Non-hairing moisture curable compositions

Abstract: A mixture of hydroxy functional polymers which can be used to form isocyanate prepolymers which are non-hairing at application temperature are disclosed. Examples of suitable mixtures of hydroxy functional polymers that can be used to form the prepolymers are: (1) linear polyester blends, comprising a first and second polyester wherein each polyester is the reaction product of a polyol and a polyacid, wherein a + b < or = 4, c + d > or = 6 a + b > 4 or ≦ 6, c + d > or = 10 a + b > 6 or ≦ 8, c + d > or = 12 herein a is the number of methylene moieties in the polyol used to form the first polyester, b is the number of methylene moieties in the polyacid used to form the first polyester, c is the number of methylene moieties in the polyol used to form the second polyester of the blend, d is the number of methylene moieties in the polyacid used to form the second polyester of the blend; and (2) a blend of at least one non-linear polyester and one linear polyester, wherein the non-linear polyester is selected from the group consisting of polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from the group consisting of polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; and (3) a blend of poly ε-caprolactone and at least one linear polyester selected from the group consisting of polyethylene adipate, polyethylene succinate and polybutylene succinate.

Description: This invention relates to polyurethane hot melt compositions. Such compositions are useful as adhesives, coatings and sealants for example. Polyurethane compositions are desirable in a variety of applications because of their excellent properties. They can be one-part and two-part solvent-borne systems, water-based systems or 100%-reactive solvent-free adhesive systems. Of particular utility are the reactive hot melt urethane adhesive systems which combine the rapid set or crystallization times of conventional hot melt adhesives with the high bond strengths of a curing system. Like conventional hot melts, the reactive hot melt urethane adhesives are solid at room temperature, melt to a viscous liquid when heated to moderate temperatures (82-121°C), and are applied in the molten state. The adhesive then cools to a solid state to provide initial bond strength (i.e., green strength) and additionally, cures on contact with ambient moisture to provide its final bond strength. These urethane-based systems are superior to conventional hot melt adhesives which lack resistance to solvents and heat, have lower bond strengths, and which can creep under load because they are non-curing. In general, hot melt systems, including the urethane-based systems, suffer from the disadvantage of "stringing" or "hairing" during application at dispensing temperatures, especially in automated dispensing equipment. By stringing or hairing is meant that during application by extrusion, thin threads of the molten system form at the applicator tip when it is removed from the point where the hot melt adhesive has been deposited. Hairing is undesirable in many applications such as electronic assembly, because of the contamination it introduces. Additionally, hairing can contaminate the work station and application equipment. The present invention overcomes this problem by providing a moisture curable, non-hairing hot melt composition of simple formulation. In certain embodiments, the composition also exhibits improved crystallization rates and possesses high green strength. Chemical Abstracts 108 :23061h (1988) discloses polyurethane adhesives composed of one or more polyester diols of MW 700 to 2500 having 2 to 4 methylene groups per diol and another polyesterdiol of MW 1000 to 3500 having 5 to 10 methylene groups per diol which are reacted with a diisocyanate. One such adhesive specifically disclosed is made from 25 parts poly(1,6-hexylene adipate)diol (MW=2600) 75 parts poly(ethylene 1,4-butylene adipate)diol (MW=1000) and 20.6 parts xylylene diisocyanate. In accordance with the present invention there is provided a non-hairing, moisture curable hot melt composition having a number average molecular weight between 1,000 and 10,000 comprising the reaction product of two or more hydroxy-functional polymers with polyisocyanates wherein said hydroxy functional polymers are selected from: (1) linear polyester blends comprising a first and second polyester, wherein each polyester is the reaction product of a polyol and a polyacid, wherein a + b < or = 4, c + d > or = 6 a + b > 4 and ≦ 6, c + d > or = 10 a + b > 6 and ≦ 8, c + d > or = 12 wherein a is the number of methylene moieties in the polyol used to form the first polyester, b is the number of methylene moieties in the polyacid used to form the first polyester, c is the number of methylene moieties in the polyol used to form the second polyester of the blend, d is the number of methylene moieties in the polyacid used to form the second polyester of the blend; and (2) a blend of at least one non-linear polyester and one linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; and (3) a blend of poly ε-caprolactone and at least one linear polyester selected from polyethylene adipate, polyethylene succinate and polybutylene succinate. The isocyanate-terminated mixture preferably has a number average molecular weight of 1,000 to 6,000, and most preferably of 3,000 to 4,500. Additionally, the mixture preferably forms an essentially non phasing blend at application temperature (about 100°C). By essentially non phasing is meant that, on visual inspection of the melt, there is no gross separation of the hydroxy functional polymers after extended (e.g. 1 hr.) heating at 100°C. The invention also provides a method for bonding substrates which comprises contacting a substrate with a bond-forming amount of a hot melt moisture curable composition in accordance with the present invention. There is also provided a mixture of hydroxy functional polymers comprising (1) linear polyester blends, comprising a first and second polyester wherein each polyester is the reaction product of a polyol and a polyacid, wherein a + b < or = 4, c + d > or = 6 a + b > 4 and ≦ 6, c + d > or = 10 a + b > 6 and ≦ 8, c + d > or = 12 wherein a is the number of methylene moieties in the polyol used to form the first polyester, b is the number of methylene moieties in the polyacid used to form the first polyester, c is the number of methylene moieties in the polyol used to form the second polyester of the blend, d is the number of methylene moieties in the polyacid used to form the second polyester of the blend; and (2) a blend of at least one non-linear polyester and one linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; and (3) a blend of poly ε-caprolactone and at least one linear polyester selected from polyethylene adipate, polyethylene succinate and polybutylene succinate. There is also provided a blend of hydroxy-functional polymers comprising (1) linear polyester blends, wherein the polyester is the reaction product of a diol and a diacid, wherein a + b = 4, c + d > or = 6 a + b = 6, c + d > or = 10 a + b = 8, c + d > or = 12 wherein a is the number of methylene moieties in the diol used to form the first polyester, b is the number of methylene moieties in the diacid used to form the first polyester, c is the number of methylene moieties in the dial used to form the second polyester, d is the number of methylene moieties in tee diacid used to form the second polyester; and (2) a blend of a linear and a non-linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; (3) a mixture of polyethylene adipate and polyhexamethylene adipate; or (4) a mixture of linear polyesters wherein one of the liner polyesters is poly ε-caprolactone and the others are selected from polyethylene adipate, polyethylene succinate and polybutylene succinate. The preparation of isocyanate-terminated prepolymers is well known in the art. Suitable prepolymers with residual isocyanate groups are formed by reaction of (1) a mixture of two or more hydroxy functional polymers as defined above wherein the total mixture generally has a combined number average molecular weight of 1,000 to 10,000, preferably of 1,000 to 6,000, and more preferably of 3,000 to 4,500 and (2) a polyisocyanate, preferably a diisocyanate. The prepolymer is preferably at least partially comprised of crystalline or semicrystalline polyester diols. Preferred polyesters have melting points between 30°C and 80°C, most preferred between 40°C and 60°C. Amorphous polyesters with glass transition temperatures up to 50°C may be useful in blends at less than 50% total polyester weight. In certain cases liquid polyesters may be useful in blends of polyesters at less than 30% total polyester weight. Such preferred polyesters can be prepared by reacting a diol with a diacid or derivatives of diacids. Especially preferred are polyesters prepared by reacting short chain diols having the structure HO-(CH₂) x -OH, where x is from 2 to 8, with diacids having the structure HOOC-(CH₂) y -COOH, where y is from 1 to 10. Examples of useful diols include ethylene glycol, 1,4-butanediol, 1,6-hexanediol; 1,4-cyclohexane dimethanol, neopentyl glycol and 1,2-propylene glycol. Examples of useful diacids include adipic, azelaic, succinic, and sebacic acids. Small amounts of triols, polyethers and up to 30 mole percent of other diacids and anhydrides such as isophthalic, terephthalic, cyclohexane dicarboxylic acid and phthalic anhydride may also be useful in the preferred polyester synthesis. Examples of commerically available polyesters that are useful in the compositions of the invention are the "Lexorez" (Registered Trade Mark) series commerically available from Inolex Chemical Co. Specific examples of such resins include Lexorez 1130-30P, Lexorez 1150-30P, and Lexorez 1110-25P. Examples of other commercially available polyesters useful in the invention are the "Rucoflex" (Registered Trade Mark) series of resins available from Ruco Polymer Corporation. An example of a commerically available polylactone that is useful in the invention is "Tone-0260" (Registered Trade Mark), commercially available from Union Carbide. Component ratios can be determined by the performance properties desired. Particularly preferred mixtures of hydroxy functional polymers are: (1) linear polyester blends, wherein the polyester is the reaction product of a diol and a diacid, wherein a + b = 4, c + d > or = 6 a + b = 6, c + d > or = 10 a + b = 8, c + d > or = 12 wherein a, b, c, and d are as described above. (2) a blend of a linear and non linear polyesters, wherein the non linear polyester is selected from the group consisting of polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from the group consisting of polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; (3) a mixture of polyethylene adipate and polyhexamethylene adipate; or (4) a mixture of linear polyesters wherein one of the linear polyesters is poly ε-caprolactone and the others are selected from the group consisting of polyethylene adipate, polyethylene succinate and polybutylene succinate. The ratio of polyesters employed in the invention can vary in the composition. However, it has been found preferable to employ a weight ratio of first to second polyesters in the range of between about 85:15 to 15:85, more preferably 80:20 to 20:80, most preferably 70:30 to 30:70. The polyisocyanates which are reacted with the hydroxy functional polymers to form the prepolymers used in the instant invention can be aliphatic or aromatic. Preferably they are aromatic diisocyanates such as diphenylmethane-2,4'-diisocyanate and/or 4,4'-diisocyanate; tolylene-2,4-diisocyanate and -2,6-diisocyanate and mixtures thereof. Other examples include: naphthylene-1,5-diisocyanate; triphenylmethane-4,4'4''-triisocyanate; phenylene-1,3-diisocyanate and -1,4-diisocyanate; dimethyl-3,3,-biphenylene-4,4'-diisocyanate; diphenylisopropylidine-4,4'-diisocyanate; biphenylene diisocyanate; xylylene-1,3-diisocyanate and xylylene -1,4-diisocyanate. A list of useful commercially available polyisocyanates is found in the Encyclopedia of Chemical Technology , Kirk-Othmer, 2nd Ed., Vol. 12, pp. 46-47, Interscience Pub., N.Y. (1967), which list is incorporated herein by reference. Especially preferable isocyanates include diphenylmethane-4,4'-diisocyanate (MDI) and tolylene-2,4-diisocyanate/tolylene-2,6-diisocyanate (TDI) and mixtures thereof. Isocyanate-functional derivative(s) of MDI and TDI may be used, such as liquid mixtures of the isocyanate-functional derivative with melting point modifiers (e.g., mixtures of MDI with polycarbodiimide adducts such as "Isonate 143L" (Registered Trade Mark), commercially available from the Dow Chemical Co., and "Mondur CD" (Registered Trade Mark), commercially available from Mobay Chemical Corp.; small amounts of polymeric diphenylmethane diisocyanates, preferably 10% or less by weight of the total isocyanate component, (e.g., "PAPI", and the series "PAPI 20" through "PAPI 901" (Registered Trade Marks), commercially available from the Dow Chemical Co., "Mondur MR", "Mondur MRS", and "Mondur MRS-10" (Registered Trade Marks), commercially available from Mobay Chemical Corp., and "Rubinate M" (Registered Trade Mark)", commercially available from ICI Chemicals, Inc.); and blocked isocyanate compounds formed by reacting aromatic isocyanates or the above-described isocyanate-functional derivatives with blocking agents such as ketoximes. Such blocked isocyanate-functional derivatives, will for convenience, be regarded herein as isocyanate-functional derivatives of MDI and TDI. The isocyanate should preferably be present in the prepolymer composition in an equivalent amount greater than that of the hydroxy containing component. The equivalent ratio of isocyanate to hydroxyl is preferably from about 1.2 to about 10 to 1.0 and especially preferably from about 1.6 to 2.2 to 1.0. The compositions of the invention can optionally contain other ingredients or adjuvants if desired. For example, chain extension agents (e.g., short chain polyols such as ethylene glycol or butanediol) fillers (e.g. carbon black, metal oxides such as zinc oxide, and minerals such as talc, clays, silica, silicates), thermoplastic resins, plasticizers, antioxidants, pigments, U.V. absorbers, adhesion promoters such as silanes may be included to impart particular characteristics to the composition. They should be added only to the levels that do not interfere with the non-hairing characteristic of the composition. These adjuvants generally comprise up to 50 weight percent of the composition either individually or in combination. In addition, the compositions can optionally contain an effective amount of catalyst or reaction accelerator such as tertiary amines, metal-organic compounds, co-curatives such as oxazolidine. Dibutyltin dilaurate is a preferred metal organic catalyst. An effective amount of metal-organic catalyst is preferably from about 0.01 to 2 percent by weight of the prepolymer. More preferably, the catalyst is present at a level of about 0.05 to about 1 percent, based on the weight of the prepolymer. The adhesive compositions of the invention may be prepared by mixing the components at elevated temperature, using conventional mixing techniques. It is preferred to mix the components under anhydrous conditions. Generally, preparation of the adhesive is done without the use of solvents. The hot melt compositions of the invention achieve their initial, or green, strength through crystallization, then continue to cure by exposure to water, e.g., water vapor or moisture. High humidity and heat will provide an accelerated rate of cure while low humidity (e.g., 15% R.H. or less) will provide a slower rate of cure. While the composition of the invention is preferably essentially non-phasing, some separation of the polyester components is acceptable. Moreover, the degree of phasing can be adjusted by varying any or several of certain factors. For example, the degree of chain extension of the polyester, the molecular weight of the polyester and the choice of isocyanate all influence phase separation. For example, as the molecular weight of the polyester decreases, the compatability of the blend increases. Additionally, as the NCO|OH ratio decreases the compatability of the components in the prepolymer increases. Moreover, simply varying the ratios of the polyester components influences their compatability as shown herein. The compositions of the invention can be employed in any application where a high-performance adhesive, coating, or sealant is desired. They can be applied to a variety of articles and substrates, such as thermoplastic materials, thermosetting materials, foam material, wood, paper, leather, rubber, textiles, non-woven materials and bare and painted metals. The following examples are offered to aid understanding of the present invention and are not to be construed as limiting the scope thereof. All parts are by weight unless otherwise stated. Examples 1-7 Preparation and testing of isocyanate-terminated hydroxy functional polymer compositions. In a 600 ml, stainless steel reactor with a gas inlet adapter and fitted with a cover having a rubber gasket, gas inlet and stirrer opening, the hydroxy functional polymer or mixture of polymers was heated to 100°C with efficient stirring and nitrogen blanket. 4,4'-Diphenylmethane diisocyanate was added with stirring. The mixture was stirred under nitrogen for about 15 minutes and dibutyltin dilaurate (DBTDL) was added. Stirring was continued under vacuum for about 1 hour. Heating at 100°C was maintained throughout. The resulting mixture was poured into nitrogen purged metal containers and sealed. The containers were stored in a dessicator. Viscosity determinations were made using a Brookfield RVF Viscometer and #27 spindle at 121°C at 10 rpm or 20 rpm. Number average molecular weights (Mn) were determined by end group analysis. The non-hairing property was determined by visual observation. If there were no strings or hairs trailing from a hot melt applicator nozzle, the composition was deemed non-hairing. Polyol, OH eq. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 PHA .55 .55 1 PEA .45 .45 1 PBA .45 .55 1 MDI NCO EQ 2 2 2 2 2 2 2 DBTDL(wgt. %) .1 .1 .1 .1 .1 .1 .1 Visc.(Cps) 12825 6550 10850 6150 5812 19375 6250 Non-hair yes no no no no no no These Examples show that only compositions according to the invention are non-hairing. Examples 8-9 The procedure and tests of Examples 1-7 was repeated. The results are given in Table 2. Polyol OH eq. Ex. 8 Ex. 9 PEA .45 PBA .45 PCP .55 .55 MDI NCO EQ 2 2 DBTDL(wgt. %) .1 .1 Visc. (Cps) 10088 13875 Non-hair yes no Examples 10-16 The following examples show the correlation between isocyanate-terminated polymer mixtures and polymer mixtures not reacted with isocyanate. The polymer mixtures are not reacted with the isocyanate for ease of handling. Blends were prepared by manually stirring the components at a temperature of about 120°C until well mixed, which was about 10 minutes. The presence or absence of hairing was determined by a visual inspection by observing if "hairs" of liquid adhesive form when a spatula contacting the surface of a melted sample was removed from that surface. If there were no "hairs", the composition was deemed to be non-hairing. This method correlates to application out of a hot melt applicator. Example No. Parts PHA Parts PEA Parts PBA Parts PCP Non-Hairing 10 50 50 yes 11 50 50 no 12 50 50 no 13 50 50 yes 14 50 50 no 15 100 no 16 100 no A comparison of the results in Tables 1, 2 and 3 show that the results obtained with the isocyanate-reacted hydroxy functional polymers and the hydroxy functional polymers which were not reacted with the isocyanate are the same. Examples 17-23 Using the same procedures as those in Examples 10-16, several blends of varying molecular weight are prepared and evaluated. Set out in the table below are the formulations and hairing property determination. Ex. No. PHA PEA-25 PEA-55 PEA-110 Non-Hairing 17 100 no 18 100 no 19 100 no 20 100 no 21 50 50 yes 22 50 50 yes 23* 50 50 no An analysis of these results show that the substitution of a component with its lower molecular weight analog affects the non-hairing characteristic of the composition. Examples 24-37 Examples 24-37 illustrate the effect of varying the ratio of the amount of individual polyesters in the mixture. The blends were prepared using the same technique as in Examples 10-16. The results are shown in Table 5. Ex. No. Parts of PHA Parts of PEA Non-Hairing 24 100 no 25 100 no 26 95 5 no 27 90 10 no 28 = 85 15 no 29 80 20 borderline 30 75 25 yes 31 70 30 yes 32 50 50 yes 33 25 75 yes 34 20 80 borderline 35 15 85 no 36 10 90 no 37 5 95 no The results show that the ratio of components in the blend influences the non-hairing property. Examples 38-82 Blends of polyesters in a 1:1 ratio by weight were prepared and tested for non-hairing using the following test method: The 0.20 cm diameter end of a 14.6 cm long wooden dowel contacted the surface of a sample whose temperature was 121°C and was drawn away from that surface using an electric motor at a speed of 12 cm/second over a distance of 10.2 cm. If the adhesive "trail" from the dowel end was less than 7.6 cm long as it was being removed from the sample surface, the sample was deemed non-hairing. If it was more than 7.6 cm long, the sample was deemed to be hairing. Results are set out in Table 6 below. For simplicity the following abbreviations are used: a is the number of -CH₂- groups in the diol used to form the first polyester, b is the number of -CH₂- groups in the diacid used to form the first polyester, c is the number of -CH₂- groups in the diol used to form the second polyester, d is the number of -CH₂- groups in the diacid used to form the second polyester. PESu = polyethylene succinate, Mn 3740 PEA = polyethylene adipate, Mn 4489 PESe = polyethylene sebacate, Mn 4172 PBSu = 1,4-polybutylene succinate, Mn 5318 PBA = 1,4-polybutylene adipate, Mn 3741 PBSe = 1,4-polybutylene sebacate, Mn 3856 PBAz = 1,4-polybutylene azelate, Mn 3704 PHSu = 1,6-polyhexamethylene succinate, Mn 3591 PHA = 1,6-polyhexamethylene adipate, Mn 3741 PHSe = 1,6-polyhexamethylene sebacate, Mn 4922 These examples illustrate that the linear polyester blends useful in the compositions of the invention follow the general formula a + b < or = 4, c + d > or = 6 a + b > 4 and,≦ 6, c + d > or = 10 a + b > 6 and ≦ 8, c + d > or = 12 and that most preferably a + b = 4, c + d > or = 6 a + b = 6, c + d > or = 10 a + b = 8, c + d > or = 12 Examples 83-109 The following examples were prepared and tested as in Examples 38-82 using non-linear polyesters as one polyester component. Polyester blends (1:1 ratio) and their non-hairing properties are set out in Table 7 below, where in addition to the abbreviations used in examples 38-82, the following abbreviations are used. PNA = polyneopentyl adipate, Mn 2953 CHDMA = 1,4-polycyclohexanedimethyl adipate, Mn 3262 PCP = poly ε-caprolactone, Mn 3033 PPA = 1,2-polypropylene adipate, Mn 2373 Ex. No. Polyester I Polyester II Non-Hairing 83 PNA PEA yes 84 PNA PESe no 85 PNA PBSu yes 86 PNA PBA no 87 PNA PBAz no 88 PNA PHA no 89 PNA PHSe yes 90 CHDMA PEA yes 91 CHDMA PBA no 92 CHDMA PBA no 93 CHDMA PBSu yes 94 CHDMA PHSe no 95 PCP PESu yes 96 PCP PESe no 97 PCP PBSu yes 98 PCP PBAz no 99 PCP PBSe no 100 PCP PHSu no 101 PPA PESu yes 102 PPA PEA no 103 PPA PESe no 104 PPA PBSu no 105 PPA PBA no 106 PPA PBAz no 107 PPA PBSe yes 108 PPA PHSu no 109 PPA PHSe yes These examples illustrate useful combinations of non-linear and linear polyesters in the compositions of the invention that show the desired non-hairing property. Examples 110-113 The following examples show the effect of the degree of phase separation (or incompatibility) on the green strength build-up of isocyanate-terminated hydroxy functional polymer compositions. Blends were prepared as in Examples 1-7. In addition to the viscosity and non-hairing (determined as in Examples 1-7) measurements, the blends were tested for degree of phase separation and ability to hold a sustained load. Phase separation was determined as follows: Approximately one gram of molten polymer blend was placed on a microscope slide and the melt was drawn out into a 0.1 to 0.2 mm thick film. The slide was then placed in a 100°C. oven for 60 minutes, then removed from the oven, allowed to cool undisturbed at room temperature and the film was visibly inspected for the formation of circular and elongated domains. The percent of the total melt area occupied by these domains was recorded as the percent of phase separation. Green strength build-up was determined as follows: A 0.5 ± 0.05 g quantity of adhesive was extruded at 107°C. onto the center portion (about 5 cm from each end) of a 2.5 cm wide x 10 cm long x 0.8 cm thick piece of Douglas Fir. A timer was started. After 10 seconds, a second piece of Fir was bonded on its center point and at right angles to the first. Firm hand pressure was used to mate the surfaces. After a specified amount of time, a 4.5 kg tensile load was pneumatically applied to the 6.45 sq. cm bond area. The time at which the bond can support the 4.5 kg load was called the "4.5 kg tensile time". The results are reported in Table 8. Polyol, OH eq. Ex. 110 Ex. 111 Ex. 112 Ex. 113 PHA 0.55 0.55 0.74 0.74 PEA 0.45 0.45 0.26 0.26 MDI eq. 2 1.8 2 1.8 Tert. Amine Catalyst 0.2 0.2 0.2 0.2 Visc.(cps) 7788 12700 6250 12050 Non-hairing yes yes yes yes Phase sep. (%) 30 5 0 0 4.5 kg Tensile Time (minutes) 2-15 1.5-2.5 1 1 It can be seen from the data that with increasing % phase separation, 4.5 kg tensile time increases and is variable. This variability in the times given in Ex. 110 and 111 was due to the variation in the melt that is being extruded, that is the extrudate may be rich in the PHA, which has a rapid crystallization rate, one time and the following extrudate rich in PEA, which has a slower crystallization rate.

Claims: A non-hairing, moisture curable, hot melt composition having a number average molecular weight between 1,000 and 10,000 comprising the reaction product of two or more hydroxy-functional polymers with polyisocyanates wherein said hydroxy functional polymers are selected from: (1) linear polyester blends comprising a first and second polyester, wherein each polyester is the reaction product of a polyol and a polyacid, wherein a + b < or = 4, c + d > or = 6 a + b > 4 and ≦ 6, c + d > or = 10 a + b > 6 and ≦ 8, c + d > or = 12 wherein a is the number of methylene moieties in the polyol used to form the first polyester, b is the number of methylene moieties in the polyacid used to form the first polyester, c is the number of methylene moieties in the polyol used to form the second polyester of the blend, d is the number of methylene moieties in the polyacid used to form the second polyester of the blend; and (2) a blend of at least one non-linear polyester and one linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; and (3) a blend of poly ε-caprolactone and at least one linear polyester selected from polyethylene adipate, polyethylene succinate and polybutylene succinate. A non-hairing composition according to claim 1, wherein said hydroxy functional polymers are selected from group (1). A non-hairing composition according to claim 1, wherein said hydroxy functional polymers are selected from group (2). A non-hairing composition according to claim 1, wherein said hydroxy functional polymers are selected from group (3). A non-hairing composition according to claim 1, wherein said hydroxy functional polymers are selected from (1) linear polyester blends, wherein the polyester is the reaction product of a diol and a diacid, wherein a + b = 4, c + d > or = 6 a + b = 6, c + d > or = 10 a + b = 8, c + d > or = 12 wherein a is the number of methylene moieties in the diol used to form the first polyester, b is the number of methylene moieties in the diacid used to form the first polyester, c is the number of methylene moieties in the diol used to form the second polyester, d is the number of methylene moieties in the diacid used to form the second polyester; and (2) a blend of a linear and a non-linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; (3) a mixture of polyethylene adipate and polyhexamethylene adipate; or (4) a mixture of linear polyesters wherein one of the linear polyesters is poly ε-caprolactone and the others are selected from polyethylene adipate, polyethylene succinate and polybutylene succinate. A non-hairing composition according to claim 5, wherein said hydroxy functional polymers are selected from group (1). A non-hairing composition according to claim 5, wherein said hydroxy functional polymers are selected from group (2). A non-hairing composition according to claim 5, wherein said hydroxy functional polymers are selected from group (3). A non-hairing composition according to claim 5, wherein said hydroxy functional polymers are selected from group (4). A non-hairing composition according to claim 8, wherein the weight ratio of polyethylene adipate to polyhexamethylene adipate is between 80:20 to 20: 80. A non-hairing composition according to claim 10, wherein the weight ratio is between 70:30 and 30:70. A non-hairing composition according to any preceding claim, wherein said polyisocyanates are aromatic polyisocyanates. The hot melt composition according to any of claims 5 to 12, wherein said diol is selected from ethylene glycol, diethylene glycol, triethylene glycol, 1,2-propylene glycol, dipropylene glycol, tripropylene glycol, 1,2-hexanediol, 1,4-butanediol, and 1,6-hexanediol. A hot melt composition according to any preceding claim, wherein said polyisocyanates are selected from diphenylmethane-4,4'-diisocyanate, tolylene-2,4-diisocyanate, tolylene-2,6-diisocyanate, and mixtures thereof. A hot melt composition according to claim 2 or any claim dependent on claim 2, wherein said polyacid is selected from saturated aliphatic dicarboxylic acids containing 4 to 10 carbon atoms, aromatic dicarboxylic acids containing 4 to 10 carbon atoms, aromatic dicarboxylic acids, and their corresponding esterified analogs. A hot melt composition according to any preceding claim which contains a catalyst. A hot melt composition according to claim 16 wherein said catalyst is selected from tertiary amines, metal-organic compounds, and co-curatives. A hot melt composition according to claim 17, wherein the catalyst is dibutyltin dilaurate. A hot melt composition according to claim 17, wherein the catalyst is a metal-organic compound and is present in an amount of at least 0.01 percent, based on the weight of the composition. A method for bonding substrates which comprises contacting a substrate with a bond-forming amount of a hot melt moisture curable composition according to any preceding claim. A composition according to any preceding claim, wherein the molecular weight of the hot melt composition is between 1000 and 6000. A blend of hydroxy functional polymers comprising (1) linear polyester blends, comprising a first and second polyester wherein each polyester is the reaction product of a polyol and a polyacid, wherein a + b < or = 4, c + d > or = 6 a + b > 4 and ≦ 6, c + d > or = 10 a + b > 6 and ≦ 8, c + d > or = 12 wherein a is the number of methylene moieties in the polyol used to form the first polyester, b is the number of methylene moieties in the polyacid used to form the first polyester, c is the number of methylene moieties in the polyol used to form the second polyester of the blend, d is the number of methylene moieties in the polyacid used to form the second polyester of the blend; and (2) a blend of at least one non-linear polyester and one linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; and (3) a blend of poly ε-caprolactone and at least one linear polyester selected from polyethylene adipate, polyethylene succinate and polybutylene succinate. A blend of hydroxy-functional polymers comprising (1) linear polyester blends, wherein the polyester is the reaction product of a diol and a diacid, wherein a + b = 4, c + d > or = 6 a + b = 6, c + d > or = 10 a + b = 8, c + d > or = 12 wherein a is the number of methylene moieties in the diol used to form the first polyester, b is the number of methylene moieties in the diacid used to form the first polyester, c is the number of methylene moieties in the diol used to form the second polyester, d is the number of methylene moieties in the diacid used to form the second polyester; and (2) a blend of a linear and a non-linear polyester, wherein the non-linear polyester is selected from polyneopentyl adipate, polypropylene adipate and polycyclohexanedimethyl adipate, and the linear polyester is selected from polyethylene adipate, polybutylene succinate, and polyhexamethylene sebacate, provided that when the linear polyester is polyhexamethylene sebacate, the non-linear polyester is polyneopentyl adipate or polypropylene adipate; (3) a mixture of polyethylene adipate and polyhexamethylene adipate; or (4) a mixture of linear polyesters wherein one of the liner polyesters is poly ε-caprolactone and the others are selected from polyethylene adipate, polyethylene succinate and polybutylene succinate.

Inventors: KANGAS LANI S C O MINNESOTA MI, STOBBIE IV CHARLES W C O MINNE, KANGAS, LANI S. C/O MINNESOTA MINING AND, STOBBIE IV, CHARLES W. C/O MINNESOTA MINING AND
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1989
Main classification: C08G18
IPC codes: C08G18, C09J175