FIRE-RETARDANT

Abstract: A fire-retardant composition comprises a mixture or reaction product of a fire-retardant ammonium salt, urea or biuret, and boric acid or a plastic composition of a sodium silicate-impregnated mat which can be applied to a substrate by transfer from a non-adherent backing sheet.

Description: FIRE-RETARDANT Field of the Invention This invention relates to fire-retardants. Summary of the Invention A first composition of the present invention comprises a mixture or reaction product of a fire-retardant ammonium salt, urea or biuret, and boric acid. A second product of the invention comprises a non-adherent substrate sheet bearing a plastic composition of a sodium silicate-impregnated mat. Description of the Invention The salt in the first composition is preferably selected from monoammonium phosphate, diammonium phosphate, ammonium sulphamate, ammonium sulphate, and mixtures thereof. The first composition can exist in dry form, e.g. as a white, water-soluble powder, or it may be provided in aqueous solution, for which purpose a surfactant may be added. The actual components of the first composition of the invention may be urea salts, e.g. urea (poly)phosphates and urea borates. A first composition of the invention is usually prepared by first mixing the ammonium salt, urea or biuret and boric acid to give a dry mixture which may then be dissolved in water. With respect to the amount of solids, there may be 25-75% by weight of the salt (or mixture of ammonium salts) , 10-40% by weight of urea or biuret and 10-30% by weight boric acid. Because these components may react to give the desired reaction product, alternative components may be used to give the same or a similar result. A first composition of the invention in aqueous form may comprise 5-40% by weight of the solids. A first composition of the invention, usually in aqueous form, can be applied to a variety of substrates' to impart fire-retardanc . Application may be by casting, spraying or any other suitable technique. The substrate may be, for example, metal, wood, wood-derived products, and textiles, e.g. of natural fibres or of a blend of natural and synthetic materials. For any particular application, a first composition of the invention may include various additives which facilitate its use. For example, a storage-stable liquid- fire-retardant suitable for protecting, e.g., wood, may be prepared by adding water glass (which of course has fire-retardant properties) to an aqueous first composition of the invention. A corrosion inhibitor such as urotropine (say in an amount of up to 0.5% by weight of the composition) may be added where the first composition is to be applied to a metal, e.g. steel, structure. Portland cement may be added, for extra strength, e.g. in an amount of up to 7% by weight of the first composition. Depending on the application, an anionic or cationic surfactant may be suitable. A first composition of the invention may comprise a filler such as glass microspheres, perlite, ballotini, vermiculite, mineral wool or waste from ground leather, mineral sanding or foundry sand. Fillers having a particle size of 200-300 mesh are suitable. A foaming agent, e.g. an anionic or neutral surfactant, may be added if an expanded/aerated structure is desired. Another preferred additive is a hardener such as sodium silicofluoride or polyethylene/polypropylene glycol diacetate. Especially for spraying, a resin such as a • low-viscosity melamine-formaldehyde, •urea-formaldehyde or acrylic latex may be included, without reducing fire-retardancy. Dyes or pigments may be added, as desired. For application by spraying, to give a filled coating, a double-feed gun or other means, whereby the fire-retardant formulation is prepared immediately before application, may be used. For example, one feed comprises a liquid first composition of the invention and hardener (freshly-prepared) and the other comprises filler. Use of first compositions of the invention provides coatings which have good heat-resistance. On rigid foam materials such as polystyrene or polyύrethane, the coated product can resist heat and fire, and the coating may remain intact while the foam melts. Suitable amounts of additives will be apparent from the following illustrative Examples, in which all parts and percentages are by weight. Example 1 33 parts monoammonium phosphate, 12.8 parts diammonium phosphate, 23.2 parts urea, 12.5 parts ammonium sulphamate and 18 parts boric acid were mixed to give a white, water-soluble powder. Example 2 A powder was prepared, as in Example 1, using ammonium sulphate instead of ammonium sulphamate. Example 3 The composition of.Example 1 was mixed with 0.5 parts of a surfactant and formulated as a 20% aqueous solution. The pH was 7.0. The- solution was anti-fungal, anti-wood pest and non-toxic to humans and animals. Example 4 Example 3 was repeated, but using the powder of Example 2. The resultant 20% solution had a pH of 5.5 and the same desirable properties as that of Example 3. The solution of Example 3, having a neutral pH, is particularly suited to the treatment of textiles. Depending on a number of factors such as the density of weave of the fabric, its bulk, and the content of synthetic fibres, the solution of Example 3 or Example 4 2 may be applied at a level of 8 to 200 g/m . Either solution may be applied to wood, depending " on its nature 3 and porosity, at a level of 15 to 75 kg/m . Example 5 3 parts of the solution of Example 3 and 7 parts 3 sodium silicate, density 1.45 g/cm , were blended slowly, using a mixer stirring at at least 300 rpm, to give a viscous solution. This solution had a density of 1.395 3 g/cm at 20 C, a viscosity of 16 ± 2s (Ford Cup No. 4 at 20 C), a pH of 11.6 and a dry mass of 42.7%. The solution is anti-fungal, anti-pest, storage-stable and, while its viscosity is high below 10 C, heating restores its desired properties. It can be mixed with water in any proportions. It is suitable for application to wood at a level of 150 to 400 g/m 2 and at a level of 200 to 700 m" for more porous substrates, e.g. chipboard. Example 6 9 litres of the solution of Example 5 and 4.5 kg perlite were mixed. 0.9 kg sodium silicofluoride was added to give a hardened filled material, suitable for rendering and coating. Example 7 15 litres of the solution of Example 5 and 2 kg mineral wool were mixed. 0.6 kg sodium silicofluoride was added to give another hardened filled material suitable for rendering and coating. Example 8 A casting material for slabs was prepared from 48% of the solution of Example 5, 3% of a foaming agent, 44% glass icrospheres and 4% sodium silicofluoride. The solution and the filler were mixed, the mixture was then aerated by the addition of the foaming agent, with stirring. The hardener was then added. Less hardener could be used, although the hardening time was then longer. Exa ple 9 A spraying material was prepared from * 48% of the solution of Example 5, 4% of a low-viscosity melamine-formaldehyde resin, 44% glass microspheres (200-300 mesh) and 4% sodium silicofluoride. The solution, resin and hardener were discharged through one feed, and the hardener through the other feed, of a double-feed gun. The resin could be replaced by urea-formaldehyde or an acrylic latex, to the same end. Example 10 A spraying material was prepared from 15 litres of the solution of Example 5, 2 kg mineral wool, 0.6 kg sodium silicofluoride powder plus, if desired, 7% by weight Portland cement. A double-feed gun was used in a manner parallel to that of Example 9. The second aspect of the invention can provide, in particular, a thin, translucent, flexible material that may be bonded to other materials. When exposed to high temperatures or directly to flame, the material expands to give an inorganic layer. The gases evolved are predominantly water and carbon dioxide, i.e. essentially non-toxic. The components of a second product according to the present invention are a glass fibre mat or other material having an open texture, according to the thickness of the final sheet; a sodium silicate solution, e.g. applied at 2 a level of 120 to 180 gm/m ; a plasticiser and/or hardener such as polyvinyl alcohol, e.g. in an amount of 3 to 5%, dependent upon the flexibility of final product requirement; a surface coating such as an epoxy varnish 2 coating, e.g. in an amount of 30 to 40 gm/m ; and a surfactant, e.g. an anionic surfactant, preferably in an amount of 0.5 to 1.0%. Novel aspects of the invention may lie in combinations of two or more of these components, and particularly in combinations formed at various stages of use of the components, e.g. as described below. An illustrative embodiment of the invention comprises the following procedure: the glass fibre mat is laid upon a non-adherent sheet, such as a thin aluminium sheet, and smoothed flat. A PTFE sheet may be used instead. The sodium silicate is mixed with the detergent and then with the polyvinyl alcohol, while stirring thoroughly. The mix is then spread on the fibre glass mat and allowed to set. When set, the translucent material is peeled from its backing and bonded to a substrate to be protected, such as wood (as a surface coating) , particle board, fabric, textiles or paper (as a backing) , e.g. using a standard bonding press such as would be used for veneers, laminates, etc. The • temperature should not exceed 110°C. The exposed surface and edges of the finished laminate are preferably covered with an epoxy or other water-permeable coating, thus preventing absorption of water and tackiness of the silicate. When used as a fire-resistant intumescent coating, a 0.7-1.0 mm thick coating of the composition bonded to a barrier of wood/wood composite construction such as door should give 30 minutes protection from a fire on the opposite side of the barrier. Two thicknesses, on opposite sides of the wooden barrier, should give more than 60 minutes fire protection. A coating 3 mm thick was tested in an oven. For an applied temperature built up to 750°C, 21 minutes elapsed before 150°C was reached; for an oven temperature building up to 900°C, it took 49 minutes to reach 500°C.

Claims: CLAIMS 1. A composition which comprises a mixture or reaction product of a fire-retardant ammonium salt, urea or biuret, and boric acid. 2. A composition according to claim 1, wherein the salt is selected from monoammonium phosphate, diammonium phosphate, ammonium sulphamate, ammonium sulphate, and mixtures thereof. 3. A composition according to claim 1 or claim 2, in aqueous solution. 4. An aqueous composition according to claim 3, which additionally comprises a filler. 5. A product comprising a non-adherent substrate sheet bearing a plastic composition of a sodium silicate- • impregnated mat. 6. A product according to claim 5, wherein the mat is of glass fibres. 7. A product according to claim 5 or claim 6, wherein the composition comprises polyvinyl alcohol. 8. A composition or product according to any of claims 3 to 7, which additionally comprises a surfactant. 9. A method for imparting fire-retardancy to a substrate, which comprises applying to the substrate a composition as defined in any preceding claim. 10. A method according to claim 9, which comprises the additional step of applying a water-impermeable coating.

Inventors: FOX MALCOLM FRANCIS, FOX, MALCOLM, FRANCIS
Applicants: PYROTEK INTERNATIONAL LTD, PYROTEK INTERNATIONAL LTD.
Application year: 1989
Main classification: C09K21
IPC codes: B32B5, B32B9, C09D5, C09K21, D06M11, D06M13, D06M101, D21H21