COATING COMPOSITIONS FOR PREVENTING ADHESION OF AQUATIC ORGANISMS

Abstract: Disclosed is a coating composition for preventing adhesion of aquatic organisms, the composition containing as a vehicle component a copolymer prepared by copolymerizing about 5 to about 85% by weight of (A) a monohydric and/or polyhydric phenol ester of acrylic or methacrylic acid; about 15 to about 75% by weight of (B) an ethylenically unsaturated monomer having a soluble parameter of about 8.0 to about 9.5 and a glass transition temperature of about 0°C or higher; and about 0 to about 50% by weight of (C) a water-soluble, ethylenically unsaturated monomer containing carboxyl group or amino group, based on the total monomer components.

Description: The present invention relates to coating compositions for preventing adhesion of aquatic organisms which compositions give coats capable of exhibiting the property of preventing adhesion of aquatic organisms for a prolonged period of time. Heretofore coating compositions for preventing adhesion of aquatic organisms have been generally applied to the submersible parts of a vessel or an offshore structure to preclude corrosion or decrease of the vessel's cruising speed which would be caused by underwater organisms clinging thereto such as barnacles, bryozoans, ascidians, algae or the like or to keep fish or shellfish from being lethally affected by aquatic organisms attached to nets or wire nettings for aquatic cultivation. These coating compositions for preventing adhesion of aquatic organisms include those comprising an anti-adhesion agent and vehicle components such as a toughener, rosin, plasticiser and the like and those comprising a homopolymer or a copolymer of an organotin-containing unsaturated monomer as disclosed in, for example, Japanese Examined Patent Publications Nos. 21,426/1965; 9,579/1969; 12,049/1976; etc. The former type of coating compositions can produce a coat which can achieve the effect of preventing adhesion of aquatic organisms (hereinafter referred to as "aquatic-adhesion preventing effect") by causing the rosin and anti-adhesion agent contained therein to dissolve out However, said coat is given an uneven surface due to the increase in the proportions of insoluble components in the coat during a long-term submersion in seawater, thereby providing a lower degree of aquatic-adhesion preventing effect. On the other hand, the latter type of coating compositions have the following problem The submersion in seawater of a coat formed from this type of coating composition induces the hydrolysis of an ester linkage. Due to the hydrolysis, the organotin compound introduced into the polymer through the ester linkage is separated from the coat and a carboxyl-containing polymer is produced and dissolved out in seawater, whereby the coat is imparted a freshly exposed surface all the time and is allowed to sustain the aquatic-adhesion preventing effect. Yet this type of coating composition is defective in adversely affecting fish and shellfish because the composition generally contains a large amount of harmful organotin compound to exhibit a high degree of the property of preventing adhesion of aquatic organisms (hereinafter referred to as "aquatic-adhesion preventing property"). WO 84/02915 is directed to an antifouling paint for protecting marine surfaces, comprising in combination: a) toxicant (e.g. a tin compound) and b) a film forming water insoluble, seawater erodible organotin free polymeric binder having recurring groups represented by the formula wherein X is H or CH₃; R is a substantially non-bioactive, alkyl, aryl or arylalkyl moiety, and where B is the residue of an ethylenically unsaturated monomer, and wherein said polymer has an hydrolysis rate of at least 5 X 10⁻⁴ milliequivalents per hour whereby the paint has an erosion rate of at least 2 microns per month in seawater. An object of the present invention is to provide a coating composition giving a coat which is capable of exhibiting an aquatic-adhesion preventing property for a long term and which has a low toxicity. Other objects and features of this invention will become more apparent from the following description. The invention provides a coating composition for preventing adhesion of aquatic organisms, the composition containing as a vehicle component a copolymer prepared by copolymerizing, based on the total monomer components, 5 to 85% by weight of (A) at least one monohydric and/or polyhydric phenol ester of acrylic or methacrylic acid selected from the group of compounds specified hereinafter; 15 to 75% by weight of (B) an ethylenically unsaturated monomer having a solubility parameter of 8.0 to 9.5 and a glass transition temperature of the corresponding homopolymer of 0°C or higher; and 0 to 50% by weight of (C) a water-soluble, carboxyl group or amino group containing ethylenically unsaturated monomer. The coating composition of the invention contains as a vehicle component the copolymer prepared by using a specific amount of the monohydric and/or polyhydric phenol ester of acrylic or methacrylic acid (monomer (A)) as one of the monomer components. When submersed, the coat formed from the coating composition of the invention causes the structural unit derived from the monomer (A) to gradually hydrolyze, whereby a monohydric and/or polyhydric phenol compound having a bactericidal action is released to achieve the aquatic-adhesion preventing effect (antifouling effect). The phenol compound to be released has a low toxicity itself, hence reliable in the safety of the human body. Described below are the monomer components used for preparation of the copolymer contained as the vehicle components in the coating composition of the invention. The monomer component (A) is selected from phenyl acrylate or methacrylate, o-chlorophenyl acrylate or methacrylate, m-chlorophenyl acrylate or methacrylate, p-chlorophenyl acrylate or methacrylate, 2,4,6-trichlorophenyl acrylate or methacrylate, o-methylphenyl acrylate or methacrylate, m-methylphenyl acrylate or methacrylate, p-methylphenyl acrylate or methacrylate and p-tert-butyl phenyl acrylate or methacrylate. The monomers (A) are usable singly or at least two of them can be used in mixture. The amount of the monomer (A) used is 5 to 85% by weight, preferably 30 to 70% by weight, based on the total monomer components. Less than 5% by weight of the monomer (A) used reduces the amount of monohydric and/or polyhydric phenol compound produced by the hydrolysis and also decreases the number of carboxyl group produced by the hydrolysis, making it impossible to achieve a long-term aquatic-adhesion preventing effect. More than 85% by weight of the monomer (A) used accelerates the dissolution of the coat in water, rendering the coat unable to afford a sustained aquatic-adhesion preventing effect. The ethylenically unsaturated monomer (monomer (B)) is used to provide better release, into water or seawater, of phenol component produced by the hydrolysis of the structural unit derived from the phenol ester of acrylic or methacrylic acid (A). Useful monomers (B) are those having a solubility parameter (SP value) of 8.0 to 9.5, preferably 8.2 to 9.4 and a glass transition temperature (Tg) of the corresponding homopolymer of 0°C or higher, preferably 10 to 150°C. The term "solubity parameter" used herein is the terminology which is found in J. Paint Tech., 42 [541], p. 76, Feb., 1970 and also in Polymer Hand Book, 2nd edition. The monomer (B) is used in an amount of 15 to 75% by weight, preferably 30 to 70% by weight, based on the total monomer components of the copolymer. Use of the copolymer serves to produce a coat well balanced in the hydrophilic property and the hardness. On submersion in water or seawater, the coat well balanced in these properties will be swollen with the water permeated deep into the coat. The hydrolysis of the structural unit derived from the monomer (A), which is initiated in this state, proceeds uniformly in the interior as well as at the surface of the coat so that the phenol component can be dissolved out at an even rate until the coat is depleted into extinction. Use of the monomer (B) with less than 8.0 in solubility parameter lowers the hydrophilic property of the coat, whereas use of the monomer (B) with more than 9.5 in said parameter enhances the hydrophilic property to an excessive extent, accelerating the dissolution of the coat and rendering the coat unable to sustain the aquatic-adhesion preventing effect for a long time. Use of the monomer (B) of Tg of the corresponding homopolymer lower than 0°C renders it difficult for water or seawater to permate into the coat which as a result fails to fully exhibit the aquatic-adhesion preventing property. Less than 15% by weight of the monomer (B) used reduces the mechanical strength and durability of the coat, hence undesirable. More than 75% by weight of the monomer (B) used is also undesirable because of failure to fully produce the aquatic-adhesion preventing effect. Preferred examples of the ethylenically unsaturated monomer (B) which can be used in the invention are methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, iso-butyl methacrylate, t-butyl methacrylate and like C₁-C₄ alkyl esters of methacrylic acids; methyl acrylate, t-butyl acrylate and like esters of acrylic acids; vinyl toluene, α-methylstyrene, styrene and like aromatic vinyl monomers; etc. Use of a relatively small amount of the monomer (A) reduces the number of carboxyl groups produced by the hydrolysis of structural unit derived from the monomer (A), leading to the tendency of the coat to become gradually insoluble in water and to fail to display a high aquatic-adhesion preventing effect for a long term. In view of this tendency, the carboxyl group or amino group containing ethylenically unsaturated monomer (monomer (C)) is a water-soluble monomer which is used, when required, to provide the coat with a proper degree of water solubility or a swelling property. The monomer (C) can be any of the monomers which serve to impart water solubility to the copolymer. Suitable examples of the monomer (C) are carboxyl-containing ethylenically unsaturated monomers which are easily neutralized with the basic substance in seawater and rendered water-soluble, and tertiary amino-containing ethylenically unsaturated monomers which per se are excellent in water solubility. Examples of the carboxyl-containing ethylenically unsaturated monomers are acrylic or methacrylic acid, maleic acid, maleic anhydride, itaconic acid, fumaric acid; α-chloroacrylic acid, citraconic acid, etc. Examples of the tertiary amino-containing ethylenically unsaturated monomers are N,N-dimethylaminoethyl acrylate or methacrylate, N,N-diethylaminoethyl acrylate or methacrylate, 1-vinyl-2-pyrrolidone, 1-vinyl-3-pyrrolidone, 2-vinyl pyridine, N,N-dimethyl acrylamide or methacrylamide, N,N-dimethylaminopropyl acrylamide or methacrylamide. The amount of the carboxyl- or amino-containing ethylenically unsaturated monomer (C) used is 0 to 50% by weight, preferably 5 to 20% by weight, based on the total monomer components More than 50% by weight of the monomer (C) used affords an excessive degree of water solubility to the coat, rendering the coat unable to sustain an aquatic-adhesion preventing effect. If necessary, other radically copolymerizable ethylenically unsaturated monomers (monomer (D)) different from the unsaturated monomers (A), (B) and (C) can be used according to the required properties of the coat. Examples of the monomer (D) are ethyl acrylate, n-butyl acrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, lauryl methacrylate, stearyl methacrylate, acrylonitrile, methacrylonitrile, 2-hydroxyethyl acrylate and 2-hydroxypropyl acrylate. The amount of the monomer (D) used is 50% by weight or less, preferably 15% by weight or less, based on the total monomer components. Given below are examples of combinations of monomer components used for preparation of the copolymer according to the invention: (1) 25 to 85% by weight of the monomer (A) and 15 to 75% by weight of the monomer (B); (2) 5 to 85% by weight of the monomer (A), 15 to 75% by weight of the monomer (B) and 10 to 50% by weight of the monomer (C); (3) 5 to 85% by weight of the monomer (A), 15 to 75% by weight of the monomer (B) and 10 to 50% by weight of the monomer (D); and (4) 5 to 85% by weight of the monomer (A), 15 to 75% by weight of the monomer (B), 5 to 50% by weight of the monomer (C) and 5 to 50% by weight of the monomer (D). The copolymer for use as the vehicle component in the coating composition of the invention can be prepared by known processes, for example, by reacting the monomer components in an inert organic solvent in the presence of a radical polymerization catalyst at a temperature of 0 to 180°C, preferably 40 to 170°C for 1 to 20 hours, preferably 6 to 10 hours. The kind of organic solvent used is not critical insofar as the solvent is capable of dissolving the produced copolymer without gelation during the copolymerization reaction. Examples of useful organic solvents are ethanol, propanol, butanol, benzyl alcohol and like alcohols; cellosolve, ethyl cellosolve, carbitol, butyl carbitol, ethylene glycol dimethyl ether, ethylene glycol monoacetate and like ethers; toluene, xylene and like aromatic hydrocarbons; ethyl acetate, butyl acetate and like esters; cyclohexanone, methyl isobutyl ketone and like ketones; etc. Usable as the radical polymerization catalyst are radical polymerization initiators commonly used for radical polymerization, e.g. azo-type compounds, peroxide-type compounds, diazo compounds, nitroso compounds, redox-type compounds and like catalysts. Optionally the radical polymerization may be initiated with ionizing radiation or other means. The copolymer for use in the invention is one having a number-average molecular weight of 3,000 to 200,000, preferably 5,000 to 50,000. Use of the copolymer less than 3,000 in number-average molecular weight enhances the hydrophilic property to an excessive extent and decreases a long-term aquatic-adhesion preventing property, whereas use thereof with more than 200,000 in the number-average molecular weight retards the dissolution of the coat owing to the difficulty of hydrolysis in seawater or the like, leading to inability of the coat to exhibit an aquatic-adhesion preventing property. Copolymers useful in the invention include those prepared by other processes than the foregoing one, for example, a copolymer prepared by reacting a phenol or a compound with a copolymer prepared using CH₂=CHCOOH or CH₂=CHCOCl as a monomer. However, it is preferred to use the copolymer prepared by the process hereinbefore described which is easy to carry out with little or no side reaction involved. The coating compositions for preventing adhesion of aquatic organisms according to the invention contain as a vehicle component the copolymer having the foregoing structure. The coat formed from the coating composition of the invention is gradually dissolved out in water or seawater, releasing the bactericidal phenol compound produced by hydrolysis in water or seawater. Therefore the coat is capable of affording an excellent aquatic-adhesion preventing effect. The coating composition contains the copolymer in an amount of 10 to 70% by weight, preferably 20 to 50% by weight. Useful as the solvent far preparation of the coating composition according to the invention are the examples of solvents shown above for the preparation of the copolymer. The coating composition of the invention may contain a known antifouling agent according to the required properties, such as cuprous oxide, copper thiocyanate, copper powder or like copper-type antifouling agents, triphenyltin fluoride, triphenyltin chloride, tributyltin oxide or like organotin antifouling agents, zinc ethylene-bis (dithiocarbamate), tetramethylthiuram disulfide or like nitrogen-containing sulfur-type antifouling agents, zinc oxide or the like. The amount of conventional antifouling agent for use is determined according to the required properties of the coat so that the agent does not adversely affect the properties of the coating compositions of the invention. The coating composition may further contain an extender pigment, coloring pigment, plasticizer, additives for coating, other resins and the like, when so required. The extender pigment and coloring pigment can be used in the total amount of 500 parts by weight or less per 100 parts by weight as the total amount of the above-mentioned copolymer, plasticizer, additives for coating and other resins. The total amount of the plasticizer, additives for coating and other resins is 100 parts by weight or less per 100 parts by weight of the copolymer. For formation of a coat, the coating composition of the present invention is applied directly to the surface of a substrate or to the surface of a coated substrate. Exemplary of the substrates for use are offshore structures and the like including vessels, harbor facilities, buoys, pipelines, bridges, undersea bases, nets for aquatic cultivation, stationary nets for fishing, etc. Representative coated substrates are substrates covered with: a single-layer coat formed by application of one of a wash primer, zinc epoxy type shop primer and like primers, oily anticorrosion type, rubber chloride type, epoxy type and like undercoat primers and long-oil phthalic resin type, rubber chloride type, epoxy type and like intercoat or topcoat compositions; or a multi-layer coat formed by applications of a primer and an undercoat primer; or a multi-layer coat formed by sequential applications of a primer, undercoat primer, and intercoat or topcoat composition. The application can be conducted by brushing, spraying, roller coating, immersion or like means. The coating composition is applied in an amount sufficient to form a layer having a thickness of 40 to 500 µm, preferably 80 to 300 µm, when dried. Subsequently the layer thus applied is dried to provide a coat having an aquatic-adhesion preventing property. Heating is not required for drying since the layer is dried when left to stand at room temperature, i.e. at -10 to 40°C, for 4 to 24 hours. The coat thus formed retains an outstanding aquatic-adhesion preventing property over a prolonged period of time, and is pronouncedly high in safety toward the human body. The present invention will be described below in greater detail with reference to the following Preparation Examples, Comparison Examples and Examples. Preparation Example 1 Preparation of copolymer I Phenyl acrylate (50 g), 50 g of methyl methacrylate, 43 g of xylene and 2.0 g of benzoyl peroxide were mixed together. The mixture was reacted with stirring at 90 to 100°C for 3 hours. To the reaction mixture were added 1.0 g of benzoyl peroxide and 107 g of xylene. The mixture was reacted with stirring at 90 to 100°C for 2 hours, giving a pale yellow viscous liquid having a solids content of 40% by weight. The thus obtained copolymer (copolymer I) had a number-average molecular weight of 23,000. Preparation Example 2 Preparation of copolymer II Styrene (30 g), 30 g of ethyl methacrylate, 40 g of o-chlorophenyl methacrylate, 43 g of xylene and 0.5 g of azobisisobutyronitrile were mixed together. The mixture was reacted with stirring at 90 to 100°C for 3 hours. To the reaction mixture were added 1.0 g of azobisisobutyronitrile and 107 g of xylene. The mixture was reacted with stirring at 90 to 100°C for 2 hours, giving a pale yellow viscous liquid having a solids content of 40% by weight. The thus obtained copolymer (copolymer II) had a number-average molecular weight of 45,000. Preparation Example 3 Preparation of copolymer III A 60 g quantity of p-t-butylphenyl acrylate, 30 g of methyl methacrylate, 10 g of n-butyl methacrylate, 43 g of xylene and 1.0 g of benzoyl peroxide were mixed together. The mixture was reacted with stirring at 90 to 100°C for 3 hours. To the reaction mixture were added 1.0 g of benzoyl peroxide and 107 g of xylene. The mixture was reacted with stirring at 90 to 100°C for 2 hours, giving a pale yellow viscous liquid having a solids content of 40% by weight. The thus obtained copolymer (copolymer III) had a number-average molecular weight of 36,000. Preparation Example 4 Preparation of copolymer IV A 50 g quantity of o,p-trichlorophenyl acrylate, 30 g of methyl methacrylate, 20 g of 2-ethylhexyl methacrylate, 43 g of xylene and 2.5 g of azobisisobutyronitrile were mixed together. The mixture was reacted with stirring at 90 to 100°C for 3 hours. To the reaction mixture were added 1.0 g of azobisisobutyronitrile and 107 g of xylene. The mixture was reacted with stirring at 90 to 100°C for 2 hours, giving a pale yellow viscous liquid having a solids content of 40% by weight. The thus obtained copolymer (copolymer IV) had a number-average molecular weight of 18,000. Preparation Example 5 Preparation of copolymer V A copolymer was produced in the same manner as in Preparation Example 1 with the exception of using n-butanol in place of xylene as a solvent and using the following monomer mixture: p-t-Butylphenyl methacrylate 30 g Methyl methacrylate 50 g Acrylic acid 10 g Ethyl acrylate 10 g Azobisisobutyronitrile 2.5 g A pale yellow viscous liquid was obtained which contained a copolymer (copolymer V) and which had a solids content of 40% by weight. The copolymer had a number-average molecular weight of 20,000. Preparation Example 6 Preparation of copolymer VI A copolymer was produced in the same manner as in Preparation Example 5 with the exception of using the following monomer mixture. Phenyl methacrylate 30 g iso-Butyl methacrylate 35 g Methyl methacrylate 20 g Methacrylic acid 15 g Azobisisobutyronitrile 0.5 g A pale yellow viscous liquid was obtained which contained a copolymer (copolymer VI) and which had a solids content of 40% by weight. The copolymer had a number-average molecular weight of 40,000. Example 1 A coating composition for preventing adhesion of aquatic organisms was prepared by mixing and dispersing 70.0 g of the solution of the copolymer I prepared above in Preparation Example 1 (solids content of 40% by weight), 5.0 g of talc, 3.0 g of red iron oxide, 0.5 g of Aerosil® #200 (product of Degussa, West Germany), 10 g of cuprous oxide and 11.5 g of xylene with a paint conditioner. Examples 2 to 9 A coating compositions for preventing adhesion or aquatic organisms were prepared by carrying out the same procedure as done in Example 1 using each mixture shown below in Table 1 in the amount listed therein. The values in the table are in terms of gram. Comparison Examples 1 to 3 Coating compositions for preventing adhesion of aquatic organisms were each prepared from the following mixture in the same manner as in Example 1. Comparison Example 1 Vinyl chloride resin 10.0 (g) Rosin 10.0 Tricresyl phosphate 4.0 Triphenyltin fluoride 10.0 Talc 5.0 Red iron oxide 5.0 Xylol 28.0 Methyl isobutyl ketone 28.0 Total 100.0 (g) Comparison Example 2 Rubber chloride resin 5.0 (g) Rosin 15.0 Tricresyl phosphate 4.0 Cuprous oxide 30.0 Talc 5.0 Barium sulfate 3.0 Red iron oxide 4.0 Xylol 34.0 Total 100.0 (g) Comparison Example 3 Vinyl chloride resin 5.5 (g) Rosin 5.5 Tricresyl phosphate 2.0 Cuprous oxide 30.0 Triphenyltin hydrooxide 10.0 Barium sulfate 4.0 Talc 11.0 Red iron oxide 10.0 Xylol 11.0 Methyl isobutyl ketone 11.0 Total 100.0 (g) The coating compositions for preventing adhesion of aquatic organisms which compositions were obtained in Examples 1 to 9 and in Comparison Examples 1 to 3 were tested for the aquatic-adhesion preventing property with the results as shown below in Table 2. Test for aquatic-adhesion preventing property The coating compositions obtained in Examples 1 to 9 and in Comparison Examples 1 to 3 were each applied to a sandblasted steel plate covered with a first layer of a zinc epoxy type shop primer (with a thickness of 15 µm when dried) and a second layer of epoxy type anticorrosion coating composition (with a thickness of 200 µm when dried) to form a coat of 100 µm thickness when dried. The coated plate was dried for 7 days to provide a test plate. The test plates were immersed in Toba Bay, Mie Prefecture, Japan to determine the aquatic-adhesion preventing property (the area of the test plate on which the aquatic organisms were attached was expressed in percentage). Table 2 below shows the results. Example Term of Immersion (month) 6 12 18 1 0 0 0 2 0 0 5 3 0 0 5 4 0 0 10 5 0 0 0 6 0 0 10 7 0 0 5 8 0 0 0 9 0 0 0 Comp. Example 1 0 10 30 2 0 0 15 3 0 0 0 The test results show that the tested coating compositions of the invention exhibited a high aquatic-adhesion preventing property. On the other hand, the coating compositions prepared in Comparison Examples 1 and 2 are poor in the long-term aquatic-adhesion preventing property and the coating composition prepared in Comparison Example 3 had the drawback of being significantly harmful because of the presence of the organotin compound although good in the aquatic-adhesion preventing property.

Claims: A coating composition for preventing adhesion of aquatic organisms, the composition containing as a vehicle component a copolymer prepared by copolymerizing, based on the total monomer components, 5 to 85% by weight of (A) at least one monohydric and/or polyhydric phenol ester of acrylic or methacrylic acid selected from phenyl acrylate or methacrylate, o-chlorophenyl acrylate or methacrylate, m-chlorophenyl acrylate or methacrylate, p-chlorophenyl acrylate or methacrylate, 2,4,6-trichlorophenyl acrylate or methacrylate, o-methylphenyl acrylate or methacrylate, m-methylphenyl acryate or methacrylate, p-methylphenyl acrylate or methacrylate and p-tert-butyl phenyl acrylate or methacrylate; 15 to 75% by weight of (B) an ethylenically unsaturated monomer having a solubility parameter of 8.0 to 9.5 and a glass transition temperature of the corresponding homopolymer of 0°C or higher; and 0 to 50% by weight of (C) a water-soluble carboxyl group or amino group containing ethylenically unsaturated monomer. Composition according to claim 1 wherein the ethylenically unsaturated monomer (B) is at least one of methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, iso-butyl methacrylate, t-butyl methacrylate, methyl acrylate, t-butyl acrylate, vinyl toluene, α-methylstyrene and styrene. Composition according to any one of claims 1 and 2 wherein the water-soluble,carboxyl group or amino group containing ethylenically unsaturated monomer (C) is at least one of acrylic or methacrylic acid, maleic acid, maleic anhydride, itaconic acid, fumaric acid, α-chloroacrylic acid, citraconic acid, N,N-dimethylaminoethyl acrylate or methacrylate, N,N-diethylaminoethyl acrylate or methacrylate, 1-vinyl-2-pyrrolidone, 1-vinyl-3-pyrrolidone, 2-vinyl pyridine, N,N-dimethyl acrylamide or methacrylamide and N,N-dimethylaminopropyl acrylamide or methacrylamide. Composition according to any one of claims 1 to 3 wherein the copolymer has been prepared by copolymerizing a monomer mixture consisting of 25 to 85% by weight of the phenol ester of acrylic or methacrylic acid (A) and 15 to 75% by weight of the ethylenically unsaturated monomer (B). Composition according to any one of claims 1 to 3 wherein the copolymer has been prepared by copolymerizing a monomer mixture consisting of 5 to 85% by weight of the phenol ester of acrylic or methacrylic acid (A), 15 to 75% by weight of the ethylenically unsaturated monomer (B) and 10 to 50% by weight of said ethylenically unsaturated monomer (C). Composition according to any one of claims 1 to 3 wherein the copolymer has been prepared by copolymerizing a monomer mixture consisting of 5 to 85% by weight of the phenol ester of acrylic or methacrylic acid (A), 15 to 75% by weight of the ethylenically unsaturated monomer (B) and 10 to 50% by weight of radically polymerizable ethylenically unsaturated monomer different from the monomers (A), (B) and (C). Composition according to any one of claims 1 to 3 wherein the copolymer has been prepared by copolymerizing a monomer mixture consisting of 5 to 85% by weight of the phenol ester of acrylic or methacrylic acid (A), 15 to 75% by weight of the ethylenically unsaturated monomer (B), 5 to 50% by weight of said unsaturated monomer (C) and 5 to 50% by weight of radically polymerizable ethylenically unsaturated monomer different from the monomers (A), (B) and (C). Composition according to any one of claims 1 to 7 wherein the copolymer has a number-average molecular weight of 3,000 to 200,000. Composition according to any one of claims 1 to 8 which contains as a vehicle component 10 to 70% by weight of the copolymer. A method of forming a coat for preventing adhesion of aquatic organisms, characterized by applying the coating composition of any one of claims 1 to 9 to a substrate.

Inventors: ISOZAKI, OSAMU, TERASHIMA, HIROKAZU
Applicants: KANSAI PAINT CO. LTD.
Application year: 1989
Main classification: C09D5
IPC codes: C09D133, C09D5