IMPROVEMENTS IN OR RELATING TO RADIATION SENSITIVE COMPOUNDS

Abstract: A radiation sensitive compound is a trimer of or has the formula wherein R¹ and R², are alkyl, aryl, X, CHX₂, CH₂X, CX₃ or NHR³ wherein R³ represents hydrogen, lower alkyl, aryl or A², R⁴ represents NCO or R² provided that R³ is not - A², and provided at least one of R¹, and R² and R⁴ is CX₃, X is halogen, and A¹ and A² are each residues of A¹-H and A²-H respectively wherein A¹-H and A²-H are each compounds containing at least one group having an active hydrogen atom. The compounds are useful as initiators and colour change indicators in radiation sensitive compositions for lithographic printing plate production.

Description: This invention relates to radiation sensitive compounds and more particularly, but not exclusively, is concerned with radiation sensitive compounds for use in the manufacture of radiation sensitive plates for lithographic printing plate production. Radiation sensitive plates comprising a substrate coated with a radiation sensitive composition are well known in the production of lithographic printing plates and similar compositions are used for other purposes such as photoresists. In use, the composition is image-wise exposed to radiation so that parts of the composition are struck by the radiation and parts are not. The radiation and non-radiation struck parts have differing solubilities in developer liquids and thus the more soluble parts can be selectively removed by application of such a liquid. Radiation sensitive compositions comprising a photopolymerisable material and an initiator are well known. Halogen containing triazines, when irradiated with actinic radiation of suitable wavelength, are known to release a halogen radical which is capable of causing free radical polymerisation. In addition, the halogen radical can form free acid. Such compounds have therefore, been used as photoinitiators or acid release agents in radiation sensitive compositions for, for example, photoresists or printing plate coatings. It is an object of the present invention to provide novel compounds which have the property of producing a free radical when irradiated and which also have other valuable properties. According to one aspect of the present invention there is provided a radiation sensitive compound having the formula wherein R¹ and R², which may be the same or different, each represents C₁ to C₄ alkyl, aryl, X, CHX₂, CH₂X, CX₃ or NHR³ wherein R³ represents hydrogen, C₁ to C₄ alkyl, aryl or and provided at least one of R¹ and R² is CX₃, X is halogen, and A¹ and A² are each residues of A¹-H and A²-H respectively wherein A¹-H and A²-H which may be the same or different, are each compounds containing at least one group having an active hydrogen atom. EP-A-0271780 is an earlier application published after the priority date of the present application and is relevant under Article 54(3) and 54(4) EPC insofar as AT, BE, CH, DE, ES, FR, GB, IT, LI and NL are concerned. It discloses substituted 1-benzyl sulphonyl-3-heteroaryl compounds of the general type. According to another aspect of the present invention there is provided a method of producing a radiation sensitive compound having the formula wherein R¹ and R², which may be the same or different, each represents C₁ to C₄ alkyl, aryl, X, CHX₂, CH₂X, CX₃ or NHR³ wherein R³ represents hydrogen, C₁ to C₄ alkyl, aryl or provided at least one of R¹ and R² is CX₃, X is halogen and A¹ and A² are each residues of A¹-H and A²-H respectively wherein A¹-H and A²-H which may be the same or different, are each compounds containing at least one group having an active hydrogen atom; which method comprises the step of reacting together an isocyanate of the formula with a compound of the formula A¹-H and/or A²-H to obtain the desired compound wherein R⁶ or R⁴ represents C₁ to C₄ alkyl, aryl, X, CHX₂, CH₂X, CX₃, NCO or NHR⁵ wherein R⁵ represents hydrogen, C₁ to C₄ alkyl or aryl and at least one of R₆ and R⁴ is CX₃. Preferably the group containing the active hydrogen atom is a OH, NH, SH or CH₂ group. In the case where R¹, R² and/or R⁴ are alkyl groups, they contain from 1 to 4 carbon atoms. In the case where R¹, R² and/or R⁴ are aryl groups, they are preferably phenyl which may be substituted with halogen or alkyl or alkoxy containing 1-4 carbon atoms. The compounds of the invention are capable of producing a free radical on irradiation and have other important properties which depend on the nature of the compound A¹-H or A²-H containing the group having the active hydrogen atom. The compounds according to the invention are particularly useful for use as a photoinitiator in radiation sensitive compositions containing photopolymerisable materials such as ethylenically unsaturated monomers. In such compositions, polymerisation is caused by the free radicals produced by irradiation of the photoinitiator and one problem with such conventional compositions of this type is that the efficiency of the polymerisation is reduced due to the tendency of the photoinitiator to migrate out of the composition. By using as compounds A¹-H or A²-H, from which A¹ and A² are derived, polymeric or oligomeric compounds which contain at least one group (and preferably two or more groups) containing an active hydrogen atom, it is possible to anchor the radical producing moiety or moieties to a larger molecule and thus produce a photoinitiator which has less tendency for migration. Suitable compounds are, for example, polyethylene glycol, pentaerythritol and hexane-1,6-diol. Similarly, it is possible to produce an initiator in which the radical producing moiety or moieties are an integral part of the polymeric or oligomeric backbone by reacting a diisocyanate (i.e. an isocyanate of the above formula in which R⁶ or R⁴ is also an NCO group) and a polymeric or oligomeric compound containing one or more groups containing an active hydrogen compound. Radiation-sensitive compositions based on monomers also conventionally contain a support (binder) resin. By using a compound of the invention wherein the compound A¹-H or A²-H from which A¹ or A² is derived is a polymer containing at least one group having an active hydrogen atom and which has appropriate support (binder) properties, the support resin and the photoinitiator are combined into a single compound, thus reducing the number of separate components of the composition as well as reducing migration. Suitable polymers for this purpose are: poly(vinyl acetals), styrene-allyl alcohol copolymers, acrylic co- or terpolymers containing hydroxy alkyl (meth)acrylates, novolak resins and poly(vinyl phenol). An alternative way of reducing initiator migration is to use a compound of the invention wherein the compound A¹-H or A²-H from which A¹ or A² is derived is a compound which contains at least one group having an active hydrogen atom and which is capable of free radical polymerisation. Suitable compounds in this respect are those containing ethylenic unsaturation for example (meth)acrylates, such as 2-hydroxyethyl methacrylate and pentaerythritol triacrylate. In this case, the photoinitiator and the ethylenically unsaturated compound to be polymerised are in one and the same molecule. As is well known, it is desirable that radiation-sensitive compositions change colour upon irradiation. One way of achieving a colour change is to incorporate, within the composition, a pH sensitive dye and a compound capable of producing acid when irradiated i.e. an acid releasing agent. As mentioned above, halogen-triazines are such agents. Thus in radiation sensitive compositions based on ethylenically unsaturated monomers, the compounds of the invention can act as both acid release agents and as photoinitiators. In other negative-working compositions and positive-working compositions, the compounds of the invention can act as acid release agents. More particularly, in the case of positive-working compositions which, as is well known, are based on quinone diazide esters (as the radiation-sensitive component) and alkali soluble binder resins (particularly novolak resins), the compound A¹-H or A²-H from which A¹ or A² is derived can be either the quinone diazide ester or the novolak resin, thus obviating the need for a separate acid releasing agent. An alternative way of obtaining a colour change is to use a compound of the invention wherein the compound A¹-H or A²-H from which A¹ or A² is derived is a pH sensitive dye containing at least one group having an active hydrogen atom. Suitable dyes are, for example: In this way, the invention provides a colour change system in a single molecule, and may also, if desired, be used to provide a polymeric or oligomeric dye. The efficient production of the free radical on irradiation depends on the radiation having the correct wavelength to be absorbed by the initiator. However, a mis-match between the radiation wavelength and the initiator can be overcome by using a photosensitiser which absorbs at the wavelength of the radiation and then transfers the energy to the photoinitiator. This can be achieved by using a compound of the invention wherein the compound A¹-H or A²-H from which A₁ or A₂ is derived is a compound which contains at least one group having an active hydrogen atom and which has photosensitising properties. Suitable compounds are for example: 4-hydroxybenzophenone; 7-hydroxy-4-methyl coumarin; 4-phenyl phenol; 2′,4′,5′,7′-tetrabromo fluorescein (C.I. 453802); Thionin; 2-mercapto benzothiozole; 4-diethylamino-4′-(N-ethyl-N-hydroxyethyl)amino benzophenone; and 2(4(N-ethyl-N-hydroxyethyl)aminobenzylidene)inden-1-one. In this way, it is possible to provide in a single compound, a sensitised initiator, which will absorb and be active at a specified wavelength. The following Examples illustrate the invention: Example 1 A solution in ethyl methyl ketone of a photopolymerisable composition comprising:- 3 parts by weight of the dimethacrylate ester of the diglycidyl ether of bisphenol A, 1 part by weight of a vinyl acetate/crotonic acid copolymer, 0.43 parts by weight of compound I, and 0.15 parts by weight of ethyl Michler's ketone, was whirler coated onto a sheet of electrochemically grained and anodised aluminium and dried to form a radiation sensitive plate. The coating weight was 1.0 g per sq.m. The dried coating was overcoated with poly(vinyl alcohol) to prevent oxygen inhibition of the photopolymerisation reaction. The radiation sensitive plate was exposed through a continuous tone Stouffer step wedge to ultra-violet light (20 mJ/cm² from a Berkey-Ascor printing down frame) and then developed with an aqueous solution containing sodium propanoate, sodium benzoate and a surfactant. The developed image of the resultant lithographic printing plate had a step wedge of solid 4, tail 10. After storage under accelerated ageing conditions (30 degC, 95% relative humidity) for 3 weeks, analysis of the radiation sensitive coating of a similar plate showed that there had been negligible migration of Compound I. Exposure and development of the aged plate under the same conditions as above gave a similar step wedge reading of solid 4, tail 10. Preparation of Compound I 3g of PEG 600 (a polyethylene glycol) was dissolved in 20mls N-methyl pyrrolidone (NMP) and to this solution was added 3.57g of 2-isocyanato-4,6-bis(trichloromethyl)-s-triazine followed by 1 drop of dibutyl tin dilaurate. The reaction was then warmed to 40 degC and held at 40 degC for 3 hours. After this time the mixture was added to 100mls water to stop the reaction, filtered and washed well with water. The product was dried under vacuum at room temperature. Comparative Example 1 Example 1 was repeated using, instead of Compound I, 0.15 parts by weight of [2-chloro-phenyl-4,6-bis(trichloromethyl)-s-triazine] as the photoinitiator. Exposure and development produced a step wedge reading of solid 4, tail 10. After storage of a similar plate under the same accelerated ageing conditions as in Example 1 for 3 weeks, analysis showed a decrease of 33% in the original initiator content indicating that substantial migration had taken place. Moreover, exposure and development of the aged plate showed that it had become less sensitive, giving a solid 2, tail 7 step wedge. Example 2 Example 1 was repeated except that Compound II was used instead of Compound I. Similar results were obtained. Preparation of Compound II 1.36g of pentaerythritol was added to 40 ml NMP and to this solution was added 101.4 g of 2-isocyanato-4-methyl-6-trichloromethyl-s-triazine followed by 1 drop of dibutyl tin dilaurate. The reaction was then warmed to 50°C and held at this temperature for ten hours. The reaction was then stopped by adding the mixture to 200 ml water. The product was filtered out, washed well with water and dried under vacuum at room temperature. Example 3 Example 1 was repeated except that Compound III was used instead of Compound I. Similar results were again obtained. Preparation of Compound III Compound III was prepared by the same method as Compound II except that 0.88 g of N,N-dimethylene diamine and 5.07 g of the triazine were used. Example 4 Example 1 was again repeated except that Compound IV was used instead of Compound I. Similar results were again obtained. Preparation of Compound IV 1.50 g of 1,6-hexane dithiol was added to 40 ml NMP and to this solution 2.81 g of 2,4-diisocyanato-6-trichloromethyl-s-triazine were added over a period of 30 minutes. The solution was stirred for an additional three hours at ambient temperature, added to 200 ml water to stop the reaction and filtered. The product was washed and dried under vacuum at room temperature. Example 5 A solution, in ethyl methyl ketone, of a photopolymerisable composition comprising: 3 parts by weight of the dimethacrylate ester of diglycidyl ether of bisphenol A, 1 part by weight of Compound V, and 0.15 parts by weight of ethyl Michler's ketone, was whirler coated onto a sheet of electrochemically grained and anodised aluminium and dried to form a radiation sensitive plate. The coating weight was 1.0g per sq.m. The dried coating was overcoated with poly(vinyl alcohol) to prevent oxygen inhibition. The resultant radiation sensitive plate was exposed and developed as described in Example 1. A step wedge reading of solid 3, tail 9 was produced. After storage for 3 weeks under the accelerated ageing conditions described in Example 1, a similar plate was exposed and developed. The sensitivity of the plate remained unchanged, as shown by a solid 3, tail 9 step wedge. Preparation of Compound V 9.74g of a modified poly(vinyl butyral) resin (containing 54 mol.% butyral, 26 mol.% hydroxy and 20 mol.% hydrogen phthalate ester) was dissolved in 50 mls NMP and to this solution was added 3.57g of 2-isocyanato-4,6-bis(trichloromethyl)-s-triazine followed by 1 drop of dibutyl tin dilaurate. The reaction was then warmed to 40 degC and held at 40 degC for 6 hours. After this time the mixture was poured into 300mls water to stop the reaction, filtered and washed well with water. The product was dried at 35 degC under vacuum. Example 6 Example 5 was repeated except that Compound VI was used instead of Compound V. Similar results were obtained. Preparation of Compound VI 18.35 g of a poly(vinyl butyral) resin (containing 48 mol% butyral, 50 mol% hydroxy and 2 mol% acetate) was dissolved in 100 ml NMP and 13.79 g of p-toluene sulphonyl isocyanate. The mixture was held at ambient temperature for one hour and then 10.71 g of 2-isocyanato-4,6-bis(trichloromethyl)-s-triazine was added followed by 1 drop of dibutyl tin dilaurate. The mixture was then warmed to 40°C and held at this temperature for six hours. The mixture was poured into water, filtered and the product was washed with water and dried under vacuum at 35°C. Example 7 Example 5 was repeated except that Compound VII was used in place of Compound V. Similar results were again obtained. Preparation of Compound VII 15 g of a modified styrene/allyl alcohol copolymer (containing 70 mol% styrene, 15 mol% hydroxy and 15 mol% hydrogen phthalate ester) was dissolved in 75 ml NMP and then 5.07 of 2-isocyanato-4-methyl-6-(trichloromethyl)-s-triazine and 1 drop of dibutyl tin dilaurate were added. The mixture was then warmed to 50°C and held at that temperature for ten hours. Finally the mixture was poured into 500 ml water, filtered and the product was washed with water and dried under vacuum at 35°C. Example 8 A positive working radiation sensitive coating solution comprising:- 6 parts by weight of a naphthoquinone diazide sulphonic acid ester, 27 parts by weight of Compound VIII, and 0.36 parts by weight of Sudan Yellow, made up to 400 mls with a mixture of 95 parts acetone and 5 parts methyl oxitol was whirler coated onto electrochemically grained and anodised aluminium and dried at 100 degC for 5 minutes to give a radiation sensitive plate with a coating weight of 2.5g per sq.m. The plate was exposed through a Stouffer step wedge to ultra-violet light (800 mJ/cm² from a Berkey-Ascor printing down frame) giving a yellow image against a red background. The plate was then dish-developed in 8% sodium metasilicate solution for 45 seconds, giving a step wedge reading of clear 2, solid 7. After storage of the coating solution for 7 days at room temperature (20 degC) analysis showed that negligible decomposition of Compound VIII had taken place. A radiation sensitive plate derived from the aged coating solution was exposed and showed equivalent contrast of the yellow image on the red background to a plate made from fresh coating solution. Preparation of Compound VIII 10.8g of cresol-novolak resin was dissolved in 50mls NMP and to this solution was added 3.57 g of 2-isocyanato-4,6-bis(trichloromethyl)-s-triazine followed by 1 drop of dibutyl tin dilaurate. The reaction was completed and the product isolated as in Example 2. Comparative Example 8 Example 8 was repeated using 27 parts by weight of novolak resin and 0.44 parts by weight of 4-diazodiphenylamine tetrafluoroborate instead of Compound VIII. After exposure the contrast of the yellow image on the red background was similar as for the plate in Example 3, and, after development, gave a similar step wedge reading of clear 2, solid 7. After storage of the coating solution for 7 days at room temperature, analysis showed that 10% of the original content of the 4-diazodiphenylamine tetrafluoroborate had decomposed. A radiation sensitive plate derived from the aged coating was exposed and the contrast of the yellow image on the red background was inferior to the contrast obtained in Example 8. Example 9 Example 8 was repeated except that the coating solution comprised: 6 parts by weight of Compound IX 27 parts by weight of cresol-novolak resin 0.36 parts by weight of Sudan Yellow Similar results were obtained. Preparation of Compound IX 6.3 g of the bis ester of 2,3,4-trihydroxy benzophenone and naphthoquinone-(1,2)-diazide(2)-5-sulphonyl chloride was dissolved in 50 ml of 1,4-dioxan and 3.57 g of 2-isocyanato-4,6-bis (trichloromethyl)-s-triazine was added. The mixture was warmed to 35°C, maintained at that temperature for four hours and then poured into 500 ml water to stop the reaction. The product was filtered, washed with water and dried under vacuum at ambient temperature. Example 10 Example 1 was repeated adding 0.1 parts by weight of Compound X to the formulation as a colour change agent. The resultant radiation sensitive plate was exposed through a step wedge to ultra-violet light (200 mJ/cm²) producing a red image on a yellow background. After development the red image retained its colour giving excellent contrast with the background, and a solid 6, tail 13 step wedge was obtained. Visual inspection of a sample of the poly(vinyl alcohol) overcoat which had been removed prior to exposure indicated that a negligible amount of the Compound X had leached into the overcoat. Preparation of Compound X 3.5g of a dye with the following structure: was dissolved in 20mls NMP and to this solution was added 2.8g of 2,4-diisocyanato-6-trichloromethyl-s-triazine followed by 1 drop of dibutyl tin dilaurate. The reaction was then warmed to 50 degC and held at 50 degC for 6 hours. After this time the mixture was added to 100mls water to stop the reaction, filtered and washed well with water. The product was dried under vacuum at room temperature. Comparative Example 10 Example 10 was repeated using 0.1 parts by weight of 3-chloro-4-(4′methoxyphenylazo)-N,N-bis(2″-hydroxyethyl)aniline instead of Compound X as the colour change agent. The radiation plate was exposed as in Example 10 producing a red image on a yellow background. After development the red image became paler in colour resulting in a poorer contrast with the background than in Example 10. Visual inspection of a removed sample of the poly(vinyl alcohol) overcoat prior to exposure revealed that it had a strong yellow colouration indicating that the colour change agent had leached into the overcoat. Example 11 Example 10 was repeated using Compound XI instead of Compound X. Similar results were obtained. Preparation of Compound XI Compound XI was prepared in a similar manner to Compound X except that 2.9 g of a dye having the structure was reacted with 3.50 g of 2-(4′-chlorophenyl-4-isocyanato-6-trichloromethyl-s-triazine. Comparative Example 11 Comparative Example 10 was repeated except that the colour change agent used was 4-(4′-methoxyphenylazo)-N-ethyl-N-(2″-hydroxyethyl)-aniline. The results were again similar. Example 12 Example 11 was repeated except that Compound XII was used instead of Compound XI. Similar results were obtained. Preparation of Compound XII Compound XII was prepared in a similar manner to Compound XI except that 2.83 g 2-N,N-(dimethylamino)-4-isocyanato-6-trichloromethyl-s-triazine was used. Example 13 A solution in ethyl methyl ketone of a photopolymerisable composition comprising:- 3 parts by weight of Compound XIII, 1 part by weight of a vinyl acetate/crotonic acid copolymer and 0.15 parts by weight of ethyl Michler's ketone, was whirler coated onto a sheet of electrochemically grained and anodised aluminium and dried to form a radiation sensitive plate. The coating weight was 1.0g per sq.m. The dried coating was overcoated with poly(vinyl alcohol) to prevent oxygen inhibition. The resultant radiation sensitive plate was exposed to radiation through a step wedge (200 mJ/cm² in a Berkey-Ascor frame) and developed as in Example 1. A step wedge reading of solid 5, tail 12 was produced. Preparation of Compound XIII To 4.84 g of 2-ethyl-2-hydroxy methyl)-1,3-propanediol diacrylate was added 2.8 g of 2,4-diisocyanato-6-trichloromethyl-s-triazine, 1 drop of dibutyl tin dilaurate and 0.01g 4-methoxy phenol. This melt was then stored at 60 degC for 10 hours to complete the reaction. Examples 14-17 Example 13 was repeated using Compounds XIV-XVIII instead of Compound XIII. Preparation of Compounds XIV-XVII These Compounds were prepared by dissolving appropriate amounts of various (meth)acrylate A-D as listed below in 150 ml of 1,4-dioxan, adding 14.05 g of 2,4-diisocyanato-6-trichloromethyl-s-triazine, heating the mixture to 50°C and holding it at this temperature for 4 hours before evaporating the solvent at reduced pressure to isolate the product. A = Pentaerythritol triacrylate (29.8 g) B = Dipentaerythritol (monohydroxy) pentaacrylate (52.4 g) C = Glycerol di(meth)acrylate (22.7 g) D = Di-trimethylolpropane triacrylate (39.8 g). Example 19 A solution in ethyl methyl ketone of a photopolymerisable composition comprising:- 3 parts by weight of the dimethacrylate ester of the diglycidyl ether of bisphenol A, 1 part by weight of a vinyl acetate/crotonic acid copolymer and 0.3 parts by weight of Compound XIX was whirler coated onto a sheet of electrochemically grained and anodised aluminium and dried to form a radiation sensitive plate. The coating weight was 1g per sq.m. The dried coating was overcoated with poly(vinyl alcohol) to prevent oxygen inhibition. The resultant radiation sensitive plate was exposed through a step wedge (20 mJ/cm² in a Berkey-Ascor frame) and developed as in Example 1. A step wedge reading of solid 2, tail 7 was produced. Preparation of Compound XIX 1.98g of 4-hydroxy benzophenone was dissolved in 20mls NMP and to this solution was added 3.57g of 2-isocyanato-4,6-bis(trichloromethyl)-s-triazine and 1 drop dibutyl tin dilaurate. The mixture was then heated to 50 degC and held at 50 degC for 6 hours. After this time the reaction mixture was poured into 100 mls water to stop the reaction, filtered and washed well with water. The product was dried under vacuum at room temperature. Examples 20 and 21 Example 19 was repeated using Compounds XX and XXI in place of Compound XIX. Similar results were obtained. Preparation of Compounds XX and XXI The compounds were produced in a similar manner to Compound XIX except that 1.76 g of 7-hydroxy-4-methyl coumarin and 1.67 g of 2-mercaptobenzothiazole were used instead of the 4-hydroxy benzophenone.

Claims: 1. A radiation sensitive compound having the formula wherein R¹ and R², which may be the same or different, each represents C₁ to C₄ alkyl, aryl, X, CHX₂, CH₂X, CX₃ or NHR³ wherein R³ represents hydrogen, C₁ to C₄ alkyl, aryl or and provided at least one of R¹ and R² is CX₃, X is halogen, and A¹ and A² are each residues of A¹-H and A²-H respectively wherein A¹-H and A²-H which may be the same or different, are each compounds containing at least one group having an active hydrogen atom. 2. A method of producing a radiation sensitive compound having the formula wherein R¹ and R² which may be the same or different each represent C₁ to C₄ alkyl, aryl, X, CHX₂, CH₂X, CX₃ or NHR³ wherein R³ represents hydrogen, C₁ to C₄ allyl aryl or provided at least one of R¹ and R² is CX₃, X is halogen and A¹ and A² are each residues of A¹-H and A²-H respectively wherein A¹-H and A²-H which may be the same or different, are each compounds containing at least one group having an active hydrogen atom; which method comprises the step of reacting together an isocyanate of the formula with a compound of the formula A¹-H and/or A²-H to obtain the desired compound wherein R⁶ or R⁴ represent C₁ to C₄ alkyl, aryl, X, CHX₂, CH₂X, CX₃, NCO or NHR⁵ wherein R⁵ represents hydrogen, lower alkyl or aryl and at least one of R⁶ and R⁴ is CX₃. 3. A method according to claim 2 wherein the group in compound A¹-H or A²-H having the active hydrogen atom is a -OH, -NH, -SH or -CH₂- group. 4. A method according to claim 2 wherein the compound A¹-H or A²-H is polyethylene glycol, pentaerythritol, hexane diol, a polyvinyl acetal a styrene-allyl alcohol copolymer, an acrylic copolymer ou terpolymer containing a hydroxyalkyl acrylate or methacrylate, novolak resin, a poly(vinyl phenol), an acrylate, methacrylate, 2-hydroxyethyl methacrylate or pentaerythritol triacrylate. 5. A method according to claim 2 wherein the compound A¹-H or A²-H is a pH sensitive dye. 6. A method according to claim 2 wherein the compound A¹-H or A²-H has photosensitising properties. 7. A method according to claim 6 wherein the compound is 4-hydroxybenzophenone; 7-hydroxy-4-methyl coumarin; 4-phenyl phenol; 2′,4′,5′,7′-tetrabromo fluorescein ; thionin; 2-mercapto benzothiozole; 4-diethylamino-4′-(N-ethyl-N-hydroxyethyl)amino benzophenone; and 2(4(N-ethyl-N-hydroxyethyl) aminobenzylidene)inden-1-one. 8. A radiation sensitive composition comprising a compound as claimed in claim 1 in admixture with a photopolymerisable material or a quinone diazide ester.

Inventors: KOLODZIEJCZYK, VICTOR, WHITE, NICHOLAS JOHN
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY (A DELAWARE CORPORATION)
Application year: 1988
Main classification: G03F7
IPC codes: C08L101, C09D5, C07D251, G03F7, C08F2, C08K5