METHOD FOR PREPARING FLAT OR SEMI-FLAT WATER PAINTS

Abstract: Flat and/or semi-flat paints are prepared by adding as rheology- and performance-improving agents both a water-soluble nonionic cellulose ether and an associative polyurethane thickener, the weight ratio of polyurethane thickener to cellulose ether being 2:8-8:2.

Description: The present invention relates to a method for preparing flat and/or semi-flat water paints, a water-soluble nonionic cellulose ether and an associative polyurethane being added as rheology- and performance-improving agents. In the making of flat or semi-flat water paints, it is customary to use cellulose ethers as thickeners. Cellulose ethers are advantageous in that they produce the desired effect at a low cost and yield a good texture (grain). The viscosity-increasing effect is relatively unaffected by additives, such as tinting colorants. On the other hand, with increasing molecular weights cellulose ethers give relatively low viscosities at high shear rates, and poor levelling, which means inadequate hiding power. It has therefore been suggested to replace the cellulose ethers with an associative thickener of the polyurethane type. It is true that the associative polyurethanes give improved viscosity at high shear rates, but they also give a poor texture (grain), which is linked with extreme levelling. The associative polyurethanes therefore have not been commonly used as rheology- and performance-improving agents for flat or semi-flat paints. It has now been found that flat and semi-flat water paints with excellent properties can be obtained at low costs by combining a nonionic water-soluble cellulose ether with an associative polyurethane thickener, the weight ratio of polyurethane thickener and cellulose ether being 2:8-8:2. In the present context, "flat and semi-flat" paints relates to paints having a pigment volume concentration of at least 30%. By combining a nonionic water-soluble cellulose ether with an associative polyurethane thickener, it has proved possible to essentially maintain the positive characteristics of the two components while suppressing their negative characteristics. In the present context, "associative polyurethane thickener" relates to a polymer containing at least 2, suitably 3 or more hydrophobic groups having 6-30 carbon atoms with intermediate hydrophilic polyether segments, the hydrophobic groups and the hydrophilic segments being interlinked to an essential extent by urethane bonds. They usually have a molecular weight of 10,000-250,000, preferably 15,000-100,000. A large number of such compounds are known and described, e.g. in US Patent Specifications 2,946,767 and 4,079,028 and European Patent Publication 96,882, of which relevant portions are included by reference in the present specification. The water-soluble nonionic cellulose ether may have both alkyl substituents and hydroxyalkyl substituents or combinations thereof. Typical examples of suitable nonionic cellulose derivatives are methylcellulose, methylhydroxyethylcellulose, methylhydroxypropylcellulose, hydroxyethylcellulose, hydroxyethylhydroxypropylcellulose, hydroxyethylhydroxybutylcellulose, ethylhydroxyethylcellulose and propylhydroxyethylcellulose. The above-mentioned cellulose ethers may also contain a minor amount of hydrocarbon substituents having 4-20 carbon atoms, such as benzyl, dodecyl, octyl and decyl substituents, provided the cellulose ethers become water-soluble. Preferred cellulose ethers are such ethers as contain an alkyl group, such as a methyl or an ethyl group. The nonionic cellulose ethers preferably have a viscosity of 5,000-150,000 mPa·s in a 2% aqueous solution measured on a Brookfield viscometer. A suitable flocculation temperature is 50-80°C. The positive effects of the invention have been observed on paints based on a number of binders which differ essentially from each other. Suitable binders are alkyd resins and latex binders, such as polyvinylacetate, polyacrylate, copolymers of vinylacetate and acrylate, copolymers of vinylacetate and ethylene, copolymers of vinylacetate, ethylene and vinylchloride and copolymers of styrene and acrylate. The present invention is further illustrated by the following Example. Example l A flat indoor paint having a pigment volume concentration of 46% and a dry solids content of 54% by weight and containing 25% by weight of a polyacrylate binder, Rhoplex 'AC-64, alternatively a binder consisting of a copolymer of vinylacetate and acrylate, UCAR 367, was admixed with one of the additives stated below in such amounts that the paints had a viscosity of l22 KU at low shear rates measured according to ASTM C 562-8l. The following results were obtained. The indicated amounts relate to active content. The different paints were then tested for levelling according to ASTM D4062-8l, the following results being obtained. A levelling value of 3-6 gives a suitable texture for a flat or semi-flat paint. A levelling value of 9 or l0 indicates excellent levelling which is however not desirable for flat or semi-flat paints because of the resulting unsatisfactory texture. From the results appears that additives 2-l5 according to the invention, all of which have the same viscosity at low shear rates, have a levelling value essentially better adapted to flat and semi-flat paints than when polyurethane alone is used as thickener. Example 2 The same paints as in Example l were admixed with additives l, 4, 7, 9, ll, l3 or l5 according to Example l and 5% by weight, based on the weight of the paint, of any of the tinting colorants Colortrend Thalo Blue and Colortrend Lamp Black. The viscosity was thereafter determined at low shear rates. The following results were obtained. The viscosities obtained should be compared with l22 KU, which was the viscosity of the paints without the addition of a tinting colorant. From the results appears that the changes in viscosity are considerably less for additives 4, 7, 9, ll, l3 and l5 according to the invention than for reference additive l. Example 3 The same flat paints as in Example l were admixed with one of the additives stated below in such amounts that they had the same viscosity at low shear rates. The components are the same as in Example l. The compositions obtained, all of which had a viscosity of l22 KU at low shear rates, were then tested for viscosity at high shear rates using an ICI viscometer. The following results were obtained. From the results appears that in those cases where the cellulose ethers gave a viscosity which was relatively low at high shear rates, it was possible to notably improve the viscosity by adding an associative polyurethane thickener without any change of the viscosity at low shear rates.

Claims: l. Method for preparing flat or semi-flat water paints, characterised by adding as rheology- and performance-improving agents both a water-soluble nonionic cellulose ether and an associative polyurethane thickener, the weight ratio of polyurethane thickener to cellulose ether being 2:8-8:2. 2. Method as claimed in claim l, characterised in that the nonionic cellulose ether has a viscosity of 5,000-l50,000 mPa·s in a 2% aqueous solution at l2 rpm. 3. Method as claimed in claim l or 2, characterised in that the nonionic cellulose ether contains an alkyl group. 4. Method as claimed in claims l-3, characterised in that the polyurethane thickener contains at least 2 hydrophobic groups having 6-30 carbon atoms with intermediate hydrophilic polyether segments, the hydrophobic groups and the hydrophilic segments being interlinked to an essential extent by urethane bonds. 5. Method as claimed in claims l-4, characterised in that the polyurethane has a molecular weight of 10,000-250,000. 6. Method as claimed in claims l-5, characterised in that the paint contains a latex as binder.

Inventors: ANDERSSON, JOHAN, INGVARSSON, INGEMAR
Applicants: BEROL NOBEL AB
Application year: 1989
Main classification: C09D5
IPC codes: C09D7