POLYIMIDE COMPOSITE FILTER FABRICS

Abstract: Composite filter cloths (10) having a top layer (12) of P84 polyimide fiber and a depth filtration type fabric substrate (20) may be structured to have a higher particulate removal efficiency than that for the substrate layer (20) and a lower pressure drop than that of the top layer (12).

Description: FIELD OF INVENTION This invention relates to filter fabrics. It specially relates to filter fabrics having a utility for the removal of fine, sub-micron particulate matter from fluid streams, although it is not restricted thereto. BACKGROUND OF INVENTION Filter fabrics made from conventional synthetic fibers, non-limiting examples of which are fibers formed from polyesters, polyamides, polyethylene polypropylene and polyacrylates and glass remove particles from a fluid stream initially by a depth filtration mechanism. Such fibers have relatively regular cross-sections of low surface area. Particulate matter in the fluid stream is trapped in the body of the fabric in the interstices between the fibers thereof, to form a cake in the body of the fabric. It is only subsequent to the formation of the body cake that a surface cake builds up, the surface cake then effectively forming the filter medium. The accumulation of the particles inside the fabric creates an appreciable resistance to the flow of fluid through the filter, and correspondingly results in an increase in pressure drop across the filter. Fabrics which are composed of membranes laminated onto a fibrous substrate considerably reduce entrapment of the particles within the fabric. However, such membranes have an inherently high flow resistance due to the small pore size thereof, and again their use is accompanied by a high pressure drop across the filter. There has latterly been made available from Lenzing AG an aromatic polyimide fiber known under the trade name P84®. Microscopic examination of this fiber indicates it to have a heavily profiled structure of significantly greater surface area than that of conventional fibers employed in the manufacture of depth filtration filters. These polyimide fibers also have charged surface sites, which generate strong electrostatic fields. The fibers are found to intercept particulate matter primarily on the surface thereof in a cake filtration mechanism. Fluid flow through the P84 fabric may be gradually restricted particularly where the feed includes very fine particles. Such particles penetrate the fabric, and since the path resistance tends to be relatively uniform throughout the depth of the fabric, the probability of entrapment is relatively high. The fibers are also very expensive, making them cost-prohibitive except for specialty use in very high temperature filtration operations i.e. 200-250 C. It is an object of this invention to provide filter cloths having improved efficiency. It is a further object of this invention to provide filter cloths having a high particulate separation efficiency and accompanied therewith a low pressure build-up. It is another object of this invention to provide filter cloths that are economic. SUMMARY OF THE INVENTION In accordance with a principle aspect of this invention, a composite filter fabric comprises cloth having a composite structure comprising a first fabric layer consisting of a non-woven P84 polyimide fiber, and a substrate fabric layer formed from at least one fiber having a relatively regular cross-section and significantly lower surface area than that of said polyimide fabric; wherein the diameter of the fibers of the first layer is less than the diameter of the fibers of the substrate layer, and wherein the layers are bonded together. By P84 polyimide fiber is meant a polymer having the theoretical structure where n is an integer A first layer consisting of a plurality of staple fibers of P84 polyimide polymer consolidated through entanglement of the fibers, such entanglement being of the character produced by a needle punching operation. The composition fabric further comprises by a substrate layer of a depth filtration filter fabric; fibers of the depth filtration filter fabric having a diameter not substantially less than that of the staple fibers; and means for bonding the fist layer to the substrate layer. The substrate fibers include without limitation fibers from organic polymers such as polyester, polypropylene, polyethylene, nylon, aromatic polyamides, polyacrylates, polyphenylene sulfide, polytetrafluoroethylene, polybenzimidazole, and inorganic materials including glass, and mixtures thereof. The diameters of the fibers of the first layer and the substrate layer will desirably be selected in accordance with the nature of the particulate matter to be removed from the fluid stream, especially the particle size distribution thereof, so as to ensure the removal of particulate matter without unnecessarily restricting fluid flow through the filter. It is also a prime consideration that the ratio of the diameters of the fibers be selected such that the pressure drop across the substrate will be less, and preferably substantially less than that across the first layer. Accordingly it will be appreciated that the relative diameters of the fibers is only one factor to be considered, together with the path length through each of the layers and also the degree of consolidation of the layers. It is to be remarked that current technology and know-how permits the manufacture of P84 polyimide fibers on a commercial scale having a fineness of about 2 denier (2 g/km) only. Generally speaking the diameter of the substrate fibers will be not less than that of the P84 fibers. Suitably the ratio of the diameter of substrate fiber to that of the fiber of the first layer will be not less than about 1.5:1; and desirably will be in the range of about 1.5:1 to about 4:1, with a ratio of about 3:1 being preferred. The term diameter as used herein relates to the mean cross-sectional dimension of the buildup of the fibers of the layer. The substrate layer may be in the form of non-woven fabric, or woven fabric or mixtures thereof. Desirably the substrate layer comprises a non-woven fabric having a woven fabric such as a scrim entangled therewith, suitably by a needle punching operation. Also suitably, the first layer of fibers is bonded to the substrate layer by needle punching, preferably so as to entangle fibers of each layer with fibers of the other layer, desirably without completely penetrating to the outer side of the other layer. The first layer will normally comprise not less than about 5% of the composite filter fabric, expressed on a weight basis. Higher percentages of the first layer fabric will normally be found desirable, particularly where elevated temperature exposure maybe expected, but this will be accompanied by an increase in pressure build-up. Suitably a filter fabric having good all-round filtration characteristics will comprise from about 25 to about 35% by weight of the first layer fabric, with about 30% being preferred. These foregoing objects and aspects of the invention, together with other objects, aspects and advantages thereof will be more apparent from the following description of a preferred embodiment thereof, taken in conjunction with the following drawings, wherein: IN THE DRAWINGS FIG. 1 - shows in exploded, figurative form the component parts of a preferred, composite filter fabric of the invention; FIG. 2 - is similar to Fig. 1 and shows a sub-stage in the manufacture of the composite filter fabric; FIG. 3 - is similar to Fig. 1 but shows the component parts of the composite filter fabric in their combined form; FIG. 4 - is a flow diagram of the various steps in the manufacture of a preferred composite filter fabric, and FIG. 5 - shows comparative test results of a composite filter fabric and a conventional (control) filter fabric. DESCRIPTION OF THE PREFERRED EMBODIMENT Referring to the drawings in detail, in particular Figs 1 - 3 thereof, a composite filter fabric is identified therein by the numeral 10. Filter fabric 10 comprises a first, outer layer 12 which consists essentially of fibers 14 of P84 polyimide, as previously defined hereinabove, needle punched together at figuratively illustrated sites 16 to form a non-woven fabric 18. Filter fabric 10 further includes a substrate layer 20, which here comprises polyester fibers 22 needle punched together at sites 24 to form a non-woven fabric 26, and a polyester scrim 28. Substrate layer 20 is formed by needle punching non-woven fabric 26 onto scrim 28 at sites 32 so as to generally embed the scrim within the non-woven fabric. Following the formation of substrate layer 20, this layer is bonded to first layer 12 by needle punching fibers from each layer into the other layer. This last recited step is controlled such that the substrate fibers 22 do not penetrate to the outer surface of the first layer, so as not to form a potential low resistance flow path therethrough. The extent of penetration of polyimide fibers 14 into the substrate 20 is commensurate with providing a firm bonding of the layers 12 and 20 together so as to resist disintegration of the filter 10, but penetration is desirably minimized due to the much higher cost of fibers 12, and their providing no effective filtration capacity when embedded into the substrate layer. Filter fabric 10 is shrunk by heat setting in a hot air chamber at a temperature somewhat more elevated than that to which the fabric 10 will be exposed on a continuous basis during operation. During the heat setting step the filter fabric 10 is desirably tensioned at least across the width thereof to prevent non-uniform shrinkage and a resulting non-uniform outer layer 12. Following the heat setting step, the outer surface of first layer 12 is exposed to open flame in order to eliminate loose fibers, the presence of which facilitates attachment of particles to the surface of filter cloth 10, making cake removal more difficult during the fabric cleaning cycles. As a last step in the method, filter 10 is compressed by passage through heated calendering rolls in order to reduce the interstitial spacing between the fibers and control the permeability to desired levels. A composite filter fabric was found in accordance with the above method wherein P84 polyimide fibers had a fineness of 2 denier (2 g/km) and the fabric of the first layer 12 formed therefrom had a weight of 125 g/m². The substrate layer 20 was formed from a 6 denier (6 g/km) polyester unwoven fabric having a weight of 285 g/m² needle punched onto polyester spun yarn scrim having a weight of 50 g/m². The composite fabric is usable on a continuous basis at a temperature of about 150°C, and was heat set at a temperature of 195°C. The permeability of this composite fabric was about 60% greater than that of a non-composite P84 fabric of comparable weight and thickness. A further composite filter fabric was formed in accordance with the above method, and was tested for filter efficiency and compared with a conventional polyester filter fabric having a comparable weight and thickness, the characteristics of the two filter fabrics being as given in table 1. Samples of the two fabrics of Table 1 were compared for particulate removal efficiency and pressure buildup at various particle concentrations and flow rates. The particulate matter consisted of a dust taken from a fluidized bed recirculating type boiler. The particles had a median size of 0.445 µm., with 82.31% of the population below 1 µm. The duration of the runs was 20 hours. The separation efficiency and pressure buildup were measured simultaneously versus time. The selected particle concentrations were as follows: 1) 11 g/m³ (5.0 Grains/ft³) 2) 110 g/m³ (50 Grains/ft³) The air flow rates to which both fabrics were subjected were: 1) 1.22 m/min (4 ft/min) 2) 1.52 m/min (5 ft/min) 3) 2.13 m/min (7 ft/min) The separation efficiencies were found to increase from a lower value and then become invariant after about 10 hours of filtration. However, the separation efficiencies were significantly higher for P84/Polyester fabric than for 100% Polyester fabric at all operating conditions. The lowest value of the separation efficiency recorded for P84/Polyester at the beginning of data acquisition was 98.899%. The equivalent value for 100% Polyester was much lower at 97.721%. Also for P84/Polyester, the asymptotic values ranged from a minimum of 99.936% to a maximum of 99.992%. The equivalent values for 100% Polyester were significantly lower at 98.605% and 99.918%, respectively. The change in separation efficiency with time for one set of operating conditions is shown in graphical form in Fig. 5, and this typifies the results of all runs. The pressure buildup increased with time and then became invariant at about the same time as the separation efficiency reached an asymptotic value. For all operating conditions, the pressure buildup remained significantly lower for the P84/Polyester composite fabric. Table 2 contains the separation efficiency and pressure buildup after 20 hours of filtration for different air flow rates for both 100% Polyester and P84/Polyester fabrics. The results showed that, for the P84 Polyester fabric, an increase in the air flow rate from 1.22 m/min to 1.52 m/min resulted in an increase in the separation efficiency recorded. Beyond 1.52 m/min, the separation efficiency remained nearly constant as the air flow rate was increased. Table 2 also shows the effect of air flow rate on the pressure buildup. For P84/Polyester, the pressure buildup did not change appreciably although the separation efficiency increased. For 100% Polyester, the pressure buildup increased with increasing air flow rate.

Claims: A composite filter fabric comprising: a first non-woven layer (12) consisting only of P84® polyimide staple fibers (14) that have an irregularly, heavily profiled structure and charged surface sites which generate strong electrostatic fields, said first non-woven layer being consolidated through entanglement by a needle punching operation; a substrate layer (20) of a depth filtration filter fabric secured to the first layer (12) by needle punching; wherein the fibres (22) of the depth filtration filter fabric have a cross-sectional diameter not substantially less than that of said staple fibres (14) and have lower surface area than the staple fibres (14). A composite filter fabric according to claim 1, wherein the first non-woven layer (12) and the substrate layer (20) are secured together to produce an entanglement of the fibers of each said layer within the fibers of the other layer. A composite filter fabric according to claim 1 or claim 2, wherein the fibers (22) of the substrate filter fabric are formed from an organic polymer. A filter fabric according to claim 3, wherein the organic polymer is selected from polyesters, polypropylene, polyethylene, nylons, aromatic polyamides, polyacrylates, polyphenylene sulfide, polytetrafluoroethylene and polybenzimidazole. A filter fabric according to any one of claims 1 to 4, wherein the substrate layer (20) is in the form of a non woven fabric commingled with a scrim (28). A filter fabric according to claim 5, wherein the fibres (22) of the substrate layer (20) are formed of polyester. A filter fabric according to any one of claims 1 to 6, wherein the first layer (12) comprises not less than about 5% by weight of the weight of the filter fabric. A filter fabric as defined in claim 7, wherein said first layer (12) comprises from 25% to 35% by weight of the weight of the filter fabric. A filter fabric according to any one of claims 1 to 8, wherein the fibers (22) of the substrate layer (20) have a diameter of not less than about 1.5 times that of the diameter of fibers (14) of the first layer (12). A filter fabric according to claim 9, wherein the fibers (22) of the substrate layer (20) have a diameter of from 1.5 to 4 times that of the diameter of the fibers (14) of the first layer (12). A composite filter fabric according to claim 10, wherein the diameter of the fibers (22) forming the substrate layer (20) is about 3 times the diameter of said fiber (14) of said first layer (12). A filter fabric according to claim 1, wherein the fibers (14) of the first layer (12) have a fineness of about 2 denier and the fibers (22) of the substrate layer (20) have a fineness of about 6 denier. A composite filter fabric according to any one of claims 1 to 12, wherein the entanglement of the fibers of each layer with the fibers of the other layers is limited whereby the fibers (22) of the substrate layer (20) do not penetrate the outer surface of the first layer (12).

Inventors: AITKEN, MARK ROGER, NODDIN, EMERSON LEE
Applicants: ALBARRIE (EUROPE) LIMITED
Application year: 1989
Main classification: B01D39
IPC codes: B01D39, D04H1, D04H13