METHOD FOR PRODUCTION OF HYDROXYLAMMONIUM SALT

Abstract: Catalysts useful for catalytic reduction of nitrogen monoxide with hydrogen to produce hydroxyl­ ammonium salts are obtained by reductive treatment of a platinum compound with a thiosulfate under conditions of S/Pt is 0.3 to 5, wherein S is amount of sulfur in thio­ sulfate and Pt is platinum in platinum compound.

Description: The present invention relates to process for producing hydroxylammonium salts by hydrogenating nitrogen monoxide in the presence of a platinum-containing catalyst catalyst. Hydroxylammonium salts are useful as important intermediates in the production of ε-caprolactam, and are also used in the synthesis of various oximes, antioxidants, dyeing auxiliaries, photographic chemicals, etc. The production of hydroxylammonium salts by the catalytic hydrogenation of nitrogen monoxide in the presence of a catalyst in an acidic medium such as sulfuric acid or the like is a well known process. As the catalyst, a platinum-containing catalyst supported on a carrier is used, however, it is recognized that the activity and selectivity of the catalyst are influenced greatly by the kind of reductant used for preparation of the Pt-containing catalyst. As methods for preparing catalysts for the production of hydroxylammonium salts, the followings are known: a) a method in which activated charcoal or graphite is used as the carrier and a reductant such as formic acid, formaldehyde or the like is added to an aqueous solution of platinum chloride, chloroplatinic acid or the like to deposit metallic platinum onto the carrier (U.S. Patent No. 2,628,899); b) a method which comprises reduction of a Pt(IV) salt to Pt(II) with a reductant selected from the group consisting of sodium dithionite, its hydrolyzate, a reaction product of sodium dithionite and formaldehyde, sulfurous acid and its salt in the presence of graphite or activated charcoal, followed by deposition of resultant Pt(II) onto the carrier in the form of metallic Pt by the use of formic acid, its sodium salt or its potassium salt (U.S. Patent No. 3,060,133); c) a method which comprises neutralizing or alkalizing a solution of platinum chloride or chloroplatinic acid in the presence of a carbonaceous substance, and reducing the platinum compound by the addition of a hydroxylammonium salt thereto (Japanese Patent Publication No. 44-8989); and d) a method based on the reduction of a Pt(IV) salt with hydrazine in the presence of an acid-resistant carrier (German Patent No. 2,551,314). However, all the above-mentioned prior methods are unsatisfactory in the selectivity regarding hydroxylammonium salts and in their yield, and necessitate complicated process for preparation of the catalyst. That is, when nitrogen monoxide is catalytically reduced with hydrogen in an acidic medium such as diluted sulfuric acid, the product obtained is not only hydroxylammonium sulfate, but ammonium sulfate and nitrous oxide are also formed as by-products. These by-products lower the selectivity regarding the hydroxylammonium salt and thereby bring about an economical disadvantage. In addition, the formation of ammonium sulfate is to be minimized because of its low commercial value. Further, since nitrous oxide constitutes an explosive mixture together with hydrogen and nitrogen monoxide, it is an important subject to improve the selectivity regarding hydroxylammonium salts from the viewpoint of safety, too. From US-A-4 024 079 there is known a catalyst which is prepared by firstly impregnating a catalyst carrier with a solution of a catalytically active metal compound and a sulfur compound and thereafter treating the impregnated carrier in a stream of high temperature steam. The said catalyst is used for treating exhaust gases produced by combustion of hydrocarbon fuels. EP-A-0 059 907 describes a process for the production of hydroxyl ammonium salts from nitrogen monoxide and hydrogen using a catalyst carrier bearing platinum; the preparation of the catalyst system itself is described in DE-B-1 088 037. Accordingly, it is an object of the present invention to provide a process for producing hydroxylammonium salts with high selectivity. The present invention provides a process for producing hydroxylammonium salts which comprises catalytic reductions of nitrogen monoxide with hydrogen in an acidic medium in the presence of a catalyst prepared by a reductive treatment of a platinum compound with a thiosulfate or a combination of a thiosulfate and an alkali metal sulfide Platinum compounds usable for preparation of the catalyst used in the present invention include platinum (II) chloride, platinum (IV) chloride, tetrachloroplatinous (II) acid and its salts, hexachloroplatinic (IV) acid and its salts, tetrammineplatinum (II) chloride, hexammineplatinum (IV) chloride, and the like. Among them, platinum chlorides and hexachloroplatinic (IV) acid are most widely used because of their availability. For the method of preparing catalyst used in the present invention, such conventional regeneration methods of platinum-containing catalysts as a method which comprises suspending a platinum-containing catalyst into aqua regia to dissolve metallic platinum, isolating the dissolved platinum and preparing a catalyst therefrom, and a method for regeneration of catalysts in the presence of a carrier are also successfully applicable. For thiosulfates used as the reductant sodium thiosulfate, potassium thiosulfate, barium thiosulfate, ammonium thiosulfate, ammonium sodium thiosulfate and the like are included. Among them, sodium thiosulfate is preferable because of its high selectivity. When the amount of thiosulfate used is expressed in terms of the ratio S/Pt in which S denotes amount of sulfur atom in the thiosulfate and Pt denotes amount of platinum atom in the platinum compound, S/Pt is in the range of 0.3 to 5, preferably 0.5 to 3. If the ratio is smaller than about 0.3, the reduction does not take place sufficiently and Pt cannot be utilized effectively as the catalyst component. If the ratio is greater than about 5, a large amount of S remains in the catalyst, causing decrease in the catalyst activity by formation of hydroxylammonium salts. As the alkali metal sulfide, sodium sulfide, potassium sulfide, lithium sulfide and the like are used. Among them, sodium sulfide is most preferable, because it has high selectivity regarding the hydroxylammonium salt formation and is readily available. When the amount of alkali metal sulfide used in the present invention is expressed in terms of the ratio S/Pt of sulfur atom S in the alkali metal sulfide to platinum atom Pt in the platinum compound, the S/Pt ratio is in the range of 0.05 to 1, preferably 0.1 to 0.8. If the ratio is smaller than 0.01, formation of ammonium salt increases. If it is greater than about 1, formation of nitrous oxide increases and the conversion of nitrogen monoxide decreases. The carrier such as graphite, activated charcoal, silica, alumina and the like which are conventionally used for supporting noble metals can be employed. Among them, graphite and activated characoal are preferable. The platinum-supporting rate of the catalyst is in the range of 0.01 to 10% by weight, preferably 0.1 to 5% by weight. If the ratio is smaller than about 0.01% by weight, the reaction activity per unit quantity of the catalyst decreases and the lifetime of catalyst tends to become shorter. If it is greater than about 10% by weight, the activity per unit quantity of catalyst reaches to the saturation and little effect is attainable in response to the increased ratio. The reduction of platinum compound is carried out in a state of suspension of carrier in a solution of the platinum compound. Thus, the reduction is carried out by suspending the carrier into the platinum compound solution, and adding under stirring the thiosulfate or a combination of the thiosulfate and the alkali metal sulfide. When a combination of the thiosulfate and the alkali metal sulfide is used, the two compounds may be added either simultaneously or separately and successively. The temperature of the reduction is 50°C to 150°C, and is preferably 80°C to 100°C. Although the time of reduction varies depending on kinds of the platinum compound, it is usually in the range of 0.5 hours to 10 hours. As a rough standard, the occasion when the supernatant has become colorless may be taken as the end point of the reduction. When pH of the platinum compound solution is previously adjusted to 1 to 11, preferably 2 to 7, the effect of the present invention is achieved more beneficially. Although the catalyst is capable of producing hydroxylammonium salts in high selectivity even employed as it is, it may be subjected to a finishing reductive treatment with a conventional reductant. As said reductant, hydrogen, alcohol, formic acid, hydrazine, sodium borohydride and the like can be mentioned. The method for preparing catalyst used in the present invention may be employed for a method for reducing the platinum compound in the presence of other metallic salt components hitherto proposed. As said other metallic salts, salts of metals such as gold, silver, iridium, mercury, lead, arsenic, antimony, bismuth, selenium, tellurium and the like can be mentioned. As salt forms of these metals, hydrochloride, nitrate, sulfate and the like can be employed. Although the amount of said salt is not critical, it is usually in the range of 0.001 to 0.2 as expressed in terms of the atomic ratio of the metal to platinum (British Patent No. 772,693, Japanese Patent Publication No. 39-20156). The reason why catalysts prepared in the abovementioned manner possess improved selectivity for the formation of hydroxylammonium salts is not well known. One of reasons, however, is estimated that the platinum compound reduced by the thiosulfate or the like tends to form particles of metallic platinum having extremely small particle diameters, i.e. so-called colloidal dispersion of platinum, which are adsorbed onto the carrier to give a catalyst carrying finely dispersed platinum particles. Further, it is also supposed that sulfur atoms remain partially in the final catalyst exercise a partial poisoning effect on the hydrogenation of nitrogen monoxide, which advance appropriately the hydrogenation of nitrogen monoxide and prevent both the formation of nitrouos oxide caused by insufficient progress of the hydrogenation as well as the formation of ammonia caused by excessive progress of the hydrogenation. The catalytic hydrogenation of nitrogen monoxide can be effected with known apparatus according to the known procedure. Good results are obtained when the hydrogenation is carried out by introducing nitrogen monoxide and hydrogen at nitrogen monoxide/hydrogen molar ratios of ranging from 1:1 to 1:6, preferably 1:1.5 to 1:5. The acid present when the reaction is carried out includes mineral acids such as hydrochloric acid, sulfuric acid, nitric acid and phosphoric acid. Preferably, the concentration of acid is in the range of 0.1 to 5 N as free acid. The reaction temperature is 30°C to 80°C, preferably 40°C to 60°C. The reaction is usually carried out under an atmospheric pressure, though an elevated pressure not exceeding 4 MPa is also applicable for the reaction. The amount of catalyst to be suspended into the acidic medium is 5 to 800 g, preferably 10 to 500 g, per liter of the medium. In carrying out the reaction of the present invention, an appropriate additive may be added to the above-mentioned reaction system as a third component in addition to the catalyst. As said additive, compounds of metals such as lead, mercury, arsenic, antimony, bismuth, selenium, tellurium and the like can be used (Ger. Patent Nos. 945,752 and 956,038). The reaction of the present invention may be carried out by a batch system using one or more reactors or by a continuous system, and the mode of reaction is not critical. The present invention will be illustrated more clearly with reference to Examples, however, the invention is by no means limited by the Examples. The conversion and selectivity referred to in the Examples and Comparative Examples are defined as follows: Example 1 Five grams of graphite, 0.067 g of hexachloroplatinic acid (H₂PtCl₆·6H₂O) and 20 ml of water were charged into a 200 ml flask, and the mixture was heated to 90°C. After replacing the inner atmosphere of the flask with argon gas, the mixture was stirred for 15 minutes. Then, a solution prepared by dissolving 0.032 g of sodium thiosulfate (Na₂S₂O₃·5H₂O) into 5 ml of water was slowly added. The resulting mixture was stirred at 90°C for one hour, and then filtered and washed to obtain a platinum catalyst. The platinum catalyst thus preapred and 300 ml of 4.3N sulfuric acid were charged into a 500 ml four-necked flask equipped with a gas inlet and a gas outlet. After heating the suspension of the catalyst to 45°C, argon gas was introduced into the suspension at a flow rate of 50 ml/minute for a period of 30 minutes. Then, a gaseous mixture having composition of NO : H₂ = 1 : 4 (by mole) was introduced into the suspension at a flow rate of 100 ml/minute to effect the reaction. The reaction temperature was 45°C. Eight hours after the start of reaction, the liquid reaction mixture and discharged gas were analyzed. As the result, it was found that NO conversion was 56.0%, (NH₃OH)₂SO₄ selectivity was 97.8%, (NH₄)₂SO₄ selectivity was 0.5%, and (N₂O + N₂) selectivity was 1.7%. The concentration of sulfuric acid in the reaction mixture was 3.5N. Example 2 Ten grams of graphite, 0.133 g of hexachloroplatinic acid (H₂PtCl₆·6H₂O) and 20 ml of water were charged into a 200 ml flask and heated to 90°C. After replacing the inner atmosphere of the flask with argon gas, the mixture was stirred for 15 minutes. A solution prepared by dissolving 0.049 g of sodium thiosulfate (Na₂S₂O₃·5H₂O) and 0.038 g of sodium sulfide (Na₂S·6H₂O) into 5 ml of water was slowly added. The resulting mixture was stirred at 90°C for one hour, and then filtered and washed to obtain a platinum catalyst. Five grams of the platinum catalyst thus prepared and 300 ml of 4.3N sulfuric acid were charged into a 500 ml four-necked flask equipped with a gas inlet and a gas outlet. After heating the catalyst suspension to 45°C, argon gas was introduced into the catalyst suspension at a flow rate of 50 ml/minute for a period of 30 minutes. Then, a gaseous mixture having composition of NO : H₂ = 1 : 4 (by mole) was introduced into the suspension at a flow rate of 100 ml/minute to effect the reaction. The reaction temperature was 45°C. Eight hours after the start of reaction, the reaction mixture and discharged gas were analyzed. As the result, it was found that NO conversion as 66.7%, (NH₃OH)₂SO₄ selectivity was 98.0%, (NH₄)₂SO₄ selectivity was 0.6%, and (N₂O + N₂) selectivity was 1.4%. The concentration of sulfuric acid in the reaction mixture was 3.4N. Examples 3 to 5 A catalyst was prepared and a reaction was carried out under the same conditions as in Example 1, except that the sodium thiosulfate was replaced with other thiosulfates mentioned in Table 1. After carrying out the reaction for 8 hours, the reaction mixture and discharged gas were analyzed. The results are shown in Table 1. Examples 6 to 9 The procedure of Example 2 was repeated, except that sodium thiosulfate and sodium sulfide were used in amounts mentioned in Table 2. The results are shown in Table 2. Example 10 Ten grams of graphite, 0.133 g of hexachloroplatinic acid (H₂PtCl₆·6H₂O) and 20 ml of water were charged into a 200 ml flask and heated to 90°C. After replacing the inner atmosphere of the flask with argon gas, the mixture was stirred for 15 minutes. A solution prepared by dissolving 0.029 g of sodium thiosulfate (Na₂S₂O₃·5H₂O) and 0.011 g of sodium sulfide (Na₂S·6H₂O) into 5 ml of water was slowly added and the resulting mixture was stirred at 90°C for one hour. Then, 1.75 ml of formic acid was added, and the whole mixture was stirred at 90°C for 3 hours, filtered and washed to obtain a platinum catalyst. A reaction was carried out under the same conditions as in Example 2, using 5 g of the platinum catalyst thus obtained. Eight hours after, the reaction mixture and discharged gas were analyzed. As the result, it was found that NO conversion was 72.4%, (NH₃OH)₂SO₄ selectivity as 98.3%, (NH₄)₂SO₄ selectivity was 0.5%, and (N₂O + N₂) selectivity was 1.2%. Examples 11 to 13 A catalyst was prepared and a reaction was carried out under the same conditions as in Example 2, except that the sodium thiosulfate or sodium sulfide was replaced with thiosulfates or alkali metal sulfides mentioned in Table 3. The results are shown in Table 3. Comparative Example 1 A catalyst was prepared according to the catalyst preparation method mentioned in U.S. Patent No. 3,060,133. Ten grams of graphite, 0.133 g of H₂PtCl₆·6H₂O, 14 ml of water and 0.88 ml of 36% hydrochloric acid were mixed together, and the mixture was heated to 80°C with stirring. The suspension thus obtained was neutralized with sodium carbonate until its pH value reached 3.7, and 0.376 g of sodium acetate (CH₃COONa·3H₂O) was added. Then, 2% (by weight) aqueous solution of sodium dithionite was added until Pt(IV) had become undetectable. Further, 0.61 ml of formic acid was added, and the resulting mixture was stirred at 80°C for 2 hours, filtered and washesd to obtain a platinum catalyst. A reaction was carried out under the same conditions as in Example 1, using 5 g of the platinum catalyst thus preapared. Eight hours after, the reaction mixture and the discharged gas were analyzed. As the result, it was found that NO conversion was 59.8%, (NH₃OH)₂SO₄ selectivity was 93.6%, (NH₄)₂SO₄ selectivity was 2.3%, and (N₂O + N₂) selectivity was 4.1%. The concentration of sulfuric acid in the reaction mixture was 3.5N. Comparative Examples 2 to 5 The procedure of Example 2 was repeated, except that sodium thiosulfate and sodium sulfide were used in amounts shown in Table 4. The results are shown in Table 4. Example Thiosulfates employed (g) NO conversion (%) (NH₃OH)₂SO₄ selectivity (%) (NH₄)₂SO₄ selectivity (%) N₂O+N₂ selectivity (%) Concentration of sulfuric acid in reaction mixture (N) 3 (NH₄)₂S₂O₃ 0.019 60.8 95.9 2.6 0.8 3.4 4 K₂S₂O₃ 0.025 66.0 96.4 1.4 2.2 3.4 5 BaS₂O₃·H₂O 0.034 63.8 97.2 1.3 1.4 3.4 Example Na₂S₂O₃·5H₂O (g) Na₂S·9H₂O (g) NO conversion (%) (NH₃OH)₂SO₄ selectivity (%) (NH₄)₂SO₄ selectivity (%) N₂O+N₂ selectivity (%) 6 0.061 0.038 63.1 97.3 0.6 2.1 7 0.029 0.038 69.8 97.8 1.3 0.9 8 0.049 0.043 58.9 96.9 0.2 2.9 9 0.049 0.018 69.4 97.9 1.4 0.7 Example Thiosulfate (g) Alkali metal sulfide (g) NO conversion (%) (NH₃OH)₂SO₄ selectivity (%) (NH₄)₂SO₄ selectivity (%) N₂O+N₂ selectivity (%) 11 K₂S₂O₃ 0.038 Na₂S·9H₂O 0.038 65.8 96.0 1.4 2.6 12 (NH₄)₂S₂O₃ 0.029 Na₂S·9H₂O 0.038 66.2 95.3 1.9 2.8 13 Na₂S₂O₃·5H₂O 0.049 K₂S 0.017 63.9 94.3 2.2 3.5 Comparative Example Na₂S₂O₃·5H₂O (g) Na₂S·9H₂O (g) NO conversion (%) (NH₃OH)₂SO₄ selectivity (%) (NH₄)₂SO₄ selectivity (%) N₂O+N₂ selectivity (%) 2 0.008 0.003 79.9 65.4 33.7 0.9 3 0.163 0.068 21.3 32.9 1.0 66.1 4 0.000 0.068 33.8 43.6 1.9 54.5 5 0.163 0.000 40.2 48.0 1.3 50.7

Claims: A process for producing a hydroxylammonium salt which comprises catalytically reducing nitrogen monoxide with hydrogen in an acidic medium in the presence of the catalyst prepared by subjecting a platinum compound to a reductive treatment with thiosulfate or thiosulfate combined with alkali metal sulfide in the presence of a catalyst carrier. The process for producing a hydroxylammonium salt according to Claim 1, wherein the molar ratio of hydrogen to nitrogen monoxide is 1 to 6. The process for producing a hydroxylammonium salt according to Claim 1, wherein said acidic medium is a mineral acid having concentration of 0.1N to 5N. The process for producing a hydroxylammonium salt according to Claim 1, wherein the temperature of catalytic reduction is 30°C to 80°C. The process for producing a hydroxylammonium salt according to Claim 1, wherein said carrier is graphite, activated charcoal, silica or alumina. The process for producing a hydroxylammonium salt according to Claim 1, wherein said platinum compound is selected from the group consisting of platinum (II) chloride, platinum (IV) chloride, tetrachloroplatinous (II) acid, hexachloroplatinic (IV) acid, salts of these acids, tetrammineplatinum (II) chloride and hexammineplatinum (IV) chloride. The process for producing a hydroxylammonium salt according to Claim 1, wherein the amount of platinum supported on the carrier is 0.01 to 10% by weight. The process for producing a hydroxylammonium salt according to Claim 1, wherein said thiosulfate is sodium thiosulfate, potassium thiosulfate, barium thiosulfate, ammonium thiosulfate or ammonium sodium thiosulfate. The process for producing a hydroxylammonium salt according to Claim 1, wherein the amount of thiosulfate used in the reductive treatment is 0.3 to 5 as expressed in terms of ratio S/Pt, wherein S is the amount of sulfur atom in the thiosulfate and Pt is the amount of platinum atom in the platinum compound. The process for producing a hydroxylammonium salt according to claim 1, wherein said alkali metal sulfide is sodium sulfide, potassium sulfide or lithium sulfide. The process for producing a hydroxylammonium salt according to Claim 1, wherein the amount of alkali metal sulfide used in the reductive treatment is 0.05 to 1 as expressed in terms of ratio S/Pt, wherein S is the amount of sulfur atom in the alkali metal sulfide and Pt is the amount of platinum atom in the platinum compound. The process for producing a hydroxylammonium salt according to Claim 1, wherein temperature of the reductive treatment is 50°C to 150°C, and time of the reductive treatment is 0.5 hours to 10 hours. The process for producing a hydroxylammonium salt according to Claim 1, wherein the reductive treatment of a platinum compound by thiosulfate or thiosulfate combined with alkali metal sulfide is further followed by the reductive treatment with formic acid, hydrogen, alcohol, hydrazine or sodium borohydride.

Inventors: ICHIHASHI, HIROSHI, TAKEDA, KIKUO, YOSHIOKA, HIROSHI
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1988
Main classification: B01J23
IPC codes: C01B21, C01C1, B01J23, B01J27