PROCESS FOR MANUFACTURING A SUPERCONDUCTING WIRE OF COMPOUND OXIDE-TYPE CERAMIC

Abstract: The process includes steps comprising filling a metal pipe with material powder of ceramic consisting of compound oxide having superconductivity, performing plastic deformation of the metal pipe filled with the ceramic metal powder to reduce the cross section of the metal pipe, and then subjecting the deformed metal pipe to heat-treatment to sinter the ceramic material powder filled in the metal pipe. The ceramic material powder may contain compound oxide having Perovskite-type crystal structure exhibiting superconductivity. The metal pipe may selected from a group comprising metals of Ag, Au, Pt, Pd, Rh, Ir, Ru, Os, Cu, Al, Fe, Ni, Cr, Ti, Mo, W and Ta and alloys including these metals as the base. The heat-treatment may be carried out at a temperature ranging from 700 to 1,000 °C. The cross section of the metal pipe is reduced at a dimensional reduction ratio ranging from 16 % to 92 % by wire-drawing or forging by means of dies, roller dies, or extruder.

Description: Background of the Invention Field of the invention The present invention relates to a process for manufacturing an elongated article made of sintered ceramic material possessing superconductivity. Particularly, it relates to a process for manufacturing a superconducting wire made of sintered ceramic of compound oxide which is applicable for producing superconducting coils or the like. More particularly, the present invention relates to a process for manufacturing a superconducting wire made of sintered ceramic of compound oxide having a higher critical current density and a higher superconductivity critical transition temperature. Description of the related art Superconductivity is a phenomenon in which electrical resistance becomes zero and hence can be utilized to realize power cables and a variety of devices and apparatus which are requested to reduce consumption of electrical energy and several ideas for its applications which utilize the phenomenon of superconductivity have been proposed. In fact, superconductivity is applicable in a variety of industrial fields, for example in the field of electrical power supply such as fusion power, MHD power generation, power transmission, or electric power reservation; in the field of transportation such as magnetic levitation trains, magnetic propulsion of ships; in the medical field such as in a high-energy beam radiation unit; in the field of science such as NMR or high-energy physics; or in the field of sensors or detectors for sensing very weak magnetic fields, microwave or radiant radiation or the like as well as in the field of electronics such as Josephson Junction devices and high-speed computers with reduced energy consumption. However, their actual usage have been restricted because the phenomenon of superconductivity can be observed only at very low cryogenic temperatures. Among known superconducting materials, a group of materials having so-called A-15 structure show rather higher Tc (critical temperature of superconductivity) than others, but even the top record of Tc in the case of Nb₃Ge which showed the highest Tc could not exceed 23.2°K as most. This means that liquidized helium (boiling point of 4.2°K) is the only cryogen that can provide such a very low temperature of Tc. However, helium is not only a limited, costly resource but also requires a large-scale system for liquefaction. Therefore, it had been desired to find another superconducting materials having much higher Tc. But research has found no material which exceeded the above-mentioned Tc during the past ten years. It is known that certain ceramics materials of compound oxides exhibit the property of superconductivity. For example, U.S. patent No. 3,932,315 discloses Ba-Pb-Bi-type compound oxide which shows superconductivity. This type of superconductor, however, possess a rather low transition temperature of lower than 13°K and hence usage of liquidized helium (boiling point of 4.2°K) as the cryogen is indispensable to realize superconductivity. The possibility of the existence of a new type of superconducting materials having much higher Tc was revealed by Bednorz and Muller who discovered a new oxide type superconductor in 1986 [Z. Phys. B64 (1986) p.189]. However this document neither describes nor mentions the use of such an oxide material to produce a superconducting wire thereof. This new oxide type superconducting material is La, Ba₂CuO₄ or La, Sr₂CuO₄ which are so-called K₂NiF₄-type oxides having a crystal structure that is similar to perovskite-type superconducting oxides which were known in the past (for example, BaPb₁- x Bi x O₃ disclosed in U.S. Patent No. 3,932,315). The K₂NiF₄-type oxides show such higher Tc at round about 30°K which is very much higher than that of known superconducting materials. As the compound oxide type superconductors consisting of oxides of elements of IIa and IIIa groups in the Periodic Table, we can be mention those of, so to say, quasi-Perovskite structure which can be considered to have a crystal structure that is similar to Perovskite-type oxides and includes an orthorhombically distorted perovskite or a distorted oxygen-deficient perovskite such as Ba₂YCu₃O₇-δ in addition to the abovementioned K₂NiF₄-type oxide such as [La,Ba]₂CuO₄ or [La,Sr]₂CuO₄. Since these superconducting materials show very high Tc of 30 to 90°K, it becomes possible to use liquidized hydrogen (b.p. = 20.4°K) or liquidized neon (b.p. = 27.3°K) as a cryogen for realizing the superconductivity in practice. Particularly, hydrogen is an inexhaustable resource except for danger of explosion. However, the above mentioned new type superconducting materials which have just come to light have been studied and developed only in a form of sintered bodies as a bulk product produced from powders but for which no attempt has been made them into a wire form. The reason is that the new type superconductors are ceramic materials of compound oxide which do not possess high plasticity or processability when compared with well-known metal type superconducting materials such as Ni-Ti alloy, and therefore they can not, or can only with difficulty, be shaped or deformed into an elongated article such as a wire by a conventional technique such as wire-drawing technique in which superconducting metal is drawn directly, or embedded in copper, to a wire form. There is proposed in laid-open Japanese patent No. 61-131,307 and also in IEEE Transactions on Magnetics, vol. MAG-19, No. 3, May 3, 1983, p.402, a method for manufacturing a superconducting wire from a metal type superconducting material which is apt to be oxidized and very fragile such as PbMo 0.35 S₈, or PbMo₆S₈ respectively, comprising charging the material powder in a metal shell, extruding the metal shell filled with the material powder at higher than 1,000°C, and then drawing the extruded composite. This metal working technique, to be more specific, can not be applied directly to ceramic material consisting of compound oxide, because the compound oxide type superconducting materials can not exhibit the superconductivity if the specific or predetermined crystal structure is not realized. In other words, a superconducting wire having higher critical temperature and higher critical current density and which is useable in actual applications can not be obtained outside predetermined optimum conditions. In particular, if the shell is not selected from suitable materials, the resulting compound oxide will be reduced due to chemical reaction with the metal of the shell, resulting in poor or inferior superconductivity properties. In the field of ceramic molding, it has been the general practice for manufacturing an elongated article such as wires or rods to add an organic binder to the material powder of ceramic in order to facilitate shaping or molding of the powder material. Thus, a mixture of the powder material and the organic binder is shaped into a rod by means of an extruder or a press machine and then the shaped rod is passed directly, or via a trimming or cutting stage, to an intermediate sintering stage to remove the organic binder before it is fed to the final sintering stage. The combination of the abovementioned press-molding and trimming or cutting operations give rise to loss of much expensive ceramics material, so that not only economy of material is low but also a dimensional ratio of longitudinal direction to cross-sectional direction of the rod can not be increased. Therefore, this process can not be used in practice. The extrusion technique is much better than the press-molding technique as regards economy of material and productivity, but requires great quantities of organic binder added to the powder material. This organic binder is difficult to remove completely during the intermediate sintering stage and hence remain in the finally sintered article, resulting in a cause of defects of the product which will lower their strength and the resistance to flexion. Therefore, it is difficult to manufacture a fine rod of ceramics having higher dimensional ratios of longitudinal direction to cross sectional direction according to the extrusion technique. In order to realize a reliable and practical superconducting structure, it is indispensable that the structure possesses sufficient strength and tenacity to endure bending forces during usage and also has as fine a cross-sectional dimension as possible so that it can transmit electrical current at higher critical current density and at higher critical temperature. Therefore, an object of the present invention is to provide a process for manufacturing a superconducting wire of sintered ceramic having a sufficient length to be used in practical applications, namely having a higher dimensional ratio of longitudinal direction to cross sectional direction, without using organic binder which is causative of lowering the strength and tenacity of the product. Another object of the present invention is to provide a process for manufacturing a fine superconducting wire of compound oxide type sintered ceramic having higher resistance to breakage, even if the diameter of the wire is reduced greatly, in other words, under higher cross section dimensional reduction ratios. Still another object of the present invention is to provide a process for manufacturing a fine superconducting wire of compound oxide type sintered ceramic having higher critical current density and higher critical temperature. Summary of the Invention The present invention provides a process for manufacturing a superconducting elongated article including the following steps: filling a metal pipe with a ceramic material powder consisting of a compound oxide having superconductivity, carrying out plastic deformation of said metal pipe filled with said ceramic material powder to reduce the cross section of said metal pipe, subjecting the deformed metal pipe to heat-treatment to sinter said ceramic material powder filling said metal pipe, and then after this step of heat treatment, cooling said metal pipe containing the sintered ceramic material powder slowly at a rate of less than 50°C/min. The elongated articles which can be manufactured by the process according to the present invention include rod, wire, strand, tape, band, or any other articles whose dimensional ratio of the elongated direction to the cross sectional direction is more than 30, the cross section of the article not being limited to a circle but may have any configuration such as a rectangular shape. The material powder of ceramic consisting of compound oxide having superconductivity include any compound oxide which exhibits superconductivity after the heat-treatment according to the present invention. Generally speaking, the material ceramic powder which can be used in the process of the present invention may have the general formula: AaBbCc, in which "A" stands for at least one element selected from a group comprising IIa and IIIa of the Periodic Table, "B" stands for at least one element selected from a group comprising Ia, IIa and IIIa of the Periodic Table, "C" stands for at least one element selected from a group comprising oxygen, carbon, nitrogen, fluorine and sulfur, and "a", "b" and "c" stand for atom ratios of the elements "A", "B" and "C". They preferably satisfy the following equation: "a"x(an average valence of "A) + "b"x (an average valence of "B") = "c"x (an average valence of "C") As the element of group Ia in the Periodic Table, H, Li, Na, K, Rb, Cs and Fr can be mentioned. The elements of group IIa in the Periodic Table may be Be, Mg, Ca, Sr, Ba and Ra. The elements of group IIIa in the Periodic Table may be Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Ac, Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, Mo and Lr. The elements of group Ib in the Periodic Table may be Cu, Ag and Au. The elements of group IIb in the Periodic Table may be Zn, Cd and Hg. The elements of group IIIb in the Periodic Table may be B, Al, Ga, In and Tl. The ceramic powder material is preferably a powder mixture containing oxides of such metals that possess higher oxygen potential for producing the oxide than that of copper. Among superconducting ceramics, we can be mention those that contain at least two elements selected from groups Ia, IIa and IIIa of the Periodic Table as "A", at least copper as "B", and oxygen as C", for example, Y-Ba-Cu-O type ceramics, Y-Sr-Cu-O type ceramics, La-Sr-Cu-O type ceramics and La-Ba-Cu-O type ceramics. The ceramic material powder may be compound oxides having the crystal structure of K₂NiF₄-type oxides, such as [La,Ba]₂CuO₄ or [La,Sr]₂CuO₄. Additionally, the material ceramic powder may be compound oxides having Perovskite-type crystal structure exhibiting superconductivity having the general formula: (α 1-x, βx) γy Oz wherein α stands for an element selected from group IIa elements of the Periodic Table, β stands for an element selected from group IIIa elements of the Periodic Table, γ stands for an element selected from elements of group Ib, IIb, IIIb, IVa or VIIIa of the Periodic Table, x, y and z are numbers which satisfy following respective ranges: 0.1 ≦ x ≦ 0.9 0.4 ≦ y ≦ 4.0, and 1 ≦ z ≦ 5, in particular, a compound oxide in which α is Ba, β is Y and γ is Cu. It is also preferable to use a ceramic material powder which is prepared by steps comprising mixing powders of Bi₂O₃, SrCO₃, CaCO₃ and CuO, drying and then compacting the powder mixture, sintering the compacted mass, and then pulverizing the sintered mass. The material powders of ceramics are preferably previously granulated before they are filled into the metal pipe. The metal pipe may be selected from a group comprising metals of Ag, Au, Pt, Pd, Rh, Ir, Ru, Os, Cu, Al, Fe, Ni, Cr, Ti, Mo, W and Ta and alloys including these metals as their base. The heat-treatment may be carried out over a temperature range of from 700 to 1,000°C. The plastic deformation of the metal pipe filled with the ceramic metal powder may be performed in such manner that the cross section of the metal pipe is reduced at a dimensional reduction ratio ranging from 16% to 92%. The operation of the plastic deformation may be carried out by wire-drawing which is performed by means of dies, roller dies, or extruder. The plastic deformation may be performed by forging, for example by means of swaging unit or rolls. It is also preferable to cool the metal pipe containing the sintered ceramic material powder therein slowly at a rate of less than 50°C/min, after the heat-treatment is completed. Now, an apparatus which can be used to realize the abovementioned process according to the present invention will be described with reference to the attached drawings which are not limitative of the present invention. Brief description of the drawings Fig. 1A to 1J illustrate a series of steps for manufacturing a superconducting elongated article according to the present invention. Fig. 2A to 2C show variations of the superconducting elongated articles according to the present invention, wherein Fig. 2A is an illustrative perspective view of the article, Fig. 2B is a cross section thereof, and Fig. 2C shows an illustrative view of another embodiment of the article. Fig. 3A and 3B show cross sections of variations of Fig. 2. Fig. 4 shows another embodiment of the present invention, wherein, Fig 4A is a cross section and Fig. 4B is a plane view of the elongated article according to the present invention. Fig. 5 shows still another embodiment of the present invention, wherein, Fig. 5A is a cross section and Fig. 5B is a perspective view of the elongated article according to the present invention. Fig. 6 is an illustrative view of an apparatus for manufacturing continuously a composite having a tape-like configuration according to the present invention. Referring to Fig. 1, the Fig. 1A to Fig. 1J illustrate manufacturing steps for an elongated article according to the present invention. First, a metal pipe 1 having a predetermined cross sectional configuration (outer diameter of "L", and inner diameter of "1") is filled with a material ceramic powder 2, as is shown in Fig. 1B. Then, the resulting metal pipe filed with the material ceramic powder is passed to wire-drawing operation which can be performed by means of roller dies 3 as is shown in Fig. 1C, or a die or a series of dies 4 shown in Fig. 1D in cross section. The wire-drawing may be performed by means of a swaging unit 5 as is shown in Fig. E or an extruder-type wire drawing machine (Fig. 1F shows a cross section of an extruder head). In the case of an elongated article having a rectangular cross section, the metal pipe may be rolled by means of rolls 7 as is shown in Fig. 1H. An annealing step can be incorporated in the wire-drawing stage in order to facilitate operation of the wire-drawing. It is also preferable to seal one end or opposite ends of the metal pipe before entering into the wire-drawing operation as is shown in Fig. 1H to prevent the powder material from escaping out of the metal pipe. Fig. 1I illustrates a perspective view of the resulting wire-drawn product comprising an inner core obtained from the material powder 2 having a reduced diameter "1'", so that the final product which will be obtained after the subsequent sintering step hereinafter described has the same configuration as Fig. 1I. Fig. 1J illustrates a case in which the outer pipe is removed. Fig. 2 shows a variation of the elongated article obtained according to the present invention, in which perforations or through holes are made in the metal pipe 11. In an embodiment shown in the perspective view of Fig. 2A, fine holes 13 are cut through the metal pipe over the whole surface thereof by means of a CO₂ laser or the like. Fig. 2B is a cross-sectional view of the pipe shown in Fig. 2A. The holes 13 may be replaced by a slit 13a shown in Fig. 2C. The slit 13a may have a dimension of about 200 µm in width. It is known that the resulting superconducting wire deteriorates under an oxygen-containing atmosphere such as air, so that it is preferable to close up the holes 13 cut in the metal pipe 11. For this purpose, the holes 13 can be filled up with sealant 14 to isolate the sintered wire of superconductor 12 from the ambient atmosphere as is shown in Fig. 3A. This method, however, is difficult to practice or has poor productivity, so that, in practice, it is preferable to cover the whole of the outer surface of the perforated metal pipe with a suitable air-tight cylindrical liner, for example a heat shrinkable plastic tube which is chemically stable as is shown in Fig. 3B. The liner may be composed of a metal layer vacuum-deposited on the whole surface of the metal pipe and more preferably may be made of low-melting point glass coated on the metal pipe to produce complete sealing. Fig. 4A illustrates an elongated sintered superconductor having a rectangular cross section according to an embodiment of the present invention and Fig. 4B shows a plan view thereof. This superconductor can be manufactured by a process including the steps of molding the superconducting material into the shape of a rectangular body 21 and then covering the molded article 21 with a metal sheath 22. Fig. 5 illustrates another embodiment of the elongated article having the same circular cross section as that of Fig. 1I according to the present invention, but, in this case, a superconductor 21 is covered with a sheath 24 made in the form of a net. Fig. 5A is a cross-sectional view and Fig. 5B is a perspective view of the resulting superconductor. The abovementioned variation can be adopted to a variety of applications. The presence of the abovementioned porous outer sheath or shell provides the following advantages: At first, the surface of the sheath 22 and 24 is oxidized by the oxidative treatment to produce copper oxide, so that the contents of oxygen in the sintered superconductor is not influenced or fluctuated by the oxidation of the sheath 22 or 24. In particular, in the case of Fig. 2A and Fig. 4, through holes 13 are dispersed over the whole surface of the metal pipe 11 and 22, so that the sintered superconductor can communicate with an outer atmosphere. Higher contact surface between the superconductor and the surrounding atmosphere can be assured by the net-like sheath 24. Fig. 6 illustrates an apparatus for continuously producing an elongated article according to the present invention. In this case, the material ceramic powder is preferably blended with organic binder. The apparatus includes a continuous furnace being provided with two heating means at a binder-removing zone 112 and a sintering zone 113. An elongated shaped tape or wire 114 is supplied to an inlet of the binder-removing zone 112 from a coiler 115. The elongated article 114 unwound from the coiler 115 is fed continuously to the binder-removing zone 112 at which the elongated article 114 is heated at a temperature of 400 to 700°C to remove the binder out of the elongated article 114. After the binder-removing zone 112, the elongated article 114 is passed to a continuous lining station 116 which is positioned at the downstream of the binder-removing zone 112. The continuous lining station 116 is provided with a drum 118 for feeding a sheet 117 of metal or alloy to a guide 119 where the sheet 117 is wound around the elongated article 117. A seam of the wound sheet 117 is welded by means of a laser welder 120 so that the elongated article 114 is wrapped by the metal sheet 117. The resulting composite comprising the elongated article 114 and the covering sheet or outer sheath 117 is then passed to the sintering zone 113 where the composite is heated at a temperature of 850 to 950°C to sinter the elongated article. The longitudinal dimension or length of the sintering zone 113 and the velocity of advance of the composite can be adjusted in such manner that the sintering is performed completely. The product 121 thus obtained may be wound about a drum 122 for stock. In this embodiment, the product possesses enough flexibility and self-supporting properties, since the elongated article 114 contains the binder. The apparatus shown in Fig. 6 permits the sintering operation to be carried out continuously at higher productivity. According to a variation of the present invention, the composite comprising the elongated article and the outer sheet can be shaped or deformed into a desired configuration such as a oil or the like due to the higher flexibility end self-supporting properties, so that the sintering can be performed in the coiled configuration condition or in a condition where the coil is supported on any other conductive body. The existence of the sheath of metal or alloy also increases the bending strength. Description of the Preferred Embodiments In a preferable embodiment according to the present invention, as the material ceramic powder, following powders may be mentioned: (1) Ceramic powder containing compound oxides having the crystal structure of K₂NiF₄-type oxides having superconducting property, particularly powders of [La,Ba]₂CuO₄ or [La,Sr]₂CuO₄. (2) Compound oxides having Perovskite-type crystal structure exhibiting superconductivity having the general formula: (α 1-x, βx) γy Oz wherein α stands for an element selected from group IIa elements of the Periodic Table, β stands for an element selected from group IIIa elements of the Periodic Table, γ stands for an element selected from elements of group Ib, IIb, IIIb, IVa or VIIIa of the Periodic Table, x, y and z are numbers which satisfy the following respective ranges: 0.1 ≦ x ≦ 0.9 0.4 ≦ y ≦ 4.0, and 1 ≦ z ≦ 5, in particular, a Ba-Y-Cu-O-type compound oxide in which α is Ba, β is Y and γ is Cu. It is possible to use another type ceramic material powders for example a compound oxide composed of at least two elements selected from a group comprising groups IIa and IIIa of the Periodic Table, one element selected from a group comprising group Va of the Periodic Table, Cu and oxygen, such as a Sr-Ca-Bi-Cu-O type compound oxide which is prepared for example by the steps comprising mixing powders of Bi₂O₃, SrCO₃, CaCO₃ and CuO, drying and then compacting the powder mixture, sintering the compacted mass, and then pulverizing the sintered mass. The material powders used in the present invention are not limited to those abovementioned. The material powders of ceramics are preferably previously granulated before they are filled into the metal pipe. When the material powder can not compacted into the metal pipe at a higher packaging density, it is desirable to granulate the material powder previously to facilitate charging operation into the metal pipe and to obtain a higher packing density. According to a preferred embodiment, the material powder is granulated into particles having an average particle size of less than 0.1 mm and then is heat-treated before being charged into the metal pipe. This heat-treatment corresponds to the final sintering used in the conventional procedure. In this case, if necessary, the material powder may be further heat-treated again after the powder is compacted in the metal pipe. If the heat-treatment of the powder material result in coagulation of powders to produce large particles having an average particle size of more than 0.1 mm, the heat-treated powder may be pulverized before it is compacted in the metal pipe. In this case, conventional final heat-treatment is carried out in the powder condition having an average particle size of less than 0.1 mm. Therefore, the resulting heat-treated powder as a whole possesses the crystal structure which exhibits superconductivity and hence there remains no portion where superconductivity is not exhibited. Furthermore, a higher packing factor or density is obtained in the metal pipe and also a higher elongation ratio of the wire is assured. In conclusion, the resulting wire obtained according to this embodiment is changed to an elongated superconducting wire having higher critical current density. In operation, a wire of compound oxide having the crystal structure of K₂NiF₄-type oxides such as a powder of [La,Ba]₂CuO₄ or [La,Sr]₂CuO₄ can be obtained by sintering a material powder mixture of oxides, carbonates, nitrate, sulfates or the like of the constituent elements of the compound oxide, for example, a powder mixture of La₂O₃, BaO₂, SrO₂ and CuO. The metal pipe may be made of a metal selected from a group comprising Ag, Au, Pt, Pd, Rh, Ir, Ru, Os, Cu, Al, Fe, Ni, Cr, Ti, Mo, W and Ta and of an alloy including these metals as the base. In particular, it is preferable to select among Ag, Au, platinum metals comprising Pb, Pd, Rh, Ir, Ru and Os and alloys containing them as the base metal. The metals of Ag, Au and platinum metals are almost inert towards the superconducting ceramic materials under heated conditions, and hence the heat-treatment operation can be carried out at a sufficiently high temperature so as to accelerate the sintering or solid-solid reaction among superconducting ceramic particles in the metal pipe to obtain a uniform elongated article. When the metal pipe made of copper is used in place of the platinum metals, there is a possibility of reaction between the superconducting material and the copper of the metal pipe, with the results that the composition in the resulting wire will deviate or fluctuate. Moreover, since the copper pipe is apt to be oxidized, it is difficult to perform the heat-treatment at a high temperature. These problems may be avoidable by using a pipe of platinum metals which is chemically inactive to the ceramics filling the pipe and hence the resulting wire possesses a composition which is uniformly distributed along the longitudinal direction. Therefore, the superconducting wire whose outer metal pipe is made of platinum metal exhibits almost the same critical temperature as a bulk or mass which is produced by sintering this same material ceramic powder and shows a much higher critical current density in comparison with a wire whose outer metal pipe is made of copper. According to the present invention, it is also possible to arrange another metal such as copper, copper alloy or stainless steel around the outer metal pipe. Such additional metal layer will increase the flexibility of the resulting wire which is obtained by plastic deformation. The plastic deformation step of the metal pipe filled with the ceramic metal powder is preferably carried out under such conditions that the cross section of the metal pipe is reduced at a dimensional reduction ratio ranging from 16% to 92%, more particularly from 20% to 90%. If the reduction ratio exceeds 92%, the material powder filling the pipe will not follow or accompany the movement of the inner surface of the metal pipe, resulting in breakage of the sintered ceramic wire inside the metal pipe at several points. On the other hand, if the reduction ratio is lower than 16%, satisfactory packing density in the metal pipe can not be expected, so that complete sintering can not be performed. The plastic deformation is preferably performed by the technique of wire-drawing, particularly, by means of a die or a series of dies, a roller die or a series of roller dies, or an extruder or a series of extruders. The plastic deformation may be carried out by forging which is preferably achieved by swaging or rolling. It is also possible to combine more than two operations of the abovementioned plastic deformations of extrusion, rolling, swaging and other wire drawing. It is also possible to shape the deformed wire into a desired configuration such as a shape of a coil which is applicable to a superconducting magnet or the like before the coil is heat-treated. The heat-treatment of the metal pipe filled with the material ceramic powder which is performed after the plastic deformation is preferably carried out at a temperature ranging from 700 to 1,000°C which is selected as a function of the constituent elements of the ceramics. Thus, the superconducting powder filled in the metal pipe are kept in a condition where they are contacted with each other but are not fused to form a continuous body even after the plastic deformation. The heat-treatment promotes sintering or reaction among the powders to produce a uniform product. Generally speaking, the temperature at which the sintering of powders of compound oxide is performed is below a melting point of the sintered body which is the upper limit and is preferably above a temperature which is 100°C lower than the melting point. If the sintering temperature is lower than the temperature which is 100°C lower than the melting point, complete sintering reaction can not be achieved and hence the resulting product will not have practical strength. On the other hand, if the sintering temperature exceeds the upper limit of the melting point, a liquid phase will be produced so that the sintered body melts or decomposes resulting in lowering the Tc. According to one embodiment, after the metal pipe filled with the material powder is deformed or wire-drawn to target configuration, the metal pipe is subjected to the sintering operation at a temperature where the compound oxide superconductor is not produced but which is greater than or equal to half, the reaction temperature expressed as absolute temperature, to such an extent that boundaries of the material powders diffuse each other. After the wire-drawing step, it is also preferable to perform an intermediate annealing which is followed by further wire-drawing. If necessary, a combination of the wire-drawing and the intermediate annealing can be repeated the desired number of times. After this, the sintered composite is subjected to the final treatment including a slow cooling at a rate of less than 50°C/min and a rapid cooling at a rate of more than 50°C to obtain the final superconductor product. The reasons why the abovementioned procedure is preferable results from the fact that the superconducting ceramic of Y-Ba-Cu-O type compound oxide does not exhibit the property of superconductivity if it is not sintered at a temperature of more than about 900°C and hence one constituent element of Cu in the ceramic is reduced by reaction with the metal which constitute the outer pipe, which result in deterioration of the superconductivity. To solve this problem, it is preferable to use, as the material powder, such a powder which is prepared by pulverizing a sintered ceramic mass which itself has superconductivity and to perform the sintering operation at a temperature where no reductive reaction occur after the wire-drawing operation. It is also preferable that, after the sintering or heat-treatment is completed, the metal pipe containing sintered ceramic body therein is cooled slowly at a rate of less than 50°C/min. When the process according to the present invention is applied to a sintered ceramic wire of Y-Ba-Cu-O type compound oxide or the like, improvement in the property of superconductivity can be achieved by heat-treatment including a slow cooling of the sintered body at a rate of less than 50°C/min. The outer metal pipe or sheath can be removed after sintering is completed, but if necessary, the outer metal pipe may remain as it is on the outer surface of the sintered ceramic body in order to improve safety for the magnetic field and to assure a heat-transmitting path as a precaution against the case where superconductivity breaks off accidentally. On the other hand, when inherent properties of a sintered ceramic body, such as resistance to chemicals and resistance to abrasion are required, it is preferable to remove the metal pipe off the sintered body (Fig. 1J). The outer metal can be removed from the sintered body mechanically for example using grinding, or chemically for example using etching liquid such as nitric acid. In a variation of the process according to the present invention, almost all the metal of the metal pipe may be removed during the sintering step, namely both sintering and removal of the metal are carried out simultaneously, while leaving a very thin skin layer on the surface of the sintered body. The thickness of the thin skin layer left on the surface of the sintered body is less than 500 µm, preferably less than 200 µm, so that the thin skin layer left on the surface is held on the surface even if the metal fuses during the sintering operation owing to its surface tension without dropping of the fused metal. It is also possible to carry out both plastic deformation for reducing the cross sectional dimension of the metal pipe and heat-treatment simultaneously, in order to complete two operations consisting of sintering of the material powder and deformation of the metal pipe by means of hot-working. In this case, the reduction ratio in the cross sectional direction of the metal pipe is preferably from 40% to 95%. The hot-working means working, treatment, or metal processing which is carried out at a temperature which is higher than the recrystallization temperature of a metal of the metal pipe. Thus, the metal pipe exhibits higher malleability above the recrystallization temperature because the metal loses considerably its resistance to deformation. Furthermore, the effects of work hardening will not disappear even if recrystallization of the metal takes place after it is quenched. Of course, this hot-working is performed below the melting point of metal, but preferably, it is performed at a temperature which is 10°C lower than the melting point. It is preferable that the plastic deformation is performed by metal working or processing which is such that compressive stress is imparted to an article to be worked, examples being wire-drawing and forging operations, so as to cause the material powder filled in the metal pipe to be compacted. It is also possible to adopt a sequence of steps comprising, after the plastic deformation operation such as wire-drawing for reducing the cross sectional dimension of the metal pipe complete, subjecting the deformed pipe to an intermediate annealing at a temperature where the metal pipe is annealed, further carrying out plastic deformation such as wire-drawing of the annealed pipe, and then subjecting the resulting pipe to the final heat-treatment to sinter the material ceramic powder filled in the metal pipe. In this case, the metal pipe may be removed after the intermediate annealing and the first annealing but before the final sintering of the material ceramic powder in order to prevent undesirable reaction between the ceramic powder and the metal of the metal pipe at a high sintering temperature. It is also possible to repeat another intermediate annealing after the first wire-drawing following the first intermediate annealing, so that, after then, the metal pipe is removed after the repeated second intermediate annealing before the final sintering. According to this sequence of operations comprising the first annealing, wire-drawing and the second annealing, the second annealing advantageously provides enough strength which can resist against external force exerted on the annealed article and/or imparts a desired configuration to the annealed body, before it is passed to, and during it is maintained in, the final sintering furnace in which the annealed article is sintered with no outer metal pipe. The combination of the wire-drawing and the intermediate annealing can be repeated a desired number of times to increase the dimensional reduction ratio in the cross sectional direction with no wire breakage, and hence the resulting wire shows a fine diameter and higher strength. The intermediate annealing may be performed in one of two temperature ranges of (1) the first temperature range where the metal pipe is annealed but ceramic powder is not sintered and (2) the second temperature range where the metal pipe is annealed and the ceramic powder is also sintered. If the intermediate annealing following the wire-drawing is performed in the first temperature range (1) where the metal pipe is annealed but ceramic powder is not sintered, a higher dimensional reduction ratio can be achieved to obtain a fine ceramic wire having satisfactory deflection strength with no breakage. In this case, the intermediate annealing can be performed at a suitable temperature which is selected as a function of the kind of metal of the metal pipe and components and composition of the ceramic powder. In the case of a combination of a metal pipe having a relatively higher annealing temperature and a material ceramic powder having a relatively lower sintering temperature, it is preferable to adopt the second temperature range (2) where the metal pipe is annealed and the ceramic powder is also sintered. It is also possible to add a cold working step before and/or after the hot working step. Furthermore, it is also possible to repeat the series of steps including the abovementioned hot working and sintering steps several times. According to a special variation of the process of the present invention, through holes which pass through a wall of the metal pipe are made after plastic deformation is completed, so that the material ceramic powder filled in the perforated metal pipe is sintered in an open condition. In this variation, after the wire drawing, the wall of the metal pipe of the wire is perforated by means of laser, electron beam or a microdrill or the like, so as to permit passage of gas, particularly oxygen-containing gas through the perforations or holes. If the metal pipe is not perforated, the material ceramic powder is sintered under a closed or sealed condition in the outer metal pipe in the sintering stage, so that oxygen deficiency in the compound oxide is too great to obtain a product having superior superconductivity. Therefore, it is preferable to make through holes in the wall and to carry out the sintering of the metal pipe in an atmosphere containing oxygen gas to supply a proper amount of oxygen to the compound oxide in the metal pipe. It is the general property of superconducting compound oxides that the superconductivity is influenced by the oxygen deficiency in the crystal structure. In other words, the oxygen deficiency as well as the crystal structure of the resulting sintered wire are keys to the superconductivity. Therefore, it is important to adjust the atom ratios of elements so as to satisfy the abovementioned ranges of elements defined in connection with the general formula: (α 1-x, βx) γy Oz as well as to fulfill the abovementioned procedure according to the present invention in order to adjust the oxygen contents defined by the general formula. Otherwise, the value of Tc can not be improved owing to a different crystal structure and improper oxygen deficiency. According to the abovementioned special variant, satisfactory oxygen can be supplied through the through holes or a slit made in the outer metal layer, so that the resulting sintered body of compound oxide possess a crystal structure of a so to say quasi-perovskite type crystal structure such as an orthorhombic structure or the like for which there is a higher possibility of producing Cooper pairs. The through holes or slit are preferably closed by filling them with sealing material or by covering the whole outer surface of the metal pipe with another metal sheath or covering in order to protect the compound oxide from deterioration due to attack by surrounding humid gas. It is also preferable to increase the partial pressure of oxygen gas during the sintering stage in order to promote penetration of oxygen gas through the holes or slits. Now, the process according to the present invention will be described with reference to illustrative Examples, but the scope of the present invention should not be limited thereto. Example 1 As a material powder to be sintered, a powder mixture of 85% by weight of La₂O₃, 4% by weight of BaCO₃ and 11% by weight of CuO was used. The powder mixture was compacted and then sintered at the conditions of 900°C, for 24 hours. The resulting sintered body itself exhibited superconductivity. The sintered body was then pulverized into powder and was compacted in a copper pipe having an inner diameter of 5 mm and a wall thickness of 0.3 mm. The metal pipe filled with the sintered powder was then heat-treated at 850°C for 10 hours to sinter the powder. After sintering was completed, the copper pipe thus treated was caulked without cooling it. The resulting superconducting wire showed a Tc of 30°K and was able to bend up to a curvature of 300 mm. Example 2 As a material powder to be sintered, a powder mixture of 85% by weight of La₂O₃, 2% by weight of SrO and 13% by weight of CuO was compacted in a copper pipe having an inner diameter of 10 mm and a wall thickness of 1 mm. The metal pipe filled with the powder mixture was heat-treated at 850°C for 24 hours. And then, before the pipe lost heat, the copper pipe thus treated was wire-drawn to such an extent that the diameter of the copper pipe was reduced to 2 mm under a hot condition. The resulting superconducting wire showed a Tc of 35°K and was able to bend up to a curvature of 100 mm. Example 3 85.5% by weight of commercially available La₂O₃ powder, 3.1% by weight of commercially available SrCO₃ and 11.4% by weight of commercially available CuO were mixed in an attrition mill in the wet state and then dried. The dried powder was compacted in a press under a pressure of 100 kg/cm² and then sintered at 900°C in air for 20 hours. The sintered body was pulverized and passed through a sieve to obtain powder of under 100 mesh. After granulation treatment, the powder material was compacted in a copper pipe having an outer diameter of 5 mm, an inner diameter of 4 mm and a length of 1 m and opposite ends of the pipe were sealed. The pipe filled with the material powder was subjected to wire-drawing to reduce its outer diameter down to 1.8 mm and then sintered at 1,050°C, for 2 hours in vacuum. The resulting sintered ceramic wire was covered with a copper sheath having a wall thickness of 0.2 mm and had a length of 7.7 m. The measured value of the critical temperature (Tc) where this sintered ceramic wire exhibited superconductivity was 35.5°K. The ceramic wire showed a deflective strength of 24.7 kg/cm² and a rupture toughness (K IC ) of 2.2 MN/m3/m². Example 4 The same material powder as in Example 3 was compacted in five pipes of iron having an outer diameter of 6 mm, an inner diameter of 5 mm and a length of 50 cm and opposite ends of each pipe were sealed. The pipes filled with the material powder were subjected to wire-drawing so as to reduce their outer diameter at dimensional reduction ratios of 95%, 88%, 56%, 37% and 14% respectively and then were heat-treated at 1,100°C for 2 hours in vacuum to sinter the material powder. After then, the outer iron pipe of sheath was removed by washing it with acid. The result showed that a sintered ceramic wire which was wire-drawn at a dimensional reduction ratio of 95% broke into nine pieces and a sintered ceramic wire which was wire-drawn at a dimensional reduction ratio of 14% was not sintered completely and hence could not keep its shape, while the other three sintered ceramic wires were sintered completely with no breakage. Example 5 The same material powder as Example 3 was compacted in five pipes of nickel having an outer diameter of 6 mm, an inner diameter of 5 mm and a length of 1 m and opposite ends of each pipe were sealed. The pipes filled with the material powder were subjected to wire-drawing to reduce the outer diameter down to 2.0 mm and were then heat-treated at 1,150°C for 2 hours to sinter the material powder. After then, the outer nickel pipe or sheath was removed mechanically by a cutting operation to obtain a sintered ceramic wire having a diameter of 1.6 mm and a length of 9 m. The measured value of the critical temperature (Tc) where this sintered ceramic wire exhibited superconductivity was 37.0°K. The ceramic wire showed a deflective strength of 24.4 kg/cm² and a rupture toughness (K IC ) of 2.1 MN/m3/m². Example 6 The same material powder as Example 3 was compacted in five pipes of silver having an outer diameter of 6 mm, an inner diameter of 5 mm and a length of 1 m and opposite ends of each pipe were sealed. The pipes filled with the material powder were subjected to wire-drawing to reduce the outer diameter down to 2.0 mm and then was heat-treated at 950°C for 2 hours to sinter the material powder. After then, the outer silver pipe or sheath was removed mechanically by a cutting operation to obtain a sintered ceramic wire having a diameter of 1.5 mm and a length of 6.3 m. The measured value of the critical temperature (Tc) where this sintered ceramic wire exhibited superconductivity was 37.0°K. Example 7 85.5% by weight of commercially available La₂O₃ powder, 3.1% by weight of commercially available SrCO₃ and 11.4% by weight of commercially available CuO were mixed in an attrition mill in the wet state and then dried. The dried powder was compacted in a press under a pressure of 100 kg/cm² and then sintered at 900°C in air for 20 hours. The sintered body was pulverized and passed through a sieve to obtain powder of under 100 mesh. After granulation treatment, the powder material was compacted in an iron pipe having an outer diameter of 5 mm, an inner diameter of 4 mm and a length of 1 m and opposite ends of the pipe were sealed. The pipe filled with the material powder was subjected to wire-drawing to reduce its outer diameter down to 1.8 mm and then sintered at 1,050°C, for 2 hours in vacuum. The resulting sintered ceramic wire was covered with an iron sheath having a wall thickness of 0.2 mm and had a length of 7.7 m. The measured value of the critical temperature (Tc) where this sintered ceramic wire exhibited superconductivity was 35.1°K. The ceramic wire showed a deflective strength of 25.1 kg/cm² and a rupture toughness (K IC ) of 2.1 MN/m3/m². Example 8 The same material powder as Example 7 was compacted in seven pipes of iron having an outer diameter of 6 mm, an inner diameter of 5 mm and a length of 50 cm and opposite ends of each pipe were sealed. The pipes filled with the material powder were subjected to wire-drawing so as to reduce their outer diameter at dimensional reduction ratios of 95%, 90%, 83%, 56%, 37%, 20% and 14% respectively and then were heat-treated at 1,100°C for 2 hours in vacuum to sinter the material powder. After then, the outer iron pipe or sheath was removed by washing it with acid. The result showed that a sintered ceramic wire which was wire-drawn at a dimensional reduction ratio of 95% broke into ten pieces while a sintered ceramic wire which was wire-drawn at a dimensional reduction ratio of 14% was not sintered completely and hence could not keep its shape, while the other three sintered ceramic wires were sintered completely with no breakage. Example 9 The same material powder as Example 7 was compacted in five pipes of nickel having an outer diameter of 6 mm, an inner diameter of 5 mm and a length of 1 m and opposite ends of each pipe were sealed. The pipes filled with the material powder were subjected to wire-drawing to reduce the outer diameter down to 2.0 mm and were then heat-treated at 1,150°C for 2 hours to sinter the material powder. After then, the outer nickel pipe or sheath was removed mechanically by a cutting operation to obtain a sintered ceramic wire having a diameter of 1.6 mm and a length of 9 m. The measured value of the critical temperature (Tc) where this sintered ceramic wire exhibited superconductivity was 35.8°K. The ceramic wire showed a deflective strength of 24.9 kg/cm² and a rupture toughness (K IC ) of 2.2 MN/m3/m². Example 10 Superconducting ceramic powder (average particle size of 3 µm) having a composition of Y 0.8 Sr 0.2 CuO₃ was compacted in a pipe of platinum. Then, the resulting platinum pipe was inserted into an outer pipe of oxygen-free copper. The composite pipe comprising the platinum pipe filled with the ceramic powder and covered by the outer oxygen-free copper pipe was subjected to metal working comprising extrusion and wire-drawing to reduce its outer diameter to 0.8 mm. The composite pipe showed an area ratio of Cu:Pt:ceramic = 10:1:2 in its cross section. The composite pipe was heat-treated at 900°C for 12 hours in air to sinter the material powder inside the metal pipes. The resulting superconducting wire showed Tc of 100°K which was almost the same level of superconductivity as a tablet which was produced by the steps of press-molding and then sintering the same powder as the abovementioned Example 10 and which showed a Tc of 105°K. For comparison, the abovementioned composite pipe which was not subjected to the heat-treatment did not show any superconductivity even n liquid helium (4.2°K). Example 11 A powder mixture of 20.8% by weight of Y₂O₃, 54.7% by weight of Ba₂CO₃ and 24.5% by weight of CuO was compacted in a silver pipe having an outer diameter of 6 mm, an inner diameter of 5 mm and a length of 1 m. After the opposite end of the pipe were sealed, the pipe was subjected to wire-drawing to reduce its outer diameter to 2.0 mm and after then was heated at 950°C for 2 hours to sinter the powder mixture. After then, the outer silver pipe or sheath was removed mechanically by cutting work to obtain a sintered ceramic wire having a diameter of 1.5 mm and a length of 6.3 m. The measured value of the critical temperature (Tc) where this sintered ceramic wire exhibited superconductivity was 87.0°K. Example 12 A ceramic powder which has been preliminary sintered was finally sintered at a 920°C for 20 hours to produce a powder having an average particle size of 0.1 µm and having a composition of YBa₂Cu₃O₇. The resulting sintered body was pulverized again to produce a material powder of 0.1 mm which was then filled in a stainless steel pipe having an inner diameter of 5 mm and an outer diameter of 9 mm. The pipes filled with the material powder were subjected to wire-drawing to reduce the outer diameter to 2 mm. The critical temperature (Tc) of this sintered ceramic wire was 97°K and the critical current density was 103 A/cm². For comparison, the same ceramic powder which has been preliminary sintered as Example 12 was molded into a tablet and the tablet was heat-treated at the same condition as Example 12. After the tablet was pulverized, the resulting powder was compacted in a stainless steel pipe and then subjected to wire-drawing under the same condition as Example 12. The superconducting wire obtained showed a critical temperature (Tc) of 92°K and a critical current density was 12 A/cm². This fact revealed that the superconducting wire manufactured according to Example 12 possess higher critical current density. Example 13 20.8% by weight of commercially available Y₂O₃ powder, 54.7% by weight of commercially available BaCO₃ and 24.5% by weight of commercially available CuO were mixed in an attrition mill in the wet state and then dried. The dried powder was sintered at 880°C in air for 24 hours. The sintered body was pulverized and passed through a sieve to obtain powder of under 100 mesh. The steps including sintering, pulverization and screening were repeated three times. After granulation treatment, the material powder was compacted in an iron pipe having an outer diameter of 5 mm, an inner diameter of 4 mm and a length of 1 m and opposite ends of the pipe were sealed. When the pipe filled with the material powder was subjected to a series of wire-drawing operations in such a manner that its outer diameter was reduced in a cross sectional reduction ratio of 19% per pass, the pipe broke when the outer diameter thereof was reduced to 1.2 mm. Therefore, the wire-drawing was ceased when the outer diameter reduced to a value of 1.5 mm. And then, the pipe was subjected to a series of operations comprising an intermediate annealing at 750°C for 25 hours, a plurality of wire-drawing operations each of which was carried out at a cross sectional reduction ratio of 18% per pass so that the pipe was reduced to 0.6 mm in diameter, and sintering being carried out at 930°C for 3 hours. The measured value of the critical temperature (Tc) was 38°K. Example 14 20.8% by weight of commercially available Y₂O₃ powder, 54.7% by weight of commercially available BaCO₃ and 24.5% by weight of commercially available CuO were mixed in an attrition mill in the wet state and then dried. The dried powder was sintered at 950°C in air for 3 hours. The sintered body was pulverized and passed through a sieve to obtain powder of under 100 mesh. The steps including sintering, pulverization and screening were repeated three times. The resulting material powder was compacted in a set of stainless steel pipes each having an outer diameter of 5 mm, an inner diameter of 4 mm and a length of 1 m and opposite ends of the pipe were sealed. After the pipes were subjected to wire-drawing to reduce their outer diameter to 3.6 mm, they were sintered in air under the following different conditions: (1) at 950°C for 3 hours (2) at 850°C for 3 hours (3) at 700°C for 3 hours (4) at 500°C for 3 hours (5) at 850°C for 30 hours (6) at 700°C for 30 hours (7) at 500°C for 30 hours The resulting sintered ceramic wires had a length of 1.6 m and an outer metal layer of 0.4 mm thick. Electrical resistance was measured to evaluate their properties as a superconductor. The results of the measurements are given below. (In the description hereinafter, Tc means the critical temperature of superconductivity and Tcf means a temperature at which electrical resistance becomes utterly zero). In the case of condition (1), no superconductivity was observed. The color of a sliced cross section was red due to reduction of copper oxide CuO in the ceramic powder. In the case of condition (2), Tc observed was 58°K and Tcf observed was 7°K. Observation of a sliced cross section revealed that CuO was not apparently reduced but changed to a rather porous mass in comparison with the original sintered body from which the material powder was prepared. In the case of condition (3), no superconductivity was observed. Observation of a sliced section revealed that the ceramic material was not sintered completely but remained in a condition of granules. In the case of condition (4), no superconductivity was observed. Observation of a sliced cross section revealed that the material powder was hardly changed but remained in a powdered condition. In the case of condition (5), measurements showed that Tc was 84°K and Tcf was 75°K. Observation of a sliced cross section revealed that the sintered ceramic body possessed almost the same color and appearance as the original ceramic body from which the material powder was prepared. In the case of condition (6), Tc was 68°K and Tcf was 47°K. A sliced cross section was observed to be similar to that of the condition (5) but a little porous. In the case of condition (7), no superconductivity was observed. A sliced section revealed that the ceramic powder remained in granular form. Example 15 Powders of BaCO₃, Y₂O₃ and CuO each having a purity of more than 99.9% were prepared. They were weighed in such a manner that the proportions of BaCO₃:Y₂O₃:CuO became 20.8:54.7:24.5 by weight, and were mixed uniformly in an attrition mill in the wet state. After the mixture was dried at 110°C for 1 hour, it was compacted under a pressure of 100 kg/cm². The resulting compact was sintered at 940°C for 15 hours and then pulverized to obtain powder of under 100 mesh. Then, the abovementioned steps of compacting, sintering and pulverization were repeated three times. The powder obtained was used in a subsequent wire-drawing stage described in Table 1. In this Example 15, a pipe of silver was used. A variety of operational conditions and combinations of procedures adopted are summarized in Table 1. The density (%) of the resulting sintered mass was determined by dividing the weight of a sample by a volume obtained by the specific gravity measurement method in which pores displaced with solution is calculated and its result was verified by dot-counting by means of a microscope. The current density (A/cm²) thereof were determined by dividing the value of current just before a resistance appeared by a cross sectional area of a current passage. The result are also summarized in Table 1. Example 16 The same material powder as Example 15 was used and the same procedure as Example 15 was repeated except that the material powder was compacted in metal pipes of Al, Cu and Ni respectively. The density (%) of the resulting sintered mass and the current density (A/cm²) thereof were determined by the same method as abovementioned. The result are summarized in Table 2. Sample No. Material of pipe Manufacturing Process (Operational condition) Density (%) Critical Current Density (A/cm²) Ag-1 Ag Wire-drawing by dies from 20 mm  to 6 mm  in air and then sintering 62 150 Ag-2 Ag Swaging in air from 20 mm  to 6 mm  and then sintering 68 210 Ag-3 Ag Swaging at 900°C from 20 mm  to 6 mm  and then sintering 87 570 Ag-4 Ag Swaging at 900°C from 20 mm  to 10 mm  and then sintering. After then, secondary swaging at 900°C from 10 mm  to 6 mm  and then sintering 95 870 Ag-5 Ag Swaging at 900°C from 20 mm  to 10 mm  and then sintering. After then, secondary swaging in air from 10 mm  to 6 mm  and then sintering 93 800 Ag-6 Ag Swaging at 900°C from 20 mm  to 6 mm  and then sintering 81 450 Ag-7 Ag Swaging at 950°C from 20 mm  to 6 mm  and then sintering note Note: In this sample, the pipe ruptured due to poor strength of Ag, and measurements could not be made. Sample No. Material of pipe Manufacturing Process (Operational condition) Density (%) Critical Current Density (A/cm²) Al-1 Al Swaging at 600°C from 20 mm  to 2 mm  and then sintering (600°C 20 h) 75 280 Ag-2 Ag Swaging in air from 20 mm  to 2 mm  and then sintering (600°C 20 h) 58 75 Cu-1 Cu Swaging at 600°C from 20 mm  to 2 mm  and then sintering (800°C 15 h) 80 350 Cu-2 Cu Swaging in air from 20 mm  to 2 mm  and then sintering (800°C 15 h) 61 100 Ni-1 Ni Swaging at 800°C from 20 mm  to 2 mm  and then sintering (900°C 15 h) 89 370 Ni-2 Ni Swaging in air from 20 mm  to 2 mm  and then sintering (900°C 15 h) 63 110 Example 17 Powders of BaCO₃, Y₂O₃ and CuO each having a purity of more than 99.9% and an average particle size of 1 µm were prepared. They were mixed in such a proportion that the amounts of Ba, Y and Cu satisfied the following composition: Ba 0.67 Y 0.33 Cu₁O₃-δ in other words, the atom ratios of Ba:Y:Cu became 2:1:3 (the proportions of BaCO₃:Y₂O₃:CuO = 52.9:15.13:31.98 by weight) and then were kneaded in the wet state for 3 hours in a mortar. The resulting powder mixture was dried at 200°C for 7 hours under vacuum to remove water. The dried powder was sintered in air at 930°C for 24 hours and then the resulting cake-like mass was pulverized in a mortar and further milled in a ball-mill to reduce it to an average particle size of less than 30 µm. The powder obtained was compacted in a pipe of stainless steel (SUS 31OS) and opposite ends of the pipe were sealed. The pipe filled with the powder therein was subjected to repetitive operations of wire-drawing each of which was performed at a dimensional reduction ratio of 25% so that the outer diameter of the pipe was finally reduced to 1.8 mm. Innumerable through holes each having a diameter of 200 µm were perforated in the pipe at a pitch of 20 mm by means of CO₂ laser. Then, the perforated pipe was heat-treated at 1,000°C for 16 hours to sinter the powder and then cooled slowly at a rate of 10 °C/min. The sintering temperatures were selected in a range where no fusion of the metal pipe occurred. Then, the pipe was heat-treated at 700°C for 10 hours and then cooled slowly at a rate of 10°C/min. The same procedure as the abovementioned was repeated for a variety of compositions of material powder and pipes of different metals which are listed in Table 3 in which α, β, x and y mean elements and atom ratios in the following formula: (α 1-x, βx)₂Cu y O₄ The results are summarized in the Table 3 in which Tci stands for the temperature at which resistance started to drop and Jc was the value of critical current density measured at 77°K. Sample No. α β x y Material of pipe Sintering temp.(°C) Tci (°K) Jc (A/cm²) 1 Ba Y 0.33 1.0 Stainless 1,000 94 1,000 2 Ba Y 0.33 1.0 Al 900 90 800 3 Ba Y 0.33 1.0 Cu 1,000 95 1,100 4 Ba Y 0.33 1.0 Fe 1,040 91 900 5 Ba Y 0.33 1.0 Ni 1,040 92 850 6 Ba Y 0.33 1.0 Ta 1,030 94 1,050 7 Ba Y 0.33 1.0 Ag 900 91 900 8 Ba Y 0.4 1.1 Stainless 1,000 88 700 9 Ba Y 0.4 1.21 Stainless 1,000 85 600 10 Ba Ho 0.33 1.0 Stainless 1,000 91 800 11 Ba Dy 0.33 1.0 Stainless 1,000 92 1,000 12 Sr La 0.75 0.5 Stainless 1,000 41 600 13 Ba La 0.75 0.4 Stainless 1,000 43 700 14 Ba Y 0.33 0.4 Stainless 1,000 88 900 15 Ba Y 0.33 0.6 Stainless 1,000 85 800 Example 18 36.42% by weight of commercially available Bi₂O₃ powder, 23.07% by weight of commercially available SrCO₃, 23.07% by weight of commercially available CaCO₃ and 24.87% by weight of commercially available CuO were mixed in an attrition mill in the wet state and then dried. The dried powder was compacted under a pressure of 1,000 kg/cm² and then sintered at 80°C in air for 8 hours. The sintered body was pulverized and passed through a sieve to obtain powder of under 100 mesh. After granulation treatment, the material powder was compacted in a silver pipe having an outer diameter of 5 mm, an inner diameter of 4 mm and a length of 1 m and opposite ends of the pipe were sealed. The pipe filled with the material powder was subjected to wire-drawing to reduce its outer diameter to 1.8 mm. Then, the pipe was sintered at 800°C for 2 hours to obtain an sintered ceramic wire having a length of 5.0 m and having an outer silver layer coating 0.3 mm thick. The measured value of the critical temperature (Tc) of this sintered ceramic wire was 100°K.

Claims: A process for manufacturing a superconducting elongated article characterized in that it comprises the following steps: filling a metal pipe with a ceramic material powder consisting of a compound oxide having superconductivity, carrying out plastic deformation of said metal pipe filled with said ceramic material powder to reduce the cross section of said metal pipe, subjecting the deformed metal pipe to heat-treatment to sinter said ceramic material powder filling said metal pipe, and then after this step of heat treatment, cooling said metal pipe containing the sintered ceramic material powder slowly at a rate of less than 50°C/min. The process according to claim 1 characterized in that said ceramic material powder is prepared by the steps comprising mixing powders of Bi₂O₃, SrCO₃, CaCO₃ and CuO, drying and then compacting the powder mixture, sintering the compacted mass, and then pulverizing the sintered mass. The process according to claim 1 or 2 characterised in that said metal pipe is made of a metal selected from the group comprising metals of Ag, Au, Pt, Pd, Rh, Ir, Ru, Os, Cu, Al, Fe, Ni, Cr, Ti, Mo, W and Ta and alloys of these metals. The process according to any one of claims 1 to 3 wherein said heat-treatment is carried out at a temperature ranging from 700 to 1,000°C. The process according to any one of claims 1 to 4 characterized in that said plastic deformation of the metal pipe is carried out in such a manner that the cross section of the metal pipe is reduced at a dimensional reduction ratio ranging from 16% to 92%. A process for manufacturing a superconduction elongated article according to any one of claims 1 to 5, characterized in that in the said step of filling a metal pipe with a ceramic material powder consisting of a compound oxide having superconductivity, the said metal pipe is made of one of the metals selected from the group comprising Ag, Au, Pt, Pd, Rh, Ir, Ru, Os, Cu, Al, Fe, Ni, Cr, Ti, Mo, W and Ta and alloys of these metals, in that the plastic deformation of the metal pipe filled with the ceramic metal powder to reduce the cross section of the metal pipe is carried out to such extent that the cross section of the metal pipe is reduced at a dimensional reduction ratio comprising between 16% and 92%, and in that the deformed metal pipe is submitted to heat-treatment at a temperature ranging from 700 to 1,000°C to sinter the ceramic material powder filling said metal pipe. A process according to any one of claims 1 to 6, characterized in that said plastic deformation of said metal pipe is carried out by hot-plastic deformation. A process according to any one of claims 1 to 6, characterized in that said plastic deformation of said metal pipe is carried out by cold-plastic deformation. A process according to any one of claims 1 to 8, characterized in that said ceramic material powder contains a compound oxide having the crystal structure of K₂NiF₄-type oxides. A process according to claim 9, characterized in that said compound oxide is (La,Ba)₂CuO₄ or (La,Sr)₂CuO₄. A process according to any one of claims 1 to 8, characterized in that said ceramic material powder contains a compound oxide having a perovskite-type crystal structure exhibiting superconductivity having the general formula: (α 1-x ,β x )γ y O z in which α stands for an element selected from IIa group elements of the Periodic Table, β stands for an element selected from IIIa elements of the Periodic Table, γ stands for an element selected from a group comprising Ib, IIb, IIIb, IVa and VIIIa elements of the Periodic Table, and x, y and z are numbers which satisfying the following respective ranges: 0.1 ≦ x ≦ 0.9, 0.4 ≦ y ≦ 4.0 and 1 ≦ z ≦ 5. A process claimed in claim 11, characterized in that said α is Ba, β is Y and γ is Cu. A process according to any one of claims 1 to 12, characterized in that said plastic deformation is performed by wire-drawing. A process according to claim 13, characterized in that said wire-drawing is performed by means of dies, roller dies, or extruder. A process according to any one of claims 1 to 12, characterized in that said plastic deformation is performed by forging. A process according to claim 15, characterized in that said forging is performed by means of swaging unit or rolls. A process according to any one of claims 1 to 16, characterized in that said ceramic material powder consisting of a compound oxide having superconductivity is granulated before said material powder is filled into said metallic pipe. The process according to any one of claims 7 and 9 to 17, characterized in that said hot-plastic deformation is carried out at a temperature ranging from 700 to 1,000°C. The process according to any one of claims 8 to 18 characterized in that at least one step of cold-plastic deformation of said metal pipe is carried out before and/or after said hot-plastic deformation. The process according to any one of claims 1 to 7 and 8 to 19, characterized in that a series of operations of said hot-plastic deformation and said sintering step is repeated more than two times. A process according to any one of claims 1 to 20 wherein the deformed metal pipe is subjected to an intermediate annealing at such a temperature that said metal pipe is annealed and that then the resulting annealed metal pipe is subjected to another plastic deformation. The process according to any one of Claims 1 to 21 wherein openings passing through a wall of said metal pipe are made after said plastic deformation but before said heat-treatment. The process according to any one of Claims 1 to 22, characterized in that said metal pipe is removed from said sintered ceramic material powder after the cooling has been completed. The process according to claim 23 wherein said ceramic material powder is granulated before said ceramic material powder is supplied into said metal pipe. The process according to any one of claims 1 to 5 and 8 to 19 wherein openings passing through a wall of said metal pipe are made after said cold-plastic deformation but before heating.

Inventors: FUJITA, NOBUHIKO C/O ITAMI WORKS, HAYASI, KAZUHIKO C/O OSAKA WORKS, ISOJIMA, SIGEKI C/O OSAKA WORKS, ITOZAKI, HIDEO C/O ITAMI WORKS, JODAI, TETSUJI C/O ITAMI WORKS, KAWABE, NOZOMU C/O ITAMI WORKS, MURAI, TERUYUKI C/O ITAMI WORKS, SASAKI, NOBUYUKI C/O ITAMI WORKS, SAWADA, KAZUO C/O OSAKA WORKS, SIBATA, KENICHIRO C/O ITAMI WORKS, YAMAMOTO, SUSUMU C/O ITAMI WORKS, YAZU, SHUJI C/O ITAMI WORKS
Applicants: SUMITOMO ELECTRIC INDUSTRIES LIMITED
Application year: 1988
Main classification: H01B12
IPC codes: H01B13, H01L39, C04B35, H01B12, B28B1, B21C1