Water-insoluble black pigment

Abstract: A water-insoluble black pigment produced by reacting C. I. Solubilized Sulphur Black 1 with a salt-forming agent selected from the group consisting of inorganic acid salts of alkylamine, alkoxyalkylamine, alkanolamine, carboxyalkylamine, alkylcarboxamide, allylamine, amide of unsaturated carboxylic acid, cyclic amine, cycloalkylamine, oxacycloalkylamine, morpholine derivative, arylamine, aralkylamine, pyridine derivative, quinoline, phthalimide, DL-α-amino-ε-caprolactam and ε-aminocaprolactam, and ammonium salt of the formula (1): wherein A₁, A₂, A₃ and A₄ each represent an alkyl or phenyl group and X⁻ represents an anionic group. The water-insoluble black pigment is usable as a colorant for printing ink, ink for jet printers, dot printer ribbon, and melt-transfer type printer, a charge-regulator for toner used on electrostatic recording system, a laser marking agent, a colorant for resin, an infrared absorber and the like.

Description: Background of the Invention : The present invention relates to water-insoluble black pigments. In particular, the present invention relates to water-insoluble black pigments produced from a specified water-soluble sulfide dyestuff and amines. Black pigments are used in quantities in various industrial fields. For example, they are used as a colorant for paint, printing ink, ink for recording materials such as ribbon for dot printers, melt transfer ink or ink for ink-jet printers, a colorant for a toner for electrostatic photography, an infrared absorber, a laser-marking agent and a charge regulator. The black pigments include inorganic and organic pigments such as carbon black, Nigrosine dyestuffs, metal complex dyestuffs and the like. Among them, carbon black is insoluble in ordinary organic solvents and it, therefore, is usually used in a dispersion state. Carbon black is quite liable to cause aggregation in dispersion state and various contrivances for maintaining the state of dispersion over a long period of time must be carried out. Thus the cost on using carbon black as a black pigment must be inevitably high. Nigrosine dyestuffs are used in limited fields, since they are soluble in only some solvents and are scarcely dispersible in resins and their fastnesses to light are not enough high. In mutagenicity tests (Ames tests), Nigrosine dyestuffs give positive results in most cases. Metal complex dyestuffs have some problems that a pure black hue can scarcely be obtained on metal complex dyestuffs and that negative results are scarcely obtained in mutagenicity tests. Thus, the development of a water-insoluble black pigment having high solubility in ordinary solvents and excellent compatibility with a resin, and exhibiting negative results in mutagenicity tests is demanded. After intensive investigations made for the purpose of solving the above-described problems, the inventors have completed the present invention. Summary of the Invention: The present invention provides water-insoluble black pigments produced by reacting C.I. Solubilized Sulphur Black 1 with a salt-forming agent selected from the group consisting of inorganic acid salts of alkylamine, alkoxyalkylamine, alkanolamine, carboxyalkylamine, alkylcarboxyamide, allylamine, amide of unsaturated carboxylic acid, cyclic amine, cycloalkylamine, oxacycloalkylamine, morpholine derivative, arylamine, aralkylamine, pyridine derivative, quinoline, phthalimide, DL-α-amino-ε-caprolactam and ε-aminocaprolactam, and ammonium salt of the formula (1) (hereinafter referred to as a salt-forming agent): wherein A₁, A₂, A₃ and A₄ each represent an alkyl or phenyl group and X⁻ represents an anionic group. Brief Explanation of the Drawings: Fig. 1 shows an infrared absorption spectrum of the water-insoluble black pigment obtained in Example 4. The ordinate is percent transmittance. Detailed Description of the Invention: Now the detailed description will be made on the water-insoluble black pigments of the present invention. C. I. Solubilized Sulphur Black 1 used as the starting material in the present invention is produced by reducing C. I. Sulphur Black 1 with, for example, a hydrogensulfite such as sodium or potassium hydrogensulfite into a thiosulfonate. Supposedly it has the following structure: wherein ℓ and m each represent an integer of 1 to 5. C. I. Solubilized Sulphur Black is registered as C. I. structural formula No. 53186 on "Color Index" and put on the market under various trade names. C. I. Sulphur Black 1 is shown by the following formula and is registered as C. I. structural formula No. 53185 on "Color Index": wherein n represents an integer of 2 to 10. C. I. Solubilized Sulphur Black 1 can be produced by, for example, the following process. A mixture of water and 2,4-dinitrochlorobenzene is heated to boil. An aqueous sodium hydroxide solution is added dropwise thereto and the mixture is stirred under heating to boil for 1 h to form 2,4-dinitrophenol. Then sodium polysulfide is added dropwise thereto over a period of 3 to 4 h while maintaining a boiling state to promote vulcanization for 24 h under exiling water. In the course of the reaction, the reaction temperature is elevated from 106°C to 120°C. Then, water in a quantity equal to that of the reaction liquid is added thereto and air is bubbled thereinto for about 10 h to oxidize the product and form crystals. The pH of the reaction mixture is adjusted to 9.2 to 9.5 and the reaction mixture is filtered to obtain a pressed cake of C. I. Sulphur Black 1. Water and sodium hydrogensulfite are added to the obtained pressed cake of C. I. Sulphur Black 1 and the mixture thus-obtained is treated at 80°C for 2 h. After adjusting the pH, the reaction mixture is filtered to obtain a pressed cake of C. I. Solubilized Sulphur Black 1 and the press cake is dried to form dried C. I. Solubilized Sulphur Black 1. [As for the process for producing C. I. Sulphur Black 1, refer to "Senryo Kagaku (Dye Chemistry)" by Yutaka Hosoda, published by Gihodo, page 775 and "Ryuka Senryo to Sono Chukantai (Sulfur Dyes and Their Intermediates)" by Hachiro Hiyama, page 147]. Among the alkylamines, alkoxyalkylamines, alkanolamines, carboxyalkylamines, alkylcarboxamides, allylamines, amides of unsaturated carboxylic acid, cyclic amines, cycloalkylamines, oxacycloalkylamines, morpholine derivatives, arylamines, aralkylamine, pyridine derivatives, quinoline, phthalimide, DL-α-amino-ε-caprolactam, ε-aminocaprolactam and ammonium salts of the above formula (1), examples of the alkylamines, alkoxyalkylamines, alkanolamines, carboxyalkylamines, alkylcarboxamides, allylamines, amides of unsaturated carboxylic acid, cyclic amines, cycloalkylamines, oxacycloalkylamines, morpholine derivatives, arylamines, aralkylamines, pyridine derivatives and ammonium salts of the formula (1) include the following compounds. Alkylamines such as H₂NCH₃, H₂NC₂H₅, H₂NCH₂CH₂CH₃, H₂N-CH(CH₃)₂, H₂NCH₂CH₂CH₂CH₃, H₂N-CH(CH₃)CH₂CH₃, H₂N-C(CH₃)₂CH₃, H₂N(CH₂)₁₁CH₃, N₂NC₁₈H₃₇, CH₃NHC₆H₁₃, CH₃CH₂CH(CH₃)NH₂, (CH₃)₃CNH₂, C₄H₉CH(C₂H₅)CH₂NH₂, (CH₃)₂CHCH(CH₃)NH₂, C₆H₁₃NH₂, (CH₃)₂CHCH(CH₃)NH₂, [C₄H₉CH(C₂H₅)CH₂]₂NH, (C₂H₅)₂NH, [(CH₃)₂CHCH₂]₂NH, (C₈H₁₇)₂NH, (C₈H₁₇)₂NCH₃, (C₃H₇)₂NH, (C₄H₉)₂NH, [(CH₃)₂CHCH₂]₂NH, C₄H₉CH(C₂H₅)CH₂N(C₄H₉)₂, (CH₃)₂CHCH(CH₃)NHC₂H₅, (C₂H₅)₃N, (C₃H₇)₃N, (C₄H₉)₃N, [(CH₃)₂CHCH₂]₃N, (C₈H₁₇)₃N and [C₄H₉CH(C₂H₅)CH₂]₃N. Alkoxyalkylamines such as CH₃OCH₂CH₂CH₂NH₂, C₉H₁₉OCH₂CH₂CH₂NH₂, C₄H₉CH(C₂H₅)CH₂OCH₂CH₂CH₂NH₂, C₂H₅OCH₂CH₂CH₂NH₂, C₃H₇OCH₂CH₂CH₂NH₂, (CH₃)₂CHOCH₂CH₂CH₂NH₂, C₄H₉OCH₂CH₂CH₂NH₂, (CH₃)₂CHCH₂OCH₂CH₂CH₂NH₂, C₄H₉CH(C₂H₅)CH₂OCH₂CH₂CH₂NH₂, C₁₀H₂₁OCH₂CH₂CH₂NH₂, C₁₂H₂₅OCH₂CH₂CH₂NH₂ and C₁₄H₂₉OCH₂CH₂CH₂NH₂. Alkanolamines such as NH₂C₂H₄OH, NH(C₂H₄OH)₂, N(C₂H₄OH)₃, H₂NCH₂CH(CH₃)OH, C₂H₅HN-C₂H₄OH, (C₂H₅)₂N-C₂H₄OH, HOCH₂NHCH₂CH₂OH, HOCH₂CH₂CH₂NH₂, HOCH₂CH₂CH₂N(CH₃)₂, (CH₃)₂CHCH₂N(CH₂CH₂OH) and CH₃CH(NH₂)CH₂OH. Carboxyalkylamines such as H₂N-CH₂COOH, H₂N-(CH₃)CHCOOH, HOOCCH(NH₂)CH₂CH₂COOH and H₂N(CH₂)₁₁COOH. Alkylcarboxamides such as C₂H₅CONH₂. Allylamines such as CH₂=CHCH₂NH₂, (CH₂=CHCH₂)₂NH, (CH₂=CHCH₂)₃N, CH₂=CHCH₂N(CH₃)₂ and CH₃N(CH₂CH=CH₂)₂. Amides of unsaturated carboxylic acid such as CH₂=CHCONH₂. Cyclic amines such as Cycloalkylamines such as cyclohexylamine and dicyclohexylamine. Oxacycloalkylamines such as Morpholine derivatives such as Arylamines such as Aralkylamines such as Pyridine derivatives such as Quaternary ammonium salts such as These compound can be used in an admixture of two or three compounds. The water-insoluble black pigments of the present invention are produced, for example, as follows: when a free amine is used, it is firstly reacted with a mineral acid such as hydrochloric acid, sulfuric acid and nitric acid in water to form the mineral acid salt thereof (salt-forming agent).Then an aqueous solution of the mineral acid salt thus produced is added to an aqueous solution of C. I. Solubilized Sulphur Black 1 under stirring. C. I. Solubilized Sulphur Black 1 forms a water-insoluble salt in the form of crystals, which are separated by filtration. The intended water-insoluble black pigments can be thus obtained. The molar ratio of C. I. Solubilized Sulphur Black 1 to a mineral acid salt of an amine in the salt forming reaction may be 1:2. Since, however, the molecular weight of C. I. Solubilized Sulphur Black 1 is not always constant, the liquid mixture of them is subjected to a spot test on filter paper and the salt forming reaction can be regarded as being completed when black liquid containing C. I. Solubilized Sulphur Black no more exudes on the spot test. Although an aqueous solution of C. I. Solubilized Sulphur Black 1 can be added to an aqueous solution of a mineral acid salt of the above-mentioned amine, usually it is preferred to add a necessary amount of an aqueous solution of a mineral acid salt of the above-mentioned amine to an aqueous solution of C. I. Solubilized Sulphur Black 1 under stirring under conducting the above-mentioned spot test at times. Although the concentrations of aqueous solutions of C. I. Solubilized Sulphur Black 1 and a mineral acid salt of the amine are not particularly limited, a concentration of each of 5 to 30 wt. % by weight is preferred from the viewpoint of workability. They are prepared at a temperature as high as, for example, 70 to 100°C. Although a salt-forming reaction between a salt-forming agent selected from the consisting of mineral acid salts of the amines and the ammonium salts of the formula (I) and C.I. Solubilized Sulphur Black 1 can satisfactorily proceed at an ambient temperature (10 to 30°C), the temperature is not particularly limited. When a quaternary ammonium salt is used as the salt forming agent, the step of forming the mineral acid salt is unnecessary. An aqueous solution containing a quaternary ammonium salt is produced and added to the aqueous solution of C. I. Solubilized Sulphur Black 1 in the same manner as that described above to conduct a salt forming reaction to thereby give an intended product. The water-insoluble black pigments produced according to the present invention may be dried, if desired, to form a dry product or they may be in the form of wet cake. They are used for various purposes in either dry or wet state. The water-insoluble black pigments produced in the present invention have pure black hue and excellent fastness to sunlight, high solubility in a solvent, high solubility or dispersibility in a resin and high absorbancy to near-infrared ray. Since these pigments contain no heavy metals, they do not pollute the environment and exhibit negative results in mutagenicity tests. The water-insoluble black pigments of the present invention are usable for various purposes. Namely, they are usable as colorants for printing inks, inks for ink jet printers, inks for dot printer ribbons, inks for melt transfer printing, inks for infrared OCR, colorants or charge-regulators for toners for electrostatic recording, laser marking agents, colorants for resins and infrared absorbers. For example, ink for melt transfer printing is prepared by dissolving a black pigment of the present invention and a wax having a low melting point such as a fatty acid amide in a solvent such as acetone. The ink thus prepared is applied to, for example, a polyester sheet and the sheet is heated to vaporize the solvent such as acetone, thus forming an ink layer. Thus a heat melt transfer sheet usable for the thermal transfer printing onto PPC paper or the like by printing with a thermal printing head or the like is prepared. A water-insoluble black pigment of the present invention is mixed by grinding with epoxy resin, bromoepoxy resin, phenolic novolac, 2-methylimidazole (hardener), flame retardant, releasing agent, silane coupling agent and silica powder with a mixing roll heated at 80°C for 10 min to form a sheet. The sheet is cooled and pulverized to give a resin molding powder. A lead frame provided with semiconductor elements is sealed with the resin molding powder thus obtained by means of a transfer press to form a satin-finished resin-sealed semiconductor device having a surface roughness of 12 µ (the molding conditions include a temperature of 175°C, a time of 2 min, a transfer pressure of 90 kg/cm² and postcure temperature and time of 175°C and 10 h, respectively). The obtained resin-sealed semi-conductor device is irradiated with carbon dioxide laser through a given mask to mark the surface of the semiconductor device. Thus a quite clear-marked device can be obtained. An ink-ribbon containing a water-insoluble black pigment of the present invention is prepared according to a usual method, as follows. A water-insoluble black pigment of the present invention is added to a vehicle prepared from mineral oil, vegetable oil, surface-active agent and etc. to obtain a mixture thereof and the mixture thus-obtained is fully mixed with a kneader or a mill having some rolls to obtain an ink-compound. The ink-compound is coated with a roll-coater on Nylon-cloth. After drying in hot-temperatured atmosphere, an ink-ribbon containing a present water-insoluble black pigment is obtained. In these usages of the present water-insoluble black pigments, these black pigments may be used in admixture of two or more black pigments. Examples The following Examples will further illustrate the present invention. In the Examples, parts and percentages are given by weight and D⁻² represents the following structure of C. I. Solubilized Sulphur Black 1: wherein ℓ and m each represent an integer of 1 to 5. Example 1 50 parts of C. I. Solubilized Sulphur Black 1 (Kayasol Black B; a product of Nippon Kayaku Co., Ltd.) were dissolved in 500 parts of boiling water. A solution of 100 parts of a quaternary ammonium salt (Kohtamin 86 P Conc; a product of Kao Corporation) of the following formula in 500 parts of water was slowly added thereto under stirring: A crystallization began immediately. After the completion of the addition of the aqueous ammonium salt solution, a spot test was conducted. Coloration was scarcely observed in the exudate. The crystal thus formed was separated by filtration, washed with water and dried to give a water-insoluble black pigment of the following formula: [D]⁻²·2[(CH₃(CH₂)₁₆CH₂N(CH₃)₃]⁺ It had λ max s of 606 nm in DMF and 631 nm in N-methylpyrrolidon. Example 2 50 parts of C. I. Solubilized Sulphur Black 1 (Kayasol Black B) were dissolved in 500 parts of boiling water. A solution of 100 parts of a quaternary ammonium salt (Kohtamin D-86 P Conc; a product of Kao Corporation) of the following formula in 500 parts of water was added dropwise thereto: A crystallization began immediately. After the completion of the addition of the aqueous ammonium salt solution, a spot test was conducted. Coloration was scarcely observed in the exudate. The crystal thus formed was separated by filtration, washed with water and dried to give a water-insoluble pigment of the following formula: [D]⁻²·2[(CH₃(CH₂)₁₆CH₂)₂N(CH₃)₂]⁺ It had λ max s of 580 nm in xylene and 632 nm in N-methylpyrrolidon. Example 3 A water-insoluble black pigment of the following formula: [D]⁻²·2[CH₃(CH₂)₁₀CH₂-N(CH₃)₃]⁺ was produced from a quaternary ammonium salt (Kohtamin 24 P Conc; a product of Kao Corporation) of the following formula: [CH₃(CH₂)₁₀CH₂N(CH₃)₃]⁺Cℓ⁻ and C. I. Solubilized Sulphur Black 1. It had λ max s of 609 nm in DMF and 628 nm in N-methylpyrrolidon. Example 4 100 parts of triethanolamine were dissolved in 500 parts of water. 100 parts of concentrated hydrochloric acid were added to the solution to give a triethanolamine hydrochloride solution. This solution was added dropwise to a solution of 50 parts of C. I. Solubilized Sulphur Black 1 in 500 parts of boiling water under stirring. A crystallization began immediately. The crystal thus formed was separated by filtration, washed with water and dried to give a water-insoluble black pigment of the following formula: [D]⁻²·2[HN(C₂H₄OH)₃]⁺ Fig. 1 shows an infrared absorption curve of this product. Example 5 100 parts of p-dodecylaniline were added to 500 parts of water. 100 parts of concentrated hydrochloric acid were added to the solution to give p-dodecylaniline hydrochloride solution. The solution was slowly added to a solution of 50 parts of C. I. Solubilized Sulphur Black 1 in 500 parts of boiling water under stirring. A crystallization began immediately. After the completion of the addition of the p-dodecylaniline hydrochloride solution, a spot test was conducted. No coloration was observed in the exudate. The crystal thus formed was separated by filtration, washed with water and dried to give a water-insoluble black pigment of the following formula: It had λ max of 569 nm in N-methylpyrrolidon. Example 6 100 parts of an alkoxyalkylamine of the formula C₄H₉(CH(C₂H₅)CH₂OC₃H₆NH₂ were added to 500 parts of water and then 100 parts of concentrated hydrochloric acid were added thereto to give a solution of the amine hydrochloride. The solution was added to a solution of 50 parts of C. I. Solubilized Sulphur Black 1 in 500 parts of boiling water. A crystallization began as soon as the addition of the hydrochloride solution was begun. After the completion of the addition, a spot test was conducted. No coloration was observed in the exudate. The crystal thus formed was separated by filtration, washed with water and dried to give a water-insoluble black pigment of the following formula: [D]⁻²·2[C₄H₉CH(C₂H₅)CH₂OC₃H₆NH₃]⁺ It had λ max of 625 nm in N-methylpyrrolidon. The black pigment thus obtained was subjected to the Ames tests using Salmonella typhimurium TA 100 and TA 98. No increase in the number of revertant colonies was observed as compared with the solvent control (blank :DMSO) Examples 7 to 19 Water-insoluble black pigments were produced in a similar manner as that of Example 6 by using amines shown in the following table: Example No. Amine used Example 7 H₂NCH₃ Example 8 H₂NCH₂CH₂CH₃ Example 9 H₂N(CH₂)₁₁CH₃ Example 10 H₂NC₁₈H₃₇ Example 11 H₂NC₂H₄OH Example 12 HN(C₂H₄OH)₂ Example 13 CH₃OCH₂CH₂CH₂NH₂ Example 14 C₉H₁₉OCH₂CH₂CH₂NH₂ Example 15 Morpholine Example 16 Aniline Example 17 H₂NCOOC₂H₅ Example 18 Acrylamide polymer (MW:700,000 to 1,000,000) Example 19 DL-α-amino-ε-caprolactam Application Example 1 A solution of a polyamide resin in toluene was applied to a capacitor paper having the thickness of 10 µm with a bar coater to form a layer having a thickness of 6 µm, which was then dried to form an intermediate adhesive layer. Separately, 2 parts of the water-insoluble black pigment produced in Example 6, 2 parts of a fatty acid amide as the melting point depressant, 0.8 part of carbon black having a surface coated with a vinyl chloride/vinyl acetate copolymer and 25 parts of acetone were kneaded together by means of a ball mill for 24 h to give a dispersion, which was applied on the intermediate adhesive layer, followed by evaporation of acetone to thereby form an ink layer having a thickness of 20 µm. The black pigment was quite compatible with the fatty acid amide and the vinyl chloride/vinyl acetate copolymer. The ink sheet thus prepared was used for the transfer recording onto PPC paper with a thermal facsimile terminal. The conditions were: 0.4 W for each dot of the printing head, print heating time of 4 ms and, therefore, printing energy density of 40 mj/mm². The recording was conducted repeatedly with the facsimile terminal using the same portion of the ink sheet while the recording paper was moved to have a new line each time under the above-described conditions. A print of a high density could be obtained. Even after repeating the printing 10 times, a sufficiently readable, clear print could be obtained. Even when the pattern of the characters was changed during the printing, the density of the transferred print was even. In the microscopic observation of the surface of the ink layer, it was found that the surface was flat and smooth. Even when the surface of the record was rubbed with fingers, the fingers were not stained and no dragging mark of the transferred image was observed. Application Example 2 Epoxy resin (epoxy equivalent: 214, softening point: 70°C) 16.0 parts brominated epoxy resin (epoxy equivalent: 274, softening point: 84°C) 2.5 phenolic novolac resin (epoxy equivalent: 105, softening point: 75°C) 8.0 hardening agent (2-methylimidazole) 0.4 flame retardent (antimony trioxide) 1.8 releasing agent (carnauba wax) 0.5 silane coupling agent (A-187; a product of Nippon Unicar Co.) 0.5 water-insoluble black pigment produced in Example 4 0.3 silica powder (inorganic filler) 70.0 Total: 100.0 parts A molding epoxy resin composition comprising the components shown above was prepared as follows: the flame retardant and the inorganic filler were treated with the silane coupling agent. The other components were added thereto, pulverized and mixed together. The mixture was treated with a mixing roll heated at 80°C for 10 min to form a sheet, which was cooled and pulverized to form a resin powder. A lead frame provided with semiconductor elements was sealed with the molding powder by means of a transfer press to form a satin-finished resin-sealed semiconductor device having a surface roughness of 20 µ (the molding conditions included a temperature of 175°C, a time of 2 h, a transfer pressure of 90 kg/cm² and postcure temperature and time of 175°C, and 10 h, respectively). The obtained resin-sealed semiconductor device was irradiated with a carbon dioxide gas laser (902 Laser Mark of Shibuya Koei Co., Ltd. having a maximum energy density of 0.4 Joule/cm²) through a given mask for 1/1,000,000 sec to mark the surface of the semiconductor. Thus a quite clear marking was obtained. It was thus confirmed that the water-insoluble black pigment produced in Example 4 served as an excellent laser marking agent. Application Example 3 25 parts of mineral oil, 25 parts of vegetable oil, 35 parts of sorbitan fatty acid ester and 10 parts of the water-insoluble black pigment produced in Example 6 were mixed by means of a mill having three rolls for 10 minutes to obtain an ink compound. Then the ink compound was coated with a roll-coater on Nylon-cloth to obtain a ink-ribbon suitable for an impact-type printer. The ink-ribbon thus prepared was set on an impact-type printer. The printer was operated for 1,000 hours (printing test) and gave printed letters having high depth of black-shade and good luster. Degree of abrasion of wire-pins equipped on the printer was very low level. On the other hand printing test using an ink-ribbon prepared from 25 parts of mineral oil, 25 parts of vegetable oil, 35 parts of sorbitan fatty acid ester and 10 parts of carbon black in the similar method above-mentioned was carried out and printed letters having lower depth of black-shade and worse luster were obtained. Degree of abrasion of wire-pins on this printing test is more high level.

Claims: A water-insoluble black pigment obtainable by reacting C. I. Solubilized Sulphur Black 1 with a salt-forming agent selected from the group consisting of inorganic acid salts of alkylamine, alkoxyalkylamine, alkanolamine, carboxyalkylamine, alkylcarboxamide, allylamine, amide of unsaturated carboxylic acid, cyclic amine, cycloalkylamine, oxacycloalkylamine, morpholine derivative, arylamine, aralkylamine, pyridine derivative, quinoline, phthalimide, DL-α-amino-ε-caprolactam and ε-aminocaprolactam, and ammonium salt of the formula (1): wherein A₁, A₂, A₃ and A₄ each represent an alkyl or phenyl group and X⁻ represents an anionic group. A water-insoluble black pigment according to Claim 1, wherein the salt-forming agent is an inorganic acid salt of an alkoxyalkylamine. A water-insoluble black pigment according to Claim 2, wherein the alkoxyalkylamine is represented by the formula: C₄H₉CH(C₂H₅)CH₂OC₃H₆NH₂ A water-insoluble black pigment according to Claim 1, wherein the salt-forming agent is an inorganic acid salt of an alkylamine. A water-insoluble black pigment according to Claim 1, wherein the salt-forming agent is ammonium salt represented by the formula: [(CH₃(CH₂)₁₆CH₂)₂N(CH₃)₂]⁺ Cℓ⁻ A water-insoluble black pigment according to Claim 1, wherein the salt-forming agent is ammonium salt represented by the formula: [CH₃(CH₂)₁₀CH₂N(CH₃)₃]⁺ Cℓ⁻ A water-insoluble black pigment according to Claim 1, wherein a salt-forming agent is ammonium salt represented by the formula: [CH₃(CH₂)₁₆CH₂N(CH₃)₃]⁺ Cℓ⁻

Inventors: ISHIZAKA YUKIO, NAKAMURA KATSUNORI, SOTOGOSHI TERUHITO, ISHIZAKA, YUKIO, NAKAMURA, KATSUNORI, SOTOGOSHI, TERUHITO
Applicants: NIPPON KAYAKU KK, NIPPON KAYAKU KABUSHIKI KAISHA
Application year: 1989
Main classification: C09B49
IPC codes: G03G9, B41M5, C09B69, C09B49