Preparation of bisphenols

Abstract: A process for the preparation of bisphenols which comprises reacting a phenol with a ketone in the presence of a cation exchange resin catalyst and a mercaptan co-catalyst in a reactor or a series of reactors wherein all of the phenol and a portion of the mercaptan is injected into the beginning of the reactor or the first reactor and the remaining mercaptan is injected along the reactor length or in the subsequent reactors whereby cyclic dimers formation is reduced.

Description: The present invention relates to a process for the preparation of bisphenols in the presence of ion-exchange resin catalysts using staged mercaptan co-catalyst addition to reduce the formation of cyclic dimers. Many processes are known to prepare bisphenols. In some of these processes, a phenol is reacted with a ketone to form the bisphenol. The reaction usually takes place in the presence of an acidic medium including inorganic acids and acidic cation exchange resins. In some cases a mercaptan, such as methyl mercaptan is used as a co-catalyst. In U.S. patent specification 2,730,552 is described the preparation of bisphenols in the presence of an inorganic mineral acid and a mercaptan co-catalyst. In such a process where the reactants are traditionally back-mixed, the water concentration is always high throughout the process. In British patent specification 785,079, which also describes the preparation of bisphenols in the presence of an inorganic mineral acid and a mercaptan co-catalyst, the ketone reagent is introduced to the reaction mixture in successive reaction stages and all of the phenol reagent is introduced to the first of these reaction stages, no preference being expressed as to the manner of introducing the mercaptan co-catalyst. However, in a process, such as described in British patent specification 1,185,102, which uses an ion-exchange resin catalyst, the reactor configuration is practically limited to a plug-flow reactor or a series of plug-flow reactors in which the activity of the ion-exchange resin catalyst is adversely affected by water formed in the reaction and therefore activity decreases sharply as the process progresses. Cyclic dimers by-product is a problem in such a process where mercaptan is added to increase the rate of reaction to achieve practical reaction rates when using an ion-exchange resin catalyst. The present invention is directed to a process for the preparation of bisphenols which comprises reacting a phenol with a ketone in the presence of an acidic cation exchange resin catalyst and a mercaptan co-catalyst in a reactor or a series of reactors wherein all of the phenol and a portion of the mercaptan is injected into the beginning of the reactor or the first reactor and the remaining mercaptan is injected along the reactor length or in the subsequent reactors whereby cyclic dimers formation is reduced. The process of staged mercaptan addition of the invention is based on Applicants' discovery that in cation exchange resin catalyzed preparation of bisphenols, little mercaptan co-catalyst is needed at the beginning of the reaction, where in the presence of low water concentrations it adversely effects the formation of undesirable cyclic dimers CDA, 1,3,3-trimethyl-6-hydroxy-3-(p-hydroxy)phenylindane, and CDB, 1,3,3-trimethyl-5-hydroxy-3-(p-hydroxy)phenylindane. By the present process of limiting the amount of mercaptan at the beginning of the reaction, where water concentration is low, the formation of undesired cyclic dimers is significantly reduced. The bisphenols prepared by the process of the invention include those prepared by the reaction of a ketone, such as acetone, ethyl methyl ketone, isobutyl methyl ketone, acetophenone, cyclohexanone, 1,3-dichloroacetone and the like, with a phenol, such as phenol, o-cresol, m-cresol, o-chlorophenol, m-chlorophenol, o-t-butylphenol, 2,5-xylenol, 2,5-di-t-butylphenol o-phenylphenol and the like. The above is not meant to limit the invention but to illustrate representative examples of ketones and phenols which are known in the art to make desirable bisphenol and for which those of skill in the art can substitute other conventional bisphenol reactants. In the preparation of the bisphenols, an excess of the phenol is usually desirable, generally from 5 to 20 moles of phenol per mole of ketone, is desirable for high conversion of the ketone. Solvents or diluents are not necessary in the preparation of the bisphenol except at low temperature. The ketone is usually introduced in stages such that from 25-75% weight of the ketone is injected into the beginning of the reactor or the first reactor, preferably from 40-50% weight. The catalysts for the process are acidic cation exchange resins. Such resins which can be used as catalysts are conventionally known in the art and include those acidic cation exchange resins that are unmodified with a mercapto modifying agent before use in the process, but which are used with the addition of a free mercaptan co-catalyst. The resin is essentially not modified to any substantial degree with the free mercaptan. The free mercaptan can be any free mercaptan of the type conventionally known in the art which includes any compound which will not react to any substantial degree under the process conditions with the acidic groups of the cation exchange resin to introduce a mercaptan substituent into the resin. Suitable mercaptan co-catalyst include those of the formula RSH in which R is hydrogen or an organic group such as aliphatic, cycloaliphatic, aryl or heterocyclic compounds containing one or more free mercaptan groups. For convenience, the mercaptan usually is a non-resinous compound containing from 1 to 20 carbon atoms. The mercaptan can contain other substituent groups, such as alkoxy, aryloxy, carboxy or hydroxy. For example, the free mercaptans include methyl mercaptan, dithioethane, ethyl mercaptan, n-pentyl mercaptan, thioglycolic acid, 1,2-dimercapto ethane, 3-mercaptopropionic acid and the like. Alkyl mercaptans are preferred, especially methyl mercaptan. The amount of mercaptan present can vary with the resin used but is usually present in a lesser amount compared to the resin. For example, the mercaptan is present from 1 mole percent to 100 mole percent based on the resin and preferably from 5 to 50 moles percent. The amount of mercaptan co-catalyst injected into the beginning of the reactor or the first reactor is from 30% to 60% weight of the total mercaptan to be used, preferably from 40% to 50% weight. The mercaptan can be injected with the ketone or separately. The remainder is added after the ketone fed to the first stage or earlier stage is substantially converted to the desired bisphenol. The effectiveness of the resin catalysts in the process of the invention is to some extent influenced by their exchange capacities such that the greater the exchange capacity then the more desirable the resin is for the condensation. Preferably, the cation exchange capacity is at least 0.5 and, preferably, greater than 4.0 meq/g dry weight. Also, those cation exchange resins having bound cationic exchange groups of the stronger exchange potential acids are preferred for use in the resin and free mercaptan co-catalyst process of the present invention. Acidic cation exchange resins suitable for use with a free mercaptan co-catalyst include sulfonated styrene-divinylbenzene copolymers, sulfonated cross-linked styrene polymers, phenol-formaldehyde-sulfonic acid resins, benzene-formaldehyde-sulfonic acid resins and the like. These include resins under such tradenames as Amberlites (Rohm and Haas Co.), DOWEX® (Dow Chemical Co.), Permutit QH (Permutit CO.), CHempro (Chemical Process Co,) and Lewatit (Bayer A.G.). Strong acid sulfonated styrene-divinylbenzene copolymers are preferred. Both modified macroreticular resins and microreticular resins are useful in the isomerization process of the present invention. The choice of resin will of course depend on the bisphenol material to be prepared, the reaction conditions and the effect of an individual resin under the conditions selected, which determination and selection is within the skill of the art. When the aromatic sulfonic acid resins are obtained as sodium salts, they are converted to the acid form prior to use. The precise amount of acidic cation exchange resin to be used will vary to some degree depending on the specific resin, feed and conditions used for the process. By way of illustration, the catalyst can be present from 0.05 kg per kg of feed to 10.0 kg per kg of feed and, preferably, from 0.2 kg to 2 kg per kg of feed. Thus, the reaction is conducted by contacting a feed stream containing a phenol with an acidic cationic exchange resin and free mercaptan co-catalyst under moderately elevated temperatures and usually in the presence of from 0 to 1% of water, preferably from 0.4 to 0.6% of water, based on the total feed. The feed stream passes through the resin catalyst in the presence of free mercaptan for a period of time sufficient to effect formation of the bisphenol depending on the feed rate, size of the resin bed, the particular resin and co-catalyst used and the like as can readily be determined by those of skill in the art. The resulting bisphenol is then recovered. Usually the recovered product is recycled back to a zone in which the bisphenol is prepared by condensation of a ketone (acetone) and phenol. The reaction time in the condensation depends on the reaction temperature and other reaction conditions, including whether the process is continuous or batch processing. The condensation reaction is conducted at moderately elevated temperature of from 50°C to 130°C at ambient pressures. The bisphenol product, e.g., bisphenol-A, is passed to a concentrator where the acetone, phenol, and free mercaptan and excess water are removed as an overhead fraction. The crude bisphenol-A product is then passed to a crystallization zone where it is chilled to a temperature between 30°C and 95°C to form an adduct of phenol and bisphenol-A which separates out as crystals. After washing of the adduct with phenol and filtering, the bisphenol-A is recovered from the adduct. As previously stated, the reactors are usually plug-flow reactors conventionally known in the art or equivalent kinds of reactors. EXAMPLES The following examples are provided for illustration purposes and should not be regarded as limiting the invention in any way. EXAMPLE 1 - Production of Bisphenol A (BPA) Two plug flow, adiabatic reactors containing Dow MSC-1 acidic ion-exchange resin were operated in series at an overall phenol to acetone mole ratio of 10. Acetone was staged by dividing it equally between the two reactors. The mixed feed temperature was 62°C for both reactor stages. Table 1 below compares results obtained when one-half percent by weight of reaction product of methylmercaptan co-catalyst was added with the acetone feed to the first reactor to results obtained when the same total amount of mercaptan feed was divided equally between the two reactors. Mercaptan Staged No Yes %w Water in Feed 0.1 0.1 WHSV in Reactor 1 3.3 3.3 WHSV in Reactor 2 1.6 1.6 Overall Conversion of Acetone 98% 98% Cyclic Dimers, ppm on BPA 5400 3700 WHSV is weight hourly space velocity. This experiment demonstrates that cyclic dimer production is reduced significantly by the staged mercaptan addition process of the present invention. EXAMPLE 2 - Production of Bisphenol A (BPA) Following procedures similar to those described in Example 1 above, staged and unstaged mercaptan addition was conducted with a feed water concentration of 0.1%w (case 1) and 0.5%w (case 2). Results are set forth in Table 2 below. Comparison of Staged to Unstaged Mercaptan Case 1 Case 2 Staged Unstaged Staged Unstaged Feed Water Content, %w 0.1 0.1 0.5 0.5 Feed Temperature, °C 62 62 62 62 Reactor 1 WHSV 3.3 3.3 3.3 3.3 Reactor 2 WHSV 1.6 1.6 1.05 1.05 Conversion 1 0.97 1 0.8 0.94 Conversion 2 0.96 0.96 0.97 0.96 CDA 1 3579 6358 2064 3328 CDA 2 2609 2609 2575 2374 CDA Overall 3081 4484 2378 2826 CDB 616 897 476 565 Total cyclic dimers, ppm on BPA 3697 5381 2854 3391 Ratio CDs (staged/unstaged) 0.68 - 0.84 - WHSV is weight hourly space velocity. CDA is 1,3,3-trimethyl-6-hydroxy-3-(p-hydroxy)phenylindane. CDB is 1,3,3-trimethyl-5-hydroxy-3-(p-hydroxy)phenylindane. These experiments demonstrate that cyclic dimer production is reduced significantly by the staged mercaptan addition process of the present invention.

Claims: A process for the preparation of bisphenols which comprises reacting a phenol with a ketone in the presence of an acidic cation exchange resin catalyst and a mercaptan co-catalyst in a reactor or a series of reactors wherein all of the phenol and a portion of the mercaptan is injected into the beginning of the reactor or the first reactor and the remaining mercaptan is injected along the reactor length or in the subsequent reactors. A process according to claim 1 wherein the co-catalyst is an alkyl mercaptan. A process according to claim 2 wherein the co-catalyst is methyl mercaptan or n-pentyl mercaptan. A process according to claim 1 wherein the resin is selected from sulfonated styrene-divinylbenzene copolymer, sulfonated cross-linked styrene polymer, phenol-formaldehyde-sulfonic acid resin and benzene formaldehyde-sulfonic acid resin. A process according to claim 4 wherein the resin is a macroreticular resin. A process according to claim 4 wherein the resin is a microreticular resin. A process according to any one of the claims 1-6 wherein the phenol is reacted with acetone.

Inventors: VAN SHAW PAUL, VAN SHAW, PAUL
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1989
Main classification: C07C39
IPC codes: C07C39, C07B61, C07C37, B01J31