ADSORBENT FOR METAL IONS, PROTEINS AND OTHER INORGANIC AND ORGANIC SUBSTANCES

Abstract: The invention relates to an adsorbent agent with special advantages to heavy metals, proteins etc. and is based upon a ligand with an atom sequence (A): N-C-Cn-N, wherein n is 1 or 2, and one terminal, a ring atom N in a heteroaromatic ring system, together with a proximal ring atom C forms a first terminal. The second terminal -Cn-N- can be an integral part of a heteroaromatic ring system with one or more heteroatoms and through a crosslinking bridge D is attached to P. The first terminal N-C- can be included in a pyridine or imidazole core. The polymer P is organic and hydrophilic such as polysaccharide, polyvinylalcohol, polyacrylamide, polyacrylester, polyethyleneimide or derivates thereof, and can also be immobilized by crosslinking, binding or adsorption or inclusion in an inorganic bearer.

Description: AiisorhFtn for metal ions, proteins and other inorganic and orga¬ nic substances. The present invention relates to an adsorbent for metal ions, proteins and other substances and indicates methods for adsorp- tion of heavy metals from water solutions. When certain heavy metals, such as copper, nickel and zinc, are adsorbed to the adsorbent according to the invention, a product is formed which in turn takes up organic substances from a water solution. The metal ions immobilized on the product may be used for separation of proteins from each other in blood serum, extracts from animals and plants, etc. Heavy metals can be concentrated from diluted solutions by ad¬ sorption, whereby the solutions will be liberated from the metal ions more or less effectively. This is of importance in the hydro metallurgy, but also in the control of the environment, where heavy metal pollution is an increasing problem, as well as in medical science relating to acute or chronic poisoning. Heavy metal ions immobilized to an insoluble bearer can also be used as an adsorbing agent for organic substances, and, where appli- cable, for its catalytic properties. Metal ions attached to high molecular soluble polymers also have potential new fields of application. Metal adsorption can be carried out on ion exchangers, and metal ions can be separated from each other effectively. In the hydro metallurgy among others metal chelating adsorbents are used, in which the chelate forming group often comprises dithiocarbamate, hydroxamatphenol or ketoenolate groups . Usually the chelate for¬ ming adsorbents are based upon insoluble hydrophobic bearers, e.g. cross-linked polystyrene and for analytical purposes poly- styrene derivatives of immino diacetate are suitable. Immino diacetate inserted in a hydrophilic bearer, such as aga- rose, is also used for chromatographic separations, IMAC (immobilized metal ion affinity chroamtography) or metal chelate affinity based protein chromatography. Other gel materials with other chelate forming groups have also been used. It is of importance that the chelate forming groups on the one hand bind certain heavy metals, and on the other hand have a high selectivity. According to a certain aspect of the invention with only nitrogen in the ligand, a high affinity for mercury, cadmium and copper will be reached, but a low affinity for iron. In this state with a high relative affinity for the above men¬ tioned metals, they can thus be concentrated effectively from water solutions containing iron, whereby alkali metals and earth alkali metals or aluminium do not disturb noticeably. The adsorbent according to the invention is characterized by the structure P-D-L, wherein P is a polymer, D a cross-linking bridge connecting P with a ligand comprising one or more hete- roaromatic ring systems with at least one ring nitrogen, N, which together with a proximal ring atom C establishes a termi¬ nal in an atom sequence A: N - C - C n - N, where n is 1 or 2, and the other terminal of which - C n - N - also can be included in a heteroaromatic ring system with one or more hetero atoms, and via D is bound to P, or where - C n - N is included in an exocyclic side group of the heterocyclic ring and bound to the polymer P via D. The ligand structure comprises a nitrogenic ring of aromatic character. Especially effective to bind heavy metals are pyri- dine and imidazole. These ring systems as such have low affi- nity to heavy metals such as e.g. copper ions, but the affinity may be magnified considerably by suitable substitution. In the ligand according to the invention a side group is inser¬ ted in 2-position to the ring nitrogen with a nitrogen group in the side chain, separated from the ring nitrogen by an atom se- quence of 2 or 3 carbon atoms. This substitution causes a 5- or 6- membered chelate ring to be established with a heavy metal with pronounced affinity to nitrogen atoms (metal ions of "hard" or "intermediate" type) . A heteroaromatic ring with the atom sequence A, where n = 1:. N 1 = C 2 - C 3 - N 4 can give a metal chelate ~ - - Metall and with the atom sequence A, where n = 2: N 1 = C 2 - C 3 - C 4 N 5 C 2 - C 3 - C 4 - N 5 a metal chelate i N - -Metall" Preferably the metal is "soft" or "intermediate" such as Cu 11 , Ni 11 , Cd 11 , Hg 11 or Co 11 . The affinity of Fe 111 as well as of Al 111 , Ca 11 , and "hard" metal ions is inconsiderable or non-exi-r stent, hich is of advantage in further shaping of ligands with selectivity for the soft metal ions. In the bidentate structures above, there are two atoms N 1 and N 4 ' 5 which will bind -to the metal ion. As is often.the case, if a nickel ion can bind coordinating atoms such as N or S in six positions, and thus is hexacoordinated valent but dipositiv, 3 structures A can be coordinated N Λ N N M ( N ' N N _ but if N N directly or indirectly is fixed in a polymer and the distances between all N N are sufficiently big, only an incomplete complex will be secured. The metal will be unsatura- ted with regard to N N, and that is used in IMAC. The strength by which a metal ion will be adsorbed is depending upon if N N stands close together, when in fact 2, or which is hardly likely 3 N N, are coupled to a metal ion, which then of course is bound stronger. The environment around N N alters the affinity of the metal, and usually the environment, the po¬ lymer and the bridge to the polymer consistutes an obstacle to the interaction. For metal adsorption the affinity shall be high, that is a strong bindning and a high selectivity, but at the same time the metal ion shall be easy to desorb. To remove e.g. Hg or Cu from water, the adsorbent may not be saturated by iron or aluminum. The adsorption capacity can be strengthened so that more of one metal ion is adsorbed upon a given amount of adsorbent, as well as the selectivity also can be strengthened by inserting further coordinating atoms, especially N and S (in thiol) . The strength¬ ening will be markedly more effective if these atoms are inser¬ ted so that 5- or 6-rings can be formed together with the coor¬ dinating atoms, e.g. - N - C - C - N - - N - C - C - C - N - - N - C - C - SH - - N - C - C - C - SH - The 5- and 6-rings according to the invention form metal chela- tes which are stronger than complexes with two N-atoms in other positions. As N is an integral part of a ring, e.g. pyridine or imidazole the metal chelate is more stabilized and if the heteroaromatic ring is imidazole very stable complexes are ob¬ tained. Here two structures are conceivable HN- CH HN CH f HC C-CH 2 - H 2 and H,N-CH,-C CH N N A ligand of picoline amine type can establish the copper chelate structure Cu . Still stronger chelates are acquired if the ligand has two pyri¬ dine cores The hydrogen proximal to the nitrogen in I can advantageously be substituted by some other chelate forming group, e.g. car b oxy methyl, and then a double ring chelate can be established. III Often fivemembered rings in chelates are very stable, as well as sometimes also sixmembered rings. A double ring chelate is acquired from I by processing with epichlorohydrin and subse¬ quent reaction with sodium hydrosulfide, and metal saturation will produce an interesting variant according to the invention, which together with metal is able to bind two nitrogen atoms and one sulfur atom. N. IV CH. \ CHj-CHOH If NaSH is exchanged for NH 3 is produced Me •N V ~ H„N CH. \ CH 2 _ CHOH If NH 3 is exchanged for an amine an alkyl derivative is procured which will also form a bichelate. If the amine is exchanged for an amino acid, e.g. glycine a further fivememberd ringsystem can be formed. With immino diacetic acid and heavy metals such as cobolt and zinc theoretically 4-to 5-membered rings can be for¬ med. If NH 3 is exchanged for polyamine, chelates with many rings and only nitrogen as the only metal coordinating atom can be- formed for instance with diethylene triamine and nickel ions. Bi- and trichelates with 2 respective 3 five- or sixmembered rings can be obtained by an other form of substitution in I, e.g. VII wherein X is NH 2 or SH. These ligands can be produced by alkyla- ting V with allylbromide, brominating the allyl derivative and then treating with ammonia respective NaSH (or via Bunte Saltz and reduction) . Imidazole and imidazole derivatives can take the place of the pyridine in the previous example, but according to the inven¬ tion, the side group can occupy two different positions. Formula V i ll a VHIb V IIc Among many varieties according to the invention the following ligands are suitably stated IX X XI XII wherein X is CH 2 COOH or CH - COOH CH - COOH. The chelate structure necessary for ring A can be obtained from two connected pyridine rings according to the following XIII XIV but then the attaching must be done through a side chain, e.g. via amino groups in 5-aminophenantrolin XIII - XV are bidentate ligands, which cannot be strengthened by nitrogen substitution as the case is in the previous examp¬ les. The derivatives described above, all contain the atom sequence - N - C — C - N - , wherein with the atoms numbered -N 1 - C 2 - C 3 - N 4 - , N 1 - C 2 is an integral part of an heteroaromatic core, which is an imidazole or a pyridine group in the examplified cases. This heteroaromatic group is substituted in 2-position with a side group, which can be a ring too, but also an alifatic or alifatic-aromatic chain. Further the heterocyclic ring can be substituted or coupled to some other ring, heteroaromatic or aromatic, so that for instance the following metal coordinating structures are obtained; The side group in the ligand L is attached to a polymer through a crosslinker D which in. the most simple case can be one single carbon atom with hydrogen. If by way of example a polysaccharide is oxidised with periodate links are formed with the structure XVII wherein X is CH 2 OH; COOH; CHO or CH 3 , which with picolylamine will form condensation products containing the structure X I CH - 0 / \ •0-CH CH-0- XVIII which can be reduced to -O-CH H-O- XIX \ In these cases the distance group D is CH or CH 2 . As is shown in the preceedeing examples the side group can be more complicated and further examples thereof can be stated. The polymer can be substituted with polyethyleneimin or be polyethy- lenimine itself, crosslinked or not crosslinked. If such an amine is treated with an aldehyde, for instance pyrol-2-aldehyde or pyridine-2-aldehyde by Schiff condensation is obtained the characteristic atom sequence N 1 - C 2 - C 3 - N 4 , where N 4 are con¬ verted primary aminogroups in the amine containing polymer (polyamine)-D- and after reduction with for instance NaBH > If the polyamine is treated with picolylchloride the picolyl group can be inserted at both primary and secondary aminogroups, e.g. where repeated sequences N 1 - C 2 - C 3 - N 4 are obtained in every ligand or in the polyethylene amine. Also the side group can contain derivatives of urea, thiourea, semicarbazide, biuret, etc. as well as for instance guanidine, hydrazine and hydrazinederi atives, for instance Picolyl or imide azolyl methyl groups, etc. can be inserted in the polymer too through triazine derivatives, for instance and XXII ®- H In these and similar examples the triazine structure can be in¬ terpreted as included in the ligand L or in the crosslinking bridge D. Further the adsorbent can be strengthened in other ways too. Thus the aminogroup in picolylamine for instance can be substi¬ tuted with an allylgroup and the product thereafter be brominated. XXIII With ammonia or NaSH then amino respective SH groups can be in- serted in 2- or 3-positions to N 4 . Many variations are possible. After immobilisation to a polymer tris(2-aminoethyl)amin will be an excellent starting material for alkylation with Q-CH 2 -X, where X is Cl or Br and Q is pyridine, imidazole or some other heteroaromatic ring system, which will generate the atom sequ¬ ence N 1 - C 2 - C 3 - N 4 and can form particularly strong metal ion complexes, for instance for instance N-CH 2 -CH 2 -NH- XXV A strengthened adsorption also can be obtained by condensing 2- hydroxy benzaldehyde with picolylamine to a Schiff b ase an d thereafter reducing and coupling to an activated polymer. Ni- ions then can form complex with the ligand of the structure Besides activating of the matrix with symmetric trichlorazine and direct coupling of amine to aldehyde groups sustituted in the polymer matrix this ligand can be bound in several ways such as by activating with a bifunctional reagent such as divinylsul- fone, bisepoxide or halocyan, for instance BrCN. OH-groups also can be transformed into active esters etc. Thus the activating reagent also can generate the crosslinking bridge. With divinyl- sulfone is obtainend the bridge -CH2-CH2-SO2-CH 2 -CH 2 - with butanediol diglycidylether - CH 2 -CHOH-CH 2 -0-CH 2 -CH 2 -CH 2 -CH 2 -0-CH 2 -CHOH-CH 2 - or XXVII -CH 2 -CH 2 -0-CH 2 -CH 2 -CH-CH 2 -0-CH 2 -CHOH-CH 2 - CH 3 We have investigated a number of different polymers in regard to their capacity as bearer materials for different uses . Generally the bearer material must endure the chemical and physical strains from regenerating of the adsorbent after saturation with metal ions. For treatment of industrial waters the bearer mate¬ rial, the matrix, must be cheap, whereabout more expensive mate¬ rials can be considered for laboratory and medical uses . As examples of practically usable, soluble or insoluble bearer ma¬ terials can be mentioned cellulose powder, filter paper, cotton and "wettex", crosslinked starch products and other crosslinked polysaccharides, for instance agar, agarose, crosslinked polyols such as polyvinylalcohol, crosslinked polyacrylamide, toilet sponges, etc. Advantageously the polymer also may be covalently bound to .an inorganic bearer such as silica or glass or be mixed with or bound to magnetic particles, which simplifies the sepa¬ ration of the adsorbent from the surrounding solution. For fixation of the ligand to the bearer a cheap and useful method is activation with epichlorhydrin, which gives a strong and good bond between matrix and ligand. We also have supplemen- ted vith oxidation of the polyol to aldehyde groups and conden¬ sed and reduced as Schiffs base. For matrixes with primary amino groups we also have coupled through dialdehydes . Through choosing and synthetzising of ligands then we have pro¬ duced adsorbing agents with great applicability. Heavy metals appear commonly in the environment, both naturally existing and as a result of human activities, and is a rapidly growing environmental problem which often disturbs the biolo¬ gical processes. Accumulating of the metal ions upon adsorbents is the chemically and technically most flexible method for neut- ralizing the heavy metals, and the adsorbents according to the present invention have proved to be able to adapt to most of the actual metals and needs. Even sheer medical applications have been possible, and tests have been made to adsorb bacteria, virus and different poisonous organic substances . The production of adsorbents according to the invention and their properties is described more explicit by the accompanying figure and the examples of the performance. All percentages are by weight. The figure illustrates immobilization of a heavy metal on a pro¬ duct according to the invention with dipicolylamine-Cu ++ as the ligand with an N content of 3,48 % and the amount of ligand 829 μmol/g dry gel. A chromatographic column with 1 cm diameter was filled with 2,5 g dipicolylgel, 50 μM ligand/ml gel according to Example 1, and charged with copper ions. The bed was washed with a buffer solu¬ tion containing 50 mM Na2H 0 4 and 0,5 M NaCl (to suppress ion exchange) and a pH adjusted to 7,6. NaCl was added into 2 ml human serum to a molarity of 0,5 and was filtered into the bed. The chromatogram was formed when the following solutions passed the bed in a rate of 25 ml per hour. I 50 mM aH 2 P0 4 , pH 7,6 with 0,5 mM NaCl,equilibrium buf¬ fer, II 0,5 M sodium acetate, pH adjusted to 5,5 by adding 0,5 M NaCl. III 50 μM imidazole, 50 μM NaH2 0 4 + 0, 1 M NaOH to pH 7,6 and with 0,5 M NaCl added. The figure shows the the chromatogram obtained when the eluating agent was changed as indicated by the arrows. The amount of pro- tein was measured with a spectrophotometer by the absorption at 280 nm. To get a conception of the selectivity of the protein adsorption a gelelectrophoretic analysis was made. A clear dividing of the serum proteins in three distinct groups was obtained. A more effective purification of the proteins can be obtained by gradi- entally changing of the concentration of the eluating substances (hydrogen ions, imidazole and phosphate) . ~~~ -__Ώ~_1____ . 45 ml water, 100 ml 4 M NaOH, 0,86 g sodium boron hydride and 18.75 ml epichlorhydrine were introduced into 300 g water swol¬ len, 6 % agarose (Sepharose 6 B®) in a 2 1 round flask. After stirring 2 hours at ambient temperature, further 100 ml 4 M NaOH and 100 ml epichlorhydrine were added. After reaction over night at ambient temperature, the epoxidated agar product was washed with water until a neutral reaction was obtained. To 40 g epoxidated agarose in a 500 ml round flask was introdu- ced 35 ml 1 M Na 2 _θ 3 and 1 ml picolylamine. After reaction 70 hours at ambient temperature, the gelproduct was washed succesi- vely with water, 0,1 M acetic acid and finally water. The product was tested in regard to adsorption capacity with so¬ lutions of Fe(III)chloride, Cu(II)chloride and Ni(II) sulfate. The copper ions were stronger adsorbed than the nickel and iron ions. The capacity was about 30 μmol Cu(II) per ml gel. Example 2. Into 20 g picolylamine gel according to Example 1 was introduced 15 g bromine acetic adid dissolved in 35 ml 3 M NaOH and the pH was adjusted with solid NaOH to 10,5. 35 ml 1 M sodium hydrogen carbonate with pH 10,5 was introduced and the suspension shaken for 15 hours at ambient temperature. The gel product was washed with water, 0,1 M acetic acid and water in their proper turns. The carboxy methylated picolylamine strongly adsorbed copper ions. As distinguished from the gel according to Example 1 fixed Cu(II) ions were not eluated by 1 M glycine, pH 8. Example 3. To 10 g picolylamine agarose according to Example 1 was added 0,4 ml picolylchloride dissolved in 20 ml 1 M NaHCθ 3 /Na 2 Cθ 3 , pH 10,0 and was shaken att 70°C for 1 hour. The gel was washed as in Example 1. The dipicolylaminegel fixed copper ions stronger than the pico- lylaminegel and got another color tint, more blue green than blue. Divalent copper ions, Cu 2+ , were fixed to all the three gels in water solution according to the Examples 1 - 3. Washing with 1 M glycine resulted in that the copper on the gels accor¬ ding to Examples 1 and 3 was eluated, whereas the blue zone on the gel according to Example 2 remained stationary. Similar tests were made with nickel and cobalt salts. These metal ions were adsorbed too, but weaker than copper ions. A comparison between carboxymethyl-picolylamine-agarose, "CMP"- agarose, and iminodiacetate-agarose, "IDA"-agarose, was made with regard to the capability to adsorb serum proteins and a de¬ finitive difference was noticed. The CMP-agarose not only gave a sharper separation, but the protein pattern was also different from the results from- IDA-agarose with identical test condi¬ tions. Example 4 (Picolyl-ethylenediamine) . Into 10 g cotton was introduced 30 ml 0,8 M NaOH and 3 ml bu¬ tane bis-glycidylether. After 20 hours at 27°C the cotton was separated and washed with water, Into the epoxidized cotton was introduced 35 ml 0,2 M a 2 Cθ3 adjusted to pH 10,5 with NaOH. 1 g dipicolyl ethylenediamine and 35 ml distilled water were heated to 70°C and the clear solution was added to the cotton with the sodium hydrogencarbonate solu- tion and was shaken at ambient temperature during about 70 hours. The product was washed with water, 0,1 M acetic acid and finally water, and got a strong blue color in contact with cop¬ per chloride solution. Only to a small extent the cotton was de¬ colored by 1 M glycine. Example 5 . 0,5 g bis-(2-aminoethyl) -sulfide was dissolved in 30 ml 1,0 M NaHC03 buffer, pH 10,5, and 25 g oxirane activated agarose ac¬ cording to Example 1 was added. After shaking over night the gel was separated and washed with water, 0,1 M HAc and finally wa¬ ter. The gel adsorbed Cu(II) ions but rather poorly. The gel was piocolylated according to Example 1, and thereafter the picolyltreated gel was tested with Cu(II) and adsorbed the copper ions much bette . Example 6. To 25 g epichlorhydrine treated agarose according to Example 1 was added 0,5 g 2-aminoethyl-2-pyridine dissolved in 30 ml 1 M sodiumhydrogencarbonate buffer, pH 10,5. After shaking at am¬ bient temperature over night the gel adsorbed copper ions . Example 7. 75 g epoxiagarose according to Example 1 was treated over night at ambient temperature with 3,5 g aminomethylimidazole dissolved in 80 ml 1 M a2_θ3 and was washed as in Example 1. After wash¬ ing as in the other examples the product was tested in regard to the capability to adsorb copper and nickel ions. Both ions were strongly adsorbed on the gel. The gel was carboxylated och treated with picolylchloride analo¬ gous to Examples 2 and 3, and the carboxymethylated gel adsorbed Cu(II) strongest when 1 ol glycine was used as eluent. Example 8 (Pico EDA-tris acrγl) . 100 g crosslinked polyacrylate containing hydroxyl (Trisacryl Fb 2000, IBF) was mixed with 100 ml 1 M NaOH and 10 ml epichlorhyd¬ rine, and was heated 1 hour at 40°C, whereafter further 10 ml epichlorhydrine was added. The suspension was left alone 1 hour at 40°C and then the gel was washed with 0,1 M Na 2 Cθ3 and water. The gel was divided in two parts and each part was mixed with 75 ml 1 M Na 2 _θ 3 and 2,5 g picolylchloride. The two parts were stirred, one for 20 hours and the other for 5 days. The gels were washed as in Example 1. The gel treated for a shorter time took up 39 μmol Cu(II) and the gel treated for 5 days 58 μmol. The gels were substantially blue colored. About half of the cop¬ per was eluated with 1 M glycin and the remainder was desorbed with 0,2 M ethylene diamine tetraacetic acid (EDTA) . Example 9. 30 g epoxidated 6 % agarose was washed with 0,2 M N3 2 C03 and 0,3 g 1,2-[2-(8-hydroxyquinolinyl) ]-ethylene diamine in 25 ml water was added. The suspension was heated to 95°C and held at this temperauture for 2 hours . The gel was washed with water, etha¬ nol, acetone, water, 20 % HAc and water in their proper turns. 23 μmol Cu(II) was adsorbed per ml gel, and the copper was not eluated by EDTA. Example 10, 5 g polyacrylamide with epoxigroups as reactive substituents (Eupergit®) was silted up in 25 ml 1 M a 2 -θ3 and 0,23 g 2-ami- nomethylimidazole was added. After reaction for 20 hours the gel was separated and washed with water, diluted acetic acid and fi¬ nally water as in the earlier examples. Copper ions were adsor¬ bed effectively, but were suppressed by 1 M glycine, pH 8,0. Example 11. 5 g Eupergit® was treated as above but with 0,15 g picolylamide instead of 2-aminomethyl imidazole. The product had similar pro¬ perties as the 2-aminomehtyl imidazole gel. Exampl e 12 . 1 g silica gel with attached polyethyleneimine was silted in 5 ml 1 M Na2_θ3 and 30 μl picolylamine was added. After reaction for 12 hours the gel was washed with diluted acetic acid and wa- ter. Copper ions were adsorbed strongly, which was shown in that the gel got a very dark blue color, which only to a small extent could be removed by 1 M glycine. Example 13. Synthes s of carboxvmethγl-picolγlaπ_i ne gel through hutanedi nl-his-diσlvπidγlether activation. To 100 g 6 % agarose was added 100 ml 0,6 M NaOH, pH 10,5 and picolylamine in the following amounts: a) 0,56 ml, b) 0,14 ml c) 0,07 ml d) 0,035 ml e) 0,0175 ml and f) 0,009 ml. After the samples had been shaken in a water bath over night whereupon their capabilities of taking up copper ions were tes- ted in water solution and were: a) 0,53 % b) 0,33 % c) 0,215 % d) 0,014 % e) 0,98 % and f) 0,043 %. The gel was carboxymethylated at ambient temperature with 29 ml of a solution of 19 g bromine acetic acid, 44 ml 3 M NaOH, 44 ml 1 M NaHCθ3 an d pH adjusted to 10,5. The carboxymethylation was made over night with shaking in an E-flask. A qualitative study of the strength of the copper ion bond to the picolylamine and carboxymetylated picolylaminogels was made. The copper fixed to the first gel was eluated at a lower concen¬ tration of glycine included in the buffer (0,1 M Tris HC1, pH 7,8) than in the later gel. Example 14. Synthesis of carboxymethylated picolvaminogel through divinylsufoneactivation■ To 100 g drysucked 6 % agarose was added 100 ml of 0,5 M 2 Cθ3 and 5 ml divinylsulfone and the mixture was shaken over night at ambient temperature. The gel was washed and divided into 6 samp¬ les of 19 g each. Each sample was silted in 20 ml 0,5 M NaHC03~ buffer adjusted to pH 10,5, and was treated with the following amounts of picolylamine: a) 0,76 ml, b) 0,19 ml, c) 0,09 ml, d) 0,048 ml, e) 0,024 ml and f) 0,012 ml. Carboxymethylation was made with 20 ml bromine acetic acid solu¬ tion per sample according to Example 13. The capability to take up copper ions was determined and was: a) 1,59 % b) 1,17 % c) 1,02 % d) 0,66 % e) 0,28 % and f) 0,13 %. Example 15. Bis-(2-pyridylmethyl)-aminogel produced by an other method than the gel of Example 1 . A. To 100 g 6 % agarose (Sepharose 6B) was added 25 ml water, 33 ml 4 M NaOH, 0,3 g sodium boron hydride and 1 ml epichlorhydrine in a 1 1 round flask provided with openings for- stirrer and two drop funnels with 33 ml NaOH and 33 ml epichlorhydrine. The sus- pension was stirred for 2 hours at ambient temperature, whereaf¬ ter the solutions in the drop funnels were introduced into the suspension for further 2 hours. The reaction was allowed to con¬ tinue over night, whereafter the gel was taken up in a funnel with glass filter and washed. To 20 g of the epichlorhydrine activated gel was added 1,48 ml bis-(2-pyridylmehtyl)-amine (dipicolylamine) in 2 ml ethanol and 20 ml 1 M a2Cθ3. The mixture was shaken at ambient temperature for 92 hours. B. 100 ml 1 M a 2 Cθ3 and 4 ml picolylamine were added to 40 g epoxidated agarose according to A. After 24 hours reaction time at ambient temperature and stirring the gel product was taken u on a filter and washed. To 50 g picolylamine gel were added 0,9 g picolylchlorid, 30 ml ethyleneglycol and 50 ml 1 M Na 2 Cθ 3 and adjusted to pH 11. After 6 hours on water bath at 80°C the suspension was allowed to cool down and left over night. The product was washed with wa- ter, 10 % acetic acid and water. Both A and B adsorbed Cu(II) ions. The copper was eluated slowly by 1 M glycine. Example 1 . Aminomethγlimidazolege.1 and deriva ves. 20 g 6 % agarose activated with epichlorhydrine according to Example 13 was mixed with 20 ml 0,5 M NaHCθ 3 / a 2 Cθ 3 , pH 9,8 and X g aminomethylimidazole shaken over night at ambient tempera¬ ture whereafter the gel was treated according to earlier examp¬ les. With X = 1 g, 0,4 g and 0,2 g, gels were obtained which took up 1,15 %, 0,78 % and 0,53 % Cu(II) respectively (counted on dry gel substance) . The aminomethylimidazolegels were carboxymethylated and picoly- lated according to the preceeding examples. The products adsor¬ bed copper stronger than the starting material. Example 17. Qligoethyleneaminederivated gels. 25 g bisoxirane activated gel was mixed with 30 ml 0,5 M NaHCθ 3 /Na 2 -θ 3 , pH 10 and 0,1 g NaBH and shaken for 18 hours at ambient temperature with aminomethyl-imidazole as in Example 16. The product adsorbed Cu(II). Picolylating resulted in a strongly metal adsorbing gel. Example 18. 110 g bisoxirane activated gel was treated with 112 ml 20 % wa¬ ter solution of tetraethylenepentamine for 18 hours at ambient temperature. The gel contained 3,58 % N counted on the dry sub¬ stance and took up 26 μM Cu(II) per ml gel. The gel was decolo- red by 0,1 M EDTA. The gel was carboxymethylated and picolylated as in the previous examples. The products were not decolored by EDTA. Similar synthesises and tests were made with triethylenetet- ramine, pentaethylenehexamine and bis-aminoethylsulfide. All the gels adsorbed Cu(II), the hexaminederivated gels strongest and the bis-aminoethylsulfide gels weakest. Example 19. A sheet of filter paper (Whatman 3 M) was divided in 3 pieces, each 5 x 5 cm. These pieces were laid in a covered, flat bowl with 200 ml 5 % divinylsulfone dissolved in 0,2 M N 2 Cθ3. After 18 hours the reagent solution was poured off and the paper washed. The following solutions were made: A. 100 ml 0,2 M NaHCθ3 + 0,5 g picolylaminehydrochloride B. " " " + 0,5 dipicolylamine dissolved in 10 ml ethanol. C. " " " + 0,5 g 2-aminomethyl-8- hydroquinoline dissolved in 10 ml ethanol. One paper was immersed in every solution A, B and C. After 24 hours the solutions were poured off and the papers were washed with water, alcohol and water. Pieces of the different papers were immersed in 1 % solutions of nickel sulfate, iron chloride and copper sulfate. After exposing for 1 minute the papers were washed with water, 0,1 M glycine, 1 M glycine and 0,1 M EDTA. All the papers took up metal ions which were not washed off by water. The papers treated with the solutions A and B adsorbed the metal ions very strongly, but all but the iron treated pa¬ pers were entirely decolored by 0,1 M EDTA.

Claims: C L A I M S 1. Adsorbing agent for metal ions, proteins etc., c h a ¬ r a c t e r i z e d in the structure P - D - L , wherein P is a polymer, D is a crosslinking bridge connecting P with a ligand L comprising one or more heteroaromatic ring systems with at least one ring nitrogen N 1 , which together with a proximal ring atom C 2 forms a terminal N 1 - C 2 - in an atom sequence A: N 1 - C 2 - C 3 n - C - N n+3 , wherein n is 1 or 2, the other terminal of which, - C 3 n - N n+3 - can be an integral part of a heteroaromatic ring system with one or more heteroatoms and through D is attached to P or wherein -C n - N - are included in an exocyclic side group to the heterocyclic ring and through D attached to the polymer P. 2. Product according to claim 1, c h a r a c t e r i z e d in that - N 1 - C 2 - is included in a pyridine core or an imidazole core. 3. Product according to claim 1 or 2, c h a r a c t e r i ¬ z e d in that the exocyclic side group with the crosslinking chain D has the structure X C 3 R 2 - N ^ wherein R is alkyl, Y is D or X, and X is - (C H 2 - C H 2 -NZ ) m - -Z wherein Z is H, alkyl or alkyl substituted with one or more of the groups amino, hydrazino, alifatic i ino, or nitrilo, nitro- gen-heterocyclic group, mercapto, carbonyl, thiocarbonyl, ether or thioether with the heteroatoms N and S separated by a chain of 2 or 3 carbon atoms in a sequence and m, o and p are 0, 1, 2 or more depending of the molecule. 4. Product according to claims 1 or 2, c h a r a c t e ¬ r i z e d in that the exocyclic side group with the crosslinking chain D has the structure - CR 2 - (NR) X - (CWNR) 0 - (NR)m wherein R is H or alkyl, W is 0, S or NH, x is 1 or 2, o is 0, 1 or 2 and m is 0 or 1. 5. Product according to any of the claims 1 - 4, c h a ¬ r a c t e r i z e d in an alifatic or aromatic link between D and the first terminal = N - CH 2 or N = CH in the atom sequence A in the ligand L. 6. Product according to any of the claims 1 - 5, c h a ¬ r a c t e r i z e d in that D contains one of the structures -0-CH 2--CH0H-CH--0-(CnH-xi)-0-(CH.-CH0H-CH 2_.)m-0- , -0-CH 2 -CH 2 -S0 2 -CH 2 -CH 2 -0- , . or ^ N N /^ N ^ 7. Product according to any of the claims 1 - 6, c h a - r a c t e r i z e d in that the polymer P is an organic, hydro- philic polymer belonging to one of the classes: polysaccharides such as agar, dextrane, starch or derivates thereof, polyvinyl- alcohol, polyacrylamide or polyacrylester, polyethyleneimid or derivatives thereof. 8. Product according to any of the claims 1 - 7, c h a ¬ r a c t e r i z e d in that the organic polymer has been immobilized by covalent or non-covalent binding to or included in an inorganic bearer, preferably silica gel or glass or magnetic particles or by crosslinking of the organic polymer by a bi- or polyfunctional crosslinking. 9. Method to produce an adsorbent agent for metal ions, proteins, etc. with the structure P - D - L; wherein P is a polymer, D a crosslinking bridge which connects P with a ligand L comprising one or more heteroaromatid ring systems with at least one ring atom N, which together with a proximal ring atom C forms a terminal N - C - in an atom sequence A: N - C- C n - N, wherein n is 1 or 2, the other terminal of which, - C n - N- can be an integral part of a heteroaromatic ring system with one or more heteroatoms and through D is attached to P or wherein - C n - N - are included in an exocyclic side group to the hetero- cyclic ring attached to the polymer P through D, c h a r a c ¬ t e r i z e d in that a gel is treated with a bifunctional substance, preferably a halohydrine, a bisepoxide or divinyl- sulfon in an alcaline water solution, preferably within the pH interval 8-12, whereby the gel is hydrophilic. 10. Method according to claim 9, c h a r a c t e r i z e d in that the gel is built up by a hydrophilic polymer or by a hydrophobic polymer substituted by hydrophilic groups, for instance OH- or amino- groups.

Inventors: PORATH JERKER OLOF, PORATH, JERKER, OLOF
Applicants: EXPLOATERINGS AB TBF, EXPLOATERINGS AB T.B.F.
Application year: 1989
Main classification: B01J20
IPC codes: B01J20, G01N30