Organic nonlinear optical material and nonlinear optical device

Abstract: Organic nonlinear optical materials and nonlinear optical devices are provided. The organic nonlinear optical materials are either derivatives of p-(N,N-dialkyl)amino-β-­ nitrostyrene represented by the structural formula (1) or derivatives of p-(β-nitroethylenyl)-julolidine represented by the structural formula (2). The organic nonlinear optical materials may be contained in optical cells or like containers to be used in optical devices, an alternatively they may be dispersed in various polymer materials or copolymerized with other monomer materials to form transparent dispersions or copolymers which can be used for similar purpose. The thus prepared optical media (1) may be assembled in optical devices in which the nonlinear optical properties, e.g. nonlinear refractive indice of the materials are used to fabricate optical switches, optical memories or other optical devices.

Description: The present invention relates a) to specific organic chemical compounds as described in the following claims for substances which satisfy all requirements of organic nonlinear optical materials and b) nonlinear optical devices as described in claims 15 to 20 which utilize the nonlinear refractive indices of a specific group of compounds. Prior Art ; Third-order nonlinear optical materials attract attention as important materials for optical devices in future because they exhibit frequency conversion functions due to third harmonic generations (hereinafter referred to as THG) and additionally they are applicable for optical switching and optical memory while making use of their optical bistable behaviors. Particularly, organic nonlinear optical materials have the following advantages superior over the known inorganic materials. Initially, when compared with crystalline inorganic ferroelectrics such as KDP (potassium dihydrogenphosphate) KH₂PO₄ and LiNbO₃ (lithium niobate), the organic nonlinear optical materials have larger nonlinear optical coefficients showing the second order nonlinear characteristics. Secondly, when compared with an inorganic semiconductor such as gallium arsenide (Ga-As), the organic nonlinear optical materials have ultrafast response times. Thirdly, different from copper(I) chloride (CuCl) exhibiting fast response and being capable of operating at room temperature but being hardly fabricated in a thin film with thickness of micrometer order, the organic nonlinear optical materials can be easily fabricated into thin films with the thickness of micrometer order. The organic nonlinear optical materials have the possibility of satisfying all requirements which have not been satisfied by the known materials, and thus eager investigations of such materials are continued. For example, the following references disclose organic nonlinear optical materials. J. L. Oudar, J. Chem. Phys., Vol 67, No. 2, pp 446 to 457 (1977), "Optical Nonlinearities of Conjugated Molecules. Stilbene Derivatives and Highly Polar Aromatic Compounds." This reference discloses the results of studies on the second- and third-order hyperpolarizabilities β and γ of 4-dimethylamino-β-nitrostyrene in addition to the derivatives of stilbene. Another reference is G. I. Stegeman and C. T. Seaton, Proceedings of SPIE - The International Society for Optical Engineering, 682 , pp 179 to 186 (1986), "Third-order Nonlinear Guided-Wave Optics." The known third-order nonlinear optical materials include the following two groups of materials. The first group includes π-conjugated polymers, the typical being polydiacetylene, particularly 2,4-hexadiyne-1,6-bis(p-toluenesulfonate) and polyacetylene. The second group includes low molecular weight compounds each having substituents disposed asymmetrically to serve as a donor and an acceptor, the typical being aminonitrostilbene, particularly 4-(N,N-diethylamino)-4′-nitrostilbene. In these compounds, the dimethylamino and diethylamino groups serve as the donors and nitro and cyano groups serve as the acceptors. The optical nonlinearities of the π-conjugated polymers are based on the polarization of free electrons in the valence electron band, and thus the π-conjugated polymers have the disadvantage resembling to that of inorganic semiconductor materials in that the response time is delayed by the resonance effect due to narrow band gap. Moreover, a π-conjugated polymer superior over PTS (2,4-hexadiyne-1,6-bis(p-toluenesulfonate)) has not yet been found. Since the low molecular weight compounds having asymmetrically disposed substituents serving as a donor and an acceptor exhibit nonlinear optical effects superior over that of 4-(N,N-diethylamino)-4′-nitrostilbene, it has been tried to introduce a longer π-conjugated chain in the compound and to introduce a more active donor-acceptor pair in the compound. However, torsion of the π-conjugated chain is induced as the length of the π-conjugated chain in the compound is increased, leading to the result that the effective length of the π-conjugated chain ( i.e. the effective length of delocalized electrons) is decreased. On the other hand, when a more active donor-acceptor pair is introduced in a compound, spontaneous polarization is enhanced leading to the result that the difference in dipole moment between the ground state and the excitation state cannot be increased so large as expected. In addition, deterioration of the material due to absorption of light and delay in response time is accerelated. As the molecular size becomes larger and the spontaneous polarization of the nonlinear optical material becomes extremely enhanced, the solubility in a solvent or a high polymer matrix is lowered and crystallization property is deteriorated to have poor processibility for the preparation of an optical element therefrom. However, the compounds having substituents disposed asymmetrically and serving as a donor and an acceptor are important organic materials for eager investigations since they exhibit high speed and highly efficient nonlinear optical responses although they have the aforementioned complicated problems. OBJECTS AND SUMMARY OF THE INVENTION : The object of this invention is to provide an organic nonlinear optical material which exhibits a high speed and highly efficient nonlinear optical response and which is improved in solubility not only for organic solvents but also polymeric materials with excellent transparency and crystallization property to form a large size crystal. A nonlinear optical device utilizing an organic material has been known, in which an input power (P i ) is a gating pulse light to obtain an output power light responsive to the wave form of the gate pulses. In this connection, reference should be made to E. P. Ippen and C. V. Shank, Appl. Phys. Lett., 26 (3), 92 (1975). Fig. 1 shows diagrammatically a known nonlinear optical device. Referring to Fig. 1, polarizers 4a and 4b are disposed with their polarization axes perpendicular with each other. A nonlinear refractive index kerr medium 1 comprises a 1 mm thick glass cell containing liquid carbon disulfide (CS₂). With the construction shown in Fig. 1, the linear polarization of the input power transmitting through the polarizer 4a is converted to the elliptical polarization due to the change in refractive index of the nonlinear refractive index kerr medium 1 as far as gate pulses P g are supplied. As the result, a portion of the input light can transmit through the perpendicular polarizer 4b, and thus the input power is optically switched by the gate light pulses. The relative signal intensity T of the input power takes the maximum intensity when the angle between the polarized gate light and the input power is 45°. The relative signal intensity T is represented by the following equations (1) and (2). T = sin²(Δ/2) (1) Δ =2 πn₂LI in /λ (2) In the equations set forth above, L is the length of the nonlinear refractive index kerr medium, λ is the wavelength of the input power, I in is the intensity of the gate light, n₂ is the nonlinear refractive index. When is sufficiently small, the equation (1) may be transformed as follows. T α n₂²L²I in ² (3) It will be seen from equation (3) that T is in proportion to the square of n₂. This known CS₂ optically-gated optical switch was prepared and tested. When λ was 0.83 µm, L was 1 mm and I in was 300 MW/cm², the relative signal intensity T was 1%. Substituting these results into the equations (1) and (2), the nonlinear refractive index n₂ was calculated as follows. n₂ = 8.8 x 10⁻¹⁴ cm²/W (4) The nonlinear susceptivity χ (3) was calculated from the value of n₂ to find that χ (3) = 4.2 x 10⁻¹² e.s.u. The known CS₂ type optically-gated optical switch exhibits a high speed response time in the order of 1 picosecond and thus can be used for instantaneous photographing or in a high speed spectrographic measuring apparatus. However, the nonlinear refractive index of the known CS₂ optically-gated optical switch is not so high, and thus it requires that the gate light has an extremely high intensity. Accordingly, another object of this invention is to provide a high speed and highly efficient nonlinear optical device which is operative with a light having a relatively low light intensity. A principal feature of the organic nonlinear optical material, according to this invention, resides in that it has a remarkably high nonlinear response efficiency as a nonlinear optical material made of a low molecular weight compound in which substituents serving as a donor and an acceptor are asymmetrically disposed in the molecule. Secondly, the material of this invention is improved in processibility in that it can be dissolved in a variety of solvents and polymer matrices to form concentrated solutions or in that a large single crystal can be formed therefrom. The organic nonlinear optical materials provided by this invention are derivatives of β-nitrostyrene having a substituted amino group at the para position as represented by the following general formula (1) or derivatives of p-(β-nitroethylenyl)-julolidine another type congugated system stylene represented by the following general formula (2) . wherein each of R₁ and R₂ of the substituted amino group at the para position stands for an alkyl or hydroxyalkyl group having 2 to 6 carbon atoms, R₁ and R₂ being same or different groups, and X₁, X₂, X₃ and X₄ each stands for at least one selected from the group consisting of hydrogen atom, hydroxyl group, halogen atoms, alkyl groups, alkoxy groups, alkyl ester groups and alkylamide groups, X₁, X₂, X₃ and X₄ being the same or different groups; and when R₁ is an alkyl group, R₂ may additionally represent an acryloyloxy alkyl group having 2 to 6 carbon atoms or a methacryloyloxy alkyl group having 2 to 6 carbon atoms, wherein, however, in case of a 4-diethylamino group at least one of the substituents X¹, X², X³ and X⁴ is not H and there is no o- substitution with Cl. wherein X₁ and X₂ may be the same or different groups and each stands for hydrogen atom, hydroxyl group, a halogen atom, an alkyl group, an alkoxy group, an alkyl ester group or an alkylamide group. The present invention further provides a nonlinear optical device comprising an optical medium and an optical element including a polarizer, an optical resonator and a reflector, said optical medium comprising an organic nonlinear optical material selected from the group consisting of derivatives (1) of 4-(N,N-dialkyl)amino-β-nitrostyrene and derivatives (2) of p-(β-nitroethylenyl)-julolidine. BRIEF DESCRIPTION OF THE DRAWINGS: Fig. 1 is a view showing diagrammatically the construction of a known nonlinear optical device and an optical switch; Fig. 2 is a chart showing the ¹HNMR of 4-(N,N-diethyl)amino-β-nitrostyrene; Fig. 3 is a chart showing the visible light absorption spectrum of a thin PMMA film doped with 4-(N,N-diethyl)amino-β-nitrostyrene according to this invention; Fig. 4 is a graph showing the relative signal intensity in terms of the concentration (wt%) of 4-(N,N-diethyl)amino-β-nitrostyrene dissolved in dimethylformamide; Fig. 5 shows the change in nonlinear refractive index n₂ of 4-(N,N-diethyl)amino-β-nitrostyrene dissolved in various solvents; Fig. 6(a) is a schematic illustration of a nonlinear optical device according to this invention; Fig. 6(b) is a chart showing the limitter operation of the device shown in Fig. 6(a); Fig. 6(c) is a chart showing the bistable operation of the device shown in Fig. 6(a); and Fig. 7 is a schematic illustration of a phase conjugated wave generator according to this invention. DESCRIPTION OF PREFERRED EMBODIMENT : It is an important feature of the organic nonlinear optical material of this invention that the structure having the π-conjugated chain is styrene or julolidine. The styrene or julolidine structure has a higher nonlinear polarizability per a unit volume than the stilbene structure which has a larger number of π-electrons. Furthermore, since the styrene structure or julolidine structure is compact, the organic nonlinear optical materials of this invention having the styrene structures or julolidine structures are superior over the compounds having stilbene or other structures in solubility in solvent and polymer matrices and also improved in crystallization property to form larger size crystals. In the derivatives of 4-(N,N-dialkyl)amino-β-nitrostyrene constituting the organic nonlinear optical materials of this invention, the behaviour as electron donator and solubility of the material are effectively improved when both of R₁ and R₂ are ethyl groups or R₁ is ethyl group and R₂ is hydroxylethyl group. The structure having the electron donating positions as represented by the general formula (2) attributes the delocalization of π-electrons by the strong conjugation of π-electrons in the ring and the lone electron pair of amine group and the improvement in solubility due to the bulkness of methylene group. All of X₁, X₂, X₃ and X₄ attached to the benzene ring of 4-(N,N-diethyl)amino-β-nitrostyrene and X₁ and X₂ of p-(β-nitroethylenyl)-julolidine may be hydrogen to exhibit enhanced effect, and likewise enhanced effect may be obtained when either one of these substituents is hydroxyl group, a halogen atom, an alkyl group, an alkoxy group, an alkyl ester group or alkylamide group with the remaining substituents being hydrogen. All of the derivatives of 4-(N,N-diethyl)amino-β-nitrostyrene, according to this invention, are excellent in solubility and thus polymer matrices may be doped therewith in high concentration. The derivatives of 4-(N,N-diethyl)amino-β-nitrostyrene, according to this invention, may be dissolved in a variety of organic solvents to give concentrated solutions. Particularly, they may be dissolved in organic solvents each having a dielectric constant higher than that of chloroform, and may also be dissolved in a mixture of organic solvents each having a dielectric constant higher than that of chloroform with other organic solvents to give concentrated solutions. Particularly preferred solvents are those each having an aromatic ring and having a dielectric constant higher than that of chloroform. For example, poly(methyl methacrylate) may be doped with 4-(N,N-diethyl)amino-β-nitrostyrene by a process comprising the steps of dissolving 4-(N,N-diethyl)amino-β-nitrostyrene in acetone, dissolving poly(methyl methacrylate) in acetone, mixing the solution of 4-(N,N-diethyl)amino-β-nitrostyrene in acetone together with the solution of poly(methyl methacrylate) in acetone, and then removing acetone from the mixed solution. Alternatively, a transparent polymer may be doped with an organic nonlinear optical material of this invention by the steps of melting the transparent polymer to fluidize the same, adding the organic nonlinear optical material of this invention to the molten transparent polymer, mixing and then cooling to solidify the transparent polymer. Transparent polymers which may be used as the matrix materials for the organic nonliner optical materials of this invention include polymers, copolymers and mixtures thereof. The known p-(N,N-dimethyl)amino-β-nitrostyrene is poor in solubility in organic solvents. For example, the solubility thereof is only 5 wt% in dimethylformamide and only 2 wt% in ethanol. In contrast thereto, the solubility of 4-(N,N-diethyl)amino-β-nitrostyrene provided by this invention is more than 50wt% in dimethylformamide and more than 40 wt% in ethanol. Likewise, the solubility of p-(N-ethyl-N-hydroxyethyl)amino-β-nitrostyrene in a variety of organic solvents is more than 30 wt%. Only 2.5 wt% of diethylamino-β-nitrostilbene can be dissolved in poly(methyl methacrylate) at the most. In contrast thereto, 30 wt% or more of 4-(N,N-diethyl)amino-β-nitrostyrene can be dissolved in poly(methyl methacrylate). Likewise, 25 wt% or more of p-(N-ethyl-N-hydroxyethyl)amino-β-nitrostyrene can be dissolved in poly(methyl methacrylate). It is difficult to form a large size single crystal of the known N,N-dimethylamino-β-nitrostyrene by recrystallization from a solution thereof in a solvent, the maximum dimensions of the obtainable single crystal being 3 mm X 5 mm X 10 mm. A larger single crystal of a derivative of p-(N,N-diethyl)amino-β-nitrostyrene may be easily obtained by recrystallization from a solution thereof in a solvent, the dimensions of the obtainable single crystal being 8 mm X 10 mm X 50 mm or more. In the derivatives of 4-(N,N-dialkyl)amino-β-nitrostyrene constituting the organic nonlinear optical materials of this invention, when either one of R₁ and R₂ is an hydroxyalkyl group and the other is an alkyl group, the hydroxyl group of the hydroxyalkyl group may be reacted with acrylic acid, methacrylic acid or alkyl esters of acrylic or methacrylic acid to introduce acryloyl or methacryloyl group in the resultant compound. For example, when acrylic acid is reacted with a derivative of amino-β-nitrostyrene having hydroxyethyl group, a derivative of amino-β-nitrostyrene having acryloyloxy group bonded to ethyl group is produced as represented by the following reaction equation of: A polymer-form nonlinear optical material having the dye attached structure may be obtained by polymerizing 4-(N-acryloyloxyethyl-N-ethyl)amino-β-nitrostyrene with methyl methacrylate in the presence of a polymerization catalyst. Likewise, by using methacrylic acid or esters of methacrylic acid, 4-(N-methacryloyloxyethyl-N-ethyl)amino-β-nitrostyrene may be prepared, and they may be copolymerized with various monomers forming transparent polymers to obtain nonlinear optical polymers having dye attached structures. In the derivatives of 4-(N,N-dialkyl)amino-β-nitrostyrene used as the organic nonlinear optical materials of this invention and having substituents X₁, X₂, X₃ and X₄ wherein at least one of them is hydroxyl group, acryloyl or methacryloyl group may be introduced by reacting the hydroxyl group attached to the benzene ring with a variety of derivatives of acrylic or methacrylic acid. The thus prepared 4-(N,N-dialkyl)amino-β-nitro-2-acryloyloxystyrene may be copolymerized with a monomer which forms a transparent polymer in the presence of a polymerization catalyst to prepare a nonlinear optical polymer having dye attached structure. Likewise, by using a derivative of methacrylic acid, methacryloyloxy group may be introduced into the benzene ring. When either one of X₁ or X₂ of p-(β-nitro-ethylenyl)-julolidine used as the organic nonlinear optical material is substituted by hydroxyl group, the substituting hydroxyl group may be converted to acryloyloxy or methacryloyloxy group by reacting the substituting hydroxyl group with a derivative of acrylic or methacrylic acid. Thus, a polymer usable as the nonlinear optical material and having dye attached structure, as represented by the following structural formula, may be prepared by copolymerizing with a monomer forming a transparent polymer. In the structural formula set forth above, m and n stand for molar fractions of the copolymerized monomers. Typical examples of compounds which are relevant per se to organic nonlinear optical materials or else constitute an essential part of the nonlinear optical device according to this invention will be set forth hereinbelow: 4-(N,N-diethyl)amino-β-nitrostyrene; DEANST 4-(β-nitroethylenyl)julolidine; JANST 4-(N-ethyl-N-hydroxyethyl)amino-β-nitrostyrene; EOEANST 4-(N,N-diethyl)amino-β-nitro-2-hydroxystyrene; Oh-DEANST 4-(N,N-diethyl)amino-β-nitrostyrene poly(methyl methacrylate) (doping); DEANST-PMMA 4-(N,N-diethyl)amino-β-nitrostyrene-Poly(2,2,3,3-tetra fluoropropyl) Methacrylate-Methylmethacrylate Copolymer; DEANST-Fluoro resin-MMA Copolymer 4-(N-ethyl-N-acryloyloxyethyl)amino-β-nitrostyrene-Methyl Methacrylate Copolymer; (DEANST-AP)-MMA Copolymer 4-(N,N-diethyl)amino-β-nitro-3-chlorostyrene; Cl-DEANST 4-(N,N-diethyl)amino-β-nitro-3-methoxystyrene; MeO-DEANST 4-(N,N-diethyl)amino-β-nitro-3-acetoxystyrene; AcO-DEANST 4-(N,N-diethyl)amino-β-nitro-2-methylstyrene; Me-DEANST 4-(N,N-diethyl)amino-β-nitro-2-acetylaminostyrene; AcNH-DEANST The organic nonlinear optical materials, according to this invention, exhibit enhanced third-order nonlinear optical properties. They are also improved in crystallization property and solubility, and thus large crystals with excellent characteristics and polymer films can be easily fabricated from them. The organic nonlinear optical materials of this invention may be dissolved in solvents having high dielectric constants, such as nitrobenzene, and the solutions are contained in sealed optical cells to prepare optical media each having high nonlinear refractive index. It had not been known until we found that the nonlinear refractive index was variable by differring the used solvent. It is preferable to use a solvent which has a dielectric constant higher than that of chloroform. Examples of preferable solvents include N-methylacetoamide, N-methylformamide, formamide, acetoamide, dimethylformamide, N,N-dimethylacetoamide, acetonitrile, nitromethane, acrylonitrile, methanol, diethylene glycol, benzonitrile, ethanol, acetoaldehyde, propanol, benzaldehyde, benzil alcohol and pyridine. A nonlinear refractive kerr medium may be fabricated by dissolving 4-(N,N-diethyl)amino-β-nitrostyrene according to this invention in a transparent polymer material followed by solidification of the polymer material. Alternatively, a transparent polymer is melted and an organic nonlinear optical material of this invention is added thereto, followed by mixing and cooling to solidify the mixture, whereby an optical medium is produced. As a still further process for the preparation of a nonlinear refractive kerr medium, a single crystal of 4-(N,N-diethyl)amino-β-nitrostyrene is prepared since a large single crystal can be formed from the material of this invention. The thus prepared nonlinear refractive kerr medium may be used as an essential element for a low optical power operative optically gated optical switch, a bistable device for optical instruments and a phase-conjugated-wave-generator, and slso used for the production of an optical integrated element for optical communication systems. EXAMPLES OF THE INVENTION: The present invention will now be described more in detail with reference to some examples thereof taken in conjunction with the appendated drawings. Example 1: Synthesis of 4-(N,N-diethyl)amino-β-nitrostyrene (DEANST) A solution was prepared by dissolving 118 grams (0.57 mol) of p-(N,N-diethyl)aminobenzaldehyde in 500 ml of nitromethane, and added with 17 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from ethanol for two times. 107 grams of red crystal was obtained. The yield was 75%. The product, p-(N,N-diethyl)amino-β-nitrostyrene, had a melting point of 95°C. The ¹H-NMR spectrum of the product is shown in Fig. 2, and details of the NMR analysis are set forth below. Solvent: CDCl₃, δ C-H (aromatic and vinyl): 6.8 to 8.0 ppm, δ C-H (methyl): 1.2 ppm, δ C-H (methylene): 3.4 ppm, Elemental Analysis: C₁₂H₁₆N₂O₂ (MW= 220.27) Cald.: C 65.44, H 7.32, N 12.72 Found: C 65.57, H 7.20, N 12.92 Example 2: Synthesis of p-(β-nitroethylenyl)-julolidine (JANST) A solution was prepared by dissolving 60 grams (0.3 mol) of p-formyljulolidine in 250 ml of nitromethane, and added with 8 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from methanol for two times. 50 grams of red crystal was obtained. The yield was 69%. Example 3: Synthesis of 4-(N-ethyl-N-hydroxyethyl)amino-β-nitrostyrene (EOEANST) A solution was prepared by dissolving 60 grams (0.31 mol) of 4-(N-ethyl-N-hydroxyethyl)aminobenzaldehyde in 250 ml of nitromethane, and added with 8 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 42 grams of red crystal was obtained. The yield was 66%. Example 4: Synthesis of 4-(N,N-diethyl)amino-β-nitro-2-hydroxystyrene (Oh-DEANST) A solution was prepared by dissolving 60 grams (0.31 mol) of 2-hydroxy-4-(N,N-diethyl)aminobenzaldehyde in 250 ml of nitromethane, and added with 8 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 34 grams of red crystal was obtained. The yield was 53%. Example 5: Synthesis of 4-(N,N-diethyl)amino-β-nitro-3-chlorostyrene A solution was prepared by dissolving 34 grams (0.16 mol) of 3-chloro-4-(N,N-diethyl)aminobenzaldehyde in 150 ml of nitromethane, and added with 5 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 16 grams of red crystal was obtained. The yield was 39%. Example 6: Synthesis of 4-(N,N-diethyl)amino-β-nitro-2-methoxystyrene (MeO-DEANST) A solution was prepared by dissolving 30 grams (0.14 mol) of 2-methoxy-4-(N,N-diethylamino)benzaldehyde in 150 ml of nitromethane, and added with 4 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 16 grams of red crystal was obtained. The yield was 44%. Example 7: Synthesis of 4-(N,N-diethyl)amino-β-nitro-2-acetyloxystyrene (AcO-DEANST) A solution was prepared by dissolving 23.5 grams (0.10 mol) of 2-acetyloxy-4-(N,N-diethylamino)benzaldehyde in 100 ml of nitromethane, and added with 3 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 10 grams of red crystal was obtained. The yield was 36%. Example 8: Synthesis of 4-(N,N-diethyl)amino-β-nitro-3-methylstyrene (Me-DEANST) A solution was prepared by dissolving 30 grams (0.16 mol) of 3-methyl-4-(N,N-diethylamino)benzaldehyde in 150 ml of nitromethane, and added with 5 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 17 grams of red crystal was obtained. The yield was 45%. Example 9: Synthesis of 4-(N,N-diethyl)amino-β-nitro-3-acetylaminostyrene (AcNH-DEANST) A solution was prepared by dissolving 28 grams (0.12 mol) of 3-acetylamino-4-(N,N-diethylamino)benzaldehyde in 120 ml of nitromethane, and added with 4 grams of ammonium acetate. The mixture was heated at 100°C for 5 hours under agitation. The reaction solution was then cooled on a dry ice-acetone bath until crystallization had been completed. The separated solid (crystal) was filtered off and dried in vacuum. The obtained product was recrystallized from acetonitrile for two times. 10 grams of red crystal was obtained. The yield was 36%. Example 10: Preparation of 4-(N,N-diethyl)amino-β-nitrostyrene(DEANST)/Polymethylmethacrylate(PMMA) (Doping) A 9.8 wt% solution of p-(N,N-diethyl)amino-β-nitrostyrene in chloroform and a 18.2 wt% solution of poly(methyl methacrylate) in chloroform were mixed in a mixing ratio of 1:1. The mixed solution was coated on a glass plate by spin coating to form a 1 micron thick film of 35 wt% p-(N,N-diethyl)amino-β-nitrostyrene-polymethyl methacrylate. The visible light absorption spectrum of the thus produced film is shown in Fig. 3. Example 11: Preparation of 4-(N,N-diethyl)amino-β-nitrostyrene(DEANST)/(2,2,3,3-tetrafluoropropyl)methacrylate(Fluoro Resin)-MMA Copolymer A 12 wt% solution of 4-(N,N-diethyl)amino-β-nitrostyrene in acetone and a 18 wt% solution of a 2:1 copolymer of 2,2,3,3-tetrafluoropropylmethacrylate/methyl methacrylate in acetone in a mixing ratio of 1:1. The mixed solution was coated on a glass plate by spin coating to form a 1.5 micron thick film of 40 wt% 4-(N,N-diethyl)amino-β-nitrostyrene(DEANST)/2,2,3,3-tetrafluoropropylmethacrylate-MMA copolymer. Example 12: Synthesis of 4-(N-ethyl-N-acryloyloxyethyl)amino-β-nitrostyrene(DEANST-Ap)/Methyl Methacrylate(MMA) Copolymer A solution was prepared by dissolving 4.5 grams of methyl methacrylate, 24.2 grams of 4-(N-ethyl-N-(2-acryloyloxyethyl)amino)-β-nitrostyrene and 0.14 gram of 2,2′-azobis(2-methylpropanenitrile) in 70 ml of dehydrated dioxane. The solution was charged in a glass polymerization ample, followed by evacuation and sealing, and then the solution was allowed to react at 60°C for 24 hours. The reaction solution was poured into hexane, whereby a precipitate was separated. The precipitate was filtered and then rinsed with methanol. The rinsed precipitate was dried to obtain a product polymer. The molar fraction of the copolymer was 0.3 for MMA and 0.7 for DEANST-Ap. The following is the structural formula of the copolymer. Example 13 A neodymium-yttrium-aluminium garnet (Nd-YAG) laser was used as the light source for the measurement of the third harmonic generation (THG). The laser had a wavelength of 1.06 µm and an intensity of 50 MW/cm². After filtering visible light, the laser beam was focused by a lens and irradiated on a sample and the light rays emitted from the sample was passed through a filter so that only the intensity of THG was detected while using an photo-multiplier tube. The sample subjected to measurement was prepared by pulverizing a crystal of an organic nonlinear material to adjust the particle size to 105 to 120 microns. In order to ascertain that the origin of the THG was not the second-order cascading in third-order nonlinear optical processes, as observed in urea or 2-methyl-4-nitroaniline (MNA), but the pure THG effect, the second harmonic generation (hereinafter referred to as SHG) of the same sample was measured. Table 1 shows the results of measurements of harmonic generation intensities for the organic nonlinear optical materials of this invention and for comparative samples. The relative SHG intensities compared to urea of individual samples are shown in the third column of Table 1, which reveal that the results are approximately zero (≈0). This means that the measured results are not the second-order cascading in third-order nonlinear processes (w + 2w → 3w), but show pure third-order effects. In the fourth column of the Table, the relative THG intensities compared to p-nitroaniline are shown. As shown, the organic nonlinear optical materials of this invention has the relative THG intensities ranging from 300 to 720, whereas the results of the comparative samples or comparative examples range from 50 to 80. The compounds used in the Comparative Examples will be set forth below. 1. 4-(N,N-dimethylamino)-β-nitrostyrene, DMA-NS 2. 4-(N,N-diethylamino)-4′-nitrostilbene, DEANS 3. 4-(β-nitrophenyl)ethylenyl-julolidine, JANS 4. 4-(N,N-dimethyl)amino-β-nitro-2-hydroxystyrene, Oh-DMANST Example No. Organic Nonlinear Optical Material Relative Intensity of SHG to Urea Ratio Relative Intensity of THG to p-Nitroaniline Ratio Working Examples of the Invention 1 DEANST ≈0 720 2 JANST ≈0 500 3 EOEANST ≈0 680 4 Oh-DEANST ≈0 630 5 Cl-DEANST ≈0 480 6 MeO-DEANST ≈0 460 7 AcO-DEANST ≈0 560 8 Me-DEANST ≈0 510 9 Ac-NH-DEANST ≈0 450 10 DEANST-PMMA (Doping) ≈0 300 11 DEANST-Fluoro Resin/MMA Copolymer ≈0 320 12 DEANST-Ap/MMA Copolymer ≈0 400 Comparative Examples (Comparative Samples) 1 DMA-NS ≈0 50 2 DEANS ≈0 60 3 JANS ≈0 80 4 Oh-DMANST ≈0 60 Example 14 An optically-gated optical switch device, in which p-(N,N-diethyl)amino-β-nitrostyrene prepared by Example 1 is used as an optical medium, will now be described. A solution prepared by dissolving p-(N,N-diethyl)amino-β-nitrostyrene in dimethylformamide (DMF, ε= 37.8) was contained in a sealed glass vessel to be used as a nonlinear refractive index kerr medium. The other parts of the construction of the device were the same as shown in Fig. 2. Fig. 4 shows the change in relative signal intensity of the optical switch in terms of the change in concentration of 4-(N,N-diethyl)amino-β-nitrostyrene. As seen from Fig. 4, the instantaneous transmittance is increased in proportion to the second power of the intensity. As the concentration is increased above 23 wt%, the instantaneous transmittance exceeds the instantaneous transmittance of liquid carbon disulfide (CS₂) which has been well known and used widely up to date. The nonlinear refractive index n₂ of the medium when the concentration of 4-(N,N-diethyl)amino-β-nitrostyrene is 40 wt% was calculated from Equation (3) set forth hereinbefore to find that n₂ took the following value. n₂ = 1.5 x 10⁻¹³ cm²/W(χ (3) = 7.3 x 10⁻¹² e.s.u.) The abscissa of the graph of Fig. 5 indicates the dielectric constant of various solvents used for dissolving the organic nonlinear optical material of the invention, individual solvents being used at the same molar concentration. The nonlinear refractive indices n₂ of the organic nonlinear optical materials when dissolved in individual solvents are plotted in the graph in terms of the dielectric constants of respective solvent group. The used solvents are aromatic solvents including nitrobenzene (A), a mixture of nitrobenzene and chlorobenzene (B), chlorobenzene (C) and benzene (D), and non-aromatic system solvents including dimethylformamide (E), acetone (F) and chloroform (G) As seen from Fig. 5, the value of n₂ becomes larger as the dielectric constant of the used solvent is higher, and aromatic solvent group are generally more preferable than non-aromatic system solvents. The highest efficiency was obtained when 4-(N,N-diethyl)amino-β-nitrostyrene was dissolved in nitrobenzene in an amount corresponding to the highest dissoluble concentration. At that time, n₂ took the value of 2.2 x 10⁻¹³ cm²/W. The value was about 2.5 times as high as that obtainable by using the known CS₂. The found effect indicated by the transmittance was about six times (2.5² = 6.25) as high as that obtainable by the use of CS₂. Search and identification of optimal solvents disclosed herein are the pioneer works done by us. Example 15 Another embodiment of the nonlinear optical device, according to this invention, is shown in Fig. 6(a). A nonlinear optical kerr medium 1 comprises a solution of 4-(N,N-diethyl)amino-β-nitrostyrene dissolved in a solvent, and the meduim is opposing to mirrors 3a and 3b each of which is made of a multi-layered film of ferroelectic material reflecting 90% of input light and transmitting the remaining 10% of input light. The medium 1 and the opposing mirrors 3a and 3b constitute an optical resonator. The aforementioned device may be operated by varying the wavelength of input light a little or by changing the resonator length, i.e. the spacing between the mirrors 3a and 3b, so that the resonator is adjusted to resonate. In this device, a light ray having a wavelength of 1.064 microns from an Nd-YAG laser was used, and the device was actuated by changing the resonator length. The interrelations between the intensity of input power P i and the intensity of output power P t are shown in Figs. 6(b) and 6(c) to find that the limiting operation and the bistable operation took places. In each of Figs. 6(b) and 6(c), the abscissa indicates the input power P i and the ordiate indicates the output power (signal) P t . The minimum input power (P i min ) can be analytically obtained from the following equation of: P i min = (Kλ)/(n₂l); wherein λ is the wavelength of used light, l is the length of the optical medium, k is a coefficient determined by the reflectivity of mirror and the adjustment of resonator length and generally taking a value of about 0.001. When the effective output of the pulse oscillation is set to 50 mW and a semiconductor laser having an oscillation wavelength of 0.83 micrometer is used, the intensity of output power is calculated to be 6 x 10⁶ W/cm² by focusing the beam diameter to 1 micrometer. The intensity of the output power is sufficiently high as compared to the minimum input power P i min of the aforementioned nonlinear optical device at that wavelength. This nonlinear optical device, according to this invention, could be operated while using a semiconductor laser as the light source. The response time of 4-(N,N-diethyl)amino-β-nitrostyrene of this invention is estimated to be approximately 10⁻¹² second. However, the response time of the device is determined by the longer one of the response time of the used medium and lifetime t p of photon in the oscillator. The lifetime of photon t p is calculated from the following equation of: t p = - l op /(c x lnR); wherein l op is the wavelength of the oscillator, c is the velosity of light, and R is the reflectivity of the mirror. The lifetime of photon is calculated to be 6 x 10⁻¹¹ seconds and thus t p >t so that the lifetime of photon determines the response time of the device. It is thus ascertained that the response time of this embodiment of the invention is shorter than 10⁻¹⁰ second. Example 16 A phase conjugated wave generator according to this invention will now be described with reference to Fig. 7. The device comprises half-mirrors 5a, 5ba, reflector 6 and a liquid optical medium 1 composed of 4-(N,N-diethyl)amino-β-nitrostyrene described in Example 14. The device is an optical alignment referred to as a degenerated four wave mixing. In detail, when three input light waves, i.e. a light wave A₁, a light wave A₂ incident from the direction reverse to the incident direction of the light wave A₁ and a light wave A p incident obliquely, are incident upon an optical medium having a nonlinear optical refractive index, the fourth light wave A c where conjugated in regard to the light wave A p only the special phase term is generated. The phase-conjugated-wave attracts attention in the image processing technology as it may be effectively used for correction of image or effective means for real time holography. It was ascertained that the device of this embodiment exhibited a high speed response could be operated with an input power of relatively low intensity.

Claims: An organic nonlinear optical material represented by the following general formula (1): wherein each of R₁ and R₂ of the substituted amino group at the para position stands for an alkyl or hydroxyalkyl group having 2 to 6 carbon atoms, R₁ and R₂ being the same or different groups; and X₁, X₂, X₃ and X₄ each stands for at least one selected from the group consisting of hydrogen atom, hydroxyl group, halogen atoms, alkyl groups, alkoxy groups, alkyl ester groups, alkylamide groups, acryloyloxy group and methacryloyloxy group, X₁, X₂, X₃ and X₄ being the same or different groups; and when R₁ is an alkyl group, R₂ may additionally represent an acryloyloxy alkyl group having 2 to 6 carbon atoms or a methacryloyloxy alkyl group having 2 to 6 carbon atoms, wherein, however, in case of a 4- diethylamino group at least one of the substituents X¹, X² , X³ and X⁴ is not H and there is no o- substitution with Cl. An organic nonlinear optical material according to claim 1, wherein either one of R₁ and R₂ of the substituted amino group at the para position is ethyl group and the other is hydroxyethyl group. An organic nonlinear optical material according to claim 1 or 2, wherein X₁ is hydroxyl group and all of X₂, X₃ and X₄ are hydrogen atoms. An organic nonlinear optical material according to claim 1, wherein R₁ is an ethyl group and R₂ is an acryloyloxy alkyl group having 2 to 6 carbon atoms or a methacryloyloxy alkyl group having 2 to 6 carbon atoms. A copolymer formed from a polymerizable unsaturated carboxylic acid ester and 4-(N-acryloyloxyethyl-N-ethyl)amino-β-nitrostyrene or 4-(N-ethyl-N-methacryloyloxyethyl)amino-β-nitrostyrene. A copolymer according to claim 5, wherein said polymerizable unsaturated carboxylic acid ester is selected from the group consisting of alkyl acrylates and alkyl methacrylates. A transparent polymer doped with an organic nonlinear optical material represented by the following general formula (1): wherein each of R₁ and R₂ of the substituted amino group at the para position stands for an alkyl or hydroxyalkyl group having 2 to 6 carbon atoms, R₁ and R₂ being the same or different groups; and X₁, X₂, X₃ and X₄ each stands for at least one selected from the group consisting of hydrogen atom, hydroxyl group, halogen atoms, alkyl groups, alkoxy groups, alkyl ester groups, alkylamide groups, acryloyloxy group and methacryloyloxy group, X₁, X₂, X₃ and X₄ being the same or different groups; and when R₁ is an alkyl group, R₂ may additionally represent an acryloyloxy alkyl group having 2 to 6 carbon atoms or a methacryloyloxy alkyl group having 2 to 6 carbon atoms. A transparent polymer doped with an organic nonlinear optical material according to claim 7, wherein said transparent polymer is selected from the group consisting of polymethyl methacrylate, poly(fluoroalkyl methacrylates) and copolymers thereof. An organic nonlinear optical material represented by the following general formula (2): wherein X₁ and X₂ may be the same or different groups and each stands for hydrogen atom, hydroxyl group, halogen atoms, alkyl groups, alkoxy groups, alkyl ester groups, alkylamide groups, acryloyloxy group and methacryloyloxy group. An organic nonlinear optical material according to claim 9, wherein both of X₁ and X₂ are hydrogen atoms. An organic nonlinear optical material according to claim 9, wherein X₁ is hydroxyl group and X₂ is hydrogen atom. An organic nonlinear optical material according to claim 9, wherein X₁ is an acryloyloxy group or a methacryloyloxy group and X₂ is a hydrogen atom. An organic nonlinear optical material comprising a copolymer of p-(β-nitroethylenyl)-meta-acryloyloxyjulolidine or p-(β-nitroethylenyl)-meta-methacryloyloxyjulolidine with a polymerizable unsaturated carboxylic acid ester selected from the group consisting of methyl methacrylate, alkyl acrylates and mixtures thereof. A transparent polymer doped with an organic nonlinear optical material according to anyone of claims 9 to 13. A nonlinear optical device characterized by an optical medium (1) and an optical element including a polarizer (4a, 4b), an optical resonator and a reflector (3a, 3b; 6), said optical medium (1) comprising an organic nonlinear optical material selected from the group consisting of those represented by the following general formulae (1) and (2): wherein each of R₁ and R₂ of the substituted amino group at the para position stands for an alkyl or hydroxyalkyl group having 2 to 6 carbon atoms, R₁ and R₂ being the same or different groups; and X₁, X₂, X₃ and X₄ each stands for at least one selected from the group consisting of hydrogen atom, hydroxyl group, halogen atoms, alkyl groups, alkoxy groups, alkyl ester groups, alkylamide groups, acryloyloxy group and methacryloyloxy group, X₁, X₂, X₃ and X₄ being the same or different groups; and when R₁ is an alkyl group, R₂ may additionally represent an acryloyloxy alkyl group having 2 to 6 carbon atoms or a methacryloyloxy alkyl group having 2 to 6 carbon atoms; wherein X₁ and X₂ may be the same or different groups and each stands for hydrogen atom, hydroxyl group, halogen atoms, alkyl groups, alkoxy groups, alkyl ester groups, alkylamide groups, acryloyloxy group and methacryloyloxy group; whereby the nonlinear refractive index of said organic nonlinear optical material is utilized in the assembled nonlinear optical device. A nonlinear optical device according to claim 15, wherein said organic nonlinear optical material is dissolved in an organic solvent having a dielectric constant higher than that of chloroform, or dissolved in a mixed solvent of an organic solvent having a dielectric constant higher than that of chloroform with one or more other organic solvents. A nonlinear optical device according to claim 16, wherein said organic solvent has a dielectric constant higher than that of chloroform and has an aromatic ring, and wherein said mixed solvent is a mixture of an organic solvent having a dielectric constant higher than that of chloroform and having an aromatic ring with one or more other organic solvents. A nonlinear optical device according to claim 15, wherein said optical medium comprises said organic nonlinear optical material dissolved in a transparent polymer material followed by solidification. A nonlinear optical device according to claim 18, wherein said transparent polymer material is selected from the group consisting of polymers each having a refractive index substantially equal to or less than that of poly(methyl methacrylate), copolymers each having a refractive index substantially equal to or less than that of poly(methyl methacrylate); and mixtures thereof. A nonlinear optical device according to claim 15, wherein said optical medium comprises a crystalline medium which is formed by crystallization of said organic nonlinear optical material.

Inventors: KAINO TOSHIKUNI, KANBARA HIROHISA, KUBODERA KENICHI, KURIHARA TAKASHI, MATSUMOTO SHIRO, KAINO, TOSHIKUNI, KANBARA, HIROHISA, KUBODERA, KENICHI, KURIHARA, TAKASHI, MATSUMOTO, SHIRO
Applicants: NIPPON TELEGRAPH & TELEPHONE, NIPPON TELEGRAPH AND TELEPHONE CORPORATION
Application year: 1989
Main classification: C07C211
IPC codes: C07C215, C07C233, C07C219, C07C211, G02F1, C07C217, C07D455, C08F12