Automotive windshield for a head-up display system

Abstract: An automotive windshield (10) for a head up display system is disclosed. The windshield (10) includes a hologram (18, 30) embedded within the windshield assembly. In fabricating the windshield, the hologram, is deposited on a carrier substrate. The hologram (18, 30) is initially adhered to the windshield interlayer (16) and the carrier substrate is removed, leaving the hologram (18, 30). The windshield (10) is then assembled and laminated.

Description: This invention relates to a method of assembling a laminated holographic transparency which can be used in a head up display system incorporated into an automotive windshield. A head up display system is a system that displays information to a viewer while he simultaneously views the real world around and through the display. A head up display system is often incorporated into aircraft cockpits for pilots to monitor flight information, and more recently the systems have been used in land vehicles, such as cars, trucks and the like. The display system is generally positioned so that the viewer does not have to glance downward towards the vehicle dashboard and away from the viewing area in front of the vehicle as is normal for vehicle operation to view the operating information. Head up display systems generally include a display projection system, a collimator and a combiner. The projection system includes a light source that projects operating information through the collimator which generally aligns the projected light rays. The collimated light is reflected off the combiner, which is a wavelength selected element positioned in a portion of the operator field of view, such that the operating information which is reflected off the combiner may be easily viewed by the operator. Depending on how the collimator aligns the projected light rays, the reflected image may be focused anywhere from a position immediately in front of the vehicle to optical infinity. The combiner may be any wavelength selective reflective material such as a holograph or reflective metallic film. In a holographic head up display windshield system, the combiner is a hologram which may be applied to a film carrier and positioned in the interlayer between the transparent glass plies of the windshield. It can be appreciated that a head up display system providing important vehicle information such as, for example, fuel supply and vehicle speed positioned within the motorist field of vision through the windshield will permit the motorist to safely maintain eye contact with the real world while simultaneously viewing the display information. The interlayer material in a windshield is typically a heat sensitive material, such as polyvinylbutyral, which flows during the windshield laminating operation. When the holographic combiner is embedded within the interlayer, the combiner may distort due to the flowing characteristics of the interlayer material, adversely affecting its reflective properties and optical quality of the windshield. In addition, the combiner reduces the windshield optical quality by introducing additional materials between the windshield glass plies. It would be advantageous to have the combiner as thin as possible and to maintain the combiner surface parallel to the major surfaces of the glass plies so as to reduce optical distortion through the windshield and maintain the reflective properties of the combiner. U.S-A-1,871,877 to Buckman teaches a display system having a glass sheet mounted on the windshield or dashboard which reflects instrumentation information to the vehicle operator. U S-A-2,264,044 to Lee teaches a motor vehicle speedometer wherein an illuminated speedometer display is reflected off the inboard surface of the vehicle windshield. U S-A-2,641,152 to Mihalakis teaches a vehicle indicator optical projection device wherein instrumentation information is reflected off of a reflecting screen on the inboard surface of the vehicle windshield. The reflecting surface has a satin finish and can be metal, glass, or plastic. U S-A-2,750,833 to Gross teaches an optical display system for eliminating double images which occur in reflector type sights such as are used in gun sighting installations in aircraft, by polarization of the collimated light beam and separation of the two-way branches by means of rotation of the plane of polarization and extinction of one of the branches. U S-A-3,276,813 to Shaw, Jr. teaches a motor vehicle display system which utilizes a highly reflective coating on the inboard surface of the vehicle windshield to reflect instrumentation information to the vehicle operator. U S-A-3,446,916 to Abel teaches an image combiner utilizing a portion of the aircraft window, the inner surface of the portion being coated with a partially reflecting film and being paraboloidal in shape. U S-A-3,899,241 to Malobicky, Jr. et al. teaches a windshield adapted for use in aircraft and includes a transparent reflective coating on the inboard surface in the center portion of the forward vision area to form a vision image receiving area. Vehicle information is reflected off the reflective coating to the vehicle operator. U S-A-3,940,204 to Withrington and 4,218,111 to Withrington et al. teach an optical display system utilizing holographic lenses. U S-A-4,261,635 to Freeman teaches a heads-up display system including a holographic combiner positioned inboard of the vehicle windshield. The hologram is disposed substantially orthogonal to and midway along an axis between the observer eye position and the projection opticals so as to deviate light from an image produced by the projection opticals to the observer eye with minimal field aberration. U S-A-4,398,799 to Swiff teaches a heads-up display system wherein the pilots view is recorded on a head mounted camera to which light from the outside scene and superimposed display is reflected off a head mounted mirror. U S-A-4,613,200 to Hartman teaches a head-up display system using two parallel holographic optical elements to reflect instrumentation information to the vehicle operator. One of the elements is made part of or attached to the vehicle windshield. U S-A-4,711,544 to Iino et al. teaches a display system for vehicle wherein instrumentation information is reflected off of the front glass of the vehicle so that the image display can be formed in a desired position aligned with the line of sight of the driver without obstructing the front sight of the driver. These patents teach various display systems. However, they do not teach a holographic windshield using solely a holographic film positioned within the windshield as the display reflecting surface, i.e., collimator, for the display system. WO 88/09942 which is a document according to Article 54(3) EPC refers to a windshield display system for automobiles comprising a holographic combiner laminated within the plies of the windshield. The lamination process includes removal of the holographic combiner from a carrier prior the final lamination process. It is the object of the invention to provide a method for preparing a laminated holographic transparency having such a structure that any optical distortion of an image viewed through an automotive windshield resulting from additional elements within said windshield is due solely to said hologram. This object is attained by a method of assembling a laminated holographic transparency by positioning an interlayer on a surface of a rigid glass ply, positioning a hologram supported on a carrier on a major surface of said interlayer sheet, laminating said glass ply interlayer sheet, hologram and carrier together by heating and applying pressure to form a unitary structure, removing said carrier from said said structure, laminating at least one additonal rigid glass ply to said interlayer sheet wherein said interlayer sheet and said hologram are positioned between said glass plies. This object is also attained by a method of assembling a laminated holographic transparency by adhering a hologram supported on a carrier to a major surface of a plastic interlayer sheet wherein said hologram is positioned between said carrier and said interlayer sheet by heating the portion of said interlayer sheet in contact with said hologram, removing said carrier from the hologram suck that said hologram remains adhered to said interlayer sheet, securing a glass ply to said interlayer sheet wherein said hologram is positioned between said glass ply and said interlayer sheet and laminating at least one additional glass ply to said interlayer sheet wherein said interlayer sheet is positioned between said glass plies. According to another embodiment this object is attained by a method of assembling a laminated holographic transparency by adhering a hologram supported on a carrier to a major surface of a glass ply wherein said hologram is positioned between said carrier and said glass ply by heating the portion of said glass ply in contact with said hologram, removing said carrier from the hologram such that said hologram remains adhered to said glass ply securing a plastic interlayer sheet to said glass ply wherein said hologram is positioned between said glass ply and said interlayer sheet and laminating at least one additonal glass ply to said interlayer sheet wherein said interlayer sheet is positioned between said glass plies. The hologram is initially developed on a flexible carrier substrate. This allows easy positioning of the hologram at the desired spot within the windshield. In assembling the windshield, the hologram and carrier are secured to either the interlayer material or glass surface of one of the glass plies during a preliminary assembly operation. The carrier substrate is then removed from the hologram, for example by peeling, so that only the hologram is left as the reflective element of the windshield. Depending on the sensitivity of the hologram to temperature and pressure variables, the laminating technique used to assemble the windshields is modified so as to maintain the integrity of the hologram throughout the assembly operation. Brief Description of the Drawing Figure 1 is a schematic of a heads-up display system incorporating a holographic windshield. Figure 2 is an enlarged cross-sectional view taken through lines 2-2 in Figure 1 showing the hologram within the windshield assembly. Figures 3 through 6 are enlarged cross-sectional views similar to that shown in Figure 2 of alternative embodiments of a windshield. Detailed Description of the Invention The present invention teaches a method for assembling a laminated windshield with a combiner for a heads up display system laminated between the glass plies of the windshield, but it is understood that the invention may be used for any type of vehicle or structure where a thin undistorted combiner is to be used in conjunction with the transparency. For the purposes of clarity, as used herein, the term "hologram" means a holographic recording media or film, such as dichromated gelatin, the term "holographic element" means the hologram supported on a carrier film or substrate, the term "combiner" means either a hologram or a holographic element positioned relative to the transparency to combine a virtual image of a projected image source with the real world view. With reference to Figures 1 and 2, the transparency of the head up display system comprises a motor vehicle windshield 10 including outer glass ply 12, inner glass ply 14, and interlayer sheet 16 and incorporates a combiner 18 for reflecting information carrying light rays into the field of vision of a motorist 20. The combiner 18 is laminated within the windshield 10, directly against a major surface of either glass ply 12 or 14, as will be discussed later. Light rays emanate from an image source 22 and are projected onto the combiner 18. The combiner 18 is manufactured to reflect wavelengths of light included within a predetermined narrow bandwidth which corresponds to the wavelength and angle of incidence of the light that is projected onto the combiner 18. A suitable projection assembly 24 is preferably mounted immediately beneath the upper surface 26 of the vehicle dashboard 28 and is positioned between the image source 22 and the combiner 18 to project the light onto the combiner 18. The light rays projected onto the combiner 18 are collimated so as to create a virtual image anywhere in front of the vehicle and preferably about 3 to 15m (10 to 50 feet) in front of the windshield 10. In situations where the combiner 18 is not a planar surface, for example, if the combiner 18 is on or within a curved windshield, the optical assembly 24 will also have to compensate for spherical and optical aberrations introduced by the curvature of the windshield. The image source 22 preferably is a transmissive liquid crystal display (LCD) that is adequately illuminated to project information carrying light rays through the optical assembly 24 to the combiner 18. The displayed image (not shown) may include numerical or graphical symbols representing, for example vehicle speed, fuel level, engine RPM, temperature, and warning messages. Referring to Figure 2, the combiner 18 is positioned between the glass plies of the windshield 10 as will be described later. The combiner 18 is located within a particular region relative to the vehicle operator's direct line of sight. The preferred location of the combiner 18 provides an information display region that permits peripheral viewing of the outside real world scene as the operator monitors the display. It is contemplated that alternative locations will also provide an effective head up display for a vehicle windshield. Referring to Figure 2, in the windshield 10 the combiner 18 is a hologram laminated between the transparent glass plies of the windshield 10. It has been found that conventionally manufactured holograms may require modified processing to withstand a typical windshield lamination process which normally heats the windshield to about 135°C (275°F) at a pressure of about 14.1 kg/cm² (200 psi), and that the hologram is more easily manufactured in planar form and then bent to conform to the final contour of the windshield 10 during lamination. Attention is now turned to the processing of one particular hologram and holographic element that was incorporated into a laminated windshield assembly for use as a combiner, but it is understood that the present invention is not limited to any particular type of hologram or reflective surface. Additional holographic windshield 10 were fabricated using other holograms supplied by Flight Dynamics, Inc., Portland, Oregan. A holographic element is formed by depositing a layer of holographic recording medium, between about 10 to 40 µm in thickness, on a substrate. The substrate which may be either transparent or opaque, is secured in a planar orientation by a support mechanism, such as a conventional vacuum holder, as the layer of holographic recording material is deposited onto the substrate. A suitable holographic recording material would be a photosensitive emulsion such as, for example, a VSP grade gelatin available from J. T. Baker Chemical Company. The substrate is flexible and preferably is a polyester or polycarbonate film approximately 0.125 millimeters in thickness. If the selected substrate is hydrophobic, a suitable subbing agent, i.e. primer, is applied to the surface of the substrate upon which the layer of gelatin is deposited. The subbing agent provides the surface with hydrophilic characteristics that provide effective bonding between the gelatin and the substrate. After it is deposited on the substrate, the gelatin layer is sensitized in a solution of ammonium dichromate as is known in the art. The gelatin is then exposed to light to create the hologram. Preferably the hologram is exposed using the techniques described in U S-A-4,582,389 to Cannata et al.. Once exposed, the hologram is processed in a conventional manner as is known in the art. One acceptable processing procedure comprises washing the holographic element for 15 minutes in running water having a temperature of between 16°C and 20°C (60°F and 68°F); soaking it in isopropanol for two minutes with continuous agitation; and drying the holographic element in a vacuum oven for two hours at a temperature at least about 100°C (212°F). After the initial processing, secondary processing of the holographic element may be required to ensure that the hologram will withstand the temperatures and pressures of a windshield lamination process. The secondary processes entail an optional step of applying a moisture barrier to the hologram followed by heat stabilizing the hologram and storing it in a relatively low humidity environment. The holographic element described above is dipped into a solution of a highly volatile solvent and a solute. After the solvent is evaporated, the remaining solute forms an effective moisture barrier covering the exposed surface of the hologram and serves as a humidity stabilizing agent for the hologram during a lamination process. A preferred solution is a two percent by weight solution of fluorocarbon powder based on a polychlorotrifluoroethylene resin such as that manufactured by M. W. Kellogg Company under the Trademark KEL-F, dissolved in liquid freon. After the holographic element is dipped in the solution, the freon is evaporated, leaving the KEL-F moisture barrier coating the hologram surface. Although a two percent solution is preferred, acceptable results can be obtained with a 0.5% to 5% solution. The above described deposition of a moisture barrier would be unnecessary if the interlayer used in the lamination process has sufficiently low moisture content, such as 0.2% or less, so as to not adversely affect the hologram. After the moisture barrier has been applied, the hologram is heat stabilized by placing the holographic element in a vacuum oven and heating it from room temperature to a peak temperature of between 120°C and 140°C (220°F to 285°F), within 30 to 90 minutes, and then slowly cooled for 60 to 120 minutes until it reaches room temperature. In the holographic element described above, it is preferably heated to about 135°C (275°F) for about 60 minutes and then cooled to room temperature in about 90 minutes. Finally, the holographic element is stored in an environment having a relative humility of less than about 30% and a temperature of between 20°C and 30°C (68°F and 86°F) until it is laminated into the windshield, as will be discussed later. After this secondary processing, the holographic element is approximately 0.15mm thick. Referring to Figure 2, it is noted that the combiner 18 of windshield 10 includes only a hologram 30 and not the substrate on which the hologram 30 is processed as discussed earlier. With continued reference to Figure 2, the holographic windshield 10 includes inner glass ply 14 laminated to outer glass ply 12 with an interlayer material 16, such as polyvinylbutyral (PVB), positioned therebetween. Glass plies 12 and 14 are bent in any conventional well known shaping technique to provide a pair of complimenting shaped glass plies. In the particular embodiment of the present invention illustrated in Figure 2, hologram 30 is positioned directly against the outboard surface 32 of inner ply 14. Holograms are sensitive to both heat and pressure. In a windshield laminating operation, for example as taught in U S-A-4,102,722 to Shoop, the windshield assembly is laminated for 30 minutes at a pressure of 14kg/cm (200 psi) and 135°C (275°F). It has been found that the hologram described earlier would be damaged if subjected to these conditions so that it could not be used as a combiner. As a result the fabrication of the windshield 10 was modified to be a multi-step operation that includes two laminating cycles. In the first laminating operation, the holographic element, which includes the hologram 30 on a carrier film, is laminated to a layer of PVB interlayer which in turn is laminated to the outer glass ply 12 to form a bilayer assembly. In one particular embodiment of the invention, the interlayer is first positioned on the inboard surface 34 of the outer glass ply 12. The interlayer sheet 16 is coated with an adhesive, such as but not limited to polyurethane, in the area that will come in contact with the holographic element. The element is then placed over the polyurethane coated area with the hologram 30 of the element in direct contact with the adhesive. The remainder of the bilayer assembly i.e., that portion of the interlayer 16 not covered by the holographic element is covered with a slip sheet having the same thickness as the holographic element. The slip sheet is a material that will not stick to the interlayer 16 during a laminating operation and may be, for example polyethylene or material with a release coating such as silicone based film. The slip sheet includes an opening located and sized to generally correspond to the location and size of the holographic element positioned on the interlayer 16. A press plate which may be the complimenting curved inner glass ply 14, is then positioned over the bilayer assembly and slip sheet and the total assembly is laminated. Although not limiting in the present invention, in the preferred laminating operation, the assembly is placed in a bag and de-aired in a manner well known in the art and as taught in U S-A-3,311,517 to Keslar et al., and autoclaved at a temperature within the range of 71°C to 93°C (160°F to 200°F) at 1.05 kg/cm² to 4.22 kg/cm² (15 psi to 60 psi) for 15 to 45 minutes. With the type of hologram 30 described earlier, the bilayer assembly is preferably laminated at about 79°C (175°F) and 1.76 kg/cm² (25 psi) for about 30 minutes. After the first laminating cycle, the bilayer assembly is removed from the bag and the press plate and slip sheet are removed from the interlayer. The carrier substrate is then separated from the hologram by a peeling operation to form a bilayer windshield 36 as shown in Figure 4 which has only the hologram secured to the interlayer. After peeling, the trilayer windshield 10 is assembled. The inner glass ply 14 is positioned over the interlayer 16 and the windshield assembly is rebagged, de-aired, and laminated in an autoclave to form the final product. This laminating operation must be controlled so as to not to destroy the hologram due to excessive heat and/or pressure. Using a hologram of the type discussed earlier, the temperatures and pressures are increased in steps. Although not limiting in the present invention in one particular laminating process, the temperature is increased from room temperature to a temperature within the range of 60°C to 79°C (140°F to 175°F) and held for about 10 to 20 minutes. The temperatures are then increased to within a range of approximately 107°C to 135°C (225°F to 275°F) and held for approximately 45 to 120 minutes. The temperature is then reduced to room temperature. With respect to the pressure, the autoclave is pressurized to within a range of approximately 1.76 kg/cm² to 7.03 kg/cm² (25 psi to 100 psi) and held until the temperature within the autoclave reaches the second elevated temperature range. At this time the pressure is increased to within a range of approximately 10.5 kg/cm² to 15.8 kg/cm² (150 psi to 225 psi) and held until the temperature is reduced back to room temperature. With the type of hologram 30 described earlier the second laminating operation preferably includes heating the assembly to about 66°C (150°F) for about 15 minutes and then increasing the temperature to about 116°C (240°F) and holding it at temperature for about 90 minutes before cooling it to room temperature. With respect to the pressure, the assembly is subjected to a pressure of about 1.05 kg/cm² (50 psi) until the temperature reaches about 116°C (240°F) at which time the pressure is increased to about 14.1 kg/cm² (200 psi) and held until the temperature is reduced back to room temperature. If required, prior to the final assembly of the windshield, the interlayer 16 may be sprayed with a solution of PVB to provide an embossed surface on the interlayer 16 so as to help de-air the assembly prior to the second laminating operation. In addition, a thin layer of polyurethane or other suitable thermoplastic adhesive may be applied either to the exposed hologram surface, and/or the outboard surface 32 of the inboard glass ply 14 in the area where the hologram will contact the inner glass ply to help wet and bond the hologram's surface. Although the windshield de-airing is preferably done by a bagging process, it would be obvious to one skilled in the art that other de-airing techniques such as using de-airing channels or prepressing rolls as taught in U S-A-3,281,296 to Jameson and 4,696,713 to Okafuji et al., respectively. The relative adhesion characteristics between the hologram and the interlayer and the hologram and the substrate may affect the peeling operation. If the hologram/interlayer adhesion is greater than the hologram/substrate adhesive, some of the adhesive between the hologram and substrate may remain on the exposed hologram surface after peeling. If the hologram/interlayer adhesion is less than the hologram/substrate adhesion, the hologram may shear, leaving imperfections in the exposed hologram surface. The former condition is preferred. As an alternative to the previously described fabrication method, the hologram 30 may be secured directly to the outboard surface 32 of the inner glass ply 14 during an initial operation. Although not limiting in the present invention, a vacuum pressing technique may be used to secure the hologram 30. In particular, the hologram 30 and/or the portion of the inner glass ply 14 to be in contact with the hologram 30 is coated with an adhesive, such as polyurethane. The holographic element is then positioned on the inner glass ply 14 with the hologram 30 contacting the surface 32. A conformable pressing member, such as for example, a vacuum blanket, may be positioned over the element to remove air from between the glass 14 and hologram 30 and press the element against the glass ply 14. When a thermoplastic adhesive is used, such as polyurethane, the assembly is heated to the range of 71°C to 93°C (160°F to 200°F) and preferably to about 79°C (175°F) during the de-airing step. After the element is secured, to the glass ply 14 the blanket is removed, the assembly is cooled, and the carrier substrate is peeled off the assembly leaving the glass ply 14 with only the hologram 30. The windshield 10 is then assembled i.e., the interlayer 16 is placed on the outboard surface of the inner glass ply 14 and the outer glass ply 12 is positioned over the interlayer. The assembled windshield is de-aired and laminated in an autoclave as discussed earlier in the second laminating operation. An an alternative to removing the carrier substrate by peeling, the substrate may be made of a material that can be dissolved once the hologram is secured to the glass or interlayer ply. Although not limiting in the present invention, the holographic recording medium may be deposited on a substrate of polystryrene. A subbing agent may be applied to obtain suitable adhesion. The hologram is processed and secured to the interlayer or glass surface of the windshield as discussed earlier. The polystryrene carrier substrate is then dissolved using, for example pentane or benzene, leaving the hologram secured in place. It should be noted that for a curved windshield, when the holographic element is secured either to the interlayer of the bilayer assembly or a glass ply, the element is curved to conform to the windshield curvature during the initial securing operation. It is believed that, as an alternative, the element may be secured to a flat interlayer 16, without a glass ply, by pressing and heating the element and interlayer 16 between slip sheets and flat press plates. After the interlayer 16 is cooled, the carrier substrate can be peeled from the interlayer 16, leaving the hologram 30. The windshield 10 may then be assembled and laminated, using the interlayer 16, as discussed earlier, to form the trilayer windshield configuration 10 illustrated in Figure 2 or the bilayer windshield configuration 36 and 38 illustrated in Figures 4 and 6, respectively. It should be appreciated that the temperatures and pressures used during the glass windshield laminating steps are dictated by the sensitively of the hologram to these variables. The less sensitive the hologram is to these variables, the closer the temperatures and pressures can be to conventional windshield laminating parameters. If the hologram 30 could survive exposure to the combined temperature and pressure of a conventional windshield laminating operation, it is believed that the multi-step operation as described above would not be necessary. It should be further appreciated that the laminating cycle described is for a glass windshield. Rather than modifying the hologram, if the laminating cycle of the assembly were different, for example if different transparent plies were used that require lower elevated temperatures and/or pressures, a one step laminating cycle could be used. As a further improvement to the process, if the hologram 30 could survive the bending temperature of the ply, e.g., about 648°C (1200°F) for glass, it can be appreciated that the hologram 30 may be adhered to the glass before a bending and shaping operation. There are several advantages resulting from positioning the combiner 18 against a glass ply and eliminating the carrier substrate. First, the glass ply provides a rigid, optically acceptable surface that will not warp, flow or deform during the laminating operation so that the hologram does not deform during lamination and remains parallel to the glass surface. In addition by eliminating the carrier, an additional element is removed from the windshield that may cause optical defects in the windshield as well as additional reflective surfaces within the windshield. Furthermore, it is believed that the incorporation of the entire holographic element as the combiner into the windshield would require multiple interlayer plies of various thicknesses to offset the thickness of the holographic element. Another advantage is that the glass provides a superior moisture barrier along the contacted major surface of the hologram. It should be obvious to one skilled in the art that the hologram may be embedded within the interlayer of the windshield rather than secured to the glass ply simply by positioning a second interlayer sheet between the bilayer assembly with the hologram and the inner glass ply and laminating the assembly as discussed earlier as shown in trilayer windshield configuration 40 in Figure 3 and bilayer configuration 42 in Figure 5.

Claims: A method of assembling a laminated holographic transparency (10) by positioning an interlayer (16) on a surface (34) of a rigid glass ply (12), positioning a hologram (30) supported on a carrier on a major surface of said interlayer sheet (16), laminating said glass ply (12), interlayer sheet (16), hologram (30) and carrier together by heating and applying pressure to form a unitary structure, removing said carrier from said structure, laminating at least one additional rigid glass ply (14) to said interlayer sheet (16) wherein said interlayer sheet (16) and said hologram (30) are positioned between said glass plies (12, 14). A method of assembling a laminated holographic transparency (10) by adhering a hologram (30) supported on a carrier to a major surface of a plastic interlayer sheet (16) wherein said hologram (30) is positioned between said carrier and said interlayer sheet (16) by heating the portion of said interlayer sheet (16) in contact with said hologram (30), removing said carrier from the hologram (30) such that said hologram (30) remains adhered to said interlayer sheet (16), securing a glass ply (12) to said interlayer sheet (16) wherein said hologram (30) is positioned between said glass ply (12) and said interlayer sheet (16) and laminating at least one additional glass ply (14) to said interlayer sheet (16) wherein said interlayer sheet (16) is positioned between said glass plies (12, 14). A method of assembling a laminated holographic transparency (10) by adhering a hologram (30) supported on a carrier to a major surface of a glass ply (12) wherein said hologram (30) is positioned between said carrier and said glass ply (12) by heating the portion of said glass ply (12) in contact with said hologram (30), removing said carrier from the hologram (30) such that said hologram (30) remains adhered to said glass ply (12), securing a plastic interlayer sheet (16) to said glass ply (12) wherein said hologram (30) is positioned between said glass ply (12) and said interlayer sheet (16) and laminating at least one additional glass ply (14) to said interlayer sheet (16) wherein said interlayer sheet (16) is positioned between said glass plies (12, 14). The method of claims 1 or 2 or 3 wherein said removing step includes peeling off said carrier from said adhered hologram (30). The method of claims 1 or 2 or 3 wherein said removing step includes dissolving said carrier from said adhered hologram (30). The method of claim 1 wherein in said first laminating step the transparency is heated to a temperature in the range of 71°C to 93°C (160°F to 200°F) and a pressure in the range of 1,034 to 4,137 bar (15 to 60 psi) is applied for 15 to 45 minutes. The method of claim 6 wherein said transparency is heated to approximately 80°C (175°F) at a pressure of approximately 1,724 bar (25 psi) for approximately 30 minutes. The method of claims 1 or 2 or 3 wherein said laminating step further includes the step of applying a pressure to said transparency in the range of approximately 1,724 to 6,845 bar (25 to 100 psi), maintaining said pressure until said temperature is elevated to the range between 107°C to 135°C (225°F to 275°F), increasing said pressure to 10,340 to 15,510 bar (150 to 225 psi) and maintaining said pressure until the temperature of said assembly is reduced approximately to room temperature. The method as in claim 8 wherein said second laminating step includes the steps of heating to about 66°C (150°F) for approximately 15 minutes, increasing said temperature to about 116°C (240°F), maintaining said temperature for approximately 90 minutes and reducing said temperature to room temperature, and further includes the steps of applying a pressure of about 3,448 bar (50 psi) while said transparency is initially heated, maintaining said pressure until said temperature is elevated to about 116°C (240°F), increasing said pressure to about 13,790 bar (200 psi) and maintaining said pressure until said temperature is reduced to room temperature. The method of claim 2 wherein said adhering step includes applying adhesive between said hologram (30) and said plastic interlayer sheet (16), positioning a pressing member in overlaying relation over said carrier and removing air from between said plastic interlayer sheet (16) and said hologram (30). The method of claim 3 wherein said adhering step includes applying adhesive between said hologram (30) and frist glass ply (12), positioning a pressing member in overlaying relation over said carrier and removing air from between said frist glass ply (12) and said hologram (30).

Inventors: DUNAWAY JAMES HUBERT, FREEMAN GLENN EDWARD, KORENKIEWICZ KAREN JANE, VALIMONT JAMES LAWRENCE, DUNAWAY, JAMES HUBERT, FREEMAN, GLENN EDWARD, KORENKIEWICZ, KAREN JANE, VALIMONT, JAMES LAWRENCE
Applicants: PPG INDUSTRIES INC, PPG INDUSTRIES, INC.
Application year: 1989
Main classification: G02B27
IPC codes: B60K35, G02B5, G09F9, G02B27, G03H1, B60R16