NON-AQUEOUS PROCESS FOR THE PREPARATION OF ALUMOXANES

Abstract: A process for the preparation of hydrocarbylalumoxanes comprising oligomeric, linear and/or cyclic hydrocarbyl­ alumoxanes which comprise contacting a hydrocarbylaluminum dissolved in an inert dry organic liquid with a trihydro­ carbylboroxine. Preferably, the trihydrocarbylboroxine is prepared by the reaction of boron oxide with an trihydrocarbylborane.

Description: Field of the Invention : The present invention relates to the non-aqueous preparation of alumoxanes, preferably trimethylalumoxane. The invention particularly relates to the use of trialkylboroxine in the preparation of alumoxanes. Background of the Invention : Alumoxanes are the products of partial hydrolysis of hydrocarbylaluminum compounds and have been found useful in a variety of chemical reactions, including catalyst components for polymerization catalysts and especially as a component for catalysts in the preparation of high-activity, homogenous Ziegler catalysts, as is described, for example, in U.S. Patent Application No. 501,740, filed June 6, 1983. Various processes are known for the preparation of alumoxanes, the simplest being to add water in predetermined amounts and under controlled conditions to a hydrocarbylaluminum compound as described in U.S. Patent No. 3,242,099. Alumoxanes can also be obtained, for example, by the action of water vapor on a benzene solution of a trialkylaluminum (J. Am. Chem. Soc., 90 , 3173 [1968]) by using lithium dialkylaluminates as the organoaluminum starting compound (J. Am. Chem. Soc., 89 , 173 [1967]). Other known methods for preparing alumoxanes include oxidizing aluminum-hydrocarbon compounds with lead dioxide (J. Organomet. Chem., 43 , 81 [1972]), treating an alkylaluminum with alkyldistannoxanes [(R₃Sn)₂0] in place of water (Racanelli, P. and Porri, L., Europ. Polym. J., 6 , 751 [1970]) and hydrolyzing alkylaluminums with copper sulfate containing water of crystallization as suggested in European Patent Application No. 0035242. In Australian Patent No. 20861/83, Kaminsky, et al. discloses a method of preparing alumoxanes by contacting aluminum salts containing water of crystallization with a trialkylaluminum. It is taught that the alumoxanes are obtained in higher yields and greater purity. In many of these processes, because of the highly exothermic nature of the reaction between the water and the hydrocarbylaluminum, the reaction can easily get out of control or even become explosive. While the use of CuSO₄·5H₂O as a source of water provides for the slow addition of water, thus reducing the risk of local excesses of water and thereby reducing the probability of a runaway or explosive reaction, the method suffers from some drawbacks. For example, the Cu(II) may be reduced to Cu(I) or even to metallic copper during the reaction with an alkylaluminum, such as trimethylaluminum. This can lead to the introduction of sulfate groups and other undesirable types of functionalities, as well as copper, into the alumoxane preparation. The alumoxane product, therefore, prior to use as a component of a catalyst system in a polymerization process, must be filtered, purified and recrystallized, since otherwise adverse conditions will exist during the polymerization, and the quality and quantity of the polymer will be adversely affected. Another disadvantage associated with CuSO₄·5H₂O in preparation of alumoxane is the low yield which is on the order of about 30% relative to the aluminum trialkyl employed. Some of these problems can be essentially eliminated, if one employs hydrated salts as the source of water in the preparation of alumoxanes, such as methyl alumoxane wherein the metal component is not reduced during the alumoxane preparation. Such a solution is disclosed in U.S. Patent No. 4,665,208, issued to Welborn on May 12, 1987. The disadvantage associated with using hydrated salts is that the heterogeneous solution of trialylaluminum, hydrated salt and hydrocarbon still has the potential for a violent reaction during the formation of the alkylalumoxane even though the danger is greatly reduced. Consequently, there is still a need for a process which can safely and efficiently produce hydrocarbylalumoxanes. Attempts to react boron oxide with trialkylaluminum without the intermediate step of producing trihydrocarbylboroxine have been unsuccessful. However, the reaction of boron oxide with trialkylboron to yield trialkylboroxine is disclosed in "The Reaction of Triorganoboranes with Boric Acid" by G. F. Hennion, et al., Journal of American Chemical Society , vol. 79, p. 5194 (1957). This reaction proceeds according to the following stoichiometry: B₂O₃ + R₃B → (RBO)₃ trialkylboroxine It has also been disclosed in "New Synthesis of Trialkylboranes," by G. C. Ashby, Journal of American Chemical Society , vol. 81, p. 4791 (1959), that trialkylboroxine produced in the above reaction can be reacted with trialkylaluminum to yield alumina and trialkylborane according to the following stoichiometry: (RBO)₃ + 2R₃Al → 3R₃B + Al₂O₃ In a similar reaction scheme published by J. G. Ruff entitled "A New Preparation of Some Dimethylalumino Derivations of Boron," Journal of Organic Chemistry , vol. 27, p. 1020 (1962), alkylboroxine was reacted with trisdimethylaminoalane to yield a byproduct generally identified as [(CH₃)₂NAlO⁻] x . The stoichiometry of this reaction was discribed as follows: 2(RBO)₃ + 3Al[N(CH₃)₂]₃ → RB[N(CH₃)₂]₃ + 3/X[(CH₃)₂NAlO⁻] x However, none of these references mention that an alkylalumoxane can be safely and efficiently produced from trihydrocarbylboroxine and trialkylaluminum. Summary of the Invention: The alumoxanes which are prepared in accordance with this invention are oligomeric, linear and/or cyclic hydrocarbylalumoxanes represented by the formulae: (I) for oligomeric, linear alumoxanes and (II) for oligomeric, cyclic alumoxanes, wherein "n" is 1-40, preferably 10-20, "m" is 3-40, preferably 3-20, and R is a C₁-C₈ alkyl group and preferably methyl. It is generally known that the alumoxanes will show maximum activity when "m" and "n" are greater than 10 and R is methyl. In the preferred embodiment, the general procedure in accordance with this invention is to first form the hydrocarbon soluble liquid trihydrocarbylboroxine, (RBO)₃. This can be accomplished by combining boron oxide with trihydrocarbylborane according to the following stoichiometry: (III) B₂O₃ + R′₃B → (R′BO)₃ wherein R′ can be a C₁-C₁₀ alkyl group or a C₆-C₁₀ aryl group, desirably a C₁-C₃ alkyl group and preferably R′ is methyl or ethyl. Next, trihydrocarbylboroxine is combined with trialkylaluminum to form an alkylalumoxane and trihydrocarbylborane according to the following stoichiometry: (IV) (R′BO)₃ + 3R₃Al → 3(RAlO) n + 3R′₃B wherein R is defined as above. R′ and R can be the same or different, most preferably R′ and R are the same. If R′ and R are different, a mixture of alumoxanes containing both R and R′ can be produced. Since trihydrocarbylboroxine is soluble in the hydrocarbon solution, it permits a homogeneous reaction to occur with the trialkylaluminum, resulting in better control of the reaction stoichiometry and product properties, e.g., degree of oligomerization. Illustrative of the hydrocarbylboroxines which can be employed are trimethylboroxine, triethylboroxine, tri-n-butylboroxine, triphenylboroxine, and unsymmetrical boroxines such as dimethylethylboroxine and the like. Detailed Description of the Invention : The present invention is directed toward a method for preparing alumoxanes, preferably methylalumoxanes, useful as one of the components in the active catalyst complex for the polymerization of olefins and particularly ethylene to high molecular weight polyethylenes, such as Linear Low Density Polyethylene (LLDPE) and High Density Polyethylene (HDPE). The polymers are intended for fabrication into articles by extrusion, injection molding, thermal forming, rotational molding and the like. In particular, the polymer prepared with the catalyst complex are homopolymers of ethylene and copolymers of ethylene with higher α-olefins having from 3 to about 10 carbon atoms and preferably 4 to 8 carbon atoms. Illustrative of the higher α-olefins are butene-1, hexene-1 and octene-1. Illustrative of the alkylaluminum compounds which can be employed are trimethylaluminum, triethylaluminum, dimethylaluminum chloride, and diethylaluminum chloride, and the like. Trimethylaluminum is preferred. The active catalyst complex useful in polymerization comprises a metallocene and an alumoxane which can be adsorbed onto the surface of a support material. Alumoxanes are oligomeric aluminum compounds represented by the general formula: (R-Al-O) m , which is believed to be a cyclic compound and R(R-Al-O-) n AlR₂, which is a linear compound. In the general formula, "R" is a C₁-C₁₀ alkyl group, such as methyl, ethyl, propyl, butyl, isobutyl and pentyl, and "n" is an integer from 1 to about 40 and "m" is an integer from 3 to 40, and they represent the degree of oligomerization of the alumoxane. Preferably, "R" is methyl, and "n" is 10-20, and "m" is 3-20. Generally, in the preparation of alumoxanes from the reaction of trimethylaluminum and water, a mixture of linear and cyclic compounds is obtained. Generally, an alumoxane having a higher degree of oligomerization will, for a given metallocene, produce a catalyst complex of higher activity than will an alumoxane having a lower degree of oligomerization. The procedure by which alumoxane is produced will affect the degree of oligomerization of the alumoxane. The metallocene useful as the other component of the catalyst complex may be any of the organometallic coordination compounds obtained as a cyclopentadienyl derivative of a transition metal. Metallocenes which are useful for preparing an active catalytic complex are the mono-, bi- and tri-cyclopentadienyl or substituted cyclopentadienyl metal compounds and most preferably, bi-cyclopentadienyl compounds. Of the metallocenes, zirconocenes and titanocenes are most preferred. A person skilled in the art can readily determine the appropriate metallocene and the relative mole ratios needed to make an effective active catalyst. Heretofore, the alumoxane component of the active catalyst complex has been prepared by contacting water in the form of a moist solvent with a solution of alkylaluminum in a suitable organic solvent such as benzene, toluene or an aliphatic hydrocarbon. As noted earlier, this procedure is susceptible to fire and explosion hazards which require the use of explosion-proof equipment and carefully controlled reaction conditions. In an alternative method, heretofore employed for the separate production of alumoxane, an alkylaluminum is contacted with a hydrated salt, such as hydrated copper sulfate. The method comprises treating a dilute solution of alkylaluminum in toluene with a copper sulfate pentahydrate. A slow, controlled hydrolysis of the alkylaluminum to alumoxane results which substantially eliminates the fire and explosion hazard, but with a disadvantage of the creation of hazardous waste products that must be disposed of and from which the alumoxane must be separated before it is suitable for use in the production of an active catalyst complex. In accordance with the preferred embodiment of the present invention, the alumoxane complex is prepared by reacting boron oxide with trihydrocarbylborane to form trihydrocarbylboroxine. Next, trihydrocarbylboroxine is combined with trialkylaluminum to form an alkylalumoxane and trihydrocarbylborane. By first forming the hydrocarbon soluble liquid trihydrocarbylboroxine, a homogeneous reaction can occur with the trialkylaluminum resulting in better control of the reaction stoichiometry and product properties, such as the degree of oligomerization. Since the reaction takes place in a homogeneous solution, there is less potential for the reaction to proceed violently, unlike heterogeneous mixtures of water, trimethylaluminum and hydrocarbon or mixtures of hydrated salt, trimethylaluminum and hydrocarbon. A further advantage is that a gaseous product, such as methane gas, is not produced during reaction. Therefore, there is no need for constant venting which has the potential for over-pressurization and loss of reactants through venting. In addition, the boroxine is readily produced using the inexpensive and readily available compound boron oxide, B₂O₃, a boric acid derivative. The reaction of the boroxine and alkylaluminum produces more borane than it used in the production of the boroxine and all by-product borane compounds can by hydrolyzed with water to produce harmless boric acid which can be readily disposed of, converted to boron oxide or recovered by, for example, distillation. The ratio by volume between the inert solvent and the hydrocarbylaluminum employed should be from about 4:1 to about 25:1 or greater, and preferably about 8:1. The molar ratio of boron oxide to hydrocarbylborane can be from about 2:1 to about 1:2, and preferably about 1:1 to produce hydrocarbylboroxine. The molar ratio of trihydrocarbylboroxine to hydrocarbylaluminum should be from about 1:3 to about 1:5, and preferably about 1:3.3. These ratios may not only depend on the stoichiometry of the chemical reaction but also upon factors which influence the equilibrium of the reaction, such as temperature. Generally, the temperature of the reactions should be between about 10°C to about 80°C. Completion of the reaction between the boron oxide and the hydrocarbylborane is indicated by the cessation of hydrocarbylboroxine production. Generally, the reaction time will be between about 2 and about 72 hours, depending on the temperature of the reaction. The reaction time between hydrocarbylboroxine and hydrocarbylaluminum can be between about 0.1 and about 24 hours. Usually the reaction time will be between 0.5 hours and about 4 hours. It is preferred that the hydrocarbylboroxine be added to the hydrocarbylaluminum. It is believed that this order of mixing forces the hydrocarbylaluminum to undergo reaction in the context of a transient localized excess of hydrocarbylaluminum compared to a transient localized deficiency of the boroxine. In order to obtain a product of desirable properties, the rate of addition of boroxine to hydrocarbylaluminum should not exceed about 0.2 moles per minute per liter of reaction medium. The solvents employed in dissolving the hydrocarbylaluminum can be any of the known inert organic solvents, preferably aliphatic or aromatic solvents, such as toluene, benzene, hexane, heptane, isooctane, cyclohexane, methylcyclohexane, decane, and the like, and preferably the same solvent is employed for dissolving the alkylaluminum and the boroxine. Toluene and heptane are preferred solvents. While the invention is described in connection with the specific examples below, it is understood that these are only for illustrative purposes. Many alternative, modifications and variations will be apparent to those skilled in the art in light of the below examples and such alternative, modifications and variations fall within the general scope of the claims. EXAMPLES Example 1 -- Preparation of Triethylboroxine A 500 cc round bottom flask was equipped with a water cooled reflux condenser, an electrically heated mantle, and a nitrogen bubbler to maintain an inert atmosphere. To the flask under nitrogen was added 70.0 g of B₂O₃ (Aldrich Gold Label) which has been ground to a powder in a mortar under dry nitrogen. Neat triethylborane (100.0 g) was added to the boron oxide all at one time and the reaction flask was set up for refluxing. Reflux was continued for 5 days at which point the reflux condenser was changed for a distillation condenser and the liquid was distilled in two fractions. The second fraction yielded 60 cc of a colorless liquid which distilled at 148°C. The H-1 and B-11 nmr of the second fraction indicated that it was pure triethylboroxine. Example 2 -- Preparation of Methylalumoxane A 100 cc round bottom flask was equipped for magnetic stirring in an inert, dry nitrogen atmosphere. Neat trimethylaluminum (2.37 g, 0.033 moles) was weighed into the flask followed by 43 g of distilled toluene. Into another flask was weighed 1.68 g of neat triethylboroxine (0.010 moles), followed by 43 g of distilled toluene. With stirring, the triethylboroxine solution was added to the trimethylaluminum solution in 5-10 cc increments separated by 5 minute intervals. The solution remained clear and colorless during and after the additions. The solution was capped and stored under nitrogen. Example 3 -- Preparation of Methylalumoxane A 100 cc round bottom flask was equipped for magnetic stirring in an inert, dry nitrogen atmosphere. Neat triethylboroxine (1.68 g, 0.033 moles) was weighed into the flask and 43 g of distilled toluene was added. Into another flask was weighed 2.37 g of triethylaluminum, followed by 43 g of distilled toluene. With stirring, the trimethylaluminum solution was added to the triethylboroxine solution in 5-10 cc increments separated by 5 minute intervals. The solution became cloudy after the first addition and a gelatinous solid separated from the solution. The solution containing the precipitated solid was capped and stored under nitrogen. Example 4 -- Polymerization Using Methylalumoxane A 1-liter Zipperclave stainless steel reactor vessel equipped with an inclined blade stirrer, an external jacket for temperature control, a septum inlet and vent line, and a regulated supply of dry ethylene and nitrogen, was cleaned with boiling toluene and dried and deoxygenated with a nitrogen flow. The reactor temperature was adjusted to 80°C, and 400 cc of distilled toluene was added. Two milliliters of the final solution from Example 2 was injected by syringe, and the mixture was stirred at 0 psig under nitrogen. A toluene solution (0.10 cc) containing 0.10 mg of dissolved bis(n-butylcyclopentadienyl)zirconium dichloride was injected. Immediately 90 psig of ethylene was admitted and the reactor was stirred and a maintained at 80°C for 5 minutes at a constant pressure of 90 psig. The product was recovered by rapidly venting, cooling, and opening the reactor. Residual toluene was evaporated in a stream of air, and the yield was weighed. The product was determined to be 10.0 g of polyethylene by infrared and gel permeation chromatography. The catalyst activity was calculated to be 885,000 grams polymer per gram zirconium-hour-bar. Example 5 -- Polymerization Using Methylalumoxane A 1-liter Zipperclave stainless steel reactor vessel equipped with an inclined blade stirrer, an external jacket for temperature control, a septum inlet and vent line, and a regulated supply of dry ethylene and nitrogen, was cleaned with boiling toluene and dried and deoxygenated with a nitrogen flow. The reactor temperature was adjusted to 80°C, and 400 cc of distilled toluene was added. Two milliliters of the final solution and precipitate from Example 3 was injected by syringe, and the mixture was stirred at 0 psig under nitrogen. A toluene solution (0.10 cc) containing 0.10 mg of dissolved bis(n-butylcyclopentadienyl)zirconium dichloride was injected. Immediately 90 psig of ethylene was admitted and the reactor was stirred and maintained at 80°C for 5 minutes at a constant pressure of 90 psig. The product was recovered by rapidly venting, cooling, and opening the reactor. Residual toluene was evaporated in a stream of air, and the yield was weighed. The product was determined to be 1.0 g of polyethylene by infrared and gel permeation chromatography. The catalyst activity was calculated to be 44,200 grams polymer per gram zirconium-hour-bar.

Claims: A process for the preparation of a mixture of linear and cyclic hydrocarbylalumoxanes, respectively represented by the formula (R-Al-O) m and R(R-Al-O) n AlR₂ wherein R is a C₁-C₁₀ alkyl group, n is an integer in the range of from 1-40 and m is an integer in the range of 3-40, which comprises adding a hydrocarbon solution containing trihydrocarbylboroxine to a hydrocarbon solution containing hydrocarbylaluminum at a molar ratio of boroxine to aluminum compound in the range of from about 1:3 to about 1:5. The process of claim 1, wherein the hydrocarbylaluminum is trialkylaluminum and the trihydrocarbylboroxine is trimethylboroxine or triethylboroxine. The process of claim 2, wherein the trialkylaluminum is trimethylaluminum. The process of claim 1, wherein the hydrocarbon solution is selected from the group consisting of toluene, hexane, and heptane. The process of claim 1, wherein the rate of addition of boroxine to hydrocarbylaluminum is about 0.2 moles or less per minute per liter of reaction medium. The process of claim 1, wherein n is in the range of from 10-20 and m is in the range of from 3-20.

Inventors: WELBORN, HOWARD CURTIS
Applicants: EXXON CHEMICAL PATENTS INC.
Application year: 1989
Main classification: C07F5
IPC codes: C07F5, C08F10, C08F4, C08G79