PLATED STEEL SHEET FOR A CAN

Abstract: The invention relates to a plated steel sheet for a can, such as a food can or a drink can. The can comprises a steel sheet, an Al or Al alloy, or a Ti or Ti alloy plated film of 0.005 to 5 µm in thickness on one surface of the steel sheet and a plated film of 0.005 to 5 µm in thickness on the other surface of the steel sheet, the plated film comprising a metal selected from the group consisting of Al, Ti, Zn, Ni, Co, Cr, Mo and Sn. This kind of surface treated steel sheet produces a minimal bimetallic corrosion in a can and, in addition, the steel sheet has improved corrosion resistence on the outer surface of the can.

Description: The present invention relates to plated steel sheet for a can such as is used for containing drinks. Tinplate made by electrolytic application of tin to a steel sheet, tin free steel made by applying chromium or nickel on a steel sheet electrolytically, or aluminium sheet and the like, have been hitherto used from materials for food and drink cans. US-A-3820368 proposes a steel sheet for drink cans, coated in a hot dipping process, with aluminium and aluminium alloy layers to a coating thickness in a range from 8 µm to 25 µm. Among those materials, surface treated steel sheets show enough strength for can use even when they are thin. In recent years, there has come to be used a convenient can which has so-called easy-open end which can be opened by hand without using a can-opener. Aluminium sheet is characterised by a facility for forming easy-open ends. Where the body of the can is made of surface treated steel sheet and the end of the can is made of aluminium sheet there occurs what is called a bi-metallic corrosion wherein one of those metals dissolves preferentially and corrodes. This bi-metallic corrosion hinders the adoption of the convenient can. The bi-metallic corrosion is a phenomenon which occurs whenever metals with different electrode potentials are electrically connected with each other in electrolyte, in which electric current flows from a noble metal to a base metal in potential and the base metal ionizes and begins to dissolve. For example, where a body of a can is made of tinplate and an end of the can of aluminium, a standard potential of aluminium is -1.66 v and that of tin is -0.14 v. In this case, tin is much nobler than aluminium. Therefore, an anodic reaction (1) occurs on the surface of the aluminium sheet and aluminium dissolves. At the same time, a cathodic reaction (2) occurs on the surface of the tinplate and hydrogen is produced. Al -- Al³⁺ + 3e (1) 3H⁺ + 3e -- 3/2 H₂ (2) The above-mentioned reaction does not occur on the whole inner surface of the can because the inner surface of the aluminium end and the tinplate body of the can is usually lacquered. On the aluminium, the above-mentioned reaction occurs concentratedly at any defect in a lacquer film. As the reaction proceeds, a hole is made in the aluminium end. On the tinplate, evolving hydrogen lifts the lacquer film to cause a blister. If this reaction proceeds further, the lacquer films are peeled from the tinplate. This phenomenon is more likely to occur when chloride ions participate in the reactions. The reactions are explained above with specific reference to an example of aluminium and tin. However, there is quite a small difference between tin free steel with an eletrolyte coating of chromium or nickel and free steel with tinplate made by applying tin on steel electrolytically. Even if the body of the can is made from aluminium alloy, the same phenomenon can occur in case of the existence of the difference in potential between the end and the body of the can. To overcome these difficulties, the following measures have previously been proposed: Firstly, there has been made an attempt to cover carefully the aluminium end with lacquer. This is an attempt to prevent the formation of an electrolytic cell. However, there remains unsolved the problem that the corrosion current is concentrated on the defects of the lacquer films and, therefore, a hole is liable to be made in the aluminium end, and that it is uneconomical to incur much expense in coating the end of the can. Subsequently, it has been proposed to make the potential of the aluminium end nobler as disclosed in "ANTI-CORROSION" Nov. 1986, p. 4. To accomplish such an object, an attempt has been made to produce an alloy by adding other metal such as copper to aluminium. In this case, the difference in potential between the end and the body of the can needs to be very small and the corrosion resistance of the end is required to be good. No satisfactory alloy, however, has yet been identified. It is an object of the present invention to provide a surface treated steel sheet with high corrosion resistance in which bi-metallic corrosion does not occur. To accomplish the above-mentioned object, the present invention provides plated steel sheet for a can as described below and as set forth in claim 1 of the claims below. When seeking to make nobler the potential of an aluminium end of a can, selection of materials is greatly limited and this makes it difficult to manufacture an appropriate alloy. However, it is comparatively easy to make more base the potential on the surface of a surface treated steel sheet of a can body to meet the potential of the aluminium end. Thereby, it is possible to prevent bi-metallic corrosion. The present invention is made from this viewpoint. A steel sheet having an Al plated film naturally has the same electrode potential as the end. Otherwise, if the plated film has an electrode potential close to the potential of Al, the corrosion current will be extremely small, even though a cell is formed between the plated film of the body and the aluminium end. Ti is proposed as a metal which forms such a film and does not inflict any injury upon the human body. The standard electrode potential of Ti is -1.63 v which is very close to the standard potential of Al. Ti is also a metal of high corrosion resistance and high workability. Thus, it is proposed bi-metallic corrosion can be prevented by applying Al plated or Ti plated surface of steel sheet to the inner surface of a can. A plated film of 0.005 µm or more in thickness is required. When the thickness of the plated film is less than 0.005 µm, the coverage of film becomes insufficient. The thicker the plated film is, the higher is the corrosion resistance. However, a film of 5 µm in thickness is sufficient. An excessively thick plated film is liable to crack during extreme bending. Purity of the plated film is almost not in question, if Al or Ti contains less than a few percent of impurities such as Mg, Cu, Fe, Si, Zn and Mn. In Al plating or Ti plating, it is impossible to deposit electrolytically Al and Ti from aqueous solutions. The use of an electrolytical deposition of Al and Ti from a salt fused bath and an organic solution bath or of dry processes such as a vacuum evaporation and an ion plating is preferred in plating Al and Ti on steel. The dry processes are suitable particularly for obtaining a plated film of high density and high corrosion resistance. Further, a high corrosion resistance of the outer surface and the beauty of the can as well as printability are required for the material used for manufacturing a can. When a plated film is formed, the requirements for those features are satisfied by coating a metal such as Al, Ti, Zn, Ni, Co, Cr, Mo or Sn. Accordingly, the features required for the outer surface of the can be fulfilled sufficiently by coating it with a film of a metal selected from these metals. When the thickness of a plated coating on the outer surface of steel sheet as well as on the inner surface of steel sheet is thinner than 0.005 µm, the coverage of film is insufficient. A plated film of 5 µm in thickness is sufficient. An excessively thickened film gives rise to difficulties in working. In plating the outer surface of steel sheet, there are metals such as Zn, Ni, Cr and Sn which precipitate easily from aqueous solutions. However, the dry processes as mentioned above are appropriate for obtaining a desirable dense and uniform film of a beautiful external appearance. In particular Embodiments, Ti plated film or Al plated film is formed on the steel surface corresponding to the inner surface of a can. The same results can be obtained when Ti alloy plated film or Al alloy plated film is formed. In the present invention, only the above-mentioned plated film is sufficiently effective. In addition, the above-mentioned metal coated steel sheets with chemical treatment are more effective for can use. Phosphate treatment, chromate treatment, chromic acid phosphate treatment and the like are useful in the above-mentioned chemical conversion treatments. The above-mentioned treatments are more particularly treatments of immersion, spraying and electrolysis. The thickness of chemical conversion film needs to be 0.01 to 0.1 µm. In the present invention, one surface of steel sheet is plated with a corrosion-resistant and harmless metal whose electrode potential is almost equal to that of aluminium. Thus, when the above-mentioned steel sheet is used in combination with aluminium, there is no possibility of bi-metallic corrosion. Further, the present invention combines in can making the advantages of a steel sheet and an easy-open end. This enables provision of a convenient can. Furthermore, the other surface of the steel sheet, being the outer surface of the can, is plated with a dense and uniform metal of high corrosion resistance. From the above-mentioned features, the present invention enables the plated steel sheet to be used widely as the material for a can and contributes much effectively to the development of the food industry. The example below provides an illustration of the invention. A first surface of cold rolled steel sheet was plated with one of Al, Al alloy, Ti and Ti alloy. Surface treated steel sheet was made from the steel sheet. The other surface of the sheet was plated with one of Ti, Cr, Al, Ni, Zn, Mo, Sn or Co. Bi-metallic corrosion tests on the first surface (the inner surface of a can) of the surface treated steel sheet were run to examine the corrosion resistance and salt spray tests were run to examine the rust resistance of the other surface of the steel sheet. Plating was achieved as follows: A laser (0.5 KW, 20 mm in a diameter, YAG laser) beam was directed onto the surface. Thereafter, the plated film on the first surface (the inner film) and the plated film on the other surface (the outer film) were formed on the steel sheet under the following conditions: Degree of vacuum 6 x 10⁻⁶ Torr Temperature of base steel sheet 200 °C Method of evaporation heating by electron beam Distance between base steel sheet and crucible 50 cm Inner plated film Al, Ti, Al-1% MG, Ti-3%Al, Ti-3%Cr Outer plated film Ti, Cr, Al, Ni, Zn, Mo, Sn, and Co Bi-metallic corrosion tests were run in the following manner: Plated steel sheet was coated with epoxy phenolic lacquer at a thickness of 50 mg/dm² and then baked. The plated steel sheet was coupled with aluminium sheet coated and baked in the same manner using a wire through an ampere meter. Both the steel test piece and the aluminium one were sealed with a tape to provide a fixed unsealed area. Those test pieces were immersed and processed (subjected to retorting) in an aqueous solution containing 0.3 % NaCl at 125 °C for 60 minutes. Thereafter, the test pieces were immersed in another aqueous solution containing 0.3 % NaCl which was kept at 80°C. Then, a coupling electric current flowing between the plated steel sheet and the aluminium sheet was measured. Salt spray tests were run according to JIS Z 2371 and the estimation of the test results was presented with a spraying time during which rust could be discerned on half of the area of the steel sheet subjected to the tests. For comparison, two sorts of steel sheets having a thin plated coating, and tinplate conventionally used, were prepared and subjected to the tests. The above-mentioned two sorts of steel sheets were prepared in the same manner as the Preferred Embodiment. The tinplate was plated electrolytically with the use of a sulphuric acid aqueous solution to form a tin film of 0.4 µm in thickness and subjected to a chromate treatment after it had been subjected to a reflow treatment. The results of the above-mentioned tests are shown in Table 1. Controls and a conventional example are shown in Table 2. As clearly seen from Table 1, in the examples of No. 1 to No. 27, the coupling electric current is 0.003 µA or less and a rust resistance of the outer surface of the test piece was good. As clearly seen from Table 2, the couple current of the test pieces No. 28 and No. 29, both of which have a film of 0.001 µm in thickness, is over 20 times higher than the one of the present invention. In the test piece No. 30 of conventional tin plate, the coupling electric current is ober 50 times more. Thus the results demonstrate that the surface treated steel sheet of the present invention is steel sheet which hardly produces bi-metallic corrosion in a can. In addition, the surface treated steel sheet of the present invention provides good corrosion resistance on the outer surface of a can. In this example, the surface of cold rolled steel sheet was cleaned by means of the laser beam. Instead of the laser beam, however, cleaning methods such as solvent degreasing by means of trichloroethylene, electrolytic degreasing by means of sodium hydroxide and the like can be used. Test pieces Nos. Inner plated film outer plated film Bi-metallic corrosion resistance Coupling current(µA) Salt spraying time for treating rust resistance of outer surface of steel (hour) Plated-metal Thickness (µm) Plated-metal Thickness (µm) Examples 1 Al 0.1 Ti 0.3 0.01 120 2 Al 0.1 Cr 0.3 0.02 75 3 Al 0.1 Al 0.3 0.01 125 4 Al 0.1 Ni 0.3 0.02 60 5 Al 0.1 Zn 0.3 0.02 50 6 Al 0.1 Mo 0.3 0.01 65 7 Al 0.1 Sn 0.3 0.01 70 8 Al 0.1 Co 0.3 0.01 95 9 Ti 0.1 Ti 0.3 0.03 125 10 Ti 0.1 Al 0.3 0.03 130 11 Al 0.01 Ti 0.01 0.02 100 12 Al 1.0 Ti 1.0 0.005 135 13 Al 3.5 Al 0.01 0.004 110 14 Ti 0.01 Al 1.0 0.04 200 15 Ti 1.0 Ni 0.01 0.007 50 16 Ti 3.5 Ni 1.0 0.005 85 17 Al 0.01 Cr 0.01 0.02 45 18 Al 0.01 Cr 1.0 0.02 70 19 Al 1.0 Zn 0.01 0.006 30 20 Al 1.0 Zn 1.0 0.005 80 21 Al 0.01 Mo 0.01 0.02 45 22 Ti 1.0 Sn 0.01 0.007 50 23 Ti 1.0 Sn 1.0 0.006 120 24 Ti 0.01 Co 0.01 0.02 45 25 Al-1%Mg 0.1 Al 1.0 0.02 120 26 Ti-3%Al 0.1 Al 0.3 0.03 135 27 Ti+ 3%Cr 0.15 Ti 0.3 0.02 130 Test pieces Nos. Inner plated film outer plated film Bi-metallic corrosion resistance Coupling current(µA) Salt spraying time for treating rust resistance of outer surface of steel (hour) Plated-metal Thickness (µm) Plated-metal Thickness (µm) Controls 28 Al 0.001 Ti 0.004 0.55 25 29 Ti 0.001 Al 0.004 0.70 30 Conventional tinplate 30 Sn 0.1 Sn 0.4 1.15 20

Claims: Plated steel sheet for the body of a can with an aluminium end, the sheet being characterized by a first film, of 0.005 to 5 µm in thickness, plated on one surface of the steel sheet which is the surface destined to be on the inside of the can, the film being of Al, Al alloy, Ti or Ti alloy; a second film, of 0.005 to 5 µm in thickness, plated on the other surface of said steel sheet, the plated film being deposited by a dry process and metal selected from Al, Ti, Zn, Ni, Co, Cr, Mo and Sn. Steel sheet as claimed in claim 1 characterized in that said plated film on said one surface is formed by means of a dry process. A body of a can, formed from coated steel sheet, the coating on the inside surface of the can being a film with a thickness of from 0.005 to 5 µm and being of Al, Al alloy, Ti or Ti alloy, the coating on the outside surface of the can being a dry coated film with a thickness of from 0.005 to 5 µm and being selected from Al, Ti, Zn, Ni, Co, Cr, Mo and Sn. A can body as claimed in claim 3 wherein the coating on the inside surface of the can is one which has been deposited by a dry process. A can comprising an easy open end of aluminium and a body as claimed in claim 3 or 4.

Inventors: ADANIYA, TAKESHI PATENT LICENSE AND QTY. ST. DEPT., ISHIKAWA, HIROSHI PATENT LICENSE AND QTY. ST. DEPT, KAGECHIKA, HIROSHI PATENT LICENSE AND QTY. ST. DEP, MISHIMA, TADAHIKO PATENT LICENSE AND QTY. ST. DEPT, OONIWA, NAOYUKI PATENT LICENSE AND QTY. ST. DEPT., YASUE, YOSHIHIKO PATENT LICENSE AND QTY. ST. DEPT., YOMURA, YOSHINORI PATENT LICENSE AND QTY. ST. DEPT
Applicants: NKK CORPORATION
Application year: 1988
Main classification: B32B15
IPC codes: C25D5, C23C14, B32B15, C25D7