Heat-resistant flock sheet

Abstract: A heat-resistant flock sheet comprising a heat-resistant film layer consisting of an infusible organic polymer, a flock layer formed by flocking a number of short fibers on the surface of said heat-resistant film layer and a drawn film layer containing a lot of voids laminated on the surface of the opposite side to said flock layer on said heat-resistant film layer.

Description: The present invention relates to a heat-resistant flock sheet and more specifically, the present invention relates to a heat-resistant flock sheet having a heat-resistant film layer as a base material and being capable of forming beautiful uneven patterns. In recent years, flock sheets prepared by flocking short fibers are being widely used as interior decorative materials adhered on the inner walls of vehicles and buildings and outer decorative materials adhered on the outer surfaces of indoor interior items. It is required that the sheet materials used for the applications of these interior decorative materials and outer decorative materials should have heat resistance and flame resistance against fire such as fire of tobacco from the viewpoint of safety against fire. A flock sheet disclosed in Japanese Patent Application Kokai Publication No. 62-7469 is proposed as such a material that satisfies this requirement and is prepared by flocking short fibers on a heat-resistant sheet base material consisting of a polyimide film and the like by using a thermoplastic resin as an adhesive layer. On the other hand, as consumers' tastes have been diversified, monotonous appearance has become unfavorable for the flock sheets used in the above described outer decorative materials and interior decorative materials. As one of the effective means giving diversification to the appearance, it is proposed that uneven patterns are given on the surface by emboss-treating the flock sheet. However, in case of the sheet where a heat-resistant film layer such as polyimide film and the like is used, it is difficult to give easily uneven patterns even if emboss treatment is carried out at high temperature and as the result it hardly meets with the consumers' tastes. An object of the present invention is to provide a heat-resistant flock sheet wherein even though a heat-resistant film layer such as polyimide film and the like is used as a base material, uneven patterns can be easily formed. A further object of the present invention is to provide a heat-resistant flock sheet wherein even though a heat-resistant film layer is used as a base material, uneven patterns can be easily formed not only under heating but also even at ambient temperature. A still further object of the present invention is to provide a heat-resistant flock sheet wherein even though a heat-resistant film layer is used as a base material, uneven patterns can be easily formed by means of mechanical treatments such as a simple crumpling treatment and so on. The flock sheet of the present invention for achieving the above described objects is characterized by comprising a heat-resistant film layer consisting of an infusible organic polymer, a flock layer formed by flocking of short fibers on the surface of said heat-resistant film layer and a drawn film layer containing voids laminated on the surface of the opposite side to the above described flock layer on the above described heat-resistant film layer. Moreover, for this flock sheet, it is also possible to laminate a flexible sheet on a surface of the above described drawn film layer being opposite side to the above described heat-resistant film layer, if necessary. As the above described drawn film layer contains a lot of voids, a part of the voids can be squashed and permanent strain can be given by a crumpling treatment and the like at ambient temperature and uneven patterns can be formed on the surface by the permanent strain. As the above described flock sheet is prepared by laminating a heat-resistant film layer on this type of drawn film layer, the same uneven patterns can be given to the heat-resistant film layer by imparting uneven patterns on this drawn film layer. Figure 1A is a vertical cross-sectional view illustrating a part of a flock sheet prepared by an Example of the present invention, Figure 1B is a vertical cross-sectional view illustrating a state where said flock sheet is mechanically treated and uneven patterns are thereon provided, Figure 2A is a vertical cross-sectional view illustrating a part of a flock sheet prepared by another Example of the present invention, Figure 2B is a vertical cross-sectional view illustrating a state where said flock sheet is mechanically treated and uneven patterns are thereon provided, Figure 3 is a vertical cross-sectional view illustrating an example of a drawn film layer containing voids and used for the flock sheet of the present invention, Figure 4 is also a vertical cross-sectional view illustrating another example of a drawn film layer containing voids, and Figure 5 is also a vertical cross-sectional view illustrating furthermore another example of a drawn film layer containing voids. In Figure 1A, S shows a flock sheet of the present invention. This flock sheet S has a heat-resistant film layer 1 consisting of an unfused organic polymer as one of the base materials and a flock layer 2 consisting of a lot of short fibers is formed on one of the surfaces through an adhesive layer 5 and a drawn film layer 3 is formed on another surfaces through an adhesive layer 6. A lot of voids are formed in the drawn film layer 3 and these voids are prepared by using particle-shaped fillers as the nuclei which are not illustrated in the figure. The flock sheets S thus formed can be used as it is in a laminated state as shown in Figure 1A and furthermore, if necessary, it may be possible to laminate a flexible sheet layer 7 on the rear face of the drawn film layer 3 through an adhesive layer 8 as shown in Figure 2A. When a mechanical treatment such as crumpling treatment, emboss treatment and so on is applied on these flock sheets S of the present invention, voids 4 in the drawn film layer 3 are partly squashed to produce permanent strains and uneven patterns are formed like Figure 1B for the sheet shown in Figure 1A and like Figure 2B for the sheet shown in Figure 2A based on the permanent strains. Uneven strains generated in this drawn film layer 3 deforms a heat-resistant film layer being thereon integrally laminated and thereby forms the similar uneven patterns on the surface of the heat-resistant film layer 1. In the flock sheets of the present invention, infusible organic polymers constituting the heat-resistant film layer are such synthetic polymers that have no melting point and decompose and are carbonized without melting when elevating temperature. As these infusible organic polymers, those which are carbonized at 400° C or higher can be preferably used and more concretely, polyimides, polyamideimides, aromatic polyamides, polyparabanic acid and so on can be used. The heat-resistant film layer can give self-fire extinguishing property on the flock layer formed on the surface based on it heat resistance and even if the short fibers of said flock layer are flammable and fired by the fire of tobacco and the like, the spread of the burning can be prevented. This heat-resistant film layer also prevent the flame fired on the above described flock layer from the spread to the flexible sheet layer laminated on the opposite side of the flock layer. Short fibers forming the flock layer in the flock sheets of the present invention are not specifically restricted. Natural fibers such as cotton, linen, wool and so on, synthetic fibers such as polyester fibers, polyamide fibers, polyacrylonitrile fibers, polyolefin fibers and so on and artificial fibers such as rayon, acetate and so on can be used. Especially, those fibers which have flame-retardant property and heat-resistance such as polyvinylidene chloride fibers, modacrylic fibers, aromatic polyamide fibers, polyarylene fibers, phenol fibers and so on are preferable. Furthermore, it is preferable that these short fibers whose monofilament denier and fiber length are in the range of 1-20 denier and 1-10 mm are used. Furthermore, as the flexible sheet layer, not only woven fabrics, knitted fabrics and non-woven fabrics consisting of natural fibers, synthetic fibers, artificial fibers and so on, or papers can be used, but also synthetic polymer films, synthetic polymer foamed sheet and so on can be also used if necessary. In the flock sheet of the present invention, the drawn film layer contains a lot of particle-shaped fillers and has a structure where voids are formed by the existence of the fillers being as nuclei. The drawn film layer containing voids like this can be prepared by drawing an undrawn synthetic polymer film where particle-shaped fillers are added. As synthetic polymers used for this drawn film layer, polyolefin such as polypropylene, polyethylene and so on, polyesters, polyamides, polyvinyl chloride and so on can be used. As particle-shaped fillers to be added in this drawn film layer, both inorganic and organic particles can be used. As the inorganic particles, calcium carbonate, magnesium carbonate, alumina, aluminum silicate, kaolin, kaolinite, talc, clay, diatom earth, dromite, titanium oxide, magnesium oxide, zeolite and so on can be cited. These inorganic particles can be used alone or by mixing two or more kinds thereof. As the organic particles, synthetic resin particles which are different from the synthetic polymer constituting the drawn film layer and have good peelability. For example, for the filler in polyester, polyolefin resins such as polyethylene, polypropylene, polymethyl pentene and so on can be cited. These organic particles are also used alone or by mixing two or more kinds thereof. The amount of the above described filler to be added is preferably 10-40 % by weight based on the synthetic polymer of the drawn film layer and more preferably 15-35 %. If the added amount of the filler is less than 10 % by weight, it becomes difficult to form uneven structures on the surface by means of a mechanical treatment such as crumpling treatment and so on and if the added amount of the filler is more than 40 % by weight, the drawn film layer becomes brittle and it tends to be broken in case of drawing. As the drawing of undrawn synthetic polymer film, either monoaxial drawing in the longitudinal direction or biaxial drawing in both longitudinal and transverse directions can be used and the draw ratio may be in such a degree that at least voids can be formed by the above described fillers being as nuclei. The content of voids included in the drawn film layer is preferably 25-60 % by volume and more preferably 30-55 % by volume. If this content of voids is less than 25 % by volume, formation of uneven patterns prepared by means of mechanical treatment becomes insufficient and this value is more than 60 % by volume, uneven patterns become easy to be formed but the film layer becomes brittle and the mechanical strength decreases. Here, the content of voids is defined by the following formula wherein density of the film containing voids is ρ₀ and density of the film where the voids are completely squashed by heat-pressing the film at a temperature close to the melting point of the film is ρ. In this case, density calculated from the weight and the volume (thickness X area) of the film is used. To give a desired content of voids within the above described range to the drawn film layer, the film forming conditions are properly selected. For example, to make the content of voids larger, either one or two or more of the conditions such as to enlarge the draw ratio, to elevate the drawing temperature or to increase the content of fillers are carried out. It is not necessary that the distribution of voids in the drawn film layer is uniform in the thickness direction and it should be rather better that the distribution of voids is smaller in the area close to the film surface and becomes larger inside. If voids largely distribute on the surface of the drawn film layer, adhesiveness of the surface tends to become insufficient and therefore peeling-off of the heat-resistant film layer and the flexible sheet layer easily occurs. However, to decrease the content of voids for preventing this peeling-off causes decrease in uneven pattern formability, which is the purpose of the present invention. Therefore, to obtain both preventing peeling-off and uneven pattern formability, it is preferable that a very thin film layer having no void is laminated on at least one face of the drawn film layer containing voids. Figure 3 illustrates one example of such a drawn film layer 3 where a thin film layer 32 having no void is laminated on the side where a flock layer is to be laminated, of a main drawn film layer 31 having voids. In the case when a flock layer 2 and a flexible sheet layer 7 are respectively provided on both faces of the drawn film layer as shown in Figure 2A, it is desirable that, thin film layers 32 having no void are respectively provided on both faces of the above described drawn film layer 31. Moreover, it is allowable that as the above described film layer, instead thereof, a film layer 33 having voids but whose content of voids is low is provided as shown in Figure 4. Moreover, it is also allowable that these thin film layers 33 whose contents of voids are low are provided on the main drawn film layer 31 as shown in Figure 5. Such drawn film layers that are constituted of a plurality of film layers can be prepared by extruding simultaneously a synthetic polymer containing fillers and another synthetic polymer containing no filler or less amount fillers in a stratified and composite film-like state from an extruder and drawing it. Instead, this film can be obtained by such a process that the above described synthetic polymer containing fillers and synthetic polymer containing no filler or less amount fillers are respectively extruded from an individual extruder into a film-shape and drawn in the longitudinal direction and both films are laminated after this longitudinal drawing and simultaneously drawn in the transverse direction. Uneven patterns given to the heat-resistant film layer can be formed based on the permanent strain generated when the drawn film layer is mechanically treated, as described above. To make shaping of the heat-resistant film layer easier, it is desirable that the thickness of the heat-resistant film layer is 1.0 time or less, preferably 0.05-0.6 times, more preferably 0.1-0.3 times of the thickness of the drawn film layer. Moreover, the absolute value of the thickness of the heat-resistant film layer is not specifically restricted if the thickness satisfies the above described relation, but it is preferably in the range of 6-50 µm, more preferably in the range of 10-40 µm. To these values, the thickness of the drawn film layer is preferably in the range of 30-150 µm, more preferably 60-120 µm. In the present invention, the flexible sheet layer is not always necessary, but if this flexible sheet is laminated, it is thereby possible to make processability of uneven patterns of the flock sheet. Moreover, it is possible to give excellent elasticity and good sewing characteristics which this flexible sheet layer has by laminating this flexible sheet layer. The thickness of this flexible sheet layer is preferably in the range of 20 µm-5 mm and is properly determined in accordance with the application of the flock sheet. Types of the mechanical treatment to give uneven patterns to the flock sheet are not specifically restricted. As the mechanical treatments like this, not only the above described crumpling treatment, emboss treatment, but also crape treatment, pleat treatment and the like can be applicable. On the flock sheet of the present invention, it is not always necessary to heat when this uneven pattern is treated. When heated on this uneven pattern treatment, it is desirable to heat at melting point or below of the synthetic polymer of the drawn film layer, preferably at the temperature being at least 50° C lower than the melting point. Especially, when the drawn film layer is constituted of polypropylene or its copolymer, the temperature is preferably in the range of from ambient temperature to 100° C. To apply the uneven treatment on the flock sheet of the present invention, it may be possible to do it after adhering the flock layer on the heat-resistant film layer, but it is also possible to do it before adhering the flock layer. In both cases, good uneven patterns can be shaped on the flock sheet. Especially, very much leather-like appearances can be given on the surfaces of those flock sheets which are uneven-treated after adhering the flock layer. Adhesives for bonding integrally each layer in the flock sheet of the present invention, are not specifically restricted. However, as adhesives for bonding the drawn film layer and the heat-resistant film layer, it is desirable to select an adhesive having good compatibility with both film layer so as to give sufficiently the uneven strain formed on the drawn film layer to the heat-resistant film layer. As such adhesives as this, it is preferable to use synthetic resin adhesives such as polyurethanes, polyacrylics and so on. More concretely, reactive type or self-crosslinkable polyacrylate adhesives, thermosetting urethane adhesives, epoxy adhesives, rubber adhesives and so on can be cited. As described above, in heat-resistant flock sheets of the present invention, a heat-resistant film layer such as polyimide film and so on is used as the base material and it is possible to shape easily uneven patterns by laminating a drawn film layer containing voids and having good processability on the heat-resistant film layer. Example 1: Pellets of polypropylene whose melt index defined by ASTM-D1238 was 1.0 and in which 20 % by weight of calcium carbonate whose average particle size was 1.7 µm were added, and pellets of ethylene-propylene block copolymer whose ethylene component was 20 % by weight were extruded from an extruder to prepare a double layer composite film, which was then biaxially drawn by 3.5 times in the longitudinal direction and by 9 times in the transverse direction and was heat-set and furthermore the surface of the film was treated by means of corona discharge treatment to obtain a composite biaxially drawn film whose thickness was about 60 µm. In the composite biaxially drawn film, the thickness of ethylene-propylene block copolymer film layer was 8 µm and the content of voids was 35 % by volume. Then, using the above described composite biaxially drawn film as a drawn film layer, a polyimide film ("Kapton" 100H manufactured by E.I. Du Pont de Nemours & Co., Inc.) whose thickness was 25 µm as a heat-resistant film layer was adhered on the side of the ethylene-propylene block copolymer layer side of the drawn film layer by using a polyurethane adhesive ("Seikabond" manufactured by Dainichi Seika Industries, Co., Ltd) to obtain a sheet I. Furthermore, in addition to this sheet I, a polyester/rayon blended fabric as a flexible sheet layer was further adhered on the side of the polypropylene layer containing voids of the above described drawn film layer to obtain another sheet II. Polyacrylonitrile short fibers whose monofilament denier and fiber length were 9 denier and 0.8 mm respectively were electrically flocked on the surfaces of the heat-resistant film layers of the above described two sheets I and II by using a heat-curable polyurethane adhesive ("Seikabond" E260/C26 manufactured by Dainichi Seika Industries, Co., Ltd.) to obtain flock sheets III and IV where flock layers were thereby formed. Wrinkling and crumpling treatment was respectively carried out on the above described four kinds of sheets I, II, III and IV by the speed of 0.5 m/minute and at ambient temperature by means of a Crumpling Machine Type YS manufactured by Yamasa Giken Co., Ltd. As the result, acute-angled and beautiful uneven patterns were given on each surface of the sheets. Furthermore, the same polyacrylonitrile short fiber flock layer as the above described one was respectively further adhered on the above described uneven pattern-shaped sheets I and II, and sheets I′ and II′, wherein acute-shaped and beautiful uneven patterns were thereby formed along the above described uneven patterns were obtained. On the other hand, a heat-resistant test and a flame resistant test of the above described sheets I′, II′, III, IV were done by bringing a tobacco fire into contact with these flock layers for 3 minutes and observing their burning conditions. The flock layers of all the sheets brought into contact with the tobacco fire were all charred, but the fires were put out without spreading. Example 2: Pellets of polyethylene terephthalate dried at 180° C for 3 hours under vacuum whose inherent viscosity (IV) is 0.6 were mixed with 20 % by weight of pellets of polymethylpentene and the mixture was extruded into a film-shape at 270-300° C by means of an extruder and cooled and solidified. The extruded film was drawn by 3 times in the longitudinal direction at 100° C and furthermore drawn by 4 times in the transverse direction at 130° C to obtain a biaxially drawn film whose thickness was 50 µm and content of voids was 32 % by volume. Then, the above described biaxially drawn film was used as the drawn film layer and a polyimide film ("Kapton" 100H manufactured by E.I. Du Pont de Nemours & Co., Inc.) whose thickness was 25 µm as a heat-resistant film layer was adhered on this drawn film layer by using a polyurethane adhesive ("Seikabond" manufactured by Dainichi Seika Industries, Co., Ltd.) to obtain a sheet V. Furthermore, in addition to this sheet V, a polyester/rayon blended fabric as a flexible sheet layer was adhered on the above described drawn film layer to obtain another sheet VI. Aromatic polyamide short fibers whose monofilament denier and fiber length were 9 denier and 0.8 mm respectively were electrically flocked as flocked layers on the surfaces of the heat-resistant film layers of the above described sheet V and VI by using a heat-curable polyurethane adhesive ("Seikabond" E260/C26 manufactured by Dainichi Seika Industries, Co., Ltd.) to obtain flock sheets VII and VIII where flock layers were thereby formed. Wrinkling and crumpling treatment was respectively carried out on the above described four kinds of sheets V, VI, VII and VIII by the speed of 0.5 m/minute and at ambient temperature by means of a Crumpling Machine Type YS manufactured by Yamasa Giken Co., Ltd. As the result, acute-angled and beautiful uneven patterns were given on each surface of the sheets. Furthermore, the same aromatic polyamide short fiber flock layer as the above described one was respectively further adhered on the above described uneven pattern-shaped sheets V and VI, and sheets V′ and VI′ wherein acuted-shaped and beautiful uneven patterns were thereby formed along the above described uneven patterns were obtained. On the other hand, a heat-resistant test and a flame resistant test of the above described sheets V′, VI′, VII and VIII were done by bringing a tobacco fire into contact with these flock layers for 3 minutes and observing their burning conditions. The flock layers of all the sheets brought into contact with the tobacco fire were all charred, but the fires were put out without spreading. Example 3: Except that an aromatic polyamide film ("TX" film manufactured by Toray Industries, Inc.) whose thickness was 12 µm instead of using the polyimide film whose thickness was 25 µm used as a heat-resistant film layer in Example 1, a sheet without flock and a flock sheet having the completely same constitutions as those in Example 1 were respectively prepared. The same wrinkling and crumpling treatment, heat-resistant test and flame resistant test as those in Example 1 were done on each sheet and the same results as those obtained in Example 1 were obtained. Good uneven patterns are given on all the sheets and good heat-resistance and flame-resistance were obtained. Comparative Example: A polyester/rayon blended fabric as a flexible sheet layer was adhered on one face of a polyimide film ("Kapton" 100H manufactured by E.I. Du Pont de Nemours & Co., Inc.) whose thickness was 25 µm as a heat-resistant film layer by using a urethane adhesive ("Seikabond" E260/C26 manufactured by Dainichi Seika Industries, Co., Ltd.) to obtain a sheet IX. Wrinkling and crumpling treatment was carried out on this sheet IX by the speed of 0.5 m/minute and at ambient temperature by means of a Crumpling Machine Type YS manufactured by Yamasa Giken Co., Ltd., but it was impossible to give uneven patterns on the surface of the sheet. Furthermore, polyacrylonitrile short fibers whose monofilament denier was 9 denier and fiber length was 0.8 mm were electrically flocked as a flocked layer on the side of the heat-resistant film layer of the above described sheet IX by using a heat-curable polyurethane adhesive ("Seikabond" E260/C26 manufactured by Dainichi Seika Industries, Co., Ltd.) to obtain a flock sheet IX′ where flock layer was thereby formed. The same wrinkling crumpling treatment was done on this flock sheet IX′ by means of the same crumpling machine as the one described above, but it was impossible to give uneven patterns on the surface of the sheet.

Claims: A heat-resistant flock sheet comprising a heat-resistant film layer consisting of an unfusible organic polymer, a flock layer formed by flocking of short fibers on a surface of said heat-resistant film and a drawn film layer containing voids laminated on a surface of said heat-resistant film layer opposite to said flock layer. A heat-resistant flock sheet according to claim 1, wherein a flexible sheet layer is furthermore laminated on a surface being opposite to said heat-resistant film layer of said drawn film layer. A heat-resistant flock sheet according to claim 1, wherein said unfusible organic polymer forming said heat-resistant film layer is a polymer to be carbonized at 400° C or higher. A heat-resistant flock sheet according to claim 1, wherein said unfusible organic polymer forming said heat-resistant film layer is either of polymers selected from polyimide, aromatic polyamide, polyamideimide and polyparabanic acid. A heat-resistant flock sheet according to claim 1, wherein the thickness of said heat-resistant film layer is 6-100 µm. A heat-resistant flock sheet according to claim 1, wherein the thickness of said heat-resistant film layer is 1.0 time or less to the thickness of said drawn film layer. A heat-resistant flock sheet according to claim 1, wherein a synthetic polymer forming said drawn film layer is either of synthetic polymers selected from polyolefins, polyesters and polyamides. A heat-resistant flock sheet according to claim 1, wherein voids of said drawn film layer are formed by particle-shaped fillers added in said drawn film layer being as the nuclei. A heat-resistant flock sheet according to claim 1, wherein content of the voids in said drawn film layer is 25-60 % by volume. A heat-resistant flock sheet according to claim 8, wherein added amount of the fillers is 10-40 % by weight to said drawn film layer. A heat-resistant flock sheet according to claim 1, wherein a part of voids inside said drawn film layer are squashed and uneven patterns are formed on a surface of said drawn film layer. A heat-resistant flock sheet according to claim 1, wherein said drawn film layer is a laminated film constituted of at least one layer of drawn films containing voids and at least one layer of drawn films containing no voids. A heat-resistant flock sheet according to claim 1, wherein said drawn film layer is a laminated film constituted of at least one layer of drawn films containing voids and a drawn film containing less amount of voids than the amount of voids of said at least one layer of drawn films. A heat-resistant flock sheet according to claim 1, wherein monofilament denier and fiber length of short fibers constituting the above described flock layer are in the ranges of 1-20 denier and 1-10 mm respectively. A heat-resistant flock sheet according to claim 2, wherein said flexible sheet layer is either one selected from woven fabrics, knitted fabrics, non-woven fabrics, papers, polymer films and polymer foam sheets.

Inventors: EBIHARA TSUTOMU, MATSUMOTO TOSHIHIDE, NAGURA SATORU, EBIHARA,TSUTOMU, MATSUMOTO, TOSHIHIDE, NAGURA, SATORU
Applicants: TORAY INDUSTRIES, TORAY INDUSTRIES, INC.
Application year: 1989
Main classification: B32B5
IPC codes: B32B5, B60R13, B32B27