Improved polyethylene modified asphalts

Abstract: Addition of linear polyethylene compounds to an asphalt having a specified minimum weight ratio of asphaltenes to saturates results in a composition which has enhanced storage stability and creep resistance relative to the unmodified asphalt. The composition is useful as a binder in paving materials and as a coating or saturant for roofing products.

Description: The present invention relates to an improved polyethylene modified asphaltic composition and its method of preparation. Asphalt is a bituminous material resulting from the distillation of crude oil. Typically, asphalt is derived from the bottoms of a vacuum distillation tower and has an atmospheric boiling point of at least 400°C. Because it is hydrophobic and has good adhesiveness and weatherability, asphalt has been used widely as a binder in paving materials and as a coating for roofing shingles. When used in roofing applications (e.g. a shingle coating or a saturant), the asphalt is usually polymerized by undergoing oxidative dehydrogenation in which the asphalt is contacted with an oxygen-containing gas (usually air) at temperatures ranging between about 200°C and about 300°C for between about 6 and about 24 hours. This procedure is described in detail by L. W. Corbett in Bituminous Materials: Asphalts, Tars and Pitches, Interscience Publishers, New York (1965) and by E. J. Barth in Asphalt Science and Technology, Gordon and Breach Science Publishers, New York (1968). Oxidative dehydrogenation improves the creep (i.e. flow) resistance and weatherability of the asphalt, and reduces its sensitivity to temperature changes. When used as a conventional paving binder, the asphalt does not usually undergo oxidative dehydrogenation, but rather, is manufactured to meet certain control specifications such as flash point (ASTM D-92), penetration at 25°C (ASTM D-5), apparent viscosity at 60°C (ASTM D-2171) and kinematic viscosity at 135°C (ASTM D-2170). In addition to the control specifications, a paving asphalt should also meet certain performance specifications such as ductility (ASTM D-113), solubility in trichloroethylene (ASTM D-2042), and thin film oven aging (ASTM D-1754). In the past, asphalts which met the above-mentioned control and performance specifications were generally considered more than adequate as paving binders. However, more recently, asphalt users have been demanding higher performance products. For example, today's increased heavy truck traffic volume is stressing and destroying roads. One of the major problems resulting from this increased traffic loading is pavement rutting due to the natural tendency of asphalt to creep over a period of time, particularly during the increased temperatures of summer. Therefore, road construction contractors are now in serious need of paving asphalt binders which have an increased resistance to creep. As a further example of the increasing demand for enhanced performance, low temperature cracking in roads and roofing products is still a major problem. Accordingly, a reduction of the temperature at which the product will crack (typically below about 0°C) would provide an additional benefit throughout the construction industry. A formulation with improved low temperature cracking properties would have higher tensile strength to resist the accumulated tensile stresses and reasonably similar or lower stiffness to minimize brittleness and fracture. One approach for changing or adjusting the rheological and chemical properties of asphalt is to incorporate certain additives therein. For example, a polymer such as polyethylene has been added to asphalt to produce asphalts which exhibit an increased resistance to creep or deformation. In addition, polyethylene modified asphalts must also have good compatibility between the asphalt and polyethylene, and be stable at high temperatures during storage and asphalt plant operation for ease of handling and application. Compatibility between the polyethylene and asphalt is very important to ensure that the engineering properties of both the asphalt and polyethylene are transferred to the finished product and to provide good long term performance. However, most polyethylene modified asphalts require either continuous mixing or the addition of various additives to avoid phase incompatibility (See for example U.S. Patents 4,240,946 and 4,314,921 which require continuous high shear mixing to obtain physical dispersion of a polyolefin in bitumen, and Jew et al., Journal of Applied Polymer Science, 31, pp. 2685-2704 (1986) which discloses the addition of one or more dispersants to a polyethylene modified asphalt to avoid phase separation. See also Transportation and Road Research Laboratory Report 1101 by Denning, J.H. et al., Highways and Structures Department, Crowthorne, Berkshire, England (1983). UK Patent 1,247,247 describes an asphaltene-free (or 'petrolene') asphalt composition which contains atactic polymer of polypropylene and/or polyethylene. By 'asphaltene-free' is meant that the asphalt composition contains less than 1.0 wt%, preferably less than 0.5 wt%, asphaltene. By 'atactic polymer' is meant a polymer which is substantially non-crystalline, i.e. which contain no more than 20 wt%, preferably less than 10 wt%, crystalline polymer. The atactic polymer, which is preferably atactic polypropylene, is added to the asphalt composition to improve its physical properties such as decreased temperature susceptibility and improved ductility and viscosity characteristics. Polyethylene has also been added to asphalt containing blends for other purposes. For example, European Patent Application 130,367 discloses thermoplastic moulding compounds which contain an ethylene copolymer having a vinyl ester and/or an alkyl ester, bitumen, carbon black, glyceryl monostearate, filler material and a second ethylene copolymer which is described as a linear low density polyethylene having a melt index from 0.1-10 g/10 mins. and a density between 0.918-0.935 g/cm³. The combination of the two ethylene copolymers with bitumen forms a bituminous moulding compound having high strength at room temperature, high dimensional stability under heat and rigidity. As another example, European Patent Application 64,630 discloses a flame retardant halogen-free thermoplastic moulding composition which contains ethylene copolymer, bitumen, aluminum hydroxide, red phosphorus, carbon black, glyceryl monostearate and, if necessary, polyethylene having a melt index of 0.1-10 g/10 min. and a density from 0.917 to 0.940 g/cm³. The dimensional stability of the mixture under heat is increased due to the polyethylene addition. Both patentees disclose that the moulding compounds formed are suitable for the preparation of moulded articles, particularly sealing widths for structural and civil engineering applications. In addition, both patentees use asphalt as a diluent rather than as a major component of the product. Accordingly, none of the foregoing references teach or suggest a polyethylene modified asphalt composition (and a method for making same) which does not require continuous mixing or addition of dispersants or other compounds to maintain phase compatibility of said composition. Now according to the present invention, it has been discovered that an asphaltic composition having improved phase stability and rheological properties can be produced by adding selected polyethylene compounds to certain asphalts. More specifically, an asphaltic composition having enhanced storage stability, phase compatibility and creep resistance relative to conventional asphalts (i.e. straight-run asphalts obtained as residua from vacuum distillation of crude oil) is formed when linear polyethylene compounds are added to an asphalt having a weight ratio of saturates to asphaltenes from 5.5:1 to 9:1. The resulting composition also has a higher tensile strength with relatively low stiffness at low temperatures compared to conventional asphalts and is particularly well suited for use as a paving binder and a coating or saturant for roofing products. In the present invention, an improved asphaltic composition is formed by the addition of at least one linear polyethylene compound to certain asphalts. The particular asphalt employed must be low in asphaltenes and relatively high in saturates to ensure satisfactory creep resistance, phase compatibility and storage stability of the polyethylene modified product. Storage stability is the more critical criteria to satisfy. Accordingly, the weight ratio of saturates to asphaltenes in the asphalt must be above about 5.5 (preferably above 5.7 and more preferably at least about 6) to avoid storage stability problems of the polyethylene modified product. The upper limit on the saturates/asphaltenes weight ratio is not critical and will vary depending on the particular application of the product formed. However, the ratio should be below that at which phase separation or loss of rheological properties will occur. Typically, the weight ratio should be below about 9. For paving binders and roofing applications, the weight ratio should preferably be between about 5.5 (preferably above 5.7) and about 8, more preferably between about 5.5 (preferably above 5.7) and about 7, as products resulting from using greater ratios would be too soft for such applications. The saturate/asphaltene weight ratio of the particular asphalt employed may be adjusted to the desired level by adding one or more feedstocks rich in saturates; e.g. a paraffin lube distillate. The asphalt used in the present invention may be obtained from a variety of sources including straight-run vacuum residue; mixtures of vacuum residue with diluents such as vacuum tower wash oil, paraffin distillate, aromatic and naphthenic oils and mixtures thereof; oxidized vacuum residues or oxidized mixtures of vacuum residues and diluent oils and the like. Other asphaltic materials such as coal tar pitch, rock asphalt and naturally occurring asphalt may also be used. Typically, the asphalt will have an atmospheric boiling point at least 380°C, more typically at least 440°C, and will comprise a major amount or portion of the asphaltic composition. In paving binder applications, the asphalt will typically comprise 85, preferably 90, wt.% or more of the resulting product. The asphalt will typically comprise 80, preferably 85, wt.% or more for roofing products. The particular polyethylene compound added must be linear polyethylenes; i.e., polyethylene compounds which are formed in the presence of a catalyst and which have minimal branching of carbon chains having more than ten carbon atoms. Branched polyethylenes cannot be suitably employed in the present invention as they will not result in the formation of a product having improved rheological and thermal properties. Linear polyethylenes which may be used in the present invention are high density, low density and very low density linear polyethylene compounds which may be characterized as follows: Linear Polyethylene Density, g/cm³ High Density Above 0.940 Low Density 0.915-0.940 Very Low Density Below 0.915 The minimum melt index of the particular linear polyethylene compound employed may vary broadly depending upon the saturates/asphaltenes weight ratio of the asphalt. More specifically, as the melt index of the polyethylene compound decreases, the saturates/asphaltenes weight ratio of the asphalt must be increased to maintain storage stability of the blended product. The melt index of the particular polyethylene compound employed will also vary depending upon the specific use of the asphaltic composition formed. In addition, practical considerations such as the amount of saturates rich feedstock available often dictate the melt index used. For typical paving applications, the minimum melt index should be at least about 6.7 for linear high density polyethylene (LHDPE) compounds, above 8 for linear low density polyethylene (LLDPE) compounds and at least about 3 for linear very low density polyethylene (LVLDPE) compounds. Similarly, there is essentially no upper limit on the melt index of the particular linear polyethylene compound employed because as melt index increases, the molecular weight of the polyethylene compound decreases, and there is less tendency for lower molecular weight compounds to cause phase separation due to asphaltene precipitation. The linear polyethylene compounds used can be in any convenient form (e.g. granular, pelletized, etc.) or shape, including irregularly shaped materials (e.g. reclaimed materials). A minimum of about 4 wt.% of the linear polyethylene compound must be added to the asphalt to obtain a modified asphalt blend which has creep resistance. The upper limit on the amount of linear polyethylene compound added is not critical and can range up to 25 wt.% or more based on weight of the asphalt, although lower amounts are preferred. Accordingly, the amount of linear polyethylene added will typically range from about 4 to about 25 wt.%, preferably from about 4 to about 15 wt.% and more preferably from about 4 to about 10 wt.%, based on weight of the asphalt. When used as a paving binder, the polyethylene modified asphalt of the present invention preferably contains from about 4 to about 8 wt.% linear polyethylene. When used for roofing applications, the polyethylene modified asphalt preferably contains from about 5 to about 15 wt.% linear polyethylenes. The particular linear polyethylene compounds employed in the present invention may be readily obtained in the marketplace from various chemical suppliers. Their method of preparation is well known to one skilled in the art and is described in Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd Edition, 16 , pp. 385-401, John Wiley & Sons, New York (1981) and "VLDPE - A New Class of Polyethylene", Plastics and Rubber International, 11 , No. 2, pp. 34-33 (1986). The asphalt may be mixed or blended with the linear polyethylene compounds in any number of ways which can readily be selected by one skilled in the art. Suitable means include external mixers, roll mills, internal mixers, Banbury mixers, screw extruders, augers and the like. Blending times can range broadly; i.e. from about 1 hour to about 8 hours or more. Typically, blending times of about 1 to about 4 hours will be employed. Similarly, the particular conditions at which the asphalt is blended with the linear polyethylene compounds are not critical. Typically, the blending will be performed at ambient pressure and at a temperature between about 150° and about 300°C, preferably between about 150° and about 230°C. The improved asphaltic composition of the present invention may be suitably employed in essentially any application requiring asphalt-based products with superior storage stability, phase compatibility and creep resistance. Examples of such applications include adhesives, coatings, fabricated products, road and roofing applications, sealants, sound and vibration dampening, water proofing membranes and the like. The composition, however, is particularly well suited for use as a paving binder and for roofing asphalt formulations. The present invention will be further understood by reference to the following Examples which are not intended to restrict the scope of the claims appended hereto. The accompanying Figures 1-4 are graphs showing the creep resistance of various asphalt compositions versus time. In the Examples, the storage stability, phase compatibility and creep resistance of the asphalts tested were measured as follows: Storage Stability A 200 gram sample is placed in a copper tube (254 mm (10 inches) high and 25.4 mm (1 inch) in diameter) and heated at 160°C for 5 days. Then the sample is removed from the tube and divided into top and bottom fractions. The viscosity of each fraction is measured at 135°C. The ratio of the top over the bottom viscosity at 135°C is then calculated. A ratio of 0.90 to 1.1 is preferred; 0.8-0.9 and 1.1-1.2 is borderline; and less than 0.8 or more than 1.2 is a failure. Phase Compatibility A thin film of the sample is spread on a microscope slide and heated at 100°C for 4 hours. Slides containing the heated and unheated sample are then examined under an optical microscope at 260 power. If there is no change in surface morphology, the blend is compatible. If phase separation is noted or a significant change occurs in surface morphology, then the blend is incompatible. Creep Resistance The sliding plate rheometer is used to measure the creep resistance and shear of the asphalts tested over a continuous range of loading times following the procedure set forth by Fenijn and Krooshof in "Proceedings of CTAA", Winnipeg, Canada, November 1970, the disclosure of which is incorporated herein by reference. In the Examples, data was obtained at 40°C (and at 20°C as well in Examples 1 and 2) since asphalt pavement will be prone to rutting under heavy loads at this temperature. From these data, creep resistance was plotted against time to show the creep behavior of the composition with time. If the composition creeps or flows with time, the curve will slope upwards. If the composition has good flow resistance, the curve will tend to become horizontal and flatten or plateau. Example 1 - Preparation of Asphalt Blends The compositions of various asphalt blends were calculated mathematically using an unmodified or conventional asphalt (i.e. a straight-run asphalt obtained as a residue from the vacuum distillation of crude oil which has not been modified by polyethylene addition) and a paraffin lube distillate (PLD) having the following compositions as measured by ASTM D-4124: Composition, wt.% Asphalt PLD Asphaltenes 3.8 0.0 Polar Aromatics 39.7 12.8 Naphthene Aromatics 39.8 35.7 Saturates 16.7 51.5 The compositions of the particular asphalts blended are shown in Table 1. The blended compositions were not measured using ASTM D-4124 because the test is not sufficiently precise to determine each fraction of the blend. Consequently, blends with different compositions can result in saturates/asphaltenes weight ratios which overlap. The mathematical calculation of the saturates/asphaltenes weight ratios provides a practical guideline by which asphalts of differing saturates/asphaltenes weight ratios can be differentiated. Example 2 - LLDPE Modified Asphalt is Superior to Unmodified Asphalt. 25.5 grams of linear low density polyethylene having a 20 melt index (M.I.) were blended with 485.2 grams of 435 cSt/100°C asphalt containing 82.4 grams of paraffinic lube distillate. The final concentration of the LLDPE in the modified asphalt was 5.0%. The blending operation was performed at 190°C for two hours in a baffled autoclave equipped with a stirrer rotating at 1750 rpm. Properties of the LLDPE modified paving binder were determined as were the corresponding properties of a unmodified asphalt paving binder. The results are summarized in Table 2 and shown in Figure 1. Table 2 shows that the linear low density polyethylene modified asphalt has superior creep resistance relative to an unmodified asphalt (also see Figure 1) as well as comparable storage stability and phase compatibility. Table 2 also shows that the viscosity at 60°C increases significantly compared to the unmodified asphalt, whereas the viscosity at 135°C is not increased significantly relative to that of the unmodified asphalt. Example 3 - LLDPE Modified Asphalt Is Superior to Low Density Polyethylene Modified Asphalt A linear low density polyethylene modified product was prepared by blending 42.0 grams of linear low density polyethylene having a 12 melt index with 797.6 grams of 435 cSt/100°C asphalt which contained 82.4 grams of paraffinic lube distillate. A branched low density polyethylene modified product was prepared by blending 28.6 grams of low density polyethylene having a 12 melt index with 544.0 grams of a 435 cSt/100°C asphalt which contained 82.4 grams of paraffinic lube distillate. Each blend was prepared in the same manner at 190°C for two hours in a baffled autoclave equipped with a stirrer rotating at 1750 rpm, and had a final polyethylene concentration of 5%. The properties of the products measured are summarized in Table 3, with the creep for each product being shown in Figure 2 along with that of the unmodified asphalt from Example 2. The results in Table 3 show that the linear low density polyethylene product had excellent creep resistance, phase compatibility and high temperature storage stability. Although the low density polyethylene modified asphalt had good storage stability, it had poor creep resistance and poor phase compatibility. Example 4 - Determination of Minimum Melt Index of LLDPE at the Same Saturates/Asphaltenes Weight Ratio Blends of 1, 3.3, 4.5, 20 and 50 melt index linear low density polyethylene modified asphalts having a saturates/asphaltenes weight ratio of 7.1 were prepared using the same feedstock and blending conditions as in Example 2. The properties of the products measured are summarized in Table 4, with the creep for each product being shown in Figure 3 along with that of the unmodified asphalt from Example 2. The results in Table 4 show linear low density polyethylenes having a melt index below 4.5 do not form blends with acceptable storage stability at the same saturates/asphaltenes weight ratio. Example 5 - Variation of LVLDPE Melt Index with Saturates/Asphaltenes Weight Ratio Blends of 1, 2 and 3.3 melt index linear very low density polyethylene modified asphalts were prepared using the same blending conditions as in Example 2. The feedstocks were prepared to give saturates/asphaltene weight ratios of 5.6, 6.3, 7.1 and 8.7 as described and shown in Example 1. The properties of the products measured are summarized in Table 5. The results in Table 5 show that as the melt index of linear very low density polyethylene decreases below about 3, the saturates/asphaltenes weight ratio must increase for the blends to have acceptable storage stability. Example 6 - Variation of LLDPE Melt Index with Saturates/Asphaltenes Weight Ratio Blends of 1, 3.3, 4.5 and 8 melt index linear low density polyethylene modified asphalts were prepared using the same blending conditions as in Example 2. The feedstocks were prepared to give saturates/asphaltenes weight ratios of 8.7, 7.1, 6.3 and 5.6 as described and shown in Example 1. The properties of the products measured are summarized in Table 6. The results in Table 6 show that as the melt index of linear low density polyethylene decreases below about 8 (progressing from 4.5, 3.3 to 1), the saturates/asphaltenes weight ratio must increase for the blends to have acceptable storage stability. Example 7 - Variation of LHDPE Melt Index with Saturates/Asphaltenes Weight Ratio Blends of 6.7, 15 and 19 melt index linear high density polyethylene modified asphalts were prepared using the same blending conditions as in Example 2. The feedstocks were prepared to give saturates/asphaltenes weight ratios of 5.6, 6.3, 7.1 and 8.7 as described and shown in Example 1. The properties of the products measured are summarized in Table 7. The results in Table 7 show that as the melt index of linear high density polyethylene decreases, the saturates/asphaltenes weight ratio must be increased to give acceptable storage stability. Example 8 - Minimum Melt Index Varies with Density of Linear Polyethylene at the Same Saturates/Asphaltenes Weight Ratio Various linear polyethylene modified asphalts having a saturates/asphaltenes weight ratio of 7.1 were prepared using the same feedstock and blending conditions as in Example 2, except that linear polyethylenes of varying density and melt indexes were used. The product inspections measured are summarized in Table 8, with the creep of each product being shown in Figure 4 along with that of the unmodified asphalt from Example 2. Example 8 demonstrates that for asphalts having the same saturates/asphaltenes weight ratio, as the density of linear polyethylene decreases, the minimum melt index which will give acceptable storage stability also decreases.

Claims: An asphalt composition comprising: (a) 75-96 wt% asphalt, optionally blended with one or more feedstocks rich in saturates, which asphalt or asphalt blend has a weight ratio of saturates to asphaltenes of from 5.5:1 to 9:1; and (b) 4 to 25 wt% of at least one linear polyethylene, the weight percentages being based on the total weight of the composition. A composition according to claim 1 where the said saturates to asphaltenes ratio is from 5.5:1 to 8:1. A composition according to claim 1 wherein the said saturates to asphaltenes ratio is from 5.7:1 to 8:1. A composition according to any preceding claim wherein the amount of linear polyethylene is from 4 to 15 wt%. A composition according to any of claims 1 to 3 wherein the amount of linear polyethylene is from 4 to 8 wt%. A composition according to any of claims 1 to 3 wherein the amount of linear polyethylene is from 5 to 15 wt%. A composition according to any preceding claim wherein the linear polyethylene is selected from linear very low density polyethylene having a density below 0.915 g/cm³, linear low density polyethylene having a density from 0.915 to 0.940 g/cm³, linear high density polyethylene having density above 0.940 g/cm³, and mixtures thereof. A composition according to claim 7 wherein the linear very low density polyethylene has a melt index of at least about 3g/10 minutes, the linear low density polyethylene has a melt index of at least about 8g/10 minutes, and the linear high density polyethylene has a melt index of at least about 6.7g/10 minutes. A composition according to any preceding claim wherein the said feedstock rich in saturates is a paraffin lube distillate. Use of linear polyethylene in an asphalt composition having a saturates to asphaltenes weight ratio of from 5.5:1 to 9:1 to provide improved storage stability of the asphalt composition. Use of linear polyethylene in an asphalt composition having a saturates to asphaltenes weight ratio of from 5.5:1 to 9:1 to provide improved creep resistance of the asphalt composition. The use according to claim 10 or 11 wherein the linear polyethylene and the asphalt are as claimed in any of claims 1 to 9.

Inventors: MORAN LYLE EDWIN, MORAN, LYLE EDWIN
Applicants: EXXON RESEARCH ENGINEERING CO, EXXON RESEARCH AND ENGINEERING COMPANY
Application year: 1988
Main classification: C08L95
IPC codes: C08L95