Process for producing pre-expanded particles of a polyolefin

Abstract: A process for producing pre-expanded particles of a thermoplastic resin, wherein said particles are of a polyolefin obtained by polymerizing an olefin in the presence of a Ziegler-Natta catalyst, and contain not more than 1% by weight of particles of diameter up to 105 µm and having a particle size distribution represented by: R(Dp) = 100exp[-(Dp/De) n ] where Dp is300 or more and represents a particle diameter (µ m); R(Dp) represents a cumulative weight percent­ age; De represents an absolute size constant that is a particle diameter (µm) corresponding to R(Dp) 36.8% by weight; and n is 25 or more and is a distribution con­ stant. The process can be carried out by dispersing the particles in a liquid medium (e.g. water) containing a blowing agent (e.g. an aliphatic hydrocarbon) and a phenolic antioxidant, heating to above the softening point of the polymer, and releasing the dispersion into a zone of lower pressure. Pre-expanded polyolefin particles free from scat­ ters of cell diameter or particle diameter and having a high expansion ratio are obtained, which can be put into a mold for expansion molding to easily provide a uniformly expanded article.

Description: This invention relates to a process for producing pre-expanded particles of a polyolefin. It has hitherto been known that a thermoplastic resin composition is pre-expanded without inducing crosslinking by dispersing thermoplastic resin particles containing a volatile blowing agent in water while stirring in a pressure-resistant container, such as an autoclave, and releasing the dispersion into a lower pressure zone while being kept at a high temperature under a high pressure, as described in West German Patent Application (OLS) No. 2,107,683 and JP-B-56-1344. EP-A-0123816 discloses a process of making pre-expanded particles of polyolefin, e.g. polyethylene, by dispersing the particles and a blowing agent into water, heating the dispersion and releasing the dispersion into an atmosphere of lower pressure; the melt tension of the polymer is less than 1500. Polystyrene can be obtained in the form of spherical resin particles by suspension polymerization, and pre-expanded particles prepared by using the polystyrene particles have a spherical form. On the other hand, pre-expanded particles of polyolefin resins, e.g., polyethylene and polypropylene, can be obtained by using uncrosslinked resin particles, whereas pre-expanded particles having a spherical form and a uniform cell diameter can hardly be obtained from pellets or pulverized pellets of polyolefin resins and, moreover, the resulting pre-expanded particles have a scatter of their expansion ratio. Such irregular pre-expanded particles cannot be effectively charged into a mold, and so it is not possible to obtain therefrom a uniformly expanded molded article. Therefore, there is room for further improvment in a process for producing pre-expanded particles of polyolefin resin. One object of this invention is to provide a process for easily producing pre-expanded particles having a high expansion ratio directly from polyolefin polymer particles without using pellets or pulverized pellets of the polymer particles. Another object of this invention is to provide a process for producing pre-expanded particles of polyolefins which can be charged into a mold efficiently to easily provide a uniform expansion-molded article. It has now been found that the above objects of this invnetion can be accomplished by using polyolefin particles having a specific diameter and size distribution. The present invention relates to a process for producing pre-expanded particles of polyolefin which process comprises dispersing polyolefin particles and a blowing agent in a dispersing medium, heating the dispersion, and releasing the dispersion into a zone of lower pressure, characterised in that said starting polyolefin particles are obtained by polymerizing an olefin in the presence of a Ziegler-Natta catalyst, said polyolefin particles containing no more than 1% by weight of particles having a particle diameter of 105 µm or smaller and having a particle size distribution represented by the equation: R(Dp) = 100exp[-(Dp/De) n ] wherein Dp represents a polymer particle diameter (µm); R(Dp) represents a residual cumulative weight percentage; De represents an absolute size constant that is a particle diameter (µm) corresponding to R-(Dp) = 36.8% by weight; and n represents a distribution constant, in which De is 300 or more, and n is 2.5 or more, and then charged directly into the dispersion mixture. The process is preferably carried out by dispersing the above-described polyolefin particles in a dispersing medium, heating the dispersion, and releasing the dispersion into a zone of lower pressure, wherein said dispersing medium contains a phenolic antioxidant. The polyolefin particles which can be used in the present invention are particles obtained by polymerization of an olefin and do not contain 1% by weight or more, preferably 0.5% by weight or more, of particles having a diameter of 105 µm or smaller. Those polymer particles having a diameter of 105 µm or smaller are hardly expanded and therefore are not preferred. Uniformly and spherically pre-expanded particles can be obtained by starting with the polyolefin polymer particles having a narrow particle size distribution. The size distribution of polymer particles is generally represented by Rosin-Rammler's distribution equation as described in Funtai Kogaku Binran - ("Handbook of Powder Technology"), pp. 7-10, The Society of Powder Technology, Japan, which is quoted above: (R(Dp) = 100exp[-(Dp/De) n ]) In that equation, the smaller is the n value, the broader is the size distribution. The polyolefin polymer particles to be used in the present invention must have a De value of 300 or more, preferably 400 or more, and n value of 2.5 or more, preferably 3 or more. If the polymer particles have too broad a size distribution, there would be an undesired distribution of expansion ratio among the resulting pre-expanded particles. The polyolefin polymer particles to be used in the present invention can be produced by homo- or copolymerization of an olefin (e.g., ethylene, propylene, butene-1, pentene-1, hexene-1, 3-methylbutene-1, 4-methylpentene-1, octene-1, decene-1 or octadecene-1) in the presence of a Ziegler-Natta catalyst by a gaseous phase process, or a solvent-free liquid phase process. The polyolefin polymer particles preferably include linear low-density polyethylene, low-, medium- or high-density polyethylene, polypropylene and polypropylene copolymers. A Ziegler-Natta catalyst comprises a compound of a transition metal of Groups IV to VIII of the Periodic Table and an organometallic compound. Generally employed transition metal compounds contain as the metal titanium, zirconium or chromium. Particularly preferred catalysts comprise combinations of a Ti-containing compound and an organoaluminum compound. More preferred are high-activity catalysts comprising a titanium trichloride composition or a Ti-Mg-containing composition as a Ti-containing component. Processes for preparing these high-activity catalysts are not particularly restricted, and any known techniques may be adopted as far as the catalyst allows the production of the above-defined polymer particles. Pre-expansion of the polyolefin polymer particles can be carried out, for example, by a process in which the particles are placed in a closed container, and a volatile blowing agent is directly poured into the container to impregnate into the particles; or a process in which the particles are dispersed in a dispersing medium in a closed container with the aid of a small amount of a dispersing agent, and a volatile blowing agent is then impregnated into the particles. The blowing agent which can be used in the present invention includes aliphatic hydrocarbons, e.g., propylene, butane, pentane or hexane; alicyclic hydrocarbons, e.g., cyclopentane or cyclobutane; and halogenated hydrocarbons, e.g., trichloromonofluoromethane, dichlorodifluorometane, dichlorotetrafluoroethane, trichlorofluoroethane, methyl chloride, methylene chloride or ethyl chloride. These blowing agents may be used either individually or in combination of two or more thereof. The amount of the blowing agent to be used is not particularly critical and can be selected appropriately depending on a desired degree of expansion, usually in an amount of 5 to 50 parts by weight per 100 parts by weight of the polymer particles to be pre-expanded. The dispersing agent to be used can be calcium tertiary phosphate, basic magnesium carbonate, basic zinc carbonate and calcium carbonate; or a small amount of a surface active agent, such as sodium dodecylbenzenesulfonate, a sodium n -paraffinsulfonates or a sodium o-olefinsulfonate. The dispersing medium to be used may be any solvent incapable of dissolving the polymer particles and includes, for example, water, ethylene glycol, glycerin, methanol, ethanol, and mixtures thereof, with water being usually preferred. It is preferable to add at least one phenolic antioxidant to the dispersing medium so as to form uniform cells on pre-expansion. Specific examples of the phenolic antioxidant are 2,6-di-t-butyl-4-methylphenol, triethylene glycol-bis[3-(3-t-butyl-5-methyl-4-hydroxyphenyl)propionate], 1,6-hexanediol-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate],pentaerythrityl-tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate], 2,2-thiodiethylenebis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate],octadecyl-3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate, 2,2-thiobis(4-methyl-6-t-butylphenol), 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, tris(3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate, 4,4'-thiobis(3-methyl-6-t-butylphenol), 2,2-methylenebis(4-methyl-6-t-butylphenol), tris(2-methyl-4-hydroxy-5-t-butylphenyl)butane, 2,2'-ethylidenebis(4,6-di-t-butylphenol), 2-t-butyl-6-(3'-t-butyl-5'-methyl-2'-hydroxybenzyl)-4-methylphenyl acrylate and 3,9-bis[2-{3-(3-t-butyl-4-hydroxy-5-methylphenyl)propionyloxy}-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane. If desired, the dispersing medium may further contain other additives, such as phosphorus type anti-oxidants, sulfur type antioxidants, copper inhibitors, photostabilizers, ultraviolet absorbents, lubricants, metal fatty acid salts, nucleating agents, antistatic agents, and the like. Specific examples of the phosphorus type anti-oxidants are trioctyl phosphite, trilauryl phosphite, tridecyl phosphite, tris(2,4-di-t-butylphenyl) phosphite, triphenyl phosphite, tris(nonylphenyl) phosphite, distearylpentaerythritol diphosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite, bis(2,6-di-t-butyl-4-methylphenyl)pentaerythritol diphosphite, tris[4,4'-isopropylidenebis(2-t-butylphenol] phosphite, di-(nonylphenyl)pentaerythritol diphosphite and tetrakis(2,4-di-t-butylphenyl)-4,4'-biphenylene diphosphonite. Specific examples of the sulfur type anti-oxidants are dialkyl thiodipropionates (e.g., dilauryl thiodipropionate, dimyristyl thiodipropionate, and distearyl thiodipropionate), esters of alkylthiopropionic acids (e.g., butylthiopropionic acid, octylthiopropionic acid, laurylthiopropionic acid, and stearylthiopropionic acid) and polyhydric alcohols (e.g., glycerin, trimethylolethane, trimethylolpropane, pentaerythritol, trishydroxyethyl isocyanurate), such as pentaerythritol tetrakis(dodecylthiopropionate). Specific examples of the photostabilizers are bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate, 4-benzoyloxy-2,2,6,6-tetramethylpiperidine, a polycondensate of succinic acid and N-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine, 1,2,3,4-tetra(2,2,6,6-tetramethyl-4-piperidyl) butanetetracarboxylate, 1,4-di(2,2,6,6-tetramethyl-4-piperidyl)-2,3-butanedione, tris(2,2,6,6-tetramethyl-4-piperidyl) trimellitate, 1,2,2,6,6-pentamethyl-4-piperidyl stearate, 1,2,2,6,6-pentamethyl-4-piperidyl n-octoate, bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, tris(2,2,6,6-tetramethyl-4-piperidyl)nitrile acetate, 4-hydroxy-2,2,6,6-tetramethylpiperidine, 4-hydroxy-1,2,2,6,6-pentamethylpiperidine, poly[(6-morpholino-s-triazin-2,4,diyl)[(2,2,6,6-tetramethyl-4-piperidyl)imino]hexamethylene[(2,2,6,6-tetramethyl-4-piperidyl)imino]], , poly[[6-(1,1,3,3-tetramethylbutyl)imino-1,3,5-triazin-2,4-diyl][[2,2,6,6-tetramethyl-4-piperidyl)imino]hexamethylene[(2,2,6,6-tetramethyl-4-piperidyl]imino]], a polycondensate of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 1,2-dibromoethane. Specific examples of the ultraviolet absorbents are hydroxybenzophenones, e.g., 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-octoxybenzophenone, 2-hydroxy-4-stearyloxybenzophenone, 2-hydroxy-4-dodecyloxybenzophenone; benzoates, e.g., phenyl salicylate, 2,4-di-t-butylphenyl 3',5'-di-t-butyl-4'-hydroxybenzoate, 4-octylphenyl 3,5-di-t-butyl-4-hydroxybenzoate; and benzotriazoles, e.g., 2-(2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(2'-hydroxy-5'-t-butylphenyl)benzotriazole, 2-(2'-hydroxy-5'-octylphenyl)benzotriazole, 2-(2'-hydroxy-4'-octoxyphenyl)benzotriazole, 2-(2'-hydroxy-3',5'-di-t-butylphenyl)benzotriazole, 2-(2'-hydroxy-3',5'-di-t-amylphenyl)benzotriazole, 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole and 2-(2'-hydroxy-3',5'-di-t-butylphenyl)-5-chlorobenzotriazole. Specific examples of the lubricants are lauramide, palmitamide, stearamide, behenamide, erucamide, oleamide, methylenebisbehenamide, methylenebisstearamide, methylenebisoleamide, ethylenebisstearamide, ethylenebisoleamide, hexamethylenebisstearamide and N-stearylerucamide. Specific examples of the metal fatty acid salts are magnesium stearate, calcium stearate and zinc stearate. Calcium hydroxide or hydrotalcite may be used in substitution therefor. The nucleating agents include sodium salts, aluminum salts, phosphorus nucleating agents and sorbitol nucleating agents. The antioxidants are not particularly limited, and those commonly employed for polyolefins are employable. The phenolic antioxidant and other additives are added to the dispersing medium in an amount of from 0.001 to 5 parts by weight, preferably from 0.003 to 1 part by weight, more preferably from 0.01 to 1 part by weight, per 100 parts by weight of the polyolefin polymer particles. After the polyolefin polymer particles are dispersed in a dispersion medium having incorporated therein a volatile blowing agent and other additives, the dispersion is heated to a temperature above the softening point of the polyolefin polymer particles. The heating temperature is appropriately selected from a range within which the particles can be expanded without collapse of cells, usually ranging from 25°C lower than the melting point of the polymer particles to 10°C higher than the melting point of the polymer particles. Upon heating, the volatile blowing agent is impregnated into the polymer particles. Then, the inner pressure is set at a pressure no less than the vapor pressure of the volatile blowing agent, and while keeping the inner pressure at that level, an opening of the container is opened to release the dispersion into a lower pressure atmosphere to thereby pre-expand the olefin resin particles. The polyolefin resin pre-expanded particles usually have closed cells in a proportion of 80% or more. If desired, the pre-expanded particles may be aged for a given period of time. The resulting preexpanded particles can be charged into a mold and expansion-molded by steam-heating to obtain an expansion-molded article. The thus produced article shows a small percentage of dimensional shrinkage and a small distortion and therefore has an extremely heightened commercial value. The present invention is now illustrated in greater detail by referring to Examples and Comparative Examples, but the present invention is not limited thereto. The percentages are by weight. Particle size distributions of polymer particles prepared in these examples were determined by the following sieve analysis. A sample weighing 200 g was loaded on a sieve having a sieve opening of 105 µm, 125 µm, 177 µm, 250 µm, 297 µm, 350 µm, 420 µm, 500 µm, 590 µm, 710 µm or 1190 µm, and sieved for 10 minutes by means of a shifting machine. The residue on the sieve was weighed, and the absolute size constant De and distribution constant n were obtained by using a Rosin-Rammler chart. EXAMPLE 1 (1) Synthesis of Titanium Trichloride: Titanium trichloride was synthesized in accordance with the process disclosed in JP-A-47-34478 (the term "JP-A" as used herein means an "unexamined published Japanese patent application") as follows. Brown titanium trichloride obtained by reduction of titanium tetrachloride with diethylaluminum chloride in an inert solvent was treated with an approximately equimolar amount of diisoamyl ether at room temperature and then chemically treated with a hexane solution of titanium tetrachloride at 65°C. (2) Synthesis of Polypropylene Polymer: In a 300 ℓ-volume autoclave equipped with a stirrer and purged with nitrogen was charged 150 ℓ of heptane. Then, 1.5 g of titanium trichloride and 10 times the molar amount of diethylaluminum chloride were added thereto. The mixture was heated to 60°C, and propylene, ethylene, and hydrogen were fed thereto to effect polymerization for 15 hours while maintaining the gaseous phase concentrations constant by gas chromatography. The unreacted gases were purged out of the system, and the resulting polymer slurry was withdrawn into a washing tank. Into the tank was poured 40 ℓ of methanol, followed by stirring at 60°C for 1 hour to decompose the catalyst. Then 100 ℓ of water was poured in, followed by stirring for 30 minutes. The mixture was subjected to centrifugation, and the solid was dried in a drier to obtain polymer particles. The resulting polypropylene polymer particles had an intrinsic viscosity [η] of 1.70 as measured in tetralin at 135°C and an ethylene content of 4.5%. The particle size distribution of the polymer particles had an absolute size constant De of 750 and a distribution constant n of 10. The proportion of particles having a diameter of 105 µm or smaller was found to be 0.03%. (3) Production of Pre-Expanded Particles: In a 5 ℓ-volume autoclave were charged 1,000 g of the polymer particles prepared in (2) above, 350 g of dichlorofluoromethane, 5 g of basic calcium tertiary phosphate and 0.06 g of sodium n-paraffinsulfonate as dispersing agents, and 3,000 g of water, and the mixture was heated to 137°C. While introducing dichlorodifluoromethane into the autoclave to keep the inner pressure constant, the aqueous dispersion in the autoclave was released by opening a valve at the bottom of the autoclave into the atmosphere to effect pre-expansion. The resulting pre-expanded particles were weighed for expansion ratio and scatters of particle size, form and cell diameter. The results obtained are shown in Table 1. When the pre-expanded particles were charged into a mold, heated and expanded, the resulting expansion-molded article was substantially free from distortion. COMPARATIVE EXAMPLE 1 Polypropylene polymer particles were prepared in the same manner as in Example 1-(2), except for replacing the titanium trichloride as used in Example 1-(2) with AA type titanium trichloride produced by Toho Titanium Co., Ltd. The resulting polypropylene polymer particles had an [η] of 1.72 and an ethylene content of 4.4%. The absolute size constant De and distribution constant n of the particle size distribution were 600 and 1.1, respectively. The proportion of particles having a diameter of 105 µm or smaller was 12%. The polymer particles were pre-expanded in the same manner as in Example 1-(3). The results obtained are shown in Table 1. EXAMPLE 2 In a 5 ℓ-volume autoclave were charged 1000 g of the same polymer particles as prepared in Example 1-(2), 350 g of dichlorodifluoromethane, 5 g of basic calcium tertiary phosphate, 0.06 g of sodium n-paraffinsulfonate, 0.2 g of 2,6-di-t-butyl-4-methylphenol, 0.15 g of tetrakis[methylene-3-(3',5'-di-t-butyl-4-hydroxyphenyl)propionate]methane, and 3,000 g of water. The mixture was heated to 137°C and then pre-expanded in the same manner as in Example 1-(3). The results obtained are shown in Table 1. EXAMPLE 3 (1) Synthesis of Solid Catalyst: A solid catalyst was synthesized in accordance with the process disclosed in JP-A-60-228504 as follows. Tetra-n-butoxytitanium was reduced with ethylaluminum sesquichloride in n-heptane. To the resulting reddish brown solid product was added triethylaluminum, and ethylene was preliminarily polymerized (amount of the preliminary polymer was 0.1 g per gram of the solid product). Then, the product was treated with an equimolar amount of diisoamyl ether at 30°C, and titanium tetrachloride was added thereto, followed by further treating at 75°C to obtain a solid catalyst. (2) Synthesis of Polypropylene Polymer Particles: Polymerization was carried out in the same manner as in Example 1-(2), except for using the titanium trichloride catalyst as prepared in (1) above. The resulting polypropylene polymer particles had an [η] of 1.71 and an ethylene content of 4.4%. The absolute size constant De and distribution constant n were 900 and 12, respectively. The proportion of particles having a diameter of 105 µm or smaller was 0.02%. The polymer particles were pre-expanded in the same manner as in Example 1-(3). The results obtained are shown in Table 1. EXAMPLE 4 (1) Synthesis of Solid Catalyst: A solid catalyst was synthesized in accordance with the process disclosed in JP-A-61-218606 as follows. n-Butylmagnesium chloride was added dropwise to an n-heptane solution containing 1 part of tetrabutoxytitanium and 17 parts of tetraethoxysilane to obtain a brown solid product. The product was treated with a toluene solution of diisobutyl phthalate at 80°C and then with a toluene solution of n-butyl ether and titanium tetrachloride at 95°C to obtain a solid catalyst. (2) Synthesis of Polypropylene Polymer Particles: In a 300 ℓ-volume autoclave equipped with a stirrer and having been purged with nitrogen was charged 150 ℓ of heptane, and 0.5 g of the solid catalyst as prepared in (1) above, 57 mmols of triethylaluminum, and 57 mmols of phenyltriethoxysilane were added thereto. Propylene, ethylene, and hydrogen were then fed thereto to effect polymerization at 60°C for 10 hours to obtain polypropylene polymer particles. The resulting polymer particles had an [η] of 1.70 and an ethylene content of 4.5%. The absolute size constant De and distribution constant n were 950 and 10, respectively. The proportion of particles having a diameter of 105 µm or smaller was 0.01%. The polymer particles were pre-expanded in the same manner as in Example 1-(3). The results obtained are shown in Table 1. COMPARATIVE EXAMPLE 2 Pre-expanded particles were obtained in the same manner as in Comparative Example 1, except that 0.2 g of 2,6-di-t-butyl-methylphenol and 0.15 g of tetrakis[methylene-3-(3',5'-di-t-butyl-4-hydroxyphenyl)propionate]methane were further added to the mixture to be pre-expanded. The results obtained are shown in Table 1. COMPARATIVE EXAMPLE 3 Polypropylene polymer particles were obtained in the same manner as in Example 1-(2), except that polymerization was carried out for 30 minutes. The resulting polymer particles had an [η] of 1.72 and an ethylene content of 4.5%. The absolute size content De and distribution constant n were 260 and 9, respectively. The proportion of particles having a diameter of 105 µm or smaller was 0.3%. The polymer particles were pre-expanded in the same manner as in Example 1-(3). The results obtained are shown in Table 1. Example No. Pre-Expansion Ratio Scatter of Pre-Expanded Particle Size Form of Pre-Expanded Particles Scatter of Cell Diameter* Example 1 About 8 small spherical fair " 2 about 8 " " good " 3 about 13 " " " " 4 about 15 " " " Comparative about 4 large amorphous bad Example 1 " 2 about 4 " " " " 3 no-substantial expansion - - - Note: * Each of 20 pre-expanded particles per sample was vertically cut at the center, and the cut surface was observed under 50× magnification. The scatter of the cell diameter was evaluated according to the following rating system: Good No substantial scatter was observed among particles or within individual particles. Fair Slight scatter was observed among particles or within individual particles Bad Scatter was observed among particles or within individual particles As described above, the process according to the present invention provides pre-expanded resin particles free from scatters of cell diameter or particle diameter without using pelletized polymer particles or pulverized pellets of polymer particles. Thus, the present invention makes it possible to easily obtain pre-expanded particles of high expansion ratio directly from polyolefin polymer particles, which can be efficiently charged in a mold for expansion molding to easily provide a uniform expanded article.

Claims: A process for producing pre-expanded particles of polyolefin which process comprises dispersing polyolefin particles and a blowing agent in dispersing medium, heatingthe dispersion, and releasing the dispersion into a zone of lower pressure, characterised in that said starting polyolefin particles are obtained by polymerizing an olefin in the presence of a Ziegler-Natta catalyst, said polyolelin particles containing no more than 1% by weight of particles having a particle diameter of 105 µm or smaller and having a particle size distribution represented by the equation: R(Dp) = 100exp[-(Dp/De) n ] wherein Dp represents a polymer particle diameter (µm); R(Dp) represents a residual cumulative weight percentage; De represents an absolute size constant that is a particle diameter (µm) corresponding to R(Dp) = 36.8% by weight; and n represents a distribution constant, in which De is 300 or more, and n is 2.5 or more, and then charged directly into the dispersion mixture. A process as claimed in Claim 1, wherein said polyolefin particles contain no more than 0.5% by weight of particles having a particle diameter of 105 µm or smaller. A process as claimed in Claim 1 or 2, wherein De is 400 or more, and n is 3 or more. A process as claimed in Claim 1, 2 or 3, wherein said polyolefin particles are particles of linear low-density polyethylene, low-, medium- or high-density polyethylene, polypropylene or a propylene copolymer. A process as claimed in any preceding claim, which process comprises dispersing said polyolefin particles in a dispersing medium containing from 0.001 to 5 parts by weight of a phenolic antioxidant per 100 parts by weight of the polyolefin particles.

Inventors: FUKUI YOSHIHARU, FUKUI, YOSHIHARU
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1988
Main classification: C08J9
IPC codes: C08J9