Alkane oxidation process

Abstract: Alkanes are catalytically oxidized using site-specific framework substituted heteropolyacid or a polyoxoanion thereof.

Description: This invention relates to the oxidation of alkanes catalyzed by polyoxoanions (POAs) or heteropolyacids (HPAs) which have been promoted or otherwise modified to improve their effectiveness. Background of the Invention The use of POAs and HPAs for the catalytic air oxidation of alkanes such as butane is known. [See, for example, M. Ai, Partial Oxidation of n-Butane with Heteropoly Compound-based Catalysts, Proceedings of the 18th International Congress on Catalysis, Berlin, 1984, Verlag Chemie Vol. 5, page 475]. In addition our copending application (S.N. 076,570, filed July 20, 1987= EP-A-0 301 723 describes the use of HPA and POAs in liquid phase oxidation of alkanes; this application is incorporated herein by reference. HPAs and POAs, both in general and those which can be used to prepare the catalysts used in our invention, and their preparation are thoroughly described in Heteropoly and Isopoly Oxo-metalates , Pope et al, Springer-Verlag, New York 1983. In order to clarify the terminology used in the art, consider first a specific precursor used in our invention, H₃PW₁₂O₄₀. Since the cations in this material are hydrogen, the compound is a heteropolyacid. If the cations are not hydrogen but are metals such as an alkali metal, potassium, sodium, or lithium, or are ammonium, as in K₃PW₁₂O₄₀ or (NH₄)₃PW₁₂O₄₀, then it is obviously no longer an acid, and is referred to as a polyoxoanion. As described in Pope, HPAs and POAs are cage-like structures with a primary, generally centrally located atom(s) surrounded by the cage framework which contains a plurality of other metal atoms, the same or different, bonded to oxygen atoms. Since the central atom is different from the other metal atoms, it is described as "hetero." The other metal atoms are transition metals and have oxygen bonding such as where four of the singly bonded oxygen atoms are bonded to other M atoms in the framework and the fifth is bonded to the central hetero atom. Summary of Invention The present invention provides an alkane oxidation process comprising contacting an alkane at a temperature of about 50-350°C with air or oxygen and in the presence of a catalytically effective amount of a framework substituted heteropolyacid having the formula H e (X k M n M'₃O y ) -e where X is a group IIIA-VIA atom, M is molybdenum, tungsten or vanadium, k is 1-5, n is 5-17 and y is 18-59, wherein M' is zinc or a transition metal, wherein M' is free of double-bonded oxygen atoms and wherein each M' atom is bonded through oxygen to another M' atom; or polyoxoanions thereof. Our invention involves HPA and POA catalyzed, selective oxidation of alkanes with oxygen at relatively mild conditions (usually under 200°C) to a product rich in alcohol and with little or no burn of alkane to carbon oxides. Our HPAs and POAs are promoted by substitution of certain metal atoms in the framework with certain other metal atoms which results in an HPA/POA which differs from a "conventional" HPA or POA. In our prior application, S.N. 076,570, filed July 20, 1987= EP-A-0 301 723, we disclosed the use of certain promoted and/or modified HPAs/POAs. In that application, we described a modification known as "framework substituted" HPAs and POAs. The present application is directed to an improved type of framework substitution wherein three metal atoms in a triangular face in the HPA/POA framework are replaced with three different metals that render the HPA/POA more active. The framework substitution described in our prior application is a random substitution. We have now discovered how to control the locus of the substitution. Detailed Description Our invention deals with improvements to HPAs (and POAs thereof) having the general formula H e (X k M n O y ) -e where X, the central atom is preferably phosphorus, but others such as antimony, silicon, and boron are also suitable as are the generally known central atoms of HPAs, i.e., the group IIIA-VIA elements. Subscript k is preferably 1 but can be as high as 4-5. M is molybdenum, tungsten, or vanadium and n will vary from 5-20. Subscript y is usually 40 but can be as low as 18 or as high as 62. Notation e is the valence of the (X k M n O y ) group and will vary from case to case, but e is always the number of H atoms needed to balance the formula. In a preferred precursor HPA, i.e., the HPA which can be improved for use in our invention, k=1, n=12 and y=40 as in H₃PMo₁₂O₄₀ and in K₄PW₁₁VO₄₀. These and similar HPAs and POAs are shown in the aforesaid Pope reference. Most of our catalysts are of the Keggin structure and its isomers, as described in Pope, but other structures such as the Dawson structure also are suitable. HPAs are conventionally made by dissolving the metal oxides in the desired proportion in water, adjusting the pH to approximately 1-2 with acid (e.g. HCl) to provide the necessary H⁺ cations and then evaporating water until the HPA precipitates. If the POA is desired, a salt such as KCl is added and the POA precipitates, without need for the evaporation step. The desired proportion of the metal oxides added will vary somewhat from the theoretical amount required for the desired product, because in the precipitation step they do not precipitate in those exact same ratios. However, this is a matter of routine testing and adjustment. The existence of the HPA structure, i.e., the metal oxygen bonds, is confirmed by their characteristic NMR and/or IR spectra, which, as explained in Pope supra, are now known for the various HPAs. We have found that the activity of the precursor HPAs described above for the oxidation of alkanes is improved by replacing certain M atoms (and the oxygen atoms doubly bonded to them) with certain transition metals. The M atoms to be replaced are best shown from the following structure This twelve-cornered polyhedron structure is the metal atom configuration of a typical HPA described above. Between any two metal atoms is an oxygen atom, not shown, and from each metal atom is a doubly bonded oxygen, also not shown, and each of the metal atoms is bonded through oxygen to the central metal atom, not shown. It can be seen from the diagram that eight of the fourteen faces of the above polyhedron are triangular and the other six are four sided polygons. The M atoms which are replaced, according to our invention are the metal atoms in a triangular face, not just any metal atoms as would happen in a random replacement. The latter is what is disclosed in our earlier application described above. Another way of expressing our triangular insertion of new metal atoms, which we designate M′, is that the M′ atoms are each joined to each other in the above structural diagram (through oxygen if the complete structure were shown). As noted above, a typical HPA to which our invention is applicable has the formula H₃PMo₁₂O₄₀. When three M=O units are replaced with, e.g., Fe, the resulting framework substituted HPA has the formula H₆PMo₉Fe₃O₃₇. Thus the general formula of the HPAs used in our invention becomes H e (X k M n M'₃O y ) -e where k is 1-5, n is 5-17 and y is 18-59. M' can be zinc or any of the transition metals, namely the Group IV(a)-VIII metals of the periodic table (IUPAC notation). These are Ti, V, Cr, Mn, Fe, Co, Ni, Zr, Nb, Mo, Te, Ru, Rh, Pd, Hf, Ta, W, Re, Os, Ir, and Pt. Preferably the transition metal is from Group VIII or the first row of Group IV(a)-VII, i.e., Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt (Group VIII) or Ti, V, Cr, Mn (IV(a)-VII first row). The more preferred M' metals are Fe and Ni. As will be seen below in the examples, the three M' atoms do not have to be the same. Also, and quite obviously, M'₃ must be different than the three M atoms replaced. As noted above the framework substitution procedure described in our earlier application is adequate for random substitution but will not consistently provide the site specific substitution of the present invention. In order to achieve the latter, the following generalized procedures are employed. The overall procedure involves the reaction of a trilacunary polyoxoanion with a trimetalacetate, the metals of the latter being those to be inserted into the POA. The framework substituted POA is then converted to the corresponding HPA if desired. The trilacunary, Na₉(PW₉O₃₄), for example is prepared by mixing Na₂WO₄ and H₃PO₄ in the stoichiometric ratio in water at room temperature for 25 minutes and then slowly acidifying with 12N HCl to a final pH of 7.1. The Na₉PW₉O₃₄ precipitates and is separated. Other trilacunaries are prepared similarly by known analogous procedures. It is apparent from the above that the PW₉O₃₄ in the trilacunary POA represents the removal three times of O-W=O from the polyoxoanion and not merely W=O as described for the framework substituted HPA/POA of our prior invention. This is merely a matter of satisfying the valences of W in the portion removed. The singly bonded oxygen in the O-W=O is reinserted when M' is inserted so that the overall effect is the replacement of an M=O with M; thus changing the number of framework oxygen atoms from 40 to 37. The trimetal acetates have the general formula M₃O (CH₃COO)₆(H₂O)₃ where M is a transition metal or zinc and M₃ may be the same or different, e.g., Fe₂ NiO(CH₃COO)₆(H₂O)₃. They are prepared, e.g., by reaction of appropriate salts. Thus the above diiron-nickel compound is prepared by mixing sodium acetate, iron nitrate, and nickel nitrate in acetic acid/H₂O at room temperature and separating the precipitate. See Blake, et al. J. Chem. Soc. Dalton Trans., p. 2509 (1985) and Uemura, et al. J. Chem. Soc. Dalton Trans., p. 2565 (1973). Once the precursors are prepared, the framework substituted HPA/POA is formed by reacting them together. For example trilacunary oxoanion Na₉(PW₉O₃₄) is dissolved in a pH 6, buffered KOAc/HOAc solution (OAc=acetate). Then an equimolar amount of the trimetal acetate, e.g., Fe₂NiO(OAc)₆(H₂O)₃ dissolved in water is added. After initial mixing, the mixture is stirred for one hour at 50°C. and then cooled to room temperature. KCl is added to precipitate the product K₇(PW₉Fe₂NiO₃₇). Various preparatory methods are described in Finke et al. JACS 108, p. 2947 (1986), F. Ortega, Ph. D. Thesis, Georgetown University (1982), and Domaille and Watunga, Inorg. Chem. , 25 , 1239-42 (1986). The polyoxoanion salt can be readily converted to the acid form if desired. This is done by reacting an aqueous solution of the salt, e.g., K₇PW₉Fe₂NiO₃₇ at 50°C for 15 minutes with an aqueous solution containing excess of tetrabutylammonium bromide. Upon refrigeration at 4°C overnight, the organic salt, (n-C₄N)₇PW₉Fe₂NiO₃₇ crystallizes in 70% yield. The organic salt is filtered off and pyrolyzed at 500°C for 1 hr. It turns into the black solid H₇PW₉Fe₂NiO₃₇ as confirmed by IR. The existence of this framework substituted HPA/POA of our invention is confirmed by IR and elemental analysis in known manner. Our earlier application, referred to above, disclosed the promotion of HPA/POAs with V, Ti, Nt, Re, or azide for use in alkane oxidation. In like manner the catalysts of the present invention may be similarly promoted to gain further advantageous results. The oxidation is usually carried out in the presence of a solvent. It should be an unreactive polar solvent such as water, acetic acid, acetonitrile, benzonitrile, mixtures of water and acetic acid with chlorobenzenes, and the like. These solvents will yield a single phase homogeneous system although this is not always critical. Some solvents, such as benzene, are useful with HPAs but not POAs because of the difference in solubility. The oxidation is carried out at 50-350°C, in many cases 50-200°C, more preferably 125-175°C, and the low temperature is an advantage of the invention. The pressure is 0-5000 psig, and preferably is high enough to maintain the liquid phase, although this is not critical. Reaction time is 0.1-10 hours depending on conditions and is readily selected by the skilled worker. The amount of catalyst employed is generally .0001-1.0 mmoles catalyst per mole of reactant, preferably .001-0.1 but is always a catalytically effective amount. The alkane starting materials include straight and branched-chain compounds having from 1-20 carbon atoms, preferably 1-10 carbon atoms, more preferably 1-5, such as methane, ethane, propane, n-butane, isobutane, n-pentane, n-hexane, 2-methylpentane, 3-methylpentane, heptane, 2-methylheptane, 3-methylheptane and the like, as well as cycloalkanes having from 5-20 carbon atoms, preferably 5-10 carbon atoms, such as cyclopentane, cyclohexane, cycloheptane, cyclooctane, and the like. These compounds, if desired, may be substituted with various moieties, although care should be taken to exclude substituents which will adversely affect the activity of the catalyst. As noted above, our process is highly selective for alcohols and extremely selective for alcohols and ketones, selectivity being defined as the mole percentage of the alkane reacted which is converted to the desired product. In our process the selectivity to alcohol is usually over 40%, often over 60%, and in some cases over 80%. The selectivity to alcohol and ketone is usually over 90%, frequently over 95%, a truly outstanding result. Small amounts of acids are sometimes formed. The amount of carbon oxides formed is generally under 2%, usually less than 1% and is often under .2-.5%, the percentages being expressed as the mole percent yield of carbon oxides based on the reacted alkane. The following examples show the use of our catalysts in liquid phase oxidation of propane. The procedure varied slightly in the various runs but is typically as follows: The propane (1.36 moles) is dissolved in 38 g. of acetonitrile containing the catalyst and the reaction mixture pressured to 100-2000 psig with air or oxygen. The oxidation employed .0008-.050 mmole catalyst per mole of propane, the actual amount being shown after the catalyst formula. The reaction is carried out at 80-200°C for 1-10 hours after which the reaction mixture is analyzed. In the table below, TON/hr is the moles of product produced per hour per mole of catalyst used. The products are isopropyl alcohol and acetone; traces of isopropyl acetate by-products are also formed. Runs identified by letters are controls, numerical runs illustrate the invention.

Claims: An alkane oxidation process comprising contacting an alkane at a temperature of about 50-350°C with air or oxygen and in the presence of a catalytically effective amount of a framework substituted heteropolyacid having the formula H e (X k M n M'₃O y ) -e where X is a group IIIA-VIA atom, M is molybdenum, tungsten or vanadium, k is 1-5, n is 5-17 and y is 18-59, wherein M′ is zinc or a transition metal, wherein M' is free of double-bonded oxygen atoms and wherein each M' atom is bonded through oxygen to another M' atom; or polyoxoanions thereof. Process according to Claim 1 wherein M' is selected from the group consisting of Group IV(a)-VII, first row, and Group VIII. Process according to Claim 1 wherein M' is iron, nickel, zinc, chromium or combinations thereof. Process according to Claim 2 wherein at least two of M' are iron. Process according to one of Claims 2, 3, or 4 wherein k is 1, n is 9, y is 37, X is phosphorus and M is molybdenum, tungsten, or combinations thereof. Process according to one of Claims 1, 2, 3, 4, or 5 wherein the catalyst is further promoted by replacing an M atom with a different atom selected from the group consisting of vanadium, niobium, titanium, or rhenium. Process according to Claim 6 wherein said promoter is vanadium. Process according to one of Claims 1, 2, 3, 4, 5, or 6 wherein the catalyst is further promoted with azide. Process according to one of Claims 1-8 wherein said alkane contains 1-20 carbon atoms.

Inventors: ELLIS JR PAUL E, LYONS JAMES E, ELLIS, JR. PAUL E., LYONS, JAMES E.
Applicants: SUN CO INC R & M, SUN COMPANY, INC. (R&M)
Application year: 1989
Main classification: C07C29
IPC codes: C07B61, C07C29, C07C27, B01J27, C07C49, C07C31, C07C45