Grinding process for high viscosity cellulose ethers

Abstract: High viscosity cellulose ether products are produced by grinding in a high speed air swept impact mill, a substantially dry, high molecular weight cellulose ether having a viscosity greater than 100 Pa.s (100,000 cps) at 20°C. These products have several times the intrinsic viscosity of a product of substantially equivalent particle size obtained by ball mill or hammer mill grinding.

Description: This invention concerns a process for preparing high viscosity cellulose ethers. Cellulose ethers such as methylcellulose and hydroxypropyl methylcellulose are used as thickeners in such diverse applications as water-based paints, foods and cosmetics. Presently, the 2 percent aqueous solution viscosities for these products range from below 5 cps (5 mPa.s) to a maximum of about 100,000 cps, (100 Pa.s) with the exact value being a function of the molecular weight of the cellulose polymer backbone in the material. In general, the greater the molecular weight of the cellulose polymer, the larger the intrinsic viscosity of the cellulose ether product. Both wood and cotton linter celluloses are used to prepare cellulose ethers, with economics favoring the use of wood pulp. The more expensive cotton linters have been required in the production of high viscosity products in the 100,000 cps (100 Pa.s) range. Cellulose ether products with intrinsic viscosities greater than 100,000 cps (100 Pa.s) would be desirable for they would provide more efficient thickening with lower raw material usage and reduced cost. Production of such high viscosity cellulose ethers has not been possible, however, due to the chemical and mechanical degradation of the cellulose polymer backbone that occurs during the manufacturing process. For example, the presence of an oxidizing agent such as air during the alkalinization and etherification steps of the process significantly reduces the viscosity of the product. Viscosity is also lost if excess caustic is not neutralized before the product is extracted and dried. Even if care is taken to exclude oxidizing agents and to neutralize excess caustic before work up, there is still a significant viscosity loss when the material is ground in a ball mill, hammer mill or disk mill to give finished product. Therefore, because significant viscosity loss occurs when the cellulose ether is ground, it is difficult to prepare a product which has small particle size and high viscosity. It would be desirable to have a process for preparing a cellulose ether product which has small particle size and minimal degradation of the cellulose polymer backbone. Thus, the resulting cellulose ether products would have higher intrinsic viscosities. This invention is directed to a process for reducing the particle size of cellulose ether without substantial change in viscosity, which comprises grinding the cellulose ether in a high speed air swept rotary impact mill, wherein prior to grinding, the cellulose ether has a viscosity greater than 100,000 cps (100 Pa.s) at 20°C. Surprisingly, it has been found that a cellulose ether product prepared under such mild mechanical conditions has a greater intrinsic viscosity compared to a product of substantially equivalent particle size produced by such methods as ball mill grinding. The invention also provides the use of a high speed air swept rotary impact mill to grind to a particle size of 40 to 400 U.S. mesh (0.4 to 0.035 mm) cellulose ether having a viscosity greater than 100,000 cps (100 Pa.s), without substantial change in said viscosity. These cellulose ether products can be employed where only small amounts of cellulose ethers are desirable, but are needed as a thickening agent. In addition, since the cellulose ethers are sensitive to shearing, these higher viscosity cellulose ethers are useful in applications where viscosity reduction is desirable. The preferred cellulose ethers used in this invention are substituted with sodium carboxymethyl, methyl, ethyl, hydroxyethyl, hydroxypropyl, hydroxybutyl groups, and combinations thereof. The more preferred cellulose ethers of this invention are substituted with methyl, hydroxypropyl, hydroxybutyl groups, and combinations thereof. The most preferred cellulose ethers of this invention are methylcellulose having a methoxyl substitution of 27 to 32 weight percent and hydroxypropyl methylcellulose having a hydroxypropyl substitution of 4 to 32 weight percent and a methoxyl substitution of 16 to 30 weight percent. In addition, the high molecular weight, high viscosity cellulose ether used in this invention prior to grinding has a viscosity greater than 100,000 cps (100 Pa.s), preferably greater than 300,000 cps (300 Pa.s) but usually within the range from 100,000 cps (100 Pa.s) to 300,000 cps (300 Pa.s) at 20°C. The mild mechanical impact conditions of this invention are defined as those conditions under which the primary breakage of a particle results from direct contact of the particles with a fast moving part of an impact grinder. Unlike hammer mills, most breakage of the particles also occurs by particle-particle contact due to high air turbulence in the high speed air swept impact mill. Typically, the smaller particles are provided by larger particles contacting only one surface at time per contact. Such conditions are encountered by utilizing a high speed air swept rotary impact mill. The particles are reduced in size by shear as they are sliced between the surfaces of the grinder. By impacting under these conditions, high viscosity cellulose ether products are formed. This mild mechanical impact mill avoids the severe mechanical degradation of the cellulose polymer backbone as seen with other methods of milling. For instance, a ball mill is a tumbling impact mill that uses hard balls, typically made of steel, as the grinding medium. In such a ball mill the primary breaking action of the particles occur as the material is caught between elements of the grinding medium or balls. The conditions of ball milling--the particle being pressed between two hard surfaces--is fundamentally different from that encountered with a high speed air swept impact mill in which the particle encounters just one hard surface during impact at a very high speed. In addition to ball mills, hammer mills are used in some grinding processes. Due to process complications, fine cellulose ether particle sizes are difficult to produce. One such problem is that hammer mills do not readily release heat and therefore tend to overheat, so it is very difficult to produce the fine particles because of thermal degradation of the polymer. In addition to overheating problems, the hammer mills do not impact to produce particle sizes that are fine and have very high viscosities. In producing these high viscosity cellulose ethers, material is fed to one or more tiers of rotating blades that are only a few millimeters from the cylindrical inner wall. The wall is usually serrated to provide surfaces for impact that are near perpendicular to the line of travel for the impacted particles. The blades are mounted on a disc so that it is only slightly smaller in diameter than the tips of the blades. Material is swept through this annulus by an air stream that is blown through the mill. A high degree of impact occurs in this annulus between the blades and the material, the inner wall and the material, and between particles. Air is the primary motivating force to move material through the mill, in contrast to a hammer mill. This air provides turbulence for particle to particle impact. It also is the heat transfer medium to remove the heat of milling. Thus, this process avoids the difficulties that are experienced with hammer mills, such as polymer degradation and fires due to insufficient heat removal. Mild mechanical impact provides a cellulose ether product with greater intrinsic viscosity compared to a product of substantially equivalent particle size produced by such methods as ball mill grinding. Preferably, such viscosity will be several times greater such as at least 1.5 times, more preferably at least 2 times, and most preferably at least 3 times the viscosity of a ball milled product. By "substantially equivalent" particle size is meant that the products are classified by passing through a sizing screen of equivalent U.S. mesh size. Generally, the high molecular weight cellulose ethers are substantially dry before mildly mechanically impacting. By "substantially dry" cellulose ether is meant that the cellulose ether has a water content of less than 3 percent by weight. This mild mechanical impacting process forms a cellulose ether product that retains a high molecular weight with substantially the same viscosity as the initial cellulose ether has before grinding. The high molecular weight, high viscosity cellulose ether product has a viscosity greater than 100,000 cps (100 Pa.s), preferably greater than 300,000 cps (300 Pa.s), but usually from 100,000 to 300,000 cps (100-300 Pa.s) at 20°C. The particle size of the cellulose ether products, after grinding, is a very fine granule, from 40 to 400 U.S. mesh (0.4-0.035 mm), preferably 80 to 325 U.S. mesh (0.2-0.045 mm). Thus, the process of this invention makes possible the production of cellulose ether products of higher intrinsic viscosities than were previously available. Such high viscosity products will provide more efficient thickening and thus reduced cost. In addition, the process of this invention makes possible the production of cellulose ether products with a viscosity from 100,000 cps to 300,000 cps (100-300 Pa.s) and greater without the use of expensive cotton linters as raw material. In addition, with the several fold increase in product viscosity that this invention provides, it is possible to use less expensive lower-molecular-weight wood pulps and still achieve cellulose ether product viscosities in this range. Example 1 An unground sample of hydroxypropyl methylcellulose was first determined to have a 2 percent aqueous solution viscosity of about 316,000 cps (316 Pa.s). The viscosity was measured by a method of using Ubbelohde tube ASTM D1347. Grinding a portion of this material without any caustic present in a MIKRO-ACM PULVERIZER rotary impact air swept impact mill to a particle size of finer than 80 U.S. mesh (0.2 mm) produced a hydroxypropyl methylcellulose product with a 2 percent solution viscosity of about 286,000 cps (286 Pa.s). Example A (Comparative) By comparison, grinding a portion of the unground material of Example 1 in a ball mill grinder of 30 foot (9 m) length and 6 foot (1.8 m) diameter containing 1.5 inch (3.8 cm) steel balls, to the same particle size of finer than 80 U.S. mesh (0.2 mm) produced a hydroxypropyl methylcellulose product with a 2 percent solution viscosity of only about 100,000 cps (100 Pa.s).

Claims: A process for preparing cellulose ether particles which comprises grinding in a high speed air swept rotary impact mill to a particle size of 0.4 to 0.035 mm (40 to 400 U.S. mesh) cellulose ether having a viscosity greater than 100 Pa.s when determined as a 2 percent aqueous solution at 20°C using Ubbelohde tube ASTM D1347. A process as claimed in Claim 1, wherein the cellulose ether is methylcellulose ether or a hydroxypropyl methylcellulose ether. A process as claimed in Claim 2, wherein the cellulose ether is a methylcellulose ether having a methoxyl substitution of 27 to 32 weight percent. A process as claimed in Claim 2, wherein the cellulose ether is a hydroxypropyl methylcellulose ether having a hydroxypropyl substitution of 4 to 32 weight percent and a methoxyl substitution of 16 to 30 weight percent. A process as claimed in any one of the preceding claims, wherein the high molecular weight cellulose ether, prior to grinding, has a viscosity from 100 to 300 Pa.s (100,000 to 300,000 cps) when determined as a 2 percent aqueous solution at 20°C using Ubbelohde tube ASTM D1347. A process as claimed in any one of the preceding claims, wherein the cellulose ether before grinding has a water content less than 3 weight percent. A process as claimed in any one of the preceding claims, wherein the cellulose ether product has a particle size of 0.2 to 0.045 mm (80 to 325 U.S. mesh). A process as claimed in any one of the preceding claims, wherein the cellulose ether is derived from wood pulp. The use of a high speed air swept rotary impact mill to grind to a particle size of 0.4 to 0.035 mm (40 to 400 U.S. mesh) cellulose ether having a viscosity greater than 100 Pa.s (100,000 cps) when determined as a 2 percent aqueous solution at 20°C using Ubbelohde tube ASTM D1347, without substantial change in said viscosity. A use as claimed in Claim 9, wherein the cellulose ether is as defined in any one of Claims 2 to 8.

Inventors: SCHULZ GARY J, SCHULZ, GARY J.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1989
Main classification: C08B11
IPC codes: C08J3, C08B11