A thermosetting resinous composition and preparation of heat resisting coating and molded product using said composition

Abstract: A thermosetting resinous composition which consists essentially of (A) at least one polyepoxide compound having 2 to 6 epoxide groups, (B) at least one polyisocyanate compound having 2 to 6 isocyanate or blocked isocyanate groups, and (C) at least one catalyst selected from the group consisting of complex of organotinhalide with onium salt, complex of organotinhalide with hexamethylphosphoramide, complex of stibonium salt with zinc halide and complex of lithium halide with hexamethylphosphoramide, the equivalent ratio of isocyanate group and epoxide group being 1:2 to 2:1. Such resinous composition if useful for forming a cured coating and also for heat resisting molded products.

Description: The present invention relates to a thermosetting resinous composition comprising polyisocyanate compound, polyepoxy compound and catalyst and to a method for preparing a heat resisting cured coating and molded product using said composition. A thermosetting resin is widely used as injection molding, dipping, laminating or molding material in the preparation of various resin products as electric insulating materials, construction materials, coating compositions, adhesives and the like. Recently, these products are often used under much severe conditions, and with the change in such use conditions, far improved properties and especially heat resisting property, are required on such thermosetting resin. Since then a plastic material having both isocyanurate and oxazolidone group was reported in German Patent Publication DE-A-3,223,153, special attentions have been directed to this heat resisting novel resin. Such resin is usually prepared by the reaction of polyepoxide compound and polyisocyanate compound and sometimes referred to as polyoxazolidone resin because of having oxazolidone ring formed by the reaction of epoxy group and isocyanate group. This oxazolidone ring forming reaction is usually carried out in the absence of catalyst at comparatively higher temperatures or in the presence of catalyst at a moderate temperature. Typical catalysts used are tertiary amines (e.g. imidazole, hexamethylenetetramine and the like), quaternary ammonium salts (e.g. iodotetraethylammonium and the like), complex of Lewis acid with base material (e.g. complex of aluminium chloride with pyrrolidone, complex of aluminium chloride with phosphoric ester and the like), lithium halide, complex of lithium halide with phosphor compound (e.g. complex of lithium bromide with tributyl phosphine oxide and the like) alkyl esters of organophosphone acid or phosphoric acid, ammonium salts of acidic esters of organophosphone acid or phosphoric acid and the like. Recently, Matuda et al proposed in J. Org. Chem. 51, (12), 2177-2184 (1986), Chemistry Letters, 1963-1966 (1986) organotin halide-Lewis base complexes and organostibonium halides as novel catalysts for effecting oxazolidone ring formation. In the case of reaction between monoepoxide and monoisocyanate compounds, the desired oxazolidone compounds may be obtained by using such catalysts and adopting higher temperatures and longer reaction times. However, in the reactions between polyepoxide compounds and polyisocyanate compounds, the situations are more complicated and many byproducts are produced together with oxazolidone compounds. Among them, the main by-products are isocyanurate formed by trimerization of isocyanates and polyether formed by homopolymerization of epoxides. Once the trimerization of isocyanates occurs, there results materials with extremely higher functionalities and hence gives highly crosslinked, brittle polymer. Therefore in the reactions between polyepoxide compounds and poly-isocyanate compounds, it is essential that the trimerization reaction be controlled by all means. However, most of the heretofore proposed catalysts are effective not only for the formation of oxazolidone structure but also for the isocyanurate formation reaction, and polyoxazolidone products obtained by the known methods do include 30 mole% or more of byproduced isocyanurates. When a cured coating is prepared by using a composition comprising polyepoxide and polyisocyanate compounds, thus formed coating is mostly composed of the resins crosslinked with isocyanurate, urea bondings and polyoxazolidone crosslinkings are very few. This may be due to the fact that since various reactions are forced to be occured in a very thin layer of the applied composition, they are liable to be affected by the action of moisture in surrounding air, causing hydrolysis of isocyanate groups and inactivation of catalyst used. Therefore, some device has to be done in obtaining a cured coating mainly of the resin crosslinked with oxazolidone ring bridge by using a resinous composition comprising polyepoxide and polyisocyanate. In the case of molded products, the abovementioned moisture effect is not so important. However, with the increase in epoxide content, there occurs severe exothermic reactions, resulting undesired scorching of the molded product. Such thermal degradation is pointed as one of the questions still awaiting good solutions for molding use of the abovesaid composition. In such application, some device has to be done to react polyepoxide and polyisocyanate under mild condition to give polyoxazolidone containing least amount of trimerized isocyanurate. It is, therefore, an object of the invention to provide a thermosetting resinous composition capable of resulting a high quality plastic having polyoxazolidone groups by the reaction of polyepoxide and polyisocyanate. Another object of the invention is to provide a method for forming a cured coating of the resin crosslinked with oxazolidone ring bridge by using a coating composition consisting essentially of polyepoxide and polyisocyanate, with the least affect of moisture in surrounding air. A further object of the invention is to provide a method for forming a molded product mainly composed of the resins crosslinked with oxazolidone ring bridge, containing the least amount of trimerized isocyanurate, by reacting polyepoxide and polyisocyanate under mild conditions. According to the invention, the abovementioned objects can be attained with the following: The present invention in a first aspect provides a thermosetting resinous composition which consists essentially of (A) at least one polyepoxide compound having 2 to 6 epoxide groups, (B) at least one polyisocyanate compound having 2 to 6 blocked isocyanate groups, and (C) at least one catalyst selected from complexes of organotinhalide with onium salt, complexes of organotinhalide with hexamethylphosphoramide, complexes of stibonium salt with zinc halide, and complexes of lithium halide with hexamethylphosphoramide, the equivalent ratio of isocyanate group and epoxide group being 1:2 to 2:1. The composition according to the first aspect of the invention is preferably formulated as one liquid type composition containing (A), (B) and (C). The invention also provides a method for forming a cured coating which comprises applying onto a substrate surface a composition according to the first aspect of the invention and subjecting the thus formed coating to curing at an elevated temperature of 40 to 180°C. The invention in a second aspect provides a thermosetting resinous composition which consists essentially of (A) at least one polyepoxide compound having 2 to 6 epoxide groups, (B) a mixture of 90 to 10%, in terms of isocyanate group ratio, of at least aromatic polyisocyanate compound and 10 to 90% of at least one aliphatic or alicyclic polyisocyanate compound having 2 to 6 isocyanate groups, and (C) at least one catalyst selected from complexes of organotinhalide with onium salt, complexes of organotinhalide with hexamethylphosphoramide, complexes of stibonium salt with zinc halide, and complexes of lithium halide with hexamethylphosphoramide, the equivalent ratio of isocyanate group and epoxide group being 1:2 to 2:1. The invention further provides a method for preparing a heat resisting molded product which comprises placing a composition according to the second aspect of the invention in a mold and reacting the same at room temperature or an elevated temperature of up to 150°C. The composition according to the second aspect of the invention may be formulated as (i) a three pack composition, each pack containing (A), (B) or (C) separately; or (ii) a two pack composition, one pack containing (A) and the other pack (B), and (C) is contained in either one of said two packs; or (iii) a two pack composition, one pack containing (A) and the other pack (B), and (C) is divided into two complex-forming components and each component is contained in each said separate pack. The invention still further provides a method for preparing a heat resisting molded product which comprises placing an above composition (i), (ii) or (iii) in a mold and reacting (A) and (B) at room temperature or an elevated temperature of up to 150°C. In this invention, any of the known polyisocyanate compounds for polyurethane resins may be satisfactorily used providing having 2 to 6 blocked isocyanate groups. They may be of aliphatic, alicyclic or aromatic nature. Examples are hexamethylene diisocyanate, hydrogenated diphenylmethane diisocyanate, isophorone diisocyanate, hydrogenated tolylene diisocyanate, tolylenediisocyanate, diphenylmethanediisocyanate, naphthylene diisocyanate, xylylene diisocyanate, polyisocyanates containing carbodiimide group, urethoimine group, urea bonding, allophanate bonding, biuret bonding or isocyanurate ring structure, and polyisocyanates previously reacted with active hydrogen containing compounds. In an application for coating use, the present composition is preferably formulated into one pack, liquid type composition and therefore, such polyisocyanate have to be blocked with a heat dissociation compound. Examples of such compounds are, as disclosed in Progress in Organic Coatings Vol.3, p. 73 (1975), alcohols, phenols, lactams, N-hydroxyimideoxims, imidazoles, triazoles, active methylene compounds (e.g. acetylacetone, diethyl malonate and the like), aromatic sec. amines, acid sodium sulfite and the like. In an application for molding use, the polyisocyanate component is preferably used in the form of mixture of 90 to 10% in terms of blocked isocyanate group ratio of aromatic polyisocyanate compound and 10 to 90% of aliphatic or alicyclic polyisocyanate compound for quality stand of view. As the other component of polyepoxide compoud, any of the known members having 2 to 6 , more preferably 2 to 4, epoxy groups may satisfactorily be used. They may also be of aliphatic, alicyclic or aromatic nature and even of heterocyclic nature. Examples of such polyepoxide compounds are diglycidyl ethers of bisphenol A derived from the reaction between bisphenol A or halogenized bisphenol A and epihalohydrin, bisphenol F digycidylether, polynuclear phenol glycidylether, epoxidophenyl novolak resin, aromatic glycidyl amine resin derived from aromatic amine and epichlorohydrin, glycidylesters of aromatic, aliphatic or alicyclic polycarboxylic acids, glycidylethers of reaction products of aromatic or alicyclic dicarboxylic acid and polyol, epoxidized cycloolefin, epoxidized derivatives of polyunsaturated compounds as vegetable oils and their modified products, epoxidized silicate compounds and the like. They may be used alone or in combination of two or more. The abovementioned blocked polyisocyanate and polyepoxide are used in the weight ratio so as to give the equivalent ratio of blocked isocyanate to epoxy groups of 1:2 to 2:1, more preferably 1:1 to 2:1. If the amount of polyisocyanate (or blocked polyisocyanate) is too small, curing reaction will take a longer time and if the said amount is too excessive, there is a tendency that the cured product will become too brittle one. Catalyst component is a compound which will accelerate the oxazolidone ring formation in the reaction between polyepoxide compound and polyisocyanate compound and as the most characteristic feature of this invention, the following catalyst is advantageously and selectively used: (1) complex of organotin halide and hexamethylphosphoramide, (2) complex of organotin halide and onium salt, or (3) complex of stibonium salt and zinc halide. The abovementioned organotin halides are preferably such members represented by the formula: R m SnX (4-m) in which X is a halogen (as Br, J ), m is an integer of 1 to 3 and R is an aliphatic,aromatic or alicyclic hydrocarbon residue. Examples are trimethyl tin iodide, trimethyl tin bromide, dimethyl tin diiodide, dimethyl tin dibromide, tripropyl tin iodide, tripropyl tin bromide, dipropyl tin diiodide, dipropyl tin dibromide, tributyl tin iodide, tributyl tin bromide, dibutyl tin diiodide, dibutyl tin dibromide, trioctyl tin iodide, trioctyl tin bromide, dioctyl tin diiodide, dioctyl tin dibromide, triphenyl tin iodide, triphenyl tin bromide, diphenyl tin diiodide, diphenyl tin dibromide, tricyclohexyl tin iodide, tricyclohexyl tin bromide, dicyclohexyl tin diiodide, dicyclohexyl tin dibromide and the like. The onium salts are ammonium, phosphonium or stibonium salts represented by the formula: in which Z is N, P or Sb atom, R¹ to R⁴ are the same or different organic group and X is a halogen atom. Examples of onium salts are such ammonium compounds as tetramethyl ammonium iodide,tetramethyl ammonium bromide, tetraethyl ammonium iodide, tetraethyl ammonium bromide, tetrapropyl ammonium iodide, tetrapropyl ammonium bromide, tetrabutyl ammonium iodide, tetrabutyl ammonium bromide, tetraisoamyl ammonium iodide, tetraisoamyl ammonium bromide, tetrabenzyl ammonium iodide, tetrabenzyl ammonium bromide, methyltriethyl ammonium iodide, methyltriethyl ammonium bromide, trimethylphenyl ammonium iodide, trimethylphenyl ammonium bromide, trimethylbenzyl ammonium iodide, trimethyl benzyl ammonium bromide and the like, such phosphonium compounds as tetrabutyl phosphonium iodide, tetrabutyl phosphonium bromide, tetraphenyl phosphonium iodide, tetraphenyl phosphonium bromide, butyltriphenyl phosphonium iodide, butyltriphenyl phosphonium bromide, methyltriphenyl phosphonium iodide, methyltriphenyl phosphonium bromide, tributylphenyl phosphonium iodide, tributylphenyl phosphonium bromide and the like, and such stibonium compounds as tetraphenyl antimony iodide, tetraphenyl antimony bromide, tetrabenzyl antimony iodide, tetrabenzyl antimony bromide, tetrabutyl antimony iodide, tetrabutyl antimony bromide and the like. In this invention complexes of these catalytic components are selectively used as heat activation catalysts and such complexes are advantageously prepared by reacting the constituting catalytic components, preferably at equivalent molar ratio, in the presence or absence of solvent, at room temperature to 150°C. However, if required, abovementioned polyepoxide or polyisocyanate per se may be used as solvent for the catalystic components and at a heat-curing stage, they may be reacted together to generate the required heat activation catalyst and make it function as effective catalyst. Therefore, the term "heat activation catalyst" as used herein shall denote not only the abovementioned complexe itself but also the combination of the constituting catalytic components of such catalyst. More specifically, in the case of a coating composition, abovementioned polyepoxide, blocked polyisocyanate and catalyst (complex or combination of catalytic components) may be combined together to make one liquid, thermosetting type composition. For molding use, the present composition may be formulated into either one of the following: (1) three packs formulation wherein the constituting elements of polyepoxide, blocked polyisocyanate and heat activation catalyst each is contained in each different pack. (2) two packs formulation wherein the polyepoxide is contained in one pack and blocked polyisocyanate in another pack, and said catalyst is in either one of said two. (3) two packs formulation wherein the polyepoxide is contained in one pack and blocked polyisocyanate in another pack, and one member of the complex forming components is in said one pack and the other member is in said another pack. Among them, for a better storage stability of the composition, (1) or (3) and especially (3) is highly recommended. For example, in the case of organotin series complex catalyst, organotin halide is preferably contained in blocked polyisocyanate component and the other member of hexamethylphosphoramide or stibonium salt is in polyepoxide component and in the case of complex of zinc halide and stibonium salt, zinc halide is preferably contained in polyepoxide component and stibonium salt is in blocked polyisocyanate component. In the present invention, the abovementioned catalyst is used in an amount of 0.01 to 10 weight parts, preferably 0.1 to 5 weight parts, per 100 parts of the mixture of polyepoxide and blocked polyisocyanate. If desired, other catalyst may be used together. In one liquid type coating composition, besides the abovesaid essential components, any of the conventional additives used in a thermosetting type coating composition as, for example, filler, reinforcing filament, antioxidant, flame retardant, pigment, surfactant, catalyst, surface conditioner and the like may be added. The present coating composition is very stable at room temperatures and is excellent in application characteristics. The said composition may be applied in a usual way on various substrates and baked at about 40 to 180°C to give a coating with excellent heat resistance, composed mainly of polyoxazolidone resin, with least amounts of trimerized isocyanurate and epoxy resin. In the molding type composition, besides the abovementioned essential components, the composition may include other additives as filler, reinforcing filament, antioxidant, flameretardant, pigment, surfactant, catalyst, mold releasing agent, forming agent and the like. The compounding ratio of polyepoxide and blocked polyisocyanate may be widely varied depending on the intended objects, and the characteristic properties of thus obtained polyoxazolidone resin may also be varied with said compounding ratio. When an excess amounts (than theoretical amounts) of blocked polyisocyanate component are used, a polymer having oxazolidone bondings in its main chain and isocyanate groups at the end portions (i.e. isocyanate-ended oxazolidone polymer precursor) may be obtained, and when an excess amounts of polyepoxide are used, a polymer having oxazolidone bondings in its main chain and epoxy groups at the end portion (i.e. epoxy-ended oxazolidone polymer precursor). From the equivalent amounts of polyepoxide and polyisocyanate components, is obtained a high molecular weight polyoxazolidone polymer. The abovementioned isocyanate-ended oxazolidone polymer precursor may be used for the preparation of polyurethane or polyurea products, according to the known technique, as wax, elastomer, foam, coating material, adhesive and the like. Epoxide-ended oxazolidone polymer precursor may be reacted with epoxy hardening material to give coating material, adhesive and the like. Said oxazolidone polymer is useful for the preparation of molding products, coating material, adhesive and the like. Such materials are likewise useful for impregnation purpose in various electric insulating materials, glass fiber reinforced laminate and the like, and for compounding purpose in the preparation of printed circuit and various other electric appliances. Particularly important and useful application is the production of aircraft and automobile parts having improved heat resistance and stress resistance. The oxazolidone forming reaction of the present resinous composition in such applications may be carried out at room temperatures or elevated temperatures up to 150°C. Though the optimum temperature may somewhat be varied with the polyepoxide and blocked polyisocyanate used, it is usually settled in a range of about 40 to 150°C, more preferably 60 to 120°C. For the preparation of a product with far improved properties, thus obtained polyoxazolidone resin may preferably be subjected to a post curing at an elevated temperature of 100 to 300°C, most preferably 120 to 200°C. The present oxazolidone forming reaction may be carried out in the presence of appropriate diluent or solvent as desired. As the diluent or solvent, any of the inert aromatic, ester, or halogenated solvents may be satisfactorily used. Said reaction may be carried out batchwise or in continuous way. In the molding operation, any of the conventional techniques as vacuum deforming molding, reaction injection molding and the like may satisfactorily used. The invention shall be now more fully explained in the following Examples. Unless otherwise being stated, all parts and % are by weight. Example 1 22.5g (0.05 mole) of phenol blocked derivative of diphenylmethane diisocyanate (MDI) were dispersed in 100ml of o-dichlorobenzene/xylene (1/1) mixture and to this, were added 17.5g of bisphenol A/ epichlorohydrin epoxy resin having an epoxy equivalent of 175 and the indicated amounts of catalyst shown in Table 1 and the mixture was stirrered well to obtain a dispersion composition. This composition was coated on a tin plate so as to give a dry film thickness of about 20µ and baked under the conditions shown in Table 1 to obtain a cured coating. By the infra-red absorption spectrum analysis, it was confirmed that epoxy group (910cm⁻¹) and carbonyl group in carbamate bonding (1720cm⁻¹) were disappeared, oxazolidone group (1750cm⁻¹) was newly formed and isocyanurate group (1705cm⁻¹) which was the trimerized isocyanate group was not found in the product. Examples 2 to 4 In each Experiment, the same procedures as stated in Example 1 were repeated excepting substituting the catalyst shown in Table 1 for that of Example 1, to obtain the cured coating, respectively. In either Example, the infra-red spectrum analysis of the coating showed that there was indeed the formation of oxazolidone group but no formation of trimerized isocyanurate . Comparative Example 1 The same procedures as stated in Example 1 were repeated excepting using no catalyst. At that time, under the conditions shown in Example 1, no cured coating was obtained. By the infra-red spectrum analysis of the product, it was confirmed that there was no formation of oxazolidone group, remaining isocyanate groups (2260cm⁻¹) and epoxy groups, and at 170°C, there was clear formation of trimerized isocyanurate. Comparative Examples 2 to 5 In each Experiment, 14.5g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO groups, 17.5g of bisphenol A/epichlorohydrin epoxy resin having an epoxy equivalent of 175 and the indicated amounts of catalyst shown in Table 2 were added to 50ml of butyl acetate/xylene (1/1) mixed solvent and the combined was stirrered well to obtain a dispersion composition. Using the abovementioned composition and following the procedures of Example 1, a cured coating was prepared and subjected to an infra-red spectrum analysis. In either case, there were no consumption of epoxy groups, no substantial decrease in isocyanate groups and no formation of oxazolidone group. There was clear indication of the formation of isocyanurate by the trimerization of isocyanate groups. Example 5 Into a 100ml flask containing 38.5g of dichloromethane, were added 16.5g of dimethyltin diiodide (Me₂SnJ₂) and 22.0g of tetraphenyl antimony iodide (Ph₄SbJ) and the combined was stirred at room temperature for about 1 hour to prepare a catalyst solution. Into a 50ml flask, 3.5g of bisphenol A/epichlorohydrin epoxy resin having an epoxy equivalent of 175 and 0.19g of the abovementioned catalyst solution were placed and stirred while removing the contained gas. To this, were added 2.32g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO groups and 0.444g of isophorondiisocyanate at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750cm⁻¹) and only slight indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). Next, into a mold, on whose inner surface Rimrikey B-659-2 (trademark, Chukyo Yushi, wax series mold releasing agent) was previously coated, the abovementioned resinous mixture was injected, heat-reacted at 80°C for 1 hour and then taken out to obtain a molded product having excellent heat resistant property. Example 6 Into a 50ml flask, 3.5g of bisphenol A/epichlorohydrin epoxy resin having an epoxy equivalent of 175 and 0.38g of the catalyst solution obtained in Example 1 were placed and stirred while removing the contained gas. To this, were added 1.45g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO groups and 1.11g of isophorondiisocyanate at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). Example 7 Into a 100ml flask containing 23.6g of dichloromethane, were added 16.5g of dimethyltin diiodide (Me₂SnJ₂) and 7.1g of hexamethylphosphoramide ((Me₂N)₃PO) and the combined was stirred at room temperature for about 1 hour to prepare a catalyst solution. Into a 50ml flask, 3.5g of bisphenol A/epichlorohydrin epoxy resin having an epoxy equivalent of 175 and 0.238g of the abovementioned catalyst solution were placed and stirred while removing the contained gas. To this, were added 2.32g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO groups and 0.444g of isophorondiisocyanate at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). Example 8 Into a 20ml flask, were added 3.5g of bisphenol A/epichlorohydrin epoxy resin having an epoxy equivalent of 175 and an acetone solution containing 0.033g of zinc diiodide (ZnJ₂) and 0.05g of tetraphenyl antimony iodide (Ph₄SbJ) and the mixture was stirred while removing the contained gas. To this, were added 2.32g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO groups and 0.444g of isophorondiisocyanate at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). Example 9 Into a 50ml flask, 3.5g of epoxide phenyl novolak resinhaving an epoxy equivalent of 175 and 0.38g of the catalyst solution obtained in Example 5 were placed and stirred while removing the contained gas. To this, were added 2.32g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO groups and 0.444g of isophorondiisocyanate at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750 cm⁻¹) and only slight indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). Example 10 Into a 50ml flask, 3.5g of epoxide phenyl novolak resin having an epoxy equivalent of 175 and 0.38g of the catalyst solution obtained in Example 5 were placed and stirred while removing the contained gas. To this, were added 1.45g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 28% NCO groups and 1.11g of isophorondiisocyanate at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). Example 11 1.58g of tetraphenyl antimony iodide (Ph₄SbJ) were added to 100g of bisphenol A/epichlorohydrine epoxy resin having an epoxy equivalent of 175 and the mixture was stirred while removing gas to obtain a polyepoxide component solution. Separately, to a mixed polyisocyanate of 83.4g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO and 16.6g of isophoronediisocyanate, were added 1.38g of dimethyl tin diiodide (Me₂SnJ₂) and the combined was stirred and degassed to obtain a polyisocyanate component solution. Into a 50ml flask, were placed 3.55g of said polyepoxide solution and 2.94g of said mixed polyisocyanate solution and the combined was stirred at room temperature and degassed. Thus obtained resinous composition was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that the absorption peaks of epoxy group (910cm⁻¹) and isocyanate group (2250cm⁻¹) had disappeared and there were clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of isocyanurate (1705cm⁻¹). The abovesaid polyepoxide component solution and polyisocyanate component solution each showed an excellent storage stability. Example 12 2.0g of hexamethyl phosphoramide ((Me₂N)₃PO) were added to 100g of bisphenol A/epichlorohydrine epoxy resin having an epoxy equivalent of 175 and the mixture was stirred while removing gas to obtain a polyepoxide component solution. Into a 50ml flask, were placed 3.57g of said polyepoxide solution and 3.06g of the abovementioned organotin halide containing mixed polyisocyanate solution obtained in Example 11 and the mixture was stirred at room temperature and degassed. Thus obtained resinous composition was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that the absorption peaks of epoxy group (910cm⁻¹) and isocyanate group (2250cm⁻¹) had disappeared and there were clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of isocyanurate (1705cm⁻¹). The abovesaid polyepoxide component solution showed an excellent storage stability. Example 13 3.6g of 25% Zinc diiodide acetone solution were added to 100g of bisphenol A/epichlorohydrine epoxy resin having an epoxy equivalent of 175 and the mixture was stirred while removing gas to obtain a polyepoxide component solution. Separately, to a mixed polyisocyanate of 83.4g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO and 16.6g of isophoronediisocyanate, were added 1.9g of tetraphenyl antimony iodide (Ph₄SbJ) and the combined was stirred and degassed to obtain a polyisocyanate component solution. Into a 50ml flask, were placed 3.53g of said polyepoxide solution and 2.95g of said mixed polyisocyanate solution and the combined was stirred at room temperature and degassed. Thus obtained resinous composition was heated at 80°C for 1 hour to obtain a hard polymer. Upon analysis by infra-red spectrum, it was confirmed that the absorption peaks of epoxy group (910cm⁻¹) and isocyanate group (2250cm⁻¹) had disappeared and there were clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of isocyanurate (1705cm⁻¹). The abovesaid polyepoxide component solution and polyisocyanate component solution each showed an excellent storage stability. Comparative Example 6 Into a 50ml flask, 3.5g of bisphenol A/epichlorohydrin epoxy resin having an epoxy equivalent of 175 and 0.38g of the catalyst solution obtained in Example 5 were placed and stirred while removing the contained gas. To this, were added 2.9g of low viscosity polyisocyanate compound based on diphenylmethane diisocyanate containing 29% NCO at room temperature and stirred while removing gas. Thus obtained resinous mixture was heated at 80°C for 1 hour to obtain a polymer. Upon analysis by infra-red spectrum, it was confirmed that spectrum peaks corresponding to epoxy groups (910cm⁻¹) and isocyanate groups (2250cm⁻¹) had disappeared and there was a clear indication showing the formation of oxazolidone group (1750cm⁻¹) and substantially no indication showing the formation of trimerized isocyanate group (i.e. isocyanurate) (1705cm⁻¹). However, there were brown colored scorching and coating appearance was no good. Comparative Examples 7 to 10 The similar experiments as stated in Comparative Example 6 were repeated excepting substituting the catalysts shown in Table 3 for the catalyst of Comparative Example 6. Upon analysis by infra-red spectrum, it was confirmed that in each product, there was indeed the formation of polyoxazolidone but always included a larger amounts of isocyanurate, too. Comp. Ex. catalyst amount (g) curing state 7 Me₂SnJ₂/Ph₄SbJ 0.02/0.03 good 8 Me₂SnJ₂/(Me₂N)₃PO 0.04/0.07 good 9 Ph₄SbJ/ZnJ₂ 0.05/0.03 scorching 10 LiBr/(Me₂N)₃PO 0.02/0.07 scorching

Claims: A thermosetting resinous composition which consists essentially of (A) at least one polyepoxide compound having 2 to 6 epoxide groups, (B) at least one polyisocyanate compound having 2 to 6 blocked isocyanate groups, and (C) at least one catalyst selected from complexes of organotinhalide with onium salt, complexes of organotinhalide with hexamethylphosphoramide, complexes of stibonium salt with zinc halide, and complexes of lithium halide with hexamethylphosphoramide, the equivalent ratio of isocyanate group and epoxide group being 1:2 to 2:1. A composition as claimed in claim 1, formulated as one liquid type composition containing (A), (B) and (C). A method for forming a cured coating which comprises applying onto a substrate surface a composition as claimed in claim 1 or 2 and subjecting the thus formed coating to curing at an elevated temperature of 40 to 180°C. A thermosetting resinous composition which consists essentially of (A) at least one polyepoxide compound having 2 to 6 epoxide groups, (B) a mixture of 90 to 10%, in terms of isocyanate group ratio, of at least one aromatic polyisocyanate compound and 10 to 90% of at least one aliphatic or alicyclic polyisocyanate compound having 2 to 6 isocyanate groups, and (C) at least one catalyst selected from complexes of organotinhalide with onium salt, complexes of organotinhalide with hexamethylphosphoramide, complexes of stibonium salt with zinc halide, and complexes of lithium halide with hexamethylphosphoramide, the equivalent ratio of isocyanate group and epoxide group being 1:2 to 2:1. A method for preparing a heat resisting molded product which comprises placing a composition as claimed in claim 4 in a mold and reacting the same at room temperature or an elevated temperature of up to 150°C. A composition as claimed in claim 4, formulated as a three pack composition, each pack containing (A), (B) or (C) separately. A composition as claimed in claim 4, formulated as a two pack composition, one pack containing (A) and the other pack (B), and (C) is contained in either one of said two packs. A composition as claimed in claim 4, formulated as a two pack composition, one pack containing (A) and the other pack (B), and (C) is divided into two complex-forming components and each component is contained in each said separate pack. A method for preparing a heat resisting molded product which comprises placing a composition as claimed in claim 6 in a mold and reacting (A) and (B) at room temperature or an elevated temperature of up to 150°C. A method for preparing a heat resisting molded product which comprises placing a composition as claimed in claim 7 in a mold and reacting (A) and (B) at room temperature or an elevated temperature of up to 150°C. A method for preparing a heat resisting molded product which comprises placing a composition as claimed in claim 8 in a mold and reacting (A) and (B) at room temperature or an elevated temperature of up to 150°C.

Inventors: IWAMOTO NORIKAZU, IWAMOTO, NORIKAZU
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1989
Main classification: C08G59
IPC codes: C08G59, C08G18