Preparation process for toner polymer

Abstract: A process for the preparation of a toner polymer which comprises the steps of carrying out suspension polymerisation of a monomer having a polymerisable vinyl group in the presence of polyvinyl alcohol as a dispersant, and then conducting oxidative decomposition of polyvinyl alcohol anchored to polymer particles obtained by suspension polymerisation.

Description: The present invention relates to a process for the preparation of a toner polymer, and more particularly to a preparation process for a toner polymer which has good moisture resistance, can maintain constant electrostatic friction over a long period and has a long service life. Various conventional polymerisation process have been proposed for making dry toners. The preparation processes include suspension polymerisation, bulk polymerisation, desolvation after solution polymerisation and salting-out after emulsion polymerisation. Suspension polymerisation is generally the most economic process. In conventional suspension polymerisation using a dispersant, the dispersant will to a certain degree remain anchored on the surface of polymer particles, despite thorough washing after polymerisation. When a toner is prepared using these polymer particles as a raw material, the remaining dispersant causes an adverse effect on such toner properties as moisture resistance, stability of electrostatic charge and fixing ability. Hence, the dispersant leads to problems in the deterioration of image quality when the toner is used at increased temperatures or high humidity and the number of duplication cycles is increased. Some improvement can be achieved by using a nonionic dispersant in place of the conventionally used anionic or cationic dispersant for suspension polymerisation but improvements to date are still unsatisfactory. An object of this invention is to provide a low cost preparation process for a toner polymer containing almost no dispersant. Another object of this invention is to provide a toner which has good moisture resistance and electrostatic charge stability and is capable of retaining a good image quality over a long period even when recycled. According to the present invention a suitable toner polymer can be prepared by a process comprising: carrying out a suspension polymerisation of a monomer having a polymerisable vinyl group in the presence of a polyvinyl alcohol dispersant wherein the monomer for suspension polymerisation is one or more monomers selected form the group consisting of styrene, styrene derivatives, α-fluoroacrylic acid esters, (meth)acrylic acid esters, vinyl esters, (meth)acrylic acids and (meth) acrylic acid derivatives; and after the polymerisation has been completed, applying an oxidising agent to said polyvinyl alcohol anchored to polymer particles obtained by said suspension polymerisation to carry out an oxidative decomposition of said polyvinyl alcohol. The invention also includes a process for preparation of a toner comprising carrying out a suspension polymerisation of a monomer having a polymerisable vinyl group, in the presence of a polyvinyl alcohol dispersant; followed by oxidative decomposition of said polyvinyl alcohol anchored to polymer particles obtained by said suspension polymerisation to produce a toner polymer and then; mixing the toner polymer with a colouring and/or charge control additive. Suitable monomers for the process are monomers having a polymerisable vinyl group and that can conduct radical polymerisation in a suspended state. Examples include styrene, α-methylstyrene and styrene derivatives having substituents such as the o-methyl group, m-methyl group, p-methyl group, p-ethyl group, 2,4-dimethyl group, p-butyl group, p-hexyl group, p-octyl group, p-nonyl group, p-decyl group, p-methoxy group and p-phenyl group; α-fluoroacrylic acid esters and (meth)acrylic acid esters represented by the formula CH₂=CR-COOR', wherein R is a hydrogen atom, fluorine atom or methyl group and R' is a monovalent group such as a methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, tert-butyl group, n-pentyl group, n-hexyl group, n-octyl group, 2-ethylhexyl group, n-nonyl group, isononyl group, decyl group, dodecyl group, tridecyl group, stearyl group, docosyl group, cyclohexyl group, benzyl group, phenyl group, methoxyethyl group, ethoxyethyl group, butoxyethyl group, fluoroalkyl group and phenoxyethyl group; vinyl esters such as vinyl acetate and vinyl propionate; (meth)acrylic acids; and acrylic acid derivatives and methacrylic acid derivatives such as acrylonitrile and methacrylonitrile. The monomer may be used singly or in combination. Representative examples of two or more monomers include monomer mixtures containing such principal components as styrene and/or derivatives thereof, and alkyl (meth)acrylates and/or α-fluoroacrylic acid esters. No particular restriction is imposed on the polymerization initiator for use in the suspension polymerization of this invention. Known initiators which may be used include, for example, di-tert-butyl peroxide, tert-butyl cumyl peroxide, dicumyl-peroxide, acetyl peroxide, isobutyryl peroxide, octanoyl peroxide, decanoyl peroxide, lauroyl peroxide, 3,5,5-trimethylhexanoyl peroxide, benzoyl peroxide, m-tolyl peroxide, tert-butylperoxy acetate, tert-butylperoxy isobutyrate, tert-butylperoxy pivalate, tert-butylperoxy neodecanoate, cumylperoxy neodecanoate, tert-butylperoxy 2-ethylhexanoate, tert-butylperoxy 3,5,5-trimethylhexanoate tert-butylperoxy laurate, tert-butylperoxy benzoate, tert-butylperoxy isopropyl carbonate, azobisisobutyronitrile and 2,2'-azobis-(2,4-dimethylvaleronitrile). These initiators may be used singly or in combination. Preferred initiators among these compounds are octanoyl peroxide, decanoyl peroxide, lauroyl peroxide, benzoyl peroxide, m-toluyl peroxide and azobisisobutyronitrile. These preferred initators provide prolonged activity during monomer polymerisation and the polymerisation is completed in a relatively short time. The dispersant to be used in the suspension polymerisation may be any known dispersant, for example, completely saponified polyvinyl alcohol, partially saponified polyvinyl alcohol and other modified polyvinyl alcohols. The polyvinyl alcohol is used in an amount required for substantially complete polymerisation but without coagulation of the polymer particles formed during polymerisation. The amount is generally from 0.01 to 5 parts by weight, preferably from 0.05 to 2 parts by weight, per 100 parts by weight of water. Additional dispersants which may be used in combination, if necessary, are electrolytes such as sodium chloride, potassium chloride, sodium sulfate and potassium sulfate. The reaction conditions for the suspension polymerisation of this invention are dependent on the kind of monomer to be polymerised and the kind and amount of polymerisation initiator. The reaction temperature is generally from 50 to 130°C, preferably from 70 to 100°C. The reaction time is suitably from 1 to 10 hours. The particle size of the polymer obtained by suspension polymerisation is from 0.5µm to 5mm, preferably from 50µm to 1mm. The polymer particles obtained by suspension polymerisation are generally solids in the form of beads and have substantially no pores. Such bead-like polymer particles are preferred because almost no polyvinyl alcohol is included in the interior of the polymer particles. Ordinary post-treatment procedures such as cooling , washing and drying are optionally carried out after completing polymerisation. Preferably, a washing step is included in the process as this removes polyvinyl alcohol from the surface of the particles and the efficiency of the oxidising agent is enhanced in the subsequent oxidative decomposition step. However, some polyvinyl alcohol may be anchored like a graft on the surface of the polymer particles and this cannot be removed by ordinary washing alone. Consequently, the oxidative decomposition step is carried out as described below. An oxidising agent which is known to break the principal chain of polyvinyl alcohol by preferentially oxidising and decomposing the 1,2-glycol bond is used to react with the anchored polyvinyl alcohol groups so that they are oxidatively decomposed. The oxidation treatment of the polymer particles may be carried out only so long as the characteristics of the toner polymer will not be impaired. Exemplary known oxidizing agents which can be used include periodic acid, periodate, dichromate, permanganate, persulfate, hydrogen peroxide, cerium (IV) salt, thallium (III) salt, cobalt (III) salt and chloric acid. No particular restriction is imposed on the oxidative decomposition step using the oxidizing agent so long as the principal chain of the polyvinyl alcohol can be broken in the step described above. For example, polymer particles may be added to a solution of the oxidizing agent and stirred at room temperature. When the treatment is carried out using an aqueous solution of suitable oxidizing agents such as those illustrated above, the principal chain of anchored polyvinyl alcohol can be broken without impairing the characteristics required for the toner polymer. The polyvinyl alcohol is broken down to low molecular weight compounds, and this reduces the amount of polyvinyl alcohol adhered to the surface of the polymer particles and the decomposed materials readily dissolve in the aqueous solution of the oxidizing agent. The solvent for the oxidizing agent of this invention is preferably water or a water-base solvent, in view of the easy dissolution of the decomposed materials. The amount of the oxidizing agent for use in the above step depends on the kind of oxidizing agent and polyvinyl alcohol, and is preferably at least 0.01 part by weight per 100 parts by weight of polyvinyl alcohol. No particular restriction is imposed on the concentration of the oxidising agent in water or the water-base solvent. In general, the solution of the oxidising agent is used in an amount of approximately 200 parts by weight per 100 parts by weight of the polymer particles, generally from 100 to 300 parts by weight per 100 parts by weight of the polymer particles. After finishing the oxidative decomposition step, conventional washing, dehydration and drying may be carried out, and the toner polymer is obtained. Preparation of the toner from the polymer can be carried out according to conventionally known methods. No particular limitation is placed on the methods. For example, the toner composition can be prepared my mixing and kneading the toner polymer with a desired amount of various additives for coloring and charge control. The toner composition thus obtained can, for example, be pulverised to provide the toner. Exemplary additives which may be mentioned include carbon black, iron black, graphite, nigrosine, metal complexes of monoazo dyestuffs, ultramarine blue, phthalocyanine blue, Hanza yellow, benzidine yellow, and various lake pigments such as quinacridone pigments. In the toner composition, other common polymers may be used in combination with the polymer of this invention but as minor ingredients relative to the polymer of this invention. Exemplary common polymers which can be added include silicone resin, polyester, polyurethane, polyamide, epoxy resin, polyvinyl butyral, rosin, modified rosin, terpene resin, phenol resin, aliphatic or alicyclic hydrocarbon resin, aromatic petroleum resin, chlorinated paraffin and paraffin wax. The toner can also contain magnetic fine particles including metals such as iron, manganese, nickel, cobalt and chromium; magnetite; hematite; various ferrites; manganes alloys and other ferromagnetic alloys. These fine particles may have an average particle size of 0.05 to 5 µm, preferably 0.1 to 2 µm. The content may be from 15 to 70% by weight, preferably from 25 to 45% by weight per total weight of the toner. Additionally, the toner may contain from 10 to 40% by weight of a fluidity improver such as a hydrophobic colloidal silica. The fluidity improver may also be used by simply mixing with the powder of the resin composition in an amount of 0.5 to 5% by weight per weight of the resin composition. The present invention will hereinafter be illustrated by way of examples. Part means part by weight in the following description. The term "fog" means a phenomenon wherein black spots appear in addition to printed characters on a copied paper or the image becomes lighter with an increase in duplication cycles. Example 1 In a monomer mixture containing 83 parts of styrene, 17 parts of 2-ethylhexyl acrylate and 0.3 part of divinylbenzene, 3 parts of benzoyl peroxide was dissolved as an initiator. The solution was added with stirring to a mixture containing 0.2 part of a partially saponified polyvinyl alcohol dispersant (GOSENOL GH-20™, a product of Nippon Synthetic Chemical Industry Co., Ltd.) in 220 parts of deionized water. The temperature was raised to 92°C and then suspension polymerization was carried out for 90 minutes. The suspension obtained was cooled to room temperature, washed and dehydrated. The bead-like polymer particles thus obtained had a particle size of about 250 µm. Subsequently, the above bead-like polymer particles were added to a solution containing 2 x 10⁻⁴ part of sodium periodate dissolved in 200 parts of water and stirred at room temperature for an hour. Thereafter, the polymer particles were thoroughly washed, dehydrated and dried. The bead-like polymer particles which had anchored polyvinyl alcohol removed by oxidative decomposition were thus obtained. A mixture of 92 parts of the polymer particles thus obtained, 7 parts of carbon black (#40 TM , a product of Mitsubishi Kasei Corp.) and 1 part of a charge controller (BONTRON S-34 TM , a product of Orient Kagaku Kogyo K.K.) was kneaded at 150°C for 5 minutes with a twin screw extruder, cooled and pulverized with a jet mill. The resulting toner had particle sizes of 5 to 15 µm. The toner thus obtained was subjected to a duplication test by using a commercial copying machine (RICOPY FT-4510 TM , a product of Ricoh Co., Ltd.). A clear image having high resolution without fog could be obtained even after copying 20,000 sheets of paper. The above toner was again added to the above copying machine and allowed to stand for 8 hours in an atmosphere having an increased temperature of 35°C and a high relative humidity of 85%. Then the same duplication test was carried out and a clear image having high resolution without fog could be obtained. Example 2 Polymer particles were obtained, a toner was prepared and a duplication test was carried out by the same procedures as conducted in Example 1, except that 2 x 10⁻⁵ part of sodium periodate was used. As a result, in a duplication test under ordinary conditions, a clear image having high resolution without fog could be obtained from the first to 10,000th sheet of paper. However, the image was very slightly fogged and resolution was somewhat lowered after duplicating 20,000 sheets of paper. Nevertheless, the deterioration caused no problem in practical use. In the same duplicaltion test conducted under increased temperature and high humidity, a good image quality was also obtained, although the image obtained was very slightly fogged. There was also no problem in practical use. Comparative Example 1 A toner was prepared and a duplication test was carried out by using the same procedures as conducted in Example 1, except that the oxidative decomposition step was omitted. As a result, in a duplication test under ordinary conditions, a clear image having high resolution without fog could be obtained in the initial stage of duplication. However, the image obtained after duplicating about 10,000 sheets of paper resulted in fogging and decreased in resolution. In a duplication test conducted under increased temperature and high humidity, the image obtained was severely fogged and could not be used. Referential Example 1 Polymer particles were obtained, a toner was prepared and a duplication test was carried out by the same procedures as conducted in Example 1, except that 2 x 10⁻⁶ part (0.001 part per 100 parts of the above polyvinyl alcohol dispersant) of sodium periodate was used. As a result, in the duplication test under ordinary conditions, a clear image having high resolution without fog could be obtained in the initial stage of duplication. However, the image obtained after duplicating 10,000 sheets of paper resulted in a certain amount of fog and decreased in resolution. In a duplication test conducted under increased temperature and high humidity, the image obtained was also fogged and decreased in resolution. The results which were inferior to the examples to a certain degree are believed to result from the fact that oxidative decomposition was insufficient for polyvinyl alcohol anchored to the polymer particles.

Claims: A process for preparation of a toner polymer comprising: carrying out a suspension polymerisation of a monomer having a polymerisable vinyl group in the presence of a polyvinyl alcohol dispersant wherein the monomer for suspension polymerisation is one or more monomers selected from the group consisting of styrene, styrene derivatives, α-fluoroacrylic acid esters, (meth)acrylic acid esters, vinyl esters, (meth)acrylic acids and (meth)acrylic acid derivatives; and after the suspension polymerisation has been completed, applying an oxidising agent to said polyvinyl alcohol anchored to polymer particles obtained by said suspension polymerisation to carry out an oxidative decomposition of said polyvinyl alcohol. A process according to claim 1 wherein the polyvinyl alcohol is used in an amount of 0.01 to 5 parts by weight per 100 parts by weight of water used for the suspension polymerisation. A process according to claim 1 or claim 2 wherein the polymer particles are bead-like particles having a particle size of 0.5µm to 5mm. A process according to any preceding claim wherein the oxidative decomposition is conducted by adding the polymer particles to a solution of an oxidising agent. A process according to any preceding claim wherein the oxidising agent is one or more oxidising agents selected from the group consisting of periodic acid, periodate, dichromate, permanganate, persulfate, hydrogen peroxide, cerium (IV) salt, thallium (III) salt, cobalt (III) salt and chloric acid. A process according to any preceding claim wherein the amount of the oxidising agent is 0.01 part by weight or more per 100 parts of the polyvinyl alcohol used in the suspension polymerisation. A process for preparation of a toner comprising carrying out a suspension polymerisation of a monomer having a polymerisable vinyl group, in the presence of a polyvinyl alcohol dispersant; followed by oxidative decomposition of said polyvinyl alcohol anchored to polymer particles obtained by said suspension polymerisation to produce a toner polymer and then; mixing the toner polymer with a colouring and/or a charge control additive. A process according to claim 7 when dependent on any of claims 2 to 6.

Inventors: FUNATO RYO C O PRODUCTS DEV LA, INAGAKI MOTOSHI C O PRODUCTS D, KUBO SHINJI C O TOYOHASHI PLAN, TAKAHIRO SYUJI C O PRODUCTS DE, YOSHIDA KEIJI C O PRODUCTS DEV, FUNATO, RYO C/O PRODUCTS DEV. LAB. MITSUBISHI, INAGAKI, MOTOSHI C/O PRODUCTS DEV. LAB. MITSUBISHI, KUBO, SHINJI C/O TOYOHASHI PLANTS MITSUBISHI, TAKAHIRO, SYUJI C/O PRODUCTS DEV. LAB. MITSUBISHI, YOSHIDA, KEIJI C/O PRODUCTS DEV. LAB. MITSUBISHI
Applicants: MITSUBISHI RAYON CO, MITSUBISHI RAYON CO., LTD.
Application year: 1989
Main classification: C08F8
IPC codes: C08F2, G03G9, C08F8