Catalyst for removing peroxide contaminants from tertiary butyl alcohol

Abstract: Motor-fuel grade tertiary butyl alcohol contaminated with residual amounts of tertiary butyl hydroperoxide and ditertiary butyl peroxide (which is prepared, for example, by reacting propylene with tertiary butyl hydroperoxide to form propylene oxide and a motor fuel grade tertiary butyl alcohol reaction product) can be effectively catalytically treated under mild conversion conditions including a tem­ perature of about 80° to 200°C with a catalyst consisting essentially of nickel, copper, chromium and barium to sub­ stantially selectively convert the two peroxide contaminants to tertiary butyl alcohol and to thereby provide a treated tertiary butyl alcohol product substantially free from con­ taminating quantities of such peroxides.

Description: This invention relates to a method for the removal of residual contaminating quantities of tertiary butyl hydroperoxide and ditertiary butyl peroxide from a tertiary butyl alcohol feedstock to provide a tert. butyl alcohol product containing only a minor amount of isobutylene which is useful as an octane-enhancing component for motor fuels. In accordance with the present invention the peroxide-contaminated feedstock is brought into contact with a hydrogenation catalyst consisting essentially of nickel, copper, chromia and baria in order to substantially selectively reduce both the tertiary butyl hydroperoxide and the ditertiary butyl peroxide to tertiary butyl alcohol without significantly increasing isobutylene contamination. A process for the manufacture of substituted epoxides from alpha olefins such as propylene is disclosed in Kollar U. S. Patent No. 3,351,635 which teaches that an organic epoxide compound can be made by reacting an olefinically unsaturated compound with an organic hydroperoxide in the presence of a molybdenum, tungsten, titanium, columbium, tantalum, rhenium, selenium, chromium, zirconium, tellurium or uranium catalyst. When the olefin is propylene and the hydroperoxide is tertiary butyl hydroperoxide, propylene oxide and tertiary butyl alcohol are coproducts. U. S. Patent No. 3,350,422 teaches a similar process using a soluble vanadium catalyst. Molybdenum is the preferred catalyst. A substantial excess of olefin relative to the hydroperoxide is taught as the normal procedure for the reaction. See also U. S. Patent No. 3,526,645 which teaches the slow addition of organic hydroperoxide to an excess of olefin as preferred. Stein, et al. in U. S. Patent No. 3,849,451 have improved upon the Kollar process of U. S. Patent Nos. 3,350,422 and 3,351,635 by requiring a close control of the reaction temperature, between 90-200°C and autogeneous pressures, among other parameters. Stein et al. also suggests the use of several reaction vessels with a somewhat higher temperature in the last vessel to ensure more complete reaction. The primary benefits are stated to be improved yields and reduced side reactions. It is known that isobutane can be oxidized with molecular oxygen to form a corresponding tertiary butyl hydroperoxide and that the oxidation reaction can be promoted, for example with an oxidation catalyst (see Johnston U. S. Patent No. 3,825,605 and Worrell U. S. Patent No. 4,296,263. Thus, tertiary butyl alcohol can be prepared either by the direct thermal or catalytic reduction of tertiary butyl hydroperoxide to tertiary butyl alcohol or by the catalytic reaction of propylene with tertiary butyl hydroperoxide to provide propylene oxide and tertiary butyl alcohol. It is also known that tertiary butyl alcohol can be used as an octane-enhancing component when added to a motor fuel, such as gasoline. Thus, it has heretofore been proposed, as shown, for example, by Grane U. S. Patent No. 3,474,151 to thermally decompose tertiary butyl hydroperoxide and ditertiary butyl peroxide to form tertiary butyl alcohol. The thermal decomposition must be conducted with care, as pointed out by Grane, in that tertiary butyl alcohol will start to dehydrate at a temperature of about 232°C (450°F) and in that the dehydration becomes rapid at temperatures above about 246°C (475°F). Moreover, the product from the thermal decomposition normally contains a minor amount of tertiary butyl hydroperoxide and ditertiary butyl peroxide which have an adverse effect upon the quality of motor fuels and must be substantially completely removed if the tertiary butyl alcohol is to be effective. Grane proposes to accomplish this thermally by heating tertiary butyl alcohol containing small quantities of such peroxides at a temperature of 190-246°C (375-475°F) for a period of 1 to 10 minutes. This concept was expanded upon by Grane et al. in U. S. Patent Nos. 4,294,999 and 4,296,262 to provide integrated processes wherein, starting with isobutane, motor-fuel grade tertiary butyl alcohol was prepared by the oxidation of isobutane (e.g., in the presence of a solubilized molybdenum catalyst) to produce a mixture of tertiary butyl alcohol and tertiary butyl hydroperoxide from which a fraction rich in tertiary butyl hydroperoxide could be recovered by distillation. This stream, after being debutanized was subjected to thermal decomposition under pressure at a temperature of less than 149°C (300°F) for several hours to significantly reduce the concentration of the tertiary butyl hydroperoxide. However, the product of this thermal decomposition step still contained residual tertiary butyl hydroperoxide, most of which was thereafter removed by a final thermal treatment of the contaminated tertiary butyl hydroperoxide in the manner taught by Grane U. S. Patent No. 3,474,151. Thus, the removal of trace quantities of tertiary butyl hydroperoxide from motor grade tertiary butyl alcohol has received appreciable attention. However, little appears to have been published concerning the removal of trace quantities of ditertiary butyl peroxide, the more refractory of the two peroxides. This may be explainable both because ditertiary butyl peroxide is not always present in trace quantities in motor grade tertiary butyl alcohol (its presence or absence being a function of the reaction conditions used in oxidizing the isobutane starting material) and because, when present, it is present in significantly lower amounts. For example, after decomposition of the major amount of tertiary butyl hydroperoxide formed by the oxidation of isobutane, the tertiary butyl hydroperoxide residual content will normally be about 0.1 to about 1 wt.%, based on the tertiary butyl alcohol, while the residual ditertiary butyl peroxide content, if any, will only be about 0.1 to 0.5 wt.%. Sanderson et al. U. S. Patent No. 4,547,598 discloses the use of unsupported cobalt borate and cobalt borate supported on titanium dioxide to decompose organic hydroperoxides to alcohols. It has also been proposed to remove the residual hydroperoxide contaminants from tertiary butyl alcohol through the use of a heterogeneous cobalt oxide catalyst containing a copper oxide promoter as shown, for example, by Coile U. S. Patent No. 4,059,598. Allison et al. in U. S. Patent No. 3,505,360 have more generically taught that alkenyl hydroperoxides can be decomposed catalytically through the use of a catalyst based on a metal or compound of a metal of group IV-A, V-A or VI-A. Other prior art patents relating to the production of hydroperoxides, but not with the problem of residual tertiary hydroperoxide contamination and tertiary butyl alcohol include patents such as Rust U. S. Patent No. 2,383,919; Harvey U. S. Patent No. 3,449,217; Poenisch et al. U. S. Patent No. 3,778,382 and Williams et al. U. S. Patent No. 3,816,548. In West German DE 3248465-A a two-step process is disclosed wherein isobutane is oxidized noncatalytically with air to a conversion of about 48-90% to form the corresponding hydroperoxide, which is then catalytically decomposed under hydrogenation conditions in the presence of a supported catalyst such as palladium, platinum, copper, rhenium, ruthenium or nickel to form tertiary butyl alcohol. The decomposition product obtained using 1.3% palladium on lithium spinel as a catalyst contained significant quantities of acetone, water and methanol. Mabuchi et al. U. S. Patent No. 4,112,004 discloses a process for preparing monohydric or polyhydric alcohols from organic peroxides in the presence of a nickel catalyst by continuously feeding a solution of the organic peroxide (e.g., butadiene peroxide) and a suspension of the nickel catalyst to a reactor in a controlled ratio and continuously withdrawing reaction mixture at a rate adequate to maintain a constant weight and composition of the reaction mixture in the reactor. In U. S. Patent No. 4,123,616 to Mabuchi et al. a process is disclosed for hydrogenating an organic peroxide to the corresponding mono- or polyhydric alcohol in a suspension or fluidized bed process under hydrogen pressure in the presence of a nickel catalyst. Examples are given showing the conversion of butadiene peroxide to 1,4-butane diol and 1,2-butane diol and the conversion of tertiary butyl hydroperoxide to tertiary butyl alcohol. A process for the decomposition of peroxides, such as a mixture of tertiary butyl hydroperoxide and tertiary butyl alcohol formed by the noncatalyzed oxidation of isobutane is disclosed in Taylor et al. U. S. Patent No. 4,551,553 wherein the decomposition is catalyzed with a catalytic system composed of chromium and ruthenium which is soluble in the hydroperoxide. EP-A-0251526 discloses that a catalyst consisting of nickel, copper, chromia and iron eventually supported on silica can be used to treat a peroxides-contaminated tert. butyl alcohol feedstock to provide a tert. butyl alcohol product substantially free from peroxide contaminants. The production of unwanted side products such as acetone, methanol and isobutylene is significantly supressed by the process, but the results obtained are not always entirely satisfactory, especially in respect of the production of isobutylene as an undesirable contaminating coproduct. EP-A-0266976 discloses the use of a base-treated group VIB or VIIIB metal or mexal oxide catalyst for the removal of peroxide contaminants from tertiary butyl alcohol, such as a base-treated nickel, copper, chromia, iron catalyst. Godfrey U. S. Patent No. 3,037,025 discloses the preparation of N-alkyl substituted piperazines using catalyst compositions consisting of the metals and oxides of copper, nickel and cobalt (including mixtures thereof) which may also be promoted by the inclusion of a normally non-reducible metal oxide such as chromium, aluminum, iron, calcium, magnesium, manganese and the rare earths. Preferred catalyst compositions are indicated as containing from about 44 to about 74 wt.% of nickel, about 5 to about 55 wt.% of copper and about 1 to about 5 wt.% of chromia. Moss U. S. Patent No. 3,151,112 discloses catalyst compositions useful for the preparation of morpholines including one or more metals from the group including copper, nickel, cobalt, chromium, molybdenum, manganese, platinum, palladium and rhodium, which may also be promoted with normally nonreducible oxides such as chromium oxide, molybdenum oxide and manganese oxide. Representative catalyst compositions include those containing from about 60 to about 85 wt.% of nickel, about 14 to about 37 wt.% of copper and about 1 to about 5 wt.% of chromia. Nickel, copper, chromia catalysts are also disclosed in Moss U. S. Patent No. 3,151,115 and Moss U. S. Patent No. 3,152,998. Winderl et al. U. S. Patent No. 3,270,059 teaches the use of catalysts containing a metal of groups I-B and VIII of the Periodic System. Examples of suitable catalysts are stated to be copper, silver, iron, nickel, and particularly, cobalt. Boettger et al. U. S. Patent No. 4,014,933 discloses catalysts containing cobalt and nickel promoted with copper such as those containing from about 70 to about 95 wt.% of a mixture of cobalt and nickel and from about 5 to about 30 wt.% of copper. Habermann U. S. Patent No. 4,152,353 discloses catalyst compositions comprising nickel, copper and a third component which may be iron, zinc, zirconium or a mixture thereof such as catalysts containing from about 20 to about 49 wt.% of nickel, about 36 to about 79 wt.% of copper and about 1 to about 15 wt.% of iron, zinc, zirconium or a mixture thereof. Similar catalyst compositions are mentioned in Habermann U. S. Patent No. 4,153,581. European patent application 0017651 filed October 20, 1980, contains a disclosure of catalyst compositions related to those disclosed by Habermann, such catalyst compositions being composed of nickel or cobalt, copper and iron, and zinc or zirconium such as compositions containing 20 to 90% cobalt, 3 to 72% copper and 1 to 16% of iron, zinc or zirconium and catalyst compositions containing 20 to 49% nickel, 36 to 79% copper and 1 to 16% of iron, zinc or zirconium. German Offen. 2,721,033 discloses a catalyst composition containing nickel, 0,5 to 20 w/w % of iron and 0,5 to 30 w/w % of chromia. Johansson et al. U. S. Patent No. 3,766,184 discloses catalyst compositions composed of iron and nickel and/or cobalt. The feedstocks of the present invention comprise tertiary butyl alcohol contaminated with tertiary butyl hydroperoxide and ditertiary butyl peroxide. When isobutane is treated to form tertiary butyl hydroperoxide, the reaction product will normally contain some tertiary butyl alcohol and other oxygenated by-products such as ditertiary butyl peroxide, acetone, etc., as well as unreacted isobutane. After the unreacted isobutane is flashed, a fraction composed mostly of tertiary butyl alcohol may be recovered as a distillate fraction in order to further concentrate the desired tertiary butyl hydroperoxide reaction product. The tertiary butyl alcohol distillate, which will normally be contaminated with tertiary butyl hydroperoxide, ditertiary butyl peroxide, etc., may be used as a feedstock for the process of the present invention. Tertiary butyl hydroperoxide is suitably reacted with propylene by a process of the type disclosed in Kollar U. S. Patent No. 3,351,635 to provide an initial reaction product composed mostly of unreacted propylene, propylene oxide and tertiary butyl alcohol. However, residual quantities of tertiary butyl hydroperoxide and ditertiary butyl peroxide and other oxygenated impurities are normally present and remain dissolved in the tertiary butyl alcohol recovered from the reaction mixture. This tertiary butyl alcohol product can also be used as a feedstock for the process of the present invention. Tertiary butyl hydroperoxide can decompose thermally and/or catalytically to form acetone. Tertiary butyl alcohol can be decomposed to form water and isobutylene. Accordingly, the tertiary butyl alcohol, as initially recovered is not entirely satisfactory for use as an octane-enhancing component for motor fuels, such as gasoline. Thus, tertiary butyl alcohol will normally be considered unsatisfactory for motor fuel use if it contains more than about 3 wt.% of acetone, more than about 1 wt.% of isobutylene, more than about 100 ppm of ditertiary butyl peroxide and more than 100 ppm of tertiary butyl hydroperoxide. Desirably, the tertiary butyl alcohol will contain about 1 wt.% or less of acetone, 0.5 wt.% or less of isobutylene and 10 ppm or less of ditertiary butyl peroxide and 100 ppm or less of tertiary butyl hydroperoxide. It has been surprisingly discovered in accordance with the present invention that motor-fuel grade tertiary butyl alcohol which is contaminated with residual amounts of ditertiary butyl peroxide and tertiary butyl hydroperoxide can be more effectively catalytically purified when the catalyst that is used is composed of a nickel, copper, chromia, barium catalyst. In accordance with the present invention, a peroxides-contaminated tert. butyl alcohol feedstock such as a feedstock contaminated with tert. butyl hydroperoxide and ditertiary butyl peroxide is brought into contact with a catalyst of the present invention under mild conditions including a temperature of about 80° to 220°C and a pressure sufficient to maintain a liquid phase reaction mixture (normally, about 1,39 to 5,53 MPa (200 to 800 psig.), depending on reaction temperature). Higher pressures of up to about 13,8 MPa (2000 psig.) can be used, if desired, but there is no particular advantage in using the higher pressures. This treatment will substantially selectively convert the peroxide contaminants to tertiary butyl alcohol and thereby provide a treated product substantially free of contaminating quantites of tertiary butyl hydroperoxide and ditertiary butyl peroxide. Thus, the formation of unwanted oxygenated derivatives of the peroxide contaminates, including acetone, methanol and isobutylene is substantially avoided. The results obtained with the process of the present invention are surprising and unexpected in several respects. Catalytic or thermal decomposition of tertiary butyl hydroperoxide and ditertiary butyl peroxide normally results in the formation of acetone as the favored decomposition product. Thus, the favorable effect on the quality of motor fuel grade tertiary butyl alcohol that is obtained by the substantially complete elimination of the two peroxides will be largely counterbalanced if the decomposition product is principally acetone or if more than trace amounts of isobutylene are present. Moreover, we have found that catalysts that are effective for the substantially complete decomposition of tertiary butyl hydroperoxide are normally only partially effective, at best, for the catalytic decomposition of ditertiary butyl peroxide. Inert supports such as silica, magnesia, etc., may be used, if desired. Thus, the provision of the process of the present invention wherein a motor-fuel grade tertiary butyl alcohol feedstock containing contaminating quantities of both ditertiary butyl peroxide and tertiary butyl hydroperoxide, is catalytically treated for the decomposition of the peroxides so that they are substantially completely removed without significantly adding to the level of contamination due to the formation of acetone, methanol and isobutylene constitutes a distinct advantage over the prior art. The starting materials for the process of the present invention include a motor-fuel grade tertiary butyl alcohol feedstock obtained in the manner described above by the reaction of propylene with tertiary butyl hydroperoxide to form propylene oxide and tertiary butyl alcohol by the oxidation of isobutane to form tertiary butyl hydroperoxide, etc. The motor-fuel grade tertiary butyl alcohol feedstock obtained by the reaction of propylene with tertiary butyl hydroperoxide to form propylene oxide and tertiary butyl alcohol will contain contaminating quantities of teritary butyl hydroperoxide, ditertiary butyl peroxide, and acetone, and may also contain contaminating quantities of methanol and isobutylene. The normal levels of contamination of such materials are such that the tertiary butyl alcohol will normally contain, prior to treatment, from about 0.1 to about 5 wt.% of tertiary butyl hydroperoxide and from about 0.1 to about 5 wt.% of ditertiary butyl peroxide. Minor quantities of other contaminants may also be present. As indicated earlier, the reaction conditions used in the catalytic oxidation of isobutane will sometimes result in the formation of ditertiary butyl peroxide. Thus, the feedstock to be used for the practice of the present invention is an impure motor grade tertiary butyl alcohol containing from about 0.1 to about 5 wt.% of tertiary butyl hydroperoxide and from about 0.1 to about 5 wt.% of ditertiary butyl peroxide. The catalyst compositions of the present invention are catalysts consisting essentially of nickel, copper, chrimium and barium. The metal components of the catalyst will normally be present, during use, as oxides of the metals. Thus, in the peroxide decomposition process of the present invention, metallic oxides will not be reduced to their metallic form whereas the metals, if present, will tend to be oxidized to the corresponding metal oxides. A preferred catalyst composition of the present invention consists essentially of a metal and/or oxide of nickel, copper, chromium and barium in the proportions (on an oxygen-free basis) of about 1 to about 20 wt.% of barium, about 1 to about 6 wt.% of chromium and with the balance being nickel and copper in the weight ratio of about 2 to 3 parts of nickel per part of copper. For example, the composition of the present invention may consist essentially of about 30 to about 60 wt.% of nickel, about 5 to about 40 wt.% of copper, about 0.5 to about 10 wt.% of chromium and about 1 to about 30 wt.% of barium, with the nickel and copper being proportioned as indicated above. More preferably, the catalyst compositions of the present invention will consist of about 1 to about 20 wt.% of baria and about 1 to about 5 wt.% of chromia, with the nickel and copper being proportioned as indicated above. The catalyst may also be supported on a suitable support such as silica (e.g., Kieselguhr), alumina, titanium dioxide, clay, and other like supports. When a support is used, the support may suitably comprise from about 30 to about 99.5 wt.% of the total weight of the catalyst composition, the balance (about 0.5 to about 70 wt.%) being composed of the metals and/or metal oxides of nickel, copper, chromia and baria. Although the catalyst compositions of the present invention may be utilized in powdered form in conducting batch reactions, their utility is enhanced when they are used in pelleted form for catalyzing the reaction in a continuous process. In accordance with the present invention, a tertiary butyl alcohol feedstock, as above described, is brought into contact with a catalyst of the present invention under reaction conditions correlated to substantially selectively catalytically convert both the tertiary butyl hydroperoxide and ditertiary butyl peroxide contaminants in the tertiary butyl alcohol feedstock to tertiary butyl alcohol with not more than a minor increase in the level of contamination of the acetone, methanol and isobutylene also normally present in the tertiary butyl alcohol as contaminants. The reaction may be conducted batchwise in an autoclave using powdered catalyst or may be conducted on a continuous basis by passing the tertiary butyl alcohol through a reactor containing a bed of a catalyst of the present invention under reaction conditions including a temperature within the range of about 80° to about 200°C. The reaction is preferably conducted at 1,39 to 5,53 MPa (200 to 800 psig.), although higher pressures of up to about 13,8 MPa (2000 psig.) may be used if desired. When the reaction is conducted batchwise, contact time may suitably be from about 0.5 to about 4 hours. When the reaction is conducted on a continuous basis, the tertiary butyl alcohol should be passed over the bed of catalyst at a liquid hourly space velocity of about 0.25 to about 5. The reaction product, after being degassed, is suitable for use as an octane-enhancing component of motor fuel, such as gasoline. Thus, for example, the effluent from the reactor may be passed through a phase separation zone in order to permit gaseous reaction components including hydrogen and isobutane to volatilize from the product to thereby provide the desired reaction product. The specific correlation of conditions to be utilized with any specific catalyst of the present invention can be determined by one of ordinary skill in the art with comparative ease. Thus, for example, the tertiary butyl alcohol feedstock should be analyzed prior to catalytic treatment to determine the level of contamination by tertiary butyl hydroperoxide, ditertiary butyl peroxide, acetone, methanol and isobutylene. If there is an insufficient reduction of the hydroperoxides such that a significant amount (e.g., more than about 0.1 wt.%) of tertiary butyl hydroperoxide and/or ditertiary butyl peroxide is still present, the reaction conditions are not sufficiently severe, and should be increased such as, for example, by increasing reaction temperature or contact time in order to obtain the desired reduction of the tertiary butyl hydroperoxide. If, on the other hand, there is a significant increase in the level of contamination of acetone, isobutylene and/or methanol, the reaction conditions are too severe for the particular catalyst and the reaction conditions should be ameliorated (e.g., by reducing contact time or temperature). WORKING EXAMPLES Procedure The reactor was a 1,29 cm (0.51") (ID) x 73 cm (29") stainless steel tube. The liquid feed was pumped into the bottom of the reactor. A pre-run was taken at each temperature before sample was taken for analysis. Percent water was determined by Karl-Fischer titration. Other products were determined by GC analysis. Catalyst XX was prepared in essentially the same manner as catalyst GGG. However, barium was not used in preparing catalyst XX. Preparation of Catalyst (6141-12-3) Two solutions prepared as follows: Solution #1 = 1405g of Ni(NO₃)₂.6H₂O; 300g of Cu(NO₃)₂XH₂O; 96g of Cr(NO₃)₃.9H₂O; 140g of Ba(NO₃)₂; and 2500 ml of H₂O. Solution #2 = 800g of Na₂CO₃ and 2500 ml of H₂O. Both solutions were heated to 80°C and added simultaneously to rapidly stirred H₂O (1000 ml) at 80°C over a 1 hour period at rates such that pH remained between 6.85 and 7.45; 280 ml of solution #2 was unconsumed when addition was completed. The resultant mixture was stirred for 1 hour more at 80°C and filtered hot. The filter cake was stirred with 2600 ml of H₂O at 80°C and refiltered. This procedure was repeated five more times (7 filtrations effected in total). after drying for one day at 155°C, the filter cake weighed 840.7g. It was calcined at 400°C for 4½ hours to yield 535.2g. It was reduced in a mixture of flowing nitrogen/hydrogen (initially) and finally all hydrogen at approximately 335°C. The resultant powder was stabilized by gradual admittance of flowing air into flowing nitrogen at 25-29°C until, finally, only air was used. Analysis of this powder indicated Ni 55.0%; Cu 15.6%; Cr 1.8%; and Ba 9.3%, as well as 2400 ppm Na. It was mixed with graphite (3 wt.%) and made into 3 mm x 3 mm (1/8" x 1/8") tablets of 90-136 kg (20-30 lb.) crushing strength. I. Equipment and Procedures In all cases, these evaluations were performed in a 100 cc reactor constructed of 1,27 cm (1/2 inch) stainless steel tubing 43 cm (17 inches) long connected to a 3 mm (1/8 inch) feed and effluent lines with swagelok fittings. The reactor tube was situated inside of a 7,6 x 7,6 cm (3 x 3 inch) aluminum block which was heated electrically with four 1000 watt strip heaters. Temperature control was achieved with a Thermoelectric controller monitoring thermocouples attached to the skin of the reactor body. The feed was charged to the reactor system with a Beckman 110A L.C. pump. The reactor effluent was collected in a glass jug and sampled after the system and lined-out at the prescribed temperature for at least 2.5 hours. The catalysts that were used in the working examples are listed in Table I together with a brief description of their composition. Compare runs 6196-30-4 with run 6129-39-4 (both runs at 160°C at approximately 0.09 kg/hr (0.2 lb/hr) feed rate). Catalyst XX produces 0.214% isobutylene whereas catalyst GGG produces only 0.004% isobutylene. Comparing similar experiments at other temperatures shows similar results - catalyst GGG always produces less isobutylene. Catalysts DD and EE, which contain molybdenum and vanadium (known peroxide decomposition catalysts), produced even higher yields of isobutylene.

Claims: A method for enchancing the motor fuel quality of a tertiary butyl alcohol feedstock contaminated with tertiary butyl hydroperoxide, ditertiary butyl peroxide, acetone, methanol and isobutylene, characterised by contacting said feedstock with a catalyst composed of nickel, copper, chromium and barium at a temperature of 80 to 200°C to form a tertiary butyl alcohol product containing not more than 100 ppm of tertiary butyl hydroperoxide, not more than 100 ppm of ditertiary butyl peroxide, not more than 1 wt.% of isobutylene and not more than 3 wt.% each of acetone and methanol. A method according to Claim 1 characterised in that the catalyst contains a metal component comprising, on an oxygen-free basis, based on the total weight of said metals component, 10 to 90 wt.% of nickel, 1 to 40 wt.% of copper, 0.5 to 30 wt.% of barium and 1 to 10 wt.% of chromium. A method according to Claim 2 characterised in that the metals component of the catalyst comprises 30 to 60 wt.% of nickel and 1 to 25 wt.% of copper, in the weight ratio of 2 to 3 parts of nickel per part of copper, and also contains 1 to 20 wt.% of barium and from 1 to 6 wt.% chromium. A method according to any one of Claims 1 to 3 characterised in that the catalyst comprises said metals component and an inert support. A method according to Claim 4 characterised in that the catalyst comprises 0.5 to 70 wt.% of said metals component (in metal and/or oxide form), and 30 to 99.5 wt.% of said support. A method according to any one of Claims 1 to 5 characterised in that the said catalyst is made by precipitating a mixture of nickel, copper, chromium and barium compounds from an aqueous solution of nickel, copper, chromium, and barium nitrates with a hot solution of an alkali metal carbonate, and thereafter recovering drying, reducing, calcining and pelleting the resultant composition. A method according to any one of Claims 1 to 6 characterised in that the tertiary butyl alcohol feedstock is contaminated with 0.1 to 5 wt.% of tertiary butyl hydroperoxide from 0.1 to 5 wt.% of ditertiary butyl peroxide, and contaminating quantities of acetone, methanol and isobutylene.

Inventors: LARKIN JOHN MICHAEL SR, SANDERSON JOHN RONALD, LARKIN, JOHN MICHAEL, SR., SANDERSON, JOHN RONALD
Applicants: TEXACO DEVELOPMENT CORP, TEXACO DEVELOPMENT CORPORATION
Application year: 1989
Main classification: C07C29
IPC codes: C07C29