PROCESS FOR PRODUCING GRAPHITE ELECTRODES

Abstract: A process for producing a graphite electrode which comprises forming a deposition layer (8) of fine globular graphite particles on a substrate (4) first, and subsequently the step of forming a metal film (9) of an iron group element or an alloy thereof on the deposition layer and forming a graphite layer (10) on the metal film to obtain an electrode having the graphite layer supported on the substrate.

Description: The present invention relates to a process for producing graphite electrodes, and more particularly to a process for efficiently producing graphite electrodes for thin batteries which are suitable as power sources for various electronic devices of small size or thickness. In preparing graphite electrodes for thin batteries or the like, iron group elements are usually used as the substrate material for depositing graphite thereon by thermal decomposition since these elements act catalytically in the thermal decomposition of various hydrocarbon compounds and further act to promote graphitization of carbon (Journal of Catalysis, 29 , 15-19(1973), Carbon, 10 , 601-611(1972)). However, when the substrate has a small specific surface area such as a common plate, it is impossible to achieve a sufficiently high deposition rate of graphite for practical purposes. The rate is still insufficiently high even if a reticular substrate is used. Accordingly, sponge metals having a large specific surface area are used solely as substrates. For example, a vapor growth process is known wherein graphite is deposited on sponge nickel by thermal decomposition (Unexamined Japanese Patent Publications SHO63-102167 and SHO 63-230512). Nevertheless, such a usual process for preparing graphite electrodes involves difficulty in controlling the amount of deposition of graphite on the surface of sponge metal because of great variations in the specific surface area thereof. Consequently, the graphite electrodes obtained vary greatly in characteristics and are not satisfactory. Further,for the efficient growth of graphite on the surface of sponge nickel substrate, the substrate needs to have a considerably large overall surface area and must therefore have a thickness at least 1 mm. In order to obtain thin electrodes, accordingly, the product of the process need to be pressed eventually to this thickness, but the pressing step breaks or releases the graphite layer formed creating the problem of reduced capacity. The present invention, which has been accomplished to overcome the foregoing problems, contemplates provision of a process for producing with ease and efficiency graphite electrodes having a high capacity and below 1 mm in thickness. From the above viewpoint, we have conducted intensive research and consequently prepared a graphite electrode by forming on a substrate a deposition layer of fine globular graphite particles larger than usual graphite particles formed on electrode substrate, covering the deposition layer with a thin metal film of an iron group element to form a surface having minute projections, and forming a usual graphite layer on the surface by the thermal decomposition CVD process. We have found that this graphite layer can be formed at a remarkably improved deposition rate and accomplishes the present invention. Accordingly, the present invention provides a process for producing a graphite electrode which comprises the steps of (a) forming a deposition layer of fine globular graphite particles on a substrate, and (b) forming on the deposition layer a metal film and subsequently forming a graphite layer on the metal film, and repeating steps (b) one or more times if desired or required, to obtain an electrode having one or more of the graphite layers supported on the substrate, both the substrate and the metal film being of an iron group element or an alloy thereof. The deposition layer of fine globular graphite particles formed on the substrate has a surface with a multiplicity of projections, which give a greatly increased surface area to the metal film covering the deposition layer. It is thought that the rate of deposition of the graphite layer can be remarkably increased by the increased surface area despite the shape of the substrate. For example, the deposition rate can be increased to about 10 to about 15 times the rate conventionally possible. With the process of the invention for producing graphite electrodes, the graphite layer can be formed at a high deposition rate on an electrode substrate in the form of a plate, rod, foil, reticular plate, net or the like and having a small surface area. Accordingly, graphite electrodes of high capacity can be produced efficiently without use of sponge metal. Since there is no need to use sponge metal, thin electrodes below 1 mm in thickness can be prepared with ease without resorting to a pressing step, while it is possible to eliminate variations in characteristics or to preclude the decrease in capacity due to the release of graphite in the pressing step. In the accompanying drawings: Fig. 1 is a schematic diagram showing an apparatus for use in an embodiment of the invention; Fig. 2 is a view in section schematically showing a graphite electrode obtained by the embodiment; and Fig. 3 is an enlarged perspective view showing the surface of a deposition layer of fine globular graphite particles formed on a nickel net by the embodiment (a sketch of photomicrograph, the blank stripes being due to reflection of light). According to the present invention, a deposition layer of fine globular graphite particles is first formed on an electrode substrate. The substrate is selected from iron group, elements and alloys thereof such as stainless steel, ferroalloys, Monel metals, permalloy, Ni-Mo alloys, Fe-Co alloys, alloys having superhigh resistance to heat, Co-Ni alloys and Co-Cr-W-Mo alloys, because these metals or alloys have catalytic activity on the thermal decomposition reaction of hydrocarbons and further promote graphitization of carbon. The substrate can be in various shapes in conformity with the shape of the electrode to be produced. For example, it is in the form of a plate, rod, foil, net or the like. Also usable when desired are porous metals or alloys, such as sponge metals, obtained by sintering or blowing. The term "fine globular graphite particles" as used herein refers to graphite particles having relatively large sizes of about 1 to about 10 µm. The deposition layer may be in the form of a single layer of such graphite particles. The deposition layer of fine globular graphite particles can be formed, for example, by thermal decomposition CVD from benzene, propane or like hydrocarbon, especially by feeding an increased concentration of hydrocarbon starting material at a low rate in the thermal decomposition CVD process. For example, a deposition layer of fine globular graphite particles, several micrometers in size, can be formed efficiently from a hydrocarbon having a molecular weight of up to 150 by using a common thermal decomposition CVD apparatus under the conditions of hydrocarbon feed rate of 0.005 to 1.5 mole/hour, molecular density of 1.3 x 10²² to 2.6 x 10²² molecules/liter, flow rate of 0.3 to 10 cm/min and thermal decomposition temperature of 450 to 1300°C, preferably 700 to 1200°C. Then, the laminating step is performed once or a plurality of times over the deposition layer. This step comprises, in combination, forming a metal film of an iron group element or an alloy thereof and subsequently forming a graphite layer on the metal film. The metal film is formed on the deposition layer from an iron group element or an alloy thereof such as ferroalloy, Monel metal, permalloy, Ni-Mo alloy, Fe-Co alloy, Co-Ni alloy or Co-Cr-W-Mo alloy. It is suitable to form the metal film usually to a thickness of about 1 to about 10 µm, for example, by vacuum evaporation, sputtering or like PVD process, or plating. While it is suitable to form the graphite layer on the metal film by the same thermal decomposition CVD process as above, the conditions therefor are not limited specifically by the conditions for forming the deposition layer of fine globular graphite particles. Various conditions can be employed which are generally useful for forming a graphite layer which exhibits satisfactory characteristics as the active component of the electrode. For example when a hydrocarbon compound having a molecular weight of up to 150 is used, the graphite layer can be formed efficiently under the conditions of hydrocarbon feed rate of 0.005 to 15 moles/hour, molecule density of 0.5 x 10²¹ to 2.6 x 10²² molecules/liter, flow rate of 0.3 to 70 cm/min, and thermal decomposition temperature of 450 to 1300°C (preferably 700 to 1200°C). However, when the procedure for forming the graphite layer over the metal film is to be executed a plurality of times, it is desirable to form the graphite layer just underlying the uppermost metal film under the same conditions as the deposition layer of fine globular graphite particles to ensure an improved deposition rate. The laminating step can be executed once or a plurality of times in accordance with the contemplated amount of graphite to be supported, the thickness of electrode, etc. For example, when an especially thin graphite electrode is to be prepared, the step is conducted once, whereas when an electrode is to be produced with an increased amount of deposited graphite, the step is repeated several times until the specified amount of graphite is deposited. Fig. 2 is a diagram showing a graphite electrode obtained by performing the laminating step over the deposition layer once. The diagram shows an electrode substrate 4, deposition layer 8 of fine globular graphite particles, film 9 of iron group element or alloy thereof, and graphite layer 10. The graphite electrode thus obtained can be used as an electrode for a battery, especially as a negative electrode for a lithium secondary battery. Example 1 Fig. 1 is a diagram schematically showing a thermal decomposition CVD apparatus for use in embodying the invention. A reaction table 3 is provided within a reactor tube 2 extending through an oven 1 and having a hydrocarbon feed inlet 5 and an exhaust outlet 6 extending to a vacuum device 7. An electrode substrate 4 in the form of a nickel net and measuring 10 mm x 10 mm x 100 µm (thickness) was placed on the table 3, and the interior of the reactor tube 2 was heated to 900°C. Next, benzene was supplied to the reactor tube 2 under the conditions of feed rate of 0.15 mole/hour, flow rate of 0.7 cm/min and molecular number density of 1.5 x 10²² molecules/liter for about 10 minutes, in accordance with the thermal decomposition CVD, whereby a deposition layer of fine globular graphite particles, about 1 to about 3 µm in diameter, was formed on the substrate 4 (i.e., nickel net) as seen in the sketch of photomicrograph of Fig. 3. Next, nickel was deposited by sputtering on the deposition layer to a thickness of 8 µm to form a nickel film. A graphite layer, weighing 10 mg, was then formed on the nickel film by depositing graphite for 20 minutes under the same conditions as employed for forming the deposition layer with the exception of changing the feed rate from 0.15 mole/hour to 1.5 mole/hour, the flow rate from 0.7 cm/min to 1.5 cm/min, the molecule number density from 1.5 x 10²² molecules/liter to 1.0 x 10²² molecules/liter, and the reaction temperature from 900° C to 950° C. The graphite deposition rate was as high as 20 mg/hour on the average. The graphite electrode obtained was 0.12 mm in thickness and was found suitable for thin batteries. Example 2 The same procedure as in Example 1 was repeated except that a nickel film was formed by electroplating after a deposition layer of fine globular graphite particles was formed on a nickel net in the same manner as in Example 1. The graphite deposition rate and the electrode thickness were comparable to the corresponding values obtained in Example 1. Example 3 A graphite deposition layer, weighing 10 mg, was formed in the same manner as in Example 1 with the exception of using 50-µm-thick iron foil in place of the 100-µm-thick nickel net as the electrode substrate and propane in place of benzene, and changing some of the conditions for forming the deposition layer on the substrate, i.e. changing the internal temperature of the reactor from 900°C to 950°C, the molecule number density from 1.5 x 10²² molecules/liter to 2.3 x 10²² molecules/liter and the deposition time from about 10 minutes to about 15 minutes. The graphite deposition rate was as high as 13 mg/hour on the average. The electrode had a thickness of 0.07 mm and was found suitable for thin batteries. Comparative Example 1 A graphite layer was formed on an electrode substrate in the same manner as in Example 1 with the exception of changing the feed rate from 0.15 mole/hour to 1.5 mole/your, the flow rate from 0.7 cm/min to 1.5 cm/min, the molecular number density from 1.5 x 10²² molecules/liter to 1.0 x 10²² molecules/liter, the reactor internal temperature from 900° C to 950° C and the graphite deposition time from 10 minutes to 10 hours. No nickel was deposited on the graphite layer. The amount of graphite thus deposited was 10 mg. The graphite deposition rate achieved was as low as 1 mg/hour on the average and was not practically useful. Comparative Example 2 A graphite layer was formed on a piece of sponge nickel serving as an electrode substrate and measuring 10 mm x 10 mm x 2.0 mm (thickness) in the same manner as in Example 1 with the exception of changing the feed rate from 0.15 mole/hour to 1.5 mole/hour, the flow rate from 0.7 cm/min to 1.5 cm/min, the molecular number density from 1.5 x 10²² molecules/liter to 1.0 x 10²² molecules/liter, the reactor internal temperature from 900° C to 950° C and the graphite deposition time from 10 minutes to 30 minutes. No nickel was deposited on the graphite layer. The amount of graphite thus deposited was 10 mg, and the graphite deposition rate was as high as 20 mg/hour on the average. However, the electrode had a large thickness of 3.2 mm. When the electrode was pressed to a thickness of 0.2 mm for use in preparing thin batteries, the graphite layer was broken and locally dislodged.

Claims: 1. A process for producing a graphite electrode which comprises the steps of (a) forming a deposition layer of fine globular graphite particles on a substrate, and (b) forming on the deposition layer a metal film and subsequently forming a graphite layer on the metal film, and repeating steps (b) one or more times if desired or required, to obtain an electrode having one or more of the graphite layers supported on the substrate, both the substrate and the metal film being of an iron group element or an alloy thereof. 2. A process according to claim 1, wherein the substrate is in the form of plate, foil or reticular plate which has a thickness of up to 1 mm. 3. A process according to claim 1 or claim 2, wherein the fine globular graphite particles have a size of 1 to 10 µm. 4. A process according to any one of claims 1 to 3, wherein the deposition layer of fine globular graphite particles is formed from a hydrocarbon having a molecular weight of up to 150 using a common thermal decomposition CVD apparatus under the conditions of a molecular density of 1.3 x 10²² to 2.6 x 10²² molecules/liter and a flow rate of 0.3 to 10 cm/min. 5. A process according to claim 4, wherein the hydrocarbon is benzene or propane. 6. A process according to any one of claims 1 to 5, wherein the metal film is of nickel or iron and has a thickness of 1 to 10 µm. 7. A process according to any one of claims 1 to 6, wherein the metal film is formed by a PVD method. 8. A process according to any one of claims 1 to 7, wherein the graphite layer is formed from a hydrocarbon having a molecular weight of up to 150 using a common thermal decomposition CVD apparatus under the conditions of a molecular density of 0.5 x 10²¹ to 2.6 x 10²² molecules/liter and a flow rate of 0.3 to 70 cm/min. 9. A process according to claim 8, wherein the graphite layer immediately underlying the uppermost metal film is formed under the conditions of a molecular density of 1.3 x 10²² to 2.6 x 10²² molecules/liter and a flow rate of 0.3 to 10 cm/min. 10. A process according to claim 8 or claim 9, wherein the hydrocarbon is benzene or propane.

Inventors: SUZUKI, TOMONARI, WADA, HIROSHI, YOSHIDA, MASARU, YOSHIMOTO, YOSHIKAZU
Applicants: SHARP KABUSHIKI KAISHA
Application year: 1989
Main classification: H01M4
IPC codes: H01M4, C23C16