A PROCESS FOR SIZING PAPER USING SELF-EMULSIFIABLE SIZE

Abstract: Self-emulsifiable sizing agent comprises a copolymer of a polyoxyalkylenealkenylether of formula (I) with maleic anhdyride, or a mixt. of the copolymer with an alkenylsuccinic anhydride (II) or with a ketone dimer (III). (where Z = residue of a cpd contg 2-8 OH gps.; AO = one or at least 2 types of oxyalkylene gps. contg. 2-18C, which may be bonded randomly or in block; R = 2-5C alkenyl gps. R' = 1-24C hydrocarbon gp. or acyl. a, b and c each is at least 0. l = 1-2; m = 0-7; n/(l+m+n) = 0-1/3 al+bm+cn = 1-500 and l+m+n =2-8).

Description: The present invention relates to a process for sizing paper using self-emulsifying sizing agents, which are particularly able to have long shelf stability and easily formable emulsifiable liquid by mixing water. As a reactive sizing agent which is usable for paper industry, alkenylsuccinic anhydrides and ketene dimers are known ("Pulp and Chemistry and Chemical Technology" Third Edition, JOHN WILEY & SONS, Inc. NEW YORK (1981). α-Olefin-maleic anhydride copolymers are also disclosed in JP-A-62-25798/1987. As emulsifying agents, addition products of ethylene oxides to higher alcohols, alkylphenols, higher fatty acids or the like (Oil chemistry, vol. 10, p.282 (1961)) are usually used, and these addition products have free hydroxyl groups. As a treating agent for sizing paper, an emulsifiable liquid which is obtained by mixing a sizing agent and an emulsifying agent and then by mixing the mixture and water is usable. Accordingly, if a mixture of a sizing agent and an emulsifying agent has long shelf stability, it is conveniently usable for sizing paper. However, since the conventional emulsifying agent has free hydroxyl groups, there are problems that the emulsifying agent and the sizing agent are reacted and the sizing effect is lowered during the mixture is preserved. Furthermore, since the conventional sizing agent has remarkable hydrophobic nature, it is required to emulsify the sizing agent with an emulsifying agent. The emulsifying agent has hydrophilic nature, so that the mixture of the sizing agent and the emulsifying agent often shows insufficient sizing effect. An object of the present invention is to provide a process for sizing paper using sizing agents which are easily emulsifiable by mixing water, which have excellent sizing effect, long shelf stability and little lowered sizing effect. Another object of the present invention is to provide a process for sizing paper using emulsifying agents which have long shelf stability even if the emulsifying agents are mixed with conventional alkenylsuccinic anhydrides or ketene dimers, and have little lowered sizing effect during the mixtures are preserved. The inventors of the present invention earnestly studied and they found that copolymers of polyoxyalkylene alkenyl ethers having a specific structure and maleic anhydride are stable and self-emulsifiable and have excellent sizing effect. Further, they found that the copolymers act so as to emulsify alkenylsuccinic anhydrides or ketene dimers which are used as sizing agents, and that the copolymers have good stability even if they are mixed with alkenylsuccinic anhydrides or ketene dimers, because there is no reaction between the copolymers and the sizing agents. Namely, the present.invention resides in a method for sizing paper by using a copolymer of polyoxylakylene alkenyl ether and maleic anhydride, the polyoxyalkylene alkenyl ether being represented by the general formula (1): wherein Z is a residue of compounds having 2-8 hydroxy groups, AO is one or more oxyalkylene groups of 2-18 carbon atoms, however, the bond may be under a random or blocking condition when AO is two oxyalkylene groups or more, R is an alkenyl group of 2-5 carbon atoms, R¹ is a hydrocarbon or an acyl group of 1-24 carbon atoms, a ≧ O, b ≧ O, c ≧ O, ℓ = 1-2, m = O-7, O ≦ n/(ℓ + m + n) ≦ 1/3, aℓ + bm + cn = 1-5OO and ℓ + m + n = 2-8. In the general formula (1), as the compounds having 2-8 hydroxy groups in which Z is a residue, glycols such as ethylene glycol, propylene glycol, butylene glycol, hexylene glycol, styrene glycol, alkylene glycol of 8-18 carbon atoms, and neopentyl glycol, polyols such as glycerin, diglycerin, polyglycerin, trimethyrolethane, trimethyrolpropane, 1,3,5-pentanetriol, erythritol, pentaerythritol, dipentaerythritol, sorbitol, sorbitan, sorbide, a condensate of sorbitol and glycerin, adonitol, arabitol, xylitol, mannitol, or their partially etherified compounds or their partially esterified compounds, sugars such as xylose, arabinose, ribose, ramnose, glucose, fructose, galactose, mannose, sorbose, cellobiose, maltose, isomaltose, trehalose, sucrose, or their partially etherified compounds or their partially esterified compounds are exemplified. As oxyalkylene groups represented by AO, oxyethylene, oxypropylene, oxytetramethylene, oxystyrene, oxydodecylene, oxytetradecylene, oxyhexadecylene, oxyoctadecylene are exemplified. One or more of these groups may be selected and two or more groups may be bound at random or in a block arrangement. As alkenyl groups of 2-5 carbon atoms represented by R, vinyl, allyl, methallyl, 3-butenyl, 4-pentenyl, 3-methyl-4-butenyl are exemplified. As hydrocarbon groups of 1-24 carbon atoms represented by R¹, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tertiary butyl, amyl, isoamyl, hexyl, heptyl, 2-ethylhexyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, hexadecyl, isohexadecyl, octadecyl, isooctadecyl, oleyl, octyldodecyl, dococyl, decyltetradecyl, benzyl, cresyl, butylphenyl, dibutylphenyl, octylphenyl, nonylphenyl, dodecylphenyl, dioctylphenyl, dinonylphenyl, styrenated phenyl are exemplified. As acyl groups of 1-24 carbon atoms, there are acyl groups derived from acetic acid, propionic acid, butyric acid, isobutyric acid, caproic acid, enanthic acid, caprylic acid, 2-ethylhexanoic acid, pelargonic acid, capric acid, undecylenic acid, lauric acid, myristic acid, palmitic acid, margaric acid, stearic acid, arachic acid, behenic acid, palmitoleic acid, oleic acid, linoleic acid, linolenic acid, erucic acid, isopalmitic acid, isostearic acid, benzoic acid, hydroxybenzoic acid, cinnamic acid, gallic acid are exemplified. Polyoxyalkylene alkenyl ether represented by the general formula (1) requires at least an alkenyl group for copolymerizing with maleic anhydride. Since polyoxyalkylene alkenyl ether having two or more alkenyl groups is apt to crosslink these groups, it is difficult to dissolve or disperse the compound in water. When the compound represented by the general formula (1) wherein ℓ is 2 is used, 0.1 moles or less of the compound to 1 mole of the compound represented by the general formula (1) is preferably used. The compounds represented by the general formula (1) wherein ℓ is 3 or more are unsuitable for using because the compounds are easily crosslinked. The sizing agents used in the process of the present invention are characterized in that these agents have functional groups of acid anhydrides. Polyoxyalkylene alkenyl ether represented by the general formula (1) having many hydroxy groups is undesirable, because esterification reaction is occurred and maleic anhydride is consumed when the ether and the acid anhydride are copolymerized. Accordingly, it is required that n/(ℓ + m + n) is 1/3 or less, preferably n is 0. The number of hydroxy groups of the polyhydroxy compound having a residue of Z is 8 or less, because the production of the compound represented by the general formula (1) becomes difficult when the number is more than 8. The number of oxyalkylene groups of the self emulsifying sizing agent is at least one. When the average number of the total amount aℓ + bm + cn is above 500, it is hard to handle the agent because the viscosity of the agent increases and it is inconvenient to emulsify. Polyoxyalkylene alkenyl ether represented by the general formula (1) is obtainable by etherifying or esterifying the addition product of alkylene oxide to monovalent alkenyl alcohol, or by etherifying with alkenyl chloride the addition product of alkylene oxide to monovalent alcohol or monovalent carboxylic acid. Further, polyoxyalkylene alkenyl ether (1) is obtainable by etherifying or esterifying a product which is obtained by adding alkylene oxide to alkenyl ether of a polyhydroxy compound, or by etherifying or esterifying after alkenyl etherifying a product which is obtained by adding alkylene oxide to a polyhydroxy compound. The copolymerization reaction of the ether (1) and maleic anhydride can be conducted by using, for example, a radical catalyst which is disclosed in JP-A-45-31950/1970. In the copolymerization of compound represented by the general formula (1) and maleic anhydride, the molar ratio of these monomers is 3:7-7:3, preferably about 1:1. The weight-average molecular weight of the copolymer is 1,000-1,000,000, preferably 3,000-500,000. As the sizing agents used in the process of the present invention, only one copolymer can be used. However, a copolymer which has a small addition number of alkylene oxides having large sizing effect is preferably used together with a copolymer which has a great addition number of alkylene oxides and is emulsible the above copolymer. The sizing agents used in the process of the present invention are usable after emulsifying in water and the usage is usually 0.01-3 wt% based on the amount of pulp. Further, the sizing agents used in the process of the present invention include a mixture of the copolymer with emulsible alkenylsuccinic anhydrides represented by the general formula (2) or ketene dimers represented by the general formula (3). The mixture of the sizing agent and the compound (2) or the compound (3) can be stably stored over a long period time, and good sizing effect is maintainable. wherein R² is an alkyl group of 6-22 carbon atoms. wherein R³ and R ⁴ are the same or different alkyl groups of 6-22 carbon atoms. As the alkyl group of 6-22 carbon atoms represented by R², hexyl, heptyl, octyl, decyl, dodecyl, tetradecyl, hexadecyl, octadecyl, eicosyl and docosyl are exemplified, and these groups may be straight chains or branched chains. The alkenylsuccinic anhydrides of the general formula (2) are obtainable by the addition reaction of olefins of 8-24 carbon atoms and maleic anhydride. As the alkyl groups of 6-22 carbon atoms represented by R³ and R⁴, hexyl, decyl, dodecyl, tetradecyl, hexadecyl, eicosyl and docosyl are exemplified. The ketene dimers of the general formula (3) are obtainable by a dehydrohalogenation reaction in which a fatty halide such as coconut oil fatty chloride, hardened beef tallow fatty chloride or stearic chloride is reacted with a trialkyl amine. The carbon numbers of the alkenylsuccinic anhydrides or the alkyl groups of the ketene dimers are limited because the sizing effect is little at the carbon number of less than 6 and the emulsification is lowered at the carbon number of more than 22. In the sizing agent which is a mixture of an alkenylsuccinic acid or a ketene dimer and a copolymer, the copolymer is 1 wt% or more of the composition, preferably 5 wt% or more. The upper limit is not particularly limited. Since the sizing agents used in the process of of the present invention are constituted from the copolymers of polyoxyalkylene alkenyl ethers having a specific structure and maleic anhydride, the agents are self-emulsifiable and have a good sizing effect and the sizing effect is not lowered after storing them over a long period of time. When the mixture of a copolymer and an alkenylsuccinic anhydride or a ketene dimer is used, in usual emulsifiers, it is necessary to mix immediately before using them because the sizing effect is lowered during the mixture is preserved. On the other hand, in the present invention, even if the mixture is preserved over a long period of time after mixing them, the sizing effect is good and not lowered. The process of present invention is illustrated by the following Examples and Comparative Examples. By using compounds of the general formula (1) shown in Table 1 and compounds of Comparative Examples shown in Table 2, sizing agents which are shown in Table 3 and 4 were prepared. Paper was treated for sizing by using these sizing agents immediately after preparing them and one month after preparing them by the following method. The extent of sizing of the paper treated was determined. To a 1.0 wt% slurry of the pulp [the mixture of NBKP (Northern pulp) and LBKP (Southern pulp) in the same amount], 0.2 wt% aqueous emulsion of the sizing agent shown in Table 3 containing 0.2 wt% solids based on pulp and then cationized starch of 0.2 wt% based on the pulp were added. The slurry obtained was manufactured to paper having a weight of 60-62 g/m² with a tappi standard sheet machine. The paper obtained was pretreated in accordance with JIS (Japanese Industrial Standard) p8111, and then the Stekihit size of the paper was determined. The results are shown in Table 5. As shown in Table 5, it was found that the sizing effect of the process of the present invention was superior to that of the Comparative Examples and it was maintained over a long period of time after preparing the sizing agents. As described above, since the self-emulsifying sizing agents used in the process of the present invention are preservable over a long period of time and emulsifiable liquid is formed by mixing these agents and water, these agents are suitable for sizing agents for treating paper.

Claims: A process for sizing paper by using a self-emulsify ing sizing agent comprising a copolymer of polyoxyalkylene alkenyl ether and maleic anhydride, the polyoxyalkylene alkenyl ether being represented by the general formula (1): wherein Z is a residue of compounds having 2-8 hydroxy groups, AO is one or more oxyalkylene groups of 2-18 carbon atoms, however, the bond of the oxyalkylene groups may be under a random or blocking condition when AO is two oxyalkylene groups or more, R is an alkenyl group of 2-5 carbon atoms, R¹ is an hydrocarbon or an acyl group of 1-24 carbon atoms, a ≧ 0, b ≧ 0, c ≧ 0, ℓ = 1-2, m = 0-7, 0 ≦ n/(ℓ + m + n) ≦ 1/3, aℓ + bm + cn = 1-500 and ℓ + m + n = 2-8. The process according to claim 1, wherein the self-emulsifying sizing agent comprises a copolymer as described in claim 1 and an alkenylsuccinic anyhride which is represented by the general formula (2): wherein R² is an alkyl group of 6-22 carbon atoms. The process according to claim 1, wherein a self-emulsifying sizing agent comprises a copolymer as described in claim 1 and a ketene dimer which is represented by the general formula (3): wherein R³ and R⁴ are the same or different alkyl groups of 6-22 carbon atoms.

Inventors: AKIMOTO SHIN-ICH, HONDA SUSUMU, TAKAHASHI FUJIO, TAKAHASHI HIDEKI - KAMINOTANI, YASUKOHCHI TOHRU - - FUJISAKI, AKIMOTO, SHIN-ICH, HONDA, SUSUMU, TAKAHASHI, FUJIO, TAKAHASHI, HIDEKI 2-49, KAMINOTANI 4-CHOME, YASUKOHCHI, TOHRU 3-10-404, FUJISAKI 2-CHOME
Applicants: NIPPON OILS & FATS CO LTD, NIPPON OIL AND FATS COMPANY, LIMITED
Application year: 1989
Main classification: D21H17
IPC codes: D21H17