Process of producing a bismuth system oxide superconductor

Abstract: A bismuth system oxide superconductor comprising the 11) K phase is effectively prepared by a process compri­ sing steps of mixing a bismuth compound, a strontium com­ pound, a calcium compound, a copper compound and optionally a lead compound, optionally provisionally sintering the mixture, and sintering the mixture.

Description: BISMUTH SYSTEM OXIDE SUPERCONDUCTORS AND PREPARATION THEREOF The present invention relates to bismuth system oxide superconductors and preparation thereof. More particularly, the present invention relates to bismuth system oxide superconductors comprising the 110 K phase. The bismuth system oxide superconductor was found in January 1988 by Maeda et al (Jap. J. Appl. Phys., 27, (1988) L209). With this bismuth system oxide, sharp decrease of electric resistance was observed around 110 K and also the Meissner effect was observed in the same temperature range. Since the critical temperature of 110 K is much higher than 90 K of YBa₂CU₃O y which had been believed to have the highest critical temperature, the bismuth system oxide is expected to find various applications in future. It is known that a phase of the bismuth system oxide having the critical temperature of 110 K can be isolated as a single crystal. However, the isolated single crystal cannot be used as a superconductive material. Then, it can be said that, at the time of finding by Maeda et al, no practically usable material consisting of a single phase of the bismuth system oxide having the critical temperature of 110 K was produced, and the produced material contained impurities such as a 80 K phase or a semiconductive phase and Ca₂PbO₄. In addition, the X-ray diffraction pattern of the bismuth system oxide had weak diffraction peaks other than that assigned to the 110 K phase, although compounds to which such weak diffraction peaks are assigned were not specified. Since the presence of several phases in the material seriously deteriorates the superconductive properties, it was desired to provide a superconductive material essentially consisting of the 110 K phase. To increase the proportion of the 110 K phase in the bismuth system oxide, it was proposed to heat said oxide. However, the heating took long time. For example, it took several days at 880°C in the air (the presentation in the International Conference on High Temperature Superconductors and Material and Mechanisms of Superconductivity held on February 29 to March 4, 1989 in Interlaken, Switzerland), or eleven days in the air (the 90th Annual Meeting of the American Ceramics Society held on May 1 to 5, 1988 in Cincinnati, Ohio, U.S.A.). Some other measures to increase the proportion of the 110 K phase were reported. For example, Takano et al (Jap. J. Appl. Phys. June 1988, pp. L 1041-1043) proposed the addition of lead (Pb), and Kijima (EP-0 359 827 A1) et al proposed the variation of the composition. Although they achieved some improvements, their process require long reaction time, for example, 244 hours in the air by Takano et al or 120 hours in the air by Kijima et al. In the practical production of the oxide superconductive materials, the decrease of the reaction temperature is one of the important requirements. In the field of semiconductors, the oxide superconductor should be produced at a sintering temperature as low as possible so as not to deteriorate properties of silicon substrates. In case of Y-system and Tl-system oxides, the bulk materials should be sintered at about 900°C and 1,000°C, respectively. Although the bismuth system oxide can be sintered at a comparatively low temperature, the sintering temperature is still about 870°C. One object of the present invention is to provide a process for effectively producing a bismuth system oxide having a larger proportion of the 110 K phase in a comparatively short time. Another object of the present invention is to provide a process for producing a bismuth system oxide superconductor in which a raw material mixture can be sintered at a comparatively low temperature. Another object of the present invention is to provide a bismuth system oxide superconductor consisting essentially of the 110 K phase. Accordingly, the present invention provides a process of producing a bismuth system oxide superconductor, which comprises mixing a bismuth compound, a strontium compound, a calcium compound and a copper compound characterized in sintering the mixture under atmospheric pressure wherein the oxygen partial pressure during sintering is not higher than 0.15 atm. Fig. 1 is the X-ray diffraction patterns of the bismuth system oxides prepared in Example 1 and Comparative Example 1, Fig. 2 is a graph showing the temperature dependency of resistance of the bismuth system oxides prepared in Example 1 and Comparative Example 1, Fig. 3 is a graph showing the temperature dependency of coil inductance change caused by the bismuth system oxides prepared in Example 1 and Comparative Example 1, Fig. 4 is the X-ray diffraction pattern of the bismuth system oxide prepared in Example 2, Fig. 5 is a graph showing the temperature dependency of resistance of the bismuth system oxide prepared in Example 2, Fig. 6 is a graph showing the temperature dependency of coil inductance change caused by the bismuth system oxide prepared in Example 2, Fig. 7 is a graph showing the temperature dependency of resistance of the bismuth system oxides prepared in Examples 3 to 5 and Comparative Examples 2 and 3, Fig. 8 is a graph showing the temperature dependency of coil inductance change caused by the bismuth system oxides prepared in Examples 3 and 5 and Comparative Examples 2 and 3, Fig. 9 is the X-ray diffraction pattern of the bismuth system oxide prepared in Example 6, Fig. 10 is a graph showing the temperature dependency of resistance of the bismuth system oxide prepared in Example 6, Fig. 11 is a graph showing the temperature dependency of the magnetic susceptibility of the bismuth system oxide prepared in Example 6, Fig. 12 is the X-ray diffraction pattern of the bismuth system oxide prepared in Example 7, Fig. 13 is a graph showing the temperature dependency of resistance of the bismuth system oxide prepared in Example 7, Fig. 14 is a graph showing the temperature dependency of coil inductance change by the bismuth system oxide prepared in Example 7, Fig. 15 shows the X-ray diffraction patterns of the bismuth system oxides prepared in Examples 8, 9, and 10, Fig 16 is the X-ray diffraction pattern of the bismuth system oxide prepared in Example 11, Fig. 17 shows the temperature dependency of the electric resistance of the bismuth system oxides produced in Examples 12 and 13, and Fig. 18 shows the X-ray diffraction patterns of the bismuth system oxides produced in Comparative Examples 4 to 8. The bismuth system oxide superconductor of the present invention comprises bismuth, strontium, calcium, copper and oxygen atoms. A part of the bismuth atoms may be replaced with lead atoms. Depending on the composition of these atoms, the bismuth system oxide has different performances. For example, in the lead-free system, when the atomic ratio of Bi:Sr:Ca:Cu is 1:1:1:2, the proportion of the 110 K phase is maximum. When said atomic ratio is 2:2:1:2, the 80 K phase dominates in the bismuth system oxide. Preferably, the atomic ratio of strontium to bismuth is from 0.8 to 1.2, that of calcium to bismuth is from 1 to 4, that of copper to bismuth is from 1.5 to 5. When the lead atoms are contained in the bismuth system oxide, the atomic ratio of lead to bismuth is from 0.1:0.9 to 0.4:0.6. The bismuth system oxide superconductive material may include the 110 K phase, the 80 K phase and the semiconductive phase. In the X-ray diffraction pattern, diffraction lines to be assigned to the 110 K phase, the 80 K phase and the semiconductive phase appear at 2 of about 4.7°, 5.7° and 7.2°, respectively. In addition, a diffraction line to be assigned to Ca₂PbO₄ which is contained as an impurity appears at 2 of 17.8°. In some cases, a weak diffraction line which may be assigned to other impurities may appear at 2 of 16.5°. In the bismuth system oxide superconductor containing the lead atoms according to the present invention, the diffraction lines at 2 of 5.7 and 7.2° should be 5 % or less of that at 2 of 4.7°. To achieve this condition, the bismuth system oxide preferably has the composition of Bi x Pb y (Sr u Ca v Cu w ) z O α wherein x is a number of from 0.150 to 0.215, y is a number of 0.030 to 0.090 and z is a number of 0.720 to 0.800 provided that the sum of x, y and z is 1 (one); and u is a number of from 0.200 to 0.290, v is a number of from 0.250 to 0.355 and w is a number of from 0.430 to 0.530 provided that the sum of u, v and w is 1 (one) and α is a number of 0.8 to 1.3. To obtain the superconductive material having no impurity, preferably x is a number of from 0.185 to 0.210, y is a number of 0.030 to 0.050 and z is a number of 0.750 to 0.770 provided that the sum of x, y and z is 1; u is a number of from 0.255 to 0.290, v is a number of from 0.275 to 0.310 and w is a number of from 0.430 to 0.455 provided that the sum of u, v and w is 1; and a is a number from 0.8 to 1.3. Another feature of the bismuth system oxide superconductive material of the present invention resides in that it includes a phase which becomes superconductive in a temperature range of 90 to 100 K (hereinafter referred to as "95 K phase"). In such case, the diffraction line may appear at 2 of 5.7° and/or 7.2°. Further, the superconductive material may contain the impurities. Since the 95 K phase provides the diffraction line at 2 of 4.7°, it is substantially the same as the 110 K phase from the view point of the X-ray diffraction pattern. The 110 K phase has a higher critical temperature but small critical current. Therefore, the critical temperature should be measured with a very small current. Otherwise, a tail appears in the lower temperature side and the apparent critical temperature is measured lower than the actual one. Although the 95 K phase has the lower critical temperature than the 110 K phase, the former has a strong pinning effect than the latter and therefore the former has the large critical current J c . The raw materials for supplying the above atoms in the bismuth system oxide may be any of inorganic compounds such as hydroxides, oxides, carbonates and nitrates and organic acid salts such as oxalates and acetates insofar as the compounds can be converted to the corresponding oxides by heating. Preferably, at least copper is used in the form of its nitrate, more preferably, all the raw materials are in the form of nitrates. When the carbonates or oxides are used, they may be dissolved in nitric acid. The raw materials are homogeneously mixed by any of the conventional methods. For example, the raw materials are ground and mixed in a mortar made of agate or with a ball mill. The raw materials are dissolved or dispersed in water and heated to dryness while stirring. Since bismuth nitrate is hardly soluble in pure water, preferably water is acidified with nitric acid. Further, the solution or dispersion of the raw materials can be spray dried and mixed. Alternatively, a thin film formed by sputtering has a homogeneous composition. The raw material mixture prepared by the above methods is provisionally sintered before sintering, although the mixture may be sintered without provisional sintering. The mixture of the compounds other than oxides is provisionally sintered at a temperature around 800°C, for example from 800 to 840°C in an atmosphere of the air, oxygen or a mixture of oxygen and an inert gas (e.g. nitrogen, helium, argon, etc.). It is not necessary to provisionally sinter the mixture of oxides or the thin film of oxides or metals formed by sputtering before sintering. Then the material is sintered. When the raw materials are in the powder form, they are molded before sintering. The raw materials may be molded in any shape and/or size. For example, the molded material may be in the form of a pellet, a thin plate or a wire. The sintering is carried out usually in the air. The partial pressure of oxygen may be from 0 (zero) to 0.015 MPa (0.15 atm), preferably from 0.003 MPa to 0.01 MPa (0.03 to 0.1 atm). To adjust the oxygen partial pressure, the air or pure oxygen gas may be diluted with the inert gas. The oxygen partial pressure of 0 (zero) means that no oxygen is contained and the sintering atmosphere consists of pure inert gas. The sintering temperature varies with the oxygen partial pressure and/or the composition of the raw materials. In general, the sintering temperature is from just below the melting point of the raw material to 50°C below said melting point, preferably 30°C below said melting point. In case of the bismuth system oxide, the raw material cannot be reacted at a temperature higher than the melting point, since the once melt material has no superconductive property. The melting points of various compositions are as follows: When the atomic ratio of Bi:Sr:Ca:Cu is 1:1:1:2, the melting point is about 870°C under the oxygen partial pressure of 0.02 MPa (0.2 atm.)., about 850°C under oxygen partial pressure of 0.003 MPa (0.03 atm.), about 830°C under oxygen partial pressure of 0.001 MPa (0.01 atm)., or about 810°C under oxygen partial pressure of 0 (zero). When the atomic ratio of Bi:Pb:Sr:Ca:Cu is 0.8:0.2:0.8:1:1.4, the melting point under the oxygen partial pressure of 0.02 MPa (0.2 atm)., is about 845°C. By the decrease of the oxygen partial pressure, the oxide product can be produced in a comparatively short time in a wide temperature range. The sintering time is at least 2 hours, preferably at least 8 hours, more preferably at least 12 hours. The sintered oxide material is cooled preferably in an atmosphere having an oxygen partial pressure higher than that in the sintering step, while it may be cooled in the atmosphere having the same oxygen partial pressure as in the sintering step. Through the bismuth system oxide cooled in the atmosphere having the higher oxygen partial pressure, a larger amount of current can be flown. In addition, the 110 K phase and the 95 K phase can be clearly separated in the magnetization measurement by cooling under the higher oxygen partial pressure. Alternatively, the sintered oxide is cooled under the same oxygen partial pressure as in the sintering pressure, heated at a temperature lower than the sintering temperature and treated with oxygen under the higher oxygen pressure. The present invention will be illustrated more in detail by following examples. Example 1 (Reference Example) Bi₂O₃, SrCO₃, CaCO₃ and CuO were weighed so that the atomic ratio of Bi:Sr:Ca:Cu was 1:1:1:2 and completely dissolved in excess nitric acid while heating. The solution was charged in an evaporating dish made of platinum and heated while continuous stirring to evaporate water off. During evaporation, excess nitric acid was also removed. The mixture of nitrates was taken in an alumina crucible and further heated, whereby the nitrates were decomposed to liberate NO₂. The heating was continued at 800°C till no NO₂ was liberated. The mixture was ground in an agate mortar and molded in a round plate of 13 mm in diameter and about 1 mm in thickness. Then, the plate was placed in an alumina boat and set at the center of a tubular furnace of 100 mm in inner diameter and 600 mm in length. Then, the plate was sintered at 867°C for 12 hours with flowing a mixture of argon and oxygen in a volume ratio of 4:1 at a flow rate of 250 ml/min. The sintered plate was ground and re-molded in a round plate having the same sizes as above. Then, the plate was sintered for 12 hours under the same conditions as above. The sintered round plate was slightly warped. This indicated that the sintering was carried out just below the melting point. With this sintered sample, an X-ray diffraction pattern, electric resistance and the Meissner effect were measured. The resistance was measured on the sintered plate as such by the standard four probe method. The Meissner effect was measured at room temperature by placing the sample in a coil having an inductance of about 1.7 mH and monitoring the change of inductance. The results are shown in Figs. 1, 2 and 3, respectively. In Fig. 1, the diffraction line assigned to the (002) plane of the 110 K phase appears around 2 of 4.7°, and the diffraction line assigned to the 80 K phase appears around 2 of 5.7°. In Figs. 2 and 3, the resistance and the coil inductance change sharply drop around 110 K. This indicates the formation of the 110 K phase. Comparative Example 1 Bi₂O₃, SrCO₃, CaCO₃ and CuO were weighed so that the atomic ratio of Bi:Sr:Ca:Cu was 1:1:1:2 and thoroughly mixed in the agate mortar. Then, the mixture was provisionally sintered at 810°C for 10 hours in a stream of air. Thereafter, the grinding and the three hour provisional sintering were repeated twice. The provisionally sintered material was again ground and molded to obtain a round plate of 13 mm in diameter and about 1 mm in thickness. Then, the plate was sintered under the same conditions as in Example 1. The sintered round plate was-slightly warped. This indicated that the sintering was carried out just below the melting point. With this sintered sample, an X-ray diffraction pattern, resistance and the Meissner effect were measured in the same manners as in Example 1. The results are also shown in Figs. 1, 2 and 3. In the X-ray diffraction pattern, only the diffraction line at 2 of 5.7° appeared but no diffraction line at 2 of 4.7° which is assigned to the 110 K phase appeared. The changes of the resistance and the inductance change near 110 K were slight, which indicates that the proportion of the 110 K phase was small. Example 2 Nitrates of Bi, Pb, Sr, Ca and Cu were weighed so that the atomic ratio of Bi:Pb:Sr:Ca:Cu was 0.8:0.2:0.8: 1.0:1.4 and completely dissolved in water acidified with nitric acid. The solution was charged in an evaporating dish made of platinum and heated while continuously stirring to evaporate water off. The mixture of nitrates was taken in an alumina crucible and further heated, whereby the nitrates were decomposed to liberate NO₂. The heating was continued at 800°C till no NO₂ was liberated. The mixture was ground in an agate mortar and molded in a round plate of 13 mm in diameter and about 1 mm in thickness. Then, the plate was placed in an alumina boat and set at the center of a tubular furnace of 100 mm in inner diameter and 600 mm in length. Then, the plate was sintered at 828°C for 12 hours with flowing a mixture of argon and oxygen in a volume ratio of 12:1 at a flow rate of 250 ml/min. The sintered plate was ground and re-molded in a round plate having the same sizes as above. Then, the plate was sintered for 108 hours under the same conditions as above. The sintered round plate was slightly warped. This indicated that the sintering was carried out just below the melting point. With this sintered sample, an X-ray diffraction pattern, electric resistance and the Meissner effect were measured in the same manners as in Example 1. The results are shown in Figs. 4, 5 and 6, respectively. In the X-ray diffraction pattern, the diffraction line at 2 of 4.7° which is assigned to the 110 K phase appeared but no diffraction line was found at 2 of 5.7°. The changes of the resistance and the coil inductance change near 110 K were considerably large, which indicates that the most portion of the sintered plate consisted of the 110 K phase. The prior arts reported that the intensity of diffraction line at 2 of 5.7° was at most 15 % of that at 2 of 4.7°. Herein, the intensity of the diffraction line is a distance from the base line to the top of the line. Synthesis of a bismuth system oxide having no diffraction line at 2 of 5.7° has not been reported. In view of the detection limit of about 1 % in the X-ray diffraction analysis, the produced bismuth system oxide is deemed to be the superconductive material consisting of the 110 K phase only. Example 3 In the same manner as in Comparative Example 1, a round plate of bismuth system oxide of 13 mm in diameter and about 1 mm in thickness was produced. Then, the plate was sintered in the same manner as in Example 1 but heating the plate at 861°C with flowing a mixture of argon and oxygen in a volume ratio of 12:1 (corresponding to the oxygen partial pressure of 0.0077 MPa (0.077 atm).) at a flow rate of 250 ml/min. The sintered round plate was slightly warped. This indicated that the sintering was carried out just below the melting point. With this sintered sample, the resistance and the Meissner effect were measured in the same manners as in Example 1. The results are shown in Figs. 7 and 8. The sharp changes of the resistance and the inductance change appeared around 110 K. This indicates the formation of the 110 K phase. Example 4 In the same manner as in Example 3 but sintering the plate of bismuth system oxide at 830°C with flowing a mixture of argon and oxygen in a volume ratio of 99:1 (corresponding to the oxygen partial pressure of 0.01 atm.), the sintered plate of bismuth system oxide was produced. The sintered round plate was slightly warped. This indicated that the sintering was carried out just below the melting point. With this sintered sample, the resistance was measured in the same manner as in Example 1. The result is shown in Fig. 7. The sharp change of the resistance appeared around 110 K. This indicates the formation of the 110 K phase. According to the present invention, the 110 K phase can be formed at a temperature at which the 110 K phase was not formed by the conventional methods. Example 5 In the same manner as in Example 3 but sintering the plate of bismuth system oxide at 816°C with flowing a mixture of argon and oxygen in a volume ratio of 99:1 (corresponding to the oxygen partial pressure of 0.001 MPa (0.01 atm).), the sintered plate of bismuth system oxide was produced. The sintered round plate was not deformed since the sintering temperature was 15°C lower than the melting point. The resistance and coil inductance change of this sample are shown in Figs. 7 and 8. The steep decreases of the resistance and coil inductance change were observed around 110 K. It is clear that, according to the present invention, the 110 K phase is formed at a comparatively low sintering temperature of 816°C. Comparative Example 2 In the same manner as in Example 3 but sintering the plate of bismuth system oxide at 887°C with flowing pure oxygen (corresponding to the oxygen partial pressure of 0.1 MPa (1 atm).), the sintered plate of bismuth system oxide was produced. The sintered round plate was slightly warped. This indicated that the sintering temperature was just below the melting point. The resistance and coil inductance change of the sample were measured in the same manners as in Example 1. The results are shown in Figs. 7 and 8. No decrease of the resistance and coil inductance change was observed around 110 K. As understood from these results, at the high oxygen partial pressure, no or few 110 K phase is created. Comparative Example 3 In the same manner as in Example 3 but sintering the plate of bismuth system oxide at 870°C with flowing a mixture of argon and oxygen in a volume ratio of 4:1 (corresponding to the oxygen partial pressure of 0.02 MPa (0.2 atm).), the sintered plate of bismuth system oxide was produced. The sintered round plate was slightly warped. This indicated that the sintering temperature was just below the melting point. The resistance and coil inductance change of the sample were measured in the same manners as in Example 1. The results are shown in Figs. 7 and 8. Slight decrease of the resistance and coil inductance change was observed around 110 K. As understood from these results, in spite of the high sintering temperature of 870°C, only a small portion of the 110 K phase is created. Example 6 Bi₂O₃, PbO, SrCO₃, CaCO₃ and CuO were weighed so that the atomic ratio of Bi:Pb:Sr:Ca:Cu was 0.8:0.15:0.86: 0.86:1.33, which corresponds to Bi 0.2 Pb 0.038 -(Sr 0.281 Ca 0.281 Cu 0.438 ) 0.763 O α , and completely dissolved in excess nitric acid while heating. The solution was charged in an evaporating dish made of platinum and heated while continuously stirring to evaporate water off. In this evaporation, excess nitric acid was also removed. The mixture of nitrates was taken in an alumina crucible and further heated, whereby the nitrates were decomposed to liberate NO₂. The heating was continued at 800°C till no NO₂ was liberated. The mixture was ground in an agate mortar and molded in a round plate of 13 mm in diameter and about 1 mm in thickness. Then, the plate was placed in an alumina boat and set at the center of a tubular furnace of 100 mm in inner diameter and 600 mm in length. Then, the plate was sintered at 835°C for 12 hours with flowing a mixture of argon and oxygen in a volume ratio of 12:1 at a flow rate of 250 ml/min. The sintered plate was cooled to room temperature, ground and re-molded in a round plate having the same sizes as above. Then, the plate was sintered for 72 hours under the same conditions as above. Thereafter, the plate was cooled at a cooling rate of about 2°C/min. When the temperature reached 750°C, the atmosphere was changed to pure oxygen and the plate was cooled to room temperature. The X-ray diffraction pattern, temperature dependency of the resistance and magnetic susceptibility of the sample were measured. The results are shown in Figs. 9, 10 and 11. As shown in Fig. 9, the diffraction line appeared at 2 of 4.7° and no diffraction line appeared at 2 of 5.7° or 7.2°. As shown in Fig. 10, the resistivity change indicates the presence of the 110 K phase alone. The Meissner effect curve of Fig. 11 has two signals corresponding to the 110 K and 95 K phases. These two phases were contained in the volume ratio of about 1:1 and occupied about 92 % of the whole volume. From these results, it can be concluded that the sample produced in this Example consisted of the 1:1 mixture of two kinds of superconductive materials both having the same structure, namely the triple Cu-O layered structure. The shielding effect curve in Fig. 11 should be noted. According to this result, the change of magnetic susceptibility due to the shielding effect was three times larger than that due to the Meissner effect, and such is significantly observed at 90 K or lower. This means that the 95 K phase has the larger shielding effect. This indicates that the pinning effect against the fluxoid quantum beam by the 95 K phase is much larger than that by the 110 K phase, which means the larger critical current. Example 7 Bi₂O₃, PbO, SrCO₃, CaCO₃ and CuO were weighed so that the atomic ratio of Bi:Pb:Sr:Ca:Cu was 0.8:0.2:0.8: 1.0:2.0, which corresponds to Bi 0.167 Pb 0.042 - (Sr 0.211 Ca 0.263 Cu 0.526 ) 0.792 O α , and thoroughly mixed in the agate mortar. The mixture was provisionally sintered at 810°C for 10 hours. Thereafter, the grinding and the three hour provisional sintering were repeated twice. The provisionally sintered mixture was again ground and molded to obtain a round plate of 13 mm in diameter and about 1 mm in thickness. Then, the plate was sintered in the same manner as in Example 1 but heating the plate at 842°C for 80 hours with flowing the mixture of argon and oxygen in the volume ratio of 12:1 at a flow rate of 250 ml/min. The sintered plate was gradually cooled to room temperature under oxygen partial pressure of 1/0.13 MPa (1/13 atm). at a cooling rate of about 2°C/min. The sintered round plate was slightly warped. This indicated that the sintering was carried out just below the melting point. With this sintered sample, an X-ray diffraction pattern, resistance and coil inductance change were measured in the same manners as above. The results are shown in Figs. 12, 13 and 14. As shown in Fig. 12, the diffraction line appeared at 2 of 4.7° but no diffraction line appeared at 2 of 5.7 or 7.2°. That is, the ratio of the intensity of the diffraction line at 2 of 5.7° or about 7.2 was 0 (zero) % of that at 2 of 4.7°. The resistivity steeply decreased from 110 K and dropped to 0 (zero) at 107 K. Correspondingly, the inductance change steeply decreased in the same temperature range. These results indicate that the proportion of the 110 K phase was large in the bismuth system oxide superconductor obtained in this Example. Examples 8-10 Bi₂O₃, PbO, SrCO₃, CaCO₃ and CuO were weighed so that the atomic ratio of Bi:Pb:Sr:Ca:Cu was 0.8:0.2:0.8: 1.0:1.4, which corresponds to Bi 0.190 Pb 0.048 - (Sr 0.250 Ca 0.313 Cu 0.438 ) 0.762 O α , and thoroughly mixed in the agate mortar. The mixture was sintered in the same manners as in Example 6 but adjusting the sintering temperature, the sintering time and oxygen partial pressure as indicated in Table 1 and keeping the same oxygen partial pressure during cooling. The X-ray diffraction patterns of the samples obtained in Examples 8-10 are shown in Fig. 15. The diffraction line appeared at 2 of 4.7° but no or very weak diffraction line appeared at 2 of 5.7° or 7.2°. This indicates that the proportion of the 110 K phase or the 95 K phase was large in each sample. Example 11 Bi₂O₃, PbO, SrCO₃, CaCO₃ and CuO were weighed so that the atomic ratio of Bi:Pb:Sr:Ca:Cu was 0.8:0.15:0.83: 0.89:1.33, which corresponds to Bi 0.2 Pb 0.0375 - (Sr 0.272 Ca 0.292 Cu 0.436 ) 0.7625 O α and thoroughly mixed in the agate mortar. The mixture was sintered in the same manners as in Example 6 but keeping the same oxygen partial pressure during cooling. The X-ray diffraction pattern of this sample is shown in Fig. 16. The strong diffraction line appeared at 2 of 4.7° but no diffraction line appeared at 2 of 5.7° or 7.2°. That is, the ratio of the intensity of the diffraction line at 2 of 5.7° or 7.2° was 0 (zero) % of that at 2 of 4.7°. While in Examples 8-10, a weak line appeared in the 2 range of 17°-18°, which was assigned to impurities, in this Example, no diffraction line at 2 of 17.8°, 16.5° or 29.9° which is to be assigned to impurities was found. This indicates that the sample of this Example would be a superconductive material consisting of the triple Cu-O layered structure. Examples 12 and 13 In the same manner as in Example 7 except that the raw materials were weighed so that the material had the composition of Bi 0.200 Pb 0.037 (Sr 0.259 Ca 0.303 Cu 0.438 ) 0.763 O α (Example 16) or Bi 0.200 Pb 0.037 (Sr 0.245 Ca 0.330 Cu 0.425 ) 0.763 O α (Example 17), the bismuth system oxide material was prepared. With these samples, the temperature dependency of electric resistance was examined. The results are shown in Fig. 17. Apparent decrease of resistance due to the 95 K phase was found at 95 K, while such decrease was not found in Example 6. Diffraction lines appeared at 2 of 5.7° and 7.2° with the strength ratio of 2 % and 9 %, respectively to that of the diffraction line at 2 of 4.7°. Despite of the appearance of the diffraction lines at 2 of 5.7° and 7.2°s, no 80 K phase was identified from the resistance-temperature curve of Fig. 17. The reason for this may be the 110 K phase and the 95 K phase being linked continuously. Comparative Examples 4-8 In the same manner as in Example 7 but weighing Bi₂O₃, PbO, SrCO₃, CaCO₃ and CuO so that the atomic ratio of Bi:Pb:Sr:Ca:Cu was as indicated in Table 2 and keeping the same oxygen partial pressure during cooling, the bismuth system oxide material was prepared. The X-ray diffraction patterns of the samples are shown in Fig. 18. The strong diffraction line appeared at 2 of 4.7°. Further, at 2 of 5.7°, a diffraction line to be assigned to the 80 K phase as well as those assigned to the impurities appeared. This indicates that the prepared material did not consist of the triple Cu-O layered structure alone.

Claims: A process of producing a bismuth system oxide superconductor, which comprises mixing a bismuth compound, a strontium compound, a calcium compound and a copper compound characterized in sintering the mixture under atmospheric pressure wherein the oxygen partial pressure during sintering is not higher than 0,015 MPa (0.15 atm). The process according to claim 1, wherein at least the copper compound is used in the form of copper nitrate, and all the compounds are dissolved or dispersed in a medium, the medium is removed and then the nitrate is thermally decomposed to mix the compounds homogeneously wherein the decomposition is performed prior to the sintering. The process according to claim 2, wherein all compounds are nitrates, and the nitrates are dissolved in a medium, the medium is removed and then the nitrates are thermally decomposed to mix the compounds homogeneously wherein the decomposition is performed prior to the sintering. The process according to claim 1, wherein said mixing step further includes mixing a lead compound. The process according to claim 2, wherein the temperature used to effect said thermal decomposition is in the range of 800°C to 840°C. The process according to claim 1, wherein said oxygen partial pressure is in the range of 0,003 to 0,01 MPa (0.03 to 0.1 atm). The process according to claim 1, wherein said sintering step is carried out at a temperature T, which is within the range (T mp - 50°C) ≤ T < (T mp ) wherein T mp is the melting point of said mixture. The process according to claim 1, wherein said sintering step is carried out for at least 2 hours. The process according to claim 1, wherein said sintering step is carried out for at least 8 hours. The process according to claim 1 or 7, wherein said sintering step is carried out for at least 12 hours. The process according to claim 1, further comprising cooling the bismuth system oxide superconductor after said sintering step in an atmosphere having an oxygen partial pressure that is greater than the oxygen partial pressure present during said sintering step.

Inventors: ENDO UTAKO, KAWAI TOMOJI, KITAZAWA KOICHI, KOYAMA SATOSHI, OKAMURA KAZUO, ENDO, UTAKO, KAWAI, TOMOJI, KITAZAWA, KOICHI, KOYAMA, SATOSHI, OKAMURA, KAZUO, ENDO, UTAKO C/O YODOGAWA WORKS OF DAIKIN, KAWAI, TOMOJI C/O OSAKA UNIVERSITY SANGYO
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LIMITED
Application year: 1989
Main classification: H01L39
IPC codes: C04B35, H01L39