DRY-ETCHING METHOD

Abstract: A dry-etching method which features an increased select ratio of a material to be treated and the underlying material as a result of an improvement in the kinds of reaction gases. The reaction gases consist of a fluoride gas and a gas of a compound that contains hydrogen as a constituent element. It is made possible to greatly increase the etching select ratio of the material to be treated and the underlying material, preventing the underlying material from being etched. The method is adapted to the production by dry-etching of semiconductors having a silicon oxide film under the silicon nitride film.

Description: The present invention relates to a dry etching method and, in particular, to a dry etching method in which the type of reactive gas used is improved and the selectivity between a film being etched and a film below is increased. BACKGROUND OF THE INVENTION (Description of the Prior Art) In the process of manufacturing ICs, the technique is known of superimposing various different films on top of a substrate of a substance such as silicon, then, using a plasma of a gas such as carbon tetrafluoride, perform dry etching to selectively remove parts of those films. Many different dry etching methods have been developed for this purpose, but the isotropy and high levels of selectivity of chemical dry etching methods make them widely used. In each of these chemical dry etching methods, a reactive gas is excited by microwaves in a plasma generation device to create an activated material, then this activated material is sent to a reaction chamber separated from the plasma chamber to react with, and hence etch, a workpiece within the reaction chamber, so the choice of reactive gas used for the etching is an important keypoint of such methods. It is conventional practice to use a mixture of carbon tetrafluoride (CF 4 ), oxygen (O 2 ), and nitrogen (N 2 ) as this reactive gas. However, this conventional technique of using a gas mixture of carbon tetrafluoride, oxygen, and nitrogen as the reactive gas causes a problem when the film to be etched is a silicon nitride film, in that it is difficult to selectively etch the silicon nitride film and not a silicon oxide film thereunder. Reference is made to EP-A-0 106 174, where a silicon nitride film on a silicon oxide film is dry etched using a gas mixture of carbon tetrafluoride, oxygen, nitrogen and hydrogen. Reference is also made to EP-A-0 174 249, where a chromium film is dry etched using a gas mixture of carbon tetrafluoride, oxygen and vaporized ethanol or methanol. The present invention solves the above problem of the prior art, and it provides a dry etching method in which the selectivity between a film being etched and a film below is increased. SUMMARY OF THE INVENTION The above object is achieved by a method as defined in claim 1. As the above fluoride gas, it is preferable to use one of CF 4 , NF 3 , or SF 6 . As the alcohol, one of vaporized ethanol or methanol can be used. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic diagram of a dry etching device to which the dry etching method of the present invention can be applied; Fig. 2 is an enlarged cross-section through a workpiece; Figs. 3 and 4 are graphs of etching selectivity against etching speed and mixing ratios of etching gases containing ethyl alcohol; Fig. 5 is a graph of etching selectivity against etching speed and mixing ratios of etching gases containing hydrogen; and Fig. 6 is a graph of etching selectivity against etching speed and mixing ratios of etching gases containing water. DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the dry etching method of the present invention is described below with reference to the figures. Figure 1 shows an example of a dry etching device to which the dry etching method of the present invention can be applied. In Fig. 1, reference number 1 denotes a vacuum vessel, and a platen 3 to support a workpiece to be etched 2 is provided within an etching chamber of the vacuum vessel 1. In an upper portion of the vacuum vessel 1 is provided a gas distribution tube 4 which opens above the workpiece to be etched 2, and this gas distribution tube 4 is connected to a gas introduction tube 5. A plasma generation device 6 is provided partway along the gas introduction tube 5, the plasma generation device 6 comprising a discharge tube 7 made of quartz with a wave guide 8 positioned at the outer side thereof, and generating a plasma therein by the application of microwaves. An exhaust tube 9 for removing reactive gases is connected via a manifold 10 to the opposite end of the vacuum vessel 1, on a lower wall thereof, and this exhaust tube 9 is connected to a vacuum pump that is not shown in the figure. According to the present invention a mixture of gases comprising a fluoride gas, oxygen and alcohol is used as the reactive gas in the etching device constructed in the above manner. Any of CF 4 , NF 3 , or SF 6 is suitable as the gas containing fluorine. In addition, any of vaporized ethanol or methanol can be used as the alcohol. This gas mixture flows from the gas introduction tube 5, and a reactive gas is excited within the discharge tube 7 made of quartz by microwaves applied from the wave guide 8, to form a plasma. An example of etching the workpiece to be etched 2 using the above dry etching method will now be described with reference to Fig. 2. In the figure, a silicon oxide film 12 on the order of 1000 Ångstrom (1 Angstrom = 10 -10 m) units thick is formed on a silicon substrate 11 by a thermal oxidation method, a silicon nitride film 13 of approximately 2000 Ångstrom units thick is then formed on the silicon oxide film 12 by a CVD method, then a pattern of photoresist 14 is formed on the silicon nitride film 13 by photolithography. A mixture of gases comprising 300 sccm of carbon tetrafluoride (CF 4 ) and 200 sccm of oxygen (O 2 ), to which was added a certain amount of ethyl alcohol, was used as the reactive gas sent into the vacuum vessel 1. This reactive gas etched the workpiece to be etched 2 under conditions of microwave energy of 700 W and a pressure of 50 Pa. The amount of ethyl alcohol added as described above was varied, and the relationships with respect to the additional amount of ethyl alcohol {expressed as the ratio (ethyl alcohol)/(CF 4 + O 2 )} of the selectivity with which the silicon nitride film 13 and the silicon oxide film 12 were etched and the speeds at which the silicon nitride film 13 and the silicon oxide film 12 were etched were as shown in Fig. 3. As is clear from this figure, when the additional amount of ethyl alcohol was on the order of 4%, the etching selectivity was on the order of 30; a dramatically improved etching selectivity over the case in which no ethyl alcohol was added. This is considered to be due to an increase in the etching rate of the silicon nitride film 13 and a decrease in the etching speed of the silicon oxide film 12. Note that, if the additional amount of ethyl alcohol exceeds about 4%, the etching rate of the silicon nitride film 13 decreases and the etching selectivity also decreases, but, so long as the additional amount of ethyl alcohol is selected from with the range of about 2% to 11%, an etching selectivity of 15 or higher can be maintained. As described above, the result of using a gas to which ethyl alcohol has been added as the gas mixture of the present invention enables a huge increase in etching selectivity. Figure 4 is a graph of the etching speeds of polysilicon and silicon oxide film, and the etching selectivity of these substances, when a gas to which ethyl alcohol has been added was used as the reactive gas, showing that, in this case as well, the addition of preferably between 2% and 11% of ethyl alcohol enables an increase in etching selectivity to 90 or higher. The above examples described cases in which a gas with additional ethyl alcohol was used as the gas mixture, but the present invention is not limited to this case; for example, the same effect can be achieved by using a gas of any substance that includes a hydroxyl group, such as methyl alcohol. Next, an example, which is not part of the invention, of using a reactive gas in which a certain quantity of hydrogen (H 2 ) is mixed with carbon tetrafluoride (CF 4 ) and oxygen (O 2 ) will be described with reference to Fig. 5. In this example, the composition ratio of H 2 with respect to 300 sccm of carbon tetrafluoride (CF 4 ) and 200 sccm of oxygen (O 2 ) was varied, and a workpiece to be etched 2 was etched in a vacuum vessel 1 under conditions of microwave energy of 700 W and a pressure of 50 Pa. In this case, measured results of the etching rate of a silicon nitride film 13 and a silicon oxide film 12 with respect to the composition ratio of H 2 {H 2 /(CF 4 + O 2 )} and the selectivity of the silicon nitride film over the silicon oxide film are shown in Fig. 5. As is clear from this figure, when the composition ratio of H 2 is 10%, the etching speed of silicon nitride film is at a maximum; and when the composition ratio of H 2 is 20%, the selectivity of silicon nitride film over silicon oxide film is at a maximum. In addition, an example, which is also not part of the invention, of using vaporized H 2 O in the reactive gas will now be described with reference to Fig. 6. As is clear from this figure, when the composition ratio of H 2 O is 40%, the etching speed of silicon nitride film is at a maximum and, in the same way, the selectivity of silicon nitride film over silicon oxide film is at a maximum. (Applicability of the Present Invention) The dry etching method of the present invention is applicable to the dry etching of a semiconductor device having a silicon oxide film under a silicon nitride film.

Claims: A method of dry etching a workpiece (2) having at the surface a silicon oxide film under a silicon nitride film or under a polysilicon film, comprising the steps of: placing the workpiece on a platen (3) in a vacuum chamber of a vacuum vessel (1), introducing a reactive gas into said vacuum chamber, said reactive gas being a mixture of fluoride gas, oxygen, and alcohol, applying microwaves to said reactive gas to generate a plasma to create activated material; and using said activated material to etch the silicon nitride film or polysilicon film selectively with respect to said silicon oxide film. A method of dry etching as set forth in claim 1, wherein said alcohol is ethylalcohol. A method of dry etching as set forth in claim 1, wherein said alcohol is methylalcohol. A method of dry etching as set forth in one of claims 1 to 3, wherein said fluoride gas is CF 4 . A method of dry etching as set forth in claim 2, wherein ethylalcohol is present in said mixture in an amount of about 2% to 11%.

Inventors: HARA HIROYUKI K, NONAKA MIKIO, HARA, HIROYUKI, NONAKA, MIKIO, HARA, Hiroyuki, Kabushiki Kaisha Tokuda Seisakusho, NONAKA, Mikio, Kabushiki Kaiha Tokuda Seisakusho
Applicants: SHIBAURA ENG WORKS LTD, KABUSHIKI KAISHA SHIBAURA SEISAKUSHO
Application year: 1989
Main classification: H01L21
IPC codes: H01L21