Method for the preparation of a resin composition

Abstract: A resin composition comprising polyphenylene sulfide and hypophosphorous acid or its salt.

Description: The present invention relates to a method for the preparation of a resin composition comprising a polyphenylene sulfide resin as the main component. A thermoplastic resin composed essentially of polyphenylene sulfide (hereinafter sometimes referred to simply as PPS) is excellent in the heat resistance, dimensional stability, chemical resistance and flame retardancy, and it is used as an engineering plastic material for various applications. PPS may be used by itself for molding films or fibers. However, it is more common to use it in combination with a reinforcing fiber such as glass fiber or other fillers such as talc, calcium carbonate or glass beads. As such PPS, a linear type and a cross-linked type are known. A thermoplastic resin composed essentially of PPS has a drawback that it is poor in the impact resistance, although it is excellent in the heat resistance, dimensional stability, chemical resistance and flame retardancy. Further, PPS has a drawback that when heated during the molding process, it tends to undergo discoloration. This tendency is remarkable with the cross-linked type. US-A-4 212 793 discloses a poly(arylene sulfide) having incorporated therein a corrosion inhibiting amount of at least one metal salt selected from the group calcium hypophosphite, sodium tetraborate, trisodium citrate, trisodium phosphate and tetrasodium pyrophosphate. It is an object of the present invention to solve such problems inherent to the PPS thermoplastic resin and to provide a PPS resin composition having high impact strength and minimum tendency for discoloration and a method for its preparation. The present invention provides a method for preparing a resin composition which comprises: uniformly mixing glass fiber strands having hypophosphorous acid or its salt attached to the surface thereof, in a melt of a polyphyenylene sulfide resin. Now, the present invention will be described in further detail with reference to the preferred embodiments. Hypophosphorous acid or its salt (hereinafter referred to simply as the compound of the present invention) includes hypophosphorous acid, sodium hypophosphite, potassium hypophosphite, calcium hypophosphite, magnesium hypophosphite and zinc hypophosphite. Preferred are hypophosphites, particularly calcium hypophosphite and sodium hypophosphite. The resin composition of the present invention may be molded into pellets, semi-processed products (such as rods or sheets) or final products. The polyphenylene sulfide may be of the linear type or the cross-linked type. The polyphenylene sulfide resin of the present invention may be a polymer alloy of PPS containing a thermoplastic resin such as polytetrafluoroethylene or polyethylene, as a subordinate resin component, in an amount of from 0.1 to 50% by weight based on the total resin. Namely, for the purpose of the present invention, the polyphenylene sulfide resin includes such a polymer alloy. According to the method of the present invention, the compound of the present invention is attached on the surface of glass fiber strand for reinforcement and the glass fiber strand is mixed to a melt of the polyphenylene sulfide resin. As such glass fiber strand, there may be employed a strand obtained by applying a known sizing agent to glass fiber, followed by bundling. There is no particular restriction as to the manner for attaching the compound of the present invention to the glass fiber strand. For example, a solution containing the compound of the present invention may be sprayed on the glass fiber strand, or such a solution may be coated on the glass fiber strand by means of a roll coater, whereby the total amount of the compound to be incorporated can be reduced. It is also possible to employ a sizing agent containing the compound of the present invention. The application of the above solution is preferably conducted under a dry state where the water content of the glass fiber strand is relatively small (preferably at most 5% by weight). The amount of the compound of the present invention to be attached on the surface of the glass fiber strand is from 0.05 to 1.5% by weight, preferably from 0.1 to 0.8% by weight, relative to the glass fiber. If the amount is too small, no adequate effects will be obtained for the improvement of the impact strength and for the prevention of discoloration or decrease in the strength. On the other hand, if the amount is excessive, no increase in the effects can be expected, and use of such an excessive amount is simply uneconomical. When the compound of the present invention is incorporated in a sizing agent, the concentration of the compound of the present invention in the sizing agent is preferably from 0.5 to 15% by weight, more preferably from 1 to 10% by weight. The glass fiber strand is dried to a water content of not higher than 0.1% by weight and then incorporated. The glass fiber strand is incorporated in an amount of from 2 to 80% by weight based on the polyphenylene sulfide resin. The glass fiber strand is mixed to the polyphenylene sulfide resin in a molten state, and the mixture is formed into pellets, semi-processed products or final products, in accordance with a conventional method. Further, it is possible to form pellets first, and then semi-processed products or final products may be prepared from such pellets. It is believed that when the glass fiber strand is mixed with a melt of the polyphenylene sulfide resin, the compound contained on the glass fiber strand diffuses into the resin and the serves to arrange PPS molecules and change the crystal structure to improve the impact resistance and to prevent the decomposition of PPS or formation of discolored components under heating. However, the exact mechanism has not yet been understood. Further, the concentration of the compound of the present invention is believed to be high at the interface of the glass fiber strand, to achieve the effect of the present invention more effectively than in a case where the compound of the present invention is simply uniformly dispersed in the polyphenylene sulfide resin without a filler. Now, the present invention will be described in further detail with reference to Examples. However, it should be understood that the present invention is by no means restricted to such specific Examples. COMPARATIVE EXAMPLE 1 60 parts by weight of PPS (KPS#214, tradename, manufactured by Kureha Chemical Industries Company Limited), 0.5 part by weight of calcium hypophosphite and 40 parts by weight of chopped glass fiber strand (#03 MA FT525, manufactured by Asahi Fiber Glass Company Limited) were mixed and pelletized in a conventional manner. The heating temperature was 320°C. These pellets were injection-molded to obtain three test pieces. The color shade (ΔE) was measured in accordance with JIS Z-8722. The results are shown in Table 1. Separately, with respect to five test pieces, the notched impact strength was measured in accordance with ASTM D-256. The results are also shown in Table 1. COMPARATIVE EXAMPLE 2 The test was conducted in the same manner as in Example 1 by using 60 parts of the same PPS as used in Example 1 and 40 parts of the same chopped strand as used in Example 1. The results are shown in Table 1. Comparative Example 1 Comparative Example 2 Color shade (ΔE) 27.4 43.4 Impact strength (kg-cm/cm) 11.3 8.7 EXAMPLE 1 60 parts by weight of PPS (KPS#214, tradename, manufactured by Kureha Chemical Industies Company Limited), and 40 parts by weight of chopped glass fiber strand obtained by using an epoxy sizing agent containing 3% by weight of calcium hypophosphite (content of calcium hypophosphite in the chopped strand: 0.3% by weight) were mixed and pellettized in a conventional manner. The heating temperature was 320°C. The pellets were injection-molded to obtain three test pieces. The color shade (ΔE) was measured in accordance with JIS Z-8722. The results are shown in Table 2. With respect to five test pieces, the notched impact strength was measured in accordance with ASTM D-256. The results are shown in Table 2. This strength is higher than the case where 0.5% by weight of the compound of the present invention is simply mixed in PPS. COMPARATIVE EXAMPLE 3 The test was conducted in the same manner as in Example 1 by using 60 parts of the same PPS as used in Example 1 and 40 parts by weight of the same chopped strand obtained by using the sizing agent containing no calcium hypophosphite. The results are shown in Table 2. Example 1 Comparative Example 3 Color shade (ΔE) 27.0 43.4 Impact strength (kg-cm/cm) 12.8 8.7 EXAMPLE 2 60 parts by weight of PPS (KPS#214, tradename, manufactured by Kureha Chemical Industries Company Limited) and 40 parts by weight of chopped glass fiber strand obtained by coating a 2 wt% calcium hypophosphite solution on the surface of a glass fiber strand obtained by using an epoxy sizing agent (amount of calcium hypophosphite coated: 0.2% by weight based on the glass fiber) and cutting and drying the glass fiber strand, were mixed and pellettized in a conventional manner. The heating temeprature was 320°C. The pellets were injection-molded to form three test pieces. The color shade (ΔE) was measured in accordance with JIS Z-8722. The results are shown in Table 3. With respect to five test pieces, the notched impact strength was measured in accordance with ASTM D-256. The results are shown in Table 3. This strength was higher than the case where 0.5% by weight of the compound of the present invention is simply mixed in PPS. COMPARATIVE EXAMPLE 4 The test was conducted in the same manner as in Example 3 by using 60 parts by weight of the same PPS as used in Example 3 and 40 parts by weight of the same chopped strand containing no calcium hypophosphite. The results are shown in Table 3. Example 2 Comparative Example 4 Color shade (ΔE) 26.5 43.4 Impact strength (kg-cm/cm) 13.0 8.7 As described in the foregoing, the present invention effectively improves the impact strength and prevents discoloration and deterioration in the strength of a polyphenylene sulfide resin.

Claims: A method for preparing a resin composition which comprises: uniformly mixing glass fiber strands having hypophosphorous acid or its salt attached to the surface thereof, in a melt of a polyphenylene sulfide resin. The method according to Claim 1, wherein the amount of hypophosphorous acid or its salt attached to the surface of the glass fiber strand ranges from 0.01 to 1.5 % by weight based on the strand. The method according to Claim 1, wherein the amount of hypophosphorous acid or its salt attached to the surface of the glass fiber strand ranges from 0.1 to 0.8 % by weight based on the strand. The method according to Claim 1, wherein the amount of the glass fiber strand ranges from 2 to 80 % by weight based on the polyphenylene sulfide resin. The method of Claim 1, wherein the salt of hypophosphorous acid is calcium or sodium hypophosphite.

Inventors: ARAI SHIGEHARU, FUNAMI FUMIYASU, KITSUNEZUKA AKIRA, OKAWARA ATSUO, SAKUMA NOBUHIRO, SUGIURA TOMIYA, ARAI, SHIGEHARU, FUNAMI, FUMIYASU, KITSUNEZUKA, AKIRA, OKAWARA, ATSUO, SAKUMA, NOBUHIRO, SUGIURA, TOMIYA
Applicants: ASAHI FIBREGLASS CO, ASAHI FIBER GLASS COMPANY LIMITED
Application year: 1989
Main classification: C08K9
IPC codes: C08K3