OPTICALLY ACTIVE COMPOUND

Abstract: A compound of (wherein n is an integer from 2 to 15; R′ is m is total number of carbon atoms in R′ and is an integer from 5 to 12, and * mark shows asymmetric carbon atom) which is useful for an electric indicative element of liquid crystal is provided.

Description: The present compound is a ferroelectric one having high speed of response to electric fields and is useful as a material for an electric indicative element of liquid crystal display. A large number of compounds have been proposed, for example, (Japan Kokai 61-271252), and (wherein R₁ is a C₆₋₁₈ alkyl group; X and Y are respectively hydrogen atom, halogen atom or a methyl group) (Japan Kokai 61-251639). Requirement for this sort of compounds useful as an electric indicative element is that a compound is able to exhibit liquid crystal phase at room temperature and that it is photochemically and chemically stable. The present compound has the formula wherein n is an integer from 2 to 15; R′ is m is total number of carbon atoms in R′ and is an integer from 5 to 12, and * mark shows asymmetric carbon atom. The present compound is prepared in the following process: Terephthalic acid dichloride is converted to 4-alkanoylbenzoic acid chloride (I) by use of a Grignard reagent. The compound (I) is esterified to obtain methyl ester (II). The ester (II) is hydrolyzed to obtain 4-n-alkanoylbenzoic acid (III). The compound (III) is allowed to react with optically active 4-alkyloxyphenol (IV) in a solvent of dicyclohexyl carbodiimide (DDC) and tetrahydrofuran (THF) in the presence of 4-dimethylaminopyridine, to obtain optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoate (V). The present compound has high speed of response to electric fields, spontaneous polarization ability and phase transition temperature near room temperature, so that it is useful for a ferroelectric liquid crystal display. Examples Preparation method and physical properties of the compounds obtained are shown in the following examples. Example 1 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoate (formula V) in which n = 5 and m = 5 1) 4-n-Hexanoylbenzoic acid A) n-Pentylbromide (100.0 g, 0.662 mol) in THF (200 ml) B) Mg (16.1 g, 0.662 mol) in THF (50 ml) A part of A) was charged in B) to cause a reaction at room temperature. The remaining of A) was added in dropwise over one hour and ten minutes. After the addition was over, the mixture was refluxed under heating for 3 hours. Reflux was further continued for 2 hours in the presence of cadmium chloride (60.7 g), before cooling. Grignard reagent thus prepared was added drop by drop to terephthaloyl chloride (268.6 g, 1.324 mol) solution in THF (1 ℓ) over 50 minutes. After being stirred for 2 hours at room temperature, the mixture was heated to 50 °C and stirred for 15 hours. Furthermore, methanol (200 ml) and pyridine (170 ml) were added at room temperature and stirring was continued for 2 hours. The solution was filtered and filtrate was distilled under reduced pressure. The residue obtained was subjected to colmun chromatography (silica gel). Ester obtained (71.0 g) was recrystallized in methanol to obtain a purufied product (44.4 g) which was hydrolyzed with alcoholic caustic potash to obtain n-hexanoylbenzoic acid (37.6 g, yield 25.8 %). 2) Objective ester To anhydrous tetrahydrofuran (THF, 60 ml) were added n-hexanoylbenzoic acid (20 mmol), optically active 4-(2-methylbutoxy)phenol (20 mmol), dicyclohexyl carbodiimide (DCC) (22 mmol) and a small amount of 4-dimethylaminopyridine. The mixture was stirred for 2 hours at room temperature. After an insoluble matter was filtered, the mixture was distilled to remove THF. The residue was recrystallized in ethanol to obtain the objective ester (9 mmol, No. 1). IR-spectrum of the ester is shown in Fig. 9. Compounds where n = 5 and m = 7, 8 and 9 in the formula (V) were prepared in the similar manner. That is, compounds (Nos. 9, 17 and 25) were prepared by using optically active 4-(4-methylhexoxy)phenol, 4-(5-methylheptoxy)phenyl and 4-(6-methyloctoxy)phenol, respectively, in place of the above optically active 4-(2-methylbutoxy) phenol. IR-spectra (KBr) of these compounds are shown in Figs.17, 25 and 33, respectively. Table 1 shows NMR spectra of the above compounds. Example 2 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates where n = 6 and m = 5, 7, 8 and 9, respectively, in the formula V 1) 4-n-Heptanoylbenzoic acid n-Hexylbromide (109.2 g, 0.622 mol), Mg (16.1 g, 0.622 mol), cadmium chloride (60.7 g) and terephthaloyl chloride (268.6 g, 1.324 mol) were allowed to react in the similar manner to Example 1 to prepare the titled acid (41.6 g). Yield 26.9 %. 2) Objective esters Esters (Nos. 2, 10, 18 and 26) (about 9 mmol each) were obtained in the similar manner to Example 1,2). IR spectra are shown in Figs.10, 18, 26 and 34, respectively. Table 1 shown NMR spectra of the above compounds. Example 3 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates where n = 7 and m = 5, 7, 8 and 9, respectively, in the formula V 1) 4-n-Octanoylbenzoic acid n-Heptylbromide (118.5 g 0.622 mol), Mg (16.1 g, 0.622 mol), cadmium chloride (60.7 g) and terephthaloylchloride (268.6 g, 1.324 mol) were allowed to react in the similar manner to Example 1 to prepare the titled acid (50.5 g). Yield 30.8 %. 2) Objective esters Esters (Nos. 3, 11, 19 and 27) (about 9 mmol each) were obtained in the similar manner to Example 1, 2). IR spectra are shown in Fig. 11, 19, 27 and 35, respectively. Table 1 shown NMR spectra of the above compounds. EXAMPLE 4 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates (formula V) in which n = 8 and m = 5, 7, 8 and 9. 1) 4-n-Nonanoylbenzoic acid A) n-Octylbromide (73.7 g, 0.382 mol) in THF (200 ml) B) Mg (9.28 g, 0.382 mol) in THF (40 ml) A part of A) was charged in B) to cause a reaction at room temperature. The remaining of A) was added in dropwise over one hour. After the addition was over, the mixture was refluxed under heating for 4 hours. Reflux was further continued for 2 hours in the presence of cadmium chloride (35.0 g), before cooling. Grignard reagent thus prepared was added drop by drop to terephthaloyl chloride (115.0 g, 0.764 mol) solution in THF (1 ℓ) over one hour. After being stirred for 3 hours at room temperature, the mixture was heated to 50°C and stirred for 12 hours. Furthermore, methanol (150 ml) and pyridine (120 ml) were added at room temperature and stirring was continued for 6 hours. The solution was filtered and filtrate was distilled under reduced pressure. The residue obtained was subjected to column chromatography (silica gel). Ester obtained (34.5 g) was hydrolysed with alcoholic caustic potash to obtain n-nonanoylbenzoic acid (31.5 g, yield 31.8%). 2) Objective esters Ester (Nos. 4, 12, 20 and 28) (about 0.895 mmol each) was obtained in the similar manner to Example 1,2). IR spectra are shown in Figs. 12, 19, 28 and 36, respectively. Table 1 shown NMR spectra of the above compounds. Example 5 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates where n = 9, m = 5, 7, 8 and 9, respectively in the formula V 1) 4-Decanoylbenzoic acid n-Nonylbromide (80.0 g, 0.387 mol), (Mg 9.40 g, 0.387 mol), cadmium chloride (35.5 g) and terephthaloyl chloride (157.0 g, 0.773 mol) were allowed to react in the similar manner to Example 1 to prepare the title acid (26.5 g). Yield 24.8%. 2) Objective esters Esters (Nos. 5, 13, 21 and 29) (about 0.9 mmol each) were obtained in the similar manner to Example 1,2). IR spectra are shown in Figs. 13, 21, 29 and 37, respectively. Table 1 shows NMR spectra of the above compounds. Example 6 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates where n = 10, m = 5, 7, 8 and 9, respectively, in the formula V 1) 4-n-Undecanoylbenzoic acid n-Decylbromide (76.2 g, 0.345 mol), Mg (8.38 g, 0.345 mol), cadmium chloride (31.7 g) and terephthaloyl chloride (140.1 g, 0.690 mol) were allowed to react in the similar manner to Example 1 to prepare the titled acid (25.7 g). Yield 25.7 %. 2) Objective esters Esters (Nos. 6, 14, 22 and 30) (about 0.9 mmol each) were obtained in the similar manner to Example 1,2). IR spectra are shown in Figs. 14, 22, 30 and 38, respectively. Table 1 shows NMR spectra of the above compounds. Example 7 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates where n = 11, m = 5, 7, 8 and 9, respectively in the formula V 1) 4-n-Dodecanoylbenzoic acid n-Undecylbromide (117.5 g, 0.500 mol), Mg (12.2 g, 0.500 mol), cadmium chloride (45.8 g) and terephthalyl chloride (202.9 g, 1.00 mol) were allowed to react in the similar manner to Example 1 to prepare the titled acid (32.3 g). Yield 21.3 %. 2) Objective esters Esters (Nos. 7, 15, 23 and 31) (about 0.9 mmol each) were obtained in the similar manner to Example 1,2). IR spectra are shown in Figs. 15, 23, 31 and 39, respectively. Table 1 shows NMR spectra of the above compounds. Example 8 Optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoates where n = 12 and m = 5, 7, 8 and 9, respectively, in the formula V 1) 4-n-Tridecanoylbenzoic acid n-Dodecylbromide (124.5 g, 0.500 mol), Mg (12.2 g, 0.500 mol), cadmium chloride (45.8 g) and terephthalyl chloride (202.9 g, 1.00 mol) were allowed to react in the similar manner to Example 1 to prepare the titled acid (28.5 g). Yield 17.9 %. 2) Objective esters Esters (Nos. 8, 16, 24 and 32) (about 0.9 mmol each) were obtained in the similar manner to Example 1,2). IR spectra are shown in Figs. 16, 24, 32 and 40, respectively. Table 1 shows NMR spectra of the above compounds. Tables 2 - 9 show phase transition temperatures of compound Nos. 1 - 32 prepared in Examples 1 - 8, in accordance with differential thermal analysis (SEIKO DENSHI KOGYO, DSC-20). Tables 10 - 13 show phase transition temperatures of some compounds prepared in Examples 1 - 8, by use of a hot stage and a polarizing microscope. Figs. 1 - 8 are graphs of carbon numbers in an aliphatic group (n) vs. phase transition temperature of the present optically active 4-alkyloxyphenyl 4′-n-alkanoylbenzoate.

Claims: 1. A compound having the formula wherein n is an integer from 2 to 15; R′ is m is total number of carbon atoms in R′ and is an integer from 5 to 12, and * mark shows asymmetric carbon atom. 2. A compound according to claim 1 wherein n is an integer from 5 to 12 and m is an integer from 5 to 9.

Inventors: IMAI, YOSHIO, KAWAMURA, ICHIRO
Applicants: SHOWA SHELL SEKIYU KABUSHIKI KAISHA
Application year: 1988
Main classification: C07C69
IPC codes: C09K19, C07C69