Polyamines partially substituted by piperidine-triazines

Abstract: The present invention relates to novel piperidyl-triazine compounds with 2 or more triazine rings, to their use as light stabilizers, heat stabi­ lizers and oxidation stabilizers for organic materials, and to the organic materials thus stabilized.

Description: It is known that synthetic polymers undergo a progressive change in mechanical strength and variation in colour when they are exposed to sunlight or other sources of ultraviolet light in the presence of oxygen. To retard the photooxidative degradation of synthetic polymers, it has been proposed to use various additives having photostabilizing properties, such as some derivatives of benzophenone and benzotriazole, nickel complexes, substituted benzoic acid esters, alkylidene malonates, cyanoacrylates, aromatic oxamides and sterically hindered amines. Some triazine derivatives of 2,2,6,6-tetramethyl-4-piperidylamine have shown effectiveness as light stabilizers, for example those disclosed in EP-A-14 683 and GB-A-2 120 248. In particular, US-A-4,108,829, US-A-4,288,593 and BE-A-904,401 describe, for example, dialkylenetriamines which contain polyalkyl-4-piperidyl-triazine groups. The present invention relates to novel piperidine-triazine compounds of the general formula (I) in which R₁ is hydrogen, C₁-C₄alkyl, O · , OH, NO, CH₂CN, C₁-C₈alkoxy, C₅-C₁₂cycloalkoxy, C₃-C₆alkenyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di- or tri-substituted on the phenyl by C₁-C₄alkyl, C₁-C₈acyl or C₂-C₄alkyl substituted by one OH in the 2-, 3- or 4-position, R₂ is hydrogen, C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di- or tri-substituted on the phenyl by C₁-C₄alkyl, or C₂-C₄alkyl substituted by OH, C₁-C₈alkoxy or di-(C₁-C₄alkyl)-amino in the 2-, 3- or 4-position, R₃ is C₁-C₁₈alkyl, phenyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, or one of the groups -OR₁₅ or -SR₁₅ in which R₁₁ is as defined above for R₁, R₁₂ is as defined above for R₂, R₁₃ and R₁₄ which can be identical or different are as defined above for R₂ or are C₃-C₆alkenyl or, together with the nitrogen atom to which they are linked, form part of a 5-membered to 7-membered heterocyclic ring and R₁₅ is C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₃-C₆alkenyl, phenyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di- or tri-substituted on the phenyl by C₁-C₄alkyl, or a group of the formula (II) with R₁₆ being as defined above for R₁, R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl or a group of the formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₁₂alkylene, n is zero or 1, R₆ and R₈ are C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₃-C₆alkenyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di- or tri-substituted on the phenyl by C₁-C₄alkyl, C₂-C₄alkyl substituted by OH in the 2-, 3- or 4-position, or a group of the formula (II) or R₆ is one of the groups of the formula (IIIb)-(IIId) or R₈ is one of the groups of the formula (IIIa)-(IIId) -(CH₂) p COOR₁₇ (IIIa), -COR₁₈COOR₁₉ (IIIb), -SO₂R₂₃ (IIId) in which p is zero or an integer from 1 to 5, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₃-C₁₈alkenyl or a group of the formula (II), R₁₈ is a direct bond or C₁-C₁₂alkylene, cyclohexylene or phenylene, R₂₀ is hydrogen, C₁-C₄alkyl or phenyl, R₂₁ is -CN or a group -COOR₂₂ with R₂₂ being as defined above, and R₂₃ is C₁-C₁₈alkyl or phenyl which is unsubstituted or mono- di- or tri-substituted by C₁-C₄alkyl, or R₈ is a group of the formula (IV) with R₁, R₂ and R₃ being as defined above, and, if n is zero or if R₈ is a group of the formula (IV), R₆ can also be one of the groups of the formulae (Va) or (Vb) -R₂₄X₁ (Va), -COOR₂₅OOCX₁ (Vb) where R₂₄ is C₂-C₁₂alkylene, 2-hydroxytrimethylene or xylylene and R₂₅ is C₂-C₁₂alkylene, C₄-C₁₂alkylene interrupted by 1, 2 or 3 oxygen atoms, cyclohexylenedimethylene, methylenedicyclohexylene, isopropylidenedicyclohexylene, phenylene, xylylene or a group with R₂₆ being hydrogen, C₁-C₄alkyl or phenyl, and X₁ is a group of the formula (VI) where R₁, R₂, R₃, R₄, R₅, R₇, R₉, R₁₀ and n are as defined above, and X₂ is a group of the formula (IV). Representative examples of C₁-C₄alkyl R₁, R₁₁, R₁₆, R₂₀, and R₂₆ are methyl, ethyl, propyl, butyl and isobutyl. R₁, R₁₁ and R₁₆ are preferably methyl. Examples of C₁-C₁₈alkyl are methyl, ethyl, propyl, isopropyl, butyl, 2-butyl, isobutyl, t-butyl, pentyl, 2-pentyl, hexyl, heptyl, octyl, 2-ethylhexyl, t-octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, hexadecyl and octadecyl. R₂, R₄, R₆, R₈, R₁₀ and R₁₂ are preferably C₁-C₁₂alkyl, in particular C₁-C₈alkyl, and R₁₇, R₁₉ and R₂₂ are preferably C₁-C₁₆alkyl. Examples of OH-substituted C₂-C₄alkyl are 2-hydroxyethyl, 2-hydroxypropyl, 3-hydroxypropyl, 2-hydroxybutyl and 4-hydroxybutyl. 2-Hydroxyethyl is a preferred example of R₁, R₁₁ and R₁₆. Examples of C₂-C₄alkyl substituted by C₁-C₈alkoxy, preferably C₁-C₄alkoxy, in particular methoxy or ethoxy, are 2-methoxyethyl, 2-ethoxyethyl, 3-methoxypropyl, 3-ethoxypropyl, 3-butoxypropyl, 3-octoxypropyl and 4-methoxybutyl. Examples of C₂-C₄alkyl substituted by di-(C₁-C₄alkyl)-amino, preferably dimethylamino or diethylamino, are 2-dimethylaminoethyl, 2-diethylaminoethyl, 3-dimethylaminopropyl, 3-diethylaminopropyl, 3-dibutylaminopropyl and 4-diethylaminobutyl. Representative examples of C₁-C₁₈alkoxy R₁, R₁₁ and R₁₆ are methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, pentoxy, isopentoxy, hexoxy, heptoxy, octoxy, decyloxy, dodecyloxy, tetradecyloxy, hexadecyloxy and octadecyloxy. C₆-C₁₂alkoxy in particular heptoxy or octoxy, is preferred. Examples of C₅-C₁₂cycloalkyl which is unsubstituted or substituted by C₁-C₄alkyl, in particular methyl, are cyclopentyl, methylcyclopentyl, dimethylcyclopentyl, cyclohexyl, methylcyclohexyl, dimethylcyclohexyl, trimethylcyclohexyl, t-butylcyclohexyl, cyclooctyl, cyclodecyl and cyclododecyl. Representative examples of C₅-C₁₂cycloalkoxy R₁, R₁₁ and R₁₆ are cyclopentoxy, cyclohexoxy, cycloheptoxy, cyclooctoxy, cyclodecyloxy and cyclododecyloxy. Cyclopentoxy and cyclohexoxy are preferred. Examples of alkenyl having up to 18 carbon atoms are allyl, 2-methylallyl, hexenyl, decenyl, undecenyl and oleyl. The carbon atom in the position 1 of the alkenyl group is preferably a primary carbon atom. Examples of substituted phenyl are methylphenyl, dimethylphenyl, trimethylphenyl, t-butylphenyl and di-t-butylphenyl. Examples of phenylalkyl which is unsubstituted or substituted on the phenyl, are benzyl, methylbenzyl, dimethylbenzyl, t-butylbenzyl and 2-phenylethyl. Benzyl is preferred. C₁-C₈acyl R₁, R₁₁ and R₁₆ can be aliphatic or aromatic acyl groups. C₁-C₈alkanoyl, C₃-C₈alkenoyl and benzoyl are preferred. Representative examples are formyl, acetyl, propionyl, butyryl, valeryl, caproyl, capryloyl, benzoyl, acryloyl and crotonyl. Examples of alkylene having up to 12 carbon atoms are methylene, ethylene, propylene, trimethylene, tetramethylene, pentamethylene, 2,2-dimethyltrimethylene, hexamethylene, trimethylhexamethylene, decamethylene and dodecamethylene. Alkylene having up to 10 carbon atoms, especially up to 8 carbon atoms, is preferred. R₅, R₇ and R₉ are in particular C₂-C₃alkylene. Examples of C₄-C₁₂alkylene interrupted by 1, 2 or 3 oxygen atoms are 3-oxapentane-1,5-diyl, 3,6-dioxaoctane-1,8-diyl and 3,6,9-trioxaundecane-1,11-diyl. 3-Oxapentane-1,5-diyl is preferred. If R₁₃ and R₁₄, together with the nitrogen atom to which they are linked, form a 5-membered to 7-membered heterocyclic radical, which preferably contains a further heteroatom, for example nitrogen or oxygen, representative examples are pyrrolidyl, piperidyl, morpholinyl, N-methylpiperazinyl and hexahydroazepinyl. Those compounds of the formula (I) are preferred in which R₂ is hydrogen, C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, benzyl or C₂-C₃alkyl substituted by OH C₁-C₄alkoxy or di-(C₁-C₄alkyl)-amino in the 2- or 3-position, R₃ is C₁-C₁₂alkyl, phenyl or one of the groups -OR₁₅ or -SR₁₅ in which R₁₁ is as defined above, R₁₂ is as defined above for R₂, R₁₃ and R₁₄ which can be identical or different are as defined above for R₂ or are allyl, or the group is 1-pyrrolidyl, 1-piperidyl, 4-morpholinyl or 1-hexahydroazepinyl and R₁₅ is C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, phenyl, benzyl or a group of the formula (II) with R₁₆ being as defined for R₁, R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, or a group of the formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₁₀alkylene, n is zero or 1, R₆ and R₈ are C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono, di- or tri-substituted by C₁-C₄alkyl, allyl, benzyl, C₂-C₃alkyl substituted by OH in the 2- or 3-position, or a group of the formula (II) or R₆ is one of the groups of the formulae (IIIb)-(IIId) or R₈ is one of the groups of the formulae (IIIa)-(IIId) in which p is zero or an integer from 1 to 3, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₈alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono- , di- or tri-substituted by C₁-C₄alkyl, C₃-C₁₈alkenyl or a group of the formula (II), R₁₈ is a direct bond or C₁-C₁₀alkylene, R₂₀ is hydrogen or C₁-C₄alkyl, R₂₁ is -CN or a group -COOR₂₂ with R₂₂ being as defined above and R₂₃ is C₁-C₁₂alkyl, phenyl or tolyl, or R₈ is a group of the formula (IV) and R₆ is also a group of the formula (Va) or (Vb) in which R₂₄ is C₂-C₁₀alkylene, 2-hydroxytrimethylene or xylylene, R₂₅ is C₂-C₁₀alkylene, C₄-C₈alkylene interrupted by 1, 2 or 3 oxygen atoms, cyclohexylenedimethylene, isopropylidenedicyclohexylene or a group with R₂₆ being hydrogen or methyl, and X₁ is a group of the formula (VI). Those compounds of the formula (I) are particularly preferred in which R₂ is hydrogen, C₁-C₁₂alkyl, cyclohexyl which is unsubstituted or mono-, di-or tri-substituted by C₁-C₄alkyl, benzyl or C₂-C₃alkyl substituted by OH, methoxy, ethoxy, dimethylamino or diethylamino in the 2- or 3-position, R₃ is C₁-C₄alkyl, phenyl or one of the groups -OR₁₅ or -SR₁₅ in which R₁₁ is as defined above, R₁₂ is as defined above for R₂, R₁₃ and R₁₄ which can be identical or different are as defined above for R₂ or are allyl, or the group is 4-morpholinyl, and R₁₅ is C₁-C₈alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, phenyl, benzyl or a group of the formula (II) with R₁₆ being as defined above for R₁, R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₈alkyl, cyclohexyl or a group of the formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₈alkylene, n is zero or 1, R₆ and R₈ are C₁-C₈alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, benzyl, 2-hydroxyethyl or R₆ is one of the groups of the formulae (IIIb)-(IIId) or R₈ is one of the groups of the formulae (IIIa)-(IIId) in which p is zero or 1, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₆alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, oleyl or a group of the formula (II), R₁₈ is a direct bond or C₁-C₈alkylene, R₂₀ is hydrogen or methyl, R₂₁ is -CN or a group -COOR₂₂ with R₂₂ being as defined above, and R₂₃ is C₁-C₈ alkyl, phenyl or tolyl, or R₈ is a group of the formula (IV) and R₆ can also be a group of the formula (Va) or (Vb) in which R₂₄ is C₂-C₈-alkylene, 2-hydroxytrimethylene or xylylene, R₂₅ is C₂-C₈alkylene, C₄-C₆-alkylene interrupted by 1 or 2 oxygen atoms, cyclohexylenedimethylene, isopropylidenedicyclohexylene or a group and X₁ is a group of the formula (VI). Compounds of the formula (I) of special interest are those in which R₂ is hydrogen, C₁-C₈alkyl, cyclohexyl or C₂-C₃alkyl which is substituted by OH, methoxy or ethoxy in the 2- or 3-position, R₃ is a group with R₁₁ being as defined above and R₁₂ being as defined above for R₂, R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₄alkyl, cyclohexyl or a group of formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₆alkylene, n is zero or 1, R₆ and R₈ are C₁-C₄alkyl, allyl, benzyl or R₆ is one of the groups of the formulae (IIIb)-(IIIc) or R₈ is one of the groups of the formulae (IIIa)-(IIIc) in which p is zero, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₂alkyl, cyclohexyl, t-butylcyclohexyl or a group of the formula (II), R₁₈ is a direct bond, R₂₀ is hydrogen and R₂₁ is -CN, or R₈ is a group of the formula (IV) and R₆ is also a group of the formula (Vb) in which R₂₅ is C₄-C₈alkylene, 3-oxapentane-1,5-diyl, cyclohexylenedimethylene or isopropylidenedicyclohexylene and X₁ is a group of the formula (VI). Compounds of the formula (I) of particular interest are those in which R₁ is hydrogen or methyl, R₂ is C₁-C₈alkyl, R₃ is a group with R₁₁ being hydrogen or methyl and R₁₂ being C₁-C₈alkyl, R₄ and R₁₀ which can be identical or different are hydrogen or methyl, R₅, R₇ and R₉ which can be identical or different are -(CH₂)₂₋₃-, n is zero or 1, R₆ and R₈ are methyl or a group or R₈ is a group -COOR₁₇ where R₁₇ and R₂₂ which can be identical or different are C₁-C₈alkyl, 2,2,6,6-tetramethyl-4-piperidyl or 1,2,2,6,6-pentamethyl-4-piperidyl, or R₈ is a group of the formula (IV) and R₆ is also a group -COO(CH₂)₄₋₆OOCX₁, where X₁ is a group of the formula (VI). R₁, R₁₁ and R₁₆ independently of one another are preferably hydrogen, C₁-C₄alkyl, OH, C₆-C₁₂alkoxy, C₅-C₈cycloalkoxy, allyl, benzyl, acetyl or 2-hydroxyethyl, in particular hydrogen or methyl. Those compounds of the formula (I) are also of interest in which R₃ is a group of the formula where R₁₁ and R₁₂ are as defined above, R₄ and R₁₀ independently of one another are hydrogen, C₁-C₄alkyl or a group of the formula (II), R₆ and R₈ independently of one another are C₁-C₄alkyl or a group of the formula (IIIc), R₈ is additionally a group of the formula (IIIa) or (IV) and R₆ is additionally a group of the formula (Vb). R₃ is preferably a group of the formula The compounds of the formula (I) can be prepared by processes known per se, for example by reacting a chlorotriazine of the formula (VII) with R₁, R₂ and R₃ being as defined above, with a polyamine of the formula (VIII) with R₄, R₅, R₇, R₉, R₁₀ and n being as defined above, by operating as described, for example, in US Patent 4,108,829, the molar ratio of compound of the formula (VII) : compound of the formula (VIII) being e.g. equal to 2:1 if n is zero, and e.g. 2:1 to 3:1 if n is 1. Compounds of the formula (I) can be obtained in this way, in which R₆ is hydrogen and R₈ is hydrogen or a group of the formula (IV); from these compounds, the corresponding compounds with R₆ and R₈ other than H can be obtained e.g. successively by reaction with suitable alkylating or acylating reagents. If R₆ and R₈ are C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl, C₇-C₉phenylalkyl or a group of the formula (II), the compounds of the formula (I) can be obtained directly, for example by reacting a chlorotriazine of the formula (VII) with a polyamine of the formula (IX) in which R₄, R₅, R₇, R₉, R₁₀ and n are as defined before and R₆ and R₈ are as defined above. If R₆ and R₈ are methyl, the compounds of the formula (I) are preferably prepared by reacting the corresponding unsubstituted compounds with formaldehyde and formic acid (Eschweiler-Clarke reaction) or with formaldehyde and hydrogen in the presence of a hydrogenation catalyst such as e.g. palladium or platinum. In these reactions, the piperidine NH groups can also be methylated and, under suitable conditions, also the melamine NH groups which may be present. The reactions of the chlorotriazines of the formula (VII) with the polyamines of the formula (VIII) or (IX) are preferably carried out in an aromatic hydrocarbon solvent, for example toluene, xylene, ethylbenzene or trimethylbenzene, operating at a temperature from e.g. -20° to 200°C, preferably from -10° to 180°C. The successive substitution reactions are preferably carried out by directly using the reaction mixture obtained in the first stage, but it is also possible to separate the intermediate compounds with R₆ and possibly R₈ being H, and using them in the successive alkylation or acylation reactions followed ultimately by possible purification using, if appropriate, a solvent other than that employed in the first stage. The hydrohalic acid eliminated in the various reactions is conveniently neutralized with an inorganic base, for example sodium or potassium hydroxide or carbonate, in a quantity at least equivalent to the acid eliminated. The product obtained can optionally be a mixture of possible isomers which are obtainable in the partial substitution reaction of the polyamines of the formula (VIII) with the chlorotriazines of the formula (VII). As mentioned at the outset, the compounds of the formula (I) are highly effective in improving the light stability, heat stability and oxidation stability of organic materials, in particular synthetic polymers and copolymers. The very high stabilizing activity of the compounds of the invention against oxidation is particularly surprising. The invention therefore also relates to a composition containing an organic material, which is susceptible to thermal, oxidative or light-induced degradation, and at least one compound of the formula (I). Examples of organic materials are: 1. Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, polybutene-1, polymethylpentene-1, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for instance of cyclopentene or norbornene, polyethylene (which optionally can be crosslinked), for example high-density polyethylene (HDPE), low-density polyethylene (LDPE) and linear low-density polyethylene (LLDPE). 2. Mixtures of the polymers mentioned under 1), for example mixtures of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of different types of polyethylene (for example LDPE/HDPE). 3. Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, such as, for example, ethylene/propylene, linear low-density polyethylene (LLDPE) and its mixtures with low-density polyethylene (LDPE), propylene/butene-1, ethylene/hexene, ethylene/ethylpentene, ethylene/heptene, ethylene/octene, propylene/isobutylene, ethylene/butene-1, propylene/butadiene, isobutylene/isoprene, ethylene/alkyl acrylates, ethylene/alkyl methacrylates, ethylene/vinyl acetate or ethylene/acrylic acid copolymers and their salts (ionomers) and terpolymers of ethylene with propylene and a diene, such as hexadiene, dicyclopentadiene or ethylidene-norbornene; as well as mixtures of such copolymers and their mixtures with polymers mentioned in 1) above, for example polypropylene/ethylene-propylene copolymers, LDPE/EVA, LDPE/EAA, LLDPE/EVA and LLDPE/EAA. 3a. Hydrocarbon resins (for example C₅-C₉) and hydrogenated modifications thereof (for example tackyfiers). 4. Polystyrene, poly-(p-methylstyrene), poly-(α-methylstyrene). 5. Copolymers of styrene or α-methylstyrene with dienes or acrylic derivatives, such as, for example, styrene/acrylonitrile, styrene/alkyl methacrylate, styrene/maleic anhydride, styrene/butadiene/ethyl acrylate, styrene/acrylonitrile/methyl acrylate; mixtures of high impact strength from styrene copolymers and another polymer, such as, for example, from a polyacrylate, a diene polymer or an ethylene/propylene/diene terpolymer; and block copolymers of styrene, such as, for example, styrene/butadiene/styrene, styrene/isoprene/styrene, styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/styrene. 6. Graft copolymers of styrene or α-methylstyrene such as, for example, styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitrile; styrene and acrylonitrile (or methacrylonitrile) on polybutadiene; styrene and maleic anhydride or maleimide on polybutadiene; styrene, acrylonitrile and maleic anhydride or maleimide on polybutadiene; styrene, acrylonitrile and methyl methacrylate on polybutadiene, styrene and alkyl acrylates or methacrylates on polybutadiene, styrene and acrylonitrile on ethylene/propylene/diene terpolymers, styrene and acrylonitrile on polyacrylates or polymethacrylates, styrene and acrylonitrile on acrylate/butadiene copolymers, as well as mixtures thereof with the copolymers listed under 5), for instance the copolymer mixtures known as ABS, MBS, ASA or AES polymers. 7. Halogen-containing polymers, such as polychloroprene, chlorinated rubbers, chlorinated or sulfochlorinated polyethylene, epichlorohydrin homo- and copolymers, polymers from halogen-containing vinyl compounds, as for example polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride, as well as copolymers thereof, as for example vinyl chloride/vinylidene chloride, vinyl chloride/vinyl acetate or vinylidene chloride/vinyl acetate copolymers. 8. Polymers which are derived from α,β-unsaturated acids and derivatives thereof, such as polyacrylates aand polymethacrylates, polyacrylamide and polyacrylonitrile. 9. Copolymers from the monomers mentioned under 8) with each other or with other unsaturated monomers, such as, for instance, acrylonitrile/butadiene, acrylonitrile/alkyl acrylate, acrylonitrile/ alkoxyalkyl acrylate or acrylonitrile/vinyl halide copolymers or acrylonitrile/alkyl methacrylate/butadiene terpolymers. 10. Polymers which are derived from unsaturated alcohols and amines, or acyl derivatives thereof or acetals thereof, such as polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallylmelamine; as well as their copolymers with olefins mentioned in 1) above. 11. Homopolymers and copolymers of cyclic ethers, such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bis-glycidyl ethers. 12. Polyacetals, such as polyoxymethylene and those polyoxymethylenes which contain ethylene oxide as a comonomer; polyacetals modified with thermoplastic polyurethanes, acrylates or MBS. 13. Polyphenylene oxides and sulfides, and mixtures of polyphenylene oxides with polystyrene or polyamides. 14. Polyurethanes which are derived from polyethers, polyesters or polybutadienes with hydroxyl groups on the one hand and on the other hand aliphatic or aromatic polyisocyanates, as well as precursors thereof (polyisocyanates, polyols or prepolymers). 15. Polyamides and copolyamides which are derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, such as polyamide 4, polyamide 6, polyamide 6/6, polyamide 6/10, 6/9, 6/12 and 4/6, polyamide 11, polyamide 12, aromatic polyamides obtained by condensation of m-xylylenediamine and adipic acid; polyamides prepared from hexamethylenediamine and isophthalic or/and terephthalic acid and optionally an elastomer as modifier, for example poly-2,4,4-trimethylhexamethylene-terephthalamide or poly-m-phenylene-isophthalamide. Further, copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers; or with polyethers, such as for instance, with polyethylene glycols, polypropylene glycols or polytetramethylene glycols. Polyamides or copolyamides modified with EPDM or ABS. Polyamides condensed during processing (RIM-polyamide systems). 16. Polyureas, polyimides and polyamide-imides. 17. Polyesters which are derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones, such as polyethylene terephthalate, polybutylene terephthalate, poly-1,4-dimethylolcyclohexane terephthalate, poly-[2,2-(4-hydroxyphenyl)-propane] terephthalate and polyhydroxybenzoates as well as block copolyetheresters derived from polyethers having hydroxyl end groups. 18. Polycarbonates and polyester-carbonates. 19. Polysulfones, polyether-sulfones and polyether-ketones. 20. Crosslinked polymers which are derived from aldehydes on the one hand and phenols, ureas and melamines on the other hand, such as phenol/formaldehyde resins, urea/formaldehyde resins and melamine formaldehyde resins. 21. Drying and non-drying alkyd resins. 22. Unsaturated polyester resins which are derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crossslinking agents, and also halogen-containing modifications thereof of low inflammability. 23. Thermosetting acrylic resins, derived from substituted acrylic esters, such as epoxy-acrylates, urethane-acrylates or polyester-acrylates. 24. Alkyd resins, polyester resins or acrylate resins in a mixture with melamine resins, urea resins, polyisocyanates or epoxide resins as crosslinking agents. 25. Crosslinked epoxide resins which are derived from polyepoxides, for example from bis-glycidyl ethers or from cycloaliphatic diepoxides. 26. Natural polymers, such as cellulose, rubber, gelatine and derivatives thereof which are chemically modified in a polymerhomologous manner, such as cellulose acetates, cellulose propionates and cellulose butyrates, or cellulose ethers, such as methylcellulose; rosins and their derivatives. 27. Mixtures of polymers as mentioned above, for example PP/EPDM, polyamide 6/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPE/HIPS, PPE/PA 6.6 and copolymers, PA/HDPE, PA/PP, PA/PPE. 28. Naturally occurring and synthetic organic materials which are pure monomeric compounds or mixtures of such compounds, for example mineral oils, animal and vegetable fats, oil and waxes, or oils, fats and soaps based on synthetic esters (e.g. phthalates, adipates, phosphates or trimellitates) and also mixtures of synthetic esters with mineral oils in any weight ratios, which materials may be used as plasticizers for polymers or as textile spinning oils, as well as aqueous emulsions of such materials. Compounds of the formula (I) are particularly suitable for improving the light stability, heat stability and oxidation stability of polyolefins, especially polyethylene and polypropylene. The compounds of the formula (I) can be used in mixtures with organic materials, including synthetic polymers, in various proportions depending on the nature of the material to be stabilized, on the end use and on the presence of other additives. In general, it is appropriate to use, for example, 0.01 to 5% by weight of the compounds of the formula (I) relative to the weight of the materials to be stabilized, preferably from 0.05 to 1%. The compounds of the formula (I) can be incorporated in the polymeric materials by various processes, such as dry mixing in the form of powder, or wet mixing in the form of solutions or suspensions or also in the form of a master batch; in such operations, the polymer can be used in the form of powder, granules, solutions, suspensions or in the form of lattices. The polymers stabilized with the products of the formula (I) can be used for the production of mouldings, films, tapes, monofilaments, suface coatings and the like. If desired, other conventional additives for synthetic polymers, such as antioxidants, UV absorbers, nickel stabilizers, pigments, fillers, plasticizers, antistatic agents, flame proofing agents, lubricating agents, corrosion inhibitors and metal deactivators, can be added to the mixtures of the compounds of the formula (I) with the organic materials. Particular examples of additives which can be used in a mixture with the compounds of the formula (I) are: 1. Antioxidants 1.1. Alkylated monophenols , for example 2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-dimethylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-isobutylphenol, 2,6-di-cyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dimethylphenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol, 2,6-di-tert-butyl-4-methoxymethylphenol, 2,6-dinonyl-4-methylphenol. 1.2. Alkylated hydroquinones , for example 2,6-di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butylhydroquinone, 2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyloxyphenol. 1.3. Hydroxylated thiodiphenyl ethers , for example 2,2'-thiobis(6-tert-butyl-4-methylphenol), 2,2'-thiobis(4-octylphenol), 4,4'-thiobis(6-tert-butyl-3-methylphenol), 4,4'-thiobis(6-tert-butyl-2-methylphenol). 1.4. Alkylidenebisphenols , for example 2,2'-methylenebis(6-tertbutyl-4-methylphenol), 2,2'-methylenebis(6-tert-butyl-4-ethylphenol), 2,2'-methylenebis[4-methyl-6-(-methylcyclohexyl)phenol], 2,2'-methylenebis(4-methyl-6-cyclohexylphenol), 2,2'-methylenebis(6-nonyl-4-methylphenol), 2,2'-methylenebis(4,6-di-tert-butylphenol), 2,2'-ethylidenebis(4,6-di-tert-butylphenol), 2,2'-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2'-methylenebis[6-(α-methylbenzyl)-4-nonylphenol], 2,2'-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol], 4,4'-methylenebis((2,6-di-tert-butylphenol), 4,4'-methylenebis(6-tert-butyl-2-methylphenol), 1,1-bis(5-tertbutyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis[3,3-bis(3'-tert-butyl-4'-hydroxyphenyl)butyrate], bis(3-tertbutyl-4-hydroxy-5-methylphenyl)-dicyclopentadiene, bis[2-(3'-tertbutyl-2'-hydroxy-5'-methylbenzyl)-6-tert-butyl-4-methylphenyl] terephthalate. 1.5. Benzyl compounds , for example 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene, bis(3,5-di-tert-butyl-4-hydroxybenzyl) sulfide, isooctyl 3,5-di-tert-butyl-4-hydroxybenzyl mercaptoacetate, bis(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl) dithiolterephthalate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanurate, dioctadecyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate, calcium salt of monoethyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate, 1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl) isocyanurate. 1.6. Acylaminophenols , for example lauric acid 4-hydroxyanilide, stearic acid 4-hydroxyanilide, 2,4-bis(octylmercapto)-6-(3,5-ditert-butyl-4-hydroxyanilino)-s-triazine, octyl N-(3,5-di-tertbutyl-4-hydroxyphenyl)carbamate. 1.7. Esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, diethylene glycol, octadecanol, triethylene glycol, 1,6-hexanediol, pentaerythritol, neopentyl glycol, tris(hydroxyethyl) isocyanurate, thiodiethylene glycol, N,N'-bis(hydroxyethyl)oxalic acid diamide. 1.8. Esters of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, diethylene glycol, octadecanol, triethylene glycol, 1,6-hexanediol, pentaerythritol, neopentyl glycol, tris(hydroxyethyl) isocyanurate, thiodiethylene glycol, N,N'-bis(hydroxyethyl)oxalic acid diamide. 1.9. Esters of β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, diethylene glycol, octadecanol, triethylene glycol, 1,6-hexanediol, pentaerythritol, neopentyl glycol, tris(hydroxyethyl) isocyanurate, thiodiethylene glycol, N,N'-bis(hydroxyethyl)oxalic acid diamide. 1.10. Amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid e.g. N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)trimethylene-diamine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine. 2. UV absorbers and light stabilizers 2.1. 2-(2'-Hydroxyphenyl)benzotriazoles, for example the 5'-methyl, 3',5'-di-tert-butyl, 5'-tert-butyl, 5'-(1,1,3,3-tetramethylbutyl), 5-chloro-3',5'-di-tert-butyl, 5-chloro-3'-tert-butyl-5'-methyl, 3'-sec-butyl-5'-tert-butyl, 4'-octoxy, 3',5'-di-tert-amyl and 3',5'-bis(α,α-dimethylbenzyl) derivatives. 2.2. 2-Hydroxbenzophenones, for example the 4-hydroxy, 4-methoxy, 4-octoxy, 4-decyloxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-trihydroxy and 2'-hydroxy-4,4'-dimethoxy derivatives. 2.3. Esters of substituted and unsubstituted benzoic acids, for example 4-tert-butylphenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoylresorcinol, bis(4-tert-butylbenzoyl)resorcinol, benzoylresorcinol, 2,4-di-tert-butylphenyl 3,5-di-tertbutyl-4-hydroxybenzoate and hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate. 2.4. Acrylates , for example ethyl α-cyano-β,β-diphenylacrylate, isooctyl α-cyano-β,β-diphenylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-β-methyl-p-methoxycinnamate, butyl α-cyanoβ-methyl-p-methoxycinnamate, methyl α-carbomethoxy-p-methoxycinnamate and N-(β-carbomethoxy-β-cyanovinyl)-2-methylindoline. 2.5. Nickel compounds, for example nickel complexes of 2,2'-thio-bis[4-(1,1,3,3-tetramethylbutyl)phenol], such as the 1:1 or 1:2 complex, with or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamine, nickel dibutyldithiocarbamate, nickel salts of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid monoalkyl esters, e.g. of the methyl or ethyl ester, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methylphenyl undecyl ketoxime, nickel complexes of 1-phenyl-4-lauroyl5-hydroxypyrazole, with or without additional ligands. 2.6. Sterically hindered amines, for example bis(2,2,6,6-tetramethylpiperidyl) sebacate, bis(1,2,2,6,6-pentamethylpiperidyl) sebacate, bis(1,2,2,6,6-pentamethylpiperidyl) n-butyl-3,5-di-tertbutyl-4-hydroxybenzylmalonate, the condensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, the condensation product of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-tert-octylamino-2,6-dichlorol,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl) nitrilotriacetate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl) 1,2,3,4-butanetetracarboxylate, 1,1'-(1,2-ethanediyl)bis(3,3,5,5-tetramethyl-piperazinone). 2.7. Oxalic acid diamides, for example 4,4'-dioctyloxyoxanilide, 2,2'-dioctyloxy-5,5'-di-tert-butyloxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butyloxanilide, 2-ethoxy-2'-ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxalamide, 2-ethoxy-5-tert-butyl-2'-ethyloxanilide and its mixtures with 2-ethoxy-2'-ethyl-5,4'-di-tert-butyloxanilide and mixtures of ortho- and paramethoxy-disubstituted oxanilides and mixtures of o-and p-ethoxy-disubstituted oxanilides. 3. Metal deactivators , for example N,N'-diphenyl, N-salicylal-N'-salicyloylhydrazine, N,N'-bis(salicyloyl)hydrazine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine, 3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalodihydrazide. 4. Phosphites and phosphonites, for example triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl) 4,4'-biphenylene-diphosphonite, 3,9-bis(2,4-di-tert-butylphenoxy)-2,4,8,10-tetra-oxa-3,9-diphosphaspiro[5.5]undecane. 5. Peroxide scavengers , for example esters of β-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercaptobenzimidazole or the zinc salt of 2-mercaptobenzimidazole, zinc dibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis(β-dodecylmercapto) propionate. 6. Polyamide stabilizers, for example copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese. 7. Basic co-stabilizers, for example melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids, for example Ca stearate, zinc stearate, magnesium stearate, sodium ricinoleate and potassium palmitate, antimony pyrocatecholate or zinc pyrocatecholate. 8. Nucleating agents , for example 4-tert-butyl-benzoic acid, adipic acid, diphenylacetic acid. 9. Fillers and reinforcing agents, for example calcium carbonate, silicates, glass fibres, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite. 10. Other additives, for example plasticizers, lubricants, emulsifiers, pigments, optical brighteners, flameproofing agents, antistatic agents and blowing agents. Preferred compounds of formula (I) are those of Examples 1, 2, 4 and 8. In the following examples the group corresponds to 2,2,6,6-tetramethyl-4-piperidyl and the group corresponds to 1,2,2,6,6-pentamethyl-4-piperidyl. EXAMPLE 1 : Preparation of 45.21 g (0.1 mol) of 2-chloro-4,6-bis[N-(2,2,6,6-tetramethyl-4-piperidyl)methylamino]-1,3,5-triazine and 5.16 g (0.05 mol) of diethylenetriamine in 200 ml of xylene are heated for 2 hours under reflux. After the addition of 6.0 g (0.15 mol) of finely powdered sodium hydroxide, the mixture is heated for 14 hours under reflux, the water of reaction being simultaneously separated off azeotropically. The mixture is cooled and washed with 3 times 80 ml of water. The organic solution thus obtained is heated to 110°C, and a solution consisting of 12.66 g (0.275 mol) of formic acid and 8.26 g (0.275 mol) of paraformaldehyde, previously dissolved in 15 ml of water containing 0.1 g of sodium hydroxide, is slowly added, the added water and the water of reaction being removed azeotropically. After the end of the addition, the mixture is heated for 1 hour at 110°C. It is cooled to 80°C, and a solution of 4.0 g (0.1 mol) of sodium hydroxide in 20 ml of water is added. The mixture is heated for 1 hour under reflux and cooled to 80°C, and the aqueous phase is separated off. After washing with twice 80 ml of water, the organic solution is evaporated in vacuo (24 mbar), the product of melting point 167-171°C being obtained. Analysis for C₅₅H₁₀₅N₁₇ Calculated: C = 65.76%; H = 10.54%; N = 23.70% Found: C = 65.12%; H = 10.39%; N = 23.68% EXAMPLES 2-4 : Proceeding analogously to Example 1 and using the respective intermediates and reagents in appropriate molar ratios, the products of the formula: are obtained. EXAMPLE A : Preparation of 48.01 g (0.1 mol) of 2-chloro-4,6-bis[N-(2,2,6,6-tetramethyl-4-piperidyl)-ethylamino]-1,3,5-triazine and 5.16 g (0.05 mol) of diethylenetriamine in 200 ml of xylene are heated for 2 hours under reflux. After the addition of 6.0 g (0.15 mol) of finely powdered sodium hydroxide, the mixture is heated for a further 14 hours under reflux, the water of reaction being simultaneously separated off azeotropically. The mixture is cooled to ambient temperature and washed with 3 times 80 ml of water. A solution of 5.43 g (0.05 mol) of ethyl chloroformate in 10 ml of xylene is then added to the organic solution cooled to -10°C. After the end of the addition, the mixture is stirred for 2 hours at 0°C, and a solution of 2.0 g of sodium hydroxide in 20 ml of water is then slowly added. The mixture is then stirred for 1 hour at ambient temperature, and the aqueous phase is separated off. The solution is evaporated in vacuo (24 mbar), a product of melting point 115-119°C being obtained. Analysis for C₅₇H₁₀₇N₁₇O₂ Calculated: C = 64.42%; H = 10.15%; N = 22.41% Found: C = 64.37%; H = 10.10%; N = 22.35% EXAMPLES 5-11 : Proceeding analogously to Example A and using the respective intermediates and reagents in appropriate molar ratios, the products of the formula: are obtained. EXAMPLE 12 : Preparation of Proceeding analogously to Example 1, 45.21 g (0.1 mol) of 2-chloro-4,6-bis[N-(2,2,6,6-tetramethyl-4-piperidyl)-methylamino]-1,3,5-triazine are reacted with 5.16 g (0.05 mol) of diethylenetriamine in 200 ml of xylene. The organic solution of the condensation product is heated to 35-40°C, and 8.46 g (0.05 mol) of ethyl (ethoxymethylene)-cyanoacetate are slowly added. After the end of the addition, the mixture is heated for 5 hours at 60°C and for another 4 hours at 80°C. The solution is then evaporated in vacuo (24 mbar), a product of melting point = 140-143°C being obtained. Analysis for C₅₆H₁₀₀N₁₈O₂ Calculated: C = 63.60%; H = 9.53%; N = 23.84% Found: C = 63.18%; H = 9.48%; N = 23.68% EXAMPLE 13: Preparation of Proceeding analogously to Example 12, 45.84 g (0.045 mol) of the product obtained by condensation of 48.01 g (0.01 mol) of 2-chloro-4,6-bis[N-(2,2,6,6-tetramethyl-4-piperidyl)-ethylamino]-1,3,5-triazine with 6.56 g (0.05 mol) of dipropylenetriamine are reacted with 7.62 g (0.045 mol) of ethyl (ethoxymethylene)-cyanoacetate in 150 ml of xylene, a product of melting point 110-114°C being obtained. Analysis for C₆₂H₁₁₂N₁₈O₂ Calculated: C = 65.23%; H = 9.89%; N = 22.08% Found: C = 65,11%; H = 9.82%; N = 21.98% EXAMPLE 14: (Antioxidant action in polypropylene plaques) 1 g of each of the compounds indicated in Table 1 and 1 g of calcium stearate are mixed in a slow mixer with 1.000 g of polypropylene powder of melt index = 2 g/10 minutes (measured at 230°C and 2.16 kg). The mixtures are extruded twice at 200- 220°C to give polymer granules which are then converted into plaques of 1 mm thickness (mould according to DIN 53,451) by compression-moulding for 3 minutes at 220°C. The plates obtained are exposed in a forced-circulation air oven maintained at a temperature of 135°C. These specimens are periodically checked by bending through 180°, in order to determine the time (in hours) required for the onset of embrittlement. Plates prepared under the same conditions as indicated above, but without the addition of the stabilizers, are exposed for comparison. The results obtained are shown in table 1. Stabilizer Time to embrittlement (hours) without stabilizer 250 compound from Example 1 1,360 compound from Example 2 1,500 compound from Example 4 1,350 compound from Example 8 1,300 compound from Example 12 1,440 EXAMPLE 15 : (Light-stabilizing action in polypropylene fibres) 2.5 g of each of the products indicated in Table 2, 0.5 g of tris-(2,4-di-t-butylphenyl) phosphite, 0.5 g of calcium monoethyl 3,5-di-t-butyl-4-hydroxybenzylphosphonate, 1 g of calcium stearate and 2.5 g of titanium dioxide (®KRONOS RN 57) are mixed in a slow mixer with 1,000 g of polypropylene powder of melt index = 12 g/10 minutes (measured at 230°C and 2.16 kg). The mixtures are extruded at 200-220°C to give polymer granules which are then converted into fibres, using a pilot-type apparatus (Leonard, Sumirago (VA), Italy) and operating under the following conditions: extruder temperature: 200-230°C head temperature: 255-260°C stretch ratio: 1 : 3.5 denier: 11 dtex per filament The fibres thus produced are exposed, mounted on a white card, in a model 65 WR Weather-O-Meter (ASTM G 26-77) at a black panel temperature of 63°C. The residual tenacity is measured on samples, taken after various times of exposure to light, by means of a constant-speed tensometer; the exposure time in hours, needed to halve the initial tenacity is then calculated (T50). Fibres prepared under the same conditions as indicated above, but without the addition of compounds according to the invention, are exposed for comparison. The results obtained are shown in Table 2. Stabilizer T50 (hours) without stabilizer 150 compound from Example 7 1,300 compound from Example 8 1,700 compound from Example 9 1,790 compound from Example 10 1,690 compound from Example 11 1,580 compound from Example 13 1,460 EXAMPLE 16 : (Light-stabilizing action in polypropylene tapes) 1 g of each of the compounds indicated in Table 3, 0.5 g of tris-(2,4-di-t-butylphenyl) phosphite, 0.5 g of pentaerythritol tetrakis-3-(3,5-di-t-butyl-4-hydroxyphenyl)-propionate and 1 g of calcium stearate are mixed in a slow mixer with 1,000 g of propylene powder of melt index = 2 g /10 minutes (measured at 230°C and 2.16 kg). The mixtures are extruded at 200-220°C to give polymer granules which are then converted into stretched tapes of 50 µm thickness and 2.5 mm width, using a pilot-type apparatus (Leonard-Sumirago (VA) Italy) and operating under the following conditions: extruder temperature: 210-230°C head temperature: 240-260°C stretch ratio = 1 : 6 The tapes thus prepared are exposed, mounted on a white card, in a model 65 WR Weather-O-Meter (ASTM G 26-77) at a black panel temperature of 63°C. The residual tenacity is measured on samples, taken after various times of exposure to light, by means of a constant-speed tensometer; the exposure time (in hours) needed to halve the initial tenacity is then calculated (T50). Tapes prepared under the same conditions as indicated above, but without the addition of stabilizer, are exposed for comparison. The results obtained are shown in Table 3: Stabilizer T50 (hours) without stabilizer 500 compound from Example 1 2,170 compound from Example 2 2,200 compound from Example 3 2,060 compound from Example 4 2,300 compound from Example 8 2,500 compound from Example 9 2,530 compound from Example 10 2,260 compound from Example 13 2,240

Claims: A compound of the formula (I) in which R₁ is hydrogen, C₁-C₄alkyl, O · , OH, NO, CH₂CN, C₁-C₁₈alkoxy, C₅-C₁₂cycloalkoxy, C₃-C₆alkenyl, C₇-C₉phenylalkyl which is unsubstituted or mono- di- or tri-substituted on the phenyl by C₁-C₄alkyl, C₁-C₈acyl or C₂-C₄alkyl substituted by one OH in the 2-, 3- or 4-position, R₂ is hydrogen, C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di-or tri-substituted on the phenyl by C₁-C₄alkyl, or C₂-C₄alkyl substituted by OH, C₁-C₈alkoxy or di-(C₁-C₄alkyl)-amino in the 2-, 3- or 4-position, R₃ is C₁-C₁₈alkyl, phenyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, or one of the groups -OR₁₅ or -SR₁₅ in which R₁₁ is as defined above for R₁, R₁₂ is as defined above for R₂, R₁₃ and R₁₄ which can be identical or different are as defined above for R₂ or are C₃-C₆alkenyl or, together with the nitrogen atom to which they are linked, form part of a 5-membered to 7-membered heterocyclic ring and R₁₅ is C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₃-C₆alkenyl, phenyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di- or tri-substituted on the phenyl by C₁-C₄alkyl, or a group of the formula (II) with R₁₆ being as defined above for R₁, R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl or a group of the formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₁₂alkylene, n is zero or 1, R₆ and R₈ are C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄-alkyl, C₃-C₆alkenyl, C₇-C₉phenylalkyl which is unsubstituted or mono-, di- or tri-substituted on the phenyl by C₁-C₄alkyl, C₂-C₄alkyl substituted by OH in the 2-, 3- or 4-position, or a group of the formula (II) or R₆ is one of the groups of the formula (IIIb)-(IIId) or R₈ is one of the groups of the formula (IIIa)-(IIId) -(CH₂) p COOR₁₇ (IIIa), -COR₁₈COOR₁₉ (IIIb), -SO₂R₂₃ (IIId) in which p is zero or an integer from 1 to 5, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₈alkyl, C₅-C₁₂cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, C₃-C₁₈alkenyl or a group of the formula (II), R₁₈ is a direct bond or C₁-C₁₂alkylene, cyclohexylene or phenylene, R₂₀ is hydrogen, C₁-C₄alkyl or phenyl, R₂₁ is -CN or a group -COOR₂₂ with R₂₂ being as defined above, and R₂₃ is C₁-C₁₈alkyl or phenyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, or R₈ is a group of the formula (IV) with R₁, R₂ and R₃ being as defined above, and, if n is zero or if R₈ is a group of the formula (IV), R₆ can also be one of the groups of the formulae (Va) or (Vb) -R₂₄X₁ (Va), -COOR₂₅OOCX₁ (Vb) where R₂₄ is C₂-C₁₂alkylene, 2-hydroxytrimethylene or xylylene and R₂₅ is C₂-C₁₂alkylene, C₄-C₁₂alkylene interrupted by 1, 2 or 3 oxygen atoms, cyclohexylenedimethylene, methylenedicyclohexylene, isopropylidenedicyclohexylene, phenylene, xylylene or a group with R₂₆ being hydrogen, C₁-C₄alkyl or phenyl, and X₁ is a group of the formula (VI) where R₁, R₂, R₃, R₄, R₅, R₇, R₉, R₁₀ and n are as defined above, and X₂ is a group of the formula (IV). A compound of the formula (I) according to claim 1, in which R₂ is hydrogen, C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, benzyl or C₂-C₃alkyl substituted by OH, C₁-C₄alkoxy or di-(C₁-C₄alkyl)-amino in the 2- or 3-position, R₃ is C₁-C₁₂alkyl, phenyl or one of the groups -OR₁₅ or -SR₁₅ in which R₁₁ is as defined in claim 1 for R₁, R₁₂ is as defined above for R₂, R₁₃ and R₁₄ which can be identical or different are as defined above for R₂ or are allyl, or the group is 1-pyrrolidyl, 1-piperidyl, 4-morpholinyl or 1-hexahydroazepinyl and R₁₅ is C₁-C₁₂alkyl, C₅-C₈-cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, phenyl, benzyl or a group of the formula (II), R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, or a group of the formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₁₀-alkylene, n is zero or 1, R₆ and R₈ are C₁-C₁₂alkyl, C₅-C₈cycloalkyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, benzyl, C₂-C₃alkyl substituted by OH in the 2- or 3-position, or a group of the formula (II) or R₆ is one of the groups of the formulae (IIIb)-(IIId) or R₈ is one of the groups of the formulae (IIIa)-(IIId) in which p is zero or an integer from 1 to 3, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₈alkyl, C₅-C₈-cycloalkyl which is unsubstituted or mono-, di-or tri-substituted by C₁-C₄alkyl, C₃-C₁₈alkenyl or a group of the formula (II), R₁₈ is a direct bond or C₁- C₁₀alkylene, R₂₀ is hydrogen or C₁-C₄alkyl, R₂₁ is -CN or a group -COOR₂₂ with R₂₂ being as defined above and R₂₃ is C₁-C₁₂alkyl, phenyl or tolyl, or R₈ is a group of the formula (IV) and R₆ is also a group of the formula (Va) or (Vb) in which R₂₄ is C₂-C₁₀alkylene, 2-hydroxytrimethylene or xylylene, R₂₅ is C₂-C₁₀alkylene, C₄-C₈alkylene interrupted by 1, 2 or 3 oxygen atoms, cyclohexylenedimethylene, isopropylidenedicyclohexylene or a group with R₂₆ being hydrogen or methyl, and X₁ is a group of the formula (VI). A compound of the formula (I) according to claim 1, in which R₂ is hydrogen, C₁-C₁₂alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, benzyl or C₂-C₃alkyl substituted by OH, methoxy, ethoxy, dimethylamino or diethylamino in the 2- or 3-position, R₃ is C₁-C₄alkyl, phenyl or one of the groups -OR₁₅ or -SR₁₅ in which R₁₁ is as defined in claim 1, R₁₂ is as defined above for R₂, R₁₃ and R₁₄ which can be identical or different are as defined above for R₂ or are allyl, or the group is 4-morpholinyl, and R₁₅ is C₁-C₈alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, phenyl, benzyl or a group of the formula (II), R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₈alkyl, cyclohexyl or a group of the formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₈alkylene, n is zero or 1, R₆ and R₈ are C₁-C₈alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄-alkyl, allyl, benzyl, 2-hydroxyethyl or R₆ is one of the groups of the formulae (IIIb)-(IIId) or R₈ is one of the groups of the formulae (IIIa)-(IIId) in which p is zero or 1, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₆alkyl, cyclohexyl which is unsubstituted or mono-, di- or tri-substituted by C₁-C₄alkyl, allyl, oleyl or a group of the formula (II), R₁₈ is a direct bond or C₁-C₈alkylene, R₂₀ is hydrogen or methyl, R₂₁ is -CN or a group -COOR₂₂ with R₂₂ being as defined above, and R₂₃ is C₁-C₈alkyl, phenyl or tolyl, or R₈ is a group of the formula (IV) and R₆ can also be a group of the formula (Va) or (Vb) in which R₂₄ is C₂-C₈alkylene, 2-hydroxytrimethylene or xylylene, R₂₅ is C₂-C₈alkylene, C₄-C₆alkylene interrupted by 1 or 2 oxygen atoms, cyclohexylenedimethylene, isopropylidenedicyclohexylene or a group and X₁ is a group of the formula (VI). A compound of the formula (I) according to claim 1, in which R₂ is hydrogen, C₁-C₈alkyl, cyclohexyl or C₂-C₃alkyl which is substituted by OH, methoxy or ethoxy in the 2- or 3-position, R₃ is a group with R₁₁ being as defined above in claim 1 and R₁₂ being as defined above for R₂, R₄ and R₁₀ which can be identical or different are hydrogen, C₁-C₄alkyl, cyclohexyl or a group of formula (II), R₅, R₇ and R₉ which can be identical or different are C₂-C₆alkylene, n is zero or 1, R₆ and R₈ are C₁-C₄alkyl, allyl, benzyl or R₆ is one of the groups of the formulae (IIIb)-(IIIc) or R₈ is one of the groups of the formulae (IIIa)-(IIIc) in which p is zero, R₁₇, R₁₉ and R₂₂ which can be identical or different are C₁-C₁₂alkyl, cyclohexyl, t-butylcyclohexyl or a group of the formula (II), R₁₈ is a direct bond, R₂₀ is hydrogen and R₂₁ is -CN, or R₈ is a group of the formula (IV) and R₆ is also a group of the formula (Vb) in which R₂₅ is C₄-C₈alkylene, 3-oxapentane-1,5-diyl, cyclohexylenedimethylene or isopropylidenedicyclohexylene and X₁ is a group of the formula (VI). A compound of the formula (I) according to claim 1, in which R₁ is hydrogen or methyl, R₂ is C₁-C₈alkyl, R₃ is a group with R₁₁ being hydrogen or methyl and R₁₂ being C₁-C₈alkyl, R₄ and R₁₀ which can be identical or different are hydrogen or methyl, R₅, R₇ and R₉ which can be identical or different are -(CH₂) 2-3 , n is zero or 1, R₆ and R₈ are methyl or a group or R₈ is a group -COOR₁₇ where R₁₇ and R₂₂ which can be identical or different are C₁-C₈alkyl 2,2,6,6-tetramethyl-4-piperidyl or 1,2,2,6,6-pentamethyl-4-piperidyl, or R₈ is a group of the formula (IV) and R₆ is also a group -COO(CH₂)₄₋₆OOCX₁, where X₁ is a group of the formula (VI). A compound of the formula (I) according to claim 1, in which R₁, R₁₁ and R₁₆ independently of one another are hydrogen, C₁-C₄alkyl, OH, C₆-C₁₂alkoxy, C₅-C₈cycloalkyl, allyl, benzyl, acetyl or 2-hydroxyethyl. A compound of the formula (I) according to claim 1, in which R₁, R₁₁ and R₁₆ independently of one another are hydrogen or methyl. A compound of the formula (I) according to claim 1, in which R₃ is a group of the formula in which R₁₁ and R₁₂ are as defined above in claim 1, R₄ and R₁₀ independently of one another are hydrogen, C₁-C₄alkyl or a group of the formula (II), R₆ and R₈ independently of one another are C₁-C₄alkyl or a group of the formula (IIIc), R₈ is additionally a group of the formula (IIIa) or (IV) and R₆ is additionally a group of the formula (Vb). A compound of the formula (I) according to claim 1, in which R₃ is a group of the formula with R₁₁ and R₁₂ being as defined in claim 1. The compounds according to claim 1. A composition comprising an organic material susceptible to thermal, oxidative or light-induced degradation and at least one compound of the formula (I) according to claim 1. A composition according to claim 11, wherein the organic material is a synthetic polymer. A composition according to claim 12, which, in addition to the compound of the formula (I), also contains other conventional additives for synthetic polymers. A composition according to claim 11, wherein the organic material is a polyolefin. A composition according to claim 11, wherein the organic material is polyethylene or polypropylene. The use of a compound of the formula (I) according to claim 1 for stabilizing an organic material against thermal, oxidative or light-induced degradation.

Inventors: BORZATTA VALERIO DR, CANTATORE GIUSEPPE DR, MASINA FRANCA, BORZATTA, VALERIO, DR., CANTATORE, GIUSEPPE, DR., MASINA, FRANCA
Applicants: CIBA GEIGY AG, CIBA GEIGY SPA, CIBA-GEIGY AG, CIBA-GEIGY S.P.A.
Application year: 1989
Main classification: C07D401
IPC codes: C08L23, C07D401, C09K15, C08K5