Superconductive photoconductive-substance of the Ca-Sr-Bi-Cu-O group system and a method for producing the same

Abstract: The disclosed oxide has a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, and the oxide shows, at a temperature below 105 to 115 K, both a photoconductivity and an either real or potential superconductivity, namely, "superconductive photo­ conductivity" in a wavelength range of 530 to 740 nm. The oxide is made by heating a mixture of starting materials for the above composition of Ca X-x -Sr x -Bi Y-y -Cu y -O z at 700-850°C for 2-10 hours so as to effect primary sintering for causing solid phase reactions in the mixture, cooling gradually, shaping under pressure, reheating the shaped materials at 750-880°C for 2-10 hours so as to effect secondary sintering thereon, cooling, keeping the reheated materials at 500-600°C for 2-3 hours and cooling the same either extremely quickly at a rate of 1500-900°C/s or slowly at a rate of 150-200°C/hour.

Description: This invention relates to superconductive photoconductive-substance of Ca-Sr-Bi-Cu-O group system and a method for producing the same, which oxide has a composition outside that of regular superconductor and exhibits a photoconductivity along with an either real or potential superconductivity. As an outcome of experiments on optical properties, especially on the photoconductivity in response to high-speed laser pulses, of those oxides whose composition falls outside the critical composition range of regular superconductor, the inventor has succeeded in finding a superconductive oxide of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z group that reveals photoconductivity which is unexpected from the standpoint of conventional common sense. The invention is based on such findings. The invention also relates to a method for producing the above oxide. In the method, the ingredient concentrations X, x, Y, y and z in the above-mentioned general formula are controlled, for instance by selecting X=2, Y=3, y=2, and a photoconductive oxide with an either real or potential superconductivity is produced by keeping the above concentration x close to zero in the 0≦x<1 range or by cooling extremely quickly. The oxide of the invention is expected to be very useful in the industrial field of "superconductive optoelectronics". There has been no publications at all on such superconductor which has inherent photoconductivity, except the inventor's disclosure in his technical papers and his patent applications; for instance, a super-conductive photoconductive oxide of Y (3-x) -Ba x -Cu y -O z group (U.S. Patent Application Serial No. 244,240) and a superconductive photoconductive oxide of La₂-Cu₁-O z group (U.S. Patent Application Serial No. 244,274). In J. Phys., Vol. 30, No. 5, May 1988, pp. L473-476, there is disclosed a superconductive oxide of the formula BiSr 0.5 Ca 1.5 Cu₂O x . There is no disclosure, however, of this oxide exhibiting photoconductivity. Conventional superconductors are metals or alloys thereof in the main. Recently, much attention has been paid to high-temperature oxide superconductors, such as superconductors of Y-Ba-Cu-O group, and considerable amounts of additives such as barium (Ba) and strontium (Sr) are used to raise the superconductive critical temperature (Tc). In view of the metallic properties of such superconductive substance, studies and measurements on their optical properties at and in the proximity of visible wavelengths have been limited to the study of reflection and scattering of light therefrom as a part of the study on overall nature of the metal. In general, it has been believed that light is simply reflected from the surface of a superconductor and is not allowed to enter therein. Study of optical properties, except the phenomena of reflection and scattering, has been treated as a completely different field from that of superconductivity. This has been a main trend in academic institutions, domestic and abroad, and in international conferences. The reason for the trend is in that researchers have considered that superconductivity is incompatible with such physical properties as light absorption and photoconductivity and they have assumed that light irradiation in a wave number with the excess energy over the energy gap of the BCS theory will merely destroy the stability of superconductivity. However, there is a certain clear correlation between them, as proven in the case of Y-Ba-Cu-O group substance and the like. If any substance having both superconductive capability and photoconductive capability is produced, a number of new electronic and optoelectronic devices may be developed; for instance, a superconductive phototransistor, a "superconductive optical computer" as a combination of the "superconductive computer" based on the Josephson devices and the "optical computer" proposed in optoelectronics both currently studied, "superconductive optical fiber", and the like. Therefore, an object of the present invention is to provide superconductive photoconductive-substance which reveals a superconductive photoconductivity, i.e., both a superconductivity and a photoconductivity at a temperature below its critical temperature for revealing the superconductivity. According to the present invention there is provided the use of a substance with a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2. and z being 4 to 9, wherein said substance has a photoconductivity Q (λ, T) at a temperature (T) below 105 to 115 K, upon photoexcitation in a range of wavelength of 530 to 740 nm. According to a further aspect of the invention there is provided a substance with a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , X being 2 to 3, 0≦x≦0.1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, wherein said substance has a photoconductivity Q (λ, T) at a temperature (T) below 105 to 115 K upon photoexcitation in a range of wavelength of 530 to 740 nm. According to another aspect of the invention there is provided a method for eliciting the photoconductivity of a photoconductive-substance of the Ca-Sr-Bi-Cu-O system having a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -0 z , X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, wherein said substance has a photoconductivity Q (λ, T), comprising the step of exposing said photoconductive substance to incident light of wavelength (λ) of 530 to 740 nm, at a temperature (T) below 105 to 115 K. Another object of the present in invention is to provide a method for producing the above-mentioned superconductive photoconductive-substance with a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, which method comprises steps of preparing a mixture of starting materials for the above substance, heating the mixture at 700-850°C for 2-10 hours, gradually cooling, shaping under pressure, reheating at 750-880°C for secondary sintering, cooling gradually, keeping at 600-500°C for 2-3 hours, and then cooling either extremely quickly at a rate of 1500-900°C/sec or slowly at a rate of 150-200°C/hour, whereby the substance becomes to have a photoconductivity associated with a superconductivity or to have both a superconductivity and a photoconductivity. The reason for limiting the composition of the substance of the invention to the above-mentioned general chemical formula is in that the substance of such composition reveals a photoconductivity associated with a superconductivity, or reveals both a superconductivity and a photoconductivity, provided that it is treated by the method of the invention; namely, through the steps of heating at about 700-850°C for 2-10 hours so as to cause solid phase reactions among starting materials thereof, cooling gradually, shaping under pressure, secondarily sintering at 750-880°C for 2-10 hours, cooling gradually, keeping at 600-500°C for 2-3 hours, and then cooling either extremely quickly at a rate of 1500-900°C/sec or slowly at a rate of 150-200°C/hour. As shown in the ensuing embodiments, the substance thus produced has such temperature dependence and exciting light wavelength dependence that it reveals potential superconductivity in a domain of insulating substance. The invention has been accomplished based on systematic studies of the above phenomena. Most of conventionally known oxide substances, such as Ba-Pb-Bi-O, La-Cu-O, and Y-Ba-Cu-O, are normally insulators or semiconductors at the ground state, e.g., at low temperatures and in the dark. An elementary excitation can be created by giving a suitable amount of energy with the corresponding momentum. Usually, for superconductors, these excitations beyond the energy gap merely destroy the superconductive ground stage in the BCS theory. There is a possibility, however, to create a coherent state of elementary excitations above the ground state of insulating semiconductors such as bipolarons and excitons even in a thermally non-equilibrium state. We have found a new substance as an outcome of studies in fundamental physics and applied physics from the standpoint of the elementary excitation concept, in a sense parallel to, but rather orthogonal to the trend of studies of high-Tc (critical temperature) superconductors. Namely, our finding relates to substance whose compositions does not result in perfect superconductor, but the substance has a composition close to that of superconductor and reveals both a superconductivity and a photoconductivity. The present invention has been completed based on that finding. The reason for selecting the general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and Z being 4 to 9, as a limitation of the composition of the substance of the invention, is in that x=1 is excluded because the composition with X being 2 to 3, Y being 3 to 4 and x=1∼2 results in a superconductor. The inventor has studied such composition range in the proximity of but outside that of superconductor which might have both a superconductivity and a photoconductivity, and they have found that an oxide with X Being 2 to 3, Y being 3 to 4 and 0≦x<1 becomes an insulator or a semiconductor, but such insulating or semiconducting oxide reveals a photoconductivity in response to incident light of specific frequencies, i.e., 500-740 nm in terms of wavelength. The inventor noted the fact that Bi₂O₃ shows a photoconductivity in response to visible light of certain frequencies, and he has tried to find out metallic elements which, when added, render the Bi₂O₃-based substanc both superconductive and photoconductive. In particular, addition of Ca, Sr, and Cu has been studied, and as a result, the oxide composition for photoconductive-substance of the above general chemical formula has been invented, which composition is similar to that of superconductor but does not provide a complete superconductivity. The concentration range of 0≦x<1, 0<y≦2, 4≦z≦9 along with X being 2 to 3 and Y being 3 to 4 in the above-mentioned general chemical formula is the condition necessary for making the oxide of the invention potentially superconductive and photoconductive, i.e. superconductive photoconductive-substance. When x=0, the oxide becomes Ca x -Sr x -Bi (Y-y) -Cu y -O z and this oxide also falls within the scope of the invention. The reasons for the limitations in the method of the invention will be described now. The two sintering processes, i.e., a primary sintering process of heating at 700-850°C for 2-10 hours so as to cause solid phase reactions among starting materials followed by the gradual cooling, shaping under presure, and a secondary sintering process of heating at 750-880°C for 2-10 hours followed by the gradual cooling, are necessary to effect complete solid phase reactions so as to produce homogeneous solid phase. In the sintering, heating above 880°C is undesirable because it tends to cause melting, while heating below 700-750°C is undesirable because it cannot fulfill the complete solid phase reactions. The process of keeping at 500-600°C for 2-3 hours is for annealing in order to remove strains and to homogenize the alloy, which strains are caused during the machining for the shaping under pressure and by the secondary sintering. The cooling after the annealing, either extremely quickly at a rate of 1500-900°C/sec or slowly at a rate of 150-200°C/hour, is to regulating the oxygen concentration z in the expression of O z . In the extremely quenching, the faster the cooling is, the smaller the oxygen concentration z in Oz becomes. When the cooling is slow, the oxygen concentration z of O z is kept at a large value. For a better understanding of the invention, reference is made to the accompanying drawings, in which: Figs. 1A and 1B are diagrammatic illustrations of the principles of photoconductivity measurement by using blocking electrodes and applying repetitive pulses; Fig. 1C shows the time sequence and waveforms of electric field, and laser light pulses in the photoconductivity measurement; Fig. 2A show sectional views of an essential part of a static susceptibility measuring device using a microwave SQUID (Superconducting Quantum Interference Device) at 9 GHz; Fig. 2B is a block diagram of the measuring system with the device of Fig. 2A; Fig. 2C is a block diagram of the feedback system with the device of Fig. 2A; Fig. 3A is a graph showing the wavelength-dependence of photoresponse Q(λ, T) of reference substance Bi₂O₃; Fig. 3B is a graph showing the wavelength-dependence of photoresponse Q(λ, T) of a superconductive photoconductive oxide of composition Ca 2-x -Sr x -Bi₁-Cu₂-O z (x=0); Fig. 4A is a graph showing the temperature-dependence of photoresponse Q(λ, T) of the reference substance Bi₂O₃ for wavelength λ=660 nm; Fig. 4B is a graph showing the temperature-dependence of photoresponse Q(λ, T) of a superconductive photoconductive-substance of composition Ca 2-x -Sr x -Bi₁-Cu₂-O z (x=0) for wavelength λ=580 nm; Fig. 4C is a graph showing the temperature-dependence of the dark resistance R(T) of a superconductive substance of composition Ca (2-x) -Sr x -Bi₁-Cu₂-O z (x=1); and Fig. 5A and Fig. 5B are graphs showing the relationship between the energy E and the density of state N(E) in the oxide of composition Ca 2-x -Sr x -Bi₁-Cu₂-O z , for the cases of x=0 and x=1, respectively. Embodiments An example of the oxide composition of the invention is Ca (2-x) Sr x Bi (3-y) Cu y O z , and the inventor has carried out a composition, with emphasis on the effects of composition, i.e., the change in the phase diagram due to variation in the concentrations x and y. The inventor's studies covered not only the superconductive phase but also the semiconductive phase and insulating phase. A large number of specimens of Ca (2-x) Sr x Bi (3-y) Cu y O z group were made from powders of CaCO₃, SrCO₃, Bi₂O₃, and CuO. The effect of the starting material composition on the concentrations x and y was checked in detail, and it was found that the concentrations x and y can be controlled by adjusting the starting composition. It was also found that the oxygen concentration z could be controlled, to a certain extent, by regulating the temperature of the secondary sintering and by selecting the rate of cooling after the annealing. Specimen #S127 was made by preparing a mixture of 0.400g of CaCO₃, 0.466g of Bi₂O₃, 0.318g of CuO and firing the mixture so as to produce Ca₂Bi₁Cu₂O z . Specimen #S170 was made by preparing a mixture of 0.200g of CaCO₃, 0.295g of SrCO₃, 0.465g of Bi₂O₃, 0.318g of CuO and firing the mixture so as to produce Ca₁Sr₁Bi₁Cu₂O z . The value of z, i.e., the oxygen concentration, in the above chemical formula was controlled in a range of 5 to 8 by carefully regulating the sintering temperature and the method and speed of cooling. The physical properties of the oxide varied depending on the oxygen concentration z therein. Starting materials of each specimen were measured so as to be mixed at proper ratios for the desired compositon, and the mixture was stirred up thoroughly, heated at 700-850°C for 2 hours so as to effect the solid phase reactions of primary sintering, cooled gradually, and shaped into pellets under pressure. The pellets were reheated at 750-880°C for 2 to 3 hours for effecting secondary sintering. The specimen #S127 was held at 500°C for 2 hours and cooled gradually. On the other hand, the specimen #S170 was annealed by reheating at 800°C for 2 hours and keeping at 500°C for 1 to 2 hours, and then cooled gradually to room temperature. Test method The phase diagram of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z group Oxide is complicated, because the oxide is of 5-element system, and the result of the inventor's study is not yet exhaustive and further studies are necessary to clarify details of the diagram. Very important factors are combinations of the element concentrations X, x, Y, and y in the composition and the control of the oxygen concentration z corresponding to the oxygen vacancy. Despite enormous efforts of a large number of scientists, we have to wait for sometime before the completion of the study. The inventor has paid attention not only to the superconductive phase but also to semiconductive phase. With a number of specimens of Ca-Sr-Bi-Cu-O group made from powders of CaCO₃, SrCO₃, Bi₂O₃, and CuO, detailed studies were made on ratio of starting materials in a mixture for each specimen, the process of quick or slow cooling, and the composition was found to be controllable to a certain extent. Since specimens or the Ca (2-x) Sr x Bi (3-y) Cu y O z group had a very high resistance within a certain value range of x, y and z, or they were semiconductive at least in a low temperature range, two types of techniques were used for the measurement of the resistivity and conductivity. First, to measure the insulating specimen (ρ≧10⁸ Ω-cm), such as the specimen #S127 at 4.2 K, a fast pulse technique with blocking electrodes as shown in Fig. 1A was adopted. Difficulties noted in the preceding applications were overcome by using the fast pulse technique. Transverse mode electrode disposition, as shown in Fig. 1B, was also used for certain measurements. In actual measurement, each electric field pulse E of up to E≃5 kV/cm has a duration of 10 ms at a repetition frequency of 13 Hz, and exciting light beam pulses of 3 ns width were synchronized with the electric field pulses so that each light beam coincides within a certain portion of the electric field pulse E as shown in Fig. 1C. Second, for moderately conductive specimens such as the specimen #S170 (ρ≦10⁻²-10⁻¹ Ω-cm), regular resistive measurements were carried out by adopting the usual four-probe method in the dark without using the exciting light. Static magnetic susceptibility or magnitude of magnetization M(T,H) was measured in weak fields up to H≃500 Oe by using a microwave SQUID (Superconducting Quantum Interference Device) at 9 GHz as shown in Figs. 2A, 2B and 2C, in a similar manner to that in the above-mentioned U.S. Patent Application Serial Nos. 244,240 and 244,274. In the measurement of photoconductivity, optical excitation was effected by using a pulsed dye laser. Spectral responses can be of the order of 10¹² cm⁻³ also carefully studied in detail. The density of excited photocarriers was of the order of 10⁵ to 10⁷/cm³, and when the absorption coefficient is large, they can be of the order of 10¹² cm⁻³ in a thin surface layer of 10⁻³ to 10⁻⁴ cm thickness. All photosignals were normal detected in the synchronized mode by using the Boxcar integrator. Experimental Results The specimen of Ca (2-x) Sr x Bi₁Cu₂O z (x=1), such as the specimen #S170, looks black, and its resistivity at room temperature is of the order of ρ ≦10⁻¹ Ω-cm. On the other hand, the specimen of Ca (2-x) Sr x Bi₁Cu₂O z (x=0), such as the specimen #S127, looked gray, and its resistivity at room temperature is as high as ρ ≧10⁸ Ω-cm. The inventor's measurement of the specimen #S127 (x=0, semiconductive) by the above-mentioned transient pulse technique proved that signals indicative of photoconductivity definitely appear at both of two temperatures below 105-115 K and below 65-85 K, probably due to two different mixed phase mechanism. It is noted at first that, as to the electric field (E) dependence of the photoresponse Q(λ, T, E), it is substantially linear at about 4.2 K up to E≃5 kV/cm. Fig. 3A illustrates a typical spectrum of pulse-excited transient photoresponse Q(λ, T) of the reference specimen #B03, i.e., Bi₂O₃, over wavelength λ of about 500-740 nm, and Fig. 3B illustrates a similar spectrum of the specimen #S127, i.e., Ca (2-x) Sr x Bi₁Cu₂O z (x=0). It is noted here that the curve of Fig. 3A is probably the first disclosure of this kind technical knowledge in the world, which relates to the photoconductivity of Bi₂O₃ corresponding to light absorption at low temperatures, thereby the curve will be used as a standard reference in the future. The curve was drawn based on the measured data obtained by the inventor. Next, temperature dependence of the pulse-excited transient photoresponse Q(λ, T) in the wavelengths λ of about 530-740 nm was studied by using the reference specimen #SB03, i.e., Bi₂O₃, and the semiconductive specimen #S127, as shown in Fig. 4A and Fig. 4B, respectively. Surprisingly, there definitely exists a systematic similarity in general characteristics of the transient photoresponse Q(λ, T) between the specimens #B03 and #S127. As clearly recognized by anybody from Figs. 4A and 4B, with decreasing temperature, the "photoresponse" appears at temperatures below 105-115 K and below 65-85 K, even in the semiconductive specimen, as if potential superconductivity exists, and the photoresponse Q increases monotonously and increases again at the temperature below 10 K depending on the case. Finally, Fig. 4C shows the dark resistivity ρ(T) of superconductive specimen #S170, i.e., Ca₁Sr₁Bi₁Cu₂O z . As can be noticed immediately by anybody, the specimen #S170 shows superconductivity at a temperature below 105-115 K and at a temperature below 65-85 K, and the photoresponse Q(λ, T) coincides with it surprisingly well as shown in Fig. 4B. It is by no means easy to interpret these experimental facts. Careful checking and evaluation show that heating effects of specimen by the exciting light is very small. At 300 K, the specimen #S127 Ca (2-x) Sr x Bi₁Cu₂O z (x=0) behaves like a semiconductor. Its "photoconductivity" observed with the blocking electrodes probably has close correlation with the "superconductivity" of the superconductive specimen #S170. This is probably due to the superconductive characters of the insulating part of the specimen, as shown in Figs. 3A, 3B and Figs. 4A, 4B, 4C. Surprisingly, there exists an "occurrence of photoconductivity phenomenon" potentially correlative with superconductivity underlying even in the semiconducting specimen #S127 as displayed in Fig. 4B. Discussion It is a widely recognized fact that, of the oxides of Ca (2-x) Sr x Bi (3-y) Cu y O z group, a semiconductive specimen usually has gray color. The spectral photoresponse Q(λ, T) of Figs. 3A and 3B strongly suggests that there exists a region of the Bi₂O₃-like state in the specimen of Ca (2-x) Sr x Bi (3-y) Cu y O z group, if not atomic layers. Optical absorption and photoconductivity by Bi₂O₃ themselves have no been thoroughly analyzed yet in experiments at low temperature and in terms of the exciton theory. However, this seems to be a typical example of Frenkel type exciton of charge transferable type in a cation shell or a few neighbors. The position of the fine structure in the Q(λ, T) of the above-mentioned Ca-Sr-Bi-Cu-O group very well coincides with basic absorption end structure of the reference substance Bi₂O₃. The inventor can recognize a few outstanding fine structures which are probably due to the excitons. For instance, the spectra of photoresponse of Ca₂Bi₁Cu₂O z are similar to those of the reference substance Bi₂O₃. In the proximity of λ≃623 nm of the spectra, the inventor notices such structure which could be considered to correspond to the state of n=2 in an exciton series of Bi₂O₃. Thus, one can reasonably conceive that there exists at least a finite fraction of the Bi₂O₃-like phase in the Ca-Sr-Bi-Cu-O group oxides which fraction cannot be ignored. In the Bi₂O₃-like phase, the photoexcited electrons and/or holes are definitely mobile. (see Fig. 5A.) A conduction electron or a positive hole in standard types of Bi₂O₃ crystals has been reported to form a rather "small polaron" as discussed before in terms of the coupling constant α. In any case, the "occurrence of photoresponse Q(λ, T)" in insulating specimen is clearly related to the "occurrence of superconductivity", as if potential superconductivity exists in the photoconductivity phenomenon. The effects of the polaron, whether it is a "large polaron" with the LO (longitudinal optical)-phonons, a "small polaron" due to the Jahn-Teller effect or possibly an intermediate one due to both effects, must be substantial at least potentially just like the "polaron effects due to electronic polarization" are, as shown in Figs. 3A, 3B and Figs. 4A, 4B, 4C. The effects of such polaron are probably effective in a coherently hybridized form of these elementary excitations. Special attention must be paid to polarons due to electronic polarization, which are also referred to as "excitonic polarons". As an outcome from the examination of the result of the above experiments, the inventor has noticed close correlation between the polarons and excitons. Referring to Fig. 5A, these polarons and excitons had yielded out of the optical inter-band transition from the hybridized 2p-O and 6s-Bi valence bands leaving a (2p)⁶(6s)¹ positive hole (a white circle) to the 6p-Bi conduction band (possibly mixing with the Cu(4s, 3d) (not shown) depending on case) creating a (6p)¹ conduction electron together with the LO-phonon interaction. A polaron of Ca-Sr-Bi-Cu-O group oxide can be created either by the optical excitation here or substitution of Ca by Sr, as shown in Fig. 5B. Here, Fig. 5B refers to a superconductor with x=1. The positive hole in the 2p-O and 6s-Bi hybridized valence band can be produced from the many-body ground state through either chemical pressure induced intra-band or optically induced inter-band transition, and the electron correlation effects are of course very important. One must pay more attention to the dynamical valence fluctuation between Cu⁺¹ and Cu⁺², especially between Bi³⁺ and Bi⁵⁺, as well as between Bi³⁺ and Bi⁴⁺ and between Cu²⁺ and Cu³⁺. Therefore, for the mechanism of high-temperature superconductivity, one may reasonably conceive potential roles of an ensemble of polarons, whether large or small, and especially closely associated with excitons. The ensemble of united polarons and excitons here are probably a set of bipolarons, polaronic excitons and/or, most probably, "exciton-mediated bipolarons" due to the dynamical electron-phonon and electron correlation effects. It was confirmed that the Q(λ, T) of the Ca-Sr-Bi-Cu-O group oxide of Fig. 3B has a smaller wavelength dependence to that of the photoresponse Q(λ, T) of Bi₂O₃ of Fig. 3B in the wavelength range of 530-740 nm. Consequently, the inventor believes that these studies of elementary excitations here must reveal the nature of the superconducting ground state, despite the enormous difference in the carrier density. To the best knowledge of the inventor, this is the first clear experimental indications of the fact that the Ca-Sr-Bi-Cu-O group oxide has superconductive photoconductivity i.e. both a superconductivity and a photoconductivity. The polaron and exciton mechanisms, which were disclosed in the preceding patent applications of the inventor with respect to other high-Tc superconductors, have been experimentally confirmed to be displayed also in the oxide of the invention in a correlated manner. The inventor has found, through their experimental study of the physical properties of the Ca-Sr-Bi-Cu-O group superconductive photoconductive oxide, that the critical temperatures for photoconductivity in the oxide of the invention coincide with the critical temperatures for superconductivity expected in the conventional superconductors, i.e., 115-105 K (high-Tc layer) and 85-65 K (low-Tc layer). The inventor has also found, for the first time, the close correlation between the x-dependent "superconductivity" of the Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z group superconductive photoconductive oxide of the invention, e.g., at x=0, and the x-dependent "photoconductivity" of the same oxide, e.g., with x in the proximity of zero. Thus, the inventor reconfirmed the existence of the dynamical mechanisms due to polaron and exciton, i.e., the dynamical mechanisms due to "exciton-mediated bipolarons", in the high-Tc superconductivity. Effect of the Invention Based on the foregoing description, we may safely conclude as follows. We have confirmed the close correlation between "photoconductivity" and "superconductivity (zero resistance and diamagnetism)" in the temperature range of 4.2 to 300 K, on the basis of extensive studies including conductivity measurements performed by using the D.C. 4-probe method and the repetitive pulse photoconductivity measuring method and static susceptibility measurement by using the microwave SQUID. We have invented both the "superconductive photoconductive oxide" of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, and the method for producing such oxide. We have theoretically analyzed "the dynamical mechanisms due to polaron and exciton", or the mechanism due to "exciton-mediated bipolarons", in the "high-Tc superconductivity", and the invention was developed from such theoretical consideration. The proposed oxide of the invention will be open a new scientific and industrial field, to be named as "superconductive optoelectronics", wherein superconductivity is to be, whether directly or indirectly, controlled by light. Although the invention has been described with a certain degree of particularly, it must be understood that the present disclosure has been made only by way of example and that numerous changes in details may be resorted to.

Claims: Use of a substance with a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z as a photoconductor, x being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, wherein said substance has a photoconductivity Q (λ, T) at a temperature (T) below 105 to 115 K upon photoexcitation in a range of wavelength of 530 to 740 nm. Use according to Claim 1, in which 0 ≦ x ≦ 0.7. Use according to Claim 1, in which 0 ≦ x ≦ 0.1. Use according to Claim 1, in which x=0. Use according to any of Claims 1 to 4, in which y=2 and Y=3. Use according to Claim 1, in which x<0.5, y=2 and Y=3. A substance with a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , X being 2 to 3, 0≦x≦0.1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, wherein said substance has a photoconductivity Q (λ, T) at a temperature (T) below 105 to 115 K upon photoexcitation in a range of wavelength of 530 to 740 nm. A substance according to Claim 7, in which x=0. A substance according to Claim 7 or Claim 8, in which y=2 and Y=3. A substance with a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -O z , in which X is from 2 to 3, x<0.50, y=2, Y=3, and z is from 4 to 9, wherein said substance has a photoconductivity Q (λ, T) at a temperature (T) below 105 to 115 K upon photoexcitation in a range of wavelength of 530 to 740 nm. A method for eliciting the photoconductivity of a photoconductive-substance of the Ca-Sr-Bi-Cu-O system having a general chemical formula of Ca (X-x) -Sr x -Bi (Y-y) -Cu y -0 z , X being 2 to 3, 0≦x<1, Y being 3 to 4, 0<y≦2, and z being 4 to 9, wherein said substance has a photoconductivity Q (λ, T), comprising the step of exposing said photoconductive substance to incident light of wavelength (λ) of 530 to 740 nm, at a temperature (T) below 105 to 115 K. A method according to Claim 11, wherein said photoconductive substance is used in combination with a superconductive substance of Ca-Sr-Bi-Cu-O system and said photoconductive substance is kept below 105 to 115 K at which temperature said superconductor is superconductive.

Inventors: MASUMI TAIZO - UTSUKUSHIGAOKA, MASUMI, TAIZO 55-10 UTSUKUSHIGAOKA 4-CHOME
Applicants: UNIV TOKYO, THE UNIVERSITY OF TOKYO
Application year: 1989
Main classification: H01B12
IPC codes: H01L39, C01G29, H01B13, G02B6, H01B12, H01B1, C04B35, C01G1, H01S3