Drilling fluid additives

Abstract: Drilling fluid additives which are able to display the properties of drilling fluid constantly regardless of presence or absence of salts, composed of water-soluble copolymer ( A ) having average molecular weight of 1,000 ∼ 50,000, which are led from monomer components composed of a monomer ( I ) of 40 ∼ 99.5 molar percentages in a series of unsaturated carboxylic acids, as shown in the following general formula ( I ), and an unsaturated monomer ( II ) of 0.5 ∼ 60 molar percentages in a series of ( meth )allylethers, as shown in the general formula ( II ). In the formula ( I ), each of A¹ and A² independently represents hydrogen, methyl, or -COOX², and A¹ and A² are not -C00X² at the same time. A³ represents hydrogen, methyl, or -CH₂COOX³ and, in a case that A³ is -CH₂C00X³, each of A¹ and A² independently represents hydrogen or methyl. Each of X¹, X², and X³, independently or at the same time represents hydrogen, monovalent metal, divalent metal, ammonium, or organic amine. In the formula ( II ) R¹ represents hydrogen or methyl , and Z represents hydroxyl; a sulfonic acid group or its monovalent metal salt, divalent metal salt, ammonium salt, and organic amine salt; a phosphoric ( or phosphorous ) acid group or its monovalent metal salt, divalent metal salt, ammonium salt, and organic amine salt.

Description: BACKGROUND OF THE INVENTION The present invention relates to additives used for stabilization of muddy water, that is drilling fluid, which is used in cases that the ground is deeply excavated, such as a foundation work in engineering works, boring of a petroleum well or a geothermal well, and so on. Hitherto, in the cases that the ground is excavated, drilling fluid prepared on the ground surface is continuously and cyclically injected into the excavating parts with a purpose to absorb frictional high heat generating during excavation, to transform excavation trash at a pit bottom toward the ground surface, to maintain drill pit wall, or to prevent collapse of a layer which is going to degradation. The drilling fluid is usually prepared in a muddy state with use of inorganic clayey substances such as bentonite, attapulgite, and sericite, with water, and also with drilling fluid additives to stabilize drilling fluid. As inorganic compounds among drilling fluid additives so far used, are cited condensed phosphates such as sodium tripolyphosphate and sodium hexametaphosphate; alkali-metal carbonates such as sodium carbonate and potassium carbonate; aluminates such as sodium aluminate and potassium aluminate. As organic compounds are cited humic acid salts, lignin sulfonic acid salts, carboxymethylcellolose ( CMC ), hydroxyethylcellulose ( HEC ), polyvinylalcohol ( PVA ), and phosphonic acids. However, there have been reported a lot of faults. Although, relatively speaking, the condensed phosphates have been highly evaluated, if their use is continued for a long period, they are spread over the ground and flow into sea or lake. Thus, they may cause generation of water-bloom or red tide, so that in recent years their use has been strictly limited. Although CMC has got a relatively favorable evaluation, there has been known a serious fault that drilling fluid used with it easily decomposes. Low effects are shown by alkali-metal carbonates, aluminates, humic acid salts, lignin sulfonic acid salts, HEC, PVA, and phosphonic acids. To solve the above-described problems for said additives hitherto used, there has been proposed an use of polyacrylic acids salts ) as drilling fluid additives in Japanese Official Patent Provisional Publications; showa 55-104383, 58-84883, 58-208376, 58-208377, 59-135280, 60-133085, and 62-199682. However, since the polyacrylic acids or salts are not satisfactorily in salt-resisting properties, in a case that water abundant in water hardness component or sea water is used as an aqueous medium to prepare drilling fluid, or in a case that plenty of underground water or sea water flows into drilling fluid in the underground working parts, viscosity of drilling fluid suffers damage and excavation becomes sometimes difficult because of resulting gelation. There has been proposed a method to remove said fault in the polyacrylic acids or salts. For example, in Japanese Official Patent Provisional Publications, showa 58-120683, 58-219289, 60-181187, 61-120881, and 62-267388, have been proposed drilling fluid additives composed of polyacrylic acids or salts in joint use with other components. These additives have been somewhat but insufficiently improved in salt-proof properties, but an use in relatively large amount is still needed, so that it is hard to say that a substantial fault in polyacrylic acids or salts has been removed. Also, there have been proposed an use of copolymers containing a sulfonic group in Japanese Official Patent Provisional Publications, showa 58-104981. 61-241382, and 62-215681. The copolymers containing a sulfonic group opened in these publications. when compared with polyacrylic acids or salts, have such advantages as that salt-resisting properties are somewhat improved, but the following problems are still involved. That is, although the copolymers containing a sulfonic group described in Japanese Official Patent Provisional Publication, showa 58-104981, have been formed among an α, β-ethylenic unsaturated carboxylic acid monomer, a monomer having a sulfonic group [ vinylsulfonic acid, ( meth ) allylsulfonic acid, styrenesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, and sulfoethyl methacrylate ] and a( meth )acryl acid ester monomer or an unsatulated nitrile monomer , all those still have faults that, if mixing percentage of sea water exceeds 50 % the effect much lowers. Although the copolymers containing a sulfonic acid described in Japanese Official Patent Provisional Publication, showa 61-241382, have been formed between a ( meth )acrylic acid monomer and a sulfoalkyl( meth )acrylate monomer, all those have a high polymerization degree, so that viscosity of drilling fluid becomes high. Although the copolymers containing a sulfonic group described in Japanese Official Patent Provisional Publication, showa 62-215681, have been formed among ( meth ) acrylamide a defined anionic vinyl monomer such as ( meth ) acrylic acid salts, 2-acrylamido-2-methylpropanesulfonic acid salts, and a defined water-soluble amphoteric vinyl monomer having a sulfonic group such as N-( 2-sulfoethyl)-N-acrylamidoethyl-N,N-dimethylammonium amphoteric monomer and N-( 3-sulfopropyl)-N-methacrylamidopropyl-N,N-dimethylammonium amphoteric monomer, all those cause lowering of the effect if mixing percentage of sea water exceeds 60 %. OBJECT OF THE INVENTION The present inventors undertook to solve the faults involved in hitherto known copolymers containing a sulfonic acid group, still taking above-described advantages in the copolymers containing a sulfonic group. This invention solves said problems involved in hitherto known drilling fluid additives which are added to stabilize drilling fluid used in a case that the ground is deeply excavated, such as a foundation work in engineering works or boring of petroleum well or geothermal well and so on. Thus, the object of this invention is to provide drilling fluid additives composed of copolymers which are obtainable by an industrially favorable process and superior in heat-resisting property. Furthermore, even though the additives are used in a relatively small amount, those sufficiently prevent change in properties of drilling fluid due to various kinds of hard water components being contained in underground water or cement as well as due to sea water, and the additives are able to display the properties of drilling fluid constantly regardless of presence or absence of salts. SUMMARY OF THE INVENTION The present invention relates to drilling fluid additives composed of water-soluble copolymer ( A ) having average molecular weight of 1,000 ∼ 50,000, which are led from monomer components composed of a monomer ( I ) of 40 ∼ 99.5 molar percentages in a series of unsaturated carboxylic acids, as shown in the following general formula ( I ), and an unsaturated monomer ( II ) of 0.5 ∼ 60 molar percentages in a series of ( meth )allylethers, as shown in the general formula ( II ). In the formula ( I ), each of A¹ and A² independently represents hydrogen, methyl, or -COOX², and A¹ and A² are not -COOX² at the same time. A³ represents hydrogen, methyl, or -CH²COOX³ and, in a case that A³ is -CH₂COOX³, each of A¹ and A² independently represents hydrogen or methyl. Each of X¹, X², and X³ independently or at the same time represents hydrogen, monovalent metal, divalent metal, ammonium, or organic amine. In the formula ( II ), R¹ represents hydrogen or methyl , and Z represents hydroxyl; a sulfonic acid group or its monovalent metal salt, divalent metal salt, ammonium salt, and organic amine salt; a phosphoric ( or phosphorous ) acid group or its monovalent metal salt, divalent metal salt, ammonium salt, and organic amine salt. As the monomers ( I ) in a series of unsaturated carboxylic acids in this invention shown as said general formula ( I ) are cited, for examples, acrylic acid, methacrylic acid, crotonic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, and partially or totally neutralized products of those acids with monovalent metal, divalent metal, ammonia, or organic amine. Here, sodium and potassium etc. are cited as monovalent metals. Calcium, magnesium, and zinc etc. are cited as divalent metals. As organic amines are cited alkylamines such as monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, and triethylamine; alkanolamines such as monoethanolamine, diethanolamine, triethanolamine, isopropanolamine, and dimethylethanolamine; and heteroaromatic amines such as pyridine. Among those monomers, ( meth ) acrylic acid and maleic acid or those products partially or totally neutralized with monovalent metals are preferred. As the unsaturated monomers ( II ) as shown as said general formula ( II ), are cited, for example, glycerol monoallyl ether, glycerol monomethallyl ether, 3-allyloxy-2-hydroxypropanesulfonic acid, 3-methallyloxy-2-hydroxypropanesulfonic acid, 3-allyloxy-2-hydroxypropanephosphoric acid, 3-methallyloxy-2-hydroxypropanephosphor ic acid, 3-allyloxy-2-hydroxypropanephosphorous acid, and 3-methallyloxy-2-hydroxypropanephosphorous acid or those products partially or totally neutralized with monovalent metals, divalent metals, ammonia, and organic amines. As monovalent metals are cited sodium and potassium etc., as divalent metals are cited calcium and magnesium, and zinc etc. As organic amines are cited alkylamines such as monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, and trimethylamine; alkanolamines such as monoethanolamine, diethanolamine, triethanolamine, isopropanolamine , and dimethylethanolamine, and heteroaromatic amines such as pyridine. Particularly, because of ecomomically cheap cost and industrially easy availability, at least one compound among glycerol monoallyl ether, 3-allyloxy-2-hydroxypropanesulfonic acid, and those products partially or totally neutralized with monovalent metals are very preferred. The water-soluble copolymer ( A ) used in the present invention is derived from a monomer component composed of 40 ∼ 99.5 molar percentages of said unsaturated carboxylic acid monomer ( I ) and 0.5 ∼ 60 molar percentages of said unsaturated monomer ( II ), where both percentages are against 100 molar percentages of a total amount of the monomers (I ) and ( II ), in a series of ( meth ) allyl ethers and its average molecular weight needs to be in a range of 1,000 ∼ 50,000. If either one of the composition of the monomer component or the average molecular weight is deviated from the above-defined range, can not be obtained the water-soluble copolymer ( A ) which is able to display superior properties as a drilling fluid additive . That is, if the composition of the monomer component and/or the average molecular weight of the water-soluble copolymer ( A ) is deviated from the above-described range, for example, when said copolymer ( A ) is added in small amount, the fluid preparation with underground water or sea water becomes difficult and, during excavation, unfavorable property change of drilling fluid due to an inflow of underground water, cement, and sea water can not be prevented. Besides, a problem may take place in heat-resistent properties. To obtain the water-soluble copolymer ( A ) used in the present invention, is polymerized, according to a known technology, a monomer component composed of the monomer in a series of unsaturated carboxylic acids ( I ) and the unsaturated monomer in a series of ( meth ) allyl ethers ( II ). For example, in a case of water solution polymerization, the polymerization reaction is carried out according to an usual method using as a polymerization catalyzer, for example, persulfates such as sodium persulfate and potassium persulfate etc.; hydrogen peroxide; and water-soluble azo compounds such as 2,2′-azobis-( 2-amidinopropane ) hydrochloride, and 4,4′-azobis-4-cyanovaleric acid etc. Furthermore, when polymerization is carried out in organic solvents of an alcohol series such as methanol and isopropanol etc., an ether series such as tetrahydrofuran and dioxane etc., an aromatics series such as benzene, toluene, and xylene etc., or a ketone series such as methylethyl ketone and methylisobutyl ketone etc., are used, according to an usual procedure, as polymerization catalyzers, for example, organic peroxides such as benzoyl peroxide, lauroyl peroxide, and peracetic acid etc.; oil-soluble azo compounds such as azobisisobutyronitrile and 2,2′-azobis-( 4-methoxy-2,4-dimethylvaleronitrile ) etc. Also, when a water-soluble copolymer ( A ) is wanted, it is possible to copolymerize, in a range of that an effect by this invention is not disturbed, any other monomer ( III ) which is copolymerizable with a monomer in a series of unsaturated carboxylic acids ( I ) and/or an unsaturated monomer in a series of ( meth allyl ether. As the other copolymerizable monomer ( III ), for example, are cited unsaturated monomers in an amide series such as ( meth ) acrylamide and N-t-butyl( meth )acrylamide etc.; hydrophobic unsaturated monomers such as ( meth )acrylates, styrene, 2-methylstyrene, and vinyl acetate etc.; unsaturated monomers in a sulfonic acid series such as vinyl sulfonic acid, allylsulfonic acid, methallylsulfonic acid, styrenesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, sulfoethyl ( meth )acrylate, sulfopropyl ( meth )acrylate, 2-hydroxysulfopropyl ( meth )acrylate, and sulfoethylmaleimide or their products partially or totally neutralized with monovalent metals, divalent metals, ammonia, and organic amines, but the monomer ( II ) is excepted; unsaturated monomers containing hydroxy group such as 2-hydroxyethyl( meth ) acrylate, polyethyleneglycol mono( meth )acrylate, polypropyleneglycol mono( meth )acrylate, allyl alcohol, polyethyleneglycol monoallyl ether, polypropyleneglycol monoallyl ether, 3-methyl-3-butene-1-ol ( isoprenol ), polyethyleneglycol monoisoprenol ether, polypropyleneglycol monoisoprenol ether, 3-methyl-2-buten-1-ol ( prenol ), polyethyleneglycol monoprenol ether, polypropyleneglycol monoprenol ether, 2-methyl-3-buten-2-ol ( isoprenealcohol ), polyethyleneglycol monoisoprenealcohol ether, polypropyleneglycol monoisoprenealcohol ether, α-hydroxyacrylic acid, N-methylol( meth )acrylamide, glycerol mono( meth )acrylate, vinylalcohol etc.; cationic unsaturated monomers such as dimethylaminoethyl ( meth )acrylate, and dimethylaminopropyl ( meth )acrylamide etc.; unsaturated monomers in a nitrile series such as ( meth )acrylonitrile etc.; unsaturated monomers containing phosphorus ( but the monomer ( II ) is excepted ) such as ( meth )acrylamidomethanephosphonic acid, methyl ( meth acrylamidomethanephosphonate, 2-( meth )acrylamido-2-methylpropanephos phonic acid etc.; monomers in an α-olefinic series such as ethylene, propylene, 1-butene, isobutylene, α-amylene, 2-methyl-1-butene, 3-methyl-1-butene ( α-isoamylene ), 1-hexene, and 1-heptene etc. In a case that these monomers ( III ) is used, it is preferred to use less than 30 moles % of the total monomers to fully display the feature in this invention. The water-soluble copolymers ( A ) thus obtained are used as drilling fluid additives by themselves or in combination with auxiliary additives ( B ) such as condensed phosphates, alkali-metal carbonates, aluminates, humic acid salts, ligninsulfonic acid salts, CMC, HEC, PVA, and phosphonic acids etc. If, among these auxiliary additives ( B ), aluminates and CMC are used in combination with the copolymer ( A ), there is an advantage that the heat-resisting properties futher increase. In the combination use with auxiliary additives ( B ), it is preferred to adjust the auxiliary additives ( B ) in a ratio of 5∼ 500 weight parts against 100 weight parts of water-soluble copolymer ( A ). If the ratio exceeds the upper limit, the heat-resisting properties may lower contrary. Drilling fluid are prepared by using drilling fluid additives of this invention with an inorganic clayey substances and an aqueous medium. Although proportion for use of these three is not especially limited, for example, it is preferred to adjust the inorganic clayey substances in 1 ∼ 10 weight parts and the drilling fluid additives in 0.1 ∼ 2 weight parts against 100 weight parts of an aqueous medium. If deviated from these ranges, the drilling fluid may become inferior in stability for a long period. The proportion for use of the present drilling fluid additives became small, compared with a necessary amount, such as 0.3 ∼ 5 weight parts for previous additives. As said inorganic clayey substances, are used bentonite, attapulgite, sericite, etc., among which bentonite is especially preferred because the drilling fluid additives of this invention displays a great effect with it. Since the drilling fluid additives in this invention are composed of said water-soluble copolymers ( A ), drilling fluid prepared with the additives has superior salt-resisting properties and, regardless of presence or absence of salts, exhibits stable physical properties. Thus, for example, in a case of drilling fluid preparation, as an aqueous medium can be used not only deionized water but also water containing relatively high content of hard water component such as underground water and industrial water, and water containg high content of inorganic salts, compared to the deionized water, such as sea water, river water, mineral spring water, hot spring water and the like. Also, during excavation, even if underground water, cement, sea water, and so on come into contact or are mixed, the drilling fluids do not cause gelation or show no tendency to increase viscosity or show only slightly. Besides, because dehydration amount does not very increase, it results in formation of a superior mud wall. Also, the drilling fluid additives in this invention, compared with hitherto known drilling fluid additives composed of copolymers containing a sulfonic group, are superior in heat-resisting properties, so that they can be used for a long time at high temperature. Furthermore, the additives display superior effects even in small amount of addition, or the water-soluble copolymers ( A ) used in the present invention may be obtained with an economically cheap cost, compared with the previous copolymers, so that the excavation cost can be greatly reduced, and the industrial value for use is very high. Why the drilling fluid additives in this invention, as described above, display superior effects even in small amount of addition and does not easily suffer bad effects due to underground water, cement, sea water, and so on is not yet clear, but may be deduced as follows. That is, it is considered that the hydroxy group in the unsaturated monomer ( II ) in the ( meth )allyl ether series reveals a significant additional effects with the anionic group in the monomer ( I ) in the unsaturated carbonic acid series and, thus, contributs for salt-resisting properties. However, due to this reason alone, the present invention is not entirely limited. DETAILED DESCRIPTION OF THE INVENTION Hereinafter, the present invention is illustrated with examples referring to examples for preparation of water-soluble copolymers, but the invention is not limited within these examples. Unless otherwise explained, the word part all represents weight part and % all represents weight % . Preparation example 1 of water-soluble copolymers Into a 1 liter volume glass-made round bottom flask equipped with thermometer and a reflux condenser was placed 175 parts of deionized water and warmed up to 95°C. With stirring, each of 371.9 parts of a 37 % aqueous sodium acrylate solution, 18.7 parts of a 80 % aqueous acrylic acid solution, 363.9 parts of a 25 % aqueous sodium 3-allyloxy-2-hydroxypropanesulfonate solution, 43.1 parts of a 15 % aqueous sodium persulfate solution, and 41.7 parts of a 5 % aqueous hydrogen peroxide solution were separately and dropwise added through a dropping nozzle during 2 hours. Temperature was controlled at 95 °C during polymerization. After the dropping finished, the reaction mixture was maintained at the temperature for 30 minutes to complete polymerization and cooled. Then, the mixture was completely neutralized adjusting at pH 10 by using a 48 % aqueous sodium hydroxide solution. The obtained water-soluble copolymer ( A ), sodium salt of a copolymer between acrylic acid and 3-allyloxy-2-hydroxypropanesulfonic acid in a molar ratio of 80 to 20 ( water-soluble copolymer ( 1 ) ) showed 4,000 for average molecular weight as listed in Table 1. Preparation examples 2 ∼ 18 of water-soluble copolymers and preparation reference examples 1 ∼ 18 of water-soluble polymers for comparison According to monomer compositions as shown in Tables 1 and 2 and the method in preparation example 1 of water-soluble copolymers, were obtained water-soluble copolymers ( 2 )∼ ( 18 ) and water-soluble polymers for comparison ( 1 ) ∼ ( 18 ). Preparation example 19 The water-soluble copolymer was treated with electrodialysis to transform it into an acid form and then, completely neutralyzed to pH 10 by using an aqueous potassium hydroxide solution yielding a water-soluble copolymer ( 19 ). Average molecular weight of this polymer is shown in Table 1. For these polymers, kinds, average molecular weights, and amounts of residual monomers are shown in Table 1 and Table 2. Example 1 In a tunk being made from stainless steel of austenite series ( SUS304 by JIS ) and having 90 mm⊘ of an inner diameter and 160 mm of height were placed 100 parts of deionized water, 6 parts of bentonite, and 0.2 parts of the water-soluble copolymer ( 1 ) which is the water-soluble copolymer ( A ) obtained as a drilling fluid additive from preparation example 1 of water-soluble copolymers, and the mixture was stirred for 15 minutes at 2000 rpm using a dissolver blades ( blade diameter, 40 mm⊘ ) to obtain a drilling fluid composition ( 1 ). For the obtained drilling fluid composition ( 1 ), Funnel viscosity ( FV ), gel strength after 10 minutes ( 10 Gel ), and dehydration amount were determined and the results were listed as fundamental properties in Table 3. Funnel viscosity was measured with a 500 cc Funnel viscosimeter ( unit, second ). The gel strength after 10 minutes was measured with a fan VG meter ( unit, pascal ). The dehydration amount was determined by a filtrate amount which is obtained after treatment for 30 minutes at pressure of 3 kg per square cm by using a API standard filter ( unit, ml ). For said drilling fluid composition ( 1 ), the cement-resisting examination, sea water-resisting examination, and heat-resisting examination below-described were carried out. As the results obtained from all these examinations show so small change from the fundamental properties, the drilling fluid composition shows excellent salt-resisting and heat-resisting properties and is superior as drilling fluid. Examination for cement-resisting properties 106.2 parts of said drilling fluid composition ( 1 ) was mixed with 5 parts of cement and stood for 1 day, for which Funnel viscosity ( FV ),gel strength after 10 minutes ( 10 Gel ), and dehydration amount were measured and results shown in Table 3. Examination for sea water-resisting properties 106.2 parts of said drilling fluid composition ( 1 ) was mixed with 4 parts of Aquamarine 5 ( a product of Yashima Pharmaceutical Co. made by 25 times concentration of artificial sea water ) and the mixture was stood for 1 day and then, it was measured for Funnel viscosity ( FV ), gel strength after 10 minutes ( 10 Gel ) , and dehydration amount. Results are shown in Table 3. Examination for heat-resisting properties 106.2 parts of said drilling fluid composition 1 was mixed with 2 parts of Aquamarine S ( a product of Yashima Pharmaceutical Co. made by 25 times concentration of artificial sea water ) and the mixture was subjected to curing for 20 hours at 260°C and then, it was measured for Funnel viscosity ( FV ) gel strength after 10 minutes ( 10 Gel ), and dehydration amount. Results are shown in Table 3. Examples 2 ∼ 18 Except that the water-soluble copolymers ( 2 ) ∼ ( 18 ), which are water-soluble copolymers ( A ) obtained from preparation examples 2 ∼ 18 of water-soluble copolymers, were used as drilling fluid additives, a drilling fluid composition was obtained in the same way as for example 1 and its fundamental properties, cement-resisting properties, sea water-resisting properties, and heat-resisting properties was evaluated. Results are shown in Table 3. Example 19 ∼ 21 Except that carboxymethylcellulose was together with the water-soluble copolymer ( A ) used as a drilling fluid additive in the amount indicated in Table 3, the same procedure as used for example 1 was carried out to obtain a drilling fluid composition, of which fundamental properties, cement-resisting properties, sea water-resisting properties, and heat-resisting properties were evaluated. Results are shown in Table 3. Example 22 ∼ 24 Except that sodium aluminate ( NaAlO₂ ) was used in the amount indicated in Table 3 instead of 0.1 part of carboxymethylcellulose, the same procedure as used for example 19 was carried out to obtain a drilling fluid composition, of which fundamental properties, cement-resisting properties, sea water-resisting properties, and heat-resisting properties were evaluated. Results are shown in Table 3. Example 25 Except that 0.1 part of potassium aluminate was jointly used as a drilling fluid additive, the procedure same as used for example 2 gave a drilling fluid composition, of which fundamental, cement-resisting, sea-water resisting, and heat-resisting properties were evaluated. Results are shown in Table 3. Example 26 Except that 0.1 part of carboxymethylcellulose was jointly used as a drilling fluid additive, the procedure same as used for example 4 gave a drilling fluid composition, of which fundamental, cement-resisting, sea water-resisting, and heat-resisting properties were evaluated. Results are shown in Table 3. Example 27 Except that the water-soluble copolymer ( 19 ) was used as a drilling fluid additive, the procedure same as used for example 1 gave a drilling fluid composition, of which fundamental, cement-resisting, sea water-resisting, and heat-resisting properties were evaluated. Results are show in Table 3. Comparison Examples 1∼ 17 Except that water-soluble polymers for comparison ( 1 ) ∼ ( 17 ) obtained from reference examples 1∼ 17 were used as drilling fluid additives, the same procedure as used for example 1 was carried out to obtain a drilling fluid composition, of which fundamental properties, cement-resisting properties, sea water-resisting properties, and heat-resisting properties were evaluated. Results are shown in Table 4. Comparison example 18 Except that as a drilling fluid additive 0.2 parts of sodium aluminate was used in combination with the water-soluble polymer for comparison ( 7 ), the same procedure as used for comparison example 7 was carried out to obtain a drilling fluid composition, of which fundamental properties, cement-resisting properties, sea water-resisting properties, and heat-resisting properties were evaluated. Results are shown in Table 4. Comparison example 19 Except that carboxymethylcellulose was only used as a drilling fluid additive, the same procedure as used for example 1 was carried out to obtain a drilling fluid composition, of which fundamental properties, cement-resisting properties, sea water-resisting properties, and heat-resisting properties were evaluated. Results are shown in Table 4. Comparison example 20 Except that none of drilling fluid additive was used, the same procedure as used for example 1 was carried out to obtain a drilling fluid composition, of which fundamental, cement-resisting, sea water-resisting, and heat-resisting properties were evaluated. Results are shown in Table 4. Comparison example 21 Except that 0.2 parts of sodium aluminate and the water-soluble polymer for comparison ( 17 ) were jointly used as a drilling fluid aditive, the procedure same as used for comparison example 17 was carried out to obtain a drilling fluid composition, of which fundamental, cement-resisting, sea water-resisting, and heat-resisting properties were evaluated. Results are shown in Table 4. Comparison example 22 Except that 0.2 parts of carboxymethylcellulose and the water-soluble polymer for comparison ( 17 ) were jointly used as a drilling fluid additive, the procedure same as used for comparison example 17 was carried out to obtain a drilling fluid composition, of which fundamental, cement-resisting, sea water-resisting, and heat-resisting properties were evaluated. Resulta are shown in Table 4. Comparison example 23 Except that the water-soluble polymer for comparison ( 18 ) obtained from reference example 18 was used as a drilling fluid additive, the procedure same as used for example 1 gave a drilling fluid composition, of which fundamental, cement-resisting, sea water-resisting, and heat-resisting properties were evaluated. Results are shown in Table 4. The water-soluble copolymers ( A ) in the present invention, as shown in Tables 1 ∼ 4, in comparison with the drilling fluid additives hitherto used, are superior in cement-, sea water-, and heat-resisting properties even in an use of small amounts, so that they are of high value for industrial use. Also, there is a secondary excellent feature which, because the residual monomer from the water-soluble copolymer ( A ) is only small in amount, enviromental pollution needs not to be afraid. Furthermore, by that the water-soluble copolymer ( A ) and carboxymethylcellulose and/or an aluminate are jointly used in a specially defined proportion, a more favorable drilling fluid additive can be obtained compared with a single use of a water-soluble copolymer ( A ).

Claims: Drilling fluid additives composed of water-soluble copolymer A , which has average molecular weight of 1,000 ∼ 50,000 and are led from monomer components composed of 40 ∼ 99.5 mole % of a monomer in an unsaturated carboxylic acid series ( I ), as shown by the following first general structure formula (I), and 0.5 ∼ 60 mole % of an unsaturated monomer in an ( meth ) allyl ether series ( II ), as shown by the following second general structure formula ( II ). In the formula ( I ), each of A¹ and A² independently represents hydrogen, methyl, or -COOX², and A¹ and A² are not -COOX² at the same time. A³ represents hydrogen, methyl, or -CH₂COOX³ and, in a case that A³ is -CH₂C00X³, each of A¹ and A² independently represents hydrogen or methyl. Each of X¹, X², and X³ independently or at the same time represents hydrogen, monovalent metal, divalent metal, ammonium, or organic amine. In the formula ( II ), R¹ represents hydrogen or methyl, and Z represents hydroxyl; a sulfonic acid group or its monovalent metal salt, divalent metal salt, ammonium salt, and organic amine salt; a phosphoric ( or phosphorous ) acid group or its monovalent metal salt, divalent metal salt, ammonium salt, and organic amine salt. Drilling fluid additives as claimed in claim 1, wherein the monomer ( I ) in an unsaturated carboxylic acid series are ( meth ) acrylic acid ( or salts ) and/or maleic acid ( or salts ). Drilling fluid additives as claimed in claim 1 or 2, wherein the unsatulated monomer (II ) in an ( meth )allyl ether series are glycerol monoallyl ether and/or 3-allyloxy-2-hydroxypropanesulfonic acid ( or salts ). Drilling fluid additives as claimed in either one of claims 1 ∼ 3 which are composed of composition of the water-soluble copolymer ( A ) with carboxymethylcellulose and/or aluminates. Drilling fluid additives as claimed in claim 4, wherein the weight proportion of carboxymethylcellulose and/or aluminates are 5 ∼ 500 parts against 100 parts of the water-soluble copolymers ( A ). Use of drilling fluid additives as claimed in either one of claims 1 ∼ 5 in drilling fluids comprising bentonite fluid.

Inventors: FUJIWARA TERUAKI, IRIE YOSHIO, SHIOJI SHORBU, FUJIWARA, TERUAKI, IRIE, YOSHIO, SHIOJI, SHORBU
Applicants: NIPPON CATALYTIC CHEM IND, NIPPON SHOKUBAI CO., LTD.
Application year: 1989
Main classification: C09K7
IPC codes: C08F220, E21B21, C09K8