Primed polymeric surfaces for cyanoacrylate adhesives

Abstract: A primed polymeric article is provided. The article comprises a polymeric substrate having graft polymerized thereon at least one organic nucleophilic graft-polymerizable monomer or salt thereof which is capable of accelerating the cure of a cyanoacrylate adhesive. The invention also provides an article wherein the primed polymeric article is adhered to a substrate with a cyanoacrylate adhesive and a method for adhering a polymeric first substrate to a second substrate with a cyanoacrylate adhesive.

Description: Field of the Invention This invention relates to specified polymeric substrates having a primed surface which provides improved bonding of cyanoacrylate adhesives thereto and a method for adhering specified primed polymeric substrates with cyanoacrylate adhesives. Background of the Invention Adhesive compositions based on alpha-cyanoacrylate esters belong to a class of adhesives known as reactive liquid adhesives. These cyanoacrylate adhesives are single-part, low viscosity adhesives which polymerize rapidly at room temperature without the use of an added catalyst when pressed between two substrates. Application of the cyanoacrylate adhesives merely involves spreading a small amount of the adhesive between two substrates, pressing the substrates together, and allowing the resultant bond to cure. The adhesive develops sufficient strength after a short period of time to hold the substrates together until the adhesive completely polymerizes and builds up to its maximum bonding strength. Initiation of polymerization, or cure, is generally believed to proceed through an anionic mechanism. The cyanoacrylate adhesives have such a great tendency to polymerize that water is a sufficiently active initiator. When the adhesive is applied to a substrate and exposed to atmospheric and surface moisture, polymerization usually begins within a relatively short period of time, generally less than one minute, and on many surfaces within a matter of a few seconds. For many years a need has existed for improved bonding of polymeric substrates to other materials, e.g., metals, wood and ceramics, or to themselves with cyanoacrylate adhesives. Untreated polymeric substrates, particularly polyolefin and polyfluorocarbon substrates, when bonded with cyanoacrylate adhesives, generally exhibit less shear strength than is desired for many end uses. Modification of polymeric surfaces has been used as a means of increasing the adhesion of various adhesives to polymeric surfaces. Surface modification techniques which have been examined are corona discharge treatment, flame treatment with, for example, helium gas plasma or oxygen gas plasma, and chemical treatment with, for example, chromic acid, potassium permanganate, or peroxydisulphate solutions. Such treatments are described by D. Briggs in "Surface Treatments for Polyolefins," Surface Analysis and Pretreatment of Plastics and Metals , D. M. Brewis, Ed., MacMillan, New York, 1982, pp. 199-226. These treatments and other surface modification procedures have a common shortcoming in poor durability. Light rubbing of the surface causes a decrease in the effect, the altered surface being easily abraded. Irradiation of polyolefin substrates, such as with an electron beam, to improve the adhesion of various coatings is also known and has been disclosed, for example, in U.S. Patent No. 4,041,192 (Heger et al.), No. 4,148,839 (Fydelor), No. 3,252,880 (Magat et al.) and No. 4,179,401 (Garnett et al.). Application of a precoat, or primer, on surfaces of various materials has also been used to improve the adhesion of cyanoacrylate adhesives to various substrates. Primers which have been used include alkyl monohydric alcohols (U.S. Patent No. 2,768,109, Coover, Jr.), monomeric epoxides (U.S. Patent No. 3,259,534, Wicker, Jr. et al.), organic amines such as secondary amines, tertiary amines, N-substituted alkanolamines, acrylated N-substituted alkanolamines, diamines and certain heterocyclic amines (U.S. Patent No. 3,260,637, Von Bramer), organometallic compounds (European Patent Publication No. 0 129 069, Toagosei), a solid mixture of alkaline or basic accelerator, such as sodium or potassium hydroxide or sodium borosilicate spheres of micro-size, combined in a chalkable calareous binder (U.S. Patent No. 4,215,173, Hubbard), alkyl 2-cyanopenta-2,4-dienoate (U.S. patent No. 4,425,471, Millet), and tannins, such as digallic acid, tannic acid, or other hydrolyzable or condensed tannin (U.S. Patent No. 4,511,686, Millet). However, many of these priming materials are easily removed from the substrate to which they are applied by evaporation or abrasion during handling of the primed substrate. Improved adhesion of cyanoacrylate adhesives to various substrates through the use of adhesive additives has also been described. Various additives which have been suggested include plasticizers, such as alkyl esters of aliphatic monocarboxylic acids, alkyl esters of aliphatic dicarboxylic acids, alkyl phosphates, triaromatic phosphates, polyfunctional aliphatic esters, and aliphatic and aromatic phosphonates (U.S. Patent No. 2,784,127, Joyner et al.), itaconic acid anhydride (U.S. Patent No. 3,948,794, Eberhard), acetic acid (U.S. Patent No. 4,125,494, Schoenberg et al.), compounds having the formula wherein R' is hydrogen or an alkyl, aryl, or cycloalkyl group having 1 to 10 carbon atoms, such as gallic acid monohydrate, methyl gallate, propyl gallate and hexyl gallate (U.S. Patent No. 4,139,693, Schoenberg), a combination of polyethylene glycols having a degree of polymerization of at least 3 and non-ionic surface active agents having a poly(ethyleneoxy) moiety therein with the poly(ethyleneoxy) moiety having a degree of polymerization of at least 3 (U.S. Patent No. 4,170,585, Motegi et al.), trichlortrifluoroethane (U.S. Patent No. 4,200,549, Okamura et al.), esters compounds such as acrylates, methacrylates, and crotonates of glycols, glycol monoethers, and monoesters (U.S. Patent No. 4,307,216, Shiraishi et al.), a combination of (1) at least one aliphatic polyol and/or polyether and derivatives thereof and (2) at least one aromatic polyol and/or carboxylic acid and derivatives thereof (U.S. Patent No. 4,377,490, Shiraishi et al.), and phthalic anhydride (U.S. Patent No 4,450,265, Harris). Polyolefin substrates have been provided with a treated surface for improved adhesion of pressure-sensitive adhesives. U.S. Patent No. 3,628,987 (Nakata et al.) discloses a pressure-sensitive adhesive film wherein the film surface to which the adhesive is adhered has graft-polymerized thereto a vinyl monomer or diene monomer, the adhesive having a solubility parameter near that of polymers of the vinyl or diene monomer. U.S. Patent No. 4,563,388 (Bonk et al.) discloses a polyolefin substrate having graft-polymerized thereto at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and ester thereof; acrylamide; methacrylamide; sterically non-hindered tertiary alkyl acrylamides and methacrylamides having three or less carbon atoms in the alkyl group; and N-vinyl pyrrolidone, and firmly adherently bonded to the graft-polymerized monomer, an acrylic-type, normally tacky and pressure-sensitive adhesive. A series of articles, "Surface Modification of Polyethylene by Radiation-Induced Grafting for Adhesive Bonding. I. Relationship Between Adhesive Bond Strength and Surface Composition," (S. Yamakawa, J. Appl. Polym. Sci. , 20 , 3057-3072 (1976); "II. Relationship Between Adhesive Bond Strength and Surface Structure," (S. Yamakawa et al., Macromolecules , 9 , 754-758, 1976); "III. Oxidative Degradation and Stabilization of Grafted Layer," (S. Yamakawa et al., J. Appl. Polym. Sci. , 22 , 2459-2470, 1978); "IV. Improvement in Wet Peel Strength," (S. Yamakawa et al., J. Appl. Polym. Sci. , 25 , 25-39, 1980), and "V. Comparison with Other Surface Treatments, " (S. Yamakawa et al., J. Appl. Polym. Sci. , 25 , 40-49, 1980), disclose grafting of methyl acrylate (followed by saponification), vinyl acetate, acrylic acid, acrylamide, and methylolacrylamide to polyethylene by vapor-phase mutual grafting or liquid-phase preirradiation at thicknesses of grafted monomer of more than 10 micrometers to improve adhesion of epoxy adhesives. European Patent Application No. 0 297 741 of patentee, which is available as a prior art reference only for the purposes of Articles 54(3) EPC and 54(4) EPC discloses on page 4 thereof, between lines 45 and 55 that a specified type of polypropylene can have graft-polymerized thereto certain types of monomers which are commonly used to modify surface characteristics of polyolefin substrates. As a particular example it is stated that the specified type of polypropylene substrate can have graft polymerized onto the surface thereof N,N-dimethyaminoethyl acrylate N-vinyl-2,pyrrolidine or 2-vinylpyridine for use with cyanoacrylate adhesives. Summary of the Invention The present invention discloses use in a method of enhancing the adhesion of cyanoacrylate adhesives to polymeric articles of a primed polymeric article comprising a polymeric substrate selected from polyethylene, polyester, polyamide, polyimide, acetal, polycarbonate, polyvinyl chloride, polysulfone, polystyrene, polyacrylonitile, polyacrylate and polyfluorocarbon, said substrate having graft-copolymerized monomer or salt thereof which is capable of accelerating the cure of a cyanoacrylate adhesive to said polymeric article. The present invention also provides a method for adhering a polymeric first substrate to a second substrate with a cyanoacrylate adhesive comprising the steps of: a) coating that portion of the polymeric first substrate to be adhered with at least one organic nucleophilic graft-polymerizable monomer or salt thereof which is capable of accelerating the cure of the cyanoacrylate adhesive wherein said polymeric first substrate is selected from polyethylene, polyester, polyamide, polyimide, acetal, polycarbonate, polyvinyl chloride, polysulfone, polystyrene, polyacrylonitrile, polyacrylate and polyfluorocarbon; b) irradiating the coated substrate to graft copolymerize said monomer to said substrate; c) coating a cyanoacrylate adhesive on at least one of (i) the graft-copolymerized monomer surface of the first substrate and (ii) a surface of the second substrate to be adhered; d) contacting said surfaces (i) and (ii); and e) allowing the cyanoacrylate adhesive to cure. The present invention further provides a primed polymeric first substrate firmly adhered to a second substrate with a cyanoacrylate adhesive, by the abovementioned method. The graft-polymerized monomeric layer provides an increase in the bond strength of the cyanoacrylate adhesive to the specified polymeric substrate. Where the second substrate is also a polymeric material, that substrate preferably has at least one of the organic nucleophilic monomers or salts thereof graft-polymerized thereto. Detailed Description of the Invention The specified substrate useful in the method of the invention is selected from polyethylene; polyesters, such as polyethylene terephthalate and polybutylene terephthalate; polyamides, such as nylon; polyimides, such as Kaptan™; acetals, such as Delrin™; polycarbonates; polyvinyl chloride; polysulfones; polystyrene; polyacrylonitrile; polyacrylates; and polyfluorocarbons, such as polytetrafluoroethylene. Such material can be formed by well-known methods such as extruding, casting, blowing and molding. These formed polymeric materials are variously useful, for example, as films, fibers, foams, sheeting, tubing and piping, automotive parts, appliance parts, glazing materials, and furniture components, and in laminates and structural applications. The particular type of polymeric material is determined by the end use of the article formed from the material. The polymeric material may contain additives, such as colorants, fillers, crosslinking agents, dispersants, plasticizers, and extrusion aids, which are known in the art. The monomers which are graft-polymerized onto the polymeric substrate are those monomers which are organic nucleophilic graft-polymerizable monomers or salts thereof which are capable of accelerating the cure of the cyanoacrylate adhesive. Such monomers include secondary amines, tertiary amines, alkanol amines, di-n-alkylamides, and epoxides which have a polymerizable substituent such as, for example, a vinyl or acrylate group. Substituted amines useful as the monomers in the present invention include substituted piperidines, substituted pyrrolidines, substituted pyridines, substituted azoles, e.g. imidazoles and pyrazoles, substituted oxazines, substituted diazines, e.g., pyridazines, pyrimidines, and pyrazines, substituted purines, and dialkylaminoalkyl acrylates and methacrylates represented by the formula R¹R²NR³OCOC(H or CH₃)=CH₂ where R¹ and R² are independently lower alkyl groups preferably having 1 to 6 carbon atoms and R³ is a lower alkyl group preferably having 1 to 8 carbon atoms. Specific monomers useful in the present invention include 4-vinyl pyridine, 2-vinyl pyridine, 1-vinyl imidazole, 1,3-dimethyl-7-vinyl xanthine, 3-methyl-7-vinyl xanthine, glycidyl acrylate, glycidyl methacrylate, dimethyl acrylamide, diethylaminoethyl acrylate, dimethylaminopropyl methacrylate, dimethylaminoneopentyl acrylate, dimethylaminoethyl methacrylate, 2-(N-piperidino)ethyl acrylate, 2-(N-pyrrolidino)ethyl acrylate, and 5-vinyl pyrimidine. The monomer composition applied to the polymeric substrate may contain various additives such as solvents, crosslinking agents, and surfactants. The monomer composition should be free of acidic contaminants which tend to inhibit polymerization of cyanoacrylate adhesives. Crosslinking agents, some of which may also be monomers suitable for grafting onto the substrate themselves, may be added to further enhance heat resistance of the product. Examples of useful crosslinking agents include polyethylene glycol diacrylate, pentaerythritol tetraacrylate, tetraethylene glycol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, allyl methacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate thiodiethylene glycol diacrylate, triallyl cyanurate, and ethoxylated trimethylol propane methyl ether diacrylate. The preferred crosslinking agents include polyethylene glycol diacrylate, tetraethylene glycol dimethacrylate trimethylol propane tricrylate, and thiodiethylene glycol diacrylate. Crosslinking agents may be present in monomer compositions in amounts of about 0 to 80 weight percent, preferably about 0 to 40 weight percent. Surfactants may be present in the monomer composition to improve the uniformity of the coating on the substrate. The thickness of the monomer composition is preferably less than 5 micrometers, more preferably less than 1 micrometer and most preferably less than 0.5 micrometer. Generally, the thickness of the monomer layer is at least 0.05 micrometers. The monomer may be graft-polymerized to the substrate by use of actinic radiation such as X-rays, beta rays, gamma rays, ultraviolet and visible light from conventional mercury sources or lasers, and electron beam irradiation. The preferred methods of graft-polymerization are by irradiation with an electron beam or ultraviolet radiation. The electron beam dosage is typically greater than 0.05 Mrads, preferably greater than 0.5 Mrads, and more preferably in the range of 2 to 10 Mrads. The ultraviolet radiation dosage, both with conventional mercury sources or laser, is typically greater than 100 mjoules/cm², preferably greater than 300 mjoules/cm², and generally less than 700 mjoules/cm². The cyanoacrylate adhesives useful in the present invention are esters of α-cyanoacrylic acid. These esters may be alkyl, alkenyl, haloalkyl, alkoxyalkyl, biscyanoacrylates, or β-substituted-α-cyanoacrylates. The preferred esters are represented by the formula where R is an alkyl or alkenyl group having form 1 to 16 carbon atoms, a cyclohexyl group, or a phenyl group. Commercially important esters include the methyl, ethyl, isopropyl, n-butyl, and allyl esters, the methyl and ethyl esters being the most commonly used. Commercially available cyanoacrylate adhesives include Scotchweld™ CA-8, available from 3M Company, Superbonder™ 414, available from Loctite Corp., Permabond™ 102, available from Permabond International Div., National Starch and Chemical Corp., Pacer Tech™ E-100, available from Pacer Technology and Resources, and TB 1743, available from Three Bond Corp. of America. The advantages of the invention are illustrated by the following examples, it being understood that numerous variations will be well within the ability of those skilled in the art. In the examples, all parts and percentages are by weight unless otherwise indicated. In the Examples, the following test was used to evaluate the shear strength of the cyanoacrylate adhesive bonds. Shear Test Two test panels (2.54 cm x 5.08 cm x .32 cm) are adhered together by placing a large drop, about 0.2 grams, of Scotchweld™ CA-8 adhesive, an ethyl cyanoacrylate adhesive, available from 3M Company, on each test panel to coat a 2.54 cm x 1.27 cm end portion of each panel and the adhesive-coated surfaces are brought into contact with each other to form a 2.54cm x 1.27 cm overlap. The test panels are clamped at each edge of the of the overlap using 0.94 cm capacity binder clips No. 10020 available from IDL Mfg. and Sales Corp., Carlstadt, N.J. The adhesive is allowed to cure at room temperature and the force to break the bond is measured using tensile testing equipment at a jaw separation rate of 2.54 mm/min Examples 1-5 and Comparative Example C1 Test panels were prepared as follows: To polyethylene panels (2.54 cm x 5.08 cm x .32 cm) was applied a blend of 100 parts of specified monomer and 0.5 part of a fluorochemical acrylate oligomer (a wetting and levelling agent commercially available from 3M Company as FC-430™). The coating thickness was about one micrometer. Each coated surface was then exposed to electron beam irradiation at a dosage of about 4 Mrads and a voltage of 150-250 kV in a nitrogen atmosphere to effect graft-polymerization of the specified monomer onto the surface of the polyethylene panels. The polyethylene panels having the specified monomer graft-polymerized thereon were surface cleaned with acetone to remove any ungrafted monomer and hompolymer of the monomer and two of the panels were adhered together at their graft-polymerized surfaces, allowed to cure for 44 hours and tested for shear strength. The various monomers set forth in Table 1 were graft-polymerized onto the surface of the test panels. The panels were adhered together at their graft-polymerized surfaces, allowed to cure for 20 hours (Examples 1 and 2) or 44 hours (Examples 3-5), and tested for shear strength. In Comparative Example C1, test panels having no monomer graft-polymerized thereon were adhered together in the same manner as in Examples 1-5, allowed to cure for 20 hours, and tested for shear strength. The results are set forth in Table 1. Example Monomer Shear strength (kPa) 1 dimethylaminoneopental acrylate 5180 2 dimethylaminoethyl methacrylate 4760 3 dimethylaminoethyl acrylate 6140 4 1-vinyl imidazole 6510 5 2-vinyl pyridine 5230 C1 none 0 Examples 6-9 and Comparative Example C2 In Examples 6-9, test panels were prepared as in Example 1, except that the panels were polytetrafluoroethylene and the various monomers set forth in Table 3 were graft polymerized onto the surface of the test panels. The panels were adhered together at their graft-polymerized surfaces with cyanoacrylate adhesive, allowed to cure for 16 hours, and tested for shear strength. In Comparative Example C3, polytetrafluoroethylene test panels which had no monomer graft polymerized thereon were adhered together with cyanoacrylate adhesive and tested for shear strength. The results are set forth in Table 2. Example Monomer Shear strength (kPa) 6 4-vinyl pyridine 2470 7 1-vinyl imidazole 2730 8 dimethylaminoethyl acrylate 2540 9 glycidyl methacrylate 1530 C2 none 800 Examples 10-13 and Comparative Example C3 In Examples 10-13, test panels were prepared as in Example 1, except that the panels were Delrin™, a linear polyoxymethylene-type acetal resin, available from E.I. du Pont de Nemours Co., and the various monomers set forth in Table 3 were graft polymerized onto the surface of the test panels. The panels were adhered together at their graft-polymerized surfaces with cyanoacrylate adhesive, allowed to cure for 16 hours, and tested for shear strength. In Comparative Example C3 Delrin™ test panels which had no monomer graft polymerized thereon were adhered together with cyanoacrylate adhesive and tested for shear strength. The results are set forth in Table 3. Example Monomer Shear strength (kPa) 10 4-vinyl pyridine 4120 11 1-vinyl imidazole 4910 12 dimethylaminoethyl acrylate 5430 13 glycidyl methacrylate 4880 C3 none 1420 Examples 14-17 and Comparative Example C4 In Examples 14-17, test panels were prepared as in Example 1, the various monomers set forth in Table 4 were graft polymerized onto the surface of the test panels. The panels were adhered together at their graft-polymerized surfaces with cyanoacrylate adhesive, allowed to cure for 16 hours, and tested for shear strength. In Comparative Example C4, polyethylene test panels which had no monomer graft polymerized thereon were adhered together with cyanoacrylate adhesive and tested for shear strength. The results are set forth in Table 4. Example Monomer Shear strength (kPa) 14 4-vinyl pyridine 2740 15 1-vinyl imidazole 4560 16 dimethylaminoethyl acrylate 3720 17 glycidyl methacrylate 2230 C4 none 510 The various modifications and alterations of this invention will be apparent to those skilled in the art without departing from the scope of this invention and this invention should not be restricted to that set forth herein for illustrative purposes.

Claims: Use in a method of enhancing the adhesion of cyanoacrylate adhesives to polymeric articles of a primed polymeric article comprising a polymeric substrate selected from polyethylene, polyester, polyamide, polyimide, acetal, polycarbonate, polyvinyl chloride, polysulfone, polystyrene, polyacrylonitrile, polyacrylate and polyfluorocarbon, said substrate having graft-copolymerized thereon at least one organic nucleophilic graft-copolymerizable monomer or salt thereof which is capable of accelerating the cure of a cyanoacrylate adhesive to said polymeric article. The use of claim 1 wherein said monomer is a secondary or tertiary amine, alkanolamine, di-n-alkylamide or epoxide which has a polymerizable substituent. The use of claim 2 wherein the substituted amines are substituted piperidines, substituted pyrrolidines, substituted pyridines, substituted azoles, substituted oxazines, substituted diazines, substituted purines, and dialkylaminoalkyl acrylates and methacrylates represented by the formula R¹R²NR³OCOC(H or CH₃)=CH₂ where R¹, R² and R³ are lower alkyl groups. The use of claim 1 wherein said monomer is 4-vinyl pyridine, 1-vinyl imidazole, 1,3-dimethyl-7-vinyl xanthine, 3-methyl-7-vinyl xanthine, glycidyl acrylate, dimethyl acrylamide, diethylaminoethyl acrylate, dimethylaminopropyl methacrylate, 2-(N-piperidino)ethyl acrylate, 2-(N-pyrrolidino)ethyl acrylate and 5-vinyl pyrimide. The use of any preceding claim wherein said monomer is free of acidic contaminants. The use of any preceding claim wherein said graft-copolymerized monomer forms a layer less than 5 micrometers thick. A method for adhering a polymeric first substrate to a second substrate with a cyanoacrylate adhesive comprising the steps of a) coating that portion of the polymeric first substrate to be adhered with at least one organic nucleophilic graft-polymerizable monomer or salt thereof which is capable of accelerating the cure of the cyanoacrylate adhesive wherein said polymeric first substrate is selected from polyethylene, polyester, polyamide, polyimide, acetal, polycarbonate, polyvinyl chloride, polysulfone, polystyrene, polyacrylonitrile, polyacrylate and polyfluorocarbon; b) irradiating the coated substrate to graft copolymerize said monomer to said substrate; c) coating a cyanoacrylate adhesive on at least one of (i) the graft-copolymerized monomer surface of the first substrate and (ii) a surface of the second substrate to be adhered; d) contacting said surfaces (i) and (ii); and e) allowing the cyanoacrylate adhesive to cure. An article having a polymeric first substrate adhered to a second substrate with a cyanoacrylate adhesive prepared according to the method of claim 7.

Inventors: HARMON KIMBERLY K, KOBE JAMES J, SIMPSON JOHN T, WRIGHT CHARLES D, HARMON, KIMBERLY K., KOBE, JAMES J., SIMPSON, JOHN T., WRIGHT, CHARLES D.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1988
Main classification: C08J7
IPC codes: C08J5, C08J7, C09J4, C08F291