ARTICLE PROVIDED WITH A NON-STICK COATING PROCESS FOR MANUFACTURE THEREOF AND COMPOSITION OF USE IN THE PROCESS

Abstract: An article consists of a substrate whose surface has -OH groups, and of at least one non-stick polymer layer, which article also has applied between the substrate ant the non-stick polymer layer, a layer which is obtained by making an appropriate bifunctional organosilane react with a polyamic-acid precursor of polyamide-imide and with -OH groups of the substrate surface, then drying and converting said polyamic-acid into a polyamide-imide by heating at an appropriately high temperature. The article is particularly of cookware whose substrate is glass or glass-ceramic.

Description: The present invention relates to an article provided with a non-stick coating whose adhesion to the aforesaid article and durability are improved, a manufacturing process for the production of such article and a composition for use in such process. The non-stick coatings used to produce cookware to which food does not stick during cooking are usually based on fluorocarbon polymers (polytetrafluoroethylene (PTFE), FEP, etc...) or on silicones. When the article to be coated is a metallic substrate, such as aluminum or cast iron, gritblasting with an abrasive is usually recommended to ensure adhesion of the coating to the substrate. When the substrate is glass or glass ceramic, gritblasting is not suitable, in particular for a PTFE coating. Because of the porosity of the coating, the polymer/substrate interface is, in use, rapidly exposed to water detergents and grease, so that the adhesion of the coating to the substrate, which is mainly a kind of anchoring, is not sufficient to avoid staining or delamination on the aforesaid interface. The damage is particularly visible when the substrate is a transparent glass, such as Pyrex R brand cookware. In order to improve adhesion of the non-stick coating to the (glass) substrate of the article to be coated it has been proposed in US Patent 3,555,345, to use aminoalkyltrialkoxysilanes as coupling agents applied on the substrate before application of the non-stick coating. Typically the glass substrate is dipped into a dilute solution of the silane coupling agent for a sufficient time (5 min to 4 hrs approximately) to hydrolyse the alkoxy groups and to allow the resulting -OH groups to condense with the silanol (= SiOH) groups existing at the glass surface (cf E.P. PLUEDDEMAN, Silylated surfaces, edited by D.E. Leyden and W. Collins, Gordon and Breach Science Publishers, N.Y., 31, 1978). The aminoalkyl groups have a high (bonding) interaction with the organic coating. However, for the condensation reaction to develop sufficiently, it is necessary for the substrate surface to be free from grease or other organic pollutants. Consequently the surface to be coated has to be thoroughly cleaned with a detergent or an organic solvent (alcohol, acetone), then dried, to ensure that silanol groups are present on the aforesaid surface, which process is, on an industrial scale, a serious inconvenience. Moreover this process is applicable only for glass substrates. There is consequently a need for a process allowing a good adhesion between a non-stick coating and a substrate, and being simpler to operate. It is an object of the present invention to meet this and other requirements. The invention provides a process for the manufacture of an article consisting of a substrate whose surface has -OH groups and of at least one non-stick polymer layer covering at least partially said surface which is characterised in that A - on that part of the substrate surface to be coated, one applies a polyamic-acid precursor of polyamide-imide and an organosilane with two types of functional groups, one of them being reactive with the -OH groups of the substrate surface, the other type being reactive with the polyamic-acid, said polyamic-acid and silane being applied as a mixture in one layer (or one application) or successively, first the silane and secondly the polyamic-acid; B - by heating up to an appropriate temperature, the polyamic-acid is dried and converted into a polyamide-imide; C - finally the non-stick coating(s) is (are) applied. The invention provides also an article consisting of a substrate whose surface has -OH groups and of at least one layer of non-stick polymer covering at least partially said surface, which article is characterised in that in addition it contains between the substrate and the non-stick polymer layer, a layer which is the product resulting from the reaction of an organosilane with two types of functional groups, one of them being able to react with the -OH groups of the substrate surface, and the other type being able to react with polyamic-acid, said reaction with a polyamic-acid precursor of polyamide-imide and with the -OH groups of the substrate surface being allowed to take place then drying and converting the polyamic-acid into a polyamide-imide by heating up to an appropriate temperature. The present invention finally provides a composition useful to improve the adhesion of a non-stick coating with a substrate, said composition characteristically consisting of a polyamic-acid precursor of polyamide-imide, and an organosilane with two types of functional groups, one of them being susceptible to react with the -OH groups of the substrate surface, and the other type being susceptible to react with the polymer-acid. The polyamic-acid precursors will preferably be used, for reasons of safety and antipollution, as aqueous compositions. Such compositions are described in the French Patent 1,460,157 applied for on November 10, 1965 by Imperial Chemical Industries, where further details can be found. In those aqueous compositions, the polyamic-acid is found as a salt either of ammonium or of an organic base. The conversion into a polyamide-imide is usually achieved by heating. An example of a polymeric-acid aqueous composition, commercially available, is code 8470 A XYLAN R from Whitford Plastics Ltd (Brindley 86, Astmoor, Runcorn, Cheshire, WA7 1PF, GB) and Whitford Corporation (Box 507, West Chester, Pa 19381, USA). If desired, polyamic-acid solution in organic solvents could be used. The skilled person will easily find, in the copious published literature devoted to polyamic-acids and to polyamides-imides, details about the preparation of such solutions in an organic solvent. The following two patents are quoted only as examples : British Patent 898,651 and U.S. Patent 3,260,691. The organosilane to be used must have two types of functional groups, One of those types must be reactive with the -OH groups present at the surface of the substrate to be coated, and possibly belonging to silanol groups or to Me-OH groups where Me is a metal. An example of groups of this type is the hydroxy group. Nevertheless, since hydroxysilanes are not very stable, alkoxysilanes are preferred and they have to be hydrolyzed into hydroxysilanes at the time when they are used or a short time before. The other type must be reactive with the polyamic-acid. An example of such groups is the amino group. Among the useful organosilanes are consequently the amino or polyamino-silanes. Among those, the preferred ones are, thus far, gamma-aminopropyltriethoxysilane, gamma-aminopropyltrimethoxysilane and N-(beta-aminoethyl)-gamma-aminopropyltrimethoxysilane, which have furthermore the advantage of being approved by the U.S. F.D.A., which is important when the final articles are intended for cooking usage. The functional silane is more easily used as an aqueous or alcoholic solution, added shortly before use (maximum 1 h) to the aqueous solution of polyamic-acid. By way of guidance, the silane amount can be 1 to 10% by volume of the total composition, preferably 1 to 5. In a variation of the process, the silane and the polyamic-acid can be applied successively on the substrate to be coated. The dry extract of the final composition including resin and pigments, is usually between 10 and 22% by volume. The pigments are those usually included in the commercial polyamic-acid compositions. The polyamic-acid and silane applied to the substrate are heated to an appropriate temperature (for example 100 to 225°C) for a few minutes to dry the layer(s) and to convert the polyamic-acid into a polyamide-imide. A thickness of a few micrometers (for example 5-20 µm) is sufficient for the coating of polyamide-imide modified by silane to fulfill the purpose of the invention. On top of that, the non-stick coating composition can be applied, in conventional way, as one or several successive layers, according to the manufacturer's prescriptions. Examples of suitable coating compositions are those based on PTFE supplied by E.I. Du Pont de Nemours and Co, Wilmington, Delaware, USA, and the coating composition based on silicones supplied by Dow Corning Co. Midland, Michigan, USA. Silane provides a high degree of adhesion, chemical in nature, with the substrate because of the condensation reaction of the -OH groups coming from hydrolysis of the alkoxy groups of the silane, with the -OH groups of the substrate surface. On the other side the amino groups of the silane create chemical bonds with the polyamic-acid and consequently with the final polyamide-imide. Experiments have indicated that the non-stick coatings adhere very well to the polyamide-imide layer modified by silane. The following non-limiting examples are given to better illustrate the invention. In these examples, the following tests have been used. ADHESION TEST Since the usual tests for coatings, such as the cross hatch test and the thumb nail test, are mainly qualitative, we have developed a test designed to quantify the adhesion of the non-stick coating with the substrate. This test, called the plough test, consists in measuring, with a dynamometer, the force F necessary to remove the coating from the substrate by means of a tungsten carbide blade (the plough share), 2.5 mm long, making a 45° angle with the substrate, and on which a load P of 6.5 newtons is applied. To measure the coating adhesion on a substrate, one measures first the friction force F F of the blade on a part of the substrate without non-stick coating, then one measures the force F T necessary to remove the non-stick coating from the substrate when the blade is moved perpendicularly to itself at a speed of 50 µm/s. The difference F T -F F = F measures the adhesion between the non-stick coating and the substrate. The test is made at 25 ± 2°C and a relative humidity 50 ± 5%. An average F is calculated from 9 measurements on three samples 5.8 x 5.8 cm. CHEMICAL DURABILITY ACCELERATED TESTS A first test consists in soaking non-stick coated samples in a solution with 3% by weight of sodium carbonate at 95°C for the indicated time. After this soaking the adhesion force F is measured with the aforesaid adhesion test. A second test, closer to real usage, consists in determining the number, N, of washes in a conventional dishwasher which the article can withstand before any damage appears, such as staining, delamination, peeling of the coating, etc. THERMAL AGEING TEST This test consists in heating non-stick coated samples in an oven at 200 or 250°C for 6 days, then submitting them to the plough test. EXAMPLE 1 In this example, we compare the adhesion of a non-stick coating, about 35 µm thick, consisting of two layers of PTFE applied by gun spraying (two coats system 458Z 62510/455Z 69801 supplied by E.I. Du Pont de Nemours and C°) on clean Pyrex R articles, without any pretreatment, with the adhesion on the same articles previously coated with gamma aminopropyltriethoxysilane (abbreviation τ-APTES) at 1% v/v in 95% ethanol, and with the adhesion of same articles previously coated with an aqueous composition of polyamic-acid (chemical supplied under reference 8470 A XYLAN R ), with 1% v/v of τ-APTES. The silane precoating has been applied by spraying on substrates preheated at 100°C in order to evaporate ethanol. The precoating consisting of the aqueous composition of polyamic-acid and τ-APTES has been sprayed on the glass, then treated at 100°C in order to convert the polyamic-acid into polyamide-imide, which is the precoating in accordance with the invention. The adhesion force (or ploughing force) F is measured on coated samples, before and after thermal ageing at 250°C, and after 1 h and 4 h of chemical ageing in the sodium carbonate solution. The results of said tests are collected in Table I; the standard deviation σ on the values of F in this example is 1.0 N. EXAMPLE 2 The same modus operandi is used as in example 1 except replacement of 1% v/v τ-APTES added to 8470 A XYLAN R by 5% v/v. The ploughing force (F, with σ = 1.0 N) reaches now more than 11.8 N before ageing, (instead of 5.0 N), 9.9 N after thermal ageing at 250°C, and 9.3 and 8.1 N after chemical ageing of 1 h and 4 h respectively. EXAMPLE 3 In this example, we compare the adhesion of a non-stick coating, about 20 µm thick, consisting of a layer of silicone resins (supplied by Dow Corning Co under the codes Q1-2531 and 6-2230) applied by spraying, then cured for 20 min at 250°C on clean Pyrex R substrates, either without any pretreatment, or provided with a precoating of τ-APTES at 1% v/v applied either as a solution in ethanol at 95% sprayed on a substrate preheated at 100°C or as an aqueous solution sprayed on a substrate preheated at 200°C, or provided with a precoating similar to the precoating of example 2 dried at 100°C. The adhesion force F is measured on the coated samples before and after thermal ageing at 200 and 250°C, and after 1/4 h, 1/2 h, 1 h, 2 h and 3 h of chemical ageing in a sodium carbonate solution. The results are given in Table II. EXAMPLE 4 The same modus operandi is used as in example 3, except for the thickness of the silicone non-stick coating, which is about 45 µm and for the concentration of silane in the polyamic-acid which is 5% v/v instead of 1%. The results are given in Table III hereafter. EXAMPLE 5 The same procedure as in example 4 is used, except for the silane concentration in the 8470 A XYLAN R precoating, which is 2.5% v/v of τ-APTES instead of 5%. The ploughing force (F, with σ = 2.0 N) is here 8.9 N before ageing, 9.9 N after thermal ageing at 200°C and 11.8 and 10.8 N after chemical ageing for 1 h and 4 h respectively. EXAMPLE 6 The same procedure as in example 4 is used, except for the silane concentration in the 8470 A XYLAN R precoating, which is 1% v/v of τ-APTES instead of 5%. The ploughing force (F with σ = 2.0 N) is here 8.1 N before ageing, 7.8 N after thermal ageing at 200°C, and 7.7 and 9.7 N after chemical ageing for 1 h and 2 h respectively. EXAMPLE 7 In this example, there is compared the adhesion of a non-stick coating, about 20 µm thick, made by gun spraying of a layer 8830 XYLAN R (a non-stick coating composition based on PTFE supplied by Whitford Plastics Ltd) on Pyrex R glass substrated and curing of said coating at 390°C for 20 min, the substrates being either without any pretreatment, or provided with a precoating consisting of an aqueous composition of polyamic-acid (code 8470 A XYLAN R ) containing 3% v/v of τ-APTES according to the modus operandi described in example 1. The adhesion force F is measured on the samples before and after thermal ageing at 250°C, and after 1 h of chemical ageing. The results are given in Table IV. EXAMPLE 8 The same procedure is used as in example 2, except that the second layer of the PTFE coating made from the composition code 455 Z 69801 from E.I. Du Pont de Nemours and Co. is replaced by the composition code 455 Z 69800 from the same company. The adhesion of the non-stick coating on the substrates is tested with a conventional dishwasher, and evaluated by the number on washing cycles withstood by the coating before being damaged. EXAMPLE 9 In this example there are compared, with the cross hatch test, and the thumb nail test, the adhesion of non-stick coatings based on PTFE made from the compositions code 459 523 and 456 396 supplied by E.I. Du Pont de Nemours and Co. applied on Pyrex R glass cookware, said cookware being either without any precoating, or precoated with an aqueous composition of polyamic-acid (code 8470 A XYLAN R ) containing 5% v/v of N-(beta-aminoethyl)-gamma-aminopropyltrimethoxysilane. The articles provided with this precoating successfully pass both tests after after 1 h of chemical ageing. By contrast the articles without any precoating fail, the PTFE coating being easily removed, after 1 h of chemical, as judged by the thumb nail test. EXAMPLE 10 In this example there are compared the adhesion of non-stick coatings based on PTFE made from compositions code 459 523 and 456 396 supplied by E.I. Du Pont de Nemours and Co. on stainless steel substrates (reference Z 6 CN 18.09) previously degreased with 1,1,1-trichlorethane then dried at 350°C, said substrates being either without any precoating or precoated with an aqueous composition of polyamic-acid (code 8470 A XYLAN R ) containing 3% v/v of τ-APTES. The samples without precoating fail the thumb nail test after 1 h of chemical ageing. The samples precoated according to the invention pass the test, even after 3 h of chemical ageing. The above examples clearly demonstrate that the present invention provides means to substantially improve adhesion and durability of non-stick coatings on a variety of substrates. The process disclosed in this invention is particularly suitable for application at an industrial scale. The procedure described above are only examples, and they could be modified, in particular by substitution of technical equivalents without departing from the scope of the present invention.

Claims: 1. A process for the production of an article consisting of a substrate, whose surface has -OH groups, and at least one layer based on a non-stick polymer, covering at least partially the aforesaid surface, characterized by (A) applying, on that portion of the substrate surface to be coated, a polyamic-acid precursor of polyamide-imide and an organosilane having two types of functional groups, one of them being reactive with the -OH groups of the substrate surface, and the other type being reactive with the polyamic-acid, said polyamic-acid and silane being applied either as a mixture in one layer, or successively in two layers, first silane, then polyamic-acid; (B) drying and converting the polyamic-acid into polyamide-imide by heating at a high enough temperature; and then (C) applying the non-stick layer(s). 2. A process as claimed in claim 1, characterized in that the fact that the functional groups present to react with the -OH groups are either hydroxy groups, or alkoxy groups which will be hydrolyzed into hydroxy groups at the time of use. 3. A process as claimed in claim 1 or claim 2 characterized in that functional groups reactive with the polyamic-acid are amino groups. 4. A process as claimed in any of claims 1 to 3 characterized in that the silane is an amino - or polyamino-alkoxysilane. 5. A process as claimed in claim 4 characterized in that the silane is either gamma-aminopropyltriethoxysilane, or gamma-aminopropyltrimethoxysilane, or N-(beta-aminoethyl)-gamma-aminopropyltrimethoxysilane. 6. A process as claimed in any of claims 1 to 5 characterized in that the proportion of organosilane applied in step (A) is between 1 and 10% of the total volume of the layer(s). 7. A process as claimed in claim 6 characterized in that the proportion of organosilane is between 1 and 5% by volume. 8. A process as claimed in any of claims 1 to 7 characterized in that the non-stick coating is either a silicone or a fluorocarbon polymer. 9. A process as claimed in any of claims 1 to 8 characterized in that the substrate consisting of glass, glass ceramic, ceramic, glazed metal or metal. 10. An article consisting of a substrate whose surface has -OH groups, and of at least one layer of a non-stick polymer covering at least partially said surface, said article characterized by the fact that it contains also, applied between said substrate and said non-stick polymer, a layer obtained by making (A) an organosilane with two types of functional groups, one of them being reactive with the -OH groups of the substrate surface, and the other type being reactive with the polyamic-acid, react with (B) a polyamic-acid precursor of polyamide-imide, and with (C)-OH groups of the substrate surface, then drying and converting the polyamic-acid into a polyamide-imide by heating up to a high enough temperature. 11. An article as claimed in claim 10 characterized in that the silane is an amino - or polyaminoalkoxysilane. 12. An article as claimed in claim 11 characterized in that the silane is either gamma-aminopropyltriethoxysilane, or gamma-aminopropyltrimethoxysilane, or N-(beta-aminoethyl)-gamma-aminopropyltrimethoxysilane. 13. An article as claimed in any of claims 10 to 12 characterized in that the non-stick polymer is a silicone or a fluorocarbon polymer. 14. An article as claimed in any of claims 10 to 13 which is cookware. 15. A composition of use in the process claimed in claim 1, characterized in that it consists of a polyamic-acid precursor of polyamide-imide and an organosilane with two types of functional groups, one of them being reactive with the -OH groups of the substrate surface, and the other type being reactive with the polyamic-acid. 16. A composition as claimed in claim 15 characterized in that the polyamic-acid is in an aqueous composition. 17. A composition as claimed in claim 15 or claim 16 characterized in that the silane is an amino- or polyamino-alkoxysilane. 18. A composition as claimed in claim 17 characterized in that the silane is either gamma-aminopropylethoxysilane, or gamma-aminoproyltrimethoxysilane, or N-(beta-aminoethyl)-gamma-aminopropylmethoxysilane. 19. A composition as claimed in any of claims 15 to 18 characterized in that it contains 1 to 10% silane by volume.

Inventors: CARRE, ALAIN ROBERT EMILE, ROGER, FRANCOISE MARIE MICHELE
Applicants: CORNING GLASS WORKS
Application year: 1989
Main classification: C03C17
IPC codes: B05D7, C03C17, C08K5, C09D179, C08L79