Crosslinked siloxane-urethane polymer contact lens

Abstract: A contact lens is described which is synthesized by reaction in a mold of an isocyanate capped poly(dialkylsiloxane) prepolymer with a poly(dialkylsiloxane) di- or polyalkanol. The clear polyurethane rubber contact lens is readily made completely wettable by a transfer-grafting process or post-­ treatment and has a high oxygen permeability.

Description: From the standpoint of comfort, durability and optical performance, an ideal contact lens should be soft, very wettable yet low in bulk water content, clear and have an oxygen permeability greater than 50 [barrers]. In present day soft contact lenses comfort and wettability are achieved by using hydrogels with 30-80 % water content, but at the expense of limited oxygen-permeability, physical strength and formation of protein-deposits. High oxygen permeability is achieved in contact lenses made entirely from silicone rubber, as described for instance in U.S. Patent No. 3,996,187, but at the expense of wettability. In addition, silicone rubber, because of its greater inherent hydrophobicity and chain mobility, rapidly and tenaciously interacts with lipids in the tear liquid, resulting in quick dewetting and potential adhesion to the cornea. It would be highly desirable to produce a contact lens composed entirely of silicone rubber since it offers the highest oxygen permeability of all presently available materials. The enhancement of eye comfort and long wear capability would represent a significant improvement in contact lens development. Silicone rubber lenses, although possessing high oxygen permeability, suffer from poor comfort characteristics because they are not soft enough to conform to the cornea in the same way a typical hydrogel lens does. Onthe other hand, silicone-free polyurethane rubbers are known for their excellent bio-compatibility, as examplifiedby the use of BIOMER - a linear polyurethane rubber - to coat artificial hearts to reduce blood clotting. Silicone rubbers are made by crosslinking liquidpolysiloxanes. These rubbers are thermoset polymers which can be made to varying degrees of hardness and elasticity by controlling the degree of crosslinking and the molecular weight of the silicone fluid. Silicone rubber is usually made by vulcanizing polydimethylsiloxane fluids with organic peroxides at elevated temperatures. Another approach to crosslinking employs hydrosilation in which poly(vinylalkyl siloxanes) are cured with poly(hydridoalkylsiloxanes) in the presence of transition metal catalysts. Silicone rubber has also been formed by chemically reacting, α,ω-difunctional poly(diorganosiloxanes) with polyfunctional silanes and siloxanes. Typically the crosslinking reaction is acondensation which formsa siloxane bond a volatileby-product. Common examples of this type of cure reaction are silanolalkoxylsilane (French Pat. 1,042,019), silanol-acetoxysilane (German Appl. 1,121,803), silanol-silane (Brit. Pat. 804,199), and silanol-silanol (via the correspondingacetoneoxime) (Belg. Pat. 614,394). Suitable catalysts for these reactions are amines and carboxylic acid salts of Sn, Pb, Zn, Sb, Fe, Cd, Ba, Ca and Mn. Organosiloxane isocyanates have been prepared (U.S. Patent 3,179,622) which vulcanize when exposed to moisture. In these cases the isocyanate group is joined to the siloxane through an alkyl group, rendering it unhydrolyzable. Besides moisture cured polyurethanes, silicone rubber, which are 2-component polyurethanes are conveniently prepared by reaction of di-, tri- or tetra hydroxyalkyl-substituted polysiloxanes with di-isocyanates, using the well known techniques of conventional polyurethane synthesis. Most commonly these polyhydroxyalkyl-polysiloxanes are used as additives to conventional polyurethane formulations, for instance to regulate pore size in polyurethane foams, to impart lubricity or gloss to polyurethane coatings or achieve water repellency. The silicone rubbers, which are described for use as soft, oxygen permeable contact lenses, are obtained by hydrosilation reaction between poly-(vinyl-alkyl siloxanes) and poly-(hydridoalkyl siloxanes), as described in U.S. Patent No. 3,996,187. Silicone rubber like materials for use as soft contact lenses which are free-radical polymerized copolymers of methacrylate-functionalized polydimethylsiloxanes have also been described in U.S. Pat. No. 4,605,712. EP-A-109,355 discloses strong, silicone containing polymers with high oxygen permeability obtained by copolymerization of (A) 8 to 70 % of a polysiloxane containing at least two terminal or pendant, polymerizable, vinyl groups which are attached to the polysiloxane through at least two urethane, thiourethane, urea or amide linkages, and (B) 30 to 92 % of a mono- or divinyl compound or a mixture of such monomers consisting of 85 to 100 % of water insoluble monomers. These polymers are useful in the preparation of hard or soft contact lenses. Crosslinking in these polymers is effected by the vinyl groups present in both components (A) and (B). It has now been found that polysiloxane-polyurethane rubbers also make excellent soft contact lens material, combining clarity, high elongation and softness with exceptional oxygen-permeability. Such contact lenses, which are entirely based on poly(dialkylsiloxane) di- or tri-alkanols and diisocyanates have not been described before. All silicone containing contact lens materials, be they conventional silicone rubbers or the polysiloxane-polyurethanes of this invention are extremely hydrophobic and attract lipid deposits when worn in the eye. In order to overcome the hydrophobic nature of silicone rubber, silicone rubber lenses, such as SILSOFT (DOW-CORNING) have to be surface treated to render them wettable. Numerous such surface treatments have been described: Relevant United States patents in this area include: U.S. 3,925,178 describes surface treatment by water-vapor subjected to an electrical discharge. U.S. Patent No. 4,099,859 describes grafting a hydrophilic polymer onto a silicone-rubber contact lens by coating the lens with a hydrophilic monomer followed by exposure to UV. U.S. Patent No. 4,229,273 describes grafting of a acrylic polymer onto a silicone rubber lens pre-irradiated in the presence of oxygen. U.S. Patent No. 4,168,112 describes the formation of a poly-electrolyte complex on the surface of a contact lens in order to render it more hydrophilic and comfortable to wear. U.S. Patent No. 4,217,038 describes the formation of a glass-coating on a silicone contact lens to improve wettability. U.S. Patent No. 4,409,258 describes a hydrophilizing treatment of contact lenses by bombardment with nitrogen and oxygen ions. U.S. Patent No. 4,388,164 describes coating the surface of a silicone rubber with a thin metal film by vacuum decomposition in the stretched state. U.S. Patent No. 4,332,922 describes hydrophilization of silicone contact lenses by a gas-discharge. U.S. Patent No. 4,143,949 describes putting a hydrophilic coating onto a hydrophobic contact lens by radiation induced polymerization. U.S. Patent Nos. 4,311,573 and 4,589,964 describe hydrophilization of hydrophobic polymer by ozone treatment, followed by a grafting of vinyl monomers through decomposition of the formed peroxy groups. Although these methods allow fabrications of wettable silicone rubber lenses, most of them have major drawbacks; for instance polymerizations can occur not only on the surface, but also in the liquid polymerization medium. Also, because the graft-polymerization depends on active centers, which decompose at different times, inhomogeneous surfaces result because of preferential absorption of monomer into already modified surface regions. In cases where exact depth-control and uniformity of the grafted region is important, such as for example in the surface modification of contact lenses, such uncontrollable grafting reactions are not acceptable. On the other hand, if to reduce inhomogeneities grafting is carried out for a short time only, the grafted surface regions are too thin and in many applications the desired effect soon wears off. Exact control over reaction conditions is therefore very important. It has now also been discovered, that polysiloxane-polyurethane rubbers are especially well suited to make soft contact lenses not only with excellent oxygen permeability, but excellent wettability and hydrogel-like softness as well, when they are prepared in contact lens molds which have previously been coated with a ractive hydrophilic polymer, which is transfer-grafted during cure. It has been further discovered, that polysiloxane-polyurethane rubbers can be made in form of an interpenetrating polymer network (IPN) with a free-radical polymerized vinyl polymer; these IPN's are often clear and besides being highly oxygen permeable, allow the physical properties of the polysiloxane-polyurethane rubber to be varied over a wide range; they include water swellable compositions and compositions bearing polar groups which are otherwise difficult to incorporate into a polyurethane. The object of the invention is to provide an ophthalmic device, preferably a contact lens, made of crosslinked siloxane-urethane polymer. Another object of this invention is a crosslinked siloxane-urethane polymer in form of an interpenetrating polymer network with a free radical polymerized vinyl polymer. The instant invention pertains to an opthalmic device, preferably a contact lens, made of a crosslinked siloxane-urethane polymer which consists essentially of the reaction product of (A) a di- or poly-hydroxyalkyl substituted alkyl polysiloxane having a number average molecular weight between 200 and 10,000, and (B) a compatible, aliphatic, cycloaliphatic or aromatic di- or tri-isocyanate; wherein the total number of hydroxyl groups in component (A) is stoichiometrically equivalent to the total number of isocyanate groups in component (B), and with the proviso that an effective crosslinking amount of (A) or (B) or both (A) and (B) is present and possesses a functionality greater than two. Poly-functional polysiloxanes, useful as component (A) are of structures: wherein R₁ is an alkyl group of 1 to 4 carbon atoms or phenyl, R₂ is a linear or branched alkylene group with 2 to 6 carbon atoms (≡ R₂a), a polyoxyalkylene group of structure wherein R₃ is hydrogen or methyl and n is an integer from 1 to 50; x₁ and x₂ are integers from 1 to 500; y₁ is 0 to 4, y₂ is 2to 5 with the proviso that the ratios of: x 1 + x 2 y 1 y 1 + 2 and x 1 + x 2 y 2 y 2 are not greater than 70. By "compatible" is meant that component (B) is reactable with component (A) to yield a reaction product which is substantially optically clear. Diisocyanates or triisocyanates (B) useful as such or to form a prepolymer intermediate are aliphatic, cycloaliphatic or aromatic polyisocyanates. Said aliphatic di- or triisocyanates are e.g. alkyl di- or triisocyanates having up to 12 alkyl carbon atoms, preferably having 2 to 9 alkyl carbon atoms, wherein alkyl is e.g. ethyl, propyl, hexyl or trimethylhexyl. Said cycloaliphatic di- or triisocyanates are e.g. cycloalkyl di- or triisocyanates having up to three C5 or C6 cycloalkyl or cycloalkenyl groups which are unsubstituted or substituted by lower alkyl and/or carboxy, including cycloalkyl lower alkyl, unsubstituted or substituted by e.g. lower alkyl, di-or triisocyanates. In case that more than one cycloalkyl group is present, these are connected to each other by a bond, lower alkylene, or a urethane group. Said aromatic di- or triisocyanates are e.g. di- or triisocyanates having a naphthalene or up to three phenyl groups, which are unsubstituted or substituted by lower alkyl, halogen, or lower alkoxy, e.g. methyl, chloro, or methoxy. In case that more than one phenyl group is present these are connected to each other by a bond, lower alkylene, or lower alkylidene or oxygen. Component (B) is preferably a diisocyanate, triisocyanate or mixture thereof selected from ethylene diisocyanate, 1,2-diisocyanatopropane, 1,3-diisocyanato-propane, 1,6-diisocyanatohexane, 1,2-diisocyanatocyclohexane, 1,3-diisocyanatocyclohexane, 1,4-diisocyanatobenzene; bis (4-isocyanatocyclohexyl)methane, bis (4-isocyanatocyclohexenyl)methane, bis(4-isocyanatophenyl)methane, 1,2-and 1,4-toluene diisocyanate; 3,3-dichloro-4,4'-diisocyanatobiphenyl; tris(4-isocyanatophenyl)methane, 1,5-diisocyanatonaphthalene, hydrogenated toluene diisocyanate; 1-isocyanatomethyl-5-isocyanato-1,3,3-trimethylcyclohexane (= isophorone diisocyanate); 1,3,5-tris(6-isocyanatohexyl)biuret, 1,6-diisocyanato-2,2,4-(2,4,4)-trimethylhexane, 2,2'-diisocyanatodiethyl fumarate; 1,5-diisocyanato-1-carboxypentane; 1,2-, 1,3-, 1,6-, 1,7-, 1,8-, 2,7- and 2,3-diisocyanatonaphthalene; 2, 4- and 2,7-diisocyanato-1-methylnaphthalene; 1,4-diisocyanato-methylcyclohexane; 1,3-diisocyanato-6(7)-methylnaphthalene; 4,4'-diisocyanatobiphenyl; 4,4'-diisocyanato-3,3'-dimethoxy-bisphenyl; 3,3'- and 4,4'-diisocyanato-2,2'-dimethyl biphenyl; bis-(4-isocyanatophenyl)ethane; bis (4-isocyanatophenyl)ether. The most preferred diisocyanates are isophorone diisocyanate, 2,2,4-(2,4,4)-trimethylhexane-1,6-diisocyanate or 1,2- or 1,4-toluene diisocyanate. In a preferred embodiment of the instant invention the di- or triisocyanate (B) or mixture of said isocyanates is reacted with approximately half the equivalent amount of the polysiloxane-polyalkanols of structure, A1, A2 or A3 to form an isocyanate capped prepolymer, which is subsequently reacted with the remaining half equivalents of polysiloxane-polyalkanol to form the crosslinked polysiloxane-polyurethane. Some preferred compositions consist of polyurethanes where (A) is of structure A1, where y₁ is zero to 1, x₁ is 5-50, x₂ is 5-50, R₁ is methyl, R₂ is propylene, butylene, 1-methyl propylene or and the diisocyanate (B) is isophorone diisocyanate (IPDI) or 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate (TMDI). Other preferred compositions consist of polyurethanes where (A) contains 40-60 equivalent percent of polysiloxane-tetrols of structure A3, and diisocyanate (B) is IPDI or TMDI. Most preferred are compositions where (A) contains 40-60 equivalent percent of polysiloxane diols of structure A1, where y₁ is zero or 1, x₁ is 1-5, x₂ is 1-5, R₁ is methyl, R₂ is propylene or butylene, and the diisocyanate (B) is IPDI or TMDI. Other most preferred compositions are where (A) contains 40-60 equivalent percent of polysiloxane tetrols A3, where x₁ is 10-50 and R₁ is methyl, and 40-60 equivalent percent A1, where y₁ is zero, x₁ is 15-60, R₁ is methyl, R₂ is propylene, 1-methylpropylene, or and (B) is isophorone diisocyanate or 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate. The compatible, interpenetrating-polymer-network compositions of the instant inventions comprise (I) 95-50 %, preferably 95-75 %, by weight of the total composition of a siloxane-urethane polymer formed by the reaction of (A) of di- or poly-hydroxyalkyl substituted alkylpolysiloxane having a number average molecuar weight between 200 and 10,000, and (B) a compatible, aliphatic, cycloaliphatic or aromatic di- or tri-isocyanate, wherein the total number of hydroxyl groups in component (A) is stoichiometrically equivalent to the total number of isocyanate groups in component (B), and with the proviso that an effective crosslinking amount of (A) or (B) or both (A) and (B) is present and possesses a functionality greater than two, and (II) 5-50 %, preferably 5-25 %, by weight of the total composition of a vinyl polymer or copolymer obtained by the free-radical polymerization of a vinyl monomer or mixture of vinyl monomers. Compatible in this context means that the interpenetrating network of polymers when converted into contact lenses are optically clear and not hazy. The crossliked polysiloxane-polyurethane of component (I) is prepared from components (A) and (B) which are described earlier in this application in detail. The vinyl polymers of component (II) are prepared by free-radical polymerization of the esters, including the C₁-C₂₂-linear or branched alkyl or hydroxyalkyl esters, or amides of acrylic, methacrylic or maleic acids, vinyl esters, vinyl ethers, styrene or N-vinyllactams. Preferably component (II) is prepared from a fluoroalkyl acrylate or methacrylate with 3 to 21 fluoro atoms in the fluoroalkyl group, such as heptafluorobutyl-, hexafluoroisopropyl- or R f -ethyl acrylate or methacrylatewhere R f is perfluoroalkyl of 6 to 10 carbon atoms, from an oligosiloxanylsilyl-alkyl acrylate or methacrylate with 2 to 10 Si atoms in the oligosiloxanyl group, from a hydroxyalkyl acrylate or methacrylate, N-vinylpyrrolidone, N,N-dimethylacrylamide or methyl methacrylate. Most preferred vinyl monomers for component (II) are N,N-dimethylacrylamide, methyl methacrylate, 2-hydroxyethyl methacrylate, methacryloxypropyl-tris(trimethylsiloxy)silane and tridecylfluorohexyl-ethyl methacrylate. The instant compatible interpenetrating-polymer-network compositions are useful for making ophthalmic devices, preferably contact lenses. Synthesis of the novel polysiloxane-polyurethanes follows the general procedures of polyurethane chemistry. Preferably, a prepolymer is prepared in a first step by reaction of approximately half the equivalent amount of polysiloxanepolyalkanol with the full equivalent amount of a diisocyanate; this prepolymer, which contains terminal isocyanate groups, is then in a final reaction step connected into the crosslinked polysiloxane-polyurethane rubber by mixing it with the remaining half of the polysiloxane-polyalkanol, filling it into a mold and curing it at elevated temperatures. Both reaction steps are preferably catalyzed by any of the catalysts commonly used in polyurethane chemistry, especially tin compounds like dibutyltin dilaurate (DBTL) a stannous octoate, or by tertiary amines, like triethylamine; the catalysts can be present in amounts of zero to 0.2 % (by weight). The reaction temperature can vary from 20-100°C and is preferably between 40-60°C. If polysiloxane-dialkanols are used, it is possible to carry out the first reaction step with an OH:NCO equivalent (or mol) ratio from 1:2 to 6:8 and thereby make prepolymer which contain from one to an average of 3 polysiloxane chains within their structure; if polysiloxane-tri (or tetra) alkanols are used for step 1, the molar ratios of polysiloxane-alkanol to diisocyanate can range from 1:3 (1:4) to 2:5 (2:7), thereby encompassing prepolymers with one or up to an average of two polysiloxane chains within their structure. Such chain extended prepolymers are thus withinthe scope of this invention. It is of course possible to use mixtures of polysiloxanealkanols of structures A1, A2 or A3 to make the prepolymers and the final polyurethane, as long as the basic rules of polyurethane synthesis familiar to those skilled in the art, are observed. Instead of preparing the poly-isocyanato polysiloxane prepolymers from (B) and polysiloxanes A1, A2 or A3, any of the above mentioned diisocyanates can be used by themselves, with isophorone diisocyanate and 1,6-diisocyanato-2,4,4-(2,2,4)trimethylhexane being the preferred isocyanates. It is also within the scope of this invention, to use minor amounts of polymeric diisocyanates of 500-5000 MW based on polyalkyleneether- or polyester-diol reacted with the diisocyanates listed above in combination with the isocyanato-functional polysiloxanes, as long as clear and compatible mixtures are obtained. Compatibility can often be improved by the use of compatibilizing aprotic solvents, such asN,N-dimethylformamide, N-methylpyrrolidone, dimethyl sulfoxide, isopropyl acetate, methyl ethyl ketone and the like. Solvents also facilitate removal from the mold and improve the quality of the molded lens, especially of the edges. Such solvents can be present in amounts from zero to 50 % (by weight). The preparation of the poly-(siloxane-urethane) in the presence of an aprotic solvent is thus within the scope of the invention. It is within the scope of this invention to have other reactive components present, as long as they remain compatible with the siloxane-urethane polymer and do not result in hazy or opaque lenses. Useful additional components are, for example, polyethylene oxide diols with 2-1000 repeating ether units to impart hydrophilicity to the bulk, or perfluorinated polyether diols to impart oleophobicity and resistance to protein and lipid absorption; ethylene glycol, glycerol, propylene glycol, butanediol, thio-diethylene glycol, and cationic groups containing diols such as N-methyldiethanol or N,N-bishydroxyethylpiperazine andthe like. These and other components can be either incorporated during the final cure, or by the known techniques of chain extension before the final crosslinking cure is carried out. In this manner unsaturated groups can also be incorporated, using for instance butenediol or butynediol, or maleic anhydride. Yet another extension of this invention is the synthesis of poly(siloxane-urethanes) as part of an interpenetrating-polymer-network (IPN) containing a vinyl polymer as the second component. Such polymers can be obtained by using vinyl monomers as reactive diluents and polymerizing these vinyl monomers either simultaneously with the polyurethane forming components or subsequently, using either heat, but preferably UV-activated free-radical polymerization. The contact lenses of this invention are prepared by casting in a suitable mold the polysiloxane-polyurethane prepolymer mixture consisting of approximately equivalent amounts of components (A) and (B) or other diisocyanate according to the known methods of polyurethane synthesis. The reaction mixture can be prepared by stirring A and B under a dry nitrogen blanket while simultaneously mixing in a catalyst , such as dibutyltin dilaurate (DBTL) or other catalysts used in polyurethane manufacture, including catalysts containing tert-amino groups. The amount of catalyst can range from zero to 0.2 % (by weight) and is preferably 0.01 to 0.03 % (by weight) DBTL. The molds can consist of glass, metal or plastic, such as polycarbonate or polypropylene. Preferably these molds are coated with a coreactive hydrophilic polymer like polyvinyl alcohol (PVA), ethoxylated PVA or hydroxyethyl cellulose to give a permanent hydrophilic coating on the lens. The cure is carried out at temperatures between 25 and 100°C for 1-10 hours after which the mold is taken apart and the lens removed. In the following examples Shore-A hardness is determined on 1 cm thick cast buttons. Oxygen permeability is determined with O₂-Permeometer-Model 201-T (Createch) and using buffered saline (pH = 7) as electrolyte and is expressed in units O 2 .DK barrers = cm 3 STP cm.10 -10 cm 2 .sec.cmHg Physical-mechanical measurements are carried out with an INSTRON testing apparatus, model 1123 on 0.5-1 mm thick sheets. In the following examples wettability is determined by measuring air in water contact angles by the captive bubble method (= receding angle), and water in air angles (=advancing angle) on 1 mm thick sheets after three days equilibration in distilled water. Example 1: Synthesis of Diisocyanate Prepolymer B (MW 4700) Dihydroxyalkylpolydimethylsiloxane (structure A1 with y₁ = zero, R₂ = R₂b, R₃ = methyl) (MW 4200, Mercor Inc.) (158.04g, 37.59mmole) is weighed into a three neck, 300 ml round bottom flask equipped with a mechanical stirrer, thermometer, andnitrogen inlet. Isophorone diisocyanate (16.71 g, 75.19 mmole, 3.0 equivalents) is then added and the two liquids are rapidly stirred to a colorless solution. Dibutyltin dilaurate, DBTL (41 mg, 0.02 %) is added and stirring is continued at room temperature. An exothermic reaction soon begins after the catalyst addition and peaks 55 minutes later at 33.5°C. Stirring is continued for another sixty minutes after which time the NCO level falls to 1/2 of the inital value. The prepolymer is stored at 10°C in a glass bottle undernitrogen. It has a MW (molecular weight) of 4700, by NCO-titration. Example 2: Synthesis of Diisocyanate Prepolymer B (MW 2550) Dihydroxyalkyl-polydimethylsiloxane (structure A1 with y₁ = zero, R₂ = R₂b) (MW 2100, Mercor Inc.) (176.58 g, 82.207mmole) is reacted with two equivalents of isophorone diisocyanate, (IPDI), (36.57 g, 0.1644 mole) in a 300 ml, 3 neck, round bottom flask in the manner described in example 1 using 71 mg (0.03 %) of DBTL catalyst. The prepolymer formed has a molecular weight of 2550 by NCO titration and is stored in a glass bottle at 10°C undernitrogen. Example 3: Synthesis of Diisocyanate Prepolymer B (MW 1400) Dihydroxyalkyl-polydimethylsiloxane (structure A1 with y₁ = zero, R₂ = R₂b) (MW 1000, Mercor Inc.) (116.84 g, 0.1117 mole) is reacted with two equivalents of isophorone diisocyanate, IPDI, (51.90 g, 0.2330 mole) in a 300 ml, 3 neck, round bottom flask with 90 mg (0.08 %) DBTL catalyst in the manner described in example 1. The prepolymer formed has a molecular weight of 1400 by NCO titration and is stored in a glass bottle at 10°C under nitrogen. Example 4: Synthesis of Tri-isocyanate Prepolymer B from Tri-hydroxyalkyl (polydimethyl-siloxane) The polydimethylsiloxane trialkanol (structure A1 with y₁ = 1, R₂ = R₂a) (MW 5750, Shin Etsu 504B) (506.8 g, 88.0 mmoles) is mechanically stirred in a one liter, three neck round bottom flask with three equivalents of isophorone diisocyanate, IPDI (58.76 g, 0.2639 mole) for six hours under a nitrogen atmosphere. A mild exotherm (28.5°C) is noted during the first hour of reaction. The product is a colorless oil with a molecular weight of 6400 as determined by NCO titration and a specific viscosity (2 % w/w in isopropanol) of 0.0916. The prepolymer is stored at 10°C under nitrogen in a glass bottle. Examples 5-11: Synthesis of Prepolymer B Using the same procedure described in example 1, the other NCO-capped PDMS-prepolymers (B) are synthesized and are summarized on the following table, together with examples 1-4: Example 12: Preparation of Silicone Rubber from a Polydimethylsiloxane Tri-isocyanate Prepolymer (B) and 1,3-Bis-(4-hydroxybutyl)-tetramethyldisiloxane (A) The tri-isocyanate prepolymer-B of example 4 (MW 6400) synthesized from the PDMS-trialkanol (Shin Etsu 504B) (22.96g, 3,588 mmole) is mixed with an equivalent amount of 1,3-bis(4-hydroxybutyl)tetramethyldisiloxane (Petrarch, Inc.)(1.50 g, 5.381 mmole) by mixing at 2 kPa (15 torr) in a 50 ml round bottom flask on a rotovaporator for 60 minutes. The formulation is used to fill 5 inch (12.7 cm) square by 1.00 mm thick and 5 inch (12.7 cm) square by 0.5 mm thick molds, the Mylar R surface of which has been previously coated with a 1.0 µ thick film of hydroxyethyl cellulose (QP100 M, MW 1,000,000, Union Carbide) from a 0.8 % aqueous solution. Also filled with the silicone formulation are two 10 mm x 15 mm polypropylene button molds. Curing is performed in an 80°C oven for six hours under a nitrogen atmosphere giving clear, rubbery silicone. The 1.00 mm thick sheets are used for measuring tensile strength, modulus, and elongation to break while the 0.50 mm thick sheets are used for measurement of oxygen permeability on a Permeometer. The buttons are used to measure the Shore A hardness of the rubber and its percent swelling and percent extractibles in absolute ethanol. Example 13: Preparation of Silicone Rubber from Poly(dimethylsiloxane)isocyanate Prepolymer (B) and Tetrahydroxyalkyl-poly(dimethylsiloxane) (A) The isocyanate-capped prepolymer B (MW 4700) of example 1 (24.66 g, 5.222 mmole) is mixed with an equivalent amount of tetrahydroxyalkyl-poly(dimethyldisiloxane) (structure A2, MW 1200; Mercor Inc.) (3.20 g, 2.612 mmoles) in a 50 ml round bottom flask at 2 kPa (15 torr). After 30 minutes a clear, degassed formulation is obtained which is used to fill 5 inch (12.7cm) square by 1.00 mm thick and 5 inch (12.7 cm) square by 0.5 mm thick molds, the Mylar R surface of which has been previously coated with a thin (< 1 micron) film of ethoxylated poly(vinyl alcohol) (Polysciences) from a 5 % aqueous solution. Two poly(propylene) button molds (15 mm x 10 mm) are also filled. Curing is performed in an 80°C oven under a nitrogen atmosphere for two hours and yields a clear, rubbery silicone. The 1.00 mm thick sheets are used to measure tensile strength, modulus, and elongation to break while the 0.5 mm sheets are used for oxygen permeability measurements on a Permeometer. Values for Shore A hardness, percent swelling and percent extractibles in absolute ethanol are made with 10 mm x 15 mm buttons. Examples 14-27: Synthesis of polysiloxane-polyurethanes Using the procedure described in example 13 polysiloxane-polyurethanes are prepared whose compositions are listed below together with that of example 13. Tetrafunctional (OH) Difunctional (NCO) Prepolymer - A Prepolymer - B Structure MW g mmol of Ex. g mmole 13 A3 1226 3.20 2.62 1 24.66 5.22 14 A3 3404 7.56 2.22 1 20.9 4.45 15 A3 6287 8.42 1.34 1 12.6 2.67 16 A3 1226 4.23 3.46 2 17.6 6.90 17 A3 3404 11.00 3.24 2 16.5 6.49 18 A3 6287 9.20 1.46 2 7.46 2.93 19 A3 1200 9.29 7.58 3 21.21 15.15 20 A3 3404 23.90 7.04 3 19.70 14.08 21 A3 6287 11.19 1.77 3 4.94 3.53 22 A3 1226 2.73 2.23 9 12.27 6.46 23 A3 3404 7.18 2.11 9 5.70 3.0 24 A3 6287 9.94 1.58 9 6.01 3.16 25 A3 1226 2.38 1.94 10 11.16 3.88 26 A3 3404 7.12 1.77 10 10.18 3.54 27 A3 6287 8.22 1.31 10 7.53 2.62 All polymers are colorless, clear and extremely wettable. Examples 28-33: Using the procedure of example 12 polysiloxane-polyurethanes are prepared with the compositions listed below. Ex. Component A: + Prepolymer (B) (Bis-4-hydroxybutyl) disiloxane (trifunctional) g mmole of Ex. g mmole 28 1.50 5.38 4 22.96 3.59 29 1.76 6.32 5 17.10 4.21 30 1.92 6.88 6 27.80 4.59 31 0.66 2.38 7 11.72 1.59 32 1.63 5.86 8 30.49 3.91 33 0.83 2.98 11 14.2 1.98 All polymers are clear, colorless and extremely wettable. Example 34: The polymers synthesized in examples 13-33 are tested for their physical-mechanical properties and oxygen permeability. Polymer of Ex. Shore-A Tensile Strength Young's Modulus Elongation to Break 0₂.DK (0.25 mm, 25°C) Dynes/cm² x 10⁵ % (Barrers) 13 38 66.59 223.89 37 169 14 35 9.61 101.40 17.8 177 15 31 10.00 72.57 22 183 16 51 26.97 99.34 47 200 17 44 19.12 89.04 41 209 18 37 20.99 50.60 159 202 19 62 37.07 248.70 22 93 20 51 14.22 115.33 19 180 22 54 176.81 99.93 105 125 23 45 127.19 49.23 63 135 24 40 87.77 39.81 58 155 25 41 64.72 91.34 159 136 26 38 103.66 54.43 120 259 27 36 54.03 27.65 86 - 28 31 14.22 40.50 60 208 29 41 35.19 80.85 75 115 30 36 38.67 61.15 134 227 31 38 36.87 69.04 133 250 32 30 26.09 45.80 109 214 33 32 17.85 46.19 59 210 Example 35: Preparation of Silicone Rubber from Tetrahydroxyalkyl-poly(dimethylsiloxane) and 2,2,4-Trimethylhexane-1,6-diisocyanate Tetrahydroxyalkyl-poly(dimethylsiloxane) of structure A3 (MW 1220, Mercor, Inc.) (15.16 g, 12.426 mmole) is formulated with an equivalent amount of 2,2,4-trimethylhexane-1,6-diisocyanate, TMDI (5.19 g, 24.714 mmole), and 9.1 mg (0.06 %) DBTL in the manner described in example 6. The formulation is cured into sheets and buttons as previously described yielding a clear, hard silicone rubber. Example 36: The tetrahydroxyalkylpoly(dimethylsiloxane) (of structure A3, MW 6300, Mercor, Inc.) (16.98 g, 2.695 mmole) is formulated with an equivalent amount of TMDI (1.12 g, 5.381 mmole) and 2.5 mg (0.015 %) DBTL in the manner described in example 6. The formulation is cured into sheets and buttons as previously described yielding a clear silicone rubber. Example 37: Trihydroxyalkyl-poly(dimethylsiloxane) (of structure A1 with y₁ = 1 and R₂= R₂a) (19.4 g, 5.07 mmole) is formulated with an equivalent amount of TMDI (1.69 g, 7.6mmole) and 52 mg DBTL in the manner described in example 6. The formulation is cured into sheets and buttons as previously described yielding a clear, resilient silicone rubber which has a Shore-A hardness of 32 and a O₂.DK (barrers) of 187. The following two examples describe the formation of contact lenses. Example 38: The poly(dimethylsiloxane)tri-isocyanate prepolymer described in example 4 (MW 6400, 9.86 g, 1.541 mmoles) is formulated with an equivalent amount of 1,3-bis(4-hydroxybutyl)tetramethyldisiloxane (MW 278.6, 0.644 g, 2.312 mmole). The composition is stirred in vacuo [2 kPa (15 torr)] until a degassed, homogeneous mixture is attained (30-45 minutes). Two drops of this formulation are placed in a polypropylene contact lens mold that has previously beendip coated with ethoxylated polyvinyl alcohol (EPVA Polysciences) from a 2 % aqueous solution containing 0.01 %LODYNE R S-100 (CIBA-GEIGY) fluorinated surfactant and dried ina forced-air oven at 80°C. The molds are closed and clamped in a spring loaded holder and cured at 80°C for two hours. After cooling and removing from the mold, the lenses are stirred in 60°C water overnight to dissolve ungrafted EPVA. Clean, highly wettable lenses are attained which retain these prdperties after stirring in boiling water for 7 days. Example 39: The poly(dimethylsiloxane)diisocyanate prepolymer described in example 1 (MW 4700, 6.17 g, 1.3086 mmole) is formulated with an equivalent amount ofpoly(dimethylsiloxane)tetra-alkanol (structure A3: MW 1220, 0.801 g, 0.6533 mmole). The composition is stirred in vacuo [2 kPa (15 torr)] for 30 minutes yielding a clear, homogenous mixture. Two drops of this formulation are placed in a polypropylene contact lens mold that has previously been dip coated with hydroxyethyl cellulose (HEC) (MW 815,000, Union Carbide) from a 1 %aqueous solution containing 0.01 % LODYNE R S-100 (CIBA-GEIGY) fluorinated surfactant. After curing for 90 minutes at 80°C the molds are cooled to room temperature and opened. The lenses formed are washed in 60°C water overnight to remove ungrafted HEC. Even after boiling in water for 7 days, the lenses remain highly wettable and clear. Example 40: a) Synthesis of Diisocyanate Prepolymer with TMDI: Dihydroxypolydimethylsiloxane of structure A2 with y₂ = 0, R₂ =R₂b) (MW 2760, Shin-Etsu A-1000) (75.63 g, 27.40 mmole) is reacted with two equivalents of 2,2,4-trimethyl-1,6-diisocyanatohexane (TMDI; 11.51 g, 54.80 mmole) in the presence of dibutyltin dilaurate (DBTL) (15 mg, 0.02 %) for 3 hours in the manner previously described after which time the NCO level falls to 1/2 the initial value. The prepolymer is stored under nitrogen in glass bottles at 10°C, the MW is 3300 by NCO titration. b) Synthesis of polysiloxane-polyurethane rubber: This prepolymer (12.11 g, 3.67 mmole) is formulated with an equivalent amount of PDMS-tetra-alkanol (Structure A3, MW1226, Mercor, Inc.) (2.25 g, 1.835 mmol) in the manner previously described, poured into molds and cured at 80°C (2 hours) giving a clear, resilient rubber with the following properties: Shore A hardness: 34, Tensile Strength: 34.3 dynes/cm² x 10⁻⁵, Young's Modulus: 100.0 dynes/cm² x 10⁻⁵, Elongation to Break: 61 %. The following three examples describe the synthesis of polysiloxane-polyurethanes with chain-extended polydimethylsiloxane-urethanes. Example 41: a) Synthesis of Chain-Extended (MW3385) Diisocyanate Prepolymer: Dihydroxyalkyl-polydimethylsiloxane of structure A1 with > y₁ = 0, R₂ = R₂b (MW 1500, Shin-Etsu; 146.33 g, 97.55 mmole) is weighed into a three neck, 300 ml round bottom flask equipped with mechanical stirrer, thermometer, and nitrogen inlet. Isophorone diisocyanate (32.53 g, 146.3mmole, 1.5 equivalents) is added and the two liquids are rapidly stirred, forming a white emulsion. Dibutyltin dilaurate, DBTL (29 mg, 0.02 %) is added and stirring is continued at room temperature. Solubilization occurs within 30 minutes and a mild exotherm (32°C) is noted approximately 100 minutes after catalyst addition. Stirring is continued for another three hours after which time the NCO level has fallen to 1/3 the initial value. The polymer is stored under nitrogen in glass bottles at 10°C; the MW is 3385, by NCO titration. b) Synthesis of Polysiloxane-Polyurethane Rubber: The prepolymer from example 41a (12.56 g. 3.710 mmole) is formulated with an equivalent amount of PDMS-tetra-alkanol (Structure A3, MW 1226, Mercor, Inc.) (2.27 g, 1.835 mmole) on a rotavaporator at 2,66 kPa (20 torr) for 30 minutes and then poured into molds in the manner previously described. The composition is cured at 80°C for 2 hours yielding a clear, colorless, resilient rubber with the following properties: Shore A hardness: 44, Tensile Strength: 54.9 dynes/cm² x 10⁻⁵, Young's Modulus: 126.6 dynes/cm² x 10⁻⁵, Elongation to Break: 104 %. Example 42: The prepolymer from example 41a (15.20 g, 4.49mmole) is formulated with an equivalent amount of PDMS-tetra-alkanol (MW 6287, Mercor, Inc.) (14.12g, 2.245mmole) in the manner previously described. Curing at 80°C for 2 hours gives a clear, colorless, resilient rubber with the following properties: Shore A hardness: 27, Tensile Strength: 12.6 dynes/cm² x 10⁻⁵, Young's Modulus: 36.2 dynes/cm² x 10⁻⁵, Elongation to Break: 80 %. Example 43: a) Synthesis of Chain-Extended (MW 2634) Diisocyanate Macromer: Dihydroxyalkyl-polydimethylsiloxane of structure A1 with y₁ = 0, R₂ = R₂b (MW 1044, Mercor, Inc.) (82.67 g, 79,19mmole) is reacted with 1.5 equivalents of isophorone diisocyanate, IPDI (26.41 g, 118.8 mmole) in the manner described in example 40. After stirring 3 1/2 hours at room temperature, the NCO level falls to 1/3 the initial value. The polymer is stored under nitrogen in glass bottles at 19°C; the MW is 2634, by NCO titration. b) Synthesis of Polysiloxane-Polyurethane Rubber: The prepolymer from example 43 (16.04 g, 6.09 mmole) is formulated with an equivalent amount of PDMS-tetra-alkanol (Structure A3, MW 1226, Mercor, Inc.) (3.73 g, 3.045 mmole) in the manner previously described. Molds are cured at 80°C for 2 hours yielding clear, resilient rubber with the following properties: Shore A hardness: 49, Tensile Strength: 91.0 dynes/cm² x 10⁻⁵, Young's Modulus: 123.4dynes/cm²x10⁻⁵, Elongation to Break: 168 %. Example 44: Preparation of a poly-(siloxane-urethane) with 2,4-toluene diisocyanate. a) Macromer Synthesis: 2,4-toluene diisocyanate (6.77 g, 0.0389 mole) is charged into a 100 ml round bottom flask equipped with mechanical stirrer, nitrogen inlet, and dropping funnel with pressure equalizer. Polysiloxane trialkanol, (Shinetsu X-61-504B, MW 5370, 69.29 g, 0.130 mole) is sparged with dry nitrogen and then dibutyltin dilaurate (DBTL) 7 mg, is dissolved in the siloxane. The latter is then added to the diisocyanate in a slow stream with vigorous stirring. After two hours the NCO level has dropped to the theoretical value and the clear, colorless prepolymer is poured into a glass bottle and stored at room temperature under nitrogen (MW 6340). b) Preparation of poly-(siloxane-urethane): The triisocyanate prepolymer of example 44a (21.81 g, 4.229 mmole) is weighed into a 50 ml round bottom flask. An equivalent amount of 1,3-bis(4-hydroxybutyl) tetramethyldisiloxane (1.76 g, 6.343mmole) is added and mixed on a rotavapor for 20 minutes. The mixture is poured into a MYLAR R lined glass mold and cured as described in example 12. A clear, colorless silicone rubber is obtained, useful for the production of soft contact lenses. Examples 45-48 describe the preparation of poly-(siloxane-urethane)-inter penetrating polymer networks (IPN's) with vinyl polymers. Example 45: The triisocyanate prepolymer of example 6 (MW 6150, 16.36 g, 2.660 mmole) is formulated with an equivalent of 1,3-bis (4-hydroxybutyl) tetramethyldisiloxane (MW 278.6, 1.11 g, 3.990 mmole) in a 50 ml round bottom flask on a rotavapor. After 20 minutes of mixing, the polysiloxanepolyurethane formulation (4.86 g) is mixed with N,N-dimethylacrylamide (0.54 g, 10 % by weight) into which VAZO R 52* initiator (2.7 mg) have previously been dissolved. The mixture is throughly degassed and poured into a 0.5 mm thick MYLAR R -lined mold, the surface of which has previously been coated with ethoxylated PVA as described in example 13. The formulation is cured first for 10 hours at 40°C, during which time the polyurethane network forms, than at 80°C for 3hours. A clear polymer with a highly wettable surface and awater content, after hydration, of 14.3 % (by weight) is obtained. *VAZO R 52 is 2,2'-azo bis (2,4-dimethylvaleronitrile). Example 46: Using the procedure described in example 45, the siloxane-urethane formulation (3.51 g) is mixed withmethacryloxypropyltris(trimethylsiloxy)silane (0.39 g, 10 % by weight) containing 2.0 mg of VAZO R 52 and cured at 40°C for 10 hours and 80°C for three hours. A clear, colorless polymer with a highly wettable surface is obtained. Example 47: The procedure of example 45 is repeated using 4.10 g of the silicone-urethane formulation and 0.46 g of tridecylfluorohexyl-ethyl methacrylate, containing 2.28 mg VAZO R 52. Curing at 40°C for 10 hours and at 80°C for 3 hours yields a clear, colorless polymer with a highly wettable surface. Example 48: The procedure of example 45 is repeated using 5.00 g of the silicone-urethane formulation and 0.56 g (10 %) of methyl methacrylate, containing 10 mg benzoin methyl ether. After curing the polyurethane at 80°C for three hours, the mold is exposed to UV radiation from a SILVANIA R Black-Lite-Blue lamp for 5 hours. A clear, highly wettable polymer is obtained.

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, GR, IT, LI, LU, NL, SE A crosslinked siloxane-urethane polymer in form of an ophthalmic device, which consists essentially of the reaction product of (A) a di- or poly-hydroxyalkyl substituted alkyl polysiloxane having a number average molecular weight between 200 and 10,000, and (B) a compatible, aliphatic, cycloaliphatic or aromatic di- or tri-isocyanate; wherein the total number of hydroxyl groups in component (A) is stoichiometrically equivalent to the total number of isocyanate groups in component (B), and with the proviso that an effective crosslinking amount of (A) or (B) or both (A) and (B) is present and possesses a functionality greater than two. An ophthalmic device according to claim 1 which is a contact lens. A siloxane-urethane polymer in form of an ophthalmic device according to claim 1 wherein component (A) is a di- or poly-hydroxy substituted polysiloxane of formula A1, A2 or A3, with the structures: wherein R₁ is an alkyl group of 1 to 4 carbon atoms or phenyl, R₂ is a linear or branched alkylene group with 2 to 6 carbon atoms (≡ R₂a), a polyoxyalkylene group of structure wherein R₃ is hydrogen or methyl and n is an integer from 1 to 50; x₁ and x₂ are integers from 1 to 500; y₁ is 0 to 4, y₂ is 2 to 5 with the proviso that the ratios of: x 1 + x 2 y 1 y 1 + 2 and x 1 + x 2 y 2 y 2 are not greater than 70. A siloxane-urethane polymer in form on an ophthalmic device according to claim 1 wherein component (B) is a diisocyanate, triisocyanate or mixture thereof selected from ethylene diisocyanate,1,2-diisocyanatopropane, 1, 3-diisocyanato-propane, 1, 6-diisocyanatohexane, 1,2-diisocyanatocyclohexane, 1,3-diisocyanatocyclohexane, 1, 4-diisocyanatobenzene; bis (4-isocyanatocyclohexyl) methane, bis (4-isocyanatocyclohexenyl) methane, bis(4-isocyanatophenyl)methane, 1,2- and 1,4-toluene diisocyanate; 3,3-dichloro-4,4'-diisocyanatobiphenyl; tris(4-isocyanatophenyl)methane, 1,5-diisocyanato-naphthalene, hydrogenated toluene diisocyanate; 1-isocyanatomethyl-5-isocyanato-1,3,3-trimethylcyclohexane (= isophorone diisocyanate) ; 1,3,5-tris-(6-isocyanatohexyl)biuret, 1, 6-diisocyanato-2,2,4-(2,4,4)-trimethylhexane, 2,2'-diisocyanatodiethyl fumarate; 1,5-diisocyanato-1-carboxypentane; 1,2-, 1,3-, 1,6-, 1,7-, 1,8-, 2,7and 2,3-diisocyanatonaphthalene; 2,4- and 2,7-diisocyanato-1-methylnaphthalene; 1,4-diisocyanato-methylcyclohexane; 1,3-diisocyanato-6 (7) -methylnaphthalene; 4,4'-diisocyanatobiphenyl; 4,4'-diisocyanato-3,3'-dimethoxy-bisphenyl; 3,3'-and 4,4'-diisocyanato-2,2'-dimethylbiphenyl; bis- (4-isocyanatophenyl)ethane; bis (4-isocyanatophenyl)ether. A crosslinked siloxane-urethane polymer in the form of an ophthalmic device according to claim 3, wherein (A) contains 40-60 equivalent percent of polysiloxane tetrols A3, where x₁ is 10-50 and R₁ is methyl, and 40-60 equivalent percent A1, where y₁ is zero, x₁ is 15-60, R₁ is methyl, R₂ is propylene, 1-methylpropylene, or and (B) is isophorone diisocyanate or 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A crosslinked siloxane-urethane polymer in form of an ophthalmic device according to claim 3, wherein (A) is of structure A1, where y₁ is zero to 1, x₁ is 5-50, x₂ is 5-50, R₁ is methyl, R₂ is propylene, butylene, 1-methyl propylene or and the diisocyanate (B) is isophorone diisocyanate (IPDI) or 2,2,4 (2,4,4)-trimethylhexane-1,6-diisocyanate (TMDI). A crosslinked siloxane-urethane polymer in form of an ophthalmic device according to claim 3, wherein (A) contains 40-60 equivalent percent of polysiloxane-tetrols of structure A3, and diisocyanate (B) is isophorone diisocyanate or 2,4,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A crosslinked siloxane-urethane polymer in form of an ophthalmic device according to claim 3, wherein (A) contains 40-60 equivalent percent of polysiloxane diols of structure A1, where y₁ is zero or 1, x₁ is 1-5, x₂ is 1-5, R₁ is methyl, R₂ is propylene or butylene, and the diisocyanate (B) is isophorone diisocyanate or 2,2,4(2,4,4) trimethylhexane-1,6-diisocyanate. A crosslinked siloxane-urethane polymer in the form of an ophthalmic device according to claim 4, wherein (B) is isophorone diisocyanate, 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate or 1,2- or 1,4-toluene diisocyanate. A compatible, interpenetrating-polymer-network composition which comprises (I) 95-50 %by weight of the total composition of a siloxane-urethane polymer formed by the reaction of (A) a di- or poly-hydroxyalkyl substituted alkyl polysiloxane having a number average molecuar weight between 200 and 10,000, and (B) a compatible, aliphatic, cycloaliphatic or aromatic di- or tri-isocyanate, wherein the total number of hydroxyl groups in component (A) is stoichiometrically equivalent to the total number of isocyanate groups in component (B), and with the proviso that an effective crosslinking amount of (A) or (B) or both (A) and (B) is present and possesses a functionality greater than two, and (II) 5-50 % by weight of the total composition of a vinyl polymer or copolymer obtained by the free-radical polymerization of a vinyl monomer or mixture of vinyl monomers. A composition according to claim 10 wherein component (I) is 95-75 % by weight and component (II) is 5-25 % by weight of the total composition. A composition according to claim 10 wherein component (A) is a di- or poly-hydroxy substituted polysiloxane of formula A1, A2 or A3, with the structures wherein R₁ is an alkyl group of 1 to 4 carbon atoms or phenyl, R₂ is a linear or branched alkylene group with 2 to 6 carbon atoms (≡ R₂a), a polyoxyalkylene group of structure wherein R₃ is hydrogen or methyl and n is an integer from 1 to 50; x₁ and x₂ are integers from 1 to 500; y₁ is 0 to 4, y₂ is 2 to 5 with the proviso that the ratios of: x 1 + x 2 y 1 y 1 + 2 and x 1 + x 2 y 2 y 2 are not greater than 70. A composition according to claim 10, wherein component (B) is a diisocyanate, triisocyanate or mixture thereof selected from ethylene diisocyanate, 1,2-diisocyanatopropane, 1,3-diisocyanato-propane, 1, 6-diisocyanatohexane, 1,2-diisocyanatocyclohexane, 1,3-diisocyanatocyclohexane, 1,4-diisocyanatobenzene; bis (4-isocyanatocyclohexyl) methane, bis (4-isocyanatocyclohexenyl)methane, bis (4-isocyanatophenyl)methane, 1,2- and 1,4-toluene diisocyanate; 3,3-dichloro-4,4'-diisocyanatobiphenyl; tris (4-isocyanatophenyl) methane, 1, 5-diisocyanato-naphthalene, hydrogenated toluene diisocyanate; 1-isocyanatomethyl-5-isocyanato-1,3,3-trimethylcyclohexane (= isophorone diisocyanate); 1,3,5-tris(6-isocyanatohexyl)biuret, 1,6-diisocyanato-2,2,4-(2,4,4)-trimethylhexane, 2,2'-diisocyanatodiethyl fumarate; 1,5-diisocyanato-1-carboxypentane; 1,2-, 1,3-, 1,6-, 1,7-, 1,8-, 2,7- and 2,3-diisocyanatonaphthalene; 2,4- and 2,7-diisocyanato-1-methylnaphthalene; 1,4-diisocyanato-methylcyclo-hexane; 1,3-diisocyanato-6(7)methylnaphthalene; 4,4'-diisocyanatobiphenyl; 4,4'-diisocyanato-3,3'-dimethoxy-bisphenyl; 3,3'- and 4,4'-diisocyanato-2,2'-dimethyl biphenyl; bis- (4-isocyanatophenyl) ethane and bis (4-isocyanatophenyl) ether. A composition according to claim 10 wherein component (A) contains 40-60 equivalent percent of polysiloxane tetrols A3, where x₁ is 10-50 and R₁ is methyl, and 40-60 equivalent percent A1, where y₁ is zero, x₁ is 15-60, R₁ is methyl, R₂ is propylene, 1-methylpropylene, or and (B) is isophorone diisocyanate or 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A composition according to claim 10 wherein component (A) is of structure A1, where y₁ is zero to 1, x₁ is 5-50, x₂ is 5-50, R₁ is methyl, R₂ is propylene, butylene, 1-methyl propylene or and the diisocyanate (B) is isophorone diisocyanate (IPDI) or 2,2,4 (2,4,4)-trimethylhexane-1,6-diisocyanate (TMDI). A composition according to claim 10 wherein component (A) contains 40-60 equivalent percent of polysiloxane-tetrols of structure A3, and diisocyanate (B) isisophorone diisocyanate or 2,4,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A composition according to claim 10 wherein component (A) contains 40-60 equivalent percent of polysiloxane diols of structure A1, where y₁ is zero or 1, x₁ is 1-5, x₂ ist 1-5, R₁ is methyl, R₂ is propylene or butylene, and the diisocyanate (B) is isophorone diisocyanate or 2,2,4(2,4,4)trimethylhexane-1,6-diisocyanate. A composition according to claim 10 wherein component (B) is isophorone diisocyanate, 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate or 1,2- or 1,4-toluene diisocyanate. A composition according to claim 10 where in component (II) the vinyl polymer is prepared from a fluoroalkyl acrylate or methacrylate with 3 to 21 fluoro atoms in the fluoroalkyl group, from an oligosiloxanyl-silylalkyl acrylate or methacrylate with 2 to 10 Si atoms in the oligosiloxanyl group, from a hydroxyalkyl acrylate or methacrylate, N-vinylpyrrolidone, N,N-dimethylacrylamide or methyl methacrylate. A composition according to claim 10 where in component (II) the vinyl polymer is prepared from N,N-dimethylacrylamide, methyl methacrylate, 2-hydroxyethyl methacrylate, methacryloxypropyl-tris (trimethylsiloxy)silane or tridecylfluorohexyl-ethyl methacrylate. An ophthalmic device prepared from the composition according to claim 10. An ophthalmic device according to claim 21 which is a contact lens. Claims for the following Contracting State : ES A process for the manufacture of a crosslinked siloxane-urethane polymer in form of an ophthalmic device, which consist essentially of the reaction product of (A) a di- or poly-hydroxyalkyl substituted alkyl polysiloxane having a number average molecular weight between 200 and 10,000, and (B) a compatible, aliphatic, cycloaliphatic or aromatic di- or tri-isocyanate; wherein the total number of hydroxyl groups in component (A) is stoichiometrically equivalent to the total number of isocyanate groups in component (B), and with the proviso that an effective crosslinking amount of (A) or (B) or both (A) and (B) is present and possesses a functionality greater than two, which process comprises reacting components (A) and (B). An process according to claim 1 wherein the ophthalmic device is a contact lens. A process according to claim 1 wherein component (A) is a di- or poly-hydroxy substituted polysiloxane of formula A1, A2 or A3, with the structures: wherein R₁ is an alkyl group of 1 to 4 carbon atoms or phenyl, R₂ is a linear or branched alkylene group with 2 to 6 carbon atoms (≡ R₂a), a polyoxyalkylene group of structure wherein R₃ is hydrogen or methyl and n is an integer from 1 to 50; x₁ and x₂ are integers from 1 to 500; y₁ is 0 to 4, y₂ is 2 to 5 with the proviso that the ratios of: x 1 + x 2 y 1 y 1 + 2 and x 1 + x 2 y 2 y 2 are not greater than 70. A process according to claim 1 wherein component (B) is a diisocyanate, triisocyanate or mixture thereof selected from ethylene diisocyanate,1,2-diisocyanatopropane, 1,3-diisocyanato-propane, 1,6-diisocyanatohexane, 1,2-diisocyanatocyclohexane, 1,3-diisocyanatocyclohexane, 1,4-diisocyanatobenzene; bis(4-isocyanatocyclohexyl)methane, bis (4-isocyanatocyclohexenyl)methane, bis (4-isocyanatophenyl)methane, 1,2- and 1,4-toluene diisocyanate; 3,3-dichloro-4,4'-diisocyanatobiphenyl; tris(4-isocyanatophenyl)methane, 1,5-diisocyanato-naphthalene, hydrogenated toluene diisocyanate; 1-isocyanatomethyl-5-isocyanato-1,3,3-trimethylcyclohexane (= isophorone diisocyanate); 1,3,5-tris(6-isocyanatohexyl)biuret, 1, 6-diisocyanato-2,2,4-(2,4,4)trimethylhexane, 2,2'-diisocyanatodiethyl fumarate; 1,5-diisocyanato-1-carboxypentane; 1,2-, 1,3-, 1,6-, 1,7-, 1,8-, 2,7- and 2,3-diisocyanatonaphthalene; 2,4- and 2,7-diisocyanato-1-methylnaphthalene; 1,4-diisocyanato-methylcyclohexane; 1,3-diisocyanato-6(7) -methylnaphthalene; 4,4'-diisocyanatobiphenyl; 4,4'-diisocyanato-3,3'-dimethoxy-bisphenyl; 3,3'-and 4,4'-diisocyanato-2,2'-dimethylbiphenyl; bis- (4-isocyanatophenyl) ethane; bis (4-isocyanatophenyl) ether. A process according to claim 3, wherein (A) contains 40-60 equivalent percent of polysiloxanetetrols A3, where x₁ is 10-50 and R₁ is methyl, and 40-60 equivalent percent A1, where y₁ is zero, x₁ is 15-60, R₁ is methyl, R₂ is propylene, 1-methylpropylene, or and (B) is isophorone diisocyanate or 2,2, 4(2,4,4)-trimethylhexane-1,6-diisocyanate. A process according to claim 3, wherein (A) is of structure A1, where y₁ is zero to 1, x₁ is 5-50, x₂ is 5-50, R₁ is methyl, R₂ is propylene, butylene, 1-methyl propylene or and the diisocyanate (B) is isophorone diisocyanate (IPDI) or 2,2,4 (2,4,4)-trimethylhexane-1,6-diisocyanate (TMDI) . A process according to claim 3, wherein (A) contains 40-60 equivalent percent of polysiloxane-tetrols of structure A3, and diisocyanate (B) is isophorone diisocyanate or 2,4,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A process according to claim 3, wherein (A) contains 40-60 equivalent percent of polysiloxane diols of structure A1, where y₁ is zero or 1, x₁ is 1-5, x₂ is 1-5, R₁ is methyl, R₂ is propylene or butylene, and the diisocyanate (B) is isophorone diisocyanate or 2,2,4(2,4,4) trimethylhexane-1,6-diisocyanate. A process according to claim 4, wherein (B) is isophorone diisocyanate, 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate or 1,2- or 1,4-toluene diisocyanate. A process for the manufacture of a compatible, interpenetrating-polymer-network composition which comprises (I) 95-50 %by weight of the total composition of a siloxane-urethane polymer formed by the reaction of (A) a di- or poly-hydroxyalkyl substituted alkyl polysiloxane having a number average molecular weight between 200 and 10,000, and (B) a compatible, aliphatic, cycloaliphatic or aromatic di- or tri-isocyanate, wherein the total number of hydroxyl groups in component (A) is stoichiometrically equivalent to the total number of isocyanate groups in component (B), and with the proviso that an effective crosslinking amount of (A) or (B) or both (A) and (B) is present and possesses a functionality greater than two, and (II) 5-50 % by weight of the total composition of a vinyl polymer or copolymer obtained by the free-radical polymerization of a vinyl monomer or mixture of vinyl monomers, which process comprises polymerizing the vinyl monomer or mixture of vinyl monomers simultaneously with the polyurethane forming components (A) and (B), or subsequently. A process according to claim 10 wherein component (I) is 95-75 % by weight and component (II) is 5-25 % by weight of the total composition. A process according to claim 10 wherein component (A) is a di- or poly-hydroxy substituted polysiloxane of formula A1, A2 or A3, with the structures wherein R₁ is an alkyl group of 1 to 4 carbon atoms or phenyl, R₂ is a linear or branched alkylene group with 2 to 6 carbon atoms (≡ R₂a), a polyoxyalkylene group of structure wherein R₃ is hydrogen or methyl and n is an integer from 1 to 50; x₁ and x₂ are integers from 1 to 500; y₁ is 0 to 4, y₂ is 2 to 5 with the proviso that the ratios of: x 1 + x 2 y 1 y 1 + 2 and x 1 + x 2 y 2 y 2 are not greater than 70. A process according to claim 10, wherein component (B) is a diisocyanate, triisocyanate or mixture thereof selected from ethylene diisocyanate, 1,2-diisocyanatopropane, 1, 3-diisocyanato-propane, 1, 6-diisocyanatohexane, 1,2-diisocyanatocyclohexane, 1,3-diisocyanatocyclohexane, 1, 4-diisocyanatobenzene; bis (4-isocyanatocyclohexyl) methane, bis (4-isocyanatocyclohexenyl)methane, bis (4-isocyanatophenyl)methane, 1,2- and 1,4-toluene diisocyanate; 3,3-dichloro-4,4'-diisocyanatobiphenyl; tris (4-isocyanatophenyl) methane, 1,5-diisocyanato-naphthalene, hydrogenated toluene diisocyanate; 1-isocyanatomethyl-5-isocyanato-1,3,3-trimethylcyclohexane (= isophorone diisocyanate); 1,3,5-tris(6-isocyanatohexyl)biuret, 1,6-diisocyanato-2,2,4-(2,4,4)-trimethylhexane, 2,2'-diisocyanatodiethyl fumarate; 1,5-diisocyanato-1-carboxypentane; 1,2-, 1,3-, 1,6-, 1,7-, 1,8-, 2,7- and 2,3-diisocyanatonaphthalene; 2,4- and 2,7-diisocyanato-1-methylnaphthalene; 1,4-diisocyanato-methylcyclo-hexane; 1,3-diisocyanato-6(7)methylnaphthalene; 4,4'-diisocyanatobiphenyl; 4,4'-diisocyanato-3,3'-dimethoxy-bisphenyl; 3,3'- and 4,4'-diisocyanato-2,2'-dimethyl biphenyl; bis- (4-isocyanatophenyl) ethane and bis (4-isocyanatophenyl) ether. A process according to claim 10 wherein component (A) contains 40-60 equivalent percent of polysiloxane tetrols A3, where x₁ is 10-50 and R₁ is methyl, and 40-60 equivalent percent A1, where y₁ is zero, x₁ is 15-60, R₁ is methyl, R₂ is propylene, 1-methylpropylene, or and (B) is isophorone diisocyanate or 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A process according to claim 10 wherein component (A) is of structure A1, where y₁ is zero to 1, x₁ is 5-50, x₂ is 5-50, R₁ is methyl, R₂ is propylene, butylene, 1-methyl propylene or and the diisocyanate (B) is isophorone diisocyanate (IPDI) or 2,2,4 (2,4,4)-trimethylhexane-1,6-diisocyanate (TMDI). A process according to claim 10 wherein component (A) contains 40-60 equivalent percent of polysiloxane-tetrols of structure A3, and diisocyanate (B) is isophorone diisocyanate or 2,4,4(2,4,4)-trimethylhexane-1,6-diisocyanate. A process according to claim 10 wherein component (A) contains 40-60 equivalent percent of polysiloxane diols of structure A1, where y₁ is zero or 1, x₁ is 1-5, x₂ ist 1-5, R₁ is methyl, R₂ is propylene or butylene, and the diisocyanate (B) is isophorone diisocyanate or 2,2,4(2,4,4) trimethylhexane-1,6-diisocyanate. A process according to claim 10 wherein component (B) is isophorone diisocyanate, 2,2,4(2,4,4)-trimethylhexane-1,6-diisocyanate or 1,2- or 1,4-toluene diisocyanate. A process according to claim 10 where in component (II) the vinyl polymer is prepared from a fluoroalkyl acrylate or methacrylate with 3 to 21 fluoro atoms in the fluoroalkyl group, from an oligosiloxanyl-silylalkyl acrylate or methacrylate with 2 to 10 Si atoms in the oligosiloxanyl group, from a hydroxyalkyl acrylate or methacrylate, N-vinylpyrrolidone, N,N-dimethylacrylamide or methyl methacrylate. A process according to claim 10 where in component (II) the vinyl polymer is prepared from N,N-dimethylacrylamide, methyl methacrylate, 2-hydroxyethylmethacrylate, methacryloxypropyl-tris (trimethylsiloxy) silane or tridecylfluorohexyl-ethyl methacrylate. An ophthalmic device prepared from the composition according to claim 10. An ophthalmic device according to claim 21 which is a contact lens.

Inventors: HARISIADES PAUL, MUELLER KARL F, HARISIADES, PAUL, MUELLER, KARL F., Müller, Karl F.
Applicants: CIBA GEIGY AG, CIBA-GEIGY AG
Application year: 1989
Main classification: C08G18
IPC codes: G02C7, C08G18, G02B1, C08L75