Process of bonding aromatic polyamide fibers to rubber compounds

Abstract: A process of bonding aromatic polyamide fibers to rubber compounds is disclosed, which comprises: a first step of treating fibers with an aqueous mixture comprising a resorcinol/formalin resin and a latex of a polymer containing halogens in amounts of not less than 45% by weight based on the polymer; a second step of treating the fibers with an adhesive composition comprising at least one activating agent selected from polyisocyanate compounds and polyepoxy compounds in an amount of 10-90 parts by weight and an adhesive rubber which is compatible with the rubber in the rubber compound in an amount of 90-10 parts by weight; and a third step of placing the fibers in close contact with the rubber compound and vulcanizing the rubber together with the fibers.

Description: This invention relates to a method of bonding aromatic polyamide fibers to rubber compounds. Industrial rubber products such as automobile tires, rubber hoses, power transmission belts and conveyor belts are normally reinforced with fiber materials. Synthetic fibers are widely used as such reinforcing fiber materials since they are in general superior to natural fibers such as cotton, wool or hemp in properties such as strength, modulus of elasticity, resistance to friction and dimensional stability when being exposed to water or heat. In recent years, polyamide fibers including aliphatic polyamide fibers and aromatic polyamide fibers and polyester fibers are especially preferred as reinforcements among a variety of synthetic fibers. Meanwhile, a variety of methods of bonding fibers to rubber compounds or mixes are known, among which there is a well known method wherein fibers are treated with so-called RFL solutions, namely aqueous mixtures of resorcinol/formalin resins and rubber latices, and placed in contact with rubber compounds, and then the rubber compounds are vulcanized together with the fibers. Resorting to this method, adhesion is attained to a degree between synthetic fibers and rubber compounds. However, adhesion between synthetic fibers and rubber compounds is an important factor to determine the properties of the industrial rubber products. In this regard, since synthetic fibers are poorly wettable to RFL solutions, the adhesion attained is still unsatisfactory. Therefore, a number of methods have heretofore been proposed wherein a variety of modified RFL solutions are employed to improve adhesion between synthetic fibers and rubber compounds. For instance, a method is disclosed in Japanese Patent Laid-open No. 49-96048 in which an RFL solution is used which contains a chlorohydrin rubber latex and a chloroprene rubber latex together with resorcinol/ formalin resin for bonding polyamide fibers to chloroprene rubber mixes. A further method is also diclosed in Japanese Patent Laid-open No. 59-89375 wherein an RFL solution is used which is composed of aqueous mixture of a chloroprene/dichlorobutadiene copolymer latex and resorcinol/formalin resin. On the other side, high saturation or complete saturation rubbers such as high saturation nitrile rubber, ethylene/propylene rubber, chlorinated polyethylene, chlorosulfonated polyethylene, epichlorohydrin rubber or fluorocarbon rubber have come to be used increasingly in various industrial fields in recent years. These rubbers are more poorly bonded to synthetic fibers. Thus, a still further method has been proposed, as disclosed in Japanese Patent Laid-open No. 61-207442, to bond high saturation hydrocarbon rubbers such as hydrogenated nitrile rubbers to fibers wherein an RFL solution is employed which is composed of aqueous mixtures of halogen containing polymers such as epichlorohydrin rubber, chloroprene rubber, chlorosulfonated polyethylene rubber or chlorinated polyethylene rubber, together with resorcinol/formalin resin. EP 0 086 063 discloses the treatment of tensile cords formed of aromatic polyamide fibers for use in drive belts to prevent raveling of the cords at the exposed ends. According to the reference, the fiber cords are provided with a first coating of an epoxy synthetic resin or an isocyanate compound and a second, outer coating comprising a mixture of chloroprene latex, resorcinol and formalin. EP 0 052 315 also discloses the treatment of textile cords formed of aromatic polyamide fibers for use in belt materials. According to the reference, the textile cords are first impregated with a solution of rubber and polyisocyanate and/or polyepoxide in an aliphatic, aromatic or chlorinated hydrocarbon and then with a resorcinol-formaldehyde rubber latex. However, aromatic polyamide fibers are very poorly wettable to RFL solutions due to their more inactive surface than those of aliphatic polyamide fibers or polyester fibers. Accordingly, when vulcanized composite products of aromatic polyamide fibers and rubbers produced by such known methods as above do not stand uses where large shearing force is generated between the rubber and fibers by, for example, bending, compression or elongation under high temperature conditions, since the adhesion therebetween is insufficient to lead to separation failure at interface between the fibers and rubbers. Thus, the composite products are of short life and fail to make the best use of excellent properties that the aromatic polyamide fibers possess. It is, therefore, an object of the invention to obviate the problems involved in the prior art adhesion of aromatic polyamide fibers to rubber compounds, and to provide a process to attain strong and durable adhesion between aromatic polyamide fibers and rubbers. In accordance with the invention, there is provided process of bonding aromatic polyamide fibers to rubber compounds, which comprises: a first step of treating fibers with an aqueous mixture comprising a resorcinol/formalin resin and a latex of a polymer containing halogens in amounts of not less than 45 % by weight based on the polymer; a second step of treating the fibers with an adhesive composition comprising at least one activating agent selected from the group consisting of a polyisocyanate compound and an epoxy compound in amounts of 10-90 parts by weight and an adhesive rubber which is compatible with the rubber in the rubber compound in amounts of 90-10 parts by weight; and a third step of placing the fibers in close contact with the rubber compound and vulcanizing the rubber together with the fibers. Fig. 1 is a graph which shows the relation between chlorine contents of polymers in the adhesive compositions used in accordance with the second process of the invention and adhesion strength of the resultant adherends of natural rubber compounds and aromatic polyamide fiber cords. Fig. 2 is a further graph which shows the relation between solubility parameters of substrate rubbers and adhesion strength between fiber cords and the substrate rubbers; Fig. 3 is a graph which shows the relation between weight ratios of adhesive rubbers/polyisocyanate or polyepoxy compounds and adhesion strength of the resultant adherends; and Fig. 4 is a graph which shows the relation between weight ratios of chlorinated natural rubbers/adhesive rubbers in the adhesive composition used in the second process of the invention and adhesion strength of the resultant adherends. The process of the invention will now be described. The resorcinol/formalin resin used in the first step of the invention is per se already known in the art of adhesion of rubbers and fibers. The resin is initial or low molecular weight condensates which are prepared by condensation of resorcinol and formalin in a molar ratio of resorcinol/formalin in the range from of 1/3 to 3/1 in the presence of a base catalyst. Usually the resin is used as aqueous solutions of 5-80 % by weight in solid content when aqueous mixtures of the resin and rubber latices or RFL solutions are prepared. The polymer which contains halogens in amounts of not less than 45 % weight used in the invention is preferably a chlorine containing polymer, and includes, for example, polyvinylcholoride, chlorinated rubber, chlorinated polyethylene, poly(dichlorobutadiene), copolymers of dichlorobutadiene with at least one of such comonomers as vinyl acetate, vinylchloride, maleic anhydride, acrylic esters, methacrylic esters, acrylonitrile, vinyl ethers, ethylene, propylene or chloroprene. In particular, polyvinyl choloride, chlorinated rubber or their mixtures are preferred. In the first step of the process of the invention, the aromatic polyamide fibers are treated with an aqueous mixture composed of the resorcinol/formalin resin and a latex of the polymer which contains halogens in amounts of not less than 45 % by weight. The aqueous mixture has a high affinity and wettability to aromatic polyamide fibers on account of high polarity of the halogen containing polymers, but also the mixture forms adhesive layers having large cohesive strength on the fibers. The use of polymers containing halogens in amounts of less than 45 % by weight based on the polymers fails to form such cohesive layers on the fibers, and hence such halogen containing polymers are not suitable for use in the process of the invention. In particular, the use of aqueous mixture containing a latex of polymers which contain halogens in amounts of less than 40 % by weight based on the polymer fails to produce strong adhesion between the aromatic polyamide fibers and rubbers. The aqueous mixture used in the first step of the process contains the halogen containing polymer in amounts preferably of 50-1000 parts by weight, more preferably in amounts of 200-800 parts by weight, in relation to 100 parts by weight of the resorcinol/formalin resin. Further, the solid contents of the aqueous mixture is preferably in the range of 5-80 % by weight based on the mixture. In the first step, the fibers are usually dipped into the aqueous mixture, and then dried, preferably under heating at temperatures, for instance, of about 100-270°C, for several minutes to fix the mixture on the fibers. The treatment of the aromatic polyamide fibers only with a latex of this halogen containing polymers fails to provide strong adhesion between the fibers and rubbers. Meanwhile, there is found a tendency that more the halogen content of the halogen containing polymers, the harder the adhesive layers, and the more the amount of the resorcinol/ formalin resin and the halogen containing polymers fixed on the fibers, the smaller the resistance to flexing fatigue. Consequently, it is preferred that the halogen content of the halogen containing polymers is not more than 50 % by weight based on the polymers. It is further preferred that the amount of the resorcinol/formalin resin and the halogen containing polymers fixed on the fibers is as small as possible from the standpoint as above described. However, when the amount is rendered small, the resultant adhesion strength may undesirably vary. Thus, in accordance with the invention, the aromatic polyamide fibers are further treated, as the second step of the process, with a solvent base adhesive composition which comprises at least one activating agent selected from the group consisting of polyisocyanate compounds and polyepoxy compounds in an amount of 10-90 parts by weight, preferably of 20-80 parts by weight, and an adhesive rubber which is compatible with the rubber in the rubber compounds in an amount of 90-10 parts by weight, preferably of 80-20 parts by weight. This second step makes it possible to attain fixed, strong and durable adhesion between the fibers and rubbers without deterioration of resistance to flexing fatigue even when small amounts of the aqueous mixture arefixed on the fibers in the first step. The polyisocyanates used are not specifically limited, but preferred examples include tolylenediisocyanate, m-phenylenediisocyanate, diphenylmethane diisocyanate, hexamethylenediisocyanate and polymethylene polyphenyl polyisocyanate. The polyisocyanates may be in the form of adducts with compounds which have not less than two active hydrogens in the molecule such as polyhydric alcohols exemplified by trimethylolpropane or pentaerythritol, or in the form of blocked polyisocyanates which are obtained by the reaction of the polyisocyanates with blocking agents such as phenols, tertiary alcohols or secondary amines. The polyepoxy compounds used include, for example, reaction products of polyhydric compounds with halogen containing epoxide compounds such as epichlorohydrin. There may be mentioned as such polyhydric compounds, for example, polyhydric alcohols such as ethylene glycol, glycerine, sorbitol or pentaerythritol; polyalkylene glycols such as polyethylene glycol or polypropylene glycol; or polyfunctional phenols such as resorcinol or bis(4-hydroxyphenyl)dimethylethane; or phenol resins such as phenol/formalin resins or resorcinol/formalin resins. The activating agent used here is resinated during the vulcanization of the rubber compounds with the fibers, thereby to improve cohesion of the adhesive layers formed, but also to form strong adhesive layers by the reaction of methylol groups in the resorcinol/formalin resin used. As the adhesive rubber which is compatible to the rubber in the rubber compound, there may be used usually the same unvulcanized rubber as the rubber species in the rubber compound or unvulcanized rubbers which have chemical structures similar to the rubber species in the rubber compound. However, rubber species which are different in chemical structures from the rubber species in the rubber compound may be used as an adhesive rubber provided that the adhesive rubber is close to the rubber species in polarity or more specifically in solubility parameter, since such adhesive rubbers are compatible to the substrate rubber species in the rubber compounds. The adhesive composition usually contains suitable vulcanizing agent depending upon the adhesive rubber used. A variety of methods are known to calculate the solubility parameters, among which is representative a Small's method which is described in detail in J. Paint Technol., 42 , 76 (1970) under the title of New Values of the Solubility Parameters from Vapor Pressure Data. In the invention, there may be preferably used, as an adhesive rubber, such a rubber as has a solubility parameter in the range of from the solubility parameter of the rubber in the rubber compound plus one to the solubility parameter of the rubber in the rubber compound minus one. The use of rubber species of solubility parameters outside the above specified range as an adhesive rubber fails to produce strong adhesion between the fibers and the rubbers since the adhesive rubber is too far from the substrate rubber species in the rubber compound in the polarity, and therefore very poorly adhesive thereto. When a rubber which contains no halogens therein such as natural rubber, styrene/butadiene rubber or acrylonitrile/ butadiene rubber is used a first adhesive rubber, it is preferred that the adhesive composition further contains chlorinated natural rubber as a second adhesive rubber in amounts of 10-1000 parts by weight in relation to 100 parts by weight of the first adhesive rubber used in the composition. The incorporation of the chlorinated natural rubber into the adhesive composition as an addtional adhesive rubber improves the compatibility of the adhesive composition to the mixture of the resorcinol/formalin resin and the halogen containing polymers, and raises cohesion of the resultant adhesive layers, thereby to successfully produce very strong and durable adhesion between the fibers and rubbers. The adhesive composition is used in the form of solutions in such organic solvents. The solvent used is not specifically limited, but there may be preferably used aromatic hydrocarbons such as benzene, xylene or toluene, aliphatic ketones such as methyl ethyl ketone or methyl isobutyl ketone, alkyl esters of lower aliphatic carboxylic acids, especially acetic acid, such as ethyl acetate or amyl acetate. It is preferred that the adhesive composition contains solids in amounts of 10-50 % by weight. In the second step of the process of the invention, the fibers are usually dipped into the solvent base adhesive composition, and then dried, preferably under heating at temperatures, for instance, of about 100-270°C, for several minutes to fix the composition on the fibers. In the process of the invention, the aromatic polyamide fibers may be pretreated with at least one activating agent selected from the group consisting of polyisocyanate compounds and polyepoxy compounds prior to the first step. The same polyisocyanate or polyepoxy compounds as those hereinbefore mentioned may be used as the activating agent in the pretreatment. The organic solvent used may also be the same as those mentioned hereinbefore. The content of the activating agent in the activating solution is usually in the range of 10-50 % by weight. The pretreatment of the fibers as above set forth activates the surfaces of the aromatic polyamide fibers to improve the wettability of the fibers to the aqueous mixture of resorcinol/formlin resin and the halogen containing polymers applied to the fibers in the first step. Further, the activating agent fixed on the fibers reacts with methylol groups of the resorcinol/formalin resin applied to the fibers in the first step, or is resinated during the vulcanization of the rubber together with the fibers, thereby to form strong and durable adhesion between the fibers and the rubbers. The fibers are finally placed in close contact with rubber compounds or mixes in the third step, and the rubber compounds are vulcanized together with the fibers in conventional manners known in the rubbers used. The process of the invention is not specifically limited to rubbers to which the aromatic polyamide fibers are bonded, but is suitably applicable to such rubbers as natural rubber, styrene/butadiene rubber, chloroprene rubber, acrylonitrile/butadiene rubber, ethylene/propylene rubber, chlorinated polyethylene rubber, chlorosulfonated polyethylene rubber, epichlorohydrin rubber or fluorocarbon rubber. The process is most suitably applied to adhesion of the aromatic polyamide fibers to natural rubber, styrene/butadiene rubber, chloroprene rubber or acrylonitrile/butadiene rubber, however. The rubber compounds used may of course contain known rubber chemicals or additives depending upon the individual rubbers used. There may be mentioned as such chemicals or additives, for example, reinforcing fillers including carbon black or silica, softening agents, antioxidants, plasticizers, vucanization accelerators, processing aids and the like. The process of the invention thus provides aromatic polyamide fibers-rubber adherend composites which have strong and durable adhesion therebetween, and the process of the invention is suitably employed in the production of dynamic rubber products such as automobile tires, transmission belts or conveyor belts. The invention will now be described with reference to examples, however, the invention is not limited to the examples. In the examples, parts and percents are by weight unless otherwise specified. In the examples, the following rubbers and latices were used. Polyvinyl chloride latex (PVC latex): Zeon 150X50 (Nippon Zeon K.K.) having a solid content of 48 % by weight. The polyvinyl chloride had a chlorine content of 57 % by weight and a solubility parameter of 9.7. Chlorinated rubber latex: An amount of 30 parts by weight of chlorinated rubber CR-150 (Asahi Denka K.K.) having a chlorine content of 65 % by weight and a solubility parameter of 9.5 was added to 60 parts by weight of toluene. The resultant solution was added to a mixture of 100 parts by weight of water and 1.4 parts by weight of an emulsifier, followed by stirring with a homomixer, to provide a latex having a solid content of 20 % by weight. Chloroprene rubber latex: LV-60 (Denki Kagaku Kogyo K.K.) having a solid content of 50 % by weight. The chloroprene had a chlorine content of 41 % by weight and a solubility parameter of 9.2. Chlorosulfonated polyethylene rubber latex: Chlorosulfonated polyethylene rubber latex (Sumitomo Seika K.K.) having a solid content of 40 % by weight. The chlorosulfonated polyethylene had a chlorine content of 25 % by weight and a solubility parameter of 9.1. Natural rubber latex: The latex of a solid content of 60 % by weight and a solubility parameter of 8.3. Styrene/butadiene rubber latex (SBR latex): Chloroprene rubber: Neoprene WRT (Showa Denko K.K.) having a solubility parameter of 9.2. Polyisocyanate: Millionate MR (polymethylene polyphenyl polyisocyanate, Nippon Polyurethane Kogyo K.K.) or PAPI (Kasei Upjohn K.K.) Polyepoxy compound: Denacol EX 313 (glycerol polyglycidyl ether, Nagase Kasei Kogyo K.K.) The abbreviations of adhesion failure stand for the followings. F-A: Interface failure between fibers and adhesive A-R: Interface failure between adhesive and rubber R : Rubber cohesive failure EXAMPLE 1 Aromatic polyamide fiber cords ("Technola" by Teijin K.K., 1500D/1x3) were dipped into an aqueous mixture (a) as shown in the Table 1, and then dried at 200°C for two minutes. Then, in the Example A and Comparative C, as shown in the Table 1, the cords were dipped into an organic solvent base adhesive composition (b) of which ingredients are shown in the Table 1, and dried at 200°C for two minutes. The thus treated fiber cords were placed in close contact with the natural rubber compound 1, and the rubber compound was vulcanized at 150°C for 30 minutes. Unvalcunized Rubber Compound 1 (parts by weight) Natural rubber 100 Zinc oxide 5 Stearic acid 2 Sulfur 2.5 FEF carbon black 45 Process oil 5 N-hydroxydiethylene-2-benzothiazyl sulfenamide 1 2,2,4-trimethyl-1,2-dihydroquinoline 0.2 In the Comparative Example B, the fiber cords were treated with the aqueous mixture (a), but not with the adhesive composition (b), and vulcanized with the rubber compound 1. The resultant adherends were subjected to measurement of 180° peeling adhesion strength between the fiber cords and the rubber at a peeling rate of 100 mm per minute by an adhesion test. The results are shown in the Table 1. Example Comparative A B C Aqueous Mixture (a) Resorcinol 5.0 5.0 5.0 Formalin 3.1 3.1 3.1 PVC latex 61.6 61.6 - Natural rubber latex - - 61.6 Water 84.3 84.3 84.3 Adhesive Composition (b) Natural rubber 7.0 - 7.0 Millionate MR 7.0 - - Carbon black 3.0 - 3.0 Toluene 83.0 - 83.0 Adhesion Strength (Kg/cord) 13.7 2.7 5.1 Adhesion Failure R A-R F-A EXAMPLE 2 The same aromatic polyamide fiber cords as in the Example 1 were dipped into an aqueous mixture (a) as shown in the Table 2, and then dried at 200°C for two minutes. The fiber cords were then dipped in the same adhesive composition(b) as in the Example A in the Table 1, and dried at 200°C for two minutes. The fiber cords were then placed in close contact with the natural rubber compound 1, and the rubber compound was vulcanized at 150°C for 30 minutes. The resultant adherends were subjected to measurement of 180° peeling adhesion strength between the fiber cords and the rubber at a peeling rate of 100 mm per minute by an adhesion test. The results are shown in the Table 2. Based on the results of the Examples A and D, and the Comparative Examples E, F and G, the relation between the chlorine contents of the polymers in the aqueous mixture (a) and the peeling adhesion strength in the resultant adherends is illustrated in Fig. 1. As apparent, when the aromatic polyamide fiber cords are first treated with an aqueous mixture or an RFL solution containing a polyvinyl chloride latex or a chlorinated rubber latex, and then with an adhesive composition containing natural rubber as an adhesive rubber and a polyisocyanate as an activating agent, followed by vulcanizing with a rubber compound, to provide a natural rubber-fiber cords composite having strong adhesion therebetween. EXAMPLE 3 The same aromatic polyamide fiber cords as in the Example 1 were dipped into an aqueous mixture (a) as shown in the Table 3, and then dried at 200°C for two minutes. The fiber cords were then dipped in an adhesive composition (b) as shown in the Table 3, and dried at 200°C for two minutes. The fiber cords were then placed in close contact with the natural rubber compound 1, chloroprene rubber compound 2 or nitrile rubber compound 3 as hereinbefore or below described, and the rubber compounds were vulcanized at 150°C for 30 minutes. Unvulcanized Rubber Compound 2 (parts by weight) Neoprene WRT 100 Magnesium oxide 4 Zinc oxide 5 SFR carbon black 40 2-mercaptoimidazoline 0.5 N,N'-di-β-naphthyl-p-phenylenediamine 0.5 2,2,4-trimethyl-1,2-dihydroquinoline 0.5 Process oil 10 Stearic acid 0.5 Unvulcanized Rubber Compound 3 (parts by weight) Nitrile rubber 100 Zinc oxide No. 1 5 Stearic acid 1 Sulfur 0.5 SFR carbon black 40 Tetramethylthiuram disulfide 2 Mercaptobenzothiazol 0.5 The resultant adherends were subjected to measurement of 180° peeling adhesion strength between the fiber cords and the rubber at a peeling rate of 100 mm per minute by an adhesion test. The results are shown in the Table 3. Example A H Aqueous Mixture (a) Resorcinol 5.0 5.0 Formalin 3.1 3.1 PVC latex 61.6 61.6 Water 84.3 84.3 Adhesive Composition (b) Natural rubber 7.0 - Nitrile rubber - 7.0 Millionate MR 7.0 7.0 Carbon black 3.0 3.0 Toluene 83.0 83.0 Unvulcanized Rubber Compound 1 Adhesion Strength (Kg/cord) 13.7 2.5 Adhesion Failure R A-R Unvulcanized Rubber Compound 2 Adhesion Strength (Kg/cord) 10.4 12.3 Adhesion Failure R R Unvulcanized Rubber Compound 3 Adhesion Strength (Kg/cord) 2.3 15.3 Adhesion Failure A-R R Based on the results with the adherends which were obtained in the Examples A and H using adhesive compositions which contained natural rubber or nitrile rubber, the relation between the solubility parameters of the substrate rubber or the rubber in the rubber compounds and adhesion strength between the fiber cords and the rubbers is illustrated in Fig. 2. In the Example A, the fiber cords were treated with an aqueous mixture (a) and then with an adhesive composition (b) which contained natural rubber having a solubility parameter of 8.3. Thus, the compound 1 of natural rubber is bonded strongly to the fiber cords. Similarly, since natural rubber has a solubility parameter close to that of chloroprene rubber, the difference therebetween being 0.9, the chloroprene rubber compound 2 is firmly bonded to the fiber cords. On the contrary, nitrile rubber has a solubility parameter of 9.7, more than that of the natural rubber as an adhesive rubber by 1.4, so that no strong adhesion is obtained between the nitrile rubber compound 3 and the fiber cords. In the Example H, the fiber cords were treated with an adhesive composition containing a nitrile rubber having a solubility parameter of 9.7, while natural rubber has a solubility parameter of 8.3, the difference therebetween being 1.4. Therefore, no strong adhesion was attained between the natural rubber compound 1 and the fiber cords. However, chloroprene rubber has a solubility parameter of 9.2, close to that of the nitrile rubber, so that there is obtained strong adhesion between the chloprene rubber compound 2 and the fiber cords. Of course, the nitrite rubber compound 3 is firmly bonded to the fiber cords. EXAMPLE 4 The same aromatic polyamide fiber cords as in the Example 1 were dipped into an aqueous mixture (a) as shown in the Table 4, and then dried at 200°C for two minutes. The fiber cords were then dipped in an adhesive composition (b) as shown in the Table 4, and dried at 200°C for two minutes. The fiber cords were then placed in close contact with the natural rubber compound 1, and the rubber compound was vulcanized at 150°C for 30 minutes. The resultant adherends were subjected to measurement of 180° peeling adhesion strength between the fiber cords and the rubber at a peeling rate of 100 mm per minute by an adhesion test. The results are shown in the Table 4. Further, the fiber cords were treated with adhesive compositions (b) having varied weight ratios of the adhesive rubbers/polyisocyanate or polyepoxy compounds used, and otherwise in the same manner as above, and the fiber cords were vulcanized with the natural rubber compound 1. Fig. 3 illustrates the relation between the weight ratios of adhesive rubbers/polyisocyanate or polyepoxy compounds and the adhesion strength of the resultant adherends. Example A I Aqueous Mixture (a) Resorcinol 5.0 5.0 Formalin 3.1 3.1 PVC latex 61.6 61.6 Water 84.3 84.3 Adhesive Composition (b) Natural rubber 7.0 7.0 Millionate MR 7.0 - Polyepoxy compound - 7.0 Carbon black 3.0 3.0 Toluene 83.0 83.0 Adhesion Strength (Kg/cord) 13.7 13.1 Adhesion Failure R R EXAMPLE 5 The same aromatic polyamide fiber cords as in the Example 1 were dipped into an aqueous mixture (a) as shown in the Example A in the Table 1, and then dried at 200°C for two minutes. The fiber cords were then dipped in adhesive compositions (b) containing chlorinated natural rubber in varied amounts in relation to natural rubber, and dried at 200°C for two minutes. The fiber cords were then placed in close contact with the natural rubber compound 1, and the rubber compound was vulcanized at 150°C for 30 minutes. The resultant adherends were subjected to measurement of 180° peeling adhesion strength between the fiber cords and the rubber at a peeling rate of 100 mm per minute by an adhesion test. The results are shown in Fig. 4. EXAMPLE 6 The same aromatic polyamide fiber cords as in the Example 1 were dipped into an activation solution (c) as shown in the Table 5, and then dried at 200°C for two minutes. The fiber cords were then treated in the same manner as in the Example A of the Example 1 with the aqueous solution (a) and the adhesive composition (b) in succession. The fiber cords were then placed in close contact with the natural rubber compound 1, and the rubber compound was vulcanized at 150°C for 30 minutes. The resultant adherends were subjected to measurement of 180° peeling adhesion strength between the fiber cords and the rubber at a peeling rate of 100 mm per minute by an adhesion test. The results are shown in the Table 5. Example X Y Z Activation Solution (c) PAPI 9.0 - 4.5 Polyepoxy compound - 9.0 4.5 10% NaOH solution - 1.0 0.5 Toluene 141 140 140.5 Adhesion Strength (Kg/cord) 13.7 14.7 13.1 Adhesion Failure R R R

Claims: A process of bonding aromatic polyamide fibers to rubber compounds which comprises: a first step of treating fibers with an aqueous mixture comprising a resorcinol/formalin resin and a latex of a polymer containing halogens in amounts of not less than 45% by weight based on the polymer; a second step of treating the fibers with an adhesive composition comprising at least one activating agent selected from polyisocyanate compounds and polyepoxy compounds in an amount of 10-90 parts by weight and an adhesive rubber which is compatible with the rubber in the rubber compound in an amount of 90-10 parts by weight; and a third step of placing the fibers in close contact with the rubber compound and vulcanizing the rubber together with the fibers. A process according to claim 1 wherein the polymer is a chlorine containing polymer. A process according to claim 1 or 2 wherein the polymer is at least one of polyvinyl chloride, chlorinated rubber, chlorinated polyethylene, poly(dichlorobutadiene) and a copolymer of dichlorobutadiene. A process according to any of claims 1 to 3 wherein the aqueous mixture contains the polymer in an amount of 50-1000 parts by weight in relation to 100 parts by weight of the resorcinol/formalin resin. A process according to any preceding claim wherein the aqueous mixture contains 5-80% by weight solids. A process according to any preceding claim wherein the adhesive rubber has a solubility parameter in the range of from the solubility parameter of the rubber in the rubber compound plus one to the solubility parameter of the rubber in the rubber compound minus one. A process according to any preceding claim wherein the adhesive composition is a solution in organic solvents. A process according to claim 7 wherein the solution contains solids in an amount of 10-50% by weight. A process according to any preceding claim wherein the adhesive composition contains at least one first adhesive rubber which contains no halogens therein and additionally chlorinated rubber as a second adhesive rubber in an amount of 10-1000 parts by weight in relation to 100 parts by weight of the first adhesive rubber. A process according to claim 9 wherein the first adhesive rubber is at least one cf natural rubber, styrene/butadiene rubber and acrylonitrile/butadiene rubber. A process according to any preceding claim wherein the fibers are pretreated with at least one activating agent selected from polyisoyanates and polyepoxy compounds.

Inventors: FUJIWARA AKINORI, HATA KATSUHIKO, FUJIWARA, AKINORI, HATA, KATSUHIKO, FUJIWARA, AKINORI, C/O BANDO CHEMICAL IND., LTD., Hata, Katsuhiko, c/o Bando Chemical Ind., Ltd.
Applicants: BANDO CHEMICAL IND, BANDO CHEMICAL INDUSTRIES, LTD.
Application year: 1989
Main classification: C08J5
IPC codes: C08J5