STIMULATION OF CHEMOTAXIS BY CHEMOTACTIC PEPTIDES

Abstract: A method of stimulating chemotaxis toward a prosthetic device is disclosed, which method comprises incorporating a chemotactic peptide of the formula B<1>-X-(AGVPGLGVG)n-(AGVPGFGVG)m-Y-B<2>, wherein B<1> is H or a biocompatible N-terminal group; B<2> is OH, OB<3> where B<3> is a non-toxic metal ion, or a biocompatible C-terminal group; X is GVPGFGVG, GVPGLGVG, VPGFGVG, VPGLGVG, PGFGVG, PGLGVG, GFGVG, GLGVG, FGVG, LGVG, GVG, VG, G or a covalent bond; Y is AGVPGFGV, AGVPGLGV, AGVPGFG, AGVPGLG, AGVPGF, AGVPGL, AGVPG, AGVP, AGV, AG, A or a covalent bond; n is an integer from 0 to 50; m is an integer from 0 to 50; with the proviso that when both n and m are 0, X and Y are selected so that the chemotactic peptide has at least 3 amino acid residues in the X and Y positions combined; into a surface of a prosthetic device.

Description: Deεcription Stimulation of Chemotaxis by C emotactic Peptides Technical Field Thiε work was supported in part by grantε from the National Inεtituteε of Health and the Government haε certain rights in the invention aε a reεult of thiε εuppor . Thiε application is a continuation-in-part of U.S. Serial No. 07/013,343, filed February 11, 1987, which iε a continuation of U.S. Serial No. 06/793,225, filed October 31, 1985, now U.S. Patent 4,693,718. Background Art Thiε invention relateε to εtimulation of chemotaxiε, particularly in relation to proεthetic devices. Diεcloεure of the Invention Replacement of a blood vessel by a prosthetic device is an important and common practice in modern vaεcular surgery. Although some use is made of veins or arteries taken from other portions of a patient's body, most of εuch proεthetic deviceε are prepared from artificial materials that can be prepared in a variety of sizeε and stored in a sterile state ready for use. There are εeveral essential properties of cardiovascular prosthetic materials, among which are the following: 1. Retardation of thrombosis and thromboembolism (an ithrombogenic) ; 2. Minimal harm to blood cells and minimal blood cell adhesion; 3. Long life as prosthetic inserts: and 4. High compliance with the physical and chemical propertieε of natural blood veεεel εuch aε similar elastic moduluε and tensile strength. Another useful property would be a chemotactic response that induced rapid endothelialization and invasion of connective tissue cells for vaεcular wall reconεtruction in a manner εuch that the proεtheεis would be slowly replaced by and/or integrated into newly syntheεized internal elaεtic lamina. None of the materialε preεently being uεed can fulfill all of these requirements. The most commonly used fabric for blood vessel prosthesiε iε made from Dacron (Trademark, DuPont), a εynthetic polyester fiber made from polyethylene tere- phthalate. Dacron has been used in several weaves and in combination with other materials. An example of a frequently used material is the DeBakey Elastic Dacron fabric manufactured by USCI, a division of CR. Bard, Inc. (Cat. No. 007830). Other commonly used materials are felted polyurethane and polytetrafluorethylene (Berkowitz et al. Surgery, 72, 221 (1972); Wagner et al, J. Surg. Res., 1, 53 (1956); Goldfarb et al, Tranε. Am. Soc. Art. Int. Org., XXIII, 268 (1977)). No chemotactic εubεtance iε normally uεed with theεe materials. Another recent development in prosthetic devices is artificial skin of the type disclosed in Yannas and Burke, J. Biomed. Mat. Res., 14, 65-81 (1980). The artificial skin is a collagen/glycosaminoglycan (GAG) composite and had been successfully tested as full- thickness skin wound replacements. Such membranes have effectively protected wounds from infection and fluid loss for long periods of time without rejection and without requiring change or other invasive manipula¬ tion. Appropriately designed artificial skin of this type has retarded wound contraction, and the artificial skin haε been replaced, at leaεt in part, by newly εyntheεized connective tissue. Additional disclosure of this artificial skin is found in Yannas et al, ibid, 107-131 (1980), and Dagalakis et al, ibid, 511-528 (1980). No synthetic chemotactic substance is normally used with these materials. One chemotactic material that might be useful in enhancing invasion of fibroblastε into εuch proεthetic deviceε iε platelet-derived growth factor (PDGF), a potent fibroblaεt chemo-attractant. Unfortunately, PDGF cannot be εynthesized and must be obtained from platelets, making the utilization of such a material on a wide scale impractical. Recently, a chemotactic peptide has been identified in tropoelastin and iε deεcribed in U.S. Patent 4,605,413. Thiε material is a chemotactic peptide having a 6-amino-acid repeating unit of formula APGVGV and its active permutation VGVAPG, in which A represents alanine, P represents proline, G represents glycine, and V represents valine. Although this material readily produces chemotaxis and is a natural component of the human body, therefore making it particularly suitable for use _in vivo, room remains for additional improvements in the field of chemotactic stimulation, for example in cell specificity and sensitivity. Accordingly, there remainε a need for an artificial and easily εyntheεized chemotactic material capable of attracting fibroblaεts and endothelial cells into prosthetic devices and thereby enhancing the incorporation of such devices into the regenerating natural tissue. Best Mode for Carrying Out the Invention Accordingly, it is an object of thiε invention to provide a synthetic material having chemotactic properties towards cells such as fibroblaεtε and endothelial cells. It is a further object of thiε invention to provide a prosthetic device which is readily incorporated into regenerating tissue, such as skin or blood vessel walls. It is still another object of this invention to provide a chemotactic material having stimulating activity to a greater extent than was previously available. These and other objectε of the invention as will hereinafter become more readily apparent have been accomplished by providing a method of stimulating chemotaxis, which compriseε: incorporating a chemotactic peptide of the formula B 1 -X-(AGVPGLGVG) n -(AGVPGFGVG) m -Y-B 2 wherein A iε a peptide-forming residue of L-alanine; P is a peptide-forming residue of L-proline; G is a peptide-forming residue of glycine; V is a peptide-forming residue of L-valine; F is a peptide-forming residue of L-phenylalanine; L is a peptide-forming reεidue of L-leucine; B 1 iε H or a biocompatible N-terminal group; B 2 is OH, OB- * - * " where B 3 is a non-toxic metal ion, or a biocompatible C-terminal group: X is GVPGFGVG, GVPGLGVG, VPGFGVG, VPGLGVG, PGFGVG, PGLGVG, GFGVG, GLGVG, FGVG, LGVG, GVG, VG, G or a covalent bond; Y is AGVPGFGV, AGVPGLGV, AGVPGFG, AGVPGLG, AGVPGF, AGVPGL, AGVPG, AGVP, AGV, AG, A or a covalent bond; n is an integer from 0 to 50; m is an integer from 0 to 50; with the proviso that when both n and m are 0, X and Y are selected so that the chemotactic peptide has at least 3 amino acid residues in the X and Y positions combined; into a layer of a prosthetic device in an amount sufficient to increase chemotaxiε towardε εaid layer. This invention also comprises chemotactic matrices and prosthetic devices prepared according to the method set forth above. Brief Description of the Drawings A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings wherein: FIGURE 1 is a graph of the chemotactic dose response of fibroblasts to AGVPGFGVG; FIGURE 2 is a graph of the chemotactic dose reεponεe of fibroblaεts to GFGVGAGVP; FIGURE 3 iε a graph of the chemotactic doεe reεponse of fibroblasts to human platelet-derived growth factor (comparison); FIGURE 4 is a graph of the chemotactic dose response of fibroblasts to VGVAPG (comparison); FIGURE 5 is a carbon-13 nuclear magnetic resonance spetra of the Phe and Leu containing nonapeptides at 25 MHz, 29°C in DMSO-d 6 . a. H-GFGVGAGVP-OH b. H-GLGVGAGVP-OH; FIGURE 6 is a phase contrast image of a typical monolayer of bovine aortic endothelial cells, which exhibit a "cobblestone" distribution pattern. After incubation with Dil-Ac-LDL, cells showed a punctate fluorescence distribution pattern, indicative of endosomal localization of the labeled LDL derivative internalized by cellε via receptor-mediated endocytosis. All cells were positive in fluorescent labeling with respect to controls, with variability in cell to cell εtaining density typically present. FIGURE 7 εhowε bovine aortic endothelial cell migration response to the elastin repeat nonapeptides; GFGVGAGVP . and GLGVGAGVP —°—. Net fibronectin migration for . curve waε 30 cellε per h.p.f. and 46 cells per h.p.f. for —°— curve. Background migration was 38 and 95 cells h.p.f. for the two nonapeptides respectively. FIGURE 8 shows bovine aortic endothelial cell migration in reεponse to the elastin repeat peptide VGVAPG. Net fibronectin migration was 28 cells per h.p.f. and background migration was 38 cells per h.p.f. Description of the Preferred Embodiments The present invention arose as the result of investigations into the structure of elastic fibers present in blood veεεel wallε and other elastic materials, such as ligaments, present in humans and animals. The central portion of the elastic fibers of vascular wall, skin, lung and ligament is derived from a single protein called tropoelastin. Polypeptide sequenceε of tropoelaεtin from vaεcular wall have been εhown by Sandberg and colleagueε to contain a repeat hexapeptide (Ala-Pro-Gly-Val-Gly-Val) n , a repeat pentapeptide (Val-Pro-Gly-Val-Gly) n , and a repeat tetrapeptide (Val-Pro-Gly-Gly) n , where Ala, Pro, Val and Gly reεpectively repreεent alanine, proline, valine and glycine amino acid residues. (Peptide representations in this application conform to the standard practice of writing the NH 2 -terminal amino acid residue at the left of the formula and the CO2H- terminal amino acid residue at the right.) A high polymer of the hexapeptide has been synthesized. whereby it forms cellophane-like sheets. The hexapeptide has therefore been thought to fill a structural role in the natural material. However, recent investigations have indicated that this hexapeptide and permutations of this sequence are chemotactic for fibroblasts which synthesize elastic fiber precursor protein in biological systems. As a result of this discovery and related investigations into the various permutations of the natural material, U.S. Patent 4,605,413 discloεes and claims a synthetic material based on the hexapeptide sequence. Further investigations into tropoelastin have revealed the presence of a nonapeptide that repeats four times in a single continuous sequence. Investigations into the property of materials based on this repeating unit had indicated that synthetic materials produced having this sequence are potent chemotactic agents having an activity even higher than synthetic materials based on the previously discovered hexapeptide sequence. At their maximum activity, the nonapeptideε are aε active aε platelet-derived growth factor (PDGF) at 30 ng/ml. The nonapeptides therefore are fully as potent as the previously discovered hexapeptides and achieve this activity at a comparable or slightly lower concentration. It is expected that enhanced invasion of elastic-fiber-synthesizing fibroblastε and/or endothelial cells will occur when a prosthetic device, designed for incorporation into regenerating tissue, is treated by incorporating a chemotactic peptide of the formula B 1 -X-(AGVPGLGVG) n ~( GVPGFGVG) m -Y-B 2 wherein A is a peptide-forming residue of L-alanine; P is a peptide-forming residue of L-proline; G is a peptide-forming residue of glycine; V is a peptide-forming residue of L-valine; F is a peptide-forming residue of L-phenylalanine; L is a peptide-forming residue of L-leucine; B 1 is H or a biocompatible N-terminal group; B" ** is OH, OB J where B is a non-toxic metal ion, or a biocompatible C-terminal group: X is GVPGFGVG, GVPGLGVG, VPGFGVG, VPGLGVG, PGFGVG, PGLGVG, GFGVG, GLGVG, FGVG, LGVG, GVG, VG, G or a covalent bond; Y is AGVPGFGV, AGVPGLGV, AGVPGFG, AGVPGLG, AGVPGF, AGVPGL, AGVPG, AGVP, AGV, AG, A or a covalent bond; n is an integer from 0 to 50; m is an integer from 0 to 50; with the proviso that when both n and m are 0, X and Y are selected so that the chemotactic peptide has at leaεt 3 amino acid reεidueε in the X and Y poεitions combined; into a surface of the prosthetic layer. In this way the layer of the prosthetic device becomes the source of a concentration gradient of the chemotactic peptide. Both the isolated nonamers, εuch aε H-AGVPGFGVG- OH, and polynonapeptides have the chemotactic property. The nonapeptide H-GFGVGAGVP-OH haε been shown to have essentially the same chemotactic activity as H-AGVPGFGVG-OH. Chemotactic activity is also expected for the other permutations; i.e., H-GVPGFGVGA- OH, H-VPGFGVGAG-OH, H-PGFGVGAGV-OH, H-FGVGAGVPG-OH, H-GVGAGVPGF-OH, H-VGAGVPGFG-OH, and H-GAGVPGFGV-OH. When a polynonapeptide is present, the compound (perhaps in the form of fragments derived therefrom by in vivo enzymatic action) is chemotactic regardless of the value of n or m. However, for ease of handling, valueε of n and m combined of no more than 100 are preferred εince higher molecular weight compounds have limited solubility and are difficult to handle. Preferred values of n and m are each from 1 to 10, with values of about 5 being most preferred. Preferably, B 1 and B 2 are H and OH, respectively. It can be seen from the above formula, that the peptides of the present invention can be made up of a repeating nonapeptide asεociated with n in the above formula or a repeating peptide aεεociated with m in the above formula. When n iε 0 and m iε 1 or greater, the reεulting compounds are the same as those in U.S. Serial No. 793,225, now U.S. Patent 4,693,718. When n and m are each 0, X and Y. are selected so that the resulting chemotactic peptide has at least 3 amino acid residueε in the X and Y positions. Still more preferably, when n and m are 0, X and Y are selected εo that the reεulting peptide haε at leaεt 5 amino acidε in the X and Y poεitions combined. More preferably, the selected chemotactic peptide has from 5 to 40 amino acid residueε. When the peptide haε 5 amino acidε, it iε preferably GFGVG. Most preferably, the chemotactic peptide has 9 amino acid residues. It is also preferred that n is at least 1. It iε alεo preferred that if m iε greater than 0, n uεt be at leaεt 1 or X or Y uεt be a residue containing a leucine residue. In a most preferred embodiment, n is 1 and m iε 0. It will be noted that polynonapeptides can be syntheεized using any of the nonapeptide "monomers" liεted above. Thuε, polynonapeptideε generally will have the structure B- 1 * —(repeati.ng uni.t) n -B' i where B1 and B 2 represent end groups which are discussed later. The repeating unit can be any of the permutations of the nonamers listed above. In fact, if the chemotactic peptide is not synthesized from nonapeptide "monomers" but rather is synthesized by sequential addition of amino acids to a growing peptide (such as in an automatic peptide synthesizer or by use of an artificial gene) the designation of a repeating unit is somewhat arbitrary. For example, the peptide H- GFGVGAGVPGFGVGAGVPGFGVGAGVPGF-OH can be conεidered to conεist of any of the following repeating unitε and end groups, among others: H-(GFGVGAGVP)3-GF-OH, H-G- (FGVGAGVPG) 3 -F-OH, H-GF-(GVGAGVPGF)3-OH, H-GFG- (VGAGVPGFG) 2 -VGAGVPGF-OH, H-GFGV-(GAGVPGFGV) 2 -GAGVPGF- OH, or H-GFGVG-(AGVPGFGVG) 2 -AGVPGF-OH. Synthesis of the chemotactic peptide iε εtraight- forward and eaεily accomplished by a peptide chemist. The resulting peptides generally have the structure B 1 - (repeating unit) n (repeating unιt) m -B' ** - where B x and B * * represent any chemically compatible end group on the amino and carboxyl ends of the molecule, respectively, and n and m are from 0 to about 50. When B 1 is H, B 2 iε OH, n = 1 and m = 0, the compound iε a nonapeptide. When n or m iε greater than 1, the compound iε a polynonapeptide (often referred to herein aε a polypeptide) . It iε poεεible that one or more amino acid residue or segment of amino acid residues not present in the normal polynonapeptide sequence may be interspersed within a polynonapeptide chain so long as the chemotactic character of the resulting molecule is not completely disrupted. As clearly indicated by the formula and by the following discussion, the invention encompasεes incorporation of a nonamer or polynonapeptide into a larger peptide chain in which B 1 and B 2 represent the remainder of the larger peptide chain . Other examples of terminal B **1 - and B 2 end groups include portions of the repeating peptide units themselves with free amino or carboxylic acid groups or εaltε thereof, free amino or carboxylic acid groups or salts (especially alkali metal salts), and peptide or amino acid units that have retained a blocking group that was present during syntheεis of the polypeptide or that have a biocompatible group added after formation of the polypeptide. Examples of blocking groups include t-butyloxycarbonyl, formyl, and acetyl for the amino end of the molecule and esters, such as methyl esters, as well as amides, εuch aε the amideε of ammonia and methyl amine, for the acid end of the molecule. The end groups are not critical and can be any organic or inorganic group that does not destroy the chemotactic properties of the polypeptide or confer bio-incompatibility to the molecule as a whole. The term biologically compatible as used in this application means that the component in question will not harm the organism in which it is implanted to such a degree that implantation is as harmful as or more harmful than the needed prosthetic device. Methods of preparing polypeptide polymers have been disclosed in Rapaka and Urry, Int. J. Peptide Protein Res. , 11, 97 (1978), Urry et al, Biochemiεtry, 13 r 609 (1974), and Urry et al, J. Mol. Biol., £6, 101 (1975), which are herein incorporated by reference. The εyntheεis of these peptides is straightforward and can be easily modified to any of the peptides disclosed herein. The following εummary, which iε not to be considered limiting, is an example of the general method of synthesizing the polypeptides. The first step in the formation of a polynona¬ peptide of the invention usually is synthesis of a nonapeptide monomer. Any of the classical methods of producing peptide molecules may be used in synthesizing the building blocks of the polymers of the present invention. For example, syntheεis can be carried out by classical solution techniques starting from the C- terminal amino acid as a benzyl (Bzl) ester p- tosylate. Each successive amino acid is then coupled to the growing peptide chain by means of its water- soluble carbodiimide and 1-hydroxybenzotriazole. A typically used carbodiimide is l-(3-dimethylamino- propyl)-3-ethylcarbodiimide hydrochloride (EDCI). During the coupling reaction the amino group is protected. The protecting group is then removed after condensation has taken place. A suitable protecting group is tert-butyloxycarbonyl (Boc), which can easily be removed by trifluoroacetic acid. The first product obtained in the εynthesis of the hexapeptide monomer is a protected nonapeptide, such as Boc-L • Ala-Gly-L • al-L • Pro-Gly-L • Phe-Gly-L • Val-Gly- OBzl. This protected monomer is converted into the reactive monomer by, for example, replacement of the benzyl ester with the p-nitrophenyl ester, for example by effectively exchanging with p-nitrophenyl trifluoroacetate, and removal of the Boc protecting group. The resulting reactive monomer is polymerized, in the preεence of a baεe such as triethylamine as necessary, to give the polypeptide. A blocking group, such as H-Val-OMe may be added at the conclusion of the polymerization reaction to convert the remaining reactive p-nitrophenyl esters to non-reactive terminal groups if desired. Since all of the amino acids present in the polypeptides of the invention have corresponding DNA codons, the polypeptideε can also be produced by genetic engineering using synthetic genes containing codons that correspond to the desired amino acid εequence. When a modified chemical εtructure iε deεired, as, for example, when chemical cross-linking between two chains of polynonapeptide or between a polynonapeptide chain and a peptide-forming part of the structure of a prosthetic device will be carried out, side-group- blocked lyεine or glutamic acid (or another amino acid with a protected side group capable of forming a cross¬ link after the protecting group is removed) may be utilized in place of one of the normal amino acids that is present in the polypeptide chain. A synthesis of a chemically crosε-linked polypentapeptide of similar structure is discloεed in U.S. Patent 4,187,852, which iε herein incorporated by reference. It is not necessary for the chemotactic peptide. of the invention to be covalently attached to the surface toward which chemotaxis is being stimulated. It is sufficient that the peptide be present at the surface or layer. Therefore, the phrase "incorporating into a surface or layer" as used in this application encompasseε all methodε of applying a chemotactic peptide of thiε invention to a εurface, whether that application reεults in chemical bonding or not. For example, solutions or suspensions containing the peptide can be painted on the surface of a proεthetic device or a device can be submerged in a solution of the chemotactic peptide and be made to swell taking in the chemotactic peptide and then can be made to contract expelling the water but leaving the chemotactic peptide within the matrix of the device. It is also possible to form covalent bonds between the chemotactic peptide and the prosthetic device. For example, during the synthesis of a chemotactic peptide as described above, various intermediates are produced which have reactive carboxy or amino terminals. Many of the prosthetic devices which are intended for incorporation into regenerating tisεue are prepared from collagen or related materials and therefore contain free amino acid functional groups, such as amino or carboxylic acid groups. Peptide bonds can easily be formed between such functional groups in the prosthetic device and reactive intermediates such as those described above. The type of prosthetic device which can be used in conjunction with the present invention is not limited, since the chemotactic property is related to the peptide and not to the prosthetic device itself. It is preferred, however, that the prosthetic device be one which is intended for incorporation into regenerating tissue, such as an artificial vein or artery or artificial skin. Publications which disclose various prosthetic devices useful for forming artificial skin or blood vesεel wallε are liεted in the εection of thiε application entitled Background of the Invention, and theεe publications are herein incorporated by reference. Two particularly preferred embodiments of the present invention involve using the chemotactic polypeptide with a collagen/glycosaminoglycan composite material as an artificial skin, as described in U.S. Patent 4,280,954, and with biocompatible artificial materials based on polypeptides as described in U.S. Patent 4,187,852: U.S. Patent Application Serial Number 308,091, filed October 2, 1981; and U.S. Patent Application 452,801, filed December 23, 1982, all of which are herein incorporated by reference. These are peptide-containing materials, and the chemotactic polypeptide may readily be attached by covalent bonding into such materials by the methods described above. However, as also previously indicated, covalent bonding iε not necessary and indeed is not preferred since the chemotactic property is also exhibited when the chemotactic peptide is merely present on the surface or in the pores of a prosthetic material. Prosthetic devices having surfaces comprising other structural peptides are also preferred over prosthetic devices having other types of surfaces, although other types of surfaces, such as Dacron, and other synthetic fibers, are specifically included. Examples include natural materials εuch tendonε or ligaments (for example, those transferred from one location to another within the same body) and synthetic or semi-synthetic materials. Semi-synthetic materials are those derived by manipulation of natural materials, such as collagen. The amount of chemotactic peptide which is required for a particular prosthetic device can easily be determined by simple experimentation. Generally, quite low concentrationε of the chemotactic peptide are required. For example, doping of a non-chemotac ic εurface to produce low concentrations of 0.1 nM to 100 nM of a chemotactic peptide at the surface will be εufficient. Generally, from 10 ~9 to 10 ~3 millimoles of nonamer or repeating unit of a polynonapeptide per 100 cm **1 of surface is sufficient for this purpose. It iε preferred to produce a concentration of the chemotactic nonamer of from 10~ 10 to 10 ~& M, preferably 10~ 9 to 10 —7' M at the reεponsive cell. Alternatively or additionally, a 2-component synthetic bioelaεtomer comprising the chemotactic peptide of this invention and the elastic polypentapeptide or polytetrapeptide of U.S. Patent 4,187,852 would act as a chemotactic elastic biopolymer which could be utilized for a variety of purposes. It is also possible to use the chemotactic peptide of this invention in a system involving natural crosslinking of synthetic bioelastomerε, as is described in U.S. Patent Application Serial Number 533,524, now Patent No. 4,589,882, which is herein incorporated by reference. That application discloses bioelastomers which are enzymatically croεε-linked by lyεyl oxidaεe. The above diεclosure generally describes the present invention. A more complete understanding can be obtained by reference to the following specific examples, which are provided herein for purposes of illuεtration only and are not intended to be limiting unless otherwise specified. Example 1 The chemotactic response of fibroblasts to two nonapeptides of the invention was measured using the techniques described below. Materials and Methods Source of Chemicals and Materials Dulbecco's Modified Eagle Medium (DMEM), noneεεential amino acids, L-glutamine, fetal bovine serum, penicillin-streptomycin solution: GIBCO, Chagrin, Ohio. Trypsin 1-300: ICN, Cleveland, Ohio. Ethylene diaminetetraacetic acid (EDTA) - sodium salt and gelatin: Sigma, St. Louis, Mo. Human serum albumin (HSA) : American National Red Crosε, Washington, D.C Hematoxylin: Harleco, Gibbstown, NJ. Platelet-derived growth factor (PDGF): Calbiochem. , San Diego, CA. Polycarbonate membraneε: Nucleopore Corp., Pleaεanton, CA. Celluloεe nitrate membranes: Millipore Corporation, Bedford, MA. Cells Passage-two fetal bovine ligamentum nuchae fibroblast cell cultures were grown to confluency in 75 cm 2 plastic tisεue culture flasks with Dulbecco's Modified Eagle (DME) medium containing 10% fetal calf serum, 2 mM L-glutamine, 0.1 mM nonesεential amino acids, penicillin (100 U/ml), streptomycin (100 μg/ml). These passage-two cell cultures were obtained from passage-one cell cultures provided by R. M. Senior and R. B. Mecham (Waεhington Univerεity, St. Louis, MO) . Ligamentum nuchae explants were obtained from fetal calveε greater than 180 dayε in geεtational age. Becauεe of the poεεibility of platelet derived factorε being present in the fetal calf serum, the cells were harvested after a 48 hour fast. At one to two days past confluency, the cells were dispersed by trypsin (0.025% trypsin, 0.1% EDTA in phosphate buffered saline, pH 7.4) and washed two times in a second DME medium containing 2 mM glutamine, 0.1 mM nonessential amino acids and 1 mg/ml human serum albumin. Cell concentration was determined with a hemocytometer and adjusted to a final concentration of 1.5 x 10^ cells/ml. The cells were used as is for the chemotaxis aεsay. Chemotaxiε Assay The chemotaxis experiment used a 30 hole multi- blindwell plate as an adaptation of the modified Boyden chamber. The upper and lower compartments were separated by an 8 μm polycarbonate membrane superi poεed on a 0.45 -urn celluloεe nitrate membrane. The 8 μm membrane waε pretreated with 5% gelatin to enhance fibroblaεt attachment. The lower compartment contained 0.24 ml of the second DME medium plus/minus chemotactic peptides while the upper one had 0.37 ml of the second DME medium with fibroblastε. In the checkerboard assay, peptide was also added to the upper compartment. The filled plate was placed in a humidified incubator at 37°C with 5% CC^-air for 6 hours, after which the cell suspension was aspirated and the membranes were recovered, fixed in ethanol, stained in Harris 1 Alum hematoxylin, dehydrated in a graded series of propanol and cleared in xylene. Quantitation of cell locomotion to the area between the two membranes was done with a light microscope, fitted with a bright field objective and eye piece grid, at 400 x. There were 3 membrane pairε per experimental condition and 5 randomly chosen fields were examined per pair. Every experiment had a negative control, i.e. medium alone, and a positive control, i.e. platelet-derived growth factor, PDGF, in the lower compartment. Number of cells per high power field are expreεsed in FIGURES 1 through 3 and in Tables I and II as the net number of cells that migrated through the polycarbonate membrane. The number of cells moving with medium alone in the lower compartment was subtracted from the number of cells moving in response to one of the peptides. Table I Checkboard Analysis of AGVPGFGVG with Fibroblasts Peptide concentration above filters (M) (10)0 + 1.3 -2 + 1.1 -2 + 0.5 -3 + 0.9 Peptide con. 10 " ■10 6 + 1.3 -3 + 1.0 -4 + 0.8 2 + 1.8 below filters 10 -9 25 + 1.6 3 ± 1.7 -4 + 0.6 -2 + 1.1 (M) 10-8 9 + 2.3 5 + 1.6 5 + 1.2 -2 + 1.1 Results are expressed as means + S.E.M. where n = 15. Positive control, PDGF at 60 μg/ml = 21. Table II Checkboard Analysis of GFGVGAGVP with Fibroblasts Peptide concentration above filters (M) 0 10 -ιo 10-9 10 "8 0 (9)0 + 1.0 1 + 1.0 3 + 1.2 -2 + 1.4 Peptide con. ιo- 10 13 + 1.6 -1 + 0.8 -3 + 0.7 -1 + 0.8 below filters 10-9 45 + 3.4 7 + 1.8 -2 + 1.0 -1 + 1.1 (M) ιo- 8 21 + 1.5 12 + 1.6 7 + 1.5 0 + 1.50 Results are expressed as mean + S.E.M. where n = 15. Positive control, PDGF at 30 μg/ml = 59. Peptide Syntheεiε Elemental analyεes were carried out by MicAnal, Tuscon Az. All amino acids are of L-configuration except for glycine. Tertiary-butyloxcarbonyl (Boc) amino acids and amino acid benzyl esters (Bzl) were purchased from Bachem, Inc., Torrance, CA. Thin-layer chromatography waε performed on εilica gel plateε obtained from Whatman, Inc., NJ and mentioned as R f 1 values in different solvent systems. R f chloroform (C), ethanol (M) , acetic acid (A), 95:5:3; R": CMA (85:15:3); R~! CMA (75:25:3); RJ ethyl acetate, acetic acid, ethanol (90:10:10). The hexapeptide was synthesized and purified as outlined in Senior et al. , J. Cell Biol. 9_9 _ 870-874 (1984). The synthesis of the nonapeptides is carried out by solution methods and is presented in Schemes 1 and 2. Scheme 1 Synthesis of HCO HI-Ala-Gly-Val-Pro-Gly-Phe-Gly-Val-Gly-OH Scheme 2 Synthesis of HCO,H*H-Gly-Phe-Gly-Val-Gly--Ala-Gly-Val-Pro-OH CF 3 C0 2 H*H-Gly-Val-Gly-OBzl (II): Boc-Gly-Val-Gly-OBzl (I) (10.0 g, 23.72 mmol) was stirred with 100 ml of trifluoroacetic acid (TFA) for one hour and solvent removed under reduced presεure. The residue was triturated with ether, filtered, washed with ether and dried, to give 9.4 g (yield: 91%) of the deblocked peptide. Boc-Phe-Gly-Val-Gly-OBzl (III): Boc-Phe-OH (9.16 g, 34.54 mmol) was disεolved in 100 ml of dimethyl- formamide (DMF), cooled to 0°C and N-methylmorpholine (NMM) (3.83 ml) added. The solution was cooled to -15°C and isobutyl chloroformate (IBCF) (3.96 ml, 30 mmol) was added slowly under stirring while maintaining the temperature at -15 + 1°C After stirring at this temperature for 15 minutes, a precooled solution of II (9.4 g, 21.59 mmol) and NMM (2.4 ml) in DMF (40 ml) was added and stirring continued for two hours at ice-bath temperature. A saturated solution of KHCO^ was added to bring the pH to 8.0 and stirred for an additional 30 minutes. The reaction mixture was poured into a cold 90% saturated NaCl solution (1000 ml) and the precipitate obtained was filtered, washed with satd. NaCl, H O and dried. The peptide was crystallized from ethyl acetate to give 10 g of III (yield: 81.5%). W 0.83 Anal. Calcd. for C 30 H 40 N 4 O 7 : C 63.35, H 7.09, N 9.85%. Found: C 62.96, H 7.37, N 9.86%. Boc-Gly-Phe-Gly-Val-Gly-OBzl (IV): III (8.0 g, 14 mmol) was deblocked as described for II and coupled with Boc-Gly-OH by the excesε mixed anhydride method and worked up aε deεcribed under III to obtain the title compound in 98.6% yield, R f 0.75. Anal. Calcd. for C 32 H 43 N 5 0 8 : C 61.42, H 6.92, N 11.19%. Found: C 61.12, H 7.21, N 11.19%. Boc-Val-Pro-Gly-Phe-Gly-Val-Gly-OBzl (VI): Boc-Val-Pro- OH (V) (29) (1.89 g, 6.02 mmol) and 1-hydroxybenzo- triazole (HOBt) (0.92 g, 6.02 mmol) were taken in DMF (20 ml), cooled with ice-salt freezing mixture and reacted with l(3-dimethylaminopropyl)-3-ethylcarbo- diimide hydrochloride (EDCI) (1.15 g, 6.02 mmol) for 15 min. IV was deblocked as described under II and an ice-cold solution of this deblocked peptide (3.5 g, 5.4 mmol), NMM (0.61 ml) in DMF (20 ml) was added to the above activated acid component and εtirred for two days at room temperature. Solvent was removed under reduced presεure. The reεidue was taken in chloroform and washed with water, 20% citric acid, water, satd. NaHC0 3 , water, dried over anhyd. MgS0 4 and solvent removed under reduced preεεure to give the desired peptide (3.4 g, yield: 75.7%), R^ 0.27, R^ 0.71 Anal. Calcd. for C 42 H 5g N 7 O 10 : C 61.36, H 7.23, N 11.93%. Found: C 61.25, H 7.66, N 12.08%. Boc-Ala-Gly-OBzl (VII): This peptide was prepared by the mixed anhydride method as described for the synthesis of III in 81% yield, R 1' 0.24, R4l 0.92. Anal. Calcd. for C 17 H 24 N 2 0 5 : C 60.16, H 7.13, N 8.25%. Found: C 59.68, H 7.17, N 8.09%. Boc-Ala-Gly-OH (VIII): VII (16.97 g, 50 mmol) was taken in glacial acetic acid (170 ml) and hydrogenated overnight in the presence of 10% Pd/C (1.7 g) as catalyst at 40 psi. The catalyεt was filtered with the aid of celite and solvent removed under reduced pressure. The residue was taken in satd. NaHC0 3 εolution, extracted with EtOAC (3x), cooled, acidified to pH 2.0 and re-extracted with EtOAC (3x). The combined EtOAC extractε were washed with satd. NaCl, and concentrated under reduced pressure. The residue was triturated with EtOAC: Pet. ether (1:1) and the precipitate obtained was filtered, washed with pet. 4 ether and dried (10.9 g, yield: 87.5%), R f 0.52. Anal Calcd. for C 10 H 18 2 O 5 -1/2H 2 0: C 46.50, H 7.41, N 10.84%. Found: C 46.64, H 7.41, N 10.84%. Boc-Ala-Gly-Val-Pro-Gly-Phe-Gly-Val-Gly-OBzl (IX) : VIII was coupled with the deblocked VI using EDCI/HOBt as described for the preparation of VI to give the desired peptide in 84.8% yield. R^ 0.76, R- 0.28. Anal, calcd. for C 47 Hg 7 g0 12 : C 59.22, H 7.08, N 13.22%. Found C 58.73, H 7.55, N 13.14 ? o- • Boc-Ala-Gly-Val-Pro-Gly-Phe-Gly-Val-Gly-OH (X): The nonapeptide benzylester (IX) was hydrogenated as described under VIII to obtain the acid in quantitative yield. Ri. 0.24. Anal, calcd. for C 40 H 61 N g O 12 *H 2 0: C 55.09, H 7.16, N 14.3%. Found: C 54.69, H 7.16, N 13.81%. HC0 2 H*H-Ala-Gly-Val-Pro-Gly-Phe-Gly-Val-Gly-OH (XI) : X (20 mg, 0.023 mmol) was εtirred with 95-97% formic acid (0.6 ml) for 6 hours and concentrated under reduced pressure. The residue was taken in dist. water and lyophilized to obtain the product in quantitative yield. R^ 0.65. This completes synthesiε of the first permutation. Boc-Ala-Gly-Val-Pro-OBzl (XIII): To obtain the second permutation, Boc-Val-Pro-OBzl (XII) was deblocked with TFA and coupled with VIII as descibed under VI to obtain the protected tetrapeptide in 67.4% 2 4 yield. R f 0.80, R f 0.80. Anal calc. for C 27 H 4Q N 0 7 : C 60.54, H 7.52, N 10.46%. Found: C 60.80, H 7.53, N 10 . 56^ Boc-Gly-Phe-Gly-Val-Gly-OH (XIV) : IV was hydrogenated and worked up as described for VIII to obtain the • 3 product in quantitative yield. R^ 0.16. Anal, calcd. for C 25 H 37 N 5 0 8 *H 2 0: C 54.23, H 7.10, N 12.65%. Found: C 54.14, H 6.93, N 12.21%. Boc-Gly-Phe-Gly-Val-Gly-Ala-Gly-Val-Pro-OBzl (XV) : After deblocking XIII with TFA, the salt was coupled with XIV using EDCI/HOBt and worked up as for the pre- - paration VI. The title compound was obtained in 75.5% yield. R . 0.57. Anal, calcd. for C 47 H 67 N 9 0 12 *2H 2 0: C 57.06, H 7.23, N 12.74%. Found C 54.23, H 7.10, N 12.74%. Boc-Gly-Phe-Gly-Val-Gly-Ala-Gly-Val-Pro-OH (XVI): The above peptide XV was hydrogenated as described for the preparation VIII to obtain the product in quantitative • 3 yield. Rz. 0.22. Anal, calcd. for C 40 H 61 9 O 12 : C 55.66, H 7.12, N 14.60%. Found: C 55.86, H 7.23, N 14.14%. HC0 2 H • H-Gly-Phe-Gly-Val-Gly-Ala-Gly-Val-Pro-OH (XVII): The peptide XVI was treated with formic acid 3 and worked up as described under XI. Rz. 0.06. This completes the syntheεis of the second permutation. Reεultε Carbon-13 nuclear magnetic resonance spectra for the two nonapeptides demonstrated their purity. The elastin nonapeptide AGVPGFGVG (compound XI) and its permutation GFGVGAGVP are both chemoattractants for elaεtin εynthesizing ligamentum nuchae fibroblasts. FIGURE 1 shows the positive migration of fibroblasts in response to a concentration gradient ranging from lO -12 to 10 ~5 M nonapeptide. Maximal activity was at 10 ~9 M for AGVPGFGVG. Four such curves were run and all peaked at 10 ~9 M. Its permutation GFGVGAGVP (compound XVII) was tested with a concentration range of 10 ~12 to 10 -** - * (FIGURE 2). Again the maximal response waε at 10 ~9 M. Again, four experiments were completed and in all 10 -9 M represented maximal activity. FIGURE 3 shows the response of the fibroblaεtε to human platelet derived growth factor at 0.3, 3, 10, 20, 30, 40, 50, 60, 70, 90, 300 and 3000 ng/ml. Maximum activity iε at 30 ng/ml (1 nM) . The hexapeptide, VGVAPG, of tropoelastin was chemotactic for fibroblaεtε with the peak of activity at 10~ 8 M (FIGURE 4). Two such tests were done and both peaked at 10 -8 M. The "checkerboard analysis" was performed with the two nonapeptides to identify the fibroblast migration as chemotaxis. Peptide was added to the lower compartment, to the upper compartment (with the cells) or to both compartments to set up a positive, a negative or zero gradient, respectively. Tables I and II for AGVPGFGVG and GFGVGAGVP show that the cells preferentially migrated in response to a positive gradient and not to a negative gradient or to no gradient. The experiments represented by the data in Tables I and II were repeated three times and two times, respectively. In all caseε, the data followed the patternε seen in Tables I and II. The data demonstrate that the peptides stimulated direct (chemotaxis) rather than random (chemokinesiε) migration of fibroblasts and that the peptides are true chemoattractants. Relative to the positive control of 30 μg/ml PDGF, the nonapeptides stimulated the same level of migration as PDGF. Example 2 Materials and Methods: Source of Chemicals and Materials Modified Medium 199, fetal bovine serum trypsin- EDTA and antibiotic antimycotic solution were purchased from GIBCO, Chagrin, OH. The sources of the polycarbonate and cellulose nitrate membranes were Nucleopore Corp., Pleasanton, CA and Millipore Corp., Bedford, MA. The hematoxylin stain was from Harleco of Gibbstown, N.J. and the Hemacolor stain was purchased from American Scientific Products, Stone Mountain, GA. Human plasma fibronectin was purchased from Calbiochem, San Diego, CA. Cell culture and cell preparation Bovine thoracic aorta endothelial cells were isolated by scraping with a scalpel blade. Harvested cells were washed by centrifuga ion in Medium 199 with Hank's salt solution containing penicillin-streptomycin and 10% fetal bovine serum. After dissociation of cell aggregates by extrusion through a 27 gauge needle, cells were seeded in 25 cm 2 flasks at densitieε of about 10 4 cellε/cm 2 and reached confluency in 3 to 4 dayε. Cells were grown in Medium 199, 10% fetal bovine serum and 5% Ryan's growth supplement (Dr. U.S. Ryan, U. Miami, FL) . When cells reached confluency, they were subcultured at a 1:3 split ratio, after removal from culture dishes with a Costar cell scraper. Cells were monitored for purity to specific fluorescent staining of endothelial uptake by acetylated low density lipoprotein (Stein and Stein, 1980, Netland et al, 1985) labeled with 1,1'-dioctadecyl-1,3,3,3' ,3'- tetramethylindocarbocyanine perchlorate (Dil-Ac-LDL, Biomedical Technologies, Stoughton, MA). All studieε were performed on first to fifth passage cells. These early pasεage cells at one to two days past confluency were dissociated in 0.05% trypsin, 0.02% EDTA in Hanks Balanced Salt Solution for 3 minutes at 37°C, centrifuged, washed 2 times and resuspended in Medium 199 without fetal calf εerum. The trypsin reaction was stopped with soybean trypsin inhibitor at 1 mg/ml. Cell concentration was determined with a hemocytometer and adjusted to a final concentration of 10 6 /ml. Chemotaxis Assay Chemotactic response was assayed wtih a 30 hole multi-blind-well plate as an adaptation of the modified Boyden chamber with the double membrane technique. A collagen coated 8μ polycarbonate, polyvinyl pyrrolidone (PVP) free, membrane superimpoεed on a 0.45μ celluloεe nitrate membrane εeparated the lower and upper compartmentε containing respectively 0.24 ml of test peptide disεolved in Medium 199 and 0.37 ml of the cell εuεpenεion. The collagen pretreatment waε intended to enhance cell attachment to the polycarbonate membrane. In the checkerboard assay, to distinguish between directed cell migration (chemotaxis) and random cell locomotion (chemokinesis) , the concentration gradient between the upper and lower chambers were aboliεhed by adding the test peptide at various concentrations to the cell suspenεion. For all experiments medium alone in the bottom chamber served as the baseline control. Human plasma fibronectin at 100 μm/ml in the bottom was the positive control. The filled plate was incubated for 5 hourε at 37°C in a humidified incubator with 5% C0 2 ~air. The membrane pairs were recovered, fixed in ethanol, stained in Harriε' alum hematoxylin, hydrated in a graded εeries of propanol and cleared in xylene. The membrane pairs were mounted on glass slides and cell locomotion quantitated in the volume between the two membranes using bright field-at 400X. Five randomly chosen fields were counted per membrane pair with there being 3 membrane pairs per experimental condition. The average of the 15 fields was calculated as was the standard error of the mean (S.E.M.) where n was 15. Net cell migration was plotted as a function of peptide concentration with net migration being the average number of cells moving in responεe to the peptide minus the average number of cells moving in response to medium alone. The chemotactic response was also assayed with the Neuroprobe (Bethesda, MD) micro blind-well chamber. The lower wellε contained 30 μl of Medium 199 + teεt peptide of fibronectin, and the upper wells 55 μl of the cells suspended in Medium 199. A 8-μm pore size. PVP-free, rectangular, polycarbonate, gelatin and f brσnectin treated, membrane separated the upper and lower chambers. The gelatin pretreated membrane was incubated in a PBS solution of 100 μg/ml fibronectin at room temperature for 2 hours, air dried and used within weeks. Once the cells were added to the assembled chamber, it was incubated at 37°C in 95% air - 5% C0 2 for 4 hours. The filter was removed, the top layer of nonmigrating cells scraped off and the bottom layer of migrating cells fixed in ethanol and stained with Hemacolor. Quantita ion of cell movement was the same as for the 30 well chamber. In the inventors' hands, both chemotaxis chambers were equally effective as were both membrane treatments (i.e., with and without a fibronectin coating on the gelatin) . Peptide Synthesis The synthetic procedures were analogous to those discusεed above. Reεultε The carbon-13 nuclear magnetic resonance (CMR) spectra of the two nonapeptides are give in FIGURE 5, indicating the correctnesε of synthesis and the purity of the final products. FIGURE 6 shows a phase contrast image of a typical monolayer of bovine aortic endothelial cells, which exhibit a "cobblestone" distribution pattern. After incubation wtih Dil-Ac- LDL, cells showed a punctate fluorescence distribution pattern, indicative of endosomal localization of the labeled LDL derivative internalized by cells via receptor-mediated endocytosiε. All cellε were positive in fluorescent labeling with respect to controls with variability to cell to cell staining density typically present. Elastin synthetic peptides are chemoattractants for bovine aortic endothelial cellε. FIGURE 7 preεents the data collected in an effort to determine the optimal concentration of maximal stimulation of the endothelial cell migration. The dose response curve for the elastin repeat nonapeptide and early pasεage endothelial cellε indicate that maximal activity is a 8 x 10 "10 M for both peptides, the Phe-containing nonamer (GFGVGAGVP) and the Leu-containing nonamer (GLGVGAGVP). These dose response experiments were repeated 10 times for the Phe-nonapeptide and 9 times for the Leu-nonapeptide; all had the same results including one study which was counted blind (i.e., the slides were coded and the code was unavailable to the microscopist) . FIGURE 7 repreεents the data from two different experimentε. The data were normalized with respect to the fibronectin positive control because of variability in cell responsiveness from experiment to experiment. The left ordinate presents the results as a percent of the fibronectin positive control, the right ordinate gives the actual number of cells migrating per high power field (h.p.f.), for both the Phe and Leu containing nonapeptides. Note the differences in the scales, indicating that in the Phe- nonapeptide experiment, the positive control was 30 cells per h.p.f. and in the Leu-nonapeptide experiment, the positive control, was 46 cells per h.p.f. With the data normalized this way, it iε evident that both nonapeptides peak at the same concentration and elicit the same degree of responsiveness. The biphasic aspect of the curves may be due to several proceεεes. One is the possibility of saturation of the cell receptors that trigger the chemotactic response and the other is the possibility of gradient breakdown. Table III presents the data for the checkerboard assay. As expected for chemotaxis, the valueε along the diagonal indicate zero net cell migration when the concentrations in the two chambers are equivalent, above the diagonal the migration is not significant whereas below the diagonal there is a concentration dependent net movement of cells. These data establiεh that the repeat elaεtin nonapeptideε promote chemotaxiε (i.e., directed movement) rather than εolely chemokinesis (i.e., increased random movement). This experiment was repeated 7 timeε and each experiment had the same pattern. The hexapeptide of elastin also induced cell migration (FIGURE 8). However, maximal activity shifted by over a decade of concentration to 10 ~8 M. Relative to the fibronectin positive control, the hexapeptide is less active than the two nonapeptides. This experiment was repeated 7 times and the same pattern was obtained. Table III Checkboard Analysis of GFGVGAGVP with Endothelial Cells GFGVGAGVP (M), GFGVGAGVP (M) , upper compartment lower compartment 0 lO "10 8 x lO "10 10 "8 0 0(16) 4 +_2 1 + 2 -3 + 1 lO" 10 6 + 2 1 + 2 3 + 2 -1 + 1 8 x lO "10 19 + 3 11 + 1 -3 + 1 3 ± 1 10' 8 4 + 2 -1 + 2 3 + 2 1 + 1 Discuεsion Peptide purity is an important issue for these chemotactic experiments; one reason is the sharpness of the concentration dependency. If impurities were present from peptide syntheεiε and varied from lot to lot, inappropriate amountε would be weighed out for the cell migration aεsay and the peak could easily be missed. Also the impurities themselveε could elicit a chemotactic reεponεe. The CMR spectra attest to the peptides 1 purity. As important as a pure chemo- attractant is to the chemotaxis experiment, so too is a pure cell population that responds to a positive control as previous deεcribed. FIGURE 6 demonεtrates the purity of the cell culture and FIGURE 7 demonstrates that these endothelial cells do migrate towards fibronectin. The resultε indicate that the elaεtin nonapeptides can serve as chemoattractants for endothelial cells. This finding haε significance in that the elastin synthetic peptide becomes one of few pure synthetic and chemically defined compounds both to support chemotaxis and to be readily available and at reasonable coεt. It also is easily handled, requiring no special storage and dissolution techniques. A wide variety of factors can effect endothelial migration. Some are from blood: platelet factors, lymphocyte products, mitogenic factors from leukocyte cultures, lymphokines, interferon, fibrinogen and its fragments. Many factors have been iεolated from tissue in soluble form. These include tumor derived factors, angiogenic factors and preparations and growth factors. There are data indicating that fibronectin alone and/or in concert with ganglioεideε or heparin constitutes a chemoattractant for endothelial cells. From this rather extensive listing it is apparent that, aside from fibronectin, fibrinogen and heparin, there are few pure and chemically defined substances that are both supportive of chemotaxis and readily obtainable. The results suggest the use of these nonapeptides as new standards for endothelial cell chemotaxis. The findings have potential relevance to development of biomaterials, especially in the area of vascular prostheses. Biomaterialε that comprise current vascular prosthes s do not adequately support the development of an endothelial lining. It is reasonable to suggest that future prostheses will need to use biomaterials that support cell attachment, cell growth and migration of the components of the vascular wall with special emphasiε on endothelial cells to improve the patency characteristicε of synthetic small vessels. The nonapeptides could provide chemotactic stimuli for endothelial cell migration into the vascular prostheεiε. One of the firεt morphological eventε obεerved in angiogenesiε is the mobilization of capillary endothelium. Directed migration of chemotaxis has been proposed as one aεpect of the proceεε of angiogenesis and neovascularization. The elastin nonapeptide may be an angiogenic factor in that it promotes directed movement of endothelial cells. It may promote the next step of causing capillaries to infiltrate tisεues. The invention now being fully described, it will be apparent to one of ordinary skill in the art, that many changes and modifications can be made thereto without departing from the spirit or scope of the invention as set forth herein.

Claims: Claimε 1. A method of εtimulating chemotaxiε toward a prosthetic device, which comprises: selecting a chemotactic peptide of the formula B 1 -X-(AGVPGLGVG) n ~(AGVPGFGVG) m ~Y-B 2 wherein A is a peptide-forming residue of L-alanine; P is a peptide-forming residue of L-proline; G is a peptide-forming residue of glycine; V is a peptide-forming residue of L-valine; F is a peptide-forming residue of L-phenylalanine; L is a peptide-forming residue of L-leucine; B- ** - is H or a biocompatible N-terminal group; B is OH, OB" *** where B 3 is a non-toxic metal ion, or a biocompatible C-terminal group: X is GVPGFGVG, GVPGLGVG, VPGFGVG, VPGLGVG, PGFGVG, PGLGVG, GFGVG, GLGVG, FGVG, LGVG, GVG, VG, G or a covalent bond; Y is AGVPGFGV, AGVPGLGV, AGVPGFG, AGVPGLG, AGVPGF, AGVPGL, AGVPG, AGVP, AGV, AG, A or a covalent bond; n is an integer from 0 to 50; m is an integer from 0 to 50; with the proviso that when both n and m are 0, X and are εelected so that the chemotactic peptide has at least 3 amino acid residues in the X and Y positionε combined; and incorporating εaid peptide into a layer of a proεthetic device in an amount sufficient to increase the invasion of endothelial cells into said prosthetic device. 2. The method of Claim 1, wherein n is from 1 to 10 and m is 0 to 10. 3. The method of Claim 1, wherein n is about 5 and m is 0 to 5. 4. The method of Claim 1, wherein n is 1 and m is 0. 5. The method of Claim 1, wherein said peptide is H-GFGVGAGVP-OH or a salt thereof. 6. The method of Claim 1, wherein B *** - is H and B 2 is OH or OB 3 where B 3 is an alkali metal ion. 7. The method of Claim 1, wherein said amount is from 10 -9 to 10 -3 millimoles of nonamer or repeating unit per 100 cm 2 of said surface. 8. The method of Claim 1, wherein εaid proεthetic device compriεeε a structural polypeptide. 9. The method of Claim 1, wherein said incorporating involves non-covalent bonding between said chemotactic peptide and said surface. 10. The method of Claim 1, wherein said incorporating involves covalent bonding between said chemotactic peptide and said surface. ιι. The method of Claim 10 wherein said surface compriseε a εtructural peptide. 12. A proεthetic device wherein a εurface of εaid device haε incorporated into said surface a chemotactic peptide of the formula B 1 - -(AGVPGLGVG) n ~(AGVPGFGVG) m "Y-B 2 wherein A iε a peptide-forming residue of L-alanine; P iε a peptide-forming residue of L-proline; G is a peptide-forming residue of glycine; V is a peptide-forming residue of L-valine; F is a peptide-forming residue of L-phenylalanine; L is a peptide-forming residue of L-leucine; B 1 is H or a biocompatible N-terminal group; B 2 is OH, OB 3 where B 3 is a non-toxic metal ion, or a biocompatible C-terminal group: X is GVPGFGVG, GVPGLGVG, VPGFGVG, VPGLGVG, PGFGVG, PGLGVG, GFGVG, GLGVG, FGVG, LGVG, GVG, VG, G or a covalent bond; Y is AGVPGFGV, AGVPGLGV, AGVPGFG, AGVPGLG, AGVPGF, AGVPGL, AGVPG, AGVP, AGV, AG, A or a covalent bond; n is an integer from 0 to 50; m is an integer from 0 to 50; with the proviso that when both n and m are 0, X and Y are selected so that the chemotactic peptide has at least 3 amino acid residues in the X and Y positions combined. 13. The device of Claim 12, wherein n is from 1 to 10 and m is 0 to 10. 14. The device of Claim 12, wherein n is about 5 and m is 0 to 5. 15. The device of Claim 12, wherein n is 1 and m is 0. 16. The device of Claim 12, wherein said peptide is H-GFGVGAGVP-OH or a salt thereof. 17. The device of Claim 12, wherein B 1 is H and B 2 is OH or OB 3 where B 3 is an alkali metal ion. 18. The device of Claim 12, wherein said amount iε from 10 ~9 to 10 ~3 millimoleε of nonamer of repeating unit per 100 cm 2 of εaid εurface. 19. The device of Claim 12, wherein said prosthetic device compriseε a εtructural polypeptide. 20. The device of Claim 12, wherein said chemotactic peptide is incorporated using non-covalent bonding between said chemotactic peptide and said surface. 21. The method of Claim 12, wherein said chemotactic peptide is incorporated using covalent bonding between said chemotactic peptide and said surface. 22. The device of Claim 21, wherein said surface comprises a structural peptide.

Inventors: LONG MARIANNA, URRY DAN W, LONG, MARIANNA, URRY, DAN, W.
Applicants: UAB RESEARCH FOUNDATION
Application year: 1989
Main classification: A61F2
IPC codes: A61L27, C07K14