FLOW DIVIDER

Abstract: Flow dividers for dividing a hot gas flow into several partial flows through parallel internal channels are used in heat exchangers and as catalyst carriers, and can be produced by shaping the flow divider from metallic aluminium through extrusion or winding, then converting it to hydrated aluminium oxide through anodic oxidation while it is slowly moving down into an electrolyte (4), and finally converting it to alpha-alumina through heat treatment.

Description: FLOW DIVIDER Background In power engineering it is a common goal to achieve within a limited volume a transfer of energy between a gas flow and a solid body or a chemical reaction in a gas aided by a catalyst fixed to the surface of a solid body. The solid body must then be shaped with a maximum contact surface with the gas flow without too high flow resistance. The solid body is then often shaped with a large number of parallel channels, separated by thin walls, thereby dividing the gas flow into a large number of partial flows with turbulent flow pattern. Examples of use of such flow dividers are found among heat exchangers, mufflers, catalyst carriers for chemical industry and for emission control in vehicles. Other examples are for gas flow direction in furnaces, burners and wind tunnels. Background For use at high temperatures above 700 degrees C two types of material are mainly used, none fully satisfactory. Ceramic materials, such as aluminium oxide, can be extruded as a slurry to bodies with parallel channels as disclosed in patents EP 294.106 and EP 275.162, and thereafter be converted by heat treatment to water-free alumina, but has disadvantages due to built-in stresses, fragility, difficulty in handling prior to the heat treatment and difficulty to shape the channel entries for low flow resistance. They may need complex mounting devices for enclosure in metal, as shown in patent US 3.966.419. Metals are easy to shape, both by extrusion and by winding together grooved, corrugated or pleated strips as shown in patent US 4.719.680, but at elevated temperatures they are mechanically unstable by creep deformation, and chemically unstable by reaction with the gases. Description of the invention The present invention concerns a method of making flow dividers, where the shaping is done in a metallic state, and a conversion to ceramic material is carried out after the shaping. This results in greater liberty in choice of shape, and lower cost. It is well known that anodic oxidation in an electrolyte containing oxalic acid permits conversion of the whole thickness of a thin-walled aluminium object to hydrated aluminium oxide. It is also known that heat treatment of hydrated aluminium oxide can convert it to non-hydrated aluminium oxide in the alpha-alumina modification, which is tough and wear resistent. It is also known to combine these known steps to fabricate simply shaped items such as loudspeaker membranes from alpha-alumina according to the patent applications DE 35 42 202 and DE 35 46 548. The shapes of metallic flow dividers, extruded as well as wound, comprise portions with larger thickness than average, such as where two walls meet, and narrow passages where the current density and the oxidation rate are less than average, such as where two layers touch when wound together, or far into the central channels. If such bodies are anodic oxidized with the known methods, it would be impossible to avoid metallic remnants where the thickness is large or the oxidation rate low, because these portions loose contact with the current source when the thinner easily oxidated portions have been converted. During a subsequent heat treatment the metal would melt and damage the shape of the body. According to the invention the flow divider with parallel channels is shaped in a first step by extrusion or by winding together corrugated, pleated or grooved strips. If desired, the mechanical stability of a wound divider can be improved by thermal bonding in heated inert gas. In a second step the channel exits or entrances are chemically deburred to lower the flow resistance. In a third step the aluminium metal is converted to hydrated aluminium oxide through anodic oxidation in an electrolyte containing oxalic acid, with a current source connected to the upper end of the flow divider and the flow divider is slowly lowered into the electrolyte with the channels vertically oriented while the current flows. All parts of the flow divider are then successively converted to hydrated aluminium oxide, with the not yet converted metal below the surface of the electrolyte occurring as a middle layer with downwards taperingly decreasing thickness as shown in figure 1. At thicker or slowly oxidized portions, the taper will reach farther down below the surface of the electrolyte, at easily oxidized portions not so far. There is no risk of formation of non-converted metallic remnants. When the desired length for the divider has been converted, the current source is disconnected. In a fourth step the flow divider is converted from hydrated aluminium oxide to water-free alpha-alumina through heat treatment at a high temperature exceeding 700 degrees C. If the flow divider is to be used as a catalyst carrier, the catalyst is thereafter applied in one or more steps. Description of the figures Figure 1 shows in cross-section how the slow immersion during the third step ensures that lower parts are first converted, and no metallic remnants are left, even at thicker or slowly oxidized portions. The current source (3) has one of its terminals connected to the electrolyte (4) and its other terminal to the upper end of the metallic preformed aluminium flow divider (5) which is shown in cross section in figure 1. Below the surface (2) of the electrolyte, the thickness of the not yet converted aluminium layer in the middle of the walls is taperingly decreasing, such that it has its original thickness at the surface (2) of the electrolyte and below this decreases to vanishingly thin at that level (1) where it has been subject to oxidation long enough for the whole thickness to be converted. Figur 2 shows a flow divider which can be manufactured through extrusion.The invention is not limited to this shape of the channels, and also includes flow dividers shaped by winding. The invention is not limited to items with cylindrical outer surface, either. Realization of the invention An elongated body of aluminium metal is formed through extrusion, with a large number of parallel internal channels, separated by thin walls. Suitable dimensions are for the wall thickness 0.1 to 0.5 mm, for the channel width 1 to 4 mm, where the smaller dimensions refer to catalyst carriers, the larger to heat exchangers. As an alternative the body can be formed by winding together one or more aluminium strips, at least one of them with a corrugated, pleated or grooved surface. This body is cut to a length somewhat exceeding the desired length of the flow divider, is then thoroughly cleaned, where after one end is dipped in an alcaline etching solution to deburr and round the channel entrances. Special shaping to facilitate later enclosure or attachment of the flow divider can be made at this stage. The other end of the body is connected to a current source, the other terminal of which is connected to an electrolytic bath, containing oxalic acid, and the body is then slowly lowered into the electrolyte while the current flows. The aluminium metal is then through anodic oxidation converted to hydrated aluminium oxide, starting at the lower end, the wall thickness becoming larger than before the conversion, and wound layers in contact becoming permanently joined. When a long enough piece of the body has been converted, it is removed from the electrolyte. Remaining metallic portions at the upper end are cut away. The body is then heated in an oven to a temperature above 700 degrees C. The choice of temperature and heating time depends on the shape of the body and the type of oven. Ovens with microwave heating will require temperatures up to 1100 degrees and times up to 30 minutes, convection ovens or radiation ovens will need higher temperatures or longer time. This converts the hydrated aluminium oxide to water-free alpha-alumina. If the body is to be used as a catalyst carrier, the channels are coated with catalyst material after it has cooled. Field of use Flow dividers according to the invention can be used as catalyst carriers in exhaust systems or chemical industry, as heat exchangers and as flow equalizers in convection ovens. The invention is not restricted to cylindrical shape or to the use within certain temperature ranges. By performing the shaping on a metallic body, it can be fitted to different shape requirements. The good chemical resistance of alpha-alumina makes the invention useful also in applications where an aggressive chemical environment is decisive.

Claims: Patent Claims 1. Method for producing a flow divider for hot or aggressive gases, comprising a body of alpha-alumina with a plurality of parallel internal channels, c h a r a c t e r i z e d by shaping the flow divider from metallic aluminium, then converting it to hydrated aluminium oxide through anodic oxidation while it it slowly moving down into an electrolyte, and finally converting it to alpha-alumina through heat treatment at a temperature exceeding 700 degrees C. 2. Method according to claim 1, c h a r a c t e r i z e d by shaping the flow divider from metallic aluminium through extrusion, cutting to the desired length and deburring of the entrances of the channels. 3. Method according to claim 1, c h a r a c t e r i z e d by shaping the flow divider from metallic aluminium through winding of at least one crosswise corrugated, pleated or grooved strip. 4. Method according to claim 3, c h a r a c t e r i z e d by thermal bonding of the layers after winding. 5. Method according to claims 2 or 3, characterized by chemical rounding and deburring of the entrances of the channels. 6. Flow divider for dividing a hot gas flow into several partial flows through parallel internal channels with thin walls, shaped by winding at least one crosswise corrugated, pleated or grooved strip, c h a r a c t e r i z e d by consisting of alpha-alumina.

Inventors: SJOEGREN G H PEDRO, SUNDSTROEM ERIK W, SJOEGREN, G., H., PEDRO, SUNDSTROEM, ERIK, W.
Applicants: SJOEGREN G H PEDRO, SUNDSTROEM ERIK W, SJOEGREN, G., H., PEDRO, SUNDSTROEM, ERIK, W.
Application year: 1989
Main classification: C01F7
IPC codes: B01J37, C04B35, C25D11