A process for the homo- or copolymerization of alpha-olefin, and a catalyst system used in the process

Abstract: The polymerization of alpha-olefins in a gas phase involves the problem of agglomeration of the product into particles disadvantageous from the viewpoint of its handl­ ing. In the present invention this problem has been solved by means of a new type of process for the homo- or copoly­ merization of alpha-olefins. In the process the catalyst system is pretreated by contacting and reacting a transi­ tion-metal compound which is solid or on a solid carrier with an organoaluminum compound, and possibly an electron donor, in a liquid medium, and by drying the thus formed reaction product to produce a solid catalyst system. The thus pretreated solid and active catalyst system is then fed together with an alpha-olefin in the gaseous state into a gas-phase reactor, and polymerization is carried out by contacting them with each other. By feeding a dry and ac­ tive catalyst system into the gas-phase reactor, it is possible to avoid the agglomeration of the product which occurs in conventional processes in which an organoaluminum compound and possibly an electron donor are fed in a liquid medium into the reactor.

Description: The invention relates to a process for the homo- or copolymerization of alpha-olefin by pretreating the catalyst-system components, which comprise a transition-metal compound on a solid carrier, an organo-aluminum compound in a liquid medium, and an external electron donor, i.e. titanium tetrachloride on a magnesium chloride carrier and a trialkyl aluminium compound by feeding the pretreated catalyst system and a gaseous-state alpha-olefin with its possible comonomers into a gas-phase reactor, and by contacting them with each other in order to produce a homo- or copolymer of the alpha-olefin. The invention also relates to a catalyst system intended for the above process and comprising a transition-metal compound, an organoaluminum compound and an electron donor, as referred to above, It is known in the art to polymerize or copolymerize alpha-olefins by using coordination catalysts, of which the most usable are the so-called Ziegler-Natta catalysts. Ziegler-Natta catalysts are made up of a transition-metal compound, which is preferably deposited on a carrier and the metal of which belongs to groups IV-VI of the Periodic Table an organometallic compound the metal of which belongs to groups I-III of the Periodic Table, and often an electron donor compound which both activates the catalyst and enhances its stereospecificity. An especially effective and selective Ziegler-Natta catalyst is a catalyst system which is formed by combining a solid catalyst comprising atitanium compound and a magnesium compound carrier with an organoaluminum cocatalyst which activates it. Usable technology in the art is represented by the polymerization of alpha-olefins, carried out in a gas phase. It is carried out by feeding the gaseous reaction components needed in the polymerization into a gas-phase reactor in which non-gaseous catalyzing components are fluidized by means of a gas flow. Thereupon the monomer in the gaseous state adheres to the active centers produced by the catalyst system and is polymerized, forming a polymer powder or polymer granulate which is suitable with respect to both its working and handling properties. The normal procedure is that a solid catalyst comprising a magnesium carrier and a transition-metal compound, and a donor and an organometallic compound acting as a cocatalyst, are fed separately into a polymerization reactor, in which they are complexed. The solid catalyst is in this case fed into the reactor dry in an inert gas flow, whereas the cocatalyst and the possible donor are fed into the reactor separately in a liquid medium. However, a method such as this has the disadvantage that in the reactor the liquid medium with the cocatalyst and donor causes the polymer product to agglomerate, forming too large particles of the powder. Attempts have been made to solve the problems due to the separate feeding in of the cocatalyst and donor in a liquid phase, for example, by combining the various components of the catalyst system in advance by means of prepolymerization. U.S. Patent 4,543,389 discloses the preparation of a shockproof ethylene propylene copolymer by first carrying out a prepolymerization with propylene and a conventional Ziegler-Natta catalyst, whereafter a second prepolymerization is carried out in which a solid catalyst, a cocatalyst and a donor are combined by polymerizing C 5 -C 9 -alpha-olefin. Thereafter the last-mentioned C 5 -C 9 -prepoly-olefin mixture, which is in the liquid state, is injected simultaneously with the first-mentioned propylene prepolymer into a polymerization reactor, which contains ethylene and propylene monomer in a gas phase. Thereupon the said solution coats the particles of the polypropylene powder, and thereafter the desired ethylene propylene copolymer grows from the active centers which are on the surface of the coated homopolypropylene particles. Although this state-of-the-art publication states that the small solid catalyst particles prevent "gel" formation, the publication has not, however, taken into account the deleterious agglomerating effect which is produced when a prepolymerized solid catalyst is fed in the form of a liquid mixture or a solution into the reactor. U.S. Patents 4,511,703 and 4,673,662 disclose similar processes for bringing a solid catalyst, a cocatalyst and an electron donor together and for stabilizing them before a polymerization which is carried out in a gas phase. The patents suggest, for example, that the catalyst complex is formed by mixing together the solid catalyst and the cocatalyst, whereafter the obtained "catalyst complex" is coated by means of prepolymerization. Such a procedure is presented, for example, in example 20 of the publications. Examples 21 and 22 show, however, that the catalyst system coated with a prepolymer does not alone suffice for the polymerization or copolymerization of alpha-olefins; it is also necessary to feed into the fluid-bed reactor a tri-n-octyl aluminum cocatalyst and a methyl paratoluate electron donor in an n-hexane solution. Since it is exactly this step that causes agglomeration, the said publications have not in a satisfactory manner solved the problems associated with the agglomeration of the product. U.S. Patent 4,520,163 also discloses the preparation of a prepolymer, but ultimately, however, there is added into the gas phase reactor zone a triethyl aluminum cocatalyst which is precisely the cause of agglomeration of the produced polymer product. The present invention provides a process and a catalyst system for the homo- or copolymerization of alpha-olefins, avoiding the adherence and agglomeration due to liquid components. The process of the invention for the homo- or co-polymerization of an alpha-olefin comprises (a) contacting titanium tetrachloride which has been deposited on a solid magnesium chloride carrier with a hydrocarbon solution of a trialkyl aluminium compound and an external electron donor, the molar ratio of the trialkyl aluminum compound to titanium tetrachloride calculated as metal being within the range 10:1 to 500:1 to form a reaction product, (b) recovering the reaction product from (a) by evaporating liquid medium to produce a dry, solid and active catalyst system, (c) feeding the catalyst system and a gaseous-state alpha-olefin and optional comonomer into a gas-phase reactor, and (d) contacting the catalyst system and alpha-olefin with each other in order to produce an alpha-olefin homo- or copolymer. The process of the invention avoids the agglomeration of the polymerization product by complexing the cocatalyst, and possibly a donor, with a solid catalyst and drying the complex to produce a solid catalyst system before it is fed into the reactor. It has thus been realized that the prepolymerization coatings of the catalyst system are not necessary for keeping the components together and for maintaining their activity. The process according to the present invention may, however, be combined with prepolymerization when this is necessary, for example, in order to produce a polymer powder of a suitable type. The process according to the invention for the homo- or copolymerization of alpha-olefins begins with a stage in which the components of the catalyst system are pretreated. The components comprise titanium tetrachloride on a solid magnesium chloride carrier and a hydrocarbon solution of a trialkyl aluminium compound and an external electron donor. In the pretreatment, the titanium tetrachloride, the trialkyl aluminium compound and the external electron donor are first contacted and reacted with each other, and then the reaction product is dried (i.e. the liquid medium is removed) to produce a solid and active catalyst system. It is assumed that the reaction taking place in the pretreatment leads to a complex formed by the transition-metal compound, the organometallic compound and the electron donor; when dried, the complex forms the said solid, relatively stable and catalytically active catalyst system. The pretreated catalyst system is then fed together with gaseous-state alpha-olefin and possible comonomers into a gas-phase reactor, in which the catalyst system and the monomer(s) are contacted with each other and the aipha-olefin with its possible comonomers polymerizes without the polymer particles becoming agglomerated. The solid catalyst component used in the process or catalyst system according to the invention is titanium tetrachloride on a solid MgCl 2 carrier. When necessary, it is also possible to use other catalytically active transition-metal compounds together with the above-mentioned titanium chloride. The solid carrier compound is MgCl 2 , which has recently become the most important carrier compound for isospecific catalysts. The carrier is preferably treated, for example ground, modified or synthesized, in such a manner that the solid catalyst formed from it has a morphology suitable in terms of activity and stereospecificity. The carrier is activated with titanium chloride in a manner known per se by depositing the titanium tetrachloride compound once or several times on the carrier surface. Thereby a solid catalyst is formed which is capable of reacting with the cocatalyst and of forming an active and stereospecific catalyst system. The cocatalyst is a trialkyl aluminum which is capable of forming an active and preferably stereospecific reaction product with the solid catalyst. The catalyst system, in addition to the solid catalyst component and the cocatalyst component, also contains an external electron donor component. It is selected from among electron donors mentioned in the state of the art and is capable of reacting with the other components mentioned above to form a solid and active product. The electron donor is a so-called external electron donor, which is added in the said manner together with the cocatalyst. The process and catalyst system according to the invention is suitable especially for the gas-phase polymerization and copolymerization of those alpha-olefins in which there occurs agglomeration of the forming polymer product. Such polymerizations include the processes for the preparation of ethylene propylene copolymers mentioned in the state of the art and other processes for the homo- or copolymerization of alpha-olefins. The process and the catalyst system are especially well suited for the polymerization of monomers which contain more than three carbon atoms, because in that case the product is a stereospecific polymer having a high isotactic index. Preferably, the α-olefin is 1-butene. According to the invention, titanium tetrachloride on a solid MgCl 2 carrier is mixed together with a hydrocarbon solution of a trialkyl aluminum compound and of an external electron donor such as a silane compound, preferably diphenyl dimethoxysilane, whereupon the said components are complexed. It is advantageous to use a hydrocarbon solution in which the molar ratio of the organoaluminum compound to the electron donor is within the range 0.5:1-40:1, preferably approximately 15:1. The amount of the solution is such that the molar ratio of the erganoaluminum compound to titanium is in the range 10-500, preferably approximately 200. The mixing temperature is by no means critical; it may be, for example, room temperature. After the mixing, the mixture is transferred into a tank, from which the hydrocarbon solution is evaporated for example by heating and/or evacuating to the boiling point, whereby a dry catalyst complex is formed. The complex is surprisingly active and stereospecific. The dry, active catalyst component is as such usable as a polymerization catalyst, or it may be coated by prepolymerizing a monomer, such as C 3 -C 10 -alpha-olefin, on its surface, for example by a prepolymerization process known per se The polymerization is preferably carried out by feeding the dried active catalyst complex as such in an inert gas flow into the polymerization reactor. By directing into the dry, preferably fluidized catalyst complex in the reactor a gaseous monomer at a predetermined pressure and temperature and for a predetermined period, the monomer can be polymerized without the forming product agglomerating into particles larger than desired. The catalyst system according to the invention stores relatively well when stored in nitrogen gas, although its stereospecificity will somewhat deteriorate. It can, however, be said that the catalyst system according to the invention does not involve the disadvantage that it should be prepared directly in connection with the polymerization. A few embodiment examples are presented below, the purpose being to illustrate the process and catalyst system according to the invention. Example 1 Approximately 50 mg of a solid titanium tetrachloride catalyst on a magnesium chloride carrier was mixed with a pentane solution of tri-isobutyl aluminum and diphenyl dimethoxysilane, the molar ratio of the aluminum compound to the silane compound in the solution being approximately 20:1. The amount of the solution was such that the molar ratio of the aluminum compound to titanium was approximately 200. The mixture was fed into an autoclave, where the pentane was evaporated out, and a dry and active catalyst compound was obtained. The dried complex was then contacted with 1-butene vapor at a temperature of 55 °C and a pressure of 5 bar for 4 hours, the hydrogen pressure in the gas-phase reactor being 0.2 bar. The obtained polymer was dried, weighed and analyzed. The results of the analysis are given in Table 1. Example 2 Example 2 was carried out in the same manner as Example 1, but the dried complex was allowed to mature in a nitrogen atmosphere for 2 hours before the monomer was fed into the reactor. Examples 3 and 4 Examples 3 and 4 were carried out in the same manner as Example 1, but the dried complex was allowed to mature in a nitrogen atmosphere for 4 hours before the monomer was fed into the reactor. Example 5 This example was carried out in the same manner as Example 1, but the dried complex was allowed to mature in a nitrogen atmosphere for 8 hours before the monomer was fed into the reactor. Example 6 Example 6 was carried out in the same manner as Example 1, but the dried complex was allowed to mature in a nitrogen atmosphere for 16 hours before the monomer was fed into the reactor. Example 7 This example was carried out in the same manner as Example 1, but the dried complex was allowed to mature in a nitrogen atmosphere for 67 hours before the monomer was fed into the reactor. Examples 8 and 9 These examples were carried out in the same manner as Example 1, but the catalyst was coated by prepolymerizing the propylene in such a manner that the catalyst contained approximately 2.4 g of polypropylene/g of the solid component. Example 10 Example 10 was carried out in the same manner as Example 8, but the dried complex was allowed to mature in a nitrogen atmosphere for 2 hours before the monomer was fed into the reactor. Example 11 This example was carried out in the same manner as Example 8, but the dried complex was allowed to mature in a nitrogen atmosphere for 4 hours before the monomer was fed into the reactor. Example 12 This example was carried out in the same manner as Example 8, but the dried complex was allowed to mature in a nitrogen atmosphere for 12 hours before the monomer was added. Example 13 This example was carried out in the same manner as Example 8, but the dried complex was allowed to mature in a nitrogen atmosphere for 22 hours before the monomer was added, Table 1 shows the catalyst activities of the products of the examples, expressed as produced polybutene bulk/g of catalyst calculated as titanium, the melt index and the isotactic index. Example Maturation time, h Productivity kg PB/g Ti Melt index g/min Isotactic index, % 1 0 182 38 94.0 2 2 186 46 89.5 3 4 46 34 - 4 4 70 29 98.0 5 8 125 39 93.2 6 16 123 44 97.5 7 67 151 57 91.7 8 0 93 30 94.5 9 0 100 31 95.1 10 2 52 17 97.9 11 4 81 23 96.3 12 12 80 33 94.8 13 22 124 7 97.7

Claims: A process for the homo- or co-polymerisation of an α-olefin, which comprises: (a) contacting titanium tetrachloride which has been deposited on a solid magnesium chloride carrier with a hydrocarbon solution of a trialkyl aluminium compound and an external electron donor, the molar ratio of the trialkyl aluminium compound to titanium tetrachloride calculated as metal being within the range 10:1 to 500:1, to form a reaction product, (b) recovering the reaction product from (a) by evaporating liquid medium to produce a dry, solid and active catalyst system, (c) feeding the catalyst system and a gaseous-state α-olefin and optional comonomer into a gas-phase reactor, and (d) contacting the catalyst system and α-olefin with each other in order to produce an α-olefin homo-or copolymer. A process according to claim 1, in which the external electron donor is a silane compound, preferably diphenyl dimethoxysilane. A process according to claim 1 or claim 2 in which the molar ratio of the trialkyl aluminium compound to titanium tetrachloride calculated as metal is 200:1. A process according to any one of the preceding claims, in which the molar ratio of the trialkyl aluminium compound to the external electron donor is approximately 0.5:1-40:1, preferably approximately 15:1. A process according to any one of the preceding claims, in which the α-olefin is 1-butene. A catalyst system for the homo- or copolymerisation of an α-olefin, comprising titanium tetrachloride on a solid magnesium chloride carrier, a trialkyl aluminium compound, and an external electron donor, which is obtainable by (a) contacting titanium tetrachloride which has been deposited on a solid magnesium chloride carrier with a hydrocarbon solution of a trialkyl aluminium compound and an external electron donor, the molar ratio of the trialkyl aluminium compound to titanium tetrachloride calculated as metal being within the range 10:1 to 500:1, to form a reaction product, and (b) recovering the reaction product from (a) by evaporating liquid medium to produce a dry, solid and active catalyst system. A catalyst system according to claim 6, in which the molar ratio of the trialkyl aluminium compound to titanium tetrachloride calculated as metal is 200:1. A catalyst system according to claim 6 or 7, in which the molar ratio of the trialkyl aluminium compound to the external electron donor is approximately 0.5:1 to 40:1, preferably approximately 15:1. A catalyst system according to any of claims 6 to 8 in which the external electron donor is diphenyl dimethoxysilane.

Inventors: AHVENAINEN ANTERO, SALMINEN HANNU, SODERBERG TARJA, TERVONEN JARI, AHVENAINEN, ANTERO, SALMINEN, HANNU, SODERBERG, TARJA, TERVONEN, JARI
Applicants: BOREALIS AS, BOREALIS A/S
Application year: 1989
Main classification: C08F10
IPC codes: C08F110, C08F4, C08F10, C08F2