Electrophotographic photosensitive material

Abstract: An electrophotographic photosensitive material wherein a charge transporting layer (2) and a charge generating layer (3) are laminated in this order on a conductive substrate (1), and wherein the charge generating layer (3) contains N-type dye and P-type dye in a ratio of 40/60 to 90/10 (N-type dye/P-type dye) by weight.

Description: This invention relates to an electrophotographic photosensitive material, and more particularly to an electrophotographic photosensitive material which has a high sensitivity and is superior in copying red-coloured originals. Recently, as an electrophotographic photosensitive material having a greater degree of freedom for functional designing, a positively charged electrophotographic photosensitive material of a laminated type has been suggested, comprising a charge generating layer (CGL) containing a charge generating substance which generates positively and negatively charged carriers (photo-carriers) by emission of light and a charge transporting layer (CTL) which contains a charge transporting substance transporting the generated positive charge and laminated on a conductive substrate in order of CTL and CGL. In such a positively charged electrophotographic photosensitive material of laminated type, in order to form an electrostatic latent image, positive charges generated by light in a surface layer of CGL must be moved through the CGL to the interface between the CGL and the CTL and injected to the CTL. Meanwhile, as a charge generating substance, red-coloured condensed polycyclic organic dyes (for example, anthanthrone series, perylene series, azo series) are widely used taking copying characteristics of colour originals (especially red colour) into consideration. However, since all these dyes are N-type dyes (electron receptive dyes), they provide a poor transporting performance of positive charges. Therefore, it has been a problem that a portion of the positive charges does not move to the interface between the CGL and the CTL upon photosensitizing but remains in the CTL, thus lowering the sensitivity of the photosensitive material. It is a primary object of the present invention to provide a positively charged electrophotographic photosensitive comprising a charge transporting layer (2) and a charge generating layer (3) which are laminated in this order on a conductive substrate (1), the charge transporting layer (2) containing, as charge transporting substances, a butadiene derivative represented by the general formula (I): wherein Ar₁ to Ar₄ are aryl groups, each of which may have a substituent, and a hydrazone compound represented by the general formula (II): wherein R is a C₁ to C₄ alkyl group, and wherein the charge generating layer (3) contains an N-type dye and a P-type dye in a ratio of 40/60 to 90/10 (N-type dye/P-type dye) by weight, wherein the N-type dye is an anthanthrone compound, or a perylene compound, or an azo compound, and wherein the P-type dye is a phthalocyanine compound, anthraquinone compound, triphenylmethane compound, nitro compound, azine compound orquinoline compound. In the photosensitive material of the invention, when the photosensitive material is positively charged by corona discharge, heat holes in the P-type dye are injected into the charge transporting layer, and a negative space-charge is generated in the charge generating layer. This negative space-charge enhances the electric field in the charge generating layer for generation of photo-carriers and acts to improve the generation efficiency of photo-carriers in the subsequent exposure process. Then, by exposing the photosensitive material in such state to a colour original, both positively and negatively charged photo-carriers are generated from the P-type dye which has a light absorption edge of 550 to 600 nm and is superior in copying red-colours in particular, and out of them, positive charges are transported through the charge generating layer to the interface with the charge transporting layer by the P-type dye which is superior in hole transporting ability and injected into the charge transporting layer. On the other hand, the negative charges are neutralized by positive charges induced in the surface layer of the photosensitive material upon charging, and thus, an electrostatic latent image is formed on the exposed part. The invention is described further herinafter, by way of example only, with reference to the accompanying drawing in which Fig.1 is a sectional view showing an example of the layer construction of an electrophotographic photosensitive material in accordance with the present invention. The photosensitive material shown in Fig.1 comprises a charge transporting layer 2 containing a charge transporting material and a charge generating layer 3 containing two types of dyes, N-type and P-type, as charge generating materials, which are laminated on the surface of a conductive substrate 1 in this order. As shown in the drawing, a surface protection layer 4 to improve the wear resistance of the photosensitive material can be laminated over the charge generating layer 3, if required. The reason of employing P-type dye in the charge generating layer 3 is, as mentioned before, to enhance electric fields for generating photo-carriers and to improve the sensitivity by an improved hole transporting ability through the charge generating layer. Moreover, in a photosensitive material of this invention, the ratio by weight of the two dyes (N-type dye/P-type dye, hereinafter called "N/P ratio") is within a range of 40/60 to 90/10. The reason for thus specifying the ratio by weight is that in the case that the N/P ratio exceeds 90/10, as the content of P-type dye in the layer relatively decreases, the enhancement of electric fields and the hole transporting ability are weakened and the sensitivity deteriorates. In the case that the N/P ratio is less than 40/60, as the content of N-type dye relatively decreases, the sensitivity and the copying performance of red-coloured originals deteriorate. As N-type dye and P-type dye used for this invention, various conventionally known dyes can be used. In other words, as the N-type dye, perylene compounds, anthanthrone compounds, azo compounds, zanthene and acridine, which have amino group or its derivative as substitution group, are listed as examples, and out of them anthanthrone compounds are preferably used from the point of a high generating efficiency of photo-carriers. As the P-type dye, azo compounds having sulfone group or carboxyl group, anthraquinone compounds, triphenylmethane compounds, nitro compounds, azine compounds, quinoline compounds and other various dyes and phthalocyanine compounds are listed as examples, out of which phthalocyanine compounds which are harmless and superior in processability are preferably used. Metal-free phthalocyanine or oxo-titanyl phthalocyanine in phthalocyanine compounds are most preferably used in view of the increased sensitivity in copying. As charge transporting substance contained in the charge transporting layer 2, fluorenone compounds such as tetracyanoethylene, 2,4,7-trinitro-9-fluorenone, nitro compounds such as 2,4,8-trinitro thioxanthone, dinitroanthracene, oxadiazole compounds such as succinic anhydride, maleic anhydride, dibromo maleic anhydride, 2,5-di(4-dimethyl aminophenyl)-1,3,4-oxadiazole, styrile compounds such as 9-(4-diethyl amino styrile)anthracene, carbazole compounds such as polyvinyl carbazole, pyrazorine compounds such as 1-phenyl-3-(p-dimethyl aminophenyl)pyrazorine, amine derivatives such as 4,4′,4″-tris(N,N-diphenyl amino)triphenyl amine, 4,4′-bis[N-phenyl-N-(3-methylphenyl)amino] diphenyl, conjugate unsaturated compounds such as 1,1-bis(4-diethyl aminophenyl)-4,4-diphenyl-1,3-butadiene, hydrazone compounds such as 4-(N,N-diethyl amino)benzaldehyde-N,N-diphenyl hydrazone, nitric ring compounds such as indole compounds, oxazole compounds, isoxazole compounds, thiazole compounds, thiadiazole compounds, imidazole compounds, pyrazole compounds and thoriazole compounds and condensed polycyclic compounds are listed. One or plural types of these charge transporting materials are used in combination. As a more preferred charge transporting substance, the combination of a butadiene derivative represented by general formula (I): wherein Ar₁ to Ar₄ are aryl groups, each of which may have substituent, and a hydrazone compound, preferably at least one selected from 4-(N,N-diethylamino) benzaldehyde-N,N-diphenylhydrazone and 4-(N,N-dimethylamino)benzaldehyde-N,N-diphenylhydrazone, is employed. In this case, as the combination ratio of both compounds, 10 to 300 parts by weight of hydrazone compound are preferably used to 100 parts by weight of butadiene derivative. By using charge transporting substances in such a combination, sensitivity of the laminated photosensitive material of this invention is increased, and generation of crystallization or cracks of the charge transporting layer is prevented. That is, the above butadiene derivative has a conjugated double bond and benzone rings, and thus π-electrons of this compound extend flatly, whereby the butadiene derivative is excellent in charge transporting capacity. However, a butadiene derivative is inferior in compatibility with a binding resin which is contained in the charge transporting layer, and has a high cohesion. Therefore, when using a solvent having high solubility such as an ester-type, ketone-type, or aromatic-type solvent in applying a coating solution for the charge generating layer, crystallization or cracks occur by so-called "solvent shock". On the other hand, a hydrazone compound, especially each of the two hydrazone compounds mentioned above, is superior to a butadiene derivative in compatibility to the binding resin, and thus functions as a plasticizer, so that the compaatibility of a butadiene derivative is stabilized to prevent crystallization or cracks. Also, since the solubility of a hydrazone compound to an alcohol-type solvent is about 0.1 to 2%, and the hydrazone compound has charge transporting capacity in itself, when using an alcohol-type solvent in applying a coating solution for the charge generating layer instead of an ester-type solvent or the like mentioned above, a part of the hydrazone compound is dissolved and diffused into the charge generating layer, and therefore injection of charge from the charge generating layer to the charge transporting layer is carried out smoothly, so that the sensitivity of the photosensitive material is increased. An example of a butadiene derivative is disclosed in Japanese Unexamined Patent Publication (kokai) No. 30255/1987, and especially in view of its excellent charge transporting capacity, a compound of the following formula (III) is preferably used. A hydrozone compound preferably used in this invention is represented by the following formula (II). wherein R is a C₁ to C₄ alkyl group, preferably a methyl group or an ethyl group. These hydrazone compounds have the most close oxidation potential to a butadiene derivative, so that the problem of charge being trapped, which occurs in the case of large difference of oxidation potential between two charge transporting substances, is prevented. In the charge transporting layer 2 and the charge generating layer 3, a binding resin is generally included in addition to the charge generating substances and charge transporting substances. As usable binding resins, for example, olefine polymers such as styrene polymers, acrylic polymers, styrene-acrylic copolymers, polyethylene, ethylene-vinyl acetate copolymers, chlorinated polyethylene, polypropylene, ionomer; polyvinyl chloride, vinyl chloride-vinyl acetate copolymer, polyester, alkyd resin, polyamide, polyurethane, epoxy resin, polycarbonate, polyarylate, polysulfone, diallyl phthalate resin, silicone resin, ketone resin, polyvinyl butyral, polyether, phenol resin, melamine resin, benzoguanamine resin, epoxyacrylate, urethane acrylate and polyester acrylate are listed. One or plural types of these binding resins are used in combination. Out of the charge transporting substances, poly-N-vinyl carbazole which is a photoconductive polymer can be used as a binding resin as well. Among these resins, polyarylate resin is preferably used for forming the charge transporting layer in view of its compatibility to the charge transporting substance and its membrane forming character. In the charge transporting layer 2 and the charge generating layer 3, sensitizers such as terfenyl, halo-naphthoquinones and acenaphthylene, antioxidants, ultraviolet absorbents and plasticizers may be included. The photosensitive material is produced by firstly forming a charge transporting layer 2 by applying a coating solution for the charge transporting layer containing the charge transporting substance, binding resin and solvent on the surface of conductive substrate 1, then, laminating a charge generating layer 3 on the charge transporting layer 2 by applying a coating solution for the charge generating layer containing P-type dyes and N-type dyes as charge generating substances, binding resin and solvent, and if required, laminating a surface protection layer 4 by applying a coating solution for surface protection layer containing binding resin and solvent. Upon forming the charge transporting layer 2, while the ratio of charge transporting substances to binding resin can be chosen appropriately, 30 to 500 parts by weight of binding resin are generally used to 100 parts by weight of charge transporting substances. The charge transporting layer 2 can be formed in an appropriate thickness, and it is generally formed approximately 10 to 30 µm thick. Examples of the solvent in which the charge transporting substnace is admixed with the binding resin include various solvents such as alcohols, cellosolves, esters, aliphatic hydrocarbons, aromatic hydrocarbons, halogenide hydrocarbons, ethers, dimethylformide or the like. On the other hand, upon forming the charge generating layer 3, 1 to 300 parts by weight of binding resin are generally used to 100 parts by weight of P-type and N-type dyes as charge generating substances. The charge generating layer 3 is generally formed approximately 0.3 to 1 µm in film thickness. A coating solution for the charge generating layer 3 is prepared by using the alcohol-type solvent. An example of the alcohol-type solvent is methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butyl alcohol or the like. Among these solvents, isopropyl alcohol or butyl alcohol is most preferably used. While the solubility of the butadiene derivative to these alcohol-type solvents is poor, the hydrazone compound has a solubility of about 0.1 to 2% of these alcohol-type solvents. Therefore, when coating, since a part of the hydrazone compound is dissolved and diffused into the charge generating layer, this prevents an electric barrier being generated in the interface between charge generating layer and charge transporting layer. Upon forming the charge generating layer 3, P-type and N-type dyes as charge generating substances can be directly formed on the charge transporting layer 2 by utilizing film forming methods such as vacuum evaporation and sputtering without using binding resin. The surface protection layer 4 laminated on the charge generating layer 3, if required, is formed with binding resin, especially silicone resin. If required, ultraviolet absorbents, antioxidants, and/or conductivity additives can be included in this surface protection layer 4. The surface protection layer 4 is generally formed approximately 0.1 to 10 µm in film thickness. Upon prepartion of coating solutions to form the charge generating layer 3, charge transporting layer 2 and surface protection layer 4, conventional methods such as a mixer, a ball mill, a paint shaker, a sand mill, an attriter and a supersonic dispenser can be used in combination. Upon applying the coating solutions, various conventional coating methods such as dip-coating, spray-coating, spin-coating, roller-coating, blade-coating, curtain-coating and bar-coating can be employed. As the conductive substrate 1 on which the layers are laminated, various conductive materials such as aluminium, aluminium alloys, copper, tin, platinum, gold, silver, vanadium, molybdenum, chromium, cadmium, titanium, nickel, palladium, indium, stainless steel, brass and other metallic single elements, plastics materials or glass on which a conductive layer of a metal, indium oxide, tin oxide is formed by a method such as evaporation are listed. The conductive substrate 1 can be formed in various shapes such as a sheet or drum. In order to improve the adhesiveness with the layers formed on the above surfaces, out of conductive materials, those having oxide surfaces, especially alumite treated aluminium, and more specifically alumite treated aluminium of which the alumite treated layer has 5 to 12 µm thickness and surface roughness is 1.5 S or less, is preferably used as conductive substrate 1. In order to further improve the adhesiveness between the conductive substrate 1 and the charge transporting layer 2, the surface of the conductive substrate 1 can be treated by surface treatment agents such as a silane coupling agent and a titanium coupling agent. EXAMPLES Referring now to the examples, the invention is described in detail below. Examples 1 to 5 Formulation of coating solution for charge generating layer Coating solutions for charge generating layer were formulated by the following components by changing the N/P ratio of content N of N-type dye to content P of P-type dye in the examples within 40/60 to 90/10 (N/P ratio) as shown in Table 1. Formulation of coating solution for charge transporting layer A coating solution for charge transporting layer was formulated in the following composition. Production of photosensitive material The coating solution for charge transporting layer was applied on an aluminium conductive substrate by dipping, then by drying it for 30 minutes at a temperature of 90°C, a charge transporting layer was produced. Successively, the coating solution for the charge generating layer was applied on the charge transporting layer by dipping, dried for 30 minutes at a temperature of 100°C to form a charge generating layer, and a positively charge electrophotographic photosensitive material of laminated type was produced. Comparison examples 1 to 5 As shown in Table 1, electrophotographic photosensitive materials were produced by the same method as in examples 1 to 5 except that N/P ratios less than 40/60 or more than 90/10 were used. Examples 6 to 10 Electrophotographic photosensitive materials were produced by the same method as in examples 1 to 5, except that a perylene compound shown by the following formula was used as the N-type dye in the place of dibromo anthanthrone. Comparison examples 6 to 10 As shown in Table 2, electrophotographic photosensitive materials were produced by the same method as in examples 6 to 10 except that N/P ratios less than 40/60 or more than 90/10 were used. Examples 11 to 15 Electrophotographic photosensitive materials were produced by the same method as in examples 1 to 5 except that an azo compound shown by the following formula was used as the N-type dye in the place of dibromo anthanthrone. Comparison examples 11 to 15 As shown in Table 3, electrophotographic photosensitive materials were produced by the same method as in examples 11 to 15 except that N/P ratios less than 40/60 or more then 90/10 were used. Examples 16 to 20 Electrophotographic photosensitive materials were produced by the same method as in examples 1 to 5 except that a copper phthalocyanine was used as the P-type dye in the place of metal-free phthalocyanine. Comparison examples 16 to 20 As shown in Table 4, electrophotographic photosensitive materials were produced in the same method as in examples 16 to 20 except that the N/P ratios less than 40/60 or more than 90/10 were used. Evaluation test In order to examine the charging characteristic of each photosensitive material for electrophotography obtained in the examples and comparison examples, each electrophotographic photosensitive material was positively charged and the surface potentials (V) were measured. In addition, by charging the electrophotographic photosensitive materials at 700V, exposing the photosensitive materials at an intensity of lumination of 771 lux through a 465 to 600 nm pass filter by using a halogen lamp, measuring the time till the surface potentials become half, the half-value exposures were calculated. Furthermore, the reflection density of a copy was measured when copying a red-coloured original having a reflection density of 0.7, and the value was taken as the evaluation value showing superiority or inferiority in copying red-coloured originals. The surface potentials, half-value exposures and evaluation values of copying performance of red-coloured originals are shown in Tables 1 to 4. As known from Table 1, in the electrophotographic photosensitive materials of the examples 1 to 5 in which the N/P ratios are between 40/60 and 90/10, both the half-value exposures and copying performances of red-coloured originals show values that can be practically used, while in the electrophotographic photosensitive materials of the comparison examples 1 to 5 in which the N/P ratios are out of the above range, at least one of the half-value exposure and copying performance of red-coloured originals is inferior. In other words, in the comparison examples 1 to 3, both the half-value exposure and copying performance of red-coloured originals are inferior, and the comparison examples 4 and 5 are superior in reproductivity of red-coloured originals but have a large half-value exposure. From Tables 2 to 4 which show the results of examinations by using different P-type dye or N-type dye from the examples 1 to 5, it is found that the same results were obtained even by changing P-type or N-type dyes. Examples 21 to 25 Formualtion of coating solution for charge transporting layer As charge transporting substance, 1,1-diphenyl-4, 4-(4-N,N-diethylamino)diphenyl-butadiene represented by formula (III) (hereinafter referred to as A compound) and 4-(N,N-diethylamino)benzaldehyde-N,N-diphenylhydrazone (hereinafter referred to as B compound) were used, and as a binding resin, polyarylate (prepared by Unitika Ltd., trade name "U-100") was used. Contents of the charge transporting substances against 100 parts by weight of the binding resin are shown in Table 5. Furthermore, 900 parts by weight of methylene chloride were admixed as solvent to form a coating solution. Formulation of coating solution for charge generating layer A coating solution for charge generating layer was formulated in the following composition by using an alcohol-type solvent shown in Table 5. Production of photosensitive material The coating solution of the charge transporting layer was applied on an aluminium conductive substrate by dipping, then by drying it for thirty minutes at 90°C, a charge transporting layer was produced. Successively, the coating solution for charge generating layer was applied on the charge transporting layer by dipping, dried for thirty minutes at 110°C to form a charge generating layer having a thickness of 0.5µm, photosensitive material was produced. Comparison examples 21 to 25 Electrophotographic photosensitive materials were produced by the same method as in examples 21 to 25 except that "A compound" and "B compound" which are charge transporting substances were used in the ratio shown in Table 5, and a solvent for the charge generating layer shown in Table 5 was used. Examples 26 to 30 Electrophotographic photosensitive materials were produced by the same method as in examples 21 to 25 except that 4-(N,N-dimethylamino)benzaldehyde-N,N-diphenylhydrazone was used as "B compound" in the place of 4-(N,N-diethylamino)benzaldehyde-N,N-diphenylhydrazone. Comparison examples 26 to 30 Electrophotographic photosensitive materials were produced by the same method as in examples 26 to 30 except that "A compound" and "B compound" which are charge transporting substances were used in the ratio shown in Table 6, and a solvent for the charge generating layer shown in Table 6 was used. Evaluation test Surface potential (V) and half-value exposure (lux · sec) were determined by the same method as in examples 1 to 20. Results are shown in Tables 5 and 6. In these Tables MIBK means methyl isobutyl ketone. As seen from Tables 5 and 6, comparison examples 21 and 26 are inferior in sensitivity, since these comparison examples do not contain B compound, and use alcohol solvent which does not fully dissolve the A compound (butadiene compound). Also, in comparison examples 22 and 27, cracks and crystallizations occur, and thus surface potentials and half-value exposures cannot be determined, since other solvents except for alcohol solvent were used. For the same reason, in comparison examples 23, 24, 28 and 29, cracks and crystallizations occurred. Furthermore, comparison examples 25 and 30 do not have sufficient sensitivity, since the charge transporting substance is B compound only. On the other hand, photosensitive materials obtained in examples 21 to 25 and 26 to 30 were superior to the comparison examples in sensitivity without generating cracks and crystallizations, since A and B compounds are contained in charge transporting layer, and alcohol solvent is used as the solvent for the charge generating layer. Example 31 As a coating solution for the charge generating layer, the same solution as in example 3 (P-type dye : N-type dye = 30 : 70, solvent is 2000 parts by weight of isopropyl alcohol) was used, as a coating solution for the charge transporting layer, the same solution as in example 27 (A compound : B compound = 70 : 30, B compound is 4-(N,N-dimethylamino-benzaldehyde- N,N-diphenylhydrazone) was used, and then photosensitive material was produced in the same method as "Production of photosensitive material" in Example 3. Example 32 Photosensitive material was produced in the same method as in example 31 except that n-butyl alcohol was used in the place of isopropyl alcohol as solvent for charge generating layer, and that 4-(N,N-diethylamino)benzaldehyde-N,N-diphenylhydrazone was used in the place of 4-(N,N-dimethylamino)benzaldehyde-N,N-diphenylhydrazone. Example 33 Photosensitive material was produced in the same method as in example 31 except that oxo-titanyl phthalocyanine was used as P-type dye in the place of metal-free phthalocyanine, and the 4-(N,N-diethylamino) benzaldehyde-N,N-diphenylhydrazone was used in the place of 4-(N,N-dimethylamino)benzaldehyde -N,N-diphenylhydrazone. Example 34 Photosensitive material was produced in the same method as in example 33 except that n-butyl alcohol was used in the place of isopropyl alcohol as solvent for charge generating layer. Examples 35 to 39 Electrophotographic photosensitive materials were produced in the same method as in example 34 except that as shown in Table 7, a ratio of P-type dye (oxo-titanyl phthalocyanine) : N-type dye (dibromoanthanthrone), alcohol solvents for producing a charge generating layer, a ratio of A compound : B compound are changed. Values in ratios of P : N and A : B shown in Table 7 means "parts by weight" against 100 parts by weight of the binding resin. Evaluation test Surface potentials (V), half-value exposure (lux ·sec) and copying performance of red-coloured originals were determined by the same methods as in examples 1 to 20. Results are shown in Table 7. In Table 7, "P : N" means the ratio of P-type dye and N-type dye. Also, "A:B" means the ratio of A compound and B compound. As seen from Table 7, the electrophotographic photosensitive materials of examples 31 to 34 are remarkably superior in sensitivity (please see half-value exposure).

Claims: An electrophotographic photosensitive material comprising a charge transporting layer (2) and a charge generating layer (3) which are laminated in this order on a conductive substrate (1), the charge transporting layer (2) containing, as charge transporting substances, a butadiene derivative represented by the general formula (I): wherein Ar₁ to Ar₄ are aryl groups, each of which may have a substituent, and a hydrazone compound represented by the general formula (II): wherein R is a C₁ to C₄ alkyl group, and wherein the charge generating layer (3) contains an N-type dye and a P-type dye in a ratio of 40/60 to 90/10 (N-type dye/P-type dye) by weight, wherein the N-type dye is an anthanthrone compound, or a perylene compound, or an azo compound, and wherein the P-type dye is a phthalocyanine compound, anthraquinone compound, triphenylmethane compound, nitro compound, azine compound or quinoline compound. An electrophotographic photosensitive material according to claim 1, wherein the charge generating layer contains 1 to 300 parts by weight of a binding resin to 100 parts by weight of the sum of N-type dye and P-type dye. An electrophotographic photosensitive material according to claim 1, wherein the film thickness of the charge generating layer is 0.3 to 1 µm. An electrophotographic photosensitive material according to claim 1, wherein the phthalocyanine compound is oxotitanyl phthalocyanine. An electrophotographic photosensitive material according to claim 1, wherein the hydrazone compound is at least one selected from the group consisting of 4-(N,N-diethylamino) benzaldehyde-N,N-diphenylhydrazone and 4-(N,N-dimethylamino) -benzaldehyde-N,N-diphenylhydrazone An electrophotographic photosensitive material according to claim 1, wherein the butadiene derivative is represented by the following formula (III). An electrophotographic photosensitive material according to claim 1, wherein the charge generating layer is formed by applying a eoating solution, which is prepared by using an alcohol-type solvent, on the charge transporting layer. An electrophotographic photosensitive material according to claim 7, wherein the alcohol-type solvent is an isopropyl alcohol or n-butyl alcohol. An electrophotographic photosensitive material according to claim 7, wherein the alcohol-type solvent is n-butyl alcohol.

Inventors: HANATANI YASUYUKI, MIZUTA YASUFUMI, NAKATANI KANAME, HANATANI, YASUYUKI, MIZUTA, YASUFUMI, NAKATANI, KANAME
Applicants: MITA INDUSTRIAL CO LTD, MITA INDUSTRIAL CO. LTD.
Application year: 1989
Main classification: G03G5
IPC codes: G03G5