Synthetic resin compositions

Abstract: A synthetic resin composition comprising 100 parts by weight of a synthetic resin, from 2 to 900 parts by weight of an inorganic filler, and from 0.02 to 20 parts by weight of a copolymer of a compound represented by formula 91) and maleic anhydride, maleic acid, a maleic acid salt or a maleic acid ester; wherein Z is a residue of a compound having from 2 to 8 hydroxyl groups; AO is an oxyalkylene group having from 2 to 18 carbon atoms; R¹ is an unsaturated hydrocarbon group having from 2 to 5 carbon atoms; R² is a hydrocarbon or acyl group having from 1 to 40 carbon; a is from 0 to 1,000, b is from 0 to 1,000, c is from 0 to 1,000, ℓ is an integer of from 1 to 8, m is an integer of from 0 to 2, and n is an integer of from 0 to 7, ℓ + m + n = 2 to 8, aℓ + bm + cn = 1 to 1,000, and m/(ℓ + n) ≦ 1/3. In the synthetic resin composition the inorganic filler is uniformly dispersed in the synthetic resin with good efficiency at molding to give excellent molding character­ istics and mechanical characteristics.

Description: FIELD OF THE INVENTION This invention relates to a synthetic resin composition containing an inorganic filler and more particularly to a synthetic resin composition composed of a synthetic resin, an inorganic filler, and a specific copolymer, wherein the inorganic filler is uniformly dispersed in the synthetic resin with good efficiency at molding to give excellent molding characteristics and mechanical characteristics. BACKGROUND OF THE INVENTION It has been widely practiced to add an inorganic filler to a synthetic resin for the improvement of the mechanical characteristics of the synthetic resin moldings, the reduction of the raw material cost, etc. However, when a large amount of an inorganic filler is added to a synthetic resin, the inorganic filler is difficult to disperse thereby to greatly reduce the moldability and, sometimes, to extremely reduce the mechanical characteristics of the moldings obtained. This is considered to be caused by the poor affinity of the synthetic resin for the inorganic filler. Hitherto, for solving such a disadvantage, it has been attempted to improve the affinity of a synthetic resin for an inorganic filler using a coupling agent such as fatty acid, fatty acid salt, fatty acid ester, and titanate, as described in U.S. Patent 4,812,282. However, by conventional methods, the improved effect of the affinity of a synthetic resin for an inorganic filler is still insufficient, the addition amount of an inorganic filler is restricted, and the reduction of mechanical characteristics is unavoidable. SUMMARY OF THE INVENTION The object of this invention is to provide a synthetic resin composition having high industrial values, wherein the affinity of a synthetic resin for an inorganic filler is improved to increase the dispersibility of the inorganic filler, whereby the molding characteristics and the mechanical characteristics are improved even by compounding the inorganic filler with the synthetic resin. It has now been discovered that the aforesaid object can be attained by the present invention as set forth herein below. According to this invention, there is provided a synthetic resin composition comprising a single type of a synthetic resin in an amount of 100 parts by weight, from 2 to 900 parts by weight of an inorganic filler, and from 0.02 to 20 parts by weight of a copolymer of a compound represented by following formula (1) and maleic anhydride, maleic acid, a maleic acid salt, or a maleic acid ester; wherein Z is a residue of a compound having from 2 to 8 hydroxyl groups; AO is an oxyalkylene group having from 2 to 18 carbon atoms; R¹ is an unsaturated hydrocarbon group having from 2 to 5 carbon atoms; R² is a hydrocarbon or acyl group having from 1 to 40 carbon; a is from 0 to 1,000, b is from 0 to 1,000, c is from 0 to 1,000, ℓ is an integer of from 1 to 8, m is an integer of from 0 to 2, and n is an integer of from 0 to 7, ℓ + m + n = 2 to 8 , aℓ + bm + cn = 1 to 1,000 , and m/(ℓ + n) ≦ 1/3 . DETAILED DESCRIPTION OF THE INVENTION The compound shown by formula (1) is explained in detail below. In formula (I) described above, examples of the compound containing Z as a residue and having from 2 to 8 hydroxy groups, include polyhydric phenols such as catechol, resorcin, hydroquinone, and phloroglucin; polyhydric alcohols such as ethylene glycol, propylene glycol, butylene glycol, dodecylene glycol, octadecylene glycol, neopentyl glycol, styrene glycol, glycerol, diglycerol, polyglycerol, trimethylolethane, trimethylolpropane, 1,3,5-pentanetriol, erythritol, pentaerythritol, dipentaerythritol, sorbitol, sorbitan, sorbide, a sorbitol-glycerol condensate, adonitol, arabitol, xylitol, and mannitol; saccharides such as xylose, arabinose, ribose, rhamnose, glucose, fructose, galactose, mannose, sorbose cellobiose, glucose, maltose, isomaltose, trehalose, sucrose, raffinose, gentianose, and melezitose; and the partially etherified or partially esterified compounds thereof. As the oxyalkylene group having from 2 to 18 carbon atoms shown by AO in formula (I), there are an oxyethylene group, an oxypropylene group, an oxybutylene group, an oxytetramethylene group, an oxystyrene group, an oxydodecylene group, an oxytetradecylene group, an oxyhexadecylene group, and an oxyoctadecylene group; the oryalkylene group may be singly or an adduct of a mixture of two or more of these groups. With adducts of two more of these groups, they may be random or block adducts. As the unsaturated hydrocarbon group having from 2 to 5 carbon atoms shown by R¹, may be mentioned hydrocarbon groups having an unsaturated bond at the terminal, such as a vinyl group, an allyl group, a methallyl group, a 3-butenyl group, a 4-pentenyl group, and a 3-methyl 3-butenyl group. As the hydrocarbon group having from 1 to 40 carbon atoms represented by R², there are a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a tert-butyl group, an amyl group, an isoamyl group, a hexyl group, a heptyl group, a 2-ethylhexyl group, an octyl group, a nonyl group, a decyl group, an undecyl group, a dodecyl group, an isotridecyl group, a tetradecyl group, a hexadecyl group, an isohexadecyl group, an octadecyl group, an isooctadecyl group, an oleyl group, an octyldodecyl group, a docosyl group, a decyltetra decyl group, a benzyl group, a cresyl group, a butylphenyl group, a dibutylphenyl group, an octylphenyl group, a nonylphenyl group, a dodecylphenyl group, a dioctylphenyl group, a dinonylphenyl group, a styrenated phenyl group, and a naphthyl group. As the acyl group represented by R² may be that derived from acetic acid, propionic acid, butyric acid, isobutyric acid, caproic acid, caprylic acid, 2-ethylhexanoic acid, pelargonic acid, capric acid, lauric acid, myristic acid, palmitic acid, isopalmitic acid, margaric acid, stearic acid, isostearic acid, arachic acid, behenic acid, palmitoleic acid, oleic acid, linoleic acid, linolenic acid, erucic acid, and benzoic acid. As the maleic acid salt may be mentioned salts of ammonium, salts of monoamines such as methylamine, ethylamine, propylamine, butylamine, hexylamine, octylamine, 2-ethylhexylamine, nonylamine, decylamine, dodecylamine, isotridecylamine, tetradecylamine, hexadecylamine, isohexadecylamine, octadecylamine, isooctadecylamine, oleylamine, linolamine, octyldodecylamine, dococylamine, decyltetradecylamine, and aniline; the salts of polyamines such as ethylenediamine, tetramethylenediamine, dodecylpropylenediamine, octadecylpropylenediamine, oleypropylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, and pentaethylene hexamine; the salts of alkanolamines such as monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, triisopropanolamine, and the alkylene oxide adducts of the aforesaid monoamines or diamines; and the salts of amino acids such as lysine, arginine, and histidine; the salts of alkali metals such as lithium, sodium, and potassium; and the salts of alkaline earth metals such as magnesium, and calcium. As the maleic acid ester may be mentioned esters with alcohols such as methanol, ethanol, allyl alcohol, methallyl alcohol, propanol, isopropanol, butanol, isobutanol, tert-butanol, pentanol, isopentanol, hexanol, heptanol, 2-ethylhexanol, octanol, nonanol, decanol, undecanol, dodecanol, isotridecanol, tetradecanol, hexadecanol, isohexadecanol, octadecanol, issoctadecanol, oleyl alcohol, octyldodecanol, docosanol, and decyltetradecanol. The copolymer for use in this invention can be obtained by copolymerizing the compound represented by formula (I) with maleic anhydride, maleic acid, a maleic acid salt, or a maleic acid ester, using a radical catalyst. Also, the copolymer with maleic acid or a salt or an ester thereof is obtained through esterification, hydrolysis, and subsequent neutralization of a copolymer of maleic anhydride. The copolymerization of the compound of formula (I) with maleic anhydride, maleic acid, a maleic acid salt, or a maleic acid ester may be performed with the addition of a copolymerizable monomer such as styrene, α-olefin, isobutylene, diisobutylene, and vinyl acetate, and the proportion of the compound of formula (I) is preferably at least 30 mol%. The weight average molecular weight of the copolymer is from 1,000 to 2,000,000, and preferably from 10,000 to 500,000. When ℓ in formula (I) is 1, a linear copolymer is obtained, while, when ℓ is 2 or more, a cross-linked copolymer is obtained. With regard to the relationship among ℓ, m and n, no preferred copolymer is obtained when m/(ℓ + n) is larger than 1/3. Also, the copolymer of formula (I) wherein the total number of oxyalkylene groups (aℓ + bm + cn) is over 1,000 is difficult to obtain. For uniformly dissolving or dispersing the compound of formula (I) in a synthetic resin and uniformly dispersing an inorganic filler in the synthetic resin, the aforesaid ranges in the compound of formula (I) is necessary but in the compound of formula (I), it is preferred that Z is a residue of a compound having from 2 to 6 hydroxyl groups, AO is an oxyalkylene group having from 3 to 4 carbon atoms, R¹ is an unsaturated hydrocarbon group having 3 or 4 carbon atoms, R² is a hydrocarbon group having from 1 to 24 carbon atoms or an acyl group, a is from 0 to 200, b is from 0 to 200, c is from 0 to 200, ℓ is from 1 to 5, m is from 0 to 2, n is from 0 to 5, ℓ + m + n is from 2 to 6, aℓ + bm + cn is from 1 to 200, and m/(ℓ + m) ≦ 1/3 . In the copolymer for use in this invention, the extent of a hydrophilic property and a lipophilic property thereof can be changed by changing Z, AO, R¹, R², a, b, c, ℓ, m and n and the extent of them can be properly selected according to the kinds of the synthetic resin and the inorganic filler being used. Examples of the synthetic resin for use in this invention, include polyamides such as Nylon 6, Nylon 6,6, Nylon 12, and polyphenylene terephthalamide; polyesters such as polyethylene terephthalate, polybutylene terephthalate, and polyarylate; polyollefins such as polyethylene and polypropylene; polycarbonate; polyacetal; polyphenylene oxide; polyimide; polystyrene; acrylo-nitrile-styrene copolymer; acrylonitrile-butadiene-styrene terpolymer; polyvinyl chloride; polyvinylidene chloride'; polyvinyl acetate; polymethyl methacrylate; polyethyl acrylate; an unsaturated polyester resin; a phenol resin; a melamine resin; a diallyl phthalate resin; a urethane resin; a silicone resin; an epoxy resin, a fluorine resin, etc. As the inorganic filler for use in this invention, may be mentioned silicates such as kaolin, aluminum silicate, clay, talc, mica, asbestos, calcium silicate, sericite, and bentonite; carbonates such as calcium carbonate, magnesium carbonate, barium carbonate, and dolomite; sulfates such as calcium sulfate, barium sulfate, etc., metal oxides such as magnesia, alumina, antimony oxide, titanium oxide, colloidal silica, diatomaceous earth, and ferric oxide; metal hydroxides such as aluminum hydroxide, magnesium hydroxide, calcium hydroxide, ferric hydroxide, and metatitanic acid; and various inorganic powders, aggregates, inorganic fibers, etc., such as silicon carbide, silicon nitride, boron nitride,zirconia, barium titanate, satin white, carbon black, graphite, sands, gravels, glass fibers and rock wools. In the composition of this invention, the inorganic filler is from 2 to 900 parts by weight, preferably from 3 to 200 parts by weight and of the copolymer of from 0.02 to 20 parts by weight, and preferably from 0.03 to 10 parts by weight, per 100 parts by weight of the synthetic resin. If the proportion of the inorganic filler is less than 2 parts by weight, the improvement of the mechanical characteristics by the inorganic filler cannot be expected. Also, if the proportion of the inorganic filler is over 900 parts by weight and the proportion of the copolymer is less than 0.02 part by weight, the effect of this invention is not sufficiently obtained to reduce the moldability and the mechanical characteristics thereof. Furthermore, if the proportion of the copolymer is over 20 parts by weight, the mechanical characteristics of the moldings are reduced. To the synthetic resin composition of this invention can be, if necessary, added ordinary additives such as antioxidants, ultraviolet absorbers, lubricants, pigments, antistatic agents, and stabilizers. The synthetic resin composition of this invention is prepared by sufficiently mixing the synthetic resin, the inorganic filler, and the copolymer as described above,using a mixer such as tumbler, a kneader, and a Henshel mixer, or a mixing roll, a mixing extruder, etc. At mixing, these three components may be simultaneously mixed or after mixing the copolymer and one of the other compounds, the other one component may be mixed with the mixture. In particular, when the inorganic filler is tre.ated by coating the copolymer thereon and the coated inorganic filler is mixed with the synthetic resin, they are very easily mixed to provide a uniform mixture. When the synthetic resin composition of this invention is intended for molding, the composition is molded into various moldings such as films, sheets, pipes, blow molding products, and extrusion profiles, by various molding machines such as molding extruder, calender, and injection molding machine. Also, the invention can be applied to a paint containing a pigment dispersed therein, a sealant containing a filler dispersed therein, a resin concrete kneaded with an aggregate, or a case of mixing an inorganic filler with a synthetic resin. The copolymer which is used for the synthetic resin of this invention has a hydrophilic group and a lipophilic group to greatly increase the affinity of synthetic resin for an inorganic filler. Accordingly, an inorganic filler is easily dispersed in a synthetic resin at a high concentration, whereby synthetic resin products having excellent characteristics such as strength and appearance can be obtained. The invention is further described by the following examples. The copolymers used in the examples are shown in Table 1 below. The parts in the examples are by weight. Example 1 In a beaker 100 parts of high-density polyethylene (Hi-Zex 5000H, trade name, made by Mitsui Petrochemical Industries, Ltd.), 100 parts of calcium carbonate,and 3 parts of the copolymer shown in Table 2 below were well mixed. The synthetic resin composition thus obtained was kneaded using a 6-inch test roll for 7 minutes at 180°C and then pressed at a temperature of 190°C (preheating 3 minutes, heating 3 minutes) and a pressure of 50 kg/cm² to provide a sheet of 2 mm in thickness. At kneading by the roll, calcium carbonate was quickly kneaded with the high-density polyethylene and the kneaded mixture could be easily released from the roll. The sheet thus obtained was cut into a specimen using a dumbbell type III die for vulcanized rubber (JIS K 6301-75) and a tensile test was applied on the specimen in compliance with JIS K 7113-81. The tensile strength at yield and the percent elongation at break are shown in Table 2. Separately, the same procedure as above was repeated except that stearic acid or calcium stearate which was conventionally used was used as an additive in place of the copolymer or that neither the copolymer nor such an additive was used. The results are also shown in Table 2. Copolymer or Additive Tensile Strength (kg/cm²) Elongation (%) Remarks No. 1 203 81 Invention No. 2 197 78 Invention No. 3 173 69 Invention No. 4 206 82 Invention No. 5 192 77 Invention No. 7 213 87 Invention No. 10 206 81 Invention No. 11 165 52 Invention No. 13 172 60 Invention No. 16 181 66 Invention None 18 8 Comparison Stearic Acid 82 12 Comparison Calcium Stearate 103 16 Comparison From the results shown in Table 2, it can be seen that the synthetic resin compositions of this invention have high tensile strength and elongation and thus are excellent in mechanical characteristics. Example 2 One hundred (100) parts of the inorganic filler shown in Table 3 below was mixed with 3 parts of the copolymer shown in the same table using a Henshel mixer to provide the inorganic filler coated with the copolymer. After mixing the coated inorganic filler and pellet-form polypropylene (UBEPOLIPRO J109G, trade name, made by Ube Industries, Ltd.) so as to give the composition shown in Table 3,the mixture was kneaded by a single screw extruder to provide a pellet-form synthetic resin composition. The synthetic resin composition was molded by an injection molding machine to provide a specimen for tensile test. A tensile test (JIS K 7113-81) was applied on the specimen and the results are shown in Table 3. Separately, the same procedure as above was repeated except that stearic acid or calcium stearate was used as additive in place of the copolymer or that neither the composition nor such an additive was used. The results are shown in the same table. Copolymer or Additive (parts) Inorganic Filler (parts) Tensile Strength (kg/cm²) Elongation (%) Remarks No. 1 3 Calcium Carbonate 100 212 90 Invention No. 6 3 " 100 242 92 Invention No. 7 3 " 100 248 92 Invention No. 8 3 " 100 223 90 Invention No. 9 3 " 100 203 86 Invention No. 12 3 " 100 236 91 Invention No. 14 3 " 100 210 88 Invention No. 15 3 " 100 230 90 Invention No. 7 0.3 Titanium Oxide 10 310 218 Invention No. 7 0.9 Talc 30 270 162 Invention None 3 Calcium Carbonate 100 20 8 Comparison Stearic Acid 3 " 100 47 16 Comparison Calcium Stearate 3 " 100 106 20 Comparison Stearic Acid 0.3 Titanium Oxide 10 210 83 Comparison Stearic Acid 0.9 Talc 30 123 36 Comparison From the results shown in Table 3, it can be seen that the synthetic resin compositions of this invention have high tensile strength and elongation and thus are excellent in mechanical characteristics. Example 3 Five hundred (500) g of precipitated calcium carbonate having a mean particle size of 0.1 µm was mixed with 10 g of the copolymer shown in Table 4 using a Henshel mixer to provide precipitated calcium carbonate coated with the copolymer. After mixing 100 parts of precipitated calcium carbonate coated with the copolymer and 100 parts by polypropylene (UBEPOLYPRO J109G, trade name, made by Ube Industries, Ltd.), the mixture was kneaded using a single screw extruder to provide pellets. The pellets were molded using an injection molding machine. The tensile strength and elongation of the molded products by JIS K 7113-81 are shown in Table 4. Copolymer or Additive Tensile Strength (kg/cm²) Elongation (%) Remarks No. 1 218 90.2 Invention No. 4 220 90.1 Invention No. 5 212 89.2 Invention No. 7 247 91.1 Invention No. 14 210 87.3 Invention No. 17 238 90.2 Invention Stearic Acid 45 13.5 Comparison Calcium Stearate 121 20.0 Comparison None 21 8.2 Comparison From the results shown in Table 4, it can be seen that the polypropylene moldings added with precipitated calcium carbonate coated with the copolymer in this invention have high tensile strength and elongation and thus are excellent in properties. Example 4 Five hundreds (500) g of titanium oxide was mixed with 10 g of the copolymer shown in Table 5 below using a Henshel mixer to provide titanium oxide coated with the copolymer. After mixing 10 parts of the titanium oxide coated with the copolymer and 100 parts of an ABS resin (Denka ABS GR1000, trade name, made by Denki Kagaku Kogyo K.K.), the mixture was kneaded using a single screw extruder to provide pellets. The pellets were molded by means of an injection molding machine. The tensile strength (JIS K 7113-81) and the flexural strength (JIS K 7203-82) of the moldings are shown in Table 5. Copolymer or Additive Tensile Strength (kg/cm²) Elongation (%) Remarks No. 1 412 720 Invention No. 2 402 711 Invention No. 4 422 752 Invention No. 7 433 771 Invention No. 13 392 692 Invention No. 17 428 728 Invention Stearic Acid 212 527 Comparison Calcium Stearate 227 562 Comparison None 182 323 Comparison From the results shown in Table 5, it can be seen that the ABS resins blended with titanium oxide coated with the copolymer have high tensile strength and flexural strength and thus are excellent in properties. Example 5 One hundred (100) parts of the inorganic filler shown in Table 6 below was mixed with 3 parts of Copolymer No. 7 using a Henshel mixer to provide the inorganic filler coated with the copolymer. After mixing the coated inorganic filler and the pellet-form synthetic resin shown in Table 6 so as to give the composition shown in 6, the mixture was kneaded by means of a single screw extruder to provide a pellet-form synthetic resin composition. The synthetic resin composition was molded by an injection molding machine to provide a specimen for strength test. A tensile test (JIS K 7113-81) and a flexural test (JIS K 7203-82) were applied onto the specimen and the results are shown in Table 6. Separately, the same procedure and test were repeated except that stearic acid was added as an additive in place of copolymer No. 7. From the results shown in Table 6, it can be seen that the synthetic resin compositions of this invention have high tensile strength and flexural strength and are excellent in mechanical characteristics. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims: A synthetic resin composition comprising a single type of a synthetic resin in an amount of 100 parts by weight, from 2 to 900 parts by weight of an inorganic filler, and from 0.02 to 20 parts by weight of a copolymer of a compound represented by formula (1) and maleic anhydride, maleic acid, a maleic acid salt or a maleic acid ester; wherein Z is a residue of a compound having from 2 to 8 hydroxyl groups; AO is an oxyalkylene group having from 2 to 18 carbon atoms; R¹ is an unsaturated hydrocarbon group having from 2 to 5 carbon atoms; R² is a hydrocarbon or acyl group having from 1 to 40 carbon; a is from 0 to 1,000, b is from 0 to 1,000, c is from 0 to 1,000, ℓ is an integer of from 1 to 8, m is an integer of from 0 to 2, and n is an integer of from 0 to 7, ℓ + m + n = 2 to 8 , aℓ + bm + cn = 1 to 1,000 , and m/(ℓ + n) ≦ 1/3 with the proviso that the presence of more than one synthetic resin in the composition is excluded. The synthetic resin composition as in claim 1, wherein the synthetic resin is Nylon 6, Nylon 6,6, Nylon 12, polyphenylene terephthalamide, polyethylene terephthalate, polybutylene terephthalate, polyarylate, polyethylene, polypropylene, polycarbonate, polyacetal, polyphenylene oxide, polyimide, polystyrene, an acrylonitrile-styrene copolymer, an acrylonitrilebutadiene-styrene terpolymer, polyvinyl chloride, polyvinylidene chloride, polyvinyl acetate, polymethyl methacrylate, polyethyl acrylate, an unsaturated polyester resin, a phenol resin, a melamine resin, a diallyl phthalate resin, a urethane resin, a silicone resin, an epoxy resin, or fluororesin. The synthetic resin composition in claim 1, wherein the inorganic filler is kaolin, aluminum silicate, clay, talc, mica, asbestos, calcium silicate, sericite, bentonite, calcium carbonate, magnesium carbonate, barium carbonate, dolomite, calcium sulfate, barium sulfate, magnesia, alumina, antimony oxide, titanium oxide, colloidal silica, diatomaceous earth, ferric oxide, aluminum hydroxide, magnesium hydroxide, calcium hydroxide, ferric hydroxide, metatitanic acid, silicon carbide, silicon nitride, boron nitride, zirconia, barium titanate, satin white, carbon black, graphite, sands, gravels, glass fibers, or rock wools. The synthetic resin composition as in claim 1, wherein in the copolymer of the compound represented by formula (1) and maleic anhydride, maleic acid, a maleic acid salt, or a maleic acid ester, Z is a residue of a compound having from 2 to 6 hydroxyl groups, AO is an oxyalkylene group having from 2 to 4 carbon atoms, R¹ is an unsaturated hydrocarbon group having from 3 or 4 carbon atoms, R2 is a hydrocarbon or acyl group having from 1 to 24 carbon atoms, a is from 0 to 200, b is 0 to 200, c is from 0 to 200, ℓ is an integer of from 1 to 5, m is an integer of from 0 to 2, n an integer of is from 0 to 5, ℓ + m + n = 2 to 6 , aℓ + bm + cn = 1 to 200 , and m/(ℓ + m) ≦ 1/3 . The synthetic resin composition as in Claim 1, which comprises 100 parts by weight of the synthetic resin, from 3 to 200 parts by weight of the inorganic filler, and from 0.03 to 10 parts by weight of the copolymer of the compound represented by formula (1) and maleic anhydride, maleic acid, a maleic acid salt, or a maleic acid ester. The use of 0.02 to 20 parts by weight of a copolymer of a compound represented by formula (1) below and maleic anhydride, maleic acid, a maleic acid salt, or a maleic acid ester in a synthetic resin composition which comprises 100 parts by weight of a synthetic resin and from 2 to 900 parts by weight of an inorganic filler in order to increase the mutual affinity between the said synthetic resin and said inorganic filler. wherein Z is a residue of a compound having from 2 to 8 hydroxyl groups; AO is an oxyalkylene group having from 2 to 18 carbon atoms; R¹ is an unsaturated hydrocarbon group having from 2 to 5 carbon atoms; R² is a hydrocarbon or acyl group having from 1 to 40 carbon; a is from 0 to 1,000, b is from 0 to 1,000, c is from 0 to 1,000, ℓ is an integer of from 1 to 8, m is an integer of from 0 to 2, and n is an integer of from 0 to 7, ℓ + m + n = 2 to 8 , aℓ + bm + cn = 1 to 1,000 , and m/(ℓ + n) ≦ 1/3 . The use according to claim 6, wherein the inorganic filler and the copolymer are added to the synthetic resin in the form that the inorganic filler is coated with the copolymer.

Inventors: HIRAO KEIJI, HONDA SUSUMU, IGARASHI TAIZO, MATSUDA HISAMICHI, SUGIHARA TAKAHIKO, HIRAO, KEIJI, HONDA, SUSUMU, IGARASHI, TAIZO, MATSUDA, HISAMICHI, SUGIHARA, TAKAHIKO
Applicants: NIPPON OILS & FATS CO LTD, NIPPON OIL AND FATS COMPANY, LIMITED
Application year: 1989
Main classification: C08K3
IPC codes: C08K9, B01F17, C08L101