Ductile, blow moldable composition containing a styrene-maleimide copolymer bearing pendant carboxyl or hydroxyl groups

Abstract: Moldable blends of rubber modified styrene/maleic anhydride copolymer, core-shell graft coplymer modified polybutylene terephthalate ester, and styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups are provided. The compositions of this invention exhibit co-continuous resin phases and facilitate the production of blow molded articles which exhibit ductility.

Description: This application is related to EP-A-0 364 240 filed of even date, entitled "Ductile, Blow Moldable Composition Containing a Styrene-Methylmethacrylate Copolymer Having Pendant Carboxy Ester Groups". This invention relates to improved molding compositions. In one of its more specific aspects, this invention relates to molding compositions containing a rubber modified styrene-maleic anhydride copolymer, a core-shell graft copolymer rubber modified polybutylene terephthalate ester, and a minor amount of a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups. Molding compositions of this invention exhibit co-continuous phases, ductility upon molding, and can be blow molded. Polymer blends of styrene-maleic anhydride copolymers (S/MA) and polybutylene terephthalate esters (PBT) are known from U.S. Pat. No. 3,644,574. Also known is a polymer mixture of PBT and a rubber modified styrene-maleic anhydride copolymer for use as an adhesive for laminates. This polymer mixture is described in EPA Publication No. 0 257 693. Molding compounds and films made from the polymer mixture are further described in EPA Publication Nos. 0 257 691 and 0 257 692, respectively. U.S. Pat. No. 4,080,354 describes compositions of PBT with a second resinous component containing 1 to 40% vinyl aromatic units with the balance being non-aromatic units. U.S. Pat. No. 4,217,427 describes PBT having incorporated thereinto pendant side chains of polystyrene to enhance its melt flow characteristics. U.S. Pat. No. 4,659,765 describes elastomeric compositions containing a polybutylene terephthalate ester and a modifier resin. The modifier resin preferred is a core-shell graft copolymer. Notwithstanding the general knowledge that blends of S/MA and PBT are useful compositions, it is well known that their combination, using melt mixing in an extruder, results in molded products which are brittle and tend to delaminate due to the gross immiscibility of the polymers. This tendency toward delamination has led the molding industry to continue to seek ways to combine these polymers attempting to obtain a composition which exhibits the high heat distortion temperature of the S/MA, the excellent solvent resistance of the PBT, and resistance to delamination. A composition having the above-mentioned combination of properties and ductility in molded form is also desired by the molding industry. Co-pending EP-A-0 357 459 discloses compositions of S/MA and PBT in which the S/MA and PBT phases are co-continuous. The co-continuous phases are achieved by incorporating a minor amount of a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups into a blend of S/MA and PBT. The molded products prepared from these compositions exhibit excellent deflection temperature under load, flexural modulus, unnotched impact strength, solvent resistance, and resistance to delamination, but they are brittle. EP-A-0 357 459 is incorporated herein in its entirety by reference. The present invention is an improvement to the compositions of said European patent application and provides molded products which possess ductility. For reasons not clearly understood, it has been found that the attainment of molded articles which are ductile requires that both of the major components of the composition, that is, the S/MA and the PBT must be impact modified. The impact modification of only one of the S/MA or PBT components does not provide a composition which exhibits ductility in molded form. Moreover, ductility is not achieved in the absence of the styrene-maleimide copolymer bearing pendant groups even if both major resin components are impact modified. According to this invention, there is provided a moldable composition which exhibits ductility upon molding comprising: (a) a rubber modified styrene-maleic anhydride copolymer; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl and hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 35:65 to about 65:35, and the amount of copolymer (c) in parts by weight is from about 1 to about 20 per each 100 total parts by weight of (a) + (b) + (c). Also according to this invention, there is provided a method of producing a moldable composition which comprises blending together the components (a), (b) and (c) identified above in the amounts specified above. Molded products prepared from the above-described moldable compositions are also provided by this invention. In accordance with one aspect of the invention, there is provided a ductile, molded composition comprising a first continuous phase, a second continuous phase, and an interface, wherein the first continuous phase comprises a rubber modified styrene-maleic anhydride copolymer, the second continuous phase comprises core-shell graft copolymer rubber modified polybutylene terephthalate, and the interface comprises a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups. The weight ratio of styrene-maleic anhydride copolymer to polybutylene terephthalate in the molded product is preferably from about 65:35 to about 35:65 and the amount of styrene-maleimide copolymer present is preferably from about 1 to 20 parts per 100 of the composition, by weight. A particularly unique feature of the moldable compositions of this invention is that they can be blow molded into articles which are ductile rather than brittle. In a preferred embodiment of the invention, the weight ratio of rubber modified S/MA copolymer to rubber modified PBT is within the range of from about 60:40 to about 40:60, and the composition exhibits co-continuous S/MA and PBT phases. The term "co-continuous" means that upon blending both the S/MA and the PBT are present as continuous phases, that is, neither polymer is identifiable as a dispersed phase in a continuous phase of the other polymer. The term is intended to include the transition area between separate dispersed phases and two continuous phases, which transition area is observed with the more narrow weight ratio of S/MA to PBT of from about 65:35 to about 60:40 and from about 35:65 to about 40:60. Any suitable rubber modified styrene-maleic anhydride copolymer can be used. Preferably, the rubber modified S/MA copolymer will contain in weight percent from about 1 to about 25 maleic anhydride from about 56 to about 94 styrene and from about 3 to about 30 rubber, which is incorporated during the polymerization of the styrene and maleic anhydride monomers. The rubber of the S/MA copolymer remains finely dispersed in the S/MA phase of the composition. The number average molecular weight of the S/MA copolymer will be within the range of from about 50,000 to about 300,000. Suitable S/MA copolymers are available from ARCO Chemical Company under the trademarks DYLARK 350, DYLARK 250, and DYLARK 700. DYLARK® 350 resin is rubber modified styrene-maleic anhydride copolymer containing in weight percent about 66 styrene, about 14 maleic anhydride, and about 20 rubber. DYLARK® 250 resin is a rubber modified styrene-maleic anhydride copolymer containing in weight percent about 77 styrene, about 8 maleic anhydride, and about 15 rubber. DYLARK® 700 resin is a rubber modified styrene-maleic anhydride copolymer containing in weight percent about 61 styrne, about 14 maleic anhydride, and about 25 rubber. The molding compositions of this invention will contain rubber modified S/MA copolymer in an amount within the range of from about 65 to about 35 weight percent, preferably from about 60 to about 40 weight percent, based on the total weight of the S/MA and PBT. Within these weight percent ranges, and in the presence of a minor amount of a styrene-maleimide copolymer bearing pendant carboxyl or hydroxyl groups, the compositions exhibit co-continuous phases. Any suitable PBT resin can be used. They are typically prepared by the condensation reaction of 1,4-butanediol and terephthalic acid. The PBT is typically impact modified by precompounding the PBT with the selected core-shell graft copolymer using any suitable method of combination which will typically include the use of conventionally employed additives such as antioxidants and the like. The weight ratio of core-shell copolymer to PBT will be from about 5:95 to about 35:65, preferably 7.5:92.5 to about 40:60. The core-shell graft copolymer rubber remains substantially finely dispersed in the PBT phase of the composition. Specific examples of suitable core-shell graft copolymers and the production thereof are disclosed in U.S. Pat. Nos. 4,180,494; 4,034,013; 4,096,202; 3,808,180; and 4,292,233, all teachings of which are incorporated herein by reference. Core-shell graft copolymers suitable for use in the practice of this invention are commercially available from Rohm & Haas Chemical Company and include KM-653 and KM-611 butadiene-based core-shell copolymers and KM-330 acrylate-based core-shell copolymer. KM-653 core-shell copolymer is preferred. The compositions of this invention will contain the modified PBT in an amount within the range of from about 35 to about 65 weight percent, preferably from about 40 to about 60 weight percent, based on the total weight of the rubber modified S/MA and the modified PBT. The styrene-maleimide copolymer containing pendant carboxyl or hydroxyl groups is not known to be commercially available. Examples 1-5 of EP-A-0 357 459 describe the preparation of styrene-maleimide copolymers which are suitable for use in this invention. Examples 1 and 2 of said EP-A-0 357 459 are repeated as Examples 1 and 2 herein. Generally, the procedure for producing the styrene-maleimide copolymer with pendant groups involves the modification of a styrene-maleic anhydride copolymer (for example, DYLARK® resin) with an amino acid or ester (e.g., p-aminobenzoic acid, ethyl p-aminobenzoate, methyl p-aminobenzoate, dimethyl aminoisophthalate, dimethyl aminoterephthalate, p-aminophenol, or glycine) by refluxing with azeotropic removal of water in a solvent. The styrene-maleimide copolymer containing pendant carboxyl or hydroxyl groups will be employed in an amount of from about 1 to about 20 parts by weight, preferably from about 8 to about 12 parts by weight, for each 100 parts by weight of total rubber modified S/MA, modified PBT, and styrene-maleimide copolymer. The styrene-maleimide copolymer functions as an interfacial modifier between the S/MA and PBT phases. The following examples will serve to further demonstrate the invention. EXAMPLE 1 This example is Example 1 of EP-A-0 357 459 and demonstrates the preparation of a styrene-maleimide copolymer having pendant carboxyl groups suitable for use in the practice of this invention. About 600 g. of a styrene-maleic anhydride copolymer containing about 14% by weight maleic anhydride and about 86% by weight styrene (DYLARK® 332 resin) and about 62 g of glycine were mixed and then refluxed in about 1400 g of a 70:30 (by weight) solvent mixture of xylene and dimethylformamide. After azeotropic removal of about 15 ml. of water, the solution was poured into a pan, and the solvent mixture was evaporated in a vacuum oven at 60°C. The resultant polymer--a styrene-maleimide copolymer with pendant carboxyl groups--was finely ground and placed in a vacuum oven to remove residual solvent. The total product recovered weight 590 g. (91.5% yield) and had a Tg of 152°C. EXAMPLE 2 This example is Example 2 of said EP-A-0 357 459 and demonstrates the preparation of a styrene-maleimide copolymer having pendant hydroxyl groups suitable for use in the practice of this invention. About 500 g. of a styrene-maleic anhydride copolymer containing 14% weight maleic anhydride and 76% weight styrene (DYLARK® 332 resin) and about 47.8 g of hydroxylamine - HCl were mixed and then refluxed in about 1400 g of a 70:30 (by weight) solvent mixture of xylene and dimethylformamide. After azeotropic removal of about 12 ml. of water, the solution was poured into a pan, and the solvent mixture was evaporated in a vacuum oven at 60°C. The resultant polymer--a styrene-maleimide copolymer with pendant hydroxyl groups--was finely ground and placed in a vacuum oven to remove residual solvent. The total product recovered weight 514 g. (96.0% yield) and had a Tg of 114°C. EXAMPLE 3 This example demonstrates the preparation of a core-shell graft copolymer modified PBT suitable for use in the practice of this invention. About 300 parts of a KM-653 acrylic core-shell rubber (Rohm & Haas Company) and about 700 parts of PBT were pre-compounded on a 25.4mm (1 in.) Sterling extruder (36:1 L/D) at 260°C (500°F.) profile. After extrusion, the compound was pelletized and dried at about 93°C (200°F) EXAMPLE 4 This example demonstrates the preparation of a ductile molded composition of this invention. A mixture of 40 parts by weight of rubber modified styrene-maleic anhydride copolymer (DYLARK® 350 resin, ARCO Chemical Company), 50 parts by weight of the core-shell copolymer modified PBT prepared in Example 3, and 10 parts by weight of the styrene-maleimide copolymer bearing pendant carboxyl groups prepared according to the procedure of Example 1 were extruded at 249°C (480°F.) profile and pelletized. The pellets were molded into ASTM test samples on a Battenfeld injection molding machine at 241°C (465°F.) profile and 60°C (140°F) mold temperature. The physical properties of the resulting molded composition of the invention is compared to three control samples in following Table I. PHYSICAL PROPERTIES OF A MOLDED COMPOSITION OF THE INVENTION (EXAMPLE 4) Example No. Control Control Control 4 Materials (Parts by Weight) Rubber Modified S/MA (DYLARK 350) 100 0 45 40 Rubber Modified PBT of Ex. 3 0 100 55 50 S/MI Copolymer of Ex. 1 0 0 0 10 Physical Property Flex. Modulus MPa (x10³, psi) 2523(366) 1517(220) 1800(261) 1731(251) Tensile Strength MPa (psi) 32.4(4700) 30.3(4400) 39.3(5700) 37.9(5500) Tensile Elongation (%) 15 100 21 48 Notched Izod J/m (ft-lbs/in) 144(2.7) 533(10) 64.0(1.2) 117(2.2) Unnotched Izod J/m ft-lbs/in) --- NB 800(15) NB Deflection Temp. under Load °C, 1-75MPa (°F., 254 psi) 207 136 184 183 Gardner Falling Weight Index Nm (in-lbs) <8.8(<80) <8.8(<80) <8.8(<80) >35.2(>320) Type of Failure Brittle Brittle Brittle Ductile The physical property data in Table I demonstrate that a molded composition of this invention in which both the S/MA and the PBT are impact modified and a minor amount of a styrene-maleimide copolymer bearing pendant groups is incorporated achieves the beneficial combination of component physical properties and ductility as compared to the three control experiments. EXAMPLE 5 The moldable composition of Example 4 is blow molded on an Impco B13 blow molding machine into a 10-inch long hourglass-shaped article having a major diameter of about 4 inches. The following approximate blow molding conditions are used: Rear Zone Temp. °C (°F.) 216-227(420 - 440) Front Zone Temp. °C (°F.) 210-221(410 - 430) Die Head Temp. °C (°F.) 216-238(420 - 460) Blow Time (sec.) 20 - 60 Exhaust (sec.) 1 - 5 Parison Drop Time (sec.) 1 - 3 Blow Pressure KPa (psi) 276-552(40 - 80) It will be evident from the foregoing that various modifications can be made to this invention. Such, however, are considered as being within the scope of the invention.

Claims: Claims for the following Contracting States : BE, FR, GB, IT, NL, DE A moldable composition which exhibits ductility upon molding comprising: (a) a rubber modified styrene-maleic anhydride copolymer; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 1 to about 20 parts per each 100 parts by weight of total (a) + (b) + (c). The composition of Claim 1 in which said rubber modified styrene-maleic anhydride copolymer contains from about 1 to about 25 weight percent maleic anhydride. The composition of Claim 1 or Claim 2 in which said rubber modified styrene-maleic anhydride copolymer contains from about 3 to about 30 weight percent rubber. The composition of any one of Claims 1 to 3 in which said rubber modified styrene-maleic anhydride copolymer contains from about 56 to about 94 weight percent styrene. The composition of any one of Claims 1 to 4 in which said amount of copolymer (c) in parts by weight is from about 8 to about 12 per each 100 parts by weight of total (a) + (b) + (c). The composition of any one of Claims 1 to 5 in which said rubber modified styrene-maleic anhydride copolymer has a number average molecular weight within the range of from about 50,000 to about 300,000. The composition of any one of Claims 1 to 6 in which said polybutylene terephthalate ester contains in weight percent from about 5 to about 35 core-shell graft copolymer with the balance being polybutylene terephthalate ester. The composition of any one of Claims 1 to 7 in which said core-shell graft copolymer is selected from butadiene-based core-shell graft copolymers and acrylate-based core-shell copolymer rubbers. A moldable composition which exhibits ductility upon molding comprising: (a) a rubber modified styrene-maleic anhydride copolymer having a number average molecular weight within the range of from about 50,000 to about 300,000; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 8 to about 12 parts per each 100 parts by weight of total (a) + (b) + (c), and wherein copolymer (a) and polyester (b) are present in the composition as co-continuous phases. The composition of any one of Claims 1 to 9 in which said weight ratio of copolymer (a) to polyester (b) is from about 60:40 to about 40:60. A method of producing a moldable composition which comprises blending: (a) a rubber modified styrene-maleic anhydride copolymer; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 1 to about 20 parts per each 100 parts of total (a) + (b) + (c). A molded article produced by molding a composition as claimed in any one of Claims 1 to 10. A molded article produced by molding a composition having two co-continuous phases comprising: (a) a rubber modified styrene-maleic anhydride copolymer having a number average molecular weight within the range of from about 50,000 to about 300,000; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 8 to about 12 parts per each 100 parts by weight of total (a) + (b) + (c), and wherein copolymer (a) and polyester (b) are present in the composition as co-continuous phases. The molded article of Claim 13 in which said weight ratio of copolymer (a) to polyester (b) is from about 60:40 to about 40:60. The molded article of any one of Claims 12 to 14 being a blow molded article produced by blow molding said composition. A ductile, molded composition comprising a first continuous phase, a second continuous phase, and an interface, wherein the first continuous phase comprises a rubber modified styrene-maleic anhydride copolymer, the second continuous phase comprises core-shell graft copolymer rubber modified polybutylene terephthalate, and the interface comprises a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups. The molded composition of Claim 16 in which the weight ratio of styrene-maleic anhydride copolymer to polybutylene terephthalate is from about 65:35 to about 35:65. The molded composition of Claim 16 in which the weight ratio of styrene-maleic anhydride copolymer to polybutylene terephthalate is from about 60:40 to about 40:60. The molded composition of any one of Claims 16 to 18 in which said styrene-maleimide copolymer is present in an amount of from about 1 to about 20 parts by weight per each 100 parts by weight of the total composition, including the styrene-maleimide copolymer. The molded composition of any one of Claims 16 to 19 in which said styrene-maleic anhydride copolymer has a number average molecular weight within the range of from about 50,000 to about 300,000 and contains from about 1 to about 25 weight percent maleic anhydride. The molded composition of any one of Claims 16 to 20 in which said polybutylene terephthalate ester contains in weight percent from about 5 to about 35 core-shell graft copolymer with the balance being polybutylene terephthalate ester. The molded composition of any one of Claims 16 to 21 in which said core-shell graft copolymer is selected from butadiene-based core-shell graft copolymers and acrylate-based core-shell copolymer rubbers. A ductile molded composition comprising a first continuous phase, a second continuous phase, and an interface wherein (a) said first continuous phase is a rubber modified styrene maleic anhydride copolymer having a number average molecular weight within the range of from about 50,000 to about 300,000 and contains in weight percent from about 56 to about 94 styrene, from about 1 to about 25 maleic anhydride, and from about 3 to about 30 rubber, (b) said second continuous phase is a core-shell graft copolymer rubber modified polybutylene terephthalate containing in weight percent from about 65 to about 35 polybutylene terephthalate and from about 35 to about 65 of a core-shell graft copolymer, (c) said interface is comprised of a styrene-maleimide copolymer bearing pendant carboxyl or hydroxyl groups, wherein the weight ratio of the rubber modified styrene maleic anhydride copolymer to core-shell graft copolymer modified polybutylene terephthalate is from about 35:65 about 35: 35, and wherein the styrene maleimide copolymer bearing pendant carboxyl or hydroxyl groups is employed in an amount of from about 1 to about 20 parts per each 100 parts of total composition, including the styrene-maleimide copolymer. The ductile, molded composition of Claim 23 in which said second continuous phase is a butadiene-based core-shell graft copolymer modified polybutylene terephthalate. Claims for the following Contracting State : ES A method of forming a moldable composition which exhibits ductility upon molding, said method comprising blending (a) a rubber modified styrene-maleic anhydride copolymer; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 1 to about 20 parts per each 100 parts by weight of total (a) + (b) + (c). The method of Claim 1 in which said rubber modified styrene-maleic anhydride copolymer contains from about 1 to about 25 weight percent maleic anhydride. The method of Claim 1 or Claim 2 in which said rubber modified styrene-maleic anhydride copolymer contains from about 3 to about 30 weight percent rubber. The method of any one of Claims 1 to 3 in which said rubber modified styrene-maleic anhydride copolymer contains from about 56 to 94 weight percent styrene. The method of any one of Claims 1 to 4 in which said amount of copolymer (c) in parts by weight is from about 8 to about 12 per each 100 parts by weight of total (a) + (b) + (c). The method of any one of Claims 1 to 5 in which said rubber modified styrene-maleic anhydride copolymer has a number average molecular weight within the range of from about 50,000 to about 300,000. The method of any one of Claims 1 to 6 in which said polybutylene terephthalate ester contains in weight percent from about 5 to 35 core-shell graft copolymer with the balance being polybutylene terephthalate ester. The method of any one of Claims 1 to 7 in which said core-shell graft copolymer is selected from butadiene-based core-shell graft copolymers and acrylate-based core-shell graft copolymer rubbers. A method of forming a moldable composition which exhibits ductility upon molding said method comprising blending (a) a rubber modified styrene-maleic anhydride copolymer having a number average molecular weight within the range of from about 50,000 to about 300,000; (b) a core-shell graft copolymer rubber modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 8 to about 12 parts per each 100 parts by weight of total (a) + (b) + (c), to form a composition wherein copolymer (a) and polyester (b) are present as co-continuous phases. The method of any one of Claims 1 to 9 in which said weight ratio of copolymer (a) to polyester (b) is from about 60:40 to about 40:60. A method of forming a molded article comprising molding a composition made by a method as claimed in any one of Claims 1 to 10 A method as claimed in Claim 11 comprising forming a blow molded article by blow molding said composition. A molded article produced by molding a composition having two co-continuous phases comprising: (a) a rubber modified styrene-maleic anhydride copolymer having a number average molecular weight within the range of from about 50,000 to about 300,000; (b) a core-shell graft rubber copolymer modified polybutylene terephthalate ester; and (c) a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups, wherein the weight ratio of copolymer (a) to polyester (b) is from about 65:35 to about 35:65, and the amount of copolymer (c) in parts by weight is from about 8 to about 12 parts per each 100 parts by weight of total (a) + (b) + (c), and wherein copolymer (a) and polyester (b) are present in the composition as co-continuous phases. The molded article of Claim 13 in which said weight ratio of copolymer (a) to polyester (b) is from about 60:40 to about 40:60. The article of Claim 13 or Claim 14 being a blow molded article produced by blow molding said composition. A ductile, molded composition comprising a first continuous phase, a second continuous phase, and an interface, wherein the first continuous phase comprises a rubber modified styrene-maleic anhydride copolymer, the second continuous phase comprises core-shell graft copolymer rubber modified polybutylene terephthalate, and the interface comprises a styrene-maleimide copolymer having pendant carboxyl or hydroxyl groups. The molded composition of Claim 16 in which the weight ratio of styrene-maleic anhydride copolymer to polybutylene terephthalate is from about 65:35 to about 35:65. The molded composition of Claim 16 in which the weight ratio of styrene-maleic anhydride copolymer to polybutylene terephthalate is from about 60:40 to about 40:60. The molded composition of any one of Claims 16 to 18 in which said styrene-maleimide copolymer is present in an amount of from about 1 to about 20 parts by weight per each 100 parts by weight of the total composition, including the styrene-maleimide copolymer. The molded composition of any one of Claims 16 to 19 in which said styrene-maleic anhydride copolymer has a number average molecular weight within the range of from about 50,000 to about 300,000 and contains from about 1 to about 25 weight percent maleic anhydride. The molded composition of any one of Claims 16 to 20 in which said polybutylene terephthalate ester contains in weight percent from about 5 to about 35 core-shell graft copolymer with the balance being polybutylene terephthalate ester. The molded composition of any one of Claims 16 to 21 in which said core-shell graft copolymer is selected from butadiene-based core-shell graft copolymers and acrylate-based core-shell copolymer rubbers. A ductile molded composition comprising a first continuous phase, a second continuous phase, and an interface wherein (a) said first continuous phase is a rubber modified styrene maleic anhydride copolymer having a number average molecular weight within the range of from about 50,000 to about 300,000 and contains in weight percent from about 56 to about 94 styrene, from about 1 to about 25 maleic anhydride, and from about 3 to about 30 rubber, (b) said second continuous phase is a core-shell graft copolymer rubber modified polybutylene terephthalate containing in weight percent from about 65 to about 35 polybutylene terephthalate and from about 35 to about 65 of a core-shell graft copolymer, (c) said interface is comprised of a styrene-maleimide copolymer bearing pendant carboxyl or hydroxyl groups, wherein the weight ratio of the rubber modified styrene maleic anhydride copolymer to core-shell graft copolymer modified polybutylene terephthalate is from about 35:65 about 35: 35, and wherein the styrene maleimide copolymer bearing pendant carboxyl or hydroxyl groups is employed in an amount of from about 1 to about 20 parts per each 100 parts of total composition, including the styrene-maleimide copolymer. The ductile, molded composition of Claim 23 in which said second continuous phase is a butadiene-based core-shell graft copolymer modified polybutylene terephthalate.

Inventors: MCCREADY RUSSELL J, MCCREADY, RUSSELL J.
Applicants: ARCO CHEM TECH, ARCO CHEMICAL TECHNOLOGY, L.P.
Application year: 1989
Main classification: C08L67
IPC codes: C08L67, B29L22, B29K25, B29C49, C08L51, C08L33, C08L25, B29K67, C08L35