Water-repellent film-forming composition

Abstract: A water-repellent film-forming composition comprising [A] a polymer selected from the group consist­ ing of (a) a (co)polymer composed of 5 to 100 % by weight of a fluoroalkyl group-containing (meth)acrylic monomer represented by the following general formula (I) wherein R₁ represents a hydrogen atom or a methyl group, ℓ is an integer of 1 to 11, and Rf represents -C m F 2m+1 or -C n F 2n H in which m is an integer of 1 to 20 and n is an integer of 1 to 20, and 0 to 95 % by weight of an un­ saturated monomer copolymerizable with the fluoroalkyl group-containing (meth)acrylic monomer, (b) a copolymer composed of 0.1 to 75 % by weight of a silicon-containing polymerizable unsaturated monomer represented by the following general formula (II) wherein R₂ represents a hydrogen atom or a methyl group, and R₃ represents a group of the formula in which j is an integer of 0 or 1, k is an integer of 0 to 6, p is an integer of 1 to 5, q is an integer of 1 to 20, r is an integer of 0 to 2, s is an integer of 1 to 3, and r + s=3, and 25 to 99.9 % by weight of an unsaturated monomer copolymerizable with the silicon-containing polymerizable unsaturated monomer, and (c) a mixture of the (co)polymer (a) and the copolymer (b), and [B] a particulate material having an average particle diameter of not more than 5 micrometers.

Description: This invention relates to a water-repellent film-forming composition comprising a fluoroalkyl group-containing polymer and a silicon-containing polymer and a particulate material as main components. Typical water-repellent materials include, for example, hydrocarbon-type polymer materials typified by polyethylene, fluorine resin-type polymer materials typified by polytetrafluoroethylene and silicone polymer materials. EP-A-0 065 388 refers to hard coatings made from a copolymer containing alkoxysilanealkylacrylates moieties and a mineral charge. DE-A-3 609 459 refers to adherent coatings of a repellent copolymer containing more than 50% of a perfluoroalkylacrylate and as remainder a trimethoxysilanealkylacrylate. FR-A-2 592 055 describes a chemical resistant coating from more than 95% perfluoroalkylacrylate copolymerised with other acrylics. US-A-2 900 355 discloses a chemical resistant rubber on the basis of dihydroperfluorobutylacrylate with carbon black filler. Chemic. Abstr. 107 :24885 (1987) describes a washing resistant coating resulting of the polymerisation of a perfluoroalkylacrylate in the presence of trimethoxymercaptopropylsilane. Polytetrafluoroethylene has a "contact angle with water", a measure of the degree of hydrophobicity, of about 120°, and is a material having particularly high hydrophobicity (the polar component γ p of its surface tension is low). The degree of water repellency of polytetrafluoroethylene is still insufficient under some environmental conditions in which it is used. It is therefore desired to develop a material having higher water repellency. To achieve this desire, the present inventors have made extensive investigations, and have finally developed a film-forming composition which has a higher "contact angle with paraffin" than that of a polytetrafluoroethylene film (the dispersed component γ d of its surface tension is lower than that of polytetrafluoroethylene) and higher water repellency than the polytetrafluoroethylene film. Thus, the present invention provides a water-repellent film-forming composition comprising [A] a mixture of (a) a (co)polymer composed of 5 to 100% by weight of a fluoroalkyl group-containing (meth)acrylic monomer represented by the following general formula (I): wherein R₁ represents a hydrogen atom or a methyl group, ℓ is an integer of 1 to 11, and Rf represents -C m F 2m+1 or -C n F 2n H in which m is an integer of 1 to 20 and n is an integer of 1 to 20, and 0 to 95% by weight of an unsaturated monomer copolymerizable with the fluoroalkyl group-containing (meth)acrylic monomer, and (b) a copolymer composed of 0.1 to 75% by weight of a silicon-containing polymerizable unsaturated monomer represented by the following general formula (II): wherein R₂ represents a hydrogen atom or a methyl group, and R₃ represents a group of the formula: in which j is an integer of 0 or 1, k is an integer of 0 to 6, p is an integer of 1 to 5, q is an integer of 1 to 20, r is an integer of 0 to 2, s is an integer of 1 to 3, and r + s = 3, and 25 to 99.9% by weight of an unsaturated monomer copolymerizable with the silicon-containing polymerizable unsaturated monomer, and [B] a particulate material having an average particle diameter of not more than 5 micrometers, the proportion of the particulate material being 20 to 600 parts by weight per 100 parts by weight of the mixture [A]. The composition of this invention will be described below in detail. Polymer [A] (Co)polymer (a) The (co)polymer (a) that can be used in the water-repellent film-forming composition of this invention denotes a homopolymer of a fluoroalkyl group-containing (meth)acrylic monomer of general formula (I), a copolymer of monomers of general formula (I) with each other, or a copolymer of the fluoroalkyl group-containing (meth)acrylic monomer with at least one other unsaturated monomer copolymerizable with it. The fluoroalkyl group-containing (meth)acrylic monomer used in the preparation of the (co)polymer (a) is a monomer represented by the following general formula (I) [to be sometimes referred to as monomer (I)] wherein R₁ represents a hydrogen atom or a methyl group; ℓ is an integer of 1 to 11, preferably 1 to 6, more preferably 1 to 3; and Rf represents a group of the formula -C m F 2m+1 or -C n F 2n H in which m is an intger of 1 to 20, preferably 1 to 10, especially preferably 2 to 8, and n is an integer of 1 to 20, preferably 1 to 10, more preferably 2 to 8. Examples of the monomer (I) include perfluoroalkyl (meth)acrylates having a perfluoroalkyl group with 1 to 20 carbon atoms, such as 2-perfluorooctylethyl (meth)acrylate, CH₂=CH-COO-CH₂CH₂-C₈F₁₇, 2-perfluoroisononylethyl (meth)acrylate, 2-perfluorononylethyl (meth)acrylate, 2-perfluorodecylethyl (meth)acrylate, 2-perfluorobutylethyl (meth)acrylate, perfluoromethylmethyl (meth)acrylate, perfluoroethylmethyl (meth)acrylate, perfluorobutylmethyl (meth)acrylate, perfluorooctylmethyl (meth)acrylate, perfluorodecylmethyl (meth)acrylate, perfluoromethylpropyl (meth)acrylate, perfluoropropylpropyl (meth)acrylate, perfluorooctylpropyl (meth)acrylate, perfluorooctylamyl (meth)acrylate, and perfluorooctylundecyl (meth)acrylate; and fluoroalkylalkyl (meth)acrylates resulting from substitution of a hydrogen atom for one fluorine atom of the perfluoroalkyl moiety in these perfluoroalkylalkyl (meth)acrylates such as 2-hydrogen hexafluoropropylmethyl acrylate, CH₂=CH-COO-CH₂-CF₂CFHCF₃ , 4-hydrogen octafluorobutylmethyl methacrylate, 6-hydrogen dodecafluorohexylmethyl methacrylate, 8-hydrogen hexadecafluorooctylmethyl acrylate, and 2-hydrogen tetrafluoroethylmethyl methacrylate. Especially preferred among them are 2-perfluorooctylethyl methacrylate and 2-perfluoroisononylethyl methacrylate. Examples of the other unsaturated monomer (to be referred to as the "comonomer") copolymerizable with the monomer (I) include C₁₋₁₈ alkyl esters of (meth)acrylic acid such as methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, butyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, n-octyl acrylate, lauryl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, isopropyl methacrylate, butyl methacrylate, hexyl methacrylate, 2-ethylhexyl methacrylate, n-octyl methacrylate and lauryl methacrylate; glycidyl esters of (meth)acrylic acid such as glycidyl acrylate and glycidyl methacrylate; C₂₋₁₈ alkoxyalkyl esters of (meth)acrylic acid such as methoxybutyl acrylate, methoxybutyl methacylate, methoxyethyl acrylate, methoxyethyl methacrylate, ethoxybutyl acrylate, and ethoxybutyl methacrylate; C₂₋₆ alkenyl esters of (meth)acrylic acid such as allyl acrylate and allyl methacrylate; C₂₋₈ hydroxyalkyl esters of (meth)acrylic acid such as hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate and hydroxypropyl methacrylate; mono- or di-(C₁₋₆ alkyl)aminoalkyl esters of (meth)acrylic acid such as dimethylaminoethyl acrylate, diethylaminoethyl acrylate, dimethylaminoethyl methacrylate and diethylaminoethyl methacrylate, dimethylaminopropyl methacrylate, methylaminoethyl methacrylate; acrylamide and methacrylamide; acrylic acid and methacrylic acid; (meth)acryloyloxyalkylpolymethylsilicones represented by the following formula wherein R₄ represents a methyl group or a hydrogen atom, t is an integer of 1 to 50, preferably 1 to 30, more preferably 1 to 15, such as gamma-(meth)acryloyloxypropylpolymethylsilicone; fluoroethers having a (meth)acryloyloxy group, such as vinyl aromatic compounds such as styrene, styrenepentafluoride, alpha-methylstyrene and vinyltoluene; and unsaturated monomers such as acrylonitrile, methacrylonitrile, acrolein, methacrolein, butadiene and isoprene. The C₁₋₁₈ alkyl esters of (meth)acrylic acid and styrene are preferred among these comonomers. Another preferred group of comonomers are silicon-containing polymerizable unsaturated monomers represented by the following general formula (II) wherein R₂ represents a hydrogen atom or a methyl group, and R₃ represents a group of the formula wherein j is an integer of 0 or 1, k is an integer of 0 to 6, preferably 1 to 4, more preferably 2 or 3, p is an intger of 1 to 5, preferably 1 to 3, q is an integer of 1 to 20, preferably 1 to 10, more preferably 1 to 4, r is an integer of 0 to 2, s is an integer of 1 to 3, and r + s=3 . Specific examples of the comonomer of general formula (II) include vinyltrimethoxysilane, vinyltriethoxysilane, gamma-acryloyloxypropyltrimethoxysilane, gamma-methacryloyloxypropyltrimethoxysilane, gamma-methacryloyloxypropylmethyldimethoxysilane, vinylmethyldimethoxysilane, vinyldimethylmethoxysilane and gamma-methacryloyloxypropyldimethylmethoxysilane. Of these, gamma-methacryloyloxypropyltrimethoxysilane and gamma-methacryloyloxypropylmethyldimethoxysilane are preferred. The proportions of the monomer (I) and the comonomer are 5 to 100 % by weight, preferably 10 to 100 % by weight, more preferably 20 to 100% by weight, for the monomer (I) and 0 to 95 % by weight, preferably 0 to 90 % by weight, more preferably 0 to 80 % by weight, for the comonomer based on the total weight of the two. If the amount of the monomer (I) is less than 5 % by weight, it is generally difficult to expect a sufficient water-repelling effect. When the silicon-containing polymerizable unsaturated monomer of formula (II) is used as the comonomer, the copolymer (a) is preferably composed of (i) 5 to 99.9 % by weight, preferably 30 to 97.5 % by weight, especially preferably 50 to 97.5 % by weight, of the monomer (I), (ii) 0.1 to 75 % by weight, preferably 2.5 to 50 % by weight, preferably 2.5 to 30 % by weight of the silicon-containing polymerizable unsaturated monomer of formula (II), and (iii) 0 to 94.9 % by weight, preferably 0 to 67.5 % by weight, especially preferably 0 to 40 % by weight, of the other comonomer mentioned above. Polymerization of the monomers for producing the (co)polymer (a) is carried out by a method known per se , for example by the same method as in the production of an ordinary acrylic resin, and any of solution polymerization and emulsion polymerization can be employed. The solvent used is a good solvent for the resulting polymer. For example, trichlorotrifluoroethane, m-xylene hexafluoride and tetrachlorohexafluorobutane are preferably used. As a polymerization initiator, usual peroxides or azo compounds, such as benzoyl peroxide, azo-bis-(dimethylvaleronitrile) and azobisisobutyronitrile, may be used. The preferred reaction temperature is generally 40 to 140 °C. Preferably, the (co)polymer (a) has a number average molecular weight of usually about 3,000 to about 500,000, more preferably about 3,000 to about 70,000, and especially preferably about 5,000 to about 45,000. If its number average molecular weight exceeds about 500,000, formation of a phase-separated-structure becomes difficult at the time of film formation. On the other hand, if the number average molecular weight is below about 3,000, the phase-separated-structure after the film formation changes rheologically and the water repellency tend to be degraded with the lapse of time. Copolymer (b) The copolymer (b) which is used as a polymer component in the composition of this invention is a copolymer of the silicon-containing polymerizable unsaturated monomer of general formula (II) and the other unsaturated monomer copolymerizable with the silicon-containing polymerizable unsaturated monomer. The silicon-containing polymerizable unsaturated monomer is a monomer represented by general formula (II) wherein R₂ represents a hydrogen atom or a methyl group, and R₃ represents a group of the formula in which j is an integer of 0 or 1, k is an integer of 0 to 6, preferably 1 to 4, especially preferably 2 or 3, p is an integer of 1 to 5, especially preferably 1 to 3, q represents an integer of 1 to 20; preferably 1 to 10, especially preferably 1 to 4, r represents an integer of 0 to 2, s represents an integer of 1 to 3, and r + s=3 [to be referred to as monomer (II)]. Specific examples of the monomer (II) are vinyltrimethoxysilane, vinyltriethoxysilane, gamma-acryloyloxypropyltrimethoxysilane, gamma-methacryloyloxypropyltrimethoxysilane, gamma-methacryloyloxypropylmethyldimethoxysilane, vinylmethyldimethoxysilane, vinyldimethylmethoxysilane and gamma-methacryloyloxypropyldimethylmethoxysilane. Of these, gamma-methacryloyloxypropyltrimethoxysilane and gamma-methacryloyloxypropylmethyldimethoxysilane are preferred. Examples of the other unsaturated monomer (comonomer) which is copolymerizable with the monomer of formula (II) may be the unsaturated monomers cited above as examples of the unsaturated monomers copolymerizable with the monomer (I) in the production of the (co)polymer (a). C₁₋₁₈ alkyl (meth)acrylates are preferred. The proportion of the monomer (II) and the other unsaturated monomer (comonomer) copolymerizable with the monomer (II) may be 0.1 to 75 % by weight, preferably 0.1 to 40 % by weight, especially preferably 0.1 to 20 % by weight, for the monomer (II) and 25 to 99.9 % by weight, preferably 60 to 99.9 % by weight, especially preferably 80 to 99.9 % by weight, for the copolymerizable unsaturated monomer (comonomer), based on the total weight of the two. If the amount of monomer (II) is less than 0.1 % by weight, curability is usually inferior and the dispersion of the particulate material is not well carried out. On the other hand, if it exceeds 75 % by weight, many silanol groups are formed by the hydrolysis of silylalkoxy groups, and the hydrophobicity of the composition tends to be unable to be retained. The copolymer (b) may be produced by a known polymerization method, for example, by the same solution polymerization method as in the production of ordinary acrylic resins. Specifically, it is preferred to add a small amount of an alcohol solvent to the polymerization solution and perform the polymerization in the presence of a polymerization initiator such as a peroxide or an azo compound. The copolymer (b) in this invention generally has a number average molecular weight of about 4,000 to about 200,000, preferably about 8,000 to about 70,000, especially preferably 8,000 to 50,000. Mixture (c) In the composition of this invention, the (co)polymer (a) and the copolymer (b) are used in a combination. The mixing ratio of the copolymer (a) to the copolymer (b) is not critical. The weight ratio of the (co)polymer (a) to the copolymer (b) is usually from 97.5:2.5 to 30:70, preferably from 97.5:2.5 to 50:50, more preferably from 97.5:2.5 to 70:30. Particulate material [B] The particulate material used in the composition of this invention is an organic or inorganic solid particulate material having an average particle diameter of not more than 5 micrometers, preferably not more than 3 micrometers, more preferably not more than 1 micrometer. It is important that the particulate material should exist as particles in the resulting film without dissolving in the polymer component. Examples of the solid particulate material are fine particles of silica, fine particles of fluorocarbons and carbon black. Of these, the fine silica particles are preferred. Particularly preferred are fine silica particles treated with a hydrophobizing compound such as silazane The smoothness of the surface of the resulting film can be improved by incorporating completely spherical fine particles such as completely spherical silica particles as the particulate material. If the particulate material has an average particle diameter of more than 5 micrometers, the resulting film has a very uneven surface when observed microscopically, and tends to have reduced water repellency. In the present invention, the proportions of the polymer [A] and the particulate material [B] are not particularly limited, and may be varied widely. Generally, for obtaining a film having satisfactory water repellency and other properties, the particulate material [B] is added in an amount of 20 to 600 parts by weight, preferably 50 to 450 parts by weight, especially preferably 80 to 300 parts by weight, per 100 parts by weight of the polymer [A] (as solids). As required, the composition of this invention may contain additives usually employed for paints, such as solvents, coloring agents (dyes, pigments), and surfactants, in addition to the polymer [A] and the particulate material [B]. The composition of this invention may be prepared by mixing the polymer [A] and the particulate material [B] and optionally the above additives by using general agitating or dispersing methods, for example by using a dissolver, a steel ball mill, a pebble mill, a sand mill or an attriter. The water-repellent film-forming composition of this invention may be directly coated on the surface of a substrate such as a metal, plastics, glass or wooden material or as a top coat on a film pre-formed on such a substrate. For example, by coating the composition of this invention on a fin material of a heat exchanger, its clogging owing to the adhesion of dew, frost or ice to the fin material can be prevented, and therefore, the decrease of the heat exchanging efficiency can be prevented. Furthermore, by coating the composition of this invention on insulators of high-voltage power cables, current short-circuiting at the time of wind, water and salt hazards can be circumvented. The composition of this invention may be molded and laminated to the surface of an article. Coating of the composition of this invention may be accomplished by a known coating method such as spray coating, brush coating or roller coating. A good film can be obtained from the composition of this invention by coating it to a dry film thickness of usually 1 to 50 micrometers, preferably 10 to 30 micrometers, and drying the coating at a temperature from room temperature to 130 °C. When the surface of the film formed from the composition of this invention is observed through a micrograph, raised and depressed portions of micron size are seen. From contact angles, the surface energy γ can be calculated from the following equation. γ = γ p + γ d (mN/m) wherein γ d = 32.8 (1 + cosϑ p )/4 γ p = {72.8 (1 + cosϑ w ) - 2√ 21.6γ d }²/204 ϑ p : contact angle with paraffin ϑ w : contact angle with water The surface energy γ of a film formed from the composition of this invention is usually not more than 4.2 mN/m which is much lower than that of Teflon having a low surface energy (γ=about 21 mN/m). This is considered to suggest the relation of the shape of the surface and the apparent contact angle advocated by Wentzel et al. On a surface having such a low surface energy, the adhesive strength of water droplets, etc. is very small, and the water droplets become spherical, therefore rapidly leave the surface. Since the surface of a coated film formed from the composition of this invention has the above-mentioned properties, the composition of this invention is very useful for preventing water adhesion, snow adhesion and ice adhesion, and for preventing current short-circuiting by water adhesion. The following examples illustrate the present invention more specifically. In these examples, parts and percentages are by weight. [Examples of producing fluoroalkyl group-containing copolymers] PRODUCTION EXAMPLE 1 Into a 1-liter flask were precisely weighed 350 parts of 2-perfluorooctylethyl methacrylate, 150 parts of 2-perfluorooctylethyl acrylate and 80 parts of hexafluoro-m-xylene (HFMX for short), and well mixed with stirring to form a mixed solution of the monomers and the solvent. The mixed solution was transferred to a 1-liter dropping funnel. A 1-liter four-necked flask fitted with a reflux condenser, a thermometer and a stirrer was provided and the 1-liter dropping funnel containing the mixed solution was attached to the flask, and 200 parts of the mixed solution was transferred to the four-necked flask. With stirring, the temperature was raised to 105 to 110 °C. Then, while maintaining this temperature, 0.8 part of azobisisobutyronitrile (AIBN for short) as a polymerization catalyst was added [at this time, the reaction system had to be set up such that the flask was cooled to enable the exotherm to subside). Subsequently, the mixed solution was dropped at a rate of 50 parts/15 minutes from the dropping funnel, and every 15 minutes, 0.2 part of AIBN was added. Twenty minutes after the end of addition, 134 parts of HFMX was added to the flask. The temperature wes raised to 115 to 120 °C, and 0.5 part by weight of AIBN was added every 30 minutes five times. One hour and thirty minutes after the final addition of AIBN, cooling of the flask was started. After the temperature reached 60 °C, 286 parts of HFMX was added as a diluting solution to terminate the reaction. The resulting fluoroalkyl group-containing copolymer solution was pale yellow and had a Gardner viscosity of F and a non-volatile content of 48.7 %. PRODUCTION EXMAPLE 2 Production Example 1 was repeated except that a mixed solution composed of 280 parts of 2-perfluorooctylethyl methacrylate, 140 parts of 2-perfluorooctylethyl acrylate, 80 parts of styrene and 80 parts of HFMX was used as the mixed monomer-solvent solution. PRODUCTION EXAMPLE 3 Production Example 1 was repeated except that a mixed solution composed of 320 parts of 2-perfluorooctylethyl methacrylate, 175 parts of perfluorooctylethyl acrylate, 5 parts of 2-hydroxyethyl acrylate, 70 parts of HFMX and 10 parts of butyl acetate was used as the monomer-solvent mixed solution, and 250 parts of HFMX and 36 parts of n-butyl alcohol were used as a diluting solvent. The resulting resin solution was pale yellow and had a Gardner viscosity of G and a non-volatile content of 49.1 %. [Examples of producing silicon-containing copolymers] PRODUCTION EXAMPLE A Two hundred parts of isobutyl acrylate, 100 parts of lauryl methacrylate, 200 parts of gamma-methacryloyloxypropyltrimethoxysilane and 33 parts of n-butyl alcohol were precisely weighed into a 1-liter flask and well mixed with stirring. To the mixture was added 7.5 parts of AIBN as a polymerization initiator, and dissolved to form a monomer-solvent-initiator mixed solution. The mixed solution was transferred to a 1-liter dropping funnel. Two hundred parts of butyl acetate and 100 parts of n-butyl alcohol were introduced into a 2-liter flask equipped with a reflux condenser, a thermometer and a stirrer, and the mixture was heated and maintained at 110°C. While this temperature was maintained, the mixed solution was added dropwise from the dropping funnel into the flask over 2 hours. One hour after the end of the addition, a mixture of 1 part of AIBN and 170 parts of butyl acetate was added dropwise over 1.5 hours. After the end of addition, the temperature was elevated to 120°C, and the reaction was carried out for 2 hours, the reaction mixture was then cooled. The resulting silicon-containing copolymer solution was colorless and tranparent and had a Gardner viscosity of P and a non-volatile content of 51.0 %. PRODUCTION EXAMPLE B Production Example A was repeated except that a mixed solution composed of 200 parts of isobutyl acrylate, 100 parts of styrene, 190 parts of methyl methacrylate, 10 parts of vinyltrimethoxysilane, 33 parts of n-butyl alcohol and 7.5 parts of AIBN was used as the monomer-solvent-initiator mixed solution. The resulting silicon-containing copolymer solution was colorless and tranparent and had a Gardner viscosity of V and a non-volatile content of 51.2 %. EXAMPLE 1 One hundred parts of the silicon-containing copolymer resin solution obtained in Production Example A, 100 parts of the fluoroalkyl group-containing copolymer resin solution obtained in Production Example 1, 600 parts of 1,1,2-trichloro-1,2,2-trifluoroethane, 600 parts of HFMX and 30 parts of hydrophobic silica A were mixed and dispersed by a shaker to form a composition. EXAMPLES 2-10 AND COMPARATIVE EXAMPLES 1-2 By operating in the same way as in Example 1, compositions of Examples 2-10 and Comparative Examples 1 and 2 were obtained except that the blending recipes shown in Table 1 were used. Method of preparing test panel Each of the compositions obtained in Examples 1 to 10 and Comparative Examples 1 and 2 was spray-coated on an aluminum panel treated with chromium phosphate so that the weight of the dried coat would become about 30 g/m². The coated panel was left to stand at room temperature for 24 hours to give a test panel. The various tests described below were carried out on the test panel, and the results are shown in Table 1. COMPARATIVE EXAMPLE 3 A polytetrafluoroethylene film was laminated on an aluminum plate to prepare a test panel. The test panel was tested as above, and the results are shown in Table 1.

Claims: A water-repellent film-forming composition comprising [A] a mixture of (a) a (co)polymer composed of 5 to 100% by weight of a fluoroalkyl group-containing (meth)acrylic monomer represented by the following general formula (I): wherein R₁ represents a hydrogen atom or a methyl group, ℓ is an integer of 1 to 11, and Rf represents -C m F 2m+1 or -C n F 2n H in which m is an integer of 1 to 20 and n is an integer of 1 to 20, and 0 to 95% by weight of an unsaturated monomer copolymerizable with the fluoroalkyl group-containing (meth)acrylic monomer, and (b) a copolymer composed of 0.1 to 75% by weight of a silicon-containing polymerizable unsaturated monomer represented by the following general formula (II): wherein R₂ represents a hydrogen atom or a methyl group, and R₃ represents a group of the formula: in which j is an integer of 0 or 1, k is an integer of 0 to 6, p is an integer of 1 to 5, q is an integer of 1 to 20, r is an integer of 0 to 2, s is an integer of 1 to 3, and r + s = 3 , and 25 to 99.9% by weight of an unsaturated monomer copolymerizable with the silicon-containing polymerizable unsaturated monomer, and [B] a particulate material having an average particle diameter of not more than 5 micrometers, the proportion of the particulate material being 20 to 600 parts by weight per 100 parts by weight of the mixture [A]. The composition of claim 1 in which in the general formula (I) R₁ represents a hydrogen atom or a methyl group, ℓ is an integer of 1 to 6, and Rf represents -C m F 2m+1 or -C n F 2n H where m is an integer of 1 to 10 and n is an integer of 1 to 10. The composition of claim 1 in which the fluoroalkyl group-containing (meth)acrylic monomer is 2-perfluorooctylethyl methacrylate or 2-perfluoroisononylethyl methacrylate. The composition of claim 1 in which the other unsaturated monomer copolymerizable with the fluoroalkyl group-containing (meth)acrylic monomer is selected from C₁₋₁₈ alkyl esters of (meth)acrylic acid and styrene. The composition of claim 1 in which the (co)polymer (a) is a (co)polymer composed of 10 to 100% by weight of the fluoroalkyl group-containing (meth)acrylic monomer of formula (I) and 0 to 90% by weight of another unsaturated monomer copolymerizable with the monomer of formula (I). The composition of claim 1 in which the (co)polymer (a) is composed of 5 to 99.9% by weight of the fluoroalkyl group-containing (meth)acrylic monomer of formula (I), 0.1 to 75% by weight of a silicon-containing polymerizable unsaturated monomer represented by the following general formula (II): wherein R₂ represents a hydrogen atom or a methyl group, and R₃ represents a group of the formula: in which j is an integer of 0 or 1, k is an integer of 0 to 6, p is an integer of 1 to 5, q is an integer of 1 to 20, r is an integer of 0 to 2, s is an integer of 1 to 3, and r + s = 3 , and 0 to 94.9% by weight of another unsaturated monomer copolymerizable with the fluoroalkyl group-containing (meth)acrylic monomer. The composition of claim 6 in which the silicon-containing polymerizable unsaturated monomer of formula (II) is selected from gamma-methacryloyloxypropyltrimethoxysilane and gamma-methacryloyloxypropylmethyldimethoxysilane. The composition of claim 1 in which the (co)polymer (a) has a number average molecular weight of about 3,000 to about 500,000. The composition of claim 1 in which in formula (II) R₂ represents a hydrogen atom or a methyl group and R₃ represents a group of the following formula: in which j is an integer of 0 or 1, k is an integer of 1 to 4, p is an integer of 1 to 3, q is an integer of 1 to 10, r is an integer of 0 to 2, s is an integer of 1 to 3, and r + s = 3 . The composition of claim 1 in which the silicon-containing polymerizable unsaturated monomer is selected from gamma-methacryloyloxypropyltrimethoxysilane and gamma-methacryloyloxypropylmethyldimethoxysilane. The composition of claim 1 in which the other unsaturated monomer copolymerizable with the silicon-containing polymerizable unsaturated monomer is selected from C₁₋₁₈ alkyl esters of (meth)acrylic acid and styrene. The composition of claim 1 in which the copolymer (b) is a copolymer composed of 0.1 to 40% by weight of the silicon-containing polymerizable unsaturated monomer of formula (II) and 60 to 99.9% by weight of another unsaturated monomer copolymerizable with the monomer of formula (II). The composition of claim 1 in which the mixture [A] is a mixture of the (co)polymer (a) and the copolymer (b) in a weight ratio of from 97.5:2.5 to 30:70. The composition of claim 13 in which the weight ratio of the (co)polymer (a) to the copolymer (b) is from 97.5:2.5 to 50:50. The composition of claim 1 in which the particulate material [B] has an average particle diameter of not more than 3 micrometers. The composition of claim 1 in which the particulate material [B] is selected from fine silica powder, fine fluorocarbon powder and carbon black. The composition of claim 1 in which the particulate material [B] is a fine silica powder optionally treated with a hydrophobizing compound such as silazane. The composition of claim 1 in which the amount of the particulate material [B] is 50 to 450 parts by weight per 100 parts by weight of the polymer [A] (as solids). An article coated with the composition of claim 1.

Inventors: KOGURE HIDEO C O GIJUTSUHONBU, MURASE HEIHACHI C O GIJUTSUHON, NANISHI KIYOSHI C O GIJUTSUHON, KOGURE, HIDEO C/O GIJUTSUHONBU OF, MURASE, HEIHACHI C/O GIJUTSUHONBU OF, NANISHI, KIYOSHI C/O GIJUTSUHONBU OF
Applicants: KANSAI PAINT CO LTD, KANSAI PAINT CO. LTD.
Application year: 1989
Main classification: C09D133
IPC codes: C09D143, C09D133, C08L33, C08L43