Fixing tape

Abstract: A fixing tape is disclosed, which comprises a plastics film having a two- or three-layer construction comprising a plastics film layer and a polymer blend layer formed on at least one side of the plastics film layer, one side of the polymer blend layer facing away from the plastics film layer being a satin surface.

Description: This invention relates to a fixing tape suitable for fixing a paper diaper or a medical instrument to the human body. JP-A-63-112704 discloses a conventional tape substrate which is made of a blend of one or more of an ethylene-vinyl acetate copolymer, a polyethylene and an ethylene-propylene copolymer with a polypropylene, the polypropylene content being 5 to 75 wt%. This conventional diaper-fixing tape, used in direct contact with the skin of the baby or infant, has been proposed in view of the handle or drape and the softness in an attempt to prevent the baby skin from being subjected to a rash, redness and a laceration. However, this conventional tape substrate is not completely satisfactory because it is a little rigid. This difficulty arises from the fact that the processability encountered when producing the tape has been taken into account. Tests of this conventional diaper-fixing tape by monitors have indicated that a rash and a laceration have not appeared on the skin, but the redness on the skin has not been sufficiently improved. EP-A-0375862 which is prior art according to Art. 54(3) EPC discloses an adhesive tape for medical or sanitary use comprising a support composed of a laminate structure of a first layer containing a thermoplastic elastomer and a second layer comprising a plastic film or nonwoven fabric, and an adhesive layer formed on at least one surface of said support. It is the object of the present invention to provide a fixing tape suitable for fixing a diaper or medical instruments to the skin of the human body which tape has a good drape or handle, is so soft that it does not irritate or damage the skin, can be easily held between the fingers, and looks soft and gives a high-quality impression. Said object is achieved by a fixing tape comprising a plastics film having a two or three-layer construction comprising a plastics film layer made of at least one member of the group consisting of a polyethylene, a polypropylene, an ethylene-vinyl acetate copolymer and an ethylene-propylene copolymer, and a polymer blend layer made of a polymer blend comprising at least two resins of the group consisting of an ethylene-vinyl acetate copolymer, an ethylene-propylene copolymer and a polyethylene, formed on at least one side of said plastics film layer, one side of said polymer blend layer facing away from said plastics film layer having a satin surface. An adhesive layer may be provided on at least one surface of the plastics film by applying an adhesive agent. On the portion of the surface of the plastics film where the adhesive layer is not provided, a back face treating layer may be provided for facilitating the release of an adhesive layer of another fixing tape and the prevention of rubbing or sticking of other materials to be in contact with the fixing tape. Figs. 1(a1) and 1(a2) each is a cross-sectional view of a fixing tape provided in accordance with one embodiment of the present invention; and Figs. 1(b) to 1(d) are cross-sectional views of fixing tapes provided in accordance with another embodiments of the present invention. Fig. 2 is a front-elevational view of a diaper using the fixing tapes of the present invention. The inventors of the present invention have made an extensive study in an attempt to obtain a diaper-fixing tape which is gentler or softer to the skin, and found that the fixing tape of the above construction has increased softness and handle or drape. Since the tape has a satin surface, it can be easily held by the fingers because of the high coefficient of friction of the satin surface, and thereby facilitating the fixing of the diaper to the skin. Further, the satin surface does not have a gloss, which gives a high-quality impression. If the tape substrate is made solely of a film of polyethylene or polypropylene, or a film of an ethylene-vinyl acetate copolymer or an ethylene-propylene copolymer, which have a good handle or drape, the following disadvantages are encountered: (1) Since the surface of the film is smooth, a release agent is liable to be removed by friction. (2) Most of such films have a poor reactivity with a silicone used as a back face treating agent. (3) The film is too soft and has no nerve. (4) The film made of polypropylene is liable to be torn. The fixing tape of the present invention has a satin surface, and therefore the removal of a back face treating agent is prevented, and also the reactivity with silicone is improved, Of course, the satin surface must be free from an antioxidant and a metal which restrict the reaction with silicone. Further, the plastics film is of a two- or three-layer laminated construction, wherein the upper layer or the upper and lower layers are laminated with the polymer blend layers having the satin surface. With this construction, the fixing tape of the present invention is sufficiently soft but has an increased nerve, and can not be torn easily. Therefore, the fixing tape is suitable for fixing a diaper or other medical instruments to the human body, since the fixing tape can be freely flexed following the motion of the human body. If the satin surface is formed after fabricating the plastics film, the use of sandblast or a textured roll is required. This is undesirable since it increases the number of process steps and hence increases the costs. In the present invention, the laminated film comprising the satinized polymer blend layer and the plastic film layer of a good handle or drape can be obtained by a simultaneous molding method. Therefore, the fixing tape of the present invention can be produced at low costs. The fixing tapes of the present invention will now be described with reference to the drawings. Figs. 1(a1) and 1(a2) each shows a fixing tape A according to the present invention. The fixing tape A comprises a plastics film layer 2, and a polymer blend layer 1 formed on one side of the plastics film layer 2. An adhesive layer 3 is provided on the other side of the plastics film layer 2. In the embodiment in Fig. 1(a2), the plastics film layer 2 is composed of two layers 2a and 2b. The polymer blend layer 1 has an outer surface which is satinized. A release agent layer or back face treating layer 4 is optionally formed on the satinized surface of the polymer blend layer 1. Figs. 1(b) to 1(d) show modified fixing tapes A1 to A3 according to other embodiments of the present invention. In the fixing tape A1 of Fig. 1(b), a pair of polymer blend layers 1 and 1' are formed respectively on the opposite sides of the plastics film layer 2, each polymer blend layer having an outer satinized surface as described above in the preceding embodiment. The adhesive layer 3 is formed on the satin surface of the lower polymer blend layer 1'. A release agent layer or a back face treating layer 4 is formed on the satin surface of the upper polymer blend layer 1. In the fixing tape A2 of Fig. 1(c), the pair of polymer blend layers 1 and 1' are formed respectively on the opposite sides of the plastics film layer 2, as described above for the fixing tape A1 of Fig. 1(b). A pair of upper and lower adhesive layers 3 and 3' of a smaller width are formed respectively on the stain surfaces of the upper and lower polymer blend layers 1 and 1'. More specifically, the upper adhesive layer 3 is formed on a generally half width of the satin surface of the upper polymer blend layer 1. The lower adhesive layer 3' is formed on a generally half width of the stain surface of the lower polymer blend layer 1'. The upper and lower adhesive layers 3 and 3' are disposed generally asymmetrically with respect to the longitudinal axis or centerline of the fixing tape A2. In the illustrated embodiment, each of the upper and lower adhesive layers 3 and 3 has a width greater than half of the width of the fixing tape A2. The portions of the satin surfaces of the polymer blend layers 1 and 1' where the adhesive layers 3 and 3' are not provided are provided with the release agent layer or the back face treating layer 4. In the fixing tape A3 of Fig. 1(d), the pair of polymer blend layers 1 and 1' are formed respectively on the opposite sides of the plastics film layer 2, as described above for the fixing tape A1 of Fig. 1(b). An adhesive layer 3' is formed on a generally half of the satin surface of the lower polymer blend layer 1'. Adhesive layers 3 and release agent layers or back face treating layers 4 are formed alternately and patternwise on the satin surface of the upper polymer blend layer 1. Alternatively, both the satin surfaces of the polymer blend layers 1 and 1' may be provided with the adhesive layers 3 and 3' and the release agent layer or the back face treating layers 4 formed alternately and patternwise. Fig. 2 shows a diaper B to which fastening tapes comprising the fixing tapes of the present invention are attached. Reference characters C and D each denotes a fastening tape. The fixing tapes A and A1 of Figs. 1(a1), 1(a2) and 1(b) can be used as the fastening tapes C and D. The plastics film layer 2 of the fixing tape of each of the above embodiments has a good handle or drape. The plastics film layer 2 is made of at least one member of the group consisting of a polyethylene, a polypropylene, an ethylene-vinyl acetate copolymer and an ethylene-propylene copolymer. The plastics film layer 2 preferably has a width direction compression strength of 200 g/mm² or less, and more preferably from 40 to 100 g/mm². By using the plastics film layer having a width direction compression strength within the above range, a fixing tape having appropriate softness and nerve can be obtained. The "width direction compression strength" used herein is determined by the following manner: the plastics film sample (65 mm x 25 mm) is made a loop (diameter: 20 mm) by looping in the longitudinal direction; the loop is placed on a plate and pressed in the width direction at 23°C, 65%RH at a rate of 10 mm/min; the maximum pressing force at which the loop starts to collapse is divided by the thickness of the plastics film sample to obtain the width direction compression strength. Preferred examples of the material for the plastics film layer 2 include an ethylene/vinyl acetate copolymer having a vinyl acetate content of 4% or more, a very low density polyethylene (VLDPE), a low density polyethylene (LDPE), a linear low density polyethylene (L-LDPE), a ethylene/propylene copolymer having a ratio of ethylene/propylene of from 9/1 to 1/9, and a chlorinated polypropylene, as well as a mixture of a polypropylene with at least one of a polyethylene, an ethylene/propylene copolymer and an ethylene/vinyl acetate copolymer having a ratio of the polypropylene to the other resins of from 0/10 to 9/1, more preferably from 4/6 to 6/4. The polymer blend layer 1, which is formed on at least one side of the plastics film layer 2 and has a satin surface, is made of a polymer blend comprising at least two resins selected from the group consisting of an ethylene-vinyl acetate copolymer, an ethylene-propylene copolymer and a polyethylene. It is preferred that the polymer blend layer 1 be made of a polymer blend composed of at least one of a polyethylene and an ethylene/propylene copolymer with a polypropylene, the polypropylene content being 5 to 95 wt%, more preferably 5 to 75 wt%. In this case, a low-density polyethylene film is preferably used as the plastics film layer 2. A mixture of a polypropylene and a polyethylene having a polypropylene content of 75 wt% is most preferred for the polymer blend layer. The thickness of the plastics film composed of the polymer blend layer 1 and the plastics film layer 2 is usually from 1 µm to 1 mm, but is not limited to such a thickness. The thickness of the polymer blend layer 1 is preferably from 3 to 5 µm, and the thickness of the plastics film layer 2 is preferably from 30 to 200 µm. Such a plastic film is preferably obtained by a simultaneous extrusion molding method using a T-die. An adhesive agent for the adhesive layer 3 is not particularly limited. The adhesive layer 3 may be made of a known adhesive agent such as an acrylic type adhesive agent, a rubber type adhesive agent and a styrene type adhesive agent. The thickness of the adhesive layer 3 is usually from 5 to 500 µm, but is not limited to such a thickness. The back face treating layer can be formed by using any conventional methods and materials, and is preferably formed by coating a silicone or a long-chain alkyl release coating agent. The present invention will now be illustrated by referring to the following Examples and Comparative Examples, EXAMPLES Various films having a two- or three-layer construction were prepared using various polymers shown in Table 1. The films of a two- or three-layer construction were formed by a simultaneous extrusion molding method using a T-die, the temperature of the die being 180°C. Then, a styrene-type adhesive agent was applied to one side of each of the thus prepared films to form an adhesive layer having a thickness of 50 µm, thereby providing fixing tapes. In the samples of Example 1, 2 and 4, the adhesive layer is formed on the intermediate layer; and in the sample of Example 3, the adhesive layer is formed on the lower layer. Various tests, which include the handle or drape (softness), the nerve and the reactivity with silicone as a back face treating agent, of the thus obtained fixing tapes were carried out, and the results of the tests and total evaluation are shown in Table 1. The evaluation in the above Table 1 was conducted in the following manner: 1. Handle or drape (softness): Organoleptic tests by ten monitors were conducted to determine the feeling through the eyes and the feeling through contact with the skin. The results were indicated in terms of the number of the monitors who determined the sample having good handle or drape per total number of the monitors. 2. Nerve: Each fixing tape was adhesively bonded to a polyester plate the back face of which was treated by a long-chain alkane at 23°C, 65%RH and pressed twice with a 2 kg roller, and after 30 minutes, the fixing tape was peeled at a rate of 300 mm/min. The tape was placed on a flat plate such that the concave of the tape was made upward. The nerve was determined by checking the degree of curling in terms of the perpendicular distance between the plate and the edge of the tape. 3. Reactivity with silicone: Silicone (X-62-1148; manufactured by Shin-etsu Silicone Co., Ltd.) was coated on the upper layer (Examples 1 to 4) or the intermediate layer (Comparative Examples 1 to 3) of each substrate in an amount of 0.5 g/m², and then the substrate was heated for 30 seconds at 100°C. Subsequently, the silicone coated layer was rubbed once with the finger to check the degree of curing of the silicone coating. Thereafter, the silicone-coated film was further rubbed five times with the finger, and then a lipophilic ink was coated on the film to see how the lipophilic ink was coated thereon, thus judging the degree of removal of the silicone from the film. If the ink formed cissings, the silicone was remained and the reactivity was evaluated as good (A). If the ink was uniformly coated, the silicone was removed by rubbing and the reactivity was evaluated as poor (C). 4. Overall evaluation: The suitability of the samples for a fixing tape for fixing a diaper or a medical instrument to the human body was evaluated in view of the results of the tests 1 to 3 above. The evaluation was made in terms of excellent (A), good (B), and poor (C). As is clear from the above Table 1, it has been recognized that the fixing tape of the present invention used as a fastening tape for a diaper is hardly irritating to the skin, and has sufficient softness and nerve, so that the fixing tape material is very practical and has a good processability. Therefore, the fixing tapes of the present invention can be suitably used not only as a diaper fixing tape but also as a tape for fixing a medical instrument to the human body.

Claims: A fixing tape comprising a plastics film having a two- or three-layer construction comprising a plastics film layer made of at least one member of the group consisting of a polyethylene, a polypropylene, an ethylene-vinyl acetate copolymer and an ethylene-propylene copolymer, and a polymer blend layer made of a polymer blend comprising at least two resins of the group consisting of an ethylene-vinyl acetate copolymer, an ethylene-propylene copolymer and a polyethylene, formed on at least one side of said plastics film layer, one side of said polymer blend layer facing away from said plastics film layer having a satin surface. The fixing tape of claim 1, wherein said plastics film layer comprises two layers. The fixing tape of claim 1, wherein an adhesive layer is provided on said satin surface of said plastics film, and a release agent layer or a back face treating layer is provided on the surface of said plastics film opposite to that provided with said adhesive layer. The fixing tape of claim 1, wherein said plastic film comprises two polymer blend layers formed on both sides of said plastics film layer, one side of each of said polymer blend layers facing away from said plastics film layer having satin surfaces. The fixing tape of claim 4, wherein an adhesive layer is provided on one of said satin surfaces of said plastics film, and a release agent layer or a back face treating layer is provided on the other satin surface of said plastics film opposite to that provided with said adhesive layer. The fixing tape of claim 1, wherein said polymer blend layer is made of a polymer blend composed of at least one of a polyethylene and an ethylene-vinyl acetate copolymer with a polypropylene, the polypropylene content being from 5 to 95 wt%. The fixing tape of claim 6, wherein said plastics film layer is made of a low density polyethylene. The fixing tape of claim 4, wherein release agent layers or back face treating layers and adhesive layers are alternately and patternwise formed on each of the opposite sides of said plastics film. The fixing tape of claim 3, wherein said release agent layer or back face treating layer is made of a silicone.

Inventors: ARAKAWA MASAAKI, HORI KATSUMI, SAKASHITA TEIJI, SIBATA KAZUMASA, TAKAHASHI MAKOTO, TANAKA NAOMITA, ARAKAWA, MASAAKI, HORI, KATSUMI, SAKASHITA, TEIJI, SIBATA, KAZUMASA, TAKAHASHI, MAKOTO, TANAKA, NAOMITA
Applicants: NITTO DENKO CORP, NITTO DENKO CORPORATION
Application year: 1989
Main classification: C09J7
IPC codes: B32B27, A61F13, C09J7