IMPROVED STARCH BASED CORRUGATING ADHESIVES

Abstract: This invention presents starch-based alkaline corrugating adhesives having improved green bond strength due to the use of undried starch as the raw starch component in the adhesive. Such adhesives can be used in corrugation processes at much higher corrugator running speeds than the conventionally employed adhesives.

Description: The procedures employed in the production of corrugated paperboard generally involve a continuous process wherein one strip of paperboard is fluted by means of heated, fluted rollers. The protruding tips on one side of this fluted paperboard strip are then coated with an adhesive, and a flat sheet of paperboard, commonly referred to in the trade as a facing, is brought into contact with these adhesive-coated tips. By applying heat and pressure, an adhesive bond is formed there between. This process produces what is known as single-faced board, named for the fact that the facing is applied to only one surface. If a double-faced paperboard (in which an inner fluted layer is sandwiched between two facings) is needed, a subsequent operation is performed wherein the adhesive is applied to the exposed tips of the single-faced board and the adhesive-coated tips are then joined with a second facing under pressure and heat. Thus, both single and double-faced board can be produced in a continuous process. The typical use of these types of adhesives in a corrugating process and the use and operation of corrugators in general are described in US-A-2,102,937 and US-A-2,051,025. FR-A-2184 455 discloses a method for the continuous production of starch-based glue for use in the manufacture of corrugated cardboard and in the paper industry. A major concern in such processes is the selection of the appropriate adhesive, as its properties will affect not only the strength and stability of the final corrugated product, but also the parameters (corrugator speed, etc.) within which the process can be operated. Thus, such adhesives are chosen in light of the specific requirements of the process and the properties desired in the ultimate corrugated paperboard. The adhesives most commonly used in corrugating are starch-based adhesives which are popular because of their desirable adhesive properties, low cost, and ease of preparation. The most common type of starch-based corrugating adhesives comprises the alkaline adhesives. Such adhesives are comprised of dried raw, ungelatinized starch suspended in an aqueous dispersion of gelatinized (cooked) starch termed the carrier. These adhesives are produced by gelatinizing starch in water with sodium hydroxide (caustic soda) to yield a gelatinized (or cooked) carrier which is then blended or mixed with the raw (ungelatinized) starch, borax and water to produce the adhesive. In the corrugating process, the adhesive is applied (usually at a temperature between 25° and 55°C.) directly to the tips of the fluted paper medium and the facing is brought into contact with the adhesive-coated surfaces; the subsequent application of heat causes the raw starch to gelatinize, resulting in an instantaneous increase in viscosity and tack, thereby forming of the adhesive bond between the fluted paper and the facing. For various applications, the adhesive composition can be varied to maximize one or more desirable properties such as extended pot life and viscosity stability, water resistance of the ultimate bond, etc. However, one property directly related to the utility of the formulation as a corrugating adhesive is its ability to rapidly form an initial bond (termed "tack" or "green bond strength"); this rate of tack development is directly related to the speed at which the corrugator can be run. There exists a need for corrugating adhesives possessing high green bond strengths and rapid development of tack. While there are different theories regarding the respective roles of the raw starch and the carrier in the development of adhesive properties, some research has centered on the view that the carrier contributes to the bond strength and setting speed of the adhesive; indeed, it has been suggested that good tack in the carrier leads to good tack (and therefore improved runnability) in the adhesive (see e.g., R. Williams, C. Leake and M. Silano, TAPPI, Vol. 60 , No. 4 April/1977 pp 86-89). Further it has been known for many years that a corrugating adhesive whose carrier portion is prepared from a high amylose starch exhibits superior tack to one prepared from pearl starch, which contains about 27% amylose, because the high amylose carrier will have improved rheological and film-forming properties, and increased moisture resistance. Thus, there are many different carriers available for use in starch based adhesives. To date, however, relatively little experimentation has been done with the raw (uncooked or ungelatinized) starch portion of the adhesive, other than varying the species of starch source utilized. Generally, the raw starch is supplied in dried powder form, and is used as such in the adhesive preparation. Thus, during commercial processing the starch is ordinarily dried in an elevated temperature dryer (generally at 200 - 250°F, 94 - 112°C) (to remove water to about 8-14% moisture content), after which it is packaged and stored until use. It is an object of this invention to present a starch-based alkaline adhesive for use in corrugation processes. It is further an object of this invention to present a starch-based alkaline corrugating adhesive which exhibits a high green strength such that it can be employed in high speed corrugating processes. This invention presents a series of starch-based alkaline corrugating adhesives which fulfill these objects. The basic components of these adhesives comprise an aqueous dispersion of a gelatinized (or cooked) starch and a preformed starch milk that has never been dried or that has not been dried at a temperature exceeding 26.7°C (80°F). (as used herein "undried" starch shall be inclusive of aqueous starch dispersions, such as undried starch milk, which have never been dried, and starches which have been dewatered and/or air-dried at ambient temperature, nominally 15.6-26.7°C (60-80°F)). The use of undried raw starch, it has been found, greatly increases the green bond strength and rate of tack development of the resultant adhesives as compared with the same adhesives prepared with standard (commercially dried) raw starch. Further, this increase is observed with high amylose carriers, other carriers such as corn starch, and blends of starch and synthetic polymers such as those disclosed in US-A-4,424,291, incorporated herein by reference. The adhesives also comprise the other standard components of starch-based corrugating adhesives, namely an alkali (such as sodium hydroxide) and borax. The undried raw starch, carrier, alkali, borax, and water are generally present in amounts of 15 to 35% (dry basis, db), 2 to 6% (db), 0.2 to 0.9% (db), 0.1 to 0.8 (db), and 60 to 80%, respectively by weight based on the total adhesive composition. Further, the adhesives can be used at a variety of starch solids contents, generally 20-40% on a "dry basis" (d.b.) of the total composition. This permits a wide degree of latitude in the potential applications in which the adhesives can be employed. While general experience has indicated that in industry, most corrugators are using corrugating adhesives containing from 18-26% (d.b.) by weight of total solids, there are certain applications in which higher % solids would be desirable. The adhesives of this invention, thus, permit employment in a wide array of applications. The raw starch component of the corrugating adhesives of this invention can be any starch suitable for use in corrugating adhesives. Preferred starches are corn, tapioca, wheat, potato, and mixtures thereof, with corn and tapioca starches being the most preferred. Mixtures of these starches and other starches are also useful, with the sole criterion for use being the requirement that the raw starches be undried. Typical forms of undried starches include starch milks (aqueous dispersions of raw starches) and starches air dried at ambient temperature [15.6-26.7°C (60-80°F)]; such starches also include dewatered starches, i.e., starches which are filtered from aqueous dispersion by gravity or vacuum filtration. In fact, it appears that the primary criterion for such "undried" starches is that they not be subjected to the elevated temperatures realized during commercial starch drying processes. While not wishing to be bound by theory, applicants postulate that high temperature drying of starches adversely affects the starch, rendering it less capable of developing tack rapidly. By eliminating such a drying step, the raw starch presumably remains in a much more reactive form, and the resultant adhesive has a much higher green bond strength and rate of tack development. While it is to be understood that the undried starches can be employed as the raw starch in any starch-based adhesive, and that use of such starches will greatly improve the green bond strength and rate of tack development in these adhesives, typically such adhesives will comprise a raw starch and a cooked starch carrier. While the use of a high amylose starch carrier is not essential for the purposes of this invention, use of such a carrier is preferred since it, too, will aid in increasing green bond strength. Thus, while the use of an undried raw starch component will increase the tack regardless of the carrier employed, the use of a high amylose carrier, generally 35-70% (by weight) amylose, will result in faster bond development. In circumstances where the use of a high amylose carrier may be undesirable or inconvenient, other carriers, such as ordinary corn starch, may be employed. The ratio of raw starch/carrier will vary as the molecular weight of the carrier varies, with lower amounts of high molecular weight carriers being required to achieve the same results. In general, however, the ratio ranges from 4/1 to 16/1, by weight, depending on the nature of the starch and the viscosity desired. The alkali (base) employed in the adhesive is preferably caustic soda, (sodium hydroxide); however, other bases may be employed in partial or full replacement of the sodium hydroxide as the particular application dictates. Such bases include, for example, alkali metal hydroxides such as potassium hydroxide, alkaline earth hydroxides such as calcium hydroxide, alkaline earth oxides such as barium oxide, alkali metal carbonates such as sodium carbonate, and alkali metal silicates such as sodium silicate. The alkali may be employed in aqueous or solid form. The alkali is generally present in a concentration of 0.2 to 0.9 (db) by weight, of the adhesive. The starch based alkaline corrugating adhesives also contain borax, in a concentration of 0.1 to 1% (by wt.) of the adhesive as the last essential component. In addition to the essential ingredients of the adhesive composition of this invention, any conventional non-chemically functional additives may be incorporated into the adhesive in minor amounts, if desired. Such additives include, for example, wetting agents, proteins, placticizers, solubilizing agents, rheology modifiers, water conditioners, penetration control agents, peptizers such as urea, gelatinization temperature modifiers, inert fillers such as clay and finely ground polymers, thickeners such as inorganic collodial clays, guar, hydroxyethyl cellulose, alginates, polyvinyl alcohol, polymers of ethylene oxide and the like, wet strength resins and emulsions such as polyvinyl acetate. The corrugating adhesives of this invention can be prepared by any standard method so long as elevated temperature drying of the raw starch is not required. In a preferred method, the carrier starch is first gelatinized (cooked) in a portion of the water with the alkali to provide the carrier component of the adhesive. The raw starch slurry is prepared by mixing the undried raw starch, borax and remaining water. The carrier and raw starch mixture are then combined to form the final adhesive. Optional ingredients, if desired, can be added at any convenient point during the preparation of either component but are usually added to the finished adhesive. The adhesive thus obtained can be used to bond single or double-faced boards using any equipment which is presently employed for the preparation of corrugated board. In general, the adhesive is maintained at a temperature preferably between 25° and 55°C. before its application to the protruding tips of the fluted paper strip. The actual application may be accomplished by the use of glue rolls which are ordinarily employed in most corrugating machines, or one may utilize other application methods which may be able to achieve a different distribution of adhesive. Following the application of the adhesive to the fluted paper strip, the latter is then brought into immediate contact with the facing board under the influence of heat and pressure, as is well known in the art. A double-faced board may be subsequently prepared by bringing a second facing in contact with the open fluted surface of the single-faced board by the usual procedures. Since the adhesives develop tack at an accelerated rate, the corrugator speed can be proportionally increased over the speeds used with conventional adhesives. This permits a more rapid and efficient production of the corrugated board. In addition, it is contemplated that the corrugating adhesives can be used in other applications, such as lamination and dual arch lamination, where bonding occurs in the presence of heat, and rapid green bond formation is desirable. The examples which follow illustrate specific embodiments of the invention. In the examples all parts and percentages are given by weight and all temperatures in degrees Fahrenheit or degrees Celsius as noted. PROCEDURE In each example, the sample adhesives were examined for tack development and (green bond strength) in the joining of a (28.124g 62 lb)/MSF wet strength) corrugating liner to a (14.974g 33 lb)/MSF wet strength) corrugating medium. The adhesive was applied to the corrugating liner using a [254 µm 10 mil] Bird applicator. Subsequently, a sheet of corrugating medium was placed on top of the adhesive and the system was placed atop a hot plate at 350°F (177°C) under a 5 g/cm² weight for 5 seconds. Immediately thereafter, one end of the liner was attached to a dial-typ spring scale. The medium was then manually separated from the liner in a continuous fashion and the force required to achieve such separation was periodically recorded; this force is a measure of the green bond strength and the rate of tack development with time, and is related to the speed at which a corrugator can be run (i.e. the higher the green bond strength and the faster tack is developed, the faster the corrugator can be run). Example 1 Preparation of Adhesive All samples of corrugating adhesives were prepared in essentially the same manner, differing only in the precise starches employed and the ratios of components. A representative preparation is presented below. A carrier component was prepared by cooking at 150°F (66°C) 26 g (d.b.) of a corn starch in 179 g of water. A total of 5.2 g of sodium hydroxide (dissolved in 15.7 g water) was then added and the system was agitated for 20 minutes. Then, 52 gm of water was added to cool the system and quench the reaction. In a separate vessel, 164 g (d.b.) of corn starch was added to 429. 3 g of water at 110°F (43°C) followed by the addition of 3.2 g of borax (pentahydrate) to provide the raw starch slurry. After 5 minutes of moderate agitation, the carrier starch was slowly added to the raw starch slurry and moderate agitation was continued resulting in an adhesive having a total solids content of 22.7% (starch solids 21.7%). Example 2 Comparison of Commercially Dried vs Air-dried Raw Starch Two adhesives, designated A and B, were prepared using the procedure of Example 1, differing only in that sample A contained a commercially dried corn starch, as the raw starch component, while sample B contained a undried raw corn starch which was prepared by filtering and air drying an undried starch slurry at ambient temperature. Both adhesives possessed gelatinization temperatures of 149°F (66°C) and the following Brookfield viscosities and Stein-Hall values at 100°F (38°C): Both samples were examined for tack development as described supra . In a series of four replicate trials, the following average results were obtained. It can be seen that, Adhesive B prepared from the air dried corn starch, develops tack at a more rapid rate than Adhesive A, prepared with commercially dried corn starch. Example 3 Effect of Increased Starch Content To assess the effects of increasing starch content on adhesive behavior, two samples designated C and D, were prepared nominally following the procedure in Example 1, but using the following formulation. Carrier Water 178.8g Corn starch (anhydrous) 26.1g Caustic 25% Sol'n 22.0g Raw Water 422.9g Cornstarch 202.8g Borax 3.5g The resultant adhesives had a solids content of 26.2% (25.2% starch solids). As in Example 2, the adhesives differed only in the raw starch employed, adhesive C contained standard (commercially) dried corn starch, D contained air-dried corn starch. The physical properties of each formulation are summarized below. The samples were assayed for tack development in four replicate trails. The average of these trials is presented below. As in Example 2, the adhesive employing the air dried raw starch (D) developed tack at a much more rapid rate than the adhesive employing its commercially dried counterpart (C). Example 4 Effect of Increased Starch Content To further assess the effect of increased starch content on adhesive behavior, two samples designated E and F were prepared following the procedure in Example 1, but using the following formulation. Carrier Water 157.7g Corn Starch (Anhydrous) 18.9g NaOH 1.5g dissolved in Water 10.5g Quench Water 52.5g Raw Water 346.9 Corn Starch 302.4 Borax 4.0 The resultant adhesive had a solids content of 36.5% (35.9% starch solids). As in Example 3, the adhesives differed only in the raw starch employed, Adhesive E contained commercially dried cornstarch, F contained air dried cornstarch. The samples were assayed for tack development in four replicate trials. The average of these trials is presented below. As in the previous examples the adhesive employing air dried raw starch (F) developed tack at a much more rapid rate that the adhesive employing its commercially dried counterpart (E). Example 5 Use of Slurried Starch Milk To assess the effects of the use of (undried) slurried starch milk in adhesives, samples G-K were prepared nominally following the procedure of Example 1 with the exception that the carrier was cooked at 110°F (43°C) (rather than 150°F) and using the following basic formulation: Carrier High Amylose Starch* 30.1g Water 160.1g Caustic 5.1g Raw Water 361.2g Starch 239.8g Borax 3.2g Total Solids 34.8% (Total Starch Solids 33.8%) * Contained approximately 70% (by wt. db) amylose, 30% (by wt. db) amylopectin Samples G and K employed undried slurried corn starch milk as the raw starch, sample H employed a standard (commercially) dried corn starch, and samples I and J employed air-dried starch which was subsequently dried in the laboratory at elevated temperatures (71-82°C and 160-177°C respetively) (160-180°F and 320-350°F respectively). The physical properties of each formulation and the results of the tack development tests are presented below: Again, the data demonstrate that the adhesives which employ the undried starch (G and K) develop tack much faster than the heat dried ones (H-J), including the air-dried samples which were subsequently heat dried (I,J). Example 6 Use of Tapioca Starch To assess the effects of using dried and undried tapioca starch in place of corn starch as the raw starch component of the adhesive, samples L-N were prepared following the procedure of Example 5, and the following basic formulation. Carrier High Amylose Starch (see Ex. 5) 30.1g Water 160.1g Caustic 5.1g Raw Water 361.2g Staren 239.8g Borax 3.2g Total Solids 34.8% (Total Starch Solids 33.8%) Sample L was prepared using heat (commercially) dried tapioca raw starch while M and N employed air-dried tapioca. The physical properties of the adhesives and the results of the tack development determinations are presented below.

Claims: 1. An improved starch-based alkaline corrugating adhesive comprising an aqueous dispersion of a gelatinized carrier starch and a raw starch wherein the improvement comprises employing a preformed starch milk that has never been dried or that has not been dried at a temperature exceeding 26.7°C (80°F) as the raw starch. 2. The adhesive of Claim 1, wherein the adhesive contains 0.2 to 0.9% (by wt. d.b.) of alkali and 0.1 to 0.8% (by wt., d.b.) of borax, wherein the percentages are based on the total weight of the adhesive. 3. The adhesive of Claim 2, wherein the water content from 60 to 80% (by wt.) based on the total weight of the mixture. 4. The adhesive of Claim 2, wherein the ratio of raw starch/carrier starch ranges from 4/1 to 16/1 by weight. 5. The adhesive of Claim 2 wherein the alkali is sodium hydroxide. 6. The adhesive of Claim 2, wherein the raw starch is selected from the group consisting of undried corn starch, undried wheat starch, undried potato starch, and mixtures thereof. 7. The adhesive of Claim 6, wherein the raw starch is an undried starch milk. 8. The adhesive of Claim 6, wherein the raw starch is air-dried at ambient temperature. 9. An improved process for making corrugated paperboard using a starch-based alkaline corrugating adhesive wherein the improvement comprises employing the starch-based corrugating adhesive of Claim 1. 10. The process of Claim 9, wherein the raw starch is air-dried at ambient temperature.

Inventors: ATKINSON, JEFFREY G., FORAN, MICHAEL, LEAKE, CRAIG
Applicants: NATIONAL STARCH AND CHEMICAL INVESTMENT HOLDING CORPORATION
Application year: 1989
Main classification: C09J103
IPC codes: C09J103