HEAT RESERVE MATERIAL

Abstract: The present invention provides a heat reserve material having excellent physical properties. The heat reserve material comprises; (A) a hydrophilic polymer having a hydroxyl group on a principal chain, (B) an oxide glass, and (C) water and/or a water-soluble alcohol, wherein the amount of the component (B) is within the range of 1 to 50 parts by weight based on 100 parts by weight of the component (A), and the amount of the component (C) is 6 to 50 times larger than the total weight of the components (A) and (B).

Description: The present invention relates to a novel heat reserve material having excellent physical properties. A composition which comprises water-impregnated polyvinyl alcohol is generally used for a low temperature reserve material, because it is a gel having a suitable viscosity and fluidity and a low heat transfer rate. The composition, however, is difficult to treat due to high adhesive properties. It also has poor shape retention and flows like liquid. PATENT ABSTRACTS OF JAPAN, vol. 12, no. 15 (C-469)(2862) teaches a composition which comprises the same components as the composition of the present invention with the only significant difference that the amount of component (C) is only from 1-5 times larger than the total weight of the components (A) and (B). This difference in the amount of component (C) does produce a very marked difference in the physical properties. The present invention provides a heat reserve material having excellent physical properties. The heat reserve material comprises; (A) a hydrophilic polymer having a hydroxyl group on a principal chain, (B) an oxide glass, and (C) water and/or a water-soluble alcohol, wherein the amount of the component (B) is within the range of 1 to 50 parts by weight based on 100 parts by weight of the component (A), and the amount of the component (C) is 6 to 50 times larger than the total weight of the components (A) and (B). The component (A) is a hydrophilic polymer having a hydroxyl group on a principal chain. By "hydrophilic" herein is meant either water-soluble or water-miscible. The hydrophilic polymer includes polyvinyl alcohols prepared by completely or partially saponifying polyvinyl acetate or copolymers of vinyl acetate with other vinyl monomers (such as, ethylene, vinyl chloride, (meth)acrylic acid, alkyl (meth)acrylates, maleic anhydride, alkyl vinyl ether and the like); modified or grafted polyvinyl alcohols; polymers or copolymers of hydroxyl group-containing polymerizable monomers (such as, 2-hydroxyethyl (meth)acrylate); and the like. Among them, more preferred are polyvinyl alcohols, because they are available in industrial scale at a low cost. The polyvinyl alcohols preferably have a saponification degree of at least 80 %, preferably at least 85 %. If the saponification degree is less than 80 %, the impact resilience of the composition is poor. The oxide glass employed in the present invention typically includes borate glass, silicate glass, phosphate glass, a mixture thereof and the like. Although the present invention is not limited to a particular theory, it is believed that the oxide glass is reacted with the hydrophilic polymer (A) in the presence of water and/or water-soluble alcohols. In the oxide glass, a network structure is generally formed through oxygen. The polymer (A) is bonded to the oxygen to partially form three-dimentional structure. In view of reactivity with the polymer (A), borate glass or a mixture of borate glass and the other glass is preferred. Borate glass is primarily formed from B₂O₃, but may contain other components, such as Al₂O₃, K₂O, Na₂O, CaO, MgO and the like. The oxide glass can be employed in the form of powder which is generally prepared by melting glass and then grinding. The particle size of the glass is not limited, but is preferably within the range of 10 to 250 micrometer, preferably 5 to 150 micrometer. The heat reserve material of the present invention contains water and/or a water-soluble alcohol. Examples of the water-soluble alcohols are monoalcohols, such as methanol, ethanol, propanol, isopropanol, butanol and t-butanol; polyhydric alcohols, such as propanediol, glycerol, ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol and trimethylolpropane. Water is most preferred because of low cost and easy control of temperature. An amount of the oxide glass (B) is within the range of 1 to 50 parts by weight, preferably 5 to 30 parts by weight based on 100 parts by weight of the polymer (A). Amounts of less than 1 part by weight result in decline of shape retention. If the oxide glass (B) is more than 50 parts by weight, it does not participate in the crosslinked matrix and is separated from the matrix. An amount of the component (C) is present in the heat reserve material of the present invention in an amount of 600 to 5,000 parts by weight, preferably 1,000 to 3,000 parts by weight based on 100 parts by weight of the total amount (A) and (B). If the component (C) is more than 5,000 parts by weight, fluidity of the obtained material is too high. The physical properties of the heat reserve material of the present invention are varied widely by the amount of the component (C). The above components (A), (B) and (C) are simply mixed to form the material of the present invention. Mixing is generally carried out at an elevated temperature, generally 60 to 100 °C for 20 minutes to 2 hours, more preferably 80 to 90 °C for 30 minutes to one hour. It is believed that the reaction mentioned above occurs in the mixing. The heat reserve material of the present invention may contain additives in addition to the above three components. Examples of the additives are a dye stuff, a pigment or an inorganic or organic filler. According to the present invention, the component (C), i.e. water or an alcohol, is entrapped in the matrix which is formed by the polymer (A) and the oxide glass (B). As is mentioned above, the matrix is three-dimentionally crosslinked and therefore can prevent flowability and have good shape retention more than a conventional gel which consists of polyvinyl alcohol and water. Since the material of the present invention contains water much more than the conventional gel, thermal energy is stored more and heat transfer rate is also low. The material is very suitable for low or high temperature insulation. The material also shows some resilience and therefore is suitable for a cushioning material, stress relaxing material and the like. It is further suitable for a water pillow, a water bed, a bedsore-preventive mattress and the like, because it constantly has a temperature lower than one's body temperature. EXAMPLES The present invention is illustrated by the following Examples, which are not to be construed as limiting the present invention to their details. Example 1 Sixty grams of polyvinyl alcohol having a saponification degree of 99 % and a polymerization degree of 2,000 was mixed with 6 g of borate glass (B₂O₃ 60 % by weight, Al₂O₃ 25 % by weight, Na₂O 15 % by weight), to which 1,500 g of water was added and mixed to form a gelled composition. The composition has some resilience and can be used for a shock absorbing material. The obtained composition of 1 Kg was charged in a 200 X 300 mm plastic bag to form a heat reserve material and heated in water at 80 °C for 30 minutes. It was then allowed to stand for 25 minutes and the time in which the surface temperature reduced to 40 °C (hereinafter referred as heat retention time (H + L)) was measured. The result is shown in Table 1. Then, the heat reserve material was cooled to 20 °C and allowed to stand in a room at 30 °C and RH of 60 %. The time in which the surface temperature increased to 30°C (hereinafter referred as heat retention time (L + H) was measured. The result is shown in Table 1. The heat reserve material was put on the shoulder. Shape retention was evaluated whether the gel on the shoulder flew downward. The result is shown in Table 1. o ; The gel did not flow downward. ▵ ; The gel flew downward a little. x ; The gel flew downward almost completely. The hardness (C₂) of the material was also determined by a Asker C₂ meter available from Kobunshi Keiki Co., Ltd and the result also is shown in Table 1. Examples 2 to 7 and Comparative Examples 1 to 4 With employing the ratio of the components (A), (B) and (C), the heat reserve materials of the present invention were prepared as generally described in Example 1 and subjected to a same test for physical properties. The results are shown in Table 1.

Claims: A heat reserve material comprising: (A) a hydrophilic polymer having a hydroxyl group on a principal chain, (B) an oxide glass, and (C) water and/or a water-soluble alcohol, wherein the amount of the component (B) is within the range of 1 to 50 parts by weight based on 100 parts by weight of the component (A), and the amount of the component (C) is 6 to 50 times larger than the total weight of the components (A) and (B). A heat reserve material according to Claim 1 wherein said component (A) comprises polyvinyl alcohol. A heat reserve material according to Claim 2 wherein said polyvinyl alcohol has a saponification degree of at least 80%. A heat reserve material according to any one of Claims 1 to 3 wherein said oxide glass comprises borate glass, silicate glass, phosphate glass or a mixture of two or more thereof. A heat reserve material according to any one of Claims 1 to 3 wherein said oxide glass is borate glass or a mixture of borate glass and another glass. A heat reserve material according to any one of Claims 1 to 5 wherein the amount of said oxide glass (B) is within the range of 1 to 50 parts by weight based on 100 parts by weight of the polymer (A). A heat reserve material according to any one of Claims 1 to 6 wherein the amount of the component (C) present is 600 to 5,000 parts by weight based on 100 parts by weight of the total weight (A) and (B). Use of a heat reserve material as claimed in any one of claims 1 to 7 as a cushioning material or stress relaxing material. A water pillow, water bed or bedsore preventative mattress comprising a heat reserve material as claimed in any one of Claims 1 to 7.

Inventors: MITSUBA, ATSUKO, NAGASE, TSUNEYUKI, NAKAHARA, AKIHIRO, NAKASHIO, YUKIYASU, NAKASHITA, TAKEFUMI, TOUJI, DAIJIRO
Applicants: SUMITOMO RUBBER INDUSTRIES LIMITED
Application year: 1989
Main classification: C09K5
IPC codes: C08K5, C08K3, C08L101, A61F7, C08K13, C09K5