Biaxially oriented multilayer barrier films

Abstract: Films having a core of ethylene-vinyl alcohol copolymer (EVOH) sandwiched between polyolefin, e.g. polypropylene are coextruded so that the polyolefin also surrounds the EVOH layer on the side edges. The films, which can contain adhesive layers are oriented to a deformation ratio which is from greater than 4 in the machine direction and to a deformation ratio which is from greater than 7 in the transverse direction to give excellent oxygen and moisture barrier properties.

Description: This invention relates to biaxially oriented multilayer barrier films; to processes for their preparation; and to their use in food packaging. More particularly, this invention relates to such films when comprising ethylene vinyl alcohol copolymer (EVOH) and polypropylene. EVOH films are excellent barriers to oxygen, carbon dioxide and nitrogen. They are also effective barriers against odors and the loss of flavor. EVOH resins are, however, moisture sensitive and their barrier properties are reduced in the presence of high humidity. Polypropylene offers excellent moisture barrier properties, together with good strength properties and a high use temperature. When EVOH resins are surrounded by layers of polypropylene, they are protected from moisture and therefore retain their barrier characteristics. U.S. Patent 4561920 discloses a method of producing a biaxially oriented oxygen and moisture barrier film which comprises first co-extruding at least one polyolefin layer of a polyolefin selected from the group consisting of polyethylene, polypropylene and copolymers of ethylene with other olefin monomers, at least one layer of an ethylen vinyl alcohol copolymer with a melt flow rate of at least about 8 grams per 10 minutes, and at least one adhesive layer wherein these layers are combined into a composite sheet with the adhesive interposed between the core layer and the EVOH. Next, the composite sheet is immediately cooled so that the crystallinity of the EVOH is no more than about 25%. Finally, the composite sheet is biaxially oriented in the longitudinal direction to a degree of about 2:1 to about 4:1 and in the transverse direction to a degree of about 3:1 to about 7:1. That specification also discloses a biaxially oriented oxygen and moisture barrier film formed by the above method. EP-A-0 133 188 discloses a process and an apparatus for producing a hot-formed plastic composite which has a core layer of ethylene vinyl alcohol copolymer and outermost layers consisting of polypropylene and which is biaxially oriented after having been heated inductively. The present invention seeks to provide biaxially oriented multilayer barrier films of improved film quality. Accordingly, the present invention provides a multilayer coextruded film which has been biaxially oriented to a deformation ratio which is from 5:1 to 7:1 in the machine direction and to a deformation ratio which is from greater than 7:1 to 10:1 in the transverse direction, which film comprises : (1) at least one (C) layer of an ethylene vinyl alcohol copolymer; and (2) at least two (A) layers, on opposite sides of the (C) layer, of polyethylene, polypropylene, poly (alpha-methylpentene), or a copolymer of ethylene with a higher olefin, and wherein the (A) layers surround the (C) layer on its top, bottom and sides. The resulting film exhibits better barrier properties to moisture and gases such as oxygen than prior art films which are oriented to a lesser degree. A very suitable such film is one wherein at least two adhesive layers (B) are contiguous with the (C) and (A) layers to form the configuration ABCBA in which the (B) layers are surrounded by the (A) layers on their surfaces opposite to the (C) layer and on their sides. Preferably the (A) layer of the film of this invention comprises polypropylene. It is also preferred that the orientation is to a deformation ratio from 8:1 to 10:1 in the transverse direction. EVOH used in invention is the saponified or hydrolyzed product of an ethylene-vinyl acetate copolymer having, generally, an ethylene content from 25 to 75 mole percent. It is preferred that the percent ethylene in the EVOH be at least 45 percent so that the EVOH is flexible enough to be stretched during the orientation process. The degree of hydrolysis should reach at least 96 percent, preferably at least 99 percent. It is also preferred that the degree of hydrolysis be greater than 96 percent because below that the barrier properties are less than optimum. In general, those skilled in the art know that it desirable that the melt flow rate of the EVOH be at least 4 grams per 10 minutes at 190°C and a load of 2,160 grams for melt viscosity match between EVOH, adhesive and polypropylene. If the melt flow rate is less than 4 grams per 10 minutes then the viscosities of the EVOH, adhesive, and skin layer are difficult to match. It is important to match the viscosities of these materials to avoid interfacial instability which causes waviness of the melt and uneven distribution of the layers, otherwise known as flow disturbance. The viscosity of these materials is most easily and effectively matched by monitoring the melt flow rate of the materials. In the present invention, however, excellent PP/adhesive/EVOH viscosity match was achieved with EVOH copolymer resins with melt flow rate ranging between 14 to 18 gm. per 10 minutes at 190°C. The polyolefin can be polyethylene, including high density polyethylene and linear low density polyethylene, polypropylene, poly (alpha-methylpentene) and copolymers of ethylene with other olefins. The preferred polyolefins are polypropylene and ethylene-propylene copolymers containing predominately propylene. The melt flow rate of the polyolefin layer is preferred to be in the 2 to 6 range. For propylene-ethylene copolymers, it is preferred that the melt flow rate be from 2.5 to 6.0 grams per 10 minutes at 230°C and a load of 2,160 grams. For polypropylene, it is preferred that the melt flow rate be from 2.5 to 4.5. In this range, the viscosities of the copolymer and the polypropylene are most compatible with EVOH and the adhesive. Also, in this range, orientation of the copolymer or the polypropylene results in the best properties. The adhesive layer when used can be any of a number of proprietary materials such as described in U.S. Patent 4,561,920. Suitable adhesives include CXA-3036 (an ethylene-vinyl acetate copolymer available from Du Pont) the Admer (TM) adhesives from the Mitsui Petrochemical Company, and the Plexar (TM) family from USI chemicals. The adhesive layer can be dispensed with by including an adhesion promoter in the polyolefin layers as described in U.S. Patent 4,650,721. That specification discloses the polyolefin layers (polypropylene) which contain a maleic acid anhydride modified olefin polymer. This invention also provides a process for producing a film which comprises: (a) coextruding (1) at least one (C) layer of an ethylene vinyl alcohol copolymer with (2) at least two (A) layers, on opposite side of the (C) layer, of polyethylene, polypropylene, poly (alpha-methylpentene) or a copolymer of ethylene with a higher olefin; (b) cooling the composite sheet to a temperature from 45° to 55°C, and (c) biaxially orienting the composite sheet to a deformation ratio which is from 5:1 to 7:1 in the machine direction and deformation ratio which is from grater than 7:1 to about 10:1. The coextrusion may be accomplished by using several extruders and having the materials fed into a combining feed block; within the feed block, the materials are layered to form the multi-layer melt stream. The melt stream is then fed into a slot cast sheet die or other type of die to form the multi-layer sheet. As the sheet exits the die, it is immediately cooled by use of a cooling drum or a water bath to a temperature of 45° to 55°C, preferably from 45° to 50°C. Immediately after cooling, the composite sheet is fed into an apparatus for MD orientation of plastic material. Any such apparatus can be used in the present invention. One example would be to feed the composite sheet into a set of differential speed heated rollers to stretch the sheet in the longitudinal direction to a degree of 5:1 to 7:1. Next, the sheet can be fed to a tenter frame where it is stretched in the transverse direction to a degree of greater than 7:1 to 10:1, preferably 8:1 to 9:1. MD orientation is generally conducted by preheating the film at 135° to 150°C, stretching in the same temperature range, and annealing at about 120°C to 130°C. Preheating for TD orientation is advantageously done at 170° to 180°C, stretching at 155°C to 165°C and annealing at 165° to 170°C. The given temperature ranges are for polypropylene. They will vary for other polyolefins. For example with copolymers of ethylene and propylene the given temperature may be 5 to 10°C lower. Finally, the sheet can optionally be subjected to corona discharge treatment in the known manner to improve its surface characteristics particularly it printability. Preferably, the multilayer extrusion is conducted in a Cloeren feedblock which is commercially available and is described in U.S. Patent 4,152,387. The Cloeren feedblock permits a great degree of control of the relative thickness of the several layers and permits the extrusion of polymers which have widely differing melt flow. It has been recognized in the art that encapsulation of the inner layer or layers of a multilayer film may be desirable. In a A-B-A coextruded composite film encapsulation means that the top surface, bottom surface and both sides (machine direction) of the B layer are covered by the A layer. For example, U.S. Patents 3,398,431, 3,448,183 and 4,533,510 describe multilayer films having an encapsulated layer and dies suitable for production of such films. The production of films in which the EVOH is encapsulated by the A layer (for example polypropylene) on its sides as well as its major surfaces is an important feature of the method of this invention. Because the EVOH layer is less viscous than the polypropylene in its normal molten condition after it emerges from the Cloeren feedblock the EVOH would leak out from the edges without the polypropylene encapsulation along the machine direction edges. Accordingly, the Cloeren feedblock is modified by providing lateral cuts in the outer edges of the vane surfaces to permit greater flow of polymer at the outer edges than in the center of the feedblock whereby the outer layer or layers of polymer envelop the sides of the B core layer (EVOH). The films of this invention are suitable in a variety of applications in which moisture and gas barrier properties are desired. The films are particularly useful in food packaging. Accordingly, in accordance with a further aspect of this invention there is provided a method of packaging foodstuffs utilising the film as herein described. The invention is illustrated by the following non-limiting examples in which all parts are by weight unless otherwise specified. EXAMPLE 1 A five-layer ABCBA sheet was coextruded using three extruders to form a 2.54 x 10⁻⁵m (1.0 mil) film. The sheet comprises: a polypropylene homopolymer (A layer) an adhesive layer (B layer); an EVOH layer (C layer); a second adhesive layer (B layer); and a second polypropylene homopolymer (A layer). The molten materials were fed into a Cloeren five-layer coextrusion feedblock with an ABCBA plug where they were combined to form a single ABCBA structure. The molten composite was fed into a slot cast sheet die at 9.1m/min (30 fpm) to get the five layer sheet. This sheet was then cooled to 49°C by means of a water bath and cast drum. After cooling, the basesheet was fed into a set of differential draw heated rolls which stretched it in the longitudinal or machine direction (MD). The sheet was then fed to a tenterframe where it was stretched in the transverse direction (TD) After the biaxial orientation the film was passed through a set of corona treatment rolls to impart surface treatment and render the film printable. Main extruder (A layer): Polypropylene Fina W-472 Satellite 1 (B layer) : Adhesive DuPont CXA-3036 Satellite 2 (C layer) : EVAL EP-G grade made by Kuraray Co. Orientation Conditions: Draw Preheat, °C Stretch, °C Anneal, °C MDX 5 143 143 127 TDX 8 175 162 166 EXAMPLE 2 Similar conditions to those of Example 1 were utilised except that the degree of orientation was 5 MDX and 9.6 TDX. EXAMPLE 3 Similar conditions to those of Example 1 were utilised except that the degree of orientation was 6 MDX and 9.6 TDX. EXAMPLE 4 Similar conditions to those of Example 1 were utilised except that the degree of orientation was 7 MDX and 9.6 TDX. The Table summarizes the optical and barrier properties for the multilayer barrier films produced with the stated conditions. Briefly, an increment in orientation conditions from 5 MDX and 8 TDX to 7 MDX and 9.6 MDX, brings improvements in the final film equivalent to over 60% lower in haze, 6% higher in gloss and 30% better in oxygen barrier. The result is a clearer film with higher barrier properties. Example Orientation Optics Haze,% Gloss, % O₂ Transmission MDX TDX 1 5 8 1.6 85.6 0.97 2 5 9.6 0.9 90.1 0.82 3 6 9.6 0.7 90.3 0.75 4 7 9.6 0.6 91.0 0.68

Claims: A multilayer coextruded film which has been biaxially oriented to a deformation ratio which is from 5:1 to 7:1 in the machine direction and to a deformation ratio which is from greater than 7:1 to 10:1 in the transverse direction, which film comprises: (1) at least one (C) layer of an ethylene vinyl alcohol copolymer; and (2) at least two (A) layers, on opposite sides of the (C) layer, of polyethylene, polypropylene, poly (alpha-methylpentene), or a copolymer of ethylene with a higher olefin, and wherein the (A) layers surround the (C) layer on its top, bottom and sides. A film according to claim 1 wherein at least two adhesive layers (B) are contiguous with the (C) and (A) layers to form the configuration ABCBA in which the (B) layers are surrounded by the (A) layers on their surfaces opposite to the (C) layer and on their sides. A film according to any preceding claim wherein the (A) layers comprise polypropylene. A film according to any preceding claim wherein the orientation is to a deformation ratio from 8:1 to 10:1 in the transverse direction. A process for producing a film which comprises: (a) coextruding: (1) at least one (C) layer of an ethylene vinyl alcohol copolymer with (2) at least two (A) layers, on opposite side of the (C) layer, of polyethylene, polypropylene, poly (alpha-methylpentene) or a copolymer of ethylene with a higher olefin; (b) cooling the composite sheet to a temperature from 45° to 55°C, and (c) biaxially orienting the composite sheet to a deformation ratio which is from 5:1 to 7:1 in the machine direction and deformation ratio which is from than 7:1 to about 10:1, and wherein the (A) layers are caused to surround the (C) layer on its top, bottom and sides. A process according to claim 5 wherein at least two adhesive layers (B) are contiguous with the (C) and (A) layers to form the configuration ABCBA in which the (B) layers are surrounded by the (A) layers on their surfaces opposite to the (C) layer and on their sides. A process according to claim 5 or 6 wherein said (A) layers comprise polypropylene. A process according to any of claims 5 to 7 wherein orientation is to a deformation ratio from 8:1 to 10:1 in the transverse direction. A process according to any of claims 5 to 8 wherein the machine orientation is carried out at a temperature from 140° to 150°C and the transverse orientation is carried out at a temperature from 160° to 170°C. The use of a multi-layer coextruded film according to any of claims 1 to 4 in the packaging of foodstuffs.

Inventors: MAZUERA GONZALO EMILIO, WAGNER JOHN RALPH JR, MAZUERA, GONZALO EMILIO, WAGNER, JOHN RALPH, JR.
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1988
Main classification: B32B27
IPC codes: B29L9, B29K29, B32B27, B29C55, B29K23