Enamel frit composition for direct coating

Abstract: The present invention provides an enamel frit composition which comprises a component selected from the group consisting of SiO₂, B₂O₃, Al₂O₃, CaO, MgO, Na₂O, K₂O, Li₂O, BaO, ZnO, TiO₂ and ZrO₂, and one or more lanthanoid elements of the atomic numbers of 58 to 60 and 62 to 71 and which enables direct coating without any ground coating.

Description: BACKGROUND OF THE INVENTION The present invention relates to an enamel frit composition used for direct coating of enamel on a base material made of a metal (iron, stainless steel or the like). Conventional enamel frit compositions for base materials made of metal (iron, stainless steel or the like) contain transition metal elements such as Co, Ni or the like which produce oxidation reactions with the base metals to form Fe-Co alloys or Fe-Ni alloys (dendrite crystal) during firing of the enamel and which adhere closely to the base metals owing to such chemical bonding. During this firing adhesion process, however, the enamel includes a large amount of gases comprising hydrogen and oxygen gases generated by reaction between the metal and water in the course of firing, carbon dioxide gas generated by oxidation of the carbon present in the metals, and air captured therein. The enamel therefore suffers from the disadvantage of becoming porous. Such enamel frit compositions are generally used in the form of a ground enamel. Conventional enamel can be obtained by spraying such ground enamel several times and then spraying several cover coatings. Since the need for several sprayings of ground enamel and cover coatings leads to complication of the overall manufacturing process, industry has recently shown a tendency to demand enamel that can be provided directly on a base metal in the form of a frit composition with resistance to chemical corrosion. In order to obtain an enamel finish by direct coating without using any ground coating, a pretreatment is required in which nickel serving as an adhesive agent or an adhesion accelerator for a base metal is deposited on the surfaces of the base metal. In this pretreatment, a low carbon steel plate to be enamelled is washed with an acid so that the surfaces of the steel plate are strongly corroded by dissolving out 25 g/m² or more of the iron on the surfaces of the steel plate, and 0.6 to 1.5 g/m² of nickel is then deposited on those surfaces by using nickel treatment. Such pretreatment with a nickel metal enables enamelling having a relatively good level of adhesion to be obtained by directly spraying a cover coating, without spraying any ground coating. The enamels obtained by this method, however, do not have a level of adhesion sufficient to allow them to be used in reaction vessels or the like which are used under harsh conditions. In order to reduce the viscosity of an enamel during firing, direct ground coatings generally contain small amounts of an SiO₂ component and large amounts of R₂O (wherein R denotes an alkali metal such as Na, K, Li or the like) and B₂O₃, as well as an element such as Co, Ni, Mn or the like. The ground coatings therefore have the disadvantage that they have substantially no resistance to chemical corrosion owing to the nature of their composition. Accordingly, it is an object of the present invention to provide an enamel frit composition used for direct coating which possesses none of the above-described disadvantages. The present invention provides methods and uses as set out in the appended claims. Fig. 1 is an explanatory view of an apparatus which is used in an Ericksen test. In the figure, numeral 1 is an enamelled sample, numeral 2 is a handle, numeral 3 is a steel ball and numeral 4 is a female mold. The adhesion of an enamel frit composition used for direct coating is improved by addition of lanthanoid elements thereto. Observation of the portion where an enamel adheres to a metal surface by means of an electron microscope showed that the dendrite crystals growing from a base metal are large, long and have a very sharp form. It is estimated from this finding that such dendrite crystals significantly contribute to improvements in the degree of adhesion. Such improvements in the adhesion enable the achievement of satisfactory adhesive strength by direct coating without any need for applying a cover coating after the ground coating has been provided, as in conventional enamelling. This leads to the achievement of a reduction in the final thickness of the enamel and inevitably provides an increase in the mechanical and thermal impact strength. Examples of lanthanoid elements that may be used in direct coating enamel frit compositions include one or more elements selected from the group consisting of Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu. Of these elements samarium Sm (atomic number 62) provides particularly strong effects and is the subject of this invention. The amount of samarium to be mixed with an enamel frit composition of a type that is generally used is more than 1 to less than 20 parts by weight, preferably 3 to 10 parts by weight, more preferably 3 to 5 parts by weight, in terms of the corresponding oxide relative to 100 parts by weight of the enamel frit composition. Mixing in an amount of less than 0.01 parts by weight brings about no improvement in the adhesion and is thus undesirable, while mixing in an amount of 20 parts by weight or more is also undesirable because it causes an increase in the melting point of the enamel frit composition obtained, and thus prevents it from being easily melted at the temperatures usually used in enamel production, i.e., 1200 to 1300°C, as well as presenting the disadvantage that it will crystallize after being fritted. In the direct coating enamel composition of the present invention, the adhesion of the enamel is remarkably improved by mixing samarium and one or more elements selected from the group Co, Ni, Mn. It is assumed that this is because the latter elements function to provide an intermediate between the samarium and the base metal. Preferable combinations that exhibit significant effects include a combination of Sm and Co or Ni, and the most preferable combination is that of Sm and Co. The proportion of at least one element selected from the group consisting of Co, Ni and Mn is 0.2 to 1.5 parts by weight in terms of the corresponding oxide relative to 100 parts by weight of the enamel frit composition. As a proportion of less than 0.2 parts by weight has no effect, it is undesirable, while a proportion of over 1.5 parts by weight leads to the generation of blistering and is also undesirable. Also, since the addition of a total proportion of over 3 parts by weight of the elements causes blistering, the total proportion is preferably less than 3 parts by weight. At least one element selected from the group consisting of Co, Ni and Mn may or may not be mixed in with the above-described enamel frit composition of the type that is commonly used, and the samarium in the form of oxide is added to the mixture therewith, whereby a direct coating enamel frit composition maintaining such enamel characteristics as resistance to corrosion, good adhesion and so on can be easily produced by using a conventional electric furnace. The common enamel frit composition used in the present invention is not particularly limited so long as it comprises a component selected from the group consisting of SiO₂, B₂O₃, Al₂O₃, CaO, MgO, Na₂O, K₂O, Li₂O, BaO, ZnO, TiO₂, ZrO₂, SbO, PbO, F₂ and the like, and any suitable composition may be used. The direct coating enamel frit composition of the present invention enables the achievement of enamelling having exblisterent characteristics by spraying one or more times using commonly used direct methods, without using any ground coating under the same conditions as those employed conventionally for spraying enamels on base metals. (Examples) The direct coating enamel frit composition of the present invention is described below with reference to examples. Example 1 The compositions of the ground coating and cover coating used in the examples and comparative examples are shown in Table 1. 5 Parts by weight of one of the oxides of the lanthanoid elements (Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) was mixed with 100 parts by weight of frit powder having the cover coating composition B shown in Table 1. The thus-formed mixture was then melted at 1200°C for 2 hours, and then quenched in water to form a direct coating enamel frit composition containing the lanthanoid elements. The thus-obtained composition was then ground by a ball mill to prepare a powder having a grain size of 5 g/200 mesh/50 g, i.e. of a 50g sample subjected to a 200 mesh sieve 5g remains unpassed. Each of the frit composition powders of the samples and comparative examples (ground coating B, cover coating A and B) were then sieve-coated on a thin steel plate for enamelling having a size of 80 mm x 100 mm x 1 mm in a dry manner using a 80 mesh sieve so as to have a glass thickness of 0.3 mm respectively. After the thus-coated plate was fired at 840°C for 10 minutes, it was subjected to an Ericksen test using the apparatus shown in Fig. 1 in accordance with the method described below for the purpose of testing the adhesion of the enamels which were deep-deformed to a depth of 3 mm. The results obtained are shown in Table 2. Each of the enamelled samples (1) was erected, as shown in Fig. 1, and then deformed to a depth of about 3 mm between a female mold of 30 mm ⊘ and a steel ball (3) of 40 mm ⊘ which was put into pressure contact with each of the samples by turning a screw-type handle (2). The separated state of each enamel sample was observed. As can be seen from the results shown in Table 2, all of the samples which contain one of the lanthanoid elements exhibited excellent adhesion, as compared with the ground coating B and the cover coatings A and B of the comparative samples. The enamel surface of each of the enamelled samples containing lanthanoid elements and the comparative samples was then observed by using a scanning electron microscope (x 100, x 500) for the purpose of testing the blister properties by examining the state wherein blisters occur in a unit area (4 mm²) of the enamel surface using the following ranges of blister diameters: 100 µm diameter 100 to 150 µm diameter 150 to 300 µm diameter 300 to 500 µm diameter The results obtained are shown in Table 2. As can be seen from Table 2, each of the samples containing lanthanoid elements had blisters numbering less than in the comparative samples. In particular, since no occurrence of blisters having diameters of 100 µm or more was observed in any of the samples respectively containing the oxides of Pr, Nd, Sm, Gd and Er, these samples were significantly dense. Example 2 In order to examine the effect of the addition of samarium and Co or Ni, samples of the direct coating enamel frit composition of the present invention were prepared by using various proportions of Sm₂O₃ relative to 100 parts by weight of the frit powder of the cover coating B shown in Table 1 and using the ingredients in the proportions shown in Table 3 by the same method as employed in Example 1. Enamels were produced by the same method as employed in Example 1 and then measured with respect to their adhesion and blister properties by the same method as employed in Example 1. The results obtained are shown in Table 3. The criteria for the evaluation of adhesion and blister properties were the same as those described in Table 2. In the specification the word lanthanoid is to be taken as meaning lanthanide.

Claims: A method for coating metal with enamel by applying directly to the metal a frit composition comprising:- i) one or more components selected from the group consisting of SiO₂, B₂O₃, Al₂O₃, CaO, Na₂O, K₂O, Li₂O, TiO₂, and ZrO₂; ii) and samarium oxide present in the amount 3 to 5 weight percent. A method as claimed in claim 1 in which the frit composition contains one or more additional elements selected from the group Co, Ni, Mn. A method as claimed in claim 2 in which the one or more additional elements comprise one or both of the groups Co or Ni. A method as claimed in claim 3 in which the additional elements comprise Co. A method as claimed in any of claims 2 to 4 in which the additional elements selected from the group Co, Ni, Mn, are present as an oxide and are present in the amount less than 3 weight percent. A method as claimed in claim 5 in which the additional elements are present in the amount 0.2 to 1.5 weight percent. Use for the purpose of improving adherence of an enamel to metal of samarium oxide in the amount 3 to 5 weight percent in an enamel frit composition comprising one or more components selected from the group consisting of SiO₂, B₂O₃, Al₂O₃, CaO, Na₂O, K₂O, Li₂O, TiO₂ and ZrO₂. A use as claimed in claim 7 in which the frit composition contains one or more additional elements selected from the group Co, Ni, Mn. A use as claimed in claim 8 in which the additional elements selected from the group Co, Ni, Mn, are present as an oxide and are present in the amount less than 3 weight percent, preferably 0.2 to 1.5 weight percent.

Inventors: IIZAWA YOSHIHIRO, KASAJIMA TOSHIYUKI, SHIMIZU TADAO, IIZAWA, YOSHIHIRO, KASAJIMA, TOSHIYUKI, SHIMIZU, TADAO
Applicants: IKEBUKURO HORO KOGYO CO, IKEBUKURO HORO KOGYO CO. LTD.
Application year: 1989
Main classification: C03C8
IPC codes: C03C8