TREATMENT FOR INHIBITING IRRADIATION INDUCED STRESS CORROSION CRACKING IN AUSTENITIC STAINLESS STEEL

Abstract: A heat treatment method for inhibiting irradiation induced stress corrosion cracking in stainless steel and related nickel-chromium alloys. The steel or alloy is heat treated at a temperature in the range of 2050°F (1121°C) up to about 2400°F (1316°C) for a period inversely in the range of 1 minute up to about 45 minutes.

Description: This invention relates to austenitic stainless steel which is employed in environments of high irradiation such as in the interior of a nuclear fission reactor. The invention is concerned with the failure of stainless steel and other alloys commonly utilized within and about nuclear reactors due to the occurrence of stress corrosion cracking resulting mainly from their exposure to high levels of irradiation. Stainless steel alloys of high chromium-nickel type are commonly used for components employed in nuclear fission reactors due to their well known high resistance to corrosive and other aggressive conditions. For example, nuclear fuel assemblies, neutron absorbing control devices, and neutron source holders are frequently clad or contained within a sheath or housing of stainless steel of Type 304, or similar alloy compositions. Frequently such components, including those mentioned, are located in and about the core of fissionable fuel of a nuclear reactor where the extremely aggressive conditions such as high radiation and temperatures are the most rigorous and debilitating. Commercial solution or mill annealed stainless steel alloys are generally considered to be essentially immune to intergranular stress corrosion cracking, among other sources of deterioration and in turn failure. However, stainless steels have been found to degrade and fail due to intergranular stress corrosion cracking following exposure to high irradiation such as is typically encountered in service within and about the fissionable fuel core of water cooled nuclear fission reactors. Such irradiation related intergranular stress corrosion cracking failures have occurred notwithstanding the stainless steel alloy having been in the so-called solution or mill annealed condition; namely having been treated by heating up to within a temperature range of about 1,850 to 2,050°F, then rapidly cooled as a means of solutionizing carbides and then deterring their nucleation and precipitation from solution out into grain boundaries. It is theorized that high levels of irradiation resulting from a concentrated field or extensive exposure, or both, are a significantly contributing cause of such degradation of stainless steel alloys, due among other possible factors to the irradiation promoting segregation of the impurity contents of the alloy. Past efforts to mitigate irradiated related intergranular stress corrosion cracking in stainless steel alloys comprise the development of resistant alloy compositions. For example, stainless steels containing low levels of impurities have been proposed. US-A-4512820 discloses a method for reducing stress, corrosion cracking attributable to irradiation in nuclear reactors in austenitic alloys containing chromium and nickel, such as Inconel, in which the alloy is subjected to hot plastic working, solution heat treatment at a temperature in the range 1000°C-1250°C for 15 to 60 minutes followed by aging at a temperature in the range 650°C-750°C for 20 hours. This invention comprises a method of treating austenitic stainless steel alloy compositions of the high chromium-nickel type and items or devices constructed thereof, which inhibits the possible future occurrence of stress corrosion cracking therein resulting from high levels of and/or prolonged exposure to irradiation. The preventative treatment comprises a specific thermal treatment procedure, or enhanced solution annealing step, which imparts to such alloys a high degree of resistance to stress corrosion cracking although subjected to concentrated irradiation. The invention provides a method of inhibiting stress corrosion cracking attributable mainly to exposure to concentrated irradiation in austenitic stainless steel comprising heat treating a stainless steel alloy consisting of in percentage by weight : Chromium 18 to 20 Nickel 8 to 14 Carbon 0.08 maximum Manganese 2.0 maximum Silicon 1.0 maximum Molybdenum 3.0 maximum Iron and incidental impurities Balance by maintaining the mass of the alloy at a temperature within the range from above 1121°C (2050°F) up to about 1316°C (2400°F) for a period of at least 1 minute up to about 45 minutes with the period of heat treatment of the alloy being approximately inversely proportional to the temperature of the treatment. Preferably the stainless steel consists of an alloy comprising in percentage by weight : Chromium 18 to 20 Nickel 8 to 12 Carbon 0.08 maximum Manganese 2.0 maximum Silicon 1.0 maximum Iron and incidental impurities Balance There are disclosed herein: a means of inhibiting the occurrence of stress corrosion cracking in austenitic stainless steel, and articles formed therefrom, which is attributable to exposure to irradiation; an effective and feasible treatment for imparting resistance to irradiation promoted stress corrosion cracking in austenitic stainless steel alloys and products produced therefrom, which are subjected to concentrated irradiation; an economical and practical method for inhibiting the failure of austenitic stainless steel components for service in nuclear reactors and other manufactured articles of stainless steel subjected to high irradiation due to stress corrosion cracking; an effective method for dealing with the problem of stress corrosion cracking in austenitic stainless steel alloys following exposure to irradiation that does not entail any adverse effects upon the alloy or products therefrom. In the accompanying drawings: Figure 1 of the drawing comprises a graph showing the various stress corrosion susceptibilities of stainless steel in relation to temperatures and time periods thereof of differing levels of heat treatments; Figure 2 of the drawing comprises a bar graph showing the relative elongation of stainless steel subjected to the heat treatment of the invention; and Figure 3 of the drawing comprises a bar graph showing the relative maximum stress attained in stress corrosion tests of stainless steel subjected to the heat treatment of this invention. This invention is especially useful for structural units and articles, or components thereof, which are manufactured from, or include austenitic stainless steel such as Type 304, and are designated for service in the radioactive environment of a nuclear fission reactor or other radiation related devices or environments. In one aspect it is directed to a preventative measure for impeding the occurrence of radiation induced degradation of austenitic stainless steel which employed in such service, including single phase austenitic stainless steels. The invention is specifically directed to a potential deficiency of susceptibility to irradiation degradation which may be encountered with chromium-nickel austenitic stainless steels comprising both commercial purity and high purity Type 304. Commercial Type 304 stainless steel alloy is specified in Tables 5-4 on pages 5-12 and 5-13 of the 1958 edition of the Engineering Materials Handbook , edited by C. L. Mantell. Typically, such an alloy comprises about 18 to 20 percent weight of chromium and about 8 to 14 percent weight of nickel, with up to a maximum of percent weight of 0.08 carbon, 2.0 manganese, 1.0 silicon and 3.0 molybdenum, and the balance iron with some insignificant amounts of incidental impurities. Components such as fuel and absorber rod containers, neutron source retainers comprising austenitic stainless steel alloys of the foregoing type, which are employed in the fuel core of nuclear fission reactors, occasionally fail due to a phenomenon referred to as "irradiation-assisted stress corrosion cracking." This type of deterioration is a unique form of stress corrosion cracking which can occur although the stainless steel alloy has been solution or mill annealed. Stainless steels which have been subjected to the conventional solution or mill annealing temperatures of 1010 to 1121°C (1850 to 2050°F) are considered in the industry to be immune to the occurrence of intergranular stress corrosion cracking. However, when such treated stainless steel alloys are subjected to high levels of radiation such as typically encountered within and about the fuel core of a nuclear reactor, the high irradiation field performs some complex role in assisting the occurrence of intergranular stress corrosion cracking. It has been theorized that a possible mechanism or cause of such a phenomenon is that the irradiation promotes the segregation of impurities within the alloy, such as phosphorus, sulfur, silicon and nitrogen, to its grain boundaries. This invention comprises a preventative heat treatment of specified conditions of temperature and time of exposure thereto which markedly diminishes the commonly manifested adverse influence or role of irradiation upon austenitic stainless steel alloys, and its deleterious effects in contributing to the occurrence of intergranular stress corrosion cracking of such alloys. The method of this invention comprises the specific step of subjecting the austenitic stainless steel alloy to a temperature of from above 2050°F (1121°C) up to about 2400°F (1316°C) over a period of at least one minute up to about 45 minutes. The period of time for maintaining such temperatures should be approximately inversely proportional to the temperature within the range. For example, relatively longer periods of time should be used with temperatures in the lower region of the given range, and conversely, shorter periods are suitable for the temperatures in the higher region of the range of conditions for effective practice of the invention. Preferably, the method of deterring the occurrence of irradiation assisted stress corrosion cracking comprises maintaining the austenitic stainless steel alloy at a temperature within the approximate optimum range of 2200 to 2400°F for a relatively brief period of about 5 minutes to about 20 minutes. As will be apparent from the examples, the allowable period of exposure to the temperature conditions is typically briefer to achieve effective corrosion residence for the commercially pure grade of Type 304 stainless steel than for the high purity grade of the same alloy. The specific temperature and time conditions of the treatment method of this invention effectively inhibit irradiation assisted stress corrosion cracking as well as the common intergranular stress corrosion cracking attributed to sensitization. The mitigating effect of the temperature/time for the solution annealing treatment of the invention appear to be the result of more effective desorption of alloy grain boundary impurities. The following evaluating tests serve as specific examples for the practice of this invention as well as demonstrating the markedly inhibiting effects of the invention in decreasing the occurrence of intergranular stress corrosion cracking in austenitic stainless steel alloys which is attributable to high irradiation exposure. Compositions of the stainless steel alloys evaluated for stress corrosion were as shown in Table 1 with the balance being iron. The stainless steel alloy test specimens were each prepared for evaluation by first subjecting each to a solution annealing heat treatment as specified hereinafter, including conditions within the scope of this invention and beyond, then all were irradiated in a nuclear reactor to a range of fast neutron fluences from 2.22 x 10²¹ n/cm² to 3.08 x 10²¹ n/cm² (E>1MeV), at a temperature of 550°F (290°C). The extent of intergranular stress corrosion observed with a scanning electron microscope on the fractured surface of the irradiated test specimens was used as a measure of the irradiation assisted stress corrosion cracking phenomenon. The temperature and times applied of the heat treatment conditions of the test specimens are given in the following Table 3: The stress corrosion test results of the test specimens, in relation to the temperatures and times applied in the heat treatments, are shown in the graph of Figure 1. It is apparent from the data of Figure 1 that the irradiation assisted stress corrosion cracking (as measured by percent intergranular stress corrosion cracking) can be reduced from about 90 percent cracking in commercial purity, mill annealed Type 304 stainless steel down to about 0 percent cracking by subjecting the alloy to a temperature of 1204°C (2200°F) for about 20 minutes, or to a temperature of 1260°C (2300°F) for about 5 minutes, or a temperature of 1316°C (2400°F) for about 1 minute. Moreover, irradiation assisted stress corrosion cracking can be reduced from about 50 percent cracking in high purity, mill annealed Type 304 stainless steel to about 0 percent cracking by subjecting the alloy to a temperature of 1204°C (2200°F) for about 45 minutes. It is noteworthy that, as shown in Figure 1, there are clear maximum heating times for effective treatment; for instance, longer heating times than one minute at 1316°C (2400°F) for commercial purity Type 304 stainless steel does not fully eliminate irradiation assisted stress corrosion cracking. Rather corrosion cracking appears to increase with increasing periods of heating, whereby about one minute is an approximate maximum heating period at 1316°C (2400°F) for commercial purity Type 304 stainless steel. The temperature and time solution annealing conditions of this invention not only eliminate irradiation assisted stress corrosion cracking in austenitic stainless steels, but they also appear to enhance the mechanical properties of such alloys when irradiated. For instance, Figure 2 of the drawing shows the elongation of commercial purity Type 304 stainless steel subjected to stress corrosion tests increases to peak values in the range from 13 to 16 percent compared to about 0.6 percent for mill annealed, commercial purity Type 304 stainless steel when both are irradiated to a similar fluence. The enhanced ductility resulting from the temperature/time solution annealing would be of significant benefit to designers of components of stainless steel subjected to irradiation since the lower limit of total elongation at 288°C (550°F) and fluences >6 x 10²⁰ n/cm² that is currently used by designers based upon test results from irradiated mill annealed stainless steel is 1.1 percent. Similarly, it is shown in Figure 3 that the maximum stress (or ultimate tensile strength) attained in the stress corrosion tests increases to peak values ranging from 697 to 807 MPa (101 to 117 ksi), compared to 310 MPa (45 ksi) for irradiated, mill annealed, commercial purity Type 304 stainless steel.

Claims: A method of inhibiting stress corrosion cracking attributable mainly to exposure to concentrated irradiation in austenitic stainless steel comprising heat treating a stainless steel alloy consisting of in percentage by weight : Chromium 18 to 20 Nickel 8 to 14 Carbon 0.08 maximum Manganese 2.0 maximum Silicon 1.0 maximum Molybdenum 3.0 maximum Iron and incidental impurities Balance by maintaining the mass of the alloy at a temperature within the range from above 1121°C (2050°F) up to about 1316°C (2400°F) for a period of at least 1 minute up to about 45 minutes with the period of heat treatment of the alloy being approximately inversely proportional to the temperature of the treatment. The method of inhibiting stress corrosion cracking in austenitic stainless steel of claim 1, wherein the heat treatment comprises maintaining the mass of austenitic stainless steel within the range of about 1204°C (2200°F) to about 1316°F (2400°F) for a period of about 1 minute up to about 20 minutes. The method of inhibiting stress corrosion cracking in austenitic stainless steel of claim 1 or 2, wherein the stainless steel comprises Type 304. The method of inhibiting stress corrosion cracking in austenitic stainless steel of claim 1, 2 or 3, wherein the stainless steel consists of an alloy comprising in percentage by weight : Chromium 18 to 20 Nickel 8 to 12 Carbon 0.08 maximum Manganese 2.0 maximum Silicon 1.0 maximum Iron and incidental impurities Balance The method of inhibiting stress corrosion cracking in austenitic stainless steel of any one of claims 1 to 4, wherein the heat treatment comprises maintaining the mass of single phase, austenitic stainless steel at a temperature of approximately 1260°C (2300°F) for a period of approximately 1 to 20 minutes.

Inventors: GORDON, GERALD MYRON, JACOBS, ALVIN JOSEPH
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1989
Main classification: C21D6
IPC codes: C21D1, C21D6