Aluminum titanate ceramic sintered body

Abstract: A ceramic sintered body having a Young's Modulus of not less than 1,600 kg/mm² produced by sintering 1 to 10 weight % of magnesium oxide, 0.5 to 10 weight % of silicon oxide, the remainder being substantially aluminum titanate.

Description: This invention relates to a ceramic sintered body having excellent strength and showing little change of dimensions produced by thermal treatment, and having a high melting point and a low thermal expansion. Especially, this invention relates to a ceramic sintered body for structural uses, e.g. as a portliner for an internal combustion engine. Aluminum titanate is a specific ceramic having a high melting point and showing a low thermal expansion. Because of these characteristics, attempts have been made to utilize it practically. However, it is subject to the problem that its mechanical strength is low, since it is difficult to obtain a fine sintered body, and it is also subject to thermal instability in that it undergoes thermal cracking when heated up to 125°C. Also, thermal expansion and contraction of the sintered body are affected by the thermal treatment history, and its strength is very adversely affected by repeated heating and cooling. This thermal treatment effect is the result of the aluminum titanate crystals having anisotropic thermal expansion characteristics, with the result that fine cracks are produced in the sintered body by a thermal treatment history of cooling after heating, thereby adversely affecting the strength of the sintered body. This formation of cracks on cooling occurs every time the ceramic sintered body is subjected to heating and cooling after sintering. It therefore causes problems of loss of strength and dimensional stability, particularly in cases where the sintered body is subjected to a cyclical heat treatment. Various additives have been introduced in attempts to ameliorate these difficulties of aluminum titanate. For example, published Japanese Patent No. SHO.56-7996 discloses low thermal expansion ceramics containing 0.05 to 10.0 weight % of at least one of silicon and zirconium, calculated as SiO₂ and ZrO₂, with respect to the aluminum titanate. It is stated that by the introduction of prescribed contents of silicon and zirconium into this ceramic, grain growth is controlled, resulting in a ceramic which is thermally stable and which shows little strength deterioration after a history of thermal treatment. The Journal of the Chemical Society of Japan (Nippon Kagaku Kaishi) (1981 No. 10) pages 1647 to 1655 reports the effects of various additives under the title "Effect of additives on the properties of aluminum titanate sintered bodies". This report describes the results of attempts to improve the cracking resistance in the low temperature region by blending in additives in order to suppress the growth of aluminum titanate crystals, while promoting sintering, increasing the mechanical strength and maintaining an apparent low thermal expansion. The additives investigated were Li₂O, B₂O₃, SiO₂, MgO, Cr₂O₃, Fe₂O₃, and ZrO₂. The effect of these additives is examined and summarized. Whereas MgO, Fe₂O₃ and ZrO₂ have the effect of increasing the density of the sintered body, Cr₂O₃ does not necessarily increase the density. Also, although Li₂O and B₂O₃ showed an effect of promoting increased fineness, SiO₂ showed a sintering promoting effect. Furthermore, published Japanese Patent No. SHO.62-32155 discloses a composite with metal incorporating a ceramic material obtained by sintering a raw material whose chemical composition is: 50 to 60 weight % Al₂O₃, 40 to 45 weight % TiO₂, 2 to 5 weight % kaolin (corresponding to Al₂O₃.2SiO₂), and 0.1 to 1 weight % magnesium silicate, and having a particle size less than 6 x 10⁻⁷m (0.6 micron). This patent document suggests that the thermal and mechanical properties of the aluminum titanate are improved by using a combination of aluminum silicate-containing and magnesium silicate-containing additives. EP-A-0 285 312 and Sprechsaal vol 108, No 12, December 1985 also disclose aluminium titanate ceramics containing silicon and magnesium oxides. Although in such ceramic sintered bodies, various properties of the aluminum titanate are improved, for practical use there remains a need for aluminium titanate ceramics exhibiting even greater improvements in properties such as strength and thermal variation in length. For example, although it would appear that the combination of sintering adjuvants of the above-mentioned published Japanese Patent No. SHO.62-32155 is desirable, experience has shown that it is extremely difficult to obtain ceramic bodies exhibiting uniformly satisfactory strength and thermal expansion characteristics with the form of starting materials and additive contents set out in Japanese Patent No. SHO.62-32155. Summary of the Invention It is therefore the object of the present invention to provide an aluminum titanate ceramic sintered body that has high strength, and wherein the deterioration of mechanical strength produced by a cyclic thermal treatment history is slight, without impairing the high melting point and low thermal expansion properties possessed by aluminum titanate. With regard to strength, the value of three point bending strength is preferred to be no less than 2.5 x 10⁶ kg.m⁻² (2.5 kg/mm²), preferably no less than 3 x 10⁶ kg.m⁻² (3.0 kg/mm²), most preferably no less than 3.5 x 10⁶ kg m⁻² (3.5 kg/mm²). The value of the Young's Modulus is no less than 1.6 x 10⁶ kg.m⁻² (1600 kg/mm²), preferably more than 2 x 10⁶ kg.m⁻² 2000 kg/mm². With regard to the thermal variation in length on cyclic heat treatment, the value of the thermal variation in length is preferred to be less than 0.33%, most preferably less than 0.25%. These objects are achieved by providing a ceramic sintered body having a Young's Modulus of not less than 1600 Kg/mm² produced by sintering 1 to 10 weight % of magnesium oxide (MgO), and 0.5 to 10 weight % of silicon oxide (SiO₂), the balance being substantially aluminum titanate, the powder having a mean particle diameter not greater that 8 x 10⁻⁶ m (8 µm) and preferably a mean particle diameter of 6 x 10⁻⁷ to 8 x 10⁻⁶ m (0.6 to 8.0 µm) Detailed Description of the Preferred Embodiments As a result of repeated investigation of sintering adjuvants of aluminum titanate, the inventors discovered that a ceramic sintered body obtained by sintering aluminum titanate to which prescribed amounts of MgO and SiO₂, respectively, had been added had excellent characteristics. Addition of MgO increases the strength of the sintered body, but, if MgO is added on its own, it produces a concomitant increase in the thermal expansion rate of the sintered body. A considerable increase in the strength of the sintered body and a low thermal expansion can be obtained if more than 0.5 weight % SiO₂ is added. So far as the effect of addition is concerned, a range up to 10 weight % is desirable. In respect of both of these, the particularly preferred range is from 1 to 6 weight %. These sintering adjuvants are added to aluminum titanate raw material powder obtained by calcining a mixture of aluminum oxide (Al₂O₃) and titanium oxide (TiO₂) in the prescribed proportion, and then grinding. The molar ratio of the Al₂O₃ and TiO₂ is preferably in the range from 1.3:0.7 to 0.8:1.2. Also, the mean particle diameter of the aluminum titanate raw material powder is preferably 0.6 x 10⁻⁶ to 7 x 10⁻⁶m (0.6 to 7 microns). If the powder is too fine, a uniform mixture is difficult to obtain. Examples 1 through 6 Two weight % of MgO and 1 weight % of SiO₂ were blended with aluminum titanate (Al₂TiO₅) raw material wherein the molar ratio of Al₂O₃ to TiO₂ was 1.1:0.9 and the mean grain size was 2.55 microns. The mixture was then formed at a forming pressure of 0.1 kg.m⁻² (1,000 kg/cm²), followed by sintering for 2 hours at 1,500°C. The thermal expansion rate, the thermal variation in length, and the strength were determined for the resulting sample (sample number 1). The measured values are shown in the following Table 1 together with the corresponding properties of similarly obtained samples containing different amounts of sintering adjuvants. The "thermal variation in length" is defined as (l max - l min )/l₀, expressed as a percentage, where the original length of the sample is l₀, its maximum length when heated from 20°C to 1,000°C is l max , and its minimum length is l min . Sample Number 1 2 3 4 5 6 Al₂TiO₅ Mean Grain Size (µm) m (2.55) 2.55 x10⁶ (2.55) 2.55 x10⁶ (2.55) 2.55 x10⁶ (2.55) 2.55 x10⁶ (2.55) 2.55 x10⁶ (8.06) 8.06 x10⁶ Sintering Adjuvant (weight-%) Mg0 2 2 2 1 0 0 Si02 1 2 4 4 0 0 Sintering Conditions (C°) 1500 1500 1500 1500 1500 1500 (hr) 2 2 2 2 2 2 Density (g/cm³) 3.44 3.37 3.30 3.19 3.40 2.16 Bending strength (kg/mm²) kg.m⁻² (5.32) 5.32 x10⁶ (4.95) 4.95 x10⁶ (5.16) 5.16 x10⁶ (3.73) 3.73 x10⁶ (1.21) 1.21 x10⁶ (0.22) 0.22 x10⁶ Thermal Expansion Rate 20-1000°C 1.11 x10⁻⁶ 0.47 x10⁻⁶ 0.79 x10⁻⁶ 0.98 x10⁻⁶ 0.18 x10⁻⁶ - Thermal variation in length (%) 0.24 0.21 0.19 0.22 0.37 - Young's Modulus (kg/mm²) kg m⁻² (2.9x10³) 2.9x10⁹ (2.8x10³) 2.8x10⁹ (2.8x10³) 2.8x10⁹ (2.1x10³) 2.1x10⁹ (0.5x10³) 0.5x10⁹ (0.1x10³) 0.1x10⁹ 1 Kg/mm² = 9,81 Megapascal As can be seen from Table 1, in the case of the embodiments of this invention (sample numbers 1 to 4), the bending strength and Young's modulus were larger and the thermal variation in length was smaller than in the case of the comparative examples (sample numbers 5 and 6). Examples 7 through 22 Sintering was carried out 2 hours at 1,500°C after forming samples in each case at a forming pressure of 0.1 x 10⁻⁴ kg.m⁻² (1,000 kg/cm²), varying the blending amounts of Mg0 and Si0₂ sintering adjuvants and using aluminum titanate raw material having an Al₂O₃:TiO₂ molar ratio of 1.1:0.9 (Al₂TiO₅), but with different mean grain sizes, obtained by varying the grinding period of the raw material. The three point bending strength, thermal expansion rate (20 to 1,000°C), thermal variation in length, and Young's Modulus were measured for the resulting samples. The results are shown in Tables 2 to 5. Three Point Bending Strength: (kg/mm²) No. Adjuvant (wt.%) Mean Grain Size (µm) Mg0 Si0₂ 8.06 6.54 4.29 2.55 1.54 7 0 0 0.22 0.15 1.28 1.21 -- 8 0 1 0.54 0.60 1.24 1.88 -- 9 0 2 0.54 0.77 1.94 1.78 -- 10 0 4 0.80 1.02 1.81 2.76 -- 11 1 0 1.33 1.90 1.64 2.93 -- 12 2 0 1.68 1.98 2.40 3.30 -- 13 1 1 2.37 3.71 4.10 3.46 5.07 14 1 2 2.61 3.42 3.21 3.18 4.66 15 1 4 2.77 3.06 3.42 3.73 4.79 16 2 1 3.36 3.99 5.00 5.32 5.53 17 2 2 3.14 4.08 4.38 4.95 5.17 18 2 4 2.48 3.30 4.31 5.16 5.24 19 2 6 -- -- -- 4.70 5.70 20 4 1 -- -- -- 5.32 5.78 21 4 2 -- -- -- 4.83 5.51 22 4 4 -- -- -- 4.17 4.31 1 Kg/mm² = 9,81 Megapascal Thermal Expansion Rate: (x10⁻⁶) No. Adjuvant (wt.%) Mean Grain Size (µm) Mg0 Si0₂ 4.29 2.55 1.54 7 0 0 -1.13 -0.18 -- 9 0 2 -- 0.47 -- 12 2 0 -- 1.02 -- 13 1 1 -- -- 0.80 14 1 2 -- 0.63 -- 15 1 4 -- 0.98 1.45 16 2 1 -- 1.11 1.30 17 2 2 -- 0.47 0.96 18 2 4 0.63 0.79 1.30 19 2 6 -- 1.14 1.54 20 4 1 -- 1.22 1.73 22 4 4 -- 0.73 1.19 Thermal Variation in Length: (%) No. Adjuvant (weight %) Mean grain size (µm) MgO SiO₂ 4.29 2.55 1.54 7 0 0 0.19 0.20 -- 9 0 2 -- 0.33 -- 12 2 0 -- 0.36 -- 13 1 1 -- -- 0.26 14 1 2 -- 0.26 -- 15 1 4 -- 0.22 0.28 16 2 1 -- 0.24 0.27 17 2 2 -- 0.21 0.25 18 2 4 0.19 0.17 0.22 19 2 6 -- 0.20 0.22 20 4 1 -- 0.22 0.27 22 4 4 -- 0.22 0.29 Young's Modulus: x10⁹ kg.m⁻² (x10³ kg/mm²) No. Adjuvant (wt.%) Mean grain size (µm) x10⁻⁶m MgO SiO2 8.06 6.54 4.29 2.55 1.54 7 0 0 0.1 0.1 0.6 0.5 -- 8 0 1 0.3 0.3 0.6 1.0 -- 9 0 2 0.3 0.4 1.0 1.0 -- 10 0 4 0.3 0.5 1.0 1.5 -- 11 1 0 0.7 1.0 1.0 1.5 -- 12 2 0 0.9 1.1 1.3 1.8 -- 13 1 1 1.3 2.0 2.2 1.9 2.7 14 1 2 1.4 1.8 1.7 1.7 2.3 15 1 4 1.5 1.6 1.8 2.0 2.6 16 2 1 1.8 2.1 2.7 2.9 3.0 17 2 2 1.7 2.2 2.4 2.8 2.8 18 2 4 1.3 1.8 2.3 2.8 2.8 19 2 6 -- -- -- 2.5 3.0 20 4 1 -- -- -- 2.9 3.1 21 4 2 -- -- -- 2.6 3.0 22 4 4 -- -- -- 2.2 2.3 1 Kg/mm² = 9,81 Megapascal As is clear from Table 2 and Table 5, the embodiments of this invention (sample numbers 13 to 22) showed high strength, high Young's Modulus and, in particular, those embodiments where the mean grain size of the aluminum titanate raw material was less than 7 µm(microns) showed superior strength and high Young's Modulus characteristics. Also, as shown in Table 3 and Table 4, in the embodiments of this invention, the aluminum titanate had excellent low thermal expansion rate and small thermal variation in length characteristics. Thus, as described above, by means of this invention, aluminum titanate ceramic sintered bodies can be obtained that have a high strength and a small thermal variation in length when subjected to cyclic thermal treatment, without impairing the high melting point and low thermal expansion possessed by aluminum titanate.

Claims: A ceramic sintered body having a Young's Modulus of not less than 1.6 x 10⁹ kg.m⁻² (1,600 kg/mm²) produced by sintering a raw material powder containing magnesium oxide, silicon dioxide and the remainder being substantially aluminium titanate, characterised in that the amount of magnesium oxide is 1 to 10 weight %, the amount of silicon dioxide is 0.5 to 10 weight %, and in that said powder has a mean particle diameter not greater than 8 x 10⁻⁶m (8µm). A body according to claim 1, wherein the Young's Modulus of said body is greater than 2 x 10⁹ kg.m⁻² (2,000 kg/mm²). A body according to claim 1 or 2, wherein said body is formed from a raw material powder having a mean particle diameter of from 6 x 10⁻⁷ to 8 x 10⁻⁶m (0.6µm to 8µm). A body according to any preceding claim, wherein said body is formed from a raw material powder having a mean particle diameter not greater than 7 x 10⁻⁶m (7µm). A body according to any preceding claim, wherein said body is formed from a raw material powder having a mean particle diameter of from 6 x 10⁻⁷ to 7 x 10⁻⁶m (0.6µm to 7µm). A body according to any preceding claim, wherein the aluminium titanate is a mixture of aluminium oxide and titanium oxide in an A1₂O₃:TiO₂ molar ratio of from 1.3:0.7 to 0.8:1.2. A body according to any preceding claim having a thermal variation in length, as herein defined, which is less than 0.33%. A body according to claim 7 wherein said thermal variation is less than 0.25%.

Inventors: KAMEDA TSUNEJI C O PATENT DIVI, KAMEDA, TSUNEJI C/O PATENT DIVISION
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1989
Main classification: C04B35
IPC codes: C04B35