ELASTIC POLYURETHANE FOAM AND PROCESS FOR ITS PRODUCTION

Abstract: An elastic polyurethane foam is produced by reacting, if necessary in the presence of a crosslinking agent, polyols (1) using a catalyst ( and isocyanate compd. ) a foaming agent and a foam-controlling agent. The polyols (1) have a high molecular weight. They are polyoxyalkylene polyols (2), or polymer dispersion polyols based on a matrix of polyoxyalkylene polyols. (2) have a hydroxy value of 5 - 38 and 2 - 8 hydroxy groups. For (2) the conditions Y 0.9 ( X - 10 ), 0.07 are satisified. where X is the hydroxy value ( mgKOH/g ); Y is the total degree of unsaturation (meq/g ) It is preferred that X 0 5 - 28 and Y 0.04. (2) contain 70 wt.% or more of oxypropylene and any number of oxyethylene groups. (2) contain 5 wt.% or more of terminal oxyethylene groups. The polymer dispersion polyols contains 1-40 wt.% of vinyl polymer fine particles. The amount of crosslinking agent is 0.2 - 10 pts. wt. based on 100 pts. wt. of polyol. The issocyanate is at least one of the aromatic polycyantes: trilane isocyanate, diphenylmethanediisocyanate, crude diphenylmeamethanediisocyanate, denatured compds. of these. The foaming agents is water or water and low-boiling pt. halogenated hydrocarbons.

Description: TECHNICAL FIELD The present invention relates to the use of a polyoxyalkylene polyol as defined in claim 1 for the manufacture of polyurethane flexible foam seat cushions for automobiles. BACKGROUND TECHNIQUE In recent years, various new studies have been made to improve the properties of polyurethane flexible foam. For example, reflecting a trend for grading up of e.g. automobiles, improvement of the vibration characteristics of seat cushions, is desired. The relation between the vibration of the car body and the human being is not uniform. However, it is suggested that it is effective for the improvement of the comfortable ride to take a particularly large attenuation of the frequency region (e.g. from 4 to 8 Hz or from 6 to 20 Hz) to which human being is particularly sensitive. Accordingly, it is considered possible to substantially improve the comfortable ride if the seat cushion is made of a polyurethane flexible foam having a resonant frequency lower than this frequency region. However, heretofore, no polyurethane flexible foam has been known which has a resonant frequency of less than 4 Hz. US-A-4,687,851 discloses polyurethane elastomers prepared from high equivalent weight polyahls. The obtained polymers are elastomeric materials having good resiliency and excellent tensile properties. EP-A-0 220 697 discloses flexible polyurethane foams obtained from polymer-polyols however, the document nothing about an unsaturation degree of a polyoxyalkylene polyol use. Further, the document does not disclose any resonant properties of the produced foams. The present invention provides a use of a polyoxyalkylene polyol having an oxypropylene group content of at least 70 % by weight, a terminal oxyethylene group content of at least 5 % by weight, a number of hydroxyl groups of from 2 to 8, a hydroxyl value (X mgKOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.04, provided that when X is from 32.5 to 38; Y satisfies the formula Y ≤ 0.9/(X-10), for the manufacture of polyurethane flexible foam seat cushions for automobiles, having an impact resilience of the core of at least 70 % (measured in accordance with JIS K 6401) and a resonant frequency of not higher than 3.5 Hz (measured in accordance with JAS O B407-82), said manufacture being defined according to claim 1. For the polyurethane flexible foam, it is essential that its resonant frequency is not higher than 3.5 Hz. In addition, the impact resiliency of the core is at least 70%, and further, the wet heat permanent strain is preferably not higher than 10%. Now, each starting material component in the present invention will be described. Polyoxyalkylene polyol The polyoxyalkylene polyol used as a starting material for polyurethane, is usually produced by ring-opening addition polymerization of an alkylene oxide such as propylene oxide to an initiator such as a polyhydric alcohol by means of an alkali catalyst such as an alkali metal hydroxide. In such a process, a monool having an unsaturated group is formed as a byproduct, and the production rate of this unsaturated monool increases with an increase of the molecular weight of the polyol (with a decrease of the hydroxyl value). The presence of this unsaturated monool is not in such a serious amount in the case of a polyoxyalkylene polyol having a hydroxyl value of about 56 which is widely used as a starting material for polyurethane flexible foam. However, in a polyoxyalkylene polyol having a low hydroxyl value which is used as a starting material for e.g. polyurethane elastomer, the presence of this unsaturated monool is likely to create a problem. For example, with a polyoxyalkylene polyol having a hydroxyl value of about 34, the total unsaturation degree usually becomes at least 0.1 meq/g. Further, it has been practically impossible to prepare a polyoxyalkylene polyol having a still lower hydroxyl value by means of an alkali catalyst, since its total unsaturation degree becomes remarkably high. Further, even if an flexible foam is produced by using a polyoxyalkylene polyol having a high total unsaturation degree, there will be problems such as a decrease in the hardness, a decrease in the impact resiliency, a deterioration in the compression permanent strain, a deterioration in the curability at the time of molding the foam, etc. The polyoxyalkylene polyol used in the present invention has a low unsaturation degree as compared with a starting material commonly employed for polyurethane flexible foam, whereby the conventional problems, particularly the problems observed in the case of employing a high molecular weight polyoxyalkylene polyol having a hydroxyl value of not higher than 38 (a decrease in the hardness, a decrease in the impact resiliency, a deterioration in the compression permanent strain and a deterioration in the curability at the time of molding the foam) can be controlled, and it is excellent in the vibration attenuation properties. Such a polyoxyalkylene polyol can usually be obtained by using a catalyst other than an alkali catalyst, for example, by using zinc diethyl, iron chloride, metal porphyrin or a double metal cyanide complex, as the catalyst. A particularly excellent polyoxyalkylene polyol is obtainable by the use of a double metal cyanide complex. Methods for producing such a polyoxyalkylene polyol are disclosed, for example, in the following documents: USP 3,829,505, USP 3,941,849, USP 4,355,188, USP 3,427,334, USP 3,427,335, USP 4,472,560, USP 4,477,589, EP 283,148 Further, in addition to the polyoxyalkylene polyol, a polyol having from 2 to 8, particularly from 2 to 4 hydroxyl groups, such as a polyester-type polyol, a hydroxyl group-containing polydiene-type polymer or a polycarbonate-type polyol, may optionally incorporated, as the case requires. It is particularly preferred to use at least one polyoxyalkylene polyol or a polymer-dispersed polyol containing such a polyoxyalkylene polyol as the matrix, or to use it as the main component in combination with a small amount (usually not more than 30% by weight) of a polyester-type or a hydroxyl group-containing polydiene-type polymer. The polyoxyalkylene polyol used in the present invention is a polyoxyalkylene polyol having at least 70% by weight, particularly at least 80% by weight, of oxypropylene groups derived from 1,2-propylene oxide, a terminal oxyethylene group content of at least 5 % by weight, a number of hydroxyl groups of from 2 to 8, a hydroxyl value (X mgKOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.04, provided that when X is from 32.5 to 38, Y satisfies the formula Y ≤ 0.9/(X-10). As the above polyoxyalkylene polyol, a polyoxyalkylene polyol having a high primary hydroxyl value is preferred. Such a polyoxyalkylene polyol has oxyethylene groups or polyoxyethylene block chains at its molecular terminals. The proportion of such oxyethylene groups present at the terminal portions is at least 5% by weight, more preferably from 5 to 30% by weight, most preferably from 5 to 20% by weight. The polyoxyalkylene polyol in the present invention may be a mixture of two or more different types. However, it is preferred that it does not substantially contain a polyoxyalkylene polyol with a hydroxyl value exceeding 38. In such a case, the hydroxyl value, the number of hydroxyl groups and the total unsaturation degree are represented by average values. In the present invention, the polyoxyalkylene polyol has the upper limit of Y being 0.07 when X is not higher than about 22.9. Further, the hydroxyl value is more preferably from 5 to 28. Polymer-dispersed polyol As the polyol of the present invention, a polymer-dispersed polyol can be employed. The polyol as the matrix for the polymer-dispersed polyol is required to be the above-mentioned polyoxyalkylene polyol. The polymer-dispersed polyol is a dispersion having fine polymer particles dispersed stably in this matrix. As the polymer, an addition polymerization polymer or a condensation polymerization polymer may be mentioned. A polymer-dispersed polyol wherein the matrix is a conventional polyol, is known and is widely used a polyol for polyurethane flexible foam. The polymer-dispersed polyol in the present invention can be produced by a conventional method using the above polyoxyalkylene polyol as the matrix. Further, a relatively small amount of a conventional polymer-dispersed polyol may be added to the above polyoxyalkylene polyol. In such a case, a polyol constituting the matrix of the conventional polymer-dispersed polyol will be added in a small amount to the above polyoxyalkylene polyol. Even in such a case, the relation of the hydroxyl value and the total unsaturation degree of the above polyoxyalkylene polyol is required to be satisfied as an average. Thus, the polyoxyalkylene polyol constituting the matrix for the polymer-dispersed polyol in the present invention, is required to satisfy the above requirements (e.g. the relation of the hydroxyl value and the total unsaturation degree). The fine polymer particles in the polymer-dispersed polyol are made of an addition polymerization type polymer such as a homopolymer or copolymer of acrylonitrile, styrene, methacrylate, an alkyl methacrylate, an alkyl acrylate or other vinyl monomer, or a condensation polymerization type polymer such as a polyester, polyurea, polyurethane or a melamine resin. By the presence of such fine polymer particles, the hydroxyl value of the entire polymer-dispersed polyol will usually be lower than the hydroxyl value of the polyol as the matrix. Accordingly, the hydroxyl value of the entire polymer-dispersed polyol having the above polyoxyalkylene polyol as the matrix, is preferably from 5 to 38, more preferably from 5 to 28. The content of the fine polymer particles in the polymer-dispersed polyol or in a mixture of such a polymer-dispersed polyol and the above polyoxyalkylene polyol, is usually not higher than 60% by weight, preferably not higher than 40% by weight. The amount of the fine polymer particles is not required to be large. On the other hand, even if the amount is excessive, there is no particular disadvantage other than the economical disadvantage. In most cases, they are sufficiently effective in an amount of not higher than 20% by weight. The presence of fine polymer particles in the polyoxyalkylene polyol is not essential. However, the presence is effective for the improvement of the hardness, the air permeability and other physical properties of the foam. Accordingly, the fine polymer particles are preferably present in an amount of at least 0.1% by weight, more preferably at least 1% by weight, most preferably at least 2% by weight. Crosslinking agent In the present invention, it is possible to react only the above polyoxyalkylene polyol having a low hydroxyl value (i.e. a high molecular weight) (provided that water is excluded) with the isocyanate compound. However, a low molecular weight polyfunctional compound reactive with an isocyanate group (which is called a crosslinking agent in the present invention) can be used together with the high molecular weight polyoxyalkylene polyol. This polyfunctional compound is a compound having two isocyanate-reactive groups such as hydroxyl groups, primary amino groups or secondary amino groups and having a molecular weight of not higher than 300, per isocyanate-reactive group. Such a crosslinking agent includes a compound which is usually called a crosslinking agent or a chain extender in the polyurethane technical field. Such a compound includes, for example, polyhydric alcohols, alkanolamines, polyamines, and low molecular weight polyoxyalkylene polyol type polyols obtained by adding small amounts of alkylene oxides to polyhydric alcohols, akanolamines, saccharides, polyamines, monoamines or polyhydric phenols. Further, low molecular weight polyester type polyols or polyamines may also be employed. Ethylene glycol, propylene glycol, 1,4-butanediol and glycerol, diethanolamine and triethanolamine, t-butyltolylenediamine, diethyltolylenediamine and chlorodiaminobenzene, are employed. Polyoxyalkylene type polyols having a hydroxyl value of at least 200 and from 3 to 8 hydroxyl groups may be used. Such a polyfunctional compound is used preferably in an amount of not higher than about 10 parts by weight, particularly not higher than 5 parts by weight, per 100 parts by weight of the high molecular weight polyol. There is no particular restriction as to the lower limit of the amount. However, in its use, adequate effectiveness is obtainable with an amount of about 0.2 part by weight. Polyisocyanate compound The polyisocyanate compound may be an aromatic, alicyclic or aliphatic polyisocyanate having at least two isocyanate groups, a mixture of at least two such polyisocyanates, as well as modified polyisocyanates obtained by modifying them. Specifically, there may be mentioned, for example, polyisocyanates such as tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), polymethylenepolyphenyl isocyanate (so called crude MDI), xylylene diisocyanate (XDI), isophorone diisocyanate (IPDI) and hexamethylene diisocyanate (HMDI), and their prepolymer type modified products, nulate modified products, urea modified products and carbodiimide modified products. Preferably, at least one aromatic polyisocyanate selected from TDI, MDI, crude MDI and their modified products, is employed. More preferably, a mixture comprising at least one of MDI, crude MDI and their modified products and TDI or its modified products, is employed. The amount of TDI is preferably from 50 to 100% by weight. The isocyanate group content in the polyisocyanate compound in the present invention is preferably at least 15% by weight, particularly preferably at least 20% by weight. Other starting material components For the reaction of the polyol and the polyisocyanate compound, it is required to employ a catalyst. As the catalyst, a metal compound catalyst such as an organotin compound for accelerating the reaction of the active hydrogen-containing group with the isocyanate group, or a tertiary amine catalyst such as triethylenediamine, may be used. Further, a polymerization catalyst for reacting isocyanate groups to one another, such as a metal salt of a carboxylic acid, may be used as the case requires. Further, a foam stabilizer for forming good foam, is used. As the foam stabilizer, a foam stabilizer of silicone type or a foam stabilizer of fluorine-containing compound type may, for example, be mentioned. Other optional additives include, for example, a filler such as silica, alumina or calcium carbonate, an antioxidant, an ultraviolet absorber, a stabilizer such as a photostabilizer, a colorant and a flame retardant. As mentioned above, in the present invention, as the foaming agent, a water-type foaming agent, a halogenated hydrocarbon such as R-11 (trichlorofluoromethane), R-12 (difluorodichloromethane), R-123 (1,1-dichloro-2,2,2-trifluoroethane), R-12B 2 (difluorodibromomethane), R-141b (1,1-dichloro-1-fluoroethane) or methylene chloride, butane, hexane, air or nitrogen, are employed. The water-type foaming agent may be water itself or a compound capable of generating water at the time of the reaction, such as a hydrate.R-11, R-12, R-123, R-12B2, R-141b or methylene chloride halogenated hydrocarbon may be used as a foaming agent in combination with the water-type foaming agent. In a case where a water-type foaming agent is employed as the foaming agent, a part of the above polyisocyanate compound reacts with water to generate carbon dioxide gas. Accordingly, the amount of the polyisocyanate compound used is calculated on the basis of the sum obtained by adding the water-type foaming agent to the total of the high molecular weight polyol and the low molecular weight polyfunctional compound, and it is preferred to use the polyisocyanate compound in an amount of from 0.8 to 1.3 equivalent relative to 1 equivalent of the sum. 100 Times of the equivalent of this polyisocyanate compound is usually called (isocyanate) index. Accordingly, the index of the polyisocyanate compound is preferably from 80 to 130. EXAMPLES The following polyoxyalkylene polyols were used as starting materials for polyurethane flexible foams described hereinafter. Each polyol was prepared by adding propylene oxide to an initiator of polyoxypropylene polyol having a molecular weight of from 400 to 600 by means of a zinc hexacyanocobaltate complex as a catalyst, then deactivating the catalyst, and adding ethylene oxide by means of an alkali catalyst, followed by purification to remove the catalyst component. In Table 1, the names of the obtained polyoxyalkylene polyols, and the numbers of hydroxyl groups (N), the hydroxyl values (X), the oxyethylene contents (EO) and the total unsaturation degrees (Y) of the polyoxyalkylene polyols, are shown. The polyols used for the purpose of comparison (polyols J, K, and L) are polyoxyalkylene polyols prepared by reacting propylene oxide to an initiator (glycerol) by means of an alkali catalyst, and then reacting ethylene oxide thereto, followed by purification. Name N EO (wt%) X (mgKOH/g) Y (meq/g) Polyol A 3 15 24 0.020 Polyol B 3 10 10 0.025 Polyol C 4 10 10 0.025 Polyol D 3 12 17 0.023 Polyol E 3 12 11 0.026 Polyol F 3 10 14 0.025 Polyol G 3 15 28 0.020 Polyol H 3 15 32 0.018 Polyol I 4 17 28 0.020 Polyol J 3 15 28 0.10 Polyol K 3 15 32 0.15 Polyol L 3 15 34 0.102 Polymer-dispersed polyols: Polymer-dispersed polyols containing the above polyoxyalkylene polyols as matrix and containing 20% by weight of fine particles of polyacrylonitrile, were used. The names of such polymer-dispersed polyols are represented by adding p to the names of the respective polyols (example: polyol Ap). Other materials used for the preparation of polyurethane flexible foams are as follows. Crosslinking agent: A: A sorbitol-propylene oxide-ethylene oxide adduct. Hydroxyl value: 450 (molecular weight of about 125 per hydroxyl group) Reference for comparison B: Diethanolamine Catalysts: A: Triethylenediamine solution ("Dabco 33LV" tradename) B: N-ethylmorpholine C: Stannous octoate D: Tertiary amine catalyst ("Kaolizer No. 1" tradename, sold by Kao Corporation) Foaming agent A: Water B: 1,1-Dichloro-2,2,2-trifluoroethane (R-123) C: 1,1-Dichloro-1-fluoroethane (R-141b) Foam stabilizer: A: Silicone type foam stabilizer ("L-5750S" tradename, sold by Nippon Unika K.K.) B: Silicone type foam stabilizer ("L-5309" tradename, sold by Nippon Unika K.K.) C: Silicone type foam stabilizer ("SF-2962" tradename, sold by Toray Silicone K.K.) D: Silicone type foam stabilizer ("SRX-274C" tradename, sold by Toray Silicone K.K.) Polyisocyanate compounds: A: TDI-80 B: Mixture of TDI-80 and crude MDI ("MR-200" tradename, sold by Nippon Polyurethane K.K.) in a weight ratio of 80/20. C: Modified MD2 for polyurethane flexible foam (NCO content: 27%) EXAMPLES 1 to 17 Using the starting materials as identified in Table 2, polyurethane flexible foams were prepared. The polyisocyanate compound was added to a mixture of all the starting materials except for the polyisocyanate compound, followed by stirring. The mixture was immediately injected into a mold of 350 mm x 350 mm and 100 mm in height heated to 60°C or 40°C (No. 1 and No. 17), and the mold was closed and left at room temperature for 5 minutes. Then, the molded polyurethane flexible foam was taken out from the mold. Then, the following physical properties of the foam were measured. The types of the starting materials, the amounts (represented by parts by weight, provided that the amount of the polyisocyanate compound used was represented by the isocyanate index (100 times of the equivalent ratio)), and the physical properties of the foam are shown in Table 2. The physical properties were measured by the following methods. Appearance: Visually evaluated Air flow: ASTM D1564 25% ILD: JIS K6401 Impact resilience: JIS K6401 Elongation: JIS K6401 Wet heat permanent strain: JIS K6401 Resonant frequency: JASO B407-82 6 Hz transmittance: JASO B407-82

Claims: Use of a polyoxyalkylene polyol having an oxypropylene group content of at least 70 % by weight, a terminal oxyethylene group content of at least 5 % by weight, a number of hydroxyl groups of from 2 to 8, hydroxyl value (X mgKOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.04, provided that when X is from 32.5 to 38, Y satisfies the formula Y ≤ 0.9/(X-10), for the manufacture of polyurethane flexible foam seat cushions for automobiles, having an impact resilience of the core of at least 70% (measured in accordance with JIS K 6401) and a resonant frequency of not higher than 3.5 Hz (measured in accordance with JAS 0 B407-82), said manufacture comprising reacting at least one high molecular weight polyol selected from the group consisting of said polyoxyalkylene polyol and a polymer-dispersed polyol containing said polyoxyalkylene polyol as the matrix, a crosslinking agent and a polyisocyanate compound in the presence of a catalyst, a foaming agent and a foam stabilizer as assisting agents, wherein the crosslinking agent is a polyfunctional compound having two isocyanate reactive groups and having a molecular weight of not higher than 300 per isocyanate-reactive group or glycerol, diethanolamine, triethanolamine, t-butyltolylenediamine, diethyltolylenediamine or chlorodiaminobenzene. The use according to Claim 1, wherein the polyoxyalkylene polyol has a hydroxyl value (X) of from 5 to 28 and a total unsaturation degree (Y) of not more than 0.04. The use according to Claim 1, wherein the polymer-dispersed polyol contains from 1 to 4°% by weight of fine polymer particles. The use according to Claim 3, wherein the fine polymer particles are fine particles of a vinyl polymer. The use according to Claim 1, wherein the crosslinking agent is used in an amount of from 0.2 to 10 parts by weight per 100 parts by weight of the polyol. The use according to Claim 1, wherein the polyisocyanate compound is an aromatic polyisocyanate. The use according to claim 1 wherein the foaming agent is water. or water and a halogenated hydrocarbon selected from R-11 (trichlorofluoromethane), R-12 (difluorodichloromethane). R-123 (1.1-dichloro-2.2,2-trifluoroethane), R-12B 2 (difluorodibromomethane), R-141b (1,1-dichloro-1-fluoroethane) or methylene chloride. Use of a polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight, a terminal oxyethylene group content of at least 5 % by weight, a number of hydroxyl groups of from 2 to 8, a hydroxyl value (X mgKOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.07, with X and Y being in the following relation: Y ≤ 0.9/(X-10) with the proviso that the formula is applicable in a range of x > 10 for the manufacture of polyurethane flexible foam seat cushions for automobiles, having an impact resilience of the core of at least 70% (measured in accordance with JIS K 6401) and a resonant frequency of not higher than 3.5 Hz (measured in accordance with JAS 0 B407-82), said manufacture comprising reacting a polymer-dispersed polyol wherein the matrix is the above-mentioned polyoxyalkylene polyol and fine polymer particles are dispersed stably in the matrix, from 0.2 to 10 parts by weight, per 100 parts by weight of the polymer-dispersed polyol, of a crosslinking agent and an aromatic polyisocyanate in an amount of from 0.8 to 1.3 equivalent of the total amount of the polymer-dispersed polyol, the crosslinking agent and water when a foaming agent contains water, in the presence of a catalyst, a foaming agent and a foam stabilizer, wherein the crosslinking agent is a polyfunctional compound having two isocyanate reactive groups and having a molecular weight of not higher than 300 per isocyanate-reactive group or glycerol, diethanolamine, triethanolamine, t-butyltolylenediamine, diethyltolylenediamine or chlorodiaminobenzene. The use according to Claim 8, wherein the polymer-dispersed polyol contains from 1 to 40% by weight of fine polymer particles. The use according to Claim 9, wherein the fine. polymer particles are fine particles of a vinyl polymer. The use according to Claim 8, wherein the polyoxyalkylene polyol has a hydroxyl value of from 5 to 28 and a total unsaturation degree of not more than 0.04.

Inventors: DOI TAKAO, SONOBE TSUNEHISA, TAKEYASU HIROMITSU, YAMAGUCHI YOSHIYUKI, DOI, TAKAO, SONOBE, TSUNEHISA, TAKEYASU, HIROMITSU, YAMAGUCHI, YOSHIYUKI
Applicants: ASAHI GLASS CO LTD, ASAHI GLASS CO., LTD.
Application year: 1989
Main classification: C08G18
IPC codes: C08J9, C08G18, C08G101