Reactive hot melt structural adhesive

Abstract: Novel reactive hot melt structural adhesives comprising urethane oligomer and epoxy mixture in specified ratios. The compositions offer very high shear, peel, and impact strengths, properties of particular value in bonding adherends in an auto body assembly line.

Description: FIELD OF THE INVENTION The invention relates to reactive hot melt compositions (RHM's) useful as adhesives, sealants, coatings, or the like. DESCRIPTION OF THE PRIOR ART RHM's are thermosetting adhesives. These materials are known in the prior art, and are known to have various disadvantages. Canadian Patent 1,229,192 of November 10, 1987, to S.C. Lin, describes an RHM comprising an epoxy urethane containing compound, which thermosets on heating. U.S. 3,723,568 teaches the use of polyepoxides and optional epoxy polymerization catalysts. U.S. 4,122,073 teaches thermosetting resin obtained from polyisocyanates, polyanhydrides and polyepoxides. Crosslinking in these patents is achieved by reaction with available sites in the base polymers. U.S. 4,137,364 teaches crosslinking of an ethylene/vinyl acetate/vinyl alcohol terpolymer using isophthaloyl, bis-caprolactam or vinyl triethoxy silane whereby crosslinking is achieved before heat activation with additional crosslinking induced by heat after application of the adhesive. U.S. 4,116,937 teaches a further method of thermal crosslinking by the use of polyamino bis-maleimide class of flexible polyimides, which compounds can be hot melt extruded up to 150°C and undergo crosslinking at elevated temperatures thereabove. In these latter two patents, thermal crosslinking is also achieved by reactions of the particular crosslinking agent with available sites of the base polymers. U.S. 3,505,283 teaches the use of simple, organic di- and polyisocyanates as chemical thickeners when reacted with hydroxyl-containing epoxy resins at temperatures between 50 and about 200°C in the presence of carboxylic acid anhydride as a curing agent. Material prepared from this process is not suitable as a reactive, hot melt adhesive since the high application temperatures required to afford processability may trigger the crosslinking reaction of the thermosetting material prematurely. Similarly, U.S. 3,424,719 teaches the use of simple diisocyanates to react with the glycidyl polyether of dihydric phenols in solvents, thereby increasing the crosslinking density which results in improved heat distortion temperatures. The solvent is necessary for processability of the solid forms of glycidyl polyether dihydric phenol and avoid the high temperature conditions required for polymerization which creates not only process problems but also may induce instability of the reactant mixture after blending with a latent curing agent. OBJECTS OF THE INVENTION Strong structural adhesives and sealants are needed for bonding substrates loaded with significant mechanical stress at the interface. Such adhesive materials must have the following requirements: High production rates with short, unvarying times for each operation in assembly line use. Minimal prior cleaning of surfaces to be bonded. Minimal health and safety hazards. Optimum balance between open time and development of handling strength. Maximum bond strength. Maximum thermal and environmental resistance. Based on these requirements, typically thermosetting materials such as epoxy resins, phenolics, polyesters, and polyurethanes are used as structural adhesives. After the crosslinking reaction the adhesive becomes part of the structural component and provides the required bond strength and thermal resistance. Normally, the structural adhesive is composed of liquid resins and curing agents in either two-package or single package form depending on the reactivity between the resin and the curing agent under storage conditions. The liquid structural adhesive has the advantage of easy application to the substrate over the solid adhesive. However, the liquid adhesive, in two-package form after mixing, has a certain length of pot-life which is the time required to stay as liquid for application purposes. Consequently, the handling strength (minimum strength necessary to maintain adhering substrates together) cannot be rapidly developed. Further, from a safety and health hazard viewpoint, the liquid adhesive usually causes more contamination of the work place than the solid form. Thus, the two-package structural adhesive requires a very precise measurement and extremely good mixing to obtain any consistency of property control. The one package liquid adhesive was designed to solve mixing and metering difficulties. To achieve one package reactive adhesive preparation, techniques such as chemical blocking and phase separation are being used in the adhesive industry. The crosslinking reaction has to be triggered by heating or other techniques which are difficult to control resulting in long time periods to develop handling strength. Two forms of solid adhesives, powder and hot melt can be used instead of liquid adhesives. Because of the phase separation between resin powder and curing agent powder, the one package adhesive can be obtained very easily. However, the application, handling cost and safety considerations make the powder adhesive less attractive to the adhesive industry. The other solid form of adhesive is hot melt which is a thermoplastic in general. The hot melt adhesive provides a bond between substrates upon cooling the molten adhesive to room temperature. The bonding process is fast and simple. The disadvantage of a thermoplastic hot melt adhesive is the fast decrease in its bonding strength upon reheating because of the nature of thermoplastics. Thus, it cannot be considered as a structural adhesive unless it is further modified. Conventional solid adhesive such as high molecular weight epoxy resin can be applied as a reactive hot melt adhesive. Without modification, this type of solid adhesive provides poor adhesion properties such as impact resistance and lap shear strength. Modification of this material such as reacting it with a carboxyl-terminated poly(butadiene-co-acrylonitrile) increases the impact resistance and the lap shear strength. However, this modification is carried out at elevated temperature, 100 - 150°C, in the presence of a catalyst, thus making the addition of a latent curing agent such as dicyandiamide and curing accelerator difficult since the curing reaction is activated by the catalyst at room temperature. Hence, due to the combination of a high cost factor and preparation difficulties, this type of adhesive is not attractive commercially. This invention is concerned with the development of a class of reactive hot melt adhesives which will provide rapid development of handling strength and, also, maximum bond strength and thermal resistance as thermosetting adhesives. This invention also relates to a process to utilize the reaction between diisocyanates and hydroxyl groups of the diol and epoxy resin to prepare the reactive hot melt adhesives having latent curability, long storage life, internally modified adhesion properties and well controlled application rheology. The materials for the preparation of this particular reactive hot melt adhesive include a polyisocyanate, a hydroxyl-containing epoxy resin for introducing reactive pendent groups and a diol, preferably a difunctional primary alcohol, for improving the physical properties and for reducing the viscosity of the bulk polymerization medium. Optionally, a reactive plasticizer for reducing the viscosity of bulk polymerization and adjusting the application temperature can be added to the system. One object of the instant invention is to produce a composition, usable as an adhesive, sealant or coating, which is solventless. Another object of the invention is to produce a composition which can be applied as a hot melt. Still another object of the instant invention is to produce a composition which is heat curable in a minimum time period. A further object of the invention is to produce a novel compound which in combination with a heat reactive epoxy curing agent will result in a thermoset coating, adhesive or sealant on heating. Yet another object of the invention is to produce a thermoplastic composition which can be applied as a hot melt and thereafter cured by a thermally triggered initiator to a thermoset adhesive, sealant or coating at a more elevated temperature. A further object of the instant invention is to produce one or more methods for making a thermoplastic composition which can be applied as a hot melt. Other objects will become apparent from a reading hereinafter. DESCRIPTION OF THE INVENTION My RHM composition is an improvement in the single-package epoxy RHM adhesive where the composition contains the hardener or catalyst, which is dormant until heat-triggered, whereupon the composition then crosslinks and thermosets. The improvement is several fold, as compared with various commercial single-package RHM adhesives presently used in the auto industry, viz.: Composition I (This invention) Composition X Shear strength , MPa (psi) 20.7 (3000) 12.4 (1800) Peel strength , N/cm (pli) 78.8 - 87.6 (45 - 50) 0 (0) Impact strength , cm kg (" lbs) 69.2 (60) 11.5 (10) Green tack to oily metal 30 sec. 30 sec. DEFINITIONS Epoxy resins Those used in the invention are so-called DGEBA-type, i.e., reaction products of diglycidyl epoxide with Bis-phenol A. All are commercially available from Shell Chemical Co. Epon-872® has the formula where X is Y is -R-K-Q where R is -CH₂CH(OH)CH₂- K is Q is Epon-1001® F is with 2.2 -OH groups/molecule Epon-828® is Q-K-Q, with 0.2 -OH groups/molecule, average MW, 350 - 400. Other materials NYAD-400®; calcium silicate powder, from Nyco Co. N-70-TS®; fumed silica powder, from Cabot Co. CK-2500®; a non-heat reactive high melting phenolic resin from Union Carbide Corp. Softening point 112.8-143.3°C (235-290°F). A-187®; gamma-Glycidoxypropyltrimethoxy silane, from Union Carbide Corp. Olin 55-28® is a 4000 g/mole ethylene oxide end-capped polypropylene glycol triblock polymer, with primary hydroxyl groups: ---EO---PO---EO---. Olin 20-28® is a 4000 g/mole polypropylene glycol homopolymer with secondary hydroxyl groups. MP-102® (BASF) is a prepolymer made by adding tripropylene glycol to MDI to make a 50:50 MDI:MDI adduct which is liquid at room temperature. Premix A Components Parts by Weight Broad Range Narrow Range Specific Olin 55-28® 5-100 20-25 22.80 Olin 20-28® 0-50 20-25 22.80 Phenyldiethanolamine 0- 2 0- 1 0.47 MP-102® 5-20 5- 9 6.97 Epon-1001F® 0-50 15-20 18.82 Epon-872® 10-50 26-30 28.14 Premix A is a urethane oligomer and is used in TABLE I in the above specific amounts in preparing Composition I. It can be used in modifications of Composition I within the above ranges. In preparing Composition I (TABLE I), the order of mixing is not critical. However, I prefer to add the dicyandiamide last, with mixing for a short time, to prolong shelf life. Composition I Parts by Weight Broad Range Narrow Range Specific Premix A 50-800 100-300 250 Epoxy mixture 10-500 50-400 200 Epon-828® 10-200 25-125 50 CaSiO₃ 0-200 50-150 100 CaO 10-100 25- 75 50 Fumed SiO₂ 5- 80 20- 60 40 CK-2500 Phenolic resin 0-100 15- 75 20 Zn₃(PO₄)₂ 5-100 5- 50 10 Dicy/Epoxy mix 50-150 60-120 80 gamma-Glycidoxypropyltrimethoxy silane 1- 10 3- 7 5 When reference is made to Composition I, it is the Composition with the Specific amounts in TABLE I unless otherwise noted. Such Composition is preferred for use herein. Example 1 This example is partially hypothetical in that is is based on properties of my Composition I that I have established in the laboratory. Composition I use is demonstrated on a section of an auto assembly line, viz., an adhesive/sealant for door hem flange binding. (1) Composition I at room temperature is a viscous liquid (a semi-solid). For application it must be heated, e.g., to 80°C, to liquefy it. At 80°C it has zero strength and is easily handled. This temperature is too low to trigger the curing mechanism. Composition I at about 80°C is applied around the interior rim of the outer plate (cold rolled steel - "CRS", optionally galvanized) of a car door. This application is preferably by spraying, but it can be by melt extrusion or other system. (2) The inner plate (CRS) is now pressed ("fixtured") against the outer plate. One or both parts may be oily. In such case Composition I quickly penetrates the oil and forms an adhesive bond to the part. At this stage (room temperature) the Composition provides a strength of about 0.07 MPa (10 psi), enough to hold the two plates together under non-stress conditions. (3) The flanges of the outer plate are now folded over the perimeter of the inner plate. In this operation, Composition I is squeezed into the flange crevices, providing a good seal all around the perimeter. The strength of the green adhesive at this stage is still about 0.07 MPa (10 psi). (4) The door is assembled onto the metal body of the car. Here, if need be, the door can be bent and twisted to fit the automobile. If the adhesive bond is broken, possible sites for corrosion are not made because the adhesive softens in Step 6. At this stage the door is dimensionally stable because of the viscosity of the Composition (about 0.07 MPa (10 psi)). (5) The assembled car body is dipped into E-coat primer bath (a room-size vat). At this point many commercial adhesives tend to dissolve or be partially washed off into the primer baths and to redeposit on the car body surfaces. Composition I does not dissolve in these baths and hence avoids this problem. In this operation, Composition I has a strength of about 0.07 MPa (10 psi). (6) The assembled body is removed from the E-bath and taken to the baking oven, where it is heated to about 177°C (350°F). Composition I at first melts and passes again through zero strength, then quickly begins to cure and soon attains its maximum strength, taking about thirty minutes for this. In its molten condition it spreads further into all cracks and crevices and ensures thorough coating and sealing between the two door plates, thereby minimizing future vapor/liquid penetration between the plates and consequent corrosion. A modification of Step 6 is discussed later on when I describe my Composition II. The process outlined above has a general applicability. The substrates (adherends) are suitably metal parts. Parts such as refrigerator doors, stove and oven doors, parts for washers and driers, double-walled panels for vans and trucks, and hardware for marine, air, and rail vehicles and accessories can be assembled by my process, using the compositions of this invention. The invention compositions can also be used as gaskets and sealants. Referring now back to Stage (4) above, at this point parts adhered with conventional adhesives are customarily visually inspected. Frequently the parts will be very slightly out of true with respect to each other and/or to the car body framework. Manual adjustments (pounding, pulling, pressure) are made at this stage to bring the elements back into true. In current practice, using commercially available structural adhesives, this type of forcible adjustment tends to produce minute cracks in the adhesive, which is a semi-solid at this stage in the process (i.e., after application but before curing). Such cracks presage corrosion and eventual bond-failure. It would be a great advantage if the adhesive could momentarily cease to be a viscous solid and become a liquid with zero strength. My Composition I will in fact do exactly that. Thus, at 100 - 160°C Composition I melts but does not cure. Above 160°C it cures. Thus, when heating to 180°C, the Composition must pass through 100 - 160°C, so it softens. This behavior provides a "window" within the process program which permits adjustments, and within which complete assemblies can be structured and/or restructured (i.e., the adherends can be moved with respect to each other). At temperatures below this window my Composition I is a semi-solid or viscous liquid, with very low adhesive strength (ca. 0.07 MPa (10 psi)). At the window, the strength is zero. At temperatures substantially above he window temperature, Composition I will cure, solidify, and develop maximum strength. Composition II For assembly lines where Stage (6) above requires something between zero strength and a small but useful strength (e.g., 0.07 MPa (10 psi)), I modify Composition I to Composition II. Composition II is like Composition I in that it is sufficiently liquid to withstand minor adherend adjustments without rupture or development of cracks. On the other hand, it is sufficiently viscous to provide a strength of about 7 kPa (1 psi) at the curing temperature (177°C), which is helpful in maintaining dimensional stability of the bonded adherends, especially where the Composition is affixed around the entire perimeter of the door or like part. Like Composition I, Composition II can be used to provide two metal substrates having between them the respective composition in uncured molten condition at a temperature of about 80-150°C. Composition II is a moisture-curing RHM adhesive, and is described below. Composition II Parts by Weight Broad Range Narrow Range Specific Premix A 200-1000 400-600 500 CKOO36 Phenolic 5-50 10-30 18.5 CaCO₃ powder 0-200 50-150 111 Fumed Silica 0-50 15-25 22.2 Dicy/Epoxy Mix 5-50 15-25 22.2 Schiff base 5-50 15-25 22.2 gamma-Glycidoxypropyltrimethoxy silane 1-10 1-5 3 The specific formulation in Table II gave a shear strength of 5.5 MPa (800 psi) and peel strength of 17.5 N/cm (10 pli), by ASTM procedures, supra . The two Compositions (I and II) described in Tables I and II are species of the broader genus set forth in Table III. Reactive Hot Melt Adhesives Component Parts by Weight Premix A 50 - 1000 Epon-872®/Epon-1001F®, 3:1 10 - 500 Epon 828® 10 - 200 Calcium Silicate 0 - 200 CaO 0 - 100 Fumed silica 0 - 80 Phenolic resin 5 - 100 Zn₃(PO₄)₂ 5 - 100 Epon-828®/dicyandiamide, 2:1 5 - 150 gamma-Glycidoxypropyltrimethoxy silane 1 - 10 Schiff base 0 - 50 Calcium carbonate powder 0 - 200 Variations The use of Epon-1001 F® is not critical. Various other Epons are useful, e.g., Epon-836®, which is: a Bis-phenol A adduct with Epon 828®, viz., QKRKQ, where Q, K, and R are as above defined. Celanese-5132® (a trimer acid adduct) may be used in whole or in part for Epon-872® (though I prefer the latter). Substantially any polyisocyanate can be used, substituting in whole or in part for MDI, viz.: Diisocyanates such as hexamethylene diisocyanate, m-phenylene diisocyanate, 2,4-toluene diisocyanate, 4,4'-diphenylmethane diisocyanate, dianisidine diisocyanate, tolidine isocyanate, isophorone diisocyanate, 4,4-dicyclohexylmethane, chlorophenylene-2,4-diisocyanate, 1,5-naphthalene diisocyanate, ethylene diisocyanate, diethylidene diisocyanate, propylene-1,2-diisocyanate, cyclohexylene-1,2-diisocyanate, 3,3'-dimethyl-4,4'-biphenylene diisocyanate, 3,3'-dimethoxy-4,4'-biphenylene diisocyanate, 3,3'-diphenyl-4,4'-biphenylene diisocyanate, 4,4'-biphenylene diisocyanate, 3,3'-dichloro-4,4'-biphenylene diisocyanate, and furfurylidene diisocyanate. Triisocyanates such as biuret of hexamethylene diisocyanate and triphenylmethane triisocyanate. Polyisocyanates such as polymeric diphenylmethane diisocyanate. Heating The heating step to cure my epoxy, urethane-containing, hot melt adhesive compounds to thermoset materials is usually carried out for a period of 10 seconds to 30 minutes at a temperature of 100 - 300°C, preferably 150 - 200°C, which is sufficient to fully cure the composition to a solid thermoset adhesive, coating or sealant. The heating step to cure the compound can be accomplished in several ways. In simple adhesive systems, the composition can be applied by manual means to an adherend, contacted with another adherend and the assembled systems heated in a forced air oven until a thermoset bond results. The composition according to the invention is defined as follows : A reactive hot melt composition obtainable by mixing, in parts by weight (1) Premix A, 50 - 1000 parts; (2) Epoxy resin mixture consisting of epoxy resin B and epoxy resin C in a weight ratio of about 3:1, 10 - 500 parts; (3) Epoxy resin D,10 - 200 parts; (4) Calcium silicate powder, 0 - 200 parts; (5) CaO, 0 - 100 parts; (6) Fumed silica, 0 - 80 parts; (7) Phenolic resin, softening point 87.8 - 143.3°C (190 - 290°F), non-heat reactive, 5 - 100 parts; (8) Zn₃(PO₄)₂, 5 - 100 parts; (9) Mixture, about 2:1 by weight, of Epoxy resin D and dicyandiamide 5 - 150 parts; (10) gamma-Glycidoxypropyltrimethoxy silane, 1 - 10 parts; (11) Schiff base, 0 - 50 parts; and (12) CaCO₃ powder, 0- 200 parts; where Premix A comprises in parts by weight, (i) a ca. 4000 g/mole ethylene oxide end-capped polypropylene glycol triblock copolymer, - - - ethylene oxide - - - propylene oxide - - -ethylene oxide - - -, containing primary -OH groups, 5 - 100 parts; (ii) a ca. 4000 g/mole polypropylene glycol homopolymer, with secondary -OH groups, 0 - 50 parts; (iii) phenyl diethanolamine, 0 - 2 parts; (iv) about 50:50 weight mixture of diphenyl-methane diisocyanate and an adduct of tripropylene glycol and diphenyl methane diisocyanate, 5 - 20 parts, wherein diphenyl methane diisocyanate can completely or partly be replaced by other diisocyanates, by triisocyanates or by other polyisocyanates, and wherein the amount of this mixture is further selected such that the molecular ratio of -NCO/polyol -OH is between 1 and 2; (v) Epoxy resin C, 0 - 50 parts; (vi) Epoxy resin B, 10 - 50 parts. where Epoxy resin B is where X is: Y is -R-K-Q R is -CH₂CH(OH)CH₂- K is Q is Epoxy resin C is Epoxy resin D is Q-K-Q Provided that, when CaO is present, then Schiff base is zero, and vice-versa; and Provided that the total of calcium silicate, fumed silica, and calcium carbonate is in the range of about 10-30 weight % of the total composition. Preferred compositions are the following: 1. A composition wherein, in parts by weight, (1) Premix A is 50 - 800 parts; (2) The mixture of epoxy resins B and C is 10 - 500 parts; (3) Epoxy resin D is 10 - 200 parts; (4) Calcium silicate is 0 - 200 parts; (5) CaO is 10 - 100 parts; (6) Fumed silica is 5 - 80 parts; (7) Phenolic resin, softening point 112.8-143.3°C (235-290°F), is 5 - 100 parts; (8) Zn₃(PO₄)₂ is 5 - 100 parts; (9) Epoxy resin D/dicyandiamide mixture is 50 - 150 parts; (10) gamma-Glycidoxypropyltrimethoxy silane is 1 - 10 parts. (11) Schiff base, 0; and (12) CaCO₃ powder, 0. 2. A Composition wherein, in parts by weight, (1) Premix A is 50 - 800 parts; (2) The mixture of epoxy resins B and C is 50 - 400 parts; (3) Epoxy resin D is 25-125 parts; (4) Calcium silicate is 50 - 150 parts; (5) CaO is 25-75 parts; (6) Fumed silica is 20 - 60 parts; (7) Phenolic resin is 15 - 75 parts; (8) Zn₃(PO₄)₂ is 5 - 50 parts; (9) Epoxy resin D/dicyandiamide mixture is 60 - 120 parts; (10) gamma-Glycidoxypropyltrimethoxy silane is 3 - 7 parts; 3. A composition wherein, in parts by weight, (1) Premix A is 50 - 800 parts; (2) The mixture of epoxy resins B and C is 200 parts; (3) Epoxy resin D is 50 parts; (4) Calcium silicate is 100 parts; (5) CaO is 50 parts; (6) Fumed silica is 40 parts; (7) Phenolic resin is 20 parts; (8) Zn₃(PO₄)₂ is 10 parts; (9) Epoxy resin D/dicyandiamide mixture is 80 parts; (10) gamma-Glycidoxypropyltrimethoxy silane is 5 parts. 4. A composition wherein, in parts by weight, (1) Premix A is 100 - 300 parts. 5. A composition-wherein, in parts by weight, (1) Premix A is 250 parts. 6. A composition consisting essentially of, in parts by weight, (1) Premix A, 200-1000 parts; (6) Fumed silica, 0-50 parts; (7) Phenolic resin, softening point 87.8-112.8°C (190-235°F), 0-50 parts; (9) Epoxy resin D/dicyandiamide mixture, 5-50 parts; (10) gamma-Glycidoxypropyltrimethoxy silane, 1-10 parts; (11) Schiff base, 5-50 parts; and (12) Calcium carbonate, 0-200 parts. 7. A composition wherein, in parts by weight, (1) Premix A is 400-600 parts; (6) Fumed silica is 15-25 parts; (7) Phenolic resin is 10-30 parts; (9) Epoxy resin D/dicyandiamide mixture is 15-25 parts; (10) gamma-Glycidoxypropyltrimethoxy silane is 1-5 parts; (11) Schiff base is 15-25 parts; and (12) Calcium carbonate is 50-150 parts. 8. A composition wherein, in parts by weight, (1) Premix A is 500 parts; (6) Fumed silica is 22.2 parts; (7) Phenolic resin is 18.5 parts; (9) Epoxy resin D/dicyandiamide mixture, 22.2 parts; (10) gamma-Glycidoxypropyltrimethoxy silane is 3 parts; (11) Schiff base is 22.2 parts; and (12) Calcium carbonate is 111 parts.

Claims: A reactive hot melt composition obtainable by mixing, in parts by weight (1) Premix A, 50 - 1000 parts; (2) Epoxy resin mixture consisting of epoxy resin B and epoxy resin C in a weight ratio of about 3:1, 10 - 500 parts; (3) Epoxy resin D,10 - 200 parts; (4) Calcium silicate powder, 0 - 200 parts; (5) CaO, 0 - 100 parts; (6) Fumed silica, 0 - 80 parts; (7) Phenolic resin, softening point 87.8 - 143.3°C (190 - 290°F), non-heat reactive, 5 - 100 parts; (8) Zn₃(PO₄) 2, 5 - 100 parts; (9) Mixture, about 2:1 by weight, of Epoxy resin D and dicyandiamide 5 - 150 parts; (10) gamma-Glycidoxypropyltrimethoxy silane, 1 - 10 parts; (11) Schiff base, 0 - 50 parts; and (12) CaCO₃ powder, 0- 200 parts; where Premix A comprises in parts by weight, (i) a ca. 4000 g/mole ethylene oxide end-capped polypropylene glycol triblock copolymer, - - - ethylene oxide - - - propylene oxide - - -ethylene oxide - - -, containing primary -OH groups, 5 - 100 parts; (ii) a ca. 4000 g/mole polypropylene glycol homopolymer, with secondary -OH groups, 0 - 50 parts; (iii) phenyl diethanolamine, 0 - 2 parts; (iv) about 50:50 weight mixture of diphenyl-methane diisocyanate and an adduct of tripropylene glycol and diphenyl methane diisocyanate, 5 - 20 parts, wherein diphenyl methane diisocyanate can completely or partly be replaced by other diisocyanates, by triisocyanates or by other polyisocyanates, and wherein the amount of this mixture is further selected such that the molecular ratio of -NCO/polyol -OH is between 1 and 2; (v) Epoxy resin C, 0 - 50 parts; (vi) Epoxy resin B, 10 - 50 parts. where Epoxy resin B is where X is: Y is -R-K-Q R is -CH₂CH(OH)CH₂- K is Q is Epoxy resin C is Epoxy resin D is Q-K-Q Provided that, when CaO is present, then Schiff base is zero, and vice-versa; and Provided that the total of calcium silicate, fumed silica, and calcium carbonate is in the range of about 10-30 weight % of the total composition. Composition according to Claim 1 wherein in parts by weight, (1) Premix A is 50 - 800 parts; (2) The mixture of epoxy resins B and C is 50 - 400 parts; (3) Epoxy resin D is 25-125 parts; (4) Calcium silicate is 50 - 150 parts; (5) CaO is 25-75 parts; (6) Fumed silica is 20 - 60 parts; (7) Phenolic resin is 15 - 75 parts; (8) Zn₃(PO₄)₂ is 5 - 50 parts; (9) Epoxy resin D/dicyandiamide mixture is 60 - 120 parts; and (10) gamma-Glycidoxypropyltrimethoxy silane is 3 - 7 parts. Cured composition made by heating the composition of Claims 1 or 2 to 100 to 300°C. Composition according to Claim 3 which is made by heating to 150 to 200°C. Article comprising two metal substrates containing therebetween the composition of Claims 1 or 2. Article comprising two metal substrates having therebetween the composition of Claims 1 or 2 in uncured molten condition at a temperature of about 80 - 150°C. Article comprising 2 metal substrates bonded by having between them uncured molten to semi-molten adhesive composition of Claims 1 or 2, having a shear strength of about 0 to 69 kPa (0 - 10 psi) and a temperature of about 80 - 160°C; the substrates being movable with respect to each other without loss of bond. Article according to Claim 5, 6 or 7, which is coated. Process of adhering two substrates together comprising the sequential steps of (1) heating the adhesive composition of Claims 1 or 2 to 80 - 140°C to melt same, but without curing; (2) applying the heated adhesive composition to a metal substrate; (3) fixturing a second metal substrate into intimate contact with the adhesive composition so as to form a bond between the two assembled substrates; (4) heating the bonded substrates at a temperature of 150 - 200°C to cure the adhesive composition, and to cause adhesion of the substrates. Process according to Claim 9 wherein between steps 3 and 4, 3-a. bonded substrates are integrated into further apparatus, said integration involving stress to the bonded substrates, but without loss of bonding integrity of the composition therein; and 3-b. the further apparatus is coated by exposure to excess coating liquid, without dissolution of the adhesive composition into the coating liquid.

Inventors: KIMBALL MICHAEL E, KIMBALL, MICHAEL E.
Applicants: TEROSON GMBH
Application year: 1989
Main classification: C08G18
IPC codes: C09J175, C08L63, C08G18, C09J163