ORAL COMPOSITIONS

Abstract: The invention relates to an oral composition for the care of the mouth to inhibit oral bacteria and to neutralize acids, produced by oral bacteria. This achieved by inclusion in the oral composition of a hydrotalcite-like material of a particular general formula, typical representatives being zinc aluminum hydrotalcite (Zn₁₂Al₆(OH)₃₆(NO₃)₆ H₂O) and copper magnesium aluminum hydrotalcite (Cu₃Mg₉Al₄(OH)₃₂Cl₄ H₂O). These hydrotalcite-like materials show significant anti-­ plaque activity. Typical examples of oral compositions are toothpastes and mouth rinses.

Description: This invention relates to oral compositions containing an analogue of a compound of the formula Mg₆Al₂(OH)₁₆CO₃4H₂O in any crystallographic form, and for convenience referred to hereinafter as a hydrotalcite-like compound. It is already known from US Patent No. 4 296 094 (Kyowa Chemical Industry) to include certain magnesium aluminium hydrotalcite-like compounds in a dental cleaning composition. The compounds are said to be very effective in removing bacteria in the oral cavity which may cause dental caries. The hydrotalcite-like compounds are said to react with acids such as lactic acid which may be produced by these bacteria in the oral cavity to neutralise them. The present invention concerns the use of other hydrotalcite-like compounds in oral compositions. The hydrotalcite-like compounds useful in the oral compounds of the present invention can be described by the following formula:- M m N n+p (OH) 2(m+n+p) A z y- xH₂O where: M is any 2+ cation or combination of 2+ cations N is any 3+ or 4+ cation or combination of 3+ and/or 4+ cations with the proviso that M is not solely Mg when N is solely aluminium, and where m is sum of the individual mole fractions of the 2+ cations n is sum of the individual mole fractions of the 3+ cations p is sum of the individual mole fractions of the 4+ cations where either but not both of n and p can be zero, m+n+p=1 and 0<n+p ≦m A y- / z is any anion of charge y- and mole fraction z, or combination of anions of similar or different y- and (the sum of the mole fraction)x(the charge on the anion) is given by the expression where t is the total number of anions and x can range from 0 to 100. The hydrotalcite-like compounds employed in the oral compositions of this invention are effective in inhibiting bacteria and neutralising acids produced by oral bacteria. The 2+ cations M in the above formula are Mg²⁺, Zn²⁺, Fe²⁺, Cu²⁺, Sn²⁺, Ca²⁺ and Sr²⁺. N cations include Al³⁺, Fe³⁺, Ti⁴⁺ and Sn⁴⁺. Preferred divalent cations are those having bacteriostatic properties such as Zn²⁺, Cu²⁺ or Sn²⁺ or a combination of these ions, or a combination thereof with other divalent cations. Such hydrotalcite-like compounds are advantageous in that by absorbing onto oral tissue the bacteriostatic M²⁺ ions are released during slow dissolution of the hydrotalcite-like compound in oral fluids and are effective in combating the growth of dental plaque. This dissolution occurs locally in the more acidic environment created by bacterial metabolism. Most preferred as the bacteriostatic cation are zinc and copper. The anion A may be an inorganic or organic anion. Preferred inorganic anions A are F⁻, Cl⁻, NO₃⁻, SO₄²⁻, FPO₃²⁻, CO₃²⁻ and OH⁻. The F⁻ and FPO₃²⁻ anions have anti-caries properties and may exchange for anions found in saliva such as Cl⁻ and PO₄³⁻. Examples of organic anions are carboxylate ions such as citrate. Preferred hydrotalcite-like compounds of this invention are: Zn₁₂Al₆(OH)₃₆(NO₃)₆ H₂O Zn₁₂Fe₆(OH)₃₆F₆ H₂O Cu₃Mg₉Al₄(OH)₃₂Cl₄ H₂0 Cu₃Zn₉Al₄(OH)₃₂(FPO₃)₂ H₂O Sn II ₃Zn₉Sn IV ₄(OH)₃₂(CO₃)₄ H₂O Sn II ₃Mg₉Ti IV ₄(OH)₃₂(F)₈ H₂O Zn₆Al₂(OH)₁₆CO₃ 4 H₂O Zn₈Ti₂(OH)₂₂CO₃ 4 H₂O The hydrotalcite-like compound is present in the oral composition of the invention in combination with a suitable diluent or carrier. For example the composition may be a mouthwash or toothpaste. The amount of the hydrotalcite-like compound is desirably present in an amount of at least about 0.01% up to about 30% by weight although greater amounts may be used. Preferred amounts are from 0.1% to 15% by weight of the oral composition. The oral composition of this invention will contain other ingredients commonly used to formulate such products, depending on the form of the oral product. For instance, in the case of an oral composition in the form of a toothpaste the product will comprise a particulate abrasive cleaning agent, an humectant-containing liquid phase and a binder or thickener which acts to maintain the particulate solid abrasive in stable suspension in the liquid phase. A surfactant and a flavouring agent are also usual ingredients of commercially acceptable toothpastes. Particulate solid abrasive cleaning agents commonly present in toothpastes include silica, alumina, hydrated alumina, calcium carbonate, anhydrous dicalcium phosphate, dicalcium phosphate dihydrate and water-insoluble sodium metaphosphate. The amount of abrasive agent is usually between about 5% and 70% by weight of the toothpaste. Humectants commonly used are glycerol and sorbitol syrup (usually comprising an approximately 70% solution). However, other humectants are known to those in the art including propylene glycol, lactitol, xylitol and hydrogenated corn syrup. The amount of humectant will generally range from about 10% to 85% by weight of the dentifrice. The remainder of the liquid phase will consist substantially of water. Likewise numerous binding or thickening agents have been indicated for use in dentifrices, preferred ones being hydroxyethylcellulose, sodium carboxymethylcellulose and xanthan gum. Others include natural gum binders such as gum tragacanth, gum karaya and gum arabic, Irish moss, alginates and carrageenans. Silica thickening agents include the silica aerogels and various precipitated silicas. Mixtures of binders may be used. The amount of binder included in a dentifrice is generally between 0.1% and 10% by weight. It is usual to include a surfactant in a dentifrice and again the literature discloses a wide variety of suitable materials. Surfactants which have found wide use in practice are sodium lauryl sulphate, sodium dodecylbenzene sulphonate and sodium lauroylsarcosinate. Other anionic surfactants may be used as well as other types such as cationic, amphoteric and non-ionic surfactants. Surfactants are usually present in an amount of form 0.5% to 5% by weight of the dentifrice. Flavours that are usually used in dentifrices are those based on oils of spearmint and peppermint. Examples of other flavouring materials used are menthol, clove, wintergreen, eucalyptus and aniseed. An amount of from 0.1% to 5% by weight is a suitable amount of flavour to incorporate in a dentifrice. The oral composition of the invention may include a wide variety of optional ingredients. These include sweetening agent such as saccharin; an opacifying agent, such as titanium dioxide; a preservative, such as formalin; a colouring agent; or pH controlling agent such as an acid, base or buffer, such as benzoic acid. Futhermore, they may include anti-caries agents such as sodium fluoride, stannous fluoride, monosodium fluorophosphate; anti-plaque agents such as stannous pyrophosphate, zinc citrate; antibacterial agents such as 2,4,4′-trichloro-2′-hydroxy-diphenylether, anti-calculus agents such as alkali metal pyrophosphates and so on. For a fuller discussion of the formulation of oral compositions reference is made to Harry's Cosmeticology, Seventh Edition, 1982, Edited by J B Wilkinson and R J More, pages 609 to 617. The invention also provides a method of treating the oral cavity with the above hydrotalcite-like compounds. The treatment may comprise rinsing with a suspension of the hydrotalcite-like compound in water or with a flavored mouthwash product containing the hydrotalcite-like compound or by brushing the teeth with a dental product comprising the hydrotalcite-like compound. Methods for the preparation of hydrotalcite-like compounds are known and have been described in a number of publications including Solid States Ionics 22 (1986) pages 135-141 where there is published a paper by Walter T Reichle entitled "Synthesis of Anionic Clay Minerals (Mixed Metal Hydroxides, Hydrotalcite)". The zinc hydrotalcite for inclusion in the oral compositions illustrated below may be prepared in the following way. 250mls of distilled water are added to a 1 litre reaction vessel. A mixture of Zn(NO₃)₂6H₂O (60g, 0.2 mol) and Al(NO₃)₃9H₂O (30 g, 0.075 mol) in one beaker and NaOH (30g, 0.75 mol) in another (both made up to 200mls with distilled water) are added via two peristaltic pumps over a period of 30 minutes. The reaction is continuously stirred by means of an overhead paddle stirrer, and the pH is maintained at pH 10±0.2 by controlling the rate of NaOH addition. The precipitate formed is aged at 95°C for 24 hours in polythene pots after which the product is filtered, washed with distilled water and dried. The zinc hydrotalcite obtained has the formula Zn₁₂Al₆(OH)₃₆(NO₃)₆H₂0. By ion exchange the nitrate anion may be exchanged for other ions such as the monofluorophosphate anion. The following Examples illustrate oral compositions in accordance with the invention. Percentages are by weight. Example 1 A toothpaste is made having the following composition. 1-formula Zn₁₂Al₆ (OH) ₃₆ (NO₃) ₆H₂O Example 2 A toothpaste is made having the following composition. 1-as in Example 1 The following experiments illustrate the acid buffering effect and release of soluble zinc from zinc hydrotalcite. Buffering Effect of Zinc Hydrotalcite The following data correspond to the addition of 0.2g of a zinc-aluminium hydrotalcite (formula Zn₁₂Al₆(OH)₃₆(NO₃)₆H₂O) to 50 mls of hydrochloric acid (0.01 M) (Table 1) or sodium hydroxide solution (10⁻⁴M) (Table 2). Release of Soluble Zinc from Zinc Hydrotalcite Table 3 illustrates the amount of soluble zinc released from a dispersion of 0.2g of Zn hydrotalcite (formula Zn₁₂A1₆(OH)₃₆(NO₃)₆H₂O) in 20 ml of solution at different pHs, the initial ionic strengths being kept constant at 10⁻²M. After 30 minutes the suspension was centrifuged and the zinc concentration in the supernatant was determined by atomic absorption spectroscopy. Hydrochloric acid and sodium hydroxide solutions were used to adjust the pH and sodium chloride used to adjust the initial ionic strength. Example 3 The zinc hydrotalcite of the formula Zn₆Al₂(OH)₁₆CO₃.4H₂O and the copper hydrotalcite of the formula Cu₃Mg₉Al₄(OH)₃₂Cl₄H₂O were tested as to their anti-plaque activity. The test protocol was as follows: Strep.sanguis cells were grown overnight on blood agar plates. The cells were harvested and suspended in sterile 1% calcium chloride. Hydroxyapatite discs were immersed in this bacterial suspension for 30 mins, then transferred to an in vitro plaque apparatus. Medium (BHI + 1% sucrose) was dripped onto the discs continuously for 24 hrs at 37°C. Test solutions were prepared by dispersing the appropriate solid material at a concentration of 1% w/w in distilled water or in water containing o.2% Natrosol 250HR (a polymeric thickening agent). They were sterilised by autoclaving before use. Sterile solutions of test products were applied to the discs (2.5 ml/disc), then a suspension of Strep.sanguis in water was used to re-inoculate each disc. The medium drip was re-started and the discs incubated for a further 24 hrs at 37°C. The amount of plaque growth was assessed by sonicating each disc for 20 secs in 2 ml of saline solution and measuring total viable counts. (TVC) The results were as follows:

Claims: An oral composition for removing oral bacteria and neutralizing acids produced by oral bacteria, comprising from 0.01% to 30% by weight of a hydrotalcite-like material of the following formula: M m N n+p (OH) 2(m+n+p) A z y- xH₂O where: M is a 2+ cation or combination of 2+ cations N is a 3+ or 4+ cation or combination of 3+ and/or 4+ cations m is sum of the individual mole fractions of the 2+ cations n is sum of the individual mole fractions of the 3+ cations p is sum of the individual mole fractions of the 4+ cations where either but not both of n and p can be zero, m+n+p=1 and 0<n+p ≦m A Y- / z is an anion of charge y- and mole fraction z, or combination of anions of similar or different Y⁻ and (the sum of the mole fraction) times (the charge on the anion) is given by the expression where t is the total number of anions and x can range from 0 to 100, characterised in that the composition comprises a hydrotalcite-like material with bacteriostatic properties of the above formula, wherein M is Mg²⁺, Zn²⁺, Fe²⁺, Cu²⁺, Sn²⁺, Ca²⁺, Sr²⁺ or a combination of two of these cations, and N is Al³⁺, Fe³⁺, Ti⁴⁺, Sn⁴⁺ or a combination of these cations, with the proviso that M is not solely Mg when N is solely Al. An oral composition according to claim 1 characterised in that M is Zn²⁺, Cu²⁺, Sn²⁺ or a combination thereof. An oral composition according to claims 1 or 2, characterised in that A is F⁻, C1⁻, NO₃⁻, SO₄²⁻, FPO₃²⁻, CO₃²⁻, citrate and OH⁻. An oral composition according to anyone of claims 1-3, characterised in that the hydrotalcite-like material comprises one or more of the following compounds: Zn₁₂Al₆(OH)₃₆(NO₃)₆ H₂O Zn₁₂Fe₆(OH)₃₆F₆ H₂O Cu₃Mg₉Al₄(OH)₃₂Cl₄ H₂O Cu₃Zn₉Al₄(OH)₃₂(FPO₃)₂ H₂O Sn II ₃Zn₉Sn IV ₄(OH)₃₂(CO₃)₄ H₂O Sn II ₃Mg₉Ti IV ₄(OH)₃₂(F)₈ H₂O Zn₆Al₂(OH)₁₆CO₃ 4 H₂O Zn₈Ti₂(OH)₂₂CO₃ 4 H₂O An oral composition according to anyone of claims 1-4, characterised in that it is formulated in the form of a toothpase or a mouthrinse composition. Method for treating the oral cavity to remove oral bacteria and to neutralize acids, produced by oral bacteria, characterised in that the oral cavity is treated with a composition according to claim 5.

Inventors: ADAM, UNUS SULAIMAN, BROWN, GRAHAM THOMAS, LYLE, IAN GARDNER, PARKINGTON, MICHAEL JOHN
Applicants: UNILEVER N.V., UNILEVER PLC
Application year: 1989
Main classification: A61K7
IPC codes: A61K8, A61Q11