METHOD FOR PRODUCING AQUEOUS SOLUTIONS OF BASIC POLY ALUMINUM SULPHATE

Abstract: The present invention relates to a process for the preparation of a basic poly aluminum sulphate solution (PAS) having the following formula: [Al A (OH) B (SO₄) C (H₂O) E ] n in which n is a positive integer; A is 1.0; B ranges from 0.75 - 2.0; C ranges from 0.5 - 1.12; and E is larger than 4 when the product is in aqueous form, wherein the basicity of said basic poly aluminum sulphate solution is defined as B/3A X 100 and said basicity is 25-66% and wherein B + 2C = 3. The process comprises reacting aluminum sulphate solution with a suitable alkali metal aluminate under high shear mixing and recovering the desired product.

Description: The present invention relates to a novel method for the preparation of basic poly aluminum sulphate (PAS). Poly aluminum sulphate is a relatively new product that has been extensively developed over the past few years especially for the field of water purification where it is useful as a flocculating agent. Various processes for the preparation of poly aluminum sulphate have been developed over the years. Traditional methods follow a partial neutralization of aluminum sulphate, referred to in the general trade (perhaps erroneously) as Alum, with hydroxyl groups from lime, caustic soda, soda ash, ammonium hydroxide or other alkali sources to a pH of approximately 3.5 to 4.3. Typically, the pH value tends to be 3.8 because aluminum hydroxide is not precipitated at or below this pH value. Stabilizers such as phosphates, or chlorides may also be added to partially replace sulphate groups, or alternatively organic complexing agents such as sodium heptonate, citric acid, sorbitol, sodium citrate, sodium tartrate, sodium gluconate and the like may be added separately to stabilize the aqueous poly aluminum sulphate as much as possible. For a good review of the various processes that have been developed over the years for synthesizing poly aluminum sulphate, one may refer to Canadian Patents 1,123,306, 1,203,364, 1,203,664 or 1,203,665, and to U.S. patents 4,284,611 and 4,536,384. For instance, in Canadian Patent 1,203,364 aluminum sulphate is neutralized with sodium hydroxide to prepare an aluminum hydroxide gel according to the following reaction: 4Al₂(SO₄)₃+ 24 NaOH → 8Al(OH)₃ + 12Na₂SO₄ Next, poly aluminum sulphate is prepared from this gel according to the following reaction: 8Al(OH)₃+ 4Al₂(SO₄)₃ → 4Al₄(OH)₆(SO₄)₃ This reaction yields a 50% basic product. Using this method, 4 moles of poly aluminum sulphate and 12 moles of sodium sulphate by-product are obtained, thereby representing a significant disadvantage. A further considerable disadvantage of this method is that a "filter cake" of aluminum hydroxide gel must be prepared before the desired product can be synthesized. Therefore, this supposes a two-step process from which large amounts of by-products are obtained. Canadian Patent 1,203,364 also teaches the neutralization of sodium aluminate with sulfuric acid to produce an amorphous aluminum hydroxide gel according to the following reaction: 4Na₂Al₂O₄ + 4H₂SO₄ + 8H₂O → 8Al(OH)₃ + 4Na₂SO₄ . This gel is then further reacted with aluminum sulphate to produce basic poly aluminum sulphate. Then for a 50% basic product: 8Al(OH)₃ + 4Al₂(SO₄)₃ → 4Al₄(OH)₆(SO₄)₃ we note that although most of the sodium sulfate is removed from the aluminum hydroxide gel through filtration, it remains nevertheless a wasted and costly by-product. Again, this is a two-step process which is difficult to perform because one must also go through the production of a "filter cake" of aluminum hydroxide gel. This yields 4 moles of by-product per 4 moles of product. The processes described in the remaining above-mentioned patents, which do not require a prior hydroxide gel formation, still present serious drawbacks. For example, with these processes, it is difficult to produce a concentrated marketable product containing the require typical 7 to 10% of Al₂O₃ concentration because diluted alkalies must be added slowly to aluminum sulphate in order to prevent simultaneous precipitation of aluminum hydroxide. Furthermore, in most instances, by-product losses are considerable. Solutions containing substances such as calcium or sodium sulphate or ammonium sulphate are the by-products that are usually generated when the processes described in the patents cited above are used. Typically, a by-product loss ranging from 20 to 30% by weight depending on basicities produced and sources of alkali used is almost unavoidable. Mixing and filtration problems are also associated with most of the processes known in the art. For example, when lime is used as the alkali in the process, serious mixing and filtration problems can be encountered. Also, crystallisation problems will unavoidably be encountered when sodium sulphate is formed as a by-product. Another method of producing a flocculant for water treatment is disclosed in UK 1,399,598 published on 2 July 1975. While this method also uses high shear mixing, the process and product are different from the present invention in that basic sodium silicate and an acidic aluminium salt are mixed (page 1, lines 59 to 62) at high dilution (page 2, lines 35 to 37) to produce a stable dispersion and not a solution (page 2, lines 82 to 84) which is preferably made just prior to injection of the product into the water to be treated (page 3, lines 97 to 107). Therefore, although the technical advantages of poly aluminum sulphate have been recognized for several years, there are still some serious problems associated with its preparation and handling. It appears that it would be highly desirable to provide a process that would minimize the losses that can be encountered through the production of by-products as well as problems associated with the separation of these by-products. In accordance with the present invention, there is provided a process for the preparation of a basic poly aluminum sulphate solution product (PAS) having the following formula: [Al A (OH) B (SO₄) C (H₂O) E ] n in which n is a positive integer; A is 1.0; B ranges from 0.75 - 2.0; C ranges from 0.5 - 1.12; and E is larger than 4, wherein the basicity of said basic poly aluminum sulphate solution is defined as B/3A X 100 and said basicity is 25-66% and wherein B + 2C = 3 , said process comprising the step of reacting in a one step process an aluminum sulphate solution with an alkali metal aluminate solution under high shear mixing conditions producing a velocity gradient exceeding 1000 sec⁻¹ sufficient to produce a reactive Al(OH)₃ gel and to produce a substantially transparent basic poly aluminum sulphate solution and recovering the desired product. In this disclosure, what is meant by a "one step" process is that all the additions of reactants, their mixing, and the collection of the desired product are done in a single one step operation in a single reaction vessel, without any precipitation of a solid product or by-product which must be removed from the reaction solution by a phase separation, for example by a solid/liquid separation such as filtration to yield a filter cake. The most important advantages resulting from the use of the product of the process of the present invention is the fact that smaller amounts of by-product for given amounts of product are produced and the formation of an aluminum hydroxide gel "filter cake" is avoided. The process of the present invention represents a clear breakthrough in the preparation of poly aluminum sulphate because it reduces the amount of by-products to approximately 25% of the by-products that were obtained with most of the already existing methods. Furthermore, the major by-product (sodium sulphate), being obtained in lesser amounts, can be maintained in the final product to enhance its performance since the level of by-product obtained will not lead to crystallisation of sodium sulphate at ambient temperatures. The process of the present invention will be explained in more detail in the following description. The product The product to be prepared in accordance with the present invention is a basic poly aluminum sulphate solution having the following general formula: [Al A (OH) B (SO₄) C (H₂O) E ] n in which n is a positive integer; A is 1.0; B ranges from 0.75 - 2.0; C ranges from 0.5 - 1.12; and E is larger than 4 when the product is in aqueous form, wherein the basicity of said basic poly aluminum sulphate solution is defined as B/3A X 100 and said basicity is 25-66% and wherein B + 2C = 3 . The value of integer n will increase as the basicity of the product increases. The basicity of the product is more generally in the range of 40-60% and preferably 45-55%. The product is also normally 7-10 wt% in Al₂O₃. The starting materials Basically, two starting materials are required to perform the novel process of the present invention. First, aluminum sulphate (Alum) must be employed. Aluminum sulphate has the following formula: Al₂(SO₄)₃. The second starting material is a source of a suitable alkali metal aluminate. Although sodium aluminate is the prefered starting material, other suitable alkali metal aluminates may also be contemplated. Water is also necessary since the reaction will be performed in an aqueous medium. The process The process for preparing poly aluminum sulphate in the context of the present invention involves a unique procedure in which aluminum sulphate is reacted with an alkali metal aluminate under "high shear" mixing. High shear mixing conditions are well known in the art. The fundamental definition of fluid shear rate is the velocity gradient, dv/dy which has units of reciprocal time (ft/(sec)(ft) = sec⁻¹). See J.Y. Oldshue, Fluid Mixing Technology, pub. McGraw-Hill, Publications Co., page 24 (1983). Standard high shear mixing conditions may be obtained using a Waring blender which achieves a velocity gradient exceeding 1000 sec⁻¹. (See, for example, T.R. Camp, Floc Volume Concentration, Jour. AWWA, 68:656-673 (1968)). Mixing conditions characterized by a velocity gradient exceeding 1000 sec⁻¹ are, therefore, known in the art as high shear mixing conditions. While velocity gradients as low as 1000 sec⁻¹ may be used at lower than ambient temperatures, it is preferred to use velocity gradients of 3000 sec⁻¹ or higher, because at these velocities it is easier to maintain the speed of the mixer or homogenizer. It has been found that the high shear mixing is an essential part of the process. While not wishing to be bound by any particular theory, it is proposed that high shear mixing provides two important functions. First, it gives instantaneous high dilution of the reactants, especially the alkali metal aluminate solution, as it is injected into the other reactants. This is required to avoid local excess concentrations of the alkali aluminate, since even small local excess concentrations relative to the aluminum will result in the formation and appearance of solid gel particles. Second, the high shear mixing provides the forces needed to disintegrate any small particles of gel into a highly dispersed, and non agglomerated form. In practice, the high shear mixing is preferably sufficient to produce a reactive gel and to produce a substantially transparent basic poly aluminium sulphate solution. Generally speaking, reacting aluminum sulphate solution contains the equivalent of 3.8-8.5 wt.% Al₂O₃ and the reacting alkali metal aluminate solution contains the equivalent of 5.6 - 16 wt.% in Al₂O₃. During the reaction step, the pH of the resulting reaction mixture is maintained between 2.0 and 4.3 (more preferably 2.0 and 3.8). Preferably, from 5600 to 8800 (preferably 5666 to 8719) parts of aluminum sulphate solution containing the equivalent of 8.3 wt.% Al₂O₃ is cooled to a temperature that may range between 10 and 35°C. Under "high shear" rate characterized by a velocity gradient exceeding 1000 sec⁻¹, is then added from 600 to 1800 parts (preferably 639 to 1704 parts) alkali metal aluminate solution, containing the equivalent of 24 wt.% Al₂O₃ and 6% free NaOH when the alkali metal aluminate is sodium aluminate, usually contained in at least 300 to 900 (preferably 320 to 843) parts of additional water respectively over a period of time typically ranging from ¼ to 1½ hour. The reaction mixture is preferably maintained at a temperature ranging from 10 to 35°C for a period of time typically ranging from ¼ to 1½ hours after which the reaction temperature is preferably slowly increased to a range that can vary from 50 to 90°C over a period of time typically ranging from ¼ to 2½ hours. This final temperature is then normally maintained for a period of time typically ranging from ½ to 2 hours or until the mixture becomes clear. Once the resulting mixture is clear, it is cooled to room temperature. It is to be noted that for this reaction, the pH of the solution should desirably be maintained between 2.0 and 4.3 (preferably 2.0 to 3.8). Alternatively, the alkali metal aluminate can be added to part of the required amount of aluminum sulphate, thereby producing a pH ranging from 5 to 9 in order to form a neutralized gel and the remaining required amount of aluminum sulphate can then be added to form the final reaction product. If the reaction is performed in this fashion, the pH variations during the process will usually vary from 2.0 to 9.0. As for temperatures and mixing times, the temperature, when alkali metal aluminate is added to the aluminum sulphate, will range between 10 and 35°C and will range from 35 to 90°C after the remaining amount of aluminum sulphate is added to the reaction mixture. Mixing times after addition will typically range from ¼ to 1½ hour for the first half of the reaction and from 1 to 4½ hours for the second half of the reaction. Another alternative reaction sequence consists in adding a part of the total aluminum sulphate to the alkali metal aluminate to form a neutralized gel. This first part of the total amount of aluminum sulphate should be such as to produce a pH ranging between 5 and 9. The remaining amount of total aluminum sulphate is then added to the reaction mixture to form the final product. In this case, the pH of the reaction will vary from 14 to 3.7. As for the temperatures, they will range from 10 to 35°C for the first part of the reaction and from 35 to 90°C for the second part of the reaction. Mixing times will also vary depending on the performed step. In the first part, the mixing time after addition will typically range from ¼ to 1½ hour while it will range from 1 to 4½ hours in the second part. It is to be noted that the process described above may also include the addition of substantial amounts of other cations such as those of iron contained in Alum when it is prepared from bauxite. Other cations, whether introduced unintentionally or otherwise, may include magnesium, calcium, zinc, zirconium and the like. Furthermore, one may also foresee the optional addition of other anions such as phosphates, chlorides, acetates, borates, carbonates or salts of organic or inorganic acids when added to the basic Alum complex. In a preferred embodiment of the present invention, from 1000 to 1600 (preferably 1022 to 1534) parts of sodium aluminate solution containing the equivalent of 24 wt % Al₂O₃ and 6% free NaOH, contained in at least 1200 to 1900 (preferably 1244 to 1867) parts of additional water respectively is added to from 6000 to 7700 (preferably 6154 to 7620) parts of aluminum sulphate solution containing the equivalent of 8.3 wt % Al₂O₃ and which has been previously cooled to a temperature ranging from 10 to 20°C. It is to be mentioned that sodium aluminate is to be added slowly on a period of time ranging from ½ to 3/4 hour under high shear mixing. The resulting mixture is held at a temperature ranging from 10 to 20°C for a period of time ranging from ½ to 3/4 hour after which the temperature is slowly increased to 20 to 70°C over a period of time ranging from 1 to 2 hours. The mixture is held at this final temperature for 3/4 to 1½ hour or until the mixture becomes clear. The resulting mixture is then cooled and ready to use. The equations describing the reaction for the preparation of poly aluminum sulphate when using aluminum sulphate and sodium aluminate are supposed to be as follows for the preparation of a 50% basic polyaluminum sulphate solution: I 3Na₂Al₂O₄ + Al₂(SO₄)₃ + 12 H₂O → 8 Al(OH)₃ + 3 Na₂SO₄ II 8Al(OH)₃ + 4 Al₂(SO₄)₃ → 4Al₄(OH)₆(SO₄)₃ therefore the overall reaction is supposed to be III 3Na₂Al₂O₄ + 5Al₂(SO₄)₃ + 12H₂O → 4Al₄(OH)₆(SO₄)₃ + 3Na₂(SO₄) Thus, by using simultaneously acid and alkali aluminum salts, the product:by-product ratio obtained is substantially higher than any ratio obtained with previously known methods. Only three moles of sodium sulphate per 4 moles of final product is obtained with the method of the present invention. One must appreciate that the important feature of the present invention is the use of high shear mixers (homogenizers) which enable the formation of the reactive Al(OH)₃ gel at a high solids content. This yields a final transparent liquid product having an equivalent concentration of Al₂O₃ ranging from 7 to 10% obtained from a unique one step procedure. The following Examples are introduced to illustrate rather than limit the scope of the present invention. The concentrations given in the examples are those of the usually available commercially sold preparations of these chemicals. It should be understood, however, that other concentrations can be successfully used, by making the necessary adjustments to the amount of water used in making the dilutions. Example 1 Preparation of polymeric basic aluminum sulphate. 700 parts of aluminum sulphate solution (28% Al₂(SO₄)₃) was added to a jacketed 1 L.flask. The mixture was cooled to 15°C and under high shear mixing, 129 parts liquid sodium aluminate (containing the equivalent of 24.0 wt.% Al₂O₃) contained in 157 parts of additional water were slowly added over one half hour. The aluminum hydroxide gel mixture was held at 10-15°C for one half hour at which time the temperature was slowly increased to 65°C over two hours. It was held for one and a half hour at 65°C until the mixture became clear and was then cooled. The product obtained contained the equivalent of 9.2% Al₂O₃ (a partial increase over theoretical due to evaporation loss) and had basicity of 50%. Example 2 Preparation of polymeric basic aluminum sulphate. 284 parts water were added to 244 parts of aluminum sulphate solution and cooled to 15°C, liquid sodium aluminate (containing the equivalent of 24 wt% Al₂O₃) 135 parts diluted with 143 parts water was then added over one half hour to a pH of 6.1. The gel was mixed for one half hour under high shear. Aluminum sulphate solution (456 parts), was then added and the temperature slowly raised over 1½ hour at 58°C and held at 58°C for an additional 1½ hours. Upon clearing the product was cooled and contained the equivalent of 7 wt. % Al₂O₃ (partial increase due to evaporation loss) and a basicity of 51.5%. Example 3 Preparation of polymeric basic aluminum sulphate. To 459 parts water, were added 140 parts sodium aluminate (containing the equivalent of 24.0 wt.% Al₂O₃). Next 255 parts aluminum sulphate solution were added under high mixing at 20°C over ½ hour. The pH was 5.6 and after 3/4 hour of mixing 445 parts of aluminum sulphate solution were added, and the temperature was kept at 20°C for an additional 1½ hour. It was then increased to 58°C over 1¼ hour and held for ½ hour at which time the mixture became totally clear. The product was cooled and showed a basicity of 52.7% and contained the equivalent of 7.3 wt.% Al₂O₃. Example 4 Comparison tests involving aluminum sulphate and poly aluminum sulphate (PAS) prepared in accordance with the present invention. Tests were carried out using aluminum sulphate or poly aluminum sulphate (PAS) having a basicity of approximately 50% using water taken from the St. Lawrence River, the treatment being performed at 25°C and 8°C. The tests were carried out using aluminum sulphate as a reference and both tests used an equivalent Al₂O₃ concentration of 6.9 mg/L. Results are shown in Tables I and II for tests conducted at 8 and 25°C respectively. It is to be noted that in 8°C water, the residual turbidity obtained with poly aluminum sulphate (PAS) prepared in accordance with the present invention is 0.32 NTU while the residual turbidity obtained with aluminum sulphate was 0.56 NTU. Furthermore, the rate of floc development was faster and the floc larger for the poly aluminum sulphate prepared in accordance with the process of the present invention. Finally, in all cases, the alkalinity of the treated water is higher when poly aluminum sulphate (PAS) is used relative to aluminum sulphate. It is also to be noted that at 25°C, even though comparable results are obtained for both products, such warm waters are not frequently treated.

Claims: A process for the preparation of a basic poly aluminum sulphate solution product having the following formula: [Al A (OH) B (SO₄) C (H₂O) E ] n in which n is a positive integer; A is 1.0; B ranges from 0.75 - 2.0; C ranges from 0.5 - 1.12; and E is larger than 4, wherein the basicity of said basic poly aluminum sulphate solution is defined as B/3A X 100 and said basicity is 25-66% and wherein B + 2C = 3 , characterized in that said process comprises the step of reacting in a one step process an aluminum sulphate solution with an alkali metal aluminate solution under high shear mixing conditions producing a velocity gradient exceeding 1000 sec⁻¹ sufficient to produce a reactive Al(OH)₃ gel and to produce a substantially transparent basic poly aluminum sulphate solution and recovering the desired product. A process according to claim 1, characterized in that the alkali aluminate is sodium aluminate. A process according to claim 1 or claim 2, characterized in that said aluminum sulphate solution is reacted with the alkali metal aluminate at a temperature ranging between 10 and 35°C and is subsequently heated at a temperature ranging from 50 to 90°C. A process according to claim 1, claim 2 or claim 3, characterized in that said basic poly aluminum sulphate solution contains additional multivalent cations. A process according to claim 4, characterized in that said multivalent cations are selected from the group consisting of iron, magnesium, calcium, zinc and zirconium. A process according to any preceding claim, characterized in that said basic poly aluminum sulphate solution contains additional anions selected from the group consisting of salts of organic and inorganic acids, such that the ratio C/A is greater than 0.5, but less than 1.12. A process according to claim 6, characterized in that said anions are selected from the group consisting of phosphate, acetate, borate, chloride and carbonate anions. A process according to claim 2, characterized in that said basicity is from 40-60% and the pH of said reaction mixture is maintained between 2.0 and 4.3. A process according to claim 2, characterized in that said basicity is 45-55%. A process according to any preceding claim, characterized in that said aluminum sulphate solution and said alkali aluminate solution are initially mixed under high shear mixing. A process according to any preceding claim, characterized in that said aluminum sulphate solution contains the equivalent of 3.8 to 8.5 wt.% Al₂O₃. A process according to any preceding claim, characterized in that said alkali metal aluminate solution contains the equivalent of 5.6 to 16 wt.% Al₂O₃. A process according to any preceding claim, characterized in that during said reacting step, the pH of the resulting reaction mixture is maintained between 2.0 and 4.3. A process according to claim 2, characterized in that from 5600 to 8800 parts by weight of said aluminum sulphate solution having a concentration in aluminum sulphate equivalent to 8.3 wt.% Al₂O₃ is reacted with from 600 to 1800 parts by weight of said sodium aluminate solution having a concentration equivalent to about 24 wt.% in Al₂O₃ and about 6% free NaOH contained in from 300 to 900 parts by weight water. A process according to claim 2, characterized in that from 6100 to 7700 parts by weight of said aluminum sulphate solution having a concentration in aluminum sulphate equivalent to about 8.3 wt.% Al₂O₃ is reacted with 1000 to 1600 parts by weight of said sodium aluminate solution having a concentration equivalent to about 24 wt.% Al₂O₃ and about 6 wt.% free NaOH contained in from 1200 to 1900 parts of water, wherein the basicity of said basic poly aluminum sulphate solution is between 40-60%. A process according to any preceding claim, characterized in that said basic poly aluminum sulphate solution contains the equivalent of 7-10 wt.% Al₂0₃.

Inventors: HAASE, DIETER, SPIRATOS, NELU
Applicants: HANDY CHEMICALS LIMITED
Application year: 1989
Main classification: C01F7
IPC codes: C01F7, B01D21, C02F1