METHOD OF CUTTING A MEMBRANE

Abstract: An organic membrane (2) is stretched over, or adhered to, a frame (3) or a substrate, and that part of the membrane (2) which extends out of the frame (3) or substrate is cut by bringing an injection syringe-like needle (1) into contact with, or approach to, the lateral end surface of the frame (3) or substrate and while moving the needle (1) along said lateral end surface, injecting an organic solvent from the needle (1) and dissolving said membrane (2) along the lateral end surface of the frame (3) or substrate. By this method, the organic membrane (2) can be cut without generating foreign matter such as cut dust.

Description: This invention relates to a method of cutting an organic membrane, and more specifically, to a method of cutting an organic membrane which comprises adhering or intimately adhering (to be referred to simply "adhering") the organic membrane to a frame or substrate and then cutting that part of the organic membrane which extends out of the frame or substrate (to be sometimes referred to as the frame or the like) along the frame or the like without generating foreign matter such as cut dust. One example of an organic membrane to be adhered to a frame or the like is a pellicle used as a dust-preventing cover for a photomask or a reticle. Generally, the pellicle is obtained by taking up on a provisional frame a thin film of nitrocellulose or ethyl cellulose, for example, formed on a glass plate by a spinner method or a pull-up method (by pulling up from a solution), then stretching the thin film over a pellicle frame, and cutting that part of the film which extends out of the frame along the frame. Cutting is usually effected by a knife, but laser may sometimes be used. In any case, cut dust inevitably occurs in knife cutting, and occurrence of burnt dust is inevitable in laser cutting. Such dusts, even minute ones can be a problem in the process of producing semiconductor devices, above all in fields requiring rigorous dust-preventing measures, for example in a step of exposing resists. If, for example, the cut dust adheres to the pellicle, it is likely to fall at the time of mounting the pellicle on the reticle and to adhere to the circuit pattern. This may lead to the production of devices having unacceptable quality. FR-A-2386494 on which the pre-characterizing portion of claims 1 and 2 are based discloses a method of cutting a laminate of glass layers separated by plastic in which the plastic is cut while hot by dissolving with solvent. According to this invention, there is provided a method of cutting a membrane by applying a solvent to the membrane along the desired line of the cut to dissolve the membrane along the line of the cut, characterized in that the solvent is applied by ejecting it from a syringe needle passed through the membrane at the start of the cut and moved in this position along the line of the cut at such a speed in relation to the rate of dissolving of the membrane that it tends not to contact the membrane directly. The present invention correspondingly further provides apparatus for performing such a method characterized by a syringe including a syringe needle for applying the solvent to the intended line of the cut, means for passing the needle through the membrane at the start of the cut and means for moving the needle in that position along the line of the cut at such a speed in relation to the rate of dissolving of the membrane that it tends not to contact the membrane directly. The present invention also provides a method of producing a device comprising a frame or a substrate and a membrane adhered to, or intimately adhered to, the frame or a substrate, whereby that part of the membrane adhering to the frame or substrate which extends out beyond the frame or substrate is cut-off using the method claimed in claim 1 characterised by passing the syringe needle through the membrane so that it is in contact with, or close to, the lateral end surface of the frame or substrate and moving it in this position along said lateral end surface whereby the membrane is cut along the frame by dissolving. According to the method of this invention, that part of the organic membrane adhering to the frame or the like which extends beyond the frame or the like is cut by the organic solvent ejected from the needle moving along the lateral end surface of the frame or the like. Hence foreign matter such as cut dust is not produced during cutting, and the method of the invention is suitable for use in fields requiring rigorous dust control, for example in the process of exposing resists in the production of semiconductor devices. The invention will be further described with reference to the accompanying drawings, in which: Figure 1 shows a first embodiment of the method of this invention, in which a needle 1 is pierced through a pellicle 2 from above or put through it while perforating it with an organic solvent dropped from the tip of the needle and then kept along the lateral end surface of a pellicle frame 3 with a suitable clearance permitting occurrence of a capillary phenomenon, and by moving this needle, the pellicle 2 is cut along the frame by the effect of the organic solvent injected from the needle. Figure 2 shows a second embodiment, in which the needle 1 is put obliquely through the pellicle 2, and moved along the lateral end surface of the frame while its tip is in approach to the lateral end surface of the frame with a suitable clearance, or in contact with the lateral end surface of the frame, thereby cutting the pellicle 2 along the frame. Figure 3 shows a third embodiment, in which the needle 1 is put obliquely through the pellicle 2 from the site of contact between the pellicle frame 3 and the pellicle 2, and is moved inclinedly with the frame 3 used as a fulcrum thereby effecting cutting of the pellicle 2 along the frame. Desirably, the organic solvent used in this invention has a low viscosity of not more than about 4 cP so that it can rapidly reach the surface of the membrane. The organic solvent may be chosen depending upon the kind of the organic membrane to be cut. For example, if the organic membrane is composed of nitrocellulose, acetone, methyl isobutyl ketone (MIBK) and butyl acetate, for example, are conveniently used as the organic solvent. If it is formed of ethyl cellulose, solvents having a boiling point of about 40 to 150°C, such as toluene, are suitably used to avoid volatilization that may occur before the solvent reaches the membrane surface at room temperature. Use of high-boiling organic solvents is likely to result in a situation in which the solvents remain in the organic membrane and exert deleterious effects. Some examples of the method of cutting a pellicle in the process of producing devices provided with pellicles will be described with reference to the accompanying drawings. In the first example shown in Figure 1, needle 1 is pierced through pellicle 2 from above, or put through the pellicle 2 while perforating it with an organic solvent trickled down from the needle tip. The needle is kept along the lateral end surface of pellicle frame 3 with a suitable clearance provided between them so as to permit occurrence of a capillary phenomenon. By the capillary phenomenon, the organic solvent injected from the tip of the needle or from a suitable site of the needle is caused to rise along the clearance and make contact with the membrane surface. While the membrane is thus dissolved with the solvent, the needle 1 is moved along the lateral end surface of the frame while the above clearance is maintained in a direction at right angles to the sheet surface in Figure 1. As a result, the pellicle is cut along the frame. In this embodiment, the needle 1 is kept along the lateral end surface of the pellicle frame with a suitable clearance between them. If desired, the needle 1 may be kept in intimate contact with the pellicle frame without providing such a clearance. In this alternative, part of the organic solvent injected from the needle 1 flows down along the lateral end surface of the frame. Furthermore, while the needle moves in contact with the lateral end surface of the frame, deflection may occur in the needle owing to friction with the lateral end surface of the frame or to the finishing of that surface. When the needle deflects, the organic solvent will scatter, and the rising of the solvent may temporarily be stopped. Despite this, since the needle moves while being guided by the lateral end surface of the frame, the cutting of the membrane along the frame can advantageously be effected easily and clearly. In the second embodiment shown in Figure 2, needle 1 is obliquely put through pellicle 2 as in the embodiment shown in Figure 1. While the needle tip is brought into contact with the lateral end surface of the frame or into approach to it with a suitable clearance, the needle is moved to cut the pellicle in the same way as in the first example. In the second embodiment, when the needle tip is kept into contact with the lateral end surface of the frame, much the same effect as in the first embodiment is obtained. When it is kept apart from the lateral end surface of the frame, the effect obtained is reverse. In the third embodiment shown in Figure 3, needle 1 is put through pellicle 2 obliquely from the site of contact between pellicle frame 3 and the pellicle 2 in the same way as in the second embodiment. The pellicle 2 is cut by moving the needle is the same way as in the second embodiment while it is inclined with the frame 3 used as a fulcrum. In this embodiment, the organic solvent injected from the needle rises by the capillary phenomenon and does not fall down along the lateral end surface of the frame. Even if the needle happens to deflect during movement and the solvent scatters, the solvent scattered to the frame is liable to adhere to the small space between the needle tip and the lateral end surface of the frame and to propagate to the membrane. Since the needle moves while being guided by the frame, the membrane can be cut easily and clearly. In any of the embodiments described above the needle moves while being pierced through the dissolved membrane. If the moving speed is too fast, mechanical cutting by the needle occurs before cutting by the solvent, and cut dust is generated. If it is too slow, a large amount of the solvent is supplied to the space between the needle and the frame to form a liquid reservoir although this depends upon the amount of the solvent supplied. This may possibly result in cutting undesired parts of the membrane, and no clear cut surface is obtained. Accordingly, the moving speed of the needle should be adjusted to a suitable value. For example, in the case of cutting a nitrocellulose membrane having a thickness of 0.8 to 3 microns, the moving speed of the needle is set usually at 1 to 100 mm/sec., preferably 45 to 10 mm/sec. If the amount of the solvent supplied to the needle is too large, there is a possibility that unwanted parts of the membrane will also be dissolved. If it is small, the membrane cannot be cut by dissolving. The suitable amount of the solvent to be supplied to the needle is usually about 1 x 10⁻⁴ ml/min. to about 1 x 10⁻¹ ml/min., preferably about 5 x 10⁻⁴ ml/min. to about 5 x 10⁻² ml/min.

Claims: A method of cutting a membrane (2) by applying a solvent to the membrane (2) along the desired line of the cut to dissolve the membrane (2) along the line of the cut, characterized in that the solvent is applied by ejecting it from a syringe needle (1) passed through the membrane (2) at the start of the cut and moved in this position along the line of the cut at such a speed in relation to the rate of dissolving of the membrane (2) that it tends not to contact the membrane (2) directly. A method of producing a device comprising a frame (3) or a substrate and a membrane (2) adhered to, or intimately adhered to, the frame (3) or a substrate, whereby that part of the membrane (2) adhering to the frame (2) or substrate which extends out beyond the frame (3) or substrate is cut-off using the method claimed in claim 1 characterised by passing the syringe needle (1) through the membrane (2) so that it is in contact with, or close to, the lateral end surface of the frame (3) or substrate and moving it in this position along said lateral end surface whereby the membrane (2) is cut along the frame (3) by dissolving. A method according to claim 2 characterized in that the needle (1) is so disposed in relation to the lateral end surface of the frame (3) and the membrane (2) that capillary action causes the solvent to flow towards the membrane (2). A method according to any one of the preceding claims characterized in that the membrane (2) is an organic membrane and said solvent is an organic solvent. The method of claim 4 characterized in that the organic membrane (2) is a pellicle. The method of claim 5 characterized in that the pellicle is a nitrocellulose membrane or an ethyl cellulose membrane. Apparatus for performing the method of any one of the preceding claims characterized by a syringe including a syringe needle (1) for applying the solvent to the intended line of the cut, means for passing the needle (1) through the membrane at the start of the cut and means for moving the needle (1) in this position along the line of the cut at such a speed in relation to the rate of dissolving of the membrane (2) that it tends not to contact the membrane directly.

Inventors: FUJIMOTO, MAKOTO, KAYA, TOSHIO
Applicants: MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1988
Main classification: B26F3
IPC codes: B29C63, B26F3, G03F1, B29C67, B29C65, B26D3, B29L9