MOLDING METHOD AND MOLDING APPARATUS BY USE OF INJECTION-COMPRESSION MOLDING MACHINE

Abstract: A molding method and an injection-compression molding machine provided with an opening/closing valve between an injection unit and a metallic mold for achieving said molding method, in which in order to make the density of molten resins uniform and thus produce stable molded products, said valve is closed to carry out the preliminary pressing within the injection unit before the molten resin is injected into the metallic mold and then the molten resin is pressed within the metallic mold during or after the injection. This molding machine is arranged in a molten resin passage (46) provided between the injection unit (10) and the metallic mold (30) so as to be opened and closed and provided with the valve (40) for closing said passage and changing a sectional area of said passage.

Description: Technical Field of the Invention The present invention relates to an injection-compression molding machine for plastic resins, and more particularly to a molding apparatus including a valve which is disposed in a flow passageway of molten resin provided between an injection unit and a metal mold of an injection-compression molding machine to perform blocking and change of a cross-section area of the aforementioned flow passageway, as well as the molding method. Background Technique of the Invention In the prior art, for instance, as disclosed in the respective specifications and drawings of Laid-Open Japanese Patent Specifications 60-21225 (1985) and 60-110419 (1985), a molding method by means of a compression molding method is achieved through the steps of pouring resin material to be molded into a heated metal mold, actuating the molding machine to press the material at a low pressure, after the molten resin material to be molded has been filled within the metal mold, once opening upper and lower metal molds a little to remove a gaseous component in the material, again pressing the material at a high pressure, continuing the pressing and the heating until the material has finished to be hardened, and thereafter taking out a molded ariticle by opening the mold. On the other hand, in injection-compression molding, when molten resin material is injected into a metal mold, an injection flow rate and an injection flow velocity of the molten resin are controlled by a moving speed of a screw and a pressing force of the screw. However, in the above-described compression molding method in the prior art, due to the fact that the pressing is effected as divided into low-pressure pressing and high-pressure pressing, a lot of man-hours are necessitated. From the EP O 244 783, a method and apparatus for injection-compression molding of thermo-plastic parts is known as well, wherein the apparatus includes a platen assembly, a toggle clamp assembly, a screw injection assembly, a hydraulic system for providing power to the toggle clamp assembly and the screw injection assembly, and a control system for controlling the hydraulic devices. Compression in this embodiment is provided by the toggle clamp assembly, and more particularly multiple stage compression of the resin to first redistribute the resin and vent the cavities and, secondly, compress the resin to compensate for cooling-induced shrinkage thereof. The GB 2138 737 also shows a method for the production of plastic article using an injection press, wherein as well the compression is divided in a first pressing and in a second pressing, provided by a moveable piston. Further, a method for pressure injection of plastic material in a two-pressure face injection cylinder has become known from CA-1059714. Said method involves the operation of a ram-screw type of plastic injection machine and includes the steps of prepressurizing the plastic material within the injection cylinder to a relative low value while the nozzle is held closed, opening the nozzle at the conclusion of a short time interval, maintaining this low pressure on the screw for a second time interval after the opening of the nozzle valve to effect a controlled injection of the plastic material under a correspondingly low pressure, then establishing a third time interval and applying and maintaining a high pressure to the screw to establish a correspondingly higher pressure in the mold cavity. This teaching is contrary to the disclosure of the references cited in said CA-1059714, i.e. in the US-patents 3,784,657 and 3,632,246 wherein it is disclosed that first plastic foam has been injected under relatively high pressure and then the injection machine has been shifted to a low pressure. The object of the teaching according to CA-1059714, however, is to assure complete filling of the mold, homogeneous foam products and prevention of shrinking of the plastic material. In addition, in the injection-compression molding, since molten resin is injected into a metal mold as varying a speed and a pressure of a screw, depending upon viscosity and elasticity of the molten resin, the responsibility would become an issue, and furthermore, in molding at a low flow resistance such as injection-compression molding, a time of injecting molten resin into a metal mold or an amount of molten resin to be molded cannot be stabilized, so that defects (short-sits, shrinks and warps) would arrive in the molded articles. Moreover, in the case where compression is commenced during injection, a flow resistance of molten resin would increase gradually, hence in the injection method in the prior art, an amount of injection would vary depending upon viscosity and elasticity of the molten resin, resulting in surplus or shortage in the amount of injection, and so, there is a shortcoming that burrs or short-sits are generated. Summary of the Invention The present invention has been worked out in view of the aforementioned circumstance, and an object of the invention is to provide a molding method which can obtain stable products within a short period of time by carrying out preliminary pressing within an injection unit before injection molten resin into a metal mold in order to make a density of the molten resin uniform and subsequently carrying out pressing of the molten resin within the metal mold during injection or after injection in an injection-compression molding machine provided with a value between an injection unit and a metal mold, and a molding apparatus for achieving the above-mentioned molding method. In other words the quality of the products is to be improved. In order to achieve the aforementioned object, according to a first aspect of the present invention, there is provided a molding method in an injection-compression molding machine including a valve disposed in a flow passageway of molten resin provided between an injection unit and a metal mold for effecting controlling resin flow area of said flow passageway, comprising the steps of: supplying a molten resin into said injection unit under a pressure; injecting a preset amount of molten resin into said metal mold through said valve; and closing said valve after completion of injection and, in conjunction therewith pressing the molten resin within said metal mold characterized in that said step of supplying the molten resin into the injection unit is performed while said valve is held in close position so as to increase the pressure within said injection unit to a relatively high value for preliminarily pressing said molten resin for uniform of density of the molten resin. According to a second aspect of the present invention, there is provided a molding method in an injection-compression molding machine according to claim 1, characterized in that the pressing on the molten resin within said metal mold is carried out from the midst of injection of the molten resin. According to a third aspect of the present invention, there is provided a molding apparatus in an injection-compression molding machine comprising: a molten resin supply means for supplying a molten resin to an injection unit; a flow passageway for supplying said molten resin from said injection unit to a metal mold; a valve means disposed in said flow passageway for adjusting a molten resin flow passageway, said valve means being operable at a fully closed position; means for controlling a valve position depending upon progress of the molding process, characterized in that said controlling means maintains said valve means at said fully closed position while the molten resin is supplied to said injection unit from said molten resin supply means so that a pressure of said molten resin in said injection unit is elevated to a given value and maintained at said given value for a predetermined period for effecting preliminary pressing for uniformity of density of said molten resin. According to a fourth aspect of the present invention, there is provided a molding apparatus in an injection-compression molding machine according to claim 3, characterized in that said valve means includes a rotary valve performing a rotary operation as actuated by a valve operating device, and there a cross-section of a flow passageway of molten resin is varied by the rotary operation of said rotary valve so as to control at least an injection flow velocity and an injection flow rate of the molten resin. According to a fifth aspect of the present invention, there is provided a molding apparatus in an injection-compression molding machine according to claim 3, characterized in that said apparatus further includes means for detecting a pressure within an injection cylinder, means for detecting a position of a screw provided within the injection cylinder, means for detecting an opening/closing speed of a metal mold, input means for setting an opening angle of a valve, input means for setting the opening/closing speed of the metal mold, input means for setting the position of the screw, means responsive to a pressure signal of the injection cylinder for generating an opening/closing signal for the valve, a valve opening/closing actuator driven by the opening/closing signal for the valve, means responsive to a position signal of the screw for generating an opening/closing speed signal for the metal mold, and a press having the metal mold mounted thereto and driven by the opening/closing speed signal for the metal mold. The above-mentioned and other objects, aspects and advantages of the present invention will become apparent for those skilled in the art from the following description showing preferred embodiments conformed to a principle of the present invention as practical examples taken in conjunction with the accompanying drawings. Brief Description of the Drawings Fig. 1 is a schematic front view showing a general construction of an injection-compression molding machine provided with a molding apparatus according to the present invention; Fig. 2 is a schematic longitudinal cross-section view showing an essential part of a molding apparatus according to the present invention; Fig. 3 is a block diagram of a control unit for a molding apparatus according to the present invention; Fig. 4A, 4B and 4C are time charts respectively showing operations of a first preferred embodiment relating to the molding method according to the present invention; Fig. 5 is a flow chart showing the operations of the first preferred embodiment relating to the molding method according to the present invention; Figs. 6A, 6B and 6C are time charts respectively showing operations of a second preferred embodiment relating to the molding method according to the present invention, with reference to a screw stroke; Fig. 7 is a flow chart showing operations of a second preferred embodiment relating to the molding method according to the present invention; Fig. 8 is a flow chart showing operations of a third preferred embodiment relating to the molding method according to the present invention; Figs. 9A, 9B and 9C are time charts respectively showing operations of a fourth preferred embodiment relating to the molding method according to the present invention, with reference to a screw stroke; and Fig. 10 is a flow chart showing the operations of the fourth preferred embodiment relating to the molding method according to the present invention. Detailed Description of the Preferred Embodiments In the following, a number of preferred embodiments of the present invention will be described in detail in connection to the accompanying drawings. Fig. 1 is a schematic front view showing a general construction of an injection-compression molding machine provided with a molding apparatus according to the present invention, in which reference numeral 1 designates an injection-conpression molding machine, numeral 10 designates an injection unit, numeral 20 designates a press, and numeral 30 designates a metal mold. Reference numeral 40 designates a valve, which is disposed within a flow passageway 46 of molten resin (hereinafter called simply "resin") provided between the injection unit 10 and the metal mold 30, and normally it is juxtaposed on the side of the injection unit 10. The injection unit 10 is mounted so as to be slidable on a bed 2 of the injection-compression molding machine 1 by means of a slider 12 fixedly secured to an injection cylinder 11. The metal mold 30 is composed of an upper mold 31 and a lower mold 32, the upper mold 31 and the lower mold 32 are fixedly secured to a slide 21 of the press 20 and to a bed 22 of the press 20, respectively, and resin within the metal mold 30 is pressed by a depressing force of the slide 21. In Fig. 2, a screw 13 is tightly inserted into the injection cylinder 11 and is also connected to a cylinder 14, and it is made to slide in the Z-direction jointly with the cylinder 14 by a hydraulic pressure fed through intake and exhaust ports 15 and 16 provided in the cylinder 14. The slide movement of the screw 13 within the injection cylinder 11 is measured as a screw position by means of a potentiometer 17. Molten resin is sealingly filled in the intension 29 of the injection cylinder 11 and is pressed by the screw 13, and the pressure of the pressed resin is detected by means of a pressure gauge 18. The cylinder 14 for pressing the screw 13 has its pressure detected by means of a pressure gauge 19. A valve 40 is associated with the injection unit 10, it is composed of a rotary valve 41, a lever 42, rods 43 and 44 and a linear motor 45, and by controlling operations of the linear motor 45, turning of the rotary valve 41 is effected to perform blocking and change of a cross-section area of a flow passageway 46 of resin. The valve 40 is made to butt against the metal mold 30 by slide movement of the injection unit 10 associated therewith, and the flow passageway 46 of the valve 40 is communicated with a flow passageway 33 of the metal mold 30. The flow passageway 33 of the metal mold 30 is provided in the lower mold 32, and is extended to a product forming portion 34. The product forming portion 34 has one end opposed to the lower mold 32 and the other end opposed to the upper mold 31, and its inner volume is reduced by movement of the upper mold 31. A mutual opening/closing speed of the metal mold and a pressure of resin sealingly filled in the product forming portion 34 are determined by a moving speed and a pressing force of the upper mold 31. The moving speed and the pressing force of the upper mold 31 are controlled by a speed and a thrust of a hydraulic cylinder 22 for driving the slide 21 of the press 20 having the upper mold 31 mounted thereto, and are determined by a flow rate and a hydraulic pressure in a hydraulic circuit extending from a port 23 but not shown. The slide 21 is provided with a potentiometer 24 and a speed sensor 25, and thereby a stroke position and a speed of the slide 21 are detected. The hydraulic cylinder 22 is associated with a hydraulic pressure gauge 26 and thereby a pressing force of the slide 21 is detected. In Fig. 3, a controller 50 consists of a CPU 51, RAM 52, ROM 53 and a clock oscillator 54, by the intermediary of an interface 55 it is associated with detecting means such as injection cylinder inner pressure detecting means 18a consisting of the pressure gauge 18 for measuring the pressure of resin within the injection cylinder or the like, screw position detecting means 17a consisting of the potentiometer 17 for measuring the position of the screw 13 within the injection cylinder or the like, cylinder hydraulic pressure detecting means 19a for measuring a hydraulic pressure in teh cylinder 14 for pushing the screw 13, metal mold opening/closing speed detecting means 25a consisting of the speed sensor 25 for measuring an opening/closing speed of the metal mold or the like, metal mold position detecting means 24a consisting of the potentiometer 24 for measuring the position of the metal mold or the like, and metal mold pressing force detecting means 26a for detecting a pressing force of the metal mold, as well as setting means such as valve angle setting means 45b for setting an opening angle of the valve 40, metal mold opening/closing speed setting means 25b and metal mold opening/closing position setting means 24b for setting an opening/closing speed and the position of the metal mold 30, screw position setting means 17b for setting the position of the screw 13 which serves as a reference for control relating to opening/closing of the valve 40 and the metal mold 30, and valve opening/closing timer setting means 54b for setting opening/closing time of the valve 40, and it outputs signals for controlling valve opening/closing drive means 45c such as the linear motor 45 for controlling opening/closing of the valve 40 or the like, and metal mold opening/closing drive means 22c such as the hydraulic cylinder 22 for controlling opening/closing of the metal mold 30 or the like, on the basis of the signals detected in correspondence to the respective setting means. In the above-described construction, description will be made on a first preferred embodiment with reference to Figs. 3 and 4. At time t ₁ of the clock oscillator 54, operation of the screw 13 is started (Step 61). A pressure of resin within the injection cylinder 11 reaches a set pressure P₀ (Step 62), and when a set time has elapsed and resin has become stable (time t ₁, Step 63), a cross-section area A₁ of the flow passageway 46 of resin is set, and an instruction for an opening angle B₁ of the valve which determines a flow velocity of resin (Step 64) and an instruction for an opening/closing speed C₁ of the metal mold for pressing the resin injected into the metal mold 30 (Step 65) are issued. After the opening angle of the valve has become the instructed angle (Step 66), count of the clock oscillator 54 is commenced, and also in Step 67, control is effected so that the opening/closing speed of the metal mold may become a predetermined speed. In Step 68, after a predetermined period has elapsed (t₃) since the valve opening angle B₁ became the predetermined angle in Step 67, that is, after a predetermined amount of resin has been injected, the control is returned to Step 64 and Step 65 for setting the next valve opening angle B₂ and metal mold opening/closing speed C₂. Thereafter, at time t₄ and t₅ similar switching is effected, at time t₅ the injection is finished, and the valve 40 is closed. Next, description will be made on a second preferred embodiment in connection to Figs. 6 and 7. A the position of stroke S₁, the screw 13 starts to operate (Step 71). The pressure in the injection cylinder 11 is brought to a set pressure P₁ so that the presence of the resin in the injection cylinder may reach a set pressure P₀ (Step 72), and when the resin has become stable stroke S₂ (Step 73), a cross-section area A₁ of the flow passageway 45 of resin is set and an instruction for a valve opening angle B₁ to determine a flow velocity of resin is issued (Step 74), and when the valve opening angle B₁ has reached the instructed value (Step 75), an instruction for a metal mold opening/closing speed C₁ to press the resin injected into the metal mold 30 is issued (Step 76). In Step 77, control is effected so that the metal mold opening/closing speed may become a predetermined speed. Injection by means of the screw 13 proceeds, and when its stroke has come to a predetermined position S₃ (Step 78), that is, when a predetermined amount of resin has been injected, the control returns to Step 74, and an instruction for a valve opening angle B₂ to determine the next flow velocity of resin, is issued. Thereafter, Steps 74 - 78 are repeated, at stroke S₅ the injection is finished and the valve is closed. Next, a third preferred embodiment will be described in connection to Fig. 8. In this third preferred embodiment, as compared to the above-described second preferred embodiment, during control for the metal mold while the metal mold closing speed was controlled according to the stroke of the screw 13 in the second preferred embodiment, in the third preferred embodiment this is modified so as to control a pressing force for the upper mold 31 of the metal mold 30. In succession, description will be made on a fourth preferred embodiment in connection to Figs. 9 and 10. Up to Step 88 of the above-described third preferred embodiment and Step 98 of this fourth preferred embodiment, the control is the same, but in the fourth preferred embodiment, when the screw stroke has reached the final instruction, the valve 40 is held closed. After the valve 40 has been closed, the pressing force for the metal mold is varied in a step-wise manner or continuously taking into consideration the shrinkage of resin caused by cooling and the like. It is to be noted that while a screw was used in the injection unit in the above-described respective embodiments, a plunger could be used therein. Also, while the valve was controlled by making use of a rotary valve and a linear motor, it is a metter of course that a combination of a valve such as a needle valve, a slide valve or the like and either angular control such as a step motor or the like or linear control such as a linear motor or the like, could be employed. In addition, while a stroke of a screw was used as a reference of control, time or a pressure in an injection unit could be used. Furthermore, regarding a press, while a hydraulic press was employed, a mechanical press could be employed, and the first preferred embodiment, the second preferred embodiment and the third preferred embodiment could be employed in combination.

Claims: A molding method in an injection-compression molding machine (1) including a valve (40) disposed in a flow passageway (46) of molten resin provided between an injection unit (10) and a metal mold (30) for effecting controlling resin flow area of said flow passageway (46), comprising the steps of: supplying a molten resin into said injection unit (10) under a pressure; injecting a preset amount of the molten resin into said metal mold (30) through said valve (40); and closing said valve (40) after completion of injection and, in conjunction therewith pressing the molten resin within said metal mold (30), characterized in that said step of supplying the molten resin into the injection unit (10) is performed while said valve (40) is held in close position so as to increase the pressure within said injection unit (10) to a relatively high value for preliminarily pressing said molten resin for uniformity of density of the molten resin. A molding method in an injection-compression molding machine (1) as claimed in Claim 1, characterized in that the pressing on the molten resin within said metal mold (30) is carried out from the midst of injection of the molten resin. A molding apparatus in an injection-compression molding machine (1), comprising: a molten resin supply means for supplying a molten resin to an injection unit (10); a flow passageway (46) for supplying said molten resin from said injection unit (10) to a metal mold (30); a valve means (40) disposed in said flow passageway for adjusting a molten resin flow passageway (46), said valve means (40) being operable at a fully closed position; means for controlling a valve position depending upon progress of the molding process, characterized in that said controlling means maintains said valve means (40) at said fully closed position while the molten resin is supplied to said injection unit (10) from said molten resin supply means so that a pressure of said molten resin in said injection unit (10) is elevated to a given value and maintained at said given value for a predetermined period for effecting preliminary pressing for uniformity of density of said molten resin. A molding apparatus in an injection-compression molding machine (1) as claimed in Claim 3, characterized in that said valve means (40) includes a rotary valve (41) performing a rotary operation as actuated by a valve operating device (42, 43, 44, 45), and there a cross-section of a flow passageway (46) of molten resin is varied by the rotary operation of said rotary valve (41) so as to control at least an injection flow velocity and an injection flow rate of the molten resin. A molding apparatus in an injection-compression molding machine (1) as claimed in Claim 3, characterized in that said apparatus further includes means (18) for detecting a pressure within an injection cylinder (11), means (17) for detecting a position of a screw (13) provided within the injection cylinder (11), means (25) for detecting an opening/closing speed of a metal mold (30), input means for setting an opening angle of a valve (40), input means for setting the opening/closing speed of the metal mold (30), input means for setting the position of the screw (13), means responsive to a pressure signal of the injection cylinder (11) for generating an opening/closing signal for the valve (40), a valve opening/closing actuator driven by the opening/closing signal for the valve (40), means responsive to a position signal of the screw (13) for generating an opening/closing speed signal for the metal mold (30), and a press (20) having the metal mold (30) mounted thereto and driven by the opening/closing speed signal for the metal mold (30).

Inventors: FUJIMOTO SATOSHI, HIGUCHI MAKOTO, NOGAWA MAKOTO, SASAKI YOSUKE, SATO KAN-ICHI, FUJIMOTO, SATOSHI, HIGUCHI, MAKOTO, NOGAWA, MAKOTO, SASAKI, YOSUKE, SATO, KAN-ICHI
Applicants: KOMATSU MFG CO LTD, KABUSHIKI KAISHA KOMATSU SEISAKUSHO
Application year: 1989
Main classification: B29C45
IPC codes: B29C45