Emulsion explosive manufacturing method

Abstract: The present invention provides a means by which chemically or thermally gassed emulsion explosives can be packaged in symmetrical cartridges, such as cylindrical paper packages (15) having crimped ends. After formation, the gassed emulsion explosive is formed into a continuous strip (1) of generally constant width and height. The strip then is passed through a cooling bath (4) to cool the emulsion explosive to a predetermined temperature. A desired length of emulsion then is cut from the cooled strip, and the cut length (12) is wrapped with a paper packaging material (17) to form a cartridge (15) of emulsion explosive.

Description: The present invention relates to packaged explosives and methods of manufacture thereof and more particularly to a method of manufacturing packaged emulsion explosives. The term "emulsion" as hereafter used shall mean an oil-continuous emulsion having a continuous organic fuel phase and a discontinuous oxidizer solution phase dispersed as fine droplets throughout the fuel phase. The term "explosive" shall mean a detonable composition which can be either cap-sensitive or noncap-sensitive, as desired. The term "packaged" shall refer to cylindrical tubes or sticks of emulsion explosive of any desired length and having a diameter of generally 50 mm or less, although larger diameter products also can be made by the methods described herein. The present invention provides a means by which chemically or thermally gassed emulsion explosives can be packaged in symmetrical cartridges, such as cylindrical paper packages having crimped ends. This is accomplished with minimal migration and coalescence of the gas bubbles and consequent loss of detonation sensitivity. Product shrinkage within the package also is minimized since the product is cooled prior to packaging. More specifically, the methods of the present invention provide for cooling of the gassed emulsion prior to final packaging. After formation, the gassed emulsion explosive is formed into a continuous strip of generally constant width and height. The strip then is passed through a cooling bath to cool the emulsion explosive to a predetermined temperature. A desired length of emulsion then is cut from the cooled strip, and the cut length is wrapped with a paper packaging material to form a cartridge of emulsion explosive. In addition to working with chemically or thermally gassed emulsion explosives, the method of the invention also allows for packaging of emulsion explosives that are gassified by entrainment of gas bubbles during mixing of the emulsion or by dissolving a gas under pressure in either the oxidizer solution or fuel phase of the emulsion, which dissolved gas then effervesces upon return to ambient pressure. The method of the invention can also be used to package emulsion explosives sensitized by a combination of void containing materials with chemically or thermally generated gas bubbles. The drawings are described briefly as follows: FIG. 1 is a perspective, partially cut away view of a strip or slab of emulsion explosive entering a cooling bath by means of a conveyor belt; FIG. 2 is a perspective, partially cut away view of a strip of emulsion explosive exiting a cooling bath by means of a conveyor belt and entering a cutting and wrapping element; and FIG. 3 is a perspective, partially cut away series of views showing the various steps in wrapping a cut length of explosive into a cylindrical package having crimped ends. The drawings (not drawn to scale) show an illustrative embodiment of the method of the present invention, wherein in FIG. 1 a strip 1 of emulsion explosive exits from a dimensioning nozzle 2 (and enters the nozzle 2 by means of a conduit 3 which leads from an emulsion manufacturing source not shown) and enters a cooling bath 4, comprising a cooling liquid 5 contained within a trough 6. The strip 1 is propelled through the cooling bath 4 in the direction shown by means of a conveyor belt 7. The dimensioning nozzle 2 forms the emulsion explosive into a continuous strip 1 of desired width and height. In FIG. 2, the strip 1 is shown exiting the cooling bath 4 at point 8 by means of an inclined conveyor belt linkage 9. Dimensioning roller 10 further modifies the width and height of the strip 1. A cutting blade 11 cuts off a desired length 12 of explosive which is lifted from the bath 4 by the cutting blade 11 and then is forced by means of a pusher arm 13 into a wrapping assembly 14, in which the length 12 of explosive is wrapped with a paper packaging material to form a cartridge 15 of emulsion explosive. FIG. 3 shows the separate steps involved in wrapping a length 12 of emulsion explosive. The left figure shows the length 12 of explosive being pushed by the pusher arm 13 into a shell 16 which forms around and cylindrically shapes the length 12. Interposed between the length 12 and shell 16 is a paper packaging material 17. The next figure to the right shows the shell 16 forming around the length 12 and the rollers 18 wrapping the paper material 17 around the cylindrical explosive. The next figure to the right shows reciprocating crimping caps 19 and 20 which crimp the ends of the paper-wrapped cartridge 15. The figure on the right shows the cartridge 15 being released from the shell. The compositions of the packaged emulsion explosives comprise an immiscible organic fuel forming the continuous phase of the composition in an amount generally from about 3% to about 12% by weight of the composition; emulsifying agent; inorganic oxidizer salt solution (or melt) forming the discontinuous phase of the composition, generally comprising inorganic oxidizer salt in an amount from about 45% to about 95%; and water and/or water-miscible organic liquids preferably in an amount of from about 2% or less to about 15%. Optionally, the compositions can be formulated without any water. The "water-in-oil" emulsifying agent is employed generally in an amount of from about 0.1% to about 5% by weight. Preferred organic fuels are mineral oil, No. 2 fuel oil, paraffin waxes, microcrystalline waxes and mixtures thereof. The oxidizer salts are selected from the group consisting of ammonium, alkali and alkaline earth metal nitrates, chlorates and perchlorates. Ammonium nitrate is usually the predominant oxidizer salt, and lesser amounts of sodium nitrate or calcium nitrate are commonly used. A portion of the total oxidizer salt may be added in particle or prill form. The packaged explosives are reduced from their natural densities by addition of a density reducing agent(s) in an amount sufficient to decompose and reduce the density to within the range of from about 0.9 to about 1.4 g/cc. The method of the present invention is used to package explosives whose density has been reduced by means of chemical or thermal gassing, entrainment or pressurized dissolution, as previously described, either alone or in combination with void containing materials, for example glass or organic microspheres, or perlite. The packaging material preferably is selected from the group consisting of paper, coated paper (wax, polymer, etc.) and laminates of plastic and paper. Various packaging machines such as a Rollex machine are well-known in the art. The actual apparatus employed is not critical and can be readily selected or designed by those skilled in the art. The emulsion explosives may be formulated in a conventional manner. Typically, the oxidizer salt(s) first is dissolved in the water (or aqueous solution of water and miscible liquid fuel) at an elevated temperature of from about 25°C to about 110°C or higher, depending upon the crystallization temperature of the salt solution. The aqueous solution then is added to a solution of the emulsifying agent and the immiscible liquid organic fuel, which solutions preferably are at the same elevated temperature, and the resulting mixture is stirred with sufficient vigor to produce an emulsion of the aqueous solution in a continuous liquid hydrocarbon fuel phase. Usually this can be accomplished essentially instantaneously with rapid stirring. (The compositions also can be prepared by adding the liquid organic to the aqueous solution.) Stirring should be continued until the formulation is uniform. Solid ingredients, if any, then are added and stirred throughout the formulation by conventional means. The gassing agents then are added and uniformly mixed throughout the formulation. These agents react or decompose to produce finely dispersed gas bubbles. The formulation process also can be accomplished in a continuous manner as is known in the art. The gassed emulsion then is formed into a continuous strip of generally constant width and height, with the width preferably ranging from about 75 mm to about 400 mm and the height preferably ranging from about 20 mm to about 45 mm. The continuous strip then is fed into a cooling bath, which is aqueous, preferably water or an aqueous salt solution, at a temperature of preferably from about 2°C to about 30°C. The cooling bath can be an elongated trough of up to 100 m or more in length. The strip preferably is cooled to a center or core temperature of from about 5°C to about 40°C. This generally can be accomplished in about 5 to 30 minutes of cooling time. The cooled strip then is fed into a cutting device wherein a desired length is cut from the strip, preferably while the strip still is submerged to utilize the lubricating properties of the cooling medium. This lubrication prevents the emulsion from adhering to the mechanical parts. The length essentially is in the form of a square-shaped rod, which then is fed into a paper packaging device which shapes and wraps the cut length with paper to form a cylindrical cartridge of emulsion explosive. The cartridge preferably is in the form of a cylindrical rod, and the ends of the paper wrapper preferably are crimped. The sizes of the cartridge can vary as desired but preferably are in the ranges of from about 20 mm to about 45 mm in diameter and from about 75 mm to about 400 mm in length (which is the width of the strip). The present invention further is illustrated by the following examples in the Table, which are prepared in accordance with the above-described methods. The process parameters for the examples are as follows: 1. The emulsion is formed at an elevated temperature of 90°C. 2. The cooling bath is maintained at a temperature of 5°C. 3. The continuous strip width and height prior to packaging are 400 mm and 32 mm respectively, which dimensions also correspond to the final cartridge length and diameter, respectively. 4. The residence time in the bath is 20 minutes. 5. The cartridges in Examples A and B are wrapped with conventional manila paper used for packaging dynamite. The compositions in the examples have the detonation properties set forth in the Table. The packaged emulsion explosives of the present invention can be used conventionally, and thus they can be used in most applications where other packaged products, such as dynamites are used.

Claims: A method of forming a paper-wrapped emulsion explosive comprising: (a) forming an oil-continuous emulsion at an elevated temperature, (b) incorporating a sensitizer, into the emulsion to form an emulsion explosive, (c) forming the emulsion explosive into a continuous strip (1) of generally constant width and height, (d) cutting a desired length (12) of emulsion explosive from the strip, (e) wrapping the cut length with a paper packaging material (17) to form a cartridge of emulsion explosive (15), the strip being cooled to a predetermined temperature prior to performing the cutting and wrapping steps, characterised in that the sensitizer comprises gas bubbles uniformly distributed in the emulsion, and the strip is cooled by being passed through an aqueous cooling bath. A method according to claim 1, wherein the oil-continuous emulsion comprises droplets of oxidizer solution or melt dispersed within a continuous fuel phase and the emulsion is formed at a temperature above the crystallization temperature of the oxidizer solution. A method according to claim 2, wherein the continuous fuel phase is selected from the group consisting of mineral oil, No. 2 fuel oil, vegetable oils, paraffin waxes, microcrystalline waxes and mixtures thereof. A method according to any preceding claim, wherein the gas bubbles are incorporated by means of a gassing agent that decomposes in the emulsion to produce gas bubbles. A method according to any one of claims 1 to 3, wherein the gas bubbles are incorporated by mechanical entrainment into the emulsion. A method according to any one of claims 1 to 3, wherein the gas bubbles are incorporated by dissolving the gas under pressure in either the oxidizer solution or fuel phase, which dissolved gas then effervesces upon return to ambient pressure. A method according to any preceding claim, wherein the sensitizer additionally comprises void containing materials that are distributed throughout the emulsion. A method according to any preceding claim, wherein the center or core of the strip of emulsion explosive is cooled in a bath to a temperature of from about 5°C to about 40°C. A method according to claim 8, wherein the cooling bath is water or an aqueous solution at a temperature of at least 5°C below the desired final temperature of the cooled emulsion explosive.

Inventors: LAWRENCE LAWRENCE D, SUDWEEKS WALTER B, LAWRENCE, LAWRENCE D., SUDWEEKS, WALTER B.
Applicants: IRECO INC, IRECO INCORPORATED
Application year: 1989
Main classification: C06B21
IPC codes: F42B3, C06B21