CONCRETE COMPOSITION CONTAINING A SUPERFLUIDIFYING ADDITIVE

Abstract: A concrete composition contains hydraulic cement, inerts, water and a superfluidifying additive obtained by salifying, in the form of an alkaline metal, alkaline earth metal or ammonium salt, the sulphonated and oxidised products resulting from the reaction between sulphur trioxide and fuel oil deriving from steam cracking. This concrete composition has improved workability characteristics and enables concretes to be obtained generally possessing greater strength and durability.

Description: This invention relates to a concrete composition containing a superfluidifying additive. It is known in the art to use additives which are added to the concrete before or during mixing. These include chemical additives, aerating agents and others. Their effects on the concrete are positive, including a smaller water requirement, improved workability, controlled setting and hardening and increased durability. In particular, superfluidifying agents are increasingly widely used, especially in the form of water-soluble salts of the products of condensation between formaldehyde and melamine sulphonate or naphthalene sulphonate. Said superfluidifying additives result in improved cement dispersion with the effect of making the mix more fluid. For equal water/cement ratios this improved workability can facilitate the laying of concrete castings and can also allow vibration to be limited or dispensed with. Alternatively, it becomes possible to increase the mechanical strength of the concrete by reducing its water/cement ratio while maintaining equal workability of the mix. USA patent 3,277,162 describes the ammonium, sodium, potassium and calcium salts of the products of condensation between formaldehyde and napthalenesulphonic acid, which can inter alia be used to reduce water losses from cement compositions injected into oil wells. However, the superfluidifying additives of the known art are costly and their preparation process is costly and difficult, with the result that there is the need for superfluidifying additives which are more economical and easier to prepare. There is also a felt need for superfluidifying additives able to further improve the characteristics of concrete compositions and of the concretes obtainable from said compositions. It has now been found that such requirements can be satisfied by the concrete compositions of the present invention, which contain hydraulic cement, inerts, water and a superfluidifying additive, said compositions being characterised in that said superfluidifying additive is the salification product, in the form of an alkaline metal, alkaline earth metal or ammonium salt, of the sulphonated and oxidised products resulting from the reaction between sulphur trioxide and fuel oil deriving from steam cracking. Fuel oil deriving from steam cracking is the residual hydrocarbon fraction in the production of ethylene and other lower hydrocarbons by pyrolysis of naphthas and gas oils. This hydrocarbon fraction has a high aromatic compounds content, at least 50 wt% of these being bicyclic or polycyclic condensed ring aromatic compounds in accordance with ASTM D-3239-81. The superfluidifying additive used in the concrete composition of the present invention is obtained by reacting liquid or gaseous sulphur trioxide with the hydrocarbon fraction operating with a weight ratio of between 0.5/1 and 2.0/1, and preferably of the order of 0.8/1-1.2/1. This fraction is preferably conducted by: dissolving the hydrocarbon fraction in a non-sulphonatable organic solvent; bringing the solution thus obtained into contact with liquid or gaseous sulphur trioxide, respecting the aforesaid ratios between the two reactants; reacting them together at a temperature of between 90 and 120°C for a time of between 0.5 and 3 hours, removing the sulphur dioxide as it forms during the reaction; after cooling, neutralizing the reaction products with an alkaline metal base, alkaline earth metal base or ammonia; recovering the additive from the neutralization products by eliminating the organic solvent and at least part of the water. For further details of the sulphonation procedure reference should be made to British Patent N. 2 159 536. In treating the steam-cracked fuel oil with sulphur trioxide not only is there a sulphonation reaction but also an oxidation reaction as demonstrated by the evolvement of sulphur dioxide during the course of the reaction. The additive obtained on treating the reaction products with an alkaline metal base, alkaline earth metal base or ammonia is in all cases a solid containing a preponderant quantity (60-80% by weight) of organic sulphonate and lesser quantities of (10-30% by weight) of alkaline, alkaline earth or ammonium sulphate, together with possible residual moisture. The organic sulphonate can be separated from the reaction mixture, but it is preferable to use the crude reaction product directly. Generally the compositions of the present invention have a water/cement ratio of between 0.4/1 and 0.6/1 by weight and a cement/inerts ratio of between 1/3 and 1/6 by weight, the superfluidifying additive being present in a weight concentration of between 0.3 and 3% of the cement, said percentage relating to the content of organic sulphonate in the additive. In the preferred embodiment the water/cement ratio varies from 0.42/1 to 0.47/1, the cement/inerts weight ratio varies from 1/4.5 to 1/5.5 and the superfluidifying additive concentration varies from 0.5 to 2.0% by weight of the cement, again referred to the organic sulphonate. In preparing the compositions of the present invention the normal hydraulic cements such as Portland cement can be used, as can the normal inerts such as sand, gravel, crushed stone and the like. The compositions of the present invention can also contain an antifoaming agent to reduce concrete porosity. For this purpose the normal silicone, alcohol or fatty acid derivative antifoaming agents can be used in a quantity of up to 10% by weight of the superfluidifying additive. The superfluidifying additive of the present invention is economical because of the raw materials used, and is obtained by a simple and convenient process. When used in modest concentrations, such an additive gives the concrete compositions improved workability with self-compacting and self-levelling characteristics. The concretes obtained from said compositions have high strength and durability. In the experimental examples given hereinafter the following superfluidifying additives are used.: Additive A: obtained by sulphonating fuel oil from steam cracking with sulphur trioxide using a weight ratio of sulphur trioxide to fuel oil of 0.66/1 and neutralizing the obtained sulphonation product with sodium hydroxide. Such an additive has the following composition: organic sulphonate 79.7% by weight sodium sulphate 12.7% by weight water 7.6% by weight Additive B: obtained as indicated above but using a weight ratio of sulphur trioxide to fuel oil of 0.89/1. Such an additive has the following composition: organic sulphonate 76.6% by weight sodium sulphate 15.1% by weight water 8.3% by weight Additive C: obtained as indicated above but using a weight ratio of sulphur trioxide to fuel oil of 1.45/1. Such an additive has the following composition: organic sulphonate 71.8% by weight sodium sulphate 19.4% by weight water 8.8% by weight. The steam cracking fuel oil used for preparing the fluidifying additives A, B and C has the following characteristics: The workability characteristics of the concrete mixes are determined in Example 1 via the characteristics of the corresponding cement pastes. This if for simplicity reasons, as the data obtained are transferable to the concrete mixes. EXAMPLE 1 200 g of Portland cement 325, water and superfluidifying additive are fed into a bladed mixer in the weight ratio of 100:25:0.5. The latter value relates to the organic sulphonate content of the additives A, B and C. This feed is stirred in the bladed mixer for 120 seconds at a rotational speed of 60 r.p.m. and a temperature of 20°C. The resultant mixture is used to prepare cylinders of 60 mm height and 35 mm diameter, the area of the resultant spread then being measured. The test is repeated 5 times for each sample. For comparison purposes the test is repeated using an equal quantity of a commercial fluidifying additive (additive D) formed by salifying into sodium salt form the products of the reaction between formaldehyde and naphthalene sulphonate. The results relative to workability are given in Table 1, in which the workability of the composition containing the comparison additive (D) is given the value of 100 in conventional manner. Composition Relative workability Additive (A) 100 Additive (B) 135 Additive (C) 117 Additive (D) 100 EXAMPLE 2 The following are fed into a mixer: 10 kg of Portland cement 325 30 kg of dry gravel 20 kg of sand 4.17 kg of water 0.405 kg of an aqueous solution containing 17% of additive (B) evaluated with reference to the organic sulphonate contained in the additive. In this composition the water/cement weight ratio is equal to 0.45/1 and the additive quantity is 0.69 wt% of the cement. The feed is mixed for 3 minutes and a cone is then prepared for a slump test operating in accordance with the UNI 7163 standard. A 21 cm slump is obtained. For comparison purposes the aforesaid composition is prepared without the fluidifying additive, a 1 cm slump then being obtained. EXAMPLE 3 The following concrete compositions are prepared operating as in Example 2. Test 1 10 kg of Portland cement 325; 30 kg of dry gravel; 20 kg of sand; 5 kg of water. Test 2 10 kg of Portland cement 325; 30 kg of dry gravel; 20 kg of sand; 4.5 kg of water; 0.70% of the cement weight as superfluidifying additive (B) (evaluated as organic sulphonate); 0.06% of the cement weight as alcoholic foaming agent. Test 3 10 kg of Portland cement 325; 30 kg of dry gravel; 20 kg of sand; 4.3 kg of water; 1.40% of the cement weight as superfluidifying additive (B) (evaluated as organic sulphonate); 0.12% of the cement weight as alcoholic foaming agent. The slump test is carried out on these compositions, the result being expressed in cm and evaluated in accordance with UNI 7163. The following values are obtained: test 1 = 6 cm; test 2 = 5 cm; test 3 = 6 cm. The compositions are used to form concrete cubes of size 16 x 16 x 16 cm operating in accordance with UNI 6132. These cubes are cured in water at 20°C for 28 days after which their compressive strength is determined. The results of the three tests repeated three times each are as follows: Test 1 = 320, 324 and 318 kg/cm²; Test 2 = 404, 392 and 405 kg/cm²; Test 3 = 488, 480 and 463 kg/cm².

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, GR, LI, LU, NL, SE A concrete mixture consisting of a hydraulic cement, fine aggregates, coarse aggregates, water and a superfluidizer, characterized in that the superfluidizer is selected from the alkali metal-, alkaline earth metal- and ammonium salts of the sulphonated and oxidized products prepared by reacting, with sulphur trioxide, the fuel oil deriving from steam cracking, which is the residual hydrocarbon fraction in the production of ethylene and other lower hydrocarbons by pyrolysis of naphthas and gas oils. Concrete mixture according to Claim 1, wherein the sulphonation and oxidation reaction is carried out at a weight ratio of sulphur trioxide to said fuel oil of from 0,5 to 2:0:1. Concrete mixture according to Claim 2, wherein the weight ratio of sulphur trioxide to said fuel oil is of from 0,8:1 to 1,2:1. Concrete mixture according to Claim 1, wherein the superfluidizer consists of a predominant fraction of organic sulphonates, an alkali metal-, alkaline earth metal- or ammonium sulphate and water. Concrete mixture according to Claim 4, wherein the superfluidizer contains, on a weight basis: from 79,7% to 71,8% of organic sulphates; from 12,7% to 19,4% of sodium sulphate, and from 7,6% to 8,8% of water. Concrete mixture according to Claim 1, wherein: the water-to-cement weight ratio is from 0,4:1 to 0,6:1; the cement-to-aggregates weight ratio is from 1:3 to 1:6, the weight percentage proportion of the organic sulphonates contained in the superfuidizer relative to the cement being from 0,3% to 3%. Concrete mixture according to Claim 6, wherein: the water-to cement weight ratio is from 0,42:1 to 0,47:1; the cement-to-aggregates weight ratio is from 1:4,5 to 1:5,5, the weight percentage proportion of the organic sulphonates contained in the superfuidizer relative to the cement being from 0,5% to 2%. Concrete mixture according to Claim 1, further containing an antifoaming agent selected from the derivatives of silicone, alcohols and fatty acids. Concrete mixture according to Claim 1, wherein the hydraulic cement is Portland cement. Claims for the following Contracting State : ES Process for preparing a concrete mixture by combining together a hydraulic cement, fine aggregates, coarse aggregates, water and a superfluidizer, characterized in that the superfluidizer is selected from the alkali metal-, alkaline earth metal- and ammonium salts of the sulphonated and oxidized products prepared by reacting, with sulphur trioxide, the fuel oil deriving from steam cracking, which is the residual hydrocarbon fraction in the production of ethylene and other lower hydrocarbons by pyrolysis of naphthas and gas oils. Process according to Claim 1, wherein the sulphonation and oxidation reaction is carried out at a weight ratio of sulphur trioxide to said fuel oil of from 0,5 to 2:0:1. Process according to Claim 2, wherein the weight ratio of sulphur trioxide to said fuel oil is of from 0,8:1 to 1,2:1. Process according to Claim 1, wherein the superfluidizer consists of a predominant fraction of organic sulphonates, an alkali metal-, alkaline earth metal- or ammonium sulphate and water. Process according to Claim 4, wherein the superfluidizer contains, on a weight basis: from 79,7% to 71,8% of organic sulphates; from 12,7% to 19,4% of sodium sulphate, and from 7,6% to 8,8% of water. Process according to Claim 1, wherein: the water-to-cement weight ratio is from 0,4:1 to 0,6:1; the cement-to-aggregates weight ratio is from 1:3 to 1:6, the weight percentage proportion of the organic sulphonates contained in the superfuidizer relative to the cement being from 0,3% to 3%. Process according to Claim 6, wherein: the water-to cement weight ratio is from 0,42:1 to 0,47:1; the cement-to-aggregates weight ratio is from 1:4,5 to 1:5,5, the weight percentage proportion of the organic sulphonates contained in the superfuidizer relative to the cement being from 0,5% to 2%. Process according to Claim 1, further containing an antifoaming agent selected from the derivatives of silicone, alcohols and fatty acids. Process according to Claim 1, wherein the hydraulic cement is Portland cement.

Inventors: DONATI, ELIO, ERCOLANI, DARIO, PLATONE, EDOARDO, PREVEDELLO ALDO
Applicants: ENIRICERCHE S.P.A., SNAMPROGETTI S.P.A.
Application year: 1989
Main classification: C04B24
IPC codes: C04B24, C04B28, C07G99