Glass cleaning composition

Abstract: A glass cleaning composition comprises an aqueous solution having a pH value greater than 2 but not greater than 4, the composition including an anionic surface active agent, phosphoric acid and an ethanolamine, the ethanolamine being in a sufficient quantity to combine with one valency of the phosphoric acid.

Description: This invention relates to a glass cleaning composition, particularly but not exclusively useful in cleaning the windscreens of motor and like vehicles. Various proposals have been made for cleaning windscreens to remove contaminants deposited thereon during the normal use of the vehicle. In particular, there was a proposal in Patent Specification No. 1081351, for the use of a cleaning composition which was acidic in nature as opposed to the usual alkaline solutions. The reason for this was that by using an acidic composition, it was possible to break down the electrochemical bonding which occurred between certain of the contaminants and the glass of the windscreen. The proposed composition was satisfactory for many years until it was found that, with advanced paints and painting techniques, there were instances where the paint was attacked by the composition and left an irreversible discolouration or other damage to the paintwork. The present invention seeks to provide an improved glass cleaning composition which, while maintaining its ability to break down the above electrochemical bonding, will nevertheless not harm the paints which are now used in automobile manufacture. According to the invention, a glass cleaning composition comprises an aqueous solution having a pH value greater than 2 but not greater than 4, the composition including an anionic surface active agent, phosphoric acid and an ethanolamine, the ethanolamine being in a sufficient quantity to combine with one valency of the phosphoric acid. Preferably the pH value of the solution is between 2.5 and 3.0. The acid may be orthophosphoric acid. The ethanolamine may be any one of monoethanolamine, diethanolamine or triethanolamine. If the ethanolamine is monoethanolamine, the ratio of acid to ethanolamine may be 1.7:0.5 by weight. If the ethanolamine is diethanolamine, the ratio of acid to ethanolamine may be in the range 1.5:1 to 2:1 by weight (preferably 1.7:1). If the ethanolamine is triethanolamine, the ratio of acid to ethanolamine may be 1.7:1.5 by weight. The ratio of surface active agent to phosphoric acid may be in the range 0.5:1 to 2:1. The invention also includes a concentrated aqueous solution which can be diluted solely with water to a concentration such as to produce a glass cleaning composition as above referred to. Two examples of the invention will now be described. Example 1. A composition with the following constituents was made up:- Constituent % by volume Industrial ethanol 50.0 Triethanolamine salt of a sulphonated dodecyl benzene 1.4 Industrial lauryl ether sulphate 0.45 Orthophosphoric acid (s.g. 1.70) 1.0 Diethanolamine 1.0 Water 46.15 To this could be added a trace amount of a dye. Of these constituents, the industrial ethanol is an anti-freeze, the next two are anionic surface active agents and may be used in the form known as EMPIMIN (Registered Trade Mark) KSN 60 and NANSA (Registered Trade Mark) T 60 respectively, orthophosphoric acid is the acidic component and diethanolamine is a buffer. The nominal pH value of this product is 3.5. Tests have shown that this product has excellent cleaning properties and no delterious effect on most types of paint. The addition of the buffering agent, diethanolamine, does not, as might be expected, reduce the efficacy of the composition but in fact adds to its operation by virtue of the fact that it is an emulsifying agent. Due to the inclusion of antifreeze, it can be used in low temperatures. Example 2. A composition with the following constituents was made up:- Component parts by weight Water 100.00 Commercial alkyl aryl sulphonate (27% active matter) 0.25 Commercial orthophosphoric acid 0.26 Diethanolamine 0.15 Tests have also shown that this is an excellent cleaning product. The nominal pH value is 2.6. The buffer component reacts with the acid by replacement of one of the hydrogen atoms. Thus theoretically, with orthophosphoric acid and diethanolamine, the compound di-hydrogen: diethanolamine: phosphoric acid is formed It will be understood that the above are only examples and are not intended to limit the invention. Other suitable surface active agents and/or antifreeze components may be used. The invention also envisages producing the glass cleaning composition in concentrated form which may, for example be diluted to twenty times its volume by the addition of water to bring it to a suitable concentration for use. One such concentrated form may suitably comprise a solution of the surface active agents, acidic components and ethanolamines in isopropyl alcohol, ethyl alcohol or methyl alcohol, the latter providing antifreeze properties. Although the composition has been designed particularly with automobile windscreens in mind, it may also be used in other circumstances for cleaning other types of glass objects.

Claims: A glass cleaning composition comprising an aqueous solution having a pH value greater than 2 but not greater than 4, the composition including an anionic surface active agent, phosphoric acid and an ethanolamine, the ethanolamine being in a sufficient quantity to combine with one valency of the phosphoric acid. A glass cleaning composition as claimed in claim 1, wherein the pH value of the aqueous solution is between 2.5 and 3.0. A glass cleaning composition as claimed in claim 1, or 2, wherein the acid is orthophosphoric acid. A glass cleaning composition as claimed in any one of claims 1 to 3, wherein the ethanolamine is monoethanolamine and the ratio of acid to ethanolamine is 1.7:0.5 by weight. A glass cleaning composition as claimed in any one of claims 1 to 3, wherein the ethanolamine is diethanolamine and the ratio of acid to ethanolamine is in the range 1.5:1 to 2.0 to 1 by weight. A glass cleaning composition as claimed in claim 5, wherein the ratio of acid to ethanolamine is 1.7:1 by weight. A glass cleaning composition as claimed in any one of claims 1 to 3, wherein the ethanolamine is triethanolamine and the ratio of acid to ethanolamine is 1.7:1.5 by weight. A glass cleaning composition as claimed in any one of claims 1 to 7, wherein the ratio of surface active agent to phosphoric acid is in the range 0.5:1 to 2:1 by weight. A concentrated aqueous solution which can be diluted solely with water to a concentration such as to produce a glass cleaning composition in accordance with any preceding claim.

Inventors: HUBER HERMANN JOSEPH, HUBER, HERMANN JOSEPH
Applicants: TRICO LTD, TRICO LIMITED
Application year: 1989
Main classification: C11D3
IPC codes: C11D1, C11D3, B01J23, C11D17, C11D10