METHOD FOR PRODUCING A MAGNETIC HEAD

Abstract: A magnetic recording playback head is formed from a pair (7) of magnetic cores joined through a gap-forming film. A ridge (8) is produced with a curved surface for sliding contact with a magnetic tape, and having a width equal to the tape track width. Sides of the ridge are made chip-resistant by a film (9).

Description: The present invention relates to a method for producing a magnetic head to be mounted adjacent the periphery of a drum which is rotated as magnetic tape is helically passed across the drum for helical recording or playback in a video tape recorder, audio digital tape recorder, etc. Prior art magnetic tape recorders of the type contemplated by the present invention have a recording or reproducing track width of the order of several tens of microns. The process for fabricating a magnetic head having such a small track width is hereinafter described with reference to Figs. 1 and 2. As shown in Fig. 1, blocks 1a and 1b serving as two halves of a core are each worked on one surface to form a plurality of track width controlling grooves 16, and a gap forming thin film is formed on the respective gap defining surfaces 2a and 2b. Then, as shown in Fig. 2, the two blocks are joined together in such a way that the opposite grooves 16 are in registry. Thereafter, the grooves 16 are filled with a glass filler material 3 to form a single head block. This head block is ground and polished to provide a cylindrical surface that contacts the magnetic tape. The thus-worked block is sliced into discrete magnetic heads. In the head fabrication process, it is important that the half blocks 1a and 1b be joined together with registry attained between the opposite track width controlling grooves 16. If misalignment occurs, the prescribed track width is not attainable. The recent tendency is to decrease the track width defined by the magnetic heads in order to achieve a higher recording density. This has introduced even greater difficulty in joining together the two half blocks without loss of registry between the opposite track width control grooves 16. To deal with this problem a magnetic head of the type shown in Fig. 3 has been proposed. This magnetic head is fabricated by the process depicted in Figs. 4 - 7. First, blocks 5a and 5b serving as two halves of a core and which are not provided with any track width control grooves are prepared as shown in Fig. 4. After a gap-forming thin film is formed on each of the blocks, they are joined together to form a single core block 6a as shown in Fig. 5. This core block 6a is ground and polished to provide a cylindrical surface that contacts magnetic tape. Thereafter, grooves 17 are formed across the magnetic gap, except for a region corresponding to the track width (see Fig. 6), and the block 6b is sliced along the centre line of each groove 17 to form discrete magnetic heads as shown in Fig. 7. Alternatively, a head block of the type shown in Fig. 3 may be produced by filling glass 18 in the grooves 17 in the head block 6b, which is thereafter sliced into discrete magnetic heads. Because of the brittleness of the core material, chipping 6c often occurs in the magnetic head shown in Fig. 7, either during the working of the head block or on account of sliding friction with the magnetic tape after it has been worked into the magnetic head. As a further problem the magnetic tape has a tendency to wear quickly since it contacts magnetic tape over a very small area. A significant problem associated with the magnetic head shown in Fig. 3 is the great difficulty involved in achieving uniform filling of the grooves 17 with glass 18, and the resulting low production rate causes an undue increase in the price of the magnetic head compared with the product fabricated by the process illustrated in Figs. 1 and 2. JP-A-56159820 discloses the use of titanium on a head to resist abrasion. An object, therefore, of the present invention is to provide a simple method of making an inexpensive but well performing magnetic head that is free from chipping and which exhibits a high wear resistance. EP-A-0 030 625 discloses a method making a magnetic head including the steps of slicing a head block into sections, grinding and lapping these sections individually, depositing a hard material on the sides of each section individually, grinding and lapping ceramic supporting structures, coating the sides of the supporting structures with hard material, bonding two supporting structures to each section, and lapping the surface of the head to provide the desired shape. This method is very complex and is thus time consuming and expensive. The present invention provides a method of fabricating a magnetic head, the method comprising the steps of providing two half blocks of a magnetic oxide material; joining the two half blocks to form a single core block with a gap-forming thin film between respective gap-forming surfaces of the half blocks, grinding and polishing the core block to form a part cylindrical surface to be, in use, in sliding contact with a magnetic tape; cutting a plurality of track width defining grooves in the cylindrical surface leaving ridges having width equal to a track width to thereby form a head block and slicing the head block along centre lines of the grooves to form discrete magnetic heads, the method being characterised by before slicing the head block, forming a thin film of a hard nonmagnetic material on the cylindrical surface and in the track width defining grooves; grinding and polishing the head block to remove the thin film except in the grooves. In the accompanying drawings:- Figs. 1 and 2 are perspective views showing two principal steps for fabricating a prior art magnetic head; Fig. 3 is a perspective view showing another process for fabricating the magnetic head shown in Fig. 7; Figs. 4 to 7 are perspective views showing the sequence of steps for fabricating another prior art magnetic head; Figs. 8 to 11 are perspective views showing a sequence of steps for fabricating the magnetic head shown in Fig. 12; and Fig. 12 is a perspective view of a magnetic head constructed according to a preferred embodiment of the present invention. An example of a process for fabricating the magnetic head of the present invention is hereinafter described with reference to Figs. 8 - 12. In Fig. 8, half blocks made of a magnetic oxide material such as a ferrite are indicated by reference numerals 10a and 10b. After forming a gap-forming thin film on the respective gap-defining surfaces, the blocks are joined together with adhesive glass 19, as shown in Fig. 9, to form a single core block 11. This block is then ground and polished to provide a cylindrical surface that is to be in sliding contact with the magnetic tape, and a plurality of track width defining grooves 12 are cut in the cylindrical surface, leaving ridges whose width is the same as the track width, thereby producing a head block 13 as shown in Fig. 10. As shown in Fig. 11, a thin film 14 made of a hard nonmagnetic material such as alumina (Al₂O₃) or titanium nitride (TiN) is formed on the cylindrical surface of the head block 13 and in the track width defining grooves 12 by a suitable thin film forming technique such as evaporation, sputtering or ion plating. As a result, a head block 15 is obtained. The cylindrical surface of the head block 15 is ground and polished again to remove the thin film of hard nonmagnetic material 14 except in the grooves 12. The head block 15 is then sliced along the center line of each groove 12 to produce discrete magnetic heads of the type shown in Fig. 12. Each of the magnetic heads has a configuration such that the track width defined by the surface of the magnetic core 7 which contacts magnetic tape is equal to the width of the ridge 8 left between adjacent grooves and both sides of the magnetic gap in the core 7 are coextensive with the flat surfaces of the ridge 8. The surfaces of the films 9 of a nonmagnetic hard material such as alumina or titanium nitride that are formed on the ridge 8 are flush with the surface of the magnetic core 7 that is in sliding contact with the magnetic tape. With the configuration described above, the magnetic tape is in sliding contact with the curved faces of the magnetic core 7 and the film 9. The potential wear of the magnetic gap of the core 7 is appreciably reduced on account of the hardness and wear resistance of the films 9. While a preferred embodiment of the present invention has been described with reference to a magnetic head used in a video tape recorder or an audio digital tape recorder, it should be understood that the concept of the present invention is also applicable to magnetic heads for use with hard disks or floppy disks. As discussed above, in the prior art technique, two blocks serving as the halves of a core have to be joined together in such a way that the opposite grooves for controlling the track width are brought into registry. However, this track matching step is unnecessary in fabricating the magnetic head of the present invention. Track width control grooves are formed in the core blocks after they are joined together into a single head block. Moreover, the surfaces on both sides of the magnetic gap are protected by a thin film of nonmagnetic hard material against core chipping that might otherwise occur upon vigorous sliding contact with magnetic tape. The potential wear of the surface of the core that is in sliding contact with the magnetic tape is appreciably reduced on account of the wear resistance of the curved faces of the thin films of nonmagnetic hard material, which contributes to an improvement in the performance and reliability of the core. The thin film of nonmagnetic hard material is formed on a single core block which is subsequently sliced into a plurality of discrete magnetic heads. Because of the high production rate, thereby obtained the magnetic head of the present invention can be manufactured at a low cost.

Claims: A method of fabricating a magnetic head, the method comprising the steps of providing two half blocks (10a, 10b) of a magnetic oxide material; joining the two half blocks (10a, 10b) to form a single core block (11) with a gap-forming thin film between respective gap-forming surfaces of the half blocks (10a, 10b); grinding and polishing the core block (11) to form a part cylindrical surface to be, in use, in sliding contact with a magnetic tape; cutting a plurality of track width defining grooves (12) in the cylindrical surface leaving ridges (8) having width equal to a track width to thereby form a head block (13); and slicing the head block along centre lines of the grooves (12) to form discrete magnetic heads, the method being characterised by before slicing the head block, forming a thin film (14) of a hard nonmagnetic material on the cylindrical surface and in the track width defining grooves (12); grinding and polishing the head block to remove the thin film (14) except in the grooves (12). A method according to claim 1, wherein the thin film (14) is alumina or titanium oxide. A method according to claim 1 or claim 2, wherein the step of forming the thin film (14) is carried out using an evaporation process. A method according to claim 1 or claim 2, wherein the step of forming the thin film (14) is carried out using a sputtering process. A method according to claim 1 or claim 2, wherein the step of forming the thin film (14) is carried out using an iron plating process.

Inventors: OTA, HIROYUKI C/O PIONEER ELECTRONIC CORPORATION, SATO, KAZUHIKO C/O PIONEER ELECTRONIC CORPORATION
Applicants: PIONEER ELECTRONIC CORPORATION
Application year: 1988
Main classification: G11B5
IPC codes: G11B5