Method of melting ceramic superconductive material

Abstract: A ceramic superconductive material (1) including a compound containing oxygen and at least two types of metal elements and having layer structure is molten in a vessel (2), at least an inner surface (3) of which is formed of a solid solution alloy having a base of gold or silver. Preferably the alloy is prepared from Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd.

Description: Field of the Invention The present invention relates to a method of melting a ceramic superconductive material. Description of the Background Art In recent years, ceramic superconductive materials have been watched as materials having higher critical temperatures of superconductivity. In order to obtain a desired superconducting product with such a ceramic superconductive material, generally employed is a method of compacting the superconductive material and thereafter sintering the same, while another method of shaping a ceramic superconductive material by melting and solidifying the same is recently watched with interest. However, it is empirically known that, in the method of melting a ceramic superconductive material for shaping the same into a wire rod or a thin film, the superconductive material may react with or be contaminated by the wall of a vessel such as a crucible employed for melting the superconductive material, cf. "Nature" Vol.328, 13. August 1987, pp. 601-6 and hence desired superconductor composition cannot be obtained or the superconductor is deteriorated in superconductivity. Accordingly, the present invention has been proposed to solve aforementioned problems, and an object thereof is to provide a method of melting a superconductive material which can attain desired composition with small deterioration in superconductivity. The present invention is directed to a method of melting a ceramic superconductive material such as a superconductive material including a compound containing oxygen and at least three types of metal elements and having layer structure, for example. In order to solve the aforementioned technical problems, the superconductive material is molten in a vessel which is at least internally formed of a solid solution alloy of Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd. The present invention is further directed to a vessel for melting a ceramic superconductive material therein having an inner surface being in contact with a ceramic superconductive material to be molten, at least said inner surface being formed of a solid solution alloy of Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd. The present invention has been proposed on the basis of such recognition that the aforementioned superconductive material can be effectively molten in a vessel which is at least internally formed of said solid solution alloy with no reaction with or contamination from the wall of the vessel. The solid solution alloy causes no reaction with the superconductive material since all metals forming the alloy are so dissolved with each other that no metal is left independent. Further, it is possible to adjust the melting point of the solid solution alloy at least internally forming the vessel by varying the content of an alloying element. Thus, various types of ceramic superconductive materials can be molten at different temperatures by adjusting the melting point of the solid solution alloy. For example, it is possible to melt superconductive materials having relatively high melting points such as those of Y-Ba-Cu-O and rare earth element-Ba-Cu-O systems as well as materials having relatively low melting points such as those of Bi-Sr-Ca-Cu-O, Bi-Pb-Sr-Ca-Cu-O and Tl-Ca-Ba-Cu-O systems. In particular, the present invention is suitable for melting the latter superconductive materials having relatively low melting points such as those of Bi-Sr-Ca-Cu-O, Bi-Pb-Sr-Ca-Cu-O and Tl-Ca-Ba-Cu-O systems. The inventor has found that gold or silver causes no reaction with a ceramic superconductive material, and selected an element which can increase the melting point and strength against a high temperature with a relatively small content with respect to gold or silver, to provide an alloy for at least internally forming the vessel. To this end, palladium was noted as an element for forming a solid solution alloy with gold or silver. Palladium can be completely dissolved in gold or silver to increase the melting point by about 90°C per atomic percentage. Although palladium itself reacts with a ceramic superconductive material, the degree of such reaction can be neglected if the content thereof is not more than 40 percent by weight. However, if the palladium content is less than 5 percent by weight, the melting point cannot be much increased and strength against a high temperature is rendered so insufficient that the vessel may be uselessly deformed in employment. Thus, a prescribed amount of palladium is added to gold or silver to enable increase in strength against a high temperature as well as increase in melting point due to alloying within a range causing no reduction in an effect of suppressing reaction of gold or silver, whereby an alloy of Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd can be advantageously employed as a material for at least internally forming a vessel for melting a superconductive material. These and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a sectional view showing a crucible employed in the present invention for melting a ceramic superconductive material. DESCRIPTION OF THE PREFERRED EMBODIMENTS Referring to Fig. 1, a ceramic superconductive material 1 is molten in a crucible 2. In order to melt the superconductive material 1, heat is applied to the crucible 2 by a heater means (not shown). The crucible 2 is formed of an alloy of Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd as a whole, for example. Alternatively, only an inner surface 3 of the crucible 2, which is brought into contact with the superconductive material 1, may be formed of the aforementioned alloy. In order to confirm an effect of the present invention, crucibles of 0.5 mm in thickness were prepared from materials listed in Table 1 to melt superconductive materials in the atmosphere at temperatures also shown in Table 1, thereby to obtain melts of Examples 1 to 8 and Reference Examples 1 to 3. The melts were cooled at the rate of 10°C/min and solidified. Table 1 also shows observation results of melting states in the crucibles and states of deformation of the crucibles in Examples 1 to 8 and Reference Examples 1 to 3 respectively. As understood from Table 1, no reaction was caused between the melt and the crucible while the crucible was not deformed in each of Examples 1 to 8. In Reference Example 1, on the other hand, the crucible was deformed to cause break-out although no reaction was caused between the melt and the crucible. In Reference Example 2, strong reaction was caused between the melt and the crucible and the crucible was partially perforated to cause break-out, although the same was not deformed. In Reference Example 3, strong reaction was caused between the melt and the crucible although the crucible was not deformed. Table 2 shows critical temperatures T C observed after holding the samples shown in Table 1 in the atmosphere at different temperatures for different periods and annealing the same at the rate of 2°C/min. Annealing Condition Tc Example 1 850°C x 6h, Annealed 83K 2 800°C x 6h, Annealed 80K 3 900°C x 10 min, Annealed 100K 4 820°C x 6 h, Annealed 78K 5 800°C x 4 h, Annealed 79K 6 910°C x 15 min, Annealed 110K 7 900°C x 6 h, Annealed 92K 8 845°C x 250 h, Annealed 105K Reference Example 1 Sampling Impossible - 2 800°C x 4 h, Annealed 55K 3 900°C x 6 h, Annealed 70K As understood from Table 2, the critical temperature exceeded the liquid nitrogen temperature in each of Examples 1 to 8. On the other hand, it was not possible to sample Reference Example 1, which caused break-out as hereinabove described. Further, it may be judged that Reference Examples 2 and 3, which presented low critical temperatures, were deteriorated in superconductivity due to reaction with the crucibles, as compared with Examples 5 and 7.

Claims: A method of melting a ceramic superconductive material, comprising the steps of: preparing a vessel at least internally formed of a solid solution alloy of Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd; introducing a ceramic superconductive material into said vessel; and melting said ceramic superconductive material in said vessel. A method in accordance with claim 1, wherein said ceramic superconductive material includes a compound containing oxygen and at least three types of metal elements and having layer structure. A method in accordance with claim 2, wherein said ceramic superconductive material includes one of those of Bi-Sr-Ca-Cu-O and Bi-Pb-Sr-Ca-Cu-O systems. A vessel for melting a ceramic superconductive material therein, said vessel (2) having an inner surface (3) being in contact with a ceramic superconductive material to be molten, at least said inner surface (3) being formed of a solid solution alloy of Au - 5 to 40 wt.% Pd or Ag - 5 to 40 wt.% Pd.

Inventors: HAYASHI KAZUHIKO C O OSAKA WOR, HAYASHI, KAZUHIKO C/O OSAKA WORKS OF
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1989
Main classification: H01L39
IPC codes: C04B35, C30B9