Use of melt-rheology modifiers in thermoplastic polymer compositions

Abstract: Acrylic polymers having a molecular weight of at leastabout 500,000, and preferably of about 1,500,000, are blended at levels of from 1 to 25% with thermoplastic resins to provide polymer blends having improved melt rheology, thereby to facilitate blow molding, thermoforming, extrusion and similar processes.

Description: This invention is concerned with melt-rheology modifiers for thermoplastic polymers, and more particularly to the use of high-molecular-weight acrylic polymers as melt-rheology modifiers, and to the thermoplastic polymers having modified melt-rheology properties. The compositions used in the present invention are particularly well suited to blow-molding processes, by which thin-walled articles such as bottles are formed from a partially shaped, usually hollow polymer article known as a parison. The parison is formed by well-known processes such as extrusion or injection molding; it is then typically placed in a final mold, expanded by gas pressure to conform to the shape of the final mold and cooled to fix its shape. Variations of this process are well known in the art, and it may be used with many thermoplastic polymers. Such polymers that have been used by others to form blow-molded articles include poly(vinyl chloride), or PVC, poly(ethylene terephthalate), or PET, and polypropylene. Desirably, such polymers balance melt-rheology properties such as flow and sag: the polymer must flow readily enough to be extruded, injection molded or otherwise formed into the parison; it must be sufficiently elastic and thermoplastic to fill the final mold readily under air pressure and heat, and without melt fracture or other surface distortion; yet it must be sufficiently resistant to flow or sag while cooling that the shape of the finished article is retained. Further, if the polymer may be crystallized, the various processing, blending, and forming operations to which it is subjected must not accelerate crystallization to the point that blow-molding properties are degraded. This combination of properties is difficult to find in unmodified polymers. Poly(vinyl chloride) may be easily modified with polymers that act as processing aids, to make a polymer that is tractable in blow-molding applications, but other polymers have been more difficult to modify satisfactorily. Condensation polymers such as polycarbonates and polyamides and polyethylene terephthalate of molecular weights in the range below about 20,000 have been difficult to modify for blow molding, and polycarbonate resins have proved especially difficult. One approach that has been used to improve the blow-molding properties of polycarbonate resins has been to introduce chain branching into the polycarbonate molecule, as taught in U.S.-A- 4,415,723. Another has been to copolymerize the polycarbonate with a polyester, as taught in EP-A- 155,989. Neither of these approaches has been entirely successful; particular properties are improved, but the balance of properties important to blow molding is not sufficiently improved. Branching or increasing the molecular weight of the polymer has been applied to other polymers used in blow molding. Branching is taught for poly(ethylene terephthalate) in U.S.-A- 4,161,579, but these approaches with polyesters either require careful control of melt reactivity or cause processing times to be extended. Polyamides having reactive amine end groups may be reacted with groups on an additive, to tie together the polyamide molecules and effectively raise the molecular weight, as is taught in relatively low-molecular weight polymers such as U.S.-A- 3,668,274 or U.S.-A- 4,145,466. This method requires careful control of stoichiometry, and may not be suited to less reactive polymers. The rheology of polycarbonates has been controlled by additives, such as the selectively hydrogenated block copolymers of vinyl monomers and olefins taught in GB-A- 2,004,284, triazines taught as softeners in US-A- 4,159,974, blends with styrene-maleic anhydride copolymers and styrene-acrylonitrile copolymers taught in U.S.-A- 4,218,544 and the like. Acrylic and methacrylic copolymers have been added to polycarbonate resins or polyester-polycarbonate blends as impact modifiers; these copolymers typically possess a core-shell (multi-stage) morphology, and they have relatively low molecular weights, generally below about 300,000. Such copolymers are taught in, for example, U.S.-A- 4,245,058, U.S.-A- 4,257,937, US-A-4,264,487 and Brinkmann, U.S.-A- 3,591,659. Such impact-modifying polymers preferably contain a core (first stage) of rubbery poly(alkyl acrylate) polymer or copolymer which is optionally crosslinked and/or graftlinked, and a thermoplastic hard shell (outer stage) preferably of poly(methyl methacrylate) polymer or copolymer, as taught in U.S.-A- 4,096,202. Other impact modifying polymers are methacrylate-butadiene-styrene resins, which are multi-stage polymers having a butadiene polymer or copolymer, optionally containing vinylaromatics, as for examples styrenics, (meth)acrylate esters, or (meth)acrylonitrile, at levels below 30% and optional crosslinking, as a first stage. One or more thermoplastic methyl methacrylate polymer stages containing styrene, lower alkyl (meth)acrylates and/or (meth)acrylonitrile and optionally other monovinyl, monovinylidene, polyvinyl and/or poly vinylidene components are polymerized onto the first stage. Such modifiers are useful for impact-property modification of polycarbonates and polyesters, and are taught in U.S.-A-3,864,428 and U.S.-A- 4,180,494. Such staged polymers are preferably made by emulsion polymerization and isolated by any of several techniques known to those skilled in the art, including coagulation, spray drying or other evaporative techniques such as extruder coagulation with dewatering and pelletization as taught in U.S.-A- 3,751,527. These impact-property-modifying polymers may be stabilized with additives during isolation and may be further treated, as by partial fusing or pelletization, for ease of handling or blending. Blends of poly(methyl methacrylate) and poly(ethylene terephthalate) are also taught for blow molding of bottles by JP-A-55-90921, 57-18221, and 57-6727; these teachings would not encourage one to depart from the relatively low molecular weights disclosed for the impact modifiers. High-molecular-weight polymers have been added to various polymers, as for instance the addition of high-molecular-weight styrene to thermoplastic polystyrene as a foaming-process aid (U.S.-A-3.903,023). U.S.-A- 4,622,363, discloses the use of high-molecular-weight copolymers of styrene with a minor amount of a nitrile or (meth)acrylic ester, in combination with low-molecular-weight copolymers of styrene with nitrile or (meth)acrylic ester and graft polymers of styrene-methyl methacrylate on a rubbery polymer, for the purpose of raising the heat distortion temperature of polycarbonate resins. There is no indication of the effect on melt-rheology properties such as flow and sag; the heat distortion temperature of resins is not related to such properties. As to the cited art, it should be understood that the characteristics of processing aids are quite distinct from those of melt rheology modifiers. US-A 4179479 teaches that the acrylic polymers, generally of lower molecular weight than those now specified in the present invention, allow for better component mixing, a more homogenous melt and promote better dispersion, surface gloss and processing and also reduce moulding pressures, cycle time and improve hot melt release and lubricity. None of these characteristics relates to low shear rheology and some, e.g. moulding pressure and cycle time, specifically relate to high shear performance. Thus, US-A 4179479 does not make available the use for increasing the extrusion sag time of thermoplastic engineering resins. Similarly, US-A- 4086296 relates to the use of core/shell polymers, with a high molecular weight acrylic shell as lubricating/processing aids. Again, the disclosure is to improvement of melt processing in general and of release from hot metal surfaces. These are distinct from the low shear melt viscosity effects involved in melt rheology modification and do not suggest an increase of the extrusion sag time. An object of the present invention is therefore to improve the extrusion sag time of certain thermoplastic polymer melts, and particularly the blow-molding properties of such melts. A further object is to provide the use of a polymeric additive which improves the melt rheological properties of thermoplastic engineering resin. We have discovered that a particularly advantageous balance of melt-rheology properties can be provided in the use of specific high-molecular-weight homopolymers or copolymers as defined hereinafter having weight-average molecular weights of at least 1,500,000. The invention is directed to the use of a polymer of units of one or more copolymerisable vinyl monomers, wherein at least 50% by weight of the units have the formula I: where R₁ is H or CH₃ and R₂is one of alkyl, substituted alkyl, cycloalkyl, aryl, aralkyl or alkaryl; said polymer having a weight average molecular weight of 1,500,000 to 10,000,000; for increasing the extrusion sag time of thermoplastic engineering resin in a process for blow moulding, thermoforming or extruding said engineering resin, in which process the said polymer is present in an amount of 1 to 25% by weight of the total weight of engineering resin plus said polymer. Preferably, R₂ is selected from the group consisting of methyl, ethyl and n-butyl and/or at least 70% by weight of the units of said polymer are units having the formula (I). Optionally a maximum of 5% of the units are units from a polyethylenically unsaturated monomer. More preferably, all of the units of the acrylic polymer are units having the formula (I) and/or the thermoplastic engineering resin comprises polycarbonate, polyester, poly(aromatic ketone), poly(phenylene ether), poly(phenylene sulfide), polysulfone, poly(ether-imide), polyacetal, polyimide, polyamide, poly(amide-imide), and/or copolymers and blends of any of the above, and/or copolymers of styrene and alkyl-substituted styrene with acrylonitrile and maleic anhydrides, and/or blends of such styrene copolymers with the above copolymers and blends. The invention is further directed to the use as set out above, wherein the said polymer is present at a level of from 1 to 10% by weight, preferably 5 to 10% by weight and/or wherein the moulded, thermoformed or extruded composition further contains impact modifier and/or filler. The improved properties are particularly advantageous for various uses, including blow molding of the polymer blends, making extruded articles and thermoformable sheet, and making thermoformed articles therefrom; preferred thermoplastic engineering resins for use in the investion are polycarbonate resins, polyester resins and blends of polycarbonate with polyester, and these are blended with the extrusion sag time improving polymers (RMR) mentioned above. As used herein the term "blend" is intended to mean a mixture obtained by any method which results in the mixture having physical properties suitable for the uses envisaged for the polymer blends of the present invetion. Such methods will be known to those skilled in the art, and some are exemplified hereinbelow. The extrusion sag time improving (MRM) polymers used in the present invention may be prepared by free-radical polymerization of copolymerizable vinyl monomers to molecular weights of at least 1,500,000. At least 50%, and more preferably at least 70%, by weight,and optionally 100% of the polymers comprises polymer units from an acrylic monomer having the formula (I) where R₁ is H or CH₃ and R₂ is selected from alkyl, substituted alkyl, cycloalkyl, aryl, aralkyl and alkaryl, and is preferably an alkyl group containing 1 to 8 carbons. Especially preferred for R₂ are methyl, ethyl and n-butyl: the most preferred MRM polymers are terpolymers of at least 70% by weight methyl methacrylate, 0-20% by weight ethyl or butyl acrylate and 0-30% by weight butyl methacrylate. As used herein the term acrylate refers to the formula (I) where R₁ is H, and methacrylate to the formula (I) where R₁ is CH₃. As a minor component of the MRM polymers, units from other copolymerizable vinyl monomers may be selected by those skilled in the art. Included among such copolymerizable vinyl monomers are those bearing functional groups, as for example the carboxylic acid groups found in (meth)acrylic acid. The MRM polymers used in the present invention may be prepared by any known polymerization techniques, including bulk, solution, emulsion or suspension polymerization. Preferred is conventional emulsion polymerization, using thermal, redox or other known initiation, batch feed or gradual feed, single or multiple staged polymerization, seeded polymerization, and similar variations of this technique which will be apparent to those skilled in the art. The emulsifier may be selected from among those known to be useful in polymerizations; preferred are those which do not degrade the color or stability of the polymer or of the resin to which it is added. Typical of emulsifiers for emulsion polymerization are alkali metal and ammonium salts of fatty carboxylic acids, such as sodium oleate or sodium stearate; salts of disproportionated resin acids; ethoxylated and/or propoxylated alkyl phenols, such as dodecyl phenol with 1-100 ethylene oxide units; salts of aliphatic or aromatic sulfates such as sodium lauryl sulfate; salts of aliphatic or aromatic sulfonates, such as sodium dodecylbenzene sulfonate; sodium or potassium or ammonium dialkylsulfosuccinates; disodium salts of mono- or dialkylated diphenylether disulfonates; C₁₂-C₁₈ alkylsulfonates, sulfates, sulfonates, phosphates, or phosphonates based on alkylene oxide adducts of alkylated phenols, such as sodium alkylphenol(ethylene oxide)₁₋₁₀₀ phosphate; and many others known to the art. Combinations of emulsifiers may be employed. Preferred are those with sufficient thermal stability that their residues in the isolated acrylic additive can be processed into the matrix resin without deleterious effects on color or stability; such emulsifiers include alkyl, aryl aralkyl, and alkaryl sulfonates, and alkyl, aryl aralkyl, and alkaryl phosphonates. Such an emulsion polymerization allows the preparation of polymer particles having small size, narrow size distribution and high molecular weight, quickly and at high conversions, with minimum residual monomers. One process by which polymers of the preferred molecular weights may be made is taught in U.S.-A- 4,201,848, and other processes are known to those skilled in the art. The polymer may be easily isolated from the reaction mixture using known techniques. The weight average molecular weight (M w ) of the MRM polymers, as measured by gel permeation chromatography (GPC) techniques, is at least 1,500,000, and still more preferably at least about 3,000,000 (3 x 10⁶). Below these values the contribution of the polymer to the blow-molding properties of the resin incorporating it is small, although benefits may be recognized from using lower-molecular-weight MRM polymers, as for example those with M w of about 400,000; however such molecular weights are outside the scope of the present invention. Difficulties with preparing extremely high-molecular-weight polymers create a practical upper limit of about ten million for the preferred polymer, although higher molecular weights are contemplated within the scope of the present invention. The preferred MRM polymers are linear or branched, but they are not crosslinked; that is, they are soluble in organic solvents such as tetrahydrofuran, toluene, ethylene, dichloride and the like. Within the broader aspect of the invention, however, use of crosslinked, and especially lightly crosslinked, polymers is also contemplated. Such crosslinking may be introduced by the incorporation of units from polyethylenically unsaturated monomers into the MRM polymer, preferably at levels up to about 5%, and more preferably from about 0.01 to about 0.5%, by weight based on the total MRM polymer weight, or it may be introduced by other techniques known to those skilled in the art, as for example thermal crosslinking or various post-cross-linking techniques. The MRM polymer used in the present invention may be isolated from the emulsion in which it is formed by any of several methods, including coagulation, evaporation, spray drying, or devolatilizing in an extruder followed by pelletization. Preferred are spray drying and coagulation. The MRM polymer used in the present invention is incorporated into a thermoplastic engineering resin selected from polycarbonates; polyesters including poly(alkylene terephthalates); blends or copolymers of polycarbonates and polyesters; poly(aromatic ketones) such as polyether ketone, polyether ether ketone, polyether ketone ketone, polyketone; poly(phenylene ethers); poly(phenylene sulfides); phenoxy resins; polysulfones such as poly(ether sulfone), poly(aryl sulfone), polysulfone; poly(ether imides); poly(ether imide esters); copoly(ether imide esters); poly(ester carbonates); polyarylates such as poly(bisphenol A isophthalate); polyimides such as poly(glutarimides); aromatic polyimides; polyacetals; poly(styrene) including crystal poly(styrene) and high impact poly(styrene); polymers of vinyl toluene or para-methyl styrene; copolymers or blends of styrene or alkyl substituted styrene with acrylonitrile or maleic anhydride; polyamides including crystalline and amorphous polyamides; acrylate-styrene-acrylonitrile resins; acrylonitrile-butadiene-styrene resins or blends thereof with polyamide or polycarbonate resins; poly(amide imides); nitrile resins; poly(methyl pentene); olefin modified styrene-acrylonitrile; styrene-butadiene resins; acrylonitrile-chlorinated polyethylene-styrene resins; thermoplastic elastomers such as poly(ether esters), poly(ether amides), poly(styrene butadiene styrenes) and poly(styrene ethylene-butylene styrenes); or copolymers and blends of the above. The "thermoplastic engineering resins", may alternatively be referred to in this specification as "matrix resins". Using methods known to those skilled in the art, the MRM polymer may be incorporated into the matrix resin at from about 1% to about 25% of the total weight of resin plus polymer. Higher levels outside the scope of the present invention may be used, but these may deleteriously affect the balance of other physical properties, such as the heat distortion temperature, of the resin in specific applications. A more preferred range is from about 1 to about 10%, and still more preferred is from about 5 to about 10% by weight. The MRM polymer may, for example, be incorporated into the resin by blending the MRM polymer, as a dry powder or pellets, with a dry powder or pellets of the matrix resin. Alternatively, if the matrix resin and the MRM polymer have been separately prepared as emulsions, the emulsions may be mixed and isolated as an intimate mixture by conventional methods such as coagulation or spray drying, or as yet another alternative, the emulsions may be isolated separately and sequentially in the same equipment, this process being termed "staged coagulation." As a less preferred method, the monomers used to prepare the MRM polymer may be polymerized in the presence of the matrix polymer, but the polymerization conditions must be carefully controlled, or the molecular weight of the resulting polymer will be too low to be fully effective. Other additives may be incorporated into the matrix resin prior or subsequent to incorporation of the polymer , or they may be incorporated simultaneously, as by coagulating or spray drying mixed emulsions of the MRM polymer and the additives and incorporating the resulting material into the matrix resin. Such procedures are conventional, and will be readily apparent to those skilled in the art. These additives may include other polymers useful as impact modifiers, lubricants, flame retardants, blowing agents, antioxidants, light stablilizers, heat stabilizers, and the like. The blends may also contain fillers such as calcium carbonate, reinforcing agents such as coupled mica, fibers such as glass fibers, and the like. Thus a typical polymer blend of the invention may comprise for example a polycarbonate resin, a poly (butylene terephthalate) resin, an MRM polymer, plus impact modifiers and/or fillers. A significant use of the resins which incorporate the MRM polymer is in the preparation of useful articles by extrusion blow molding, but the enhanced melt strength imparted by the MRM polymers will also be advantageous in preparing useful articles by processes such as injection blow molding, thermoforming and stamping processes on polymer sheet, rods, or tubes, and the like, performed upon resins containing the MRM polymers. The resins which incorporate the MRM polymer will also be advantageous in other applications where high melt strength is a desirable property. Other uses will be readily apparent to those skilled in the art. Useful articles which may be made from the resins which incorporate the MRM polymer include items for automotive use, such as bumpers, spoiler panels, dashboard panels, rear window panels, external air spoilers, seat backs, truck bed liners, wind deflectors, motorcycle fairings and skirtings and the like. Further uses may include toys, such as tricycles, surfboards, exercise equipment, television housings, other equipment housings, such as typewriter cases, and the like. Still further uses include containers such as bottles, tanks for organic or inorganic liquids, and the like. The formed materials may be useful in buildings, such as decorative or tough protective panels, thermoformed panels, seating construction, pipe, profiled shapes for window and door construction and the like. Many other uses for such tough, heat resistant, readily blow-molded, thermoformed or otherwise processed plastics having high melt strength will be readily apparent to those skilled in the art. All percentages and ratios given herein are by weight, unless otherwise stated, and all reagents are of good commercial quality unless otherwise stated. Physical-property tests performed on the matrix resins incorporating the MRM polymers include melt viscosity, melt creep rate, extrusion sag time, modulus and impact resistance. Melt viscosity was determined for the samples using a Rheometrics "Dynamic Spectrometer" in the parallel-plate mode. A sample with a radius of 12.5 mm and approximately 2 mm thick was placed between the plates, and dynamic torsional shear was applied to the sample at a rate of 100 radians/sec as the sample temperature was raised. The temperature at which the sample viscosity at that shear rate reached 20,000 poise was taken as the "process temperature". The sample was then held at the process temperature and the shear rate was reduced to 1 radian/second. The melt viscosity was measured at the lower shear rate, and the dynamic melt-strength parameter, R*, was determined by dividing the measured melt viscosity at the lower shear rate by the 20,000-poise value obtained at the higher shear rate. Melt creep rate (MCR) was measured using a Rheometrics "Stress Rheometer". A sample with a radius of 12.5 mm and a thickness of 1 mm was placed between the parallel plates of the instrument. A constant shear load of 3 x 10⁴ dynes/cm² applied to the sample at the process temperature determined above, and the angle, in radians, through which the loaded plate moved with respect to the fixed plate was measured. The strain was calculated by multiplying the angle by the radius of the sample disk and dividing the sample thickeners. The MCR was then determined by dividing the strain by the time over which the strain was measured. MCR units are sec⁻¹. Extrusion sag time was determined by horizontally extruding a strand of polymer from a Killion 25-mm extruder operating at a rate of 60 rpm, through the specified die at the specified temperature. The time for the strand to sag to a point 100 meter below the die was recorded in seconds. Tensile modulus was measured according to ASTM Standard Method D-638. Impact resistance was measured using a notched Izod impact sample according to ASTM Standard Method No. D-256. Both number-average and weight-average molecular weights (M n and M w ) were determined by gel-permeation chromatography, using a poly(methyl methacrylate) reference. The following abbreviations are used to indicate monomer components of the polymers in the following examples: MMA - Methyl Methacrylate EA - Ethyl Acrylate BA - n-Butyl Acrylate BMA - n-Butyl Methacrylate In the examples and elsewhere in the specification and claims, all ratios and percentages are by weight unless otherwise indicated, and all reagents are of good commercial quality unless otherwise indicated. In all emulsion preparations, the water used is deionized water. The following examples are intended to illustrate the invention. Example 1 This example illustrates the preparation of a high-molecular-weight acrylic MRM polymer employed in the present invention having an overall composition MMA/EA/BMA = 79.8/13.2/7.0, and molecular weights or M w = 4 x 10⁶ and M n = 1 x 10⁶. To a 3-neck, 5-liter flask equipped with a stirrer, reflux condenser and nitrogen sweep was added 455 g water, 0.16 g glacial acetic acid, 0.78 g sodium chloride and 4 g of emulsifier; the emulsifier was rinsed into the vessel with an additional 35 ml of water. The contents of the vessel were adjusted to, and maintained at, 30°C while 100.4 g methyl methacrylate, 63.8 g ethyl acrylate and 18.2 g n-butyl methacrylate were added; the monomers were rinsed into the vessel with an additional 10 ml of water. A mixture of 0.231 g sodium formaldehyde sulfoxylate in 25 ml water was added to the vessel, followed by 0.33 g t-butyl hydroperoxide (70% active) as an initiator. Polymerization was evidenced by a rise in temperature of the vessel contents, beginning about two minutes after the initiation was added, with a peak temperature of about 65-70°C. The vessel contents were then cooled to 50°C by adding 130 ml water. An additional 12.2 g emulsifier were rinsed into the reactor with 5 ml water, and 481.1 g methyl methacrylate, 32.8 g ethyl acrylate and 32.8 g n-butyl methacrylate were added and rinsed into the vessel with 20 ml water. The temperature was adjusted to 35°C and the nitrogen sweep was discontinued. A mixture of 0.219 g sodium formaldehyde sulfoxylate in 20 ml water was added, followed by 0.39 g t-butyl hydroperoxide. After the exotherm peak, the vessel was cooled to room temperature, and a latex having 50.5% solids was removed from the vessel. Examples 2-7 These examples show the modification of blow-molding-related physical properties of polymer blends that simulate commercial blow-molding resins. The latex from Example 1 was isolated by spray drying, and melt blended at various levels, in a 25 mm ]illion extruder at 249°C, into a stabilized, 43/57 blend of poly(butylene terephthalate) (PBT) having an intrinsic viscosity, measured in 60/40 phenol/tetrachloroethane, of 1.1 dl/g at 25°C, with branched aromatic polycarbonate as described in U.S.-A-4,001,184, having an intrinsic viscosity, measured in methylene chloride, of 0.5 dl/g at 25°C, and marketed by General Electric Company as Lexan 151 (PC), containing 18% (based on the PBT + PC weight) core-shell impact modifier having a core (77.5 parts) polymerized from 71 parts butadiene, 3 parts styrene, 4 parts methyl methacrylate and 1 part divinylbenzene; a second stage polymerized from 11 parts styrene; and a shell polymerized from 11 parts methyl methacrylate and 0.1 parts 1.3-butylene glycol dimethacrylate. Impact resistance, modulus, extrusion sag time, melt creep rate and the dynamic melt-strength parameter, R*, described above, were determined for these blends, and are shown in Table I as Examples 2-4. The isolated latex was similarly blended at various levels into a stabilized, 75/25 blend of co-polyester-polycarbonate made according to EP-A-155,989 with stabilized poly(ethylene terephthalate) containing 18% (based on the co-polyester-polycarbonate weight) core-shell impact modifier having core of rubbery crosslinked poly(n-butyl acrylate, and graftlinked thereto, an outer, rigid shell of methyl methacrylate. Similar physical property measurements were made for these blends and are shown in Table I as Examples 5-7; extrusion sag time was determined using a barrel temperature of 249°C and a 3.18 mm die. Example MRM Polymer of Example 1, (wt. %) Notched Izod (joules/cm) Tensile MCR sec⁻¹ Extrusion Sag Time sec. Modulus (kPa) R* 2 0 7.74 2210 7.8 0.091 20 3 3 8.01 2217 10.0 0.037 29 4 5 7.90 2204 11.1 0.029 34 5 0 5.71 1188 4.9 0.13 27 6 3 6.30 1181 5.4 0.09 40 7 5 5.82 1167 5.8 0.06 44 As may be seen from the above table, the physical properties, such as the notched Izod impact values and the tensile modulus, of the resins were unchanged by the addition of the MRM polymer, but the melt-rheology properties, such as the melt creep rate, R* and extrusion sag time, were significantly improved. Example 8 This example illustrates preparation of blow-molding parisons from the blends of Examples 2 and 4 above, and the higher melt strength obtainable with the blends containing the MRM polymer. The blow-molding equipment used in this example was a 3.2 kg Sterling blow-molding machine with a 3.2 kg-capacity accumulator head, and controlled by a Maco 8000 process control system. The accumulator was fed with an 8.9 cm extruder equipped with a single Sterling barrier-type screw. The parison die was a 35.5 cm-diameter, annular die with a programmed gap width set to produce nominal 2.5 mm parison wall thickness. The blended polymer was pelletized, the pellets were fed to the single-screw extruder and extruded into the accumulator; when the accumulator was full, the polymer melt at 249°C was forced through the die to form a 122 cm-long parison. The polymer of Example 4 produced a short parison, about half the length of that from an equal weight of the control polymer of Example 2, indicative of thicker walls caused by a higher melt strength for polymer containing the MRM polymer. To obtain a parison of comparable length and wall thickness, the die gap for the polymer of Example 4 was decreased. Parison hang time for the similar-sized parisons was taken as the time for the bottom of the parison to sag to the floor, 1.0 meters below the bottom of the parison as formed. The hang time for the parison made from the control polymer of Example 2 was 2.5 seconds, and the parison sagged to the floor, with considerable narrowing at the top, while the hang time for the parison made from the resin of Example 4 was 6.2 seconds at the same temperature and 3.7 seconds at 260°C; both of the parisons made from the resin of Example 4 broke away near the die, after essentially no narrowing at the top, and fell to the floor. Examples 9-18 The following examples illustrate that high-molecular-weight acrylic MRM polymers of the present invention having various compositions are effective in improving the blow-molding-related rheological property of extrusion sag time when blended into the resin of Examples 2-4 at a level of 5%. The MRM polymers of the present invention used in these examples have the compositions and molecular weights indicated in Table II. The processes by which they were prepared are as follows: Process I is the process of Example 1, Process II indicates a multi-step, thermal emulsion polymerization, and Process III indicates a two-stage, redox emulsion polymerization. Extrusion sag time was determined as described above, using an extruder speed of 60 rpm, a barrel temperature of 249°C and a 1.59-mm die. The result are shown in Table II below: Example Composition (MMA/EA/BA/BMA) ( Ratio ) Prepared by Process M w (x10⁶) Extrusion Sag Time (sec) R* 9 99/1/0/0 III 2.7 153 9.6 10 99/1/0/0 II 2.7 107 9.9 11 99/1/0/0 III 1.5 115 10.3 12 79/13/0/3 I 4.1 126 9.7 13 79/13/0/3 I 7.5 177 9.8 14 75/1/0/24 III 2.9 145 9.6 15 75/1/0/24 II 3.3 145 10.3 16 100/0/0/0 3.1 142 9.8 17 86/0/7/7 I 2.5 109 10.6 18 Matrix Resin - - 76 7.0 Examples 19-23 In the following examples high-molecular-weight methyl methacrylate/ethyl acrylate/butyl methacrylate MRM polymers of the present invention were blended at a level of 5% with the resin of Examples 2-4. The composition of the MRM polymers, weight-average molecular weight, rheological parameter R*, melt creep rate (MCR) and extrusion sag time at a 249°C barrel temperature using a 1.59 mm die are shown in Table III, below: Example Compositions (MMA/EA/BMA (Ratio) M w (x10⁶) R* MCR (sec⁻¹) Extrusion Sag Time (sec) 19 75/1/24 4.1 9.7 0.04 12.3 20 73/3/24 4.5 9.5 0.06 12.8 21 89/1/10 3.5 10.1 0.06 11.5 22 87/3/10 3.2 10.6 0.05 11.6 23 798/7/132 4.2 10.2 0.08 12.1 Examples 24-27 In the following examples, high-molecular-weight methyl methacrylate/butyl acrylate/butyl methacrylate polymers of the present invention were blended at a level of 5% with the resin of Examples 2-4. The blends were tested as in Examples 19-23, and the results are shown in Table IV, below: Example Compositions (MMA/EA/BMA Ratio) M w (x10⁶) R* MCR (sec⁻¹) Extrusion Sag Time 24 747/13/24 4.7 10.5 0.04 12.8 25 722/38/24 4.6 10.3 0.05 12.7 26 887/13/10 3.2 10.6 0.07 11.7 27 862/38/10 3.2 10.4 0.07 11.3 Examples 28-35 These examples illustrate the effect of functional monomers, when incorporated into the MRM polymers of the present invention, upon physical properties of blends of the polymers with the resin of Examples 2-4. Functional monomers used include maleic anhydride (MAH), methacrylic acid (MAA), diallyl maleate (DALM) and butylene glycol dimethacrylate (BGDMA), and the polymers were prepared using a two-stage redox emulsion polymerization. The compositions of the MRM polymers were as follows: MRM Polymer B MMA/BMA/EA/DALM = 728/24/3/02 MRM Polymer C MMA/BMA/EA/DALM = 809/17/2/01 MRM Polymer D MMA/BMA/EA/DALM = 888/10/1/02 MRM Polymer E MMA/BA/DALM//MMA/BGDMA = 7824/16/16//198/02 Properties measured were extrusion sag time, the rheological parameter (R*) and melt creep rate (MCR). The extrusion sag time was determined as described above, using an extruder speed of 60 rpm, a barrel temperature of 249°C and a 159-mm die. The results are shown in Table V. Example MRM Polymer, Level (%) MRM Polymer M w (x10⁶) Extrusion Sag Time (sec) R* MCR (sec⁻¹) 28 0 -- 7.3 6.7 -- 29 0 -- 7.8 7.1 0.090 30 B, 5% Note 11.0 10.0 0.040 31 C, 5% 3.7 11.5 10.3 0.034 32 D, 5% Note 11.5 10.0 0.036 33 0 -- 7.1 0.090 34 E, 3% Note -- 8.5 0.039 35 E, 5% Note -- 12.7 0.030 Note: The molecular weight for these polymers could not be determined, because they were insoluble in tetrahydrofuran. Examples 36-38 These examples illustrate the improvement of extrusion sag time as the level of an MRM polymer is increased in a branched polycarbonate (PC). The MRM polymer was prepared using a two-stage, redox emulsion polymerization and has a molecular weight of 4.6 x 10⁶ and the composition 72.16% MMA/ 24% BMA/ 3.84% BA, and the branched polycarbonate is that described in Examples 2-4 as a component of the blended polycarbonate-polyester resin. The extrusion sag time was determined as described above, using an extruder speed of 60 rpm, a barrel temperature of 266°C and a 3.18-mm die. The results are shown in Table VI, below. Example Branched PC (%) Acrylic Polymer (%) Extrusion Sag Time (sec) 36 (comparative) 100.00 0.0 10.5 37 95.0 5.0 15.0 38 90.0 10.0 20.1 Examples 39-41 These examples illustrate that inclusion of a conventional impact modifier into a branched polycarbonate fails to improve its extrusion sag time, and in fact decreases it slightly, while addition of the high-molecular-weight acrylic MRM polymer according to the present invention substantially improves the extrusion sag time. The branched polycarbonate (PC) is that described in Examples 2-4 as a component of the blended polycarbonate-polyester resin. The MRM polymer was that of Example 1 and had molecular weight of 4.1 x 10⁶, and the impact modifier was the core-shell impact modifier described in Examples 5-7. The extrusion sag time was measured as described above, using an extruder speed of 60 rpm, a barrel temperature of 266°C and a 1.59-mm die. The results are shown in Table VII. Example Branched PC (%) Impact Modifier (%) Acrylic Polymer (%) Extrusion Sag Time (sec) 39 (comparative) 100.0 0.0 0.0 8.4 40 (comparative) 90.0 10.0 0.0 8.0 41 85.0 10.0 5.0 13.5 Examples 42-49 These examples show the improvement of the blow-molding-related property, extrusion sag time, as the level of an MRM polymer of the present invention is increased in a resin similar to that of Examples 2-4. In these examples the amount of impact modifier of Examples 2-4 was held constant, and the high-molecular-weight acrylic MRM polymer, made using a two-stage, redox emulsion polymerization and having a molecular weight of 4.3 x 10⁶ and a composition of 72.16% MMA/3.84% EA/24% BMA, replaced a portion of the polycarbonate-poly(butylene terephthalate) (PC-PBT) in the blend, to the extent indicated below in Table VIII. Extrusion sag time was measured as described above, using an extruder speed or 60 rpm, a barrel temperature of 249°C and a 1.59-mm die. Example PC-PBT (%) Impact Modifier (%) Acrylic Polymer (%) Extrusion Sag time (sec) 42 (comparative) 85.0 15.0 0.0 7.8 43 84.0 15.0 1.0 9.9 44 82.0 15.0 3.0 12.0 45 80.0 15.0 5.0 14.3 46 78.00 15.0 7.0 15.3 47 75.00 15.0 10.0 17.2 48 70.00 15.0 15.0 19.4 49 65.00 15.0 20.0 22.5 Examples 50-52 These examples show the improvement of extrusion sag time as the level of a MRM polymer of the present invention is increased in an unmodified, linear polycarbonate (PC). The MRM polymer was made using a two-stage redox emulsion polymerization and had a composition of 72.16% MMA/24% BMA/3.84% BA, and a molecular weight of 46 x 10⁶. The extrusion sag time was determined as described above, using an extruder speed of 60 rpm, a barrel temperature of 266°C and a 159-mm die. The results are shown in Table IX, below. Example Linear PC (%) Acrylic Polymer (%) Extrusion Sag Time (sec) 50 (comparative) 100.0 0.0 3.3 51 95.0 5.0 5.2 52 90.0 10.0 7.1 Examples 53-58 These examples illustrate the effect on extrusion sag time of additional thermoplastic engineering resins when the high-molecular-weight acrylic MRM polymers are incorporated in them according to the present invention. In the following table, the resins listed are S/AN, a poly(styrene-acrylonitrile) resin marketed by Monsanto as Lustran® SAN-35; S/MAH, a poly(styrene-maleic anhydride) resin marketed by Arco as Dylark® 332; polyarylate, an aromatic polyester resin marketed by Union Carbide as Ardel® D-240; PEI, as poly(ether-imide) resin marketed by General Electric Company as Ultem® 1000; Nylon-6 a poly(caprolactam) marketed as Capron® 8202 by Allied Chemical and PBT, a poly(butylene terephthalate) resin having an intrinsic viscosity measured in 60/40 phenol/tetrachloroethane of 1.1 dl/g at 25°C and marketed by General Electric Company as Valox® 315. The acrylic polymers were blended into the thermoplastic resins using 25 mm Killion single-screw extruder at the indicated barrel temperatures. Extrusion sag time was also measured at the indicated barrel temperatures using a 3.18 mm die and the procedure described above. The results are shown in Table X where Examples 53B to 58B are comparative. Example Acrylic Polymer M w x10⁶ Blend Level Thermo-Plastic Resin Barrel Temp (°C) Extrusion Sag time (sec) 53A A 4.6 10 S/AN 360 48.2 53B - 0 S/AN 360 22.6 54A A 4.6 10 S/MAH 425 43.5 54B - 0 S/MAH 425 9.9 55A A 4.6 10 Polyarylate 500 10.3 55B - 0 Polyarylate 500 4.7 56A A 4.6 10 PEI 600 11.5 56B - 0 PEI 600 6.5 57A B 4.9 5 Nylon-6 450 16.8 57B - 0 Nylon-6 450 8.5 58A B 4.9 10 PBT 480 10.5 58B - 0 PBT 480 5.2 Examples 59-60 These examples illustrate the preparation and testing of thermoformable sheet from thermoplastic engineering resins containing the MRM polymers of the present invention. By a process similar to that of Examples 2-4 blends were prepared having the following compositions: Example 59 (Comparative) Example 60 PBT of Examples 2-4 34.00% 34.00% PC of Examples 2-4 44.75% 39.75% Impact Modifier of Examples 2-4 20.00% 20.00% Stabilizers 1.25% 12.5% MRM Polymer 0.00% 50.0% The MRM polymer was that described in Examples 50-52. The initial extrusion blending was carried out in a 6/35-cm Prodex extruder; the extruded, pelletized blends were then extruded into sheets and cut to 43-cm by 91-cm tests sheets with a thickness of 1.6 to 2.0 mm. The sheets were hung by one edge in an oven at 175-190°C to soften them for thermoforming. The sheets of blend without the MRM polymer were observed to fall to the oven floor if allowed to remain at the thermoforming temperature for longer necessary for handling, while the sheets of blends containing the MRM polymer had sufficient melt strength to hang in place for long periods. Using the Rheometrics Dynamic Spectrometer described above in the oscillating parallel-plate mode, the rheology of the two blends was determined at 15% strain during a 260°C-205°C temperature sweep; the oscillation frequency was 1 hr. The contributions of elastic (G') and viscous (G'') rheology components to the complex viscosity of the blend are shown in Table XI. Rheology Component Example 59 (Comparative) Example 60 (G') elastic (dynes/cm²) 9.6 x 10⁵ 1.2 x 10⁶ (G'') viscous (dynes/cm²) 8.9 x 105 1.1 x 10⁶ Complex viscosity (poise) 1.3 x 10⁶ 6.6 x 10⁶

Claims: The use of a polymer of units of one or more copolymerisable vinyl monomers, wherein at least 50% by weight of the units have the formula I: where R₁ is H or CH₃ and R₂is one of alkyl, substituted alkyl, cycloalkyl, aryl, aralkyl or alkaryl; said polymer having a weight average molecular weight of 1,500,000 to 10,000,000; for increasing the extrusion sag time of thermoplastic engineering resin in a process for blow moulding, thermoforming or extruding said engineering resin, in which process the said polymer is present in an amount of 1 to 25% by weight of the total weight of engineering resin plus said polymer. Use, according to claim 1, wherein R₂ is selected from the group consisting of methyl, ethyl and n-butyl. Use, according to claim 1 or 2, wherein at least 70% by weight of the units of said polymer are units having the formula (I). Use, according to claim 3, wherein a maximum of 5% of the units are units from a polyethylenically unsaturated monomer. Use, according to claim 1 or 2, wherein all of the units of the acrylic polymer are units having the formula (I). Use, according to any preceding claim, wherein the thermoplastic engineering resin comprises polycarbonate, polyester, poly(aromatic ketone), poly(phenylene ether), poly(phenylene sulfide), polysulfone, poly(ether-imide), polyacetal, polyimide, polyamide, poly(amide-imide), and/or copolymers and blends of any of the above, and/or copolymers of styrene and alkyl-substituted styrene with acrylonitrile and maleic anhydrides, and/or blends of such styrene copolymers with the above copolymers and blends. Use, according to any preceding claim, wherein the said polymer is present at a level of from 1 to 10% by weight, preferably 5 to 10% by weight. Use, according to any preceding claim, wherein the moulded, thermoformed or extruded composition further contains impact modifier and/or filler

Inventors: MEMON NAZIR AHMED, MEMON, NAZIR AHMED
Applicants: ROHM & HAAS, ROHM AND HAAS COMPANY
Application year: 1989
Main classification: C08L101
IPC codes: B29C49, C08L101