PROCESS FOR PREPARING VINYLIDENE FLUORIDE BY THE DIRECT FLUORINATION OF VINYLIDENE CHLORIDE

Abstract: Vinylidene fluoride is produced by the gaseous phase reaction of vinylidene chloride with hydrofluoric acid at a temperature of from about 400° to 700°C in the presence of oxygen and a catalyst containing AlF₃ either alone or in combination with a transition metal fluoride selected from iron, cobalt, chromium, nickel, zinc and combinations thereof.

Description: Vinylidene fluoride is a useful monomer in the preparation of fluorocarbon polymers which have excellent weathering and chemical resistant properties. Vinylidene fluoride is currently manufactured on an industrial scale by the dehydrochlorination of 1,1-difluoro-1-chloroethane (142b) which must first be prepared by the fluorination of 1,1,1-trichloroethane. Such a multi-step process is typical for vinylidene fluoride preparation. A one-step process for converting vinylidene chloride, a readily available material, to vinylidene fluoride by gas phase reaction with HF using chromium salts or a combination of AlF₃ and a "activator" selected from La(NO₃)₃, NH₄VO₃, and SnCl₂ has been disclosed in U.S. Patent 3,600,450. Unsatisfactory results were reported when AlF₃ was impregnated with metals such as cadmium, chromium, iron, manganese, molybdenum, nickel, zinc, or zirconium. Another process for catalytically converting vinylidene chloride is disclosed in US-A-4,147,733 using an alumina based catalyst coated with Cr₂O₃ and NiO. This process uses highly corrosive aqueous HF as the fluorinating agent. This invention provides a process for the one-step gas phase conversion of vinylidene chloride (VCl₂) to vinylidene fluoride (VF₂) using anhydrous AlF₃, or a combination of AlF₃ with certain transition metals, as catalyst. These catalysts which have theretofore not been considered useful for such conversions are effective when oxygen is added to the reactant mixture. In accordance with this invention there is provided a process for the preparation of vinylidene fluoride comprising reacting vinylidene chloride with HF in the gaseous phase at a temperature of from 400°C to 700°C in the presence of oxygen and a catalyst containing anhydrous AlF₃. The AlF₃ can be used either alone or in combination with a transition metal fluoride selected from iron, cobalt, chromium, nickel, zinc and combinations thereof. In the process of the invention vinylidene chloride is directly fluorinated to vinylidene fluoride according to the following reaction: CH₂=CCl₂ + 2HF → CH₂=CF₂ + 2HCl The product vinylidene fluoride is recovered from the reaction mixture by conventional techniques. The anhydrous AlF₃ catalyst for use in the process of the invention can be prepared by reacting alumina with aqueous HF to precipitate the powdered hydrate AlF₃·9H₂O. This hydrate when air dried at room temperature loses water to give AlF₃·3H₂O. Heating the latter hydrate (100°C - 175°C) provides anhydrous AlF₃ which is then ground and sieved to provide the desired particle size fraction for use as a catalyst, for example, 60-100 mesh. The AlF₃ can also be combined with a transition metal fluoride selected from iron, cobalt, chromium, nickel and zinc. The catalyst can contain up to about 30 wt% (7.5 to 10 wt% preferred) of transition metal based on the weight of aluminum fluoride. The combination catalysts are prepared by adding an aqueous solution of transition metal salt or salts either before, during or after the addition of the alumina to an aqueous HF solution. The precipitated material is recovered, dried and then heated at temperatures from 100° to 175°C in one or more stages to provide the anhydrous AlF₃/transition metal fluoride combination catalyst which is then ground and sieved to the desired particle size. In operation, the catalyst is loaded into a reactor tube which is formed from a hydrogen fluoride resistant material, preferably nickel or a high nickel alloy such as "Hastelloy C®" The catalyst is activated by heating the reactor tube at temperatures from 400°-700°C (preferably 650° C) and passing air or oxygen through the catalyst for from about 2 to 72 (preferably about 60) hours. Additionally, anhydrous HF can be passed through the catalyst at room temperature up to 600°C for from 2 to 72 hours. Nitrogen is usually included with the oxygen or HF stream during activation. The process of the invention is carried out using a reactor fitted with inlets for reactant and carrier gases and equipped with means such as a single or multi-zone furnace for heating the reactor and the catalyst to controlled temperatures. The reactant gases are passed through the catalyst bed, which is heated to from 400° to 700°C (preferably 575° to 675°C), at a rate to provide contact times of from 1 to 60 seconds and preferably from 8 to 15 seconds. The molar ratio of HF and VCl₂ reactants can range from 2:1 to 10:1. Nitrogen in amounts of up to 80 percent by volume of total gas flow can be used as a carrier gas. In the absence of oxygen the amount of VF₂ produced, even with fresh catalyst, is generally less than about 5 mol percent (except in the case of a FeF₃/AlF₃ catalyst where a 90 mol percent initial conversion to VF₂ was achieved but which dropped to 16 mol percent after 1 hour). The major byproduct of the reaction is 1,1,1-trifluoroethane (143a). Adding oxygen (either neat or air) to the reaction mixture dramatically improves the results as shown in the following Examples. Amounts of from 1 to 160 mole percent oxygen based on the amount of vinylidene chloride have been found to increase both the amounts of VF₂ produced and the catalyst lifetime. However, because amounts of over 25 mole percent oxygen cause the formation of oxygenated byproducts and a lowering of the mass balance below 90% due to burn-off, preferably from 1 to 25 mole percent and most preferably, from 1 to 10 mole percent O₂, based on the moles of vinylidene chloride, is used. Although the presence of oxygen also extends the time of high efficiency catalyst operation, when the conversion of VCl₂ to VF₂ falls below a selected level, such as 35 percent, the catalyst efficiency can be readily restored by discontinuing the flow of HF and VCl₂ and passing oxygen or air through the reactor for 1-8 hours while maintaining the catalyst temperature at 500°C to 700°C. The invention is further illustrated by, but is not intended to be limited to, the following Examples wherein parts are parts by weight unless otherwise indicated. Example 1 A 7.5 wt % FeF₃/AlF₃ catalyst was prepared and evaluated in the conversion of VCl₂ to VF₂ in the presence of oxygen. Alumina (200 gs, 1.96 mol) was added portionwise to a magnetically stirred solution of 52% by weight aqueous HF (500 ml, 15 mol). Addition was controlled to keep the temperature of the reaction mixture between 40° and 45°C. The addition took seven hours and the milky suspension was left at room temperature overnight. Upon standing, a fine powder of AlF₃.9H₂O precipitated. A solution of 37.5 g FeCl₃ (0.23 mol) in 20 ml H₂O was added gradually to the mechanically stirred aqueous AlF₃ mixture. The solution turned a light violet color, the stirring was continued for four hours and the mixture was left to settle at room temperature overnight. The product precipitate was filtered and washed with acetone several times until the filtrate was acid free. The solid obtained was dried in air at room temperature and was heated at 100°C/2 h, 150°C/2 h and finally at 175°C/16 h. The FeF₃/AlF₃ catalyst was ground using a mortar and pestle and was sieved. The 60 to 100 mesh particles were collected and used to fill a nickle, fixed bed reactor (2.54 cm O.D. x 30.5 cm; 1"x 12") which was heated using a single zone furnace. The catalyst was activated at 414°C with a 72 ml/minute (m) flow of nitrogen through the reactor for 2½ hours. The reactor temperature was then increased to 600°C, and a mixture of nitrogen (70ml/m) and anhydrous HF gas (0.04 g/m) was fed for 18 hours. Next VCl₂ liquid (0.04 g/m) and anhydrous liquid HF 0.02 g/m were vaporized separately and fed as gases into the reactor together with nitrogen (129 ml/m) and oxygen (15 ml/m, 162 mol % based on VCl₂). After scrubbing and drying the gaseous products using 16% by weight KOH solution and anhydrous CaSO₄ respectively, the resulting product stream was analyzed on-line using a gas chromatograph which sampled automatically. Under these conditions, the product stream contained 80 mole % VF₂ product together with 20 mole % of an unidentified product believed to be 1,1-difluoroethylene oxide. An 80% mass balance was calculated using a wet test meter. The reaction conditions and results are summarized in Table 1 below. Example 2 A 7.5 wt % ZnF₂/AlF₃ catalyst was prepared and evaluated in the conversion of VCl₂ to VF₂ in the presence of oxygen. To a stirred solution of 500 ml aqueous HF (52%-55%) by weight was added 200 grams of alumina in portions at a rate sufficient to maintain the solution temperature between 40°-45°C. After the addition was completed the suspension was left to precipitate overnight. To the precipitated AlF₃ was added a solution of ZnCl₂ (35 gm in 20 ml of water) with continuous stirring. The reaction mixture was left to settle overnight and then filtered. The precipitate was washed several times with acetone until the filtrate was neutral to litmus paper. The solid was collected, air dried and heated in an oven at 250°C for 18 hours. The solid ZnF₂/AlF₃ catalyst was ground using a mortar and pestle. The ground material (42 g) was loaded in a 2.54 cm O.D. x 30.5 cm (1" X 12") nickel reactor which was heated using a single zone furnace. The catalyst was activated by feeding a mixture of nitrogen (100 ml/m) and hydrogen fluoride (0.13 g/m) for four hours at 100°C. The reactor temperature was raised to 665°C and VCl₂ (0.02 g/m), anhydrous HF (0.025 g/m), nitrogen (80 ml/m) and oxygen (1.5 ml/m, 32 mol % on VCl₂) were fed to the reactor. The product stream was scrubbed, dried and analyzed as in Example 1. The product distribution in the product stream was 38 mole percent VF₂ and 61 mole percent 143a. The process conditions and results are summarized in Table 1 below. Examples 3-5 Three catalysts containing 7.5 wt% of either CrF₃, CoF₂ or NiF₂ combined with AlF₃ were prepared and evaluated following the procedure described in Example 2. The process parameters and results obtained are set out in Table 1 below. The mol % O₂ on VCl₂ for Examples 3-5 was 9, 78 and 102 respectively. Examples 6 and 7 In order to provide a comparison between the process of the invention using an oxygen containing carrier gas and the prior art process without oxygen, the 7.5 wt % NiF₂/AlF₃ and 7.5 wt % CoF₂/AlF₃ catalysts were evaluated. The process parameters and results are reported in Tables 2 and 3 below. Example 8 Preparation and Evaluation of 7.5 Wt% FeF₃/AlF₃, Effect of Activation and Temperature The catalyst was prepared by the identical method used in Example 1. The ground 60 to 100 mesh particles were collected and loaded into the 2.54 cm x 5.08 cm (1" x 2") nickel, fixed bed reactor. The catalyst was gradually heated (100°C/1 hour) to 650°C using 20 ml/m of air and was maintained at this temperature for two and one half days. The temperature of the reactor was then lowered to 550°C and a mixture of HF 0.035 g/m together with nitrogen 20 ml /m was fed for 24 hours. A reactant mixture of VCl₂ (0.07 g/m), HF (0.03 g/m), nitrogen (16 ml/m) and oxygen (1.2 ml/m, 6 mole % on VCl₂) was then fed to the reactor. A gradual increase in both conversion of the VCl₂ and selectivity of VF₂ was obtained by increasing the temperature, e.g. at 550°C conversion was 29% and VF₂ selectivity was 12.8%. At 625°C, conversion of the VCl₂ was 100% and selectivity for VF₂ was 66%. The catalyst was continuously used for a total of 62 hours without any sign of catalyst deactivation or deterioriation. Table 4 summarizes the results of the catalyst performance between 550°C and 625°C. The same catalyst was activated under different conditions, e.g., at 550°C using 20 ml/m of air for 24 hours, followed by HF activation (0.035 g/m) for 24 hours, under these conditions, selectivity was only 1% for VF₂ using the same reactor feed at a reaction temperature of 550°C. The results listed in Table 5 indicate that air activation of the catalyst at a higher temperature for a longer time provided a significant improvement in selectivity under comparable reaction conditions. Therefore, it is preferred to use high temperatures (650°C or above) and air (60 hours) to activate the catalyst. Example 9 Alumina (200 g) was added portionwise to a stirred solution of 52 % by weight aqueous HF (500 ml). Addition was controlled in such a way to keep the solution temperature between 40° and 45°C. After complete addition (7 hours), the milky reaction mixture was left to cool down to room temperature without stirring and AlF₃.9H₂O precipitated. The solid was recovered on a filter and washed several times with acetone until it tested neutral with litmus paper. The collected solid was air dried at room temperature to give AlF₃.3H₂O, which was then heated in stages, e.g. 100°C/2 hours, 150°C/2 hours and finally at 175°C for 18 hours. The resulting anhydrous material was ground with a mortar and pestle. The fine powder obtained was sieved and a 60 to 100 mesh fraction of the anhydrous AlF₃ particles were evaluated for catalytic activity as described below. The aluminum fluoride (31 g) was placed in the middle 10.2 cm (4") of a 2.54 cm O.D. x 30.5 cm (1" O.D. x 12") Monel reactor. The gas inlet tube for the reactants extended directly to the catalyst powder. The bottom 10.2 cm (4") of the reactor was filled with nickel alloy chips which were separated from the catalyst powder using an 80 mesh screen. Under these conditions, the temperature range over the length of the catalyst bed was 30°C with the maximum temperature equal to 560°C. The catalyst was activated at 650° for 24 hours using 20ml/m flow of air, followed by HF activation, (0.035 g/m for 24 hours at 550°C using 20 ml/m of nitrogen as a co-carrier gas). VCl₂ was separately vaporized and then combined with 17 ml/m of nitrogen and 0.6 ml/m (3.7 mole % of the VCl₂ feed) of O₂ at the top of the reactor and the mixture passed through the catalyst bed together with HF at a reaction temperature of 557°C. The flow of VCl₂ was 0.07 grams/minute and the flow of HF was 0.03 grams/minute. The mol percent conversion of VF₂ increased with reaction time to a maximum at 10 hours as shown in Table 6. Example 10 Preparation and Evaluation of CrF₃ 4.4%/FeF₃ 4%/AlF₃ 91.6% Catalyst CrF₃·3H₂O (30 g) was dissolved in hot water (80°C) (150 ml) in presence of 1.5 g of SnCl₂. To the resulting dark green solution were added 500 ml (52% by weight) of aqueous HF, followed by 20.5 g of FeCl₃. Subsequently, alumina (200 g) was added portionwise in such a way to maintain the temperature between 40 and 45°C. The light green solution was covered and left at room temperature. A solid separated on standing and the precipitated solid was filtered and washed several times with acetone until it was acid free. The solid was air dried for 18 h and then was heated in stages in an oven at 100°C/2 h, 150°C/2 h , and finally at 175°C for 18 h. The catalyst was ground using a mortar and pestle, 65 g of the sieved 60 to 100 mesh catalyst was placed in 2.54 cm x 30.5 cm (1" x 12") Hastelloy C® reactor. The catalyst was activated at 650°C using 20 ml/m of air for 18 h, followed by HF activation (0.05 g/m 24 h). A mixture of VCl₂ (0.07 g/m), HF (03 g/m), N₂ 16 ml/m and O₂ 1.2 ml/m, was fed to the reactor. An increase in both % conversion and % VF₂ selectivity was obtained by increasing the temperature as found in Example 8., e.g. at 500°C, the VF₂ selectivity was 14.6 at 31% conversion, and, at 625°C, the VF₂ selectivity was 76% at 100% conversion (Table 7). The catalyst was used continuously for 60 hours without the need for regeneration.

Claims: A process for the preparation of vinylidene fluoride comprising reacting vinylidene chloride with anhydrous HF in the gas phase at a temperature of from 400° to 700°C in the presence of oxygen and an anhydrous AlF₃ containing catalyst. The process of claim 1 wherein the molar ratio of HF to vinylidene chloride ranges from 2:1 to 10:1 and the amount of oxygen ranges from 1 to 160 mole percent based on the amount of vinylidene chloride. The process of claim 2 wherein the amount of oxygen ranges from 1 to 25 mole percent based on the amount of vinylidene chloride. The process of claim 2 wherein the amount of oxygen ranges from 1 to 10 mole percent based on the amount of vinylidene chloride, the reaction temperature is from 575° to 625°C, and the catalyst is activated in the presence of oxygen at a temperature of from 400° to 700°C and in the presence of anhydrous HF at a temperature up to 600°C. The process of claim 1 wherein the catalyst is anhydrous AlF₃. The process of claim 2 including nitrogen as a carrier gas. The process of claim 1 including the step of periodically regenerating the catalyst by passing oxygen through the catalyst bed at a temperature of at least 500°C. The process of claim 1 wherein the catalyst is anhydrous AlF₃ in combination with a transition metal fluoride selected from iron, cobalt, chromium, nickel, zinc and combinations thereof. The process of claim 8 wherein the molar ratio of HF to vinylidene chloride ranges from 2:1 to 10:1 and the amount of oxygen ranges from 1 to 160 mole percent based on the amount of vinylidene chloride. The process of claim 8 wherein the amount of oxygen ranges from 1 to 25 mole percent based on the amount of vinylidene chloride. The process of claim 9 including nitrogen as a carrier gas. The process of claim 8 including the step of periodically regenerating the catalyst by passing oxygen through the catalyst bed. The process of claim 8 wherein the catalyst contains up to 30 weight percent of transition metal based on the weight of aluminum fluoride. The process of claim 13 wherein the catalyst contains from 7.5 to 10 weight percent transition metal based on the weight of aluminum fluoride. The process of claim 8 wherein the amount of oxygen ranges from 1 to 10 mole percent based on the amount of vinylidene chloride, the reaction temperature is from 575° to 625°C and the catalyst is activated in the presence of oxygen at a temperature of from 400° to 700°C and in the presence of anhydrous HF at a temperature up to 600°C.

Inventors: ELSHEIKH, MAHER YOUSEF
Applicants: ATOCHEM NORTH AMERICA, INC. (A PENNSYLVANIA CORP.)
Application year: 1988
Main classification: C07C21
IPC codes: C07C17, C07B61, B01J27, C07C67, B01J23, C07C21