FERROELECTRIC LIQUID CRYSTAL COMPOSITION

Abstract: A ferroelectric liquid crystal composition and a photoswitching element prepared by using same are disclosed. This composition gives the element a quick response. The composition comprises at least one compound represented by general formula (I) (wherein R<1> and R<2> each represents an alkyl group containing 1 to 18 carbon atoms) and at least one optically active compound represented by general formula (II) (wherein R<3> represents an alkyl or alkoxy group containing 1 to 18 carbon atoms, R<4> represents an alkyl group containing 2 to 18 carbon atoms, X represents a single bond, -COO-, -OCO-, -N=CH-, -CH=N-, -OCH<2>- or -CH2O-, m and n each represents an integer of 1 or 2, and * represents an asymmetric carbon atom). The photo-switching element prepared by using the compositon shows a quick response.

Description: The present invention relates to a ferroelectric liquid crystal material. More specifically, it relates to a ferroelectric liquid crystal composition having quick response properties which comprises a smectic liquid crystal compound and an optically active compound, and an light switching element in which the above-mentioned composition is contained. Background Technique Liquid crystal compounds are widely used as materials for display elements, and most of these liquid crystal elements are based on TN type display system and liquid crystal materials are in the state of nematic phase. The TN type display system has advantages such as less tiredness of eyes and extremely small consumption of electric power because of non-emissive type, whereas it has disadvantages such as slow response and disappearance of display at certain visual angles. In recent years, this system is being improved in such a direction as to keep up characteristics of flat displays, and in particular, quick response and the enlargement of the visual angle are demanded. In order to meet these demands, improvements in liquid crystal materials have been attempted. However, as compared with other emissive type displays (e.g., electroluminescence displays and plasma displays), it is apparent that the TN type display system is much poorer in points of the response time and the extent of the visual angle. In order that characteristics of the liquid display element such as features of the non-emissive type and the small consumption of electric power may be maintained and in order that the quick response corresponding to that of the emissive type displays may be assured, it is essential to develop a novel liquid display system in place of the TN type display system. As one of such attempts, a display system in which the light switching phenomenon of ferroelectric liquid crystals is utilized has been suggested by N.A. Clark and S.T. Lagerwall (see Appl. Phys. Lett. 36 , p 899, 1980). The presence of the ferroelectric liquid crystals has been announced for the first time in 1975 by R.B. Mayer et al. (see J. Phys., 36 , p 69, 1975), and from the viewpoint of a liquid crystal structure, these crystals belong to a chiral smectic C phase, a chiral smectic I phase, a chiral smectic F phase, a chiral smectic G phase and a chiral smectic II phase (hereinafter referred to simply as "S C * phase", "S I * phase", "S F * phase", "S G * phase" and "S H * phase", respectively). In the chiral smectic phase, molecules form a layer and tilt to the surface of the layer, and a helical axis is vertical to this layer surface. In the chiral smectic phase, spontaneous polarization takes place, and therefore, when DC electric field is applied to this layer in parallel therewith, the molecules turn round the helical axis in accordance with its polarity. Display elements containing the ferroelectric liquid crystals utilize this switching phenomenon. Nowadays, of the chiral smectic phases, much attention is particularly paid to the S c * phase. As the display systems in which switching phenomenon of the S c * phase is utilized, there are a birefringence type system using two polarizers and a guest/host type system using a dichoric dye. Features of these display systems are as follows: (1) The response is very quick. (2) Memory properties are present. (3) Display performance is not so affected by the visual angle. Thus, the display systems have the possibility of achieving the high-density display and is considered to be effectively utilizable in the display elements. However, in the case that this ferroelectric liquid crystal is used in the practical display elements, there are now many problems such as slow response properties and very difficult alignment. Therefore, requirements which are necessary for the ferroelectric liquid crystal material are (1) further improvement in the response properties, (2) the exhibition of the S c * phase in a wide temperature range inclusive of room temperatures. and (3) improvement in alignment. At present, any chiral smectic liquid crystal compounds in a single state which satisfy all of such requirements are not present, and thus one attempt is to provide a ferroelectric liquid crystal composition satisfying the above-mentioned requirements by mixing several chiral smectic liquid crystal compounds or several non-liquid crystal compounds which can meet a part of the above-mentioned requirements. In addition to the ferroelectric liquid crystal compositions each comprising the ferroelectric liquid crystal compound alone, Japanese Patent Laid-open Publication No. 195,187/1986 discloses a ferroelectric liquid crystal composition which can be prepared by mixing one or more compounds assuming a ferroelectric liquid crystal phase with fundamental materials of compounds and compositions assuming achiral smectic C, F, G, H and I phases (hereinafter referred to simply as "S c and other phases"). Furthermore, another ferroelectric liquid crystal composition is also reported in which one or more compounds having optical activity but not assuming any ferroelectric liquid crystal phase are mixed with fundamental materials of compounds and compositions assuming the S c and other phases (Mol. Cryst. Liq. Cryst., 89 , p 327, 1982). The above-mentioned smectic liquid crystal mixture which comprises the fundamental material assuming at least one of the achiral S c and other phases and which has at least one of the S c and other phases will be hereinafter referred to as the base Sm mixture. The preferable base Sm mixture is a liquid crystal mixture assuming the S c phase in an extensive temperature range inclusive of room temperatures. Components for the base Sm mixture are suitably selected from liquid crystal compounds such as phenylbenzole series, Schiff base series, phenylpyridine series and 5-alkyl-2-(4-alkoxyphenyl)pyridine. For example, in Japanese Patent Laid-open Publication No. 291 ,679/1986 and the pamphlet of PCT International publication W086/06401, the ferroelectric liquid crystal prepared by mixing 5-alkyl-2-(4-alkoxyphenyl)pyrimidine with an optically active compound can assume the S C * phase in a wide temperature range inclusive of room temperatures. In the former publication, it is also described that when an light switching element is prepared by the use the ferroelectric smectic liquid crystal material in which the above-mentioned pyrimidine derivative is used as the base Sm mixture, the thus prepared switching element has a shortened response time. Furthermore, in Japanese Patent Laid-open Publication No. 291 ,679/1986, it is disclosed that the ferroelectric liquid crystal material comprising 5-alkyl-2-(4′-alkylbiphenylyl-4)pyrimidine, 5-alkyl-2-(4-alkoxyphenyl)-pyrimidine and an optically active compound also assumes the S C * phase in an extensive temperature range including room temperatures, and that it is effective for the improvement in the response time. Nevertheless, the improvement in the response properties at room temperatures is further demanded. A first object of the present invention is to provide a ferroelectric liquid crystal composition having quick response properties, and a second object thereof is to provide a switching element containing the liquid crystal composition which has quick response properties. Disclosure of the Invention A ferroelectric liquid crystal composition which is a first feature of the present invention is comprising at least one of achiral compounds represented by the formula (I) wherein each of R¹ and R² is an alkyl group having 1 to 18 carbon atoms, and at least one of optically active compounds represented by the general formula (II) wherein R³ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, R⁴ is an alkyl group having 2 to 18 carbon atoms, X is a single bond, -COO-, -OCO-, -N = CH-, -CH = N-, -OCH₂- or - CH₂O -, each of m and n is an integer of 1 or 2, and the symbol * is an asymmetric carbon atom, and it is preferred that the amount of the compound represented by the formula (I) is from 20 to 98% by weight, and that of the compound represented by the formula (II) is from 1 to 40% by weight. Furthermore, another ferroelectric liquid crystal composition of the present invention is comprising a blend of the achiral compound represented by the formula (I) and the optically active compound represented by the formula (II) with a compound represented by the formula (III) wherein each of represents or , R⁵ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, Y is a single bond, -CH₂O- or -OCH₂-, p is an integer of 0 or 1, and 7 is an alkyl group having 1 to 18 carbon atoms or -C*H(CH₃)-O-R⁶ wherein R⁶ is an alkyl group having 1 to 18 carbon atoms and the symbol * represents an asymmetric carbon atom, and it is preferred that the amount of the compound represented by the formula (I) is from 20 to 98% by weight, that of the compound represented by the formula (II) is from 1 to 40% by weight, and that of the compound represented by the formula (III) is from 1 to 40% by weight. A second invention of the present invention is directed to an light switching element containing a ferroelectric liquid crystal composition which contains at least one kind of achiral compounds represented by the formula (I) and at least one kind of optically active compounds represented by the formula (II). Another embodiment of the present case is directed to an light switching element which contains a compound represented by the formula (I), a compound represented by the formula (II) and a compound represented by the formula (III). Examples of the optically active compounds represented by the formula (II) of the present invention include compounds having the following formulae wherein R³ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, and R⁴ is an alkyl group having 2 to 18 carbon atoms. Typical preferable examples of the optically active compounds represented by the formula (II) include which are disclosed in Japanese Patent Laid-open Publication No. 118744/1984 and Ferroelectrics, 58 , 21 (1984). In addition, similar compounds are described in Japanese Patent Laid-open No. 149547/1985. The optically active compounds represented by the formula (III) of the present invention include compounds represented by the following formulae wherein R⁵ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, and R⁶ is an alkyl group having 1 to 18 carbon atoms. Typical examples of the optically active compounds represented by the formula (III) are as follows: (Japanese Patent Application No. 133269/1986) (Japanese Patent Application No. 49796/1987) (Japanese Patent Application No. 220824/1987) (Japanese Patent Application No. 103977/1987) (Japanese Patent Application No. 25234/1987) (Japanese Patent Application No. 133269/1986) (Japanese Patent Application No. 49796/1987) (Japanese Patent Application No. 220824/1987) (Japanese Patent Application No. 103977/1987) (Japanese patent Application No. 25234/1987) and 4′-heptyl-4-[4-{2-(butanoyloxy)-propoxy}-phenoxymethyl]-biphenyl and 4′-nonyl-4-[4-{2-(pentanoyloxy)-propoxy}-phenoxymethyl]-biphenyl. Moreover, other compounds can be added to the liquid crystal composition of the present invention, so long as they do not disturb the accomplishment of the objects of the present invention. As the achiral compound represented by the formula (I) of the present invention, a material having a smectic C phase is particularly preferable, but a material which does not exhibit the smectic C phase can also be used, though its amount is limited to such a range that a temperature range of the S c phase is not particularly reduced. Main compounds of such a kind are exemplified in Table 1. The compounds (I) shown in Table 1 are represented by the formula (I) wherein R¹ = n-C x H 2x + 1 and R² = n-C y H 2y + 1 . With regard to phase states, Cr indicates a crystal state, S₃ an unknown smectic phase, S c a smectic C phase, S A a smectic A phase, N a nematic phase, and I SO an isotropic liquid phase. The symbols .17 and - indicate the presence and the lack of each phase, respectively. The compound represented by the formula (I) in the liquid crystal composition of the present invention can be prepared by the following manufacturing process A. Manufacturing Process A wherein R is an alkyl group such as methyl or ethyl, and X is an elimination group such as chlorine, bromine, iodine, a p-toluenesulfonyloxy group, a benzenesulfonyloxy group or a methanesulfonyl group. That is, p-alkylbenzamidine hydrochloride (1) is reacted with methoxymalonic diester in the presence of a sodium alcoholate in order to form a diol (2), and the latter is then halogenated (3) with a halogenating agent such as phosphorus oxychloride. Afterward, dehalogenation is carried out in the presence of a base to form a dehalogenated compound (4), and the latter is then thermally treated in diethylene glycol in the presence of an alkali to obtain a compound (5). Furthermore, the latter compound is then subjected to etherification in order to prepare the desired compound (I). Alternatively, the compound of the formula (I) may be also prepared by the following manufacturing process B. Manufacturing Process B That is, a compound (6) described in Collection Czechoslov. Chem. Commun., 38 , p 1168 (1973) is reacted with p-alkylbenzamidine hydrochloride (1) in the presence of a sodium alcoholate in order to form a compound (7), and the latter is then subjected to an alkali treatment to obtain a compound (5). The subsequent procedure is made in the same manner as in the above-mentioned manufacturing process A. The p-alkylbenzamidine hydrochloride which is the starting material is easily available and can be prepared from a p-alkylbenzonitrile by a known process. The ferroelectric liquid crystal composition of the present invention has very excellent quick response properties, and when this composition is used, switching elements having quick response properties can be provided. Brief Description of the Drawing Fig. 1 shows a phase in the case that a composition A in Example 1 is mixed with a compound represented by the formula (a). Preferred Embodiments to Practice the Invention The present invention will be described in detail in reference to examples, but it should not be limited to these examples. Example 1 A composition A comprising the following components represented by the formula (I) was prepared, and its physical properties were then measured. Components: The phase transition temperature of the composition A was Fig. 1 shows a phase in the case that the composition A was mixed with a compound represented by the formula (II) As exhibited in Fig. 1, an S I * phase appears on a lower temperature side of an S C * phase when the concentration of the compound (a) is 40% or more. In order that the S C * phase is caused to appear at room temperatures, it is desirable that the concentration of the compound (a) is less than 40% or less. Additionally, at various concentrations of the materials, response times (τ/µs) at 25 ° C and spontaneous polarization values (Ps/nCcm⁻²) are as follows: As described above, when the achiral compound represented by the formula (I) is mixed with the optically active compound represented by the formula (II), the ferroelectric liquid crystal composition can be obtained which has the high upper limit temperature of the S C * phase and very excellent response properties. Here, the phase transition temperature was measured from the observation of texture by means of DSC and a polarizing microscope. The response time was measured as follows: A liquid crystal element was first put between two polarizing plates perpendicular to each other, and a rectangular wave of ± 10 V/µm and 1 KHz was then applied thereto, so that the strength of trasmitted light changed. The response time was determined by this change. Furthermore, the spontaneous polarization values were measured in accordance with the Sowyer-Tower method. In the undermentioned examples, there were shown values under the same conditions. Example 2 A composition B was prepared by blending the composi-tion A with the following compounds represented by the formula (III), and its physical properties were then measured. Components: A phase transition temperature of the composition B was Furthermore, a response time at 25° C was 28 microseconds. In view of the fact that most of the conventional known ferroelectric liquid crystal compositions have a response time of 100 microseconds, it is definite that the ferroelectric liquid crystal composition of the present invention has very quick response properties. Example 3 A composition C was prepared from the following components represented by the formulae (I) and (II), and its physical properties were measured. Components: The phase transition temperature of the composition C was In the composition C, a response time (τ) at 25° C was 43 microseconds, a spontaneous polarization value (Ps) was 19.2 nCcm⁻² , and a tilt angle was 22.5°. Example 4 A composition D having the following components was prepared from the compounds represented by the formulae (I) and (II), and its physical properties were measured Components: The phase transition temperature of the composition D was In the composition D, a response time (τ) at 25° C was 45 microseconds, a spontaneous polarization value (Ps) was 15.0 nCcm⁻², and a tilt angle was 20.9°. Example 5 A composition E was prepared from the following components represented by the formulae (I) and (II), and its physical properties were then measured. Components: The phase transition temperature of the composition E was In the composition E, a response time (τ) at 25° C was 41 microseconds, a spontaneous polarization value was 14.0 nCcm⁻², and a tilt was 20.8 °. Example 6 A composition F comprising the following components represented by the formulae (I), (II) and (III) was prepared, and its physical properties were then measured. Components: The phase transition temperature of the composition F was In the composition F, a response time (τ) at 25° C was 23 microseconds, a spontaneous polarization value was 57.1 nCcm⁻², and a tilt angle was 20°. Example 7 A composition G comprising the following components represented by the formulae (I), (II) and (III) was prepared, and its physical properties were then measured. Components: The phase transition temperature of the composition G was In the composition G, a response time (τ) at 25° C was 33 microseconds, a spontaneous polarization value was 87.5 nCcm⁻², and a tilt angle was 23.7°, and a response time (τ) at 30° C was 28 microseconds, a spontaneous polarization value was 81.4 nCcm⁻², and a tilt angle was 23.6°. Example 8 A composition H comprising the following components represented by the formulae (I), (II) and (III) was prepared, and its physical properties were then measured. Components: The phase transition temperature of the composition H was In the composition H, a response time (τ) at 25° C was 25 microseconds, a spontaneous polarization value was 59.9 nCcm⁻², and a tilt angle was 22.1°. Example 9 A composition I comprising the following components represented by the formulae (I), (II) and (III) was prepared, and its physical properties were then measured. Components: The phase transition temperature of the composition I was In the composition I, a response time (τ) at 25° C was 24 microseconds, a spontaneous polarization value was 66.9 nCcm⁻², and a tilt angle was 22.1°. Example 10 A composition J comprising the following components represented by the formulae (I), (II) and (III) was prepared, and its physical properties were then measured. Components: The phase transition temperature of the composition J was In the composition J, a response time (τ) at 25° C was 24 microseconds, a spontaneous polarization value was 57.0 nCcm⁻², and a tilt angle was 22.3 °. Possibility of Industrial Utilization The composition of the present invention can exhibit an S C * phase in an extensive temperature range inclusive of room temperatures and has quick response properties, and therefore it can solve the problem of conventional liquid crystal elements which has been outstanding for a long time. Moreover, by the use of this liquid crystal composition, switching elements having quick response properties can be obtained.

Claims: A ferroelectric liquid crystal composition comprising at least one of achiral compounds represented by the formula (I) wherein each of R¹ and R² is an alkyl group having 1 to 18 carbon atoms, and at least one of optically active compounds represented by the formula (II) wherein R³ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, R⁴ is an alkyl group having 2 to 18 carbon atoms, X is a single bond, -COO-, -OCO-, -N = CH-, -CH = N-, -OCH₂- or -CH₂O-, each of m and n is an integer of 1 or 2, and the symbol * is an asymmetric carbon atom. A ferroelectric liquid crystal composition according to Claim 1 wherein the proportion of the compound represented by the formula (I) is from 20 to 98% by weight, and that of the compound represented by the formula (II) is from 1 to 40% by weight. A ferroelectric liquid crystal composition according to Claim 1 wherein the compound represented by the formula (I) comprises at least one of compounds in the cases of R¹ = n-CxH 2x + 1 and R² = n-C y H 2y + 1 wherein when x = 6, y = 6 to 15, when x = 7, y = 5 to 12, when x = 8, y = 3 to 13, when x = 9, y = 2 or 6 to 13, or when x = 10, y = 5 to 12. A ferroelectric liquid crystal composition according to Claim 1 wherein the compound represented by the formula (II) comprises at least one of compounds represented by the formulae wherein R³ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, and R⁴ is an alkyl group having 2 to 18 carbon atoms, A ferroelectric liquid crystal composition according to Claim 1 which comprises, in addition to at least one of the compounds represented by the formula (I) and at least one of the compounds represented by the formula (II), at least one compound represented by the formula (III) wherein each of represents or , R⁵ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, Y is a single bond, c-CH₂O- or -OCH₂-, p is an integer of 0 or 1, and Z is an alkyl group having 1 to 18 carbon atoms or -C*H(CH₃)-O-R⁶ wherein R⁶ is an alkyl group having 1 to 18 carbon atoms and the symbol * represents an asymmetric carbon atom. A ferroelectric liquid crystal composition according to Claim 5 wherein the compound represented by the formula (III) comprises at least one of compounds represented by the formulae wherein R⁵ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, and R⁶ is an alkyl group having 1 to 18 carbon atoms. A ferroelectric liquid crystal composition according to Claim 5 wherein the compound represented by the formula (III) comprises at least one of or 4′-heptyl-4-[4-{2-(butanoyloxy)-propoxy}-phenoxymethyl]-biphenyl or 4′-nonyl-4-[4-{2-(pentanoyloxy)-propoxy}-phenoxymethyl]-biphenyl. An light switching element containing a ferroelectric liquid crystal composition which comprises at least one of achiral compounds represented by a formula (I) wherein each of R¹ and R² is an alkyl group having 1 to 18 carbon atoms, and at least one of optically active compounds represented by the formula (II) wherein R³ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, R⁴ is an alkyl group having 2 to 18 carbon atoms, X is a single bond, -COO-, -OCO-, -N = CH-, -CH = N-, -OCH₂- or -CH₂O-, each of m and n is an integer of 1 or 2, and the symbol * is an asymmetric carbon atom. An light switching element according to Claim 7 which contains a ferroelectric liquid crystal composition comprising , in addition to at least one of the compounds represented by the formula (I) and at least one of the compounds represented by the formula (II), a compound represented by the formula (III) wherein each of represents or , R⁵ is an alkyl group or an alkoxy group having 1 to 18 carbon atoms, Y is a single bond, - CH₂O - or - OCH₂-, p is an integer of 0 or 1, and Z is an alkyl group having 1 to 18 carbon atoms or - C*H(CH₃)-O- R⁶ wherein R⁶ is an alkyl group having 1 to 18 carbon atoms and the symbol * represents an asymmetric carbon atom.

Inventors: FURUKAWA, KENJI, ICHIHASHI, MITSUYOSHI, KIKUCHI, MAKOTO, TAKESHITA, FUSAYUKI, TERASHIMA, KANETSUGU
Applicants: CHISSO CORPORATION
Application year: 1988
Main classification: C09K19
IPC codes: C09K19, G02F1