Superconductive electromagnetic wave mixer, and apparatus incorporating same

Abstract: The present invention relates to a superconductive electromagnetic wave mixer comprising a local-oscillator section and a receiving section, said receiving section serving as a section at which an electromagnetic wave from the local-oscillator section and an externally originating electromagnetic wave are combined; wherein said local-oscillator section and said receiving section are formed by at least one Josephson junction employing at least one oxide superconductor, respectively.

Description: BACKGROUND OF THE INVENTION Field of the invention The present invention relates to a heterodyne mixer that employs a superconductor, utilized in detecting electromagnetic waves such as millimetre waves, and an electromagnetic wave mixing apparatus that employs such a mixer. Related Background Art Heterodyne detectors utilized in detecting electromagnetic waves such as millimetre waves have been hitherto constituted of an antenna, a local oscillator such as a Gunn oscillator or a klystron, and a heterodyne mixer device. As the heterodyne mixer devices, heterodyne mixer devices employing Josephson junctions comprising a metal such as Nb are used, which mixer devices have been so constituted as to have an SIS-type laminated structure so that its junctions can have capacitance. In the conventional heterodyne detectors, however, the local oscillator and the Josephson mixer device are separately constituted from each other, and these are connected with each other using a waveguide, resulting in a very large-scale apparatus. In addition, the local oscillator is required to have an output of from 10 nW to 100 nW, also bringing about a great power dissipation. To cope with these problems, an integral-type heterodyne mixer has been devised in which a niobium plane-type weak-link Josephson junction is used at the local oscillator and mixer section (Josephson Triode; DENSHI TSUSHIN GAKKAI RONBUNSHI (Journal of Electron Transmission Society) '86/5, Vol. J69-C, p.639; DENSI JOUHO TSUSHIN GAKKAI-SHI, '87/5 SCE 87-9, P.49). This Josephson triode is of integrated type, and hence can make the apparatus greatly compact. Fig. 11A schematically illustrates a constitution of the above Josephson triode, numeral 1 designates a converter terminal, 2 designates an ocsillator terminal, 3 designates a common ground. Fig. 11B illustrates an equivalent circuit thereof. Among three weak-link Josephson junctions JJ1, JJ2 and JJ3, JJ1 is used as a converter for heterodyne detection, JJ2, as an oscillator for local oscillation, and JJ3, as an isolator for separating JJ1 from JJ2. The device is operated by applying a bias current to JJ2 to cause local oscillation attributable to the AC Josephson effect, and mixing the signals resulting from this local oscillation and an externally originating electromagnetic wave in the JJ1 serving as the converter so that an intermediate frequency signal is obtained. In the above Josephson triode, however, it is necessary to set the characteristics of normal resistance Rn 13 , Rn 12 , Rn 23 , etc. of each Josephson junction each at a proper value. In the conventional Josephson junction of a weak-link type of junction employing a material such as Nb, however, it is difficult to control the characteristics at the time of manufacture. Hence, the above Josephson triode can be manufactured with great difficulty. Moreover, the above conventional apparatus or device employs the material such as Nb, having a low critical temperature Tc (around the liquid helium temperature), so that the device must be made to operate at a low temperature, requiring a very largescale cooling apparatus in which the Joule-Thomson effect is utilized. In addition, the maximum frequency that can be used is as low as about 1 THz, and hence the recent demand of providing a high-frequency band mixer cannot be completely satisfied. SUMMARY OF THE INVENTION On account of the problems involved in the above prior art, an object of the present invention is to make it possible to realise an integrated electromagnetic wave mixer capable of being prepared with a good reproducibility, having a very simple structure, and employing an oxide superconductor. The present invention is defined in the appended claims, and provides a superconductive electromagnetic wave mixer comprising a substrate, a local oscillator section integral with said substrate and including at least a first Josephson junction for generating an electromagnetic wave reference signal, a receiving section also integral with the substrate, including at least a second Josephson junction for receiving an externally originating electromagnetic wave input signal and for mixing the reference signal and the input signal, coupling means arranged to provide electromagnetic coupling between the local oscillator section and the receiving section in which the coupling means includes a stripe or a layer of insulating material or a member of conductive material), disposed inbetween, and in contact with, both the local oscillator section and the receiving section. The Josephson junction may be comprised of a narrowed section of an oxide superconductor polycrystalline thin film. The present invention also provides a superconductive electromagnetic wave mixing apparatus comprising: a superconductive electromagnetic wave mixer as described above in combination with introducing means through which an externally originating electromagnetic wave signal is introduced into the receiving section of the mixer, an amplifier that amplifies the electromagnetic wave signal of an intermediate frequency band, obtained as a result of the mixing the reference signal and the input signal, and a cooler that cools at least the mixer. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1A to 1D, schematically illustrate a process for preparing a superconductive electromagnetic wave mixer according to an embodiment of the present invention; Fig. 1E schematically illustrates an other embodiment of the present invention; Figs. 2A to 2E show an other process corresponding to Figs. 1A to 1D; Figs. 3A and 3B schematically illustrate an another embodiment of the present invention; Figs. 4A to 4D schematically illustrate an other process for preparing a superconductive electromagnetic wave mixer according to an other embodiment of the present invention; Fig. 5 schematically illustrates an other embodiment of the present invention; Figs. 6A to 6C schematically illustrate a superconductive electromagnetic wave mixer according to a further other embodiment of the present invention; Figs. 7A to 7E schematically illustrate a superconductive electromagnetic wave mixer according to an embodiment of the present invention; Fig. 8 schematically illustrates an equivalent circuit of the device shown in Fig. 7C; Fig. 9 schematically illustrates a superconductive electromagnetic wave mixer according to an embodiment of the present invention; Figs. 10A to 10D schematically illustrate a superconductive electromagnetic wave mixer according to an embodiment of the present invention; Figs. 11A and 11B schematically illustrate a prior art Josephson triode; Fig. 12 schematically illustrates an embodiment of a mixing apparatus employing the superconductive electromagnetic wave mixer of the present invention; and Fig. 13 schematically illustrates another embodiment of the mixing apparatus employing the superconductive electromagnetic wave mixer of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The superconductive electromagnetic wave mixer of the present invention will be described below using schematic illustrations of its structure. In the first embodiment of the superconductive electromagnetic wave mixer of the present invention, a plurality of Josephson junction regions comprised of crystal grain boundaries of an oxide superconductor thin film are coupled interposing an insulating layer between them. In its operation, a bias voltage is applied to a Josephson junction region used as the local-oscillator section among the above plurality of Josephson junction regions so that a local oscillator signal is generated. This local-oscillator signal and the externally originating electromagnetic wave are combined (or undergo mixing) at the Josephson junction region used as the receiving section among the above plurality of Josephson junction regions, and the intermediate frequency signal is thus taken out. Description will be specifically made with reference to the drawings. The first embodiment of the superconductive electromagnetic wave mixer of the present invention is roughly grouped into a plane type as shown in Figs. 1C and 1D, a laminate type as shown in Figs. 2D and 2E, and also a multiple type as shown in Figs. 3A and 3B. Firstly, Figs. 1C (a plan view) and 1D (a cross-section along the line a-a' in Fig. 1C) illustrate a plane-type superconductive electromagnetic wave mixer, in which on the substrate 4 two Josephson junction regions 6 and 7 comprised of crystal grain boundaries of the oxide superconductor thin film 5, which regions serve as the local-oscillator section and the receiving section, respectively, and in which these local-oscillator section and receiving section are laterally arranged interposing the insulating material 8 between them. This plane type superconductive electromagnetic wave mixer can be prepared by a method comprising depositing one layer of the oxide superconductor thin film 5 of a polycrystalline material on the substrate 4, followed by patterning using a technique such as photolithography or ion implantation, and then bringing the two Josephson junction regions 6 and 7 into a very close plane arrangement interposing the insulating material 8 between them. Secondly, Figs. 2D (a plan view) and 2E (a cross-section along the line b-b' in Fig. 2D) illustrate a laminate type superconductive electromagnetic wave mixer, in which on the substrate 4 two Josephson junction regions 6 and 7 comprised of crystal grain boundaries of the lower and upper films 5a and 5b, are laminated interposing the insulating material 8 between them, and the regions 6 and 7 serve as the local-oscillator section and the receiving section, respectively. This laminate type superconductive electromagnetic wave mixer can be prepared by a method comprising depositing on the substrate 4 the lower film 5a, the insulating material 8 and the upper film 5b in this order, followed by patterning using a technique such as photolithography, thus, the two Josephson junction regions 6 and 7 can be arranged close to each other with the insulating material 8 interposed between them. Thirdly, Figs. 3A (a plan view) and 3B (a cross section along the line c-c' in Fig. 3A) illustrate a multiple type superconductive electromagnetic wave mixer, in which on the substrate 4 the lower and upper films 5a and 5b are laminated interposing the insulating material 8 between them, and the Josephson junction regions 6, 9 and 11 serving as local-oscillator sections and Josephson junction regions 7, 10 and 12 serving as receiving section are formed interposing the insulating material 8, and further the electrodes 13, 14 and 15, 16 are formed. The multiple type mixer specifically refers to a superconductive electromagnetic wave mixer of the type in which the respective local-oscillator sections and receiving sections are contained in a plural number. This multiple type superconductive electromagnetic wave mixer can be prepared by the same method as the method of preparing the above laminate type superconductive electromagnetic wave mixer, except that a larger number of Josephson junctions are formed by patterning. Though not shown in the drawings, it is also possible in the plane type superconductive electromagnetic wave mixer previously described to respectively form the local-oscillator section and receiving section into multiplicity. Needless to say, such a plane type multiple superconductive electromagnetic wave mixer is also embraced in the first embodiment of the present invention. In the above embodiment, the Josephson junction region comprised of crystal grain boundaries of an oxide superconductor thin film is used. Any preparation method, material and form may be employed so long as the polycrystalline thin film of an oxide superconductor is used. The insulating material through which the two Josephson junction regions are coupled together may be made of any materials, by any method and in any form, including insulating thin films comprising MgO, YSZ (yttrium stabilized zirconia) or a polymer of an organic substance, those obtained by making an oxide superconductor into an insulating material by means of ion implantation or the like. In a second embodiment of the superconductive electromagnetic wave mixer of the present invention, a plurality of Josephson junction regions comprised of crystal grain boundaries of an oxide superconductor thin film are coupled through a conductive material between them. Its operation is the same as in the above first embodiment. Description will be specifically made with reference to the drawings. The second embodiment of the superconductive electromagnetic wave mixer of the present invention is roughly grouped into a plane type as shown in Figs. 4C and 4D, and a multiple type as shown in Fig. 5. Firstly, Figs. 4C and 4D (4D: a plan view of Fig. 4C) illustrate a plane type superconductive electromagnetic wave mixer, in which on the substrate 4 two Josephson junction regions 6 and 7 of a plane-type or quasi-plane-type comprised of crystal grain boundaries of the oxide superconductor thin film 5, one region of which serves as the local-oscillator section and also the other region of which serves as the receiving section, are provided, and the above two Josephson junction regions 6 and 7 are coupled using the conductive material 17. The superconductive electromagnetic wave mixer according to the present embodiment can be prepared, for example, in the following manner: First, on the substrate 4 made of MgO or the like, the superconductive thin film 5 is formed (Fig. 4A). Next, patterning is carried out by photolithography or the like to form two Josephson junction regions 6 and 7 (Fig. 4B). Then, the conductive material 17 taking the form of extending over the two Josephson junction regions is formed (Fig. 4C). Secondly, Fig. 5 illustrates a multiple type super-conductive electromagnetic wave mixer, in which on the substrate 4 the oxide-superconductor thin film 5, which is subjected to patterning to form Josephson junction regions 6a, 6b and 6c serving as local-oscillator sections and Josephson junction regions 7a, 7b and 7c serving as receiving sections, are provided and the local-oscillator sections and the receiving sections being coupled through the conductive material 17, and electrodes 13, 14 and 15, 16 being further formed. This multiple type superconductive electromagnetic wave mixer can be prepared by the same method as the method of preparing the above plane type (or quasi-plane type) superconductive electromagnetic wave mixer, except that a larger number of Josephson junctions are formed by patterning. In the above embodiment, the Josephson junction region comprised of crystal grain boundaries of an oxide superconductor thin film is used. Any preparation method, material and form may be employed so long as the polycrystalline thin film of an oxide superconductor is used. The conductive material through which the local-oscillator sections and receiving sections are coupled together may be made by any method and of any materials so long as it is a conductive material such as a metal, a semiconductor, or a superconductor. The third embodiment of the superconductive electromagnetic wave mixer of the present invention, comprises a local-oscillator section and a receiving section constituted of a tunneling Josephson junction using an oxide superconductor thin film, respectively, and said local-oscillator section and receiving section being coupled by any of Josephson junction, capacitance, resistance and inductance formed of a conductive material or insulating material. Figs. 6A to 6C schematically illustrate an example of the structure of the superconductive electromagnetic wave mixer according to the present embodiment, and a preparation method therefor. First, on the substrate 4 made of, for example, MgO, the lower film 5a is formed, the insulating material layer 8' is formed thereon, and the upper film 5b is further formed thereon (Fig. 6A). Next, patterning is carried out by photolithography or the like to form a groove 18 (Fig. 6B). Here, superconductive properties change at the bottom (coupling part 19) of the groove as a result of processing as exemplified by ion milling, and the desired characteristics of any of the insulating material and the conductive material can be obtained. The conductive material herein mentioned includes even semiconductors and superconductors. This utilizes the property that the characteristics of oxide superconductors are very sensitively governed by compositional ratios. A pair of tunneling Josephson junction regions having Josephson current values suited to the local-oscillator section and receiving section can also be formed by changing right and left extent of the groove 18. Here, the groove 18 need not be physically cut so long as the groove is capable of changing the degree of the coupling of the right and left Josephson junction regions, and may be formed by an ion implant 22 or the like as shown in Fig. 6C. In the device as shown in Figs. 6A to 6C, a bias current is applied to the left-side Josephson junction region 20 to generate a local-oscillator signal, and the signal is introduced into the right-side Josephson junction region 21, where the mixing with the electromagnetic wave irradiated from the outside is carried out to achieve heterodyne detection. In Figs. 6A to 6C an example is shown in which the device is processed after lamination, but the preparation method is not limited to this. In the respective embodiments, in order for the device to operate as an electromagnetic wave mixer, the relationship I 1 > I 2 > I 3 is required to be established between the value I 1 for the Josephson current flowing through the Josephson junction region that forms the local-oscillator section, the value I 2 for the Josephson current flowing through the Josephson junction region that forms the receiving section, and the value I 3 for the isolator current that may flow between the above local-oscillator section and receiving section. For the achievement of the imbalance between these current values, it is possible to use, in the first embodiment, a method in which, for example, the widths of the Josephson junction regions 6 and 7 as shown in Fig. 1C are made different (the width of the local-oscillator section > the width of the receiving section), or the film 26 such as an MgO thin film, a ZrO 2 thin film or an Ag thin film is deposited only beneath the receiving section so that the superconductivity may be changed at its upper part (see Fig. 1E). This method is preferred because the respective Josephson current values can be readily controlled only by variously selecting the materials or changing conditions for film formation. A similar method is possible also in the second embodiment. In the third embodiment, it is possible to use a method in which, for example, the Josephson junction regions 20 and 21 as shown in Figs. 6B and 6C are coupled to give a junction unbalanced in its extent. Materials that can be used for the above film 26 include, for example, the following: Ag, Au, Nb, NbN, Pb, Pb-Bi, MgO, ZrO 2 , SiO x , a-Si, and other oxides. In the case that Josephson current may be increased by the above methods for controlling Josephson current, the Josephson junction serves as the local oscillation section, while in the case that Josephson current may be decreased by the above methods, the Josephson junction serves as the receiving section. The superconductor that constitutes the oxide superconductor thin film in the respective embodiments described above, when represented by the formula A-B-C-D, it is desirable that A is at least one element selected from the group consisting of La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Sc, Y, and Bi; B is at least one element selected from the group consisting of Ca, Sr, Ba, and Pb; C is at least one element selected from the group consisting of V, Ti, Cr, Mn, Fe, Ni, Co, Ag, Cd, Cu, Zn, Hg, and Ru; and D is O. More specifically, it includes; (1) 214 type: (La 1-x M x ) 2 CuO 4-δ (M = Na, Ca, Sr, Ba) (Ln, Sr, Ce) 2 CuO 4-δ (Ln = a lanthanide such as Nd) (Ln, Ce) 2 CuO 4-δ (Ln = a lanthanide such as Pr or Nd) (2) 123 type: Ln(Ba 2 Cu 3 O 7-δ (Ln = any sort of lanthanide), and those wherein Ln has been substituted with any sort of element) (3) Bi base: Bi 2 Sr 2 CuO y , Bi 2 Sr 2-x Ln x CuO y , Bi 2 Sr 2 CaCu 2 O y , Bi 2 Sr 3-x Ln x Cu 2 O y , Bi 2-x Pb x Sr 2 Ca 2 Cu 3 O y , Bi 2 Sr(LnCe) 2 Cu 2 O y . (In the above, Ln = any sort of lanthanide), (4) Tl base: Tl 2 Ba 2 Ca n Cu 1+n O y (n = 0, 1, 2, 3 .....), TlBa 2 Ca n Cu 1+n O y (n = 0, 1, 2, 3 .....). (5) Pb base: Pb 2 Sr 2 Ca 1-x Ln x Cu 3 O y (x = about 0.5) (6) 223 type: (LnBa) 2 (LnCe) 2 Cu 3 O y (Ln: a lanthanide). Use of materials having a critical temperature of not less than 77 K as exemplified by Y-Ba-Cu-O-based, Bi-Sr-Ca-Cu-O-based or Tl-Ba-Ca-Cu-O-based superconductors may also make it possible to use inexpensive liquid nitrogen as a refrigerant. When the mixer is continuously driven, it is possible to use a compact and inexpensive cryostat having no Joule-Thomson valve, thus bringing about an effective Josephson triode as the mixer of an integral type. When the materials of the above types are used, the energy gap 2Δ is several 10 meV, which is larger by one figure than that of niobium. This means that the maximum frequency that can be used in a mixer extends up to about 10 THz, which is higher by one figure than that of niobium (about 1 THz). The superconductive materials constituting the local-oscillator section and the receiving section may be composed of plural materials, respectively. A mixing apparatus employing the superconductive electromagnetic wave mixer having been described above will be described below. A superconductive electromagnetic wave mixing apparatus embodying the present invention will be detailed below with reference to the drawings. First, as Fig. 12 shows, the above superconductive electromagnetic wave mixer, designated as 30, is installed in the cooler 31, such as cryostat and the externally originating electromagnetic wave 32 is introduced into the superconductive electromagnetic wave mixer 30 by the introducing means 33 for the externally originating electromagnetic wave 32, comprising a waveguide, a horn type antenna, etc. A bias current is also fed from the direct-current electric source 34 outside the cooler to the local-oscillator section of the superconductive electromagnetic wave mixer 30 to cause oscillation with a desired frequency. The externally originating electromagnetic wave 32 and the local-oscillator wave are combined (or caused to undergo mixing) to give the electromagnetic wave 35 of an intermediate frequency band (IF). This IF wave 35 is amplified using an amplifier 36, so that the output 37 after heterodyne mixing can be obtained. In Fig. 12, the introducing means 33 and the amplifier 36 are provided inside the cooler 31, but, without limitation thereto, at least the superconductive electromagnetic wave mixer 30 may be cooled in the cooler 31. In the superconductive electromagnetic wave mixing apparatus of the present invention, a preferred embodiment is the embodiment as shown in Fig. 13, in which the waveguide 38 is used as the introducing means and the superconductive electromagnetic wave mixer 30 is provided inside the waveguide 38. This embodiment, in which the superconductive electromagnetic wave mixer having a localoscillator section inside the waveguide is provided, enables generation of local-oscillator waves within the same closed space as that for the introducing means for the externally originating electromagnetic wave, so that the mixing efficiency increases, in other words, the efficiency of the propagation of electromagnetic waves to the receiving section increased. It is also to be noted that the power of local-oscillator outputs can be decreased, which is accompanied with a decrease in the inflow of heat due to Joule heating, so that not only the device itself can be made compact, but also the whole apparatus including the cooler can be made to operate with a low power dissipation and made compact. The superconductive electromagnetic wave mixer of the present invention is equipped with both the local-oscillator section and the heterodyne mixer section in the same device, compared with the prior art heterodyne detectors as previously discussed. Thus, it is unnecessary to provide the external local oscillator and a waveguide used for making connection thereto, and also it is possible to make the mixing apparatus very compact. In addition, the use of the external local oscillator has ever required a local-oscillator output of from 10 nW to 100 nW, but the devices embodying the present invention require only from 0.1 nW to 1 nW, resulting in greatly decreased power dissipation. It is further possible to prepare an electromagnetic wave mixer that can operate at a relatively high temperature (around liquid nitrogen temperature), using an oxide superconductor having a relatively high critical temperature Tc. Thus, it is possible to construct a compact and inexpensive system with a simplified cooling unit. Moreover, the mixers described may be used for high frequency bands if, as is preferred, they employ an oxide superconductor having a larger band gap than that of Nb or the like (the energy gap of Nb is about 3 meV, but that of the oxide superconductor as exemplified by a Y-based superconductor is larger than it by one figure). More specifically, a possible frequency limit is found to be about 700 GHz in the case of Nb, and about 10 THz in the case of Y-based superconductors. This further means that the information transmission speed is 10 times and the band width is also 10 times, namely, the information that can be transmitted in the same time increases by nearly two figures. It has also become possible to successfully couple the local-oscillator section and the receiving section by virtue of the oxide superconductor having the property that the electrical characteristics may greatly change depending on the compositional changes. It has further become easy to obtain the desired Josephson current values because of the junction made to comprise the tunneling Josephson junction. The foregoing has made it possible to prepare a Josephson triode with a good yield. It is preferred to couple the local-oscillator section and receiving section of the mixer through an insulating material or a conductive material, rather than to form a gap between them. More specifically, it is found that, also when they are coupled through an insulating material, the dielectric constant of the insulating material is larger than ε O of vacuum by about one figure, the electric capacity held between the local-oscillator section and receiving section is also larger than the case when the gap is formed between them, and thus the coupling between the two sections is considered to have become stronger, bringing about an increase in the mixing efficiency (i.e., the efficiency of the propagation of electromagnetic waves from the local-oscillator section). A still stronger coupling results when the insulating material is replaced with a conductive material, and a greater improvement is seen in the mixing efficiency. A Josephson junction of a grain boundary type is of weak-link type, which is more preferable than a tunneling Josephson junction with respect to the maximum frequency used and mixing efficiency. This is also preferable in the sense of making the most of the advantage resulting from the employment of a high-temperature oxide superconductor that can be applied to high-frequency bands, as previously mentioned. The Josephson junction region that constitutes the local-oscillator section may be made plural in number, whereby the voltage to be applied to the local-oscillator section can be made larger and thus the local-oscillator frequency can be made more stable. The Josephson junction region that constitutes the receiving section may also be made plural in number, whereby the detection efficiency can be improved. EXAMPLES The present invention will be described below in greater detail by giving Examples. Example 1 Figs. 2A to 2D schematically illustrate the structure of, and preparation steps for, a superconductive electromagnetic wave mixer according to an embodiment of the present invention. In the steps as shown in Figs. 2A to 2B, the lower film 5a of Y 1 Ba 2 Cu 3 O 7-x (x = 0 to 0.5) was formed on the substrate 4 by the cluster ion beam method (Fig. 2A). An SrTiO 3 monocrystalline substrate was used as the substrate 4. This film formation was carried out under conditions as follows: Y, BaO and Cu were used as evaporation sources, the acceleration voltage and ionization current therefor were 1 kV and 300 mA, respectively, for each element, the substrate temperature was set to 500°C, and oxygen gas was introduced at 1 x 10 -3 Torr at the time of deposition. The lower film 5a was comprised of a polycrystalline film with a film thickness of 0.1 µm, having crystal grains with a size of about 1 µm, and its resistance turned zero at a temperature of not more than 83 K. Next, an MgO thin film was formed by deposition by RF sputtering method to form the insulating material 8 (Fig. 2B). This film formation was made under conditions as follows: Using an MgO target, in a sputtering gas of Ar:O 2 = 1:1 under 1.33Pa (1 x 10 -2 Torr), the substrate temperature was set to 200°C, and the sputtering power, to 200 W. The resulting layer had a film thickness of 0.08 µm. Subsequently, the upper film 5b was formed in the same manner as the lower film 5a (Fig. 2C). This upper film 5b showed zero resistance at a temperature of not more than 81 K. Patterning was further carried out by photolithography to form two Josephson junction regions 6 and 7 in a laminate form (Figs. 2D and 2E). The two Josephson junction regions 6 and 7 were each 2 µm in width and 3 µm in length. The superconductive electromagnetic wave mixer thus prepared was cooled to 40 K by means of a simple cooling unit, and then a bias current was applied to the Josephson junction region 7 from a DC electric source to make it the local-oscillator section, and an electromagnetic wave was irradiated on the Josephson junction 6 serving as the receiving section. As a result, the device satisfactorily operated as a mixer of electromagnetic waves in a frequency region of from 100 GHz to 1 THz. In the present Example, devices obtained by replacing Y in the superconductive thin film material Y 1 Ba 2 Cu 3 O 7-x (x = 0 to 0.5) with a lanthanoid such as Ho, Er, Yb, Eu or La also operated similarly. Example 2 Figs. 1A to 1E illustrate preparation steps for a superconductive electromagnetic wave mixer according to an embodiment of the present invention. In the superconductive electromagnetic wave mixer shown in these Figs. 1A to 1D, ion implantation by FIB was carried out for a superconductive thin film to make an insulating material. First, on the substrate 4, the superconductive thin film 5 was formed (Fig. 1A). An MgO monocrystalline substrate was used as the substrate 4. As the superconductive thin film 5 used, a film, which was formed by RF magnetron sputtering, using a Bi 2 Sr 2 Ca 2 Cu 3 O 10 target under conditions of an Ar pressure of 1.33Pa (1 x 10 -2 Torr), an RF power of 200 W and a substrate temperature of 100°C, and heating at 860°C in the atmosphere after the film formation, was used. This superconductive thin film 5 was comprised of a polycrystalline film with a film thickness of 0.2 µm, having crystal grains with a size of from 2 to 3 µm, and exhibited superconductivity at a temperature of not more than 95 K. Next, patterning was carried out by photolithography to form a narrow region 5' in the superconductive thin film 5 (Fig. 1B). This narrow region 5' was made to have a dimension of 5 µm in length and 8 µm in width. Subsequently, along the centre line of this narrow portion, 5' Ar ions were further implanted by FIB in a width of 0.5 µm to form the insulating material 8. Thus, the narrow region 5' was divided into two parts to form the Josephson junction regions 6 and 7 in a very close arrangement, and at the same time the superconductive thin film 5 was divided into two parts (Fig. 1C). The superconductive electromagnetic wave mixer thus prepared operated like that in Example 1. In the present Example, devices obtained by changing the superconductive thin film material to Bi 2-x Pb x Sr 2 Ca 2 Cu 3 O 10 or replacing Bi thereof with lead also operated similarly. Example 3 Fig. 5 schematically illustrates the structure of a superconductive electromagnetic wave mixer according to an embodiment of the present invention. The superconductive electromagnetic wave mixer shown in Fig. 5 was prepared according to the following steps. First, using an MgO monocrystalline substrate as the substrate 4, the oxide superconductor thin film 5 was formed thereon. The oxide superconductor thin film 5 was formed by RF magnetron sputtering, using a Bi 2 Sr 2 Ca 2 Cu 3 O 10 target under conditions of a sputtering power of 150 W, a sputtering gas of Ar, gas pressure of 0.27Pa (2 x 10 -3 Torr) and a substrate temperature of 100°C to give a film thickness of 0.25 µm, followed by heating at 860°C in an atmosphere of 30 % O 2 and 70 % N 2 . This thin film 5 turned to a polycrystalline film having crystal grains with a size of about 2 µm, and exhibited superconductivity at a temperature of not more than 95 K. On this oxide superconductor thin film 5, patterning was carried out by photolithography to form Josephson junction regions 6a, 6b and 6c serving as the local-oscillator sections and Josephson junction regions 7a, 7b and 7c serving as the receiving sections, all of which were made to be 4 µm in both width and length. Next, Cr and Au were deposited by resistance heating to give films of 0.01 µm and 0.05 µm, respectively, in thickness, thus forming the conductive material 17 and the electrodes 13, 14 and 15, 16. The superconductive electromagnetic wave mixer thus prepared was cooled to 40 K using a simple cooling unit. As a result, it satisfactorily operated as a mixer of electromagnetic waves in a frequency region of from 100 GHz to 1 THz. The voltage necessary for applying a bias current to the local-oscillator section was larger than that in Example 2 by three or four times, so a stable operation could be achieved. In the present Example, devices obtained by changing the superconductive thin film material to Tl 2 Ba 2 Ca n Cu 1+n O y (n = 1, 2 or 3) or TlBa 2 Ca n Cu 1+n O y (n = 1, 2 or 3) also operated similarly. Example 4 Figs. 3A and 3B schematically illustrate the structure of a superconductive electromagnetic wave mixer according to another embodiment of the present invention. The superconductive electromagnetic wave mixer as shown in Figs.3A and 3B comprises the local-oscillator section and receiving section which are coupled across an insulating material so as to form capacitance. Fig. 3A is a plan view thereof, and Fig. 3B is a cross section along the line c-c' in Fig. 3A. This superconductive electromagnetic wave mixer was prepared by the steps as follows: First, using an SrTiO 3 monocrystalline substrate as the substrate 4, the lower film 5a was formed thereon. This lower film 5a was formed using the cluster ion beam method, and using Y, BaO and Cu as deposition sources to deposit them on the substrate so as to be Y:Ba:Cu = 1:2:1.5. The acceleration voltage and ionization current therefor were 1 kV and 300 mA, respectively, for each element, and the deposition was carried out by introducing oxygen gas of 0.13Pa (1 x 10 -3 Torr) and setting the substrate temperature to 500°C. The lower film 5a was comprised of a polycrystalline film with a film thickness of 0.1 µm, having crystal grains with a size of about 1 µm, and exhibited superconductivity at a temperature of not more than 83 K. Next, an MgO thin film was formed by deposition by RF sputtering to form the insulating material 8. This film formation was made under conditions as follows: Using an MgO target, in a sputtering gas of Ar:O 2 = 1:1 under 1.33Pa (1 x 10 -2 Torr), the substrate temperature was set to 200°C, and the sputtering power, to 200 W. The resulting layer had a film thickness of 0.08 µm. Subsequently, the upper film 5b was formed in the same manner as the lower film 5a. This upper film 5b exhibited superconductivity at a temperature of not more than 81 K. These lower and upper films 5a and 5b were further subjected to patterning by photolithography to form Josephson junction regions 6, 9 and 11 serving as the local-oscillator sections and Josephson junction regions 7, 10 and 12 serving as the receiving sections in a laminate form. Thereafter, Cr and Au were deposited by resistance heating in a laminate form to give films of 0.01 µm and 0.05 µm, respectively, in thickness, thus forming the electrodes 13, 14 and 15, 16. The superconductive electromagnetic wave mixer thus prepared satisfactorily operated like that in Example 3. In the present Example, a device obtained by changing the superconductive thin film material to Nd 1.85 Ce 0.15 CuO y also similarly operated. This material, however, had a Tc of about 25 K, and hence was used by cooling it to 20 K. Also in the case that the lower and upper films 5a and 5b were constituted by different materials, the mixer operated similarly. Example 5 In the steps as shown in Fig. 4, an MgO monocrystalline substrate was used as the substrate 4, and the superconductive thin film 5 of Bi 2 Sr 2 Ca 2 Cu 3 O x was formed on the substrate 4 by RF magnetron sputtering. This film formation was carried out under conditions as follows: In an atmosphere of Ar:O 2 = 1:1 and a pressure of 0.93Pa (7 x 10 -3 Torr), using a Bi 2 Sr 2 Ca 2 Cu 3 O x sinter as a target, the film was formed at a sputtering power of 100 W and a substrate temperature of 200°C and the film thus formed was then heated at 850°C for 1 hour in an oxidizing atmosphere. The film had a thickness of 0.8 µm. This thin film was comprised of a polycrystalline thin film having crystal grains with a size of from 2 to 3 µm (Fig. 4A). Next, patterning was carried out by photolithography to form two Josephson junction regions 6 and 7 in a close arrangement. The junction regions each had a dimension of 8 µm in length and 4 µm in width, and the space between the two Josephson junction regions was 1 µm (Fig. 4B). Next, Ag was vacuum-deposited thereon by resistance heating to form a film of 0.5 µm thick, followed by patterning by photolithography to form the conductive material 17 (Fig. 4C). Here, the Josephson junction is comprised utilizing crystal grain boundaries (Fig. 4D). The electromagnetic wave mixer thus prepared satisfactorily operated as a heterodyne mixer of electromagnetic waves in a frequency region of from 100 GHz to 1 THz. In the present Example, a device obtained by changing the superconductive thin film material to Pb 2 Sr 2 Ca 0.5 Y 0.5 Cu 3 O y also similarly operated. Example 6 Here will be described an instance in which, in the embodiment shown in Fig. 4, SrTiO 3 was used as the substrate, a YBaCuO-based material was used as a superconductive material, and cluster ion beam deposition was used as a method of forming a superconductive thin film. First, on the substrate 4, the superconductive thin film 5 of Y 1 Ba 2 Cu 3 O 7-x (x = 0.1 to 0.4) was formed by cluster ion beam deposition. This film was formed under conditions as follows: using Y, BaO and Cu as evaporation sources, the acceleration voltage and ionization current therefor were 2 kV and 100 mA, respectively, for Y, 4 kV and 200 mA for BaO, and 4 kV and 200 mA for Cu. The substrate temperature was set to 600°C, and O 2 gas of 1.73Pa (1.3 x 10 -2 Torr) was introduced at the time of deposition. The resulting film had a thickness of 0.5 µm. This thin film was comprised of a polycrystalline thin film having crystal grains with a size of about 2 µm, and exhibited superconductivity without heat treatment (Fig. 4A). Patterning was carried out thereon in the same manner as in Example 5 to form two Josephson junction regions 6 and 7 (Fig. 4B). The conductive material 17 was further formed in the same manner (Fig. 4C). The electromagnetic wave mixer thus prepared satisfactorily operated like that in Example 5. Example 7 Figs. 10A to 10D illustrate another embodiment. This utilizes a level difference formed on the substrate, for the formation of the Josephson junction. First, a level difference of 0.5 µm was formed by photolithography on the substrate 4 of an MgO monocrystalline (Fig. 10A). Next, on the substrate 4 on which the level difference was made, the superconductive thin film 5 of Er 1 Ba 2 Cu 3 O 7-x (x = 0.1 to 0.4) was formed by RF magnetron sputtering. The film was formed under conditions as follows: In an atmosphere of an Ar gas pressure 0.93Pa (7 x 10 -3 Torr), using a Er 1 Ba 2 Cu 3 O 7-x (x = 0.1 to 0.4) sinter as a target, the film was formed at a sputtering power of 150 W and a substrate temperature set to 100°C and the film thus formed was then heated at 900°C for 1 hour in an oxidizing atmosphere. The film had a thickness of 0.5 µm. This thin film was comprised of a polycrystalline thin film having crystal grains with a size of from 4 to 6 µm (Fig. 10B). Next, patterning was carried out in the same manner as in Example 5 to form two Josephson junction regions 6 and 7. However, the junction regions were each made to be 16 µm in length and 8 µm in width (Fig. 10C). The conductive material 17 was further formed in the same manner as in Example 5 (Fig. 10D). The electromagnetic wave mixer thus prepared satisfactorily operated like that in Example 5. Example 8 In the steps as shown in Fig. 6, an MgO monocrystalline substrate was used as the substrate 4, and the lower film 5a of Bi 2 Sr 2 Ca 2 Cu 3 O x was formed on the substrate 4 by ion beam sputtering. This film formation was carried out, using a Bi 2 Sr 2 Ca 2 Cu 3 O sinter as a target, under conditions of a background pressure of 2.66 x 10 -3 Pa (2 x 10 -5 Torr), an Ar pressure of 0.4Pa (3 x 10 -3 Torr),an ion current of 100 µA, an acceleration voltage of 7kV, and a substrate temperature of 600°C. The resulting film had a thickness of 0.05 µm. Next, the insulating material layer 8' of MgO was formed by RF sputtering, using an MgO target, under conditions of an Ar pressure of 0.92Pa (7 x 10 -3 Torr), a sputtering power of 100 W, and a substrate temperature of 150°C. Further thereon, the upper film 5b of Bi 2 Sr 2 Ca 2 Cu 3 O was formed under the above conditions (Fig. 6A). Next, patterning was carried out by photolithography to form Josephson junction regions 20 and 21 as shown in Fig. 6B. Junction areas were 10 µm x 8 µm for the Josephson junction region 20 and 5 µm x 8µm for the Josephson junction region 21. The groove 18 was 1 µm in width, and the film thickness at the coupling part 19 was 0.015 µm. At this time, current-voltage characteristics between the lower film 5a of the Josephson junction regions 20 and the lower film 5a of the the Josephson junction 21 were measured at the liquid nitrogen temperature to reveal that the characteristics of a microbridge Josephson junction were exhibited. In other words, the coupling part 19 was made up of a weak-link Josephson junction. The Josephson current was found to be 80 µA. The electromagnetic wave mixer thus prepared was set in a waveguide under liquid nitrogen cooling and evaluated. As a result, it satisfactorily operated as a heterodyne mixer of electromagnetic waves in a frequency region of from 100 GHz to 800 GHz. Example 9 Here will be described an instance in which, in the steps shown in Fig. 6, SrTiO 3 was used as the substrate 4, a YBaCuO-based material was used as the superconductive material, and the cluster ion beam deposition method was used for forming the superconductive thin film. First, on the substrate 4, the lower film 5a of YBa 2 Cu 3 O 7-x (x = 0.1 to 0.4) was formed by cluster ion beam deposition. This film was formed under conditions as follows: Using Y, BaO and Cu as evaporation sources, the acceleration voltage and ionization current therefor were 3 kV and 100 mA, respectively, for Y, 5 kV and 200 mA for BaO, and 5 kV and 200 mA for Cu. The substrate temperature was set to 700°C, and O 2 gas of 0.66Pa ) 5 x 10 -3 Torr) was introduced at the time of deposition. The resulting thin film was 0.06 µm thick. Next, Ag was deposited with a thickness of 0.002 µm by resistance heating, and ZrO 2 was formed thereon with a thickness of 0.001 µm by RF sputtering. At this time, YSZ was used as a target, the Ar pressure was 0.93Pa (7 x 10 -3 Torr), the sputtering power was 100 W, and the substrate temperature was 100°C. The upper film 5b of YBaCuO of 0.08 µm thick was further formed thereon by the above cluster ion beam deposition at a substrate temperature set to 550°C (Fig. 6A). Next, the Josephson junction regions 20 and 21 were formed by photolithography and cluster ion implantation (Fig. 6C). The ion implantation was carried out using Ar ions (5 keV). Junction areas were 12 µm x 10 µm for the Josephson junction region 20 and 6 µm x 10 µm for the Josephson junction region 21. The part at which the ions were implanted was 0.8 µm in width. The electric characteristics at the coupling part 19 were measured in the same manner as in Example 8, and were found to be semiconductive. The resistivity at the liquid nitrogen temperature was about 10 3 Ω·cm. The electromagnetic wave mixer thus prepared satisfactorily operated at the liquid nitrogen temperature, like that in Example 8. Example 10 Figs. 7A to 7D illustrate an electromagnetic wave mixer of Example 10. First, by the same process as in Example 9, the lower film 5a composed of a Y-based thin film of 0.06 µm thick and Ag of 0.002 µm thick and the insulating material layer 8′ composed of ZrO 2 of 0.001 µm thick in this order was formed on the substrate 4, and patterning was carried out by photolithography (Fig. 7A). Next, the upper film 5b of Y-based thin film was formed thereon with a thickness of 0.06 µm, and patterning was carried out by photolithography to form a series array of tunneling Josephson junctions (Fig. 7B). Subsequently, using an excimer laser, the left-end junction was etched to form the groove 18 (Fig. 7C). Figs. 7D and 7E show cross sections along the lines a-a' and b-b', respectively, in Fig. 7C. The groove 18 shown in Fig. 7C had a width of 0.5 µm. The electric characteristics at the coupling part 19 were measured in the same manner as in Example 8 to reveal that the resistivity was 10 6 Ω·cm or more and the electric capacitance was about 1 nF. Fig. 8 shows an equivalent circuit of this device. Namely, both the local-oscillator section 23 and the receiving section 24 are set in 10 series arrays. This constitution makes it possible to make 10 times larger the operation voltage applied when the bias current is flowed to the local-oscillator section, and also makes 10 times larger the voltage at the receiving section. This can improve the stability and noise resistance required when the device is actually operated. The electromagnetic wave mixer thus prepared satisfactorily operated as a heterodyne mixer of electromagnetic waves in a region of from 100 GHz to 800 GHz at the liquid nitrogen temperature. Example 11 The procedure of Example 2 was repeated to form two Josephson junction regions, one of which was made to have a width of 2 µm, the other of which a width of 5 µm, respectively, and both of which a length of 5 µm in common. Here, the Josephson current was 11 mA at the 2 µm wide Josephson junction region, which was used as the receiving section, and the Josephson current was 23 mA at the 5 µm wide Josephson junction region, which was used as the local-oscillator section. As a result, the device satisfactorily operated like that in Example 2, but it was possible to take out the power of electromagnetic waves of intermediate frequencies at a higher level than that in Example 2. Example 12 Fig. 9 schematically illustrates the structure of a superconductive electromagnetic wave mixer according to Example 12. The superconductive electromagnetic wave mixer shown in Fig. 9 was prepared according to the following steps. First, an MgO monocrystalline substrate was used as the substrate 4. The thin film 26 of ZrO 2 was formed only half on the substrate with a thickness of only 0.002 µm. The film was formed by RF magnetron sputtering, using YSZ as a target, in a sputtering gas of Ar:O 2 = 1:1 and a pressure of 1.3Pa (1 x 10 -2 Torr), at a substrate temperature of 200°C, and a power of 100 W. Thereafter, the procedure of Example 3 was repeated to form the local-oscillator section (7a, 7b and 7c) and the receiving section (6a, 6b and 6c). Here, the Josephson current at the local-oscillator section (7a, 7b and 7c) was 3.5 mA, and the Josephson current at the receiving section (6a, 6b and 6c) was 0.7 mA. The superconductive electromagnetic wave mixer thus prepared satisfactorily operated like that in Example 3, but it was possible to take out the power of electromagnetic waves of intermediate frequencies at a higher level than that in Example 3. Example 13 Fig. 13 illustrates the constitution of a mixing apparatus according to Example 13. A superconductive electromagnetic wave mixer prepared by the method previously described in Example 1 was installed inside the rectangular waveguide 38 of 1 mm x 0.5 mm in inner size. This waveguide 38 was fixed on the cold head 31' of the cryostat 31 using a circulating helium gas and cooled to 15 K. Here, the waveguide 38 is partitioned with the Teflon sheet 39 of a 0.2 mm thick at the joining part thereof with the cryostat 31, so that the inside of the cryostat is kept vacuum. Under this constitution, using the direct current electric source 34 provided outside the cryostat, a bias current was fed to the local-oscillator section of the superconductive electromagnetic wave mixer described above. An electromagnetic wave of 200 GHz was introduced into the waveguide 38, using a Gunn oscillator and a frequency doubler, and the bias current was applied at 15 to 39 mA. As a result, it was possible to obtain the mixing output 37 with an intermediate frequency of 1 to 0.7 GHz. Here, a GaAs FET amplifier was used as the amplifier 36.

Claims: A superconductive elecromagnetic wave mixer comprising: a substrate (4); a local oscillator section (6;20), integral with said substrate (4), including at least a first Josephson junction (6;20), for generating an electromagnetic wave reference signal; a receiving section (7;21), also integral with said substrate (4), including at least a second Josephson junction (7;21) for receiving an externally originating electromagnetic wave input signal (32) and for mixing said reference signal and said input signal (32); and coupling means (8;17;19), arranged to provide electromagnetic coupling between said local oscillator section (6;20) and said receiving section (7;21); wherein said superconductive electromagnetic wave mixer is characterised in that: said coupling means includes any one of a stripe or a layer of insulating material (8), or a member of conductive material (17;19), said any one of which is disposed inbetween, and in contact with both said local oscillator section (6;20) and said receiving section (7;21). The superconductive electromagnetic wave mixer according to claim 1, wherein each of said first and second Josephson junctions (6,7) is a Josephson junction comprised of a narrowed section of an oxide superconductor polycrystalline thin film (5). The superconductive electromagnetic wave mixer according to claim 1, wherein each of said first and second Josephson junctions (20,21) is a tunnelling Josephson junction. The superconductive electromagnetic wave mixer according to claims 1 or 2, wherein said local-oscillator section (6) and said receiving section (7) each comprise a plurality of serially connected Josephson junctions (6,9,11 & 7, 10, 12). The superconductive electromagnetic wave mixer according to claim 1, 2 or 4 wherein said local-oscillator section (6) and said receiving section (7) are co-planar and separated by said stripe (8) of insulating material. The superconductive electromagnetic wave mixer according to claim 5 wherein said local-oscillator section (6) and said receiving section (7), are formed of a common oxide superconductor polycrystalline thin film (5) and said stripe (8) is constituted by an ion implanted portion of said common film (5). The superconductive electromagnetic wave mixer according to claims 1, 2 or 4 wherein said local oscillator section (6) and said receiving section (7) are coplanar and separated by a gap, and said coupling means includes said member of conductive material (17). The superconductive electromagnetic wave mixer according to claim 1, 2 or 4 wherein said local-oscillator section (6) and said receiving section (7) are laminated one above the other each side of said layer (8) of insulating material. The superconductive electromagnetic wave mixer according to any one of the preceding claims 1, 2, 4 to 6 or 8 wherein said local-oscillator section (6) and said receiving section (7) are of different width. The superconductive electromagnetic wave mixer according to claim 5 wherein a thin-film (26) of MgO, ZrO 2 or Ag is interposed between said receiving section (7) and said substrate (4). The superconductive electromagnetic wave mixer according to claim 3 wherein said local oscillator section (20) and said receiving section (21) are formed of first and second common oxide superconductor polycrystalline thin films (5a,5b) laminated each side of a layer (8') of insulating material, and delineated by either a groove (18) or an ion implanted insulative region (22) formed in said thin films (5a,5b) and layer (8') of insulating material, said coupling means being constituted by a remaining portion (19) of said first oxide superconductor polycrystalline thin film (5a) beneath said groove (18) or insulative region (22). A superconductive electromagnetic wave mixing apparatus comprising: a superconductive electromagnetic wave mixer (30) according to any one of the preceding claims; an introducing means (33) through which the externally originating electromagnetic wave signal (32) is introduced into the receiving section (7;21) of said electromagnetic wave mixer (30); an amplifier (36) that amplifies the electromagnetic wave signal of an intermediate frequency band, obtained as a result of the mixing said reference signal and said input signal (32) in said electromagnetic wave mixer (30); and a cooler (31') that cools at least said electromagnetic wave mixer (30).

Inventors: KANEKO NORIO, KAWASAKI TAKEHIKO, SHINJO KATSUHIKO, YAMAMOTO KEISUKE, KANEKO, NORIO, KAWASAKI, TAKEHIKO, SHINJO, KATSUHIKO, YAMAMOTO, KEISUKE
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1989
Main classification: H03D9
IPC codes: H01L39, H03D9, H03B15