Ferroelectric chiral smectic liquid crystal composition and liquid crystal device using same

Abstract: A ferroelectric chiral smectic liquid crystal composition, comprising at least one compound represented by the following formula (I): wherein R₁ denotes a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₁ denotes a single bond, -O- or - O-; Z denotes a single bond or - O-; and n is an integer of 1 - 12; and at least one compound represented by the following formula (II): wherein R₂ and R₃ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having substituent, at lease one of R₂ and R₃ being optically active; X₂ and X₃ respectively denote a single bond, -O-, -O -, -O- or -OO-.

Description: FIELD OF THE INVENTION AND RELATED ART The present invention relates to a liquid crystal composition used in a liquid crystal display device, a liquid crystal-optical shutter, etc., more particularly to a novel liquid crystal composition with improved responsiveness to an electric field and a liquid crystal device using the liquid crystal composition. Hitherto, liquid crystal devices have been used as an electro-optical device in various fields. Most liquid crystal devices which have been put into practice use TN (twisted nematic) type liquid crystals, as shown in "Voltage-Dependent Optical Activity of a Twisted Nematic Liquid Crystal" by M. Schadt and W. Helfrich "Applied Physics Letters" Vol. 18, No. 4 (Feb. 15, 1971) pp. 127-128. These devices are based on the dielectric alignment effect of a liquid crystal and utilize an effect that the average molecular axis direction is directed to a specific direction in response to an applied electric field because of the dielectric anisotropy of liquid crystal molecules. It is said that the limit of response speed is on the order of milli-seconds, which is too slow for many uses. On the other hand, a simple matrix system of driving is most promising for application to a large-area flat display in view of cost, productivity, etc., in combination. In the simple matrix system, an electrode arrangement wherein scanning electrodes and signal electrodes are arranged in a matrix, and for driving, a multiplex driving scheme is adopted wherein an address signal is sequentially, periodically and selectively applied to the scanning electrodes and prescribed data signals are selectively applied in parallel to the signal electrodes in synchronism with the address signal. When the above-mentioned TN-type liquid crystal is used in a device of such a driving system, a certain electric field is applied to regions where a scanning electrode is selected and signal electrodes are not selected or regions where a scanning electrode is not selected and a signal electrode is selected (which regions are so called "half-selected points"). If the difference between a voltage applied to the selected points and a voltage applied to the half-selected points is sufficiently large, and a voltage threshold level required for allowing liquid crystal molecules to be aligned or oriented perpendicular to an electric field is set to a value therebetween, display devices normally operate. However, in fact, as the number (N) of scanning lines increases, a time (duty ratio) during which an effective electric field is applied to one selected point when a whole image area (corresponding to one frame) is scanned decreases with a ratio of 1/N. Accordingly, the larger the number of scanning lines are, the smaller is the voltage difference of an effective value applied to a selected point and non-selected points when scanning is repeatedly effected. As a result, this leads to unavoidable drawbacks of lowering of image contrast or occurrence of interference or crosstalk. These phenomena are regarded as essentially unavoidable problems appearing when a liquid crystal having no bistability (i.e. liquid crystal molecules are horizontally oriented with respect to the electrode surface as stable state and is vertically oriented with respect to the electrode surface only when an electric field is effectively applied) is driven (i.e. repeatedly scanned) by making use of a time storage effect. To overcome these drawbacks, the voltage averaging method, the two-frequency driving method, the multiple matrix method, etc. has been already proposed. However, any method is not sufficient to overcome the above-mentioned drawbacks. As a result, it is the present state that the development of large image area or high packaging density in respect to display elements is delayed because it is difficult to sufficiently increase the number of scanning lines. To overcome drawbacks with such prior art liquid crystal devices, the use of liquid crystal devices having bistability has been proposed by Clark and Lagerwall (e.g. Japanese Laid-Open Patent Appln. No. 56-107216, U.S.P. No. 4367924, etc.). In this instance, as the liquid crystals having bistability, ferroelectric liquid crystals having chiral smectic C-phase (SmC*) or H-phase (SmH*) are generally used. These liquid crystals have bistable states of first and second stable states with respect to an electric field applied thereto. Accordingly, as different from optical modulation devices in which the above-mentioned TN-type liquid crystals are used, the bistable liquid crystal molecules are oriented to first and second optically stable states with respect to one and the other electric field vectors, respectively. Further, this type of liquid crystal has a property (bistability) of assuming either one of the two stable states in response to an applied electric and retaining the resultant state in the absence of an electric field. In addition to the above-described characteristic of showing bistability, such a ferroelectric liquid crystal (hereinafter sometimes abbreviated as "FLC") has an excellent property, i.e., a high-speed responsiveness. This is because the spontaneous polarization of the ferroelectric liquid crystal and an applied electric field directly interact with each other to induce transition of orientation states. The resultant response speed is faster than the response speed due to the interaction between dielectric anisotropy and an electric field by 3 to 4 digits. Thus, a ferroelectric liquid crystal potentially has very excellent characteristics, and by making use of these properties, it is possible to provide essential improvements to many of the above-mentioned problems with the conventional TN-type devices. Particularly, the application to a high-speed optical shutter and a display of a high density and a large picture is expected. For this reason, there has been made extensive research with respect to liquid crystal materials showing ferroelectricity. The EP-A-0 267 585 (D2) discloses a liquid crystal composition comprising: a fluorine-substituted optically avtice compound of a formula (III) (particularly the compounds (33) and (35) on page 16 and the compounds on page 48, lines 45 to 50) falling under the formula (I) of the present application, and an optically active compound (particularly the compounds (13), (27) and (29) on pages 12 and 15) which come close to the formula (II) of the present application. However, the D2 does not disclose a specific compound satisfying the formula (II) of the present claim 1. More specifically, the D2 only discloses an optically active compound having a terminal alkoxyalkyl group, whereas the compound of the formula (II) presently claimed has an alkyl terminal group with no substituent. However, ferroelectric liquid crystal materials developed heretofore cannot be said to satisfy sufficient characteristics required for a liquid crystal device including low-temperature operation characteristic, high-speed responsiveness, etc. A high response speed can be obtained by (a) increasing the spontaneous polarization, (b) lowering the viscosity η, or (c) increasing the applied voltage. However, the driving voltage has a certain upper limit in view of driving with IC, etc., and should desirably be as low as possible. Accordingly, it is actually necessary to lower the viscosity or increase the spontaneous polarization. A ferroelectric chiral smectic liquid crystal having a large spontaneous polarization generally provides a large internal electric field in a cell given by the spontaneous polarization and is liable to pose many constraints on the device construction giving bistability. Further, an excessively large spontaneous polarization is liable to accompany an increase in viscosity, so that remarkable increase in response speed may not be attained as a result. Further, if it is assumed that the operation temperature of an actual display device is 5 - 40 o C, the response speed changes by a factor of about 20, so that it actually exceeds the range controllable by driving voltage and frequency. As described hereinabove, commercialization of a ferroelectric liquid crystal device requires a ferroelectric chiral smectic liquid crystal composition having a low viscosity, a high-speed responsiveness and a small temperature-dependence of response speed. In a representative FLC cell structure, a pair of substrates are disposed, each substrate of e.g. glass being provided with an electrode pattern of e.g. ITO, further thereon with a layer of e.g. SiO₂ (about 1000 Å) for preventing short circuit between the pair of substrates and further thereon with a film of e.g. polyimide (PI; such as SP-510, 710, ... available from Toray K.K.) of about 500 Å in thickness, which is then treated for alignment control by rubbing with e.g. an acetate fiber-planted cloth. Such a pair of substrates are disposed opposite to each other so that their alignment control directions are symmetrical and the spacing between the substrates is held at 1 - 3 microns. On the other hand, it is known that the ferroelectric liquid crystal molecules under such non-helical conditions are disposed in succession so that their directors (longer molecular axes) are gradually twisted between the substrates and do not show a uniaxial orientation or alignment (i.e., in a splay alignment state). A problem in this case is a low transmittance through the liquid crystal layer. Transmitted light intensity I through a liquid crystal is given by the following equation with respect to the incident light intensity I₀ under cross nicols when the uniaxial alignment of the molecules is assumed: I = I₀sin²(4ϑa) sin²(πΔnd/λ) (1), wherein Δn denotes the refractive index anisotropy of the FLC; d, the cell thickness; λ, the wavelength of the incident light; and ϑa, a half of the angle between two stable states (tilt angle). When a conventional FLC cell is used, it has been experimentally known that ϑa is 5 - 8 degrees under a twisted alignment condition. The control of physical properties affecting the term Δndπ/λ cannot be easily performed, so that it is desired to increase ϑa to increase I. However, this has not been successfully accomplished by only a static alignment technique. With respect to such a problem, it has been proposed to utilize a torque relating to a dielectric anisotropy Δε of an FLC (1983 SID report from AT & T; Japanese Laid-Open Patent Applns. 245142/1986, 246722/1986, 246723/1986, 246724/1986, 249024/1986 and 249025/1986). More specifically, a liquid crystal molecule having a negative Δε tends to become parallel to the substrates under application of an electric field. By utilizing this property, if an effective value of AC electric field is applied even in a period other than switching, the above-mentioned twisted alignment is removed, so that ϑa is increased to provide an increased transmittance (AC stabilization effect). A torque ΓP S acting on FLC molecules involved in switching of states and a torque ΓΔε acting on FLC molecules relating to the AC stabilization effect are respectively proportional to physical properties as shown in the following formulas: ΓP S ∝ P S ·E (2) ΓΔε ∝ 1/2 Δε·ε₀·E² (3) The above formula (3) apparently shows that the sign and absolute value of Δε of the FLC play an important role. Figure 4 attached hereto shows the change of ϑa versus Vrms experimentally measured for 4 FLCs having different values of Δε. The measurement was conducted under application of AC rectangular pulses of 60 KHz so as to remove the influence of P S . The curves (I) - (IV) correspond to the results obtained by using FLCs showing the following Δε values (I) Δε ≃ -5.5, (II) Δε ≃ -3.0, (III) Δε ≃ -0, (IV) Δε ≃ 1.0. As is clear from the graph in Figure 4, a larger negative value of Δε provides a large ϑa at a lower voltage and thus contributes to provision of an increased I. The transmittances obtained by using the liquid crystals (I) and (III) were 15 % for (I) and 6 % for (III) (under application of rectangular AC waveforms of 60 kHz and ±8 V), thus showing a clear difference. As is known from the above examples, the display characteristics of an SSFLC (Surface-Stabilized FLC) can be remarkably changed by controlling the properties relating to Δε and P S . In order to provide a ferroelectric liquid crystal composition having a negatively large Δε, it is most effective to include a compound having a negative with a large absolute value. For example, it is possible to obtain a compound having a negatively large Δε by introducing a halogen or cyano group in a shorter axis direction of a molecule or by introducing a heterocyclic skeleton in a molecule. The magnitude of Δε of a compound having a negative Δε substantially varies depending on the structure thereof. Some examples of such compounds are shown below: Herein, R and R′ respectively denote an alkyl group. These may be classified roughly into three groups including compounds having a negatively small ( |Δε| ≦ 2), compounds having a negatively medium Δε (2 < |Δε| ≦ 10) and compounds having a negatively large Δε ( |Δε| > 10). Among these, compounds having a |Δε| of ≦ 2 have little effect of increasing |Δε|. Compounds having a |Δε| of > 10 are very effective in increasing |Δε| but those available heretofore are only dicyanohydroquinone derivatives. However, a dicyanohydroquinone derivative, while it has a large |Δε| -increasing effect, has a high viscosity, so that it is liable to degrade a switching characteristic when its content is increased. On the other hand, among the compounds having a medium |Δε| (2 < |Δε| ≦ 10), some compounds have a moderately low viscosity while their |Δε|-increasing effect is somewhat lower than those having a large |Δε|. From the above consideration, it is essential to select a compound having a negative anisotropy, preferably one having a |Δε| of > 2, and mixing it with an appropriately selected other compound in a properly selected mixing ratio. SUMMARY OF THE INVENTION An object of the present invention is to provide a chiral smectic liquid crystal composition having a large response speed and a decrease temperature-dependence of the response speed adapted for providing a practical ferroelectric liquid crystal device. Another object of the present invention is to provide a liquid crystal composition further containing a mesomorphic compound having a negative dielectric anisotropy to show an AC stabilization effect providing remarkably improved display characteristics. A further object of the present invention is to provide a liquid crystal device using such a liquid crystal composition and showing improved driving and display characteristics. According to the present invention, there is provided a ferroelectric chiral smectic liquid crystal composition, comprising at least one optically active compound represented by the following formula (I): wherein R₁ denotes a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a subtituent; X₁ denotes a single bond, -O- or Z denotes a single bond or denotes or and n is an integer of 1 - 12; and at least one compound represented by the following formula (II): wherein R₂ and R₃ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms at least one of R₂ and R₃ being optically active; X₂ and X₃ respectively denote a single bond, -O-, or According to the present invention, there is further provided a ferroelectric liquid crystal composition as described above further comprising a mesomorphic compound having a negative dielectric anisotropy, which is preferably one having a Δε < -2, more preferably Δε < -5, most preferably Δε < -10. The present invention further provides a liquid crystal device comprising a pair of substrates and such a ferroelectric liquid crystal composition as described above disposed between the electrode plates. These and other objects, features and advantages of the present invention will become more apparent upon a consideration of the following description of the preferred embodiments of the present invention taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic sectional view of a liquid crystal display device using a ferroelectric liquid crystal; Figures 2 and 3 are schematic perspective views of a device cell embodiment for illustrating the operation principle of a ferroelectric liquid crystal device; and Figure 4 is a graph showing changes in tilt angle ϑa versus effective voltage Vrms with respect to several ferroelectric liquid crystals having different values of dielectric anisotropy Δε. DETAILED DESCRIPTION OF THE INVENTION Preferred examples of the optically active compounds represented by the above-mentioned general formula (I) may include those represented by the following formulas (I-a) and (I-b). In the above-formulas (I-a) and (I-b), R₁, X₁ and n are the same as in the general formula (I). In the formula (II), R₃, R₄, X₂ and X₃ are respectively the same as in the general formula (II). Preferred examples of X₃ and X₄ may include the following combinations (II-i) to (II-viii): (II-i) X₂ is a single bond and X₃ is -O-, (II-ii) X₂ is a single bond and X₃ is (II-iii) X₂ is a single bond and X₃ is (II-iv) X₂ is a single bond and X₃ is a single bond, (II-v) X₂ is -O- and X₃ is -O-, (II-vi) X₂ is -O- and X₃ is (II-vii) X₂ is -O- and X₃ is (II-viii) X₂ is -O- and X₃ is a single bond. Further, preferred examples of R₂ and R₃ in the formula (II) may include the following combinations (II-ix) to (II-xi): (II-ix) R₂ is an n-alkyl group and R₃ is (II-x) R₂ is and R₃ is an n-alkyl group. (II-xi) R₂ is and R₃ is In the above combinations (II-ix) to (II-xi), x and y are respectively 0 - 7, and R₈ and R₉ are respectively a linear or branched alkyl group. Specific examples of the compounds represented by the above-mentioned general formula (I) may include those shown by the following structural formulas. The compounds represented by the general formula (I) may be synthesized through the following reaction scheme A, B or C. Some representative examples of synthesis of the compound represented by the general formula (I) are shown hereinbelow. Synthesis Example 1 (Synthesis of Compound Example 1-17) 1.00 g (4.16 mM) of p-2-fluorooctyloxyphenol was dissolved in a mixture of 10 ml of pyridine and 5 ml of toluene, and a solution of 1.30 g (6.0 mM) of trans-4-n-pentylcyclohexanecarbonyl chloride was added dropwise thereto in 20 - 40 min. at below 5 °C. After the addition, the mixture was stirred overnight at room temperature to obtain a white precipitate. After the reaction, the reaction product was extracted with benzene, and the resultant benzene layer was washed with distilled water, followed by drying with magnesium sulfate and distilling-off of the benzene, purification by silica gel column chromatography and recrystallization from ethanol/methanol to obtain 1.20 g (2.85 mM) of trans-4-n-pentylcyclohexanecarboxylic acid-p-2-fluorooctyloxyphenyl-ester. (Yield: 68.6 %) NMR data (ppm) 0.83 - 2.83 ppm (34H, m) 4.00 - 4.50 ppm (2H, q) 7.11 ppm (4H, s) IR data (cm⁻¹) 3456, 2928, 2852, 1742, 1508, 1470, 1248, 1200, 1166, 1132, 854. Phase transition temperature ( o C) Herein, the respective symbols denote the following phases, Iso.: isotropic phase, Ch.: cholesteric phase, SmA: smectic A phase, SmC: smectic C phase, S₃ - S₆: phases of higher other than SmC or SmC* (chiral smectic C phase), and Cryst.: crystal phase. Synthesis Example 2 (Synthesis of Compound Example 1-29) In a vessel sufficiently replaced with nitrogen, 0.40 g (3.0 mmol) of (-)-2-fluoroheptanol and 1.00 g (13 mmol) of dry pyridine were placed and dried for 30 min. under cooling on an ice bath. Into the solution, 0.69 g (36 mmol) of p-toluenesulfonyl chloride was added, and the mixture was stirred for 5 hours. After the reaction, 10 ml of 1N-HCl was added, and the resultant mixture was subjected to two times of extraction with 10 ml of methylene chloride. The extract liquid was washed once with 10 ml of distilled water and dried with an appropriate amount of anhydrous sodium sulfate, followed by distilling-off of the solvent to obtain 0.59 g (2.0 mmol) of (+)-2-fluoroheptyl p-toluenesulfonate. The yield was 66 %, and the product showed the following optical rotation and IR data. Optical rotation: IR (cm⁻¹): 2900, 2850, 1600, 1450, 1350, 1170, 1090, 980, 810, 660, 550 0.43 g (1.5 mmol) of the thus obtained (+)-2-fluoroheptyl p-toluenesulfonate and 0.28 g (1.0 mmol) of 5-octyl-2-(4-hydroxyphenyl)pyrimidine were mixed with 0.2 ml of 1-butanol, followed by sufficient stirring. To the solution was quickly added a previously obtained alkaline solution of 0.048 g (1.2 mmol) of sodium hydroxide in 1.0 ml of 1-butanol, followed by 5.5 hours of heat-refluxing. After the reaction, 10 ml of distilled water was added, and the mixture was extracted respectively once with 10 ml of benzene and 5 ml of benzene, followed by drying with an appropriate amount of anhydrous sodium sulfate, distilling-off of the solvent and purification by silica gel column chromatography (chloroform) to obtain 0.17 g (0.43 mmol) of objective (+)-5-octyl-2-[4-(2-fluoroheptyloxy)phenyl]pyrimidine. The yield was 43 %, and the product showed the following optical rotation and IR data. Optical rotation: IR (cm⁻¹) 2900, 2850, 1600, 1580, 1420, 1250, 1160, 800, 720, 650, 550. Specific examples of the compounds represented by the above-mentioned general formula (II) may include those shown by the following structural formulas. The compounds represented by the formula (II) may be synthesized through processes as disclosed by, e.g., Japanese Laid-Open Patent Applications (KOKAI) 93170/1986, 24576/1986, 129170/1986, 200972/1986, 200973/1986, 215372/1986 and 291574/1986. More specifically, for example, the following reaction scheme may be used for the synthesis: R₂, R₃ and X₃ are the same as defined above. In a preferred embodiment, the ferroelectric chiral smectic liquid crystal composition according to the present invention further comprises a mesomorphic compound having a negative dielectric anisotropy, which is preferably selected from those represented by the following formulas (III-1) to (III-5): wherein Ra and Rb respectively denote a linear or branched alkyl group capable of having a substituent; Xa and Xd respectively denote a single bond, -O-, or Xb and Xc respectively denote a single bond, or -CH₂CH₂-; Aa and Ab respectively denote a single bond, or with proviso that when Aa and Ab are both single bonds, Xb and Xc are both single bonds, and Xa and Xd are both single bonds or -O-, or Xa is and Xd is and Ya and Yb are respectively cyano group, halogen or hydrogen with proviso that Ya and Yb cannot be hydrogen simultaneously; wherein Re and Rf respectively denote a linear or branched alkyl group capable of having a substituent; Xe and Xh are respectively a single bond, -O-, or Xf and Xg are respectively or a single bond; and Ae and Af are respectively or a single bond with proviso that Ae and Af cannot be a single bond simultaneously; wherein Ai is a single bond or Aj is a single bond, or Ri and Rj are respectively a linear or branched alkyl group capable of having a substituent with proviso that Ri and Rj are linear alkyl groups when Aj is a single bond; Z₁ is -O- or -S-; Xi and Xk are respectively a single bond, -O-, or Xj is a single bond, -CH₂O- or -OCH₂- with proviso that Xi is a single bond when Ai is a single bond, Xj is not a single bond when Aj is or and Xk is a single bond when Aj is a single bond; wherein Rl and Rm are respectively a linear or branched alkyl group capable of having a substituent; Al and Am are respectively a single bond, or with proviso that Al and Am cannot be a single bond simultaneously; Xl is a single bond, -O-, or and Xm is a single bond, -CH₂O-, -OCH₂-, -CH₂CH₂- or -C≡C-; wherein Rn and Ro are respectively a linear or branched alkyl group capable of having a substituent; Xn and Xq are respectively a single bond, -O-, or Xo and Xp are respectively a single bond, -CH₂O-, -OCH₂- or -CH₂CH₂-; An and Ap are respectively a single bond, or Ao is or and Z₂ is or In the above formulas (III-1) to (III-5), the alkyl groups Ra - Ro may respectively have 1 - 18 carbon atoms, preferably 4 - 16 carbon atoms, further preferably 6 - 12 carbon atoms. Specific examples of mesomorphic compounds represented by the general formulas (III-1) to (III-5) may respectively include those denoted by the structural formulas shown below. The mesomorphic compound having a negative dielectric anisotropy Δε may preferably have Δε < -2, preferably Δε < -5, further preferably Δε < -10. The liquid crystal composition according to the present invention may be obtained by mixing at least one species of the compound represented by the formula (I), at least one species of the compound represented by the formula (II), optionally at least one species of a mesomorphic compound having a negative dielectric anisotropy and another mesomorphic compound in appropriate proportions. The liquid crystal composition according to the present invention may preferably be formulated as a ferroelectric liquid crystal composition, particularly a ferroelectric chiral smectic liquid crystal composition. Specific examples of another mesomorphic compound as described above may include those denoted by the following structure formulas. In formulating the liquid crystal composition according to the present invention, it is desirable to mix 1 - 300 wt. parts each, preferably 2 - 100 wt. parts each, of a compound represented by the formula (I) and a compound represented by the formula (II) with 100 wt. parts of another mesomorphic compound as mentioned above which can be composed of two or more species. Further, when two or more species of either one or both of the compounds represented by the formulas (I) and (II) are used, the two or more species of the compound of the formula (I) or (II) may be used in a total amount of 1 - 500 wt. parts, preferably 2 - 100 wt. parts, per 100 wt. parts of another mesomorphic compound as described above which can be composed of two or more species. Further, the weight ratio of the compound of the formula (I)/the compound of the formula (II) may desirably be 1/300 - 300/1, preferably 1/50 - 50/1. When two or more species each of the compounds of the formulas (I) and (II) are used, the weight ratio of the total amount of the compounds of the formula (I)/the total amounts of the compounds of the formula (II) may desirably be 1/500 - 500/1, preferably 1/50 - 50/1. Further, the total amounts of the compounds of the formulas (I) and (II) may desirably be 2 - 600 wt. parts, preferably 4 - 200 wt. parts, when one species each is selected from the formulas (I) and (II), or 2 - 1000 wt. parts, preferably 4 - 200 wt. parts, when two or more species are selected from at least one of the formulas (I) and (II), respectively, with respect to 100 wt. parts of the above-mentioned another mesomorphic compound which may be composed of two or more species. Further, a mesomorphic compound having a negative dielectric anisotropy as described above can be contained in a proportion of 1 - 98 wt. % of the liquid crystal composition of the present invention so as to provide a composition having a negative dielectric anisotropy. Particularly, when a mesomorphic compound having Δε < -2 is used, it may be contained in a proportion of 1 - 70 wt. %, preferably 1 - 50 wt. %, of the liquid crystal composition of the present invention. Further, the total of the compounds of the formulas (I) and (II) and the mesomorphic compound having a negative dielectric anisotropy can constitute 3 - 100 wt. % of the liquid crystal composition of the present invention. The ferroelectric liquid crystal device according to the present invention may preferably be prepared by heating the liquid crystal composition prepared as described above into an isotropic liquid under vacuum, filling a blank cell comprising a pair of oppositely spaced electrode plates with the composition, gradually cooling the cell to form a liquid crystal layer and restoring the normal pressure. Figure 1 is a schematic sectional view of an embodiment of the ferroelectric liquid crystal device prepared as described above for explanation of the structure thereof. Referring to Figure 1, the ferroelectric liquid crystal device includes a ferroelectric liquid crystal layer 1 disposed between a pair of glass substrates 2 each having thereon a transparent electrode 3 and an insulating alignment control layer 4. Lead wires 6 are connected to the electrodes so as to apply a driving voltage to the liquid crystal layer 1 from a power supply 7. Outside the substrates 2, a pair of polarizers 8 are disposed so as to modulate incident light I₀ from a light source 9 in cooperation with the liquid crystal 1 to provide modulated light I. Each of two glass substrates 2 is coated with a transparent electrode 3 comprising a film of In₂O₃, SnO₂ or ITO (indium-tin-oxide) to form an electrode plate. Further thereon, an insulating alignment control layer 4 is formed by rubbing a film of a polymer such as polyimide with gauze or acetate fiber-planted cloth so as to align the liquid crystal molecules in the rubbing direction. Further, it is also possible to compose the alignment control layer of two layers, e.g., by first forming an insulating layer of an inorganic material, such as silicon nitride, silicon nitride containing hydrogen, silicon carbide, silicon carbide containing hydrogen, silicon oxide, boron nitride, boron nitride containing hydrogen, cerium oxide, aluminum oxide, zirconium oxide, titanium oxide, or magnesium fluoride, and forming thereon an alignment control layer of an organic insulating material, such as polyvinyl alcohol, polyimide, polyamide-imide, polyester-imide, polyparaxylylene, polyester, polycarbonate, polyvinyl acetal, polyvinyl chloride, polyvinyl acetate, polyamide, polystyrene, cellulose resin, melamine resin, urea resin, acrylic resin, or photoresist resin. Alternatively, it is also possible to use a single layer of inorganic insulating alignment control layer or organic insulating alignment control layer. An inorganic insulating alignment control layer may be formed by vapor deposition, while an organic insulating alignment control layer may be formed by applying a selection of an organic insulating material or a precursor thereof in a concentration of 0.1 to 20 wt. %, preferably 0.2 - 10 wt. %, by spinner coating, dip coating, screen printing, spray coating or roller coating, followed by curing or hardening under prescribed hardening condition (e.g., by heating). The insulating alignment control layer may have a thickness of ordinarily 30 Å - 1 micron, preferably 30 - 3000 Å, further preferably 50 - 1000 Å. The two glass substrates 2 with transparent electrodes 3 (which may be inclusively referred to herein as "electrode plates") and further with insulating alignment control layers 4 thereof are held to have a prescribed (but arbitrary) gap with a spacer 5. For example, such a cell structure with a prescribed gap may be formed by sandwiching spacers of silica beads or alumina beads having a prescribed diameter with two glass plates, and then sealing the periphery thereof with, e.g., an epoxy adhesive. Alternatively, a polymer film or glass fiber may also be used as a spacer. Between the two glass plates, a ferroelectric liquid crystal is sealed up to provide a ferroelectric liquid crystal layer 1 in a thickness of generally 0.5 to 20 microns, preferably 1 to 5 microns. The ferroelectric liquid crystal provided by the composition of the present invention may desirably assume a SmC* phase (chiral smectic C phase) in a wide temperature range including room temperature (particularly, broad in a lower temperature side) and also shows wide drive voltage margin and drive temperature margin when contained in a device. Particularly, in order to show a good alignment characteristic to form a uniform monodomain, the ferroelectric liquid crystal may show a phase transition series comprising isotropic phase - Ch phase (cholesteric phase) - SmA phase (smectic A phase) - SmC* phase (chiral smectic C phase) on temperature decrease. The transparent electrodes 3 are connected to the external power supply 7 through the lead wires 6. Further, outside the glass substrates 2, polarizers 8 are applied. The device shown in Figure 1 is of a transmission type and is provided with a light source 9. Figure 2 is a schematic illustration of a ferroelectric liquid crystal cell (device) for explaining operation thereof. Reference numerals 21a and 21b denote substrates (glass plates) on which a transparent electrode of, e.g., In₂O₃, SnO₂, ITO (indium-tin-oxide), etc., is disposed, respectively. A liquid crystal of an SmC*-phase (chiral smectic C phase) in which liquid crystal molecular layers 22 are aligned perpendicular to surfaces of the glass plates is hermetically disposed therebetween. Full lines 23 show liquid crystal molecules. Each liquid crystal molecule 23 has a dipole moment (P⊥) 24 in a direction perpendicular to the axis thereof. The liquid crystal molecules 23 continuously form a helical structure in the direction of extension of the substrates. When a voltage higher than a certain threshold level is applied between electrodes formed on the substrates 21a and 21b, a helical structure of the liquid crystal molecule 23 is unwound or released to change the alignment direction of respective liquid crystal molecules 23 so that the dipole moments (P⊥) 24 are all directed in the direction of the electric field. The liquid crystal molecules 23 have an elongated shape and show refractive anisotropy between the long axis and the short axis thereof. Accordingly, it is easily understood that when, for instance, polarizers arranged in a cross nicol relationship, i.e., with their polarizing directions crossing each other, are disposed on the upper and the lower surfaces of the glass plates, the liquid crystal cell thus arranged functions as a liquid crystal optical modulation device of which optical characteristics vary depending upon the polarity of an applied voltage. Further, when the liquid crystal cell is made sufficiently thin (e.g., less than about 10 microns), the helical structure of the liquid crystal molecules is unwound to provide a non-helical structure even in the absence of an electric field, whereby the dipole moment assumes either of the two states, i.e., Pa in an upper direction 34a or Pb in a lower direction 34b as shown in Figure 3, thus providing a bistable condition. When an electric field Ea or Eb higher than a certain threshold level and different from each other in polarity as shown in Figure 3 is applied to a cell having the above-mentioned characteristics, the dipole moment is directed either in the upper direction 34a or in the lower direction 34b depending on the vector of the electric field Ea or Eb. In correspondence with this, the liquid crystal molecules are oriented in either of a first stable state 33a and a second stable state 33b. When the above-mentioned ferroelectric liquid crystal is used as an optical modulation element, it is possible to obtain two advantages. First is that the response speed is quite fast. Second is that the orientation of the liquid crystal shows bistability. The second advantage will be further explained, e.g., with reference to Figure 3. When the electric field Ea is applied to the liquid crystal molecules, they are oriented in the first stable state 33a. This state is stably retained even if the electric field is removed. On the other hand, when the electric field Eb of which direction is opposite to that of the electric field Ea is applied thereto, the liquid crystal molecules are oriented to the second stable state 33b, whereby the directions of molecules are changed. This state is similarly stably retained even if the electric field is removed. Further, as long as the magnitude of the electric field Ea or Eb being applied is not above a certain threshold value, the liquid crystal molecules are placed in the respective orientation states. When such a ferroelectric liquid crystal device comprising a ferroelectric liquid crystal composition as described above between a pair of electrode plates is constituted as a simple matrix display device, the device may be driven by a driving method as disclosed in Japanese Laid-Open Patent Applications (KOKAI) Nos. 193426/1984, 193427/1984, 156046/1985, 156047/1985, etc. Hereinbelow, the present invention will be explained more specifically with reference to examples. It is however to be understood that the present invention is not restricted to these examples. Example 1 A liquid crystal composition 1-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 1-B was prepared by mixing the following example compounds 1-8 and 2-12 with the above prepared composition 1-A. The above-prepared liquid crystal composition 1-B was used to prepare a liquid crystal device in combination with a blank cell prepared in the following manner. Two 1.1 mm-thick glass plates were provided and respectively coated with an ITO film to form an electrode for voltage application, which was further coated with an insulating layer of vapor-deposited SiO₂. The insulating layer was further coated with a 1.0 %-solution of polyimide resin precursor (SP-510, available from Toray K.K.) in dimethylacetoamide by a spinner coater rotating at 3000 rpm for 15 seconds. Thereafter, the coating film was subjected to heat curing at 300 °C for 60 min. to obtain about 120 Å-thick film. The coating film was rubbed with acetate fiber-planted cloth. The thus treated two glass plates were washed with isopropyl alcohol. After silica beads with an average particle size of 1.5 microns were dispersed on one of the glass plates, the two glass plates were applied to each other with a bonding sealing agent (Lixon Bond, available from Chisso K.K.) so that their rubbed directions were parallel to each other and heated at 100 °C for 60 min. to form a blank cell. The cell gap was found to be about 1.5 microns as measured by a Berek compensator. Then, the above-prepared liquid crystal composition 1-B was heated into an isotropic liquid, and injected into the above prepared cell under vacuum and, after sealing, was gradually cooled at a rate of 20 °C/hour to 25 °C to prepare a ferroelectric liquid crystal device. The ferroelectric liquid crystal device was subjected to measurement of an optical response time (time from voltage application until the transmittance change reaches 90 % of the maximum) at specified temperatures under the application of a peak-to-peak voltage Vpp of 25 volts. The results are shown below. 10 o C 25 o C 40 o C Response time 990 µsec 265 µsec 90 µsec Further, a contrast of 14 was attained at 25 o C during the driving, and a clear switching function was observed. Comparative Example 1 A liquid crystal composition 1-C was prepared by omitting Example compound No. 1-8 from the liquid crystal composition 1-B, i.e., by adding only Example compound No. 2-12 to the liquid crystal composition 1-A, and a liquid crystal composition 1-D was prepared by omitting Example compound No. 2-12 from the composition 1-B, i.e., by adding only Example compound No. 1-8 to the composition 1-A. Ferroelectric liquid crystal devices 1-A, 1-C and 1-D were prepared by using the compositions 1-A, 1-C and 1-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 o C 25 o C 40 o C 1-A 1600 µsec 430 µsec 120 µsec 1-C 1400 µsec 370 µsec 110 µsec 1-D 1320 µsec 340 µsec 105 µsec As apparent from the above Example 1 and Comparative Example 1, the ferroelectric liquid crystal device containing the liquid crystal composition 1-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed (ratio of response time (10 o C/40 o C)). Example 2 A liquid crystal composition 2-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 1-A prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 2-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 950 µsec 255 µsec 85 µsec Further, a contrast of 13 was attained at 25 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 2 A liquid crystal composition 2-C was prepared by omitting Example compounds Nos. 1-3 and 1-11 from the liquid crystal composition 2-B, i.e., by adding only Example compounds Nos. 2-46 and 2-80 to the liquid crystal composition 1-A, and a liquid crystal composition 2-D was prepared by omitting Example compounds Nos. 2-46 and 2-80 from the composition 2-B, i.e., by adding only Example compounds Nos. 1-3 and 1-11 to the composition 1-A. Ferroelectric liquid crystal devices 2-C and 2-D were prepared by using the compositions 2-C and 2-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 o C 25 o C 40 o C 2-C 1310 µsec 375 µsec 110 µsec 2-D 1250 µsec 315 µsec 100 µsec As apparent from the above Example 2 and Comparative Example 2, the ferroelectric liquid crystal device containing the liquid crystal composition 2-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 3 A liquid crystal composition 3-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 1-A prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 3-B was used, and the device was subjected to measurement of driving voltage margin and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 1060 µsec 285 µsec 95 µsec Further, a contrast of 14 was attained at 25 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 3 A liquid crystal composition 3-C was prepared by omitting Example compounds Nos. 1-28 and 1-48 from the liquid crystal composition 3-B, i.e., by adding only Example compounds Nos. 2-3 and 2-30 to the liquid crystal composition 1-A, and a liquid crystal composition 3-D was prepared by omitting Example compounds Nos. 2-3 and 2-30 from the composition 3-B, i.e., by adding only Example compounds Nos. 1-28 and 1-48 to the composition 1-A. Ferroelectric liquid crystal devices 3-C and 3-D were prepared by using the compositions 3-C and 3-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 o C 25 o C 40 o C 3-C 1450 µsec 390 µsec 115 µsec 3-D 1300 µsec 340 µsec 105 µsec As apparent from the above Example 3 and Comparative Example 3, the ferroelectric liquid crystal device containing the liquid crystal composition 3-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 4 A liquid crystal composition 4-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 1-A prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 4-B was used, and the device was subjected to measurement of driving voltage margin and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 945 µsec 260 µsec 85 µsec Further, a contrast of 14 was attained at 25 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 4 A liquid crystal composition 4-C was prepared by omitting Example compounds Nos. 1-31 and 1-40 from the liquid crystal composition 4-B, i.e., by adding only Example compounds Nos. 2-51 and 2-72 to the liquid crystal composition 1-A, and a liquid crystal composition 4-D was prepared by omitting Example compounds Nos. 2-51 and 2-72 from the composition 4-B, i.e., by adding only Example compounds Nos. 1-31 and 1-40 to the composition 1-A. Ferroelectric liquid crystal devices 4-C and 4-D were prepared by using the compositions 4-C and 4-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 o C 25 o C 40 o C 4-C 1420 µsec 375 µsec 110 µsec 4-D 1150 µsec 310 µsec 95 µsec As apparent from the above Example 4 and Comparative Example 4, the ferroelectric liquid crystal device containing the liquid crystal composition 4-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 5 A liquid crystal composition 5-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 5-B was prepared by mixing the following example compounds 1-8 and 2-12 with the above prepared composition 5-A. A ferroelectric liquid crystal device 5-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 5-B was used instead of the composition 1-B. The device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 1275 µsec 310 µsec 115 µsec Further, a contrast of 13 was attained at 25 o C during the driving, and a clear switching function was observed. Comparative Example 5 A liquid crystal composition 5-C was prepared by omitting Example compound No. 1-8 from the liquid crystal composition 5-B prepared in Example 5, i.e., by adding only Example compound No. 2-12 to the liquid crystal composition 5-A, and a liquid crystal composition 5-D was prepared by omitting Example compound No. 2-12 from the composition 5-B, i.e., by adding only Example compound No. 1-8 to the composition 5-A. Ferroelectric liquid crystal devices 5-A, 5-C and 5-D were prepared by using the compositions 5-A, 5-C and 5-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 5-A 2000 530 158 5-C 1810 465 145 5-D 1450 360 120 As apparent from the above Example 5 and Comparative Example 5, the ferroelectric liquid crystal device containing the liquid crystal composition 5-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 6 A liquid crystal composition 6-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 5-A prepared in Example 5. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 6-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 1250 µsec 305 µsec 115 µsec Further, a contrast of 14 was attained at 30 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 6 A liquid crystal composition 6-C was prepared by omitting Example compounds Nos. 1-3 and 1-11 from the liquid crystal composition 6-B prepared in Example 6, i.e., by adding only Example compounds Nos. 2-46 and 2-80 to the liquid crystal composition 5-A, and a liquid crystal composition 6-D was prepared by omitting Example compounds Nos. 2-46 and 2-80 from the composition 6-B, i.e., by adding only Example compounds Nos. 1-3 and 1-11 to the composition 5-A. Ferroelectric liquid crystal devices 6-C and 6-D were prepared by using the compositions 6-C and 6-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 o C 25 o C 40 o C 6-C 1820 µsec 470 µsec 145 µsec 6-D 1440 µsec 360 µsec 120 µsec As apparent from the above Example 6 and Comparative Example 6, the ferroelectric liquid crystal device containing the liquid crystal composition 6-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 7 A liquid crystal composition 7-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 5-A prepared in Example 5. A ferroelectric liquid crystal device 7-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 7-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 1160 µsec 295 µsec 110 µsec Further, a contrast of 13 was attained at 25 o C during the driving, and a clear switching function was observed. Comparative Example 7 A liquid crystal composition 7-C was prepared by omitting Example compounds Nos. 1-28 and 1-48 from the liquid crystal composition 7-B prepared in Example 7, i.e., by adding only Example compounds Nos. 2-3 and 2-30 to the liquid crystal composition 5-A, and a liquid crystal composition 7-D was prepared by omitting Example compounds Nos. 2-3 and 2-30 from the composition 7-B, i.e., by adding only Example compounds Nos. 1-28 and 1-48 to the composition 5-A. Ferroelectric liquid crystal devices 7-C and 7-D were prepared by using the compositions 7-C and 7-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 7-C 1730 450 140 7-D 1520 385 130 As apparent from the above Example 7 and Comparative Example 7, the ferroelectric liquid crystal device containing the liquid crystal composition 7-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 8 A liquid crystal composition 8-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 5-A prepared in Example 5. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 8-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 1150 µsec 285 µsec 105 µsec Further, a contrast of 14 was attained at 25 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 8 A liquid crystal composition 8-C was prepared by omitting Example compounds Nos. 1-31 and 1-40 from the liquid crystal composition 8-B prepared in Example 8, i.e., by adding only Example compounds Nos. 2-51 and 2-72 to the liquid crystal composition 5-A, and a liquid crystal composition 8-D was prepared by omitting Example compounds Nos. 2-51 and 2-72 from the composition 8-B, i.e., by adding only Example compounds Nos. 1-31 and 1-40 to the composition 5-A. Ferroelectric liquid crystal devices 8-C and 8-D were prepared by using the compositions 8-C and 8-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 8-C 1625 425 135 8-D 1500 370 125 As apparent from the above Example 8 and Comparative Example 8, the ferroelectric liquid crystal device containing the liquid crystal composition 8-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 9 A liquid crystal composition 9-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 9-B was prepared by mixing the following example compounds 1-8 and 2-12 with the above prepared composition 9-A. A ferroelectric liquid crystal device 9-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 9-B was used instead of the composition 1-B. The device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 420 µsec 110 µsec 40 µsec Further, a contrast of 13 was attained at 25 o C during the driving, and a clear switching function was observed. Comparative Example 9 A liquid crystal composition 9-C was prepared by omitting Example compound No. 1-8 from the liquid crystal composition 9-B prepared in Example 9, i.e., by adding only Example compound No. 2-12 to the liquid crystal composition 9-A, and a liquid crystal composition 9-D was prepared by omitting Example compound No. 2-12 from the composition 9-B, i.e., by adding only Example compound No. 1-8 to the composition 9-A. Ferroelectric liquid crystal devices 9-A, 9-C and 9-D were prepared by using the compositions 9-A, 9-C and 9-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 9-A 620 170 52 9-C 520 142 45 9-D 450 120 40 As apparent from the above Example 9 and Comparative Example 9, the ferroelectric liquid crystal device containing the liquid crystal composition 9-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 10 A liquid crystal composition 10-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 9-A prepared in Example 9. A ferroelectric liquid crystal device 10-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 10-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 415 µsec 100 µsec 40 µsec Further, a contrast of 14 was attained at 25 o C during the driving, and a clear switching function was observed. Comparative Example 10 A liquid crystal composition 10-C was prepared by omitting Example compounds Nos. 1-3 and 1-11 from the liquid crystal composition 10-B prepared in Example 10, i.e., by adding only Example compounds Nos. 2-46 and 2-80 to the liquid crystal composition 9-A, and a liquid crystal composition 10-D was prepared by omitting Example compounds Nos. 2-46 and 2-80 from the composition 10-B, i.e., by adding only Example compounds Nos. 1-3 and 1-11 to the composition 9-A. Ferroelectric liquid crystal devices 10-C and 10-D were prepared by using the compositions 10-C and 10-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 10-C 510 140 45 10-D 445 120 40 As apparent from the above Example 10 and Comparative Example 10, the ferroelectric liquid crystal device containing the liquid crystal composition 10-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 11 A liquid crystal composition 11-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 9-A prepared in Example 9. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 11-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 365 µsec 96 µsec 35 µsec Further, a contrast of 12 was attained at 25 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 11 A liquid crystal composition 11-C was prepared by omitting Example compounds Nos. 1-28 and 1-48 from the liquid crystal composition 11-B prepared in Example 11, i.e., by adding only Example compounds Nos. 2-3 and 2-30 to the liquid crystal composition 9-A, and a liquid crystal composition 11-D was prepared by omitting Example compounds Nos. 2-3 and 2-30 from the composition 11-B, i.e., by adding only Example compounds Nos. 1-28 and 1-48 to the composition 9-A. Ferroelectric liquid crystal devices 11-C and 11-D were prepared by using the compositions 11-C and 11-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 11-C 470 125 40 11-D 445 125 40 As apparent from the above Example 11 and Comparative Example 11, the ferroelectric liquid crystal device containing the liquid crystal composition 11-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 12 A liquid crystal composition 12-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 9-A prepared in Example 9. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 12-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 o C 25 o C 40 o C Response time 365 µsec 94 µsec 35 µsec Further, a contrast of 14 was attained at 25 o C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 12 A liquid crystal composition 12-C was prepared by omitting Example compounds Nos. 1-31 and 1-40 from the liquid crystal composition 12-B prepared in Example 12, i.e., by adding only Example compounds Nos. 2-51 and 2-72 to the liquid crystal composition 9-A, and a liquid crystal composition 12-D was prepared by omitting Example compounds Nos. 2-51 and 2-72 from the composition 12-B, i.e., by adding only Example compounds Nos. 1-31 and 1-40 to the composition 9-A. Ferroelectric liquid crystal devices 12-C and 12-D were prepared by using the compositions 12-C and 12-D, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 o C 25 o C 40 o C 12-C 530 µsec 140 µsec 45 µsec 12-D 455 µsec 119 µsec 40 µsec As apparent from the above Example 12 and Comparative Example 12, the ferroelectric liquid crystal device containing the liquid crystal composition 12-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 13 A blank cell was prepared in the same manner as in Example 1 except for omitting the SiO₂ layer to form an alignment control layer composed of the polyimide resin layer alone on each electrode plate. Four ferroelectric liquid crystal devices were prepared by filling such a blank cell with liquid crystal compositions 1-B, 1-A, 1-C and 1-D, respectively, prepared in Example 1 and Comparative Example 1. These liquid crystal devices were subjected to measurement of optical response time in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 o C 25 o C 40 o C 1-B 960 255 90 1-A 1360 355 105 1-C 1290 320 100 1-D 1530 420 120 As is apparent from the above Example 13, also in the case of a different device structure, the device containing the ferroelectric liquid crystal composition 1-B according to the present invention provided improved operation characteristic at a lower temperature and also a decreased temperature dependence of response speed. Examples 14 - 21 Liquid crystal compositions 14-B to 21-B were prepared by replacing the example compounds and the liquid crystal compositions used in Examples 1, 5 and 9 with example compounds and liquid crystal compositions shown in the following Table 1. Ferroelectric liquid crystal devices were prepared by respectively using these compositions instead of the composition 1-B, and subjected to measurement of optical response time and observation of switching states. In the devices, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown in the following Table 1. As is apparent from the results shown in the above Table 1, the ferroelectric liquid crystal devices containing the liquid crystal compositions 14-B to 21-B provided improved response speed and a decreased temperature dependence of the response speed. Example 22 A liquid crystal composition 22-B was prepared by mixing the following example compound in the indicated proportion with the liquid crystal composition 1-B prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition was used, and the device was subjected to measurement of optical response time in the same manner as in Example 1 to obtain the following results. Response time 10 o C 25 o C 40 o C 1154 µsec 294 µsec 97 µsec Then, the tilt angle of the above device was measured under right-angle cross nicols at 25 o C to provide 7.4 degrees. Further, the tilt angle of the device was again measured while being subjected to application of rectangular waveforms of ±8 V and a frequency of 60 KHz and found to be 14.2 degrees. The transmittance measured at that time was 15.0%, and a contrast of 60:1 was attained. Comparative Example 22 A liquid crystal composition 22-C was prepared in the same manner as in Example 22 except that the liquid crystal composition 1-A prepared in Example 1 was used instead of the composition 1-B to be mixed with the example compound No. 3-10 in the same proportions. Ferroelectric liquid crystal devices were prepared by using the compositions 22-C, 1-A and 1-B respectively and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. Further, the tilt angles of these devices were measured in the same manner as in Example 22. The results are shown below. Response time 10 o C 25 o C 40 o C 1-A 1600 µsec 430 µsec 120 µsec 1-B 990 µsec 265 µsec 90 µsec 22-C 1928 µsec 470 µsec 133 µsec Tilt angle (25 o C) Comp. Initial (no electric field) Under AC appln. (60 KHz, ±8 V, rectangular) 1-A 7.5 degrees 7.8 degrees 1-B 7.3 degrees 7.6 degrees 22-C 7.7 degrees 13.3 degrees As apparent from Example 22 and Comparative Example 22, the liquid crystal composition 22-B obtained by mixing a mesomorphic compound having a negative dielectric anisotropy (example compound No. 3-10) with the liquid crystal composition 1-B according to the present invention provided an improved response characteristic and also provided a remarkably improved display characteristic when used in a display method utilizing AC application (or AC stabilization). Example 23 A liquid crystal composition 23-B was prepared by mixing the following example compounds in the respectively indicated proportions with the liquid crystal composition 1-B prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition was used, and the device was subjected to measurement of optical response time in the same manner as in Example 1 to obtain the following results. 10 o C 25 o C 40 o C Response time 1130 µsec 302 µsec 102 µsec Then, the tilt angle of the above device was measured under right-angle cross nicols at 25 o C to provide 8.6 degrees. Further, the tilt angle of the device was again measured while being subjected to application of rectangular waveforms of ±8 V and a frequency of 60 KHz and found to be 13.9 degrees. The transmittance measured at that time was 15.1%, and a contrast of 63:1 was attained. Comparative Example 23 A liquid crystal composition 23-C was prepared in the same manner as in Example 23 except that the liquid crystal composition 1-A prepared in Example 1 was used instead of the composition 1-B to be mixed with the other example compounds in the same proportions. Ferroelectric liquid crystal devices were prepared by using the compositions 23-C, 1-A and 1-B respectively and subjected to measurement of driving voltage margin, otherwise in the same manner as in Example 1. Further, the tilt angles of these devices were measured in the same manner as in Example 23. The results are shown below. Response time 10 o C 25 o C 40 o C 1-A 1600 µsec 430 µsec 120 µsec 1-B 990 µsec 265 µsec 90 µsec 23-C 1767 µsec 453 µsec 129 µsec Tilt angle (25 o C) Comp. Initial (no electric field) Under AC appln. (60 KHz, ±8 V, rectangular) 1-A 7.5 degrees 7.8 degrees 1-B 7.3 degrees 7.6 degrees 23-C 8.5 degrees 13.0 degrees As apparent from Example 23 and Comparative Example 23, the liquid crystal composition 23-B obtained by mixing mesomorphic compounds having a negative dielectric anisotropy with the liquid crystal composition 1-B according to the present invention provided an improved responsive characteristic and also provided a remarkably improved display characteristic when used in a display method utilizing AC application (or AC stabilization). For example, the dielectric anisotropy Δε of a mesomorphic compound or a liquid crystal composition referred to herein may be measured in the following manner. A 5 micron-thick homogeneous alignment cell having an electrode of 0.7 cm² in area and a homogeneous alignment layer (rubbed polyimide) on both substrates, and a 5 micron-thick homeotropic alignment cell having an electrode of 0.7 cm² in area and a homeotropic alignment layer (aligning agent: "ODS-E" available from Chisso K.K.) on both substrates, are provided. The respective cells are filled with a sample liquid crystal material (compound or composition) to prepare liquid crystal devices. The capacitances of the liquid crystal layers are measured by applying a sine wave with a frequency of 100 KHz and amplitudes of ±0.5 V to the respective devices at a prescribed temperature set for the liquid crystal material, and the dielectric constants ε∥ and ε⊥ are obtained from the measured capacitance values of the respective devices, whereby the dielectric anisotropy Δε is calculated by the equation of Δε = ε∥ - ε⊥ . As described hereinabove, the ferroelectric liquid crystal composition according to the present invention provides a liquid crystal device which shows a good switching characteristic, an improved operation characteristic and a decreased temperature dependence of response speed. Further, the liquid crystal composition according to the present invention further containing a mesomorphic compound having a negative dielectric anisotropy, provides a liquid crystal device which retains the above-mentioned characteristics and further shows a remarkably improved display characteristic when used in a driving method utilizing AC stabilization. A ferroelectric chiral smectic liquid crystal composition, comprising at least one compound represented by the following formula (I): wherein R₁ denotes a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₁ denotes a single bond, -O- or Z denotes a single bond or denotes or and n is an integer of 1 - 12; and at least one compound represented by the following formula (II): wherein R₂ and R₃ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent, at lease one of R₂ and R₃ being optically active; X₂ and X₃ respectively denote a single bond, -O-, or

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, GR, IT, LI, LU, NL, SE A ferroelectric chiral smectic liquid crystal composition, comprising: at least one compound represented by the following formula (I): wherein R₁ denotes a linear or branched alkyl group having 1-18 carbon atoms capable of having a substituent; X₁ denotes a single bond, -O- or Z denotes a single bond or denotes or and n is an integer of 1-12; and at least one compound represented by the following formula (II): wherein R₂ and R₃ respectively denote a linear or branched alkyl group having 1-18 carbon atoms capable of having a substituent, at least one of R₂ and R₃ being optically active; X₂ and X₃ respectively denote a single bond, -O-, or A composition according to Claim 1, which further comprises a mesomorphic compound having a negative dielectric anisotropy. A composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -2. A composition according to Claim 3, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -5. A composition according to Claim 4, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -10. A composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy is a mesomorphic compound represented by any of the following formulas (III-1) to (III-5); wherein Ra and Rb respectively denote a linear or branched alkyl group capable of having a substituent; Xa and Xd respectively denote a single bond, -O-, or Xb and Xc respectively denote a single bond, or -CH₂CH₂-; Aa and Ab respectively denote a single bond, or with proviso that when Aa and Ab are both single bonds, Xb and Xc are both single bonds, and Xa and Xd are both single bonds or -O-, or Xa is and Xd is and Ya and Yb are respectively cyano group, halogen or hydrogen with proviso that Ya and Yb cannot be hydrogen simultaneously; wherein Re and Rf respectively denote a linear or branched alkyl group capable of having a substituent; Xe and Xh are respectively a single bond, -O-, or Xf and Xg are respectively or a single bond; and Ae and Af are respectively or a single bond with proviso that Ae and Af cannot be a single bond simultaneously; wherein Ai is a single bond or Aj is a single bond, or Ri and Rj are respectively a linear or branched alkyl group capable of having a substituent with proviso that Ri and Rj are linear alkyl groups when Aj is a single bond; Z₁ is -O- or -S-; Xi and Xk are respectively a single bond, -O-, or Xj is a single bond, -CH₂O- or -OCH₂- with proviso that Xi is a single bond when Ai is a single bond, Xj is not a single bond when Aj is or and Xk is a single bond when Aj is a single bond; wherein Rl and Rm are respectively a linear or branched alkyl group capable of having a substituent; Al and Am are respectively a single bond, or with proviso that Al and Am cannot be a single bond simultaneously; Xl is a single bond, -O-, or and Xm is a single bond, -CH₂O-, -OCH₂-, -CH₂CH₂- or -C≡C-; wherein Rn and Ro are respectively a linear or branched alkyl group capable of having a substituent; Xn and Xq are respectively a single bond, -O-, or Xo and Xp are respectively a single bond, -CH₂O-, -OCH₂- or -CH₂CH₂-; An and Ap are respectively a single bond, or Ao is or and Z₂ is or A liquid crystal device, comprising a pair of electrode plates and a ferroelectric liquid crystal composition according to any one of Claims 1 - 6 disposed between the electrode plates. Claims for the following Contracting State : ES A use of a ferroelectric chiral smectic liquid crystal composition, comprising: at least one compound represented by the following formula (I): wherein R₁ denotes a linear or branched alkyl group having 1-18 carbon atoms capable of having a substituent; X₁ denotes a single band, -O- or Z denotes a single bond or denotes or and n is an integer of 1-12; and at least one compound represented by the following formula (II): wherein R₂ and R₃ respectively denote a linear or branched alkyl group having 1-18 carbon atoms, at least one of R₂ and R₃ being optically active; X₂ and X₃ respectively denote a single bond, -O-, or in a liquid crystal device. A use of a composition according to Claim 1, which further comprises a mesomorphic compound having a negative dielectric anisotropy. A use of a composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -2. A use of a composition according to Claim 3, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -5. A use of a composition according to Claim 4, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -10. A use of a composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy is a mesomorphic compound represented by any of the following formulas (III-1) to (III-5); wherein Ra and Rb respectively denote a linear or branched alkyl group capable of having a substituent; Xa and Xd respectively denote a single bond, -O-, or Xb and Xc respectively denote a single bond, or -CH₂CH₂-; Aa and Ab respectively denote a single bond, or with proviso that when Aa and Ab are both single bonds, Xb and Xc are both single bonds, and Xa and Xd are both single bonds or -O-, or Xa is and Xd is and Ya and Yb are respectively cyano group, halogen or hydrogen with proviso that Ya and Yb cannot be hydrogen simultaneously; wherein Re and Rf respectively denote a linear or branched alkyl group capable of having a substituent; Xe and Xh are respectively a single bond, -O-, or Xf and Xg are respectively or a single bond; and Ae and Af are respectively or a single bond with proviso that Ae and Af cannot be a single bond simultaneously; wherein Ai is a single bond or Aj is a single bond, or Ri and Rj are respectively a linear or branched alkyl group capable of having a substituent with proviso that Ri and Rj are linear alkyl groups when Aj is a single bond; Z₁ is -O- or -S-; Xi and Xk are respectively a single bond, -O-, or Xj is a single bond, -CH₂O- or -OCH₂- with proviso that Xi is a single bond when Ai is a single bond, Xj is not a single bond when Aj is or and Xk is a single bond when Aj is a single bond; wherein Rl and Rm are respectively a linear or branched alkyl group capable of having a substituent; Al and Am are respectively a single bond, or with proviso that Al and Am cannot be a single bond simultaneously; Xl is a single bond, -O-, or and Xm is a single bond, -CH₂O-, -OCH₂-, -CH₂CH₂- or -C≡C-; wherein Rn and Ro are respectively a linear or branched alkyl group capable of having a substituent; Xn and Xq are respectively a single bond, -O-, or Xo and Xp are respectively a single bond, -CH₂O-, -OCH₂- or -CH₂CH₂-; An and Ap are respectively a single bond, or Ao is or and Z₂ is or A liquid crystal device, comprising a pair of electrode plates and a ferroelectric liquid crystal composition according to any one of Claims 1 - 6 disposed between the electrode plates.

Inventors: ASAOKA MASANOBU, KATAGIRI KAZUHARU, KITAYAMA HIROYUKI, SHINJO KENJI, TAKIGUCHI TAKAO, TERADA MASAHIRO, TOGANO TAKESHI, YAMASHITA MASATAKA, ASAOKA, MASANOBU, KATAGIRI, KAZUHARU, KITAYAMA, HIROYUKI, SHINJO, KENJI, TAKIGUCHI, TAKAO, TERADA, MASAHIRO, TOGANO, TAKESHI, YAMASHITA, MASATAKA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1989
Main classification: C09K19
IPC codes: C09K19, C07D285, C07D271