Triboelectrically processable powder coating

Abstract: The invention relates to a triboelectrically processable powder coating based on a polyester-containing binding agent and a nitrogen-containing additive. The nitrogen-containing additive is a sterically hindered tertiary amine or aminoalcohol.

Description: The invention relates to a triboelectrically processable powder coating based on a polyester-containing binding agent and a nitrogen-containing additive. Such a powder coating has previously been described in DE-A-3600395. Powder coatings are frequently sprayed onto earthed surfaces to be coated, using electric spray guns. Guns generating electrically charged particles by friction ('triboelectric') are used notably for the application of top coats on strongly curved articles comprising Faraday cages. It is difficult for powder coatings substantially based on polyesters to be applied via a triboelectric process, because they have a low charging potential. From DE-A-3600395 it is known that the addition of triethylamine does indeed have a positive effect on the chargeability of the particles. Triethylamine however decreases the stability of powder coatings because of an undesired catalytic activity with respect to the curing reaction if epoxy compounds are used in the binding agent. The invention provides a solution for this problem. The triboelectrically processable powder coating based on a polyester-containing binding agent and a nitrogen-containing additive is characterized in that the nitrogen-containing additive is a sterically hindered tertiary amine or aminoalcohol. The nitrogen-containing additives must show no or very small catalytic activity and thus not influencing the kinetic of the curing process. The nitrogen-containing additive should not decrease the gel time of the coating more than 2/3, preferably 5/6, compared to the gel time of the additive free system. According to a preferred embodiment of the invention, the sterically hindered tertiary amine or aminoalcohol is an amine having the formula: where R¹, R² and R³ are alkyl groups or aryl groups and where at least one of the R¹, R² and R³ groups is a branched alkyl group with at least 3 carbon atoms; and in case of an aminoalcohol, at least one of the three groups contains a hydroxylgroup. According to a preferred embodiment of the invention the nitrogen-containing additive is a sterically hindered tertiary amine containing at least two hydroxyl groups. Preferably the hindered tertiary amine or aminoalcohol is an amine having the formula where R¹, R² and R³ are alkyl groups or aryl groups and where at least one of the R¹, R² and R³ groups is a branched alkyl group with at least 3 carbon atoms, and where R¹, R² and/or R³ contain two hydroxyl groups. Preferably R¹ contains 1-10 carbon atoms, R² 1-10 carbon atoms and R³ 3-10 carbon atoms. According to a further preferred embodiment of the invention R³ contains at least 4 carbon atoms. The alkyl groups of the nitrogen-containing additive are preferably so branched that at the α-positions in respect of the nitrogen atom there is at least 1 carbon atom linked with two carbon atoms or that at the β-positions there are at least two carbon atoms each of them linked with three carbon atoms or 1 carbon atom is present linked with four carbon atoms. The nitrogen-containing additive preferably contains at α-and/or β-positions at least two, particularly at least three carbon atoms that are linked - as described above - with carbon atoms. According to a preferred embodiment of the invention, the sterically hindered tertiary amine or aminoalcohol applied is N,N-diisobutyl-3-amino-2,4-dimethylpentane. Other suitable sterically hindered tertiary amines are, for instance, N,N-dimethyl-3-amino-2,4-dimethylpentane and 2-methyl-N,N-bis(2-methylpropyl)-1-propaneamine. According to another preferred embodiment of the invention, the sterically hindered tertiary amine or aminoalcohol is tertiary butyldiethanol amine. Other suitable sterically hindered tertiary amines or aminoalcohols are, for instance, N,N-dimethyl-3-amino-2,4-dimethylpentane; 2-methyl-N,N-bis(2-methylolpropyl)-2-propaneamine; N,N-diethaynol-3-amino-2,4-dimethylpentane; diisopropylethanolamine and dimethylneopentanolamine. The nitrogen-containing additive according to the invention can be used in combination with other sterically hindered compounds such as, for instance, sterically hindered secondary amines or sterically hindered alcohols. According to a preferred embodiment of the invention the amount of nitrogen-containing additive is 0.01-10% (wt) calculated on the formulation powder coating composition. The polyesters that are used are carboxyl-functional polyesters or hydroxyl-functional polyesters. The binder system preferably contains 97-40% (wt) polyester, more particularly 95-50% (wt) polyester. The compound according to the invention can be used, for instance, in a powder coating the binding agent of which substantially comprises 94-90 parts by weight polyester with an acid number of between 10 and 80 and as curing agent 6-10 parts by weight epoxy compound. The epoxy compound applied may, for instance, be triglycidylisocyanurate (TGIC) or diglycidylterephthalate. However, by applying, for instance, epoxies based on bisphenol-A, it is possible also to produce binding agents in which the epoxy : polyester ratio is between 20 : 80 and 50 : 50. The polyester is preferably based on aromatic dicarboxylic acids, such as iso- and terephthalic acid, and aliphatic glycols such as, for instance, neopentyl glycol, butane diol and propylene glycol. According to a preferred embodiment of the invention the polyester for the triboelectrically processable powder coating based on aromatic acids and glycols is characterized in that a part of the glycols consist of a sterically hindered tertiary amine containing at least two hydroxyl groups. Trifunctional monomers such as, for instance, trimethylolpropane and trimellitic acid can be used in minor amounts. Optionally a tertiary amine can be used having three or more hydroxyl groups, so that this compound also serves as a branching agent. Mostly, the binder components, catalyst and additives are first melted and mixed in an extruder and subsequently cooled and ground to form a powder that can be used, for instance, for the coating of metal parts used particularly in the open air. The additives applied are, for instance, colourants, UV stabilizer, flow-promoting agents and antifoaming agents. The nitrogen-containing additive can be added to the binding agent during the cooling of the resin, during the cooking of the resin or, in the extruder, during the powder coating production process. The nitrogen-containing resin can be added to the curing agent, too. The sterically hindered tertiary amine containing at least two hydroxyl groups is added preferably during the preparation of the polyester, so that the additive is copolymerized. As a result, diffusion of the additive from the coating is avoided. The coating of a substrate with a powder coating is effected by spraying the present powder coating with a tribo system. Tribo systems are described, for instance, in Oppervlaktetechnieken (31) 1987, no. 2, pp. 28-31, and Farbe und Lack 10/1985, pp. 900-906. The invention will further be elucidated in the examples below without being limited thereto. Examples Examples I-V and Comparative Examples 1-2 Seven powder coatings were produced by mixing the components mentioned in Table I (in units by weight) in an extruder. As compound A N,N-diisobutyl-3-amino-2,4-dimethylpentane, as compound B N,N-dimethyl-3-amino-2,4-dimethyl-pentane, as compound C 2-methyl-N,N-bis-2-methylpropyl-1-propaneamine, as compound D diisopropylethanolamine, as compound E dimethylneopentanolamine and as comparative compound F triethylamine were used. Formulation I II III IV V 1 2 polyester 558 558 558 558 558 558 558 TGIC 42 42 42 42 42 42 42 TiO₂ 300 300 300 300 300 300 300 flow-prom. agent 9 9 9 9 9 9 9 benzoin 4.5 4.5 4.5 4.5 4.5 4.5 4.5 compound A 1 - - - - - - compound B - 0.6 - - - - - compound C - - 0.8 - - - - compound D - - - 0.64 - - - compound E - - - - 0.57 - - compound F - - - - - - 0.45 The chargeability and curing characteristics are mentioned in Table II. The gun used for the triboelectric spraying of the powder coatings was a Ransburg-Gema HT 100 gun. The DSC (differential scanning calorimetry) measurements were carried out on a Mettler TA 3000. In order to obtain a proper triboelectric process, chargeability up to at least 2 µA will be necessary. The measurements based on formulations I up to and including V and 1 show that the addition of additives containing sterically hindered nitrogen results in tribochargeability of the powder beyond 2 µA as well as in a good flow. The measurements based on formulation 2 show that the tribochargeability is indeed sufficient, but that this formulation results in such a high reactivity that the flow obtained is not good. Examples VI-VIII and Comparative Examples 3-5 In these Examples, respectively Comparative Examples, the effect of N,N-diisobutyl-3-amino-2,4-dimethylpentane (= 'Compound A') on the chargeability in hybride systems based on polyesters and epoxy resins was determined. Formulation VI VII VIII 3 4 5 parts by weight polyester (a.n.: 35) 420 - - 420 - - polyester (a.n.: 50) - 360 - - 360 - polyester (a.n.: 80) - - 300 - - 300 epoxy resin 180 240 300 180 240 300 TiO₂ 300 300 300 300 300 300 flow-promoting agent 9 9 9 9 9 9 benzoin 4.5 4.5 4.5 4.5 4.5 4.5 compound A 1 1 1 0 0 0 chargeability 3.5 4.0 2.2 1.0 1.0 0.8 gel time (sec) 145 120 130 145 115 130 Example IX A polyester resin was produced by esterifying 633 kg terephthalic acid, 13 kg trimethylolpropane, 478 kg neopentylglycol and 4 kg tertiary butyldiethanolamine for 12 hours at 250¤C to an OH-value of 38 during distillation of water. Subsequently, 93 kg isophthalic acid was added, followed by heating for three hours more until an acid number of 36 is reached. The polyester resin obtained was cooled and ground. After mixing in an extruder with 7% (wt) triglycidylisocyanurate (calculated on the polyester) and 50% (wt) titaniumdioxide (calculated on the binding agent), 1.5%. (wt) flow-promoting agent and 0.8% (wt) benzoin, the mixture was cooled and ground. The gun used for the triboelectric spraying of the powder coating was a Ransburg-Gema HT 100 gun. In order to obtain a proper triboelectric process, chargeability up to at least 2 µA will be necessary. The chargeability and curing characteristics were both good because they were respectively 2,2 µA and 160 seconds.

Claims: Triboelectrically processable powder coating based on a polyester-containing binding agent and a nitrogen-containing additive, characterized in that the nitrogen-containing additive is a sterically hindered tertiary amine or aminoalcohol. Powder coating according to claim 1, characterized in that the sterically hindered tertiary amine or aminoalcohol is an amine having the formula where R¹, R² and R³ are alkyl groups or aryl groups and where at least one of the R¹, R² and R³ groups is a branched alkyl group with at least 3 carbon atoms; and in case of an aminoalcohol, at least one of the three groups contains a hydroxylgroup. Powder coating according to claim 1, characterized in that the sterically hindered tertiary amine or aminoalcohol is an amine having the formula where R¹, R² and R³ are alkyl groups or aryl groups and where at least one of the R¹, R² and R³ groups is a branched alkyl group with at least 3 carbon atoms, and where R¹, R² and/or R³ contain two hydroxyl groups. Powder coating according to any of claims 2-3, characterized in that R¹ contains 1-10 carbon atoms, R² contains 1-10 carbon atoms and R³ contains 3-10 carbon atoms. Powder coating according to any one of claims 1-4, characterized in that the alkyl groups of the nitrogen-containing additive are so branched that at the α-positions in respect of the nitrogen atom there is at least 1 carbon atom linked with two carbon atoms or that at the β-positions there are at least two carbon atoms linked each of them with three carbon atoms or 1 carbon atom is present linked with four carbon atoms. Powder coating according to any one of claims 1-5 characterized in that the nitrogen containing additive is a sterically hindered tertiary amine or aminealcohol, which does not decrease the geltime of the coating more than 2/3 (compared to the geltime of the additive free system). Powder coating according to claim 6 characterized in that the nitrogen containing additive is a sterically hindered tertiary amine or aminealcohol, which does not decrease the geltime of the coating more than 5/6 (compared to the geltime of the additive free system). Powder coating according to any one of claims 1-7, characterized in that it has a chargeability of at least 2 µA. Powder coating according to any one of claims 1-8, characterized in that the sterically hindered tertiary amine or aminoalcohol used is N,N-diisobutyl-3-amino-2,4-dimethylpentane or tertiary butyldiethanolamine. Polyester for a triboelectrically processable powder coating based on aromatic diacids and glycols, characterized in that a part of the glycols consists of a sterically hindered tertiary amine containing two hydroxyl groups. Application of a powder coating according to any one of claims 1-9 or a polyester according to claim 10 in a tribo system. Process for coating a substrate with a powder coating according to any one of claims 1-9, in which process the powder coating is sprayed with a tribo system.

Inventors: BINDA PAUL HERMAN GUILLAUME, MISEV TOSKO ALEXANDER, BINDA, PAUL HERMAN GUILLAUME, MISEV, TOSKO ALEXANDER
Applicants: DSM NV, DSM N.V.
Application year: 1989
Main classification: C09D167
IPC codes: B05D7, C09D5, C08K5, B05D1, C08G63, C09D167