Polyurethanes made from blends of polypropyleneoxide polyol and organic-silicone block copolymer based polyol intermediates

Abstract: A urethane sealant or coating composition is made from a physical blend of a polypropyleneoxide polyol intermediate and an organic-silicone block copolymer based polyol intermediate. The urethane prepolymer is made by reacting the physical intermediate blend with a polyisocyanate and preferably blocking the same with blocking agents such as phenols to prevent reaction with moisture in the air. Cure is effected through the utili­ zation of curing agents such as polyamines or polyimines, for example, diamines, amine terminated polyethers, keti­ mines, aldimines, and the like. The sealant composition can contain various fillers, organosilanes, and the like. The prepolymers of the present invention generally have improved elongation and reduced modulus. Either a one-­ part or a two-part system can be utilized.

Description: FIELD OF THE INVENTION The present invention relates to a polyurethane sealant composition or a prepolymer composition comprising a blocked isocyanate-terminated prepolymer, a polyamine or a polyimine curing agent, and optional organosilanes, fillers, and the like. The prepolymer is made from a physical blend of intermediates containing a minor amount of an organic-silicone block copolymer based polyol. BACKGROUND Sealant and coating compositions desirably have a combination of properties which render them particularly suitable for their intended applications. Such compositions should be able to be packaged in sealed containers or cartridges and stored for relatively long periods of time without objectionable "setting up" or hardening, that is curing of the components in the package. The one component sealant composition should form a relatively tack-free surface upon application and upon exposure to atmospheric moisture should cure without the formation of bubbles within a suitable time. The two component system can be formulated into package stable systems with adjustable cure rate and cured sealant properties. When cured, they should adhere tenaciously to a wide variety of surfaces such as glass, aluminum, concrete, marble, and steel. They should also have sufficient elasticity and flexibility to withstand contraction and expansion of panels, and the like, generally associated with temperature variations as a result of climatic changes and/or wind forces. SUMMARY OF THE INVENTION According to the concepts of the present invention, urethane sealants and coatings having improved elongation and reduced modulus are produced when a physical blend of polyol intermediates is utilized. Thus, provided are a prepolymer composition, comprising: an isocyanante-terminated urethane prepolymer prepared from (i) a polyisocyanate having the formula R(NCO) n wherein R is an aliphatic, aromatic, or an aliphatic substituted aromatic having from 4 to 20 carbon atoms, wherein n is 2, 3 or 4, (ii) a blend of polypropyleneoxide polyol intermediate and an organic-silicone block copolymer based polyol intermediate, the amount of said polypropyleneoxide polyol intermediate being from 60 percent to 92 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, the amount of said organic-silicone block copolymer based polyol intermediate being from 8 percent to 40 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, said polypropyleneoxide polyol having a weight average molecular weight of from 1,000 to 10,000, and said organic-silicone block copolymer based polyol intermediate having a weight average molecular weight of from 1,000 to 10,000, wherein said organic-silicone block copolymer based polyol intermediate has the formula HO―A―(B―A) x ―OH wherein x is 1 to 10, wherein A is an organic block portion, and wherein B is said silicone block portion, wherein said "A" organic block is made from a polyalkyleneoxide monomer having from 2 to 5 carbon atoms, wherein said "B" silicone block contains repeating units of the formula wherein "m" is from 5 to 100, wherein R¹ and R², independently, is an aliphatic having from 1 to 6 carbon atoms, wherein the amount of said two or more organic blocks is from 20 percent to 80 percent by weight and wherein said silicone block is from 20 percent to 80 percent by weight based upon the total weight of said organic-silicone block copolymer based polyol intermediate, said isocyanate-terminated urethane prepolymer being subsequently blocked with (iii) a blocking agent wherein the equivalent ratio of the blocking agent to the terminated isocyanate groups is at least 0.85, and a polyurethane sealant composition or admixture, comprising: an isocyanate-terminated and blocked prepolymer and an effective amount of a polyamine or a polyimine curing agent capable of curing said blocked urethane prepolymer. The polyol intermediate blend contains a major amount of a polypropyleneoxide polyol having a molecular weight of from 1,000 to 10,000 in association with a minor amount of an organic-silicone block copolymer based polyol. The polypropyleneoxide polyol can also be a copolymer. The organic-silicone block copolymer based polyol can be a triblock copolymer having terminal block(s) made from polyalkyleneoxide polyol wherein the alkylene portion contains from 2 to 100 carbon atoms. The silicone block contains a dialiphatic substituted siliconeoxide repeating unit wherein the aliphatic groups independently contain from 1 to 6 carbon atoms. The molecular weight of the organic-silicone block copolymer based polyol is from 1,000 to 10,000. Reaction of the polyol intermediate blend with a polyisocyanate yields a prepolymer which is subsequently blocked with blocking agents such as a phenol. The curing agent can be a polyamine such as a di-or triamine, e.g. an amine terminated polyether, or a fatty acid amine, or polyimines such as ketimines or aldimines. The sealants and coating compositions of the present invention can be either a two-part system or a one-part system which is moisture curable and forms a tack-free surface upon being exposed to the atmosphere for a short period of time. A cured sealant is formed within a matter of hours after application which adheres tenaciously to a wide variety of substrates. DETAILED DESCRIPTION OF THE INVENTION The urethane prepolymers of the present invention are made from a physical blend of a polypropyleneoxide polyol intermediate and an organic-silicone block copolymer based polyol intermediate. The polypropyleneoxide polyol intermediate is a homo- or a copolymer having a weight average molecular weight of from 1,000 to 10,000 and preferably from 4,000 to 7,000. The amount of the polypropyleneoxide polyol intermediate is from 60 to 92 percent by weight, and preferably from 80 to 90 percent by weight based upon the total weight of the polypropyleneoxide polyol intermediate and the organic-silicone block copolymer based polyol intermediate. The polypropylene oxide polyol may be a copolymer in which the amount of the comonomer is generally from 0 to 60 percent and preferably from 2 to 6 percent by weight based upon the total weight of the comonomer and the propyleneoxide monomer. Comonomers include butyleneoxide, pentyleneoxide, with ethyleneoxide being preferred. The copolymers can either be random or blocked. The polyol intermediate may or may not be a blend of monols, diols, or triols. Generally, the average functionality of the polypropyleneoxide polyol intermediate is from 1.9 to 3.0. Considering the organic-silicone block copolymer based polyol intermediate, it generally contains two or more organic blocks which are made from an alkyleneoxide monomer having from 2 to 5 carbon atoms with 3 carbon atoms, that is propyleneoxide, being preferred. The two or more organic blocks are terminal blocks and contain hydroxyl end groups. The organic-silicone block copolymer based polyol intermediate is represented by the formula HO―A―(B―A) x ―OH where x is from 1 to 10 with one being preferred, A is the organic block, and B is the silicone block. The organic block, that is A, has been described hereinabove. The silicone (B) block contains repeating units of the formula wherein m is 5 to 100 and preferably 20 to 50, wherein R¹ and R², independently, is an aliphatic, especially an alkyl, having from 1 to 6 carbon atoms with methyl being preferred. The amount of the silicone block is from 20 to 80 percent by weight and preferably from 40 to 60 percent by weight based upon the total weight of the organic-silicone block copolymer. The amount of the A organic block portion is from 20 to 80 percent by weight and preferably from 40 to 60 percent by weight based upon the total weight of the organic-silicone block copolymer. The organic-silicone block copolymer based polyol generally has a weight average molecular weight of from 1,000 to 10,000 with from 3,000 to 6,000 being preferred. The amount of the organic-silicone block copolymer based polyol intermediate utilized in forming the intermediate blends of the present invention is from 8 percent to 40 percent by weight and preferably from 10 percent to 20 percent by weight based upon the total weight of the polypropyleneoxide polyol intermediate and the organic-silicone block copolymer based polyol intermediate. The polyisocyanates which are reacted with the physical blend of the polyol intermediates have the formula R(NCO) n wherein n is 2, 3 or 4 and R is an aliphatic, an aromatic, or an aliphatic substituted aromatic having from 4 to 20 carbon atoms and preferably from 6 to 15 carbon atoms. Desirably the aliphatic groups are alkyl groups. Examples of specific di- or triisocyanates which can be utilized include p,p',p''-triisocyanato triphenyl methane, p,p'-diisocyanato diphenyl methane (MDI), hexamethylene diisocyanate, naphthalene-1,5-diisocyanate, and various isomers of toluene diisocyanates (TDI) such as 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, and mixtures thereof. MDI and TDI are preferred. Inasmuch as an adhesive type composition is desired, the equivalent weight ratio of the polyisocyanate to the polyol intermediate, that is the NCO/OH ratio is from 1.8 to 2.2 and preferably from 2.0 to 2.1. The formation of the prepolymer while occurring at ambient temperature is generally conducted at higher temperatures to reduce the reaction time as from between 40 o to 125 o C with from 60 o to 100 o C being preferred. In order to provide a prepolymer that is more stable during storage, the isocyanate-terminated prepolymer described above is substantially "blocked" with a blocking agent that reacts with the terminal isocyanate groups of the prepolymer. Blocking agents useful in the present invention include conventional blocking agents as well as those known to the art and to the literature that produce blocked terminal isocyanates that do not readily react with moisture in air at room temperature (25 o C). However, upon exposure of the curing agents to moisture, they will "unblock" the isocyanate and react therewith. General types of blocking agents include the various phenol type compounds, various oxime compounds, various ester compounds, and the like. Examples of suitable blocking agents include phenol, 3-methoxyphenol, 4-methoxyphenol, nonylphenol, meta-cresol, paracresol, 4-chlorophenol, meta-hydroxybenzaldehyde, ortho-hydroxybenzaldehyde, parahydroxybenzaldehyde, hydroquinone, 1-hydroxy-2-propanone, 3-hydroxyacetophenone, 4-hydroxyacetophenone, ethyl acetyl acetate and cyclohexanone oxime. A sufficient amount of the blocking agent is utilized to react with the isocyanate prepolymers to substantially "block" the terminal isocyanate groups and preferably to block all of the terminal isocyanate groups. The amount of blocking agent utilized is such that the equivalent weight ratio of the blocking agent to the terminal isocyanate groups is at least 0.85, generally it is at least 1.00 or more and can be utilized in a large excess since it can be used as a plasticizing agent. The curing agents of the present invention include the various polyamine and the various polyimine compounds. The particular type of curing agent utilized generally depends upon whether a two-part urethane sealant or coating system is utilized or a one-part system. When a two-part system is utilized, the curing agent is contained as a separate component or composition which is not mixed with the prepolymer component or composition until immediately prior to application of the sealant or coating composition. Generally, any conventional polyamine curing agent can be utilized including those known to the art and to the literature. An example of a typical polyamine curing agent is a diamine or a triamine represented by the formula wherein R is an aliphatic, or an aliphatic substituted aromatic, with the aliphatic group being connected to the amine group having from 1 to 25 carbon atoms and preferably from 2 to 10 carbon atoms, with x being 0 or 1, and preferably 0. Examples of specific amine compounds include ethylene diamine, propylene diamine, butylene diamine, octamethylene diamine, decamethylene diamine, and the like. Another class of suitable polyamine compounds are the various amine terminated polyethers. These compounds are generally diamines or triamines containing polyether groups therein wherein the number of ether repeating units can vary as from 2 or 3 up to 150. The molecular weight of the amine terminated polyethers is generally from 200 to 7000. Such compounds are produced by the Texaco Chemical Co. under the brand name Jeffamine® such as the M series, the D series, the ED series, the DU series, the BuD series, and the Jeffamine® T series. Such amine terminated polyethers are described in the bulletin, "The Jeffamine® Polyoxyalkyleneamines", by the Texaco Chemical Co., Copyright 1985, NPD-024 102-0745. A particularly preferred compound is the Jeffamine® D compounds which have the following formula: wherein n is from 2 to 100 and preferably from 4 to 20. Still another class of suitable polyamine compounds are the polyamide polyamines made from polyamines and dicarboxylic acids having from 2 to 36 carbon atoms such as oxalic acid, malonic acid, succinic acid, adipic acid, suberic acid, azelalic acid, dimerized fatty acids, trimerized fatty acids, and the like. When a one-part system is utilized, that is a composition in which all of the components of the polyurethane sealant or coating are contained together, a polyimine curing agent is generally utilized. The polyimines will not react with the blocked isocyanate-terminated prepolymer unless exposed to moisture as upon application of the sealant. Various polyimines can be prepared by reacting any of the above polyamine compounds with either a ketone or an aldehyde as well known to those skilled in the art and to the literature. The end result is the production of various ketimine compounds or aldimine compounds. Examples of specific ketimine type compounds which can be utilized are set forth in U.S. Patent No. 4,507,443. Regardless of whether a one-part or two-part system is utilized, the amount of the polyamine or polyimine curing agent is from 0.6 to 1.5 weight equivalents and preferably 0.8 to 1.2 weight equivalents per equivalent of a blocked isocyanate. When a two-component system is utilized, as noted above, one of the components contains the prepolymer and the second component contains the curing agent. The curing agent component generally contains the polyamine curing agent, and various additives in conventional amounts, if desired, such as various plasticizers, pigments, thickeners, drying agents, and the like. The prepolymer or base component contains various conventional additives or compounding ingredients such as fillers, thixotropic agents, extenders, pigments, plasticizers, UV absorbers, solvents, and the like. Typically, the prepolymer component contains large amounts of a filler such as talc, various types of silicates, various types of clays, calcium carbonate, and the like, in an amount of from 60 to 200 parts by weight per 100 parts by weight of the prepolymer; a thickening agent such as a thixotropic compound in an amount of from 0 to 30 parts by weight per 100 parts by weight of the prepolymer; UV absorbers in an amount of usually less than 1 or 2 parts by weight per 100 parts by weight of the prepolymer; and plasticizers in an amount of from 0 to 50 parts by weight per 100 parts by weight of the prepolymer. Solvents, which are generally utilized to adjust the viscosity of the prepolymer or base component to a desired range, constitute generally less than 10 percent volatility of the total prepolymer component for sealant compositions. In coating compositions, the amount of solvent is generally higher. An optional aspect of the present invention is the utilization of an organosilane or an organosiloxane as an adhesion promoter. The amount of such adhesion promoter is from 0.1 to 10 parts by weight per 100 parts by weight of the prepolymer. Types of various adhesion promoters which are desired include an epoxysilane, an isocyanato silane, a ketimino silane, an aminosilane, and the like, such as those set forth in U.S. Patent No. 4,067,844 to Barron. The prepolymers of the present invention utilizing the above-noted physical blend of a polypropyleneoxide polyol intermediate and an organic-silicone block copolymer based polyol intermediate can be formulated into sealants or coatings with improved properties such as improved elongation in accordance with ASTM D-412, and reduced modulus 100 % in accordance with ASTM D-412 while maintaining generally good tensile strength in accordance with ASTM D-412. The invention will be better understood by reference to the following examples. EXAMPLE 1 A mixture of polypropyleneoxidetriol (R-1322, an experimental product from Union Carbide, molecular weight, 7300) (900 grams), Masil® 219-135 (an experimental silicone organic block copolymer based polyol from Mazer Chemicals, Molecular Weight, 4600, molecular weight of combined ether blocks is approximately equal to the molecular weight of silicone block) (100 grams), 76.1 grams of an 80/20 weight percent mixture of 2,4-tolylene diisocyanate and 2,6-tolylene diisocyanate, toluene (100 grams) were heated at 92 o C for three hours. 100.6 grams of nonyl phenol was then added and heating continued for an additional 45 minutes. 0.1 grams of stannous octoate was then added and heating continued for another two hours to give a polymer used in Examples A and C. EXAMPLE 2 (Control) A polyurethane prepolymer used in Examples B and D were prepared using 1001 grams of R-1322 (see Example 1), 75.2 grams of an 80/20 weight percent mixture of 2,4-tolylene diisocyanate, and 2,6-tolylene diisocyanates, 100 grams of toluene, 99.6 grams of nonyl phenol, and 0.2 grams of stannous octoate. Procedure for preparing this prepolymer is given in Example 1. EXAMPLE 3 A mixture of polypropyleneoxidetriol (molecular weight, about 6000, 300 grams), Masil® 219-135 (100 grams), 35.2 grams of an 80/20 weight percent mixture of 2,4-tolylene diisocyanate and 2,6-tolylene diisocyanate, toluene (40 grams) were heated at 95 o C for two hours. 44.5 grams of nonyl phenol was then added and heating continued for an additional one hour. 0.04 grams of stannous octoate was then added and heating continued for another two hours to give a polymer used in Example E. EXAMPLE 4 (Comparative) A mixture of Masil® 219-135 (1000 grams), 82.0 grams of an 80/20 weight percent mixture of 2,4-tolylene diisocyanate and 2,6-tolylene diisocyanate, toluene (70 grams) were heated at 80 o C for two hours. 99.9 grams of nonyl phenol was then added and heating continued for an additional one hour. 0.1 grams of stannous octoate was then added and heating continued for another two hours to give a polymer used in Example F. As apparent from Table I, by comparing Example A to B and by comparing Example C to D, utilization of 10 percent by weight of an organic-silicone block copolymer based polyol intermediate of the present invention resulted in improved elongation and reduced 100 percent modulus at different cure levels. The tensile strength in Examples A and C were very adequate. Example E utilizing 25 percent of the organic-silicone block copolymer based polyol intermediate gave adequate elongation and reduced 100 percent modulus as well as adequate tensile strength. However, when the amount of the organic-silicone block copolymer based polyol intermediatee was increased to 100 percent as in Example F, poor properties were obtained.

Claims: Claims for the following Contracting States : DE, FR, GB, IT A prepolymer composition, comprising: an isocyanate-terminated urethane prepolymer prepared from (i) a polyisocyanate having the formula R(NCO) n wherein R is an aliphatic, aromatic, or an aliphatic substituted aromatic having from 4 to 20 carbon atoms, wherein n is 2, 3 or 4, (ii) a blend of a polypropyleneoxide polyol intermediate and an organic-silicone block copolymer based polyol intermediate, the amount of said polypropyleneoxide polyol intermediate being from 60 percent to 92 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, the amount of said organic-silicone block copolymer based polyol intermediate being from 8 percent to 40 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, said polypropyleneoxide polyol having a weight average molecular weight of from 1,000 to 10,000, and said organic-silicone block copolymer based polyol intermediate having a weight average molecular weight of from 1,000 to 10,000, wherein said organic-silicone block copolymer based polyol intermediate has the formula HO―A―(B―A) x ―OH wherein x is 1 to 10, wherein A is an organic block portion, and wherein B is said silicone block portion, wherein said "A" organic block is made from a polyalkyleneoxide monomer having from 2 to 5 carbon atoms, wherein said "B" silicone block contains repeating units of the formula wherein "m" is from 5 to 100, wherein R¹ and R², independently, is an aliphatic having from 1 to 6 carbon atoms, wherein the amount of said two or more organic blocks is from 20 percent to 80 percent by weight and wherein said silicone block is from 20 percent to 80 percent by weight based upon the total weight of said organic-silicone block copolymer based polyol intermediate, said isocyanate-terminated urethane prepolymer being subsequently blocked with (iii) a blocking agent wherein the equivalent ratio of the blocking agent to the terminated isocyanate groups is at least 0.85. A prepolymer composition according to Claim 1, wherein said polypropyleneoxide polyol intermediate is a homopolymer or a copolymer, wherein said copolymer is made from propyleneoxide monomer and an ethyleneoxide, butyleneoxide, or pentyleneoxide comonomer, wherein the amount of said comonomer is from 0 percent to 60 percent by weight based upon the total weight of said propyleneoxide monomer and said comonomer. A prepolymer composition according to Claim 2, wherein R¹ and R², independently, is an alkyl having from 1 to 6 carbon atoms. A prepolymer composition according to Claim 3, wherein said organic-silicone block copolymer based polyol intermediate has two organic blocks, wherein said organic block is made from a polypropyleneoxide monomer, and wherein the equivalent weight ratio of said polyisocyanate (i) to said polyol blend (ii) is from 1.8 to 2.2. A prepolymer composition according to Claim 4, wherein the molecular weight of said polypropyleneoxide polyol is from 4,000 to 7,000, wherein the molecular weight of said organic-silicone block copolymer based polyol intermediate is from 3,000 to 6,000, wherein the equivalent weight ratio of said blocking agent (iii) to said terminated isocyanate groups is at least 1.0, and wherein the amount of said two organic block portions is from 40 percent to 60 percent by weight and wherein the amount of said silicone-block portion is from 40 percent to 60 percent by weight based upon the total weight of said organic-silicone block copolymer based polyol intermediate. A prepolymer composition according to Claim 5, wherein the amount of said polypropyleneoxide polyol intermediate is from 80 percent to 90 percent by weight and wherein the amount of said organic-silicone block copolymer based polyol intermediate is from 10 percent to 20 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, wherein the comonomer is ethyleneoxide, wherein the amount of said ethyleneoxide comonomer is from 2 percent to 6 percent by weight based upon the total weight of said propyleneoxide monomer and said ethyleneoxide comonomer, wherein R¹ and R² is methyl, and wherein said polyisocyanate is MDI or TDI. A prepolymer composition according to Claim 2, 4 or 6 wherein said prepolymer is cured. A polyurethane sealant composition or admixture, comprising: an isocyanate-terminated and blocked prepolymer as claimed in claim 1 and an effective amount of a polyamine or a polyimine curing agent capable of curing said blocked urethane prepolymer. A polyurethane sealant composition according to Claim 8, wherein the polypropyleneoxide polyol intermediate is a homopolymer or a copolymer as claimed in claim 2. A polyurethane sealant composition according to Claim 8 comprising a prepolymer according to claim 4. A polyurethane sealant composition according to Claim 10 comprising a prepolymer according to claim 5. A polyurethane sealant composition according to Claim 11 comprising a prepolymer according to claim 6 and wherein "m" is 20 to 50. A polyurethane sealant composition or admixture according to Claim 9 or 11, wherein said composition or admixture is cured. A polyurethane sealant composition or admixture according to Claim 8 or 12, wherein said composition or admixture is a one-part system, and wherein said one-part system is cured. Claims for the following Contracting State : ES A process of preparing a prepolymer composition, comprising: an isocyanate-terminated urethane prepolymer prepared from (i) a polyisocyanate having the formula R(NCO) n therein R is an aliphatic, aromatic, or an aliphatic substituted aromatic having from 4 to 20 carbon atoms, wherein n is 2, 3 or 4, (ii) a blend of a polypropyleneoxide polyol intermediate and an organic-silicone block copolymer based polyol intermediate, the amount of said polypropyleneoxide polyol intermediate being from 60 percent to 92 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, the amount of said organic-silicone block copolymer based polyol intermediate being from 8 percent to 40 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, said polypropyleneoxide polyol having a weight average molecular weight of from 1,000 to 10,000, and said organic-silicone block copolymer based polyol intermediate having a weight average molecular weight of from 1,000 to 10,000, wherein said organic-silicone block copolymer based polyol intermediate has the formula HO―A―(B―A) x ―OH wherein x is 1 to 10, wherein A is an organic block portion, and wherein B is said silicone block portion, wherein said "A" organic block is made from a polyalkyleneoxide monomer having from 2 to 5 carbon atoms, wherein said "B" silicone block contains repeating units of the formula wherein "m" is from 5 to 100, wherein R¹ and R², independently, is an aliphatic having from 1 to 6 carbon atoms, wherein the amount of said two or more organic blocks is from 20 percent to 80 percent by weight and wherein said silicone block is from 20 percent to 80 percent by weight based upon the total weight of said organic-silicone block copolymer based polyol intermediate, said isocyanate-terminated urethane prepolymer being subsequently blocked with (iii) a blocking agent wherein the equivalent ratio of the blocking agent to the terminated isocyanate groups is at least 0.85. A process according to Claim 1, wherein said polypropyleneoxide polyol intermediate is used as a homopolymer or a copolymer, wherein said copolymer is made from propyleneoxide monomer and an ethyleneoxide, butyleneoxide, or pentyleneoxide comonomer, wherein the amount of said comonomer is from 0 percent to 60 percent by weight based upon the total weight of said propyleneoxide monomer and said comonomer. A process according to Claim 2, wherein R¹ and R², independently, is an alkyl having from 1 to 6 carbon atoms. A process according to Claim 3, wherein said organic-silicone block copolymer based polyol intermediate has two organic blocks, wherein said organic block is made from a polypropyleneoxide monomer, and wherein the equivalent weight ratio of said polyisocyanate (i) to said polyol blend (ii) is from 1.8 to 2.2. A process according to Claim 4, wherein the molecular weight of said polypropyleneoxide polyol is from 4,000 to 7,000, wherein the molecular weight of said organic-silicone block copolymer based polyol intermediate is from 3,000 to 6,000, wherein the equivalent weight ratio of said blocking agent (iii) to said terminated isocyanate groups is at least 1.0, and wherein the amount of said two organic block portions is from 40 percent to 60 percent by weight and wherein the amount of said silicone-block portion is from 40 percent to 60 percent by weight based upon the total weight of said organic-silicone block copolymer based polyol intermediate. A process according to Claim 5, wherein the amount of said polypropyleneoxide polyol intermediate is from 80 percent to 90 percent by weight and wherein the amount of said organic-silicone block copolymer based polyol intermediate is from 10 percent to 20 percent by weight based upon the total weight of said polypropyleneoxide polyol intermediate and said organic-silicone block copolymer based polyol intermediate, wherein the comonomer is ethyleneoxide, wherein the amount of said ethyleneoxide comonomer is from 2 percent to 6 percent by weight based upon the total weight of said propyleneoxide monomer and said ethyleneoxide comonomer, wherein R¹ and R² is methyl, and wherein said polyisocyanate is MDI or TDI. A process according to Claim 2, 4 or 6 wherein said prepolymer is cured. A process of preparing a polyurethane sealant composition or admixture, which comprises blending an isocyanate-terminated and blocked prepolymer prepared as claimed in claim 1 and an effective amount of a polyamine or a polyimine curing agent capable of curing said blocked urethane prepolymer. A process according to Claim 8, wherein the polypropyleneoxide polyol intermediate is a homopolymer or a copolymer prepared as claimed in claim 2. A process according to Claim 8 comprising a prepolymer prepared according to claim 4. A process according to Claim 10 comprising a prepolymer prepared according to claim 5. A process according to Claim 11 comprising a prepolymer prepared according to claim 6 and wherein "m" is 20 to 50. A process according to Claim 9 or 11, wherein said composition or admixture is cured. A process according to Claim 8 or 12, wherein said composition or admixture is a one-part system, and wherein said one-part system is cured.

Inventors: BANDLISH BALDEV K, BARRON LARRY R, BANDLISH, BALDEV K., BARRON, LARRY R.
Applicants: TREMCO INC, TREMCO INCORPORATED (AN OHIO CORPORATION)
Application year: 1989
Main classification: C08G18
IPC codes: C08G18