THERMOSENSITIVE RECORDING MEDIUM

Abstract: A thermosensitive recording medium comprises a substrate and a thermosensitive, coloring layer, provided on the substrate, comprising a binder, a colorless or light-colored electron-donating dye, an electron-accepting compound to react with the electron-donating dye and form a coloring matter and then an ester compound obtained from a fatty acid having 20 to 28 carbon atoms and a straight or cyclic alcohol, the ester having a melting point of 50 to 100 degree C and one or more non-phenolic hydroxy group. It is improved in prevention from fogging and sensitivity.

Description: The present invention relates to a thermal recording material. In particular, the present invention relates to a thermal recording material having an excellent coloring sensitivity which is free of abrasion marks. Prior Art Thermal recording materials are widely used as recording materials for facsimiles, computers and various measuring instruments and apparatuses, since they are maintenance-free and relatively inexpensive and do not generate noise. With a recent trend toward an increase in the facsimile transmission speed and the printout speed of computer terminals, a thermal recording material having a high sensitivity, i.e., a power of forming a dense color with a low energy, is eagerly demanded. To increase the sensitivity, the following processes have been proposed heretofore: (1) a process wherein a dye or a developer is finely milled to increase the color forming efficiency (see, for example, JP-A-56-15394 and 58-76293), (2) a process wherein a substance having a low melting point is added or a color developer having a low melting point is used to lower the color forming temperature (see, for example, JP-A-48-19231 and JP-B-50-14531), (3) a process wherein the smoothness of the surface of a recording material is increased to improve the thermal conductivity (see, for example, JP-B-52-20142), and (4) a process wherein the amount of a color forming component is increased to increase the density of the color. Although these sensitivity increasing techniques have an advantage of increasing the recording sensitivity, they induce coloration caused by abrasion, the so-called abrasion marks, since coloration is effected with a low energy and, therefore, the products have only a low commercial value. The abrasion marks have been controlled by using petroleum wax such as paraffin wax or micro-crystalline wax or natural vegetable wax such as carnauba wax in the prior art. However, these waxes have no chemical affinity with an electron-donating dye or an electron-accepting compound such as a phenolic substance capable of forming color upon reaction with the electron-donating dye and, therefore, they impair the coloring sensitivity and accelerate the whitening of the formed color with the lapse of time. Under these circumstances, a further development has been demanded. An object of the present invention is to provide a thermal recording material free of abrasion marks and having a high coloring senstivity. Summary of the Invention After intensive investigations made for the purpose of solving the above-described problems, the inventors have found that substances having a melting point of as low as 50 to 100° C are effective in preventing the formation of abrasion marks and that among them, esters of a higher fatty acid having at least one non-phenolic hydroxyl group and 20 to 28 carbon atoms with a straight-chain or cyclic alcohol are capable of inhibiting the whitening with the lapse of time and have a remarkable sensitizing effect. The present invention has been completed on the basis of these findings. The present invention provides a thermosensitive recording medium comprising a substrate and a thermosensitive, coloring layer, provided on the substrate, comprising a binder, a colorless or light-colored electron-donating dye, an electron-accepting compound reactive with the electron-donating dye to form a coloring matter wherein the color-forming layer contains an ester of a higher fatty acid having 20 to 28 carbon atoms with a straight-chain or cyclic alcohol, said ester having a melting point of 50 to 100° C and at least one non-phenolic hydroxyl group in the molecule. It is preferred that the esters of a higher fatty acid having 20 to 28 carbon atoms with a straight-chain or cyclic alcohol which have a melting point of 50 to 100° C and at least one non-phenolic hydroxyl group in the molecule include (1) partial esters of a hydroxyl-free higher fatty acid having 20 to 28 carbon atoms with a straight-chain or cyclic polyhydric alcohol and (2) esters of a higher fatty acid having a hydroxyl group and 20 to 28 carbon atoms with a straight-chain or cyclic monohydric or polyhydric alcohol. It is preferable that the ester is a glyceride mixture comprising 70% by weight or more of a monoglyceride of a fatty acid having to 22 to 28 carbon atoms. Preferably the layer comprises 5 to 50% by weight, as the solid, of the ester compound. The thermal recording medium of the present invention is free of abrasion marks and has a high coloring sensitivity and is improved in prevention of fogging. The higher fatty acids having 20 to 28 carbon atoms include straight-chain fatty acids such as arachic, heneicosanoic, behenic, tetracosanoic and montanic acids; and branched fatty acids such as 2-methyltetracosanoic acid. The straight-chain or cyclic polyhydric alcohols include, for example, glycerol, erythritol, arabitol, sorbitol, sorbitan, mannitol and mannitan. The esters include, for example, partial esters having a melting point of 50 to 100°C formed from the above-mentioned higher fatty acid having 20 to 28 carbon atoms and the straight-chain or cyclic polyhydric alcohol. Examples of them include monoglycerides of higher fatty acids such as behenic acid, mannitan monobehenate (melting point: 67°C) and sorbitan dibehenate (melting point: 65°C). Among the above-mentioned esters, higher fatty acid glycerides are particularly preferred, since they are not only effective as a sensitizing agent or abrasion mark inhibitor but also quite effective in inhibiting blotting of the print and for resisting heat (i.e. for preventing color formation at low temperature). The inventors have investigated the influences of the number of carbon atoms of the fatty acids used for forming the higher fatty acid glycerides and glyceride composition (i.e. mono-, di- or triglyceride) to reveal that monoglycerides of higher fatty acids having 22 to 28 carbon atoms which have a monoglyceride purity of at least 70 wt. % among the glycerides are preferred, since they have not only the functions of the sensitizer and abrasion mark inhibitor but also effects of improving the quality of the print, i.e. inhibiting the blotting of the print and improving the heat resistance (preventing color formation at low temperatures). In addition, they increase the stability of the product when they are used for forming a coating layer. Among them, monoglycerides of higher fatty acids having 22 to 24 carbon atoms are particularly preferred. The monoglycerides of higher fatty acids having 22 to 28 carbon atoms and a monoglyceride purity of at least 70 wt. % based on the total glycerides are produced by direct esterification of a higher fatty acid such as behenic, tetracosanoic or montanic acid with glycerol or by transesterification of a higher fatty acid triglyceride with glycerol. The purity of them is increased by molecular distillation with, for example, a thin-film distillation device. The amount of the ester of the higher fatty acid having 20 to 28 carbon atoms with a straight-chain or cyclic alcohol having a melting point of 50 to 100°C and at least one non-phenolic hydroxyl group in the molecule is preferably 5 to 50 wt. % based on the total solid content of the heat-sensitive color-forming layer. When it is less than 5 wt. %, both the sensitizing and abrasion mark inhibiting effects are reduced and, on the other hand, when it exceeds 50 wt. %, the dye content is reduced to reduce the density of the formed color. Although the function mechanism of the ester used in the present invention has not been elucidated yet, it is supposed that a frictional heat generated when the surface of the thermal recording material of the present invention is rubbed is absorbed by the ester, whereby the ester is molten to inhibit the transmission of the frictional heat to the dye/developer to thereby inhibit the formation of the abrasion marks. Supposedly the non-phenolic hydroxyl group of the ester has some intermolecular interaction with the hydroxyl group of the developer to cause a eutectic phenomenon to thereby increase the sensitivity and the interaction continues even after the color formation to inhibit the sublimation of the developer or the phase separation, thus inhibiting the whitening with the lapse of time. However, when an ester of a branched polyhydric alcohol such as trimethylolpropane or pentaerythritol with a higher fatty acid is used, the dispersion stability of the heat-sensitive coating agent is poor even it has hydroxyl residues in its molecule. The sensitivity of the heat-sensitive paper having a coating of this agent is also poor, supposedly since its molecular structure is bulkier than that of a non-branched one. When the higher fatty acid monoglyceride having 22 to 28 carbon atoms and a monoglyceride purity of at least 70 wt. % based on the total glycerides is selected from the group of higher fatty acid glycerides, the blotting of the print is prevented, thermal resistance is improved and a stable coating material can be produced, supposedly since this compound has a melting point and HLB in suitable ranges, though the details are yet unknown. The electron-donating dyes used in the present invention are preferably leuco dyes such as triphenylmethane, fluoran, phenothiazine Auramine, spiropyran and indolinophthalide dyes. They can be used either alone or in the form of a mixture of two or more of them. They include, for example, the following compounds: 3,3-bis(p-dimethylaminophenyl)phthalide, 3,3-bis(p-dimethylaminophenyl)-6-dimethylaminophthalide, 3,3-bis(p-dimethylaminophenyl)-6-diethylaminophthalide, 3,3-bis(p-dimethylaminophenyl)-6-chlorophthalide, 3,3-bis(p-dibutylaminophenyl)phthalide, 3-cyclohexylamino-6-chlorofluoran, 3-dimethylamino-5,7-dimethylfluoran, 3-diethylamino-7-chlorofluoran, 3-diethylamino-7-methylfluoran, 3-diethylamino-7,8-benzofluoran, 3-diethylamino-6-methyl-7-chlorofluoran, 3-(N-p-tolyl-N-ethylamino)-6-methyl-7-anilinofluoran, 3-pyrrolidino-6-methyl-7-anilinofluoran, 2-(N-(3'-trifluoromethylphenyl)amino)-6-diethylaminofluoran, 2-(3,6-bis(diethylamino)-9-(o-chloroanilino)xanthylbenzoic acid lactam), 3-diethylamino-6-methyl-7-(m-trichloromethylanilino)fluoran, 3-diethylamino-7-(o-chloroanilino)fluoran, 3-dibutylamino-7-(o-chloroanilino)fluoran, 3-N-methyl-N-amylamino-6-methyl-7-anilinofluoran, 3-N-methyl-N-cyclohexylamino-6-methyl-7-anilinofluoran, 3-diethylamino-6-methyl-7-anilinofluoran, 3-(N,N-diethylamino)-5-methyl-7-(N,N-dibenzylamino)fluoran, Benzoyl Leucomethylene Blue, 6'-chloro-3'-methoxybenzindolinopyrrylospiran, 6'-bromo-3'-methoxybenzindolinopyrrylospiran, 3-(2'-hydroxy-4'-dimethylaminophenyl)-3-(2'-methoxy-5'-chlorophenyl)phthalide, 3-(2'-hydroxy-4'-dimethylaminophenyl)-3-(2'-methoxy-5'-nitrophenyl)phthalide, 3-(2'-hydroxy-4'-diethylaminophenyl)-3-(2'-methoxy-5'-methylphenyl)phthalide, 3-(2'-methoxy-4'-dimethylaminophenyl)-3-(2'-hydroxy-4'-chloro-5'-methylphenyl)phthalide, 3-morpholino-7-(N-propyl-trifluoromethylanilino)fluoran, 3-pyrrolidino-7-trifluoromethylanilinofluoran, 3-diethylamino-5-chloro-7-(N-benzyl-trifluoromethylanilino)fluoran, 3-pyrrolidino-7-(di-p-chlorophenyl)-methylanilinofluoran, 3-diethylamino-5-chloro-7-(α-phenylethylamino)fluoran, 3-(N-ethyl-p-toluidino)-7-(α-phenylethylamino)fluoran, 3-diethylamino-7-(o-methoxycarbonylpnenylamino)fluorar, 3-diethylamino-5-methyl-7-(α-phenylethylamino)fluoran, 3-diethylamino-7-piperidinofluoran, 2-chloro-3-(N-methyltoluidino)-7-(p-n-butylanilino)fluoran, 3-(N-benzyl-N-cyclohexylamino)-5,6-benso-7α-naphthylamino-4'bromofluoran, 3-diethylamino-6-methyl-7-mesidino-4',5'-benzofluoran, 3,6-dimethoxyfluoran, 3-(p-dimethylaminophenyl)-3-phenylphthalide, 3-di(1-ethyl-2-methylindol)-3-yl-phthalide, 3-diethylamino-6-phenyl-7-azafluoran, 3,3-bis(p-diethylaminophenyl)-6-dimethylaminophthalide, 2-bis(p-dimethylaminophenyl)methyl-5-dimethylaminobenzoic acid, 3-(p-dimethylaminophenyl)-3-(p-dibenzylaminophenyl)-phthalide, 3-(N-ethyl-N-namyl)amino-6-methyl-7-anilinofluoran and 3-(N-ethyl-N-tetrahydrofurfuryl)amino-6-methyl-7-anilinofluoran. The electron-accepting compounds (developers) used in the present invention are preferably phenolic compounds and hydroxybenzoid esters. Examples of them include the following compounds: 4,4'-isopropylidenediphenol, 4,4'-isopropylidenebis(2-chlorophenol), 4,4'-isopropylidenebis(2,6-dibromophenol), 4,4'-isopropylidenebis(2,6-dichlorophenol), 4,4'-isopropylidenebis(2-methylphenol), 4,4'-isopropylidenebis(2,6-dimethylphenol), 4,4'-isopropylidenebis(2-tert-butylphenol), 4,4'-sec-butylidenediphenol, 4,4'-cyclohexylidenebisphenol, 4,4'-cyclohexylidenebis(2-methylphenol), 4-tert-butylphenol, 4-phenylphenol, 4-hydroxydiphenoxide, α-naphthol, β-naphthol, 3,5-xylenol, thymol, methyl 4-hydroxybenzoate, 4-hydroxyacetophenone, novolaktype phenolic resin, 2,2'-thiobis(4,6-dichlorophenol), catechol, resorcinol, hydroquinone, pyrogallol, phloroglucinol, phloroglucinoloarboxylic acid, 4-tert-octylcatechol, 2,2'-methylenebis(4-chlorophenol), 2,2'-methylenebis(4-methyl-6-tert-butylphenol), 2,2'-dihydroxydiphenyl, ethyl p-hydroxybenzoate, propyl p-hydroxybenzoate, butyl p-hydroxybenzoate, benzyl p-hydroxybenzoate, p-chlorobenzyl p-hydroxybenzoate, o-chlorobenzyl p-hydroxybenzoate, p-methylbenzyl p-hydroxybenzoate, n-octyl p-hydroxybenzoate, 1-hydroxy-2-naphthoic acid, 2-hydroxy-6-naphthoic acid, zinc 2-hydroxy-6-naphthoate, 4-hydroxydiphenyl sulfone, 4-hydroxy-4'-chlorodiphenyl sulfone, bis(4-hydroxyphenyl) sulfide and 2-hydroxy-p-toluic acid. The electron-donating dyes and developers used in the present invention are finely milled into particles having a diameter of several µm (microns) in a dispersion medium. The dispersion medium is usually an aqueous solution of a water-soluble polymer having a concentration of about 10 wt. %. They include, for example, polyvinyl alcohol; starches and their derivatives; cellulose derivatives such as methylcellulose, hydroxyethylcellulose and carboxymethylcellulose; synthetic polymers such as polysodium acrylate, polyvinylpyrrolidone, acrylamide/acrylio ester copolymers and acrylamide/acrylic ester/methacrylic acid copolymers; sodium alginate, casein and gelatin. The dispersion is conducted with a ball mill, a sand mill or an attritor. The water-soluble polymers used herein function as a binder for the heat-sensitive coating component after the application. A water-resisting agent can be added to the coating liquid for the purpose of imparting water resistance thereto or a binder such as styrene/butadiene latex or a polymer emulsion such as acrylic emulsion can be added thereto. The heat-sensitive coating liquid thus prepared may further contain various additives. For example, an oil-absorbing substance such as an inorganic pigment can be added thereto in order to potect a recording head from stains. The inorganic pigments include, for example, kaolin, talc, calcium carbonate, aluminum hydroxide, magnesium hydroxide, magnesium carbonate, titanium oxide and fine particles of silica. Head travelling improvers such as fatty acids and metallic soaps can also be added thereto. They include, for example, stearic acid, behenic acid, aluminum stearate, zinc stearate, calcium stearate and zinc oleate. The heat-sensitive coating liquid containing the above-described additives is applied to the surface of a base (such as a paper sheet or a film) by means of a blade, air knife or roll coater or by a gravure method, then dried and smoothened to obtain the thermal recording material of the present invention. [Examples] The following Examples will further illustrate the present invention. In the Examples, parts and percentages are given by weight. In the following Examples, the esters used are those shown in Tables 1 and 2. Products 1 to 8 of the present invention and Comparative products 1 to 4 were produced by an ordinary process and purified by molecular distillation with Model 2-03 thin-film distillation apparatus (a product of Shinko Pfaudler Co., Ltd.). The monoglyceride purity was determined by separating the mono-, di- and triglycerides by GPC. The melting point was a temperature at which the melting started and determined with a differential scanning calorimeter. Product No. 9 of the present invention and Comparative Products 5 to 9 were those on the market. In the following Examples, the thermal recording materials were evaluated by the following methods: (1) Coloring sensitivity: The color formation was conducted with a dynamic color forming test apparatus (a product of Ohkura Electric Co., Ltd.) with a printing energy of 0.45 mj/dot. The color density was determined with Macbeth RD-918. (2) Whitening with the lapse of time: The colored samples prepared in above-described method (1) were left to stand in a room for one month and the color density was again determined. The rate of retention of the density was calculated. (3) Heat resistance: A heat gradient tester of Toyo Seiki Co., Ltd. was used. In the test, a hot plate of 55 to 95°C was pressed against the test sample for 5 sec to form color. The color densities of the sample at these temperatures were determined with Macbeth RD-918. The temperature of the hot plate at which the value of the optical density (OD) was 0.2 (heat resistance temperature) was employed as the index of the heat resistance. The higher the heat resistance temperature, the better the heat resistance. (4) Blotting of print: The surroundings of the colored part of the sample prepared in above process (3) at 95°C were observed with an optical microscope at x100 magnification. The results were evaluated as follows: o ○ : no blotting found at all, ○ : blotting scarcely observed, ▵ : slight blotting observed, and X : blotting serious. (5) Stability of coating agent: A compound shown in Table 1 was finely milled. The viscosity of the compound was determined immediately after the milling (η o ) and after leaving it to stand at 30°C for two weeks (η¹). The value of η¹/η o was employed as the index of the stability of the coating agent. The closer the value of η¹/η o to 1, the higher the stability. Example 1 (Liquid A) 3-N-Methyl-N-cyclohexylamino-6-methyl-7-anilinofluoran 10 parts 10 % aqueous polyvinyl alcohol solution 10 parts water 10 parts (Liquid B) 4,4'-isopropylidenediphenol 10 parts 10 % aqueous hydroxyethylcellulose solution 10 parts water 10 parts (Liquid C) ester of Table 1 or 2 10 parts calcium carbonate 10 parts 10 % aqueous polyvinyl alcohol solution 20 parts water 20 parts Demol EP (a dispersant of Kao Corporation; added only to the synthetic esters of Table 1) 0.5 parts Liquids A, B and C mentioned above were treated separately from each other with a sand mill to an average particle diameter of 3 µm or less. Then 1 part of liquid A, 3 parts of liquid B and 3 parts of liquid C were mixed together to prepare a heat-sensitive coating material, which was then applied to a commercially available wood-free paper having a basis weight of 53 g/m² in a coating weight of 6 g (in terms of solid)/m², dried and smoothened with a supercalender to prepare a thermal recording material. The thermal recording material thus obtained was tested to examine its coloring sensitivity, degree of whitening with the lapse of time, heat resistance, blotting of print and stability of the coating material. The results are shown in Table 3. Example 2 (Liquid A) 3-dibutylamino-7-(o-chloroanilino)fluoran 15 parts 10 % aqueous polyvinyl alcohol solution 15 parts water 20 parts (Liquid B) benzyl p-hydroxybenzoate 10 parts 10 % aqueous polyvinyl alcohol solution 20 parts water 10 parts (Liquid C) calcium carbonate 10 parts ester of Table 2 20 parts 10 % aqueous solution of carboxyl-modified polyvinyl alcohol 20 parts water 10 parts Liquids A, B and C were treated separately from each other with a sand mill to an average particle diameter of 3 µm or less. Then 1 part of liquid A, 3 parts of liquid B and 2 parts of liquid C were mixed together to prepare a heat-sensitive coating material, which was then applied to a commercially available wood-free paper having a basis weight of 53 g/m² in a coating weight of 6 g (in terms of solid)/m². After drying followed by smoothening with a supercalender, a thermal recording material was obtained. The coloring sensitivity and degree of whitening with the lapse of time of the obtained thermal recording material were determined. Example 3 (Liquid A) 3-diethylamino-6-methyl-7-anilinofluoran 15 parts 10 % aqueous polyvinyl alcohol solution 15 parts water 20 parts (Liquid B) benzyl p-hydroxybenzoate 5 parts ester of Table 1 5 parts calcium carbonate 10 parts 7 % aqueous polyvinyl alcohol solution 30 parts Demol EP (dispersant of Kao Corporation) 0.5 parts Liquids A and B were treated separately from each other with a sand mill to an average particle diameter of 3 µm or less. Then 1 part of liquid A was mixed with 10 parts of liquid B to prepare a heat-sensitive coating material, which was then applied to a commercially available wood-free paper having a basis weight of 53 g/m² in a coating weight of 5 g (in terms of solid)/m² . After drying followed by smoothening with a supercalender, a thermal recording material was obtained. The obtained thermal recording material was tested to determine its coloring sensitivity, degree of whitening with the lapse of time, heat resistance, blotting of print and stability of the coating material. The results obtained in Examples 2 and 3 are shown in Table 4. It is apparent from Tables 3 and 4 that the thermal recording materials of the present invention which have an excellent coloring sensitivity and which are not whitened with the lapse of time have a high commercial value. On the contrary, comparative products 1 to 4 prepared from a monoglyceride of a higher fatty acid having less than 20 carbon atoms were inferior with regard to the whitening with the lapse of time, heat resistance and blotting of the print. Comparative products 5 and 6 prepared from an ester having no non-phenolic hydroxyl group in the molecule gave poor results in the tests of the coloring sensitivity and whitening with the lapse of time because of the absence of the non-phenolic hydroxyl group in the molecule. Comparative product 7 prepared from the ester having a non-phenolic hydroxyl group in the molecule but having a melting point not higher than 50°C was whitened with the lapse of time because of the bleeding of the ester on the surface of the thermal recording material with the lapse of time, since it had a low melting point. Comparative products 8 and 9 free of the ester of the present invention gave bad results in the tests of the coloring sensitivity and whitening with the lapse of time. It is apparent from Tables 3 and 4 that the thermal recording material of the present invention comprising the monoglyceride of the higher fatty acid having 22 to 28 carbon atoms and also having a monoglyceride purity of at least 70 wt. % based on the total glycerides had not only excellent coloring sensitivity and resistance to the whitening with the lapse of tame but also excellent heat resistance, resistance to the blotting of the print and stability of the coating material. The abrasion marks of the products of the present invention were examined with a tester for fastness to rubbing (type of the Japan Society for Promotion of Scientific Research). In the test, the sample was rubbed with a cotton cloth 100 times and the density of the color in the rubbed part was determined with Macbeth RD-918. The products of the present invention gave only slight abrasion marks and excellent results.

Claims: A thermosensitive recording medium comprising a substrate and a thermosensitive, coloring layer, provided on the substrate, comprising a binder, a colorless or light-colored electron-donating dye, an electron-accepting compound reactive with the electron-donating dye to form a coloring matter wherein the color-forming layer contains an ester of a higher fatty acid having 20 to 28 carbon atoms with a straight-chain or cyclic alcohol, said ester having a melting point of 50 to 100° C and at least one non-phenolic hydroxyl group in the molecule. A recording medium according to claim 1, wherein the ester includes (1) a partial ester of a hydroxyl-free higher fatty acid having 20 to 28 carbon atoms with a straight-chain or cyclic polyhydric alcohol and (2) an ester of a higher fatty acid having a hydroxyl group and 20 to 28 carbon atoms with a straight-chain or cyclic monohydric or polyhydric alcohol. A recording medium according to claim 1, wherein the ester is a glyceride mixture comprising 70 percent by weight or more of a monoglyceride of a fatty acid having 22 to 28 carbon atoms. A recording medium according to claim 1, wherein the layer comprises 5 to 50 percent by weight, as the solid, of the ester compound.

Inventors: KANOH, YOSHIJI, NAKASHIMA, NORIHIKO, SUZUKI, ATSUSHI, UEDA, SADASHI
Applicants: KAO CORPORATION
Application year: 1989
Main classification: B41M5
IPC codes: B41M5