Mouldable composition

Abstract: Mouldable compositions comprising a metallic powder or a combination thereof with ceramic powder, mixed with an organic binder are disclosed, at least a part of which binder comprises a synthetic resin component (A) having a heat deformation temperature of 130°C or higher. The component A may be used in combination with another component (B) having a melting point of 30°C - 100°C, with or without another thermoplastic component (C), having a heat deformation temperature of 130°C or less. Mouldable compositions, comprising metallic and/or ceramic powder mixed with an organic binder comprising a secondary or tertiary amine (D), or a combination thereof with a thermoplastic resin (E), are also disclosed.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to mouldable metallic and/or ceramic compositions, and to a process for producing a sintered body therefrom. 2. Description of the Prior Art It is known to produce sintered bodies from metallic or ceramic powder mixed with thermoplastic binders (such as polypropylene, methacrylate copolymer, polystyrene, ethylene-vinyl acetate copolymer, low density polyethylene, and combinations of them), or combinations thereof with plasticizer or lubricants (such as paraffin wax, diethyl phthalate, and stearic acid). It is also known to produce sintered bodies by injection moulding such compositions and then removing or driving off the binder (hereinafter referred to as debinding) from the moulded articles, followed by sintering the articles (U.S.Patent 2,593,943). As there is a tendency of deformation of moulded bodies by gravity, or cracking or blistering with decomposed gas, during debinding of moulded articles produced from these known moulding compositions; moulded bodies are buried in ceramic or metallic powder to prevent deformation, or heated up slowly such as at a rate of 1 - 10° C/hour to depress generation of decomposed gas, and therefore it is necessary to brush off the powder from the surface of the debinded bodies prior to sintering, or it takes long time to drive off the binder. Thus, these known moulding compositions are not satisfactory for industrial production. SUMMARY OF THE INVENTION It is an object of the present invention to provide a mouldable metallic and/or ceramic composition, having little or reduced tendency of deformation during debinding. It is another object of the present invention to provide a mouldable metallic or ceramic composition, which can be debinded within a short period of time without blistering. It is still another object of the present invention to provide a mouldable metallic or ceramic composition, capable of providing economically sintered bodies free from defects, such as deformation or blistering. It is yet another object of the present invention to provide a process for producing economically sintered bodies, within a short period of time without blistering. Briefly, these and other objects of the present invention as hereinafter will become more readily apparent have been attained broadly by a mouldable composition, which comprises a metallic powder or a mixed powder of metallic and ceramic powder, mixed with an organic binder comprising at least one synthetic resin component (A) having a heat deformation temperature of 130°C or higher, with or without at least one other component (B) having a melting point of 30°C - 100°C. The binder may comprise thermoplastic component (C), having a heat deformation temperature of 130°C or less. If component (A) is selected from polyamides, polyesters, polysulfones and semi-synthetic resins, the binder may further comprise at least one secondary and/or tertiary amine (D). In a second aspect, the present invention provides a process for producing a mouldable composition according to the first aspect of the invention. In a third aspect the invention provides a process for producing a sintered body shaped from a mouldable composition obtainable by a process according to the second aspect of the invention. Fig. 1 is a perspective view of a specimen. Fig. 2 is a cross sectional view illustrating the method for measuring deformation of a specimen. Fig.3 is a cross sectional view illustrating the deformed amount (h). [Component A] Said synthetic resin component (A) has a heat deformation temperature of 130°C or higher, preferably 150°C or higher, as measured acording to ASTM D648 using a load of 4.6 Kg/cm². Suitable synthetic resins include thermoplastic resins, for example, polyacetals, including homopolymers of trioxane, and copolymers of trioxane with ethylene oxide, dioxorane, substituted dioxoranes, 1,4-dioxane or the like; polyaryl ethers, such as polyphenylene oxides, polyphenylene sulfides; polyamides, such as nylons 6, 11, 12 and 66, and copolymers of them; polycarbonates; polyesters, such as polyethylene terephthalates and polybutylene terephthalates; polysulfones, such as polyaryl sulfones, polyether sulfones; polyether ketones, polyvinylidene fluorides, and the like, as well as mixtures of two or more of them. Among these, preferred are polyacetals, polyphenylene oxides, polysulfones, polycarbonates, polyesters and polyamides. Particularly preferred are polyacetals, in view of their low melt viscosity and facilities for moulding and thermal decomposition. As at least a part (preferably 10 - 40 %)of said component (A), there may be used one or more crosslinked thermoplastic resins and/or thermosetting resins. Suitable examples of crosslinked thermoplastic resins include resins of addition polymerization type [for example, those mentioned below, such as acrylic resins, olefinic resins, styrene copolymers and other vinyl polymers], copolymerized with one or more crosslinking monomers. Suitable crosslinking monomers include, for example, bis(meth)acrylamides (bisacrylamides and bismethacrylamides; similar expressions are used hereinafter), such as N,N′-methylenebis(meth)acrylamides; polyvinyl compounds, such as divinylbenzenes, divinyltoluens, divinylether, divinylketone, trivinylbenzenes and the like; polyesters of unsaturated mono- or poly-carboxylic acids with polyols, such as ethylene glycol di(meth)acrylates, trimethylolpropane tri(meth)acrylates, glycerin tri(meth)acrylates; and poly(meth)allyl ethers of polyols, such as di(meth)allyl ethers of alkylene glycols (such as ethylene glycol). Among these, preferred are bis(meth)acrylamides, polyvinyl compounds, and polyesters of unsaturated mono-or poly-carboxylic acids with polyols. Particularly preferred are N,N′-methylene bis-(meth)acrylamides, divinylbenzenes, ethylene glycol di(meth)acrylates, and trimethylolpropane tri(meth)acrylates. Illustrative examples of such resins are crossliked polystyrenes, and crosslinked styrene-(meth)acrylate copolymers. Other examples of crosslinked thermoplastic resins include polycondensation type resins [for example, polyesters (such as polyethylene terephthalates), polyamides (such as Nylon 66), polyimides, polysulfones, poly-para-phenylenes], crosslinked with one or more crosslinkers. Suitable examples of such crosslinkers include polycondensation compounds, for instance, polycarboxylic acids, such for instance, polycarboxylic acids, such as aromatic and aliphatic polycarboxylic acids (benzene tricarboxylic acids and the like); polyamines, such as aromatic and aliphatic polyamines (polyalkylene polyamines, such as diethylene triamine and the like); polyols, such as polyhydric alcohols (glycerin, trimethylol propane and the like) and alkylene oxide (such as ethylene oxide and/or propylene oxide) adducts of these compounds containing 3 or more active hydrogen atoms. Suitable thermosetting resins include, for example, phenolic resins, urea resins, cured epoxy resins, and polyurethane resins. Semi-synthetic resins, such as nitrocellulose and cellulose acetates may also be used. These resins are usually used in the form of powder. Such resin powder may be those produced in powder form, or those powdered after production of resins. Particle size of these resins is not particularly restricted, and can vary according to particle size of particulate material (metallic and/or ceramic powder). Preferably, these resins have an average diameter smaller than that of the particulate material, particularly smaller than a half of the latter. [Component B] Said component A is used preferably in combination with at least one other component (B) having a melting point of 30 C - 100°C, preferably 50 - 100°C. Suitable examples of said component B are polyethers, such as those represented by the formula : wherein R is a residue of active hydrogen atom-containing compound; R′ is H, a mono-valent hydrocarbon radical or acyl radical; Z an alkylene radical containing 1 - 4 carbon atoms, or an alkylene radical containing 2 - 4 carbon atoms, having an aryl-substituent; m is an integer of 1 - 8 (preferably 1 - 3); and n is an integer of at least 2 (preferably at least 4). Examples of active hydrogen atom-containing compounds, constituting the residue R, are water; alcohols, for instance, low molecular weight polyols (such as ethylene glycol, propylene glycols, 1,3- and 1,4-butane diols, 1,6-hexane diol, neopentyl glycol, cyclohexylene glycol, glycerin, trimethylol propane, pentaerythritol, sorbitol, sucrose and the like), and monohydric alcohols (such as aliphatic alcohols containing 1 - 20 carbon atoms and aromatic alcohols); phenols, for example, polyhydric phenols (bisphenols, such as bisphenol A), and mono-hydric phenols [phenol, naphthols, alkyl(C₁-C₁₂)- or aryl-substituted phenols, such as octylphenol, nonylphenol, dodecylphenol and phenylphenols]; amines, for example, alkanol amines (such as mono-, di- and tri- ethanol amines and propanol amines), aliphatic or aromatic polyamines (such as ethylene diamine and diethylene triamine), aliphatic or aromatic monoamines [mono- and di- alkyl(C₁-C₂₀) amine, aniline and the like]; and mixtures of two or more of them. Among these, preferred are water and low molecular weight polyols, particularly ethylene glycol and propylene glycols. Suitable mono-valent hydrocarbon radicals in R' include, for example, alkyl radicals containing 1 - 20 carbon atoms, such as methyl, ethyl, propyl, butyl, hexyl, octyl and decyl radicals; aromatic hydrocarbon radicals, including aryl radicals (such as phenyl and naphthyl), aralkyl radicals (such as benzyl and phenethyl), and alkylaryl (octylphenyl and nonylphenyl). Examples of suitable acyl radicals in R' are those of carboxylic acids containing 2 - 20 carbon atoms, such as acetyl. Among R', preferred are H and C₁-C₄ alkyl, particularly H, methyl and ethyl. Examples of said alkylene radicals Z include alkylene radicals, such as methylene, ethylene, propylene, butylene, and phenyl-ethylene groups. Among these, preferred are ethylene, propylene, butylene and combinations of ethylene with propylene. Particularly preferred is ethylene. Molecular weight of polyethers can vary widely, but preferably up to about 20,000. Illustrative examples of suitable polyethers are polyalkylene glycols, including those having a molecular weight of usually about 150 - about 20,000, preferably 1000 - 10,000, and containing 2 - 4 carbon atoms in each alkylene group, such as polyethylene glycols (MW 150 - 20,000), polypropylene glycols (MW 200 - 5,000), polytetramethylene glycols (MW 200 - 3,000), copolymers of ethylene oxide and propylene oxide (MW 200 - 20,000). Other examples of said component B are waxes, such as petroleum wax, natural waxes (such as bees wax), and synthetic waxes (such as polyethylene wax); low molecular weight solid materials, such as fatty acids (C₁₀-C₂₀ or more, such as stearic acid), salts thereof (soaps and metal soaps such as aluminum stearate), fatty alcohols (C₁₂-C₂₀ or more, such as stearic alcohol), fatty amines (C₁₂-C₂₀ or more, such as mono- and di-stearyl amines), and various surfactants (such as those written in U.S.Patent 4,331,447); and mixtures of two or more of them. Among these, perferred are polyethers, particularly polyalkylene glycols, especially polyethylene glycols, in view of compatibility, when used in conjunction with a polyacetal as the component A. [Component C] The binder may contain thermoplastic component (C) having a heat deformation temperature of 130°C or less. Component (C) may have a melting point of more than 100°C. Suitable components C include, for example, polyethers[ those represented by the formula (1) but having higher molecular weight, such as polyethylene oxides]; and polymers of ethylenically unsaturated monomers, including polyolefins (such as polyethylenes, polypropylenes, poly-4-methylpentene-1, polystyrenes, polyalpha-methyl-styrenes , ethylene-vinyl acetate copolymers), and (meth)acrylic polymers [such as poly(meth) acrylates and two or more of them. Molecular weight of these polymers may vary widely; but preferred are those having a molecular weight of about 1000 - about 10 millions, more preferably about 5000 - about 5 millions. These polymers have thermal decomposition temperarure of usually 150 - 600°C, preferably 200 - 400°C. Among these, preferred are polyethylene oxides, particularly those having a molecular weight of about 50,000 - about 5 millions, with respect to compatibility. [Component A - suitable resins to be cross linked] Suitable examples of resins of addition polymerization type include acrylic resins [polymers and copolymers of esters of (meth)acrylic acids, such as polymethyl (meth)acrylates, polyethyl (meth)acrylates, polybutyl (meth)acrylates, polycyclohexyl (meth)acrylates, butyl (meth)acrylate-methyl (meth) acrylate copolymers, butyl (meth)acrylate-dodecyl (meth) acrylate copolymers, butyl (meth)acrylate-acrylonitrile copolymers, methyl (meth)acrylate-acrylamide copolymers, ethyl (meth)acrylate-2-chloroethyl vinyl ether copolymers, methyl (meth)-acrylate-(meth)acrylic acid copolymers, methyl (meth)-acrylate-hydroxyethyl (meth)acrylate copolymers, and butyl (meth)acrylate-N,N-dimethylaminoethyl (meth)acrylate copolymers]; olefinic resins [(co)polymers of hydrocarbon monomers or derivatives thereof], such as polyethylenes, polypropylenes, polybutenes, polyisobutylenes, polystyrenes, poly-alpha-methylstyrenes, chlorinated polyethylenes, ethylene copolymers, such as ethylene-vinyl acetate copolymers, ethylene-acrylic copolymers [ethylene-methyl (meth)acrylate copolymers, ethylene-butyl (meth)acrylate copolymers, ethylene-(meth)acrylic acid copolymers and the like], styrene copolymers, such as styrene-acrylic copolymers [styrene-methyl (meth)acrylate copolymers, styrene-butyl (meth)acrylate copolymers, styrene-(meth)acrylic acid copolymers and the like]; vinyl esteric or alcoholic resins, such as polyvinyl acetates, polyvinylacetals (polyvinylformals, polyvinylacetoacetals, polyvinylpropionals, polyvinylbutyrals, polyvinylhexylals and the like; halo-containing resins, such as polyvinyl chlorides, vinyl chloride-methyl (meth)acrylate copolymers, vinyl chloride-acrylonitrile copolymers, vinyl chloride-ethylene copolymers, polyvinylidene chlorides, poly-4-fluoro-ethylene, poly-3-fluoroethylene, polyvinylidene fluorides, and the like; nitrogen-containing resins, such as poly(meth)acrylonitriles, polymethyl cyanoacrylates, polyvinylidene cyanides; and so on. [Component D] In another embodiment of the present invention, the binder comprises component (A), selected from polyamides, polyesters, polysulfones and semi-synthetic resins, together with at least one amine (D), selected from the group consisting of secondary amines and tertiary amines. Suitable examples of said amine (D) are monoamines and polyamines (including ones containing a primary amino group in addition to the secondary and/or tertiary amino group), having an amine value of usually 50 - 500, preferably 40 - 400 and a molecular weight of usually at most 3000, preferably 100 - 1000. Preferable amines include those represented by the formula : In the formula (2), R₁ is a monovalent hydrocarbon radical containing 5 - 30 carbon atoms, R₂ is hydrogen atom or a monovalent hydrocarbon radical containing 1 - 30 carbon atoms, R₃ is hydrogen atom or a monovalent hydrocarbon radical containing 1 - 30 carbon atoms, R₄ is is hydrogen atom or a monovalent hydrocarbon radical containing 1 - 5 carbon atoms, Y is an alkylene group containing 2 - 4 carbon atoms, which may have an aryl side group, and n is an integer of 0 - 5. Examples of said hydrocarbon radical R₁, include aliphatic hydrocarbon radicals, for example, alkyl groups (such as pentyl, 2-ethylhexyl, octyl, dodecyl, hexadecyl, octadecyl, eicosyl and docosyl groups), alkenyl groups (such as myristoleyl, palmitoleyl, oleyl and rinoleyl groups); cycloaliphatic hydrocarbon radicals, for instance, cycloalkyl groups (such as cyclohexyl grpoup); and aromatic hydrocarbon radicals, for example, aryl groups (phenyl and naphthyl groups), aralkyl groups (such as phenethyl, phenyloctyl and phenyldodecyl groups), alkylaryl groups (such as methylphenyl, octylphenyl and dodecylphenyl). Among these, preferred are aliphatic hydrocarbon radicals, particularly those containing 10 - 30 carbon atoms. Suitable hydrocarbon radicals in R₂ and R₃ include the above-mentioned monovalent hydrocarbon radicals containing 5 - 30 carbon atoms, and lower aliphatic hydrocarbon radicals, for example, lower alkyl groups (such as methyl, ethyl, n- and i-propyl and butyl groups) and lower alkenyl groups (such as allyl and butenyl groups). Preferred as R₂ are aliphatic hydrocarbon radicals (particularly those containing 1 - 20 carbon atoms); and preferred as R₃ are aliphatic hydrocarbon radicals (particularly those containing 1 - 20 carbon atoms) and hydrogen atom. Suitable monovalent hydrocarbon radicals in R₄ are those as mentioned above, containing 1 - 5 carbon atoms. Plural R₄s(in case where n is 2 or more) may be the same or different. Preferred as R₄ are methyl and ethyl groups (particularly ethyl group) and hydrogen atom. Suitable examples of said alkylene groups Y are inclusive of alkylene proups containing 2 - 4 carbon atoms, such as ethylene, propylene and butylene groups; and aryl-substituted alkylene groups, such as phenylethylene group. Plural Y (in case where n is 2 or more) may be the same or different. Among Y, preferred are ethylene, propylene and butylene groups, and combination of ethylene and propylene groups, particularly ethylene group. Said n is an integer of 0 - 5, preferably 0 - 1. Illustrative of amines of the formula (2) are : [I] Secondary amines : aliphatic amines, for instance, alkyl amines (such as methyl octyl amine, dodecyl octadecyl amine, dioctadecyl amine, di-hardened tallow alkyl amine and didocosyl amine), and alkenylamines (such as octadecyl allyl amine, methyl oleyl amine and dioleyl amine); cycloaliphatic amines, such as octadecyl cyclohexyl amine; and aromatic amines, such as dibenzyl amine, diphenyl amine, phenyldodecyl methyl amine, diphenyldodecyl amine, and N-octadecyl aniline ; [II] Tertiary amines : aliphatic amines, for instance, alkyl amines (such as dimethyl octyl amine, dimethyl decyl amine, dimethyl dodecyl amine, dimethyl coconut amine, dimethyl myristyl amine, dimethyl palmityl amine, dimethyl octadodecyl amine, methyl didodecyl amine, methyl dioctadodecyl amine, trioctyl amine and tridodecyl amine), and alkenylamines (such as dioctadecyl allyl amine, octadecyl diallyl amine, dimethyl oleyl amine, methyl dioleyl amine and dimethyl rinoleyl amine); cycloaliphatic amines, such as methyl octadecyl cyclohexyl amine; and aromatic amines, such as tribenzylamine, triphenylamine, dimethyl benzyl amine, dimethyl phenyldodecyl amine and N,N-dimethyl-p-dodecyl aniline ; and [III] Polyamines : apiphatic polyamines, for example, alkyl-substituted alkylene(C₂-C₄) diamines or dialkylene (C₂-C₄) triamines, such as octadecyl ethylene diamines, tridodecyl propylene diamines and octadecyl tetramethyl diethylene triamines ; as well as mixtures of two or more of these amines. Among these, preferred are aliphatic monoamines, especially those containing at least one aliphatic hydrocarbon radical of 10 - 30 carbon atoms. In stead of or in combination with these amines of the formula (2), there may be used other secondary and/or tertiary amines, for instance, cycloaliphatic polyamines, such as dodecyl cyclohexylene diamine and methyl octadecyl isophorone diamine); aromatic polyamines, such as tetradodecyl phenylene diamine, dioctadecyl tolylene diamines, octadecyl xylylene diamines and dioctadecyl diphenylmethane diamine; heterocyclic amines, such as N-amino dodecylpiperazine and N-octadecyl morpholine; alkanol amines, such as dodecyl ethanol amine; and mixtures of two or more of them. Said amine (D) is used together with one or more of organic binders comprising resin component (A) selected from polyesters, such as polyethylene terephthalates, polytetramethylene terephthalates and polyethylene sebacates; polyamides, such as Nylon 66; polysulfones; and semi-synthetic polymers, such as nitrocellulose, cellulose acetate and ethyl cellulose. [Additional components] Furthermore, the binder may contain optionally one or more additional components, such as plasticizers, lubricants, surfactants, various coupling agents (such as silane coupling agents), and so on. Suitable examples of plasticizers include ester plasticizers, including carboxylates, for example, esters of aromatic mono- or poly- carboxylic acids, such as phthalates (dimethyl, diethyl, dibutyl, diheptyl, di-n-octyl, di-2-ethylhexyl, diisononyl, diisodecyl, dilauryl, dicyclohexyl and butylbenzyl phthalates, and the like), trimellitates (tris-C₄-C₁₁alkyl trimellitates, such as tris-2-ethylhexyl trimellitate, and the like), benzoates (polyoxyalkylene benzoates, such as polyoxyethylene benzoates, and the like); esters of aliphatic monobasic acids, such as butyl oleate and glycerin monooleate; esters of aliphatic dibasic acids, such as adipates (dibutyl, dihexyl, di-n-octyl, di-2-ethylhexyl, didecyl, diisodecyl and other dialkyl adipates, dibutyldiglycol adipate and the like), azelates (such as di-2-ethylbutyl and di-2-ethylhexyl azelates), sebacates (such as dibutyl, di-n-octyl and di-2-ethylhexyl sebacates), maleates (such as dibutyl and di-2-ethylhexyl maleates), fumarates (such as dibutyl fumarate), and so on; esters of hihydric alcohols, such as diethylene glycol dibenzoate and triethylene glycol di-2-ethyl-butyrate; esters of hydroxy acids, such as ricinoleates (methyl acetyl-ricinoleate, butyl acetyl-ricinoleate and the like), glycolates (such as butyl phthaloyl butyl glycolate), citrates (triethyl acetyl-citrate, tributyl acetyl-citrate and the like); and polyesters, such as polypropylene adipates; and phosphates, such as triethyl, tributyl, trioctyl, trichloroethyl, tricresyl, tributoxyethyl, trisdichloropropyl, tris-beta-chloropropyl, triphenyl, octyl diphenyl and tris-iso-propylphenyl phosphates; epoxy plasticizers, such as epoxidized fatty esters; and other plasticizers, such as stearic acid plasticizers and chlorinated paraffin plasticizers; as well as mixtures of two or more of these plasticizers. Among these, preferred are phthalates, esters of aliphatic dibasic acids, and polyoxyalkylene benzoates. More preferred are phthalates, particularly dibutyl, dioctyl and butylbenzyl phthalates. Illustrative examples of lubricants are aliphatic hydrocarbons, liquid paraffins, microcrystalline waxes, natural paraffins, synthetic paraffins , polyolefin waxes, and derivatives of them (such as partially oxidized ones, chlorinated ones and fluorinated ones); higher fatty alcohols, such as lauric, stearyl and oleyl alcohols, and mixed fatty alcohols; higher fatty acids, such as lauric, stearic and oleic acids, and mixed fatty acids (those obtainable from tallow, fish oil, coconut oil, soybean oil, colza oil, rice bran oil and the like), fatty amides (oleylamide, stearamide, methylene-bis-stearamide, ethylene-bis-stearamide and the like), soaps and metallic soaps (stearates of barium, calcium, zinc, aluminum, magnesium and the like), fatty esters [higher fatty acid esters of monohydric alcohols (such as butyl oleate), higher fatty acid (partial) esters of polyhydric alcohols (such as glycerin monooleate), montan wax, and the like]; and mixtures of two or more of them. Among these, preferred are aliphatic hydrocarbons, higher fatty acids and fatty esters, especially liquid paraffins, stearic acid and montan wax. Suitable surfactants include those written in U.S.Patent 4,331,447, for example, anionic surfactants, such as dodecylbenzene sulfonates and polyoxyethylene(4) nonylphenylether sulfates; nonionic surfactants, such as polyoxyethylene(4) stearyl amine, mono- and/or di-ethanol amide of stearic acids; cationic surfactants, such as lauryltrimethylammonium chloride; ampholytic surfactants, such as stearyldimethylcarboxymethyl-betain; and mixtures of two or more of them. Surfactants can improve wettability of the binder towards the particulate material. [Particulate Material] Metallic powders employed with the binder in the preparation of the mouldable compositions of this invention may be prepared from any metal which is stable in the atmosphere and is reducible to powdered form. Examples of materials of metal character that are applicable for use are metals, for example, iron (such as carbonyl iron, atomized iron and reduced iron), nickel (such as carbonyl nickel), cobalt, aluminum, copper, titanium, molybdenum, zirconum, chromium, lead, manganese, wolfram, zinc, tin, beryllium, germanium, magnesium, silicon and boron; and alloys containing two or more thereof, for example, stainless steel, iron-nickel alloy, high speed steel, super alloy, magnetic materials, brass, bronze, monel metal, iron-silicon alloy, iron-boron alloy and the like. Among these, preferred are iron, and iron alloys, such as stainless steel, iron-nickel alloy and high speed steel. Ceramic powders, which may be utilized in the invention in conjunction with (or in stead of) metallic powders, include for example, oxides, such as alumina, silica, zirconia, beryllia, magnesia and titania; silicates such as mullite and cordulite; titanates, such as barium titanate; carbides (particularly water non-reactive carbides), such as carbides of silicon, boron, aluminium, wolfram, titanium, zirconium, hafnium, chromium and vanadium, and carbon; nitrides, such as those of silicon, aluminum, boron and titanium; silicides, such as molybdenum disilicide; sulfides, such as cadmium sulfide and zinc sulfide; and so on, as well as mixtures of two or more of them. Among these, preferred are alumina, zirconia, mullite, silicon carbide and silicon nitride. There can be used mixtures of metallic and ceramic powders, for example, wolfram carbide-cobalt, and alumina-aluminium. Such mixtures include blends of metallic powder and ceramic powder, and alloys of metallic powder and ceramic powder. These particulate materials (metallic powders and/or ceramic powders) may contain usual small percentage of impurities or/and additives. For instance, sintering aids, moulding agents and other additives for improving physical properties may be added by blending merely or by surface-coating onto the materials. The average particle size of these particulate materials can vary widely, for instance, ranging from 0.01 to 50 µm (microns), preferably 0.1 to 20 µm (microns). The average particle size may vary somewhat larger range, such as from 0.01 to 100 µm (microns). These particulate materials may be used alone or as a mixture of two or more of such materials of different kinds or different particle sizes. Particulates of less than 0.01µm (micron)diameter are bulky and difficult to handle and result in poor mouldability. Particulates of larger than 50 µm (microns) are of poor sinterability. [Composition] In mouldable composition of the present invention, the component A, having a heat deformation temperature of 130°C or higher, serves for reducing deformation during debinding, as well as imparting flowability to the composition; while components having a heat deformation temperature of less than 130°C are insufficient for reducing deformation during debinding. The component A may be used in such an amount of generally 20 - 100 %, preferably 30 - 60 %, based on the weight of the binder. Using less than 20 % results in moulded bodies of poor strength and difficulty in handling. The component B, having a melting point of usually 30 C - 100°C, serves for heightening the deformation reducing effects and for accelerating debinding, along with improving flowability to facilitate injection moulding. Compounds, having a melting point of more than 100°C, have insufficient deformation reducing effects; and compounds, having a melting point of less than 30, will result in moulded products of lower strength. The component B can be used in such an amount of generally 0 - 80 %, preferably 40 - 70 %, based on the weight of the binder. Using more than 80 % results in moulded products of insufficient strength. The component C may be used in such an amount of generally 0 - 60 %, preferably 0 - 40 %, more preferably 0.1 - 30 %, based on the weight of the binder. Moulded bodies obtained by using more than 60 % of the component C are likely to be deformed. In the mouldable composition of the present invention, the particulate material may be used in such an amount of generally 40 - 70 %, preferably 50 - 60 %, based on the volume of the composition. When the amount of the particulates is more than 70 %, it become difficult to knead them homogeneously with the binder and to injection mould. Using the particulates in smaller than 40 % causes larger deformation of moulded bodies during debinding. In the mouldable compositions, comprising an amine (D), the amounts of (D) and the particulate material can vary widely, and moulding can be attained with use of lower amount of the organic components. For instance, (D) and the particulate material may be used in such amounts of generally 0.1 - 50 % preferably 0.1 - 30 %, and usually 50 -99.5 % preferably 70 - 99.9 %, respectively, based on the weight of the composition. Use of less than 0.1 % of (D) or more than 99.9% of the particulate material results in poor mouldability; and use of more than 50 % of (D) or less than 50% of the particulate material causes reduction of strength of debinded bodies. The amount of the organic binder may be usually 0.5 - 29.9 %. Use of more than 50 % of the binder results in debinded bodies of poor strength. Additional components (plasticizers, lubricants, surfactants and so on) may be used in such an amount as usually used (for instance 0 - 40 %, preferably 0 - 30 %, based on the weight of the composition. [Process] The composition of the invention can be produced by mixing or/and kneading the components. Mixing can be carried out by using conventional mixing means, such as a twin-cylinder mixer, a Henschel mixer, a ball mill or the like, followed by drying if necessary. When using a twin-cylinder mixer, a Henschel mixer or the like, mixing temperature is usually 0 - 100°C preferably 0 - 50°C, and mixing time is generally 10 minutes - 6 hours preferably 30 minutes - 2 hours. Mixing with a ball mill or the like may be carried out under dry or wet conditions, at a temperature of usually 0 - 50°C, for generally 6 - 72 hours preferably 6 - 36 hours. Drying may be done within an air or an atmosphere of an inert gas, at normal pressure or under a reduced pressure, under heating and/or with hot-air. It is preferred drying under non-oxidizing atmosphere (an atmosphere of inert gas, such as nitrogen, argon or the like), or under reduced pressure. Kneading may be carried out under melting by using any of known kneading machines, such as Banbury mixers, plast mills, kneaders, pressure kneaders, roll mills extruders (screw extruders) and the like. Among these, preferred are pressure kneaders and extruders. Kneading temperature is generally 50 - 300°C or higher (such as up to 350°C), preferably 100 - 250°C, more preferably 150 - 200°C, and the temperature may be controled at a constant, increasing or decreasing temperature. Kneading may be carried out within an air or an atmosphere of an inert gas, preferably under non-oxidizing atmosphere (an atmosphere of inert gas, such as nitrogen, argon or the like) or under reduced pressure (in vacuo). Kneading time is usually 10 minutes - 3 hours or longer (such as up to 10 hours), preferably 20 minutes - 2 hours, more preferably 30 minutes - an hour. The components may be mixed or kneaded in any order as far as a homogeneous mixture is obtained. Each component or a mixture may be dried before kneading, if necessary. Suitable kneading methods include, for example, those by charging and kneading all the components at once; those by kneading a part of the components at first, followed by adding thereto the rest and kneading [for instance, those by kneading the organic components at first and then adding thereto the particulate material(s); those by kneading the particulate material(s) with a part of the organic components at first and then adding thereto the rest of the organic components and those by adding the organic or binder components afterwards.] The kneaded compositions may be crushed (or granulated) after cooling, followed by pelletizing if necessary. The mouldable compositions thus obtained can be formed into various moulded bodies (such as sheet, articles of complicated shape, and so on), by known moulding techniques, for example, injection moulding, extrusion moulding, press moulding (such as could press, compression moulding and transfer moulding), and the like. Among these, preferred are injection moulding. Injection moulding may be carried out by means of usual injection moulding machines, such as plunger injection machines and screw injection machines. Moulding conditions may vary according to the shape of moulds and mouldable compositions. In general, moulding pressure is usually 10 - 20,000 Kg/cm², preferably 20 - 10,000 Kg/cm², more preferably 100 - 3000 Kg/cm², most preferably 200 - 2000 Kg/cm², and moulding temperature is generally 20 - 300°C or higher (such as up to 350°C), preferably 50 - 250°C, more preferably 150 - 200°C. Moulding may be carried out under reduced pressure (in vacuo) or under non-oxidizing atmosphere (an atmosphere of inert gas, such as nitrogen, argon or the like). The moulded articles after demoulding are debinded or baked. Debinding or baking process is preferably carried out in an atmosphere of oxidizing gas (such as air), reducing gas (such as hydrogen or carbon mono-oxide) or inert gas (such as nitrogen or argon), under reduced pressure, under normal pressure or under pressure, heating at a rate of usually 1 - 500°C/hr, preferably 1 - 200°C/hr, more preferably 1 - 60°C/hr, most preferably 10 - 40°C/hr to a final temperature of usually 200 - 500°C or higher, preferably 250 - 500°C, more preferably 250 - 350°C, followed by maintaining the above temperature generally for 0 - 10 hours, preferably for 1 - 5 hours. It is preferred to debind under an atmosphere of oxidizing gas, such as air. Moulded bodies comprising the composition of this invention have no or little tendency of deformation and may be debinded as such, without necessity of burying in particulated material or supporting with a setter. Debinding can be accomplished merely by placing the bodies on a shelf board within a debinding furnace. By using an atmosphere-flowable shelf board, the body surface including the underside can be exposed to the atmospheric gas, whereby debinding time can be shortened. Examples of such shelf boards include wire sheets, such as stainless steel wire cloth, and support grid or ceramic formed in the shape of lattice. The product from the debinding or baking step is then sintered to obtain the final product. Sintering can be carried out in an atmosphere of oxidizing gas, reducing gas or inert gas, under reduced pressure, under normal pressure or under pressure, heating to a final temperature of usually 600 - 2500°C, preferably 600 - 2200°C, more preferably 800- 2000°C. Heating rate is usually 50 - 1000° C/hr, preferably 50 - 300°C/hr. The final temperature is maintained generally for 10 minutes - 10 hours, preferably for 30 minutes - 3 hours. In case where the sintering operation is carried out in a vacuum, the degree of vacuum is generally 1.33Pa (10⁻² Torr) or less, preferably 0.133 Pa (10⁻³ Torr) or less. In this invention, there is no necessity of brushing off of the particulate materials used in conventional methods for burying moulded bodies to prevent deformation; and therefore the steps from debinding to sintering according to the invention can be carried out continuously within a same furnace. [Effects] Mouldable compositions of the present invention containing as the binder the resin component (A) having HDT of at least 130°C, particularly those containing (A) in conjunction with the component (B) having a melting point of 30°C - 100°C, can provide debinded articles of excellent appearence free from deformation, even at a longer distance (L) between supporting rods (that is even a larger molded articles), or even when is used such a particulate material as stainless steel which is liable to cause deformation during debinding; while moldable compositions comprising low HDT components such as PP and wax, without said component (A), were apt to be deformed by gravity, particularly in case of stainless steel powder. By using as the component (A) in this invention such a resin as polyacetal which has HDT of at least 150°C and is easily decomposed and using as the component (B) such a low melting component as polyethyleneglycol which is also easily decomposed, debinding can be attained within a short period of time, at lower temperature, in addition to improvement of deformation inhibiting effects. According to the present invention, there can be obtained the following effects: 1) Deformation by gravity can be inhibited, and therefore burying molded bodies in ceramic or metallic powder during debinding and use of holding fixture for shape retention become unneeded. As the results, productivity and precision of products can be improved remarkably. 2) There can be produced debinded bodies without deformation, even molded products of complicated configuration or of oversize, or even products of particulate materials as stainless steel liable to cause deformation during debinding, 3) Needlessness for burying in particulate material and removing therefrom makes it possible to carry out series production from debinding to sintering to improve productivity. 4) There can be attained increase of heating rate and accordingly shortening of debinding time. Moldable compositions, comprising an amine (D), can provide the following effects: 1) Time required for debinding molded bodies can be reduced remarkably. 2) Molding can be attained with use of lower amount of organic components, and therefore gas evolution amount can be reduced. 3) Sintered bodies substantially free from residue of impurities, such as carbon, can be obtained. 4) Sintered bodies of high denseness, substantially free from residue of impurities, such as carbon, can be obtained. 5) Molded articles thus obtained have high relative density and improved strength. By carrying out kneading and/or molding under non-oxidizing atmosphere or in vacuo, thermal decomposition of the binder during kneading or molding can be inhibited, and there can be attained sintered articles of stable or constant qualities even when the compounds are used recycling. In the following examples, parts, ratio and % mean parts by weight, weight ratio and % by weight, respectively, unless otherwise specified. Abbreviated words used in the following examples are as follows : PC : polycarbonate; CO-POM : polyacetal copolymer; POM : polyacetal homopolymer; PSF : polysulfon; PMMA : polymethylmethacrylate; PP : polypropyrene; PBA : polybutyl acrylate; PBM : polybutyl methacrylate; PEG-4000 : polyethylene glycol (MW 4000); PEO : polyethylene oxide; X-PS : Crosslinked polystyrene; X-SA : Crosslinked sutyrene/acrylate copolymer; PW : paraffin wax; DBP : dibutyl phthalate; DOA : di-octadecyl amine; DOA : di-octadecyl amine; DMOA : dimethyl octadecyl amine; ODA : octadecyl amine; E/VAc : ethylene-vinyl acetate copolymer; FEN-8 powder : a mixed powder comprising 92 % of iron powder (average diameter of 4 µm (microns)) and 8% of nickel powder (average diameter of 10µm (microns)); SUS 304 powder : 304 stainless steel powder (average diameter of 10 µm (microns)) HDT : heat distortion temperature; RD : relative density; BSG : bulk specific gravity and MC : micro-cracking. Examples 1 - 4 Mouldable compositions were prepared by combinations of 56 volume % of iron powder (average diameter of 4µm (microns))or SUS 304 powder with each of 4 resins (PC, CO-POM, POM and PSF), having HDT of at least 130°C, as written in Table 1. Each composition was kneaded with a pressure kneader, for about 45 minutes at a temperature between 180°C and 380°C depending on the resin used, followed by heat pressing at 200 - 380°C to form specimens (100mm x 10mm x 4mm) as shown in Fig. 1. Each specimen was put on two supporting rods placed at a certain distance L (10mm, 20mm or 30mm), as shown in Fig.2, followed by heating it within a circulating furnace at a rate of 10° C/hr to a temperature between 300°C and 500°C depending on the resin to decompose and remove at least 90 % of the resin. Degree of deformation of the debinded body was evaluated by the deformed height (h) as shown in Fig.3. Comparative Examples 1 and 2 Example 1 was repeated except using each of 2 resins (PMMA and PP), having HDT of less than 130°C, as written in Table 1. The results were as shown in Table 1. The specimen of Example 1 showed some deformation at longer L, but the specimens of Examples 2, 3 and 4 using resins of at least 150°C of HDT showed no deformation. On the other hand, the specimens of Comparative Examples 1 and 2 resulted in considerable deformation. Examples 5 - 7 (1) Mouldable compositions were prepared by using as the metallic powder either FEN-8 powder or SUS 304 powder and using as the binder the same POM or CO-POM as in Examples 2 and 3 in admixture with PEG-4000 [melting point: 56°C], in accordance with the formulation shown in Table 2. Each composition was kneaded with a pressure kneader, for about 45 minutes at a temperature between 150° C and 180°C, followed by crushing under cooling to obtain an injection mouldable compound. (2) Then, each compound was moulded into the same specimen as in Fig.1, using a injection moulding machine under conditions of the heating cylinder temperature of 150 - 170°C, the mould temperature of 50°C and the injection pressure of 1500 Kg/cm². (3) Each specimen was set in the same manner as in Example 1 and debinded by heating within a circulating furnace at a rate of 20°C/hr to a temperature of 350°C and maintaining the temperature for 2 hrs to attain a debinding ratio of about 98 %, and degree of deformation of the debinded body was evaluated as in Example 1. The debinded specimens showed no deformation, and there was observed no something wrong, such as cracking or blistering. (4) The above debinding process was repeated except that the heating rate was raised to 30°C/hr. Similarly, nothing wrong was observed. Comparative Examples 3 and 4 (1) Injection mouldable compositions were prepared by repeating Example 5(1) except using the same PP as in Comparative Example 2 in admixture with PW [melting point: 58° C], in accordance with the formulation shown in Table 2. (2) Then, Example 5(2) was repeated under injection moulding conditions of the heating cylinder temperature of 150°C, the mould temperature of 50°C and the injection pressure of 1500 Kg/cm², and resulted in a debinding ratio of about 85 % and degree of deformation as written in Table 2. Example 8 Example 7 was repeated except that the moulded specimen was debinded by heating within a circulating furnace set on stainless steel wire cloth so as to exposing the surface including the underside to circulating hot air to shorten the debinding time. There was obtained a debinded body of good appearance with a debinding ratio of about 98 %. Example 9 (1) The debinded body obtained in Example 7 was sintered in a vacuum of 0.133Pa (10⁻³ Torr) or less, at 1250°C for 2 hrs to obtain a sintered body having RD of 95 %. (2) Example 7 was repeated except that a stainless steel powder having average diameter of 4.7 µm (micron) was used as the metallic powder. The resulting debinded body was sintered in the same manner as in the above (1) to obtain a sintered body having RD of 98 %. Examples 10 - 13 Examples 1 - 4 were repeated except using, instead of metallic powder, mixtures of metalic powder and ceramic powder as follows. There were obtained debinded bodies free from deformation. metalic powder : cobalt ceramic powder : wolfram carbide Examples 14 - 16 and Comparative Examples 5 and 6 Mouldable compositions were prepared, according to the formulations as written in Table 5, by mixing the components in a labo plastic mill at 130°C and at 30 rpm rotor revolution and then kneading at 80°C and 50 rpm rotor revolution, followed by crushing the kneaded product to obtain mouldable compositions. Each composition of Examples 14 - 16 and Comparative Examples 5 and 6 was moulded using a screw injection moulding machine under conditions of the injection pressure of 1500 Kg/cm² and the moulding temperature of 150°C to form a injection moulded article, followed by debinding under conditions of the maximum temperature of 400°C and debinding period of 32 hours, and then sintering under conditions of at 1600°C for 2 hours within air in case of alumina, or at 1250°C for 2 hours under reduced pressure in case of stainless steel. Occurrences of thermal deformation and microcracking (hereinafter referred to as MC) and RD of the resulting sintered articles were examined. The results were as shown in Table 6. Composition Example Comparative Ex. 14 15 16 5 6 Thermal deformation NO NO NO Ob Ob MC NO NO NO NO NO RD 99 95 95 99 95 Example 17 A moulded specimen, formed in the same manner as in Example 7, was debinded by heating within a circulating furnace at a rate of 60°C/hr to a temperature of 120°C and then at a rate of 5°C/hr to a temperature of 165°C, followed by maintaining the temperature for 2 hrs to obtain a debinded body having good appearance and a debinding ratio of about 92 %. The resulting debinded body was sintered in the same manner as in Example 9 (1) to obtain a sintered product having RD of 95 %. Example 18 Example 7(1) was repeated except that kneading was carried out under an atmosphere of nitrogen to obtained a kneaded mixture. The kneaded mixture was moulded under the same conditions as Example 7(2), except that moulding was carried out under an atmosphere of nitrogen, and the mixture was moulded recycling 10 times under the same conditions as above. Even after 10 times recycling, there were no substantial reduction of the amount of the binder by thermal decomposition and no change in mouldability. The resulting moulded product was debinded under the same conditions as in Example 17 to obtain a debinded body having good appearance and a debinding ratio of about 92 %. The resulting debinded body was sintered in the same manner as in the above (1) to obtain a sintered product having RD of 95 %. Dimensional accuracy of each part of the sintered product was within tolerance limits of 0.2 %. In case where kneading and moulding were carried out without using an atmosphere of nitrogen, the amount of the binder was reduced about 2 % by thermal decomposition after 10 times recycling, and the resulting sintered product after 10 times recycling showed maximum 0.5 % of dimensional inacuracy as compared with the first (non-recycled) product.

Claims: A mouldable composition comprising a particulate material, comprising a metallic powder and/or ceramic powder, mixed with an organic binder comprising at least one synthetic resin component (A) having a heat deformation temperature of 130°C or higher. A composition according to claim 1 in which the binder further comprises at least one component (B) having a melting point of 30°C to 100°C. A composition according to claim 2 in which component (B) is at least one of a polyether, a wax, a fatty acid, or salt thereof, a fatty amine, and a fatty alcohol. A composition according to claim 3 in which component (B) is a polyether of formula wherein R is a residue of active hydrogen atom-containing compound; R' is H, a mono-valent hydrocarbon radical or acyl radical; Z is an alkylene radical containing 1 - 4 carbon atoms or an alkylene radical containing 2 - 4 carbon atoms having an aryl-substituent; m is an integer between 1 and 8; and n is an integer greater than 1. A composition according to any of claims 2 and 3 in which component (B) is a polyethylene gylcol having a molecular weight of at most 20,000. A composition according to any of claims 2 to 5 which contains component (B) in an amount of 40 to 70 % based on the weight of the binder. A composition according to any preceding claim in which the binder further comprises at least one thermo-plastic component (C), having a heat deformation temperature of 130°C or less. A composition according to claim 7 in which component (C) is at least one thermoplastic resin selected from polyethyleneoxides, polyethylenes, polypropylenes, polyacrylates and polymethacrylates. A composition according to claim 7 in which component (C) is a polyether. A composition according to claim 9 in which component (C) is a polyether of formula wherein R is a residue of active hydrogen atom-containing compound; R' is H, a mono-valent hydrocarbon radical or acyl radical; Z is an alkylene radical containing 1 - 4 carbon atoms or an alkylene radical containing 2 - 4 carbon atoms having an aryl-substituent; m is an integer between 1 and 8; and n is an integer greater than 1. A composition according to any of claims 7 to 9 in which component (C) is a polyethyleneoxide having a molecular weight of at least 100,000. A composition according to any of claims 7 to 11 which contains component (C) in an amount of at most 40% based on the weight of the binder. A composition according to any preceding claim in which component (A) comprises at least one resin selected from polyacetals, polyphenylene-oxides, polysulfones, polycarbonates, polyesters and polyamides. A composition according to any preceding claim, in which a part of component (A) is a powder of at least one resin selected from crosslinked thermoplastic resins and thermosetting resins. A composition according to claim 14 in which the resin powder has an average particle diameter smaller than that of the ceramic powder and/or metallic powder. A composition according to claim 1 in which component (A) is selected from polyamides, polyesters, polysulfones and semi-synthetic resins, and the binder further comprises at least one secondary and/or tertiary amine (D). A composition according to claim 16 in which component (D) is represented by the formula wherein R₁ is a monovalent hydrocarbon radical containing 5 - 30 carbon atoms, R₂ is hydrogen atom or a monovalent hydrocarbon radical containing 1 - 30 carbon atoms, R₃ is hydrogen atom or a monovalent hydrocarbon radical containing 1 - 30 carbon atoms, R₄ is hydrogen atom or a monovalent hydrocarbon radical containing 1 - 5 carbon atoms, Y is an alkylene group containing 2 - 4 carbon atoms, which may have an aryl side group, an n is an integer of 0 - 5. A composition according to claim 16 or 17 which contains component (D) in an amount of 0.1 to 50% based on the weight of the composition. A process for producing a moudable composition according to any of claims 1 - 18 , which comprises kneading under heating the particulate material with the organic binder. A process according to claim 19 in which the kneading is carried out at a temperature lower than the heat deformation temperature of a resin powder which is a part of component (A). A process according to claim 19 or 20 in which the kneading is carried out under a non-oxidizing atmosphere or in vacuo . A process for producing a sintered body, which comprises shaping a body from a mouldable composition obtainable according to a process according to claim 19,20 or 21, heating the shaped body to remove the binder, and sintering the debinded body. A process according to claim 22 in which the shaping is carried out under a non-oxidizing atmosphere or in vacuo . A process according to claim 22 or 23 in which the shaped body is heated under an oxidizing atmosphere. A process according to any of claims 22,23 or 24 in which the shaped body is heated at an atmosphere temperature of at most 250°C to remove the binder. A process according to any of claims 22 to 25 in which the shaped body is heated by placing it on a shelf through which the atmosphere can flow so as to expose the body surface including the underside to the atmosphere. A process according to any of claims 22 to 26 in which the sintering is carried out in vacuo . A process according to claim 27 in which the sintering is carried out at a pressure of 0.133Pa (10⁻³ Torr) or less. A process according to any of claims 22 to 27 which the mouldable composition is shaped into a body by injection moulding.

Inventors: KAWAMOTO KOHSHI, NAKATA YOSHIROH, OSANAGA TAKAHIOR, RYUHGOH JIROH, KAWAMOTO, KOHSHI, NAKATA, YOSHIROH, OSANAGA, TAKAHIOR, RYUHGOH, JIROH
Applicants: SANYO CHEMICAL IND LTD, SANYO CHEMICAL INDUSTRIES LTD.
Application year: 1989
Main classification: B22F1
IPC codes: C08K3, C04B35, B22F1, B22F3