TRANSDERMAL ESTRADIOL DELIVERY SYSTEM

Abstract: A pressure-sensitive adhesive sheet material for delivering estradiol to skin, the sheet material comprising a backing with a layer of a pressure-sensitive adhesive adjacent thereto, said pressure-sensitive adhesive layer comprising a pressure-sensitive adhesive polymer, two or more skin penetration-enhancing ingredients and estradiol. The sheet material is useful for systemic treatment of conditions associated with estradiol deficiency. Methods of using such adhesive sheet material are also described.

Description: ^TRANSDERMAL ESTRADIOL DELIVERY SYSTEM^ Technical Field This invention relates to a pressure-sensitive adhesive sheet material containing estradiol in the adhesive portion of the sheet material. This invention further relates to a method of treating conditions associated with estradiol deficiency, such as osteoporosis and headaches, nausea, depression, hot flashes or other discomforts that often occur during menopause. Background of the Invention Estradiol is a natural estrogen which has limited oral effectiveness because it is rapidly metabolized by the liver to estrone and its conjugates, giving rise to higher circulating levels of estrone than estradiol. In contrast, the skin metabolizes estradiol only to a small extent. Therefore, transdermal administration produces therapeutic serum levels of estradiol with lower circulating levels of estrone and estrone conjugates, and requires smaller total doses than does oral therapy. Since estradiol has a short half-life (about one hour), transdermal administration of estradiol allows a rapid decline in blood levels after a transdermal system is removed. Estraderm R is an estradiol transdermal system available from CIBA Pharmaceutical Company. This system comprises four layers: a transparent polyester film; a drug reservoir of estradiol and alcohol gel with hydroxypropyl cellulose; an ethylene-vinylacetate copolymer membrane; and an adhesive formulation of light mineral oil and polyisobutylene for adhering the patch to skin. Japanese Application 57075917 describes the manufacture of a tacky tape for use with a variety of sex hormones including valeric acid-estradiol . The tape is prepared by (1) copolymerizing (a) 60-98 parts by weight of dodecyl methacrylate, (b) 2-40 pts. wt. of a functional monomer and (c) 0-40 pts. wt. of at least one short chain unsaturated monomer selected from vinyl acetate, an alkyl acrylate, and an alkyl methacrylate; (2) combining the drug with the copolymer; and (3) spreading the resulting composition onto base material. U. S. Patent 3,598,123 describes a medical bandage for use with a variety of drugs including estradiol. The bandage comprises: a backing member and a layer of pressure-sensitive adhesive containing a plurality of discrete microcapεules containing the drug. Acrylic adhesives are specifically mentioned. U.S. Patent No. 4,460,372 describes a transdermal device comprising a backing and an adhesive layer, the adhesive layer containing both estradiol and a microencapsulated percutaneous absorption enhancer such as ethanol. GB Application 2158355 describes an estradiol containing transdermal dosage form comprising: a solid non-polymeric gel; a mixture of propylene glycol and glycerin; the therapeutic agent dispersed in the solvent mixture; and a thin, flexible, non-polymeric matrix in planar form. The mixture of propylene glycol and glycerine is described as enhancing the skin penetration of the therapeutic agent. U.S. Patent Nos. 3,598,122, 4,379,452, 4,573,996, 4,585,454, 4,624,665, and 4,460,372 (also mentioned above) all describe estradiol transdermal patches which include layers in addition to a backing and an adhesive layer. For example, many of these patents describe patches comprising a backing, a drug reservoir layer; a semipermeable membrane; and an adhesive layer coated on the exterior surface of the semipermeable membrane. Said U.S. Patent No. 4,573,996 discloses a variety of penetration enhancers in Col. 11, lines 44-68. European Application 86.902978.5 describes a transdermal nitroglycerin delivery system comprising a flexible backing and a pressure-sensitive adhesive coating comprising an acrylic polymer and nitroglycerin. The adhesive coating may also comprise a skin penetration enhancing combination comprising a fatty acid ester of a fatty acid and glyceryl monolaurate. U.S. Patent No. 4,722,941 discloses transdermal and oral formulations employing a fatty acid of medium chain length and optionally a monoglyceride of a saturated or unsaturated fatty acid of about 6 to 18 carbon atoms to enhance drug absorption. The formulations may include a steroid. Glyceryl monolaurate, isopropyl myriεtate and ethyl oleate are known enhancers for transdermal administration of medicaments. BRIEF SUMMARY OF THE INVENTION The present invention provides a novel adhesive-coated sheet material comprising: a) a flexible backing; and b) a pressure-sensitive adhesive-coating contiguousl adhered to one surface of said backing and comprising a homogeneous mixture of: i) an acrylic polymer comprising at least about 91 t 98 percent by weight of a hydrophobic monomeric acrylic or ethacrylic acid ester of an alkyl alcohol based on the weight of all monomers in th polymer, the alkyl alcohol containing 4 to 10 carbon atoms; ii) estradiol in an amount by weight of about 0.2 to percent of the total weight of the adhesive coating; and iii) a skin penetration enhancer combination comprisin isopropyl myristate and glyceryl monolaurate in amounts of about 5 to 20 percent and about 1 to 6 percent by weight, respectively, based on the weight of the adhesive-coating with the relative amounts being selected so as to enhance the penetration of the estradiol through skin as compared to when the adhesive coating is free of said skin penetration enhancers; the sheet material being suitable for substantially continuous transdermal delivery of estradiol to a subject over a prolonged period in an amount which is therapeutical effective for treating a condition associated with estradio deficiency. The present invention also provides a novel adhesive-coated sheet material comprising: a) a flexible backing; and b) a pressure-sensitive adhesive-coating contiguousl adhered to one surface of said backing and comprising a homogeneous mixture of: i) an acrylic copolymer comprising (1) about 60 to 8 percent by weight of a hydrophobic monomeric acrylic or methacrylic acid ester of an alkyl alcohol based on the weight of all of the monomer in the copolymer, the alkyl alcohol containing 4 10 carbon atoms; (2) about 4 to 9 percent by weig based on the weight of all of the monomers in the copolymer of a reinforcing monomer selected from the group consisting of acrylic acid, methacrylic acid, an alkyl acrylate or methacrylate containin 1 to 3 carbon atoms in the alkyl group, acrylamid methacrylamide, a lower alkyl-substituted acrylamide, diacetone acrylamide, and a N-vinyl-2 pyrrolidone; and (3) about 15 to 35 percent by weight of vinyl acetate based on the weight of al of the monomers in the copolymer; ii) estradiol in an amount by weight of about 0.2 to percent of the total weight of the adhesive coating; and iii) a skin penetration enhancer combination comprisin isopropyl myristate and glyceryl monolaurate in amounts of about 5 to 20 percent and about 1 to 6 percent by weight, respectively, based on the weight of the adhesive coating, with the relativ amounts being selected so as to enhance the penetration of the estradiol through skin as compared to when the adhesive coating is free of the skin penetration enhancers; the sheet material being suitable for substantially continuous transdermal delivery of estradiol to a subject over a prolonged period in an amount which is therapeutica effective for treating a condition associated with estradi deficiency. In preferred embodiments of the invention, the skin penetration enhancer combination further contains ethyl oleate. BRIEF DESCRIPTION OF THE DRAWING The invention may be better understood by reference to the accompanying drawing wherein: The drawing is an isometric view of a diffusion cell f measuring flux of estradiol across mammalian skin. DETAILED DESCRIPTION OF THE INVENTION The present invention relates to pressure-sensitive adhesive sheet materials comprising a backing and a layer o pressure-sensitive adhesive containing estradiol coated thereon. Further, this invention relates to a method of treating conditions associated with estradiol deficiency. By "treating a condition associated with estradiol deficiency" as used in the instant specification and claims is meant administering a dose of estradiol in an amount and at a rate which eliminates or reduces the occurrence of one or more of the following conditions: osteoporosis, headaches, nausea, depression, hot flashes and any other discomfort that occurs during menopause. By "prolonged period" as used in the instant specification and claims is meant for a period of at least 12 hours. The adhesiveε utilized in the practice of the inventio should be substantially chemically inert to estradiol. Suitable acrylic adhesive polymers for use in one embodimen of the invention comprise in an amount of about 91 to 98 percent by weight, and preferably about 94 to 98 percent by weight, respectively, of all monomers in the polymer of a hydrophobic monomeric acrylic or methacrylic acid ester of alkyl alcohol, the alkyl alcohol containing 4 to 10 carbon atoms. Examples of suitable monomers are those discussed below in connection with the "A Monomer". These adhesive polymers further comprise minor amounts of other monomers such as the "B Monomers" listed below. Preferred adhesives are acrylic pressure-sensitive adhesive copolymerε comprising A and B monomers as follows: Monomer A is a hydrophobic monomeric acrylic or methacrylic acid ester of an alkyl alcohol, the alkyl alcohol containin 4 to 10 carbon atoms, preferably 6 to 10 carbon atoms, more preferably 6 to 8 carbon atoms, and most preferably 8 carbo atoms. Examples of suitable A monomers are n-butyl, n-pent n-hexyl, isoheptyl, n-nonyl, n-decyl, isohexyl, 2-ethyloct iεooctyl and 2-ethylhexyl acrylateε. The moεt preferred A monomer iε iεooctyl acrylate. Monomer B iε a reinforcing monomer εelected from the group conεisting of acrylic acid; methacrylic acid; alkyl acrylates and methacrylates containing 1 to 3 carbon atoms the alkyl group; acrylamide; methacrylamide; lower alkyl-subεtituted acrylamideε (i.e. the alkyl group containing 1 to 4 carbon atomε) εuch aε tertiary-butyl acrylamide; diacetone acrylamide; n-vinyl-2-pyrrolidone ; vinyl etherε εuch aε vinyl tertiary-butyl ether; εubεtitute ethyleneε εuch aε derivatives of maleic anhydride, dimethyl itaconate and monoethyl formate and vinyl perfluoro-n-butyrate. The preferred B monomers are acrylic acid, methacrylic acid, the above-described alkyl acrylateε and methacrylates, acrylamide, methacrylamide, and the above-described lower alkyl substituted acrylamideε. The mo preferred B monomer is acrylamide. The B monomer in such a copolymer iε present in the pressure-εenεitive adheεive copolymer in an amount by weigh of about 2 to 9 percent by weight, and preferably about 2 t 6 percent by weight of the weight of all monomers in the copolymer. In another embodiment of the invention, the acrylic copolymer compriεeε about 60 to 80 percent by weight (and preferably about 70 to 80 percent by weight) of the above-mentioned hydrophobic monomeric acrylic or methacryli acid ester of an alkyl alcohol based on the weight of the monomers in the copolymer; about 4 to 9 percent by weight based on the weight of all monomers in the copolymer of a reinforcing monomer selected from the group consisting of acrylic acid, methacrylic acid, an alkyl acrylate or methacrylate containing 1 to 3 carbon atoms in the alkyl group, acrylamide, methacrylamide, a lower alkyl-subεtitute acrylamide, diacetone acrylamide and N-vinyl-2-pyrrolidone; and about 15 to 35 percent by weight (and preferably about to 25 percent by weight) of vinyl acetate based on the weig of all monomers in the copolymer. In this embodiment the preferred acrylic or methacrylic acid ester is isooctyl acrylate and the preferred reinforcing monomer iε acrylamid Uεe of vinyl acetate in preparing the acrylic polymer iε a convenient way to reduce the amount of reεidual monomer in the final preparation aε haε been deεcribed in U.S. Patent No. 4,737,577. The adheεive copolymerε of the above type are known an their method of preparation is well known to those skilled i the art, having been deεcribed for example, in U.S. Patent 24,906 of Ulrich, incorporated herein by reference. Since t presεure-εenεitive adheεiveε deεcribed above are inherently rubbery and tacky and are εuitably heat and light εtable, there iε no need to add tackifierε or εtabilizerε. However, εuch may be added if deεired. The estradiol iε present in the adheεive in a pharmaceutically effective amount. Generally thiε amount wil be from about 0.2 to 12 percent by weight of the total weigh of the preεsure-senεitive adhesive layer of the sheet material, and will preferably be about 1 to 5 percent by weight. The most preferred is an amount of about 2 to 3.5 percent by weight. It has been found that the addition of certain skin penetration enhancers significantly enhances the penetratio of estradiol in vitro when this phenomena iε measured using the hairless mouse εkin model as deεcribed hereinbelow. Hence, the adheεive sheet material of the invention haε an adhesive coating comprising a combination of two or more ingredients in an amount effective to enhance the penetrati of estradiol through skin aε compared to when said adheεive coating iε free of the εkin penetration enhancers. More specifically, the adhesive-coating compriseε iεopropyl myriεtate and glyceryl monolaurate aε penetration enhancerε. In a preferred embodiment, the adhesive-coating additionally compriseε ethyl oleate. The iεopropyl myristate will generally be present in a amount of about 5 to 20 percent by weight, and preferably about 5 to 15 percent by weight, of the total weight of the adheεive coating and the glyceryl monolaurate will generall be preεent in an amount of about 1 to 6 percent, and preferably about 2 to 4 percent by weight. When the adheεive-coating additionally containε ethyl oleate, ethyl oleate will generally be preεent in an amount by weight of about 4 to 18 percent, and preferably about 5 to 15 percent baεed on the weight of the adheεive coating. When ethyl oleate iε present the total weight of ethyl oleate and isopropyl myristate will not exceed about 25 percent by weight of the adheεive-coating. A εuitable glyceryl monolaurate iε that commercially available from Lauricidin Inc. (Monroe, Michigan) under the trade deεignation Lauricidin (diεtilled monoglyceride ) . The backing of the tape may be occluεive, non-occluεive or breathable film. The backing may be any of the normal materialε for preεεure-εenεitive adhesive tapes such as polyethylene, particularly low-density polyethylene, linear low denεity polyethylene, high denεity polyethylene, randomly-oriented nylon fiberε, polypropylene, ethylene-vinylacetate copolymer, polyurethane, rayon and like. The backing εhould be εubεtantially non-reactive wi estradiol. The presently preferred backing iε low denεity polyethylene. Low denεity polyethylene backingε provide a excellent barrier to loεε of eεtradiol when uεed with the adheεive formulationε of the invention, including thoεe formulationε which contain a skin penetration enhancer. Backingε which are layered εuch as polyethylene- aluminum-polyethylene composites are alεo εuitable. Although animal εkinε are known to give εignificant quantitative differences in drug penetration rates versus human skin, the rank order correlation is generally obser with various drugε (M. J. Bartek and J. A. LaBudde in "Ani Modeε in Dermatology", H. Maibach, Ed. Churchill Livingεto New York, 1975, pp. 103-119). Hairleεε mouse skin has been recommended as a readily available animal skin for use in diffuεion cells with steroidε and εmall moleculeε (R. B. Stoughton, Arch. Derm., 99_, 753 (1969), J. L. Cohen and R. Stoughton, J. Invest. Derm., j^2, 507 (1974), R. B. Stought in "Animal Modeε in Dermatology", H. Maibach, Ed., Churchi Livingεtone, New York, 1975, pp. 121-131). In the εpecific test procedure used herein, skin remo from female hairless mice (available from Jackson Laborato Strain HRS/J, age 2-5 months) is used. It is maintained on ice until used. The mouse εkin is cut in half and each hal iε mounted, or the εkin iε uεed whole, on a diffuεion cell the type shown in the drawing. The cell is modeled after those described in the literature (e.g. J. L. Cohen, R. B. Stoughton, J. Invest. Derm. 6_2 507 (1974) and R. B. Stoughton, Arch. Derm. 9_9, 753 (1964). As shown in the figure, the mouse or human εkin (20) iε mounted epidermal εide up between the upper and lower portionε of the cell ( and (22), which are held together by meanε of a ball joint clamp (23). The cell below the εkin is filled with 30% N-methyl-2-pyrrolidone in water to act aε the "acceptor" fluid. The acceptor fluid iε εtirred uεing a magnetic εtirring bar (24) and a magnetic εtirrer (not illuεtrated) . The εampling port (25) iε εtoppered except when in uεe. A known amount of a formulation to be evaluated iε applied to the epidermal (upper) εide of the εkin in a uniform layer aε follows: The desired area and weight of a sheet material formulation is accurately determined so tha the amount of adhesive applied to the cell can be accurate determined. The sheet material iε applied to the skin alre mounted on the diffuεion cell and preεsed to cause uniform contact to the skin. The cell is then placed in a constant temperature (31 33 C) constant humidity chamber (generally maintained at humidity between 40 and 50%, preferably about 50%) and kep there throughout the experiment. The chamber utilizes a heat exchanger coupled to a constant temperature bath, wit fan to circulate air. A saturated calcium nitrate solution uεed to maintain the humidity. The acceptor fluid iε εtirr by means of a magnetic stirring bar throughout the experim to asεure a uniform sample and a reduced diffusion layer o the dermal side of the εkin. The acceptor fluid iε removed specified time intervals and fresh fluid is immediately ad to replace the withdrawn fluid. The withdrawn aliquots are analyzed for drug content by conventional high preεεure liquid chromatograpy and the cumulative amount of the drug penetrating the εkin iε calculated. Plotε of the cumulativ drug penetration aε a function of time give a profile of t drug flux meaεured in microg/cm /hour. The uεe of other εkin εuch aε human εkin in the above apparatuε has confirmed the utility of the formulations of the invention. The sheet materials of the present invention are preferably prepared by combining dry adhesive, estradiol a the εkin penetration enhancers with an organic solvent. Preferred organic solventε are methanol and ethyl acetate. The total solids content will be in the range of about 15 40% and preferably about 20 to 35%. The reεulting mixture shaken at a high εpeed until a homogeneous solution is obtained and then allowed to εtand to diεεipate air bubble The reεulting formulation may be wet caεt or coated by wet-cast or knife coating techniques to provide a predetermined uniform thickneεε of the wet adheεive formulation onto a εuitable releaεe liner. Thiε εheet iε t dried and laminated onto a backing material using conventional methodε. Suitable release liners are known εilicone-type releaεe linerε εuch as that available under trade deεignation Daubert 164, from Daubert Co. which are coated onto polyeεter film. The adheεive coated εheet material of the invention may be in the form of a tape, a patch, a εheet, a dresεing or other forms known to the art will be apparent to one skilled in the art. Preferably, the adhesive coated εheet material will contain about 0.2 to 7. mg, and preferably about 1.0 to 2.0 mg, of eεtradiol per 5 cm of the εheet material. Further, the sheet material will generally be about 1 to 40 cm 2 , and preferably 10 to 30 cm 2 in dimension. Generally, a transdermal patch of the invention will b applied to the εkin of a mammal (preferably a human) and wi be replaced with a freεh patch aε required to maintain the therapeutic effect. Those εkilled in the art may eaεily determine the frequency at which the patcheε of the inventi εhould be replaced to achieve the deεired therapeutic effect. The following exampleε are provided to illuεtrate the invention, but are not intended to be limiting thereof. Par and percentageε are by weight unleεε otherwise specified. Flux rates are expressed in units of micrograms of eεtradio per cm 2 for the time period εpecified in the example. Each reεult repreεentε the average value of several (e.g., 3 to independent determinationε . Inherent Viscosity Measurement In the examples which follow, it iε uεeful to refer to the molecular weight of the adhesive polymer uεed in the adheεive formulations. The comparative molecular weights a determined by meaεuring the viεcoεity of dilute solutions o the adhesiveε prepared according to theεe teachingε. The inherent viscosity values which are reported in th examples which follow were obtained by the conventional method used by those skilled in the art. The measurement o the viscoεity of dilute εolutionε of the adheεive, when compared to controlε run under the same conditions, clearly demonstrates the relative molecular weights. It iε the comparative valueε which are εignificant and abεolute figur are not required. In the examples, the inherent viscosity values were obtained using a Cannon-Fenske #50 viscometer i a water bath controlled at 25°C to measure the flow time of 10 ml of a polymer solution. The exampleε and controls bei run for comparison were run under identical conditions. Th test procedure followed and the apparatus used are explaine in detail in the Textbook of Polymer Science, F. W. Billmeyer, Wiley-Interscience, 2nd Edition, 1971 under: Polymer chainε and their characterization, D. Solution Viεcoεity and Molecular Size, pages 84 and 85. Preparation of Isooctyl Acrylate: Acrylamide (94:6) Copolymer To a 114 gram narrow-mouth glass bottle were added: 127.84 g. isooctyl acrylate, 8.6 g. acrylamide, 0.41 g. benzoyl peroxide, 237.6 g. ethyl acetate and 26.4 g. methyl alcohol. The solution was purged for two minutes with nitrogen at a flow rate of one liter per minute. The bottl was sealed and placed in a rotating water bath at 55°C for twenty four hours to effect essentially complete polymerization. The polymer was diluted with ethyl acetate/methyl alcohol (90/10) to 28.4% solids and had. a measured inherent viεcoεity of 1.02 dl/g. in ethyl acetate a concentration of 0.15 g/dl . Itε Brookfield viεcoεity wa 9,120 centipoiεe. Preparation of Iεooctyl Acrylate: Acrylamide (95:5) Copolymer The procedures above were repeated, this time employi 152.00 g. isoctyl acrylate, 8.0 g. acrylamide, 0.48 g. benzoyl peroxide, 216.0 g. ethyl acetate and 24.0 g. methy alcohol. The reεulting polymer was diluted with the ethyl acetate/methyl alcohol mixture to 29.38% solids. The poly had a measured inherent viεcoεity of 1.32 dl/g in ethyl acetate at a concentration of 0.15 g/dl. Itε Brookfield viεcoεity waε 9,900 centipoise. A 25-30 percent solidε solution of the above isooctyl acrylate:acrylamide (94:6) adhesive copolymer or the above isooctyl acrylate: acrylamide (95:5) adhesive copolymer in ethyl acetate/methanol (90:10) waε coated onto a 2-sided release liner using a knife-coater and coating at 20 milε i thickness. The adhesive-coated laminate was dried first a 180° F for 3 minutes and then at 240° for 3 minutes. The dried adhesive coating was then stripped off the release liner and placed into a small glass bottle. The foregoing procedure results in a reduction of the amount of residual monomer which may be contained in the adhesive copolymer. Preparation of Isooctyl Acrylate: Acrylamide: Vinyl Acetate (75:5:20) Copolymer The procedures above were repreated this time employin 120.0 g. isooctyl acrylate, 8.0 g. acrylamide, 32.0 g. viny acetate, 0.32 g. benzoyl peroxide, 216.0 g. ethyl acetate a 24.0 g. methyl alcohol. The resulting polymer waε diluted with the ethyl acetate/methyl alcohol mixture to 21.52% εolids. The adhesive polymer had a measured inherent viεcoεity of 1.40 dl/g in ethyl acetate at a concentration 0.15 g/dl. Itε Brookfield viεcoεity waε 2,300 centipoise. Example 1 A mixture of 200.62 g of 95:5 isoctyl acrylate:acrylamide adhesive copolymer, 33.75 g of isopropy myristate, 8.75 g of glyceryl monolaurate, 6.88 g of eεtradiol USP, 525.00 g of ethyl acetate and 58.33 g of methanol waε placed in a jar. The jar was placed on a platform shaker and shaken for about 18 hours. The formulation was allowed to εtand until all the air bubbleε had dissipated. The formulation was coated at a thicknesε 0.022 inches onto a εilicone coated 5 mil liner. The laminate was oven dried for 2 minutes at 125°F, for 2 minut at 185°F and for 2 minutes at 235°F (too vigorous condition for drying may result in loss of a major amount of the isopropyl myristate). The resulting adhesive coating contained 80.25 percent 95:5 iεooctyl acrylate:acrylamide adhesive copolymer, 13.50 percent isopropyl myristrate, 3.5 percent glyceryl monolaurate and 2.75 percent eεtradiol. T material was allowed to cool and was then laminated onto th corona treated surface of a 3 mil low density polyethylene backing. The laminate was die cut into 2 cm 2 patches. Penetration through hairless mouse skin was measured using the diffusion apparatus and method described above. The acceptor fluid was 30% N-methyl-2-pyrrolidone in water. Three independent determinations were carried out. The average penetration in 24 hours was 74 micrograms/cm . Exampleε 2-4 Using the general method of Example 1 the formulations shown in Table 1 were prepared and the penetration through hairlesε mouεe skin measured. The acceptor fluid waε 30% N-methyl-2-pyrrolidone in water. Patcheε which meaεured 2 cm were employed. Table 1 Penetration Formulation Micrograms/cm 2 in 24 hr 2.75% estradiol 5 3.50% glyceryl monolaurate 13.50% isopropyl myristate 80.25% isooctyl acrylate: acrylamide copolymer (94:6) 75 2.75% estradiol 3.50% glyceryl monolaurate n 10.60% isopropyl myristate 5.30% ethyl oleate 77.85% isooctyl acrylate: acrylamide copolymer (95:5) 87 2.75% estradiol 3.50% glyceryl monolaurate 10.60% isopropyl myristate 5 5.30% ethyl oleate 77.85% isooctyl acrylate: acrylamide copolymer (94:6) 87 Example 5 A mixture of 23.31 g of isooctyl acrylate:acrylamide:vinyl acetate adhesive copolymer, 21.66% solids in 90:10 ethyl acetate:methanol, 0.184 g of estradiol USP, 0.8035 g of isopropyl myristate, 0.2402 g of glyceryl monolaurate and 0.4130 g of ethyl oleate waε placed in a jar. The jar was placed on a platform shaker and shaken for about 20 hours. The formulation was allowed to stand until air bubbles had dissipated. The formulation was coated at a thickness of 0.022 inches onto a 5 mil Daubert 164Z release liner. The laminate was oven dried for 4 min. at 125°F, for 2 minutes at 185°F and for 1 minute at 225°F. The resulting adhesive coating contained 75.5 percent 75:5:20 isooctyl acrylate:acrylamide:vinyl acetate adhesive copolymer, 2.75 percent estradiol, 12.0 percent isopropyl myristate, 6.2 percent ethyl oleate and 3.6 percent glyceryl monolaurate. The material was then laminated onto the corona treated surface of a 3 mil low density polyethylene film and die cut into 5.07 cm 2 patches. Penetration through hairless mouse skin was measured. The acceptor fluid was 30% N-methyl-2-pyrrolidone in water. Three independent determinations were made. The average amount penetrating in 24 hours was 84 microgra s/cm 2 . Examples 6-8 Using the general method of Example 5 the formulations shown in Table 2 were prepared and the penetration through hairless mouse skin measured. The adhesive used was an isooctyl acrylate:acrylamide:vinyl acetate 75:5:20 copolymer. The acceptor fluid was 30% N-methyl-2-pyrrolidone in water. Patches measuring 5.07 cm 2 were employed. Table 2 Penetration Formulation Micrograms/cm 2 in 24 hr 2.75% estradiol 14.0% isopropyl myristate 7.4% ethyl oleate 3.5% glyceryl monolaurate 72.7% adhesive 112 2.74% estradiol 6.1% isopropyl myristate 12.4% ethyl oleate 3.5% glyceryl monolaurate 75.2% adhesive 98 2.76% estradiol 7.0% isopropyl myristate 14.1% ethyl oleate 3.5% glyceryl monolaurate 72.6% adhesive 130

Claims: WHAT IS CLAIMED IS: 1. An adhesive-coated sheet material comprising: a) a flexible backing; and b) a pressure-sensitive adhesive coating contiguously adhered to one surface of sai backing and comprising a homogeneous mixtur of: i) an acrylic copolymer comprising about to 98 percent by weight of a hydrophob monomeric acrylic or methacrylic acid ester of an alkyl alcohol based on the weight of all monomers in said copolym the alkyl alcohol containing 4 to 10 carbon atoms; ii) estradiol in an amount by weight of ab 0.2 to 12 percent of the total weight said adhesive coating; and iii) a skin penetration enhancer combinatio comprising isopropyl myristate and glyceryl monolaurate in amounts of abo 5 to 20 percent and about 1 to 6 perce by weight, respectively, based on the weight of said adhesive-coating, with relative amounts being selected so as enhance the penetration of said estrad through skin as compared to when said adhesive coating is free of said skin penetration enhancers; said sheet material being further characterized in th over a prolonged period it adheres suitably to skin a provides for substantially continuous transdermal delivery of estradiol to a subject in an amount which therapeutically effective for treating a condition associated with estradiol deficiency. 2. An adhesive-coated sheet material according to Claim 1, wherein said pressure-sensitive acrylic adhesive copolymer comprises A and B monomers as follows: A is a hydrophobic monomeric acrylic or methacrylic acid ester of an alkyl alcohol, the alkyl alcohol containing 4 to 10 carbon atoms, said A monomer being present in an amount by weight of about 91 98 percent of the total weight of all monomers in said copolymer; and B is a reinforcing monomer selected from the group consisting of acrylic acid, methacrylic acid, an alkyl acrylate or methacrylate containing 1 to 3 carbon atoms in the alkyl group, acrylamide, methacrylamide, a lower alkyl-substituted acrylamide, diacetone acrylamide, N-vinyl-2-pyrrolidone, a vinyl ether, a substitut ethylene and a vinyl ester, the B monomer being present in an amount by weight of about 2 to 9 percent of the total weight of all monomers in sa copolymer. 3. An adhesive-coated sheet material according to Claim 1, wherein said adhesive copolymer comprises said acrylic or methacrylic acid ester in an amount of about 94 98 percent by weight. 4. An adhesive-coated sheet material according to Claim 2, wherein said adhesive copolymer comprises isooctyl actylate as the A monomer and acrylamide as the B monomer. 5. An adhesive-coated sheet material according to Claim 1, wherein the amount of estradiol in said adhesive coating is about 1 to 5 percent by weight of said adhesive coating. 6. An adhesive-coated sheet material according to Claim 1, wherein the amount of estradiol in said adhesive coating is about 2 to 3.5 percent by weight of said adhesi coating. 7. An adhesive-coated sheet material according to Claim 1, wherein said isopropyl myristate and glyceryl monolaurate are present in amounts by weight of about 5 t 15 percent and 2 to 4 percent, respectively, based on the weight said adhesive coating. 8. An adhesive-coated sheet material according to Claim 1, wherein said skin penetration enhancer combinatio further comprises about 4 to 18 percent by weight of ethyl oleate based on the weight of said adhesive coating, and wherein the total amount by weight of isopropyl myristate ethyl oleate is less than about 25 percent based on the weight of said adhesive coating. 9. A method of treating a condition associated with estradiol deficiency wherein an adhesive-coated sheet material according to Claim 1 is applied and adhered to th skin of a mammal to permit systemic delivery of estradiol said mammal. 10. An adhesive-coated sheet material comprising: a) a flexible backing; and b) a pressure-sensitive adhesive coating contiguously adhered to one surface of said backing and comprising a homogeneous mixture of: i) an acrylic copolymer comprising (1) abo 60 to 80 percent by weight of a hydrophobic monomeric acrylic or methacrylic acid ester of an alkyl alcohol based on the weight of all monomers in said copolymer, the alkyl alcohol containing 4 to 10 carbon atoms (2) about 4 to 9 percent by weight base on the weight of all monomers in said copolymer of a reinforcing monomer selected from the group consisting of acrylic acid, methacrylic acid, an alky acrylate or methacrylate containing 1 t 3 carbon atoms in the alkyl group, acrylamide, methacrylamide, a lower alkyl-substituted acrylamide, diacetone acrylamide, and N-vinyl-2-pyrrolidone; and (3) about 15 to 35 percent by weigh of vinyl acetate based on the weight of all monomers in said copolymer; ii) estradiol in an amount by weight of abo 0.2 to 12 percent of the total weight o said adhesive coating; and iii) a skin penetration enhancer combination comprising isopropyl myristate and glyceryl monolaurate in amounts of abou 8 to 20 percent and about 1 to 6 percen by weight, respectively, based on the weight of said adhesive coating with th relative amounts being selected so as t enhance the penetration of said estradi through skin as compared to when said adhesive coating is free of said skin penetration enhancers f said sheet material being further characterized in that ove a prolonged period it adheres suitably to skin and provides substantially continuous transdermal delivery of estradiol a subject in an amount which is therapeutically effective f treating a condition associated with estradiol deficiency. 11. An adhesive-coated sheet material according to Claim 10, wherein said ester is isooctyl acrylate and said reinforcing monomer is acrylamide. 12. An adhesive-coated sheet material according to Claim 10, wherein the amount of estradiol in said adhesive coating is about 1 to 5 percent by weight of said adhesive coating. 13. An adhesive-coated sheet material according to Claim 10 , wherein the amount of estradiol in said adhesive coating is about 2 to 3.5 percent by weight of said adhesiv coating. 14. An adhesive-coated sheet material according to Claim 10, wherein said isopropyl myristate and glyceryl monolaurate are present in amounts by weight of about 5 to percent and 2 to 4 percent, respectively, based on the weig of said adhesive coating. 15. An adhesive-coated sheet material according to Claim 10, wherein said skin penetration enhancer combinatio further comprises about 4 to 18% by weight of ethyl oleate based on the weight of said adhesive coating, and wherein t total amount by weight of isopropyl myristate and ethyl oleate is less than about 25% by weight based on the weight of said adhesive coating. 16. A method of treating a condition associated with estradiol deficiency wherein an adhesive-coated sheet material according to Claim 10 is applied and adhered to th skin of a mammal to permit systemic delivery of estradiol t said mammal.

Inventors: MOORE CHERYL L, NELSON GREGORY R, WICK STEVEN M, ZERBE HORST-GEORG, MOORE, CHERYL, L., NELSON, GREGORY, R., WICK, STEVEN, M., ZERBE, HORST-GEORG
Applicants: RIKER LABORATORIES INC, RIKER LABORATORIES, INC.
Application year: 1989
Main classification: A61L15
IPC codes: A61K9, A61K31, A61K47