Oxide glasses having low glass transformation temperatures

Abstract: PbO-B₂O₃-Ag₂O glasses having a preferred weight ratio range of 76-88:10-15:2-10 have glass transition temperatures of less than 300°C and are especially useful for adhering together ceramic substrates such as for attaching integrated circuits to ceramic substrates. The glasses can be formulated with Ag particulates and organics and applied as pastes to provide conductive adhesives.

Description: Background of the Invention 1. Field of the Invention This invention relates to adhesive glasses and more particularly to PbO-B₂O₃-Ag₂O glasses with low glass transformation temperatures (T g ). 2. Description of the Previously Published Art Current conductive die attach adhesives which are used for attaching integrated circuits to ceramic substrates are essentially a mixture of silver and glass powder in an organic vehicle. They require firing at temperatures in the range 420-450°C to achieve strong bonding so as to ensure reliability of the integrated circuit package assembly. The primary reason for requiring such firing temperatures is to achieve sufficient flow in the glass component of the adhesive to allow wetting of the integrated circuit chip and the ceramic substrate. These high firing temperatures can result in degradation of the integrated circuit chips and migration and oxidation of Ni on the metallization of the substrate. See, for example, Owens, N. L., Microelectronic Manuf. and Test ., April 1986, pp. 6-7, at p. 7, which reviews nickel migration during organic burn-off. To lower the firing temperature and still achieve good bonding, glasses having lower glass transformation temperatures (T g ) or having more fluid properties at lower temperatures are required. Most glasses used in conductive die-attach adhesives are PbO-B₂O₃ based glasses with various oxide additives such as SiO₂, ZnO, Bi₂O₃, and BaO. These glasses have a T g typically above 300°C. Alkali metal oxides (Na₂O, K₂O) and thallium oxide can be added to the glass melt to lower the T g , but such oxide additions are known to result in glasses having poor resistance to moisture and, therefore, not acceptable as die-attach adhesives. See Takamori, T., "Solder Glasses", a chapter at pages 173-255 in Treatise on Materials Science and Technology , Vol . 17, Glass II, Edit. M. Momozawa and R. H. Doremus, Academic Press (1979). Certain other oxides lower the T g of PbO-B₂O₃ glasses but are avoided for various reasons. CdO and BaO present additional toxicity problems; Bi₂O₃ attacks platinum crucibles conventionally used in preparing the melts. PbO-B₂O₃ based glasses will dissolve oxide crucibles such as silica, alumina, clay, porcelain, etc. It is therefore important to match the glass to the melt container and vice-versa. To meet the stringent requirements for die attachment, aside from lower T g and considerations above mentioned, the glasses must also be resistant to crystallization during the firing step. This is because crystallization of the glass can lead to abrupt increases in viscosity and, hence, prevent flow and wetting of the integrated circuit and ceramic substrate. Prior patents disclose various glass compositions, but they provide no suggestion of the low Tg PbO-B₂O₃-Ag₂O glass composition which are found effective here for die attach adhesives. U.S. Patent 3,711,328, Wada et al. (1973), discloses a glass frit consisting essentially of 0.1-17 weight % Ag₂O and 83-99.9 % of a base composition consisting essentially of 60-80 % PbO, 8-16 % B₂O₃, 12-24 % ZnO. The basic glass composition has ZnO as a required component. In Example 12 of the patent, PbO is 64.7 weight %, B₂O₃ 11.6%, ZnO 13.7%, Al₂O₃ 7.0%, and Ag₂O 3.3%. It is used in making a resistor paste with no suggestion for use as an adhesive. U.S. 4,401,765, Dietz et al. (1983), discloses a silver-filled lead borosilicate glass metallizing paste for bonding silicon dies to ceramic substrates. Ag₂O is absent. U.S. 4,446,059, Eustice (1984) discloses a conductive composition containing lead borosilicate, Ag₂O, and Ag powder for use as automotive window defoggers. Proportions of ingredients for such composition are stated in column 3 of the patent as (with respect to the instant invention), 60-98.5% Ag, 20-1% lead borosilicate, and 5-60% of a blend of Ag₂O and B₂O₃ as a colorant. This is a physical mixture of the ingredients and does not disclose the homogenous composition as set forth herein. U.S. 4,636,254, Husson et al. (1987); discloses a silicon die attach paste consisting of a physical mixture of Ag flake 65.38 weight %, lead borate glass frit 17%, Ag₂O 2.62%, balance organics to make 100%. The Ag flake is 50% 200 mesh, 50% 100 mesh. We differ from Husson, inter alia , in that our Ag₂O is an integral component of our glass, whereas in Husson the Ag₂O is in physical mixture. U.S. 4,699,888, Dumesnil et al. (1987), discloses adhesive glass pastes containing 75-85 weight % Ag powder and a glass containing PbO, B₂O₃, SiO₂, Cu₂O, a metal fluoride, and optionally ZnO, Bi₂O₃. The materials were powdered, formulated as a paste, and used to bond silicon wafers to alumina substrates. Ag₂O was not disclosed. The pastes were fired at 380° and 450°C. JP 74 02,169 (Application No. 70 101,763 of November 16, 1970) describes a glass composite used as a cover for an electrically resistant element consisting of cadmium oxide. The electrically resistant element was prepared for an integrated circuit by calcining a mixture of a noble metal powder or metal oxide and a glass binder. The glass cover contains 70-76% PbO, 6-12% B₂O₃, 0.5-4% SiO₂, 6-12% Al₂O₃, 0.1-10% CdO+Ag₂O, ≧0.05% CdO and ≧0.05% Ag₂O. 3. Objects of the Invention It is an object of the invention to provide a die attach adhesive containing a glass characterized by a T g not higher than about 300°C, good wetting properties, containing components which are compatible with melting in platinum crucibles to maintain high purity, and resistant to moisture and to recrystallization of components. Another object is to provide two-piece ceramic articles bonded with a low-T g PbO-B₂O₃-Ag₂O glass. A still further object is to adhere integrated circuit chips to a ceramic base without degrading the chip. An additional object is to reduce formation of NiO on substrate metallization. Further objects are to provide particulate sizes of glass and Ag to minimize cracking and voids in the adhesive. These and further objects will become apparent as the description of the invention proceeds. Summary of the Invention PbO-B₂O₃-Ag₂O glass having compositions with a respective weight ratio of 76-88: 10-15: 2-10 have glass transformation temperatures (T g ) of less than 300°C and can be used as adhesives for adhering together two or more substrates such as for attaching integrated circuit chips to ceramic substrates. The lower fusion temperatures avoid damage to the circuits on the chips. Also, lower temperatures reduce NiO formation, which eliminates the need for hydrogen reduction prior to lid sealing an integrated circuit into the package. In a preferred embodiment the comminuted ("powderized") glasses can be mixed with silver particles to provide thermally and electrically conductive adhesives for such attachments. When making the powdered glass and silver particle mixture, it has been found very effective to have the glass to Ag in a weight ratio of about 1:3-5.7 and to have the Ag particles in a mixture of two components A and B. Component A has Ag particles with an average size of about 9 µm and with about 90 weight % less than 15 µm and about 10% less than 4 µm. Component B has Ag particles with an average size of about 3.5 µm and with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm. The weight ratio of components A:B is preferably about 3-6:1. Conductive adhesive pastes are made from the glass powders of this invention, conductive metal particulates (preferably Ag) and organic binder components including solvents. Detailed Description of the Invention The preferred procedure for the preparation of PbO-B₂O₃-Ag₂O glasses on a small scale in 25 gm batches involves mixing powders of PbO (76-88 wt. %), B₂O₃ (10-15) wt. %), and Ag₂O (2-10 wt. %) and melting in platinum crucibles in an electrically heated furnace at 800°C for about 15 minutes. The glasses are formed by quenching the melts to ambient temperature by pouring onto a steel platen. It was found preferable to add Ag₂O in a different, non-oxide form such as AgNO₃ to form a homogeneous glass and to obtain the benefit of having a lower T g . If Ag₂O was used as such, the undesired reaction Ag₂O → 2 Ag + 1/2 O₂ occurs during heating of the powder mixture, leading to Ag particulate inclusions in the glass and no substantial lowering of T g since Ag₂O is not incorporated into the structure of the glass. The T g of the glasses was determined by differential scanning calorimetry carried out at heating rate of 20°C/min in air. The results are shown in Table I. The glasses in all examples herein were prepared by the general procedure described above, using the amounts of ingredients as stated. As can be seen in Table I, glasses in the PbO-B₂O₃-Ag₂O system exhibit a very low T g , particularly when Ag₂O is substituted for PbO (while the B₂O₃ content remains constant), and when Ag₂O is substituted for B₂O₃ (while the PbO content remains constant). The glasses of examples 12-14 have greater than 15% B₂O₃ and are not preferred glasses because the Tg temperature is greater than 300°C. Variation of T g with Composition of Glasses Weight Percent Example No. PbO B₂O₃ Ag₂O T g (°C) 1 90 10 0 281 2 88 10 2 266 3 85 10 5 254 4 80 10 10 250 5 88 12 0 293 6 85 12 3 284 7 82 12 6 264 8 80 12 8 260 9 85 15 0 320 10 80 15 5 293 11 76 15 9 283 12 76 18 6 317 13 80 20 0 354 14 76 21 3 338 To illustrate further the effectiveness of Ag₂O in PbO-B₂O₃ glasses, PbO-B₂O₃ mixtures having the same proportion of PbO and B₂O₃ as in the glass of Example No. 6, but where the Ag₂O has been replaced with other additives were prepared in the same way and the T g determined. Results of the Comparison Examples 15-20, with various additives are given in Table II. As can be seen from Tables I and II, the addition of Ag₂O produced the lowest T g . With a view of increasing resistance to crystallization, multicomponent glasses have been developed within the generic concept of the invention. It is expected that the addition of ZnO in an amount of up to 10 wt. % and the addition of Al₂O₃ in an amount of up to 2 wt. % in PbO-B₂O₃-Ag₂O glass compositions can improve the resistance to crystallization. Examples are given in Table III. A preferred composition in Table III is shown in Example 23. That composition in particular has excellent stability towards devitrification, as indicated by the large temperature difference between T x and T g . Tx is the temperature where crystallization first appears. The resistance to moisture was tested by powderizing the glass and placing it in a Parr bomb in water at 121°C for 21 hours. The amount of extractable ions (in the water) from the glass of Example No. 23 was found to be much less than 25 ppm. See Table VI infra. This shows the composition had excellent resistance to moisture. Composition of PbO-B₂O₃-Ag₂O -Based Glasses in Weight % Example PbO B₂O₃ Al₂O₃ ZnO Ag₂O T g (°C) T x (°C) 21 83.42 11.61 1.64 3.33 279 398 22 83.78 11.66 1.88 2.68 281 404 23 83.71 11.45 0.29 1.88 2.67 280 410 Adhesive Pastes Adhesive pastes can be made using the glasses of this invention by comminuting the glasses such as the composition of Example No. 23 into a powder and optionally mixing with conductive particulates such as Ag followed by mixing with an organic binder conventionally used for this purpose. The glass comminution process can be done by conventional processes such as by ball milling. However, particular attention should be paid such that all the particles used for our invention pass through a 0.07mm (200-mesh) screen and particles less than about 1-2 µm are not generated. In other words, if particles less than about 1-2 µm are generated, they should be discarded. Glass particles finer than one or two microns will shrink excessively during the firing of the adhesive paste. This results in voiding underneath the die with consequently less heat dissipation from the device such as an integrated circuit. Excessive shrinkage also causes cracks to form in the adhesive around the perimeter of the die. These cracks reduce both die shear and die pull strengths. A homogeneous blend of two types of silver particles is preferably used. The silver used in larger amount is of an average particle size of approximately 9 µm. Its preferred particle size distribution is relatively narrow, having approximately 90% less than 15 µm and about 10% less than 4 µm. These coarse particles provide a conductive skeleton which shrinks minimally during the firing of the adhesive. It allows the glass to flow readily through its interstices, which in turn supplies its high fired strength. The silver used in the smaller amounts is of an average particle size of approximately 3.5 µm. Its particle size distribution ranges from about 90% less than 11 µm to about 10% less than 0.7 µm. The advantage to this material is that it fits into the conductive skeleton mentioned before, while providing accelerated sintering at the reduced firing temperature of this adhesive. This increases both the thermal and electrical conductivity of the adhesive as well as its ultimate strength. The ratio of these two types of silver particles is chosen to minimize unwanted shrinkage (e.g., by choosing a larger amount of the coarse silver), while maximizing conductivity and strength (e.g., by choosing an increased amount of the finer silver). It has been found that the optimum ratio of coarse to fine silver is about 4:1. Good adhesives can be generated in ranges from about 6:1 to 3:1. So far as we can determine, these silver blends are novel per se. Various conventional organic binders are available, such as isobutyl methacrylate, nitrocellulose, cellulose acetate butyrate, etc. A preferred organic binder is ethylcellulose. These materials are conventionally dissolved in a solvent for formulating the paste. The amount of binder (exclusive of solvent) is typically about 0.2-1.0 weight %, preferably about 0.35 weight %, based on the total weight of paste. Various solvents may be used alone or in combination to generate the desired evaporation rates. Ester-alcohols, terpene-alcohols, dibasic esters and glycol-ethers and their acetates are particularly suitable for this application. These solvents have relatively high boiling points and, therefore, avoid unwanted room temperature volatility. Solvents are chosen for the combination of properties desired. Ester- and terpene-alcohols impart excellent strength and dispersibility. Dibasic esters and glycol ethers allow virtually void-free films upon drying. Typical solvent to suspend the solid particulates is in the range 9-24.8 weight %. Conductive adhesive pastes of our invention have the following formulations: (A) Glass powder of the invention, 11-23 weight %, preferably 15-19 weight %; (B) Conductive metal particulates (preferably Ag), 56-77 weight %, preferably 65-70 weight %; and (C) Organic (including solvent), 10-25 weight %, preferably 13-17 weight %. Our preferred paste uses the powdered glass of Example No. 23, one part by weight; Ag particulates, four parts; and organic, one part, where the organic comprises ethylcellulose in an ester-alcohol solvent such as Texanol R (manufactured by Eastman Kodak). The Ag is a 4:1 blend of the two particle sizes as above described. The paste may be applied to a ceramic base, and then the second ceramic item to be attached such as an integrated circuit chip, may be applied to the paste before firing. In the typical and most convenient application the paste is applied to a ceramic base such as alumina, and then a second ceramic such as an integrated silicon circuit chip is applied to the paste, and the assembly is heated to about 100°C above the glass T g point, whereupon a good bond results. For example, bare-back silicon chips were attached to 96% alumina substrates using the paste of Example 23 at different temperatures. The results are set forth in Table IV. The die shear strength test which is described in MIL STD 883 Method 2019.5 is essentially a measure of the shear force necessary to remove the die from the substrate to which it is adhered. A material would be considered accepted by the MIL specification if it had a die shear of 49 N (5 kg). Since the values achieved here are over 3 times the specification requirement as reflected in die shear strength values shown in Table IV, they are considered to be bonded excellently at temperatures less than 400°C. Shear and pull strengths and ionic purity of a glass of this invention as compared with a typical prior art glass was conducted as follows. Glass was manufactured using the preferred embodiment of U.S. Patent No. 4,699,888 to Dumesnil et al. The glass composition was made from 5.44 g PbF₂, 0.90 g SiO₂, 2.18 g Cu₂O, 1.46 g Bi₂O₂, 5.44 g ZnO, 1.18 g Al₂O₃, 8.16 g B₂O₃ and 75.24 g PbO. Although Dumesnil et al discloses adding powdered silver metal, there is no suggestion of the present composition using Ag₂O. Dumesnil et al employ an 8-component glass system utilizing PbF₂, Cu₂O and Bi₂O₃ for lowering Tg. Bi₂O₃ , as mentioned before, attacks the platinum crucible used for melting of high purity glasses. PbF₂, as will be seen below, renders the glass to be less stable with respect to attack by moisture. None of these components are present in our invention. The T g measured 269°C for the Dumesnil et al composition as compared to a glass from Example 23 of this application at 280°C. Although the T g of the prior art material was lower than that of the glass of this invention, its fluidity when fired at 395°C for six minutes is less than that reported here as demonstrated by the following strength numbers achieved by substituting each glass into the formulation mentioned previously (i.e., glass 1 part, Ag 4 parts, and organic 1 part, where the organic comprises ethylcellulose in an ester-alcohol solvent): Dumesnil This Invention (Example 23) Die Shear 107.9N (11 kg) 362.8N (37 kg) Die Pull 13.3N (3 lb) 222.4N (50 lb) The die shear test is according to MIL STD 883 Method 2019 and the die pull test is according to MIL STD 883 Method 2027. Additionally, ionic purity was measured on these two adhesive pastes made with these glasses. Results were as follows: Dumesnil This Invention (Example 23) F⁻ 53 ppm 14 ppm Cl⁻ 14 " 11 " Na⁺ 15 " 15 " K⁺ 6 " 3 " Ionic purity is generally required in die attach adhesives as it is to be used in most electronic devices. Residual moisture in the sealed package will combine with available Na and K ions which can short the circuiting on the chip. F and Cl ions when combined with moisture, form corrosives which also degrade the device. Consequently, the lower the value for the concentration of extractable ions shows that the composition of this invention is not only more resistant to water than the prior art, but also better in terms of long-term device reliability. The substrate-paste-chip assembly is preferably heated in a two step process. First a drying step is used to drive off the organic components, then the firing step melts the glass and bonds the substrates. Broadly speaking, both steps are well known in the art. We differ in that our glasses permit a lower firing temperature while giving a bond of superior properties. The initial drying step (to drive off the organic) may be omitted under certain circumstances, for example, if the die size is 0.3 cm square (0.05 inches square) or less. Also, for larger dies, drying can be incorporated into the firing cycle by slowing the heating rate. Laminates may be made by additional layers of paste and ceramic. Considerable variation in the PbO-B₂O₃-Ag₂O composition of the glass is possible while retaining low T g and other desirable properties. Our work indicates that a PbO-B₂O₃-Ag₂O weight range of 76-88:10-15:2-10 is operable, and preferably 80-88:10-12:2-10. Our examples used 25 g. batches. Obviously, any size batch can be made up, limited only by the size of the platinum crucible and the heat source. Melt times may range from a few minutes to several hours, depending on batch size, heat source, etc. The invention glasses can be mixed with Ag (or any other conductive particulates) in a glass:conductive particulate weight range of 1:2.3-7.3, preferably 1:3-5.7. With respect to substrates adherable by the glasses of this invention, alumina and silicon ceramics are especially suitable. Others include beryllia, steatite, silicon nitride, silicon carbide, gallium arsenide, etc. The glasses of this invention are especially designed for adhesive function at about, or less than, 400°C, which temperature is sufficiently low to prevent degradation of most integrated circuit chips and Ni migration and oxidation. Obviously, if chips are being adhered where such degradation is not a problem, higher temperatures can be used, e.g., up to about 450°C. In our examples we used Ag as the conductive matrix. However, our invention is not limited to Ag; substantially any of the conductive particulates conventionally used in the die adhesive art are useful, such as gold, platinum, or any of the air-fired metals. Nickel may be used with care at low temperatures. It is understood that the foregoing detailed description is given merely by way of illustration and that many variations may be made therein without departing from the spirit of this invention.

Claims: Claims for the following Contracting States : AT, BE, DE, FR, GB, GR, IT, LU, NL, SE A glass composition having a glass transformation temperature below about 300°C, comprising PbO, B₂O₃, and Ag₂O in a respective weight ratio of 76-88:10-15:2-10, preferably of about 80-88:10-12:2-10. A glass composition according to Claim 1, additionally containing up to 10 wt. % ZnO and optionally up to 2 wt. % Al₂O₃. A glass composition according to Claim 2, consisting essentially of, in weight %, PbO 83.71%; B₂O₃ 11.45%; Al₂O₃ 0.29%; ZnO 1.88%; and Ag₂O 2.67%. A glass composition according to Claim 1 in powder form. A glass composition according to Claims 3 or 4 in powder form having a particle size which pa-ses through a 200 U.S. mesh screen, but being not less than about 2 µm. A homogeneous conductive adhesive composition comprising powdered glass of Claim 4 and conductive particulates. A homogeneous conductive adhesive composition comprising powdered glass of Claim 5 and Ag particulates, in a glass:Ag weight ratio of about 1:2.3-7.3, preferably of about 1:3-5.7. A homogeneous conductive adhesive composition comprising powdered glass of Claim 5 and Ag particles, in glass:Ag weight ratio of 1:3-5.7 and preferably being 1:4; said Ag particles consisting essentially of a mixture of components A and B; component A being Ag particles having an average size of about 9 µm, with about 90 weight % less than 15 µm and about 10% less than 4 µm; component B being Ag particles having an average size of about 3.5 µm, with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm; and the weight ratio of components A:B is about 3-6:1, preferably about 4:1. A paste composition comprising the composition of Claims 6 to 8 and an organic binder. A paste composition comprising (A) 11-23 weight %, preferably 15-19 weight % powdered glass, said glass comprising PbO, B₂O₃, and Ag₂O in a respective weight ratio of 76-88:10-15:2-10; (B) 56-77 weight %, preferably 65-70 weight % conductive metal particulates; (C) 10-25 weight %, preferably 13-17 weight % organic, including solvent. A paste composition according to Claim 10, wherein (B) is Ag consisting of a homogeneous blend of (I) Ag particles having an average size of about 9 µm, with about 90 weight % less than 15 µm and then about 10% less than 4 µm, and (II) Ag particles having an average size of about 3.5 µm, with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm; the weight ratio of I:II being about 3-6:1, preferably about 4:1. Article comprising a substrate and a layer containing a glass composition of claims 1 to 3 the glass composition being melted onto the substrate. Article according to Claim 12, wherein the glass composition lies between and adheres together two substrates, at least one substrate being preferably alumina or silicon. Article comprising two ceramic substrates adhered together with an adhesive composition, said adhesive composition comprising, in parts by weight, about 4 parts Ag powder and about 1 part of a glass, said glass having a T g of about 280°C and a T x of about 410°C and said glass having a composition comprising PbO 83.71, B₂O₃ 11.45, Al 2 O 3 0.29, ZnO 1.88 and Ag₂O 2.67. Method of adhering two ceramic substrates comprising applying therebetween a paste composition according to claim 9, then heating the result to a temperature sufficient to melt the glass portion of the paste composition but less than 400°C, thereby to adhere together the two substrates, the conductive powder in the paste composition being preferably Ag. Method according to Claim 15, wherein the powdered glass in the composition comprises in parts by weight PbO 85, B 2 O 3 12, and Ag₂O 3. Method according to Claim 15, wherein the composition comprises in parts by weight, (a) 1 part of a composition comprising about PbO 83.71, B₂O₃ 11.45, Al₂O₃ 0.29, ZnO 1.88, and Ag₂O 2.67; (b) 4 parts Ag particulates; and (c) 1 part organic including solvent; said Ag particulates consisting essentially of a homogeneous blend of components A and B, component A being Ag particles having an average size of about 9 µm, with about 90 weight % less than 15 µm and about 10 weight % less than 4 µm; component B being Ag particles having an average size of about 3.5 µm, with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm; and the weight ratio of components A:B is about 4:1. Method according to Claims 15 or 17, wherein at least one of the substrates carries a metal pattern, said pattern being unaffected by the heating operation. Method according to Claim 18, wherein the substrate with the metal pattern is an integrated circuit silicon chip. Claims for the following Contracting State : ES A homogeneous conductive adhesive composition comprising conductive particulates and a powdered glass composition having a glass transformation temperature below about 300°C, comprising PbO, B₂O₃, and Ag₂O in respective weight ratio of 76-88:10-15:2-10, preferably of about 80-88:10-12:2-10. A homogeneous conductive adhesive composition according to Claim 1, wherein the powdered glass composition additionally contains up to 10 wt. % ZnO and optionally up to 2 wt. % Al₂O₃. A homogeneous conductive adhesive composition according to Claim 2, wherein the powdered glass composition consists essentially of, in weight %, PbO 83.71%; B₂O₃ 11.45%; Al₂O₃ 0.29%; ZnO 1.88%; and Ag₂O 2.67%. A homogeneous conductive adhesive composition according to Claims 1 to 3 wherein the powdered glass composition has a particle size which passes through a 200 U.S. mesh screen, but being not less than about 2 µm. A homogeneous conductive adhesive composition according to Claim 4 comprising Ag particulates, in a glass:Ag weight ratio of about 1:2.3-7.3, preferably of about 1:3-5.7. A homogeneous conductive adhesive composition according to Claim 4 comprising Ag particles in glass:Ag weight ratio of 1:3-5.7 and preferably being 1:4; said Ag particles consisting essentially of a mixture of components A and B; component A being Ag particles having an average size of about 9 µm, with about 90 weight % less than 15 µm and about 10% less than 4 µm; component B being Ag particles having an average size of about 3.5 µm, with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm; and the weight ratio of components A:B is about 3-6:1, preferably about 4:1. A paste composition comprising the composition of Claims 1 to 6 and an organic binder. A paste composition comprising (A) 11-23 weight %, preferably 15-19 weight % powdered glass, said glass comprising PbO, B₂O₃, and Ag₂O in a respective weight ratio of 76-88:10-15:2-10; (B) 56-77 weight %, preferably 65-70 weight % conductive metal particulates; (C) 10-25 weight %, preferably 13-17 weight % organic, including solvent. A paste composition according to Claim 8, wherein (B) is Ag consisting of a homogeneous blend of (I) Ag particles having an average size of about 9 µm, with about 90 weight % less than 15 µm and then about 10% less than 4 µm, and (II) Ag particles having an average size of about 3.5 µm, with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm; the weight ratio of I:II being about 3-6:1, preferably about 4:1. Article comprising a substrate and a layer containing a glass composition of claims 1 to 3 the glass composition being melted onto the substrate. Article according to Claim 10, wherein the glass composition lies between and adheres together two substrates, at least one substrate being preferably alumina or silicon. Article comprising two ceramic substrates adhered together with an adhesive composition, said adhesive composition comprising, in parts by weight, about 4 parts Ag powder and about 1 part of a glass, said glass having a T g of about 280°C and a T x of about 410°C and said glass having a composition comprising PbO 83.71, B₂O₃ 11.45, Al₂O₃ 0.29, ZnO 1.88 and Ag₂O 2.67. Method of adhering two ceramic substrates comprising applying therebetween a paste composition according to claim 9, then heating the result to a temperature sufficient to melt the glass portion of the paste composition but less than 400°C, thereby to adhere together the two substrates, the conductive powder in the paste composition being preferably Ag. Method according to Claim 13, wherein the powdered glass in the composition comprises in parts by weight PbO 85, B₂O₃ 12, and Ag₂O 3. Method according to Claim 13, wherein the composition comprises in parts by weight, (a) 1 part of a composition comprising about PbO 83.71, B₂O₃ 11.45, Al₂O₃ 0 29, ZnO 1.88, and Ag₂O 2.67; (b) 4 parts Ag particulates; and (c) 1 part organic including solvent; said Ag particulates consisting essentially of a homogeneous blend of components A and B, component A being Ag particles having an average size of about 9 µm, with about 90 weight % less than 15 µm and about 10 weight % less than 4 µm; component B being Ag particles having an average size of about 3.5 µm, with about 90 weight % less than 11 µm and about 10 weight % less than 0.7 µm; and the weight ratio of components A:B is about 4:1. Method according to Claims 13 or 15, wherein at least one of the substrates carries a metal pattern, said pattern being unaffected by the heating operation. Method according to Claim 16, wherein the substrate with the metal pattern is an integrated circuit silicon chip. A glass composition having a glass transformation temperature below about 300°C, comprising PbO, B₂O₃, and Ag₂O in a respective weight ratio of 76-88:10-15:2-10, preferably of about 80-88:10-12:2-10. A glass composition according to Claim 18, additionally containing up to 10 wt. % ZnO and optionally up to 2 wt. % Al 2 O 3 A glass composition according to Claim 19, consisting essentially of, in weight %, PbO 83.71%; B₂O₃ 11.45%; Al₂O₃ 0.29%; ZnO 1.88%; and Ag₂O 2.67%. A glass composition according to Claim 18 in powder form. A glass composition according to Claims 20 or 21 in powder form having a particle size which passes through a 200 U.S. mesh screen, but being not less than about 2 µm.

Inventors: CONLON ANASTASIA MARY, LAU JOHN WING-KEUNG, CONLON, ANASTASIA MARY, LAU, JOHN WING-KEUNG
Applicants: GRACE W R & CO, W.R. GRACE & CO.-CONN.
Application year: 1989
Main classification: C03C8
IPC codes: C03C8, C04B37, C03C3, C22C32