Process for the formaldehyde-free durable press finishing of cotton textiles with polycarboxylic acids

Abstract: Catalysts for the rapid esterification and crosslinking of fibrous cellulose in textile form by polycarboxylic acids at elevated temperatures are dis­ closed. The catalysts are acidic or weakly basic salts selected from the alkali metal salts of phosphorous, hypophosphorous, and polyphosphoric acids. Suitable polycarboxylic acids include saturated, unsaturated and aromatic acids, as well as alpha-hydroxy acids. The textiles so treated exhibit high levels of wrinkle resis­ tance and smooth drying properties durable to repeated laundering in alkaline detergents, and do not contain or release formaldehyde.

Description: This invention relates to new esterification catalysts and esterification processes for crosslinking cellulose as a means of imparting wrinkle resistance and smooth drying properties to cellulosic textiles without the use of formaldehyde or derivatives that release formaldehyde. There are numerous commercial processes for imparting wrinkle resistance, shrinkage resistance and smooth drying properties to cotton fabrics and garments, so that they retain their dimensions, smooth appearance and normal shape while in use and also when machine washed and tumble dried. In most of these processes, formaldehyde or an addition product of formaldehyde is applied to the cotton textile together with an acid catalyst, and heat is then applied to produce crosslinking of the cotton cellulose molecules. The crosslinks thus formed in the cellulose impart to the fabric a tendency to return to its original shape and smoothness when deformed by mechanical forces temporarily exerted on the fabric during its use or during laundering and tumble drying. Formaldehyde addition products with urea, cyclic ureas, carbamate esters or with other amides are widely used crosslinking agents for durable press finishing, as the above wrinkle resistant, smooth drying treatments are called. The formaldehyde addition products, also known as N-methylol agents or N-methylolamides, are effective and inexpensive, but have serious disadvantages. They continuously release vapors of formaldehyde during durable press finishing of cotton fabric, subsequent storage of the treated fabric, manufacture of the resulting garment, retailing of the garment, and finally during use of the garment or textile by the consumer. The irritating effect of formaldehyde vapor on the eyes and skin is a marked disadvantage of such finishes, but more serious is the knowledge that formaldehyde is a carcinogen to animals and apparently also to humans continuously exposed to formaldehyde vapor for very long periods. A need is evident for durable press finishing agents and processes that do not require formaldehyde or its unstable derivatives. Another disadvantage of the use of N-methylol agents in durable press treatments is that Lewis acid catalysts and high temperatures are required to bring about sufficiently rapid crosslinking of the cotton cellulose by such finishing agents. The Lewis acid catalysts cause undesirable losses of breaking and tearing strength in cotton fabric during the heat curing step. The strength losses are due to degradation of cellulose molecules by the Lewis acid catalysts at elevated temperature. Such strength losses occur over and above the adverse effects on strength of the crosslinkages produced in the cellulose. An added disadvantage of certain nitrogenous finishes is their tendency to retain chlorine from chlorine bleaches, with resultant fabric discoloration and strength loss if subsequently given a touch-up ironing. The use of polycarboxylic acids with or without catalysts in pad, dry and cure treatments to impart wrinkle resistance to cotton fabric was studied by Gagliardi and Shippee, American Dyestuff Reporter 52 , P300-P303 (1963). They observed small increases in fabric wrinkle resistance after relatively long periods of heating, and noted larger fabric strength losses than are obtained with formaldehyde-based crosslinking agents. These excessive strength losses and the low yield of crosslinkages were attributed to the long heat curing times needed with the inefficient catalysts then available. A more rapid and effective curing process for introducing ester crosslinks into cotton cellulose was described by Rowland et al , Textile Research Journal 37 , 933-941 (1967). Polycarboxylic acids were partially neutralized with sodium carbonate or triethylamine prior to application to the fabric in a pad, dry and heat cure type of treatment. Crosslinking of cellulose was obtained whenever the polycarboxylic acid contained three or more carboxyl groups suitably located in each molecule. With certain polycarboxylic acids, a useful level of wrinkle resistance was imparted. The conditioned wrinkle recovery angle was measured before and after five laundering cycles, and was found to decrease somewhat as a result of laundering, even though no loss of ester groups was detected. Neutralization of carboxyl groups with 2% sodium carbonate even at room temperature caused a 30% loss of ester groups. This indicates a lack of durability of the finish to alkaline solutions such as solutions of alkaline laundering detergents. The curing time needed in fabric finishing was moreover too long to permit high speed, mill-scale production. Subsequently it was shown by Rowland and Brannan, Textile Research Journal 38 , 634-643 (1968), that cotton fabrics given the above cellulose crosslinking treatment with polycarboxylic acids were recurable. Creases durable to 5 laundering cycles could be put into the fabrics by wetting the latter, folding, and applying a heated iron. Evidence was obtained that the ester crosslinkages are mobile under the influence of heat, due to a transesterification reaction taking place between ester groups and adjacent unesterified hydroxyl groups on cotton cellulose. These findings were elaborated by Rowland et al , U.S. Patent No. 3,526,048. Sodium carbonate or triethylamine were again the examples of bases used to partially neutralize the polycarboxylic acid subsequently applied as the cellulose crosslinking agent. Rowland et al defined their process as requiring neutralization of 1% to 50% of all carboxylic acid functionality by a "strong base" selected from the group consisting of alkali metal hydroxides, carbonates, bicarbonates, acetates, phosphates and borates, prior to impregnating the fibrous cellulose with the aqueous polycarboxylic acid and heating to induce crosslinking. A strong base selected from the group consisting of ammonia and certain amines also was indicated as suitable for the partial neutralization of the polycarboxylic acid. Stated limitations of the process of Rowland et al are that the process cannot be conducted with acids of fewer than three carboxyl groups per molecule, or with acids containing olefinic unsaturation or hydroxyl groups. The reasons were lack of reaction with cellulose and lack of effective crosslinking of cellulose chains for development of high levels of wrinkle resistance. The limited durability of the finishes noted above was also a disadvantage, and the time required for complete curing was too long to permit practical rates of cloth finishing. This invention is intended to provide rapid processes for durably imparting to fibrous cellulosic material, such as cotton and other cellulosic textiles, a high level of wrinkle resistance and smooth drying properties by means of non-nitrogenous cellulose crosslinking agents, without the use of formaldehyde or derivatives that release formaldehyde, and with less loss of tearing strength and breaking strength than produced by conventional N-methylolamides. An object of the present invention is to provide a process for improving the wrinkle resistance, shrinkage resistance and smooth drying properties of cellulosic fiber-containing textiles without the use of formaldehyde or agents that release formaldehyde. A second object of the present invention is to provide a non-nitrogenous durable press finish for cellulosic fiber textiles in which the level of smooth drying performance, wrinkle resistance and shrinkage resistance imparted is comparable to that obtained with nitrogenous durable press finishing agents such as N-methylol agents. A third object of the present invention is to provide a durable press process producing less tearing and breaking strength loss in the cellulosic textile than is produced by an N -methylol agent at a given level of wrinkle resistance and durable press performance imparted. A fourth object is to provide a wrinkle resistant and smooth drying fabric of polycarboxylic acid-esterified cellulosic fiber, such as cotton, that retains its durable press properties after repeated laundering with alkaline detergents at elevated wash temperatures. A fifth object is to provide esterification catalysts giving sufficiently rapid esterification and crosslinking of cellulosic fiber by polycarboxylic acids to permit practical rates of durable press finishing of cellulosic fiber-containing fabrics at cure temperatures below the scorch temperature of the cellulose. A sixth object is to provide odor-free durable press finishes for cellulosic fiber-containing fabric that also impart thermal recurability, soil release properties and an affinity for basic or cationic dyes to the cellulosic fabric. According to the present invention there is provided a process for treating fibrous cellulosic material, comprising impregnating fibrous cellulosic material with a treating solution containing a polycarboxylic acid and a curing catalyst, characterized in that the polycarboxylic acid is selected from the group consisting of: aliphatic, alicyclic and aromatic acids either olefinically saturated or unsaturated and having at least three carboxyl groups per molecule; aliphatic, alicyclic and aromatic acids having two carboxyl groups per molecule and having a carbon-carbon double bond located alpha, beta to one or both of the carboxyl groups; aliphatic acids either olefinically saturated or unsaturated and having at least three carboxyl groups per molecule and a hydroxyl group present on a carbon atom attached to one of the carboxyl groups of the molecule; and, said aliphatic and alicyclic acids wherein the acid contains an oxygen or sulfur atom in the chain or ring to which the carboxyl groups are attached; one carboxyl group being separated from a second carboxyl group by either two or three carbon atoms in the aliphatic and alicyclic acids; one carboxyl group being ortho to a second carboxyl group in the aromatic acids; and, one carboxyl group being in the cis configuration relative to a second carboxyl group where two carboxyl groups are separated by a carbon-carbon double bond or are both connected to the same ring; the curing catalyst is selected from the group consisting of alkali metal hypophosphites and alkali metal phosphites and;in that the impregnated material is heated to produce esterification and crosslinking of the cellulose with the polycarboxylic acid in the material. In a preferred embodiment, the process is carried out as a pad, dry and heat cure procedure with the drying and heat curing done either consecutively or simultaneously. Most of the curing catalysts are weak bases, since they are alkali metal salts of acids stronger than ortho-phosphoric acid. In a second aspect, the invention relates to a fibrous cellulosic material characterised by having been treated by a process in accordance with the first aspect of the invention. The present invention is applicable to fibrous cellulosic material containing not less than 30% by weight of cellulosic fibers including cotton, flax, jute, hemp, ramie and regenerated unsubstituted wood celluloses such as rayon. The disclosed process may be applied to fibrous cellulosic material in the form of woven and non-woven textiles such as yarns and woven or knit fabrics, and to fibers, linters, roving, slivers, or paper. The disclosed process is most advantageous with textiles containing 50%-100% cotton. The present invention is based on the discovery that several classes of alkali metal salts of phosphorus-containing acids have a greater accelerating effect on the esterification and crosslinking of cellulose by polycarboxylic acids than is produced by the strong base catalysts used in prior art processes. Since the curing catalysts of the present invention are in most instances weak bases or even acidic salts, their greater effect in speeding the desired crosslinking of the cellulose in a fabric indicates new mechanisms of catalysis, which are not operative in the simple neutralization of a portion of the carboxyl groups of the polycarboxylic acid by a strong base acting as a buffering agent. Moreover the greater laundering durability of the fabric finishes of the present invention also demonstrates the operation of new principles. The most active and effective curing catalysts of this invention are alkali metal hypophosphites, which in anhydrous form have the formula MH₂PO₂ where M is an alkali metal atom. The mechanism of the catalysis is unknown. It is hypothesized that during the heat cure, the polycarboxylic acid forms cyclic anhydrides which then add to the alkali metal hypophosphite to form acylphosphinates, (HOOC)xR[C(O)P(O)(H)OM]x where X is an integer from 1 to 3 equal to the number of cyclic anhydride rings that have formed and reacted with the alkali metal hypophosphite, and R represents the structure of the polycarboxylic acid molecule joined to the anhydride rings transitorily formed. The hypothetical acylphosphinates so formed may react with cellulose to yield the desired crosslinked esters of the polycarboxylic acid, and regenerate the alkali hypophosphite catalyst. Experimentally it is found that the catalyst is effective at concentrations as low as 0.3% by weight in a treating bath, but the durability of the finish is greatest at higher concentrations. A concentration range of 0.3%-11% is operable. The weight gains of the fibrous cellulosic material are larger than accounted for by the polycarboxylic acid and any auxiliary agents such as fabric softeners that are applied. It is evident some of the curing agent is bound to the cellulose. The alkali metal hypophosphites are effective even with a crosslinking agent such as maleic acid which has only two carboxyl groups per molecule. It is possible that two molecules of maleic acid add to one molecule of alkali metal hypophosphite to yield a tetracarboxylic acid that is the actual cellulose crosslinking agent. A second class of curing catalysts employed in the present invention are alkali metal phosphites having the formula MH₂PO₃ and M₂HPO₃. These are nearly as active as alkali metal hypophosphites, but the durable press finishes obtained by their use are slightly less durable to laundering. Their mode of action is not known, but it is possible that the polycarboxylic acid on heat curing forms cyclic anhydrides which may react with the alkali metal phosphites to form acylphosphonates (HOOC)xR[C(O)P(O)(OH)OM]x and (HOOC)xR[C(O)P(O)(OM)₂]x where X and R are defined as above, and X has integral values of 1-3. The hypothetical intermediate so formed may react with cellulose to form the desired crosslinked esters of the polycarboxylic acid, and regenerate the alkali metal phosphite catalyst. The concentrations of alkali metal phosphites effective in accelerating the desired cellulose crosslinking are in the range of 0.3%-11% by weight in the treating solution. For dibasic phosphite salts, however, it is preferable that the molar concentration of the catalyst does not exceed 65% of the normality of the polycarboxylic acid in the treating bath used to impregnate the cellulosic fiber-containing material. The processes of the present invention are carried out by first impregnating the fibrous cellulosic material with a treating solution containing the polycarboxylic acid, the curing catalyst, a solvent and optionally a fabric softener. This may be done, for example, by immersing the material in a bath of the treating solution. The solvent used to prepare the treating solution is preferably water, although any inert volatile solvent in which the polycarboxylic acid and curing catalyst are soluble or uniformly dispersible can be used. The fabric softener, if present, should be an inert, emulsified nonionic or anionic material such as the usual nonionic polyethylene, polypropylene, or silicone softeners. After being thoroughly wet in the treating bath, the cellulosic material is passed between squeeze rolls to remove excess liquid, and is then oven-dried at any convenient temperature just sufficient to remove the solvent within the desired time. The material is then oven-cured at 150-240°C for 5 seconds to 30 minutes to cause cellulose esterification and crosslinking to occur. Alternatively the above drying step may be omitted, and the material can be "flash-cured" to remove solvent at the same time that cellulose esterification and crosslinking take place. If desired, the cured material may subsequently be given a water rinse to remove unreacted reagent and curing catalyst, and may then be redried. The polycarboxylic acids effective in the present invention, as cellulose crosslinking agents, are defined above. It appears from these definitions that for a carboxyl group to be reactive, it must be able to form a cyclic 5-or 6-membered anhydride ring with a neighboring carboxyl group in the polycarboxylic acid molecule. In aliphatic acids containing three or more carboxyl groups per molecule, a hydroxyl group attached to a carbon atom alpha to a carboxyl group does not interfere with the esterification and crosslinking of cellulose by the acid, although the presence of the hydroxyl group causes a noticeable yellowing of the material during the heat cure. Such an alpha -hydroxy acid is suitable for durable press finishing of suitably dyed cotton fabric, since the color of the dye conceals the discoloration caused by the hydroxyl group. Fabric discoloration is similarly observed with an unsaturated acid having an olefinic double bond that is not only alpha , beta to one carboxyl group but also beta , gamma to a second carboxyl group. The discoloration produced in a white cellulosic material by crosslinking it with an alpha -hydroxy acid such as citric acid can be removed by impregnating the discolored material with an aqueous solution containing from 0.5% to 5% by weight of a decolorizing agent selected from the group consisting of magnesium monoperoxyphthalate, sodium perborate, sodium tetraborate, boric acid, sodium borohydride, sodium hypochlorite, and hydrogen chloride. The material is immersed in the solution of decolorizing agent and soaked for 5 to 120 minutes at ambient temperature or if necessary in such a solution warmed to a temperature not exceeding 60°C. The material is subsequently rinsed with water to remove excess chemicals and solubilized colored products, and then is dried. Examples of specific polycarboxylic acids which fall within the scope of this invention are the following: maleic acid; citraconic acid also called methylmaleic acid; citric acid also known as 2-hydroxy-1,2,3-propanetricarboxylic acid; itaconic acid also called methylenesuccinic acid; tricarballylic acid also known as 1,2,3-propanetricarboxylic acid; trans -aconitic acid also known as trans -1-propene-1,2,3-tricarboxylic acid; 1,2,3,4-butanetetracarboxylic acid; all- cis -1,2,3,4-cyclopentanetetracarboxylic acid; mellitic acid also known as benzenehexacarboxylic acid; oxydisuccinic acid also known as 2,2'-oxybis(butanedioic acid); thiodisuccinic acid; and the like. The concentration of polycarboxylic acid used in the treating solution may be in the range of 1% to 20% by weight depending on the solubility of the polycarboxylic acid and the degree of cellulose crosslinking required as determined by the level of wrinkle resistance, smooth drying properties and shrinkage resistance desired. In the examples to be given, the properties of the treated fabrics were measured by standard test methods, which were as follows: conditioned and wet wrinkle recovery angle-ASTM method D-1295-67, Elmendorf tearing strength-ASTM Method D-1424-63, strip breaking strength-ASTM Method D-1682-64, stiffness by the Tinius Olsen Method (Federal Test 191, Method 5202), durable press appearance ratings-AATCC Method 124-1967. The machine launderings were at a wash temperature of 50°C. The pH of the wash water was 9.8 due to use of standard AATCC detergent. Thus the laundering was at high alkalinity in order to test the durability to alkaline detergent of the durable press finishes of this invention. In the following examples, all parts and percentages are by weight. The examples are only illustrative of the processes of the present invention. Changes and modifications in the specifically described embodiments can be carried out without departing from the scope of the invention which is intended to be limited only by the scope of the claims. Example 1 Sodium Hypophosphite as a Curing Catalyst for the Durable Press Finishing of Cotton Fabric with 1,2,3,4-Butanetetracarboxylic Acid An aqueous treating bath was prepared containing 6.3% by weight of 1,2,3,4-butanetetracarboxylic acid, a specified concentration of sodium hypophosphite monohydrate as curing catalyst, and 1% emulsified nonionic polyethylene which served as a fabric softener. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 76g/m² (3.2 oz/yd²) was thoroughly wetted by immersion in this treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 116%-134% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at a specified temperature for a stated time. The fabric was subsequently rinsed for 30 minutes in hot running water to remove any unreacted agents, and was oven dried at 85°C for 5 minutes. The durable press appearance rating of the treated fabric after one machine laundering and tumble drying cycle was determined as a function of the curing temperature and time, as well as the concentration of sodium hypophosphite monohydrate used. The results appear in Table I. Conc. NaH₂PO₂.H₂O Catalyst Cure Temp. Cure Time Fabric Weight Gain Durable Press Rating Fabric Color Before Rinse After Rinse 0.0% 180°C 90sec. 7.8% 2.9 pale tan faint tan 0.4 180 90 10.0 4.1 pale tan faint yellow 0.8 180 90 9.3 4.4 faint yellow white 1.6 180 90 9.9 4.6 off-white white 3.3 180 90 9.9 4.8 white white 6.5 180 90 12.1 4.5 white white 6.5 180 90 9.9 4.7 white white 6.5 180 45 11.8 4.6 white white 6.5 180 30 10.8 4.1 white white 6.5 195 30 11.1 4.6 white white DMDHEU 160 180 7.3 4.6 off-white off-white 6.5 180 90 0.9 1.8 white white Untreated fabric 1.5 white white Fibers were removed from cotton fabric which had been treated as above with 6.3% 1,2,3,4-butanetetracarboxylic acid and 6.5% sodium hypophosphite monohydrate with heat curing at 180° for 90 seconds. The fibers were completely insoluble in 1.0M aqueous cupriethylenediamine hydroxide solution even after 1 hour. Fibers from untreated fabric dissolved within 30 seconds in this solution. The results show the cotton cellulose was highly crosslinked after being heat-cured with 1,2,3,4-butanetetracarboxylic acid and the sodium hypophosphite catalyst. The same positive test for crosslinking was obtained after the heat cure when 1% emulsified polyethylene was also present with the butanetetracarboxylic acid and sodium hypophosphite used to treat the fabric. A number of textile properties were measured on the treated fabric samples prior to machine laundering, and are compared in Table II. Conc. NaH₂PO₂.H₂O Catalyst Cure Wrinkle Recovery Angle(W+F) Warp Tear Strength Retained Warp Break Strength Retained Stiffness, Bending Moment (Warp) Cond. Wet 6.5% 180°/90sec 300° 268° 60% 54% ( 5.8x10⁻⁴in.- 6.4x10⁻⁵N.m lb.) 6.5 180/45 293 267 58 57 (4.3) 4.7 6.5 195/30 288 276 54 59 (4.3) 4.7 DMDHEU 160/180 303 271 54 44 (4.2) 4.6 Untreated fabric 200 141 (100) (100) (4.8) 5.3 The data show that sodium hypophosphite induced very fast curing reactions of 1,2,3,4-butanetetracarboxylic acid with cotton to impart essentially the same durable press appearance ratings and wrinkle recovery angles to fabric as a conventional finishing agent, DMDHEU, and did so with less breaking and tearing strength loss in the fabric then did the conventional agent. Other properties of the two finishes were comparable. Example 2 Comparison of Sodium Hypophosphite and Disodium Phosphite with other Catalysts for Durable Press Finishing of Cotton Fabric with 1,2,3,4-Butanetetracarboxylic Acid An aqueous treating bath was prepared containing 6.3% by weight of 1,2,3,4-butanetetracarboxylic acid, a specified catalyst, and 1% emulsified nonionic polyethylene which served as a fabric softener. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 76 g/m² (3.2 oz/yd²) was treated with this mixture by the procedure of Example 1. The heat cure was at 180°C for 90 seconds. After the final 30 minute water rinse and oven drying, the treated fabric samples were repeatedly machine washed and tumble dried, and durable press appearance ratings were determined after a specified number of wash-and-tumble dry cycles. The ratings appear in Table III as a function of the number of cycles carried out and the type of catalyst used. The data show that the use of the sodium hypophosphite and disodium phosphite catalysts of the present invention resulted in higher initial durable press appearance ratings, and greater durability of the smooth drying finish to repeated laundering, than was obtained with strongly alkaline trisodium phosphate and sodium carbonate catalysts. This was true when the catalysts were compared at the same normality as bases, and also when compared at the concentrations of maximum effectiveness. The teaching of Rowland et al., that the effectiveness of a given alkali metal salt as a curing agent for this type of cellulose crosslinking depends solely on the salt being a "strong base capable of forming a soluble, partial salt of polybasic acid in an effective concentration", proved inapplicable to sodium hypophosphite. The latter is a very weak base derived from an acid much stronger than 1,2,3,4-butanetetracarboxylic acid, and is relatively ineffective in forming the partial sodium salts of 1,2,3,4-butanetetracarboxylic acid. The importance of catalyst structure rather than catalyst basicity is also evident in comparing disodium phosphite and disodium phosphate, the former being the more effective catalyst, even though appreciably less alkaline than the latter. Example 3 Comparison of Various Polycarboxylic Acids as Durable Press Finishing Agents for Cotton Fabric with Sodium Hypophosphite or Disodium Phosphite as the Curing Catalyst An aqueous treating bath was prepared containing a specified concentration of a given polycarboxylic acid, a stated catalyst, and 1% emulsified nonionic polyethylene which served as a fabric softener. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 76 g/m² (3.2 oz/yd²) was thoroughly wetted by immersion in this treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 112%-126% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at 180°C for 90 seconds. The fabric was subsequently rinsed for 30 minutes in hot running water to remove any unreacted agents, and was oven dried at 85°C for 5 minutes. The durable press appearance ratings were determined after varying numbers of machine wash-and-tumble dry cycles, and are shown in Table IV as a function of the particular polycarboxylic acid and catalyst used. Other textile properties of certain of the above treated fabrics were determined prior to machine laundering, and are shown in Table V. The curing catalyst was 6.5% sodium hypophosphite monohydrate in these runs. Polycarboxylic Acid Wrinkle Recovery Angle (W+F) Warp Tear Strength Retained Warp Break Strength Retained Stiffness, Bending Moment (Warp) Cond. Wet 9.5% 1,2,3-propanetricarboxylic acid 300° 274° 61% 57% ( 5.3x10⁻⁴in.-lb.) 5.8 x 10⁻⁵ N.m 10.4% citric acid 295 251 62 56 (4.8 ) 5.3 9.4% trans -1-propene-1,2,3-tricarboxylic acid 296 238 72 58 (3.9 ) 4.3 6.3% all- cis -1,2,3,4-cyclopentanetetracarboxylic acid 298 262 68 54 (4.9 ) 5.4 6% DMDHEU 303 271 54 44 (4.2 ) 4.6 Untreated fabric 200 141 (100) (100) (4.8 ) 5.3 The data show aliphatic, alicyclic and aromatic polycarboxylic acids having 2-6 carboxyl groups per molecule impart wrinkle resistance and smooth drying properties to cotton fabric when heat cured on the fabric in the presence of an alkali metal phosphite or hypophosphite as a curing catalyst. The polycarboxylic acid used may also contain a carbon-carbon double bond or a hydroxyl group on a carbon atom attached to a carboxyl group in the molecule without eliminating the effectiveness in imparting durable press properties. The appearance of a yellow discoloration in white fabric treated with polycarboxylic acids containing a double bond or hydroxyl group can be concealed by afterdyeing the fabric with a basic dye, or by the use of fabric suitably dyed prior to treatment. A carboxyalkylthio substituent on a carbon atom attached to a carboxyl group in the polycarboxylic acid had no adverse effect on fabric whiteness, and was beneficial to the smooth drying properties. The use of polycarboxylic acids as durable press finishing agents with sodium hypophosphite as the curing agent resulted in durable press appearance ratings and conditioned wrinkle recovery angles comparable to those imparted by the conventional durable press finishing agent. DMDHEU, but with consistently less loss of tearing and breaking strength than was produced by DMDHEU. Example 4 Sodium hypophosphite as a Curing Catalyst for the Durable Press Finishing of Cotton Fabric with Citric Acid without Softener An aqueous treating bath was prepared containing 6.9% citric acid, and the stated catalyst. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 76 g/m² (3.2 oz/yd²) was thoroughly wetted by immersion in this treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 90-100% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at 180°C for 90 seconds, causing some fabric yellowing. The fabric was subsequently machine laundered and tumble dried. Textile properties after the one laundering cycle are reported in Table VI. Catalyst (% in pad (bath) % Fabric weight gain, % Durable press rating Wrinkle Recovery Angle, cond., deg, (W+F) Tear Strength retained,% Break Strength retained,% H₂NaPO₂.H₂O (5.9) 3.3 3.5 245 49 43 (4.9) 3.3 3.5 248 49 47 (3.9) 3.4 3.5 251 52 45 (2.9) 2.9 3.5 249 52 48 Untreated fabric 1.0 177 100 100 From Table VI, it can be seen that the use of sodium hypophosphite as a curing catalyst, for durable press finishing of cotton fabric with citric acid, improved the appearance properties over that of untreated cotton. Improvements were realized over a range of catalyst concentrations. Example 5 Sodium Hypophosphite as a Curing Catalyst for the Durable Press Finishing of Cotton Fabric with Citric Acid without Fabric Softener Aqueous treating baths were prepared containing citric acid in a range of concentrations and sodium hypophosphite curing catalysts as 50% of agent weight. An all-cotton desized, scoured and bleached 80x80 printcloth weighing 76 g/m² (3.2 oz/yd²) was thoroughly wetted by immersion in the treating bath, was passed between the rolls of a wringer, was again immersed in the treating bath, and was again passed through the wringer, the pressure of the wringer rolls being sufficient to give a wet pickup of 90-100% of aqueous mixture on the fabric, based on the original weight of fabric sample. The fabric was then dried in a forced draft oven at 85°C for 5 minutes, and was heat-cured in a second forced draft oven at 180°C for 90 seconds. The fabric was subsequently machine laundered and tumble dried. Textile properties after the one laundering cycle are reported in Table VII. Citric acid (% in pad bath) % Fabric weight gain, % Durable press rating Wrinkle Recovery Angle, cond., deg.,(W+F) Tear strength retained,% Break strength retained,% 12 6.4 3.5 253 36 42 9 3.9 3.5 253 37 41 7 3.3 3.5 249 42 42 5 1.3 3.3 241 42 45 Sodium hypophosphite, used as a curing catalyst for citric acid, produced durable press properties in cotton fabric. All of the samples of Examples 4 and 5 that were treated with citric acid to produce durable press appearance properties in cotton fabric were yellowed by the treatment; the yellow color could be substantially removed by treatment with the following agents: 1.5% magnesium monoperoxide, 1.5% sodium perborate, 1.5% sodium tetraborate, 1.5% boric acid, 1.5% sodium borohydride, 2% HC1, and 1% NaOC1.

Claims: A process for treating fibrous cellulosic material, comprising impregnating fibrous cellulosic material with a treating solution containing a polycarboxylic acid and a curing catalyst,characterized in that the polycarboxylic acid is selected from the group consisting of: aliphatic, alicyclic and aromatic acids either olefinically saturated or unsaturated and having at least three carboxyl groups per molecule; aliphatic, alicyclic and aromatic acids having two carboxyl groups per molecule and having a carbon-carbon double bond located alpha, beta to one or both of the carboxyl groups; aliphatic acids either olefinically saturated or unsaturated and having at least three carboxyl groups per molecule and a hydroxyl group present on a carbon atom attached to one of the carboxyl groups of the molecule; and, said aliphatic and alicyclic acids wherein the acid contains an oxygen or sulfur atom in the chain or ring to which the carboxyl groups are attached; one carboxyl group being separated from a second carboxyl group by either two or three carbon atoms in the aliphatic and alicyclic acids; one carboxyl group being ortho to a second carboxyl group in the aromatic acids; and, one carboxyl group being in the cis configuration relative to a second carboxyl group where two carboxyl groups are separated by a carbon-carbon double bond or are both connected to the same ring; the curing catalyst is selected from the group consisting of alkali metal hypophosphites and alkali metal phosphites;and in that the impregnated material is heated to produce esterification and crosslinking of the cellulose with the polycarboxylic acid in the material. A process as claimed in claim 1 wherein the polycarboxylic acid is selected from the group consisting of: maleic acid, citraconic acid; citric acid; itaconic acid; tricarballylic acid; trans-1-propene-1,2,3-tricarboxylic acid; 1,2,3,4-butanetetracarboxylic acid; all-cis-1,2,3,4-cyclopentanetetracarboxylic acid; mellitic acid; oxydisuccinic acid; and, thiodisuccinic acid. A process as claimed in claim 2 wherein the curing catalyst is selected from the group consisting of sodium hypophosphite and disodium phosphite. A process as claimed in claim 1 wherein the fibrous cellulosic material contains not less than 30% by weight of cellulosic fibers selected from the group consisting of cotton, flax, jute, hemp, ramie and regenerated unsubstituted wood celluloses. A fibrous cellulosic material characterized by having been treated by a process as claimed in any of claims 1-3. A fibrous cellulosic material as claimed in claim 5 wherein the polycarboxylic acid is 1,2,3,4-butanetetracarboxylic acid and the curing catalyst is selected from the group consisting of sodium hypophosphite and disodium phosphite.

Inventors: ANDREWS BETHLEHEM K, WELCH CLARK M, ANDREWS, BETHLEHEM K., WELCH, CLARK M.
Applicants: US AGRICULTURE, THE UNITED STATES OF AMERICA AS REPRESENTED BY THE SECRETARY UNITED STATES DEPARTMENT OF COMMERCE
Application year: 1989
Main classification: D06M13
IPC codes: D06M13, D06M11, D06M101