COMPOSITION AND METHOD FOR PRODUCING BORON CARBIDE/TITANIUM DIBORIDE COMPOSITE CERAMIC POWDERS USING A BORON CARBIDE SUBSTRATE

Abstract: A boron carbide/titanium diboride composite ceramic powder is disclosed produced by mixing boron carbide and a titanium source, such that the average reactant particle size is less than 20 micrometers and substantially all discrete reactant areas are less than micrometers, followed by heating the mixture wherein the boron carbide particles form substrates to which the titanium diboride particles are attached. The resulting powder has boron carbide and titanium diboride particles less than 20 micrometers in diameter. This powder can then be densified to form a part wherein the titanium diboride grains have an average size of less than 20 micrometers and the boron carbide grains having an average size of less than 50 micrometers. Because of the uniformity of initial dispersion, the densified part shows a microstructure that is also very uniform in distribution of boron carbide and titanium diboride.

Description: The present invention relates to the field of ceramic powders. More particularly, it relates to a method for producing ceramic powders and the ceramic powders and densified ceramic compositions produced therefrom. In recent years there has been much interest in composite ceramic materials. This is because some composite materials possess properties which are significantly improved over the properties of the individual constituents. These ceramic composites, including both fiber-reinforced and multicomponent structures, have been targeted as applicable to a variety of scientific and technological uses. Some of these uses include tooling applications, indenters, nozzles, and so forth. For these and other uses the desirable material should be as lightweight and as tough as possible; however, the attainment of one of these properties has in many cases been accomplished at the expense of the other property. Boron carbide has been found to exhibit excellent hardness and a relatively low specific gravity, but it lacks toughness (K Ic = 3.6 MN/m 3/2 ). Titanium diboride, on the other hand, is nearly as hard and much tougher when compared with boron carbide, but it is also much heavier. Because of the potentially complementary properties of these two materials, researchers have directed attention to producing composites comprising both compounds. Results of this research indicate that a ceramic produced therefrom approximates titanium diboride's toughness and exceeds boron carbide's hardness while maintaining a low specific gravity. For example, U. S. Patent 2,613,154 discloses the manufacture of titanium diboride/boron carbide composites from a mixture of titanium powder and boron-rich boron carbide powder. This method does not, however, appear to be suitable for producing a variety of titanium diboride/boron carbide compositions without the incorporation of excess carbon or boron in the densified piece. The same problem is encountered in connection with research done by Russian workers, as disclosed in E.V. Marek, "Reaction of Boron Carbide with Group IV Transition Metals of the Periodic Table," Mater. Izdeliya, Poluchaemye Metodom Poroshk. Metall., Dokl. Nauchn. Konf. Aspir. Molodykh Issled. Inst. Probl. Materialoved. Akad. Nauk Ukr. SSR , 6th, 7th, Meeting Date 1972-1973, 156-9. This paper describes mixtures of boron, carbon and titanium which are hot-pressed to composites comprising B₄C and TiB₂ phases. A microhardness superior to that of either B₄C or the borides is reported. Japanese Patent Application 1985-235764 discloses boron carbide/titanium diboride composites prepared by dispersing boron carbide powder and titanium diboride powder in organic solvents such as toluene, and ball milling using a tungsten carbide-cobalt alloy as a milling medium. This material is then dried and cold-pressed. The authors report an extreme hardness for a sintered piece prepared from 40 to 50 percent titanium diboride. U.S. Patent 4,029,000 discloses a boron carbide/titanium diboride composite, prepared from a physical mixture of boron carbide and titanium diboride powders, for use as an injection pump for molten metals. The particle diameter is in the range of 2 to 6 µm for the boron carbide and 5 to 15 µm for the titanium diboride. The hardness attained upon sintering is reported to be lower than that of boron carbide alone. Research has also been directed toward other composites comprising titanium, boron and carbon. For example, the literature also describes various methods of preparing composite materials comprising titanium carbide and titanium borides. Among these are, e.g., U. S. Patents 4,138,456 and 3,804,034, which describe preparation of a TiC/TiB₂ composite and a TiC/TiB/B₄C composite, respectively, produced from physical mixtures of powders. U. S. Patent 4,266,977 discloses preparation of a composite prepared in a plasma reactor from an "intimate" mixture of the three constituents. An important factor in the ultimate utility of a ceramic composite is the degree to which the constituents are dispersed. To realize the maximum benefit of a particulate composite, the components should be uniformly distributed on a microscopic scale. However, such uniform distribution is at best extremely difficult to attain in physical mixtures, such as those produced using any of various milling techniques, in part because of agglomeration of component particles. Physical mixtures are defined as mixtures of components in which the starting and ending components are the same. This is in contrast with the in situ production of ending components by various means. A further consideration in producing an "ideal" composite material relates to particle size. This is because the high incidence of failure in engineered ceramic parts can often be attributed to small cracks or voids which result from incomplete packing of the precursor powders. A solution to this problem would be to use extremely fine composite powders that are substantially uniform as to particle diameter. Such powders would pack more tightly and thereby reduce the number of void spaces formed in the ceramic body. It has been suggested, by E. A. Barringer and H. K. Bowen in "Formation, Packing and Sintering of Monodispersed TiO₂ Powders," J. Amer. Ceram. Soc. 65, C-199 (1982), that an "ideal" ceramic powder for producing a high quality part would be of high purity and contain particles which are substantially spherical, nonagglomerated, and both fine and uniform in size. As a ceramic powder is sintered, adjacent particles fuse into grains. In general, the grain size is governed by the particle size of the powder from which the part is prepared. Thus, the sintering of finer particles presents the opportunity to produce fine-grained bodies. This is especially important in TiB₂/B₄C composites, in which the TiB₂ and B₄C grain sizes are preferably less than or equal to about 20 µm in order to maximize the hardness and toughness of the composite. Thus, the particle sizes should preferably be significantly smaller than 20 µm. The effect of grain size on the integrity of boron carbide bodies having no titanium diboride constituent has been investigated by A. D. Osipov et al., "Effect of Porosity and Grain Size on the Mechanical Properties of Hot-Pressed Boron Carbide," Sov. Powder Metall. Met . Ceram . (Engl. Transl.) 21(1), 55-8 (1982). The authors disclose that parts exhibiting a fine grain size are stronger than parts consisting of coarse grains. In order to produce the desired particle sizes, especially in the under-20 µm range, it is often necessary to mill the powder. While milling does promote size reduction, it is time consuming, may impart impurities such as metals, and does not decrease size beyond a certain point, even with additional milling time. This point depends on both the substance being milled and the chosen milling technique. See, e.g., W. Summers, "Broad scope particle size reduction by means of vibratory grinding, Ceramic Bulletin 62(2) (1983) 212-215. For most techniques boron carbide, a hard substance. reaches its minimum size at around 1 um in diameter using attrition milling techniques. Further steps, such as acid leach and washing steps, may be required subsequent to milling in order to increase purity of the product. Thus, what is needed is a method of producing a composite titanium diboride/boron carbide ceramic powder that is fine, uniform and of high purity, and which shows a high degree of mixing of the constituents. The method should reduce or eliminate the need for extended milling or purification procedures subsequent to production. The present invention provides a method of producing a boron carbide/titanium diboride composite ceramic powder comprising: (a) intimately mixing as reactants boron carbide and a titanium source such that the average reactant particle size is less than 20 µm and there are substantially no discrete reactant areas greater than 50 µm; and (b) reacting the product of step (a) under conditions sufficient to produce a boron carbide/titanium diboride composite ceramic powder. A densified part prepared from this powder and having a microstructure characterized by titanium diboride grains having an average size of less than 20 µm and boron carbide grains having an average size of less than 50 µm is also provided. The present invention further provides a ceramic composite powder consisting essentially of boron carbide and titanium diboride, the boron carbide and titanium diboride comprising particles averaging less than 20 µm in diameter, at least a portion of the boron carbide particles forming substrates to which at least a portion of the titanium diboride particles are attached. The present invention also provides a densified ceramic part prepared from this powder. Finally, the present invention also provides a densified composite ceramic part consisting essentially of boron carbide and titanium diboride wherein the boron carbide and titanium diboride grains show a dispersion which can be characterized as having an average coefficient of variation of the area percent of the minor phase, over a titanium diboride concentration of 0.1 percent to 99.9 percent, which is less than 10, as determined by scanning electron microscopic analysis of 20 fields measuring 26 x 26 µm each at a magnification of 778 x. It can be further characterized as having an average range of the area percent of the minor phase that is less than 9. FIG. 1 shows an energy dispersive spectroscopic (EDS) X-ray map at a magnification of 2,100 x of the boron carbide/titanium diboride ceramic composite powder prepared as described in Example 1. The titanium diboride component is shown as the light phase. FIG. 2a shows a scanning transmission electron micrograph (STEM) of the powder prepared as described in Example 2 at a magnification of 50,000 x, illustrating the size of the crystallites and orientation of the smaller titanium diboride particles on the surface of the larger boron carbide particles. FIG 2b shows a scanning electron micrograph (SEM) of the same particle at the same magnification. FIG. 3 shows a transmission electron micrograph of the powder prepared as described in Example 2 at a magnification of 87,000 x, illustrating the grain size and orientation of the titanium diboride along the grain boundaries. FIG. 4 shows a scanning electron micrograph of the densified part prepared as described in Example 2. The part is prepared from a composite ceramic powder of 20 percent titanium diboride and 80 percent boron carbide. The micrograph, at a magnification of 778 x, is divided into a grid including 20 fields measuring 26 x 26 µm each. FIG. 5 shows an optical micrograph of the etched, densified part prepared as described in Example 2, illustrating the distribution of titanium diboride along boron carbide grain boundaries. The magnification is 2,000 x. FIG. 6 shows a comparative scanning electron micrograph of a densified part prepared from a physical mixture of boron carbide and titanium diboride powders prepared by mixing commercial powders together as described in Comparative Experiment 2. The mixture is 19 percent titanium diboride and 81 percent boron carbide. This comparative figure, at a magnification of 778 x, has a grid of 20 fields measuring 26 x 26 µm each. FIG. 7 shows a scanning electron micrograph of the densified part prepared as described in Comparative Example 2 at a concentration of 30 percent titanium diboride. The micrograph, at a magnification of 778 x, is divided into a grid including 20 fields measuring 26 x 26 µm each. The present invention provides a composition of a boron carbide/titanium diboride composite ceramic powder having a novel association between the particles of boron carbide and titanium diboride. It further provides a densified part, showing a unique microstructure, which can be prepared from the powder composition. Finally, it provides a method of preparing the powder that is both fast and economical. The powder composition is novel in that there is a physical attachment between the boron carbide particles and the titanium diboride particles. This physical attachment is due to the fact that the titanium diboride particles are formed in situ , on the surface of the boron carbide particles, having as their boron source the boron in the boron carbide particles. Thus, the boron carbide forms a substrate for the physically attached titanium diboride particles. This associational level means that, at relatively comparable concentration levels, individual boron carbide particles will be to a significant extent surrounded by the generally smaller titanium diboride particles. This level of association tends to both preclude agglomeration of the titanium diboride particles, and maximize the potential for crack deflection by the titanium diboride particles in a densified part prepared from the composite powder. There are a number of possible reactant choices within the scope of the invention as claimed. The term "boron carbide" is used generically to encompass any boron carbide, including the various non-stoichiometric boron carbides such as boron-rich boron carbides. For example, B₄C, B₈C, B₁₃C₂, B₂₅C, and mixtures thereof are all within the scope of the invention. Of these, B₄C is preferred. The titanium source can preferably be titanium in any reducible form, or it can be a reduced titanium source. Thus, reducible or reduced forms such as TiO, TiO₂, Ti₂O₃, TiO₂, Ti₃O₅, TiC, TiN, TiH₂, Ti, and reduced titanium halides are preferred, and more preferred is TiO₂. If a reducible titanium source is used it is necessary to use as a third reactant a reducing agent suitable to reduce the titanium source. This reducing agent is preferably a carbon source, and more preferably elemental carbon, such as carbon black, acetylene carbon black, graphite, or a mixture thereof; a hydrocarbon; a carbohydrate, such as a sugar, starch, or a mixture thereof. Of these, carbon black and acetylene carbon black are more preferred. The reducing agent can also be a hydrogen source such as hydrogen gas or a hydrocarbon. If a reduced titanium source is selected, it is preferable to use a boron-rich boron carbide in order to minimize the presence of free carbon in the product. The method for producing the boron carbide/titanium diboride ceramic composite powder of one embodiment of the present invention is essentially a two-step process in which the individual reactants are first mixed and then heated. The initial mixing step is important in ensuring maximum distribution of the reactants, particularly of the titanium source and, if needed, the reducing agent, to obtain the maximum distribution of the physically associated and attached boron carbide/titanium diboride particles. This mixing can be done using either a dry mixing or wet mixing method as known to the skilled artisan. In general the wet mixing method is preferred, using aqueous or other media in order to suspend the starting materials. Dry mixing, using for example ball-mills or agitation equipment, can also be performed. If dry mixing is done it is preferred to use polymeric or compatible ceramic mixing media rather than metallic media in order to reduce the introduction of impurities into the mixture. The goal is to mix the constituents "intimately," the term "intimate" being defined as a degree of association such that light microscopy or general elemental analytical techniques, such as, for example, electron dispersive spectroscopy, transmission electron microscopy, and carbon/oxygen analysis, preferably reveal that substantially all individual discrete areas of reactants are less than 50 micrometers in diameter, more preferably less than 25 micrometers, and most preferably less than 10 micrometers. "Substantially" as used herein means that at least 85 percent of discrete areas fall within the maximum preferred diameters. In view of the preference for relatively small discrete concentrations of reactants, there is also an inherent preferred maximum average particle size for the mixed materials. The preferred particle size after the mixing is done is such that the average boron carbide particle size is less than 20 µm, more preferably less than 10 µm, and most preferably less than 1 µm. It is preferred to use pre-comminuted powders in order to reduce the introduction of impurities. However, it is also possible to use a boron carbide powder that prior to mixing exhibits a larger particle size and then mix by a ball-milling technique, such that the particle sizes are reduced at the same time as the areas of discrete concentrations are reduced. Similarly, it is preferred that the post-mixed titanium source particle size is less than 20 µm, more preferred that it is less than 10 µm, and most preferred that it is less than 1 µm. It should also be noted that it is possible, and preferred, to deagglomerate the reactants prior to the mixing step. This helps to increase the degree of mixing possible. Deagglomeration can be done, for example, by a prior jet-milling or ball-milling step. Once the constituent powders have been intimately mixed the next step is to react them under conditions sufficient to form the boron carbide/titanium diboride composite ceramic powder showing the desired associational level in which the titanium source reacts with some of the boron in the boron carbide and forms titanium diboride on the boron carbide substrate. This is preferably done by heating. In the case of using a reducible titanium source and a reducing agent such as a carbon source, the heating induces the carbothermal reduction of the titanium source with the carbon and boron carbide and subsequent formation of TiB₂. This heating is preferably done under an inert or reaction-compatible atmosphere, which is preferably selected from the group consisting of argon, helium, neon, hydrogen, carbon monoxide, xenon, krypton, and mixtures thereof, with argon being more preferred. Appropriate stoichiometric adjustments may be advisable when using a reaction-compatible gas such as carbon monoxide or other gases and a reducible titanium source such as titanium dioxide or the suboxides or halides thereof, because of the resultant reduction of a portion of the titanium source by the gas. The heating is done at a temperature preferably above 1000°C, and more preferably 1200°C to 2000°C. Still more preferred is a range of 1500°C to 1800°C, and most preferred is 1600°C to 1750°C. Temperatures that are too low may result in either very slow or incomplete reaction, while temperatures that are too high encourage grain growth, thus making a very fine powder less likely to be produced. The time period generally required to effect the reaction in the most preferred temperature range, i.e., 1600°C to 1750°C, is preferably on the order of 10 to 15 minutes for powder quantities of about 30 grams or less; however, longer time periods may be needed for lower temperatures and greater quantities of reactants. Variations in powder depths also require appropriate heating time adjustments. In batch reactions it is helpful to monitor the reaction by gas chromatography using a carbon monoxide detector, which will show a drop in the carbon monoxide concentration when the carbothermal reduction has been completed and the yield therefore maximized. The heating can be done using equipment generally known to those skilled in the art. A graphite crucible, for example, can be employed as a carrier for the reactants through a standard-type induction furnace. Alternatively, the heating can be performed in a resistance-heated furnace, wherein the crucible is moved through the furnace at a rate determined by the length of the passage and the desired reaction time. A fixed crucible can also be used. An advantage of the present method is that, because of the reaction involved, it is possible to "purify" the composite powder concurrently with producing it. "Purify" as used herein refers to the substantial elimination of excess reactants present in the product. This purification can be accomplished by adjustment of the stoichiometry of the desired reaction. For example, in the case of a reaction using TiO₂ and elemental carbon as reactant sources, an "idealized" reaction sequence would be: (1 + x)B₄C + 2TiO₂ + 3C = xB₄C + 2TiB₂ + 4CO In the above equation, x is the mole percent of B₄C not converted to TiB₂. However, in some cases there will be stoichiometric deviations in the boron or carbon phases, such as for example where a portion of the boron carbide is a boron-rich or carbon-rich boron carbide. In this case it is possible for those skilled in the art to analyze the boron carbide prior to mixing, in order to determine its stoichiometry, and then adjust the titanium oxide and/or carbon concentration accordingly to ensure maximization of yield as well as purity. Similar adjustments can be made in order to produce a purer product when different titanium and, when needed, reducing agent sources are selected. The final boron carbide/titanium diboride powder produced by the method of one embodiment of the present invention will preferably show the composition of another embodiment of the present invention, i.e., one in which there is a physical attachment of the titanium diboride particles on the surfaces of the boron carbide particles, the boron carbide particles thus serving as substrates. The overall composition of the powder can vary, from 0.1 percent boron carbide and 99.9 percent titanium diboride, to its converse, 0.1 percent titanium diboride and 99.9 percent boron carbide. It will be understood that the proportion of the constituents will obviously have an effect on determinations of mixing level in the powder, as well as distribution in a densified part prepared from this powder. An advantage of the present invention is that, by careful control of time and temperature and because of the way the titanium diboride forms on the boron carbide substrate, it is possible to obtain an individual titanium diboride particle no greater than the maximum initial boron carbide particle size. Thus, control of the boron carbide particle size in turn enables control of the maximum titanium diboride particle size. The composite ceramic powder of the present invention is suitable for use in preparing a densified part that will show a novel microstructure. Methods of densification are known to the skilled artisan, and can include hot pressing, hot isostatic pressing, sintering, and so forth. The densified part, like the powder, can be 0.1 to 99.9 weight percent boron carbide and 99.9 to 0.1 weight percent titanium diboride. Where the titanium diboride content is very significant, grain growth of the boron carbide during the densification process tends to be inhibited because there is sufficient titanium diboride to allow for substantial isolation of the boron carbide. This inhibition of grain growth of the boron carbide in general tends to improve the crack deflection capability of the final densified part. The densified part, because of the powder from which it is made, shows a very uniform distribution of titanium diboride and boron carbide grains. It is preferred that the microstructure of the densified part shows substantially all of the titanium diboride grains are less than 20 µm in diameter, more preferably less than 5 µm, and most preferably less than 2 µm. It is also preferred that the boron carbide grains are less than 50 µm in diameter, more preferably less than 20 µm, and most preferably less than 10 µm. The grain size of the part is partially determined by the particle size of the composite powder, which is in turn partially determined by the particle size of the reactant powders. Thus, control of the particle size of the starting boron source helps to predetermine the grain size in the densified piece. It is further preferred that the dispersion level of the titanium diboride and boron carbide grains can be characterized as having an average coefficient of variation of the area percent of the minor phase, over a titanium diboride concentration range of 0.1 percent to 99.9 percent, which is less than or equal to 10, as determined by scanning electron microscopic analysis of 20 fields measuring 26 x 26 µm each at a magnification of 778 x. This is more preferably less than or equal to 5. The coefficient of variation can be defined as the value representing the standard deviation divided by the average of the area percent of the minor phase. Analysis of the 778 x magnification fields at a magnification of at least 3,000 x improves accuracy. The dispersion can preferably be further characterized as having a range of the area percent of the minor phase which is less than 9, as determined by scanning electron microscopic analysis at a magnification of 778 x of 20 fields measuring 26 x 26 µm each. This range is more preferably less than about 5. Range is defined as the average of the differences between the high and low values of the area percent of either constituent in each field, taken over the 20 fields as described above. The following examples are given to illustrate and not to limit the scope of the invention. All parts and percentages are by weight unless otherwise stated. Example 1 An amount of 5.89 g of titanium dioxide; about 22.8g of subµm boron carbide assaying as 94.64 weight B₄C containing 3.1 percent free carbon, 1.11 percent oxygen, 1.02 percent nitrogen and 6.69 percent excess boron; and a quantity of carbon weighing 1.19 g are made into a slurry under high agitation and then heated to a thick paste. The still wet mass is transferred to a circulating air drying oven at 105°C and dried overnight. The resulting cake is gently crushed to a powder weighing 29.28 g. Examination by light microscope reveals that substantially all boron carbide and titanium source particles are less than 20 µm in diameter, and substantially all individual discrete reactant areas are less than 50 µm in diameter. About 15 g of the precursor is placed in a graphite crucible and inserted into an induction furnace. The chamber is evacuated and subsequently kept under flowing argon gas. The sample is then heated to 1650°C over a period of 30 minutes and maintained at temperature for 10 minutes. The furnace is then turned off and the sample allowed to cool under flowing argon gas. A black product weighing 12.69 g, i.e., about 84.06 percent of the initial 15.0g of precursor, is obtained and is determined to be a composite of B₄C/TiB₂ by X-ray diffractometry. X-ray mapping of the composite by energy dispersive spectroscopy indicates a uniform distribution of the titanium component throughout the sample, as shown in FIG. 1. The sample is further analyzed by transmission electron microscopy, which indicates well-formed crystallites covering the surfaces of boron carbide particles, as shown in FIGS. 2a and 2b. Examination of the composite powder by optical microscope also indicates that particles covering the surface produce color reflections that are different from that of boron carbide, appearing to be titanium diboride. Examination of the powder indicates that most titanium diboride grains are less than 1 µm in diameter, and are distributed along the boron carbide boundaries, as shown in FIG. 3. A portion of this sample is hot-pressed at 2100°C and 5,000 psi (34.5 MPa) pressure. FIG. 4 shows the scanning electron micrograph from which the dispersion level is determined. This dispersion level can be characterized as having a coefficient of variation of the area percent of the minor phase of 6, when 20 fields measuring 26 x 26 µm each are examined by scanning electron microscopy at 778 x. Total titanium diboride concentration is calculated to be 20 percent. The analysis of each field is done at a magnification of 3,000 x. FIG. 5 shows an optical micrograph of the densified part which has been chemically etched to illustrate the distribution of titanium diboride grains around the boron carbide grains. Comparative Experiment 1 In comparison to the fine microstructure obtained using the process of the present invention, a physical mixture of subµm titanium diboride and subµm boron carbide in similar proportions, i.e., about 19 percent titanium diboride and about 81 percent boron carbide, which is ultrasonically treated to deagglomerate it prior to hot pressing under similar conditions, gives essentially coarse grains of up to about 10 µm in diameter, as shown by scanning electron microscopy in FIG. 6. In that scanning electron micrograph the titanium diboride is shown as the light phase. Example 2 An amount of 5.74 g of titanium dioxide, 21.88 g of boron carbide, and 1.56 g of carbon are wet mixed under high agitation and concurrently dried. The boron carbide initially has an average particle size of 4 µm and assays as 99.36 percent B₄C containing 0.13 percent nitrogen, 0.51 percent oxygen, and 4.2 percent excess boron. The precursor thus formed weighs 28.85 g. About 15 g of this precursor is heated to 1600°C in an induction furnace under an argon atmosphere. After cooling under flowing argon a black powder is obtained, weighing about 12.79 g. This is shown to be a composite of titanium diboride and boron carbide by X-ray diffractometry. X-ray mapping of the sample by energy dispersive spectroscopy further indicates a uniform distribution of titanium throughout the powder. A dense part is prepared from the powder using methods known to those skilled in the art. Examination of the microstructure of the part indicates a distribution of fine grains of TiB₂ in the B₄C matrix. Comparative Experiment 2 The following Table 1 shows a comparison of the coefficients of variation (C/V) of the area percent titanium diboride for densified parts produced from a powder of the present invention's process and of physically mixed composite powders having comparable percents of titanium diboride. In the physically mixed powders the starting powders are subµm boron carbide and titanium diboride powders. To prepare a physically mixed powder the boron carbide is dispersed in methanol and the dispersion then sonicated 1 minute. Then the titanium diboride is added and the dispersion is again sonicated 1 minute. The product is then dried, crushed, and sieved to -100 mesh (149 micrometers). The table includes the coefficient of variation data from Example 1 and Comparative Experiment 1, as well as coefficients of variation for parts showing other titanium diboride loadings. Table 2 shows a comparison of the ranges for parts prepared from a physically mixed powder and a powder of the present invention at comparable loadings. It will be seen that the process of the present invention produces in general significantly lower coefficients of variation, as determined by scanning electron microscopic analysis at 778 x of 20 fields measuring 26 x 26 µm each. The exception, which is a densified part having an area percent of titanium diboride of 30 and a coefficient of variation for the carbothermal process of 25, is believed to be unexpectedly high due to insufficient mixing of the boron carbide in the first step of the process. This interpretation is supported by FIG. 7, which shows that the specimen has good titanium diboride dispersion but unusually large boron carbide regions when compared with, e.g., FIG. 4, which has a lower titanium diboride loading. The range is also substantially less for parts produced from the process and powder of the present invention. Example 3 Raw materials of the same chemistry and stoichiometry as shown in Example 2 are mixed dry and about 15.00 g of the resulting powder is heated in an induction furnace and under flowing argon to about 1600°C for about 5 minutes. Upon cooling a black powder weighing 12.82 g is obtained and identified as a composite of TiB₂ and B₄C by X-ray diffractometry. Microscopic examination of the microstructure of a dense part reveals a distribution of fine titanium diboride grains, about 1 µm in diameter, situated in a boron carbide matrix. Example 4 An amount of 5.74 g of titanium dioxide, 22.18 g of boron carbide, and 1.45 g of carbon are dry mixed to give 29.13 g of precursor powder. The boron carbide initially has an average particle size of 2 µm and assays as 97.95 percent B₄C containing 0.12 percent nitrogen, 0.96 percent oxygen, 0.25 percent free carbon, and 1.76 percent excess boron. 15.01 g of this powder is heated as described in Example 2 to 1600°C for about 10 minutes and subsequently cooled. A black powder weighing 12.79 g is obtained and gives an X-ray diffraction pattern corresponding to a TiB₂/B₄C composite. Example 5 An amount of 33.37 lbs of titanium dioxide, 41.25 lbs of boron carbide, and 5.4 lbs of carbon black are mixed in a plastic lined mill using polymeric milling media to prevent contamination. The boron carbide has an average particle size of 2 µm and assays as 21.58 percent total carbon including 0.6 percent free carbon, 1.17 percent oxygen and 0.24 percent nitrogen. The sample is then loaded into graphite boats a half-inch (1.27 cm) deep and calcined in a graphite heated tunnel kiln under a flowing argon atmosphere at a temperature of 1740°C for about 50 minutes. The fine powder obtained is subjected to a mild jet milling operation to break up and mix in any soft agglomerates. Examination of the powder by X-ray diffractometry indicates the formation of TiB₂/B₄C composites which by chemical analysis are shown to be composed of 50 percent by weight titanium diboride and 50 percent by weight boron carbide.

Claims: A method of producing a boron carbide/titanium diboride composite ceramic powder, comprising: (a) intimately mixing as reactants boron carbide and a titanium source such that the average reactant particle size is less than 20 micrometers in diameter and there are substantially no individual discrete reactant areas greater than 50 micrometers; and (b) reacting the mixture of step (a) such that a boron carbide/titanium diboride composite ceramic powder is produced wherein at least a portion of the boron carbide particles form substrates to which at least a portion of the titanium diboride particles are attached. The method of Claim 1 wherein reacting the mixture comprises heating to a temperature above 1000°C. The method of Claim 2 wherein said heating is at a temperature of 1600°C to 1750°C. The method of any one of claims 1 to 3 wherein the heating is under an inert or reaction-compatible atomsphere that is argon, helium, hydrogen, carbon monoxide, or a mixture of two or more thereof. The method of any one of the preceding claims further comprising the step of deagglomerating at least one of the reactants prior to mixing by jet-milling or ball-milling the reactant. The method of any one of the preceding claims wherein said intimate mixing includes an aqueous medium and optionally includes a dispersant. The method of any one of the preceding claims wherein the boron carbide is B₄C, B₈C, B₁₃C₂, B₂₅C or a mixture of two or more thereof. The method of any one of the preceding claims wherein the titanium source is a reducible titanium source that is TiO, TiO₂, Ti₂O₃, Ti₃O₅, TiC, TiN, a reduced titanium halide or a mixture of two or more thereof, and a reducing agent is also mixed as a reactant in step (a). The method of Claim 8 wherein the reducing agent is a carbon source, a hydrogen source, or a mixture thereof that is elemental carbon, a hydrocarbon, a carboydrate or a mixture of two or more thereof. The method of any one of claims 1 to 7 wherein the titanium source is a reduced titanium source which is Ti or TiH₂. The method of any one of claims 1 to 7 claims wherein the ceramic composite powder comprises 0.1 to 99.9 weight percent boron carbide and the balance is titanium diboride. The method of any one of claims 1 to 7, further comprising: densifying the composite ceramic power to form a densified part, wherein the densified part is a microstructure characterized by titanium diboride grains having an average size of less than 20 micrometers in diameter and boron carbide grains having an average size of less than 50 micrometers. A composite ceramic powder consisting essentially of boron carbide and titanium diboride particles averaging less than 20 µm in diameter, at least a portion of the boron carbide particles forming substrates to which at least a portion of the titanium diboride particles are attached. The composite ceramic powder of Claim 13 formed into a densified composite ceramic part consisting essentially of boron carbide and titanium diboride wherein the boron carbide and titanium diboride grains show a dispersion characterized as having an average coefficient of variation of the area percent of the minor phase, over a titanium diboride concentration range of 0.1 percent to 99.9 percent, that is less than 10, as determined by scanning electron microscopic analysis at a magnification of 778 x of 20 fields measuring 26 x 26 micrometers each.

Inventors: KHAZAI, BIJAN, MOORE, WILLIAM G.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1989
Main classification: C04B35
IPC codes: C04B35