Polyketone related polymers

Abstract: Polyketone related polymers, characterized in that they consist of linear chains in which units A and units B occur in alternating order, that the units A are the same or different optionally mono-alkyl-substituted ethylene groups and that the units B are the same or different optionally 3-alkyl-substituted 2,5-tetrahydrofurandiyl groups. They may be prepared from linear alternating polyketones by hydrogenation in the presence of a complex ruthenium catalyst.

Description: The invention relates to novel polymers which can be thought of as polyketone derivatives, as they may be prepared starting from alternating carbon monoxide/α-olefin polymers. Polymers of carbon monoxide with one or more α-olefins in which the monomer units are randomly distributed can be prepared by contacting the monomers with a radical catalyst, such as a peroxide. These polymers contain functional carbonyl groups and are therefore also referred to as polymeric polyketones. The carbonyl groups present in these polymeric polyketones can be converted into secondary alcohol groups by catalytic hydrogenation. Both the carbonyl groups present in the polymeric polyketones and the secondary alcohol groups present in the polymeric polyketones obtained occur randomly distributed within the polymers. A special class of polymeric polyalcohols is formed by the polyvinyl alcohols, which can be prepared by hydrolysis or saponification of polyvinyl acetates. Unlike the afore-mentioned polymeric polyalcohols prepared from polyketones, the polyvinyl alcohols have a regular structure in which secondary alcohol groups and methylene groups occur in alternating order. Although, in general, polyvinyl alcohols have excellent properties, their thermal stability is somewhat unsatisfactory. This is due to their special structure, in which there is a methylene group between every two successive secondary alcohol groups, as a result of which the liberation of water leads to the formation of a system of conjugated double bonds in the polymer. Speculating that the risk of the formation of a system of conjugated double bonds might be removed by changing the special structure of the polyvinyl alcohols, and that thus their thermal stability might be improved, the Applicant has carried out an investigation into the preparation of linear polymeric polyalcohols which are closely related to polyvinyl alcohols but in which there is an ethylene group or a monoalkyl-substituted ethylene group between every two successive secondary alcohol groups. It was assumed that such linear polymeric polyalcohols could be prepared by the catalytic hydrogenation of linear polymeric polyketones obtained by the polymerization of carbon monoxide with one or more α-olefins, provided that in these polyketones the monomer units originating in carbon monoxide and the units originating in the α-olefins occur in alternating order. Earlier research done by the Applicant had already shown that such linear alternating polyketones can be prepared by contacting the monomers at an elevated temperature and pressure with a catalyst composition based upon, for example, a) a palladium compound, b) an anion of an acid with a pKa of less than 6, and c) a bisphosphine of the general formula (R₁)₂P-R-P(R₁)₂, in which R₁ represents an optionally polar-substituted aryl group and R is a bivalent organic bridging group containing at least two carbon atoms in the bridge. At first, the results of the Applicant's efforts to prepare linear polymeric polyalcohols in which secondary alcohol groups and, optionally, monoalkyl-substituted ethylene groups occur in alternating order, by way of the catalytic hydrogenation of the alternating polyketones obtained as described hereinbefore, were very disappointing. The investigation involved various catalyst compositions which per se had been found suitable for the almost quantitative conversion of monoketones, such as acetone, into the corresponding secondary alcohols. In some cases, these catalyst compositions when used for the hydrogenation of the alternating polyketones failed to produce any reaction; in other cases, there was some reaction, but this led to a complex polymer mixture in which the alternating character of the starting material was lost altogether. Among the tested catalyst compositions, however, there was one group which did produce a surprising and altogether unexpected result. These are the catalyst compositions which comprise a complex ruthenium carbonyl compound and an iodide. Contacting an alternating carbon monoxide/ethene copolymer prepared in the afore-described manner at an elevated temperature and pressure and in the presence of hydrogen with a solution of such a catalyst composition in an organic solvent afforded an entirely novel polymer material in high yield. Instead of the expected linear polymeric alternating polyalcohol, a linear polymer was obtained in which ethylene groups and 2,5-tetrahydrofurandiyl groups occurred in alternating order. Apparently, a combination of hydrogenation on the one hand and dehydration with ring closure on the other hand came about under the influence of this catalyst composition. Linear polymers in which ethylene groups and 2,5-tetrahydrofurandiyl groups alternate with one another are novel. Novel are also such polymers in which at least part of the ethylene groups contain one alkyl substituent and/or in which at least part of the 2,5-tetrahydrofurandiyl groups contain an alkyl substituent in the 3-position. Such polymers can be obtained in a manner corresponding to that of the non-alkyl-substituted polymers, by applying the conversion to an alternating polyketone which was prepared from a monomer mixture which, in addition to carbon monoxide, contained one or more other α-olefins instead of or in combination with ethene. The present patent application therefore relates to novel polyketone related polymers characterized by consisting of linear chains in which units A and units B occur in alternating order and in which the units A are the same or different optionally monoalkyl-substituted ethylene groups and the units B are the same or different optionally 3-alkyl-substituted 2,5-tetrahydrofurandiyl groups. The patent application further relates to the preparation of these novel polymers. If at least part of the ethylene groups and/or at least part of the 2,5-tetrahydrofurandiyl groups from which the polymers of the invention are synthesized include alkyl substituents, the alkyl substituents are preferably methyl groups. Such polymers can be obtained by applying the conversion to an alternating polyketone prepared from a monomer mixture containing, in addition to carbon monoxide, propene or a mixture of ethene and propene. As described hereinbefore, the polymers of the invention can be prepared by contacting a linear polymer of carbon monoxide with one or more α-olefins, in which polymer units originating from carbon monoxide and units originating from the used α-olefins(s) alternate, with hydrogen, at an elevated temperature and pressure and in the presence of a catalyst composition comprising a solution of a complex ruthenium carbonyl compound and an iodide dissolved in an organic solvent. 2-Methoxyethanol has been found to be a very suitable organic solvent for the catalyst composition. The complex ruthenium carbonyl compound that is required for the catalytic conversion can be taken up in the organic solvent as such or it may be formed in situ, by taking up an other ruthenium compound, such as ruthenium (acetyl acetonate)₃, in the solvent and carrying out the conversion of the alternating carbon monoxide/α-olefin copolymer in an atmosphere containing carbon monoxide in addition to hydrogen. Methyl iodide has been found to be a very suitable iodide component in the catalyst composition. Besides the complex ruthenium carbonyl compound and the iodide, further components, such as hydrogenation promoters and dehydration promoters, may be included in the catalyst solution. An example of a suitable hydrogenation promoter is triphenyl phosphineoxide and an example of a suitable dehydration promoter is acetic acid. The preparation of the polymers of the invention by employing the ruthenium-containing catalyst compositions described hereinbefore is preferably carried out at a temperature of from 75 to 200°C and a hydrogen pressure of from 5 to 200 bar. The polymers of the invention are preferably prepared starting from an alternating polymer of carbon monoxide with one or more α-olefins, which polymer has been obtained by polymerizing the monomers using a catalyst composition based upon the components a), b) and c) mentioned hereinbefore. This polymerization is preferably carried out by contacting a mixture of carbon monoxide and one of more α-olefins at a temperature of from 40 to 120°C, an overall pressure of from 20 to 150 bar and an α-olefin/carbon monoxide partial pressure ratio of from 0.5 to 5 with a solution of a catalyst composition in a diluent in which the polymers are insoluble or virtually insoluble, which catalyst composition is based upon a) a palladium salt of a carboxylic acid, b) an anion of an acid with a pKa of less than 2 in a quantity of 0.5-50 mol per mol palladium, and c) a bisphosphine of the general formula (R₁)₂P-R-P(R₁)₂, in which R₁ represents a phenyl group containing one or more alkoxy substituents at least one of which occupies an ortho position relative to the phosphorus atom, and in which R is a bivalent organic bridging group containing three atoms in the brigde at least two of which are carbon atoms, in a quantity of from 0.5 to 2 mol per mol palladium, the quantity of catalyst composition used per mol of α-olefin to be polymerized being such as to contain 10⁻⁷ to 10⁻³ mol palladium. Special preference is given to polymerization in which a mixture of carbon monoxide with ethene or ethene and propene is contacted at a temperature of from 50 to 100°C, an overall pressure of from 30 to 100 bar and an α-olefin/carbon monoxide partial pressure ratio of from 0.6 to 3.5, with a solution of a catalyst composition in methanol, which catalyst composition is based upon a) palladium acetate, b) trifluoroacetic acid in a quantity of from 1 to 25 mol per mol palladium, and c) 1,3-bis[bis(2-methoxyphenyl)phosphino]propane in a quantity of from 0.75 to 1.5 mol per mol palladium, and in which such a quantity of catalyst composition per mol of α-olefin to be polymerized is used as to contain 10⁻⁶ to 10⁻⁴ mol palladium. The invention will now be illustrated with the aid of the following examples. Example 1 A carbon monoxide/ethene copolymer was prepared as follows. A mechanically stirred autoclave having a volume of 4 l was charged with 2 l methanol. After the contents of the autoclave were brought to 65°C, ethene and carbon monoxide were pressed in to respective partial pressures of 18 and 36 bar. Subsequently, a catalyst solution was introduced into the autoclave which comprised 18 ml methanol, 0.03 mmol palladium acetate, 0.06 mmol para-toluenesulphonic acid, and 0.03 mmol 2-methyl,2-(diphenylphosphinomethyl)-1,3-bis(diphenylphosphino)propane. The pressure was kept at 55 bar by pressing in a 1:1 carbon monoxide/ethene mixture. After 10 hours, polymerization was terminated by cooling down to room temperature and releasing the pressure. The polymer was filtered off, washed with methanol and dried at 70°C. The product was 96 g copolymer. The polymerization rate was 3200 g copolymer/g palladium.hour. With the aid of ¹³C-NMR analysis it was established that the copolymer consisted of linear chains in which units -(CO)- and units -(C₂H₄)- occurred in alternating order. Example 2 A mechanically stirred autoclave with a volume of 300 ml was charged with 100 ml 2-methoxyethanol. Herein were consecutively suspended 10 g of a catalyst comprising 50% nickel supported on a carrier, and 10 g of the carbon monoxide/ethene copolymer prepared as described in Example 1. The autoclave was flushed with nitrogen, after which hydrogen was pressed in to a pressure of 50 bar. The contents of the autoclave were brought to 200°C. After 16 hours, the reaction mixture was cooled down to room temperature and the pressure was released. After filtration of the reaction mixture to remove the catalyst and unconverted carbon monoxide/ethene copolymer, water was added to the filtrate, allowing 6 g of polymer to precipitate in the form of a white dust. For further analysis, the polymer was dissolved in hexafluoroisopropanol. As shown by ¹³C-NMR analysis of this solution, the polymer obtained contained no carbonyl groups. It was further found that the product was formed of a complex mixture of polymeric structures in which the alternating character of the starting material had been lost entirely. In the product, the presence, inter alia, of alcohol groups, ether groups and polymethylene groups was established. Example 3 Example 2 was substantially repeated, but with the following differences a) 100 ml of ortho-cresol instead of 2-methoxyethanol was introduced into the autoclave and herein, first of all, 10 g polymer was dissolved and next, 10 g copper chromite catalyst was suspended, and b) after filtration of the reaction mixture, the polymer was precipitated with methanol. As shown by ¹³C-NMR analysis of the product, no significant degree of hydrogenation had taken place. Example 4 Example 2 was substantially repeated, the difference being that a cobalt phosphine complex was used as the catalyst that was soluble in the reaction medium. It was established by analysis that no reaction had taken place. Example 5 A stirred autoclave having a volume of 300 ml was charged with 100 ml 2-methoxyethanol. Into this, 10 g of the carbon monoxide/ethene copolymer prepared as described in Example 1 was introduced. Then, a catalyst solution was added which comprised 10 ml acetic acid, 0.2 g ruthenium(acetyl acetonate)₃, 0.2 g triphenyl phosphineoxide, and 1 ml methyl iodide. The autoclave was degassed with nitrogen and subsequently carbon monoxide and hydrogen were pressed in, to partial pressures of 15 bar and 40 bar, respectively. The contents of the autoclave were brought to 150°C. After 4 hours, the reaction mixture was cooled down to room temperature and the pressure was released. The reaction product which was obtained in the form of a viscous oil was extracted with methanol in order to remove solvent and catalyst. Drying of the extraced reaction product afforded a hard glassy material in a yield of 90%, calculated on the starting carbon monoxide/ethene copolymer. With the aid of ¹³C-NMR analysis, combined with elementary analysis, it was established that the product obtained was a polymer consisting of linear chains in which ethylene units and 2,5-tetrahydrofurandiyl units occurred in alternating order. Of Examples 1-5, Example 5 is in accordance with the invention. Example 1 describes the preparation of an alternating copolymer of carbon monoxide and ethene. Examples 2-4 relate to hydrogenation experiments and fall outside the scope of the invention. They have been included in the patent application for comparison.

Claims: Polyketone related polymers, characterized in that they consist of linear chains in which units A and units B occur in alternating order and that the units A, being the same or different, are ethylene groups which optionally carry mono-alkyl-substituents and that the units B, being the same or different, are 2,5-tetrahydrofurandiyl groups which optionally carry 3-alkyl-substituents. Polymers as claimed in claim 1, characterized in that if at least part of the ethylene groups and/or at least part of the 2,5-tetrahydrofurandiyl groups include alkyl substituents, these alkyl substituents are methyl groups. Process for the preparation of polymers as claimed in claim 1, characterized in that a linear polymer of carbon monoxide with one or more α-olefins, in which polymer units originating from carbon monoxide and units originating from the used α-olefin(s) alternate, is contacted with hydrogen at an elevated temperature and pressure and in the presence of a catalyst composition comprising a solution of a complex ruthenium carbonyl compound and an iodide dissolved in an organic solvent. A process as claimed in claim 3, characterized in that the complex ruthenium carbonyl compound required for the catalytic conversion of the carbon monoxide/α-olefin polymer is formed in situ by taking up an other ruthenium compound, such as ruthenium(acetyl acetonate)₃, in the solvent and carrying out the conversion in an atmosphere containing carbon monoxide in addition to hydrogen. A process as claimed in claim 3 or 4, characterized in that the iodide component used in the catalyst composition is methyl iodide. A process as claimed in one or more of claims 3-5, characterized in that, in addition, the catalyst composition comprises a hydrogenation promoter, such as triphenyl phosphine oxide and/or a dehydration promoter, such as acetic acid. Process as claimed in one or more of claims 3-6, characterized in that it is carried out at a temperature of from 75 to 200°C and a hydrogen pressure of from 5 to 200 bar.

Inventors: VAN BROEKHOVEN JOHANNES ADRIAN, VAN BROEKHOVEN, JOHANNES ADRIANUS MARIA
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1989
Main classification: C08G67
IPC codes: C08G65, C08G67