Toner

Abstract: A polyester resin comprised of (a) units derived from a terephthalic acid component and/or a isophthalic acid component, (b) 0 to 80 mole%, based on the total carboxylic acid component, of units derived from a diol component represented by the formula: wherein R represents an alkyl group having 2 or 3 carbon atoms, and x and y are integers satisfying the requirement of 2 ≦ x + y ≦ 6, and (c) 20 to 100 mole%, based on the total carboxylic acid component, of units derived from an aliphatic diol component. The polyester has a weight average molecular weight M w of 3,000 to 20,000, a number average molecular weight M n of 1,000 to 10,000, a glass transition temperature T g of 40 to 70°C, and a softening temperature of 70 to 130°C. The polyester is valuable for a toner.

Description: This invention relates to a toner to be used for the development of statically charged images in an electrophotographic process, an electrostatic recording process or an electro-static printing process. More particularly, it relates to toner containing a polyester resin which has an excellent blocking resistance, melt flow characteristics and fixing property, and being especially valuable for full-color reproduction where a high melt flowability is required, and for the development in a high-speed copying machine or high-speed printer where a low-temperature fixing property is required. In the process for obtaining a permanent visible image from a statically charged image, the statically charge image formed on a photoconductive photosensitive material or electrostatic recording material is developed with toner triboelectrically charged in advance and the developed image is fixed. The fixation is performed by directly fusior bonding the toner image obtained by the development onto the photoconductive photosensitive material or electrostati recording material, or by transferring the toner image onto a paper or sheet and fusion-bonding the toner image to the transfer sheet. Fusion bonding of the toner image is effected by contact with a vapor of a solvent, pressurization or heating. The heat-fixing method includes a non-contact heating method using an electric oven or flash and a press heating method using a heating roller. To cope with recent requirements for an increased fixing speed, the latter method is preferably adopted. In the process for obtaining a color image, toners of three to four colors are applied to a transfer sheet at the above mentioned developing step, and coloration and fixation are effected while melting and mixing the respective toners at the fixing step. A resin having a good mixing property at the fixing step, that is, a resin having a good melt flowability is urgently required as the binder for a full-color toner. If a binder having a good melt flowability is used, a problem of an occurrence of an offset phenomenon at the fixing step arises, but if the binder is crosslinked or the molecular weight of the binder is increased, to prevent the offset phenomenon, the melt flowability becomes poor and the binder is not suitable for a full-color toner. Accordingly, a method of preventing the occurrence of an offset phenomenon, which comprises coating a silicone on the surface of a fixing roller of a copying machine, is currently adopted. At present, an increase of the operation speed in the fixing zone and a realization of energy-saving are urgently required, and in a copying machine other than a full-color copying machine, and a printer, a method is often adopted in which the occurrence of an offset phenomenon is prevented by coating a silicone on a fixing roller. The use of a low-molecular-weight resin composed of a divalent unsaturated carboxylic acid and an aromatic diol component as a toner resin has been proposed, but since the reactivity of the aromatic diol component with an un saturated carboxylic acid component is low, to obtain a resin having the desired physical properties, it is necessary to carry out the reaction at a high temperature. If the reaction is carried out at a high temperature, however, the aromatic diol is decomposed and a bad smell is generated and the image quality is poor. Furthermore, the aromatic diol is relatively expensive, and the use of a toner formed by using a large quantity of the aromatic diol is not preferable from the economical viewpoint during the current popularity of copying machines. Moreover, since an unsaturated carboxylic acid is used as the divalent carboxylic acid, hydroquinone or the like should be used as an agent for preventing the radical reaction, and the use of this radical reaction-preventing agen can produce environmental pollution. Under these circumstances, a low-molecular-weight toner suitable for full-color reproduction with a good fixing property, which has a good melt fiowability, good heat stability and good polymerization reactivity, is urgently requirec A primary object of the present invention is to provide a toner containing a resin binder, which has a low softening temperature and an excellent melt flowability, fixing property and blocking resistance. This toner is especially valuable for a full-color copying machine, high-speed copying machine or high-speed printer wherein a high melt flowability and a good low-temperature fixing property are required. In accordance with the present invention, there is provided a toner containing a polyester resin, which consists of (a) units derived from at least one dicarboxylic acid component selected from the group consisting of terephthalic acid components and isophthalic acid components, (b) as an essential feature up to 80% by mole, based on the total carboxylic acid component, of units derived from a diol componer represented by the following formula [I]: wherein R represents an alkyl group having 2 or 3 carbon atoms, and x and y are integers satisfying the requirement of 2 ≦ X + Y ≦ 6. and. (C) 20% by mole or more, based on the total carboxylic acid component, of units derived from an aliphatic diol component, and which has a weight average molecular weight M w of 3,000 to 20,000, a number average molecular weight M n of 1,000 to 10,000, a glass transition temperature T g of 40 to 70°C, and a softening temperature of 70 to 130°C DESCRIPTION OF THE PREFERRED EMBODIMENTS In the present invention, by the term terephthalic acid component" we mean a component derived from terephthalic acid or a lower alkyl ester thereof having 1 to 4 carbon atoms in the alkyl group, and by the term "isophthalic acid component" we mean a component derived from isophthalic acid or a lower alkyl ester thereof having 1 to 4 carbon atoms in the alkyl group. The terephthalic acid component effectively improves the glass transition temperature T g and blocking resistance of the polyester, and the isophthalic acid component effectively controls the polymerization reactivity and the softening temperature of the polyester. As specific examples of the diol component of formula [I] used in the present invention, there can be mentioned polyoxypropylene(n)-polyoxyethylene(n') -2,2-bis(4-hydroxyphenyl)propane, polyoxypropylene(n)-2,2-bis(4-hydroxy-phenyl)propane and polyoxyethylene(n)-2,2-bis(4-hydroxyphenyl)propane. Among them, polyoxypropylene(n)-2,2-bis (4-hydroxyphenyl)propane in which n is a number of from 2.1 to 2.5 is especially preferable. This diol component is advantageous in that, by using this diol component, the glass transition temperature of the polyester is improved and the reaction is easily controlled. Nevertheless, the diol component is easily heat-decomposed as a high temperature, and thus use of the diol component in combination with the aromatic dicarboxylic acid requiring a high reaction temperature is difficult. Therefore, the amount of the diol component used is limited to a maximum of 80% by mole, preferably up to 70% by mole, based on the total carboxylic acid component. As specific examples of the aliphatic diol used in the present invention, there can be mentioned ethylene glycol, diethylene glycol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, neopentyl glycol and propylene glycol. The aliphatic diol increases the rate of polycondensation reaction. Among the foregoing aliphatic diols, ethylene glycol, neopentyl glycol and butanediol are preferably used in view of the fixing property. The aliphatic diol is used in an amount of 20% to 100% by mole, preferably at least 30% by mole, based on the total carboxylic acid component. It is important that the toner according to the present invention contains a polyester resin having a weight average molecular weight M w of 3,000 to 20,000, a number average molecular weight M n of 1,000 to 10,000, a glass transition temperature T g of 40 to 70°C, and a softening temperature of 70 to 130°C. If the weight average molecular weight M w is lower than 3,000, the glass transition temperature T g is drastically reduced and the blocking resistance becomes poor although the melt flowability and fixing property of the resin are improved. If the weight average molecular weight M w exceeds 20,000, the melt flowability and fixing property of the resin become poor. Accordingly, the weight average molecular weight M w should be 3,000 to 20,000, preferably 3,000 to 15,000. The number average molecular weight M n should be 1,000 to 10,000, preferably 2,000 to 7,500, in correspondence to the above-mentioned weight average molecular weight M w . A good blocking resistance is obtained if the glass transition temperature T g is 40 to 70°C. In general, if an inorganic powder such as silica is incorporated into the toner the blocking resistance is improved, and this improvement is especially conspicuous when the glass transition temperature T g of the binder is low. If the glass transition temperature T g is 40 to 70°C, a good blocking resistance can be obtained even if the inorganic powder is not added. If the glass transition temperature T g is lower than 40°C, the blocking resistance is becomes very poor, although the fixing property is good, and even if the inorganic powder is incorporated, the blocking resistance is not improved. If the glass transition temperature T g is higher than 70°C, the fixing property becomes poor. The glass transition temperature T g is preferably 50 to 65°C. If the softening temperature is lower than 70°C, reduction of the glass transition temperature T g is conspicuous and the blocking resistance becomes poor, although the melt flowability and fixing property are good. If the softening temperature is higher than 130°C, the melt flowability and fixing property becomes poor, and therefore, the resin is not suitable as a binder for a full-color toner or a toner for a high-speed copying machine. The polyester resin for the toner of the present invention can be synthesized by a usual polyester-forming process in which the dicarboxylic acid component and diol component are subjected to esterification reaction or ester exchange reaction, and then polycondensation is carried out while removing the low-boiling-point diol component by distillation. A known polymerization catalyst, for example, titanium tetrabutoxide dibutyltin oxide, tin acetate, zinc acetate, tin disulfide, antimony trioxide or germanium dioxide, can be used for the polycondensation. The polyester resin for the toner of the present invention can be used in a dry toner, alone or in combination with another toner resin. Even if the polyester resin for the toner of the present invention is blended with another toner resin, the fixing property of the toner is improved without a lowering of the blocking resistance. In the present invention, the softening temperature means the temperature at which 1/2 of 1 g of a sample flows out when the measurement is carried out at a constant temperature-elevating rate of 3°C/min under a load of 30 kgf by using a nozzle having an orifice diameter of 1 mm and a length of 10 mm in a flow tester, Model CFT-500 supplied by Shimadzu Corp. The glass transition temperature T g is the temperature at the intersection point of the base line of the chart and the tangential line on the endothermic curve in the vicinity of T g , observed when the measurement is carried out at a temperature-elevating rate of 5°C/min by using a differential scanning calorimeter. The weight average molecular weight M w and number average molecular weight M n are those determined by using a gel permeation chromatograph, Model HCL-8200 supplied by Tosoh Corp. The present invention will now be described in detail with reference to the following examples, that by no means limit the scope of the invention. Example 1 Terephthalic acid, isophthalic acid, ethylene glycol, neopentyl glycol and polyoxypropylene(2.3)-2,2-bis(4-hydroxyphenyl)propane were charged at ratios shown in Table 1-1 into a reaction vessel, and antimony trioxide was added as the polymerization catalyst in an amount of 400 ppm based on the dicarboxylic acid component. An esterification reaction was carried out under atmospheric pressure at an inner temperature of 230°C, while stirring at 200 rpm. Then the pressure was gradually reduced to 1.0 mmHg (130 Pa) over a period of 40 minutes at an inner temperature of 240°C, while stirring at 200 rpm. Under this reduced pressure, ethylene glycol was removed by distillation. The softening temperature was traced, and the point at which the softening temperature reached a desired level was designated as the point of termination of the polycondensation. The desired softening temperature was obtained about 10 hours after the start of the reduction of the pressure. Accordingly, the pressure of the reaction system was elevated to atmospheric pressure to complete the polymerization and obtain a light yellow solid. The results of the analysis of the composition of the resin and the results of the measurement of the physical properties are shown in Table 1-2. Resin Charged amounts (molar parts) Dicarboxylic acid component Diol component Terephthalic acid Isophthalic acid Diol A* Ethylene glycol Neopentyl glycol A 50 50 50 70 - B 100 - 50 70 - C - 100 50 70 - D 50 50 30 90 - E 50 50 50 70 - F 50 50 50 70 - G 50 50 45 40 45 H 50 50 40 - 90 In view of the data of the weight average molecular weight M w and softening temperature shown in Table 1-2, it is seen that resins A through H have good melt flowability, mixing property and smoothness, and that when these resins A through H are used for a color toner, a good image sharpness is obtained, and when they are used for a usual toner, a good fixing property is obtained. Furthermore, from the data of the glass transition temperature T g shown in Table 1-2, it is seen that resins A through H have an excellent blocking resistance. Example 2 Dimethyl terephthalate, dimethyl isophthalate, ethylene glycol and polyoxypropylene(2.3)-2,2-bis(4-hydroxyphenyl)propane were charged in amounts shown in Table 2-1 in a reaction vessel, and titanium tetrabutoxide was added as the polymerization catalyst in an amount of 500 ppm based on the dicarboxylic acid components. Then the pressure was gradually reduced to 1.0 mmHg (130 Pa) over a period of 40 minutes at an inner temperature of 200°C, while stirring at 200 rpm, and under this reduced pressure, ethylene glycol was removed by distillation. The softening temperature was traced, and the point at which the softening temperature reached a desired level was designated as the point of termination of the polycondensation. About 9 hours after the start of the reduction of the pressure, the desired softening temperature was obtained. Accordingly, the pressure of the reaction system was elevated to atmospheric pressure to complete the polymerization. Resin Charged amounts (molar parts) Dicarboxylic acid components Diol components Dimethyl terephthalic Dimethyl isophthalic Diol A* Ethylene glycol I 50 50 70 50 J 100 - 20 100 The obtained resin was a yellowish red solid. The results of the analysis of the composition of the resin and the results of the measurement of the physical properties are shown in Table 2-2. Then the resin I was melt-kneaded with a resin X for a usual toner at a mixing ratio shown in Table 2-3 by using an extruder to obtain a resin K or M. The softening temperature and glass transition temperature T g of the obtained resin is shown in Table 2-3. Resin Blending ratio (% by weight) Softening temperature (°C) T g (°C) X X = 100 142 60.5 K X/I=90/10 138 60.0 L X/I=80/20 135 60.0 From Table 2-3, it is seen that a resin formed by blending the low-molecular-weight polyester into the toner resin X has a lower softening temperature than that of the toner resin X, while retaining the T g at the same level. This means that the resins I and J have an improved low-temperature fixing property compared to the resin X without a lowering of the blocking resistance. Note, the melt kneading was carried out at 150°C and 50 rpm by using a conical type twin-screw extruder supplied by Haake Buchler Instrumentals, Inc. Comparative Example 1 Terephthalic acid, isophthalic acid, ethylene glycol and polyoxypropylene(2.3)-2,2-bis(4-hydroxyphenyl)propane were charged in amounts shown in Table 3-1 in a reaction vessel, and antimony trioxide was added as the polymerization catalyst in an amount of 500 ppm based on the dicarboxylic acid components. The polycondensation was carried out in the same manner and under the same conditions as in Example 1, to obtain a light yellow solid M, N or O. The results of the analysis of the composition of the resin and the results of the measurement of the physical properties are shown in Table 3-2. Charged amount (molar parts) Dicarboxylic acid component Diol component Resin Terephthalic acid Isophthalic acid *1 Diol A Ethylene glycol M 50 50 95 20 N 50 50 50 70 O 50 50 20 120 From Table 3-2, it is seen that in the resin M, since the diol A is used in a large amount, the T g is lowered and the blocking resistance is poor, although the melt flowability and fixing property are good. In this case, since a large amount of the diol A having a poor reactivity was used, the polycondensation was conducted for 18 hours, but the T g was not elevated. Furthermore, when the polymerization temperature was elevated to 270°C, a large quantity of the decomposition product of the diol A was distilled off. From Table 3-2, it is seen that the resin N has a low T g and poor blocking resistance, although the melt flowability and fixing property are good. From Table 3-2, it is also seen that the resin O has a weight average molecular weight M w of 40,000, a high glass transition temperature T g , and a good blocking resistance, but the softening temperature is high and is not suitable for a toner to be used in the field wherein a high melt flowability and high fixing property and required. Moreover, the resin O had a poor adaptability to pulverization. Comparative Example 2 Following substantially the same procedure as mentioned in Example 1, a mixture of 100 parts by mole of terephthatic acid, 70 parts by mole of ethylene glycol and 60 parts by mole of neopentyl glycol was subjected to esterification reaction to obtain a resin composed of 100% by mole of terephthalic acid units, 42% by mole of ethylene glycol units and 58% by mole of neopentyl glycol units. This resin had the following physical properties. T g : 58.6°C M w : 12,000 M n : 5,800 Softening temperature : 110°C The polyester resin for the toner has a softening temperature and an excellent melt flowability, fixing property and blocking resistance. Accordingly, an image formed by using the toner has a high sharpness.

Claims: A toner containing a polyester resin, which consists of (a) units derived from at least one dicarboxylic acid component selected from the group consisting of terephthalic acid components and isophthalic acid components, (b) as an essential feature, up to 80% by mole, based on the total carboxylic acid component, of units derived from a diol component represented by the following formula [I]: wherein R represents an alkyl group having 2 or 3 carbon atoms, and x and y are integers satisfying the requirement of 2 ≤ x + y ≤ 6, and (c) 20% by mole or more, based on the total carboxylic acid component, of units derived from an aliphatic diol component, and which has a weight average molecular weight M w of 3,000 to 20,000, a number average molecular weight M n of 1,000 to 10,000, a glass transition temperature T g of 40 to 70°C and a softening temperature of 70 to 130°C. The toner according to claim 1, wherein the diol component (b) represented by formula [I] is polyoxypropylene(n)-2,2-bis(4-hydroxyphenyl)propane wherein n is a number of 2.1 to 2.5, and the amount of the units derived therefrom is up to 70% by mole; based on the total carboxylic acid component. The toner according to claim 1 or 2 in which the aliphatic diol component is selected from the group consisting of ethylene glycol, diethylene glycol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, neopentyl glycol and propylene glycol. The toner according to claim 3, wherein the aliphatic diol component is selected from the group consisting of ethylene glycol, neopentyl glycol and butanediol and the amount of the units derived therefrom is at least 30% by mole based on the total carboxylic acid component. The toner according to any preceding claim, which has a weight average molecular weight M w of 3,000 to 15,000, a number average molecular weight M n of 2,000 to 7,500, and a glass transition temperature T g of 40 to 70°C.

Inventors: FUNATO RYO, ITO HIROKAZU, KUBO SHINJI, TAJIRI NORIYUKI, TAKYU MASAYUKI, FUNATO, RYO, ITO, HIROKAZU, KUBO, SHINJI, TAJIRI, NORIYUKI, TAKYU, MASAYUKI, FUNATO, RYO C/O PRODUCTS DEVELOPMENT LAB., ITO, HIROKAZU C/O PRODUCTS DEVELOPMENT LAB., KUBO, SHINJI C/O TOYOHASHI PLANTS, TAJIRI, NORIYUKI C/O TOYOHASHI PLANTS, TAKYU, MASAYUKI C/O TOYOHASHI PLANTS
Applicants: MITSUBISHI RAYON CO, MITSUBISHI RAYON CO., LTD.
Application year: 1989
Main classification: G03G9
IPC codes: G03G9, C08G63, C09D167