Sealer material and method for applying the same

Abstract: Disclosed is a sealer material, comprising an ionizing radiation curable resin composition layer which is not flowable at a normal temperature and a sealer composition layer and optionally a substrate. Disclosed is also a method for applying the sealer material having the construction as mentioned above. By using the sealer material of this invention, easy and sure sealing can be made to the portion, to which sealing can not be made easily according to conventional methods.

Description: BACKGROUND OF THE INVENTION This invention relates to a sealer material which can be applied easily and surely even at sites where application is difficult, and a method for applying the same. Sealer materials or sealing member materials have been heretofore used in large amounts for sealing of seams of metal plates such as iron plates forming vehicle bodies of automobiles, a street car, etc., the space or gap between iron plates at the seaming portion, corner portion, the space between construction materials such as wood material, plastic material, etc. in buildings and various kinds of gaps. Generally speaking, for application of sealer materials as described above, necessary sealing is performed by use of a sealer gun, by pushing the sealer gun against the application site for sealing and moving the sealer gun while discharging a sealer material. However, since the gun is moved while being pushed against the application site, for example, the vehicle body of an automobile, application according to this method can be effected very efficiently and effectively only at the site where application operation with a gun can be easily done as in the case of the side face of the vehicle body, but it is not suitable for application at a site where gun operation is difficult such as at the backside face of the floor or a corner portion, etc. Also, application of a sealer material with a gun is almost impossible at a portion having a sharp angle, a place with narrow width or a portion with unevenness such as the cut section of iron plate or rod steel. For this reason, sealing at such portions has been effected by coating an appropriate coating material considerably thick, but satisfactory sealing can be obtained with difficulty only due to poor coatability of the coating material, particularly receiving influence from moisture in the case of iron materials, whereby rust is liable to be generated from this portion to pose a great problem. US-A-3 424 638 describes the bonding of different materials to each other by means of a liquid layer of acrylic acid which is irradiated to form the bond. Specifically, well known films of polyethylene or other polymers may be bonded by this known method to divers other materials. However, sealer materials are not nentioned in this document. Summary of the invention It is an object of this invention to provide a sealer material which can be easily and surely applied at a portion where sealing can be effected which difficulty only whith the sealer or by the application method of the prior art as described above, and to provide a method for applying the sealer material. This object of the invention is accomplished by a laminated sealer material comprising an UV-ray transmissive substrate on which an ionizing radiation curable resin composition is provided wherein the ionizing radiation curable resin composition having a viscosity of at least 10⁴ cps at 0 to 60°C comprises at least one compound selected from the group consisting of polyesteracrylate, epoxyacrylate, polyurethane acrylate, polyether acrylate, oligo acrylate, alkyd acrylate, polyol acrylate, and that a sealer composition layer is provided thereon. Advantageous embodiments of the invention are defined in the subclaims 2 to 11 while the inventive method is defined in claim 12 and the subclaims related thereto. The gist of the invention is indeed using a combination of known sealer material as a layer, provided with a layer of an ionizing radiation curable resin composition which is cured before or after application of the laminated sealer material to the desired site of application, and the laminated sealer material can preferably comprise a UV-ray transmissive substrate as a layer on the other side of the layer of ionizing radiation curable resin composition. The usability of the sealer material is thereby greatly improved, as explained in the following description. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows a perspective view of an embodiment of this invention; Fig. 2 a sectional view of the embodiment of Fig. 1; Fig. 3 a perspective view of a sealer molded product; Fig. 4 a sectional view showing a modification example; Fig. 5 a sectional view of another sealer molded product; and Fig. 6 a diagram for illustrating the applying method of this invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS The specific feature in constitution of the sealer material of this invention resides in use of a specific ionizing radiation curable resin composition layer as a part or all of a curable resin composition layer laminated with the sealer composition layer. In this meaning, the ionizing radiation curable resin composition can be cured partially by, for example, placing a nega-film having an image on the sealer material during irradiation to make the curable resin to be partially cured and the like. As the ionizing radiation curable resin composition, a UV-ray curable resin composition for which no installation cost is required can be used. In the following, description is made by referring to the case in which the UV-ray curable resin composition is used. The sealer composition may be either thermosetting or non-thermosetting. An embodiment of the sealer material of this invention is obtained by adhering on a UV-ray transmissive substrate of plastic films such as polyethylene terephthalate (PET), polypropylene (PP) and polyvinylalcohol (PVA) and other materials, a UV-ray curable resin composition layer which is not flowable at a normal temperature (about 0 to 60 °C), and providing a sealer composition layer thereon to form into a sheet or tape shape. The sealer material of this invention, other than the above embodiment, may be formed by laminating suitable number of three or more layers which are alternately laminated UV-ray curable resin composition layers and sealer composition layers. In this description, "not flowable at a normal temperature" means that no flowability is revealed at normal temperature and that the material has a viscosity of 10⁴ cps or more at 60 °C, preferably 10⁵ to 10⁶ cps at 60 °C. The above UV-ray curable resin composition layers are not flowable at normal temperature and have physical properties so that a sealer composition layer can be provided thereon. Specifically, for example, the UV-ray curable resin composition may include combinations of various polymers with acrylic oligomers or monomers, or epoxy type UV-ray curable resin. Further, thickeners and extender pigments may be added thereto, and materials which are not flowable, but flexible and plasticizable under normal conditions, for example, clay-like material, etc. may be used. Preferred UV-ray curable resin include resin compounds of each of methacrylic series, acrylic series, cinnamoyl series, vinyl series, phenylmaleimide series. Preferred are acrylic series resin compounds such as polyesteracrylate, epoxyacrylate, polyurethane acrylate, polyether acrylate, oligo acrylate, alkyd acrylate, polyol acrylate. Among them, most preferred is polyurethane acrylate. For the sealer composition layer, resins, fillers and other additives are not limitative so far as, in the case of either non-curable or curable, the layer has a sufficient form retention and adhesiveness to the portion to be sealed to form laminated construction having desired film thickness on the UV-ray curable resin composition layer. Further, in the case of a thermosetting sealer composition, it is required to exhibit no significant reduction in viscosity, to cause no sagging and flowing out of the sealer material applied when thermosetting is done. The sealer composition should preferably have a sufficient ionizing radiation transmission so that the UV-ray curable resin composition layer laminated therewith can be uniformly cured in a short time when irradiated with ionizing radiation. The sealer composition of this invention may generally include known sealer materials which may be curable or non-curable, having been produced by adding plasticizers, fillers, stabilizers, curing agent, etc. to at least one elastomer selected from synthetic resins such as vinyl chloride resins, ethylene - vinyl acetate copolymers, epoxy resins, alkyd resins, acrylic resins and urethane resins, synthetic rubbers such as chloroprene rubber, butyl rubber, styrene butadiene rubber and isobutene rubber, bituminous substances, natural rubbers and the like. Moreover, the sealer composition may include a reactive adhesive composition which was described separately by the present inventors in Japanese Patent Application No. 266899/1987, with various fillers and other additives in combination. The reactive adhesive composition described therein is one obtained by combining at least one of acrylic type adhesives such as saturated polyester resin, acrylic rubber, polybutadiene, acrylic type copolymer and acrylate type polymer which are in a solid state at a normal temperature; at least one of (meth)acrylic urethane monomer, oligomer and other low molecular weight substance such as (meth)acrylic oligomer which have a viscosity of 10² cps or more at normal temperature; and light-curable or thermosetting catalyst. Preferred sealer composition is a composition comprising 20 to 80 parts by weight of a thermoplastic resin such as a saturated polyester, acrylic rubber, polybutadiene and acrylic- polymer and copolymer, and 80 to 20 parts by weight of a thermosetting or photocurable resin such as a resinous acrylic urethane monomer or oligomer. Particularly preferred ratio of thermoplastic resin/thermosetting or photocurable resin is 40/60 to 60/40 in terms of parts by weight. As described above, the sealer material of this invention can be formed into a multi-layer structure, and, for example, when a UV-ray curable resin composition layer is sandwiched between the sealer composition layers to form thick three-layers structure, it can be formed in desired shape and used as an adhesive which also functions as the sealer. Although a thin sealer material can be obtained by spreading thinly a sealer composition layer containing a thermosetting resin, etc. as also described in the present specification, it has been impossible to impart a shape thereto. Since, however, a thick and non-flowable sealer material of this invention can be formed in a desired shape and to be a heat-reactive adhesive sheet, adhesion and sealing of molded products can be easily done and thus the work efficiency can be greatly improved. Particularly, it was found that such sealer material is I extremely effective for sealing or adhesion between faces having complicated unevenness. There are various methods for using and applying the sealer material formed as described above, but they can be classified into, for example, two kinds of methods as described below. The first method comprises first forming a sealer material by laminating ionizing radiation curable resin composition layer(s) and thermosetting or non-curable sealer composition layer(s), applying the sealer material formed in, for example, a tape as such by plastering it onto an application portion, adjusting the shape corresponding to the application portion and then irradiating it with UV-ray to cure the UV-ray curable resin layer and fix the shape of the sealer material, and further, in the case of a thermosetting sealer composition layer, heating the sealer material to cure the sealer composition layer to effect sealing on the application portion. The advantage of this method is that, since the outside faces are fixed by UV-ray irradiation after adjusting the shape by application onto a portion having a complicated shape or sharp angle, there occurs no disfiguring of the sealer in the subsequent curing process by heating in instances where the sealer composition is curable. This method is particularly effective for application at the edge portion of a steel plate. After a sealer material shaped in a tape is pushed against the edge portion to have the zones of its both end portions stuck on both side surfaces of the edge portions, the shape can be fixed by irradiation with UV-ray. Then, heating is effected and the thermosetting sealer composition layer even if flowability may be increased by heating, will flow with difficulty and not be disfigured in shape, because the UV-ray curable resin composition layer provided on an outer side surface of the sealer composition layer is fixed. When the sealer composition layer of tape- or sheet-like sealer material is non-curable, there is also the advantage that the tack on the surface of the sealer composition layer can be removed by UV-ray irradiation. In the conventional system in which the sealer material is extruded through a sealer gun, it was impossible to apply desired sealing at the edge portion of steel plate and its both side surface portions as described above. The second method comprises first reforming or molding the sealer material, formed in shape of a tape, into a predetermined shape by such means as press molding, etc., and irradiating it to cure the UV-ray curable resin composition layer and thus impart a desired shape thereto under such state. This method is suitable for, for example, the case of applying the sealer onto a surface having much unevenness. Although the application onto the portion having much unevenness may be possible according to the first method, enormous labors are required in the case of applying on a large number of the same shape. Application becomes extremely efficient if first a shape is imparted to the tape-shaped sealer material corresponding to the shape of the material to be applied. According to the methods as mentioned above, it has become possible to apply sealer to sites where it could not be applied by the conventional application method with use of a sealer gun, and also application is rendered possible easily for a material with complicated shape. The present invention is further described below by referring to the following examples, wherein "parts" means "parts by weight". Example 1 A sealer material as shown in Fig. 1 was prepared in the following manner. On a polyethylene terephthalate (PET) film (substrate) 1 with a thickness of 25 µm, a UV-ray curable resin composition layer 2 with the following formulation was provided to have a thickness of 20 µm. UV-ray curable resin composition Acrylic rubber, PS-250 (Toa Paint K.K.) 20 parts Urethane acrylate, Biscoat 812 (Osaka Yuki Kagaku Kogyo K.K.) 80 parts Darocure 1173 (Merck Co.) 3 parts The composition obtained by mixing the above starting materials had no flowability at normal temperature, and also the surface had substantially no tack. Next, on the UV-ray curable resin composition layer 2, a sealer composition layer 3 with the following formulation was provided. Saturated polyester, LP-022 (Nippon Gosei Kagaku K.K.) 70 parts Urethane acrylate, Biscoat 812 (Osaka Yuki Kagaku Kogyo K.K.) 30 parts Perbutyl IF (Nihon Yushi K.K.) 1 part The sealer composition layer starting materials of the above formulation were homogeneously mixed as a whole at 60 °C, and spread as such on the UV-ray curable resin composition layer to have a thickness of 700 µm and cooled to obtain a sealer material 4 consisting of three layers including the substrate as shown in Fig. 1. The surface of the sealer composition layer was tacky, and, when it was lightly plastered on an iron plate and the like, it could be also peeled off and plastered again. The sealer material obtained as described above was pushed against the whole edge portions of a cold rolled steel plate with a thickness of 0.3 mm, a length of 15 cm and a width of 7 cm so that said edge portion is placed at the center, and plastered on the side surfaces of the plate by folding the both ends of the sealer material. Then it was UV-ray irradiated by a 1 kW high pressure mercury lamp (80 W/cm) at a distance of 10 to 15 cm for about 2 seconds. The PET film used as the substrate was readily peeled off. Also, the surface of the sealer material applied had no tack at all. Then, a sheet of steel plate provided with the sealer material at the edge portions was prepared in the same manner. These plates were heated at 140 °C for 30 minutes while one of them was placed vertically and another one horizontally, to obtain test pieces of which the sealer material as a whole was cured. In the sealer materials applied on the test pieces obtained, there was neither sagging nor peel off at all at the horizontal portion, the vertical portion and the ceiling portion, and also non of the bubbles involved during plastering of the sealer materiel penetrated through the sealer layer. Then, a coating material was coated and baked, but there was no pinhole at all. Comparative example 1 On a PET film with a thickness of 25 µm, the sealer composition layer used in Example 1 was spread to have a thickness of 700 µm and cooled without provision of a UV-ray curable resin composition layer to obtain a sealer material. The sealer material obtained was used similarly as in Example 1 to prepare two sheets of iron plate, and these sheets were heated at 140 °C for 30 minutes, while one of them was placed horizontally and the other vertically to obtain test pieces with cured sealer composition layer. In the test piece heated with the steel plate placed vertically, sagging was observed at the portions of the four corners of the steel plate where the sealer layers were overlapped. Also, at the portion where the sealer layer consists of one layer, the bubbles involved during plastering were found to be punctured to penetrate through the sealer layer elsewhere. In the test piece heated with the steel plate placed horizontally, there were some places where the portion applied at the lower side of the steel plate was peeled and sagged. Then, a coating material was coated and baked similarly as in Example 1, but the bubbles involved were broken and the portion formed by penetration of bubbles through the sealer composition layer remained as pinhole. Example 2 A molded sealer material as shown in Fig. 3 was prepared in the following manner. The sealer material 4 consisting of three layers obtained in Example 1 was cut into a width of 20 mm and a length of 20 cm, and the PET film 1 was peeled off and the remaining layer consisting of layers 2 and 3 was applied onto a molding machine (UV-ray transmissive), of which the working surface was treated with Teflon so that the molded product can easily be removed, to be molded into a U-shape having an opening of 0.8 mm at a temperature of 60 °C, and after UV-ray irradiation by a 1 kW high pressure mercury lamp (80 W/cm) at a distance of 10 to 15 cm for about 2 seconds, the U-shaped sealer molded product was taken out from the mold. The molded product is shown in Fig. 3. The inner side surface 8b was the sealer composition layer and the outer side surface 8a was UV-ray curable resin composition layer. The sealer molded product 4a had no tack on the outer side surface 8a, but had a tack on the inner side surface 8b of the opening 5. When the sealer molded product was applied on the edge portion (cut section) of a cold rolled steel plate with a thickness of 0.8 mm, application could be smoothly done because of no presence of tack at all on the outer side surface of said molded product. The material was subjected to curing by heating at a temperature of 150 °C for 20 minutes, whereby there was no sagging at all. Also, none of the bubbles involved during plastering penetrated through the layer. Subsequently, a coating material was coated and baked, but there was no pinhole, at all. Next, molded sealer materials having the similar shapes were prepared by, for example, replacing the inner side material and outer side material; using a sealer material comprising alternately sandwiched layers and the like. There were revealed the similar good results at the application sites such as inner side of a gap, slot and the like. Example 3 A sealer material 4 as shown in Fig. 4 was firstly prepared as follows. On a substrate of a biaxially stretched polypropylene film 1 with a thickness of 30 µm, a thermosetting sealer composition layer 3, a UV-ray curable resin composition layer 2, a thermosetting sealer composition layer 3 with the following formulations were laminated in this order to obtain a sealer material 4. Thermosetting sealer composition Polyacrylate resin 100 parts Epoxy resin, Alardite Y-261 (Ciba Geigy Co.) 80 parts Dicyandiamide (Carbide K.K.) 5 parts Aerosil No. 300 (Nippon Aerosil K.K.) 10 parts Photo (UV-ray) curable resin composition Acrylic urethane resin, Thiocol 60 parts Saturated polyester resin, Bylon 200 (Toyo Boseki K.K.) 40 parts Darocure 1173 (Merck Co.) 3 parts The thickness of the thermosetting sealer composition layer was controlled to be 500 µm and the UV-ray curable resin composition layer 100 µm. The sheet-shaped sealer material thus obtained was further covered with a non-stretched polyethylene film with a thickness of 75 µm The sealer material obtained as described above was shaped by applying a pressing machine having a concave mold portion of 10 mm x 10 mm with a depth of 3 mm and a convex mold portion of 8 mm x 8 mm with a height of 2 mm to be pressed at 60 °C. Subsequently, after one of the concave or convex mold of the pressing machine was removed, it was UV-ray irradiated by 1 kW high pressure mercury lamp (80 W/cm) for about 2 seconds to obtain a sealer material 4a as shown in Fig. 5 provided with a desired shape. After removal of the polyethylene cover film having a convex surface, the sealer material 4a was inserted between the steel plates 6 and 7 as shown in Fig. 6, which were shaped into the same shape by means of the concave mold and the convex mold of the pressing machine, by fitting application of the sealer material into the iron plate 6 formed in concave shape, placing the other iron plate 7 formed in convex shape thereon and applying a pressure to plaster the iron plates shaped in concave mold shape and convex mold shape. Application could be done easily because the shapes were the same. The application is briefly illustrated in Fig. 6. Then, heating was effected at 140 °C for 30 minutes, whereby the two sheets of the iron plates were found to be firmly bonded. Example 4 On a PP (polypropylene) film 1 with a thickness of 30 µm, a UV-ray curable resin composition layer 2 with the following formulation was provided to have a thickness of 30 µm. UV-ray curable resin composition Ethylene - vinyl acetate copolymer, Evaflex EV-150 (Mitsui Polychemical) 30 parts Urethane acrylate, UV-4200B (Nippon Gosei) 70 parts Irugacure 651 (Ciba Geigy Co.) 3 parts The UV-ray curable resin composition layer formed had no flowability at normal temperature, and also the surface had substantially no tack. Next, on the UV-ray curable resin composition layer, a sealer composition layer with the following formulation was spread to have a thickness of 300 µm, and the surface was covered with a non-stretched polyethylene film having a thickness of 40 µm. Sealer composition (non-curable) Butyl rubber (Nihon Butyl, Butyl LM) 100 parts Fine silicate powder (Nippon Aerosil K.K., Aerosil #300) 40 parts Carbon black (Asahi Carbon, Asahi #60FEF) 100 parts Polybutene resin (Nihon Sekiyu Kagaku, Nisseki Polybutene HV-1900) 180 parts Next, the polyethylene film side was fitted and pushed to a molding face having a corner of 90°, followed by UV-ray irradiation from the PP film side to obtain a sealer material with a folding degree of 90°. The cover film of polyethylene was peeled off and the sealer material was applied onto a portion of a steel plate folded in right angle. The sealer material was kept stably by the sealer composition layer having adhesiveness, resulting in easy application. Example 5 On a polyvinyl alcohol (PVA) film with a thickness of 40 µm, a UV-ray curable resin composition layer with the following formulation was provided to have a thickness of 50 µm UV-ray curable resin composition Urethane acrylate, UV-3000B (Nippon Gosei) 60 parts Aerosil R-972 (Nippon Aerosil K.K.) 40 parts Darocure 1173 (Merck Co.) 3 parts The composition obtained by mixing the above starting materials had no flowability at normal temperature, and also the surface had substantially no tack. Sealer composition (non-curable) Vinyl chloride resin (Nihon Zeon, Zeon 121) 16 parts Styrene butadiene rubber (Nihon Synthetic Rubber, JSR 1500) 5 parts Calcium carbonate (Maruo Calcium, MSK-C) 48 parts Synthetic resin (acrylic resin; Mitsubishi Rayon, Acrypet VH) 2 parts Phthalic acid ester (Kao, DOP) 27 parts Aging inhibitor (Kawaguchi Kagaku Kogyo, Antage W-500) 2 parts The sealer composition layer with the above formulation was spread on the above UV-ray curable resin composition layer to have a thickness of 1 mm to obtain a sealer sheet. The thus obtained sealer sheet was cut into a width of 20 mm and applied onto an edge portion of a glass plate with a thickness of 30 mm by fitting the sealer composition layer side to the glass to be molded into a U-shape. After UV-ray irradiation by a 1 kW high pressure mercury lamp of 1 kW for about 1 second, the PVA film was peeled off to obtain a glass plate of which the edge portion was sealed by a sealer material having a sealer composition layer coated with a UV-ray cured resin layer. The sealer material was kept stably on an edge portion of the glass plate by the adhesiveness of the sealer composition. The surface of the sealer material had no tack and was easy in handling. Example 6 On a PET film with a thickness of 25 µm, a UV-ray curable resin composition layer with the following formulation was provided to have a thickness of 50 µm. The resin composition obtained by mixing them had no flowability at normal temperature and also the surface had substantially no tack. UV-ray curable resin composition Saturated polyester resin, Polyester LP-044 (Nippon Gosei) 60 parts Urethane acrylate, C-9054 (Sartomer) 40 parts Irgacure 651 3 parts Next, on the above UV-ray curable resin composition layer, a thermosetting sealer composition layer with the following formulation was spread to have a thickness of 500 µm to obtain a sealer sheet. The thus obtained sealer sheet had a sufficient adhesiveness to keep itself on the portion to be applied. Sealer composition (thermosetting) Saturated polyester resin, Bylon 200 40 parts Acrylic urethane resin, thiocol 60 parts Perbutyl IF 5 parts The sealer sheet obtained was cut into a width of 15 mm and a length of 15 cm, and this was fitted to a fore-end portion of a cool-rolled steel plate with a thickness of 0.3 mm, a length of 15 cm and a width of 7 cm so that the edge portion is placed on the center of the sheet. The both ends of the sheet were folded to the side faces of the steel plate and adhered thereon. Then, UV-ray irradiation was made by use of a 1 kW high pressure mercury lamp for about 2 seconds and the PET film was peeled off easily. The surface of the sealer material had no tack. Next, the sealer sheet was heated at 140 °C for 30 minutes, resulting in good sealing of the edge portion of the steel plate without flowing and sagging. Example 7 On a conveyor belt of which the surface was coated with PTFE (Teflon) sheet, the following sealer composition was coated to have a thickness of 500 µm and further the following UV-ray curable resin composition was coated to have a thickness of 5 µm, followed by UV-ray irradiation by use of a high pressure mercury lamp (80 W/cm, 1 kW) at a distance of 10 cm for about 2 seconds. The surface thus obtained had no tack. Sealer composition Saturated polyester, Polyster LP-202 (Nippon Gosei Kagaku Kogyo K.K.) 70 parts Urethane acrylate, Biscoat 812 (Osaka Yuki-Kagaku Kogyo K.K.) 30 parts Perbutyl IF (Nihon Yushi K.K.) 1 part UV-ray curable resin composition Aronix M-5700 (Toa Gosei Kagaku Kogyo K.K.) 50 parts Aronix M-1100 (Toa Gosei Kagaku Kogyo K.K.) 50 parts saturated polyester Bylon 200 100 parts Darocure 1173 (Merck Co.) 3 parts The thus obtained sheet was rolled around a core rod with a diameter of 10 cm to obtain a sealer material having no substrate. Since the UV-ray curable resin composition layer was thin and had an expansibility, the sheet could be wholly expanded by pulling strongly and applied easily to complicated figures such as concave-convex faces. Also, since one side of the sheet was not tacky, it could efficiently be handled in application by pressing the side which was not tacky. Example 8 By using a polypropylene film with a thickness of 30 µm as a substrate, a tape-shaped sealer material with a substrate was obtained by repeating the same procedure as in Example 4. The sealer material after peeling of the substrate could be applied efficiently as in Example 4.

Claims: A laminated sealer material comprising a UV-ray transmissive substrate on which an ionizing radiation curable resin composition is provided, characterized in that the ionizing radiation curable resin composition having a viscosity of at least 10⁴ cps at 0 to 60 °C comprises at least one compound selected from the group consisting of polyesteracrylate, epoxyacrylate, polyurethane acrylate, polyether acrylate, oligo acrylate, alkyd acrylate and polyol acrylate, and that a sealer composition layer is provided thereon. A sealer material according to claim 1, wherein the substrate is at least one of the group consisting of polyethylene terephthalate, polypropylene and polyvinylalcohol. A sealer material according to claim 1 or 2, wherein the ionizing radiation curable resin composition layer and the sealer composition layer are laminated alternately. A sealer material according to any of claims 1 to 3, wherein the ionizing radiation curable resin composition has a viscosity of 10⁵ to 10⁶ cps at 60 °C. A sealer material according to any of claims 1 to 4, wherein the ionizing radiation curable resin composition is at least one selected from the group consisting of a combination of polymers with acrylic oligomers or monomers, and epoxy type UV-ray curable resin. A sealer material according to any of claims 1 to 4, wherein the ionizing radiation curable resin composition is composed of an oligomer having a (meth)acryloyl group and the sealer layer is a non-curable or a heat curable sealer layer. A sealer material according to any of claims 1 to 6, wherein the ionizing radiation curable resin composition comprises at least one from the group consisting of methacrylic, acrylic, cinnamoyl, vinyl and phenylmaleimide resin compounds. A sealer material according to any of claims 1 to 7, wherein the sealer composition is at least one combination of the group selected from the group consisting of vinyl chloride resins, ethylene - vinyl acetate copolymers, epoxy resins, alkyd resins, acrylic resins, urethane resins, chloroprene rubber, butyl rubber, styrene butadiene rubber, isobutene rubber, bituminous substances, natural rubbers, and a composition obtained by combining at least one of acrylic type adhesives which are in a solid state at a normal temperature of 0 - 60 °C, at least one of (meth)acrylic urethane monomer and oligomer which have a viscosity of 10² cps or more at normal temperature and a light-curable or thermosetting catalyst. A sealer material according to claim 8, wherein the sealer composition comprises 20 to 80 parts by weight, preferably 40 to 60 parts by weight, of a thermoplastic resin and 80 to 20 parts by weight, preferably 60 to 40 parts by weight, of a thermosetting or photocurable resin. A sealer material according to claim 9, wherein the thermoplastic resin is at least one selected from the group consisting of a saturated polyester, acrylic rubber, polybutadiene and acrylic-polymer and copolymer; and the thermosetting or photocurable resin is at least one selected from the group consisting of a resinous acrylic urethane monomer or oligomer. A laminated sealer material according to any of claims 1 to 10, characterized in that one layer of said ionizing radiation curable resin composition is cured and, as an outer layer constitutes said substrate. A method for applying a laminated sealer material according to any of claims 1 to 11 which comprises: pushing the sealer material against a portion to be applied to adhere and fix the sealer material thereon; irradiating an ionizing radiation to fix the shape of the ionizing radiation curable resin composition layer; and heating the sealer material to melt and cure the sealer composition layer. A method for applying a sealer material according to any of claims 1 to 11 which comprises: molding said sealer material into a shape corresponding to a portion to be applied; irradiating an ionizing radiation to fix the shape of the ionizing radiation curable resin composition layer; and heating the sealer material to melt and cure the sealer composition layer. A method according to claim 12, wherein the sealer material comprises a UV-ray transmissive substrate to which at least one of the ionizing radiation curable resin composition layer and the sealer composition layer is provided.

Inventors: KISHIMOTO YOSHIO, ONO KIYOSHI, SATOU TETSUHITO, KISHIMOTO, YOSHIO, ONO, KIYOSHI, SATOU, TETSUHITO
Applicants: NICHIBAN KK, NICHIBAN CO. LTD.
Application year: 1989
Main classification: C09K3
IPC codes: C09K3, B32B7, B32B37, B32B27