Catalysts and process for oligomerization of olefins with nickel-containing zeolite catalysts

Abstract: There are disclosed catalysts and process for oligomerizing C₃-C₁₂ olefins in the liquid phase at 50°C-150°C in the presence of a nickel containing zeolite catalyst, the zeolite being a Cs or Ba exchanged CSZ-1, high silica ultra-stable faujasite and zeolites isostruc­ tural with mazzite.

Description: This invention relates to an improved liquid phase process for the oligomerization of olefins having about 3 to 12 carbon atoms and certain zeolite catalysts useful therefor. More particularly this invention relates to a liquid phase oligomerization process for preparing oligomers of olefins such as propylene and butene at moderate temperatures in the liquid phase using nickel-containing synthetic zeolites such as CSZ-1, high silica faujasites and zeolites isostructural with mazzite. In general the use of nickel-containing catalysts to effect the oligomerization reaction of olefins is known. It is also known to use certain types of nickel-containing zeolites. The present invention is based upon the discovery that nickel-containing CSZ-1, high silica faujasite and mazzite-like zeolites are highly effective and provide greater yields of oligomerized products in a relatively shorter reaction period than prior art catalysts. U.S. Patent 4,309,313, issued January 9, 1982 to Barrett et al. describes CSZ-1 zeolites and their manner of preparation. It further discloses that the zeolites are useful as hydrocarbon conversion catalysts for cracking and aromatization processes. This patent describes CSZ-1 which is used in the formation of the catalysts of the present invention. U.S. Patent 3,402,217, issued September 17, 1968 to Engelbreckt et al. discloses the use of NiO and 13X zeolite for oligomerizing propylene to hexenes. However, a very low catalyst efficiency is reported. U.S. Patent 4,029,719, issued June 14, 1977 to Forni et al. also discloses nickel 13X zeolites as olefin oligomerization catalysts but requires pre-treatment of the catalyst with organic or inorganic base prior to use. U.S. Patent 4,542,257, issued September 17, 1985 to S. J. Miller discloses liquid phase oligomerization of C₂ to C₂₀ olefins with nickel-containing HZSM-5, HZSM-11 zeolites and mixtures thereof at temperatures in the range of 45°F to 450°F. U.S. Patent 4,551,438, issued November 5, 1985 to S. J. Miller discloses the use in olefin oligomerization of nickel-containing ZSM-5, ZSM-11, silicalite or CZM zeolite, wherein the zeolite is treated with a hydrocarbyl aluminum halide. U.S. Patent 3,325,465, issued June 13, 1967 to Jones et al. contains a broad disclosure of the use of alumino silicate catalysts containing nickel or cobalt for use in the polymerization of olefins. U.S. Patent 3,960,978, issued June 1, 1976 to Givens et al. discloses the use of nickel-containing ZSM-5 and ZSM-11 zeolite for oligomerizing olefins useful for gasoline blending at reaction temperatures of 500°F to 900°F. U.S. Patent 3,827,968, issued August 6, 1974 to Givens et al. describes a two stage process for oligomerization and aromatization using a ZSM-5 zeolite which may contain nickel. U.S. Patent 4538012 discloses a liquid phase process for the oligomerisation of olefines using a nickel containing catalyst. U.S. Patents 4,628,138 and 4,628,139, both issued December 9, 1986 to Barnett et al. and K. W. Barnett, respectively, disclose omega zeolites, which are isostructural with mazzite, formed by either reducing a nickelocene on the zeolite or depositing a cyclooctadiene Ni(O) onto the zeolite. The only specific disclosures relate to the oligomerization of ethylene. The present invention is distinguished from the foregoing references in that the nickel-containing zeolites of this invention are different from those disclosed for olefin oligomerisation in the prior art references and provide a degree of catalyst activity and selectivity not found in prior art processes for oligomerizing propylene and higher olefins. The present invention therefore provides a process for oligomerizing C₃ - C₁₂ olefins which comprises contacting a C₃-C₁₂ olefin, or mixtures thereof, in the liquid phase at a temperature of 50°C to 150°C with a calcined, nickel-containing zeolite catalyst containing from 0.2% to 20% by weight nickel, the nickel being added either by cation exchange or by impregnation, the zeolite being selected from the group consisting of cesium or barium-exchanged CSZ-1, ultra-stable high silica faujasite and zeolites isostructural with mazzite. The nickel-containing zeolite catalysts per se are considered to be novel compositions of matter and as such constitute a further embodiment of the present invention. The terms oligomerization and oligomers as used herein are employed in their normal sense and refer to polymerization wherein the degree of polymerization is about two to five although somewhat higher molecular weight oligomers can also be formed in the reaction. A preferred aspect of the present invention is to prepare dimers, trimers, tetramers and pentamers of propylene, butene-1 and butene-2. The first category of catalysts of this invention are the zeolites categorized as CSZ-1 which are cesium-exchanged or barium-exchanged as well as nickel-containing. This type of zeolite was first disclosed in U.S. Patent 4,309,313 issued to Barrett et al. Those useful in this invention may have a composition 0.05 to 0.55 cesium:0.45 to 0.95 Na₂O:Al₂O₃: 3 to 100 SiO₂:X H₂O where X is 0 to 10. The foregoing ratios include the high silica forms of CSZ-1. To prepare the nickel-containing CSZ-1 zeolite useful in the present invention the CSZ-1 is cation exchanged with either cesium or barium cations and then nickel is added using either simple impregnation or further cation exchange. The catalyst of this invention contain 0.2 to 20% by weight nickel and preferably 1 to 15% by weight nickel. Nickel is added by contacting the zeolite with an aqueous solution of a nickel salt. While a wide variety of nickel salts are useful, it is preferred to use chlorides or nitrates. The other types of novel nickel-containing zeolite catalysts useful in the present invention are high silica "ultra-stable" faujasites and mazzite-like zeolites. High silica faujasites are those faujasite zeolites having a high silica:alumina ratio, i.e., SiO₂: Al₂O₃ ratios of at least 4.0. The Si:Al ratios of a variety of readily synthesized NaY materials can be increased by a wide range of chemical or physical chemical treatments. These processes involve removal of Al from the zeolite framework and creation of a metastable defect structure followed by filling the defects with Si from another part of the structure by further chemical treatments or hydrothermal annealing. Typical treatments use steam, e.g., U.S. Patent 3,293,192; acid leaching, e.g., U.S. Patent 3,506,400; treatment with EDTA, e.g., U.S. Patent 4,093,560; treatment with SiCl₄ as disclosed by Beyer et al. in Catalysis by Zeolites , p. 203 (Elsevier Press; 1980) or treatment with CHF₃ as in U.S. Patent 4,275,046 or other chemicals. These products are also referred to as "ultra-stable" because of their very high thermal and hydrothermal stability resulting from the replacement of Al³⁺ by Si⁴⁺ in the zeolite lattice. The other methods of so called secondary synthesis using (NH₄)₂SiF₆ in aqueous solution have also been demonstrated to yield high silica faujasites as in U.S. Patent 4,503,023. Directly synthesized high silica faujasites such as ECR-4 and ECR-32 or modifications thereof are also useful substrates. A steamed, ultra-stable faujasite is prepared as follows: 100 gms. NaY faujasite commercial zeolite (Si/Al = 2.4) was exchanged with a 10 wt. % solution of NH₄Cl at 60°C for one hour with stirring. The slurry was filtered, washed with one liter of distilled water and the filter cake was exchanged a second time with NH₄Cl in a procedure identical with the first exchange. After filtering and washing the second time, the product was dried at 100°C for one hour, then steam calcined in a closed crucible for three hours at 600°C. The product was exchanged two more times with NH₄Cl at which time the Na₂O level was about 0.5 wt. %. ELZ-20 is a commercially available form of this material from Union Carbide Corp. Steamed, ultra-stable Y faujasites are also described in U.S. Patent 3,293,192, issued December 12, 1966 and are manufactured by W. R. Grace and Company. Mazzite is a rare mineral and a naturally occurring zeolite; see Galli, Crystal Struct. Comm., 3 (1974), pp. 339-344. Isostructural forms of mazzite include ZSM-4, disclosed in British Patent 1,178,186, and zeolite omega, disclosed in British Patent 1,117,568, which differ only in Si/Al ratios and cation contents; see Meier et al., Atlas of Zeolite Structures (1978). Zeolite omega has the following chemical composition on an anhydrous basis and has been designated ELZ-omega-5 by Union Carbide Corporation: Al₂O₃ 15.49 wt. % SiO₂ 77.12 wt. % Na₂O 6.44 wt. % SiO₂/Al₂O₃ Molar Ratio 8.6 Na₂O/Al₂O₃ Molar Ratio 0.68 The process of this invention is carried out by contacting the catalyst with the olefin to be oligomerized under a pressure adequate to maintain the reactant in the liquid phase at the reaction temperature and intimately mixing the catalyst and olefin as the reaction proceeds. A particular advantage of the present invention is that the catalysts exhibit a high turnover number (TON) which is defined as the moles of olefin converted per mole of nickel per hour. TON values of at least 25 are obtained in accordance with this invention. When using a preferred nickel-containing barium-exchanged CSZ-1 catalyst in accordance with the invention, a TON value of 175 moles of olefin converted was obtained. In contrast, when TON values are computed based on the disclosure of U.S. Patents 3,402,717, 4,029,719, 4,542,251 and 4,551,438, TON values per hour for butene and propylene were about 9 to 18; these prior art patents disclose the use of nickel-containing zeolite catalysts for olefin oligomerization. TON values are computed by calculating the moles of olefin which are converted, determining the moles of nickel present in the catalyst used and dividing the moles of olefin converted by the moles of nickel present and dividing that value by the number of hours the reaction was run. Thus, for U.S. Patent 3,402,717 the TON for Example 1 was calculated from the following data: Rate of feed = 1.25 g/hr/g catalyst Catalyst is 3% by weight Ni Feed is 80% propylene, 20% propane Propylene rate of feed = 1.0 g/.03g Ni/hr 20% of propylene was converted Propylene converted = 0.2 g/.03 g Ni/hr = .0048 moles propylene/.0052 moles Ni/hr = 9.3 moles propylene/mole Ni/hr Thus, the TON value for this catalyst was 9.3. A similar calculation was made for Example 2 of U.S.Patent 4,029,719. for this calculation, the catalyst density was estimated at 1.5. the calculation was done as follows: Example 2 , Feed butene-1, 2 volumes/volume catalyst/hr density of butene = 0.6, density of catalyst estimated as 1.5 feed = 0.6 X 2 gms butene/1.5 X 1 gm catalyst/hr = 1.2 gms butene/1.5 gms catalyst/hr catalyst is 5% Ni feed = 1.2 gms butene/(1.5 X .05 = 0.075) gm Ni/hr Product 79.2% conversion For U.S. Patent 4,542,257, the TON was calculated for Example 6 as follows: Example 6 gives highest rate with Ni catalyst 98% conversion, LHSV = 0.5 (liquid hourly space velocity) Catalyst 3 wt. % Ni Density of propylene = 0.6, density of catalyst assumed 1.5 Feed 0.5 ml propylene/1.5 gm catalyst/hr 0.3 gm propylene/0.045 gm Ni/hr 0.0071 moles propylene/0.00078 mole Ni/hr rate = 9.2 TON/hr Also, for U.S. Patent 4,551,438, a TON value of 18.4 was computed based on the data of Example 5. U.S. Patents 4,628,138 and 4,628,139 disclose the use of zeolite catalysts containing nickel for ethylene oligomerizations and very high TON values, 1766 and 5860, were computed for the ethylene reactions disclosed in these references. However, TON values for ethylene catalysis are not comparable with catalysts for higher olefins oligomerization. The process of the present invention is preferably employed to oligomerize propylene, butene-1 and butene-2 at a temperature of 80°C to 120°C using a nickel-containing CSZ-1 zeolite which has been cesium or barium-exchanged. Preferred are catalysts having the following compositions (expressed as mole ratios): 0.81 Cs₂O:0.14 Na₂O:0.2 NiO:Al₂O₃: 5.92SiO₂ and 0.33 Cs₂O:0.58 BaO:NiO: Al₂O₃:5.86 SiO₂ and 0.62 BaO:0.26 Cs₂O:Al₂O3: 5.96SiO₂:2.24 NiO and 0.66 BaO:0.29 Cs₂O:Al₂O₃:5.96 SiO₂:0.78 NiO. To prepare products having a substantial proportion of linear oligomers, i.e., 10-20% by weight linear oligomers, it is preferred to use the CSZ-1 cesium or barium exchanged nickel-containing catalysts of this invention. Within this category, preferred catalyst embodiments are cesium exchanged CSZ-1 zeolites having a Cs⁺/Na⁺ mole ratio greater than 0.7, especially a Cs⁺/Na⁺ of at least 2.0 up to 6.0, and a cesium content of about 18 to 35% by weight, more preferably about 25 to 30% by weight. Barium exchanged catalysts in this preferred category will have a Ba/Cs mole ratio of at least 1 and up to about 2.5. When it is desired to prepare highly branched products as a result of the oligomerization process of this invention, then either the nickel-containing ELZ-20 or ELZ-omega-5 zeolite catalysts should be used. Typically, these catalysts will provide products containing less than 2 wt. % of linear oligomers. Prior to use the catalysts of this invention are vacuum calcined at temperatures of 375°C to 475°C. Somewhat lower calcination temperature, i.e., 275°C may also be suitable, but generally lower conversions have resulted. Relative to the amount of olefin, there is employed generally 10 to 20% by weight of the nickel-containing catalyst of this invention. The invention is further illustrated by the following examples which are not to be considered as limitative of its scope. (Percentages reported are by weight, except where otherwise indicated.) CATALYST COMPOSITIONS - Examples 1-11 Example 1 A sample of CSZ-1 was synthesized from a gel having a composition (mole ratios) of 0.5 Cs₂O:3.5 Na₂O:Al₂O₃: 12.5 SiO₂:187 H₂O, using the general method of U.S. Patent No. 4,309,313. The product had a chemical composition 0.6 Na₂O:0.4 Cs₂O:Al₂O₃:5.9 SiO₂. Twenty grams of this material was exchanged with a solution of 40 g. CsCl in 160 g. water for one hour at room temperature, filtered, then washed with 800 g. water on the filter. The sample was dried at 100°C, then Ni⁺⁺-exchanged in a solution of 8.8 g. NiCl₂.7H₂O dissolved in 160 g. 29% aqueous ammonia solution for 1 hour at room temperature. The sample was vacuum filtered (not washed) and dried at 110°C for 16 hours. The composition of this final catalyst was: 0.81 Cs₂O:0.14 Na₂O:0.2 NiO:Al₂5.92 SiO₂, i.e., 1.65% Ni. The catalyst was calcined at 375°C, under vacuum, for 2 hours before use. Example 2 CSZ-1 was made in a similar manner to that in Example 1, but having a chemical composition of 0.41 Cs₂O:0.59 Na₂O:Al₂O₃:5.92 SiO₂. 190 g. was added to 2350 ml. of a 5% solution of Ba(OH)₂ pre-adjusted to a pH of 7 with conc. HNO₃, and barium-exchanged at 60°C for 1 hour. After filtering, the barium-exchange was repeated, the product filtered, then washed with 5 l. water and dried at 110°C. A duplicate sample was made in a similar manner. Both samples were combined, placed in a muffle furnace at room temperature and slowly heated to 350°C, then held there for one hour. The hot powder was placed in a Hobart Mixer, and slowly stirred while adding a solution of 155 g. Ni(NO₃)₂.6H₂O dissolved in 485 g. water. The catalyst was air-dried at room temperature for 16 hours, followed by a similar period at 100°C. Chemical analysis gave a composition of 0.33 Cs₂O:0.58 BaO:NiO:Al₂O₃:5.86 SiO₂. The catalyst was calcined at 375°C, under vacuum, for 2 hours before use. Example 3 The CSZ-1 zeolite of Example 2 was double Ba⁺⁺ exchanged at 80°C (100 g. CSZ-1 in 11 H₂O + 65 g. Ba(NO₃)₂), followed by calcination at 110°C for 3 hours and 350°C for 2 hours. Half of this Ba-CSZ-1 was impregnated with a solution of 45 g. Ni(NO₃)2.6H₂O in 90 g. of water, followed by air-drying overnight. Chemical analysis gave a composition of 0.62 BaO:0.26 CS₂O:Al₂O₃:5.96 SiO₂:2.24 NiO. The sample was vacuum calcined at 375°C for 2 hours before use. Example 4 The second half of the Ba-CSZ-1 described in Example 3 was impregnated with a solution of 15 g. Ni(NO₃)₂.6H₂O dissolved in 90 g. of H₂O, then calcined as in Example 3. Chemical analysis of this sample gave 0.66 BaO:0.29 Cs₂O:Al₂O₃:5.96 SiO₂:0.78 NiO. The sample was vacuum calcined at 375°C before use. Example 5 The catalyst was prepared as in Example 2, but the final calcination temperature was 475°C. Example 6 A steamed ultra stable faujasite (ELZ-20, 100 g.), having an Si/Al ratio of 2.7 was heated at 90°C in 500 g. 2N HCl for 3 hours to remove detrital alumina, filtered and washed with 500 g. water. After drying at 100°C and rehydrating, the material was steamed in a covered dish at 1500°C for 20 minutes to further de-aluminate the zeolite framework. The product was again acid washed to remove detrital alumina (2 hours/2N HCl/90°C), filtered and washed on the filter, first with 300 ml. 1N HCl, then with sufficient water to remove all chloride ion, as demonstrated by testing the filtrate with Ba(NO₃)₂ solution. After drying at 100°C, the sample had very good retention of x-ray crystallinity. Ten grams of this high silica faujasite was K⁺ exchanged (10 g. KCl + 80 g. H₂O) for 1 hour at 60°C, filtered, washed with water, then exchanged with 4.4 g. NiCl₂.7H₂O in 80 g. H₂O for 1 hour at room temperature. After filtering, the sample was dried at 110°C. Chemical analysis using an IC plasma spectrometer gave values of 30.9 Si, 1.31% Al, 0.895% Ni and < 0.01% Na, representing Si/Al = 22.6 and Ni/Al = 0.31. Example 7 A sample of high silica faujasite was made as described in Example 6, but not exchanged with Ni⁺⁺. Example 8 A 200 g. sample of ammonium exchanged zeolite omega (ELZ-omega-5), having an Si/Al ratio of 4.3, was exchanged with 2 l. 10% ammonium sulfate solution for 1 hour at room temperature. After filtering, it was washed with 4 l. of H₂O, then air dried 16 hours at room temperature. It was then exchanged with a solution of 50 g. Ni(NO₃)₂.6H₂O in 1200 g. H₂O for 1 hour at room temperature. After filtering and washing it was dried at 110°C. Chemical analysis gave 29.8% Si, 7.28% Al, 0.82% Ni, 0.07% Na. Example 9 A sample of the omega-5 was ammonia exchanged as in Example 8. It was not exchanged further with Ni⁺⁺. Example 10 A sample of ELZ-omega-5 (20 g.) was exchanged with a solution of 20 g. NH₄Cl in 200 g. H₂O for 1 hour at room temperature, filtered, washed with 1 l. H₂O, then dried at 100°C. It was then exchanged with a solution of 5 g. Ni(NO₃)₂.6H₂O in 120 g. H₂O for 1 hour at room temperature, filtered, washed and dried. Chemical analysis gave a composition of 29.84% Si, 7.00% Al, 0.06% Na, 0.87% Ni. Example 11 A sample of CSZ-1 having an approximate composition 0.4 Cs₂O:0.6 Na₂O:Al₂O₃:5.26 SiO₂ was made using the method of U.S. Patent No. 4,309,303. 20 g. was exchanged with ammonium, then nickel, in the same manner as Example 1. Chemical analysis gave a composition of 21.02% Si, 8.20% Al, 0.34% Na, 2.26% Ni. OLIGOMERIZATIONS - Examples 12-42 General Procedure A 300 ml. Hoke pressure vessel was fitted with an internal thermocouple at one end and an 1800 psi safety disk and valve at the other end. The valve and safety disk were connected for easy removal. The solid catalyst was charged by detaching the valve and safety disk, then adding the catalyst through the resulting opening. The olefin was added as a liquid. The Hoke vessel was closed, evacuated and attached to a second vessel charged with a measured amount of liquid propylene or butene. The connecting valve was opened, whereby the liquid was transferred into the reaction vessel. The vessel was placed on a mechanical shaker and heated at the designated temperature while shaking. After the completion of the test, the vessel and contents were cooled and slowly vented of unreacted monomeric olefin. The contents were removed and weighed. For analysis, the product was diluted with heptane and analyzed by gas chromatographic techniques to obtain the monomer-dimer-trimer-tetramer composition. It was then hydrogenated in a Parr apparatus, under 60 psi (413.7 Kpa) H₂ 60°C, over 0.5% pt. on Al₂O₃ catalyst for 4 hours. Re-analysis by gas chromatography allowed a determination of the dimer skeletal structure by comparison of retention times with known isomers. Example 12 The Ni/Ba/CSZ-1 catalyst described in Example 2, 12.05 g., was charged into the Hoke reaction vessel. Then 82.5 gms. 1-butene was added and the reaction conducted at 110°C for 15 minutes. Analysis showed that 50.7% of the butene-1 had been converted to oligomers, of which 72.4% was C₈, 21.6% was C₁₂ and 5.6% was C₁₆. The C₈ component analyzed after hydrogenation 15.9% linear octane, 52.2% 3-methylheptane and 27.4% 3,4-dimethylhexane. The rate corresponds to 177 moles of olefin converted per mole of nickel per hour (TON). The residual butene was only 3.8% butene-1, indicating a facile concomitant isomerization of 1-butene. Example 13 The reaction was conducted as in Example 12, except for a reaction time of 2.5 hours. The corresponding values from product analyses were: Conversion, 66.7% Composition, 65.8% octenes, 15.5% linear 47.4% monomethyl-C₇ 29.1% dimethyl-C₆ 25.5% dodecenes 6.8% hexadecenes Example 14 Example 12 was repeated with a reaction time of 4.5 hours. The corresponding values from product analyses were: Conversion, 69.8% Composition, 64.3% octenes, 15.3% linear 46.6% methyl-C₇ 29.3% dimethyl-C₆ 27.1% dodecenes 7.8% hexadecenes Examples 12-14 demonstrate the rapid conversion to a maximum value of 70%, beyond which no further reaction occurs. Example 15 The procedure of Example 12 was followed with 12.05 g. of the catalyst described in Example 3 being used with 83.8 g. of butene. The reaction temperature was 80°C, the heating period 6.0 hours. The values from product analyses were: Conversion, 64.0% Composition, 67.2% octenes, 15.2% linear 49.2% methyl-C₇ 29.9% dimethyl-C₆ 25.1% dodecenes 6.1% hexadecenes Example 16 Example 15 was repeated with a reaction temperature of 120°C and a reaction time of 1.5 hours. The values from product analyses were: Conversion, 65.3% Composition, 64.6% octenes, 14.4% linear 41.2% methyl-C₇ 32.7% dimethyl-C₆ 11.8% other isomers formed by skeletal rearrangements at the higher temperature. 26.8% dodecenes 6.8% hexadecenes Example 17 The procedure of Example 12 was followed with 12.0 g. of the catalyst described in Example 4 and 79.6 g. of 1-butene. The reaction temperature was 120°C, held there for 1.5 hours. The values from product analyses were: Conversion, 65.4% Composition, 66.6% octenes, 13.9% linear 43.2% methyl-C₇ 31.5% dimethyl-C₆ 11.5% others 25.7% dodecenes 7.1% hexadecenes Example 18 Example 17 was repeated with a reaction temperature of 80°C, time 6.0 hours. The values from product analyses were: Conversion, 63.7% Composition, 69.0% octenes, 14.2% linear 50.8% methyl-C₇ 29.3% dimethyl-C₆ 23.8% dodecenes 6.5% hexadecenes Examples 12-18 demonstrate that a wide variety of Ni⁺⁺ and Ba⁺⁺ loadings on CSZ-1 zeolite can be tolerated without substantial alteration of conversion and selectivity. Temperatures likewise can be varied with little effect on ultimate conversion, although selectivities may change slightly at the higher end of the range. Examples 19-22 The procedure of Example 12 was followed with 12.0 gms of the catalyst described in Example 3 and 81-86 gms of 2-butene. The reaction temperature was 110°C. The reaction times were 0.75, 2.5,5.5 and 10.0 hours for the following Examples 19-22, respectively. The results are tabulated below. The results show the major components formed; the final three columns show the isomeric distribution of the C₈ products. Example Conversion, % C8, % C12, % C16, % Linear C8, % Me-C7, % Me2-C6, % 19 57.3 70.0 22.3 6.0 12.3 49.8 31.7 20 65.2 67.9 23.8 6.6 12.5 48.1 31.6 21 68.3 65.9 25.4 7.0 12.8 46.9 32.0 22 69.9 65.6 25.7 7.0 12.8 45.8 32.3 These examples demonstrate that 2-butene also reacts rapidly to give essentially the same results as 1-butene. Analysis of the unreacted butenes from Example 19 showed 3.9% 1-butene. This is the same as that obtained in Example 12, equilibrium of isomers is reached very rapidly. The TON of Example 19 was 34.3 moles of butene converted per hour per mole of nickel. Example 23 The catalyst for this example was prepared as in Example 5. The oligomerization was conducted as in Example 17. The values obtained from product analyses were: Conversion, 68.8% Composition, 62.8% octenes, 15.1% linear 41.4% methyl-C₇ 32.2% dimethyl-C₆ 11.4% others 27.9% dodecenes 7.6% hexadecenes Example 24 The catalyst for this example was also calcined at 475°C. The oligomerization was conducted as in Example 18. The values from analyses were: Conversion, 68.9% Composition, 63.7% octenes, 16.6% linear 50.4% methyl-C₇ 30.5% dimethyl-C₆ 27.1% dodecenes 7.5% hexadecenes Examples 23 and 24 demonstrate that a calcining temperature of 475°C is equivalent to, but no better than, calcining at 375°C. Example 25 The catalyst for this example was prepared as in Example 2, but was calcined at 275°C under vacuum. The oligomerization was conducted as in Example 18. The values from analyses were: Conversion, 32.5% Composition, 79.5% octenes, 18.1% linear 52.0% methyl-C₇ 28.0% dimethyl-C₆ 17.9% dodecenes 2.6% hexadecenes Example 26 The catalyst was that of Example 25. The oligomerization was conducted as in Example 17. The product analyses were: Conversion, 29.7% Composition, 81.3% octenes, 18.4% linear 51.1% methyl-C₇ 27.1% dimethyl-C₆ 16.3% dodecenes 2.5% hexadecenes Example 27 Example 26 was repeated, except the reaction time at 120°C was 6.0 hours. The product analyses were: Conversion, 35.4% Composition, 79.5% octenes, 16.7% linear 51.1% methyl-C₇ 28.6% dimethyl-C₆ Examples 25-27 show that a calcination temperature of only 275°C is very deleterious to the ultimate conversion obtainable. This low conversion is not improved by higher reaction temperature and/or longer reaction time. Example 28 (Comparative) The catalyst was nickel oxide supported on 75% SiO₂/25% Al₂O₃ and contained approximately 20% nickel. It was calcined at 500°C and protected from air and moisture before use. This catalyst (2.5 g., 8.5 m.mole Ni) and 80.6 g. of 1-butene were heated at 91°C for 1.0 hour with shaking. Recovery and analysis of the product indicated a conversion of 10.4%, for a TON of 17.6 moles per hour. Also, the unreactive butene was 45% 1-butene, which indicated a relatively slow isomerization. Example 29 (Comparative) Example 28 was repeated with 5.4 g. catalyst (18.4 m.mole Ni) and a 3.0 hours reaction time. The conversion was 39.0% with a TON of 10.1 moles per mole Ni per hour. Example 30 (Comparative) Example 28 was repeated with 10.0 g. catalyst (34.1 m.mole Ni) and a 5.0 hours reaction time. The conversion was 58.2% and the product composition was analyzed as follows: 61.8% octenes, 14.7% linear 38.1% methyl-C₇ 47.2% dimethyl-C₆ Example 31 (Comparative) Example 28 was repeated with 10.6 g. catalyst (36,1 m.mole Ni), 5.0 hours reaction time and 2- butene as the olefin. The product analyses were: Conversion, 55.4% (TON, 4.4) Composition, 67.3% octenes, 7.7% linear 45.2% methyl-C₇ 45.4% dimethyl-C₆ Examples 28-31 show that the the well-known supported nickel-on-silica/alumina catalysts are much less active than the zeolite-based catalysts of this invention. In addition, the zeolite-based catalyst produced 50% more linear octenes from butene-2. Example 32 The catalyst prepared in Example 2, 12.05 g., was charged into the 300 ml. Hoke vessel, then a mixture of 77.1 g. 1-butene and 34.1 g. propylene was charged. The mixture was heated to 80°C for 5.5 hours. After venting unreacted olefin, the product weighed 91.4 g. and analyzed as follows: Hexenes 9.0% 39.7% linear hexenes 51.7% 2-methylpentenes 8.7% dimethylbutenes Heptenes 22.3% Octenes 23.4% 15.2% linear octenes 54.0% 3-methylheptenes 30.8% 3,4-dimethylhexenes Nonenes 15.7% C₁₀+ 28.3% Example 33 Example 32 was repeated with 4.4 g. catalyst, 76.3 g. 1-butene and 76.5 g. propylene. The reaction was run at 65°C for 2.0 hours. The product weighed 51.3 g. and analyzed as follows: Hexenes 38.1% 24.6% linear hexenes 68.0% 2-methylpentenes 7.3% dimethylbutenes 31.3% Heptenes 25.4% linear 17.1% Octenes 23.4% linear octenes 48.5% 3-methylheptenes 18.5% 3,4-dimethylhexenes 13.5% C₉⁺ Examples 32 and 33 demonstrate that a mixture of olefins can be employed for co-oligomerization, that the composition can be varied by varying the ratio of olefins in the reacting mixture, and that products with high linear content can be produced. Example 34 The catalyst described in Example 2 was calcined at 375°C under vacuum for two hours. This catalyst, 7.5 g., was charged into the 300 cc Hoke vessel, then 96.1 g. propylene was charged. The vessel and contents were heated at 90°C for two hours with shaking. An initial exotherm to 103°C occurred, which indicated a high catalyst activity. The contents were discharged and hydrogenated for analysis. The results indicated: Conversion, 73.4% Composition, 58.5% hexenes, 30.7% linear 62.1% 2-methylpentenes 6.4% 2,3-dimethylbutenes 22.5% nonenes 11.6% dodecenes 2.7% pentadecenes Example 35 The catalyst described in Example 2 was calcined at 375°C for 2 hours under vacuum. A sample, 6.1 g., was charged to the 300 cc Hoke vessel, followed by 81.1 g. propylene. The vessel and contents were heated to 70°C with shaking for 1.33 hours. Work-up in the usual manner gave the following analytical results: Conversion, 70.9% Composition, 55.1% hexenes, 29.2% linear 63.6% 2-methylpentenes 7.1% 2,3-dimethylbutenes 29.8% nonenes 9.5% dodecenes 2.5% pentadecenes Examples 34 and 35 indicate that the catalyst is very active for the oligomerization of propylene. Example 36 The catalyst for this oligomerization, 7.0 g., was that described in Example 1 which was subsequently calcined at 375°C for 2 hours under vacuum. After charging the Hoke vessel with this catalyst, 84.8 g. of 1-butene was added and the vessel sealed. The vessel and contents were heated at 120°C, with shaking, for 3 hours. The product was removed and prepared for analysis in the usual manner. Analyses indicated the following: Conversion, 61.7% Composition, 61.1% octenes, 15.4% linear 27.5% methyl-C₇ 42.7% dimethyl-C₆ 31.6% dodecenes 6.2% hexadecenes The unreacted butene was a mixture of 5.1% 1-butene and 94.9% 2-butene. This example shows the effectiveness of a cesium-exchanged CSZ-1 catalyst as a support for nickel-catalyzed oligomerization of butenes. Example 37 The catalyst described in Example 6 was calcined at 275°C. A sample, 5.7 g., was heated with 83.8 g. 1-butene at 91°C for 5 hours. Analysis of the product, after hydrogenation, indicated the following: Conversion, 68.7% Composition, 58.7% octenes, 1.0% linear 5.7% methyl-C₇ 77.7% dimethyl-C₆ 15.5% others 31.1% dodecenes 8.4% hexadecenes Example 38 The catalyst described in Example 7 was calcined at 275°C under vacuum for 2 hours. A portion, 4.9 g., was charged to a 300 ml. Hoke vessel, followed by 82.0 g. of 1-butene. The mixture was heated with shaking at 91°C for 5 hours. Analyses indicated the following: Conversion, 64.8% Composition, 52.4% octenes, 0.2% linear 6.5% methyl-C₆ 76.3% dimethyl-C₆ 17.0% others 35.1% dodecenes 9.3% hexadecenes Examples 37 and 38 indicate that the acidic high-silica faujasites produce highly-branched products, even when nickel is present. Example 39 The catalyst described in Example 8 was calcined at 275°C for 2 hours under vacuum. A sample of this catalyst, 11.8 g., was charged into the 300 cc Hoke vessel in the dry box. After addition of 82.6 g. of 1-butene, the vessel and contents were heated at 91°C for 5 hours. The product was removed, vented of unreacted butenes (5.0% 1-butene) and analyzed after hydrogenation. The results were: Conversion, 88.0% Composition, 58.5% octenes, 0.5% linear 3.0% methyl-C₇ 71.1% dimethyl-C₆ 25.4% others 33.2% dodecenes 7.3% hexadecenes Example 40 Example 39 was repeated with the nickel-free catalyst described in Example 9. Analysis indicated the following: Conversion, 66.6% Composition, 60.5% octenes, 0.1% linear 5.5% methyl-C₇ 77.2% dimethyl-C₆ 17.2% others 32.4% dodecenes 6.1% hexadecenes Examples 39 and 40 show the effectiveness of the omega zeolite for selective oligomerizing butenes to highly branched products. The catalyst containing nickel produced higher conversion, with retention of the high selectivity to branched products. Example 41 The catalyst described in Example 10 was calcined at 275°C under vacuum for two hours. A portion of this catalyst, 11.6 g., was utilized for oligomerizing 81.5 g. of 1-butene at 130°C for 5 hours. Analyses of the resulting product showed the following results: Conversion, 98.4% Composition, 20.4% octenes, 0.7% linear 38.0% methyl-C₇ 29.9% dimethyl-C₆ 31.5% others 37.9% dodecenes 27.5% hexadecenes 14.2% C₂₀⁺ This example shows that the nickel-omega catalyst, at higher temperatures, produces a high selectivity for long-chain, branched hydrocarbons. Example 42 The catalyst described in Example 11 was calcined at 275°C for 2 hours under vacuum. A portion, 8.9 g., was used to catalyze the oligomerization of 85.1 g. of 1-butene at 130°C for 2.5 hours. The product analyzed: Conversion, 94.1% Composition, 28.1% octenes, 0.7% linear 28.0% methyl-C₇ 48.8% dimethyl-C₆ 22.5% others 36.8% dodecenes 23.5% hexadecenes 11.6% C₂₀⁺

Claims: A process for oligomerizing C₃-C₁₂ olefins characterised by contacting a C₃-C₁₂ olefin or mixtures thereof in the liquid phase at a temperature of 50°C to 150°C with a calcined nickel-containing zeolite catalyst, containing from 0.2% to 20% by weight nickel, the nickel being added either by cation exchange or by impregnation, the zeolite being selected from the group consisting of cesium or barium exchanged CSZ-1, high silica ultra-stable faujasites and zeolites isostructural with mazzite. The process of claim 1 wherein the olefin is propylene or butene-1. The process of claim 1 or claim 2 wherein the catalyst is calcined at a temperature of 375°C to 475°C. The process of any of the preceding claims wherein the catalyst contains from 0.2% to 20% by weight nickel. The process of claim 4 wherein the catalyst contains from 1% to 15% by weight nickel. The process of any of the preceding claims wherein the catalyst is a cesium exchanged CSZ-1 zeolite having a CS+/NA+ -ratio of from 2.0 to 6.0, a cesium content of 18% to 35% by weight and a nickel content of from 0.2 to 20% by weight. The process of claim 6 wherein the cesium content is 25 to 30% by weight and the nickel content is 1 to 15% by weight. The process of any of claims 1 to 5 wherein the catalyst is a barium exchanged CSZ-1 zeolite having a Ba/Cs ratio of 1 to 2.5 and a nickel content of 0.2 to 20% by weight. The process of claim 8 wherein the nickel content is 1% to 15% by weight. The process of any of the preceding claims wherein the oligomerized olefins contain from 10 to 30% by weight linear oligomers. The process of claim 10 wherein the olefin is a C₃ or C₄ olefin. The process of claim 11 wherein the catalyst is a high silica ultra-stable faujasite. The process of any of claim 1 to 5 wherein the catalyst is zeolite omega. The process of claim 12 or 13 wherein the oligomerized olefins contain less than 2% by weight linear oligomers.

Inventors: PRUETT ROY LAVELLE, TUNISON MAFER EUGENE, VAUGHAN DAVID EVAN WILLIAM, YOUNG DAVID ALEXANDER, PRUETT, ROY LAVELLE, TUNISON, MAFER EUGENE, VAUGHAN, DAVID EVAN WILLIAM, YOUNG, DAVID ALEXANDER
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1989
Main classification: C07C2
IPC codes: C07C67, B01J29, C07C1, C07B61, C07C11, C07C2