Process for preparing a perovskite type superconductor film

Abstract: A perovskite type superconductor film having a high content, almost a single phase, of high Tc phase, is formed by the steps of: depositing at least one first film of a first material (e.g., a composite oxide of Bi-Sr-Ca-Cu-O system or Tl-Ba-Ca-Cu-O system) con­ stituting a perovskite type superconductor over a substrate; depositing at least one second film of a second material containing an oxide or element (Bi₂O₃ , Tl₂O₃ , PbO x , etc., particularly PbO x ) having a vapor pressure of more than 10 ⁻⁴Pa at 800°C at least as a main component over the substrate; to thereby form a stack of the first and second films; and heat treating the stack of the first and second films to form the perovskite type superconductor film on the substrate.

Description: The present invention relates to a process for preparing a perovskite type superconductor film, particularly Bi-(Pb)-Sr-Ca-Cu-O system with a high content of the high Tc phase, i.e., having a high critical temperature Tc of superconductivity. Research and development into high temperature superconductive materials exhibiting superconductivity at above the boiling point of liquid nitrogen is proceeding rapidly, and investigations into practical applications therefor are also underway. Particularly, superconductors having a critical temperature Tc above 100 K are under investigation because they advantageously have a large temperature margin for liquid nitrogen application, theoretically having an increased critical current density Jc and critical magnetic field Hc. Known superconductors having a critical temperature Tc above 100 K are Bi-Sr-Ca-Cu-O and Tl-Ba-Ca-Cu-O systems. These Bi- and Tl- systems have the advantages of a resistance to water and oxygen degradation. Nevertheless, the Bi- and Tl-system superconductors have a disadvantage in that a low Tc phase is easily formed and the formation of a single high Tc phase is difficult. The Bi-system is typically a mixed phase formed of a low Tc phase with a critical temperature Tc of about 80 K and a high Tc phase with a Tc of about 110K. The Tl-system is typically a mixed phase formed of a low Tc phase with a critical temperature Tc of about 105 K and a high Tc phase with a Tc of about 125 K. The formation of isolated high Tc phases has not been accomplished. A new high TC Bi-Sr-Ca-Cu-O system superconductor was found by Maeda et al (Jpn. J. Appl. Phys. 27, 1988, L209). It was also found that this system contains three superconducting phases represented by the formula Bi 2 Sr 2 Ca n-1 Cu n O x . The system contains a first phase corresponding to n=1 in the formula and having a Tc of 7 K, a second phase corresponding to n=2 and having a Tc of 80K, and a third phase corresponding to n=3 and having a Tc of 105 K. With the increase of n from 1 to 3, the number of CuO layers in the crystal structure is increased from 1 to 3 and the c axis of the crystal is elongated from 2.4nm to 3.0 nm to 3.7 nm. Takano et al reported that the volume occupied by the high Tc phase is increased by partially substituting Pb for Bi (Jpn. J. Appl. Phys. 27, 1988, L1041), but the role of Pb is not clear at present. In a typical process for preparing a superconductor film of, for example, a Bi-Sr-Ca-Cu-O system superconductor, an oxide is deposited on a substrate of MgO, SrTiO 3 , etc. by sputtering, evaporation, etc., followed by a heat treatment to react the deposited film, thereby to form a superconducting film. There is a need to provide a process for reproducibly forming a single phase film, having a high Tc phase, of the Bi-(Pb)-Sr-Ca-Cu-O system. The present invention provides a process for preparing on a substrate a film of a perovskite-type Bi-(Pb)-Sr-Ca-Cu-O system superconductor having a high content of a phase having a high Tc, said process comprising: providing a film on a substrate, said film having an average composition having a ratio of Bi-Pb-Sr-Ca-Cu of 0.8-1.1:0.5-1.0:1:0.9-1.1:1.5-1.7; and heat treating said film in an oxygen containing atmosphere to form said superconductor film having a high content of said Tc phase. Particularly, the present invention provides a process as foresaid for preparing a perovskite type superconductor film on a substrate, comprising the steps of: depositing a composite oxide film of a Bi-Sr-Ca-Cu-O system having a thickness of 50 to 2,000 nm on a substrate at a first temperature; optionally depositing a Bi 2 O 3 film having a thickness of 5 to 20 nm on the first composite oxide film at a temperature of 200 to 500°C; depositing a PbO x film having a thickness of 5 to 20 nm on the first composite oxide film at a second temperature less than 500°C; optionally depositing a CuO film having a thickness of 5 to 30 nm at a temperature of 200 to 500°C; repeating the deposition of the composite oxide, Bi 2 O 3 if necessary and PbO films to form a stack of composite oxide films, Bi 2 O 3 films if present, the CuO film if present, and PbO x films on the substrate, the stack having a top film of the composite oxide film; and heat treating the stack at a third temperature of 835 to 870°C i.e. higher than the first, and second temperatures to form a superconductor film being represented by the formula Bi 2-y Pb r (Sr 1-x Ca x ) 4 Cu 3 O z where O < x < 1, 2 > y > 0, r > 0, and z > 0. By the present invention there is also provided an optimum composition for forming high Tc phase Bi 2 Sr 2 Ca 2 Cu 3 O x in Pb-doped Bi system thin films. Although it was reported that doping with Pb enhanced the high Tc phase formation in the bulk system, the present inventors found that in thin films, doped Pb easily evaporates during post-annealing or sintering and a larger amount of Pb is necessary to synthesize the high Tc phase. Further, the present inventors optimized the Cu content in the deposited film. A slightly excess Cu effectively decreases the low Tc phase. Thus a preferred composition for the as-deposited film before post-annealing is a ratio of Bi/Pb of 1/0.6-0.9, and a ratio of Sr/Cu of 1/1.5-1.7. For a better understanding of the invention and to show how the same can be carried into effect, reference will now be made, by way of example only, to the accompanying drawings, wherein: Figures 1 and 2 show X-ray diffraction patterns of Bi-Sr-Ca-Cu-O and Bi-Pb-Sr-Ca-Cu-O superconductor films in the prior art; Fig. 3 shows the electric resistivity v.s. the temperature of a Bi-Pb-Sr-Ca-Cu-O superconductor film in the prior art; Fig. 4 shows the structure of an as-deposited stack of the present invention; Fig. 5 shows the electric resistivity v.s. the temperature of a Bi-Pb-Sr-Ca-Cu-O superconductor film of the present invention; Fig. 6 shows the electric resistivity v.s. the temperature of a Bi-Pb-Sr-Ca-Cu-O superconductor film of the present invention at several current densities; Fig. 7 shows the structure of another as-deposited stack of the present invention; Fig. 8 shows X-ray diffraction patterns of Bi-Pb-Sr-Ca-Cu-O superconductor films of the present invention; Fig. 9 shows the composition of a Bi-Pb-Sr-Ca-Cu-O system superconductor film during a heat treatment; Fig. 10 shows the electric resistivity v.s. the temperature of Bi-Pb-Sr-Ca-Cu-O superconductor films of the present invention; Fig. 11 shows X-ray diffraction patterns of Bi-Pb-Sr-Ca-Cu-O superconductor films of the prior art; Fig. 12 shows the electric resistance v.s. the temperature, of Bi-Pb-Sr-Ca-Cu-O superconductor films of the prior art; Fig. 13 shows the structure of a further as-deposited stack of the present invention; Fig. 14 shows an X-ray diffraction pattern of a Bi-Pb-Sr-Ca-Cu-O system superconductor film of the present invention; Figs. 15A and 15B show microstructures of a Bi-Pb-Sr-Ca-Cu-O system superconductor film of the present invention; Fig. 16 shows the electric resistance v.s. the temperature of a Bi-Pb-Sr-Ca-Cu-O system superconductor film of the present invention; and Fig. 17 shows X-ray intensity ratios of high Tc/low Tc at several Cu/Sr and Pb/Bi ratios. Bi-Sr-Ca-Cu-O system superconductors comprise at least four metal elements, and as a result, it is difficult to adjust the composition to a desired value. Further, metal elements having a relatively high vapor pressure, such as Bi and Pb, tend to be lost from a deposited film, e.g., by evaporation during the deposition and annealing of the film. The extent to which the elements in the deposited film are lost depends on the substrate temperature, the deposition rate of the film and the annealing temperature. Therefore, the composition of the film is not reproducible. The vapor pressure (P) of an oxide is represented by the formula: log P = AT -1 + B logT + C x 10 -3 x T + D where T stands for the absolute temperature (K), and A, B, C and D are constants ("Metal Data Handbook", p86). Examples of the vapor pressure of elements and oxides at 1073 K (800°C) are shown below: Element Oxide A B C D log P (mm Hg) P 0 (Pa) PbO -13480 -0.92 -0.35 14.36 -1.366 (8.507 at 400°C 0.057 Pb -10130 -0.985 11.16 -1.266 0.072 Bi -10400 -1.26 12.35 -1.16 0.092 Cu -17700 -0.86 12.29 -6.812 2 x 10 -7 Figure 1 shows the X-ray diffraction pattern of a Bi-Sr-Ca-Cu-O film formed in accordance with the prior art. A sintered oxide target of Bi 2 Sr 2 Ca 2 Cu 3 O x was prepared by firing a mixture of oxides in air at 800°C for 24 hours. A film was deposited by RF magnetron sputtering on a MgO substrate from the above target heated to 400°C under 1 Pa, and the obtained film having a thickness of 1 µm was then heat treated at 875°C for 5 hours. The thus-obtained film comprised of, as seen from Fig. 1, Bi 2 Sr 2 CuO x and Bi 2 Sr 2 CaCu 2 O x (the low Tc phase having a Tc of 80 K). The film had a composition of Bi:Sr:Ca:Cu = 0.63 : 1.00 : 1.07 : 1.40 by EPMA (electron probe micro analysis), which greatly deviated from the stoichiometric composition of the high Tc phase (Bi 2 Sr 2 Ca 2 Cu 3 O x ) having a Tc of 110 K. When Pb was added to the above target, so that the Pb-doped target had a composition of Bi 2 Pb 0.4 Sr 2 Ca 2 Cu 3 O x , and the deposited film was heat treated at 850°C for 12 hours, the resultant film contained a high Tc phase. However, the volume fraction was small (see Fig. 2). Figure 3 shows the electric resistivity of the film vs. the temperature, in which the on-set is seen to be around 110 K but in which zero resistance is not achieved until 75 K. It was when an appropriate amount of Pb is added to a bulk sample of Bi-Sr-Ca-Cu-O that a high volume fraction of the high Tc phase was obtainable. By Koyama et al (JJAPL. vol. 27, pp-L1861-1863), a sufficient amount of Pb was not added to the deposited film because Pb is easily evaporated during the deposition and annealing of the film. The present invention offers a solution to the difficulty of including sufficient Pb in the deposited film. For this purpose there is independently formed a layer containing PbO x , which has a high vapour pressure being more than 10 -4 Pa, indeed more than 10 -2 , at 800°C. By effecting alternating deposition of composite oxide film and PbO x , it is possible to produce a stack of oxide layers having an average composition close to a desired value whereby, after heat treating the stack for a short time, a superconductor film is obtained comprising a phase having a structure containing three CuO planes in a 1/2 unit, the superconductor film having a high critical temperature and a high critical current density. Thus, in a preferred procedure, the present invention provides a process in which the stack of composite oxide films and PbO x films is heated at a temperature higher than any deposition temperature used in an atmosphere containing oxygen to form the perovskite type superconductor film on the substrate. The process described herein may be applied to composite oxide films as deposited which, themselves, have superconductor behaviour. Important examples thereof are Bi 2 (Sr 1-x Ca x ) m Cu n O z , where 0 < x < 1, m = 4 and n = 3, and z > 0 whereby a high Tc phase composition is obtained. It should be noted that the average composition of the high Tc phase superconductor may show some variation (at most 10%) from the stoichiometric values. Thus, the perovskite type superconductor of the present invention may itself be a superconductor having the above composition, Bi 2 (Sr 1-x Ca x ) 4 Cu 3 O z , in which a part of an element or elements thereof is replaced by Pb and/or Pb is further added. Such superconductors may be represented by the formula: Bi 2-y Pb r (Sr 1-x Ca x ) 4 Cu 3 O z where 0 < x < 1, 2 > y > 0, r > 0, and z > 0. The PbO x having a vapor pressure of higher than 10 -4 Pa at 800°C is deposited at a temperature (less than 500°C) which is lower than a temperature (typically 750 - 890°C) of a heat treatment for forming a perovskite type superconductor. At a temperature higher than 500°C, evaporation occurs, and at a temperature lower than 200°C, the adhesion of the deposited oxide film is poor. A preferable temperature for depositing the PbO x is 350 to 400°C. Overall the as-deposited film can be expressed by a ratio of Bi:Pb:Sr:Ca:Cu = 0.8-1.1:0.5-1.0:1:0.9-1.1:1.5-1.7. To meet this requirement, the film of Bi-(Pb)-Sr-Ca-Cu-O system as deposited and before the heat treatment preferably has an average composition with a ratio of preferably 1/0.6 - 0.9. In the prior art, a ratio of Bi/Pb of about 1.8/0.34 (i.e., 1/0.189) is thought preferable as a starting material for forming a bulk superconductor (Kawai et al, Jpn. J. Appl. Phys. 27, 1988, L1476). Nevertheless, the present inventors found that Pb or PbO x in a film is preferentially and greatly evaporated during a heat treatment of the stack, and the high Tc phase is formed mainly when Pb remains in the film after deposition, and therefore, to form a high Tc phase superconductor film, Pb is necessary in an as-deposited film in an amount more than the amount adequate for bulk samples. But if too much Pb is in the as-deposited film, the film is partially fused during the heat treatment and the heat treated film phase separated. In addition to Pb doping, it is found that an Sr/Cu ratio of 1/1.5-1.7 is desired. An excess amount of CuO is preferred because the high Tc phase is more easily formed when an excess amount of CuO is present. CuO may be deposited as a separate CuO film in a stack of films, as the above described element or oxide having a high vapor pressure. The deposition of the oxides may be performed by physical vapor deposition such as sputtering, evaporation, molecular beam epitaxy (MBE), etc., or chemical vapor deposition (CVD) including plasma CVD, etc., or other processes. Certain elements or oxides of the superconductor may be deposited together because they do not have a high vapor pressure, and therefore, can be deposited without hard evaporation even by simultaneous deposition, or if desired may be separately deposited, particularly CuO. In the multi-layer deposition procedure described herein, the thickness of the Bi-Sr-Ca-Cu-O film having a low oxide or element vapor pressure is 50 nm to 2000 nm. The order of the deposition of the films is as follows: first depositing the composite oxide layer having a low vapor pressure directly on a substrate so that adhesion of the film to the substrate is firm; and last depositing a composite oxide layer having a low vapor pressure as the top film of the stack to prevent evaporation of oxide or element having a high vapor pressure from the top of the stack during the heat treatment in order to form the perovskite type superconductor. The stack of the films may have a composition which is stepwise or gradually changed from one film to an adjacent film. The number of films in the stack is not limited, and a combination of a film of an oxide having a high vapor pressure and a film of an oxide having a low vapor pressure may be repeatedly stacked. The stack thus obtained is heat treated at a temperature higher than the temperature at which the oxides were deposited. By this heat treatment, a perovskite type superconductor is formed having an approximately stoichiometric composition and containing the high Tc phase at a high volume fraction. After the heat treatment, the amount of oxide having a high vapor pressure may be lower than that of the as-deposited stack. Particularly the content of Pb is often reduced after the heat treatment, but a high volume fraction of the high Tc phase is obtainable. This suggests that Pb acts as an accelerator for forming the high Tc phase and is not necessarily a component of the high Tc phase to any great extent. A separate formation of the PbO film is an important feature of the present invention. A preferred content of the PbO in the as-deposited stack has been described. The temperature of the heat treatment or annealing in the multi-layer deposition procedure described herein is 835 to 870°C. At a temperature lower than 835°C, a low Tc phase superconductor is also formed, and at a temperature higher than 870°C, the superconductor may be melted. In accordance with the preferred multi-layer deposition procedure described in the present invention, among elements constituting a perovskite type superconductor, an oxide of an element having a high vapor pressure and which is difficult to deposit or an element or oxide which is relatively easily evaporated during a post-annealing of the deposited film is independently and concentratedly deposited, and thus the time for depositing such an oxide is shortened and variations of the composition by evaporation during the deposition and the annealing of the deposited film or stack can be reduced or neglected. By depositing an oxide with a low vapor pressure immediately on the above oxide, evaporation of the stack as a whole is also largely prevented. Thus, the composition of the film can be very precisely controlled and a perovskite type superconductor having a high Tc and a high Jc is finally obtained. Also, in accordance with the present invention, particularly by adding to an as-deposited film or stack an appropriate amount of Pb and a slightly excess amount of CuO, a Bi-(Pb)-Sr-Ca-Cu-O system superconductor which is almost a single phase of the high Tc phase, and therefore, has a high Tc and a high current density, is obtained after a heat treatment or annealing. This is a most important feature and effect of the present invention. The following Examples illustrate this invention: In the following Working Example and Comparative Examples 1 - 3, depositions were carried out by a RF magnetron sputtering under the following conditions: Substrate: Single crystal (100) MgO; Temperature of substrate: 400°C; Atmosphere: A mixed gas of Ar and O 2 with Ar:O 2 = 1:1; Pressure: 1 Pa; RF power: 100 W (about 1.3 W/cm 2 ); Target A: Bi 2 Sr 2 Ca 2 Cu 3 O z sintered at 800°C for 24 hours; Target B: Bi 2 Pb 0.4 Sr 2 Ca 2 Cu 3 O z sintered at 800°C for 24 hours; Target C: Bi 2 O 3 ; Target D: PbO x . Comparative Example 1 A film was deposited from the target A (Bi:Sr:Ca:Cu = 2:2:2:3) onto a MgO substrate heated at 400°C to a thickness of 1 µm, and then heated in air at 875°C for 5 hours. Figure 1 shows the X-ray diffraction pattern of the heat-treated sample. It is seen from Fig. 1 that a Bi 2 Sr 2 CuO x phase having a Tc of 10 K and a low Tc Bi 2 Sr 2 CaCu 2 O 3 phase having a Tc of 80 K were formed. The composition of the film determined by EPMA was Bi:Sr:Ca:Cu = 0.63 : 1.00 : 1.07 : 1.40, in which the content of Bi was remarkably decreased from the composition of the target of Bi:Sr:Ca:Cu = 2:2:2:3. Comparative Example 2 A film was deposited from the target B (Bi:Pb:Sr:Ca:Cu = 2:0.4:2:2:3) onto a MgO substrate heated at 400°C to a thickness of 1 µm, and then heated in air at 850°C for 12 hours. Figure 2 shows the X-ray diffraction pattern of the above heat treated sample. It is seen from Fig. 2 that the high Tc phase of Bi 2 Sr 2 Ca 2 Cu 3 O z was formed but the volume fraction thereof was still very low in comparison with the volume fraction of the low Tc phase of Bi 2 Sr 2 CaCu 2 O x . Figure 3 shows the electric resistivity dependence on the temperature in which the on-set temperature was higher than 110 K but the Tce (end point of the critical temperature) was 75 K. The composition of the film was determined by EPMA and it was found that Bi was lacking and the composition was non-stoichiometric, and that only a little Pb was doped in the deposited film (therefore, it is understood that the content of Pb was not enough to form a high Tc phase). Comparative Example 3 A film was deposited from the target A (Bi:Sr:Ca:Cu = 2:2:2:3) and the target C (Bi 2 O 3 ) onto a MgO substrate heated at 400°C to form a stack of five films of Bi-Sr-Ca-Cu-O, 200 nm thick, and three films of Bi 2 O 3 , 15 nm thick, the stack having a total thickness of 1 µm, and then being heated in air at 875°C for 5 hours. EPMA analysis revealed that the annealed film had a composition very close to the stoichiometric composition of the high Tc phase, i.e., the content of Bi was adequately compensated. Nevertheless, it was also revealed that the high Tc phase was formed only in a very small amount such that it could be only just detected. Working Example 1 Figure 4 illustrates the layer structure of the stack formed in this example, in which a plurality of Bi-Sr-Ca-Cu-O films 2, Bi 2 O 3 films 3 and PbO films 4, in this order, are deposited on a MgO substrate 1 and another Bi-Sr-Ca-Cu-O film 2′ is finally deposited on the top of the stack of the films 2, 3 and 4. The above deposition was carried out by magnetron sputtering using the targets A, C and D. The thicknesses of the Bi-Sr-Ca-Cu-O film 2, the Bi 2 O 3 film 3, and the PbO film 4 were 300 nm, 20 nm and 10 nm, respectively, and the total thickness of the stack was about 1 µm. The thus-obtained stack was heat treated in air at 850°C for 10 minutes to 15 hours. The composition of the film after 1 hour heat treatment at 850°C was Bi:Pb:Sr:Ca:Cu = 0.87:0.34:1.00:1.27:1.88, (or 1:0.39:1.15:1.46:2.16), by EPMA. This clearly suggests that the amount of Bi was adequate and a sufficient amount of Pb was doped in the film. It was found that, in this example, the Pb continuously evaporated during the heat treatment of the stack and only a small amount of Pb remained after 3 hours at 850°C. The as-deposited oxide films were amorphous, but reacted to form the high Tc phase after the heat treatment at 850°C for 10 minutes, the volume fraction of the high Tc phase in the reacted film being one third. After 1 hour, more than half of the film was high Tc phase, and after 15 hours, only a small amount of Pb remained but the film was almost entirely high Tc phase only. This suggests that Pb accelerates the formation of the high Tc phase but the formation of the high Tc phase does not always require Pb. Figure 5 shows the electric resistivity v.s. the temperature of the thus-obtained film. As seen in Fig. 5, the electric resistivity is linearly decreased with a lowering of the temperature, and rapidly decreased at around 110 K. The Tce of the film was 94.5 K after 10 minutes heat treatment at 850°C and 106.5 K after 1 hour heat treatment. After 15 hours heat treatment at 850°C, the Tce of the film was 105.4 K and almost the same as that after 1 hour heat treatment, but the on-set temperature was slightly elevated. Figure 6 shows the temperature dependence of the electric resistivity in relation to the current density. It is seen that a satisfactory characteristic was obtained 2.47 x 10 3 A/cm 2 at liquid nitrogen temperature. As understood from the above, in the process of the prior art, magnetron sputtering was carried out by using a single target (Bi 2 Sr 2 Ca 2 Cu 3 O z ) and the resultant film was then heat-treated in an oxide-containing atmosphere at a certain temperature, and the film obtained having a nonstoichiometric composition due to a lack of Bi. When a single target (Bi 2 Pb 0.4 Sr 2 Ca 2 Cu 3 O z ) doped with Pb, which is said to accelerate the formation of the high Tc phase, is used in a similar process, the resultant film also has a nonstoichiometric composition due to a lack of Bi, and an amount of Pb sufficient to form the high Tc phase is not deposited. As a result, the film obtained using a single target in the prior art is multiphase and the film has a very small volume fraction of the high Tc phase. In contrast, in accordance with the present invention, there are a plurality of features including a sintered oxide target (Bi 2 Sr 2 Ca 2 Cu 3 O z , Bi 2 Pb 0.4 Sr 2 Ca 2 Cu 3 O z , etc.) for depositing a complex oxide containing the elements to constitute the perovskite type superconductor; possibly a compensating feature (Bi 2 O 3 etc.) for depositing a compensating film to compensate for a component which, among the elements constituting the superconductor, has a high vapor pressure at a temperature of the film deposition or at a temperature of the heat treatment or annealing, and evaporates during the steps such that the content thereof is very low in the deposited or heat treated film; and the use of a high Tc phase formation accelerating component (PbO x ) for supplying PbO x as a high Tc phase formation accelerating component, which is not an essential component of the high Tc phase of the super-conductor and has the effect of accelerating the formation of the high Tc phase but easily evaporates at the deposition or heat treatment temperature as above; etc., are used to form a stack of a plurality of films on a substrate and then heat treated or annealed. This process of the present invention provides the following effects. 1) A component such as Bi can be adequately compensated, so that the composition of the formed superconductor film can be stoichiometric. 2) A sufficient amount of Pb for accelerating the formation of the high Tc phase can be doped. 3) Due to the composition of the superconductor film being close to that of the high Tc phase and a sufficient amount of Pb being doped, as attained in the above 2) and 3), a superconductor film exhibiting a high quality high Tc phase can be formed by an extremely short time heat treatment. Comparative Example 4 A stack of films having a structure as shown in Fig. 7 was formed on a single crystal MgO substrate by magnetron sputtering. In Fig. 7, 11 denotes the substrate, 12 a Bi-Sr-Ca-Cu-O system film having a thickness of 200 nm, and 13 a PbO film having a thickness of 20 nm. There were four films 12 and three films 13. The following conditions were used in the magnetron sputtering: Target E: a complex oxide with a ratio of Bi:Sr:Ca:Cu = 3:2:2:3 Atmosphere: a mixed gas of Ar and O 2 with a ratio of Ar/O 2 of 2/1 Pressure: 1 Pa RF power: 100 W for the Bi-Sr-Ca-Cu-O film and 75 W for the PbO x film Temperature of substrate: 400°C The thus-obtained stack or film was composition evaluated by an ICP (induced coupled plasma) and found to have a ratio of Bi:Pb:Sr:Ca:Cu = 0.9:0.8:1.0:1.2:1.7 (or 1:0.89:1.11:1.33:1.89). The amount of Bi was adequate due to the high content thereof in the target. The ratio between Pb and Bi was 0.9:1.0, which is almost adequate. The stack was then heat-treated in air at 850°C for 10 minutes. Similarly, the stacks were formed as above and then heat treated in air at 850°C for 1 hour and 15 hours. The thus obtained superconductor films X, Y, Z were analyzed by an X-ray diffraction and the X-ray diffraction patterns X, Y, Z are shown in Fig. 8, in which H denotes the high Tc phase having the Tc of 110 K and L denotes the low Tc phase having the Tc of 80 K. In all of the superconductor films heat-treated for different time periods, it is clear that a large high Tc phase was formed. Figure 9 shows the composition of the superconductor film in relation to the heat treatment time, evaluated by EPMA. Along with the time of the heat treatment, Pb is rapidly evaporated and disappears from the film in about 3 hours. On the other hand, the X-ray diffraction patterns indicate that the high Tc phase was rapidly formed at the beginning of the heat treatment, i.e., when Pb existed. In Fig. 9, the left side ordinate represents the composition ratio and the right side ordinate represents the X-ray diffraction intensity ratio of the high Tc phase peak (002) to the low Tc phase peak (002). Figure 10 shows the electric resistivities of the superconductor films X, Y, Z in relation to the temperature. The highest Tce was 106.5 K after a 1 hour heat treatment at 850°C. Comparative Example 5 The procedures of Working Example 1 were repeated except that the deposited stack had a ratio of Bi/Pb of 1/0.2 by reducing the thickness of the PbO film 13 from 30 nm to 6 nm. The following is the change of the composition occurring during the heat treatment, as determined by EPMA. Sample No. Time of heat treatment Bi : Pb : Sr : Ca : Cu 1 10 minutes 1.02 : 0.21 : 1.00 : 1.08 : 2.26 2 1 hour 1.00 : 0.14 : 1.00 : 1.02 : 1.76 3 15 hours 0.91 : 0.10 : 1.00 : 1.09 : 1.55 Figure 11 shows the X-ray diffraction patterns of the above three superconductors. It is clear that the amount of the high Tc phase was not increased by the prolongation of the heat treatment. Figure 12 shows the electric resistivity of the superconductor film in relation to the temperature. The on-set temperature is 110 K but the end point Tce is 77 K. Working Example 2 A stack of films having a structure as shown in Fig. 13 was formed on a single crystal MgO substrate by magnetron sputtering. In Fig. 13, 21 denotes the substrate, 22 a Bi-Sr-Ca-Cu-O system film having a thickness of 200 nm, 23 a PbO x film having a thickness of 30 nm and 24 a CuO film having a thickness of 30 nm. There were four films 22 and three films 23 and 24. The following conditions were used in the magnetron sputtering: Target E: a complex oxide with a ratio of Bi:Sr:Ca:Cu = 3:2:2:3 Atmosphere: a mixed gas of Ar and O 2 with a ratio of Ar/O 2 of 2/1 Pressure: 1 Pa RF power: 100 W for the Bi-Sr-Ca-Cu-O film and 75 W for the PbO x film and CuO film Temperature of substrate: 400°C The composition of the thus-obtained stack or film was evaluated by an ICP (induced coupled plasma) and found to have a ratio of Bi:Pb:Sr:Ca:Cu = 1.0 : 0.8 : 1.0: 1.0 : 1.6. The amount of Bi was adequate (just the stoichiometric ratio to Sr). The obtained stack was then heat treated in air at 850°C for 1 hour and a superconductor film was obtained. Figure 14 shows the X-ray diffraction pattern of the superconductor film. It is seen that an almost single high Tc phase of the superconductor was obtained. Figures 15A and 15B show microstructures of the superconductor film observed by a scanning electron microscope (SEM), in which c-axis aligned scaly superconductor crystals are seen. Figure 16 shows the electric resistivity of the superconductor film in relation to the temperature. The resistance was rapidly lowered from around 106.5 K and reached zero resistivity at 106.5 K. The critical current density was high, 5.8 x 10 4 A/cm 2 at 77.3 K Working example 3 Superconducting films were deposited by RF magnetron sputtering using three targets. The films were deposited on 20 x 20 mm 2 MgO (100) single crystals. A Bi-Sr-Ca-Cu-O (BSCCO) target with the composition of Bi:Sr:Ca:Cu = 3:2:2:3 was used. The films Bi content is usually less than the target value, and a Bi-rich target is usually used to compensate for the lack of Bi in the films. PbO and CuO targets were also used to dope enough Pb into the films and to optimize the Cu content. PbO and CuO layers were stacked repeatedly on BSCCO layers to control the composition precisely. The PbO and CuO layers were several dozen nanometers thick. The total thickness of the deposited films was about 0.85 µm. As-deposited films were amorphous and insulating. A film was divided into about 10 x 10 mm 2 samples, and one of these was analyzed by inductively coupled plasma analysis (ICP) to determine the film composition. The other films were sintered in air for 1 h at around 850°C. A muffle furnace was used and the temperature was measured by an R-type (Pt-13% Rh, Pt) thermocouple. The heating rate was 10°/min to 800°C and 1°/min above that to avoid overshooting the set temperature. During heating, the films were kept at 800°C for 20 min. The films were cooled at 10°/min. The films were examined using X-ray diffraction with a Cu Kα source and a scanning electron microscope. The electrical resistivity of the films was also measured with the four-point probe method using dc current. The films were doped heavily with Pb because it promoted the high Tc phase. As-deposited film compositions are listed in the following Table. Number 134 was Pb doped to the stoichiometric film at a ratio of 1.03 to the Sr content. X-ray diffraction showed that after 1 h of sintering at 852°C, large amounts of the film transformed to the high Tc phase, but about one-fourth of the film remained in the low Tc phase. In addition to superconducting crystals, needle-like precipitations several dozen µm long were observed with a scanning electron microscope (SEM). Heavy Pb doping spoils the film morphology because the film melts more easily during sintering as the Pb content increases. This causes an inhomogeneous distribution of the elements and forms needle-like crystals which were found to be Ca-Cu-O by electron probe microanalysis (EPMA) and led to a low critical current density (Jc). It was found that in thin films the Cu content decreased by about 3% during an hour of sintering. An attempt was then made to decrease the amount of Pb doping and to investigate the Cu composition dependence of the high Tc phase formation. Figure 17 shows the intensity ratios of the peaks from the high Tc phase (00 14 ) and the low Tc phase (00 12 ). Similar results are obtained from the ratios of H(002)/L(002) and H(00 10 )/L(008). The analyses of compositions obtained in the various runs are summarised in the following Table with the compositions runs 128, 132, 134, 136, 138, 139 and 140 being non-inventive and indicated for comparative purposes only. Insofar as the tabulated analyses are concerned, the atomic compositions of Bi, Pb, Sr, Ca, and Cu determined by ICP were normalized by the Sr composition. For the upper samples, a PbO target was sputtered for 8 min and for the lower, 6 min. BSCCO target was sputtered for 100 min and CuO from 15 to 24 min. Run No. Compositions Bi:Pb:Sr:Ca:Cu 128 0.90:1.19:1.00:0.98:1.35 132 0.93:1.10:1.00:1.02:1.36 134 0.96:1.03:1.00:1.09:1.47 136 0.99:1.11:1.00:1.04:1.72 138 0.95:1.04:1.00:0.98:1.73 139 0.95:1.09:1.00:1.05:1.78 145 0.93:0.78:1.00:0.96:1.44 146 0.96:0.79:1.00:0.98:1.60 147 1.01:0.85:1.00:0.99:1.62 142 0.98:0.82:1.00:0.96:1.63 144 1.02:0.80:1.00:0.99:1.64 137 1.00:0.84:1.00:1.01:1.69 140 1.03:0.89:1.00:1.02:1.82 In Fig. 17, the large numbers indicate run number and the small numbers indicate sintering temperature. The dotted line is a guide for the eye. The amount of the high Tc phase depends strongly on the Cu content. The sintering temperature also greatly affects the amount of the high Tc phase formed. The low Tc phase forms below 848°C and above 853°C. This suggests that the single-phase high Tc film forms in a very narrow temperature range. For Bi:Pb:Sr:Ca:Cu = 1.00:0.80:1.00:0.99:1.64, a nearly single-phase high Tc thin film was obtained after an hour of sintering at 851°C in air. The resistivity decreased linearly with temperature and had a zero resistance at 106.5 K. Jc reached 4.1 x 10 4 A/cm 2 at 77.3 K with a criterion of 1 µV/cm.

Claims: A process for preparing on a substrate a film of a perovskite-type Bi-(Pb)-Sr-Ca-Cu-O system superconductor having a high content of a phase having a high Tc, said process comprising: providing a film on a substrate, said film having an average composition having a ratio of Bi-Pb-Sr-Ca-Cu of 0.8-1.1:0.5-1.0:1:0.9-1.1:1.5-1.7; and heat treating said film in an oxygen containing atmosphere to form said superconductor film having a high content of said Tc phase. A process according to claim 1, wherein said film as provided has an average composition to include a ratio of Bi/Pb of 1/0.6 to 1/0.9. A process according to claim 1, wherein the said perovskite type system superconductor film has a composition which is represented by the formula Bi 2 (Sr 1-x Ca x ) 4 Cu 3 O z , where 0 < x < 1 and z > 0. A process according to claim 3, wherein said superconductor is a Pb-doped Bi-Sr-Ca-Cu-O perovskite type system. A process according to claim 1, wherein said film as provided is comprised by a stack of layers, said stack of layers including a layer of at least one of PbO x and Bi 2 O 3 . A process according to claim 5, comprising the steps of; depositing a composite oxide film of a Bi-Sr-Ca-Cu-O system having a thickness of 50 to 2,000 nm on a substrate at a first temperature; depositing a PbO x film having a thickness of 5 to 20 nm on the first composite oxide film at a second temperature less than 500°C; repeating deposition of the composite oxide and PbO x films alternatingly to form a stack of the composite oxide and PbO x films on the substrate, the stack of films as deposited having a top film of the composite oxide film; heat treating the stack of films at a third temperature of 835 to 870°C in an oxygen containing atmosphere to form a superconductor film, the superconductor being represented by the formula Bi 2-y Pb r (Sr 1-x Ca x ) 4 Cu 3 O z where 0 < x < 1, 2 > y > 0, r > 0 and z > 0. A process according to claim 6, wherein the second temperature is 350 to 400°C. A process according to claim 6 or 7, wherein the Bi-Sr-Ca-Cu-O system composite oxide film as deposited is represented by the formula Bi 2 (Sr 1-x Ca x ) m Cu n O z , where 0 < x < 1, m = 4 and n = 3, and z > 0. A process according to any one of claims 6 to 8, wherein the composite oxide film of the Bi-Sr-Ca-Cu-O system further contains Pb. A process according to any one of claims 5 to 9, wherein said stack of layers has an average composition to include a ratio of Bi/Pb of 1/0.6 to 1/0.9. A process according to any one of claims 5 to 10, wherein said stack of layers includes additionally a layer of CuO. A process according to any one of claims 5 to 11, wherein said stack of layers has an average composition to include a ratio of Sr/Cu of 1/1.5 to 1/1.7.

Inventors: KAMEHARA NOBUO, NIWA KOICHI, TANAKA ATSUSHI, KAMEHARA, NOBUO, NIWA, KOICHI, TANAKA, ATSUSHI
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1989
Main classification: C04B35
IPC codes: C04B35, B32B18, H01L39