A method for decolouring sulphuric acid deriving from acid production processes

Abstract: The present invention relates to a method for decolouring sulphuric acid produced in accordance with the contact method, comprising one or more absorption circuits. The produced sulphuric acid is decoloured by adding hydrogen peroxide to the system. The method is characterized by adding the hydrogen peroxide to the sulphuric acid in the final absorption circuit, and by maintaining the temperature in this circuit above about 70°C.

Description: The present invention relates to a method for decolouring sulphuric acid produced in accordance with the contact method, comprising one or more absorption circuits and the addition of hydrogen peroxide to the resultant sulphuric acid, for the purpose of decolouring the same. Process gases led to sulphuric acid plants often contain contaminants, in greater or lesser quantities, inter alia saturated and non-saturated carbon compounds, resulting in discolouration of the sulphuric acid produced. This discolouration of the acid has several causes. For example, discolouration may be caused from oil present in the seals of dust separators in the process-gas purification system, oil-containing waste present in the processes from which the gases derive, combustion gases deriving from thick oil used for heating process apparatus, or even coal particles used for this purpose, and residues of different flotation agents in treated ore concentrate. Several methods for decolouring sulphuric acid are known to the art. These methods include the addition of oxidants, such as potassium permanganate, hydrogen peroxide and ozone, by electrolytic oxidation and with the aid of activated carbon. Such oxidants as potassium permanganate and ozone are expensive and present many problems in practice. Potassium permanganate is not readily soluble in water, resulting in a decrease in the concentration of the acid when potassium permanganate is added. Furthermore, the presence of the manganese residues also presents a risk of renewed discolouration. Ozone is a chemical which has a harmful effect when inhaled, even at extremely low levels. The process of electrolytic oxidation requires the use of extremely complicated apparatus and the costs involved by this method are so high that the method has not been used anywhere for decolouring purposes. Neither are decolouring methods which use activated carbon fully satisfactory in practice, because the technical effect of such methods is in doubt. The components of many carbon qualities result in a certain degree of discolouration. Consequently, the only known discolouration method acceptable in practice is one in which hydrogen peroxide is added to the sulphuric acid. One such method is disclosed in DE-B-10 67 793, in which the treatment is effected on an acid derived from a separate pre-drying tower upstreams of the final absorption stage. The hydrogen peroxide is added to tube vessels in which the acid is agitated about two hours. Another method is the standard method proposed by the suppliers of contact sulphuric-acid plants. This method requires the addition of hydrogen peroxide to a pump receiver located downstream of the last absorption stage of the system, but upstream of the tanks in which the sulphuric acid produced is stored, in which pump receiver the concentration of the sulphuric acid can fluctuate between 94 and 97% and in which the temperature is normally about 60-70°C. It has been found, however, that this known standard method for decolouring sulphuric acid is not sufficiently effective, and that at times sulphuric acid will be heavily darkened, despite the addition of hydrogen-peroxide in excess quantities. The addition of excess quantities of hydrogen peroxide also results in the presence of peroxide residues in the acid, which renders the acid unacceptable to many consumers. This complicates the marketing situation, since the possibilities of depositing darkly-coloured acids are very limited and the drop in turnover is accordingly quite significant. In principle, darkly-coloured acid is accepted solely for the manufacture of fertilizers. An increase in the temperature of production acid for the purpose of accelerating the reaction has been found to result in problems relating to the corrosion of material in the pumps and conduits of the plant apparatus, making it necessary to also cleanse the acid from corrosion products. The Japanese company Mitsubishi has proposed a method of improving decolouration of sulphuric acid with hydrogen peroxide, and of rendering such methods more effective. The acid produced is decoloured in a plant comprising three, Teflon®-lined tanks mutually connected in series. The plant is dimensioned to provide an acid stay-time of about 30 min in each tank. The coloured acid is first steam heated to about 105°C and pumped to the bottom of the first tank, subsequent to having been admixed with hydrogen peroxide in the form of a ca 35-percent solution. Subsequent to passing through the tanks, the acid is cooled in a cooler to a suitable temperature, prior to being conducted to the storage tanks. Although the Mitsubishi method would appear to be effective for decolouring acids, it is not an attractive method for practical use in the majority of cases. The method is complicated and the necessity to install additional tanks for decolouring the product acid coupled with the necessity to provide heat exchangers and coolers both upstream and downstream of the decolouring units adds greatly to the costs. Consequently, there is a need for an effective decolouring method which can be used with existing contact sulphuric-acid plants, and which can be carried out without appreciable additional investment costs and operating costs, and which will not add to environmental or working hazards or contamination of the sulphuric acid produced. It has now surprisingly been found possible to provide a method for decolouring sulphuric acid produced from acid production processes which fulfills the above desiderata and requirements placed on the production of sulphuric acid, as discussed in the aforegoing. The inventive method is characterized by the process steps set forth in the following claims. Thus, in accordance with the novel method hydrogen peroxide is introduced to the acid receiver of the sulphuric acid circulating in the final absorption circuit, while maintaining the acid at a temperature of above about 80°C, thereby providing a sulphuric acid having a colour index below 50 APHA. The concentration of the sulphuric acid in the absorption circuits is an important criterium for effective absorption, and is always maintained within the narrowest of limits, and is preferably above 98.3%, normally close to 99%. The temperature in the absorption circuit when decolouring the acid is preferably maintained within a range of 80-100°C. The addition of hydrogen peroxide to the absorption circuit provides the advantage of an increased stay time with respect to H₂O₂. It has been found that an advantage is gained when the hydrogen peroxide is added in a finely divided state, for instance through spray-type metering pipes. The hydrogen peroxide addition is advantageously controlled automatically with respect to the acid produced. Thus, it is possible to monitor the decolouring effect continuously, and therewith determine the amount of peroxide that needs to be added. It has also been found advantageous to thoroughly agitate or stir the acid at the time of adding peroxide to the system. The hydrogen peroxide can be added together with other flows entering the final absorption stage, for instance sulphuric acid from other stages in the process. The peroxide can also be added in the form of chemical compounds from which peroxide is released when coming into contact with sulphuric acid, for instance peroximonosulphuric sulphuric acid, even though the addition of peroxide in this form is less effective than when adding peroxide itself. Normally, in order to achieve satisfactory colour reduction of the acid while ensuring, at the same time, that no traceable quantities of residual peroxide remain, it is necessary to introduce peroxide in dosages of 0.5-0.6 kg H₂O₂/tonne sulphuric acid (H₂O₂ is here calculated as 100% H₂O₂). The amount of H₂O₂ required is contingent, inter alia, on the degree of discolouration of the acid. The invention will now be described in more detail, partly with reference to working examples. Blackening of sulphuric acid can be measured in different ways, one standard method being the so-called APHA-method, in which the results are designated "colour index" and are given APHA or mg Pt/l. Example 1 In a sulphuric acid plant, in which decolouring was effected with hydrogen peroxide introduced to a pump receiver located downstream of the final absorption stage, but before the acid storage tanks, a progressively higher colour index was obtained, despite increasing the normal dosage of hydrogen peroxide. An attempt was made to improve the colour index, by changing the operating conditions of the roasting processes from which the sulphur dioxide gas originated. Among other things, changes were made to the quantities and qualities of the various roasting materials treated. None of the measures taken improved the acid colour index, however. By changing the location at which hydrogen peroxide was introduced to the system, from said pump receiver, in which the concentration of H₂SO₄ was 94-97% and the temperature 60-70°C, to the acid receiver in the final absorption circuit, where the sulphuric-acid concentration was 98.5% and the temperature 70-80°C, a considerable improvement in acid quality was obtained immediately, in that the colour index fell from an average of 1140 mg Pt/l (with certain peaks up to about 4000 mg Pt/l) down to 400 mg Pt/l. In order to improve the contact between hydrogen peroxide and sulphuric acid still further, a separate metering pipe made of Teflon® was placed in the nozzle system or arrangement. As a result, the colour index fell to 50-200 mg Pt/l, this level being maintained for three production months. The temperature range of the final absorption acid was then raised from 70-80°C to 80-100°C, wherewith the colour index fell further to 15-50 mg Pt/l. An acid having a colour index of 50 APHA is discerned as colourless by the human eye. Example 2 Absorption sulphuric acid containing 98.9% H₂SO₄ and having a colour index of 1250 APHA was treated with 50% hydrogen-peroxide solution at mutually different temperatures, reaction times and in mutually different dosages, in order to establish the kinetics taking place when decolouring with hydrogen peroxide. The object was to achieve satisfactory colour reduction together with a residual content of H₂O₂∼0. Some results typical of the experiments are shown in Tables 1 and 2 below, in which H₂O₂ is calculated as 100% H₂O₂. Colour index and residual contents H₂O₂ when metering 0.6 kg H₂O₂ per tonne H₂SO₄ to the system at 100°C. Time min With agitation Without agitation APHA H₂O₂ g/l APHA H₂O₂ g/l 5 50 0.25 100 0.3 20 40 0.02 50 0.05 40 40 0.01 40 0.02 60 40 0 40 0 Colour index and residual contents H₂O₂ at varying temperatures and H₂O₂-additions Temp °C Time min H₂O₂ kg/tonne Residual H₂O₂ g/l Colour index APHA 80 5 0.3 650 20 " 435 40 " 260 60 " 0.03 200 80 5 0.6 650 20 " 360 40 " 260 60 " 0.3 125 80 5 0.9 580 20 " 290 40 " 260 60 " 0.5 100 90 5 0.6 0.6 275 20 " 0.3 100 40 " 0.1 75 60 " 0.01 50 100 5 0.4 0.2 175 20 " 0.03 75 40 " 0 75 60 " 0 75 100 5 0.6 0.25 50 20 " 0.12 40 40 " 0.01 40 60 " 0 40 Example 3 Experiments corresponding to the experiments of Example 2 were carried out, but with the H₂O₂ additions being made in the form of peroximonosulphuric acid (1% by weight H₂O₂, 27 % by weight H₂SO₅). The resultant reduction in colour was poorer than the colour reduction achieved in corresponding experiments in which hydrogen peroxide was used. When dosing with 0.6 kg H₂O₂ in the form of H₂SO₅, a colour index of 320 was obtained after 60 minutes. The corresponding colour index obtained when using a pure hydrogen peroxide solution was 125.

Claims: A method for decolouring sulphuric acid formed in the contact method, including one or more absorption circuits and in which hydrogen peroxide is added to the acid in the absorption circuits, characterized by adding the hydrogen peroxide to the acid receiver in the final absorption circuit, and by maintaining the temperature of the acid in the final absorption circuit at above about 80°C at the same time, thereby providing a sulphuric acid having a colour index below 50 APHA. A method according to Claim 1, characterized by maintaining the temperature within the range of 80-100°C. A method according to Claim 1 or 2, characterized by adding finely divided hydrogen peroxide to the sulphuric acid. A method according to Claims 1-3, characterized by automatically controlling the addition of hydrogen peroxide with respect to the produced acid. A method according to Claims 1-4, characterized by agitating or stirring the sulphuric acid vigorously when adding hydrogen peroxide thereto. A method according to Claims 1-5, characterized by adding the hydrogen peroxide together with other flows entering the final absorption stage.

Inventors: JONSSON JAN LENNART, NILSSON STEN AKE, JONSSON, JAN LENNART, NILSSON, STEN AKE
Applicants: BOLIDEN CONTECH AB
Application year: 1989
Main classification: C01B17
IPC codes: C01B17