METHOD FOR PRODUCING A SLIDING MEMBER

Abstract: The slider consists of an injection molded product or polyethylene having a viscosity average molecular weight of 500,000-6,000,000. Slider has a low coefft. of friction and both excellent abrasion resisting characteristics and excellent characteristics of preventing another material from being worn out. @(81pp Dwg.No.0/11)

Description: The present invention relates to a method for producing a sliding member of synthetic resins and, more particularly, to a method for producing a tape guide used with magnetic tapes for VTR, sound recording and digital recording, and the like. Heretofore, various materials have been used for guides for movable systems for magnetic tapes such as VTR and cassette tapes. For instance, known organic materials involve polyoxymethylene (POM for short) which are used alone or in combination with a fluororesin and even silicone. Some plastic parts contain carbon so as to release charges generated by frictional contact with the surface of a tape, since plastics tend to be electrified. Known inorganic materials include metals and ceramics, while known metallic guides are formed of stainless materials or brass plated on its surface with nickel or chromium. Such guides as mentioned above operate in two manners, according to one of which they rotate in association with the travelling of a tape. According to another, they are fixed relative to the travelling of a tape. In most cases, the fixed type of metallic guides are used for portions through which a tape travels under relatively increased tape tension with increased changes in the direction of its movement. Some problems with such conventional guides originate from the properties of the materials used and some arise from the processing techniques applied. JP-A-59/120423 describes a process for the preparation of slidable sheets by blending uniformly ultra high molecular weight polyethylene powder with powdery graphite, pressing the blend to form a block, slicing the block into sheets and heat treating said sheets. JP-A-58/210929 describes a process for the preparation of sheets by moulding ultra high molecular weight polyethylene powder under increased pressure, cutting the block moulding into sheets, winding core material with the sheets, irradiating the sheets with radioactive rays and thereby crosslinking to such extent that the sheets have a gel content of 60 to 90%. JP-A-60/9723 describes a process for producing injection-moulded articles from raw materials to be made by adding an inorganic complex material to ultra-macromolecular weight polyethylene and pouring the molten raw materials into a cavity prior to commencement of thermal bridging, using an injection technique. US-A-4 489 033 describes a process for injection compression moulding ultra high molecular weight polyethylenes. Of noteworthy in connection with the materials used is that in view of the principles of friction or tribology, a material of larger momentum should basically be harder than its associated material of smaller momentum. In other words, a tape's material should fundamentally be harder than its associated guide. Under such conditions, the amount of abrasion is considered to be minimized. In view of tribology, however, the material used for the conventional guides is totally reversed in combination or not in ideal conditions at all. More specifically, the POM that is a polymeric material used for guides is much harder than PET that is a base film of magnetic tapes. In addition, stainless or chromium-plated brass materials used for fixed guides are harder than the POM. This implies that if guides become irregular even slightly on their surfaces, then magnetic tapes will be likely to be damaged. To avoid this problem, the surfaces of guides over which tapes travel, i.e., in contact with them, are now polished into mirror surfaces to increase the area of their surfaces in contact with the tapes, thereby applying local contact pressure to the tapes for the purpose of preventing the travelling resistance from increasing and so the surfaces of the tapes from being damaged. More illustratively, the guides are polished to such a surface roughness as expressed in terms of Rmax equal to or less than 0.1 µm. For the rotary guides, on the other hand, a roundness of 0.1 µm or below is required in addition to having such a surface roughness as mentioned. Thus, a problem with the conventional guides is that as a result of unavoidably making no account of the basic principles of tribology in view of some limitations placed on materials, it is required to increase their accuracy of processing to the highest level now achievable, leading to increases in product costs. In the case of the fixed type of guides in particular, it is still impossible to make them of plastics. Thus, metallic guides are still forcibly used even for cassette cases or decks, imposing considerable limitations on making them light, mass-producing them and cutting down their costs. As a result of various studies made by the present inventors so as to provide a solution to the above problems, it has now been found that a sliding material formed of a polyethylene resin having a relatively high molecular weight of the order of 500,000 to 6,000,000 can meet the basic principles of tribology, as already mentioned, and can be mass-produced at lower costs by making a high-molecular weight polyethylene injection-moldable, which has heretofore been considered difficult-to-mold. Such findings underlie the present invention. More specifically, the present invention provides a method for producing a sliding member as characterized by the embodiments in the claims. Figure 1 is a general view of a guide for magnetic tapes produced by the method of the present invention, Figure 2 is a sectional view showing part of a mold used in the present invention, Figures 3-4 and 6-8 each are a sectional view of an injection-molding machine used in the present invention, Figure 5 is a sectional view illustrating a jar for making an ultrahigh-molecular polyethylene used in the present invention composite, Figure 9 is a schematic view illustrating part of a sand slurry tester, Figure 10 is a graphical view showing the results of sand slurry testing, and Figure 11 is a graphical view showing the results of abrasion resistance testing. In what follows, the sliding member produced by the method of the present invention will be explained with reference to a guide for magnetic tapes as an example. Generally, the guide for guiding a magnetic tape produced by the method of the present invention is in such a form as illustrated in Fig. 1, e.g., in a cylindrical form of about 6 mm in outer diameter, about 4.85 mm in inner diameter and about 16 mm in length. This example is applicable to a 12,7 mm (1/2-inch) magnetic tape. It is to be understood, however, that the outer and inner diameters and length of guides may vary depending upon the width of tapes and even the structure of cassette cases. It is also understood that the guide is not limited to such a cylindrical form and may be in any form best-suited for tapes to pass over it. Basically, however, it is suitable that the guide is in a columnar form which may be of any desired section. The material used for the guide produced by the method of the present invention is a polyethylene having a molecular weight of 500,000 to 6,000,000 inclusive. A preferable molecular-weight range is between 600,000 and 2,000,000. As a result of the analysis of the results of tribological measurement of the surface of a polyester film that is a material of magnetic tapes and a polyethylene guide, the present inventors have now found that the polyethylene is worn down by the polyester in a molecular weight less than 500,000, whereas the polyester film is worn down in a molecular weight higher than 6,000,000. In other words, if the molecular weight is in the above-defined range, then it is possible to obtain a guide which successfully meets three requirements of (a) having a reduced coefficient of friction, (b) having increased abrasion resistance and (c) reducing the abrasion of an associated member (e.g., a polyester film) in a well-harmonized state. Usually, sliding members such as guides pose an electrification problem due to friction in addition to such friction and abrasion problems as mentioned above. Explaining this referring to the above example, the polarization of charges takes place on the surfaces of both the polyethylene and the associated polyester, since they are independently good insulators. For that reason, attraction by charge occurs between the polyester film and the polyethylene guide, actually leading to a phenomenon that the film sticks to the guide. This problem is effectively solved by the incorporation of suitable additives. More illustratively, this is achievable by making polyethylene composite with electrically conductive materials such as carbon, gold, silver, aluminium, copper, chromium, nickel, iron, lead, molybdenum, zinc, tin, indium, bismuth, platinum, selenium, magnesium, manganese, cobalt, tungsten, titanium, germanium, mercury and so on. In view of economical considerations and electrical properties, particular preference is given to carbon, silver, gold, aluminium, copper, iron, zinc and nickel which may be used alone or in combination of two or more. The electrically conductive materials should be added in an amount of preferably 0.1 to 20% by weight, more preferably 1 to 8% by weight. More preferably, organic additives may be added in order to improve the sliding properties of the polyethylene guide with respect to the associated polyester film. Detailed experimentation has revealed that the addition of a hydrocarbonaceous oligomer having a number-average molecular weight of 400 to 4000, e.g., ethylene-α-olefin oligomer is much more effective for improvements in the sliding properties. The amount of the hydrocarbonaceous oligomer added should be in a range of 0.1 to 20% by weight, preferably 3 to 10% by weight. It is noted that the organic material to be added to polyethylene is not limited to one type. Much more improved sliding properties are obtainable by the addition of any organic materials in combination of two or more depending upon what properties are required for the travelling of tapes. As an example, a combination of a polyethylene having an ultrahigh-molecular weight higher than 2,000,000 with additives, say, 5% by weight of carbon, 1% by weight of polyethylene wax and 5% by weight of a hydrocarbonaceous oligomer provides sliding properties fit for a guide for conventional VTR tapes. Another example of the organic additives according to the present invention is a surface active agent based on fluorine. The fluorine base surfactants may include anionic ones such as ammonium salts of perfluoroalkyl sulfonic acids, potassium salts of perfluoroalkyl sulfonic acids and potassium salts of perfluoroalkyl carboxylic acids; cationic ones such as iodides of perfluoroalkyl quaternary ammonium; and nonionic ones such as perfluroalkyl polyoxyethylene ethanol and fluoroalkyl esters. They are all effective for improvements in the sliding properties between the polyester film and the polyethylene. Among others, the anionic surfactants based on fluorine are most effective, probably because of the anionic, cationic and nonionic systems, the anionic ones are so low in the compatibility in polyethylene that they can bleed out onto the surfaces of molded pieces even in slight amounts. The fluorine base surfactants should be added in an amount of preferably 0.01 to 5% by weight, more preferably 0.1 to 1% by weight. For their uniform dispersion at the time of mixing, it is desired that said fluorine base surfactants, either in powdery forms or in viscous liquid forms, be dissolved in and diluted to a low concentration with an organic solvent which can be evaporated off at relatively low temperatures and in which they are soluble such as, for instance, methanol, ethanol, isopropyl alcohol, acetone and methyl ethyl ketone. The resulting solution is further atomized with a spray at the time of mixing, thereby making it possible to disperse it uniformly throughout polyethylene. It is noted that the organic material to be added to polyethylene is not limited to one type. Much more improved sliding properties are obtainable by the addition of any organic materials in combination of two or more depending upon what properties are required for the passing of tapes. As an example, a combination of a polyethylene having an ultra high-molecular weight higher than 2,000,000 with additives, say, 5% by weight of carbon, 5% by weight of the hydrocarbonaceous oligomer and 0.2% by weight of the anionic fluorine base surfactant provides sliding properties fit for a guide for conventional VTR tapes. Still another example of the organic additives according to the present invention is finely divided tetrafluoroethylene or a fluororesin having a mean particle size of 5 to 20 µm, which is again found to be most effective for improvements in sliding properties. The fluororesin powders should be added in an amount of preferably 0.1 to 50% by weight, more preferably 5 to 25% by weight. It is noted that the organic material to be added to polyethylene is not limited to one type. Much more improved sliding properties are obtainable by the addition of any organic materials in combination of two or more depending upon what properties are required for the passing of tapes. As an example, a combination of a polyethylene having an ultrahigh-molecular weight higher than 2,000,000 with additives, say, 5% by weight of carbon, 5% by weight of the hydrocarbonaceous oligomer and 15% by weight of the fluororesin powders having a mean particle size of 13 µm provides sliding properties fit for a guide for conventional VTR tapes. Under the conditions under which guides are to be used, improvements in heat resistance and rigidity may be taken in account. Polyethylene may then be made composite with not only the above electrically conductive materials but also ceramic materials. The ceramic materials used may include those based on aluminium oxide, zirconia, calcium, silicone, silicon and so on. Polyethylene made composite with short carbon and Kepler fibers, etc. may again be effective. These materials should be added in an amount of 0.1 to 20% by weight, preferably 1 to 10% by weight. For how to make the above electrically conductive and reinforcing materials composite with polyethylene, there is used a system in which they are fast agitated together at a temperature just below the melting temperature of the polyethylene resin employed to make use of the heat generated by the friction between the resin and the additives. Stirring is carried out in an inert gas atmosphere to avoid a reduction in the molecular weight of the polyethylene by its oxidation. It is suitable that the polyethylene resin used has a particle size of 10 to 300 µm, preferably 50 to 200 µm, whereas the additives used have a particle size of 0.01 to 100 µm, preferably 0.05 to 10 µm. The powders of the polyethylene and additives are first agitated at high speeds in an inert gas. Stirring is carried out at an initial chamber temperature of 60°C, while rotating an agitating blade at 100 to 10,000 rpm, preferably 300 to 3,000 rpm, and is then continued until a temperature of 80 to 120°C is reached by frictional heat generation. According to the findings of the present inventors, the additives adhere closely to the surfaces of the polyethylene particles under the above conditions, so that improvements can be introduced in electrical conductivity and strength even in small amounts at the time of mixing. One means for meeting the above conditions is preferably a Henschel mixer. Processing the thus treated polyethylene resin into a guide form is achieved by using the injection-molding technique provided by the invention of the present inventors, which will be described later. For molds for obtaining the molded guides produced by the method of the present invention, use may be made of vacuum/compression molds to be described later. One typical basic structure of the mold used, which will be described in detail, is shown in Figure 2, wherein reference numeral 51 stands for a core pin, 52 a sleeve (for an ejector), 53 a cavity, 54 a cavity plate, 55 a seal ring, 56 a secondary sprue, 57 a film gate and 58 a molded piece or part. As an example, the molded piece is in the form of such a cylindrical guide as depicted in Figure 1. The cavity space, in which the composite polyethylene resin according to the present invention is to be filled, is vacuumized through a parting line of the mold. For vacuumization, a vacuum pump is used, which connects with a pipeline arranged externally of the mold. After filling, the resin is compressed by moving the sleeve 52 horizontally (on the drawing). Effectively, the sleeve 52 is actuated just after the resin is allowed to dwell under pressure following its filling in the mold cavity. Driving is effected by a hydraulic or pneumatic cylinder with the aid of an electric motor, etc. Reasonably, an actuation signal is outputted from the sequence of an injection-molding machine. The temperature of the mold is in a range of preferably 40-100°C, more preferably 60-90°C. The conditions for injection molding may basically follow the above molding conditions. In the case of the composite polyethylene, it is noted that a compression ratio at the screw of 1.1-1.6 gives satisfactory molded pieces and brings about stable plasticization. It is also noted that the lower the cylinder temperature of a feeder zone, which is to be preferably brought down by fan-induced forced cooling, the lower the molecular weight of the obtained molded pieces. The above polyethylene guide produced by the method of the present invention is advantageous over the conventional metallic guides in the following points. (1) In principle, the metallic guides cost twice as much as the resinous guide according to the present invention, because their production involves important steps of pipe cutting, mirror finish and plating. (2) In the case of the metallic guides, their surfaces to slide over an associated tape member should have a surface roughness or Rmax of 0.1 µm or below. With the resinous guide according to the present invention, however, sufficient effects are obtainable even when its sliding surface has a roughness-after-finished or Rmax on the order of 2-5 µm, partly because of being consistent with the theory of tribology. Moreover, no special technique is needed for making molds. (3) The resinous guide produced by the method of the present invention can make much more contributions to weight reductions than do the prior art metallic guides. This is less significant for a single cassette, but is more significant for the step of stocking a large amount of cassettes, as encountered in the cassette assembly line, firstly because a guide loader in the cassette assembly line can be made small and secondly because resinous guides can be placed in bulk, but metallic guides are likely to be damaged on their mirror-finished surfaces when they come into contact with each other due to their own weight. Usually, metallic guides are transported in the form of being arranged in a case or tray. (4) A comparison of currently available metallic guides with polyethylene guides in terms of the stability-with-time, stability to temperature and humidity, running noise, weight and cost required for tape guides reveals that an ultrahigh-molecular weight polyethylene having a molecular weight exceeding 1,000,000 gives molded pieces having their stability-with-time comparable or superior to those of metallic guides now in use, partly because it excels in chemical resistance and partly because it is very stable to appearance changes. Referring to the stability to temperature and humidity, in particular temperature, polyethylene guides are stable at usually applied temperatures. The results of experimentation indicate that they service well at a temperature of -45°C to 80°C during transportation, unless any particular external force is applied thereto. As regards the stability to humidity, polyethylene itself has a hygroscopicity of as low as 0.01% or below and so undergoes no change due to humidity. Turning to running noises generated due to stick slipping, the results of experimentation indicates that the guide of polyethylene made composite produced by the method of the present invention is very limited in terms of stick slipping and so poses no practical problem at all. Therefore, running noises are reduced to practical levels even at high speeds. The weight of polyethylene guides can be reduced to 1/5 to 1/10 of that of metallic guides. The cost of polyethylene guides is cut down to about 1/2 of metallic guides by increased molding cycles. The ultrahigh-molecular weight polyethylene used may have a viscosity-average molecular weight of 1,000,000 to 6,000,000. For instance, use may preferably be made of Hi-Zex million 240 M® (having a molecular weight of 2,900,000 and made by Mitsui Petrochemical Industries, Ltd.) and Hostaren GUR 412® (having a molecular weight of 2,400,000 and made by Hoechst, West Germany, both available in powdery forms, and so on. Alternatively, use may be made of a synthesized high-molecular weight polyethylene having a viscosity-average molecular weight of 1,000,000-6,000,000 or more, a so-called crosslinked polyethylene formed by crosslinking with a crosslinker or electron beams, and so on. In the present invention, the polyethylene used should preferably be in such finely divided forms as expressed in terms of a particle size of 10-300 µm, particularly 50-200 µm, in order to achieve as uniform mixing as possible. The function of the ultrahigh-molecular weight polyethylene varies depending upon how high or low molecular weight it has. For instance, when it is applied to a guide bush for video tapes, its molecular weight correlates with the friction occurring between that guide bush and a PET film that is a tape material. In other words, if its molecular weight is below 500,000, then the guide bush wears away, whereas if its molecular weight is higher than 2,000,000, then the PET film wears away prematurely. Thus, how high or low molecular weight the ultrahigh-molecular weight polyethylene possesses has so important relation to its use that its molecular weight has to be regulated depending upon what properties the products are required to have. As already mentioned, polyethylene resins increase generally in their melting viscosity with an increase in their molecular weight. Especially at a molecular weight exceeding 1,000,000, they are so likely to stagnate in the barrel of a general (in-line screw type of) injection-molding machine that they cannot be molded. When they are to be forcedly plasticized, the main molecular chain of polyethylene is cut out by high shear stress occurring between the barrel and the screw, resulting in the formation of polyethylene having its molecular weight reduced. As already mentioned, such low-molecular weight polyethylene (having a molecular weight below 500,000) is unfit for the tape guides of the present invention. Heretofore, the ultrahigh-molecular weight polyethylene has thus been molded by compression molding or extrusion molding. With such molding techniques, however, it is impossible to obtain molded pieces or parts of high accuracy at low costs. On the other hand, improvements in the rigidity of gears, etc. are considered to be achievable by making the ultrahigh-molecular weight polyethylene composite with an inorganic material such as carbon fibers. With compression molding, the inorganic material may be made composite with the ultrahigh-molecular weight polyethylene in powdery forms, since the former is fused onto the surface of each particle of the latter. With ordinary injection molding, however, the inorganic material is made composite with the ultrahigh-molecular weight polyethylene by way of the fusion of its respective particles, thus resulting in its molecular weight being reduced and its basic properties being lost. According to the method of the present invention, it is possible to efficiently obtain injection-molded pieces of high accuracy from a raw material comprising the ultrahigh-molecular with or without the inorganic material to be made composite with it by means of injection molding. The injection-molding machine used in the present invention is an in-line screw type of molding machine in which a hopper is connected with an atmospheric gas supply pipe for melting an ultrahigh-molecular weight polyethylene feed in a non-oxidizing atmosphere, only the compression and nozzle zones of a cylinder with a built-in screw are provided with heaters and a heat-radiating zone is defined by a part of a feeder region. A more illustrative example of an injection-molding machine used in the present invention will now be explained with reference to the accompanying drawings. Figure 3 is a sectional view illustrating an injection-molding machine which may be used to make the sliding members of the present invention. Main parts of this injection-molding machine are a cylinder 2 with a built-in screw 1, a hopper 4 for inputting a feed stock 3 into the cylinder 2, a mold 6 having therein a molding cavity 5, in which the leading end of the cylinder 2 is located, a vacuum tank 7 for vacuumizing the cavity 5 and a rotary pump 8. The hopper 4 is connected with a pipe 9 for supplying to it an atmospheric gas such as nitrogen gas so as to melt the feed stock 3 fed into the cylinder 2 in a non-oxidizing atmosphere. At its lower portion, the hopper 4 includes a regulating plate 10 having therein a circular or rectangular slit 10a for regulating the input of the feed stock 3. Suitably, the screw 1 driven by a vane motor 11 gives rise to a compression ratio of 2.3 or below, esp., 1.3-2.0 with the length to diameter (L/D) ratio being in a range of preferably 10-25, more preferably 15-20. Without recourse to any back-flow ring, the screw head has a flight extending to its extreme end, and is smaller in diameter than the inner diameter of the cylinder 2 by 0.1 to 0.2 mm. The cylinder 2 is divided into a rear section defining a feeder zone 2a and a front section defining a compression zone 2b with the leading end defining a nozzle zone 2c. Preferably, the length of the feeder zone 2a, over which a heat-radiating fin 12 is to be mounted, is 1/4 to 1/3 of the entire length of the cylinder 2. The ultrahigh-molecular weight polyethylene powders are delivered by the screw through the cylinder, and generate heat due to their friction, as the compression ratio increases. It is when the polyethylene reaches the compression zone of the screw that this state is achieved, and it is in this zone 2b that the powders are individually softened for the first time by external heating. In other words, in the zone 2a in front of the zone 2b, heating should be avoided as much as possible to radiate frictional heat, thereby preventing crosslinking. In the absence of the heat-radiating fin 12, heating control at the compression zone 2b is so impossible that the polyethylene powders can be prematurely crosslinked. For the instantaneous melting of the feed stock 3, the compression and nozzle zones 2b and 2c are provided with heaters 13. In order to obtain highly accurate injection-molded pieces of the ultrahigh-molecular weight polyethylene, it is essentially required to apply sufficient injection rates to the resin at the injection step and give sufficient pressures to the resin in the process of filling it in the mold cavity. From the flowability of the ultrahigh-molecular weight polyethylene, it has now been found that of particular importance for improving shapeability and dimensional accuracy is to maintain the pressure applied to the resin at the dwell step. Part of the screw head portion of the injection-molding machine used in the present invention is shown in the sectional view of Fig. 4, wherein reference numeral 31 stands for a screw, 32 a cylinder (a barrel) and 33 a cylinder nozzle. Reference numeral 34 indicates a screw head portion, which is constructed from a cylindrical section 35 extending from the screw portion and a conical section 36 contiguous to and extending from it. The cylinder nozzle 33 is threadedly fixed to an end portion of the cylinder 32 with its inner bore wall 37 following the shape of the screw head portion 34. When the screw 31 moves forward to such a position as illustrated, there is formed a gap or space between the cylindrical section 35 of the screw head portion 34 and the inner bore wall 37 of the cylinder nozzle 33, which defines a pressure-to-the-resin (hereinafter called the resin pressure) generating region 38 - an important feature of the present invention. This pressure generating region 38 may be located between the cylindrical section 35 and the cylinder 32, not the cylinder nozzle 33. It is noted that reference numerals 39 and 40 stand for a nozzle tip and a lock nut, respectively. A back-flow ring having a diameter substantially equal to the cylinder diameter is provided to the screw head portion, and is designed in such a way that it stops at the extreme end of the cylinder, even when it moves forward to a maximum. According to the present invention, it is possible to prevent the back-flow of the resin at the time of dwell by meeting the condition of D > D' wherein D is the diameter of the screw 31 and D' is the diameter of the cylindrical section 35 of the screw head portion 34. However, the length L' of the cylindrical section 35 can be determined arbitrarily. Referring then to the resin pressure generating region 39, the diameter D' of the cylindrical section is preferably identical with or smaller than a groove diameter DM of the flight lying on the metering region of the screw 31. The length L' may meet 1/10D' ≦ L' ≦ 10D' , preferably 1/2D' ≦ L' ≦ 3/2D' . The screw head portion 34 may be adapted to be separated from the screw 31. In this case, another screw head 34 having a length L' varied depending upon the nature of the resin used may be provided to regulate the generation of a dwell pressure arbitrarily. Reference will now be made to how to make molded pieces of the ultrahigh-molecular weight polyethylene with the use of such an injection-molding machine as mentioned above. The ultrahigh-molecular weight polyethylene in the form of fine powders having a particles size of about 30 to 100 µm is first supplied as the feed stock 3 into the hopper 4 shown in Figure 3. It is here noted that the input of the feed stock per time can be determined only by the regulation of the diameter 10a because, unlike ordinary polyethylene, the ultrahigh-molecular weight polyethylene is in powdery form, rather than in pellet form, so that the coefficient of friction among the polyethylene particles can be reduced. The regulation of the input of the feed stock to the feeder zone 2a means that the compression ratio of the screw 1 decrease relatively, with the result that when the ultrahigh-molecular weight polyethylene is plasticized, the compression ratio is so excessively increased that the stagnation of the feed stock in the cylinder 2 can be avoided. Then, the ultrahigh-molecular weight polyethylene fed into the cylinder 2 is delivered from the feeder zone 2a to the compression zone 2a, in which it is instantaneously heated. That polyethylene is in turn melted (on its surface alone) in the nozzle zone 2c. It is here noted that since the hopper 4 is filled with a nitrogen gas, the cylinder 2 is therein maintained in a non-oxidizing atmosphere to prevent the molecular weight of the polyethylene from being reduced by oxidation. The ultrahigh-molecular weight polyethylene has the property of starting crosslinking immediately upon melted. Thus, if the polyethylene is momentarily melted in the compression zone and, just thereafter, is cast through the nozzle zone into the cavity 5, as carried out in the present embodiment, then it is possible to cast the molten polyethylene in the cavity, while it remains flowable. It is understood that for the resinous guides produced by the method of the present invention, the polyethylene having a molecular weight of 500,000 or higher may be used alone and, more effectively, it may be made composite with carbon or hydrocarbonaceous oligomers, polyethylene waxes, fluororesins and the like. Even in this case, no limitation is imposed on the present invention. In other words, although the melting viscosity of the resin is further increased by composite-making, yet it is possible to impart sufficient shapeability to high-viscosity materials, if the mold and injection-molding technique according to the present invention are used. As already mentioned, plastic materials are non-Newtonian fluids which decrease generally in their apparent viscosity at increased shear rates. This is also true of the polyethylene having a molecular weight of 500,000 or higher. In actual molding, this implies that viscosity decreases at increased shear rates so that thin-wall molding is feasible, thus giving rise to improvements in shapeability. As an example, it is possible to mold sliding guides for magnetic tapes by increasing shear rates and decreasing viscosity, because they are in thin-wall form. The problems then arising are that: (1) voids are generated, because the resin being molded entrains the air remaining in the mold; (2) short shots are generated, as if the volume of the cavity is decreased, because no air escapes from within the cavity; and (3) resin burning occurs due to the friction between the flowing end of the resin and the air, resulting in a lowering of its molecular weight. According to the mold used in the present invention, the cavity space is so filled with the insert piece at an initial stage of filling that the air prevailing in the runner and sprue portions is under reduced pressure. At the time of resin filling, therefore, the amount of air remaining in the cavity is so small that the above problems can be eliminated. In what follows, reference will be made to how to composite the ultrahigh-molecular weight polyethylene inputted in the above injection-molding machine. Figure 5 is a longitudinal section of the jar used for compositing the ultrahigh-molecular weight polyethylene. A jar 18 includes a side wall filled with an oil 19 for heating, is provided at its bottom with an agitating blade 21 rotated by a motor 20 and is connected through its upper portion with a pipe 22 for feeding a non-oxidizing atmospheric gas such as nitrogen gas. The ultrahigh-molecular weight polyethylene and the material to be made composite with it are to be inputted in the above jar 18. That material is preferably an inorganic material such as CaCO₃Al₂(OH)₃, Al₂O₃, Ca₃(PO₄)₂, glass fiber powders, carbon fibers powders, wood powders, paper powders, glass beads, metal particles and carbon, which are added in an amount of 30% by weight or less, particularly 3 to 30% by weight. At the same time, the aforesaid organic materials may be added. A mixture 23 of the ultrahigh-molecular weight polyethylene with the material to be made composite with it is inputted and mixed in the jar 18 fixed at a temperature of 80 to 120°C, preferably 85 to 100°C, while the speed of rotation the agitating blade 21 is rotating at 1,800 to 3,000 rpm. After the temperature of the mixture 23 reaches 110 to 120°C, the speed of rotation of the agitating blade blade is reduced to 90 rpm. The thus composited ultrahigh-molecular weight polyethylene is placed in a cooling jar in which it is cooled down to normal temperature at 60 rpm. That is to say, if the ultrahigh-molecular weight polyethylene particles are completely melt, then compositing cannot be achieved. By carrying out agitation in the above manner, however, the ultrahigh-molecular weight polyethylene particles absorb heat from the wall surface of the jar 18, and are then softened on their surfaces by frictional heat by agitation. Thereupon, the material to be composited is driven and deposited onto the softened particles' surfaces by acceleration by agitation. Thus, compositing is achieved. The thus composited raw material is inputted in the hopper 4 of the injection-molding machine shown in Figure 3, in which it is melted within such a short time as already mentioned. The melt is immediately injected into the cavity for molding. Illustrative Example of Injection Molding First of all, an ultrahigh-molecular weight polyethylene having a molecular weight of 3,000,000 (Hi-Zex million 240 M made by Mitsui Petrochemical Industries, Ltd.) was inputted in the hopper 4 of the injection-molding machine according to the present invention, and the slit 10a for regulating the input of the feed stock, located at the bottom of the hopper, was fully opened. The screw had then a diameter of 40 mm, a compression ratio of 1.4, a pitch of 30 mm, an L/D ratio of 20 and a speed of rotation of 180 rpm. The nozzle (an open nozzle) and compression zones 2c and 2b of the cylinder 2 were fixed at 220°C and 170°C, while the feeder zone 2a was not heated, but reached 70 to 100°C, as measured during molding. Further, the hopper 4 was fed with a nitrogen gas at a ratio of 1.0 liter/min. On the other hand, the mold 6 was fixed at 70°C, while the cavity 5 was vacuumized to 10⁻³ torr. Molding was carried out with an annular gate (having a gate width of 0.8 mm) for the sliding guide for magnetic tapes so as to obtain molded pieces in which D = 6 mm, D = 4.85 mm and L = 16 mm, as shown in Figure 8. The molding conditions were an injection time of 0.3 sec., a dwell time of 3 sec., a cooling time of 20 sec., an interval of 3 sec. and an overall cycle of 26.5 sec. The pressure to be applied to the resin in the mold was fixed at 8 × 10⁶ Pa (800 kg/cm²) (as measured by a sensor), and the spring for producing a compression effect was built in the mold with a spring constant and deflection, both calculated and determined such that when the resin was filled in the cavity and the piece to be molded reached L = 16 mm, the spring produced a compression pressure of 1.5 × 10⁵ Pa (15 kg/cm²). Figure 6 is a sectional view of a 12-cavity mold assembly for injection-molding 12 sliding guides for magnetic tapes according to the embodiment of the present invention. Referring to this figure, the mold assembly comprises a fixed bottom plate 103, a runner plate 104, a fixed retainer plate 105, a movable retainer plate 106, a back plate 107, a spacer plate 108, an ejector front plate 109, an ejector back plate 110 and a movable bottom plate 111 with a vacuum packing 119 interposed between the fixed and movable retainer plates 105 and 106 and O-rings (not shown) provided between the respective plates for complete sealing. While the mold is closed up, it is placed in a completely closed-up state and vacuumized through a hole 120 for vacuumization by means of a vacuum pump. Reference numeral 101 stands for a locating ring, 102 a sprue bush, and 112 a primary sprue formed in the sprue bush 102. A pressure sensor pin 126 is slidably fitted with respect to the runner plate 104 to transmit a load due to the resin pressure from a runner 113 to a sensor 127 therefor. The transmitted load is fed back to a machine control for closed-loop controlling. The cavity is constructed from a movable piece 115, a compression piece slidable by the resin pressure and a spring force and an inner core (a gate cutting piece) 117. When the cavity is unfilled, the compression piece 116 is in an advanced position with a gap of 1 mm located between it and the fixed retainer plate 105. The movable piece 115 is slidably fitted with the compression piece 116 in such a way that as the resin flows in the cavity and so the volume of the cavity increases, the compression piece 116 is retracted by the resin pressure. The compression piece 116 is connected and fixed with a spring 118 for generating a reaction force with respect to the resin pressure and determining the volume of the cavity by the resin pressure and spring force, thereby distributing the resin pressure uniformly throughout the piece to be molded. That is to say, the characteristic feature of the present invention is to vary the volume of the cavity by the amount of the resin filled, thereby generating a spring force corresponding to that volume or a force for making the cavity pressure distribution uniform. As illustrated in Figure 7, an annular gate 124 is located between the inner core (gate cutting piece) 117 and a secondary sprue 114. The inner core (gate cutting piece) 117 and the compression piece 116 are slidably fitted with each other, so that the inner core (gate cutting piece) 117 is ejected forward through the ejector front and back plates 109 and 110 for gate cutting by driving a pressure cylinder 123 for gate cutting, thereby cutting the annular gate 124. An illustrative example of the injection compression molding process will now be explained. The process is started from mold closing. In the course of mold closing, the vacuum pump is actuated to start vacuumizing the mold. At the time of completion of mold closing, the mold is vacuumized to about 10-3 torr. Afterwards, the weighed ultrahigh-molecular weight polyethylene is injected from the cylinder into the mold and filled in the cavity through the primary sprue 112, runner 113, secondary sprue 114 and annular gate 124. The resin is measured in terms of its pressure by the pressure sensor 127 and enters the dwell step after the preset pressure [8 × 10⁶ Pa (800 kg/cm²)] is reached. Simultaneously with the completion of the dwell step, the pressure cylinder 123 for gate cutting is driven for gate cutting by the inner core (gate cutting piece) 117, Afterwards, the resin enters the cooling step and, in the meantime, the resin is weighed out in the cylinder for the next shot. As the cooling step is completed, the mold is so opened that the compression piece 116 is ejected forward by the spring 118 with the molded piece being pushed out of the mold. In this manner, a succession of molding steps are completed. As a result of measuring the dimensions of the thus obtained sliding guides for magnetic tapes, it has been found that they are in a range of 10 µm of the standard dimensions and have a roundness of 15 µm. According to the present method and apparatus in which, as explained above, a polyethylene having a molecular weight of 500,000 or higher is instantaneously melted and the melt is immediately injected into the cavity, it is possible to easily produce molded pieces of high precision such as sliding guides for tapes. By injection compression-molding a polyethylene having a molecular weight of 500,000 or higher, it is also possible to achieve improvements in shapeability such as easy transfer of the mold surface and a reduction in surface roughness. In addition, reductions in frictional resistance and the prevention of undulation of the molded pieces' surfaces are achieved, thus making it possible to improve the travelling characteristics of tapes. Because of having self-wettability, the obtained sliding guides for tapes dispenses with lubrication and so are applicable both in vacuo and in the water. Example-1 With such an injection-molding machine as shown in Figure 3, polyethylene resins having varied molecular weights were molded, and the wear resistance of the polyethylene resins was estimated with such a sand slurry testing machine as shown in Figure 9. Referring to the testing conditions, a slurry 91 was prepared by adding 2 liters of water to 3 kg of No. 4 silica sand prescribed by the Civil Engineering Society. A test piece 92 measuring 50 × 25 × 3 mm was cut out of an injection-molded, 85 mm diameter disc having a similar width. As illustrated, the test piece 92 was continuously rotated by a motor 93 in the sand slurry for 20 hours at 1,000 rpm. For comparison, a test piece of similar dimensions were formed of carbon tool steel SK-5 and subjected to wear-resistant testing under similar conditions, using silicon carbide as a slurry. The polyethylene resins used are Hi-Zex 5000H (having a molecular weight of 130,000 and made by Mitsui Petrochemical Industries, Ltd.), SHOLEX-SUPER 4451H (having a molecular weight of 330,000 and made by Showa Denko K.K.), Hi-Zex million 240M (having a molecular weight of 2,200,000 and made by Mitsui Petrochemical Industries, Ltd.) and Hosteren GUR413 (having a molecular weight of 2,900,000 and made by Hoechst). The molding conditions were a screw's speed of rotation of 180 rpm, a cylinder nozzle zone's temperature of 240°C and a compression zone's temperature of 170°C, but the feeder zone was cooled off by spontaneous heat radiation. The mold's temperature was fixed at 70°C, and a nitrogen gas was fed into the hopper at a ratio of 1.0 liter/min. The results of wear resistance by the sand slurry testing are set forth in Figure 10, from which it is found that the higher the molecular weight, the smaller the volume reduction and the less the wearing. The results of a comparison with the carbon tool steel are also set forth in Figure 11. These results prove that the present molding method is equivalent in terms of the abrasion loss of the ultrahigh-molecular weight polyethylene to conventional compression molding, and is improved in terms of productivity without causing damage to the function of the ultrahigh-molecular weight polyethylene. The following examples refer to the results of the following resins, formulations and additives investigated. Example-2 The resins shown in Table 1 were mixed together to prepare polyethylene resins having varied molecular weights. Five (5)% by weight of carbon black (acetylene black) were added to the resulting mixtures which were in turn molded with a molding machine similar to that used in Ex. 1 to obtain molded pieces of such a shape as shown in Figure 1. They were then estimated as tape guides. The mixing ratios are set out in Table 2-1. Carbon black was mixed with the resins of 50°C by dry-blending them together at 1800 rpm and normal temperature over 5 minutes with a Henschel mixer. The molding conditions were similar to those applied in Ex. 1, i.e., a mold temperature of 70°C, a resin temperature of 240°C and a screw's speed of rotation of 180 rpm. The molding cycle was 25 seconds and the mold used was of a four-cavity type. The tape guides molded under the above conditions were loaded in an actual cassette (T-120) according to the VHS specification to measure the take-up time of a tape in fast forward (FF for short) and rewind (REW for short), using a rewinder (KMV-750) made by TAPEX. The larger the dynamic frictional force of the tape guides to a magnetic tape, the longer the time taken will be, and vice versa. By such actual experimentation, damages to the magnetic tape (marring) can also be estimated. The results are set forth in Table 2-2. (Blend Examples) (1) Hi-Zex million 240M alone (M.W.: 2,900,000) (2) 240M:L5000P 3:1 (M.W.: 2,400,000) (3) 240M:L5000P 1:1 (M.W.: 1,900,000) (4) 240M:L5000P 1:3 (M.W.: 1,400,000) (5) Lubmer L500P alone (M.W.: 900,000) (6) L5000P:P3000P 1:1 (M.W.: 600,000) (7) Lubmer L3000P alone (M.W.: 300,000) (Travelling Time by Rewinder) No. Travelling Time Tape Marring Guide Marring (1) 5'13 37 0 (2) 5'05 32 0 (3) 4'38 5 0 (4) 4'36 4 0 (5) 4'34 6 0 (6) 4'35 8 3 (7) 4'35 9 5 Comp. (1) 4'35 5 0 Comp. (2) 4'36 >100 80 Note 1: Travelling time - an average of ten travelling time values in FF and REW, measured with a TAPEX rewinder. Note 2: Tape marring - the number of marrings occurring on a tape reciprocated 50 times under a load of 50 g at a speed of 1000 mm/min. over a length of 150 mm. Note 3: Guide marring - the number of marrings occurring on a guide, as measured by similar procedures as applied in Note 2. Note 4: Comparative (1) refers to a value of a generally available metallic guide. Note 5: Comparative (2) refers to a value of a resinous (POM) guide built in a cassette sold by Victor Company of Japan, Ltd. From the above results, it is desired that in view of the travelling time and no tape marring, the molecular weight be up to 2,000,000. In view of no guide marring, it is desired that the molecular weight be about 800,000 or higher. From the above results, it is desired that the molecular weight be from 800,000 to 2,000,000 inclusive. It has also been found that the guides of the present invention are superior in terms of marring to the comparative resinous guides. Example-3 This example was performed to determine the quantitative range, of carbon black added to the ultrahigh-molecular weight polyethylene. How to blend resins, how to mold tape guides, etc. are similar to those described in Examples 1 and 2. For estimation, static and dynamic frictional forces applied to magnetic tapes were measured with a tensile tester made by Orientic Co., Ltd. (Tensilon). In other words, the frictional forces applied on a tape, when reciprocated 50 times under a load of 50 g at a speed of 1000 mm/min., were measured with a load cell. The tape used to this end are an HS type T-120 tape made by TDK. The obtained conclusions are that taking the frictional forces and the number of marrings occurring on the tapes and the sliding surfaces of the tape guides into account, the most preferable amount of acetylene black added is 5% by weight, while the most favorable amount of ketchen black added is in a range of 2 to 5% by weight. The resins used for estimation are listed up in Table 3-1, and the results of estimation are set forth in Table 3-2. Example-4 In order to reduce frictional resistance, investigation was made of additives. The resins used were similar three types as used in Example 3, and 5% by weight of acetylene black were added as carbon black. As was the case with the addition of carbon black, acetylene black was added simultaneously with the mixing of carbon black. Mixing conditions were similar as applied in Ex. 2. Measurement was also carried out in similar manners as used in Ex. 3. Additives in liquid or powdery form and used in smaller amounts were diluted and mixed with volatile solvents for dissolving them such as ethyl alcohol, methyl alcohol, isopropyl alcohol, methyl ethyl ketone and acetone, followed by the removal of excessive solvents by the application of heating and reduced pressure. The additives used are shown in Table 4-1 along with their amounts. The obtained results are set forth in Tables 4-2 to 4-4. (Results of frictional Results Found (25°C: TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 80 80 81 (2) 78 79 77 (3) 80 81 81 (4) 76 76 77 (5) 80 81 82 (6) 77 78 78 (7) 77 77 78 (8) 77 78 78 (9) 77 79 77 (10) 83 83 83 (11) 77 78 77 (12) 83 82 83 (13) 80 80 80 Comp. (1) 83 83 83 Comp. (2) 83 83 83 (Results of frictional Results Found (60°C: TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 84 83 84 (2) 83 83 82 (3) 78 79 79 (4) 76 76 76 (5) 78 78 79 (6) 80 81 79 (7) 81 80 81 (8) 80 81 79 (9) 81 81 80 (10) 83 82 81 (11) 82 81 81 (12) 80 80 81 (13) 76 76 76 Comp. (1) 75 75 75 Comp. (2) 79 79 79 (Results of frictional Results Found (10°C: TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 86 85 86 (2) 87 86 86 (3) 85 85 84 (4) 83 83 82 (5) 85 86 85 (6) 85 85 86 (7) 88 88 87 (8) 88 88 88 (9) 88 87 88 (10) 89 90 90 (11) 85 85 85 (12) 89 90 89 (13) 91 90 91 Comp. (1) 85 85 85 Comp. (2) 92 92 92 From the above results, it is found that frictional resistance varies depending upon what temperature is used far measurement, and that the types of additives for reducing frictional resistance differ at low or high temperatures. It was only silicone oil (3) that satisfied all the conditions. Saving at low temperatures, the test pieces containing no additive showed relatively good values, but such values dropped at low temperatures. These data hold for HS grade tapes sold by TDK, and the types of suitable additives vary depending upon the tapes used by various makers and whether or not back coating is applied. For instance, a combination of a fluorine base surfactant with a hydrocarbonaceous oil is most effective for a reduction in the frictional resistance of JVC tapes. That is, it is required to select the additives according to the characteristics of various makers and it is desired that the above additives be used alone or in combination of two or more. Example-5 In this example, the travelling torque, which the tape guides of the present invention exerted on an actual tape deck, was estimated by measuring the output voltage of a deck's motor. The tape deck used far estimation is a VTR BR-7000A made by JVC. The tape used was an HS type T-120 made by TDK. The resins used and how to add them are similar as described in Example 4. This holds for the molding conditions, molding machine and mold. The results are set forth in Tables 5-1 to 5-4. (Results of Torque Found (at the beginning of winding in FF; TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 32 32 32 (2) 31 32 31 (3) 32 33 32 (4) 31 31 31 (5) 32 33 32 (6) 32 32 32 (7) 32 32 32 (8) 32 32 32 (9) 32 33 32 (10) 34 35 34 (11) 31 32 31 (12) 35 35 35 (13) 32 32 32 Comp. (1) 32 32 32 Comp. (2) 35 35 35 Note 1: Torque - a torque (in mV) applied to a motor in FF and REW which was measured at the beginning and end of winding with Victor VTR BR-7000A. (Results of Torque Found (at the end of winding in FF; TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 194 192 190 (2) 191 190 189 (3) 197 198 196 (4) 184 185 184 (5) 195 195 194 (6) 191 190 189 (7) 192 194 191 (8) 187 188 186 (9) 192 192 190 (10) 195 193 191 (11) 188 187 185 (12) 192 191 189 (13) 199 197 195 Comp. (1) 184 184 184 Comp. (2) 190 190 190 (Results of Torque Found (at the beginning of winding in REW; TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 32 31 32 (2) 30 31 30 (3) 32 32 31 (4) 30 29 30 (5) 32 32 31 (6) 31 32 32 (7) 30 30 30 (8) 32 32 32 (9) 32 32 32 (10) 34 34 33 (11) 30 32 31 (12) 33 34 33 (13) 31 32 32 Comp. (1) 31 31 31 Comp. (2) 33 33 33 (Results of Torque Found (at the end of winding in REW; TDK HS)) No. 1,900,000 1,400,000 900,000 (1) 154 152 150 (2) 151 150 149 (3) 157 155 156 (4) 145 144 144 (5) 155 155 154 (6) 151 150 149 (7) 152 154 151 (8) 147 148 146 (9) 152 152 150 (10) 155 153 151 (11) 148 147 145 (12) 152 151 149 (13) 159 157 155 Comp. (1) 144 144 144 Comp. (2) 150 150 150 The conclusions obtained from the above results are that torque is higher at the end of winding than at the beginning of winding and is higher and much more varied in FF than in REW. In the case of HS tapes made by TDK, the best results are obtained with silicone oil (3). At the beginning of winding, the tape travels at a slow speed with limited friction, but the results of torque coincide substantially in both FF and REW with the results of fictional resistance obtained in Ex. 4. In order to reduce torque at the beginning of winding, additives such as those capable of reducing frictional resistance may be selected. In order to reduce torque at the end of winding, however, it may be required to take changes in the shape of tape guides per se such as limiting their eccentricity into consideration.

Claims: A method for producing a sliding member comprising a polyethylene having a viscosity-average molecular weight of 500,000 to 6,000,000 inclusive, having a low coefficient of friction and excelling in both its own wear resistance and its property of preventing the abrasion of an associated member by injection molding, which includes: a step of vacuumizing a mold cavity portion prior to an injection step and, after injection, reducing a space of said cavity prior to solidifying the resins filled in said space, thereby compressing the resins filled, wherein said sliding member contains an additive comprising an organic material or an inorganic material in addition to said polyethylene resin, and said polyethylene resin powders and additive, that are raw materials, are mixed together at a temperature up to the melting point of said resin in the presence of stirring acceleration, thereby depositing said additive onto only the surfaces of said polyethylene resin powder particles. The method as claimed in claim 1, wherein the viscosity-average molecular weight of said polyethylene is in the range of 500,000 to 2,000,000 inclusive. The method as claimed in claim 1 or 2, wherein said sliding member is a guide for aiding the travelling of a tape, sheet or film. The method as claimed in claim 3, wherein said sliding member is a guide for magnetic tapes. The method as claimed in any of claims 1 to 4, wherein said additive comprises a hydrocarbonaceous oligomer. The method as claimed in any of claims 1 to 5, wherein said additive comprises a fluorine base surfactant. The method as claimed in any of claims 1 to 5, wherein said additive comprises a fine powder of tetrafluoroethylene. The method as claimed in any of claims 1 to 7, wherein a polyethylene resin feed in liquid form is supplied to an injection cylinder in a non-oxidizing atmosphere, in which it is melted within a short time by fixing the compression ratio of a screw of the injection cylinder at 1.3 to 2.0 and regulating the length to diameter ratio of the screw to from 15 to 20, and the melt feed is injected into the cavity prior to the initiation of its thermal crosslinking.

Inventors: FUJII HIDEAKI DAI NIPPON INSAT, NISHIYAMA MASASHI DAI NIPPON I, TAKAHASHI TATSUMI DAI NIPPON I, FUJII, HIDEAKI DAI NIPPON INSATSU KABUSHIKI, NISHIYAMA, MASASHI DAI NIPPON INSATSU, TAKAHASHI, TATSUMI DAI NIPPON INSATSU
Applicants: DAINIPPON PRINTING CO LTD, DAI NIPPON INSATSU KABUSHIKI KAISHA
Application year: 1989
Main classification: C10M107
IPC codes: C10M107, B29C45, B29C47, G11B15