RADIATION SENSITIVE ELEMENT CONTAINING A MACROHETEROCYCLE

Abstract: This invention is directed to a radiation sensitive silver halide emulsion comprising a macroheterocycle having an acid function and to an element containing such emulsion. The macroheterocycle comprises at least two atoms of sulfur or selenium, each of which atoms being separated from one another by a chain of at least two carbon atoms. Such compound acts as a solvent and as a growth modifying agent for silver halide grains. Also described is a process for modifying the growth of silver halide grains.

Description: This invention relates to a radiation sensitive silver halide element which contains a macroheterocycle, which comprises an acid function, and a process for the preparation of such an element. Published art shows that addition of thioether compounds to various stages of silver halide manufacture has the effect of imparting improvements to silver halide properties. For example, US Patents Nos 3062646 and 3271157 disclose macrocyclic thioether compounds which are described as being useful as sensitizers and as solvents for silver halide. These compounds may comprise from 1 to 4 sulfur atoms and from 0 to 4 oxygen atoms in the cyclic ring. However, as is shown below by comparative data, such compounds have a tendency to cause fog on storage of the emulsions prior to use and therefore are unsatisfactory for commercial utilization. Accordingly, the object of this invention is to provide a silver halide element containing compounds capable of modification of properties of said element during manufacture or processing without causing objectionable increase in fog formation during storage. Another object of this invention is to provide a process for the preparation of such a photographic silver halide element. The present invention provides a radiation sensitive silver halide element comprising a macroheterocycle having one of the structural formulae: in which formulae: A is ―(L) p -DR; L is a hydrocarbon chain, which is straight or branched, which can be interrupted or substituted by nitrogen, oxygen, sulfur or a carbonyl (C=O) containing group; D is an acid function; R is hydrogen, an inorganic cation, ammonium or substituted ammonium, or an organic cation; each B is independently hydrogen or is as defined for A; each X is independently a sulfur, selenium or oxygen atom; m is 1 or 2, and if m is 2, both groups are adjacent or non-adjacent; n is 3 to 6; o is 1 or 2; each p is independently 0, 1 or 2; and Z is the atoms necessary to complete an aromatic carbocyclic or an aromatic heterocyclic ring, with the proviso that there are at least 2 sulfur or selenium atoms in the macroheterocycle, which atoms are separated from one another by an alkylene chain having at least two carbon atoms. The hydrocarbon chain represented by L, when present, can comprise from 1 to 5 carbon atoms. These carbon atoms can be in a continuous chain or they can be interrupted. Examples of interrupted chains include ―CH₂-S-CH₂―, ―CH₂-O-CH₂, ―CH₂-N(R¹)-CH₂ or ―CH₂-CO-CH₂―, R₁ can be hydrogen or an alkyl group having from 1 to 5 carbon atoms. The DR group is referred to herein as an "acid function" and includes groups such as carboxylic (―COOH), sulfinic (―SO₂H), sulfonic (―SO₃H), hydroxamic (―CO-NHOH) and sulfonamides (―SO₂NH―), as well as inorganic and organic salts of these groups. A preferred acidic group is carboxylic, including carboxylate ions derived from salts thereof. At least one DR group must be present on the macrocycle described herein. Additional DR groups are possible. Without being bound by theorical considerations, it is the acid function, in combination with the ring structure of the compound, which has been found to impart a superior combination of silver halide grain ripening and fog reduction properties to the macroheterocycles described herein. Aromatic carbocyclic rings which can be completed by Z include those having from 6 to 10 ring carbon atoms, including, for example benzene and naphtalene. Aromatic heterocyclic rings completed by Z include those having from 5 to 10 ring atoms. In addition to carbon, the heteroatoms can include, nitrogen, oxygen and sulfur atoms. As noted in the formulae above, each sulfur, selenium or oxygen atom in the cyclic structure is separated from other sulfur, selenium or oxygen atoms by the carbon of an alkylene unit. Successive alkylene units, each including one of the atoms above-defined, are linked together forming a cyclic structure having from 12 to 30 ring atoms, preferably from 15 to 21 ring atoms. Included within the cyclic structure are from 4 to 8 atoms which are sulfur, selenium or oxygen, at least 2 of which are sulfur or selenium. Preferably, the ring comprises 5 to 7 atoms which are sulfur, selenium or oxygen. Particular compounds falling within the disclosure of this invention include the following: References which provide instructions for the preparation of macrocyclic compounds include "Synthetic Multidentate Macrocyclic Compounds", R. Izatt and J. Christensen, Academic Press, New York, 1978 and "The Chemistry of Ethers, Crown Ethers and Their Sulfur Analogues", ed. S. Patai, John Wiley & Sons, New York, 1980. Introduction of an acid function group on a macrocyclic ether molecule can be accomplished by a multistep synthesis. For example, Compound 1, as shown above, is prepared by following a multiple step synthetic route, the first five steps of which are disclosed by B. Czech et al in "Organic Preparation and Procedures, Inc., 15 (1-2), 29-34 (1983)". The preparation is as follows: Intermediate Compound G, shown above in Step 5 is used to prepare intermediate Compound H as follows: At 45°C, under a nitrogen atmosphere, 26.2 g (0.22 mol) of SOCl₂ is added slowly, over 15 minutes, to a stirred solution of 27 g (0.1 mol) of Compound G in 20 ml of dry pyridine. After the addition, the mixture is heated for 10 minutes at 60-65°C and then cooled. Excess SOCl₂ is destroyed by addition of 50 ml of water. Then the mixture is extracted by 3 × 100 ml of CH₂Cl₂. The combined organic layers are dried (MgSO₄) and solvents are eliminated under reduced pressure. Intermediate Compound H is obtained with a yield of 76%. Intermediate Compound H is utilized in the preparation of Compound I: 30.6 g of Intermediate Compound H are dissolved in 200 ml of acetic acid, 0.5 g of Pd/C 10% and 1 ml HC10₄ are added. The compound is reduced under hydrogen pressure (20 psi or 137.8 kPa) at 50°C during 10 hours with two more additions of 0.5 g of Pd/C. After filtration the acetic acid is eliminated under reduced pressure, the crude product is dissolved in 200 ml CH₂Cl₂ then washed twice with 100 ml H₂O. The organic layer is dried (MgSO₄) and the solvent is eliminated under reduced pressure to yield Intermediate Compound I (70% yield). Intermediate Compound I is converted to Compound J by the following procedure: 10.4 g (0.04 mol) of Compound I are stirred 1 hour at room temperature with 8.8 g (0.06 mol) of K₂CO₃ in 100 ml CH₃OH and 50 ml H₂O. Solvents are eliminated under reduced pressure and the crude product is diluted with 100 ml acidified water then extracted with 3 × 100 ml CH₂Cl₂. The combined organic layers are dried (MgSO₄) and solvents eliminated under reduced pressure. Compound J is obtained with a yield of 89%. Intermediate Compound J is oxidized to Compound K by the following procedure: 10.85 g (0.05 mol) of Compound J are added over a 10 minute period to HNO₃ (d = 1.42) at room temperature. During addition, the temperature rises and a violent reaction starts at about 45°C with emission of NO₂. After 1 hour at room temperature 50 ml of water are added to the reaction mixture which is then extracted with 3 × 100 ml CH₂Cl₂ and 2 × 100 ml diethylether. The combined organic layers are dried (MgSO₄) and solvents eliminated under reduced pressure. The residue is dissolved in 50 ml H₂O containing 7.6 g of K₂CO₃ then extracted twice with 100 ml of diethyl ether. The aqueous layer is acidified with HCl 6N, then extracted with 4 × 100 ml of diethylether and 2 × 100 ml CH₂Cl₂. The combined organic layers are dried (MgSO₄) and solvents eliminated. The crude acid Compound K is obtained with a yield of 80% and used as such in preparation of the ethyl ester. 5.7 g (0.0247 mol) of Intermediate Compound K is dissolved in 300 ml of a 1: 1 mixture of absolute ethanol and benzene. p-toluenesulfonic acid (0.5 g) is added and the mixture is refluxed for 6 hours with continuous circulation of the condensing vapors through a Soxhlet thimble containing anhydrous Na₂SO₄. The solvents are removed under reduced pressure and the residue is dissolved in 150 ml CH₂Cl₂ and washed with saturated NaHCO₃. The organic layer is dried (MgSO₄) and solvents eliminated under reduced pressure. The ethyl ester is obtained as Compound L. The overall yield based on synthesis of intermediate Compounds J and K was 65%. Intermediate Compound L is reacted with a dithiolether compound to produce the ester derivative of cyclic thioether of Compound I: At 80°C, under nitrogen atmosphere and with rapid stirring, a mixture of 3.9 g (0.015 mol) of Intermediate Compound L and 3.0 g (0.0165 mol) of HS-(CH₂)₂-O-(CH₂)₂-O-(CH₂)₂-SH, in 75 ml of dry dimethylformamide (DMF) is slowly added over 3.5 hours to 270 ml of dry DMF containing 4.89 g (0.015 mol) of Cs₂CO₃ and 0.3 mg of dicyclohexyl 18-CROWN-6. After cooling and filtration, the DMF is eliminated under reduced pressure. The residue is dissolved in 150 ml CH₂Cl₂ and washed twice with 100 ml H₂O. The organic layer is dried (MgSO₄) and the solvent eliminated. The ester of Compound 1 is isolated by chromatography on silica gel (Merck 60H: 70 parts, eluent CH₂Cl₂). Hydrolysis of the ester yielded Compound 1: 1.62 g (0,0044 mol) of the ester of Compound 1 is stirred at room temperature during 3 hours in 50 ml of NaOH 1N and 50 ml of CH₃OH. The resulting solution is extracted twice with 50 ml CH₂Cl₂. The aqueous layer is acidified, then extracted with 3 × 100 ml CH₂Cl₂. The combined organic layers are dried. Elimination of solvent yielded Compound 1. Compound 6 can be prepared according to the following synthetic route, from compound J of the previous synthesis. A mixture of 450 ml of DMF and 6.52 g (0.020 mol) of Cs₂CO₃ is heated to 80°C, then a solution containing 3.64 g (0.020 mol) of dithiol and 4.34 g (0.020 mol) of dichloro compound J in 50 ml of DMF is added over a 6 hour period. The heating is maintained at 90°C for 6 hours. The reaction mixture is filtered and DMF is removed. The residue is dissolved in 100 ml of CH₂Cl₂, filtrated and the solvent is eliminated. 7.8 g of crude product is obtained. The product is purified by chromatography on SiO₂ (Merck 60, 60-200 µm; eluent: CH₂Cl₂/Methanol 98: 2), and dried. 4.56 g of 2-hydroxymethyl-1,4,10,13-tetraoxa-7,16-dithiacyclooctadecane is obtained with a yield of 70%. In a 100 ml three-necked flask, is placed 5 g (15.3 mmol) of the compound obtained in the previous step, 1.89 g (16.8 mmol) of potassium t-butoxide, and 30 ml of t-butyl alcohol; the mixture is refluxed for 30 min. Ethyl chloroacetate is added at once. The mixture is refluxed overnight. Solvent is eliminated under reduced pressure. The resulting black oil is dissolved in 60 ml of CH₂Cl₂ then washed with 50 ml of H₂O and 5 ml of HCl (10 N). The product is washed again with 50 ml of H₂O and dried (MgSO₄); the solvent is eliminated. 5.89 of crude compound is obtained, then purified by chromatography on SiO₂(Merck 60 µm ― Eluent CH₂Cl₂/Ethanol 99.5: 0.5). A solution containing 3.33 g (7.9 mmol) of the ester obtained in the previous step and 18 ml of methanol is prepared in a 100 ml flask; A solution of 3.15 g (79 mmol) of NaOH in 18 ml of H₂O is added. The mixture is stirred at room temperature overnight. 12 ml of HCl (10 N) is added and the mixture is extracted with 3 × 50 ml of CH₂Cl₂. The organic phase is dried and the solvent eliminated. The crude product obtained is dissolved in 50 ml of NaOH (2N), then washed with 2 × 50 ml of CH₂Cl₂. The aqueous phase is acidified with 40 ml of HCl (10 N). The solution is extracted with 2 × 250 ml of CH₂Cl₂, then dried. The solvent is removed. 2.80 g (92%) of compound 6 is obtained. Compounds 20 and 21 can be prepared in the same way, by using appropriate dithiols. Compound 9 can be prepared according to the following synthetic route. The first five steps are disclosed in the publication of A Anantanarayan, P.J. Dutton, T.M. Fyles et M.J. Pitre, J. Org. Chem. 1986 Vol. 51 No 5 p. 752.5. Preparation of intermediate compound N,N,N′,N′-tetramethyl-1,4,10,13-tetraoxa-7,16-dithiocyclooctadecane-1,2-dicarboxamide. (Compound T) In a 2 l, three-necked, round-bottomed flask fitted with a reflux condenser, thermometer, dropping funnel and magnetic stirring is placed, under a nitrogen atmosphere, 6.3 g (19.3 mmol) of cesium carbonate. 900 ml of dry DMF is poured and the mixture is heated to 50°C. Then, a solution of 9.91 g (19.3 mmol) of tetramethyl-bis(iodoethoxy)-succinamide and 3.5 g (19.3 mmol) of 3,6-dioxa-1,8-dithiaoctane in 100 ml of DMF is slowly added in 6 hours. The mixture is stirred overnight at 50° C, filtered, and DMF is evaporated under reduced pressure. The crude product is purified by chromatography on silica and yielded 1.86 g (22%) of Compound T. Preparation of compound 9 In a 50 ml round-bottom flask equipped with a stirring rod and a reflux condenser is placed 1.66 g (3.79 mmol) of the diamide, 34.4 ml of H₂O and 3.44 ml of HCl lON (34.4 mmol). The mixture is heated at 80°C for 20 hours and cooled down to room temperature. The mixture is eluted through a column of 150 g of Dowex 50 × 2 - 200 resin in the acidic form in order to exchange (CH₃)NH + / 2 cations with H⁺ cations. The eluate is then concentrated to approximatively 50 ml on the rotative evaporator under high vacuum at 50°C. In order to remove chloride anions, a solution of 6.03 g (36.1 mmol) of AcOAg in 615 ml of hot water is added to the chlorhydric solution of the dicarboxylic thioether. Silver chloride is eliminated by centrifugation and filtration through an hydrophilic 0.2 µm-filter (Millipore: EG type) to remove last traces of solid. The solution is then concentrated to approximatively 50 ml and filtered again as above in order to remove precipitated silver chloride and acetate. The solution is then passed through a 100 g Dowex 50 × 2 - 200 resin in its acidic form to exchange Ag⁺ cations of the excess AcOAg and the complex with H⁺ cations. The eluate is concentated to 50 ml. This solution is free of chloride anions (no precipitate with silver nitrate solution) and free of silver cations (no precipitate with sodium chloride solution). The acetic solution resulting is then evaporated and yielded 0.70 g (48%) of compound 9. Compound 22 can be prepared in the same way, by using the appropriate dithiol. Compounds 23, 24 and 25, as well as their homologues comprising various cyclic thioethers type linkages can be prepared in quantitative yield from intermediate compounds which have an alcohol function. Such intermediate compounds are similar to Intermediate A′, described above in the preparation of Compound 6, and have the general formula designated "U": where V is ―OCH₂CH₂O―, ―S― or ―O―. The preparation comprises reacting "U" with an anhydride of the formula: in the presence of triethylamine. Compounds 23, 24 and 25 were prepared wherein V was in each instance ―OCH₂CH₂O― and wherein for Compound 23, W was ―CH₂-CH₂: for Compound 24, W was ―CH₂-O-CH₂―; and for Compound 25, W was A photographic element of this invention comprises a support, at least one photosensitive silver halide emulsion layer and a macroheterocycle as described above. Preferably, the cyclic compound is present in a silver halide emulsion layer. However, when the macroheterocycle is to be used as a silver halide solvent during the development or the further steps of the processing (e.g. during a silver diffusion process), the macroheterocycle may be present in another hydrophilic colloid layer, such as an intermediate layer, from which it can diffuse during processing into a silver halide emulsion layer. Incorporation of a macroheterocycle in a silver halide emulsion layer can be achieved at various steps in the preparation of the emulsion. The preparation of silver halide emulsions is well known and is described, for example, in Research Disclosure , Vol. 176, December 1978, Item 17643, paragraphs I and II. The emulsions can be chemically sensitized as described in paragraph III of the same publication. A macroheterocycle can be incorporated during a ripening step where it will serve to modify the growth of silver halide grains. It can be used by itself or in combination with other ripening agents or growth modifiers or spectral sensitizers, stabilizers, antifoggants and other useful emulsion additives. The macroheterocycle can also be incorporated in the chemical sensitization step, preferably simultaneously with other chemical sensitizing agents. Useful amounts of macroheterocycle will vary depending upon such factors as the type of emulsion, the particular macroheterocycle selected, and the specific effects that are sought. Generally, amounts range from 5 × 10⁻⁶ to 1 × 10⁻¹ mol/silver mol, with from 10⁻⁴ to 10⁻² mol/silver mol being preferred. Preferably, chemical sensitizing agents employed in combination with cyclic ethers are noble metals such as gold or gold in combination with sulfur or selenium compounds. In comparison to thioether compounds used as co-sensitizing agents according to the prior art, the macroheterocycles described herein do not cause undesirable fog increase or loss of spectral sensitivity. This is shown by examples below. Alternatively, the macroheterocycles described herein can be incorporated during the melting step for the silver halide emulsion immediately prior to coating. In this case, the amount of macroheterocycle is preferably from 1 × 10⁻⁴ to 10⁻² mol/silver mol. When a macroheterocycle as described herein is incorporated in a hydrophilic colloid layer adjacent to a silver halide emulsion layer, such as in an intermediate layer separating adjacent silver halide emulsion layers, the macroheterocycle is preferably coated at a coverage of from 1 × 10⁻⁷ to 1 × 10⁻⁵ mg/dm²: When the macroheterocycle is incorporated in a silver halide emulsion layer during the melting stage prior to coating it is believed that the macroheterocycle functions primarily as a silver halide solvent and a development modifying agent rather than as a co-sensitizing agent. In still another alternative, a macroheterocycle of this invention can be incorporated in a photographic element from a processing solution by incorporating the macroheterocycle in the processing solution in an amount of from 5 × 10⁻⁵ to 1 × 10⁻³ mol/liter. In this alternative, the macroheterocycle acts basically as a processing accelerator. However, enhancement of the desired properties of the photographic element results regardless of which manner of action is ascribed to the macroheterocycle. This invention also provides a process for the growth modification of silver halide grains during the ripening step. In this embodiment, an amount of macroheterocycle effective for modifying the growth of grains is added during the ripening step. A preferred concentration of macroheterocycle to achieve growth modification of silver halide is from 10⁻⁴ do 10⁻² mol thereof per mol of silver halide. The silver halide grains can be of any halide compositions (e.g., silver bromide, silver bromoiodide, silver chloride, or silver chlorobromoiodide), of any size (e.g., coarse or fine), and can be of any regular or irregular shape (e.g., spherical, regular cubic, regular octahedral, cubo-octahedral, or tabular octahedral) known to be useful in photography. Conventional vehicles can be used, such as those described in Research Disclosure (RD), Item 17643, cited above, paragraph IX. Silver halides can be spectrally sensitized as described in paragraph IV of the same RD reference. The improvements of this invention can be applied to black and white photography (including radiography), or, preferably, to color photography, to form silver images and/or dye images by selective dye destruction, formation or physical elimination, as described in paragraph VII of the RD publication noted. Preferred color photographic elements are those that form dye images by means of color developers or dye forming couplers. To use these elements, they can be exposed and processed in any known manner as described in paragraphs XVIII and XIX of the above-mentioned RD reference. The following examples are presented as further illustrations of the invention. Example 1 Four tabular grain silver bromoiodide emulsions were prepared according to a procedure similar to the one disclosed in Example 3 of French Patent 2,516,257. One of these emulsions is prepared without additive (Control 1), another with a thioether of U.S. Patent 3,062,646 (1,10-dithia-4,7,13,16-tetraoxacyclooctadecane, Control 2) the third with Compound 1 as identified above, and the fourth with Compound 4. Each macroheterocycle is added in an amount of 1.69 × 10⁻⁴ mol/mol Ag in the silver nitrate solution during grain growth. Average diameter and average thickness of grains, and width variation coefficient are determined on the resulting emulsions. The following table summarizes the results obtained. These results show that the macroheterocycles of this invention allow to modify the growth of silver halide grains and thus to obtain grains having aspect ratios different from those obtained with the prior art thioethers. Example 2 Experiments were carried out with 8 mmol AgBr dispersed at pH 3, pBr 3 in 0.02% ossein gelatin (isoelectric point 4.9) containing 28 mmol KNO₃ and 0.3 mmol of the macroheterocycle noted in the following table. These emulsions were stirred for 16.5 h at 25°C. Evaluation of subsequently obtained electronmicrographs yielded the following results. It is apparent that under the given conditions, Compound 1 is an effective ripening agent and increases AgBr particle dimensions more than does the non-acid function containing parent compound of the prior art. Example 3 The following test is based on a polydispersed, negative-type silver bromoiodide (6 mol % iodide) gelatin emulsion containing 0.15 mmol/mol silver of a disulfoalkyl oxacarbocyanine dye. After addition of the indicated compounds at 40°C, pH 5.8 and pBr 3, the emulsions were coated and conventionally processed in Kodak developer D19. Unprocessed coatings were used for the determination of absorptance, a, which is defined by a = 1 - (R + T), where the last terms refer, respectively, to reflectance and transmittance. To test for storage stability, unprocessed coatings were kept at 49°C, 50% relative humidity (RH) for 1 week. The following Table III summarizes the results obtained. Part 1 demonstrates that the intensity of the 555 nm peak, which is associated with the adsorbed cyanine dye, is much more decreased by thioether B than by Compound 4, an acid-substituted macroheterocycle useful in this invention. Similarly, it is apparent from Part 2 that spectral sensitization by the cyanine dye is barely influenced by an acid-function containing macroheterocycle as described herein. By contrast, the neutral prior art thioether (Compound A) is seen to inferfere with this spectral sensitization process and to induce a drastic speed loss. From part 3 it is apparent that while neither the macroheterocycle of the invention, nor thioether A of the prior art has initially any deleterious effect on the emulsion intrinsic sensitivity, the acid-substituted macroheterocycle of the invention, as described herein, is also without deleterious effect on the emulsion storage stability. This inertness is distinct from the behavior of the prior art thioether which destabilizes the emulsion during storage and enhances formation of fog. Example 4 This example illustrates the improved fog reduction on storage obtained by the acid-function cyclic ether compounds. Three samples of an octahedric AgBrI emulsion were prepared. Before the chemical sensitization step, the following compounds were added: Control 1 = none Comparison (a) 30 mg/mol Ag Invention = Compound 23 60 mg/mol Ag Comparison (a) 1,10-dithia-4-7,13,16-tetraoxacyclooctadene of US patent 3,062,646. The completed emulsions were tested in an Xray type of processing, then incubated at 50 C, 50% RH, for periods of 2 days, 7 days, 14 days and 24 days. Results are shown in Table IV. From the results of Table IV, it is apparent that the emulsion containing the Compound 23 gives no more fog than the emulsion without a thioether compound, and much less fog than the thioether compound of the prior art.

Claims: 1. A photographic element comprising a support and at least one silver halide emulsion layer characterized in that said element comprises a macroheterocycle having one of the structural formulae: in which formulae A is ―(L) p -DR; L is a hydrocarbon chain which can be interrupted or substituted by nitrogen, oxygen, sulfur or a carbonyl containing group; D is an acid function; R is hydrogen, an inorganic cation, ammonium or substituted ammonium, or an organic cation; each B is independently hydrogen or is as defined for A; each X is independently a sulfur, selenium or oxygen atom; m is 1 or 2, and if m is 2, both groups are adjacent or non-adjacent; n is 3 to 6; o is 1 or 2; each p is independently 0, 1 or 2, and Z is the atoms necessary to complete an aromatic carbocyclic or an aromatic heterocyclic ring, with the proviso that there are at least 2 sulfur or selenium atoms in the macroheterocycle, which atoms are separated from one another by an alkylene chain having at least two carbon atoms. 2. The photographic element of claim 1 wherein the acid function DR of the macroheterocycle is a carboxylic, hydroxamic, sulfinic or sulfonic group. 3. The photographic element of claim 1 or 2 wherein said macroheterocycle comprises from 12 to 24 atoms in the ring structure. 4. The photographic element of claim 3 wherein said macroheterocycle comprises from 15 to 21 atoms in the ring structure. 5. The photographic element according to any of claims 1 to 4 wherein said macroheterocycle comprises from 4 to 8 sulfur, selenium and oxygen atoms in the ring structure. 6. The photographic element according to any of claims 1 to 5 wherein group B of the macroheterocycle is hydrogen. 7. The photographic element according to any of claims 1 to 6 wherein group A of the macroheterocycle represents a carboxy group. 8. The photographic element of claim 7 wherein the macroheterocycle comprises carboxy groups on adjacent ring carbon atoms. 9. The photographic element according to any of claims 1 to 8, wherein in the macroheterocycle formula p is o. 10. The photographic element according to any of claims 1 to 9, wherein the macroheterocycle is present in at least one silver halide emulsion layer. 11. The photographic element of claim 10, wherein the silver halide emulsion layer comprises silver halide grains having an aspect ratio higher than 5: 1. 12. The photographic element of any of claims 10 to 11 wherein said macroheterocycle is present in an amount of from 5 × 10⁻⁶ to 1 × 10⁻¹ mol thereof per mol of silver halide. 13. The photographic element of claim 12 wherein said macroheterocycle is present in an amount of from 10⁻⁴ to 10⁻² mol thereof per mol of silver halide. 14. A process for the preparation of a photographic silver halide element according to any of claims 10 to 13, characterized in that the macroheterocycle is added to the element during the physical growth step of silver halide grains in an amount sufficient for modifying the growth of said grains.

Inventors: FRIOUR, GERARD, HERZ, ARTHUR, PARIS, CHRISTIAN, RIVECCIE, MARCEL, Friour, Gérard
Applicants: EASTMAN KODAK COMPANY, KODAK-PATHE
Application year: 1988
Main classification: G03C1
IPC codes: C07D329, G03C1, C07D327