The stabilization of dye images produced in photographic materials

Abstract: A photographic silver halide material com­ prises an organophosphorus dye stabilizer represented by the formula: wherein A represents the atoms necessary to complete a substituted or unsubstituted heterocyclic ring; R₁ represents substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl, or a heterocyclic group; Y is an oxygen or a sulfur atom; and, n is 0 or 1. Such a photographic silver halide material enables improved stability of dye images in the material.

Description: The invention relates to the stabilization of dye images produced in photographic materials. More particularly, it relates to the use of certain organophosphorus compounds as stabilizers for improving the stability of dye images obtained by colour developing coupler-incorporated photographic silver halide materials. A common form of colour photographic material comprises red-, green- and blue-sensitive silver halide emulsion layers in or adjacent to which are incorporated cyan-, magenta- and yellow-dye forming couplers, respectively. On development of such a material with a developer containing p -phenylenediamine colour developing agent, the oxidation product produced on reduction of the silver halide by the developing agent reacts with the appropriate coupler to give image dye. The dye image obtained by colour development can deteriorate as a result of the action of light, heat and/or humidity and various measures are known for reducing such deterioration. U.S. Patent No. 4,326,022 describes the use of high boiling organophosphorus coupler solvents which are said to improve the resistance of developed dye images to such deterioration. While dye stabilization can be achieved in this way, it is desirable to be able to improve dye stability without putting any restriction on the coupler solvent employed. Japanese Patent No. 48-32728 describes the use of certain open-chain phosphorus acid esters to improve dye stability in photographic materials. The esters may be liquids or solids. The present invention provides heterocyclic organophosphorus compounds which can be incorporated in a colour photographic material to improve dye stability independently of the coupler solvent used. Unlike the high boiling solvents described in the prior art, the compounds used in the invention are solids which can be readily obtained in pure form. Further, the compounds used in the invention are more resistant to hydrolysis than the open-chain phosphorus acid esters described in the prior art. An additional advantage of the compounds of the invention is that they can be prepared easily and at low cost. The structural features of the compounds can be chosen to maintain and even improve other desirable characteristics of the photographic system such as dispersion stability, coupling activity, dye hue and emulsion photosensitivity. According to the present invention there is provided a photographic material comprising a support bearing at least one developable silver halide emulsion layer and, incorporated in that layer or a water-permeable layer adjacent thereto, a dye-forming coupler, said material also containing, incorporated in the coupler-containing layer or a water-permeable layer adjacent thereto, as a dye stabilizer, an organophosphorus compound having the formula wherein A represents the atoms necessary to complete an optionally substituted heterocyclic ring; R₁ represents substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl, or heterocyclyl; Y is an oxygen or a sulphur atom; and, n is 0 or 1. In a preferred embodiment of the invention the organophosphorus compound is represented by the formula wherein R₁, Y and n are as defined above; each Z independently represents the atoms necessary to complete an optionally substituted benzene ring; and, X is a single bond or a linking group wherein a single atom separates the benzene rings. Particularly preferred organophosphorus compounds have the formula wherein Y, n, R₁ and X are as defined above; and, each of R₂, R₃, R₄ and R₅ independently represents hydrogen, substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl or heterocyclyl. Examples of linking group X include substituted or unsubstituted methylene; substituted or unsubstituted alkylidene e.g. butylidene or 3,5,5,-trimethylhexylidene; a heteroatom e.g. oxygen or sulphur; and sulphonyl. Preferably, X is -CR₆R₇- in which each of R₆ and R₇ independently represents hydrogen, substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl or heterocyclyl. Preferably, at least one of R₆ and R₇ is hydrogen. Preferably, R₂ and R₃ are identical and, independently, R₄ and R₅ are identical. Examples of suitable R₁ groups include alkyl groups having from 1 to 20 carbon atoms such as methyl, ethyl, propyl, butyl, decyl and heptadecyl; cycloalkyl groups such as cyclohexyl; aryl groups such as phenyl and naphthyl; and heterocyclic groups such as pyrrolidinyl and morpholinyl. In one preferred embodiment of the invention R₁ is a substituted or unsubstituted phenyl group or a substituted or unsubstituted alkyl group. Specific examples of organophosphorus compounds suitable for use in the present invention are as follows: The organophosphorus compounds are readily prepared by reacting an appropriate phosphorus acid chloride with an appropriate phenol or alcohol, usually in the presence of a strong base. Many of these starting materials are commercially available. Thus, for example, the reaction for the preparation of compound I-1 may be represented as follows: The organophosphorus compounds are used in an amount sufficient to stabilize the photographic image dyes and their precursors e.g. in an amount from 0.1 to 2.0 moles per mole coupler, more preferably from 0.5 to 1.0 mole per mole coupler. Because the compound is used as a dye stabilizer, it must be incorporated in the silver halide emulsion layer or a layer adjacent thereto. It can be incorporated as a separate dispersion, but is preferably incorporated in admixture with the coupler. Both coupler and stabilizer may be dissolved in a conventional coupler solvent, such as dibutyl phthalate. As in the production of ordinary coupler dispersions, a volatile and/or water-miscible auxiliary solvent, such as ethyl acetate, may be used to aid the dispersion process and then removed by evaporation or by washing the set dispersion. Also, the dispersion process can be assisted by the presence of a surface active compound, as usual in the manufacture of coupler dispersions. In the following discussion of suitable materials for use in the emulsions and elements of this invention, reference will be made to Research Disclosure, December 1978, Item 17643, published by Industrial Opportunities Ltd., The Old Harbourmaster's, 8 North Street, Emsworth, Hants P010 7DD, U.K., the disclosures of which are incorporated herein by reference. This publication will be identified hereafter as "Research Disclosure". References giving information on couplers and on methods for their dispersions are given in Sections VII and XIV, respectively, of Research Disclosure. The couplers commonly employed in photographic materials are water-insoluble compounds often containing ballast groups, phenolic (including naphtholic) couplers being used for producing cyan dyes and compounds containing an activated methylene group, including both heterocyclic and open-chain compounds, being used for producing magenta and yellow dyes. Important magenta couplers are pyrazolones and important yellow couplers are benzoylacetanilides.Patents describing couplers include the following United States Patents: An account of dye-forming development is given in 'Modern Photographic Processing', Vol. 2, Grant Haist, Wiley, New York, 1978, Chapter 9. The stabilizers are useful in any coupler-incorporated silver halide photographic materials, including monochrome materials, false-colour materials and colour transparency, negative and print materials, to stabilize the image dye obtained on development with a solution including a p -phenylenediamine colour developing agent. Such developing agents are well-known, being described in,for example Photographic Processing Chemistry, L.F.A. Mason, Focal Press, London, 2nd edition (1975) pp 229-235 and Modern Photographic Processing, , Grant Haist, Wiley, New York (1979), Volume 2 pp 463-8. The silver halide emulsion employed in the elements of this invention can be either negative-working or positive-working. Suitable emulsions and their preparation are described in Research Disclosure Sections 1 and II and the publications cited therein. Suitable vehicles for the emulsion layers and other layers of elements of this invention are described in Research Disclosure Section IX and the publications cited therein. The photographic elements of this invention or individual layers thereof, can contain brighteners (see Research Disclosure Section V), antifoggants and stabilizers (see Research Disclosure Section VI), antistain agents and image dye stabilizer (see Research Disclosure Section VII, paragraphs I and J),light absorbing and scattering materials (see Research Disclosure Section VIII), hardeners (see Research Disclosure Section XI), plasticizers and lubricants (see Research Disclosure Section XII), antistatic agents (see Research Disclosure Section XIII), matting agents (see Research Disclosure Section XVI) and development modifiers (see Research Disclosure Section XXI). The photographic elements can be coated on a variety of supports as described in Research Disclosure Section XVII and the references described therein. Photographic elements can be exposed to actinic radiation, typically in the visible region of the spectrum, to form a latent image as described in Research Disclosure Section XVIII and then processed to form a visible dye image as described in Research Disclosure Section XIX. Processing to form a visible dye image includes the step of contacting the element with a colour developing agent to reduce developable silver halide and oxidize the colour developing agent. Oxidized colour developing agent in turn reacts with the coupler to yield a dye. With negative working silver halide emulsions this processing step leads to a negative image. To obtain a positive (or reversal) image, this step can be preceded by development with a non-chromogenic developing agent to develop exposed silver halide, but not form dye, and then uniform fogging of the element to render unexposed silver halide developable. Alternatively, a direct positive emulsion can be employed to obtain a positive image. Development is followed by the conventional steps of bleaching, fixing, or bleach-fixing, to remove silver and silver halide, washing and drying. An example of the preparation of a stabilizer compound used in the present invention is as follows: Preparation of 2,4,8,10-Tetra-t-butyl-6-phenyl-12H-dibenzo(d,g)-(1,3,2)-dioxaphosphocin (Compound I-1) 2,2′-Methylenebis(2,4-di-t-butylphenol) (84.93g, 0.2 mole) and triethylamine (50g) were dissolved in dry toluene (500ml). Dichlorophenylphosphine (34.58g, 0.2 mole) was added dropwise at around 5°C. The reaction mixture was stirred overnight at room temperature and extracted with dilute hydrochloric acid. The organic layer was dried over magnesium sulphate, evaporated under vacuum and the residue recrystallized from ethyl acetate. Yield = 81%, m.p. of pure product = 207-209°C. Compounds I-2 to I-17 were prepared in an analogous manner. All the compounds prepared were fully characterized by elemental analysis, nuclear magnetic resonance, thin layer chromatography, high performance liquid chromatography and melting point. The invention is further illustrated in the following Examples. Example 1 Single layer strips were prepared by coating gelatin-subbed polyethylene coated paper supports or polyethyleneterephthalate supports with a photosensitive layer containing a silver bromoiodide emulsion at 0.38g Ag m⁻², gelatin at 1.36 g m⁻² and a dispersion of the yellow image Coupler I in dibutyl phthalate as the coupler solvent (1.5 moles per mole of coupler) and Compound I-1 (0.5 mole per mole of coupler). The coupler coverage was 0.83 millimoles m⁻². The photographic layer was overcoated with a layer containing gelatin at 3.0 g m⁻² and bis-vinylsulphonylmethyl ether hardener at 1.0 weight percent based on total gelatin. Control coatings were prepared in the same way except that Compound I-1 was omitted. Samples were exposed through a graduated density test object and developed using a standard Ektaprint-2 process (see British Journal of Photography Annual 1986, pages 37 and 38). The processed strips were faded using a 5.4 Klux xenon light source, the ultraviolet component of which was removed using a filter consisting of a coating of Tinuvin 328 (Ciba-Geigy) (750 mg m⁻²) in a gelatin dispersion, on a polyester support. Table 1 shows the relevant data. The results show that the presence of the organophosphorus compound considerably improved the stability of the yellow image dye. Examples 2 to 4 The procedure of Example 1 was repeated using different stabilizer compounds. Fading was measured after a period of six weeks for each of the coatings produced. The results are shown in Table 2. The results show that the presence of the organophosphorus compound improved dye stability.

Claims: A photographic material comprising a support bearing at least one developable silver halide emulsion layer and, incorporated in that layer or a water-permeable layer adjacent thereto, a dye-forming coupler, said material also containing, incorporated in the coupler-containing layer or a water-permeable layer adjacent thereto, as a dye stabilizer, an organophosphorus compound having the formula wherein A represents the atoms necessary to complete an optionally substituted heterocyclic ring; R₁ represents substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl, or heterocyclyl; Y is an oxygen or a sulphur atom; and, n is 0 or 1. A material according to claim 1, wherein the organophosphorus compound is represented by the formula wherein R₁, Y and n are as defined; each Z independently represents the atoms necessary to complete an optionally substituted benzene ring; and, X is a single bond or a linking group wherein a single atom separates the benzene rings. A material according to claim 2, wherein the organophosphorus compound has the formula wherein Y, n, R₁ and X are as defined; and, each of R₂, R₃, R₄ and R₅ independently represents hydrogen, substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl or heterocyclyl. A material according to claim 2 or claim 3, wherein X is substituted or unsubstituted methylene; substituted or unsubstituted alkylidene; a heteroatom; or sulphonyl. A material according to claim 2 or claim 3, wherein X is -CR₆R₇- in which each of R₆ and R₇ independently represents hydrogen, substituted or unsubstituted alkyl, substituted or unsubstituted cycloalkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl or heterocyclyl. A material according to claim 5, wherein at least one of R₆ and R₇ is hydrogen. A material according to any one of claims 3 to 6, wherein R₂ and R₃ are identical and, independently, R₄ and R₅ are identical. A material according to any one of the preceding claims, wherein R₁ is a substituted or unsubstituted phenyl group or a substituted or unsubstituted alkyl group. A material according to any one of the preceding claims, wherein the organophosphorus compound is present in an amount from 0.1 to 2.0 moles per mole of coupler. A process of forming a photographic image that comprises developing an exposed silver halide photographic material comprising a dye-forming coupler in the presence of an organophosphorus dye stabilizer as defined in any one of claims 1 to 8.

Inventors: GODDARD JOHN DEMITA, GODDARD, JOHN DEMITA
Applicants: EASTMAN KODAK CO, KODAK LTD, EASTMAN KODAK COMPANY (A NEW JERSEY CORPORATION), KODAK LIMITED
Application year: 1989
Main classification: G03C7
IPC codes: C07F9, G03C7, G03C1