AN ABSORBENT FOR CHLOROSILANE COMPOUND

Abstract: When a liquid chlorosilane compound inadvertently runs out of a container, the liquid must be disposed by absorbing using an absorbent since chlorosilane compounds are generally very dan­ gerous and toxic. Instead of dry sand conventionally used as an ab­ sorbent in such a purpose, the invention purposes that a very ef­ ficient effect of absorption can be obtained by using a silica-, sili­ ca/alumina-based porous ceramic material or a mixture of them as an absorbent without gas evolution in the liquid and with little temperature increase of the liquid when the absorbent material has a specified content of silica or silica/alumina and a pore diam­ eter distribution.

Description: The present invention relates to an absorbent of chlorosilane compounds or, more particularly, to an absorbent material having a capacity of absorbing a large volume of chlorosilane compounds without the problem of Producing toxic gases by the reaction with the chlorosilane compound. From GB-A-1 362 331 a process is known, in which a chromatographic adsorbent is produced from finely dispersed non-porous silica for use as an active packing in chromatographic columns and as a support of stationary phases in gas and liquid chromatography. According to an example of the known process the production of adsorbent is started from silica having a specific surface area between 35 and 380 m²/g, which is mixed with water to form an aqueous suspension. The suspension is dried in a spraying furnace at 400° C to form silica xerogel, which is particulated and calcinated at 550° C and thereafter is hydrothermally treated in an autoclave at 220° C under 20 atm pressure for 96 hours. Finally, the xerogel is dried at 120° C and calcinated in air at 900° C for 24 hours, whereupon the absorbent is screened to separate the 0.1 to 1 mm fraction. The yield of the final product is 98 % by weight of the starting silica, this product having an avarage pore diameter of 0.15 µm and a pore volume of 1.68 cm³/g. As a class of important starting materials, consumption of chlorosilane compounds is rapidly increasing year by year in various industries for the production of silicones, semiconductors silicon, synthetic quartz glass and the like. Chlorosilane compounds in general, however, are chemically very unstable and must be handled with utmost care in order to prevent hazardous troubles. When a chlorosilane compound is exposed to atmospheric air by being leaked out of a tightly stoppered container in which the compound is stored, for example, the chlorosilane compound is readily reacted with the moisture in the atmospheric air and rapidly hydrolyzed to produce toxic and corrosive hydrogen chloride gas and, sometimes, inflammable and explosive hydrogen gas. In addition, chlorosilane compounds per se generally have a low flash point and are very inflammable so that handling of chlorosilane compounds is always accompanied by a danger of fire and explosion and, once a chlorosilane compound has caught fire, the fire can be extinguished only with great difficulties. In this regard, it is important for safety that a chlorosilane compound running out of a container is immediately absorbed in an absorbent material in order to be prevented from spreading. The most conventional and traditional absorbent material used in the prior art for the above mentioned purpose of absorption is dry sand which, however, is not free from the disadvantages that the amount of the chlorosilane compound which can be absorbed by a unit weight of dry sand is relatively small and that impurities contained in natural sand may sometimes react with the chlorosilane compound to produce toxic gases. SUMMARY Of THE INVENTION The objective underlying the present invention is to suggest a most efficient absorbent of and a method for efficiently absorbing a chlorosilane compound eventually running out of a container, whereby a volume of a chlorosilane compound will be quickly and entirely absorbed by relatively small amounts of the absorbent, and whereby the danger of fire and explosion and of production of toxic gases is avoided. Thus, the absorbent material of a chlorosilane compound provided by the invention is a silica-or silica/alumina-based porous ceramic material or a mixture of them, powdery or granular, the pores of which have a pore diameter in the range from 0.1 to 100 µm, and the surface of which is rendered hydrophobic by treatment with an organosilane compound or with an organopolysiloxane compound, the content of silicon dioxide SiO₂ and aluminum oxide A1₂O₃ in the silica/alumina-based material being at least 90% by weight. The method of the present invention for absorbing a chlorosilane compound by use of an absorbent material contacted with the chlorosilane compound comprises using as the absorbent, a silica- or silica/alumina-based porous ceramic material or a mixture of them, of which the pores have a pore diameter in the range from 0.1 to 100 µm, the content of silicon dioxide SiO₂ in the silica-based material being at least 80% by weight, and the total content of silicon dioxide SiO₂ and aluminum oxide Al₂O₃ in the silica/alumina-based material being at least 90% by weight. It is further preferable, when the surface of the absorbent has been rendered hydrophobic by treatment with an organosilane compound or an organopolysiloxane compound. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The chlorosilane compound implied in the present invention includes methyl chlorosilanes and phenyl chlorosilanes used in large quantities in recent years as a starting material in the manufacture of silicones, high-purity semiconductors silicon, synthetic quartz glass and the like and is represented by the general formula R a SiH b Cl c , in which R is a methyl group or phenyl group, the subscripts a and b are each zero, 1, 2 or 3 and the subscript c is a positive integer not exceeding 4 with the proviso that a + b + c = 4. Examples of typical chlorosilane compounds include trichlorosilane, silicon tetrachloride, trimethyl chlorosilane, methyl dichlorosilane, dimethyl dichlorosilane, methyl trichlorosilane, phenyl trichlorosilane, diphenyl dichlorosilane and the like. These possible since moisture contained therein causes hydrolysis of the chlorosilane compound. One of the suitable silica-based materials to meet the above described requirements is a natural amorphous silica sand as a kind of geyserite or siliceous sinter occurring in Japan and sold under a tradename of Silton 3S which should be calcined and purified prior to use as an absorbent. The powdery silica-based material thus obtained typically contains 89.1% by weight of silicon dioxide and a porosity of 70% with a true density of 2.3 g/cm³. When a silica/alumina-based porous powdery material is desired, the above mentioned Silton 3S is uniformly blended with kaolin together with water and the blend is dried, calcined, pulverized and finally classified relative to the particle size using a sieve. The thus prepared porous silica/alumina-based powdery material typically contains 68% by weight of silicon dioxide and 23% by weight of aluminum oxide and has a porosity of 80%. It is preferable that the above mentioned porous powdery or granular ceramic material has a surface rendered hydrophobic by a treatment with an organosilane compound or an organopolysiloxane compound. When a chlorosilane compound inadvertently runs out of a container and is spread over the ground or floor of a plant in which the compound is under handling, the absorbent material of the invention is sprinkled in a sufficiently large amount on the pool of the chlorosilane compound on the ground or floor so that the liquid chlorosilane compound is absorbed into the numberless pores of the absorbent material and prevented from vaporization and contacting with the atmospher ic air without reacting with the absorbent material. Therefore, not only vaporization of the chlorosilane compounds per se but also formation of toxic gases such as hydrogen chloride and inflammable gases such as hydrogen can efficiently be prevented thereby. It is of course that the danger of fire or explosion can be minimized in this manner even when the chlorosilane compound is highly inflammable. The above described advantages can be fully exhibited only when the pore diameter of the porous absorbent material is within the above mentioned range. Otherwise, it is unavoidable that a considerably large quantity of heat is evolved by way of the adsorption, which predominantly occurs for the pore diameter less than 0.1 µm across, of a chlorosilane compound in the porous adsorbent material. There are usually known silica gel and alumina gel are excellent adsorbents being 0.001 µm to 0.1 µm in the pore diameter. Silica gel of the pore diameter of 0.001 µm to 0.05 µm added to a liquid trichlorosilane, the adsorption heat is so great that the temperature rapidly increase to the extent that the liquid eventually comes to boil up, vaporize and as a result cannot be confined from the ambient air through the strong adsorption effect. In this regard, the absorbent material of the invention can be used for the purpose of fire extinguishment by sprinkling it over a chlorosilane compound in burning by the absorbing effect thereof along with sprinkling of other fire-extinguishment agents such as water and highly halogenated hydrocarbon compounds. In the following, examples are given to illustrate the present invention in more detail. Example 1. Trichlorosilane in a volume of 50 ml was taken in a glass beaker of 150 ml capacity and 43 g of a porous silica/alumina-based ceramic material were added thereto by using a spoon as an absorbent material at an ambient temperature of 19 °C. The absorbent material contained 68% by weight of silicon dioxide and 25% by weight of aluminum oxide and had a particle size distribution ranging from 10 to 500 µm with a pore diameter ranging from 0.1 to 50 µm. It was noted in this test that the volume of gas evolution was very small and the temperature of the liquid trichlorosilane was only slightly increased from 19 °C to 20 °C by the addition of the absorbent. For comparison, the same test as above was repeated except that 43 g of the silica/alumina-based porous ceramic absorbent were replaced with 154 g of dry sand. In this case, a considerably large volume of gas evolution was noted with gas bubbles rising in the liquid. The temperature of the liquid was increased from 19 °C to30 °C. The above described comparative tests show that the porous ceramic absorbent according to the invention is much more effective as an absorbent of trichloroislane than conventional dry sands even when the amount of the absorbent used is only one-third or smaller than that of the dry sand with a smaller volume of gas evolution during addition. Example 2. Trichlorosilane in a volume of 500 ml was taken in a steel-made vessel of 2500 ml capacity and 190 g of a porous silica/alumina-based ceramic absorbent material were sprinkled thereover by using a small scoop at an ambient temperature of 7.5 °C. The absorbent material contained 85% by weight of silicon dioxide and 12% by weight of aluminum oxide and had a particle size distribution ranging from 10 to 1000 µm with a pore diameter ranging from 0.1 to 100 µm. It was noted that no reaction took place at all with the temperature of the trichlorosilane unchanged at 8 °C. For comparison, the same test as above was repeated except that 190 g of the porous ceramic absorbent material were replaced with 2900 g of dry sand. It was noted in this case that a reaction took place to some extent in the trichlorosilane with bubbles rising in the liquid. The temperature of the trichlorosilane was increased by the addition of the sand from 8 °C to 17 °C. As is understood from the above given comparative tests, the porous ceramic absorbent material of the invention is more effective than dry sand even when the amount thereof is only one-fifteenth of dry sand and is free from the problem of temperature elevation of the chlorosilane compound due to the reaction of the silane with the absorbent material or rather with the impurities contained in the absorbent material. Suppose that the above described results are also held in an industrial accident in which 500 liters at 20 °C or 670 kg of trichlorosilane have run out of a reservoir tank, 190 kg of the porous ceramic material according to the invention are sufficient to absorb the whole volume of the chlorosilane compound while the same absorbing effect can be obtained by using dry sand only when the amount of the dry sand is as large as 2900 kg or larger. Example 3. Absorption tests of various chlorosilane compounds other than trichlorosilane were undertaken by adding either the same porous ceramic absorbent as used in Example 1 according to the invention (Test A) or dry sand (Test B) in amounts indicated below to 50 ml of the chlorosilane compound contained in a vessel of stainless steel at an ambient temperature of 29 to 30 °C. The results of the tests were as described below. (a) Trimethyl chlorosilane Test A (35 g absorbent): No gas evolution; liquid temperature from 28 °C to 29 °C Test B (280 g absorbent): Medium volume of gas evolution, bubbles rising in the liquid; liquid temperature from 28 °C to 36 °C (b) Methyl dichlorosilane Test A (35 g absorbent): No gas evolution; liquid temperature from 28 °C to 29 °C Test B (210 g absorbent): Large volume of gas evolution; bubbles rising in the liquid; liquid temperature from 28 °C to 31 °C (c) Dimethyl dichlorosilane Test A (40 g absorbent): No gas evolution; liquid temperature from 28 °C to 30 °C Test B (270 g absorbent): Medium volume of gas evolution; bubbles rising in the liquid; liquid temperature from 28 °C to 41 °C (d) Methyl trichlorosilane Test A (40 g absorbent): No gas evolution; liquid temperature from 28 °C to 30 °C Test B (285 g absorbent): Medium volume of gas evolution; bubbles rising in the liquid; liquid temperature from 28 °C to 41 °C (e) Phenyl trichlorosilane Test A (45 g absorbent): No gas evolution; liquid temperature from 28 °C to 32 °C Test B (370 g absorbent): Small volume of gas evolution; liquid temperature from 28 °C to 34 °C (f) Diphenyl dichlorosilane Test A (55 g absorbent): No gas evolution; liquid temperature from 28 °C to 34 °C Test B (350 g absorbent): Small volume of gas evolution; liquid temperature from 28 °C to 42 °C (g) Silicon tetrachloride Test A (35 g absorbent): No gas evolution; liquid temperature from 26 °C to 28 °C Test B (215 g absorbent): Medium volume of gas evolution; bubbles rising in the liquid; liquid temperature from 28 °C to 42 °C As is understood from the results shown above, dry sand as a conventional absorbent of chlorosilane compounds is disadvantageous because gas evolution takes places more or less by the addition thereof to a chlorosilane compound sometimes accompanied by a large volume of bubbles rising in the liquid bringing the liquid to a seemingly boiling condition along with a large increase of the liquid temperature. In contrast thereto, the porous ceramic material used as the absorbent according to the invention is much more advantageous in safety than the conventional absorbent materials because the effect of absorption can be fully obtained even when the added amount thereof is only one-sixth or smaller of that of the dry sand absolutely without gas evolution or bubbles in the liquid when the absorbent is added to a chlorosilane compound and also with a relatively small increase of the liquid temperature. Thus, the present invention provides a very efficient and advantageous means to absorb a chlorosilane compound running out of a container without evolution of a toxic gas by the reaction with the chlorosilane compound so that the invention is industrially useful even by setting aside the economical advantage because a volume of a chlorosilane compound can be fully absorbed with a relatively small amount of the absorbent.

Claims: An absorbent for a liquid chlorosilane compound consisting of a silica-, silica/alumina-based porous ceramic material or of a mixture of them, powdery or granular, the pores of which have a pore diameter in the range from 0.1 to 100 µm, and the surface of which is rendered hydrophobic by treatment with an organosilane compound or with an organopolysiloxane compound, the content of silicon dioxide SiO₂ and aluminum oxide Al₂O₃ in the silica/alumina-based material being at least 90% by weight. In a method for absorbing a liquid chlorosilane compound by use of an absorbent material contacted with the chlorosilane compound, an improvement which comprises using, as the absorbent, a silica-,silica/alumina-based porous ceramic material or a mixture of them, of which the pores have a pore diameter in the range from 0.1 to 100 µm, the content of silicon dioxide SiO₂ in the silica-based material being at least 80 % by weight and the total content of silicon dioxide SiO₂ and aluminum oxide Al₂O₃ in the silica/alumina-based material being at least 90 % by weight. A method according to claim 2, wherein the surface of the absorbent has been rendered hydrophobic by treatment with an organosilane compound or with an organopolysiloxane compound.

Inventors: KOBAYASHI, MINORU, YAMAGUCHI, HISAYOSHI, YANAGISAWA, TAMOTSU
Applicants: SHIN-ETSU HANDOTAI COMPANY, LIMITED
Application year: 1988
Main classification: B01J20
IPC codes: B01J20, C09K3