Acetal copolymers with backbone amine groups

Abstract: Acetal copolymers of trioxane with epoxy functional groups are obtained by copolymerizing trioxane with 5,6-epoxy-­ 1,3-dioxepane. The epoxide group in the polymer chain provides a highly reactive functional group for further modification. Acetal copolymers with backbone epoxide groups exhibit toughness and thermal stability. The backbone epoxide groups can also be aminated in a one step hydrolysis-amination process.

Description: BACKGROUND OF THE INVENTION Polyacetal copolymers are technically important macromolecules competitive with metals, ceramics and nylons in many applications. In the current technical processes, they are prepared by copolymerization of trioxane, with a comonomer such as ethylene oxide, dioxolane or butanediol formal. Each such copolymer molecule carries a maximum of two functional groups, e.g. hydroxyl end groups. For purposes such as preparation of graft copolymers and polymers with chemically bound stablizers, it is desirable to synthesize polyacetals with higher levels of functional groups. It is an object of this invention to prepare polyacetal copolymers of trioxane that have stability equivalent to or greater than that of commercially available acetal copolymer while at the same time having functional groups which may be useful for further modifications or the attachment of additives. EP-A-0,033,426 discloses compounds of the formula wherein Z is azido or HNW, and wherein W is hydrogen or a substituted organic radical of from 1 to 12 carbon atoms, eg hydrocarbyl, and the Rs which may be the same or different are hydrogen or an organic radical. In conventional acetal resin products, additives such as amidine thermal stabilizers and the like tend to reside in the amorphous regions of the polymer. Since the distribution of such non-crystalline areas is spatially random, the distribution of additives is often not optimal in terms of macroscopic properties. If functional sites can be provided at regular or semi-regular intervals (e.g. random copolymer) such that stabilizers or impact modifiers could be attached at a predetemined locus of points within the resin, then superior and more uniform properties could be achieved. This approach may be particularly advantageous since the crystal structure of acetal is such that additives are sterically obstructed from the crystalline areas. It therefore may be desirable to provide polymer backbone moieties that may disrupt the polymer's crystal structure in a controlled manner and provide a locus for attachment of additives. Polyacetal copolymers with such backbone functional groups would be useful in many important applications such as: a) preparing trioxane copolymers with chemically bonded stabilisers; b) preparing trioxane copolymers with chemically attached impact modifiers; c) preparing grafted copolymers of trioxane as compatibilizers with existing commercial acetal copolymer blends; d) preparing copolymers amenable to surface modifications; and e) preparing crosslinked copolymers. SUMMARY OF THE INVENTION The present invention is concerned with compounds of the formula: wherein R is diethylene-triamine, diethylamine, ethylenediamine or tetraethylene-pentamine. Also according to the invention an acetal copolymer containing backbone amine groups is prepared by a method Comprising copolymerizing trioxane with the compound having the formula wherein R is an amine. This invention also includes the copolymer obtainable by this method. BRIEF DESCRIPTION OF THE FIGURES Figure 1 illustrates a TGA Thermogram of TX-EPDXPA copolymer after one-step hydrolysis plus amination. Figure 2 illustrates a proton-NMR spectrum of TX-EPDXPA copolymer in DMSO-d₆. DETAILED DESCRIPTION OF THE INVENTION EXAMPLE 1 Amination of 5,6-epoxy-1,3-dioxepane , 5,6-epoxy-1,3-dioxepane (EPDXPA) 0.58g. (FW 116, 0.005 mole) and 0.55 ml. of diethylene-triamine were dissolved in 30 ml. of methanol. The mixture was refluxed at 75°C for 5 hours. The solvent was removed by a rotary evaporator and the unreacted amine was separated under vacuum at 100°C. The product was a brown gummy material. The same procedure was carried out for aminations with diethylamine, ethylenediamine and tetraethylenepentamine. PREPARATION 1 Copolymerization of Trioxane with 5,6-epoxy-1,3 dioxepane In a dry flask (Kjeldahl, 100 ml.) were placed 12.7g. of trioxane and 1.41g. (10%, of 5,6-epoxy-1,3-dioxepane). The flask was capped with a serum stopper. After removing the air and the dissolved gas under vacuum from the reaction mixture, the flask was flushed with nitrogen gas. The contents were melted and mixed together with a magnetic stirrer in an oil bath (60-65°C). Boron-trifluoride etherate (0.05 ml.) was then injected through the serum stopper into the flask. The color of the solution changed from brown to white. Within about fifteen minutes the solution became immobilized due to the growth of the polymer throughout the flask. The reaction was allowed to proceed at 60°c for 20 hours. At the conclusion of polymerization, the TX-EPDXPA polymer was removed and ground into small chunks. The crude polymer (6.9 gm.) was washed once with 40 ml. solution of 5% triethanolamine in methanol and then three times with methanol. The copolymer was dried under vacuum at 40°C. The incorporation of epoxide group through the copolymerization of trioxane with EPDXPA was substantiated by the 3.3 ppm proton absorption in proton NMR spectra and the 57.5 ppm absorption in C¹³ NMR spectra. When this copolymerization reaction was carried out with a high EPDXPA comonomer feed, e.g. 16% feed, a cross-linked copolymer with extreme toughness was produced. EXAMPLE 2 The amine-modified EPDXPA comonomers described above in Example 1 may also be used in copolymerizations with trioxane to produce acetal copolymers with backbone amino groups. PREPARATION 2 One-step Hydrolysis and Amination of Epoxidized Copolymer The epoxide group in the polymer chain provides a reactive site for further modification. This example demonstrates that the amination of the epoxide group can take place while the copolymerization product of Preparation 1 is being hydrolyzed to remove its unstable end groups. Into a 250 ml., two necked flask fitted with a air cooled condenser and a thermometer were placed 4g. epoxidized copolymer, DMF (40 ml.), benzyl alcohol (20 ml.) and 0.9 ml. diethylenetriamine. The mixture was stirred by means of a magnetic stirrer and refluxed at 170°C for 30 minutes. Refluxing conditions were maintained until visible evolution of formaldehyde stopped. The reaction mixture changed in color from yellow to brown. The solution was cooled in order to precipitate solid material. The solid was then filtered and washed three times with acetone. The polymer was filtered and dried at 40°C under vacuum. The yield was 2.6 gms. EXAMPLE 3 When the TX-EPDXPA copolymer was aminated in the one-step hydrolysis plus amination process a copolymer of unusually high thermal stability was produced. A Carbon 13 NMR spectrum of a sample from such a one step procedure evidenced the amination of the TX-EPDXPA copolymer. The TGA thermogram of such an animated polymer shows superior thermal stability to that of commercially available trioxane-ethylene oxide polymer. (Fig. 1). EXAMPLE 4 Amination of TX-EPDXPA Into a 50 ml round bottom flask fitted with an air cooled condenser were placed 1 g of copolymer (TX EPDXPA 1% incorporation) and 10 ml DMF. The polymer was dissolved in the solvent by heating at 150°C. Phenethylamine (1 ml) was then added directly and the mixture was stirred at 150°C for 2 hours. The reaction mixture gradually became a brown solution. The solution was cooled to precipitate solid material. The aminated polymer was then filtered and washed three times with acetone. The polymer was filtered and dried at 40°C under vacuum. Reaction of TX-EPDXPA with dodecylamine was also performed. Proton NMR spectrum of the product of the reaction of the epoxy copolymer with dodecylamine indicated that some of the amine reacted with the backbone epoxy-groups even though most of the epoxy groups remained unreacted. Only a low level of the (-CH₂-)₁₀ group was found, indicating the low reactivity of back bone epoxy functional groups. PREPARATION 3 The mole percent epoxide incorporation into the acetal copolymers was derived from peak areas of the proton NMR spectrum as shown in Figure 2 as follows: The following table summarizes the feed of EPDXPA vs. incorporation of EPDXPA in mole percent for TX-EPDXPA: Epoxide Mole % Sample Feed % EPDXPA Incorporation % EPXDPA #40 3.9 1.1 #42 5.5 1.5 #27 7.9 7.0 At 7.9% EPDXPA feed, a portion of the copolymer was not soluble. At 16% feed, a highly cross-linked copolymer with extreme toughness was produced. EXAMPLE 5 The TX-EPDXPA copolymer of Preparation 3 was aminated with phenythylamine. Proton-NMR spectrum were performed which indicated an absorption peak at 1.2ppm. due to the methylene protons of the amine; and a 7.2ppm peak corresponding to the aromatic protons. For a copolymer with 1% epoxide in corporation, a 0.1% mole amination was obtained.

Claims: A compound of the formula: wherein R is diethylene-triamine, diethylamine, ethylenediamine or tetraethylene-pentamine. A method for producing an acetal copolymer containing backbone amine groups which comprises copolymerizing trioxane with a compound of the formula wherein R is an amine. The copolymer obtainable by the method of claim 2.

Inventors: AUERBACH ANDREW, PAUL JAMES L, WANG SHIAN S, YANG NAN-LOH, ZHENG YONG CHANG, AUERBACH, ANDREW, PAUL, JAMES L., WANG, SHIAN S., YANG, NAN-LOH, ZHENG, YONG CHANG
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1989
Main classification: C07D321
IPC codes: C08G59, C08G77, C08G2, C08G18, C08G4, C07D321, C07D493