Method of making a double hetero type epitaxial wafer

Abstract: A double hetero type epitaxial wafer comprises; a substrate; conductive and opposite conductive type clad layers consisting respectively of a III-V group compound mixed crystal having an indirect transition type band structure; and an active layer consisting of a III-V group compound mixed crystal having a direct transition type band structure intervened between the clad layers, wherein the refractive index of the single crystal substrate side clad layer is smaller than that of the other clad layer.

Description: The present invention relates to a method of making a double hetero type epitaxial wafer, and more particularly, a double hetero type epitaxial wafer suitable for producing a light emitting diode (LED) having a large light emission power output. In this specification, a compound consisting of a IIIb group element and a V b group element in the periodic table is referred to as a III-V group compound. A III-V group compound mixed crystal epitaxial wafer having a double hetero structure is suitable for producing an LED having a large power output, since it can confine carriers in an active layer and it has a low carrier loss due to a non-radiative recombination process. Particularly, since by using an epitaxial wafer of a gallium aluminum arsenide (GaAlAs) mixed crystal a red LED having a large power out put can be produced, the epitaxial wafer is widely used for a display device or an automatic focus measuring device of a camera, etc. The epitaxial wafer can be produced by an epitaxial growth of a required III-V group compound mixed crystal, which growth is carried out by a liquid phase epitaxial growth process, a chemical vapour epitaxial growth process, etc. on a single crystal substrate (hereinafter referred to as a substrate of gallium arsenide (GaAs)) Nevertheless, since the GaAs used as a substrate has a low light penetration, light generated at a pn junction is absorbed by the substrate before being emitted to the outside. Conventionally, to prevent this light absorption by the substrate the substrate was cleaned by polishing or etching after the epitaxial growth. Preferably, an epitaxial wafer has a thickness of at least 0.1 mm or more, to prevent a breakage of the wafer during the production of an LED. Therefore, the epitaxial layer is grown to a thickness of 0.1 mm or more. When the thickness of the epitaxial layer is made thicker, however, a nonuniform mixed crystal composition is generated in an epitaxial layer particularly the clad layers, due to a difference of the segregation coefficient thereof. Examples of double hetero type epitaxial wafers in the prior art are given in EP-A-180479 and Sov. Phys. Tech. Phys. 23(4), April 1978, 476-480. It is desired to provide a III-V group compound epitaxial wafer suitable for the production of a high power output LED in which light absorption by the substrate does not occur or is very low. Accordingly there is provided a method of making a double hetero type epitaxial wafer as set out in claim 1. Mixed crystals are suitable for producing a double hetero type epitaxial wafer, since by changing the mixed crystal ratio, a mixed crystal having an indirect transition type or direct transition type band structure can be obtained. In the case of a gallium aluminum arsenide crystal, at a mixed crystal ratio of about 0.45 or less the crystal has a direct transition type structure, and at a mixed crystal ratio of more than 0.45, the crystal has an indirect transition type structure. According to the present specification the "mixed crystal ratio" means a ratio of respective elements of the III-V group compound composing a mixed crystal. In the case of gallium aluminum arsenide, the value of x (0 ≦ x ≦ 1) of (GaAs) 1-x (AlAs) x , by which gallium aluminum arsenide is expressed, is the mixed crystal ratio. The epitaxial wafer produced by the present invention is produced by an epitaxial growth of gallium aluminum arsenide on a gallium arsenide substrate using a liquid phase epitaxial growth process. Since a single crystal layer having a larger thickness can be easily obtained in the liquid phase epitaxial growth process, the growth process is selected in accordance with the object of the epitaxial growth. When an epitaxial wafer containing GaAlAs is grown, a p clad layer, an active layer, and an n clad layer are formed, in this order, on a p type GaAs substrate. Accordingly, when a p type GaAs substrate is used, since the difference between lattice constants of a p type GaAs and a GaAlAs is small, no generation of misfit dislocation is found, and since the p type carrier concentration of the GaAs substrate can be greatly increased, the electrode is easily formed. According to the present invention a substrate side clad layer having a refractive index smaller than that of an upper side clad layer is used. Namely, a substrate side clad layer having a mixed crystal ratio larger than that of the upper side clad layer is used. Consequently, the light reflected at the interface between the substrate and the clad layer passes through the interface between the clad layer and the active layer, without an irregular reflection thereof, whereby the exterior quantum efficiency of the LED is enhanced and the emission power of the LED is increased. In the case of gallium aluminum arsenide mixed crystal epitaxial wafer, a substrate side p clad layer having a mixed crystal ratio larger by at least 0.02 than that of the upper side n clad layer is used. In a III-V compound mixed crystal, the wider the band width, which is an energy gap between the valence band and a conductive band, the smaller the refractive index. For example, in a gallium aluminum arsenide, the larger the mixed crystal ratio, the larger the band width and the smaller the refractive index. In the case of a gallium aluminum arsenide mixed crystal epitaxial wafer, 1 ○ a layer thickness and 2 ○ mixed crystal ratio of each layer are preferably selected as follows. (1) p clad layer; 1 ○ about 5 to about 40 µm, 2 ○ about 0.6 to about 0.9. (2) active layer; 1 ○ about 0.5 to about 7 µm 2 ○ about 0 to about 0.45. A p conductive type active layer is selected. Accordingly wave length of output light varies from about 870 nm to 620 nm. (3) n clad layer; 1 ○ about 5 to about 40 µm, 2 ○ about 0.5 to about 0.88. Further, the carrier concentration of each layer is in a usual range, for example, about 1 x 10¹⁷ to 1 x 10¹⁸/cm³. Preferably, the active layer has a larger carrier concentration than that of the p clad layer. Example. The following gallium aluminum arsenide mixed crystal epitaxial wafer for red LED was grown by a liquid phase epitaxial growth process. (1) Substrate; The surface direction was (100). The substrate was a zinc doped p type gallium arsenide single crystal substrate having a thickness of 0.3 mm. In the following example of the present invention and the comparative example, 1 ○ layer thickness, 2 ○ carrier concentration, and 3 ○ mixed crystal ratio are respectively described, in this order. (2) a p clad layer (substrate side clad layer); 1 ○ 20 µm, 2 ○ 3.0 x 10¹⁷/cm³, 3 ○ 0.81. The refractive index of the p clad layer is about 3.15. (3) an active layer; 1 ○ 2.0 µm, 2 ○ 5.2 x 10¹⁷/cm³, 3 ○ 0.34. (4) an n clad layer (upper side clad layer); 1 ○ 40 µm, 2 ○ 2.0 x 10¹⁷/cm³, 3 ○ 0.72. The refractive index of the n clad layer is about 3.19. The carrier concentration was measured by a C-V process and a Van Der Pauw method. Further, the mixed crystal ratio was measured by obtaining a value measured by an x-ray microanalysis method, and correcting the value by a ZAF correction process. LED chips having a square with a one side length of 0.3 mm and having a thickness of 0.25 mm were made from the obtained epitaxial wafer. After the obtained chips were coated with an epoxy resin, the various properties thereof were measured under a condition of a current density of 8 A/cm². The obtained LED light output was 1.8 cd (average value of 100 LEDs), the emission wavelength was 661 nm, and the forward voltage was 1.85 V (average of 100 chips). Comparative example. On a gallium arsenide single crystal similar to that used in the example of the present invention, the following gallium aluminum arsenide mixed crystal was grown by a liquid phase epitaxial growth process. (1) a p clad layer; 1 ○ 18 µm, 2 ○ 3.5 x 10¹⁷/cm³, 3 ○ 0.65 The refractive index of the p clad layer was about 3.21. (2) an active layer; 1 ○ 1.8 µm, 2 ○ 5.2 x 10¹⁷/cm³, 3 ○ 0.34. (3) an n clad layer; 1 ○ 45 µm, 2 ○ 2.0 x 10¹⁷/cm³, 3 ○ 0.72 The refractive index of the n clad layer was about 3.18. LED chips were made from the obtained epitaxial wafer in the same manner as used in the example of the present invention. The LED light output measured in the same manner as in the example of the present invention was 1.1 cd (average valve of 100 LEDs), and the peak light emission wavelength was 663 nm. According to the present invention, a strong light output can be obtained without removing the substrate. Further, since it is not necessary to grow a large and thick epitaxial layer to remove a substrate, the nonuniformity of the composition of the epitaxial layer is not generated.

Claims: A method of making a double hetero type epitaxial wafer comprising: forming the following layers by liquid phase epitaxial growth on a p-type gallium arsenide single crystal substrate; a clad layer of a first conductivity type and a clad layer of opposite conductivity type, each consisting of a gallium aluminum arsenide mixed crystal having an indirect transition type band structure; and an active layer of p-type consisting of a gallium aluminum arsenide mixed crystal having a direct transition type band structure between the clad layers, the clad layer located closer to the single crystal substrate being of p-type and having a smaller refractive index than the other clad layer. A method according to claim 1 wherein the p-type clad layer consists of a mixed crystal of gallium aluminum arsenide of the formula (GaAs) 1-χ (AlAs) χ in which χ is in the range 0.6 to 0.9 and has a thickness in the range 5 to 40 µm. A method according to any one of claims 1 or 2 wherein the n-type clad layer consists of a mixed crystal of gallium aluminum arsenide of the formula (GaAs) 1-χ (AlAs) χ in which χ is in the range 0.5 to 0.88 and has a thickness in the range 5 to 40 µm. A method according to any one of claims 1 to 3 wherein the p-type active layer consists of a mixed crystal of gallium aluminum arsenide which is of the formula (GaAs) 1-χ (AlAs) χ in which χ is up to 0.45 and has a thickness in the range of 0.5 to 7 µm.

Inventors: FUJITA HISANORI, ISHIWATARI TOSHIO, SATO TADASHIGE MITSUBISHI MONS, FUJITA, HISANORI, ISHIWATARI, TOSHIO, SATO, TADASHIGE MITSUBISHI MONSANTO
Applicants: MITSUBISHI CHEM CORP, MITSUBISHI CHEMICAL CORPORATION
Application year: 1989
Main classification: H01L33
IPC codes: H01L21, H01L33