MODIFIED ZEOLITE CATALYSTS AND USE THEREOF IN THE PREPARATION AND TRANSFORMATION OF HYDROCARBONS

Abstract: There is disclosed a method for the modification of a natural clinoptilolite by acid treatment using a mineral acid at a suitable temperature and for a suitable period of time, followed by calcination, to produce a modified clinoptilolite which may be used as a catalyst in a reaction for the preparation of or transformation of hydrocarbons, e.g. the cracking of hydrocarbon products. There is also disclosed a method of regenerating the deactivated modified catalyst after use by treatment in the presence of nitrous oxide.

Description: BACKGROUND OF THE INVENTION This invention relates to the modification of a natural zeolite known as clinoptilolite, to the use of the modified clinoptilolite in the preparation and transformation of hydrocarbons, and to the regeneration of the modified clinoptilolite after use. Synthetic zeolite catalysts such as Zeolite Y have been used for many years in processes for hydrocarbon cracking. Further, in 1973 it was discovered that methanol can be converted to gasoline over a synthetic zeolite catalyst known as ZSM 5. However, ZSM 5 is not the optimum catalyst for the chemical industry because it results in the formation largely of gasoline. The chemical industry would prefer a process, and thus a catalyst for the process, which results in the formation of ethene, propene and butene as these products are more flexible for further use. Further, ZSM 5 is expensive. Synthetic zeolite catalysts are also of interest for the conversion of natural gases to more useful products. For example, when the gas obtained from a natural gas field is essentially methane, the gas may be steam reformed to form carbon monoxide and hydrogen. Thereafter there are two possible synthesis routes. The carbon monoxide and hydrogen can be subjected to a Fischer Tropsch process which will produce a range of products or the gas can be converted to methanol and then to gasoline utilising a synthetic zeolite catalyst. In an article in Applied Catalysis, 16 (1985) 249-253 by Sakoh, Nitta and Aomura, it is disclosed that a natural (i.e. naturally occurring) clinoptilolite from Futatsui, Japan, after modification, can be used in the conversion of methanol to light olefins. The modification of the natural clinoptilolite was carried out following two different procedures. The first procedure involved treating the natural clinoptilolite with 1 M HCl at 80°C for 24 hours after which the sample was filtered off, washed with distilled water and dried in air. The second procedure involved impregnating the clinoptilolite with 0,05 M and 0,5 M H₂SO₄, whereafter the samples were filtered off, dried in air and then calcined at 400°C for 3 hours in air. Thereafter, the catalysts were placed in a fixed bed continuous flow reactor under atmospheric pressure, and methanol vapour was carried through the reactor using helium as a carrier gas. Methanol was converted to hydrocarbons and water at the reaction temperature of 250-400°C over all the modified clinoptilolite catalysts. The hydrocarbons produced contained essentially aliphatic hydrocarbons. Further, this article discloses the regeneration of these catalysts by recalcination in air. SUMMARY OF THE INVENTION According to a first aspect of the invention there is provided a method for the modification of a natural clinoptilolite to produce a modified clinoptilolite for use in a reaction for the preparation of or transformation of hydrocarbons, which method includes the step of treating the natural clinoptilolite with hydrochloric acid at a concentration of greater than 1 M, up to and including 2.5 M for a treatment time longer than 24 hours up to and including 72 hours, and at a treatment temperature of from 40 to 80°C, to produce the modified clinoptilolite. Preferably, the natural clinoptilolite is treated with hydrochloric acid at a concentration of 2 M. After the acid treatment step, the modified clinoptilolite is preferably calcined at a suitable calcining temperature of from 450°C to 550°C for a suitable calcining time of from 3 hours. The modified clinoptilolite may be produced starting from a natural clinoptilolite from Zululand, South Africa, or from any other suitable natural clinoptilolite such as that from Futatsui, Japan. According to another aspect of the invention, there is provided a modified clinoptilolite, modified according to the method set out above, for use in a process for the conversion of methanol and/or dimethyl ether to hydrocarbon reaction products. According to a further aspect of the invention there is provided a method for the regeneration of a deactivated modified clinoptilolite used in a process for the preparation of or transformation of hydrocarbons, which method includes the step of heating the deactivated modified clinoptilolite at a suitable regeneration temperature and for a suitable regeneration time in the presence of nitrous oxide (N₂O) or a mixture of nitrous oxide and a second oxidant such as oxygen or air. Preferably, the deactivated modified clinoptilolite is treated with the nitrous oxide or a mixture of nitrous oxide and a second oxidant at a regeneration temperature of from 450°C to 550°C, more preferably 500°C, for a period of 2 to 6 hours or more, preferably approximately 3 hours. According to a further aspect of the invention there is provided a modified clinoptilolite, modified according to the method set out above, or any other method, for use in a process for the cracking of hydrocarbon products. DESCRIPTION OF PREFERRED EMBODIMENTS The first aspect of the invention is a method for the modification of a natural clinoptilolite to provide a catalyst which is suitable for use in various reactions. The starting material is any suitable natural clinoptilolite, produced in South Africa or anywhere else in the world. The natural clinoptilolite before modification, is not particularly active. To activate the natural clinoptilolite, it is treated with hydrocloric acid having a molarity of greater than 1 M, up to and including 2,5 M, more preferably 2 M, at a treatment temperature of from 40°C to 80°C, and for a treatment time longer than 24 hours up to and including 72 hours. These conditions are more severe than the conditions disclosed in the article in Applied Catalysis, 16 (1985) 245-253 and thus result in a more effective modified clinoptilolite. Further, after the acid treatment step, the clinoptilolite is preferably calcined at a suitable calcining temperature, e.g. from 450°C to 550°C, more preferably 500°C, for a suitable calcining time, e.g. 3 or 4 hours. Examples of this method are given at the end of this specification. The modified clinoptilolite may be produced starting from a natural clinoptilolite mined in Zululand, South Africa, or from any other suitable natural clinoptilolite. It is known that natural clinoptilolites from different locations differ in their properties and thus the modified clinoptilolite produced from natural clinoptilolite from Zululand, South Africa, will have somewhat different properties from the modified clinoptilolite produced from natural clinoptilolite from Futatsui, Japan. The next aspect of the invention is the use of a modified clinoptilolite, produced by the method described above, in a process for the conversion of methanol or dimethyl ether or a mixture of methanol and dimethyl ether to hydrocarbon reaction products. This reaction is a well-known reaction and in the present case may be carried out utilising the usual reaction conditions. The reaction may be carried out in a fixed-bed or in a fluidised bed reactor at suitable temperatures and pressures. It has been found that the use of a modified clinoptilolite catalyst gives a hydrocarbon reaction product which is rich in ethene, propene and butene. Examples of this process are also given at the end of this specification. The next aspect of the invention is a method for the regeneration of a modified clinoptilolite catalyst which has become deactivated through use in a process for the preparation of or transformation of hydrocarbons. It is well-known that zeolite catalysts deactivate with time, as coke (highly carbonaceous material) deposits on the catalyst. It is believed that the production of methane in the conversion reaction is related to coke formation. Thus, reducing methane formation will increase the lifetime of a catalyst. The method for the regeneration of the catalyst comprises the step of treating the deactivated catalyst at a suitable regeneration temperature and for a suitable regeneration time with nitrous oxide or a mixture of nitrous oxide and a second oxidant such as oxygen or air. The regeneration may be carried out at a regeneration temperature of from 450°C to 550°C, more preferably approximately 500°C for a time period of approximately 3 hours or more. Surprisingly, it has been found that the regeneration of deactivated modified clinoptilolite proceeds far more effectively when nitrous oxide is used over the use of oxygen or air alone. Examples of this regeneration method are also given at the end of this specification. The next aspect of the invention is the use of modified clinoptilolite produced according to the method set out above, or any other method, e.g. the method disclosed in Applied Catalysis, 16 (1985) 249-253, as a cracking catalyst, i.e. in a process for the cracking of higher hydrocarbons to lower hydrocarbons. Cracking processes are well-known and the conditions of use of the modified clinoptilolite are substantially the same as the known conditions of use. It has been found that higher hydrocarbons such as hexene, heptene, octene and decene may be cracked over a modified clinoptilolite catalyst to produce selectively C₃-C₅ alkenes. This reaction may be carried out in a fixed catalyst bed or in a fluidised catalyst bed. Examples of this cracking process using a modified clinoptilolite catalyst, are also given at the end of this specification. In place of natural clinoptilolite, one may use another natural zeolite having a similar pore size. Natural clinoptilolite has a first pore size of 0,34 by 0,35 mm (3,4 by 3,5 Å) and a second pore size, which is the important pore size for the present invention, of 0,34 by 0,72 mm (3,4 by 7,2 Å). Other suitable natural zeolites include: EXAMPLE 1 ― Comparative Example A sample of the unmodified naturally occurring zeolite clinoptilolite from Zululand, South Africa, denoted NC, (4 g, particle size 0,5-1,0 mm) and having a surface area (determined by the BET method) of 20,9 m²/g, was utilised as a catalyst for the methanol conversion reaction in a fixed bed downflow glass microreactor. Methanol was reacted over the zeolite at a weight hourly space velocity (WHSV) of 0,097h⁻¹ at 400°C. Products were collected and analysed by standard gas chromatographic techniques. The results, given in Table 1, demonstrate that the unmodified zeolite is a poor catalyst for this reaction and only effects partial methanol conversion. EXAMPLE 2 ― Comparative Example This example demonstrates that calcination of the unmodified zeolite in the absence of acid extraction is not beneficial. A sample of the unmodified zeolite NC was calcined in air (3 h, 500°C) and denoted NC-1. The surface area (determined by the BET method) was 18,8 m²/g. NC-1 was then utilised as a catalyst for methanol conversion as discussed in Example 1 and the results are shown in Table 1. The calcination treatment was found to deactivate the zeolite and hence NC-1 was a poorer catalyst than the unmodified natural zeolite, NC. EXAMPLE 3 A sample of the unmodified natural clinoptilolite NC was suspended with stirring in a solution of 1 M ammonium sulphate at 25°C for 40 minutes. Following this treatment the sample was collected by filtration and washed with distilled water. This procedure was repeated a total of 4 times. Following the final treatment the sample was dried (120°C, 3 h) in air and then calcined (500°C, 3 h) to give a modified zeolite denoted NC-2. The surface area (determined by the BET method) was 65,2 m²/g. NC-2 was then utilised as a catalyst for methanol conversion as described in Example 1 and the results are shown in Table 1. The ammonium ion exchange and calcination procedures improves the catalytic activity and lifetime of the zeolite. EXAMPLE 4 A sample of unmodified natural clinoptilolite NC (100 g) was suspended with stirring in aqueous hydrochloric acid (1M, 1 ℓ) at 74°C for 8 h. The zeolite was recovered by filtration, washed with distilled water and this procedure was repeated a total of 3 times. After the final treatment the sample was dired (120°C, 3 h) in air and calcined (500°C, 3 h) to give a modified zeolite denoted NC-3. NC-3 was then utilised as a catalyst for methanol conversion as described in Example 1 and the results are shown in Table 1. Acid treatment of the natural clinoptilolite according to this procedure improves the activity and lifetime of the zeolite when compared with samples NC, NC-1 and NC-2. EXAMPLE 5 A sample of unmodified natural clinoptilolite NC (100 g) was suspended with stirring in aqueous hydrochloric acid (2 M, 1 ℓ) at 70°C for 13,3 h. The zeolite was recovered by filtration, washed with distilled water and this procedure was repeated a total of 3 times. After the final treatment the sample was dried (120°C, 3 h) in air and calcined (500°C, 3 h) to give a modified zeolite catalyst NC-4. NC-4 was then utilised as a catalyst for methanol conversion as described in Example 1 and the results are shown in Table 1. 2 M acid treatment according to these procedures gives a superior catalytic performance when compared to the performance of the 1 M acid treated material, NC-3, and additionally is also superior to the performance of samples NC, NC-1 and NC-2. Treated clinoptilolites all give very high yields of C₂-C₄ alkenes when tested as catalysts for methanol conversion. EXAMPLE 6 This example demonstrates the use of a modified clinoptilolite as a hydrocarbon cracking catalyst. Modified clinoptilolite was prepared as described in Example 3 (i.e. ammonium exchange and calcination), sample NC-2, and this zeolite was used as a catalyst for 1-hexene cracking at hexene WHSV 0,2 h⁻¹ and at 400°C; and also at WHSV 0,16 h⁻¹ and at 500°C. The results are shown in Table 2. The results demonstrate that the modified zeolite is very active for hydrocarbon cracking. Additionally, the natural clinoptilolite was modified as described in Example 5 (i.e. treatment with HCl and calcination), sample NC-4, and this zeolite was used as a catalyst for (a) hex-1-ene cracking at WHSV 0,13 h⁻¹ and at 500°C; (b) hept-1-ene at WHSV of 0,2 h⁻¹ at 400°C; (c) oct-1-ene at WHSV of 0,08 h⁻¹ at 400°C; and (d) dec-1-ene at WHSV of 0,06 h⁻¹ at 400°C. The results are shown in Tables 3, 4, 5 and 6. The results demonstrate that the modified clinoptilolite is very active for hex-1-ene, hept-1-ene, oct-1-ene and dec-1-ene cracking and the major products observed are C₃-C₅ alkenes. At 500°C 60% propene selectivity can be obtained. EXAMPLE 7 ― Catalyst Lifetime The modified zeolites when used as catalysts for methanol conversion or hydrocarbon cracking reactions became deactivated with the deposition of highly carbonaceous material known as coke. This build up of coke occurs at a rate of ca. 0,5 g C/100 g catalyst/h during methanol conversion at 400°C and WHSV 0,1 h⁻¹. The lifetime of the catalysts NC, NC-1, NC-2, NC-3 and NC-4 are shown in a plot of conversion against reaction time for methanol conversion and this is shown in Figure 1. It is apparent that acid treatment of the zeolite according to the method of the invention considerably improves the operating lifetime of the zeolite. EXAMPLE 8 This example demonstrates that the deactivated, i.e. coked, zeolite catalysts described in the previous examples can be successfully reactivated by removing the coke as CO₂ and H₂O on oxidation by reaction with N₂O as oxidant, and that surprisingly N₂O is a more effective oxidant than O₂. O₂ is well-known as an oxidant for zeolite catalyst reactivation in industrial processes. Deactivated samples of catalyst NC-3 (see Example 4) were prepared by reaction of NC-3 with methanol as described in Example 1. The deactivated NC-3 was reactivated either using an N₂O treatment (500°C, 3 h, N₂O GHSV-3600 h⁻¹) to give sample NC-3B or an O₂ treatment (500°C, 3 h, O₂ GHSV-3600 h⁻¹) to give sample NC-3A. The effectiveness of N₂O verscs O₂ reactivation is shown by the catalytic activity and lifetime of a catalyst when tested as catalysts for methanol conversion following reactivation, and the results are shown in Table 7 and Figure 2. The N₂O reactivated zeolite is more active than the O₂ reactivated material and furthermore the N₂O reactivated zeolite exhibited a much longer active lifetime. Further experiments showed that similar results can be obtained for regeneration of NC-4 as well.

Claims: 1. A method for the modification of a natural clinoptilolite to produce a modified clinoptilolite for use in a reaction for the preparation of or transformation of hydrocarbons, the method including the step of treating the natural clinoptilolite with hydrochloric acid at a concentration of greater than 1 M up to and including 2.5 M for a treatment time of longer than 24 hours up to and including 72 hours and at a treatment temperature of from 40°C to 80°C to produce the modified clinoptilolite. 2. A method according to claim 1, wherein the concentration of the hydrochloric acid is 2 M. 3. A method according to claims 1 or 2, wherein after the acid treatment step the modified clinoptilolite is calcined. 4. A method according to claim 3, where the calcining is carried out at a calcining temperature of from 450°C to 550°C for a calcining time of from 3 hours. 5. A method according to any preceding claim, wherein the natural clinoptilolite is from Zululand, South Africa. 6. The use of a modified clinoptilolite when produced by a method according to any one of claims 1 to 5, in a process for the conversion of methanol or dimethyl ether to hydrocarbon reaction products. 7. A method for the regeneration of a deactivated modified clinoptilolite used in a process for the preparation of or transformation of hydrocarbons, the modified clinoptilolite having been produced by a method as claimed in any one of claims 1 to 5, the regeneration method including the step of heating the deactivated modified clinoptilolite at a suitable regeneration temperature and for a suitable regeneration time in the presence of nitrous oxide or a mixture of nitrous oxide and a second oxidant. 8. A method according to claim 7, wherein the regeneration temperature is from 450°C to 550°C. 9. A method according to claim 8, wherein the regeneration temperature is 500°C. 10. A method according to any one of claims 7 to 9, wherein the regeneration time is 2 hours or more. 11. A method according to any one of claims 7 to 10, wherein the second oxidant is selected from oxygen and air. 12. The use of a modified clinoptilolite when produced by a method according to any one of claims 1 to 5 in a process for the cracking of hydrocarbon products. 13. The use of a modified clinoptilolite when regenerated by a method according to any one of claims 7 to 11 in a process for the conversion of methanol or dimethyl ether to hydrocarbon reaction products. 14. The use of a modified clinoptilolite when regenerated by a method as claimed in any one of claims 7 to 11, in a process for the cracking of hydrocarbon products.

Inventors: COPPERTHWAITE, RICHARD GEORGE 14 3RD AVENUE, HUTCHINGS, GRAHAM JOHN, THEMISTOCLEOUS, THEMISTOCLIS 3 GRADUATE LODGE
Applicants: PRATLEY INVESTMENTS (PROPRIETARY) LIMITED
Application year: 1988
Main classification: B01J29
IPC codes: C10G11, B01J29