Silicone composition, elastic revolution body and fixing device using the same

Abstract: An addition reaction-type dimethylsilicone composition, including a diorganopolysiloxane containing a reactive vinyl group; an organopoly­ siloxane containing an active hydrogen atom; and silicic acid fine powder of which surface has been treated with a fluoroalkylsilane, an alkylsilane compound, a fluorosilicone oil, a dimethylsilicone oil, or a mixture thereof, and a silane compound containing an unsaturated group having a reactivity to the organopolysiloxane containing an active hydrogen atom.

Description: FIELD OF THE INVENTION AND RELATED ARTS The present invention relates to an addition reaction-type dimethylsilicone composition containing silica fine powder surface-treated with a fluoroalkylsilane, an alkylsilane compound, fluorosilicone, dimethylsilicone oil or a mixture thereof, and a silane compound including an unsaturated group having a reactivity with an addition reaction-type silicone; a dimethylsilicone rubber composition formed from the silicone composition; an elastic revolution body (or body of revolution) including an elastic body having a surface layer formed from the dimethylsilicone rubber composition; and a fixing device including the elastic revolution body. The silicone rubber composition according to the present invention is particularly suitable for an elastic coating material of an elastic revolution body which is used for a conveyor roller for conveying a sheet transfer material (or recording material) or a fixing roller in an image forming apparatus such as electrophotographic copying machine and printer. In an image forming apparatus such as electrophotographic copying machine, conveying ability, releasability and durability are generally required for the conveyer roller for conveying a sheet transfer material (or recording material) in the form of a sheet such as plain paper along a prescribed conveying path. Further, conveying ability, releasability, abrasion resistance, fixing characteristics and durability are also required under severer conditions with respect to a fixing device comprising a fixing roller and a pressure roller, which applies heat to an unfixed toner image formed on a transfer paper under pressure, and must convey the transfer paper to the prescribed conveying path while preventing an offset phenomenon due to sintering or melted toner. Conventionally, the fixing device of this type comprises at least a fixing roller and a pressure roller which contacts the fixing roller under pressure and rotates corresponding to the rotation thereof. The fixing roller comprises a hollow core bar (or cylinder) formed of a metal such as aluminum and iron, and a layer of a material having good releasability such as silicone rubber and fluorine-containing resin including polytetrafluoroethylene, tetrafluoroethylene-fluoroalkoxyethylene copolymer, etc., which covers the core bar. Inside the fixing roller, a heater such as halogen lamp is disposed as desired, thereby to elevate the surface temperature of the fixing roller to a temperature suitable for the fixing. In many cases, the above-mentioned surface temperature of the fixing roller is controlled by means of a sensor so that it is set to a prescribed temperature. Further, around the peripheral surface of the fixing roller, there is sometimes disposed a cleaner for removing the offset toner and paper dust, or a separation claw for preventing a transfer material or image-carrying material from winding about the fixing roller. On the other hand, the pressure roller comprises a core bar formed of a metal such as iron and stainless steel, and an elastic layer having releasability and comprising a material such as silicone rubber, which covers the core bar. The pressure roller is caused to contact the fixing roller under pressure by a pressure-applying means such as spring. The image-supporting material carrying thereon an unfixed toner image is sandwiched between and conveyed by the above-mentioned fixing roller and pressure roller under pressure, whereby the unfixed toner image is fixed to the image-carrying material under pressure, or under heating and pressure. However, when the conventional dimethylsilicone rubber is used for the layer covering the core bar of a fixing roller, the fixing roller covered with the silicone rubber is capable of providing good fixability of an unfixed toner image to an image-carrying material such as plain paper and good image quality of the resultant fixed image (e.g., capable of providing a fixed image having a reduced gloss), but has a problem such that it is inferior to a fixing roller covered with a fluorine-containing resin in releasability and durability. Image forming apparatus such as electrophotographic copying machine tend to employ the fixing roller covered with a silicone rubber which is inferior to that covered with a fluorine-containing resin in releasability and durability but is capable of providing an excellent image quality of a fixed image because the latter is more important to the above-mentioned image forming apparatus. Accordingly, the releasability and durability of a silicone rubber material has been desired to be improved. For example, it is known that silicic acid such as synthetic hydrous silicic acid and synthetic anhydrous silicic acid is added to a silicone rubber material as a reinforcement in order to improve the durability. However, in the case of the synthetic hydrous silicic acid, the reinforcement effect thereof is not substantially achieved unless it is added to a silicone rubber material in a considerable large amount of 20 - 50 wt. parts per 100 wt. parts of the silicone rubber material. Further, such addition causes a problem such that the releasability of the silicone rubber material is considerably decreased. In the case of the synthetic anhydrous silicic acid, somewhat reinforcement effect can be achieved when it is added to a silicone rubber material in a smaller amount (e.g., 10 - 20 wt. parts per 100 wt. parts of the silicone rubber material) than that in the case of the synthetic hydrous silicic acid, but the releasability is also decreased considerably. Accordingly, in either case, it has been difficult to remarkably improve the durability of a silicone rubber material without decreasing the releasability thereof. The US-A-4 196 273 discloses curable organopolysiloxane compositions which comprise dimethoxysiloxane with vinyldimethylsilyl end-groups; copolymer of (Me)₂(CH₂=CH)SiO 0.5 , Me₃SiO 0.5 and SiO₂; methylhydrogenpolysiloxane; fumed silica, surface treated with trimethylchlorosilane and having a surface area of about 200 m²/g; platinum catalyst; and vinylmethoxysilane. The composition is prepared by merely blending these components uniformly. The EP-A-0 062 408 discloses a curable organopolysiloxane composition for heat fixing rolls, the composition comprising a diorganopolysiloxane with a siloxane unit containing a vinyl group; an organopolysiloxane with a siloxane unit containing a hydrogen atom; a siliceous filler such as fumed silica of surface area of 200 m²/g and quartz powder of average paticle size of 5µm; and a platinum group catalyst. SUMMARY OF THE INVENTION An object of the present invention is to provide an addition reaction-type dimethylsilicone composition and an addition reaction-type dimethylsilicone rubber composition which are excellent in mechanical strength and have good releasability. Another object of the present invention is to provide an elastic revolution body which is excellent in mechanical strength and has good releasability. A further object of the present invention is to provide an elastic revolution body which excellent in durability. A still further object of the present invention is to provide fixing device which is excellent in durability I have earnestly researched on a silicone rubber composition excellent in both releasability and durability which may be used as a coating material for an elastic revolution body for conveying a sheet transfer material or recording material such as plain paper and fixing an unfixed toner image to form a fixed image, in an image forming apparatus such as electrophotographic copying machine and printer. On the basis of such study, I have found that a silicone rubber composition having a good balance between reinforcement and releaseability can be obtained by incorporating, in an addition reaction-type dimethylsilicone composition, silica powder (IV) having a BET specific surface area of 40 to 500 m²/g, whose surface has been treated with (or modified by) (IV-1) a fluoroalkylsilane, an alkylsilane compound, fluorosilicone oil, dimethylsilicone oil or a mixture thereof, and (IV-2) a silane compound containing an unsaturated group having a reactivity to an organopolysiloxane containing an active hydrogen atom (II) which is also incorporated into the composition, said unsaturated group of the silane compound (IV-2) being in a form suitable to be introduced onto the surface of the silica powder; and the durability of a fixing roller is remarkably improved by using the above-mentioned silicone rubber composition as a coating layer thereof. The addition reaction-type dimethylsilicone composition according to the present invention is based on the above discovery and comprises: (I) a diorganopolysiloxane containing at least one reactive vinyl group connected to a silicon atom, (II) an organopolysiloxane containing at least one active hydrogen atom connected to a silicon atom, and (IV) silica powder, having a BET specific surface area of 40 to 500 m²/g, whose surface has been treated, prior to the mixing with (I) and (II), with (IV-1) a fluoroalkylsilane, an alkylsilane compound, a fluorosilicone oil, a dimethlysilicone oil, or a mixture thereof, and (IV-2) a silane compound containing an unsaturated group having a reactivity to said organopolysiloxane containing an active hydrogen atom (II), said unsaturated group being in a form suitable to be introduced onto the surface of the silica powder. The present invention also provides a dimethylsilicone rubber composition obtained by heating a platinum-type catalyst; and an addition reaction-type dimethylsilicone composition as specified above. The present invention also provides an elastic revolution body comprising an elastic layer formed from a dimethylsilicone rubber composition; the dimethylsilicone rubber composition being obtained by heating a platinum-type catalyst and an addition reaction-type dimethylsilicone composition as specified above. The present invention further provides a fixing device, comprising at least a pair of rollers between which a toner image-supporting material carrying an unfixed toner image is passed under pressure to fix the toner image to the toner image-supporting material; wherein at least one of the pair of rollers comprises an elastic layer formed from a dimethylsilicone rubber composition; the dimethylsilicone rubber composition being obtained by heating a platinum-type catalyst and an addition reaction-type dimethylsilicone composition as specified above. In the present invention, "silica powder (IV)" means one which is solid at normal or room temperature and also includes a silicic acid compound such as orthosilicic acid. These and other objects, features and advantages of the present invention will become more apparent upon a consideration of the following description of the preferred embodiments of the present invention taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Figures 1 to 3 are graphs showing relationships between the mol.ratio of (active hydrogen)/(vinyl group) and hardness, impact resilience and toner releasability of the silicone rubber composition obtained in Example 3 appearing hereinafter; Figure 4 is a schematic sectional view showing a hot roller-type fixing device for fixing a toner image according to the present invention; and Figures 5 to 7 are graphs showing relationships between the mol.ratio of (active hydrogen)/(vinyl group) and hardness, impact resilience and toner releasability of the silicone rubber composition obtained in Example 9 appearing hereinafter. DETAILED DESCRIPTION OF THE INVENTION The addition reaction-type dimethylsilicone composition according to the present invention comprises, at least, a component (I), a component (II) and a component (IV) as described below, and may further compirses a component (III) as described below. Examples of the organopolysiloxane component (I) containing a reactive vinyl group connected to a silicon atom may include: an organopolysiloxane such as a reactive vinyl group-containing dimethylpolysiloxane having a vinyl group at the end thereof, which is represented by the following general formula: or a diorganopolysiloxane such as a reactive vinyl group-containing dimethylpolysiloxane having a methyl group at the end thereof and having a vinyl group in the side chain thereof, which is represented by the following general formula: or wherein m and k respectively denote 0 or a positive integer, (m+k) may preferably be 50 - 2,000, and n may preferably be an integer of 1 - 10; or a vinyl group-containing dimethylpolysiloxane comprising two or more species of the above-mentioned polysiloxane, and l may preferably be 50 - 2,000. The component (I) may preferably have a viscosity of 500 - 5x10⁶ centistoke at room temperature. In the above formulas, l , m and n respectively denote a positive integer. Another example of the component (I) may include an organopolysiloxane copolymer (a) which includes an organosiloxane unit represented by and a fluoroalkyl group-containing organosiloxane unit represented by and has a vinyl group at the end of its molecular chain. R¹ and R² used herein respectively denote an alkyl group (preferably having 1 - 3 carbon atoms) such as methyl, ethyl, and propyl. The organopolysiloxane copolymer (a) may preferably contain the CF₃CH₂CH₂(CH₃)SiO- unit in an amount of 10 - 60 mol. %, more preferably 20 - 40 mol. %. The active hydrogen-containing organopolysiloxane component (II) may for example be a methylhydrogenpolysiloxane represented by the following general formulas: wherein p and r denotes 0 or a positive integer, and q denotes a positive integer. (p+q) may preferably be 50 - 500, and q may preferably be an integer of 1 - 10. This organopolysiloxane, contains at least one active hydrogen atom connected (or bonded) to a silicon atom (-Si-H) per unit molecule. Another example of the component (II) may be one which includes at least one hydrogen atom connected to a silicon atom, on the average, per one molecule, and includes an organosiloxane unit represented by and an organosiloxane unit represented by R³ and R⁴ used herein respectively denote an alkyl group (preferably having 1 - 3 carbon atoms) such as methyl, ethyl, and propyl. Such a component (II) may for example have the following formula: wherein p , q and r are as denoted above and x denotes a positive integer, except that p and r cannot be simultaneously zero. The component (III) used in the present invention is a platinum-type catalyst such as platinum and a platinum compound. The platinum-type catalyst component (III) is one which is effective in catalyzing a reaction between an active hydrogen connected to a silicon atom, and a vinyl group. An optimum addition amount of the catalyst may be determined in consideration of a length of pot-life, but may preferably be 100 - 5,000 ppm. Specific examples of the surface-treated silica fine powder component (IV) may include surface-modified silica powder, having a BET specific surface area of 40-500 m²/g, obtained by treating the surface of silica powder such as synthetic anhydrous silica powder and synthetic hydrous silica powder, with (IV-1) fluoroalkylsilane, an alkylsilane compound, fluorosilicone, dimethylsilicone oil, or a mixture thereof, and (IV-2) a silane compound having an unsaturated group which has a reactivity to an active hydrogen-containing organopolysiloxane (II), said unsaturated group being in a form suitable to be introduced onto the surface of the silica powder. The addition reaction-type dimethylsilicone rubber composition according to the present invention is a hardenable (or curable) composition comprising a homogeneous mixture of the above-mentioned silicone composition. Each of the components (I), (II) and (III) per se constituting the composition may be one which is known as that constituting a liquid addition reaction-type dimethylsilicone composition. The vinyl group connected to a silicon atom in the component (I) (-Si-CH=CH₂ group) and the hydrogen atom connected to a silicon atom in the component (II) (-Si-H group) initiate an addition reaction when they are heated in the presence of the platinum-type catalyst (ordinarily, at a temperature of 100 - 180 °C for 0.5 to 20 min.), whereby the silicone composition becomes a silicone rubber composition, i.e., a rubber-like elastic material. In the present invention, the unsaturated group of the treated silica fine powder (IV) constituting the composition according to the present invention reacts with the hydrogen atom connected to a silicon atom of the component (II) and forms a chemical bond. As a result, a desired mechanical strength, which has not been obtained in the prior art until a large amount of synthetic silicic acid is used, may be obtained by adding a relatively small amount of the component (IV). Further, the increase in the surface energy due to the addition of a large amount of filler such as synthetic silicic acid can be prevented or suppressed. Specific examples of the silica powder used in the present invention may include: white ultra-fine powder (or superfines) commonly called "white carbon", such as anhydrous silicic acid (SiO₂ · nH₂O; SiO₂ content = 95 % or higher), hydrous silic acid (SiO₂ · nH₂O; SiO₂ content = 80 - 95 %), hydrous calcium silicate (xSiO₂ · CaO · yH₂O, SiO₂ content = 55 - 70 %), and hydrous aluminum silicate (xSiO₂ · Al₂O₃ · yH₂; SiO₂ content = 60 - 70 %). In the present invention, silica powder having a BET specific surface area of 40 - 500 m²/g is used. The silica powder preferably has a primary particle size of 7 - 100 nm (milli-micron). Further, as the silica powder, hydrous silicic acid or anhydrous silicic acid having a primary particle size of 5 - 50 nm (more preferably 7 - 25 nm) and a BET specific surface area of 70 - 400 m²/g (more preferably 100 - 300 m²/g) may more preferably be used. Specific examples of the surface-treating agent (IV-1) may include: fluoroalkylsilanes represented by C n F 2n+1 CH₂CH₂SiR m (OR') 3-m , or C n F 2n+1 CH₂CH₂SiR m Cl 3-m wherein n denotes an integer of 1 - 8, m denotes 0 or 1, and R and R' respectively denote methyl or ethyl group; alkysilanes such as trimethylmethoxysilane, trimethylethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, methyltrimethoxysilane, methyltriethosysilane, trimethylchlorosilane, dimethyldichlorosilane, methyltrichlorosilane, and hexamethyldisilazane; fluorosilicone oil; and diemthylsilicone oil. Further specific examples of a reactive unsaturated group-containing silane (IV-2) may include: vinylsilanes such as vinyltriethoxysilane, dimethylvinylmethoxysilane, dimethylvinylethoxysilane, methylvinyldimethoxysilane, methylvinyldiethoxysilane, vinyltrichlorosilane, dimethylvinylchlorosilane, and methylvinyldichlorosilane; and silane compounds having a methacryloxypropyl group such as γ-metharyloxypropyltrimethoxysilane, and γ-methacryloxypropylmethyldimethoxysilane. The surface of the silica powder may be treated with the above-mentioned treating agent in a known treating process. In order to enhance the releasability and the wettability with the components (I) and (II), a treating agent (IV-1) comprising fluoroalkylsilane, alkylsilane, fluorosilicone oil, or dimethylsilicone oil or a mixture thereof may preferably be used for treatment in an amount of 1 - 30 wt. parts, more preferably 3 - 25 wt. parts, per 100 wt. parts of silica powder. When the fluoroalkylsilane, or alkylsilane is used, in view of the specific surface area, 30 - 90 %, more preferably 40 - 80 % of the surface area of the silica powder may preferably be covered with the treating agent. In other words, when the amount of total silanol groups present at the surface of the silica powder is represented by 100 %, 30 - 90 % (or 40 - 80 %) of the silanol groups may preferably react with the silane compound. In view of the reinforcement of the silicone rubber composition, 100 wt. parts of silica powder may preferably be coated with 1 - 30 wt. parts, more preferably 5 - 25 wt. parts of an unsaturated group-containing silane (IV-2). In view of the specific surface area, 10 - 60 % (more preferably 20 - 60 %, particularly preferably 30 - 50 %) of the surface area of the silica powder may preferably be covered with the treating agent (IV-2). In view of both releasability and reinforcement, the surface-treated synthetic silica powder may preferably added in an amount of 5 - 30 wt. parts, more preferably 5 - 20 wt. parts particularly, 6 - 15 wt. parts per 100 wt. parts of the components (I), (II) and (III) in total. When a considerable amount of unreacted reactive groups remain in the cured product, they may impair the releasability. Accordingly, the mol ratio of (hydrogen atom connected to silicon atom)/(unsaturated group) may preferably be adjusted to 0.6 - 1.5, more preferably 0.8 - 1.2, before the reaction. When the above-mentioned mol ratio is about 1.0 (e.g., 0.95 - 1.05), i.e., these numbers of moles are substantially equal to each other, the mechanical strength, hardness, impact resilience and releasability become particularly good. The composition according to the present invention may further contain a colorant, a heat-resistance improver, a permanent compression set-improver, and/or a thioxatropic agent. The silicone rubber composition according to the present invention shows much better releasability and durability as compared with the conventional silicone rubber material which has been used as a coating material for a heat fixing roller in an electrophotographic copying machine. The reason for this is not necessarily clear, but may be considered that, since an unreacted component does not substantially remain in the cured silicone rubber product, the mechanical strength and viscoelasticity characteristic are improved, the surface energy increase of the cured product is prevented or suppressed, and further the adsorption of a toner to the cured product surface, which may be attributable to the presence of the unreacted component, is obviated. However, such an explanation should not limit the present invention at all. A fluorosilicone rubber mainly formed from an organopolysiloxane containing a fluorine atom and a reactive vinyl group, and/or an organopolysiloxane containing a fluorine atom and an active hydrogen atom (i.e., a hydrogen atom connected to an Si atom), has a lower surface energy than that of dimethylsilicone rubber, whereby the releasability is further improved. Ordinarily, for the purpose of reinforcement, 5 - 30 wt. parts of silica powder may be added to 100 wt. parts of silicone rubber, but the releasability decreases as the addition amount of the silica powder increases. However, in the silica powder (IV) used in the present invention of which surface has been modified by a reactive group-containing treating agent, the surface of the fine powder has been treated with a low-surface energy material (IV-1) such as fluoroalkylsilane, alkylsilane, fluorosilicone oil, and dimethylsilicone oil, whereby the surface energy increase in the silicone rubber composition may be suppressed. Further, since the silica powder (IV) is treated with an unsaturated group-containing silane (IV-2), a reactive group is introduced into the surface of synthetic silicic acid, and the reactive group may react with a hydrogen atom connected to a silicon atom of the component (II) (e.g., to cause a crosslinking reaction), whereby the mechanical strength may be enhanced simultaneously. Accordingly, the silicone rubber composition according to the present invention may provide a coating material for a roller for heating and pressure fixing to be used in an electrophotographic copying machine, etc., which is excellent in releasability, strength and durability. The composition according to the present invention may be prepared by simply mixing the respective components (I), (II), (IV) and, optionally, (III). However, in a preferred embodiment of the present invention, an A -liquid comprising the components (I), (III) and (IV), and a B -liquid comprising the components (II) and (IV); or an A -liquid comprising the components (I), (III) and (IV), and B -liquid comprising the components (I), (II) and (IV) are separately prepared, and the two components of the thus prepared A -liquid and B -liquid are mixed at a prescribed mixing ratio when the resultant composition is converted into a cured product. Such an embodiment is most advantageous in view of convenience. In such an embodiment, the three componentns of the unsaturated group-containing component, -Si-H group-containing component, and platinum-type catalyst must not be included in the same package, in order to prevent a reaction from gradually progressing at room temperature. In the present invention, it is preferred to regulate the amounts of the components (I), (II) and (IV) to be mixed so that the total amount of the unsaturated groups contained in the components (I) and (IV) is substantially equal to the amount of the hydrogen atom connected to the silicon atom of the component (II), i.e., the mol ratio therebetween is 0.95 - 1.05. The addition reaction-type dimethylsilicone rubber composition is suitably used for an elastic coating material of an elastic revolution body which is used for conveying a sheet transfer material such as plain paper or plastic sheet, and/or for fixing an unfixed toner image to form a permanent image in various image forming apparatus such as electrophotographic copying machine and printer. Hereinbelow, the elastic revolution body and fixing device according to the present invention are described. The elastic revolution body according to the present invention comprises a substrate and an elastic (or elastomeric) coating layer. The substrate may preferably be a pipe or bar (preferably having a diameter of 5 - 100 mm) comprising a metal such as aluminum, iron and stainless steel. The elastic coating layer may preferably have a thickness of 0.1 - 10 mm. Figure 4 is a schematic side sectional view showing an embodiment of the fixing device according to the present invention. Referring to Figure 4, a heat roller (hereinafter, referred to as "fixing roller") 1 and a pressure roller 2 are disposed so that they contact each other under an appropriate pressure, and are supported by bearings (not shown) so that they are disposed in upper and lower positions in parallel with each other. Each of these rollers 1 and 2 is rotated in the direction of an arrow shown in the figure. The fixing roller 1 comprises a core of a hollow roller 11 formed of a metal such as aluminum, of which peripheral surface is covered with an elastic coating layer 12 comprising the addition reaction-type dimethylsilicone composition according to the present invention. A heater 13 such as halogen heater bar is disposed in the inner space of the core 11, and the core 11 is heated by heat generation due to the heater 13. The current applied to the heater 13 is controlled on and off, or the amount of the current is controlled by an automatic temperature control means (not shown), whereby the temperature of the outer peripheral surface is always controlled at a prescribed constant temperature. The pressure roller 2 comprises a core 21 of a metal roller comprising iron, aluminum, etc., and a relatively thick layer 22 of an elastic material such as rubber covering the outer peripheral surface of the core 21. "Relatively thick" layer 22 means that layer 22 is thicker than layer 12 of the fixing roller 1. The addition reaction-type demethylsilicone rubber composition according to the present invention can be used for the elastic material layer 22. The fixing device shown in Figure 4 further comprises a device 3 for applying a releasing aid or assistant such as dimethylsilicone oil onto the outer peripheral surface of the fixing roller 1. The application device 3 used in this embodiment comprises a continuous web member 31, a feed shaft 32, a wind-up shaft 33 and a pressing roller 34. The web member 31 is preliminarily impregnated with a releasing aid having a considerably high viscosity of, e.g., about 10,000 mPa·s 10,000 cs) at 25°C, is formed into a roll, and is loaded on the feed shaft 32. The free end of the roll web member 31 is hooked on the wind-up shaft 33 and the intermediate portion thereof disposed between the feed shaft 32 and wind-up shaft 33 is pressed to the surface of the fixing roller 1 by means of the pressing roller 34. The roll web member 31 on the feed shaft 32 side is gradually wound around the wind-up shaft 33, whereby the releasing aid which has soaked into the web member 31 is applied onto the outer peripheral surface of the fixing roller 1. The web member 31 may also function as a cleaning member for cleaning the outer surface of the fixing roller 1. Under a condition under which the above-mentioned fixing roller 1 and pressure roller 2 are rotated, an image-supporting material 5 such as transfer material, electro-fax paper and electrostatic printing paper on which an unfixed toner image T has been formed and carried by an image-forming mechanism (not shown) such as electrophotography and electrostatic recording, is introduced into and passed through a nip portion 4 disposed between the above-mentioned two rollers so that the toner image-carrying surface of the image-supporting material 5 contacts the fixing roller 1. As a result, the toner image T is sequentially fixed onto the image-supporting material 5 under heat due to the fixing roller 1 and pressing force due to the fixing roller 1 and pressure roller 2 contacting each other, whereby a permanent fixed image is formed on the image-supporting material 5. In Figure 4, there are also disposed a separation claw member 6 for surely separating the image-supporting material 5 from the surface of the fixing roller 1, and a sensor 7 for detecting the temperature of the outer peripheral surface of the fixing roller 1 to regulate the temperature thereof. In Figure 4, W denotes the width (in the moving direction of the image-supporting material 5) of the contact portion at which the fixing roller 1 and pressure roller 2 contact each other. The layer 12 of a releasing material 12 covering the peripheral surface of the core 11 of the fixing roller 1 may generally be caused to have a considerably small thickness (e.g., about 0.5 mm or smaller), in order to rapidly supply heat due to the heater 13 to the outer surface of the above-mentioned layer 12 (i.e., the outer peripheral surface of the fixing roller 1) by heat conduction. When the addition reaction-type dimethylsilicone rubber composition according to the present invention is used for the coating layer 12 of the fixing roller 1, since the cured product of the composition is an elastic material, the outer surface of the elastic coating layer 12 is deformed faithfully corresponding to the surface unevenness of the supporting material 5 per se and the unevenness of the toner image T disposed on the supporting material 5, whereby the outer surface uniformly contacts the respective portions of the uneven toner image T. Accordingly, the fixability of the toner image T to the surface of the image-supporting material 5 is entirely improved and the resultant fixed image entirely becomes good (i.e., the image quality of the fixed image is enhanced). As a result, the deformation or distortion of an image, gloss, and toner scattering, which have occurred when a rigid coating layer is used, is reduced or obviated. Hereinbelow, the present invention is described in more detail with reference to Examples. Example 1 A silicone composition according to the present invention was prepared by using the following components (I), (II) and (IV) as main components. Component (I) : An organopolysiloxane copolymer comprising about 80 mol % of a diorganosiloxane unit represented by (CH₃)₂SiO, and 20 mol % of an organosiloxane comprising a 3,3,3-trifluoropropyl group represented by CF₃CH₂CH₂(CH₃)SiO, and having vinyl groups at both ends of the molecular chain, wherein the CF₃CH₂CH₂(CH₃)SiO content was 20 mol %, and the ends of the molecular chiain were blocked by the vinyl groups. The component (I) used herein heat a viscosity of about 1,000 mPa·s (1,000 centistoke) at room temperature. Component (II): An organopolysiloxane copolymer containing a hydrogen atom connected to a silicon atom, which comprise a diorganosiloxane unit represented by (CH₃)₂SiO and an organosiloxane unit represented by CF₃CH₂CH₂(CH₃)SiO, and containing more than one hydrogen atom connected to a silicon atom on an average per one molecule. Component (IV): A surface-modified synthetic hydrous silicic acid containing a reactive group, which had been modified by a fluoroalkylsilane and a vinyl group-containing silane. The above-mentioned Component (IV) was prepared in the following manner. 100 g of synthetic hydrous silicic acid (trade name: Nipsil N 300A, mfd. by Nihon Silica K.K.) having a particle size of 0.1 - 7 microns and a BET specific surface area of 170 m²/g was charged into a mixer. While the silicic acid was forcibly stirred by means of the mixer, 12 g of vinyltriethoxysilane was added thereto by spraying by use of N₂ gas, 12 g of 3,3,3-trifluoropropyltrimethoxysilane was added in the same manner as described above, and the resultant mixture was subjected to heat treatment at 100 °C for one hour under stirring, whereby the above-mentioned modified silicic acid was prepared. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 5 wt. parts Constituent (iii) : A platinum-type catalyst component (III) 0.001 wt. part Constituent (iv): A surface-modified synthetic hydrous silicic acid of the Component (IV) modified by 3,3,3-trifluoropropyltrimethoxysilane and vinyltriethoxysilane, wherein the number of the vinyl group was 3.8x10²⁰ groups/g 10 wt. parts Constituent (v) : Iron oxide (red iron oxide) 5 wt. parts The above-mentioned Constituents (i), (ii), (iii), (iv) and (v) were those constituting a composition according to the present invention, which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom (12.3x10⁻³ mol per 5 g of the Component (II)), i.e., the mol ratio therebetween was 1.0. The respective constituents were packed in the following manner so as to prepare a two-pack (or two-component) type of formulation. A-liquid Constituent (i) 52.5 wt. parts Constituent (iii) 0.001 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 47.5 wt. parts Constituent (ii) 5 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body was obtained. Example 2 Modified synthetic hydrous silicic acid as a Component (IV) was prepared in the following manner. 100 g of synthetic hydrous silicic acid (trade name: Nipsil SS 30P, mfd. by Nihon Silica K.K.) having a particle size of 8.6 microns and a specific surface area of 114 m²/g of which surface had been treated with about 9 wt. % of dimethylsilicone oil to be imparted with hydrophobicity, was charged into a mixer. While the silicic acid was forcibly stirred by means of the mixer, 12 g of vinyltriethoxysilane was added thereto by spraying by use of N₂ gas, and the resultant mixture was subjected to heat treatment at 100 °C for one hour, whereby the above-mentioned modified silicic acid was prepared. A silicon rubber elastic body was prepared in the same manner as in Example 1 by using the following silicone composition. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 5 wt. parts Constituent (iii) : A platinum catalyst component (III) 0.001 wt. part Constituent (iv): A surface-modified synthetic hydrous silicic acid containing a reactive group which had been obtained by further modifying the synthetic hydrous silicic acid of the Component (IV) (imparted with hydrophobicity by dimethylsilicone oil) by vinyltriethoxysilane, wherein the number of the vinyl group was 3.8x10²⁰ groups/g 10 wt. parts Constituent (v) : Iron oxide 5 wt. parts The above-mentioned Constituents (i) to (v) were those constituting a composition according to the present invention, which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (i) 52.5 wt. parts Constituent (iii) 0.001 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 47.5 wt. parts Constituent (ii) 5 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body. Comparative Example 1 A silicon rubber-like elastic body was prepared in the same manner as in Example 1 by using the following silicone composition. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 2.44 wt. parts Constituent (iii) : Platinum-type catalyst 0.001 wt. part Constituent (v) : Iron oxide 5 wt. parts The above-mentioned composition was prepared so that the total amount (mol) of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (i) 51.22 wt. parts Constituent (iii) 0.001 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 48.78 wt. parts Constituent (ii) 2.44 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body. Comparative Example 2 A silicon rubber-like elastic body was prepared in the same manner as in Example 1 by using the following silicone composition. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 2.44 wt. parts. Constituent (iii) : Platinum catalyst 0.001 wt. part Constituent (iv): Synthetic hydrous silicic acid (Nipsil N 300A, mfd. by Nihon Silica K.K.) having a particle size of 0.1 - 7 microns, and a specific surface area of 170 m²/g 10 wt. parts Constituent (v) : Iron oxide 5 wt. parts The above-mentioned composition was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (i) 51.22 wt. parts Constituent (iii) 0.001 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 48.78 wt. parts Constituent (ii) 2.44 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body. Comparative Example 3 Modified synthetic hydrous silicic acid as a Component (IV) was prepared in the following manner. 100 g of synthetic hydrous silicic acid (trade name: Nipsil N 300A, mfd. by Nihon Silica K.K.) having a particle size of 0.1 - 7 microns and a specific surface area of 170 m²/g was charged into a mixer. While the silicic acid was forcibly stirred by means of the mixer, 12 g of vinyltriethoxysilane was added thereto by spraying by use of N₂ gas, and the resultant mixture was subjected to heat treatment at 100 °C for one hour, whereby the above-mentioned modified silicic acid was prepared. A silicon rubber-like elastic body was prepared in the same manner as in Example 1 by using the following silicone composition. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 5 wt. parts Constituent (iii) : Platinum catalyst 0.001 wt. part Constituent (iv): Surface-modified synthetic hydrous silicic acid modified only by vinyltriethoxysilane, wherein the number of the vinyl group was 3.8x10²⁰ groups/g 10 wt. parts Constituent (v) : Iron oxide 5 wt. parts The above-mentioned composition was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (i) 52.5 wt. parts Constituent (iii) 0.001 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 47.5 wt. parts Constituent (ii) 5 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body. Comparative Example 4 Modified synthetic hydrous silicone rubber as a Component (IV) was prepared in the following manner. 100 g of synthetic hydrous silicic acid (trade name: Nipsil N 300A, mfd. by Nihon Silica K.K.) having a particle size of 0.1 - 7 microns and a specific surface area of 170 m²/g was charged into a mixer. While the silicic acid was forcibly stirred by means of the mixer, 12 g of 3,3,3-trifluoropropyltrimethoxysilane was added thereto by spraying by use of N₂ gas, and the resultant mixture was subjected to heat treatment at 100 °C for one hour, whereby the above-mentioned modified silicic acid was prepared. A silicon rubber-like elastic body was prepared in the same manner as in Example 1 by using the following silicone composition. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 2.44 wt. parts Constituent (iii) : platinum catalyst 0.001 wt. part Constituent (iv): Surface-modified synthetic hydrous silicic acid of the Component (IV) modified only by 3,3,3-trifluoropropyltrimethoxysilane 10 wt. parts Constituent (v) : Iron oxide 5 wt. parts The above-mentioned composition was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (i) 51.22 wt. parts Constituent (iii) 0.001 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 48.78 wt. parts Constituent (ii) 2.44 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body. Comparative Example 5 Modified synthetic hydrous silicic acid as a Component (IV) was prepared in the following manner. Synthetic hydrous silicic acid (trade name: Nipsil SS-30P, mfd. by Nihon Silica K.K.) having a particle size of 8.6 microns and a specific surface area of 114 m²/g (after the treatment) treated with dimethylsilicone oil alone. A silicone rubber-like elastic body was prepared in the same manner as in Example 1 by using the following silicone composition. Constituent (i) : An organopolysiloxane copolymer of the Component (I) wherein the end of the molecular chain was blocked by vinyl group and the number of the vinyl group was 6.00x10⁻⁵ mol/g 100 wt. parts Constituent (ii) : An organopolysiloxane of the Component (II) containing a hydrogen atom connected to a silicon atom, wherein the number of the hydrogen atom connected to the silicon atom was 2.46x10⁻³ mol/g 2.44 wt. parts Constituent (iii) : platinum catalyst 0.001 wt. part Constituent (iv): Surface-modified synthetic hydrous silicic acid of the Component (IV) modified only by the dimethylsilicone oil 2.44 wt. parts Constituent (v) : Iron oxide 5 wt. parts The above-mentioned composition was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom connected to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (i) 51.22 wt. parts Constituent (iii) 0.001 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts B-liquid Constituent (i) 48.78 wt. parts Constituent (ii) 2.44 wt. parts Constituent (iv) 5 wt. parts Constituent (v) 2.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 180 °C for 10 min., whereby a silicone rubber-like elastic body. Some physical properties and toner releasability of the above-mentioned elastic materials obtained in Examples 1 and 2, and Comparative Examples 1 to 5 are shown in the following Table 1. 50 circular toner images having a diameter of 2 mm and a thickness of 50 microns were formed on a sample rubber piece (20 mm x 60 mm x 15 mm), and the toner images were heat-melted at an environmental temperature of 180 °C for 30 min., and then cooled to room temperature to be solidified. An adhesive tape (Union-A tape mfd. by Union Kogyo K.K.) was attached to the toner images, and along the tape, a rigid roller was reciprocated ten times, and then the tape was peeled. The thus obtained peeling conditions of the toner images were classified into five classes, and the numbers of the toner images allotted to the classes were respectively measured and marked. The sums of the thus obtained marks were calculated and divided by the total marks to obtain percentages. The toner releasability was represented by the thus obtained percentage. The peeling conditions of the toner images were classified in the following manner. A: A state wherein the toner image was completely released (4 marks) B: An intermediate state between the state A and the state C (3 marks) C: A state wherein 1/2 of total area was released (2 marks) D: An intermediate state between the state C and the state D (1 mark) E: A state wherein the toner image completely remained (O mark) The toner releasability was calculated according to the following formula: Toner releasability (%) = 1/200 x (4 x a + 3 x b + 2 x C + 1 x d + 0 x e) x 100 , wherein a + b + c + d + e = 50 . The above-mentioned sample piece was used after it was subjected to aging at 200 °C for 4 hours. Example 3 While the addition amount of the Component (IV) used in Example 1, i.e., the surface-modified synthetic hydrous silicic acid containing a reactive group which had been modified by 3,3,3-trifluoropropyltrimethoxysilane and vinyltriethoxysilane was 10 wt. % based on the total amount of the composition, and the mole of the vinyl group (hereinafter, referred to as "Vi") contained in the Component (I), and the hydrogen atom (hereinafter, referred to "H") bonded to the silicon atom of the Component (II) were changed. The mole ratio between the hydrogen atom bonded to the silicon atom (H) and the reactive vinyl group (Vi) was represented by H/Vi. More specifically, 100 wt. parts of the Component (I) was used and the proportion of the Component (II) to be mixed therewith was changed, whereby the mol ratio of H/Vi was changed. While the ratio H/Vi was changed, various silicone compositions corresponding to the respective H/Vi values were prepared in the same manner as in Example 1, hardened under heating in a heat press at 180 °C for 10 min., and further subjected to aging at 200 °C for 4 hours. The hardness, impact resilience, and toner-releasability of the resultant products were evaluated in the same manner as in Table 1. The results are shown in Figures 1, 2 and 3. From the results of the hardness and impact resilience, it was clear that the vinyl group of the Component (III) of the surface-modified synthetic hydrous silicic acid containing a vinyl group reacted with the hydrogen group of the Component (II). More specifically, as the value of the H/Vi increased (i.e., the amount of the active hydrogen atom became larger), the hardness and impact resilience of the silicone rubber increased, as shown in Figures 1 and 2. Accordingly, it is clear that the vinyl groups present at the surface of the silicic acid fine powder reacted with the polysiloxane having an active hydrogen atom, whereby the crosslinking structure became stronger (or crosslinking bonds increased). Further, when H/Vi = 1.0 , (i.e., mole of the vinyl group was equal to that of the hydrogen atom bonded to the silicon atom), the toner-releasability became maximum, as shown in Figure 3. Example 4 The addition reaction-type silicone rubber compositions A and B obtained in Example 1 were uniformly mixed at a weight ratio of 100:100, and then degassed to prepare a liquid mixture. The mixture was injected into a cylindrical metal mold in which an aluminum core bar for a heat-fixing roller to be used in an electrophotographic copying machine with an outside diameter of 60 mm coated with a siloxane-type primer had been disposed in advance and had preliminarily been heated up to 150 °C, and kept at the same temperature for 5 min. thereby to cure and mold the mixture. After the curing, the thus formed fixing roller covered with the silicone rubber was taken out from the metal mold. The silicone rubber covering layer had a thickness of 0.5 mm. The thus obtained fixing roller was disposed in a heat fixing device as shown in Figure 4, and a fixing test was conducted while sheets of paper were continuously passed through the fixing device under the following conditions. 〈Fixing conditions〉 Controlled temperature of fixing roller 1 surface: 175 - 185 °C Oil application device 3: A web-type application device including a paper web (trade name: Normex Web, mfd. by Japan Vilene Co., Ltd.) impregnated with a silicone oil (KP96H, mfd. by Shinetsu Kagaku K.K.) having a viscosity of 10,000 mPa·s (10,000 cs) at 25 °C Web feed speed: 1 m per 10,000 sheets of paper supply (A-4 size) Supplied paper: A4 size transfer paper (plain paper) on which an unfixed toner image corresponding to a test pattern was formed. Paper supply speed: 50 sheets/min. Nip width (W) between the fixing roller 1 and pressure roller 2: 9 - 10 mm As a result, even after 300,000 sheets of paper were passed through the fixing device, the fixing roller 1 retained good releasability, and considerable toner offset or sheet jamming trouble due to the toner offset, which was practically problematic, did not occur, and the image quality of the fixed image was well retained. Further, the durability of the roller was excellent (i.e., roller life was considerably long). Example 5 A fixing roller was prepared in the same manner as in Example 4 except that the liquid addition reaction-type silicone rubber obtained in Example 2 was used, and was subjected to a fixing test while sheets of paper were continuously passed through the fixing device. As a result, until 200,000 sheets of paper were passed through the fixing device, the fixing roller 1 retained good releasability, and considerable toner offset or sheet jamming trouble due to the toner offset, which was practically problematic, did not occur, and the image quality of the fixed image was well retained. Further, the durability of the roller was excellent (i.e., roller life was considerably long). Comparative Examples 6 - 10 Fixing rollers were prepared in the same manner as in Example 4 except that the silicone compositions (the liquid addition reaction-type silicone rubber compositions) obtained in Comparative Examples 1 - 5 were used, and were subjected to a fixing test while sheets of paper were continuously passed through the fixing device. Comparative Example 11 A fixing roller was prepared in the same manner as in Example 4 except that the a commercially available liquid addition reaction-type silicone rubber composition providing a hardness (JIS A) of 40 was used, and was subjected to a fixing test while sheets of paper were continuously passed through the fixing device. The results obtained in Examples 4 and 5, and Comparative Examples 6 - 11 are shown in the following Table 2. Example 6 The above-mentioned constituent (IV) was prepared in the following manner. 100 wt. parts of synthetic hydrous silicic acid (trade name: Nipsil SS 30P, mfd. by Nihon Silica K.K.) having an average particle size of 8.6 microns and a specific surface area of 114 m²/g, of which surface had been treated with about 9 wt. % of dimethylsilicone oil, was charged into a stirrer. While the silicic acid was forcibly stirred by means of the stirrer, 12 wt. parts of vinyltriethoxysilane was gradually dripped thereto, the resultant mixture was then taken out from the stirrer, and thereafter was air-dried at 100 °C for one hour, whereby the above-mentioned surface-treated synthetic hydrous silicic acid containing a vinyl group was obtained. In the resultant powder, the amount of the vinyl group was about 3.8x10²⁰ groups per 1 g of the powder. The above-mentioned Constituents (i) to (v) were those constituting a composition according to the present invention, which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom bonded to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack (or two-component) type of formulation. A-liquid Constituent (I) 45.35 wt. parts Constituent (III) 0.001 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts B-liquid Constituent (I) 39.29 wt. parts Constituent (II) 6.05 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 °C for 10 min., whereby a silicone rubber-like elastic body formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Example 7 Constituent (I) : A vinyl group-containing dimethylpolysiloxane comprising dimethylpolysiloxane of which end was blocked by a vinyl group, and vinyl group-containing dimethylpolysiloxane of which end is blocked by a methyl group, wherein the total number of vinyl group was 8.0x10⁻⁵ mol/g 100 wt. parts Constituent (II) : A methylhydrogenpolysiloxane wherein the number of hydrogen atoms bonded to the silicon atom was 2.0x10⁻³ mol/g 7.15 wt. parts Constituent (III) : Platinum catalyst 0.001 wt. part Constituent (IV) : Surface-modified synthetic anhydrous hydrophobic silicic acid containing a vinyl group of which surface had been modified by a vinyl group-containing silane compound 10 wt. parts Constituent (V) : Red iron oxide 1 wt. part The above-mentioned constituent (IV) was prepared in the following manner. 100 wt. parts of synthetic anhydrous hydrophobic silicic acid (trade name: Aerosil R-812, mfd. by Degusa Co.) having a specific surface area of 200 m²/g and a bulk specific gravity of 50 g/l, of which surface had been treated with about 6 wt. % of dimethyldichlorosilane was charged into a stirrer. While the silicic acid was forcibly stirred by means of the stirrer, 12 g of vinyltriethoxysilane was gradually dripped thereto, the resultant mixture was then taken out from the stirrer, and thereafter was air-dried at 100 °C for one hour, whereby the above-mentioned surface-treated synthetic anhydrous silicic acid containing a vinyl group was obtained. In the resultant powder, the amount of the vinyl group was about 3.8x10²⁰ groups per 1 g of the powder. The above-mentioned Constituents (i) to (v) were those constituting a composition according to the present invention, which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom bonded to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack (or two-component) type of formulation. A-liquid Constituent (I) 45.35 wt. parts Constituent (III) 0.001 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts B-liquid Constituent (I) 39.29 wt. parts Constituent (II) 6.05 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 °C for 10 min., whereby a silicone rubber-like elastic body formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Example 8 A composition according to the present invention was formed from the Constituents (I), (II) and (III) used in Example 6 and Constituent (IV) prepared in the following manner. 100 wt. parts synthetic hydrous silicic acid (trade name: Nipsil N 300A, mfd. by Nihon Silica K.K.) having an average particle size of 2 microns and a specific surface area of 170 m²/g was charged into a stirrer. While the silicic acid was forcibly stirred by means of the stirrer, 3 wt. parts of methyltrimethoxysilane was gradually dripped thereto and, after the addition, 12 wt. parts of vinyltriethoxysilane was gradually dripped in a similar manner. After the dripping was completed, the powder was taken out from the stirrer, and thereafter was air-dried at 100°C for one hour, whereby the above-mentioned surface-treated synthetic hydrous silicic acid containing a vinyl group was obtained. In the resultant powder, the amount of the vinyl group was about 3.8x10²⁰ groups per 1 g of the powder. The above-mentioned Constituents (i) to (v) were those constituting a composition according to the present invention, which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom bonded to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (I) 45.35 wt. parts Constituent (III) 0.001 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts B-liquid Constituent (I) 39.29 wt. parts Constituent (II) 6.05 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 °C for 10 min., whereby a silicone rubber-like elastic body formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Comparative Example 12 There was prepared a liquid A (viscosity: 80,000 mPa·s (800 poise)) which comprised 100 wt. parts of a vinyl group-containing dimethylpolysiloxane, 5 wt. parts of synthetic anhydrous silicic acid, 20 wt. parts of quarts powder, 1 wt. parts of red iron oxide and a platinum-type catalyst. Separately, there was prepared a liquid B (viscosity: 60,000 mPa·s (600 poise)) which comprised 100 wt. parts of mixture (comprising a vinyl group - containing diorganopolysiloxane and an active hydrogen group-containing siloxane), 5 wt. parts of synthetic anhydrous silicic acid, 20 wt. parts of quartz powder, and 1 wt. parts of red iron oxide. The A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 °C for 10 min, whereby a silicone rubber-like elastic body was formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Comparative Example 13 A rubber-like elastic body was obtained in the same manner as in Comparative Example 12 except that 30 wt. % of the synthetic anhydrous silicic acid was used. Comparative Example 14 Constituent (I) : A vinyl group-containing dimethylpolysiloxane comprising dimethylpolysiloxane of which end was blocked by a vinyl group, and vinyl group-containing dimethylpolysiloxane of which end is blocked by a methyl group, wherein the total number of vinyl group was 8.0x10⁻⁵ mol/g 100 wt. parts Constituent II) : A methylhydrogenpolysiloxane wherein the number of hydrogen atoms bonded to the silicon atom was 2.0x10⁻³ mol/g 4 wt. parts Constituent (III) : Platinum catalyst 0.001 wt. part Constituent (V) : Red iron oxide 1 wt. part The above-mentioned Constituents (I), (II), (III) and (V) were those constituting a silicone composition which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom bonded to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-pack type of formulation. A-liquid Constituent (I) 52 wt. parts Constituent (III) 0.001 wt. parts Constituent (V) 0.5 wt. parts B-liquid Constituent (I) 48 wt. parts Constituent (II) 4 wt. parts Constituent (V) 0.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 °C for 10 min., whereby a silicone rubber-like elastic body was formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Comparative Example 15 Constituent (I) : A vinyl group-containing dimethylpolysiloxane comprising dimethylpolysiloxane of which end was blocked by a vinyl group, and vinyl group-containing dimethylpolysiloxane of which end is blocked by a methyl group, wherein the total number of vinyl group was 8.0x10⁻⁵ mol/g 100 wt. parts Constituent (II) : A methylhydrogenpolysiloxane wherein the number of hydrogen atoms bonded to the silicon atom was 2.0x10⁻³ mol/g 7.15 wt. parts Constituent (III) : Platinum catalyst 0.001 wt. part Constituent (IV) : Surface-modified synthetic hydrous silicic acid containing a vinyl group of which surface had been modified by a vinyl group-containing silane compound 10 wt. parts Constituent (V) : Red iron oxide 1 wt. part The above-mentioned constituent (IV) was prepared in the following manner. 100 wt. parts of synthetic hydrous silicic acid (trade name: Nipsil N-300A, mfd. by Nihon Silica K.K.) having an average particle size of 2 microns and a specific surface area of 170 m²/g, was charged into a stirrer. While the silicic acid was forcibly stirred by means of the stirrer, 12 g of vinyltriethoxysilane was gradually dripped thereto, the resultant mixture was then taken out from the stirrer, and thereafter was air-dried at 100 °C for one hour, whereby the above-mentioned surface-treated synthetic hydrous silicic acid containing a vinyl group was obtained. In the resultant powder, the amount of the vinyl group was about 3.8x10²⁰ groups per 1 g of the powder. The above-mentioned Constituents (I) to (V) were those constituting a silicone composition, which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom bonded to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-component type of formulation. A-liquid Constituent (I) 45.35 wt. parts Constituent (III) 0.001 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts B-liquid Constituent (I) 39.29 wt. parts Constituent (II) 6.05 wt. parts Constituent (IV) 4.23 wt. parts Constituent (V) 0.43 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 °C for 10 min., whereby a silicone rubber-like elastic body was formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Comparative Example 16 Constituent (I) : A vinyl group-containing dimethylpolysiloxane comprising dimethylpolysiloxane of which end was blocked by a vinyl group, and vinyl group-containing dimethylpolysiloxane of which end is blocked by a methyl group, wherein the total number of vinyl group was 8.0x10⁻⁵ mol/g 100 wt. parts Constituent (II) : A methylhydrogenpolysiloxane wherein the number of hydrogen atoms bonded to the silicon atom was 2.0x10⁻³ mol/g 4 wt. parts Constituent (III) : Platinum catalyst 0.001 wt. part Constituent (IV) : Surface-modified synthetic hydrous silicic acid containing a vinyl group of which surface had been modified by methyltrimethoxysilane 10 wt. parts Constituent (V) : Red iron oxide 1 wt. part The above-mentioned constituent (IV) was prepared in the following manner. 100 wt. parts of synthetic hydrous silicic acid (trade name: Nipsil N 300A, mfd. by Nihon Silica K.K.) having an average particle size of 2 microns and a specific surface area of 170 m²/g, was charged into a stirrer. While the silicic acid was forcibly stirred by means of the stirrer, 3 wt. parts of methyltriethoxysilane was gradually dripped thereto, the resultant mixture was then taken out from the stirrer, and thereafter was air-dried at 100 °C for one hour, whereby the above-mentioned surface-treated synthetic hydrous silicic acid was obtained. The above-mentioned Constituents (I) to (V) were those constituting a silicone composition which was prepared so that the total amount of the vinyl group contained therein was substantially equal to that of the hydrogen atom bonded to the silicon atom. The respective constituents were packed in the following manner so as to prepare a two-component type of formulation. A-liquid Constituent (I) 52 wt. parts Constituent (III) 0.001 wt. parts Constituent (IV) 5 wt. parts Constituent (V) 0.5 wt. parts B-liquid Constituent (I) 48 wt. parts Constituent (II) 4 wt. parts Constituent (IV) 5 wt. parts Constituent (V) 0.5 wt. parts The above-mentioned components were uniformly mixed to prepare the A-liquid and B-liquid, respectively. The thus prepared A -liquid and B -liquid were mixed at a wt. ratio of 100:100, degassed, and heated in a heat press at 150 o C for 10 min., whereby a silicone rubber-like elastic body was formed from the silicone rubber composition. The rubber-like elastic body was further subjected to post curing at 200 °C for 4 hours. Some physical properties and toner-releasability of the above-mentioned elastic materials obtained in Examples 6 to 8, and Comparative Examples 12 to 16 are shown in the following Table 3. Example 9 The addition amount of the Constituent (IV) used in Example 6, i.e., the surface-modified synthetic hydrous silicic acid containing a vinyl group which had been modified by dimethylsilicone oil and vinyl group-containing silane was fixed at 10 wt. parts per 100 wt. parts of the Constituent (I) of a vinyl group-containing dimethylpolysiloxane, and the addition amount of the Constituent (II), i.e., methylhydrogenpolysiloxane was changed. At this time, the ratio between the total amount (total mole number) of the vinyl groups bonded to the silicon atom contained in the Constituent (I) and the vinyl group of the surface-modified synthetic hydrous silicic acid containing a vinyl group, which had been modified by a silicone oil and a vinyl group-containing silane, and the mole of the hydrogen atom -Si-H) bonded to the Constituent (II), i.e., methylhydrogenepolysiloxane was represented by -Si-H/Vi (Vi denotes a vinyl group). While the ratio Si-H/Vi was changed, various silicone compositions corresponding to the respective Si-H/Vi values were prepared in the same manner as in Example 6, hardened under heating in a heat press at 150 °C for 10 min., and further subjected to post-curing at 200 °C for 4 hours. The hardness, impact resilience, and toner-releasability of the resultant products were evaluated. The results are shown in Figure 5. As shown in Figure 5, when mole of the vinyl group was substantially equal to that of the hydrogen atom bonded to the silicon atom, the hardness, impact resilience and toner-releasability became maximum. Example 10 A fixing roller having an elastic material layer formed of an addition reaction-type dimethylsilicone composition to be used for a heat and pressure fixing device was prepared in the following manner. First, the surface of an aluminum core bar having an outside diameter of 58.3 mm in the central portion thereof (wall thickness: 6.5 mm, reverse camber degree: 150 microns) was subjected to sand-blasting for the purpose of decreasing, dried and then coated with a siloxane-type primer, and air-dried under heating at 130 °C for 15 min. Then, the thus prepared core bar was disposed in a cylindrical metal mold which had preliminarily been heated to 150 °C. The addition reaction-type silicone rubber compositions A and B obtained in Example 6 were uniformly mixed at a weight ratio of 100:100, and then degassed to prepare a liquid mixture. The mixture was injected into the cylindrical metal mold and kept at the same temperature (150 °C) for 5 min. thereby to cure the mixture. After the curing, the thus formed fixing roller covered with the silicone rubber was taken out from the metal mold. The silicone rubber covering layer had a thickness of 0.5 mm. The thus obtained fixing roller was disposed in a heat fixing device as shown in Figure 4, and a fixing test was conducted while sheets of paper were continuously passed through the fixing device under the following conditions. 〈Fixing conditions〉 Controlled temperature of fixing roller 1 surface: 180 - 190 °C Oil application device 3: A web-type application device including a web (trade name: Normex Paper Web) impregnated with a dimethyl silicone oil (KP96H, mfd. by Shinetsu Kagaku K.K.) having a viscosity of 10,000 mPa·s (10,000 cs) at 25 °C Web feed speed: 1 m per 10,000 sheets of paper supply (A-4 size) Supplied paper: A4 size transfer paper (plain paper) on which an unfixed toner image corresponding to a test pattern was formed. Paper supply speed: 70 sheets/min. Nip width (W) between the fixing roller 1 and pressure roller 2: 9 - 10 mm Example 11 A fixing roller was prepared in the same manner as in Example 10 except that the dimethyl silicone rubber composition obtained in Example 7 was used, and was subjected to a fixing test while sheets of paper were continuously passed through the fixing device in the same manner as in Example 10. Comparative Example 17 A fixing roller was prepared in the same manner as in Example 10 except that the dimethylsilicone composition obtained in Comparative Example 12 was used, and was subjected to a fixing test while sheets of paper were continuously passed through the fixing device in the same manner as in Example 10. Example 18 A fixing roller was prepared in the same manner as in Example 10 except that the dimethylsilicone composition obtained in Comparative Example 13 was used, and was subjected to a fixing test while sheets of paper were continuously passed through the fixing device in the same manner as in Example 10. The results obtained in Examples 10 and 11, and Comparative Examples 14 - 15 are shown in the following Table 4. As described hereinabove, the present invention provides an addition reaction-type dimethylsilicone rubber composition which is excellent in mechanical strength and has good releasability. When the dimethylsilicone rubber composition according to the present invention is used as a coating material of a heat fixing roller, it provides sufficient durability because of its excellent mechanical strength and good releasability. The fixing device including a fixing roller comprising the dimethylsilicone rubber composition according to the present invention as a coating material can solve various problems such as paper curl, paper wrinkle, paper jamming, toner offset and contamination due to toner attachment which can occur in paper conveying or fixing operation, and can retain excellent releasability and fixing ability together with sufficient durability. In a fixing device, both of the fixing and pressure rollers may use the silicone rubber composition according to the present invention as their coating material, or any one of them may use the silicone rubber composition.

Claims: An addition reaction-type dimethylsilicone composition, comprising: (I) a diorganopolysiloxane containing at least one reactive vinyl group connected to a silicon atom, (II) an organopolysiloxane containing at least one active hydrogen atom connected to a silicon atom, and (IV) silica powder, having a BET specific surface area of 40 - 500 m²/g, whose surface has been treated, prior to the mixing with (I) and (II), with (IV-1) a fluoroalkylsilane, an alkylsilane compound, a fluorosilicone oil, a dimethylsilicone oil, or a mixture thereof, and (IV-2) a silane compound containing an unsaturated group having a reactivity to said organopolysiloxane containing an active hydrogen atom (II), said unsaturated group being in a form suitable to be introduced onto the surface of the silica powder. A composition according to claim 1, wherein said silane compound containing an unsaturated group (IV-2) is a vinylsilane compound A composition according to claim 1, wherein said silane compound containing an unsaturated group (IV-2) is a vinylsilane compound selected from the group consisting of vinyltriethoxysilane, dimethylvinylmethoxysilane, dimethylvinyltriethoxysilane, methylvinyldimethoxysilane, methylvinyldiethoxysilane, vinyltrichlorosilane, dimethylvinylchlorosilane, and methylvinyldichlorosilane. A composition according to claim 1, wherein said diorganopolysiloxane containing a reactive vinyl group (I) comprises a diorganopolysiloxane having vinyl groups at both ends thereof. A composition according to claim 4, wherein said diorganopolysiloxane containing a reactive vinyl group comprises (I) an organosiloxane unit represented by the formula of wherein R₁ and R₂ respectively denote an alkyl group, and an organosiloxane unit containing a fluoroalkyl group represented by the formula of A composition according to claim 4, wherein said diorganopolysiloxane containing a reactive vinyl group (I) comprises a dimethylpolysiloxane having vinyl groups at both ends thereof. A composition according to claim 1, wherein said diorganopolysiloxane containing a reactive vinyl group (I) comprises a mixture of a diorganopolysiloxane having vinyl groups at both ends thereof, and a diorganopolysiloxane having methyl groups at both ends thereof and having a vinyl group in the side chain thereof. A composition according to claim 7, wherein said diorganopolysiloxane containing a reactive vinyl group (I) comprises a mixture of a dimethylpolysiloxane having vinyl groups at both ends thereof, and a dimethylpolysiloxane having methyl groups at both ends thereof and having a vinyl group in the side chain thereof. A composition according to claim 1, wherein said diorganopolysiloxane containing an active hydrogen atom (II) contains one or more hydrogen atoms banded to a silicon atom per one organopolysiloxane molecule, and comprises an organosiloxane unit represented by the formula of wherein R₃ and R₄ respectively denote an alkyl group, and an organosiloxane unit containing a fluoroalkyl group represented by the formula of A composition according to claim 1, wherein said diorganopolysiloxane containing an active hydrogen atom (II) comprises a methylhydrogenpolysiloxane containing one or more hydrogen atoms bonded to a silicon atom per one organopolysiloxane molecule. A composition according to claim 1, wherein said silica powder (IV) has a BET specific surface area of 70-400 m²/g. A composition according to claim 1, wherein said silica powder (IV) has a particle size of 7 - 100 mµ and a BET specific surface area of 40 - 500 m²/g. A composition according to claim 1, wherein said silica powder (IV) has a particle size of 5 - 50 mµ and a BET specific surface area of 70 - 400 m²/g. A composition according to claim 1, wherein said silica powder (IV) has a particle size of 7 - 25 mµ and a BET specific surface area of 100 - 300 m²/g. A composition according to claim 1, wherein said silica powder (IV) has been treated with a silane compound containing an unsaturated group (IV-2) selected from the group consisting of vinyltriethoxysilane, dimethylvinylmethoxysilane, dimethylvinylethoxysilane, methylvinyldimethoxysilane, methylvinyldiethoxysilane, vinyltrichlorosilane, dimethylvinylchlorosilane, and methylvinyldichlorosilane; and has further been treated with a surface-treating agent (IV-1) selected from the group consisting of a fluoroalkylsilane represented by C n F 2n+1 CH₂CH₂SiR m (OR') 3-m , or C n F 2n+1 CH₂CH₂SiR m Cl 3-m wherein n denotes an integer of 1 - 8, m denotes 0 or 1, and R and R' respectively denote a methyl or ethyl group; trimethylmethoxysilane, trimethylethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, trimethylchlorosilane, dimethyldichlorosilane, methyltrichlorosilane, hexamethyldisilazane, fluorosilicone oil, and dimethylsilicone oil. A composition according to claim 15, wherein said silica powder (IV) has been treated with 1 - 30 wt. parts of the silane compound containing an unsaturated group (IV-2), and has further been treated with 1 - 30 wt. parts of the surface-treating agent (IV-1), with respect to 100 wt. part of the silica powder (IV). A composition according to claim 15, wherein said silica powder (IV) has been treated with 5 - 25 wt. parts of the silane compound containing an unsaturated group (IV-2), and has further been treated with 3 - 25 wt. parts of the surface-treating agent (IV-1), with respect to 100 wt. part of the silica powder. A dimethylsilicone rubber composition obtained by heating a platinum-type catalyst (III); and an addition reaction-type dimethylsilicone composition according to any of claims 1 to 17. A rubber composition according to claim 18, which has been obtained by using 5 - 30 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). A rubber composition according to claim 18, which has been obtained by using 5 - 20 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). A rubber composition according to claim 18, which has been obtained by using 6 - 15 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). A rubber composition according to claim 18, which has been obtained by heating the addition reaction-type dimethylsilicone composition at 100 - 180 °C for 0.5 - 20 min. An elastic revolution body comprising an elastic layer formed from a dimethylsilicone rubber composition; said dimethylsilicone rubber composition being obtained by heating a platinum-type catalyst and an addition reaction-type dimethylsilicone composition according to any of claims 1 to 17. An elastic revolution body according to claim 23, wherein said dimethylsilicone rubber composition has been obtained by using 5 - 30 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). An elastic revolution body according to claim 23, wherein said dimethylsilicone rubber composition has been obtained by using 5 - 20 wt. parts of the silica powder with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). An elastic revolution body according to claim 23, wherein said dimethylsilicone rubber composition has been obtained by using 6 - 15 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). An elastic revolution body according to claim 23, wherein said dimethylsilicone rubber composition has been obtained by heating the addition reaction-type dimethylsilicone composition at 100 - 180 °C for 0.5 - 20 min. A fixing device, comprising at least a pair of rollers between which a toner image-supporting material carrying an unfixed toner image is passed under pressure to fix the toner image to the toner image-supporting material; wherein at least one of said pair of rollers comprises an elastic layer formed from a dimethylsilicone rubber composition; said dimethylsilicone rubber composition being obtained by heating a platinum-type catalyst and an addition reaction-type dimethylsilicone composition according to any of claims 1 to 17. A fixing device according to claim 28, wherein said dimethylsilicone rubber composition has been obtained by using 5 - 30 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). A fixing device according to claim 28, wherein said dimethylsilicone rubber composition has been obtained by using 5 - 20 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). A fixing device according to claim 28, wherein said dimethylsilicone rubber composition has been obtained by using 6 - 15 wt. parts of the silica powder (IV) with respect to 100 wt. parts of a mixture of the diorganopolysiloxane containing a reactive vinyl group (I), organopolysiloxane containing an active hydrogen atom (II) and platinum-type catalyst (III). A fixing device according to claim 28, wherein said dimethylsilicone rubber composition has been obtained by heating the addition reaction-type dimethylsilicone composition at 100 - 180 °C for 0.5 - 20 min.

Inventors: MIYABAYASHI TOSHIYUKI, MIYABAYASHI, TOSHIYUKI
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1989
Main classification: C08L83
IPC codes: C08L83, G03G15, C08K9