THERMOSETTING RESIN COMPOSITION

Abstract: The present invention relates to thermosetting resin compositions comprising a bismaleimide compound represented by the formula (I) and an aromatic amine resin represented by the general formula (II) and to processes for preparing the same.

Description: The present invention relates to novel thermosetting resin compositions useful for preparing molded articles that are heat resistant and exhibit high mechanical strength. Prior to the present invention, thermosetting resins having an imide structure have been extensively utilized in various industrial fields, since cured materials obtained from these resins exhibit excellent electrical insulating properties, heat resistance and dimensional stability. However, thermosetting resins obtained by thermal polymerization of aromatic bismaleimides alone are extremely brittle and have poor flexibility although they are excellent in heat resistance. In an attempt to overcome these disadvantages, thermosetting resin compositions have been developed that contain an aromatic bismaleimide and an aromatic diamine. For example, a polyaminobismaleimide resin (Rhone-Poulenc; registered trade mark Kelimid) comprising N,N'-4,4'-diphenylmethanebismaleimide and 4,4'-diaminodiphenylmethane is widely used in the fields of impregnating varnishes, laminated plates, molded articles and the like (Japanese Patent Laid-open Publication No. 23250/1971). However, thermosetting resin compositions containing an aromatic bismaleimide and an aromatic diamine exhibit poor heat resistance, and unsatisfactory impact resistance and flexibility. Preferred embodiments of the present invention overcome the problems and disadvantages of the prior art by providing thermosetting resin compositions useful for preparing molded articles that exhibit superior mechanical strength and heat resistance than prior art resins. They may also provide thermosetting resin compositions that are useful for preparing molded articles having high mechanical strength and heat resistance. Additional objects and advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. EP-A-0 311 387, which is prior art only under EPC Article 54(3), and thus relevant only to novelty, also discloses bismaleimide/amine resins. However the bismaleimides disclosed therein are not according to the present invention. The invention provides a thermosetting resin composition comprising (a) 100 parts by weight of a bismaleimide compound of the formula (I) wherein R represents a divalent group selected from wherein X represents a direct bond between the benzene rings, or represents a group selected from a divalent hydrocarbon group having from 1 to 10 carbon atoms, an isopropylidene group having six fluorine atoms, a carbonyl group, a thio group, a sulfinyl group, a sulfonyl group and an oxo group, and (b) from 5 to 100 parts by weight of an aromatic amine resin of the formula (II) wherein A is selected from a phenylene group, an alkyl-substituted phenylene group, a diphenylene group, a diphenyl ether group and a naphthylenyl group; R¹ is selected from a halogen atom, a hydroxyl group, an alkoxy group having up to 4 carbon atoms, and an alkyl group having up to 5 carbon atoms; ℓ is 1 or 2; m is an integer of from 0 to 3, and when m is 2 or 3, the groups represented by R¹ may be identical or different, and two of these groups may form a five-membered ring or six-membered aliphatic ring which may have a side chain; and n is an integer of from 0 to 300. Reference will now be made in detail to the present preferred embodiments of the invention. A bismaleimide compound represented by the formula (I) can be prepared by subjecting to a conventional condensation/dehydration reaction and a maleic anhydride and a diamine compound represented by the formula (III) wherein R represents a divalent group selected from wherein X is directly bonded to the benzene rings and is a group selected from a divalent hydrocarbon group having from 1 to 10 carbon atoms, an isopropylidene group having six fluorine atoms, a carbonyl group, a thio group, a sulfinyl group, a sulfonyl group and an oxo group. Exemplary divalent groups of the moiety R in the bismaleimide compound (I) include Preferably, the moiety R is selected from Exemplary suitable bismaleimide compounds of the formula (I) for use in the present invention include 1,3-bis(3-maleimidophenoxy)benzene, bis[4-(3-maleimidophenoxy)phenyl]methane, 1,1-bis[4-(3-maleimidophenoxy)phenyl]ethane, 1,2-bis[4-(3-maleimidophenoxy)phenyl]ethane, 2,2-bis[4-(3-maleimidophenoxy)phenyl]propane, 2,2-bis[4-(3-maleimidophenoxy)phenyl]butane, 2,2-bis[4-(3-maleimidophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 4,4-bis(3-maleimidophenoxy)biphenyl, bis[4-(3-maleimidophenoxy)phenyl]ketone, bis[4-(3-maleimidophenoxy)phenyl] sulfide, bis[4-(3-maleimidophenoxy)phenyl] sulfoxide, bis[4-(3-maleimidophenoxy)phenyl]sulfone and bis[4-(3-maleimidophenoxy)phenyl] ether. The bismaleimide compounds can be used singly or in combination. The aromatic amine resin of the formula (II) used in the present invention can be prepared by reacting (a) 1 mole of an aralkyl alcohol derivative represented by the formula (IV) R²OCH₂-A-CH₂OR² (IV) wherein A is selected from a phenylene group, an alkyl-substituted phenylene group, a diphenylene group, a diphenyl ether group and a naphthylenyl group, and R² is selected from a hydrogen atom, an acyl group and an alkyl group having up to 4 carbon atoms, with (b) from 1 to 15 moles of an aromatic amine compound represented by the formula (V) wherein R¹ is selected from a halogen atom, a hydroxyl group, an alkoxy group having up to 4 carbon atoms, and an alkyl group having up to 5 carbon atoms; ℓ is 1 or 2; m is an integer of from 0 to 3, and when m is 2 or 3, the groups represented by R¹ may be identical or different, and two of these groups may form a five-membered ring or six-membered aliphatic ring which may have a side chain (Japanese Patent Application No. 252517/1987). The moiety A in the aralkyl alcohol derivative represented by the formula (IV) is preferably a phenylene group selected from an alkyl-substituted phenylene group selected from a diphenylene group of a diphenyl ether group of and a naphthylene group of Preferably, the moiety A is selected from Most preferably, the moiety A is R² in the formula (IV) is selected from a hydrogen atom, an acyl group or an alkyl group. Exemplary suitable derivatives of formula IV include α,α'-dihydroxy-o-xylene, α,α'-dihydroxy-m-xylene, α,α'-dihydroxy-p-xylene, α,α'-diacetoxy-o-xylene, α,α'-diacetoxy-m-xylene, α,α'-diacetoxy-p-xylene, α,α'-dipropionoxy-p-xylene, α,α'-di-n-butyloxy-p-xylene, α,α'-dimethoxy-o-xylene, α,α'-dimethoxy-m-xylene, α,α'-dimethoxy-p-xylene, α,α'-diethoxy-o-xylene, α,α'-diethoxy-m-xylene, α,α'-diethoxy-p-xylene, α,α'-diisopropoxy-o-xylene, α,α'-diisopropoxy-m-xylene, α,α'-diisopropoxy-p-xylene, α,α'-di-n-propoxy-p-xylene, α,α'-di-n-butoxy-m-xylene, α,α'-di-n-butoxy-p-xylene, α,α'-di-secbutoxy-p-xylene, α,α'-diisobutoxy-p-xylene, 4,4'-dihydroxymethyldiphenyl ether, 4,4'-dihydroxymethyldiphenyl, 2,6-dihydroxymethylnaphthalene, 4,4'-diacetoxymethyldiphenyl ether, 4,4'-diacetoxymethyldiphenyl, 2,6-diacetoxymethylnaphthalene, 4,4'-methoxydiphenyl ether, 4,4'-methoxymethyldiphenyl, 4,4'-diethoxymethylphenyl ether, 4,4'-diisopropoxymethyldiphenyl, 4,4'-diisobutoxymethyldiphenyl ether, α,α'-dimethoxy-2-methyl-p-xylene, α,α'-dimethoxy-3-methyl-m-xylene, α,α'-dihydroxy-2,5-dimethyl-p-xylene, α,α'-dimethoxy-2,5-dimethyl-p-xylene, α,α'-dimethoxy-2,4-dimethyl-1,3-xylene and α,α'-dimethoxy-2,4-dimethyl-1,5-xylene. Preferably, R² is α,α'-dimethoxy-p-xylene. R¹ in the aromatic amine compound represented by the formula (V) is selected from a halogen atom, a hydroxyl group, an alkoxy group having up to 4 carbon atoms, and an alkyl group having up to 5 carbon atoms. Preferably, R¹ is selected from an alkyl group having from 1 to 3 carbon atoms, a hydroxy group and a halogen atom. It is also preferred that R¹ does not exist in the general formula (V), i.e., that m is 0. Preferably, only one or two amino groups is or are present in the amine compound represented by the general formula (V). Exemplary suitable amino compounds include aniline, o-toluidine, m-toluidine, p-toluidine, o-ethylaniline, m-ethylaniline, p-ethylaniline, o-isopropylaniline, m-isopropylaniline, p-isopropylaniline, o-n-propylaniline, o-tert-butylaniline, p-tert-butylaniline, o-n-butylaniline, p-sec-butylaniline, 2,3-xylidine, 2,4-xylidine, 2,6-xylidine, 3,4-xylidine, 3,5-xylidine, 2-methyl-3-ethylaniline, 2-methyl-4-isopropylaniline, 2,6-diethylaniline, 2-ethyl-5-tert-butylaniline, 2,4-diisopropylaniline, 2,4,6-trimethylaniline, 4-chloroaniline, 4-bromoaniline, 4-fluoroaniline, 3-chloroaniline, 3-bromoaniline, 3,4-dichloroaniline, 3-chloro-o-toluidine, 3-chloro-p-toluidine, 2,6-dimethyl-4-chloroaniline, o-aminophenol, m-aminophenol, p-aminophenol, 2-amino-4-cresol, 4-amino-2-tert-butylphenol, 2,6-dimethyl-4-aminophenol, 2,6-dichloro-4-aminophenol, 2-amino-1,3-resorcin, 4-amino-1,3-resorcin, 2-aminohydroquinone, 2-methoxyaniline, 3-methoxyaniline, 4-methoxyaniline, 2-isopropoxyaniline, 2,4-dimethoxyaniline, o-phenylenediamine, m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diaminotoluene, 2,4-diaminoethylbenzene, 2,6-diaminoethylbenzene, 2,4-diaminoisopropylbenzene, 2,4-diamino-tert-butylbenzene, 2,6-diamino-tert-butylbenzene, 2,4-diamino-1,3-dimethylbenzene, 1,1-dimethyl-4-aminoindane and 1,1-dimethyl-4,6-diaminoindane. Particularly preferred, examples from this list are:-aniline, toluidines, xylidines, aminophenols and diamines is employed. With regard to the reaction of the aralkyl alcohol derivative of the formula (IV) and the aromatic amine compound of the formula (V), a condensation reaction is performed in a ratio of from about 1 to about 15 moles, preferably from about 1.1 to about 10 moles of the aromatic amine compound per mole of the aralkyl alcohol derivative at a temperature of from about 170 to about 240°C for a period of from about 10 to about 40 hours in the presence of an acid catalyst such as hydrochloric acid. After completion of the reaction, the reaction mixture is neutralized with an alkali such as caustic soda, and is then washed with water. Afterwards, the unreacted aromatic amine compound is removed from the system under reduced pressure, thereby producing an aromatic amine resin of the formula (II). The molecular weight of the aromatic amine resin is preferably from about 300 to about 60,000, and the softening point thereof is preferably from room temperature, at which the aromatic amine resin is liquid, to 250°C (determined by a ring and ball method in accordance with JIS-K-2548). Particularly preferred molecular weights and softening points of the aromatic amine resin are from 300 to 20,000 and from room temperature to 200°C. A preferred aromatic amine resin (II) is The thermosetting resin composition of the present invention can be prepared from the bismaleimide compound of the formula (I) and the aromatic amine resin of the formula (II) by any of the following procedures. (I) The bismaleimide and the aromatic amine resin can be ground and mixed in a solid-solid state or in a solid-liquid state. Alternatively, these materials may be thermally treated to form a prepolymer, which is then ground into pellets or a powder. In this case, heating conditions are preferably such that curing proceeds partially up to the stage of the prepolymer. Usually heating treatment is carried out at a temperature of from 70°C to 220°C for from 5 to 240 minutes, preferably at from 80°C to 200°C for from 10 to 180 minutes. (2) The bismaleimide and the aromatic amine resin are dissolved in an organic solvent, and the solution is then introduced into a poor solvent to deposit crystals, the latter are afterward collected by filtration and then dried to obtain pellets or a powder. Alternatively, after being dissolved in the organic solvent, the materials may be thermally treated to partially cure them to the stage of a prepolymer and are then introduced into the poor solvent. The deposited crystals are afterward collected by filtration and then dried to obtain pellets or a powder. The heating conditions in this case are the same as in the above-mentioned procedure (I). The organic solvent must not react with either component, and in addition, it is preferred that the organic solvent be a good solvent to both components. Exemplary suitable reaction solvents include halogenated hydrocarbons such as methylene chloride, dichloroethane and trichloroethylene; ketones such as acetone, methyl ethyl ketone, cyclohexanone and diisopropyl ketone; ethers such as tetrahydrofuran, dioxane and methyl cellosolve; aromatic compounds such as benzene, toluene and chlorobenzene; and non-protonic polar solvents such as acetonitrile, N,N-dimethylformamide, N,N-dimethylacetamide, dimethyl sulfoxide, N-methyl-2-pyrrolidone and 1,3-dimethyl-2-imidazolidinone. The aromatic amine resin of the formula (II) is present in the composition of the invention in an anount of from 5 to 100 parts by weight, preferably from 5 to 80 parts by weight, based on 100 parts by weight of the bismaleimide compound of the formula (I). When the amount of the aromatic amine resin present in the composition is less than 5 parts by weight, a cured article which is manufactured therefrom is extremely brittle and thus satisfactory bending strength cannot be obtained. Inversely, when the aromatic amine resin is present in an amount greater than 100 parts by weight, the heat resistance of the cured article is low. To the thermosetting resin composition of the present invention, the following components a, b and c may be added in amounts such that they do not to hinder achievement of the objects of the present invention. (a) A curing accelerator: For example, a radical polymerization initiator such as an azo compound or an organic peroxide, or an ionic catalyst such as a tertiary amine, a quaternary ammonium salt, an imidazole or a boron trifluoride/amine salt. (b) A powdery reinforcing material or filler: For example, a metallic oxide such as aluminum oxide or magnesium oxide, a metallic hydroxide such as aluminum hydroxide, a metallic carbonate such as magnesium carbonate, diatomaceous earth powder, basic magnesium silicate, calcined clay, fine silica powder, molten silica, crystalline silica, carbon black, kaolin, fine mica powder, quartz powder, metallic hydroxide such as aluminum hydroxide, graphite, asbestos, molybdenum disulfide or antimony trioxide. A fibrous reinforcing material or filler: For example, an inorganic fiber such as glass fiber, rock wool, ceramic fiber, alumina fiber or potassium titanate fiber, or an organic fiber such as carbon fiber or aromatic polyamide. (c) Various synthetic resins which are used to improve characteristics of resins for final coating films, adhesive layers or resinous molded articles: For example, a thermosetting resin such as phenolic resin, epoxy resin or melamine resin or silicone resin, polyamide, polycarbonate, polysulfone, polyether sulfone, polyether ether ketone, modified polyphenylene oxide, polyphenylene sulfide, polyether imide and fluorine-containing resins. The thermosetting resin composition of the present invention can be molded by known molding techniques such as compression molding, transfer molding, extrusion molding or injection molding. The composition of the invention is excellent in moldability. In addition, the molded articles prepared from the thermosetting resin compositions of the present invention exhibit excellent mechanical strength and heat resistance. The composition of the invention have numerous applications in the electrical and electronic fields as well as mechanical fields, particularly aircrafts and vehicles and thus are of great industrial utility. The invention will be further clarified by the following examples, which are intended to be purely exemplary of the invention. Synthesis Example 1 In a reaction vessel equipped with a stirrer, a thermometer and a Dean Stark azeotropic distillation trap were placed 1,116 g (12.0 moles) of aniline as an aromatic amine compound represented by the general formula (V), 665 g (4.0 moles) of α,α'-dimethoxy-p-xylene as an aralkyl alcohol derivative represented by the general formula (IV) and 626 g (6.0 moles) of a 35% aqueous hydrochloric acid solution as a catalyst, and the temperature of the solution was raised while a nitrogen gas was fed thereinto. When the temperature in the reaction vessel, i.e., the inside temperature had reached a level of about 110°C, water began to distill and to collect in the trap, and the collected water was thrown away from the system. Afterwards, the temperature was further elevated, and when it reached a level of about 130°C, distillation of methanol was observed. While methanol was distilled off, the temperature was continuously raised, and after the inside temperature had reached 170°C, the temperature level was maintained constantly for 3 hours. When the period of time had elapsed, the generation of methanol was scarcely confirmed. Afterward, the inside temperature was continuously raised, and reaction was carried out at a temperature of 190 to 200°C for 12 hours. Next, the inside temperature was lowered to 95°C by cooling, and 1,680 g of a 15% caustic soda solution were added thereto, followed by stirring and neutralizing. After standing, the resultant lower water layer was removed therefrom, and 3,000 g of a saturated saline solution were then added thereto, and washing and separation followed. Next, heating and dehydration were carried out under nitrogen flow, followed by pressing and filtering to remove inorganic salts and the like therefrom. The solution was then concentrated under a reduced pressure of from 2 to 3 mmHg to recover 519 g of unreacted aniline. The remaining solution was collected, and 945 g of a light yellowish brown aniline resin (aromatic amine resin) were obtained. The aromatic amine resin was then analyzed by high performance liquid chromatography. The compound of the general formula (II) in which n = 0 was present in an amount of 28 mole%, the compound of n = 1 in an amount of 16.8 mole%, the compound of n = 2 in an amount of 10.5 mole%, the compound of n = 3 in an amount of 7.8 mole%, and the compound of n ≧ 4 in an amount of 36.9 mole%. Furthermore, with regard to the thus obtained resin, its amine equivalent was 0.578 equivalent/100 g (perchloric acid-glacial acetic acid method), and its softening point was 68°C, when measured by a ring and ball method softening point measuring device in accordance with JIS-K-2548. In addition, the average molecular weight of the resin was 960. Synthesis Example 2 Following the same procedure as in Synthesis Example 1 with the exception that 745 g (8.0 moles) of aniline, 664 g (4.0 moles) of α,α'-dimethoxy-p-xylene and 420 g (4.0 moles) of a 35% aqueous hydrochloric acid solution as a catalyst were used, a reaction was performed, thereby obtaining 747 g of a light yellowish brown aniline resin (aromatic amine resin). The thus obtained aromatic amine resin was then analyzed by high performance liquid chromatography. The compound of the general formula (II) in which n = 0 was present in an amount of 17.0 mole%, the compound of n = 1 in an amount of 14.5 mole%, the compound of n = 2 in an amount of 13.2 mole%, and the compound of n ≧ 3 in an amount of 55.2 mole%. Furthermore, with regard to the obtained resin, its amine equivalent was 0.520 equivalent/100 g, its softening point of the resin was 61°C, and its average molecular weight was 2,100. Synthesis Example 3 Following the same procedure as in Synthesis Example 1 with the exception that 244.4 g (2.0 moles) of 2,4-diaminotoluene as an aromatic amine compound represented by the general formula (V) and 209 g (2.0 moles) of a 35% aqueous hydrochloric acid-solution as a catalyst were used, a reaction was performed, thereby obtaining 132 g of a reddish brown oily diamino toluene resin (aromatic amine resin). The thus obtained aromatic amine resin was then analyzed by high performance liquid chromatography. The compound of the general formula (II) in which n = 0 was present in an amount of 44.5 mole%, the compound of n = 1 in an amount of 29.7 mole%, the compound of n = 2 in an amount of 14.6 mole%, and the compound of n ≧ 3 in an amount of 11.2 mole%. Furthermore, with regard to the obtained resin, its amine equivalent was 1.204, its softening point was 46°C, and its average molecular weight was 550. Synthesis Example 4 Following the same procedure as in Synthesis Example 1 with the exception that 121.1 g (1.3 moles) of aniline as an aromatic amine compound represented by the general formula (V), 138.2 g (1.0 mole) of an α,α'-dihydroxy-m-xylene as an aralykyl alcohol derivative represented by the general formula (IV) and 33 g (0.325 mole) of concentrated sulfuric acid as a catalyst were used, reaction was performed, thereby obtaining 151 g of a light yellowish brown aniline resin (aromatic amine resin). Furthermore, with regard to the obtained aromatic amine resin, its amine equivalent was 0.496, its softening point was 118°C, when measured by a ring and ball method softening point measuring device in accordance with JIS-K-2548, and its average molecular weight was 6,500. Synthesis Example 5 In a reaction vessel were placed 109 g (1.0 mole) of p-aminophenol as an aromatic amine compound represented by the general formula (V), 110.2 g (0.5 mole) of α,α′-diacetoxy-p-xylene as an aralkyl alcohol derivative represented by the general formula (IV), and 6.8 g (0.05 mole) of zinc chloride and 19 g (0.1 mole) of p-toluenesulfonic acid as catalysts, and a reaction was carried out under reduced pressure given by a water jet pump. The reaction began at about 30°C, and the temperature was raised up to 170°C in 3 hours. In the meantime, the formed acetic acid was recovered through a deep cooling trap. The temperature level was maintained for 3 hours, and then the reaction temperature was raised up to 200°C. Aging was then carried out at a temperature of from 200 to 210°C for 1 hour, and at this point of time, the reaction was brought to an end. The solution was then cooled to 95°C, and 300 ml of toluene were added thereto, followed by stirring and dissolving. Afterward, 20.2 g of triethylamine were added thereto, and 200 ml of water were further added thereto. The solution was then stirred and allowed to stand, and the resultant lower water layer was removed therefrom. The solution was further washed with 200 ml of water one more time, and the water layer was then removed therefrom. Afterward, the solution was concentrated under reduced pressure so as to remove toluene and unreacted p-aminophenol therefrom, so that a brown residue which was a co-condensation resin (aromatic amine resin) of p-aminophenol was obtained in an amount of 138 g. With regard to the thus obtained aromatic amine resin, its amine equivalent was 0.525, its softening point was 94°C, when measured by a ring and ball method softening point measuring device in accordance with JIS-K-2548, and its average molecular weight was 2,200. Synthesis Examples 6 to 14 Reactions were performed in accordance with the same procedure as in Synthesis Example 1 with the exception that the kind of aromatic amine compound represented by the general formula (V), the kind and amount of aralkyl alcohol derivative represented by the general formula (IV), the kind and amount of catalysts and rection conditions were as shown in Table 1, thereby obtaining various aromatic amine resins shown in Table 1. Examples 1 to 4 In a stainless steel reaction vessel equipped with a stirrer, a reflux condenser and a nitrogen introduction pipe were placed 4,4'-bis(3-maleimidophenoxy)biphenyl and the aromatic amine resin obtained in Synthesis Example 1 in amounts shown in Table 2. The compositions were heated and melted at 180°C for 20 minutes. Afterward, defoaming was carried out at 150°C under reduced pressure (10 to 15 mmHg) ( ca 1300 - 2000 Nm²) for 30 minutes, and the material was then cooled to room temperature, thereby obtaining a brown semitransparent resin composition which was solidified in a glass state. A mold which had been heated to 180°C was then packed with the thus obtained composition, while the latter was heated and melted, and it was then maintained at 200°C under 50 kg/cm² for 30 minutes to perform compression molding. Afterward, the molded piece was taken out therefrom. The piece was further postcured at 250°C for 4 hours in an oven, so that a 127-mm-long, 12.7-mm-wide, 6.4-mm-thick cured specimen was prepared. For the respective specimens prepared by the above-mentioned procedure, thermal deformation temperature and bending strength were measured in accordance with ASTM-D-648 and ASTM-D-790, and a thermal decomposition starting temperature was also measured in the air at a temperature rise rate of 10°C/minute. The results are set forth in Table 2. Examples 5 to 20 and Comparative Examples 1 and 2 The same procedure as in Examples 1 to 4 was repeated with the exception that 100 parts by weight of each bismaleimide compound shown in Table 2 were used and each aromatic amine resin shown in Table 2 was used in an amount shown in Table 2. The results are set forth in Table 2. Comparative Example 3 The same procedure as in Examples 1 to 4 was repeated with the exception that N,N'-4,4'-diphenylmethanebismaleimide and 4,4'-diaminodiphenylmethane were used in amounts shown in Table 2. The results are set forth in Table 2. Comparative Example 4 A molded specimen was prepared in accordance with the same procedure as in Examples 1 to 4 with the exception that a polyaminobismaleimide resin (trade name Kelimid-1050; made by Nippon Polyimide Co., Ltd.) was substituted for the resin composition of the present invention, and various physical properties were measured. The results are set forth in Table 2. According to the results in Table 2, molded articles obtained from the thermosetting resin composition of the present invention had high bending strength and bending elasticity modulus, and had a thermal deformation temperature of 290°C or more and a thermal decomposition starting temperature of 350°C or more, which was indicative that the articles obtained from the composition of the present invention were also excellent in heat resistance.

Claims: A thermosetting resin composition comprising (i) 100 parts by weight of a bismaleimide compound represented by the formula (I) wherein R represents a divalent group selected from wherein X represents a direct bond between the benzene rings, or is a group selected from a divalent hydrocarbon group having from 1 to 10 carbon atoms, an isopropylidene group having six fluorine atoms, a carbonyl group, a thio group, a sulfinyl group, a sulfonyl group and an oxo group, and (ii) from 5 to 100 parts by weight of an aromatic amine resin represented by the formula (II) wherein A represents a group selected from a phenylene group, an alkyl-substituted phenylene group, a diphenylene group, a diphenyl ether group and a naphthylenyl group; R¹ is selected from a halogen atom, a hydroxyl group, an alkoxy group having up to 4 carbon atoms, and an alkyl group having up to 5 carbon atoms; ℓ is 1 or 2; m is an integer of from 0 to 3, and n is an integer of from 0 to 300. The thermosetting resin composition of claim 1 wherein m is 2 or 3 and the groups represented by R¹ are identical. The thermosetting resin composition of claim 1 wherein m is 2 or 3 and the groups represented by R¹ are different. The thermosetting resin composition of claim 1 wherein m is 2 or 3 and two of the groups represented by R¹ form a five membered ring or six membered aliphatic ring which may have a side chain. The thermosetting resin composition of any preceding claim wherein said R in said formula (I) represents a divalent group selected from The thermosetting resin composition of any of claims 1-4 wherein R in said formula (I) represents a divalent group selected from The thermosetting resin composition of any preceding claim wherein A in said formula (II) represents a group selected from The thermosetting resin composition of any of claims 1-6 wherein A in said formula (II) represents a group selected from The thermosetting resin composition of claim 1 wherein A in said formula (II) represents The thermosetting resin composition of any preceding claim wherein R¹ in said formula (II) is selected from an alkyl group having from 1 to 3 carbon atoms, a hydroxyl group and a halogen atom. The thermosetting resin composition of any preceding claim wherein m in said formula (II) is 0. The thermosetting resin composition of any preceding claim wherein said ℓ in said formula (II) is 1. The thermosetting resin composition of any preceding claim wherein the aromatic amine resin of the formula (II) is The thermosetting resin composition of claim 13 wherein the bismaleimide compound of the formula (I) is The thermosetting resin compostion of claim 13 wherein the bismaleimide compound of the formula (I) is The thermosetting resin composition of claim 13 wherein the bismaleimide compound of the formula (I) is The thermosetting resin composition of claim 13 wherein the bismaleimide compound of the formula (I) is The thermosetting resin composition of any preceding claim wherein the molecular weight of said aromatic amine resin is from 300 to 60,000. The thermosetting resin composition of any preceding claim wherein the molecular weight of said aromatic amine resin is from 300 to 20,000. A process for preparing the thermosetting resin composition of any preceding claim comprising mixing 100 parts of said bismaleimide compound of the formula (I) with from 5 to 100 parts by weight of said aromatic amine resin of the formula (II). The process of claim 20 further comprising heating a mixture of said bismaleimide compound of the formula (I) and said aromatic amine resin of the formula (II) at a temperature of from 70 to 220°C for from 10 to 180 minutes to partially cure said mixture to form a prepolymer.

Inventors: OHTA, MASAHIRO, YAMAGUCHI, AKIHIRO, YAMAYA, NORIMASA
Applicants: MITSUI TOATSU CHEMICALS, INC.
Application year: 1989
Main classification: C08G73
IPC codes: C08G73