Photosensor device

Abstract: A photosensor device, comprises a semiconductor layer formed on an insulating substrate and composed of first semiconductor areas (e.g. 3, 13) of one conductivity type or intrinsic type and second semiconductor areas (e.g. 4, 24, 14) of the other conductivity type. A horizontal type photosensor is formed by a junction between said first semiconductor areas and second semiconductor areas while a field effect transistor constituting a processing circuit for the sensor signal is simultaneously formed with a source and a drain composed of said second semiconductor areas (e.g. 14, 24) and with a channel area composed of said first semi-­ conductor area (e.g. 13) positioned between said source and drain.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a photosensor device for photoelectric conversion, and more particularly to a photosensor device for photoelectric conversion adapted for use for example in a long image sensor. Related Background Art Conventional photosensor devices, such as CCD, have been prepared by diffusion processes on a semi-conductor substrate. Therefore the size thereof is limited, at maximum, to the size of the semiconductor substrate, and it has been difficult to obtain a long sensor array. Also in case of forming the photosensor device on another substrate as a system, there is required a process of adhering a separately prepared semiconductor sensor chip on the substrate, thus requiring a number of steps and resulting in a lowered accuracy of registration. On the other hand, for obtaining wider freedom of selection of substrate, there has been developed a photosensor device utilizing amorhpous silicon. However, transistors based on amorphous silicon have been inevitably slow in the function. In order to overcome this drawback, there has been proposed, in the Japanese Laid-Open Patent 59-126666, a method of forming a sensor portion with amorphous silicon and a transistor portion with polycrystalline silicon. However this method requires an increased number of steps and involves a high cost, since the photosensor based on amorphous silicon is prepared after the polycrystalline silicon transistor is prepared by an ordinary IC process. In this manner it has been difficult to produce the photosensor device of satisfactory performance and low cost on a non-semiconductor substrate. US-A-4236831 proposes an arrangement in which a layer of polycrystalline silicon is formed in a silicon dioxide layer which extends over a silicon substrate. The polycrystalline silicon layer is formed into alternating p-type and n-type strips, and alternative pn junctions are shorted by metallic shorting bars in ohmic contact with both of the regions forming the junction. The un-shorted juctions each provide a pn junction photodiode, so that the structure as a whole provides a series string of photodiodes. One end of the polycrystalline silicon layer is electrically connected to the semiconductor substrate, whereas the other end is brought close to the semiconductor substrate to act as a gate for a field effect transistor having source, channel and drain regions in the semiconductor substrate, so that the voltages developed across the individual photodiodes are summed by the series connection and the total voltage is applied between the gate of the FET and the semiconductor substrate. US-A-4346395 proposes an arrangement in which a silicon layer is grown epitaxially on a sapphire substrate. A photodiode is formed by making a lower part of the layer n-type and an upper part of the layer p-type so as to form a horizontal pn junction, and at one side of the photodiode the p-type layer extends down to the sapphire substrate and is adjacent to another n region and then another p region, so as to provide an MOS transistor switch connected to the photodiode. SUMMARY OF THE INVENTION According to the present invention there is provided a photosensor device as set out in claim 1. Claims 2 to 9 set out optional features. The invention also provides a method of making a photosensor device as set out in claim 10. In this specification, the term "horizontal type photosensor" is used to refer to a photosensor in which the junction of the first and second semiconductor areas of the photosensor is perpendicular to the surface. In an embodiment, a photosensor device of satisfactory performance can be obtained through a simple process, by forming the second conductivity type semiconductor areas in desired parts of the semiconductor layer formed on the insulating substrate, thus simultaneously forming the horizontal type photosensor and the field effect transistor (FET) at the junction of said semiconductor areas. In an embodiment, the photosensor provides a horizontal type photodiode of stripe structure which is highly sensitive to the light of short wavelengths. In another embodiment, there is provided a photosensor device which is highly sensitive to the light of short wavelengths, by forming the photosensor as a horizontal type phototransistor in which the base area has a rectangular wave shape. The horizontal type structure of the photosensor facilitates formation of rectangular wave-shaped base portion. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a perspective view of a photosensor device constituting a first embodiment of the present invention; Fig. 2 is an equivalent circuit diagram of the photosensor device shown in Fig. 1; Fig. 3 is a plan view of a photosensor device constituting a second embodiment of the present invention; Fig. 4 is a cross-secontional view of the device shown in Fig. 3; Fig. 5 is an equivalent circuit diagram of the photosensor device shown in Fig. 3; Figs. 6A to 6D are cross-sectional views showing manufacturing steps of a third embodiment of the present invention; Fig. 7 is a schematic view showing crystal growth of a large-grain polycrystalline silicon film; Fig. 8 is a chart showing the influence of nucleation density controlling gas on the nucleation density of large-grain polycrystalline silicon film; Fig. 9 is a chart showing the influence of nucleation density controlling gas on the crystal size of large-grain polycrystalline silicon film; Fig. 10 is a chart showing the influence of pressure on the crystal size of large-grain poIycrystalline silicon film: Fig. 11 is a chart showing the influence of temperature on the nucleation density of large-grain polycrystalline silicon film; Fig. 12 is a plan view of a device constituting a fourth embodiment of the present invention; Fig. 13 is a cross-sectional view of the device shown in Fig. 12: Fig. 14 is an equivalent circuit diagram of the device shown in Fig. 12: Fig. 15 is a plan view showing a fifth embodiment of the present invention; Fig. 16 is a cross-sectional view of the device shown in Fig. 15: and Fig. 17 is an equivalent circuit diagram of the device shown in Fig. 15. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS (First embodiment) Fig. 1 is a perspective view of a photosensor device constituting a first embodiment of the present invention, and Fig. 2 is an equivalent circuit diagram of the device shown in Fig. 1. In Fig. 1, a thin semiconductor film 2 of n-or i-type is formed on a substrate 1. The substrate 1 is composed of a transparent substrate such as quartz or glass if the device receives the light through the substrate. The first semiconductor film can be composed of polycrystalline silicon or monocrystalline silicon. The polycrystalline silicon can be of a grain size not exceeding 50 nm (500 Å) obtained by deposition with CVD under reduced pressure from ordinary silane (SiH 4 ) gas, but is preferably large-grain polycrystalline silicon proposed by the present applicant in the Japanese Patent Applications 62-73629 and 62-73630 for realizing a photosensor device of higher performance. Also the monocrystalline silicon may be obtained by recrystallization with laser annealing or by monocrystal growth from a seed composed of a small SiH 4 pattern on SiO 2 followed by flattening. Said large-grain polycrystalline silicon is most suitable for the present embodiment, due to the ease of forming process. Said large-grain polycrystalline silicon will be detailedly explained later. The film thickness is determined in consideration of the spectral sensitivity, but is generally in the order of 1 µm. The semiconductor film of n- or i-type explained above is doped with a p-type impurity such as boron in predetermined areas 4, 24, 14, down to the substrate. The diffusion can be achieved by gaseous diffusion from BBr 3 or the like utilizing a diffusion mask composed of SiO 2 or Si 3 N 4 in an unnecessary area 3, or diffusion from a BSG film, or by ion implantation utilizing a photoresist mask. Thus there are simultaneously formed a P + -area 4 of a photosensor 7, and a source 24 and a drain 14 of a MOS-FET 8. The photosensor 7 composed of P + -n type horizontal photodiode has a striped arrangement of P + -areas 4 and n- or i-type areas 3. The horizontal type photodiode has a high spectral sensitivity for shorter wavelength (blue side) since the absence of a high concentration layer at the surface of n- or i-type area allows the utilization of the carriers, generated at the surface by the light of short wavelength, for generating a photocurrent without immediate recombination. Also in the large-grain polycrystalline silicon mentioned above, a larger photocurrent can be obtained with a smaller pitch of the stripe pattern, in consideration of the diffusion length of the carriers. In the MOS-FET 8, source and drain areas 14, 24 of P + -type are formed across the n- or i-type channel 13, and a gate 6 is formed on a gate film 5 of a thickness of about 100 nm (1000 Å). Said gate film is preferably composed of a thermally oxidized semiconductor film in consideration of the functional characteristic, but a SiO 2 film formed by CVD under reduced pressure or a Si 3 N 4 film formed by plasma CVD in consideration of the manufacturing cost. The gate is formed by depositing polycrystalline or amorphous silicon or aluminum and patterning it into a width so as to partially cover the source and drain areas as shown in Fig. 1. In Fig. 1 the contacts and wiring are omitted. As will be apparent from the equivalent circuit shown in Fig. 2, the photosensor device of the present embodiment is capable of switching the output from the photodiode 7 of high sensitivity with the high-speed MOS-FET 8, so that a high-speed image reading is possible even when a sensor array is formed from a large number of sensor elements. When an intrinsic semiconductor layer is employed, the channel area is preferably doped lightly with an n-type impurity. In the following there will be explained the process of forming said large-grain polycrystalline silicon film. Fig. 7 conceptually illustrates the growth of a large-grain polycrystalline film on a deposition plane of a SiO 2 film 71. Fig. 7A shows a state in which nuclei are formed; Fig. 7B shows a state in which said nuclei are grown into mutually contacting islands: and Fig. 7C shows a state in which a continuous film 73 is obtained by further growth. The nucleation density in Fig. 7A depends greatly on the interaction between the incoming atoms and the deposition surface, but also on the depositing conditions such as gas species, pressure and temperature. Fig. 8 shows the change in the nucleation density (N D ), in the formation of silicon nuclei on a Si 3 N 4 or SiO 2 film, as a function of the flow rate ratio of HCl as a depositing parameter. The Si 3 N 4 film was formed by low pressure CVD, while the SiO 2 film was formed by normal pressure CVD. There were employed SiH 2 Cl 2 as source gas and H 2 as carrier gas, and the reaction was conducted under a reduced pressure of about 20 kPa (150 Torr) with a composition SiH 2 Cl 2 : HCl:H 2 = 1.2 : x : 100 (ℓ/min), with a substrate temperature of 950°C. Curves 81 and 82 respectively show the nucleation density on the Si 3 N 4 film and the SiO 2 film. As will be apparent from Fig. 8, the nucleation density is governed by the deposition surface, but is more strongly dependent and is controllable by the flow rate ratio (mixing ratio) of HCl. Consequently HCl can be considered as a nucleation density controlling gas. Fig. 9 shows the relationship between the amount of HCl and the average grain size. A large-grain polycrystalline silicon film with an average grain size of 3 µm could be obtained by the deposition for 30 minutes with a HCl flow rate of 1.1 ℓ/min which corresponds to a nucleation density of 10 7 /cm 2 . Since the average grain size is inversely proportional to the square root of the nucleation density, an average grain size exceeding 1 µm can be obtained by maintaining the nucleation density at 10 8 /cm 2 or lower. However, the grain size becomes uneven of the nucleation density is significantly low, because of a statistical fluctuation and a fact that the distance between nuclei becomes no longer negligible with respect to the diffusion length of silicon atoms on the deposition surface. A nucleation density equal to or higher than 10 6 /cm 2 , or an average grain size equal to or lower than 10 µm was experimentally confirmed practical for the actual semiconductor device formation. As shown in Fig. 8, the SiO 2 film, showing a nucleation density lower by about two powers often than that on the Si 3 N 4 film, is suitable for obtaining a polycrystalline film of larger grain size. Fig. 10 shows the pressure dependence of the average grain size. The depositing conditions are same as those shown in Fig. 9, except that the HCl flow rate is 1.1 ℓ/min. A lower pressure reduces the nucleation density and provides a more uniform distribution of nuclei, thus giving rise to more uniform grain size. Other conditions employed were SiH 2 Cl 2 : HCl : H 2 = 1.2 : 1.1 : 100 (ℓ/min), a temperature of 960°C and a deposition time of 30 minutes. The effect of lower pressure is particularly evident at 200 Torr or lower. Fig. 11 shows the temperature dependence of the average grain size and the deposited film thickness. Other depositing conditions employed were SiH 2 Cl 2 : HCl H 2 = 1.2 : 10 : 100 (ℓ/min), a pressure of 20 kPa (150 Torr) and a deposition time of 10 minutes. The average grain size increases as the temperature is lowered from 1000°C. However, as will be apparent from the curve of the deposited film thickness, the growth rate decreases simultaneously and becomes almost zero at 850°C. Consequently the lower temperature limit is determined by the growth rate. The crystalline nature of each grain is naturally better at a higher temperature, so that a suitable temperature can be selected according to the device specifications. The foregoing explanation is limited to the use of SiH 2 Cl 2 as the source gas, but similar tendencies can be obtained with other silicon-containing source gases such as SiHCl 2 , SiH 2 or SiCl 4 . Also a same process is applicable to a compound semiconductor such as GaAs by employing a 60:1 mixture of trimethyl gallium (TMG) and arsine (AsH 3 ). In this case the deposition can be conducted with H 2 as the carrier gas, with a temperature equal to or higher than 600°C and a pressure of 1 1 / 3 to 2 2 / 3 kPa (10 to 20 Torr). In addition to HCl, the nucleation density controlling gas can be composed of Cl 2 , F 2 , CCl 4 or CCl 2 F 2 which react with the semiconductor material. The surface of the large-grain polycrystalline silicon film formed on a transparent quartz substrate as explained above, was subjected to mechanochemical polishing and to the preparation of a p-channel MOS-FET. There was obtained a hole mobility of about 70 cm 2 /V·sec which is significantly higher than that in the ordinary polycrystalline silicon film. Thus a high speed image reading is possible even when an array is formed with a large number of phototransistors. In case an i-type semiconductor layer is employed, the channel area is preferably doped lightly with an n-type impurity. As explained in the foregoing, the present embodiment provides a photosensor device which shows a high photosensitivity at the short wavelength due to the use of a horizontal type photodiode, which is capable of transmitting weak photocurrent without loss in the wirings because the highly doped area (P + ) of the photodiode constitutes the drain area of the MOS-FET, and which can be produced with a very limited number of diffusion steps. (Second embodiment) Fig. 3 is a plan view of a second embodiment of the present invention, while Fig. 4 is a cross-sectional view of the device shown in Fig. 3, and Fig. 5 is an equivalent circuit diagram of the device shown in Fig. 3. In Fig. 3, an n-type semiconductor film 2 is doped with boron to simultaneously form P + -areas within a sensor area 4, source and drain areas 14, 24 and a MOS capacitance area 34. Then, after the formation of a gate film, a gate 16 of the MOS capacitance and a gate 6 of the MOS-FET are formed with n + -type polycrystalline silicon or n + -type amorphous silicon. There are provided contacts 12 for wiring. In the present embodiment, as shown by the equivalent circuit in Fig. 5, there is provided a capacitance 9 for accumulating the photocurrent. It is therefore suitable for a sensor array in which weak photocurrents are temporarily stored and sequentially read. Also the present embodiment reduces the steps for wiring and the leak of signal, and can effectively utilize the area of the substrate since the P + -area 4 of the sensor, the P + -area 34 of the MOS capacitance and the drain 14 of the MOS-FET are composed of a common diffusion area. Therefore the production yield high, and the present embodiment is advantageous for production. The structure of the sensor array is not shown in the foregoing embodiments, but a sensor array can be basically obtained by parallel arrangement of the device shown in Fig. 1 or 3. In this case each element has to be electrically insulated except the n-type area 3 of the sensor, so that the semiconductor film of each element has to be separated, for example by etching, from that of the neighboring elements. In the foregoing explanation, the n-type layer and the p-type layer may be mutually exchanged, and in such case, the intrinsic layer is used as a low concentration layer. (Third embodiment) Figs. 6A to 6D are cross-sectional views showing the process steps of a third embodiment of the present invention. In the following there will be explained the manufacturing process, with reference to Figs. 6A to 6D. On a transparent insulating substrate 1, there is deposited an n- or i-type semiconductor layer of low concentration. Then a mask 30 for impurity diffusion or ion implantation is formed in predetermined areas, and p-type areas are formed by the diffusion of a p-type impurity in the areas not covered by said mask (a). After the elimination of the mask, a gate oxide film 5 is formed, and a contact hole 31 is formed in a desired position in the n- or i-type area (b). Subsequently an n + -type polycrystalline silicon of high concentration or amorphous silicon is deposited thereon, and is eliminated by etching excluding a contact portion 36 and a gate portion 6 (c). Then an interlayer insulating film 10 is deposited on the entire area. There are formed a second contact hole and an electrode 11 (d). Thermal annealing in the process causes the diffusion of an n-type impurity from the n + -type polycrystalline silicon (or n + -type amorphous silicon) layer 36 of high concentration into the n- or i-type area of low concentration, thereby forming an n + -type area 40. The above-explained process provided a photosensor device with satisfactory ohmic contact. The process of the present embodiment is capable of providing reliable contact with fewer process steps, without the additional n-type diffusion of high concentration required in the conventional process. As explained in the foregoing, the present embodiment is capable of forming a switch and a processing circuit together with a photosensor on a transparent insulating substrate with a reduced number of steps, thereby easily providing a photosensor device of wide application. Besides, since the photosensor is horizontal type, the junctions can be easily formed in a stripe pattern, and the area of the sensor can be effectively utilized. Also the sensor array obtained with the present embodiment can be utilized for realizing a high-speed image reader. (Fourth embodiment) Figs. 12 and 13 are respectively a plan view and a lateral view of a fourth embodiment of the present invention, and Fig. 14 is an equivalent circuit diagram of the device shown in Fig. 12. In Figs. 12 and 13, in desired areas of a semiconductor layer 102 of a first conductive type, there are formed semiconductor layers 102-3, 102-4, 102-5 of a second conductive type. The layers 102-3 and 102-4 constitute emitter and collector of a phototransistor 105 shown in Fig. 14, and the layer 102-4 and 102-5 constitute source and drain of a MOS transistor 106. Base 102-1 of the phototransistor 105 and channel area 102-2 of the MOS transistor 106 are composed of the semiconductor layer of the first conductive type. In order to maximize the light receiving area, the phototransistor is constructed in a rectangular wave form. As shown in Fig. 12, an n- or i-type semiconductor film 102 is formed on a substrate 101. Said substrate is composed of a transparent substrate such as quartz or glass, if the device receives the light through the substrate. The semiconductor film is composed of polycrystalline silicon or monocrystalline silicon. The polycrystalline silicon is preferably, rather than usual polycrystalline silicon of a grain size of 50 nm (500 Å) or lower deposited by low pressure CVD from silane (SiH 4 ) gas, the large-grain polycrystalline silicon proposed by the present applicant in the Japanese Patent Applications 62-73629 and 62-73630 for obtaining a photosensor device of high performance. The monocrystalline silicon can be that recrystallized by laser annealing or that obtained by monocrystalline growth from a seed composed of a small Si 3 N 4 pattern on SiO 2 followed by crystal flattening. The large-grain polycrystalline silicon is most suitable for the present embodiment because of ease of formation, as has already been explained. The n- or i-type semiconductor film thus formed is subjected to the diffusion of a p-type impurity, such as boron, in desired areas. Thus there are simultaneously formed the emitter and collector of the phototransistor and the source and drain of the MOS-FET. The phototransistor is composed of a horizontal p + -n (or i)-p + transistor. Such horizontal phototransistor has a high spectral sensitivity at the short wavelength (blue side), because the carriers generated at the surface by the light of short wavelength can be utilized without immediate recombination due to the absence of a high concentration layer at the surface of the n- or i-type base area. Also in the large-grain polycrystalline silicon mentioned above, the width of the base area should be as small as possible for obtaining a large signal current as the diffusion length of the carriers is not so large. In the MOS-FET, source and drain of p + -type are formed across an n- or i-type channel area, and a gate electrode 104 is formed on a gate insulating film 103 of a thickness of about 100 nm (100 Å). The gate insulating film 103 is preferably composed of a thermally oxidized semiconductor film in consideration of the functional characteristic, but a SiO 2 film formed by low pressure CVD or Si 3 N 4 film formed by plasma CVD in terms of cost. Also the gate electrode is formed by depositing an n + -type polycrystalline silicon or aluminum and patterning it on the channel area 102-5, as shown in Fig. 12, with a registration margin to partially cover the source and drain 102-4, 102-5. In Fig. 12 the gate insulating film 103 is omitted. As will be apparent from the equivalent circuit shown in Fig. 14, in the photosensor device of the present embodiment, the phototransistor of the above-explained structure is biased between the emitter 102-3 and the collector 102-4 in such a manner that the base 102-1 and the collector 102-4 are inversely biased, and the base area is irradiated with light. Thus pairs of electrons and holes are generated in the base area, and the carriers of one kind diffuse into the collector area due to the inverse bias between the base and the collector, while those of the other kind are accumulated in the base area. If a current is supplied from the emitter in this state, it flows to the collector due to the effect of the carriers accumulated in the base area. The collector current in this state is about h fe times of the photocurrent generated between the base and the collector, so that a very weak light signal can also be detected. The collector current thus obtained is supplied to the drain 102-5 and processed therein by turing on the MOS transistor. The process of forming said large-grain polycrystalline silicon is same as that already explained in reference to Figs. 7 to 11, and will not, therefore, be explained again. (Fifth embodiment) Fig. 15 is a plan view of a fifth embodiment of the present invention, Fig. 16 is a lateral view of the device shown in Fig. 15, and Fig. 17 is an equivalent circuit diagram of the device shown in Fig. 15. In the present embodiment, a MOS capacitance 107 is formed on an area 102-4 constituting the collector of the phototransistor 105 and the source of the MOS transistor 106, whereby the photocarriers generated by the phototransistor 105 in response to light can be temporarily stored in said MOS capacitance 107 and supplied to a processing circuit by sequentially turning on the MOS transistors 6. The present embodiment is therefore suitable for detecting a very small current. The present embodiment can reduce the steps of wirings and the current leak and effectively utilize the area, since the collector of the phototransistor, the p + -area of the MOS capacitance and the drain of the MOS-FET are composed of a common doped area. Thus the present embodiment can achieve a high production yield and is therefore advantageous for manufacture. The structure of the sensor array has not been shown in the foregoing fourth and fifth embodiments, but a sensor array can be basically obtained by a parallel arrangement of the element shown in Fig. 12 or 15. In this case, each element has to be electrically insulated from the neighboring elements except for n- or i-type area 102-1 of the sensor, and this can be achieved by separating the semiconductor film of each element for example by etching from that of the neighboring elements. The present embodiment enables a simplified process and a lower cost, since the phototransistor and the signal processing circuit therefor can be simultaneously formed by a impurity diffusing step. Also the present embodiment enables easy formation of a phototransistor capable of detecting a very weak light signal. Furthermore, the use of horizontal structure for the device enables a rectangular waving form of the junction of the phototransistor, thereby achieving effective utilization of the light receiving area.

Claims: A photosensor device comprising a photosensor (7) and a lateral field effect transistor (8) formed in a layer (2, 102) of semiconductor material on an insulating substrate (1, 101), the photosensor (7) comprising a first area (3, 102-1) of intrinsic or first conductivity type semiconductor formed in said layer (2,102) and a second area (4, 102-4) of second conductivity type semiconductor formed in said layer (2,102) and the field effect transistor (8) being connected to switch the output of the photosensor (7), the source and drain of the field effect transistor comprising second conductivity type semiconductor formed in said layer (2,102) and the channel (13, 102-2) comprising intrinsic or first conductivity type semiconductor formed between said source and said drain in said layer (2,102), characterised in that the first and second areas (3, 4; 102-1, 102-4) of the photosensor are positioned one beside the other and interdigitated with each other in a pattern of plural stripes of portions of the first area and portions of the second area, and the junction between them extends perpendicular to the surface of said layer. A photosensor device according to claim 1 in which the junction between the said stripe portions of the first and second areas of the photosensor has a rectangular waving form. A photosensor device according to claim 1 or claim 2 in which the photosensor (7) is a photodiode (7) formed by the first and second areas. A photosensor device according to claim 1 or claim 2 in which the photosensor is a phototransistor (105) formed by the first and second areas and a third area (102-3) of second conductivity type semiconductor, the first area forming the base. A photosensor device according to claim 4 in which the base of the phototransistor has a rectangular waving form. A photosensor device according to any one of the preceding claims comprising a capacitor (9, 107) between the photosensor and the field effect transistor, the capacitor including an area (34) of second conductivity type in the layer of semiconductor material. A photosensor device according to claim 6 in which the said area (34) of the capacitor comprises a portion of the said second area (4, 102-4) of semiconductor. A photosensor device according to any one of the preceding claims in which the field effect transistor comprises: a part of the said second area; a further area (13,102-2) of the first conductivity type or intrinsic semiconductor for the channel, and a further area (24,102-5) of the second conductivity type semiconductor, all the said areas being formed in the layer of semiconductor material. A photosensor device according to any one of the preceding claims in which the layer (2, 102) of semiconductor material comprises polycrystalline silicon having a grain size of 0.5 µm or larger. A method of making a photosensor device according to any one of the preceding claims in which the layer of semiconductor material is provided as an intrinsic or first conductivity type layer, and the second conductivity type areas of the photosensor and the field effect transistor are formed simultaneously with each other.

Inventors: KONDO SHIGEKI, MIZUTANI HIDEMASA, KONDO, SHIGEKI, MIZUTANI, HIDEMASA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1988
Main classification: H01L31
IPC codes: H01L31