Ferroelectric chiral smectic liquid crystal composition and liquid crystal device using same

Abstract: A ferroelectric chiral smectic liquid crystal composition, comprising: at least one optically active compound represented by the following formula (II): at least one compound represented by the following formula (III): and at least one compound represented by the following formula (I) or (IV): wherein: R₁ to R₇ respectively denote a linear or branched alkyl group at least one of R₄ and R₅ being optically active; X₁ and X₂ respectively denote a single bond, -O-, X₃ denotes a single bond, -O- or X₄ denotes a single bond -O-, and X₅ denotes a single bond -O-, X₆ and X₇ respectively denote a single bond, -O-, Z₁ denotes a single bond or Z₂ denotes -CH₂O-, -OCH₂-or a single bond;

Description: FIELD OF THE INVENTION AND RELATED ART The present invention relates to a liquid crystal composition used in a liquid crystal display device, a liquid crystal-optical shutter, etc., more particularly to a novel liquid crystal composition with improved responsiveness to an electric field and a liquid crystal device using the liquid crystal composition. Hitherto, liquid crystal devices have been used as an electro-optical device in various fields. Most liquid crystal devices which have been put into practice use TN (twisted nematic) type liquid crystals, as shown in "Voltage-Dependent Optical Activity of a Twisted Nematic Liquid Crystal" by M. Schadt and W. Helfrich "Applied Physics Letters" Vol. 18, No. 4 (Feb. 15, 1971) pp. 127-128. These devices are based on the dielectric alignment effect of a liquid crystal and utilize an effect that the average molecular axis direction is directed to a specific direction in response to an applied electric field because of the dielectric anisotropy of liquid crystal molecules. It is said that the limit of response speed is on the order of milli-seconds, which is too slow for many uses. On the other hand, a simple matrix system of driving is most promising for application to a large-area flat display in view of cost, productivity, etc., in combination. In the simple matrix system, an electrode arrangement wherein scanning electrodes and signal electrodes are arranged in a matrix, and for driving, a multiplex driving scheme is adopted wherein an address signal is sequentially, periodically and selectively applied to the scanning electrodes and prescribed data signals are selectively applied in parallel to the signal electrodes in synchronism with the address signal. When the above-mentioned TN-type liquid crystal is used in a device of such a driving system, a certain electric field is applied to regions where a scanning electrode is selected and signal electrodes are not selected or regions where a scanning electrode is not selected and a signal electrode is selected (which regions are so called "half-selected points"). If the difference between a voltage applied to the selected points and a voltage applied to the half-selected points is sufficiently large, and a voltage threshold level required for allowing liquid crystal molecules to be aligned or oriented perpendicular to an electric field is set to a value therebetween, display devices normally operate. However, in fact, as the number (N) of scanning lines increases, a time (duty ratio) during which an effective electric field is applied to one selected point when a whole image area (corresponding to one frame) is scanned decreases with a ratio of 1/N. Accordingly, the larger the number of scanning lines are, the smaller is the voltage difference of an effective value applied to a selected point and non-selected points when scanning is repeatedly effected. As a result, this leads to unavoidable drawbacks of lowering of image contrast or occurrence of interference or crosstalk. These phenomena are regarded as essentially unavoidable problems appearing when a liquid crystal having no bistability (i.e. liquid crystal molecules are horizontally oriented with respect to the electrode surface as stable state and is vertically oriented with respect to the electrode surface only when an electric field is effectively applied) is driven (i.e. repeatedly scanned) by making use of a time storage effect. To overcome these drawbacks, the voltage averaging method, the two-frequency driving method, the multiple matrix method, etc. has been already proposed. However, any method is not sufficient to overcome the above-mentioned drawbacks. As a result, it is the present state that the development of large image area or high packaging density in respect to display elements is delayed because it is difficult to sufficiently increase the number of scanning lines. To overcome drawbacks with such prior art liquid crystal devices, the use of liquid crystal devices having bistability has been proposed by Clark and Lagerwall (e.g. Japanese Laid-Open Patent Appln. No. 56-107216, U.S.P. No. 4367924, etc.). In this instance, as the liquid crystals having bistability, ferroelectric liquid crystals having chiral smectic C-phase (SmC*) or H-phase (SmH*) are generally used. These liquid crystals have bistable states of first and second stable states with respect to an electric field applied thereto. Accordingly, as different from optical modulation devices in which the above-mentioned TN-type liquid crystals are used, the bistable liquid crystal molecules are oriented to first and second optically stable states with respect to one and the other electric field vectors, respectively. Further, this type of liquid crystal has a property (bistability) of assuming either one of the two stable states in response to an applied electric and retaining the resultant state in the absence of an electric field. In addition to the above-described characteristic of showing bistability, such a ferroelectric liquid crystal (hereinafter sometimes abbreviated as "FLC") has an excellent property, i.e., a high-speed responsiveness. This is because the spontaneous polarization of the ferroelectric liquid crystal and an applied electric field directly interact with each other to induce transition of orientation states. The resultant response speed is faster than the response speed due to the interaction between dielectric anisotropy and an electric field by 3 to 4 digits. The EP-A-178 647, the EP-A-0 267 585 and the EP-A-0 237 007 disclose examples of compositions applying the cumulative use of ferroelectric liquid crystal compounds. Thus, a ferroelectric liquid crystal potentially has very excellent characteristics, and by making use of these properties, it is possible to provide essential improvements to many of the above-mentioned problems with the conventional TN-type devices. Particularly, the application to a high-speed optical shutter and a display of a high density and a large picture is expected. For this reason, there has been made extensive research with respect to liquid crystal materials showing ferroelectricity. However, ferroelectric liquid crystal materials developed heretofore cannot be said to satisfy sufficient characteristics required for a liquid crystal device including low-temperature operation characteristic, high-speed responsiveness, etc. A high response speed can be obtained by (a) increasing the spontaneous polarization, (b) lowering the viscosity η, or (c) increasing the applied voltage. However, the driving voltage has a certain upper limit in view of driving with IC, etc., and should desirably be as low as possible. Accordingly, it is actually necessary to lower the viscosity or increase the spontaneous polarization. A ferroelectric chiral smectic liquid crystal having a large spontaneous polarization generally provides a large internal electric field in a cell given by the spontaneous polarization and is liable to pose many constraints on the device construction giving bistability. Further, an excessively large spontaneous polarization is liable to accompany an increase in viscosity, so that remarkable increase in response speed may not be attained as a result. Further, if it is assumed that the operation temperature of an actual display device is 5 - 40 °C, the response speed changes by a factor of about 20, so that it actually exceeds the range controllable by driving voltage and frequency. As described hereinabove, commercialization of a ferroelectric liquid crystal device requires a ferroelectric chiral smectic liquid crystal composition having a low viscosity, a high-speed responsiveness and a small temperature-dependence of response speed. In a representative FLC cell structure, a pair of substrates are disposed, each substrate of e.g. glass being provided with an electrode pattern of e.g. ITO, further thereon with a layer of e.g. SiO₂ (about 1000 Å) for preventing short circuit between the pair of substrates and further thereon with a film of e.g. polyimide (PI; such as SP-510, 710, ... available from Toray K.K.) of about 500 Å in thickness, which is then treated for alignment control by rubbing with e.g. an acetate fiber-planted cloth. Such a pair of substrates are disposed opposite to each other so that their alignment control directions are symmetrical and the spacing between the substrates is held at 1 - 3 microns. On the other hand, it is known that the ferroelectric liquid crystal molecules under such non-helical conditions are disposed in succession so that their directors (longer molecular axes) are gradually twisted between the substrates and do not show a uniaxial orientation or alignment (i.e., in a splay alignment state). A problem in this case is a low transmittance through the liquid crystal layer. Transmitted light intensity I through a liquid crystal is given by the following equation with respect to the incident light intensity I₀ under cross nicols when the uniaxial alignment of the molecules is assumed: I = I₀sin²(4ϑa) sin²(πΔnd/λ) (1), wherein Δn denotes the refractive index anisotropy of the FLC; d, the cell thickness; λ, the wavelength of the incident light; and ϑa, a half of the angle between two stable states (tilt angle). When a conventional FLC cell is used, it has been experimentally known that ϑa is 5 - 8 degrees under a twisted alignment condition. The control of physical properties affecting the term Δndπ/λ cannot be easily performed, so that it is desired to increase ϑa to increase I. However, this has not been successfully accomplished by only a static alignment technique. With respect to such a problem, it has been proposed to utilize a torque relating to a dielectric anisotropy Δε of an FLC (1983 SID report from AT & T; Japanese Laid-Open Patent Applns. 245142/1986, 246722/1986, 246723/1986, 246724/1986, 249024/1986 and 249025/1986). More specifically, a liquid crystal molecule having a negative Δε tends to become parallel to the substrates under application of an electric field. By utilizing this property, if an effective value of AC electric field is applied even in a period other than switching, the above-mentioned twisted alignment is removed, so that ϑa is increased to provide an increased transmittance (AC stabilization effect). A torque ΓP S acting on FLC molecules involved in switching of states and a torque ΓΔε acting on FLC molecules relating to the AC stabilization effect are respectively proportional to physical properties as shown in the following formulas: ΓP S ∝ P S ·E (2) ΓΔε ∝ 1/2 Δε·ε₀·E² (3) The above formula (3) apparently shows that the sign and absolute value of Δε of the FLC play an important role. Figure 4 attached hereto shows the change of ϑa versus Vrms experimentally measured for 4 FLCs having different values of Δε. The measurement was conducted under application of AC rectangular pulses of 60 KHz so as to remove the influence of P S . The curves (I) - (IV) correspond to the results obtained by using FLCs showing the following Δε values (I) Δε ≃ -5.5, (II) Δε ≃ -3.0, (III) Δε ≃ -0, (IV) Δε ≃ 1.0. As is clear from the graph in Figure 8, a larger negative value of Δε provides a large ϑa at a lower voltage and thus contributes to provision of an increased I. The transmittances obtained by using the liquid crystals (I) and (III) were 15 % for (I) and 6 % for (III) (under application of rectangular AC waveforms of 60 kHz and ±8 V), thus showing a clear difference. As is known from the above examples, the display characteristics of an SSFLC (Surface-Stabilized FLC) can be remarkably changed by controlling the properties relating to Δε and P S . In order to provide a ferroelectric liquid crystal composition having a negatively large Δε, it is most effective to include a compound having a negative Δε with a large absolute value. For example, it is possible to obtain a compound having a negatively large Δε by introducing a halogen or cyano group in a shorter axis direction of a molecule or by introducing a heterocyclic skeleton in a molecule. The magnitude of Δε of a compound having a negative Δε substantially varies depending on the structure thereof. Some examples of such compounds are shown below: Herein, R and R′ respectively denote an alkyl group. These may be classified roughly into three groups including compounds having a negatively small Δε ( |Δε| ≦ 2), compounds having a negatively medium Δε (2 < |Δε| ≦ 10) and compounds having a negatively large Δε( |Δε| > 10). Among these, compounds having a |Δε| of ≦ 2 have little effect of increasing |Δε|. Compounds having a |Δε| of > 10 are very effective in increasing |Δε| but those available heretofore are only dicyanohydroquinone derivatives. However, a dicyanohydroquinone derivative, while it has a large |Δε|-increasing effect, has a high viscosity, so that it is liable to degrade a switching characteristic when its content is increased. On the other hand, among the compounds having a medium |Δε| (2 < |Δε| ≦ 10), some compounds have a moderately low viscosity while their |Δε|-increasing effect is somewhat lower than those having a large |Δε|. From the above consideration, it is essential to select a compound having a negative anisotropy, preferably one having a |Δε| of > 2, and mixing it with an appropriately selected other compound in a properly selected mixing ratio. SUMMARY OF THE INVENTION An object of the present invention is to provide a chiral smectic liquid crystal composition having a large response speed and a decrease temperature-dependence of the response speed adapted for providing a practical ferroelectric liquid crystal device. Another object of the present invention is to provide a liquid crystal composition further containing a mesomorphic compound having a negative dielectric anisotropy to show an AC stabilization effect providing remarkably improved display characteristics. A further object of the present invention is to provide a liquid crystal device using such a liquid crystal composition and showing improved driving and display characteristics. According to the present invention, there is provided a ferroelectric chiral smectic liquid crystal composition, comprising: at least one optically active compound represented by the following formula (II): wherein R₃ denotes a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₃ denotes a single bond, -O- or Z₁ denotes a single bond or denotes or and m is 1 - 12; at least one compound represented by the following formula (III): wherein R₄ and R₅ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms, at least one of R₄ and R₅ being optically active; X₄ denotes a single bond, -O-, or and X₅ denotes a single bond, -O-, or and at least one compound represented by the following formula (I) or (IV): wherein R₁ and R₂ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent of C₁ - C₁₂ alkoxy group; X₁ and X₂ respectively denote a single bond, -O-, or wherein R₆ and R₇ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₆ and X₇ respectively denote a single bond, -O-, or Z₂ denotes -CH₂O-, -OCH₂- or a single bond; and respectively denote or and denotes or with proviso that at least one of and is or According to the present invention, there is further provided a ferroelectric liquid crystal composition as described above further comprising a mesomorphic compound having a negative dielectric anisotropy, which is preferably one having a Δε < -2 more preferably Δε < -5, most preferably Δε < -10. The present invention further provides a liquid crystal device comprising a pair of substrates and such a ferroelectric liquid crystal composition as described above disposed between the electrode plates. These and other objects, features and advantages of the present invention will become more apparent upon a consideration of the following description of the preferred embodiments of the present invention taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic sectional view of a liquid crystal display device using a ferroelectric liquid crystal; Figures 2 and 3 are schematic perspective views of a device cell embodiment for illustrating the operation principle of a ferroelectric liquid crystal device; and Figure 4 is a graph showing changes in tilt angle ϑa versus effective voltage Vrms with respect to several ferroelectric liquid crystals having different values of dielectric anisotropy Δε. DETAILED DESCRIPTION OF THE INVENTION Preferred examples of the compounds represented by the above-mentioned general formula (I) may include those represented by the following formulas (I-a) to (I-p). In the formulas (I-a) to (I-p), R₁ and R₂ are the same as in the general formula (I). Preferred examples of R₁ and R₂ may include those of the following combinations (I-i) to (I-vi): (I-i) R₁ is an n-alkyl group and R₂ is an n-alkyl group. (I-ii) R₁ is an n-alkyl group and R₂ is (optically active or inactive). (I-iii) R₁ is an n-alkyl group and R₂ is (optically active or inactive). (I-iv) R₁ is (optically active or inactive), and R₂ is an n-alkyl group. (I-v) R₁ is optically active or inactive) and R₂ is (optically active or inactive). (I-vi) R₁ is (optically active or inactive) and R₂ is (optically active or inactive). In the above formulas (I-i) to (I-vi), R₈, R₉ and R₁₀ respectively denote a linear or branched alkyl group; p, q and s are respectively 0 - 7; and r is 0 or 1. Further, preferred examples of the compounds represented by the above-mentioned general formula (II) may include those represented by the following formulas (II-a) and (II-b). In the above-formulas (II-a) and (II-b), R₁, X₁ and m are the same as in the general formula (II). Further, in the above-mentioned general formula (III), X₄ may preferably be -O- or and X₅ may preferably be -O- or Preferred examples of R₄ and R₅ may include those of the following combinations (III-i) to (III-v). (III-i) R₄ is an n-alkyl group and R₅ is (III-ii) R₄ is and R₅ is an n-alkyl group. (III-iii) R₄ is and R₅ is (III-iv) R₄ is an n-alkyl group and R₅ is (III-v) R₄ is and R₅ is an n-alkyl group. In the above combinations (III-i) to (III-v), R₁₁ to R₁₄ respectively denote a linear or branched alkyl group; s, t, u and y are respectively 0 - 7, and x and z are respectively 0 or 1. Further, preferred examples of the compounds represented by the above-mentioned general formula (IV) may include those represented by the following formulas (IV-a) to (IV-q). In the formulas (IV-a) to (IV-q), R₆, R₇, X₆ and X₇ are respectively the same as in the general formula (IV). Preferred examples of X₆ and X₇ may include the following combinations (IV-i) to (IV-viii): (IV-i) X₆ is a single bond and X₇ is a single bond, (IV-ii) X₆ is a single bond and X₇ is -O-, (IV-iii) X₆ is -O- and X₇ is a single bond, (IV-iv) X₆ is -O- and X₇ is -O-, (IV-v) X₆ is and X₇ is a single bond, (IV-vi) X₆ is and X₇ is -O-, (IV-vii) X₆ is and X₇ is a single bond, (IV-viii) X₆ is and X₇ is -O-. Further, preferred examples of R₆ and R₇ in the formulas (II-a) to (II-q) may include linear alkyl groups. Specific examples of the compounds represented by the above-mentioned general formula (I) may include those shown by the following structural formulas. The compounds represented by the formula (I) may be synthesized through processes as disclosed by, e.g., Japanese Laid-Open Patent Applications (KOKAI) 93170/1986, 24576/1986, 129170/1986, 200972/1986, 200973/1986, 215372/1986 and 291574/1986, and East German Patent 95892 (1973). For example, the following reaction scheme may be used for the synthesis. R₁, R₂ and X₂ are the same as defined above. A representative example of synthesis of a compound represented by the formula (I) is described below. Synthesis Example 1 (Synthesis of compound Example No. 1-71) A solution of 1.83 g (9.6 mmol) of p-toluenesulfonic acid chloride in 5 ml of pyridine was added dropwise to a solution of 1.06 g (8.0 mmol) of 5-methoxyhexanol in 5 ml of pyridine below 5 °C on an iced water bath. After stirring for 6 hours at room temperature, the reaction mixture was injected into 100 ml of cold water and, after being acidified with 6N-hydrochloric acid, was extracted with isopropyl ether. The organic layer was washed with water and dried with anhydrous magnesium sulfate, followed by distilling-off of the solvent to obtain 5-methoxyhexyl-p-toluenesulfonate. Separately, 2.0 g (6.41 mmol) of 5-decyl-2-(p-hydroxyphenyl)pyrimidine and 0.61 g of potassium hydroxide were added to 10 ml of dimethylformamide, and the mixture was stirred for 40 min. at 100 °C. To the mixture was added the above-prepared 5-methoxyhexyl-p-toluenesulfonate followed by 4 hours of stirring under heating at 100 °C. After the reaction, the reaction mixture was poured into 100 ml of cold water and extracted with benzene, followed by washing with water, drying with anhydrous magnesium sulfate and distilling-off of the solvent, to obtain a pale yellow oily product. The product was purified by column chromatography (silica gel - ethyl acetate/benzene = 1/9) and recrystallized from hexane to obtain 1.35 g of 5-decyl-2-[4-(5′-methoxyhexyloxy)phenyl]pyrimidine. Phase transition temperature (°C) Synthesis Example 2 (Synthesis of Compound Example No. 1-76) 2.04 g of 6-pentyloxyheptanol was dissolved in 8 ml of pyridine and cooled on an ice bath. Then, a solution of 2.26 g of tosyl chloride in 5 ml of pyridine was gradually added dropwise thereto below 5 °C in 5 min., followed by 5 hours of stirring at room temperature. The reaction mixture was poured into 150 ml of iced water and acidified to about pH 3 with 6N-hydrochloric acid aqueous solution, followed by extraction with ethyl acetate. The extract liquid was then washed with water, dried with anhydrous magnesium sulfate and subjected to distilling-off of the solvent to obtain 2.98 g of 6-pentyloxyheptyl p-toluenesulfonate. 3.12 g of 5-n-decyl-2-(4-hydroxyphenyl)pyrimidine and 0.53 g of potassium hydroxide were dissolved in 14 ml of dimethylformamide, and the mixture was stirred for 3 hours under heating at 100 °C, followed by addition of the 2.98 g of 6-pentyloxyheptyl p-toluenesulfonate and 5 hours of stirring under heating at 100 °C. The reaction mixture was poured into 200 ml of iced water, acidified to pH of about 3 and extracted with benzene. The extract liquid was washed with water, dried with anhydrous magnesium sulfate and subjected to distilling-off of the solvent to obtain 4.71 g of a crude product, which was then purified by silica gel column chromatography (n-hexane/ethyl acetate = 10/2) and recrystallized from hexane to obtain 1.56 g of 5-n-decyl-2-[4-(6-pentyloxyheptyloxy)phenyl]pyrimidine. IR (cm⁻¹) 2924, 2852, 1610, 1586, 1472, 1436, 1254, 1168, 1096, 798 Phase transition temperature (°C) The compounds other than those of the above-mentioned Synthesis Examples may be prepared along the following reaction scheme A or B. In the above schemes, R₁, R₉, X₁, q and r are the same as defined before. Specific examples of the compounds represented by the above-mentioned general formula (II) may include those shown by the following structural formulas. The compounds represented by the general formula (II) may be synthesized through the following reaction schemes A, B and C. Representative examples of synthesis of the compound represented by the general formula (II) are shown hereinbelow. Synthesis Example 3 (Synthesis of Compound Example 2-17) 1.00 g (4.16 mM) of p-2-fluorooctyloxyphenol was dissolved in a mixture of 10 ml of pyridine and 5 ml of toluene, and a solution of 1.30 g (6.0 mM) of trans-4-n-pentylcyclohexanecarbonyl chloride was added dropwise thereto in 20 - 40 min. at below 5 °C. After the addition, the mixture was stirred overnight at room temperature to obtain a white precipitate. After the reaction, the reaction product was extracted with benzene, and the resultant benzene layer was washed with distilled water, followed by drying with magnesium sulfate and distilling-off of the benzene, purification by silica gel column chromatography and recrystallization from ethanol/methanol to obtain 1.20 g (2.85 mM) of trans-4-n-pentylcyclohexanecarboxylic acid-p-2-fluorooctyloxyphenyl-ester. (Yield: 68.6 %) NMR data (ppm) 0.83 - 2.83 ppm (34H, m) 4.00 - 4.50 ppm (2H, q) 7.11 ppm (4H, s) IR data (cm⁻¹) 3456, 2928, 2852, 1742, 1508, 1470, 1248, 1200, 1166, 1132, 854. Phase transition temperature (°C) Herein, the respective symbols denote the following phases, Iso.: isotropic phase, Ch.: cholesteric phase, SmA: smectic A phase, SmC: smectic C phase, S₃ - S₆: phases of higher other than SmC or SmC* (chiral smectic C phase), and Cryst.: crystal phase. Synthesis Example 4 (Synthesis of Compound Example 2-29) In a vessel sufficiently replaced with nitrogen, 0.40 g (3.0 mmol) of (-)-2-fluoroheptanol and 1.00 g (13 mmol) of dry pyridine were placed and dried for 30 min. under cooling on an ice bath. Into the solution, 0.69 g (3.6 mmol) of p-toluenesulfonyl chloride was added, and the mixture was stirred for 5 hours. After the reaction, 10 ml of 1N-HCl was added, and the resultant mixture was subjected to two times of extraction with 10 ml of methylene chloride. The extract liquid was washed once with 10 ml of distilled water and dried with an appropriate amount of anhydrous sodium sulfate, followed by distilling-off of the solvent to obtain 0.59 g (2.0 mmol) of.(+)-2-fluoroheptyl p-toluenesulfonate. The yield was 66 %, and the product showed the following optical rotation and IR data. Optical rotation: IR (cm⁻¹): 2900, 2850, 1600, 1450, 1350, 1170, 1090 980, 810, 660, 550 0.43 g (1.5 mmol) of the thus obtained (+)-2-fluoroheptyl p-toluenesulfonate and 0.28 g (1.0 mmol) of 5-octyl-2-(4-hydroxyphenyl)pyrimidine were mixed with 0.2 ml of 1-butanol, followed by sufficient stirring. To the solution was quickly added a previously obtained alkaline solution of 0.048 g (1.2 mmol) of sodium hydroxide in 1.0 ml of 1-butanol, followed by 5.5 hours of heat-refluxing. After the reaction, 10 ml of distilled water was added, and the mixture was extracted respectively once with 10 ml of benzene and 5 ml of benzene, followed by drying with an appropriate amount of anhydrous sodium sulfate, distilling-off of the solvent and purification by silica gel column chromatography (chloroform) to obtain 0.17 g (0.43 mmol) of objective (+)-5-octyl-2-[4-(2-fluoroheptyloxy)phenyl]pyrimidine. The yield was 43 %, and the product showed the following optical rotation and IR data. Optical rotation: IR (cm⁻¹) 2900, 2850, 1600, 1580, 1420, 1250 1260, 800, 720, 650, 550. Specific examples of the compounds represented by the above-mentioned general formula (III) may include those shown by the following structural formulas. The compounds represented by the formula (III), for example, may be synthesized through the following reaction scheme. R₄ and R₅ are the same as defined above. Specific examples of the compounds represented by the above-mentioned general formula (IV) may include those shown by the following structural formulas. Representative examples of synthesis of the compound represented by the general formula (IV) are shown below. Synthesis Example 5 (Synthesis of Compound Example No. 4-4) 1.0 g (2.94 mmol) of 5-dodecyl-2-(4′-hydroxyphenyl)pyrimidine was dissolved in 4 ml of toluene and 4 ml of pyrimidine. To the solution was gradually added dropwise a solution of 0.55 g of trans-4-n-propylcyclohexanecarbonyl chloride (mfd. by Kanto Kagaku K.K.) in 4 ml of toluene below 5 °C on an iced water bath. After the addition, the mixture was stirred for 12 hours at room temperature and then injected into 100 ml of iced water, followed by acidification with 6N-hydrochloric acid, extraction with benzene and successive washing with water, 5 %-sodium bicarbonate aqueous solution and water. After drying with magnesium sulfate, the solvent was distilled off to obtain a cream-colored crude product, which was purified by column chromatography and recrystallized from a solvent mixture of ethanol/ethyl acetate, whereby 0.94 g of a white objective product. (Yield: 64.8 %) Phase transition temperature (°C): Synthesis Example 6 (Synthesis of Compound Example No. 4-72) (I) 10 g (53.6 mmol) of trans-4-n-propylcyclohexanecarbonyl chloride was dissolved in 30 ml of ethanol, and a small amount of triethylamine was added thereto, followed by 10 hours of stirring at room temperature. The reaction mixture was injected into 100 ml of iced water, acidified with 6N-hydrochloric acid aqueous solution and extracted with isopropyl ether. The organic layer was repeatedly washed with water until the washing liquid became neutral and then dried with magnesium sulfate. After distilling off the solvent, the product was purified by silica gel column chromatography to obtain 9.9 g of trans-4-n-propylcyclohexanecarboxylic acid-ethyl-ester. (II) 0.73 g (19.1 mmol) of aluminum lithium hydride was added to 30 ml of dry ether and subjected to 1 hour of heat-refluxing. After cooling to about 10 °C on an iced water bath, a solution of 5 g (25.5 mmol) of the trans-4-n-propylcyclohexanecarboxylic acid-ethyl-ester was gradually added dropwise thereto. After the addition, the mixture was stirred for 1 hour at room temperature and heat-refluxed for 1 hour. The product was treated with ethyl acetate and 6N-hydrochloric acid aqueous solution and then injected into 200 ml of iced water. After extraction with isopropyl ether, the organic layer was successively washed with water, aqueous sodium hydroxide solution and water and then dried with magnesium sulfate. After distilling off the solvent, the product was purified by silica gel column chromatography to obtain 3.5 g of trans-4-n-propylcyclohexylmethanol. (III) 3.4 g (22.4 mmol) of the trans-4-n-propylcyclohexylmethanol was dissolved in 20 ml of pyridine. To the solution was added dropwise 5.3 g of p-toluenesulfonyl chloride dissolved in 20 ml of pyridine while being cooled below 5 °C on an iced water bath. After 10 hours of stirring at room temperature, the reaction mixture was injected into 200 ml of iced water, acidified with 6N-hydrochloric acid aqueous solution and then extracted with isopropyl ether. The organic layer was repeatedly washed with water until the washing liquid became neutral and then dried with magnesium sulfate. After distilling off the solvent, trans-4-propylcyclohexylmethyl-p-toluenesulfonate was obtained. (IV) 6.3 g (20.2 mmol) of 5-decyl-2-(4′-hydroxyphenyl)pyrimidine was dissolved in 40 ml of dimethylformamide, and 1.5 g of 85 %-potassium hydroxide was added thereto, followed by 1 hour of stirring at 100 °C. to the mixture was further added 6.9 g of trans-4-n-propylcyclohexylmethyl-p-toluenesulfonate, followed by 4 hours of stirring at 100 °C. After the reaction, the reaction product was injected into 200 ml of iced water and extracted with benzene. The organic layer was washed with water and dried with magnesium sulfate. After distilling off the solvent, the product was purified by silica gel column chromatography and recrystallized from an ethanol/ethyl acetate mixture solvent to obtain the above-mentioned Example Compound No. 4-72. IR (cm⁻¹) 2920, 2840, 1608, 1584, 1428, 1258, 1164, 800 Phase transition temperature (°C) wherein Sm2 denotes a smectic phase (un-identified) other than SmA and SmC. Further, in case where Z₂ is a single bond, the compound, for example, represented by the following formula: may be synthesized along the following reaction scheme. In a preferred embodiment, the ferroelectric chiral smectic liquid crystal composition according to the present invention further comprises a mesomorphic compound having a negative dielectric anisotropy, which is preferably selected from those represented by the following formulas (V-1) to (V-5): wherein Ra and Rb respectively denote a linear or branched alkyl group capable of having a substituent; Xa and Xd respectively denote a single bond, -O-, or Xb and Xc respectively denote a single bond, or -CH₂CH₂-; Aa and Ab respectively denote a single bond, or with proviso that when Aa and Ab are both single bonds, Xb and Xc are both single bonds, and Xa and Xd are both single bonds or -O-, or Xa is and Xd is and Ya and Yb are respectively cyano group, halogen or hydrogen with proviso that Ya and Yb cannot be hydrogen simultaneously; wherein Re and Rf respectively denote a linear or branched alkyl group capable of having a substituent; Xe and Xh are respectively a single bond, -O-, or Xf and Xg are respectively or a single bond; and Ae and Af are respectively or a single bond with proviso that Ae and Af cannot be a single bond simultaneously; wherein Ai is a single bond or Aj is a single bond, or Ri and Rj are respectively a linear or branched alkyl group capable of having a substituent with proviso that Ri and Rj are linear alkyl groups when Aj is a single bond; Z₃ is -O- or -S-; Xi and Xk are respectively a single bond, -O-, or Xj is a single bond, -CH₂O- or -OCH₂- with proviso that Xi is a single bond when Ai is a single bond, Xj is not a single bond when Aj is or and Xk is a single bond when Aj is a single bond; wherein Rl and Rm are respectively a linear or branched alkyl group capable of having a substituent; Al and Am are respectively a single bond, or with proviso that Al and Am cannot be a single bond simultaneously; Xl is a single bond, -O-, or and Xm is a single bond, -CH₂O-, -OCH₂-, -CH₂CH₂- or -C≡C-; wherein Rn and Ro are respectively a linear or branched alkyl group capable of having a substituent; Xn and Xq are respectively a single bond, -O-, or Xo and Xp are respectively a single bond, -CH₂O-, -OCH₂- or -CH₂CH₂-; An and Ap are respectively a single bond, or Ao is or and Z₄ is or In the above formulas (V-1) to (V-5), the alkyl groups Ra - Ro may respectively have 1 - 18 carbon atoms, preferably 4 - 16 carbon atoms, further preferably 6 - 12 carbon atoms. Specific examples of mesomorphic compounds represented by the general formulas (V-1) to (V-5) may respectively include those denoted by the structural formulas shown below. Formula (V-1) Formula (V-2) Formula (V-3) Formula (V-4) Formula (V-5) The mesomorphic compound having a negative dielectric anisotropy Δε may preferably have Δε < -2, preferably Δε < -5, further preferably Δε < -10. The liquid crystal composition according to the present invention may be obtained by mixing at least one species of the compound represented by the formula (II), at least one species of the compound represented by the formula (III), at least one species of the compound represented by any of the formulas (I) and (IV), optionally at least one species of a mesomorphic compound having a negative dielectric anisotropy, and another mesomorphic compound in appropriate proportions. The compounds of the formulas (I) and (IV) can be used in combination. The liquid crystal composition according to the present invention may preferably be formulated as a ferroelectric liquid crystal composition, particularly a ferroelectric chiral smectic liquid crystal composition. Specific examples of another mesomorphic compound as described above may include those denoted by the following structure formulas. In formulating the liquid crystal composition according to the present invention, it is desirable to mix 1 - 300 wt. parts each, preferably 2 - 100 wt. parts each, of a compound represented by the formula (II), a compound represented by the formula (III) and a compound represented by either the formula (I) or (IV) with 100 wt. parts of another mesomorphic compound as mentioned above which can be composed of two or more species. Further, when two or more species of either one or two or all of the compounds represented by the formulas (II), (III) and either (I) or (IV) are used, the two or more species of the compound of the formula (II), (III), (I) or (IV) may be used in a total amount of 1 - 500 wt. parts, preferably 2 - 100 wt. parts, per 100 wt. parts of another mesomorphic compound as described above which can be composed of two or more species. Further, the weight ratio of the compound of the formula (II)/the compound of the formula (III)/the compound of either the formula (I) or (IV) may desirably be 1-300/1-300/1-300, preferably 1-50/1-50/1-50. When two or more species each of the compounds of the formulas (II), (III) and (I) or (IV) are used, the weight ratio of the total amount of the compounds of the formula (II)/the total amounts of the compounds of the formula (III)/the total amounts of the compounds of the formula (I) or (IV) may desirably be 1-500/1-500/1-500, preferably 1-50/1-50/1-50. Further, the total amounts of the compounds of the formulas (II), (III) and (I) or (IV) may desirably be 3 - 90 wt. parts, preferably 6 - 300 wt. parts, when one species each is selected from the formulas (II), (III) and either (I) or (IV), or 3 - 1500 wt. parts, preferably 6 - 300 wt. parts, when two or more species are selected from at least one of the formulas (II), (III) and either (I) or (IV), respectively, with respect to 100 wt. parts of the above-mentioned another mesomorphic compound which may be composed of two or more species. Further, a mesomorphic compound having a negative dielectric anisotropy as described above can be contained in a proportion of 1 - 97 wt. % of the liquid crystal composition of the present invention so as to provide a composition having a negative dielectric anisotropy. Particularly, when a mesomorphic compound having Δε < -2 is used, it may be contained in a proportion of 1 - 70 wt. %, preferably 1 - 50 wt. %, of the liquid crystal composition of the present invention. Further, the total of the compounds of the formulas (II), (III) and either (I) or (IV) and the mesomorphic compound having a negative dielectric anisotropy can constitute 4 - 100 wt. % of the liquid crystal composition of the present invention. The ferroelectric liquid crystal device according to the present invention may preferably be prepared by heating the liquid crystal composition prepared as described above into an isotropic liquid under vacuum, filling a blank cell comprising a pair of oppositely spaced electrode plates with the composition, gradually cooling the cell to form a liquid crystal layer and restoring the normal pressure. Figure 1 is a schematic sectional view of an embodiment of the ferroelectric liquid crystal device prepared as described above for explanation of the structure thereof. Referring to Figure 1, the ferroelectric liquid crystal device includes a ferroelectric liquid crystal layer 1 disposed between a pair of glass substrates 2 each having thereon a transparent electrode 3 and an insulating alignment control layer 4. Lead wires 6 are connected to the electrodes so as to apply a driving voltage to the liquid crystal layer 1 from a power supply 7. Outside the substrates 2, a pair of polarizers 8 are disposed so as to modulate incident light I₀ from a light source 9 in cooperation with the liquid crystal 1 to provide modulated light I. Each of two glass substrates 2 is coated with a transparent electrode 3 comprising a film of In₂O₃, SnO₂ or ITO (indium-tin-oxide) to form an electrode plate. Further thereon, an insulating alignment control layer 4 is formed by rubbing a film of a polymer such as polyimide with gauze or acetate fiber-planted cloth so as to align the liquid crystal molecules in the rubbing direction. Further, it is also possible to compose the alignment control layer of two layers, e.g., by first forming an insulating layer of an inorganic material, such as silicon nitride, silicon nitride containing hydrogen, silicon carbide, silicon carbide containing hydrogen, silicon oxide, boron nitride, boron nitride containing hydrogen, cerium oxide, aluminum oxide, zirconium oxide, titanium oxide, or magnesium fluoride, and forming thereon an alignment control layer of an organic insulating material, such as polyvinyl alcohol, polyimide, polyamide-imide, polyester-imide, polyparaxylylene, polyester, polycarbonate, polyvinyl acetal, polyvinyl chloride, polyvinyl acetate, polyamide, polystyrene, cellulose resin, melamine resin, urea resin, acrylic resin, or photoresist resin. Alternatively, it is also possible to use a single layer of inorganic insulating alignment control layer or organic insulating alignment control layer. An inorganic insulating alignment control layer may be formed by vapor deposition, while an organic insulating alignment control layer may be formed by applying a selection of an organic insulating material or a precursor thereof in a concentration of 0.1 to 20 wt. %, preferably 0.2 - 10 wt. %, by spinner coating, dip coating, screen printing, spray coating or roller coating, followed by curing or hardening under prescribed hardening condition (e.g., by heating). The insulating alignment control layer may have a thickness of ordinarily 30 Å - 1 micron, preferably 30 - 3000 Å, further preferably 50 - 1000 Å. The two glass substrates 2 with transparent electrodes 3 (which may be inclusively referred to herein as "electrode plates") and further with insulating alignment control layers 4 thereof are held to have a prescribed (but arbitrary) gap with a spacer 5. For example, such a cell structure with a prescribed gap may be formed by sandwiching spacers of silica beads or alumina beads having a prescribed diameter with two glass plates, and then sealing the periphery thereof with, e.g., an epoxy adhesive. Alternatively, a polymer film or glass fiber may also be used as a spacer. Between the two glass plates, a ferroelectric liquid crystal is sealed up to provide a ferroelectric liquid crystal layer 1 in a thickness of generally 0.5 to 20 microns, preferably 1 to 5 microns. The ferroelectric liquid crystal provided by the composition of the present invention may desirably assume a SmC* phase (chiral smectic C phase) in a wide temperature range including room temperature (particularly, broad in a lower temperature side) and also shows wide drive voltage margin and drive temperature margin when contained in a device. Particularly, in order to show a good alignment characteristic to form a uniform monodomain, the ferroelectric liquid crystal may show a phase transition series comprising isotropic phase - Ch phase (cholesteric phase) - SmA phase (smectic A phase) - SmC* phase (chiral smectic C phase) on temperature decrease. The transparent electrodes 3 are connected to the external power supply 7 through the lead wires 6. Further, outside the glass substrates 2, polarizers 8 are applied. The device shown in Figure 1 is of a transmission type and is provided with a light source 9. Figure 2 is a schematic illustration of a ferroelectric liquid crystal cell (device) for explaining operation thereof. Reference numerals 21a and 21b denote substrates (glass plates) on which a transparent electrode of, e.g., In₂O₃, SnO₂, ITO (indium-tin-oxide), etc., is disposed, respectively. A liquid crystal of an SmC*-phase (chiral smectic C phase) in which liquid crystal molecular layers 22 are aligned perpendicular to surfaces of the glass plates is hermetically disposed therebetween. Full lines 23 show liquid crystal molecules. Each liquid crystal molecule 23 has a dipole moment (P ⊥ ) 24 in a direction perpendicular to the axis thereof. The liquid crystal molecules 23 continuously form a helical structure in the direction of extension of the substrates. When a voltage higher than a certain threshold level is applied between electrodes formed on the substrates 21a and 21b, a helical structure of the liquid crystal molecule 23 is unwound or released to change the alignment direction of respective liquid crystal molecules 23 so that the dipole moments (P ⊥ ) 24 are all directed in the direction of the electric field. The liquid crystal molecules 23 have an elongated shape and show refractive anisotropy between the long axis and the short axis thereof. Accordingly, it is easily understood that when, for instance, polarizers arranged in a cross nicol relationship, i.e., with their polarizing directions crossing each other, are disposed on the upper and the lower surfaces of the glass plates, the liquid crystal cell thus arranged functions as a liquid crystal optical modulation device of which optical characteristics vary depending upon the polarity of an applied voltage. Further, when the liquid crystal cell is made sufficiently thin (e.g., less than about 10 microns), the helical structure of the liquid crystal molecules is unwound to provide a non-helical structure even in the absence of an electric field, whereby the dipole moment assumes either of the two states, i.e., Pa in an upper direction 34a or Pb in a lower direction 34b as shown in Figure 3, thus providing a bistable condition. When an electric field Ea or Eb higher than a certain threshold level and different from each other in polarity as shown in Figure 3 is applied to a cell having the above-mentioned characteristics, the dipole moment is directed either in the upper direction 34a or in the lower direction 34b depending on the vector of the electric field Ea or Eb. In correspondence with this, the liquid crystal molecules are oriented in either of a first stable state 33a and a second stable state 33b. When the above-mentioned ferroelectric liquid crystal is used as an optical modulation element, it is possible to obtain two advantages. First is that the response speed is quite fast. Second is that the orientation of the liquid crystal shows bistability. The second advantage will be further explained, e.g., with reference to Figure 3. When the electric field Ea is applied to the liquid crystal molecules, they are oriented in the first stable state 33a. This state is stably retained even if the electric field is removed. On the other hand, when the electric field Eb of which direction is opposite to that of the electric field Ea is applied thereto, the liquid crystal molecules are oriented to the second stable state 33b, whereby the directions of molecules are changed. This state is similarly stably retained even if the electric field is removed. Further, as long as the magnitude of the electric field Ea or Eb being applied is not above a certain threshold value, the liquid crystal molecules are placed in the respective orientation states. When such a ferroelectric liquid crystal device comprising a ferroelectric liquid crystal composition as described above between a pair of electrode plates is constituted as a simple matrix display device, the device may be driven by a driving method as disclosed in Japanese Laid-Open Patent Applications (KOKAI) Nos. 193426/1984, 193427/1984, 156046/1985, 156047/1985, etc. Hereinbelow, the present invention will be explained more specifically with reference to examples. It is however to be understood that the present invention is not restricted to these examples. Example 1 A liquid crystal composition 1-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 1-B was prepared by mixing the following example compounds in the respectively indicated proportions with the above prepared composition 1-A. The above-prepared liquid crystal composition 1-B was used to prepare a liquid crystal device in combination with a blank cell prepared in the following manner. Two 1.1 mm-thick glass plates were provided and respectively coated with an ITO film to form an electrode for voltage application, which was further coated with an insulating layer of vapor-deposited SiO₂. The insulating layer was further coated with a 1.0 %-solution of polyimide resin precursor (SP-710, available from Toray K.K.) in dimethylacetamide by a spinner coater rotating at 2500 rpm for 15 seconds. Thereafter, the coating film was subjected to heat curing at 300 °C for 60 min. to obtain about 200 Å-thick film. The coating film was rubbed with acetate fiber-planted cloth. The thus treated two glass plates were washed with isopropyl alcohol. After silica beads with an average particle size of 1.5 microns were dispersed on one of the glass plates, the two glass plates were applied to each other with a bonding sealing agent (Lixon Bond, available from Chisso K.K.) so that their rubbed directions were parallel to each other and heated at 100 °C for 60 min. to form a blank cell. The cell gap was found to be about 1.5 microns as measured by a Berek compensator. Then, the above-prepared liquid crystal composition 1-B was heated into an isotropic liquid, and injected into the above prepared cell under vacuum and, after sealing, was gradually cooled at a rate of 20 °C/hour to 25 °C to prepare a ferroelectric liquid crystal device. The ferroelectric liquid crystal device was subjected to measurement of an optical response time (time from voltage application until the transmittance change reaches 90 % of the maximum) at specified temperatures under the application of a peak-to-peak voltage Vpp of 25 volts. The results are shown below. 10 °C 25 °C 40 °C Response time 964 µsec 338 µsec 127 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage applicationi was also good. Comparative Example 1 A liquid crystal composition 1-C was prepared by omitting Example compounds Nos. 1-23, 1-106 and 1-148 from the liquid crystal composition 1-B, i.e., by adding only Example compounds Nos. 2-2 and 3-27 to the liquid crystal composition 1-A, a liquid crystal composition 1-D was prepared by omitting Example compound No. 2-2 from the composition 1-B, i.e., by adding only Example compounds Nos. 1-23, 1-106, 1-148 and 3-27 to the composition 1-A, and a liquid crystal composition 1-E was prepared by omitting Example compound No. 3-27 from the composition 1-B, i.e., by adding only Example compounds Nos. 1-23, 1-106, 1-148 and 2-2 to the composition 1-A. Ferroelectric liquid crystal devices 1-A, 1-C 1-D and 1-E were prepared by using the compositions 1-A, 1-C, 1-D and 1-E, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 1-A 1410 µsec 435 µsec 155 µsec 1-C 1012 µsec 348 µsec 130 µsec 1-D 1131 µsec 378 µsec 136 µsec 1-E 997 µsec 345 µsec 129 µsec As apparent from the above Example 1 and Comparative Example 1, the ferroelectric liquid crystal device containing the liquid crystal composition 1-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed (ratio of response time (10 °C/40 °C)). Example 2 A liquid crystal composition 2-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 1-A prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 2-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 711 µsec 240 µsec 92 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 2 A liquid crystal composition 2-C was prepared by adding only Example compounds Nos. 1-57, 1-80, 1-141 and 3-24 and without adding Example compound No. 2-28 to the composition 1-A. Ferroelectric liquid crystal devices were prepared by using the compositions 2-C and 1-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 1-A 1410 µsec 435 µsec 155 µsec 2-C 1175 µsec 384 µsec 136 µsec As apparent from the above Example 2 and Comparative Example 2, the ferroelectric liquid crystal device containing the liquid crystal composition 2-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 3 A liquid crystal composition 3-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 1-A prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 3-B was used, and the device was subjected to measurement of driving voltage margin and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 763 µsec 266 µsec 98 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 3 A liquid crystal composition 3-C was prepared by adding only Example compounds Nos. 1-73, 1-118, 3-36 and 3-41 and without adding Example compound No. 2-63 to the composition 1-A. Ferroelectric liquid crystal devices were prepared by using the compositions 3-C and 1-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 1-A 1410 µsec 435 µsec 155 µsec 3-C 1080 µsec 372 µsec 139 µsec As apparent from the above Example 3 and Comparative Example 3, the ferroelectric liquid crystal device containing the liquid crystal composition 3-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 4 A liquid crystal composition 4-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 4-B was prepared by mixing the following example compounds in the respectively indicated proportions with the above prepared compositions 4-A A ferroelectric liquid crystal device 4-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 4-B was used instead of the composition 1-B. The device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 837 µsec 292 µsec 114 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. Comparative Example 4 A liquid crystal composition 4-C was prepared by adding only Example compounds Nos. 2-2 and 3-27 and without adding Example compound No. 1-23, 1-148 or 1-106 to the composition 4-A; a liquid crystal composition 4-D was prepared by adding only Example compounds Nos. 1-23, 1-148, 1-106 and 3-27 and without adding Example compound No. 2-2 to the composition 4-A; and a liquid crystal composition 4-E was prepared by adding only Example compounds Nos. 1-23, 1-148, 1-106 and 2-2 and without adding Example compound No. 3-27 to the composition 4-A. Ferroelectric liquid crystal devices were prepared by using the compositions 4-C, 4-D, 4-E and 4-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 4-A 1260 µsec 374 µsec 137 µsec 4-C 936 µsec 322 µsec 120 µsec 4-D 1072 µsec 359 µsec 132 µsec 4-E 872 µsec 303 µsec 117 µsec As apparent from the above Example 4 and Comparative Example 4, the ferroelectric liquid crystal device containing the liquid crystal composition 4-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 5 A liquid crystal composition 5-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 4-A prepared in Example 4. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 5-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 815 µsec 285 µsec 111 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 5 A liquid crystal composition 5-C was prepared by adding only Example compound No. 2-53 and without adding Example compound No. 1-12, 1-14, 1-72 or 3-49 to the composition 4-A. Ferroelectric liquid crystal devices were prepared by using the compositions 5-C and 4-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 4-A 1260 374 137 5-C 869 300 113 As apparent from the above Example 5 and Comparative Example 5, the ferroelectric liquid crystal device containing the liquid crystal composition 5-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 6 A liquid crystal composition 6-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 4-B prepared in Example 4. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 6-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 682 µsec 244 µsec 93 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 6 A liquid crystal composition 6-C was prepared by adding only Example compounds Nos. 1-97, 1-138 and 1-140 and without adding Example compound No. 2-12 or 3-42 to the composition 4-A. Ferroelectric liquid crystal devices were prepared by using the compositions 6-C and 4-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 4-A 1260 µsec 374 µsec 137 µsec 6-C 1044 µsec 357 µsec 132 µsec As apparent from the above Example 6 and Comparative Example 6, the ferroelectric liquid crystal device containing the liquid crystal composition 6-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 7 A liquid crystal composition 7-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 7-B was prepared by mixing the following example compounds in the respectively indicated proportions with the above prepared composition 7-A. A ferroelectric liquid crystal device 7-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 7-B was used instead of the composition 1-B. The device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 580 µsec 219 µsec 89 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application application was also good. Comparative Example 7 A liquid crystal composition 7-C was prepared by adding only Example compounds Nos. 1-23, 1-106, 1-148 and 3-27 and without adding Example compound No. 3-2 to the composition 7-A. Ferroelectric liquid crystal devices were prepared by using the compositions 7-C and 7-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 7-A 872 285 115 7-C 759 205 108 As apparent from the above Example 7 and Comparative Example 7, the ferroelectric liquid crystal device containing the liquid crystal composition 7-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 8 A liquid crystal composition 8-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 7-A prepared in Example 7. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 8-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 527 µsec 198 µsec 82 µsec Further, a contrast of 12 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 8 A liquid crystal composition 8-C was prepared by adding only Example compounds Nos. 2-53 and 3-49 and without adding Example compound No. 1-21, 1-46 or 1-72 to the composition 7-A. Ferroelectric liquid crystal devices were prepared by using the compositions 8-C and 7-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 7-A 872 285 115 8-C 583 211 83 As apparent from the above Example 8 and Comparative Example 8, the ferroelectric liquid crystal device containing the liquid crystal composition 8-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 9 A liquid crystal composition 9-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 7-A prepared in Example 7. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 9-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 485 µsec 185 µsec 77 µsec Further, a contrast of 12 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 9 A liquid crystal composition 9-C was prepared by adding only Example compounds Nos. 3-21 and 3-33 and without adding Example compound No. 1-7, 1-38, 2-78 or 2-20 to the composition 7-A. Ferroelectric liquid crystal devices were prepared by using the compositions 9-C and 7-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 7-A 872 µsec 285 µsec 115 µsec 9-C 835 µsec 280 µsec 116 µsec As apparent from the above Example 9 and Comparative Example 9, the ferroelectric liquid crystal device containing the liquid crystal composition 9-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Examples 10 - 17 Liquid crystal compositions 10-B to 17-B were prepared by replacing the example compounds and the liquid crystal compositions used in Examples 1, 4 and 7 with example compounds and liquid crystal compositions shown in the following Table 1. Ferroelectric liquid crystal devices were prepared by respectively using these compositions instead of the composition 1-B, and subjected to measurement of optical response time and observation of switching states. In the devices, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown in the following Table 1. As is apparent from the results shown in the following Table 1, the ferroelectric liquid crystal devices containing the liquid crystal compositions 10-B to 17-B provided improved response speed and a decreased temperature dependence of the response speed. Example 18 A liquid crystal composition 18-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 18-B was prepared by mixing the following example compounds in the respectively indicated proportions with the above prepared compositin 18-A. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 18-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 825 µsec 284 µsec 107 µsec Further, a contrast of 12 was attained at 25 °C during the driving, and a clear switching function was voltage application was also good. Comparative Example 18 A liquid crystal composition 18-C was prepared by adding only Example compounds Nos. 2-42 and 3-23 and without adding Example compound No. 4-5 or 4-73 to the composition 18-A; a liquid crystal composition 18-D was prepared by adding only Example compounds Nos. 4-5, 4-73 and 2-42 and without adding Example compound No. 2-42 to the composition 18-A; and a liquid crystal composition 18-E was prepared by adding only Example compounds Nos. 4-5, 4-73 and 2-42 and without adding Example compound No. 3-23 to the composition 18-A. Ferroelectric liquid crystal devices were prepared by using the compositions 18-C, 18-D and 18-E and 18-A, respectively, instead of the composition 18-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 18. The results are shown below. Response time 10 °C 25 °C 40 °C 18-A 1360 µsec 430 µsec 147 µsec 18-C 936 µsec 322 µsec 117 µsec 18-D 1164 µsec 369 µsec 128 µsec 18-E 871 µsec 298 µsec 110 µsec As apparent from the above Example 18 and Comparative Example 18, the ferroelectric liquid crystal device containing the liquid crystal composition 18-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 19 A liquid crystal composition 19-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 18-A prepared in Example 18. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 19-B was used, and the device was subjected to measurement of driving voltage margin and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 757 µsec 263 µsec 100 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 19 A liquid crystal composition 19-C was prepared by adding only Example compounds Nos. 4-10, 4-151 and 3-7 and without adding Example compound No. 2-32 or 2-14 to the composition 18-A. Ferroelectric liquid crystal devices were prepared by using the compositions 19-C and 18-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 18-A 1360 µsec 430 µsec 147 µsec 19-C 1183 µsec 384 µsec 134 µsec As apparent from the above Example 19 and Comparative Example 19, the ferroelectric liquid crystal device containing the liquid crystal composition 19-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 20 A liquid crystal composition 20-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 18-A prepared in Example 18. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 20-B was used, and the device was subjected to measurement of driving voltage margin and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 719 µsec 249 µsec 91 µsec Further, a contrast of 14 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 20 A liquid crystal composition 20-C was prepared by adding only Example compounds Nos. 4-115, 4-147, 3-42 and 3-50 and without adding Example compound No. 2-6 to the composition 18-A. Ferroelectric liquid crystal devices were prepared by using the compositions 20-C and 18-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 18-A 1360 µsec 430 µsec 147 µsec 20-C 1007 µsec 339 µsec 118 µsec As apparent from the above Example 20 and Comparative Example 20, the ferroelectric liquid crystal device containing the liquid crystal composition 20-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 21 A liquid crystal composition 21-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 21-B was prepared by mixing the following example compounds in the respectively indicated proportions with the above prepared compositions 21-A. A ferroelectric liquid crystal device 21-B was prepared in the same manner as in Example 1 except that the liquid crystal composition 21-B was used instead of the composition 1-B. The device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 743 µsec 264 µsec 102 µsec Further, a contrast of 12 was attained at 25 °C during the driving, and a clear switching function was observed. Comparative Example 21 A liquid crystal composition 21-C was prepared by adding only Example compounds Nos. 2-42 and 3-23 and without adding Example compound No. 4-5 or 4-73 to the composition 21-A; a liquid crystal composition 21-D was prepared by adding only Example compounds Nos. 4-5, 4-73 and 3-23 and without adding Example compound No. 2-42 to the composition 21-A; and a liquid crystal composition 21-E was prepared by adding only Example compounds Nos. 4-5, 4-73 and 2-42 and without adding Example compound No. 3-23 to the composition 21-A. Ferroelectric liquid crystal devices were prepared by using the compositions 21-C, 21-D, 21-E and 21-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 21-A 1155 µsec 362 µsec 133 µsec 21-C 820 µsec 284 µsec 104 µsec 21-D 1004 µsec 326 µsec 115 µsec 21-E 801 µsec 283 µsec 108 µsec As apparent from the above Example 21 and Comparative Example 21, the ferroelectric liquid crystal device containing the liquid crystal composition 21-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 22 A liquid crystal composition 22-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 21-A prepared in Example 21. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 22-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 827 µsec 292 µsec 112 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 22 A liquid crystal composition 22-C was prepared by adding only Example compounds Nos. 2-36 and 2-72 and without adding Example compound No. 4-69, 4-105 or 3-38 to the composition 21-A. Ferroelectric liquid crystal devices were prepared by using the compositions 22-C and 21-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 21-A 1155 362 133 22-C 905 303 110 As apparent from the above Example 22 and Comparative Example 22, the ferroelectric liquid crystal device containing the liquid crystal composition 22-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 23 A liquid crystal composition 23-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 21-A prepared in Example 21. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 23-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 724 µsec 260 µsec 101 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 23 A liquid crystal composition 23-C was prepared by adding only Example compounds Nos. 4-11 and 4-34 and without adding Example compound No. 2-21, 2-2 or 3-60 to the composition 21-A. Ferroelectric liquid crystal devices were prepared by using the compositions 23-C and 21-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 21-A 1155 µsec 362 µsec 133 µsec 23-C 1004 µsec 344 µsec 127 µsec As apparent from the above Example 23 and Comparative Example 23, the ferroelectric liquid crystal device containing the liquid crystal composition 23-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 24 A liquid crystal composition 24-A was prepared by mixing the following compounds in respectively indicated proportions. A liquid crystal composition 24-B was prepared by mixing the following example compounds in the respectively indicated proportions with the above prepared composition 24-A. A ferroelectric liquid crystal device 24-B was prepared in same manner as in Example 1 except that the liquid crystal composition 24-B was used instead of the composition 1-B. The device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 542 µsec 201 µsec 83 µsec Further, a contrast of 14 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application application was also good. Comparative Example 24 A liquid crystal composition 24-C was prepared by adding only Example compounds Nos. 4-5, 4-73 and 3-23 and without adding Example compound No. 2-42 to the composition 24-A. Ferroelectric liquid crystal devices were prepared by using the compositions 24-C and 24-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 24-A 762 246 98 24-C 663 235 91 As apparent from the above Example 24 and Comparative Example 24, the ferroelectric liquid crystal device containing the liquid crystal composition 24-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 25 A liquid crystal composition 25-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 24-A prepared in Example 24. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 25-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 529 µsec 196 µsec 82 µsec Further, a contrast of 12 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 25 A liquid crystal composition 25-C was prepared by adding only Example compounds Nos. 2-36, 2-72 and 3-38 and without adding Example compound No. 4-69 or 4-105 to the composition 24-A. Ferroelectric liquid crystal devices were prepared by using the compositions 25-C and 24-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 24-A 762 246 98 25-C 563 202 81 As apparent from the above Example 25 and Comparative Example 25, the ferroelectric liquid crystal device containing the liquid crystal composition 25-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Example 26 A liquid crystal composition 26-B was prepared by mixing the following example compounds in the indicated proportions with the liquid crystal composition 24-A prepared in Example 24. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition 26-B was used, and the device was subjected to measurement of optical response time and observation of switching states. In the device, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown below. 10 °C 25 °C 40 °C Response time 423 µsec 162 µsec 66 µsec Further, a contrast of 13 was attained at 25 °C during the driving, and a clear switching function was observed. The bistability after termination of the voltage application was also good. Comparative Example 26 A liquid crystal composition 26-C was prepared by adding only Example compound No. 3-29 and without adding Example compound No. 4-82, 4-165, 2-77 or 2-12 to the composition 24-A. Ferroelectric liquid crystal devices were prepared by using the compositions 26-C and 24-A, respectively, instead of the composition 1-B, and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. The results are shown below. Response time 10 °C 25 °C 40 °C 24-A 762 µsec 246 µsec 98 µsec 26-C 561 µsec 199 µsec 78 µsec As apparent from the above Example 26 and Comparative Example 26, the ferroelectric liquid crystal device containing the liquid crystal composition 26-B according to the present invention provided improved response speed and operation characteristic at a lower temperature and also provided a descreased temperature dependence of response speed. Examples 27 - 33 Liquid crystal compositions 27-B to 33-B were prepared by replacing the example compounds and the liquid crystal compositions used in Examples 18, 21 and 24 with example compounds and liquid crystal compositions shown in the following Table 2. Ferroelectric liquid crystal devices were prepared by respectively using these compositions instead of the composition 1-B, and subjected to measurement of optical response time and observation of switching states. In the devices, a monodomain with a good and uniform alignment characteristic was observed. The results of the measurement are shown in the following Table 2. As is apparent from the results shown in the above Table 2, the ferroelectric liquid crystal devices containing the liquid crystal compositions 27-B to 33-B provided improved response speed and a decreased temperature dependence of the response speed. Example 34 A liquid crystal composition 34-B was prepared by mixing the following example compound in the indicated proportion with the liquid crystal composition 1-B prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition was used, and the device was subjected to measurement of optical response time in the same manner as in Example 1 to obtain the following results. Response time 10 °C 25 °C 40 °C 1211 µsec 407 µsec 146 µsec Then, the tilt angle of the above device was measured under right-angle cross nicols at 25 °C to provide 7.3 degrees. Further, the tilt angle of the device was again measured while being subjected to application of rectangular waveforms of ±8 V and a frequency of 60 KHz and found to be 13.3 degrees. The transmittance measured at that time was 12.8%, and a contrast of 53:1 was attained. Comparative Example 34 A liquid crystal composition 34-C was prepared in the same manner as in Example 34 except that the liquid crystal composition 1-A prepared in Example 1 was used instead of the composition 1-B to be mixed with the example compound No. 5-10 in the same proportions. Ferroelectric liquid crystal devices were prepared by using the compositions 34-C, 1-A and 1-B respectively and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. Further, the tilt angles of these devices were measured in the same manner as in Example 34. The results are shown below. Response time 10 °C 25 °C 40 °C 1-A 1410 µsec 435 µsec 155 µsec 1-B 964 µsec 338 µsec 127 µsec 34-C 1830 µsec 550 µsec 178 µsec Tilt angle (25 °C) Comp. Initial (no electric field) Under AC appln. (60 KHz, ±8 V, rectangular) 1-A 7.6 degrees 8.0 degrees 1-B 7.5 degrees 7.7 degrees 34-C 7.5 degrees 13.6 degrees As apparent from Example 34 and Comparative Example 34, the liquid crystal composition 34-B obtained by mixing a mesomorphic compound having a negative dielectric anisotropy (example compound No. 5-10) with the liquid crystal composition 1-B according to the present invention provided an improved response characteristic and also provided a remarkably improved display characteristic when used in a display method utilizing AC application (or AC stabilization). Example 35 A liquid crystal composition 35-B was prepared by mixing the following example compounds in the respectively indicated proportions with the liquid crystal composition 1-B prepared in Example 1. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition was used, and the device was subjected to measurement of optical response time in the same manner as in Example 1 to obtain the following results. 10 °C 25 °C 40 °C Response time 1100 µsec 395 µsec 140 µsec Then, the tilt angle of the above device was measured under right-angle cross nicols at 25 °C to provide 8.6 degrees. Further, the tilt angle of the device was again measured while being subjected to application of rectangular waveforms of ±8 V and a frequency of 60 KHz and found to be 12.7 degrees. The transmittance measured at that time was 12.8%, and a contrast of 53:1 was attained. Comparative Example 35 A liquid crystal composition 35-C was prepared in the same manner as in Example 35 except that the liquid crystal composition 1-A prepared in Example 1 was used instead of the composition 1-B to be mixed with the other example compounds in the same proportions. Ferroelectric liquid crystal devices were prepared by using the compositions 35-C, 1-A and 1-B respectively and subjected to measurement of driving voltage margin, otherwise in the same manner as in Example 1. Further, the tilt angles of these devices were measured in the same manner as in Example 35. The results are shown below. Response time 10 °C 25 °C 40 °C 1-A 1410 µsec 435 µsec 155 µsec 1-B 964 µsec 338 µsec 127 µsec 35-C 1805 µsec 538 µsec 190 µsec Tilt angle (25 °C) Comp. Initial (no electric field) Under AC appln. (60 KHz, ±8 V, rectangular) 1-A 7.6 degrees 8.0 degrees 1-B 7.5 degrees 7.7 degrees 35-C 8.0 degrees 12.9 degrees As apparent from Example 35 and Comparative Example 35, the liquid crystal composition 35-B obtained by mixing mesomorphic compounds having a negative dielectric anisotropy with the liquid crystal composition 1-B according to the present invention provided an improved responsive characteristic and also provided a remarkably improved display characteristic when used in a display method utilizing AC application (or AC stabilization). Example 36 A liquid crystal composition 36-B was prepared by mixing the following example compound in the indicated proportion with the liquid crystal composition 18-B prepared in Example 18. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition was used, and the device was subjected to measurement of optical response time in the same manner as in Example 1 to obtain the following results. Response time 10 °C 25 °C 40 °C 1000 µsec 330 µsec 122 µsec Then, the tilt angle of the above device was measured under right-angle cross nicols at 25 °C to provide 7.1 degrees. Further, the tilt angle of the device was again measured while being subjected to application of rectangular waveforms of ±8 V and a frequency of 60 KHz and found to be 13.0 degrees. The transmittance measured at that time was 12.3%, and a contrast of 50:1 was attained. Comparative Example 36 A liquid crystal composition 36-C was prepared in the same manner as in Example 36 except that the liquid crystal composition 18-A prepared in Example 18 was used instead of the composition 18-B to be mixed with the example compound No. 5-10 in the same proportions. Ferroelectric liquid crystal devices were prepared by using the conpositions 36-C, 18-A and 18-B respectively and subjected to measurement of optical response time, otherwise in the same manner as in Example 1. Further, the tilt angles of these devices were measured in the same manner as in Example 36. The results are shown below. Response time 10 °C 25 °C 40 °C 18-A 1360 µsec 430 µsec 147 µsec 18-B 825 µsec 284 µsec 107 µsec 36-C 1785 µsec 530 µsec 170 µsec Tilt angle (25 °C) Comp. Initial (no electric field) Under AC appln. (60 KHz, ±8 V, rectangular) 18-A 7.3 degrees 7.5 degrees 18-B 7.2 degrees 7.3 degrees 36-C 7.0 degrees 13.0 degrees As apparent from Example 36 and Comparative Example 36, the liquid crystal composition 36-B obtained by mixing a mesomorphic compound having a negative dielectric anisotropy (example compound No. 5-10) with the liquid crystal composition 1-B according to the present invention provided an improved response characteristic and also provided a remarkably improved display characteristic when used in a display method utilizing AC application (or AC stabilization). Example 37 A liquid crystal composition 37-B was prepared by mixing the following example compounds in the respectively indicated proportions with the liquid crytal coposition 18-B prepared in Example 18. A ferroelectric liquid crystal device was prepared in the same manner as in Example 1 except that the above liquid crystal composition was used, and the device was subjected to measurement of optical response time in the same manner as in Example 1 to obtain the following results. 10 °C 25 °C 40 °C Response time 930 µsec 320 µsec 118 µsec Then, the tilt angle of the above device was measured under right-angle cross nicols at 25 °C to provide 8.0 degrees. Further, the tilt angle of the device was again measured while being subjected to application of rectangular waveforms of ±8 V and a frequency of 60 KHz and found to be 12.1 degrees. The transmittance measured at that time was 11.9%, and a contrast of 47:1 was attained. Comparative Example 37 A liquid crystal composition 37-C was prepared in the same manner as in Example 37 except that the liquid crystal composition 18-A prepared in Example 18 was used instead of the composition 18-B to be mixed with the other example compounds in the same proportions. Ferroelectric liquid crystal devices were prepared by using the compositions 37-C, 18-A and 18-B respectively and subjected to measurement of driving voltage margin, otherwise in the same manner as in Example 1. Further, the tilt angles of these devices were measured in the same manner as in Example 37. The results are shown below. Response time 10 °C 25 °C 40 °C 18-A 1360 µsec 430 µsec 147 µsec 18-B 825 µsec 284 µsec 107 µsec 37-C 1652 µsec 503 µsec 165 µsec Tilt angle (25 °C) Comp. Initial (no electric field) Under AC appln. (60 KHz, ±8 V, rectangular) 18-A 7.3 degrees 7.5 degrees 18-B 7.2 degrees 7.3 degrees 37-C 7.0 degrees 13.0 degrees As apparent from Example 37 and Comparative Example 37, the liquid crystal composition 37-B obtained by mixing mesomorphic compounds having a negative dielectric anisotropy with the liquid crystal composition 18-B according to the present invention provided an improved responsive characteristic and also provided a remarkably improved display characteristic when used in a display method utilizing AC application (or AC stabilization). For example, the dielectric anisotropy Δε of a mesomorphic compound or a liquid crystal composition referred to herein may be measured in the following manner. A 5 micron-thick homogeneous alignment cell having an electrode of 0.7 cm² in area and a homogeneous alignment layer (rubbed polyimide) on both substrates, and a 5 micron-thick homeotropic alignment cell having an electrode of 0.7 cm² in area and a homeotropic alignment layer (aligning agent: "ODS-E" available from Chisso K.K.) on both substrates, are provided. The respective cells are filled with a sample liquid crystal material (compound or composition) to prepare liquid crystal devices. The capacitances of the liquid crystal layers are measured by applying a sine wave with a frequency of 100 KHz and amplitudes of ±0.5 V to the respective devices at a prescribed temperature set for the liquid crystal material, and the dielectric constants ε ∥ and ε ⊥ are obtained from the measured capacitance values of the respective devices, whereby the dielectric anisotropy Δε is calculated by the equation of Δε = ε ∥ - ε ⊥ . Example 38 A blank cell was prepared in the same manner as in Example 1 except for omitting the SiO₂ layer to form an alignment control layer composed of the polyimide resin layer alone on each electrode plate. Five ferroelectric liquid crystal devices were prepared by filling such a blank cell with liquid crystal compositions 18-B, 18-A, 18-C, 18-D and 18-E, respectively, prepared in Example 18 and Comparative Example 18. These liquid crystal devices were subjected to measurement of optical response time in the same manner as in Example 1. The results are shown below. Response time (µsec) 10 °C 25 °C 40 °C 18-B 820 264 92 18-A 1340 415 138 18-C 918 312 112 18-D 1145 349 118 18-E 863 279 104 As is apparent from the above Example 38, also in the case of a different device structure, the device containing the ferroelectric liquid crystal composition 18-B according to the present invention provided improved operation characteristic at a lower temperature and also a decreased temperature dependence of response speed. As described hereinabove, the ferroelectric liquid crystal composition according to the present invention provides a liquid crystal device which shows a good switching characteristic, an improved operation characteristic and a decreased temperature dependence of response speed. Further, the liquid crystal composition according to the present invention further containing a mesomorphic compound having a negative dielectric anisotropy, provides a liquid crystal device which retains the above-mentioned characteristics and further shows a remarkably improved display characteristic when used in a driving method utilizing AC stabilization.

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, GR, IT, LI, LU, NL, SE A ferroelectric chiral smectic liquid crystal composition, comprising: at least one compound represented by the following formula (II): wherein R₃ denotes a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₃ denotes a single bond, -O- or Z₁ denotes a single bond or denotes or and m is 1 - 12; at least one compound represented by the following formula (III): wherein R₄ and R₅ respectively denote an unsubstituted linear or branched alkyl group having 1 - 18 carbon atoms, at least one of R₄ and R₅ being optically active; X₄ denotes a single bond, -O-, or and X₅ denotes a single bond, -O-, or and at least one compound represented by the following formula (I) or (IV): wherein R₁ and R₂ respetively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent of C₁ - C₁₂ alkoxy group; X₁ and X₂ respectively denote a single bond, -O-, or wherein R₆ and R₇ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₆ and X₇ respetively denote a single bond, -O-, or Z₂ denotes -CH₂O-, -OCH₂- or a single bond; and respectively denote or and denotes or with proviso that at least one of and is or A composition according to Claim 1, which further comprises a mesomorphic compound having a negative dielectric anisotropy. A composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -2. A composition according to Claim 3, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -5. A composition according to Claim 4, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -10. A composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy is a mesomorphic compound represented by any of the following formulas (V-1) to (V-5); wherein Ra and Rb respectively denote a linear or branched alkyl group capable of having a substituent; Xa and Xd respectively denote a single bond, -O-, or Xb and Xc respectively denote a single bond, or -CH₂CH₂-; Aa and Ab respectively denote a single bond, or with proviso that when Aa and Ab are both single bonds, Xb and Xc are both single bonds, and Xa and Xd are both single bonds or -O-, or Xa is and Xd is and Ya and Yb are respectively cyano group, halogen or hydrogen with proviso that Ya and Yb cannot be hydrogen simultaneously; wherein Re and Rf respectively denote a linear or branched alkyl group capable of having a substituent; Xe and Xh are respectively a single bond, -O-, or Xf and Xg are respectively or a single bond; and Ae and Af are respectively or a single bond with proviso that Ae and Af cannot be a single bond simultaneously; wherein Ai is a single bond or Aj is a single bond, or Ri and Rj are respectively a linear or branched alkyl group capable of having a substituent with proviso that Ri and Rj are linear alkyl groups when Aj is a single bond; Z₃ is -O- or -S-; Xi and Xk are respectively a single bond, -O-, or Xj is a single bond, -CH₂O- or -OCH₂- with proviso that Xi is a single bond when Ai is a single bond, Xj is not a single bond when Aj is or and Xk is a single bond when Aj is a single bond; wherein Rl and Rm are respectively a linear or branched alkyl group capable of having a substituent; Al and Am are respectively a single bond, or with proviso that Al and Am cannot be a single bond simultaneously; Xl is a single bond, -O-, or and Xm is a single bond, -CH₂O-, -OCH₂-, -CH₂CH₂- or -C≡C-; wherein Rn and Ro are respectively a linear or branched alkyl group capable of having a substituent; Xn and Xq are respectively a single bond, -O-, or Xo and Xp are respectively a single bond, -CH₂O-, -OCH₂- or -CH₂CH₂-; An and Ap are respectively a single bond, or Ao is or and Z₄ is or A liquid crystal device, comprising a pair of electrode plates and a ferroelectric liquid crystal composition according to any one of Claims 1 - 6 disposed between the electrode plates. Claims for the following Contracting State : ES A use of a ferroelectric chiral smectic liquid crystal composition, comprising: at least one compound represented by the following formula (II): wherein R₃ denotes a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₃ denotes a single bond, -O- or Z₁ denotes a single bond or denotes or and m is 1 - 12; at least one compound represented by the following formula (III): wherein R₄ and R₅ respectively denote an unsubstituted linear or branched alkyl group having 1 - 18 carbon atoms, at least one of R₄ and R₅ being optically active; X₄ denotes a single bond, -O-, or and X₅ denotes a single bond, -O-, or and at least one compound represented by the following formula (I) or (IV): wherein R₁ and R₂ respetively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent of C₁ - C₁₂ alkoxy group; X₁ and X₂ respectively denote a single bond, -O-, or wherein R₆ and R₇ respectively denote a linear or branched alkyl group having 1 - 18 carbon atoms capable of having a substituent; X₆ and X₇ respetively denote a single bond, -O-, or Z₂ denotes -CH₂O-, -OCH₂- or a single bond; and respectively denote or and denotes or with proviso that at least one of and is or in a liquid crystal device. A use of a composition according to Claim 1, which further comprises a mesomorphic compound having a negative dielectric anisotropy, in a liquid crystal device. A use of a composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -2 , in a liquid crystal device. A use of a composition according to Claim 3, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -5, in a liquid crystal device. A use of a composition according to Claim 4, wherein said mesomorphic compound having a negative dielectric anisotropy has a dielectric anisotropy Δε of below -10, in a liquid crystal device. A use of a composition according to Claim 2, wherein said mesomorphic compound having a negative dielectric anisotropy is a mesomorphic compound represented by any of the following formulas (V-1) to (V-5); wherein Ra and Rb respectively denote a linear or branched alkyl group capable of having a substituent; Xa and Xd respectively denote a single bond, -O-, or Xb and Xc respectively denote a single bond, or -CH₂CH₂-; Aa and Ab respectively denote a single bond, or with proviso that when Aa and Ab are both single bonds, Xb and Xc are both single bonds, and Xa and Xd are both single bonds or -O-, or Xa is and Xd is and Ya and Yb are respectively cyano group, halogen or hydrogen with proviso that Ya and Yb cannot be hydrogen simultaneously; wherein Re and Rf respectively denote a linear or branched alkyl group capable of having a substituent; Xe and Xh are respectively a single bond, -O-, or Xf and Xg are respectively or a single bond; and Ae and Af are respectively or a single bond with proviso that Ae and Af cannot be a single bond simultaneously; wherein Ai is a single bond or Aj is a single bond, or Ri and Rj are respectively a linear or branched alkyl group capable of having a substituent with proviso that Ri and Rj are linear alkyl groups when Aj is a single bond; Z₃ is -O- or -S-; Xi and Xk are respectively a single bond, -O-, or Xj is a single bond, -CH₂O- or -OCH₂-with proviso that Xi is a single bond when Ai is a single bond, Xj is not a single bond when Aj is or and Xk is a single bond when Aj is a single bond; wherein Rl and Rm are respectively a linear or branched alkyl group capable of having a substituent; Al and Am are respectively a single bond, or with proviso that Al and Am cannot be a single bond simultaneously; Xl is a single bond, -O-, or and Xm is a single bond, -CH₂O-, -OCH₂-, -CH₂CH₂- or -C≡C-; wherein Rn and Ro are respectively a linear or branched alkyl group capable of having a substituent; Xn and Xq are respectively a single bond, -O-, or Xo and Xp are respectively a single bond, -CH₂O-, -OCH₂- or -CH₂CH₂-; An and Ap are respectively a single bond, or Ao is or and Z₄ is or in a liquid crystal device. A liquid crystal device, comprising a pair of electrode plates and a ferroelectric liquid crystal composition according to any one of Claims 1 - 6 disposed between the electrode plates.

Inventors: ASAOKA MASANOBU, KATAGIRI KAZUHARU, KIMURA YOSHIKO, KITAYAMA HIROYUKI, SATO JUNKO, SHINJO KENJI, TAKIGUCHI TAKAO, TERADA MASAHIRO, TOGANO TAKESHI, YAMASHITA MASATAKA, ASAOKA, MASANOBU, KATAGIRI, KAZUHARU, KIMURA, YOSHIKO, KITAYAMA, HIROYUKI, SATO, JUNKO, SHINJO, KENJI, TAKIGUCHI, TAKAO, TERADA, MASAHIRO, TOGANO, TAKESHI, YAMASHITA, MASATAKA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1989
Main classification: C09K19
IPC codes: C09K19