Process for producing vulcanized rubber-synthetic resin composite structure

Abstract: A process for producing a vulcanized rubber-synthetic resin composite structure which comprises forming a layer of a curable adhesive on the surface of the vulcanized rubber molding, said curable adhesive being composed mainly of chlorosulfonated polyethylene, disposing the vulcanized rubber molding in the heated state in a mold, injecting a molten resin into the mold, and demolding the composite structure after the setting of the injected resin.

Description: The present invention relates to a process for producing a vulcanized rubber-synthetic resin composite structure, and more particularly, to a process for producing a vulcanized rubber-synthetic resin composite structure in which the vulcanized rubber and the synthetic resin are bonded extremely firmly to each other. Industrial rubber products are often used in the form of rubber-metal composite structure. Recently, metals for this purpose are being supplanted by the recently developed engineering plastics which have outstanding mechanical strength, heat resistance, oil resistance, and creep resistance. As a result, new application areas are being opened up by the rubber-synthetic resin composite structure. An example of such application areas is the automotive suspension rod. The conventional metal rod with rubber bushings is being supplanted by the plastics rod with rubber bushings whose plan view is shown in Fig. 1 and whose sectional view taken through section II-II of Fig. 1 is shown in Fig. 2. There are shown a rod proper 2 made of plastics (such as polyamide resin), a bushing 3 made of vulcanized rubber, and a steel bearing 4. The rubber bushings 3 attached to both ends of the rod 1 are intended to reduce the torsional rigidity, and the rod 1 is joined to the automotive body through the bushings 3 and steel bearings 4. The rubber-synthetic resin composite structure is usually produced by curing a desired part of unvulcanized rubber in contact with the surface of the synthetic resin moldings to which a chlorine-containing vulcanizable adhesive has been applied. According to the disclosure of Japanese Patent Laid-open No. 104717/1987, the plastics rod with rubber bushings as shown in Figs. 1 and 2 is produced by disposing the bushings of vulcanized rubber in a mold and injecting a melt of a synthetic resin into the mold. GB-691252 discloses a process for making composite articles which comprises subjecting the surface of a soft-vulcanized rubber component to chemical modification, bringing said modified surface into contact with a rigid component with a bonding layer therebetween and hardening the bonding layer whilst pressing the rubber component against the rigid component. Needless to say, firm bonding between rubber and resin is very important for the rubber-resin composite structure. In the case of the plastics rod with rubber bushings, the plastics rod proper and the rubber bushing should be bonded extremely firmly to each other. Unfortunately, adhesion between rubber and plastics is poor, and a sufficient bond strength is not achieved by simply injecting a molten resin into a cavity surrounding the bushing of vulcanised rubber, as disclosed in the above-mentioned Japanese Patent Laid-open No. 104717/1987. A high adhesion strength is obtained when bonding is performed by curing unvulcanized rubber in contact with a synthetic resin molding. However, this bonding method has a disadvantage that the physical properties of the synthetic resin molding might be deteriorated by the heat history encountered in the curing step. Moreover, a resin molding having a low melting point might be deformed by the curing heat. An additional disadvantage is a comparatively high production cost. Therefore, the above-mentioned method is inefficient for the production of a composite structure (having a rubber bushing embedded in plastics) as shown in Figs. 1 and 2. The present invention provides a process for producing a vulcanized rubber-synthetic resin composite structure which comprises forming a layer of a curable adhesive on the surface of the vulcanized rubber molding, said curable adhesive being composed mainly of chlorosulfonated polyethylene, heating the vulcanized rubber molding at 90-140°C for 10-90 minutes, disposing the vulcanized rubber molding in the heated state in a mold, injecting a molten resin into the mold, and demolding the composite structure after the setting of the injected resin. The present invention is concerned with an improved process for producing a vulcanized rubber-synthetic resin composite structure by injecting a molten synthetic resin into a mold in which a vulcanized rubber molding has been disposed, wherein the improvement comprises forming a curable adhesive layer composed mainly of chlorosulfonated polyethylene on the surface of the vulcanized rubber molding which comes into contact with the synthetic resin, and injecting the molten synthetic resin while keeping the vulcanized rubber molding heated. A preferred embodiment of the present invention will now be described by way of example only with reference to the accompanying drawings, in which: Fig. 1 is a plan view showing a plastics rod with rubber bushings; Fig. 2 is a sectional view taken in the direction of the arrows along the line II-II of Fig. 1; Fig. 3 is a plan view showing a test piece prepared in Examples and Comparative Examples; and Fig. 4 is a sectional view taken in the direction of the arrows along the line IV-IV of Fig. 3. In the process in accordance with the present invention, the vulcanized rubber molding to be disposed in the mold is coated with a curable adhesive layer composed mainly of chlorosulfonated polyethylene such that at least the surface which comes into contact with the synthetic resin is coated. The thickness of the adhesive layer is not specifically limited; and it may be properly determined according to the product dimensions, the manufacturing conditions, and the properties required. The curable adhesive layer is subsequently heated for activation. The heating may be accomplished by, for example, heating the vulcanized rubber molding entirely in an oven. The heating in an oven should be carried out at an ambient temperature of 90-140°C for 10-90 minutes, preferably at 120°C for 30 minutes. After heat treatment, the vulcanized rubber molding is disposed in a mold, and a molten resin is injected into the mold to make an integrated body. Immediately after demolding, the vulcanized rubber-synthetic resin composite structure should preferably be heated so as to improve the adhesion strength between the vulcanized rubber and the synthetic resin. The heating may be accomplished by, for example, heating the demolded composite structure in an oven or the like. The heating in an oven should be carried out at an ambient temperature of 90-140°C for 10-120 minutes, preferably at 120°C for 60 minutes. There are no specific limitations on the rubber constituting the vulcanized rubber molding. The preferred rubber is natural rubber, synthetic rubber having a carbon-carbon double bond in the structural formula, butyl rubber, or chloroprene rubber. These rubbers may be used alone or in combination with another. The rubber is incorporated with a filler (such as carbon black, silica, calcium carbonate, and mica) and commonly used additives (such as softener, antioxidant, vulcanization accelerator, and crosslinking agent). After thorough mixing, the resulting rubber compound is cured or semicured into the vulcanized rubber molding under proper conditions. The synthetic resin used for injection molding is usually a thermoplastic resin. It includes, for example, polyamide resin, ABS resin, acetal resin, methacrylic resin, ethylene-vinyl acetate copolymer, fluoroplastics, polycarbonate, polyethylene terephthalate, polybutylene terephthalate, polypropylene, polyimide, polystyrene, polysulfone, polyphenylene sulfide, vinyl acetate resin, vinylidene chloride resin, AS resin, and vinyl chloride resin. Preferable among them are polyamide resins, especially those which have amide groups on the main chain structure. Examples of such polyamide resins include nylon-6, nylon-11, nylon-12, nylon-66, nylon-610, and copolymers and blends thereof, with the functional group partly modified or not modified. These polyamide resins may be incorporated with other thermoplastic resins and rubber components for the improvement of their physical properties. They may also be incorporated with a reinforcement (such as glass fiber, carbon fiber, and whiskers) and an inorganic filler (such as calcium carbonate and talc). According to the process of the present invention, a vulcanized rubber molding is disposed in a mold and a molten synthetic resin is injected into the mold. Therefore, the process enables the efficient production of the vulcanized rubber-synthetic resin composite structure. In addition, the vulcanised rubber molding previously undergoes special treatment for the improvement of adhesion properties. Therefore, firm bonding is established between the vulcanized rubber molding and the injected synthetic resin, and the resulting vulcanized rubber-synthetic resin composite structure has an extremely high bond strength. The process of the present invention enables the efficient production of the extremely firmly bonded vulcanized rubber-synthetic resin composite structure at a low production cost and with a high productivity without causing the deterioration and deformation of the synthetic resin by heat history. The process of the present invention will be very effective for the production of plastics rod with rubber bushings for automotive use. The invention will be understood more readily by reference to the following Examples and Comparative Examples; however, these Examples are intended to illustrate the invention and should not be construed as limiting the scope of the invention. Example 1 A vulcanized rubber test piece conforming to ASTM D429 (Method B, for 90° peel test) was prepared from the rubber compound of the formulation shown in Table 1 below. Formulation of Rubber Compound Component parts by weight Natural rubber 50 SBR 50 Carbon black HAF 30 Zinc oxide 5 Aromatic oil 5 Stearic acid 1 Vulcanization accelerator DM 1 Sulfur 1.5 The vulcanized rubber test piece was coated with a curable adhesive (about 15-25 microns thick) composed mainly of chlorosulfonated polyethylene ("Chemlok 252" made by Lord Corp.). The test piece was preheated in an oven at 120°C for 30 minutes. Then, the test piece was disposed in a mold. The mold was filled by injection molding with completely dried nylon-66 ("CM-3001M" made by Toray Industries, Inc.). Immediately after demolding, the molding underwent post-heating in an oven at 120°C for 60 minutes. Thus there was obtained a test piece 13 of composite structure in which vulcanized rubber 11 and polyamide resin 12 are integrated as shown in Fig. 3 (plan view) and Fig. 4 (sectional view through section IV-IV of Fig. 3). Incidentally, this test piece 13 has the following dimensions. I 1 = 25.4 mm I 2 = 110 mm I 3 = 55 mm d 1 = 4 mm d 2 = 7 mm The thus obtained test piece 13 of composite structure was tested for adhesion according to ASTM D429, Method B, 90°. The results are shown in Table 2. Example 2 The same procedure as in Example 1 was repeated except that post-heating was not performed after demolding. The test piece was tested for adhesion. The results are shown in Table 2. Comparative Example 1 The same procedure as in Example 1 was repeated except that the vulcanized rubber test piece was disposed in the mold without preheating after the application of the curable adhesive. The test piece was tested for adhesion. The results are shown in Table 2. Comparative Example 2 The same procedure as in Example 2 was repeated except that the vulcanized rubber test piece was disposed in the mold without preheating after the application of the curable adhesive. The test piece was tested for adhesion. The results are shown in Table 2. Comparative Example 3 A molding of nylon-66 ("CM-3001N") made by Toray Industries, Inc.) and an unvulcanized rubber molding of the rubber compound used in Example 1 were bonded to each other with a curable adhesive ("Chemlok 220/205" made by Lord Corp.) to give a test piece of composite structure as shown in Figs. 3 and 4. The test piece was tested for adhesion. The results are shown in Table 2. It is noted from Table 2 that the process of the present invention enables the easy and efficient production of the vulcanized rubber-synthetic resin composite structure by injection molding. The resulting product has an extremely high adhesion strength between the vulcanized rubber and the synthetic resin which is comparable to that achieved by the conventional cure adhesion method. Example No. Comparative Example No. Items 1 2 1 2 3 Chlorination treatment no no no no - Adhesive (b) (b) (b) (b) (c) Pretreatment before injection (120°C, 30 min) yes yes no no - Post-heating after demolding (120°C, 60 min) yes no yes no - Adhesion strength (kg/inch) 41 28 9 0 38 Peel and failure 100R 85R 25R R/P 95R The present invention aims to solve the problems in the prior art. Accordingly, the preferred embodiment of the present invention aims to provide a process for producing a vulcanized rubber-synthetic resin composite structure in which the vulcanized rubber and the synthetic resin are bonded extremely firmly to each other. The preferred embodiment of the present invention further aims to provide a process for producing a vulcanized rubber-synthetic resin composite structure easily and efficiently at a low production cost and with a high productivity, without causing the degradation and deformation of the synthetic resins by heat history.

Claims: A process for producing a vulcanized rubber-synthetic resin composite structure which comprises forming a layer of a curable adhesive on the surface of the vulcanized rubber molding, said curable adhesive being composed mainly of chlorosulfonated polyethylene, heating the vulcanized rubber molding at 90-140°C for 10-90 minutes, disposing the vulcanized rubber molding in the heated state in a mold, injecting a molten resin into the mold, and demolding the composite structure after the setting of the injected resin. A process according to claim 1, wherein the vulcanized rubber-synthetic resin composite structure obtained after the injection of the synthetic resin is subjected to post-heating. A process according to claim 2, wherein the post-heating is performed at 90-140°C for 30-120 minutes. A process according to any one of claims 1 to 3, wherein the rubber component of the vulcanized rubber constituting the vulcanized rubber molding is natural rubber, synthetic rubber having a carbon-carbon double bond in the structural formula, butyl rubber, or chloroprene rubber. A process according to any one of claims 1 to 4, wherein the synthetic resin in a polyamide resin.

Inventors: IIZUMI SHINGO, TAKANO KAZUYA, IIZUMI, SHINGO, TAKANO, KAZUYA, Iizumi, Shingo, c/0 Bridgestone Corporation
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1989
Main classification: C08J5
IPC codes: C08J5, B29C45