COMPOSITE FABRIC STRUCTURES

Abstract: A flexible, impermeable, universally chemically resistant composite structure (10) which may be fabricated into protective clothing useful, for example, in the handling and clean up of hazardous chemicals is provided for, which composite structure (10) comprises a fabric substrate (11), and thermally-melt-bonded on both sides thereof, a coated film (12), which coated film comprises a PTFE film (13) having a thermoplastic fluoropolymer coating (14) on both sides thereof. Preferably, the fabric substrate (11) of the composite structure (10) has been treated with an antiwicking agent. A method for forming such composite structures is provided for, which method comprises thermally-melt-bonding a PTFE film (13) having a thermoplastic fluoropolymer coating (14) on both sides thereof to each side of a fabric substrate (11). Articles of protective clothing are also provided for which are fabricated from the subject composite structures.

Description: This invention is related to composite structures suitable for use in protective clothing. More particularly, it is directed to flexible, impermeable, universally chemically resistant composite structures which may be fabricated into protective clothing useful, for example, in the handling and cleanup of hazardous chemicals. Polytetrafluoroethylene (PTFE) is widely regarded as one of the most universally chemically resistant chemical compounds. PTFE films are manufactured by special techniques well-known in the art, such as molding-skinning, and are commercially available. They are not well-suited, however, for use in fabricating protective clothing. Such films tear easily, and accordingly, often are damaged as they are fabricated into clothing. In handling chemicals or cleaning up spills, a person typically encounters a variety of tools and other objects with sharp or protruding edges. In other words, protective clothing must be capable of withstanding considerable wear and tear and fairly rough use, and PTFE films simply are not durable enough. Increasing the thickness of the PTFE film, while increasing the tensile strength of the film, is an inadequate solution because the natural stiffness of PTFE makes the film less flexible and introduces problems, especially splitting, during fabrication and wear of protective clothing. Accordingly, PTFE films frequently are applied to both sides of a fabric substrate, such as a woven polyaramide or polyamide fabric. The resulting composite structure is more rugged than PTFE films alone. The fabric substrate acts to reinforce the PTFE film. Thinner PTFE films generally may be used, and thus, problems associated with stiffness of the film, although not eliminated, are reduced. Moreover, if the exterior PTFE film is punctured, the fabric substrate may be capable of preventing the puncture of the inner PTFE film, preserving the structural integrity of the barrier as a whole. Such composite structures, however, are far from perfect. PTFE films are not self-adhering to fabric substrates. They also adhere poorly to most conventional adhesives, and in fact, Teflon® PTFE material sold by DuPont de Nemours, E.I. & Co., Inc., Wilmington, Delaware, is widely used as a coating to prevent sticking of adhesives to machine rolls and parts. The surface of the PTFE film, however, may be chemically-etched to permit the use of some high-performance adhesives, such as epoxy and acrylic adhesives. Unfortunately, being subject to a variety of mechanical forces, adhesives often permit separation of the PTFE film from the fabric substrate during fabrication and use of the protective clothing. This problem is exacerbated if the outer PTFE film has split or has been punctured, thereby permitting potentially deleterious chemicals to penetrate the composite structure and destroy the adhesive. Alternately, the PTFE film may be formed on the fabric substrate by successive coatings of PTFE emulsions. An excessive amount of PTFE, however, is required to produce an effective, pin-hole free chemical barrier, and the resulting composite structures typically are heavy and stiff. Moreover, if the outer PTFE film is split or punctured and chemicals penetrate into the fabric substrate, many chemicals tend to wick through the fabric substrate and contaminate areas removed from the point of penetration. If the garment is to be repaired, larger portions of the composite material must be replaced, thereby increasing the cost of the repair and compromising unnecessarily the structural integrity of the garment. Conventional antiwicking agents typically are not universal in their action. For example, silicone based antiwicking agents resist wicking of aqueous solutions, but not of organic solvents. Other antiwicking agents suffer the additional defect of having to be applied in amounts that create unacceptable stiffness. It is also important, of course, that the effectiveness of the barrier not be compromised at the seams of the garments. In many applications, sewn seams are preferred because of their strength, but in sewing, holes are made in the barrier which are not leak-proof until sealed. A number of approaches to sealing seam holes are utilized by workers in the art. Rubber, self-sealing tape can be placed between the portions to be sewn together whereby the self-sealing tape provides the primary seal in the seam holes. Alternately, a rubber sealant can be applied over the stitching to fill the holes. Yet another approach is to cover one or both sides of the seam with a heat-sealable tape consisting of a PTFE film coated on one side with an adhesive, such as silicone, or a thermoplastic fluoropolymer, such as fluorinated ethylene/propylene copolymers (FEP). Self-sealing tape, rubber sealants, and silicone adhesives, however, are not sufficiently chemically resistant, and when sealants or heat-sealable tape is used, additional processing steps must be used in fabricating protective clothing. The subject invention, therefore, is directed to composite structures and garments produced therefrom in which a PTFE barrier is securely adhered to a fabric substrate in a manner such that the composite structure may not only be successfully fabricated into garments with a low incidence of tearing or damage, but also such that the composite structure maintains its integrity during the life of the garment. It is also directed to composite structures and garments produced therefrom which provide light, flexible, universally chemically resistant barriers. It is directed further to composite structures and garments produced therefrom, the seams of which may be more efficiently formed and sealed and in such a manner as to provide a durable seal. Finally, the subject invention is directed to composite structures wherein the wicking of chemicals accidentally coming into contact with the fabric substrate is minimized, and wherein the anti-wicking agent is more universally effective and does not decrease significantly the flexibility of the composite structure. EP-A-0202996 discloses a fire and chemical resistant flexible composite made from flexible woven, non-woven or knitted substrates and fluoropolymer films. A layer of melt adhesive may be applied to the outer surface of the substrate. The subject invention provides a composite structure suitable for use as material for articles of protective clothing, which composite structure comprises a fabric substrate treated with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant, and thermally-melt-bonded on both sides of the substrate, a coated film, which coated film comprises a PTFE film having a thermoplastic fluoropolymer coating on at least the inner side thereof. The subject invention also provides for such a composite structure in which the coated film comprises a PTFE film having a thermoplastic fluoropolymer coating on both sides thereof. The subject invention also provides a composite structure suitable for use as material for articles of protective clothing, which composite structure comprises a fabric substrate treated with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant and on both sides of the substrate, a thermoplastic fluoropolymer film and a PTFE film, wherein said thermoplastic fluoropolymer thermally-melt-bonds said PTFE film to said substrate. The subject invention further provides for a method for forming a composite structure suitable for use as material for articles of protective clothing, which method comprises treating a fabric substrate with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant and thermally-melt bonding a PTFE film having a thermoplastic fluoropolymer coating on at least the inner side thereof to both sides of the fabric substrate. The subject invention further provides for a method for forming a composite structure suitable for use as material for articles of protective clothing, which method comprises treating a fabric substrate with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant and thermally-melt-bonding a PTFE film to both sides of the substrate by thermally-melt-bonding a thermoplastic fluoropolymer film interposed between said substrate and each of said PTFE films. The subject invention also provides for articles of protective clothing fabricated from the subject composite structures. Figure 1 is an unscaled, cross-section of a preferred embodiment of a composite structure; Figure 2 is an unscaled, cross-sectional view of a parallel seam preferred in fabricating garments, wherein the various layers of the composite structure are not shown; and FIGURE 3 is a graph showing impermeability of the novel composite structures, as discussed in greater detail in Example 2. As can be seen best in Fig. 1, a preferred embodiment of the composite structures 10 comprises a fabric substrate 11, and thermally bonded on both sides thereof, a coated film 12 such as a coated, universally chemically resistant film, which coated film 12 comprises a PTFE film 13 having a thermoplastic fluoropolymer coating 14 on both sides thereof. Surprisingly, it was found from experimentation that with careful control of the thermal-melt-bonding process, it was possible to melt the thermoplastic fluoropolymer, thereby permitting it to bond the film to the fabric without melting the fabric. The fabric substrate may comprise any knit, woven, or non-woven fabric material which is generally suitable for use as clothing and which presents a reasonably flat contact area for bonding. Such fabric material also should be dimensionally stable and otherwise capable of withstanding the temperatures encountered in thermally-melt-bonding the coated film to the fabric substrate. Those temperatures will vary according to the thermoplastic fluoropolymers selected for the coated film, but in general will be higher than about 288°C (550°F). Accordingly, such fabric materials are composed of a variety of natural and synthetic fibers, including metal, polyamide, aromatic aramid, carbon, glass, graphite, ceramic, potassium titanate, and blends thereof. In general, the fabric substrate will have a thickness of from 0.025 to 0.508 cm (from 0.010 to 0.200 inch), preferably from 0.127 to 0.152 cm (from 0.050 to 0.060 inch), and a weight of from 67.8 to 339.1 gram/meter² (from 2.0 to 10.0 ounce/yard²), preferably from 101.7 to 135.6 grams/meter² (from 3.0 to 4.0 ounce/yard²). While suitable fabric substrate material may be manufactured by methods well known in the art, they also are available commercially from a variety of manufacturers. Woven fabric is preferred because of its relatively greater strength and flexibility as compared to non-woven fabric material. For this reason, polyaramide and polyamide fabrics, and blends thereof, are especially preferred. Those fabrics are tough and durable, and are extremely resistant to tearing and puncturing, especially on an equivalent weight and weave basis. Accordingly, even when the outer coated film layer is penetrated, a polyaramide or polyamide fabric substrate is much more capable of preventing puncturing or tearing of the inside coated film and, thus, of preserving a leak-proof, impermeable chemical barrier. Polyaramide and polyamide fabrics also impart a degree of thermal insulation against the heat generated by fires which may be encountered in chemical accidents. Further, they are flame-resistant and somewhat chemically inert. Woven fabrics, however, are relatively expensive. It has been found that a less expensive, spun-laced Nomex®/Kevlar® polyaramide blend fabric provides adequate strength and flexibility while providing a better bonding surface, and accordingly, such fabrics are especially preferred. Those fabrics are preferred also because they have a high voids volume which also acts as thermal insulation. Suitable polyaramide fabrics, and blends thereof, may be manufactured by methods well known in the art and are commercially available in a variety of weights and weaves from a number of sources, including Burlington Industrial Fabrics Co., Greensboro, North Carolina; Hexcel Corporation, Dublin, California; Uniroyal Goodrich Tire Co., Winnsboro, South Carolina; and DuPont de Nemours, E.I. & Co., Inc., which markets Kevlar® and Nomex® polyaramide fibers and the spun-laced Nomex®/Kevlar® E-89 polyaramid blend fabric referred to above. The fabric substrate is treated with a particular antiwicking composition. The antiwicking compositions are as described in the copending application EP-A-0 320 257. These antiwicking compositions provide more universal antiwicking properties, that is, they repel water, oil, organic solvents, and chemicals, not merely aqueous chemicals. They also do not significantly decrease the flexibility of the fabric substrate or composite structure and, because they are based on fluorocarbon polymers, they are especially compatible with a thermoplastic fluoropolymer coated PTFE film. The antiwicking compositions of the above-referenced application comprise a fluorinated ethylene/polypropylene copolymer (FEP), a polymeric fluoroaliphatic ester (PFE), a liquid carrier, and a dispersant. The antiwicking composition may further comprise a wetting/saturating agent. The FEP component, along with the PFE component, are the primary components of the composition which remain in the fabric after drying, the other components being volatilized in large part during the application process. The FEP component includes any of the well known and conventional copolymers of tetrafluoroethylene and hexafluoropropylene. In general, the FEP may comprise from 2.0 to 8.0 wt% and preferably from 3.5 to 6.5 wt%, of the antiwicking composition. In greater amounts, the FEP may tend to coat on the surface of the fabric or tend to form a film through the fabric and thereby decrease the fabrics flexibility. If too little FEP is used, inadequate antiwicking properties may be imparted. The amount of FEP should be coordinated with the amount of PFE comprised by the antiwicking composition. The PFE should also be applied in amount sufficient to impart the desired antiwicking properties but not in amounts that will unnecessarily stiffen the fabric or will tend to fill in or close its pores. Accordingly, the PFE may comprise from 1.0 to 6.0 wt%, and preferably from 3.5 to 5.0 wt%, of the composition. Furthermore, the FEP and PFE preferably should be used in combined amounts of from 3.0 to 13.0 wt% and preferably 4.0 to 8.0 wt%. The carrier liquid should be selected and included in amounts sufficient to enable the FEP and PFE to be carried into the fabric in a reproducible manner. Such carriers may be selected from a variety of organic and inorganic liquids but water, and in particular, distilled or deionized water is the preferred carrier. The dispersant should be selected and included in amounts sufficient to provide a stable, uniform dispersion to ensure uniform, complete, and reproducible application of the FEP and PFE to the fabric. Suitable dispersants may be selected from a variety of conventional anionic and non-ionic dispersants, including those selected from the group consisting of poly (acrylic) acid and its derivatives, e.g., sodium polyacrylate and amonium polyacrylate; cellulose and its derivatives, e.g., methylcellulose, carboxymethyl cellulose, and hydroxyethyl cellulose; and mixtures thereof. The optimum amount of dispersant used will vary somewhat depending on the choice of the dispersant and other components. The dispersant typically will comprise from 0.5 to 1.5 wt%, and preferably from 0.75 to 1.25 wt%, of the composition. The wetting/saturating agent facilitates preparation of the composition and permits the composition to be sufficiently retained in, contact, and saturate, as opposed to flowing through, the fabric. Wetting/saturating agents may be selected from conventional anionic or non-ionic wetting agents with the non-ionic wetting agents such as water soluble alcohols, e.g., isopropyl alcohol, being preferred. The wetting/saturating agent may comprise from 0.1 to 1.5 wt%, and preferably from 0.5 to 1.25 wt% of the composition. The antiwicking compositions are preferably prepared from FEP and PFE dispersions. Suitable dispersions, which are available commercially, are mixed along with the other components. Typically, commercially available dispersions will be in a more concentrated form than is preferred, e.g. , from 30 to 60 wt% solids. Thus, they should be diluted before or after mixing. If additional dispersants and/or wetting agents are desired, however, they preferably are diluted somewhat in the carrier prior to admixture with the other components. The antiwicking agents, in general, may be applied to any knit, woven, or non-woven fabric. Because of its more universal antiwicking properties, however, the novel antiwicking compositions preferably are applied to fabric to be used in composite material for protective clothing used in handling and cleaning up chemicals. Although the amounts applied may vary according to the particular fabric chosen or according to the desired degree of antiwicking properties or flexibility, the antiwicking compositions typically are applied in amounts ranging from 50.86 to 169.6 gram/meter² (1.5 to 5.0 ounce/yard²), preferably from 67.8 to 135.6 gram/meter² (2.0 to 4.0 ounce/yard²) add-on weight. They may be applied to the fabric by methods well-known for applying conventional antiwicking agents, e.g. , saturating the fabric, squeezing out the excess, and drying the saturated fabric. Drying typically will be conducted at elevated temperatures, e.g. , from 274 to 288°C (525 to 550°F), and preferably is accompanied by the application of pressure, e.g. , calendaring the treated fabric. The composite structures comprise in one embodiment a coated, universally chemically resistant film, which coated film comprises a PTFE film preferably having a thermoplastic fluoropolymer coating on both sides thereof. As noted above, preferred composites of said first embodiment may comprise a PTFE film coated only on its inner side with a thermoplastic fluoropolymer. A second embodiment comprises separate, pre-formed PTFE and thermoplastic polymer films. An understanding of those second embodiment, however, will come from the description which follows wherein a PTFE film is coated on both sides with the thermoplastic fluoropolymer. The PTFE films may be composed primarily of PTFE. While they may contain certain additives, such as wetting agents or copolymers, preferably the presence of such components in the PTFE films at least is minimized, if not avoided altogether. Necessarily, any such component is not as universally chemically resistant as PTFE, and if present, the chemical resistance of the film is decreased. Thus, PTFE films substantially free of additional components are especially preferred. Hard polymers, such as epoxy, phenolics, and the like especially are to be avoided in that they not only decrease the chemical resistance of the PTFE film, but they also increase the stiffness of the PTFE film. The PTFE film preferably is coated on both sides with a thermoplastic fluoropolymer. Thermoplastic fluoropolymers, unlike PTFE which sinters, flow when heated and are fusible. Accordingly, any of a number of well-known thermoplastic polymers may be used herein, such as FEP, tetrafluoroethylene/ethylene copolymers, tetrafluoro-ethylene/perfluorovinyl ether copolymers, polychlorotri-fluoroethylene, poly(vinyl fluoride), poly(vinylidene fluoride), and mixtures thereof. Because it is more universally chemically resistant, it will be appreciated that the primary barrier is provided by the PTFE film. Being fluorocarbon polymers, however, thermoplastic fluoropolymers are similarly resistant to a wide variety of chemicals, and the thermoplastic fluorocarbon coatings do contribute to the formation of an effective chemical barrier. More importantly, because of their thermoplastic properties, the thermoplastic fluoropolymer coatings also bind the coated film to the fabric substrate and assist in maintaining the integrity of the barrier in the seam area. The inner coating of thermoplastic fluoropolymer is thermally-melt-bonded directly to the fabric substrate, and thereby binds the PTFE film securely to the fabric substrate without the use of adhesives. Unlike conventional adhesives, the bond between the inner thermoplastic fluoropolymer coating and the fabric substrate is not easily destroyed by chemicals penetrating the laminate. Moreover, the inner thermoplastic fluoropolymer coating bonds the PTFE film to the fabric substrate without appreciably increasing the stiffness of the composite structure and, when heated, can assist in sealing the seam area by flowing into and around the seam holes. An outer thermoplastic fluoropolymer coating, in those embodiments wherein it is present, contributes additional, important benefits. It enables more efficient filling of the seam holes in sewn seams. The outer coatings of adjacent portions of composite material also may be thermally-melt-bonded in the seam area. Depending on the stress which the seam is expected to encounter, such thermal-melt-bonding alone may provide a seam of sufficient strength without stitching. Even where the seam is sewn, however, the strength of the seam and the effectiveness of the seal may be increased by thermally-melt-bonding the seam area. Similarly, if the use of such tape is desired in fabricating protective clothing, an outer coating enables a more effective bonding with PTFE/FEP tape. The thickness and weight of the coated film will vary depending on the wear and chemical exposure which the material is expected to withstand, and will also depend on the relative thickness and weight of the PTFE layer and the thermoplastic fluoropolymer coatings. As the coated film is made thicker and heavier, it will become unacceptably inflexible and fatiguing to those wearing clothing made therefrom. The physical barrier will be thicker, and all other factors equal, will be more effective of course, but this theoretical enhancement of the barrier is more than offset by discomfort resulting from increasing weight. In general, the thinnest possible coated film, consistent with the formation of an effective barrier, should be used insofar as this contributes to a lighter, more flexible garment, and one in which thermal bonding of the coated film and heat sealing of the seams can be accomplished more effectively. That is, the thickness and weight of each coated film layer of the composite structure preferably is such that each coated film layer alone can provide an effective chemical barrier in itself. Thinner, lighter coated films may be used, but if the outer coated film layer is punctured, the inner coated film layer preferably will be sufficient to provide an effective chemical barrier alone. In any event, the coated film should not be so thin and light that it is difficult to handle during fabrication. Accordingly, the overall thickness of each coated film is from 0.004 to 0.013 cm (0.0015 to 0.005 inch), preferably from 0.005 to 0.008 cm (0.002 to 0.003 inch). The weight generally is from 101.7 to 339.1 grams/meter² (3.0 to 10.0 oz/yard²), preferably from 135.6 to 203.5 grams/meter² (4.0 to 6.0 oz/yard²). The PTFE film of the coated film layer should be thick and heavy enough to form an effective chemical barrier in itself and to enable it to be handled during coating with the thermoplastic fluoropolymer. That is, as for the coated film layer, the PTFE film also should provide an effective chemical barrier apart from the combined effectiveness of the two coated film layers or the thermoplastic fluorocarbon coatings. Apart from other considerations, there always is the risk of the thermal-melt-bonding process compromising the integrity of the thermoplastic fluorocarbon coating, and thus, each PTFE film should present an effective chemical barrier regardless of whether the structural integrity of the thermoplastic fluoropolymer coating or the other coated film layer is compromised. The PTFE film also should not be so thin and light, however, that it is easily punctured or torn during processing. In general, therefore, each PTFE film will be from 0.003 to 0.008 cm (0.0013 to 0.003 inch), preferably from 0.004 to 0.005 cm (0.0016 to 0.0018 inch) thick. The weight of the PTFE film generally is from 88.2 to 203.5 grams/meter² (2.6 to 6.0 oz/yard²), preferably from 108.5 to 122.1 grams/meter² (3.2 to 3.6 oz/yard²). The thermoplastic fluoropolymer coating preferably is of the minimum thickness needed to effectively bind the coated film layer to the fabric substrate, although the outer coating, since it does not have to bond to fabric, may be somewhat thinner than the inner coating. Excessive thermoplastic fluoropolymer will increase the stiffness of the coated film and the composite structure and will not appreciably increase the effectiveness of the chemical barrier during use. Accordingly, each thermoplastic fluoropolymer coating generally is from 0.0003 to 0.0048 cm (0.0001 to 0.0019 inch), preferably from about 0.0010 to 0.0015 cm (0.0004 to 0.0006 inch) thick. The weight of the thermoplastic fluoropolymer coating generally is from 6.78 to 67.8 grams/meter² (0.20 to 2.0 oz/yard²) , preferably from 13.6 to 40.7 grams/meter² (0.40 to 1.2 oz/yards²). The composite structure according to the first embodiment is formed by thermally-melt-bonding pre-formed coated films preferably to each side of the fabric substrate. The fabric substrate is pre-treated with the antiwicking composition mentioned above. Methods of applying the antiwicking composition are well known in the art and also are disclosed in the co-pending application EP-A-0 320 257, referenced above. The coated film itself preferably is formed by coating a PTFE film with a thermoplastic fluoropolymer. Suitable PTFE films may be manufactured by well-known procedures, e.g. , molding-skinning a PTFE dispersion. Suitable PTFE dispersions, as well as PTFE films, are available commercially from a number of sources, including, DuPont (Teflon ® ), and Allied Chemical, Morristown, N.J. (Halon ® ). The PTFE film also may be coated by methods well-known in the art, e.g. , by casting a thermoplastic fluoropolymer dispersion over the film or by dipping the film into a thermoplastic fluoropolymer dispersion. Suitable thermoplastic fluoropolymer dispersions are available commercially, e.g. , Teflon ® FEP dispersions sold by DuPont. Thermoplastic fluoropolymer coated PTFE films also are available commercially, e.g. , Emflon TM FEP coated PTFE films sold by Pallflex, Inc., Putnam, Connecticut. The coated film then is thermally-melt-bonded to the fabric substrate. Thermal-melt-bonding techniques are well-known in the art and in general may be utilized. In the context of the above structures, however, it will be appreciated that the thermal rating of the fabric substrate typically is lower than that of the thermoplastic fluoropolymer. Thus, care should be taken to ensure that the substrate is not melted or scorched during the thermal-melt-bonding process. The thermal-melt-bonding process, therefore, typically is conducted at somewhat higher temperatures, higher pressures, and shorter dwell times than would be utilized where the thermal ratings of the substrate and film were more nearly equal. Thereby, the thermoplastic fluoropolymer coating preferably is not melted per se , but rather it is heated to a gel-like condition. Accordingly, the thermal-melt-bonding typically will involve temperatures of from 260° to 371°C (500 to 700°F), pressures of from 0.069 to 1.723 bars (1.0 to 25.0 psi), and dwell times from 1.0 to 20.0 sec. The specific bonding parameters will depend primarily on the composition, thickness, and weight of the coated film and the substrate, but are readily optimized by those skilled in the art. The novel composite structures according to the second embodiment are made by thermally-melt-bonding pre-formed PTFE and thermoplastic fluoropolymer films to the substrate. Suitable thermoplastic fluoropolymer films may be made by methods well-known in the art, and are also commercially available. The pre-formed thermoplastic fluoropolymer film, in theory, may be as thick as the thermoplastic fluoropolymer coating, i.e. , from 0.0003 to 0.0048 cm (0.0001 to 0.0019 inch), preferably from 0.0010 to 0.0015 cm (0.0004 to 0.0006 inch) thick. It will be appreciated, however, that at the lower limits of those ranges, the thin thermoplastic fluoropolymer films are somewhat difficult to handle, and may tend to tear during processing. Accordingly, if a pre-formed thermoplastic fluoropolymer film is used, it generally will be from 0.0018 to 0.0048 cm (0.0007 to 0.0019 inch) thick, or of such other minimum thickness which enables it to sufficiently bond the PTFE film and to be handled by the processing equipment used. In theory, it should be possible to pre-coat the fabric substrate with the thermoplastic fluoropolymer and then melt-bond a PTFE film thereto. In practice, however, that process generally will result in an excessively thick and heavy thermoplastic fluoropolymer layer and should be avoided. If possible at all, it is very difficult to obtain the full benefits of the subject invention by that technique. The composite structures may be used to fabricate articles of protective clothing, such as hats, gloves, jump suits, coveralls, and the like, in general, by conventional processes. Because the composite structures have increased strength and flexibility, they may be joined by a variety of seams, especially when the coated film comprises an outer coating. Some seams, such as those in the crotch or arm pit areas of clothing, must be very sturdy, whereas others, such as those in head gear, may be subject to very little stress. Where increased strength is important, sewn seams are preferred. There are a variety of sewn seams which are well-known in the art and which may be used (such as lap seams), but because folded parallel seams are both strong and may be efficiently sealed, they are especially preferred. In folded parallel seams, as shown in Fig. 2, one of the two pieces of composite material 21a and 21b is folded over the stitched area 22 of the seam 20 in such a manner that a portion of the composite structure 21b is folded over and abuts those portions of the composite structures 21a and 21b, the barrier of which has been structurally compromised by the stitching. The risk of chemical penetration through the seam area, and in particular through the stitching, is reduced, and accordingly, protective clothing of the subject invention preferably will utilize parallel seams. The outer thermoplastic fluoropolymer coatings abutting each other at the stitching area 22 and/or the fold-over area 25 may be thermally-melt-bonded together for added strength. Even where such added strength is not needed, the seam area preferably is heated to a degree sufficient to permit portions of the thermoplastic fluoropolymer coating to flow into and seal the stitching holes. Additionally, a layer of heat sealed PTFE/FEP tape 23 preferably is applied on one side of the seam area to cover otherwise exposed stitching. A second layer of PTFE/FEP tape 24 (shown in broken lines) may be applied to the other side for added strength and sealing, but for many purposes neither tape layer is strictly necessary, especially if the seam has been heat sealed as described above. If the coated film is provided with an outer thermoplastic fluoropolymer coating, it may not be necessary to stitch a seam. Thermal-melt-bonding of the outer coating of joined pieces may provide a seam of sufficient strength for the particular application, and this has the benefit of not forming holes which later must be sealed. The invention will be further described by reference to the following examples. Example 1 Two coated films are tested for liquid permeation of 50 wt% NaOH and 96 wt% H₂SO₄ at room temperature. The coated films comprise a PTFE film coated on both sides with FEP. The liquid permeation test follows the procedure set forth in publication F739-85 of the American Society for Testing and Materials (ASTM), 1916 Race Street, Philadelphia, PA 19103, wherein the duration of the measurement period is 90 minutes and impermeability is defined as less than one part per million permeation. The results of this experiment will be as set forth below in Table I. Specimen Contact Area (cm²) Film Thickness (cm) Weight Per Unit Area (grams/m²) Challenge Fluid Impermeable 1 20.4 0.0058 235 50 wt% NaOH yes 2 20.4 0.0053 232 96 wt% H₂S₄ yes In summary, the coated PTFE films will exhibit complete resistance to liquid permeation, as defined herein, of 50 wt% NaOH and of 96 wt% H₂SO₄ for a period of 90 minutes. Example 2 PTFE film coated on both sides with FEP is thermally-melt-bonded to both sides of a spun-laced Nomex®/Kevlar® polyaramid blend fabric. The fabric is obtained from DuPont, Product No. E-89, and has a thickness of 0.0559 cm (0.022 inch) and a weight of 94.9 grams/meter² (2.8 oz/yard²). The film is generally as described in Example 1 and has a thickness of 0.008 cm (0.003 inch) and a weight of 203.5 grams/meter² (6.0 oz/yard²). The composite structure is evaluated for permeation by following generally the procedure set forth in Example 1, wherein the challenge fluids are dimethylformamide in hexane, toluene, vinyl acetate, 50 wt% NaOH, 97 wt% H₂SO₄, and glacial acetic acid. Permeation may be detected and measured by techniques appropriate to the challenge fluid. For example, impermeability of the film to dimethylformamide in hexane is confirmed by monitoring the uv absorbance (g = 238 nm) in the test cell. The results will be as shown in Fig. 3, wherein a decrease in absorbance of approximately 0.0012 absorbance units indicates permeation as defined herein, i.e. , 1 part per million. In sum, the composite structures will be light, flexible, and exhibit resistance to liquid permeation, as defined herein, of the challenge fluids for a period of 90 minutes. As noted above, this invention has been disclosed and discussed primarily in terms of specific embodiments thereof, but is not intended to be limited thereto. Other modifications and embodiments will be apparent to the worker in the art. For example, the composite structures have been described primarily in the context of protective clothing. While that is a particularly preferred application, the composite structures may be used for other purposes, such as wall coverings. In such applications, increased flexibility may not be of as great a concern, and thicker, stiffer composite structures may be utilized.

Claims: A composite structure (10) suitable for use as material for articles of protective clothing, which composite structure comprises a fabric substrate (11) treated with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant, and thermally-melt-bonded on both sides of the substrate, a coated film (12), which coated film (12) comprises a PTFE film (13) having a thermoplastic fluoropolymer coating (14) on at least the inner side thereof. The composite structure (10) of claim 1, wherein said coated film (12) comprises a PTFE film (13) having a thermoplastic fluoropolymer coating (14) on both sides thereof. The composite structure (10) of claim 1 or claim 2, wherein said anti-wicking composition includes a wetting/saturating agent. The composite structure (10) of any one of claims 1 to 3, wherein said fabric substrate (11) is selected from the group consisting of polyaramide and polyamide fabrics, and blends thereof. The composite structure (10) of any of claims 1 to 4, wherein said thermoplastic polymer coating (14) comprises a thermoplastic fluoropolymer selected from the group consisting of fluorinated ethylene/propylene copolymers, tetrafluoro-ethylene/ethylene copolymers, tetrafluoro-ethylene/perfluoro-vinyl ether copolymers, polychlorotrifluoroethylene, poly(vinyl fluoride), poly(vinylidene fluoride), and mixtures thereof. The composite structure (10) of any one of claims 1 to 5, wherein said fabric substrate (11) has a thickness of from 0.025 to 0.508 cm (0.010 to 0.200 inch), and a weight of from 67.8 to 339 grams/meter² (2.0 to 10.0 oz/yard²), said PTFE film (13) has a thickness of from 0.003 to 0.008 cm (0.0013 to 0.003 inch), and a weight from 88.2 to 203.5 grams/meter² (2.6 to 6.0 oz/yard²), and said thermoplastic fluoropolymer coating (14) has a thickness of from 0.0003 to 0.0048 cm (0.0001 to 0.0019 inch), and a weight of from 6.78 to 67.8 grams/meter² (0.20 to 2.0 oz/yard²). An article of clothing comprising the composite structure of claim 1 or 2. A method for forming a composite structure (10) suitable for use as material for articles of protective clothing, which method comprises treating a fabric substrate (11) with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant and thermally-melt-bonding a PTFE film (13) having a thermoplastic fluoropolymer coating (14) on at least the inner side thereof to both sides of the fabric substrate (11). A method according to claim 8 wherein the PTFE film (13) has a thermoplastic fluoropolymer coating (14) on both sides thereof. A method according to claim 8 or claim 9 wherein the anti-wicking composition includes a wetting/saturating agent. A composite structure (10) suitable for use as material for articles of protective clothing, which composite structure (10) comprises a fabric substrate (11) treated with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant and on both sides of the substrate, a thermoplastic fluoropolymer film (12) and a PTFE film (13), wherein said thermoplastic fluoropolymer thermally-melt-bonds said PTFE film (13) to said substrate. An article of clothing comprising the composite structure of claim 11. A method for forming a composite structure (10) suitable for use as material for articles of protective clothing, which method comprises treating a fabric substrate (11) with an anti-wicking composition comprising a fluorinated ethylene/propylene copolymer, a polymeric fluoroaliphatic ester, a carrier liquid and a dispersant and thermally-melt-bonding a PTFE film (13) to both sides of the substrate (11) by thermally-melt-bonding a thermoplastic fluoropolymer film (12) interposed between said substrate (11) and each of said PTFE films (13).

Inventors: ADILETTA, JOSEPH G.
Applicants: PALL CORPORATION
Application year: 1988
Main classification: A62D5
IPC codes: A41D31, B32B27, A62B17, A62D5