METHOD FOR PRODUCING SEMICONDUCTIVE SINGLE CRYSTAL

Abstract: A n-type ZnSe thin layer is prepared by heating a ZnSe single crystal substrate in a hydrogen atmosphere under a pressure of from 0.1 Torr. to 10 Torr. at a temperature of from 250°C to 450°C while supplying a gaseous organozinc compound, H₂Se gas and a gaseous organoaluminum compound in such amounts that a molar ratio of Se/Zn is from 10 to 100 and a molar ratio of Al/Zn is from 0.02 to 0.07 to grow the aluminum-doped ZnSe thin film on the ZnSe single crystal substrate.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method for producing a semiconductive single crystal. More particularly, the present invention relates to a method for producing a thin film of aluminum-doped ZnSe single crystal which is epitaxially grown on a ZnSe single crystal substrate by the MOCVD method. Description of the Related Art Presently, LEDs for emitting infrared, red, orange, yellow and green light are available. However, none of the practically used LEDs can emit blue light. To emit the blue light, a band gap should be larger than 2.5 eV. Hitherto, many materials such as GaN, SiC and GaAlN have been proposed as materials of the blue light emitting LED. However, none of these materials has been able to provide a practically usable blue light emitting LED. Since ZnSe has a band gap of 2.7 eV which is a direct transition type, it is one of promising materials of the blue light emitting LED. However, many problems should be solved before ZnSe is used as the material of the blue light emitting LED. To produce LED, a p-n junction should be formed. To this end, a p-type thin film should be formed on a n-type substrate with low resistance, or a n-type thin film should be formed on a p-type substrate with low resistance. However, the ZnSe crystal as such is an n-type semiconductive material with high resistance. For example, the ZnSe crystal has resistivity of 10⁸ ohm.cm to 10⁹ ohm.cm. Therefore, the ZnSe crystal as such cannot be used as the substrate of LED. Then, it is proposed to convert a bulk single crystal of ZnSe to the n-type one with low resistance through doping the ZnSe single crystal with impurities. In addition, to form the p-n junction, the p-type film is also required. However, it was believed that any p-type ZnSe could be prepared. Recently, the growth of the p-type ZnSe through Li-doping was reported by J. Nishizawa et al, "Blue Light Emission from ZnSe p-n Junctions", J. Appl. Phys., 57 (6), 2210-2216 (1985). But, the reported method has unsatisfactory reproducibility and the p-type ZnSe cannot be obtained easily. The most fundamental problem resides in the production of a ZnSe bulk single crystal. Namely, a large ZnSe bulk single crystal with high purity has not been produced. Since ZnSe is easily sublimated, it cannot be melt by simply heating it under atmospheric or moderately pressure. However, it can be melt under high pressure of about 8x10⁶Pa (80 atm.) or higher. The melting point of ZnSe is reported to be about 1,520°C, but this melting point is measured under such high pressure. To produce the ZnSe single crystal, many methods such as a high pressure melting method, an iodine transporting method, a solution growth method, a sublimation method and the Piper method have been attempted. The first two methods can produce a comparatively large single crystal although the singly crystal contains a large amount of impurities and has many defects. The latter three methods produce a small single crystal, so that they are not practically applied. Further, the single crystal produced by these three methods has insufficient purity. Since a large ZnSe single crystal with good quality cannot be produced by those conventional methods, many attempts have been made to epitaxially grow the n-type ZnSe thin layer on a GaAs substrate. Since the technique for growing the GaAs single crystal has been established, a large GaAs single crystal having less defects can be grown. Fortunately, difference of the lattice constants between GaAs and ZnSe is small. The epitaxial growth of ZnSe/GaAs is disclosed by, for example, W. Stutivs, Appl. Phys. Lett., Vol. 38 (1981) 352 and K. Ohkawa et al, J. Appl. Phys. Vol. 62 (1987) 3216. However, since the ZnSe/GaAs junction is a junction between the different materials, it has some drawbacks such as follows: 1. Although the lattice constants of both materials are close at room temperature, they have different coefficients of thermal expansion. Since the ZnSe film is grown on the GaAs substrate is at high temperature and cooled to room temperature, stress is generated in the thin film due to the difference of coefficients of thermal expansion between two materials. Since the stress is surprisingly large, deterioration caused by stress lead to unsatisfactory electrical characteristics. 2. The impurities migrate from the substrate. For example, Ga atoms migrate from the substrate into the ZnSe thin film to form n-type impurities. Depending on the degree of migration, a carrier concentration varies. These drawbacks are common to the heteroepitaxy. To overcome these drawbacks, it may be contemplated to grow ZnSe on the ZnSe substrate. Hitherto, no ZnSe single crystal with good quality could have been obtained. Only one paper, namely P. Blammonnier et al, J. Appl. Phys. Vol. 52 (1981) 6895 reported the ZnSe/ZnSe epitaxy. Blammonnier et al grew the ZnSe thin film on the ZnSe substrate by the iodine transporting method or the Piper method. According to Blammonnier et al, the ZnSe thin film formed by the iodine transporting method contains many iodine atoms as impurities. In the photoluminescence measurement, strong emission due to excitons constrained with neutral donor impurities is observed. This is due to the presence of the iodine atoms. The contamination with the iodine atoms is an expected consequence since the iodine transporting method utilizes the following reaction: ZnSe + I₂ ⇄ ZnI₂ + 1/2Se. The Piper method is one of the sublimation methods. The ZnSe thin film grown by this method has a strong emission line from excitons constrained with deep neutral accepters. According to Blammonnier et al, the ZnSe thin film was formed by the MOCVD method using dimethylzinc [Zn(CH₃)₂] and H₂Se as raw materials at the substrate temperature of 500°C. The ZnSe thin film formed on the ZnSe substrate had a strong emission line from excitons constrained with the neutral donors. This can be attributed to the Ga atoms, which generated a deep donor impurity level. Blammonnier et al assumed that Ga might be contained in dimethylzinc. Although they did not intend to dope the impurities in the ZnSe single crystal, the Ga atoms were accidentally contained as the impurity. In the prior arts, no report has been made on the epitaxial growth of a thin film of ZnSe doped with the n-type impurity on the ZnSe substrate. SUMMARY OF THE INVENTION An object of the present invention is to provide a method for epitaxially growing an aluminum-doped ZnSe thin film on a ZnSe single crystal. Accordingly, the present invention provides a method for growing an aluminum-doped ZnSe thin film which comprises the steps of: (i) placing a piece of a ZnSe polycrystal in a sealed reactor tube having an atmosphere of at least one gas selected from the group consisting of an inert gas, nitrogen and H₂Se kept at a pressure of 13-13,332 Pa (from 0.1 Torr to 100 Torr), (ii) moving the reactor tube containing the piece of ZnSe polycrystal through a low temperature first zone kept at a temperature of from room temperature to 100°C, a temperature-raising second zone having a temperature gradient of from 50°C/cm to 200°C/cm, a high temperature third zone kept at a temperature of from 700°C to 900°C, a temperature-lowering fourth zone having a temperature gradient of from -200°C/cm to -50°C/cm and a low temperature fifth zone kept at a temperature of from room temperature to 100°C in this order at a moving rate of from 0.05 mm/day to 5 mm/day while keeping the solid state of the ZnSe material whereby the ZnSe polycrystal is converted to a ZnSe single crystal, (iii) cutting the ZnSe single crystal to yield a ZnSe single crystal substrate, and (iv) heating the ZnSe single crystal substrate in a hydrogen atmosphere under a pressure of 13-1333 Pa (from 0.1 Torr to 10 Torr) at a temperature of from 250°C to 450°C while supplying a gaseous organozinc compound, H₂Se gas an a gaseous organoaluminium compound in such amounts that the molar ratio of Se/Zn is from 10 to 100 and the molar ratio of Al/Zn is from 0.02 to 0.07 to grow the aluminium-doped ZnSe thin film on the ZnSe single crystal substrate. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 schematically shows an apparatus for carrying out the method of the present invention, Fig. 2 is a graph showing a relationship between resistivity and the Al/Zn molar ratio when the ZnSe thin layer is grown on the ZnSe single crystal substrate according to the present invention, Fig. 3 shows the results of photoluminescence of the ZnSe thin layer when the Al/Zn molar ratio is 0, 0.035, 0.052 or 0.069, and Fig 4 schematically shows the RTHM (Recrystallization Traveling Heater Method) for producing the ZnSe single crystal substrate. DETAILED DESCRIPTION OF THE DRAWINGS The present invention should be clearly distinguished from the method of Blammonnier et al described above in the following points: 1. In the method of Blammonnier et al, the ZnSe thin film was of n-type through the accidental Ga doping, while according to the present invention, aluminum is intentionally doped as the n-type dopant. Although Ga and Al are both n-type impurities, they have big differences. For example, Ga generates a deep donor level so that the electron constrained with the donor cannot be easily raised to a conduction band. That is, at the higher temperature, the electrons can hardly provide free carriers. On the contrary, Al generates a comparatively shallow donor level. Therefore, the electron of aluminum can be easily shifted up to the conduction band, namely aluminum can easily provide a free electron. This achieve the purpose to lower the resistance. The carrier concentration, namely the electron concentration, increases in proportion to the donor concentration. This is true for the shallow donor level. In case of the deep donor level, the free carriers cannot be provided unless the temperature is raised to considerably high. 2. Another difference is the possibility to control the carrier concentration. Blammonnier et al tried to produce the non-doped ZnSe thin film but Ga was accidentally doped. Such is not suitable for the industrial application. Since a desired range of resistivity is determined beforehand, the amount of the dopant should be controlled to achieve this range. According to the present invention, the aluminum-doped ZnSe thin film is formed on the ZnSe substrate by the MOCVD method. One of the characteristics of the present invention resides in the substrate. Without the large area substrate having high purity, ZnSe cannot be epitaxially grown on the substrate. The method for the production of the ZnSe single crystal is described in japanese Patent Kokai Publication No. 230599/1988 (Patent Application No. 65389/1987 filed on March 18, 1987). This method will be illustrated with making reference to Fig 4. The ZnSe polycrystal having a suitable size can be produced by the conventional CVD or sintering method. From the polycrystal bulk, a rod is cut out. The polycrystal rod is placed in a reaction tube, for example a quartz capsule. Then, the tube is filled with at least one gas selected from the group consisting of an inert gas, nitrogen and H₂Se, and sealed. The amount of the gas is so adjusted that the inner pressure reaches 13-13.332 Pa (0.1 Torr. to 100 Torr.) during heating. Then, the reactor tube is heated. The temperature distribution to be achieved by a heater is shown in Fig. 4 by the line A-B-C-D-E-F. A low temperature first zone corresponding to the line A-B is kept at a temperature of from room temperature to 100°C. A temperature-raising second zone corresponding to the line B-C has a temperature gradient of from 50°C/cm to 200°C/cm. A high temperature third zone corresponding to the line C-D is kept at a temperature of from 700°C to 900°C. The length of the third zone (C-D) is made as short as possible, for example 5 mm to 20 mm. A temperature-lowering fourth zone corresponding to the line D-E has a temperature gradient of from -200°C/cm to -50°C/cm. Finally, a low temperature fifth zone corresponding to the line E-F is kept at a temperature of from room temperature to 100°C. The reactor tube is passed from the first zone to the fifth zone at a rate of from 0.05 mm/day to 5 mm/day while keeping the solid state of the ZnSe material. Since only the zone C-D is kept at the high temperature, the ZnSe polycrystal is converted to a ZnSe single crystal. The temperature is not higher than 900°C even in the high temperature third zone, ZnSe is not sublimated and keeps the solid state. In Fig. 4, the zones are vertically arranged, although they may be horizontally or slantwise arranged. Preferably, the ZnSe polycrystal is of a thin long rod, since a very limited part should be locally heated. For example the rod has a diameter of from 3 to 30 mm. Since the crystal is moved relatively to the heater, this method is a kind of the traveling heater methods. Since the polycrystal is converted to the single crystal through rotation of crystalline grains, this method is in the category of recrystallization. Then, the above method for converting the polycrystal to the single crystal can be named as "Recrystallization Traveling Heater Method (RTHM). Another characteristic of the present invention resides in the molar ratio of aluminum to zinc (Al/Zn). Aluminum is doped to generate the shallow donor level so that as many as possible electrons are present in the crystal as the free carriers and in turn the resistivity is decreased. In case of silicon (Si), B, P or As is doped to produce the p- or n-type one. In this case, the carrier density is exactly proportional to the amount of the impurity. As the doping amount increases, the free carrier density increases and the electrical resistance decreases. In case of GaAs, such relation can be established. However, when aluminum is doped in the ZnSe thin film, the carrier concentration is not simply proportional to the amount of the dopant. Then, the amount of aluminum to be doped should be controlled. According to the present invention, the molar ratio of Al to Zn is from 0.02 to 0.07. Now, the method of the present invention will be explained in detail. As the substrate, a wafer of the ZnSe single crystal which is produced by the above described RTHM is used. Any plane of the single crystal may be used. For example, the (100), (110) or (111) plane can be used, although other planes can be used. The temperature of the substrate is usually from 250°C to 450°C, preferably from 300°C to 400°C. As the zinc source, any of organozinc compounds may be used. Preferred examples of the organozinc compounds are dimethylzinc [Zn(CH₃)₂] and diethylzinc [Zn(C₂H₅)₂]. As the selenium source, H₂Se is used. As the aluminum source, any of organoaluminum compounds may be used. Preferred examples of the organo-aluminum compounds are trimethylaluminum [Al(CH₃)₃] and triethylaluminum [Al(C₂H₅)₃] are preferably used. To obtain the epitaxially grown film with good quality, the molar ratio of selenium to zinc (Se/Zn) is from 10 to 100. By making reference to Fig. 1, the MOCVD apparatus for carrying out the method of the present invention will be illustrated. In Fig. 1, the apparatus is placed horizontally, although a vertically arranged apparatus can be used in the present invention. Since the MOCVD apparatus is well known in the art, it will be briefly explained. A CVD furnace 1 consists of a vessel which can be evacuated. In the furnace 1, a suscepter 2 is installed. On the suscepter 2, a ZnSe substrate 3 is horizontally placed, and below the suscepter 2, a heater 4 is arranged. By the heater 4, the suscepter 2 and then the substrate 3 are heated at a desired temperature. The furnace 1 is evacuated with a rotary pump 10 and further with anoil diffusion pump through a main valve 6 and a trap 7 cooled with liquid nitrogen. With a vacuum gauge 5, a degree of high vacuum in the furnace 1 is monitored. A trap 11 is used to remove the impurities and the like. The degree of vacuum during evacuating the furnace 1 with the rotary pump 10 is roughly indicated by a Geissler tube 13. Cylinders 21, 22 and 23 contain helium gas containing 0.16 % of dimethylzinc, hydrogen gas containing 10 % of H₂Se and pure hydrogen gas, respectively. The pure hydrogen gas is used as an atmospheric gas to keep the pressure in the furnace at 13-1333Pa (from 0.1 Torr to 10 Torr). The dimethylzinc-containing helium is supplied into the CVD furnace 1 from a gas inlet 28 through a regulator 24, a mass-flow controller 25, a cutting valve 26 and a valve 27. The H₂Se-containing hydrogen gas and triethylaluminum gas are supplied into the CVD furnace 1 in the similar way. As already described, the substrate temperature is adjusted at a temperature of from 250°C to 450°C, the Al/Zn ratio and the Se/Zn ratio are controlled to be from 0.02 to 0.07 and from 10 to 100, respectively. Under the above conditions, the aluminum-doped ZnSe thin film is formed on the substrate through the gas phase reaction. The thickness of the aluminum-doped ZnSe thin film can be adjusted by the reaction time. Usually, the thickness is from 0.001 to 10 µm, preferably from 0.1 to 1 µm. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be illustrated further in detail by following Examples. Example From the ZnSe single crystal mass produced by the RTHM method, a wafer having the (110) plane on the surface was cut out and etched with a boiling 25 % aqueous solution of sodium hydroxide. Then, the wafer was treated in a hycrogen stream under several ten Torr. at 500°C for several minutes to clean the surface. As the zinc source, the helium gas containing 0.16 % of dimethylzinc was used. As the selenium source, the hydrogen gas containing 10 % of H₂Se was used. As the aluminum source, triethylaluminum was used. After evacuating the CVD furnace to 0.013 mPa (10⁻⁷ Torr.), ZnSe was grown on the wafer surface under following conditions: The reason why the flow rate of trimethylaluminum was varied is to find the optimum flow rate Fig. 2 shows the relationship between the resistivity (ohm.cm) of the grown ZnSe thin film having a thickness of 1.4 µm and the Al/Zn-molar ratio. The resistivity of the substrate was 10⁸ ohm.cm. When the doped amount of aluminum was zero (0), the resistivity of the ZnSe thin film was about 3 x 10³ ohm.cm. This resistivity might be due to the presence of aluminum which may be contained in the zinc source gas or liberated from the wall of the furnace and accidentally doped. As the supplied amount of aluminum is increased, the resistivity decreased. At the Al/Zn molar ratio of about 5.1 x 10⁻², the resistivity decreased to the minimum value of about 10⁻¹ ohm.cm. In this case, the carrier concentration was 10 cm²/V.sec. As the supplied amount of aluminum is further increased, the resistivity increases. The reason for such increase of resistivity has not been clarified. From the above results, it is understood that the resistivity of the ZnSe thin film is made lower than 10 ohm.cm when the Al/Zn molar ratio is in the range from 0.02 to 0.07. Fig. 3 shows the results of photoluminescence measurement of the epitaxially grown ZnSe thin films. The photoluminescence measurement was carried out by exciting the thin layer with the He-Cd laser, splitting the luminescence light and measuring the intensity of said light at 4.2 K. Fig. 3 includes the results for the Al/Zn molar ratios of 0 (zero), 3.5 x 10⁻², 5.2 x 10⁻² and 6.9 x 10⁻². The peaks indicated as "I₂ A " correspond to the emission from the excitons constrained with the neutral donor impurities. Even in case of the undoped ZnSe film, this peak was observed since aluminum was accidentally doped. The wavelength at which the I₂ A peak is observed is the same for all the aluminum concentrations. At the Al/Zn molar ratio of 6.9 x 10⁻², the SA emission was strong. This phenomenon corresponds to the turbulence of the sites at which the aluminum atoms were introduced or increase of the number of vacant lattices of zinc. According to the present invention, the thin film of the n-type ZnSe single crystal is formed by epitaxially growing the aluminum-doped ZnSe thin film on the ZnSe substrate. Thereby, the n-type ZnSe thin film having the resistivity of as low as 10⁻¹ ohm.cm and the electron concentration of as high as 10¹⁸ cm⁻³ can be produced. Since the ZnSe thin film is homoepitaxially formed, it does not suffer from stress due to the difference of thermal expansion between the substrate and the thin film or the problems caused by the impurities which migrate from the substrate to the thin film. The ZnSe thin film can be used as an n-type layer in the blue light-emitting diode.

Claims: 1. A method for growing an aluminium-doped ZnSe thin film which comprises the steps of: (i) placing a piece of a ZnSe polycrystal in a sealed reactor tube having an atmosphere of at least one gas selected from the group consisting of an inert gas, nitrogen and H₂Se kept at a pressure of 13-13,332 Pa (from 0.1 Torr to 100 Torr), (ii) moving the reactor tube containing the piece of ZnSe polycrystal through a low temperature first zone kept at a temperature of from room temperature to 100°C, a temperature-raising second zone having a temperature gradient of from 50°C/cm to 200°C/cm, a high temperature third zone kept at a temperature of from 700°C to 900°C , a temperature-lowering fourth zone having a temperature gradient of from -200°C/cm to -50°C/cm and a low temperature fifth zone kept at a temperature of from room temperature to 100°C in this order at a moving rate of from 0.05 mm/day to 5 mm/day while keeping the solid state of the ZnSe material whereby the ZnSe polycrystal is converted to a ZnSe single crystal, (iii) cutting the ZnSe single crystal to yield a ZnSe single crystal substrate, and (iv) heating the ZnSe single crystal substrate in a hydrogen atmosphere under a pressure of 13-1333 Pa (from 0.1 Torr to Torr) at a temperature of from 250°C to 450°C while supplying a gaseous organozinc compound, H₂Se gas and a gaseous organoaluminium compound in such amounts that the molar ratio of Se/Zn is from 10 to 100 and the molar ratio of Al/Zn is from 0.02 to 0.07 to grow the aluminium-doped ZnSe thin film on the ZnSe single crystal substrate. 2. The method according to claim 1, wherein the organozinc compound is dimethylzinc and/or diethylzinc. 3. The method according to claim 1, wherein the organoaluminium compound is trimethylaluminium and/or triethylaluminium. 4. The method according to claim 1, wherein the ZnSe single crystal substrate has the (100) plane, the (110) plane or the (111) plane on its surface.

Inventors: NANBA, HIROKUNI C/O OSAKA WORKS OF SUMITOMO, TAGUCHI, TSUNEMASA
Applicants: PRODUCTION ENGINEERING ASSOCIATION, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1989
Main classification: C30B25
IPC codes: C30B25, H01L21, H01L33