PRESSURE SENSITIVE ADHESIVE COMPOSITIONS FOR USE ON VINYL SUBSTRATES

Abstract: Adhesive compositions having a Tg of -45 to -25°C suitable for application to plasticized polyvinyl chloride comprising 25-48% by weight of a vinyl ester of an alkanoic acid; 10-25% by weight ethylene; 40-70% by weight of an acrylic acid ester; 1 to 10% by weight of tertiary octyl acrylamide; and 1 to 10% by weight of a mono-carboxylic acid.

Description: This invention relates to pressure sensitive adhesive compositions particularly adapted for use on vinyl substrates. These adhesives comprise polymers of ethylene, a vinyl ester, tertiary octyl acrylamide, an acrylic acid ester, and an unsaturated mono-carboxylic acid. Pressure-sensitive adhesives function to provide instantaneous adhesion when applied under light pressure. They are characterized by having a built-in capacity to secure this adhesion to a surface without activation, such as by treatment with solvents or heat, and also by having sufficient internal strength so that the adhesive material will not rupture before the bond between the adhesive material and the surface ruptures. The capacity to obtain instantaneous adhesion is usually expressed as the amount of "tack" or "tackiness". Ordinarily it is desirable to obtain as much tack as possible without losing a significant amount of internal strength (cohesion). The latter balance of adhesive and cohesive properties has been difficult to obtain in adhesive polymers since monomers conventionally incorporated into the polymers to increase the cohesion strength generally result in a decrease in adhesive tack. A specific class of pressure sensitive adhesives are used on vinyl substrates such as are utilized in a wide variety of industrial applications including as vinyl roof tops in automobiles, for decorative trim as in vinyl labels, and decals and in specialty types. Unlike common polyolefin films such as polyethylene and polypropylene, these polyvinyl chloride (PVC) films by nature of their process requirements and high glass transition temperature, require formulation with a number of additives. Some of these are migratory components and will affect the long-term performance of a vinyl decal or label. The amounts and types of additives vary among vinyl formulations, therefore, a wide range of vinyl characteristics are available. A typical flexible PVC film formulation contains a number of additives including plasticizers. Plasticizers used include the migratory monomeric types such as phthalate esters (e.g., dioctylphthalate) or the less migratory polymeric plasticizers (e.g., polyesters, epoxidized soybean oils). These applications require stringent requirements on the adhesive composition. In particular, the vinyl substrates contain substantial amounts of these plasticizers which tend to migrate into the adhesive, especially after aging, the migration of which will destroy the adhesive and cause the bond to fail. Thus, the use of adhesive-coated flexible polyvinylchloride films has traditionally been plagued, to various degrees, by deterioration of properties due to migration of plasticizer out of the PVC film into the adhesive coating. The degree to which this occurs is dependent on the PVC formulation and the adhesive used. In addition to resistance to this plasticizer migration on aging, adhesives for use on vinyl decals must also possess the previously discussed high initial peel values both cohesive and adhesive strength and must inhibit resistance to shrinkage. Two of the most important factors influencing the real-life performance of an adhesive-coated vinyl decal or label are the plasticizer type and level in a PVC film. These additives which allow use of PVC for flexible application are a major cause of the deterioration of polymer coating applied to PVC. As a result of their more migratory character, monomeric plasticizers will have a bigger effect on adhesive properties than will polymeric plasticizers. All else being equal, the higher the content of monomeric plasticizer in a vinyl film, the more deterioration experienced by the adhesive-coated decal as a function of time. To accurately predict the extent of plasticizer migration and its effects on adhesive properties, it is important to address what happens to the plasticizer when it leaves the vinyl film. If the adhesive totally blocks out the plasticizer, the result is an accumulation of plasticizer at the adhesive-vinyl surface. This can result in bond failure at this boundary. If the adhesive is too accepting of the plasticizer, the viscoelastic properties of the adhesive deteriorate resulting in a weak, leggy polymer film. A third possibility involves migration of the plasticizer out of the PVC, through the adhesive mass, to the adhesive-­ substrate interface. This can retard or destroy bond formation. The destiny of the plasticizer after the migration process is actually a combination of these three extremes. The degree to which one case predominates is dependent on adhesive, substrate and the PVC backing. The most obvious indication of plasticizer migration related adhesive deterioration is the degradation of adhesive properties as a function of aging on vinyl. Many adhesive systems display a dramatic drop off in peel adhesion and creep resistance during contact with plasticized vinyl; however, through proper polymer design, control over the migration process and the subsequent effect on the pressure sensitive adhesive properties can be achieved. In contrast to the adhesive compositions of the prior art, the problems associated with plasticizer migration are overcome in accordance with the present invention by use of a pressure sensitive adhesive comprising 25-48% by weight of a vinyl ester of an alkanoic acid; 10-25% by weight ethylene; 40-70% by weight of an acrylic acid ester containing 4 to 12 carbon atoms in the ester moiety, 1 to 10% of tertiary octyl acrylamide; and 1 to 10% by weight of a mono-carboxylic acid. The adhesives are characterized by superior resistance to plasticizer migration, resulting in excellent overall adhesive properties after storage of the adhesive coated substrates accompanied by high initial peel strength. As such, the pressure sensitive adhesives find particular application for adhering vinyl substrates and especially for use as adhesive for vinyl decals. The vinyl esters utilized herein are the esters of alkanoic acids having from one to about 13 carbon atoms. Typical examples include; vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl valerate, vinyl-2-ethyl-hexanoate, vinyl isooctanoate, vinyl nonate, vinyl decanoate, vinyl pivalate, vinyl versatate, etc. Of the foregoing, vinyl acetate is the preferred monomer because of its ready availability and low cost. The vinyl ester is present in the copolymer in amounts of about 25 to 48% by weight, preferably 30 to 40%. The acrylic acid esters are prepared from alcohols, such as alkanols having from 4 to 12 carbon atoms. Preferably, alkanols having from 6 to 10 carbon atoms are used, and especially the inexpensive 2-­ ethylhexyl acrylate. Other examples of such acrylic acid esters are butyl acrylate, hexyl acrylate, heptyl acrylate, octyl acrylate, n-decyl acrylate and dodecyl acrylate. The amounts by weight used range from 40% to 70% by weight, preferably 50% to 60% by weight. The unsaturated mono-carboxylic acids utilized herein include, for example, acrylic and methacrylic acid or the half esters of maleic acid such as monoethyl, monobutyl or monooctyl maleate, with acrylic acid or methacrylic acid being preferred. The acid is present in an amount of 1 to 10% by weight, preferably 2 to 6%. In all cases, the T g of the resultant pressure sensitive adhesive should be within the range of about -45 to -25°C, so the choice of the particular comonomers employed as well as their respective amounts should be regulated accordingly. In addition, certain copolymerizable monomers which assist in the stability of the copolymer emulsion, e.g., vinyl sulfonic acid, are also useful herein as latex stabilizers. These optionally present monomers, if employed, are added in very low amounts of from 0.1 to about 2% by weight of the monomer mixture. Conventional batch, semi-batch or continuous emulsion polymerization procedures may be utilized herein. Generally, the monomers are poly­ merized in an aqueous medium under pressures not exceeding 100 atmospheres in the presence of a catalyst and at least one emulsifying agent. The quantity of ethylene entering into the copolymer is influenced by the pressure, the agitation, and the viscosity of the polymerization medium. Thus, to increase the ethylene content of the copolymer, higher pressures are employed. A pressure of at least about 10 atmospheres is most suitably employed. The mixture is thoroughly agitated to dissolve the ethylene, agitation being continued until substantial equilibrium is achieved. This generally requires about 15 minutes. However, less time may be required depending upon the vessel, the efficiency of agitation, the specific system, and the like. Suitable as polymerization catalysts are the water-soluble free-­ radical-formers generally used in emulsion polymerization, such as hydrogen peroxide, sodium persulfate, potassium persulfate and ammonium persulfate, as well as tert-butyl hydroperoxide, in amounts of between 0.01 and 3% by weight, preferably 0.01 and 1% by weight based on the total amount of the emulsion. They can be used alone or together with reducing agents such as sodium formaldehyde-sulfoxylate, ferrous salts, sodium dithionite, sodium hydrogen sulfite, sodium sulfite, sodium thiosulfate, as redox catalysts in amounts of 0.01 to 3% by weight, preferably 0.01 to 1% by weight, based on the total amount of the emulsion. The free-radi­ cal-formers can be charged in the aqueous emulsifier solution or be added during the polymerization in doses. The polymerization is carried out at a pH of between 2 and 7, preferably between 3 and 5. In order to maintain the pH range, it may be useful to work in the presence of customary buffer systems, for example, in the presence of alkali metal acetates, alkali metal carbonates, alkali metal phosphates. Polymerization regulators, like mercaptans, aldehydes, chloroform, ethylene chloride, and trichloroethylene, can also be added in some cases. The emulsifying agents are those generally used in emulsion polymerization, as well as optionally present protective colloids. It is also possible to use emulsifiers alone or in mixtures with protective colloids. The emulsifiers can be anionic, cationic, nonionic surface-active compounds or mixtures thereof. Suitable anionic emulsifiers are, for example, alkyl sulfonates, alkylaryl sulfonates, alkyl sulfates, sulfates of hydroxylalkanols, alkyl and alkylaryl disulfonates, sulfonated fatty acids, sulfates and phosphates polyethyoxylated alkanols and alkyl­ phenols, as well as esters of sulfosuccinic acid. Suitable cationic emulsifiers are, for example, alkyl quaternary ammonium salts, and alkyl quaternary phosphonium salts. Examples of suitable non-ionic emulsifiers are the addition products of 5 to 50 mols of ethylene oxide adducted to straight-chained and branch-chained alkanols with 6 to 22 carbon atoms, or alkylphenols, or higher fatty acids, or higher fatty acid amides, or primary and secondary high alkyl amines; as well as block copolymers of propylene oxide with ethylene oxide and mixtures thereof. When combin­ ations of emulsifying agents are used, it is advantageous to use a rela­ tively hydrophobic emulsifying agent in combination with a relatively hydrophilic agent. The amount of emulsifying agent is generally from about 1 to about 10, preferably from about 2 to about 8, weight percent of the monomers used in the polymerization. The emulsifier used in the polymerization can also be added, in its entirety, to the initial charge to the polymerization zone or a portion of the emulsifier, e.g. from 90 to 25 percent thereof, can be added continuously or intermittently during polymerization. Various protective colloids may also be used in placed of or in addi­ tion to the emulsifiers described above. Suitable colloids include partially acetylated polyvinyl alcohol, e.g., up to 50 percent acetylated, casein, hydroxyethyl starch, carboxymethyl cellulose, gum arabic, and the like, as known in the art of synthetic emulsion polymer technology. In general, these colloids are used at levels of 0.05 to 4% by weight based on the total emulsion. The polymerization reaction is generally continued until the residual vinyl acetate monomer content is below about 1%. The completed reaction product is then allowed to cool to about room temperature, while sealed from the atmosphere. The adhesive emulsions are produced and used at relatively high solids contents, e.g. between 35 and 70%, preferably not less than 50%, although they may be diluted with water if desired. The particle size of the latex can be regulated by the quantity of nonionic or anionic emulsifying agent or protective colloid employed. To obtain smaller particles sizes, greater amounts of emulsifying agents are used. As a general rule, the greater the amount of the emulsifying agent employed, the smaller the average particle size. If desired, conventional additives may be incorporated into the novel adhesives of our invention in order to modify the properties thereof. Among these additives may be included thickeners, fillers or pigments, such as talc and clay, small amounts of tackifiers, etc. The emulsion adhesive is useful on any conventional tape or other face stock, especially vinyl substrates such as vinyl films or foils. The adhesive may be applied using conventional techniques. Typical methods involve application of the adhesive onto a release liner by use of mechanical coating processes such as air knife, trailing blade, knife coater, reverse roll or gravure coating techniques. The adhesive is allowed to dry at room temperature and then oven dried at about 250°F for 10 minutes. The coated release liner may then be laminated to the face stock by a nip roll using pressure between a rubber roll and a steel roll. This technique effects a transfer of the adhesive mass to the face stock with a minimum of penetration. Example 1 This example illustrates the polymerization method used in preparing pressure sensitive adhesives of the present invention. A 10 liter stainless steel autoclave equipped with heating/cooling means, variable rate stirrer and means of metering monomers and initiators was employed. To the 10 liter autoclave was charged 450 g (of a 20% w/w solution) sodium alkyl aryl polyethylene oxide sulphate (3 moles ethylene oxide), 40 g (of a 70% w/w solution in water) alkyl aryl polyethylene oxide (30 mole ethylene oxide), 90 g (of a 25% w/w solution in water) sodium vinyl suphonate, 2 g sodium formaldehyde sulphoxylate, 0.5 g sodium acetate, 5 g (of a 1% solution in water) ferrous sulphate solution and 2250 g water. After purging with nitrogen all the vinyl acetate (1400 g) was added and the reactor was pressurized to 650 psi with ethylene and equilibrated at 50°C for 15 minutes. The polymerization was started by metering in a solution of 50 g. tertiary butyl hydroperoxide in 250 g of water and 50 g sodium formaldehyde sulphoxylate in 250 g of water. The initiators were added at a uniform rate over a period of 5-1/4 hours. Concurrently added with the initiators over a period of 4 hrs was a pre-emulsified blend of 2600 g 2 ethylhexyl acrylate, 140 g methacrylic acid and 140 g tertiary octyl acrylamide in a solution of 450 g (of a 20% w/w solution in water) sodium alkyl aryl polyethylene oxide sulphate (3 mole ethylene oxide), 25 g (of a 70% w/w solution in water) alkyl aryl polyethylene oxide (30 mole ethylene oxide) and 1 g sodium acetate in 400 g water. During the polymerization, the temperature of the reaction was maintained at 55-60°C by means of cooling and at the end of the reaction, the emulsion was transformed to an evacuated vessel (30 liter) to remove residual ethylene from the system. Composition and analysis of the latex is given in Table 1. Using the general procedure described above, seven additional emulsions were prepared varying the amounts and/or monomeric compositions. The major monomers and their respective amounts are shown in Table I (Ex. 2-8). In order to demonstrate the necessity for the use of the t-octyl acrylamide component additional emulsions were prepared and tested as adhesives. In Example 9, no t-octyl acrylamide was employed; Example 10 and 11 utilized acrylamide and methacrylamide such as are used in U.S. Pat. No. 4,522,516; Example 12 utilized isobutoxy methyl acrylamide and Example 13 utilized N-methylol acrylamide. Each emulsion adhesive was then coated on a plasticized vinyl film and dried in an oven for 5 minutes at 105°C. The resulting dry adhesive deposition was 20 mg./in². This coating was then tested for peel strength according to the Pressure Sensitive Tape Council, Test Method No. 1, modified here to vary the dwell time between placing the coating in contact with the stainless steel test panel and measuring the peel strength. In addition, the bonded test specimen was heat aged as indicated in Table II to accelerate any tendency to lose adhesion on aging on the PVC substrate due to plasticizer migration into the polymer. The results show the superior retention of adhesive properties of the instant polymers (Ex. 1-8) compared to the controls and/or those of the prior art (Ex. 9-13) when subjected to aging on PVC film (vinyl). To further illustrate the differences in properties between the compositions of the 4,522,516, the emulsion prepared in Example 1 was compared for moisture and humidity resistance with that of Example 10. The testing procedure described above was respected with the samples being exposed for 1 week at 100°F and 100% relative humidity and also soaked 1 week in water at room temperature. The results of the testing are shown in Table III. The results again show the improved performance of the adhesives of the present invention, particularly with respect to their water resistance properties.

Claims: 1. Plasticized polyvinyl chloride substrates coated with a pressure sensitive adhesive composition comprising 25-48% by weight of a vinyl ester of a alkanoic acid; selected from the group consisting of vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl valerate, vinyl-2-ethyl-hexanoate, vinyl isooctanoate, vinyl nonate, vinyl decanoate, vinyl pivalate, and vinyl versatate; 10-25% by weight ethylene; 40-70% by weight of an acrylic acid ester containing 4 to 12 carbon atoms in the ester moiety; 1 to 10% by weight tertiary octyl acrylamide; and 1 to 10% by weight of a mono-carboxylic acid. 2. The substrate of Claim 1 wherein the polyvinyl chloride substrate is plasticized with a migratory plasticizer. 3. The substrate of Claim 2 wherein the plasticizer is a phthalate ester, a polyester or an epoxidized soybean oil. 4. The substrate of Claim 1 wherein the vinyl ester in the adhesive is vinyl acetate. 5. The substrate of Claim 1 wherein the vinyl ester is present in the adhesive in an amount of 30 to 40% by weight; the acrylic acid ester is present in the adhesive in an amount of 50 to 60% by weight and the tertiary octyl acrylamide is present in an amount of 3 to 6% by weight. 6. The substrate of Claim 1 wherein the acrylic acid ester is 2-ethyl-­ hexyl acrylate. 7. The substrate of Claim 1 wherein the acid in the adhesive is acrylic acid or methacrylic acid or a half ester of maleic acid. 8. Pressure sensitive adhesive compositions having a Tg of -45 to -25 C suitable for application to plasticized polyvinyl chloride films consisting essentially of 25-48% by weight a vinyl ester of a alkanoic acid selected from the group consisting of vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl valerate, vinyl-2-ethyl-hexanoate, vinyl isooctanoate, vinyl nonate, vinyl decanoate, vinyl pivalate, and vinyl versatate; 10-25% by weight ethylene; 40-70% by weight of an acrylic acid ester containing 4 to 12 carbon atoms in the ester moiety; 1 to 10% by weight of a mono-carboxylic acid and 1-­ 10% of tertiary octyl acrylamide. 9. The adhesive of Claim 8 wherein the vinyl ester is vinyl acetate, and the acrylic acid ester is 2-ethylhexyl acrylate. 10. The adhesive of Claim 8 wherein the vinyl ester is present in the adhesive in an amount of 30 to 40% by weight; the acrylic acid ester is present in an amount of 50 to 60% by weight; and the tertiary octyl acrylamide is present in an amount of 3 to 6% by weight. Claims for the following contracting State: ES 1. A method for producing coating plasticized polyvinyl chloride substrates by coating the substrates with a pressure sensitive adhesive composition comprising 25-48% by weight of a vinyl ester of an alkanoic acid; selected from the group consisting of vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl valerate, vinyl-2-ethyl-hexanoate, vinyl iso­ octanoate, vinyl nonate, vinyl decanoate, vinyl pivalate, and vinyl versatate; 10-25% by weight ethylene, 40-70% by weight of an acrylic acid ester containing 4 to 12 carbon atoms in the ester moiety; 1 to 10% by weight tertiary octyl acrylamide; and 1 to 10% by weight of a mono-carboxylic acid. 2. The method of Claim 1 wherein the polyvinyl chloride sub­ strate is plasticized with a migratory plasticizer. 3. The method of Claim 2 wherein the plasticizer is a phthalate ester, a polyester of an epoxidized soybean oil. 4. The method of Claim 1 wherein the vinyl ester in the adhesive is vinyl acetate. 5. The method of Claim 1 wherein the vinyl ester is present in the adhesive in an amount of 30 to 40% by weight; the acrylic acid ester is present in the adhesive in an amount of 50 to 60% by weight and the tertiary octyl acrylamide is present in an amount of 3 to 6% by weight. 6. The method of Claim 1 wherein the acrylic acid ester is 2-ethylhexyl acrylate. 7. The method of Claim 1 wherein the acid in the adhesive is acrylic acid or methacrylic acid or a half ester of maleic acid. 8. The use of a pressure sensitive composition having a Tg of -45 to -25°C for the application to plasticized polyvinyl chloride films consisting essentially of 25-48% by weight a vinyl ester of an alkanoic acid selected from the group consisting of vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl valerate, vinyl-2-ethyl-hexanoate, vinyl isooctanoate, vinyl nonate, vinyl decanoate, vinyl pivalate, and vinyl versatate; 10-25% by weight ethylene; 40-70% by weight of an acrylic acid ester containing 4 to 12 carbon atoms in the ester moiety; 1 to 10% by weight of a mono-carboxylic acid; and 1-10% by weight of tertiary octyl acrylamide. 9. The use of Claim 8 wherein the vinyl ester is vinyl acetate, and the acrylic acid ester is 2-ethylhexyl acrylate. 10. The use of Claim 8 wherein the vinyl ester is present in the adhesive in an amount of 30 to 40% by weight; the acrylic acid ester is present in an amount of 50 to 60% by weight; and the tertiary octyl acrylamide is present in an amount of 3 to 6% by weight.

Inventors: MUDGE, PAUL R.
Applicants: NATIONAL STARCH AND CHEMICAL CORPORATION
Application year: 1988
Main classification: C09J4
IPC codes: C08F220, C09J131, C09J133, C09J7