A process for paraffin isomerization of a distillate range hydrocarbon feedstock

Abstract: A process for paraffinic isomerization of a hydrocarbon feedstock, which has a paraffin content having no more than 20 carbon atoms per molecule, comprises contacting the feedstock with a crystalline aluminosilicate zeolite catalyst having pore openings defined by: (1) a ratio of sorption of n-hexane to o-xylene, on a volume percent basis, of greater than 3, which sorption is determined at a P/P₀ of 0.1 and at a temperature of 50°C for n-hexane and 80°C for o-xylene and (2) by the ability of selectively cracking 3-methylpentane (3MP) in preference to the doubly branched 2,3-dimethylbutane (DMB) at 540°C (1000°F) and 101 kPa (1 atmosphere) pressure from a 1/1/1 weight ratio mixture of n-hexane/3-methyl-pentane/2,3-dimethylbutane, with the ratio of rate constants k 3MP /k DMB determined at a temperature of 540°C (1000°F) being in excess of 2, e.g., ZSM-22, ZSM-23, ZSM-35 and mixtures thereof. The catalyst is combined with a Group VIII metal, and has a zeolite SiO₂/Al₂O₃ ratio of at least 20:1.

Description: The present invention relates to a process for paraffin isomerization, for example hydroisomerisation of a distillate range hydrocarbon feedstock. Various catalytic processes have been proposed for isomerizing n-paraffins so as to lower the pour point of distillate range hydrocarbon feedstocks. However, many available feedstocks contain nitrogen impurities (typically at least 20 ppm) which tend to poison conventional paraffin isomerization catalysts. An object of the present invention is therefore to obviate or alleviate this problem. Accordingly, the present invention resides in a process for paraffin isomerization of a hydrocarbon feedstock having a boiling range of 165 - 343°C and a paraffinic content of molecules with not more than 20 carbon atoms, and preferably no more than 16 carbon atoms, which includes contacting the paraffin-containing feedstock with a crystalline aluminosilicate zeolite catalyst having pore openings defined by: (1) a ratio of sorption of n-hexane to o-xylene, on a volume percent basis, of greater than 3, which sorption is determined at a P/P o of 0.1 and at a temperature of 50°C for n-hexane and 80°C for o-xylene and (2) by the ability of selectively cracking 3-methylpentane (3MP) in preference to the doubly branched 2,3-dimethylbutane (DMB) at 538°C (1000°F) and 101 kPa (1 atmosphere) pressure from a 1/1/1 weight ratio mixture of n-hexane/3-methyl-pentane/2,3-dimethylbutane, with the ratio of rate constants k 3MP /k DMB determined at a temperature of 538°C (1000°F) being in excess of 2, said catalyst including 0.01 to 10% wt. of a platinum Group metal incorporated into said zeolite by ion exchange, and having a zeolite SiO₂/Al₂O₃ ratio of at least 20:1, and said contacting being effected at a temperature of 199 - 454°C (390 to 850°F) and a pressure of 790 - 7000 kPa (100 to 1,000 psig). Preferably, said contacting is effected at a pressure of 1825 - 4240 kPa (250 - 600 psig). The expression, "P/P o , as utilized herein, is accorded its usual significance as described in the literature, for example, in "The Dynamical Character of Adsorption" by J.H. deBoer, 2nd Edition, Oxford University Press (1968) and is the relative pressure defined as the ratio of the partial pressure of sorbate to the vapor pressure of sorbate at the temperature of sorption. The ratio of the rate constants, k 3MP /k DMB , is determined from 1st order kinetics, in the usual manner, by the following equation: k=(1/T c )In(1/1-ε) where k is the rate constant for each component, T c is the constant time and ε is the fractional conversion of each component. The zeolite catalysts described above are effective for the isomerization of n-paraffins and are resistant to nitrogen poisons, especially those found in distillate range feedstocks, as a result of their specific pore size openings which are effective to exclude most nitrogen containing organic molecules from entering therein. Inasmuch as medium pore zeolites have in the past been considered as somewhat limited for purposes of isomerization as a result of their pore size, the present invention provides an unexpectedly efficient procedure and catalyst for effectively isomerizing paraffinic feedstocks, especially in hydrocarbon distillate range feedstock having nitrogen poisons. The group of medium pore zeolites which can be used in the process of the present invention includes ZSM-22, ZSM-23, and ZSM-35. ZSM-22 is described in U.S. Patent No. 4556477, ZSM-23 is described in U.S. Patent No. 4076842 and ZSM-35 is described in U.S. Patent No. 4016245. The metals used in the catalyst of the present invention are selected from platinum, palladium, iridium, osmium, rhodium and rhuthenium, and are preferably present in the amount of from 0.1% to 3% by weight of the zeolite. The zeolite can be supported in a binder selected from one of silica, alumina, silica-alumina, and titania. When the feedstock is distillate range feedstock, having a boiling point of 165 - 343°C (330 to 650°F), the catalyst of the present invention has been shown to resist poisoning by nitrogenous compounds under the conditions necessary to isomerize n-paraffins in the feedstock. Furthermore, a hydrocarbon feedstock having a substantial paraffinic content can be converted to reduce the boiling point 5-11°C (10 to 20°F) without the unwanted side effects of significant cracking which normally results from high temperature, high pressure procedures in the presence of a zeolitic catalyst. As a result, the feedstock can be treated without significant reduction of distillate range yield. The product resulting from this process contains a significantly greater amount of isoparaffinic compounds, i.e., branched hydrocarbon chains, than straight hydrocarbon chains. This is unlike the product resulting from hydrocracking processes which includes a greater amount of straight chain molecules. Consequently, the yield of nonparaffinic distillate is significantly increased. Thus, while other procedures have been found to be useful in reducing the paraffinic content by hydrocracking, the present invention has been found to be unexpectedly efficient in reducing the n-paraffin content by hydroisomerization while maintaining high distillate range yields. The following Examples illustrate the invention. Example 1 (Comparative) The isomerization selectivity of Pt/ZSM-5/Al₂O₃ was measured using N-hexadecane at 3550 kPa (550 psig) 277°C (531°F), H₂/HC=13.1 and 1 liquid hourly space velocity (LHSV). At 77% n-C₁₆ conversion, the selectivity (the ratio of the i-C₁₆ yield and the n-C₁₆ conversion) was only 0.30. Benzoquinoline was then added to the n-C₁₆ feed in an amount to obtain 20 ppm nitrogen. It was necessary to increase the reactor temperature 30°C (54°F) to maintain the n-C₁₆ conversion at 77 wt.%. The isomerization selectivity increased to 0.43. Example 2 The isomerization selectivity of Pt/ZSM-22/Al₂O₃ was measured as described in Example 1. 85 wt.% conversion of n-C₁₆ was obtained at 302°C (576°F) and the isomerization selectivity was 0.76. When 20 ppm nitrogen was added as benzoquinoline, the reactor temperature was increased 29°C (52°F) to maintain conversion, no change in isomerization selectivity was observed. Thus this catalyst showed better isomerization selectivity compared to ZSM-5 for a clean feed and in the presence of a nitrogen poison. Example 3 The performance of Pt/ZSM-23/Al₂O₃ for isomerization was tested as described in Example 1. At 320°C (608°F), 69 wt.% conversion of n-C₁₆ was observed with 0.60 isomerization selectivity. The reactor temperature was increased only 20°C (36°F) to maintain the n-C₁₆ conversion after benzoquinoline was added. This catalyst shows higher isomerization selectivity and better nitrogen resistance compared to Pt/ZSM-5/Al₂O₃ in Example 1. Example 4 Pt/ZSM-35/Al₂O₃ was used to isomerize n-C₁₆ at the conditions described in Example 1. 76 wt.% n-C₁₆ conversion was observed at 307°C (585°F) with 0.50 isomerization selectivity. When 20 ppm nitrogen as benzoquinoline was added the reactor temperature was increased by 60°C (108°F) to maintain conversion, however, the isomerization selectivity increased to 0.70. Although a larger temperature increase was required to maintain n-C₁₆ conversion activity compared to Pt/ZSM-5/Al₂O₃, the isomerization selectivity was much higher for Pt/ZSM-35/Al₂O₃ for a clean feed and for a feed containing nitrogen. The results of the above Examples are summarized in Table 1 below. Example 1 Example 2 Example 3 Example 4 n-C₁₆ Conversion w/o Nitrogen 77% 85% 69% 76% n-C₁₆ Conversion w/ Nitrogen 77% 85% 69% 76% i-C₁₆ Selectivity w/o Nitrogen 0.30 0.76 0.60 0.50 i-C₁₆ Selectivity w/ Nitrogen 0.43 0.76 0.60 0.70

Claims: A process for paraffin isomerization of a distillate range hydrocarbon feedstock having a boiling range of 165 - 343°C (330 - 650°F) and a paraffinic content of molecules with not more than 20 carbon atoms and containing nitrogen impurities of at least 20 ppm comprising: contacting said paraffin-containing feedstock with a catalyst including a crystalline zeolite catalyst having pore openings defined by: (1) a ratio of sorption of n-hexane to o-xylene, on a volume percent basis, of greater than 3, which sorption is determined at a P/P o of 0.1 and at a temperature of 50°C for n-hexane and 80°C for o-xylene and (2) by the ability of selectively cracking 3-methylpentane (3MP) in preference to the 2,3dimethylbutane (DMB) at 538°C (1000°F) and 101 kPa (1 atmosphere) pressure from a 1/1/1 weight ratio mixture of n-hexane/3-methyl-pentane/2,3dimethylbutane (DMB), with the ratio rate constants k 3MP /k DMB determined at a temperature of 538°C (1000°F) being in excess of 2, said catalyst including 0.01 to 10% wt. of a platinum Group metal incorporated into said zeolite by ion exchange, and having a zeolite SiO₂/Al₂O₃ ratio of at least 20:1, and said contacting being effected at a temperature of 199 - 454°C (390 to 850°F) and a pressure of 790 - 7000 kPa (100 to 1,000 psig). The process of Claim 1 wherein said crystalline aluminosilicate catalyst is selected from ZSM-22, ZSM-23 and ZSM-35. The process of Claim 1 or Claim 2 wherein said metal is selected from Pt, Pd, Ir, Os, Rh and Ru. The process of any preceding Claim wherein said metal content is from 0.1% to 3.0% by weight. The process of any preceding Claim wherein said zeolite is supported in a binder selected from silica, alumina, silica-alumina, and titania. The process of any preceding Claim wherein said paraffin content has molecules of no greater than 16 carbon atoms. A process according to claim 1 which is a hydroisomerisation process and wherin the catalyst comprises ZSM-22, ZSM-23 or ZSM-25.

Inventors: CHEN NAI YUEN, GARWOOD WILLIAM EVERETT, MCCULLEN SHARON BRAWNER, CHEN, NAI YUEN, GARWOOD, WILLIAM EVERETT, MCCULLEN, SHARON BRAWNER
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1989
Main classification: C10G45
IPC codes: C10G45, C07C5, B01J29