PROCESS FOR THE PRODUCTION OF FORMED ARTICLE OF AROMATIC VINYL RESIN

Abstract: A process for the production of formed articles of aromatic vinyl resin having a small birefringence and a high refractive index by a cast polymerization rapidly and with productivity, said formed articles of aromatic vinyl resin being light and useful for the production of various optical elements such as lenses and prisms.

Description: This invention relates to a process for the production of a formed article of an aromatic vinyl resin. More particularly, it relates to a process for the production of a formed or shaped article (e.g. various lenses, prisms, etc.) of a resin having a small birefringence and a high refractive index by a cast polymerization process rapidly and with high productivity. Prior Art Optical elements such as lenses and prisms have hitherto been mainly prepared from glass, but glass has such disadvantages that it is heavy and easily broken, and hence, there is recently a remarkable tendency to use plastics instead of glass. There are known clear plastic materials such as polymethyl methacrylate, polydiethylene glycol bisallylcarbonate (a tradename: CR 39), but these plastic materials are still disadvantageous in that they have less refractive index than glass while they are excellent in clearness and lightness. It is also known that resins having high refractive index can be formed into lenses, etc. having very thin thickness, which is advantageous in that an article can be made compact. The articles are also advantageous in spherical aberration, etc. Accordingly, recent investigators have intensively studied with resins having high refractive index. A representative example of the known resins having high refractive index is polystyrene (refractive index = 1.59). However, in view of the high refractive index, the polystyrene is hard to form into an optical element having excellent optical properties by an injection molding. On the other hand, according to cast polymerization process which is usually applied to polymethyl methacrylate and polydiethylene glycol bisallylcarbonate resin, there can be produced an optical element having less birefringence. However, this polymerization process can merely be applied to a monomer such as methyl methacrylate which can be polymerized with high polymerization speed, or to a monomer such as diethylene glycol bisallylcarbonate which is accompanied with crosslinking reaction during the polymerization thereof, but is hardly applied to an aromatic vinyl monomer such as styrene which is polymerized with lower polymerization speed. Accordingly, this polymerization process has rarely been used for such aromatic vinyl monomers. It is disclosed in L. E. Coleman et al, Journal of Polymer Science, vol. 38, 241, 1959 that an aromatic vinyl monomer (e.g. styrene, etc.) and a maleimide monomer have an alternating copolymerizability of 1 : 1. It is also reported in Japanese Patent First Publication (Kokai) Nos. 93091/1979 and 162616/1983 that a copolymer of an aromatic vinyl monomer and a maleimide monomer is produced by reacting them with adding the meleimide monomer intermittently or continuously to obtain a copolymer having homogeneous component. Japanese Patent First Publication (Kokai) No. 166807/1986 discloses a process for the production of a copolymer of an aromatic vinyl monomer, a maleimide and an unsaturated dicarboxylic anhydride which is used as a matrix material for glass fiber-reinforced conjugate products. Japanese Patent First Publication (Kokai) No. 207910/1984 discloses a copolymer of bromostyrene and bromophenyl-maleimide which is used as a fire retardant additive for thermoplastic resins. Japanese Patent First Publication (Kokai) No. 171708/1986 discloses a copolymer of an aromatic vinyl monomer and a maleimide as well as methyl methacrylate which is used as a resin for optical elements. Japanese Patent First Publication (Kokai) No. 278509/1986 discloses a copolymer of an aromatic vinyl monomer and a maleimide which is used as a resin for optical disc substrates. Summary Description of the Invention The invention provides a process for the production of a formed or shaped article of a resin having small birefringence and high refractive index. By the process of the invention formed or shaped articles are prepared by a rapid polymerization of an aromatic vinyl monomer which has originally a low polymerization speed. Detailed Description of the Invention This invention provides a process for producing a formed or shaped article, such as optical elements including lenses and prisms, of an aromatic vinyl resin, which comprises copolymerizing an aromatic vinyl monomer, a maleimide monomer of 0.1 to 1.5 mole per mole of the aromatic vinyl monomer, and a polyfunctional monomer having two or more radically polymerizable vinyl or vinylidene groups with the molecule of 1 to 30 % by weight based on the weight of whole monomers in the presence of a radical polymerization initiator by a cast polymerization technique. The aromatic vinyl monomer used in this invention includes compounds having a carbon-carbon double bond which binds directly to the aromatic ring which are effective for giving the resulting resin the desired high refractive index. Suitable examples of the aromatic vinyl monomer are styrenes (e.g. styrene, -methylstyrene, o-methylstyrene, m-methylstyrene, p-methylstyrene, monomethoxystyrene, monochlorostyrene, dichlorostyrene, trichlorostyrene, monobromostyrene, dibromostyrene, tribromostyrene, iodostyrene and p-(trimethylsilyloxy)styrene); polycyclic hydrocarbon aromatic vinyl compounds (e.g. vinylnaphthalene and vinylanthracene); heterocyclic vinyl compounds (e.g. N-vinylcarbazole, vinylfuran and vinylpyridine). Among them, styrenes are preferable in view of the easier handling and easier purification. These aromatic vinyl monomers may be used alone or in combination of two or more thereof. The aromatic vinyl monomer is copolymerized in an amount of 35 to 95 % by weight, preferably 45 to 90 % by weight, based on the weight of the whole monomer mixtures. The maleimide monomer is used for the purpose of promoting the polymerization of the aromatic vinyl monomer by using together with the aromatic vinyl monomer. Suitable examples of the maleimide monomer are maleimide, aliphatic monomaleimides (e.g. N-methylmaleimide, N-ethylmaleimide, N-isopropylmaleimide, N-butylmaleimide and N-laurylmaleimide), alicyclic monomaleimides (e.g. N-cyclohexylmaleimide and N-cyclopentylmaleimide), aromatic monomaleimides (e.g. N-phenylmaleimide, N-(2-methylphenyl)maleimide, N-(4-methylphenyl)maleimide, N-(2-chlorophenyl)maleimide, N-(2-methoxyphenyl)maleimide, N-xylylmaleimide and N-(2,4,6-trichlorophenyl)maleimide), bismaleimides having no aromatic ring (e.g. N,N'-sulfonbismaleimide and N,N'-etherbismaleimide), aromatic ring bismaleimides (e.g. m-tolylenebismaleimide, N,N'-m-phenylenebismaleimide and N,N'-diphenylmethanebismaleimide). Among these maleimides, aromatic monomaleimides and alicyclic monomaleimides are preferable in view of the excellent solubility to other monomers, giving high refractive index to the resin, and high polymerization speed. Particularly, 2-substituted phenylmaleimides, such as N-(2-chlorophenyl)maleimide and N-(2-methoxyphenyl)maleimide, and alicyclic monomaleimides are more preferable as no coloring of resin results from the use of these monomers. These maleimide monomers may be used alone or in combination of two or more thereof. The maleimide monomers are used in an amount of 0.1 to 1.5 mole, preferably 0.2 to 1.0 mole, per mole of the aromatic vinyl monomer, in view of the excellent strength and refractive index of the desired resin. When the amount of the maleimide monomers is over 1.5 mole, the monomer mixture is not always a homogeneous liquid at room temperature and gives an undesirable brittle resin. On the other hand, when the amount of the maleimide monomers is less than 0.1 mole, the polymerization reaction proceeds at an undesirably low speed. The polyfunctional monomer having two or more radically polymerizable vinyl or vinylidene groups within the molecule is effective for enhancing the strength of the resin. Suitable examples of the polyfunctional monomer are phthalic acid derivatives (e.g. bis(2-methacryloyloxyethyl) phthalate, bis(2-methacryloyloxyethyl) tetrabromophthalate, etc.), aliphatic polyol (meth)acrylate derivatives (e.g. neopentylglycol dimethacrylate, hexanediol dimethacrylate, glycelol dimethacrylate, trimethylolpropane triacrylate and pentaerythritol tetraacrylate), (meth)acrylate derivatives having (poly)ethylene glycol chain (e.g. ethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, nonaethylene glycol dimethacrylate and nonaethylene glycol diacrylate), bisphenol A derivatives (e.g. 2,2-bis(4-methacryloyloxyphenyl)propane, 2,2-bis(4-acryloyloxyphenyl)propane, 2,2-bis[4-(2-methacryloyloxyethoxy)phenyl]propane, 2,2-bis[4-(3-methacryloyloxy-2-hydroxypropyloxy)phenyl]propane and 2,2-bis[3,5-dibromo-4-(2-methacryloyloxyethoxy)phenyl]propane), isocyanuric acid - tris(2-hydroxyethyl methacylate), and the like. Among these, those compounds having at least one hydroxyl group in the molecule, such as glycelol dimethacrylate or 2,2-bis[4-(3-methacryloyloxy-2-hydroxypropyloxy)phenyl]propane, are preferable because they are more effective for enhancement of the strength of the resin. The polyfunctional monomers are used in an amount of 1 to 30 % by weight, preferably 5 to 20 % by weight, based on the weight of the whole monomer mixture. When the amount of the polyfunctional monomers is less than 1 % by weight or over 30 % by weight, the enhancement the strength of the resin is undesirably inferior. In addition to the aromatic vinyl monomer, maleimide monomer and polyfunctional monomer, there can also be incorporated a copolymerizable, radical polymerizable monomer. The copolymerizable, radical polymerizable monomer includes, for example, methacrylates (e.g. methyl methacrylate, ethyl methacrylate, benzyl methacrylate, phenyl, methacrylate, cyclohexyl methacrylate, bornyl methacrylate, dicyclopentanyl methacrylate, 2,3-dibromopropyl methacrylate, monobromophenyl methacrylate, dibromophenyl methacrylate and tribromophenyl methacrylate), acrylates (e.g. methyl acrylate, ethyl acrylate and n-butyl acrylate), unsaturated acids (e.g. methacrylic acid and acrylic acid), unsaturated acid anhydrides (e.g. maleic anhydride and citraconic anhydride). The radical polymerization initiator includes known various initiators. Suitable examples are azo polymerization initiators (e.g. azobisisobutyronitrile and azobiscyclohexanecarbonitrile), peroxide polymerization initiators (e.g. lauroyl peroxide, benzoyl peroxide, dicumyl peroxide, di-t-butyl peroxide, t-butyl peroxybenzoate, t-butyl hydroperoxide and methyl ethyl ketone peroxide). In the process of the invention, even when each of the above radical polymerization initiators is used alone, the polymerization proceeds fairly rapidly, but in order to cause the polymerization to proceed more rapidly, it is preferable to use a redox polymerization initiator which consists of a combination of the above peroxide polymerization initiator with a reducing compound, or a known peroxide/metallic ion polymerization initiator which consists of a combination of the above peroxide polymerization initiator with a matallic ion which is effective as a polymerization promoter. Particularly, a redox polymerization initiator is preferable. The reducing compound used in combination of the peroxide polymerization initiator for the redox initiator includes compounds which dissolve in the monomer mixture, for example, tertiary amines (e.g. N,N-dimethylaniline and N,N-dimethyl-p-toluidine), aldehydes (e.g. formaldehyde and acetaldehyde), trivalent phosphur compounds such as phosphites (e.g. trimethylphosphite and triethylphosphite), sulfinic acid or derivatives thereof (e.g. p-toluenesulfinic acid and p-toluenesulfinic acid esters), thioureas (e.g. tetramethylthiourea and dibutylthiourea), mercaptans (e.g. laurylmercaptan, t-dodecylmercaptan, 2-ethylhexyl thioglycolate, octylmercaptan, n-butylmercaptan, pentaerythritol tetrathioglycolate, glycol dimercaptoacetate, glycol dimercaptopropionate, trimethylolpropane trismercaptopropionate, 2-mercaptoethanol and its esters and β-mercaptopropionic acid and its esters). The peroxide polymerization initiator and the reducing compound are used in a ratio of 0.05 to 5 equivalents of the reducing material to 1 equivalent of the peroxide initiator wherein the equivalent means oxidation-reduction equivalent. When the ratio is less than 0.05 or more than 5, the desired rapid occurrence of radical becomes disadvantageously less effective. In addition to the reducing compound, there may be used other conventional polymerization promoting agents such as amines, amine hydrohalides, quaternary ammonium halides and metal-containing compounds. These agents are used for promoting the polymerization reaction. The radical polymerisation initiator is usually used in an amount of 0.001 to 5 % by weight, preferably 0.01 to 2 % by weight, based on the weight of whole monomer mixture. In the process of this invention, there may also be used any other conventional materials for improving the properties of the resin formed article having high refractive index, such as conventional ultraviolet absorbents and antioxidants. Moreover, in order to prevent undesirable rough surface of the formed article due to releasing from the mold during the cast polymerization, there may be used a conventional release-preventing agent. The cast polymerization in this invention can be carried out by using a mold made of glass, metal, and any other materials and having various shapes such as plate-like, lens-like, cylindrical, spherical shapes, which are designed depending on the utilities. The polymerization is carried out by pouring the starting mixture comprising the monomer mixture and a radical polymerization initiator into the mold and subjecting to polymerization reaction optionally with heating and/or under pressure, by which the formed article of the polymer is directly produced. In the process, when the radical polymerization initiator is added, the polymerization reaction starts. Accordingly, when the radical polymerization initiator is mixed with the monomers, the mixture should be poured into the mold as soon as possible. The method for mixing and pouring is conveniently carried out in the following manner: When a redox initiator is used as the radical polymerization initiator, the redox polymerization initiator may be added to the monomer mixture, but it is preferable that the monomer mixture is divided into two parts, and a peroxide is mixed with one part of the monomer mixture and a reducing compound is mixed with other part of the monomer mixture, or alternatively, a peroxide is mixed with any one or more of the monomers and a reducing compound is mixed with the remaining monomer(s), and immediately before pouring into the mold, both mixtures are mixed. In the mixing of the monomers, when the maleimide monomer is added to the aromatic vinyl monomer, the polymerizability is enhanced. Particularly, when both monomers are used in approximately equimolar amount, the polymerizability is significantly enhanced, and hence, in such a case, each monomer is kept separately, and the polymerization initiator is added to either one or both of the monomers, and immediately before pouring into the mold, both are mixed. The above mixing procedure is preferably carried out at a temperature of 50°C or or lower within a short period of time such as within 10 minutes. When the mixing is carried out at a temperature of higher than 50°C, the polymerization reaction proceeds undesirably partly during mixing procedure. Besides, when the mixing procedure is carried out in a longer period of time, the polymerization reaction proceeds undesirably during the mixing procedure, too. Thus, if the mixing is well effected, the mixing time should be as short as possible. The mixing procedure can be done by batch system for producing of a small amount of small formed articles, but is preferably carried out by continuous system for producing large formed articles or a large amount of formed articles with a plurality of molds. The continuous mixing can be carried out by a conventional mixing method using a dynamic mixer or a static mixer. The cast polymerization may be carried out at room temperature but is preferably carried out at a temperature of 50 to 150°C. The polymerization reaction may proceed by charging the materials to be polymerized into a mold and heating at a fixed temperature, or may be carried out by charging the materials to be polymerized into a mold which is previously heated at a fixed temperature. Besides, the polymerization reaction may be carried out under atmospheric pressure, but is optionally carried out under pressure in order to prevent undesirable sink marks or voids due to polymerization shrinkage or undesirable foams due to exothermic polymerization heat. The formed articles of this invention are useful for producing various optical elements, particularly optical elements having a large refractive index, such as various lenses (e.g. lens for glasses, lens for camera, pickup lens and Fresnel lens), and various prisms. The invention is illustrated by the following Examples and Reference Examples but should not be construed to be limited thereto. In the Examples and Reference Examples, various properties were measured by the following methods. (1) Birefringence (n D ) and Abbe number (ν D ): These were measured with Abbe refractometer (manufactured by Shimadzu Seisakusho, Japan) at 25°C, wherein monobromonaphthalene was used as a contacting liquid. (2) Total light transmittance (Tt): It was measured according to ASTM D-1003 by using an integrating sphere type haze meter (type SEP-H-2D, manufactured by Nippon Seimitsu Kogaku K.K., Japan). (3) Flexural strength: It was measured according to ASTM D-790 by using an autograph (manufactured by Shimadzu Seisakusho, Japan). (4) Specific gravity: It was measured by placing the test sample in water in accordance with JIS K-6911. (5) Birefringence: The molded article was put between two polarizing films which were set so that the polarized light direction is in crosswise direction. The data were evaluated as follows. Bad: article appeared wholly white and bright owing to birefringence. No good: article appeared partly white and bright. Good: article appeared almost not white and bright. Example 1 A stainless vessel (2 liter volume) was charged with styrene (630 g), N-cyclohexylmaleimide (270 g), 2,2-bis[4-(3-methacryloyloxy-2-hydroxypropyloxy)phenyl]propane (100 g), t-butyl peroxybenzoate (20 g), and dimethyloctylamine hydrochloride (1.2 g) to give a homogeneous starting liquid (X). Other stainless vessel was charged with styrene (630 g), N-cyclohexylmaleimide (270 g), 2,2-bis[4-(3-methacroyloxy-2-hydroxypropyloxy)phenyl]propane (100 g), glycol dimercaptoacetate (12 g), and copper naphthenate (copper content: 10 % by weight, 0.008 g) to give a homogeneous starting liquid (Y). The starting liquid (X) (about 250 g) and the starting liquid (Y) (about 250 g) were charged into a dynamic mixer with a pump and mixed therein in a mean retention time of 30 seconds and then the resulting mixture was poured into a stainless frame (350 x 350 x 3 mm) which was kept at 85°C. Two minutes after completion of the pouring, the temperature within the frame became maximum. After the temperature lowered to 85°C, the formed product was released from the frame. The formed product thus obtained showed light transmittance (Tt): 86 %, birefringence (n D ): 1.567, Abbe number (ν D ): 34, flexural strength: 870 kg/cm², specific gravity: 1.12, and showed good birefringence and good surface state. Examples 2 to 13 and Reference Examples 1 to 3 In the same manner as described in Example 1 except that the components as shown in Table 1 were used, the polymerization reaction was carried out. The results are shown in Table 2. Example 14 A stainless vessel (200 ml volume) was charged with styrene (63 g), N-cyclohexylmaleimide (27 g), and 2,2-bis[4-(3-methacryloyloxy-2-hydroxypropyloxy)phenyl]propane (10 g) to give a homogeneous liquid. To the liquid was added azobisisobutyronitrile (0.15 g) to give a homogeneous starting liquid. The starting liquid was poured into a stainless frame (160 x 160 x 3 mm) which was kept at 85°C and then subjected to polymerization reaction at 85°C on a warmed bath. About 9 minutes after initiation of the polymerization reaction, the temperature within the frame became maximum. After the temperature lowered to 85°C, the formed product was released from the frame. The formed product thus obtained showed light transmittance (Tt): 90 %, birefringence (n D ): 1.573, Abbe number (ν D ): 34, flexural strength: 810 kg/cm², specific gravity: 1.11, and showed good birefringence and good surface state. Example 15 and Reference Example 4 In the same manner as described in Example 14 except that the components as shown in Table 1 were used, the polymerization reaction was carried out. The results are shown in Table 2. The peak time in Table 2 means a time of from pouring of the starting liquid into the frame till becoming maximum temperature within the frame. According to this invention, the desired formed article having high strength can be produced from an aromatic vinyl resin having high refractive index rapidly and with high productivity. The thus produced formed article of a resin having high refractive index has a specific gravity of about 1.10 to 1.25 and hence is lighter than glass (specific gravity: about 2.5), and further, the formed article has low birefringence. Accordingly, the formed article of this invention has excellent properties suitable for producing various optical elements such as lenses and prisms.

Claims: A process for producing a formed or shaped article, such as optical elements including lenses and prisms, of an aromatic vinyl resin, which comprises copolymerizing an aromatic vinyl monomer, a maleimide monomer, in an amount of 0.1 to 1.5 mole per mole of the aromatic vinyl monomer, and a polyfunctional monomer having two or more radically polymerizable vinyl or vinylidene groups within the molecule, in an amount of 1 to 30 % by weight based on the weight of whole monomer mixture, in the presence of a radical polymerization initiator by a cast polymerization technique. A process according to claim 1, wherein the aromatic vinyl monomer is polymerized in an amount of 35 to 95% by weight based on the weight of the whole monomer mixture. A process according to claim 1 or claim 2, wherein the aromatic vinyl monomer is selected from the group consisting of styrenes, polycyclic hydrocarbon aromatic vinyl compound and heterocyclic vinyl compound, the maleimide monomer is selected from the group consisting of maleimide, aliphatic monomaleimides, alicyclic monomaleimides, aromatic monomaleimides, bismaleimides having no aromatic ring, and aromatic ring bismaleimides, and the polyfunctional monomer is selected from the group consisting of phthalic acid derivatives, aliphatic polyol (meth)acrylate derivatives, (meth)acrylate derivatives having (poly)ethylene glycol chain, bisphenol A derivatives, isocyanuric acid - tri(2-hydroxyethyl methacrylate). A process according to claim 3, wherein the aromatic vinyl monomer is a styrene compound, the maleimide monomer is selected from aromatic monomaleimides and alicyclic monomaleimides, and the polyfunctional monomer is selected from glycerol dimethacrylate and 2,2,-bis[4-(3-methacryloyloxy-2-hydroxypropyloxy)phenyl]propane. A process according to any one of the preceding claims, wherein the radical polymerization initiator is used in an amount of 0.001 to 5 % by weight based on the weight of whole monomer mixture. A process according to any one of the preceding claims, wherein the cast polymerization is carried out by pouring the starting monomer mixture and radical polymerization initiator into a mold and subjecting to polymerization reaction optionally with heating and/or under pressure. A process according to claim 6, wherein the monomers to be copolymerized and the polymerization initiator are mixed before pouring into the mold. A process according to any one of the preceding claims, wherein the radical polymerization initiator is a redox polymerization initiator consisting of a peroxide polymerization initiator and a reducing compound. A process according to claim 8, wherein the peroxide initiator is mixed with one part of the monomer mixture and the reducing compound is mixed with other part of the monomer mixture and both mixtures are mixed immediately before pouring into the mold. A process according to either claim 8 or claim 9, wherein the peroxide initiator is mixed with any one or more of the monomers and the reducing compound is mixed with the remaining monomer, and both mixtures are mixed immediately before pouring into the mold. A process according to any one of claims 6 to 10, wherein the cast polymerization reaction is carried out at a temperature of 50 to 150°C and optionally under pressure.

Inventors: FUJITA, TAKANORI, MORITANI, MASAHIKO, NIWANO, MASAHIRO, YOKOO, KAZUHIRO
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1988
Main classification: C08F212
IPC codes: C08F2, C08F222, C08F20, G02B1, C08F212, C08F214, C08F22, C08F220