Optical recording element

Abstract: An optical recording element according to the present invention comprising: (i) a transparent substrate (1) through which light passes; (ii) a transparent low-resistance layer (2) having a specific resistance so as to prevent the adhesion of dust to the surface of the element caused by a static charge, the layer being formed on the surface, on which a light beam is incident, of the transparent substrate; and (iii) an optical thin film (3) composed of at least one layer, formed on the other surface of the transparent substrate so as to transmit light beams used for recording, erasing and playback, and reflect lights which have wavelengths different from the wavelength of the above light beams and are within a specified visible region of the spectrum. With this arrangement, lights within a specified visible region of the spectrum are reflected so that the element appears to be colored according to the wavelengths of the reflected lights. Also, a problem often found in a conventional optical recording element having a transparent substrate of a resin material that the surface of the element is hardened by a light beam, can be solved. Even if a static charge is generated on the surface of such an element, the conductive transparent low-resistance substrate can eliminate the static charge outward whereby a static charge is less likely to be accumulated and the surface can be kept clean in order to improve the reliability.

Description: FIELD OF THE INVENTION The present invention relates to an optical recording element for use in optically recording, erasing and playing back information such as optical disks, optical memory cards and the like. BACKGROUND OF THE INVENTION Whilst there has been an increasing need for high density memory systems capable of storing a large amount of information and being accessec at a high speed, optical recording elements capable of optically recording, erasing and playing back information begin to attract attention. Research and development especially aimed at improving DRAW (Direct Read After Write) type optical disks, rewritable optical disks and portable memory cards are expedited in order to find wide application for the octical recording elements. Conventionally, a multiple-layer construction having anit-reflection properties is widely employed in such optical recording elements. As the optical recording element of multiple-layer construction, there are known (i) optical recording elements comprising a recording medium 20 formed on one face of a transparent substrate 14, the recording medium 20 including a recording layer 11, transparent dielectnc layer 12 and reflective film layer 13 (see Fig. 5(a)); (ii) optical recording elements comprising a recording medium 21 formed on one face of the transparent substrate 14, the recording medium 21 including two transparent dielectric layers 15 and 16, and the recording layer 11 (see Fig. 5(b)); and (iii) optical recording elements comprising a recording medium 22 formed on one face of the transparent substrate 14. the recording medium 22 including two transparent dielectric layers 17 and 18, the recording layer 11, and the reflective film layer 13 (see Fig. 5(c)). These types of optical recording elements have anti-reflection properties exhibited by the interference effect of the transparent dielectnc layers 12, 15, 16, 17 and 18 respectively. In DRAW type optical recording elements, e.g. punching type optical recording elements, the anti-reflection properties achieved by the multiple-layer construction is essential for enhancing the contrast in the reproduced information and obtaining high recording sensitivity. Also, the above anti-reflection properties are required in a magneto-optical recording element which is widely known as a typical rewritable optical recording element, in order to improve the playback performance by enhancing the magneto-optical effects. The aforesaid transparent substrate 14 is made of a plastic such as polycarbonate resin, glass or the like. In particular, it is possible to produce large quantities of the substrates 14 made of a plastic at low cost by injection molding or similar methods, and therefore such substrates 14 are widely used. The recording layer 11 comprises, for example, an amorphous rare earth-transition metal thin film such as GdTbFe which is suitable for magneto-optical recording. Although the recording and playback performances of the optical recording elements can be improved by the conventional constructions, the amount of reflected light from the recording layer 11 is inevitably decreased since it is required to effectively cause the interference of light at the abovementioned transparent dielectric layers 12, 15, 16, 17 and 18. Therefore, the optical recording element having any of the above constructions suffers from the problem that it has a dark tone appearance, and shows up badly in comparison with disks in which a material having metallic lustre is used for obtaining a high reflective factor such as compact disks and video disks for playback use only; and magnetic cards having a colorful design provided thereon such as cash cards, credit cards and various prepaid cards. A further problem is that the transparent substrate 14 used in the conventional optical recording element tends to generate a static charge, as apparent from the fact that the optical recording element having the transparent substrate 14 of polycarbonate resin shows a specific resistance of approximately 1 x 10 16 Ω·cm on the surface thereof. Since the surface of the transparent substrate 14 attracts dust because of the static charge, noise is generated and the reliability of the optical recording element deteriorates. Japanese published patent application JP-A-62 167637 discloses an optical recording medium having a recording layer of the kind which is selectively converted from an initial colored state to a decolored state by the application of laser light. The sensitivity of the medium is enhanced by a multi-layered film between a substrate of the medium and the recording layer on the light incident side of the latter, this film increases a light interference effect at the operative wavelength by strengthening the light reflected at the upper boundary of the recording layer, and the layer thicknesses in the multi-layer film are set to achieve this effect. JP-A-60-138 749 discloses an optical disc in which reflection preventing films are prodived on a light incident surface and a rear surface of a tranparent substrate. According layer, which may be a reflecting film, is provided on the rear side reflection preventing film. The present invention aims to provide an optical recording element which can reflect light at wavelengths in a specified visible region of the spectrum in order to make the optical recording element look colorful without adversely affecting its characteristics at the operational wavelength. According to the present invention, there is provided an optical recording element according to claim 1. With the above arrangement. the reflected light in said given visible region of the spectrum causes the surface of the element to appear to be colored according to the wavelengths of the reflected lights, and the cisadvantage of a dark appearance can be thus overcome. On the other hand, light beams used for the recording, erasing and playback of information pass through the optical recording element, and therefore there is no fear of damaging the functions of recording, erasing and playback. In the element of the invention the optical thin film layer is disposed on the light incident side of the substrate. In such an arrangement if the thin film layer is made of inorganic material, hardening of the substrate surface by the incident light beam is inhibited. A secondary aim of the invention is to inhibit the generation of a surface static charge on the recording element so as to prevent the adhesion of dust to the surface, thereby increasing the reliability of the element. Accordingly, in a preferred embodiment the transparent substrate has a surface resistance of 1 x 10 6 Ω·cm or less, and there is provided a protective layer formed on the face of the recording medium remote from the transparent low-resistance substrate. Having a low specific resistance, i.e., 1 x 10 8 Ω·cm or less, the transparent low-resistance substrate in the above arrangement is electrically conductive. More specifically, when a static charge is generated on the optical recording element, the transparent low-resistance substrate can transmit the static charge outward thereby to prevent the accumulation of static charges and the adhesion of oust to the surface of the transparent low-resistance substrate. Consequently, noise can be reduced. Embodiments of the invention will now be described by way of example with reference to the accompanying drawings, in wnich:- Fig. 1 is a sectional view of an optical recording element according to the present invention; Fig. 2 is a graph showing the dependence of the reflectivity on the wavelength at the optical recording element in the respective cases in which the optical recording element has a transparent dielectric thin film laminated layer of bi-layer construction and in which it has a transparent dielectnc thin film laminated layer of quadri-layer construction; Fig. 3 is a graph showing the dependence of the reflectivity on the wavelength at the surface of the optical recording element having a transparent dielectric thin film laminated layer of the quadri-layer construction when the thickness only of a low refractive index dielectric thin film is changed more or less from the value of the thickness thereof obtained by the equation (1); Fig. 4 is a vertical sectional view illustrating the structure of some of the layers of an optical recording element according to another embodiment, which has a low specific resistance, and Figs. 5(a) to (c) are sectional views respectrvely showing different multiple-layer anti-reflection constructions of a conventional optical recording element Referring to Fig. 1, an optical recording element of the present invention, comprises a transparent substrate 1 through which light beams utilized for the recording, erasing, playback of information pass; recording medium 2 formed on one face of the transparent substrate 1; and a transparent dielectric thin film laminated layer 3 formed on the other face of the transparent substrate 1. Like conventional optical recording elements, the recording medium 2 has a construction for anti-reflection, in which transparent dielectnc layers, a reflective film layer and a recording layer are formed in combination. The transparent dielectric thin film laminated layer 3 includes high refractive index dielectric thin films 3a which are optical thin films having a refractive index higher than that of the transparent substrate 1, and low refractive index dielectric thin films 3b having a refractive index lower than that of the transparent substrate 1. These high refractive index dielectnc thin films 3a and low refractive index dielectric thin films 3b are alternately laminated forming N layers, such that the first layer, as viewed from the side on which light beams used for the recording, erasing and playback are incident, is the high refractive index dielectric thin film 3a. Accordingly, the high refractive index dielectric thin film 3a is formed at the odd layers and the low refractive index dielectric thin film 3b at the even layers. The thicknesses of the high refractive index dielectric thin film 3a and the low refractive index dielectric thin film 3b are respectively given by: n k d k = λ 2 m (m = 1, 2, 3 ···) where n k : the refractive index of the k-th transparent dielectnc thin film as counted from the side on which a light beam is incident. d k : the thickness of the k-tn transparent dielectric thin film. λ : the wavelength of light beams used for recording, erasing and playing back information. With the above arrangement, due to the interference effect of the multiple-layers, the reflectivity of the optical recording element of multiple-layer construction for wavelength λ is equivalent to that of the optical recording element wherein neither the high refractive index dielectric thin film 3a nor low refractive index dielectric thin film 3b are provided. In other words, the reflectivity for the incident light beam of the wavelength λ is the minimum value. Also, the amount of reflected light becomes large when light having other wavelengths than the above wavelength λ is incident on the optical recording element, and therefore the optical recording element has colors corresponding to the wavelengths of the reflected light. More concretely, when employing ZnS (the refractive index n = 2.39) as the high refractive index dielectric thin film 3a; MgF 2 (the refractive index n = 1.39) as the low refractive index dielectric thin film 3b; polycarbonate (the refractive index n = 1.585) as the transparent substrate 1, and setting the wavelength λ of the light beams used for recording, erasing and playback to 780 nm, the thicknesses of the ZnS layer and MgF 2 layer are respectively octained using the above equation (1). The thickness t zns of the Zns layer and the thickness T MgF2 of the MgF 2 layer are approximately 163 nm and 281 nm respectively. Under the above condition, the dependence of the reflectivity on the wavelength at the surface of the optical recording element is observed in the respective cases that the transparent dielectric thin film laminated layer 3 is composed of two layers (i.e. in the case of N = 2 in Fig. 1) and composed of four layers (i.e. in the case of N = 4 in Fig. 1). As shown in Fig. 2, in both cases, the reflectivity is the minimum value R 0 at the waveiength of 780 nm, and is high at the wavelength which Is in the vicinity of 520 nm (the reflectivity of the optical recording element having no transparent dielectric thin film is also the value R 0 at the wavelength of 780 nm). Hence, the light beams used for recording, erasing and playback pass through the transparent substrate 1 without being reflected so as to reach the recording film, while lights (in this case, the lights whose wavelength is in the vicinity of 520 nm) having other wavelengths than that of the above light beams do not pass through the transparent substrate 1 but are reflected thereat. As a result, an optical recording element whose appearance is in yellow tone can be obtained without damaging the recording, erasing and playback functions of the optical recording element. It often occurs that the surface of the transparent substrate 1 is hardened by incident light beams, when the transparent substrate 1 is of a resin material. but such a drawback can be avoided in this embodiment wherein an inorganic transparent dielectric thin film is laminated on the surface of the transparent substrate 1. When the thickness of the MgF 2 layer serving as the low refractive index dielectric thin film 3b more or less differs from the value obtained by the foregoing equation (1) (e.g. t MgF2 = 100 nm) and the transparent dielectric thin film laminated layer 3 is of quadari-layer construction (i.e. in the case of N = 4 in Fig. 1), the dependence of the reflectivity on the wavelength at the surface of the optical recording element is observed. As shown in Fig. 3, not only is the wavelength region at which the reflectivity of the cptical recording element is high wider compared with that in the first example shown in Fig. 2, but the reflectivity at the wavelength of 780 nm is lower than the minimum value R 0 . Therefore, the adverse influence of light reflected at the surface of the optical recording element in the course of recording, erasing or playback operation can be reduced. In the above examples, transparent dielectric thin films which are optical thin films are laminated to form a multiple-layer construction, whereby the light beams used for recording, erasing and playback pass therethrough due to the interference effect, while lights having wavelengths within a specified visible region of the spectrum, different from the wavelength of the above light beams are reflected thereat. Also, it is to be understood that the transparent dielectric thin film laminated layer 3 is not limited only to the alternate layers of ZnS and MgF 2 , but other materials may be employed in combination selecting from materials such as Sb 2 S 3 , TiO 2 , CdS, CeO 2 , PbCℓ 2 , WO 3 , SiO, Aℓ 2 O 3 , SiO 2 , CaF 2 , LiF, NaF, AℓN, SiN, etc. so as to satisfy the aforementioned relation between two materials regarding the refractive index. In the case of conventional optical recording element having the transparent substrate made of polycarbonate resin or the like, the specific resistance at the surface of the transparent substrate is very high i.e. 1 × 10 16 Ω · cm and therefore a static charge is likely to be generated, causing dust to adhere to the surface thereof. This is one of the reasons for deteriorating the reliability of the optical recording element. In order to overcome such a drawback, another optical recording element according to the present invention comprises (i) the transparent substrate 1; (ii) the recording medium 2 formed on one face of the transparent substrate 1; (iii) a protective layer 9 for protecting the recording medium 2, formed on the surface of the recording medium 2, the surface being opposite to the side at which the transparent substrate 1 is formed: and (iv) a coating layer 4 formed on the other face (on which a light beam is incident) of the transparent substrate 1. Incidentally, in this embodiment. parts that are substantially equivalent or function substantially similarly to those in the first embodiment are indicated by the same reference numerals for convenience of explanation and the description thereof is omitted. The material of the transparent substrate 1 is not limited, but any material so long as it is light-permeable like plastics such as polycarbonate resin, and glass. The recording medium 2 may have at least one of functions such as optical recording, playback and erasing operation. The coating layer 4 comprises a transparent conductive coating of a transition element oxide such as SnO 2 , In 2 O 3 and CdO, and is 50 to 600 nm in thickness. This coating layer 4 permits the transparent low-resistance substrate 5 composed of the transparent substrate 1 and the coating layer 4 to have a specific resistance of 1 × 10 6 Ω·cm or less which is lower compared with the case in which no coating layer 4 is provided. A transparent dielectric thin film layer corresponding to layer 3 of the earlier embodiments is also provided in the Figure 4 embodiment though it is not shown. In the case that the optical recording element has the construction shown in Fig. 1, the coating layer 4 is formed on that face of the transparent dielectric thin film laminated layer 3 on which the light beam is incident. In the case that the optical recording element has the transparent dielectric thin film laminated layer 3 (shown in Fig. 1) formed between the transparent substrate 1 and the recording medium 2. the coating layer 4 is formed on that face of the transparent substrate 1 on which the light beam is incident. The following description descnbes the manufacturing method of the optical recording element having the coating layer 4. For producing the optical recording element, the coating layer of SnO 2 or the like having a thickness of about 100 nm is deposited on one face of the transparent substrate 1 made of polycarbonate resin (or the transparent dielectric thin film laminated layer 3) by means of sputtenng or other method. Then, the other face of the transparent substrate 1 is provided with the recording medium 2 composed of an amorphous rare earth-transition metal thin film such as GdTbFe and the protective layer 9 is further covered thereon. The method for forming the coating layer 4 is not limited to the sputtering but may be a heat decomposition method for instance, so long as the coating layer 4 having a thickness from 50 nm to 600 nm can be obtained with it. Also, the coating layer 4 may be formed after depositing the recording medium 2 and the protective layer 9. As decribed above, since the transparent low-resistance substrate 5 compnses the coating layer 4 formed on one face of the transparent substrate 1, the coating layer 4 being composed of the transparent conductive coating, and the specific resistance at the surface of the transparent low-resistance substrate 5 is not more than 1 × 10 6 Ω · cm, even if a static charge is generated on the optical recording element, the static charge will be eliminated outward by the transparent low-resistance substrate 5. Accordingly, the optical recording element is less likely to generate a static charge and attract dust. As a result, the surface of the transparent low-resistance substrate 5 can be kept clean, thereby reducing noise to be generated when recording, playing back or erasing information. In this embodiment, the transparent low-resistance substrate 5 comprises the transparent substrate 1 and the coating layer 4 composed of the transparent conductive coating, the coating layer 4 being formed on the transparent substrate 1, but the transparent low-resistance substrate 5 is not limited to the above construction. It may be composed of conductive glass which contains V 2 O 3 , WO 3 , MoO 3 , TiO 2 , Fe 2 O 3 or others. More specifically, the noise can be reduced so long as the transparent low-resistance substrate 5 is light permeable and the specific resistance at the surface thereof is in the range from more than 0 Ω · cm to 1 × 10 6 Ω · cm.

Claims: An optical recording element on which data can be recorded, erased and/or played back using light of a predetermined wavelength incident on one side thereof, the element comprising a transparent substrate (1), a magneto-optic recording medium (2) having itself and anti-reflection construction supported on the side of the substrate opposite the light incident side, and an optical thin film layer (3) disposed on the light incident side of said substrate so as to transmit the incident light of said predetermined wavelength to the recording medium, wherein said optical thin film layer (3) consists of one more first thin films (3a) and one or more second thin films (3b) laminated alternately with said one or more first thin films, the or each first thin film (3a) of the thin film layer having a higher refractive index than that of said transparent substrate and the or each second thin film (3b) of the thin film layer having a lower refractive index than that of said transparent substrate; the film thicknesses in the optical thin film layer being such that due to the interference effect thereof said optical thin film layer has minimum reflectance at said predetermined wavelength, and reflects incident light at wavelenghts which are different from said predetermined wavelength and which lie within a given visible region of the spectrum, in order to give the element a colourful appearance. An optical recording element according to claim 1, wherein the or each first thin film is made of ZnS and the or each second thin film is made of MgF 2 . An optical recording element according to claim 1 or claim 2, wherein the materials for said first and second thin films are inorganic transparent dielecttic materials selected from 1) sulfides such as Sb 2 S 3 and CdS; 2) oxides such as TiO 2 , CeO 2 , WO 3 , SiO, Aℓ 2 O 3 and SiO 2 ; 3) fluorides such as CaF 2 , LiF and NaF; 4) nitrides such as SiN and AℓN; and 5) chlorides such as PbCℓ 2 , so as to satisfy the specified relationship between the refractive indices of said first and second thin films and of said transparent substrate. An optical recording element according to any preceding claim, wherein each thin film (3a,3b) is a transparent dielectric thin film. An optical recording element according to any preceding claim, wherein each thin film has a refractive index and thickness of which the product is an integral multiple of one half of said predetermined wavelength of the light which is to be transmitted by the optical thin film layer (3). An optical recording element according to any of claims 1 to 4, wherein the or each of said first thin films (3a) has a refractive index and thickness of which the product is an integral multiple of one half of said predetermined wavelength of the light which is to be transmitted by the optical thin film layer (3), and the or each of said second thin films (3b) has a thickness which differs from that value of which the product with the refractive index is a said integral multiple. An optical recording element according to any preceding claim, further comprising a transparent low-resistance layer (4) having a specific resistance so as to prevent the adhesion of dust to the surface of the element caused by a static charge, said layer being formed on the light incident side of the transparent substrate. An optical recording element according to any of claims 1 to 6, wherein said transparent substrate has a surface resistance of 1 x 10 6 Ω·cm or less, and wherein there is provided a protective layer (9) formed on the face of the recording medium (2) remote from the transparent low-resistance substrate. An optical recording element according to claim 8, wherein said transparent low-resistance substrate (5) comprises a transparent substrate (1) and a coating layer (4). An optical recording element according to claim 9, wherein the coating layer (4) comprises a transparent conductive coating of a transition element oxide such as SnO 2 , In 2 O 3 and CdO, and has a thickness of 50 nm to 600 nm. An optical recording element according to claim 8, wherein the transparent low-resistance substrate is of conductive glass including one or more oxides. An optical recording element according to claim 11, wherein said one or more oxides is/are selected from the group consisting of V 2 O 3 , WO 3 , MoO 3 , TiO 2 and Fe 2 O 3 . An optical recording element according to any preceding claim, wherein said transparent substrate is made of plastic such as polycarbonate resin, or glass.

Inventors: ISHIKAWA TOSHIO, KATAYAMA HIROYUKI, MIYAKE TOMOYUKI, NAKAYAMA JUNICHIRO, OHTA KENJI, VAN KAZUO, YAMAOKA HIDEYOSHI, ISHIKAWA, TOSHIO, KATAYAMA, HIROYUKI, MIYAKE, TOMOYUKI, NAKAYAMA, JUNICHIRO, OHTA, KENJI, VAN, KAZUO, YAMAOKA, HIDEYOSHI
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1989
Main classification: G11B7
IPC codes: G11B7