Cement compositions

Abstract: Cement compositions containing fly ash having a carbon content are given satisfactory air entrainment by including a water soluble C8 fatty acid salt.

Description: The invention relates to cement compositions and to additives for use in such compositions which improve the air entrainment properties during manufacture. In particular, the invention relates to cement compositions containing pulverised fuel ash which contains carbon as a component. Cement compositions with which the invention is concerned includes concretes which comprise cement aggregate, sand and water; mortars which comprise cement, sand and water; lime sand and water or mixtures containing both lime and cement. High pressure steam cured concretes comprising cement aggregate and water, lime or limestone and siliceous materials such as silica flour and water are also included. The improved physical characteristics produced in cement compositions prepared according to this invention result from air entrainment. The entraining of air in such compositions is known to improve durability of concretes, particularly resistance to frost damage and also improve the flow characteristics, which are of importance for cement pumping and other concrete placing operations. The working characteristics of mortars are also improved by entraining a proportion of air which can reduce the proportion of lime required in the composition. It has been proposed to utilise pulverised fuel ash, also referred to as flyash, as a component in concretes and the requirements for such a component are given in British Standard 3892 (Part 1) 1982, however the present invention is not limited to the fuel ashes described in this standard. The pulverised fuel ash, as it will be termed in this specification, is the ash residue from pulverised fuel. The Applicants have found the presence of carbon in the fuel ash reduces the ability of air entraining agents to operate effectively. GB-A-1434924 discloses a cement composition containing pulverised fuel ash and C8 to C10 fatty acids in order to improve the water absorption of a cement. Thus the present invention describes cement compositions having a proportion of pulverised fuel ash as a component, usually up to about 65% and having a loss on ignition up to about 12%, with an air entrainment agent which is effective despite the presence of the carbon. The invention provides a cement composition containing up to about 65% of pulverised fuel ash and an air entrainment agent together with an amount of a water soluble C₈ fatty acid salt effective to negate the surface activity of the carbon content of the fuel ash. The C8 fatty acid salt is preferentially absorbed on the carbon surface thus allowing the air entrainment agent to remain free in the composition. Usually the fatty acid salt used will be the sodium or potassium salt but the invention contemplates having an additive, the fatty acid, added to the cement composition which reacts with other components of the composition to generate the desired fatty acid salts in situ. The upper level of C8 fatty acid salt added is usually determined by economic factors but it is usually not above about 0.1%, more usually not above 0.05% w/w on the amount of cement. The air entrainment agent is preferably the water soluble C9 and C10 fatty acid salts described in GB 1435301 (Unilever); these are added preferably in an amount of 0.005 to 0.1% by weight of the active binder i.e. cement in the formulation. The active binder is the cement in a cementiferous composition and/or the calcium silicate produced by reaction of lime or limestone with siliceous materials in the compositions. Other air entrainment agents are usable with the octanoate salt of the present invention. Examples of these agents are salts of vinsol resins (abietic acid salts) ether sulphates, alkyl sulphonates, alkyl aryl sulphonates, salts of fatty acids and amine oxide salts. The additive defined above provides air entrainment which is stable over a period and effective for pulverised fuel ashes having a range of loss on ignition (LOI) values. The latter values measure the loss of water and other volatiles, and in particular carbon, at elevated temperatures. The water soluble C8 fatty acid salts are effective with LOI of from about 1.5% to about 6% by weight. Suitable fatty acid fractions for use in this invention may be obtained as by product fractions from the distillation of vegetable oils, for example coconut or ground nut oils, which contain a proportion of the desired chain length acids. The following experiments illustrate the benefit achieved with the use of the cement additive of the invention. A cementitious composition comprising:- Kg/m³ Ordinary Portland Cement 200 Pulverised Fuel Ash 100 Almington Pit Sand (Grade M) 600 Croxden 20 mm's, Gravel 850 Croxden 10 mm's, Gravel 375 Free Water 175 The composition was formed into concrete using the procedure described in British Standard 5075. The additive comprised 6% of sodium octanoate and 8% sodium decanoate in aqueous solution. The performance of the additive was compared with that of a solution of 14% sodium vinsolate, a material widely used in this application. The air content was measured by the method given in British Standard 5075. That is four sets of experiments were conducted using pulverised fuel ashes with varying levels of carbon content (loss on ignition). For each set of experiments both the additive and sodium vinsolate were used to produce air entrained concretes. The stability of the air in the concrete was then measured before and after vigorous mixing. The objective was to introduce an air entrainment of about 6% V/V. In all cases, the air void system produced by the additive was markedly superior to that produced by sodium vinsolate in that the retained air was more stable and thus the rate of air loss was lower with the additive of the invention. The additive was dosed as mls per 50 Kg cement. EXPERIMENT 1 PULVERISED FUEL ASH, SOURCE 1 NOMINAL L.O.I ADMIXTURE DOSE (mls/50 Kg) AIR CONTENT (% V.V) INITIAL ADDITIONAL MIXING 2 MINS MIXING 4 MINS MIXING Low The additive 100 7.5 7.5 7.3 Low Vinsol Resin Type 80 5.6 4.7 3.9 EXPERIMENT 2 PULVERISED FUEL ASH, SOURCE 2 NOMINAL L.O.I ADMIXTURE DOSE (mls/50 Kg) AIR CONTENT (% V.V) INITIAL ADDITIONAL MIXING 2 MINS MIXING 4 MINS MIXING Medium The additive 50 6.0 6.0 6.0 Medium Vinsol Resin Type 40 6.0 4.5 3.6 EXPERIMENT 3 PULVERISED FUEL ASH, SOURCE 3 NOMINAL L.O.I ADMIXTURE DOSE (mls/50 Kg) AIR CONTENT (% V.V) INITIAL ADDITIONAL MIXING 2 MINS MIXING 4 MINS MIXING High The additive 100 7.5 7.6 7.3 High Vinsol Resin Type 100 6.6 4.6 3.7 EXPERIMENT 4 PULVERISED FUEL ASH, SOURCE 4 NOMINAL L.O.I ADMIXTURE DOSE (mls/50 Kg) AIR CONTENT (% V.V) INITIAL ADDITIONAL MIXING 2 MINS MIXING 4 MINS MIXING High The additive 250 6.8 6.2 6.1 High Vinsol Resin Type 200 6.1 2.8 1.7 EXPERIMENT 5 A cement additive composition prepared from: C8/C10 fatty acids (60/40%w/w) 15% bywt Sodium hydroxide solution (100°Tw) 8.5% Tetralon A (a surfactant) 1.0% Water Remainder was tested for air entrainment using a pulverised fuel ash containing 5.7% carbon (LO1). This additive composition gave 4.7% air entrainment while the use of 6% C8 fatty acid and 6% C10 fatty acid (i.e. 12% w/w of a 50:50 mixture) gave 3.4% air entrainment. Thus the benefit of using C8 fatty acid salt is clearly demonstrated. The C8 fatty acid alone gave no air entrainment and the C10 acid alone gave a value (2.0%) below that required by the British Standard (4.5 ± 1.5%)

Claims: A cement composition comprising (i)up to 65 % by weight of pulverised fuel ash having a carbon content (ii) an air entrainment agent and (iii) an amount of a water soluble C8 fatty acid salt effective to negate the surface activity of the carbon content of the fuel ash. A cement composition according to claim 1 wherein the pulverised fuel ash has a loss on ignition up to about 12%. A cement composition according to any preceding claim wherein the air entrainment is selected from water soluble C9/C10 fatty acid salts, abietic acid salts, ether sulphates, alkyl sulphonates, alkyl aryl sulphonates and amine oxide salts. A cement composition according to any preceding claim wherein the water soluble C8 fatty acid salt is not above about 0.1% by weight of cement present. Use of a compound selected from water soluble C9/C10 fatty acid salts, abietic acid salts, ether sulphates, alkyl sulphonates, alkyl aryl sulphonates and amine oxide salts as an air entrainment agent in a cement composition comprising (i) pulverised fuel ash having a carbon content and (ii) an amount of a water soluble C8 fatty acid salt effective to negate the surface activity of the carbon content of the fuel ash.

Inventors: HOARTY JOHN TERRENCE, HODGKINSON LESLIE, WADDICOR MICHAEL JOSEPH, HOARTY, JOHN TERRENCE, HODGKINSON, LESLIE, WADDICOR, MICHAEL JOSEPH
Applicants: UNILEVER NV, UNILEVER PLC, UNILEVER N.V.
Application year: 1989
Main classification: C04B24
IPC codes: C04B24, C04B38, C04B28