Polymer mixture comprising a polyphenylene ether and a polyarylene sulphide

Abstract: The properties of polyphenylene ether-polyarylene sulphide mixtures are improved by the addition of an agent as is known for the improvement of the properties of polyphenylene ether-polyamide mixtures, such as an aliphatic polycarboxylic acid or a derivative thereof. A suitable acid is citric acid.

Description: The invention relates to a polymer mixture comprising a polyphenylene ether, a polyarylene sulfide and an agent to improve the homogeneity as used for polyphenylene ether-polyamide polymer mixture. Polyphenylene ether-polyamide mixtures are described in various patent publications: US-A-4,021,596; JP-A-55/129422 (see WPI Acc. No. 80-83415 C/47); JP-A-62/065351 (see WPI Acc. No. 80-120241/17); JP-A-55/135160 (see WPI Acc. No. 80-87164C/49); JP-A-50/156,561 (see CA, Vol. 84, 1976, page 35, No. 84:106514 v). Polymer mixtures comprising a polyphenylene ether and a polyarylene sulphide have a combination of properties which each of the individual components does not have, for example, a combination of certain mechanical properties, a good resistance against organic solvents, a better processability and flame-retarding properties. In accordance with the desired combination of properties, the two polymers were used in a variety of mixing ratios. The disadvantage of the known polymer mixtures is that the two polymers do not form a homogeneous mixture. Products manufactured, for example, from these polymer mixtures by injection moulding, show a tendency of delamination. This often leads to a surface having pearl gloss. It also often appears that the addition of further additives, for example, agents to improve the impact strength, to non-homogeneous polymer mixtures, only results in a small improvement of the properties. The invention provides polymer mixtures which have a better homogeneity. The invention is based on the discovery that aliphatic polycarboxylic acids or derivatives thereof as defined in claim 1 are suitable agent to improve the homogeneity. EP-A-262901 describes polymer blends comprising as dispersing phase a polyphenylene ether, a crystalline thermoplastic resin matrix phase and a mutual compatibiliser. The crystalline thermoplastic resin can be a polyphenylene sulfide. The mutual compatibiliser can be chosen among a great number of compounds for example unsaturated acids such as fumaric acid. The polymer mixture according to the invention is characterised in that it comprises as an agent to improve the homogeneity aliphatic polycarboxylic acids or derivatives thereof of the general formula: (R 1 O) m R(COOR 2 ) n (CONR 3 R 4 ) s , wherein R is a saturated hydrocarbon group having 2 to 20 carbon atoms with a linear or branched chain; R 1 is a hydrogen atom or an alkyl group, aryl group, acyl group or carbonyldioxy group having 1 to 10 carbon atoms; each R 2 independently of each other is a hydrogen atom or an alkyl group or aryl group having 1 to 20 carbon atoms; each R 3 and R 4 independently of each other represents a hydrogen atom or an alkyl group or aryl group having 1 to 10 carbon atoms; m is equal to 1 and (n + s) is larger than or equal to 2 and n and s each are larger than or equal to zero; and wherein (OR 1 ) is in an alpha position or beta position with respect to a carbonyl group and in which at least two carbonyl groups are separated by 2 to 6 carbon atoms, in a quantity of 0.05 to 5 parts by weight per 100 parts by weight of polyarylene sulphide plus polyphenylene ether. The agents to improve the homogeneity are also referred to as an agent to improve the compatibility or as an agent to improve the properties. All the known agents to improve the homogeneity c.q. compatibility of polyphenylene ether-polyamide mixtures have a chemical group which most likely can react with the amine and/or amide group in the polyamide. Polyarylene sulfides, however, have a quite different structure from polyamides. The applicability of the agents known for polyphenylene ether-polyamide mixtures could not be predicted. The polymer mixture according to the invention comprises in any case the following constituents: A : a polyphenylene ether B : a polyarylene sulfide C : the agent to improve the homogeneity. A. Polyphenylene ether Polyphenylene ethers are compounds known perse . For this purpose reference may be made to the United States Patent Specifications 3,306,874, 3,306,875; 3,257,357 and 3,257,358. Polyphenylene ethers are usually prepared by an oxidative coupling reaction - in the presence of a copper amine complex - of one or more two-fold or three-fold substituted phenols, homopolymers and copolymers, respectively, being obtained. Copper amine complexes derived from primary, secondary and/or tertiary amines may be used. Examples of suitable polyphenylene ethers are: poly(2,3-dimethyl-6-ethylphenylene-1,4-ether) poly(2,3,6-trimethylphenylene-1,4-ether) poly[2-(4'-methylphenyl)phenylene-1,4-ether poly(2-bromo-6-phenylphenylene-1-4-ether) poly(2-methyl-6-phenylphenylene-1,4-ether) poly(2-phenylphenylene-1,4-ether) poly(2-chlorophenylene-1,4-ether) poly(2-methylphenylene-1,4-ether) poly(2-chloro-6-ethy)phenylene-1,4-ether) poly(2-chloro-6-bromophenylene-1,4-ether) poly(2,6-di-n-propylphenylene-1,4-ether) poly(2-methyl-6-isopropylphenylene- 1,4-ether) poly(2-chloro-6-methylphenylene-1,4-ether) poly(2-methyl-6-ethylphenylene-1,4-ether) poly(2,6-dibromophenylene-1,4-ether) poly(2,6-dichlorophenylene-1,4-ether) poly(2,6-diethylphenylene-1,4-ether) poly(2,6-dimethylphenylene-1,4-ether) Copolymers, for example copolymers derived from two or more phenols as used in the preparation of the monopolymers mentioned hereinbefore, are also suitable. Furthermore suitable are graft copolymers and block copolymers of vinylaromatic compounds, for example, polystyrene and of polyphenylene ether as described above. B. Polyarylene sulfide Polyarylene sulfides are polymers known per se. Polyarylene sulfides prepared according to one of the known methods of preparing polyarylene sulfides, for example, as described in US-A-3,354,129 may be used in the polymer mixtures according to the invention. In this method, polyhaloromatic compounds, alkali metal sulfides and organic amides are contacted with each other in polymerisation conditions. A second suitable method is described for example, in US-A-3,919,177 in which a p-dihalobenzene, an alkali metal sulphide, an organic amide and an alkali metal carboxylate are contacted with each other in polymerisation conditions. Polyarylene sulfides which have been subjected to an after-treatment to increase the molecular weight, sometimes termed curing, are preferably used in the polymer mixture according to the invention. This after-treatment is described, for example, in US-A-3,699,087; US-A-3,717,620; US-A-3,725,362 and US-A-3,793,256. Such cured polyarylene sulfides are known for example from Encyclopedia of polymer science, Vol 11, p. 531-533. They have a higher molecular weight and a darker color as compared to non-cured polyarylene sulfide. C. Agent to improve the homogeneity The invention is based on the discovery that polycarboxylic acids as used for the compatibilisation and/or homogenisation of polyphenylene ether-polyamide mixtures are suitable to improve the homogeneity of polyphenylene ether-polyarylene sulphide. The polycarboxylic acids can be defined as follws: Aliphatic polycarboxylic acids or derivatives thereof of the general formula: (R 1 O) m R(COOR 2 ) n (CONR 3 R 4 ) s ,, wherein R is a saturated hydrocarbon group having 2 to 20 carbon atoms with a linear or branched chain; R1 is a hydrogen atom or an alkyl group, aryl group, acyl group or carbonyldioxy group having 1 to 10 carbon atoms; each R 2 independently of each other represents a hydrogen atom or an alkyl group or aryl group having 1 to 20 carbon atoms; each R 3 and R 4 independently of each other represents a hydrogen atom or an alkyl group or aryl group having 1 to 10 carbon atoms; m is equal to 1 and ( n + s ) is larger than or equal to 2 and n and s each are larger than or equal to zero; and wherein (OR 1 ) is in an alpha position or beta position with respect to a carbonyl group and in which at least two carbonyl groups are separated by 2 to 6 carbon atoms, in a quantity of 0.05 to 5 parts by weight per 100 parts by weight of polyarylene sulphide plus polyphenylene ether. The above-mentioned agents are more explicitly described in EP-A-0236593 and the literature reference mentioned therein. In addition to the agent mentioned hereinbefore, the following agents are to be considered. The reaction product of one of the agents mentioned above with a polyphenylene ether. This reaction product may be formed in situ in the polymer mixture according to the invention when the various constituents are mixed in the melt, for example, in an extruder. It is also possible to form this reaction product separately and to then add it to the other constituents of the polymer mixture according to the invention. The ratio of the various constituents in the polymer mixtures according to the invention may be chosen within wide limits. The polymer mixture according to the invention is preferably composed so that it comprises 1-99 parts by weight, even more preferably 10-90 parts by weight, of polyarylene sulphide per 100 parts by weight of polyphenylene ether plus polyarylene sulphide. The quantities to be chosen depent on the kind of properties which it is desired to obtain. However, in all the ratios the possibility exists that delamination occurs. The said delamination can be suppressed by the addition of an agent as described hereinbefore sub C. The minimum quantity of agent C to be used depends on the nature of the agent and on the relative quantity of the constituents A and B. In general, a minimum quantity of 0.1-10 parts by weight of agent C per 100 parts by weight of A plus B will suffice. This quantity can be determined experimentally comparatively easily. In addition to the constituents mentioned hereinbefore the polymer mixture according to the invention may comprise any conventional constituent, for example: styrene homopolymers and styrene copolymers, high-impact polystyrene, agents to improve the impact strength, reinforcing fibres, for example, glass fibres, mineral fillers, agents to improve the stability, dyes and pigments, flame retardants, plasticizers. The polymer mixture according to the invention preferably also comprises one or more agents to improve the impact strength. The addition of such agents leads to a considerable improvement of the impact strength in the homogeneous polymer mixtures according to the invention; an improvement which is larger than that which can be obtained in non-homogeneous polymer mixtures. Any agent suitable for polyphenylene ethers and/or polyarylene sulphides to improve the impact strength may be used in the polymer mixtures according to the invention. Particularly suitable are the so-called core-shell copolymers with a rubbery core and one or more shells. Further suitable agents are the vinylaromatic polydiene di- or triblock copolymers, in which the block copolymer is not hydrogenated or is partially hydrogenated. Partially hydrogenated or non-hydrogenated linear styrene-butadiene-styrene triblock copolymers and partially hydrogenated or non-partially hydrogenated radial styrene-butadiene block copolymers may be mentioned in particular. Some types of polybutadiene, notably those types which are commercially available as a crumbly product, are also suitable. The polyoctenylene rubbers described in DE-A-3,518,277 and DE-A-3,442,273 are also suitable. The polymer mixture according to the invention may comprise in addition one or more additives known for polyphenylene ethers and/or for polyarylene sulphides. In particular may be mentioned: reinforcing fibres, for example, glass fibres and fillers. The polymer mixtures according to the invention are preferably prepared by melt extrusion. In melt extrusion, the individual constituents are provided, for example, in an extruder. The constituents are heated in the extruder, usually to a temperature above the melting temperature of the constituent or one of the constituents having the highest melting-point, for example, the polyarylene sulphide, and are intimately mixed. The so-called extrudate, usually in form of a strand, emanates from the extruder and is then chopped up. The resulting pellets of the polymer mixtures according to the invention can be further processed according to methods known per se for injection moulding of thermoplastic synthetic resins. It has been found in the preparation of the polymer mixtures according to the invention in an extruder that the sequence in which the various constitents are mixed is of importance. For example, polymer mixtures having better properties are often obtained when the polyphenylene ether or a part of the polyphenylene ether to be used is premixed with the agent C in an extruder in a separate step. The pre-extrudate thus obtained is then mixed with the other constituents in an extruder. The invention also relates to products obtained from the polymer mixtures according to the invention.

Claims: A polymer mixture comprising a polyphenylene ether, a polyarylene sulfide and an agent to improve the homogeneity as used for polyphenylene ether-polyamide polymer mixtures, wherein the polymer mixture comprises as an agent to improve the homogeneity aliphatic polycarboxylic acids or derivatives thereof of the general formula: (R 1 O) m R(COOR 2 )n(CONR 3 R 4 ) s , wherein R is a saturated hydrocarbon group having 2 to 20 carbon atoms with a linear or branched chain; R 1 is a hydrogen atom or an alkyl group, aryl group, acyl group or carbonyldioxy group having 1 to 10 carbon atoms; each R 2 independently of each other is a hydrogen atom or an alkyl group or aryl group having 1 to 20 carbon atoms; each R 3 and R 4 independently of each other represents a hydrogen atom or an alkyl group or aryl group having 1 to 10 carbon atoms; m is equal to 1 and (n + s) is larger than or equal to 2 and n and s each are larger than or equal to zero; and wherein (OR 1 ) is in an alpha position or beta position with respect to a carbonyl group and in which at least two carbonyl groups are separated by 2 to 6 carbon atoms, in a quantity of 0.05 to 5 parts by weight per 100 parts by weight of polyarylene sulphide plus polyphenylene ether. A polymer mixture as claimed in Claim 1, characterised in that the polymer mixture comprises as polyarylene sulfide a cured polyarylene sulfide. A polymer mixture as claimed in Claim 1, charaterised in that the polymer mixture comprises as an agent to improve the homogeneity the reaction product of the agent mentioned in Claim 1 with a polyphenylene ether. A polymer mixture as claimed Claim 1, characterised in that the polymer mixture comprises any further agent suitable to improve the impact strength of polyarylene ether and/or polyarylene sulfides. Articles formed from the polymer mixture as claimed in Claim 1.

Inventors: DEKKERS MARINUS EMMANUEL JOHAN, DEKKERS, MARINUS EMMANUEL JOHANNES
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1989
Main classification: C08L71
IPC codes: C08L81, C08L71