Polyimide resin compositions

Abstract: A semiconductor encapsulating material is obtained from a polyimide resin composition comprising (A) a polyaminobismaleimide resin, (B) a silicone monomer and/or oligomer having a hydroxyl or alkoxyl group bonded to a silicon atom and mixtures thereof, and (C) an inorganic filler wherein the weight ratio of polyaminobismaleimide resin (A) to silicone component (B) ranges from 99.5/0.5 to 70/30, and the weight ratio of polyaminobismaleimide resin (A) to inorganic filler (C) ranges from 100/50 to 100/1000.

Description: This invention relates to polyimide resin compositions. More particularly, it relates to polyimide resin compositions useful as semiconductor encapsulating materials and also applicable as semiconductor package substrates and hybrid IC substrates. At present, IC, LSI and other semiconductor circuits are encapsulated with resinous sealants, typically epoxy resin-silica blends by transfer molding. With a rapidly increasing degree of integration of semiconductor circuit, the conventional epoxy-silica encapsulating compounds turn to be unsatisfactory because they have an increased coefficient of linear thermal expansion and are less heat resistant and less reliable. There is a need for a resin based encapsulating compound having a higher heat resistance and a lower coefficient of linear expansion. In this respect, polyimide resins are promising resins. In general, polyimide resins are less resistant to humidity. Polyimide resins are blended with inorganic fillers to form semiconductor encapsulating compounds which often fail to play the requisite role of imparting humidity resistance to semiconductor circuits. The polyimide resins are thus regarded unsuitable as encapsulating compound. Tailored polyimide resins are known in the art, including reaction products from oligoimides and hydroxylic organic silicon compounds and reaction products from oligoimides, polyamines and hydroxylic organic silicon compounds as disclosed in Japanese Patent Application Kokai No. 54-138100 and 56-11926. Aging resistance is imparted to ordinary polyamide resins while maintaining their heat resistance. In summary, conventional epoxy resin-silica blends have a high coefficient of linear expansion and are less heat resistant and less reliable, and conventional polyimide resins are less moisture-proof. According to the present invention, there is provided a polyimide resin composition comprising (A) a polyaminobismaleimide resin comprising a reaction product obtained by reacting a bismaleimide of general formula (I): wherein R is a divalent organic radical, with an aromatic diamine of general formula (II): wherein Z is -CH₂-, -O-, -S-, -SO- or -SO₂-, and R¹ and R² are independently selected from hydrogen, C₁-C₄ alkyl, aryl, cycloalkyl and C₁-C₄ acyl, (B) a silicone component which is at least one of triphenylsilanol, diphenylsilane diol, methylphenylsilane diol, diethylsilane diol, dimethoxydiphenylsilane, diethoxydiphenylsilane, phenyltriethoxysilane, diethoxydimethylsilane, triethoxysilane, 1,1-dimethyl-3,3-diphenyldisiloxane-1,3-diol, 1,4-bis(hydroxy-dimethylsilyl)benzene and diphenylethoxyvinylsilane, and (C) an inorganic filler comprising at least one of fused silica, crystalline silica and alumina, wherein the weight ratio of polyaminobismaleimide resin (A) to silicone component (B) is from 99.5/0.5 to 70/30, and the weight ratio of polyaminobismaleimide resin (A) to inorganic filler (C) is from 100/50 to 100/1000. We have found that the humidity resistance of a polyimide resin can be drastically improved by blending therein a silicone component (B) and an inorganic filler (C). There is obtained a polyimide resin composition which experiences little loss of volume resistance after a pressure cooker test (PCT) while maintaining the high heat resistance and low coefficient of linear thermal expansion inherent to polyimide resin. It is outstandingly useful for encapsulating semiconductors, as a semiconductor package substrate and as a hybrid IC substrate. The polyimide resin composition may be prepared by mixing components (A), (B) and (C) while heating at a temperature above the softening point of the polyaminobismaleimide resin (A) whereby the components (A), (B) and (C) are homogeneously mixed and the silicone component (B) condenses primarily by itself and/or gives rise to coupling reaction with inorganic filler (C). There is obtained a molding resin composition. The composition is comminuted into particles of a suitable size so that it may be molded by any desired molding methods including transfer molding, injection molding and compression molding. The composition may be applied as semiconductor encapsulating material or as semiconductor boards and post-cured into a product which experiences little loss of volume resistance after a pressure cooker test (PCT) and maintains the high heat resistance and low coefficient of linear thermal expansion characteristic of polyimide resin. The components of the polyimide resin composition according to the present invention will be described in detail. (A) Polyaminobismaleimide resin The polyaminobismaleimide resin used herein is a reaction product obtained by reacting a bismaleimide of general formula (I): wherein R is a divalent organic radical, preferably an aromatic radical, with an aromatic diamine of general formula (II): wherein Z is -CH₂-, -O-, -S-, -SO- or -SO₂-, and R¹ and R² are independently selected from the group consisting of hydrogen, C₁-C₄ alkyl, aryl, cycloalkyl and C₁-C₄ acyl. Examples of the bismaleimides represented by formula (I) include N,N'-m-phenylenedimaleimide, N,N'-p-phenylenedimaleimide, N,N'-oxy(di-p-phenylene)dimaleimide, N,N'-methylene(di-p-phenylene)dimaleimide, N,N'-ethylene(di-p-phenylene)dimaleimide, N,N'-sulfo(di-p-phenylene)dimaleimide, N,N'-m-phenylenebis(p-oxyphenylene)dimaleimide, N,N'-methylene(di-1,4-cyclohexylene)dimaleimide, N,N'-isopropylidene(di-1,4-cyclohexylene)dimaleimide, 2,6-xylylenedimaleimide, 2,5-oxadiazolylenedimaleimide, N,N'-p-phenylene(dimethylene)dimaleimide, N,N'-2-methyl-p-toluylenedimaleimide, N,N'-thio(diphenylene)dicitraconimide, N,N'-methylene(di-p-phenylene)bis(chloromaleimide), and N,N'-hexamethylenebis(cyanomethylmaleimide). Examples of the aromatic diamines represented by formula (II) include 4,4'-diaminodiphenylsulfone, 3,3'-diaminodiphenylsulfone, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylether and 4,4'-diaminodiphenylsulfide. The polyaminobismaleimide resin used herein may be obtained by reacting a bismaleimide of formula (I) with an aromatic diamine of formula (II) by any known method. The reaction product preferably has a molecular weight of 400 to 1,500 and may contain a substantial amount of unreacted monomers. The silicone component is at least one of triphenylsilanol, diphenylsilane diol, methylphenylsilane diol, diethylsilane diol, dimethoxydiphenylsilane, diethoxydiphenylsilane, phenyltriethoxysilane, diethoxydimethylsilane, triethoxysilane, 1,1-dimethyl-3,3-diphenyldisiloxane-1,3-diol, 1,4-bis(hydroxydimethylsilyl)benzene, and diphenylethoxyvinylsilane. (C) Inorganic filler The inorganic fillers used herein COMPRISE AT LEAST ONE OF fused silica (amorphous), crystalline silica and alumina, These fillers may be used as a blend thereof with another filler such as titanium, mica, calcium carbonate, talc, aluminum hydroxide, cordierite, boron nitride, silicon carbide, and glass fibers. The components (A) and (B) described above preferably are blended such that the weight ratio (A/B) of polyaminobismaleimide resin to silicone component ranges from 99.5/0.5 to 70/30, more preferably from 98/2 to 80/20. Within this range (70/30 ≦ A/B ≦ 99.5/0.5), good humidity resistance, higher heat resistance, and lower coefficient of linear expansion of the resulting composition are realized. The components (A) and (C) described above preferably are blended such that the weight ratio (A/C) of polyaminobismaleimide resin to inorganic filler ranges from 100/50 to 100/1000, more preferably from 100/100 to 100/600. Within this range (100/1000 ≦ A/C ≦ 100/50), good moldability, better humidity resistance, and lower coefficient of linear expansion of the resulting composition are realized. In addition to the foregoing essential components, the composition of the present invention may further contain any well-known additives, for example curing accelerators, internal release agents, silane coupling agents, coloring agents, and flame retardants alone or in combination of two or more. These additives may be blended in a commonly used proportion as long as the object of the present invention is not impaired. Examples of the agents for accelerating curing of polyaminobismaleimide are peroxides and imidazoles; the internal release agents include carnauba wax, stearic acid, and montan wax; the silane coupling agents include γ-glycidoxypropyltrimethoxysilane and γ-aminopropyltriethoxysilane; the coloring agents include carbon black; and the flame retardants include bromine compounds and antimony oxide. The polyimide resin composition of the present invention may be prepared by blending predetermined amounts of polyaminobismaleimide resin (A), monomeric or oligomeric silicone (B), and inorganic filler (C). The blend is placed in a kneader, for example, a twin screw extruder or a two roll mill where it is milled at a temperature above the softening point of the polyaminobismaleimide resin, for example, at a temperature in the range of from 100° to 130°C. The blend is cooled to room temperature and comminuted into granules or powder, obtaining a compound for molding. The compound is ready for molding by any desired molding methods including transfer molding, injection molding, and compression molding. In the case of transfer molding, for example, the resin compound may be molded at a temperature of from 180 to 200°C for a time of from 5 to 15 minutes. The molding pressure may vary with the molding technique and temperature, but generally ranges from 30 to 100 kg/cm². In the case of room temperature compression molding or sintering molding, a high pressure of from 200 kg/cm² to several t/cm² is preferably applied. When the resin compound is used as substrates for example rather than as encapsulating material, a pressure of 30 kg/cm² to 1 t/cm² is applicable. The article molded by the afore-mentioned method may be post cured at a temperature as high as 180 to 220°C in an air oven for 6 to 24 hours, obtaining a cured article having the desired properties as well as the properties characteristic of polyimide resin. The article of the resin composition prepared as above is substantially improved in properties as compared with the conventional encapsulating resins. The article experiences little loss of volume resistance after a pressure cooker test and has improved heat resistance and a low coefficient of linear expansion. Although the resin composition of the present invention is described as primarily used as semiconductor encapsulating material, the composition may also be used as semiconductor substrate material such as semiconductor package boards and hybrid IC boards which require the same properties as the encapsulating material. EXAMPLE Examples of the polyimide resin composition are given below by way of illustration and not by way of limitation. Examples 1-4 and Comparative Examples 1 and 2 A compound for molding was prepared by blending the components shown in Table 1 in the amounts indicated therein, thoroughly milling the blend in a two roll mill, cooling the blend, and comminuting the blend into granules. This compound was molded by a transfer molding machine under the following conditions into prism and plate shaped test pieces of 12.5 mm x 12.5 mm x 60 mm and 100 mm x 100 mm x 2 mm. Molding temperature: 180°C Molding time: 10 minutes Molding pressure: 70 kg/cm² The test pieces were post cured in an air oven at 180°C for 20 hours before they were measured for physical properties. Measurement of physical properties was carried out on the test pieces according to the following procedures. The results are shown in Table 1. (1) Coefficient of linear expansion A test piece of 12.5 mm x 12.5 mm x 60 mm was used. The coefficient of linear expansion of a test piece was measured according to ASTM D-696. (2) Glass transition temperature (Tg) The glass transition temperature is a point of inflection in the temperature-deformation curve obtained from the measurement of coefficient of linear expansion according to ASTM D-696. (3) Volume resistance A plate test piece of 100 mm x 100 mm x 2 mm was used. The volume resistance of the test piece in normal state was measured according to JIS K-6911. To examine humidity resistance, a pressure cooker test (PCT) was carried out wherein the test piece was maintained in an autoclave (water medium) at a temperature of 121°C and a pressure of 2 kg/cm², for 200 hours. After the test, the volume resistance of the test piece was again measured. The (PCT) test was carried out by admitting pure water into an autoclave, immersing the test piece in the water, pressurizing the water under an internal pressure of 2 kg/cm², placing the autoclave in an oil bath at 125°C, and maintaining the autoclave in the conditions for 200 hours. Composition (parts by weight) Example Comparative Example 1 2 3 4 1 2 Polyimide 92 94 96 94 100 100 Silicone dimethoxydiphenylsilane 8 - - - - - diphenylsilane diol - 6 4 - - - silicone oligomer - - - 6 - - Fused silica 235 235 180 235 235 235 Alumina - - 55 - - - γ-glycidoxypropyltrimethoxysilane 1 1 1 1 1 - Stearic acid 1 1 1 1 1 1 Carnauba wax 1 1 1 1 1 1 Carbon black 0.5 0.5 0.5 0.5 0.5 0.5 Properties Tg (°C) 232 235 234 236 240 241 Coefficient of linear expansion (x10⁻⁵ cm/cm.°C) 1.6 1.5 1.8 1.5 1.5 1.5 Volume resistance Normal (x10¹⁶ Ωcm) 2.6 4.2 4.0 3.1 3.3 2.4 After PCT (x10¹⁴ Ωcm) 5.4 8.5 6.3 4.5 0.41 0.063

Claims: A polyimide resin composition comprising (A) a polyaminobismaleimide resin comprising a reaction product obtained by reacting a bismaleimide of general formula (I): wherein R is a divalent organic radical, with an aromatic diamine of general formula (II): wherein Z is -CH₂-, -O-, -S-, -SO-, or -SO₂-, and R¹ and R² are independently selected from hydrogen, C₁-C₄ alkyl, aryl, cycloalkyl and C₁-C₄ acyl, (B) a silicone component which is at least one of triphenylsilanol, diphenylsilane diol, methylphenylsilane diol, diethylsilane diol, dimethoxydiphenylsilane, diethoxydiphenylsilane, phenyltriethoxysilane, diethoxydimethylsilane, triethoxysilane, 1,1-dimethyl-3,3-diphenyldisiloxane-1,3-diol, 1,4-bis(hydroxydimethylsilyl)benzene and diphenylethoxyvinylsilane, and (C) an inorganic filler comprising at least one of fused silica, crystalline silica and alumina, wherein the weight ratio of polyaminobismaleimide resin (A) to silicone component (B) is from 99.5/0.5 to 70/30, and the weight ratio of polyaminobismaleimide resin (A) to inorganic filler (C) is from 100/50 to 100/1000. A composition according to claim 1 wherein R in the formula (I) is a divalent aromatic group. A composition according to claim 1 or 2 wherein the weight ratio of polyaminobismaleimide resin (A) to silicone component (B) is from 98/2 to 80/20, and the weight ratio of polyaminobismaleimide resin (A) to inorganic filler (C) is from 100/100 to 100/600. Shaped articles obtained by molding a composition as claimed in any one of the preceding claims.

Inventors: KAN KOJIRO, TAKATA TOSHIMASA, TOMINAGA KAORU, TOMOSHIGE TORU, TAKATA, TOSHIMASA, TOMINAGA, KAORU, TOMOSHIGE, TORU
Applicants: MITSUI PETROCHEMICAL IND, MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1988
Main classification: C08L79
IPC codes: C08G73, C08G77, C08L79