A CATALYZED FAST CURE POLYURETHANE SEALANT COMPOSITION

Abstract: A polyurethane sealant composition is made from a polyurethane prepolymer having blocked isocyanate groups. A 1,8-diaza bicyclo(5:4:0)undecene-7 (DBU) catalyst or a derivative thereof is utilized in association with an amine curing agent having at least two primary amine groups to achieve a relatively fast cure time. The catalyst is a true catalyst in that it merely aids in unblocking the isocyanate groups whereby the curing agent can react therewith.

Description: FIELD OF THE INVENTION The present invention relates to a polyurethane sealant composition and a cured polyurethane sealant composition. Heretofore, various sealant compositions have been proposed. For example, U.S. Patent No. 3,248,371 relates to a blocked isocyanate-terminated coating composition which is unblocked by reacting it with a hydroxy tertiary amine. U.S. Patent No. 3,267,078 relates to a coating composition that contains a blocked isocyanate-terminated polyether-based urethane intermediate and which is reacted with a diamine prepared by reacting a diamine with a carbonyl compound such as a ketone or an aldehyde. EP-A-0 247 692 (priority date 29.05.1986 but published 06.07.1988) discloses an elastomeric fluid composition for sealants crosslinkable under ambient conditions of temperature and humidity, comprising: A) an elastomeric polymer constituted by an elastomeric basis of aliphatic polycarbonate, bearing functional phenylcarbamate or (phenyl-substituted)-carbamate end groups, and having a molecular weight value of from 500 to 5,000; B) an organic compound containing in its molecule at least two N=C groups, selected from bisketimines, bisketiminoenamines and bisketiminosilazanes; C) a tertiary amine with stressed nitrogen and containing a ketiminic carbon atoms bonded to nitrogen; wherein the (B) Component is present in the amount which supplies a maximum of 2 total ketimino and enamino groups per each arylcarbamate group in the (A) Component, and the (C) Component is present in an amount of at least 0.5 parts by weight per each 100 parts by weight of the (A) Component. US-A-3 245 961 discloses cured compositions prepared from a caprolactam blocked isocyanate component and an amine cross-linker. Sealant compositions desirably have a combination of properties which render them particularly suitable for their intended applications. Such compositions should be able to be packaged in sealed containers or cartridges and stored for relatively long periods of time without objectionably "setting up" or hardening (as a result of cross-linking). When applied as a caulking sealant composition, they should form a relatively tack-free surface soon after being applied and exposed to atmospheric moisture and should cure without the formation of bubbles within an acceptable time period. They should also adhere tenaciously in the cured state to a wide variety of surfaces, such as to glass, aluminum, concrete, marble and steel surfaces. The sealant in the cured state should have sufficient elasticity and flexibility to withstand expansions and contractions of panels, etc. with which it is associated during temperature variations experienced as a result of climatic changes and to withstand wind forces that cause panels with which it is associated to flex or twist. It is therefore an aspect of the present invention to provide a fast cure polyurethane sealant composition. It is a further aspect of the present invention to provide a fast cure polyurethane sealant system, as above, wherein an unblocking bicyclic amidine catalyst is utilized. It is another aspect of the present invention to provide a fast cure polyurethane sealant composition, as above, wherein the prepolymer is made from a polyether polyol intermediate and a polyisocyanate with the isocyanate groups being subsequently blocked so that the prepolymer has a relatively long shelf life. It is yet another aspect of the present invention to provide a fast cure polyurethane sealant composition, as above, wherein a variety of amine curing agents having at least two primary amine groups therein can be utilized. It is yet another aspect of the present invention to provide a fast cure polyurethane sealant composition, as above, wherein additives can be utilized such as thixotropes, alcohols, and other hydroxyl species which could not normally otherwise be utilized as they would react with free isocyanates. It is yet another aspect of the present invention to provide a fast cure polyurethane sealant composition, as above, wherein cure of the composition can be controlled from essentially instantaneous to one or two hours or longer by varying the amount of catalyst utilized. It is yet another aspect of the present invention to provide a fast cure polyurethane sealant composition, as above, wherein cure occurs at ambient temperatures. The present invention relates to a polyurethane sealant composition, comprising: a cured polyurethane, said cured polyurethane made from a polyurethane prepolymer having blocked isocyanate groups, a curing agent, and an effective amount of a bicyclic amidine catalyst or a derivative thereof, said curing agent having at least two primary amine groups therein, wherein said blocked urethane prepolymer is made from a polyester polyol (excluding polycarbonate polyols), a polybutadiene polyol, or a polyether polyol, and an aromatic polyisocyanate with a blocking agent subsequently blocking terminal isocyanate groups, wherein the blocking agent is selected from phenol, 3-methoxyphenol, 4-methoxyphenol, nonylphenol, meta-cresol, para-cresol, 4-chlorophenol, meta-hydroxybenzaldehyde, ortho-hydroxybenzaldehyde, para-hydroxybenzaldehyde, hydroquinone, 1-hydroxy-2-propanone, 3-hydroxyacetophenone, 4-hydroxyacetophenone, ethyl acetyl acetate and cyclohexanone oxime. The present invention relates to a curable polyurethane composition which contains two different components, that is a polyurethane prepolymer component as well as a curing agent component. The components are separately maintained from one another and are brought together generally at the application site whereupon cure readily occurs in a short period of time. The prepolymer is made by reacting a hydroxy terminated intermediate with a polyisocyanate. The hydroxy terminated intermediate can be any conventional polyester polyol or a conventional polybutadiene polyol. Desirably, the hydroxy terminated intermediate is a polyether polyol. More specifically, a poly(oxyalkylene) diol or triol is utilized wherein the alkylene group contains from 2 to 6 carbon atoms with 3 carbon atoms being preferred. Thus, poly(oxypropylene) diol or triol can be utilzied with the latter being highly preferred. Suitable polyether polyols thus include polyethylene ether triol, polypropylene ether triol, polybutylene ether triol, and the like. In lieu of the above triol polyethers, the corresponding diol polyether can be utilized. The equivalent weight of the various hydroxyl terminated intermediates is from 500 to 10,000, desirably from 500 to 3,000, and preferably from 1,000 to 2,100. Such intermediates thus generally have a long flexible backbone which is desired for use in the present invention. An optional, although often preferred, aspect of the polyether polyols of the present invention is that they are end capped with ethylene oxide end blocks. The provision of ethylene oxide end blocks provides a primary hydroxyl group which tends to be more reactive with polyisocyanate than the polyether polyol. The total amount of the ethylene oxide end caps is rather small, that is generally 10% or less by weight, and preferably 5% or less by weight based upon the total weight of the end capped polyethylene polyol. Amounts in excess of approximately 5% by weight of ethylene oxide end blocks are avoided since the intermediate tends to become moisture sensitive. The polyisocyanates which can be utilized in the present invention desirably contain aromatic groups since aliphatic polyisocyanates generally cannot be unblocked and usually are not reactive. The aromatic polyisocyanates can generally be represented by the formula R(NCO) n wherein n is 2 or 3 with 2 being highly preferred. R is an aromatic or an alkyl substituted aromatic containing from 6 to 20 carbon atoms, with from 6 to 15 carbon atoms being desired. Examples of specific aromatic polyisocyanates include the various diphenyl methane isocyanates, the various naphthalene diisocyanates such as naphthalene 1,5-diisocyanate, the various tolylene diisocyanates such as 2,4-tolylene diisocyanate and 2,6-tolylene diisocyanate, the various phenylene diisocyanates, the various toluene diisocyanates such as toluene-2,4-diisocyanate, the various biphenylene diisocyanates, and combinations thereof. A preferred polyisocyanate of the present invention is toluene diisocyanate. The polyurethane prepolymer is readily prepared by mixing the polyether polyol with the polyisocyanate at ambient temperature and pressure although desirably the reaction is carried out at elevated temperatures, such as from 60°C to 100°C since the reaction rate is significantly increased. The equivalent ratio of the polyisocyanate to the the polyether polyol can be from 0.8 to 3.0. However, a slight excess is preferred to ensure complete reaction of the terminal hydroxy groups. In order to provide a polymer that is more stable during storage, the isocyanate-terminated prepolymer described above is "blocked" with a blocking agent that reacts with the terminal isocyanate groups of the prepolymer. Blocking agents useful in the present invention include blocking agents that produce blocked terminal isocyanates that do not react readily with moisture in air at room temperature (25°C), but which will be readily "unblocked" and quickly or rapidly react with a curative of the present invention at room temperature, i.e. blocking agents selected from phenol, 3-methoxyphenol, 4-methoxyphenol, nonylphenol, meta-cresol, para-cresol, 4-chlorophenol, meta-hydroxybenzaldehyde, ortho-hydroxybenzaldehyde, para-hydroxybenzaldehyde, hydroquinone, 1-hydroxy-2-propanone, 3-hydroxyacetophenone, 4-hydroxyacetophenone, ethyl acetyl acetate and cyclohexanone oxime. Sufficient blocking agent is reacted with the isocyanate-terminated polymer to theoretically "block" all of the terminal isocyanates, e.g. an equivalent excess, of the polymer. Generally, at least a 10% equivalent excess is utilized. The polyurethane prepolymer of the present invention is cured with any conventional amine curing agent as well as those known to the art and to the literature which contain at least two primary amine groups therein. The amine curing agents can be compounds having from 3 to 260 carbon atoms therein or desirably from 6 to 36 carbon atoms. Additionally, the amine curing agents can be a polymer having a molecular weight up to 5,000 and desirably from 200 to 450. Examples of specific amine compounds include triethylene tetraamine, bisaminopropylpiperazine (BAPP), diethylene triamine, tris (2-aminoethyl) amine, 2-methyl pentamethylene diamine, isophorone diamine, and the like. Various polymeric amines can be utilized such as the various Jeffamines® produced by The Texaco Chemical Company. A desired polymeric amine are the Jeffamine® D-400 compounds which generally have the following formula. wherein n is 5 or 6. Numerous other polymeric amine compounds can be utilized such as the various other Jeffamine® D series compounds wherein n varies from 2 to 70, and other types of Jeffamines®. As noted above, the basic requirement is that the amine curing agent contain at least two primary amine groups therein whether it be an amine compound or a polymeric amine compound. Although various amine curing agents of the present invention can be utilized, including various combinations thereof, a desired amine curing agent is a blend of the Jeffamine D-400 amines and BAPP in relatively equal equivalent amounts of each compound, for example, from 0.8 to 1.2 equivalents of one compound based upon one equivalent of the remaining compound. The amount of the amine curing agent containing at least two primary amines therein is from 0.8 to 1.2 equivalents and desirably 1 equivalent for each blocked isocyanate equivalent. Although the amine curing agents of the present invention are effective in removing the blocking agents and thus permitting the polyurethane prepolymer to cure, the time is generally slow as often from a few hours to many days. However, according to the concepts of the present invention, it has been found that a particular catalyst and various derivatives thereof, e.g. a reation product, are effective in quickly removing the blocking agents thereby permitting the amine curing agent to rapidly cure the polyurethane prepolymer in a very short period of time, generally within a couple hours, desirably within an hour, and possibly within a matter of minutes. The effective catalyst of the present invention is a bicyclo amidine and specifically is 1,8-diaza bicyclo(5:4:0)undecene-7, that is DBU, and generally has the following formula The various derivatives or reaction products of DBU which can be utilized in the present invention as a catalyst include the reaction product of DBU with phenol, as well as with various other acidic compounds. Such acidic compounds include the various sulfonic acids such as p-toluenesulfonic, sulfimides, sulfamides, phosphonic acids, the various N-sulfonylcarboxamides which have a total of from 2 to 36 carbon atoms, and the various carboxylic acids which have a total of from 2 to 18 carbon atoms. The reaction product with phenol is desired whereas the unreacted catalyst DBU, is preferred. The amount of the unblocking catalyst often depends upon the application and desired end result since larger amounts of catalyst generally effect a quicker cure time. That is, amounts can utilized to effect a cure in a hour or two or in a matter of minutes. Still higher amounts can effect cure almost instantaneously. Generally, the amount of catalyst can range from 0.01 to 2.5 parts, desirably from 0.02 to 1.2 parts, and preferably from 0.1 to 0.25 part by weight per 100 parts by weight of prepolymer. Furthermore, the catalyst may be the reaction product of DBU with phenol or 2-ethylhexanoic acid. As noted, the polyurethane sealant composition of the present invention is generally contained as two separate components. That is a prepolymer or base component and a curing agent component. The curing agent component generally contains the amine curing agent, the DBU catalyst or derivatives thereof, as well as optional plasticizers, pigments, thickeners, drying agents, and the like. The base component contains the prepolymer as well as various conventional additives or compounding ingredients such as fillers, thickeners or thixotropic agents, pigments, plasticizers, UV absorbers, solvents, and the like. The base component generally contains large amounts, that is from 60 to 200 parts by weight per 100 parts by weight of prepolymer of a filler such as talc, various silicates, various clays, calcium carbonate, and the like. The thickening agents are generally thixotropic compounds such as hydrogenated castor oils, fumed silica, crosslinked acrylates, and utilized in amounts of from 10 to 30 parts by weight per 100 parts by weight of prepolymer. The amount of UV absorbers are generally very small, usually less than 1 or 2 parts by weight per 100 parts by weight of prepolymer and include the various hindered amines, benzotriazoles, and hindered phenols. The plasticizers can include the various phthalates, the various adipates such as dioctyl adipate, dipropylene glycol dibenzoate, in amounts of from 15 to 50 parts by weight per 100 parts by weight of prepolymer. Solvents are generally utilized to adjust the viscosity of the prepolymer or base component to a desired range and constitute less than 10% volatility of the total composition. Suitable solvents include naphthalene, toluene, xylene. Pigments such as titanium dioxide, iron oxides, carbon black, can be utilized in suitable amounts to achieve a desired color. It is noted that the curing agent component can also contain some of the above compounds such as the fillers, the thickening agents, the plasticizers, the pigments. The amount of the prepolymer component with respect to the curing agent component can vary over a wide range depending upon a desired end use with a preferred range often being from 10 parts to 12 parts by weight of the prepolymer component per 1 part by weight of curing agent component. The polyurethane sealant composition of the present invention naturally is stored as two separate components. It is then combined and immediately applied to a substrate, to achieve a desired utility such as forming a sealant between curtain wall sections, between concrete, between stone, or between any construction material. The polyurethane sealant composition of the present invention has certain inherent advantages over conventional free isocyanates and polyol cure systems in that the prepolymer component containing the blocked isocyanate prepolymer is more stable than free isocyanate systems. Since the prepolymer component system is not predried or prereacted, it can contain additives that normally would react with free isocyanate such as hydrogenated castor oil, alcohols. The cure time can be adjusted from instantaneous, that is, a few seconds, hours or even longer, by varying the concentration of the catalyst. The DBU compound or DBU derivative is a true catalyst and final properties are unaffected by its presence. Other conventional urethane catalysts such as tin salts have been found not to work with regard to the blocked isocyanate prepolymer. The fast cure times of the present invention are accomplished at room temperature, that is at ambient or even sub-ambient temperatures as from 0°C to 60°C, and preferably from 20°C to 30°C. The polyurethane sealant compositions of the present invention will be better understood by reference to the following example. EXAMPLE A prepolymer component was prepared from the following compounds. The urethane prepolymer was made from an ethylene oxide end capped (approximately 5% by weight) polyoxypropylene triol reacted with toluene diisocyanate and subsequently blocked with nonyl phenol. BASE COMPONENT FORMULATION DESCRIPTION OF THE CHEM. ITEM PARTS BY WEIGHT 6,000 molecular wt. trifunctional blocked isocyanate prepolymer 100 Hydrogenated castor oil 14 Calcium Carbonate 60 Aliphatic Solvent, Naphtha 3 Dipropylene Glycol Dibenzoate 20 Pigment, TiO₂, carbon black, iron oxides 8 UV Stabilizer, benzotriazole/hindered amine 0.5 The prepolymer composition was prepared as follows: 33 1/3 parts of the urethane prepolymer was added to a clean caulk mixer rotating at 5 RPM along with the UV stabilizers and the hydrogenated castor oil. The compounds were mixed at 20 RPM for 15 minutes until uniform and then an additional 33 1/3 parts by weight of the prepolymer was added along with the calcium carbonate. The compounds were then mixed for 15 minutes at 20 RPM until well dispersed and examined for lumps. When no lumps remained, the remaining 33 1/3 parts by weight of the prepolymer was added along with the plasticizer. The compounds were then mixed at 15 RPM under heat until the temperature reached 51.67°C - 54.44°C (125°F - 130°F). The mixer was then cooled to 46.11°C (115°F) at which time the solvent was added. Mixing was continued until a uniform blend was obtained. The curing agent component had the following formulation. CURING AGENT COMPONENT FORMULATION DESCRIPTION WT. PERCENT OF COMPOUND Dipropylene glycol dibenzoate 58 Titanium dioxide 0.9 Hydrophobic fumed silica 5.9 Methyl trimethoxy silane 0.3 BAPP 11 Jeffamine D-400 23 DBU 0.8 The preparation of the curing component was as follows. Into a clean mixer under a nitrogen atmosphere was charged the dipropylene glycol dibenzoate plasticizer, the titanium dioxide pigment, and the fumed silica and mixed at 40 RPM for 5 minutes. The methyl trimethoxy silane drying agent was then added and mixed at 20 RPM for about 10 minutes. The amine curing agent and the DBU catalyst were then added and mixed at 20 RPM for about 10 minutes. A vacuum was pulled to 914 hPa (27 inches of mercury) until the composition was completely de-aired and packaged. The base component and the curing agent component were mixed in the desired stoichiometric proportion of 1 to 1, that is approximately 12 parts by weight of the base component to approximately 1 part by weight of the curing agent component. The components were applied from a two component meter-mix pump with a static mixing device on the nozzle. The mixed composition was then applied between aluminum and granite curtain wall sections and formed a sealed joint. The joint was flexible and good adhesion was obtained within 20 minutes. The sealant compositions of the present invention have excellent storage stability in sealed containers, have excellent flowability characteristics and thus can be pumped or utilized in caulking guns, have good flexibility and pliability, do not shrink objectionally upon curing, and have good adhesion to various primed substrates. While in accordance with the patent statutes, a best mode and preferred embodiment have been set forth in detail, the scope of the present invention is not limited thereto, but rather by the scope of the attached claims.

Claims: A polyurethane sealant composition, comprising: a cured polyurethane, said cured polyurethane made from a polyurethane prepolymer having blocked isocyanate groups, a curing agent, and an effective amount of a bicyclic amidine catalyst or a derivative thereof, said curing agent having at least two primary amine groups therein, wherein said blocked urethane prepolymer is made from a polyester polyol (excluding polycarbonate polyols), a polybutadiene polyol, or a polyether polyol, and an aromatic polyisocyanate with a blocking agent subsequently blocking terminal isocyanate groups, wherein the blocking agent is selected from phenol, 3-methoxyphenol, 4-methoxyphenol, nonylphenol, meta-cresol, para-cresol, 4-chlorophenol, meta-hydroxybenzaldehyde, ortho-hydroxybenzaldehyde, para-hydroxybenzaldehyde, hydroquinone, 1-hydroxy-2-propanone, 3-hydroxyacetophenone, 4-hydroxyacetophenone, ethyl acetyl acetate and cyclohexanone oxime. A polyurethane sealant composition according to claim 1, wherein said bicyclic amidine catalyst is 1,8-diaza bicyclo(5:4:0)undecene-7, (DBU), wherein said derivative of said catalyst is the reaction product of said catalyst with phenol, a sulfonic acid, a sulfimide, a sulfamide, a phosphonic acid, a N-sulfonylcarboxamide having a total of from 2 to 36 carbon atoms, or a carboxylic acid having from 2 to 18 carbon atoms. A polyurethane sealant composition according to claim 2, wherein said effective amount of said catalyst is from 0.01 to 2.5 parts by weight per 100 parts by weight of said prepolymer, and wherein said catalyst derivative is the reaction product of DBU with phenol or 2-ethylhexanoic acid. A polyurethane sealant composition according to claim 3, wherein the amount of said catalyst is from 0.02 to 1.2 parts by weight per 100 parts by weight of said prepolymer. A polyurethane sealant composition according to claim 4, wherein said catalyst is said 1,8-diaza bicyclo(5:4:0)undecene-7 or a phenol reaction product thereof. A polyurethane sealant composition according to claim 5, wherein the amount of said catalyst is from 0.1 to 0.25 part by weight per 100 parts by weight of said prepolymer. A polyurethane sealant composition according to claim 2, wherein said prepolymer is made from a poly(oxyalkylene) diol or triol, wherein said alkylene group has from 2 to 6 carbon atoms, wherein said poly(oxyalkylene) diol or triol is optionally end capped with ethylene oxide block polymers wherein the total amount of said block polymers is 10% by weight or less based upon the total weight of said end capped poly(oxyalkylene) diol or triol, and wherein the equivalent weight of said poly(oxyalkylene) diol or triol is from 500 to 10,000. A polyurethane sealant composition according to claim 3, wherein said prepolymer is made from a poly(oxyalkylene) diol or triol, wherein said alkylene group has from 2 to 6 carbon atoms, wherein said poly(oxyalkylene) diol or triol is optionally end capped with ethylene oxide block polymers wherein the total amount of said block polymers is 10% by weight or less based upon the total weight of said end capped poly(oxyalkylene) diol or triol, wherein the equivalent weight of said poly(oxyalkylene) diol or triol is from 500 to 3,000, and wherein said aromatic polyisocyanate is an aromatic diisocyanate. A polyurethane sealant composition according to claim 4, wherein said prepolymer is made from a poly(oxypropylene) diol or triol, wherein said poly(oxypropylene) diol or triol is optionally end capped with ethylene oxide block polymers wherein the total amount of said block polymers is 10% by weight or less based upon the total weight of said end capped poly(oxyalkylene) diol or triol, wherein the equivalent weight of said poly(oxypropylene) diol or triol is from 500 to 3,000, wherein said aromatic polyisocyanate is an aromatic diisocyanate, and wherein said amine curing agent has a total of from 3 to 260 carbon atoms or is a polymer having a molecular weight up to 5,000. A polyurethane sealant composition according to claim 5, wherein said prepolymer is made from a poly(oxypropylene) diol or triol, wherein said poly(oxypropylene) diol or triol is optionally end capped with ethylene oxide block polymers wherein the total amount of said block polymers is 5% by weight or less based upon the total weight of said end capped poly(oxypropylene) diol or triol, wherein the equivalent weight of said poly(oxypropylene) diol or triol is from 1,000 to 2,100, wherein said blocking agent is nonylphenol, wherein said aromatic polyisocyanate is toluene diisocyanate, and wherein said amine curing agent has a total of from 6 to 36 carbon atoms or is a polymer having a molecular weight of from 200 to 450. A curable polyurethane composition, comprising, a polyurethane prepolymer component, said polyurethane prepolymer component is made from a polyester polyol, a polybutadiene polyol, or a poly(oxyalkylene) polyol and an aromatic polyisocyanate, said alkylene group of said poly(oxyalkylene) polyol having from 2 to 6 carbon atoms, said polyurethane prepolymer having blocked isocyanate groups, and a curing agent component, said curing agent component comprising an amine curing agent containing at least two primary amines, and an effective amount of a bicyclic amidine catalyst or a derivative thereof capable of unblocking said blocked isocyanate groups. A curable polyurethane composition according to claim 11, wherein said bicyclic amidine catalyst is 1,8-diaza bicyclo(5:4:0)undecene-7, (DBU), wherein said derivative of said catalyst is the reaction product of said catalyst with phenol, a sulfonic acid, a sulfimide, a sulfamide, a phosphonic acid, a N-sulfonylcarboxamide having a total of from 2 to 36 carbon atoms, or a carboxylic acid having from 2 to 18 carbon atoms, and wherein said blocked urethane prepolymer is made from a polyester polyol, a polybutadiene polyol, or a polyether polyol, and an aromatic polyisocyanate with a blocking agent subsequently blocking terminal isocyanate groups, and wherein the amount of said catalyst is from 0.01 to 2.5 parts by weight per 100 parts by weight of said prepolymer. A curable polyurethane composition according to claim 12 wherein said derivative is the reaction product of DBU with phenol or 2-ethyl hexanoic acid. A curable polyurethane composition according to claim 13, wherein said prepolymer is made from a poly(oxyalkylene) polyol, wherein said poly(oxyalkylene) polyol has an equivalent weight of from 500 to 3,000, wherein said poly(oxyalkylene) polyol optionally has ethylene oxide end blocks with the total amount of said ethylene oxide end blocks being 10% by weight or less based upon the total weight of said end blocked poly(oxyalkylene) polyol, wherein said polyisocyanate is an aromatic diisocyanate, and wherein said amine curing agent contains a total of from 3 to 260 carbon atoms or is a polymer having a molecular weight up to 5,000. A curable polyurethane composition according to claim 14, wherein the amount of said catalyst is from 0.02 to 1.2 parts by weight per 100 parts by weight of said prepolymer. A curable polyurethane composition according to claim 14, wherein said poly(oxyalkylene) polyol is a poly(oxypropylene) diol or triol, and wherein said aromatic diisocyanate is toluene diisocyanate. A curable polyurethane composition according to claim 16, wherein a blocking agent forms said blocked prepolymer, wherein said blocking agent is is phenol, 3-methoxyphenol, 4-methoxyphenol, nonylphenol, meta-cresol, para-cresol, 4-chlorophenol, meta-hydroxybenzaldehyde, ortho-hydroxybenzaldehyde, para-hydroxybenzaldehyde, hydroquinone, 1-hydroxy-2-propanone, 3-hydroxy-acetophenone, 4-hydroxyacetophenone, ethyl acetyl acetate and cyclohexanone oxime. A curable polyurethane composition according to claim 12 or 13, wherein said separate components are brought together and cured at a temperature of from 0°C to 60°C. A curable polyurethane composition according to claim 12 or 13, wherein said separate components are brought together and cured at a temperature of from 20°C to 30°C.

Inventors: GREENLEE, THOMAS W., HANNAH, STEVEN LANIER, WILLIAMS, MAUREEN ROSE
Applicants: TREMCO INCORPORATED
Application year: 1988
Main classification: C08G18
IPC codes: C08G18, C09K3