Alloy for building up valve

Abstract: An alloy for building up a valve according to the present invention comprises: with respect to the total weight of the alloy taken as 100 %, 30 to 40 % by weight of chromium; 15 to 31 % by weight of nickel; 7 to 20 % by weight of molybdenum; 0.7 to 2.2 % by weight of carbon; 1.5 % or less by weight of silicon; and balance of iron and inevitable impurities. The alloy is superior in hardness at high temperatures, PbO resistance and PbO + PbSO₄ resistance. In addition, the alloy is suitable for powder buildup welding.

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to an alloy for building up valves of internal combustion engines, especially for building up exhaust valves of automobile engines. Description of the Prior Art Many conventional valves of internal combustion engines have been used after buildup welding the portions thereof to be abraded with various surface-hardening alloys. A cobalt-base alloy, consisting mainly of cobalt-chromium and added with small amounts of tungsten, molybdenum, carbon and so on, is often employed as a buildup alloy for exhaust valves of automobile engines since the cobalt-base alloy is superior in hardness at high temperatures and lead oxide corrosion resistance (hereinafter referred to PbO resistance). However, the cobalt-base alloy contains a large amount of expensive cobalt, and is a highly expensive material for buildup welding. Therefore a less expensive material which exhibits no less performance than that of the cobalt-base alloy has been required for buildup welding the exhaust valves of the automobile engines. Japanese Unexamined Patent Publication (KOKAI) No. 153872/1984 discloses an iron-chromium-nickel alloy for engine valves developed for solving the above mentioned problem. The iron-chromium-nickel alloy is employed for forming portions of the engine valve to be withstood against abrasion by buildup by casting or by building up with a welding rod. The iron-chromium-nickel alloy is added with tungsten and titanium for controlling and fining the growth of the crystal grains of the base metal. The iron-chromium-nickel is further added with manganese for deoxidizing and desulfurizing. The iron-chromium-nickel alloy is furthermore added with aluminum for improving the PbO resistance. However, the inventors of the present invention have investigated and discovered that the iron-chromium-nickel alloy is inferior in the PbO resistance. Further, instead of the buildup with the welding rod, a method for buildup with alloy powder has been drawing attention because of its operability, buildup efficiency and ease of automation. However, when the iron-chromium-nickel alloy is employed for the method for the buildup with alloy powder, the following drawbacks arise: i.e., a poor powder deposition rate, an uneven bead configuration, pin holes and plow holes in the buildup layer and oxide intrusions into the buildup layer. The above drawbacks are believed to be resulting from the titanium added for controlling and fining the growth of the crystal grains of the base metal and the aluminium for improving the PbO resistance. Further, Japanese Unexamined Patent Publication (KOKAI) No. 179891/1987 discloses a nickel-chromium-molybdenum alloy for buildup, although it is not so cheap as the abovementioned iron-chromium-nickel alloy. The nickel-chromium-molybdenum alloy is superior in hardness at high temperatures and the PbO resistance, and the buildup method with alloy powder can be conducted favorably. However, the inventors have investigated and found that the corrosion of the exhaust valves is caused not only by lead oxide but also by lead oxide containing lead sulfate. The inventors have discovered that the nickel-chromium-molybdenum alloy is inferior in corrosion resistance against lead oxide containing lead sulfate (hereinafter referred to as PbO + PbSO₄ resistance). SUMMARY OF THE INVENTION It is an object of the present invention to develop a buildup welding alloy applicable to the buildup welding and the buildup method with alloy powder, and the build-up welding alloy maintaining required hardness at high temperatures and having excellent PbO resistance and PbO + PbSO₄ resistance, thereby satisfying the requirements of valves of internal combustion engines, especially the severe requirements of valves of recent high performance automobile engines. An alloy for building up a valve according to the present invention comprises: with respect to the total weight of the alloy taken as 100%, 30 to 40% by weight of chromium; 15 to 31% by weight of nickel; 7 to 20% by weight of molybdenum; 0.7 to 2.2% by weight of carbon; 1.5% or less by weight of silicon; and balance of iron and inevitable impurities wherein the contents of manganese, aluminum and titanium contained in said inevitable impurities are 0.1% or less by weight, respectively, and said alloy being in the form of powders. It is a feature of the present invention that the buildup alloy contains 7% or more by weight of molybdenum, more preferably 10% or more by weight of molybdenum in an iron-chromium-nickel alloy. The alloy accordingly becomes superior in hardness at high temperatures, and both in PbO resistance and PbSO₄ resistance. Further, the alloy is also suitable for the powder buildup method since the alloy does not contain a large amount of titanium, aluminum and manganese which are undesirable for the components of the powder buildup alloy. The reasons for restricting the contents of the buildup alloy components of the present invention as above will be hereinafter explained. (Chromium) The chromium is solidified in the iron, nickel and molybdenum to form a primary crystal solid solution. The primary crystal solid solution constitutes the substrate of the alloy. A part of the chromium bonds with the carbon as well as the molybdenum to form composite carbide consisting mainly of chromium and molybdenum. In the alloy composition region of the present invention, the composite carbide forms eutectic with the solid solution, and is present in the eutectic. Namely, the chromium coexists with the carbon, and improves the hardness of the alloy. Further, the chromium contributes to improve the PbO resistance and the PbO + PbSO₄ resistance. The PbO resistance is improved by the formation of chromic oxide on the surface of the alloy, and the PbO + PbSO₄ resistance is improved by the formation of chromic sulfate and chromic oxide on the surface of the alloy, whereby the corrosion of the alloy has been prevented from propagating. The effect of the chromium addition becomes poor when the chromium content is less than 30 % by weight. When the chromium content exceeds 40 % by weight, the effect of the chromium addition has not been enhanced. In addition, the tenacity of the alloy tends to deteriorate when the chromium content exceeds 40 % by weight. The chromium content is accordingly restricted in the range of 30 to 40 % by weight. More preferably, the chromium content may be in the range of 33 to 38 % by weight. (Nickel) The nickel is solidified in the solid solution of the substrate to improve the tenacity of the alloy and maintain the hardness thereof at high temperatures. The relationship between the nickel content and the Vickers hardness is shown in Fig. 1. Further, the nickel coexists with the chromium to improve the PbO resistance. Namely, the chromic oxide film becomes finer and bonds more firmly on the alloy by the nickel. The relationship between the nickel content and the PbO resistance and the PbO + PbSO₄ resistance, namely the relationship between the nickel content and the corrosion loss is shown in Fig. 2. The PbO resistance improvement effect of the nickel addition becomes poor when the nickel content is 15 % or less by weight. When the nickel content exceeds 31 % or more by weight, the effect of the nickel addition cannot be expected to improve. On the contrary, a high nickel content tends to deteriorate the PbO + PbSO₄ resistance. This is because the nickel sulfate of a low melting point is generated on the surface of the alloy, and the corrosion of the alloy is facilitated. Hence, it is undesirable to add a large amount of nickel in the alloy. The nickel content is accordingly restricted in the range of 15 to 31 % by weight. More preferably, the nickel content is in the range of 17.0 to 27.5 % by weight. Much more preferably, the nickel content is in the range of 20.0 to 27.5 % by weight. (Molybdenum) The molybdenum is solidified in the solid solution of the substrate to improve the tenacity of the alloy as well as the strength of the alloy. Further, the molybdenum bonds with the carbon as well as the chromium and forms the composite carbide of the chromium and molybdenum to improve the hardness of the alloy at high temperatures. Furthermore, the molybdenum contributes greatly to the improvement of the PbO resistance, especially to the improvement of the PbO + PbSO₄ resistance. The molybdenum sulfate as well as the chromic oxide and chromic sulfate are formed on the surface of the alloy, whereby the corrosion of the alloy has been prevented from propagating. The alloy exhibits the most excellent PbO + PbSO₄ resistance when the molybdenum content is 10 % by weight. When the molybdenum content is less than 10 % by weight, the PbO + PbSO₄ resistance tends to deteriorate. A lower limitation of the molybdenum content lies at approximately 7 % by weight, though it depends on the nickel content. The PbO + PbSO₄ resistance deteriorates when the molybdenum content is less than 7 % by weight. It is also undesirable to add the molybdenum by more than 20 % by weight, since the alloy becomes too harder and the tenacity threreof deteriorates. The molybdenum content is accordingly restricted in the range of 7 to 20 % by weight. More preferably, the molybdenum content is in the range of 8 to 15 % by weight. Much more preferably, the molybdenum content is in the range of 10 to 15 % by weight. (Carbon) A part of the carbon is solidified in the solid solution consisting mainly of the iron-nickel as the substrate to increase the strength and hardness of the substrate, but most of the carbon forms the composite carbide consisting mainly of the chromium and molybdenum and forms eutectic composite carbide with the solid solution of the substrate. As a result, the carbon increases the hardness and abrasion resistance of the alloy, and decreases the melting point of the alloy. The effect of the carbon addition is poor when the carbon content is less than 0.7 % by weight. When the carbon content exceeds 2.2 % by weight, the composite carbide is formed too much, and hyper-eutectic appears to crystallize the primary crystal of the composite carbide consisting mainly of the chromium and molybdenum. Consequently, it is undesirable to add the carbon by more than 2.2 % by weight, since the tenacity of the alloy deteriorates. The carbon content is accordingly restricted in the range of 0.7 to 2.2 % by weight. More preferably, the carbon content is in the range of 1.2 to 2.0 % by weight. (Silicon) Silicon is usually added as a deoxidizer. In the alloy of the present invention, however, when the silicon is added by more than 1.5 % by weight, the tenacity of the alloy deteriorates. This is because an eutectic structure of a low melting point is formed between the solid solution of the substrate, consisting mainly of iron-nickel, and molybdenum silicide. The silicon content is accordingly restricted to 1.5 % or less by weight. More preferably, the silicon content is in the range of 0.4 to 1.2 % by weight. (Inevitable impurities) The alloy of the present invention can be employed for the powder buildup. In this case, however, there arises concerns on the characteristics of the powder buildup alloy; i.e., the deposition rate during the powder buildup, the bead configuration, the defects in the buildup layer and the like. The inventors of the present invention have investigated various inevitable impurities contained in the alloy of the present invention, and have discovered that it is preferable to keep the {O} content, resulting from the surface oxidation of the powder and the like, to 0.2 % or less by weight. The inventers have also discovered that it is preferable to keep the contents of manganese, aluminium, and titanium, which work as deoxidizer, to 0.1 % or less by weight, respectively. When the {O} content is more than 0.2 % by weight, and when the contents of the manganese, aluminium and titanium are more than 0.1 % by weight, respectively, the bead configuration becomes uneven, and defects may occur in the buildup layer. Further, the protective film of the chromium oxide, formed on the surface of the alloy and contributing to the PbO resistance, is affected when active metals such as the manganese, aluminium and titanium are contained more than 0.1 % by weight in the alloy. In this case, the protective film of the chromium oxide turns into a protective film thereof containing the oxides of manganese, aluminium and titanium. The protective film becomes inferior in the finess and adhesion to the alloy. The PbO resistance of the alloy thus deteriorates since the protective film does not exhibit the sufficient protection effect. It is accordingly preferable to restrict the contents of the manganese, aluminium and titanium, contained as inevitable impurities in the alloy, to 0.1 % or less by weight to obtain the alloy having superior PbO resistance and suitable for the powder buildup. As described above, the alloy for building up a valve of the present invention is less expensive, and is superior in the hardness at high temperatures, the PbO resistance and the PbO + PbSO₄ resistance. Further, the alloy is suitable for the powder buildup. When an exhaust valve is made by the powder buildup employing the alloy of the present invention, the exhaust valve endures the severe operation condition of the high performance automobile engine. BRIEF DESCRIPTION OF THE DRAWINGS The above and other objects, features and advantages of this invention will become fully apparent from the following description taken in conjunction with the accompanying drawings, in which; Fig. 1 is a graph showing the relationship between the nickel content and the Vickers hardness at 700 °C; and Fig. 2 is a graph showing the relationship between the nickel content and the corrosion losses in PbO resistance test and PbO + PbSO₄ resistance test. DESCRIPTION OF THE PREFERRED EMBODIMENTS Having generally described this invention, a further understanding can be obtained by reference to certain specific preferred embodiments which are provided herein for purposes of illustration only and are not intended to be limiting unless otherewise specified. The hardness at an ordinary temperature, the hardness at a high temperature, the PbO resistance, the PbO + PbSO₄ resistance and the powder buildup characteristic were examined to evaluate the alloys of preferred embodiments and comparative examples. The alloys of the preferred embodiments and comparative examples were prepared by mixing and melting the components in the compositions shown in Tables 1 and 2 in the ordinary manner. The results of the test concerning the preferred embodiments and comparative examples are shown in Table 1 and Table 2, respectively. The data of the preferred embodiment alloy Nos. 3, 5, 6, 16, and 17, and comparative example alloy Nos. 4 and 5 in the hardness test at high temperature, the PbO resistance test, and the PbO + PbSO₄ resistance test, set forth in Tables 1 and 2, are plotted in Figs. 1 and 2, respectively, to explain the relationship between the nickel content and the hardness at high temperature, and the relationship between the nickel content and the PbO resistance and the PbO + PbSO₄ resistance, respectively. The methods for measuring and examining the above characteristics will be described hereinafter. (1) Hardness test at an ordinary temperature The alloys of the preferred embodiments and comparative examples were melted in an electric furnace in argon gas atmosphere, and molded in a mold made of graphite. The mold had a cavity having an inside diameter of 15 mm and a chiller at the bottom thereof. The molded bodies were cut into 15 mm ⊘ x 10 mm to obtain test pieces. The hardness was measured at a chilled portion of the test piece, namely the portion contacted with the chiller, by using a Vickers hardness tester (load: 20 kgf). (2) Hardness test at a high temperature The same test pieces obtained for the above hardness test at the ordinary temperature were employed to measure Vickers hardness at 700°C using a Vickers hardness tester for a high temperature application (load: 5 kgf). (3) PbO resistance test The alloys of the preferred embodiments and comparative examples were melted in an electric furnace in argon gas atmosphere, and molded in a glass tube by suction. The glass tube had an inside diameter of 5 mm ⊘. The molded bodies were cut into 5 mm ⊘ x 20 mm to obtain test pieces. The test pieces were immersed into 30 g of PbO heated at 920°C for an hour to measure the corrosion loss. (4) PbO + PbSO resistance test The same test pieces obtained for the above PbO resistance test were also employed in this test. The test pieces were immersed into a mixture of PbO and PbSO₄ heated at 900 °C for one hour to measure the corrosion loss. The mixture weighed 30 g, and consisted of 60 % by weight of PbO and 40 % by weight of PbSO₄. (5) Powder buildup test The alloys of the preferred embodiments and comparative examples were powdered by an ordinary gas atomizing. The powders of 80 to 350 mesh JIS Z 8801-1966, equivalent to aperture size of 177-44 µm were built up on a base metal of austenite heat resistance steel "SUH35" (Japanese Industrial Standards) by using a plasma powder buildup apparatus in the conditions shown in Table 3. The base metal size was 50 mm in width x 100 mm in length x 10 mm in thickness. The wettability and the bead configuration were measured to evaluate the powder building up character. Shielding gas discharge 30 ℓ/min Plasma gas discharge 4 ℓ/min Welding current 130 A Welding speed 65mm/min Powder supply 30g/min (6) Durability test using an actual engine and its results Sample No. 3 of the preferred embodiment and sample No. 1 of the comparative example were powdered by the ordinary gas atomizing. The powders of 80 to 350 meshes were built up on a valve preform of the austenite heat resistance steel "SUH35" in a condition shown in Table 4. The valve preform had a valve head having a diameter of 43 mm ⊘. After the buildup, the valve preforms built-up with the alloys of sample No. 3 of the preferred embodiment and sample No. 1 of the comparative example were finished to a predetermined shape of predetermined diameters. The valves were thus molded. The {O} content was 750 ppm in the alloy powders of sample No. 3 of the preferred embodiment. Shielding gas discharge 40 ℓ/min Plasma gas discharge 4 ℓ/min Welding current 120 A Welding speed 300mm/min Powder supply 10g/min A 2.5 liter in-line 6-cylindered gasoline engine was prepared, and the valves built-up with the alloys of sample No. 3 of the preferred embodiments and sample No. 1 of the comparative examples were mounted on the first to third cylinders of the engine and the fourth to sixth cylinders thereof, respectively. Then, a durability test using the actual engine was conducted in the conditions shown in Table 5. Engine speed 4200 rpm Engine load Full Cooling water temp. 90 °C Lubricating oil temp. 120 °C Fuel Leaded gasoline Duration 300 hours The corrosion losses of the faces of the valves built-up with sample No. 3 of the preferred embodiment and sample No. 1 of the comparative example were 8 to 12 µm and 10 to 21 µm, respectively. The depths of the corrosion in the faces of the valves were 2.5 µm and 23 µm, respectively. (Evaluation) As shown in Table 1, the alloys of the preferred embodiments were superior in hardness at the high temperature. Namely, the Vickers hardness at the ordinary temperature was from Hv 390 to Hv 590, and the Vickers hardness at 700°C was Hv 300 or more for all of the alloys of the preferred embodiments. Further, the alloys of the preferred embodiments were superior in the corrosion resistance. Namely, the corrosion losses when immersed into the PbO heated at 920°C and the corrosion losses when immersed into the mixture of 60 % by weight of PbO and 40 % by weight of PbSO₄ heated at 900°C were 100 mg/cm² per hour or less in both cases. Furthermore, there arose no problems on the buildup operability when the powdered alloys of the preferred embodiments were built-up on the valve preforms. The deposition rates were 90 % or more, and there were no defects in the buildup layers. Moreover, the engine valves built-up with the powdered alloys of the preferred embodiments were superior in the abrasion resistance, the PbO resistance and the PbSO₄ resistance, and had performance sufficiently satisfying the severe operation conditions of the high performance automobile engine. On the other hand, as shown in Table 2, when neither one of the component elements fell in the limiting ranges of the present invention, at least one of the abovementioned characteristics; i.e., the hardness at the high temperature, the abrasion resistance, the PbO resistance and the PbO + PbSO₄ resistance deteriorated. As can be seen from the results of the durability test using the actual engine, the valve built-up with sample No. 1 alloy of the comparative example was inferior in the abrasion resistance and the corrosion resistance. Sample No. 3 alloy of the comparative example, in which only the chromium content did not fall in the limiting ranges of the present invention (namely the chromium content was 41.2 %) exhibited the characteristics no less than the preferred embodiments did, however, sample No. 3 alloy was undesirable from the viewpoint of practicality. This is because the hardness at the high temperature, the corrosion resistance (the PbO resistance and the PbO + PbSO₄ resistance) and so on were not improved greatly even when more than 40 % of chromium was added in the alloy. The upper limit of the chromium content was thus set to 40 % by weight in the present invention.

Claims: An alloy for building up a valve comprising: with respect to the total weight of said alloy taken as 100%, 30 to 40% by weight of chromium; 15 to 31% by weight of nickel; 7 to 20% by weight of molybdenum; 0.7 to 2.2% by weight of carbon; 1.5% or less by weight of silicon; and balance of iron and inevitable impurities wherein the contents of manganese, aluminum and titanium contained in said inevitable impurities are 0.1% or less by weight, respectively, and said alloy being in the form of powders. An alloy for building up a valve according to Claim 1, wherein the content of said chromium is 33 to 38% by weight. An alloy for building up a valve according to Claim 1, wherein the content of said nickel is 17.0 to 27.5% by weight. An alloy for building up a valve according to Claim 3, wherein the content of said nickel is 20.0 to 27.5% by weight. An alloy for building up a valve according to Claim 1, wherein the content of said molybdenum is 8 to 15% by weight. An alloy for building up a valve according to Claim 5, wherein the content of said molybdenum is 10 to 15% by weight. An alloy for building up a valve according to Claim 1, wherein the content of said carbon is 1.2 to 2.0% by weight. An alloy for building up a valve according to Claim 1, wherein the content of said silicon is 0.4 to 1.2% by weight. An alloy for building up a valve according to any one of Claims 1 - 8, wherein said alloy is in a form of powders of mesh aperture size of 177 - 44 micrometers. An alloy for building up a valve comprises: with respect to the total weight of said alloy taken as 100%, 30 to 40% by weight of chromium; 15 to 31% by weight of nickel; 7 to 20% by weight of molybdenum; 0.7 to 2.2% by weight of carbon; 1.5% or less by weight of silicon; and balance of iron and inevitable impurities, wherein the contents of manganese, aluminum and titanium contained in said inevitable impurities are 0.1% or less by weight, respectively and the content of oxygen contained in said inevitable impurities is 0.2% or less by weight, and said alloy being in the form of powders. An alloy for building up a valve comprises: with respect to the total weight of said alloy taken as 100%, 30 to 40% by weight of chromium; 15 to 31% by weight of nickel; 7 to 20% by weight of molybdenum; 0.7 to 2.2% by weight of carbon; 1.5% or less by weight of silicon; and balance of iron and inevitable impurities, wherein said alloy is free from manganese, aluminum and titanium, and said alloy being in the form of powders.

Inventors: HIDAKA KENSUKE C O FUKUDA META, KOYAMA MOTOTSUGU, NAGAI SYOZO C O FUKUDA METAL F, NAKAGAWA MASAHIRO, OISHI SHINJI, TANAKA KANICHI C O FUKUDA META, HIDAKA, KENSUKE C/O FUKUDA METAL FOIL &, KOYAMA, MOTOTSUGU, NAGAI, SYOZO C/O FUKUDA METAL FOIL &, NAKAGAWA, MASAHIRO, OISHI, SHINJI, TANAKA, KANICHI C/O FUKUDA METAL FOIL &, Hidaka, Kensuke c/o Fukuda Metal Foil &amp;, Nagai, Syozo c/o Fukuda Metal Foil &amp;, Tanaka, Kanichi c/o Fukuda Metal Foil &amp;
Applicants: FUKUDA METAL FOIL POWDER, TOYOTA MOTOR CO LTD, FUKUDA METAL FOIL & POWDER CO., LTD., TOYOTA JIDOSHA KABUSHIKI KAISHA
Application year: 1989
Main classification: B23K35
IPC codes: B23K35, F01L3, F02B1, C22C30