Coated coiled metal for use as automotive veneer

Abstract: A coated article comprises an outer, coated metal veneer coated with at least one coating selected from primer coatings, pigmented topcoat coatings, pigmented basecoat coatings and outer clear topcoat coating, the coated metal veneer affixed to an underlying substrate having substantially the same shape as the coated veneer. The coated articles are particularly useful as body parts such as doors, hoods, trunk and roof panels, fenders, and rocker panels of automobile and truck bodies. A method of manufacturing the coated articles is also disclosed.

Description: The invention relates to a coated article and a method of manufacturing a coated article. In the automotive Original Equipment Manufacturer (O.E.M.) industry, it is an accepted, guiding principle that the appearance and styling sells automobiles and vehicles. When purchasing a vehicle, appearance and styling are as important to the consumer as are other vehicle characteristics such as safety, performance and fuel economy. One of the most important characteristics of an automobile's appearance and styling is the paint finish. Improvements in automotive paints and paint processes have resulted in O.E.M.'s using almost exclusively "high-tech" glamour finishes such as base coat/clear topcoat coatings which consist of a thin, pigmented, inner base coat and a thicker clear outer top coat. These "high-tech" finishes have improved depth, gloss, chromaticity and durability. The importance of the coating process for both appearance and corrosion protection is evidenced by the fact that approximately 40% to 50% of the cost of building an automobile is attributable to the cost of the coatings and the coating application process. In addition, the coating process takes up approximately 40% of the floor space in an O.E.M. assembly plant. There is a need in the automotive industry to move the coating operation out of the OEM assembly plant. There are numerous reasons why it is not desirable to have a coating operation in an OEM plant. First of all, the present OEM coating operations are extremely inefficient. It is estimated that about 50% of the coatings are wasted as overspray during the coating process. Massive, costly environmental controls are necessary to capture the overspray. The cost of the wasted overspray paint and the costs attributable to the required environmental controls add considerably to the OEM's overhead. Secondly, an OEM assembly plant is essentially a mechanical assembly operation, while the coating operations are in essence physico-chemical processes. The efficiency of the assembly process could be greatly enhanced by moving the coating process outside of the assembly plant. Thirdly, it is known that dust and particles adversely affect coatings, both in appearance and integrity. Since the nature of an OEM assembly plant is mechanical assembly requiring a large open facility, it is difficult to control the environment of such a plant to completely eliminate dust and particles. There is a need to conduct coating operations in a controlled environment wherein the process takes place in a contained area with state-of-the-art heating, ventilating, air-conditioning, and filtration utilities, and environmental controls. Environmental concerns as previously mentioned are yet another reason for moving the coating operation outside of the OEM assembly plant. The typical OEM coating and curing operations generate significant emissions of volatile organic compounds (VOC) into the environment, both within and outside of the OEM assembly plant. Along with the VOC emissions, significant quantities of waste are generated by the coating processes. This waste must be disposed of in strict compliance with all applicable federal, state and local environmental regulations at considerable cost. Automobile manufacturers would prefer that automobile bodies painted are "off-site" and shipped to the assembly plant. While it is theoretically possible to coat the automobile bodies at the off-site manufacturing facility, this has not been possible due to the likelihood of damage to the finishes that would almost certainly occur during shipping. In addition to the problems associated with in-plant coating operations, another problem facing OEM assembly plants is the coating of plastic bodies. There is a movement in the industry to convert from carbon steel to plastic bodied cars. Plastic parts are difficult to coat due to the inherent nature of plastics, which typically have difficult to adhere to surfaces. Plastics are also susceptible to attack and degradation from the solvents that are typically contained in automotive paints. Plastics are typically heat sensitive and require low temperature cure coatings. However, low temperature coatings do not always have optimal coating properties such as durability, gloss and solvent resistance. In addition, it is difficult to produce an automotive quality "glamour" finish on a plastic body part due to the inherent surface distortions and imperfections associated with molded body parts. In order to compensate for surface defects, primers and primer/surfaces must be used on plastic parts, not for corrosion protection, but to mask surface defects. In addition to plastic bodies, alternative substitute materials such as cellulosic materials and ceramic materials as well as other available materials are under consideration for use in automobile bodies. There have been attempts to move a coating process out of assembly plants. U.S. Patent 2,331,546 discloses a method of coating a flat steel plate with a flexible automotive coating. The coated plates are then die-formed into automobile body parts which can be directly assembled into an automobile body, purportedly without requiring any additional finishing treatment. U.S. Patent No. 3,774,428 discloses a method of precoating coiled aluminum metal and subjecting the metal to a die process to create a surface pattern. The resulting die-formed coated articles are used as siding for buildings. U.S. Patent No. 4,769,100 discloses a method of applying carrier films prepainted with metallic paint to automobile body panels. While such prepainted free films have the advantage of application over flexible substrates, they are subject to certain disadvantages. Such films tend to trap bubbles during application to the substrate; they also tend to "telegraph" imperfections in the surface of the substrate such as bumps, dimples, or reinforcing fiber patterns. EP-A-285 974 discloses an article comprising an outer metal veneer, said metal veneer formed from metal, the veneer having an inner surface and an outer surface and an underlying substrate having substantially the same shape as the veneer, said substrate having an inner surface and an outer surface, the outer surface being affixed to the inner surface of the veneer to form the article. EP-A-285 974 is not concerned with the technical problems underlying the present invention. What is needed in this art is a method of coating automobile body parts which would eliminate the need for having a coating process in an OEM assembly plant. The coated parts would be assembled directly onto an automobile chassis. There is also a need in this art for a way of producing glamour coating finishes on body parts wherein the body parts comprise various materials other than metal. Disclosure of the Invention The disclosed coated article is comprising an outer metal veneer, the veneer having an inner surface and an outer surface and an underlying substrate having substantially the same shape as the veneer, said substrate having an inner surface and an outer surface, the outer surface of said-substrate being affixed to the inner surface of the veneer to form the article, wherein the metal veneer is formed from coiled metal, at least one surface of the coiled metal is coated with at least one coating selected from the group consisting of primer coatings; pigmented topcoat coatings; inner pigmented basecoat coatings, and outer clear topcoat coatings. The inner, underlying substrate is formed from metal, solid or foamed plastic, fiber reinforced resinous material such as fiberglass. Yet another aspect of the present invention is a method of manufacturing a coated article comprising the steps of a) forming metal pieces into veneers in a die forming means, the veneers having an outer surface and an inner surface; and b) affixing the inner surface of the veneer to the outer surface of a substrate, the substrate having substantially the same shape as the veneer; wherein the metal pieces are formed from coated coiled metal by c) coating at least one side of a coiled metal stock with at least one coating selected from the group consisting of primer coatings; pigmented topcoat coatings; inner pigmented basecoat coatings and outer clear topcoat coatings; and d) cutting the coated metal from step c) into pieces in a cutting means. In the method of this invention, the metal is coated prior to the steps of cutting, forming, and affixing, by coil coating. The coated metal is cut into pieces and the coated pieces are formed into coated veneers. The veneers have an outer surface and an inner surface. The coated veneer is then affixed to an underlying substrate, the substrate formed of metal, solid or foamed plastic, or fiber-reinforced resinous material which has a shape substantially conforming to or similar to the shape of the veneer. The substrate has an outer surface and an inner surface. The inner surface of the coated veneer is affixed to the outer surface of the substrate, thereby producing the coated article. In yet another aspect of the present invention, automobile bodies comprise coated articles manufactured by the process of the present invention. The foregoing, and other features and advantages of the present invention will become more apparent from the following description. BRIEF DESCRIPTION OF THE DRAWINGS FIGURE 1 shows an automobile fabricated, at least in part, of veneers of the present invention. Section 3-3, depicted in detail in Figure 3, is a vertical section of the automobile door panel. FIGURE 2 shows a cross-section of one embodiment of the veneers of the present invention. FIGURE 3 is a detailed cross section of a veneer of the present invention. FIGURE 4 shows a flow process for producing veneers of the present invention. BEST MODE FOR CARRYING OUT THE INVENTION The coil coating process is well known in the coating arts. Coil coating can be defined as a continuous, automated process for applying coatings to coiled metal stock. Typically the process is initiated by simultaneously unwinding coiled metal and feeding the uncoiled metal stock to a coil coating means. A coil coating means typically consists of a plurality of rollers, feed mechanisms and coating means. As the metal stock from the coil is fed through the coil coating means it is cleaned and then coatings are applied and cured or dried at various stages. The coated metal stock is then rewound as it exits the coil coating means. In the coil coating process of the present invention, the coiled metal is fed into a coil coating means. The metal stock is initially cleaned at a cleaning section in the following manner. The coil is passed through a series of solvent baths or baths in combination with solvent vapor degreasers to remove mill oils and other surface contaminants. Solvent selection is determined by contaminants to be removed and metal being treated. Trichlorethylene, perchlorethylene and similar solvents are commonly used. The moving coil is then pretreated with suitable surface protective chemicals. Zinc and/or iron phosphate treatments are typical for ferrous metals and crystalline and amorphous phosphate or amorphous chromate is used on aluminum substrate. Next, the metal is dried in an oven at a sufficient temperature, typically about 140°C. The dried metal stock then moves to a primer coating application section. The primer coating is optionally applied to one or both sides of the metal stock to produce a coating having sufficient thickness, typically about 0.0005 cm (0.2 mil) to about 0.005 cm (2.0 mils). Next, the primer is moved through a curing oven where it is baked at a temperature sufficient to cure the primer, typically about 52°C (125°F) to about 815°C (1500°F). Then, after the primed coil exits the curing oven, it moves to a pigmented base coat application section. A pigmented base coat coating composition is applied to at least one side of the coil, preferably the top side by using a roller coating method commonly used in the coil coating industry whereby rollers are used to pick up paint from a reservoir and transfer it through a series of nearly contacting rollers to the metal coil stock from a final application roller. Alternatively, the coating may be applied by an air atomised spray. The coating is applied to a sufficient dry film thickness, typically about 0.0003 cm (0.1 mil) to about 0.0064 cm (2.5 mil). An optional bake stage to dry or flash the base coat might be used at this step. Then, once the base coat has been applied, the coil moves to the next section where a clear outer topcoat is applied over the basecoat. The outer topcoat is also applied through the use of transfer rollers to apply a clear overcoat to a sufficient dry film thickness or, alternatively, by spray methods known in the art. The film thickness of the top coat is typically about 0.009 cm (3.5 mils) on a dry film basis. Once the clear topcoat has been applied, the coil moves to an oven section. The coil resides in the oven for a sufficient length of time at a sufficient temperature to cure the basecoat and clearcoat to a hard, but flexible, and durable coating. It will be appreciated by those skilled in the art that the topcoat can consist of a pigmented topcoat, a pigmented inner basecoat and clear outer topcoat, a clear topcoat, or multilayer coatings such as those disclosed in U.S. Patents Nos. 4,753,829; 4,615,940; and 4,598,020 which are incorporated herein by reference. Next, the coil stock moves to a coating station where a sufficient thickness of a protective coating is applied over the topcoat by roller transfer coating, doctor knife, curtain coater, dip coating, spray coating, or other means well known to those in the art. After drying or curing the protective coating to a protective, but removeable, outer coating, the coated metal is preferably rewound as it exits the coil coating means, and removed from the coil coating means. It is optional, however, to feed the coated metal stock to the next stage without coiling. In the next stage of the process, the metal is unwound, and cut into pieces of sufficient size and shape to form a particular contoured veneer. The term "veneer" is defined to mean a contoured, coated metal article produced by the processes of the present invention. The cutting is accomplished by cutting apparatuses known in the art such as die cutting, laser cutting, saw cutting, and high pressure water cutting apparatuses or by other methods and apparatuses common to the metal fabrication industry. After the coiled metal is cut into pieces, the pieces are inserted into die forming means and processed under sufficient pressure for a sufficient length of time and optionally at elevated temperature for enhanced flexibility of the coating system to produce a contoured veneer having an automotive grade exterior finish overcoated with a protective removable film. Examples of die-forming means include drawing, ironing, flexible dye forming such as the Verson-Wheelon process, Marform process, stretch forming, stretch-draw forming and other techniques known in the art. The veneers can either be affixed to preformed, contoured automotive body parts or co-molded to a substrate, preferably plastic, to form coated metal veneer body parts. Figure 4 is a flow diagram showing a typical process according to this invention. Referring to this diagram, the process is initiated by feeding a continuous band of metal coil 115 into coil coating means 180 via feed means 120 . Coil stock 115 is pretreated in pretreatment means 125 with a conventional pretreatment such as a phosphating solution. Pretreated coil stock 115 then moves to primer application means 135 where a coating of primer is applied. The primed coil stock 115 is then moved to oven 140 where the primer coating is cured and/or dried. The primed coil stock 115 is then moved to coating means 145 where a topcoat coating is applied over the optional primer coating. The top coating preferably consists of a pigmented inner base coat coating and a clear outer topcoat coating applied over the pigmented base coat. The top coated coil stock 115 then is moved to oven 150 where the basecoat coating and the clear outer topcoat coating are cured. The top coated coil stock 115 is optionally moved to protective coating application means 155 where an optional, removable, protective coating is applied over top coated coil stock 115 . Coil stock 115 is then moved to oven 160 where the protective coating is cured and/or dried to form coated coil stock 165 . The coated coil stock 165 is then moved to coiling means 170 where it is rewound. Coated coil stock 165 is moved to uncoiling feed means 175 . In the next stages of the process, the uncoiled coated stock 165 is fed to cutting means 180 where it is cut into coated blanks 185 . Coated blanks 185 are fed into die-forming means 190 where the blanks are formed into coated veneers 195 . Coated veneers are then affixed to a structural substrate to form the final coated structure. One embodiment of a veneer of the present invention, affixed to a structural substrate, is shown in Figure 2. The structure 40 is shown between the male 20 and female 10 halves of a die-forming means. Structure 40 consists of an outer coated veneer 60 and an inner substrate 50 . Inner substrate 50 is affixed to veneer 60 and conforms to the shape of veneer 60 . A magnified section of structure 40 is illustrated in Figure 3. Referring to Figure 3, structure 40 is seen to comprise metal veneer 60 and underlying substrate 50 which is bonded to veneer 60 . Veneer 60 consists of metal substrate 70 having top surface 72 and inner surface 68 . Optional primer coating 80 is on top surface 72 of metal substrate 70 . Pigmented base coat 90 covers primer coating 80 . Clear topcoat 100 is on top of pigmented basecoat 90 . Optional protective coating 110 is over clear coat coating 100 . Substrate 50 has substantially the same shape as veneer 60 and is affixed to inner surface 68 of metal veneer 60 to form coated structure 40 . Substrate 50 can be affixed to veneer 60 by several techniques including glueing, fastening, hot melt adhesives, Velcro ® , riveting, stapeling and the like. Figure 1 illustrates a typical automobile body fabricated, at least in part, of veneer structures of the present invention. The veneers may comprise such parts of the automobile body as door, hood, and trunk panels, fenders, rocker panels, and the like. Section 3-3 through the door panel shows a detail of the veneer door panel which appears in detail in Figure 3. The veneer panel structures of this invention may be mounted to the body structure of the automobile by techniques well known in the art such as conventional adhesives, hot-melt adhesives, riveting, stapeling, Velcro ® , nuts and bolts or other similar fastening means, and tongue-and-groove fastening means. The primer coating compositions of the present invention will be based upon resinous film-forming polymer systems such as epoxies, polyesters, polyurethanes, acrylics, ureas and the like. The coating will contain sufficient amounts of cross-linking agents, pigments, and conventional additives. The cross-linking agent will include melamine, amines, ureas, carboxy, urethanes and the like. The pigments will include those commonly used for the end application including titanium dioxide, phthalocyanines, quinacridones, iron oxides, carbon blacks and fillers such as clays, talcs, etc. The conventional additives will include acid catalysts such as sulfonic acids and salts thereof, silicone flow control additives and surface slip aids and various waxes for surface slip and mar resistance. The film-forming basecoat coating compositions useful in the practice of the present invention will typically contain a resinous film-forming polymer, a pigment, a cross-linking agent and other additives typically included in coating compositions in this art. The film-forming polymer system includes epoxies, polyesters, polyurethanes, acrylics, fluoropolymers, and the like. The pigments will include titanium dioxide, phthalocyanines, lamp black, iron oxides, quinacridones, aluminum flake, micas, perylenes, imizadoles, and the like. The cross-linking agents typically used will include melamines, amines, urethanes, carboxy resin, and the like. The additives will include acids and salts thereof,silicone flow controls, fumed silicas, and ultraviolet absorbers (e.g., Tinuvin 328 benzatriazole derivative). The clear topcoat coating compositions will be similar to the basecoat coating compositions except that they will not contain pigment, although slight amounts of pigment could be added as long as the top coat remains transparent. Pigmented topcoat coating systems can be used instead of pigmented basecoat,/clearcoat coating systems. The removable protective coating compositions useful in the processes of the present invention will consist of acrylics, vinyls, urethanes, and the like. These compositions may be plasticized and would typically be thermoplastic in nature. The protective coatings can be removed after application by simply peeling the protective coating off of the coated veneer. Alternatively, the coatings may be designed to be removed by dissolving in amine and water mixtures, for example. The following examples are illustrative of the principles and practice of this invention, although not limited thereto. Parts and percentages where used are parts and percentages by weight. EXAMPLES Example 1 Black basecoat components A and B were made in conventional mixing and milling equipment in accordance with the following formulations and procedures: Component A - The following components were mixed and dispersed in a sand mill: Polyester polyol resin 6.75 kg (14.90 lb) Xylene 2.25 kg ( 4.97 lb) Carbon black 0.68 kg ( 1.49 lb) These components were mixed, after which the following were added: Polyester polyol resin 1.66 kg ( 3.67 lb) Xylene 0.45 kg ( 0.99 lb) The components were mixed and dispersed in a sand mill, after which an additional 12.2 kg (26.92 lb) of polyester polyol resin (1) were added. The resulting mixture was again mixed to form 23.7 kg (52.3 lb) of Component A. Component B - The following components were mixed in a typical mixing vessel: Polyisocyanate DESZ4370 20.10 kg (44.29 lb) Polyisocyanate DEXN75 1.54 kg ( 3.40 lb) Example 2 Black basecoat components A and B from example 1 above are mixed a ratio of 52.31 to 47.69, respectively, and fed to the paint feed supply of the roller coater of an aluminum coil coating applicator. Coil stock is suitably cleaned and pretreated with chromic surface treatment and fed to the coil coating line where the black two-component mixture is applied. The coated coil stock then passes to a baking zone for drying and curing. The coil then proceeds to a second coating roller system where the mixed A and B components are supplied (61.15 to 38.86 ratio) and again cured. 0.003 cm (one mil) of dry film black basecoat and 0.004 cm (one and one-half mil) of dry film clearcoat are applied. The vinyl temporary coating may then be applied and dried again by roller coating the coil. The coated aluminum coil is then cut and die stamped in the form of automotive body exterior skin components. Automotive body skin components having necessary structural properties but lacking exterior final color finish coating are then given final desired surface appearance by affixing this precoated, formed aluminum veneer to these skin parts of essentially the same shape and dimensions. Excellent painted appearance results from this process. Example 3 White basecoat componets A and B were made in conventional mixing and milling equipment in accordance with the following formulations and procedures: Component A - TiO₂ paste Polyester polyol resin 5.75 kg (12.67 lb) TiO₂ pigment 15.5 kg (34.21 lb) Xylene 3.40 kg (7.50 lb) The components are mixed and dispersed in a sand mill. The following components are then added to the sand milled mixture: Polyester polyol resin 4.59 kg (10.12 lb) Tint paste Trace Tint paste Trace Tint paste Trace Tint paste Trace n-Butyl acetate 5.11 kg (11.26 lb) The components are mixed to form 25.4 kg (75.56 lb) of component A. Component B- The following components were mixed in a typical mixing vessel. Polyisocyanate DESZ 4370 10.21 kg (22.51 lb) Polyisocyanate BRSN75 (9) 0.78 kg ( 1.73 lb) Total 10.99 kg (24.24 lb) Example 4 White basecoat is applied by electrostatic high speed rotational atomizing spray (turbobell) as a mixture of Parts A and B (formulated as described above in Example 3) in a ratio of 75.76 parts to 24.24 parts, repectively to a pretreated coil of aluminum stock. The moving coil passes by the turbobell applicator and passes through an oven for solvent dry off and cure. The white coating is 0.004 cm (1.5 mils). This white aluminum coil stock is die cut and stamped into a veneer in the form of an automotive engine compartment hood. A hood of conforming shape is formed and primed according to standard practice. An adhesive is then applied to the exterior surface of the primed, steel hood and the white aluminum veneer is affixed to the surface of the primed steel counterpart by means of this adhesive to form a veneer-coated hood. This structure exhibits a very uniform, smooth, defect free paint appearance to the hood which can then be installed on the automobile in the conventional manner. Example 5 The coated veneer of Example 2 is placed painted face down in the cavity half of a conventional heated compression molding apparatus designed to mold the automobile hood. A properly sized and shaped sheet molding compound (SMC) charge is loaded into the cavity on top of the veneer. The mold is closed and, under sufficient heat and pressure, the SMC flows to fill the mold and achieve intimate contact and physical and/or chemical bond with the treated aluminum surface of the skin. After 1 minute at 177°C (350°F), the mold is opened and the laminate part is ejected and allowed to cool. Secondary trimming, hole cutting, and hardware installation operations may now be performed as required by the design. At this point a fully-finished, automotive quality, laminated body part has been produced and is ready for mechanical assembly to the auto chassis in an OEM assembly plant. The part has an automotive quality coating.

Claims: A coated article comprising an outer metal veneer (70), the veneer having an inner surface (68) and an outer surface (72) and an underlying substrate (50) having substantially the same shape as the veneer, said substrate having an inner surface and an outer surface, the outer surface of said substrate being affixed to the inner surface of the veneer to form the article, characterized in that the metal veneer is formed from coiled metal, at least one surface of the coiled metal (115) is coated with at least one coating selected from the group consisting of primer coatings (80); pigmented topcoat coatings; inner pigmented basecoat coatings (90), and outer clear topcoat coatings (100). The article of claim 1 wherein the coiled metal comprises aluminium. The article of Claim 1 additionally comprising an adhesion-promoting coating on at least one surface of the veneer. The article of Claim 1 additionally comprising a removable, protective coating (110) on at least one surface of the coated veneer. The article of Claim 1 wherein said substrate is formed of metal. The article of Claim 1 wherein said substrate is formed of solid or foamed plastic. The article of Claim 1 wherein said substrate is formed of fiber reinforced resinous material. A method of manufacturing a coated article comprising the steps of a) forming metal pieces into veneers in a die forming means, the veneers (70) having an outer surface (72) and an inner surface (68); and b) affixing the inner surface of the veneer to the outer surface of a substrate (50), the substrate having substantially the same shape as the veneer; characterized in that the metal pieces are formed from coated coiled metal by c) coating at least one side of a coiled metal stock (115) with at least one coating selected from the group consisting of primer coatings (80, 135, 140); pigmented topcoat coatings; inner pigmented basecoat coatings and outer clear topcoat coatings (90, 100,145, 150); and d) cutting the coated metal from step c) (170, 165) into pieces (185) in a cutting means (180). The method of Claim 8 wherein the metal comprises aluminium. The method of Claim 8 wherein said substrate is formed of a material selected from metal, plastic, and fiber-reinforced resinous material. The method of Claim 8 wherein the step of affixing the inner surface of the veneer to the outer surface of the substrate comprises adhesive bonding. The method of Claim 8 wherein a removable protective coating is applied over at least one side of the coated metal prior to cutting (110, 155, 160).

Inventors: BENEFIEL JAMES W, BENEFIEL, JAMES W.
Applicants: BASF CORP, BASF CORPORATION
Application year: 1989
Main classification: B05D7
IPC codes: B05D7, B32B38, B05D1, B32B15, C09D5