Flame retardant olefinic resin composition

Abstract: A flame-retardant olefinic resin composition comprising (a) at least one ethylene copolymer selected from the group consisting of ethylene-α-olefin copolymers, ethylene-ethyl acrylate copolymer and ethylene-methyl methacrylate copolymer, (b) a silane-grafted polymer obtained by grafting a silane to an olefinic resin, (c) a maleic acid or maleic anhydride derivative of a polyethylene, an ethylene-vinyl acetate copolymer or an ethylene-α-olefin copolymer, (d)(i) an ethylene-ethyl acrylate-maleic anhydride copolymer or an ethylene-methyl methacrylate-­ maleic anhydride copolymer, or (d)(ii) a silicone-­ modified polymer obtained by graft-polymerizing a reactive polyorganosiloxane to a thermoplastic resin, or (d)(iii) a mixture of (d)(i) and (d)(ii), and (e) a hydrated metal compound, wherein there are incorporated the component (c) in an amount of 0.1-30 parts by weight, the component (d)(i) in an amount of 0.1-30 parts by weight when used, the component (d)(ii) in an amount of 0.1-30 parts by weight when used, and the component (e) in an amount of 50-300 parts by weight, all based on 100 parts by weight of the components (a) and (b).

Description: The present invention relates to flame-retardant olefinic resin compositions which generate no hazardous and corrosive gas of halogen type during burning due to fire outbreak and which are intended to be applied particularly to electric wires and cables. Imparting flame retardancy to polyolefin compositions which have been extensively used as an insulating material for electric wires, cables and electric appliances, has conventionally been achieved by adding a halogen compound and antimony trioxide to a polyolefin. However, the resulting compositions contain a halogen, and therefore generate, during burning, a halide gas which is harmful to the human body and corrodes metals. Moreover, these compositions produce, during burning, a large amount of fume making the visibility poor. This has imposed a remarkable restriction with respect to evacuation of people and fire fighting activity during fire. Hence, it has recently become a strong desire from a safety standpoint that these resin compositions produce no halogen-based gas upon burning. Under such situation, hydrated metal compounds have come to draw attention as an inorganic flame retardant, because their fuming property and harmfulness are very low. Resin compositions containing a large amount of magnesium hydroxide, aluminum hydroxide or the like for improving flame retardancy have been used in recent years. However, these resin compositions have the following drawbacks. (1) Magnesium hydroxide reacts with the moisture and carbon dioxide present in the air and changes to magnesium carbonate. Accordingly, on the surface of a resin composition containing magnesium hydroxide, there appear white crystals of magnesium carbonate. (2) Magnesium hydroxide and aluminum hydroxide have very low resistances to acids and alkalis. Therefore, when a resin composition containing magnesium hydroxide or aluminum hydroxide is in contact with an acid or an alkali, magnesium hydroxide or aluminum hydroxide readily dissolves in the acid or alkali at the surface of the resin composition. It dissolves in a large amount even in a weak acid having a pH of about 2 and, as a result, is liable to cause the deterioration of the resin composition surface. (3) The presence of a large amount of an inorganic filler in a resin composition easily incurs the surface damaging of the resin composition. (4) A resin composition containing magnesium hydroxide, aluminum hydroxide or the like causes surface whitening when bended, or buckling. These drawbacks have delayed the practical applications of the resin compositions containing magnesium hydroxide, aluminum hydroxide or the like to electric wires and cables. In connection with the present invention, Japanese Patent Application Nos. 129064/1986, which corresponds to EP-A-0237713, and 138316/1986 state as follows: A silane-grafted polymer causes crosslinking without requiring any catalyst. More specifically, hydroxyl groups (-OH) on the surface of a hydrated metal compound and silanol groups (→Si-OH) of a silane-grafted polymer cause a hydrolytic condensation reaction to form strong siloxane linkages [-Si-O-M m O n (M is a metal)], under the influences of (a) a small amount of water present on the surface of the hydrated metal compound and (b) the hydrated metal compound which acts similarly to an organic metal compound catalyst and in the presence of frictional heat generated during kneading; in this reaction, no catalyst is required. The above two patent applications further state that said strong siloxane linkages are effective in providing a resin composition with excellent shape retention at high temperatures, improved drip prevention during burning and improved mechanical properties (e.g. improved whitening on bending, and improved wear resistance). The above patent applications also state in the Examples that the strong siloxane linkages bring about improvements in mechanical properties, surface properties, thermal properties including heat deformation, and burning properties including oxygen index. EP-A-0 082 407 discloses a thermoplastic halogen-free flame-retardant polymer mixture comprising a elastomer component consisting of ethylene copolymer or ethylene terpolymer having a comonomer content of at least 38%, and a plastomer component containing at least 70% ethylene monomer polymerized therein, wherein the content of said elastomer component is at least 15% and the content of the plastomer component is in the range between 40% and 85%, based on the weight of all the polymer contents, and a mineral filler containing at least one metal hydroxide, having a weight of 180% to 320% of the polymer mixture, and having carboxylic groups. There have conventionally been proposed unsaturated dicarboxylic acid-modified polymers obtained by reacting maleic anhydride with polyethylene, polypropylene, ethylene-vinyl acetate copolymer (hereinafter referred to as EVA), ethylene-ethyl acrylate copolymer (hereinafter referred to as EEA), ethylene-α-olefin copolymers, or a liquid hydrocarbon polymer (e.g. a liquid polybutadiene) as a polymer skeleton in the presence of a radical-generating agent such as a peroxide. These resins are being marketed in Japan in large amounts. The addition of such a modified olefinic resin for imparting an adhesive property to other resins and metal powders has been reported in many papers. On this point, a number of patent applications have been filed. The examples are Japanese Patent Publication Nos. 5788/1987 and 9135/1987. As another example of maleic anhydride utilization, maleic anhydride is subjected to addition reaction to ethylene-α-olefin copolymers in the presence of a peroxide or the like to improve the latter's heat resistance and mechanical strength, as described in Japanese Patent Application Kokai (Laid-Open) Nos. 10151/1987 and 11745/1987. In this approach, the polar group of maleic anhydride is added to a non-polar olefinic resin to merely improve the latter's affinity with a filler and to finally improve the mechanical strength and heat resistance of the latter. Therefore, the purpose of this approach is different from that of an approach intended by the present invention wherein siloxane linkages are formed between a silane-grafted polymer and a hydrated metal compound through the water present on the surface of the hydrated metal compound and furthermore complex salt linkages are formed by the reaction between the hydrated metal compound and a dicarboxylic acid anhydride derivative. In order to solve the above mentioned problems, the present inventors proposed in Japanese Patent Application No. 45200/1987, which corresponds to EP-A-0280761, a flame-retardant olefinic resin composition comprising an olefinic resin, a silane-grafted polymer (a silane-grafted olefinic resin), a hydrated metal compound and a dicarboxylic acid or dicarboxylic anhydride derivative. The present invention provides a flame-retardant resin composition which contains a hydrated metal compound as an effective flame retardant but in which the surface deterioration and very low chemical resistance caused by the incorporation of the hydrated metal compound during various environmental tests or actual usage are prevented and thereby the surface damaging and the surface whitening on bending and buckling are improved furthermore. The present invention resides in a flame-retardant olefinic resin composition according to claim 1. In the present invention, the olefinic resin to which a silane is to be grafted, includes low density polyethylene, medium density polyethylene, high density polyethylene, ethylene-α-olefin copolymers, EVA, EEA, EMMA, ethylene-propylene rubber, ethylene-propylene-diene rubbers, etc. As the α-olefin of the ethylene-α-olefin copolymers used in the components (a), (b) and (c), there can be cited those having 3-12 carbon atoms, such as propylene, butene 1, pentene-1, hexene-1, heptene-1, octene-1, 4-methylpentene-1, 4-methylhexene-1, 4,4-dimethylpentene-1, nonene-1, decene-1, undecene-1, dodecene-1 and the like. Of these α-olefins, particularly preferable are butene-1, pentene-1, hexene-1, heptene-1 and 4-methylpentene-1. The silane-grafted polymer used in the present invention is obtained by reacting the above mentioned olefinic resin with an organic silane represented by the general formula RR′SiY₂ (R is a monovalent olefinically unsaturated hydrocarbon group; Y is a hydrolyzable organic group; and R′ is a monovalent hydrocarbon group other than unsaturated aliphatic hydrocarbon groups or is same as Y) in the presence of a free-radical-generating compound. This reaction is conducted according to a known method described in Japanese Patent Publication No. 24373/1982, Japanese Patent Publication No. 1711/1973, Japanese Patent Application Kokai (Laid-Open) No. 24342/1975, etc. In a specific example, a polyolefin resin is reacted with vinyltrimethoxysilane in the presence of an organic peroxide [e.g. DCP (dicumyl peroxide)] having a strong polymerization-initiating action, whereby a silane-grafted polymer is obtained. The amount of the silane-grafted polymer used is preferably at least 2 parts by weight per 100 parts by weight of the components (a) and (b). When the amount is less than 2 parts by weight, the resulting resin composition shows little improvements in shape retention at high temperatures and drip prevention during burning. The crosslinking degree of the silane-grafted polymer is preferably 20-80% by weight in terms of a gel fraction which is defined as a xylene insoluble. When the gel fraction is less than 20% by weight, the resulting resin composition is low in shape retention at high temperatures and drip prevention during burning. When the gel fraction is more than 80% by weight, the resulting resin composition has poor moldability. The amount of the maleic acid or maleic anhydride derivative of a polyethylene, an EVA or an ethylene-α-olefin copolymer is 0.1-30 parts by weight based on 100 parts by weight of the components (a) and (b). When the amount is less than 0.1 part by weight, the addition effect is very low. When the amount is more than 30 parts by weight, the reaction between the derivative and the hydrated metal compound takes place excessively and the composition shows poor extrudability and the extrudate shows deteriorated appearance. When there is used a component (d)(i), namely, an ethylene-ethyl acrylate-maleic anhydride copolymer or an ethylene-methyl methacrylate-maleic anhydride copolymer, the amount is 0.1-30 parts by weight based on 100 parts by weight of the components (a) and (b). When the amount is less than 0.1 part by weight, the addition effect is very low. When the amount is more than 30 parts by weight, the composition shows poor extrudability and poor heat aging property. In the present invention, the thermoplastic resin to which a reactive polyorganosiloxane is to be graft-polymerized, includes polyolefin resins such as polyethylene, polypropylene, ethylene-α-olefin copolymers, EVA, EEA, EMMA and the like; polystyrene; and acrylonitrile-butadiene-styrene copolymer. When there is used a component (d)(ii), namely, a silane-modified polymer obtained by graft-polymerizing a reactive polyorganosiloxane to the above thermoplastic resin, the amount is 0.1-30 parts by weight based on 100 parts by weight of the components (a) and (b). When the amount is less than 0.1 part by weight, the addition effect is very low. When the amount is more than 30 parts by weight, no corresponding improvement in effect is obtained and the composition cost is higher, which is not practical. The hydrated metal compound used in the present invention is a compound having a decomposition-starting temperature of 150-450°C and represented by the general formula M m O n ·XH₂O (M is a metal; m and n are each an integer of 1 or more determined by the valency of the metal; and X is the number of molecules of bound water) or a double salt containing said compound. Specific examples of the hydrated metal compound are aluminum hydroxide [Al₂O₃ · 3H₂O or Al(OH)₃], magnesium hydroxide [MgO·H₂O or Mg(OH)₂], calcium hydroxide [CaO·H₂O or Ca(OH)₂], barium hydroxide [BaO·H₂O or BaO·9H₂O], zirconium oxide hydrate (ZrO·nH₂O), tin oxide hydrate (SnO·H₂O), basic magnesium carbonate [3MgCO₃·Mg(OH)₂·3H₂O], hydrotalcite (6MgO·Al₂O₃·H₂O), dawsonite (Na₂CO₃·Al₂O₃·nH₂O), borax (Na₂O·B₂O₅·5H₂O) and zinc borate (ZnB₄O₇·2H₂O). The hydrated metal compound is added in an amount of 50-300 parts by weight based on 100 parts by weight of the components (a) and (b). When the amount is less than 50 parts by weight, the resulting resin composition is difficult to have desired flame retardancy. When the amount is more than 300 parts by weight, the resulting resin composition shows low mechanical properties (e.g. low tensile strength) and poor extrudability. The flame-retardant olefinic resin composition of the present invention can further contain, if desired, various additives conventionally used, such as antioxidant, neutralizing agent, UV absorber, antistatic agent, pigment, dispersing agent, lubricant, thickener, foaming agent, metal deterioration inhibitor, fungicide, flow control agent, flame retardant of phosphorus or phosphine derivative type, other inorganic fillers, crosslinking agent, crosslinking aid and the like and furthermore other synthetic resins. The present composition can be subjected to crosslinking by electron rays. In producing the present resin composition comprising (a) at least one ethylene copolymer selected from the group consisting of ethylene-α-olefin copolymers, ethylene-ethyl acrylate copolymer and ethylene-methyl methacrylate copolymer, (b) a silane-grafted polymer obtained by grafting a silane to an olefinic resin, (c) a maleic acid or maleic anhydride derivative of a polyethylene, an ethylene-vinyl acetate copolymer or an ethylene-α-olefin copolymer, (d) (i) an ethylene-ethyl acrylate-maleic anhydride copolymer or an ethylene methyl methacrylate-maleic anhydride copolymer, or (d)(ii) a silicone-modified polymer obtained by graft-polymerizing a reactive polyorganosiloxane to a thermoplastic resin, or (d)(iii) a mixture of (d)(i) and (d)(ii), and (e) a hydrated metal compound, any of the following processes can be employed. (1) A process in which the components (a), (b), (c), (d) and (e) are kneaded together. (2) A process in which at least either one of the components (c) and (d) is added at the time of preparation of the component (b) (a silane-grafted polymer) and, after the preparation of pellet-shaped silane-grafted polymer, the remaining components are added and the mixture is kneaded. (3) A process in which some components arbitrarily selected from components (a), (b), (c), (d) and (e) are kneaded and then the mixture is kneaded with the remaining components. When the components (a), (b), (c), (d) and (e) are compounded to produce a composition of the present invention and then the composition is shaped, the following effects can be obtained. (1) The silane-grafted polymer causes crosslinking without requiring any catalyst. More specifically, hydroxyl groups (-OH) on the surface of the hydrated metal compound and silanol groups (→Si-OH) of the silane grafted polymer cause a hydrolytic condensation reaction to form strong siloxane linkages [-Si-O-M m O n (M is a metal)], under the influences of (a) a small amount of water present on the surface of the hydrated metal compound and (b) the hydrated metal compound which acts similarly to an organic metal compound catalyst and in the presence of frictional heat generated during kneading; in this reaction, no catalyst is required. (2) The component (c) (a maleic acid or maleic anhydride derivative of a polyethylene, an EVA or an ethylene-α-olefin copolymer) and the component (d)(i) (an ethylene-ethyl acrylate-maleic anhydride copolymer or an ethylene-methyl methacrylate-maleic anhydride copolymer) react with the metal ions of the hydrated metal compound to form a complex salt. The combination use of the component (c) and the component (d)(i) yields striking effect. (3) The silicone-modified polymer contributes to the improvement of the composition in wear resistance and moldability. The siloxane linkages formed between the silane-grafted polymer and the hydrated metal compound, and the complex salt linkages formed by the reaction of the maleic acid or maleic anhydride derivative [the component (c)] or the ethylene-ethyl acrylate-maleic anhydride copolymer or ethylene-methyl methacrylate maleic anhydride copolymer [the component (d)(i)] with the hydrated metal compound [the component (e)] give synergistic effect. This synergistic effect and the effect of the silicone-modified polymer can provide a flame retardant resin composition with significantly improved surface deterioration, chemical resistance, surface damaging, surface whitening on bending, and buckling. Severe requirements for flame-retardant resin compositions can be met by the synergistic effect of the siloxane linkages and the complex salt linkages and can never be met by either one of the two linkages. The present composition has combustion-controlling effect quite different from that of the prior art using carbon powders and accordingly can exhibit the combustion-controlling effect irrespective of the kind of various pigments which may be added to the present composition for easier identification in use. Hence, the present composition can be colored in any desired color depending on application purposes. The present invention is explained specifically with reference to Examples. Examples First, three silane-grafted olefinic resins (three silane-grafted polymers) were prepared according to the formulations shown in Table 1, using the following procedures. Dicumyl peroxide (DCP) was dissolved in vinyltrimethoxysilane. The solution was independently mixed under agitation with two low-crystalline ethylene copolymers (1) and (2) and a low density polyethylene (3). The resulting silane-grafted polymers were extruded at 150-200°C using a single-screw extruder of 50 mm⊘ to obtain silane-grafted polymers A, B and C in a pellet form. Each polymer was placed in an aluminum-laminated bag and the bag was sealed to prevent the influence of external moisture. The polymer was taken out by each necessary amount whenever required. Formulations used in production of silane-grafted polymers (silane-grafted olefinic resins) Materials Silane-grafted olefinic resins A B C (1) D9052 100 (2) A2150 100 (3) G701 100 DCP 0.2 0.2 0.2 Vinyltrimethoxysilane 3 3 3 Gel fraction, % by weight 57 60 65 (1) Softrex, an ethylene-α-olefin copolymer manufactured by Nippon Petrochemicals Co., Ltd. (2) Rexlon, an EEA copolymer manufactured by Nippon Petrochemicals Co., Ltd. (3) A low density polyethylene manufactured by Sumitomo Chemical Co., Ltd. Next, various components shown in Tables 2-(i) to 2-(iii) were mixed together in a container. Each of the resulting mixtures was then kneaded in a Banbury roll and pelletized. The pellets were roll-pressed to prepare various test pieces. These test pieces were measured for degree of surface whitening due to formation of magnesium carbonate, weight change when immersed in 10% sulfuric acid (or 3% sodium hydroxide) aqueous solution, resistance to surface damaging, whitening on bending, and flame retardancy in terms of oxygen index. The above pellets were extruded through an extruder to obtain a tube of 20 mm⊘ in outside diameter, 18 mm⊘ in inside diameter and 1 mm in thickness, whereby extrudability was measured. Using this tube, buckling was measured. The results are shown in Tables 2-(i) to 2-(iii). As seen from these Tables, the present compositions (Examples) show remarkable improvements in whitening, resistances to sulfuric acid and sodium hydroxide, resistance to surface damaging, surface whitening on bending, and buckling.

Claims: A flame-retardant olefinic resin composition comprising (a) at least one ethylene copolymer selected from the group consisting of ethylene-α-olefin copolymers, ethylene-ethyl acrylate copolymer and ethylene-methyl methacrylate copolymer, (b) a silane-grafted polymer obtained by grafting a silane to an olefinic resin wherein the crosslinking degree of the silane-grafted polymer is 20 - 80 % by weight in terms of a gel fraction which is defined as a xylene insoluble, (c) a maleic anhydride-grafted polyethylene, a maleic anhydride-grafted ethylene-vinyl acetate copolymer or a maleic anhydride-grafted ethylene-α-olefin copolymer, (d)(i) an ethylene-ethyl acrylate-maleic anhydride copolymer or an ethylene-methyl methacrylate-maleic anhydride copolymer, or (d)(ii) a silicone-modified polymer obtained by graft-polymerizing a reactive polyorganosiloxane to a thermoplastic resin, or (d)(iii) a mixture of (d)(i) and (d)(ii), and (e) a hydrated metal compound, wherein the hydrated metal compound is a compound having a decomposition-starting temperature of 150-450°C and represented by the general formula M m O n ·XH₂O, wherein M is a metal; m and n are each an integer of 1 or more determined by the valency of the metal; and X is the number of molecules of bound water, or a double salt containing said compound, wherein there are incorporated the component (b) in an amount of at least 2 parts by weight per 100 parts by weight of the components (a) and (b), the component (c) in an amount of 0.1-30 parts by weight, the component (d)(i) in an amount of 0.1-30 parts by weight when used, the component (d)(ii) in an amount of 0.1-30 parts by weight when used, and the component (e) in an amount of 50-300 parts by weight, all based on 100 parts by weight of the components (a) and (b). A flame-retardant olefinic resin composition according to Claim 1, wherein the α-olefin of the ethylene-α-olefin copolymers is selected from the group consisting of propylene, butene-1, pentene-1, hexene-1, heptene-1, octene-1, 4-methylpentene-1, 4-methylhexene-1, 4,4-dimethylpentene-1, nonene-1, decene-1, undecene-1 and dodecene-1. A flame-retardant olefinic resin composition according to Claim 1, wherein the olefinic resin to be grafted with a silane is selected from the group consisting of low density polyethylene, medium density polyethylene, high density polyethylene, ethylene-α-olefin copolymers, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, ethylene-methyl methacrylate copolymer, ethylene-propylene rubber, and ethylene-propylene-diene rubbers. A flame-retardant olefinic resin composition according to Claim 1, wherein the silane-grafted polymer is obtained by reacting an olefinic resin with an organic silane represented by the general formula RR'SiY₂ wherein R is a monovalent olefinically unsaturated hydrocarbon group; Y is a hydrolyzable organic group; and R' is a monovalent hydrocarbon group other than unsaturated aliphatic hydrocarbon groups or is same as Y, in the presence of a free-radical-generating compound. A flame-retardant olefinic resin composition according to Claim 1, wherein the thermoplastic resin to which a reactive polyorganosiloxane is to be graft-polymerized, is selected from the group consisting of polyethylene, polypropylene, ethylene-α-olefin copolymers, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, ethylene-methyl methacrylate copolymer, polystyrene and acrylonitrile-butadiene-styrene copolymer. A flame-retardant olefinic resin composition according to claim 1, wherein the hydrated metal compound is selected from the group consisting of aluminum hydroxide [Al₂O₃·3H₂O or Al(OH)₃], magnesium hydroxide [MgO·H₂O or Mg(OH)₂], calcium hydroxide [CaO·H₂O or Ca(OH)₂], barium hydroxide [BaO·H₂O or BaO·9H₂O], zirconium oxide hydrate [ZrO·nH₂O], tin oxide hydrate [SnO·H₂O], basic magnesium carbonate [3MgCO₃·Mg(OH)₂·3H₂O], hydrotalcite [6MgO·Al₂O₃·H₂O], dawsonite [Na₂CO₃·Al₂O₃·nH₂O], borax [Na₂O·B₂O₅·5H₂O] and zinc borate [ZnB₄O₇·2H₂O]. A flame-retardant olefinic resin composition according to claim 6, wherein the hydrated metal compound is aluminum hydroxide or magnesium hydroxide.

Inventors: NAKAGAWA YASUO, OKUDA NOBUAKI, NAKAGAWA, YASUO, OKUDA, NOBUAKI
Applicants: SUMITOMO BAKELITE CO, SUMITOMO BAKELITE COMPANY LIMITED
Application year: 1989
Main classification: C08L23
IPC codes: C08F255, C08K3, C08L23, C08L51