PROCESS FOR OBTAINING HIGH-PURITY BISPHENOL A

Abstract: There is provided a process for obtaining high-purity bisphenol A by removing most part of phenol from an adduct of bisphenol A with phenol and removing continuously the residual phenol by steam stripping, wherein a multi-tubular packed column is used as a stripping equipment. According to the process of the present invention, the residual phenol in bisphenol A can be removed constantly. In addition, the process of the present invention is economical because the residual phenol can be removed with a small amount of steam.

Description: The present invention relates to a process for obtaining high-purity bisphenol A and, more particularly, it relates to a process for removing phenol from bisphenol A effectively and constantly through a special steam stripping process. Bisphenol A is used as a raw material for polycarbonate resins. However, since phenol contained in bisphenol A acts as a terminal-group capping agent in polycarbonate resins, it has been desired to remove completely phenol from bisphenol A. One of the processes for obtaining bisphenol A consists of reacting phenol with acetone in the presence of an acid catalyst, removing the catalyst, water, unreacted acetone and a small amount of phenol from the product mixture, cooling the residual liquid mixture to crystallize bisphenol A as an adduct with phenol, separating the adduct from the mother liquor, and removing phenol from the adduct to obtain bisphenol A. A known method for removing phenol from the adduct of bisphenol A with phenol comprises distilling off phenol under reduced pressure. However, phenol cannot be removed completely with this method. Accordingly, it is necessary to use another step such as steam stripping as described in Japanese Patent Publication No. 43937/1972 or No. 7186/1965, or recrystallization from a hot aqueous solution as disclosed in Japanese Patent Laid-Open No. 88137/1982. So as to remove phenol industrially by steam stripping, a packed column or a wetted-wall column is used, and bisphenol A containing phenol is introduced at the top while superheated steam is supplied at the bottom to contact them in counterflow. When a packed column is used, a deflected flow is caused in the column as the diameter of the column increases and therefore the contact between gas and liquid becomes uneven and thus a large amount of phenol remains in the thus-obtained bisphenol A. In addition, since the melting point of bisphenol A is high and reaches about 157°C, bisphenol A is apt to solidify in the packed column and block it even if the packed column is heated as a whole. When a wetted-wall column is used, there occurs no above-mentioned trouble. However, so as to enlarge its throughput capacity, it is necessary to increase the diameter ad the length of the column because the contact area between gas and liquid is small. Furthermore, in both cases, there is needed an enormous amount of steam in order to remove phenol completely and, in these cases, a post treatment is necessary and the above-mentioned methods for removing phenol are not economical. SUMMARY OF THE INVENTION It is an object of the present invention to provide a process for removing a small amount of phenol contained in bisphenol A by steam stripping, wherein phenol can be removed effectively and the process is carried out stably. As a result of our extensive studies, we found that the above-mentioned object is achieved by using a multi-tubular packed column as a stripping equipment. The present invention was completed on the basis of this finding. In accordance with the present invention, there is provided a process for obtaining high-purity bisphenol A by removing the greatest part of phenol from an adduct of bisphenol A with phenol and removing continuously the residual phenol by steam stripping, wherein a multi-tubular packed column is used as a stripping equipment. DETAILED DESCRIPTION OF THE INVENTION The adduct of bisphenol A with phenol to be treated in the present invention may be the one obtained by reacting phenol with acetone in the presence of an acid catalyst, removing the catalyst, water, unreacted acetone and a small amount of phenol from the product mixture, cooling the residual liquid mixture to crystallize bisphenol A as an adduct with phenol, separating the adduct from the mother liquor, and removing phenol from the adduct to obtain bisphenol A, or the one obtained by dissolving crude bisphenol A in phenol, cooling the resulting liquid mixture to crystallize an adduct of bisphenol A with phenol, and separating the adduct from the mother liquor. In the present invention, the removal of the greatest part of phenol from the adduct of bisphenol A with phenol can be accomplished with a variety of known processes such as distillation, extraction, steam stripping and so on. At this stage, it is preferable to remove phenol from the adduct to such extent that the weight ratio of phenol to bisphenol A attains a value of from 0.01:1 to 0.1:1. The multi-tubular packed column to be used in the present invention is a multi-tubular wetted-wall column whose wetted-wall inner tubes are packed with a packing such as a Raschig rings and it is preferable that each inner tube can be heated from the exterior thereof. The inner diameter of the inner tubes can vary according to the throughput rate of the packed column and is preferably 1.27 to 12.7 cm (0.5 to 5.0 inches). The length of the inner tube is preferably 1 to 10 meters. Various sizes of packings can be used according to the diameter of the tube, throughput rate and the shape of the packing. The weight ratio of steam to bisphenol A introduced into the multi-tubular packed column is preferable from 0.01:1 to 1:1 The optimum conditions for stripping in the multi-tubular packed column are from 160 to 200°C in temperature and from 27.10² to 540.10² Pa (20 to 400 Torr) in pressure. EXAMPLES The present invention will be described in more detail with reference to the following examples. In the examples, "%" means "wt%" unless otherwise indicated. Example 1 A product mixture was obtained by condensating phenol with acetone in the presence of a hydrochloric acid catalyst. The product mixture was composed of 59.3% of phenol, 32% of bisphenol A, 2% of by-products, 4% of water and 2.7% of hydrogen chloride. This product mixture was transferred to a dehydrochlorination tower and the tower was operated at 9.33 x 10³ Pa (70 Torr) and with its bottom temperature at 120°C. Water, hydrochloric acid and a small amount of phenol were removed in the tower. The product mixture obtained from the bottom of the tower was cooled and an adduct of bisphenol A with phenol was crystallized at 45°C. The crystallized adduct was separated from the mother liquor by using a separator. This separated adduct was transferred to a phenol stripping tower and the tower was operated at 50 Torr and with its bottom temperature at 180°C. After the removal of phenol in the tower, the concentration of phenol in bisphenol A at the bottom became 3%. The bisphenol A was then transferred to a stripping tower at the flow rate of 250 kg/hr. The stripping tower was a multi-tubular packed column equipped with ten wetted-wall tubes with their inner diameter of 69 mm and with their length of 6,000 mm and these tubes were packed respectively with 1.27 cm (half-inch) Raschig rings. The stripping tower was operated at 10⁴ Pa (75 Torr) and 190°C. Superheated steam at 180°C was blown into the supplied bisphenol A with the ratio of 3% to the supplied bisphenol A and the concentration of phenol in the bisphenol A discharged from the bottom of the tower became 0.001%. Comparative example 1 Bisphenol A was obtained through the treatment as described in Example 1 except for the above stripping operation. The stripping tower used in this comparative example was the same multi-tubular wetted-wall column used in Example 1 except that the packing was removed from the multi-tubular packed column. The stripping tower was operated at 75 Torr and 190°C. Even when superheated steam at 180°C was blowed into the supplied bisphenol A with the ratio of 10% to the bisphenol A supplied at the flow rate of 250 kg/hr, the concentration of phenol in the bisphenol A discharged from the bottom of the tower was high and reached 0.010%. Comparative example 2 Bisphenol A was obtained through the treatment as described in Example 1 except for the above stripping operation. The stripping tower used in this comparative example was a packed column with its inner diameter of 211 mm and with its length 6,000 mm and the equipped tubes were packed with 1.27 cm (half-inch) Raschig rings. The stripping tower was operated at 10⁴ Pa (75 Torr) and 190°C. Even when superheated steam at 180°C was blown into the supplied bisphenol A with the ratio of 10% to the bisphenol A supplied at the flow rate of 250 kg/hr, the concentration of phenol in the bisphenol A discharged from the bottom of the tower varied between 0.020 and 0.040%. According to the process of the present invention, the residual phenol in bisphenol A can be removed constantly. In addition, the process of the present invention is economical because the residual phenol can be removed with a small amount of steam.

Claims: A process for obtaining high-purity bisphenol A by removing the greatest part of phenol from an adduct of bisphenol A with phenol and removing continuously the residual phenol by steam stripping, wherein a multi-tubular packed column is used as a stripping equipment. A process as claimed in Claim 1, wherein the multi-tubular packed column is the one whose each inner tubes can be heated from the exterior thereof. A process as claimed in Claim 1 or 2, wherein the stripping conditions in the multi-tubular packed column comprise a temperature in the range of 160 to 200°C and a pressure in the range of 27x10² to 54x10³ Pa. A process as claimed in any of the claims 1 to 3, wherein the weight ratio of steam to bisphenol A introduced into the multi-tubular packed column is from 0.01:1 to 1:1.

Inventors: IIMURO, SHIGERU, KITAMURA, TAKASHI, MORIMOTO, YOSHIO
Applicants: MITSUI TOATSU CHEMICALS, INC.
Application year: 1989
Main classification: C07C39
IPC codes: C07C37