MAGNETORESISTIVE READ TRANSDUCER

Abstract: In a magnetoresistive (MR) read transducer comprising a thin MR film (10) formed of ferromagnetic material and a thin nonmagnetic spacer film layer (14) in contact with the MR film, the spacer film (14) comprises a material selected from the group consisting of nichrome and nichrome with chromium oxide. To make such a transducer, a thin soft magnetic material film is deposited in contact with the spacer film so that a transverse bias is produced in at least a part of the MR film. The resistivity of the spacer film can be chosen by selecting the ratio of nichrome to chromium oxide in the spacer film. In a specific embodiment (Fig. 2) the spacer film (24) extends over only the central region of the MR film (10). Where the MR film consists of a nickel based alloy, a wet chemical etching process using an etchant comprising an aqueous solution of ceric ammonium nitrate and acetic acid can be used to pattern the spacer film.

Description: This invention relates to a magnetoresistive read transducer for reading information signals from a magnetic record medium. A known magnetoresistive (MR) transducer has been shown to be capable of reading data from a magnetic surface at great linear densities. An MR transducer detects magnetic field signals through the resistance changes of a read element made from a magnetoresistive material as a function of the amount and direction of magnetic flux being sensed by the element. It is also known that in order for an MR element to operate optimally, certain bias fields should be provided. In order to bias the MR element so that its response to a flux field is linear, a transverse bias field is generally provided. This bias field is normal to the plane of the magnetic media and parallel to the surface of the planar MR element. U.S.-A- 3,864,751 discloses an MR read transducer in which transverse bias is produced by a soft magnetic bias film which is spaced from the MR element by an insulating layer. The material disclosed for the insulating layer is silicon dioxide about 200 nm thick. U.S.-A- 3,814,863 and U.S.-A- 3,967,368 disclose an MR read transducer in which the MR element is in contact with a high resistivity non-magnetic shunt film, and the MR element is magnetically biased by a portion of the MR sense current being shunted through the non-magnetic layer. The preferred material for the shunt film is titanium, and chromium is mentioned as an unsuitable material for the shunt film. U.S.-A- 4,663,685 discloses an MR read transducer in which transverse bias is produced by a soft magnetic film which is spaced from the MR element by a non-magnetic spacer layer. The preferred material for the spacer layer is tantalum, but Al₂O₃ and SiO₂ could also be used. EP-A- 0265798 discloses an MR read transducer in which transverse bias is provided by a soft magnetic film which is spaced from the MR element in the central region only of the MR element. The preferred material for the spacer layer is tantalum. The MR sensors disclosed in the aforementioned US-A- 4663685 and EP-A- 0265798 can be made having operating parameters which have successfully met the requirements for magnetic recording systems up to the present. However, to further enhance the operating parameters, it would be desirable to more closely control the resistivity characteristics of the spacer layer in terms of resistivity stability, in terms of the ability to select a resistivity over a broad value range, and in terms of a spacer layer the processing steps of which are compatible with the processing steps utilized in fabricating an associated magnetic write head. This invention seeks to provide a magnetoresistive (MR) transducer which includes a nonmagnetic spacer layer in which the resistivity characteristics can be closely controlled. According to one aspect, the invention provides a magnetoresistive read transducer comprising a thin magnetoresistive film formed of ferromagnetic material, a thin spacer film in contact with the magnetoresistive film, and a thin soft magnetic material film in contact with the spacer film so that the soft magnetic material film is positioned parallel to but spaced from the magnetoresistive film whereby a transverse bias can be produced in at least a part of the magnetoresistive film to maintain that part of the magnetoresistive film in a linear response mode, the transducer being characterised by the thin spacer film comprising a material selected from the group consisting of nichrome and nichrome with chromium oxide. According to another aspect, the invention provides a method of making a magnetoresistive read transducer comprising the steps of depositing a thin magnetoresistive film formed of ferromagnetic material onto a substrate; depositing a thin spacer film in contact with the said magnetoresistive film, the spacer film comprising a material selected from the group consisting of nichrome and nichrome with chromium oxide; and depositing a thin soft magnetic material film in contact with the spacer film so that the soft magnetic material film is positioned parallel to but spaced from the magnetoresistive film whereby a transverse bias can be produced in at least a part of the said magnetoresistive film to maintain that part of the magnetoresistive film in a linear response mode. The resistivity of the spacer layer can be a specific value selected from a broad range of resistivity values by selecting the ratio of nichrome to chromium oxide in the spacer layer. In a specific embodiment, the spacer layer extends over only the central region of the MR region. In a further specific embodiment, the MR layer is a nickel based alloy, and the spacer layer is patterned by a wet chemical etching process by the use of an etchant comprising an aqueous solution of ceric ammonium nitrate and acetic acid. How the invention can be carried out will now be described by way of example, with reference to the accompanying drawings, in which:- Fig. 1 is an end view of a first magnetoresistive read transducer assembly embodying the invention; Fig. 2 is an end view of a second magnetoresistive read transducer embodying the invention; Fig. 3 is a graph of resistivity of the spacer layer as a function of the ratio of nichrome and chromium oxide in the spacer layer; and Fig. 4 is a diagram showing steps A through E of a process for making the magnetoresistive read transducer of Fig. 2. A magnetic read head (Fig. 1) comprises a magnetoresistive (MR) sensor 8, and transverse bias for MR sensor 8 is produced by a soft magnetic film layer 12 which is separated from an MR layer 10 by a thin nonmagnetic spacer layer 14 whose purpose is to prevent a magnetic exchange bias between the MR layer 10 and the soft magnetic bias film layer 12. A layer of antiferromagnetic material 16 is deposited in direct contact with MR layer 10 to provide longitudinal bias by means of exchange coupling across the interface between the MR layer 10 and the antiferromagnetic layer 16. Conductor leads 18, 20 are also included for connection to a sensing means (not shown) for sensing an output signal. The nonmagnetic spacer layer 14 should be of considerably higher resistivity than the magnetic films it separates, so as not to shunt current from the MR layer 10. The spacer layer 14 must also be compatible with the process for manufacturing the MR sensor, and this means that the spacer layer must be deposited in situ, sequentially with the MR layer 10 and the soft magnetic bias layer 12 without vacuum break. In addition the electrical and material properties of the spacer layer 14 must be stable not only during deposition but also during subsequent process steps involving annealing at higher temperatures. The subsequent processing steps should leave the resistivity of the spacer layer 14 and the magnetic properties of the adjacent films 10 and 12 unaffected. For example, the resistivity of the spacer layer 14 could change as a result of phase and microstructure changes, and the magnetic properties of the MR layer 10 and the soft magnetic bias layer 12 could change should there be any atomic diffusion of the spacer material into either of the adjacent magnetic films 10 and 12, which could in turn quench the magnetic moments of the MR layer 10 and the soft magnetic bias layer 12 and shift the bias point of the MR sensor structure. We have found that all of the above requirements are met by the use of nichrome (NiCr) or nichrome with chromium oxide additions (NiCrO x ) as the material for nonmagnetic spacer layer 14. The material of nichrome with chromium oxide additions is specified as (NiCrO x ) since, even though the starting material may comprise a hot pressed target having Ni₈₀Cr₂₀ and Cr₂O₃ in a chosen ratio, it is believed that the composition of the resulting film includes one or more sub-oxides of chromium rather than Cr₂O₃. In a specific embodiment, the MR layer comprises NiFe and the soft magnetic bias layer comprises NiFeRh and these films have an electrical resistivity (ρ) of about 25 and about 60µΩ-cm, respectively. The electrical resistivity of evaporated and sputtered nichrome films about 100 nm thick is of the order of 120 µΩ-cm, and this resistivity value is sufficiently high to be suitable for use as the spacer layer 14 between the two above-mentioned magnetic films. Higher values of ρ are even more desirable, and a feature of the present invention provides the ability to obtain a spacer layer 14 with ρ much higher than that of the magnetic films it separates. It has been found that deposition conditions can substantially affect the value of ρ as a result of the varying amounts of oxygen incorporated in the films and the formation of chromium oxides such as Cr₂O₃ during preparation. The composition of the nichrome appears to have a considerably lesser effect on ρ and the value is fairly constant within the range of about 20 to 80% Cr. Table I illustrates how the deposition conditions can substantially affect the value of ρ. This table shows that a Ni₈₀Cr₂₀ film about 100 nm thick has a ρ of about 100µΩ-cm, but a change in ρ by over an order of magnitude to about 1100µΩ-cm can be achieved by the addition of about 20% CrO x to the film. Effect of Cr-O on Nichrome Resistivity Composition (nm) Thickness Resistivity (µΩ-cm) Ni₈₀Cr₂₀ 100 100 +/- 20 Ni₈₀Cr₂₀) 0.8 (CrO x ) 0.2 100 1000 +/- 100 (Ni₈₀Cr₂₀) 0.2 (CrO x ) 0.8 100 100,000 +/- 10,000 To have increased flexibility in the design of MR sensors, it would be desirable to have a spacer layer the characteristics of which include the possibility of an adjustable resistivity to specific values within a broad range. We have found that this can be accomplished by choosing the amount of oxygen present during the deposition process and hence the concentration ratio of NiCr/Cr₂O₃. One way in which this can be done is by changing the target composition/purity. By employing vacuum cast and hot-pressed targets of various nichrome compositions, we were able to obtain films with dramatically varied resistivity values up to 1mΩ-cm. There are a number of ways in which the amount of oxygen present in the deposition process can be established so that sputtered films having high and highly specific resistivity can be produced. One way is by adjusting the sputtering target oxygen concentration. This can be conveniently accomplished by providing vacuum cast and hot-pressed targets having a specified ratio of Cr₂O₃, such as 10% to 80%, for example, to NiCr in the target. Targets with a range of 50% to 80% Cr₂O₃ were preferred in a specific application. Another way to establish the amount of oxygen present in the deposition process is by depositing the film in an appropriately oxygen-rich atmosphere. A further way to obtain this result is by dual-target co-sputtering with targets of high purity nichrome and Cr₂O₃. Fig. 3 shows a graph of the resistivity that can be achieved as a function of the concentration ratio of NiCr/CrO x . This graph shows the fraction that is proportional to the amount of CrO x that is present in the films as measured by Auger spectroscopy. An alternative embodiment of the invention will now be described briefly with reference to Fig. 2 which shows a magnetic read head comprising a magnetoresistive (MR) sensor 22 having an MR layer 10 which is formed of magnetic material, and a nonmagnetic spacer layer 24 covering only the central region 28 of the MR layer 10. A thin film of soft magnetic material 30 extends over and in contact with the end regions 32 of the MR layer 10 and in contact with the spacer layer 24 in the central region 28 so that the thin film of soft magnetic material 30 is separated from the MR layer 10 in the central region 28 but in contact with the MR layer 10 in the end regions 32. This structure makes it possible to provide transverse bias to the MR sensor in the central region only, where actual sensing of data is accomplished. Additional layers (not shown) for longitudinal bias and electrical leads may also be provided as in the embodiment of Fig. 1. In the embodiment of Fig. 2, the spacer layer 24 comprises nichrome (NiCr) or nichrome with chromium oxide additions (NiCrO x ). The electrical and materials properties of the spacer layer 24 are the same as those described in conjunction with the embodiment of Fig. 1. The preferred way of patterning the spacer layer 24 is by a wet chemical etching process. In cases where the adjacent MR layer 10 comprises a NiFe alloy, this creates a problem since an effective chemical etchant should have a highly differential etch rate between the material of the spacer layer 24 and that of the MR layer 10. Since both are Ni-base alloys, of similar composition (Ni₈₀₋₆₀Cr₂₀₋₄₀ and Ni₈₀Fe₂₀ respectively), such an etchant is difficult to find. However, one wet chemical etchant that offers an etch ratio of >200 comprises an aqueous solution of ceric ammonium nitrate and acetic acid (100 mL, 15 gr and 3.5 mL). This etching solution thoroughly dissolved nichrome films at an etch rate exceeding 90 nm per minute. This high etch rate holds for all the different nichrome compositions tried regardless of their ρ values. The ability to selectively etch the spacer layer 24 without attacking the underlying MR layer 10 significantly reduces the complexity of the manufacturing operation for the Fig. 2 embodiment of the MR sensor 22. The sequence for that manufacturing process is shown in steps A-E of Fig. 4. In step A of Fig. 4, the MR layer 10 and the spacer layer 24 are deposited as full films on a suitable substrate (not shown) by any suitable thin film deposition process. The preferred deposition process is sputtering. A suitable masking material such as a photoresist material 26 is deposited and patterned to the desired shape as shown in step B so that the spacer layer 24 is masked in the central region of the MR layer 10. The unmasked areas of spacer layer 24 are then removed as shown in step C by using a wet chemical etchant comprising an aqueous solution of ceric ammonium nitrate and acetic acid. The photoresist material 26 is then removed and the soft magnetic bias film 30 is then deposited by a sputtering process as shown in step D. The soft magnetic film 30 extends over the entire sensor so that it is in contact with the MR layer 10 in the end regions 32 and separated from the MR layer 10 in the central region 28 by the spacer layer 24. The MR sensor 22 is then formed as shown in step E by an appropriate etching process to shape the MR sensor 22 to the desired configuration. The use of nichrome or nichrome with chromium oxide additions as spacer materials in MR sensors permits considerable design and manufacturing improvements. This use also affords many materials and process advantages as well as added flexibility to design modification and extension.

Claims: A magnetoresistive read transducer comprising a thin magnetoresistive film (10) formed of ferromagnetic material, a thin spacer film (14; 24) in contact with the magnetoresistive film (10), and a thin soft magnetic material film (12; 30) in contact with the spacer film (14; 24) so that the soft magnetic material film (12; 30) is positioned parallel to but spaced from the magnetoresistive film (10) whereby a transverse bias can be produced in at least a part of the magnetoresistive film (10) to maintain that part of the magnetoresistive film (10) in a linear response mode, the transducer being characterised by the thin spacer film (14; 24) comprising a material selected from the group consisting of nichrome and nichrome with chromium oxide. A magnetoresistive read transducer as claimed in claim 1, wherein the resistivity of the material of the spacer film (14; 24) is established by selecting the ratio of nichrome to chromium oxide in the material. A magnetoresistive read transducer as claimed in claim 1 or claim 2, wherein the thin spacer film (24) extends over only the central region (28) of the magnetoresistive film. A method of making a magnetoresistive read transducer comprising the steps of: depositing a thin magnetoresistive film (10) formed of ferromagnetic material onto a substrate; depositing a thin spacer film (14; 24) in contact with the said magnetoresistive film, the spacer film (14; 24) comprising a material selected from the group consisting of nichrome and nichrome with chromium oxide; and depositing a thin soft magnetic material film (12; 30) in contact with the spacer film so that the soft magnetic material film (12; 30) is positioned parallel to but spaced from the magnetoresistive film (10) whereby a transverse bias can be produced in at least a part of the magnetoresistive film (10) to maintain that part of the magnetoresistive film (10) in a linear response mode. A method of making a magnetoresistive read transducer as claimed in claim 4, additionally comprising, prior to the step of depositing the thin soft magnetic material film (12; 30), patterning the thin spacer film (14; 24) so that it extends over only the central region of the magnetoresistive film (10). A method of making a magnetoresistive read transducer as claimed in claim 5, wherein the magnetoresistive film (10) comprises a nickel based alloy. A method of making a magnetoresistive read transducer as claimed in claim 6, wherein the patterning step is carried out by the use of a wet chemical etching process. A method of making a magnetoresistive read transducer as claimed in claim 7, wherein the wet chemical etching process is carried out by an etchant comprising an aqueous solution of ceric ammonium nitrate and acetic acid.

Inventors: FONTANA, ROBERT EDWARD JR., HOWARD, JAMES KENT, LEE, JAMES HSI-TANG, LEFAKIS, HARALAMBOS
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1989
Main classification: G11B5
IPC codes: G11B5