Dry etching with hydrogen bromide or bromine

Abstract: Plasma etching with hydrogen bromide or bromine as an etching gas allows precise control of etching for attaining vertical etching or taper etching with a desired taper angle by controlling a temperature of a mass to be etched, which mass is usually a semiconductor wafer.

Description: The present invention relates to dry etching a material such as polycrystalline silicon with hydrogen bromide or bromine. As a result of the increased degree of integration and switching speed of IC's, an insulating film such as a gate insulating film must be made thinner, for example, 30 nm to 50 nm, and further, a multilayer technology for electrical conductive materials such as polycrystalline silicon must be utilized. This processing of such a polycrystalline silicon determines a gate length, which influences the characteristics of an FET, and thus, during etching of the polycrystalline silicon, the width of a pattern must be strictly controlled and there must be high etching selectivity of the polycrystalline silicon obtained in relation to an underlying gate insulating layer. To accomplish the above, vertical etching methods, such as reactive ion etching, can be used, but if a lower layer, for example, a first polycrystalline silicon layer, is vertically etched, the thickness of an upper layer, for example, a second polycrystalline silicon layer, becomes thicker at a portion of a step of the vertically etched first polycrystalline silicon layer than at the other flat portion. This thicker portion of the second polycrystalline silicon layer remains after the second polycrystalline silicon layer is etched, and leads to a short circuiting of adjacent patterns of the second polycrystallino silicon layer through the remaining portion. If the second polycrystalline silicon layer is over-etched for an extended time, to completely remove the polycrystalline silicon at the step portion, the width of a pattern is narrowed and the underlying insulating layer is excessively etched. One solution to the above problems is the use of a vertical etching process having a high selectivity, so that an underlying layer is not excessively etched. To obtain this high selectivity, a chlorine-bearing or fluorine-bearing etching gas is widely used, but etching with a chlorine or fluorine-bearing gas tends to cause side-etching, due to the isotropic nature thereof, and it becomes difficult to control the width of a pattern. To protect the side wall of a pattern from such an etching gas, a carbon-bearing gas may be used, but use of a carbon-bearing gas increases the etching rate of an insulating layer, whereby the selectivity of etching of a polycrystalline silicon, etc. in relation to an insulating layer is reduced. Further, a polymer containing carbon is deposited onto a wall of an etching chamber, which causes contamination and a reduction of the product yield. Another solution is to form a pattern of a first polycrystalline silicon layer having a tapered shape, i.e., a declined, not vertical, side wall, on which a second polycrystalline silicon layer is deposited and then etched. The known methods of taper etching are as follows: (1) Phosphorus is diffused and phosphorus ions are then implanted to a first polycrystalline silicon layer, to make the ion implanted surface portion of the layer more receptive to etching. Then isotropic etching is carried out on the polycrystalline silicon layer, and thus the polycrystalline silicon layer is taper etched. [Japanese Unexamined Patent Publication Nos. 58-4932 and 53-73086 and Japanese Examined Patent Publication No. 60-782] Nevertheless, this process is complicated, since a diffusion of phosphorus and ion implantation is necessary before the etching. Also, it is difficult to control a width of a pattern during isotropic etching. (2) Etching with an etching gas to which a depositing gas such as C 2 H 6 , C 2 H 4 , is added to provide a simultaneous etching and deposition to form a tapered pattern. [Japanese Unexamined Patent Publication Nos. 59-103338, 62-30330 and 62-32618] This method allows a deposition on on a wall of an etching chamber, which results in contamination by particles and reduces the product yield. (3) A resist mask is tapered and etching is effected with a low etching selectivity between polycrystalline silicon and the resist. [Japanese Unexamined Patent Publication (Kokai) No. 61-61424] In this method, since the thickness of the resist is varied, it is difficult to control the width of a pattern. (4) Alternate etching and ashing of a resist mask. [Japanese Unexamined Patent Publication (Kokai) No. 56-93319 and 57-59331] This process is complicated and control of the width of a pattern is difficult, since the thickness of the resist mask is reduced. (5) Isotropic etching followed by anisotropic etching. The isotropic etching is stopped when only an upper part of a polycrystalline silicon layer is etched, and then the anisotropic etching is carried out. [Japanese Unexamined Patent Publication No. 57-7936 and 56-90525] This process also is complicated, and the control of the width of a pattern is difficult. (6) A mask having an overhanging portion having a lower surface facing upward is used, so that the flow of ions is disturbed and thus a tapered pattern is formed. [Japanese Examined Patent Publication No. 57-42154] It is not easy, however, to form a resist mask having an overhanging portion as above, and it is difficult to control the width of an etched pattern. According to the present invention high selectivity of etch is achieved in a process for selectively etching a mass of silicon, comprising: providing an etching mask over the mass, defining exposed areas of the mass that are to be etched; and providing a plasma of an etching gas in contact with the exposed areas of said mass in an etching chamber; characterised in that said etching chamber has no carbon-containing material in contact with said,plasma of the etching gas and in that said etching gas contains hydrogen bromide, bromine or a combination thereof as a main reactive component that reacts with said mass and has a carbon content of less than 120 ppm of carbon based on the total weight of said etching gas. In one process embodying this invention, to achieve in the etched mass of silicon a sidewall having an inclination of less than 90°C, it should be ensured that the etching gas does not include any carbon-containing component and that etching is carried out at a temperature of from -40°C to +50°C. As described above, a carbon-bearing gas may cause deposition of a polymer onto a wall of an etching chamber, which may result in contamination by particles in products. Further, a carbon-bearing etching gas may reduce the etching selectivity of materials such as polycrystalline silicon. Accordingly, any carbon content of the etching gas used in a process of the present invention is less than 120 ppm, preferably less than 40 ppm, based on the total weight of the etching gas. Ideally, the carbon content of the etching gas should be zero. Similarly, the etching chamber does not include a carbon-bearing material which can come into contact with a plasma of an etching gas. Such a carbon-bearing material could disadvantageously reduce the etching selectivity of a material to be etched. In a preferred embodiment of the invention, to etch selectively said exposed area of said mass to form said mass with an etched portion and a side wall along a periphery of said etching mask having a predetermined angle of inclination, a temperature is imparted to said mass during said etching which is set to give the etched mass side wall the predetermined angle of inclination. Japanese Examined Patent Publication No.58-14507, corresponding to U.S. patent application S.N. 594418, filed on July 9, 1975, suggests that bromine or a bromine compound may be used for a vertical etching of silicon, but in this publication, only carbon tetrachloride is actually used in experiments, and bromine or a bromine compound is mentioned merely as a possible alternative. Furthermore, this publication states that a target electrode must be heated, since the boiling point of SiBr, at which it is thought to be vaporized, is 153°C. The present inventors, however, surprisingly found that a vertical etching of silicon, etc., can be carried out at a temperature lower than 150°C, and further, that a taper etching can be obtained at a temperature of -40°C to 50°C, in which process the taper angle of the etching is precisely controlled in accordance with the temperature. U.S. Patent No. 4,490,209 issued on December 25, 1984 to Hartman discloses a plasma etching which allows an anisotropic etching of silicon, in which a gaseous mixture of a chlorine-bearing species and hydrogen bromide is used. In this patent, however, a chlorine-bearing species must be used as a main reactive component and hydrogen bromide added in a small amount of about 1 to about 10%, to allow a near perfect anisotropic etching. This process is different from the process of the present invention, in which hydrogen bromide or bromine is used as a main etching or reactive component and not only a vertical etching but also a taper etching can be carried out, and the taper angle controlled as desired. Therefore, in an embodiment of the present invention, a taper etching having an inclination angle of the side wall of an etched mass of less than 90° is obtained at a temperature of the mass etched of -40°C to +50°C, and a substantially vertical etching is carried out at a temperature of the etched mass of 50°C to 150°C. The relationship between the angle of inclination of the side wall of the mass etched and the temperature of the mass etched is expressed as follows: where  stands for the inclination angle of the side wall of the etched mass and t stands for the temperature of the mass during etching, the inclination angle  having a dispersion of ±5°. Note, the temperature mentioned above is that of the mass to be etched, not that of an atmosphere surrounding the mass to be etched. Furthermore, for a p-type or non-doped polycrystalline silicon, at a temperature of an etched mass of more than 150°C, a taper etching having an inclination angle of the side wall of the etched mass of more than 90° can be obtained. For an n-type polycrystalline silicon, at a temperature of more them 150°C, side etching or undercut profile is obtained. For a better understanding of the invention and to show how the same can be carried into effect, reference will now be made, by way of example only to the accompanying drawings, wherein: Figures 1A to 1C show the main steps of dry etching an upper layer of polycrystalline silicon on a lower layer of polycrystalline silicon as effected conventionally; Fig. 2 is a perspective view showing an etching residue resulting from dry etching as shown in Figs. 1A to 1C; Fig. 3 is a schematical view of an apparatus for plasma etching used in a process according to the present invention; Figs. 4A to 4E are sectional views of patterns etched in accordance with a process of the present invention; Fig. 5 shows relationships of the taper angle obtainable by the dry etching and the temperature of a wafer during etching; Fig. 6 is a schematical view of an apparatus for plasma etching used in an embodiment of the present invention; and Fig. 7 shows the relationship of the etching selectivity of polycrystalline silicon to SiO 2 and the carbon content in etching gas. Before describing an embodiment of the present invention in detail, the prior art is briefly illustrated using drawings. Figures 1A to 1C illustrate the steps of an RIE of an upper polycrystalline silicon layer on a step portion of a lower polycrystalline silicon layer. In Fig. 1A, 1 denotes a silicon substrate, 2 an insulating film, 3 a first polycrystalline silicon layer, 4 an insulating film, and 5 a second polycrystalline silicon layer deposited by CVD. The second layer 5 has different thickness A and B over flat and step portions of the first layer 3; the thickness B of the second layer over the step portion is larger than the thickness A over the flat portion. When this structure is subject to RIE, a portion 7 of the second polycrystalline silicon layer near the step portion of the first polycrystalline silicon layer 3 remains unetched, as seen in Fig. 1B. This remaining portion 7 may cause a short circuit between adjacent wiring patterns of the second polycrystalline silicon layer, as seen in Fig. 2. If the second polycrystalline silicon layer 5 is subject to overetching, to completely remove the portion 7, the insulating films 2 and 4 are undesirably excessively etched as seen in Fig. 1C. This is because of a relatively low selectivity of etching between the polycrystalline silicon and the insulating films. An embodiment of the present invention is now described in more detail. Figure 3 shows a reactive ion etching (RIE) apparatus used in the following example. In this apparatus, a wafer 11 is electrostatically mounted to an electrostatic chuck 12 by applying a voltage of ±1500 V to the chuck 12 through low pass filters 13, from a DC power source 14. A gas, for example, helium under a pressure of 0 - 20 Torr (1 Torr = 133.3 Pa), is introduced between the wafer and the chuck 12, through a gas inlet 21 from a pressure-adjusting unit (not shown), to facilitate thermal conduction. The temperature of the electrode 15 is controlled by cooling water 16. When the electrode 15 is to be cooled to less than 0°C, the cooling liquid is composed of methanol, a mixture of water and ethylene glycol, or a mixture of water and methanol. An etching chamber 22 is evacuated through an exhaust port 20 by a vacuum pump (not shown). An etching gas is introduced to the chamber 22 through a gas introducing port 19, and a high frequency wave is applied to the gas by an RF generator 18 through a matching box 17, to generate a plasma and thereby carry out an etching. The temperature of the wafer 11 during etching is detected by a fluorescent thermometer 24. A fluorescent material 26 is applied on a rear side surface of the wafer 11, and a pulse light is irradiated to the fluorescent material 26 through a glass fiber 23 passing through a pore 25 of the electrode 15, and a fluorescent light generated from the fluorescent material 26 is observed through the same glass fiber 23 to determine the temperature of the wafer 11. The fluorescent thermometer 24 used is the LUXTRON 750 marketed by LUXTRON (1060 Terra Bella Avenve, Mountain View, CA 94043, U.S.A.). This thermometer can advantageously precisely determine the wafer temperature without interference by noise from the RF, since it uses a glass fiber unlike a conventional thermocouple which cannot block the noise from the RF. This precise determination, of the wafer temperature is essential to the preferred embodiment of the present invention. The temperature of a wafer depends on the etching gas, pressure, RF power, etc., but can be controlled, even when these conditions are fixed, by changing the temperature of the cooling liquid 16 to change the temperature of the electrode 15, by changing the kind or pressure of the gas such as He introduced between the wafer 11 and the electrostatic chuck 12, or by changing the voltage applied to the chuck 12 to change the force attracting the wafer 11, to change the thermal conduction between the wafer 11 and the electrode 15. Figures 4A to 4D show cross sections of a phosphorus-doped n-type polycrystalline silicon (resistance 60 Ω/cm 2 pattern etched in accordance with the present invention and using an apparatus shown in Fig. 3. In Figs. 4A and 4B, reference numeral 38 denotes a mask of a photoresist, SiO 2 , Si 3 N 4 , etc., 33 denotes a polycrystalline silicon layer to be etched, 32 denotes an underlying insulating film of SiO 2 , etc., and 31 denotes a silicon substrate. The etching conditions are as follows: a gas of Br 2 (16 SCCM) + He (57 SCCM), a pressure of 0.1 Torr, a power of 300 W, and 100% overetching after etching the polycrystalline silicon layer 33. Figure 4A shows a pattern etched at 80°C; Fig. 4B a pattern etched at 0°C; and Fig. 4C a pattern etched at 160°C; and Fig. 4D a pattern etched at 200°C. In these figures the angle of inclination of a side wall 39 of the etched pattern 33 is designated by the mark . The angle  is about 90° in Fig. 4A, about 60° in Fig. 4B. As seen in these figures, varied etching shapes are obtainable by changing only the temperature of a wafer. Figure 5 shows the relationship between the inclination angle  of an etched polycrystalline silicon and a temperature of the wafer, in which n-type doped and non-doped polycrystalline silicons are etched with a mask of a photoresist or SiO 2 . In Fig. 5, the black triangles represent an n-type doped polycrystalline silicon etched with a photoresist mask; the black circles represent an n-type doped polycrystalline silicon etched with an SiO 2 mask; the white triangles represent a non-doped polycrystalline silicon etched with a photoresist mask; and, the white circles represent a non-doped polycrystalline silicon etched with an SiO 2 mask. As seen in Fig. 5, an angle of inclination of an etched pattern of less than 90° is obtained at a wafer'temperature of -40° to +50° and the inclination angle is increased with an increase of the wafer temperature in the above temperature range. This relationship is represented by the formula:  = t/2 + 65 ± 5, i.e., t/2 + 60 ≦  ≦ t/2 + 70, wherein t stands for the wafer temperature. At a wafer temperature of 50°C to 150°C, the polycrystalline silicons are etched substantially vertically, i.e., the inclination angle  is about 90°. At a wafer temperature of more than 150°C, for a non-doped polycrystalline silicon, the inclination angle  of the etched polycrystalline silicons may be more than 90° as shown in Fig. 4E. Note that, at a wafer temperature of more than about 150°C, the photoresist may be burnt and special heat treatment such as deep UV cure is required. Accordingly, a desired inclination angle  of an etched polycrystalline silicon pattern can be obtained by changing the wafer temperature. At a wafer temperature of less than -40°C, an appropriate etching cannot be carried out and needle-like residues remain. In the Examples which follow, Examples 15 to 32 serve to establish the principle underlying the present invention. The principle of the preferred embodiment wherein temperature selection is used to control side wall inclination is established in Example 18 and discussed more fully in Examples 1 to 14. Example 1 An SiO 2 layer having a thickness of 20 nm, on which a phosphorus-doped polycrystalline silicon layer (resistance 20 Ω/cm 2 ) was deposited to a thickness of 400 nm, was thermally grown on the surface of a silicon substrate. A photoresist pattern was formed on the phosphorus-doped polycrystalline silicon layer by a usual photolithography technique. The substrate or wafer was mounted in the apparatus as shown in Fig. 3, and an RIE was carried out under a supply of an etching gas of 16 SCCM - Br 2 + 57 SCCM - He, a pressure of 0.1 Torr, a power of 300 W, He supplied between the wafer and the electrostatical chuck at 10 Torr, a cooling liquid temperature of -15°C, and an electrode temperature of -10°C. The maximum wafer temperature was 0°C. The results are shown in the following Table 1. The width of the etched polycrystalline silicon pattern was the same as that of the mask. Example 2 The procedures of Example 1 were repeated except that the cooling liquid temperature was 25°C, the electrode temperature was 25°C, and the He pressure was 2 Torr. The maximum wafer temperature was 50°C. The results are shown in Table 1. Example 3 A phosphorus-doped polycrystalline silicon layer was deposited, and a CVD SiO 2 layer having a thickness of 100 nm was grown thereon and patterned by a usual photolithography technique using RIE with photoresist. After removing the photoresist, the procedures of Example 1 were repeated. The results are shown in Table 1. Example 4 A sample prepared in accordance with the procedures of Example 3 was etched under the same conditions as in Example 2, followed by an overetching of the polycrystalline silicon for the same time as required for the former etching. The results are shown in Table 1. Example 5 The same sample as in Example 1 was etched under a supply of an etching gas of 25 SCCM - HBr + 57 SCCM - He, a pressure of 0.12 Torr, a power of 350 W, He supplied between the wafer and the chuck at 10 Torr, a cooling liquid temperature of -15°C, and an electrode temperature of -10°C. The maximum wafer temperature was 5°C. The results are shown in Table 1. Example 6 As in Example 5, etching was carried out under a cooling liquid temperature of 20°C, an electrode temperature of 20°C, and an He pressure of 2 Torr. The maximum wafer temperature was 50°C. Overetching was carried out for the same time as required for the former etching. The results are shown in Table 1. Ex. Mask Wafer temp. (°C) Etching rate (nm/min) Etching selectivity Etching inclination angle  1 Resist 0 150 10 57° 2 Resist 50 200 23 82° 3 SiO 2 0 150 30 62° 4 SiO 2 50 200 50 89° 5 Resist 5 100 15 62° 6 Resist 50 170 27 92° Examples 7 - 14 A sample prepared as in Example 3 was etched under a supply of an etching gas of 50 SCCM - HBr, a pressure of 0.1 Torr, a power of 300 W (a power density of 0.66 W/cm 2 ), and He supplied between the wafer and the chuck at 10 Torr. The electrode temperature was controlled by heating with a heater arranged in the electrode, to within 80°C to 300°C. The results are shown in Table 2. Ex. Mask Wafer temp. (°C) Etching rate (nm/min) Etching selectivity Etching inclination angle  7 SiO 2 80°C 300 30 vertical (90°) 8 SiO 2 100°C 310 31 vertical (90°) 9 SiO 2 130°C 320 32 vertical (90°) 10 SiO 2 150°C 330 33 vertical (90°) 11 SiO 2 160°C 320 32 slightly undercut (as in Fig. 4C) 12 SiO 2 180°C 310 26 undercut (as in Fig. 4D) 13 SiO 2 200°C 300 21 undercut (as in Fig. 4D) 14 SiO 2 300°C 240 13 undercut (as in Fig. 4D) Example 15 Figure 6 shows a parallel plan-type apparatus for RIE used in these Examples, in which 41 denotes a wafer, 42 an etching chamber, 43 an upper electrode, 44 a lower electrode, 45 an electrostatic chuck, 46 a block of quartz glass for holding a wafer, 47 a DC power source for electrostatic attraction of a wafer, 48 a high frequency power, 49 a gas inlet, and 50 a gas outlet. The wafer temperature was determined by a fluorescent thermometer, not shown. The walls of the etching chamber 42 and the surface of the upper electrode 42 are covered with quartz glass or a material that does not contain carbon. A sample for etching was prepared as follows: On a silicon substrate or wafer, an SiO 2 film having a thickness of 100 nm was thermally grown, on which a polycrystalline silicon layer having a thickness of about 400 nm was deposited, on which, in turn, a mask pattern of SiO 2 or Si 3 N 4 having a thickness of about 200 nm and a width of 1 µm was deposited. The above sample was held by the holder 46 or by the electrostatic chuck 45, and the sample was subject to RIE to selectively etch the polycrystalline silicon. The etching gas was HBr and was introduced at 50 SCCM from the gas inlet 49 into the etching chamber 42 and evacuated through the gas outlet 50 to keep a pressure inside the chamber 42 at 0.1 Torr, and to which a high frequency (13.56 MHz) power of 300 W was applied by the power source 48. Accordingly, the RIE was carried out while varying the wafer temperature, and as a result, a vertical etching was attained at a wafer temperature of 50°C to 150°C. The etching rate of the polycrystalline silicon was 220 nm/min and that of the SiO 2 was 2 nm/min, and thus the obtained etching selectivity of the polycrystalline silicon to the SiO 2 was as high as 110, and was repeatable. The results are shown in Table 3. Example 16 The procedures of Example 15 were repeated except that the flow rate of HBr was increased. This increase of the flow rate of HBr, increased the etching rate of the polycrystalline silicon. At an HBr flow rate of 100 SCCM, the polycrystalline silicon etching rate was about 290 nm/min, while the etching selectivity of the polycrystalline silicon to the SiO 2 was 82. The results are shown in Table 3. Example 17 The procedures of Example 15 were repeated except that oxygen (O 2 ) or water (H 2 O), bearing an oxygen atom but no carbon atom, was added to the HBr etching gas. As a result, the etching rate of the polycrystalline silicon was not changed (220 nm/min), but the etching rate of the SiO 2 was lowered to 1 nm/min, and therefore, the etching selectivity of the polycrystalline silicon to the SiO 2 was higher than 200. The results are shown in Table 3. Ex. Etching gas Mask Temp. for vertical etching (°C) Etch rate of Poly-Si (nm/min) Etch rate of SiO 2 (nm/min) Selectivity of Poly-Si/SiO 2 15 HBr 25 SCCM SiO 2 (or Si 3 N 4 ) 50 - 150 220 2 110 16 HBr 100 SCCM SiO 2 (or Si 3 N 4 ) 50 - 150 290 3.5 82 17 HBr +O2 SiO 2 (or Si 3 N 4 ) 50 - 150 220 1 220 Example 18 In Examples 15 to 17, vertical etching was attained at a temperature of the wafer of 50°C to 150°C. When the temperature of the wafer was lowered to less than 50°C, taper etching was attained with an inclination angle  of the side wall of the etched pattern of less than 90°. Example 19 The procedures of Examples 15 to 18 were repeated, except that the etching chamber was made of aluminum coated with a polytetrafluoroethylene film. The results are shown in Table 4. Ex. Etching gas Mask Temp. for vertical etching(°C) Etch rate of Poly-Si (nm/min) Etch rate of SiO 2 (nm/min) Selectivity of Poly-Si/SiO 2 19 HBr Resist 50 - 90 220 15 15 20 HBr SiO 2 50 - 150 220 7 31 21 HBr Si 3 N 4 50 - 150 220 7 31 22 HBr/O 2 SiO 2 50 - 150 220 5 44 As seen in Table 4, by using a chamber having a coating of a carbon-bearing material, the etching rate of the polycrystalline silicon was not changed, but the SiO 2 etching rate was increased, and thus the etching selectivity of the polycrystalline silicon to SiO 2 was decreased. When other carbon-bearing materials such as polyacetal resin, carbon, silicon carbide etc. were used in the chamber or on the electrode, the SiO 2 etching rate was increased and the etching selectivity was decreased. Examples 23 to 28 The procedures of Examples 15 to 22 were repeated except that the etching gas was changed from HBr to other gases. The results are shown in Table 5. The results were not varied, regardless of the material of the etching chamber. Note, that, although etching with SF 6 at -130°C provided an excellent etching rate and etching selectivity, etching at a low temperature of -130°C requires a cooling mechanism using liquid nitrogen, etc., making the apparatus complicated, less reliable, and expensive. Ex. Etching gas Mask Temp. for vertical etching (°C) Etch rate of Poly-Si (nm/min) Etch rate of SiO 2 (nm/min) Selectivity of Poly-Si/SiO 2 23 SF 6 SiO 2 -130 or less 600 6 100 24 CCl 4 Resist 50 - 100 400 80 5 25 Cl 2 Resist 0 or less 420 40 11 26 Cl 2 SiO 2 -50 or less 400 16 25 27 Br 2 /He Resist 50 - 70 190 14 14 28 Br 2 /He SiO 2 50 - 70 190 9.5 20 Example 29 The procedures of Example 15 were repeated, except that the HBr used had a purity of 99.99% and a carbon content of 30 ppm by volume based on CO 2 . The results are shown in Table 6. Example 30 The procedures of Example 29 were repeated, except that the HBr used had a purity of 99.8% and a carbon content of 350 ppm by volume based on CO 2 . The results are shown in Table 6. The etching of the polycrystalline silicon per se was not affected, but the SiO 2 etching rate of was increased so that the etching selectivity of the polycrystalline silicon to the SiO 2 was reduced to 31. Ex. Etching gas Mask Temp. for vertical etching (°C) Etch rate of Poly-Si (nm/min) Etch rate of SiO 2 (nm/min) Selectivity of Poly-Si/SiO 2 29 HBr 25 SCCM (high purity) SiO 2 50 - 150 220 2 110 Si 3 N 4 50 - 150 220 2 110 30 HBr 25 SCCM (low purity) SiO 2 50 - 150 220 7 31 Si 3 N 4 50 - 150 220 7 31 Example 31 The procedures of Example 29 were repeated except that the etching gases used were 50 SCCM of the 99.99% HBr having a carbon content of 30 ppm (by volume as CO 2 ), mixed with 5 SCCM of a mixture of argon containing 3000 ppm by volume of CH 4 or CO 2 and a high purity argon containing no carbon at a various ratio. Namely, the HBr etching gas used had a varied carbon content. The etching of the polycrystalline silicon was not changed by mixing the carbon content of the HBr, but the etching rate of the SiO 2 was increased when the carbon content was increased, and the etching selectivity of the polycrystalline silicon to the SiO 2 was decreased. Namely, selectivity was 100 at a 40 ppm carbon content and 60 at a 120 ppm carbon content. These results are shown in Fig. 7. Example 32 Three kinds of samples were prepared for the following Examples. Sample A: On a silicon wafer, a thermally oxidized film having a thickness of 10 nm was grown, on which a polycrystalline silicon layer having a thickness of 200 nm was deposited by CVD. Into the polycrystalline silicon layer, arsenic ions were implanted at 70 keV and 4 x 10 15 /cm 2 . On the As-doped polycrystalline silicon layer, a positive-type photoresist layer having a thickness of 1.2 µm was coated and patterned to a minimum width of 0.6 µm. Sample B: This sample was similar to sample A, but As was not the ion implanted. Phosphorus was thermally diffused into the polycrystalline silicon to obtain a resistance of 60 Ω/cm 2 . Sample C: A thermally oxidized film having a thickness of 400 nm was grown on a silicon wafer. A resist pattern was formed on the oxidized film, in the same manner as for sample A. The etching apparatus used was similar to that shown in Fig. 6. The etching conditions were: an HBr etching gas at 120 SCCM, and a wafer temperature of 20°C to 150°C. The etching of the samples A and B was stopped before the polycrystalline silicon layer was completely removed and the etching rates of As-doped and P-doped polycrystalline silicons were determined. The sample C was etched for 5 minutes and the etching rate of the oxidized film and the etching selectivity of the polycrystalline silicon to the oxidized film were determined. The results are shown in Table 7.

Claims: A process for selectively etching a mass of silicon, comprising: providing over the mass an etching mask defining exposed areas of the mass that are to be etched; and providing a plasma of an etching gas in contact with the exposed areas of said mass in an etching chamber; characterized in that said etching chamber has no carbon-containing material in contact with said plasma of the etching gas and that said etching gas contains hydrogen bromide, bromine or a combination thereof as a main reactive component that reacts with said mass and has a carbon content of less than 120 ppm of carbon based on the total weight of said etching gas. A process as claimed in claim 1, wherein said etching gas does not include any carbon-containing component and etching is carried out at a temperature of from -40°C to +50°C. A process as claimed in claim 2, wherein, in order to cause an etched side wall portion of the mass to have an angle of inclination  ± 5°, the said mass is maintained during said etching at a temperature chosen in accordance with the following formula:  = t 2 + 65 where t is the temperature of the mass in degrees Celsius. A process as claimed in claim 1, 2 or 3, wherein said mass is made of a polycrystalline silicon. A process as claimed in any preceding claim, wherein said etching mask is composed of a non-carbon-containing material. A process as claimed in claim 4, wherein said etching mask is made of silicon oxide or nitride. A process as claimed in claim 1 or claim 3, 4, 5 or 6, when not appended to claim 2, wherein said etching gas has a carbon content of less than 40 ppm of carbon based on the total weight of said etching gas. A process as claimed in claim 1, wherein said etching gas does not contain any carbon-containing compound and the said mass is formed of p-type silicon or undoped silicon and is maintained at a temperature greater than +150°C during said etching to cause an etched side wall portion of the mass, along a periphery of said etching mask, to have an angle of inclination () greater than 90°. A process as claimed in claim 3 or any one of claims 4 to 8 when appended to claim 3, wherein said etching gas contains only hydrogen bromide as the reactive component and further contains an inert gas. A process as claimed in claim 3 or any one of claims 4 to 8 when appended to claim 3, wherein said etching gas contains only bromine as the reactive component and further contains an inert gas.

Inventors: IIZUKA KATSUHIKO, KURIMOTO TAKASHI, NAKAMURA MORITAKA, IIZUKA, KATSUHIKO, KURIMOTO, TAKASHI, NAKAMURA, MORITAKA
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1989
Main classification: H01L21
IPC codes: H01L29, H01L21