Recording and reproducing apparatus and recording and reproducing method and recording medium for the recording and reproducing method

Abstract: A recording-reproducing apparatus, comprising a material (1), in which an intramolecular electron distribution can be changed, by electromagnetic wave irradiation and electric field application, a probe electrode (2) brought close to the material, a means (15) for projecting an electromagnetic wave onto the material, and a means (8) for applying an electric field between the material and the probe electrode, is provided.

Description: The present invention relates to a recording medium suitable for the writing of data by means of a probe that is scanned above the medium and suitable for the reading of data by measuring a tunnel current between the medium and a probe. The invention also provides an information recording method, an information reproducing method, a method of recording and erasing, and a recording, reproducing and/or erasing apparatus. The invention employs electromagnetic wave irradiation and application of an electric field during recording and carries out reproduction by detecting a tunnel current. Memory materials are of widespread application in the electronic industry, and are incorporated in computers and related apparatus, video disks and digital audio disks. The development of memory materials has been the subject of comprehensive research in recent years. Although the performance required for a memory material depends on the field in which it is applied, the generally required performance characteristics are set out below: (1) High recording density and large recording capacity (2) High response speed in recording and reproduction (3) Low consumption of electric power and (4) High productivity and low cost. Up to now memory materials have predominantly been semiconductors and magnetic materials. More recently as a result of progress in laser technology, low cost and high density recording media have been developed which employ an optical memory using a thin film of an organic colouring matter, a photopolymer etc. The scanning tunnelling microscope (hereinafter referred to as STM) has recently been developed and enables direct observation to be made of the electronic structure of the surface atoms or molecules of a conductor. It can exhibit a resolution of 0.3 nm [G. Binning et al., Phys. Rev. Lett., 49 (1982), 57]. Recently an experiment has been conducted using STM in which a pulse voltage has been applied between a probe electrode and an electroconductive material to locally fabricate the surface of the electroconductive material and to read the change of shape or state of the surface [J.S. Foster et al., Nature, 331 (1988), 324]. Furthermore STM has been used to investigate the switching characteristics and rectification characteristics of organic molecules [A. Aviram et al., Chem. Phys. Lett., 146 (1988), 490]. Conventional optical memories in practical use, even those having the highest density and the largest recording capacity, have a recording capacity of at most 10 8 bit/cm 2 , which is becoming insufficient for image recording in modern computers and video apparatus. Although STM can be used for recording and reproduction with a bit size which is of the order of an interatomic or intermolecular distance (0.5 to 50 nm), it is not satisfactory from the viewpoint of reproducibility or stability, and its recording and erasing mechanism has not been elucidated. Furthermore, when a molecule is accessed by STM to enable its electric characteristics to be measured, the record can sometimes be affected by the operation of reproducing (voltage application) because both recording and reproduction are carried out by application of a voltage. Therefore STM is not satisfactory for memory applications. The problem with which the invention is concerned is therefore the provision of a recording/reproducing apparatus in which recording can be carried out with improved reproducibility and stability, and which has a large recording capacity. This problem is solved by the provision of a recording medium having the features of claim 1 of the accompanying claims. The invention also is concerned with an information recording method as set out in claim 12 of the accompanying claims, apd an information reproducing method as set out in claim 13 of the accompanying claims, a recording-erasing method as set out in accompanying claim 14, a recording, reproducing and/or erasing apparatus as set out in claim 15 or 16 and a recording-erasing method as set out in claim 17. EP-A-0238759 discloses a recording-reproducing apparatus which comprises a recording medium in the form of a thin film of an organic charge transfer complex containing donor molecules and acceptor molecules. Voltage is applied to the thin organic film by a pair of electrodes which brings about charge transfer between the donor molecules and the acceptor molecules. Information is recorded as a result of the change in optical or electrical characteristics of the organic thin film as a result of the charge transfer. Selective light irradiation is performed while a voltage is applied between the electrodes. However there is no disclosure in this specification of a recording medium suitable for scanning tunnelling electromicroscopy. A further optical device using an organic charge transfer material as a switching and storage medium is disclosed in WO84/03169. EP-A-0272935 discloses a recording device which comprises a probe electrode and a recording medium and which works by scanning tunnelling microscopy. The recording medium is stated to have a so-called "electric memory effect" but this effect is produced simply by the application of different voltages to the recording medium. How the invention may be put into effect will now be described by way of example only, with reference to the accompanying drawings. Fig. 1 illustrates a block constitution of the embodiment of a recording-reproducing apparatus of the present invention. Fig. 2 illustrates a block constitution of another embodiment of a recording-reproducing apparatus of the present invention. Fig. 3 illustrates an example of the signal in recording operation. Fig. 4 illustrates an example of the signal in erasing operation. Fig. 5 shows the principle of recording by memory materials. Fig. 6 shows a memory material and the principle of erasing therewith. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention is described in detail below. The materials employed in the present invention are those, in which an electron distribution in the molecule can be changed, by irradiation of an electromagnetic wave and application of voltage. Embodiment of the materials includes (1) memory materials, in which a redox pair (an oxidation-reduction pair) within the molecule or between the molecules is formed due to isomerization in the molecular structure by electromagnetic wave irradiation, and an electron distribution in the molecule is changed due to proton transfer in the redox pair by further electric field application, and (2) memory materials, in which an molecular distribution in the molecule is changed, by irradiation with electomagnetic wave and simultaneous application of an electric voltage exceeding the threshold voltage for causing memory effect. Embodiment (1) of the memory materials includes specifically azo compounds having a quinone group and a hydroquinone group within the molecule, styrene derivatives having a quinone group and a hydroquinone group within the molecule, imino compounds having a quinone group and a hydroquinone group within the molecule, azo compounds having two amino groups within the molecule, styrene derivatives having two amino groups within the molecule, and imino compounds having two amino groups within the molecule. Examples of the preferred compounds are shown below: (In the formulae, R 1 - R 5 are CH 3 , C 2 H 5 , or isopropyl, and the positions of =O, or -OH are in the relation of ortho, meta, or para positions.) Compounds of Nos. 1, 2, 4 and 5 among them are particularly preferred because of a high photoisomerication efficiency. By use of these materials, the recording/reproducing/erasing are conducted as follows. The electromagnetic wave irradiation onto the material causes isomerization in the molecular structure, forming a redox pair in the molecule, and further application of voltage causes proton transfer within the redox pair, resulting in change in intramolecular electron distribution into the recorded state of the present invention. Erasing is conducted by irradiation of electromagnetic wave onto the recorded portion and simultaneous application of electric field in the reverse direction to cause reversed proton transfer. In a non-irradiated state, application of an electric field onto the material does not cause the proton transfer and the resulting change of intramolecular electron distribution since no redox pair is present. Thus, in the memory material employed here, recording and erasing can be conducted by voltage application only under irradiation of an electromagnetic wave. In reproduction, since the material is not irradiated, no change occurs in recorded and erased states by application of an electric field between the memory material and the probe for tunnel current detection. Embodiment (2) of the memory materials includes charge transfer complexes of a metal with an organic electron acceptor. Specific examples are, for example, n-octadecyltetracyanoquinodimethan copper complex (ODTCNQ/Cu), n-dodecyltetracyanoquinodimethan copper complex (DDTCNQ/Cu), n-octadecyltetracyanoquinodimethan silver complex (ODTCNQ/Ag), n-dodecyltetracyanoquinodimethan silver complex (DDTCNQ/Ag), and their derivatives. By employing these materials, the recording/reproduction/erasing are conducted as follows. Recording is conducted by applying to a probe electrode a voltage exceeding a threshold voltage for giving a memory effect corresponding to the information while irradiating an electromagnetic wave (or light); reproduction is conducted by applying a voltage to the probe electrode, and scanning the material with the probe electrode keeping a constant distance between the material and the probe electrode, and detecting the change of intensity of current flowing the probe electrode; and erasing is conducted by introducing vibration energy to the material. Such memory material is used by depositing it on an electrode material. As the electrode material, any material may be used which is capable of forming a film having electroconductivity and smoothness. Examples of suitable materials are Au/Pd, Pt, n + -Si, ITO, etc. A preferable method for depositing a memory material onto an electrode is the Langmuir-Blodgette process in view of easiness of formation of a uniform, and defectless thin film with high regularity. For projecting an electromagnetic wave onto the memory material, any electromagnetic wave source may be employed which emits a light having a wavelength of from visible to infrared retions. Various light sources can be used as desired such as a xenon lamp, a helium-neon laser, an argon laser, a semiconductor laser, and carbon dioxide laser. The application voltage may be varied in connection with the light intensity. Fig. 1 illustrates a block constitution of a recording apparatus of the present invention, where the numeral 5 denotes a probe current amplifier; 6 denotes a servo circuit for controlling fine adjusting mechanism 7 which employs a piezo-element to maintain the probe corrent constant; and 8 denotes a power source for applying a pulse voltage between probe electrode 2 and electrode 3 for recording/erasing. On application of a pulse voltage, the probe current abruptly changes, so that servo circuit 6 controls the HOLD circuit to be in an ON state during the change to maintain the output voltage constant. 9 is an XY scan-driving circuit for controlling the movement of probe electrode 2 in the XY directions. 10 is a coarse adjusting mechanism and 11 is a coarse adjusting-driving circuit, which coarsely control the distance between probe electrode 2 and recording medium 1 so as to give a probe current of approximately 10 -9 A. These mechanisms are all subjected to central control of microcomputor 12 . 13 is a display device. 14 is an XY stage. 15 and 16 are each an electromagnetic wave source. Examples of the mechanical performances in movement control employing a piezo-element are shown below. Range of fine movement control in the Z direction: 0.1 nm to 1 nm Range of coarse movement control in the Z direction: 10 nm to 10 mm Range of scanning in the XY directions: 0.1 nm to 1 nm Tolerance in measurement and control: less than 0.1 nm The examples below are intended to illustrate specifically the present invention. Example 1 Fig. 1 illustrates a recording-reproducing apparatus of the present invention. Probe electrode 2 is made of platinum/rhodium. Probe electrode 2 is finely controlled by a piezo-element to keep the distance (Z) from the surface of recording layer 101 to maintain the current at a constant level. Fine movement control mechanism 7 is designed to control finely the movement of the probe electrode in the plane (XY) direction with retention of the distance Z. Probe electrode 2 is capable directly of recording, reproducing and erasing information. The recording medium is placed on XY stage 14 and can be moved to a desired position. The film of octadecyltetracyanoquinodimethan copper complex (ODTCNQ/Cu) was formed in the following procedure. A solution of 4 x 10 -6 M ODTCNQ/Cu in acetonitrile (ACN) was prepared. The solution was spread on pure water at 20°C, and the surface pressure was raised to 20 mN/m to form a monomolecular film on the surface of water. A glass substrate having a vapor-deposited gold/palladium (Au/Pd) film of 300 Å thick which had been previously immersed in the water phase was slowly pulled up at a rate of 5 mm/min in the direction crossing the water surface with the surface pressure maintained constant to form a monomolecular film of ODTCNQ/Cu on the glass substrate having vapor-deposited Au/Pd. This was employed as recording medium 1. The experiment on recording-reproducing-erasing was conducted by employing recording medium 1 having a monolayer LB film of the ODTCNQ/Cu. Firstly, recording medium 1 was placed on XY stage 14, and probe electrode 2 was fixed at a visually determined position. The distance Z between probe electrode 2 and the surface of recording layer 101 was adjusted by applying the voltage of 3 V between Au/Pd electrode 3 and the probe and by monitoring the current. On application of voltage of +300 mV to probe electrode 2, the current was found to be not more than 1 pA. After stopping an application of the voltage, the recording was conducted by irradiating a light to recording medium 1 with xenon lamp 15 and by applying again a voltage of +5 V to probe electrode 2. The recording medium was found to have transferred to an ON state in which the electricity flowed well. The light irradiation and the voltage application were stopped, and then at the same position, a voltage of +300 mV was applied to probe electrode 2 to reproduce the record. A current of 5 nA was found to flow there, which shows the retention of the ON state, namely the retention of the record. After stopping an application of a voltage argon laser 16 was projected onto the recorded portion and vibration energy was given thereto. The vibration energy shall mean here an electromagnetic wave having about one figure smaller energy amount than that of an electromagnetic wave used for recording. Thereafter at the same position, a voltage of +300 mV was applied again to probe electrode 2 to reproduce the record. A current of not more than 1 pA was found to flow, which shows the transition to an OFF state, namely erasure of the record. Example 2 The recording-reproducing apparatus illustrated in Fig. 1 was employed in the same manner as in Example 1. The film of dodecyltetracyanoquinodimethan copper complex (DDTCNQ/Cu) was formed in the following procedure. A solution of 4 x 10 -6 M DDTCNQ/Cu in acetonitrile (ACN) was prepared., The solution was spread on pure water at 20°C, and the surface pressure was raised to 20 mN/m to form a monomolecular film on the surface of water. A glass substrate having a vapor-deposited gold/palladium (Au/Pd) film of 300 Å thick which had been previously immersed in the water phase was slowly pulled up at a rate of 5 mm/min in the direction crossing the water surface with the surface pressure maintained constant to form a monomolecular film of DDTCNQ/Cu on the glass substrate having vapor-deposited Au/Pd. This was employed as recording medium 1. The experiment on recording-reproducing-erasing was conducted by employing recording medium 1 having a monolayer LB film of the DDTCNQ/Cu. Firstly, recording medium 1 was placed on XY stage 14, and probe electrode 2 was fixed at a visually determined position. The distance Z between probe electrode 2 and the surface of recording layer 101 was adjusted by applying the voltage of 3 V between Au/Pd electrode 3 and the probe and by monitoring the current. On application of voltage of +300 mV to probe electrode 2, the current was found to be not more than 1 pA. After stopping an application of the voltage, the recording was conducted by irradiating a light to recording medium 1 with xenon lamp 15 and by applying again a voltage of +5 V to probe electrode 2. The recording medium was found to have transferred to an ON state in which the electricity flows well. The light irradiation and the voltage application were stopped, and then at the same position, a voltage of +300 mV was applied to probe electrode 2 to reproduce the record. A current of 5 nA was found to flow, which shows the retention of the ON state, namely the retention of the record. After stopping an application of the voltage, argon laser 16 was projected onto the recorded portion and vibration energy was given thereto. Thereafter at the same position, a voltage of +300 mV was applied again to probe electrode 2 to reproduce the record. A current of not more than 1 pA was found to flow, which shows the transition to an OFF state, namely erasure of the record. Example 3 The recording-reproducing apparatus illustrated in Fig. 1 was employed in the same manner as in Example 1. The film of octadecyltetracyanoquinodimethan silver complex (ODTCNQ/Ag) was formed in the following procedure. A solution of 4 x 10 -6 M ODTCNQ/Ag in acetonitrile (ACN) was prepared. The solution was spread on pure water at 20°C, and the surface pressure was raised to 15 mN/m to form a monomolecular film on the surface of water. A glass substrate having a vapor-deposited gold/palladium (Au/Pd) film of 300 Å thick which had been previously immersed in the water phase was slowly pulled up at a rate of 5 mm/min in the direction crossing the water surface with the surface pressure maintained constant to form a monomolecular film of ODTCNQ/Ag on the glass substrate having vapor-deposited Au/Pd. This was employed as recording medium 1. The experiment on recording-reproducing-erasing was conducted by employing recording medium 1 having a monolayer LB film of the ODTCNQ/Ag. Firstly, recording medium 1 was placed on XY stage 14, and probe electrode 2 was fixed at a visually determined position. The distance Z between probe electrode 2 and the surface of recording layer 101 was adjusted by applying the voltage of 3 V between Au/Pd electrode 3 and the probe and by monitoring the current. On application of voltage of +300 mV to the probe electrode 2, the current was found to be not more than 1 pA. After stopping an application of the voltage, the recording was conducted by irradiating a light to recording medium 1 with a helium-neon laser in place of xenon lamp 15 and applying again a voltage of +3 V to probe electrode 2. The recording medium was found to have transferred to an ON state in which the electricity flowed well. The light irradiation and the voltage application were stopped, and then at the same position, a voltage of +300 mV was applied to the probe electrode 2 to reproduce the record. A current of 5 nA was found to flow, which shows the retention of the ON state, namely the retention of the record. After stopping an application of the voltage, a carbon dioxide laser in place of argon laser 16 was projected onto the recorded portion and vibration energy was given thereto. Thereafter at the same position, a voltage of +300 mV was applied again to probe electrode 2 to reproduce the record. A current of not more than 1 pA was found to flow, which shows the transition to OFF state, namely erasure of the record. Example 4 The recording-reproducing apparatus illustrated in Fig. 1 was employed in the same manner as in Example 1. The film of octadecyltetracyanoquinodimethan silver complex (ODTCNQ/Ag) was formed in the following procedure. A solution of 4 x 10 -6 M ODTCNQ/Ag in acetonitrile (ACN) was prepared. The solution was spread on pure water at 20°C, and the surface pressure was raised to 15 mN/m to form a monomolecular film on the surface of water. An n + -Si substrate which had been previously immersed in the water phase was slowly pulled up at a rate of 5 mm/min in the direction crossing the water surface with the surface pressure maintained constant to form a monomolecular film of ODTCNQ/Ag on the n + -Si substrate, which was employed as recording medium 1. The experiment on recording-reproducing-erasing was conducted by employing recording medium 1 having a monolayer LB film of the ODTCNQ/Ag. Firstly, recording medium 1 was placed on XY stage 14, and probe electrode 2 was fixed at a visually determined position. The distance Z between probe electrode 2 and the surface of recording layer 101 was adjusted by applying the voltage of 3 V between electrode (n + -Si) 3 and the probe and by monitoring the current. On application of voltage of +300 mV to probe electrode 2, the current was found to be not more than 1 pA. After stopping an application of the voltage, the recording was conducted by irradiating a light to recording medium 1 with helium-neon laser 15 and by applying again a voltage of +3 V to probe electrode 2. The recording medium was found to have transferred to an ON state in which the electricity flowed well. The light irradiation and the voltage application were stopped, and then at the same position, a voltage of +300 mV was applied to probe electrode 2 to reproduce the record. A current of 5 nA was found to flow, which shows the retention of the ON state, namely the retention of the record. After stopping an application of the voltage, carbon dioxide laser 16 was projected onto the recorded portion and vibration energy was given thereto. Thereafter at the same position, a voltage of +300 mV was applied again to probe electrode 2 to reproduce the record. A current of not more than 1 pA was found to flow, which shows the transition to OFF state, namely erasure of the record. Example 5 Fig. 2 illustrates an example of another embodiment of the present invention. In the Fig., memory material 103 (described later) is adhered by the Langmuir-Blodgette process or other method onto electroconductive transparent electrode 102 such as ITO (indium-tin oxide) provided on glass plate 101. Further probe 104 is brought to proximity of approximately sub-nanometer to the desired position of the memory material by means of a probe-position-controlling means. Probe 104 is made of an electrolytically polished tungsten wire, a mechanically cut platinum wire, or the like having a sharp tip (a radius of curvature of less than 1 µm) and is electroconductive. Probe-position-controlling means 105 comprises such as a PTZ element and serves to move probe 104 to a desired position within a plane and the normal line direction in the memory area. Writing/erasing is conducted in the following manner. Firstly, electromagnetic wave 108 is projected onto memory material 103 in the memory region through the glass substrate 101 and the transparent electrode by operating electromagnetic wave source 107 with lens 109 in accordance with the signal from writing/erasing signal generator 106. Simultaneously the signal from writing/erasing singal generator 106 is sent to transparent electrode 102 to apply the electric field formed between transparent electrode 102 and probe 104 to the desired position of memory material 103, thus writing or erasing being conducted. Examples of the signals in writing are shown in Fig. 3A to Fig. 3C. Fig. 3A shows a signal given to probe-position-controlling means 105, by which probe 104 accesses the desired position in the memory region. Fig. 3B shows an electromagnetic-wave-source-operating signal. Fig. 3C shows a writing signal given to the memory material. The writing is conducted at a memory position where the two signals are given simultaneously (namely region M in Fig.3). Examples of signals in erasing are shown in Fig. 4A to Fig. 4C, which illustrate erasing in the region where the writing has been conducted in the process shown in Fig. 3. Fig. 4A and Fig. 4B are the same as Fig. 3A and Fig. 3B, and Fig. 4C shows an erasing signal given to the memory material. The erasing is conducted at a memory position where the two kinds of signals are given simultaneously (namely region E in Fig. 4). Readout is conducted in the following manner. A bias voltage is applied by bias source 110 onto the memory material on transparent electrode 102, and tunnel current 111 flowing between memory material 103 and probe 104 which is in the proximity of sub-nanometer to memory material 103 is detected by means of current detecting circuit 112. The tunnel current intensity at a written portion (being in an ON state) is different from the intensity at a non-written portion or an erased portion (being in an OFF state) on memory material 103 because the electron distribution state on the surface and the inside of the memory material is different between the two state. This difference of the tunnel current intensity is treated with readout treating circuit 113 to provide a readout signal (ON-OFF signals). Examples of signals in readout operation are shown in Fig. 3D and Fig. 4D. Fig. 3D shows the tunnel current signal detected, after writing is conducted as described referring to Fig. 3A to Fig. 3C, by scanning again the same region. In this example, the tunnel current increases at the portions corresponding to the written portions. Fig. 4D shows the tunnel current signal detected, after erasing is conducted as described by referring to Fig. 4A to Fig. 4C, by scanning again the same region. The memory material employed in the present invention and the principle of writing/erasing therein are described below. As an example of the memory material, an azo compound is taken which has the structure shown in Fig. 5A (in which the positions of the quinone groups, and the hydroquinone groups include ortho, meta, and para positions). Irradiation to the compound with light of wavelength of 400 nm causes photoisomerization from the trans configuration to the cis configuration at the azo group in the molecule to give the structure shown in Fig. 5B. With the irradiation of the light maintained, the application of an electric field between transparent electrode 102 and probe 104 in the direction as shown in the figure causes proton (H + ) transfer between the quinone group and the hydroquinone group, which are in a hydrogen-bonded state, giving the structure shown in Fig. 5C. On stopping the light irradiation, a photoisomerization occurs again from the cis configuration to the trans configuration to give the structure shown in Fig. 5D. This structure corresponds to the written state which is different from the structure of the initial state shown in Fig. 5A in the intramolecular electron distribution and is caused by the proton transfer between the hydroquinone group and the quinone group. As the result, the shape of the tunnel barrier between transparent electrode 102 and probe 104 changes corresponding to the structure as shown in Fig. 5A (the initial state) and the structure as shown in Fig. 5D (the written state), thus giving the change of the tunnel current intensity flowing under the application of the bias voltage between transparent electrode 102 and probe 104. The detection of this change enables the discrimination of the states of the molecules (the initial state and the written state) at the position, to which probe 104 is in access. An example of the detected tunnel current signals are shown in Fig. 3D, corresponding to the instance of Fig. 3A to Fig. 3C in which the tunnel current rises at the portion in the written state in comparison with the initial state. The erasing of the written state of the memory material shown in Fig. 5 is explained in reference to Fig. 6. Irradiation with light of wavelength of 400 nm onto the compound having the structure shown in Fig. 6A in a written state causes photoisomerization of the compound from the trans configuration to the cis configuration at the azo group in the molecule to give the structure shown in Fig. 6B. With the light irradiation maintained, the application of an electric field between transparent electrode 102 and probe 104 in the direction shown in Fig. 6C (in the direction reverse to that shown in Fig. 5C) causes proton (H + ) transfer between the quinone group and the hydroquinone group which are in a hydrogen-bonded state, giving the structure shown in Fig. 6C. On stopping the light irradiation, the photoisomerization occurs again from the cis configuration of the trans configuration to give the structure shown in Fig. 6C. This structure corresponds to an erased state which is the same as the initial state shown in Fig. 5A. The erasing of the written state is conducted in such a manner. An example of the detected tunnel current is shown in Fig. 4D corresponding to Fig. 4A to Fig. 4C. In the position where once writing was conducted and then erasing has been conducted, the tunnel current falls to the same value as that at the initial state. The experiments of recording-reproducing-erasing were repeatedly conducted with the memory material shown in Fig. 5 and Fig. 6 by employing the apparatus having the constitution as shown in Fig. 2 in the same manner above. The result showed that recording/erasing could be made at least approximately 100 times of repetition without deterioration of the memory material and the reproduction without causing the change of the recording-erasing state. The memory materials employed in the present invention are those capable of undergoing photoisomerization between a trans configuration and a cis configuration (or between a syn configuration and an anti-syn configuration) on light irradiation. Such materials include those having a carbon-carbon double bond or an imino group in addition to the material employed in the above examples having an azo group. The redox pair undergoing proton transfer on application of an electric field includes a hydrogen bonding system of amino group-amino group in addition to the hydrogen bonding system of quinone group-hydroquinone group employed in the above examples. As described above, the recording-reproducing apparatus of the present invention which is based on the principle of STM can conduct recording and erasing by electromagnetic wave irradiation and electric field application on a memory material, and conduct reproduction by tunnel current detection, so that it enables a large capacity of recording and reproducing without change of record at reproduction with reproducibility and stability. With a bit size of 10 nm for the recording, a large capacity of a recording-reproducing apparatus of as large as 10 12 bit/cm 2 is achievable. Further, the present invention has the advantages as follows: The formation of a monomolecular film in the present invention according to an LB process can give a film having an excellent order of the molecules and a high density, which is suitable for super-high-density recording media. An erroneous writing is prevented at the time of reproduction because recording is conducted under irradiation of light. The storage stabilty is excellent because erasing of a record requires a vibration energy to be given.

Claims: A recording medium suitable for the writing of data by means of a probe that is scanned above the medium and suitable for the reading of data by measuring a tunnel current between the medium and a probe, said medium comprising (a) a conductive substrate and (b) a recording layer carried by the substrate which has first and second states between which it can be switched, the layer being readable by applying a voltage to the probe electrode, scanning the layer with the probe electrode, and detecting changes of current flowing in the probe electrode, the first and second states giving rise to different tunnel current; characterised in that switching of the recording layer from the first state to the second state is by simultaneous application of a voltage and irradiation with electromagnetic waves, and characterised in that the recording layer comprises either (i) a compound that on switching responds to the electromagnetic waves by forming an isomeric structure in which there is a redox pair within its molecules or between its molecules and responds to the voltage by proton transfer in the redox pair, so that the effect of the voltage and electromagnetic wave irradiation is to alter the electron distribution in the compound, said compound being selected from: (a) azo compounds having a quinone group and a hydroquinone group within the molecule; (b) styrene derivatives having a quinone group and a hydroquinone group within the molecule; (c) imino compounds having a quinone group and a hydroquinone group within the molecule; (d) azo compounds having two amino groups within the molecule; (e) styrene derivatives having two amino groups within the molecule; and (f) imino compounds having two amino groups within the molecule; or (ii) a compound which is a charge transfer complex of a metal with an organic electron acceptor, said complex being selected from: (a) n-octadecyltetracyanoquinodimethane copper complex; (b) n-dodecyltetracyanoquinodimethane copper complex; (c) n-octadecyltetracyanoquinodimethane silver complex; and (d) n-dodecyltetracyanoquinodimethane silver complex. The medium of claim 1, wherein the recording layer containing compound (ii) is switched from the second state to the first state by irradiation with electromagnetic waves. The medium of claim 1, wherein the recording layer containing compound (i) is switched from the second state to the first state by the simultaneous application of a voltage of opposite polarity to that for recording and electromagnetic waves. The medium of any preceding claim, wherein the substrate is transparent so that the irradiation can be from a face of the medium opposite to that which carries the layer. The medium of any preceding claim, wherein the layer is carried by a smooth electroconductive substrate of Au/Pd, Pt, n + -Si or ITO. The medium of claim 5, wherein the substrate is of glass carrying an Au/Pd film or is of n + -Si. The medium of any preceding claim, wherein the recording layer comprises a Langmuir-Blodgett film. The medium of any preceding claim wherein the compound is of any of formulae (i)-(vi) wherein R 1 - R 5 represent CH 3 , C 2 H 5 or isopropyl and the =0 and -OH groups may be in the meta- and para-positions as well as the ortho-position. The medium of any preceding claim, recorded with digital information. The medium of claim 9, wherein the bit size of the recorded information is 0.5 to 50 nm. The medium of any preceding claim, recorded with 10 8 -10 12 bits/cm 2 . An information recording method comprising the steps of: providing a recording medium as claimed in any of claims 1-11; bringing an electrically conductive probe having a pointed tip close to said recording layer; projecting first electromagnetic waves onto said recording layer, applying a first voltage between said recording layer and said conductive probe for applying an electric field to said layer; and thereby changing the intramolecular electron distribution in the recording layer to write information to said layer. An information reproducing method comprising the steps of: providing a medium according to any of claims 1-11 recorded with information according to claim 12; bringing an electrically conductive probe having a pointed tip close to the recording layer; applying a second voltage between said recording layer and said conductive probe; and detecting a tunnel current flowing through said recording layer to read out information therefrom. A recording-erasing method, comprising the steps of: providing a recording medium as claimed in any of claims 1 and 3-11; bringing an electrically conductive probe having a pointed tip close to the recording layer of said medium; projecting a first electromagnetic wave onto said recording layer; applying a first voltage between said recording layer and said conductive probe for applying an electric field to said recording layer; changing the intramolecular electron distribution of a compound in the recording layer to write information thereto; projecting a second electromagnetic wave onto a written portion of said recording layer; applying a second voltage between said recording layer and said conductive probe for applying an electric field to said material; and erasing said written information. A Apparatus for carrying out any one or more of the operations recording, reproducing and erasing, comprising: a recording medium; an electrically conductive probe having a pointed tip; a means for changing a distance between said probe and said recording medium; and a means for applying a pulse voltage between said recording medium and said conductive probe. characterised in that the recording medium is as claimed in any of claims 1-11, and in that means is provided for projecting electromagnetic waves onto said recording medium. An apparatus for recording, reproducing and/or erasing according to claim 15, further comprising a means for applying a bias voltage between said electrode and said conductive probe and a means for detecting current flowing between said electrode and said conductive probe. A recording-erasing method, comprising the steps of: providing a recording medium as claimed in any of claims 1, 2 and 4-11; bringing an electrically conductive probe having a pointed tip close to the recording layer of said medium; projecting a first electromagnetic wave onto said recording layer; applying a first voltage between said recording layer and said conductive probe for applying an electric field to said recording layer; changing the intramolecular electron distribution of a compound in the recording layer to write information thereto; projecting a second electromagnetic wave onto a written portion of said recording layer; and erasing said written information.

Inventors: KAWADA HARUKI, MATSUDA HIROSHI, NOSE HIROYASU, TAKIMOTO KIYOSHI, KAWADA, HARUKI, MATSUDA, HIROSHI, NOSE, HIROYASU
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1989
Main classification: G11B9
IPC codes: G11B11, G11B9, G11B13