Superconducting composite

Abstract: A superconducting composite comprising a compound oxide type superconductor and an outer metal pipe on which said superconductor is supported, characterized in that (i) said outer metal pipe is made of at least one of metals selected from a group comprising gold, silver and platinum metals and their alloys or (ii) an intermediate layer made of these precious metals is interposed between the compound oxide and the metal pipe. The composite may be in a form of a solid pipe or a hollow pipe having a superconducting thin layer deposited on an inner surface of the metal pipe.

Description: Background of the Invention Field of the invention The present invention relates to a composite having superconducting property and a process for manufacturing the same. Particularly, it relates to a superconducting composite, such as a wire having high and stable critical temperature and critical current density. Description of the related art Under the superconducting condition, a perfect diamagnetism is observed and no difference in potential is observed for all that an electric current of a constant finite value is observed internally, and hence, a variety of applications of superconductivity have been proposed in the field of electric power transmission as a means for delivering electric power without loss. The superconductivity can be utilized in the field of power electric applications such as MHD power generation, power transmission, electric power reservation or the like; in the field of transportation such as magnetic levitation trains or magnetically propelled ships; high sensitive sensors or detectors for sensing very weak magnetic fields, microwave, radiant ray or the like, in the medical field such as high-energy beam radiation unit; in the field of science such as NMR or high-energy physics; or in the field of fusion power generation. In addition to the abovementioned power electric applications, the superconducting materials can be used in the field of electronics, for example, as a Josephson device which is an indispensable switching device for realizing a high-speed computer which consumes very reduced power. However, their actual use has been restricted because the phenomenon of superconductivity can be observed only at very low cryogenic temperatures. Among known superconducting materials, a group of materials having so-called A-15 structure show rather higher Tc (critical temperature of superconductivity) than others, but even the top record of Tc in the case of Nb 3 Ge which showed the highest Tc could not exceed 23.2 K at most. This means that liquidized helium (boiling point of 4.2K) is the only cryogen which can realize such very low temperatures of Tc. However, helium is not only a limited costly resource but also requires a large-scaled system for liquefaction. Therefore, there has been a strong demand for other superconducting materials having higher Tc. But no material which exceeded the abovementioned Tc had been found for all studies for the past ten years. It has been known that certain ceramics material of compound oxides exhibit the property of superconductivity. For example, U. S. patent No. 3,932,315 discloses a Ba-Pb-Bi type compound oxide which shows superconductivity and Japanese patent laid-open No. 60-173,885 discloses that Ba-Bi type compound oxides also show superconductivity. These types of superconductors, however, possess a rather low transition temperature of about 10 K and hence usage of liquidized helium (boiling point of 4.2 K) as cryogen is indispensable to realize superconductivity. Possibility of existence of a new type of superconducting materials having much higher Tc was revealed by Bednorz and Müller who discovered a new oxide type superconductor in 1986 [Z. Phys. B64 (1986) 189]. This new oxide type superconducting material is [La, Ba] 2 CuO 4 or [La, Sr] 2 CuO 4 which are called K 2 NiF 4 -type oxides having a crystal structure which is similar to known perovskite type oxides. The K 2 NiF 4 -type oxides show such higher Tc as 30 K which are much higher than the known superconducting materials and hence it becomes possible to use liquidized hydrogen (b.p. = 20.4 K) or liquidized neon (b.p. = 27.3 K) as a cryogen which brings them to exhibit the superconductivity. It was also reported that C. W. Chu et al discovered in the United States of America another type of superconducting material having a critical temperature in the order of 90 K in February 1987, and hence possibility of existence of high-temperature superconductors has burst on the scene. However, the above mentioned new type of superconducting materials which was just born have been studied and developed only in the form of sintered bodies as a bulk produced from powders but have not been tried to be shaped into a wire form. The reason is that the new type of superconductors are ceramic materials of compound oxide which do not possess enough plasticity or cannot be worked easily in comparison with well-known metal type superconducting materials such as Ni-Ti alloy, and therefore they cannot or are difficult to be shaped or deformed into an elongated article such as a wire by conventional techniques such as wire-drawing technique in which superconducting metal is drawn directly or in embedded condition in copper into a wire form. Still more, the above mentioned sintered ceramic materials must be shaped into an elongated structure when they are used as a superconducting wire in practice. However, the above mentioned superconducting materials obtained in the form of a sintered body are very fragile and are apt to be broken or cracked under even very weak mechanical stress. And hence, when they are shaped into a wire, special attention must be paid for their handling in order not to be broken. It was proposed in Japanese patent laid-open No. 61-131,307 a method for manufacturing a superconducting wire from a metal type superconducting material which is apt to be oxidized and very fragile such as PbMo 0.35 S 8 , comprising charging the material metal powder in a metal shell, extruding the metal shell filled with the material powder at a temperature higher than 1,000 °C, and then drawing the extruded composite. This metal working technique, however, cannot apply directly to ceramic material consisting of compound oxide, because the compound oxide type superconducting materials cannot exhibit the superconductivity if the specified or predetermined crystal structure is not realized. In other words, a superconducting wire which shows higher critical temperature and higher critical current density and which is useable in actual applications cannot be obtained outside predetermined optimum conditions. In particular, if the shell is not selected from proper materials, the resulting compound oxide will be reduced due to chemical reaction with the metal of the shell, resulting in poor or inferior properties of superconductivity. A polycrystal having completely uniform crystal structure cannot be obtained from particles having superconducting properties alone. Still more, the phenomenon of superconductivity is apt to be easily broken down in stronger magnetic field and under the fluctuation or unhomogeneous distribution of temperature in the sintered body as well as the abovementioned oxide type superconducting materials possess rather higher specific resistance and lower heat-conductivity above the critical temperature. Therefore, if the phenomenon of superconductivity breaks down locally, the sintered body produces Joule heat caused by the superconducting current preserved therein and explosive evaporation of cryogen is induced when the heated portion of the sintered body contacts with the cryogen. In order to avert this danger, in conventional metal type superconducting materials, the superconducting metal is shaped in the form of fine wires or filaments a plurality of which are embedded in electroconductive metal which plays the roll of a by-pass of electric current when superconductivity breaks down. The oxide type superconducting materials are, however, difficult to be shaped or deformed into such filaments, because they have not enough plasticity or processability in comparison with well-known metal type superconducting materials such as Ni-Ti alloy. In order to realize a reliable and practical superconducting structure, it is indispensable that the structure possesses enough strength and tenacity which is sufficient to endure bending force during usage and also has as fine a cross sectional dimension as possible in such manner that it can transmit currents at higher critical current density and at higher critical temperature. However, conventional techniques cannot or are difficult to produce wire shaped ceramic articles possessing satisfactory mechanical strength and tenacity as well as a higher dimensional ratio of length to cross section. Taking the abovementioned situation into consideration, the present inventors have proposed processes for producing sintered ceramic wires having a practically usable higher dimensional ratio of length to cross section without using organic binder which is a cause of deterioration of strength and tenacity in EP-A-0 281 444 and 0 281 474 in which a metal pipe filled with material powder is subjected to plastic deformation such as wire-drawing technique by means of a die and then is sintered. These solutions are themselves satisfactory but the present inventors continued to develop another process which can produce a ceramic wire possessing higher strength and no breakage and complete the present invention. Therefore, an object of the present invention is to overcome the abovementioned problems of the conventional technique and to provide an improved process for producing a superconducting wire-like composite which has a higher Tc and higher stability as superconductor which can be applicable to practical uses. Summary of the Invention The present invention provides a solid superconducting wire comprising an outer metal pipe and a core of sintered powder of compound oxide superconductor compacted in said outer metal pipe, said outer pipe having on its inner surface a protective layer, characterised in that said outer metal pipe is made of at least one metal selected from the group comprising gold, silver, platinum metals and their alloys, and said protective layer is made of an oxide of a material of which said outer metal pipe is made. It is to be noted that a solid superconducting wire comprising an outer metal tube, for instance of silver, and a core of sintered powder of compound oxide compacted in said outer metal pipe is known from Extended Abstracts High Temperature Proceedings of Symposium S, 1987, Spring Meeting of Material Research Society, 23rd-24th April 1987, pp 219-221; S. Jin et al. Anyway the outer pipe of this known superconducting wire is devoid of any protective layer on its inner surface . The superconductor is compacted in the outer metal pipe made of precious metals having a lower electrical resistance, a higher specific heat and a higher heat conductivity, so that the resulting solid wire-like composite shows higher mechanical strength because a fragile sintered article is supported by a metallic sheath having relatively higher strength and tenacity than the sintered article. Still more, according to the present invention, oxygen contents in the superconducting sintered body can be stabilized because of the presence of the outer metal pipe. In fact, the oxygen contents of the abovementioned compound oxides such as an oxide containing a IIa element and a IIIa element which can be used advantageously in the present invention may vary or change if they contact directly with a metal which is liable to be oxidized. To solve this problem, according to the present invention, the outer metal pipe is made of at least one of precious metals selected from gold, silver, platinum metals or their alloys to enclose the oxide therein so that the variation of oxygen contents in the compound oxide is suppressed. An inner surface of the metal pipe has a protective layer which resists to oxidation so that the oxygen contents in the compound oxide is maintained within an optimum range. This protective layer is made of an oxide such as Ago which can be produced by oxidizing the inner surface of the metal pipe. The outer metal pipe may have perforations or through holes which make a part of the superconductor open to the atmosphere. To realize such structure, the outer metal pipe may be made of a cylindrical wire netting surrounding tightly the solid superconductor. A metal wire or wires may be embedded in the superconductor. The wires are preferably surface-treated with a material which is inert or inactive with respect to the superconductor. The solid composite abovementioned is produced by a process characterized by the steps comprising preparing at least one powder selected from the group comprising (i) a powder mixture of compounds each containing at least one of constituent elements of the compound oxide and (ii) a sintered powder of compound oxide prepared by sintering the powder mixture of (i) and then by pulverizing the obtained sintered body, compacting the material powder in a metal pipe made of at least one metal selected from the group comprising gold, silver and platinum metals and their alloys, and then heating the metal pipe filled with the material powder at a temperature ranging between an upper limit corresponding to the lowest melting point of any one of constituent components in the material powder and a lower limit which is lower by 100 °C than said upper limit to sinter said material powder inside the outer metal pipe. Each of the compounds may be an oxide powder or a carbonate powder of constituent elements of said compound oxide. The atomic ratio of elements in said material powders may be adjusted to the same value as the atomic ratio of constituent elements in said compound oxide to be produced. The material powder may be compacted under a pressed condition and/or may be granulated previously. Wire-drawing may be performed during or after the sintering operation. It is also possible to heat-treat a sintered product at a temperature ranging from 160 °C to 700 °C. The heat-treatment may be carried out after wire-drawing but before the sintering operation. Generally the sintering of the material powder may be carried out at a temperature ranging from 500 °C to 1,200 °C in which metal oxide such as AgO is decomposed to Ag and oxygen which do not reduce the compound oxide, so that the oxygen contents in the oxide can be maintained at a constant value which is beneficial to the crystal structure and/or oxygen deficiency of superior superconductor of compound oxides. A hollow composite comprises an outer metal pipe made of Ag, Au or platinum elements or their alloys and a layer of compound oxide type superconductor applied or deposited on an inner surface of the metal pipe. The layer of compound oxide type superconductor may be preferably deposited by sputtering technique on an inner surface of the metal pipe. The outer metal pipe may be closed at opposite ends thereof and/or may be filled with inert gas. It is also possible to circulate a coolant through the interior of the hollow pipe. It is also possible to reduce the cross section of the metal pipe by wire-drawing to obtain a finer pipe after the layer of compound oxide type superconductor is formed on the inner surface of the metal pipe. It is also possible to form an additional inner protective layer consisting of a material which has a lower coefficient of thermal expansion than the superconducting compound oxide layer supported on the inner surface of the metal pipe. The material having lower coefficient of thermal expansion may be Si, zirconium, SiO 2 or glass. The layer of superconductor may be formed also by a wet-coating technique including application or coating of a thin film layer of superconducting material containing an organic binder on the inner surface followed by sintering thereof. Now, the present invention will be described with reference to attached drawings which illustrate preferred embodiments of the present invention but are not limitative of the present invention. Brief Description of the drawings FIG. 1 is an illustrative cross sectional view which is similar to FIG. 1 and which shows another embodiment of a solid composite according to the present invention. FIG. 2A and 2B illustrate two variations of the solid composite shown in FIG.2. FIG. 3, 4 and 5 are cross sectional views of still another embodiment of composites according to the present invention. FIG. 6 is an illustrative view of an apparatus which can be used for manufacturing continuously a composite having a tape-like configuration according to the present invention. FIG. 1 illustrates an embodiment of a composite in which a layer of PtO 23 is interposed between an outer Pt pipe 22 and a sintered mass of compound oxide 21 compacted in the Pt pipe 22. The PtO layer 23 can be produced previously by heating an inner surface of the Pt pipe 22 in air and will supply oxygen produced by thermal decomposition thereof at the following sintering stage to the superconducting material filled therein to control the oxygen contents of the sintered compound oxide to a proper value. Two variations shown in FIG. 2A and 2B illustrate a rectangular superconducting wire or rod and a flat tape-like superconductor according to the present invention. In these variations, a sintered mass 31a and 31b is enclosed in an outer Pt pipe 32a or in a platinum band 32b through an interface layer of PtO 33a and 33b. The composite of FIG. 2A may be produced by deforming a round pipe or by using a rectangular pipe or can be manufactured by a process including steps of molding a rectangular superconductor and then covering the molded article with a metal sheath . FIG. 3, 4 and 5 show three variations of solid composite according to the present invention. In these embodiments, a plurality of platinum wires 84, 94 and 104 covered with respective oxide layers 85, 95 and 105 are embedded in a core of compound oxide type superconductor 81, 91 and 101 which is surrounded by an outer platinum pipe 82, 92 or an outer platinum band 102. In the embodiments shown, an oxide layer of PtO 83, 93 and 103 is interposed at an interface between the core 81, 91 and 101 and the outer sheath 82, 92 and 102. The oxide layer 83, 93 and 103 can be produced easily by heating in air an inner surface of the outer sheath 82, 92 and 102 to oxidize the same. The existence of the oxide layer 83, 93 and 103 is preferable to prevent the oxygen contents in the sintered compound oxide from being influenced by chemical reaction with a material of the pipe. The composite shown in FIG. 4 is similar to that of FIG. 3, but contains a larger number and/or thicker platinum wires 94 in the superconducting compound oxide core 91. In fact, if superconductivity is broken down accidentally, a very high intensity of electric current must be passed by through the ordinary conductors composed of the outer metal pipe 92 and embedded wires 94. Therefore, the embodiment shown in FIG. 4 is preferable for applications requiring higher current intensity such as electromagnets used in a strong magnetic field. FIG. 6 is an illustrative and diagrammatical drawing of an apparatus which can be applied to the production of a composite according to the present invention continuously. In this case, the material ceramic powder is preferably blended with an organic binder and can be prepared as follows: At first, powders of Y 2 O 3 , Ba 2 CO 3 and CuO each having purity of more than 3 N and an average particle size of 5 µm were mixed with such an atom ratio that the proportions of Ba, Y and Cu in a composition of (Ba 1-x Y x )Cu y O z correspond to values of x = 0.2 and y = 1 and then the resulting mixture was sintered in air at 920 °C for 12 hours. Then, the sintered mass is pulverized in a mortar. After the same procedure of sintering and pulverization is repeated for three times, the resulting sintered powder is ground by high purity alumina balls in a ball mill for 5 hours to obtain a material powder having an average particle size of less than 5 µm. The material powder is mixed and kneaded with a binder of PVB (polyvinylbutylal) in a solvent of toluene containing a plasticizer of DBP (dibutylphthalate). The resulting paste is shaped into a sheet having a thickness of 0.8 mm, a width of 300 mm and a length of 5 m and dried to ready to be used in the apparatus shown in FIG. 6. The apparatus shown in FIG. 6 includes a continuous furnace provided with two heating zones, i.e. a binder-removing zone 242 and a sintering zone 243. An elongated shaped tape or wire 244 is supplied to the inlet of the binder-removing zone 242 from a coiler 245. The elongated article 244 unwound from the coiler 245 is fed continuously to the binder-removing zone 242 in which the elongated article 244 is heated at a temperature of 400 to 700 °C to remove the binder out of the elongated article 244. After the binder-removing zone 242, the elongated article 244 is passed to a continuous lining station 246 which is positioned at the downstream side of the binder-removing zone 242. The continuous lining station 246 is provided with a drum 248 for feeding a sheet 247 of precious metal or alloy to a guide 249 where the sheet 247 is wound around the elongated article 247. A seam of the wound sheet 247 is welded by means of a laser welder 220 so that the elongated article 244 is wrapped by the metal sheet 247. The resulting composite comprising the elongated article 244 and the covering sheet or outer sheath 247 is then passed to the sintering zone 243 where the composite is heated at a temperature of 850 to 950 °C in oxygen containing atmosphere to sinter the elongated article. The longitudinal dimension or length of the sintering zone 243 and the advancing velocity of the composite can be adjusted in such manner that the sintering is performed completely. The product 241 thus obtained is cooled down slowly at a cooling speed of 8 °C/min and may be wound about a drum 252 for stock. The product possesses enough flexibility and self-supporting properties, since the elongated article 244 contains the binder. The apparatus shown in FIG. 6 permits to carry out the sintering operation continuously at a high productivity. The product produced by the abovementioned apparatus is further heat-treated for example at 700 °C for 36 hours under oxygen containing atmosphere to obtain the superconducting composite shown in FIG. 2B. The composite shown in FIG. 5 can be also produced by the apparatus shown in FIG. 6. In this case, when the paste is shaped into a sheet having a thickness of 0.8 mm, a width of 300 mm and a length of 5 m, for example fifty platinum wires whose surface is oxidized previously are embedded in the sheet and dried to ready to be used in the apparatus shown in FIG. 6. In the apparatus, the binder is removed at 400 to 700 °C and a silver sheath is put around the sheet. The resulting composite is heated in air at 935 °C for 5 hours to sinter the sheet. The composite comprising the elongated compound oxide and the outer metal sheath produced by the present invention can be shaped or deformed into a desired configuration such as a coil or the like due to the higher flexibility and self-supporting property, so that the sintering can be performed in the condition of the coiled configuration or in a condition that the coiled is supported on any other conductive body. The existence of the sheath of Pt metal or its alloy also increase the deflective strength. The composites obtained by the abovementioned processes according to the present invention can be utilized in a variety of applications of superconductors as they are. However, when a clearance which may occur eventually between the outer metal pipe and the sintered compound oxide core is undesirable, the composite can be further caulked or wire-drawn under moderate condition during the sintering operation or before the composite loses heat. The wire-drawing is preferably performed during the sintering stage. In still another variation, the outer metal pipe may have a plurality of axial recesses or holes or bores in which the material powder is filled which is sintered according to the process described hereabove. In this structure, the outer metal pipe functions as a heat radiant passage during quenching stage and a bypass of electric current when superconductivity is broken down. It is apparent from the above description that there is no possibility of chemical reduction of the sintered compound oxide with the outer metal pipe and hence the superconductor is stabilized chemically, because the pipe is made of precious metal and has an interface layer made of precious metal. Namely, the resulting ceramic wire exhibits improved property of superconductivity due to its crystal structure and oxygen deficiency which are critical factor in perovskite type or quasi-perovskite type superconductors. Still more, since the composite of the present invention is isolated from oxidative atmosphere because of the presence of the outer metal sheath, the perovskite type or quasi-perovskite type superconductors which have no high resistance to oxidation can be protected from surrounding atmosphere effectively. The composites obtained by the present invention can be utilized as superconducting wires or parts due to their high and stable Tc. Description of the preferred embodiments Superconductor One of the preferred embodiments of the compound oxide from which the superconductor is composed is a compound oxide represented by the general formula: (α 1 - x β x )γ y O z in which α stands for an element selected from IIa group of the Periodic Table, β stands for an element selected from IIIa group of the Periodic Table and γ stands for an element selected from a group comprising Ib, IIb, IIIb and VIII grougs of the Periodic Table, and small letter "x" represents the atomic ratio of β and is a number which satisfies the range of 0.1 ≤ x ≤ 0.9 with respect to the total of (α+β) which is equal to 1, small letters "y" and "z" represent atomic ratios of y and oxygen (O) respectively and satisfy ranges of 1.0 ≤ y ≤ 4.0 and 1 ≤ z ≤ 5 respectively. The superconducting compound oxide have preferably perovskite type structure or quasi-perovskite type structure. The term of "quasi-perovskite type structure" means any oxide that can be considered to have a crystal structure that is similar to perovskite-type oxides and may include an orthorhombically distorted perovskite or a distorted oxygen-deficient perovskite or the like. In practice, the element α is preferably selected from Ba, Sr and/or Ca and the element β is preferably selected from Y, La and/or lanthanid such as Sc, Ce, Gd, Ho, Er, Tm, Yb, Lu and the element γ is preferably Cu. It can be mentioned, as preferred compound oxides obtained by combinations of these elements, Ba-Y-Cu-O type oxide such as YBa 2 Cu 3 O 7-δ , Ba-La-Cu-O type oxide or Sr-La-Cu-O type oxide such as [La 1-x , Ba x ] 2 CuO 4-y , in which x and y are numbers which are less than 1. In case of Ba-Y-Cu type compound oxides, a proportion of from 10 to 80 % of Ba may be substituted by one or two elements selected from a group comprising Mg, Ca and Sr and/or a proportion of from 10 to 80 % of Y may be substituted by one or two elements selected from a group comprising La and lanthanid. If the proportions of the substituents become outside of the abovementioned range of from 10 to 80 %, no improvement of superconductivity is expected. In the preferred embodiment, the compound oxide type superconductor can be prepared from a material powder which may be (i) a powder mixture of oxide powders or carbonate powders of constituent elements of the compound oxide to be produced, such as BaCO 3 , Y 2 O 3 , CuO or (ii) a sintered powder of compound oxide prepared by sintering the powder mixture of (i) and then by pulverizing the obtained sintered mass such as YBa 2 Cu 3 O 7-δ or [La 1-x , Ba x ] 2 CuO 4-y . The sintered powder mixture (ii) is preferable to facilitate control of proportions of the constituent elements in the material powder in order to obtain a uniform product of sintered compound oxide having proper proportions of the constituent elements. The material powder may be prepared also from fluoride, nitrate, sulphate, or the like in addition to or in place of the oxide and carbonate. According to a preferred embodiment, additional operations such as wire-drawing, heat-treatment or annealing can be carried out before or after or during the sintering operation. Namely, after a powder mixture of compounds is compacted in a metal pipe made of precious metals such as gold, silver or platinum metals, the pipe is subjected to a series of operations comprising annealing, wire-drawing and sintering. The wire-drawing may be performed by any means including dies, roller dies, rolling mill, swaging units or extruder. The sintering can be carried out at a temperature ranging between an upper limit which is defined by a melting point which corresponds to the lowest melting point of any one of the constituent components in the material powder and a lower limit which is lower by 100 °C than said upper limit. The annealing can be carried out at a temperature which is lower than the sintering temperature, preferably lower than 160 °C. Cooling of the hot composite after the annealing and sintering operations is carried out at a cooling speed lower than 50 °C/min, more particularly lower than 10 °C/min. It is also possible to remove the outer metal pipe after the annealing or wire-drawing. According to another preferred embodiment, after a powder mixture of compounds is compacted in a metal pipe made of silver, the pipe is subjected to a series of operations comprising annealing, wire-drawing, intermediate sintering, wire-drawing and sintering. According to still another preferred embodiment, an additional outer metal layer is formed on an outer surface of the pipe. Namely, after a powder mixture of compounds is compacted in a metal pipe and the pipe is subjected to annealing and wire-drawing, an additional outer metal layer is applied on the outer surface of the pipe and then the resulting pipe is wire-drawn before the composite is heated to sinter the material powder. In this case, the additional outer metal layer can be formed by plating technique or caulking or cladding technique in which a metal pipe having a larger inner diameter than the composite pipe is put on the composite pipe and then is caulked tightly on the outer surface of the composite pipe. In this case also, after the pipe filled with the material powder therein is wire-drawn, it is possible to remove the outer metal pipe at the same time when the material powder is sintered. The sintered composite is cooled at a low cooling speed. The dimensional reduction ratio of the wire-drawing is preferably within a rage of 16 to 92 %. According to still another embodiment, after a powder mixture of compounds is compacted in a metal pipe and the pipe is wire-drawn, the pipe is subjected to a series of operations comprising annealing, wire-drawing and sintering. The steps of wire-drawing, annealing and second wire-drawing may be repeated for several times. Another type of superconductors which are applicable to the present invention include following compound oxides: (i) a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element δ selected from Va group of the Periodic Table and an element γ selected from a group comprising Ib, IIb, IIIb and VIII groups of the Periodic Table. Particularly, the elements α 1 and α 2 are preferably Sr and Ca, the element δ is preferably Bi and the element γ is preferably Cu such as in the case of Ca-Sr-Bi-Cu type oxides for example Ca 2 Sr 4 Bi 4 Cu 6 O 20+δ , and (ii) a compound oxide including at least two elements α 1 and α 2 selected from IIa group of the Periodic Table, an element ε selected from IIIa group of the Periodic Table and an element y selected from a group comprising Ib, IIb, IIIb and VIII groups of the Periodic Table. Particularly, the elements α 1 and α 2 are preferably Ba and Ca, the element δ is preferably Tl and the element γ is preferably Cu such as a case of Tl 4 Ba 4 Ca 4 Cu 6 O 20+δ .

Claims: A solid superconducting wire comprising an outer metal pipe and a core of sintered powder of compound oxide superconductor compacted in said outer metal pipe, said outer pipe having on its inner surface a protective layer, characterised in that said outer metal pipe (22, 32a, 32b) is made of at least one metal selected from the group comprising gold, silver, platinum metals and their alloys, and said protective layer (23, 33a, 33b) is made of an oxide of a material of which said outer metal pipe (22, 32a, 32b) is made.

Inventors: AWAZU TOMOYUKI, JODAI TETSUJI, KAWABE NOZOMU, MURAI TERUYUKI, YAMAMOTO SUSUMU, YAZU SHUJI, AWAZU, TOMOYUKI, JODAI, TETSUJI, KAWABE, NOZOMU, MURAI, TERUYUKI, YAMAMOTO, SUSUMU, YAZU, SHUJI, AWAZU, TOMOYUKI C/O ITAMI WORKS, JODAI, TETSUJI C/O ITAMI WORKS, KAWABE, NOZOMU C/O ITAMI WORKS, MURAI, TERUYUKI C/O ITAMI WORKS, YAMAMOTO, SUSUMU C/O ITAMI WORKS, YAZU, SHUJI C/O ITAMI WORKS
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES LIMITED
Application year: 1988
Main classification: H01L39
IPC codes: B21C1, H01B12, H01L39, H01B13, C04B35, C01G1, B28B1