Nitrile emulsion polymers having improved adhesion properties

Abstract: Nitrile rubber emulsion latexes containing anionic emulsifying aids such as surfactants are treated with large amounts of cationic polymeric coagulants to form innocuous water insoluble residues. The polymeric coagulants chemically react with the anionic emulsifying aids by forming polymer adducts whereby the adducts are physically maintained in the nitrile rubber. The need for complete or thorough washing steps, which is gener­ ally tedious, expensive, and commercially impractical, is thus reduced or eliminated. Moreover, the dried latex particles have been found to have improved properties such as water resistance, adhesion, and the like.

Description: The present invention relates to nitrile rubber emulsion latex polymers and to a method of preparation thereof wherein various emulsifying aids such as anionic surfactants are chemically reacted with a cationic polymer to render the same innocuous as well as insoluble in water. Heretofore, surfactants, electrolytes, and other anionic emulsifying aids were necessarily utilized in the polymerization of nitrile rubber latex compositions. However, once the polymer was formed, washing or other removal steps were required to remove as much of the emulsifying aids as possible. Significant amounts remained, however, and could only be further reduced by tedious, expensive and complicated steps such as multiple washing, filtration, solvent extraction, and the like. From a commercial aspect, a nearly complete removal was impractical. Various cationic coagulant polymers such as condensation products of epichlorohydrin and an amine which is subsequently quaternized or various quaternary ammonium compounds are introduced into a nitrile rubber latex where the cationic polymer chemically reacts with the various anionic emulsifying aids such as surfactants and electrolytes. The various anionic emulsifying aids are conveniently tied up or neutralized and generally exist within the agglomerated latex polymer particles as opposed to on the surface thereof so that dried latex particles have improved properties such as improved adhesion, better electrical resistance, reduced fouling of molds during the manufacture of parts and non-interference with cure systems. The amount of the cationic polymeric coagulants is generally a stoichiometric weight equivalent to the total amount of the anionic components in the latex so as to generally form innocuous water insoluble residues. In detail the present invention relates to a dried nitrile rubber composition, comprising: a nitrile rubber composition and emulsifying aids characterized in that said nitrile rubber compositions containing a reacted anionic emulsifying aid dispersed therein, said anionic emulsifying aid having been reacted with a cationic polymeric coagulant, said cationic polymeric coagulant is a quaternized poly-(alkylene polyamine), a quaternized poly (hydroyalkylene polyamine), a quaternized poly(carbonylalkylene polyamine) or a quaternized polymer made from epichlorohydrin and a dialkylamine having from 1 to 5 carbon atoms, and wherein the amount of said cationic polymeric coagulant is from 0.75 weight equivalents to 1.5 weight equivalents for every weight equivalent of said anionic emulsifying aid. The nitrile rubber emulsion latex of the present invention generally contains conventional nitrile rubbers known to the art and to the literature, that is rubbers generally made from one or more monomers of acrylonitrile or an alkyl derivative thereof with one or more conjugated dienes and optionally one or more monomers of acrylic acid, or an ester thereof, or a dicarboxylic acid. Examples of acrylonitrile monomers or alkyl derivatives thereof include acrylonitrile and alkyl derivatives thereof having from 1 to 4 carbon atoms such as methacrylonitrile. The amount of the acrylonitrile or alkyl derivative monomers is from 0 or 1 percent to 50 percent by weight and preferably from 25 percent to 45 percent by weight based upon the total weight of the nitrile rubber forming monomers. That is, although an acrylonitrile or monomer or derivative thereof is generally utilized, it need not always be utilized as known to those skilled in the art. The conjugated diene monomers generally have from 4 to 10 carbon atoms with from 4 to 6 carbon atoms being preferred. Examples of specific conjugated diene monomers include butadiene, isoprene, hexadiene. The amount of such conjugated dienes is generally from 50 percent to 99 percent by weight and preferably from 55 percent to 75 percent by weight based upon the total weight of the nitrile rubber forming monomers. The nitrile rubbers of the present invention can also contain various optional comonomers as known to those skilled in the art as well as to the literature. Such optional comonomers generally include acrylic acid or various esters thereof, dicarboxylic acids, or combinations thereof. The acrylic acid or the esters thereof can generally be represented by the formula where R¹ is hydrogen or an alkyl having from 1 to 4 carbon atoms, and wherein R² is hydrogen, or (a) a nitrile containing ester wherein the ester portion contains a total of from 1 to 8 carbon atoms, (b) a hydroxyl containing ester wherein the ester portion contains a total of from 1 to 8 carbon atoms, (c) an unsaturated epoxy containing monomer which contains a total of from 3 to 12 carbon atoms, or (d) or combinations thereof. When R² is hydrogen, examples of suitable acids include acrylic acid and methacrylic acid. When R² is a nitrile containing ester, examples of suitable optional monomers include cyanoethyl acrylate, cyanoethyl methacrylate and cyanobutyl ether acrylates. Examples of suitable hydroxyl containing esters include hydroxy ethyl methacrylate, hydroxy propyl methacrylate and hydroxy ethyl acrylate. Examples of suitable epoxy containing monomers include glycidyl methacrylate, glycidyl acrylate and allyl glycidyl ether. The dicarboxylic acids generally contain from 3 to 10 carbon atoms and specific examples include maleic acid, fumaric acid and itaconic acid. When utilized, the amount of the above-noted optional monomers is generally from 0.1 to 25 percent by weight and preferably from 4 to 12 percent by weight based upon the total weight of the nitrile rubber forming monomers. As noted hereinabove, although generally utilized, an acrylonitrile monomer or an alkyl derivative thereof need not always be utilized in association with the conjugated diene monomers. In such an event, one or more of the above-noted optional monomers are utilized. The nitrile rubber latex is made in a conventional manner. That is, the above-noted monomers are added to suitable amounts of water in a polymerization vessel along with one or more conventional ingredients and polymerized. The amount of polymerized solids or particles is generally from 15 percent to 50 percent with from 25 to 35 percent by weight being desired. The temperature of polymerization is generally from 5°C to 80°C with from 30°C to 40°C being preferred. Typically in excess of 60 percent and usually from 70 percent to 95 percent conversion is obtained with from 80 percent to 85 percent conversion being preferred. The polymerization is generally initiated by free radical catalysts which are utilized in conventional amounts. Examples of such catalysts include organic peroxides and hydroperoxides such as benzoyl peroxide, dicumyl peroxide, cumene hydroperoxide and paramethane hydroperoxide, used alone or with redox systems; diazo compounds such as azobisisobutyronitrile; persulfate salts such as sodium, potassium, and ammonium persulfate, used alone or with redox systems; and the use of ultraviolet light with photo-sensitive agents such as benzophenone, triphenylphosphine and organic diazos. Inasmuch as the nitrile rubbers are prepared via an emulsion latex polymerization route, anionic emulsifying aids are utilized. Thus, various conventional anionic surfactants known to the art as well as to the literature are utilized. Generally, any suitable anionic surfactant can be utilized such as those set forth in McCutcheons, "Detergents and Emulsifiers," 1978, North American Edition, Published by McCutcheon's Division, MC Publishing Corp., Glen Rock, New Jersey, U.S.A., as well as the various subsequent editions thereof. Desirably, various conventional soaps or detergents are utilized such as a sodium alkyl sulfate, wherein the alkyl has from 8 to 22 carbon atoms such as sodium lauryl sulfate, sodium stearyl sulfate as well as various sodium alkyl benzene sulfonates, wherein the alkyl has from 8 to 22 carbon atoms such as sodium dodecyl benzene sulfonate. Other anionic surfactants include sulfosuccinates and disulfonated alkyl benzene derivatives having a total of from 8 to 22 carbon atoms. Various phenyl type phosphates can also be utilized. Yet other anionic surfactants include various fatty acid salts having from 12 to 22 carbon atoms as well as various rosin acid salts wherein the salt portion is generally lithium, sodium, potassium, ammonium and magnesium. The selection of the anionic surfactant generally depends on the pH of the polymerization action. Hence, fatty acid salts and rosin acid salts are not utilized at low pH values. The amount of the surfactant can vary depending upon the size of nitrile rubber particles desired, but typically is from 1 percent to 6 percent and desirably from 2 percent to 3 percent by weight for every 100 parts by weight of the nitrile rubber forming monomers. Other anionic emulsifying aids are various anionic electrolytes which control particle size by controlling the solubility of the soap. Examples of various conventional electrolytes generally include sodium, potassium, or ammonium naphthalene sulfonates. Other suitable electrolytes include sodium sulfate, sodium carbonate, sodium chloride and potassium carbonate. The amount of electrolyte is generally from 0.1 to 1.0 parts by weight with from 0.2 to 0.5 parts by weight for every 100 parts by weight of the nitrile rubber forming monomers. Molecular weight modifiers are also utilized to maintain the molecular weight within desirable limits as otherwise the viscosity of the polymer would be exceedingly high for subsequent handling and processing. Generally, known conventional molecular weight modifiers can be utilized such as various mercaptans which have from 8 to 22 carbon atoms, generally in the form of an alkyl group. Various sulfide compounds can also be utilized such as diisopropylxanthogendisulfide and di-sec-butylxanthogendisulfide. The amount of the molecular modifiers is generally an effective amount such that the Mooney viscosity, that is ML-4' @ 100°C is from 10 to 120 and desirably from 20 to 80. Yet another conventional emulsion latex additive is various short stop agents which are added generally to stop the polymerization and to tie up and react with residual catalysts. The amount of the short stop agents is from 0.05 to 1.0 parts by weight per 100 parts by weight of said nitrile rubber forming monomers. Examples of specific short stop agents include hydroxyl ammonium sulfate, hydroquinone and derivatives thereof, e.g., ditertiaryamylhydroquinone, various carbamate salts such as sodium diethyldithiocarbamate, various hydroxyl amine salts. Various antioxidants can be added and such are known to the art as well as to the literature including various phenolic type antioxidants such as ditertbutylparacresol, various diphenylamine antioxidants such as octylated diphenylamine, various phosphite antioxidants such as trisnonyl phenyl phosphite. Once the short stop has been added to the latex solution, excess monomer is stripped from the resultant latex, as for example by steam. According to the concepts of the present invention, a cationic coagulant polymer is utilized to coagulate the anionic emulsifying aids such as the various anionic surfactants and the various anionic electrolytes utilized. Polymeric cationic type coagulants are utilized according to the present invention inasmuch as they have a positive site which generally reacts with the negative or anionic site of the surfactant, electrolyte, etc., and thereby neutralize the same and render it innocuous. That is, according to the concepts of the present invention, the anionic emulsifying aids are not physically removed but rather are chemically reacted with a cationic polymeric coagulant to form an adduct which is generally dispersed throughout the nitrile particle. An important aspect of the present invention is that large stoichiometrically equivalent amounts of cationic polymeric coagulants are utilized. That is, large weight equivalents are required in order to yield a nitrile rubber having improved properties. Generally, from 0.75 to 1.5 weight equivalents, desirably from 0.85 to 1.25, and preferably from 0.95 to 1.05 weight equivalents of the cationic polymeric coagulant is utilized for every weight equivalent of said anionic emulsifying aids. Equivalent weight amounts less than those set forth herein do not result in effective neutralization, tying up, or negate the effect which the various anionic emulsifying aids have upon the properties of the dried nitrile rubber particles. The cationic polymeric coagulants utilized in the present invention generally contain a tetravalent nitrogen and are sometimes referred to as polyquats. Cationicity of the quaternary nitrogen is generally independent of pH, although other parts of the polymer molecule may exhibit sensitivity to pH such as hydrolysis of ester linkages. Typically, cationic polymers are prepared either by quaternization of poly(alkylene polyamines), poly(hydroxyalkylene polyamines), or poly(carbonylalkylene polyamine) with alkyl halides or sulfates, or by step-growth polymerization from dialkylamines, tetraalkyl amines, or derivatives thereof, with suitable bifunctional alkylating agents, and with or without small amounts of polyfunctional primary amines (such as ammonia, ethylene diamines, and others) for molecular weight enhancement. Polyamines produced from ammonia and ethylene dichloride, quaternized with methyl chloride, and polyquaternaries produced directly from dimethylamine and 1-chloro-2,3-epoxypropane are generally of commercial significance. Epichlorohydrin reacts with ammonia and primary, secondary, or polyfunctional amines to form polyamines or polyquats. The polyamines can be subsequently quaternized to yield a cationic polymeric coagulant of the present invention. As known to those skilled in the art and to the literature, literally hundreds of cationic polymeric coagulants exist and generally the same can be utilized in the present invention. Examples of specific polymeric cationic coagulants include poly(2-hydroxypropyl-1-N-methylammonium chloride), poly(2-hydroxypropyl-1,1-N-dimethylammonium chloride), poly(diallyldimethylammonium chloride), poly(N,N-dimethylaminoethyl methacrylate) quaternized, and a quaternized polymer of epichlorohydrin and a dialkylamine wherein the alkyl group has from 1 to 5 carbon atoms with methyl being preferred. The method of preparing cationic polymeric coagulants, general types of such compounds as well as specific individual compounds are set forth in the following documents: Encyclopedia of Polymer Science and Technology , John Wiley & Sons, New York, 1987, Volume 11, 2nd Edition, pages 489-503. Encyclopedia of Polymer Science and Technology , John Wiley & Sons, New York, 1987, Volume 7, 2nd Edition, pages 211-229. Kirk Othermer's Encyclopedia of Chemical Technology , 3rd Edition, Volume 10, John Wiley & Sons, New York, 1980, pages 489-523. Commercial Organic Flocculants , Josef Vostrcil and Frantisek Juracka, Noyes Data Corporation, Park Ridge, New Jersey, 1976. The cationic polymeric coagulants utilized in the present invention generally have a molecular weight of from 1,000 to 10,000,000. According to the present invention, the cationic polymeric coagulant treated nitrile rubber latex generally results in a slurry of rubber crumbs in a clear aqueous liquid. The crumbs contain the various anionic emulsifying aids physically incorporated therein. Such crumbs can be separated in any conventional manner as by filtering. Inasmuch as the anionic emulsifying aids have been rendered innocuous, multiple washing steps or other expensive, tedious process steps such as solvent extraction are not utilized. The nitrile rubbers of the present invention once dried as by conventional means, have improved properties such as good water resistance, good adhesion properties, non-interference with cure systems when cured, reduce fouling of molds during the manufacture of parts and improved electrical insulating properties. Such polymers can accordingly be utilized as adhesives, that is polymeric adhesives, binders, films, e.g., electrical insulating films, coatings such as for electrical circuit boards along with other conventional coating additives and fillers known to the art and to the literature. Suitable adhesive uses include metal-to-metal adhesion, metal-to-fabric adhesion and metal-to-plastic adhesion. The invention will be better understood by reference to the following examples. EXAMPLE 1 Various nitrile rubbers were prepared in a conventional or standard manner well known to the art and to the literature utilizing conventional or standard anionic emulsifying aids. The same nitrile rubber emulsion latex was coagulated with brine or calcium chloride and tested for the amount of remaining sodium, calcium, or potassium within the rubber particles. The results are set forth in Table I. As apparent from Table I, significant high amounts of sodium, calcium, and potassium remained within the rubber particles when conventional inorganic coagulants were utilized. Table II sets forth the use of various conventional coagulants (Examples F-H) and a cationic polymeric coagulant of the present invention, specifically, a quaternized polymer made from epichlorohydrin and dimethylamine, that is, ECH/DMA QUAT. As apparent from Table II, when calcium chloride or magnesium sulfate was utilized as an inorganic coagulant, significant high amounts of the various types of compounds indicated were obtained. In contrast thereto, when a cationic polymeric coagulant of the present invention was utilized, vast reductions in the amount of such compounds were obtained. Overall, the cationic polymeric coagulant of the present invention resulted in only 330 parts by weight of inorganic residues per million of nitrile rubber. In contrast, the prior art inorganic coagulants resulted in amounts well above 900 parts by weight of inorganic residues per million parts by weight of nitrile rubber. Hence, a reduction of at least 3 times and often in excess of 10 times in the amount of inorganic residues was obtained. All of the above examples were treated in the same manner including washing. When reduced amounts of cationic polymeric coagulants of the present invention was utilized, that is amounts generally below 0.75 weight equivalents for every weight equivalent of the total amount of said anionic emulsifying aids contained in the nitrile rubber emulsion latex was utilized, the latex could not be completely coagulated and product was thus lost. The water resistance of nitrile rubber as prepared according to the present invention utilizing canionic coagulants was compared with the same compound of nitrile rubber recovered in a conventional manner, that is dried and subject to multiple washings. The compounding recipes are as follows: As apparent from the above data, the nitrile rubbers prepared according to the present invention utilizing cationic polymers result in a much less water swell and increased electrical resistivity than did otherwise conventionally prepared nitrile rubbers. The cationic polymeric coagulants of the present invention resulted in nitrile-phenolic adhesives which had improved lap shear and peel strength as set forth in Table IV. As apparent from Table IV, the lap shear strength obtained utilizing the cationic polymeric coagulant of the present invention resulted in significant improvement as did the peel strength.

Claims: A dried nitrile rubber composition, comprising: a nitrile rubber composition and emulsifying aids characterized in that said nitrile rubber composition containing a reacted anionic emulsifying aid dispersed therein, said anionic emulsifying aid having been reacted with a cationic polymeric coagulant, said cationic polymeric coagulant is a quaternized poly(alkylene polyamine), a quaternized poly(hydroxyalkylene polyamine), a quaternized poly(carbonylalkylene polyamine) or a quaternized polymer made from epichlorohydrin and a dialkylamine having from 1 to 5 carbon atoms, and wherein the amount of said cationic polymeric coagulant is from 0.75 weight equivalents to 1.5 weight equivalents for every weight equivalent of said anionic emulsifying aid. A dried nitrile rubber emulsion latex composition according to Claim 1, wherein the amount of said cationic polymeric coagulant is from 0.85 weight equivalents to 1.25 weight equivalents for every weight equivalent of said anionic emulsifying aid. A dried nitrile rubber emulsion latex composition according to Claim 1, wherein the amount of said cationic polymeric coagulant is from 0.95 weight equivalents to 1.05 weight equivalents for every weight equivalent of said anionic emulsifying aid. A dried nitrile rubber emulsion latex composition according to Claim 1, wherein said cationic polymeric coagulant is a quaternized polymer made from epichlorohydrin and a dialkylamine having from 1 to 5 carbon atoms. A dried nitrile rubber emulsion latex composition according to Claim 1, wherein said cationic polymeric coagulant is a quaternized polymer made from epichlorohydrin and dimethylamine. An adhesive or a coating for an electrical circuit board including the composition of any of Claims 1 to 5.

Inventors: JORGENSEN AUGUST HENRY JR, JORGENSEN, AUGUST HENRY, JR.
Applicants: GOODRICH CO B F, THE B.F. GOODRICH COMPANY
Application year: 1989
Main classification: C08C1
IPC codes: C08C1, C09J121, H01B3, C08K9, C09J109, C09D109, C08L21, C08L9, C09D7