METHOD AND DEVICE FOR THE CONDITIONING OF THE TEMPERATURE OF A PREFORM

Abstract: The invention relates to a method for temperature conditioning a blank (10) of plastic material, a conditioning mandrel (20) being placed within the blank (10) and thereafter expanded to reliable abutment against the inner surface of the blank. The mandrel is thereafter displaced back to its starting position. The outer surface of the mandrel is adjusted to and maintained at a certain temperature, whereby, during the abutment, an energy exchange takes place between the blank and the mandrel for adjusting the material temperature of the blank. At high temperatures of the mandrel, the mandrel is displaced out of the blank after such short time that the plastic material in the region of the abutment surface never passes the critical temperature at which tacking between the plastic material and/or thermal crystallization of the plastic material occurs to any appreciable degree. As a rule, this process is repeated one or more times. In an apparatus according to the invention, the dimensions of the conditioning mandrel (20) and the blank (10) are adapted to one another such that, in the position within the blank, the outer surface of the conditioning mandrel abuts, after expansion, against the inner surface of the blank. Control and regulation means are provided for abutment of the conditioning mandrel against the inner surface of the blank during an adjustable time interval.

Description: Method and a device for the conditioning of the temperature of a preform. The present invention relates to a method and an apparatus accordinc to the preambles of the independent claims. It is previously known to reform, using a mechanical tool, a blank of plastic material into an intermediate preform cr into a container. Thus, it is known to reform ε tubular blank into an intermediate preform by extending the blank in its axial direction and during simultaneous orientation of its material. This takes place once the material in the blank has been set at an elevated temperature, whereafter, for example, a rod displaces the bottom of the blank relative to the mouth portion of the blank. US—A— .5όϋ, 6ύ describes an alternative technique in which a tubular blank is reformed into an intermediate preform in that the material of the blank passes through a gap in a mechanical forming tool, the C2D width being less than the material thickness of the blank. In such instance, a transition zone is movec in the axial direction of the blank between substantially amorphous plastic material (thick material) and oriented material (thin material) under the reduction of the amount of amorphous (thick) material and increase of the amount of oriented (thin) material. On displacement of the transition zone, the plastic material is oriented. Said patent specification describes an embodiment in which the gap is formed between a drawing ring and a mandrel located within the blank. Displacement of the transition zone is realized in that the mandrel displaces a blank placed on the mandrel in relation to the drawing ring, amorphous material in the blank passing through the gap and being oriented in the direction of displacement of the transition zone. The above-described orientation of the plastic material in a blank by means of a mandrel and a drawing ring is generally preceded by a setting of the temperature of the material at an elevated level. For, example, polyethyleneterefthaiate, hereinafter generally abbreviated to PET, a temperature is normally selected which slightly exceeds the glass transition temperature of the material, or a temperature in the region of or slightly less than the glass transition temperature of the material. Hereinafter, the designation TG will generally be employed to indicate the glass transition temperature of the plastic material. On entry into the above- mentioned gap, the material is generally at the elevated temperature. The material then passes through the gap, it being required that the contact surface of the material against the drawing ring is at a temperature less than a certain maximum temperature. This permitted maximum temperature is determined by the material in the drawing ring which forms an abutment surface against the plastic material in its transition zone and by the relevant plastic material. The above disclosure relating to maximum temperature of the plastic material also applies in the contact region between the plastic material and the mandrel disposed within the blank. A further requirement related to adjustment of the temperature of the plastic material is that such temperature adjustment must, for reasons of process engineering and also for reasons of production capacity, if possible be effected with as a slight an influence as possible on the cycle time of the equip¬ ment and preferably without affecting this cycle time whatsoever. Naturally, this requirement is conditioned by the desire of main- taining the capital cost per produced unit as low as possible. Moreover, in certain physical applications there are requirements that the temperature of the plastic material displays slight varia¬ tion from one blank to another. In the above-described orientation of plastic material by means of a gap, it is desirable for certain plas- tic materials that the material temperature vary by at most approx. 2° C. EP 204 810 describes a technique in which a hot mandrel is inserted in a preform of thin plastic material and progressively heats up the material during simultaneous expansion of the preform according as the material of the preform is brought into abutment against and displaced over the outer defining surface of the mandrel. The drawback inherent in this technique is that the temperature of the mandrel must be kept relatively high, which, for certain plastic materials such as PET, leads to undesirably high friction. In all of the above-described physical applications, the plastic material is, as a rule, given an elevated temperature before the reforming operation, since the elevated temperature is normally a prerequisite to enable application of the technique involved and in order that the product obtain the contemplated properties. The heating is effected in accordance with prior art using radiation energy. Because of the characteristics of the plastic material, such heating has a low level of efficiency. In order to reduce the heating time, use is made, therefore, of high temperatures at the radiation source, which, however, leads to problems if the blank remains in the heating position for too long. Such unintentional extended heating time often occurs in disruptions in the production process, for example an interruption in any of the processing stages which follow after heating of the blank. Such undesirable extension of the heating time in operational disruption will often result in the blank fastening in the heating position or, at worst, will result in the blank catching fire unless special measures are implemented to screen off or remove the blank from the radiation source when the unintentional disruption occurs. It is obvious that if a blank fastens in the equipment, a relatively lengthy disruption in production will occur, in particular if the heating devices must be cooled in order to enable removal of the blank v/hich has fastened. c oth such disruptions and extra arrangements included in the equipment to screen off the blank from the radiation source in connection with production disruptions entail extra costs which render production and, thereby, the product itself more expensive. It will be obvious to one skilled in the art that there are, in many technical contexts, needs for a rapid temperature conditioning of plastic material, often in combination with desires for slight deviation in the temperature of the material for which the temperature conditionino has been carried out. In addition, there are often requirements that the temperature of the material in all parts of the blank be set at the predetermined temperature. The term temperature conditioning is also here taken to mean cooling of the plastic material. The present invention relates to a method and an apparatus in wnich the above drawbacks have been obviated and in which the above requirements have been satisfied. This is attained by means of a method and an apparatus as disclosed in the characterizing clauses of the independent claims. At excessively high temperatures of plastic material, a considerable increase in friction will generally occur on contact against metal, and often also a tendency to tackiness between the plastic material and the metal. In case of PET for example, an increase by a factor of lii of the friction w ll occur if the material temperature in the region of TG increases by approx. 10° C. This is one of the reasons why prior art technology generally avoids, on heating of the plastic material in a blank, direct contact between plastic material and mechanical heating tools and instead calls for the employment of radiation energy for the heating operation. As disclosed in the characterizing clauses of the independent claims, a temperature conditioning of the material in the blank takes place according to the present invention by means of a mechanical tool which is displaced to a position within the blank. The mechanical tool is hereinafter also referred to as temperature conditioning device or first mechanical device. The device consists, in the region where it abuts against the blank, of a material of superior thermal conductive capacity, normally of metal. In that the temperature conditioning device abuts against the plastic material of the blank for but a short time, the above-mentioned tendency to tackiness will be avoided even though the device, in certain embodiments, is at a relatively high temperature. The direction of displacement of the device in relation to the plastic material is selected such that friction problems are avoided. The selected direction of displacement also entails the advantage that, for all of the material portions which are temperature conditioned, temperature adjustment takes place during a substantially equal length of time. When the possibility of employing a large temperature difference between the temperature conditioning device (the temperature conditioning mandrel) and the plastic material is employed, an extremely rapid transfer of energy will be achieved between the conditioning device and the plastic material . At high temperatures of the conditioning device, the abutment is limited to such a short time that the plastic material in the region of the abutment surface never passes the critical temperature at which tacking between the plastic material and the material of the heating mandrel and/or thermal crystallization of the plastic material begin to occur. The supply of energy during the brief contact between the heating device and the plastic material continues once contact has ceased into the plastic material, at the same time as the temperature of the plastic material in the region most proxi- mal the abutment surface of the blank begins to fall. Under continued displacement of the thermal energy towards the opposing side of the blank, a reduction of the temperature of the plastic material continues adjacent that surface with which the blank abutted against the heating device. When the temperature reduction has continued so far that the risk of tacking and/or thermal crystallization is eliminated, the same conditioning device or another conditioning device is once again displaced into the blank, being moved into abutment against the ' inner surface of the blank. A thermal transfer during a limited period of time once again takes place to the plastic material, whereby a further thermal wave commences its displacement towards the opposing side of the blank. In one preferred embodiment, energy supply to the material of the blank takes place on at least two mutually subsequent occasions. Each time and after the first occasion when energy is supplied to the material of the blank, the thermal energy from the immediately preceding occasion has reached material in,the blank located a distance from the abutment surface of the blank corresponding to at least approx. 1/5, as a rule at least approx. 1/5 and preferably at least approx. 1/4 of the wall thickness of the blank. However, it has surprisingly proved that, in certain physical applications, only one heating occasion is required, in particular when the material is thin and is heated to relatively low te pera- tures. As a rule, an individual blank abuts only once against each conditioning device. However, the inventive concept as herein disclosed also encompasses embodiments in which one and the same conditioning device abuts against the individual blank more than once, in certain applications on all occasions. In one preferred embodiment of the present invention, the blank is placed, prior to the displacement in relation to the conditioning mandrel, in a holder which is also at an elevated temperature. The holder is disposed to be rotated about a centre axis located out- side the holder and . , thereat, to be displaced to mutually sub¬ sequently located positions. In at least one of these positions - as a rule the second - a displacement of a conditioning mandrel takes place to a position within the blank. After the predetermined abutment time against the inner surface of the blank, the conditioning mandrel is withdrawn from the blank, whereafter the holder is rotated about its centre axis to its next position. During this displacement, the migration of the energy wave commences towards the outer surface of the blank. After a predetermined time, a conditioning mandrel is once again displaced into the blank, energy being once again supplied to the plastic material of the blank. The mandrel is thereafter moved from the position within the blank, whereby the blank is given the possibility of being moved to the next position by means of the holder. The number of positions, abutment times and/or displacement speeds of the container are determined int. al. by the thickness of the plastic material in the blank, by the thermal conductivity, of the plastic material, by the temperatures of the abutment surfaces of the conditioning mandrels, and by the temperature to which the plastic material is to be heated. It should be observed tha the described embodiment with the blank placed in a holder which is rotated about a centre axis located outside the holder gives the possibility of providing, in each position, one conditioning mandrel specific to that position, the mandrel being, for instance, set at a predetermined and specific temperature for the position, having a design specific to the position, having a pattern of movement specific to that position, etc. Hence, in certain embodiments temperature and/or material in the abutment surface of the mandrel vary from position to position. Hereby, the possibility is created of controlling both the abutment time of the plastic material in each separate position and of minimizing the risk of undesirable friction and/or tacking tendencies in each respective position. In physical applications of the present invention in which the plastic material of the blank is temperature conditioned in order that the material be " of a suitable temperature for attenuation, for example be oriented in that it passes throuαh a α?.n (for instance employing a technique corresponding to that described by way of introduction " ;, one preferred embodiment of the present invention calls for the selection of the speed of the drawing ring in relation to the plastic material of the blank to be lower in the initial stage of the displacement of the drawing ring than during the remainder of the forming process. Hereby, an energy wave will be established in the transition region between thick material and attenuated material occasioned by the thermal energy which is released in connection with the reduction of the material thickness. As a result of the selected low speed of displacement of the drawing ring, this energy wave will have time to move in the plastic material such that th.is attains a temperature suited for the subsequent processing (the attenuation). When this has taken place, it has surprisingly proved possible tc achieve a drastic increase of the speed of displacement of the drawing ring. Thus, an increase by a factor of up to approx. 5 will be tolerated by the material without any injurious effect on the quality of the attenuated material. If, conversely, the initial drawing speed is too high, the energy wave will net have sufficient time to exercise its full effect. (This is probably because the speed of displacement of the drawing ring exceeds the speed of propagation of the energy in th? plastic material). Further purposeful embodiments of the present invention are disclosed in the appended subclaims. The present invention and its aspects will be more readily understood from the following brief description of the accompanying Drawings, and discussion relating thereto. In the accompanying Drawings: Fig la is a cross section through a combined holder and receptacle device for a blank; Fig. lb is a cross section corresponding to the cross section of Fig. 1a, with a conditioning mandrel located above the holder; Fig. 2 is a cross section corresponding to the section of Fig. 1 in which the conditioning mandrel is inserted in the blank; Fig. 3 is a cross section corresponding to the section of Fig. 2, in which the conditioning mandrel has been expanded; Fig. 4 is a cross section corresponding to the previous cross sections, in which an orientation mandrel is inserted in the blank; Fig. 4a shows the region marked A in Fig. 4 on a larger scale; Fig. 5a is a cross section corresponding to the section in Fig. -. without a blank in the holder and receptacle device, in which the orientation anαrel has been displaced downwardly in the Figure; Fig. 5b is a cross section corresponding to the section of Fie. 5a with the blank in the holder and receptacle device; and Fig. 6 is a top plan view of an apparatus for receiving, temperature conditioning and reforming of the blank. Referring to the Dravnngs. the Figures, which show one embodiment of the present invention, depict a blank 10 with a sealed bottom portion 11 and a mouth portion 12. The blank has an inwardly facing bottom surface 13 and an inwardly facing, generally substantially cylindri¬ cal or slightly conical surface 14 which defines the wall 15 of the blank. In a conical surface, this has its largest circumference in tne mouth portion 12. The outer surface of the wall has reference numeral 17. Fig. 5b shows how the blank has been partially subjec- ted to a reforming, whereby there is formed a thinner v/all portion 15a in the lower region of the blank, while the remaining wall portion 16b still retains its original form. Λ transition region 13 is to be found between the v/all portion of original thickness and the all portion of reduced thickness. A receiving device 30 (cf. Figs, la and lb), which also constitutes a holder for the blank, has a side wall 31 whose inner defining surface 32 is of a size and configuration which substantially correspond to 0 the outer configuration of the v/all 15 of the blank. Channels- 33 for thermal medium (heat carrying medium) are disposed in the side wall. A substrate, for example a plate 33, is located beneath the side wall 31 of the holder for supporting the blank. T5 A mechanical device which, in the Figures, is shown as a mandrel 20 (ef. Fig. lb), hereinafter non-restrictively designated conditioning mandrel, is connected by the intermediary of a drive shaft 21 to drive means (not shown). The drive means are disposed to displace the mandrel from the position illustrated in Fig. 1b τ in which the 20 mandrel is located above the blank, to,the position illustrated in Fig. 2, in which the mandrel ' is inserted in the blank. The condi¬ tioning mandrel is disposed to be adjusted at a certain temperature which is adapted to that temperature at which the material of the blank is to be set. To this end, the conditioning mandrel is provided 25 with ducts 23 for heat carrying medium. In certain physical applications, the mandrel placed within the blank emits energy to the blank, while in other physical applications, the mandrel leads off energy from the blank. The outer defining surface (side surface) 25 of the conditioning mandrel is dimensioned so as to have a 30 confiquration substantially corresponding to the configuration of the inwardly facing defining surface 14 of the blank. However, as a rule the dimensions of the blank vary from one blank to another, for which reason the conditioning mandrel is, in one preferred embodiment, provided with a first mandrel portion 22 and a second mandrel portior. 3523 which, by drive means (not shown), are displaceable from one another while increasing the circumference of the conditioning mandrel. The mandrel portions are, in this instance, separated fro-. 1 1 one another at the longitudinal section having reference numeral 24. It will be obvious to one skilled in the art that, in certain embodiments, use is made of more than two mandrel portions particular in physical applications in which the variation of the circumference of the conditioning mandrel is to be large. The mandrel is defined by a bottom surface 25. As is apparent from Fig. 3, at least one gap 27 is formed between the mandrel portions on their displacement from one another. Figs. 4, 4a, 5a and 5b show the receiving device, the holder 30, under cooperation with an orientation mandrel 60 which, via a drive shaft 61. is connected to drive means (not shown). The mandrel has outer dimensions corresponding to the inner dimensions of the blank 1C, which entails that, with the mandrel placed in the position illustrated in Fig. 4, the side surface 66 of the mandrel abuts, at Least with its lower portion, against the inner surface 14 of the blank. Channels 63 are provided in the orientation mandrel for adjusting the temperature of the side surface 66 of the orientation mandrel. The bottom surface 65 of the mandrel is disposed to abut against tne inwardly facing bottom surface 13 of the blank. igs. 4, 4a, 5a and 5b show how the substrate 33 is provided with an aperture 35 of a size allowing the blank to pass through the aperture. In association with the aperture, there is provided e drawing ring 50 with a circumferential region 51 in which the inner circumference of the drawing ring is reduced from a larger size most proximal the blank to a smaller size more distal from the blank (cf. Fig. 4a). This circumferential region is defined towards the centre of the aperture by a working surface 52. Just as the side wall 31 of the holαer is provided with one or more channels 3S for heat carrying medium, tne drawing ring 50 is provided with one or more channels 5 C for adjusting the temperature of the working surface 52 of the drawing ring. With the drawing ring inserted in the aperture (cf. Fig. 5a) a gap 54, hereinafter referred to as a drawing ring gap, is formed between the. drawing ring and the orientation mandrel, tne gap having a width which is less tnan the materiel thickness of tne blank Fig. 6 shov/s one preferred embodiment of the present invention in which the substrate plate 33 is disposed under a composite unit 37 formed by a number of reception cups (holders) 30a-30e, which are secured to one another by the intermediary of connection devices 36. In such instance, the holders are generally designed as substantially cylindrical tubes 30a-30e open at both ends. The composite unit is, via the connection devices, connected to a centre shaft 34 about which drive means (not shown) rotate the unit to predetermined positions in which the combinations of devices described with reference to Figs. 1-5 are formed. In certain physical applications, the centre shaft is fixedly connected to the composite unit so as to rotate it. The movement of rotation about the centre of the composite unit is, in this instance, indexed such that the holders are located, with preadjustable intervals, in one of the positions indicated by reference numerals 1-5. The displacement of the holders to positions 1-5 takes place by relative movement in relation to the substrate 33 which, as a rule, is in a fixed position. In position 1, which has its counterpart in Fig. la, the blank 10 is received by the receiving device (the holder) 30a which, in Fig. 6, is located in position 1. Positions 2, 3 and 4 each correspond to those combinations of devices as are illustrated in Figs, lb, 2 and 3; and position 5 has its counterpart in the combination of devices shown in Figs. 4, 5a and 5b. In the region corresponding to position 5 for the holder 30, the plate 33 is provided with the aperture 35 and the drawing ring 50. In the illustrated embodiment, the apparatus allows for temperature conditioning of the blank at a maximum of 3 occasions as necessary. The apparatus includes control and regulation means (not shown) for controlling and regulating the movements and expansion of the condi¬ tioning mandrel and, in this instance, also the time interval during which the abutment of the mandrel proceeds. The control and regula¬ tion means (not shown) are also disposed for adjustments of the temperature of the medium supplied to the conditioning mandrel 20, the holder 30 and. where applicable, the crawing ring 50. When the present invention is reduced into practice, the blank 10 is displaced into the receiving device (the holder 30a) to the position illustrated in Fig. la. Thereafter, the composite unit 37 is rotated through one position, whereby the holder 30a is moved to position 2. During this displacement, the holder slides on the upper defining surface of the plate 33. In position 2, the conditioning mandrel 20 is displaced from an upper position (cf. Fig. 1b) to a lower position (cf. Fig. 2). In the upper position, the conditioning mandrel is located above and outside the blank, and in the lower position within. the blank. In one preferred embodiment, the conditioning mandrel is dimensioned so as, with its outer defining surface 26, to form a gap 41 with the inner defining surface 14 of the blank. As a result, the inwardly facing surface 14 of the blank is prevented from coming into contact with the mandrel 20 during its movement into the blank and this, thereby, a ' voids the risk of, for instance, uncontrolled heating of the material of the blank and consequential risk of undesirable friction between mandrel and plastic material. In view of the varying sizes of the blanks, the holder is, in one p referred embodiment, also dimensioned to form a gap 40 between itself and the outwardly facing defining surface 17 of the blank. The conditioning mandrel is thereafter expanded into abutment against the inner defining surface of the blank and, as a rule, thereafter an additional distance to displace material of the blank outwardly, into reliable abutment against the inwardly facing defining surface 32 of the holder. The expansion of the conditioning mandrel is controlled so as to continue until the blank abuts with its outer surface against the inner surface of the holder. By such means, there will be achieved reliable contact between the conditioning mandrel and the blank and between the holder and the blank, and efficient control of the energy transfer between the blank, the mandrel and the holder, respectively. In one preferred embodiment, use is made of a relatively slight degree of expansion, as a rule limited to at most approx. 20 and preferably to at most approx. 10%. In case of slight expansion, but a limited number of mandrel parts are required, while in case of a greater degree of expansion, the number of mandrel parts is increased so as to reduce the width of those gaps which are formed on expansion between the mandrel parts. As a result, there will be ensured a uniform heating of the plastic material. The temperature of the abutment surfaces of the mandrel against the blank are adjusted by means of heat carrying medium in the ducts 23 and channels 38 of the conditioning mandrel and holder, respectively. The following example of employed temperatures and times may be given for temperature conditioning of PET. The temperature of the outer surface 26 of the conditioning mandrel 20 is, as a rule, in excess of the region of TG and in such instance, by at least 10° C, as a rule by at least 30° C and preferably by at least 5C° C. Control and regulation means are employed to adjust the time for the abutment of the conditioning mandrel against the inner surface of the blank, this being selected to be at most approx. 5 sec, normally at most approx. 3 sec. and preferably at most approx. 2 sec. naturally, the abutment time employed is adapted to the temperature of the conditioning mandrel and the properties of the plastic material. The temperatures and times disclosed in this paragraph relate to temperature conditioning of a blank of PET whose v/all thickness is of the order °f magnitude of 2 mm. It will be obvious that, for other plastic materials and/or other dimensions of the blank, the conditioning time will be adapted to meet the relevant situation. Once the conditioning mandrel has abutted against the blank during the predetermined time, the mandrel is contracted and withdrawn from the blank. This is then displaced to the next position where, in applicable cases, a new abutment of the conditioning mandrel of this position takes place against the material of the blank for exchange of thermal energy between mandrel and blank. Also in this position, the abutment time is governed in analogy v/ith that disclosed in the preceding paragraph. It will be obvious that the cycle for the temperature conditioning of the blank may be repeated in one individual station by allowing the mandrel to run through the above-disclosed schedule more than once with the holder remaining in the same position. Having passed the positions for temperature conditioning, the blank is moved to position 5. As -a rule, the blank rests in this position on the working surface 52 of the drawing ring 50 (cf. Fig. 4a). When the blank has assumed its location in position 5, the orientation mandrel 60 is displaced downwardly and through the aperture 35 in the base plate 33, whereupon the bottom surface 65 of the mandrel, on abutment against the inwardly facing bottom surface 13 of the blank, displaces this surface, and thereby also the blank 10, through the aperture. At this point, the drawing ring gap 54 is formed between the orientation mandrel 60 and the drawing ring 50, the size of this gap being less than the thickness of the wall 15 of the blank. On the passing the drawing ring gap, the material in the wall abuts against the working surface 52 of the drawing ring 50, whereby, in conjunction with the passage into the gap, the material thickness of the wall of the blank is reduced and tensile forces are exercised on the material in the blank in the axial direction of the blank. A transition zone is formed between thin (as a rule oriented) material which has passed through the drawing ring gap, and thick (as a rule generally amorphous) material which has not yet passed through the gap. On displacement of the orientation mandrel, the transition zone is shifted into the amorphous material. Hereby, the material in the wall 15 is oriented in an axial direction when the material passes the working surface 52. Depending upon the desired application of the invention, all material in the blank is oriented or only a part thereof. In practical applications in which reduced .material thickness is imparted to all of the material in the wall of the blank, the reformed blank is located beneath the drawing ring once the movement of the orientation mandrel is completed. A channel 62 for pressure medium is provided for releasing the reformed blank from the orientation mandrel. Once the orientation mandrel has returned to its starting position, the holder 30 is displaced to position 1, whereafter the above cycle is repeated. The temperature of the holder 30 is generally adjusted to a level which at most amounts to a temperature at which the thermoplastic material begins to thermocrystal 1ize. As a rule, adjustment is therefore effected at a temperature within the range of the TG of the thermoplastic material, but in certain embodiments at a temperature which is less than TG. For PET a temperature of at most approx. 85° C, preferably at most approx. 80° C, has proved to entail good temperature distribution in the wall of the blank. Since all of the mechanical devices which are in contact with the plastic material consist of material with a good coefficient o thermal conductivity (as a rule metals) there will be achieved according to the invention an adjustment and control within narrow tolerance limits of the temperature of the thermoplastic material in all stages of the above-described cycle. This is particularly important in the transition region 18 of the wall of the blank where, in conjunction with the reduction of material and prevailing orientation, energy is released which needs to be removed. Since the plastic material abuts against the orientation mandrel 60, against the holder 30 and against the working surface 52, the material is, also in this critical region, wholly enclosed by material possessing good thermal conductivity properties, which makes for the requisite transfer of energy between the thermoplastic material and the mechanical devices. It will further be apparent from the above description that also before its passage of the drawing ring, the thermoplastic material is, by means of the holder wall 31 of the mechanical devices, the conditioning mandrel 20 and the orientation mandrel 50, respectively, given a temperature adapted to those conditions which apply in order that the desired reduction of the thickness of the thermopl stic material and orientation (crystalli¬ zation) of the material shall take place on passage by the blank of the drawing ring. Both during passage through the drawing ring gap 54 and thereafter - like during the previously described temperature conditioning cycle - the side wall 31 of the holder 30 has, via its defining surface 32 turned to face the blank, influenced the temperature distribution within the blank. In certain practical applications and/or positions, the definino surface 32 is at a lower temperature than the side surface 26 of the conditioning mandrel 20 while in other practical applications and/or positions, the defining surface 32 is at a temperature which exceeds the surface temperature of the side surface 26 of the conditioning mandrel. In the normal case, the side surface 26 of the holder is at a temperature which is less than, or in the region of, TG. On displacement by the drive means of the orientation mandrel 60 through the aperture 35, the orientation mandrel shunts the closed bottom portion 11 of the blank ahead of it, at the same time as the orientation mandrel forms, between itself and the drawing ring 50, the drawing ring gap whose size in case of PET at most amounts to approx. half of the material thickness of the original blank, which consists substantially of amorphous material. This is taken to mean thermoplastic material of a crystallinity at most amounting to approx. 10 . As a result of the relative displacement of the orientation mandrel 60 in relation to the drawing ring 50 and thereby the displacement of the bottom portion of the blank, the wall of the blank is forced to pass through the drawing ring gap, whereby the thickness of the wall of the blank is reduced on the simultaneous onoaxial orientation of the material of the blank. Thus, during displacement of the orientation mandrel, the amount and length of the oπoaxially oriented material are progressively increased while, at the same time the amount and length of the amorphous material are reαuced. In practical applications in which all material in the wall of the blank passes through the gap, all material in the wall will, thus, be oriented. By means of the channels 33, 58 and 68 in the all 31 of the holder 30, in the drav/ing ring 50 and in the orientation mandrel 60, respectively, the temperature of the material in the transition region 18 is controlled. Hence, it applies that for amorphous material, i.e. material which has not yet passed through the gap, a final adjustment of the temperature of the material of the blank is effected by means of the orientation mandrel 60 and the side wall 31 cf the holder 30. During the orientation process proper, the drawing ring 50 plays an active role in drawing off that thermal energy which is developed in connection with orientation of the material, but also the orientation mandrel 60 itself assists in preventing the temperature from passing that temperature range within which the contemplated orientation is achieved. In the embodiment illustrated in Fig. 6, the system is stepwise rotated by the holder about the centre shaft 34. Each time the system stops, one operation is executed. In position 1, the holder 30 is loaded v/ith the blank consisting substantially of amorphous material. In the next step, the holder is moved to position 2 where the blank undergoes heating or cooling in accordance v/ith that described above v/ith reference to Figs. lb-3. Thereafter, the blank is displaced to positions 3 and 4, respectively, v/here a corresponding treatment is repeated, in applicable cases. Finally, the blank is displaced to position 5 where the temperature conditioning and reforming of the blank described with reference to Figs. 4 and 5 take place. In order to enable this reforming, the substrate, i.e. the plate 33, is, in position 5, provided with an aperture corresponding to the aperture 35 in Fig. 4. When the orientation mandrel has been displaced to its lowermost position and all material in the blank has passed through the gap between the orientation mandrel and the drawing ring, compressed air is generally employed to release the reformed blank from the orientation mandrel. This is achieved in that the orientation mandrel is provided v/ith a channel 62 through which the compressed air passes and whereby the reformed blank is blown free of the orientation mandrel. Thereafter, this returns to its starting position. In certain embodiments, the channels and ducts for heat carrying medium are replaced by electric resistor wires. The channels and ducts for said medium are generally employed only when the holder 30 or the orientation mandrel 60, respectively, is used for cooling material in the blank. In the foregoing, the invention has been described in connection with temperature conditioning of a blank whose material thickness is to be reduced in that the blank is to pass through a gap 54. It will, however, be obvious to one skilled in the art that the technique described above is suited for application for temperature condi¬ tioning of plastic material as a preparatory measure for reforming a blank into a container irrespective of the prior art techniαue employed for such reforming. The above detailed description has referred to but a limited number of embodiments of the " present invention, but it will be readily perceived by those skilled in the art that the inventive concept as herein disclosed encompasses a large number of embodiments without departing from the spirit and scope of the appended claims.

Claims: CLAIMS 1. A method, in an open and hollow blank (10) of plastic material, as a rule a substanti lly cup-like or tubular blank, of adjusting, by energy exchanged between the blank and a first mechanical device (20) placed within the blank, the temperature of material in the blank at a level within a predetermined temperature range in which, for adjustment of the temperature of said material, the mechanical device abuts against said material in at least one region with its outer defining surface (26), and in which the temperature of the mechanical device, at least in the region or regions, respectively, of the abutment against the blank are set at a level which is determined by the change desired through such abutment of the temperature of the material of the blank abutting against the outer surface (25), characte¬ rized in that the mechanical device (20), on having been placed within the blank (10), is expanded into abutment against the inner defining surface (14) of the blank; and that after a certain abutment time, the mechanical device is contracted for discontinuing the abutment of the device against the inner defining surface of the blank. 2. The method as claimed in claim 1, characterized in that the temperature of the abutment surface (26) for the mechanical device (20) placed within the blank is set at e. level in excess of the glass transition temperature (TG) of the plastic material; that the abutment of the device against the blank is discontinued before the temperature of the plastic material in the abutment surface attains such a high level that tacking tendencies between plastic material and the mechanical device arise, the plastic material thermally crystallizes. 2. The method as claimed in claim 1 or 2, characterized in that said abutment against the inner defining surface (14) of the blank (10) takes place at least once; and that in applications in which the blank is heated on the abutment, each abutment after the first takes place once the thermal energy supplied on the 21 immediately preceding abutment has reached material in the blank located in spaced-apart relationship from the inner defining surface of the blank corresponding to at least 1/5 of the wall thickness of the blank, as a rule at least approx. 1/5 and preferably at least approx. 1/4. 4. The method as claimed in any one of claims 1 to 3, charac¬ terized in that the temperature of the outer surface (26) of that mechanical device (20) which abuts against the inner defining surface (14) of the blank exceeds TG by at least 10° C, as a rule by at least 30° C, and preferably by at least 50° C; and/or that the abutment of the mechanical device (20) against the inner defining surface (14) of the blank on each occasion lasts for at most approx. 5 sec, as a rule at most approx. 3 sec and preferably for at most approx. 2 sec. 5. The method as claimed in any one of claims 1 to 4, charac¬ terized in that, on its expansion the mechanical device (20) placed within the blank displaces the wall (15) of the blank into abutment against a defining surface (32) of a second outer mechanical device (30) which at least partly surrounds the blank and whose defining surface, in the region of abutment of the blank, is at a temperature set at a level which is determined by the change desired by such abutment of the temperature of the material abutting against the defining surface (32) of the blank. 6. The method as claimed in claim 5, characterized in that the temperature of the abutment surface (32) of the outer mechanical device (30) against the blank (10) amounts at most to a temperature in the proximity of that temperature range within which the thermoplastic material begins to ther ocrystallize, as a rule at most at a temperature within the range of the TG cf the thermoplastic material, and preferably c temperature which is less than TG. 7. The method as claimed in any one of claims 1 to 6, characte¬ rized in that the blank is supplied to a reception cup (30) of the second outer mechanical device; and that the reception cup (30) is rotated about a centre shaft (34) located outside same, for displacement to mutually subsequent positions (1-5); and that at least in one of the positions, a mechanical device corresponding to the first mechanical device (20) is displaced to and from the position within the blank (10). 8. An apparatus for adjusting the temperature of a hollow blank (10) of plastic material, as a rule a substantially cup-shaped or tubular blank, the apparatus including a first mechanical device (20) and a second mechanical device (30) which are disposed to be displaced in relation to one another, the second mechanical device being disposed to hold the blank in a certain position and the first mechanical device disposed to be displaced to a position v/ithin the blank, characterized in that the first mechanical device (20) is operative, once it has been placed within the blank (10), to be expanded into abutment against the inner defining surface (14) of the blank; and that the apparatus includes control and regulation means operative to regulate the abutment of the first mechanical device against the inner surface of the blank and to allov/ the abutment to sustain during an adjustable time interval. 2. The apparatus as claimed in claim 8, characterized in that the second mechanical device (30) is designed as a holder (30), and said holder (30) has a form (shape) adapted to the blank (10) for abutment of the holder against the outer surface (17) of the blank. 10. The apparatus as claimed in claim 8 or _ , characterized in that the first mechanical device (20) is expandably disposed in the circumferential direction in order, during abutment against the inner surface (14) of the blank (TO) to bring, by expansion, the outer surface (17) of the blank into contact v/ith the surfac (32) of the holder (3C) facing the blank. 11. The apparatus as claimed in any one of claims 8-10, characterized in that the first mechanical device (20) includes a substantially cylindrical or gently conical mandrel (20); and that the mandrel is divided into at least two mandrel segments (22, 23) axially displaceable from one another. 12. The apparatus as claimed in any one of claims 9-11, charac¬ terized in that the apparatus includes a plurality of other (outer) mechanical devices (30) which are designed as substantial- 1y cylindrical tubes (30a-30e) which are open at both ends and are fixed in relation to one another at mutually equal spaced apart relationship along a circle periphery for the formation of a composite unit (37); that the composite unit is step ise rotary in agreement with the distance between the outer mechani- cal devices for placing thereof in positions (1-5) which are located on a circle periphery; that the first device (20) is disposed in association with at least one of these positions; that the apparatus includes a substrate (33) which is disposed beneath the composite unit and which carries the blanks; and that in one of said positions, the substrate is provided with an aperture (35) through which the blank passes, for example to leave the apparatus.

Inventors: NILSSON TORSTEN, NILSSON, TORSTEN
Applicants: PLM AB
Application year: 1989
Main classification: B29C35
IPC codes: B29B13, B29C35, B29C49, B29C51, B29C55