Resinous composition for coating use

Abstract: A resinous composition for coating use comprising (a) 3 to 70% by weight of organopolysiloxane represented by the formula: R¹ n R² m SiO (4-n-m)/2 wherein R¹ represents hydrogen, allyloxy group, an alkoxy group having 1 to 20 carbon atoms, an aryl group, methyl group, or an organic group having 2 to 100 carbon; R² is a hydroxyl group bearing organic group having 2 to 100 carbon atoms; m and n each represents a positive number fulfiling the requirements of 0<n<4, 0<m<4 and 2≦m+n<4, having a number average molecular weight or 200 to 100,000 and a hydroxyl value of 20 to 400, (b) 97 to 30% by weight of hydroxyl group containing resin having a hydroxyl value of 20 to 300, and (c) crosslinking agent which is reactive with hydroxyl group This composition is particularly useful in the area in where durability and weather resistance of the formed coating are specifically required.

Description: Field of the invention The present invention relates to a resinous composition for coating use and more specifically, it concerns a resinous composition containing an alcoholic hydroxyl group bearing polysiloxane and being particularly useful in the area in where durability and weather resistance of the formed coating are specifically required. Background of the invention Though a polysiloxane resin is excellent in thermal resistance, water repellency, weather resistance and the like, it has never been used alone because of its poor mechanical strength. Therefore, attempts have been made to use this resin for the modification of other kind of resins as acrylic resin, polyester resin or the like, whereby making the most of the excellent properties of said resin. However, in the heretofore proposed modification means, use is made of the reaction between silanol or alkoxy group contained in the polysiloxane resin and hydroxyl group contained in the organic base resin as acrylic or polyester resin. Therefore, both resins are always connected with each other through Si-O-C bonding. Nevertheless, this Si-O-C bonding is liable to be easily hydrolyzed and hence the siloxane resin is regenerated by hydrolysis and gradually removed off, resulting the decrease in corrosion resistance, weather resistance, stain resistance and the like of the coating. In Japanese Patent publication (unexamined) Sho 58-217515, Japanese Patent Publication Sho 58-58123 and the like, has been proposed a modification of urethane resin with dimethylpolysiloxane having at both ends alcoholic hydroxyl groups. However, this leaves much to be desired because the crosslinking density is comparatively low and hence the surface hardness and mechanical strength of the formed coating are fairly in lower order. The same applies to the polyurethanes disclosed in US-A-3 923 747 which are obtained by reacting together a hydroxyl-terminated polyester, a poly (epsilon-caprolactone) diol, an aliphatic diol containing at least 5-carbon atomes, a hydroxyl terminated dimethyl polysiloxane and an acyclic or alicyclic diisocyanate. In Japanese Patent Publication Sho 60-1886 and 63-23212, there is another proposal such that plural alcoholic hydroxyl groups are located at the side chain portions of polysiloxane resin, thereby increasing the crosslinking density. However, such resin can not be added in a quantity to the organic base resin because of its poor compatibility and hence it is hardly possible to obtain a thoroughly modified resin. It is, therefore, an object of the invention to provide the measures for incorporating strongly a quantity of silicone resin into a base resin and provide a resinous composition for coating use by making use of said measures. It is an additional object of the invention to provide a resinous composition which is useful in a coating composition capable resulting a coating with excellent durability and weather resistance. Summary of the invention According to the invention, the aforesaid objects can be attained with a resinous composition for coating use comprising (a) 3 to 70% by weight, based on (a) and (b), of organopolysiloxane represented by the formula: A x R 3-x SiO(R₂SiO) y (RASiO) z SiR 3-x A x in which A is HOCH₂CH₂OCH₂CH₂CH₂-; the groups R are independently an aryl group, a methyl group or an organic group of 2 to 100 carbon atoms having 2 to 100 methylene groups in its main chain which may be interrupted with an ester, an ether or a urethane group and may contain carbon-carbon unsaturation or functional groups other than hydroxyl groups; x is 0 or 1; and y and z each represents a positive number fulfilling the requirements of 1 ≦ y ≦ 20 and 1 ≦ z ≦ 10, having a number average molecular weight of 200 to 100,000 and a hydroxyl value of 20 to 400, (b) 97 to 30% by weight, based on (a) and (b), of a hydroxyl group containing acrylic, alkyd, polyester, epoxy, acryl modified alkyd or acryl modified polyester resin having a hydroxyl value of 20 to 300, and (c) a crosslinking agent which is a polyisocyanate, a melamine-formaldehyde resin or a dibasic acid anhydride. For the preparation of organopolysiloxanes for use according to the invention which contain a group A (HO-C₂H₄-O-C₃H₆-) as a side chain, there can be referred to the several routes which will generally be described hereinafter. Such polysiloxanes may be advantageously prepared by first obtaining a cyclic siloxane represented by the formula: (in which R₃ is an alkylene chain having 2 to 100 carbon atoms and optionally containing ether and/or ester bonding in the chain) by the method wherein a siloxane of the formula: is reacted with m moles of alkylene in the presence of a platinic acid catalyst to obtain the compound of the formula: which is then subjected to an addition reaction with n moles of alkeneoxytrialkylsilane in the presence of a platinic acid catalyst to obtain the compound of the formula: and hydrolized to and then subjecting thus obtained cyclic siloxane ring-opening polymerization by using heat and/or catalyst means. As the catalyst, the following may be advantageously used: conc.sulfuric acid, alkali metal hydroxide or silanolate, quaternary ammonium hydroxide and the like. During the polymerization, it is also possible to use the siloxane compound of the formula: (R')₃-Si-O-Si-(R')₃ in which R' is an alkyl group having 1 to 3 carbon atoms, which may include hydroxyl group. Alternatively, such polysiloxanes may be prepared by reacting a polysiloxane of the formula: with m moles of alkeneoxytrimethylsilane in the presence of a platinic acid catalyst to give the compound of the formula: which is then hydrolized to give a compound of the formula: It is also possible to extend the chain length of -R₃-OH by reacting it with ε-caprolactone in the presence of a catalyst as tetrabutyltitanate and the like, thereby improving the compatibility of thus formed organopolysiloxane with an acrylic or polyester resin. In the formula: A x R 3-x SiO(R₂SiO) y (RASiO) z SiR 3-x A x 10 to 50 mole% of R should preferably be phenyl group for a better compatibility of the resin with the organic base resins. More specifically, the organopolysiloxanes include the following: In these formula, Ph stands for phenyl and Me is methyl group. Number average molecular weight of such organopolysiloxane should be in a range of 200 to 100,000, and most preferably 500 to 20,000. If it is less than 200, sufficient mechanical strength at the coating surface can not be obtained, whereas if it is more than 100,000, sufficiently cured coating can not be obtained because of its poor compatibility with the hydroxyl group containing resin and the crosslinking agent. Hydroxyl value of the organopolysiloxane measured by the method of JIS K8004 should be in a range of 20 to 400, and most preferably 50 to 200. This is because if the hydroxyl value is less than 20, such siloxane compound can hardly react with the hardening agent, resulting deficient curring and poor mechanical properties of the coating. Whereas, when the hydroxyl value of the organopolysiloxane is more than 200, there is a problem of poor compatibility with the hydroxyl group containing resin and the crosslinking agent, resulting the deficient curring of the coating, too. The hydroxyl group containing resin co-used with the abovementioned polysiloxane in the present invention may be any acrylic resin, alkyd resin, polyester resin, epoxy resin, acryl modified alkyd resin or acryl modified polyester resin customarily used in paint area, providing having hydroxyl value of 20 to 300. Among them, particularly preferable members are acrylic resins obtained by the copolymerization of hydroxyalkyl(meth)acrylate and (meth)acrylic acid, (meth)acrylate, epoxy resins obtained by the reaction of bisphenol A and epichlorhydrine and polyester resins obtained by the reaction of polycarboxylic acid and polyol polycondensation product. As the crosslinking agent which is another component co-used with the present alcoholic hydroxyl group containing polysiloxane and hydroxyl group containing resin, any of the known crosslinking agents selected from polyisocyanate compounds, melamine-formaldehyde resins and dibasic acid anhydrides having two or more functional groups reactive with hydroxyl group may be satisfactorily used. The role of this crosslinking agent is to crosslink the abovementioned organopolysiloxane with organic resin, organopolysiloxane with other organopolysiloxane, and organic resin witrh other organic resin at room temperatures or under heating conditions. As to the compounding ratio of these components, it may vary in a wide range of 3 to 70% by weight of alcoholic hydroxyl group containing polysiloxane and 97 to 30% by weight of hydroxyl group containing resin. More preferably, the former is in a range of 5 to 40% by weight and the latter is 95 to 60% by weight. The inventors have found that if the content of alcoholic hydroxyl group containing polysiloxane is less than 3% by weight, it is unable to expect the characteristic properties of the polysiloxane in full, and if it is more than the upper limit of 70% by weight, there is a tendency that compatibility of polysiloxane with the said hydroxyl containing resin be lowered and hence a fully cured coating can not be obtained. In this invention, the functional groups contained in the crosslinking agent are reacted with hydroxyl groups of said polysiloxane and hydroxyl group containing resin, thereby resulting three dimensionally crosslinked polymer structure having improved mechanical strength. At that time, said crosslinking agent is used in an appropriate amount so as to give the desired degree of crosslinking. Thus, in the present invention, particular organopolysiloxane and particular hydroxyl-group-containing resin are used together each in defined amounts. However, if desired, all or parts of said organopolysiloxane and hydroxyl group containing resin may be previously reacted and combined together, before being compounded with the said crosslinking agent. For example, the present polysiloxane having hydroxyl group may be reacted with a compound having both unsaturated double bonding and a functional group other than hydroxyl such as, for example, maleic anhydride, methacryloyl isocyanate and the like, to obtain polysiloxane having unsaturated double bonding in its side chain, which is then copolymerized with other α,β -unsaturated acrylic monomers. Thus, in the present invention, differing from the heretofore proposed surface controlling silicone oil, the content of polysiloxane in the resinous composition may be easily controlled and comparatively larger quantity of such polysiloxane can be firmly incorporated into the resinous composition and therefore, quite attractive, novel crosslinked product, which may keep its excellent water repellency for a long duration of time and is excellent in weather resistance and durability can be obtained. In the heretofore known silicone modified acrylic or polyester resins, the modification is usually carried out by the method wherein an organopolysiloxane having silanol or alkoxy groups and a hydroxyl group containing organic resin are heated in the presence of a catalyst as alkyl titanate, zinc octate and the like. Therefore, said organopolysiloxane is incorporated into the organic resin through Si-O-C bonding, which is easily hydrolyzed under ionic atmosphere. Whereas, in the present invention, crosslinking is occured between the functional groups of the crosslinking agent and hydroxyl groups of the polysiloxane and of the organic resin, and therefore, the bonding included in the crosslinking is either one of ester bonding, ether bonding and urethane bonding, which are stable and hardly affected by hydrolysis. Thus in the present invention, while keep maintaining the characteristic properties possed by siloxane compound, i.e. excellent gas and ion permeabilities thermal resistance and water repellency, the formed novel crosslinked product whose properties are far better than those of heretofore known resinous compositions can be obtained. Therefore, the present resinous composition is very useful as a resinous vehicle for coating composition capable of resulting a coating with excellent durability, weather resistance and corrosion resistance. The invention shall be now more fully explained in the following Examples. Unless otherwise being stated, all parts are by weight. Example 1 20 parts of polysiloxane having formula: 160 parts of Acridic A-801 (Acrylic resin, hydroxyl value 50, non-volatile content 50%, trademark of Dainippon Ink K.K.) and 40 parts of Taipake R-820 (titanium dioxide, trademark of Ishihara Sangyo K.K.) were dispersed well in a ball mil, and the mixture was added with 54 parts of Vernock D-950 (polyisocyanate, trademark of Dainippon Ink K.K.), applied by spraying on an iron plate to a dry film thickness of about 30 µm and cured at room temperature for 1 week. The properties of thus obtained coating were tested and the results were shown in Table 1. Example 2 20 parts of the same polysiloxane as used in Example 1, 133 parts of Acridic A-430-60 (Acrylic resin, non-volatile content 60%, trademark of Dainippon Ink K.K.) 55 parts of Super Beckamin L-127-60 (melamine-formaldehyde resin, trademark of Dainippon Ink K.K.) and 40 parts of Taipake R-820 were used and the same experiments as stated in Example 1 were repeated. In this experiment, the coating was cured at 150°C for 30 minutes. The test results obtained were shown in Table 1. Example 3 20 parts of the same polysiloxane as used in Example 1, 100 parts of methyl isobutyl ketone, and 80 parts of phthalic anhydride were reacted at 140°C for 2 hours and the mixture was added with 30 parts of xylene and allowed to cool. To this mixture, 40 parts of Taipake R-820 were added and the similar coating as in Example 1 was prepared with thus obtained composition. The formed coating was cured at 180°C for 30 minutes and tested as in Example 1. The test results were give in Table 1. Example 4 Into a reaction vessel fitted with a heating device, a stirrer, a reflux condenser and a thermometer, were placed 20 parts of the same polysiloxane as used in Example 1, 1.2 parts of maleic anhydride, 0.04 part of dibutyl tin oxide and 25 parts of xylene and the mixture was heated at 90°C for 1 hour. Next, 35 parts of xylene and 20 parts of methyl isobutyl ketone were added and the combined was heated to 110°C. While maintaining the same temperature, a mixture of 40 parts of methyl methacrylate, 25 parts of 2-ethylhexyl methacrylate, 12 parts of 2-hydroxyethyl methacrylate, 3 parts of methacrylic acid and 1.2 parts of t-butyl peroxy-2-ethylhexanoate was dropwise added in 3 hours. After maintaining the same temperature for 1 hour, a solution of 0.2 part of t-butylperoxy2-ethyl-hexanoate in 20 parts of xylene was dropwise added thereto and the combined mixture was maintained at the same temperature for additional 30 minutes to obtained a resinous solution A. 180 parts of thus obtained resinous solution A and 40 parts of Taipake R-820 were subjected to a ball mill dispersion, added with 54 parts of Vernock D-950 and the resulted composition was applied on an iron plate as in Example 1 and cured. The coating was tested as in Example 1 and the test results were shown in Table 1. Comparative Example 1 200 parts of Acridick A-801 and 40 parts of Taipake R-820 were subjected to a ball mill dispersion and then added with 50 parts of Vernock D-950. The similar coating as stated in Example 1 was prepared, cured at room temperature for 1 week, and tested. The test results are shown in Table 1. Comparative Example 2 A mixture of 536 parts of trimethylol propane, 296 parts of phthalic acid and 138 parts of adipic acid was subjected to a dehydration polycondensation at 200°C to give a polyester resin, which was diluted with Cellosolve acetate to give a polyester solution (non-volatile content of 50% and an acid value of 5). 140 parts of thus obtained polyester solution were added with 30 parts of KR-9218 (Phenylmethylmethoxypolysiloxane manufactured by Shinetsu Kagaku K.K.) and 0.3 part of tetrabutyl titanate and the mixture was heated at 150°C for 2 hours, added with 30 parts of Cellosolve acetate and allowed to cool. Thereafter, the mixture was added with 40 parts of Taipake R-820 and thus obtained composition was applied on an iron plate as in Example 1 and the coating was cured at 180°C for 30 minutes. The coating was tested as in Example 1 and the test results were shown in Table 1. Example Comp.Ex. 1 2 3 4 1 2 Pencil hardness 2H 3H 2H 2H H H rubbing test (xylene) o ○ o ○ o ○ o ○ o ○ o ○ 60° specular reflectance 95 93 92 95 82 92 salt spray resistance o ○ o ○ o ○ o ○ o ○ X accelerated weather resis. gloss retention (%) 90 95 68 90 40 81 The test methods used and evaluation standards are as follows: Pencil hardness: JIS K 5400 Rubbing test: Rubbing tests (50 times back and forth) with xylene were carried out and thereafter the coating surface was evaluated by naked eyes. Evaluation standards were as follows: o ○ normal 60° Specular reflectance: Following the test method of JIS-K5400 6.7 Contact angle toward water: Contact angle of the coating surface toward water was measured in a conventional way. Salt spray resistance: Test coating was sprayed with saline solution for 10 days following the method of JIS-K5400 7.8 and coating conditions were evaluated by naked eyes. o ○ normal X many rusts and blisters Accelerated weather resistance: Test coating was illuminated by using Sunshine Weather-O-meter for 1,000 hours and 60° specular gloss was measured and gloss retention (%) was calculated.

Claims: A resinous coating composition comprising (a) 3 to 70% by weight, based on (a) and (b), of organopolysiloxane represented by the formula: A x R 3-x SiO(R₂SiO) y (RASiO) z SiR 3-x A x in which A is HOCH₂CH₂OCH₂CH₂CH₂-; the groups R are independently an aryl group, a methyl group or an organic group of 2 to 100 carbon atoms having 2 to 100 methylene groups in its main chain which may be interrupted with an ester, an ether or a urethane group and may contain carbon-carbon unsaturation or functional groups other than hydroxyl groups; x is 0 or 1; and y and z each represents a positive number fulfilling the requirements of 1 ≦ y ≦ 20 and 1 ≦ z ≦ 10, having a number average molecular weight of 200 to 100,000 and a hydroxyl value of 20 to 400, (b) 97 to 30% by weight, based on (a) and (b), of a hydroxyl group containing acrylic, alkyd, polyester, epoxy, acryl modified alkyd or acryl modified polyester resin having a hydroxyl value of 20 to 300, and (c) a crosslinking agent which is a polyisocyanate, a melamine-formaldehyde resin or dibasic acid anhydride. A resinous coating composition according to claim 1 wherein the hydroxyl group containing resin (b) is an acrylic resin and all or parts of said (a) and (b) have previously been reacted with each other. A resinous coating composition acording to claim 1 or 2 wherein the substituent R is selected from methyl, propyl and phenyl groups.

Inventors: KANAKURA AKIHIRO, OHSUGI HIROHARU, OKAMURA YOSHIO, TAKARADA MITSUHIRO, UMEMOTO HIROTOSHI, YAMAMOTO KENJI C O SHINETSU CH, KANAKURA, AKIHIRO, OHSUGI, HIROHARU, OKAMURA, YOSHIO, TAKARADA, MITSUHIRO, UMEMOTO, HIROTOSHI, YAMAMOTO, KENJI C/O SHINETSU CHEM. IND. LTD.
Applicants: NIPPON PAINT CO LTD, SHINETSU CHEM IND LTD, NIPPON PAINT CO., LTD., SHINETSU CHEM. IND. LTD.
Application year: 1989
Main classification: C08L83
IPC codes: C08L83, C09D133, C09D201, C09D183