USE OF PERFLUOROPOLYETHER DERIVATIVES IN THE FORM OF AN AQUEOUS EMULSION FOR PROTECTING STONY MATERIALS FROM ATMOSPHERIC AGENTS

Abstract: There is described a process for protecting marble, stone, tiles, cement and analogous materials, utilized in the buil­ ding industry, from the action of atmospheric agents and po­ lutants, by applying to the surface of the material a micro­ emulsion of perfluoropolyethers, optionally having at one end or at both ends or in the chain functional groups capable of acting as anchoring agents to the substrate.

Description: It is known that perfluoropolyethers impart remarked water-repellent and oil-repellent properties to the material surfaces onto which they are applicated. Furthermore, perfluoropolyethers exhibit a high Bunsen coefficient for the air gas components, wherefore they permit a good passage of the air through the surface of the treated materials. By virtue of these properties perfluoropolyethers are interesting as liquids useful to protect from atmospheric agents the building works and, in general, the articles made of stone, marble, cement, tiles, gypsums or wood. Furthermore, the low refraction index of perfluoropolyethers, which corresponds to a value of about 1.3 measured at 20°C with the light of a sodium-vapor lamp, causes the treated article to retain its original appearance, avoiding optical interference phenomena, which lead to a color alteration. The abovesaid use of perfluoropolyethers was described in an earlier Italian patent application No. 19,933 A/81 in the name of the Applicant. The perfluoropolyethers indicated by the above-cited prior art were of the type with chemically inert end groups, consisting of perfluoroalkyl groups. It was observed that the presence of porosity in the material to be protected led to a phenomenon consisting in a slow absorption of the perfluoropolyether type used so far, said phenomenon causing a more or less slow migration (depending on the type of the material porosity) of the protective liquid towards the innermost layers of the article. That results in a reduced effectiveness, in the course of time, of the protection of the outermost areas of the treated article. While on particular materials, for example sandstones, this inward diffusion is sufficiently slow as to secure a protection stability for a long time, in other cases (for example tiles) this phenomenon causes such a decrease in the surface protective effect as to require, in the course of time, further surface treatments, although the protection of the underlying layers remains efficacious enough to remarkably slacken the alteration phenomena. From Italian patent application No. 19,628 A/85 in the name of the Applicant it is known that it is possible to obtain a permanent protection of the surface area of the above-mentioned materials if perfluoropolyethereal derivatives with functional end groups capable of forming chemical and/or physical bonds with the substrate are used as protective agents or as coadjuvants. Said functionalized end groups fix to the substrate to be protected, thereby reducing the perfluoropolyether mobility and increasing the duration of the protective effect on the treated surface. All the systems described in patent applications Nos. 19,933 A/81, 19,628 A/85, 22,258 A/85 of the same Applicant comprise, as an essential component, a solvent, in particular a fluorocarbon or a chlorofluorocarbon. The application of said compounds to the substrate is preferably carried out by using 1,1,2-trifluorotrichloroethane in admixture with other organic solvents containing from 50 to 80% by weight of perfluoropolyethereal products. Application occurs by means of atomised liquid jet spraying, either with compressed air or without compressed air, or by means of another proper method. The perfluoropolyethereal protective agent amount utilized is strongly depending on the porosity of the material to be treated and varies from 10 g/m² to 300 g/m², as a the substrate porosity increaser. From the viewpoint of ecology and environmental protection, the advantage, which would derive from the use of systems free from chlorofluorocarbons, and optionally in the complete absence of volatile organic solvents, is evident. It has now surprisingly been found that it is possible to attain this and further advantages in the protection of works and articles made of stones, marble, cement, gypsum and wood by using, instead of perfluoropolyethers as such or in chlorofluorocarbon solutions, aqueous microemulsions of functional perfluoropolyethers. The term "microemulsion" is generally used to designate products macroscopically consisting of a single transparent or opalescent and optically isotropic liquid phase comprising two immiscible liquids and at least a surfactant, wherein one of the two immiscible liquids is dispersed in the other liquid in the form of droplets having diameters approximately ranging from 50 to 2,000 A° (500 nm to 20 µm). In principle, the presence of particles having greater or smaller sizes up to the limit of the molecular dispersion cannot be excluded. Furthermore, structures are possible, in which the two liquids are interdispersed as bicontinuous tridimensional films, or in which the two immiscible liquids are co-solubilized at a molecular level. Such products spontaneously form by simple mixing of the components when the interface tension between the two immiscible liquids decreases to values close to zero and are indefinitely stable in a certain temperature range. In the present invention, the term "microemulsion" has a broader meaning, as it comprises also non-optically isotropic systems (i.e. birefringent) characterized by a liquid-crystalline orientation of the components. There is an advantage in having available microemulsions insteads of emulsions, as the former do not require a high dispersion energy for obtaining them, are regenerable and indefinitely stable in the long run, while the emulsions must be prepared taking into account the order of addition of the components, they supply a high dispersion energy and have a limited stability in the course of time; furthermore, when they give rise to a phase separation due to ageing, often they cannot be restored to the original emulsion state even if the high energy amount necessary to obtain them is employed. The microemulsions utilized in the present invention can be of the oil-in-water type or of the water-in-oil type, and preferably of the o/w (oil-in-water) type, and consist, in the present case, of perfluoropolyethereal chain compounds, having end groups at least in part of the functionalized type and optionally peroxide bridges in the chain, and composed of mixtures of products of different molecular weight, of a perfluorinated surfactant and/or a co-surfactant such as an alkanol with 1-12 carbon atoms, and of an aqueous phase optionally comprising an electrolyte and/or an inorganic water-soluble base. The microemulsions to be used according to the present invention can be prepared by following the modalities indicated in Italian patent applications Nos. 20,910 A/86 and 19,494 A/87 in the name of the Applicant. The functional groups can be present also on branchings of the perfluoropolyethereal chain, as is described in European patent application No. 244,839. The perfluoropolyethers of the present invention can be prepared by photooxidation of C₂F₄ and C₃F₆, without any further thermal treatment and can have peroxidic bridges in the chain. It is possible also to utilize perfluoropolyethers prepared by means of a process for oxidizing in the liquid phase with molecular O₂ a mixture of C₂F₄ and/or C₃F₆ and a perfluorinated conjugated diene, with subsequent photochemical decomposition of the peroxide groups contained in the photooxidation product by thermal treatment in the presence of UV-rays, for example the ones having general formula: where m, n and p are integers, X = F or CF₃ and R f and R′ f may be functional groups or perfluoroalkyl having from 1 to 3 carbon atoms. The perfluoropolyethers of the present invention are well known from the technical and patent literature and are generally obtained as mixtures of compounds having the necessary perfluoropolyethereal structure, a molecular weight varying over a certain range and possible different end groups. The mean functionality of the perfluoropolyethers ranges from 0.1 to 4, preferably from 0.1 to 2 and more preferably from 0.2 to 1. The functional groups present in the PFPE chains can be represented by the formula: ―(B) J -Z K where J = 0 or 1, B is a divalent or polyvalent linking hydrocarbon radical, in particular an alkylene or a cycloalkylene or an arylene radical, having up to 20 carbon atoms and preferably up to 8 carbon atoms, K ranges from 1 to 3 and preferably is 1, Z is the actual functional group. "Functional group Z" means a group capable of forming a chemical and/or physical bond with the aforesaid material to be protected, and selected from: a non-aromatic, non-fluorinated organic radical containing electron doublets donor heteroatoms, or an aromatic radical, either or not containing heteroatoms, capable of giving rise to coordinative bonds or to chain transfer bonds, thereby causing different kinds of adsorption phenomena on the substrate; ―CONR²R³, ―COOR where R is H or an alkyl group having 1 to 8 carbon atoms, an aromatic or alkyl aromatic group such as benzyl; ―OH; ―NCO, ―NHR, ―COR SO₃H; polyoxyalkylene OH; quaternary ammonium. The preferred functional groups are: ―COOH, ―OH, ― polyoxyalkylene-OH, quaternay ammonium groups. The acid end group is preferably salified. As starting products it is possible to use also perfluoropolyethers with ―COF or ―SO₂F end groups which, during the preparation of the microemulsion, hydrolize to ―COOH and ―SO₃H groups. The mean molecular weight of the perfluoropolyethereal chain ranges from 1,000 to 10,000, preferably from 2,000 to 6,000. The perfluoropolyethers utilized in the present invention may contain, besides the above-mentioned functional groups, also perfluoroalkyl end groups. The perfluoropolyethers utilized in the present invention are the ones consisting of fluorooxyalkylene units selected from the following ones: (CF₂CF₂CH₂O) and in particular belonging to the following classes: with a random distribution of the perfluorooxyalkylene units, where m, n, p have such mean values as to meet the abovesaid requirements concerning the mean molecular weight; 2) R f O(CF₂CF₂O) n (CF₂O) m R′ f with a random distribution of the perfluorooxyalkylene units, where m, n have such mean values as to meet the abovesaid requirements; where R f and R′ f , either like or different from each other, can be perfluoroalkyl end groups optionally containing 1 to 3 carbon atoms or functional end groups of type (B) J -Z K , where B, J, Z and K are the same as defined hereinbefore; where m, n, p, o have such mean values as to meet the abovesaid requirements; where n has such a mean value as to meet to abovesaid requirement; 5) R f O(CF₂CF₃O) n R′ f where n has such a mean value as to meet the abovesaid requirements; 6) R f O(CF₂CF₂CF₂O) n R′ f or R f O(CH₂CF₂CF₂O) n R′ f where n has such a value as to meet the abovesaid requirements. Perfluoropolyethers of class (1) are marketed under the trade-name Fomblin® Y, those of class (2) under the tradename Fomblin® Z, all of them being produced by Montedison. Commercially known products of class (4) are Krytox® (DuPont). The products of class (5) are described in U.S. patent 4,523,039; those of class (6) are described in European patent EP 148,482 to Daikin. The products of class (3) are prepared according to U.S. patent 3,665,041. Suitable are also the perfluoropolyethers described in U.S. patent 4,523,039 or in J. Am. Chem. Soc. 1985, 107, 1195-1201. The products of classes 1, 2 and 3, which are obtained through photochemical oxidation processes, are utilizable as rough products of the photooxidation process, which contain in the chain peroxide groups ―OO― inserted between the perfluorooxyalkylene units. Perfluoropolyethers suitable for preparing microemulsions according to the invention are also the ones described in Italian patent application No. 20,346 A/86, which comprise functional groups of the above-indicated type, arranged along the chain and functional or perfluoroalkyl end groups. The microemulsions to be used in the present invention are preparable according to the methods described in Italian patent applications Nos. 20,910 A/86 and 19,494 A/87. An essential ingredient is a ionic or non-ionic fluorinated surfactant. In particular, the following ones can be cited: (a) perfluorocarboxylic acids having 5 to 11 carbon atoms and the salts thereof; (b) perfluorosulphonic acids having 5 to 11 carbon atoms and the salts thereof; (c) the non-ionic surfactants indicated in European patent application 51,526 and consisting of a perfluoroalkyl chain and of a polyoxyalkylene hydrophilic head; (d) mono- and bi-carboxylic acids derived from perfluoropolyethers and the salts thereof; (e) non-ionic surfactants consisting of a perfluoropolyethereal chain linked to a polyoxyalkylene chain; (f) perfluorinated cationic surfactants or cationic surfactants derived from perfluoropolyethers having 1, 2 or 3 hydrophobic chains. As a co-surfactant it is possible to use a hydrogenated alcohol having 1 to 12 carbon atoms, preferably 1 to 6 carbon atoms, or a fluoroalkanol. The perfluoropolyethereal protective agent amount to be used varies as a function of the nature of the material to be treated, in particular of its porosity. The total perfluoropolyether amount ranges from 7 g/m² for low-porosity materials to be protected to 100 g/m² for materials exhibiting a higher porosity. The following examples are given merely to illustrate the present invention, without being however a limitation thereof. Example 1 There were prepared three marble test pieces measuring 8 × 6.5 cm, characterized by different porosities. Each test piece was superficially treated with a microemulsion having the following composition: 37.8 g of a rough perfluoropolyether belonging to class I, having a mean functionality equal to 0.46 and a viscosimetric average molecular weight of 4,600, containing peroxide bridges (peroxide power (P.O.) = 1.02), and consisting of a mixture of polymers having different molecular weight, 6.5 ml of a solution at 10% by weight of NH₃, 111 ml of bidistilled water, 1.5 ml of an acid having a perfluoropolyethereal structure belonging to class I and an equivalent average molecular weight equal to 668, and 0.5 ml of an acid having a perfluoropolyethereal structure belonging to class I and an equivalent average molecular weight equal to 367, 21.5 ml of t.butanol. The composition by weight of the system was the following: ― aqueous phase 66,7% ― alcohol 9.8% ― fluorinated surfactants 2.0% ― rough perfluoropolyether 21.5%. This microemulsion was applicated by means of a brush or of a compressed air sprayer in such manner as to cause a total fluorinated components amount equal to about 20 g/m² to deposit onto the test piece surface. On the test pieces, the absorbed water amount was measured after 4 days. Such amount was compared with the one absorbed by four equivalent untreated test pieces, utilized as a check. The water absorption measurement was effected by causing to adhere to a face of the test pieces a rubber cylindrical gaskets, into which a measured amount of bidistilled water was introduced. At pre-established time intervals the test piece surface was dried and the absorbed water amount was determined by means of weighing. The data obtained are reported hereinafter; the absorbed water is expressed in microliters/cm² of surface. The results of this example prove that, for all the test pieces tested, the water absorption after the surface treatment with a microemulsion based on rough perfluoropolyethers is considerably reduced as compared with the corresponding untreated test pieces. Example 2 From a fibre-cement sheet, two test pieces measuring 15 × 24 cm were obtained. One of the two test pieces was left as such as a check, while onto the surface of the other test piece, by means of a compressed air sprayer there was applicated a microemulsion having the following composition: 11.8 g of a rough perfluoropolyether belonging to class I, hydrolized by hot treatment with H₂SO₄, having an average functionality equal to 0.6 and a viscosimetric average molecular weight of 4,000, containing peroxide bridges and consisting of a mixture of polymers having different molecular weight, 2.55 ml of a solution at 10% by weight of NH₃, 31.0 ml of bidistilled water, 5.8 ml of isopropanol. The composition by weight of the system was as follows: ― aqueous phase 67.1% ― alcohol 9.3% ― rough perfluoropolyether 23.6%. The total fluorinated components amount deposited on the test piece was equal to about 7 g/m². Water absorption measurements were carried out after three months by using a method analogous with the one described in the preceding example. After 2 hours, the water amount absorbed by the untreated test piece was of 41.3 mg/cm², while the water amount absorbed by the treated test piece sank to 8.7 mg/cm². Example 3 Utilized were two Carrara marble test pieces having composition and porosity like those of the test piece described in example 1 of Italian patent application No. 19,626 A/85. One of the two test pieces was superficially treated with a microemulsion having the following composition: 12.6 g of a rough perfluoropolyether belonging to class I, having an average functionality equal to 0.46 and a viscosimetric average molecular weight equal to 4,600, containing peroxide bridges (P.0.= 1.02) and consisting of a mixture of polymers having different molecular weights, 3.7 ml of a solution at 10% by weight of NH₃, 31 ml of bidistilled water, 5.73 ml of t.butanol, 1.71 g of an acid having a perfluoropolyethereal structure belonging to class I, an average molecular weight equal to 668 and the following by weight composition: ― water phase 63.40% ― alcohol 10.47% ― fluorinated surfactants 3.12% ― rough perfluoropolyether 23.10%. The microemulsion was applicated by means of a brush. It was not possible to deposit the same amount (30 g/m²) as indicated in example 1 of the above-cited patent application, because the test piece did not absorb a microemulsion amount higher than 7.7 g of total fluorinated compounds/m². The water absorption measurement was carried out in the same manner as is described in example 1 of the present invention. In the treated test piece, the absorbed water amount/cm² was equal to zero up to 30 minutes; in the untreated test piece the absorbed water amount measured after 30 minutes was, conversely, equal to 7.6 l/cm². Example 4 (comparative test) Utilized were two marble test pieces like the ones used in example 4 and having a mean porosity. One of the two test pieces was treated on the surface with a Freon solution at 50% by weight of a rough perfluoropolyether belonging to class I, having an average functionality equal to 0.57 and a viscosimetric average molecular weight equal to 4,000, containing peroxide bridges (P.0.= 1,02% by weight) and consisting of a mixture of polymers having different molecular weights. Application was carried out by means of a brush; the fluorinated compound amount deposited on the test piece surface was of 7.9 g/m². The other test piece was left as such, as a check. Water absorption measurement was carried out according to the modalities described in example 1 of the present invention. In the treated example, the absorbed water amount expressed in l/cm² was equal to 4.7 after 30 minutes, while in the untreated test piece the water amount absorbed after the same time was of 7.6. From a comparison of the data of examples 4 and 5 it is apparent that ― the amount of fluorinated compounds present on the test piece surface being equal ― the water absorption was equal to zero when the microemulsion was used (example 3), while it was reduced by about 60%, referred to the test piece as such, when a Freon solution of the fluorinated compound was used. Example 5 Two Siena brick test pieces having a mean porosity of 40% were treated with a microemulsion having the following composition: 19.8 g of a perfluoropolyether hydrolized to acid by heat treatment, belonging to class I, having a viscosimetric average molecular weight equal to 2,080 and an equivalent average weight equal to 2,860, consisting of a mixture of polymers having different molecular weights, 7 ml of a solution at 10% by weight of NH₃, 49.5 ml of bidistilled water, 5.4 g of an acid having a perfluoropolyethereal structure belonging to class I and an average molecular weight equal to 668, and 8.1 g of an acid having perfluoropolyethereal structure and an equivalent average molecular weight equal to 361, exhibiting the following composition by weight: ― aqueous phase 64.12% ― fluorinated surfactants 14.55% ― rough perfluoropolyether 21.33%. The protective efficiency was measured by means of water absorption tests on the same test pieces before and after 2 and 25 days after the treatment. "Per cent protective efficiency" means the ratio between the difference of water absorbed before and after the treatment and the water amount absorbed by the untreated material, multiplied by hundred. The water amount absorbed by a test piece was measured in accordance with the method proposed by UNESCO-RILEH (International Symposium on Deterioration and Protection of Stone Instruments, Paris, 5-9 June 1978, Vol. 5, Test II.4). The data obtained are repoted hereinafter: Example 6 Utilized were two fibre-cement test pieces measuring 15 × 10 cm. One of these test pieces was kept as a check, while the other test piece was brush-treated with a microemulsion prepared by adding to 25.44 g of a rough perfluoropolyether belonging to class I, hydrolized by hot treatment with H₂SO₄, having an equivalent average molecular weight equal to 10,000 with respect to the acid groups and a viscosimetric average molecular weight equal to 4,600, containing peroxide bridges (P.0. = 1.02) and consisting of a mixture of polymers having different molecular weights, neutralized with 1.5 ml of an ammonia solution at 10% by weight of NH₃, 76,4 ml of tridistilled water, 14.4 g of isopropanol, 2.16 g of a carboxylic acid having an equivalent average weight equal to 668 and a perfluoropolyethereal structure belonging to class I. Obtained was a system characterized by a single limpid, transparent phase, which was indefinitely stable at a temperature higher than 20 and lower than 80°C. The composition by weight of the system was the following: ― rough perfluoropolyether 21.2% ― aqueous phase 64.9% ― fluorinated surfactant 1.8% ― alcohol 12.1%. The amount of total fluorinated components deposited on the test piece was of 6.4 g/m². The obtained data are reported hereinbelow. Example 7 A low-porosity marble test piece was kept as a check. The surface of a second test piece was brush-treated with a protective agent consisting of a microemulsion prepared pared by adding to 25.44 g of a rough perfluoropolyether belonging to class I, hydrolized by hot treatment with H₂SO₄, having an average equivalent weight of 10,000 with respect to the acid groups and a viscosimetric molecular weight equal to 4,600, containing peroxide bridges (P.0. = 1.02) and composed of a mixture of polymers having different molecular weights, neutralized with 1.5 ml of an ammonia solution at 10% by weight of NH₃, 76.4 ml of bidistilled water, 14.4 g of isopropanol, 2.16 g of a carboxylic acid having an average equivalent weight equal to 668 and a perfluoropolyethereal structure belonging to class I. The resulting system was characterized by a single limpid, transparent phase, which was indefinitely stable at a temperature higher than 20° and lower than 80°C. The composition by weight of the system was as follows: ― rough perfluoropolyether 21.2% ― aqueous phase 64.9% ― fluorinated surfactant 1.8% ― alcohol 12.1%. The amount of total fluorinated components deposited on the test piece was equal to 19.1 g/m². The data obtained are reported hereinafter Example 8 Two high-porosity marbel test pieces were utilized. The first one was kept as a check, while the second one was treated with a microemulsion prepared by adding 25.44 g of a rough perfluoropolyether belonging to class I, hydrolized by hot treatment with H₂SO₄, having an average equivalent weight of 10,000 with respect to the acid groups and a viscosimetric molecular weight equal to 4,600, containing peroxide bridges (P.0. = 1.02) and consisting of a mixture of polymers having different molecular weights, neutralized with 1.5 ml of an ammonia solution at 10% by weight of NH₃, 76.5 ml of bidistilled water, 14.4 g of isopropanol, 2.16 g of a carboxylic acid having an average equivalent weight of 668 and a perfluoropolyethereal structure belonging to class I. The system obtained was characterized by a single limpid, transparent phase, which was indefinitely stable at a temperature higher than 20° and lower than 80°C. The composition by weight of the system was as follows: ― rough perfluoropolyether 21.2% ― aqueous phase 64.9% ― fluorinated surfactant 1.8% ― alcohol 12.1%. The amount of total fluorinated components deposited on the test piece was equal to 20.2 g/m². The per cent protective efficiency measured after 1 hour exhibited a value of 88.4%. Such value was unchanged after 7 hours. Example 9 Four sandstone test pieces having a porosity of 8,5% and measuring 50 × 50 × 20 cm were used. Test pieces 1 and 3 were not treated; test pieces 2 and 4 were treated by applicating, by means of a brush, a microemulsion having the following composition: 1.55 g of a rough perfluoropolyether belonging to class I, from by hot treatment, having an average equivalent weight equal to 2,860 with respect to acid groups and a viscosimetric molecular weight equal to 2,080, consisting of a mixture of polymers having different molecular weights, 0.5 ml of an ammonia solution at 10% by weight of NH₃, 9.48 g of bidistilled water, 2.2 g of isopropanol. The resulting system was characterized by a single limpid, transparent phase, indefinitely stable at a temperature higher than 25 and lower than 75°C. The composition by weight of the system was as follows: ― rough perfluoropolyether 11.3% ― aqueous phase 72.7% ― alcohol 16.0%. The amount of total fluorinated components deposited on the test pieces was of 30 g/m² for test piece 2 and of 40 g/m² for test piece 4. The treatment efficiency was evaluated on the basis of the water amount absorbed by the various test pieces in 60 minutes and is expressed by the per cent ratio of the difference between the water amount absorbed by the untreated test piece and the water amount absorbed by the test piece after it was treated, to the water amount absorbed by the untreated test piece. The test was carried out by applicating to a face of the test pieces a device consisting of a glass cylinder filled with water and connected to a graduated micropipette which permitted to measure the water amount absorbed by the contact surface of each test piece. The device is described in the document published by UNESCO-RILEM PEM No. 78,182. The absorbed water amount was read at pre-established intervals of time and the read value is expressed in g/cm² of surface. Test piece Absorbed water amount Per cent protective. Example 10 Four Siena brick test pieces having a porosity of 40% and measuring 50 × 50 × 52 cm were utilized. The first test piece was not treated; the other test pieces were brush-treated with a microemulsion having the following composition: 18.8 g of a rough perfluoropolyehter from by hot treatment, belonging to class I, having an average equivalent weight of 2,860 with respect to the acid groups and a viscosimetric average molecular weight equal to 2,080, consisting of a mixture of polymers having different molecular weights; 10 ml of an ammonia solution at 10% by weight of NH₃; 49.5 ml of bidistilled water; 5.4 g of a carboxylic acid having an average equivalent weight of 668 and 8.1 g of a carboxylic acid having an average equivalent weight of 361, each of them having a perfluoropolyethereal structure and belonging to class I. The resulting system consisted of a single limpid phase, which was stable at a temperature higher than 25 and lower than 75°C the per cent by-weight-composition of which was as follows: ― rough perfluoropolyether 21.3% ― aqueous phase 64.1% ― fluorinated surfactants 14.6%. The amount of total fluorinated components deposited on the test pieces was of 30, 60, 90 g/m² for test pieces 2, 3 and 4, respectively. The treatment efficiency was evaluated according to the method described in example 9. Example 11 Six Vicenza stone test pieces (biocalcaselenite with a porosity of 30%) were used. Test pieces 1 and 4 were not treated; test pieces 2 and 3 were brush-treated with a microemulsion having the composition indicated in example 10; test pieces 5 and 6 were treated by applicating by means of a brush a microemulsion having the following composition: 37.9 g of a rough perfluoropolyether belonging to class I, hydrolized by hot treatment with H₂SO₄, having an average equivalent weight of 10,000 with respect to the acid groups and a viscosimetric average molecular weight equal to 4,600, containing peroxide bridges (P.0. = 1.02) and consisting of a mixture of polymers having different molecular weights; 6.5 ml of an ammonia solution at 10% by weight of NH₃; 111 ml of bidistilled water; 17.2 g of ter.butanol; 0.9 g of a carboxylic acid having an average equivalent weight of 361 and 2.7 g of a carboxylic acid having an average equivalent weight of 668, each of them having a perfluoropolyethereal structure and belonging to class I. The resulting system was characterized by a single limpid phase, stable at a temperature higher than 25 and lower than 75°C and having the following per cent by-weight-composition: ― rough perfluoropolyether 21.5% ― aqueous phase 66.7% ― alcohol 9.8% ― fluorinated surfactants 2.0%. The amount of total fluorinated components deposited on the test pieces was of 90 g/m² for test pieces 2 and 5 and of 120 g/m² for test pieces 3 and 6. The treatment efficiency was evaluated according to the modalities described in example 9. Example 12 Four cement A test pieces (porosity: 18%) and two cement B test pieces (porosity: 25%) were utilized. A test piece of each cement type was left as such as a check; the other test pieces were brush-treated with the microemulsion having the composition indicated in example 10. For cement A, the amount of total fluorinated components deposited on test pieces 2, 3 and 4 was of 36, 45 and 60 g/m² respectively. For cement B, the amount of total fluorinated components deposited on test piece 2 was of 43 g/m². The treatment efficiency was evaluated according to the modalities described in example 9.

Claims: 1. A process for protecting marble, stones, tiles, cement, gypsum or wood and other analogous materials utilized in particular in the bulding sector from the deterioration action of atmospheric agents and pollutants, by applicating onto said materials a protective agent comprising microemulsions of perfluoropolyethers containing functionalized groups. 2. A process for protecting marble, stones, tiles, cement, gypsum or wood and other similar materials utilized in particular in the building sector from the deteriorating action caused by atmospheric agents and pollutants, by applicating onto said materials a protective agent selected from the products having a perfluoropolyethereal structure, consisting of sequences of fluoro-oxyalkylene units selected from: and having at least a functional end group, optionally also in the chain, said functional group being represented by the formula: ―(B) J -Z K where J = 0 or 1, B is a divalent or polyvalent linking hydrocarbon radical, in particular an alkylene or a cycloalkylene or an arylene radical having up to 20 carbon atoms, K varies from 1 to 3 and Z is a group capable of forming a chemical and/or physical bond with the abovecited material and selected from: a non-aromatic, non-fluorinated organic radical containing heteroatoms which are electron doublets donors, or an aromatic radical whether or not containing heteroatoms, capable of giving rise to coordinative bonds or to charge transfer bonds, thus causing various kinds of adsorption phenomena on the substrate; ―CONR²R³, ―COOR, where R is H or an alkyl group containing 1 to 8 carbon atoms, an aromatic or alkyl-aromatic group such as benzyl; ―OH; ―NCO, ―NHR, ―COR; SO₃H; polyoxyalkylene OH; quaternary ammonium; and characterized furthermore in that the perfluoropolyethereal product is applicated in the form of an aqueous microemulsion. 3. The process of claim 2, wherein the perfluoropolyethers utilized for preparing the microemulsion are obtained by photo-oxidation of C₂F₄ and/or C₃F₆. 4. The process of claim 3, wherein the perfluoropolyethers utilized for preparing the microemulsion are obtained through an oxidation process in the liquid phase with molecular oxygen in the presence of ultraviolet rays, of a mixture of C₂F₄ and/or C₃F₆ and a perfluorinated conjugated diene at a temperature ranging from -80°C to 50°C, and subsequent heat treatment. 5. The process of claim 4, wherein the perfluoropolyethers utilized for preparing the microemulsions have one of the following formulas: where m, n, p are integers different from zero and R f and R′ f can be COF groups or perfluoroalkyls having 1 to 3 carbon atoms. 6. The process of claim 2, wherein the perfluorooxyalkylene units belong to the following classes: with a random distribution of the perfluorooxyalkylene units, where m, n, p have such mean values as to meet the abovesaid requirements concerning the mean molecular weight; where R f and R′ f , either like or different from each other, can be perfluoroalkyl end groups containing 1 to 3 carbon atoms and at least one fo said end groups is a functional group of type (B) J -Z K , where B, J, Z and K are the same as defined hereinbefore; 2) R f O(CF₂CF₂O) n (CF₂O) m R′ f with a random distribution of the perfluorooxyalkuylene units, where m, n have such mean values as to meet the abovesaid requirements; where R f and R′ f can be perfluoroalkylene end groups having 1 to 3 carbon atoms and at least one of said end groups is a functional groups of type (B) J -K K where B, J, Z, K are the same as defined hereinbefore; where m, n, p, o have such mean values as to meet to abovesaid requirements and R f and R′ f are the same as defined hereinbefore; where n has such an average value as to meet the abovesaid requirements and R f and R′ f are the same as defined hereinbefore; 5) R f O(CF₂CF₂O) n R′ f , where n has such an average value as to meet the abovesaid requirements and R f and R′ f are the same as defined hereinbefore; 6) R f O(CF₂CF₂CF₂O) n R′ f or R f O(CH₂CF₂CF₂O) n R′ f , where n has such an average value as to meet the abovesaid requirements and R f and R′ f are the same as defined hereinbefore. 7. The process of claim 2, wherein the functional perfluoropolyethers have a molecular weight ranging from 1,000 to 10,000. 8. The process to claim 2, wherein the functional perfluoropolyethers have a molecular weight ranging from 2,000 to 6,000. 9. The process to claim 2, wherein said microemulsions are of the oil-in-water type or of the water-in-oil type. 10. The process of claim 2, wherein K is equal to 1 and B has up to 8 carbon atoms. 11. The process of claim 2, wherein Z is selected from COOH, OH, polyoxyalkylene OH, quaternary aminic groups. 12. The process of claim 11, wherein the acid end group is salified.

Inventors: LENTI, DARIA, DR., VISCA, MARIO, DR.
Applicants: AUSIMONT S.P.A.
Application year: 1989
Main classification: C04B41
IPC codes: C04B41, C09K3, C08G65