Novel ceramic material, method for the preparation thereof and ceramic shaped body obtained therefrom

Abstract: A novel ceramic material affording a ceramic molded bodies having a high toughness and a high tensile strength is disclosed which comprises a smectite clay mineral having at least a portion of ion-exchangeable cations thereof ion-­ exchanged with bismuth ions. The ceramic material is prepared by treating a smectite clay mineral with an aqueous solution containing bismuth ions to ion-exchange at least a portion of ion-exchangeable cations thereof with bismuth ions.

Description: This invention relates to ceramic shaped bodies having a high toughness and a high tensile strength and to a ceramic shaped body obtained therefrom, and to a process of preparing such a ceramic body. It is known that a ceramic shaped body can be formed from a smectite clay mineral such as montmorillonite, biderite, saponite through a series of treatments involving kneading the clay with water, shaping the kneaded clay into a desired form, drying and calcining the shaped green body at a high temperature. The ceramic shaped body thus obtained, however, has a problem because it is low in impact and toughness. Recently, there has been developed a new type of ceramic body generally called a high strength ceramic and obtained by a method including blending a super fine particulate material such as of alumina with various additives such as sintering aids and binders, and molding the blend at a high temperature and a high pressure using a hot press. This technique, however, has a problem because it is very difficult to obtain ceramic shaped bodies with complicated structures. A paper by Yamanaka et al in Clays & Clay Minerals, Vol. 28, No. 4, 1980, pages 281-284 describes an experiment in which interlayer sodium ions of montmorillonite were exchanged with hydroxy-bismuth polycations which were prepared from bismuth perchlorate solutions. However, no utility for the resulting ceramic material is suggested. In accordance with one aspect of the present invention there is provided a shaped ceramic body obtained by shaping a ceramic material comprising a smectite clay mineral having at least a portion of ion-exchangeable cations thereof ion-exchanged with bismuth ions, and drying the resultant shaped product. The present invention also provides a process of preparing a shaped ceramic body, comprising the steps of shaping a ceramic material comprising a smectite clay mineral having at least a portion of ion-exchangeable cations thereof ion-exchanged with bismuth ions, and drying the resulting shaped product. Since the ceramic material used according to the present invention is plastic in nature, it can be easily formed into any desired shapes. When the shaped body of the ceramic material is dried, there is obtainable a ceramic shaped body having a high tensile strength and a high toughness. Such a high tensile strength is considered to be attributed to the presence of structural water contained in the clay mineral. Since the structural water is not lost unless the dried, shaped body is heated at a temperature of above about 800°C, the ceramic shaped body exhibits a high tensile strength at a temperature of below about 800°C. When calcined at a temperature higher than 800°C, the tensile strength of the ceramic shaped body tends to decrease but its compression strength becomes improved. The present invention will now be described in more detail below. The ceramic material used according to the present invention comprises a smectite clay mineral having at least a portion of ion-exchangeable cations thereof ion-exchanged with bismuth ions. Any smectite clay mineral, such as a montmorillonite, biderite, saponite or hectorite clay mineral may be used for the purpose of the present invention. A naturally occurring smectite clay mineral or a synthetic clay having a structure similar to smectite may be used. To obtain the ceramic material, the smectite mineral is treated with a bismuth ion-containing aqueous solution so that at least a portion of the ion-exchangeable cations of the clay mineral is ion-exchanged with bismuth ions. The ion-exhange treatment may be effected mixing a raw material clay mineral with an aqueous solution of a bismuth salt. Any water-soluble bismuth salt may be suitably used. Illustrative of suitable bismuth salts are 4BiNO₃(OH)₂·BiO(OH) and bismuth nitrate. The aqueous solution preferably has a bismuth salt concentration of 0.001-0.005 mol/liter, more preferably 0.002-0.004 mol/liter. The bismuth salt is preferably used in an amount of 0.1-0.5 mole, more preferably 0.2-0.4 mole per mole of the smectite clay mineral. The ion-exhange treatment is preferably performed at a temperature of 70-130 °C, more preferably 80-120 °C. After the ion-exchange treatment, the mixture is preferably filtered to remove excess water. The solids are preferably washed with hot water. The thus obtained ceramic material which is plastic in nature can be shaped in any desired forms manually or by means of a suitable shaping machine such as an extruder. By merely drying the shaped body formed of the ceramic material, a ceramic shaped body having a high tensile strength is obtainable. The drying is generally performed at a temperature of 200 °C or below, preferably at a temperature of 50-100 °C. The shaping and drying may be performed simultaneously by means of a hot press or a hot isostatic pressing. The thus obtained ceramic shaped body preferably has a tensile strength of 30-200 kg/cm², more preferably 80-160 kg/cm². If desired, the ceramic shaped body may be further calcined at a temperature of 200-1300 °C for 1-200 hours to improve the compression strength. The ceramic shaped body according to the present invention may be prepared at low cost because the clay mineral and bismuth salts used as the raw material are easily available at cheap cost and because the process for the production thereof is simple and energy saving. The ceramic shaped body may find a variety of industrial applications such as for the fabrication of ceramic molded articles and catalysts. The following examples will further illustrate the present invention. Example 1 Basic bismuth nitrate, 4BiNO₃(OH)₂·BiO(OH) (molecular weight, 1,462) (2.92 grams) was added to 1,000 ml of water, and the mixture was heated in an oil bath (110 - 120°C ) with stirring to dissolve virtually the whole amount of the bismuth salt. After filtration, 4.0 grams of montmorillonite (natural montmorillonite mined at Atarazawa Kozan; molecular weight, ca. 403; true density, 2.61 kg/cm³, when measured with a density measuring instrument manufactured by Toshiba Beckmann) was added to the bismuth-containing aqueous solution and the mixture was heated for about 1 hour with stirring, yielding a pale grayish white precipitate. The precipitate was suction filtered, washed with a hot water, and dried at 80°C. The thus prepared bismuth-containing montmorillonite was aggregated so hard that it was crushed with an agate mortar. Then the crushed material was pulverized with an agate pulverizer of electromagnetic type into super fine powder having a particle size of 26 mesh or finer. A total of six samples of super fine powder (0.9 grams; true density, 3.32 kg/cm³) were molded under a pressure of 400 kg/cm² for 5 minutes into disk-like bodies (diameter D, about 13 mm; thickness W, about 3 mm; bulk density, 2.75 kg/cm³, measured from weight and volume). All of the molded bodies were subjected to a diametral compression test using a universal tensile compression tester. The tensile strength (St) of each of the molded bodies was computed from the applied pressure (F) and a rupture area (D x W) on the basis of the following formula: St = 2F/( π D x W) The ceramic molded bodies of the bismuth-containing montmorillonite prepared by the above procedures were found to have a high a tensile strength of 99.8 kg/cm² as a mean value. Example 2 Four different bismuth-containing montmorillonite ceramic materials were prepared using varying amounts of the bismuth salt added to the montmorillonite (molar ratios of basic bismuth nitrate to montmorillonite being 0.1, 0.2, 0.3 and 0.5), and were then molded under pressure according to the procedures of Example 1. The molded bodies were then tested for tensile strength. As a result, groups of several samples having molar ratios of basic bismuth nitrate to montmorillonite of 0.1, 0.2, 0.3 and 0.5 were found to have tensile strengths of 60.7, 90.6, 81.9 and 71.8 kg/cm², respectively, as mean values. The above results show that the bismuth-containing montmorillonite gives the highest tensile strength when the molar ratio of the basic bismuth nitrate to montmorillonite is about 0.2. Example 3 Two bismuth-containing montmorillonite ceramic materials were prepared with varying amounts of the bismuth salt to the montmorillonite (molar ratios of the basic bismuth nitrate to montmorillonite being 0.1 and 0.2, respectively) and then molded under pressure in accordance with the procedures of Example 1. The molded bodies were calcined at 600 °C for 4 hours and then tested for tensile strength. As a result, the molded bodies formed from the ceramic material with bismuth-to-clay molar ratios of 0.1 and 0.2 were found to have compression strengths of 112.0 and 149.4 kg/cm², respectively as a mean value. Thus, the tensile strength of the ceramic molded bodies was found to increase, rather than deteriorate, by the heat treatment at up to 600 °C. Comparative Example 1 Natural montmorillonite (mined at Atarazawa Kozan; about 1 gram) was molded under a pressure of 400 kg/cm² into 4 samples (bulk density, 2.05 kg/cm³), which were then tested for tensile strength. The tensile strength was found to be 26.4 kg/cm² as a mean value.

Claims: A shaped ceramic body obtained by shaping a ceramic material comprising a smectite clay mineral having at least a portion of ion-exchangeable cations thereof ion-exchanged with bismuth ions, and drying the resultant shaped product. A shaped ceramic body as set forth in Claim 1, wherein the smectite clay mineral is selected from montmorillonite, biderite, saponite and hectorite. A shaped ceramic body as set forth in Claim 1 or Claim 2, wherein said ceramic material has been obtained by treating a smectite clay mineral with an aqueous solution containing bismuth ions to ion-exchange at least a portion of ion-exchangeable cations thereof with bismuth ions. A shaped ceramic body as set forth in Claim 3, wherein said aqueous solution has been obtained by dissolving a bismuth salt in water. A shaped ceramic body as set forth in Claim 4, wherein said bismuth salt is 4BiNO₃(OH)₂.BiO(OH) or bismuth nitrate. A shaped ceramic body as set forth in Claim 4 or Claim 5, wherein said aqueous solution has a bismuth salt concentration of 0.001-0.005 mol/liter. A shaped ceramic body as set forth in any one of Claims 4-6, wherein the bismuth salt is used in an amount of 0.1-0.5 mole per mole of the smectite clay mineral. A shaped ceramic body as set forth in any one of Claims 3-7, wherein said treatment is performed at a temperature of 70-130°C. A shaped ceramic body as set forth in any one of Claims 3-8, wherein said treatment is followed by filtration. A shaped ceramic body as set forth in Claim 9, wherein filtration is followed by washing with hot water. A shaped ceramic body as set forth in any preceding claim, wherein said drying of the shaped product is performed at a temperature not higher than 200°C. A shaped ceramic body as set forth in any preceding claim, wherein the resulting dried shaped body is further calcined at a temperature of 200-1300°C for 1-200 hours. A shaped ceramic body as set forth in any preceding claim and having a tensile strength of 30-200 kg/cm² (2.9-19.6 M Pa). A process of preparing a shaped ceramic body, comprising the steps of shaping a ceramic material comprising a smectite clay mineral having at least a portion of ion-exchangeable cations thereof ion-exchanged with bismuth ions, and drying the resulting shaped product. A process as set forth in Claim 14, wherein said drying is performed at a temperature not higher than 200°C. A process as set forth in Claim 14 or Claim 15, wherein the resulting dried shaped body is further calcined at a temperature of 200-1300°C for 1-200 hours. A process as set forth in any one of Claims 14-16, wherein the ceramic starting material has been obtained as defined in any one of Claims 3-10. A process as set forth in any one of Claims 14-17, wherein the smectite clay mineral is selected from montmorillonite, biderite, saponite and hectorite.

Inventors: IKAZAKI FUMIKAZU, KIYOZUMI YOSHIMICHI, SEKINE TADAO, SHIN SHIGEMITSU, SUZUKI KUNIO, UCHIDA KUNIO, YONEMURA MICHIKO, IKAZAKI, FUMIKAZU, KIYOZUMI, YOSHIMICHI, SEKINE, TADAO, SHIN, SHIGEMITSU, SUZUKI, KUNIO, UCHIDA, KUNIO, YONEMURA, MICHIKO
Applicants: AGENCY IND SCIENCE TECHN, DIRECTOR-GENERAL OF THE AGENCY OF INDUSTRIAL SCIENCE AND TECHNOLOGY
Application year: 1989
Main classification: C04B33
IPC codes: C04B33