MULTILAYER NON-WOVEN FABRIC

Abstract: A multilayer non-woven fabric which provides high strength under low distortion or elongation conditions without impairing the draining properties of conventional non-woven fabrics or the ease with which they can be transported or be made to conform to the earth surfaces over which they are laid. The multilayer non-­ woven fabric disclosed comprises knitted or woven fabric layers and non-woven fabric layers multilaid together; the knitted or woven fabric layers consist of synthetic resin multifilaments oriented at least in one direction and having a tensile elastic modulus of 20GPa or more, preferably 50GPa or more, and a tensile strength of 1.2GPa or more, preferably 1.5GPa or more, while the non-woven fabric layers consist of long or short synthetic resin fibers arranged at random.

Description: This invention relates to a multilayer, water permeable non-woven fabric which displays the same draining properties as prior art non-woven fabrics and high strength under low distortion or elongation (15% or less) conditions. In construction works undertaken in the field of civil engineering, in particular, in anti-flood afforestation works, riparian works, road construction works, or the construction of structures on soft ground, synthetic resin drainage materials or reinforcing materials are sometimes spread over the bottom or inner zone of an earth structure or a building for the purpose of improving the operational efficiency and stability after construction has been completed. However, none of these synthetic resin materials excel in both draining and reinforcing properties, each only satisfying one or the other to an adequate extent. Some materials may be regarded as satisfactory in both aspects to a certain degree. In such cases, however, the significance of one of these two categories of properties is only like that of an accessory with respect to the other. In earth structures or building bases, any deformation of a structure due to distortion of about 5% to 15% is judged to be indicative of its breakdown or its ceasing to function as designed. Synthetic resins exhibiting a distortion rate in the range 5 % to 15 % (as shown by the results of a distortion test as set forth in JIS L-1096) are conventionally employed as reinforcing materials. The problem with these conventionally used synthetic resin materials, which have a distortion rate in the above range and which exhibit a high strength, is that they only provide poor draining properties. The present invention provides a multilayer, water permeable non-woven fabric comprising knitted or woven fabric layers and non-woven layers multilaid together, said knitted or woven fabric layers consisting of synthetic resin multifilaments oriented in at least one direction and having a tensile elastic modulus of at least 20GPa, preferably at least 50GPa, and a tensile strength of at least 1.2GPa, preferably at least 1.5GPa, and said non-woven fabric layers consisting of synthetic resin fibers arranged at random. The fabric of the present invention has high strength under low distortion conditions without impaired draining properties as compared to conventional non-woven fabrics and retains the ease with which they can be transported or be made to conform to the earth surfaces over which they are laid. The synthetic fibers which are arranged at random may be, for example, long or short. There are now described preferred embodiments of the invention. (A) The synthetic resin multifilaments used in the knitted or woven fabric layers are multifilaments which have an initial tensile elastic modulus of at least 20GPa, preferably at least 50GPa, and a tensile strength of at least 1.2GPa, preferably at least 1.5GPa, as measured in accordance with the test method of JIS L-1013. Any deviation of the initial tensile elastic modulus and the tensile strength from the above-mentioned ranges results in synthetic resin multifilaments whose strength is unsatisfactory for reinforcing materials. The monofilaments making up each of the above multifilaments may consist of filaments made of, for example, synthetic resins of the polyamide type, polyester type, polyacrylonitrile type, polyvinylalcohol type, polyolefin type or polystyrene type. Of these, synthetic resins of the polyolefin type, such as polyethylene and polypropylene, are preferred. In particular, drawn products of ultra-high molecular weight polyethylene are most preferred. Such drawn products can be produced, for example, by the methods disclosed in JP-A-59-187614 and JP-A-59-130313. The multifilaments may consist of unwoven threads or ciliary threads made of materials selected from the above-mentioned synthetic resins. By "unwoven threads" is meant threads obtained by regularly or irregularly unweaving films or tapes of a synthetic resin with a carding machine. The term "ciliary threads" means bulky, spun-thread-like threads which have no network structure and which can be obtained by controlling the fiber distribution in each component fiber section. The fineness of the multifilaments used in this invention is preferably from 300 to 2500 denier (33.4 to 278 tex), in particular 500 to 2000 denier (55.6 to 222 tex). These multifilaments are oriented in at least one direction of the texture of a knitted or woven fabric, thereby enhancing the strength of the texture in that direction. The texture type of the woven fabric may be plain weave, stain weave, twill weave, or various other texture types to which these basic texture types are applied. When multifilaments of the above-specified type are oriented in one direction, the filaments arranged in other directions may be of some other type, such as multifilaments or monofilaments whose tensile elastic modulus and tensile strength are not in the above-mentioned ranges. It is also possible to use, additional to the multifilaments oriented in at least one direction as described above, multifilaments whose tensile elastic modulus and tensile strength are not in the above-mentioned ranges not only in a single but in a plurality of directions such as, for example, warp and weft. This arrangement helps to enhance the strength in any particular direction. The mass (weight/area ratio) of a knitted or woven fabric layer in which multifilaments of the above-specified type are arranged in at least one direction is preferably 50 to 1000g/m², in particular 100 to 500g/m² (B) The non-woven fabric layers in which synthetic resin fibers are arranged at random may be non-woven fabric layers composed of long fibers (including continuous fibers) or short fibers, for example polyamide fibers, polyester fibers, polyacrylonitrile fibers, polyvinylalcohol fibers, polyvinyl chloride fibers, polyvinylidene chloride fibers, polyethylene fibers, polypropylene fibers or polystyrene fibers. The layers are preferably made of a non-woven fabric of polyamide fibers, polyester fibers, polyvinylalcohol fibers, polyethylene fibers or polypropylene fibers. While the above-mentioned fibers vary in draft ratio and drawing factor, those having a high strength and a low drawing factor are preferred. In view of the fact that a mechanical confounding method, for example using a needle punch, is employed, as described later, long fibers are more preferred than short ones. Normally, the long or short fibers in the non-woven fabric layers are formed by melt spinning. As a result, the fiber groups are randomized, and are mended with, for example, screens to form webs. If so desired, a thermal stabilizer, an antioxidant, an ultraviolet radiation absorbent, a pigment, a flame retarder or a surface active agent, for example, may be added to the molten material during, before or after melt spinning and web forming, or may be applied to the surface of the formed fibers. The fineness of the long or short fibers in non-woven fabric layers thus formed is preferably 50 to 1000g/m², in particular 100 to 500g/m². (C) The following structures are examples of multilayer structures consisting of layers of a knitted or woven fabric and a non-woven fabric: (1) A bilaminar structure in which one is superposed on the other; (2) A triplex structure in which a knitted or woven fabric layer is sandwiched between non-woven fabric layers; (3) A triplex structure in which a non-woven fabric layer is sandwiched between knitted or woven fabric layers; and (4) A multilayer structure in which structures of the above type (1) are laid on each other. Of these, a triplex structure (2) is particularly preferred. (D) A knitted or woven fabric layer and a non-woven fabric layer may be connected to each other by, for example, a needle punch, a water jet punch, an ultrasonic welder, a high-frequency welder or heat embossing. When using a needle punch, a satisfactory connection between layers can be attained if the needle punch penetrates each layer 30 to 150 times, preferably 50 times or more, per 1cm². The needle depth of the needle punch is preferably 8 to 15mm, in particular 10 to 14mm. Since at least one direction component of the knitted or woven fabric layer in the multilaid structure thus obtained consists of multifilaments, the degeneration in initial tensile strength due to the needle punch is relatively low in this multilayer structure, as compared with flat-type structures. It also displays excellent water permeability. Furthermore, by performing surface treatment of each layer with a nonionic surface active agent, such as a polyoxyethylene alkyl ether or polyoxyethylene alkyl phenyl ether, before or during the needle punch operation, the degree of fiber mutilation by the needle punch in each layer is mitigated, and deterioration in the initial tensile strength is more reliably prevented. This is also advantageous in that each layer is made hydrophilic, which improves its water permeability. The connections between layers through thermal fusion effected by means of the above-mentioned welders or heat embossing may be partial connections. To establish firm connection between layers, it is desirable that the knitted or woven fabric layer and the non-woven fabric layer be made of the same synthetic resin, or, if different, synthetic resins which are compatible with each other. The tensile strength of this product is preferably such that it can be indicated by a maximum load of 4.5tf/m or more when the extensional distortion in at least one direction, as measured by a test conducted in accordance with the cut strip method of JIS-1096, is 15% or less. Its water permeability coefficient is preferably 1 x 10¹ to 1 x 10²cm/s in the in-plane direction (horizontal direction) and 1 x 10⁰ to 1 x 10²cm/s in the vertical direction. As described above, the multilayer non-woven fabric of this invention provides a more satisfactory initial tensile strength and water permeability (draining property) than conventional laminated sheets used as materials in the field of civil engineering. Furthermore, since the non-woven fabric layers serve as cushions to protect the knitted or woven fabric layers, they not only provide a high tensile strength and a good elongation percentage but also display resistance under repeated loading, thereby maintaining its high performance as a sheet material for use in civil engineering works for long periods of time. These characteristics make the multilayer non-woven fabric of this invention suited to use as a foundation reinforcing material for stabilizing banking and weak ground. In addition, since it exhibits excellent load stress distributing properties when used in road foundations, it can also, for example, be used for promoting the consolidation of weak ground in vertical draining works. Apart from this, it can also be used as a material for use in draining, for example, percolated water or ground water, or as an anti-drafting or anti-scouring material, for example for protecting the shores of rivers or the sea. Furthermore, it is also suited to use as an anti-mud-pumping material for the ground beneath railroads where resistance to sediment separation and repeated loading is required. It also finds a variety of uses in civil engineering, such as use as a sheet for mortar or beton spraying work, as a material for preventing the clogging of culverts (drainage piping below ground), as a draining or insulating material for tunnels and as a material for preventing oil leakage from pipelines. The following Example further illustrates the present invention. EXAMPLE A laminated non-woven fabric was formed under the following conditions, and was subjected to a tensile strength test: (Non-Woven Fabric): A long-fiber non-woven fabric made of polypropylene; mass (weight/area ratio) : about 130g/m² (Knitted or Woven Fabric): A plain-weave fabric in which drawn multifilaments of ultra-high molecular polyethylene having a fineness of 1000D are oriented in one direction, seven per inch (2.54cm), as warp, and in which unwoven threads of monofilaments made of polypropylene are provided as weft. Strength of the drawn multifilaments: 25g/D (Forming Conditions): A knitted or woven fabric sheet was sandwiched between two non-woven fabric sheets, and they were connected together by a needle punch. Number of needle punches: 50/m² Needle depth: 14mm (Test Method): The tensile strength of the knitted or woven fabric in the warp direction was measured by applying load to the multilayer non-woven fabric in accordance with the cut split method of JIS-1096. The maximum load was 4.6tf/m, and the elongation distortion under the maximum load was 5.0%.

Claims: A multilayer, water permeable non-woven fabric comprising knitted or woven fabric and non-woven fabric layers multilaid together, said knitted or woven fabric layer(s) consisting of synthetic resin multifilaments oriented in at least one direction and having a tensile elastic modulus of at least 20GPa and a tensile strength of at least 1.2GPa and said non-woven fabric layer(s)consisting of synthetic resin fibers arranged at random. A fabric according to claim 1 wherein the multifilaments of said knitted or woven fabric layer(s) have a tensile elastic modulus of at least 50GPa and a tensile strength of at least 1.5 GPa. A fabric according to claim 1 or 2 wherein the multifilaments of said knitted or woven fabric layer(s) are of ultra-high molecular weight polyethylene. A fabric according to claim 1, 2 or 3 wherein the multifilaments of said knitted or woven fabric layer(s) are of 500 to 2000 denier (55.6 to 222 tex). A fabric according to any one of the preceding claims wherein each knitted or woven fabric layer has a mass/area ratio of 100 to 500 g/m².

Inventors: KATOH, TAKASHI MITSUI PETROCHEMICAL IND. LTD., MIYAZAKI, YOSHITOMO MITSUI PETROCHEMICAL IND. LTD., NISHIMURA, JUN MITSUI PETROCHEMICAL IND. LTD.
Applicants: MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1989
Main classification: D04H13
IPC codes: E02D3, D04H13, E02B11