SILVER HALIDE EMULSION AND PHOTOGRAPHIC LIGHT-SENSITIVE MATERIAL USING THE SAME

Abstract: A silver halide emulsion comprises a dispersion medium and silver halide grains, the silver halide emulsion containing tabular silver halide grains having a thickness of less than 0.5 µm, a diameter of 0.3 µm or more, and a mean diameter-to-thickness ratio of 2 or more. The tabular grains occupy at least 50% of a pro­ jected area of all the silver halide grains, and 50% or more (number) of the tabular grains include 10 or more dislocations per grain. A photographic light-sensitive material comprises the aforementioned silver halide emulsion.

Description: The present invention relates to a silver halide emulsion and a photographic light-sensitive material having improved photographic characteristics and storage properties. Methods of forming and techniques of utilizing tabular silver halide grains are already disclosed in, for example, U.S. Patents 4,434,226, 4,439,520, 4,414,310, 4,433,048, 4,414,306, and 4,459,353 and Japanese Patent Application (OPI) Nos. 59-99433 and 62-209445. Tabular silver halide grains have advantages such as improvements in sensitivity including an improvement in spectral sensitization efficiency obtained by a sensitizing dye, an improvement in a sensitivity/graininess relationship, an improvement in sharpness obtained by unique characteristics of the tabular grains, an improvement in covering power. However, a strong demand has arisen for a more advantageous photographic silver halide emulsion. That is, in addition to photographic characteristics such as sensitivity, and image quality such as graininess and sharpness, a higher level demand has arisen for so-called toughness such as an exposure intensity dependency, storage stability, and resistance to pressure. Conventional silver halide grains do not completely satisfy the above demand. Japanese Patent Application (OPI) No. 59-99433 discloses a technique for improving resistance to pressure of a light-sensitive material containing tabular silver halide grains having a grain diameter/thickness ratio of 5 or more. However, in this technique, exposure intensity dependency and storage stability of photographic characteristics cannot be completely improved. This invention relates to a technique for controlling formation of dislocations in tabular silver halide grains. Dislocations of the silver halide grains are described in, for example, 1 ○ C.R. Berry, J.Appl. Phys., 27, 636 (1956), 2 ○ C.R. Berry, D.C. Skillman, J.Appl. Phys., 35, 2165 (1964), 3 ○ J.F. Hamilton, Phot. Sci. Eng., 11, 57, (1967), 4 ○ T. Shiozawa, J. Soc. Phot. Sci Japan, 34, 16, (1971), and 5 ○ T. Shiozawa, J. Soc. Phot. Sci Japan, 35, 213 (1972). 1 ○ to 4 ○ describe that dislocations in grains can be observed by an X-ray diffraction method or can be observed directly by a transmission electron microscope at a low temperature and that a variety of dislocations can be generated in grains by intentionally applying stress to the grains. However, 1 ○ to 4 ○ do not describe that the technique for controlling formation of dislocations in tabular silver halide grains during a formation process of the grains is important to toughness as described above. 5 ○ describes that dislocations can be observed in most of unsensitized tabular silver halide grains having a composition AgBrI (I = 1 mol%) and a grain diameter/thickness ratio of 75 by a transmission electron microscope at a low temperature. However, 5 ○ only describes the observation of the individual grains but does not refer to the relationship between dislocation and the photographic characteristics at all. That is, overall photographic characteristics, of the grains, as an emulsion containing a large number of tabular silver halide grains having dislocations, are not examined at all. It is, therefore, the object of the present invention to provide a silver halide emulsion having a high sensitivity, good graininess, sharpness, and resistance to pressure and improved exposure intensity dependency and storage stability, and a photographic light-sensitive material using the same. Said object is achieved by: (1) A silver halide emulsion comprising a dispersion medium and silver halide grains, the silver halide emulsion containing tabular silver halide grains having a thickness of 0.5 µm or less, a diameter of 0.3 µm or more, and a mean diameter-to-thickness ratio of 2 or more, characterized in that said tabular grains occupy at least 50% of a projected area of all the silver halide grains, and 50% (number) or more of said tabular grains include 10 or more dislocations per grain and said tabular grains have an inner region portion having a higher silver iodide content than the surface region of the tabular grains (2) A photographic light-sensitive material comprising a support having thereon at least one silver halide emulsion layer containing a silver halide emulsion comprising a dispersion medium and silver halide grains, the silver halide emulsion containing tabular silver halide grains having a thickness of 0.5 µm or less, a diameter of 0.3 µm or more and a mean diameter-to-thickness ratio of 2 or more, characterized in that said tabular grains occupy at least 50% of a projected area of all the silver halide grains, and 50% (number) or more of said tabular grains include 10 or more dislocations per grain and said tabular grains have an inner region portion having a higher silver iodide content than the surface region of the tabular grains. Tabular silver halide grains (to be referred to as "tabular grains") have two opposing parallel major faces whose diameter (diameter of a circle having the same area as the projected area of the major faces) is twice or more the distance (i.e., the thickness of a grain) between the major faces. The mean grain diameter/thickness ratio of the tabular grains used in the emulsion of this invention is preferably 3 to 12, and more preferably, 5 to 10. The mean grain diameter/thickness ratio can be obtained by averaging the grain diameter/thickness ratios of all tabular grains. However, this can be obtained more easily as the ratio of the mean diameter to the mean thickness of all tabular grains. The diameter of the tabular grains used in this invention (diameter of the circle having the same area as the projected area of the tabular grains) is 0,3 µm or more, suitably 0,3 to 10 µm, preferably 0,05 to 0,5 µm, and more preferably 0,5 to 2,0 µm. The grain thickness is 0,5 µm or less, preferably 0,05 to 0,5 µm, and more preferably 0,08 to 0,3 µm. The diameter and thickness of the grains used in this invention can be measured by an electron microscopic photograph of grains as described in U.S. Patent 4.434,226. The halide composition of the tabular grains is preferably silver iodobromide or silver iodochlorobromide, and more preferably, silver iodobromide having a silver iodide content of 0,1 to 20 mol%, preferably 1 to 10 mol%. The dislocations of the tabular grains can be observed directly by a transmission electron microscope at a low temperature as described in J.F. Hamilton, Phot. Sci. Eng., , 57, (1967) and T. Shiozawa, J. Soc. Phot. Sci Japan, , 213, (1972). That is, a silver halide grain carefully picked up from an emulsion so that a pressure capable of generating dislocations in the grain is not applied thereto is placed on a mesh for electron microscopic observation. Then, the sample is cooled to prevent damage (e.g., print out) by the electron beam and observed by a transmission method. Since it is difficult for a thick grain to transmit the electron beam, the grain can be observed more clearly by an electron microscope of a high voltage type (200 kV or more with respect to a grain having a thickness of 0.25 µm). Using photographs of grains obtained in this manner, the positions and number of dislocations of each grain, viewed from a direction perpendicular to the major face, can be determined. The dislocations of the tabular grains used in this invention are generated in a major axis direction of the tabular grains from a position away from the center by a distance which is x% of the length between the center and an edge, to the edge. The value of x is preferably 10 ≦ x < 100, more preferably 30 ≦ x < 98, and most preferably 50 ≦ x < 95. At this time, a shape obtained by connecting the positions at which dislocations start is close to a similar figure of the grain but is not always a complete similar figure, i.e., distorted. The dislocation lines extend substantially from the center to the edge but sometimes extend in a zig-zag manner. Grains including 10 or more dislocations exist in all tabular grains in a percentage ratio of 50% (number) or more of all tabular grains. More specifically, grains including 10 or more dislocations preferably exist in a percentage ratio of 80% (number) or more, and more specifically, grains including 20 or more dislocations preferably exist in a percentage ratio of 80% (number) or more. The structure of the halide composition of the tabular grains can be checked using for example a combination of X-ray diffraction, an EPMA (also called XMA) method (of scanning silver halide grains by an electron beam to detect the silver halide composition) or an ESCA (also called XPS) method (of radiating X-rays to perform spectral analysis of photoelectrons emitted from the surface of grains). The surface region of the grains is a region extending from the surface to a depth of about 5 nm (50 Å.). The halide composition of such a region can be measured by the ESCA method. The inner region of the grains is the region other than the above surface region. A method for preparing tabular grains will be described below. The tabular grains can be formed using a proper combination of methods known to those skilled in the art. For example, a seed crystal in which tabular grains exist in an amount of 40 wt% is formed in an atmosphere having a relatively high pAg value with a pBr of 1.3 or less. Then, a solution of silver ions and a solution of halide ions is added to the seed crystal while maintaining the above pBr value or more to grow the seed crystal, thereby forming tabular grains. In a grain growth process performed by adding silver and/or a halide, preferably the solution of silver and the solution of the halide are carefully added to the seed crystal so that a new crystal nucleus is not generated. The size of the tabular grains can be adjusted by controlling the temperature, selecting the type and the amount of a solvent, and controlling addition speed of the silver salt and the halide used in the grain growth process. The dislocations in the tabular grains can be controlled by providing specific iodide rich phases in the internal portion of the grains. More specifically, substrate grains are prepared, iodide rich phases are formed by method 1 ○ or 2 ○ to be described below, and the iodide rich phases are covered with phases having an iodide content lower than that of the iodide rich phases, thereby obtaining dislocations. The iodide content of the tabular substrate grains is lower than that of the rich iodide phases, preferably 0 to 12 mol%, and more preferably 0 to 10 mol%. Internal iodide rich phases mean a silver halide solid solution containing iodide. In this case, silver iodide, silver iodobromide, or silver iodochlorobromide is preferred as the silver halide. Silver iodide or silver iodobromide (iodide content: 10 to 40 mol%) is more preferable, and silver iodide is especially preferable. It is Important that the internal iodide rich phases are deposited not uniformly but locally on faces of the substrate grains. Such a localization may be performed on any of a major face, a side face, an edge, and a corner. In addition, this localization may be selectively epitaxially coordinated in the above portions. 1 ○ For this purpose, a so-called conversion method described in E. Klein, E. Moisar, G. Murch, Phot. Korr., , (4), 59 to 63, (1966) may be used. In this method, during the grain formation process, halide ions having a lower silver salt solubility than that of silver halide which form a grain (or a portion close to the surface of the grain) at this time are added. The amount of halide ions having a lower silver salt solubility to be added is preferably larger than the value (associated with the halide composition) with respect to the surface area of the grain at this time. For example, during grain formation, KI is preferably added in an amount larger than a certain value with respect to the surface area of the AgBr grain at this time. More specifically, KI is preferably added in an amount of 8.2 × 10⁻⁵ mol/m² or more. 2 ○ In addition, an epitaxial junction method as described in, for example, Japanese Patent Application (OPI) Nos. 59-133540, 58-108526, and 59-162540 can be used. In this method, site directors of epitaxial growth such as an absorptive spectral sensitizing dye can be used. By adding the site directors or by selecting conditions (e.g., a pAg, pH, and temperature) for crystal growth and adding a solution of a silver salt and a solution of a halide solution containing iodide ions, the internal iodide rich phases are formed. In order to practice the above two methods, the solubility of the silver halide in a mixture system is preferably as low as possible. This is because the solubility in the system affects the distribution of the iodide rich phases on the surface (if the solubility is high, the phases tend to be uniformly distributed). When the internal iodide rich phases are to be formed, the pAg of the mixture system preferably falls within the range of 6.4 to 10.5, and more preferably 7.1 to 10.2. The external phases covering the iodide rich phases have an iodide content lower than that of the iodide rich phases. More specifically, the iodide content of the external phases is preferably 0 to 12 mol%, more preferably 0 to 10 mol%, and most preferably 0 to 3 mol%. The internal iodide rich phases preferably exist in the major axis direction of the tabular grains within the range of 5 to 80 mol% preferably 10 to 70 mol%, and more preferably, 20 to 60 mol% in terms of the silver content of the entire grains. In this case, the major axis direction of the grain means the diameter direction of the tabular grains, and the minor axis direction means the thickness direction thereof. The iodide content of the internal iodide rich phases is higher than the mean iodide content of silver bromide, silver iodobromide, or silver iodochlorobromide present on the grain surface. The iodide content of the internal iodide rich phases is preferably 5 times or more, and more preferably 20 times or more of the mean iodide content of the grain surface. The content of the silver halide which forms the internal iodide rich phases is 50 mol% or less, preferably 10 mol% or less, and more preferably, 5 mol% or less in terms of the silver content of the entire grains. The following mono-dispersion hexagonal tabular grains can be used. This emulsion is a silver halide emulsion consisting of a dispersion medium and silver halide grains. In this emulsion, 70% or more of the entire projected area of the silver halide grains is occupied by tabular silver halide grains which are hexagons in which the ratio of the length of an edge having a maximum length to the length of an edge having a minimum length is 2 or less and which have two parallel faces as outer surfaces. This emulsion is a mono-dispersion emulsion, i.e., the variation coefficient of the grain size distribution of the hexagonal tabular silver halide grains is 20% or less. The variation coefficient is a value obtained by dividing the variation (standard deviation) of the grain size, which is represented by the diameter of a circle having the same area as the projected area of the grains, by the average grain size. The aspect ratio is 2.5 or more, and the grain size is 0.2 µm or more. The composition of the hexagonal tabular grains may be any of silver bromide, silver iodobromide, silver chlorobromide, and silver iodochlorobromide. If iodide ions are contained, its content is 0 to 30 mol%. The crystal structure may be any of a uniform structure, a structure whose inner portion consists of a halide composition different from that of the outer portion, and a layer structure. A reduction sensitized silver nucleus is preferably contained in the grains. The silver halide grains can be manufactured through nucleus formation, Ostwald ripening, and grain growth. During manufacture of the tabular grains a method of increasing the addition speed, the addition amount, and the addition concentration of the salt of silver solution (e.g., an aqueous AgNO₃ solution) and the halide solution (e.g., an aqueous KBr solution) to be added to accelerate grain growth is preferably used. Examples of this method are described in British Patent 1,335,925, U.S. Patents 3,672,900, 3,650,757, and 4,242,445, and Japanese Patent Application (OPI) Nos. 55-142329 and 55-158124. A solvent for silver halide is effective to promote ripening. For example, in order to promote ripening, an excessive amount of halide ions is supplied into a reaction vessel. Therefore, it is obvious that ripening can be promoted by only supplying a solution of a salt of halide into the reaction vessel. Other ripening agents may also be used. These ripening agents may be entirely mixed in the dispersion medium in the reaction vessel before the salt of silver and the salt of halide are added or may be supplied into the reaction vessel together with 1 or more salts of halides, salts of silver, or deflocculating agents. As another modification, the ripening agents may be independently supplied when the salt of a halide and the salt of silver are added. Examples of the ripening agent other than halide ions are ammonia, an amine compound, a thiocyanate such as an alkaline metal thiocyanate, especially sodium or potassium thiocyanate, and ammonium thiocyanate. Methods of using a thiocyanate ripening agent are described in U.S. Patents 2,222,264, 2,448,534, and 3,320,069. A conventional thioether ripening agent can be used as described in U.S. Patents 3,271,157, 3,574,628, and 3,737,313. A thionic compound as disclosed in Japanese Patent Application (OPI) Nos. 53-82408 and 53-144319 can also be used. By supplying a variety of compounds during the process of forming the silver halide precipitation, the characteristics of the silver halide grains can be controlled. Such compounds may be initially supplied in the reaction vessel or may be added together with 1 or more salts in accordance with a conventional method. As described in U.S. Patents 2,448,060, 2,628,167, 3,737,313, and 3,772,031 and Research Disclosure, Vol. 134, No. 13452 (June 1975), compounds of copper, iridium, lead, bismuth, cadmium, zinc, (a chalcogenide of sulfur, selenium or tellurium, and compounds of gold, and noble metals of Group VII may be supplied during the process of forming the silver halide precipitation to control the characteristics of the silver halide. As described in Japanese Patent Publication No. 58-1410 and Moisar et al., Journal of Photographic Science, Vol. 25, 19-27 (1977), the interiors of the grains of the silver halide emulsion can be subjected to reduction sensitization in the process of forming the precipitation. In the tabular grains used in this invention, silver halides having different compositions may be bonded to each other by an epitaxial junction or a silver halide may be bonded to a compound other than silver halides, such as silver rhodanide or lead oxide. These emulsion grains are disclosed in, for example, U.S. Patents 4,094,684, 4,142,900, and 4,459,353, British Patent 2,038,792, U.S. Patents 4,349,622, 4,395,478, 4,433,501, 4,463,087, 3,656,962, and 3,852,067, and Japanese Patent Application (OPI) No. 59-162540. Normally, the tabular grains used in this invention are chemically sensitized. As described in T.H. James, The Theory of the Photographic Process, 4th ed., Macmillan (1977), 67-76, chemical sensitization can be performed by using active gelatin. Chemical sensitization can also be performed by using sulfur, selenium, tellurium, gold, platinum, palladium, and iridium or a combination of a plurality of these sensitizing agents in an atmosphere in which the pAg is 5 to 10, the pH is 5 to 8 and the temperature is 30 to 80°C as described in Research Disclosure, Vol. 120, No. 12008 (Apr. 1974); Research Disclosure, Vol. 34, No. 13452 (June 1975), U.S. Patents 2,642,361, 3,297,446, 3,772,031, 3,857,711, 3,901,714, 4,266,018, and 3,904,415, and British Patent 1,315,755. The chemical sensitization is optimally performed in the presence of gold and thiocyanate compounds, or in the presence of sulfur-containing compounds described in U.S. Patents 3,857,711, 4,266,018, and 4,054,457 or a sulfur-containing compound such as hypo, a thiourea series compound, or a rhodanic series compound. The chemical sensitization can also be performed in the presence of a chemical sensitizing aid. An example of a chemical sensitizing aid is a compound such as azaindene, azapyridazine, or azapyrimidine which is known to reduce fog and to increase sensitivity in a chemical sensitizing process. Examples of chemical sensitization modifiers are described in U.S. Patents 2,131,038, 3,411,914, and 3,554,757, Japanese Patent Application (OPI) No. 58-126526, and G.F. Duffin, Photographic Emulsion Chemistry, 138-143. In addition to or in place of chemical sensitization, reduction sensitization can be performed using hydrogen as described in U.S. Patents 3,891,446 and 3,984,249, using stannous chloride, thiourea dioxide, polyamine and a reducing agent as described in U.S. Patents 2,518,698, 2,743,182, and 2,743,183, or by a low pAg (e.g., less than 5) and/or high pH (e.g., more than 8) treatment. The spectral sensitization can be improved by the chemical sensitization methods described in U.S. Patents 3,917,485 and 3,966,476. Furthermore, a sensitization method using an oxidizing agent described in Japanese Patent Application (OPI) No. 61-3134 or 61-3136 can also be used. The emulsion containing tabular grains can be used together with an emulsion containing silver halide grains (to be referred to as non-tabular grains hereinafter) which are subjected to normal chemical sensitization, in a single silver halide emulsion layer. Especially in a color photographic light-sensitive material, the tabular grain and non-tabular grain emulsions can be used in different emulsion layers and/or the same emulsion layer. Examples of non-tabular grains are regular grains having a regular crystal form such as a cube, octahedron, tetradecahedron, and an irregular crystal form such as a sphere or potato-like. Silver bromide, silver iodobromide, silver iodochlorobromide, silver chlorobromide, or silver chloride can be used as silver halide in the non-tabular grains. The preferred silver halide is silver iodobromide or silver iodochlorobromide containing at most about 30 mol% of silver iodide. A particularly preferred silver halide is silver iodobromide containing about 2% to about 25% of silver iodide. The non-tabular grains may be fine grains having grain sizes (diameters) of not more than about 0.1 µm. They may be large grains as long as the diameter of their projected areas does not exceed 10 µm. Also, the silver halide emulsion for of this invention may be a mono-dispersed silver halide emulsion having a narrow grain size distribution or a poly-dispersed silver halide emulsion having a broad grain distibution. The non-tabular grains for use in this invention can be prepared using the methods described, for example, in P. Glafkides, Chimie et Physique Photographique Paul Montel, published by Paul Montel, 1967; G.F. Duffin, Photographic Emulsion Chemistry, published by Focal Press, 1966; and V.L. Zelikman et al., Making and Coating Photographic Emulsion, published by Focal Press, 1964. That is, the photographic emulsion may be prepared by an acid method, a neutralization method or an ammonia method. Also, as a system for reacting a soluble silver salt and a soluble halide, a single jet method, a double jet method, or a combination thereof may be used. Also, a so-called back mixing method for forming silver halide grains in the existence of excessive silver ions can be used. As one system of the double jet method, a so-called controlled double jet method wherein the pAg in the liquid phase of forming the silver halide is kept at a constant value can be used. According to this method, a silver halide emulsion having a regular crystal form and almost uniform grain sizes is obtained. Two or more kinds of silver halide emulsions separately prepared can be used as a mixture thereof. The silver halide emulsion containing the above-described regular silver halide grains can be obtained by controlling the pAg and pH during the formation of the silver halide grains. More particularly, such a method is described in Photographic Science and Engineering, Vol. 6, 159-165 (1962); Journal of Photographic Science, Vol. 12, 242-251 (1964); U.S. Patent 3,655,394, and British Patent 1,413,748. Mono-dispersed emulsions are described in Japanese Patent Application (OPI) Nos. 48-8600, 51-39027, 51-83097, 53-137133, 54-48521, 54-99419, 58-37635, and 58-49938, Japanese Patent Publication No. 47-11386, U.S. Patent No. 3,655,394, and British Patent No.1,413,748. As to the crystal structure of the silver halide for use in this invention, the non-tabular grains may be uniform, may have a different halide composition between the inside and the outside thereof, or may have a layer structure. These emulsion grains are disclosed in British Patent 1,027,146, U.S. Patents 3,505,068 and 4,444,877, and Japanese Patent Application (OPI) No. 58-248469. In this invention, a non-light-sensitive fine grain emulsion containing grains having a grain size of at most 0.6 µm, and preferably at most 0.2 µm may be added to a silver halide emulsion layer, an interlayer, or a protective layer for the purpose of promoting development, improving storage stability or effectively utilizing reflected light. The tabular grains are preferably used in a color light-sensitive material for photographing. When the tabular grain emulsion of this invention is used together with, especially, a non-tabular monodispersed silver halide grain emulsion in a single emulsion layer and/or different emulsion layers, sharpness and graininess can be improved at the same time. In this case, the mono-dispersed silver halide emulsion (non-tabular grains) is defined such that 95% or more of the total weight or the total number of silver halide grains contained in the emulsion have grain sizes falling within the range of ± 40%, and preferably, ± 30% of the mean grain size. As described in Japanese Patent Publication No. 47-11386, Japanese Patent Application (OPI) Nos. 55-142329, 57-17235, and 59-72440, the graininess can be improved by using a mono-dispersed silver halide emulsion in the silver halide photographic light-sensitive material. As described in T.H. James, The Theory of the Photographic Process, 580-585, mono-dispersed silver halide grains having sizes of 0.3 to 0.8 µm have a high light scattering property with respect to light of a specific wavelength range but have a relatively low light scattering property with respect to light of other wavelength ranges. Therefore, when the tabular silver halide emulsion having a grain diameter/thickness ratio of 2 or more and the mono-dispersed silver halide emulsion are properly arranged in consideration of the optical characteristics and graininess of both emulsions, sharpness and graininess of the silver halide photographic light-sensitive material can be improved at the same time. Some examples of a light-sensitive material using tabular and mono-dispersed silver halide emulsions will be described below. Example 1): In a light-sensitive material in which red-sensitive, green-sensitive, and blue-sensitive layers are arranged in the order named from a support, if the mean grain size of silver halide grains contained in the silver halide emulsion layer constituting the blue-sensitive layer falls within the range of 0.3 to 0.8 µm, the tabular grain emulsion is used as the emulsion layer, and if the mean grain diameter does not fall within the above range, the mono-dispersed silver halide emulsion is used. As a result, the sharpness of the green- and red-sensitive layers and the graininess of the blue-sensitive layer can be improved. Example 2); In a light-sensitive material having a layer arrangement similar to that of Example 1, if the mean grain size of silver halide grains contained in the silver halide emulsion layer constituting the green-sensitive layer falls within the range of 0.4 to 0.8 µm, the tabular grain emulsion is used as the emulsion layer, and if the mean grain size does not fall within the above range, the mono-dispersed emulsion is used. As a result, the sharpness of the red-sensitive layer and the graininess of the green-sensitive layer can be improved at the same time. Example 3); In a light-sensitive material having a layer arrangement similar to that of Example 1 in which the emulsion layers having the same color sensitivity consist of two or more layers having different sensitivities or speeds, if silver halide grains contained in the blue-sensitive layer having the highest sensitivity are mono-dispersed silver halide grains (preferably, double structure grains) having a mean grain size of 1.0 µm or more and light scattering of a blue-sensitive layer having lower sensitivity is large, the tabular grain emulsion is used as the blue-sensitive layer having the lower sensitivity. As a result, the sharpness of the green- and red-sensitive layers can be improved. Example 4); In a light-sensitive material having a layer arrangement similar to that of Example 3, if all of the plurality of green-sensitive layers have large light scattering, the tabular grain emulsion is used as all the green-sensitive layers. As a result, the sharpness of the red-sensitive layers and the graininess of the green-sensitive layers can be improved at the same time. As in Examples 3 and 4, when each of the blue-, green-, and red-sensitive layers consists of a plurality of emulsion layers, the tabular grain emulsion should be used as emulsion layer having large light scattering and the mono-dispersed emulsion must be used as those having small light scattering so as to improve the sharpness and graininess. When the tabular grain emulsion is also used in the red-sensitive layers in Example 4), light scattering between the emulsion layers is sometimes increased to degrade the sharpness of the green-sensitive layers on the red-sensitive layers. That is, it is not always preferable to use the tabular grain emulsion as the red-sensitive layer closest to the support. As described above, the tabular and non-tabular grain emulsions for use in this invention are usually subjected to physical ripening, chemical ripening, and spectral sensitization. Additives which are used in such steps are described in Research Disclosures, RD No. 17643 (Dec. 1978) and RD No. 18716 (Nov. 1979) and they are summarized in the following table. In this case, a spectral sensitizing dye may be added before the chemical sensitization starts. In addition, a plurality of sensitizing dyes of 500 nm or less may be used at the same time. Also, photographic additives which can be used in this invention are described in the above-described two Research Disclosures publications and they are also summarized in the same table. Additives RD No.17643 RD No.18716 1. Chemical sensitizers page 23 page 648, right column 2. Sensitivity increasing agents page 648, right column 3. Spectral sensitizers, super sensitizers pages 23-24 page 648, right column to page 649, right column 4. Brighteners page 24 5. Antifoggants and stabilizers pages 24-25 page 649, right column 6. Light absorbent, filter dye, ultraviolet absorbents pages 25-26 page 649, right column to page 650, left column 7. Stain preventing agents page 25, right column page 650, left to right columns 8. Dye image stabilizers page 25 9. Hardening agents column page 26 page 651, left 10. Binder page 26 do 11. Plasticizers, lubricants page 27 page 650, right column 12. Coating aids, surface active agents pages 26-27 pages 26-27 do do 13. Antistatic agents page 27 do Various color couplers can be used in the light-sensitive material. Specific examples of these couplers are described in the above-described Research Disclosure, No. 17643, VII-C to VII-G as patent references. As dye-forming couplers, couplers giving three primary colors (i.e., yellow, magenta, and cyan) by a subtraction color process by color development are typically important, and specific examples of non-diffusible couplers, four-equivalent couplers, and two-equivalent couplers are described in Patents referred in the above-described Research Disclosure, No. 17643, VII-C and VII-D and further the following couplers can also preferably be used in this invention. Typical yellow couplers which can be used in the light-sensitive material of this invention include hydrophobic acetylacetamide series couplers having a ballast group. Specific examples of the yellow coupler are described in U.S. Patents 2,407,210, 2,875,057, The use of two-and 3,265,506. equivalent yellow couplers is preferred. Typical examples thereof are oxygen atom-releasing type yellow couplers described in U.S. Patents 3,408,194, 3,447,928, 3,933,501, and 4,022,620 and nitrogen atom-releasing type yellow couplers described in Japanese Patent Publication 10,739/83, U.S. Patents 4,401,752, 4,326,024, Research Disclosure, No. 18053 (April, 1979), British Patent 1,425,020, West German Patent Application (OLS) Nos. 2,219,917, 2,261,361, 2,329,587, and 2,433,812. Furthermore, α-pivaloylacetanilide series couplers are excellent in fastness, in particular light fastness of the colored dye. On the other hand, α-benzoylacetanilide series couplers show a high coloring density. Typical magenta couplers which can be used in the light-sensitive material of this invention include hydrophobic indazolone type or cyanoacetyl series, preferably 5-pyrazolone type and pyrazoloazole series couplers each having a ballast group. The 5-pyrazolone series couplers the 3-position of which is substituted by an arylamino group or an acylamino group are preferred in the view of the hue and coloring density of the colored dye. Specific examples of such couplers are described in, for example, U.S. Patents 2,311,082, 2,343,703, 2,600,788, 2,908,573, 3,062,653, 3,152,896, and 3,936,015. As the releasable group of a two-equivalent 5-pyrazolone type coupler, the nitrogen atom releasing group described in U.S. Patent 4,310,619 and the arylthio group described in U.S. Patent 4,351,897 are particularly preferred. Also, the 5-pyrazolone type couplers having a ballast group described in European Patent No. 73,636 give high coloring density. As the pyrazoloazole type magenta couplers, there are the pyrazolobenzimidazoles described in U.S. Patent 3,061,432, preferably the pyrazolo[5,1-c] [1,2,4]triazoles described in U.S. Patent 3,725,067, the pyrazolotetrazoles described in Research Disclosure, RD No. 24220 (June, 1984) and Japanese Patent Application (OPI) No. 33,552/85, and the pyrazolopyrazoles described in Research Disclosure, RD No. 24230 (June, 1984) and Japanese Patent Application (OPI) No. 43,659/85. With respect to the points of showing less side yellow absorption and light fastness of the colored dye, the imidazo[1,2-b]pyrazoles described in U.S. Patent 4,500,630 are preferred and the pyrazolo[1,5-b][1,2,4] triazoles described in European Patent 119,860A are particularly preferred. Typical cyan couplers which can be used in the light-sensitive material of this invention include hydrophobic and non-diffusible naphtholic and phenolic couplers. Typical examples of the cyan couplers are the naphtholic couplers described in U.S. Patent 2,474,293 and preferably the oxygen atom releasing type two-equivalent naphtholic couplers described in, for example, U.S. Patents 4,052,212, 4,146,396, 4,228,233, and 4,296,200. Also, specific examples of the phenolic couplers are described in U.S. Patents 2,369,929, 2,801,171, 2,772,162, and 2,895,826. Cyan couplers which form dyes having fastness to humidity and temperature are preferably used in this invention and specific examples of such cyan couplers are phenolic cyan couplers having an alkyl group of at least 2 carbon atoms at the metaposition of the phenol nucleus described in U.S. Patent 3,772,002, the 2,5-diacylamino-substituted phenolic couplers described in U.S. Patents 2,772,162, 3,758,308, 4,126,396, 4,334,011, and 4,327,173, West German Patent Application (OLS) No. 3,329,720, and European Patent No. 121,365, and the phenolic couplers having a phenylureido group at the 2-position thereof and an acylamino group at the 5-position thereof described in U.S. Patents 3,446,622, 4,333,999, 4,451,559, and 4,427,767. A naphtholic cyan coupler in which for example, a sulfonamido group or an amide group, is substituted at the 5-position described in European Patent No. 161,626A has excellent fastness of the colored image and hence can be preferably used in this invention. For correcting an additional, undesirable absorption of the colored dye, it is preferred to perform color masking by using colored couplers together in the case of color photographic materials for in-camera use. Specific examples of these colored couplers are yellow-colored magenta couplers described in U.S. Patent 4,163,670 and Japanese Patent Publication No. 39,413/82, and magenta-colored cyan couplers described in U.S. Patents 4,004,929, 4,138,258 and British Patent 1,146,368. Other colored couplers which can be used in this invention are described in the above-described Research Disclosure, RD No. 17643, VII-G. The graininess can be improved by using couplers capable of forming colored dyes having a proper diffusibility. As such couplers, specific examples of magenta couplers are described in U.S. Patent 4,366,237 and British Patent 2,125,570 and specific examples of yellow couplers, magenta couplers and cyan couplers are described in European patent 96,570 and West German Patent Application (OLS) No. 3,234,533. The dye-forming couplers and the above-described specific couplers each may form a dimer or higher polymers. Typical examples of the polymerized dye-forming couplers are described in U.S. Patents 3,451,820 and 4,080,211. Also, specific examples of the polymerized magenta couplers are described in British Patent 2,102,173 and U.S. Patent 4,367,282. Couplers releasing a photographically useful residue upon coupling are preferably used in this invention. DIR couplers, i.e., couplers releasing a development inhibitor are described in the patents cited in the above-described Research Disclosure, No. 17643, VII-F. Preferred examples of these couplers which can be used in this invention are developer inactivating type couplers described in Japanese Patent Application (OPI) No. 151,944/82, timing type couplers described in, for example, U.S. Patent 4,248,962 and Japanese Patent Application (OPI) No. 154,234/82, reaction type couplers described in Japanese Patent Application (OPI) No. 39,653/84. Particularly preferred examples of these couplers are development inactivating type DIR couplers described in, for example, Japanese Patent Application (OPI) Nos. 151,944/82, 217,932/83, Japanese Patent Application Nos. 75,474/84, 82,214/84, 90,438/84, and reaction type DIR couplers described in, for example, Japanese Patent Application No. 39,653/84. For the photographic light-sensitive materials of this invention, couplers imagewise releasing a nucleating agent or a development accelerator at the development can be used. Specific examples of these couplers are described in British Patents 2,097,140 and 2,131,188. Also, couplers releasing a nucleating agent having an adsorptive action for silver halide are particularly preferred in this invention and specific examples thereof are described in Japanese Patent Application (OPI) Nos. 157,638/84 and 170,840/84. The couplers for use in this invention can be used in the light-sensitive materials by various known dispersion methods. Examples of a high-boiling solvent used in an oil-in-water dispersion method are described in U.S. Patent 2,322,027, Steps and effects of a latex dispersion method and examples of a loadable latex are described in, for example, U.S. Patent No. 4,199,363, West German Patent Application (OLS) Nos. 2,541,274 and 2,541,230. Examples of a support suitable for use in this invention are described in the above-described RD. No. 17643, page 28 and ibid., No. 18716, page 647, right column to page 648, left column. The color photographic light-sensitive materials of this invention can be processed by ordinary processes as described, for example, in the above-described Research Disclosure, No. 17643, pages 28 to 29 and ibid., No. 18716, page 651, left column to right column. The color photographic light-sensitive materials of this invention are usually subjected to a water-washing treatment or stabilization treatment after development and blixing or fixing. The water washing step is generally performed by a countercurrent washing using two or more water baths in order to save water. Also, as the stabilizing process, the multistage countercurrent stabilizing process described in Japanese Patent Application (OPI) No. 8543/82 is typical. Such a stabilizing process may be used in place of the water washing step. In the case of the stabilizing process, 2 to 9 counter-current baths are required. The stabilizing composition contains various compounds for stabilizing images. For example, there are various kinds of buffers (e.g., borates, metaborates, borax, phosphates, carbonates, potassium hydroxide, sodium hydroxide, aqueous ammonia, monocarboxylic acids, dicarboxylic acids, polycarboxylic acids, or a combination thereof) and formalin for adjusting the pH of films (e.g., pH 3 to 8). Furthermore, if necessary, the stabilizer composition may contain other additives such as a water softener (e.g., an inorganic phosphoric acid, aminopolycarboxylic acid, an organic phosphoric acid, and aminopolyphosphonic acid, a phosphonocarboxylic acid), a germicide (e.g., benzoisothiazolinone, isothiazolone, 4-thiazolinebenzimidazole, halogenated phenol), a surface active agent, an optical whitening agent, a hardening agent. Two or more kinds of these compounds may be used in combination. Also, as the film pH adjusting agent after processing, the use of an ammonium salt such as ammonium chloride, ammonium nitrate, ammonium sulfate, ammonium phosphate, ammonium sulfate, ammonium thiosulfate, is preferred. This invention can be applied to various kinds of color photographic light-sensitive materials. For example, there are general negative color photographic films, negative color photographic cinema films, color reversal photographic films for slide or television, color photographic papers, color positive photographic films, color reversal photographic papers. This invention can be also applied to a black and white light-sensitive material utilizing a mixture of three-color couplers described in Research Disclosure, RD., No. 17123 (July, 1978). This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: Figs. 1, 2, and 3 are electron microscopic photographs of typical silver halide crystal grains contained in emulsions A, 1, and 2 of Example 1, respectively. The present invention will be described by way of examples below. EXAMPLE 1 (1) Preparation of Emulsions While an aqueous solution obtained by dissolving 6 g of potassium bromide and 30 g of inactive gelatin to 3.7 l of distilled water was agitated, a 14% aqueous potassium bromide solution and a 20% aqueous silver nitrate solution were added to the above aqueous solution by a double jet method at constant flow rates, over 1 min, under the conditions of 55°C and a pBr of 1.0 (in this addition (I), 2.40% of the total silver amount was consumed). Then, an aqueous gelatin solution (17%, 300 ml) was added to the resultant mixture, and the solution was agitated at 55°C. Thereafter, a 20% aqueous silver nitrate solution was added to the mixture at a constant flow rate until the pBr reached 1.40 (in this addition (II), 5.0% of the total silver amount was consumed). A 20% aqueous potassium bromide solution containing 8.3 g of potassium iodide and a 33% aqueous silver nitrate solution were added to the resultant mixture by the double jet method, over 80 min (in this addition (III), 92.6% of the total silver amount was consumed). During the addition, a temperature and the pBr were maintained at 55°C and 1.50, respectively. The silver nitrate amount used in this emulsion was 425 g. Then, the resultant solution was desalted by a conventional flocculation method and optimally subjected to gold-plus-sulfur sensitization. As a result, comparative emulsion A containing tabular AgBrI (AgI = 2.0 mol%) grains having a mean grain diameter/thickness ratio of 6.5 and a sphere-equivalent diameter of 0.8 µm was prepared. The "sphere-equivalent" diameter is a diameter which the grain would have if it were spherical. Comparative emulsion B containing tabular AgBrI (AgI = 2.0 mol%) grains, wherein the mean grain diameter/thickness ratio was 6.4 and the sphere-equivalent diameter was 0.8 µm, was prepared following the same procedures as for emulsion A except that potassium iodide was removed from the halide solution used in addition (III) and a solution containing 8.3 g of potassium iodide was added at the end of addition (III). Emulsion 1 of this invention containing tabular AgBrI (AgI = 2.0 mol%) grains, wherein the mean grain diameter/thickness ratio was 6.3 and a sphere-equivalent diameter was 0.8 µm, was prepared following the same procedures as for emulsion B except that when 57% of the total silver amount was consumed in addition (III), the addition of silver nitrate and potassium bromide was temporarily stopped and a solution containing 8.3 g of potassium iodide was added. Emulsion 2 of this invention containing tabular AgBrI (AgI = 2.0 mol%) grains, wherein the mean grain diameter/thickness ratio was 6.0 and the sphere-equivalent diameter was 0.8 µm, was prepared following the same procedures as for emulsion A except that a 20% aqueous potassium bromide solution containing 4.0 g of potassium iodide was used as a halide solution in addition (III), and when 25% of the total silver amount was consumed in addition (III), the addition of silver nitrate and the above halide solution was temporarily stopped and a solution containing 4.3 g of potassium iodide was added. (2) Observation of Dislocations in Grains The dislocations in the grains in emulsions A, B, 1, and 2 were directly observed using the transmission electron microscope described in this specification. The JEM-2000FX (tradename) available from Nihon Denshi K.K. was used as the electron microscope, and observation was performed with a voltage of 200 kV at a liquid nitrogen temperature. Fig. 1 is a photograph of typical grains obtained in emulsion A. In the photograph of Fig. 1, round black spots are found at random positions. These spots are sometimes gradually enlarged during observation and hence can be assumed to be contamination or print out silver. That is, no clear dislocations are found in Fig. 1. In emulsion A, 90% or more of the total grains are such grains as shown in Fig. 1. Fig. 2 is a photograph of typical grains obtained in emulsion 1. In the photograph of Fig. 2, in addition to the black spots as in Fig. 1, a large number of dislocation lines are clearly found from a position away from the center of the grain by about 90% of a length between the center and an edge, to the edge. In emulsion 1, 80% or more (number) of the total of silver halide grains include 20 or more of such dislocation lines. Fig. 3 is a photograph of typical grains obtained in emulsion 2. In the photograph of Fig. 3, a large number of dislocation lines are clearly found from a position away from the center of the grain by about 80% of the length between the center and an edge, to the edge as in Fig. 2. In emulsion 2, 90% or more (number) of the total silver halide grains include 20 or more of such dislocation lines. In emulsion B, no dislocation lines as in Figs. 2 and 3 were observed (in this sample a large number of AgI grains were adhered to a portion near an edge of the tabular grain). (3) Preparation and Evaluation of Coated Samples Sensitizing dye S-5 was added to the emulsions obtained in (1). Then, dodecylbenzene sulfonate as a coating aid, p-vinyl benzene sulfonate as a thickening agent, a vinyl sulfonate series compound as a hardening agent, and a polyethylene oxide series compound as a photographic characteristics modifying agent were added to the resultant emulsions, thereby obtaining emulsion liquids for coating. Subsequently, these liquids for coating were independently uniformly applied on an undercoated polyester base, and a surface protective layer mainly consisting of an aqueous gelatin solution was applied thereon. As a result, coated samples 1 and 2 respectively having comparative emulsions A and B and coated samples 3 and 4 respectively having emulsions 1 and 2 of this invention were prepared. In samples 1 to 4, the amount of coated silver was 4.0 g/m², the amount of coated gelatin of the protective layers was 1.3 g/m², and the amount of coated gelatin emulsion layers was 2.7 g/m². In order to evaluate the coated samples obtained as described above, the following tests were performed. 1 ○ Exposure Intensity Dependency; Sample pieces of coated samples 1 to 4 subjected to wedge exposure with an exposure amount of 50 cd.m.s for an exposure time of 1/100 and with an exposure amount of 50cd.m.s for an exposure time of 10 were simultaneously developed by a processing solution consisting of the following composition at 20°C for 4 min. Then, after fixing, washing, and drying, sensitometry was performed. Thereafter, the senstivity was obtained in accordance with the reciprocal of the exposure amount which gives a density of fog + 0.1, and values of 1/100 s - and 10 s -exposures were compared. 2 ○ Resistance to incubation; Three sets of sample pieces of coated samples 1 to 4 were prepared. One of the three sets was kept at a temperature of 50°C and a humidity of 30% RH for three days, another set was kept at 50°C and 80% RH, and the remaining one was kept at room temperature as a control test. These samples were wedge-exposed for 1/100 s and subjected to the treatment and sensitometry following the same procedures as in 1 ○ to obtain the sensitivity. Then, the values of the obtained sensitivity were compared. 3 ○ Latent Image Stability; Three sets of sample pieces of coated samples 1 to 4 were prepared and wedge-exposed for 1/100 s . Then, one of the three sets was kept at 50°C and 30% RH for three days, another set was kept at 50°C and 80% RH for three days, and the remaining one was kept in a freezer as a control test. Following the same procedures as in 1 ○, these samples were subjected to the treatment and sensitometry to obtain sensitivity. The, the values of the obtained sensitivity were compared. 4 ○ Resistance to pressure; Sample pieces of coated samples 1 to 4 were bent through a predetermined angle and processed following the same procedures as in 1 ○. Then, the values of fog density at bent portions were compared. Processing Solution: 1-phenyl-3-pyrazolidone 0.5 g Hydroquinone 10 g Disodium Ethylenediaminetetraacetate 2 g Potassium Sulfite 60 g Boric Acid 4 g Potassium Carbonate 20 g Sodium Bromide 5 g Diethylene Glycol 20 g Sodium Hydroxide to obtain a pH of 10.0 Water to make 1 l As is apparent from Table 1, as compared with samples 1 and 2 comprising comparative emulsions A and B, samples 3 and 4 comprising emulsions 1 and 2 of this invention had higher sensitivities, smaller desensitization at low intensity and smaller sensitization and latent image fading upon incubation. That is, the effects of this invention are notable. In addition, samples 3 and 4 had less stress marks than sample 1. EXAMPLE 2 A multilayer color light-sensitive material comprising a plurality of layers having the following compositions was formed on an undercoated triacetyl-cellulose film support to prepare samples 101 to 104 containing emulsions A, B, 1, and 2 described in Example 1 in their third green-sensitive layers and second and third blue-sensitive layers. Layer 1: Antihalation Layer: Black Colloid Silver 0.25 g/m² Ultraviolet Absorbent U-1 0.1 g/m² Ultraviolet Absorbent U-2 0.1 g/m² High Boiling organic Solvent Oil-1 0.1 ml/cm² Gelatin 1.9g/m² Layer 2: Interlayer-1: Compound Cpd D 10 mg/m² High Boiling Organic Solvent Oil-3 40 mg/m² Gelatin 0.4 g/m² Layer 3: Interlayer-2: Surface-fogged Fine Silver Iodobromide Emulsion (mean grain size: 0.06 µm, AgI content: 1 mol%) silver 0.05 g/m² Gelatin 0.4 g/m² Layer 4: 1st Red-sensitive Emulsion Layer: Silver Iodobromide Emulsion (a 1 : 1 mixture of a mono-dispersed cubic emulsion having a mean grain size of 0.2 µm and an AgI content of 5 mol% and a mono-dispersed cubic emulsion having a mean grain size of 0.1 µm and an AgI content of 5 mol%) Spectrally Sensitized with Sensitizing Dyes S-1 and S-2 silver 0.4 g/m² Coupler C-1 0.2 g/m² Coupler C-2 0.05 g/m² High Boiling Organic Solvent Oil-1 0.1 ml/m² Gelatin 0.8 g/m² Layer 5: 2nd Red-sensitive Emulsion Layer: Silver Iodobromide Emulsion (a mono-dispersed cubic emulsion having a mean grain size of 0.3 µm and an AgI content of 4 mol%) Spectrally Sensitized with Sensitising Dyes S-1 and S-2 silver 0.4 g/m² Coupler C-1 0.2 g/m² Coupler C-3 0.2 g/m² Coupler C-2 0.05 g/m² High Boiling Organic Solvent Oil-1 0.1 ml/m² Gelatin 0.8 g/m² Layer 6: 3rd Red-sensitive Emulsion Layer: Silver Iodobromide Emulsion (a mono-dispersed cubic emulsion having a mean grain size of 0.4 µm and an AgI content of 2 mol%) Spectrally Sensitized with Sensitizing Dyes S-1 and S-2 silver 0.4 g/m² Coupler C-3 0.7 g/m² Gelatin 1.1 g/m² Layer 7: Interlayer-3: Dye D-1 0.02 g/m² Gelatin 0.6 g/m² Layer 8: Interlayer-4: Surface-fogged Fine Silver Iodobromide Emulsion (mean grain size: 0.06 µm, AgI content: 1 mol%) silver 0.05 g/m² Compound Cpd A 0.2 g/m² Gelatin 1.0 g/m² Layer 9: 1st Green-sensitive Emulsion Layer: Silver Iodobromide Emulsion (a 1 : 1 mixture of a mono-dispersed cubic emulsion having a mean grain size of 0.2µm and an AgI content of 5 mol% and a mono-dispersed cubic emulsion having a mean grain size of 0.1 µm and an AgI content of 5 mol%) Spectrally Sensitized with Sensitizing Dyes S-3 and S-4 silver 0.5 g/m² Coupler C-4 0.3 g/m² Compound Cpd B 0.03 g/m² Gelatin 0.5 g/m² Layer 10: 2nd Green-sensitive Emulsion Layer: Silver Iodobromide Emulsion (a mono-dispersed cubic emulsion having a mean grain size of 0.4 µm and an AgI content of 5 mol%) Spectrally Sensitized with Sensitizing Dyes S-3 and S-4 silver 0.4 g/m² Coupler C-4 0.3 g/m² Compound Cpd B 0.03 g/m² Gelatin 0.6 g/m² Layer 11: 3rd Green-sensitive Emulsion Layer: Silver Iodobromide Emulsion (emulsion A, B, 1, or 2 described in Example 1) Spectrally Sensitized with Sensitizing Dyes S-3 and S-4 silver 0.5 g/m² Coupler C-4 0.8 g/m² Compound Cpd B 0.08 g/m² Gelatin 1.0 g/m² Layer 12: Interlayer-5: Dye D-2 0.05 g/m² Gelatin 0.6 g/m² Layer 13: Yellow Filter Layer: Yellow Colloid Silver 0.1 g/m² Compound Cpd A 0.01 g/m² Gelatin 1.1 g/m² Layer 14: 1st Blue-sensitive Emulsion Layer: Silver Iodobromide Emulsion (a 1 : 1 mixture of a mono-dispersed cubic emulsion having a mean grain size of 0.2µm and an AgI content of 3 mol% and a mono-dispersed cubic emulsion having a mean grain size of 0.1µm and an AgI content 3 mol%) Spectrally Sensitized with Sensitizing Dyes S-5 and S-6 silver 0.6 g/m² Coupler C-5 0.6 g/m² Gelatin 0.8 g/m² Layer 15: 2nd Blue-sensitive Emulsion Layer: Silver Iodobromide Emulsion (the same emulsion as the emulsion of the 3rd green-sensitive emulsion layer) Spectrally Sensitized with Sensitizing Dyes S-5 and S-6 silver 0.4 g/m² Coupler C-5 0.3 g/m² Coupler C-6 0.3 g/m² Gelatin 0.9 g/m² Layer 16: 3rd Blue-sensitive Emulsion Layer: Silver Iodobromide Emulsion (the same emulsion as the emulsion of the 3rd green-sensitive emulsion layer) Spectrally Sensitized with Sensitizing Dyes S-5 and S-6 silver 0.4 g/m² Coupler C-6 0.7 g/m² Gelatin 1.2 g/m² Layer 17: 1st Protective Layer: Ultraviolet Absorvent U-1 0.04 g/m² Ultraviolet Absorvent U-3 0.03 g/m² Ultraviolet Absorvent U-4 0.03 g/m² Ultraviolet Absorvent U-5 0.05 g/m² Ultraviolet Absorvent U-6 0.05 g/m² Compound Cpd C 0.8 g/m² Dye D-3 0.05 g/m² Gelatin 0.7 g/m² Layer 18: 2nd Protective Layer: Surface-fogged Fine Silver Iodobromide Emulsion (mean grain size: 0.06µm, AgI content: 1 mol%) silver 0.1 g/m² Polymethyl Methacrylate Grains (mean grain size: 1.5 µm) 0.1 g/m² 4 : 6 Copolymer of Methyl Methyacrylate and Acrylic Acid (mean grain size: 1.5 µm) 0.1 g/m² Silicone Oil 0.03 g/m² Fluorine-containing Surface Active Agent W-1 3 mg/m² Gelatin 0.8 g/m² Gelatin hardening agent H-1 and a surface active agent were added to the layers in addition to the above compositions. Samples 101 to 104 obtained as described above were processed following the same procedures as in 1 ○ to 4 ○ in Example 1 except for development, and developed as described below. Process Steps of Development: Step Time Temperature 1st Development 6 min 38°C washing 2 min 38°C Reversal Development 2 min 38°C Color Development 6 min 38°C Conditioning 2 min 38°C Bleaching 6 min 38°C Fixing 4 min 38°C Washing 4 min 38°C Stabilizing 1 min Room Temperature Drying The compositions of the processing solutions were as follows. First Developer: Water 700 mℓ Pentasodium Nitrilo-N N,N-trimethylenephosphonate 2 g Sodium Sulfite 20 g Hydroquinone Monosulfonate 30 g Sodium Carbonate (Monohydrate) 30 g 1-phenyl-4-methyl-4-hydroxymethyl-3-pyrazolidone 2 g Potassium Bromide 2.5 g Potassium Thiocyanate 1.2 g Potassium Iodide (0.1% solution) 2 mℓ Water to make 1,000 mℓ Reversing Solution: Water 700 mℓ Pentasodium Nitrilo-N,N,N-trimethylenephosphonate 3 g Stannous Chloride (Dihydrate) 1 g p-aminophenol 0.1 g Sodium Hydroxide 8 g Glacial Acetic Acid 15 mℓ Water to make 1,000 mℓ Color Developer: Water 700 mℓ Pentasodium Nitrilo-N,N,N-trimethylenephosphonate 3 g Sodium Sulfite 7 g Tribasic Sodium Phosphate (Dodecahydrate) 36 g Potassium Bromide 1 g Potassium Iodide (0.1% solution) 90 mℓ Sodium Hydroxide 3 g Citrazinic Acid 1.5 g N-ethyl-N-(β-methanesulfonamidoethyl)-3-methyl-4-aminoaniline Sulfate 11 g 3,6-dithiaoctane-1,8-diol 1 g Water to make 1,000 mℓ Conditioning Solution: Water 700 mℓ Sodium Sulfite 12 g Sodium Ethylenediaminetetraacetate (Dihydrate) 8 g Thioglycerin 0.4 mℓ Glacial Acetic Acid 3 mℓ Water to make 1,000 mℓ Bleaching Solution: Water 800 mℓ Sodium ethylenediaminetetraacetate (Dihydrate) 2 g Ammonium Iron (III) Ethylenediaminetetraacetate (Dihydrate) 120 g Potassium Bromide 100 g Water to make 1,000 mℓ Fixing Solution: Water 800 mℓ Ammmonium Thiosulfate 80.0 g Sodium Sulfite 5.0 g Sodium Bisulfite 5.0 g Water to make 1,000 mℓ Stabilizing Solution: Water 800 mℓ Formalin (37 wt%) 5.0 mℓ Fuji Driwel (surface active agent available from Fuji Photo Film Co., Ltd.) 5.0 mℓ Water to make 1,000 mℓ The color reversal sensitivities of the 3rd green-sensitive layer and the 2nd and 3rd blue-sensitive layers were estimated on the basis of the relative exposure amount for giving a density larger by 2.0 than the minimum density of magenta and yellow densities. As a result, similar results to the results in Example-1-(3) were obtained. As for resistance to pressure, as compared with comparative sample 101, reductions in the yellow and magenta densities of pressurized portions at the high density side of samples 103 and 104 of this invention are largely reduced. EXAMPLE 3 Layers consisting of the following compositions were applied on an undercoated triacetylcellulose support, thereby preparing multilayer color light-sensitive material samples 201 to 204 containing emulsions A, B, 1, and 2 described in Example 1 in their 3rd green-sensitive layers and 3rd blue-sensitive layers. Layer 1: Antihalation Layer: Black Colloid Silver silver 0.18 g/m² Gelatin 1.40 g/m² Layer 2: Interlayer: 2,5-di-t-Pentadecyl Hydroquinone 0.18 g/m² C-11 0.07 g/m² C-13 0.02 g/m² U-11 0.08 g/m² U-12 0.08 g/m² Oil-2 0.10 g/m² Oil-1 0.02 g/m² Gelatin 1.0 g/m² Layer 3: 1st Red-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.3µm) Spectrally Sensitized with Sensitizing Dyes S-11, S-12, S-13, and S-18 silver 1.15 g/m² C-12 0.14 g/m² Oil-2 0.005 g/m² C-20 0.005 g/m² Gelatin 1.20 g/m² Layer 4: 2nd Red-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.6µm) Spectrally Sensitized with Sensitizing Dyes S-11, S-12, S-13, and S-18 silver 1.50 g/m² C-12 0.060 g/m² C-13 0.008 g/m² C-20 0.004 g/m² Oil-2 0.005 g/m² Gelatin 1.50 g/m² Layer 5: 3rd Red-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.8µm) Spectrally Sensitized with Sensitizing Dyes S-11, S-12, S-13, and S-18 silver 1.50 g/m² C-15 0.012 g/m² C-13 0.003 g/m² C-14 0.004 g/m² Oil-2 0.32 g/m² Gelatin 1.63 g/m² Layer 6: Interlayer: Gelatin 1.06 g/m² Layer 7: 1st Green-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.3µm) Spectrally Sensitized with Sensitizing Dyes S-14, S-15, and S-16 silver 0.35 g/m² C-16 0.120 g/m² C-11 0.021 g/m² C-17 0.030 g/m² C-18 0.025 g/m² Oil-2 0.20 g/m² Gelatin 0.70 g/m² Layer 8: 2nd Green-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.6µm) Spectrally Sensitized with Sensitizing Dyes S-14, S-15, and S-16 silver 0.75 g/m² C-16 0.021 g/m² C-18 0.004 g/m² C-11 0.002 g/m² C-17 0.003 g/m² Oil-2 0.15 g/m² Gelatin 0.80 g/m² Layer 9: 3rd Green-sensitive Emulsion Layer: Silver Iodobromide Emulsion (emulsion A, B, 1, or 2 described in Example 1) Spectrally Sensitized with Sensitizing Dyes S-14, S-15, and S-16 silver 1.80 g/m² C-16 0.011 g/m² C-11 0.001 g/m² Oil-1 0.69 g/m² Gelatin 1.74 g/m² Layer 10: Yellow Filter Layer: Yellow Colloid Silver silver 0.05 g/m² 2,5-di-t-pentadecyl Hydroquinone 0.03 g/m² Gelatin 0.95 g/m² Layer 11: 1st Blue-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.3µm) Spectrally Sensitized with Sensitizing Dye S-17 silver 0.24 g/m² C-19 0.27 g/m² C-18 0.005 g/m² Oil-2 0.28 g/m² Gelatin 1.28 g/m² Layer 12: 2nd Blue-sensitive Emulsion Layer: Silver Iodobromide Emulsion (irregular multi-twinning grains having an iodide content of 2 mol% and a mean grain sphere-equivalent size of 0.6µm) Spectrally Sensitized with Sensitizing Dye S-17 silver 0.45 g/m² C-19 0.098 g/m² Oil-2 0.03 g/m² Gelatin 0.46 g/m² Layer 13: 3rd Blue-sensitive Emulsion Layer: Silver Iodobromide Emulsion (the same emulsion as the emulsion of the 3rd green-sensitive layer) Spectrally Sensitized with Sensitizing Dye S-17 silver 0.77 g/m² C-19 0.036 g/m² Oil-2 0.07 g/m² Gelatin 0.69 g/m² Layer 14: 1st Protective Layer: Silver Iodobromide (silver iodide: 1 mol%, mean grain size: 0.07µm) silver 0.5 g/m² U-11 0.11 g/m² U-12 0.17 g/m² Oil-2 0.90 g/m² Layer 15: 2nd Protective Layer: Polymethylmethacrylate Grains (size: about 1.5 µm) 0.54 g/m² U-13 0.15 g/m² U-14 0.10 g/m² Gelatin 0.72 g/m² Gelatin hardening agent H-1 and a surface active agent were added to the layers in addition to the above compositions. Samples 201 to 204 obtained as described above were processed following the same procedures as in 1 ○ to 4 ○ in Example-1-(3) except for development, and developed as described below. Step of Development (38°C) Time Color Development 3 min 15 s Bleaching 6 min 30 s Washing 2 min 10 s Fixing 4 min 20 s Washing 3 min 15 s Stabilizing 1 min 05 s The compositions of the processing solutions used in the above steps were as follows. Color Developer: Diethylenetriaminepentaacetic Acid 1.0 g 1-hydroxyethylidene-1,1-Diphosphonic Acid 2.0 g Sodium Sulfite 4.0 g Potassium Carbonate 30.0 g Potassium Bromide 1.4 g Potassium Iodide 1.3 mℓ Hydroxyamine Sulfate 2.4 g 4-(N-ethyl-N-β-hydroxyethylamino)-2-methylaniline Sulfate 4.5 g Water to make 1.0 l pH 10.0 Bleaching Solution: Ferric Ammonium Ethylenediaminetetraacetate 100.0 g Disodium Ethylenediaminetetraacetate 10.0 g Ammonium Bromide 150.0 g Ammonium Nitrate 10.0 g Water to make 1.0 l pH 6.0 Fixing Solution: Disodium Ethylenediaminetetraacetate 1.0 g Sodium Sulfite 4.0 g Aqueous Ammonium Thiosulfate Solution (70%) 175.0 mℓ Sodium Bisulfite 4.6 g Water to make 1.0 pH 6.6 l Stabilizing Solution: Formalin (40%) 2.0 mℓ Polyoxyethylene-p-monononylphenylether (mean polymerization degree: 10) 0.3 g Water to make 1.0 l The color negative sensitivities of the 3rd green-sensitive layer and the 3rd blue-sensitive layer were estimated on the basis of the relative exposure amount for giving a density larger by 0.1 than the minimum density of magenta and yellow densities. As a result, as in Example-1-(3), samples 203 and 204 had a higher sensitivity, a smaller low-intensity reciprocity failure, a smaller sensitization and a latent image fading upon incubation, and less stress marks than those of comparative samples 201 and 202. That is, the advantages of this invention are notable. The structures of the compounds used in Examples 1 to 3 were shown in Table 5. EXAMPLE 4 (1) Preparation of Emulsion In preparation of emulsion A described in Example-1-(1), the amount of potassium bromide in a vessel before silver nitrate was added, the amount of gelatin, the temperature, and the addition time of addition (I) were controlled, thereby preparing comparative emulsions C to G containing tabular AgBrI (AgI = 2.0 mol%) grains, wherein the various mean grain diameter/thickness ratios were as shown in Table 2 and the sphere corresponding diameter was about 0.8 µm. In preparation of emulsion 1 described in Example-1-(1), the parameters described above were controlled thereby preparing emulsions 3 to 7 of the invention containing tabular AgBrI (AgI = 2.0 mol%) grains, wherein the various mean grain diameter/thickness ratios were as shown in Table 2 and the sphere corresponding diameter was about 0.8 µm, Emulsions C to G and 3 to 7 obtained as described above were mono-dispersed hexagonal tabular emulsions wherein the variation coefficient of the grain size distribution was 15% or less. (2) Observation of Dislocations in Grains Following the same procedures as in Example-1-(2), the dislocations in grains in the above emulsions were observed. As a result, similar to emulsion A, 90% or more of the grains of emulsions C to G had no clear dislocations. Emulsions 3 to 7 had dislocations similar to those of emulsion 1. In this case, 80% or more of the total of grains contained 10 or more dislocations. (3) Preparation and Evaluation of Coated Samples Following the same procedures as in Example-1-(3), coated samples 5 to 14 listed in Table 2 were prepared using emulsions C to G and 3 to 7, respectively. Following the same procedures as in 2 ○ and 4 ○ described in Example-1-(3), the resistance to incubation and resistance to pressure were evaluated. The results of resistance to incubation are shown in Table 2. As is apparent from Table 2, the advantage of this invention is significant for the tabular emulsions having mean grain diameter/thickness ratios of 4 to 10. As for resistance to pressure, almost no stress marks were generated in samples 10 to 13, but some stress marks smaller than those in sample 9 were generated in sample 14. EXAMPLE 5 (1) Preparation of Emulsion An aqueous solution was obtained by dissolving 6 g of potassium bromide and 30 g of inactive gelatin in 3.7 l of distilled water. A 14% aqueous potassium bromide solution and a 20% aqueous silver nitrate solution were added to the above aqueous solution by a double jet method at constant flow rates over 1 min under the conditions of 55°C and a pBr of 1.0 while the above solution was agitated well (in this addition (I), 2.40% of a total silver amount was consumed). Then, an aqueous gelatin solution (17%, 300 mℓ) was added and agitated at 55°C, and a 20% aqueous silver nitrate solution was added at a constant flow rate until the pBr reached 1.40 (in this addition (II), 5.0% of the total silver amount was consumed). A 20% aqueous potassium bromide solution and a 33% aqueous silver nitrate solution were added by the double jet method over 43 min (in this addition (III), 49.6% of the total silver amount was consumed). During the addition, the temperature and the pBr were maintained at 55°C and 1.50, respectively. 0.7 m mol/Ag mol of sodium anhydro-5-chloro-9-ethyl-5'-phenyl-3,3'-di(3-sulfopropyl) oxacarbocyaninehydroxide was added and adsorbed. Then, a solution containing 8.3 g of potassium iodide and a 33% aqueous silver nitrate solution were added by the double jet method over 2 min (in this addition (IV), 2.0% of the total silver amount was consumed). Then, the resultant material was washed until the above composition lost site directivity, and the pBr was returned to 1.50. Aqueous potassium bromide and aqueous silver nitrate solutions having the same concentrations as in addition (III) were added by the double jet method over 26.3 min (in this addition (V), 31.0% of the total silver amount was consumed). During the addition, the temperature and the pBr were maintained at 55°C and 1.50, respectively. The amount of silver nitrate used in this emulsion was 425 g. Desalting and after-ripening were performed following the same procedures as for emulsion A described in Example-1-(1), thereby preparing tabular AgBrI (AgI = 2.0 mol%) emulsion 8 of this invention having a mean grain diameter/thickness ratio of 6.0 and a sphere equivalent diameter of 0.8 µm. Tabular AgBrI (AgI = 2.0 mol%) emulsion 9 of this invention having a mean grain diameter/thickness ratio of 7.0 and a sphere equivalent diameter of 0.9 µm was prepared following the same procedures as for emulsion 7 except that sodium 5,5',6,6'-tetrachloro-1,1'-diethyl-3,3'-di(3-sulfopropyl)-imidacarbocyanine was used as the site director and the pH was set to be 3.0 instead of washing in order to remove this director after addition (IV). Emulsion 10 of this invention having a mean grain diameter/thickness ratio of 5.0 and a sphere-equivalent diameter of 0.8 µm was prepared following the same procedures as for emulsion 7 except that 3-carboxymethyl-5-{2-(3-ethyl-2(3H)-thiazolinidene)ethylidene}rhodanine was used as the site director and 0.7 m mol/Ag mol of H₂O₂ was added instead of washing in order to remove this director after addition (IV). An aqueous solution was obtained by dissolving 6 g of potassium bromide and 30 g of inactive gelatin in 2 l of distilled water. Then, a 14% aqueous potassium bromide solution containing potassium iodide in an amount of a g and a 20% aqueous silver nitrate solution were added to the above aqueous solution by the double jet method at constant flow rates over a predetermined time under the conditions of 55°C and a predetermined pBr (in this addition (I'), 5.0% of the total silver amount was consumed). An aqueous gelatin solution (17%, 300 ml) was added at 55°C and the resultant was agitated. Then, a solution containing potassium iodide in an amount of b g and a 20% aqueous silver nitrate solution were added at constant flow rates until the pBr reached a predetermined value (in this addition (II'), 10.0% of the total silver amount was consumed). A 20% aqueous potassium bromide solution containing potassium iodide in an amount for adding c g of potassium iodide and a 33% aqueous silver nitrate solution were added by the double jet method, thereby preparing core grains (in this addition (III'), 35% of the total silver amount was consumed). During the addition, the temperature and the pBr were maintained at 55°C and a predetermined value, respectively. A solution containing d g of potassium iodide was added over 1 min. Then, a 20% aqueous potassium bromide solution containing potassium iodide in an amount for adding e g of potassium iodide and a 33% aqueous silver nitrate solution were added by the double jet method to form a shell on the core grain (in this addition (IV'), 50% of the total silver amount was consumed). During the addition, the temperature and the pBr were maintained at 55°C and a predetermined value. The silver nitrate amount used in this emulsion was 425 g. Thereafter, desalting and after-ripening were performed following the same procedures as for emulsion A in Example-1-(1). In this formulation method, the amounts of potassium iodide, a to e, were changed and the addition time and the pBr were controlled, thereby preparing comparative emulsion H containing tabular AgBrI (AgI = 8 mol%) grains, wherein a mean sphere-equivalent diameter was 0.7 µm, and emulsions 11 to 13 of this invention listed in Table 3. Emulsion 14 of this invention containing tabular AgBrI (AgI = 2 mol%) grains, wherein the mean grain diameter/thickness ratio was 5.0 and the sphere equivalent diameter of 0.8 µm, was prepared following the same procedures as for emulsion 1 described in Example-1-(1) except that a solution containing 1.5 g of KSCN was added immediately before addition (III). Emulsion 15 of this invention containing tabular AgBrI (AgI = 2 mol%) grains, wherein the mean grain diameter/thickness ratio was 7.5 and the sphere equivalent diameter was 0.8 µm was prepared following the same procedures as for emulsion 2 described in Example-1-(1) except that addition (III) was acceleratedly performed over 40 min so that the flow rate at the end is three times as large as the flow rate at the start. Emulsion 16 of this invention containing tabular AgBrI (AgI = 2.0 mol%) grains, wherein the mean grain diameter/thickness ratio was 6.3 and the sphere equivalent diameter was 0.8 µm, was prepared following the same procedures as for emulsion 1 described in Example-1-(1) except that when 95% of the total silver amount was consumed during addition (III), addition of the silver nitrate and potassium bromide solutions were temporarily stopped and the solution containing 8.3 g of potassium iodide was added. (2) Observation of Dislocations in Grains Following the same procedures as in Example-1-(2), dislocations in grains in the above emulsions were observed. As a result, similar to emulsion A, 60% or more of the total grains of emulsion H had no clear dislocations. Emulsions 8 to 15 had dislocations similar to those of emulsion 1. In this case, 50% or more of the total grains of emulsions 8 to 15 had 10 or more dislocations. Emulsion 16 had dislocations at a position immediately close to an edge of tabular (i.e., outside a position separated away from the center by a distance which is 98% of a length between the center and the edge). (3) Preparation and Evaluation of Coated Samples Following the same procedures as in Example-1-(3), coated samples 15 to 24 were prepared as listed in Table 4. Then, following the same procedures as in Example-1-(3), coated samples 15 to 24 together with coated samples 1, 2, and 3 obtained in Example-1-(1) were evaluated. Table 4 Sample No. Used Emulsion No. Sample 15 Emulsion 8 Present Invention Sample 16 Emulsion 9 " Sample 17 Emulsion 10 " Sample 18 Emulsion H Comparative Example Sample 19 Emulsion 11 Present Invention Sample 20 Emulsion 12 " Sample 21 Emulsion 13 " Sample 22 Emulsion 14 " Sample 23 Emulsion 15 " Sample 24 Emulsion 16 " As a result, it was shown that as compared with coated sample 1, the advantage of this invention was significant in coated samples 15 to 17, 22 and 23 as in Example-1-(3). That is, coated samples 15 to 17, 22 and 23 had an excellent storage stability, exposure intensity dependency and resistance to pressure. In addition, as compared with coated sample 18, the advantage of this invention was significant in coated samples 19 to 21 of this invention. The characteristics of coated sample 24 were intermediate between those of coated samples 2 and 3, and were closer to those of coated sample 2. EXAMPLE 6 Comparative emulsion J containing tabular AgBrI (AgI = 4.0 mol%) grains, wherein the mean grain diameter/thickness ratio was 7.0 and the sphere equivalent diameter was 0.3 µm, was prepared following the same procedures as for emulsion A described in Example-1-(1) except that the temperature during grain formation was 40°C, addition (I) was performed over 30 S, and as the halide solution of addition (III), a 20% aqueous potassium bromide solution containing 16.6 g of potassium iodide was used. Emulsion 17 of this invention containing tabular AgBrI (AgI = 4.0 mol%) grains, wherein the mean grain diameter/thickness ratio was 6.5 and the sphere equivalent diameter was 0.3 µm, was prepared following the same procedures as for emulsion J except that potassium iodide was removed from the halide solution used in addition (III), and when 50% of the total silver amount was consumed during addition (III), addition of the silver nitrate and potassium bromide solutions were temporarily stopped and the solution containing 16.6 g of potassium iodide was added. A multilayer color light-sensitive material comprising layers having the following compositions was formed on an undercoated triacetylcellulose film support thereby preparing samples 301 and 302 containing emulsion J or 17 in their 1st red-sensitive, 1st green-sensitive, and 1st blue-sensitive layers. Layer 1: Antihalaticn Layer: Gelatin Layer (dry film thickness: 2 µm) containing Black Colloid Silver 0.25 g/m² Ultraviolet Absorbent U-1 0.04 g/m² Ultraviolet Absorbent U-2 0.1 g/m² Ultraviolet Absorbent U-3 0.1 g/m² High Boiling Organic Solvent O-1 0.1 ml/m² Layer 2: Interlayer: Gelatin layer (dry film thickness: 1 µm) containing Compound H-1 0.05 g/m² High Boiling Organic Solvent O-2 0.05 ml/m² Layer 3: 1st Red-sensitive Emulsion Layer: Gelatin Layer (dry film thickness: 1 µm) containing Silver Iodobromide Emulsion (emulsion J or 17) Spectrally Sensitized with Sensitizing Dyes S-1 and S-2 silver 0.5 g/m² Coupler C-1 0.2 g/m² Coupler C-2 0.05 g/m² High Boiling Organic Solvent O-2 0.12 ml/m² Layer 4: 2nd Red-sensitive Emulsion Layer: Gelatin Layer (dry film thickness: 2.5 µm) containing Silver Iodobromide Emulsion (mono-dispersed cubic grains having an iodide content of 3.0 mol% and a mean grain size of 0.6 µm) Spectrally Sensitized with Sensitizing Dyes S-1 and S-2 silver 0.8 g/m² Coupler C-1 0.55 g/m² Coupler C-2 0.14 g/m² High Boiling Organic Solvent O-1 0.33 ml/m² Layer 5: Interlayer: Gelatin Layer (dry film thickness: 1 µm) containing Compound H-1 0.1 g/m² High Boiling Organic Solvent O-2 0.1 ml/m² Layer 6: 1st Green-sensitive Emulsion Layer: Gelatin Layer (dry film thickness: 1 µm) containing Silver Iodobromide Emulsion (same as the emulsion 1st red-sensitive layer) Spectrally Sensitized with Sensitizing Dyes S-3 and S-4 silver 0.7 g/m² Coupler C-3 0.35 g/m² High Boiling Organic Solvent O-2 0.26 ml/m² Layer 7: 2nd Green-sensitive Emulsion Layer: Gelatin Layer (dry film thickness: 2.5 µm) containing Silver Iodobromide Emulsion (mono-dispersed cubic grains having an iodide content of 2.0 mol% and a mean grain size of 0:6 µ Spectrally Sensitized with Sensitizing Dyes S-3 and S-4 silver 0.7 g/m² Coupler C-4 0.25 g/m² High Boiling Organic Solvent O-2 0.05 ml/m² Layer 8: Interlayer: Gelatin Layer (dry film thickness: 1 µm) containing Compound H-1 0.05 g/m² High Boiling Organic Solvent O-2 0.1 ml/m² Layer 9: Yellow Filter Layer: Gelatin Layer (dry film thickness: 1 µm) containing Yellow Colloid Silver 0.1 g/m² Compound H-1 0.02 g/m² Compound H-2 0.03 g/m² High Boiling Organic Solvent O-2 0.04 ml/m² Layer 10: 1st Blue-sensitive Emulsion Layer: Gelatin Layer (dry film thickness: 1.5 µm) containing Silver Iodobromide Emulsion (same as the emulsion 1st red-sensitizing layer) Spectrally Sensitized with Sensitizing Dye S-5 silver 0.6 g/m² Coupler C-5 0.5 g/m² High Boiling Organic Solvent O-2 0.1 g/m² Layer 11: 2nd Blue-sensitive Emulsion Layer: Gelatin Layer (dry film thickness: 3 µm) containing Silver Iodobromide Emulsion (mono-dispersed cubic grains having an iodide content of 1.5 mol% and a mean grain size of 0.6 µm) Spectrally Sensitized with Sensitizing Dye S-5 silver 1.1 g/m² Coupler C-5 1.2 g/m² High Boiling Organic Solvent O-2 0.23 ml/m² Layer 12: 1st Protective Layer: Gelatin Layer (dry film thickness: 2 µm) containing Ultraviolet Absorbent U-1 0.02 g/m² Ultraviolet Absorbent U-2 0.03 g/m² Ultraviolet Absorbent U-3 0.03 g/m² Ultraviolet Absorbent U-4 0.29 g/m² High Boiling Organic Solvent O-1 0.28 ml/m² Layer 13: 2nd Protective Layer: Gelatin Layer (dry film thickness: 0.8 µm) containing Surface-fogged Fine Silver Iodobromide Grain Emulsion (iodide content: 1 mol%, mean grain size: 0.06 µm) silver 0.1 g/m² Polymethylmethacrylate Grains (mean grain size: 1.5 µm) Gelatin hardening agent H-3 and a surface active agent were added to the layers in addition to the above compositions. Samples 301 and 302 obtained as described above were processed following the same procedures as in 1 ○ to 4 ○ in Example-1-(3) except for development, and developed as described below. Process Steps: Step Time Temperature 1st Development 6 min 38°C Washing 2 min 38°C Reversal Development 2 min 38°C Color Development 6 min 38°C Conditioning 2 min 38°C Bleaching 6 min 38°C Fixing 4 min 38°C Washing 4 min 38°C Stabilizing 1 min Room Temperature Drying The compositions of the processing solutions were as follows. 1st Developer: Water 700 mℓ Pentasodium Nitrilo-N,N,N-trimethylenephosphonate 2 g Sodium Sulfite 20 g Hydroquinone Monosulfonate 30 g Sodium Carbonate (Monohydrate) 30 g 1-phenyl-4-methyl-4-hydroxymethyl-3-pyrazolidone 2 g Potassium Bromide 2.5 g Potassium Thiocyanic Acid 1.2 g Potassium Iodide (0.1% solution) 2 mℓ Water to make 700 mℓ Reversal Bath: Water 700 mℓ Pentasodium Nitrilo-N,N,N-trimethylenephosphonate 3 g Stannous Chloride (Dihydrate) 1 g p-aminophenol 0.1 g Sodium Hydroxide 8 g Glacial Acetic Acid 15 mℓ Water to make 1,000 mℓ Color Developer: Water 700 mℓ Pentasodium Nitrilo-N,N,N-trimethylenephosphonate 3 g Sodium Sulfite 7 g Tribasic Sodium Phosphate (Dodecahydrate) 36 g Potassium Bromide 1 g Potassium Iodide (0.1% solution) 90 mℓ Sodium Hydroxide 3 g Citrazinic Acid 1.5 g N-ethyl-N-(β-methanesulfonamidoethyl)3-methyl-4-aminoaniline Sulfate 11 g 3,6-dithiaoctane-1,8-diode 1 g Water to make 1,000 mℓ Conditioning Solution: Water 700 mℓ Sodium Sulfite 12 g Sodium Ethylenediaminetetraacetate (dihydrate) 8 g Thioglycerin 0.4 mℓ Glacial Acetic Acid 3 mℓ Water to make 1,000 mℓ Bleaching Solution: Water 800 mℓ Sodium Ethylenediaminetetraacetate (Dihydrate) 2 g Ferric (III) Ammonium Ethylenediaminetetraacetate (Dihydrate) 120 g Potassium Bromide 100 g Water to make 1,000 mℓ Fixing Solution: Water 800 mℓ Ammonium Thiosulfate 80.0 g Sodium Sulfite 5.0 g Sodium Bisulfite 5.0 g Water to make 1,000 mℓ Stabilizing Solution: Water 800 mℓ Formalin (37 wt%) 5.0 mℓ Fuji Driwel (surface active agent available from Fuji Photo Film Co., Ltd.) 5.0 mℓ Water to make 1,000 mℓ The color negative sensitivities of the 1st red-sensitive layer, the 1st green-sensitive layer and the 3re blue-sensitive layer were estimated on the basis of the relative exposure amount for giving a density larger by 0.5 than a minimum density of cyan, magenta and yellow densities. As a result, it was shown that as in Example-1-(3), coated sample 302 containing emulsion 17 of this invention had a better storage stability, exposure intensity dependency, and resistance to pressure than those of coated sample 301 containing comparative emulsion J. As for the resistance to pressure, the reductions in cyan, magenta, and yellow densities of a pressurized portion at the low density side were small in sample 302 while they were large in sample 301. The structures of the compounds used in Example 6 are shown in Table 6.

Claims: A silver halide emulsion comprising a dispersion medium and silver halide grains, the silver halide emulsion containing tabular silver halide grains having a thickness of 0.5 µm or less, a diameter of 0.3 µm or more, and a mean diameter-to-thickness ratio of 2 or more, characterized in that said tabular grains occupy at least 50% of a projected area of all the silver halide grains, and 50% (number) or more of said tabular grains include 10 or more dislocations per grain and said tabular grains have an inner region portion having a higher silver iodide content than the surface region of the tabular grains. A photographic light-sensitive material comprising a support having thereon at least one silver halide emulsion layer containing a silver halide emulsion comprising a dispersion medium and silver halide grains, the silver halide emulsion containing tabular silver halide grains having a thickness of 0.5 µm or less, a diameter of 0.3 µm or more and a mean diameter-to-thickness ratio of 2 or more, characterized in that said tabular grains occupy at least 50% of a projected area of all the silver halide grains, and 50% (number) or more of said tabular grains include 10 or more dislocations per grain and said tabular grains have an inner region portion having a higher silver iodide content than the surface region of the tabular grains.

Inventors: AYATO, HIROSHI FUJI PHOTO FILM CO., LTD., FUJITA, MUNEHISA FUJI PHOTO FILM CO., LTD., IKEDA, HIDEO FUJI PHOTO FILM CO., LTD., ISHIMARU, SHINGO FUJI PHOTO FILM CO., LTD., URABE, SHIGEHARU FUJI PHOTO FILM CO., LTD.
Applicants: FUJI PHOTO FILM CO., LTD.
Application year: 1988
Main classification: G03C1
IPC codes: G03C1