Organic coating for metals

Abstract: The present invention provides a thin continuous organic coating on metals, particularly on continuous metal bodies, so that the product obtained is weldable and resistant to corrosion as well as to the effect of strongly acid and strongly alkaline baths, while being punchable and paintable. The coating according to the invention comprises organic resins characterized by ultimate elongation higher than 10%, electrical insulation resistance less than 2000 Ohm/cm², able to produce a continuous coating on the metal substrate with micro-roughnesses (Ra) of about 3 µm - being Ra the average roughness - and capable of withstanding for thirty minutes liquids with pH between 2 and 12,5.

Description: Present invention refers to an organic coating for metals such as Fe, Al and Cu, for instance, particularly continuous metal bodies like wires, strips or sheets, particularly of steel. Such metal bodies are usually subjected to protective surface treatment. In particular, steel sheet used in the automotive industry to produce car bodies must possess very high resistance to cosmetic and perforating corrosion, so it may be subjected to zinc-based surface treatments, after which it is painted. In the case of such coatings, the Zn, which is sacrificial vis-à-vis Fe, oxidizes in the place of the latter. However, as the products of Zn oxidation have a high surface area, they produce blisters that adversely affect the appearance of the covering paintwork. Moreover, during mechanical deformation and forming, electrogalvanized sheets tend to produce a large quantity of debris (powdering). Consequently, the surface of the sheet becomes marked and pitted and the coating is lost, so the amount of protection is decreased. In order to improve corrosion resistance, therefore, organic coatings have been developed that can be applied directly to the bare sheet or to sheet that has been coated as indicated above. It has been found that the thickness of the organic coatings is a critical parameter, because although a thick coating increases corrosion resistance, it also reduces sheet weldability. When applied in very thin layers (e.g. 2 µm or less), organic coatings obtained with conventional resins have been considered unsatisfactory from the corrosion point of view (see pages 81 to 90 of SAE December 1986). The same article describes the development of thick organic coatings containing metal fillers which are added to obtain a good compromise between corrosion resistance and weldability when applied to metals. However, these fillers further intensify the quantity of powder produced during forming, hence aggravating the problems of sheet pitting. Furthermore, the fillers tend to settle out when the resin is being applied, causing serious applications problems. An improvement in the field of organic coatings has been made with the introduction of silicate-modified resins as described on pages 49 to 54 of Nippon Kokan Technical Report Overseas No 34 (1982). But although these resins are applied in very thin layers, even in the order of 1 µm, and are satisfactory from the weldability aspect, they are unsatisfactory where corrosion is concerned, especially following the alkaline degreasing to which the sheet is subjected after car-body assembly. This unsatisfactory behaviour probably stems from poor adhesion of the organic coating to the metal, very likely because of coating deterioration in an alkaline medium. Furthermore, because of the high temperature required for curing the resins employed, there is a decline in the mechanical properties of the metal substrate. LU-A-8 571 7 discloses an acid bath for coating metal sheets. The resulting coating is characterized by the presence of an inorganic part (constituted by phosphates) for which the resin acts as a binder. Such inorganic part is present in large amounts in the coating. DE-A-1 570 860 discloses a spot-weldable coating based on epoxide compounds having low molecular weight. The process disclosed provides that the coating be applied onto the sheets to be welded; then the welding is performed and after the welding the coated sheet is subjected to a thermal post-treatment above 100°C to perform the final hardening of the coating. Drawbacks come from the too long and unacceptable times involved in said post-treatment and from the welding step, that must be performed before the final drying of the coating. Quite evidently, therefore, an organic coating is needed that has better characteristics than those previously known. A continuous organic coating thus been developed, as per this invention, for application to metals, especially continuous metal bodies, the coating being thin and such that the ensuing coated product is weldable, resistant to corrosion and to the effects of strongly acid and strongly alkaline baths, as well as being punchable and paintable. The coating which forms the object of this invention includes organic resins characterized by ultimate elongation greater than 10%, electrical insulation resistance less than 2000 Ohm/cm 2 , around thirty minutes resistance to liquids with a pH in the 2 to 12.5 range, capability of coating micro-roughnesse (Ra) of about 3 µm where Ra is the average roughness parameter, said resins being selected among solid epoxy resins having epoxy equivalent comprised between 500 and 2000, said coating being obtained by dispersing the resins in an aqueous vehicle or by dissolving them in a solvent chosen between cellosolve, methyl ethyl ketone and isobutyl alcohol containing also a curing agent selected between amines, amine adducts, melamines, phenolic resins, isocyanates and polysulphides, and applying the solution thus obtained onto said metal bodies, said solution having a viscosity ranging between 2 and 100 cP at 25°C when the same is applied on metals by applicator rollers made of rubber having hardness between 5 and 60 Shore A. Hot or cold cross-linking or non cross-linking resins which can be applied as-is or dissolved in solvent or in a dispersion so as to produce continuous coatings with a thickness of 2µm or less and preferably between 0.5 and 1µm can be advantageously used for this purpose. If the selected resin is of the hot cross-linking type, the resin should preferably cure at temperatures no higher than 200°C. Resins with a curing rate not exceeding two minutes are preferred. The resins as per this invention can be applied for instance by dispersing them in an aqueous vehicle or by dissolving them in suitable solvents such as ketones, ethers, alcohols and in known aliphatic and aromatic compounds in general. The resins can be applied on the metal substrate using known techniques such as, for instance, electrophoresis. However, the following known methods are particularly advantageous for obtaining uniform coatings having a constant thickness of between 0.5 and 2.0 µm on continuous sheet: dipping the sheet in the coating bath containing the resins and regulation of thickness by means of grooved or sanded squeeze rollers coating using applicator rollers of the coil-coating type with a system of two or more rollers In the case of this particular procedure, tests have been made on rollers with different degrees of hardness using solutions or dispersions containing resins of various viscosities. It has been found that the best results as regards thickness and continuity of the deposited resin layer are obtained with rubber applicator rollers of hardness between 35 and 60 Shore A, and with the resin solution or dispersion at a viscosity between 2 and 100 cP at 25°C, preferably 2 to 20 cP. Resin adhesion to the metal substrate can be improved by known treatments such as chromate passivation, mixed oxide conversion and phosphating or by treatments like that described in USP 4 547 268. A particularly interesting method of embodiment of the invention involves the use of epoxy resins: in organic solvents such as cellosolve, methyl ethyl ketone, isobutyl alcohol, and curable with amines, amine adducts, phenolic resins, isocyanates and polysulphides known to the experts working in the field in aqueous dispersion, applicable also via electrophoresis and curable with blocked isocyanates or melamine catalyzers, also known. Some formulations within the ambit of the present invention are indicated below: Formulation 1 A) Solid epoxy resin (epoxy equivalent 500) in 2 to 20% solution by weight in a solvent consisting of: 2 parts by weight of methyl isobutyl ketone 4 parts by weight of xylene 1 part by weight of isobutyl alcohol. B) Isolated polyamine adducts in 50% solution by weight (equivalent active H about 370) in solvent consisting of: 4 parts by weight of xylene 4 parts by weight of polyglycol monomethyl ether 1 part by weight of isobutyl alcohol. A-B mixing ratio of 100/75. Hardening can occur by curing at room temperature where needed for particular production problems or preferably at a temperature of 180°C. Formulation 2 A) Solid epoxy resin (epoxy equivalent 1500-2000) in 3 to 20% solution in solvent consisiting of: 1 part by weight of diacetone alcohol or cellosolve 1 part by weight of toluene or cellosolve acetate B) Phenolic resin, 70% by weight in butyl alcohol. B is added to A in quantities equal to 60-70% of A. Hardening occurs in the presence of known basic accelerators equal to 0.1-0.5% by weight of the mix at temperatures between 160 and 200°C. Coatings as per the invention, applied on metal substrates at thicknesses of less than 2 µm, are continuous and cause no welding problems. Furthermore the coated bodies give excellent results when subjected to mechanical working, such as bending, deep drawing and forming. These bodies also acquire greater corrosion resistance and compatibility with such organic materials as cataphoretic and noncataphoretic paints applied subsequently. A further advantage of products coated as per the invention stems from the fact that their use results in a decrease in the consumption of phosphating reagents used in the automotive industry, since these come to be applied only on such metal parts as are not resin coated. The use of protective and forming oils is also eliminated. Then, too, companies engaged on the production of household electrical appliances or on coil coating can advantageously use products coated as per the invention, since they can thus eliminate from the manufacturing process surface conversion treatments prior to painting. Plants can therefore be simpler and there are also ecological advantages, since polluting baths do not have to be used. To explain the invention in greater detail a number of examples are given, but these must in no way be construed as limiting the scope and purposes of the invention. The tests were performed on 0.75 mm thick steel specimens, two-side galvanized with Zn thickness of about 8 µm and roughness Ra of 1.8 to 2.0 µm. The organic coating was applied to these specimens whose surfaces were activated through mixed oxide surface conversion obtained by using Italbonder's commercial product, Bonderite. The application was made by dipping the specimens in the solution described as Formulation 1, the thickness of the resins being controlled by two squeeze rollers. The average thickness of resin on the specimens was 0.8 µm. The results of the characterization tests on the specimens coated as per the invention were compared with the corresponding results for bare specimens without any organic coating. I Resistance to degreasing alkaline and acid phosphating baths Degreasing bath: Industrial type alkaline soap, 5% concentration in water, pH 12, T 60°C, immersion time 7 minutes. Phosphating bath: Industrial type zinc phosphating, pH 2.2, T 55°C, immersion time 3 minutes. The coated specimens remained unaltered after immersion in the baths. The percentage of area found to have been destroyed or peeled off after this operation was less than 1% according to microscopic assessment. II Corrosion resistance Test conditions as per ASTM B117 with evaluation of the increase in time to appearance of red rust compared with specimens without the organic coating. The coated specimens exhibited an increase in corrosion resistance more than 300% compared with the bare specimens. III Cataphoretic paintability and paint adhesion to substrate It was found that, under the same operating conditions, the thicknesses of cataphoretic paints deposited on the bare and the coated specimens are identical. Wet Adhesion and Cathodic Wet Adhesion, between cataphoretic paint and organic film is comparable or better than that between paint and the best phosphate treatment for zinc. A = industrial phosphating cycle with high-Zn phosphating bath B = industrial phosphating cycle with Zn/Ni/Mn phosphating bath WA= Wet Adhesion CWA=Cathodic Wet Adhesion Wet Adhesion Conditions: Incised with 2x2 mm grid Immersion in distilled water at 40°C for one week Covering test area with adhesive tape strip, and removing the same Evaluation with automatic image analyzer (QTM) of percent area of paint removed by the tape strip. Cathodic Wet Adhesion Conditions: Incised with 2x2 mm grid Immersion in 0.5 N NaCl solution at room temperature for 24 h and contemporary imposition of 30 µA/cm 2 cathodic current Covering test area with adhesive tape and removing the same QTM evaluation of percentage of paint removed by tape strip. IV Wear resistance during forming This test is performed pulling a strip of material through a clamping device having either a flat clamp and a convex clamp (flat tools) or a concave clamp and a convex clamp (draw-bead tools). In the latter case the strip moves obviously in a curved path. In our tests bare and coated strips of 15x350 mm and 30x350 mm (with flat tools) and of 15x350 mm (for draw-bead tools) were pulled for 200 mm through testing devices, with a speed of 500 mm/min. Bare specimens were lubricated. It was observed that un-lubricated coated strips suffered much less surface damage than lubricated bare specimens; in fact detritus collected from tests of bare specimens was 400% more abundant than detritus collected from tests of coated specimens. V Weldability Spot weldability conditions for sheet with an organic film are broader and there is a shift towards lower currents. After 3000 spot welds on a pair of two-side-clad, superimposed sheets, there was no evidence of variations in the shear strength of the weld. Weldability conditions Electrode diameter 5.5 mm Clamping load 2.3 kN Hold time (HT) 30 cycles (50 Hz)

Claims: Organic layer having a thickness of 2 or less µm, coated on metals, particularly continuous elongated metal bodies, such that obtained coated product is weldable, resistant to corrosion as well as to strongly acid and strongly alkaline baths, while being punchable, deformable and paintable, said coating consisting of organic resins having an ultimate elongation in excess of 10%, electrical insulation resistance less than 2000 Ohm/cm 2 , around thirty minutes resistance to liquids with a pH in the 2 to 12.5 range, capability of coating micro-roughnesse (Ra) of about 3 µm where Ra is the average roughness parameter, said resins being selected among solid epoxy resins having epoxy equivalent comprised between 500 and 2000, said coating being obtained by dispersing the resins in an aqueous vehicle or by dissolving them in a solvent chosen between cellosolve, methyl ethyl ketone and isobutyl alcohol containing also a curing agent selected between amines, amine adducts, melamines, phenolic resins, isocyanates and polysulphides, and applying the solution thus obtained onto said metal bodies, said solution having a viscosity ranging between 2 and 100 cP at 25°C when the same is applied on metals by applicator rollers made of rubber having hardness between 5 and 60 Shore A. Organic continuous coating according to claim 1 in which the resins are selected among those that cure at temperature no higher than 200°C. Organic continuous coating according to claim 1 in which the resins are selected among those that cure in a time not exceeding 2 minutes. Organic continuous coating according to claim 1 having a thickness ranging between 0.5 and 1 µm. Organic continuous coating according to claim 1 in which the resins are dissolved in an organic solvent chosen between cellosolve, mehtyl ethyl ketone, isobutyl alchol, and are cured by a compound chosen between amines, amine adducts, melamines, phenolic resins, isocyanates and polysulphydes. Organic continuous coating according to claim 1 in which the resins are dispersed in water and cured by blocked isocyanates or melamine catalyzers. Process for to obtain a continuous organic coating according to claims 1-7 in which the application of the resins is performed according to the coil coating technique. Process to obtain a continuous organic coating according to claims 1-7 in which the application of the resins is performed according to the electrophoretic technique. Metal bodies coated with a continuous organic coating according to claims 1-7.

Inventors: COLAIACOVO FERDINANDO, DERCHI DOMENICO, MEMMI MASSIMO, COLAIACOVO, FERDINANDO, DERCHI, DOMENICO, MEMMI, MASSIMO
Applicants: SVILUPPO MATERIALI SPA, CENTRO SVILUPPO MATERIALI S.P.A.
Application year: 1989
Main classification: C09D163
IPC codes: C09D163, B05D1, B05D7, B32B15