Adhesive resin compositions and laminates utilizing same

Abstract: The invention provides an adhesive resin composition comprising (A) 95-50% by weight of an ethylene/α-olefin copolymer having a density of 0.850-0.900 g/cm³, and an ethylene content of 75-95% mol%. (B) 5-50% by weight of a copolymer of ethylene and a radical polymerizable polar unsaturated monomer, said copolymer having a content of the radical polymerizable polar unsaurated monomer of 5-40% by weight, and (C) 1.0-30 parts by weight, based on 100 parts by weight of the sum of the above-mentioned (A) + (B), of a graft-modified polyethylene, wherein a part or whole of a polyethylene has been graft-modified with an unsaturated carboxylic acid or derivative thereof and a laminate using this adhesive resin composition.

Description: This invention relates to adhesive resin compositions and laminates utilizing the same and more particularly to such adhesive resin compositions as will not decrease in adhesive strength even when they come into contact with hot water and laminates utilizing the same, which have excellent gas and moisture barrier properties and can be used as food packaging materials resistant to heat sterilization in a retort (retort treatment). Polyolefins particularly such as polypropylene are excellent in heat-sealing properties, mechanical strength and water resistance, lightweight, nontoxic, tasteless and odorless and, moreover, have heat resisting properties capable of withstanding the retort treatment. Utilizing such properties as mentioned above, polyolefins particularly such as polypropylene are widely used as packaging materials such as food packaging films, cups and bottles. However, polyolefins such as polypropylene are relatively high in permeability to gases such as oxygen and carbon dioxide, and are somewhat poor in oil resistance and grease resistance, and cannot be used alone in packaging perishable food such as fish meat, edible meat or processed products thereof, food rich in fats and oils, and the like food. In order to solve such problems as mentioned above, there has been proposed to laminate polyolefins particularly such as polypropylene with polyvinylidene chlorides or saponification products of ethylene/vinyl acetate copolymer, both of which are of excellent gas barrier and oil resistance properties. Particularly, polyvinylidene chlorides are suitable as materials for gas barrier layers of food packaging containers which require the retort treatment, because polyvinylidene chlorides are low in hydroscopicity and exhibit no decrease in gas barrier properties when used as the gas barrier layers. However, the existing circumstances were such that because polyolefins such as polypropylene have no polar groups, even when a polyolefin layer is directly laminated with a layer of polyvinylidene chloride or saponification product of ethylene/vinyl acetate copolymer, the resulting lamination layers are very low in adhesion therebetween and the laminate thus obtained is of little practical use. As procedures for improving adhesion between a polypropylene layer and a polyvinylidene chloride layer, there have heretofore been proposed a process in which a modified polypropylene grafted with an unsaturated carboxylic acid or its derivative is used for forming a polypropylene layer (JP-A-57,014,970) and a process in which a resin comprising a mixture of a low crystalline ethylene/α-olefin copolymer and an ethylene/vinyl acetate copolymer, at least one of which has been graft-modified with an unsaturated carboxylic acid or its derivative, is used to form an adhesive layer to be interposed between the polypropylene layer and polyvinylidene chloride layer (JP-A-55,013,718). In these processes as referred to above, adhesion between the layers after the retort treatment or such high temperature treatment as high temperature filling markedly decreases, though the initial adhesion between the layers is high. Further, polyethylene terephthalate resin is excellent in mechanical strength, rigidity, heat resistance, chemical resistance, oil resistance, transparency, etc., and widely used as packaging materials such as films, sheets, containers, etc., by utilizing these characteristics as mentioned above. However, because of its not so low permeability to gases such as oxygen, etc., such it could not be used as packaging materials for products such as food, chemicals, cosmetics and the like for which high gas barrier properties of the packaging materials are strictly required. Furthermore, because of its not so lows permeability to gases such as oxygen, etc., polycarbonate resins could not be used as packaging materials particularly for such products as food and the like for which high gas barrier properties of the packaging materials are strictly required, though the polycarbonate resins are excellent in transparency, heat resistance, perfume barrier properties, etc., similarly to the polyester resins. In order to improve gas barrier properties of the polyethylene terephthalate resins or polycarbonate resins, there has been proposed a procedure wherein the polyethylene terephthalate resins or polycarbonate resins are laminated with a resin which is superior in gas barrier properties to these resins, for example, saponification products of ethylene/vinyl acetate copolymers. In the proposed procedure, however, adhesion between the polyethylene terephthalate or polycarbonate resins and the ethylene/vinyl acetate copolymer saponification products is not always sufficient, and in some cases parts of the lamination layers peel off from each other at the time of lamination or use thereof, gas barrier properties of the laminate obtained decreases, or the lamination products prepared therefrom are marred in appearance or deteriorate in mechanical strength. JP-A-61,270,155 and JP-A-62,158,043 disclose laminates which are obtained by joining polycarbonate or polyester layers to layers of saponification products of ethylene/vinyl acetate copolymers by the use as an intermediate adhesive layer of graft-modified ethylene/α-olefin copolymers graft-modified with unsaturated carboxylic acids or derivatives thereof. The disclosed laminates have excellent gas barrier properties and the layers of the laminate adhere strongly each other at ordinary temperature, However, when these laminates are subjected to heat treatment such as high temperature filling or retort treatment, adhesive strength between layers of the laminates sometimes decreases after such treatments, and on that account those layers peel off from each other and gas barrier properties of the laminates decreases. The invention seeks to provide adhesive resin compositions which do not substantially lose adhesive strength even when subjected to such severe treatment as high temperature filling or retort treatment. The invention also provides laminates comprising the adhesive resin composition, said laminates having excellent gas barrier properties, moisture barrier properties and resistance to delamination after being subjected to high temperatures. According to the invention there is provided an adhesive resin composition comprising (A) 95-50% by weight of an ethylene/α-olefin copolymer having a density of 0.850-0.900 g/cm³, an ethylene content of 75-95 mol% and a crystallinity index as measured by X-ray of less than 30%, (B) 5-50% by weight of a copolymer of ethylene and a radical polymerizable polar unsaturated monomer, said copolymer having a content of the radical polymerizable polar unsaturated monomer of 5-40% by weight, and (C) 1.0-30 parts by weight, based on 100 parts by weight of the sum of the above-mentioned (A) + (B), of a graft-modified polyethylene having a density of 0.900 to 0.980 g/cm³ and a crystallinity index as measured by X-ray of at least 30%, wherein a part or whole of a polyethylene has been graft-modified with an unsaturated carboxylic acid or derivative thereof. The adhesive resin compositions of the present invention are particularly useful for joining (i) a polyolefin layer to a polyvinylidene chloride layer, (ii) a polyester layer to an olefin/vinyl acetate copolymer saponification product layer, and (iii) a polycarbonate layer to an olefin/vinyl acetate copolymer saponification product layer. Thus, a first laminate of the invention comprises a polyolefin layer and a polyvinylidene chloride layer laminated through an intermediate layer comprising an adhesive resin composition of the invention. A second laminate of the invention comprises a polyester layer and an olefin/vinyl acetate copolymer saponification product layer laminated through an intermediate layer comprising an adhesive resin composition of the invention. A third laminate of the invention comprises a polycarbonate layer and an olefin/vinyl acetate copolymer saponification product layer laminated through an intermediate layer comprising an adhesive resin composition of the invention. The adhesive resin compositions of the present invention and laminates using the same are illustrated below in detail. First, the adhesive resin compositions of the present invention comprise (A) an ethylene/α-olefin copolymer, (B) a copolymer of ethylene and a radical polymerizable polar unsaturated monomer, and (C) a graft-modified polyethylene. Each of the above-mentioned components is described hereinafter in detail. (A) Ethylene/α-olefin copolymer This ethylene/α-olefin copolymer is a random copolymer of ethylene and α-olefin, and has the following characteristics. Melt flow rate (ASDM D 1238 E): preferably 0.1-50 g/10 min, more preferably 0.3-30 g/10 min Density : 0.850-0.900 g/cm³ preferably 0.850-0.890 g/cm³ Ethylene content: 75-95 mol%, preferably 75-90 mol% Crystallinity index as measured by X-ray: less than 30%, preferably less than 25% Method for measuring crystallinity index by X-ray: (i) Preparation of sample A sample of a sheet of a 1 mm thick is prepared by pressing the obtained product at 200 °C, followed by quenching while pressing the pressed sample at 30°C. (ii) Measurement by X-ray A ratio of the crystallized portion to the non-crystallized portion is calculated by diffraction pattern of a wide angle X-ray (target: Cu). If the copolymer used is found to be beyond the ranges of the above-mentioned characteristics, the resulting adhesive resin composition undesirably decreases in adhesive power. The α-olefin used as one of the components of this ethylene/α-olefin copolymer has 3-20 carbon atoms and includes, for example, propylene, 1-butene, 1-hexane, 4-methy-1-pentene, 1-octene, 1-decene, 1-tetradecene and 1-octadecene, and these α-olefins may be used either singly or in mixtures of two or more. The ethylene/α-olefin copolymer usually has a melting point (ASTM D3418) of less than 100°C. The ethylene/α-olefin copolymer is used in an amount of 95-50% by weight, preferably 90-60% by weight, based on the total weight of this copolymer and (B) an ethylene/vinyl acetate copolymer as will be mentioned later. (B) Copolymer of ethylene and a radical polymerizable polar unsaturated monomer This random copolymer of ethylene and a radical polymerizable polar unsaturated monomer includes, for example, (i) ethylene/vinyl acetate copolymers [EVA], (ii) ethylene/ethyl acrylate copolymers [EEA], (iii) ethylene/methyl acrylate copolymers [EMA], (iv) ethylene/acrylic acid copolymers [EAA] and (v) ethylene/methacrylic acid copolymers [EMAA]. Preferred copolymers are (i) ethylene/vinyl acetate copolymers, (ii) ethylene/ethyl acrylate copolymers and (iii) ethylene/methyl acrylate copolymers, and particularly preferred are (i) ethylene/vinyl acetate copolymers. (i) Ethylene/vinyl acetate copolymers Vinyl acetate content: 5-40% by weight, preferably 10-35% by weight This ethylene/vinyl acetate copolymer is used in an amount of 5-50% by weight, preferably 10-40% by weight based on the total weight of this copolymer and the above-mentioned (A) an ethylene/α-olefin copolymer. (ii) Ethylene/ethyl acrylate copolymers Ethyl acrylate content: 5-40% by weight, preferably 10-35% by weight This ethylene/ethyl acrylate copolymer is used in an amount of 5-50% by weight, preferably 10-40% by weight based on the total weight of this copolymer and the above-mentioned (A) an ethylene/α-olefin copolymer. (iii) Ethylene/methyl acrylate copolymers Methyl acrylate content: 5-40% by weight, preferably 10-35% by weight This ethylene/methyl acrylate copolymer is used in an amount of 5-50% by weight, preferably 10-40% by weight based on the total weight of this copolymer and the above-mentioned (A) an ethylene/α-olefin copolymer. (iv) Ethylene/acrylic acid copolymers Acrylic acid content: 5-40% by weight, preferably 5-30% by weight, and more preferably 8-25% by weight This ethylene/acrylic acid copolymer is used in an amount of 5-50% by weight, preferably 10-40% by weight based on the total weight of this copolymer and the above-mentioned (A) an ethylene/α-olefin copolymer. (v) Ethylene/methacrylic acid copolymer Methacrylic acid content: 5-40% by weight, preferably 5-25% by weight, and more preferably 7-20% by weight This ethylene/methacrylic acid copolymer is used in an amount of 5-50% by weight, preferably 10-40% by weight based on the total weight of this copolymer and the above-mentioned (A) an ethylene/α-olefin copolymer. (C) Graft-modified polyethylene This graft-modified polyethylene has the following characteristics. Amount of unsaturated carboxylic acid or its derivative: preferably 0.05-15% by weight, more preferably 0.1-10% by weight Melt flow rate: preferably 0.1-50 g/10 min, more preferably 0.3-30 g/10 min Density: 0.900-0.980 g/cm³, preferably 0.905-0.970 g/cm³ Crystallinity index as measured by X-ray: at least 30%, preferably 35-75% In this graft-modified polyethylene, a part or whole of polyethylene has been graft-modified. Under certain circumstances, the graft-modified polyethylene may be a graft-modified ethylene/α-olefin copolymer of ethylene and at least one α-olefin, for example propylene, 1-butene, 4-methyl-1-pentene, 1-hexene, 1-octene or 1-decene, in small amounts, for example, up to 5 mol%, at least a part or whole of which has been graft-modified. Such graft-modified polyethylene may be obtained by graft-modifying a part or whole of polyethylene or an ethylene/α-olefin copolymer with an unsaturated carboxylic acid or its derivative. The unsaturated carboxylic acid may be, for example, acrylic acid, maleic acid, fumaric acid, tetrahydrophthalic acid, itaconic acid, citraconic acid, crotonic acid, isocrotonic acid and nadic acid® (endocis-bicyclo [2,2,1] hepto-5-en-2,3-dicarboxylic acid), and suitable derivatives include, for example, acid halides, amides, imides, anhydrides and esters, for example malenyl chloride, maleimide, maleic anhydride, citraconic anhydride, monomethyl maleate, dimethyl maleate and glycidyl maleate. Among these, unsaturated dicarboxylic acids or acid anhydrides thereof are preferred, and particularly useful are maleic acid, nadic acid® or acid anhydrides thereof. In preparing modified products by graft copolymerization of a graft monomer selected from among such unsaturated carboxylic acids or their derivatives as mentioned above with polyethylene, there can be adopted various methods, per se, known. For instance, there is a method in which a graft monomer is added to molten polyethylene and the mixture is graft copolymerized or a method in which a graft monomer is added to a solvent solution of polyethylene and the mixture is graft copolymerized. In either case, it is desirable to carry out the reaction in the presence of a radical initiator in order to efficiently effect the graft copolymerization of the above-mentioned graft monomer with polyethylene. The graft reaction is carried out usually at a temperature of 60-350°C. The proportion of the radical initiator used is usually in the range of from 0.001 to 1 part by weight based on 100 parts by weight of polyethylene. Useful radical initiators include organic peroxides, organic peresters, for example, benzoyl peroxide, dichlorobenzoyl peroxide, dicumyl peroxide, di-tert-butyl peroxide, 2,5-dimethyl-2,5-di(peroxidibenzoate)hexine-3, 1,4-bis(tert-butylperoxyisopropyl)benzene, lauroyl peroxide, tert-butylperacetate, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexine-3, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane, tert-butyl perbenzoate, tert-butyl perphenyl acetate, tert-butyl perisobutyrate, tert-butyl per-sec-octoate, tert-butyl perbivalerate, cumyl perbivalerate and tert-butyl perdiethyl acetate, and azo compounds such as azobisisobutyronitrile, dimethyl azoisobutyrate, etc. Among these, preferred are dialkylperoxides such as dicumyl peroxide, di-tert-butyl peroxide, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexine-3, 2,5-dimethyl-2,5-(tert-butylperoxy)hexane, 1,4-bis(tert-butylperoxyisopropyl)benzene, etc. This graft-modified polyethylene is used in an amount of 1-30 parts by weight, preferably 2-28 parts by weight, based on 100 parts by weight of the total weight of the above-mentioned (A) an ethylene/α-olefin copolymer and (B) a copolymer of ethylene and a radical polymerizable polar unsaturated monomer. The adhesive resin compositions of the present invention as a whole contain a grafted monomer in an amount of usually 0.01-3% by weight, preferably 0.05-2.5% by weight, this grafted monomer being derived from the above grafted-modified polyethylene (C). The adhesive resin compositions of the present invention may be prepared by mixing components (A), (B) and (C) in suitable amounts by various known methods, for example by mixing the components together with a Henschel mixer, v-blender, ribbon blender or tumbler blender, or melt kneading the resulting mixture with a single roll extruder, twin roll extruder, kneader or Banbury mixer, followed by granulating or pulverizing. In addition to the above-mentioned components, the adhesive resin compositions of the present invention can contain , for example, heat stabilizers, weathering agents, antistatic agents, pigments, dyes or rust preventives, in such amounts that no objects of the invention are hindered. The adhesive resin compositions of the invention are preferably used for joining particularly (i) a polyolefin layer to a polyvinylidene chloride layer, (ii) a polyester layer to an olefin/vinyl acetate copolymer saponification product layer, and (iii) a polycarbonate layer to an olefin/vinyl acetate copolymer saponification product layer. The laminates of the present invention prepared by the use of such adhesive resin compositions as illustrated above are described in detail hereinafter. The first laminate of the present invention is basically composed of a polypropylene layer (X-1)/an adhesive layer (Y)/a polyvinylidene chloride layer (Z-1). So long as any laminate has this basic structure of (X-1)/(Y)/(Z-1), the present invention further includes a laminate having a structure of (X-1)/(Y)/(Z-1)/(X-1). Furthermore, such laminates as having the above-mentioned structures to which a ribro layer (W) comprising a mixture of (X-1), (Y) and (X-1) has been added, that is, those having such structures as (X-1)/(W)/(Y)/(Z-1), (X-1)/(W)/(Y)/(Z-1)/(Y)/(X-1) and (X-1)/(W)/(Y)/(Z-1)/(Y)/(W)/(X-1) may also be included in the scope of the first laminate of the present invention. Polypropylene constituting (X-1) layer Polypropylene used for constituting the first laminate of the present invention includes concretely propylene homopolymer (so-called homopolypropylene), propylene random copolymers of propylene and α-olefins such as propylene/ethylene random copolymers, propylene/1-butene random copolymers, etc., and propylene block copolymers of propylene and α-olefins such as ethylene. The polypropylenes usually used in the present invention for forming the (X-1) layer are those having a melt flow rate (ASTM D 1238L) in the range of 0.01-200 g/10 min, preferably 0.1-100 g/10 min. Polyvinylidene chloride constituting (Z-1) layer Polyvinylidene chloride useful for constituting (Z-1) layer of the first laminate of the present invention are copolymers of vinylidene chloride as a principal component and acrylonitrile, vinyl chloride, acrylates or methacrylates. Adhesive resin composition constituting (Y) layer The adhesive resin composition used for constituting adhesive layer (Y) of the first laminate of the present invention is composed, as mentioned previously in detail, of (A) an ethylene/α-olefin copolymer, (B) a copolymer of ethylene and a radical polymerizable polar unsaturated monomer and (C) a graft-modified polyethylene. Further, the second laminate of the present invention is composed of a polyester layer (X-2)/an adhesive layer (Y)/an olefin/vinyl acetate copolymer saponification product layer (Z-2). In the same manner as in the case of the first laminate of the present invention, however, this second laminate may have a structure different from the above-mentioned one, for example, (X-2)/(Y)/(Z-2)/(Y)/(X-2). Polyester resin constituting (X-2) layer The polyester resins are polyesters which are formed from aliphatic glycol such as ethylene glycol, propylene glycol, 1,4-butanediol, neopentyl glycol, hexamethylene glycol, etc., alicyclic glycol such as cyclohexane dimethanol, etc., aromatic dihydroxy compound such as bisphenol, etc., or dihydroxy compound unit selected from among at least two compounds mentioned above, and aromatic dicarboxylic acid such as terephthalic acid, isophthalic acid, 2,6-naphthalenedicarboxylic acid, etc., aliphatic dicarboxylic acid such as oxalic acid, succinic acid, adipic acid, sebacic acid, undecadicarboxylic acid, etc., or dicarboxylic acid unit selected from among at least two acids mentioned above. So long as the polyester resins exhibit thermoplasticity, they may be modified with a small amount of polyhydroxy compound exhibiting at least three valences such as triol or tricarboxylic acid, or carboxylic acid. Useful as these thermoplastic polyesters are concretely polyethylene terephthalate, polybutylene terephthalate, polyethylene isophthalate/terephthalate copolymers, etc. Olefin/vinyl acetate copolymer saponification product constituting (Z-2) layer The olefin/vinyl acetate copolymer saponification products used in the present invention are those obtained by saponifying an olefin/vinyl acetate copolymer having the olefin content of 15-60 mol%, preferably 25-50 mol%, so that a saponification degree of the saponified product becomes at least 50%, preferably at least 90%. If the saponification products obtained have the olefin content of less than 15 mol%, they are not desirable, because they are liable to heat decomposition, involve difficulty in the melt molding thereof, and they are also poor in stretchability and become poor in water resistance as they absorb water and are apt to swell. On one hand, if the above-mentioned olefin content exceeds 60 mol%, the saponification products obtained are not desirable, because they become poor in gas barrier properties. Furthermore, the saponification products are undesirable if they have a saponification degree of less than 50%, because they become poor in gas barrier properties. Preferably useful olefins which are copolymerizable with vinyl acetate include concretely ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, 1-octene, 1-decene, 1-tetracene and 1-octadecene, and among these, particularly preferred is ethylene from the standpoint of mechanical strength and moldability. The adhesive layer (Y) used in the second laminate of the present invention is such adhesive layer (Y) as aforementioned. Next, the third laminate of the present invention is composed of a polycarbonate layer (X-3)/an adhesive layer (Y)/an olefin/vinyl acetate copolymer saponification product layer (Z-2). In the same manner as in the case of the first laminate of the present invetion, however, the third laminate of the invention may have such structure, for example, as (X-3)/(Y)/(Z-2)/(Y)/(X-3), etc. Polycarbonate resin constituting (X-3) layer The polycarbonate resins used herein include various polycarbonates and copolycarbonates which are obtained by reacting, according to the known method, dihydroxy compounds with phosgene or diphenyl carbonate. The dihydroxy compounds include hydroquinone, resorcinol, 4,4′-dihydroxy-diphenyl-methane, 4,4′-dihydroxy-diphenyl-ethane, 4,4′-dihydroxy-diphenyl-n-butane, 4,4′-dihydroxy-diphenyl-heptane, 4,4′-dihydroxy-diphenyl-phenyl-methane, 4,4′-dihydroxy-diphenyl-2,2-propane(bisphenol A), 4,4′-dihydroxy-3,3′-dimethyl-diphenyl-2,2-propane, 4,4′-dihydroxy-3,3′-diphenyl-diphenyl-2,2-propane, 4,4′-dihydroxy-dichloro-diphenyl-2,2-propane, 4,4′-dihydroxy-diphenyl-1,1-cyclopentane, 4,4′-dihydroxy-diphenyl-1,1-cyclohexane, 4,4′-dihydroxy-diphenyl-methyl-phenyl-methane, 4,4′-dihydroxy-diphenyl-ethyl-phenyl-methane, 4,4′-dihydroxy-diphenyl-2,2,2-trichloro-1,1-ethane, 2,2′-dihydroxydiphenyl, 2,6-dihydroxynaphthalene, 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy-3,3′-dichlorodiphenyl ether and 4,4′-dihydroxy-2,5-diethoxyphenyl ether. The polycarbonates obtained by using 4,4′-dihydroxy-diphenyl-2,2-propane(bisphenol A) are preferred because they are excellent in mechanical properties and transparency. The olefin/vinyl acetate copolymer saponification product layer (Z-2) and adhesive layer (Y) used in the third laminate of the present invention are the same as those illustrated already hereinbefore. Further, the adhesive resin compositions of the present invention can also be used for joining (iv) a polyester layer to polyvinylidene chloride layer, (v) a polycarbonate layer to a polyvinylidene chloride layer, and (vi) a polyolefin layer to an olefin/vinyl acetate copolymer saponification product layer. Accordingly, by virtue of using the adhesive resin compositions of the present invention, there are obtained laminate comprising a polyester layer/adhesive layer/polyvinylidene chloride layer, a laminate comprising a polycarbonate layer/adhesive layer/polyvinylidene chloride layer and further a laminate comprising a polyolefin layer/adhesive layer/olefin/vinyl acetate copolymer saponification product layer. Preparation of laminate The laminates of the present invention may be prepared by various known methods. For instance, when the laminate to be prepared is in the form of film or sheet, there may be mentioned a method wherein the resin to constitute (X) layer, the adhesive resin composition to constitute (Y) layer and the resin to constitute (Z) layer are individually melt extruded through separate extruders and fed to a die of three-layer structure, whereby these three components are co-extrusion molded so that the adhesive resin composition is positioned as an intermediate layer, a so-called sandwich lamination method wherein the adhesive resin composition is melt extruded in between the previously formed (X) layer and (Z) layer, and a so-called co-extrusion laminate method wherein the resin to constitute (X) layer and the adhesive resin composition to constitute (Y) layer are melted with separate extruders, extruded through a die of two-layer structure to form two layers, and the two layers are individually laminated on each of both sides of the previously formed (Z) layer. Further, when the laminate to be prepared is in the form of bottle, leg, pipe or tube, there may be adopted a co-extrusion molding method. Furthermore, when (X) layer or (Z) layer has been previously formed, these layer may be mono- or biaxially oriented. A film thickness of each layer of the laminates of the present invention may be decided in various ways according to the purpose for which the laminate is used. Usually, however, the film thickness is preferably 0.02-5 mm in (X) layer, 0.01-1 mm in (Y) layer, and 0.01-1 mm in (Z) layer. The adhesive resin compositions of the present invention exhibit excellent adhesive power, particularly they do not decrease in their adhesive power even when they come in contact with water at elevated temperatures. Accordingly, when a polyolefin layer is joined to a polyvinylidene chloride layer by using the adhesive resin compositions, there is obtained a laminate which is not only excellent in gas barrier properties and moisture barrier properties. The present invention is illustrated below with reference to examples, but it should be construed that the invention is in no way limited to those examples. Example 1 Composition (I) was prepared by mixing together 75 parts by weight of an ethylene/propylene random copolymer (hereinafter called EPR-1; a melt flow rate (MFR) 1.0g/10 min, ethylene content 80 mol%, density 0.865/cm³, crystallinity index 4%), 25 parts by weight of an ethylene/vinyl acetate copolymer (hereinafter called EVA-1; MFR 2.5 g/10 min, vinyl acetate content 25% by weight) and 20 parts by weight of a maleic anhydride-modified polyethylene (hereinafter called MAH-PE-1; MFR 1.0 g/10 min, density 0.925 g/cm³, crystallinity index 52%, butene content 3.6 mol%, graft amount of maleic anhydride 1.0 g/100 g polymer), the graft amount of maleic anhydride, crystallinity index and MFR of said composition (I) being 0.2 g/100 g polymer, 15% and 1.2 g/10 min, respectively. Subsequently, the composition (I) thus prepared was formed by the compression molding method into a sheet of 150 in thickness. Subsequently, on both sides of the sheet thus formed were laminated a polyvinylidene chloride (PVDC-1) [a product of Dow Chemical (U.S.) sold under a trade name of SARAN X05253-16] layer (Z) of 150 µmin thickness and a homopolypropylene (hereinafter called PP-1; MFR 6.0 g/10 min) layer (X) of 150 µmin thickness so that the sheet of the composition (I) becomes an intermediate layer (Y). Leaving a part of the laminate thus prepared behind for peeling test, the remaining laminate was heat sealed at a temperature of 230°C, a heating time of 3 seconds and a pressure of 1kg/cm² to form a three-layer laminate comprising PVDC-1 layer/composition (I) layer/PP-1 layer. Test specimens of 15 mm in width were cut off from this three-layer laminate, and the initial adhesion strength between the PVDC-1 layer and composition (I) layer, and the initial adhesion strength between the composition (I) layer and PP-1 layer were measured by means of a T-peel tester (peeling speed 300 mm/min, measurement temperature 23°). The results obtained are shown in Table 1. Subsequently, the test specimens of 15 mm in width obtained above were subjected to heat treatment with an autoclave for 1 hour at 131°C, and the adhesion strength between the layers was measured in the same manner as in the peel test with the above-mentioned T-peel tester. The results obtained are shown in Table 1. Example 2 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of an ethylene/1-butene random copolymer (hereinafter called EBR-1; MFR 3.0 g/10 min, ethylene content 90 mol%, density 0.885 g/cm³, crystallinity index 14%), 25 parts by weight of EVA-1 and 20 parts by weight of MAH-PE-1, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.17 g/100 g polymer, 21% and 2.4 g/10 min, respectively, and in place of the PP-1, there was used a propylene random copolymer (hereinafter called PP-2; MFR 6.2 g/10 min, ethylene content 4 mol%). The results obtained are shown in Table 1. Example 3 Example 1 was repeated except that in place of the composition (I) used therein, there used a composition comprising a mixture of 75 parts by weight of an ethylene/1-butene copolymer (hereinafter called EBR-2; MFR 2.0 g/10 min, ethylene contents 93 mol%, density 0.892 g/cm³, crystallinity index 22%), 25 parts by weight of EVA-1 and 20 parts by weight of MAH-PE-1, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.17 g/100 g polymer, 27% and 1.9 g/10 min, respectively. The results obtained are shown in Table 1. Example 4 Example 1 was repeated except that in place of the composition used therein, there used a composition comprising a mixture of 65 parts by weight of EPR-1, 35 parts by weight of an ethylene/vinyl acetate copolymer (hereinafter called EVA-2; MFR 2.0 g/10 min, vinyl acetate content 10% by weight), and 25 parts by weight of a maleic anhydride graft-modified polyethylene (hereinafter called MAH-PE-2; MFR 3.5 g/10 min, density 0.910 g/cm³, cristallinity index 40%, butene content 5.5 mol%, graft amount of maleic anhydride 0.5 g/100 g polymer), the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.1 g/100 g of polymer, 20% and 1.6 g/10 min. The results obtained are shown in Table 1. Example 5 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of EPR-1, 25 parts by weight of EVA-1 and 5 parts by weight of a maleic anhydride graft-modified polyethylene (hereinafter called MAH-PE-3; MFR 4.3 g/10 min, density 0.962 g/cm³, crystallinity index 72%, butene content 0.5 mol%, graft amount of maleic anhydride 2.2 g/100 g polymer), the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.11 g/100 g polymer, 11% and 3 g/10 min, respectively. The results obtained are shown in Table 1. Example 6 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 85 parts by weight of EPR-1, 15 parts by weight of EVA-1 and 5 parts by weight of MAH-PE-3, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.11 g/100 g polymer, 9% and 1.2 g/10 min, respectively, and in place of PP-1, there was used a propylene block copolymer (hereinafter called PP-3; MFR 5.5 g/10 min). The results obtained are shown in Table 1. Example 7 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of an ethylene/propylene random copolymer (hereinafter called EPR-2; MFR 12 g/10 min, ethylene content 80 mol%, density 0.865 g/cm³, crystallinity index 4%), 25 parts by weight of an ethylene/vinyl acetate copolymer (hereinafter called EVA-3; MFR 15 g/10 min, vinyl acetate content 28%) and 15 parts by weight of MAH-PE-3, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.29 g/100 g polymer, 15% and 11 g/10 min, respectively. The results obtained are shown in Table 1. Example 8 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of EPR-1, 25 parts by weight of an ethylene/ethyl acrylate copolymer (hereinafter called EEA-1; MFR 5 g/10 min, ethyl acrylate content 25% by weight) and 5 parts by weight of MAH-PE-3, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.11 g/100 g polymer, 11% and 1.4 g/10 min. The results obtained are shown in Table 1. Comparative Example 1 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 100 parts of EPR-1 and 25 parts by weight of MAH-PE-1, the graft amount of maleic anhydride, crystallinity and MFR of said composition being 0.2 g/100 g polymer, 14% and 1.0 g/10 min, respectively. The results obtained are shown in Table 1. Comparative Example 2 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 80 parts by weight of EPR-1 and 20 parts by weight of EVA-1, the graft amount of maleic anhydride, crystallinity and MFR of said composition being 0 g/100 g polymer, 7% and 1.2 g/10 min, respectively. The results obtained are shown in Table 1. Comparative Example 3 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 100 parts by weight of EVA-1 and 25 parts by weight of MAH-PE-1, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.2 g/100 g polymer, 25% and 2.1 g/10 min, respectively. The results obtained are shown in Table 1. Comparative Example 4 Example 1 was repeated except that in place of the composition (I) used therein, there was used MAH-EPR-1 (MFR 0.5 g/10 min, ethylene content 80 mol%, density of 0.865 g/cm³, graft amount of maleic anhydride 0.5 g/100 g polymer. The results obtained are shown in Table 1. Comparative Example 5 Example 1 was repeated except that in place of the composition (I) used therein, there was used MAH-EVA-1 (MFR 1.2 g/10 min, content of vinyl acetate 25% by weight, crystallinity index 18%, graft amount of maleic anhydride 0.5 g/100 g polymer). The results obtained are shown in Table 1. Comparative Example 6 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 70 parts by weight of MAH-EPR-1 and 30 parts by weight of MAH-EVA-1, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.5 g/100 g polymer, 8% and 0.7 g/10 min, respectively. The results obtained are shown in Table 1. Example 9 Example 1 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of EPR-1, 25 parts by weight of EVA-1 and 5 parts by weight of MAH-PE-3, and in place of the PP-1, there was used a low density polyethylne (hereinafter called LDPE-1; MFR 2.0g/10 min, density 0.920g/cm³). The results obtained are shown in Table 2. Example 11 The composition (I) obtained in Example 1, polycarbonate (hereinafter called PC; a product of Teijin Kasei K.K. sold under a trade name of TEIJIN PANLITE L-1250 and an ethylene/vinyl acetate copolymer saponification product (hereinafter called EVOH; MFR 1.3 g/10 min, density 1.19 g/cm³, ethylene content 32 mol%; a product of Kuraray Co., Ltd. sold under a trade name of KURARAYEVAL EP-F) were laminated together under the following conditions to obtain a five-layer bottle. Bottle structure: PC / (I) / EVOH / (I) / PC Film thickness of layer (µm): 200/50/50/50/200 Bottle shape: 200 cc Cylindrical bottle Extruder: 65 mm  Extruder 280°C (for PC) 40 mm  Extruder 250°C (for (I) ) 40 mm  Extruder 210°C (for EVOH) The five-layer bottle thus obtained was tested with a T-peel tester for interfacial adhesion strength (FPC, g/15 mm) between PC layer and (I) layer and interfacial adhesion strength (FEVOH, g/15 mm) between EVOH layer and (I) layer. Further, this bottle was filled with hot water kept at 90°C, formed with hand, and the hot water was discharged therefrom to inspect visually occurrence of interfacial peeling of this bottle. The results obtained are shown in Table 3. Subsequently, a five-layer sheet was formed by using the composition (I), the above-mentioned EVOH and polyethylene terephthalate (hereinafter called PET; a product of Mitsui PET K.K. sold under a trade name of J-135 to which a crystallization accelerator has been added) under the following conditions. Sheet structure: PET/ (I)/ EVOH/ (I)/ PET Film thickness of layer (µm): 150/50/50/50/150 Extruder: 65 mm ⊘ Extruder 280°C (for PET) 40 mm ⊘ Extruder 250°C (for (I) ) 40 mm ⊘ Extruder 210°C (for EVOH) The sheet thus obtained was vacuum formed at a mold temperature of 160°C into the form of cup, whereby the PET layer was crystallized. The cup obtained was limbed from it wall side to obtain interfacial adhesion strength (FPET, g/15 mm) between PET layer and (I) layer, and interfacial adhesion strength (FEVOH, g/15 mm) between EVOH layer and (I) layer. Further, this cup was filled with hot water kept at 90°C, the cup was deformed with hand and the hot water was discharged therefrom to inspect visually occurrence of interfacial peeling of the cup. The results obtained are shown in Table 3 Example 12 Example 11 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of an ethylene/1-butene random copolymer (hereinafter called EBR-1; MFR 3.0 g/10 min, ethylene content 90 mol%, density 0.885/cm³, crystallinity index 14%), 25 parts by weight of EVA-1 and 20 parts by weight of MAH-PE-1, the graft ratio of maleic anhydride, crystallinity index and MFR of said composition being 0.17 g/100 g polymer, 21% and 2.4 g/10 min, respectively. The results obtained are shown in Table 3. Example 13 Example 11 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of an ethylene/1-butene random copolymer (hereinafter called EBR-2; MFR 2.0 g/10 min, ethylene content 93 mol%, density 0.892 g/cm³, crystallinity index 22%), 25 parts by weight of EVA and 20 parts by weight of MAH-PE-1, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.17 g/100 g polymer, 27% and 1.9 g/10 min, respectively. The results obtained are shown in Table 3. Example 14 Example 11 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 65 parts by weight of EPR-1, 35 parts by weight of an ethylene/vinyl acetate copolymer (hereinafter called EVA-2; MFR 2.0 g/10 min, vinyl acetate content 10% by weight) and 25 parts by weight of a maleic anhydride graft-modified polyethylene (hereinafter called MAH-PH-2; MFR 3.5 g/10 min, density 0.910 g/cm³, crystallinity index 40%, butene content 5.5 mol%, graft amount of maleic anhydride 0.5 g/100 g polymer), the graft ratio of maleic anhydride, crystallinity index and MFR of said composition being 0.1 g/100 g polymer, 20% and 1.6 g/10 min, respectively. The results obtained are shown in Table 3. Example 15 Example 11 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of EPR-1, 25 parts by weight of EVA-1 and 5 parts by weight of a maleic anhydride graft-modified polyethylene (hereinafter called MAH-PE-3; MFR 4.3 g/10 min, density 0.962 g/cm³, crystallinity index 72%, butene content 0.5 mol%, graft amount of maleic anhydride 2.2 g/100 g polymer), the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.11 g/100 g polymer, 11% and 1.3 g/10 min, respectively. The results obtained are shown in Table 3. Example 16 Example 11 was repeated except that in place of the composition (I) used therein, there was used a composition comprising 85 parts by weight of EPR-1, 15 parts by weight of EVA and 5 parts by weight of MAH-PE-3, the graft ratio of maleic anhydride, crystallinity index and MFR of said composition being 0.11 g/100 g polymer, 9% and 1.2 g/10 min, respectively. The results obtained are shown in Table 3. Example 17 Example 11 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 75 parts by weight of an ethylene/propylene random copolymer (hereinafter called EPR-2; MFR 12 g/10 min, ethylene content 80 mol%, density 0.865 g/cm³, crystallinity index 4%), 25 parts by weight of an ethylene/vinyl acetate copolymer (hereinafter called EVA-3; MFR 15 g/10 min, vinyl acetate content 28% by weight) and 15 parts by weight of MAH-PE-3, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0.29 g/100 g polymer, 15% and 11 g/10 min, respectively. The results obtained are shown in Table 3. Comparative Example 7 Example 9 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 100 parts by weight of EPR-1 and 25 parts by weight of MAH-PE-1, the graft ratio of maleic anhydride, crystallinity index and MFR of said composition being 0.2 g/100 g polymer, 14% and 1.0 g/10 min, respectively. The results obtained are shown in Table 3. Comparative Example 8 Example 9 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 80 parts by weight of EPR-1 and 20 parts by weight of EVA, the graft amount of maleic anhydride, crystallinity index and MFR of said composition being 0 g/100 g polymer, 7% and 1.2 g/10 min, respectively. The results obtained are shown in Table 3. Comparative Example 9 Example 9 was repeated except that in place of the composition (I) used therein, there was used a composition comprising a mixture of 100 parts by weight of EVA-1 and 25 parts by weight of MAH-PE-1, the graft amount of maleic anhydride, crystallinity index and MFR of said composition (X) being 0.2 g/100 g polymer, 25% and 2.1 g/10 min, respectively. The results obtained are shown in Table 3. Comparative Example 10 Example 9 was repeated except that in place of the composition (I) used therein, there was used MAH-EPR-1 (MFR 0.5 g/10 min, ethylene content 80 mol%, density 0.865 g/cm³, crystallinity index 4%, graft amount of maleic anhydride 0.5 g/100 g polymer). The results obtained are shown in Table 3. Comparative Example 11 Example 9 was repeated except that in place of the composition (I) used therein, there was used MAH-EVA-1 (MFR 1.2 g/10 min, vinyl acetate content 25% by weight, crystallinity index 18%, graft amount of maleic anhydride 0.5 g/100 g polymer). The results obtained are shown in Table 3. Comparative Example 12 Example 9 was repeated except that in place of the composition (I) used therein, there was a composition comprising 70 parts by weight of MAH-EPR-1 and 30 parts by weight of MAH-EVA-1, the graft ratio of maleic anhydride, crystallinity index and MFR of said composition being 0.5 g/100 g polymer, 8% and 0.7 g/10 min, respectively. The results obtained are shown in Table 3.

Claims: An adhesive resin composition comprising (A) 95-50% by weight of an ethylene/α-olefin copolymer having a density of 0.850-0.900 g/cm³, an ethylene content of 75-95 mol% and a crystallinity index as measured by X-ray of less than 30%, (B) 5-50% by weight of a copolymer of ethylene and a radical polymerizable polar unsaturated monomer, said copolymer having a content of the radical polymerizable polar unsaturated monomer of 5-40% by weight, and (C) 1.0-30 parts by weight, based on 100 parts by weight of the sum of the above-mentioned (A) + (B), of a graft-modified polyethylene having a density of 0.900 to 0.980 g/cm³ and a crystallinity index as measured by X-ray of at least 30%, wherein a part or whole of a polyethylene has been graft-modified with an unsaturated carboxylic acid or derivative thereof. A composition according to claim 1 wherein the copolymer (B) is selected from ethylene/vinyl acetate copolymers, ethylene/ethyl acrylate copolymers, ethylene/methyl acrylate copolymers, ethylene/acrylic acid copolymers and ethylene/methacrylic acid copolymers. A laminate comprising a polyolefin layer and a polyvinylidene chloride layer laminated through an intermediate layer consisting of an adhesive resin composition as claimed in claim 1 or 2. A laminate according to claim 3, wherein the polyolefin layer is of polypropylene. A laminate comprising a polyester layer and a layer of an olefin/vinyl acetate copolymer saponification product laminated through an intermediate layer consisting of an adhesive resin composition as claimed in claim 1 or 2. A laminate comprising a polycarbonate layer and a layer of an olefin/vinyl acetate saponification product laminated through an intermediate layer consisting of an adhesive resin composition as claimed in claim 1 or 2.

Inventors: KUBO MINEO, NAKAGAWA MIKIO, SATO KOICHIRO, KUBO, MINEO, NAKAGAWA, MIKIO, SATO, KOICHIRO
Applicants: MITSUI PETROCHEMICAL IND, MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1988
Main classification: B32B27
IPC codes: C09J123, C08L23, B32B27