WETTABLE, FLEXIBLE, OXYGEN PERMEABLE CONTACT LENS CONTAINING BLOCK COPOLYMER POLYSILOXANE-POLYOXYALKYLENE BACKBONE UNITS

Abstract: This invention relates to ophthalmic devices, such as contact lenses and intraocular implants, and particularly contact lenses of a block copoly­ mer containing polysiloxane and polyoxyalkylene oxide units possessing an advantageous blend of desirable properties including a) high oxygen permeability, b) good wettability, c) flexibility and d) optical clarity, in the ocular environment of use. Further disclosed are the preparation thereof and methods of treating vision defects therewith as well as the polymers which may be used for the ophthalmic devices.

Description: This invention relates to ophthalmic devices, such as contact lenses and intraocular implants, and particularly contact lenses of a block copolymer containing polysiloxane and polyoxyalkylene oxide units possessing an advantageous blend of desirable properties including a) high oxygen permeability, b) good wettability, c) flexibility and d) optical clarity, in the ocular environment of use as claimed in Claim 1, to a polymer as claimed in Claim 37 and the use of this polymer for the manufacture of an ophthalmic device as claimed in Claim 48. The use of siloxane containing materials of various types in the fabrication of ophthalmic devices is well known. Thus, in U.S. 3,996,187; 3,996,189; 3,341,490 and 3,228,741 there are described contact lenses fabricated from poly (organosiloxanes) containing fillers. While such lenses are generally soft and of high oxygen permeability, the use of fillers such as silica, is indicated in order to increase the otherwise generally poor tear strength and tensile strength. Also, such silicone rubber lenses are characteristically both hydrophobic and lipophilic. U.S. 3,808,178 discloses hard contact lenses fabricated from copolymers of a polysiloxanylalkyl acrylate or methacrylate ester and an alkyl acrylate or methacrylate ester. The monomers and polymers of the patent are hydrophobic and are incompatible with hydrophilic materials such as hydroxyethyl methacrylate. While the disclosed lenses have increased oxygen permeability, they are rigid. U.S. 4,136,250 discloses hydrogels of a copolymer of about 20 to about 90% of a hydrophilic (or mixture of hydrophilic and hydrophobic) monomer and about 10 to about 80% of a polyolefinic siloxane macromer which can be used to fabricate a contact lens. Typically, such hydrogels are recited to possess a degree of swelling of about 10 to about 12%. It has been found, however, that the pressure of substantial amounts of water in such hydrogels limits the oxygen permeability of such materials. U.S. 4,153,641 relates, in relevant part, to contact lenses fabricated from a polymer of a polyorganosiloxane terminated with vinylic groups, or copolymers thereof with other monomers. The exemplified products therein are hydrophobic in nature. U.S. 4,486,577 relates to copolymers of about 8 to 70% of a polysiloxane macromer containing at least two vinyl groups and 30-92% of a monomer which is at least predominantly water insoluble to make polymers useful, for example, as contact lenses. Generally, such prior art contact lens compositions are either insufficiently hydrophilic in terms of surface wettability to be acceptable to the contact lens profession, even though they may possess high oxygen permeability, or such contact lenses are of acceptable wettability but the hydrophilicity is coupled with water swellability, which tends to limit optimum oxygen permeability. It is an object of the present invention to overcome these and other disadvantages of the art by providing ophthalmic devices, such as contact lenses and corneal implants, possessing a high degree of surface wettability and possessing a high degree of oxygen permeability notwithstanding their swellability by employing a crosslinked block polymer containing polysiloxane and polyalkylene oxide units. A further object of the invention is to provide a method of correcting visual defects in the form of refractive errors by fitting to the patient's eye in need of the same a corrective contact lens of such polymer. These and other objects of the invention are apparent from the following detailed description of the invention. One embodiment of the present invention relates to an optically clear, hydrolytically stable, biologically inert, wettable, flexible, oxygen permeable ophthalmically acceptable polymer and device, such as a contact lens having at least 10% water content when swollen in its environment of use, which is fabricated from a crosslinked polymer of a reactive monomer having a segment S″ of the formula Ia, wherein a is 1 to 10; each D is independently oxygen or _N(R²¹)_; each W is a bond, oxygen or _N(R²¹)_; each L is independently _BRB′_, _BR_, _RB′_ or _R_; each S′ is independently a segment of formula II, each A is independently a segment of formula III, the terminal oxygen within each unit of formula III being replaceable by _N(R²¹)_; wherein each b, d and f is independently 0-4; q is a number from 1 to 1000; each x, y and z is independently 0 to 200, preferably 0 to 100 provided at least one of x, y and z is at least 1; such that (x + y + z) multiplied by q is 4 to 1000; each h and i is an integer from 1 to 6, v is an integer from 2 to 300, preferably 2 to 75, preferably 2 to 50, more preferably 10 to 50, most preferably 15 to 50; R¹ and R² are independently alkyl of up to 18 carbon atoms, or aryl of up to 12 carbon atoms, preferably lower alkyl or phenyl, most preferably methyl; each of R³, R⁴, R⁷-R¹⁰, R¹³-R¹⁶, R¹⁹ and R²⁰ is independently selected from the group consisting of hydrogen, halogen, (preferably fluorine or chlorine, more preferably fluorine), an aliphatic, aromatic or heterocyclic containing radical selected from unsubstituted C₁-C₁₆ alkyl; substituted C₁-C₁₆ alkyl; unsubstituted C₂-C₁₆ alkenyl; and substituted C₂-C₁₆ alkenyl; wherein the alkyl and alkenyl substituents are independently selected from C₁-C₁₆ alkoxycarbonyl, C₂-C₁₆ alkenyloxycarbonyl, fluoro, aryl of up to 10 carbon atoms, C₁-C₁₆ alkoxy, C₁-C₁₆ alkanoyloxy, aryloxy of up to 10 carbon atoms, C₃-C₆ alkenoyloxy, aroyl of up to 10 carbon atoms, aroyloxy of up to 11 carbon atoms, C₃-C₈ cycloalkyl, C₃-C₈ cycloalkoxy, C₃-C₈ cycloalkyl-carbonyloxy, C₃-C₈ cycloalkoxycarbonyl, oxacycloalkyl of up to 7 carbon atoms, oxacycloalkoxy of up to 7 carbon atoms, oxacycloalkoxy (up to 7 carbon atoms)-carbonyl, oxacycloalkyl (up to 7 carbon atoms)-carbonyloxy, and aryl (of up to 10 carbon atoms)-oxycarbonyl, each of said alkyl and alkenyl substituents being, in turn, optionally substituted by C₁-C₆ alkyl, fluoro or a C₁-C₆ alkoxy provided said last mentioned alkoxy is not bound to a carbon atom already singly bound to another oxygen atom; R³, R⁴, R⁷-R¹⁰, R¹³-R¹⁶, R¹⁹ and R²⁰ being further independently selected from aryl of up to 10 carbon atoms, C₃-C₈ cycloalkyl, and oxacycloalkyl of up to 7 carbon atoms, each of which may be unsubstituted or further substituted with a substituent selected from the group of substituents for said R³ alkyl set forth above; R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are selected from the same group set forth above for R³; and R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are further independently selected from C₁-C₁₆ alkoxycarbonyl, C₃-C₁₆ alkenoyloxy, C₂-C₁₆ alkenyloxycarbonyl, and C₁-C₁₆ alkanoyloxy, each of which may be further substituted by fluoro, aryl of up to 10 carbon atoms, or C₁-C₁₆ alkoxy, and R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are still further independently selected from aryloxy of up to 10 carbon atoms, cycloalkoxy of up to 8 carbon atoms, cycloalkyl (of up to 8 carbon atoms)-carbonyloxy, cycloalkoxy (of up to 8 carbon atoms)-carbonyl, aroyloxy of up to 11 carbon atoms, oxacycloalkoxy of up to 7 carbon atoms, oxacycloalkenyloxy of up to 7 carbon atoms, oxacycloalkoxy (of up to 7 carbon atoms)-carbonyl, oxacycloalkyl (of up to 7 carbon atoms)-carbonyloxy, and aryloxy (of up to 10 carbon atoms)-carbonyl, each of which may be further substituted by fluoro, C₁-C₆ alkyl or C₁-C₆ alkoxy, provided that any substituent having a singly bound oxygen atom as its link to the rest of the molecule may not be a substituent on the same carbon atom which is singly bonded to another oxygen atom; or 2 adjacent groups, selected from R³-R²⁰, together with the atoms to which they are attached may form a 5-8 membered cycloalkyl, oxacycloalkyl or bicycloalkyl ring; each R²¹ is independently selected from hydrogen, C₁-C₄ alkyl and phenyl, and is preferably hydrogen; each B and B′ is selected from with the carbonyl group being bound to A, S′, D or P′; and each R is independently a divalent linking group preferably selected from a) a divalent aliphatic group preferably alkyl, alkenyl or alkynyl, of up to 25 carbon atoms which may be interrupted by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino, or carbonylamino; b) a divalent 5-7 membered cycloaliphatic and 5-7 membered cycloaliphatic-C₁-C₂₀-aliphatic group; c) a divalent arylene group having 6-25, preferably 7-15 carbon atoms; and d) a divalent aralkyl or alkaryl group having 7 to 25, preferably 8-16 carbon atoms; e) a divalent alkylene-aryl-alkylene having 8 to 30 carbon atoms, wherein groups b), d) and e) can be optionally interrupted in their non-cyclic aliphatic and alkyl groups respectively by the same groups as in group a) and wherein the aryl rings in groups c), d) and e) may be further substituted with one or more substituents selected from halogen, preferably fluorine or chlorine, C₁-C₄ alkyl, preferably methyl, and C₁-C₁₂ perhalo alkyl, especially C₁-C₁₂ perfluoro alkyl; and wherein an interrupting group set forth in group a) may be present between the cyclic and non-cyclic portions of groups b), d) and e). The monomer preferably has segments of formula Ib, or of formula Ic, or of formula Id even more preferably said monomer is of formula I, and more preferably said monomer being divinylic; wherein D, A, L, S′, S″ are as defined hereinbefore; and wherein c is 1 to 10; e is zero or one; a times c is 1 to 10; La is selected from _BRB′_ and _BR_; L′ is hydrogen, P′-R_, P′-BR_, P′-RB′_, or P′-BRB′_; and L″ is hydrogen, or _P′, or, in case that e is zero, also _D-S′-BR-P′ or _D-S′-P′ and wherein P′ is hydrogen, amino, hydroxy, NCO, NCS, vinyl or a moiety containing a crosslinkable group which may be crosslinked when coreacted with a suitable crosslinking agent or when irradiated by actinic radiation. In the foregoing, all alkyl groups whether mentioned alone or as part of another group are preferably C₁-C₄ alkyl, such as methyl, ethyl, propyl and butyl, especially t-butyl, with the exception that adjacent groups on aryl rings cannot each be t-butyl. These alkyl groups may be straight chain or branched chain. When the alkyl is a substituent on a phenyl ring, it is preferably attached at the para position. Preferably alkenyl groups, whether alone or as part of another group, are C₂-C₄ alkenyl, such as ethenyl, propenyl and butenyl. Preferred aryl groups (whether alone or as part of another group) are phenyl and naphthyl, more preferably phenyl. Preferably the aryl groups are still further substituted by C₁-C₄ alkyl, more preferably t-butyl, most preferably in the para position. Halogen may be chloro, bromo, iodo and fluoro. Preferably b, d and f are independently 0-3, more preferably 0-2, most preferably 0 or 1. While the group identified by formula I may be highly halogenated, it is preferably at least 25% halogen free, more preferably 30%, still more preferably 40%, and most preferably substantially halogen free. Wherever cyclo groups are indicated, whether carbocyclic or heterocyclic they preferably have 5-6 ring members and the heterocyclics preferably have only carbon atoms and an oxygen atom as ring members. Bicycloalkyl is understood to cover those groups when two adjacent R groups in a segment of formula III together form a ring and one of them already is a cycloalkyl group. In other words a fused ring system made up of two geminal R groups and the carbon atom to which they are attached results. For example if R³ is cyclopropyl and R⁴ is methyl then R³ and R⁴ together with the carbon to which it is attached could be (2,1,0) cyclopent-2,2-diyl. In formula I, when b is greater than one, each of the multiple R⁵ and R⁶ groups may be the same or different; however preferably all of the R⁵ groups are the same and all of the R⁶ groups are the same. The same is true with respect to d, R¹¹, and R¹²; and f, R¹⁷, and R¹⁸. Preferably, each of b, d and f is independently an integer of 0 to 2, and most preferably zero or one. In one aspect of the invention, each of R³-R⁷, R⁹-R¹³ and R¹⁵-R¹⁹ is hydrogen. Preferably the substituents R⁸, R¹⁴ and R²⁰ are alkyl of up to 16 carbon atoms; alkyl of up to 16 carbon atoms substituted by alkoxy of up to 8 carbon atoms, or fluoro; phenyl which is unsubstituted or substituted by fluoro, alkoxy of up to 6 carbon atoms or alkyl of up to 6 carbon atoms; benzyl wherein the phenyl ring thereof is unsubstituted or substituted by fluor, alkoxy of up to 6 carbon atoms or alkyl of up to 6 carbon atoms; cyclohexyl; or oxacycloalkyl or 4 or 5 ring carbon atoms. A highly advantageous subembodiment relates to wettable, ophthalmic devices, preferably contact lenses, fabricated from a polymer of formula I wherein A is of the formula IV, wherein b, d, f, q, x, y, z, R⁸, R¹⁴ and R²⁰ are as defined above. There are two very highly advantageous embodiments having formula IV which are represented by either formula V wherein n is b + 1; m is d + 1, p is f + 1; n, m and p each independently being preferably 1-3, more preferably 1 or 2, most preferably 1; and x, y, z and q are as defined above; R⁸ and R²⁰ are hydrogen or one is, but preferably both are, an aliphatic, aromatic, or heterocyclic radical, preferably alkyl of up to 6 carbon atoms, alkyl of up to 6 carbon atoms substituted by alkoxy of up to 6 carbon atoms or fluoro; phenyl which is unsubstituted or substituted by fluoro, alkoxy of up to 6 carbon atoms or alkyl of up to 6 carbon atoms; benzyl wherein the phenyl ring thereof is unsubstituted or substituted by fluoro, alkoxy of up to 6 carbon atoms or alkyl of up to 6 carbon atoms; cyclohexyl or oxacycloalkyl of 4 or 5 ring carbon atoms; or which are represented by formula VI wherein n, m, p, x, y, z and q are as defined above for formula V and R¹⁴ is preferably selected from the same group as R⁸ in formula V. In the foregoing it is to be understood that the units of x, y and z may be positioned randomly, in block segments, or alternately. Another preferred embodiment corresponds to formulae IV, V and VI wherein z is zero. Desirably, the polymer segments of formula III or IV in the completed polymer are predominantly and preferably substantially devoid of free hydroxyl groups in the interior of the polymer as such groups tend to reduce oxygen permeability. Free hydroxy groups on the outer surfaces of the formed polymer are acceptable as they increase wettability without drawing water into the polymer matrix. However, it is still preferable to have as few free hydroxy groups in the finished polymer as practical if a contact lens having high oxygen permeability is to be prepared. This is balanced against the desirability of increased water content and therefore, for particular purposes, varying levels of internal hydroxy groups may be acceptable. A suitable means of tying up the excess undesired, free hydroxy groups present would be to interact them with a color group. Typical color groups useful in these embodiments include, but are not limited to, the hydroxy-reactive dyes known in the art under the tradename Remazol, manufactured by American Hoechst. Examples of the Remazol dyes which are especially useful are: all of which have at least one group of the formula _SO₂-CH₂CH₂O-SO₃ ⊖ which reacts with the polymer or monomer hydroxy group to yield a group, preferably the former. In such a manner, both excess free hydroxy groups are disposed of and colored contact lenses can be realized simultaneously. The color group or former can be reacted with monomer before the monomer is incorporated into the structure of formula I or afterwards. Another means of disposing of these excessive hydroxy groups is to utilize their presence to form various degrees and types of crosslinking. When polymers resulting from monomers of formula I polymerized or copolymerized in the absence of hydrophilic monomer, as defined below, have a water content greater than at least 10% they can be utilized as is. However, such non-hydrophilic modifying monomer containing polymers having a fully swollen water content of less than 10% are not suitable and must be modified by a hydrophilic modifier. Such compounds of formula I are modified by reacting them with or polymerizing them with a coreactive or copolymerizsable hydrophilic modifier. The hydrophilic modifier may be introduced by being coreactive with a functional group present in one or more of R, R³-R²¹ and/or with a functional group within L′ and/or L″. When the hydrophilic modifier is monofunctionally reactive (other than a vinylic unsaturation), it merely modifies the polymer properties and terminates a chain or sidechain at that point. When the hydrophilic modifier is di- or polyfunctionally reactive, i.e. contains more than one coreactive functional group or at least one coreactive vinylic group, the modifier can also act as a copolymerizable monomer and/or crosslinking agent. However, the hydrophilic modifier need not be the only crosslinking agent, nor need it be the only copolymerizable monomer present. When other such agents are employed any of the conventional crosslinking agents and coreactive monomers may be used in minor amounts. In any event, the polymer resulting from the polymerization of the monomer of formula I should not be crosslinked in excess of 25%, preferably not in excess of 20%, more preferably not in excess of 15%, still more preferably not in excess of 10%, even still more preferably not in excess of 5%, and most preferably in the range of 2-3%. The purpose of the hydrophilic modifier is to maintain the water content of the resulting polymer to at least 10% when swollen in its normal environment of use. For those polymers which absent the hydrophilic modifier already meet this limit, its purpose is to increase the water content of the polymer material over that when the hydrophilic modifier is absent. However, if the polymer, without the hydrophilic modifier, is sufficiently hydrophilic, i.e. the water content is at least 10%, it need not be present, but preferably is. Whether the hydrophilic modifier is needed or not, and the amount which is needed, is dependent upon the polymer water content and other hydrophilic properties desired. Preferably, the hydrophilic modifier is present, in accordance with the above in an amount of from zero to about 50% by weight, preferably about 1% to about 30%, more preferably about 5% to about 25%, still more preferably about 10% to about 15% of the resultant polymer. In addition to the hydrophilic modifier, other comonomers which may be present in the polymer are monomers coreactive with the monomer of formula I exclusive of monomers which are hydrophilic modifiers. Such additional monomers may be present in a minor amount of up to about 20% by weight of the resultant polymer. When such comonomers are excessively hydrophobic, additional hydrophilic modifier may be incorporated so as to achieve the appropriate water content. The hydrophilic modifier is a monomer which is coreactive with a monomer of formula I and is typically selected from aa) polyethylene glycols of the formula or ab) pyrrolidones of the formula wherein R²² is hydrogen or C₁-C₇ alkyl, preferably C₁-C₄ alkyl, g is an integer of from 1-25, or ac) a compound of the formula (R²⁴-div) nz Hy wherein R²³ is a polymerizable or reactive moiety selected from i) ethylenically unsaturated radicals, preferably vinyl, 1-methylvinyl, 2-methylvinyl, or allyl, ii) anhydrides, iii) amines, iv) acids, v) esters, vi) amides, vii) ethers, viii) acid halides, R²⁴ is selected from the meanings given for R²³ and ix) epoxy groups, especially glycidyl, x) isocyanates and isothiocyanates and xi) hydroxy; div is selected from ba) a divalent aliphatic group of up to 25 carbon atoms, preferably alkyl, alkenyl or alkynyl, which may also be interrupted, or terminated, or interrupted and terminated by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino, or carbonylamino; bb) a divalent 5-7 membered cycloaliphatic and 5-7 membered cycloaliphatic-C₁-C₂₀-aliphatic group which may also be interrupted, terminated, or interrupted and terminated as in group ba) above except that said interruptions cannot occur within said cycloaliphatic portions; bc) a divalent arylene group having 6-25 carbon atoms which is unsubstituted or substituted by at least one substituent selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhaloalkyl; bd) a divalent aralkyl or alkaryl or alkylene-aryl-alkylene having 7-25 carbon atoms which is uninterrupted or interrupted in the alkyl portion, or terminated, or interrupted in the alkyl portion and terminated with an interrupting or terminating group as mentioned in ba) above, and each of said uninterrupted, interrupted, and terminated aralkyl and alkaryl groups is further unsubstituted or substituted by a substituent selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhaloalkyl; wherein na is an integer of 8-100; and bea) R a is hydrogen, R b is methyl, nb is zero; or beb) R a is methyl, R b is hydrogen, and nb is zero; or bec) R a and R b are hydrogen and nb is one; even more preferably div is selected from nz is an integer of 1 up to the valence of Hy and where nz is less than the valence of Hy, the remaining valences of Hy are taken up with hydrogens; and Hy is a hydrophilic group selected from ca) morpholino; cyclic amide radicals of 5-7 ring members; saturated and unsaturated cyclic N,N-diamide radicals of 5-6 ring members; groups of the formula having 6-7 ring members wherein nc and nd are selected from 0-2; and cyclic amines of 5-6 ring members; each unsubstituted or substituted by hydroxy-C₁-C₅ alkyl, carboxy, or lower alkyl; cb) tetrahydrofurfuryl; cc) mono-, di-, and polysaccharide radicals, whether straight chain or cyclic, their corresponding sugar alcohol radicals, pentaerythritol radicals, and polyvinyl alcohol radicals; and cd) polyhydroxy C₂-C₇ alkyl radicals; and said reactive group R²³ or R²⁴ is capable of reacting with one or more sites in said formula I. Preferably the hydrophilic modifier has R²⁴ selected from and the terminus of div to which it is bound is _C(O)R²⁶, the carbonyl being bound to R²⁴, where R²⁵ is hydrogen or methyl and R²⁶ is _O_, or _NR²⁷_ with R²⁷ being hydrogen or lower alkyl; ib) H₂C=CH_ and the terminus of div to which it is bound is the left hand bond being bound to R²⁴, wherein R²⁸ is _O_, _NR²⁷_, _C(O)_, or _C(O)O_; and and the terminus of div to which it is bound is _C(O)R³⁰_, the carbonyl being bound to R²⁴ wherein R³⁰ is lower alkylene or _[CH₂CH(loweralkyl)-]O₁₋₅_ and R²⁹ is hydrogen, lower alkyl, or cyano; and has Hy selected from ce) morpholino which is unsubstituted or mono- up to tetra-substituted by lower alkyl, preferably methyl or ethyl; wherein ne is one, two, or three, preferably 1, each of which is unsubstituted or substituted, preferably mono- or disubstituted, by lower alkyl, preferably methyl or ethyl; where nf is 2 or 3, preferably 2, each of which is unsubstituted or substituted by lower alkyl, preferably methyl or ethyl; ch) a divalent group of the formula wherein R³¹ is hydrogen or carboxy; where ng is one or two, each of which is unsubstituted or substituted by lower alkyl, preferably methyl or ethyl; cl) a polyol selected from polyvinyl alcohol radicals, wherein xa is 2-10, preferably 3-4, and xb is an integer from zero, preferably at least 0.5 times xa up to xa + 1 inclusive, the cyclic saccharide analogs thereof, the di-tetra saccharides thereof, preferably having saccharide-saccharide links between the 1 and 4 carbon positions thereof, preferably β-linkages, C(CH₂O)₄(H) xc wherein xc is 0-3, and polyhydroxy lower alkylene glycol radicals wherein up to 50%, preferably up to 25%, more preferably up to 10%, of the hydroxy groups are missing their alcoholic hydrogens. Most preferably the hydrophilic modifier of formula (C) is selected from wherein R³² is in which yc is 1-6, preferably 3-4 and yb is 0 up to (yc + 1), preferably (yc - 1) to (yc + 1), more preferably yc to (yc + 1), ya is 1 up to (yc + 2 - yb), wherein R³³ is C(CH₂O)₄(H) 4-yd and yd is 1-4, preferably 1-2; ace) polyvinyl alcohol having at least one and up to 50% preferably 25%, more preferably 10%, inclusive, of the alcoholic hydrogens thereof absent; Preferably, when P′ is a vinyl containing group or one or more of the aforementioned R groups contain an ethylenically unsaturated group, for example preferably with one of R a and R b being methyl or hydrogen and the other being hydrogen, then the monomer of formula I can be crosslinked in the presence of a vinylic group containing hydrophilic modifier and/or vinylic group containing crosslinking agents. When P′ is with R a and R b as defined above or contains such a group then the monomer of formula I can be crosslinked in the presence or absence of up to less than about 50%, preferably up to about 30%, most preferably up to about 10% by weight of vinylically unsaturated hydrophilic modifiers and/or other vinylic comonomers. When P′ does not have a vinylic group, but takes in crosslinking, P′ contains e.g. an active hydrogen. In such cases, P′ preferably terminates in an OH, NHR c (R c being hydrogen or lower alkyl), a leaving group bound directly to the B or B′ carbonyl, a conventional acyl leaving group when not so bound, SCN_ or OCN_. Crosslinking is then typically carried out by condensation or addition with a di- or polyfunctional coreactive monomer which may or may not be a hydrophilic modifier. For example, when P′ is OH, then the coreactive monomer functional group can be _NHR c , _COOH, OCN_, SCN_, etc.; when P′ is NHR c , the reactive comonomer functional group can be a conventional acyl, or acyl bound to a conventional leaving group; and when P′ has OCN_ or SCN_, then the reactive comonomer functional group can be OH. Similarly, the other coreactive functional groups mentioned in terms of either P′ or the coreactive monomer can be interchanged (those mentioned as part of P′ being on the coreactive monomer and those mentioned as part of the coreactive monomer being part of P′). Suitable vinylic comonomers and coreactive monomers for condensation are set forth below. However, the list is not exhaustive and those of ordinary skill will appreciate the modifications, additions, and alternatives which may also be employed. When either or both L′ or L″ are hydrogen, or terminate in P′ with P′ being hydrogen, at least one additional crosslinkable moiety must be present as one of, or as substituent on one of, the groups R³-R²⁰. Such crosslinkable groups may also be present as a substituent on or in place of one or more of R³-R²⁰ even when one or both of L′ and L″ have crosslinkable groups therein. However, the degree of crosslinking in the finished crosslinked polymer should not exceed 20%, preferably not more than 10%, more preferably not more than 5% and should be still more preferably in the range of 1-4%, most preferably in the range of 2-3%. Within the polymer fabricated from monomers of formula I, not more than 20-70%, preferably not more than 50% of the A groups are polyethylene glycol. The number of A units and the chain length and nature of the substituents on the polyoxyethylene segment is determined by the degree of wettability desired in the polymer of the compound of formula I. In general, the polymer should be sufficiently hydrophilic in its surface properties such that the polymer exhibits a contact angle with distilled water at 20°C of less than 60°, preferably less than 40°, more preferably less than 25°, still more preferably less than 15°, most preferably less than 10°. The greater the number of siloxane units, the greater the number of oxyalkylene units is generally required to reduce the contact angle to within the above limits. As water is taken up, the oxygen permeability of the polymers tends to be reduced. However, with the water content and swellability increased due to hydrophilic modifier the drop in Dk over the low water content analogs is surprisingly less drastic than would otherwise be expected. Advantageously, the instant polymers absorb at least 10% by weight water, preferably 15-90% by weight, more preferably 20-85% by weight, still more preferably 25-75% by weigth, most preferably 35-55% by weight water. Highly preferred are those polymers which exhibit a contact angle of less than 25°, more preferably less than 15° and most preferably less than 10°. Preferred crosslinked polymers are those consisting essentially of a polymer of a divinylic monomer according to formula I wherein R¹ and R² are methyl, h and i are 2 to 4, v is 2-20; b, d and f are zero; R³, R⁴ are hydrogen; R⁸, R¹⁴ and R²⁰ are independently alkyl of up to 8 carbon atoms, (x + y + z) multiplied by q is 4-40 and P′ is: with R a being hydrogen or methyl. Very highly advantageous are those polymers of reactive vinylic monomers of the formula VII, one of e and k is one and the other zero; R a is hydrogen or methyl; each R is a divalent arylene group of 6 to 15 carbon atoms, a divalent C₆-C₁₀-arylene-amino carbonyloxy-C₂-C₆ alkylene; or divalent C₃-C₁₅ cycloaliphatic; L is BRB′, BR or RB′ and B and B′ are each each R⁷ is alkyl of 1 to 6 carbon atoms, or mixtures thereof with units wherein R⁷ is hydrogen, preferably with the proviso that R⁷ can be hydrogen in no more than about 75%, more preferably 50%, still more preferably no more than 30%, of the units; each x is 2-200, preferably 4-75, more preferably 6-70, most preferably 8-66; v is 2-300, preferably 2-75, more preferably 2-25, still more preferably 2-20, and most preferably at least 6; i and h are independently 2, 3 or 4; and a is an integer of 1-10, preferably 1-8, more preferably 1-6, still more preferably 1-4, most preferably 1-2. Within this very highly advantageous embodiment, R a is most preferably methyl; R is most preferably -phenylene-, _CH₂CH₂OCONH-phenylene- or _CH₂CH₂OCONH-tolylene-; R⁷ is methyl, x is most preferably 60 to 66; v is most preferably 15 to 20; a is most preferably 1 to 3; k is most preferably zero; and e is most preferably one. Within formula VII preferably k is zero, e is one, a is 1 to 3, Q is H₂C = C(R a ) _ wherein R a is hydrogen or methyl, L is _BR_ or _RB′_ wherein B and B′ is _CONH_ and R is phenylene, D is oxygen, W is a bond, R⁷ is methyl or hydrogen with the above proviso, x is 2 to 200, h and i are each 2 and v is 2 to 75. A very highly preferred embodiment are those polymers from monomers of formula VII wherein each group is of the formula wherein R³⁶ is alkyl of 1 to 4 carbon atoms, most preferably methyl, and s is from about 6 to about 200, preferably from about 25 to about 100, and most preferably from about 50 to about 75. Also highly preferred are those polymers of monomers of formula VII wherein each group is of the formula VIII wherein x′ is from about 2 to about 20, x″ is from about 8 to about 100, and x‴ from about 4 to about 80. Another valuable embodiment requires the value of x″ to be at least about twice that of x′ or x‴ and R³⁶ to be alkyl of 1 to 4 carbon atoms, preferably methyl. The reactive vinylic monomers of formula I can characteristically be polymerized to form crosslinked polymers under conventional polymerization conditions. If desired, the monomer reaction mixture may contain a catalytic amount of a conventional polymerization catalyst, preferably a free radical catalyst. Of particular interest are conventional peroxide and azo catalysts, such as hydrogen peroxide, benzoyl peroxide, tert-butyl peroctoate, benzoyl peroxide or azobis(isobutyronitrile). The polymerization can generally be carried out at temperatures between about 20° and about 150°C, for a period between about 1 and about 24 hours. It is understood that the time and temperature in such a reaction are inversely related. Thus, temperatures employed in the upper end of the temperature range will generally provide reaction times near the lower end of the time range. Preferably, the polymerization is conducted in the presence of actinic radiation, such as UV light. Depending upon the nature of the polymer mixture, it may be desirable for the polymers obtained from such polymerizations to be post cured, e.g. at a somewhat elevated temperature such as between about 60°C and about 150°C. For the preparation of contact lenses, the polymer mixture may be cast directly in the shape of the lens, or the polymerization may be carried out in a mold having a shape convenient for further processing, such as in the shape of small cyclinders or "buttons", which can then be machined. Minor amounts i.e. less than 50%, preferably up to 30%, and most preferably up to no more than about 10% by weight, of conventional copolymerizable vinyl monomers other than hydrophilic modifiers, can be employed as extenders or the like, in the preparation of the instant polymer, as copolymer constituents. However, if the total hydrophilic modifier content is within the foregoing limits, the hydrophilic modifiers can also be used as such extenders. Suitable vinyl monomers include: acrylates and methacrylates of the general formula where R³⁴ is hydrogen or methyl and R³⁵ is a straight chain or branched aliphatic, cycloaliphatic or aromatic group having up to 20 carbon atoms which is unsubstituted or substituted by one or more alkoxy, alkanoyloxy or alkyl of up to 12 carbon atoms, or by halo, especially chloro or preferably fluoro, or C₃-C₅ polyalkyleneoxy of 2 to about 100 units; acrylamides and methacrylamides of the general formula where R³⁴ and R³⁵ are as defined above; vinyl ethers of the formula H₂C=CH-O-R³⁵ where R³⁵ is as defined above; vinyl esters of the formula H₂C=CH-OOC-R³⁵ where R³⁵ is as defined above; maleates and fumarates of the formula R³⁵OOC-HC=CH-COOR³⁵ where R³⁵ is as defined above; and vinylic substituted hydrocarbons of the formula R³⁴CH=CHR³⁵ where R³⁴ and R³⁵ are as defined above. Useful monomers include, for example: methyl-, ethyl-, propyl-, isopropyl-, butyl-, ethoxyethyl-, methoxyethyl-, ethoxypropyl-, phenyl-, benzyl-, cyclohexyl-, hexafluoroisopropyl-, or n-octyl-acrylates and -methacrylates as well as the corresponding acrylamides and methacrylamides: dimethylfumarate, dimethylmaleate, diethylfumarate, methyl vinyl ether, ethoxyethyl vinyl ether, vinyl acetate, vinyl propionate, vinyl benzoate, acrylonitrile, styrene, alphamethyl styrene, 1-hexene, vinyl chloride, vinyl methyl ketone, vinyl stearate, 2-hexene and 2-ethylhexyl methacrylate. Most preferably, the instant polymers are free from copolymer units of such conventional vinyl monomers which are not hydrophilic modifiers. The vinylic monomers of formula I can be prepared by methods known, per se. For example, the siloxane/polyalkylene oxide containing divinylic monomers of formula I may be prepared by reacting a siloxane diol of the formula HO-(S′)-H, wherein _S′_ is a group of the formula II as defined hereinbefore with a sufficient amount of a difunctional reactive group containing compound having the group _X_ or _X-Y_, wherein the difunctional reactive groups are isocyanate; activated carboxy, such as an anhydride, an acid halide or a carboxy ester; or is a leaving group, such as a halide, sulfato or the like, to form the corresponding reactive group containing endcapped derivative. The resulting endcapped siloxane derivative can then be reacted with a polyoxyalkylene diol of the formula HO-(A)-H, wherein _A_ is a group of the formula III above to form the corresponding polyoxyalkylene-siloxane-polyoxyalkylene diol. This diol can then be reacted with a reactive group containing vinylic monomer having the terminal H₂C=C(R a )-L-moiety, wherein the reactive group is an isocyanate; activated carboxy, such as an anhydride, an acid halide or carboxy ester, or is a leaving group such as halo, sulfato or the like to form the corresponding divinyl derivative where a is 1. Alternatively, the aforementioned polyoxyalkylene _ siloxane _ polyoxyalkylene diols can be further sequentially reacted with a further difunctional reactive group containing compound having the group _BR_ or _BRB′-D_ to form the corresponding di-functional reactive endcapped derivative which is then reacted with a siloxane diol of the formula HO-(S′)-H. One may continue building up alternative polyoxyalkylene/siloxane unit containing diols in this manner, corresponding to the value of either "c(a plus e)" or c(a plus k)". Then this diol may be endcapped with a reactive group containing vinylic monomer having a terminal H₂C=C(R a )-L_ moiety or the diol reacted with a sufficient amount of difunctional reactive group containing compound to endcap the diol with a reactive group, such as eg. an isocyanate, etc. group which is then reacted with the appropriate vinylic containing compound, such as a vinylic amine or alcohol, or other copolymerizable monomer having a crosslinkable group to obtain the corresponding product of formula I. Of course, instead of starting with a siloxane diol of the formula HO-(S′)-H and building up the alternating sequence to the desired value of "a", one may instead begin with a polyoxyalkylene diol of the formula HO-(A)-H and, after endcapping the same with difunctional reactive groups, condense the same with the siloxane diol until the desired value of "e" is attained, and terminate the diol with vinylic groups as described above. The above reactive vinylic monomers are characteristically polymerized under conventional polymerization conditions with a hydrophilic modifier of formula C or a mixture of a hydrophilic modifier of formula C and a copolymerizable monomer. In those vinylic monomers containing but one vinyl group, a minor amount e.g. from about 0.01 to about 5 weight percent, based on the monomer of formula I, of a conventional crosslinking agent, may be employed. Suitable crosslinking agents include diolefinic monomers such as: Allyl acrylate and methacrylate, alkylene glycol and polyalkylene glycol diacrylates and dimethacrylates, such as ethyleneglycol dimethacrylate, diethylene glycol dimethacrylate, and propylene glycol dimethacrylate; trimethylol propane triacrylate; pentaerythritol tetraacrylate, divinylbenzene; divinyl ether; divinyl sulfone; bisphenol A diacrylate or dimethacrylate; methylene bisacrylamide; diallyl phthalate; triallyl melamine and hexamethylene diacrylate and dimethacrylate. Also, such minor amounts of a crosslinking agent may be employed, if desired, in the polymerization of the di-vinyl monomer of formula I and VII. When the monomers of formula I have free hydroxy, isocyanato, carboxylic or amine groups, suitable crosslinking agents contain di- or polyfunctional co-reactive groups to form addition or condensation reactions linking 2 or more chains. If desired, the monomer reaction mixture may contain a catalytic amount of a conventional catalyst, preferably a free radical catalyst. Of particular interest are conventional peroxide and azo catalysts, such as hydrogen peroxide, benzoyl peroxide, tert-butyl, peroctoate, benzoyl peroxide or azobis (isobutyronitrile). The aforementioned reactions are generally straight forward additions or condensations and are typically conducted at a reaction temperature between about -10°C and about 100°C, depending upon the relative reactivity of the species involved, in the presence or absence of an inert diluent and in the optional presence of an addition or condensation catalyst if desired or appropriate. For reactions involving an isocyanate or acid halide, with a diol, for example, suitable optional catalysts include pyridine and triethylamine. In a further subembodiment, the ophthalmic device, preferably contact lens, is fabricated from a polymer consisting essentially of an addition product of a monomer of formula I in which L′ and L″ are other than ethylenically unsaturated and a1) a monomer of formula F (E¹) t -G¹, wherein t is an integer of 2 to 4; G¹ is an aliphatic, aromatic, araliphatic, carbocyclic or heterocyclic residue having a valency corresponding to the value of t and containing up to about 24 carbon atoms, or, where t is 2, may also represent a divalent group of the formula wherein A, L and D are as defined above, w is a number from 0 to 8, Y¹ is a divalent aliphatic group of up to 14 carbon atoms which may be interrupted by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino or carbonyl; a divalent aliphatic hydrocarbylcarbonyl or -aminocarbonyl group of up to 14 carbon atoms and wherein the carbonyl group thereof is covalently bonded to the adjacent oxygen or _N(R²¹)_ moiety; a divalent 5 to 7-membered cycloaliphatic group of from 5 to 14 carbon atoms; a divalent arylene group of 6 to 14 carbon atoms; a divalent aralkyl or alkaryl group of 7 to 14 carbon atoms; a divalent 5 to 7-membered cycloaliphatic-carbonyl or -aminocarbonyl group of from 6 to 15 carbon atoms, wherein the carbonyl group thereof is covalently bonded to the adjacent oxygen or _N(R²¹)_ moiety; or a divalent arylene-, aralkyl- or alkaryl-carbonyl or -aminocarbonyl group wherein the arylene group is of 6 to 14 carbon atoms, the aralkyl or alkaryl group is of 7 to 14 carbon atoms, and the carbonyl group is covalently bonded to the adjacent oxygen or _N(R²¹)_ moiety; or Y¹ is a direct bond where E¹ is hydrogen; E¹ is hydrogen, hydroxy, amino, isocyanato or isothiocyanato and E¹ is coreactive with L′ or L″; or a2) a hydrophilic modifier of formula C wherein R²⁴ is coreactive with L′ or L″; or a3) a mixture of a compound of formula F and formula C. Advantageously, in order to insure adequate crosslinking, in one sub-embodiment there is employed at least a minor amount of those compounds wherein t is 3, for example at about 0.2% by weight based upon the amount of compound of formula I employed. Generally, a stoichiometrically equivalent amount of the compounds of formula I and F is combined; however, a slight excess of di- or polyisocyanate or -isothiocyanate may be employed to insure sufficient crosslinking to maintain dimensional stability in the product. As a further alternative, additional conventional crosslinking agents may be employed to insure sufficient crosslinking such that the product maintains dimensional stability. Thus, in addition to the compounds of formula I and F and C, there may also be added to the reaction mixture a minor amount, e.g. up to about 5 weight percent, of a conventional di-isocyanate or tri-isocyanate such as toluene di-isocyanate, isophorone di-isocyanate, 4,4′-methylenebis(phenyl isocyanate), methylenebis(cyclohexyl isocyanate), melamine tri-isocyanate, and the like. Alternatively, where a stoichiometric excess of isocyanate is employed in the reaction of C, I and F, a minor amount, e.g. up to about 5 weight percent, of a di- or polyfunctional amine or hydroxylated crosslinking agent may be employed. Suitably such crosslinking agents include, for example ethylene glycol, glycerin, diethylene glycol, ethylene diamine, ethanolamine, triethanolamine, diethanolamine and the like. The addition reaction between the compounds of formula C, I and formula F and any additional crosslinker can be conducted under conditions known, per se. Thus, the compounds may be simply admixed, in the presence of an inert diluent if necessary or desired, at a reaction temperature between about 0°C and about 100°C, preferably between about 20°C and 80°C, optionally in the presence of a condensation catalyst, such as triethyl amine or di-n-butyltin diacetate. In the preparation of opthalmic devices, such as contact lenses, the reaction mixture may be cast directly in the shape of the lens, or the polymerization may be carried out in a mold having a shape convenient for further processing, such as the shape of a small cylinder or "button", which can then be machined. The compounds of the formula C and F are either known or can be prepared by methods which are known, per se. The compounds of formula C are more fully described in concurrently filed U.S. patent application entitled HYDROPHILIC MODIFIER MONOMERS, invented by Frank Molock, Richard Robertson and Kai Su. The siloxane diols of the formula HO-(S′)-H are known in the art and many are commercially readily available. Also, the polyoxyalkylene diols of the formula HO-A-H are known or can be prepared by known methods. Thus, the polyols of the formula HO-A-H are generally prepared by the addition reaction of xq moles of an epoxide of the formula IX, where R³-R⁸, b, x, and q are as defined above, with yq moles of an epoxide of the formula X, where R⁹-R¹⁴, d, y, and q are as defined above, and zq moles of an epoxide of the formula XI, wherein R¹⁵-R²⁰, f, z, and q are as defined above, optionally in the presence of a conventional alkylation catalyst, at atmospheric to elevated pressures of up to about 3000 kPa gauge, at temperatures between 0°C and about 130°C, optionally in the presence of an inert diluent. If desired, one may add to the reaction mixture, prior to the reaction of the epoxides, an aliphatic, aromatic or cycloaliphatic alcohol, acid or amine having up to 14 carbon atoms to prepare the corresponding mono-ols terminating in the group D. The reaction between the epoxides, when mixtures of different epoxides are employed to obtain the polyol of the formula HO-A-H, can be conducted by admixing the epoxides to obtain random copolymers or terpolymers, etc., or the addition can be conducted sequentially to form block copolymers having terminal hydroxy groups. Suitable catalysts include alkaline earth oxides, alkaline earth carbonates, alkyl zinc compounds, aluminum alkoxides, hydrates of ferric chloride, bromide and acetate, and gamma radiation. The reaction may also be initiated by the presence of a glycol, such as ethylene glycol or propylene glycol or by a polyol of higher functionality such as sucrose, or by an amine, such as ethylene diamine, toluenediamine, and so forth. Generally the length of time of the reaction will depend in part on the alkylene oxide employed, but can generally be from less than one to several score hours. Thus, ethylene oxide generally is about three times as active as propylene oxide, which in turn reacts more rapidly than 1,2-butylene oxide. The preparation of polyoxetanes and polytetrahydrofurans is generally initiated via ring opening oxonium formation using trialkyloxonium salts, carboxonium salts, acylium salts and the like. Suitable diols of the formula HO-A-H include those prepared from epoxides such as: 1,2-propylene oxide; 1,2-butylene oxide; 1,2-epoxydecane; 1,2-epoxydodecane; 1,2-epoxyoctane; 2,3-epoxynorbornane; 1,2-epoxy-3-ethoxypropane; 1,2-epoxy-3-phenoxypropane; 2,3-epoxypropyl 4-methoxyphenyl ether; tetrahydrofuran; 1,2-epoxy-3-cyclohexyloxypropane; oxetane; 1,2-epoxy-5-hexene; 1,2-epoxyethylbenzene; 1,2-epoxy-1-methoxy-2-methylpropane; perfluorohexylethoxypropylene oxide; benzyloxypropylene oxide, and the like. Also, the aforementioned epoxides may be employed as mixtures thereof. Further, certain cyclic ethers of formula IX, X or XI where b or d or f, respectively is 3 and the carbocyclic portion of the ring is substituted are resistant to polymerization alone, but copolymerize quite readily with more reactive cyclic ethers. Suitable co-monomers include, for example, 2-methyl-tetrahydrofuran and 3-methyl-tetrahydrofuran. Also, while ethylene oxide may be employed as a co-monomer, ethylene oxide polymers, in the absence of more hydrophobic units, is characteristically too hydrophilic and absorbs too much aqueous fluid to be of use in accordance with the instant invention. However, ethylene oxide/propylene oxide copolymeric diols wherein there is 30-80%, preferably greater than 50%, more preferably greater than 66% propylene oxide, on a mole basis, is sufficiently hydrophobic so as to be substantially non-swellable in aqueous media, and yet sufficiently hydrophilic so as to exhibit a contact angle with water of less than 60°; preferably less than 40°, more preferably less than 25°, more preferably less than 15°, most preferably less than 10°. Many polymer diols of the formula HO-A-H are commercially available. Thus, suitable diol products include poloxamers having the general formula HO(CH₂CH₂O) a ′-(CH(CH₃)CH₂O) b ′-(CH₂CH₂O) c ′-H wherein b′ has a value between about 16 and 100 and the sum of a′ and c′ is between about 4 and about 100. Examples of such poloxamers, and their average values of a′, b′ and c′, include poloxamer 101 (a′ is 2, b′ is 16, c′ is 2); poloxamer 122 (a′ is 5, b′ is 21, c′ is 5); poloxamer 181 (a′ is 3, b′ is 30, c′ is 3); poloxamer 212 (a′ is 8, b′ is 35, c′ is 8); poloxamer 231 (a′ is 6, b′ is 39, c′ is 6); poloxamer 282 (a′ is 10, b′ is 47, c′ is 10); poloxamer 333 (a′ is 7, b′ is 54, c′ is 7); poloxamer 401 (a′ is 6, b′ is 67, c′ is 6). Such poloxamers are available, e.g. from BASF Wyandotte under their Pluronic® brand name. Also suitable are the "reverse poloxamers", having polyethylene glycol bounded on each side by polypropylene glycol. Polypropylene ether glycols include commercially available products having a molecular weight range between about 400 and about 4,000. As stated above, the polymers for use in the instant invention are those which exhibit a receding contact angle at 20°C of less than 60°, preferably less than 40°, more preferably less than 25°, more preferably less than 15° and most preferably less than 10°. The measurement of such contact angle is conveniently preformed using a modified "Wilhelmy Plate" technique, as described, for example, for J.D. Androde, et al. Surface and Interfacial Aspects of Biomedical Polymers , Vol. 1, Surface Chemistry and Physics , Plenum Press, 1985, wherein a specimen sample in the form of a plate of known dimensions is immersed into the wetting solution, pure water, at a slow controlled rate, e.g. at 2-20 mm per minute. As mentioned above, the instant polymers for use in the present invention possess a high degree of oxygen permeability. The oxygen permeability, Dk(× 10⁻¹⁰), is measured using a modification of ASTM standard D3985-81 in that (a) there is used 21% oxygen, i.e. air, instead of 99-100% oxygen, (b) the surface area of sample employed is 0.50 square meters versus 100 square meters and the humidity is controlled to be at 95-100% relative humidity instead of 0% relative humidity. The unit of Dk is (mm · ml O₂/cm² · sec · mmHg). Typically, conventional fully swollen polyhydroxyethyl methacrylate lenses which are sparingly crosslinked possess a Dk(× 10⁻¹⁰), (mm · ml O₂/cm² · sec · mmHg) value of about 5-7. The instant polymers for use as an opthalmic device, such as a contact lens, possess a Dk(× 10⁻¹⁰) value generally greater than 7-10, preferably greater than about 15, more preferably greater than about 20 and still more preferably greater than about 40, yet more preferably greater than 80, even more preferably greater than 100, most preferably at least 150. The following examples are for illustrative purposes and are not to be construed as limiting the invention. All parts are by weight unless otherwise specified. Examples 1-2: Hydrophilic Precursor Preparation Using the following procedure, Examples 1 and 2 are prepared with the components outlined in Table 1. To a 500 ml, 3-necked flask fitted with a constant pressure dropping funnel, condensor and nitrogen inlet and outlet adapters are charged all the styrene isocyanate, catalyst and 80% of methylene chloride. To the dropping funnel is added all the diol and 20 percent of the methylene chloride. The reaction system is sealed under nitrogen atmosphere, stirred magnetically and the contents of the dropping funnel added dropwise. After 18 hours the reaction is monitored via FT-infrared spectroscopy to insure that all the isocyanate band disappeared. Syntheses and analyses data for each example are shown in Tables I and II. Example 3: Silicone Block Copolymer Synthesis To a 250 ml, 3-necked flask equipped with a condensor, constant pressure dropping funnel and nitrogen inlet and outlet adapters are added 50.89 g (0.006 moles) styryl capped poly(propylene glycol) precursor and 0.27 ml Speier's catalyst. The mixture is stirred magnetically, heated to 60°C and 3.52 g (0.003 moles) of alpha,omega-dihydride-polydimethylsiloxane (having an average of about 16 silicon atoms) added dropwise via the dropping funnel under nitrogen atmosphere. After 24 hours, FT-infrared spectroscopy indicates the hydride band has disappeared. The reaction product is diluted with 100 ml methylene chloride, charged with sodium carbonate and carbon black, stirred 2 hours, filtered twice and the solvent removed via rotary evaporation. The product is clear, viscous fluid. Example 4: To 0.45 g of the silicone block copolymer prepared in example 3 is added one drop of 2-hydroxy-2-methyl-1-phenyl-propan-1-one (approximately 0.01 g). The formulation is stirred and protected from light at room temperature until the entrapped bubbles have escaped. The formulation is then transferred to polypropylene molds and UV cured for four hours. A translucent, flexible film is obtained with a water content of six percent. Examples 5-7: Formulations of the silicone block copolymer described in example 3 are prepared with various concentrations of n-vinyl pyrrolidone (NVP). One drop of 2-hydroxy-2-methyl-1-phenyl-propan-1-one, approximately 0.01 g, is added to each formulation as the initiator. The formulations are stirred and protected from light until the bubbles caused by stirring have escaped. The formulations are transferred to polypropylene molds and cured four hours in ultra-violet light. Each formulation composition and the water content of the cured materials are shown in Table III. The cured materials are clear when dry and remain clear when hydrated except example 7 which develops a slight haze in the hydrated state. Examples 8-10: Formulations of the silicone block copolymer described in example 3 are prepared with various concentrations of 2-hydroxyethyl methacrylate (HEMA). One drop of 2-hydroxy-2-methyl-1-phenyl-propan-1-one, approximately 0.01 g, is added to each formulation as the initiator. The formulations are stirred and protected from light until the bubbles caused by stirring have escaped. The formulations are transferred to polypropylene molds and cured four hours in ultra-violet light. Each formulation composition and the water content of the cured materials are shown in Table IV. The cured materials are clear in dry state and remain clear when hydrated. Example 11: Silicone Block Copolymer Synthesis To a 250 ml, 3-necked flask equipped with a condenser constant pressure dropping funnel and nitrogen inlet and outlet adapters are added 47.58 g of styryl capped poly(propylene glycol) precursor and 75 g methylene chloride. The mixture is stirred magnetically, and 3.68 g (0.013 moles) of alpha, omega-dihydride-polydimethylsiloxane (having an average of about 4 Si atoms) and 0.05 g of Speir's catalyst added dropwise via the dropping funnel under nitrogen atmosphere. After 92 hours FT-infrared spectroscopy indicates the silicone hydride band disappeared. The reaction product is charged with sodium carbonate and carbon black, stirred 2 hours, filtered twice and the solvent removed via rotary evaporation. The product is a clear, viscous fluid. Examples 12-15: Formulations of the silicone block copolymer described in example 11 are prepared with various concentrations of divinylbenzene (DVB) and n-vinyl pyrrolidone (NVP). One drop of 2-hydroxy-2-methyl-1-phenyl-propan-1-one, approximately 0.01 g, is added to each formulation as the initiator. The formulations are stirred and protected from light until the bubbles caused by stirring have escaped. The formulations are transferred to polypropylene molds and cured two hours in ultra-violet light. Each formulation composition and the water content of the cured materials are shown in Table V. The cured materials are clear in the dry and hydrated states. Examples 16-18: Formulations of the silicone block copolymer described in example 11 are prepared with various concentrations of 2-hydroxyethylmethacrylate (HEMA), ethylene glycol dimethacrylate (EGDMA) and n-vinyl pyrrolidone (NVP). One drop of 2-hydroxy-2-methyl-1-phenyl-propan-1-one, approximately 0.01 g, is added to each formulation as the initiator. The formulations are stirred and protected from light until the bubbles caused by stirring have escaped. The formulations are transferred to polypropylene molds and cured two hours in ultra-violet light. Each formulation composition and the water content of the cured materials are shown in Table VI. The cured materials are clear in dry and hydrated states. Example 19: Silicone Block Copolymer Synthesis To a 250 ml 3-necked flask equipped with a condensor, thermometer and nitrogen inlet and outlet adapters are added 150 ml toluene, 37.00 g (0.08 moles) of styryl terminated tripropylene glycol, 21.06 g (0.04 moles) of alpha-omega-dihydride-polydimethylsiloxane (having an average of about 7 silicon atoms) and 0.21 g of Speier's catalyst. The reaction mixture is heated to 50°C. After five days, the reaction is cooled to ambient temperature, neutralized and decolorized with sodium carbonate and carbon black, filtered and the solvent removed via rotary evaporation. The product is a clear, viscous fluid. Examples 20-28: Formulations of the silicone block copolymer described in example 19 are prepared with various concentrations of ethylene glycol dimethylacrylate (EGDMA), 2-hydroxyethyl methacrylate (HEMA) and styryl terminated poly(ethylene glycol 4000) (STPEG). One drop of 2-hydroxy-2-methyl-1-phenyl-propan-1-one, approximately 0.01 g, is added to each formulation as the initiator. The formulations are stirred and protected from light until the bubbles caused by stirring have escaped. The formulations are transferred to polypropylene molds and cured 2 hours in ultra-violet light. Each formulation composition and the water content of the cured materials are shown in Table VII. The cured materials are clear.

Claims: Claims for the following Contracting States: AT, BE, CH, DE, FR, GB, GR, IT, LI, LU, NL, SE 1. An optically clear wettable, flexible, oxygen permeable ophthalmic device fabricated from a polymer of a) a crosslinkable monomer having a segment S″ of the formula Ia, wherein a is 1 to 10; each D is independently oxygen or _N(R²¹)_; each W is a bond, oxygen or _N(R²¹)_; each L is independently _BRB′_, _BR_, _RB′_ or _R_; each S′ is independently a segment of formula II, each A is independently a segment of formula III, the terminal oxygen within each unit of formula III being replaceable by _N(R²¹)_; wherein each b, d and f is independently 0-4; q is a number from 1 to 1000; each x, y and z is independently 0 to 200, provided at least one of x, y and z is at least 1; such that (x + y + z) multiplied by q is 4 to 1000; each h and i is an integer from 1 to 6, v is an integer from 2 to 300; R¹ and R² are independently alkyl of up to 18 carbon atoms, or aryl of up to 12 carbon atoms; each of R³, R⁴, R⁷-R¹⁰, R¹³-R¹⁶, R¹⁹ and R²⁰ is independently selected from the group consisting of hydrogen, halogen, an aliphatic, aromatic or heterocyclic containing radical selected from unsubstituted C₁-C₁₆ alkyl; substituted C₁-C₁₆ alkyl; unsubstituted C₂-C₁₆ alkenyl; and substituted C₂-C₁₆ alkenyl; wherein the alkyl and alkenyl substituents are independently selected from C₁-C₁₆ alkoxycarbonyl, C₂-C₁₆ alkenyloxycarbonyl, fluoro, aryl of up to 10 carbon atoms, C₁-C₁₆ alkoxy, C₁-C₁₆ alkanoyloxy, aryloxy of up to 10 carbon atoms, C₃-C₆ alkenoyloxy, aroyl of up to 10 carbon atoms, aroyloxy of up to 11 carbon atoms, C₃-C₈ cycloalkyl, C₃-C₈ cycloalkoxy, C₃-C₈ cycloalkyl-carbonyloxy, C₃-C₈ cycloalkoxy-carbonyl, oxacycloalkyl of up to 7 carbon atoms, oxacycloalkoxy of up to 7 carbon atoms, oxacycloalkoxy (up to 7 carbon atoms)-carbony, oxacycloalkyl (up to 7 carbon atoms)-carbonyloxy, and aryl (of up to 10 carbon atoms)-oxycarbonyl, each of said alkyl and alkenyl substituents being, in turn, optionally substituted by C₁-C₆ alkyl, fluoro or a C₁-C₆ alkoxy provided said last mentioned alkoxy is not bound to a carbon atom already singly bound to another oxygen atom; R³, R⁴, R⁷-R¹⁰, R¹³-R¹⁶, R¹⁹ and R²⁰ being further independently selected from aryl of up to 10 carbon atoms, C₃-C₈ cycloalkyl, and oxacycloalkyl of up to 7 carbon atoms, each of which may be unsubstituted or further substituted with a substituent selected from the group of substituents for said R³ alkyl set forth above; R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are selected from the same group set forth above for R³; and R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are further independently selected from C₁-C₁₆ alkoxycarbonyl, C₃-C₁₆ alkenoyloxy, C₂-C₁₆ alkenyloxycarbonyl, and C₁-C₁₆ alkanoyloxy, each of which may be further substituted by fluoro, aryl of up to 10 carbon atoms, or C₁-C₁₆ alkoxy, and R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are still further independently selected from aryloxy of up to 10 carbon atoms, cycloalkoxy of up to 8 carbon atoms, cycloalkyl (of up to 8 carbon atoms)-carbonyloxy, cycloalkoxy (of up to 8 carbon atoms)-carbonyl, aroyloxy of up to 11 carbon atoms, oxacycloalkoxy of up to 7 carbon atoms, oxacycloalkenyloxy of up to 7 carbon atoms, oxacycloalkoxy (of up to 7 carbon atoms)-carbonyl, oxacycloalkyl (of up to 7 carbon atoms)-carbonyloxy, and aryloxy (of up to 10 carbon atoms)-carbonyl, each of which may be further substituted by fluoro, C₁-C₆ alkyl or C₁-C₆ alkoxy, provided that any substituent having a singly bound oxygen atom as its link to the rest of the molecule may not be a substituent on the same carbon atom which is singly bonded to another oxygen atom; or 2 adjacent groups, selected from R³-R²⁰, together with the atoms to which they are attached may form a 5-8 membered cycloalkyl, oxacycloalkyl or bicycloalkyl ring. each R²¹ is independently selected from hydrogen, C₁-C₄ alkyl and phenyl, each B and B′ is selected from with the carbonyl group being bound to A, S′, or D; and each R is independently a divalent linking group selected from a) a divalent aliphatic group of up to 25 carbon atoms which may be interrupted by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino, or carbonylamino; b) a divalent 5-7 membered cycloaliphatic and 5-7 membered cycloaliphatic-C₁-C₂₀-aliphatic group; c) a divalent arylene group having 6-25 atoms; d) a divalent aralkyl or alkaryl group having 7 to 25 carbon atoms; and e) a divalent alkylene-aryl-alkylene having 8 to 30 carbon atoms, wherein groups b), d) and e) can be optionally interrupted in their non-cyclic aliphatic and alkyl groups respectively by the same groups as in group a) and wherein the aryl rings in groups c), d) and e) may be further substituted with one or more substituents selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhalo alkyl, and wherein an interrupting group set forth in group a) may be present between the cyclic and non-cyclic portions of groups b), d) and e); and b) from zero up to a sufficient amount of a hydrophilic modifying monomer to impart to said polymer a water content in its aqueous swollen state of at least 10%, said hydrophilic modifying monomer being selected from aa) polyethylene glycols of the formula or ab) pyrrolidones of the formula wherein R²² is hydrogen or C₁-C₇ alkyl, g is an integer of from 1-25, or ac) a compound of the formula (R²⁴-div) nz Hy wherein R²³ is a polymerizable or reactive moiety selected from i) ethylenically unsaturated radicals, ii) anhydrides, iii) amines, iv) acids, v) esters, vi) amides, vii) ethers, viii) acid halides, R²⁴ is selected from the meanings given for R²³ and ix) epoxy groups, x) isocyanates and isothiocyanates and xi) hydroxy; div is selected from ba) a divalent aliphatic group of up to 25 carbon atoms, preferably alkyl, alkenyl or alkynyl, which may also be interrupted, or terminated, or interrupted and terminated by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino, or carbonylamino; bb) a divalent 5-7 membered cycloaliphatic and 5-7 membered cycloaliphatic-C₁-C₂₀-aliphatic group which may also be interrupted, terminated, or interrupted and terminated as in group ba) above except that said interruptions cannot occur within said cycloaliphatic portions; bc) a divalent arylene group having 6-25 carbon atoms which is unsubstituted or substituted by at least one substituent selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhaloalkyl; bd) a divalent aralkyl or alkaryl or alkylene-aryl-alkylene having 7-25 carbon atoms which is uninterrupted or interrupted in the alkyl portion, or terminated, or interrupted in the alkyl portion and terminated with an interrupting or terminating group as mentioned in ba) above, and each of said uninterrupted, interrupted, and terminated aralkyl and alkaryl groups is further unsubstituted or substituted by a substituent selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhaloalkyl; wherein na is an integer of 8-100; and bea) R a is hydrogen, R b is methyl, and nb is zero; or beb) R a is methyl, R b is hydrogen, and nb is zero; or bec) R a and R b are hydrogen and nb is one; nz is an integer of 1 up to the valence of Hy and where nz is less than the valence of Hy, the remaining valences of Hy are taken up with hydrogens; and Hy is a hydrophilic group selected from ca) morpholino; cyclic amide radicals of 5-7 ring members; saturated and unsaturated cyclic N,N-diamide radicals of 5-6 ring members; groups of the formula having 6-7 ring members wherein nc and nd are selected from 0-2; and cyclic amines of 5-6 ring members; each unsubstituted or substituted by hydroxy-C₁-C₅ alkyl, carboxy, or lower alkyl; cb) tetrahydrofurfuryl; cc) mono-, di-, and polysaccharide radicals, whether straight chain or cyclic, their corresponding sugar alcohol radicals, pentaerythritol radicals, and polyvinyl alcohol radicals; and cd) polyhydroxy C₂-C₇ alkyl radicals; and said device having a receding contact angle of less than 60°; and having a Dk (× 10 ⁻¹⁰ mm · ml O₂/cm² · sec · mmHg) of at least about 7. 2. The device of claim 1 wherein a is one and each D is oxygen. 3. The device of claim 1 wherein each L is _BRB′_, _BR_ or _RB′, each B is _C(O)NH_ wherein the nitrogen atom is bound to R, and R is phenylene unsubstituted or substituted by methyl. 4. The device of claim 1 wherein each R¹ and R² is methyl, h is 4; i is 4; and v is from about 15 to about 50. 5. The device of claim 1 wherein (x + y + z) times q is from about 25 to about 75. 6. The device of claim 1 wherein a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen or b) each b, d and f is zero, each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶, and R²⁰ is hydrogen, and each R⁷, R¹³, and R¹⁹ is methyl. 7. The device of claim 6 wherein (x + y + z) times q is about 25 to about 75. 8. The device of claim 1 wherein a is 1; each D is oxygen; each L is _BRB′_, _BR_ or _RB′_; each B and B′ are _C(O)NH_ with the nitrogen atom bound to R; each R is phenylene unsubstituted or substituted by methyl; each R¹ and R² is methyl; h and i are each 4; v is from about 15 to about 50; (x + y + z) times q is about 25 to about 75; and a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen; or b) each b, d and f is zero; each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶ and R²⁰ is hydrogen; and each R⁷, R¹³, and R¹⁹ is methyl. 9. The device of claim 8 wherein each W is a bond and each L is _BR_ or _RB′_. 10. The wettable, flexible, oxygen permeable, ophthalmic device of claim 1, the crosslinkable monomer a) having segments of formula Ib, or of formula Ic, or of formula Id wherein each S″ is independently a segment of formula Ia of claim 1; each D, A and L is independently as defined in claim 1; c is 1-10; and a times c is 1-10; La being selected from _BRB′_ and _BR_; and wherein S′, B, R and B′ are as defined in claim 1. 11. The device of claim 10 wherein a is one and each D is oxygen. 12. The device of claim 10 wherein each L is _BRB′_, _BR_ or _RB′_, each B is _C(O)NH_ wherein the nitrogen atom is bound to R, and R is phenylene unsubstituted or substituted by methyl. 13. The device of claim 10 wherein each R¹ and R² is methyl; h is 4; i is 4; and v is from about 15 to about 50. 14. The device of claim 10 wherein (x + y + z) times q is from about 25 to about 75. 15. The device of claim 10 wherein a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen or b) each b, d and f is zero, each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶, and R²⁰ is hydrogen, and each R⁷, R¹³, and R¹⁹ is methyl. 16. The device of claim 15 wherein (x + y + z) times q is about 25 to about 75. 17. The device of claim 10 wherein c is 1. 18. The device of claim 10 wherein a is 1; each D is oxygen; each L is _BRB′_, _BR_ or _RB′_; each B and B′ are _C(O)NH_ with the nitrogen atom bound to R; each R is phenylene unsubstituted or substituted by methyl; each R¹ and R² is methyl; h and i are each 4; v is from about 15 to about 50; (x + y + z) times q is about 25 to about 75; and a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen; or b) each b, d and f is zero; each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶ and R²⁰ is hydrogen; and each R⁷, R¹³, and R¹⁹ is methyl; and c is one. 19. The device of claim 18 wherein each W is a bond and each L is _BR_ or _RB′_. 20. The wettable, flexible, oxygen permeable ophthalmic device of claim 14 the monomer a having the formula wherein e is zero or 1; each D, A, L, S″, and c is independently as defined in claim 10; L′ is hydrogen, P′-R_, P′-BR_, P′-RB′_, or P′-BRB′_; and L″ is hydrogen, or _P′, or, in case that e is zero, also _D-S′-BR-P′ or _D-S′-BRB′-P′ and wherein P′ is hydrogen, amino, hydroxy, NCO, NCS, vinyl or a moiety containing a crosslinkable group which may be crosslinked when coreacted with a suitable crosslinking agent or when irradiated by actinic radiation. 21. The device of claim 20 wherein a is one and each D is oxygen. 22. The device of claim 20 wherein each L is _BRB′_, _BR_ or _RB′_, each B is _C(O)NH_ wherein the nitrogen atom is bound to R, and R is phenylene unsubstituted or substituted by methyl. 23. The device of claim 20 wherein each R¹ and R² is methyl, h is 4; i is 4; and v is from about 15 to about 50. 24. The device of claim 20 wherein (x + y + z) times q is from about 25 to about 75. 25. The device of claim 20 wherein a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen or b) each b, d and f is zero, each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶, and R²⁰ is hydrogen, and each R⁷, R¹³, and R¹⁹ is methyl. 26. The device of claim 25 wherein (x + y + z) times q is about 25 to about 75. 27. The device of claim 20 wherein c is 1. 28. The device of claim 20 wherein L′ is P′-BRB′_. 29. The device of claim 20 wherein each P′ is 30. The device of claim 20 wherein a is 1; each D is oxygen; each L is _BRB′_, _BR_ or _RB′_; each B and B′ are _C(O)NH_ with the nitrogen atom bound to R; each R is phenylene unsubstituted or substituted by methyl; each R¹ and R² is methyl; h and i are each 4; v is from about 15 to about 50; (x + y + z) times q is about 25 to about 75; and a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen; or b) each b, d and f is zero; each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶ and R²⁰ is hydrogen; and each R⁷, R¹³, and R¹⁹ is methyl; L′ is P′-BRB′ or P′; and P′ is 31. The device of claim 30 wherein each W is a bond, each L is _BR_ or _RB′_ and L′ and L″ are each _CH=CH₂. 32. The device of claim 1 which is a contact lens. 33. The device of claim 1 wherein each A is of the formula wherein each of x, y, z, and q are greater than zero. 34. The device of claim 33 wherein q is one. 35. The device of claim 33 wherein x and z within any one A are the same. 36. The device of claim 33 wherein each x and each z has the same value. 37. An optically clear wettable, flexible, oxygen permeable polymer of a) a crosslinkable monomer having a segment S″ of the formula wherein each of the variables is as defined in claim 1, and b) a sufficient amount of a hydrophilic modifying monomer to impart to said polymer a water content in its aqueous swollen state of at least 10%, said hydrophilic modifying monomer being selected from the compounds of formula (A), (B) and (C) as defined in claim 1; and said polymer having a receding contact angle of less than 60°; and having a Dk (× 10 ⁻¹⁰ mm · ml O₂/cm² · sec · mmHg) of at least about 7. 38. The wettable, flexible, oxygen permeable, polymer of claim 37 the crosslinkable monomer a) having segments of formula Ib, or of formula Ic, or of formula Id wherein each S″ is independently a segment of formula Ia of claim 1; each D, A and L is independently as defined in claim 1; c is 1-10; and a times c is 1-10; La being selected from _BRB′_ and _BR_; and wherein S′, B, R and B′ are as defined in claim 1. 39. The wettable, flexible, oxygen permeable, polymer of claim 38 the monomer a) having the formula wherein e is zero or 1; each D, A, L, S″, and c is independently as defined in claim 10; L′ is hydrogen, P′-R_, P′-BR_, P′-RB′_, or P′-BRB′_; and L″ is hydrogen, or _P′, or, in case that e is zero, also _D-S′-BR-P′ or _D-S′-BRB′-P′ and wherein P′ is hydrogen, amino, hydroxy, NCO, NCS, vinyl or a moiety containing a crosslinkable group which may be crosslinked when coreacted with a suitable crosslinking agent or when irradiated by actinic radiation. 40. The device of claim 1 wherein said hydrophilic modifying monomer is selected from the group of the formula (R²⁴-div) nz Hy 41. The polymer of claim 37 wherein said hydrophilic modifying monomer is selected from the group of the formula (R²⁴-div) nz Hy 42. The polymer of claim 41 wherein R²⁴ is an ethylenically unsaturated group. 43. The polymer of claim 42 wherein R²⁴ is vinyl, 1-methylvinyl, 2-methylvinyl or allyl; and the terminus of div to which it is bound is _C(O)R²⁶, the carbonyl being bound to R²⁴, where R²⁵ is hydrogen or methyl and R²⁶ is _O_, or _NR²⁷_ with R²⁷ being hydrogen or lower alkyl; ib) H₂C=CH_ and the terminus of div to which it is bound is the left hand bond being bound to R²⁴, wherein R²⁸ is _O_, _NR²⁷_, _C(O)_, or _C(O)O_; and and the terminus of div to which it is bound is _C(O)R³⁰_, the carbonyl being bound to R²⁴ wherein R³⁰ is lower alkylene or _[CH₂CH(loweralkyl)-O]₁₋₅_ and R²⁹ is hydrogen, lower alkyl, or cyano. 44. The polymer of claim 41 wherein Hy is ce) morpholino which is unsubstituted or mono- up to tetra-substituted by lower alkyl; wherein ne is one, two, or three, each of which is unsubstituted or substituted, by lower alkyl; where nf is 2 or 3, each of which is unsubstituted or substituted by lower alkyl; ch) a divalent group of the formula wherein R³¹ is hydrogen or carboxy; where ng is one or two, each of which is unsubstituted or substituted by lower alkyl; cl) a polyol selected from polyvinyl alcohol radicals, wherein xa is 2-10 and xb is an integer from zero up to xa + 1 inclusive, the cyclic saccharide analogs thereof, the di-tetra saccharides thereof, C(CH₂O)₄(H) xc wherein xc is 0-3, and polyhydroxy lower alkylene glycol radicals wherein up to 50%, of the hydroxy groups are missing their alcoholic hydrogens. 45. The polymer of claim 41 wherein div is selected from 46. The polymer of claim 41 wherein said hydrophilic modifying monomer is selected from wherein R³² is in which yc is 1-6, and yb is 0 up to (yc + 1), and ya is 1 up to (yc + 2 - yb), wherein R³³ is C(CH₂O)₄(H) 4-yd and yd is 1-4; ace) polyvinyl alcohol having at least one and up to 50% inclusive, of the alcoholic hydrogens thereof absent; and 47. The polymer of claim 46 wherein said hydrophilic modifying monomer is selected from said groups aca), acb) and acf). 48. Use of a polymer of claim 37 or 39 for the manufacture of an ophthalmic device. Claims for the Contracting State: ES 1. An optically clear wettable, flexible, oxygen permeable ophthalmic device fabricated from a polymer of a) a crosslinkable monomer having a segment S″ of the formula Ia, wherein a is 1 to 10; each D is independently oxygen or _N(R²¹)_; each W is a bond, oxygen or _NR²¹)_; each L is independently _BRB′_, _BR_, _RB′_ or _R_; each S′ is independently a segment of formula II, each A is independently a segment of formula III, the terminal oxygen within each unit of formula III being replaceable by _N(R²¹)_; wherein each b, d and f is independently 0-4; q is a number from 1 to 1000; each x, y and z is independently 0 to 200, provided at least one of x, y and z is at least 1; such that (x + y + z) multiplied by q is 4 to 1000; each h and i is an integer from 1 to 6, v is an integer from 2 to 300; R¹ and R² are independently alkyl of up to 18 carbon atoms, or aryl of up to 12 carbon atoms; each of R³, R⁴, R⁷-R¹⁰, R¹³-R¹⁶, R¹⁹ and R²⁰ is independently selected from the group consisting of hydrogen, halogen, an aliphatic, aromatic or heterocyclic containing radical selected from unsubstituted C₁-C₁₆ alkyl; substituted C₁-C₁₆ alkyl; unsubstituted C₂-C₁₆ alkenyl; and substituted C₂-C₁₆ alkenyl; wherein the alkyl and alkenyl substituents are independently selected from C₁-C₁₆ alkoxycarbonyl, C₂-C₁₆ alkenyloxycarbonyl, fluoro, aryl of up to 10 carbon atoms, C₁-C₁₆ alkoxy, C₁-C₁₆ alkanoyloxy, aryloxy of up to 10 carbon atoms, C₃-C₆ alkenoyloxy, aroyl of up to 10 carbon atoms, aroyloxy of up to 11 carbon atoms, C₃-C₈ cycloalkyl, C₃-C₈ cycloalkoxy, C₃-C₈ cycloalkyl-carbonyloxy, C₃-C₈cycloalkoxy-carbonyl, oxacycloalkyl of up to 7 carbon atoms, oxacycloalkoxy of up to 7 carbon atoms, oxacycloalkoxy (up to 7 carbon atoms)-carbonyl, oxacycloalkyl (up to carbon atoms)-carbonyloxy, an aryl (of up to 10 carbon atoms)-oxycarbonyl, each of said alkyl and alkenyl substituents being, in turn, optionally substituted by C₁-C₆ alkyl, fluoro or a C₁-C₆ alkoxy provided said last mentioned alxoxy is not bound to a carbon atom already singly bound to another oxygen atom; R³, R⁴, R⁷-R¹⁰, R¹³-R¹⁶, R¹⁹ and R²⁰ being further independently selected from aryl of up to 10 carbon atoms, C₃-C₈ cycloalkyl, and oxacycloalkyl of up to 7 carbon atoms, each of which may be unsubstituted or further substituted with a substituent selected from the group of substituents for said R³ alkyl set forth above; R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are selected from the same group set forth above for R³; and R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are further independently selected from C₁-C₁₆ alkoxycarbonyl, C₃-C₁₆ alkenoyloxy, C₂-C₁₆ alkenyloxycarbonyl, and C₁-C₁₆ alkanoyloxy, each of which may be further substituted by fluoro, aryl of up to 10 carbon atoms, or C₁-C₁₆ alkoxy, and R⁵, R⁶, R¹¹, R¹², R¹⁷ and R¹⁸ are still further independently selected from aryloxy of up to 10 carbon atoms, cycloalkoxy of up to 8 carbon atoms, cycloalkyl (of up to 8 carbon atoms)-carbonyloxy, cycloalkoxy (of up to 8 carbon atoms)-carbonyl, aroyloxy of up to 11 carbon atoms, oxacycloalkoxy of up to 7 carbon atoms, oxacycloalkenyloxy of up to 7 carbon atoms, oxacycloalkoxy (of up to 7 carbon atoms)-carbonyl, oxacycloalkyl (of up to 7 carbon atoms)-carbonyloxy, and aryloxy (of up to 10 carbon atoms)-carbonyl, each of which may be further substituted by fluoro, C₁-C₆ alkyl or C₁-C₆ alkoxy, provided that any substituent having a singly bound oxygen atom as its link to the rest of the molecule may not be a substituent on the same carbon atom which is singly bonded to another oxygen atom; or 2 adjacent groups, selected from R³-R²⁰, together with the atoms to which they are attached may form a 5-8 membered cycloalkyl, oxacycloalkyl or bicycloalkyl ring. each R²¹ is independently selected from hydrogen, C₁-C₄ alkyl and phenyl, each B and B′ is selected from with the carbonyl group being bound to A, S′, or D; and each R is independently a divalent linking group selected from a) a divalent aliphatic group of up to 25 carbon atoms which may be interrupted by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino, or carbonylamino; b) a divalent 5-7 membered cycloaliphatic and 5-7 membered cycloaliphatic-C₁-C₂₀-aliphatic group; c) a divalent arylene group having 6-25 atoms; d) a divalent aralkyl or alkaryl group having 7 to 25 carbon atoms; and e) a divalent alkylene-aryl-alkylene having 8 to 30 carbon atoms, wherein groups b), d) and e) can be optionally interrupted in their non-cyclic aliphatic and alkyl groups respectively by the same groups as in group a) and wherein the aryl rings in groups c), d) and e) may be further substituted with one or more substituents selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhalo alkyl, and wherein an interrupting group set forth in group a) may be present between the cyclic and non-cyclic portions of groups b), d) and e); and b) from zero up to a sufficient amount of a hydrophilic modifying monomer to impart to said polymer a water content in its aqueous swollen state of at least 10%, said hydrophilic modifying monomer being selected from aa) polyethylene glycols of the formula or ab) pyrrolidones of the formula wherein R²² is hydrogen or C₁-C₇ alkyl, g is an integer of from 1-25, or ac) a compound of the formula (R²⁴-div) nz Hy wherein R²³ is a polymerizable or reactive moiety selected from i) ethylenically unsaturated radicals, ii) anhydrides, iii) amines, iv) acids, v) esters, vi) amides, vii) ethers, viii) acid halides, R²⁴ is selected from the meanings given for R²³ and ix) epoxy groups, x) isocyanates and isothiocyanates and xi) hydroxy; div is selected from ba) a divalent aliphatic group of up to 25 carbon atoms, preferably alkyl, alkenyl or alkynyl, which may also be interrupted, or terminated, or interrupted and terminated by oxy, carbonyloxy, amino, aminocarbonyl, oxycarbonyl, ureido, oxycarbonylamino, or carbonylamino; bb) a divalent 5-7 membered cycloaliphatic and 5-7 membered cycloaliphatic-C₁-C₂₀-aliphatic group which may also be interrupted, terminated, or interrupted and terminated as in group ba) above except that said interruptions cannot occur within said cycloaliphatic portions; bc) a divalent arylene group having 6-25 carbon atoms which is unsubstituted or substituted by at least one substituent selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhaloalkyl; bd) a divalent aralkyl or alkaryl or alkylene-aryl-alkylene having 7-25 carbon atoms which is uninterrupted or interrupted in the alkyl portion, or terminated, or interrupted in the alkyl portion and terminated with an interrupting or terminating group as mentioned in ba) above, and each of said uninterrupted, interrupted, and terminated aralkyl and alkaryl groups is further unsubstituted or substituted by a substituent selected from halogen, C₁-C₄ alkyl, and C₁-C₁₂ perhaloalkyl; wherein na is an integer of 8-100; and bea) R a is hydrogen, R b is methyl, and nb is zero; or beb) R a is methyl, R b is hydrogen, and nb is zero; or bec) R a and R b are hydrogen and nb is one; nz is an integer of 1 up to the valence of Hy and where nz is less than the valence of Hy, the remaining valences of Hy are taken up with hydrogens; and Hy is a hydrophilic group selected from ca) morpholino; cyclyc amide radicals of 5-7 ring members; saturated and unsaturated cyclic N,N-diamide radicals of 5-6 ring members; groups of the formula having 6-7 ring members wherein nc and nd are selected from 0-2; and cyclic amines of 5-6 ring members; each unsubstituted or substituted by hydroxy-C₁-C₅ alkyl, carboxy, or lower alkyl; cb) tetrahydrofurfuryl; cc) mono-, di-, and polysaccharide radicals, whether straight chain or cyclic, their corresponding sugar alcohol radicals, pentaerythritol radicals, and polyvinyl alcohol radicals; and cd) polyhydroxy C₂-C₇ alkyl radicals; and said device having a receding contact angle of less than 60°; and having a Dk (× 10⁻¹⁰ mm · ml O₂/cm² · sec · mmHg) of at least about 7. 2. The device of claim 1 wherein a is one and each D is oxygen. 3. The device of claim 1 wherein each L is _BRB′_, _BR_ or _RB′, each B is _C(O)NH_ wherein the nitrogen atom is bound to R, and R is phenylene unsubstituted or substituted by methyl. 4. The device of claim 1 wherein each R¹ and R² is methyl, h is 4; i is 4; and v is from about 15 to about 50. 5. The device of claim 1 wherein (x + y + z) times q is from about 25 to about 75. 6. The device of claim 1 wherein a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen or b) each b, d and f is zero, each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶, and R²⁰ is hydrogen, and each R⁷, R¹³, and R¹⁹ is methyl. 7. The device of claim 6 wherein (x + y + z) times q is about 25 to about 75. 8. The device of claim 1 wherein a is 1; each D is oxygen; each L is _BRB′_, _BR_ or _RB′_; each B and B′ are _C(O)NH_ with the nitrogen atom bound to R; each R is phenylene unsubstituted or substituted by methyl; each R¹ and R² is methyl; h and i are each 4; v is from about 15 to about 50; (x + y + z) times q is about 25 to about 75; and a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen; or b) each b, d and f is zero; each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶ and R²⁰ is hydrogen; and each R⁷, R¹³, and R¹⁹ is methyl. 9. The device of claim 8 wherein each W is a bond and each L is _BR_ or _RB′_. 10. The wettable, flexible, oxygen permeable, ophthalmic device of claim 1, the crosslinkable monomer a) having segments of formula Ib, or of formula Ic, or of formula Id wherein each S″ is independently a segment of formula Ia of claim 1; each D, A and L is independently as defined in claim 1; c is 1-10; and a times c is 1-10; La being selected from _BRB′_ and _BR_; and wherein S′, B, R and B′ are as defined in claim 1. 11. The device of claim 10 wherein a is one and each D is oxygen. 12. The device of claim 10 wherein each L is _BRB′_, _BR_ or _RB′_, each B is _C(O)NH_ wherein the nitrogen atom is bound to R, and R is phenylene unsubstituted or substituted by methyl. 13. The device of claim 10 wherein each R¹ and R² is methyl; h is 4; i is 4; and v is from about 15 to about 50. 14. The device of claim 10 wherein (x + y + z) times q is from about 25 to about 75. 15. The device of claim 10 wherein a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen or b) each b, d and f is zero, each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶, and R²⁰ is hydrogen, and each R⁷, R¹³, and R¹⁹ is methyl. 16. The device of claim 15 wherein (x + y + z) times q is about 25 to about 75. 17. The device of claim 10 wherein c is 1. 18. The device of claim 10 wherein a is 1; each D is oxygen; each L is _BRB′_, _BR_ or _RB′_; each B and B′ are _C(O)NH_ with the nitrogen atom bound to R; each R is phenylene unsubstituted or substituted by methyl; each R¹ and R² is methyl; h and i are each 4; v is from about 15 to about 50; (x + y + z) times q is about 25 to about 75; and a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen; or b) each b, d and f is zero; each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶ and R²⁰ is hydrogen; and each R⁷, R¹³, and R¹⁹ is methyl; and c is one. 19. The device of claim 18 wherein each W is a bond and each L is _BR_ or _RB′_. 20. The wettable, flexible, oxygen permeable ophthalmic device of claim 14 the monomer a) having the formula wherein e is zero or 1; each D, A, L, S″, and c is independently as defined in claim 10; L′ is hydrogen, P′-R_, P′-BR_, P′-RB′_, or P′-BRB′_; and L″ is hydrogen, or _P′, or, in case that e is zero, also _D-S′-BR-P′ or _D-S′-BRB′-P′ and wherein P′ is hydrogen, amino, hydroxy, NCO, NCS, vinyl or a moiety containing a crosslinkable group which may be crosslinked when coreacted with a suitable crosslinking agent or when irradiated by actinic radiation. 21. The device of claim 20 wherein a is one and each D is oxygen. 22. The device of claim 20 wherein each L is _BRB′_, _BR_ or _RB′_, each B is _C(O)NH_ wherein the nitrogen atom is bound to R, and R is phenylene unsubstituted or substituted by methyl. 23. The device of claim 20 wherein each R¹ and R² is methyl, h is 4; i is 4; and v is from about 15 to about 50. 24. The device of claim 20 wherein (x + y + z) times q is from about 25 to about 75. 25. The device of claim 20 wherein a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen or b) each b, d and f is zero, each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶, and R²⁰ is hydrogen, and each R⁷, R¹³, and R¹⁹ is methyl. 26. The device of claim 25 wherein (x + y + z) times q is about 25 to about 75. 27. The device of claim 20 wherein c is 1. 28. The device of claim 20 wherein L′ is P′-BRB′_. 29. The device of claim 20 wherein each P′ is 30. The device of claim 20 wherein a is 1; each D is oxygen; each L is _BRB′_, _BR_ or _RB′_; each B and B′ are _C(O)NH_ with the nitrogen atom bound to R; each R is phenylene unsubstituted or substituted by methyl; each R¹ and R² is methyl; h and i are each 4; v is from about 15 to about 50; (x + y + z) times q is about 25 to about 75; and a) each b, d, and f is 1 and R³-R²⁰ are all hydrogen; or b) each b, d and f is zero; each R³, R⁴, R⁸-R¹⁰, R¹⁴-R¹⁶ and R²⁰ is hydrogen; and each R⁷, R¹³, and R¹⁹ is methyl; L′ is P′-BRB′ or P′; and P′ is 31. The device of claim 30 wherein each W is a bond, each L is _BR_ or _RB′_, and L′ and L″ are each _CH=CH₂. 32. The device of claim 1 which is a contact lens. 33. The device of claim 1 wherein each A is of the formula wherein each of x, y, z, and q are greater than zero. 34. The device of claim 33 wherein q is one. 35. The device of claim 33 wherein x and z within any one A are the same. 36. The device of claim 33 wherein each x and each z has the same value. 37. A process for the manufacture of an optically clear wettable, flexible, oxygen permeable polymer of a) a crosslinkable monomer having a segment S″ of the formula wherein each of the variables is as defined in claim 1, and b) a sufficient amount of a hydrophilic modifying monomer to impart to said polymer a water content in its aqueous swollen state of at least 10%, said hydrophilic modifying monomer being selected from the compounds of formula (A), (B) and (C) as defined in claim 1; and said polymer having a receding contact angle of less than 60°; and having a Dk (× 10⁻¹⁰ mm · ml O₂/cm² · sec · mmHg) of at least about 7, by reacting the required intermediates in a manner known per se. 38. The process of claim 37 for the manufacture of a wettable, flexible, oxygen permeable, polymer wherein the crosslinkable monomer a) has segments of formula Ib, or of formula Ic, or of formula Id wherein each S″ is independently a segment of formula Ia of claim 1; each D, A and L is independently as defined in claim 1; c is 1-10; and a times c is 1-10; La being selected from _BRB′_ and _BR_; and wherein S′, B, R and B′ are as defined in claim 1. 39. The process of claim 38 for the manufacture of a wettable, flexible, oxygen permeable, polymer wherein the monomer a) has the formula wherein e is zero or 1; each D, A, L, S″, and c is independently as defined in claim 10; L′ is hydrogen, P′-R_, P′-BR_, P′-RB′_, or P′-BRB′_; and L″ is hydrogen, or _P′, or, in case that e is zero, also _D-S′-BR-P′ or _D-S′-BRB′-P′ and wherein P′ is hydrogen, amino, hydroxy, NCO, NCS, vinyl or a moiety containing a crosslinkable group which may be crosslinked when coreacted with a suitable crosslinking agent or when irradiated by actinic radiation. 40. The device of claim 1 wherein said hydrophilic modifying monomer is selected from the group of the formula (R²⁴-div) nz Hy 41. The process of claim 37 wherein said hydrophilic modifying monomer is selected from the group of the formula (R²⁴-div) nz Hy 42. The process of claim 41 wherein R²⁴ is an ethylenically unsaturated group. 43. The process of claim 42 wherein R²⁴ is vinyl, 1-methylvinyl, 2-methylvinyl or allyl; and the terminus of div to which it is bound is _C(O)R²⁶, the carbonyl being bound to R²⁴, where R²⁵ is hydrogen or methyl and R²⁶ is _O_, or _NR²⁷_ with R²⁷ being hydrogen or lower alkyl; ib) H₂C=CH_ and the terminus of div to which it is bound is the left hand bond being bound to R²⁴, wherein R²⁸ is _O_, _NR²⁷_, _C(O)_, or _C(O)O_; and and the terminus of div to which it is bound is _C(O)R³⁰_, the carbonyl being bound to R²⁴ wherein R³⁰ is lower alkylene or _[CH₂CH(loweralkyl)-O]₁₋₅_ and R²⁹ is hydrogen, lower alkyl, or cyano. 44. The process of claim 41 wherein Hy is ce) morpholino which is unsubstituted or mono- up to tetra-substituted by lower alkyl; wherein ne is one, two, or three, each of which is unsubstituted or substituted, by lower alkyl; where nf is 2 or 3, each of which is unsubstituted or substituted by lower alkyl; ch) a divalent group of the formula wherein R³¹ is hydrogen or carboxy; where ng is one or two, each of which is unsubstituted or substituted by lower alkyl; cl) a polyol selected from polyvinyl alcohol radicals, wherein xa is 2-10 and xb is an integer from zero up to xa + 1 inclusive, the cyclic saccharide analogs thereof, the di-tetra saccharides thereof, C(CH₂O)₄(H) xc wherein xc is 0-3, and polyhydroxy lower alkylene glycol radicals wherein up to 50%, of the hydroxy groups are missing their alcoholic hydrogens. 45. The process of claim 41 wherein div is selected from 46. The process of claim 41 wherein said hydrophilic modifying monomer is selected from wherein R³² is in which yc is 1-6, and yb is 0 up to (yc + 1), and ya is 1 up to (yc + 2 - yb), wherein R³³ is C(CH₂O)₄(H) 4-yd and yd is 1-4; ace) polyvinyl alcohol having at least one and up to 50% inclusive, of the alcoholic hydrogens thereof absent; and 47. The process of claim 46 wherein said hydrophilic modifying monomer is selected from said groups aca), acb) and acf). 48. Use of a polymer of claim 37 or 39 for the manufacture of an ophthalmic device.

Inventors: ROBERTSON, J. RICHARD, SU, KAI CHIANG
Applicants: CIBA-GEIGY AG
Application year: 1989
Main classification: G02B1
IPC codes: C08G77, G02C7, A61L27, C08G18, G02B1