Straight oil composition for fibrous material

Abstract: Straight oil compositions for fibrous materials, which provide excellent smoothness and antistatic properties and also have excellent separation resistance, even without compatibilizers, comprise (A) 100 parts by weight of dimethyl polysiloxane having a viscosity of from 3 to 30 cSt at 25°C and (B) 0.5 to 50 parts by weight of a polyoxyalkylene group- terminated organopolysiloxane. The polyoxyalkylene groups of Component (B) have a block structure of polyoxypropylene and polyoxyethylene units, with the former being bonded to the siloxane moiety. Component (A) is preferably a trimethylsiloxy-terminated polydimethylsiloxane.

Description: The present invention concerns straight oil compositions for fibrous materials. Conventionally, for excellence in heat resistance, lubricity, etc., dimethyl polysiloxane oils have been used widely as straight oils such as spandex oils and sewing machine thread oils. The term "straight oil" means 100% oil treatment agents free from solvent or water. Recently, for improving smoothness and antistatic properties of dimethyl polysiloxane oils, various improved straight oils have been developed. Examples include mixtures of ethylene oxide- and propylene oxide-based polyoxyalkylene- modified silicones, smoothing agents of viscosity below 100 (cSt) mm²/s (centistokes), and higher alcohols; mixtures of dimethyl polysiloxane oils of viscosity 3-50 mm²/s (cSt) and an alpha-olefin polyether-modified oil; mixtures of mineral oil and/or polydiorganosiloxane and amino-modified silicone oil; and mixtures of polydimethylsiloxane and polyamylsiloxane. However, conventional oxyalkylene-modified silicones use polyoxyalkylenes that are random copolymers of ethylene oxide and propylene oxide, thus compatibility with the base oil, dimethyl polysiloxane oil is extremely poor, and use of compatibilizers such as higher alcohols and their fatty acid esters is required. However, even with such compatibilizers, there is a limit in solubilizing power. Namely, complete compatibility is not possible, and separation occurs with the elapse of time. From Japanese Patents Gazette issued 31 October 1977, accession No. 67893Y-38, it was known to use oxyalkylene modified silicones which are block copolymers in admixture with dimethylpolysiloxane. However, the chemical structure of this known composition is different from the structure of the composition of the present invention. With more of such compatibilizers used, the lubricity of dimethyl polysiloxane oils and the antistatic properties of the polyoxyalkylene-modified silicone oils decrease, thus development of straight oils requiring no compatibilizers is desired. The amino-modified silicones and amylsiloxanes are not sufficient in antistatic properties, and they yellow fibrous materials. It is an object of the present invention to provide straight oil compositions for fibrous materials, which have excellent smoothness and antistatic properties and also excellent separation resistance even without compatibilizers. The above object can be achieved by a straight oil composition for fibrous materials comprising: (A) 100 parts by weight of dimethyl polysiloxane having a viscosity of from 3 to 30 mm²/s (cSt) at 25°C and (B) 0.5 to 50 parts by weight of a polyoxyalkylene group-containing organopolysiloxane represented by the general formula Q{(CH₃)₂SiO} x Si(CH₃)₂Q, wherein x is an integer of one or more and each Q represents. independently, a polyoxyalkylene group having the formula -RO(C₃H₆O) a (C₂H₄O) b R¹ wherein R represents an alkylene group having from 2 to 5 carbon atoms; R¹ represents a radical selected from the group consisting of the hydrogen atom, alkyl groups having from 1 to 6 carbon atoms, -COCH₃, and -COR²COOH; R² represents a divalent hydrocarbon group having from 1 to 15 carbon atoms; (C₃H₆O) a and (C₂H₄O) b represent oxyalkylene blocks and these oxyalkylene blocks are connected as shown in the formula Q; a is an integer of 1-15; b is an integer of 1-15; and the a/b ratio is 1/10 to 10/1. The dimethyl polysiloxane used as component (A) has a viscosity of 3-30 mm²/s (cSt) at 25°C and provides lubrication to the fibrous materials. With viscosity below 3 mm²/s (cSt), the lubrication is not sufficient, while above 30 mm²/s (cSt), too much dimethyl polysiloxane adheres to the fibrous materials. The molecular structure may be linear, cyclic, or partially branched and consists of dimethyl siloxane units and, in the case of linear structures, trimethylsiloxy or hydroxy end groups and, additionally, in the case of partially branched structures trace amounts of methyl siloxane units and silica units. Dimethyl polysiloxanes are well known in the organosilicon art and need no further delineation herein. Many, including the cyclic and linear compounds, are commercially available. A preferred dimethyl polysiloxane is a linear trimethylsiloxy-terminated polydimethylsiloxane. The polyoxyalkylene group-containing organopolysiloxanes used as component (B) are the components that effect the characteristics of the present invention, i.e., they are compatible with component (A) and impart good antistatic properties to the fibrous materials. They are represented by the general formula Q{(CH₃)₂SiO} x Si(CH₃)₂Q where the subscript x is an integer of at least one and Q represents a polyoxyalkylene group. In the formula immediately above the maximum value of x is not narrowly restricted; it has been found that excellent results have been obtained with polyoxyalkylene group- containing organopolysiloxanes wherein the average value of x is as large as 100. In the formula immediately above Q represents a polyoxyalkylene having the formula -RO(C₃H₆O) a (C₂H₄O) b R¹. In the formula for Q, R represents an alkylene group having from 2 to 5 carbon atoms; R¹ represents a hydrogen atom, an alkyl group having from 1 to 6 carbon atoms, -COCH₃, or -COR²COOH; R² represents a divalent hydrocarbon group having from 1 to 15 carbon atoms; (C₃H₆O) a and (C₂H₄O) b are blocks, and these oxyalkylene blocks are connected as shown in the formula Q; the subscript a is an integer of 1-15 preferably 3-10; the subscript b is an integer of 1-15 preferably 3-10; the a/b ratio is 1/10 to 10/1, preferably 3/10 to 10/3. The alkylene group of 2-5 carbon atoms for R may be an ethylene group, propylene group, butylene group, isobutylene group, pentylene group, etc. R¹ represents a hydrogen atom, an alkyl group of 1-6 carbon atoms, -COCH₃, or -COR₂COOH. The alkyl group of 1-6 carbon atoms for R¹ may be a methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, n-pentyl, etc. R² represents a divalent hydrocarbon group of 1-15 carbon atoms such as an alkylene group, e.g., an ethylene group, a propylene group, etc.; alkenylene group, e.g., a vinylene group, a propenylene group, etc.; an arylene group, e.g. a phenylene group, etc.; or a divalent group having the following formula. The preferred R¹ is a hydrogen atom, a methyl group or an acetoxy group. The propylene oxide units of the polyoxalkylene group Q in the polyoxyalkylene-group-containing organopolysiloxanes of the present invention are located as a block at the organopolysiloxane, i.e. internal, side of the Q radical and the ethylene oxide units are located as a block on the opposite, i.e. terminal, side, of the Q radical. According to our study, it has been learned that such polyoxyalkylene group structure is useful for enhancing the compatibility with dimethyl polysiloxane. The amount of this component (B) used, based on 100 parts by weight of the component (A), is 0.5-50 parts by weight, preferably 3-10 parts by weight, and for heavy antistatic effects, 5-20 parts by weight. The polyoxyalkylene group-containing organopolysiloxanes can be prepared by any suitable method that will provide a block structure. For example, a desired number of moles of propylene oxide is first added to an unsaturated alcohol, such as allyl alcohol, followed by adding a desired number of moles of ethylene oxide to obtain an unsaturated-group-containing polyoxyalkylene. Next, this product is subjected to an addition reaction with an organohydrogenpolysiloxane containing silicon-bonded hydrogen atoms at its terminal portions in the presence of a platinum catalyst to synthesize the organopolysiloxane of this component. The compositions of the present invention can be prepared by simple mixing of components comprising components (A) and (B) to provide a transparent liquid with good compatibility of components (A) and (B). Within the scope of the present invention, the compositions of the present invention may be compounded with other additives, such as anticorrosive agents, and organopolysiloxanes other than components (A) and (B). In treating fibrous materials, the fibrous materials may be immersed in a treatment bath of the composition of the present invention followed by squeezing with rollers, or fibrous materials are run through the bath and contacted by a pickup roll, or the compositions are sprayed on the fibrous materials. The amount applied varies depending on the fibrous materials, and thus is not restricted in any particular way. It is usually 0.05-7.0 wt%, preferably 0.5- 5.0% as organopolysiloxane, based on the fibrous material. After application, heat treatment gives uniformity. The fibrous materials may be natural fibers such as wool, silk, jute, cotton, angora, mohair, etc.; regenerated fibers such as viscose rayon, cuprammonium rayon, etc.; semisynthetic fibers such as acetate, etc.; synthetic fibers such as polyesters, polyamides, polyacrylonitrile, poly(vinyl chloride), poly(vinyl alcohol), polyethylene, polypropylene, spandex, etc. Next, the present invention is explained with examples. Unless stated otherwise, parts are by weight, and percentages are by weight. Viscosity values are at 25°C. The following ten organopolysiloxanes are synthesized. A. Invention Compound HOC₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄-OC₃H₆OC₃H₆OC₃H₆OC₃H₆-OC₃H₆-{(CH₃)₂SiO}₁₀₀(CH₃)₂Si-C₃H₆O-C₃H₆OC₃H₆OC₃H₆OC₃H₆OC₃H₆O-C₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄OH Viscosity: 748 (cSt). mm²/s B. Invention Compound HOC₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄-OC₃H₆OC₃H₆OC₃H₆OC₃H₆-OC₃H₆-{(CH₃)₂SiO}₉₀(CH₃)₂Si-C₃H₆O-C₃H₆OC₃H₆OC₃H₆OC₃H₆OC₃H₆O-C₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄OH Viscosity: 678 (cSt). mm²/s C. Invention Compound HOCO(CH₂)₂COOC₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄-OC₃H₆OC₃H₆OC₃H₆OC₃H₆-OC₃H₆-{(CH₃)₂SiO}₉₀(CH₃)₂Si-C₃H₆O-C₃H₆OC₃H₆OC₃H₆OC₃H₆OC₃H₆O-C₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄OCO(CH₂)₂COOH Viscosity 2110 mm²/s (cSt). D. Invention Compound HOCO(CH₂)₂COOC₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄-OC₃H₆OC₃H₆OC₃H₆OC₃H₆-OC₃H₆-{(CH₃)₂SiO}₆₀(CH₃)₂Si-C₃H₆O-C₃H₆OC₃H₆OC₃H₆OC₃H₆OC₃H₆O-C₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄OCO(CH₂)₂COOH Viscosity: 1521 mm²/s (cSt). E. Comparison Compound H(OC₃H₆)₅(OC₂H₄)₅-OC₃H₆-{(CH₃)₂SiO}₁₀₀(CH₃)₂Si-C₃H₆O-(C₂H₄O)₅(C₃H₆O)₅H Viscosity: 536 mm²/s (cSt). (ethylene oxide and propylene oxide random copolymer) F. Comparison Compound H(OC₂H₄)₁₂-OC₃H₆-{(CH₃)₂SiO}₁₀₀(CH₃)₂Si-C₃H₆O-(C₂H₄O)₁₂H Viscosity: 3820 mm²/s (cSt). G. Comparison Compound H(OC₂H₄)₅-OC₃H₆-{(CH₃)₂SiO}₁₀₀(CH₃)₂Si-C₃H₆O-(C₂H₄O)₅H Viscosity: 284 mm²/s (cSt). H. Comparison Compound (CH₃)₃Si{(CH₃)₂SiO}₄₀₀{(CH₃)(NH₂CH₂CH₂NHC₃H₆)SiO}₈Si(CH₃)₃ Viscosity: 1200 mm²/s (cSt). I. Comparison Compound Partial hydrolytic condensate of C₄H₉Si(OCH₃)₃ Viscosity: 23000 mm²/s (cSt). J. Comparison Compound HOC₃H₆OC₃H₆OC₃H₆OC₃H₆OC₃H₆-OC₂H₄OC₂H₄OC₂H₄OC₂H₄-OC₃H₆-{(CH₃)₂SiO}₁₀₀(CH₃)₂Si-C₃H₆O-C₂H₄OC₂H₄OC₂H₄OC₂H₄OC₂H₄O-C₃H₆OC₃H₆OC₃H₆OC₃H₆OC₃H₆OH Viscosity: 425 mm²/s (cSt). Application Example 1 Dimethyl polysiloxane terminated by trimethylsiloxy groups at both chain ends (Silicone) was compounded with the organopolysiloxanes A-J (Polyoxyalkylenesiloxane) above, as described in Table I, and mixed for 15 minutes to obtain treatment liquids for spandex fibers. The dimethyl polysiloxane used had a viscosity of 10 mm²/s (cSt) or 20 mm²/s (cSt). Treatment Liquid No. Composition, parts Silicone Polyoxyalkylenesiloxane 10(cSt). mm²/s 20(Sts). mm²/s A B C D E F G H I J Invention 1 100 1 Invention 2 100 3 Invention 3 100 5 Invention 4 100 10 Invention 4 100 20 Invention 6 100 10 Invention 7 100 10 Invention 8 100 10 Comparison 9 100 5 Comparison 10 100 5 Comparison 11 100 5 Comparison 12 100 5 Comparison 13 100 5 Comparison 14 100 5 Comparison 15 100 Comparison 16 100 In glass bottles were placed 100 cm³ of each treatment liquid separately, they were allowed to stand at 25°C for 1 week, and compatibility was evaluated by the standard below: 〈a〉 = Uniform dissolution and dispersion, transparent: 〈b〉 = Slightly turbid when compounded, some separation after 1 week: 〈c〉 = Turbid when compounded, complete separation after 1 week. Volume resistivity in compounding was measured according to JIS C2101, using a volume resistivity meter from the Hewlett Packard Co. of the U.S.A. As shown in Table II, the treatment liquids of the present invention show good compatibility, uniform dispersion, and stability and low volume resistivity, and are thus very favorable as straight oils for spandex fibers. Application Example 2 A nylon sewing machine thread skein that had been woolie finished and fluorescent whitened was immersed in the treatment liquid of 3, 12, or 15 and adjusted to 5.5% pickup using a centrifugal dewatering machine. Next, the treated machine thread was wound on 5 sheets of thick paper of 3 cm X 5 cm X 0.2 cm, and 4 sheets were fitted on a Todai Kaken-type rotary static tester and rubbed with 100% cotton shirting No. 3 at 800 rpm for 60 sec, then the triboelectric voltage was measured. One-half of the remaining sheet was covered with a black paper, irradiated in a fadeometer-type weather tester for 3 hr, and the yellowing caused by the light irradiation was evaluated according to JIS L0804 using a fading gray scale. As shown in Table III, the samples treated with the treatment agents of the present invention had low triboelectric voltage and no yellowing, thus the treatment agents are suitable as lubricants for machine threads. Application Example 3 Two organopolysiloxanes shown below were synthesized: K. Invention Compound H(OC₂H₄)₅(OC₃H₆)₁₀-OC₃H₆-{(CH₃)₂SiO}₉₀(CH₃)₂Si-C₃H₆O-(C₃H₆O)₁₀(C₂H₄O)₅H (ethylene oxide-propylene oxide block copolymer) Viscosity: 1020 mm²/s (cSt). L. Invention Compound H(OC₂H₄)₅(OC₃H₆)₃-OC₃H₆-{(CH₃)₂SiO}₉₀(CH₃)₂Si-C₃H₆O-(C₃H₆O)₃(C₂H₄O)₅H (ethylene oxide-propylene oxide block copolymer) Viscosity: 584 mm²/s (cSt). Treatment liquids for spandex fiber were prepared similarly to those in Application Example 1 by mixing 100 parts of dimethyl polysiloxane terminated by trimethylsiloxy groups at both chain ends and having a viscosity of 5 mm²/s (cSt) and 10 parts of organopolysiloxanes prepared above and the liquids were evaluated. Results are given in Table IV. The results showed good compatibility and antistatic properties of the treatment liquids of the present invention. Application Example 4 Two organopolysiloxanes shown below were synthesized: M. Invention Compound CH₃(OC₂H₄)₅(OC₃H₆)₃-OC₃H₆-{(CH₃)₂SiO}₉₀(CH₃)₂Si-C₃H₆O-(C₃H₆O)₃(C₂H₄O)₅CH₃ (ethylene oxide-propylene oxide block copolymer) Viscosity: 430 mm²/s (cSt). N. Invention Compound CH₃CO(OC₂H₄)₅(OC₃H₆)₁₀-OC₃H₆-{(CH₃)₂SiO}₉₀(CH₃)₂Si-C₃H₆O-(C₃H₆O)₁₀(C₂H₄O)₅COCH₃ (ethylene oxide-propylene oxide block copolymer) Viscosity: 460 mm²/s (cSt). Treatment liquids for spandex fiber were prepared similarly to those in Application Example 1 by mixing 100 parts of dimethyl polysiloxane, terminated by trimethylsiloxy groups at both chain ends and having a viscosity of 5 mm²/s (cSt), and 10 parts of prepared organopolysiloxanes M and N. The results showed good compatibility and volume resistivity 8.5x10¹¹ ohm-cm (M) and 7.3x10¹¹ ohm-cm (N) indicating good antistatic properties. Thus these liquids are suitable as oils for spandex. The straight oils of the present invention for fibrous materials are excellent in providing smoothness, antistatic properties, separation resistance, and yellowing resistance to a fibrous material treated therewith.

Claims: A straight oil composition for fibrous materials comprising: (A) 100 parts by weight of dimethyl polysiloxane having a viscosity of from 3 to 30 mm²/s (cSt) at 25°C and (B) 0.5 to 50 parts by weight of a polyoxyalkylene group-containing organopolysiloxane represented by the general formula Q{(CH₃)₂SiO} x Si(CH₃)₂Q, wherein x is an integer of one or more and each Q represents, independently, a polyoxyalkylene group having the formula -RO(C₃H₆O) a (C₂H₄O) b R¹, wherein R represents an alkylene group having from 2 to 5 carbon atoms; R¹ represents a radical selected from the group consisting of the hydrogen atom, alkyl groups having from 1 to 6 carbon atoms, -COCH₃, and -COR²COOH; R² represents a divalent hydrocarbon group having from 1 to 15 carbon atoms; (C₃H₆O) a and (C₂H₄O) b represent oxyalkylene blocks and these oxyalkylene blocks are connected as shown in the formula Q; a is an integer of 1-15; b is an integer of 1-15; and the a/b ratio is 1/10 to 10/1.

Inventors: ONA ISAO, OZAKI MASURU, ONA, ISAO, OZAKI, MASURU
Applicants: TORAY SILICONE CO, TORAY SILICONE COMPANY, LIMITED
Application year: 1989
Main classification: D06M15
IPC codes: D06M15