IMPROVED NYLON COMPOSITIONS FOR BLOWMOLDING

Abstract: It has now been found that a unique combination of additives makes semi-crystalline polyamides readily processible by extrusion blowmolding to make hollow, stiff parts of various shapes. The compositions consist essentially of semicrystalline polyamide, a selected toughening agent and an anhydride-rich ethylene copolymer, and a fibrillar polytetrafluoroethylene.

Description: TITLE IMPROVED NYLON COMPOSITIONS FOR BLOWMOLDING BACKGROUND OF THE INVENTION Polyamides that are semicrystalline are used extensively in many applications that require good solvent resistance and good properties at elevated temperatures. They are ordinarily processed by injection molding, but there are many components of automobiles and other systems wherein such parts are hollow and to manufacture these by injection molding is very difficult and expensive. Many such parts can conceivably be made by blowmolding provided the polymer system has adequate melt strength and viscosity. Unfortunately, polyamides commonly used for injection molding have number average molecular weights generally between 10000 and 25000 which is too low to make them suitable for extrusion blowmolding. It would be desirable to have a blow moldable polyamide composition made from the usual injection moldable polyamides. For many applications polyamide compositions with improved toughness are required. The prior art describes various techniques of modifying polyamides with tougheners. Such tougheners include low modulus ethylene copolymers containing small amounts of carboxyl or anhydride functionality. Other tougheners include ethylene acid copolymers neutralized with metal cations (see Epstein U. S. Patent 4,174,358 or Murch U. S. Patent 3,845,163. Combinations of polyamides with such tougheners afford unique combinations that are tough and suitable for injection molding and extrusions. These combinations, however, possess lower than optimum viscosities and melt strength for use in blowmolding. SUMMARY OF THE INVENTION Recently, in a companion patent application, the melt viscosities of such combinations of polyamides and the aforementioned toughening polymers are increased substantially by addition of small amounts of an anhydride rich polymer which acts as a coupling or crosslinking agent to react preferentially with the polyamide to increase molecular weight. At the same time such anhydride-rich polymers react with the acid groups in the toughening polymer as well, increasing its viscosity. Thus, addition of the anhydride-rich polymer makes the semicrystalline polyamide readily processible by extrusion blowmolding to make hollow, stiff parts of various shapes. It has now been found that if a fibrillar fluoropolymer resin is added the amount of the anhydride-rich copolymer or the toughening polymer can be reduced. The compositions consist essentially of: a) 99-65 parts by weight semicrystalline polyamide having a number average molecular weight between 10000 and 25000; b) 1-30 parts by weight of either: 1) an ionic copolymer of at least one °—olefin and at least one a , β-unsaturated organic carboxylic acid which is partially or completely neutralized with a metal cation or, 2) a mixture of a polyethylene and a functionalized polyethylene that contains up to 10% by weight carboxylic acid or anhydride functional moieties; and c) 0.1 to 3 parts by weight of an anhydride-rich copolymer containing alternating units of maleic anhydride and an α-olefin, such as styrene, ethylene, or octadecene, which copolymer contains at least 15% by weight anhydride units; d) 0.1 to 3 parts by weight of fibrillar fluoropolymer resin. Of course, the amounts of each additive present are relative. For example, as the amount of component b) is decreased, the amount of component c) should be increased, and as more component b) is employed, the amount of c) can be decreased. The same principle is true for component d) . These compositions have high melt strength compared to the base polyamide. This property aids in making the compositions blow- oldable. The compositions are readily processible by extrusion blowmolding to make hollow parts, such as containers or automotive components for under-the-hood applications. DETAILED DESCRIPTION OF THE INVENTION The polyamide matrix resin of the compositions of this invention is well known in the art and embraces those semi-crystalline resins having a molecular weight of between about 10000 and 25000 and commonly referred to as nylons. Suitable polyamides include those described in U.S. Pat. Nos. 2,071,250; 2,071,251, 2,130,523; 2,130,948; 2,241,322, 2,312,966; 2,512,606; and 3,393,210. The polyamide resin can be produced by condensation of equimolar amounts of a saturated dicarboxylic acid containing from 4 to 12 carbon atoms with a diamine, in which the diamine contains from 4 to 14 carbon atoms. Excess diamine can be employed to provide an excess of amine end groups over carboxyl end groups in the polyamide. Examples of polyamides include polyhexamethylene adipamide (66 nylon) , polyhexamethylene azelaamide (69 nylon) , polyhexamethylene sebaca ide (610 nylon) , and polyhexamethylene dodecanoamide (612 nylon) , the polyamide produced by ring opening of lacta s; i.e., polycaprolactam, polylauric lactam, poly-11-aminoundecanoic acid, bis(paraaminocyclohexyl) methane dodecanoamide. It is also possible to use in this invention polyamides prepared by the copolymerization of two of the above polymers or terpolymerization of the above polymers or their components; e.g., an adipic, iεophthalic acid 0 hexamethylene diamine copolymer. Preferable the polyamides are linear with a melting point in excess of 200 β C. As great as 99 percent by weight of the composition can be composed of polyamide; however, preferred compositions contain from 60 to 99 percent, 5 and more narrowly 80 to 95 percent, by weight of polyamide. By "semicrystalline is meant that the polyamide has a distinct melting point with a measurable heat of fusion, as described in U. S. Patent 4,410,661 in Columns 1 and 2. Q The ionic copolymer is made of recurring units of at least one alpha-olefin and at least one alpha,beta-unsaturated carboxylic acid, in which the acid moiety is at least partially ionized with metal ions. The alpha-olefin is preferably of 2-6 carbon 5 atoms and the acid is preferably of 3-6 carbon atoms. Preferably the alpha-olefin is ethylene and the acid isacrylic or methacrylic acid. Other polymerizable comono ers can be present, such as acrylates or ethacrylates. The metal ion can be monovalent, 0 divalent or trivalent, as for example Na, Zn, Al, K and the like. Representative copolymers include ethylene/isobutylacrylate/methacrylic acid (80/10/10) 70% zinc neutralized. When unmodified polyethylene is used, an 5 anhydride modified polyethylene (modified witlj 1% aleic anhydride) is used as a compatibilizer. The polyethylene used can be high or low density. The functionalized polyethylene can be a polyethylene that contains up to 10% carboxylic acid or anhydride functionality. These are described in Epstein U. S. Patent 4,174,358. The ratio of polyethylene to functionalized polyethylene is preferably 1:1 to 2:1 by weight. Small amounts of an anhydride-rich polymer comprise the third additive component. This component can be an alternating polymer of εtyrene and maleic anhydride (e.g., SMA 3000 sold by ARCO Chemical, an alternating polymer of ethylene and maleic anhydride (e.g., ethylene-maleic anhydride polymer EMA-31 manufactured by Monsanto Chemical Company) , or a higher α-olefin/maleic anhydride polymer (e.g., Octadecene-maleic anhydride polymer PA-18 made by Gulf Oil Company) . By alternating is meant that the units substantially alternate between comonomers. The fibrillar fluoropolymer resin is preferably a non-melt-fabricable tetrafluoroethylene polymer. The tetrafluoroethylene polymers are made by the dispersion polymerization process, in which the polymer particles formed remain dispersed in the reaction mix during the polymerization. The particles are coagulated and dried. The particles fibrillate while being physically mixed into the composition of the invention. The fibrillatable PTFE is a well known material in the art and readily available as a commercial product. The commercially available fibrillatable PTFE is in the form of an aqueous dispersion prepared by the emulsion polymerization or in the form of a powder obtained by separation of the resin from the aqueous dispersion followed by drying. SUBSTITUTE SHEET The aqueous dispersion of the fibrillatable PTFE contains usually several tens of %, say, up to 60% of the PTFE particles having a diameter of about 0.2 μ while the powdery products are agglomerates of these particles of about 0.5 mm average diameter. The PTFE particles of either form can be readily converted into fibrils when the particles are subjected to mechanical shearing forces. Several of the examples of the commercially available fibrillatable PTFE are as follows: Teflon 6 (a product by Mitsui Fluorochemical Co.), Teflon 6JC (a product by the same company) , Polyflon F-103 (a product of Daikin Kogyo Co.) and Polyflon F-201 (a product by the same company) as the examples of the powdery products and Teflon 30-J (a product by Mitsui Fluorochemical Co.) and Polyflons D-l and D-2 (products by Diakin Kogyo Co.) as the examples of the aqueous dispersion products. It has unexpectedly been discovered that if the amounts of additive ingredients are such that certain low shear/high shear viscosity ratios are obtained, good blowmolding resins are produced. For example, when the viscosity is measured at a shear rate of 3.5 per seconds and at a shear rate of 588 per second, it was found that if the ratio of low shear viscosity to high shear viscosity was greater than about 5 or 6 or so, the compositions could be extrusion blowmolded. The ingredients used to make the compositions of the invention may be combined by tumble blending the components and feeding the blend to the extruder of the blowmolding equipment. It is preferable, however, that the anhydride-rich copolymer be dispersed uniformly and it has been found that melt blending the ingredients, by using such equipment as a melt extruder (e.g., single screw extruders or twin screw extruders) is preferred. The blended product is pelletized (i.e., the extruded strand is cut), dried and used for subsequent blowmolding purposes using an extrusion blowmolding machine (e.g., made by Rocheleau Inc., Hayssen Inc., etc.) and fabricated into hollow articles such as containers. EXAMPLES The examples set forth below were carried out using as the polyamide a 66 polyamide "Zytel" (16,000 - 20,000 number average molecular weight) made from adipic acid and hexamethylene diamine. The ionomeric polyolefin additive was a 70% zinc neutralized ethylene-methacrylic acid (90/10) copolymer ("Surlyn" 9520) . Anhydride-Rich Copolymers used were: SMA-3000, Styrene-Maleic anhydride copolymer by ARCO Chemical PA-18, Octadecene-Maleic anhydride copolymers made by Gulf Oil Co. (Chemicals Div.) The fluoropolymer used was Teflon fluoropolymer 6C or 60 sold by the Du Pont Company. Number average molecular weight was determined by Waters 150C gel permeation chromatography equipment at 110 ' C with meta-cresol as a solvent. Melt viscosity was measured on a melt capillary rheometer made by Kayeness Test Instrument. Melt flow was measured using a melt index apparatus made by F. F. Sloan Corporation, Wilmington, Delaware. The materials were extrusion blended using a Sterling extruder equipped with a single screw or a Weraer & Pfleiderer twin screw extruder and the polymer strands cut into pellets, dried and used to SUBSTITUTE SHEF- 8 blow mold one-quart containers using a Rocheleau extrusion blowmolding machine. Blowmolding Procedure The appropriate mixture of materials were blended and melt extruded using an extruder equipped with a 2 inch screw and the polymer melt made into strands and cut into small pellets. The pellets then were fed into a blowmolding machine which was equipped with a 1-1/2 inch diameter screw and a mold to make a bottle with a volume of 1 quart. The extruder temperatures were kept at about 270*C The vertically extruded tube of the melt (parison) was qualitatively judged for its strength by stopping the extrusion and the molten parison allowed to stand and support its own weight, before pinching and blowing to make the container. If the parison does not have adequate strength, the parison breaks off easily and the melt falls down without being able to blow and make the container. If it has good strength, the molten tube (parison) supports itself without breaking and lends itself to blowing to make the container. Cpntrol Example 1 Using 90 parts of 66 polyamide and 10 parts ionomeric copolymer, the extruded melt did not have enough strength to support itself, broke off and fell down rapidly. No containers could be blowmolded. Control Example 2 Adding 0.5 parts anhydride-rich copolymer to the mixture of Control Example 1 did help, but not enough to make a satisfactory container. The composition of Control Example 2 (88.5 parts polyamide and 10 parts ionomeric copolymer and 0.5 anhydride-rich copolymer)was melt blended with 1 part of fluoropolymer Teflon 6C. On blowmolding as described above, good blowmolded containers were obtained. Table I shows the ingredients used and blowmoldability results for Control Examples 1 and 2 amd for Example 1. In a like manner, additional Examples and Controls were carried out using the ingredients shown in Table I with the blowmolding results shown in the Table. TABLE I EFFECT OF HIGH MOLECULAR WEIGHT "TEFLON" ON THE MELT VISCOSITIES @ 285°C AND BLOW MOLDABILITY OF POLYHEXAMETHYLENE ADIPAMIDE BLENDS ISC. RATIO @ 3/5 SEC 1 588 /SEC BLOWMOLDABILITY NO MELT 1.87 STRENGTH NOT ENOUGH 3.58 MELT STRENGTH GOOD, COULD BE 8.00 BLOWMOLDED 7.87 " 8.08 " NO MELT STRENGTH COULD NOT BE 1.28 BLOWMOLDED 13.41 BLOWSMOLDS READILY 13.78 BLOWMOLDS WELL 17.28 BLOWMOLDS WELL 18.23 BLOWMOLDS WELL 15.31 BLOWMOLDS WELL 14.27 BLOWMOLDS WELL

Claims: CLAIMS 1. A composition consisting essentially of: a) 99-65 parts semicrystalline polyamide having a number average molecular weight between 10000 and 25000; b) 1-30 parts by weight percent based on polyamide of either: 1) an ionic copolymer of at least one α-olefin and at least one α ,β-unsaturated organic carboxylic acid which is partially or completely neutralized with a metal cation or, 2) mixture of a polyethylene and a functionalized polyethylene that contains up to 10% by weight carboxylic acid or anhydride functional moieties; and c) 0.1 to 3 parts by weight of an anhydride-rich copolymer containing alternating units of maleic anhydride and an α-olefin, such as styrene, ethylene, or octadecene, which copolymer contains at least 15% by weight anhydride units. ) 0.1 to 3 parts by weight of fibrillar fluoropolymer resin. 2. The composition of Claim 1 wherein the polyamide is 66 nylon. 3. The composition of Claim 1 or 2 wherein component (b) is an ionic copolymer of at least one alpha-olefin and at least one alpha,beta-unsaturated organic carboxylic acid, in which the acid moiety is partially neutralized with a metal cation. BS TITUTESHEET

Inventors: SUBRAMANIAN PALLATHERI MANACKA, SUBRAMANIAN, PALLATHERI, MANACKAL
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1989
Main classification: C08L77
IPC codes: B29C49, B29K77, B29L22, C08L77