SEGMENTED POLYETHER POLYURETHANE

Abstract: A hydrophilic, segmented polyether polyurethane-urea that exhibits an increase in tensile strength and elongation when wet with water and is capable of forming visually clear films permeable to water vapor is disclosed.

Description: This invention relates to a segmented polyether polyurethane-urea according the first part of the main claim. Segmented polyurethanes are prepared from hydroxyl terminated low molecular weight polyethers or polyesters or mixtures thereof by reacting these materials with a stoichiometric excess of a diisocyanate to produce an isocyanate terminated prepolymer. This reactive prepolymer is then chain extended with a difunctional compound containing an active hydrogen such as water, glycols, aminoalcohols or diamines. Diamine-extended polyurethanes have a relatively high urea linkage content due to their diamine extension. This high urea linkage content results in relatively high levels of hydrogen bonding which, in turn, produces strong elastic materials with good flex life properties. However, this high level of hydrogen bonding renders the polyurethane non-thermoplastic. This non-thermoplastic nature severely restricts the processes which may be utilized to fabricate these polyurethanes into useful devices. Techniques such as extrusion, injection molding and heat sealing cannot be utilized due to the polyurethanes' inability to melt and flow prior to decomposition. Segmented polyurethanes have also been synthesized utilizing relatively low molecular weight diols as chain extension agents. The use of diols produces a segmented polyurethane having reduced levels of hydrogen bonding. As a result of this reduction in hydrogen bonding, these particular polyurethanes have reduced physical properties such as elongation, ultimate tensile strength and flex life as compared to their equivalent diamine extended counterparts. However, this relatively lower level of hydrogen bonding renders the polyurethane thermoplastic and allows it to be extruded, injection molded, heat sealed, etc. It is known that the mechanical properties and predominately the elastic properties of linear segmented polyurethane block copolymers arise from a two phase microstructure. This two phase structure is derived from the individual chain structure of the polyurethane. Segmented polyurethane polymer chains may be considered as a series of alternating "soft" and "hard" blocks. Typically, the "soft" blocks are diisocyanate-coupled relatively low melting point polyester or polyether polymers of relatively low molecular weight. The "hard" blocks include single diurethane linkages resulting when a diisocyanate molecule couples two polyester or polyether molecules. More particularly, they are the relatively higher melting urethane or urea chain segments formed by the reaction of diisocyanate with a glycol and/or a diamine chain extender. The polar nature of the recurring rigid "hard" urethane/urea chain segments results in their strong mutual attraction. This attraction (both inter- and intra-molecular) leads to aggregation and ordering into crystalline and paracrystalline domains (also called pseudo crystalline domains) in a mobile polymer matrix. The high level of urethane and urea hydrogen atoms together with carbonyl and ether oxygen groups permits extensive hydrogen bonding in these systems. The level of this hydrogen bonding restricts the mobility of chain segments to organize extensively into crystalline lattices. The result is a polymer system in which there are at least three levels of association. Portions of "hard" blocks form discernible crystalline domains while portions of the "soft" blocks form the basis for an amorphous polymer matrix. There is, however, at least a third "phase" which is formed from the complex interaction of paracrystallinity and hydrogen bonding. This leads to the formation of what has been described as "pseudo crosslinks". That is, primary polyurethane chains are crosslinked in effect, but not in fact. The overall consequence is the formation of a labile network of polymer chains which display many of the mechanical, chemical and physical properties of truly crosslinked networks. This type of "pseudo crosslinking" may be partially reversed or enhanced by heat and solvation. Extrudable, water-extended polytetramethylene ether polyurethane-urea resins are described in U.S. Patent No. 4,062,834 to Gilding et al. The described resins have been rendered extrudable by a reduction and rearrangement of the hydrogen bonds in the polymer chain. This is accomplished by reacting the isocyanate terminated prepolymer with water to form an unstable carbamate which in turn decomposes to form an amine and carbon dioxide. The so formed amine terminated prepolymer is then reacted with another molecule of isocyanate terminated prepolymer. The polyurethanes thus produced prove to be thermoplastic; however, the physical properties such as elongation, ultimate tensile strength and flex life are inferior. U.S. Patent No. 3,635,907 to Schulze, et al. discloses a polyurethane wherein a mixture of chain extenders such as diamines, hydrazine, or hydrazine derivatives, and aminoalcohols is utilized for chain extension, followed by further addition of a diisocyanate and a diol. The ultimate tensile strength of the polyurethane is varied by varying the quantity of diisocyanate added (column 4, lines 8-11). The reaction between the chain extenders and the NCO-groups of the prepolymer is terminated by the addition of aliphatic alcohols (column 1, lines 70-72). Films produced from polyurethanes derived from linear polyesters admixed with relatively low molecular weight aliphatic diols are said to be non-porous and impermeable to water vapor (column 2, lines 27-28). A segmented polyether polyurethane-urea according the first part of claim 1 is known from DE-A-36 06 440 and WO-A-85 05 322. It is the object of the present invention to provide segmented polyether polyurethane-urea resins which have superior physical properties such as an increase in strength when wet with water, elongation, ultimate tensile strength, and flex life. This object is solved by a segmented polyether polyurethane-urea with the features of the claim 1. Some of the present resins may be readily extruded, injection molded and heat sealed, and can be made into visually clear films that are hydrophilic and are permeable to water vapor. Such films are eminently well suited for the fabrication of wound dressings. The present invention contemplates a hydrophilic, segmented polyether polyurethane-urea that exhibits an increase in tensile strength and elongation when wet with water, and that is capable of forming a visually clear film. In addition, films embodying this invention exhibit a moisture vapor transport rate several orders of magnitude higher than that of silicone-derived films. This polyurethane-urea is a reaction product of a diisocyanate-polyalkylene ether glycol mixture prepolymer chain extended with a difunctional amine chain extender such as an aliphatic diamine and/or an alkanolamine. More particularly, segmented polyurethane-urea resins of the present invention are derived from a prepolymer formed from a diisocyanate reacted with a certain mixture of polyalkylene ether glycols to form an isocyanate-terminated prepolymer. The polyalkylene ether glycols selected for the mixture have repeating alkyleneoxy segments of unequal lengths. That is, a polyalkylene ether glycol having relatively longer alkyleneoxy segments is mixed with at least one other polyalkylene ether glycol having relatively shorter alkyleneoxy segments. This prepolymer is then chain extended to a desired, relatively higher, number average molecular weight, usually in the range of about 20,000 to about 260,000, by reaction with an admixture of at least one difunctional chain extender, such as an aliphatic diamine, and preferably admixed with at least one chain control agent such as a monofunctional amine. Optionally, a polymeric wetting agent such as polyvinylpyrrolidone or the like is also present. Control of the hydrophilicity of the present polyurethane-urea resins can be done intrinsically by selecting a desired mixture of polyalkylene ether glycols and by adjusting the ratio of these polyalkylene ether glycols as the prepolymer of the resin is made. Hydrophilicity of the resin can also be controlled extrinsically by incorporation into the prepared resin of a hydrophilic polymer that is soluble in the segmented polyurethane resin, e.g., polyvinylpyrrolidone. As the degree of hydrophilicity is varied, the rate of moisture transport and vapor permeability through the present polyurethanes are also varied. The present polyurethane-urea resins can be processed into porous films or membranes, if desired, in accordance with practices taught in U.S. Patent No. 4,704,130 to Gilding et al. Such porous films have utility as membranes for various separation processes, for wound dressings, and the like. Numerous other advantages and features of the present invention will become readily apparent from the following detailed description of invention, the accompanying examples and the appended claims. Brief Description of Drawings In the drawings, FIGURES 1 through 15 are graphical representations showing constant dry tensile strength - wet tensile strength differential contours (expressed in kilograms per square millimeter) derived from a multiple regression model of experimental data. In FIGURES 1, 3, 5, 7, 9, 11, 13 and 15 all variables except the coordinate variables were held at their mean experimental values, and in FIGURES 2, 4, 6, 8, 10, 12 and 14 all variables except the coordinate variables were held at about their optimum values. The mean experimental values were as follows: mole percent polyethylene glycol (PEG) 49.026 molecular weight of PEG 1426 molecular weight of polytetramethylene glycol (PTMEG) 1268.2 extension 23.776 mole fraction ethylene diamine (EDA) 0.49026 The optimum values were as follows: mole percent PEG 25 molecular weight of PEG 2000 molecular weight of PTMEG 2000 extension 40 mole fraction of EDA 0.5 In the present polyurethane-ureas the level of "pseudo crosslinking" and general phase separation present can be adjusted in a controllable, predictable fashion. This enables the physical and mechanical properties to be tailored to specific requirements. The modification of these materials has been accomplished by controlling the following parameters. The "soft" block of the resins of the present invention is ideally a relatively low melting point polyether of low molecular weight. The "hard" block is ideally formed from the diurethane linkages resulting from the reaction of two polyether molecules and the urethane/urea segments formed from the reaction of diisocyanate and/or an alkanolamine and a diamine. The stoichiometry of the polyurethane-ureas of the present invention is such that the "soft" blocks are of relatively greater block length than the corresponding "hard" blocks. In fact, the "hard" blocks can be better characterized as "hard" units as they are present in limited numbers and are of relatively short block length. This situation ensures that little true crystallization of the "hard" block can take place. Crystallization of the "soft" block is possible, but produces less rigid crystallites than those potentially formed from the "hard" blocks. The stoichiometry of the diamines and alkanolamines used in the chain extension of these polyurethane-ureas allows adjustment of the degree and distribution of hydrogen bonding in the produced polymers. The polyurethane-ureas of the present invention, while encompassing traditional theories, depart, however, from the currently held views regarding phase separation, hydrogen bonding, etc. This departure can be seen clearly in the current polyurethane-urea's mechanical properties after equilibration in a series of organic and aqueous solutions as will be described in greater detail hereinbelow. As previously described, conventional polyurethanes obtain their mechanical properties from "pseudo crosslinks". These crosslinks are considered to be a function of the level of hydrogen bonding between the various polar groups present in the polymer's structure. The placement of these polar groups and, therefore, hydrogen bonds is accepted as being predominately in the "hard" blocks of the polymer (i.e., associated wth the urethane and urea linkages). Contributions to the strength of the material from the "soft" block portions are considered negligible by conventional theories. It would be expected, therefore, that an equilibration with a liquid which disrupts hydrogen bonds (e.g., water) would reduce the polymer's mechanical strength and elongation. However, such a reduction in mechanical strength and elongation for polyurethane-ureas of the present invention is not observed when these polyurethane-ureas are equilibrated with water. In fact, the contrary is found to be the case. The polyurethane-ureas of the present invention increase in tensile strength and elongation when wet with water. While not wishing to be bound by a particular theory, it is believed that the polymers of the present invention behave as follows. Water, being a small, highly polar molecule, is known to participate in "bridging" reactions with various chemical groupings through its hydrogen atom. In the case of the polyurethanes of the present invention, the hydrogen atoms in the water molecules participate in a "bridging" reaction between oxygen atoms in the polyether "soft" block segments. The "soft" blocks are considered to be coiled and the hydrogen "bridging" takes place both between oxygen contained in adjacent loops of the mixed polyether coil and between oxygen present in other surrounding coils (either in the same polymer chain or a second chain). The "bridging" increases the strength of the respective chain which is observed as an increase in mechanical strength of the polymer. The observed increase in elongation is believed to be due to the changing balance of the inter- to intra-molecular "bridging" that is present as the materials are placed under tensile stress. The stress also induces chain slippage which allows alignment and optimization of "bridging" and hydrogen bonding. When equilibrated with a liquid which is not capable of "bridging" (e.g., methanol) the polyurethane-ureas of the present invention do not show an increase in mechanical properties. As a matter of fact, decrease in tensile strength and elongation is observed as compared with dry samples of the same materials. The observed decrease is considered to be due to methanol's effect on the balance of "pseudo crosslinking" and "pseudo crystallinity". The present segmented polyurethane-urea resins are the reaction products of certain isocyanate-terminated prepolymers with certain amounts of chain extenders or chain extender mixtures. The aforementioned prepolymers, in turn, are the products of the reaction of a stoichiometric excess of a diisocyanate with an admixture of polyalkylene ether glycols having repeating alkyleneoxy groups of different size, i.e., the length of repeating alkylene units is different in each of the glycols. The preferred mol ratio of diisocyanate-to-polyalkylene ether glycol mixture is 3:2. The prepolymer contains no residual hydroxyl groups. Any of a wide variety of organic diisocyanates may be utilized for present purposes, including aromatic, aliphatic and cycloaliphatic diisocyanates and combinations thereof. Representative diisocyanates include toluene diisocyanate (TDI), diphenylmethylene diisocyanate (MDI), hexamethylene diisocyanate, cyclohexylene diisocyanate, methylene dicyclohexane diisocyanate, 2,2,4-trimethyl hexamethylene diisocyanate, isophorone diisocyanate, m-phenylene diisocyanate, 4-chloro-1,3-phenylene diisocyanate, 4,4'-biphenylene diisocyanate, 1,5-naphthylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,10-decamethylene diisocyanate and 1,4-cyclohexylene diisocyanate. The preferred diisocyanates are aromatic in nature, e.g., TDI, MDI, and the like. The polyalkylene ether glycols that constitute an admixture suitable for the present purposes are chosen so that the repeating alkyleneoxy segments in each of the glycols is of a different size. The polyalkylene ether glycol having the relatively shorter alkyleneoxy segments preferably has a number average molecular weight in the range of 1,000 to 3,000. The polyalkylene ether glycol having the relatively longer alkyleneoxy segments has a number average molecular weight of at least about 800, and the molecular weight can be as high as 4,000. Preferably the polyalkylene ether glycols that constitute the admixture have substantially the same number average molecular weight, more preferably a number average molecular weight of 2,000. It is also preferable that the polyalkylene ether glycol having the relatively shorter alkyleneoxy segments constitutes at least 10 mole percent of the admixture, and the polyalkylene ether glycol having the relatively longer alkyleneoxy segments constitutes a major portion of the admixture, i.e., more than 50 mole percent of the glycol admixture. Particularly preferred are polyalkylene ether glycol admixtures containing 25 mole percent of the glycol having the relatively shorter alkyleneoxy segments and 75 mole percent of the glycol having the relatively longer alkyleneoxy segments. For films suitable for use in wound dressings, the inventive combination of the polyalkylene ether glycol admixture is polytetramethylene glycol (PTMEG) having a number average molecular weight of 2,000 and polyethylene glycol (PEG) having a number average molecular weight of 2,000 in a mole ratio of 1:1 to 3:1, respectively, for an optimum degree of hydrophilicity in combination with a desired degree of hydrogen bonding in the produced film. The formation of the isocyanate terminated prepolymer occurs in a liquid state and at a temperature of 50 to 100°C., preferably at 80 to 85°C. The reaction time is 1 to 1-1/2 hours. Although it is preferred that this reaction take place in a melt, it may equally well be carried out in solution using a suitable solvent such as dimethylacetamide (DMAC), dimethylformamide (DMF), tetrahydrofuran (THF), or the like. The preferred solvent is DMAC. If the reaction takes place in the melt, the prepolymer is then dissolved in the aforementioned solvent. When dissolution is complete, the prepolymer is chain extended to the desired number average molecular weight, usually in the range of 20,000 to 260,000, using a difunctional chain extender, preferably an admixture of such chain extenders. In the chain extender admixture at least one chain extender is an aliphatic diamine and at least one other chain extender is an alkanolamine. Suitable aliphatic diamine chain extenders include ethylene diamine, m-xylylene diamine, propylene diamine, and the like. Suitable alkanolamine chain extenders include ethanolamine, and the like. Other chain extenders such as diols can also be present. A preferred combination of chain extenders is ethylene diamine with ethanolamine. The mol ratio of ethylene diamine to ethanolamine can be about 0.25:0.75 to about 0.75:0.25. A preferred monofunctional amine chain control agent includes at least one member of the group consisting of 3,3-dimethylbutylamine, dimethylcyclohexylamine, 1,5-dimethylhexylamine, and dimethylethylene diamine. The amount of the chain control agent is dependent on the amount of NCO-groups present in the prepolymer and the desired chain extension. In any particular case, sufficient chain control agent is added to react with the remaining NCO-groups present after the desired degree of chain extension has been achieved. The chain extender and chain control agent are dissolved in a suitable solvent such as DMAC, DMF, THF, etc. as mentioned hereinabove. The prepolymer is then reacted with the chain extender and chain control agent solution to obtain the desired chain extension of the prepolymer. This reaction is usually carried out at a temperature of 80 to 85°C. over a time period of 2 to 3-1/2 hours. A polyurethane-urea resin solution is thus produced. Optionally, the hydrophilicity of the polyurethane resin may be enhanced by the use of an extrinsic wetting agent such as polyvinylpyrrolidone or the like, which is added to the polymerized resin prior to film forming. The amount of polyvinylpyrrolidone utilized for this purpose is 1 to 50 percent by weight of the composition. The following examples illustrate typical preparations of polyurethane-ureas embodying the present invention. In these examples, the polyurethane-urea prepolymer was prepared in a suitable reactor vessel equipped with an agitator, a temperature sensor, a temperature control and a nitrogen source and bleed. The chain extenders and chain control agents were admixed in a separate mixing vessel and the resulting admixture was then added to the reactor vessel. EXAMPLE 1 Polytetramethylene glycol (M.W. 1000; 257.14 grams) and polyethylene glycol (M.W. 1000; 28.57 grams) were combined and melted at a temperature of 40 to 45°C. in the reactor under a nitrogen blanket. 4,4'-Diphenylmethane diisocyanate (117.86 grams) was added to the reactor under agitation. The resulting mixture was stirred, heated to a temperature of 60 to 65°C. and maintained within this temperature range for a time period of 1 to 1-1/2 hours to produce a molten prepolymer. Dry dimethylacetamide (DMAC; 857.59 grams) was then added to the molten prepolymer and the admixture was stirred until dissolution of the prepolymer was complete. This occurred in 15 to 30 minutes. Dry DMAC (350.0 grams), ethanolamine (4.68 grams), ethylene diamine (4.60 grams) and dimethylethylene diamine (0.88 grams) were combined in a separate vessel, mixed at room temperature, and then added rapidly to the prepolymer solution with vigorous agitation. Thereafter, the prepolymer solution containing these additives was maintained at a temperature of 80 to 85 °C. for a time period of 2 to 3-1/2 hours. The resultant polyurethane resin solution was colorless and viscous, and was cast into a visually clear film. EXAMPLE 2 Polytetramethylene glycol (M.W. 1000; 214.29 grams) and polyethylene glycol (M.W. 1000; 71.43 grams) were combined and melted at a temperature of 40 to 45°C. in the reactor under a nitrogen blanket. 4,4'-Diphenylmethane diisocyanate (117.86 grams) was added to the reactor under agitation. The resulting mixture was stirred, heated to a temperature of 60 to 65°C. and maintained within this temperature range for a time period of 1 to 1-1/2 hours. Dry dimethylacetamide (DMAC; 857.59 grams) was then added to the molten prepolymer and the admixture was stirred until dissolution of the prepolymer was complete. This occurred in 15 to 30 minutes. Dry DMAC (350.0 grams), ethanolamine (4.86 grams), ethylene diamine (4.77 grams) and dimethylethylene diamine (0.92 grams) were combined together in a separate vessel, mixed at room temperature, and then added rapidly to the prepolymer solution with vigorous agitation. Thereafter, the prepolymer solution containing the additives was maintained at a temperature of 80 to 85°C. for a time period of 2 to 3-1/2 hours. The resultant polyurethane resin solution was colorless and viscous, and was cast into a visually clear film. EXAMPLE 3 Polytetramethylene glycol (M.W. 1000; 142.86 grams) and polyethylene glycol (M.W. 1000; 142.86 grams) were combined and melted at a temperature of 40 to 45°C. in the reactor under a nitrogen blanket. 4,4'-Diphenylmethane diisocyanate (117.86 grams) was added to the reactor under agitation. The resulting mixture was stirred, heated to a temperature of 60 to 65°C. and maintained within this temperature range for a time period of 1 to 1-1/2 hours to produce a molten prepolymer. Dry dimethylacetamide (DMAC; 857.59 grams) was then added to the molten prepolymer and the admixture was stirred until dissolution of the prepolymer was complete. This occurred in 15 to 30 minutes. Dry DMAC (350.0 grams), ethanolamine (4.47 grams), ethylene diamine (4.49 grams) and dimethylethylene diamine (0.84 grams) were combined together in a separate vessel, mixed at room temperature, and then added rapidly to the prepolymer solution with vigorous agitation. Thereafter, the prepolymer solution containing these additives was maintained at a temperature of 80 to 85°C. for a time period of 2 to 3-1/2 hours. The resultant polyurethane resin solution was colorless and viscous, and was cast into a visually clear film. EXAMPLE 4 Polytetramethylene glycol (M.W. 1000; 71.43 grams) and polyethylene glycol (M.W. 1000; 214.29 grams) were combined and melted at approximately 40 to 45°C. in the reactor under a nitrogen blanket. 4,4'-Diphenylmethane diisocyanate (117.86 grams) was added to the reactor under agitation. The resulting mixture was stirred, heated to a temperature of 60 to 65°C. and maintained within this temperature range for a time period of 1 to 1-1/2 hours to produce a molten prepolymer. Dry dimethylacetamide (DMAC; 857.61 grams) was then added to the molten prepolymer and the admixture was stirred until dissolution of the prepolymer was complete. This occurred in 15 to 30 minutes. Dry DMAC (350.0 grams), ethanolamine (4.34 grams), ethylene diamine (4.27 grams) and dimethylethylene diamine (0.82 grams) were combined in a separate vessel, mixed at room temperature, and then added rapidly to the prepolymer solution with vigorous agitation. Thereafter, the prepolymer solution containing these additives was maintained at a temperature of 80 to 85°C. for a time period of 2 to 3-1/2 hours. The resultant polyurethane resin solution was colorless and viscous, and was cast into a visually clear film. In a manner similar to that of the foregoing examples, additional polyurethane-ureas embodying this invention were prepared and the physical properties thereof noted. The amounts of reactants used and the properties noted are set forth in the Tables hereinbelow. The polyurethane resins of the present invention are particularly well suited for the manufacture of components for wound dressings and closures inasmuch as the high level of hydrophilicity, and therefore the absorption capacity, inherent in these polymers are important properties in this regard. Environmental wound dressings rely upon being able to absorb wound exudate while maintaining a moist microenvironment at the wound site to obtain optimum healing. Wounds or injuries to the skin generate varying amounts of discharge fluid known as exudate. Modern wound care management techniques seek to maintain the moisture level at the wound site at a relatively high level. But, excessive build up of exudate is unacceptable. The present polyurethane resins can be tailored to have properties, when cast into films, so as to absorb excess exudate while maintaining a high level of moisture at the wound site. In addition, the chemical, physical and mechanical properties of the present polyurethanes allow their use in a wide variety of other applications. The material's wet strength properties and selective permeability towards water vapor and other gases are particularly significant in this regard. The present polymers may be coated onto textile substrates to provide breathability while retaining resistance to liquids, particularly water. In a similar fashion, selectively permeable films may be fabricated for use as containers for desiccants and other absorbent agents (e.g., crystalline aluminosilicates, silica gel, etc.). The use of these films in this application has the advantage of preventing particulate contamination of the article into which the desiccant package will be placed and reduction of efficiency due to nonspecific absorption. Films of these materials are also suitable for packaging. Their selective gaseous and moisture vapor transmission properties allow their application in the area of environmental packaging. These polymers are biocompatible and noncytotoxic which makes them ideal for medical and biological applications. These properties enable the present polymers to be used as substrates for the support, growth and attachment of biological materials. They are of particular utility in the area of cell growth substrates for mammalian cell culture. The attachment and growth of cells to structures manufactured from these polymers makes them ideal for use in bioreactor systems for large scale production of cell lines, etc. Immobilization of proteins, enzymes and other biologically active materials, while maintaining biological activity, allows the use of these polymers as active structures in biosensors and diagnostic test kits. Similarly, nonbiologically active catalysts may be incorporated in these polymers, thereby facilitating their use in numerous chemical and physical processes. Selective transport of chemical agents through polymer films fabricated from these polymers can be used in the areas of filtration, separation and purification of liquids and gases. These properties are also of use in the area of drug delivery over an extended time period where therapeutic agents are delivered from a reservoir across a polymer membrane into the physiological environment. It is also envisaged that these polymers may be used as specialty coatings to inhibit corrosion of metallic surfaces while facilitating selective gaseous transport. The present segmented polyether polyurethane resins are also useful for the fabrication of vascular grafts, ureters and other biocompatible elements.

Claims: A segmented polyether polyurethane-urea being the reaction product of prepolymer which is derived from a stoichiometric excess of a diisocyanate reacted with an admixture of polytetramethylene ether glycol (PTMEG) and polyethylene ether glycol (PEG) and which is extended with a difunctional amine chain extender, characterized in , that the chain extender is a mixture of ethylene diamine (EDA) and ethanolamine (EA) and that the amounts of the used reactants are as follows Mole% PEG Mole% PTEG Molecular PEG Weights PTEG CHAIN EXTENSION Mole EDA Fraction EA %NCO 25 75 600 1000 10 0.75 0.25 1.130 25 75 600 2000 20 0.25 0.75 0.720 25 75 600 2000 10 0.5 0.5 0.750 25 75 1000 1000 10 0.5 0.5 1.050 25 75 1000 2000 40 0.5 0.5 0.780 25 75 1000 2000 10 0.25 0.75 0.740 50 50 1000 650 10 0.5 0.5 1.190 50 50 1000 650 40 0.75 0.25 1.190 50 50 1000 1000 20 0.5 0.5 1.060 50 50 1000 1000 20 0.5 0.5 1.070 50 50 1000 1000 40 0.5 0.5 1.040 50 50 1000 2000 20 0.5 0.5 0.820 75 25 1000 650 20 0.75 0.25 1.120 75 25 1000 1000 20 0.5 0.5 0.980 75 25 1000 1000 40 0.25 0.75 1.090 75 25 1000 2000 10 0.5 0.5 0.910 75 25 1000 2000 20 0.25 0.75 0.790 75 25 1000 2000 40 0.75 0.25 0.930 whereby chain extension stands for the number of folds by which the prepolymer was chain extended. A segmented polyether polyurethane-urea according to claim 1, characterized in that the mole ratio of diisocyanate-to-polyalkylene etherglycol mixture is about 3:2. A segmented polyether polyurethane-urea according to claim 1 or 2, characterized in that 4, 4' diphenylmethane diisocyanate is used as diisocyanate.

Inventors: ASKILL, IAN N., REED, ANDREW M., WEBER, WILLIS W.
Applicants: POLYMEDICA INDUSTRIES, INC.
Application year: 1989
Main classification: C08G18
IPC codes: C08G18, C08J5, A61F13