A polycrystal diamond fluted tool and a process for the production of the same

Abstract: A polycrystal diamond fluted tool which is capable of effecting working with much higher accuracy and longer life as compared with the sintered diamond straight flute tool of the prior art, and is particularly suitable for finishing working with high accuracy is provided by forming a polycrystal diamond film (3, 4, 5) on the surface of a substrate subjected to helical grinding by a vapor phase synthesis method, then subjecting the product to a chemical treatment to dissolve and remove only the substrate, brazing the resulting polycrystal diamond film (3, 4, 5) in a fluted form to at least a part of the rake face (2) of a tool base metal (1) subjected to helical grinding in the similar manner to the substrate and then subjecting the brazed tool base metal to working of a flank face to form a cutting edge.

Description: This invention relates to a polycrystal diamond fluted tool according to the preamble of claim 1 and a process for the production of the same according to the preamble of claim 8. The polycrystal diamond tool of the present invention corresponds to such a largely improved rotary tool that sufficient performances cannot be obtained by the sintered diamond tool of the prior art. A diamond compact obtained by sintering diamond powder with a binder metal at an ultra-high pressure and a high temperature at which diamond is stable has the features of diamond with the highest hardness of all tool materials and does not tend to so beak by cleavage at a low stress as in the case of single crystal diamond. Thus, this diamond compact has been used as a cutting tool, wire drawing die, dresser, rock eacavator or the like. On the other hand, end mills, drills and reamers have been developed using sintered dies as tool materials. However, it is very difficult technically to produce a flute-shaped material by sintering at an ultra-high pressure and it is expensive to form a flute by after-working, so at the present time, such tools have been limited to straight fluted base metals or tool base metals subjected to helical grinding, which are brazed with plate-shaped tool materials. These tools have disadvantages that the cutting edge strikes on a workpiece at a stroke, so that the cutting resistance is rapidly changed and the dimensional accuracy is lowered. Furthermore, there arise a problem that chip is not discharged well and the surface roughness of a workpiece is not good, because of being not fluted. In order to solve these problems, there has been developed a fluted rotary tool of cemented carbide, whose cutting part is coated with a thin layer of polycrystal diamond by a vapor phase synthetic method. However, this tool has not been put to practical use yet because of the problem that the adhesiveness between a cemented carbide substrate and coating film is not sufficient and consequently, the coating film tends to be stripped during use. EP-A-0166708 has addressed this problem by bonding the polycrystal diamond layer to the core through an interlayer. This however requires the deposition of multiple layers on the core. We have now developed a polycrystal diamond fluted tool, which overcomes the above drawbacks of the prior art tools and, in particular an improved revolving tool of polycrystal diamond, which is capable of working with a high accuracy and long life. Accordingly, the present invention provides a polycrystal diamond fluted tool comprising a helically fluted tool base metal body and a polycrystal diamond film covering at least a part of a rake face of said fluted tool base metal body, said polycrystal diamond film being formed by a vapour phase method characterised in that said polycrystal diamond film is brazed to said at least a part of said rake face using a brazing agent. The present invention also provides a process for the production of a polycrystal diamond fluted tool, which comprises forming a polycrystal diamond film on a helically ground surface of a substrate by a vapour phase synthesis method, then subjecting the product to a chemical treatment to dissolve and remove only the substrate and brazing the resulting helical polycrystal diamond film to at least a part of a correspondingly ground helical rake face in the flute of a tool base metal. The accompanying drawings are to illustrate the principle and merits of the present invention in more detail. Fig. 1 is a perspective view of a drill as one embodiment of the polycrystal diamond fluted tool according to the present invention; Fig. 2 is a perspective view of an end mill as another embodiment of the polycrystal diamond fluted tool according to the present invention; Fig. 3(a) and (b) are respectively a front view and side view of a straight end mill of two flutes using sintered diamond as a tool material according to the prior art. Fig. 1 is a perspective view of a drill as one embodiment of the polycrystal diamond fluted tool of the present invention, in which a part of a rake face 2 of a tool base metal 1 is brazed with a vapour phase synthesized polycrystal diamond film 3 and 4, 5 and ϑ respectively designate a cutting edge, flank face and helical angle. In the present invention, a polycrystal diamond film in the form of a flute to be a tool material is firstly formed by vapour phase synthesis on the suface of a substrate which has been subjected to helical grinding to give the same flute shape as that of a base tool base metal. The vapour phase synthesis can be carried out by any known method and in particular, methods comprising subjecting raw material gases to cracking and excitation utilizing thermoelectron radiation or plasma discharge and methods comprising forming films using combustion flames are effective. In view of the uniformity of film quality and film thickness, it is preferable to use a hot filament method, above all. As the raw material gas, for example, mixed gases containing, as predominant components, hydrogen and organocarbon compounds, in general, hydrocarbons such as methane, ethane and propane, alcohols such as methanol and ethanol and esters are preferably used. Furthermore, the raw material gas may contain inert gases such as argon, and oxygen, carbon monoxide and water in such a range that the synthesis reactions and properties of carbon are not hindered. As the substrate, metals each having a coefficient of thermal expansion that is not very different from that of diamond, for example, Si, Mo, W etc. are preferably used so as to prevent the synthesized film from separation due to thermal stress. Then using these materials as the substrate, it is possible to recover effectively only the synthesized film by subjecting, after film making, the film-coated substrate to a chemical treatment, for example, by immersing in an acid to dissolve and remove the substrate. In this way, a polycrystal diamond film with a desired flute shape can be obtained. The film thickness is generally 50 to 300 micrometres, preferably 100 micrometres, since the above described tool is ordinarily used until the wearing thereof reaches about 50 micrometres and it is expensive to prepare and use a film with a thickness of more than 300 micrometres. The helical angle is generally in the range of 5 to 50°, since if the helical angle is less than 5°, the performance as a fluted tool cannot sufficiently be achieved while if larger than 50°, in particular, a large diameter tool material becomes long so that synthesis thereof or brazing is difficult, and on the other hand, the tool performance is not improved. The polycrystal diamond film in a fluted shape is then brazed directly onto the rake face of a fluted tool base metal having the same helical angle using an ordinary silver or gold brazing agent, or a braze which further contains a metal capable of forming its carbide at the interface with the diamond film, such as Ti, Ta, Cr, Mn, etc. Such a metal is preferably in a proportion of 0.5 to 10 vol.%, since if it is less than the lower limit, the quantity of the carbide formed is decreased and the bonding strength is not improved, while if it is more than the upper limit, the quantity of the carbide formed is so increased as to render the brazed layer brittle and the unreacted metal is oxidized with the increase of edge temperature during use to form the oxide, resulting in brittleness of the brazed layer. This brazing is preferably carried out by a method comprising using an ordinary silver braze or gold braze further containing Ti or Ta in a non-oxidizing atmosphere, or a method comprising previously coating the surface to be brazed of the polycrystal diamond film first with a Ti film having a thickness of 0.5 to 2 micrometres and further with a Ni film having a thickness of 1 to 10 micrometres by a PVD method and then subjecting the film coated tool to brazing with an ordinary silver braze via these coating films. In the case of the latter method, the brazing can be carried out in the air since the Ni coating serves as an anti-oxidation film for the Ti. According to these brazing methods, the resulting tool does not have any problems of peeling-off or separation of the polycrystal diamond film during use thereof,as in the diamond coating tools of the prior art. As the tool base metal, there are generally used cemented carbide alloys considering the rigidity of the tool, the difference in coefficient of thermal expansion from diamond and the brazing property with tool materials. In particular, it is preferred to use a cemented carbide alloy containing 90 to 95% by weight of fine grain tungsten carbide of at most 1 micrometre in grain size from the standpoint of hardness and coefficient of thermal expansion, and cobalt. Other components can optionally be incorporated as usual. After brazing, the resulting product is subjected to working of a flank face by a diamond wheel to form a cutting edge. Since the thus obtained tool has a polycrystal diamond film with a smaller thickness than that of the prior art sintered diamond (0.5 to 1.0 mm), working of it can be carried out in relatively easy manner with less consumption of an abrasive or diamond wheel and thus the working cost can be reduced. Furthermore, the tool of the present invention is free from a metal binder that the sintered diamond of the prior art contains, thus resulting in very excellent cutting property. The fluted tool of the present invention, prepared by the above described method, exhibits a much improved performance as well as a higher stability and is favourably compared with the prior art tools using sintered diamond or diamond coatings. As illustrated above, according to the method of the present invention, comprising brazing a polycrystal diamond film prepared in a fluted form by vapor phase synthesis to a tool base material having the same flute form, a fluted cutting edge can readily be realized and the adhesiveness of the base material to the diamond film can largely be improved. Therefore, the polycrystal diamond fluted tool of the present invention is capable of effecting working with much higher accuracy and longer life as compared with the sintered diamond straight flute tool of the prior art, and is particularly suitable for finishing working with high accuracy. The following examples are given in order to illustrate the present invention in greater detail without limiting the same. Example 1 A round bar of Mo having a diameter of 10 mm was subjected to helical grinding with a helical angle of 20° and cut in a length of 20 mm. Using the product as a substrate, a polycrystal diamond fluted film was synthesized by means of a microwave plasma CVD apparatus under the following conditions: Raw Material Gas (flow rate): H₂ 200 ml/min, CH₄ 10 ml/min, Ar 100 ml/min Pressure: 150 torr Microwave output: 700 W Synthesis Time: 8 hours When the recovered sample was immersed in hot aqua regia for 30 minutes to dissolve and remove only the Mo substrate, a black and semitransparent polycrystal diamond film with a thickness of 0.1 mm and a fluted shape of 2 mm in width, 20 mm in length and 20° in helical angle was obtained. The resulting polycrystal film showed a density of 3.51 as a result of measurement and a diamond single phase by the identification using Raman spectrum. Two samples of the polycrystal diamond were prepared and subjected to coating of the grown surface with Ti and Ni to give respectively a film thickness of 1 µm and 2 µm. On the other hand, a round bar of 10 mm in diameter, made of a cemented carbide containing 95% by weight of WC having a grain diameter of 1 µm and the balance Co, was subjected to helical grinding with a helical angle of 20° to prepare a fluted shank. The above described coated polycrystal diamond film was silver-brazed using BAg-4 (JIS Standard) in the air to along the rake face of the shank. Then, only the flank face thereof was worked by a diamond wheel to form a cutting edge, thus obtaining a polycrystal diamond fluted end mill as shown in Fig. 2, in which 1 designates a tool base metal and 3 designates a polycrystal diamond film. Evaluation of the thus obtained tool was carried out by subjecting it to working of a VTR chassis of 200 mm-square ADC 12 (commercial name, Al-11% Si die casting) under working conditions of: Revolving Number: 800 rpm Feed: 0.05 mm/edge Cutting Depth: 0.5 mm by Wet Process For comparison, evaluation of the following comparative samples was similarly carried out: Comparative Example 1 A straight end mill of two flutes and 10 mm in diameter using a sintered diamond with a shape as shown in Fig. 3, in which 1 designates a tool base metal and 3 designates sintered diamond. Comparative Example 2 A solid end mill of a cemented carbide having the same composition as used in the tool base metal of Example 1, a diameter of 10 mm and a helical angle of 30°. Comparative Example 3 The solid end mill of the cemented carbide of Comparative Example 2, the surface of which is coated with a diamond thin film of 3 µm thick. In Table 1 are shown results obtained by evaluation of the tool life when the worked surface roughness Rmax became 3 µm or more. It is apparent from these results that the polycrystal diamond fluted end mill of Example 1 according to the present invention shows a less quantity of wearing and a longer tool life due to good discharge of chip than the sintered diamond straight flute end mill or the cemented carbide end mill of the prior art, and does not meet with separation of the polycrystal diamond film as in the diamond coated end mill of the prior art. Example No. Tool Number of Workpieces Worked until Life Example 1 (Present Invention) Polycrystal Diamond Fluted End Mill 120,000 Comparative Example 1 Sintered Diamond Straight Flute End Mill 50,000 Comparative Example 2 Cemented Carbide Solid End Mill 1,000 Comparative Example 3 Diamond Coated End Mill Separation of Coating Film after Working of 30,000 Samples Example 2 A round bar of Si having a diameter of 6 mm was subjected to helical grinding with a helical angle as shown in Table 2 by means of a diamond wheel and then cut in a length of 5 mm. Using the product as a substrate, a polycrystal diamond film was synthesized by a hot filament method comprising using a wire of W of 0.5 mm in diameter and 20 mm in length as a thermoelectron radiation material under synthesis conditions as shown in Table 2. Identification of each of the thus synthesized film showed that it contained no amorphous carbon and consisted of diamond single phase. Separation of the synthesized film from the substrate was carried out by immersing the sample in a mixture of hydrofluoric acid and nitric acid heated at 80°C for 1 hour to dissolve and remove only Si. The recovered synthesized film was washed with alcohol and then brazed to a shank of a cemented carbide alloy fluted in the corresponding flute angle and having the same composition as that of Example 1 by the use of an Au-Ti braze (Ti 5 vol.%) in vacuum, which was then worked to form a margin part and end cutting edge part by means of a diamond wheel, thus obtaining a drill. Each of the resulting drills was subjected to hole-making of an A 390 alloy (commercial name, Al-17% Si alloy, T6 heat treated alloy) to evaluate its performances under cutting conditions of: Revolving Number: 5000 rpm Feed: 0.3 mm/rev Wet Process In Table 3 are shown the above described test results with those of comparative tools of 6 mm in diameter, i.e., a sintered diamond drill using a plate-shaped sintered diamond with an average grain size of 10 µm as a tool material, a cemented carbide drill having the same composition as the tool base metal of Example 2 and a diamond coating drill consisting of this cemented carbide drill the surface of which was coated with a diamond film with a thickness of 10 µm. It will clearly be understood from these results that the tool with a smaller helical angle, i.e., Sample A does not give sufficient performances, but Sample B to D have more excellent performances by at least 10 times than the cemented carbide drill. Example 3 A mixed gas of C₂H₆ and H₂ in a proportion by volume of 1:100 was fed to a reaction tube in which each of substrates as shown in Table 4 was placed at a flow rate of 200 ml/min while adjusting the pressure to 180 Torr. Sample No. Substrate Material Helical Angle (°) E W 25 F Mo 15 G Si 20 Then, the gas in the reaction tube was excited to form a plasma by applying an output of 900 W from a high frequency oscillator (13.56 MHz) to a high frequency coil through a coaxial cable. When this condition was maintained for 10 hours, a polycrystal diamond film with a thickness of 0.2 mm was formed on the surface of each of the substrates. After dissolving out and removing the substrate by an acid treatment, the thus resulting polycrystal diamond film was used as a tool material and brazed with a braze of 93 vol.% Au-7 vol.% Ta to a tool base metal of a cemented carbide containing 90% by weight of WC with a grain diameter of 0.5 µm and 5% by weight of Co and 5% by weight of Ni, having a diameter of 10 mm, which had been subjected to helical grinding with the corresponding helical angle, thus preparing a reamer. Evaluation of the performances of these reamers was carried out by subjecting to finishing hole-making using, as a workpiece, ADC 12 Alloy (commercial name) of 20 mm in thickness, having a hole of 9.5 mm in diameter with a key way, under cutting conditions of a revolving number of 3200 rpm and a feed of 0.2 mm/rev. Evaluation of comparative tools was similarly carried out as to a straight flute reamer of the prior art using sintered diamond as a tool material, a reamer of a cemented carbide having a helical angle of 25° and the same composition as the tool base metal of Example 3 and a reamer consisting of this cemented carbide reamer the surface of which was coated with a polycrystal diamond film with a thickness of 3 µm. The evaluation results are shown in Table 5. It is apparent from these test results that the reamers of the present invention all have a higher wear resistance and are capable of working with higher accuracy because of the fluted shape.

Claims: A polycrystal diamond fluted tool comprising a helically fluted tool base metal body (1) and a polycrystal diamond film (3) covering at least a part of a rake face (2) of said fluted tool base metal body (1), said polycrystal diamond film (3) being formed by a vapour phase method characterised in that said polycrystal diamond film (3) is brazed to said at least a part of said rake face using a brazing agent. A polycrystal diamond fluted tool as claimed in Claim 1 wherein the brazing is carried out directly, or through a Ti layer and Ni layer. A polycrystal diamond fluted tool as claimed in Claim 1 or Claim 2 wherein the polycrystal diamond film (3) has a thickness in the range of from 50 to 300 micrometres. A polycrystal diamond fluted tool as claimed in any one of the preceding claims wherein the rake face (2) of the fluted tool base metal body (1) has a helical angle of 5 to 50°. A polycrystal diamond fluted tool as claimed in any one of the preceding claims wherein the tool base metal is of a cemented carbide alloy. A polycrystal diamond fluted tool as claimed in any one of the preceding claims wherein the brazing is carried out using a silver braze containing Ti or Ta. A polycrystal diamond fluted tool as claimed in Claim 5 wherein the cemented carbide alloy contains 90 to 95% by weight of fine grain tungsten carbide powder with a grain diameter of not more than 1 micrometre. A process for the production of a polycrystal diamond fluted tool, which comprises forming a polycrystal diamond film (3) on a helically ground surface of a substrate by a vapour phase synthesis method, then subjecting the product to a chemical treatment to dissolve and remove only the substrate and brazing the resulting helical polycrystal diamond film (3) to at least a part of a correspondingly ground helical rake face (2) in the flute of a tool base metal (1). A process as claimed in Claim 8 wherein the brazing is carried out directly or through a Ti layer and Ni layer. A process as claimed in Claim 8 or Claim 9 wherein the polycrystal diamond film (3) has a thickness of 50 to 300 micrometres. A process as claimed in any one of Claims 8 to 10 wherein the tool base metal (1) is in a fluted form with a helical angle of 5 to 50°. A process as claimed in any one of Claims 8 to 11 wherein the tool base metal (1) is of a cemented carbide alloy. A process as claimed in Claim 12 wherein the cemented carbide alloy contains 90 to 95% by weight of fine grain tungsten carbide alloy powder with a grain diameter of not more than 1 micrometre. A process as claimed in any one of Claims 8 to 13 wherein the brazing is carried out using a silver braze containing Ti or Ta. A process as claimed in any one of Claims 8 to 14 wherein the vapour phase synthesis method is carried out by the use of thermoelectron radiation, plasma discharge or combustion flame. A process as claimed in any one of the Claims 8 to 15 wherein the vapour phase synthesis method is carried out by the use of a raw material gas selected from mixed gases containing, as predominant components, hydrogen and organocarbon compounds. A process as claimed in any one of Claims 8 to 16 wherein the substrate consists of at least one of Si, Mo and W. A process as claimed in any one of Claims 8 to 17 wherein the chemical treatment is carried out with a strong acid.

Inventors: NAKAI TETSUO C O ITAMI WORKS O, NAKAMURA TSUTOMU C O ITAMI WOR, NAKAI, TETSUO C/O ITAMI WORKS OF, NAKAMURA, TSUTOMU C/O ITAMI WORKS OF
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1989
Main classification: B23B27
IPC codes: B23B51, B23D77, B23C5, B23P5, B23P15