Fluorinated beta-ketoimines and beta-ketoiminato metal complexes

Abstract: Fluorinated β-ketoimine ligands and highly volatile β-ketoiminato metal complexes of the ligands are synthesized by silylating a fluorinated β-diketone to form a silylenolether, and subsequently reacting the silylenolether with a primary diamine to form the desired ligand having the structural formula: wherein R₁, R₂, R₄ and R₅ are independently linear or branched perfluorinated, C₁-C₈ alkyl groups and R₃ is any organic functionality such as a C₁-C₈ alkyl, phenyl or hydroxyalkyl group, all of which can be partially or fully fluorinated. The corresponding metal complex is formed by treating the ligand with a metal halide.

Description: TECHNICAL FIELD The present invention relates to fluorinated organic ligands and volatile metal complexes formed from such ligands. BACKGROUND OF THE INVENTION In the electronics industry there is a growing need for volatile sources of different metals to be used in the chemical vapor deposition (CVD) of metallic films, metal oxide films, metal silicide films, and the like. The key property required for such metal sources is that they readily evaporate or sublime to give a metal containing vapor or gas which can be decomposed in a controlled manner to deposit a film onto a target substrate. Examples of such materials which are commonly utilized in the microelectronics industry in the preparation of printed circuits and semiconductor devices include the complex H₃SiCo(CO)₄ complex which is pyrolyzed in the gas phase at 670-770°K to produce CoSi and dimethylzinc (1,4 dioxane) which is reacted with hydrogen selenide at 250-550°C to produce ZnSe. References teaching the above CVD methods are B. J. Aylett, et al in Vacuum, 35 p 435-439(1985) and P. J. Wright, et al., in a paper accepted for publication in J. of Crystal Growth, London (1986), respectively. Known fluorinated metal complexes that are chemically stable and easily volatized into the gas phase are the perfluorinated β-diketone metal coordination compounds along with their parent β-diketone precursor ligands, represented by the formulas: wherein R₁ is alkyl or fluoroalkyl, R₂ is fluoroalkyl, and M +n is a metal ion capable of forming a coordination compound. The volatility and gas phase stability of these compounds have been exploited for the gas chromatographic separation of various metals, the purification of uranium and the manufacture of specialty glasses. Decomposing such metal complexes by reaction with hydrogen in the gas phase to deposit thin metal films is taught in U.S. Patent 3,356,527. In the past, attempts have been made to condense primary amines or primary diamines with ligands similar to those having the above structure. In instances in which R₁ and R₂ are not both fluorocarbon groups, it was reported that an O atom could be replaced with a N atom from an amine by direct Schiff-base condensation between an appropriate β-diketone and an amine. Additionally, the corresponding metal complex could be synthesized by chelation to a metal ion. See A. E. Martell, et al J. Inorg. Chem. Vol. 5 pp 170-181 (1958). As reported by Sievers, et al in J. Inorg. Nucl. Chem. Vol. 32 pp 1895-1906 (1970), ligands in which R₁ and R₂ are both perfluoralkyl and in which an oxygen has been replaced with an amine have not been obtainable. It is believed that such methods have been unsuccessful because the perfluorinated β-diketones are of such high acidity that the amine used in the reaction becomes protonated, thereby forming a salt between the amine and the β-diketone rather than forming the desired ligand. Sievers, et al do report synthesizing a ligand having the structure: wherein R₁ = R₂ = CF₃ and R₃ = -CH₂CH₂-. This ligand was reportedly synthesized by sublimation of the salt [(CF₃C(O)CHC(O)CF₃)] - / 2 [NH₃-CH₂CH₂NH₃]⁺². The ligand was reported to be chemically unstable and hence impossible to isolate. Charles, U.S. Patent 3,594,216 discloses a process for depositing a metallic coating on a substrate by heating the substrate and contacting it with vaporized metal-organic beta-ketoamine chelates. The metal-organic beta-ketoamines were prepared by conventional synthesis techniques. While a wide range of metal chelates are disclosed generally, none of the examples or synthesis techniques specifically use perfluorinated metal chelates. Johnson, et al in Journal of Fluorine Chemistry, 27 pp 371-378 (1985) reported synthesizing a ligand in which R₁ and R₂ are perfluoroalkyl and oxygen was replaced with an ammonia nitrogen. The Cu⁺² complex was also prepared and was reported to be volatile. BRIEF SUMMARY OF THE INVENTION The present invention is a class of novel, β-ketoimine ligands and highly volatile metal complexes of the ligands and also a process for making the same. The β-ketoimine ligands of the present invention are those of the general structural formula: wherein R₁, R₂, R₄ and R₅ are independently linear or branched perfluorinated, C₁-C₈ alkyl groups and R₃ is any organic functionality such as a C₁-C₈ alkyl, phenyl or hydroxyalkyl group, all of which can be partially or fully fluorinated. The highly volatile β-ketoiminato metal complexes which are synthesized from these ligands have the structural formula: wherein R₁, R₂, R₃, R₄ and R₅ are as described above, and M⁺² is a divalent metal ion. The present invention is also a process for making both the β-ketoimine ligands and metal complexes described above. The ligands are synthesized by silylating a fluorinated β-diketone to form a silylenolether, and subsequently reacting the silylenolether with a primary diamine to form the desired ligand. The corresponding metal complex is formed by treating the resulting ligand with potassium methoxide followed by treatment with a halide salt of the desired metal. DETAILED DESCRIPTION OF THE INVENTION The present invention is a class of heavily fluorinated β-ketoimine ligands and thermally volatilizable β-ketoiminato metal complexes of the ligands. The ligands are characterized in that they are highly fluorinated and contain oxygen and nitrogen donor atoms which can be covalently coordinated to a central metal atom to form the corresponding metal complex. This class of ligand, as well as the corresponding metal complex, are chemically stable and easily volatized into the gas phase. The high fluorine content of the complex is believed to reduce the Van der Waals forces between individual molecules and hence lower the boiling or sublimination point of the compound. The heavily fluorinated β-ketoimine ligands of the present invention can be represented by the structural formula: wherein R₁, R₂, R₄ and R₅ are independently linear or branched perfluorinated, C₁-C₈ alkyl groups and R₃ is any organic functionality such as a C₁-C₈ alkyl, phenyl or hydroxyalkyl group, all of which can be partially or fully fluorinated. The highly volatile metal complexes which are synthesized from these ligands have the structural formula: wherein R₁, R₂, R₃, R₄ and R₅ are as described above, and M⁺² is a is a divalent metal ion. These volatile complexes hold great potential for use as metal sources in Chemical Vapor Deposition (CVD) processes engaged in the art of depositing, for instance, metal films or metal oxide films. The ligands of structure I above are synthesized by treating a fluorinated β-diketone of the formula R₁COCH₂COR₂ with potassium hydride under anhydrous conditions to produce a compound of the formula R₁COCHCOR - / 2K⁺ and subsequently reacting the resultant R₁COCHCOR - / 2K⁺ with a silylchloride such as, t-butyldimethylsilylchloride, to produce a silylenolether having the general formula: wherein R₁ and R₂ are as described above, and each R₆ is independently an alkyl group. The silylenolether described above is then treated with a primary diamine, NH₂R₃NH₂ wherein R₃ is as above to produce the desired β-ketoimine ligand of structural formula I. To form the metal complex of the β-ketoimine ligand formed above, the ligand is initially treated with potassium methoxide and the resultant compound is subsequently treated with a metal halide of the formula M⁺²(X) - / 2, where X is a halogen, to form the desired highly fluorinated β-ketoiminato complex of formula II above. The ligands of formula I produced in accordance with this invention can exist in two tautomeric forms, enol and keto, with the keto form being represented generally by formula I. Preferred ligands and metal complexes of the present invention include: Ligands . Where R₁=R₂=R₄=R₅=CF₃, R₃=(CH₂)₂ R₁=R₄=CF₂CF₃, R₂=R₅=CF₃, R₃=(CH₂)₂ R₁=R₄=CF₂CF₂CF₃, R₂=R₅=CF₃, R₃=(CH₂)₂ R₁=R₂=R₄=R₅=CF₃, R₃=(CH₂)₃ R₁=R₂=R₄=R₅=CF₃, R₃=CH₂CH(OH)CH₂ Complexes . Where R₁=R₂=R₄-R₅=CF₃, R₃=(CH₂)₂, M⁺²=Cu⁺² R₁=R₂=R₄-R₅=CF₃, R₃=(CH₂)₂, M⁺²=Co⁺² R₁=R₄=CF₂CF₃, R₂=R₅=CF₃, R₃=(CH₂)₂ M⁺²=Cu⁺² R₁=R₄=CF₂CF₃, R₂=R₅=CF₃, R₃=(CH₂)₂ M⁺²=Co⁺² R₁=R₄=CF₂CF₂CF₃, R₂=R₅=CF₃, R₃=(CH₂)₂, M⁺²=Cu⁺² R₁=R₄=CF₂CF₂CF₃, R₂=R₅=CF₃, R₃=(CH₂)₂, M⁺²=Co⁺² Experimental In the following examples, temperatures are set forth uncorrected in degrees Celcius. Unless otherwise indicated, all parts and percentages are by weight. 1,1,1,5,5,5 hexafluoro-2,4-pentanedione, t-butyldimethylsilylchloride, potassium hydride, 2,2,2-trifluoroethylamine, ethylenediamine, ethanolamine, 1,3-propanediamine, 1,3-diamino-2-propanol and analine were obtained from Aldrich Chemical Co. (940 West St. Paul Ave. Milwaukee, Wis. 53233). 1,1,1,2,2,6,6,6-octafluoro-3,5-hexanedione and 1,1,1,2,2,3,3,7,7,7-decafluoro-4,6-heptanedione were obtained from Fairfield Chemical Company Inc. (P.O. Box 20, Blythewood, SC 29016). Solvents used are HPLC grade. Tetrahydrofuran (THF) was distilled from calcium hydride under nitrogen, methanol was distilled from Mg metal under nitrogen. All operations in the preparation of the free ligands or corresponding complexes are carried out using Standard Schlenk line techniques described by D. F. Shriver, "The Manipulation of Air Sensitive Compounds" McGraw-Hill Publishing Co. Microanalyses were performed by Schwarzkopf Microanalytical Laboratory, Woodside, NY or Research Services, Air Products and Chemicals, Inc. ¹H, ¹⁹F and ¹³C NMR spectra were recorded using an IBM SY-200 and a Bruker WH-200 NMR spectrometer. The chemical structure, along with both the IUPAC and abbreviated names of the ligands synthesized in the following examples are set out below. The corresponding metal complexes have the similar structure with an (H) being replaced by the metal (see formula II above). The charge on the metal complex must remain neutral, i.e., if the ligand is diprotonated one divalent metal ion such as Cu⁺² is required. 1,2-di-[4-imino-1,1,1,5,5,5-hexafloro-2-pentanone] ethane (H₂)DODECA-F[EDA] 1,2-di-[5-imino-1,1,1,2,2,6,6-octafloro-3-hexanone] ethane (H₂)HEXADECA-F[EDA] 1,2-di-[6-imino-1,1,1,2,2,3,3,7,7,7-decafluoro-4-heptanone] ethane (H₂)EiCOSA-F[EDA] Bis[4(methylene)imino-1,1,1,5,5,5-hexafluoro-2-pentanone]methane (H₂)DODECA-F[PDA] Bis[4(methylene)imino-1,1,1,5,5,5-hexafluoro-2-pentanone]methanol (H₂)DODECA-F[POA] Example 1 Synthesis of the silylenolethers of perfluorinated β-diketones The following represents a generic synthesis for the preparation of: (i) 4-(t-butyldimethylsiloxy)-1,1,1,5,5,5-hexafluoro-3-penten-2-one from 1,1,1,5,5,5-hexafluoro-2,4-pentanediane. (ii) 4-(T-butyldimethylsiloxy)-1,1,1,5,5,6,6,6 octafluoro-3-hexen-2-one (and its isomer 2-(t-butyldimethylisiloxy)-1,1,1,5,5,6,6,6-octafluoro-2-hexen-4-one) from 1,1,1,5,5,6,6,6-octafluoro-2,4-hexane dione. (iii) 4-(t-butyldimethylsiloxy)-1,1,1,5,5,6,6,7,7,7-decafluoro-3-hepten-2-one (and its isomer 2-(t-butyldimethylsiloxy)-1,1,1,5,5,6,6,7,7,7-decafluoro-2-hepten-4-one) from 1,1,1,5,5,6,6,7,7,7-decafluoro-2-hepten-4-one. Potassium hydride (20.0 g, 0.5 moles) is charged into a solid addition funnel which is fitted to a 1.01 reaction flask; the latter is also fitted with a rubber septum, an inlet for nitrogen, and a magnetic stir bar. Under an atmosphere of dry nitrogen THF (500 ml) is added to the flask which is subsequently cooled to -78°C. The perfluoro β-diketone (0.5 moles) is then added by syringe to the stirred THF at approx. 0.5 ml/min while also slowly adding potassium hydride at such a rate that it is consumed without an excess accumulating in the reaction flask. After adding all the reagents, the reaction is left to stir at room temperature until all traces of hydride are digested (up to 18 hrs). A reflux condenser and an addition funnel charged with t-butyldimethylsilylchloride (75.36 g. 0.5 moles) are fitted to the reaction flask, 150 ml THF is run into the addition funnel to dissolve the silylchloride. This solution is added dropwise over 30 mins to the stirring reaction mixture after which it is refluxed for 18 hrs. During this time a thick white precipitate of potassium chloride forms. The mixture is then filtered under nitrogen to give a pale brown or yellow filtrate. Approximately 500 ml of THF is then distilled off under nitrogen and the resulting concentrated silylenol ether solution left to cool, thereby precipitating further potassium chloride. This solution is then filtered as before then distilled under nitrogen to give the silylenolether as a moisture sensitive pale yellow liquid. NOTE: Care must be taken to not heat the distillation flask too near to dryness. As the residual brown colored liquid in the distillation flask evaporates down to ∼30 ml it may start to evolve thick yellow-grey fumes prior to rapidly decomposing and producing a surge of pressure within the apparatus. It is noted that two silylenolether isomers form when starting with unsymmetrical perfluoro β-diketones (i.e., 1,1,1,2,2,6,6,6-octafluoro-3,5-hexadenione and 1,1,1,2,2,3,3,7,7,7-decafluoro-4,6-heptanedione. However, these are not separated in this distillation stage and are collected as one fraction composed of a mixture of two isomers. Each enolether is collected as one main fraction BPT 165-180°C. The yields and analytical data are reported in Table 1. Example 2 Preparation of ligands (H₂)DODECA-F[EDA], (H₂)HEXADECA-F[EDA], (H₂)EiCOSA-F[EDA], (H₂)DODECA-F[PDA] The above ligands are prepared by reaction of a diamine and a silylenolether of a perfluorinated β-diketone. Under nitrogen a dry 100ml reaction flask fitted with a mechanical stirrer, addition funnel and rubber septum is charged with silylenolether (0.125 moles) and cooled to -78°C. The addition funnel charged with diamine (0.0625 moles) dissolved in an equal volume of THF is added over 5 minutes to the stirring enolether. The mixture is then allowed to warm to room temperature where it is stirred for one further hour. During either the addition of the diamine or the warm up period a thick white precipitate of ligand forms. This solid is filtered off and washed with methanol, boiled down in fresh methanol until white crystals appear, then left to stand and cool. Filtration yields colorless needles. Yields of specific compounds are listed in Table 2. Example 3 Preparation of ligand (H₂)DODECA-F[POA] Under a cover of nitrogen, a 100 ml reaction flask fitted with a reflux condenser, addition funnel and magnetic stir bar is charged with the t-butyl dimethylsilylenolether of hexafluoro-2,4-pentadione (9.66 g, 3 x 10⁻² moles). The addition funnel is charged with 1,3-diamino-2-propanol (POA) (1.35g, 1.5 X 10⁻² moles) in 5ml THF and this solution is then added over 5 mins, with stirring, to the enolether after which the reaction mixture is refluxed 15 hrs. Upon cooling and standing overnight a buff colored solid forms which is filtered off and recrystallized from hexane/CH₂Cl₂ 50/50 to give colorless blocks. The yield was 6.5%. Analytical data is reported in Table 3 below. Example 4 Preparation of metal complexes of Perfluoro bis-(β-ketoimine) ligands Under nitrogen, potassium methoxide (1.75 g, 0.025 moles) is dissolved in 150 ml dry methanol and 0.0125 mole of a bis-(β-ketoimine) ligand is added. The mixture is then stirred for 15 minutes to give a clear bright yellow solution. Solid metal dibromide (0.0125 moles) is then added and the mixture stirred an additional 1 hour. The mixture is then filtered, the methanol evaporated off from the filtrate and the resultant solid redissolved in toluene (100 ml). This solution is filtered to remove residual potassium bromide and the filtrate evaporated to a solid that is then sublimed under a dynamic vacuum to yield the product complex. The analytical data is reported in Table 4 below: Example 5 Relative volatility measurement of perfluoro β-ketoiminato complexes A standard weight loss experiment for each metal complex was conducted by heating a sample of approximately 50 mg at 10°C/min under a 100 cc/min flow of nitrogen using a DuPont Model No. 951. Thermal Gravimetric Analyzer in conjunction with a model No. 9900 Controller. Table 5 below indicates that all of the metal complexes tested in this way are clearly volatile, leaving as little as 0.641% residue at the end of an evaporation cycle. The data reported indicates that the evaporation of these complexes is a smooth process, i.e. a gradual and even transition from the solid to the gas phase. Volatility of Perfluoro bis-(β-ketoiminato) Copper Complexes Complex Temperature T°C at which complex is completely vaporized Residual weight left at T°C Cu⁺²DODECA-F[EDA] 245 1.07% Cu⁺²HEXADECA-F[EDA] 245 1.94% Cu⁺²EICOSA-F[EDA] 245 0. 641% Having thus described the present invention, what is now deemed appropriate for Letters Patent in set out in the following appended claims.

Claims: A chemically stable, β-ketoimine ligand having the structural formula: wherein R₁, R₂, R₄ and R₅ are independently linear or branched, perfluorinated C₁-C₈ alkyl groups, and R₃ is an organic functionality. A ligand in accordance with Claim 1 wherein R₃ is a C₁-C₈ alkyl, phenyl or hydroxyalkyl group. A ligand in accordance with Claim 1 wherein R₃ is a C₁-C₈ alkyl, phenyl or hydroxyalkyl group which is at least partially fluorinated. A ligand in accordance with Claim 1 wherein R₁, R₂, R₄ and R₅ are CF₃. A ligand in accordance with Claim 1 wherein R₁ and R₂ are independently perfluorinated methyl, ethyl or propyl groups. A ligand in accordance with Claim 5 wherein R₃ is CH₂CH₂. A ligand in accordance with Claim 1 wherein said ligand is 1,2-di-[4-imino-1,1,1,5,5,5-hexafluoro-2-pentanone]ethane. A ligand in accordance with Claim 1 wherein said ligand is 1,2-di[5-imino-1,1,1,2,2,6,6,6-octafluoro-3-hexanone]ethane. A ligand in accordance with Claim 1 wherein said ligand is 1,2-di-[6-imino-1,1,1,2,2,3,3,7,7,7-decafluoro-4-heptanone]ethane. A thermally volatilizable, β-ketoiminato metal complex having the structural formula: wherein R₁, R₂, R₄ and R₅ are independently linear or branched, perfluorinated, C₁-C₈ alkyl groups, R₃ is an organic functionality, M⁺² is a divalent metal ion. A metal complex in accordance with Claim 10 wherein R₃ is a C₁-C₈ alkyl, phenyl or hydroxyalkyl group. A metal complex in accordance with Claim 10 wherein R₃ is a C₁-C₈ alkyl, phenyl or hydroxyalkyl group which is at least partially fluorinated. A metal complex in accordance with Claim 10 wherein R₁, R₂, R₄ and R₅ are CF₃. A metal complex in accordance with Claim 10 wherein R₁ and R₂ are independently perfluorinated methyl, ethyl or propyl groups. A metal complex in accordance with Claim 14 wherein R₃ is CH₂CH₂. A metal complex in accordance with Claim 10 wherein M⁺² is Cu⁺². A metal complex in accordance with Claim 10 wherein M⁺² is Co⁺². A process for making a stable, β-ketoimine ligand having the structural formula: wherein R₁, R₂, R₄ and R₅ are independently linear or branched, perfluorinated C₁-C₈ alkyl groups, and R₃ is an organic functionality, said process comprising: a) treating β-diketones of the formulae R₁COCH₂COR₂ and R₄COCH₂COR₅ with potassium hydride under anhydrous conditions to produce compounds of the formulae R₁COCHCOR - / 2K⁺ and R₄COCHCOR - / 5 K+ ; b) treating the resultant R₁COCHCOR - / 2K⁺ and R₄COCHCOR - / 5 K+ with a silylchloride of the formula (R₆)₃SiCl, wherein each R₆ is independently an alkyl group, to produce silylenolethers of the formulae wherein R₁, R₂, R₄, R₅, and R₆ are as above; and (c) treating said silylenolethers with a primary diamine of the formula NH₂R₃NH₂ wherein R₃ is as described above to produce the desired B-ketoimine ligand. A process in accordance with Claim 18 wherein said silylchloride is t-butyldimethylsilylchloride. A process in accordance with Claim 18 wherein R₃ is a C₁-C₈ alkyl, phenyl or hydroxyalkyl group. A process in accordance with Claim 18, wherein the desired β-ketoimine ligand produced in step (c) is treated with potassium methoxide and the resultant compound is subsequently treated with a metal halide of the formula M⁺²(X) - / 2, wherein X is a halogen, to form a β-ketoiminato metal complex.

Inventors: NORMAN JOHN ANTHONY THOMAS, NORMAN, JOHN ANTHONY THOMAS
Applicants: AIR PROD & CHEM, AIR PRODUCTS AND CHEMICALS, INC.
Application year: 1989
Main classification: C07C251
IPC codes: C07C251, C07F15, C23C16, C07C249, C07F1, C07F7