Potassium niobate crystals and method for their preparation

Abstract: A KNbO₃ single domain, crack-free and striaton free crystal, having an iron content of 15 ppm or less than 15 ppm, and a method for its preparation from a molten flux. Growth and aftertreatment of such crystals for use in a laser system.

Description: According to the invention, there is provided a KNbO₃ single domain, crack-free and striation-free crystal, having an iron content of 15 ppm or of less than 15 ppm. Preferably the amount of iron present is 2 to 15 ppm. Up until now it has not been possible to produce a KNbO₃ crystal having the amount of iron impurities as low as 15 ppm. Crystals that are available to date appear to have an iron content of about 50 ppm. The crystals according to the invention have an absorption loss (of light of wavelength 1.06µm) of less than 1% when passing through 1 cm of crystal. The refractive index of such a crystal is substantially the same, i.e. uniform over the length of the crystal, the variation in refractive index being less than 10⁻⁵ per cm length of crystal. Crystals according to the invention can produce a half width of temperature phase matching curves, of light of wavelength 840nm, of about 0.3°C in a 1 cm long crystal. This is important as it allows good reinforcement of second harmonics that can be generated in the crystal. In a crystal according to the invention, the variation in conversion efficiency to form a second harmonic from a fundamental is practically negligible, e.g. is ± 5% over 1 cm length of crystal for a wave width of about 200µm. This is important because it allows good second harmonic reinforcement and enables the second and fundamental waves to be kept in phase. One very surprising advantage of a crystal according to the invention is that the peak damage threshold of uncoated KNbO₃ crystals has been significantly increased to a value, for example of greater than 1.2 KW/cm² of the surface of the crystal at a wavelength of 1.06µm. A crystal according to the invention preferably has a hardness of about 5 Mohs, lattice parameters of a= 5.6896 x 10⁻¹⁰m, b=3.9692 x 10⁻¹⁰m and c=5.7256 x 10⁻¹⁰m and a density of about 4.62 g/cm³. A crystal according to the invention preferably has a melting point of from 1050-1060°C. It preferably also has structural phase transitions of -50°C, +225°C and +430°C. In producing a good crystal according to the invention, it is important to polish it carefully. Polishing should be carried out to produce a good surface homogenity that hardly differs across the surface, e.g. of less than λ/10 where λ is the wavelength in metres and so that two opposite surfaces are substantially parallel, for example that the difference in parallelity is less than 1/180 of a degree. Further according to the invention, there is provided a process for preparing a KNbO₃ crystal comprising a) i) mixing 50 percent of anhydrous K₂CO₃ with 50 mol percent of Nb₂O₅ in powder form and homogenising the mixture; ii) sintering at 750-850°C; iii) crushing the sintered material into powdered form and homogenising; iv) sintering in the presence of excess water-free K₂CO₃ (anhydrous); so that the final percentages of K₂CO₃ is 50.5 to 54 mol% and the final molar percentages of Nb₂O₅ is 49.5 to 46% mol%; v) crushing the sintered material in powdered form; and vi) pouring the mixture into a container of an inert material (preferably a platinium crucible) and heating the mixture to melting or just over its melting point to form a molten flux seeding solution; b) seeding the solution; and c) polishing the resultant seeded crystal. Preferably the temperature of the flux is 1050 to 1060°C. Step b) is preferably a top seeded solution growth variation of the Czochralski method. More preferably step b) comprises i) inserting, whilst rotating, a KNbO₃ seed which is commercially available having orientation (110) or (100), (rotating preferably at a constant value in the range of 15-30 revs/min) into the upper regions of the molten flux seeding solution; whereby the temperature of the flux is regulated so that the weight of the seed does not increase by more than 0.1g over the first 6 to 12 hours (preferably 6 hours); ii) changing the temperature of the flux (preferably decreasing the temperature) to cause the crystal to be drawn at rate of crystal growth of not more than 0.5 mm per hour; (preferably the temperature is decreased at not more than 0.3°C per hour until the flux temperature is reduced by 5 or 6°C); iii) once the crystal has reached the weight required, withdrawing the crystal from direct contact with the melt and cooling at a constant temperature gradient (e.g. 30°C per hour) (from the top to the bottom of the crystal) to room temperature. Step c) is then preferably carried out by i) grinding all surfaces of the crystal; ii) placing the crystal for 1 hour in 30% liquid hydrofluoric acid at 80°C; iii) washing the crystal in cold water; iv) where necessary, realigning by means of a Laue (X-ray) diagram any spontaneous polarisation on the b-surfaces caused through grinding; v) grinding the surfaces again and realigning any spontaneous polarisation; vi) then cutting the crystal (preferably with a diamond saw) to its required size; vii) grinding the a- and c- surfaces again; viii) surface grinding of the a- and b- surfaces to maximum transparency; ix) submerging the crystal in an inert liquid or gas (preferably silicon oil or in pure oxygen or in air) heating to 120-200°C and then applying a 0.5 to 5 KV/cm field to the c-axis surfaces to remove any domains that come about due to polishing; very finely polishing all surfaces. One result of the development of the crystals according to the invention is that it has enabled a laser system to be developed that can convert green light into blue light. Further according to the invention, there is provided a laser system, containing a single domain, crack-free and striation-free KNbO₃ crystal (preferably having an iron content of less than 15 ppm), which system converts green light (preferably wavelength of 500-540 nm) into blue light (of wavelength between 430 and 490 nm). Preferably such a laser system comprises i) a Ti:Al₂O₃ crystal-containing, pumped laser system for converting green light to infra-red light (of a wavelength in the range 860-940 nm) ii) means for introducing green light into the Ti:Al₂O₃ (laser) crystal; iii) downstream of the Ti:Al₂O₃ crystal, a single domain, crack-free and striation free KNbO₃ crystal (preferably according to the invention) located in an oven for heating the KNbO₃ crystal for phase matching of the second harmonic with its fundamental; and iv) means for introducing only infra-red light of a specified wavelength from the Ti:Al₂O₃ crystal into the KNbO₃ crystal where the infra-red light is converted to blue light by frequency doubling. Preferably such a laser system is in a single cavity or container. Preferably green light is introduced into the Ti:Al₂O₃ crystal from a Q switched Nd:YAG laser (emitting light of wavelength 532 nm for example the laser B.M. Industries Model 501-D.NS); from an Argon-laser, emitting light of wavelength 514.5 nm), both lasers operating at 30 Hz, the pulses having energies of up to 18 mJ and a typical pulse width of 20 ns or from an adjustable laser diode. The collimated beam that results often has too wide a band width (e.g. 10 mm) and this can be reduced (e.g. to 1 mm) by a suitable system of lenses. The Ti:Al₂O₃ laser is then pumped with the second harmonic from the green light and passes through the Ti:Al₂O₃ crystal, where preferably the light passes to a prism. In order to tune out any undesired wavelengths, preferably an optical resonator is set up. This functions by creating a pathway for I.R. light generated in the Ti:Al₂O₃ crystal to a prism, where the various different wavelengths of I.R. light produced by the Ti:Al₂O₃ crystal are diffused. By judicious adjustment of a concave mirror downstream of the prism in the resonator, only I.R. light of the desired wavelength is passed down the pathway to the KNbO₃ crystal. In order to avoid damage of the prism, it is useful to use a paraxial pumping system where the intersection of the angle of pumping with the resonator axis is about 15° inside the Ti:Al₂O₃ crystal. This beam of I.R. light of specified wavelength is then passed into the KNbO₃ crystal, which by appropriate heating allows the second harmonic generated blue light to be brought into phase with the fundemental. The definition of the a-, b- and c- axes can be found in Ferroelectrics 6, p 263-281 in an article by E. Wiesendanger. The invention will now be illustrated by the following Examples. Example 1 19.19g of pure, water-free finely divided powdered K₂CO₃ (PA, Fluka) and 36.92g of pure, water-free, finely divided powdered Nb₂O₅ are mixed in a suitable container for 16 hours with a rotor rotating at 30 rpm. The mixture is then poured into a platinum crucible which is then placed in a sintering oven. The mixture is then heated to 820°C and left in the oven for 6 hours at this temperature, after which it is taken out of the oven and cooled to room temperature. The net weight (including crucible of 144.35g) is 195.85g. The slightly clumpy powder mixture is stirred with a spatula and the clumps of material are crushed into a fine powder. The crucible (with mixture) is sintered a further six hours at 820°C. After cooling, the mixture is crushed again and mixed with 0.019g of pure, water-free, fine powder K₂CO₃. The seed for crystallisation is a KNbO₃ rod-shaped crystal with an orientation (110) or (100) and is 3.5 x 3.5 x 15 mm. It is carefully attached with a fine platinium wire to a crystal support and is positioned on a balance arm over the flux melt and the seed is brought into a position from which it can be lowered into the upper regions of the flux melt. The platinium crucible is treated in an oven (as described in the article by Wu Xing et al "Progress in KNbO₃ Crystal Growth in Journal of Crystal Growth" 78 (1986) p. 431-437). The mass is raised over 18 hours to 1 to 3°C above the melting point of the KNbO₃ crystal (1050 to 1060°C) and the crystal seed (whilst continuous rotating at 30 rpm until the termination of crystal growth) is then lowered into the upper regions of the melt flux (controlled visually with assistance from the balance arm). The crucible is rotated intermittently in the same direction as the crystal seed but at varying speeds. First, it is rotating slowly and this is then increased to about 20 rpm, then for about 20 seconds the crucible rotation and the speed of the seed are the same (30 rpm) and then the crucible slowly brought to a standstill. When that is reached, the sequence of variating rotation starts again after 20 seconds. After the seed portion in contact with the melt flux has become molten, the temperature of the melt is reduced so that over the first 6-12 hours, the weight of the seed increases by around 0.1g. However, if the seed becomes too heavy in this time period, the temperature must be slightly raised to cause a part of the seed to become molten again and if the seed is too light then the temperature is slightly decreased. After this first 6-12 hours are passed, the temperature of the melt is slowly reduced at a rate of 0.03°C per hour over the next 6-12 hours. Crystal formation then starts. The rate of growing the seed is about 0.5 mm per hour. Before the crystal grows onto the crucible side, the rate of temperature decrease is slowed down. Once the crystal has reached the required dimensions, it is separated by being withdrawn a few mm above the surface of the flux Cooling then begins. Down to a temperature of about 480°C, the crystal is cooled starting at a rate of about 30°C per hour and progressing more slowly later so that room temperature is reached after 3 days. Cooling of the crystal is on a temperature gradient so that the upper region of the crystal is always a little cooler than the lower regions of the crystal. Once the crystal reaches room temperature, the crystal is removed from the crystal support by removal of the platinium wire. The resultant rough crystal is then ground on all natural surfaces (including additional facets of the crystal), immersed for 1 hour in a Teflon container in 30% hydrofluoric acid at 80°C, washed with cold water and dried. With the aid of an etch pattern seen under a microscope, the b-surfaces and spontaneous polarisation can be determined. By means of a Laue (X-ray) diagram, the b-surfaces can be orientated, ground and the facing b-surfaces are then finely surface ground. The crystal is then separated from the seed by using a diamond saw along c-axis and is cut into the derived crystal sizes. From each piece of crystal, a- and c- surfaces are oriented (using a Laue diagram or a Bragg Reflexion). The surfaces are then ground and the opposite faces finely surface ground. All a- and b- surfaces are then polished to transparency and the c-surfaces are ground fine. Each piece of crystal is then immersed in silicon oil (or in oxygen or air, heated to 120-200°C and a 0.5 to 5 KV/cm field is exerted across the c-axis surfaces, to remove any domains that might be present. The c-axis surfaces are then polished to the desired fineness. Example 2 The KNbO₃ crystal, cut to a size a x b x c = 7.9 x 7.6 x 8.8 mm , can be used in a frequency doubling and tunable blue laser as shown in Fig. 1 below. Green light of 532 nm is introduced from a Q-switched Nd: YAG laser (BM Industries Model 501-D.N.S) operating at 30 HZ to a Ti:Al₂O₃ laser through 2 lenses L₁(f=300m) and L₂(f=-30mm) so that the collimated pump beam is reduced from 10 mm to 1mm. The green light is converted to I.R. light in the Ti:Al₂O₃ laser. A mirror M₄ is used to pump back residual pump light (green light) into the Ti:Al₂O₃ crystal to increase efficiency in I.R. light conversion. The I.R. light is pumped to a prism P in an optical resonator system. In order to avoid laser damage of the prism, a paraxial pumping scheme is used. The intersection angle of the pump beam with the resonation axis is about 15° inside the laser crystal. The optical resonator is stable two fold cavity of 0.3 m length with two flat mirrors M₁ and M₂ and a concave mirror M₃ of 0.5 m radius of curvature. All mirrors are highly reflective (R>98%) from 700nm to 1000nm (-that is to say they reflect I.R. light) while M₂ has a high transmission for both 532nm (Green light) and the second harmonic wave (T>85%). Prism P, operated at the Brewster angle enables dispersion of the I.R. light so that by judicious tuning of mirror M₃ only the fundamental wave of I.R. light of a specific wavelength is reflected through the optical resonator. The Ti:Al₂O₃ laser crystal (10mm) is grown by the Czochralski method and has a nominal doping of 1%. The crystallographic b-axis is parallel to the resonator axis and the c-axis is horizontal like the polarisation of the pump beam. A.R. coatings for both 532nm and the laser operating range are deposited on the polished (010)- and (010)-faces. I.R. light from the optical resonator is reflected off mirror M₂ into the KNbO₃ crystal (a x b x c = 7.9 x 7.6 x 8.8 mm) . The polished faces have a single layer AR-coating for 860nm. The KNbO₃ crystal is mounted in an oven with the a-axis parallel to the resonator axis. The c-axis is vertical to allow to type I phase matched second harmonic generation by the non-linear coefficient d₃₂. Using temperature tuning, two tunable blue beams are generated in opposite directions along the KNbO₃ crystal and by having M₁ reflecting the blue light an enhanced blue light signal is emitted through mirror M₂ which transmits blue light (430-470nm)(designated as OUTPUT). The temporal pulse shape and pulse to pulse stability is measured using a fast photodiode (MRD-500 tyre) and a Tektronix 7904 oscilloscope. The time resolution is less than 1 nanosecond. The infrared and SH pulse lengths are typically 35 nanoseconds and 30 nanoseconds. No significant pulse compression is observed in the second harmonic generation process. By heating the KNbO₃ crystal from room temperature to 180°C, phase matching is obtained for fundamental waves of 860nm to 940nm. By tuning the Ti:Al₂O₃ laser and prism to appropriate fundamental wavelength and heating the KNbO₃ crystal to the phase matching temperature, any wavelength in the range 430nm to 470nm can be generated. The infrared to blue conversion efficiency (total blue output power/intracavity travelling power) is measured using a power meter (United Detector Technology Inc. 80 x Opto-meter). From the maximum power of the fundamental of 14 Kw, a total blue output power of 7.8 Kw is obtained, giving an efficiency of 45%. As can be seen, an efficient intracavity frequency doubling of a pulsed Ti:Al₂O₃ laser using KNbO₃ as the non linear crystal has been shown.

Claims: A KNbO₃ single domain, crack-free and striation free crystal, having an iron content of 15 ppm or less than 15 ppm. A crystal according to Claim 1 in which the amount of iron present is from 2 to 15 ppm. A crystal according to any one of the preceding claims having lattice parameters of a= 5.6896 x 10⁻¹⁰m; b=3.9692 x 10⁻¹⁰m and c=5.7256 x 10⁻¹⁰m. A crystal according to any one of the preceding claims in which the density is about 4.62 g/cm³. A process for preparing a crystal according to any one of the preceding claims comprising a) i) mixing 50mol percent of anhydrous K₂CO₃ with 50 mol percent of Nb₂O₅ in powder form and homogenising the mixture; ii) sintering at 750-850°C; iii) crushing the sintered material into powdered form and homogenising; iv) sintering in the presence of excess water-free K₂CO₃ (anhydrous); so that the final percentages of K₂CO₃ is 50.5 to 54 mol% and the final molar percentages of Nb₂O₅ is 49.5 to 46% mol%; v) crushing the sintered material in powdered form; and vi) pouring the mixture into a container of an inert material and heating the mixture to melting or just over its melting point to form a molten flux seeding solution. b) seeding the solution; and c) polishing the resultant seeded crystal. A process according to Claim 5 in which step b) comprises i) inserting, whilst rotating, a KNbO₃ seed which is commercially available having orientation (110) or (100) into the upper regions of the molten flux seeding solution; whereby the temperature of the flux is regulated so that the weight of the seed does not increase by more than 0.1g over the first 6 to 12 hours; ii) changing the temperature of the flux to cause the crystal to be drawn at rate of crystal growth of not more than 0.5 mm per hour; iii) once the crystal has reached the weight required, withdrawing the crystal from direct contact with the melt and cooling at a constant temperature gradient to room temperature. A process according to claim 5 or claim 6 in which step c) comprises i) grinding all surfaces of the crystal; ii) placing the crystal for 1 hour in 30% liquid hydrofluoric acid at 80°C; iii) washing the crystal in cold water; iv) where necessary, realigning by means of a Laue (X-ray) diagram any spontaneous polarisation on the b-surfaces caused through grinding; v) grinding the surfaces again and realigning any spontaneous polarisation; vi) then cutting the crystal to its required size; vii) grinding the a- and c- surfaces again; viii) surface grinding of the a- and b- surfaces to maximum transparency; ix) submerging the crystal in an inert liquid or gas, heating to 120-200°C and then applying a 0.5 to 5 KV/cm field to the c-axis surfaces to remove any domains that come about due to polishing and very finely polishing all surfaces. A laser system containing a single domain, substantially crack free and striation free KNbO₃ crystal according to any one of claims 1 to 4 which system converts green light of wavelength 500-540 nm into blue light of wavelength 430 to 490 nm. A laser system according to Claim 8 comprising i) a Ti:Al₂O₃ crystal-containing, pumped laser system for converting green light to infra-red light (of a wavelength in the range 860-940 nm) ii) means for introducing green light into the Ti:Al₂O₃ (laser) crystal; iii) downstream of the Ti:Al₂O₃ crystal, a single domain, crack-free and striation free KNbO₃ crystal located in an oven for heating the KNbO₃ crystal for phase matching of the second harmonic with its fundamental; and iv) means for introducing only infra-red light of a specified wavelength from the Ti:Al₂O₃ crystal into the KNbO₃ crystal where the infra-red light is converted to blue light by frequency doubling. A laser system according to Claim 8 or Claim 9 in which the laser system is in a single cavity or container.

Inventors: GUENTER PETER, GUENTER, PETER, Günter, Peter
Applicants: SANDOZ AG, SANDOZ-ERFINDUNGEN VERWALTUNGSGESELLSCHAFT M.B.H., SANDOZ-PATENT-GMBH
Application year: 1989
Main classification: C30B29
IPC codes: C30B29, C30B9, C30B15