Eyeglass frame having Ti-Ni-V alloy element with improved wear comfortability

Abstract: In an eyeglass frame comprising a pair of lens fixing rims, a bridge connecting the paired rims, and a pair of temples, the bridge and/or the temples are made of Ti-Ni-V alloy having a super elasticity of a generally rectangular stress-strain hysteresis loop over a relevant temperature range of 0-20°C so as to improve eyeglass wearing comfortability. The Ti-Ni-V alloy comprises Ni and Ti with an atomic ratio Ni/Ti of 1.02-1.06 and V 0.25-2.0 at.%, and is worked into a desired shape and thereafter is heat-treated at 425-525°C for 10-60 minutes.

Description: The present invention relates to eyeglass frames according to the preamble of claim 1 and to a method of producing an eyeglass frame according to the preamble of claim 6. U.S. Patent No. 4,772,112 (Reference 1) issued to Zider et al and assigned to CVI/Beta Ventures, Inc. discloses to use a shape memory alloy such as Ti-Ni alloy for elements of an eyeglass frame. It is well known in the art that the Ti-Ni shape memory alloy has an elasticity or a pseudo elasticity as well as a shape memory effect. The reference 1 proposes to use, as an optimized elasticity, a combination of a super elasticity as shown in Fig. 2f and a work-hardened pseudo elasticity of Fig. 2h in the Reference 1. The stress-strain curve according to the optimized elasticity has a comparatively small hysteresis loop and the strain variation is almost in proportion to variation of the stress. Although reference 1 recommends utilization of the optimized elasticity for the eyeglass frame, it has been confirmed by the present inventor that the super or pseudo elasticity having a generally rectangular hysteresis is more relevant for the eyeglass frame elements such as bridges and temples. Although the conventional Ti-Ni shape memory alloy has the stress-strain curve of the rectangular hysteresis loop as shown in Fig. 2c in the reference 1, the curve is realized only in a limited temperature range which is smaller than a broad relevant temperature range such as 0-20°C. Therefore, the Reference 1 abandones utilization of the pseudo elasticity having the generally rectangular-hysteresis for the eyeglass frame elements. A Ti-Ni-V alloy was proposed by Yamauchi in JP-A-63-14834 (which is corresponding to a copending U.S. Patent Application Serial No. 142,672 and is assinged to Tohoku Kinzoku Kogyo K. K. having an English name of Tokin Corporation). Examples of the Ti-Ni-V alloy will be described below. It is an object of the invention to provide an eyeglass frame having an elasticity characterized by a stress-strain curve of the rectangular hysteresis loop so as to improve wearing comfortability of the eyeglass frame over a relevant temperature range including 0-20°C. The present invention is directed to an eyeglass frame comprising bridge means connecting a pair of lens fixing rims and temples connected to the rims, respectively, with the features of claim 1 and to a method of producing such an eyeglass frame with the steps according to claim 6. In production, the at least one element of said Ti-Ni-V alloy is cold worked into a shape and then heat treated at 425-525°C for 10-60 minutes. Fig. 1 is a perspective view of an eyeglass using a frame according to an embodiment of the present invention; Fig. 2 shows plots of the measured Ms with alloy numbers in connection with the V amount X; Figs. 3(a)-4(f) are cited from JP-A-63-14834, Figs. 3(a)-3(f) show stress-strain curves of sample wires of alloy No. 6 heat treated at different temperatures which were measured at different temperatures; Figs. 4(a)-4(f) show stress-strain curves of sample wires of alloy No. 15 heat treated at different temperatures which were measured at different temperatures; Fig. 5 is a perspective view of a temple piece; Fig. 6 is a stress-strain curve of the temple piece of sample alloy No. 2; Fig. 7 is a stress-strain curve of the temple piece of sample alloy No. 15; Figs. 8a and 8b are perspective views illustrating the temple and a cap before and after they are connected; Fig. 9 is a perspective view of a reinforcing bridge; and Fig. 10 is a perspective view of a nose bridge. Referring to Fig. 1, an eyeglass frame according to an embodiment of the present invention comprises a pair of rims 11 for supporting lenses 12, a reinforcing bridge 13 connecting tops of the paired rims 11 and a nose bridge 14 connecting opposite sides of the paired rims 11, and a pair of temples 15 connected to rims 11 by hinges 16, respectively. Each of the temples 15 is made of a Ti-Ni-V alloy which comprises V of 0.25-2.0 atomic percent and the balance of Ti and Ni with an atomic ratio Ni/Ti of 1.02-1.06. Alloy ingots containing ingredients shown in Table 1 were prepared by use of a high frequency induction vacuum furnace. Alloy No. Ingredients (at%) Cold Workability Ti Ni V 1 49 50.75 0.25 Good 2 49 50.50 0.50 Good 3 49 50.0 1.0 Good 4 49 48.5 2.5 Impossible 5 48.875 50.875 0.25 Good 6 48.75 50.75 0.50 Good 7 48.50 50.50 1.0 Good 8 47.75 49.75 2.5 Impossible 9 47.0 49.0 4.0 Impossible 10 46.5 48.5 5.0 Impossible 11 48.75 51.0 0.25 Good 12 48.50 51.0 0.50 Difficult 13 48.0 51.0 1.0 Impossible 14 46.5 51.0 2.5 Impossible 15 49 51 - Good Alloy ingots of Nos. 1-15 were heat treated at 750°C for one hour and their martensitic transition start points (Ms) were measured by use of a differential scanning calorimeter. The measured Ms are plotted with the alloy numbers in Fig. 2 in connection with V amount x. Nos. 1-4 alloys are represented by a formula of Ti 49 Ni 51-x V x and are on a line A. Nos. 5-9 alloys are represented by another formula of Ti 49-x/2 Ni 51-x/2 V x and are on another line B. The other alloys Nos. 11-14 are represented by a formula of Ti 49-x Ni 51 V x and are on a line C. Fig. 2 teaches us that addition of V shifts Ms to a lower temperature. On the other hand, those prepared ingots were subjected to a solution heat treatment. Then, the treated ingots were worked into wires having a diameter of 1.3mm, respectively, through hot hammering, hot rolling and cold wire drawing processes. Thereafter, the wires were further subjected through no annealing to another cold wire drawing to form sample wires having a diameter of 1.0mm, respectively. It was impossible to cold work Nos. 4, 8-10, 13, and 14 alloys, as described in Table 1. Accordingly, sample wires of these alloys were not obtained. Although No. 12 alloy was difficult in cold working, sample wires were obtained. The obtained sample wires of each alloy were heat treated for 30 minutes at different temperatures, that is, 400°C, 450°C, and 500°C, respectively. Tensile tests of the heat-treated sample wires were run at different temperatures within a temperature range from -20°C to 50°C. The stress was loaded to make a strain of 5% and then unloaded to zero. The measured stress-to-strain curves of sample wires of Nos. 6 and 15 are representatively demonstrated in Figs. 3(a)-3(f) and Figs. 4(a)-4(f), respectively. Figs. 3(a), 3(b), 4(a), and 4(b) are for samples heat treated at 500°C. Figs. 3(c), 3(d), 4(c), and 4(d) are for samples heat treated at 450°C. Figs. 3(e), 3(f), 4(e), and 4(f) are for samples heat treated at 400°C. Figs. 3(a), 3(c), 3(e), 4(a), 4(c), and 4(e) are for samples measured at 0°C and Figs. 3(b), 3(d), 3(f), 4(b), 4(d), and 4(f) are for samples measured at 20°C. Sample wires of alloy No. 6 all exhibit an excellent pseudo elasticity at 20°C, and some of the sample wires which were heated at 400°C and 450°C has also an excellent pseudo elasticity even at 0°C. On the other hand, samples of No. 15 alloy containing no vanadium do not exhibit the pseudo elasticity at 0°C, at all, and a sample heated at 500°C has no pseudo elasticity even at 20°C. In order to produce a temple 15 of the Ti-Ni-V alloy, the alloy ingot is prepared by use of high frequency induction melting in vacuum. The ingot is solution treated at 900°C for 2 hours and is worked to a wire having a diameter of 1.4 mm by hot hammering, hot rolling and cold drawing. Thereafter, it is cold worked to have a diameter of 1.2 mm without annealing and a portion of it is annealed at 750°C for 10 minutes and thereafter, is rolled to have a thickness of 1.0 mm to obtain a temple piece 15' having a shape shown in Fig. 5. The obtained temple piece 15' is treated at 425°C for 15 minutes and is polished to make a temple 15 having a metallic brilliance. A part of the temple piece 15' is cut out and is subjected to a tensile test at 0°C and 20°C. The resultant stress-strain curve is shown in Fig. 6 with respect to sample Alloy No. 2 in Table 1. A comparative alloy of Ti-51 at% Ni (sample No. 15 in table 1) is worked in the similar manner and is subjected to the similar tensile test. The resultant stress-strain curve is also shown in Fig. 7. Fig. 6 shows that the super elasticity having the stress-strain curve of a rectangular hysteresis loop is obtained even at 0°C similar to sample alloy No. 6 in Table 1 (Figs. 3(c) and 3(d)) where strain returns to the initial value at a moment when stress is removed, but Fig. 7 shows the super elasticity is only present at 20°C. Therefore, the temple 15 of the embodiment is preferable in the super elasticity. To an end of the produced temple 15, a cap 17 is fitted and mechanically fixed which is made of metal such as stainless steel having good soldering-property, and thereafter, is joined by the soldering, as shown in Fig. 8. The cap 17 is for connecting the temple 15 to the hinge 16. Although the above description has been made as to temple 15, application is similarly made to the bridges 13 and 14 with a similar advantage. Fig. 9 shows a shape of a bridge piece for producing the reinforcing bridge 13 and Fig. 10 shows a shape of a nose bridge piece for producing a nose bridge 14. The rim 11 can also be produced in a manner as the temple 15 as described above.

Claims: An eyeglass frame comprising bridge means (14) connecting a pair of lens fixing rims (11) and temples (15) connected to the rims, respectively, wherein at least one element of said bridge means (14) and said temples (15) is made of an alloy having an elasticity defined by a stress-strain curve having a generally rectangular hysteresis loop wherein strain gradually increases with increase of stress and rapidly and suddenly increases at an elevated stress, and strain gradually reduces with reduction of stress and rapidly and suddenly reduces at a reduced stress, characterized in that said alloy is made of Ti-Ni-V comprising V at 0.25 - 2.0 at.% and the balance of Ni and Ti with an atomic ratio Ni/Ti of 1.02 - 1.06, said elasticity existing over a temperature range of 0 - 20 °C, and in that each of said temples (15) of the eyeglass frame is formed of said alloy by the following steps: an alloy ingot is prepared by use of high frequency induction melting in vacuum, the ingot is solution treated at 900°C for 2 hours and is worked to a wire having a diameter of 1.4 mm by hot hammering, hot rolling and cold drawing, thereafter it is cold worked to have a diameter of 1.2 mm without annealing and a portion of it is annealed at 750°C for 10 minutes and thereafter is rolled to have a thickness of 1.0 mm to obtain a temple piece (15'), which temple piece is treated at 425°C for 15 minutes. An eyeglass frame as claimed in claim 1, wherein said bridge means (14) comprises a nose bridge portion (14) connecting opposite side portions of said rims (11) to each other and a reinforcing bridge portion (13) connecting top portions of said rims (11) to each other. An eyeglass frame as claimed in claim 1, wherein said Ti-Ni-V alloy is one represented by Ti 49-x Ni 51 V x (0.25 ≤ x ≤ 0.50). An eyeglass frame as claimed in claim 1, wherein said Ti-Ni-V alloy is one represented by Ti 49-x/2 Ni 51-x/2 V x (0.25 < x < 2. 0). An eyeglass frame as claimed in claim 1, wherein said Ti-Ni-V alloy is one represented by Ti 49 Ni 51-x V x (0.25 < x < 2. 0). Method of producing an eyeglass frame, the eyeglass frame comprising bridge means (14) connecting a pair of lens fixing rims (11) and temples (15) connected to the rims, respectively, wherein at least one element of said bridge means (14) and said temples (15) is made of an alloy having an elasticity defined by a stress-strain curve having a generally rectangular hysteresis loop wherein strain gradually increases with increase of stress and rapidly and suddenly increases at an elevated stress, and strain gradually reduces with reduction of stress and rapidly and suddenly reduces at a reduced stress, and wherein said alloy is made of Ti-Ni-V comprising V at 0.25 - 2.0 at.% and the balance of Ni and Ti with an atomic ratio Ni/Ti of 1.02 - 1.06, said elasticity existing over a temperature range of 0 - 20°C, wherein said method comprises forming a temple (15) of the eyeglass frame from said alloy with the following steps: preparing an ingot of said alloy by use of high frequency induction melting in vacuum, solution treating said ingot at 900°C for 2 hours, working said ingot into a wire having a diameter of 1.4 mm by hot hammering, hot rolling and cold drawing, thereafter cold working said wire to have a diameter of 1.2 mm without annealing, annealing a portion of said wire at 750°C for 10 minutes, thereafter rolling said portion to have a thickness of 1.0 mm to obtain a temple piece (15'), and heat treating said temple piece at 425°C for 15 minutes.

Inventors: SATO SYOICHI, SATO, SYOICHI
Applicants: NAKANISHI OPTICAL CORP, TOKIN CORP, NAKANISHI OPTICAL CORPORATION, TOKIN CORPORATION
Application year: 1989
Main classification: G02C5
IPC codes: G02C5