Rubber-modified cyanate ester resins, their preparation and polytriazines derived therefrom

Abstract: Polytriazines exhibiting improved toughness without sacrificing heat resistance are prepared by curing a cyanate ester resin having dispersed therein resin-insoluble rubber particles grafted with a resin-­ soluble polymer. The resin-soluble polymer stabilizes the rubber particles and maintains the particles in an essentially discrete, nonagglomerated form

Description: This invention relates to rubber-modified cyanate ester compounds and polytriazines prepared therefrom. It also relates to a process for preparing the rubber-modified cyanate ester compounds and polytriazines. Polytriazines are well-known thermosets. They possess good heat resistance, hardness, electrical properties, dimensional stability, corrosion resistance, and chemical resistance. Polytriazines are useful as adhesives and as coatings for substrates. They are also useful for the preparation of advanced composites and for the preparation of electrical laminates. Attempts have been made to toughen or reinforce polytriazines for demanding electronic and aerospace applications by incorporating liquid or elastic rubbers, such as polybutadiene and carboxyl-terminated butadiene-acrylonitrile copolymers, into cyanate ester resins before cure. See, for example, US-A's 4,403,073; 4,404,330; 4,396,745; and 4,503,186. The liquid or elastic rubber is mixed with a cyanate ester resin or the prepolymer of the resin and the resulting mixture is cured to form the rubber-modified polytriazine. Unfortunately, the liquid or elastic rubber is soluble in the cyanate ester resin. The formation of discrete rubber particles in the polytriazine will therefore depend on the degree of solubility of the rubber in the polytriazine. If the rubber is highly soluble, then discrete rubber particles will not form and the heat resistance of the rubber-modified polytriazine as measured by the glass transition temperature will be severely reduced because the rubber plasticizes the polytriazine. If the rubber is only partially soluble, then discrete rubber particles may form but the particle size, particle size distribution and particle composition will be uncontrollable. The heat resistance of the rubber-modified polytriazine will be reduced because of the presence of partially dissolved rubber in the polytriazine matrix. Additionally, the heat resistance and other important properties of the polytriazine will vary with the morphology of the rubber incorporated into the polytriazine. In view of the unsuccessful attempts at preparing rubber-modified polytriazines without significantly sacrificing heat resistance, and in view of the unsuccessful attempts at controlling the morphology of the rubber incorporated into the polytriazine, it would be desirable to prepare a rubber-modified polytriazine exhibiting acceptable heat resistance and a controlled morphology. It would also be desirable to prepare a rubber-modified cyanate ester compound that could be cured to form the desired rubber-modified polytriazine. In one aspect, the present invention is a method of preparing a rubber-modified cyanate ester compound comprising the step of (a) making an emulsion that contains: 1) an emulsion polymerizable monomer selected from a vinyl aromatic monomer, an a,β-ethylenically unsaturated acid, an alkyl ester of an a,β-ethylenically unsaturated acid wherein the alkyl group has less than 4 carbon atoms, a hydroxyalkyl ester of an a,β-ethylenically unsaturated acid, an unsaturated nitrile, an epoxy funtional monomer, an unsaturated ester of an a,β-ethylenically unsaturated acid, and any mixture thereof, and 2) an aqueous rubber latex having a surfactant or emulsifier and rubber particles, which are 0.03 µm - 2 µm in diameter and are insoluble in a cyanate ester compound that contains at least one cyanate group, (b) polymerizing the emulsion from step (a) to form a colloidal dispersion of the rubber particles wherein essentially every rubber particles is grafted with the resulting polymer that is soluble in the cyanate ester compound, and (c) mixing the grafted rubber particles with the cyanate ester compound and forming a homogeneous dispersion of the rubber particles within the continuous phase of the cyanate ester compound. The invention is also a rubber-modified cyanate ester compound. The cyanate ester compound comprises (a) a discontinuous phase of grafted rubber particles which contain rubber particles that are 0,03 µm to 2 µm in diameter and are insoluble in the cyanate ester compound that contains at least one cyanate group, grafted with a polymer that is soluble in the cyanate ester compound and results from emulsion polymerization of monomers selected from a vinyl aromatic monomer, an a,β-ethylenically unsaturated acid, an alkyl ester of an a,β-ethylenically unsaturated acid wherein the alkyl group has less than 4 carbon atoms,a hydroxyalkyl ester of an a,β-ethylenically unsaturated acid, an unsaturated nitrile, an epoxy functional monomer, an unsaturated ester of an a,β-ethylenically unsaturated acid, and any mixture thereof homogenously dispersed within (b) a continuous phase of a cyanate ester compound that contains at least on cyanate group. In another aspect, the invention is a rubber-modified polytriazine of a cyanate ester compound. The rubber-modified polytriazine of a cyanate ester compound that contains at least one cyanate group comprises: (a) a discontinuous phase of grafted rubber particles that are 0.03 µm to 2 µm in diameter and are insoluble in the cyanate ester compounds from which the polytriazine is derived, where essentially every rubber particle is grafted with a polymer that is soluble in the cyanate ester compound from which the polytriazine is derived and results from emulsion polymerisation of monomers selected from a vinyl aromatic monomer, an a,β-ethylenically unsaturated acid, an alkyl ester of an a,β-ethylenically unsaturated acid wherein the alkyl group has less than 4 carbon atoms, a hydroxyalkyl ester of an a,β-ethylenically unsaturated acid, an unsaturated nitrile, an epoxy functional monomer, an unsaturated ester of an a,β-ethylenically unsaturated acid, and any mixture thereof homogeneously dispersed within (b) a continuous phase of a polytriazine. The rubber particles in all embodiments of the present invention are maintained in a discrete spaced apart relationship to each other by the grafted polymer. Surprisingly, the rubber-modified polytriazines of this invention exhibit a substantial increase in toughness with little or no decrease in heat resistance. They can be prepared by curing the rubber-modified cyanate ester compounds of this invention. The rubber particles are stabilized by the grafted polymer formed during the polymerization so that the particles remain in an essentially discrete, nonagglomerated form. The rubber particles are uniformly dispersed in the cyanate ester compound and the polytriazine prepared therefrom. The average rubber particle size, the distribution of particle sizes, the particle composition and the degree to which the particles are uniformly dispersed can be carefully controlled. The rubber-modified polytriazines of this invention are useful for preparing advanced composites for aerospace structures and for preparing fiber-reinforced laminates, and for any other application where polytriazines are used. Cyanate ester compounds having at least one cyanate group. are well known in the art and are disclosed in US-A s 3,553,244; 3,740,348; and 3,755,402. Preferred cyanate ester compounds are difunctional and polyfunctional aromatic polycyanates, which are disclosed in the patents referenced above and additionally in US-A s 3,448,079; 4,094,852; and 4,528,366. The preferred aromatic polycyanates are prepared from the polyhydric phenols of bisphenol A, bisphenol S, halogenated and alkylated analogs of bisphenol A and bisphenol S, novolak resins, and polyphenols bridged by at least one polycyclic aliphatic group as described in US-A 4,528,366. The most preferred cyanate ester compound has the following formula: wherein the average value of n is 0.2. A process for preparing the most preferred cyanate ester compound and other preferred cyanate ester compound is disclosed in copending US-A 4,748,270 dated May 31, 1988. A polytriazine is the polymer formed by the trimerization of a cyanate ester compound. Included within the term are oligomers and prepolymers. Also included are copolymers of the cyanate ester compound and a monomer having at least one cyanate-reactive functionality. Examples of monomers with cyanate-reactive functionalities include but are not limited to epoxies, maleimides, and vinyl-terminated monomers. The rubber particles of this invention have diameters of 0.03 µm - 2 µm (300 Å to 20,000 Å), more preferably from 0.09 µm - 0,2 µm (900 Å to 2,000 Å). The particles form a colloidal dispersion in water if they are treated with a surfactant or emulsifier and tend to agglomerate if they are untreated. If desired, a bimodal distribution of rubber particles can be employed. A bimodal distribution is a distribution of large and small particles. This distribution is possible by agglomerating small particles or selectively growing small particles. In preferred embodiments, a bimodal distribution of grafted rubber particles dispersed in a cyanate ester compound exhibits a reduced viscosity relative to the viscosity exhibited by a uniform, or monodisperse, distribution of grafted rubber particles dispersed in the cyanate ester compound. The small particles have diameters of 0.09 µm - 0.15 µm (900 Å to 1500 Å) more preferably 0.1 µm (1000 Å), and the large particles have diameters of 0.4 µm - 1 µm (4000 Å to 10,000 Å), more preferably 0.8 µm (8000 Å). The rubber particles are insoluble in (1) water, (2) the cyanate ester compound, and (3) any solvent for the cyanate ester compound. Examples of insoluble rubber particles are polymers from alkyl esters of α,β-ethylenically unsaturated monomers wherein the alkyl group has at least 4 carbon atoms, such as polybutyl acrylate or methacrylate, and poly(2-ethyl-1-hexyl)acrylate or methacrylate. In a preferred embodiment, rubber particles are crosslinked to render them insoluble. Crosslinked rubber particles form a gel and swell in the cyanate ester compound but do not dissolve. The percent gel can range from 50 to 98 percent of the weight of the particles, more preferably from 70 to 95 percent, and the swelling index can range from 3 to 50, more preferably from 10 to 30. A method for determining the percent gel and swelling index is disclosed in US-A 4,146,589. Examples of rubbers that can be crosslinked to render them insoluble include polybutadiene, styrene-butadiene copolymer, acrylate rubbers, neoprene, butyl rubber, nitrile rubber, acrylonitrile-butadiene-styrene (ABS) terpolymer, polyisoprene, ethylene-propylene copolymer (EPDM), fluoroelastomers, and mixtures of the above. Preferred rubber particles are crosslinked ABS terpolymer as described in the Encyclopedia of Polymer Sciences and Engineering , Vol. 2, 2nd ed., pp. 388-426 (1985), and crosslinked styrene-butadiene copolymer wherein the amount of butadiene in the copolymer ranges from 50 to 99 percent of the weight of the particles, more preferably from 85 to 95 percent. The emulsion polymerizable monomers of this invention polymerize under emulsion polymerization conditions. The polymer formed is insoluble in water and must be soluble in the cyanate ester compound otherwise, uncontrolled agglomeration of the rubber particles can occur. Examples of suitable emulsion polymerizable monomers include vinyl aromatic monomers, such as styrene, vinyl toluene, and t-butyl styrene; α,β-ethylenically unsaturated acids such as acrylic and methacrylic acid, and itaconic acid; alkyl esters of α,β-ethylenically unsaturated acids wherein the alkyl group has less than 4 carbon atoms, such as methyl acrylate and methacrylate, and ethyl acrylate; hydroxyalkyl esters of α,β-ethylenically unsaturated acids such as hydroxyethyl acrylate and methacrylate, and hydroxypropyl acrylate; unsaturated nitriles such as acrylonitrile; epoxy functional monomers such as glycidyl acrylate and methacrylate; and unsaturated esters of α,β-ethylenically unsaturated acids such as allyl acrylate and methacrylate, and dicyclopentadiene acrylate and methacrylate; and mixtures of the above. Preferred monomer recipes are those containing mixtures of styrene, methyl methacrylate, and acrylonitrile. The most preferred monomer recipe further contains either allyl acrylate or dicyclopentadiene acrylate. The aqueous colloidal dispersion of discrete rubber particles maintained in a reasonably stable state with a surfactant or emulsifier is commonly referred to as a rubber latex. The preparation of rubber latexes is well known in the art and is disclosed, for example, in The Vanderbilt Rubber Handbook , Vanderbilt Co. Inc., (1978). For a good discussion of suitable surfactants and emulsifiers, see the paragraph bridging columns 3 and 4 of US-A 4,421,660. The emulsion polymerizable monomer and the rubber latex can be combined and emulsified by normal mixing procedures, for example, by passing both the monomer and the latex through a high shear mixing device such as a Waring blender, homogenizer, or ultrasonic mixer. Preferably, the monomer is added continuously to the rubber latex during the polymerization while the rubber latex is being stirred. The continuous monomer stream can be an aqueous emulsion of the monomer where the emulsion is maintained by a surfactant or emulsifier. As another alternative, the aqueous emulsion of rubber particles and monomer can be prepared by adding rubber particles to an aqueous emulsion of monomer. In such instances, it is desirable to add more surfactant or emulsifier prior to or during the addition of the rubber particles. The amount of rubber particles in the emulsion desirably ranges from 15 to 65 percent of the weight of the emulsion, more preferably from 20 to 50 percent, and most preferably from 30 to 45 percent. The monomer is present in an amount sufficient to graft onto essentially every rubber particle when the monomer is polymerized. This amount can range from 5 to 50 percent of the weight of the rubber particles, more preferably from 10 to 30 percent. The surfactant or emulsifier is present in an amount sufficient to stabilize the aqueous dispersion of rubber particles. This amount can range from 2 to 5 percent of the weight of the rubber particles, more preferably from 2 to 3 percent. The remaining aqueous phase, which comprises water, initiator, and other additives, must be present in an amount sufficient to be the continuous phase of the emulsion. The emulsion polymerization conditions of this invention are generally conventional free-radical type polymerizations carried out in the presence of a radical initiator such as a peroxygen compound, an azo compound, ultraviolet light and the like. Preferably, the polymerization is carried out in the presence of a water-soluble peroxygen compound at temperatures in the range from 50° to 90°C. The amount of free-radical initiator can range from 0.005 to 8 percent of the weight of the monomer, preferably from 0.01 to 5 percent. Examples of suitable initiators include inorganic persulfate compounds such as sodium persulfate, potassium persulfate, ammonium persulfate; peroxides such as hydrogen peroxide, t-butyl hydroperoxide, dibenzoyl peroxide and dilauroyl peroxide; azo compounds such as azobis-(isobutyronitrile), and other common free-radical generating compounds. Also suitable are various forms of free-radical generating radiation means such as ultraviolet radiation, electron beam radiation and gamma radiation. Alternatively, a redox initiator composition can be employed wherein the polymerization temperature ranges from 25° to 80°C. Exemplary redox initiator compositions include a peroxygen compound as described hereinbefore, preferably potassium persulfate or t-butyl hydroperoxide, and a reducing component such as sodium metabisulfite or sodium formaldehyde hydrosulfite. Chain transfer agents can be employed to control the molecular weight of the graft polymer prepared during the polymerization. Examples include mercaptans such as dodecyl mercaptan, dialkyl xanthogen disulfides, diaryl disulfides, and others listed in Blackley, Emulsion Polymerization , Wiley and Sons, Chapter 8 (1975), in amounts as described therein. The weight average molecular weight of the graft polymer can vary and generally ranges from 10,000 to 250,000, more preferably from 20,000 to 100,000, as measured by gel permeation chromatography. Following polymerization, the grafted rubber particles are mixed with the cyanate ester compound to form a homogeneous dispersion of the particles in the cyanate ester compound. The grafted rubber particles can be dispersed in either liquid cyanate ester compound or solid after the resin is melted or placed in solution. For example, if the cyanate ester compound is a liquid, then an aqueous dispersion of grafted rubber particles can be mixed with the resin and the aqueous phase can then be removed. If the cyanate ester compound is a solid, then an aqueous dispersion of grafted rubber particles can be mixed with a resin dissolved in an organic solvent and both the aqueous and organic phases can then be removed. Alternatively, the grafted rubber particles can be extracted from the aqueous phase with an organic solvent of the cyanate ester compound and then the dispersion of grafted rubber particles can be mixed with the solid resin. If desired, a dried rubber concentrate can be mixed with the cyanate ester compound. Preferably, in such instances the mixing is accomplished using a high shear mixing device. The amount of grafted rubber particles incorporated into the cyanate ester compound is an amount effective to provide the desired degree of toughening for the polytriazine. Generally, this amount ranges from 0.1 to 30 percent of the weight of the cyanate ester compound. Amounts below 0.1 percent will not provide an appreciable increase in toughness and amounts above 30 percent could adversely affect the stiffness or rigidity of the polytriazine. Amounts ranging from 2.5 to 10 percent are preferred. Additives that improve the physical and chemical properties of the polytriazine can be incorporated into the cyanate ester compound in minor amounts before cure. For example, antioxidants can be added to improve the thermal stability of the grafted rubber and polytriazine. The homogeneous dispersion of grafted rubber particles and cyanate ester compound is cured to form the rubber-modified polytriazine. The dispersion is cured in a manner similar to the curing of a cyanate ester compound that does not contain a dispersion of grafted rubber particles. The dispersion can be cured thermally without the use of a catalyst. Preferably, a catalyst is used. US-A s 3,694,410; 4,094,852; and 4,528,366 disclose suitable catalysts. Preferred catalysts are cobalt catalysts such as cobalt acetylacetonate, cobalt octoate, and cobalt naphthenate. The amount of catalyst can range from 10 ppm to 1000 ppm based on the weight of cyanate ester resin. The rubber-modified polytriazines of this invention exhibit dramatically improved toughness without a significant reduction in heat resistance. This improvement is possible because the rubber particles are grafted with a polymer that maintains the particles in a discrete, spaced apart relationship to each other when the particles are incorporated into the cyanate ester compound and cured. The particles have a uniform particle size and are uniformly distributed. This ideal morphology allows the particles to substantially increase the toughness without sacrificing the heat resistance of the polytriazine. The following example is illustrative of this invention. Example In each of a series of runs, 1014 grams (g) of a rubber latex containing 300 g of rubber particles was charged into a two-liter, 3-neck, roundbottom glass flask equipped with a mechanical stirrer, temperature controller, and reflux condensor with a nitrogen inlet. The rubber particles were crosslinked styrene-butadiene copolymer (7 percent styrene, 93 percent butadiene) having an average diameter of 0.11 µm (1100 Å) as measured by a Brice Phoenix Light Scattering Unit. The particles were stabilized in the latex with 3 percent sodium dodecylbenzene sulfonate soap. 0.56 Grams of 2,2-azobis(isobutyronitrile) was added to the flask and the contents were agitated at 150 rpm. The reactor was flushed with nitrogen and was heated with the aid of a water bath to a temperature of 70°C. For each run, 56.3 g of a monomer stream having one of the compositions disclosed as Samples 1-6 in Table I was added to the reactor and was emulsified in the rubber latex. Twenty percent of the monomer stream was initially added continuously at 70°C at a rate of 0.075 g per minute for 150 minutes. After this addition, the reactor temperature was raised to 80°C and the remaining monomer stream was added continuously over a 90 minute period. The reaction mixture was heated at 80°C for an additional 2 hours, and then was allowed to cool before being transferred to another flask. The rubber latex was vacuum stripped to remove any unreacted monomers. The resulting grafted rubber latex contains 32.3 percent solids and has an average particle diameter of 0.12 µm (1200 Å) as measured by a Brice Phoenix Light Scattering Unit. The grafted rubber latex was diluted with methylethylketone (MEK) and water. The diluted mixture was allowed to settle and the bottom aqueous layer was removed. The top layer was washed 4 times with an aqueous solution of 25 percent MEK to remove the ionic soap and salts. For each run, the most preferred cyanate ester compound was dissolved in the MEK dispersion of grafted rubber particles in an amount sufficient to bring the grafted rubber content to 5 percent of the total weight of the combination of the grafted rubber particles and the cyanate ester compound. The solvent and any remaining water were then vacuum stripped to yield a dispersion of the grafted rubber in the cyanate ester compound wherein the grafted rubber content is 5 percent of the dispersion. A solution of cobalt acetylacetonate in acetonitrile was added to the dispersion to bring the total cobalt concentration to 100 parts per million based on the weight of the cyanate ester compound. The resulting mixture was then cured in a mold for 1 hour at 175°C, 2 hours at 225°C and 0.5 hours at 250°C. The resulting rubber-modified polytriazine was then machined into test specimens. The identical procedure for preparing the rubber-modified polytriazine was repeated at least once for each run, except that the grafted rubber content of the cyanate ester compound was varied. The physical properties for each specimen were analyzed and the results are disclosed in Table II. Composition of Monomer Stream Sample Weight Percent of Each Monomer Component S¹ MMA² AN³ GMA⁴ AA⁵ DCPDA⁶ 1 30 30 25 15 -- -- 2 30 30 25 -- 15 -- 3 30 30 25 -- -- 15 4 55 -- 30 -- -- 15 5 45 15 25 -- -- 15 6 37.5 37.5 25 -- -- -- S = Styrene; MMA = Methyl methacrylate; AN = Acrylonitrile; GMA = Glycidyl methacrylate; AA = Allyl Acrylate; DCPDA = Dicyclopentadiene acrylate. Properties of Rubber-Modified Polytriazines Sample From Which Grafted Rubber Latex is Derived Grafted Rubber Content of Dispersion of Modified Cyanate Ester compound (Weight Percent) T g (°C) of Rubber Modified Polytriazine G IC (J/m²) of Rubber-Modified Polytriazine Control* 0 248 60 1 5 235 290 1 10 235 490 2 5 237 340 2 10 not measured 560 3 5 234 340 3 10 not measured 560 4 2.5 240 190 4 5 236 390 4 10 not measured 720 5 5 not measured 420 5 10 not measured 720 6 2.5 254 200 6 5 253 320 6 10 255 630 The data in Table II indicates a dramatic increase in the fracture energy of the rubber-modified polytriazines relative to the fracture energy of the unmodified polytriazine (control). The results shown in Table II also indicate little or no decrease in the glass transition temperature of the rubber-modified polytriazines relative to the glass transition temperature of the unmodified polytriazine.

Claims: A method of preparing a rubber-modified cyanate ester compound comprising the step of: (a) making an emulsion that contains: 1) an emulsion polymerizable monomer selected from a vinyl aromatic monomer, an a,β-ethylenically unsaturated acid, an alkyl ester of an a,β-ethylenically unsaturated acid wherein the alkyl group has less than 4 carbon atoms, a hydroxyalkyl ester of an a,β-ethylenically unsaturated acid, an unsaturated nitrile, an epoxy funtional monomer, an unsaturated ester of an a,β-ethylenically unsaturated acid, and any mixture thereof, and 2) an aqueous rubber latex having a surfactant or emulsifier and rubber particles, which are 0.03 µm - 2 µm in diameter and are insoluble in a cyanate ester compound that contains at least one cyanate group. (b) polymerizing the emulsion from step (a) to form a colloidal dispersion of the rubber particles wherein essentially every rubber particles is grafted with the resulting polymer that is soluble in the cyanate ester compound, and (c) mixing the grafted rubber particles with the cyanate ester compound and forming a homogeneous dispersion of the rubber particles within the continuous phase of the cyanate ester compound. A rubber modified cyanate ester compound comprising (a) a discontinuous phase of grafted rubber particles which contain rubber particles that are 0,03 µm to 2 µm in diameter and are insoluble in the cyanate ester compound, that contains at least one cyanate group grafted with a polymer that is soluble in the cyanate ester compound and results from emulsion polymerization of monomers selected from a vinyl aromatic monomer, an a,β-ethylenically unsaturated acid, an alkyl ester of an a,β-ethylenically unsaturated acid wherein the alkyl group has less than 4 carbon atoms, a hydroxyalkyl ester of an a,β-ethylenically unsaturated acid, an unsaturated nitrile, an epoxy functional monomer, an unsaturated ester of an a,β-ethylenically unsaturated acid, and any mixture thereof homogenously dispersed within (b) a continous phase of a cyanate ester compound that contains at least on cyanate group. A rubber-modified polytriazine of a cyanate ester compound that contains at least one cyanate group comprising: (a) a discontinuous phase of grafted rubber particles that are 0.03 µm to 2 µm in diameter and are insoluble in the cyanate ester compounds from which the polytriazine is derived, where essentially every rubber particle is grafted with a polymer that is soluble in the cyanate ester compound from which the polytriazine is derived and results from emulsion polymerisation of monomers selected from a vinyl aromatic monomer, an a,β-ethylenically unsaturated acid, an alkyl ester of an a,β-ethylenically unsaturated acid wherein the alkyl group has less than 4 carbon atoms, a hydroxyalkyl ester of an a,β-ethylenically unsaturated acid, an unsaturated nitrile, an epoxy functional monomer, an unsaturated ester of an a,β-ethylenically unsaturated acid, and any mixture thereof homogenously dispersed within a (b) a continuous phase of a polytriazine. The method of claim 1 wherein the rubber-modified cyanate ester compound that contains at least one cyanate group is cured whereby a rubber modified polytriazine is formed. The rubber-modified compound of any of claims 2, 3 and the method of claim 1 and 4, wherein the cyanate ester compound is a difunctional or polyfunctional aromatic polycyanate. The rubber-modified compound of any of claims 2, 3, 5 and the method of claim 1 , 4 and 5 wherein the cyanate ester compound that contains at least one cyanate group is a copolymer of a cyanate ester compound that contains at least one cyanate group and a monomer having at least one cyanate-reactive functionality The rubber-modified compound of any of claims 2, 3, 5, 6 and the method of claims 1, and 4 wherein the rubber particles are selected from polybutadiene, styrene-butadienecopolymer, acrylate rubbers, neoprene, butyl rubbers, nitrile rubber, acrylonitile-butadien-styrene terpolymer,polyisoprene, ethylene-propylene copolymer fluoroelastomers and polymer from an alkyl ester of an a,β-ethylenically unsaturated monomer wherein the alkyl group has at least 4 carbon atoms. The rubber-modified compound of any of claims 2, 3, 5-7 and the method of claim 1 and 4 wherein the amount of grafted rubber particles dispersed in the continuous phase range from 0.1 to 30 percent by weight of the weight of the continuous phase.

Inventors: PICKELMAN DALE M, YANG PHILIP C, PICKELMAN, DALE M., YANG, PHILIP C.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1988
Main classification: C08G73
IPC codes: C08L51, C08L79, C08G18, C08F2, H05K1, C08F291, C08G73