ETHYLENE POLYMERIZATION CATALYST

Abstract: A vanadium catalyst composition comprising: (i) the reaction product of a vanadium trihalide wherein the halogen is chlorine, bromine, or iodine, or mixtures thereof, and an electron donor, which is a liquid, organic Lewis base in which the vanadium trihalide is soluble; (ii) a silica support onto which component (i) is impregnated; (iii) a salt admixed with the silica support, the cation of said salt being selected from the group consisting of Groups I and II of the Periodic Chart of the Atoms; (iv) a halocarbon promoter; and (v) a hydrocarbyl aluminum cocatalyst.

Description: This invention relates to a vanadium catalyst useful in ethylene polymerization. A number of vanadium catalysts have been described in the literature based on species such as VCl₄, VCl₃, VOCl₃, and vanadyl tris-acetylacetonate. Impregnated on or chemically anchored to supports such as silica, these catalysts provide polyethylene with a broad molecular weight distribution and certain desirable properties. However, these catalyst systems are plagued by several problems, among them, low activity. Particularly in a gas phase process, high activity and hence low catalyst residues, obviating the need for removal, are desired. Recently vanadium catalysts have come to the fore in polyethylene production because of the discovery of a particular catalyst composition, which is singularly effective in gas phase processes. The advantages of this catalyst composition are superior hydrogen response thus achieving very low levels of unsaturation in the polymer; a high degree of productivity resulting in very low catalyst residues; and the production of polyethylenes having a relatively broad molecular weight distribution and a wide melt index range. Further, they permit the utilization of a broad range of alpha-olefin comonomers, which enables the production of a wide range of densities; and they provide polymers having high bulk densities and readily fluidizable particle sizes low in fines, substantially free of agglomeration. The particular catalyst composition referred to comprises (i) the reaction product of a vanadium trihalide and an electron donor and a modifier impregnated onto a silica support; (ii) a halocarbon promoter; and (iii) a hydrocarbyl aluminum cocatalyst. The catalyst composition can be prepared as follows: the vanadium trihalide is first dissolved in the electron donor at a temperature in the range of about 20°C to below the boiling point of the electron donor for about 2 to about 6 hours. Silica is then added as a dry powder or as a slurry in the electron donor or an inert solvent whereupon the silica becomes impregnated with the vanadium trihalide/electron donor reaction product. The liquid is then removed by drying at less than 100°C for about 3 to about 6 hours. The modifier, dissolved in an inert solvent, is subsequently mixed with the impregnated carrier, and the liquid is removed by drying at a temperature of less than about 70°C for about 2 to about 4 hours. The halocarbon promoter and the hydrocarbyl aluminum cocatalyst are added to the supported catalyst either before and/or during polymerization. Since its introduction into commerce, the art has sought to optimize this catalyst composition particularly with regard to its polymerization activity. For example, GB-A-2 058 804 discloses an olefin polymerization process wherein a catalyst is employed which comprises, e.g., a silicon oxide, a compound of formula ROH, R being an organic radical having 1 to 20 carbon atoms, and and a vanadium compound supported on a solid compound selected from magnesium halides and manganese halides. The examples of said document do not, however illustrate a corresponding catalyst but exclusively relate to titanium containing catalyst compositions. An object of the invention is to enhance the polymerization activity of the above vanadium catalyst composition. Other objects and advantages will become apparent hereinafter. According to the present invention, then, the vanadium catalyst composition has been discovered having increased polymerization activity. The enhanced composition comprises: (i) the reaction product of a vanadium trihalide wherein the halogen is chlorine, bromine, or iodine, or mixtures thereof, and an electron donor, which is a liquid, organic Lewis base in which the vanadium trihalide is soluble, (ii) a silica support onto which component (i) is impregnated; (iii) a salt admixed with the silica support, the cation of said salt being selected from the metals of Groups I and II of the Periodic Chart of the Elements and the anion of said salt being selected from carbonates and sulfates; (iv) a halocarbon promoter; and (v) a hydrocarbyl aluminum cocatalyst. Optionally, the following component is included in the above composition and impregnated onto the silica support: (vi) a modifier having the formula MX a wherein M is boron or AlR( 3-a ); each R is an alkyl radical having 1 to 14 carbon atoms and is alike or different; X is chlorine, bromine, or iodine; and a is 0, 1, or 2 except that when M is boron, a is 3. A second aspect of the invention resides in a process for the polymerization or copolymerization of ethylene comprising passing ethylene with or without an alpha-olefin comonomer in contact with the vanadium catalyst composition as defined above, said contact between ethylene and the catalyst composition being effected in such a manner that polyethylene is formed. The Periodic Chart of Elements referred to above is the 1969 Edition published by Sargent-Welch Scientific Company, Skokie, Illinois, and is incorporated by reference herein. As noted, the trihalide portion of the vanadium trihalide is either chlorine, bromine, or iodine, or mixtures thereof. The electron donor is a liquid, organic Lewis base in which the vanadium trihalide is soluble. It is generally selected from alkyl esters of aliphatic and aromatic carboxylic acids, aliphatic ketones, aliphatic amines, aliphatic alcohols, alkyl and cycloalkyl ethers, and mixtures thereof, each electron donor having 2 to 20 carbon atoms. Among these electron donors, the preferred are alkyl and cycloalkyl ethers having 2 to 20 carbon atoms; dialkyl, diaryl, and alkylaryl ketones having 3 to 20 carbon atoms; and alkyl, alkoxy, and alkylalkoxy esters of alkyl and aryl carboxylic acids having 2 to 20 carbon atoms. The most preferred electron donor is tetrahydrofuran. Other examples of suitable electron donors are methyl formate, ethyl acetate, butyl acetate, ethyl ether, dioxane, di-n-propyl ether, dibutyl ether, ethyl formate, methyl acetate, ethyl anisate, ethylene carbonate, tetrahydropyran, and ethyl propionate. While an excess of electron donor is used initially to provide the reaction product of vanadium trihalide and electron donor, the reaction product finally contains preferably 1 to 20 moles of electron donor per mole of vanadium trihalide and particularly 1 to 10 moles of electron donor per mole of vanadium trihalide. About 3 moles of electron donor per mole of vanadium trihalide has been found to be most preferable. The silica support is a solid, particulate porous material essentially inert to the polymerization. It is used as a dry powder generally having an average particle size of 10 to 250 µm (microns) and preferably 30 to 100 µm (microns); a surface area of at least 3 square meters per gram and preferably 50 square meters per gram; and a pore size of at least 8 nm (80 Angstroms) and preferably at least 10 nm (100 Angstroms). Generally, the amount of support used is that which will provide 0.05 to 0.5 millimole of vanadium trihalide per gram of support and preferably 0.2 to 0.3 millimole of vanadium trihalide per gram of support. Preferred cations of the salts of component (iii) are sodium, potassium, magnesium and calcium. Mixtures of salts can be used if desired. The salt of choice is calcium carbonate. The amount of salt generally is in the range of 1.5 to 90 percent by weight based on the weight of the silica support exclusive of impregnated components, and is preferably in the range of 2 to 10 percent by weight. The salt can be dry mixed with the silica support prior to activation or the salt and the silica support can be activated separately and slurried in an electron donor or other inert solvent with silica prior to the addition of the reaction product of vanadium trihalide and the same electron donor. Either of these routes is more effective than dry mixing the salt with the silica supported vanadium catalyst. In any case, the salts used in the preparation of subject catalyst should be essentially free of water. The halocarbon promoter can have the following formula: R X CX (4-X) wherein R = hydrogen or an unsubstituted or halogen substituted alkyl radical having 1 to 6 carbon atoms; X = a halogen; and x = 0, 1, or 2. Preferred promoters include fluoro-, chloro-, and bromo-substituted methane or ethane having at least 2 halogen atoms attached to a carbon atom, e.g., methylene dichloride, 1,1,1-trichloroethane, chloroform, CBr₄, CFCl₃, hexachloroethane, CH₃CCl₃, and CF₂ClCCl₃. The first three mentioned promoters are especially preferred. Generally 0.1 to 10 moles, and preferably 0.2 to 2 moles, of promoter are used per mole of cocatalyst. The hydrocarbyl aluminum cocatalyst can be represented by the formula R₃Al wherein each R is an alkyl radical; each R can be alike or different; and each R has 1 to 14 carbon atoms, and preferably 2 to 8 carbon atoms. Further, each alkyl radical can be a straight or branched chain. Examples of suitable radicals are: methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, pentyl, neopentyl, hexyl, 2-methylpentyl, heptyl, octyl, isooctyl, 2-ethylhexyl, 5,5-dimethylhexyl, nonyl, decyl, isodecyl, undecyl, and dodecyl. Examples of suitable hydrocarbyl aluminum compounds are as follows: triisobutylaluminum, trihexylaluminum, di-isobutylhexylaluminum, isobutyl dihexylaluminum, trimethylaluminum, triethylaluminum, tripropylaluminum, triisopropylaluminum, tri-n-butylaluminum, trioctyaluminum, tridecylaluminum, tridodecylaluminum, tribenzylaluminum, triphenylaluminum, trinaphthylaluminum, and tritolylaluminum. The preferred hydrocarbyl aluminums, are triethylaluminum, triisobutylaluminum, and trihexylaluminum. The cocatalyst and promoter can be added to the supported vanadium complex either before or during the polymerisation reaction. They can be added together or separately, simultaneously or sequentially. The cocatalyst and promoter are preferably added separately as solutions in an inert solvent, such as isopentane, to the polymerization reaction at the same time as the flow of the ethylene is initiated. The cocatalyst is necessary to obtain any significant polymerization. The promoter, on the other hand, can be considered a preferred option. Generally 5 to 500 moles, and preferably 10 to 40 moles, of cocatalyst are used per mole of vanadium catalyst, i.e., the reaction product of the vanadium trihalide and the electron donor. The formula of the modifier is MX a wherein M is boron or AlR (3-a) ; each R is an alkyl radical having 1 to 14 carbon atoms and is alike or different; X is chlorine, bromine, or iodine, or mixtures thereof; and a is 0, 1, or 2 except that when M is boron, a is 3. Preferred modifiers include alkylaluminum mono- and di-chlorides wherein each alkyl radical has 1 to 6 carbon atoms, and boron trichloride. A particularly preferred modifier is diethyl aluminum chloride. Generally 0.1 to 10 moles, and preferably 0.2 to 2.5 moles, of modifier are used per mole of electron donor. When the modifier is used it is considered to be part of the vanadium trichloride/electron donor complex. The supported catalyst is typically prepared as follows: silica gel is activated at a temperature in the range of 250°C to 800 °C under a dry, inert gas such as nitrogen for 8 to 16 hours to give a support essentially free of adsorbed water and containing less than 0.7 millimole per gram of silica of surface hydroxy groups. Commercially available powdered "anhydrous" salts are used. The salt is activated at a temperature in the range of 200°C to 400°C under a dry, inert gas such as nitrogen for 8 to 16 hours. The silica and salt are slurried in freshly distilled tetrahydrofuran (THF), under nitrogen. An amount of VCl₃(THF)₃ is added to give a loading of 0.2 to 0.35 millimole of vanadium per gram of support. The mixture is stirred for 20 to 40 minutes, then excess THF is removed to give a free flowing powder. If diethylaluminum chloride (DEAC) modification is desired, the dry catalyst is slurried in dry, deoxygenated hexane. DEAC is added, and, after stirring for 20 to 30 minutes, the hexane is removed to give a free-flowing powder. Rather than activating the salt and silica separately, as above, the two components can be dry mixed and activated at a temperature below the decomposition temperature of the particular salt. Alternatively, the salt can be activated and added to the supported catalyst. The catalyst is slurried in hexane with the salt under nitrogen. The mixture is stirred for 20 to 30 minutes, and the hexane is removed to give a free flowing powder. This method is generally less effective than the above two techniques insofar as increasing polymerization activity is concerned. The ethylene polymerization can be conducted in the gas phase or liquid phase using conventional techniques such as fluidized bed, slurry, or solution processes. A continuous, fluidized bed process is preferred. Using this fluidized bed process, the vanadium complex, the cocatalyst, the promoter, the ethylene monomer, and any comonomers are continuously fed into the reactor and polyethylene product is continuously removed. The density of the ethylene copolymer produced may be varied over a wide range depending upon the amount of alpha-olefin comonomer added and upon the particular comonomer employed. The greater the mole percent of alpha-olefin, the lower the density. The fluidized bed polymerization is conducted at a temperature below the sintering temperature of the product. The operating temperature is generally in the range of 10°C to 115°C. Preferred operating temperatures will vary depending upon the density desired. High density polyethylenes of greater than 0.94 grams per cubic centimeter (g/cm³) are produced at operating temperatures of 85°C to 115°C, and preferably 90°C to 100°C. Low density polyethylenes ranging in density from 0.91 to 0.94 g/cm³ are preferably produced at an operating temperature of 75°C to 90°C. Very low density polyethylenes of less than 0.91 g/cm³ are preferably produced at an operating temperature of 10°C to 80°C. In the case of very low density polyethylenes, it is necessary to dilute the reaction mixture with a large quantity of diluent gas in order to prevent the formation of polymer agglomerates and sustain polymerization on a continuous basis. The fluidized bed reactor is typically operated at pressures of up to 7.0 MPa (1,000), and preferably 0.44 to 2.5 MPa (50 to 350, psig). A chain transfer agent, such as hydrogen, can be used to terminate the polymer chain. Usually the ratio of hydrogen to ethylene will vary between 0.001 to 2.0 moles of hydrogen per mole of ethylene. In the past, improvements in polymerization activity have been achieved through the use of halocarbon promoters or by pretreatment with modifiers such as haloaluminum alkyls. This invention provides a new class of activity enhancers, namely, the Groups I and II salts. Added to the catalyst support, these salts result in improved activity while preserving the desired high hydrogen response and broad molecular weight distribution. The materials are readily available, easily handled, and have the added advantage of being neutral salts. They, therefore, do not contribute to reactor and post-reactor corrosion problems associated with the use of aluminum alkyls and halocarbons. It has been noted that the most preferred salt is calcium carbonate. Calcium is the preferred cation; carbonate is the preferred anion. The optimum amount of salt depends on each salt, e.g., low levels of calcium carbonate, but high levels of calcium sulfate, offer the most significant activity boost among the salts tested. Modifiers such as diethylaluminum chloride are used in vanadium catalyst systems to improve hydrogen response, increase bulk density, and decrease fines. Calcium carbonate can replace these modifiers at low levels and hydrogen response and bulk density will be comparable while the activity is significantly improved. At higher levels, modifier treatment results in higher activity and hydrogen response. In this case, high levels of calcium carbonate are not equivalent to high modifier levels. Used in conjunction with a modifier, however, calcium carbonate offers activity enhancement. Subject catalyst, except for the salt, and its preparation are closely related to the catalyst described in EP-A-120 501 (corresponding to US-A-4,508,842). The invention is illustrated by the following examples: Examples 1 to 18 Powdered calcium carbonate is activated at 200°C nitrogen for 12 hours. VCl₃·3THF solution is added to a slurry of calcium carbonate and silica in THF and then dried at 45°C until free-flowing. DEAC treatment, when used, is accomplished as discussed above. Powdered Na, K, Mg, and Ca sulfates are treated in the same manner as calcium carbonate. The catalyst, a cocatalyst, and a promoter are slurried in 480 milliliters of hexane and the mixture is introduced into a reactor along with ethylene and 6.89 or 34.45 kPa (1 or 5 pounds per square inch) of hydrogen to give a total pressure of 1.2 MPa (160 pounds per square inch gauge). An amount of catalyst sufficient to give a charge of 0.03 or 0.06 millimole of vanadium is used. 20 milliliters of 1-hexene are also introduced into the reactor in each example except example 13. Forty equivalents each of cocatalyst and promoter are used per equivalent of vanadium. The temperature in the reactor is maintained at 85°C and the residence time in the reactor is 30 minutes. Variables and results are set forth in the Table. Notes with respect to the Table: 1. Wt. % salt = the percent by weight of salt based on the weight of the silica support exclusive of impregnated components. 2. mmol = millimole. 3. TIBA = trisobutylaluminum. 4. TEAL = triethylaluminum. 5. psi = pounds per square inch. 6. Relative Activity = activity of catalyst on salt treated (doped) silica/activity of VCl₃·3THF on silica (not doped). 7. The activity of the catalyst is measured in grams of polyethylene per millimole of vanadium per hour per 0.69 MPa (100 psi) of ethylene. 8. MI=Melt index: ASTM D-1238, Condition E. Measured at 190°C and reported as grams per 10 minutes. 9. MFR=Melt flow ratio: Ratio of Flow Index to Melt Index. FI=Flow index: ASTM D-1238, Condition F. Measured at 10 times the weight used in the melt index test above. 10. Bulk density: ASTM D-1895, Method B. The resin is poured via a 0.95 cm (3/8-inch) diameter funnel into a 400 milliliter graduated cylinder to the 400 milliliter line without shaking the cylinder, and weighed by difference. Density values are reported as kilograms per cubic meter (kg/m³). 11. DEAC = diethylaluminum chloride. 12. Polymer density: ASTM D-1505 procedure is followed for polymers having a density of less than 0.940 gram per cubic centimeter and a modified procedure is used for polymers having a density equal to or greater than 0.940 gram per cubic centimeter. For the low density polymers, a plaque is made and conditioned for one hour at 100°C to approach equilibrium crystallinity. For the high density polymers, the plaque is conditioned for one hour at 120°C to approach equilibrium crystallinity, and is then quickly cooled to room temperature. Measurement for density is then made in a density gradient column and density values are reported as grams per cubic centimeter.

Claims: A vanadium catalyst composition comprising: (i) the reaction product of a vanadium trihalide wherein the halogen is chlorine, bromine, or iodine, or mixtures thereof, and an electron donor, which is a liquid, organic Lewis base in which the vanadium trihalide is soluble; (ii) a silica support onto which component (i) is impregnated; (iii) a salt admixed with the silica support, the cation of said salt being selected from the metals of Groups I and II of the Periodic Chart of Elements and the anion of said salt being selected from carbonates and sulfates; (iv) a halocarbon promoter; and (v) a hydrocarbyl aluminum cocatalyst. The vanadium catalyst composition defined in claim 1 wherein the Lewis base is selected from alkyl esters of aliphatic and aromatic carboxylic acids, aliphatic ketones, aliphatic amines, aliphatic alcohols, alkyl and cycloalkyl ethers, and mixtures thereof. The vanadium catalyst composition defined in claim 1 or 2 additionally comprising: (vi) a modifier having the formula MX a wherein M is boron or AlR (3-a) ; each R is an alkyl radical having 1 to 14 carbon atoms and is alike or different; X is chlorine, bromine, or iodine, or mixtures thereof; and a is 0, 1, or 2 except that when M is boron, a is 3. The vanadium catalyst composition defined in any one of claims 1 to 3 wherein the cation of the salt is selected from sodium, potassium, magnesium, and calcium. The vanadium catalyst composition defined in any one of claims 1 to 4 wherein the salt is calcium carbonate. The vanadium catalyst composition defined in any one of claims 1 to 5 wherein the salt is present in an amount of 1.5 to 90, preferably 2 to 10 percent by weight, based on the weight of the silica support. The vanadium catalyst composition defined in any one of claims 1 to 6 wherein the cocatalyst is triisobutyl aluminum or triethylaluminum. The vanadium catalyst composition defined in any one of claims 1 to 7 wherein the promoter is CHCl₃ or CFCl₃. The vanadium catalyst composition defined in any one of claims 3 to 8 wherein the modifier is diethylaluminum chloride. The vanadium catalyst composition defined in any one of claims 3 to 9 wherein the modifier is present in an amount of 0.1 to 10 moles, preferably 0.2 to 2.5 moles per mole of electron donor. A process for the polymerization or copolymerization of ethylene comprising passing ethylene with or without an alpha-olefin comonomer into contact with the vanadium catalyst composition defined in any one of claims 1 to 10, said contact between ethylene and the catalyst composition being effected in such a manner that polyethylene is formed.

Inventors: KAROL, FREDERICK JOHN, ZOECKLER, MARY THERESE
Applicants: UNION CARBIDE CORPORATION
Application year: 1988
Main classification: C08F4
IPC codes: C08F10, C08F4