Additives for curing fluoroelastomers containing bromine or iodine

Abstract: The emission of the highly toxic volatile products methyl bromides or iodides or ethyl bromides or iodides during the curing of fluoroelastomers containing bromine or iodine atoms with peroxides, is substantially reduced by adding to the cure mix small amounts of substances capable of combining with the radicals which give rise to the abovesaid toxid products, thereby preventing them from forming. This procedure does not significantly affect the cure trend and results.

Description: Curing fluoroelastomers containing, as cure sites, bromine or iodine atoms along the polymeric chain and/or at the end of the chain with organic peroxides is well known. In said fluoroelastomers, bromine or iodine is introduced into the elastomeric macromolecule by using, in the polymerisation step, brominated or iodidated comonomers such as, in particular, fluorobrominated olefins, brominated or iodidated fluorovinyl ethers, or brominated or iodidated compounds such as chain transfer agents. In peroxide curing use is generally made of organic peroxides of the aliphatic or cycloaliphatic type, or saturated or unsaturated alkylaromatics, such as for example: 2,5-dimethyl-2,5-di(ter.butylperoxy)hex-3-ene 2,5-dimethyl-2,4-di(ter.butylperoxy)hexane dicumylperoxide ter.butylperbenzoate ethyl-3,3-di(ter.butylperoxy)butyrate 1,1-bis(ter.butylperoxy)3,3,5-trimethylcyclohexane which gives rise, in the cure process, to the formation of methyl or ethyl radicals. These radicals, when combining with the bromine or iodine contained in the fluoroelastomer, can give rise to the above-mentioned methyl or ethyl bromides or iodides, which are highly toxic and probably also carcenogenic volatile products. Therefore, while the cured articles produced by means of peroxide curing of fluoroelastomers containing bromine or iodine exhibit excellent properties and characteristics at least partially higher than those of the fluoroelastomers cured by means of ions, such peroxide curing involves a serious health hazard for operators, and express prohibition of such processing is considered possible in the near future by the appropriate authorities. Thus, it is an object of the present invention to overcome the above-mentioned serious drawback by adding to the cure mix a substance capable of substantially reducing the emission of methyl or ethyl bromides or iodides during curing. In fact, surprisingly, it has been found that certain substance types introduced into the mix in a moderate amount, generally ranging from 0.1 to 3 parts by weight for 100 parts by weight of fluoroelastomer, are capable of substantially reducing the emission of said toxic products without sensibly altering the cure trend or the characteristics of the vulcanizate. The action mechanism of the additives according to the present invention is probably based on the fact that they are capable of combining with the methyl or ethyl radical deriving from the organic peroxide, thereby forming new radicals capable of continuing the cross-linking reaction, so preventing any formation of methyl or ethyl bromides or iodides. However, on the basis of such an assumption it is not possible to foresee which substances are actually suited for use as additives according to the invention; in fact, many substances which are surely capable of blocking the methyl and ethyl radicals and which drastically reduce the emission of the above said bromides and iodides, negatively interfere with the cure process, causing it to become extremely slow and inefficacious and giving rise to vulcanizates of very bad quality. According to the present invention a fluoroelastomeric composition containing bromine and/or iodine in the polymeric chain as peroxide cure sites, comprising organic peroxides of the aliphatic, cycloaliphatic or alkylaromatic type, either saturated or unsaturated, and an additive in an amount equal to 0.1-3 parts by weight for 100 parts by weight of fluoroelastomer, selected from the compounds belonging to the following classes: (a) Benzothiazole and derivatives thereof of general formula: wherein: X represents H, -SH, b) Maleamide derivatives of general formula: wherein A = H, or together with T forms a bond, T represents -OH, or together with A forms a bond; R represents H, alkyl with 1 to 6C, halogen, -NO₂ and when T forms a bond with A, R may be also in which the or each phenyl group may be replaced by a naphthyl group. c) Thiuram derivatives of general formula: wherein Y represents R' represents alkyl with 1 to 4C, (d) Diphenylguanidine derivatives of general formula: wherein R² represents H or alkyl with 1 to 6C. (e) Maleic anhydride. (f) Diaryl-formamidines. (g) Diazo- and triazo-dicyclodecenes derivatives. Preferred compounds for use as additives from class (a) are selected from benzothiazole disulphide, morpholin-2-benzothiazole sulphonamide or zinc mercapto-benzothiazole. Preferred compounds for use as additives from class (c) are selected from tetraalkylthiuram disulphide or zinc diethyldithiocarbamate. Preferred compounds for use a additives from class (d) are selected from compounds wherein R² represents H or CH₃. Preferably the additive is contained in an amount from 0.2 to 2 p.h.r. According to the present invention a process for curing a fluoroelastomer, wherein the fluoroelastomer is as defined above and is cured with an organic peroxide as defined above, is carried out in the presence of an additive in an amount as defined above and selected from compounds as defined above. Besides significantly reducing the emission of the toxic products methyl or ethyl bromide or iodide, in some cases by up to 90%, these additives impart to the curable composition the following improved characteristics: increase of the time which is necessary for the scorching to occur (scorching time) and, by consequence, a higher processing safety; decrease of the Mooney viscosity of the mix and therefore an improved processability; moderate influence on the cross-linking rate and yield at 180°C. All the additives indicated hereinbefore can be prepared according to known methods described in the technical literature. The fluoroelastomers, to which the present invention is applicable, are all those which contain bromine or iodine atoms as cure sites. Among the most well known, the following are to be considered copolymers of CH₂ = CF₂ with CF₃ -CF = CF₂ and optionally also with C₂F₄ and perfluorovinylethers, containing little amounts of bromine or iodine which are introduced by copolymerising a little amount of brominated or iodidated monomer such as brominated olefins, perfluorobromoalkyl-perfluorovinylethers, or also by using chain transfer agents consisting of bromo- or iodo-alkyl compounds. The mixes based on fluoroelastomers to be cured with peroxides, according to the present invention comprise, beside the organic peroxide, conventional ingredients such as carbon black and other reinforcing fillers, peroxide curing co-agents (for example triallyl isocyanurate), metal oxides or hydroxides (for example PbO, ZnO), and processing aids. The following examples are given merely to illustrate, but not to limit the present invention. The evaluation of the CH₃Br emission under curing conditions was generally carried out according to the following method: Methods for determining the CH₃Br emission 20g of a finely particled mix (polymer and fillers) are treated at 180°C in a closed reactor, for 30 minutes at a pressure of 0.5 kg/cm² abs. in a nitrogen atmosphere. Then the mix is cooled to 40-50°C and, as an interior standard, 1cc of A114 (C₂Cl₂F₄, b.p. = 4°C) is added. The gas phase is mixed and subjected to gaschromatographic analysis. Column: POROPAK Q T = 100°C In example 2, conversely, the actual emission occurring under practical curing conditions at 170°C is determined by determining the CH₃Br in air samples withdrawn from above the mold. Utilized elastomer: P.1 terpolymer of CH₂ = CF₂ 66.2% by moles, C₃F₆ 18.2%, C₂F₄ 15.2%, containing bromoperfluoroethylvinylether in an amount equal to 0.65% by weight of bromine. P.2 terpolymer of CH₂ = CF₂ 54.1% by moles, C₃F₆ 22.2%, C₂F₄ 22.9%, containing bromoperfluoroethylvinylether in an amount equal to 0.54% by weight of bromine. The ingredients of the mixes, besides the additive according to the invention, are, in parts by weight for 100 parts by weight of terpolymer, the following: 2,5-dimethyl-2,5-di-ter.butyl-peroxy-hexane at 45% on inert filler (Luperco 101XL), 3 parts; triallyl isocyanurate (TAIC) at 75% on inert filler, 4 parts; PbO, 3 parts; carbon black MT, 30 parts. The evaluation of the cure trend is carried out by determining the Δ torque (MH-ML) by means of an ODR, oscillating disc rheometer (Monsanto type), according to standard ASTM D 2084/81. Measurement is carried out at 180 o C, the maximum torque MH is determined after 12 minutes, by "arc 3". EXAMPLE 1 The tests were carried out using terpolymer P.1. The elastomer without the additive of the invention provided during curing a Δ torque equal to 71. In some tests, the low reduction of the CH₃Br emission was due to insufficient amount of additives; by increasing said amount within the above-cited range, it is possible to improved the effect (see for example tests 7 and 8). Test 21 is a comparison test and represents those products which drastically reduce the CH₃Br emission, but at the same time prevent or strongly reduce the curing. Example 2 Tests were carried out in order to check the correspondence between the reduction in CH₃ Br emission determined by means of the laboratory test described for example 1 and the actual reduction achieved in the curing process in the mold at 170°C under reaction conditions, determined by analysis of an air sample withdrawn from above the molded article immediately after having drawn the vulcanizate from the mold. The additive utilised was mercaptobenzothiazole disulphite (MBTS); a test was carried out without the additive in order to have a comparison of the values of the Δ torque and of the CH₃Br emission. The elastomer utilized was of the type P.2 described hereinbefore. The results are the average of analytical determinations on 5 air drawings. ADDITIVE PHR Δ MH-ML PERCENT REDUCTION OF CH₃Br EMISSION LABORATORY TESTS PERCENT REDUCTION OF CH₃Br EMISSION MOLDING TESTS - - 62 - - MBTS 0.25 64 79% 62% MBTS 0.5 66 85% 98% Example 3 Characterisation of the curable mixes and of the vulcanized product. The characteristics compared with those of the products formed when no additives were included in the mix. In particular, from table 3 it is apparent that the mixes containing the additive according to the invention exhibit a remarkably higher scorching time, a decrease of the Mooney scorch viscosity (at 135°C) and a decrease of the Mooney viscosity at 121°C; these characteristics are indicative of a better processability of the mix. Table 4 contains some characteristic values which provide idications about the cure trend. The characteristics of the cured material are reported in Table 5. EXAMPLE 4 The tests reported in Table 6 show that the reduction in CH₃Br emission and the cure trend vary with polymer type used and the bromine content. In all the tests reported in Table 6 the additive used was phenylmaleinimide: Other components of the mix were: - Luperco 3 p.h.r. - TAIC 4 p.h.r. - PbO 3 p.h.r. - carbon black 30 p.h.r. POLYMER ADDITIVE P.H.R. Δ TORQUE MH-ML % REDUCTION OF CH₃Br EMITTED P.1 - 71 - P.1 1,5 76 15% P.41 - 62 - P.41 1,5 55 29% P.2+P.41(+) mix - 65 - P.2+P.41(+) mix 1,5 64 37% Polymer P.41 contains: CH₂ = CF₂ 53,4%; C₂F₄ 23,9%; C₃F₆ 22,7%, and bromovinylether in an amount equal to 0.93% of Br. (+) Bromine content of the polymeric mix: Br = 0.72%.

Claims: Claims for the following Contracting States : AT, BE, FR, DE, GB, NL, SE A fluoroelastomeric composition containing bromine and/or iodine in the polymeric chain as peroxide cure sites, comprising organic peroxides of the aliphatic, cycloaliphatic or alkylaromatic type, either saturated or unsaturated, and an additive in an amount equal to 0.1-3 parts by weight for 100 parts by weight of flurooelastomer, selected from the compounds belonging to the following classes: (a) Benzothiazole and derivatives thereof of general formula: wherein: X represents H, -SH, b) Maleamide derivatives of general formula: wherein A = H, or together with T forms a bond, T represents -OH, or together with A forms a bond; R represents H, alkyl with 1 to 6C, halogen, -NO₂ and when T forms a bond with A, R may be also in which the or each phenyl group may be replaced by a naphthyl group. c) Thiuram derivatives of general formula: wherein Y represents represents alkyl with 1 to 4C, (d) Diphenylguanidine derivatives of general formula: wherein R² represents H or alkyl with 1 to 6C; (e) Maleic anhydride. (f) Diarylformamidines. (g) Diazo- and triazo-dicyclodecenes derivatives. A fluoroelastomeric composition according to claim 1, wherein the additive is contained in an amount from 0.2 to 2 p.h.r. A fluoroelastomeric composition according to any preceding claim wherein the additive used is a benzothiazole derivative and is preferably selected from benzothiazole, 2-mercaptobenzothiazole, benzothiazole disulphide, morpholin-2-benzothiazole sulphonamide or zinc mercapto-benzothiazole. A fluoroelastomeric composition according to claims 1 or 2 wherein the additive used is a thiuram derivative and is preferably selected from tetra-alkylthiuram disulphide or zinc diethyldithiocarbamate. A fluoroelastomeric composition according to claim 1 or 2 wherein the additive used is a diphenylguanidine derivative and is preferably selected from compounds wherein R² represents H or CH₃. A process for curing a fluoroelastomer wherein the chain fluoroelastomer is as defined in claim 1 and is cured with an organic peroxide as defined in claim 1, and characterised in that the process is carried out in the presence of an additive in an amount as defined in claim 1 and selected from compounds as defined in claim 1. A process for curing a fluoroelastomer according to claim 6 wherein the additive is contained in an amount as defined in claim 2. A process for curing a fluoroelastomers according to claim 6 or claim 7 wherein the additive is selected from compounds as defined in any of claims 3, 4 and 5. Claims for the following Contracting State : ES A method for forming a fluoroelastomeric composition containing bromine and/or iodine in the polymeric chain as peroxide cure sites, comprising mixing with the fluoroelastomer, organic peroxides of the aliphatic, cycloaliphatic or alkylaromatic type, either saturated or unsaturated, and an additive in an amount equal to 0.1-3 parts by weight for 100 parts by weight of flurooelastomer, selected from the compounds belonging to the following classes: (a) Benzothiazole and derivatives thereof of general formula: wherein: X represents H, -SH, b) Maleamide derivatives of general formula: wherein A = H, or together with T forms a bond, T represents -OH, or together with A forms a bond; R represents H, alkyl with 1 to 6C, halogen, -NO₂ and when T forms a bond with A, R may be also in which the or each phenyl group may be replaced by a naphthyl group. c) Thiuram derivatives of general formula: wherein Y represents R' represents alkyl with 1 to 4C, (d) Diphenylguanidine derivatives of general formula: wherein R² represents H or alkyl with 1 to 6C; (e) Maleic anhydride. (f) Diarylformamidines. (g) Diazo- and triazo-dicyclodecenes derivatives. A method according to claim 1, wherein the additive is contained in an amount from 0.2 to 2 p.h.r. A method according to any preceding claim wherein the additive used is a benzothiazole derivative and is preferably selected from benzothiazole, 2-mercaptobenzothiazole, benzothiazole disulphide, morpholin-2-benzothiazole sulphonamide or zinc mercapto-benzothiazole. A method according to claims 1 or 2 wherein the additive used is a thiuram derivative and is preferably selected from tetra-alkylthiuram disulphide or zinc diethyldithiocarbamate. A method according to claim 1 or 2 wherein the additive used is a diphenylguanidine derivative and is preferably selected from compounds wherein R² represents H or CH₃. A process for curing a fluoroelastomer wherein the chain fluoroelastomer contains bromine and/or iodine in the polymeric chain as peroxide cure sites and is cured with an organic peroxide as defined in claim 1, and characterised in that the process is carried out in the presence of an additive in an amount as defined in claim 1 and selected from compounds as defined in claim 1. A process for curing a fluoroelastomer according to claim 6 wherein the additive is contained in an amount as defined in claim 2. A process for curing a fluoroelastomers according to claim 6 or claim 7 wherein the additive is selected from compounds as defined in any of claims 3, 4 and 5.

Inventors: CHIODINI GRAZIELLA, MINUTILLO ANNA, CHIODINI, GRAZIELLA, MINUTILLO, ANNA
Applicants: AUSIMONT SPA, AUSIMONT S.P.A.
Application year: 1989
Main classification: C08L27
IPC codes: C08K5, C08L27