Low equivalent weight sulfonic fluoropolymers

Abstract: The invention is a sulfonic fluoropolymer having a fluoropolymer backbone having pendant groups attached thereto and represented by the general formula: ZSO₂-(CF₂) a -(CFR f ) b -O- where: Z is selected from a halogen, an alkali metal, hydrogen, or OR; R is a branched or linear alkyl radical having from 1 to 10 carbon atoms or an aryl radical; a is 0-2; b is 0-2; provided a + b is not equal to 0; R f is selected from -F, -Cl, perfluoroalkyl radials having from 1 to 10 carbon atoms and fluorochloroalkyl radicals having from 1 to 10 carbon atoms, wherein the sulfonic fluoropolymer has an equivalent weight of less than 800, and a hydration product of less than 29,000.

Description: The present invention resides in sulfonic fluoropolymers that have improved and unexpected physical and chemical properties. Sulfonic fluoropolymers containing pendant groups terminating with sulfonic groups have been described in the prior art including, for example, U.S. Patent 4,478,695, issued October 23, 1984; U.S. Patent 4,417,969, issued November 29, 1983; and U.S. Patent 4,358,545, issued November 9, 1982. Such sulfonic fluoropolymers have been found to be useful in hot, aqueous media, such as chlor-alkali cells, when the sulfonic fluoropolymer's equivalent weight is above 800 and its hydration product is less than 22,000. These sulfonic fluoropolymers were also taught as being useful for a variety of other membrane separator applications and to be useful as acid catalysts. When sulfonic fluoropolymers are used as membranes, it is desirable for them to be in the form of films. They should have physical integrity commensurate with the physical demands of the device in which they will be used. In electrochemical devices, such as electrochemical cells, physical demands on the membrane vary, depending upon the type of cell and the configuration of the cell. For example, in some cells, electrodes (anodes and cathodes) are spaced substantially apart from each other and have the membrane placed between the two electrodes. In such cell configurations, the membrane functions, more or less, as a free-standing film. Such free-standing membrane films are commonly reinforced to increase their strength. Reinforcement materials which are commonly used include a variety of materials in the form of woven scrims and randomly-dispersed fibers. However, even when supported, there are still certain minimum levels of physical integrity which the membrane is required to have. Otherwise, it breaks apart and looses its utility. There are other types of electrochemical cells which are constructed to have electrodes or current collectors in intermittent or continuous contact with a membrane positioned between an anode and a cathode. Such cells are generally referred to as zero gap or solid polymer electrolyte cells. In such cells, the electrodes provide physical support such that membrane films with less physical integrity can be used, whether reinforced or not. Physical integrity of ionic fluoropolymers are determined, to a large degree, by the amount of water or solvent the fluoropolymers contain. Thus, a sulfonic fluoropolymer that swells excessively because it absorbs substantial amounts of water or solvent, tends to become gel-like and loses much of its physical integrity, relative to an unswollen sulfonic fluoropolymer. The level of swelling (the level of water absorption) is largely determined by the temperature and the environment. For example, a given sulfonic fluoropolymer may be swollen to different levels by water under different conditions. Pure water at a given temperature swells the sulfonic fluoropolymer more than aqueous, salt-containing electrolytes, which, in turn, swell the sulfonic fluoropolymer more than humid gases. However, it is known that increasing the temperature results in increased swelling (water absorption) in each environment listed above. Thus, a single definition of suitable physical characteristics of a sulfonic fluoropolymer to define its usefulness is difficult, because utility depends upon the use to which the sulfonic fluoropolymer will be put. The prior art defines sulfonic fluoropolymers as being useful primarily in terms of the water absorption of the sulfonic fluoropolymers in an environment of hot aqueous electrolytes, such as the type of environment found in electrolytic cells, for example chlor-alkali cells. From such considerations were derived the limitations of equivalent weights of from 800 to 1500 and hydration products of less than 22,000. In U.S. Patent No. 4,358,545 a sulfonic fluoropolymer having an equivalent weight of 798 and a hydration product of 29,400 was not considered useful because of excessive hydration. However, it has now been discovered that such equivalent weight and hydration product limitations are not valid for certain sulfonic fluoropolymers that are described herein. Another matter of concern in defining usefulness of sulfonic fluoropolymers as membranes, is the chemical requirements in a given application. Thus, a membrane of a sulfonic fluoropolymer in a chlor-alkali cell has two critical criteria that it should preferably meet: electrical conductivity and the ability to reject anions. The sulfonic fluoropolymer chosen for use in such conditions is usually based on a trade-off between the electrical conductivity of the polymer, which is effected by both equivalent weight and water absorption, and the polymer's ability to reject hydroxide ions, which is largely determined by the level of hydration, i.e., the degree of hydration per functional group in the sulfonic fluoropolymer. Under these circumstances, where it is desired to minimize the passage of hydroxide ions, the expert usually chooses a sulfonic fluoropolymer having a higher equivalent weight than if one based his decision strictly upon electrical conductivity of the fluoropolymer, alone. Thus, the physical properties of the fluoropolymer, as determined by swelling, is not the deciding factor in choosing the fluoropolymer for this particular use. Therefore, it would be very advantageous to have fluoropolymers which have high ionic conductivity while yet maintaining physical integrity as a viable selective ion transport medium. Other applications, such as fuel cells and proton pumps, present entirely different chemical and physical requirements for a membrane. The different conditions result in different levels of swelling of the sulfonic fluoropolymer, than encountered in the hot electrolytes of chlor-alkali cells. In fuel cell or proton pump applications, there is little, if any, requirement for rejection of negative ions. The primary requirement is transport of protons at the lowest possible electrical resistance. Thus, the sulfonic fluoropolymer having the lowest equivalent weight within physical constraints resulting from swelling characteristics is desired. The prior art (U.S. Patent 4,358,545) used the measured water swelling of a sulfonic fluoropolymer in its acid form (-H⁺) to calculate a hydration product as a means of combining two important sulfonic fluoropolymer properties: hydration as measured in moles of water per functional group and equivalent weight. This criteria continues to appear sufficient to characterize sulfonic fluoropolymers having superior performance characteristics. In addition, this prior art found a surprising difference between hydration characteristics of sulfonic fluoropolymers having short pendant chains as opposed to sulfonic fluoropolymers having longer pendant chains (U.S. Patent 3,282,875). EP-A 0 041 732 corresponding to US-A 4,470,889 discloses fluorinated sulfonic polymers having hydrolyzed equivalent weights of from 860 to 1500 which are useful as self-supporting membranes for chlorine-alkali electrolysis. EP-A 0 041 733 corresponding to US-A 4,358,545 discloses fluorinated sulfonic polymers. Polymers having an equivalent weight of between 800 and 1500 and a hydration product of less than 22,000 are designated as being suitable for the preparation of ion exchange membranes. A polymer having an equivalent weight of 798 and a hydration product of 29,400 was found to show an unacceptable degree of water absorption in contrast to polymers having a higher equivalent weight. EP-A 0 041 735 discloses fluorinated sulfonic polymers having equivalent weights of 894 (Example 1), 1240 (Example 2), 1725 (Example 3), 1666 (Example 5), 1275 (Example 6) and 1350 (Example 7). GB-A 2,053,902 discloses fluorinated sulfonic polymers having calculated hydrolyzed equivalent weights of 928 (Example 6), 774 (Comparative Example 2) and 1384 (Example 10). The polymer with an equivalent weight of 774 could not be formed into a film with sufficient mechanical strength. The invention is a sulfonic fluoropolymer having a fluoropolymer backbone having pendant groups attached thereto and represented by the general formula: ZSO₂-(CF₂) a -(CFR f ) b -O- where: Z is selected from a halogen, OM wherein M is an alkali metal, OH or OR; R is a branched or linear alkyl radical having from 1 to 10 carbon atoms or an aryl radical; a is 0-2; b is 0-2; provided a + b is not equal to 0; R f is selected from -F, -Cl, perfluoroalkyl radicals having from 1 to 10 carbon atoms and fluorochloroalkyl radicals having from 1 to 10 carbon atoms, wherein the sulfonic fluoropolymer has an equivalent weight of 766 or less and a hydration product of less than 29,000, when Z is OH. In a preferred embodiment, a + b is equal to 2 or 3, and the sulfonic fluoropolymer has an equivalent weight of less than 750. Prior to the present invention, it was thought that sulfonic fluoropolymers having attached pendant groups which terminate with a sulfonic group had insufficient strength, when formed into films, and exposed to conditions that swelled the sulfonic fluoropolymers, to maintain their physical integrity. It was thought that such sulfonic fluoropolymers, in the presence of water or another polar media, would merely be a gel and would have substantially no structural properties at all. Thus, it was believed that such sulfonic fluoropolymers were of substantially no value, even if they were cast into films and provided with additional supporting structures. However, it has now been discovered that sulfonic fluoropolymers can be prepared (using carefully controlled techniques) that have equivalent weights below 800 and which are perfectly suitable for many uses, including uses where the sulfonic fluoropolymer must have film properties (supported or unsupported). This discovery is particularly significant because it provides sulfonic fluoropolymers which have substantially more functional groups per unit mass of sulfonic fluoropolymer, than do sulfonic fluoropolymers of the prior art. This increase in the concentration of functional groups, while maintaining the physical integrity of the sulfonic fluoropolymer films, provides a sulfonic fluoropolymer that has the ability to transport more ions, and thus, the ability to operate much more efficiently than corresponding sulfonic fluoropolymers of the prior art that have higher equivalent weights. Polymer compositions of the invention have a broader range of hydration properties and an equivalent weight range previously believed to be deficient. It is believed that the sulfonic fluoropolymers of the present invention have surprisingly good film properties because their molecular and equivalent weights are more uniform (molecule to molecule), than the molecular weight of the sulfonic fluoropolymers of the prior art. It is thought that molecular weight, as well as molecular weight distribution of sulfonic fluoropolymers, play a role in the degree to which the sulfonic fluoropolymer will swell, when exposed to water or other polar media. Low molecular weight sulfonic fluoropolymer fractions are believed to plasticize the sulfonic fluoropolymer and result in increased swelling. Lower equivalent weight sulfonic fluoropolymer fractions are also thought to distort the swelling of the sulfonic fluoropolymer, measured for a given equivalent weight sulfonic fluoropolymer, because of nonlinear swelling that occurs at sufficiently low equivalent weight. The exact molecular weight and molecular weight distribution of sulfonic fluoropolymers, as well as equivalent weight distribution, are difficult to measure. However, the resultant effects of these factors, and possibly other factors yet to be identified, can be seen by the simple measurement of water swelling of the sulfonic fluoropolymer in its acid form using, what has come to be accepted as a standard method, a method described by W. G. F. Grot et al., Perfluorinated Ion Exchange Membranes , 141st National Meeting of The Electrochemical Society, Houston, Texas, May 1972. It would, of course, be possible to develop similar swelling relationships with ionic forms of the fluoropolymer other than the acid (hydrogen) form, but for conventional reasons, the acid form is used throughout the present specification. It has been found that sulfonic fluoropolymers of the invention having short pendant chains can have hydration products of less than 22,000 at equivalent weight values well below 800, while still demonstrating film properties useful in a variety of processes. Sulfonic fluoropolymers meeting such useful criteria have been prepared at equivalent weights as low as 687, while having a hydration product of 19,700. Preferably, the sulfonic fluoropolymers of the invention have hydration products of less than 26,000, more preferably less than 22,000, and even more preferably less than 15,000. Likewise, the sulfonic fluoropolymers of the invention can have equivalent weights of less than 750, preferably less than 700, more preferably less than 675, and most preferably less than 650. These sulfonic fluoropolymers are particularly useful in applications where the environment does not consist of hot liquid electrolytes or when there are less severe physical requirements. Exemplary of these applications is where the environment is largely humid vapors such as in fuel cells or proton pumps. Sulfonic fluoropolymers having a hydration product up to as high as 29,000 even in applications involving hot aqueous media when used as support layers in composite membranes, and particularly when reinforced, are useful. It has been discovered that fluoropolymers can have good film properties at equivalent weights below 750 and a hydration product of less than 26,000, less than 22,000, or even less than 15,000. Some sulfonic fluoropolymers can have hydration products below 22,000 and have equivalent weights below 700, or even below 675. Sulfonic fluoropolymers of the invention having a fluoropolymer backbone and having pendant groups attached thereto represented by the general formula: ZSO₂-(CF₂) a -(CFR f ) b -O- where Z, a, b and R f are as hereinbefore defined, provided however, that a + b is equal to 1 or 2, and wherein the sulfonic fluoropolymer has an equivalent weight less than 750 have only minimal film properties but are still useful for a variety of purposes including, for example, coating ion selective electrodes. Also, such sulfonic fluoropolymers may be mixed with or coated onto support materials where the physical shape and integrity of the final product are controlled by the support material. In these cases the sulfonic fluoropolymer may be used as either a protective barrier, an ionic conducting material, or both, such as in the case of an electrode coating. Since the sulfonic fluoropolymer is not dependent upon itself for its physical stability, the necessity of the sulfonic fluoropolymer film being self-supporting is not needed. In such cases, the hydration product of the sulfonic fluoropolymer is not critical and may exceed 29,000. In fact, the hydration product of such sulfonic fluoropolymers can be quite high. They may be as high as, or higher, than 100,000. The primary requirements for these types of sulfonic fluoropolymers are that they are not soluble in the environment where they are used or that they are soluble during the processing step to convert the sulfonic fluoropolymers to their ionic form, as described later in the specification. The equivalent weight of such polymers can be less than 725, less than 700, less than 675, or even less than 650. Some sulfonic fluoropolymers have been shown to have equivalent weights of less than 600 or even less than 575. Sulfonic fluoropolymers having equivalent weights less than 766 and hydration products less than 29,000 are useful as films in a variety of electrochemical applications whereas sulfonic fluoropolymers having equivalent weights less than 750, but usually not less than 500, are useful where ionic conductivity is the prime concern and physical requirements are minimal, but the requirement for insolubility as described above is necessary. It is believed that the combination of shorter pendant groups and careful control to produce uniform sulfonic fluoropolymers allows the existence of such materials. Sulfonic fluoropolymers having fluoropolymer backbones and pendant groups attached thereto and terminating in a sulfonyl group are suitable for use in the present invention. Examples of such sulfonic fluoropolymers are illustrated, for example, in U.S. Patent Nos. 4,578,512, Mar. 25, 1986; 4,554,112, Nov. 19, 1985; 4,515,989, May 7, 1985; 4,478,695, Oct. 23, 1984; 4,470,889, Sept. 11, 1984; 4,462,877, July 31, 1984; 4,417,969, Nov. 29, 1983; 4,358,545, Nov. 9, 1982; 4,358,412, Nov. 9, 1982; 4,337,211, June 29, 1982; 4,337,137, June 29, 1982; and 4,330,654, May 18, 1982. Other short-chain polymers are shown in U.S. Patent Nos. 4,329,434 and 4,329,435. Particularly preferred sulfonic fluoropolymer materials for use in the present invention are copolymers of monomer I with monomer II (as defined below). Optionally, a third type of monomer may be copolymerized with I and II. The first type of monomer is represented by the general formula: (I) CF₂=CZ'Z'' where: Z' and Z'' are independently selected from -H, -Cl, -F, or -CF₃. Upon polymerization with monomer II or with monomers II and III, monomer (I) forms part of the backbone of the sulfonic fluoropolymer. The second monomer comprises one or more monomers selected from compounds represented by the general formula: (II) ZSO₂-(CF₂) a -(CFR f ) b -O-CF=CF₂ where: Z is selected from a halogen, OM wherein M is an alkali metal, OH, or OR; R is a branched or linear alkyl radical having from 1 to 10 carbon atoms or an aryl radical; a is 0-2; b is 0-2; provided a + b is not equal to 0; R f is selected from F, Cl, perfluoroalkyl radicals having from 1 to 10 carbon atoms or fluorochloroalkyl radicals having from 1 to 10 carbon atoms. Particularly preferred is when R f is F; and a + b is 2 or 3. Most particularly preferred is when R f is -F and a + b is 2. Monomer (II) forms a pendant group having the formula: ZSO₂-(CF₂) a -(CFR f ) b -O- The third, and optional, monomer suitable is one or more monomers selected from the compounds represented by the general formula: (III) Y-(CF₂) a' -(CFR f' ) b' -CFR f'' -O-[CF(CF₂X)CF₂-O-]n-CF=CF₂ where: Y is selected from -F, -Cl or -Br; a' and b' are independently 0-3; n is 0-6; R f' and R f'' are independently selected from -Br, -Cl, -F, perfluoroalkyl radicals having from 1 to 10 carbon atoms, and chloroperfluoroalkyl radicals having from 1 to 10 carbon atoms; and X is selected from -F, -Cl, -Br, or mixtures thereof when n>1. Monomer (III) forms a pendant group having the following formula: Y-(CF₂) a' -(CFR f' ) b' -CFR f'' -O-[CF(CF₂X)CF₂-O-]n- Particularly preferred are monomers (III) where n is 0, and R f' and R f'' are each -F. Sulfonic fluoropolymers of the present invention can be produced by a variety of polymerization processes. The process used should be those that are known to result in high molecular weight sulfonic fluoropolymers. Care should be exercised to ensure good control of molecular weight distribution and equivalent weight distribution of the sulfonic fluoropolymer being produced. Exemplary of such a process is emulsion polymerization. Emulsion polymerization is a polymerization reaction carried out with the reactants in emulsified form. It is usually performed at normal pressure and at a temperature of from -20 to +100°C. There are two basic types of emulsion polymerization, continuous and batch. In continuous emulsion polymerization, the polymerization reaches a steady state that ensures a constant condition during the polymerization. The continuous process provides for the maintenance of conditions that lead to sulfonic fluoropolymers having consistent molecular weights, consistent equivalent weights and surprisingly good film properties. Batch emulsion polymerization processes are, in many cases, less costly and more convenient, especially for smaller scale production of sulfonic fluoropolymers. However, care should be taken to avoid excessive monomer conversion which can result in drift in sulfonic fluoropolymer composition (nonuniform molecular and equivalent weights). Batch emulsion polymerization reactions are usually performed by loading all of the fluorosulfonyl monomer reactant into a reactor and then maintaining a supply of the second reactant under constant pressure of the comonomer. In the present case, the comonomer is e.g. tetrafluoroethylene (TFE). Conversion of the fluorosulfonyl monomer into the sulfonic fluoropolymer beyond a conversion level of from 50 to 60 percent and particularly from 80 to 90 percent, can lead to higher equivalent weight sulfonic fluoropolymers being formed in the latter part of the reaction. If the comonomer pressure is allowed to trail too far downward during the reaction, sulfonic fluoropolymer fractions with lower molecular and lower equivalent weight can, and usually do, result. Naturally, the formation of lower equivalent weight sulfonic fluoropolymers is not desired, because, it is thought, that their presence leads to sulfonic fluoropolymers that have inferior film properties. Excessively long startup times for reaching constant temperature and pressure can also result in inconsistent molecular and equivalent weight sulfonic fluoropolymers. In general, it is thought to be best to ensure that as constant conditions as possible are maintained throughout the emulsion polymerization reaction. After polymerization, conversion of the fluorosulfonyl to an ionic form requires alkaline hydrolysis. The hydrolysis may be done in a variety of ways, but usually involves the use of caustic soda or potash in water, or a mixture of water and an organic solvent such as alcohols or dimethylsulfoxide. The sulfonic fluoropolymer may be converted to its ionic form by reacting it with 25 weight percent NaOH under the following conditions: (1) immerse the sulfonic fluoropolymer in about 25 weight percent sodium hydroxide for about 16 hours at a temperature of about 90°C; (2) rinse the sulfonic fluoropolymer twice in deionized water heated to about 90°C, using from 30 to 60 minutes per rinse. The pendant group is then in the -SO₃⁻Na⁺ form. Cations other than -Na⁺ can be made to replace the Na⁺ if practical (such as -H⁺). The fluoropolymers of the present invention can be laminated with other fluoropolymers to form laminated composite films. For example, they can be laminated with fluoropolymer films containing sulfonic or carboxylic ion exchange active groups. Such other films and lamination techniques are well known in the art. The fluoropolymers of the present invention can be used alone, or as a laminated structure with other fluoropolymers in electrolytic cells, such as chloralkali cells. In such cells, the membrane films are positioned between an anode and a cathode. They provide an ion permeable barrier between the electrodes. EXAMPLE 1 This example demonstrates the preparation of a sulfonic fluoropolymer having an equivalent weight (Eq. Wgt.) of about 717 and a Hydration Product (H.P.) of about 13,928. A 0.5 liter glass-lined reactor with titanium wetted parts kept under a gaseous pad of tetrafluoroethylene gas (TFE) is charged with about 250 milliliters (ml) of deionized, deoxygenated water, about 3 grams of ammonium perfluorooctanoate, about 1.5 grams of Na₂HPO₄·7H₂O, and about 1.0 gram of Na₂HPO₄·7H₂O. The reactor is equipped with internal titanium cooling coils, a turbine agitator, a platinum resistance temperature device, a magnetically coupled stirring device, a titanium dip tube, a gaseous monomer feed inlet, and a liquid jacket which is temperature controlled. Additive feed cylinders are attached to overhead lines. Gaseous monomers are fed through an integrating mass flow indicator to indicate and control their flow. After charging the above-described ingredients into the reactor, the jacket temperature controller which is a three-loop proportioning integrating derivative pressure controller, is set to control the temperature of the contents of the reactor at about 45°C. The upper, gas-filled portion of the reactor is evacuated to about 122 kPa and pressured to about 170 kPa with TFE, three times, leaving a vacuum the last time. After this, the agitator is started and set at about 800 revolutions per minute (rpm). The temperature of the reaction is allowed to stabilize at a temperature of about 45°C. Then about 50 grams of 2-fluorosulfonylperfluoroethyl vinyl ether is injected into the reactor. Thereafter, about 50 ml of deionized, deoxygenated water with about 0.1 gram of (NH₄)₂S₂O₈ (serving the purpose of an initiator or source of radicals) is injected using TFE pressure. Switching to bottom feed (i.e., injecting the TFE through an injection point at the bottom of the reactor rather than into the upper gaseous area), the TFE pressure is quickly raised to about 1135 kPa. The pressure is allowed to vary between 983 kPa and 1162 kPa as the TFE feed rate is set at about 0.7 percent of a 500 standard cubic centimeters per minute (sccm) flow control valve. As the pressure reached about 983 kPa, the TFE feed rate is raised to 42 percent of a 500 sccm flow control valve to bring the TFE pressure back to about 1135 kPa over a period of about 5 minutes. After a total of about 4 hours, the reactor is vented and the contents are acidified to coagulate the latex produced during the reaction by adding about 50 ml of about 6 normal HCl. The mixture is stirred. The coagulated sulfonic fluoropolymer is filtered and washed repeatedly with 2 reactor-volumes of water (about 600 ml, total) and then 2 reactor-volumes of anhydrous methanol (about 600 ml, total). The sulfonic fluoropolymer is vacuum dried overnight at about 26 inches Hg vacuum at about 110°C (658.7 torr, 87.7 kPa). The polymerization yielded about 19.1 grams sulfonic fluoropolymer at an equivalent weight of about 717 for a comonomer conversion of about 15 percent. The equivalent weight of the dried sulfonic fluoropolymer powder is determined by using a basic digestion bath with a difference titration of residual base when an excess is added. The dried sulfonic fluoropolymer powder is used in this procedure. About 2 grams of sulfonic fluoropolymer is weighed into a 250 ml TEFLON®-coated Erlenmeyer flask. A TEFLON®-covered stirring bar is added to the flask (TEFLON® is a trademark owned by E. I. Du Pont de Nemours and Company). Then about 20 ml of an about 1.0 weight percent solution of cetyltrimethylammonium bromide is added. Thereafter, about 100 ml of approximately 0.1 normal NaOH solution and about 50 ml of dimethylsulfoxide is added to the flask. The flask is then placed on a stirring hot plate with a condenser attached to the top of the flask through a stopper. The flask is positioned in an oil bath and the temperature of the contents of the flask is controlled to a temperature of about 80°C. The flask is left with stirring at 80°C for about 24 hours. The condenser is removed and rinsed with deionized water and the contents of the flask are allowed to cool to room temperature. The sulfonic fluoropolymer sample is then transferred to a beaker and the flask is rinsed thoroughly. The beaker contents are then titrated with approximately 0.1 normal HCl solution. The equivalent weight is then calculated using the following formula: Equivalent weight = {(wt. of dry sample*2000)/[meq. of base - (volume of 0.1N HCl/10)]} An about 3.02 gram sample of the sulfonic fluoropolymer is placed between 2 sheets of TEFLON® coated glass cloth and 2 chrome-plated brass photographic plates and then the sand which is put into the jaws of a hydraulic hot press at about 260°C for 2 minutes with the jaws barely closed on the plates. After about 2 minutes, the jaws are closed, causing them to exert about 8896 newtons (about 1 ton) applied force to the plates for about 2 minutes. The sheets are removed and peeled apart. The sulfonic fluoropolymer is then in the form of a disk about 0.2 mm thick and about 118 mm in diameter. The sulfonic fluoropolymer film is hydrolyzed in about 25 weight percent NaOH for about 16 hours at about 80°C to convert the functional groups to the -SO₃Na ionomer form. Then the film is placed in about 6 normal HCl for from 4 to 8 hours to convert it to the -SO₃H form. After this, the film is boiled in deionized water, then placed in a vacuum oven overnight at about 26 inches Hg vacuum and about 110°C (658.7 torr, 87.7 kPa). The dried film is removed from the oven and quickly weighed. It is found to have a mass of about 3.082 grams. The film is boiled in deionized water for about 30 minutes, removed and wiped dry quickly. It is then weighed. This was repeated a total of 3 times. The films were determined to gain an average of about 48.7 percent water absorption. The films were calculated to have a hydration product of about 13,928 and have about 19.4 moles water per functional group. The hydration product is calculated according to the following formula: [((wet weight-dry weight)/dry weight)*(Equivalent Weight/18)]*Equivalent Weight = Hydration Product The film is observed as having stiffness and elasticity in its hydrated form, which is qualitatively similar to polymers of the prior art in the region of 800 equivalent weight. The polymer exhibits viscous melt behavior (ease of pressing) characteristic of narrower molecular weight distributions. EXAMPLE 2 This example illustrates the preparation of a sulfonic fluoropolymer having an Eq. Wgt. of about 564 and a H.P. of about 114,229. An about 76 liter glass-lined reactor equipped with an anchor agitator, H-baffles, a platinum resistance temperature device and temperature control jacket, is charged with about 0.448 kg of ammonium perfluorooctanoate, about 0.339 kg of Na₂HPO₄·7H₂O, about 0.279 kg of Na₂HPO₄·7H₂O and about 0.179 kg of (NH₄)₂S₂O₈. The reactor is padded with nitrogen and then evacuated to about 0.4 inches H₂O (0.75 torr, 1.3 kPa). The jacket temperature control is set to bring the reactor contents to about 60°C, and the agitator is set to about 250 rpm. Water is fed into the reactor to a total charge of about 84,400 grams, with the final reactor pressure arriving at about 20.7 kPa. Heat is then applied on the jacket, and thus to the contents of the reactor. About 25.89 kg of 2-fluorosulfonylperfluoroethyl vinyl ether is then charged into the reactor. TFE gas is added to bring the pressure of the reactor up to about 929 kPa in about 20 minutes and the pressure is held constant until a total of about 20 kg of TFE gas had been fed into the reactor over a run time of about 2 hours and 56 minutes. TFE flow is then stopped and the pressure is bled down. A sample of the sulfonic fluoropolymer latex produced during the reaction is analyzed and found to contain about 24.66 percent solids and has a pH of about 2.45, at about 33°C. A portion of the sulfonic fluoropolymer latex produced during the reaction is transferred to an about 38 liter vessel where residual monomer is withdrawn by settling and vacuum. About 30.4 kg of the sulfonic fluoropolymer latex, after the residual monomer has been withdrawn, is treated with about 769 grams of H₂SO₄ (concentrated) with agitation at about 220 rpm. The temperature rises from 5°C to 10°C. About 17,958 grams of coagulated sulfonic fluoropolymer latex is removed from the vessel, and about 7,696 grams of deionized water is added to the vessel with continued agitation. After about 15 minutes, the agitator is stopped and about 9,000 grams of water is drained. About 9,000 grams of water is added and the process is repeated, removing about 13,242 grams of water, adding a like amount, then removing about 1,000 grams of water, then 168 grams of water. Finally, about 37.5 grams of about 50 weight percent NaOH is added to the vessel and the contents of the vessel, and it is agitated for about 5 minutes and then stopped. Washes are performed, totaling approximately 136 kg of water. Final conductivity of the wash water is found to be about 175 micro mhos (µS). The water is then drained away from the sulfonic fluoropolymer and the sulfonic fluoropolymer is allowed to dry on standing. The sample was titrated (as described in Example 1) to determine its equivalent weight. It was found to be about 564. An approximately 3.00 gram sample of this sulfonic fluoropolymer is placed in a hydraulic press between photographic plates and heated to about 260°C for about 2 minutes at no applied pressure. After about 2 minutes, the jaws of the press are partially closed, exerting a pressure of about 4500 newtons (0.5 ton force) and, after an additional 1 minute, the plates are removed and the sulfonic fluoropolymer, between 2 thin sheets of TEFLON® coated glass cloth, is in the form of a disc about 0.25 mm thick and about 95 mm in diameter. The film is hydrolyzed in about 25 weight percent NaOH for about 16 hours at about 80°C and then converted to the -SO₃H form by immersion for about 8 hours in about 6 normal HCl. The film is then washed in deionized water, boiled in deionized water, and then vacuum dried overnight at about 27 inches Hg vacuum at about 105°C (684 torr, 91.1 kPa). The film is found to have a mass of about 2.75 grams. The film is then placed in deionized water and boiled for about 30 minutes, removed, wiped dry and weighed as quickly as possible. The hydrated sulfonic fluoropolymer has a weight of about 20.5 grams. Using the weight gain, it has, thus, had a water absorption of 646 percent. This represents a hydration of about 202 moles H₂O per functional group. The hydration product for this sulfonic fluoropolymer is calculated to be about 114,229. This film still maintains its form despite being grossly extended. The film could be handled and unfolded from its wrinkled state. EXAMPLE 3 This example shows the preparation of a sulfonic fluoropolymer having an Eq. Wgt. of about 766 and a H.P. of about 24,064. A 76 liter glass-lined reactor equipped with an anchor agitator, H-baffle, a platinum resistance temperature device, and a temperature control jacket is charged with about 527 grams of ammonium perfluorooctanoate, about 398.4 grams of Na₂HPO₄·7H₂O, about 328.8 grams Na₂HPO₄·7H₂O, and about 210.8 grams of (NH₄)₂S₂O₈. The reactor is then evacuated down to about 0.0 atmosphere, as measured on the electronic pressure readout, and then an inert gas (nitrogen) is added to pressure up the reactor to a pressure of about 448 kPa. This is done a total of 4 times, then the reactor is evacuated one more time. About 99 liters of deoxygenated, deionized water is added, the agitator is started and heat is applied to the jacket. The agitator is set to about 250 rpm and then about 16.65 kg of 2-fluorosulfonyl perfluoroethyl vinyl ether is added. With the temperature at about 60°C, TFE gas is fed to the reactor at a rate of from 0.5 to 0.567 kg per minute until a pressure of about 1495 kPa is reached over a period of about 17 minutes. The feed continued for about another 10 minutes at which time feed is stopped and nitrogen is blown through the gas phase portion of the system and ambient temperature water is added to the jacket surrounding the reactor. A total of about 13.5 kilograms of TFE gas had been added to the reactor. The latex produced during the reaction is found to contain about 16.9 percent solids. The latex is transferred to a larger vessel for separation and stripping of residual monomer. A portion, about 14.5 kg, of the latex is added to a 38 liter vessel with agitation to about 110 rpm. Then about 0.92 kilograms of concentrated H₂SO₄ is added over a period of from 3 to 4 minutes. The contents temperature rose from 14°C to 18°C. The contents is then neutralized by adding about 1.0 normal NaOH. The coagulated sulfonic fluoropolymer is filtered away from the neutralized solution, centrifuged and washed repeatedly with water in the centrifuge. The wet cake weighed about 2054.2 grams. The cake is dried overnight in a rotary cone dryer at about 110°C under about 26 inches Hg vacuum (658.7 torr, 87.7 kPa) and about 1709.2 grams is recovered. The equivalent weight of the sulfonic fluoropolymer is determined according to the method described in Example 1 and was found to be about 766. About 3 grams of the sulfonic fluoropolymer is pressed into a film at about 260°C and about 8896 newtons (1 ton) force on a hydraulic hot press between sheets of TEFLON® covered glass cloth and brass photographic plates for about 2 minutes after preheating to 260°C for about 2 minutes at zero pressure. The film is hydrolyzed to the Na⁺ ionic form by placing it in about a 25 weight percent NaOH solution at about 80°C for about 16 hours. The film is then placed in about a 6 normal HCl bath for about 8 hours for conversion of the groups to the H⁺ form. The film is then boiled for about 30 minutes in deionized water and placed in a vacuum oven at about 110°C and about 26 inches Hg vacuum (658.7 torr, 87.7 kPa) overnight. The film is then quickly removed from the oven and weighed and found to weigh about 2.865 grams. The film is then placed in a beaker of deionized water and boiled for about 30 minutes, removed and wiped dry and weighed as quickly as possible. The film is found to weigh about 4.98 grams in its hydrated state. This is about 73.8 percent water absorption and the hydration product is therefore about 24064. The film is tough and fairly elastic and the quality of pressing into a film easily (under the conditions described above) indicates the polymer has a favorable molecular weight distribution. EXAMPLE 4 This example illustrates the preparation of a sulfonic fluoropolymer having an Eq. Wgt. of about 699 and a H.P. of about 21,886. A nominally 3.78 liter glass lined reactor equipped with an anchor agitator, a paddle baffle, a platinum resistance temperature device and a temperature control jacket is charged with about 25 grams ammonium perfluorooctanoate, about 18.9 grams Na₂HPO₄·7H₂O, about 15.6 grams ,and Na₂HPO₄·7H₂O about 3.0 grams of (NH₄)₂S₂O₈. The reactor is then evacuated down to about 0.0 atmosphere as measured on the electronic pressure readout and then inert gas (nitrogen) is added to pressure up the reactor to about 448 kPa. This is done a total of 4 times, then evacuated one more time. About 4,702 grams of deoxygenated, deionized water is added, the agitator is started and heat is applied to the jacket. The agitator is set to about 500 rpm and then about 778 grams of 2-fluorosulfonyl perfluoroethyl vinyl ether is added. With the temperature at about 60°C, TFE gas is fed to the reactor until a pressure of about 1789 kPa is reached over a period of about 5 minutes. The reaction continued for about 4 hours and 38 minutes. The feed is stopped and nitrogen is blown through the gas phase portion of the reactor and ambient-temperature water is added to the jacket. A total of about 870 grams of TFE gas has been added to the reactor. The latex produced during the reaction is found to contain about 23.8 percent solids. The latex is weighed and found to be weigh about 6386.4 grams after stripping of residual monomer. The latex is coagulated with about 6 normal HCl, filtered and washed repeatedly with water, then vacuum dried at about 110°C. The resulting sulfonic fluoropolymer powder is hydrolyzed and titrated (as described in Example 1) to determine the equivalent weight. The equivalent weight is found to be about 699. About 3 grams of the sulfonic fluoropolymer is pressed into a film at about 260°C and about 8896 newtons (1 ton) on a hydraulic hot press between sheets of TEFLON®-covered glass cloth and grass photographic plates for about 2 minutes, after preheating to 260°C at about 101 kPa (at 0.0 atmosphere). The film is then hydrolyzed to the Na⁺ ionic form by placing it in about a 25 weight percent NaOH solution at about 80°C for about 16 hours. The film is then placed in about a 6 normal HCl bath for about 8 hours for conversion of the groups to the H⁺ form. The film is then boiled for about 30 minutes in deionized water and placed in a vacuum oven at about 110°C and about 26 inches Hg vacuum (658.7 torr, 87.7 kPa) overnight. The film is then quickly removed from the oven and weighed and found to weigh about 2.5245 grams. The film is then placed in a beaker of deionized water and boiled for about 30 minutes, removed and wiped dry and weighed as quickly as possible. The film is found to weigh about 4.56 grams in its hydrated state. This is about 80.6 percent water absorption and the hydration product is therefore about 21886. The film is surprisingly tough and flexible even when totally dry. The hydrated film is not fragile, as other films of the prior art. The elasticity without softness is unusual for the low equivalent weight polymer. EXAMPLE 5 This example illustrates the preparation of a sulfonic fluoropolymer having an Eq. Wgt. of about 650 and a H.P. of about 22,256. A nominal 3.78 liter glass-lined reactor, equipped with an anchor agitator, a paddle baffle, a platinum resistance temperature device, and a temperature control jacket, is charged with about 25 grams ammonium perfluorooctanoate, about 18.9 grams Na₂HPO₄·7H₂O, about 15.6 grams Na₂HPO₄·7H₂O, and about 10.0 grams of (NH₄)₂S₂O₈. The reactor is then evacuated down to about 0.0 atmosphere as measured on the electronic pressure readout and then inert gas (nitrogen) is added to pressure up the reactor to about 448 kPa. This is done a total of four times, then evacuated one more time. About 4,702 grams of deoxygenated, deionized water is added, the agitator is started, and heat is applied to the jacket. The contents are heated to a temperature of about 60°C, while being stirred with the agitator set to about 500 rpm. Then about 787 grams of 2-fluorosulfonyl perfluoroethyl vinyl ether is added to the reactor. With the temperature at about 60°C, TFE gas is fed into the reactor over a period of about 5 minutes to reach a pressure of about 1425 kPa and that pressure is held for the reaction period of about 41 minutes. The TFE feed is stopped and nitrogen is blown through the gas phase portion of the reactor and ambient-temperature water is added to the jacket. A total of about 898 grams of TFE gas has been added to the reactor. The latex produced during the reaction is found to contain about 18.6 percent solids. The latex is weighed and found to be about 6169 grams after stripping of residual monomer. The latex is coagulated with about 6 normal acid, filtered, and washed repeatedly with water, then vacuum dried at about 110°C sulfonic fluoropolymer powder is hydrolyzed and titrated (as described in Example 1) to determine the equivalent weight of the sulfonic fluoropolymer. The equivalent weight is found to be about 650. About 3 grams of the sulfonic fluoropolymer is pressed into a film at about 260°C and about 8896 newtons (1 ton) on a hydraulic hot press between sheets of TEFLON®-covered glass cloth and brass photographic plates for about 2 minutes after being preheated to a temperature of about 260°C at about 101 kPa (0.0 atmosphere) pressure. The film is hydrolyzed to the Na⁺ ionic form by placing it in about a 25 weight percent NaOH solution at about 80°C for about 16 hours. The film is then placed in about a 6 normal HCl bath for about 8 hours for conversion of the groups to the H⁺ form. The film is then boiled for about 30 minutes in deionized water and placed in a vacuum oven at about 110°C and about 26 inches Hg vacuum (658.7 torr, 87.7 kPa) overnight. The film is then quickly removed from the oven and weighed and found to weigh about 2.9164 grams. The film is then placed in a beaker of deionized water and boiled for about 30 minutes, removed and wiped dry, and weighed as quickly as possible. The film is found to weigh about 5.68 grams in its hydrated state. This is about 94.8 percent water absorption and the hydration product is therefore about 22256. The polymer of this low equivalent weight pressed easily into a film that is tough and elastic at the 8896 newtons (1 ton) force level at 260°C. Upon hydrolysis and acidification, the film remained tough and flexible, even after hydration. EXAMPLE 6 This example illustrates the preparation of a sulfonic fluoropolymer having an Eq. Wgt. of about 675 and a H.P. of about 26,126. A nominal 3.78 liter glass-lined reactor equipped with an anchor agitator, paddle baffle, a platinum resistance temperature device, and a temperature control jacket is charged with about 25 grams ammonium perfluorooctanoate, about 18.9 grams Na₂HPO₄·7H₂O, about 15.6 grams Na₂HPO₄·7H₂O, and about 10.0 grams of (NH₄)₂S₂O₈. The reactor is then evacuated down to about 0.0 atmosphere as measured on the electronic pressure readout, and then inert gas (nitrogen) is added to pressure up the reactor to about 448 kPa. This is done a total of 4 times, then evacuated one more time. About 4,702 grams of deoxygenated, deionized water is added, the agitator is started and heat is applied to the jacket. The agitator is set to about 500 rpm and then about 789 grams of 2-fluorosulfonyl perfluoroethyl vinyl ether is added. With the temperature at about 60°C, TFE gas is fed to the reactor over a period of about 5 minutes to reach a pressure of about 1398 kPa, and that pressure is held for the reaction period of about 69 minutes. The feed is stopped and nitrogen is blown through the gas phase portion of the system and ambient-temperature water is added to the jacket. A total of about 898 grams of TFE gas has been added to the reactor. The latex produced during the reaction is found to contain about 18.4 percent solids. The latex is weighed and found to be about 6145.6 grams after stripping of residual monomer. The latex is coagulated with about 6 normal HCl, filtered and washed repeatedly with water, then vacuum dried at about 110°C. The sulfonic fluoropolymer powder produced thereby is hydrolyzed and titrated (as described in Example 1) to determine its equivalent weight. The equivalent weight is found to be about 675. About 3.2 grams of the sulfonic fluoropolymer is pressed into a film at about 260°C and about 8896 newtons (1 ton) is applied on a hydraulic hot press between sheets of TEFLON®-covered glass cloth and brass photographic plates for 2 minutes after preheating to a temperature of about 260°C, for about 2 minutes and pressed at 101 kPa (0.0 atmosphere) pressure. The film is hydrolyzed to the Na⁺ ionic form by placing it in about a 25 weight percent NaOH solution at about 80°C for about 16 hours. The film is then placed in about a 6 normal HCl bath for about 8 hours for conversion of the groups to the H⁺ form. The film is then boiled for about 30 minutes in deionized water and placed in a vacuum oven at about 110°C and about 26 inches Hg vacuum (658.7 torr, 87.7 kPa) overnight. The film is then quickly removed from the oven and weighed and found to weigh about 3.1370 grams. The film is then placed in a beaker of deionized water and boiled for about 30 minutes, removed and wiped dry and weighed as quickly as possible. The film is found to weigh about 6.3749 grams in its hydrated state. This is about 103.2 percent water absorption and the hydration product is therefore about 26126. The film is somewhat softer than the films at lower hydration products, i.e., it is less elastic in its response, and is a viable film with somewhat lower stiffness.

Claims: A sulfonic fluoropolymer having a fluoropolymer backbone having pendant groups attached thereto and represented by the general formula: ZSO₂-(CF₂) a -(CFR f ) b -O- where: Z is selected from a halogen, OM wherein M is an alkali metal, OH or OR; R is a branched or linear alkyl radical having from 1 to 10 carbon atoms or an aryl radical; a is 0-2; b is 0-2; provided a + b is not equal to 0; R f is selected from -F, -Cl, perfluoroalkyl radicals having from 1 to 10 carbon atoms and fluorochloroalkyl radicals having from 1 to 10 carbon atoms, wherein the sulfonic fluoropolymer has an equivalent weight of 766 or less, and a hydration product of less than 29,000 when Z is hydroxy. The sulfonic fluoropolymer of Claim 1, wherein the sulfonic fluoropolymer is a copolymer derived from monomers of general formulas (I) and (II): (I) CF₂=CZ'Z'' where: Z' and Z'' are independently selected from -H, -Cl, -F, or -CF₃, and (II) ZSO₂-(CF₂) a -(CFR f ) b -O-CF=CF₂ where: Z, R, a, b, and R f are defined as in Claim 1. The sulfonic fluoropolymer of Claim 2, wherein R f is F; and a + b is 2 or 3. The sulfonic fluoropolymer of Claim 3, wherein a + b is 2. The sulfonic fluoropolymer of Claim 2, including a third monomer represented by the general formula: (III) (Y-CF₂) a' -(CFR f' ) b' -CFR f'' -O-[CF(CF₂X)CF₂-O-] n -CF=CF₂ where: Y is selected from -F, -Cl or -Br; a' and b' are independently 0-3; n is 0-6; R f' and R f'' are independently selected from -Br, -Cl, -F, perfluoroalkyl radicals having from 1 to 10 carbon atoms, or chloroperfluoroalkyl radicals having from 1 to 10 carbon atoms; and X is selected from -F, -Cl, -Br, or mixtures thereof when n>1. The sulfonic fluoropolymer of any one of Claims 1 to 5, wherein the hydration product is from 29,000 to 15,000 when Z is OH, and the equivalent weight is from 766 to 575. A laminated composite film comprising as one layer the sulfonic fluoropolymer of any one of the preceding claims and as the other layer a fluoropolymer film having sulfonic ion exchange active groups or carboxylic ion exchange active groups.

Inventors: CARL WILLIAM P, EZZELL BOBBY R, CARL, WILLIAM P., EZZELL, BOBBY R.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1988
Main classification: C08F214
IPC codes: C08F2, C08J5, C08F214, B01D71, C08F14, B32B27