate, with the result that the yield of the desired product deteriorates. The reaction between the haloalkylalkoxysilane and the diamine makes progress on the basis of dehydrohalogenation reaction between an N-H group of the amine and a C-X group (X is a halogen atom) of the haloalkylalkoxysilane. In order to obtain the excellent coupling agent, it is important that the reaction is performed sufficiently so that the conversion of the raw materials may be 100%. However, the diamine which is the raw material captures the released hydrogen halide, so that the reactivity of the diamine declines, which impedes the smooth progress of the reaction. In addition, an intermediate in the reaction and the reaction product also capture the hydrogen halide of the by-product. In consequence, when this reaction product is further reacted with the halomethylstyrene, the hydrogen halide which is reacted to the reaction product impedes the raction with the halomethylstyrene. Thus, it is necessary to remove the hydrogen halide from the diamine, the intermediate and the reaction product to which it is reacted, by a basic material inert to the diamine of the raw material, the intermediate and the reaction product. It is preferred that this basic material is inert to the raw material diamine, intermediate and reaction product and has a higher basicity than the raw material diamine or the like. Examples of the basic material include metallic alkoxides such as sodium methylate and sodium ethylate, and organic bases such as triethylamine, triethylenediamine, 1,8-diazabicyclo(5,4,0)undecene-7. In reacting the haloalkylalkoxysilane with the diamine, the haloalkylalkoxysilane is used in an amount of 1.4 to 2.5 mols per mol of the diamine. If the amount of the haloalkylalkoxysilane is less than 1.3 mols, it is impossible to obtain any silane coupling agent which can provide the glass fiber product for laminates having excellent epoxy resin impregnation properties and the above-mentioned various characteristics. When the haloalkylalkoxysilane is used in an amount more than the mol of the active hydrogen of the diamine, the unreacted haloalkylalkoxysilane remains, which is inconveniently uneconomical and which lowers the concentration of the desired effective component. In this case, it can be presumed that the unreacted haloalkylalkoxysilane is removed by distillation or the like, but this means is also inconvenient, because the step of the distillation additionally increases. Consequently, in reacting the haloalkylalkoxysilane with the diamine, it is preferred that the haloalkylalkoxysilane is used in an amoumt of 2.5 mols with respect to 1 mol of the diamine A, B or C. The start of the reaction is made by dissolving the haloalkylalkoxysilane and the diamine in the above-mentioned solvent, or adding dropwise the haloalkylalkoxysilane to the diamine. This reaction makes progress at a temperature of 60°C or more, but the preferable range of the reaction temperature is from 100 to 180°C. As the reaction proceeds, the secondarily produced hydrogen halide is reacted to the raw materials and product. Therefore, as the time of the reaction lapses, a reaction rate decreases gradually, and at last the reaction attains equilibrium. At this point of time, the basic material is added to the system in an amount corresponding to that of the secondarily produced hydrogen halide in order to remove the hydrogen halide from the raw materials and product, whereby the reaction rate can be recovered. In this way, the steps of the reaction and the removal of the hydrogen halide by the basic material are repeatedly carried out until the conversion of the raw materials has reached substantially 100%, and afterward the reaction is brought to an end. Another novel silane coupling agent comprising a composition of various compounds is a silane coupling agent prepared by reacting a halomethylstyrene with a reaction product obtained by reacting 1 mol of the diamine with 1.4 to 2.5 mols of a haloalkylalkoxysilane, the amount of the aforesaid halomethylstyrene being not more than 80% of mol amounts given by subtracting the mols of the used haloalkylalkoxysilane from the mols of the active hydrogen of the used diamine (the reaction product obtained by reacting the diamine with the haloalkylalkoxysilane in such a ratio, which is to be reacted with the halomethylstyrene, will be hereinafter referred to as "reaction product F"). In reacting the haloalkylalkoxysilane with the diamine, the haloalkylalkoxysilane is used in an amount of 1.4 to 2.5 mols per mol of the diamine. If the amount of the haloalkylalkoxysilane is less than 1.3 mols, it is impossible to obtain any silane coupling agent which can provide the glass fiber product for laminates having excellent epoxy resin impregnation properties and the above-mentioned various characteristics. Inversely, if the amount of the haloalkylalkoxysilane is more than 2.5 mols, the addition amount of the halomethylstyrene is deficient at the time of the subsequent reaction with the halomethylstyrene. The start of the reaction is made by dissolving the haloalkylalkoxysilane and the diamine in the above-mentioned solvent, or adding dropwise the haloalkylalkoxysilane to the diamine. The reaction makes progress at a temperature of 60°C or more, but the preferable range of the reaction temperature is from 100 to 180°C. As the rection proceeds, the secondarily produced hydrogen halide is reacted to the raw materials and product. Therefore, as the time of the reaction lapses, a reaction rate decreases gradually, and at last the reaction attains equilibrium, as described above. At this point of time, a basic substance is added to the system in an amount corresponding to that of the secondarily produced hydrogen halide in order to remove the hydrogen halide from the raw materials and product, whereby the reaction rate can be recovered. In this way, the two processes of the reaction and the removal of the hydrogen halide by the basic material are repeatedly carried out until the conversion of the raw materials has reached substantially 100%, and afterward the reaction is brought to an end. In consequence, the desired reaction product F is obtained. In the reaction between the reaction product F and the halomethylstyrene, the amount of halomethylstyrene is preferably not more than 80 mol% of mol amounts given by subtracting mols of the used haloalkylalkoxysilane from mols of the active hydrogen of the used diamine. If the amount of the halomethylstyrene is more than 80%, it is difficult to dissolve in water a product manufactured therefrom, when the product is used in the form of an aqueous solution. In addition, the use of too much the halomethylstyrene is practically uneconomical. The start of the reaction is given by dissolving the reaction product F in the above-mentioned solvent, and then adding dropwise the halomethylstyrene to the resulting solution. As the time of the addition lapses, the temperature of the reaction system rises gradually by exothermic heat. The reaction is performed in the temperature range of from room temperature to 100°C, preferably 30 to 80°C for a period of 1 to 10 hours (the resulting reaction product will be hereinafter referred to as "reaction product G"). In the reaction product obtained by the reaction between the haloalkylalkoxysilane and the diamine, and in the reaction products F and G, many kinds of compounds are contained. The reaction product F or the reaction product obtained by the reaction between the haloalkylalkoxysilane and the diamine is considered to be a composition of various molecules in which 0 to 4 alkoxysilylalkyl groups are bound to 1 molecule of the diamine. Furthermore, the reaction product G is considered to be a composition of various molecules in which 0 to 4 halomethylstyrenes are bound to 1 molecule of diamine contained in the reaction product F. The constitutional ratio of the various products depends upon a blend ratio of the raw materials and reaction conditions, and therefore it is necessary to optimize the constitutional ratio for each use application so as to obtain good performace. Owing to this optimization, the silane coupling agent of the present invention can characteristically adapt itself to the change in treatment conditions, when used as a surface treating agent. The silane coupling agent of the present invention is useful as the surface treating agent for inorganic materials in common with usual silane coupling agents. Examples of the inorganic material to which the silane coupling agent of the present invention can be applied include naturally occurring minerals and artificially synthesized minerals such as glass, silica, alumina, talc, kaolin clay, mica, calcium carbonate, potassium titanate, silas, aluminum hydroxide, zeolite, titanium oxide, asbestos, silicon nitride and iron oxide. In addition, the silane coupling agent of the present invention can also be applied to metals such as stainless steel, aluminum and copper which are oxidized and covered with an oxide layer. It has been found that the glass fiber product for print-circuit boards having excellent epoxy resin impregnation properties and solvent resistance, high soldering heat resistance, good heat shock resistance and low water absorption properties can be obtained by treating the glass fiber product itself with the silane coupling agent described in either one of the previous paragraph (1) or (2). The amount of the silane coupling agent used in this treatment depends upon the kind of glass fiber product, but it is from 0.2 to 3.0% (% by weight; the same shall apply hereinafter), preferably 0.5 to 2.0% in terms of the concentration of a treating solution, and in other words, the amount of the silane coupling agent is from 0.06 to 0.50%, preferably 0.10 to 0.35% in terms of its adhered amount on the glass fiber. In the surface treatment, the silane coupling agent is usually used in the form of an aqueous solution, but it can be also used in the form of a mixed solution of water and an organic solvent such as an alcohol, a ketone or a glycol ether. In that case, a pH of the solution containing the silane coupling agent is 4 or less, preferably in the range of from 2 to 4. As the organic solvent, methanol is particularly preferable, and the concentration of the silane coupling agent in the solution is preferably from 30 to 40%. The other steps for the surface treatment of the glass fiber can be carried out in a usual manner. That is, an application step is done by an immersion step or the use of a roll coater or by means of spraying or the like at ordinary temperature. As the glass fiber, E glass (non-alkali fiber glass for electric uses ) is particularly preferable, but S glass (high-strength glass), D glass (low-dielectric glass) and quartz glass can be also utilized. Furthermore, examples of the glass fiber product include glass cloth, glass tape, glass yarn, glass roving glass mat, glass paper and glass powder. The silane coupling agent of the present invention is excellent in affinity for and compatibility with thermosetting resins and thermoplastic resins. Therefore, when the surface of the glass fiber product is treated with the silane coupling agent, the affinity, i.e. adhesion between the glass fiber product and the above-mentoned matrix resin can be improved. This reason would be as follows: A general conventional silane coupling agent contains, as the main component, a compound having one silyl group [-Si(OR) 3 ] in its molecule, but the silane coupling agent of the present invention contains, as the fundamental component, the reaction product obtained by reacting the diamine with the haloalkylalkoxysilane in a specific molar ratio. That is, the silane coupling agent of the present invention is basically, for example, a silane coupling agent prepared by reacting 1.4 to 2.5 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to one of which one alkylenesilyl group substituted by methoxy or ethoxy groups and optionally methyl groups is bound and to the residual bonds of which 3 active hydrogen atoms are bound. Therefore, the silane coupling agent of the present invention contains, as the main components, the reaction product having 2 silyl groups, the reaction product having 3 silyl groups and the reaction product having the 4 silyl groups, and if the silane coupling agent of the present invention is regarded as a mixture of these reaction products, 2.4 or more silyl groups are contained in one molecule of the agent. With regard to the silane coupling agent of the present invention, when -Si(OR) 3 is hydrolyzed to -Si(OH) 3 , the group which reacts with the silanol group on the surface of the glass fiber is present 2.4 times or more as much as in the conventional silane coupling agent. Additionally, when a siloxane bond is formed, a crosslinking density in the molecular structure of the siloxane is heightened 2.4-fold or more by the reactive group which is present 2.4 times or more than in the conventional one, so that a closer network structure is formed. In consequence, water resistance and adhesive strength increase, and heat resistance also improves. If the molar ratio between the diamine and the haloalkylalkoxysilane is lower than the above-mentioned range, for example, if the molar ratio of the haloalkylalkoxysialne to the diamine having the N atoms to which 4 active hydrogen atoms are bound is less than 2.4, a sufficient effect cannot be obtained. This fact indicates that when the number of the silyl groups present in one molecule of the diamine is 2 on the average, the closer network structure can scarcely be obtained. Also in the case that the haloalkylalkoxysilane which reacts with the diamine is a compound having the formula wherein each of R 1 and R 2 is independently a substituted or unsubstituted alkyl group, an aryl group or an alkenyl group each having 1 to 6 carbon atoms, R 3 is a straight-chain or branched alkylene group having 1 to 6 carbon atoms, n is 1 , 2 or 3, and X is a halogen atom, a similar effect can be obtained as compared with the case where the silyl group is -Si(OR) 3 . The forth silane coupling agent of the present invention to which the halomethylstyrene is added has a styryl group in its molecule, and therefore this type of silane coupling agent has increased affinity for and compatibility with a matrix resin. In consequence, a greater effect can be expected. The silane coupling agent of the present invention is a mixture of the rection products in which isomers and homologues are present, and therefore the constitutional ratio of the products can be adjusted by optimizing the blend ratio of the raw materials and reaction conditions so as to adapt changes in preparation conditions of a treating agent, treatment conditions and the like at the time when the product is used as a surface treating agent. An inorganic material treated by the silane coupling agent of the present invention can be mixed with a thermo-setting resin such as epoxy resin or polyimide resin and then thermally cured, thereby obtaining a strong composite material. In particular, a glass fiber base material treated with the silane coupling agent of the present invention can have excellent affinity for and compatibility with a matrix resin as well as improved adhesion to the matrix resin. Therefore, print-circuit boards manufactured by using the glass fiber base material of the present invention are excellent in heat resistance such as soldering heat resistance or heat shock resistance, water absorption properties and solvent resistance. EXAMPLES Now, the present invention will be described in detail in reference to examples, but the scope of the present case should not be limited to these examples. In the examples and comparative examples, mols of each component in a mixture are expressed in terms of an average composition. Example 1 In a 10-liter flask the inner atmosphere of which was previously replaced with dried nitrogen were placed 1,606 g (7.23 mols) of N-2-aminoethylaminopropyltrimethoxysilane, 2,440 g (12.3 mols) of 3-chloropropyltrimethoxysilane and xylene, and reaction was then performed with stirring at 130°C for 5 hours. Next, 1,630 g of a sodium methylate solution (28% methanol solvent; in the following, this solvent was similarly used) was added dropwise thereto over about 4 hours. Afterward, the reaction was further continued for 5 hours, and 740 g of the sodium methylate solution was then added dropwise thereto again over 2 hours to perform the reaction. During this operation, vapored methanol was distilled off in order to maintain a reaction temperature. After completion of the reaction, secondarily produced sodium chloride was removed from the system, whereby a light brown reaction solution was obtained. This reaction solution was then analyzed by gas chromatography, and it was confirmed that the raw materials were consumed up. According to silver nitrate titration, it was found that the amount of a chlorine atom was 240 ppm, which means that most of the sodium chloride by-product was removed therefrom. Furthermore, methanol and xylene were removed from this reaction solution in order to obtain a reaction product. The latter was then analyzed by NMR, and it was confirmed that the product had the following structure. Results of NMR analysis: Intensity Ratio (ppm) Found Calcd. Si-C H 2 - 0.6 2.0H 2.0H Si-CH 2 -C H 2 - + NH 1.5 2.7H 2.5H SiCH 2 CH 2 -C H 2 - + NC H 2 C H 2 N 2.4 3.8H 3.5H Si-O-C H 3 3.5 8.5H 9.0H Structural formula: wherein m + n = 2.7 . Example 2 In a 10-liter flask the inner atmosphere of which was previously replaced with dried nitrogen were placed 1,700 g (8.25 mols) of N-2-aminoethylaminopropylmethyldimethoxysilane, 2,110 g (11.5 mols) of 3-chloropropylmethyldimethoxysilane and xylene, and reaction was then performed with stirring at 130°C for 5 hours. Next, 1,560 g of a sodium methylate solution was added dropwise thereto over about 4 hours. Afterward, the reaction was further continued for 5 hours, and 667 g of the sodium methylate solution was then added dropwise thereto again over 2 hours to perform the reaction. During this operation, vapored methanol was distilled off in order to maintain a reaction temperature. After completion of the reaction, secondarily produced sodium chloride was removed from the system, whereby a light brown reaction solution was obtained. This reaction solution was then analyzed by gas chromatography, and it was confirmed that the raw materials were consumed up. According to silver nitrate titration, it was found that the amount of a chlorine atom was 210 ppm, which means that most of the sodium chloride by-product was removed therefrom. Furthermore, methanol and xylene were removed from this reaction solution in order to obtain a reaction product. The latter was then analyzed by NMR, and it was confirmed that the product had the following structure. Results of NMR analysis: Intensity Ratio (ppm) Found Calcd. Si-C H 3 0.1 2.9H 3.0H Si-C H 2 - 0.6 2.0H 2.0H Si-CH 2 -C H 2 - + NH 1.5 2.8H 2.7H SiCH 2 CH 2 -C H 2 - + NC H 2 C H 2 N 2.4 3.6H 3.7H Si-O-C H 3 3.5 5.7H 6.0H Structural formula: wherein m + n = 2.4 . Examples 3 and 4, Comparative Example 1 The same procedure as in Example 1 was repeated with the exception that amounts of the raw materials were changed as shown in Table 1, in order to obtain reaction products. With regard to these reaction products, analyzed values of a chlorine atom by silver nitrate titration and proton ratios measured by NMR analysis are set forth in Tables 2 and 3, respectively. Moreover, a structural formula is also shown hereinafter. Raw Material Example 3 Example 4 Comp. Ex. 1 3-Chloropropyltrimethoxysilane 2,440g 2,440g 2,440g (12.3) (12.3) (12.3) N-2-Aminoethylaminopropyltrimethoxysilane 1,950g 1,365g 2,730g (8.8) (6.15) (12.3) Note: A value in each pair of parentheses denotes mols. Example 3 Example 4 Comp. Ex. 1 Content of Cl (ppm) 400 570 410 Structural formula: wherein in the reaction product of Example 3, m + n = 2.4 , in the reaction product of Example 4, m + n = 3.0 , and in the reaction product of Comparative Example 1, m + n = 2.0 . (Intensity Ratio) (ppm) Reaction Product in Example 3 Reaction Product in Example 4 Reaction Product Comp. Example 1 Found Calcd. Found Calcd. Found Calcd. Si-C H 2 - 0.6 2.1H 2.0H 2.0H 2.0H 2.0H 2.0H Si-CH 2 -C H 2 - + NH 1.5 2.6H 2.7H 2.5H 2.3H 3.1H 3.0H Si-CH 2 CH 2 -C H 2 - + NC H 2 C H 2 N 2.4 3.9H 3.7H 3.4H 3.3H 4.1H 4.0H Si-O-C H 3 3.5 8.9H 9.0H 8.7H 9.0H 8.8H 9.0H Example 5 In a 10-liter flask the inner atmosphere of which was previously replaced with dried nitrogen were placed 2,250 g (4.52 mols) of the methanol-free and xylene-free reaction product (reaction product F) obtained in Example 1 and 2,250 g of methanol, and while the resulting mixture was maintained at 50°C, a mixed solution of 690 g (4.52 mols) of chloromethylstyrene and 690 g of methanol was added dropwise thereto over 4 hours. Afterward, the reaction was performed with at the same temperature for 10 hours. After completion of the reaction, the resulting reaction product was analyzed by gas chromatography, and it was confirmed that the raw materials were consumed up. Moreover, this reaction solution was then subjected to silver nitrate titration, and it was found that 98% or more of a chlorine atom derived from chloromethylstyrene was converted into hydrochloric acid. Examples 6, 7 and 8 All the same procedure as in Example 5 was repeated with the exception that each ratio of materials was changed as shown in Table 4, in order to obtain reaction products. Each reaction product was then analyzed by gas chromatography, and it was confirmed that most of the raw materials were consumed up. Moreover, each reaction solution was then subjected to silver nitrate titration, it was found that 98% or more of a chlorine atom derived from chloromethylstyrene was converted into hydrochloric acid. Material Example 6 Example 7 Example 8 Reaction Product F in Example 1 2,400 g 2,400 g - (4.82) (4.82) - Reaction Product F in Example 2 - - 2,400 g - - (5.83) Methanol (for dissolving reaction product F) 2,400 g 2,400 g 2,400 g - - - Chloromethylstyrene 660 g 150 g 403 g (4.33) (0.98) (2.64) Methanol (for dissolving chloromethylstyrene) 660 g 150 g 403 g - - - Molar Ratio (%) of Chloromethylstyrene to Remaining Active Hydrogen of Reaction Product F 69.1 15.6 28.3 Note: The value in each pair of parentheses denotes mol or mols. Example 9 Pieces of glass cloth were treated with the silane coupling agents obtained in Examples 1 to 8 and the reaction products obtained in Comparative Example 1, and epoxy prepregs were made of the treated pieces of glass cloth. Afterward, epoxy laminates were prepared from the epoxy prepregs. Comparative Examples 2, 3 and 4 For comparison, epoxy resin laminates were prepared in like manner, using γ-glycidoxypropyltrimethoxysilane (trade name S510 made by Chisso Corp.), 3-(N-styrylmethyl-2-aminoethylamino)propyltrimethoxysilane hydrochloride and N,N' -bis-(trimethoxysilylpropyl)ethylenediamine. They are respectively comparative examples 2, 3 and 4. Afterward, the respective epoxy resin laminates were evaluated, and the results are set forth in Table 5. In the present invention, performances of the products were evaluated as follows: Treatment of Glass Cloth Each of the reaction products obtained in Examples 1, 2, 3 and 4 as well as Comparative Example 1 was dissolved in methanol to prepare a solution having a solid content of 50%. Furthermore, the compositions obtained in Examples 5 to 8, γ-glycidoxypropyltrimethoxysilane and N,N'-bis(trimethoxysilylpropyl)ethylenediamine were used directly without any treatment. The compound 3-(N-styrylmethyl-2-aminoethylamino)propyltrimethoxysilane hydrochloride was used in the form of a methanol solution in which a solid content was 40%. The above-mentioned silane coupling agent was dissolved in distilled water a pH of which was previously adjusted to 4 with acetic acid, in order to prepare a solution having a solid content of 0.5% by weight. Each of γ-glycidoxypropyltrimethoxysilane and N,N'-bis(trimethoxysilylpropyl)ethylenediamine was dissolved in distilled water a pH of which was previously adjusted to 4 with acetic acid, in order to prepare a solution in which a solid content was 0.5% by weight. Moreover, 3-(N-styrylmethyl-2-aminoethylamino)propyltrimethoxysilane hydrochloride was dissloved in distilled water a pH of which was previously adjusted to 2.5 with formic acid, in order to prepare a solution having a solid content of 0.5% by weight. Each piece of heat cleaned glass cloth (glass fiber fabric made by Nitto Boseki Co., Ltd.; trade name WEA-18K) was immersed in each of the above-mentioned solutions and then squeezed by squeeze rolls, followed by drying at 110°C for 10 minutes. Preparation of Laminate Specimens Pieces of surface-treated glass cloth were impregnated with G-10 type epoxy resin (trade name Epicoat 1001 made by Shell Petrochemical Co., Ltd.) and then dried at 130°C for 15 minutes in order to form prepregs. Eight sheets of these prepregs were superposed upon each other, and these prepregs were then sandwiched between two copper foils. Afterward, the sandwiched prepregs were heated at 175°C for 60 minutes under a load of 30 kg/cm 2 so as to perform molding. The copper foils were then removed therefrom by etching, thereby preparing specimens. (1) Boiling Water Absorption Rate In accordance with a test procedure of JIS C-6481, each laminate specimen was boiled for a period of 5 to 20 hours, and afterward water absorption rate was measured. (2) Soldering Heat Resistance Test Each laminate specimen was boiled in a pressure cooker at 133°C and then immersed in a solder bath at 280°C for 20 seconds. After the specimen was taken out therefrom, blister or peeling on the specimen were observed. A boiling time until the occurrence of these drawbacks was regarded as a soldering heat resistance time. (3) Heat Shock Resistance Each laminate specimen was immersed in liquid nitrogen for about 1 minute, and immediately it was then floated on a solder bath at 280°C. Afterward, damages on the specimen were observed, and evaluation was made on the basis of the following standards. o ○ No damages were observed. O Spot-like damages occurred slightly. ▵ A great many spot-like damages occurred. X Spot-like damages occurred all over the surface. (4) Resin Impregnation Characteristics (prepreg) Resin impregnation states were observed, and evaluation was made on the basis of the following standars. o ○ Transparency was very good. O Transparency was good. ▵ Transparency was slightly bad. X Transparency was bad. (5) Methylene Chloride Resistance In accordance with JIS C-6481, each laminate specimen was immersed in methylene chloride at 20°C for 1 hour, and evaluation was then made by observing the appearance of the specimen. As shown in Table 5, the products prepared in the respective examples regarding the present invention have more excellent results than the products prepared in the respective comparative examples, particularly 3-(N-styrylmethyl-2-aminoethylamino)propyltrimethoxysilane hydrochloride which is presently often used as a silane coupling agent for print-circuit boards, in all points of water absorption, soldering heat resistance, heat shock resistance and methylene chloride resistance.

Claims: A silane coupling agent obtainable by reacting 1.4 to 2.5 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to one of which one alkylenesilyl group substituted by methoxy or ethoxy groups and optionally methyl groups is bound and to the residual bonds of which 3 active hydrogen atoms are bound. A silane coupling agent obtainable by reacting a halomethylstyrene with a reaction product obtainable by reacting 1.4 to 2.5 mols of a haloalkylalkoxysilane with 1 mol of a diamine having N atoms to one of which one alkylenesilyl group substituted by methoxy or ethoxy groups and optionally methyl groups is bound and to the residual bonds of which 3 active hydrogen atoms are bound, the amount of said halomethylstyrene being not more than 80 mol% of mol amounts given by subtracting the mols of said used haloalkylalkoxysilane from the mols of said active hydrogen of said used diamine. A silane coupling agent according to Claim 2, wherein said halomethylstyrene is chloromethylstyrene. A silane coupling agent according to any preceding Claim, wherein said haloalkylalkoxysilane is a compound represented by the formula wherein each of R 1 and R 2 is independently a substituted or unsubstituted alkyl group, an aryl group or an alkenyl group having 1 to 6 carbon atoms, R 3 is a straight-chain or branched alkylene group having 1 to 6 carbon atoms, n is 1, 2 or 3, and X is a halogen atom. A process for preparing a silane coupling agent according to any preceding Claim, which comprises the step of reacting a haloalkylalkoxysilane with a diamine having N atoms to which active hydrogen atoms are bound, while a secondarily produced hydrogen halide is removed by the use of a basic material which is inert to said raw materials and said reaction product. A glass fiber product for laminates treated with a silane coupling agent according to any of Claims 1-4.

Inventors: KAKIUCHI HIDEAKI, MURAKOSHI MOTOHARU, OHGUSHI MASUHITO, SAWAI TOSHIYA, SUZUKI YOSHIHARU, WAKETA HIDEHARU, WATANABE KENICHI, KAKIUCHI,HIDEAKI, MURAKOSHI, MOTOHARU, OHGUSHI, MASUHITO, SAWAI, TOSHIYA, SUZUKI, YOSHIHARU, WAKETA, HIDEHARU, WATANABE, KENICHI
Applicants: CHISSO CORP, NITTO BOSEKI CO LTD, CHISSO CORPORATION, NITTO BOSEKI CO., LTD.
Application year: 1989
Main classification: C07F7
IPC codes: C09D7, C08K9, C09J11, H05K1, B32B17, C03C25, C07F7, C09C3