Semiconductor device

Abstract: A semiconductor device includes a semiconductor substrate, a pair of low breakdown voltage elements formed in the substrate so as to be adjacent to each other, and a high breakdown voltage element formed to be adjacent to one of the low breakdown voltage elements. The pair of low breakdown voltage elements are isolated from each other by a pn junction and the one of the low breakdown voltage elements and the high breakdown voltage element are isolated from each other by a dielectric material. The semiconductor substrate is a composite substrate formed by directly bonding a first substrate serving as an element region to a second substrate serving as a supporting member through an insulating film.

Description: The present invention relates to a semiconductor device having a high breakdown voltage element and a low breakdown voltage element formed in a single substrate. Pn junction isolation and dielectric isolation are known as isolation techniques for semiconductor integrated circuits. Dielectric isolation is preferably employed to isolate a high breakdown voltage element used for large current switching from other elements so as to ensure reliable electrical isolation. When a high breakdown voltage element and a plurality of low breakdown voltage elements, such as bipolar transistors, constituting a control circuit for the high breakdown voltage element are integrated, dielectric isolation is preferably employed to prevent the low breakdown voltage elements from being electrically influenced by the high breakdown voltage element, e.g., prevent mixing of noise in the bipolar transistors due to large current switching. Generally, therefore, in a conventional integrated circuit using such dielectric isolation, a plurality of low breakdown voltage elements are respectively formed in different island regions isolated by a dielectric material in a substrate. The publication : OHATA YET AL: 'Dielectrically isolated intelligent power switch'. PROCEEDINGS OF THE IEEE 1987 CUSTOM INTEGRATED CIRCUITS CONFERENCE (CAT. NO.87CH2430-7), PORTLAND, OR, USA, 4-7 MAY 1987, 1987, NEW YORK, NY, USA, IEEE, USA, PAGE(S) 443 - 446 discloses a dielectrically isolated intelligent power switch which uses trench isolation between a power MOSFET and bipolar/CMOS devices. A structure wherein all the elements are isolated from each other by a dielectric material in such a manner is not preferable in terms of integration density, because dielectric isolation requires a larger area than pn junction isolation. As described above, if the structure wherein all the elements are isolated by a dielectric material is employed in an integrated circuit having high and low breakdown voltage elements formed in a single substrate, an increase in integration density is limited. It is an object of the present invention to provide a semiconductor device in which a decrease in integration density due to isolation is prevented when high and low breakdown voltage elements are integrally formed on a single substrate. According to the present invention, there is provided: a semiconductor device, comprising: a semiconductor substrate; a plurality of low breakdown voltage elements formed on said substrate so as to be adjacent to each other; and a high breakdown voltage element formed to be adjacent to one of said low breakdown voltage elements, wherein said plurality of low breakdown voltage elements are isolated from each other by a pn junction and one of said low breakdown voltage elements and said high breakdown voltage element are isolated from each other, characterized in that said semiconductor substrate is a composite substrate comprising a first substrate of a p-type serving as an element region bonded to a second substrate serving as a supporting member with a first insulating film interposed therebetween, wherein said first substrate is divided into first and second island regions which are isolated from each other by an isolating layer covering an inner surface of a trench reaching the first insulating film, said trench having a semiconductor material buried therein, said high breakdown voltage element is a lateral insulated gate bipolar transistor formed in said first island region, said low breakdown voltage elements are bipolar transistors or bipolar transistors and complementary MOS transistors formed in said second island region. In the semiconductor device of the present invention, a composite substrate formed by directly bonding a first substrate serving as an element region a second substrate serving as a supporting member with an insulating film interposed therebetween is used as the semiconductor substrate. In this case, the second substrate is of a first conductivity type having a low impurity concentration and is divided into a plurality of island regions which are isolated from each other by an isolating layer formed by burying a dielectric material in a trench. The high breakdown voltage element is formed in one island region, whereas the low breakdown voltage elements are formed in the other island region. The low breakdown voltage elements are isolated from each other by a pn junction. The composite semiconductor substrate may be manufactured by a method comprising the steps of mirror-polishing one surface of each of first semiconductor substrate of a first conductivity type and second semiconductor substrate, forming a first impurity region of the first conductivity type in the mirror-polished surface of the first semiconductor substrate, forming a first insulating film on at least one of a surface of the first impurity region and the mirror-polished surface of the second semiconductor substrate, forming a composite substrate by directly bonding the mirror-polished surface of the first semiconductor substrate to the mirror-polished surface of the second substrate, forming at least one groove by selectively etching a portion of the first semiconductor substrate of the composite substrate, forming second impurity regions by diffusing an impurity in side walls of a plurality of semiconductor layers which are isolated from each other by the groove, forming a second insulating film in surfaces of the second impurity regions, forming the IGBT in one of the semiconductor layers, and forming a plurality of low breakdown voltage elements which are isolated from each other by a pn junction in the other one of the semiconductor layers. Furthermore, the device may be manufactured by a method comprising the steps of mirror-polishing one surface of each of first semiconductor substrate of a first conductivity type and second semiconductor substrate, forming a first impurity region of the first conductivity type in the mirror-polished surface of the first semiconductor substrate, forming a first insulating film on at least one of a surface of the first impurity region and the mirror-polished surface of the second semiconductor substrate, forming a composite substrate by directly bonding the mirror-polished surface of the first semiconductor substrate to the mirror-polished surface of the second substrate, forming a first groove which reaches the insulating film and a plurality of second grooves which do not reach the first impurity region by selectively etching a portion of the first semiconductor substrate of the composite substrate, the first substrate being divided into a first semiconductor region and a second semiconductor region having the second trench which are isolated from each other by the first trench, forming second impurity region by diffusing an impurity in side walls of the first trench, forming a second insulating film on a surface of the second impurity region in the first groove, burying a dielectric material and semiconductor material layer in the first groove and the second grooves, respectively, forming the IGBT in the first semiconductor region, and forming the low breakdown voltage elements which are isolated from each other by a pn junction in the semiconductor material layers. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: Fig. 1 is a sectional view of a semiconductor device according to one embodiment of the present invention; Figs. 2A to 2G are sectional views showing the steps in manufacturing the semiconductor device in Fig. 1; Fig. 3 is a sectional view of a semiconductor device in which a formation region of low breakdown voltage elements is formed by impurity diffusion; Figs. 4 to 7 are sectional views of semiconductor devices in which an arrangement of low breakdown voltage elements is variously changed; Fig. 8 is a sectional view of a semiconductor device in which a space is formed in a part of a bonding interface of a substrate; Fig. 9 is a sectional view of a semiconductor device in which a formation region of low breakdown voltage elements is formed simultaneously with formation of a trench for isolation; Figs. 10A to 10G are sectional views showing the steps in manufacturing the semiconductor device in Fig. 9; Figs. 11 and 12 are sectional views of semiconductor devices as modifications of the device in Fig. 11; and Figs. 13A to 13C are sectional views for explaining a modification of the present invention. Preferred embodiments will be described below with reference to the accompanying drawings. Fig. 1 is a sectional view of a semiconductor device according to an embodiment of the present invention. In this semiconductor device, lateral i nsulated g ate b ipolar t ransistor (IGBT) T1 as a high breakdown voltage element, and a plurality of bipolar transistors (Fig. 1 shows two transistors, i.e., pnp and npn transistors T2 and T3) as a plurality of low breakdown voltage elements used for a control circuit of transistor T1 are integrally formed. More specifically, a plurality of p - -type Si layers 4a and 4b which are isolated from each other in island forms by SiO 2 layers 3a and 3b are formed in Si substrate 4 on Si substrate 1. IGBT T1 is formed in one Si layer, i.e. layer 4a, whereas pnp and npn transistors T2 and T3 which are isolated from each other by pn junction isolation are formed in the other Si layer, i.e., layer 4b. This process will be described in detail in accordance with practical manufacturing steps. Figs. 2A to 2G show the manufacturing steps. First, two Si substrates 1 and 4 are prepared. One surface of each of Si substrates is mirror-polished. One substrate, i.e., Si substrate (first semiconductor substrate) 4 is a p - -type substrate for element formation, and has a resistivity of 70 to 100 Ω·cm. After p + -type layer 6a is formed in the mirror-polished surface of substrate 4 by diffusing boron at a high concentration, SiO 2 film 3a having a thickness of about 1 µm is formed on the surface of the resultant structure. The other substrate, i.e., Si substrate (second semiconductor substrate) 1 may be of p- or n-type, and has no limitation as to specific resistivity. Such two substrates 1 and 4 are bonded to each other by a silicon wafer direct-bonding technique. Then, a surface of substrate 4, which is opposite to the bonding surface, is polished to obtain p - -type Si layer 4 having a thickness of about 60 µm (Fig. 2B). SiO 2 film 3a is used for element isolation. It has been confirmed from experiments performed by the present inventors that in order to reduce warpage of the resultant wafer, SiO 2 film 3a must be formed on element formation substrate 4 in advance, and that bonding interface 2 must face the upper surface of SiO 2 film 3a which is formed on element formation substrate 4 in advance. The steps of practical direct bonding are performed in the following manner. Substrates to be bonded are cleaned by an H 2 SO 4 -H 2 O 2 mixture solution, HCl-H 2 O 2 mixture solution, aqua regia, or the like. Subsequently, the substrates are cleaned by water for about ten minutes, and are dried by a spin dryer or the like. The substrates subjected to these processes are set in a clean atmosphere below, e.g., class 100, and their mirror-polished surfaces are bonded to each other in a state wherein substantially no contaminant is present therebetween. With this process, the two substrates are bonded to each other with a certain strength. When the substrates bonded to each other in this manner are subjected to heat-treatment in a diffusion furnace or the like, bonding strength is increased, and the two substrates are completely bonded. An increase in bonding strength is observed at about 200°C or more, preferably at 800 to 1200°C. No special attention need be paid to the atmosphere for the heat-treatment process. For example, heat-treatment can be performed in an oxygen, nitrogen, hydrogen, inert gas, steam, or a gas mixture thereof. In the embodiment, cleaning was performed by an H 2 SO 4 -H 2 O 2 mixture solution and an HCl-H 2 O 2 mixture solution, and heat-treatment was performed a nitrogen atmosphere including a small amount of oxygen at 1,100°C for two hours. Subsequently, the surface of Si substrate 4 is lapped and polished to reduce the thickness. And, SiO 2 film 31 is formed on the upper surface of Si substrate 4. Tapered isolation trench 32 is then formed by etching, e.g., anisotropic etching Si layer 4 to a depth reaching SiO 2 film 3a using pattern 31a obtained by patterning SiO 2 film 31 as a mask. With this process, Si layers 4a and 4b are isolated in the forms of islands (Fig. 2C). Boron is diffused in isolation trench 32 by diffusion so as to form p + -type layers 6b in the side walls of island Si layers 4a and 4b. P + -type layers 6b are integrated with p + -type layer 6a on the bottom of the isolation trench so as to constitute p + -type layer 6. SiO 2 film 3b is formed in the side wall of each Si layer 4 by another thermal oxidation of the side wall. Then, SiO 2 film 31 on the surface of Si layer 4b on the low breakdown voltage element side is patterned to form pattern 31a. Si layer 4 is etched by using pattern 31a as an etching mask to form recesses in the element region. Phosphorus or antimony is introduced in the recesses at a high concentration by diffusion to form n + -type layers 21a and 21b (Fig. 2D). Subsequently, SiO 2 film 31b on the surface of Si layer 4b in which the recesses are formed is removed, and epitaxial growth of Si is performed to form high-resistance n - -type layer 22. At the same time, polysilicon layer 5 is formed on SiO 2 film 31a on the isolation region covered with SiO 2 film 3b and on the other Si layer, i.e., layer 4a (Fig. 2E). The growth layer surface is then lapped and polished so that the thickness of substrate 4 is 20 to 100 µm, and n - -type layers 22a and 22b are buried in the recesses to obtain a flat state wherein polysilicon film 5 is buried in the isolation trench (Fig. 2F). Since n - -type layer 22 is buried only in the recesses and other portions thereof are removed, only portions of SiO 2 film 31b overhanging in the recesses need be theoretically removed when the epitaxial growth process in Fig. 2E is performed. However, if crystal growth is performed while SiO 2 film 31b is locally left, a high-quality single crystal cannot be buried, and hence defects are often caused. In order to decrease the defects, SiO 2 film 31b on the surface of Si layer 4b is preferably removed substantially entirely in crystal growth, as described above. Pnp transistor T2 and npn transistor T3 which are isolated from each other by a pn junction isolation are respectively formed in n - -type layers 22a and 22b buried in this manner. More specifically, p-type layers 23 and 24 are formed in the surface region of n - -type 22a at a predetermined interval. Thereafter, collector, emitter, and base electrodes 27a, 28a, and 29a are formed. As a result, lateral type pnp transistor T2 having n - -type layer 22a serving as a base, and p-type layers 23 and 24 respectively serving as a collector and a emitter is formed. p-type layer 25 is formed in the surface region of n-type layer 22b by impurity diffusion. In addition, n-type layer 26 is formed in the surface region of p-type layer 25. Then, collector, emitter, and base electrodes 27b, 28b, and 29b are formed to form vertical type npn transistor T3 having n - -type layer 22b as a collector, p-type layer 26 as a base, and n-type layer 26 as an emitter. Subsequently, in p - -type Si layer 4a, p-type base layer 7 is formed in its peripheral portion, n-type source layer 8 is formed therein, n-type base layer 9 is formed in its central portion, and p-type drain layer 11 is formed therein by impurity diffusion. N - -type layer 10 serving as a guard ring is formed around n-type base layer 11 by impurity diffusion. Gate electrode 13 is formed on a region between n-type source layer 8 and n - -type layer 10 with gate insulating film 12 interposed therebetween. Then, drain electrode 15 is formed on p-type drain layer 11, and source electrode 14 is formed on n-type source layer 8 and p-type base layer 7 so as to be simultaneously in contact with layers 8 and 7, thereby obtaining IGBT-T1 (Fig. 2G). In the semiconductor device obtained in the above-described manner, high breakdown voltage IGBT-T1 processing a large current can be electrically isolated from low breakdown voltage transistors T2 and T3 operated by a small current with high reliability by a dielectric material. On the other hand, since transistors T2 and T3 are isolated from each other by a pn junction isolation, an extra area for element isolation is not required. Therefore, a high integration density can be realized. In the above embodiment, two bipolar transistors are integrated as low breakdown voltage elements. The present invention, however, exhibits a noticeable effect in terms of integration density especially when a large number of low breakdown voltage elements are integrated. Furthermore, in the above embodiment, high-concentration p + -type layers 6 are formed on the oxide film interfaces of the bottom and side walls of the p - -type layers isolated in the forms of islands, thereby obtaining high reliability. More specifically, many defects are normally present in an oxide film interface. If a depletion layer extending from an element formed in the device reaches this interface, leak, a decrease in breakdown voltage, or the like may be caused. However, formation of p + -type layers 6 can prevent the depletion layer from reaching the interface. Note that in the above embodiment, only one IGBT serving as a high breakdown voltage element is exemplified. However, a plurality of such elements may be integrally formed. In this case, the high breakdown voltage elements preferably have a dielectric isolation structure. The present invention is not limited to the above embodiment. Other embodiments will be described below. The same reference numerals in the drawings of the following embodiments denote the same parts as in the drawings of the previous embodiment, and a detailed description thereof will be omitted. Fig. 3 shows an embodiment wherein transistors T2 and T3 in Fig. 1 are modified. In this embodiment, n-type layers 33a and 33b respectively serving as a base layer and a collector layer of each of transistors T2 and T3 are formed by impurity diffusion. According to this embodiment, since a low-resistance n + -type buried layer such as shown in the previous embodiment is not formed, transistor characteristics are slightly inferior to those in the previous embodiment. However, since the steps of forming the recesses, crystal growth, etching, and the like upon formation of the dielectric isolation structure are omitted, the overall steps can be greatly simplified, thereby decreasing the manufacturing cost. Figs. 4 to 7 show embodiments wherein the arrangement of the bipolar transistor portions serving as low breakdown voltage elements is modified. In Fig.4, p - -type layer 46, n-type well 61, and p-type well are formed by impurity diffusion, and a collector, a base, and an emitter are sequentially formed in the respective wells by impurity diffusion, thereby forming pnp and npn transistors T2 and T3. In Fig.5, n- and p-type wells 61 and 62 are formed by diffusion, and hence lateral type pnp and npn transistors T2 and T3 are respectively formed therein. In Fig.6, p-type layer 81 is formed in p - -type layer 4b independently of p + -type layer 6 prior to substrate bonding so as to reduce the resistance. In Fig. 7, lateral type transistor T2a and vertical type transistor T2b are simultaneously integrated as pnp transistors. In the embodiments shown in Figs. 4 to 7, the same effects as in the previous embodiment can be obtained. Fig. 8 shows a structure of still another embodiment. In this embodiment, space 91 is formed at a position of bonding interface 2 below the IGBT-T1 region serving as the high breakdown voltage element in Fig. 1. This structure is obtained by forming oxide film 3a to a sufficient thickness by a process prior to bonding, etching oxide film 3a in the high breakdown voltage element region, forming thin oxide film 3c in the etched portion again, and performing bonding. With this structure, a breakdown voltage in a bottom portion of the high breakdown voltage element side can be further increased. Fig. 9 is a sectional view of a semiconductor device in which low breakdown voltage elements are formed in two wells having V-shaped sectional areas. In the above-described embodiments, the method of forming a trench and burying a semiconductor layer therein, and the method of impurity diffusion are described as methods of forming wells isolated by pn junction isolation. The method of forming trenches described with reference to Figs. 2A to 2G is performed independently of the selective etching process for forming island Si layers by isolation. In this embodiment, however, trenches are formed in the wells simultaneously with the selective etching process for isolation of the island Si layers. The trenches for isolating/forming the island layers must reach the bottom portions while the trenches in the well regions must not reach the bottom portions. Such conditions can be obtained by applying anisotropic etching capable of obtaining a predetermined taper angle to selective etching so as to select the size of an etching window. Figs. 10A to 10G are sectional views showing the steps in manufacturing the semiconductor device in Fig. 9. The steps shown in Figs. 10A and 10B are the same as those in Figs. 2A and 2B. Si layer 4a on the high breakdown voltage element side and Si layer 4b on the low breakdown voltage element side are isolated from each other by forming isolation trench 32 by selective etching. At the same time, trenches 32a and 32b are formed in the well regions on the low breakdown voltage element side (Fig. 10C). By selecting the size of a window of SiO 2 upon anisotropic etching, trench 32 of the isolation region can be caused to reach the bottom portion while trenches 32a and 32b in the well regions do not reach the bottom portions. Thereafter, n + -type layers 6c, 21a, and 21b are formed in the side walls of trenches 32, 32a, and 32b upon diffusion of phosphorus or arsenic by epitaxial diffusion (Fig. 10D). Similar to the embodiment shown in Figs. 2A to 2G, high-resistance n - -type Si layer 22 is formed by removing an oxide film on the low breakdown voltage element side and forming an Si layer by epitaxial growth. At the same time, polysilicon layer 5 is deposited on the high breakdown voltage element covered with the oxide film (Fig. 10E). Then, the grown layer is lapped, n - -type layers 22a and 22b serving as wells are buried in the respective recesses in Si layer 4, and polysilicon layer 5 is buried in the isolation trench (Fig. 10F). Thereafter, in an element forming process, IGBT-T1 is formed in Si layer 4a, and lateral type pnp transistor T2 and vertical type npn transistor T3 which are isolated from each other by a pn junction isolation are formed in Si layer 4b (Fig. 10G). According to this embodiment, since isolation of the island Si layers and formation of the recesses in the well formation regions in the Si layers can be performed in a single etching process, the overall process can be simplified. Fig. 11 shows an embodiment wherein the structure in Fig. 9 is slightly modified. In Fig. 9, p + -type layers 6a are formed in the bottom portions of Si layers 4a and 4b, and n + -type layers 6c are formed on the side walls of the isolation trench simultaneously with formation of the n + -type layers on the side surfaces of the well region trenches. In this embodiment, however, the p + -type layers are formed on the bottom and side walls of the island Si layers. Fig. 12 shows a structure of still another embodiment. In this embodiment, n- and p-channel MOS transistors T4 and T5 constituting a CMOS circuit together with bipolar transistors T2 and T3 are formed in Si layer 4b on the low breakdown voltage element side. Bipolar transistors T2 and T3 are formed such that n - -type layer 22a formed by epitaxial growth is divided into a plurality of regions which are isolated from each other by a pn junction isolation, and transistors T2 and T3 are respectively formed in the regions. MOS transistors T4 and T5 are respectively formed in p- and n-type layers 22c and 22b formed by impurity diffusion. In the embodiment shown in Figs. 2A to 2G, and also the embodiment shown in Figs. 10A to 10G, a p + -type layer and an n + -type layer are formed on the inner surface of trench 32 shown in Figs. 2C and 10D, and SiO 2 film 31, which has been used as the mask, is then removed by means or etching. When SiO 2 film 31 is removed away, SiO 2 film 3a is inevitably etched away from the bottom of trench 32 as is shown in Fig. 13A. At the same time, the side etching of SiO 2 film 3a also proceeds. Thereafter, as is shown in Fig. 13B, SiO 2 film 3b is formed on the inner surface of trench 32 by means of thermal oxidation. The thickness of SiO 2 film 3a is determined by the breakdown voltage which is required of the interface between two Si substrates 1 and 4. On the other hand, the thickness of SiO 2 film 3b is determined by the breakdown voltage which is required of the interface between island-shaped Si layers 4a and 4b. The breakdown voltage required of the interface between two Si substrates 1 and 4 is equal, in most cases, to that required of the interface between island-shaped Si layers 4a and 4b. Nonetheless, SiO 2 film 3b is thinner than SiO 2 film 3a since it is this SiO 2 film 3b that isolates island-shaped Si layers 4a and 4b from each other. Since SiO 2 film 3b is thinner than SiO 2 film 3a, SiO 2 film 3a is etched away from the bottom of trench 32 when SiO 2 film 31 is etched away. Consequently, SiO 2 film 3b formed on the bottom of trench 32 by thermal oxidation is thinner than SiO 2 film 3a. The side-etched portion of SiO 2 film 3a is particularly thin. SiO 2 film 3b formed on the bottom of trench 32, which is thin, is electrically weak, and fails to have a breakdown voltage as high as is desired. This problem can be solved by making SiO 2 film 3b, that is formed on the inner surface of trench 32, thicker than SiO 2 film 3a formed between two Si substrates 1 and 4. In fact, when SiO 2 film 3b was made 1.5 µm thick, whereas SiO 2 film 3a was made 1 um thick, as is shown in Fig. 13C, the breakdown voltage of the interface between Si substrates 1 and 4 was as high as 700 to 800V. By contrast, when SiO 2 film 3b was made 0.8 µm thick, while SiO 2 film 3a was made 1 um thick, the breakdown voltage of the interface between Si substrates 1 and 4 was only 500V to 600V. As has been described above, according to the present invention, in an integrated circuit in which high and low breakdown voltage elements coexist, a dielectric isolation structure and a pn junction isolation structure are combined so that the integration density can be sufficiently increased while influences of noise and the like due to large current switching are effectively prevented.

Claims: A semiconductor device, comprising: a semiconductor substrate; a plurality of low breakdown voltage elements (T2, T3, T4, T5) formed on said substrate so as to be adjacent to each other; and a high breakdown voltage element (T1) formed to be adjacent to one of said low breakdown voltage elements, wherein said plurality of low breakdown voltage elements (T2, T3, T4, T5) are isolated from each other by a pn junction and one of said low breakdown voltage elements (T2, T3, T4, T5) and said high breakdown voltage element (T1) are isolated from each other, characterized in that said semiconductor substrate is a composite substrate comprising a first substrate (4) of a p-type serving as an element region bonded to a second substrate (1) serving as a supporting member with a first insulating film (3a) interposed therebetween, wherein said first substrate (4) is divided into first and second island regions (4a, 4b) which are isolated from each other by an isolating layer (3b) covering an inner surface of a trench (32) reaching the first insulating film (3a), said trench having a semiconductor material (5), buried therein, said high breakdown voltage element (T1) is a lateral insulated gate bipolar transistor formed in said first island region (4a) and said low breakdown voltage elements are bipolar transistors (T2, T3) or bipolar transistors (T2, T3) and complementary MOS transistors (T4, T5) formed in said second island region (4b). A device according to claim 1, further characterised in that a space (91) is formed in a bonding interface (2) between said first island region (4a) and said second substrate (1). A device according to claim 1, wherein said semiconductor material which is buried in the trench is polycrystalline silicon (5).

Inventors: FURUKAWA KAZUYOSHI, NAKAGAWA AKIO, OGURA TSUNEO, FURUKAWA, KAZUYOSHI, NAKAGAWA, AKIO, OGURA, TSUNEO, Furukawa, Kazuyoshi, c/o Patent Div.K.K.Toshiba, Nakagawa, Akio, c/o Patent Div. K.K. Toshiba, Ogura, Tsuneo, c/o Patent Div. K.K. Toshiba
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1989
Main classification: H01L21
IPC codes: H01L27, H01L29, H01L21