Fast-curve polyurethane sealant composition containing silylsubstituted piperazine accelerators

Abstract: One-component, moisture-curable sealant compositions having fast cure times comprise a mixture of a silane-­ capped polyurethane polymer, an aminosilane cross-linking agent, and a silyl-substituted piperazinyl accelerator.

Description: This invention relates to room temperature moisture-curable polymer sealant compositions. More particularly, this invention concerns one-part room temperature curable polyurethane sealant compositions containing silyl-substituted piperazinyl accelerating agents having improved cure rates. Sealants are comprised of pigmented or unpigmented synthetic elastomeric polymers which, in the uncured state, constitute pourable or easily extrudable putty-like mastics. When cured, the sealants are transformed into elastomeric materials which have viscoelastic properties and can react to the relative motion of the structural elements which the sealant connects and seals. They also form a tight barrier against moisture, gases and chemicals. Such sealants find a wide variety of applications in the building trades industry and the automotive industry. In the latter case they are widely used to seal fixed window panels and taillight glass panels to coated auto, truck, and bus bodies. Such sealants include compositions based on polysiloxane polymers as well as others which include polyurethane or polyacrylate polymers. Additionally, modern sealant compositions include one-part and two-part formulations which cure by a variety of chemical mechanisms. One-part sealant compositions generally contain an end-capped base polymer together with a reactive cross-linking agent and, typically, a curing catalyst which promotes the cross-linking reaction either when heated or exposed to atmospheric moisture. Upon application under normal conditions of temperature and moisture, one-part sealants react to form tough, pliable elastomeric seals. Two-part sealant compositions, on the other hand, comprise two reactive components which are separately packaged and mixed just prior to or at the time of application and react upon mixing to form the semi-rigid sealant bead. Two-part sealant compositions are less convenient to use since it is necessary to accurately premeasure and mix the components prior to use or accurately meter the components during application to insure correct proportions if the two components are applied together to form the sealant bead. For this reason, one-part sealants have found wider acceptance in the market. A number of such one-part moisture-curable sealant compositions are known. Because of their convenience and ease of use, there has been increasing demand for such sealants, especially if they possess both good shelf life and rapid curing rates. To enhance the curing rates of moisture-cured sealants, a variety of curing catalysts and accelerators have been incorporated into such one-part compositions. The following United States patents disclose one-part moisture-curable polyurethane based sealant compositions and curing catalysts: 3,779,794 to De Santis (1,2,4-trimethylpiperazine); 3,979,344 to Bryant (dibutyl tin diacetate); 4,038,239 to Coyner, et al. (metallic salts of tin, lead, mercury, or Group VIII such as iron, organo-tin (IV) and organo-lead compounds, and organic amines such as trialkylamines, N -substituted piperidines, N,N' -substituted piperazines, pyridine); 4,469,831 to Bueltjer, et al. (aliphatic or aromatic carboxylic acids, toluenesulfonic acid); 4,672,003 to Letoffe (silane- or siloxane-substituted morpholines; and 4,707,515 to Gilch, et al. (organic and inorganic acids, salts of organic acids such as tin naphthenate, tin ocotate, tin butyrate, dibutyltin dioctoate, dibutyltin dilaurate, dibutyltin diacetate, iron stearate, lead octoate, or organic amines). FR-A-2 292 015 discloses curable compositions comprising a siloxane terminated polyurethane, a minor amount of aminoalkyl siloxane and tin curing catalysts. The use of a piperzinyl siloxane accelerator is not described in this document. It has been found, in accordance with the present invention, that one-component polyurethane-based sealant compositions having fast cure rates at room temperature in the presence of moisture comprise a mixture of a silane-capped polyurethane polymer, from 0.2 to 1.0 parts by weight of an aminosilane per 100 parts by weight of the polyurethane polymer and a curing catalyst, characterized in that the sealant compositions comprise from 0.2 to 1.0 parts by weight of a silyl-substituted piperazinyl accelerator per 100 parts of the polyurethane polymer. The silane capped polyurethane polymer has the structure where R is lower alkyl of from 1 to 6 carbon atoms and R¹ is a divalent bridging radical selected from the group consisting of divalent hydrocarbon radicals, divalent hydrocarbon ether radicals, and divalent hydrocarbon amino radicals. The group A is selected from -S- and - NR²- where R² is hydrogen or alkyl from one to six carbon atoms. The aminosilane has the structure where x is an integer of from one to three, and R³ and R⁴ may be the same or different and are selected from alkyl of from one to four carbon atoms. The group R⁵ is alkyl of from one to four carbon atoms or alkoxyl of from one to four carbon atoms and R⁶ is hydrogen or -(CH₂) y NHR⁷ where R⁷ is hydrogen or -(CH₂) z NH₂. The subscripts y and z may be the same or different and are integers of from one to three. The silyl-substituted piperazinyl accelerator is selected from the group consisting of mono- di- or tri-silylsubstituted piperazine compounds having the structure where w is an integer of from one to five, R⁸, is hydrogen or where a is an integer of from one to four, b is zero or an integer of from one to four, B is a direct bond or is a divalent hydrocarbaryl radical or a divalent cyclohydrocarbyl radical, and R⁹ and R¹⁰ are independently hydrogen, alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴, and R⁵, are as defined above, with the proviso that at least one of R⁸, R⁹ and R¹⁰ must be The composition may also contain other ingredients generally known to formulators of polymeric sealant compositions such as pigments, thixotropic agents, fillers, acidic or basic polymerization agents. As used throughout this specification and the appended claims, the term "alkyl" means a hydrocarbon residue derived from branched or unbranched alkane by removal of a single hydrogen atom. The term "alkoxyl" denotes alkyl groups attached through an oxygen ether linkage to the remainder of the parent molecule. The term "divalent hydrocarbyl" means a branched or unbranched hydrocarbon group derived by removal of two hydrogen atoms from a saturated or unsaturated acrylic hydrocarbon. The term "divalent hydrocarbaryl" denotes a group derived from the removal of two hydrogen atoms from hydrocarbon containing one or more carbocyclic aromatic rings including phenyl, alkylphenyl, and phenylalkyl. The term "divalent cyclohydrocarbyl" means a group derived by the removal of two hydrogen atoms from a carbocyclic non-aromatic hydrocarbon ring including cyclohexane, alkylcyclohexane. The sealant compositions of the present invention comprise a base silane-capped polyurethane polymer having a number average molecular weight in the range of from 10,000 to 30,000 having the structure where R, R¹, and A are defined above. Such silane-capped polyurethane polymers are prepared by conventional polymerization techniques by reacting a polyether polyol having a least two free hydroxyl groups per molecule with an isocyanate compound having at least two isocyanate reactive groups per molecule. The polyether polyol and isocyanate compound are reacted in a weight ratio of 8:1 to 12:1, respectively. The starting polyether polyol preferably has a number average molecular weight of between 1,000 and 5,000. One such preferred starting material is polypropylene glycol available as Polypropylene Glycol 2025 from Union Carbide Co., 270 Park Avenue, New York,NY 10017. The starting isocyanate compound may be selected from a variety of materials known in the art for such purposes, but one such preferred material is toluene diisocyanate. The copolymer formed by reaction of these two monomers is end-capped with a silane group having the structure -A-R¹-Si-(OR)₃. The group A is sulfur or an alkylamino group in which the alkyl portion contains from one to six carbon atoms. The bridging group R¹ may be a divalent hydrocarbon radical, a divalent hydrocarbon radical containing one or more oxygen ether linkages, or a divalent hydrocarbon radical containing one or more > NH linkages. The end-capping of the polyurethane polymer is achieved by including in the reaction mixture containing the polyether polyol and isocyanate compound an aminosilane compound such as gamma-aminopropyl-trimethoxysilane (A 1110) available from Union Carbide Corp., 270 Park Ave., New-York, NY 10017). The silane-capped polyurethane polymer is mixed with from 20 to 50 parts by weight of a pigmenting agent and/or filler such as carbon black per 100 parts by weight of the capped polyurethane polymer. Small amounts, ranging from 0.25 to 0.75 parts by weight of a thixotropic agent per 100 parts by weight of polyurethane polymer may also be added to adjust the flow characteristics of the sealant composition. A typical thixotropic agent suitable for this purpose is Thixseal 1085 available from NL Chemicals, Inc., Heightstown, NJ 08520. Additional aminosilane is added to the sealant composition in amounts ranging between 0.2 to 1.0 parts by weight (preferably between 0.4 to 0.8 parts by weight) per 100 parts by weight of the polyurethane polymer. The aminosilane used is selected from compounds having the formula where x is an integer of from one to three and R³ and R⁴ may be the same or different and are selected from alkyl of from one to four carbon atoms. The group R⁵ is alkyl of from one to four carbon atoms or alkoxyl of from one to four carbon atoms and R⁶ is hydrogen or -(CH₂) y NHR⁷. R⁷ is hydrogen or -(CH₂) z NH₂ wherein y and z may be the same or different and are integers of from one to three. Suitable materials for this purpose are aminosilanes such as A 1110, A 1120, and A 1130, available from Union Carbide Corp., 270 Park Ave., New York, NY 10017. The sealant compositions of this invention further contain from 0.2 to 1.0 parts by weight (preferably between 0.2 to 0.8 parts by weight) per 100 parts by weight of the polyurethane polymer of a silyl-substituted piperazinyl accelerator selected from compounds having the structure where w is an integer of from one to five R⁸, is hydrogen or where a is an integer of from one to four, b is zero or an integer of from one to four, B is a direct bond or is a divalent hydrocarbaryl radical or a divalent cyclohydrocarbyl radical, and R⁹ and R¹⁰ are indepentently hydrogen, alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴, and R⁵, are as defined above, with the proviso that at least one of R⁸, R⁹ and R¹⁰ must be Preferred substituted piperazine compounds include those in which one ring nitrogen atom of piperazine is substituted by a silyl group and the other ring nitrogen atom is substituted by (a) aminoalkyl of from one to five carbon atoms, (b) alkylaminoalkyl of from two to ten carbon atoms, or (c) dialkylaminoalkyl of from three to fifteen carbon atoms, for example, aminomethyl, methylaminomethyl, dimethylamino-methyl, 1- and 2- aminoethyl, 2-(methylamino)ethyl, 2-(dimethylamino) ethyl, 2-(ethylamino)ethyl, 2-(diethylamino)ethyl, 1-, 2-or 3-aminopropyl, 3-(methylamino)propyl, and 3-(dimethylamino)-propyl. Silyl-substituted piperazinyl compounds ot the type suitable for use in sealant compositions of the present invention are made by reacting the appropriate chlorosilane with the desired substituted piperazine compound in an aprotic inert polar organic solvent such as 1,1,1-trichloroethane at a temperature between 50°C and 100°C preferably at 80°C. The reaction is carried out for a period sufficient to effect substantially complete reaction between the two starting materials, typically for two to six hours. The starting chlorosilane compounds are commercially available from Dynamit Nobel Chemicals, Silanes & Silicones Group, Bartram Road, Bristol, PA 19007, USA. The starting aminoalkyl-substituted piperazines are commercially available from such sources as Aldrich Chemical Co., 940 West St. Paul Ave., Milwaukee, WI, 53233 USA or are easily synthesized by conventional methods known to practitioners of the organic chemical arts. A mixture of products is obtained from the reaction between the chlorosilane and starting piperazine compound since there are one, two, or three reactive sites for the chlorosilane, depending upon whether the starting piperazine compound is a dialkylaminoalkyl-, alkylaminoalkyl-, or aminoalkylpiperazine compound, respectively. This process is typified by the following Reaction Scheme where, for the sake of example, the reaction between 1-(2-aminoethyl)piperazine and 1-chloro-3-(trimethoxysilyl)propane is shown. While not adhering to any particular theory to the exclusion of others, it is believed that the function of the silyl-substituted piperizinyl compounds is at least three-fold: first, the silyl-substituted piperazinyl compound is thought to be instumental in accelerating the curing rate of the polymeric composition; second, it is believed to promote the adherence of the resulting elastomer; and third, the amine functionality present in the substituted piperazinyl compound is believed to act as an acid scavenger in the composition, promoting its shelf-life. It has been found in accordance with the present invention that the inclusion of such substituted piperazinyl accelerators in the sealant compositions significantly increases the cure rates over the cure rates for similar sealant compositions which lack such accelerator compounds, as can be seen from the data provided in the following Table. Enhanced cure rates provide an important advantage when the sealants of this invention are employed, for example, in sealing fixed window panels and taillight glass panels to motor vehicle bodies where slowly curing sealants may present problems in a continuous production assembly line operation. Testing Procedures The lap shear strength of several materials prepared in accordance with the teachings of the present invention were tested according to the following method. In each instance, pairs of shear strength test plates were prepared by bonding two previously primed and painted steel plates, each 1 inch by 0.32 inches (2.54 cm x 0.81 cm), with a sealant bead 1 inch long by 0.25 inches wide by 5/16 inches thick (2.54 cm x 0.64 cm x 0.79 cm). The sealant bead was applied along one of the one-inch edges of the test plates by means of a sealant tube. The plates were then pressed together so that the sealant bead was about 0.25 inches (0.64 cm) thick. The sealant bead applied to the bonded test plates was allowed to cure at room temperature and 50% relative humidity for periods which varied between three hours and seven days. After the appropriate cure time in each case, the shear strength of each sealant bead was tested on an Instron testing machine by pulling in a direction parallel to the faces of the bonded test plates. The results of these tests, along with other properties of the tested compositions, appear in the following Table. As can be seen by comparison of the data for Examples 5 and 10, the sealant composition have a much faster cure rate when the accelerators of the present invention are a component of the composition. Example 5 contained a preferred accelerator of the invention, while in Example 10 the composition was identical, except that the accelerator and the amino siloxane were missing. After three hours of curing, the lap shear strength of the material of Example 5 was almost nine times as great as that of Example 10. Morover, the data in Table indicate that increasing the amount of accelerator has a positive effect on the cure rate as shone by comparing the three-hour lap shear strength of the compositions of Examples 5, 8 and 9. The three-hour lap shear strength increased as the amount of accelerator was increased in each instance. In Examples 8 and 9, the aminosilane was omitted to test the resulting effect, and the data indicate that there was a little effect of the omission on the enhancement of the cure rate. (The presence of the aminosilane is preferred, however, to enhance other desirable properties of the final sealant composition such as adhesion.) The following exmaples are provided to enable one skilled in the art to practice the present invention. These examples are merely illustrative of the present invention and are not to read as limiting the scope of the invention which is defined by the appended claims. Preparation of Starting Materials Example 1 Preparation of Base Polyurethane Polymer A silane-capped polyurethane polymer of the type described in United States Patent 3,632,557 was prepared as follows: A. Niax PPG 2025 ONE (2000 Molecular weight polyether polyol available from Union Carbide Corp., 270 Park Ave., New York, NY 10017) 2001.00g Hylene R (80:20 Grade toluene diisocyante available from E.I. duPont de Nemours & Co., Wilmington, DE 19898) 204.00g Glacial acetic acid 0.55 g Dibutyltin diacetate 0.45 g B. Anhydrous toluene 110.00 g C. Anhydrous toluene 81.00 g Silane A 1110 ( gamma -Aminopropyl)trimethoxy silane availiable from Union Carbide Corp., 270 Park Ave., New York, NY 10017) 68.30 g D. Anhydrous methanol 273.00 g The components of A above were mixed and heated to 155°F (68.3°C) under anhydrous conditions and maintained at that temperature for fifty-five minutes. At the end of that time, B was added. Over the next forty-five minutes, the temperature of the mixture was gradually reduced to 105°F (40.6°C) and heating was continued for two and one-quarter hours. At the end of this time, C was added to the mixture and the resulting mixture was heated at 150-165°F (65.6-73.9°C) for an additional two and one-quarter hours. During this time, samples of the reaction mixture were tested for free isocyanate functional groups. When the tests indicated no residual free isocyanate, D was added and the mixture heated under reflux for a short time. The mixture was degassed and cooled to room temperature. Example 2 Preparation or 1-[2-[3-(Trimethoxysilyl)propyl]aminoethyl]piperazine Accelerator A one-liter, four-necked flask was equipped with a thermometer, a condensor, an inlet tube for nitrogen gas and an outlet tube for vent gases. Chloropropyltrimethoxysilane (198.72 g) was introduced into the flask, together wityh 50 g of anhydrrous 1,1,1-trichloroethane and 86.14 g of 1-(2-aminoethyl)- piperazine. The mixture was heated to 80°C with continuous agitation for four hours and then cooled to room temperature. The reaction mixture was rapidly filtered to collect the 1-(2-aminoethyl)piperazine hydrochloride salt which had formed. The filtrate was distilled to yield 182 g of 1-[2-[3-(trimethoxysilyl)- propyl]aminoethyl]piperazine, bp 120-143°C at 10 mm Hg (69 kPa) as a pale yellow oil. The yield corresponded to 64% of theoretical. This material was used as an accelerator and adhesion promoter in the sealant compositions of this invention as detailed below in Example 5. Along with the primary reaction product, smaller amounts of three other products were obtained: a) 1-(2-aminoethyl)-4-[3-(trimethoxysilyl)propyl]piperazine; b) bis [3-trimethoxysilyl)propyl)piperazine; and c) 1,4- bis [3-trimethoxypropyl)silyl]piperazine. Example 3 Preparation of 1-[2-[3-(Triethoxysilyl)propyl]aminoethyl]piperazine Accelerator Starting with 241 g of chloropropyltrimethoxy-silane and 110 g of 2-aminoethylpiperazine, the procedure described in Example 2 was used to prepare 75 g of the title compound, boiling point range 145-163°C at 5 mm Hg (34 kPa). Example 4 Preparation of 1-[2-[3-(Methyldimethoxysilyl)propyl]aminoethyl]piperazine Accelerator Starting with 182.7 g of chloropropylmethyldimethoxysilane and 79 g of 2-aminoethylpiperazine, the procedure described in Example 2 was used to prepare 75 g of the title compound, boiling point range 90-110°C at 5 mm Hg (34 kPa). Preparation of Sealant Compositions Example 5 Preparation of Sealant Composition Containing Accelerator of Example 2 A five gallon Meyers mixer with dual mixing blades was charged with 25 lb (11.34 kg) of the silane-terminated polyurethane base polymer composition of Example 1 and thoroughly mixed for five minutes under a slight vacuum with 3 lb (1.36 kg) of anhydrous methanol. To this mixture was then added 64 g of adhesion promoter N-beta -aminoethyl- gamma -aminopropyl trimethoxysilane, (available as Silane A1120 from Union Carbide Company, 270 Park Avenue, New York, NY 10017), 77 g of a rheology control agent, Thixseal 1084 (available from NL Chemicals, Inc., Heightstown, NJ 08520), 64 g of DBTDA anti-oxidant (available as anti-oxidant AO 2246 from American Cyanamide Co., Bound Brook, NJ 08805), and 12.0 g of dibutyltin diacetate. The resulting mixture was stirred for ten minutes under slight vacuum, after which time 75 g of 1-[2-[3-trimethoxysilyl)propyl]aminoethylpiperazine were added as an accelerating agent. Carbon black (10 lb, 4.54 kg) which had been previously dried to less than 0.05% by weight moisture content, was added and the resulting mixture was mixed for one hour. The resulting mixture was stirred for ten minutes under slight vacuum, cooled to room temperature, and packaged under anhydrous conditions. The final sealant material had the following composition (normalized to 100 parts by weight of the base polyurethane polymer): Component Parts by Weight Base polyurethane polymer 100 Solvent (methanol) 7.76 Carbon black 40.14 Thixotropic agent 0.68 A 1120 Aminosilane 0.56 1-[2-[(3-Trimethoxysilyl)propyl]-aminoethyl]piperazine accelerator 0.66 AO 2246 Anti-oxidant 0.56 Dibutyl tin diacetate 0.11 Example 6 Preparation of Sealant Composition Containing Accelerator of Example 3 The procedure of Example 5 was followed to prepare a sealant material having the composition given below. Component Parts by Weight Base polyurethane polymer 100 Solvent (methanol) 7.76 Carbon black 40.14 Thixotropic agent 0.68 A 1120 Aminosilane 0.56 1-[2-[(3-Triethoxysilyl)propyl]-aminoethyl]piperazine accelerator 0.66 AO 2246 Anti-oxidant 0.56 Dibutyl tin diacetate 0.11 Example 7 Preparation of Sealant Composition Containing Accelerator of Example 3 The procedure of Example 5 was followed to prepare a sealant material having the composition given below. Component Parts by Weight Base polyurethane polymer 100 Solvent (methanol) 7.76 Carbon black 40.14 Thixotropic agent 0.68 A 1120 Aminosilane 0.56 1-[2-[3-(Methyldimethoxysilyl)-propyl]aminoethyl]piperazine accelerator 0.66 AO 2246 Anti-oxidant 0.56 Dibutyl tin diacetate 0.11 Example 8 The procedure of Example 5 was followed to prepare a sealant composition in which the amount of accelerator was decreased, and the aminosilane was omitted. The material had the following composition: Component Parts by Weight Base polyurethane polymer 100 Solvent (methanol) 7.76 Carbon black 40.14 Thixotropic agent 0.68 A 1120 Aminosilane ---- 1-[2-[3-(Trimethoxysilyl)propyl]-aminoethyl]piperazine accelerator 0.46 AO 2246 Anti-oxidant 0.56 Dibutyl tin diacetate 0.11 Example 9 The procedure of Example 5 was followed to prepare a sealant composition in which the amount of accelerator was increased, and the aminosilane was omitted. The material had the following composition: Component Parts by Weight Base polyurethane polymer 100 Solvent (methanol) 7.76 Carbon black 40.14 Thixotropic agent 0.68 A 1120 Aminosilane ---- 1-[2-[3-(Trimethoxysilyl)propyl]-aminoethyl]piperazine accelerator 0.77 AO 2246 Anti-oxidant 0.56 Dibutyl tin diacetate 0.11 Example 10 The procedure of Example 5 was followed to prepare a sealant composition in which both the accelerator and the aminosilane were omitted. The material had the following composition: Component Parts by Weight Base polyurethane polymer 100 Solvent (methanol) 7.76 Carbon black 40.14 Thixotropic agent 0.68 A 1120 Aminosilane ---- Accelerator ---- AO 2246 Anti-oxidant 0.56 Dibutyl tin diacetate 0.11

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, IT, LI, LU, NL, SE A one-component, moisture-curable sealant composition comprising a mixture of (a) a silane-capped polyurethane polymer of the formula wherein R is lower alkyl of from 1 to 6 carbon atoms; R¹ is a divalent bridging radical selected from the group consisting of a divalent hydrocarbon radical, a divalent hydrocarbon ether radical, and a divalent hydrocarbon amino radical; A is selected from the group consisting of -S- and -NR²- where R² is hydrogen or alkyl of from one to six carbon atoms; (b) from 0.2 to 1.0 parts by weight of an aminosilane per 100 parts by weight of said polyurethane polymer, said aminosilane having the structure wherein x is an integer of from one to three; R³ and R⁴ may be the same or different and are selected from alkyl of from one to four carbon atoms; R⁵ is alkyl of from one to four carbon atoms or alkoxyl of from one to four carbon atoms; R⁶ is hydrogen or -(CH₂) y NHR⁷ wherein R⁷ is hydrogen or - (CH₂) z NH₂ and y and z may be the same or different and are integers of from one to three; (d) a curing catalyst characterized in that the sealant composition comprises (c) from 0.2 to 1.0 parts by weight of an accelerator per 100 parts by weight of said polyurethane polymer, said accelerator selected from the group consisting of compounds or mixtures thereof having the structure where w is an integer of from one to five, R⁸ is hydrogen or where a is an integer of from one to four, b is zero or an integer of from one to four, B is a direct bond or is a divalent hydrocarbaryl radical or a divalent cyclohydrocarbyl radical, and R³, R⁴, and R⁵ are as previously defined, R⁹and R¹⁰ are independently hydrogen, alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴, and R⁵ are as defined above, with the proviso that at least one of R⁸, R⁹ and R¹⁰ must be A one component, moisture-curable sealant composition as defined in Claim 1 wherein said polyurethane polymer is the reaction product of a polyether polyol containing at least two hydroxyl groups per molecule and a number average molecular weight of 1000 to 3000 and an isocyanate having at least two isocyanat groups per molecule. A one-component,moisture-curable sealant composition as defined in Claim 1 wherein said polyurethane polymer has a number average molecular weight of from 10,000 to 30,000. A one-component, moisture-curable sealant composition as defined in Claim 3 wherein A is -NR²-where R² is as defined therein. A one-component, moisutre-curable sealant composition as defined in Claim 1 wherein said composition comprises from 0.4 to 0.8 parts by weight of said aminosilane per 100 parts by weight of said polyurethane polymer. A one-component, moisture-curable sealant composition as defined in Claim 5 wherein said aminosilane is N-(beta -aminoethyl)- gamma -aminopropyl trimethoxysilane. A one-component, moisture-curable sealant composition as defined in Claim 1 wherein said composition comprises from 0.2 to 0.8 parts by weight of said accelerator per 100 parts by weight of said polyurethane polymer. A one-component, moisture-curable sealant composition as defined in Claim 1 wherein said accelerator is selected from the group consisting of (a) 1-[2-[3-(trimethoxysilyl)propyl]aminoethyl]piperazine; (b) 1-[2-[3-(triethoxysilyl)propyl]aminoethyl]piperazine; and (c) 1-[2-[3-(methyldimethoxysilyl)propyl]aminoethyl]piperazine A one-component, moisture-curable sealant composition as defined in Claim 8 wherein said accelerator is 1-[2-[3-(trimethoxysilyl)propyl]aminoethyl]piperazine. A one-component, moisture-curable sealant composition as defined in Claim 8 wherein said accelerator is 1-[2-[3-(triethoxysilyl)propyl]aminoethyl]piperazine. A one-component, moisture-curable sealant composition as defined in Claim 8 wherein said accelerator is 1-[2-[3-(methyldimethoxysilyl)propyl]aminoethyl]piperazine. An accelerator compound selected from compounds having the structure where w is an integer of from one to five, R⁸, is hydrogen or where a is an integer of from one to four, b is zero or an integer of from one to four, B is a direct bond or is a divalent hydrocarbaryl radical or a divalent cyclohydrocarbyl radical, and R⁹ and R¹⁰ are independently hydrogen, alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴, and R⁵, are as defined above, with the proviso that at least one of R⁸, R⁹ and R¹⁰ must be An accelerator compound as defined in Claim 12 wherein R⁸ is where a, b, B, R³, R⁴, and R⁵, are as defined, and R⁹, and R¹⁰ are hydrogen or An accelerator compound as defined in Claim 12 wherein R⁸ is where a, b, B, R³, R⁴, and R⁵, are as defined therein, R⁹ is hydrogen, and R¹⁰ is alkyl of from one to five carbon atoms, or An accelerator compound as defined in Claim 12 wherein R⁸ is where a, b, B, R³, R⁴, and R⁵, are as defined therein, and R⁹ and R¹⁰ are independently alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴, and R⁵, are as defined therein. The compound as defined by Claim 12 having the name 1-[2-[3-(trimethoxysilyl)propyl]aminoethyl]piperazine. The compound as defined by Claim 12 having the name 1-[2-[3-(triethoxysilyl)propyl]aminoethyl]piperazine. The compound as defined by Claim 12 having the name 1-[2-[3-(methyl dimethoxysilyl)propyl]aminoethyl]piperazine. Claims for the following Contracting States : ES, GR A process for the preparation of a one-component, moisture-curable sealant composition wherein (a) a silane-capped polyurethane polymer of the formula wherein R is lower alkyl of from 1 to 6 carbon atoms; R¹ is a divalent bridging radical selected from the group consisting of a divalent hydrocarbon radical, a divalent hydrocarbon ether radical, and a divalent hydrocarbon amino radical; A is selected from the group consisting of -S- and -NR²- where R² is hydrogen or alkyl of from one to six carbon atoms; (b) from 0.2 to 1.0 parts by weight of an aminosilane per 100 parts by weight of said polyurethane polymer, said aminosilane having the structure wherein x is an integer of from one to three; R³ and R⁴ may be the same or different and are selected from alkyl of from one to four carbon atoms; R⁵ is alkyl of from one to four carbon atoms or alkoxyl of from one to four carbon atoms; R⁶ is hydrogen or -(CH₂) y NHR⁷ wherein R⁷ is hydrogen or - (CH₂) z NH₂ and y and z may be the same or different and are integers of from one to three; and (d) a curing catylyst are mixed, characterized in that (c) from 0.2 to 1.0 parts by weight of an accelerator per 100 parts by weight of said polyurethane polymer, said accelerator selected from the group consisting of compounds or mixtures thereof having the structure where w is an integer of from one to five, R⁸ is hydrogen or where a is an integer of from one to four, b is zero or an integer of from one to four, B is a direct bond or is a divalent hydrocarbaryl radical or a divalent cyclohydrocarbyl radical, and R³, R⁴ and R⁵ are as previously defined, R⁹ and R¹⁰ are independently hydrogen, alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴ and R⁵ are as defined above, with the proviso that at least one of R⁸, R⁹, and R¹⁰ must be are incorporated into the sealant composition. A process as defined in Claim 1 wherein a polyurethane polymer is used which is the reaction product of a polyether polyol containing at least two hydroxyl groups per molecule and a number average molecular weight of 1000 to 3000 and an isocyanate having at least two isocyanate groups per molecule. A process as defined in Claim 1 wherein a polyurethane polymer is used which has a number average molecular weight of from 10,000 to 30,000. A process as defined in Claim 3 wherein a polyurethane polymer is used in which A is -NR²- where R² is as defined therein. A process as defined in Claim 1 wherein from 0.4 to 0.8 parts by weight of said aminosilane per 100 parts by weight of said polyurethane polymer are used. A process as defined in Claim 5 wherein said aminosilane is N-(β-aminoethyl)-γ-aminopropyl trimethoxysilane. A process as defined in Claim 1 wherein from 0.2 to 0.8 parts by weight of said accelerator per 100 parts by weight of said polyurethane polymer are used. A process as defined in Claim 1 wherein said accelerator is selected from the group consisting of (a) 1-[2-[3-(trimethoxysilyl)propyl]aminoethyl]piperazine; (b) 1-[2-[3-(triethoxysilyl)propyl]aminoethyl]piperazine; and (c) 1-[2-[3-(methyldimethoxysilyl)propyl]-aminoethyl]piperazine. A process as defined in Claim 8 wherein said accelerator is 1-[2-[3-trimethoxysilyl)propyl]-aminoethyl]piperazine. A process as defined in Claim 8 wherein said accelerator is 1-[2-[3-(triethoxysilyl)propyl]-aminoethyl]piperazine. A process as defined in Claim 8 wherein said accelerator is 1-[2-[3-(methyldimethoxysilyl)propyl]aminoethyl]piperazine. A process for the production of a silyl-substituted piperazinyl compound by reacting the appropriate chlorosilane with the desired substituted piperazine compound in an aprotic inert polar organic solvent, wherein a compound having the structure where w is an integer of from one to five, R⁸ is hydrogen or where a is an integer of from one to four, b is zero or an integer of from one to four, B is a direct bond or is a divalent hydrocarbaryl radical or a divalent cyclohydrocarbyl radical, and R⁹ and R¹⁰ are independently hydrogen, alkyl of from one to five carbon atoms, or where a, b, B, R³, R⁴, and R⁵, are as defined above, with the proviso that at least one of R⁸, R⁹ and R¹⁰ must be is produced. A process as defined in Claim 12 wherein R⁸ is where a, b, B, R³, R⁴ and R⁵, are as defined, and R⁹, and R¹⁰ are hydrogen or A process as defined in Claim 12 wherein R⁸ is where a, b, B, R³, R⁴ and R⁵, are as defined therein, R⁹ is hydrogen, and R¹⁰ is alkyl of from one to five carbon atoms, or A process as defined in Claim 12 wherein R⁸ is where a, b, B, R³, R⁴ and R⁵, are as defined therein, and R⁹ and R¹⁰ are independently alkyl of from one to five carbon atoms or where a, b, B, R³, R⁴, and R⁵ are as defined therein. A process as defined by Claim 12 wherein 1-[2-[3-(trimethoxysilyl)propyl]aminoethyl]-piperazine is produced. A process as defined by Claim 12 wherein 1-[2-[3-(triethoxysilyl)propyl]aminoethyl]piperazine is produced. A process as defined by Claim 12 wherein 1-[2-[3-(methyl dimethoxysilyl)propyl]aminoethyl]piperazine is produced.

Inventors: BAGHDACHI JAMIL, MAHONEY KEITH H, BAGHDACHI, JAMIL, MAHONEY, KEITH H.
Applicants: ADCO PRODUCTS INC, ADCO PRODUCTS, INC.
Application year: 1989
Main classification: C08G18
IPC codes: C08G18, C08L75, C09K3, C08K5, F16J15, C09J175