COATED GRANULAR FERTILIZER COMPOSITION AND ITS PRODUCTION

Abstract: A coated granular fertilizer composition compris­ ing fertilizer granules, wherein each particle is coated with a copolymer comprising units of vinyl chloride and units of ethylene in a weight ratio of about 50:50 to 90:10 with units of at least one functional monomer chosen from acrylamide, methacrylamide, N-methylolacrylamide, N-butoxymethylacrylamide, acrylic acid, glycidyl meth­ acrylate and hydroxyethyl acrylate in an amount of not more than about 10 % by weight based on the total amount of vinyl chloride units and ethylene units in an amount of about 5 to 40 % by weight based on the weight of the granule.

Description: The present invention relates to a coated granular fertilizer composition and its production. More particularly, it relates to a coated granular fertilizer composition with slow-release properties, thereby enabling the timely supply of nutrients to cultivated plants. Various attempts have been made to delay the immediate action of chemical fertilizers for high fertilizer efficiency. A typical example of such attempts is to coat a fertilizer composition in a granular state with a resinous material to exert slow release properties. For instance, a solution of a resinous material in an organic solvent is applied to fertilizer granules for coating. As the resinous material, polyolefin or ethylene/vinyl acetate copolymers (JP-B-44-28457, JP-B-54-3104, JP-B-60-21952 and JP-B-60-37074), a mixture of polyolefin, polyvinylidene chloride and ethylene/vinyl acetate copolymers with an inorganic carrier JP-B-60-3040), a styrenated alkyd resin or a phenol resin (GB-A-954,555), a styrene resin, a vinyl chloride resin or a vinylidene chloride resin (GB-A-815,829), etc. are usable. Further, a resin emulsion is applied to fertilizer granules for coating. As the resin emulsion, a polyethylene emulsion, a polyvinylidene chloride emulsion, anethylene/vinylidene chloride copolymer emulsion, anethylene-vinyl acetate copolymer emulsion, an acryl resin emulsion, etc. (JP-B-60-18640) may be used. However, when a resinous material solution in an organic solvent is used, care must be taken regarding the toxicity and inflammability of the organic solvent. In addition, blocking tends to occur on the coating. The coating film of a resin emulsion is inferior to that from said resinous material solution in various physical properties such as strength and gas permeability. Further, production of the fertilizer granules having a coating film with sufficiently controlled release properties is difficult, because the fertilizer components are soluble in water and therefore in the resin emulsion. Furthermore, entire coating of the fertilizer granules is prevented by blocking due to the stringiness of the resin emulsion. To overcome said drawbacks of conventional techniques, an extensive study has been made. It has been found that coating of fertilizer granules with a certain specific copolymer comprising units of vinyl chloride and units of ethylene with units of at least one functional monomer chosen from acrylamide, methacrylamide, N-methylolacrylamide, N-butoxymethylacrylamide, acrylic acid, glycidyl methacrylate and hydroxyethyl acrylate can afford coated fertilizer granules having slow-release properties so that the fertilizer components are properly released in water as the plants under cultivation grow. Advantageously, no blocking occurs during the coating process. The coated granular fertilizer composition of the invention comprises fertilizer granules, wherein each granule is coated with a copolymer comprising units of vinyl chloride and units of ethylene in a weight ratio of about 50:50 to 90:10 with units of at least one functional monomer chosen from acrylamide, methacrylamide, N-methylolacrylamide, N-butoxymethylacrylamide, acrylic acid, glycidyl methacrylate and hydroxyethyl acrylate in an amount of not more than about 10 % by weight based on the total amount of vinyl chloride units and ethylene units (hereinafter referred to as "a vinyl chloride/ethylene copolymer") in an amount of about 5 to 40 % by weight based on the weight of the granule. For the preparation of the coated granular fertilizer composition, an emulsion comprising the vinyl chloride/ethylene copolymer is applied onto fertilizer granules by spraying at a temperature of about 40 to 50°C for coating, followed by drying with hot air. When desired, an antiblocking agent may be applied by spraying onto the thus coated fertilizer granules in an amount of about 0.05 to 2 % by weight based on the weight of the vinyl chloride/ethylene copolymer. The resulting granules are then heated at a temperature of about 80 to 130°C for aging. There is no particular limitation on the fertilizer granules to be coated according to the invention. Such fertilizer granules may be, for instance, made of chemical fertilizers (e.g. urea, ammonium sulfate, ammonium chloride, ammonium nitrate, potassium chloride, potassium sulfate, potassium nitrate, sodium nitrate, ammonium phosphate, potassium phosphate, calcium phosphate) and shaped in spheres or the like having a particle size of about 2 to 10 mm. The emulsion usable for coating is normally an oil-in-water type emulsion and may be one obtained by emulsion polymerization of a mixture of monomer components, one obtained by dissolving a polymeric resin in a solvent (e.g. benzene, toluene, xylene, heptane, octane, ethylcyclohexane, trichloroethylene, tetrachloroethylene, methylchloroform, carbon tetrachloride, tetrachloroethane, tetrahydrofuran) and admixing the same with water in the presence of a surfactant (e.g. sodium salts of dialkylsulfosuccinic esters, sodium salts of higher alcohol sulfuric esters, sodium dodecylbenzenesulfonate, alkylpicolinium chloride, ammonium salts of polyoxyethylene alkyl phenyl ether sulfates) or the like. The solid content of such an emulsion is usually about 10 to 60 % by weight. The polymer component in the emulsion is the vinyl chloride/ethylene copolymer as defined above. When the ethylene unit content in the copolymer is more than about 50% by weight, blocking tends to occur among the fertilizer granules upon coating and production of the coated granular fertilizer composition is thus difficult. When the vinyl chloride unit content is more than 90 % by weight, the shrinking property of the coating film is increased so that perfect coating is unlikely and the control of the release properties becomes difficult. The functional monomer is used to provide the vinyl chloride/ethylene copolymer with hydrophilic properties, and therefore the permeability of the resulting coating film to water or an aqueous solution of the fertilizer is better than that of the coating film resulting from a vinyl chloride/ethylene copolymer not comprising units of the functional monomer. The content of the functional monomer units in the vinyl chloride/ethylene copolymer is not more than about 10 % by weight, preferably from about 1 to 10 % by weight. When the content is more than about 10 % by weight, the water resistance of the coating film is deteriorated so that the fertilizer is released too quickly. If necessary, two or more different kinds of the vinyl chloride/ethylene copolymer may be used in combination in the composition to assure better film-forming and anti-blocking properties. The amount of the vinyl chloride/ethylene copolymer to be applied as the coating material onto the granules may be from about 5 to 40 % by weight based on the weight of the granules. When the amount is less than about 5 % by weight, sufficient coating can not be achieved, and the coating film may have pinholes. As a result, the release rate is not well controlled. When it is more than 40 % by weight, the release rate is not delayed much and it is disadvantageous from the economical viewpoint. For the preparation of the coated granular fertilizer composition of the invention, the coating may be carried out by the use of a conventional coating apparatus such as a coating material spray apparatus (e.g. rotary coating pan, fluidized bed granulator), a granular fertilizer fluidizing apparatus equipped with a hot wind supplier as shown in Fig. 1 of the accompanying drawing or the like. Spraying and drying should be carried out at a temperature of about 40 to 50°C. When the temperature is lower than about 40°C, a long time is needed for drying so that the fertilizer components are dissolved in the emulsion, such that the coating film formed cannot have the desired release properties. When the temperature is higher than about 50°C, blocking may undesirably occur. After drying, an anti-blocking agent is optionally sprayed onto the coated fertilizer granules to prevent blocking, which may otherwise occur upon the subsequent heating for aging. Examples of anti-blocking agents are agalmatolite, talc, calcium carbonate, silica, etc.. It may be used in a small amount such as about 0.05 to 2 % by weight of the amount of the vinyl chloride/ethylene copolymer. Heating for aging should be effected at a temperature of about 80 to 130°C. A temperature lower than about 80°C can not sufficiently accomplish aging, while a temperature higher than about 130°C does not produce any increase in the aging effect and may unfavorably approach the melting point of the fertilizer component (e.g. urea). The coating operation as explained above may be repeated (e.g. several times) when desired, particularly when a large amount of the vinyl chloride/ethylene copolymer is to be coated. When desired, the fertilizer granules may be incorporated or admixed with any other optional component such as a fungicide, a herbicide, an insecticide, a coloring agent, a surfactant for release control or a water-insoluble inorganic material insofar the object of the invention can be maintained. The coated granular fertilizer composition of the invention can release the fertilizer component over a long period of time depending upon the need of the plants such as rice plants under cultivation so that better crop yields can be obtained in comparison with conventional fertilizer granules under appropriate weather conditions. Practical and presently preferred embodiments of the invention are illustratively shown in the following examples wherein % is by weight unless otherwise indicated. Examples 1 to 3 and Comparative Example 1 Using a coating device as shown in Fig. 1 of the accompanying drawing wherein (1) is a spray air conduit, (2) is a hot air conduit, (3) is a spray nozzle, (4) is fertilizer granules comprising urea and (5) is a fertilizer supporting metal net, fertilizer granules were coated under the following condition: Fertilizer granules: urea (2 to 4 mm⊘) Amount of fertilizer granules: 1000 g Temperature at spraying and drying: 43-45°C Temperature for aging: 82°C (Example 1) 100°C (Example 2) 130°C (Example 3) 75°C (Comparative Example 1) Amount of air blown: 130 m²/hr Air pressure in nozzle: 1.8 kg/cm² Amount of coating material: 17 % of the fertilizer granules Anti-blocking agent: (talc) 0.2 % of the coating material The fertilizer granules (4) were charged into the coating device on the metal net (5) and fluidized by blowing hot air therein through the hot air conduit (2) at a pre-determined rate. An emulsion comprising the vinyl chloride/ethylene copolymer (a copolymer consisting of ethylene units (21.1 %), vinyl chloride units (75.0 %), acrylamide units (1.9 %) and N-methylolacrylamide units (1.9 %)) was sent through the spray air conduit 1 and sprayed from the spray nozzle (3) onto the fertilizer granules at a temperature of 43 to 45°C for 60 minutes with immediate drying. Talc (0.2 %) was sprayed through the hot air conduit (2) thereto, and the temperature was raised to 82°C (Example 1), 100°C (Example 2), 130°C (Example 3) and 75°C (Comparative Example 1) for 45 minutes for aging. The thus coated fertilizer granules were subjected to measurement of their release rate into water at 30°C . The results are shown in Table 1. In case of Example 1, the change of the release rate into water at 30°C for 70 days is shown in Table 2. Release rate (%) After 1 day After 7 days Example 1 0.6 2.8 Example 2 0.3 0.9 Example 3 0.3 0.9 Comparative Example 1 44.7 67.1 Days elapsed Release rate (%) 1 0.6 7 2.8 10 9.8 20 20.2 30 36.8 50 68.7 70 77.5 Example 4 In the same manner as in Example 1, a chemical fertilizer comprising N (10 %), P₂O₅ (14 %) and K (13 %) in a granular state by ("EBISU"® manufactured by Sumitomo Chemical Co., Ltd.) was coated to give coated fertilizer granules having a release rate into water at 30°C of 1.7 % after one day and of 3.4 % after one week. Comparative Example 2 Using the same coating device as shown in Fig. 1, an emulsion comprising an ethylene/vinyl acetate copolymer consisting of ethylene units (5 %), vinyl acetate units (42 %) and vinyl chloride units (53 %) ("SUMIKAFLEX 830″® manufactured by Sumitomo Chemical Co., Ltd.), an emulsion comprising an ethylene/vinyl acetate copolymer consisting of ethylene units (3 %), vinyl acetate units (36 %) and vinyl chloride units (61 %) ("SUMIKAFLEX 850"® manufactured by Sumitomo Chemical Co., Ltd.), an emulsion comprising a vinylidene chloride polymer emulsion ("L-502" manufactured by Asahi Chemical Industries, Ltd.) or an emulsion comprising a vinylidene chloride polymer emulsion ("L-511" manufactured by Asahi Chemical Industries, Ltd.) was sprayed onto granules of urea having a particle size of 2 to 4 mm under the same condition as in Example 1 for coating. However, complete coating could not be achieved in any case because the occurrence of blocking during the operation. Example 5 In the same manner as in Example 1, an emulsion comprising a vinyl chloride/ethylene copolymer (consisting of ethylene units (21.2 %), vinyl chloride units (75.0 %), acrylamide units (1.9 %) and N-methylolacrylamide units (1.9 %)) and a vinyl chloride/ethylene copolymer (consisting of ethylene units (18.3 %), vinyl chloride (77.9 %), acrylamide (1.9 %) and N-methylolacrylamide (1.9 %)) in a weight proportion of 3 : 2 was sprayed onto granules of urea for coating to give coated granules having a release rate into water at 30°C of 1.3 % after one day and of 7.9 % after one week. Example 6 In the same manner as in Example 1, the same emulsion as in Example 5 but divided into half was sprayed onto granules of urea for coating, and the coating operation was repeated twice. The obtained coated granules had a release rate into water at 30°C of 0.8 % after one day and of 2.7 % after one week. As is evident from the above, this invention can accomplish the coating of fertilizer granules without the occurrence of blocking during the coating operation and can afford coated fertilizer granules with suitable release properties into water for supplying nourishment to cultivated plants depending on their growth.

Claims: A coated granular fertilizer composition comprising fertilizer granules, wherein each particle is coated with a copolymer comprising units of vinyl chloride and units of ethylene in a weight ratio of about 50:50 to 90:10 with units of at least one functional monomer chosen from acrylamide, methacrylamide, N-methylolacrylamide, N-butoxymethylacrylamide, acrylic acid, glycidyl methacrylate and hydroxyethyl acrylate in an amount of not more than about 10 % by weight based on the total amount of vinyl chloride units and ethylene units in an amount of about 5 to 40 % by weight based on the weight of the granules. The composition according to claim 1, wherein the granules have a particle size of 2 to 10 mm before coating. The composition according to claim 1, wherein the granules comprise at least one chemical fertilizer chosen from urea, ammonium sulfate, ammonium chloride, ammonium nitrate, potassium chloride, potassium sulfate, potassium nitrate, sodium nitrate, ammonium phosphate, potassium phosphate and calcium phosphate. The composition according to claim 1, wherein the granules comprise an anti-blocking agent in an amount of about 0.05 to 2 % by weight based on the copolymer as the coating material. A process for preparing the composition according to claim 1, which comprises applying an emulsion comprising a copolymer comprising units of vinyl chloride and units of ethylene in a weight ratio of about 50:50 to 90:10 with units of at least one functional monomer chosen from acrylamide, methacrylamide, N-methylolacrylamide, N-butoxymethylacrylamide, acrylic acid, glycidyl methacrylate and hydroxyethyl acrylate in an amount of not more than about 10 % by weight based on the total amount of vinyl chloride units and ethylene units, onto fertilizer granules in an amount of about 5 to 40 % by weight of the copolymer based on the weight of the fertilizer granules by spraying at a temperature of 40 to 50°C, applying hot air of the same temperature as above to the coated granules for drying, and heating the resultant coated granules for aging. The process according to claim 5, wherein an anti-blocking agent is applied to the coated granules by spraying after drying and before aging in an amount of 0.05 to 2 % by weight of the vinyl chloride/ethylene copolymer. The process according to claim 6, wherein the anti-blocking agent is chosen from agalmatolite, talc, calcium carbonate and silica. The process according to claim 5 wherein the heating for aging is carried out at a temperature of about 80 to 130°C.

Inventors: KODAMA, KIHACHIRO, MAHARA, AKIRA, SHIMOOKA, TADAMI
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1989
Main classification: C05G3
IPC codes: C05G3