Polymer material based on a high-impact polyphenylene ether mixture

Abstract: The invention relates to a polymer material based on a high-impact polyphenylene ether mixture which comprises as a flame retardant 5-20% by weight - related to the polymer component - of a mixture of aluminium- or lithium-methyl-methyl phosphonate and a tetra-aryl phenylene diphosphate.

Description: The invention relates to a polymer material based on a high-impact polyphenylene ether mixture which comprises 20% by weight - related to the polymer component - of a mixture of aluminium- or lithium-methyl-methyl phosphonate and a phosphate as a flame retardant. Polyphenylene ether containing diphenyl dicresyl resorcin diphosphate is disclosed in JP-A-1982-207 642. In so far as aluminium-methyl-methyl phosphonate is used, such mixtures are known from EP-A-0 245 207, in which the combination with phosphates is stated on page 7, first full paragraph. For the lithium salt a possible combination with other flame retardants is revealed in Applicants' non-pre-published Netherlands Patent Application 8703025. It has been found, however, that such combinations with simple triaryl phosphates, for example, triphenyl phosphate or isopropylated and/or butylated triphenyl phosphate, still leave to be desired as regards their flame retarding effect and in addition show other undesired properties, for example, a deformation temperature which is higher than is commercially desired and furthermore side phenomena in the injection moulding process, in particular the formation of cracks and the so-called "juicing", i.e. the volatilisation and recondensation on the workpiece of a volatile component. It has been found surprisingly that a better flame resistance is obtained with a special choice of the phosphate component, while the disadvantages mentioned hereinbefore do not occur. The invention therefore relates to a polymer material of the type mentioned in the opening paragraph which is characterised in that the phosphate is a tetra-aryl phenylene diphosphate. The high-impact polyphenylene ether mixture may be one of the conventional mixtures, for example, a mixture of polyphenylene ether with high-impact polystyrene or a mixture of polyphenylene ether with EPDM-rubber. The aluminium- or lithium-methyl-methyl phosphonate is preferably present in a quantity of 2-10% by weight related to the polymer component. The tetra-aryl penylene diphosphate is preferably present in a quantity of 5-15% by weight related to the polymer component. Tetra-aryl metaphenylene diphosphate, in particular the commercial products CR 733, cresyl-triphenyl-resorcinol diphosphate and CR 733 S, tetraphenyl-resorcinol diphosphate have proved to be particularly suitable. The materials of the invention may moreover comprise one or more additives conventionally used for such materials, for example, fillers, reinforcing fibres, stabilisers, pigments and dyes, plasticisers, mould release agents and agents to improve the notch impact value. The flame retardants of the invention can simply be incorporated in the basic material by mixing at any desired instant. The invention will now be described in greater detail with reference to the ensuing specific examples. In these examples the following abbreviations are used: PPO® = polyphenylene ether HIPS = high-impact polystyrene AMMP = aluminium-methyl-methyl phosphonate HDT = deformation temperature EXAMPLE 1 PPO®-HIPS materials were prepared containing the commercial product CR 733 and/or AMMP described above. The compositions of these materials and the test results obtained therewith are as follows: Test 1 2 3 PPO® 35 35 35 HIPS 65 65 65 CR 733 18 - 13 AMMP - 18 5 HDT,°C 82 129 96 Melt viscosity (PaS) 106 185 128 UL-94, evaluation V1 V0 V0 "Juicing"/crack formation during injection moulding moderate none none An HDT between 90 and 100° C is most desirable for practical purposes. The material according to the invention satisfies this desire. The material with exclusively CR 733 does not reach the V0 evaluation in the UL-94 test and gives too much juicing and crack formation; the material with exclusively AMMP is not satisfactory as regards its HDT and melt viscosity. The melt viscosity was determined at 280° C, the temperature of injection moulding, and with a shear rate of 1500 sec.⁻¹. EXAMPLE 2 Comparative experiments were carried out with the commercial product Reofos® 50, a mixture of triphenyl phosphate and isopropylated triphenyl phosphate. Incorporated in this test were furthermore the above-described commercial products CR 733 and CR 733 S. The composition of the various materials and the test results obtained therewith are as follows. Test 4 5 6 7 8 PPO® 30 30 30 30 30 HIPS 70 70 70 70 70 Reofos 50 - 15 10 - - CR 733 - - - 10 - CR 733 S - - - - 10 AMMP 15 - 5 5 5 HDT, °C 123 78 93 97 96 Melt viscosity (PaS) 165 65 102 110 107 UL-94, evaluation V0 V1 V1 V0 V0 Average extinction time over 10 ignitions, sec. 4 12 5 2 2.4 "Juicing"/crack formation no yes yes no no It will be seen immediately that good results in the UL-94 test in combination with other favourable properties are obtained with the two materials of the invention. The only other test in which the UL-94 evaluation reached V0 is that with exclusively AMMP, but then HDT and melt viscosity are not satisfactory.

Claims: A polymer material based on a high-impact polyphenylene ether mixture which comprises 5-20% by weight - related to the polymer component - of a mixture of aluminium- or lithium-methyl-methyl phosphonate and a phosphate as a flame retardant, characterised in that the phosphate is a tetra-aryl phenylene diphosphate. A polymer material as claimed in Claim 1, characterised in that the polyphenylene ether mixture is a mixture comprising high-impact polystyrene. A polymer material as claimed in Claim 1, characterised in that the polyphenylene ether mixture is a mixture comprising EPDM-rubber. A polymer material as claimed in Claims 1-3, characterised in that the aluminium- or lithium-methyl-methyl phosphonate is present in a quantity of 2-10% by weight related to the polymer component. A polymer material as claimed in Claims 1-4, characterised in that the tetra-aryl phenylene phosphate is present in a quantity of 5-15% by weight related to the polymer component. A polymer material as claimed in Claims 1-5, characterised in that the tetra-aryl phenylene diphosphate is a tetra-aryl metaphenylene diphosphate.

Inventors: CLAESEN CHRISTIANUS ADRIANUS A, LOHMEIJER JOHANNES HUBERTUS GA, CLAESEN, CHRISTIANUS ADRIANUS ARNOLDUS, LOHMEIJER, JOHANNES HUBERTUS GABRIEL
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1989
Main classification: C08K5
IPC codes: C08L23, C08K5, C08L71, C08L25