Method of manufacturing ceramic artifact

Abstract: The invention provides a method of making a ceramic artifact by sintering a mixture of particulate zircon and alumina or precursors thereof. The method involves doping the mixture by dispersing a dopant therein prior to sintering. The dopant comprises BaO, SrO, NiO, ZnO or mixtures thereof.

Description: THIS INVENTION relates to a method of manufacturing a structural ceramic artifact. In particular it relates to a method of manufacturing a structural ceramic artifact suitable for use in structural, wear resistant and refractory applications, by sintering a mixture of zircon (ZrSiO 4 ) and alumina (Al 2 O 3 ), to transform them into a product consisting partly or predominantly of zirconia and mullite. Zirconia is ZrO 2 and mullite is usually represented as Al 6 Si 2 O 13 but can also be represented as xAl 2 O 3 .2SiO 2 in which x is 3-4, so that it has a variable alumina content of 70-83% by mass and a variable SiO 2 content of 17-30% by mass. Methods of making refractory ceramic artifacts from relatively coarse mixtures of zircon and alumina are known from Swiss Patent No 354 019 and this possibility is disclosed in published British Patent Application No 2 147 893. These refractory ceramic artifacts, are suitable for use in high temperature applications in blast furnaces, metal melting furnaces, rotary cement furnaces, refuse incineration furnaces, glass bath furnaces or the like. Desirable features of these products are good heat stability, good resistance to corrosion and good resistant to dissociation at elevated temperatures when attacked by molten metals and slags or by infiltrating corrosive gases and alkaline salts; and good resistance to cracking upon heating and cooling in use, with good cold compressive strengths. These refractory ceramics are however not considered to be suitable for use as structural ceramics for engineering applications, and are not stated therein to have this utility, as they are lacking in sufficient hardness, toughness, strength, wear-resistance, abrasion resistance and density. Surprisingly, it has now been found that, by dispersing barium oxide and/or strontium oxide in a relatively fine zircon/alumina starting mixture, advantageous properties for structural uses can be obtained, relating to high hardness, strength, toughness, wear resistance, abrasion-resistance and density, together with suitability for use, if required at high temperatures. Accordingly, the invention provides a method of manufacturing a structural ceramic having a toughness of at least 3,2 MPa.m ½ by sintering a mixture of particulate zircon [ZrSiO 4 ] or a precursor thereof and articulate alumina [Al 2 O 3 ] or a precursor thereof, characterized in that the method includes doping the mixture by dispersing therein a dopant comprising at least one member of the group consisting of barium oxide [BaO], strontium oxide [SrO], and the precursors thereof, prior to sintering, the mixture being formed to have, before it is sintered, a particle size of at most 10 microns, a minimum content of 20% by mass ZrSiO 4 or its precursor [as the oxide], a minimum content of 20% by mass of Al 2 O 3 or its precursor [as the oxide] and a content of 0.01 - 25% by mass of the dopant or its precursor [as the oxide]. The doped mixture may comprise 40-70% by mass of the ZrSiO 4 or its precursor [as the oxide]; the doped mixture may comprise 30-70% by mass of the Al 2 O 3 or its precursor [as the oxide]; and the doped mixture may have 0,5-6% by mass of the dopant [as the oxide] dispersed therein. The dopant may be entirely any one of BaO or SrO, or it may comprise a mixture in any suitable proportions of BaO and SrO. The method may include dispersing in the mixture, prior to the sintering, an additive comprising at least one member of the group consisting of boron oxide [B 2 O 3 ], calcium oxide (CaO], magnesium oxide [MgO], lithium oxide [Li 2 O], titanium dioxide [TiO 2 ] and the precursors thereof. An amount of 0.05 - 10% by mass of the additive [as the oxide] may be dispersed in the mixture, preferably 0.05-5% by mass thereof. As indicated above, although the proportions of the dopants and additives are specified in terms of mass of the oxides of the metals in question, they may naturally be present in the mixture before sintering as the equivalent amounts of the precursors of said oxides, ie compounds such as the carbonates or the hydroxides of said metals, which, during hearing to the sintering temperature, decompose to form said oxides. Similarly, precursors of the Al 2 O 3 starting materials may be used, for example alumina hydrates, eg a monohydrate such as a boehmite, which dehydroyxylates to alumina during heating up to the sintering temperature; precursors of zircon may also be used, provided they decompose or combine to form zircon during the heating up to the sintering temperature. The mixture which is sintered may be formed in any convenient fashion. Thus the mixture may be formed by milling, eg wet milling. In particular the mixture may be formed to have, before it is sintered, an average particle size of at most 3.7 µm, preferably at most 1 µm. The milling may be effected by means of a suitable attrition mill. The milled mixture may then be dried, eg in an oven, or by spray- or freeze-drying. The sintering may be by heating at a rate of 10-600°C/hr, preferably at a rate of 25-300°C/hr, from ambient temperature up to a maximum temperature in the range 1200-1700°C, preferably 1350 - 1500°C, holding the maximum temperature for a period of at least 1 hr, and cooling the sintered material at a rate of 20-500°C/hr, preferably 100-300°C/hr. Heating plateaus or holds may be provided at certain temperatures for certain periods during the heating, at temperatures below the maximum temperature. Any holds or plateaus will usually be provided in the temperature range of 100-1500°C, typically 200-1400°C. These holds will typically last for ½ hr - 5 hrs, more usually 1-2 hrs. The maximum temperature may be held for a period of 1-10 hrs, preferably 2-5 hrs. Plateaus or holds may be provided during the cooling at certain temperatures and for certain periods. In particular, the method may include the step, during the cooling, of holding the temperature constant for a period of at least ½ hr, and optionally up to 5 hrs, preferably 1-2 hrs, at a temperature below the maximum temperature, in the range 1000-1450°C, preferably 1200-1400°C. This hold is for the purpose of annealing the product. This annealing can involve removal of glassy phases therein by crystallization thereof, or it can involve the transformation of unstable crystalline phases. Typically the artifact will be pressed in a green state after drying and prior to sintering. Pressing may be uniaxial and/or isostatic. When pressing is uniaxial it may be to a pressure in the range of 2-200 MPa, preferably 10-50 MPa. When the pressing is isostatic, it may be to a pressure in the range 50-300 MPa, preferably 100-200 MPa. For this purpose a binder such as a suitable wax or polyethylene glycol may be added to the mixture before pressing, eg before milling, in a proportion of 1-10% by mass on a water-free basis, preferably 2-4%. In a particular embodiment of the method, the method may accordingly include the steps, prior to the sintering, of dispersing a binder in the mixture and forming a green artifact from the mixture by pressing at a pressure in the range 10-200 MPa. If necessary, after the drying and before the pressing, the mixture may be screened, after dry milling if necessary, through a screen of at most 600 µm screen size, preferably at most 300 µm screen size. The method may include dispersing, in the mixture, prior to the sintering, at least one additional metal oxide or precursor thereof selected from the group consisting of nickel oxide [NiO], zinc oxide [ZnO] and the precursors thereof. As indicated above, the mixture is preferably formed to have, prior to the sintering, an average particle size of at most 1 µm. The invention will now be described by way of non-limiting illustration, with reference to the accompanying Examples and drawings, which drawings are X-ray diffraction traces of samples of artifacts made in accordance with the Examples. In the Examples described hereunder, the zircon employed was obtained from Ferro Industrial Products, Brakpan, Transvaal Province, Republic of South Africa, as mined by Richards Bay Minerals, Richards Bay, Natal Province, Republic of South Africa. The alumina used was alpha-alumina obtained from Aluminium Company of America, Pittsburgh, Pennsylvania, United States of America. The type of zircon used was that designated F.Z.O. super fine by Ferro Industrial Products and the type of alumina used was that designated Alcoa [Registered Trade Mark] A16SG by Aluminium Company of America. Analyses of the zircon and alumina are set forth hereunder in the following table, Table 1. Constituent Zircon Alumina % by mass % by mass Al 2 O 3 0.12 99.5 ZrO 2 65.9 - P 2 O 5 0.1 - Na 2 O - 0.09 - 0.10 Fe 2 O 3 0.08 0.01 - 0.03 CaO 0.09 - MgO 0.02 - SiO 2 [Total] 32.00 0.025 - 0.07 SiO 2 [Free] 0.20 - H 2 O 0.10 - Loss on ignition 0.20 - In each case the average particle size in microns was determined using a Microtac Particle Size Analyser, Model No. 7995-30 having a measurement range of 0,12 - 42,2 microns, made by Leeds and Northrop Instruments, Sumneytown Pike, North Wales, Pennsylvania, United States of America. The instrument makes use of laser light scattering techniques for particle size estimations. The average particle size of the zircon was found to be 0.66 µm, and that of the alumina to be 0.4 µm. A particle size distribution analyses was carried out on each of the zircon and alumina set forth in Table 1, and results of these analyses are set forth in the following table, Table 2: Equivalent spherical diameter in microns [µm] Cumulative percent by volume finer than stated size Zircon Alumina 0.12 0.0 0.0 0.17 6.6 11.2 0.24 12.4 20.9 0.34 21.4 34.5 0.43 36.0 54.1 0.66 50.5 70.3 1.0 66.6 83.8 1.7 80.8 90.0 2.6 87.7 92.0 3.7 100.0 100.0 Details of Examples are now described. EXAMPLE 1 In this Example the aforegoing zircon and alumina were used as starting materials, together with a strontium oxide [SrO] dopant. The strontium oxide dopant was in fact added in the form of a laboratory grade strontium carbonate precursor [SrCO 3 ] of strontium oxide, obtained from E Merck of Darmstadt, Germany. The zircon, alumina and strontium oxide were sintered in accordance with the equation: 0.04SrO + 3.04Al 2 O 3 + 2.08ZrSiO 4 →Al 6 Si 2 O 13 + 2.08ZrO 2 + 0.04SrAl 2 Si 2 O 8 . The starting materials, ie the zircon, alumina and strontium carbonate were mixed by wet milling in a Netzsch Molinex laboratory attritor. Several samples were prepared, and in each case 275g of stoichiometric mix according to the abovementioned equation was batch mixed employing 1 200 g of 2 mm zirconia bead grinding media and 150 mℓ of demineralized water. As a binder 6 g of polyethylene glycol was employed, obtained from BDH Chemicals of Poole, England. This polyethylene glycol was supplied by BDH Chemicals as having a molecular weight of 200, a density of about 1.12 g/cm 3 and a viscosity at 20°C of 53 x 10 -6 - 63 x 10 -6 m 2 /s (53-63 cS). This binder was added during the wet milling. The milled material was then granulated through a 300 µm sieve after oven drying at 100°C for 3 hrs. Samples of the granulated dried mixture were then uniaxially pressed at 10 MPa pressure and then cold isostatically pressed at 170 MPa to form samples in the form of green artifacts. The samples were then sintered in a Carbolite Kanthal furnace, Model No. RHF 16/10. The sintering was in accordance with three different heating regimes as set forth hereunder. FIRST REGIME According to this regime the samples were heated and cooled respectively at rates of 300C/hr, a hold being provided during heating and a hold being provided at the maximum temperature. Thus, the samples were heated at 300°C/hr from ambient at 30°C up to 500°C, followed by a hold at 500°C of 1 hr, followed by further heating at 300°C/hr up to a maximum of 1490°C. At 1490°C there was a hold of 1 hr , followed by cooling at 300°C down to ambient at 30°C. SECOND REGIME This regime also employed heating and cooling rates of 300°C/hr, but employed two holds during heating and a hold at the maximum temperature. Thus, the samples were heated from 30°C up to 500°C at 300°C/hr, followed by a hold of 1 hr at 500°C. The samples were then heated from 500°C up to 1450°C at 300°C/hr, followed by a hold at 1450°C of 2 hrs. Final heating took place thereafter at 300°C/hr from 1450°C up to 1490°C. At the maximum temperature of 1490°C there was a hold of 1 hr. The samples were then cooled at 300°C/hr from 1490°C down to ambient at 30°C. THIRD REGIME This regime was essentially similar to the first regime, except that when a temperature of 1400°C was reached during the heating, the heating rate was dropped to 50°C/hr, and the hold at the maximum temperature was for only 1 hr. Thus the samples were heated from ambient at 30°C up to 500°C at 300°C/hr, followed by a hold at 500°C of 1 hr. The samples were then heated from 500°C up to 1400°C at 300°C/hr, followed by further heating from 1400°C up to 1490°C at 50°C/hr. There was a hold at the maximum temperature of 1490°C of 1 hr, followed by cooling at 300°C/hr down to 30°C. Various properties of the fired samples were then measured. Density was measured employing Archimedean techniques; strength was measured by a four-point bend test employing a 56 mm span and a load rate of 0.1 mm/min; toughness was measured from the cracks formed by a Vickers indentation device and calculated using the Anstis equation; and hardness was measured by a Vickers indentation device. Results are set forth in the following table, Table 3. Heating regime Density [g/cm 3 ] Strength [MPa] Toughness [MPa.m ½ ] Vickers Hardness [GPa] Young's Modulus [GPa] First 3.86 150 3.5 - 3.8 12.3 220 Second 3.89 210 3.5 - 3.8 12.3 224 Third 3.91 225 3.5 - 3.8 12.3 230 Abrasive wear tests were carried out employing quartz with a mean grit size of 220 µm. The quartz was fired using a sand blasting nozzle at targets constituted by the abovementioned samples, at a rate of 400 g quartz fired over a period of 20 minutes. Compressed air was used as the carrier at a pressure of 160 kPa. Tests were carried out at angles of impingement of the quartz on the samples of 90° and 30° respectively. The end of the sand blasting nozzle was held 50 mm from the target in each case. Two commercially available aluminas were used for comparative purposes, being respectively nominally 90 and 94% aluminas. In each case erosion rate was measured as mg of material lost/kg of quartz fired. The samples made in accordance with the present invention displayed substantially higher wear resistance than the commercially available aluminas, results being set out in the following table, Table 4. Target Material Material Lost [mg/kg] 90° impingement angle 30° impingement angle 90% alumina 74 11 94% alumina 51 12 Samples from first regime 6 4 Samples from second regime 6 3.5 An X-ray diffraction trace was obtained of one of the samples according to this Example, fired according to the third heating regime. This is set forth in Figure 1 of the drawings, as a plot of counts/sec [CPS] against 2 theta Bragg angle. Figure 1 shows that firing of this sample had converted approximately half of the zircon/alumina starting material to zirconia/mullite. EXAMPLE 2 In this Example, zircon, alumina and strontium oxide [the same starting materials as Example 1] were sintered in accordance with the equation: 0.35SrO + 3.3Al 2 O 3 + 2.6ZrSiO 4 → 0.3SrAl 2 Si 2 O 8 + 2.6ZrO 2 + Al 6 Si 2 O 13 The procedure followed in this Example was substantially the same as that described above for Example 1, except that the heating regimes were different, there being once again three separate heating regimes as set forth hereunder. FIRST REGIME According to this regime heating was from 30°C ambient temperature up to 500°C at 300°C/hr followed by a hold at 500°C of 1 hr. Heating then took place from 500°C up to a maximum temperature of 1425°C at 300°C/hr with a hold of 3 hrs at 1425°C. Cooling then took place down to 30°C ambient temperature at a rate of 300°C/hr. SECOND HEATING REGIME This was substantially the same as the first regime except that the maximum temperature where the 3 hr hold took place was at 1450°C. THIRD REGIME This regime was substantially the same as the first and second regimes, except that the maximum temperature at which the 3 hr hold took place was 1475°C. A sample heated in accordance with the second heating regime was found to have a density of 4.12 g/cm 3 ; a strength of 220 MPa; a toughness of 3.2 - 3.7 MPa.m ½ ; a Vickers hardness of 11,5 GPa and a Young's modulus of 257 GPa. X-ray diffraction traces are shown in Figure 2 of the drawings, similar to the trace of Figure 1, for samples heated in accordance with each of the three heating regimes of this Example. These traces show a conversion from a zircon/alumina starting material to a zirconia/mullite artifact. It was noted during the third regime that the sintering was accompanied by liquid exudation at 1475°C. EXAMPLE 3 In this Example a starting material was prepared comprising 10.3 g BaCO 3 , 87.36 g Al 2 O 3 , 104.64 g ZrSiO 4 and 9.96 g polyethylene glycol. The alumina, zircon and polyethylene glycol were as described above for Example 1, and the BaCO 3 was of laboratory grade. The starting mixture was milled in the same fashion as Example 1, employing 1.2 kg of the 2 mm diameter zirconia grinding medium, for 2 hrs and employing 250 mℓ demineralized water. The resultant mix was dried for 16 hrs at 85°C in a conventional drying oven and sieved through a 300 micron mesh screen. Samples were pressed as described in Example 1, and were heated from 30°C ambient temperature at 300°C/hr to respective maximum temperatures of 1450°C, 1475°C, 1500°C and 1550°C, there being in each case a 4 hr hold at the maximum temperature followed by cooling to ambient temperature at 300°C/hr. The samples fired to the various maximum temperatures and cooled to ambient as described above had certain of their mechanical properties tested, and these are set forth in the following table, Table 5. Maximum Firing Temperature [°C] Density [g/cm 3 ] Apparent Porosity [%] Young's Modulus [GPa] Vickers Hardness [GPa] Toughness [MPa/m ½ ] 1450 4.007 0.02 218 11.3 3.7 1475 3.822 0.04 193 9.7 - 1500 3.774 0.02 189 - - 1550 3.746 0.05 185 - - Apparent porosity was measured by the amount of residual water retained in each sample after it has been subjected to a vacuum and them immersed in water. X-ray diffraction traces for the samples heated respectively to 1450°C, 1500°C and 1550°C are shown in Figure 3. These display a transformation from zircon/alumina [1450°C] to zirconia/mullite [1475°C]. The samples fired at 1450°C and 1550°C show no sign of BaO.Al 2 O 3 .2SiO 3 [celsian]. The firings to 1450°C and 1550°C were repeated, except that, during cooling, they were subjected to an annealing hold of 3 hrs at 1300°C. X-ray diffraction traces of the products obtained from these annealed samples are shown in Figure 4, from which it is apparent that one of the crystal forms of celsian appeared, together with a slight reappearance of zircon. This demonstrated the potential for annealing to form crystalline phases from an amorphous glass formed at higher temperatures. EXAMPLE 4 A mixture was prepared comprising 52% and 44% by mass respectively of the abovementioned ZrSiO 4 and Al 2 O 3 with 2% by mass of laboratory grade SrO and 2% by mass of laboratory grade ZnO. This mixture was prepared as described in Example 1. These samples were fired at a heating rate of 300°C/hr from ambient at 30°C up to respective maximum temperatures of 1400°C, 1413°C, 1425°C and 1450°C . All the samples were provided with a 4 hour hold at their maximum temperature, after which they were cooled at 300°C/hr to ambient temperature. Mechanical properties are shown in the following table, Table 6. Maximum Sintering Temperature [°C] Hardness [GPa] Toughness [MPa.m ½ ] 1450 9.8 4.1 1413 11.2 3.2 1400 10.9 3.0 X-ray diffraction traces for the samples fired at 1400°C, 1413°C and 1425°C are shown in Figure 5, and from these X-ray diffraction traces it appears that the reaction from zircon/alumina to zirconia/mullite is substantially complete at 1413°C. EXAMPLE 5 A mixture was made of 126 g of Cera Hydrate [Registered Trade Mark] boehmite obtained from BA Chemicals Plc, Gerrards Cross, Buckinghamshire, England [boehmite is alpha-alumina monohydrate- Al 2 O 3 .H 2 O], together with 2.6 g of laboratory grade Li 2 CO 3 , 119,8 g of the zircon described in Example 1 and 19.7 g of laboratory grade Ba[OH] 2 .8H 2 O. This gave a mixture, in terms of the oxides, of 43.5% by mass Al 2 O 3 , 1% by mass Li 2 O, 51.5% by mass of ZrSiO 4 and 4% by mass BaO. This mixture was prepared in the same fashion as Example 4, and samples thereof were fired to respective maximum temperatures of 1350°C, 1375°C, 1400°C and 1425°C. X-ray diffraction traces of these fired samples are shown in Figure 6, from which it will be noted that the zircon/alumina conversion to zirconia/mullite is virtually complete at 1400°C. A feature of the invention is that relatively low maximum sintering temperatures can be employed, with the attendant major practical advantages, to obtain a product of acceptable toughness, hardness and density. The lowering of the sintering temperature, at least as far as the Examples are concerned, is believed to be made possible by the use of the various dopants employed, which is believed to promote the decomposition of ZrSiO 4 into ZrO 2 and SiO 2 and to inhibit the recombination of these products into ZrSiO 4 upon cooling. Furthermore, these dopants are believed to facilitate the reaction of SiO 2 and Al 2 O 3 resulting in the formation of mullite according to the equation: 3Al 2 O 3 + 2SiO 2 →Al 6 Si 2 O 13 These dopants are believed to enhance densification of the ceramics produced, and to enhance the zircon/alumina reaction, possibly by the presence of transient or permanent liquid phases which may form during sintering, although other mechanisms may be responsible for the utility of the dopants. By varying the nature of the dopant or dopants and the sintering conditions, the reaction may be taken to completion or stopped after partial completion according to the equation: 2ZrSiO 2 + 3Al 2 O 3 → 2ZrO 2 + Al 6 SiO 13 Thus the final ceramic product may consist of zirconia-mullite or zircon-zirconia-alumina-mullite, together with minor phases or glasses, depending on the nature of the dopant used.

Claims: A method of manufacturing a structural ceramic artifact having a toughness of at least 3.2 MPa.m ½ by sintering a mixture of particulate zircon [ZrSiO 4 ] or a precursor thereof and particulate alumina [Al 2 O 3 ] or a precursor thereof, characterised in that the method includes doping the mixture by dispersing therein a dopant comprising at least one member of the group consisting of barium oxide [BaO], strontium oxide [SrO], and the precursors thereof, prior to the sintering, the mixture being formed to have, before it is sintered, a particle size of at most 10 µm, a minimum content of 20% by mass of ZrSiO 4 or its precursor [as the oxide], a minimum content of 20% by mass of Al 2 O 3 or its precursor [as the oxide] and a content of 0.01 - 25% by mass of the dopant or its precursor [as the oxide]. A method as claimed in claim 1, characterised in that the doped mixture comprises 40 - 70% by mass of the ZrSiO 4 or its precursor [as the oxide]. A method as claimed in claim 1 or claim 2, characterised in that the doped mixture comprises 30 - 70% by mass of the Al 2 O 3 or its precursor [as the oxide]. A method as claimed in any one of claims 1 - 3 inclusive, characterised in that the doped mixture has 0.05 - 6% by mass of said dopant [as the oxide] dispersed therein. A method as claimed in any one of the preceding claims, characterised in that it includes dispersing in the mixture, prior to the sintering, an additive comprising at least one member of the group consisting of boron oxide [B 2 O 3 ], calcium oxide [CaO], magnesium oxide [MgO], lithium oxide [Li 2 O], titanium dioxide [TiO 2 ] and the precursors thereof. A method as claimed in claim 5, characterised in that 0,05 - 10% by mass of additive [as the oxide] is dispersed in the mixture. A method as claimed in any one of the preceding claims, characterised in that the mixture is formed to have, before it is sintered, a particle size lower than 3.7 µm. A method as claimed in any one of the preceding claims, characterised in that the sintering is by heating at a rate of 10-600°C/hr from ambient temperature up to a maximum temperature in the range 1200 - 1700°C, holding the maximum temperature for a period of at least one hour, and cooling the sintered material at a rate of 20 - 500°C/hr. A method as claimed in claim 8, characterized in that it includes the step, during the cooling, of holding the temperature constant for period of at least half an hour at a temperature, below the maximum temperature, in the range 1000-1450°C. A method as claimed in any one of the preceding claims, characterized in that it includes the steps, prior to the sintering, of dispersing a binder in the mixture and forming a green artifact from the mixture by pressing at a pressure in the range 2-200 MPa.

Inventors: CARR NEIL STEPHEN, PATERSON ADRIAN WALTER, CARR, NEIL STEPHEN, PATERSON, ADRIAN WALTER
Applicants: CSIR
Application year: 1989
Main classification: C04B35
IPC codes: C04B35