DECORATIVE ARTICLE AND PROCESS FOR MAKING THE SAME

Abstract: A decorative article (10) is made by a process in which a controlled-flatness substrate (20) having an effective edge (16) in a closed pattern on its surface receives a fluent plastic composition which is cast into an area (18) defined by the edge (16). The fluent plastic flows to the effective edge (16) and is then cured to form a clear plastic cap (14). During casting and curing the substrate (12) is held flat and horizontal by reason of its being releasably adhered to a flat, smooth-surfaced, stiff release liner. The resulting decorative article is free of optical distortions and may be used as a covering, preferably for an elongated automotive component such as an external vertical pillar (24) between the passenger compartments of an automobile.

Description: The present invention relates to a process for making generally decorative articles having a lens cap thereon and to the articles made by this process. More particularly, it relates to a process and article in which a fluent plastic composition is cast onto a controlled-flatness substrate so as to produce a decorative article which is free of optical distortions. Trim strips of various configurations and decorative articles and emblems have been used in the automotive industry to decorate and protect automobile body surfaces, and other surfaces in the passenger compartment. In recent years, emphasis has been placed on the use of plastic trim strips which do not corrode and which can be adhesively attached to the automobile body without fasteners. One such trim strip is shown in U.S. Patent No. 4,446,179, issued May 1, 1984, to Waugh and assigned to us Waugh discloses a decorative trim strip which may consist of an elongate decorative foil member having thereon an impact-resistant overlay having radiused edges and providing a lens effect to the foil member. An adhesive is used to bond the trim strip to the surface to be decorated. Another trim strip is shown in U.S. Patent No. 4,560,596, issued December 24, 1985, to Coscia, and also assigned to the assignee of the present invention. Coscia discloses a trim strip which includes a foil member whose upper surface is provided with a decorative pattern. The upper surface is partially covered by a weather-resistant and impact-resistant plastic overlay having radiused edges and providing a lens effect to the foil member. The plastic overlay section of the foil member is essentially coextensive with the width of the automotive body component to be decorated. When the trim strip is applied to the body component, the uncovered end portions of the foil member are wrapped around the component. In the processes of Waugh and Coscia the substrate is held flat and horizontal, preferably by vacuum hold-down, during casting and curing of the plastic overlay or lens cap. Recently, interest has arisen in utilizing decorative articles to cover large, irregularly shaped surface areas and components on an automobile. Previously, trim strips of the type shown in the Waugh and Coscia patents have been of a constant width and shape. This facilitates uniform casting of a fluent plastic composition onto the foil member prior to curing the composition to form the plastic overlay. When a decorative article which varies in width or shape is to be produced by casting a fluent plastic composition onto a substrate, ensuring that proper amounts of the composition are deposited on all portions of the substrate is important. One technique which has been used in the past to cast a fluent composition on a substrate in an irregular pattern is disclosed in U.S. Patent No. 4,409,264, issued October 11, 1983, to Gilleo et al, and U.S. Patent No. 4,468,425, issued August 28, 1984, to Gilleo et al. The Gilleo et al patents suggest that an irregularly shaped area defined by a pattern of a low surface energy compound, such as a fluorochemical, printed on the substrate surface, can receive a quantity of a liquid resin. The substrate is then wobbled or tipped in various directions, causing the liquid resin to flow over the irregularly shaped area to the area boundaries. While this may be an acceptable technique to use with some area shapes. it is not effective when the area to be covered with a fluent composition is significantly elongated. Our EP application No.88302027.3 (EP-A-0282271) provides for an improved process for making a decorative article in which an elongate substrate area of varying width or shape is cast with a fluent plastic composition and cured to form a clear plastic lens cap. As with the Waugh and Coscia processes discussed above, the substrate is held substantially flat and horizontal. preferably by vacuum hold-down, during the casting and curing process. However, it has been found that in some instances optical distortions occur in the decorative articles produced by such processes. The optical distortions. which can be described as an "orange peel" appearance, occur primarily in large area decorative trim strips having elongate areas of varying width or shape which are conformed to an automobile body component such as the verticle pillars located just to the rear of the front doors of many passenger automobiles. Such pillars are known in the industry as "B-pillars" and "C-pillars". It has become fashionable for the covering, paint, or coating on B-pillars and C-pillars to have a smooth glass-like luster. The use of decorative articles having a lens cap as described in Waugh, Coscia and our EP-A-0282271 are particularly well suited as a covering for B-pillars and C-pillars because ot the lens effect which optically enhances the surface beneath the lens cap. But, this is only true to the extent that there are no optical distortions in that covering. Accordingly, the need exists for an improved process for making a decorative article in which a controlled-flatness substrate is cast with a fluent plastic composition to produce an elongate decorative article which is free of optical distortions. A process according to the present invention for making decorative articles comprises: a) providing a flexible substrate of approximately 0.005 to 0.025 cm (0.002 to 0.010 inch) thick vinyl having a first surface and a second surface, said flexible substrate being produced by casting vinyl plastisol on a smooth surface so as to produce a smooth cast-side surface as said first surface and an air-side surface as said second surface, said substrate being releasably adhered with an approximately 0.005 to 0.013 cm (0.002 to 0.005 inch) thick layer of pressure sensitive adhesive by said first surface thereof to a flat smooth-surfaced, stiff release liner, and said substrate having an effective edge in a closed pattern on said second surface thereof, which edge circumscribes an area on said surface; b) casting a fluent plastics composition from a casting head onto said second surface of said substrate within said area while said substrate is adhered to said release liner and held flat and horizontal whereby said flat, smooth-surfaced, stiff release liner maintains said substrate flat and smooth during casting and subsequent curing of said fluent plastics composition; and c) curing said plastics composition to form a clear plastics cap which optically enhances the appearance of said substrate as viewed through said clear plastics cap. The flatness of the substrate is controlled in part by the type of release liner to which it is releasably adhered. That release liner is a flat, smooth-surfaced, stiff one such as a stiff plastics member which will maintain the surface of the substrate to which it is adhered flat and smooth during casting and curing. No vacuum or adhesive hold-down is used. To the contrary, it has been found desirable to avoid such hold-down methods if the substrate is to be maintained as flat and horizontal as possible during casting and curing and thereby avoid induced distortions. Rather, the release liner is the principal means for holding the substrate flat and horizontal during casting and curing. Preferably, the release liner is a polyester sheet, such as a Mylar polyethylene terephthalate sheet, having a thickness of approximately 0.018 to 0.030 cm (0.007 to 0.012 inch), and having a smooth silicone resin treatment on the release surface thereof. The flatness of the substrate is also controlled by the particular type of substrate used and its method of manufacture. That is, the substrate, which is a vinyl sheet such as polyvinyl chloride sheet, has a thickness of approximately 0.005 to 0.025 cm (0.002 to 0.010 inch), most preferably 0.008 cm (0.003 inch). The vinyl sheet is produced by casting a vinyl plastisol on a smooth mold surface, such as a smooth plastics or metal mold surface, so that the as-cast vinyl sheet has a first surface which is a smooth "cast-side" surface when it is removed from the mold surface. The second surface, or "air" surface, tends not to be as smooth as the first cast-side surface. It is the second, not-so-smooth, air surface, of the vinyl sheet onto which the fluent plastics of the lens cap is cast. Surprisingly, it has been found that using the not-so-smooth surface of the vinyl substrate as the decorative surface over which the lens cap is placed does not lead to optical distortions when that surface is viewed through the lens cap, but rather minimizes such distortions. That is, it has been found that the fluent plastics is self-leveling in that it smooths over the not-so-smooth surface, fills the rough areas and voids, and when cured produces an optically effective lens cap. On the other hand, it has been found that the smoothness of the first surface (i.e., the one bearing the adhesive) which is to be adjacent to the automobile body is a key to avoiding optical distortions. Evidently, when a decorative article of the present type has a rough adhesive bearing surface and is applied to an intended base such as the "B-pillar" or "C-pillar" of an automobile, the pressure used in applying the decorative article may cause the underside roughness to be observed through the lens cap. An "orange peel" appearance often results. But, if the first, cast-side, surface is used as the adhesive bearing surface, and a relatively thick adhesive layer is used, then, no such optical distortions occur. The smooth first surface of the vinyl substrate maintains its smoothness and the relatively thick adhesive helps cover over any imperfections in the component of the automobile body to which the decorative article is attached. The adhesive is a pressure sensitive adhesive having a thickness of approximately 0.005 to 0.013 cm (0.002 to 0.005 inch), and most preferably 0.008 cm (0.003 inch). As mentioned, the substrate has an effective edge which circumscribes preferably an elongate area on the second surface of the substrate. By elongate, is meant either horizontally elongate or vertically elongate. That is, the elongate area generally has a greater length or height, depending on whether it is horizontally or vertically elongate, than width. The effective edge may be formed by a coating of an essentially non-wettable material which is peripherally contiguous with the elongate area over which the lens cap is to be applied. The clear plastics lens cap may be formed of a flexible, abrasion resistant plastics such as polyurethane. The fluent plastics is cast over the elongate area, flows to the effective edge of the area, and forms a positive meniscus. The casting head may be a programmed articulated head, or a series of heads which are manipulated in conjunction with one another as disclosed in our EP-A-0282271. The casting head may be stationary and the substrate may be moved therebeneath. The rate of relative movement between the substrate and the casting head may be substantially constant and the fluent plastics composition may be dispensed from the casting head at a varying rate in dependence upon the width of the area. The rate of relative movement between the substrate and the casting head may vary in dependence upon the width of the area with the fluent plastics composition being dispensed from the casting head at a substantially constant rate. A decorative article according to the present invention for covering an automotive component, comprises: a flexible substrate of approximately 0.005 to 0.025 cm (0.002 to 0.010 inch) thick vinyl, having a first surface and a second surface, said flexible substrate being produced by casting vinyl plastisol on a smooth surface so as to produce a smooth cast-side surface as said first surface and an air-side surface as said second surface; an essentially non-wettable material forming a closed edge pattern on said substrate, said edge pattern circumscribing an area on said second surface of said substrate and defining a margin area of generally uniform dimension surrounding said area; a cured clear plastics cap within said area on said second surface of said substrate which enhances the appearance of said substrate as viewed through said clear plastics cap; and means for mounting the article on said automotive component to provide a decorative covering therefore, with said margin area being wrapped around the edges of said component, said means for mounting including an approximately 0.005 to 0.013 cm (0.002 to 0.005 inch) thick layer of pressure sensitive adhesive on said first surface of said substrate. The vinyl material may have a decorative uniform color, a decorative colored pattern, or may have indicia printed thereon. The cured, clear plastics cap within the elongate area on the substrate enhances the appearance of the substrate as viewed through the cap. Even when mounted, the decorative article of the present invention remains optically distortion free. In order that the invention may be more readily understood, reference will now be made by example to the accompanying drawings in which: Fig. 1 is a top view of a decorative article constructed according to an embodiment of the present invention; Fig. 2 is an enlarged end view of the decorative article, as seen looking right to left in Fig. 1; Fig. 3 is a sectional view, illustrating the decorative article as it is applied to an automotive component. Reference is made to Figs. 1-3 which illustrate a decorative article 10 embodying the present invention. This article comprises a flexible substrate 12 upon which is mounted a cured, clear plastics cap 14. The clear plastics cap 14, approximately 0.127 cm (50 mils) in thickness, provides a lens effect over the substrate 12. This enhances the appearance of any design or other ornamentation which may be provided on the surface of the substrate beneath the clear plastics cap 14. Additionally, it has been found that the clear plastics cap 14 provides an enhanced appearance for the article even if the surface of flexible substrate 12 is devoid of design or ornamentation, but rather is uniformly coloured. The flexible substrate 12 is a vinyl sheet, which may be metallized, having a thickness of approximately 0.005 to 0.025 cm (0.002 to 0.010 inch), and most preferred is an approximately 0.008 cm (0.003 inch) black polyvinyl chloride sheet from 3M of St. Paul, Minnesota, USA. Such vinyl sheets are manufactured by casting a black tinted polyvinyl chloride plastisol on a smooth polyester mold surface and curing. When the cured vinyl sheet is removed from the mold surface, it has a first, "cast-side", surface which is smooth, and a second, "air-side", surface which is less smooth. The flexible substrate 12 is, then, adhered to a flat, smooth-surfaced, stiff release liner (not shown) by use of adhesive layer 22. A 0.005 to 0.013 cm (0.002 to 0.005 inch) thick layer of pressure sensitive adhesive, such as one of the pressure sensitive acrylic adhesives from 3M of St. Paul, Minnesota, USA., and most preferably 0.008 cm (0.003 inch) thick pressure sensitive adhesive is cast on a 0.018 to 0.030 cm (0.007 to 0.012 inch) thick silicone treated polyester release liner. Most preferred is a 0.008 cm (0.003 inch) thick pressure sensitive adhesive and a 0.018 cm (0.007 inch) thick silicone treated Mylar polyethylene terephthalate release liner. After the vinyl sheet is stripped from its mold surface, it is "laminated" to the adhesive bearing release liner with the first, cast-side, surface being pressed against the pressure sensitive adhesive. This places the smooth side of the vinyl sheet face to face with the smooth side of the release liner with a relatively thick layer of adhesive therebetween. The resulting laminated assembly is then sheared to a size approximate for the decorative article being produced. As mentioned, the preferred decorative article is one for covering a elongate automobile component such as a "B-pillar" or "C-pillar". Such decorative articles preferably have the wrap-around edge feature of the type disclosed in Coscia U.S. Patent No. 4,560,596 and our EP-A-0282271. That wrap-around feature is shown in Figs. 1-3 where there is shown an elongate area 18 and a margin area 20. Other decorative articles of different shapes may also be produced by the present process. The clear plastic cap 14 is formed by casting a fluent plastics composition in elongated area 18 on the upper surface of flexible substrate 12, which is the second, air-side surface of the vinyl sheet. To retain the fluent plastics composition in the desired position during the casting operation and during subsequent curing, an essentially non-wettable material 16 forming a closed edge pattern is provided on flexible substrate 12. The thickness of material 16 is exaggerated in Figs. 2 and 3 for purposes of clarity. The edge pattern circumscribes an elongate area 18 on the substrate and defines a margin area 20 of generally uniform dimension surrounding the elongate area 18. In the embodiment shown in Figs. 1-3, elongate area 18 increases in width from one end thereof to the other end. The essentially non-wettable material 16 may be any one of a number of materials which are known to limit the flow of a fluent plastics composition over a substrate surface, such as various fluorinated polymers. A number of suitable materials are discussed in U.S. Patent No. 4,409,264. Preferred is a mixture of 50% polytetrofluorethylene, 45% solvents, and 5% fillers, binders, and pigments. After application, non-wettable material 16 is allowed to dry for one hour or more. Alternatively, an effective edge to preclude the flow of the fluent composition over the substrate surface may be provided by means of a ridge which is mechanically embossed or otherwise formed in flexible substrate 12. The cast plastics composition forming the clear plastics cap 14 is a thermosetting material which is weather-resistant and does not yellow or cloud as a result of prolonged exposure to sunlight and which withstands strong detergent. The cast plastics should also be resistant to abrasion and impact. A number of plastics can be used for this purpose, but one which is particularly advantageous because it satisfies all of the above needs is an impact-resistant polyurethane of the type disclosed in Waugh U.S. Patent No. 4,446,179 and Coscia U.S. Patent No. 4,560,596. Other plastics, such as acrylics and epoxies also may be used. The plastics composition preferably is cured by heat or ultraviolet radiation, most preferably by convection heating at 43.3 to 65.6°C (110° to 150°F). Depending on the plastics used, other means such as R.F. heating and air drying may be used to harden the plastics material. During casting and curing, flexible substrate 12 is held flat and horizontal by reason of the fact that during this stage of the process it is releasably adhered to the flat, smooth-surfaced, stiff release liner. That assembly is transported on a flat, smooth, level carrier through the casting station, and then curing oven, to an unloading station. Preferably, no vacuum platens, adhesive or other hold-down means, are used during either casting or curing. Following unloading, the decorative article may be further die cut to a finished geometry, if necessary. It is, then, shipped, still on the release liner to the user, such as the automobile parts or assembly plant. There, the decorative article is removed from the release liner and mounted on the elongate automotive component. Fig. 3 depicts the decorative article 10 mounted on an elongate automotive component 24 which may, for example, be the external vertical pillar which is just to the rear of the front doors of many passenger automobiles. It should be noted that the margin area 20 overlaps the edges of the component 24, providing a neat appearance and facilitating the application of decorative article 10 to the component.

Claims: A process for making decorative articles (10), comprising: a) providing a flexible substrate (12) of approximately 0.005 to 0.025 cm (0.002 to 0.010 inch) thick vinyl having a first surface and a second surface, said flexible substrate (12) being produced by casting vinyl plastisol on a smooth surface so as to produce a smooth cast-side surface as said first surface and an air-side surface as said second surface, said substrate being releasably adhered with an approximately 0.005 to 0.013 cm (0.002 to 0.005 inch) thick layer of pressure sensitive adhesive (22) by said first surface thereof to a flat smooth-surfaced, stiff release liner, and said substrate having an effective edge (16) in a closed pattern on said second surface thereof, which edge circumscribes an area (18) on said surface; b) casting a fluent plastics composition from a casting head onto said second surface of said substrate (12) within said area (18) while said substrate is adhered to said release liner and held flat and horizontal whereby said flat, smooth-surfaced, stiff release liner maintains said substrate flat and smooth during casting and subsequent curing of said fluent plastics composition; and c) curing said plastics composition to form a clear plastics cap (14) which optically enhances the appearance of said substrate (12) as viewed through said clear plastics cap (14). A process as claimed in claim 1, which includes forming said edge (16) by a coating of an essentially non-wettable material in a pattern which is peripherally contiguous with an elongate area (18). A process as claimed in claim 1 or 2, wherein said release liner is a stiff plastics member. A process as claimed in claim 3, wherein said release liner is a polyester sheet having a thickness of approximately 0.018 to 0.030 cm (0.007 to 0.012 inch.) A process as claimed in claim 3 or 4, which includes treating said release liner with silicone resin. A process as claimed in any preceding claim, wherein said release liner is a silicone resin-treated polyester sheet and said pressure sensitive adhesive is a 0.008 cm (0.003 inch) thick layer which has been cast onto said silicone resin-treated polyester sheet. A process as claimed in any preceding claim, which includes forming said clear plastics cap (14) of a flexible, abrasion-resistant polyurethane. A decorative article (10) for covering an elongated automotive component (24), comprising: a flexible substrate (12) of approximately 0.005 to 0.025 cm (0.002 to 0.010 inch) thick vinyl, having a first surface and a second surface, said flexible substrate (12) being produced by casting vinyl plastisol on a smooth surface so as to produce a smooth cast-side surface as said first surface and an air-side surface as said second surface; an essentially non-wettable material forming a closed edge pattern (16) on said substrate, said edge pattern circumscribing an area (18) on said second surface of said substrate and defining a margin area (20) of generally uniform dimension surrounding said area (18); a cured clear plastics cap (14) within said area (18) on said second surface of said substrate (12) which enhances the appearance of said substrate (12) as viewed through said clear plastics cap (14); and means for mounting the article on said automotive component (24) to provide a decorative covering therefore, with said margin area (20) being wrapped around the edges of said component (24), said means for mounting including an approximately 0.005 to 0.013 cm (0.002 to 0.005 inch) thick layer of pressure sensitive adhesive (22) on said first surface of said substrate (12). An article as claimed in claim 8, wherein said vinyl substrate is of uniform color. An article as claimed in claim 8 or 9, wherein said area (18) is elongate and increases in width from one end thereof to the other end. An article as claimed in claim 8, 9 or 10, wherein said clear plastics cap (14) is formed of a flexible, abrasion-resistant polyurethane.

Inventors: COSCIA, CHARLES M., FIELDER, WILLIAM A.
Applicants: THE D.L.AULD COMPANY
Application year: 1988
Main classification: B44C1
IPC codes: B44C3, B05D1, B44C5, B44C1, B60R13, B32B27, B29D11, B29L31, B29C39, B44F1