Fatty emulsion stabilized by a polysaccharide derivative

Abstract: The invention is a fatty emulsion stabilized by a polysaccharide derivative, characterized in that the fatty emulsion contains a polysaccharide derivative which is substituted by a fatty acid or cholesterol at a pro­ portion of 0.5-5 per 100 sugar units.

Description: The present invention relates to emulsions used in medicine, food and the like, more particularly to fatty emulsions stabilized by polysaccharide derivatives which can embed fat-soluble substances in large quantities. As medicine carriers, albumin, fibrinogen, erythrocyte ghost, gelatin, starch, polylactide, polyglyceride, dextran, polyethyl carbonate, liposomes, emulsions and the like have been used. In these materials, liposomes and O/W emulsions are promising. It is well-known that, when the surface of a liposome is coated with a polysaccharide derivative by their mutual interaction of non-covalent bonds, the liposome structure is stabilized. (Japanese Laid-Open Patent Publication Nos. 58-49311 and 61-69801). Lately, as mentioned above, liposomes and O/W emulsions are promising as medicine carriers. Among them, liposomes have disadvantages which are the lack of chemical and mechanical stabilities and the difficulty of long-term preservation. The present inventors found that the structural stability of liposomes was considerably improved by coating the liposome surface with a polysaccharide. However, a satisfactory stability is not yet obtained. On the other hand, on O/W emulsion comprising lecithin, oil and water is excellent as a carrier of fat-soluble medicines because it is possible to embed them in large quantities. Furthermore, fatty emulsions (lipid microsphere) have been conventionally prepared by emulsifying oil with phospholipids of negative electric charge for obtaining the colloid stability. When the surface electric charge of particles is neutralized by the presence of calcium ions and the like, the embedding of fat-soluble medicines, the pH change in the system, etc., these fatty emulsions tend to associate or aggregate. Accordingly, there are problems in regard of the colloid stability. The present inventors have conducted research for resolving the above problems and for stably emulsifying oil with emulsions other than phospholipids and they have found that oil is stably emulsified by using polysaccharide derivatives which can efficiently improve the structure stability of liposomes. Then, they have found fatty emulsions stablized by polysaccharide derivatives. An object of the present invention is to provide colloid-chemically and biochemically stable fatty emulsions which can embed and maintain fat-soluble materials in large quantities. The present invention provides a composition containing a polysaccharide derivative substituted by cholesterol to an extent of 0.5 to 5 per 100 sugar units, characterised in that the composition is a fatty emulsion which is stabilized by the polysaccharide derivative alone. The polysaccharide derivative is preferably a pullulan, an amylopectin or a dextrin, more preferably N-[2-(cholesteryloxycarbonylamino)ethyl]carbamoylmethylated pullulan. The invention will now be described further with reference to the drawings, in which: Fig. 1 is a figure of ESR signal intensities showing the stability of the emulsions obtained in Example 1. Fig. 2 is a transmission electronic micrograph in which the particle structure of the emulsion of Sample 3 in Example 1 is shown. Fig. 3 shows grain size distribution of Sample 3 in Example 1. Fig. 4 shows ESR signal intensities that the stability of the product obtained in Example 2 are compared with the stability of the commercially available product. Fig. 5 shows ESR signal intensities that the stability of the product obtained in Example 2 are compared with the stability of the commercially available product in the presence of CaCl₂. In Figures 4 & 5, o shows the results obtained by using five emulsions of the present invention and x shows the results obtained by using a commercially available lipid microsphere. The polysaccharide derivative to be used in accordance with the present invention can be obtained from natural or synthetic products. As the polysaccharide which constitutes the polysaccharide derivative, pullulan, amylopectin, amylose, dextrin, cyclodextrin, dextran, hydroxyethyldextran, mannan or the like can be exemplified. The polysaccharide derivative is a compound in which the hydroxy groups of the polysaccharide are substituted by choresterol to an extent of 0.5 to five per 100 of sugar units. When the proportion is less than 0.5, a stable fatty emulsion cannot be obtained. When the proportion is more than 5, it is difficult to synthesize the polysaccharide derivative. The polysaccharide derivative preferred in particular is a compound in which the hydroxy groups of carbons situated in 6- or 3-positions of the sugar skeleton are substituted by -OCH₂CONHCH₂CH₂NHR wherein R is H or a cholesteryloxycarbonyl group, and the hydroxy groups are substituted by the above formulae wherein R is a cholesteryloxycarbonyl group at a proportion of 0.5 to three per 100 of sugar units. For bonding a cholesterol to a polysaccharide directly ethylenediamine, for example, may be used as a spacer in view of the steric hindrance of the cholesterol and the polysaccharide. Firstly, primary hydroxy groups (in 6-position) of the polysaccharide having high reactivities are carboxymethylated under alkali conditions. Then, the compound obtained and ethylenediamine are reacted with a condensation agent (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC)) to obtain amide bonds. Finally, the amide obtained and cholesteryl chloroformate are reacted in an anhydrous system to introduce cholesterol groups in the polysaccharide. The fatty emulsion of the present invention can contain water and oil in addition to the above polysaccharide derivative. As oil to be used, fish oil, vegetable oil, such as soy bean oil, sesame oil, rape oil, palm oil and cottonseed oil, fatty acids, fatty esters, middle length chain fatty acid triglycerides and mixtures of these can be exemplified. The ratio of the polysaccharide derivative of the present invention and the oil is preferably 0.1 to 1.0 (wt/wt) so as to form a stable emulsion. As water, pure water such as distilled water for injection and sterilized water, glucose liquid and physiological sodium chloride solution can be used. The concentration of the fatty emulsion of the present invention is preferably high. However, when the concentration is too high, the density and the viscosity become too high. Practically, the ratio of oil / water is 0.01-0.5 (wt/wt). The fatty emulsion of the present invention can dissolve fat-soluble anticancer agents, fat-soluble compounds such as antibiotics, steroid hormones and prostaglandins in large quantities in the oil phase and it can be used as a solubilizer of these fat-soluble substances. Accordingly, when the fatty emulsion of the present invention is used as a medicine carrier, it can be given by the use of an intravenous injection, an intraarterial injection or an intralymphangial injection, or directly to a diseased part. Specifically, the polysaccharide derivative to be used in accordance with the present invention contributes to improve the stability of the colloidal chemical structure of oil drops and to develop the cell specificity required to targetting treatments and shows ideal properties as the medicine carrier. The sugar chains are concerned in the mechanism of information transmission in vivo. By changing the kind of the polysaccharide which constitutes the polysaccharide derivative to be used in accordance with the present invention, for example, by introducing a sialic acid residue or an amino sugar chain, or by phosphorizing the sugar chains, the cell recognition properties of the oil drops themselves which are coated with the polysaccharide can be artificially changed. By binding an antibody to the polysaccharide derivative, an emulsion capable of targetting the aimed part by the antigen-antibody reaction can be prepared. For preparing the emulsion of the present invention, various homogenizers such as a Manton-Gory type homogenizer and the like and an ultrasonic generator of high output power can be used. For controlling the particle diameters of the oil drops after the emulsification, gel filtration or ultracentrifugation can be conducted. The emulsion of the present invention principally comprises oil and water in addition to the polysaccharide derivative. Furthermore, isotonic agents such as glycerin and anti-oxidizing agents for oil can be added to the emulsion. According to the present invention, fat-soluble materials can be emulsified in water or solubilized by homogeneous dispersion. Especially, the fat-soluble medicines can be solubilized in large quantities and targetting treatments can be conducted. As a result, medical lipid microspheres which are ideal for the fat-soluble medicines can be provided. The fatty emulsion can be used as a carrier for the fat-soluble medicines and can be broadly used in fields of food chemistry and the other industry. The following Examples illustrate the present invention more specifically. Synthesis Example 1 Synthesis of carboxymethylated pullulan Pullulan (average molecular weight 50,000) 3.0 g (1.9 x 10⁻² mole monosaccharide units) was charged in a 200 ml flask of an eggplant type and an aqueous solution 74 ml of 1.35 M sodium monochloroacetate was added to dissolve the pullulan thoroughly. An aqueous solution 10 ml of 10 N sodium hydroxide was added with stirring on a magnetic stirrer and 16 ml of distilled water was added. The solution obtained contained 1 M sodium monochloroacetate and 1 N sodium hydroxide. The solution was allowed to react for seven hours at 25°C with stirring. (Carboxy methyl groups at a proportion of about 10 per 100 g of monosaccharide units were introduced). Then, an aqueous solution 20 ml of 1 M sodium dihydrogen phosphate (1.0 x 10⁻² moles) was added to the reacted solution. The reaction was stopped at pH 7 by adding an aqueous solution of 6 N hydrochloric acid and an aqueous solution of 1 N hydrochloric acid. The obtained solution was transferred to a dialysis tube and dialyzed against distilled water. The dialysis was continued with 1 liter x 15 changes of distilled water. The absence of free monochloroacetic acid was confirmed by UV measurement after concentrating the dialyzed outer liquid to about one-hundred. Yield: 2.96 g (1.8 x 10⁻² mole monosaccharide units). Synthesis of N-(2-aminoethyl)carbamoylmethylated pullulan Carboxymethylated pullulan 2.9 g (1.8 x 10⁻² mole monosaccharide units) obtained as described above was charged in a 200 ml flask of an eggplant type and 40 ml of distilled water was added to dissolve throughly carboxymethylated pullulan. Then, an aqueous solution of 0.1 N sodium hydroxide and an aqueous solution of 0.1 N hydrochloric acid were added with stirring on a magnetic stirrer to obtain a solution of pH 4.7. Further, ethylenediamine dihydrochloride 1.6 g (1.2 x 10⁻² mole) was added and EDC hydrochloride 2.3 g (1.2 x 10⁻² mole) which was divided into three lots was added at 10 minutes intervals to adjust the pH value of the solution to pH 4.7. The mole ratio of the solutes in the reaction system was carboxymethylated pullulan : ethylenediamine : EDC = 3 : 2 : 2. The mixed solution was allowed to react for seven hours at 25°C with stirring while maintaining at pH 4.7. (N-(2-Aminoethyl)carbamoylmethyl groups at a proportion of about 3 per 100 of monosaccharide units were introduced). Then, the reacted solution was transferred to a dialysis tube and dialyzed against distilled water. The dialysis was continued with 1 liter x 15 changes of distilled water. The absence of free ethylenediamine was confirmed by a ninhydrin reaction after concentrating the dialyzed outer liquid to about one-hundredth. Yield: 2.81 g (1.7 x 10⁻² mole monosaccharide units). Synthesis of N-[2-(cholesteryloxycarbonylamino)ethyl]carbamylmethylated pullulan N-(2-Aminoethyl)carbamoylmethylated pullulan 2.7 g (1.7 x 10⁻² mole monosaccharide units) was charged in a 100 ml flask of an eggplant type equipped with a reflux condenser which was sealed with a calcium chloride tube and anhydrous dimethyl sulfoxide 30 ml was added with stirring on a magnetic stirrer to dissolve throughly N-(2-aminoethyl)carbamoylmethylated pullulan. Then, anhydrous pyridine 2 ml was added and the flask was heated at 60-70°C in an oil bath. The other hand, cholesteryl chloroformate 0.77 g (1.7 x 10⁻³ mole) was charged to a sample bottle and anhydrous dimethylformamide 5 ml was added. The mixture was heated and cholesteryl chloroformate was throughly dissolved. The cholesteryl chloroformate solution obtained was added to the above N-(2-aminoethyl)carbamoylmethylated pullulan solution. The mole ratio of the solutes in the reaction system was N-(2-aminoethyl)carbamoylmethylated pullulan : cholesteryl chloroformate = 10 : 1. The mixed solution was allowed to react for seven hours at 60-70°C with stirring. Then, the hot solution was added dropwise to ethanol 200 ml to precipitate a polysaccharide. The polysaccharide obtained by filtration was dissolved in distilled water 100 ml. The solution obtained was dialyzed against distilled water. The dialysis was continued with 1 liter x 10 changes of distilled water. Then, impurities (e.g. fibers of filter paper) were removed by filtration and the filtrate was lyophilized. Yield: 2.03 g (1.3 x 10⁻² mole monosaccharide units). The amount of the introduced cholesterol per 100 of monosaccharide units was calculated from a proton integral ratio of polysaccharide and cholesterol which are obtained by ¹H-NMR measurement. Using the above process, the final product CHP-50-1.9 was obtained. (CHP: cholesterol-modified pullulan, 50: average molecular weight (MW = 50,000), 1.9: the numbers of the substituted cholesterol per 100 of monosaccharide units). Example 1 Changing the ratio of the obtained polysaccharide derivative (CHP-50-1.9) and oil (a fatty acid triglyceride of medium chain length : Panasate 800 produced by Nippon Oil & Fats CO., Ltd.), fatty emulsions of Samples 1,2 and 3 were prepared. In the process for emulsifying, using a probe type sonicator (200 W, Model UR-200P, manufactured by Tommy Company in Japan), the samples were prepared by ultrasonic treatment at 70°C for 15 minutes in a stream of N₂. The polysaccharide derivative (CHP-50-1.9) used in the experiments is the pullulan cholesterol derivative obtained the above Synthesis Example and the molecular weight of pullulan was 50,000 and the numbers of the substituted cholesterol was 1.9 per 100 of monosaccharide units. For comparison, an emulsion of Sample 4 was prepared by using the same method as in the above method from a non-treated pullulan. The emulsified conditions of the emulsion obtained were firstly estimated with the naked eye. The results are shown in Table 1. The emulsified conditions of Samples 1,2 and 3 are good. Sample CHP-50-1.9 /mg Panasate 800 /mg Glycerin /mg Water /ml Emulsified conditions 1 10 20 25 1 o 2 20 100 25 1 o 3 50 100 25 1 o 4 10 20 25 1 x o ... Good emulsified condition (homogeneous white turbidity condition) x ... No Good. Small liberated and phase-separated oil drops floated on the emulsified liquid surface. Estimation of stability of the emulsified liquid by ESR method To the emulsified liquid 3 ml of Sample 3 in Table 1, 4.3 µg methyl 12-doxylstearate (12-NS)) of an ESR probe was added. The probe was solubilized by ultrasonic treatment at 70°C for 2 minutes in a stream of N₂. When the emulsified liquid was unstable, oil drops condensed or fused, and the water phase and the oil phase separated. Since the above 12-NS was dissolved in the oil phase only, when the emulsified liquid was stable, the 12-NS was homogemeously dispersed in the emulsified liquid and the ESR signal strength was always kept constant. However, when the oil phase and the water phase were separated, the oil phase having small specific gravity floated on the surface of the solution in a tube for the ESR measurement and the ESR signal strength lowered. By using the above phenomena, the ESR signal strength of the 12-NS was measured every given period of time and the colloidal stability of the emulsified liquid was estimated. By using the ESR method, the stability of Samples 1,2,3 and 4 in Table 1 was compared. The results are shown in Fig. 1. As shown in Fig. 1, when the ratio of polysaccharide derivative / oil (wt/wt) is 0.1 or more, the stable emulsions are obtained. Observation under an electron microscope Sample 3 in Table 1 was observed under a transmission electron microscope (JEM-100SX, JEOL, X25,000). After the sample was dyed with uranyl acetate, it was fixed on a copper mesh coated with a colloidal-carbon film and observed. In Fig. 2, a transmission electron microscope photograph of the sample is shown. Oil drops having a particle diameter of 0.5 µm and less can be observed. Furthermore, the sample was observed under a scanning electron microscope (JSM-T100, JEOL, X7500). After the sample was adsorbed on a filter paper (Wattman NO. 2), it was dyed with a glutaraldehyde / malachite green liquid and fixed with osmium tetroxide. Then the sample was deposited with gold and observed. Oil drops having a particle diameter of 0.5 µm and less can be observed. Measurement of grain size distribution The grain size distribution of Sample 3 in Table 1 was measured with a device for measuring grain size distribution (NICOMP 370HPL, Pacific Science Company). The results are shown in Fig. 3. In this experiment, it was found that the emulsion prepared had an average particle diameter of 0.3 µm and that the particle size was normally distributed. Example 2 Using the same constituents as used in Sample 3 of Example 1 except that the CHP-50-1.9 was changed to several polysaccharide derivatives, emulsions were prepared. The stability of these emulsions was observed with the naked eye. The same emulsifying method as in Example 1 was used. Three kinds of polysaccharide derivatives are used: CHAp-112-2.0 (amylopectin having a molecular weight of 112,000 and substituted cholesterol 2.0 per 100 of monosaccharide units), CHD-176-1.7 (dextran having a molecular weight of 176,000 and substituted cholesterol 1.7 per 100 of monosaccharide units) and CHP-50-1.9 (pullulan having a molecular weight of 50,000 and substituted cholesterol 1.9 per 100 of monosaccharide units). The results are shown in Table 2. Stable emulsions were obtained without depending on the kinds of polysaccharides. Sample Polysaccharide derivatives Emulsified After the preparation Conditions One month after 1 CHAp-112-2.0 o o 2 CHD-176-1.7 o o 3 CHO-50-1.9 o o o ... Good emulsified condition (homogemeously white turbidity condition) Example 3 Using the same constituents and conditions as used in Sample 3 of Example 1 except that Panasate 800 was changed to several kinds of oil, emulsions were prepared. The stability of these emulsions was observed with the naked eye. The same emulsifying method as in Example 1 was used. The results are shown in Table 3. Stable emulsions were obtained without depending on the kind of oil. Sample Oil Emulsified Conditions After the preparation One month after 1 Panasate 800 o o 2 Soy bean oil o o 3 Fish oil o o 4 Perilla oil o o 5 α-Linolenic acid o o o ... Good emulsified condition (homogemeously white turbidity condition) Example 4 The 12-NS was embeded as a probe. The stability of the emulsions of the present invention and the stability of a commercially available lipid microsphere were compared by the ESR method. Five emulsions of the present invention were prepared by the same method as in Example 2. The results are shown in Fig. 4. When the 12-NS was added as a probe, the commercially available lipid microshpere became unstable and the phases were immediately separated. On the other hand, all of the emulsions of the present invention were stable. Example 5 When the emulsions of the present invention were injected in a blood vessel, the stability of emulsions to Ca (II) ion under physiological conditions should be considered. The stability of the emulsions of the present invention and the stability of a commercially available lipid microsphere were compared in the presence of CaCl₂ by the same ESR method as in Example 4. Five emulsions of the present invention were prepared by the same method as in Example 2. The results in the presence of CaCl₂ (5 mM) are shown in Fig. 5. The commercially available lipid microsphere became unstable in the presence of CaCl₂ (5 mM) and the phases were easily separated. On the other hand, all of the emulsions of the present invention was very stable in spite of the presence CaCl₂.

Claims: A composition containing a polysaccharide derivative substituted by cholesterol to an extent of 0.5 to 5 per 100 sugar units, characterised in that the composition is a fatty emulsion which is stabilized by the polysaccharide derivative alone. A composition as claimed in claim 1, wherein the polysaccharide derivative is a pullulan, an amylopectin or a dextrin. A composition as claimed in claim 2, wherein the polysaccharide derivative is N-[2-(cholesteryloxycarbonylamino)ethyl]carbamoylmethylated pullulan.

Inventors: SUNAMOTO JUNZO, YAMAGUCHI SHIGEHIKO, SUNAMOTO, JUNZO, YAMAGUCHI, SHIGEHIKO
Applicants: NIPPON OILS & FATS CO LTD, NIPPON OIL AND FATS COMPANY, LIMITED
Application year: 1989
Main classification: B01F17
IPC codes: A23L1, B01F17, B01J13, C08B37, A61K47, A61K9