PROCESS FOR FORMING A PLANARIZED, METAL-STRAPPED POLYSILICON GATE FET

Abstract: A process for forming a planarized, low sheet resistance FET. A gate stack is defined on an exposed surface of a semiconductor substrate, the gate stack including a gate mask disposed on a patterned polysilicon layer. First and second diffusion having first and second silicide electrodes are then formed on the substrate, to provide low sheet resistance source and drain electrodes. An insulating layer is then formed on the substrate, and is planarized to expose an upper surface of the gate mask. The gate mask is then removed in wet H₃PO₄ to define an aperture in the insulating layer that exposes the polysilicon layer, and a conductive material is selectively grown on the substrate to provide a metal-strapped polysilicon gate electrode that is relatively co-planar with the planarized insulating layer.

Description: The present invention relates to reducing the sheet resistance of the source, gate and drain electrodes of an FET device. In the manufacture of highly dense semiconductor memory devices, a greater number of storage cells are coupled together along a single conductive line. This conductive line (i.e., word line) typically forms the control electrode of at least one of the devices that comprise a given memory cell. For example, in the so called one-device dynamic random access memory cell comprising a transistor coupled to a storage capacitor, the word line provides the gate electrode of the transistor. It is known in the art to reduce the sheet resistance of word lines by utilizing low resistance conductors such as aluminum. Back in the early to mid 1970's these materials were widely accepted throughout the industry. However, the development of the self-aligned FET (in which the source and drain impurity regions are implanted into regions of the substrate partially defined by the gate electrode) necessitated the adoption of heat-resistant conductors such as polysilicon. Another method of reducing sheet resistance is to use refractory metal silicides that are formed on top of (i.e., "strap") a polysilicon gate. Typically, as shown in U.S. Patent 4,593,454 (issued June 10, 1986 to Baudrant et al), a silicide layer is formed simultaneously over the gate electrode and the source/drain diffusion regions of an FET device. More specifically, after a polysilicon gate electrode has been defined on a substrate, ions are implanted to define the source/drain diffusion regions. Then an oxide layer is deposited and etched so that the sidewalls of the polysilicon gate electrode are covered with oxide. Then a refractory metal layer (the patent utilizes tantalum) is deposited on the substrate, and a heat cycle is carried out to form tantalum silicide in those portions of the tantalum disposed on exposed silicon. Note that the oxide disposed on the sidewalls of the polysilicon gate electrode prevent the silicide formed on the upper surface of the gate electrode from being connected to the silicide formed on the source/drain regions. The general simultaneous gate and source/drain silicide formation process as exemplified by the Baudrant et al patent suffers from several shortcomings. A recent trend in the semiconductor industry is to decrease the depth of the source/drain diffusion regions to less than 0.5 microns. These so-called "shallow junctions" are more resistant to punchthrough defects as the channel length of FET's is decreased below the one micron barrier. If a refractory metal is deposited over the shallow junctions to form a silicide thereon, the amount of junction silicon consumed during the silicide reaction may substantially degrade the characteristics of these shallow junction regions. In the prior art, this problem has been addressed by incorporating extra silicon at the shallow junction surface prior to refractory metal deposition. For example, as shown in an article by Reith et al, entitled "Controlled Ohmic Contact and Planarization For Very Shallow Junction Structures," IBM Technical Disclosure Bulletin , Vol. 20, No. 9, Feb. 1979, pp. 3480-3482, after implantation epitaxial silicon is grown so as to maintain the integrity of the shallow junctions after silicide formation. This process presents a tradeoff. By decreasing the silicon consumption of the source/drain regions by selective epi growth, the high temperature inherent in this process will drive the source/drain dopants further into the substrate, thus degrading the desired shallow junction characteristics. In U.S. Patent 4,587,718 (issued May 13, 1986 to Haken et al) the gate electrode silicide is formed prior to the source/drain silicides. A nitride mask is used to define a polysilicon gate electrode atop an oxide layer that completely covers the device area. The source/drain diffusion regions are then formed by implantation through this oxide layer, using the nitride/poly stack as an implantation mask. The nitride mask is then removed, and a layer of refractory metal is deposited on the substrate. The refractory metal layer (in this case titanium) will react with the exposed polysilicon gate without forming a silicide over the source/drain regions, because these regions are covered with the silicon oxide layer. After the gate electrode silicide formation process is completed, the oxide layer above the source/drain diffusion regions is removed, and a second layer of titanium is deposited on the substrate. During the course of the subsequent source/drain silicide reaction, the earlier-formed titanium silicide gate electrode will increase in thickness. Thus, a thick titanium silicide layer is formed on the gate electrode, and a thin titanium silicide layer is formed over the source/drain regions. In European Patent Application EP-A-0 106 458 a metal film is formed on a polysilicon gate electrode of a FET, by covering the substrate with planarised layers, etching back the planarised layers, so as to expose the mask layer on the gate, removing the mask layer on the polysilicon gate and forming a metal layer in contact with the polysilicon gate. See also U.S. Patent 4,453,306 (issued June 12, 1984 to Lynch et al). A gate electrode is formed of a polysilicon layer, a silicon dioxide layer and a palladium layer. The entire structure is covered with a polysilicon layer and the palladium electrode is converted into palladium-silicide. After removing this silicide, leaving the polysilicon gate electrode covered by the silicon dioxide layer, the remaining portions of the polysilicon layer are etched, as to form the source and drain electrodes. Cobalt is deposited over the polysilicon portions and converted into cobalt-silicide. The present inventors have investigated various methods of reducing the sheet resistance of the gate electrode below that obtained by refractory metal silicides. Tungsten silicide provides a resistivity of approximately 50 micro ohms-cm. On the other hand, a tungsten layer has a resistivity of approximately 10 micro ohms-cm, and an aluminum layer has a resistivity on the order of 3 micro ohms-cm. Thus, the inventors considered modifying an approach similar to the Lynch et al patent by replacing the silicide gate formation step with depositing either tungsten or aluminum. However, this modification would not achieve the intended result. If tungsten were to be deposited on top of a layer of polysilicon, the layers would react to form a silicide during the subsequent implant drive-in and source/drain silicide formation steps. This would greatly increase the sheet resistance of the gate electrode by forming tungsten silicide (as opposed to pure tungsten). Similarly, the physical/electrical qualities of an aluminum layer (or an aluminum alloy such as aluminum/silicon) would substantially degrade when exposed to these high processing temperatures. Another potential problem is presented by forming a refractory metal silicide on the gate electrode. Some CMOS circuits utilize so-called "dual work function" gate electrodes. In this technology, the polysilicon gates for the n-channel and p-channel devices are doped with P-type and N-type dopants, respectively, in order to achieve an enhanced p-channel device characteristic. If these differentially-doped polysilicon gate electrodes are covered with a refractory metal layer for subsequent silicide formation, the polysilicon dopants may intermix (due to the high dopant diffusively in refractory metal silicides) to destroy the above dual-work function advantages. Accordingly, a need has developed in the art to provide a FET device having a low sheet resistance metal-strapped polysilicon gate electrode as well as silicide source/drain electrodes. The invention as claimed solves the problem of providing the lowest possible sheet resistance metal-strapped polysilicon gate electrode for an FET device having a planar upper surface without causing intermixing of dual work function dopants and of providing the shallowest possible source/drain regions for the FET device while also providing low sheet resistance silicide electrodes for the source/drain regions. The advantages of the present invention are realized by a process for forming a low sheet resistance metal-strapped polysilicon gate FET. A gate stack is defined on an exposed surface of a semiconductor substrate. The gate stack includes a gate mask disposed on a patterned polysilicon layer. Using the gate stack as a supplemental implant and electrode formation mask, first and second shallow diffusion regions are formed having first and second silicide electrodes disposed on them. An insulating layer is then deposited on the substrate. The insulating layer has a thickness that is substantially equal to that of said gate stack. The insulator layer is planarized so as to expose an upper surface of said gate mask and the gate mask is removed to define an aperture in the insulating layer that exposes the polysilicon layer. N-type and p-type dopants are introduced to selected regions of the exposed polysilicon to define dual work function gates, and a low sheet resistance conductive material is deposited on the substrate to at least partially fill the apertures in said insulating layer so as to form a gate electrode of said FET that is relatively co-planar with the planarized insulating layer. The invention is described in detail below with reference to the drawings, in which: Figs. 1-6 are cross-sectional views of a semiconductor substrate undergoing the process sequence of the invention. As shown in Fig. 1, layers of polysilicon 30 and silicon nitride 40 are formed on a substrate 1. The substrate 1 is a P+ type, <100> monocrystalline silicon wafer having an isolation region 10 formed therein. In practice, a thin p-type epitaxial layer is grown on the p+ substrate, and an n-well is formed in selected portions of the epitaxial layer. The epi layer and the n-well are not shown solely for the sake of simplicity. The isolation region 10 could be conventional semi-recessed oxide isolation (S-ROX) structures. However, it is contemplated that the present invention will be utilized in conjunction with highly dense technologies in which the width of the isolation regions must be tightly controlled. Moreover, for reasons that will be discussed in more detail below, it is important in the present invention to retain a relatively high degree of planarity between the upper surface of the substrate and the upper surface of the isolation region. Accordingly, it is preferred to utilize an isolation structure that is fully buried in the substrate. An example of such a structure is shown in an article by Kuroxawa et al, "A New Bird's Beak Free Isolation for VLSI," IEDM Digest of Technical Papers 1981 , p. 384. Diffusion region 15 is then formed by simply implanting dopant into the substrate after the isolation region 10 is formed. Diffusion region 15 is formed by implanting or diffusing an n-type dopant. The purpose of region 15 is to control the threshold voltages of the FET devices to be subsequently formed. After the diffusion region 15 is provided, a thin dielectric layer 20 is formed on the exposed surface of the substrate. Typically, dielectric layer 20 is a 10 nm thick layer of silicon oxide. In practice, other structures having suitable dielectric properties (e.g. silicon oxynitride, silicon nitride, or a plurality of silicon nitride and silicon oxide layers) could also be used. A 200 nm thick layer of p-type polycrystalline silicon 30 is then deposited on the dielectric layer 20 using conventional techniques, and a 250 nm thick layer of CVD silicon nitride 40 is formed on the polysilicon layer 30, also using conventional techniques. With reference to Fig. 2, a layer of photosensitive polymer (e.g., a novolak-based photoresist) is coated on the silicon nitride layer 40, and is exposed and developed to define a photomask 50 having substantially vertical sidewalls. The exposed portions of silicon nitride layer 40 and polysilicon layer 30 are then sequentially etched in a directional mode to define a gate stack 100 that includes a silicon nitride portion 40A and a polysilicon portion 30A. In practice, the silicon nitride layer can be patterned by exposure to a CF₄/O₂ plasma and the polysilicon layer 30 can be patterned by exposure to an HCl/Cl₂ gaseous plasma. At this point in the process, note that the silicon nitride portion 40A defines a masking structure above the polysilicon gate electrode 30A. With reference to Fig. 3, after photomask 50 is removed, sidewall spacers 60 are formed on the exposed sides of polysilicon portion 30A. The sidewall spacers 60 can be formed using one of two methods. The first method is to simply oxidize the exposed surfaces of polysilicon portion 30A. Note that the overlying silicon nitride masking structure 40A prevents the upper surface of polysilicon portion 30A from being oxidized during this step. The preferred method is to deposit a layer of oxide over the entire structure, and directionally etch the deposited layer so that it is removed from the horizontal surfaces of the substrate. During this removal step, exposed portions of the underlying oxide layer 20 are also removed to define gate dielectric 20A. After sidewall spacers 60 are formed, the source and drain regions 70, 80 are formed, and silicide electrodes 70A, 80A are formed thereon, respectively. The diffusion regions and silicide electrodes can be formed using one of several techniques. One technique is to simply implant the dopant ions to define the diffusion regions using the gate stack 100 as an implantation mask, deposit a refractory metal such as cobalt or titanium over the substrate, and sinter the structure to form CoSi2 or TiSi2 over the junction regions. Note that the silicon nitride 40A and the sidewalls 60 prevent the refractory metal from combining with polysilicon 30A to form a gate silicide. A first alternative is to first grow epitaxial silicon over the exposed silicon regions in order to reduce the amount of silicon consumed during the silicide reaction, and then to carry out the above-described implant, refractory metal deposition and anneal steps. This first alternative would be employed when shallow junctions are desired. Another alternative is to deposit the refractory metal (e.g. Cobalt), heat treat the substrate for an amount of time sufficient to form a metal-rich silicide (by carrying out the anneal at temperatures or for times that are insufficient to form a silicon-rich silicide), remove the refractory metal without removing the metal-rich silicide, implant ions into the metal-rich silicide, and anneal the substrate in order to drive the dopants out of the metal-rich silicide to define shallow source/drain junction regions while converting the metal-rich silicide into silicon-rich silicide. This latter alternative is preferred, in that it is compatible with shallow junctions without necessitating selective epitaxial silicon growth. Whichever method is chosen, the key factor is that the process is carried out in the presence of a masking structure atop the polysilicon gate. Thus, the silicide formation and dopant diffusion steps, which are typically carried out at temperatures ranging between 800°C-1000°C, are performed prior to complete formation of the gate electrode of the FET. As shown in Fig. 4, the substrate is then covered with a thick conformal layer 90, preferably of silicon dioxide. The thickness of the deposited conformal layer 90 should be slightly less than the gate stack thickness (i.e., approximately 450 nm). This thickness differential is needed to account for variations in the topography across the wafer surface. For example, although the isolation region 10 is constructed to have a surface that is relatively co-planar with the upper surface of substrate 1, in practice the surface of isolation region 10 may extend above the surface of substrate 1. Moreover, note that a portion 90A of conformal layer 90 extends above the upper surface the gate stack 100. The thickness differential between conformal layer 90 and gate stack 100 is particularly important in removing portion 90A by polishing as described below. As shown in Fig. 5, the surface of conformal layer 90 is then planarized so as to remove portion 90A extending above the upper surface of the gate stack 100. A preferred method of planarizing the conformal layer 90 is to subject the wafer to a mechanical polishing procedure in the presence of an abrasive slurry. More specifically, a slurry commercially available from Cabot Corp. under the tradename "Cabot SCO1" is supplied to a Strasbaugh wafer polishing tool having a Suba IV perforated abrasive pad held at a pressure of 0,41 - 0,55 mbar. It has been found that carrying out this procedure for approximately four minutes is sufficient to remove portion 90A and to planarize the bulk film 90. That is, after portion 90A of layer 90 is removed, the polishing pad contacts the upper surface of the remainder of the conformal layer. It has been found that the frictional force experienced by the polishing pad greatly increases as the polishing pad contacts the bulk conformal layer surface. The force experienced by the pad can be monitored, such that the polishing procedure can be stopped at this point or continued for a discrete amount of time afterward. Thus, as shown in Fig. 5, the upper surface of the silicon nitride masking structure is approximately co-planar with, and is exposed by, the remaining portions of conformal layer 90. Another planarization method consists of coating the surface of conformal oxide layer 90 with a layer of photoresist, and exposing the substrate to an etchant that will remove the photoresist and the underlaying oxide at substantially the same rate. Since the photoresist is a non-conformal layer, its planar upper surface is simply replicated in the oxide layer. Then, as shown in Fig. 6, the silicon nitride masking structure is removed to expose the underlaying portion of polysilicon gate 30A. In practice, silicon nitride can be removed without appreciably attacking silicon dioxide or polysilicon by exposure to H₃PO₄ solvent at a temperature of 165°C. After the silicon nitride mask is removed, a block mask is deposited over the n-channel devices, and the exposed polysilicon within the exposed vias is implanted with p-type impurity. Then a second block mask (the complement of the first block mask) is defined, and the exposed polysilicon is implanted with an n-type dopant. Thus, the dual work-function implants are carried out after the polysilicon has been patterned and after the silicon nitride mask is removed. If the implants were carried out before the polysilicon was patterned, the resulting n and p doped polysilicon regions would subsequently etch at different rates. If the implants were carried out after patterning, the high implant energy required to penetrate the silicon nitride mask may result in the undesired doping other structures. Finally, metal 30B is deposited and defined (as needed) to strap the FET gate electrode. It is preferred to form metal layer 30B of selective tungsten. Under conditions discussed in an article by Foster et al, entitled "Selective Tungsten Deposition In a Varian/Torrex Cold Wall CVD Reactor," Tungsten and Other Refractory Metals for VLSI II , (Conference Proceedings, Nov. 12-14, 1986), pp. 147-155, tungsten can be chemically vapor deposited such that it only grows on silicon. Thus, tungsten can be grown to fill the space that was previously defined by nitride mask 40A. Such a procedure eliminates the need to etch back the deposited metal. One alternative is to first deposit a thin barrier layer (such as titanium/tungsten or titanium nitride) and then deposit a metal such as aluminum. The barrier layer would prevent spiking of the aluminum through the underlying polysilicon portion 30A. Portions of the Ti/W and aluminum layers lying above conformal layer 90 could then be removed by conventional photoresist planarization and etchback techniques. Thus, the process of the invention provides an FET device having a low sheet resistance gate electrode as well as silicide source and drain electrodes. By the method of the invention, the tungsten component of the tungsten-polysilicon composite gate electrode is not introduced until after the hot process steps associated with the source/drain dopant diffusion and silicide formation steps are carried out. Thus tungsten (which normally forms a silicide with silicon at a temperature of approximately 600°C) will not interact with the underlying polysilicon to form a silicide, greatly decreasing the sheet resistance of the composite gate electrode. Another advantage of the invention is that the final structure is planar as between the final gate electrode and the surrounding conformal oxide layer. Thus, when a passivating oxide layer is subsequently deposited on the formed device, there is no need to reflow the passivation layer so as to form a planar upper surface. Conventionally, this reflow step is carried out at a temperature of 800-1000°C. Thus, the invention further reduced the risk of silicide gate formation by eliminating a subsequent hot process step that is normally carried out in conventional device fabrication processes, while also providing an FET device that is more compatible with multiple levels of metal. Another advantage of the present invention is that the metal on top of the polysilicon does not allow intermixing of the dual work function polysilicon dopants. Thus, the invention provides a low sheet resistant gate electrode that is compatible with dual work function CMOS polysilicon gate technology.

Claims: A process of forming a planarized, metal-strapped polysilicon gate FET, comprising the steps of: defining a gate stack on an exposed surface of a semiconductor substrate, said gate stack including a gate mask disposed on top of a patterned polysilicon layer; defining first and second diffusion regions in said substrate having first and second silicide electrodes formed thereon by refactory metal deposition and subsequent annealing, said first and second diffusion regions being self-aligned to said gate stack and forming source and drain electrodes of said FET, said gate mask preventing silicide formation over said polysilicon layer; depositing an insulating layer on said substrate, said insulating layer having a thickness substantially equal to that of said gate stack; planarizing said insulating layer so as to expose an upper surface of said gate mask; removing said gate mask to define an aperture in said insulating layer that exposes said polysilicon layer; and depositing a low sheet resistance conductive material on said substrate to at least partially fill said aperture in said insulating layer so as to form a gate electrode of said FET that is relatively co-planar with said planarized insulating layer. The process as recited in Claim 1, further comprising, prior to said step of defining a gate stack, the step of: defining isolation regions in said surface of said semiconductor substrate, said isolation regions having an upper surface that is relatively co-planar with said exposed surface of said semiconductor substrate. The process as recited in Claim 1, wherein said step of defining said gate stack comprises the steps of: forming a thin dielectric structure on said surface of said substrate; depositing a layer of doped polysilicon on said thin dielectric structure; depositing a masking layer on said doped polysilicon layer; patterning said masking layer to define said gate mask; and removing portions of said doped polysilicon layer exposed by said gate mask. The process as recited in Claim 3, wherein said dielectric structure is comprised of a material selected from the group consisting of silicon oxide, silicon nitride, and silicon oxynitride. The process as recited in Claim 3, wherein said mask layer is comprised of silicon nitride. The process as recited in Claim 2, wherein said step of defining first and second diffusion regions and first and second silicide electrodes comprises the steps of: implanting dopant ions into portions of said substrate exposed by said gate mask and said isolation regions; annealing said substrate to diffuse said implanted dopant ions therein; depositing a layer of refractory metal on said surface of said substrate; annealing said substrate to form silicides in portions of said refractory metal that contact said semiconductor substrate; and removing remaining portions of said refractory metal layer without appreciably attacking said silicide regions. The process as recited in Claim 6, further comprising, prior to said step of implanting dopant ions into said substrate, the step of: selectively growing epitaxial silicon on portions of said semiconductor substrate exposed by said gate stack and said isolation regions. The process as recited in Claim 6, wherein said refractory metal comprises titanium. The process as recited in Claim 2, wherein said step of defining said first and second diffusion regions comprises the steps of: depositing a layer of refractory metal on said semiconductor substrate; annealing said semiconductor substrate in order to form metal-rich silicide regions in portions of said refractory metal layer disposed on exposed portions of said semiconductor surface; removing remaining portions of said refractory metal layer without appreciably attacking said metal-rich silicide regions; implanting dopant ions into said metal-rich silicide regions; and annealing said substrate so as to diffuse said dopant ions from said metal-rich silicide regions into underlying portions of said semiconductor substrate while converting said metal-rich silicide regions into silicon-rich silicide regions. The process as recited in Claim 9, further comprising, prior to said step of depositing said refractory metal, the step of: selectively growing epitaxial silicon on portions of said semiconductor substrate exposed by said gate stack and said isolation regions. The process as recited in Claim 9, wherein said refractory metal is comprised of cobalt. The process as recited in Claim 1, wherein said insulating layer is comprised of a conformal layer of silicon oxide. The process as recited in Claim 12, wherein said step of planarizing said insulating layer comprises physically polishing said insulating layer in the presence of an abrasive slurry. The method as recited in Claim 12, wherein said step of planarizing said insulating layer comprises depositing a planarizing layer on said insulating layer, and exposing said substrate to an etchant which removes said planarizing layer and said insulating layer at substantially the same rate. The process as recited in Claim 1, wherein said step of removing said gate mask comprises exposing said substrate to H₃PO₄. The process as recited in Claim 1, wherein said conductive material is selectively deposited only on an exposed surface of said polysilicon layer. The process as recited in Claim 1, wherein said first and second diffusion regions extend less than 0.5 micrmeter into said substrate. A process of forming metal-strapped polysilicon gate CMOS transistors, comprising the steps of defining well regions of a second conductivity type in a surface portion of a substrate of a first conductivity type; defining planarized isolation regions in said substrate; defining gate stacks on said well regions and on the remaining portions of said substrate, respectively, said gate stack comprising a layer of silicon nitride disposed on a doped polysilicon layer; defining first and second diffusion regions of said first conductivity type on either side of said gate stacks formed on said well regions of said substrate, and defining first and second diffusion regions of said second conductivity type on either side of said gate stacks formed on remaining portions of said substrate; forming silicide electrodes on said diffusion regions by refractory metal deposition and subsequent annealing, said silicon nitride layer preventing silicide formation on said polysilicon layer; depositing an insulator layer on said substrate to cover said gate stack; planarizing said insulator layer to expose said silicon nitride layer; removing said silicon nitride layer to define apertures in said insulator layer that expose said polysilicon layer; implanting portions of said polysilicon layer disposed on said well region of said substrate with a dopant of said first conductivity type; implanting portions of said polysilicon layer disposed on remaining portions of said substrate with a dopant of said second conductivity type; and selectively depositing a conductor material on said polysilicon layer to substantially fill said apertures in said insulator layer.

Inventors: ABERNATHEY, JOHN ROBERT, CRONIN, JOHN EDWARD, LASKY, JEROME BRETT
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1988
Main classification: H01L21
IPC codes: H01L21, H01L23, H01L29