Process for preparing flowable, stable and hardenable suspensions, and thus-obtained compositions

Abstract: A process for preparing flowable, stable and hardenable compositions, comprising mixing: a) a liquid basis constituted by at least one polymerizable monomer; b) a finely ground mineral filler; c) a silanizing agent for the mineral filler; and d) a hydrolysis catalyst of the silanizing agent, selected from the ammonium salts of organic acids.

Description: The present invention relates to a process for preparing flowable, stable and hardenable suspensions, and to the thus-obtained compositions. More particularly, the present invention relates to a process of preparing stable suspensions of mineral fillers in acrylic and/or methacrylic monomers, suitable for bulk polymerization. It is known that suspensions of mineral fillers in polymerizable liquids, having a high stability over the time necessary before being used in the preparation of finished articles by polymerization, can be obtained by using suitable suspending and viscosity-depressing agents. An Italian patent No. 1,038,488, flowable, stable and hardenable suspensions based on a polymerizable organic liquid and on a particulated inorganic filler are disclosed, which are obtained in the presence of a copolymeric suspending agent (polymeric dispersant) containing in its chain a component solvatable by the hardenable liquid, and at least one group capable of associating with the mineral filler dispersed in the liquid basis. In order to improve the mechanical properties of the finished articles, to the suspension is added a low-molecular-weight coupling agent, generally a silane, which is capable of forming strong chemical bonds with both the liquid basis and the mineral filler. As an alternative, processes for preparing the above mentioned compositions have been disclosed, wherein as the viscosity depressants only coupling agents, possibly in admixture with surfactants of the anionic, cationic or non-ionic type, are used. U.K. Patent Nos. 1,111,603; 1,132,261; and 1,140,542 disclose compositions based on alkyl-methacrylic type monomers, which contain high amounts of finely ground mineral fillers pretreated with a coupling agent selected from the organic derivatives of silicon. According to the disclosures of these patents, a mineral filler, preferably on a siliceous basis, is treated, before being mixed with the polymerizable liquid monomer, with an organic derivative of silicon containing at least one functional group capable of reacting with the surface of the inorganic filler and at least one functional group capable of copolymerizing with the methacrylic monomer. The functional group reactive with the mineral filler is preferably a hydrolysable group bonded to the silicon atom and which supposedly reacts with the hydroxy groups bonded to the surface of the inorganic material, in order to form very stable oxygen-bridge bonds. The thus pre-treated inorganic material is added to the polymerized liquid basis and the obtained composition, to which surfactants are possibly added, in order to improve its flowability, results in a composition stable over time, pourable into moulds, and capable of yielding finished articles having good mechanical properties. In European patent application No. EP-A-218,866 compositions based on esters of acrylic or methacrylic acid are disclosed, which contain a finely ground mineral filler, wherein the silanization of the above described inorganic material takes place in situ when the mineral filler is added to the polymerizable liquid basis. According to the disclosure of that patent application, there are added to the polymerizable liquid basis an organic compound of silicon, also capable of polymerizing with the acrylic or methacrylic monomer and of reacting with the inorganic filler, and an alkylamine capable of acting as a catalyst for the above said silicon-organic compound. However, in order to obtain a composition having good flowability, and therefore suitable for being poured into moulds, the mineral filler should be added to the liquid blend very slowly, in such a way that the viscosity of the obtained composition never exceeds 10 Pa.s. In German patent application No. 3,531,913, the above mentioned drawback is overcome by adding to the composition an amount of up to 5% by weight of a suitable viscosity-depressing agent, such as soy lecithin. We have now found that it is possible to prepare stable and flowable (fluid) suspensions of finely ground mineral fillers in a polymerizable liquid, by directly silanizing the inorganic material in situ , but without the drawbacks of the prior art (controlled addition of the mineral filler, or use of soy lecithin), by using particularly efficacious silanization catalysts. The present invention provides a process for preparing flowable, stable and hardenable suspensions, comprising mixing: a) a liquid basis, constituted by at least one polymerizable monomer; b) a finely ground mineral filler; c) a silanizing agent for the mineral filler; and d) a hydrolysis catalyst for the silanizing agent, selected from the ammonium salts of organic acids. The polymerizable monomer is preferably selected from the alkyl esters of acrylic or methacrylic acid, wherein the alkyl group contains from 1 to 6 carbon atoms. Examples of such esters are methyl methacrylate (MMA), ethyl methacrylate, propyl methacrylate, butyl methacrylate, methyl acrylate, ethyl acrylate, and butyl acrylate. Furthermore, as polymerizable monomers, vinylic monomers such as styrene, alpha-methyl-styrene, or acrylonitrile, can be used. Methyl methacrylate, either alone, or mixed with up to 50% by weight of the above-said monomers, is particularly preferred. Mineral fillers suitable for use in the process of the present invention are inorganic substances having hydrophilic surfaces characterized by the presence of polar groups, preferably hydroxyl groups, which can react with the silanizing agent or form a hydrogen bridge with the siloxanic groups. Examples of suitable fillers are amorphous or crystalline silica (quartz, cristobalite), glass, alumina, aluminium trihydroxide, calcium carbonate, mineral silicates, aluminosilicates (mica, talc, wollastonite), mineral oxides, such as Fe₂O₃, TiO₂, Cr₂O₃, asbestos, and fibreglass. The mineral fillers are finely ground both in order to obtain adequate aesthetic and mechanical properties in the finished articles and in order to obtain a proper stability of the suspension. The particles of the filler should preferably have granular or spheroidal shape; however for particular applications, particles having a different shape, e.g. needle-like, as in case of use of fibreglass, can be used as well. For particular applications, mixtures of particles of granular or spheroidal shape with particles of needle-like shape can be used. The average particle diameter is preferably from 0.1 to 50 micrometres, and more preferably from 1 to 20 micrometres. The surface area is generally from 0.5 to 10 m²/g, preferably from 2 to 7 m²/g. The silanizing agent is an organic derivative of silicon containing hydrolysable groups, and is preferably selected from those having general formula: R₁ZR₂Si(OR₃) wherein: R₁ represents a hydrogen atom, an either saturated or unsaturated alkyl, cycloalkyl, or alkylaryl radical or an aryl radical containing from 1 to 20 carbon atoms, optionally substituted with hydroxy, mercapto, amino, epoxy, optionally esterified or amidated carboxyl groups, or a saturated or unsaturated acyl radical containing from 2 to 20 carbon atoms; Z represents a direct bond or a bivalent radical selected from -O-, -NH-, -S-, -CH₂-: R₂ represents a direct bond or an alkylenic, arylenic, optionally alkyl-substituted radical, containing from 1 to 20 carbon atoms; R₃ represents an alkyl, aryl, alkyl-aryl radical containing from 1 to 20 carbon atoms, optionally substituted with alkoxy, alkylamino or alkylmercapto groups, wherein the alkyl group contains from 1 to 12 carbon atoms. Examples of usable silanes are methyltriethoxysilane, methyltrimethoxysilane, vinyltriethoxysilane, gamma-methacryloxypropyltrimethoxysilane, gamma-methacryloxyloxypropyltris(2-methoxyethoxy)silane, gamma-glycidoxypropyltrimethoxysilane, gamma-mercaptopropyltriethoxysilane, gamma-aminopropyltriethoxysilane, and N-beta(aminoethyl)gamma-amino-propyltrimethoxysilane. The catalyst of silane hydroylsis is preferably selected from the ammonium salts of organic acids having general formula: R₄COO⁻/NR₅R₆R₇R₈/⁺ wherein: R₄ represents a hydrogen atom or an optionally unsaturated alkyl, cycloalkyl, or alkylaryl radical or an aryl radical containing from 1 to 20 carbon atoms, and R₅, R₆, R₇, R₈, which may be the same as or different from each other, may be hydrogen, or alkyl or cycloalkyl radicals containing from 1 to 20 carbon atoms. Examples of catalysts are isopropylammonium acetate, isopropylammonium methacrylate, ammonium oleate, ammonium stearate, ammonium methacrylate, n-propylammonium methacrylate, dimethylammonium butyrate, isopropylammonium oleate, isopropylammonium benzoate, and ethylammonium acrylate. The catalyst can be prepared by means of the direct addition of the organic acid to ammonia or to the amine; such a reaction can be carried out separately, or directly in situ in the composition. According to a preferred embodiment of the present invention, to the suspensions there may be also added surface-active agents soluble in the monomer, and with a high enough affinity for the mineral filler. In general, the use of surfactants containing ethoxy or propoxy groups, such as ethoxylated alkylphenols, sulphonate agents, alkyl sulphates, alkylammonium phosphates and phosphonates, wherein the alkyl group contains up to 20 carbon atoms, and phosphoric esters, is advisable. Examples of surfactants are ethoxylate nonylphenol containing from 1 to 15 molecules of ethylene oxide, ethoxylated octylphenol containing from 1 to 15 molecules of ethylene oxide, ammonium dodecylbenzenesulphonate, sodium 2-ethylhexylsulphosuccinate, double sulphate of ammonium and ethoxylated lauryl alcohol with 1-3 ethylene oxide molecules, (C₄C₁₂)-alcohol phosphates, and acid phosphates of stearamidopropyldimethyl-β-hydroxyethylammonium. The amount of surfactant is preferably from 0 to 0.5% by weight, more preferably from 0.05 to 0.20% by weight, based on the total mass. The amount of mineral filler to be used in the compositions of the present invention depends on the desired characteristics of the end articles and on the characteristics of flowability of the suspension. In general, the use of high percentages of fillers, from 30 to 80% by weight based on the total, is preferred. As an example, in the case of siliceous fillers, it is better to work with concentrations higher than 50% by weight. Correspondingly, percentages of from 70 to 20% by weight of the polymerizable monomer, or monomer mixture, are generally used. The silanizing agent is preferably used at concentrations from 0.01 to 2%, more preferably from 0.05 to 0.1%, by weight, based on the filler. The catalyst is preferably used at concentrations from 0.01 to 1%, more preferably from 0.01 to 0.5%, by weight, based on the total composition. Besides the above listed compounds, to the suspensions other compounds may be possibly added, such as: 1) mono-, or bi-, or polyfunctional monomers soluble in the main monomer and copolymerizable with it, e.g. ethyleneglycol dimethacrylate, triethyleneglycol dimethacrylate, tetraethyleneglycol dimethacrylate, pentaerythritol tetraacrylate, and divinylbenzene, the amounts thereof being from 0 to 2% by weight, based on the total composition: 2) pigments and/or inorganic and/or organic dyes, the amounts thereof being from 0 to 5% by weight based on the total composition; 3) mould-release agents, antistatic agents, plasticizers, anti-U.V. agents, antioxidants, polymerization inhibitors, in amount from 0 to 2% by weight, based on the total composition. The stable compositions of the present invention can be prepared within short times and at room temperature, have a low viscosity which depends on the filler content and granulometry, but which is generally from 0.01 to 0.3 Pa.s, and are easily redispersable after a long storage. The viscosity of the suspension can be furthermore increased, and adjusted at an optimum level for injection moulding or for bulk polymerizatrion by means of the addition of well-known viscosity modifiers, such as methacrylic or vinylic homo- and/or copolymers. In order to obtain considerable viscosity changes with a small addition of the modifier, high-molecular-weight modifiers are advantageously used. Polymers or copolymers having an average molecular weight (Mw) comprised within the range of from 20,000 to 1,000,000, more preferably of from 50,000 to 500,000, are the most commonly used ones. Examples of polymers to be used as viscosity modifiers are polymethylmethacrylate, methylmethacrylatemethylacrylate copolymers, methylmethacrylate-styrene copolymers, methylmethacrylate-butylacrylate copolymers, polyethylmethacrylate, methylmethacrylate-methacryloxypropyltrimethoxysilane copolymers, polystyrene, and poly-alpha-methylstyrene. The amount of the polymeric modifier to be used also depends, partially, on the molecular weight thereof. In general, additions of up to 20% by weight based on the monomer, more preferably of from 0.05 to 10%, are advisable. The manner of carrying out the process of the present invention is of a conventional type; e.g., a ball mill can be used, the reactants being charged all at once, or at successive times, the mill being kept running until fluidization occurs. According to a different technique, the suspensions can be obtained by loading the components into a reactor, then submitting them to a slow stirring, and subsequently to a fast stirring, until fluidization occurs. The transformation into finished articles of the compositions of the present invention can take place by moulding under a pressure of from 1 to 4 atmospheres, and at a temperature from 70 to 100°C in case of sealed moulds, an amount of a peroxidic catalyst (e.g.benzoylperoxide or tert-butylcyclohexylperoxycarbonate) being preliminarily added, in an amount from 0.1 to 2%, preferably 0.2 to 0.7%, by weight, and with the possible preliminary addition of mould-release agents, such as stearic acid and glycerol monostearate. Before being moulded, the suspension is advantageously deaerated, by being submitted to a reduced pressure under stirring. By using milder polymerization conditions and proper thermal cycles, the suspension can be polymerized by means of techniques similar to those used for manufacturing cast methacrylic sheets, or for preparing articles according to roto-moulding technology. The invention in another aspect provides a flowable, stable and hardenable composition, comprising: a) a liquid basis constituted by at least one polymerizable monomer; b) a finely ground mineral filler; c) a silanizing agent for the mineral filler; and d) a hydrolysis catalyst for the silanizing agent, selected from the ammonium salts of organic acids. According to a preferred method of carrying out the process of the invention, there are effected the following steps. 1. There is charged into a ball mill the mineral filler (e.g. cristobalite) and a methyl methacrylate/methyl acrylate (98:2) copolymer such as that sold under the Trade-Name VEDRIL®. 2. Theres is charged into the mill a liquid component, comprising the polymerizable monomer, preferably methyl methacrylate; a polymerization inhibitor, such as that sold under the Trade-Name TOPANOL®; and a curing agent, such as tetraethyleneglycoldimethacrylate. 3. There is charged into the mill a silane, such as gamma-methacryloxypropyl-trimethoxysilane. 4. The mill is rotated overnight, for about 18 hours, to obtain a viscous paste. 5. There is added to the resulting paste, in the mill, a catalyst, such as isopropyl ammonium oleate; and a colouring component, suitably comprising a pigment (such as TiO₂), an organic liquid carrier (dibutyℓ phthalate) and a small amount of a conventional non-ionic surfactant (a polyethoxylated nonyl phenol containing on average 9 mols of ethylene oxide per mol). 6. The mill is rotated to complete the reaction, during about 6 hours, to obtain the final product. The invention will be further described with reference to the following illustrative Examples. EXAMPLE 1 Into a 5 litre porcelain mill, containing ceramic balls of 30 mm diameter for a total actual volume of 1.2 litres, were charged 615 g of methylmethacrylate (MMA) containing 200 ppm of Topanol A (2,4-dimethyl-6-tert.-butylphenol) as the inhibitor; 6 g of ethyleneglycol dimethacrylate; 21 g of gamma-methacryloxypropyltrimethoxysilane; 5 g of isopropylammonium oleate; and 1500 g of cristobalitic silica having an average granulometry of approximately 6 micrometres and a surface area of 3.5 m²/g. The mill was revolved for 5 hours at a revolution speed of approximately 25 rpm, and the obtained suspension had a viscosity of 0.038 Pa.s. 70 g of TiO₂-based dyeing paste (80% by weight of TiO₂, 15% by weight of dibutyl phthalate, 5% by weight of nonylphenol ethoxylated with 9 mol of ethyleneoxide) and 45 g of MMA-ethyl acrylate copolymer (98/2 ratio by weight, average molecular weight 100,000) were added in the mill to 2,000 g of the above suspension. The mill was allowed to revolve for a further 6 hours, and was then discharged. The suspension was a flowing fluid, with a viscosity of 0.25 Pa.s. (as measured by Brookfield Viscometer LVT4, rotor No. 2) at the discharge point, and of 0.17 Pa.s. after 24-hour standing. The viscosity of the suspension was measured again after a 3-month storage at room temperature. For such purpose, the suspension was homogenized again by tumbling the container for approximately 6 hours; the viscosity was found to be equal to the original value (0.15 Pa.s). To the suspension were added 0.6% by weight of Perkadox 16® (bis-4-tert.-butylcyclohexylperoxydicarbonate), and 0.15% of stearic acid, the suspension was stirred up to complete solution and homogenization, and deaerated under reduced pressure for 10 minutes and poured between two crystal plates. The resulting sandwich was plunged into a water bath at 85°C for 30 minutes, in order to carry out the polymerization. A polymerized slab of 200 cm², and of 3 mm thickness, was obtained, with glossy surface and free from cracks or other faults. From the slab, specimens were obtained for the evaluation of the mechanical and physical characteristics. The results were the following. Test Method Results Specific Gravity - 1.8 Kg/dm³ Rockwell Surface Hardness-B Scale ASTM D 785 98 Flexural Modulus ASTM D 790 16.880 MN/m² Mechanics of Fracture on Pendulum (Kic) - 1.6 MN/m 3/2 Gloss at 85° ASTM D 523 96% White Index - amber 84.9 blue 85.0 green 85.5 The White Index was measured by a Photovolt Model 60 type apparatus manufactured by Photovolt, with ultra-pure magnesium oxide being used as the reference. The method adopted for measuring Kic according to the Mechanics of Fracture on Pendulum was based on principles applied in the evaluation of the tenacity of composite materials (ASTM STP 410 - William F. Brown Jr. and John E. Srawly 1966, page 13). The evaluation technique was so set up, as to measure the tenacity at high speed of the test, under extremely critical conditions of notch sharpness, such as can occur in manufactured articles in correspondence of faults. The test was carried out on specimens 3 mm in thickness (B), 6 mm in width (W) and 60 mm in length. The depth of the sharp notch (a), realized with a normal razor-blade, was 2.5 mm, and the distance from the supports was 48 mm. The thus-obtained specimens were submitted to an impact at a speed of 0.5 m/second. The Kic values were computed on the basis of the equation: Kic = Y o C a wherein a is the depth of the notch, Y is the geometric factor (ASTM STP 410) and o C = 3/2 Fr.s (s = distance between the supports; Fr = break point). EXAMPLE 2 To the mill of Example 1 were charged 650 g of MMA containing 200 ppm of Topanol A; 12 g of ethyleneglycol dimethacrylate; 48 g of gamma-methacryloxypropyltrimethoxysilane; 2.38 g of isopropylammonium methacrylate; and 1,680 g of cristobalitic silica, having the same characteristics as of that of Example 1. The mill was revolved for 1 hour at a speed of approximately 25 rpm and the obtained suspension had a viscosity of 0.05 Pa.s. For comparative purposes, a similar suspension was prepared, but without the ammonium salt; after 5 hours of tumbling, the composition had a viscosity higher than 10 Pa.s, with a thixotropic behaviour. After a further 3 hours, the suspension has a viscosity of 0.45 Pa.s, which dropped to 0.12 Pa.s after 24 hours of tumbling. EXAMPLE 3 To the mill of Example 1 where charged 650 g of MMA stabilized with 200 ppm of Topanol A; 15 g of tetraethyleneglycoldimethacrylate; 4.6 g of gamma-methacryloxypropyltrimethoxysilane; 40 g of MMA-methyl acrylate copolymer, with a weight ratio of 98/2 and average molecular weight 100,000; and 1,700 g of cristobalitic silica. The mill was tumbled for 10 hours, and then to the mixture were added 10 g of methylmethacrylate; 80 g of TiO₂ paste having the same characteristics as reported in Example 1; and 2.5 g of isopropylammonium methacrylate. After 4 hours of tumbling, the viscosity of the suspension was 0.3 Pa.s. EXAMPLE 4 The test were run according to the same manner as described in Example 3, except that the ammonium salt was prepared in situ , by adding 1.5 g of methacrylic acid and 1.029 g of isopropylamine. The end viscosity, after 4 hours of tumbling, was 0.3 Pa.s.

Claims: A process for preparing flowable, stable and hardenable suspensions, comprising mixing: a) a liquid basis constituted by at least one polymerizable monomer; b) a finely ground mineral filler; c) a silanizing agent for the mineral filler; and d) a hydrolysis catalyst of the silanizing agent, selected from the ammonium salts of organic acids. A process as claimed in claim 1, wherein the polymerizable monomer is at least one alkyl ester of acrylic or methacrylic acid, wherein the alkyl group contains from 1 to 6 carbon atoms. A process as claimed in claim 2, wherein the polymerizable monomer is selected from methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, methyl acrylate, ethyl acrylate, and butyl acrylate. A process as claimed in any of claims 1 to 3, wherein the polymerizable monomer is methyl methacrylate, either alone or admixed with up to 50% by weight of one or more other monomers. A process as claimed in claim 1, wherein the polymerizable monomer is a vinylic monomer such as styrene, alpha-methyl-styrene, or acrylonitrile. A process as claimed in any of claims 1 to 5, wherein the mineral filler is at least one inorganic substance having a hydrophilic surface containing polar groups capable of reacting with the silanizing agent, or of forming hydrogen bridges with siloxanic groups and having particle diameter from 0.1 to 50 micrometres and a surface area from 0.5 to 10 m²/g. A process as claimed in claim 6, wherein the mineral filler has particle diameter from 1 to 20 micrometres and a surface area from 2 to 7 m²/g. A process as claimed in claim 6 or 7, wherein the mineral filler is selected from one or more amorphous or crystalline silica, glass, alumina, aluminium trihydroxide, calcium carbonate, mineral silicates, alumino-silicates, mineral oxides, such as Fe₂O₃, TiO₂, Cr₂O₃, asbestos, and fibreglass. A process as claimed in any of claims 1 to 8, wherein the amount of mineral filler is from 30 to 80% based on the total composition. A process as claimed in any of claims 1 to 9, where the silanizing agent is an organic derivative of silicon containing hydrolysable groups, and is selected from those having general formula: R₁ZR₂Si(OR₃) wherein: R₁ represents a hydrogen atom, a saturated or unsaturated alkyl, cycloalkyl, or alkylaryl radical, an aryl radical containing from 1 to 20 carbon atoms, optionally substituted with hydroxy, mercapto, amino, epoxy, optionally esterified or amidated carboxyl groups, or a saturated or unsaturated acyl radical containing from 2 to 20 carbon atoms; Z represents a direct bond or a bivalent radical selected from -O-, -NH-, -S-, -CH₂-; R₂ represents a direct bond or an alkylenic, arylenic, optionally alkyl-substituted radical, containing from 1 to 20 carbon atoms; R₃ represents an alkyl, aryl, or alkyl-aryl radical containing from 1 to 20 carbon atoms, optionally substituted by alkoxy, alkylamino or alkylmercapto groups, wherein the alkyl group contains from 1 to 12 carbon atoms. A process as claimed in claim 10, wherein the silanizing agent is selected from methyltriethoxysilane, methyltrimethoxysilane, vinyltriethoxysilane, gamma-methacryloxypropyltrimethoxysilane, gamma-methacryloxyloxypropyltris(2-methoxyethoxy)silane, gamma-glycidoxypropyltrimethoxysilane, gamma-mercaptopropyltriethoxysilane, gamma-aminopropyltriethoxysilane, and N-beta(aminoethyl)gamma-amino-propyltrimethoxysilane. A process as claimed in any of claims 1 to 11, wherein the silanizing agent is used at a concentration from 0.01 to 2%, and preferably from 0.05 to 1%, by weight based on the loaded material. A process as claimed in any of claims 1 to 12, wherein the catalyst for silane hydrolysis is selected from the ammonium salts of organic acids having general formula; R₄COO⁻/NR₅R₆R₇R₈/⁺ wherein: R₄ represents a hydrogen atom or an optionally unsaturated alkyl, cycloalkyl, or alkylaryl radical, or an aryl radical containing from 1 to 20 carbon atoms, and R₅, R₆, R₇, R₈, which may be the same as or different from each other, may be hydrogen, or alkyl or cycloalkyl radicals containing from 1 to 20 carbon atoms A process as claimed in claim 13, wherein the catalyst is selected from isopropylammonium acetate, isopropylammonium methacrylate, ammonium oleate, ammonium stearate, ammonium methacrylate, n-propylammonium methacrylate, dimethylammonium butyrate, isopropylammonium oleate, isopropylammonium benzoate, and ethylammonium acrylate. A process as claimed in any of claims 1 to 14, wherein the amount of catalyst is from 0.01 to 1%, preferably from 0.01 to 0.5%, by weight based on the total composition. A process as claimed in any of claims 1 to 15, wherein a surface-active agent containing ethoxy or propoxy groups is added to the composition. A process as claimed in claim 16, wherein the surface-active agent is selected from ethoxylated alkylphenols, sulphonated agents, alkyl sulphates, alkylammonium phosphates and phosphonates, and phosphoric esters. A process as claimed in any of claims 1 to 17, wherein the amount of surface-active agent is from 0 to 0.5%, preferably from 0.05 to 0.2%, by weight based on the total mass. A flowable, stable and hardenable composition, obtained from: a) a liquid basis constituted by at least one polymerizable monomer; b) a finely ground mineral filler; c) a silanizing agent for the mineral filler; and d) a hydrolysis catalyst for the silanizing agent, selected from the ammonium salts of organic acids. A composition as claimed in claim 19, having a viscosity from 0.01 to 0.3 Pa.s. A composition comprising the product of the process as claimed in any of claims 1 to 18. A shaped article, manufactured by pouring and cross-linking in a mould a composition as claimed in any of claims 19 to 21.

Inventors: BINAGHI MARCO, GIUDICI DARIO, MARCIANDI FRANCO, BINAGHI, MARCO, GIUDICI, DARIO, MARCIANDI, FRANCO
Applicants: ATOCHEM ELF ITALIA, ELF ATOCHEM ITALIA S.R.L.
Application year: 1988
Main classification: C08F2
IPC codes: C08F2, C08F20, C08G77, C08F30