Corrosion control

Abstract: A method of removing iron contaminants in an aqueous system by introducing and maintaining within the system an ortho dihydroxylaromatic compound having at least one electron withdrawing group pendant from the aromatic ring and, further, a method of inhibiting calcium scale formation in the presence of iron contaminants by utilizing a dihydroxylaromatic compound in combination with a calcium scale inhibitor.

Description: The present invention is directed to a novel method of removing iron contaminant formations commonly found in aqueous systems. The present method provides a means for dislodging and removing iron III scale formations which have formed in systems having iron and/or iron based alloy components in contact with the aqueous system. The subject invention is directed to the use of a substantially non-toxic method of removing corrosion products of ferrous metals in contact with aqueous systems by effectively dislodging and removing these products from the system. The method described and claimed herein requires the use of at least one adjacent-paired or ortho-dihydroxy aromatic compound which further contains at least one electron withdrawing group pendant from the aromatic ring. The present invention shall be described in terms of its utilization in conjunction with cooling water systems. However, the invention is not so limited but can be effectively used in conjunction with other aqueous systems which are in contact with iron base alloy material and, in particular, difficult to control systems which present conditions of elevated pH, high temperatures and/or high hardness levels such as boilers, heat exchangers and the like. The dislodgement and/or removal of iron corrosion formation is essential in cooling water systems to cause the equipment to be free from obstruction and to produce an efficient system by maximizing flow rate and heat transfer. Iron(III) oxide scale is known to build-up in these systems and cause a marked decrease in their efficiency. The iron oxide scale is particularly troublesome because of its extremely low solubility in aqueous media and, therefore, deposits and builds up in the equipment to reduce the flow rate and impede the heat transfer. Thus, there is a need for additives which are capable of removing the iron scale and maintaining the system free of scale build-up. In order to effectively do this, the additive must be capable of dislodging and dissolving the iron oxide solids present in the system. There are many means which have been suggested for iron scale removal. For a product to be useful under the conditions commonly found in cooling systems and the like, it must be capable of meeting the following combination of rigorous criteria: 1) dissolution of old rust scale; 2) dissolution of solids of iron(III) oxides and iron(III) hydroxides which are materials normally insoluble in cooling water conditions of high pH and which normally is very hard water having high calcium and magnesium content; 3) capable of controlling the formation of new rust scale as iron(III) over a sustained period; 4) capable of removing the iron scale from the system without mere dislodgement of solids from its site of formation as such solids tend to be trapped at other locations of small dimension causing a clogging of the system; 5) utilize material or compositions which are stable under the adverse conditions presented, such as high pH (6.5 - 9.5), high temperature (eg. 38-79°C (100-175°F)) and/or hardness associated with the presence of excess calcium, magnesium and carbonate ions; 6) utilize material which is capable of remaining soluble under the adverse conditions presented; 7) not being a source of corrosion or of accelerating the corrosion of the system; 8) capable of complexing iron at low levels; 9) capable of enhancing the performance of threshold scale inhibitors in the presence of iron; and 10) capable of promoting the formation of protective oxide layers which render the metal surface passive to further corrosion. It is readily seen that a means of achieving this combination of desired properties would find a high degree of acceptance in the control of iron scale in cooling water systems. Scale prevention should be the primary goal for maintaining a clean system. However inadvertent system upsets in pH, temperature, cycles of concentration, flow rate, etc., result in the formation of some iron scale which is not prevented by the normal maintenance dosage of conventional additives. Thus, there is a need for an additive which will remove iron oxide deposits which have been formed due to such upsets. Classical methods for removing iron scale involve acid or mechanical cleaning. These are undesirable since they require costly shut down of the system being treated and lead to equipment degradation via corrosion and/or mechanical abrasion. A means for the removal of iron scale during normal operation of the cooling water system would present an improvement in economics, simplication of operation and minimize equipment degradation. Polymeric additives have been used in an attempt to control iron scale in cooling water. For example, U.S. patent 3,898,037 describes the dispersion of insoluble iron compounds with polymers of 2-acrylamido-2-methylpropanesulfonic acid. Sulfonated polymers have also been used for this purpose (Proc. -Int. Water Conf. Eng. Soc. West. Pa. 1978 , 39, 299). These dispersants are capable of preventing iron oxide solids from depositing. They do not, however, dissolve iron(III) oxides and are not effective in removing hardened or crystalline deposits which are often present in cooling water systems. Chelating agents have been used to prevent and remove iron oxide scales by sequestration. Ethylenediaminetetraacetic acid has been used to remove iron oxide scale (U.S. 2,396,938), but it is effective only in the absence of excess calcium, a common condition encountered in cooling systems and the like. Its use can also lead to increased corrosion. Organophosphonates such as aminotrimethylenephosphonic acid (ATMP) have been shown to sequester iron(III) and thereby keep it soluble up to pH=10 (Dequest , Technical Bulletin 1-247, Monsanto, 1972). However, it is known that these organophosphonates will, in general, not dissolve iron oxide or iron hydroxide solids in water containing high concentrations of calcium ions at pH of 8 or above. These water conditions are typical for normal operation of a cooling water system and the like. In addition, these organophosphonates have been found to precipitate with high levels of calcium, precluding their use for iron-scale control in high hardness waters. JP-A-58133382 describes compounds of the general formula wherein X represents hydrogen, alkyl of 1 to 4 carbon atoms, hydroxy, alkoxy of 1 to 4 carbon atoms or carboxy, and Y represents hydrogen or hydroxy (provided that when Y is hydroxy X is other than hydroxy or alkoxy) as corrosion inhibitors for calcium chloride brine: such brine generally contains 15-35 wt% of calcium chloride. The compounds are described as suppressing corrosion of ferrous metals in contact with such brine: there is no disclosure or suggestion that they might be effective in removing iron contaminants from such systems, in cleaning solid iron (III) corrosion products or in inhibiting calcium scale formation. It is highly desired to have a means of dislodging and removing built up iron corrosion products and to disperse and dissolve them while further preventing such product formation of systems in which aqueous solution and iron or iron based alloy materials are in contact. Summary of the Invention The present invention is directed to a method for removing formations of iron corrosion products in systems presenting an aqueous/iron or iron base alloy interface, in particular to cooling water or heat exchange systems and, thus, presents a means of clearing the systems of such products. The present method requires introducing and maintaining within the aqueous component of the system at least one aromatic compound having two hydroxyl groups positioned ortho as adjacent-paired with respect to each other and at least one electron withdrawing group substituted for a hydrogen atom of the aromatic group. Detailed Description The present invention is directed to a process using a soluble additive for cleaning cooling water systems of iron scale formation. It has now been unexpectedly found that certain dihydroxy-aromatic compounds, which also contain electron-withdrawing substituents provide all of the desired properties as described in the Background of the Invention. The combination of paired hydroxyl groups and at least one electron-withdrawing group are essential for maintaining these dihydroxy aromatic additives as stable and soluble materials having the ability to effectively remove the unwanted iron contaminant solids under cooling water conditions. The present invention accordingly provides a method of removing iron contaminants from an aqueous system comprising introducing into the system an aqueous solution comprising a dihydroxylaromatic compound represented by the formula: Q―(Ar)―(OH)₂ wherein Ar represents a benzene aromatic moiety, Q represents at least one electron withdrawing group substituted on the Ar moiety, and the hydroxyl (OH) groups are substituted on the Ar moiety in ortho positions with respect to each other, to provide a concentration from 0.1 to 50,000 parts per million of the dihydroxylaromatic compound within the system, and removing portions of the aqueous system containing said iron contaminants. The invention further provides a method of cleaning solid iron (III) corrosion products from systems comprising an aqueous/iron or iron base alloy interface which comprises introducing into the aqueous component of the system an aqueous solution comprising a dihydroxylaromatic compound as defined above to dislodge and/or to dissolve said corrosion products, and removing portions of the aqueous system containing said corrosion products. The compound required to be used in the present process will be described herein and in the appended claims as an aromatic compound having adjacent-paired dihydroxy groups or ortho dihydroxy groups as well as at least one electron withdrawing group directly attached to the same aromatic moiety. The term "paired" or "ortho" as used herein and in the appended claim refers to the positioning of two hydroxy groups on adjacent carbon atoms of a single benzylic ring. The compounds required to be used according to the method of the present invention are aromatic compounds containing paired hydroxyl groups and containing at least one electron withdrawing group. The term "aromatic" as used in this description and in the appended claims shall, unless specifically indicated otherwise, refer to benzylic compounds. The term "electron-withdrawing group" refers herein and in the appended claims to any group which has an electron-withdrawing inductive effect which is known to intensify a positive charge and destabilize a carbonium ion of the aromatic group. Suitable electron-withdrawing groups include SO₃H, SOR, SO₂R, -NO₂, -F, -Cl, -Br, -CHO, -COR (eg. -COCH₃), -CONH₂, -CONHR, CONR₂, -CO₂H, -PO₃H₂ (where R = an alkyl group of 1 to 10 carbon atoms). The preferred groups are sulfonyl, carboxyl and nitro groups. Examples of the subject compounds are 3,4-dihydroxybenzene-sulfonic acid (catechol-4-sulfonic acid), 4-nitro-1, 2-benzenediol, 3,4-dihydroxybenzoic acid, 4,5-dihydroxy-1,3, benzene disulfonic acid (catechol-3,5-disulfonic acid) and salts of said acids. The salts are preferably formed from alkali and alkaline earth metals. The required compound is represented by the formula: Q―(Ar)―(OH)₂ wherein Ar represents a benzene aromatic moiety, Q represents at least one electron withdrawing group substituted on the aromatic moiety and the hydroxyl groups are in paired position on the benzene aromatic Ar group. These aromatic compounds may be used in combination with known water treatment additives such as chelants, scale inhibitors, pH regulating agents, dispersants, biocides and/or corrosion inhibitors and mixtures thereof. Examples of chelants are N,N,N′,N′ ethylenediamine tetraacetic acid and N,N′-bis (2-hydroxybenzyl) ethylenedinitrilo-N,N′-diacetic acid. Examples of pH regulating agents are mineral acid (e.g., H₂SO₄), organic acids (acetic acid), base (e.g., NaOH) and various buffers (e.g., phosphates or borates). Examples of scale inhibitors are organophosphonates as, for example, aminotrimethylenephosphonic acid and hydroxyethylidene-1, 1-diphosphonic acid as well as polyacrylates. Examples of dispersants include carboxylate and sulfonate containing polymers. Examples of biocides are chlorine- and bromine-containing materials and quaternary ammonium salts. Examples of corrosion inhibitors suitable for use herein are inorganic acids (i.e. phosphoric acid) organic acids (i.e. citric, HEDPA) and salts of these acids such as, phosphates, organophosphonates, chromates, molybdates, and zinc salts. The method of this invention for removing iron-based scale in cooling water and similar systems comprises maintaining in the aqueous liquid from 0.1 to 50,000 parts per million ("ppm") preferably 1 to 2000 ppm and most preferably 5 to 200 ppm of at least one of the subject paired dihydroxy aromatic compounds (single or multi-component) and removing portions of the aqueous system containing iron contaminants. When the subject agents are used to slug clean (quick clean a corrosion containing system) the agents are normally used in from 500 to 5000 ppm and the system is maintained at a pH of from 6 to 9.5 (preferably 6 to 8). For example, after removal of iron contaminants, the system may be maintained free from iron contaminants by maintaining the subject compounds in the system in concentrations of from 2 to 20 parts per million with the pH being from 7.5 to 9.5 (preferably less than 8). The temperature of the system being treated should be maintained from ambiant to 93 o C (200 o F) and preferably up to 71 o C (160 o F). The composition employed for this invention can be added to the water by conventional bypass feeder using briquettes containing the treatment, by adding the compounds either separately or together as dry powder mixtures to the water, or it can be fed as an aqueous feed solution containing the treatment components. Another embodiment of the present invention is the utilization of the subject paired dihydroxy aromatic compounds in combination with conventional calcium scale inhibitors, such as exemplified above. Such scale inhibitor agents do not normally provide the desired inhibiting characteristics when the system being treated contains iron contaminants. In turn, conventional agents used to prevent and remove iron are not normally effective in the presence of calcium and known calcium scale inhibiting agents. It has unexpectedly been found that conventional calcium scale inhibitors, such as, for example, organophosphonates and polyacrylates, can act effectively and efficiently in the presence of the present paired dihydroxy aromatic agents when the system being treated contains iron contaminants. In turn, the subject aromatic agents can exhibit effective removal of iron contaminants when used with calcium scale inhibitors. The calcium inhibitor and pair dihydroxy aromatic agent can be used in weight ratios of from 1:50 to 50:1, preferably from 1:10 to 10:1. The calcium inhibitor is most preferably maintained in from 0.1 to 10 ppm in the liquid of the system being treated. The exact amount will depend on the amounts of each contaminant present and can be determined by routine experimentation. The use of dihydroxy aromatic compounds, which contain electron-withdrawing substituents (either alone or in combination with known additives for cooling water) in aqueous solution, controls iron scale in cooling water systems. The result is to maintain equipment free from obstruction, maximize flow rates and heat transfer, and minimize corrosion and biological fouling. The aqueous solutions used in the methods of the invention comprise the dihydroxyaromatic compound (and optionally a calcium scale inhibitor) and may consist essentially of them. The following examples are given for illustrative purposes only. All parts and percentages are by weight unless otherwise specified. Examples 1-10 Test water was prepared and contained 99 parts per million (ppm) CaSO₄, 13 ppm CaCl₂, 55 ppm MgSO₄ and 176 ppm NaHCO₃. To 48.5 ml of this test water was added a solution of 5.1 mg of FeCl₃ 6H₂O in 1.5 ml of water. While stirring vigorously, the pH was adjusted to 8.1 with NaOH(ag) and then stirred for 2 hours. This resulted in the precipitation of an iron-containing solid, presumably FeO(OH) nH₂O. A second solution was prepared to contain 100 ppm of the additive (as listed in Table I) in 50 ml of the test solution at pH 8.1. The two solutions were combined, and the mixture was stirred at 54°C for 17 hours. The mixture was then filtered through a 0.1 micron membrane, and the amount of dissolved iron was determined by atomic absorption. Results are listed in Table I. Examples 1-6 are not part of the present invention but are included for comparative purposes. Example Additive (50 ppm) Dissolved Iron (ppm) 1 none 0.1 2 Ethylenediaminetetraacetic acid 0.25 3 iethylenetriaminepentaacetic acid 0.61 4 Hydroxyethylidene-1,1-diphosphonic acid 0.37 5 Aminotrimethylenephosphonic acid 0.38 6 Catechol 0.38 7 Catechol-4-sulfonic acid 4.8 8 4-nitrocatechol 5.3 9 Catechol-3,5-disulfonic acid 6.8 10 3,4-dihydroxybenzoic acid 2.3 From the results given above it is clearly evident that the method using the presently required compounds provides a far superior means of dissolving iron solids than representative known materials conventionally used for this purpose. Examples 11-15 A solution of 50 ppm of the additive in the test water at pH 8.1 was combined with 1000 ppm Fe₂O₃ (hematite, particle size = 0-10 microns). This mixture was stirred for 17 hours at 54°C, then allowed to settle, undisturbed for 1 hour. A sample as removed at 50% depth and analyzed for Fe by atomic absorption (after dissolution with HCl). Results are listed in Table II. Examples 11-13 are not part of the present invention but are included for comparative purposes. Example Additive (50 ppm) Dispersed Fe₂O₃ (ppm) 11 none ≦30 12 Diethylenetriaminepentaacetic acid ≦30 13 Aminotrimethylenephosphonic acid ≦30 14 Catechol-4-sulfonic acid 460 15 Catechol-3,5-disulfonic acid 580 Example 16 Weighed mild steel coupons were pre-corroded by suspending vertically above an aerated saline solution (1% NaCl) for 24 hours. This process was found to give a deposit weight of 700 mg ± 15%. Two pre-corroded coupons were suspended in a tall form beaker containing 900 ml of the solution under test. The test solution having a pH of 7.0 - 7.5 contains an additive according to table III below, 500 ppm Ca²⁺, 100 ppm Mg²⁺, at 500 r.p.m., 25°C. At the end of this period the coupons were removed and a 50 cm³ sample of solution taken. This sample was filtered through a 0.2 micron filter paper, acidified with two drops of 1:1 HCl and analyzed for total iron with atomic absorption. The steel coupons were dried at 100°C for 1 hour and weighed. The coupons were then cleaned with inhibited HCl, washed with water and acetone and reweighed in order to determine the final weight of deposit. The results of this test are expressed in terms of both soluble iron and also the percentage of deposit removal. Additive Dosage, ppm Deposit Removal % Soluble Fe, ppm Blank 0 0 0.1 Catechol-4-sulfonic acid 1,500 62 75 Catechol-3,5-disulfonic acid 1,500 56 114 Table III illustrates the capability of the presently required compounds to remove rust in hard water. Examples 17-19 All iron interference tests for calcium carbonate threshold inhibitors were performed in the following water: MgSO₄ . 7H₂O 266.1 ppm; CaCl₂ 234.8 ppm; CaSO₄.½H₂O 199.9 ppm; Na₂SO₄ 91.5 ppm; and NaHCO₃ 498.3 ppm. The test solution was prepared by adding to a 1000ml beaker, 1 ppm of hydroxyethylidene-1,1-diphosphonic acid (HEDPA) to the above water followed by the indicated amount of additive of Table IV and then in turn 1 ppm of ferrous ion obtained from an aqueous solution of ferrous sulphate. The total volume of the solution was made up to 750 ml. The solution was stirred at 500 rpm and heated in a water bath to 60°C. The pH of the solution was monitored and kept below pH 7.3 with addition of dilute HCl. On achieving the required temperature 0.066N NaOH was added at a rate of 0.3 ml/min using an automatic titrator. The pH was monitored and recorded during the titration. When calcium carbonate starts to precipitate a decrease or plateau in the pH is observed. This point is termed the critical pH. Threshold inhibitiors such as HEDPA act to increase the critical pH and thus decrease the scaling tendency of the water. When iron interferes with the HEDPA a decrease in its threshold activity is noted by a decrease in the critical pH. Results are summarized in Table IV. Example 17 is not part of the present invention but is included for comparative purposes. Example Additive Critical pH for Additive Concentration of: 0 ppm 1 ppm 5 ppm 10 ppm 17 Ethylenediaminetetraacetic acid 8.70 8.70 8.70 8.70 18 Catechol-4-sulfonic acid 8.70 8.70 8.95 9.00 19 Catechol-3,5-disulfonic acid 8.70 8.75 9.10 9.00 HEDPA gave a critical pH value of 9.10 in the absence of ferrous ion and a critical pH value of 8.70 in the presence of ferrous ion, which represents a significant loss in threshold activity. Therefore, a critical pH reading of 8.70 shows 0% activity by the indicated additive for the removal of the iron interference, while a critical pH reading of 9.10 represents a 100% activity. As shown in Table IV, ethylenediaminetetraacetic acid, a commonly used chelant, is completely ineffective for removing the iron interference for HEDPA, which is a calcium carbonate scale inhibitor. On the other hand, the addition of catechol-4-sulfonic acid or catechol-3,5-disulfonic acid at 5 ppm restored the majority of the threshold activity of HEDPA.

Claims: A method of removing iron contaminants from an aqueous system comprising introducing into the system an aqueous solution comprising a dihydroxylaromatic compound represented by the formula: Q―(Ar)―(OH)₂ wherein Ar represents a benzene aromatic moiety, Q represents at least one electron withdrawing group substituted on the Ar moiety, and the hydroxyl (OH) groups are substituted on the Ar moiety in ortho positions with respect to each other, to provide a concentration from 0.1 to 50,000 parts per million of the dihydroxylaromatic compound within the system, and removing portions of the aqueous system containing said iron contaminants. A method according to Claim 1, wherein the system is maintained at a pH of less than 9.5 and a temperature of less than 93 o C (200 o F). A method according to Claim 2, wherein the dihydroxyl aromatic compound is introduced into the said system to provide a concentration therein of from 500 to 5,000 ppm and wherein the system is maintained at a pH of from 6 to 9.5. A method of cleaning solid iron(III) corrosion products from systems comprising an aqueous/iron or iron base alloy interface which comprises introducing into the aqueous component of the system an aqueous solution comprising a dihydroxyaromatic compound represented by the formula: Q―(Ar)―(OH)₂ wherein Ar represents a benzene aromatic moiety, Q represents at least one electron withdrawing group substituted on the Ar moeity, and the hydroxyl groups are in ortho positions with respect to each other, to provide a concentration from 0.1 to 50,000 ppm of the compound within the system, contacting said aqueous component with the solid iron(III) product to dislodge and/or dissolve said products and removing portions of the aqueous system containing said corrosion products. A method according to Claim 4, wherein Q represents -SO₃H, SO₂R, -COOH, NO₂, -F, -Cl, -Br, -CHO, -COR, -CONH₂, -CONHR, -CONR₂, -PO₃H₂, a metal sulfonate salt, or a metal carboxylate salt and R is an alkyl group. A method according to any preceding claims, in which the aqueous system is rich in calcium and in which a calcium scale inhibitor is also introduced into the aqueous system in a weight ratio of from 1/50 to 50/1 of the scale inhibitor to the dihydroxylaromatic compound. A method according to Claim 6, wherein the scale inhibitor is an organophosphonate or a polyacrylate. A method according to Claim 6 or 7, wherein the scale inhibitor and dihydroxyl aromatic compound are in a weight ratio of from 1:10 to 10:1. A method according to any one of the preceding Claims, wherein the dihydroxyl aromatic compound is introduced into the said system to provide a concentration of from 1 to 2000 ppm of the dihydroxylaromatic compound within the system. A method according to any one of the preceding Claims, wherein Q represents SO₃H, COOH, NO₂, a metal sulfonate salt or a metal carboxylate salt. A method according to Claim 10, wherein the dihydroxy aromatic compound is 3,4-dihydroxy benzenesulfonic acid, 3,4-dihydroxybenzoic acid, 4,5-dihydroxy-1,3-benzenedisulfonic acid, a salt of one of said acid, or 4-nitro-1,2-benzenediol. A method according to any one of the preceding Claims, wherein the aqueous component of the system further comprises a water treatment agent which is a chelant, scale inhibitor, pH regulator, dispersant, corrosion inhibitor, or biocide.

Inventors: HENRY WAYNE LAMAR, KELLY JOHN ARTHUR, KREH ROBERT PAUL, KUHN VINCENT ROBERT, LUNDQUIST JOSEPH THEODORE, HENRY, WAYNE LAMAR, KELLY, JOHN ARTHUR, KREH, ROBERT PAUL, KUHN, VINCENT ROBERT, LUNDQUIST, JOSEPH THEODORE
Applicants: GRACE W R & CO, W.R. GRACE & CO.-CONN.
Application year: 1989
Main classification: C02F1
IPC codes: C02F5, C23F11, C09K15, C23G1