Use of hydroxycarboxylic acids as stabilizers for bisphenols

Abstract: Lactic, malic and glyceric acids have been found to be superior to the hydroxy carboxylic acids heretofore employed for stabilizing bisphenols. The hydroxy carboxylic acids of the present invention or their ammonium or alkali metal salts can be added to the feed reactants used to make a bisphenol or to the reaction mixture after the reaction is complete or at any point in between. Lactic, malic and glyceric acids are particularly useful when the bisphenol is exposed to high temperatures, e.g. during the separation of the bisphenol from the reaction mixture or in a melt.

Description: Most polymers are generally thought to be heat and oxygen sensitive and tend to degrade to form degradation products which have an adverse effect on the color of the polymers, as well as the physical properties of the polymers. Bisphenols, which are important in the preparation of epoxy resins and polyesters, are also known to be heat and oxygen sensitive, and when subjected to heat and/or oxygen, bisphenols form degradation products which adversely affect polymers subsequently made from the bisphenols containing these degradation products. Thus, bisphenol A is known to decompose with heat to form degradation products such as phenol and p-isopropylidene phenol. Additional heating of bisphenol A can cause formation of other degradation products such as complex non-volatile compounds. These degradation products from bisphenol A, even in small concentrations, can cause a lowering of the molecular weight of polyesters prepared from bisphenol A. Some of the degradation products formed in bisphenol can cause undesirable color in the bisphenol itself during is purification and in epoxy resins and/or polyesters since both purification and manufacturing processes employing bisphenol involve heating. Stabilization of polymers from thermal degradation is believed to be achieved by incorporating a primary radical scavenger, usually a phenolic derivative. To combat the oxidation of the polymer one also must use a hydroperoxide decomposer together with the radical scavenger. Representative of hydroperoxide decomposers are thioesters and phosphites, such as dilaurylthiodipropionate and tri(nonylphenyl)phosphite. One reference, J. Appld. Polym. Sci., Vol. 27 , 951-955 (1982), reports the investigation of tetrakis(2,4-di-tert-butylphenyl)4,4'-biphenylylene diphosphonite (SANDOSTAB PEPQ, a trademark of Sandoz Corporation) as both a hydroperoxide decomposer and a primary radical scavenger. The presence of metal ions in bisphenol is also thought to have an adverse affect on the color of bisphenols, probably by promoting degradation. Various other additives have been employed to inhibit the formation of degradation products in bisphenols. Thus, alkaline earth phosphates, stannous oxide and oxalate, tin powder and tin dioxide, terephthalic and isophthalic acids, oxalic, sebacic and adipic acids and boron and antimony trioxides and their mixtures are useful additives for providing thermal stability to bisphenols as taught in GB-B-890,432. GB-B-1,022,583, teaches that improved color stability is provided to bisphenols by incorporating oxalic, citric or tartaric acids or their alkali metal or ammonium salts in bisphenols during the bisphenol manufacturing process. It also teaches that the acids themselves or their ammonium salts are preferred and the acids or salts thereof may be added to the reactants for making bisphenol or to the reaction mixture after the reaction is complete, but before the bisphenol is separated from the reaction mixture. US-A-3,629,339 teaches stabilizing phenols and bisphenols with an inorganic arsenic compound such as arsenic trioxide or ammonium and alkali metal arsenites. US-A-4,160,110 teaches that various phthalic anhydrides are useful as distillation inhibitors against degradation of bisphenols. Thus, phthalic anhydride itself and tetrahydrophthalic anhydride are indicated by US-A-4,160,110 as useful as distillation inhibitors. JP-B-48-097854 discloses stabilizing bisphenol A by distilling it in the presence of a polypropylene glycol, epoxy soybean oil, 2,2-bis-(p-glycidylphenyl)-propane or a glycerol poly(oxypropylene) adduct. Bisphenols are stabilized against thermal decomposition by incorporating therein a quaternary aliphatic ester of ortho titanic acid according to the teachings of US-A-4,359,590. JP-B-47043937 teaches that the heat stability of bisphenol A can be improved by adjusting the pH of the Bisphenol A to between 2.0 and 5.0 by adding to the bisphenol A a weak acid such as glycolic, thioglycolic and polyphosphoric acid. JP-B-47043937 also reported testing other acids in addition to glycolic, thioglycolic and polyphosphonic acid for comparative purposes including phosphorous, boric and, lactic acid, none of which were considered to be effective. JP-B-47043937 reported that the use of lactic acid as an inhibitor produced no better results than an uninhibited product with respect to color when bisphenol A was tested for discoloration by heating in air for 1.5 hours at 250°C. It is the object of the present invention to stabilize a bisphenol during its preparation or purification more effectively. The object is solved by the use of lactic, malic, glyceric acids, or mixtures thereof, in form of the acids or as their ammonium or alkali metal salts or inhibiting the thermal degradation of a bisphenol, prepared from an aldehyde or a ketone and a phenol, during the preparation or purification of such bisphenol. The present invention is based on the discovery that certain hydroxy carboxylic acids, not hitherto employed as stabilizers, act as excellent stabilizers (inhibitors). The hydroxy carboxylic acids of the present invention have been found to be excellent inhibitors against the degradation of bisphenols and especially for inhibiting the formation of degradation products which can cause color in the bisphenol itself or in the polymeric products made from bisphenol. The particular hydroxy carboxylic acids found to be useful as inhibitors are lactic, malic and glyceric, with lactic or malic being preferred. The acids of the present invention can also be employed as their ammonium or alkali metal salts. Lactic, malic and glyceric acids have been found to be superior to the hydroxy carboxylic acids heretofore employed. The acids of the present invention are particularly useful in stabilizing bisphenols during purification of the bisphenols by distillation or during separation of the bisphenols from the reaction mixture, during which the bisphenols are exposed to elevated temperatures. As is known in the art, bisphenols are prepared by reacting an aldehyde or a ketone with a phenol in the presence of an acid catalyst. Thus, for example. bisphenol A is produced by condensing phenol and acetone in the presence of an acid catalyst such as hydrochloric acid, sulfuric acid or a cation exchange resin in acid form and, if necessary, in the presence of a small amount of an accelerator such as a mercaptan Generally, bisphenol A is obtained from the reaction mixture by distilling or recrystallizing, extracting the residual bisphenol A directly from the reaction mixture or by distilling off excess phenol and water after neutralization. Inhibitors or stabilizers employed by the prior art have been added to the feed reactants prior to the condensation reaction which forms the bisphenol. The prior art also teaches that inhibitors or stabilizers can be added at any point after the condensation reaction so long as the addition is prior to the distillation which separates the bisphenol from the reaction mixture. The hydroxy carboxylic acids of the present invention can be added to the feed reactants used to make the bisphenols or to the reaction mixture after the reaction is complete or at any point in between. While the inhibitor hydroxy carboxylic acids of the present invention can be added either to the reactants or in the reaction mixture, preferably the addition is carried out before the distillation of the bisphenol at which point degradation is most likely to occur. The inhibitors of the present invention perform well either in solution or in a melt containing the bisphenol. The hydroxy carboxylic acids of this invention can be employed separately, in combination with each other, or in combination with other known inhibitors or stabilizers. The operable amount of the inhibitor of the present invention to be employed herein is in the range of from 2 ppm to 300 ppm based on the total weight of bisphenol. A preferred operable amount employed herein is from 5 ppm to 100 ppm and a most preferred operable amount employed herein is from 10 ppm to 30 ppm. Employing less than the above operable amount range will not satisfactorily inhibit the formation of degradation products in bisphenol. While employing more than 300 ppm herein will probably not be deleterious to the bisphenol, it is to no advantage. Test Apparatus and Method A 4-neck, 2 L flask, containing a stirring device and thermometer, padded with nitrogen and fitted with a heating mantle was used to conduct the test for stabilizing bisphenols. Nitrogen pressure was maintained in the flask at 68.9 kPa (10 psig). A stainless steel mesh coupon was inserted through one of the necks of the flask and allowed to remain under the surface of liquid mixture contained in the flask for one hour while the flask was heated to a temperature of 80°C. The liquid mixture was continuously stirred throughout a two-hour period of heating. A 20-gram sample of the liquid mixture was removed from the flask at 1, 1½ and 2-hour intervals. Phenol and water was then stripped from the sample by a roto-evaporator at 180°C. Bisphenol was then checked for color using a Klett colorimeter. Klett readings taken by the Klett colorimeter were converted to APHA numbers based on ASTM (Pt-Co) P1209-69 standards. The following experiments illustrate the inhibiting effect on the degradation of or the stabilization of the bisphenol by the compounds of the present invention: Example 1 To a reaction mixture containing water, acetone, phenol and bisphenol A was added 20 ppm lactic acid based on the bisphenol. The mixture was then heated to a temperature of 180°C and maintained thereat for two hours. The APHA color of the mixture was measured prior to the addition of the lactic acid and after the addition of the lactic acid from time to time during the two-hour period of heating. The increase in APHA color of a bisphenol mixture using a stabilizer of the present invention compared to that of an uninhibited bisphenol mixture (control) is shown in Table I. Examples 2 and 3 In the manner of Example 1, malic and glyceric acids were added to separate mixtures of water, acetone, phenol and bisphenol A (same basis). The APHA color of the mixture was measured prior to the addition of the acids and after the addition of the acids from time to time during the two-hour period of heating while the temperature of the mixture was maintained at 180°C. The increase in APHA color of the bisphenol mixture using the stabilizer of the present invention is shown in Table I along with a comparison of an uninhibited bisphenol mixture (control). Comparative Examples A, B, C and D For comparative purposes, various compounds designated A, B, C and D in Table I were tested as inhibitors for bisphenol under the same conditions employed in Example 1. Results of the tests using inhibitors designated as comparative inhibitors A, B, C and D, Examples 1-3, and a control are shown in Table I. Stabilizer Compound APHA Color at 0 hr. 1 hr. 1½ hrs. 2.0 hrs. None (control) 24 41 49 59 Lactic acid same 30 33 41 Malic acid same 27 29 32 Glyceric acid same 22 26 29 (A) Citric acid same 33 38 45 (B) Tartaric Acid same 41 49 55 (C) Glycolic Acid same 54 63 80 (D) Oxalic Acid same 39 50 71 Other inhibitors known to the art and used commercially, including phosphoric acid, a tris(2,4-di-tert-butylphenyl)phosphite (IRGAFOS 168, a trademark of Ciba-Geigy Corporation) and SANDOSTAB PEPQ, were tested in the same manner as that of Example 1. The inhibitors of the present invention were shown to be superior to these commercially used inhibitors also.

Claims: The use of lactic, malic, glyceric acids, or mixtures thereof, in form of the acids or as their ammonium or alkali metal salts for inhibiting the thermal degradation of a bisphenol, prepared from an aldehyde or a ketone and a phenol, during the preparation or purification of such bisphenol. The use according to claim 1 wherein the acids are employed as their ammonium or alkali metal salts. The use according to claim 1 wherein the bisphenol is bisphenol A. The use according to claim 1 wherein the amount of the inhibitor is in the range of from 2 to 300 ppm based on the weight of the bisphenol. The use according to claim 4 wherein the amount of the inhibitor is in the range of from 5 to 100 ppm. The use according to claim 5 wherein the amount of the inhibitor is in the range of from 10 to 30 ppm.

Inventors: GORMANOS THEODORE J, NEIL LAWRENCE E JR, GORMANOS, THEODORE J., NEIL, LAWRENCE E., JR.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1989
Main classification: C07C37
IPC codes: C08K5, C08L63, C08G59, C07C37, C07C39