Curing composition showing improved drying characteristics of alkyd coating

Abstract: A curing composition showing improved drying characteristics of an alkyd coating which comprises: (A) an oxyalkylene polymer having at least one silicon atom-containing group which has a hydroxyl group or a hydrolyzable group bound to a silicon atom and is capable of crosslinking by forming a siloxane bond; (B) a polymeric plasticizer and/or a viscous plasticizer; and (C) an air curing compound.

Description: This invention relates to a curing composition which comprises an oxyalkylene polymer having a silicon atom-containing group which has a hydroxyl group or a hydrolyzable group bound to a silicon atom and is capable of crosslinking by forming a siloxane bond. The silicon-atom containing group will be simply called a reactive silicon group hereinafter. An oxyalkylene polymer having a reactive silicon group is curable at room temperature to thereby give a rubber-like material, similar to a room temperature curing silicone rubber. The cured material thus obtained is excellent in tensile properties and adhesiveness and thus is widely available in, for example, sealants and adhesives. One of the characteristics of an oxyalkylene polymer having a reactive silicon group is that almost every common coating can be applied onto the surface of the material obtained by curing said oxyalkylene polymer. In contrast thereto, no coating can be applied onto the surface of a silicone rubber in practice, since said surface is water- and oil-repellant. However it is observed that an alkyd coating film formed on the surface of a cured material of a composition comprising an oxyalkylene polymer having a reactive silicon group shows sometimes poor drying characteristics, which can make it impractical to apply said coating onto said cured material. It was not known why the alkyd coating shows such poor drying characteristics. As the result of our extensive studies, we have found that a plasticizer, in particular, one having a low viscosity and a low molecular weight contained in a curing composition comprising an oxyalkylene polymer having a reactive silicon group deteriorates the drying characteristics of an alkyd coating. A plasticizer is employed in order to lower the viscosity of the composition to thereby improve its workability or to improve the tensile properties of the cured material. We have attempted to determine a plasticizer which would not deteriorate the drying characteristics of an alkyd coating. As a result, we have found that the above problem can be solved by using a so-called polymeric plasticizer. We have already filed U.S. patent applications (entitled "Method of Applying Alkyd Paints to Oxyalkylene Polymers Having a Reactive Silicone Group" and "Curing Composition of Oxyalkylene Polymer" on Dec. 26, 1987 and Dec. 28, 1987, respectively) directed to this discovery. The U.S. application filed on Dec. 26, 1987 is the priority document for EP-A-324 156 and the U.S. application filed on Dec. 28, 1987 is the priority document for EP-A-322 857. We have attempted to further improve the drying characteristics of an alkyd coating and consequently found that the drying characteristics of an alkyd coating can be further improved by using a composition which comprises an oxyalkylene polymer having a reactive functional silicon group and a polymeric plasticizer, thus completing the present invention. Accordingly, the present invention relates to a curing composition showing improved drying characteristics of an alkyd coating which comprises: (A) an oxyalkylene polymer having at least one silicon atom-containing group which has a hydroxyl group or a hydrolyzable group bound to a silicon atom and is capable of crosslinking by forming a siloxane bond; (B) a polymeric plasticizer having a molecular weight of 500 to 15,000 selected from polyesters and polyethers wherein a terminal hydroxyl group of the polyether plasticizer is blocked with an alkyl group, an aryl group or an alkenyl group through an ether bond, an ester bond, an urea bond, an amide bond or a carbonate bond; and (C) a liquid polybutadiene. In the present invention, an oxyalkylene polymer having at least one reactive silicon group, which will be also called an oxyalkylene polymer (A) hereinafter, is used. The abovementioned oxyalkylene polymer (A) is described, for example, in U.S. Patent Nos. 3,971,751, 3,979,384 and 4,323,488 and JP-B-45-36319, 46-12154, 49-32673, 50-156599, 51-73561, 54-6096, 55-82123, 55-123620, 55-125121, 55-131022, 55-135135 and 55-137129. (The term "JP-B" means an examined Japanese patent publication). The molecular chain of the oxyalkylene polymer (A) essentially comprises a repeating unit represented by the following general formula: -R¹-O- wherein R¹ is an optionally substituted divalent hydrocarbon group having one to eight carbon atoms. It is preferred that R¹ is a divalent alkylene group having one to eight, more preferably, two to four, carbon atoms. Some of the hydrogen atoms of this alkylene group may be substituted by substituent(s) such as a chlorine atom. Preferred examples of R¹ include and -CH₂CH₂CH₂CH₂-. Among these groups, is particularly preferred. The molecular chain of said oxyalkylene polymer (A) may comprise either one or more kinds of said repeating units. The main chain of the oxyalkylene polymer (A) may comprise a repeating unit of the general formula -R¹-O-optionally together with other repeating unit(s). When it comprises repeating unit(s) other than the one defined above, it preferably comprises 60% (by weight, the same will apply hereinafter) or more, preferably 80% or more, of the repeating -R¹-O- based on the weight of the total polymer. The reactive silicon group contained in the oxyalkylene polymer (A) is a well known functional group. It can be crosslinked even at room temperature. A typical example of the reactive silicon group is the one represented by the following general formula (I): wherein R² represents an optionally substituted monovalent organic group having 1 to 20 carbon atoms, provided that two or more R² groups, if present, may be either the same or different from each other; X represents a hydroxyl group or a hydrolyzable group, provided that two or more X groups, if present, may be either the same or different from each other; a is 0, 1 or 2; b is 0, 1, 2 or 3, provided that (the sum of a and b) ≧ 1; and m is 0 or an integer of 1 to 19, provided that may be either the same or different from each other, when m is 2 or above. Among reactive silicon groups of the general formula (I), those represented by the following general formula (II) are preferred from, for example, an economic viewpoint: wherein R² is as defined above; and ℓ is 1, 2 or 3. Examples of the hydrolyzable group represented by X in the general formula (I) or (II) include a halogen atom such as a chlorine atom; a hydrogen atom; an alkoxy group such as a methoxy group or an ethoxy group; an acyloxy group such as an acetoxy group; a ketoxymate group such as a dimethyl ketoxymate group; an amino group such as a dimethylamino group; an amide group such as an N-methylacetamide group; an aminooxy group such as a dimethylaminooxy group; a mercapto group such as a thiophenoxy group; and an alkenyloxy group such as an isopropenyloxy group. Among these hydrolyzable groups, alkoxy groups such as methoxy and ethoxy groups are preferred because of the mild hydrolysis properties thereof. Examples of the R² group in the general formula (I) or (II) include optionally substituted hydrocarbon groups having 1 to 20, preferably 1 to 10, carbon atoms such as an alkyl group such as a methyl group, an ethyl group or a chloromethyl group; a cycloalkyl group such as a cyclohexyl group; an aryl group such as a phenyl group, a tolyl group or a chlorophenyl group; an aralkyl group such as a benzyl group; and an alkenyl group such as a vinyl group. Examples of the R² group further include a triorganosiloxy group represented by the following general formula: (R')₃ SiO- wherein R' represents an optionally substituted monovalent hydrocarbon group, provided that the three R' groups are not always the same as each other; such as a trimethylsiloxy group. Among these groups, a methyl group is particularly preferred as a substituent. Although the oxyalkylene polymer (A) may have at least one reactive silicon group, it is preferred that said oxyalkylene polymer have at least 1.1, on average, more preferably 1.5 to 4, reactive silicon groups in order to achieve sufficient curing characteristics. Furthermore, it is preferred that said reactive silicon group(s) is located at the terminal of the molecular chain of the oxyalkylene polymer (A). The oxyalkylene polymer preferably has a number-average molecular weight of 3,000 to 30,000, more preferably, 5,000 to 15,000. An oxyalkylene polymer (A) may be employed alone. Alternatively, two or more oxyalkylene polymers (A) may be employed together. The oxyalkylene polymer (A) may be prepared by, for example, subjecting a hydrosilane compound wherein a hydrogen atom is bound to the group represented by the general formula (I) to an addition reaction together with an oxyalkylene polymer having an olefinically unsaturated group represented by the following general formula (III): wherein R³ represents a hydrogen atom or an organic group having 1 to 20 carbon atoms; R⁴ represents a divalent organic group having 1 to 20 carbon atoms; and c is 0 or 1; in the presence of a catalyst such as a platinum compound. Alternatively, the oxyalkylene polymer (A) may be prepared by the following methods. (1) A polyoxyalkylene group having a terminal hydroxyl group is reacted with a polyisocyanate compound such as toluene diisocyanate to thereby give an alkylene oxide polymer having a terminal isocyanate group which is then reacted with a silicon compound represented by the following general formula (IV): wherein W represents an active hydrogen-containing group selected from among a hydroxyl group, a carboxyl group, a mercapto group and a primary or secondary amino group; and ℓ, R², R⁴ and X are as defined above. (2) An oxyalkylene polymer having an olefinically unsaturated group represented by the general formula (III) is reacted with a silicon compound represented by the general formula (IV) wherein W is a mercapto group. (3) An oxyalkylene polymer having a terminal hydroxyl group is reacted with a compound represented by the following general formula: wherein R², R⁴, X and ℓ are as defined above. However, the process for preparing the oxyalkylene polymer (A) is not restricted thereby. In the preparation of the oxyalkylene polymer (A), some or all of the X groups may be further converted into other hydrolyzable groups or hydroxyl groups. When X groups are halogen atoms or hydrogen atoms, for example, they may be preferably converted into, for example, alkoxy groups, acyloxy groups, aminooxy groups, alkenyloxy groups or hydroxyl groups. In the general formula (III), R³ represents a hydrogen atom or an optionally substituted monovalent organic group having 1 to 20 carbon atoms. R³ preferably represents a hydrogen atom or a hydrocarbon group. A hydrogen atom is particularly preferred therefor. The R⁴ group as defined above is a divalent organic group. Preferable examples thereof include -R⁵-, -R⁵OR⁵-, groups wherein R⁵ represents a divalent hydrocarbon group having 1 to 10 carbon atoms. Particularly preferred examples thereof include methylene, ethylene, propylene and butylene groups. The oxyalkylene polymer having an olefinically unsaturated group represented by the general formula (III) may be prepared by, for example, a method disclosed in JP-A-54-6097 (the term "JP-A" means an unexamined published Japanese Patent Application) which comprises reacting the terminal hydroxyl group of an oxyalkylene polymer with a compound having an unsaturated group to thereby introduce said unsaturated group into the terminal of the oxyalkylene polymer through the formation of an ether bond, an ester bond, an urethane bond or a carbonate bond. Alternatively, the oxyalkylene polymer (A) may be prepared by copolymerizing an epoxy compound such as ethylene oxide or propylene oxide together with an olefinically unsaturated group-containing epoxy compound such as allyl glycidyl ether to thereby introduce said olefinically unsaturated group into a side chain. The composition of the present invention comprises a polymeric plasticizer. The polymeric plasticizer has a molecular weight of 500 to 15,000, preferably 700 to 10,000. Examples of the polymeric plasticizer include polyesters such as a polymer of a dibasic acid and a dihydric alcohol or a lactone polymer and polyethers such as polypropylene glycol or derivatives thereof. Polyesters and polyethers are preferred since they can improve the drying characteristics of an alkyd coating, they are highly compatible with the oxyalkylene polymer (A) and they can lower the viscosity of the composition. Polyethers are particularly preferred since they would impart a low modulus and a high elongation to the resulting cured composition. Among the abovementioned polyethers, those having a number-average molecular weight of at least 4,000, preferably at least 4,500 and more preferably 5,000 to 10,000, are favorable. A polyether having a small number of terminal hydroxyl groups is preferred since it can give improved drying characteristics to an alkyd coating. Those having essentially no terminal hydroxyl groups are more preferred. These polyethers include those wherein a terminal hydroxyl group is blocked with an alkyl group, an aryl group or an alkenyl group through an ether bond, an ester bond, an urea bond, an amide bond or a carbonate bond. It is preferred that the polyether comprises 10% or below, more preferably, 5% or below, (determined by the GPC method, the same will apply hereinafter) of component(s) of a number-average molecular weight of 1,000 or below in order to achieve improved drying characteristics of an alkyd coating. It is preferred that the polyether has a narrow range of molecular weight distribution (i.e., weight-average molecular weight (Mw)/number-average molecular weight (Mn)) in order to achieve improved drying characteristics of an alkyd coating, since the content of low molecular weight component(s) would decrease with a decrease in the above ratio. Namely, the polyether preferably has an Mw/Mn ratio of 2 or below, still preferably 1.5 or below. Examples of such a polyether as described above include polyoxypropylene glycol having a number-average molecular weight of 4,000 or above and showing a narrow molecular weight distribution or containing a small amount of component(s) having a molecular weight of 1,000 or below whose terminal hydroxyl group, preferably both terminal hydroxyl groups, is blocked with, for example, alkyl ether bond(s), alkyl phenyl ether bond(s), alkenyl ether bond(s) or aryl ether bond(s). The plasticizer may be blended as a solvent during the preparation of the oxyalkylene polymer (A). The polymeric plasticizer is preferably employed in an amount of 1 to 150 parts (by weight, the same will apply hereinafter), more preferably 10 to 120 parts and, most preferably 20 to 100 parts, per 100 parts of the oxyalkylene polymer (A). When the amount of the plasticizer is smaller than one part, the effects thereof as a plasticizer cannot be fully exerted. When it exceeds 150 parts, on the other hand, the resulting curing composition shows a lowered mechanical strength as well as insufficient drying characteristics of an alkyd coating. The liquid polybutadiene is an air curing compound which means a compound which cures through a reaction with atmospheric oxygen, and liquid 1,2-polybutadiene is more preferred. Examples of other air curing compounds include drying oils such as tung oil and linseed oil; various alkyd resins obtained by denaturing said drying oils; acrylic polymers, epoxy resins and silicone resins denatured with said drying oils; diene polymers such as C5 to C8 diene polymers; and materials obtained by denaturing the aforementioned polymers or copolymers with maleic acid or a boiled oil. Among these materials, tung oil, liquid diene polymers and denatured products thereof are particularly preferred. Examples of said liquid diene polymers include liquid polymers obtained by polymerizing diene compounds such as chloroprene, isoprene or 1,3-pentadiene; those obtained by copolymerizing these diene compounds with compatible monomers such as acrylonitrile or styrene; and materials obtained by denaturing said polymers with maleic acid or a boiled oil. One of these other air curing compounds or a mixture thereof can be used in the present invention. The air curing compound is preferably employed in the composition of the present invention in an amount of 0.1 to 20 parts, more preferably 1 to 10 parts, per 100 parts of the oxyalkylene polymer (A). When the content of the air curing compound is smaller than 0.1 part, the aimed improvement in the drying characteristics of an alkyd coating cannot be fully achieved. When it exceeds 20 parts, on the other hand, the resulting curing composition shows deteriorated tensile properties. There are some compounds which can serve both as a polymeric plasticizer and as an air curing compound. Such a compound may be used in a large amount as a plasticizer, though it is preferably used in an amount within the range as an air curing compound defined above. The composition of the present invention can be prepared by any method without restriction. A particular example of a method for preparing the same comprises simply adding the liquid polybutadiene and the polymeric plasticizer to the oxyalkylene polymer (A). In this case, the liquid polybutadiene and plasticizer can be homogeneously dispersed or dissolved in the oxyalkylene polymer (A) by appropriately controlling the conditions including heating and stirring. However, it is not required to establish a completely homogeneous and transparent dispersion. Namely, the object of the present invention can be satisfactorily achieved by establishing a dispersion, even if cloudy. A dispersion accelerator such as a surfactant can be further used together, if desired. Another process for preparing the composition of the present invention comprises blending definite amounts of the liquid polybutadiene and plasticizer with the oxyalkylene polymer (A) prior to the final use. When the composition of the present invention is to be formulated into, for example, a two-component sealing agent, the oxyalkylene polymer (A) is mixed with the liquid polybutadiene and plasticizer immediately before use. The composition of the present invention can further comprise various additives such as a curing catalyst for the oxyalkylene polymer (A) or a bulking agent. Examples of the curing catalyst include organotin compounds, acidic phosphates, materials obtained by reacting an acidic phosphate and an amine, saturated or unsaturated carboxylic acids and anhydrides thereof and organic titanate compounds. Examples of said organotin compounds include dibutyltin dilaurate, dioctyltin dimaleate, dibutyltin phthalate, tin octylate and dibutyltin methoxide. Examples of said acidic phosphates mean phosphates including a moiety, such as an organic acidic phosphate of the formula wherein d is 1 or 2 and R represents an optionally substituted hydrocarbon group having 1 to 20 carbon atoms. Examples thereof include the following compounds: Examples of said organic titanate compounds include titanates such as tetrabutyl titanate, tetraisopropyl titanate and triethanolamine titanate. When a curing catalyst is to be employed, it may be preferably added in an amount of 0.1 to 20 parts per 100 parts of the oxyalkylene polymer (A). Examples of said bulking agent include heavy calcium carbonate, light calcium carbonate, glue calcium carbonate, kaolin, talc, silica, titanium oxide, aluminum silicate, magnesium oxide, zinc oxide and carbon black. Examples of said other additives include anti-sagging agents such as hydrogenated castor oil or organic bentonite, colorants and antioxidants. The composition of the present invention can further comprise, as a matter of course, a low molecular weight and a less viscous plasticizer such as dioctyl phthalate, so long as the objects of the present invention are not inhibited thereby. The composition of the present invention thus obtained is useful in, for example, adhesives, pressure-sensitive adhesives, coatings, waterproof materials, sealants, templating materials, rubber-molding materials and foamed materials. For example, a construction sealant may be prepared in the following manner: 10 to 300 parts of an inorganic bulking agent(s) such as calcium carbonate, talc or kaolin are added to 100 parts of the oxyalkylene polymer (A) to be used in the present invention. Further appropriate amounts of pigment(s) such as titanium oxide or carbon black and antioxidant(s) such as UV absorber(s) and radical chain terminator(s) are added thereto, if desired. The mixture thus obtained is thoroughly kneaded homogeneously with a kneader or a paint roll and then applied. It is then exposed to the atmospheric moisture and cured therewith. Thus a rubber-like elastic material excellent in weathering properties, transparency and tensile elongation is obtained. When employed as a coating, the composition is cured under the same conditions as those described above. Thus it is highly useful as a highly elastic coating for construction uses, a primer for concrete materials and a waterproof material. An alkyd coating may be applied onto the cured material obtained from the composition of the present invention. In this case, the application can be readily conducted after the composition is almost completely cured. However, the application can be conducted when a cured material is formed on the surface of the composition. Any alkyd coating may be used without restriction. Examples thereof include those mainly comprising so-called oil-denatured alkyd resins which are obtained by denaturing a condensate obtained from a polybasic acid, such as phthalic anhydride or maleic anhydride, and a polyhydric alcohol, such as glycerol, pentaerythritol, ethylene glycol or trimethylolethane, with a fatty oil or a fatty acid such as linseed oil, soybean oil, castor oil or safflower oil; or denatured alkyd resins obtained by denaturing various resins with, for example, a vinyl monomer. It may be in any form, for example, alkyd resin varnish or enamel for automobile, aircraft or industrial uses; alkyd resin-blended paints (which are also called synthetic resin-blended paints) for coating buildings, bridges or marine structures; and alkyd resin primer coatings for automobiles, machinery, electrical devices and furniture. The present invention is hereinafter described in greater detail with reference to examples. Synthesis Example 1 800g of a polyoxypropylene polymer of an average molecular weight of approximately 8000, to approximately 97% of the total terminals of which allyl ether groups were introduced, was introduced into a pressure reactor provided with a stirrer and 19g of methyldimethoxysilane was added thereto. Then 0.34 ml of a solution of platinic chloride catalyst solution, obtained by dissolving 8.9g of H₂PtCl.6H₂O in 18 ml of isopropyl alcohol and 160 ml of tetrahydrofuran, was added thereto and the obtained mixture was allowed to react at 80°C for six hours. The amount of the silicon hydride remaining in the reaction mixture was determined by IR spectrometry. As a result, scarcely any silicon hydride was detected. Reactive silicon groups were determined by NMR. As a result, it was found that a polyoxypropylene polymer having approximately 1.7 terminal groups per molecule was obtained. Examples 1 to 3 and Comparative Examples 1' to 13' 100g of the polymer obtained in Synthesis Example 1 was blended with the plasticizer and the air curing compound, each in a definite amount, as shown in Table 1. Then 120g of calcium carbonate (CCR: manufactured by Shiraishi Kogyo K.K.), 20g of titanium oxide (R820: manufactured by Ishihara Sangyo K.K.), 0.5g of styrenated phenol and 2g of dibutyltin diacetylacetonate were added thereto. The obtained mixture was rolled thrice and then a sheet of 3 mm in thickness was prepared. The obtained sheet was cured at 23°C under a relative humidity (RH) of 65% for one day. Subsequently, a commercially available alkyd coating (Rubbol AZ: manufactured by Sikkens Co.) was applied thereto with a brush and then allowed to stand at 23°C under an RH of 65% to thereby examine the drying characteristics of the coating. Table 1 summarizes the results. In Table 1, the plasticizer A is the polyoxypropylene having allyl ether terminals used in Synthesis Example 1 (viscosity at 25°C: 35 poise); the plasticizer B is poly-α-methylstyrene (viscosity at 25°C: 35 poise); the plasticizer C is polypropylene glycol (MW: 5000, viscosity at 25°C: 9 poise); the plasticizer D is an isomeric triaryldiethane mixture (viscosity at 20°C: 50 poise); DOP means di-2-ethylhexyl phthalate (viscosity at 25°C: 0.5 poise); BBP means butyl benzyl phthalate (viscosity at 25°C: 0.5 poise); the liquid 1,2-polybutadiene is Nisso Polybutadiene B-100 manufactured by Nippon Soda Co., Ltd.; and the liquid 1,4-polybutadiene is Polyoil 130 manufactured by Nippon Zeon Co. In Table 1, A means that the applied coating was completely cured and showed no stickiness; B means that the applied coating was cured by somewhat sticky on the surface; C means that the applied coating was insufficiently cured and showed fingermarks; and D means that the applied coating was not cured.

Claims: A curing composition showing improved drying characteristics of an alkyd coating which comprises: (A) An oxyalkylene polymer having at least one silicon atom-containing group which has a hydroxyl group or a hydrolyzable group bound to a silicon atom and is capable of crosslinking by forming a siloxane bond; (B) a polymeric plasticizer having a molecular weight of 500 to 15,000 selected from polyesters and polyethers, wherein a terminal hydroxyl group of the polyether plasticizer is blocked with an alkyl group, an aryl group or an alkenyl group through an ether bond, an ester bond, an urea bond, an amide bond or a carbonate bond; and (C) a liquid polybutadiene. A curing composition as set forth in Claim 1, wherein said oxyalkylene polymer is an oxyalkylene polymer which has a main chain essentially comprising a repeating unit of the following general formula: -R'-O- wherein R' represents a substituted or unsubstituted hydrocarbon group having one to eight carbon atoms. A curing composition as set forth in Claim 1, wherein said silicon atom-containing group is represented by the following general formula (I): wherein R² represents a substituted or unsubstituted monovalent organic group having 1 to 20 carbon atoms, provided that two or more R² groups, if present, can be either the same or different from each other; X represents a hydroxyl group or a hydrolyzable group, provided that two or more X groups, if present, can be either the same or different from each other; a is 0, 1 or 2; b is 0, 1, 2 or 3, provided that (the sum of a and b) ≧ 1; and m is 0 or an integer of 1 to 19, provided that may be either the same or different from each other, when m is 2 or more. A curing composition as set forth in Claim 3, wherein X represents a hydrogen atom, a halogen atom, a hydroxyl group, an alkoxy group, an acyloxy group, a ketoxymate group, an amino group, an acid amido group, an aminooxy group, a mercapto group or an alkenyloxy group. A curing composition as set forth in Claim 3, wherein X represents an alkoxy group. A curing composition as set forth in Claim 1, wherein said polymeric plasticizer is a polyether.

Inventors: HIROSE TOSHIFUMI, ISAYAMA KATSUHIKO, YUKIMOTO SADAO, HIROSE, TOSHIFUMI, ISAYAMA, KATSUHIKO, YUKIMOTO, SADAO
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1989
Main classification: C08L71
IPC codes: C08L83, C08L67, C08K5, C08L63, C08L33, C08L91, C08J7, C08L47, C08L71