Glass for projection cathode ray tube faceplate

Abstract: This invention relates to glass compositions especially suitable for projection cathode ray tube faceplates which are essentially free from PbO and other readily reducible metal oxides, fluorine, ZnO, TiO₂, and MgO, and which consist essentially, in weight percent, of Li₂O 0.75-3 Na₂O 5-7 K₂O 5-7 SrO 7.5-10 BaO 14-16 CaO 0-3 Li₂O+Na₂O+K₂O 11-16 CaO+SrO+BaO 21.5-26 Al₂O₃ 1-2 ZrO₂ 2-7 CeO₂ 0.4-0.8 SiO₂ 55-60.

Description: Background of the Invention This invention is directed to the production of glass compositions suitable for use as faceplates for projection cathode ray tubes; i.e., television picture tubes used to project images on a large screen. Faceplates for use in projection cathode ray tubes have been commercially fabricated for a number of years from glasses having compositions encompassed within U. S. Patent No. 4,277,286. The preferred glasses disclosed in that patent consisted essentially, in weight percent, of: SiO₂ 48-53 K₂O 5-6 SrO 3-7 Al₂O₃ 1-2 CeO₂ 0.4-0.8 BaO 14-16 ZnO 7-11 TiO₂ 0.5-1.0 CaO+SrO+BaO 18-24 Li₂O 1-3 ZrO₂ 2-7 Li₂O+Na₂O+K₂O 11-16 Na₂O 5-7 CaO 0-3 Those glasses exhibited exceptional absorptions of X-radiation (linear X-ray absorption coefficients at 0.6Å of at least 35 cm⁻¹) and very little browning from subjection to high velocity electron impingement. Those glasses do, however, demonstrate one undesirable feature; viz., faceplates prepared therefrom appear to be slightly yellow to the eye. This yellow coloration, caused by absorption in the blue end of the visible radiation spectrum, renders it necessary for the electron gun utilized in developing the blue color in the projection television system to be run "harder," i.e., to be operated at a higher voltage, than the electron guns used for generating the red and green colors. Hence, the yellow color is not only undesirable from an aesthetic standpoint, but also from a tube operation point of view. Therefore, the principal objective of the present invention was to devise glass compositions having the exceptional absorption of X-radiation and resistance to browning resulting from the impingement of high velocity electrons demonstrated by the glasses of Patent No. 4,277,286, but which would exhibit essentially no yellow color to the eye. Chemical Abstracts, Vol. 99, No. 24, 12 December 1983, page 275, Abstract No. 1995344c, Columbus, Ohio, US, discloses glass panels for cathode ray tubes containing SiO₂ 50-60%, Al₂O₃ 0.5-2%, Li₂O 0.3-2%, Na₂O 4-8%, K₂O 5-8%, SrO 8-12%, BaO 10-16%, ZnO 0-4.9%, MgO 0-4%, CaO 0-4%, ZrO₂ 2-4%, TiO₂ 0-2%, CeO₂ 0.1-1%, and Sb₂O₃ 0-0.5%, and have X-ray absorption coefficent ≧ 34cm⁻¹ at 0.6 Å wavelength. Chemical Abstracts, Vol. 101, No. 20, November 1984, page 304, Abstract No. 176263f, Columbus, Ohio, US, discloses panel glass for color cathode-ray tubes, wherein the glass has a base composition composed of SiO₂ 50-75%, Al₂O₃ 0-5%, CaO 0-4%, MgO 0-3%, SrO 0-13%, BaO 0-16%, PbO 0-3%, ZnO 0-3%, ZrO₂ 0-4% such that (SrO + BaO + PbO + ZnO + ZrO₂ = 5-25%), Li₂O 0-4%, Na₂O 3-15%, K₂O 3-15% such that (Na₂O + K₂O = 6-20%), TiO₂ 0-2%, and CeO₂ 0-3 wt.% and additionally contains Nd₂O₃ 0.1-6.0, Er₂O₃ 0.1-6.0%, and Cr₂O₃ 0-0.05 wt.%. This glass transmits red, green, and blue light of the phosphor and absorbs light having other wavelengths. Summary of the Invention As was observed in Patent No. 4,277,286, a glass designed for use as a cathode ray tube faceplate must possess a critical matrix of electrical and physical properties. Thus, the patent cited five properties which are required in faceplate glasses: (a) the electrical resistivity of the glass, when measured at 350°C, must be at least 10⁷ ohm-cm; (b) the linear coefficient of thermal expansion (0°-300°C) must not exceed 102x10⁻⁷/°C, and will preferably range between 95-100x10⁻⁷/°C; (c) the internal liquidus of the glass will be less than 900°C; (d) the strain point of the glass will not exceed 500°C; and (e) the softening point of the glass will be no higher than 690°C. To achieve those electrical and physical properties, the patent defines base compositions within the R₂O-RO-ZnO-ZrO₂-SiO₂ system wherein the ranges of the individual ingredients are quite narrowly delimited. (As employed in the patent, R₂O represents Li₂O+Na₂O+K₂O and RO consists of CaO+SrO+BaO). A combination of CeO₂+TiO₂ was employed to inhibit browning discoloration when the glass was exposed to X-radiation. I have found that the objectionable yellow color can be eliminated from the preferred glass compositions of Patent No. 4,277,286, thereby substantially improving the visible transmission of the glass, by removing TiO₂ from the composition. Then, in order to insure against browning of the glass when subjected to high velocity electrons, I have found that ZnO must be excluded from the composition and additional SrO substituted at least in part therefor to maintain the required X-radiation absorption character. Maintenance of the above-described matrix of electrical and physical properties which must be demonstrated by glasses designed for cathode ray tube faceplates is achieved through minor modifications in the concentrations of the other ingredients. In summary, I have found that glasses eminently suitable for use as faceplates for projection cathode ray tubes in being essentially free from a yellow color, in exhibiting linear X-radiation absorption coefficients at a wavelength of 0.6Å of at least 35 cm⁻¹, while displaying essentially no browning discoloration upon being subjected to high velocity electrons, and in demonstrating an electrical resistivity at 350°C of at least 10⁷ ohm-cm, a linear coefficient of thermal expansion (0°-300°C) not greater than 102x10⁻⁷/°C, preferably between 95-100x10⁻⁷/°C, an internal liquidus less than 900°C, a strain point not in excess of 500°C, and a softening point no higher than 690°C can be produced from compositions essentially free from PbO and other readily reducible metal oxides, fluorine, ZnO, TiO₂, and MgO, and which consist essentially, expressed in terms of weight percent on the oxide basis, of: Li₂O 0.75-3 Li₂O+Na₂O+K₂O 11-16 Na₂O 5-7 CaO+SrO+BaO 21.5-26 K₂O 5-7 Al₂O₃ 1-2 SrO 7.5-10 ZrO₂ 2-7 BaO 14-16 CeO₂ 0.4-0.8 CaO 0-3 SiO₂ 55-60 Where the use of a fining agent is deemed desirable, Sb₂O₃, rather than As₂O₃, will be selected because it is less readily reduced. Colorants conventionally used in cathode ray tube faceplate glasses, e.g., Co₃O₄, Cr₂O₃, and NiO, may be included in the customary levels, but, inasmuch as images from projection cathode ray tubes are not viewed directly, colorants are normally omitted from faceplates used in such tubes. Prior Art U. S. Patent No. 4,734,388 provides a fairly extensive survey of glass compositions wherein ZrO₂ is utilized in conjunction with SrO and BaO to impart high X-radiation absorption to a glass. None of the references, however, defines glasses expressly encompassed within the sharply delimited composition intervals of the present inventive glasses. Patent No. 4,277,286 is considered to be the most pertinent disclosure to the glasses of the instant invention. Description of Preferred Embodiments Table I presents a number of glass compositions, expressed in terms of parts by weight on the oxide basis, example 3 illustrating parameters of the instant invention. Inasmuch as the sum of the individual components totals or very closely approximates 100, for all practical purposes each of the recorded values may be deemed to reflect weight percent. The actual batch ingredients may comprise any materials, either oxides or other compounds, which, when melted together, will be converted into the desired oxides in the proper proportions. The batch constituents were compounded, ballmilled together to assist in securing a homogeneous melt, and charged into platinum crucibles. After placing lids thereon, the crucibles were introduced into a furnace operating at about 1500°C. After melting for about four hours with occasional stirring, the melts were allowed to stand for about 15 minutes to fine the glass. Thereafter, the melts were poured into steel molds to form glass slabs having dimensions of about 6″ x 6″ x 0.5″, and those slabs were transferred immediately to an annealer operating at about 520°C. Whereas the above description reflects laboratory practice, it will be appreciated that the compositions recited in Table I could be melted and formed in much larger quantities employing conventional commercial melting units and glass forming techniques. Sb₂O₃ was included in the batches to perform its function as a fining agent. 1 2 3 SiO₂ 51.51 52.32 57.53 Al₂O₃ 1.70 1.70 1.73 Na₂O 6.91 6.91 6.31 K₂O 5.10 5.10 5.71 Li₂O 1.00 1.00 0.99 BaO 14.90 14.90 15.02 SrO 6.40 6.40 8.66 ZnO 7.60 7.60 - ZrO₂ 3.00 3.00 2.99 CeO₂ 0.66 0.66 0.66 TiO₂ 0.82 0.01 - Sb₂O₃ 0.40 0.40 0.40 The minute amount of TiO₂ in Example 2 represents an impurity present in the batch materials. TiO₂ was purposely included in Example 1 only. Specimens were cut from the above glass slabs and Table II lists measurements of electrical and physical properties carried out on those specimens employing techniques conventional in the glass art. The softening point (Soft), annealing point (Ann), and strain point (Str) are reported in °C; the linear coefficient of thermal expansion over the 0°-300°C interval (Exp) is recorded in terms of x10⁻⁷/°C; the internal liquidus (Liq) is tabulated in °C; the electrical resistivity measured at 350°C is expressed in terms of Log ρ ; and the linear X-ray absorption coefficient at 0.6Å (Abs) is entered in terms of cm⁻¹. 1 2 3 Soft 679 678 675 Ann 512 506 493 Str 471 473 452 Exp 96.5 96.2 97 Liq 800 797 887 Log ρ 7.925 7.900 7.670 Abs 39.8 39.8 35.5 Visible transmittance spectra were measured spectrophotometrically on samples of Examples 1, 2, and 3 having thicknesses approximating 6.35 mm. Example 1 showed absorption beginning at a wavelength of about 500 nm which became quite pronounced at about 450 nm, resulting in about a 15% loss of blue from the spectrum and thereby leading to the yellow coloration perceived by the eye. In contrast, the spectra exhibited by Examples 2 and 3 evidenced essentially no absorption across the visible portion of the radiation spectrum. As can be observed from Table I, Example 1 contained ZnO and TiO₂; Example 2 contained ZnO, but was essentially free from TiO₂; and Example 3 was free from both ZnO and TiO₂. The above spectra measurements clearly illustrate that the removal of TiO₂ from the glass composition eliminated the absorption of transmission in the blue end of the visible spectrum. Visible transmittance spectra were measured spectrophotometrically on samples of Examples 2 and 3 which had been cut from the faceplate of a television projection tube. The tubes had no screens in them, but were aluminized and exhausted normally. The tubes were aged in conventional commercial projection tube ageing racks for about 29.5 hours, resulting in an accumulated electron charge of 1.65 coulombs/cm². Example 2 exhibited a loss in transmission greater than 15% across the visible portion of the spectrum to a wavelength of approximately 500 nm with a somewhat further loss below 450 nm. A definite brownish cast in the sample was apparent to the eye. In contrast, Example 3 exhibited a loss in transmission less than 10% across the visible portion of the spectrum to a wavelength of approximately 450 nm with a slight further loss down to 400 nm. Essentially no brownish discoloration was discernible in the glass. The above spectra measurements clearly illustrate that the removal of ZnO from the glass composition is necessary to produce glasses demonstrating good resistance to electron browning.

Claims: Claims for the following Contracting States : DE, FR, GB, IT, NL A glass which is free from PbO and other readily reducible metal oxides, fluorine, ZnO, TiO₂, and MgO except minute amounts of impurities, which is free from a yellow color, and which exhibits a linear X-radiation absorption coefficient at a wavelength of 0.6Å of at least 35 cm⁻¹, essentially no browning discoloration upon being subjected to high velocity electrons, an electrical resistivity at 350°C of at least 10⁷ ohm-cm, a linear coefficient of thermal expansion (0°-300°C) not in excess of 102x10⁻⁷/°C, an internal liquidus below 900°C, a strain point not over 500°C, and a softening point no higher than 690°C, said glass consisting essentially, expressed in terms of weight percent on the oxide basis, of Li₂O 0.75-3 Li₂O+Na₂O+K₂O 11-16 Na₂O 5-7 CaO+SrO+BaO 21.5-26 K₂O 5-7 Al₂O₃ 1-2 SrO 7.5-10 ZrO₂ 2-7 BaO 14-16 CeO₂ 0.4-0.8 CaO 0-3 SiO₂ 55-60. A faceplate for a projection cathode ray tube consisting of a glass which is free from PbO and other readily reducible metal oxides, fluorine, ZnO, TiO₂, and MgO except minute amounts of impurities, which is free from a yellow color, and which exhibits a linear X-radiation absorption coefficient at a wavelength of 0.6Å of at least 35 cm⁻¹, essentially no browning discoloration upon being subjected to high velocity electrons, an electrical resistivity at 350°C of at least 10⁷ ohm-cm, a linear coefficient of thermal expansion (0°-300°C) not in excess of 102x10⁻⁷/°C, an internal liquidus below 900°C, a strain point not over 500°C, and a softening point no higher than 690°C, said glass consisting essentially, expressed in terms of weight percent on the oxide basis, of Li₂O 0.75-3 Li₂O+Na₂O+K₂O 11-16 Na₂O 5-7 CaO+SrO+BaO 21.5-26 K₂O 5-7 Al₂O₃ 1-2 SrO 7.5-10 ZrO₂ 2-7 BaO 14-16 CeO₂ 0.4-0.8 CaO 0-3 SiO₂ 55-60. Claims for the following Contracting State : ES A process for producing a glass, which is free from PbO and other readily reducible metal oxides, fluorine, ZnO, TiO₂, and MgO except minute amounts of impurities, which is free from a yellow color, and which exhibits a linear X-radiation absorption coefficient at a wavelength of 0.6Å of at least 35 cm⁻¹, essentially no browning discoloration upon being subjected to high velocity electrons, an electrical resistivity at 350°C of at least 10⁷ ohm-cm, a linear coefficient of thermal expansion (0°-300°C) not in excess of 102x10⁻⁷/°C, an internal liquidus below 900°C, a strain point not over 500°C, and a softening point no higher than 690°C, wherein the batch constituents are compounded and melt together to form said glass consisting essentially, expressed in terms of weight percent on the oxide basis, of Li₂O 0.75-3 Li₂O+Na₂O+K₂O 11-16 Na₂O 5-7 CaO+SrO+BaO 21.5-26 K₂O 5-7 Al₂O₃ 1-2 SrO 7.5-10 ZrO₂ 2-7 BaO 14-16 CeO₂ 0.4-0.8 CaO 0-3 SiO₂ 55-60 . A process for producing a faceplate for a projection cathode ray tube consisting of a glass which is free from PbO and other readily reducible metal oxides, fluorine, ZnO, TiO₂, and MgO except minute amounts of impurities, which is free from a yellow color, and which exhibits a linear X-radiation absorption coefficient at a wavelenght of 0.6Å of at least 35 cm⁻¹, essentially no browning discoloration upon being subjected to high velocity electrons, an electrical resistivity at 350°C of at least 10⁷ ohm-cm, a linear coefficient of thermal expansion (0°-300°C) not in excess of 102x10⁻⁷/°C, an internal liquidus below 900°C, a strain point not over 500°C, and a softening point no higher than 690°C, wherein the batch constituents are compounded and melt together to form said glass consisting essentially, expressed in terms of weight percent on the oxide basis of Li₂O 0.75-3 Li₂O+Na₂O+K₂O 11-16 Na₂O 5-7 CaO+SrO+BaO 21.5-26 K₂O 5-7 Al₂O₃ 1-2 SrO 7.5-10 ZrO₂ 2-7 BaO 14-16 CeO₂ 0.4-0.8 CaO 0-3 SiO₂ 55-60 and wherein said glass is formed into said faceplate.

Inventors: CONNELLY JOHN HUMPHREY, CONNELLY, JOHN HUMPHREY
Applicants: CORNING INC, CORNING INCORPORATED
Application year: 1989
Main classification: C03C3
IPC codes: C03C4, C03C3, H01J29