Process for preparing superconductor of compound oxide of Bi-Sr-Ca-Cu system

Abstract: A compound oxide superconductor represented by the general formula: Bi 4+d (Sr 1-x , Ca x ) m Cu n O p+y in which, "d" is an amount of excess bismuth and satisfies a range of 0 < d ≦ 1.2, "m" is a number which satisfies a range of 6 ≦ m ≦ 10, "n" is a number which satisfies a range of 4 ≦ n ≦ 8, "p" = 6 + m + n, "x" is a number which satisfies a range of 0 < x < 1, and "y" is a number which satisfies a range of -2 ≦ < y ≦ +2.

Description: Background of the Invention Field of the Invention The present invention relates to a process of preparing a thin film of a superconductor of bismuth-containing compound oxide, more particularly, a superconductor of compound oxide of Bi-Sr-Ca-Cu system improved in the critical current density (Jc). Description of the related art The critical temperature "Tc" of superconductivity could not exceed 23.2 K of Nb 3 Ge which was the the highest Tc for the past ten years. The possibility of an existence of new types of superconducting materials having much higher Tc was revealed by Bednorz and Müller who discovered a new oxide type superconductor in 1986 (Z. Phys. B64, 1986 p 189). The new type compound oxide superconductor discovered by Bednorz and Müller is represented by [La,Sr] 2 CuO 4 which show such higher Tc as 30 K which are extremely higher than known superconducting materials. It was also reported that C. W. Chu et al. discovered, in the United States of America, another superconducting material so called YBCO type represented by YBa 2 Cu 3 O 7-x having the critical temperature of about 90 K in February 1987 (Physical Review letters, Vol. 58, No. 9, p 908). It had been known that certain compound oxides containing bismuth exhibit the property of superconductivity. For example, U. S. Patent No. 3,923,315 disdoses Ba-Pb-Bi type compound oxide which shows superconductivity and Japanese patent laid-open No. 60-173,885 disdoses that Ba-Bi type compound oxides also show superconductivity. These superconductors, however, possess rather low transition temperatures of about 10 K and hence usage of liquidized helium (boiling point of 4.2 K) as cryogen was indispensable to realize superconductivity. Maeda et al reported the other type new bismuth-containing superconducting material of Bi-Sr-Ca-Cu-O system (Japanese Journal of Applied Physics. Vol 27, No. 2, p 1209 to 1210). Bismuth type compound oxides are chemically much stable than the abovementioned YBCO type compound oxide and have such a very important merit that high Tc superconductors of higher than 100 K can be realized without using rear earth elements as a constituent element so that the production cost can be reduced. The above-mentioned new types superconducting materials were obtained firstly in a bulk form of sintered block which was obtained by a solid reaction or sintering technique from a powder mixture of oxides and/or carbonates of constituent metal elements which have predetermined atomic ratios. At the present, it is thought that thin films of these material are much useful in actual uses. Such thin films can be deposited on a substrate by physical vapour deposition (PVD) technique such as RF sputtering, vacuum deposition, ion-plating or MBE or chemical vapor deposition (CVD) technique such as thermal CVD, plasma CVD, photo-CVD or MOCVD. Usually, the thin films are prepared by RF sputtering technique by using a sintered mass as a target. It is also a general practice to heat-treat the sintered blocks or thin films in oxygen-containing atmosphere to adjust the oxygen deficiency in crystals of which sintered block or thin films are composed. The sintered blocks or thin films prepared by the conventional process, however, possessed too low critical current density (Jc) to be used as a material for thin film devices. In fact, the critical current density of the thin film of Bi-Sr-Ca-Cu system obtained heretofore was about 10,000 A/cm 2 at most although its critical temperature (Tc) was as high as more than 100 K. The present inventor found in the course of experiments that the superconducting property, particularly the critical current density (Jc) can be improved remarkably if the amount of bismuth is increased excessively with respect to the stoichiometrical amount and the present invention was completed. Therefore, an object of the present invention is to overcome the problem of the conventional process and to provide a superconductor of bismuth-containing compound oxide, more particularly, Bi-Sr-Ca-Cu system compound oxide improved in the critical current density (Jc). Summary of the Invention The superconducting compound oxide produced according to the present invention is a compound oxide system having the following general formula: Bi 4+d Sr 4 Ca 4 Cu 6 O 20+y in which, 0 < d ≦ 1.2 and -2 ≦ < y ≦ +2. This compound oxide system consists of two stratified layers each having an identical chemical composition but being offset to each other, so that this system can be expressed also by the following general formula: Bi 2+d/2 Sr 2 Ca 2 Cu 3 O 10+y/2 in which "d" and "y" have the same definition as above. The superconductor produced according to the present invention is preferably in a form of thin film deposited on a substrate but can be also a block or a pre-shaped article such as coil or a ring. Preparation of the superconductor The superconductor produced according to the present invention can be prepared by the conventional techniques. A bulk-form superconductor according to the present invention can be prepared by sintering a material powder mixture containing constituent elements such as oxides and/or carbonates whose atomic ratios of constituent elements are adjusted in such a manner that the resulting sintered mass has the composition defined by the present invention. A thin film form superconductor produced according to the present invention can be prepared by the conventional PVC (physical vapour deposition) such as RF magnetron sputtering, vacuum deposition, ion-plating and MBE or by the conventional CVD (chemical vapour deposition) such as thermal CVD, plasma CVD, photo CVD and MOCVD. When RF magnetron sputtering, vacuum deposition or ion-plating method is used as the physical vapour deposition technique, a vapour source or a target can be composed of elemental metals, alloys and/or their compounds such as oxides or carbonates. The vapour source or the target is preferably a sintered mass which is prepared by powder-sintering technique of a material power mixture comprising metal elements and/or their compounds such as oxides, carbonates and fluorides or a sintered powder which is obtained by pulverizing the sintered mass. The vapour source or the target can be also divided into a plurality of segments. In the case of the molecular beam epitaxy (MBE), elemental metals of Bi, Sr, Ca and Cu or their compounds such as their oxides are evaporated by means of a K-cell or an ion beam gun. In this case, oxygen is supplied, if necessary, separately or additionally into an evaporation atmosphere. In any case, the atomic ratios of metal elements contained in the vapour source or the target are adjusted according to difference in the evaporation rate as well as difference in adsorption of metal elements to the substrate in such a manner that the resulting thin film has the composition defined by the present invention. In practice, the atomic ratio of bismuth in the vapour source or the target is increase by a range defined above comparing to the conventional value. In a preferred embodiment, the superconductor produced according to the present invention is prepared in a form of a thin film by RF magnetron sputtering. In the RF magnetron sputtering, the sputtering gas pressure is preferably selected in a range of 1 x 10 -2 to 1 x 10 -1 Torr and sputtering gas is preferably a mixture of Ar gas and O 2 gas in which the proportion of O 2 gas is preferably 10 to 60 % by volume. The substrate on which the thin film of compound oxide is deposited is preferably a single crystal of MgO, ZrO 2 , SrTiO 3 , LiNbO 3 , LiTaO 3 , LaAlO 3 , LaGaO 3 or the like. It may be used also LiAlO 3 , LiCaO 3 , KTaO 3 , CaF 2 , BeF 2 , CSZ, YSZ or even silicon. When a single crystal of silicon is used as the substrate, a buffer layer of MgO or ZrO 2 is preferably interposed between the compound oxide layer and the substrate. The superconductor obtained by the process according to the present invention show crystalline anisotropy in electric resistance, so that the current passing along a direction which is in parallel to a plane defined by a-axis and b-axis of the crystal show a very high critical current density, while the current passing along c-axis is relatively lower. Therefore, it is preferable to give a desired orientation of crystal to the thin film. For example, when the thin film of the compound oxide is deposited on (001) plane of a single crystal of MgO or SrTiO 3 , the c-axis of the crystal of the thin film deposited is oriented perpendicular or nearly perpendicular to a surface of the thin film, so that the critical current density (Jc) along the surface is improved. In special applications, it is possible to use {110} plane of the substrate of SrTiO 3 in order to orient the c-axis of the crystal of the thin film deposited in parallel to the surface so that higher current density is obtained to the direction of depth. The substrate made of a single crystal of MgO or SrTiO 3 are preferable because their thermal expansion coefficient is similar to that of the compound oxide and hence the thin film of the compound oxide doesn't receive serious thermal shock or stress by heat history caused by heat and cool of the substrate. The substrate is preferably heated during the sputtering at a temperature between 670 and 750°C, preferably between 670 and 720°C, more preferably between 680 and 710°C. The high-frequency power applied to the target is selected preferably between 0.064 and 1.27 W/cm 2 and the deposition rate is selected preferably between 0.05 to 1 Å/min. It is also preferably to heat-treat or anneal the resulting thin film at a temperature between 870 and 910°C. Particularly, if the substrate temperature during the sputtering is outside the range mentioned above, the critical current density of the resulting thin film drops sharply. The heat-treatment or post-annealing is also very effective to improve the critical current density. This heat-treatment is carried out preferably in oxygen-containing atmosphere or in oxygen stream. Since the annealing temperature is a very important factor, the annealing temperature should be maintained between 870 and 910 °C, preferably between 880 and 905 °C for a predetermined time duration, for example between 10 minute and 5 hours. The superconducting properties of the thin film will become worse if the thin film is heat-treated outside the above-mentioned conditions. The thin film of Bi-Sr-Ca-Cu system prepared under the above-mentioned conditions shows remarkably improved critical current density (Jc) without spoiling the high critical temperature (Tc) which is inherent to this system compound oxide, so that the thin film prepared by the process according to the present invention can be used advantageously to fabricate a variety of superconducting devices induding Josephson device which functions above a boiling point of liquid nitrogen. In fact, development of high Tc and high Jc superconductor is demanded in order to realize Josephson device in which quantum efficiency is observed macroscopically when an electric current is passed through a weakjunction arranged between two superconductors. The tunnel junction type Josephson device is also expected to be a high-speed and low-power consuming switching device owing to a smaller energy gap of the superconducting material. High Tc and high Jc superconductor is demanded also in the field of ultra high sensitive sensors for detecting magnetic filed, micro wave or radiation. Development of the superconducting devices such as high-speed logic units or of no power-loss wiring materials is also demanded in the field of high-speed computers in which the power consumption per unit area is reaching to the upper limit of the cooling capacity with increment of the integration density in order to reduce energy consumption. The superconductor produced according to the present invention can be used as a material in these applications. Brief Description of the drawings FIG. 1 to 5 are respective X-ray diffraction charts of thin films of Sample No 1 to No. 5 prepared in Example. Now, the present invention will be described with reference to Example, but the scope of the invention should not be limited to the Example. Example Five thin film samples of superconductor of Bi-Sr-Ca-Cu system compound oxide were prepared by RF magnetron sputtering technique. In order to prepare each target used in the RF-magnetron sputtering, commercially available powders of Bi 2 O 3 , SrCO 3 , CaCO 3 and CuO were mixed intimately in such proportions that the resulting powder mixtures in each five powder samples had the atomic ratios of elements of Bi : Sr: Ca : Cu as following: Powder sample 1: Bi : Sr: Ca : Cu = 1.4 : 1.0 : 1.0 : 1.5 Powder sample 2 : Bi : Sr: Ca : Cu = 1.5 : 1.0 : 1.0 : 1.5 Powder sample 3 : Bi : Sr : Ca : Cu = 1.6 : 1.0 : 1.0 : 1.5 Powder sample 4 : Bi : Sr: Ca : Cu = 1.7 : 1.0 : 1.0 : 1.5 Powder sample 5 : Bi : Sr: Ca : Cu = 1.8 : 1.0 : 1.0 : 1.5 Then, each powder sample was sintered at 800 °C for 8 hours to obtain sintered mass of Bi-Sr-Ca-Cu compound oxide which was pulverized. The resulting each sintered powder was used, as a powder target, in each sputtering. As a substrate on which the thin film was deposited, a single crystal of MgO was used and the thin film was deposited on {110} plane of the MgO substrate. RF magnetron sputtering was effected under the following common condition: Substrate temperature 690 °C Sputtering gas pressure 2 x 10 -2 Torr Sputtering gas a mixed gas of Ar and O 2 (O 2 /Ar+O 2 ) = 0.2 (vol) RF-frequency power 50 W (0.64W/cm 2 ) Each thin film was deposited up to a thickness of 2,000 Å. The resulting thin films were annealed at 900 °C for 1 hour in oxygen gas of 1 atm. It was confirmed that all thin films (Sample No. 1 to No. 5) obtained were superconductors by resistance measurement in which the MgO substrates having the thin films were dipped in liquid helium in a cryostat at 8 K and the temperature was elevated gradually to determine a critical temperature (Tc) where the thin film showed normal resistance. The critical temperatures (Tc) determined are summarized in Table 1. The critical current density was determined at 77.3 K by the conventional four probe method and compositions of the thin films were determined by ICP. These results are also summarized in Table 1. Fig. 1 to Fig. 5 show X-ray diffraction charts obtained from the thin films (Sample No. 1 to No. 5). Fig. 2 to Fig. 4 reveal that the thin films of Sample No. 2 to No. 4 are c-axis oriented films each consists of so-called 2-2-2-3 phase alone. To the contrary, the thin films of Sample No. 1 and No. 5 contain also so-called 2-2-1-2 phase which is a lower superconducting phase. Sample No. Composition of superconducting thin film Critical temperature (K) Critical current density (A/cm 2 at 77.3K) 1 Bi 2 Sr 2 Ca 2 Cu 3 O 10-δ 92 1.2 x 10 4 2 Bi 2.2 Sr 2 Ca 2 Cu 3 O 10-δ 103 5.2 x 10 5 3 Bi 2.4 Sr 2 Ca 2 Cu 3 O 10-δ 102 1.8 x 10 6 4 Bi 2.6 Sr 2 Ca 2 Cu 3 O 10-δ 100 3.7 x 10 5 5 Bi 2.8 Sr 2 Ca 2 Cu 3 O 10-δ 88 2.3 x 10 4 (Sample No. 1 and No. 5 are comparative)

Claims: A process of preparing a superconducting thin film of compound oxide of Bi, Sr, Ca and Cu on a substrate by a physical vapour deposition technique in oxygen-containing atmosphere, characterized in that atomic ratios of Bi, Sr, Ca and Cu in a vapour source or a target used in the physical vapour deposition technique are adjusted in such a manner that the deposited thin film has a composition represented by the general formula: Bi 4+d Sr 4 Ca 4 Cu 6 O 20+y in which "d" is a number which satisfies a range of 0.4 ≤ d ≤ 1.2, "y" is a number which satisfies a range of -2≤y≤+2; and said substrate is heated at a temperature between 670 and 750°C during the physical vapour deposition. The process set forth in claim 1, characterized in that the thin film obtained by the physical vapour deposition is further heat-treated at a temperature between 870 and 910°C. The process set forth in claim 2, characterized in that the heat-treatment is effected in oxygen containing atmosphere or in oxygen gas stream. The process set forth in any one of claims 1 to 3, characterized in that said vapour source or target is a sintered mass of a compound oxide of Bi, Sr, Ca and Cu. The process set forth in any one of claims 1 to 4, characterized in that said substrate is a single crystal of MgO. The process set forth in claim 5, characterized in that the thin film is deposited on {100} plane or {110} plane of a single crystal of MgO. The process set forth in any one of claims 1 to 6, characterized in that said physical vapour deposition is sputtering.

Inventors: HARADA KEIZO, HIGAKI KENJIRO, ITOZAKI HIDEO, YAZU SHUJI, HARADA, KEIZO, HIGAKI, KENJIRO, ITOZAKI, HIDEO, YAZU, SHUJI
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1989
Main classification: H01L39
IPC codes: C23C14, H01L39, C23C16, C04B35