HEATING ELEMENT AND METHOD FOR MAKING SUCH A HEATING ELEMENT

Abstract: This invention relates to a self limiting electrical heating element comprising resistance components having a positive temperature coefficient (PTC) and a zero temperature coefficient (ZTC), and consisting of a layered structure with two electrodes (4, 5; 14, 15) placed diagonally within or in contact with two ZTC layers (1, 2; 11, 12) which are separated by a PTC layer (3; 13). The components of the layered structure is such that at room temperature, the resistance in the PTC layer between the ZTC layers is very much less than the resistance in the combined ZTC layers, which in turn is very much less than the resistance in the PTC layer between the electrodes. At control temperature the resistance in the PTC layer between the parallel ZTC layers is equal to the resistance in the parallel ZTC layers. The geometry is such that at the control temperature where the resistances of the two components are equal, the watt densities are also essentially equal.

Description: Heating element and method for* making such a heating element My invention relates to a self limiting electrical heating element as defined in the preamble of the main claim, i .e. a heating element comprising resistance components having a positive temperature coefficient (PTC) and a zero temperature coefficient (ZTC), and consisting of a layered structure with two electrodes placed diagonally within or in contact with two ZTC layers which a re separated by a PTC layer. There are known several types of self limiting electrical heating elements having geometrical configurations similar to those preferred in my invention. Such heating elements are known from e.g. DE 2 543 314 and the corresponding US Patent Nos. 4 177 376, 4 330 703, 4 543 474 and 4 654 511. The heating elements described relate in particular to heat recoverable articles. These articles are mostly used for sealing purposes such as covers for electrical components and cable joints. The heat recoverable article is arranged to be placed around the component or joint to be sealed, whereupon the article is connected to a power supply. The compositions and combinations of layers constituting the article are chosen such that the article is heated to a defined temperature at which the article shrinks and seals the electrical components or cable joint. Similar heating elements are also described in US Patent No. 4 017 715 and EP 0 237 228. One of the objects of my invention is to provide a self regulating heating device, a property of which is its relative i nsensi t i ty to large variations in voltage at or near the thermal control temperature. The invention will be desc ibed primarily in terms of composite devices wherein one component exhibits a positive temperature coefficient of resistance (PTC) and the other component exhibits essentially zero coefficient of resistance (ZTC) behaviour. A .problem inherent in prior art devices depending solely on the. variation of resistivity with temperature, has been that certain performance character stics of the device were not always obtainable. For example, it is most desirable to maintain a given power output within a narrow control temperature range, and this temperature range does not always coincide with the anomaly temperature where most polymers exhibit their Ts (switching temperature) and which is closely associated with the melting point in the case of crystalline polymers . A feature of my invention is therefore to establish the control temperature of the device further removed from its crystalline melting point, since experience has shown that the closer a PTC component operates to its melting point, the less stable it is. These features are obtained in accordance with my invention by making the components of the layered structure such that at room temperature, the resistance in the PTC layer between the ZTC layers is very much less than the resistance in the combined ZTC layers, which in turn is very much less than the resistance in the PTC layer between the electrodes, and where at control temperature the resistance in the PTC layer between the parallel ZTC layers is equal to the resistance n the parallel ZTC layers, the geometry being such that at the control temperature where the resistances of the two components are equal, the watt densities are also essentially equal. Due to these relationships in my invention the PTC layer at room temperature acts as a short circuit between the parallel ZTC layers. But because of geometry the resistance between electrodes in the PTC layer is very high when voltage is at first applied and the ZTC layers alone develop heat. However as the temperature rises the resistivity in the PTC layer increases until the resistance between the ZTC layers is equal to that of the combined ZTC layers. Slightly above this temperature the two ZTC layers act as electrodes and heat is generated uniformally throughout the system, and any further rise in temperature anywhere in the area of the ZTC layers effectively reduces or shuts off the current. In this way the PTC component acts almost only as a control, and the ZTC components perform as the active heating elements. Under controlling conditions, because the ZTC layers act as electrodes, heat is generated over the entire area,- even outside the current carrying electrodes. Because the initial current is independent of the resistance in the PTC control layer, variations of as much as 2 to 5 times the room temperature original PTC resistance play almost no role. Therefore the initial power output is unchanged in spite of a considerable degree of instability in the PTC layer. Furthermore the cut-off, or control temperature is only slightly effected by large variations in voltage. Since the heating function is carried out mainly by the ZTC layers these elements have almost no inrush. Because the ZTC layers are the main source of heat, and the PTC layer acts as the control in a current direction normal to the ZTC layers, the characteristic 'hot line 1 effect of a pure PTC element is completely eliminated and the element generates even heat over the entire area, and the temperature is regulated almost regardless of heat loss variations. Because the PTC component is equal in area to the parallel ZTC components the maximum watt density in the PTC occurs when the resistances are equal, and at any higher temperature the density decreases rapidly. In this way the PTC component is never highly stressed which is conducive to a long and stable l fe. The critical and unique requirement of my invention is the limit placed on watt density at the control temperature. In the prior art patents much is said about the resistance and the resistivity of the two active components, but nowhere is watt density at control temperature mentioned. That this was not recognized as a factor can be shown from the examples of the mentioned patents. These clearly illustrate that the only concern was to control the effective Ts of the elements and that no consideration was given (in fact no recognition of the problem) to the critical effect of relative watt densities. Furthermore, the test method described in the prior art patents cannot be used to evaluate all the examples shown, because it would give false indication of the performance to be expected under selfheating heating conditions. In the test method described, the heating element was energized with a small power input, for measuring the variation in resistance of the whole element, but the temperature was controlled by an outside source which therefore was not sensitive to heat generated separately in the two components. This was important because in many cases the area of the two components differed. Therefore in a selfheating mode, such an element with a relatively small PTC component, but having the same resistance as the ZTC component at the control temperature would experience overheating in the PTC layer and this could easily result in failure. The whole intent of the heating elements described in US 4 017 715 is to provide a means for exceeding (if only temporary) the melting point of the PTC layer. On the other hand the construction of the elements described in some of the other prior art patents place no limits on the temperature experienced by the PTC layer due to watt density or voltage gradient effects. Much has been written about the so-called 'hot-line' effect, where, due to the positive coefficient of resistance of a PTC element, the tendency is for heat to be unevenly generated along a line midway between the two electrodes. This is especially the case where higher watt densities are experienced, or especially where there is insufficient heat loss so that a portion of the PTC film overheats. Another result of the hot line effect is that the voltage gradient in the area of the hot line becomes very great, and failure may actually occur first because of a dielectric breakdown effect. At any rate, to promote stability, the voltage gradient at control temperature, when the resistances are equal, must also be equal and this is the result of equal geometry as well as 100% electrical and thermal contact. The PTC portion of a series PTC-ZTC element cannot shut off the power of the whole element until its resistance equals and then exceeds the resistance of the ZTC portion at that temperature. The temperature that each component of the element attains is a function of the power density inherent in its individual operation, and if the power density in the PTC component is very high when shut down occurs, its local temperature can be very high. Polymeric PTC materials are notably unstable close to or above the melting point of the plastic, which in turn is associated with the Ts temperature. Therefore, it is a critical factor in my invention to make series PTC-ZTC elements where the PTC component performs its limiting effect at temperatures well below the melting point of the plastic, or somewhat below its Ts temperature. To accomplish this it is therefore essential that the heat generation or the watt density of the PTC component must not exceed the watt density of the ZTC component at the control temperature. If we use the same terminology as in the mentioned prior art patents, then the PTC component of type 3 or 4 would be preferred over the sharp cut offs depicted for types 1 and 2. With such a PTC component, and assuming the cut off of the series element to occur when R(PTC) = R(ZTC), then the cut off temperature may be regulated over a wide range, and well below the melting point of the plastic or its type 1 Ts. In fact, making use of non-crystalline polymers with sufficient coefficient of expansion, but with no real melting point, would be more desirable. Because of the inherent instability of the PTC compositions and especially near the melting point (e.g Ts) of crystalline polymers it is therefore important to develop limiting temperatures well below the melting point of the polymer in PTC component, or to make use of a suitable non crystalline polymer. This is in contrast to the configurations developed by prior workers in the field where cut off is desired as close as possible to the Ts of the matrix polymer. It is the relationship between the watt densities at the cut off temperature, e.g. where resistances of the two components are equal , that constitute a major achievement of my invention. For example, the same principle holds for a series construction between parallel facing electrodes. Here, again, the PTC control layer is protected from excess voltage gradients, and watt densities by the coextensive layers of the ZTC or NTC material . Above mentioned and other features and objects of my invention will clearly appear from the following detailed description of embodiments of the invention taken in conjunction with the drawings, where Figure 1 shows a layered PTC-ZTC structure, Figure 2 is a res stance-temperature curve, Figure 3 shows an embodiment of a heating element, and figure 4 illustrates the performance of the element according to my invention as compared to elements made according to the prior art technique. In Figure 1 is schematically illustrated a structure having two ZTC layers 1 and 2 with a PTC layer 3 in between. The layers are in full contact with each other. Electrodes 4 and 5 are diagonally arranged in the ZTC layers, within the layers as shown or in contact with the layers as an alternative. 2R(ZTC) is the resistance in each of the ZTC layers so that the resistance of both layers in parallel is R(ZTC). The resistance across the PTC layer is R(PTC1) and the resistance along the PTC layer between the electrodes is R(PTC2). In Figure 2 is illustrated a curve showing the relation¬ ship between the PTC resistance (PTC1) and the ZTC resistance as a function of temperature. At room temperature the resistance across the PTC in the electrode area must be very small compared to the resistance in the ZTC layers. Its function is to couple the parallel ZTC layers. At the same time the resistance in the PTC layer between the electrodes (PTC2), because of the ratio of thickness to width, must be substantially greater than the resistance in the ZTC layers, so that heat is generated almost only in the ZTC layers. At control temperature the resistivity in the PTC layer has risen so that its resistance between the ZTC layers equals the resistance in the ZTC layers themselves. Once the heating element has reached the control temperature the wattage output remains virtually unaffected despite substantial increases in voltage. Another way of expressing the relationsh ps between the resistances, and in more detail , is as follows: The relationship between R(PTC1) and R(PTC2) is inherently taken care of by the geometry involving the ratio between the thickness of the PTC layer and the distance between the electrodes. The main requirement is that the resistances and thus power development at the control temperature are equal . Again, because of the 100% contact area of the PTC and ZTC components the watt density requirements are fulfilled. The reason for the requirement that at control temperature the resistances in the PTC and ZTC components are equal, is that below this temperature, essentially all power is developed in the ZTC layers. When the resistance in the PTC layer exceeds the resistance in the ZTC layer, and because of the nature of the PTC resistance temperature curve, the heat will be generated predominantly in the PTC layer, but this also means that the resistance of the whole composite rapidly increases. In other words, at temperatures below the control temperature the characteristics, power output, stability etc are only a function of the ZTC component and the PTC provides only the l miting control. To calculate the relative values of resistance and resistivity in a given heating element we can then go through the following procedure. In essence this is the same as that outlined above. The effects of geometry on effective resistance in the PTC layer is as follows: The resistance through the PTC layer is greatly dependant on the direction of current flow. For example, the resistance through the thickness of the PTC layer is very small compared to the resistance from electrode to electrode through the width of the layer. And furthermore the resistance across the PTC layer n the limited area of the electrodes must also be small compared to the resistance in the parallel ZTC layer. Since R(PTC2) = ohmcm • d/(t-l ) and R(PTC1) = ohmcm • t/(d-l ) then R(PTC1) = R(PTC2) • t2/d 2 Depending on the ratio of distance between the electrodes (d) and the thickness of the PTC layer (t), the resistance in the vertical direction will at all times be t^/d*? times that in the horizontal direction. Since at room temperature the ZTC resistance must be very much less than the R(PTC2) and very much greater than the R(PTC1), this sets limits on these resistance values in relation to the geometry of the device. But to be fully effective, at room temperature, the resistance through the PTC layer only in the area of the electrodes must also be so small compared to the ZTC resistance, that it acts as a coupling short circuit between the two ZTC layers, and then the watt density developed in this area is no greater than the watt density developed in the combined ZTC layers. Under these conditions the current w ll flow essentially straight across the PTC layer at each electrode, and then through the ZTC layers to the opposing electrodes. Now, as the temperature rises and the sensitivity in the PTC layer increases, more and more of the PTC layer conducts current between the ZTC layers until a temperature is reached where the resistance offered by the PTC layer equals the resistance of the ZTC layers. Under these conditions equal heat is developed in both components. If the temperature rises still further, the PTC component in the series starts to limit the current passing through it and hence through the whole device. At this control temperature the current is flowing in effect half through the PTC and half through the ZTC and if the temperature increases further, due to for example an increased voltage, the resistivity in the PTC component continues to rise while the current flows more and more vertically through the PTC and less and less horizontally through the ZTC. This then surprisingly causes a compensating reduction in element resistance, which has the effect of maintaining a controlled wattage output over the whole control temperature range. The relationship between the geometry of my heating elements and the PTC and ZTC compositions used to make the elements will clearly appear from the following examples, with reference to Figure 3 where two ZTC layers 11 and 12 are separated by a PTC layer 13. Electrodes 14 and 15 are connected diagonally to the ZTC layers. The PTC layer has a thickness t, a length 1 and a distance d between the electrodes 14,15 which is equal to the length 1, when the heater element is formed as a square. In the squarely formed elements tested, the size of the elements varied from d = 1.6 cm to d = 45 cm. The thickness of the PTC layer varied from 0.05 to 0.10 cm, and the thickness of the combined ZTC layers from 0.0032 to 0.10 cm. It is a requirement of my invention that at cut-off or control temperature: R(PTC-between layers) = R(ZTC-paral 1 el layers) Therefore, in an electrical square, - since R = ohmcm • (distance between electrodes/area of electrodes), then R(ZTC-paral lei layers) = ohmcm(ZTC) * d/(t(ZTC)-d) = ohmcm(ZTC) l/t(ZTC) and R(PTC-between layers) = oh cm(PTC) t(PTC)/d-d so that the ohmcm ratio ohmcm(PTC)/ohmcm(ZTC) = d 2 /(t(ZTC) t(PTO) where t(ZTC) = the combined thickness of the two ZTC layers, and t(PTC) = the thickness of the PTC layer. When the thickness of the PTC layer is 0.025 cm and the thickness of the combined ZTC layers are 0.0032 cm (using glass scrim impregnated layers), the ohmcm ratio values for my heaters are as follows, - at control temperature (CT) and at room temperature (RT): d CT RT 1.6 32,000 3,200 4.5 250,000 25,000 45 2.5-10 7 2.5-10 6 The corresponding ratios for heaters made with extruded ZTC layers of 0.025 cm thickness were: d CT RT 1.6 2,048 204 4.5 16,200 1,620 45 1.6-10 6 1.6-10 5 A comparison with a prior art heating element (Beispiel 5,' DE 25 43 314) shows an ohmcm ratio of 20/7 = 2.85 at room temperature with a 2.54 times 2.54 size heating element, whereas one of my heating elements of the same size have an ohmcm ratio of 516 at room temperature and 5.161 at cut-off temperature. These ratios show the main difference between the prior art concepts and my concept. An example of a heating device made in accordance with my invention and compared with a heating device made in accor¬ dance with the prior art patents are as follows: The PTC layer consisted of 45 parts of Elftex (TM) carbon in 100 parts of PE or EVA resin. The compound was made into a 0.1 cm thick film at a resistivity of 4*10^ ohmcm at room temperature. The ZTC layers consisted of a glass scrim impregnated with an aqueous dispersion of etchen Black (TM). The Ketchen Black was run through a fluid energy machine along with 20% by weight of 40% colloidal silica (DuPont Ludox HS- 40 (TM)). This material was dispersed in water along with 5 % Polyethylene Imine to effectively wet the carbon black and control the charge on the carbon particles. The coating is modified with a binder consisting of an acrylic latex, clay and Ludox and also PEI, the binder being in a proportion to produce the desired resistance level on the coated scrim. Thus with the PTC layer at a resistivity of 4-10 * ^ ohmcm and an ohm/square resistance of 400,000 combined with two ZTC layers of 30,000 ohm/square each (together in parallel 1,500 ohm/square) this device had at room temperature a resistance of 1,520 ohm where the area between the electrodes was 6.3-6.3 cm. For comparison a sample was made according to the principles outlined in the prior art patents, the ohm/square resistance in the PTC layer was 1,600 and the ohm/square resistance in the combined ZTC layers was 15,000 ohms. As will be seen from the above, the resistances of the components of the prior art device at room temperature, have the following characteristics: R(PTC-between layers) << R(PTC-between electrodes) << R(ZTC- parallel layers), which is quite different from the resistance relationships of the components according to my invention. The room temperature resistance of the two samples, before connecting them to a power supply, was comparable, but the performance, when connected to a power supply, was very different as can be seen from the curves illustrated in Figure 4, especially with respect to the increasing voltage in the control temperature region. The above detailed description of embodiments of this invention must be taken as examples only and should not be considered as limitations on the scope of protection.

Claims: Claims 1. Self limiting electric heating element including resis¬ tance elements with positive temperature coefficient (PTC) and zero temperature coefficient (ZTC), comprising a layered structure with two diagonally arranged electrodes (4,5;14,15) within or in contact with two ZTC layers (1,2;11,12)) which are separated by a PTC layer (3 ; 13 ) c h a r a c t e r i z e d i n t h i s t h a t a the resistances of the components have the following characteristics: at room temperature: R(PTC-between layers) << R(ZTC-paral 1 el layers) <<R (PTC- between electrodes), and at control temperature: R(PTC-between layers) = R(ZTC-paral 1 el layers), the geometry of the element being such that at the control temperature where the resistances in the two components are equal, the watt densities are also essentially equal. 2. Heating element according to claim 1, c h a r a c t e r z e d i n t h i s t h a t at control temperature in an element having sides d-d, a thickness t(PTC) of the PTC layer and a combined thickness t(ZTC) of the two ZTC layers, the ratio of resistivity of the PTC layer to that of the ZTC layers are: d 2 /(t(PTC) • t(ZTC). 3. Method for making a heating element according to claim 1 or 2, c h a r a c t e r ! ' z e d i n t h i s t h a t the PTC layer (3;13) is made from 20 to 50 parts of a large particle carbon black such as Elftex (TM) carbon in 100 parts of a thermoplastic resin such as PE or EVA and that the compound is made into a 0.025 to 0.20 cm thick film at a required resistivity 4. Method for making a heating element according to claim 1,2 or 3, c h a r a c t e r ! ' z e d i n t h s t h a t the ZTC layers (1,2;11,12) are made from a glass scrim impregnated with an aqueous dispersion of highly conductive carbon black, e.g. Ketchen Black (TM). 5. Method according to claim 4, c h a r a c t e r i z e d i n h i s t h a t the ZTC carbon black is run through a fluid energy machine along with 5 to 30% by weight of some 40% aqueous colloidal silica (DuPont Ludox HS-40 (TM)) and that this material is dispersed in water along with Polye¬ thylene Imine. 6. Method according to claims 4 or 5, c h a r a c t e r i z e d i n t h i s t h a t the ZTC carbon black mixture is modified with a binder consisting of an acrylic latex, clay and Ludox and also PEI, the binder being in a proportion to produce the desired resistance level on the coated scrim.

Inventors: SMITH-JOHANNSEN ROBERT, SMITH-JOHANNSEN, ROBERT
Applicants: RAMU INT, RAMU INTERNATIONAL
Application year: 1989
Main classification: H05B3
IPC codes: H05B3