FRICTION ACTIVATING COMPOSITION FOR ICY SURFACES

Abstract: The composition according to the invention is based on the use of an inert porous material which can be natural, artificial or synthetic, granular in form, and weighing less than 1 kg/dm3 in bulk. The porous granules, e.g. of expanded clay or similar, are partially saturated to the extent of 20 - 30% of their weight, with active ingredients which lower the freezing point of water. The melting additives can be added in the pure state or diluted in water, and there is provision for the addition of about 2% by weight of the melting additive, of anti-­ acid limiters. The advantages of the composition with respect to sand are the greater managability and ease with which it can be spread on icy or snow-bound surfaces; the low specific weight which reduces the tendency to sedimentation in road drains and sewers, and, compared to salt, the almost non-existent corrosive action on ironwork of vehicles and street ironwork. Ecologically, the composition does not damage the natural vegatative environment. The optimum results thus obtained are attributed to the synergetic effect of the inert material (activated grit) and the melting additive incorporated in it.

Description: The present invention concerns a light composition, grit activator, particularly for icy or snow-bound surfaces, with de-icing properties. At present in winter or in snow or icy conditions, de-icing materials e.g. sodium chloride or calcium chloride, are spread to lower the freezing point of water and/or sand to increase the coefficient of friction to a less dangerous level for people and vehicles. It is known that such salts, injurious to the vegetation as well, have the disadvantage of speeding up the corrosion of the mechanical parts of vehicles, as well as the iron fixtures of the pavement such as manhole covers, watercourse liners etc. to such an extent that their use today has been limited or completely forbidden. Sand, on the other hand, because of its high specific weight, tends to accumulate in the pipes of street drains necessitating expensive clearing operations and, when it gets into the sewers, obstructing the normal water flow. Further, because of its weight, sand is a difficult material to transport and handle especially in the private sector and can only be spread with reasonable uniformity by mechanized means. An object of the present invention is to produce a light composition, easily transported and spread, even manually by individual people on, for example, footpaths where mechanized vehicles cannot go, which has simultaneously gritting and de-icing features. According to the invention it is has been surprisingly ascertained that the spreading on an icy surface of expanded clay, preferably reduced to granular size and at least partially soaked with a melting additive, causes an immediate increase in the coefficient of friction even better than that achieved by spreading sand and/or salt, separately or together, on the surface to be treated. The characteristics of lightness and managability, added to the speed and efficiency of action of this composition, have the following advantages: increasing the grip in an area almost three times the size of that covered by an equal weight of simple sand or sand/salt mix; ease of manual spreading since even when partially soaked with melting additives the composition does not show any tendency to agglomerate; actual impossibility to accumulate in drains since the specific weight of the composition, even when saturated with water, remains close to unity and the composition is easily washed through the sewers by the melted ice water; almost non-existent damage to the metal parts of vehicles and street ironwork; the possibility, according to an invention embodiment, of further reducing the attack on the ferrous parts by the addition of a small quantity of anti-acid limiter to the melting additives; the simple soaking of the melting additives in the desired proportions by very simple dispensing devices; particular utility of private use e.g. on doorsteps and entries to houses, on pavements, in areas around schools, public offices and social centres at least as an initial and immediate precaution; ability to be packed in easily transported sacks, with results equal to those of three times the same weight of sand. The materials and their proportions preferably used in the activated grit composition will now be described: The base material of the activated grit is expanded clay with a weight per volume (or apparent weight in bulk) of less than 1kg/dm3 preferably in the range 0.5 - 0.8 kg/dm3. Such material should be reduced to a granular size depending on the requirements and the use, within a variable range of grain size to an illustrative but not limiting maximum size of 6mm diameter. A grain range similar to crushed sand for construction with the following size distribution gave very satisfactory results: about 2% between 4 and 2 mm about 60% between 2 and 0.5 mm about 20% between 0.5 and 0.2 mm about 10% between 0.2 and 0.1 mm the remainder was similar to dust. Expanded clay tested, in the Laboratorio Stradale dell 'Istituto Vie e Transporti del Politecnico di Milano (Road Laboratory of the Roads and Transport Institute of Milan Polytecnic) under conditions which will be described below, gave the following physical results, in a grain size distribution similar to crushed sand as described above: EXPANDED CLAY kg/dm3 Apparent bulk weight in natural humidity of 24% 0.60 As above but soaked with melting additive at 24% on the dry weight 0.75 As above but saturated with water 1.15 In these trials the melting additives were : alcohols; calcium acetate; magnesium acetate; calcium/magnesium acetate; calcium chloride; sodium chloride ; magnesium chloride; glycerine; glycol or polyglycol; natural and synthetic anionic, cationic and non-ionic surface tension agents. These melting additives are used either pure or in solution in an amount of from 5 to 50% by weight. The preferred addition of pure melting additives or melting additives dissolved in water is about 15 - 25% of the base material weight. The proportion of melting additive to water in its turn can vary from 5 to 50% (preferably from 10 to 30%). Anti-acid limiters can be selected from a wide range including: amines and their salts; polyamines and their salts; oxyethylated amines; quaternary salts of ammonia; amphoterics, added in an illustrative proportion of two per thousand of the weight of the base melting additive. The Skid-test conducted by the Road Laboratory of the Milan Polytecnic on a patch of ice with a surface temperature of -10°C (ambient temperature +30°C) gave the following results: pure ice 20 ice spread with sand 30 - 40 ice spread with the composition using expanded clay and melting additives 50 - 60 The variation on the range of values of the device used to measure the radial friction is obviusly influenced by the high ambient temperature. The trials carried out with the materials described above on the basis of expanded clay, distributed according to the grain size similar to that of crushed sand, produced results ranging between the given value limits with different types of melting additives which shows at least that the use of a melting additive, different from salt does not prejudice the results and has the advantage of not having the corrosive action of salt. The data of some of the trials carried out are herein reported : 90% and 80% of the dry inert material with 10% and 20% respectively of sodium chloride in solution; 12% water and 12% ethylene glycol on 100 parts by weight of dry expanded clay; 24% ethylene glycol on 100 parts by weight of dry expanded clay as above. The only difference was in the freezing point of water which was -12°C and -9°C respectively for the 20% sodium chloride and 24% ethylene glycol. The explanation of the unexpected efficiency of the attivation of the friction of the composition according to the invention, resides most probably in the creation of a synergistic effect between the action of the melting additive soaked into each individual grain, which, causing local melting, permits the fixing of the same grains on the frozen surface. The action of the composition is even more sensitive and useful on the dangerous icy mirror-like "verglas" surfaces. Without leaving the area of protection of the present invention it remains understood that the composition described can be used in conjunction with a variable quantity of up to 20% by weight of a heavy inert material such as sand, gravel, or other heavy fillers. The soaking of the expanded clay can be easily achieved either in a mixing drum or by means of a measured spray of melting additive, prepared according to the proportions provided for the solution in water, directly on a conveyor belt fitted with mixing combs or through a hopper.

Claims: A friction activating composition for icy or snow-bound surfaces being composed of expanded clay soaked with a liquid or water soluble ice melting additive and characterised in that it has a final bulk weight between 0.4 and 1.0 kg/dm³. A composition according to Claim 1, characterized in that the bulk weight of the expanded clay in the granular form and in the natural state is between 0.5 and 0.8 kg/dm³. A composition according to claim 1 or 2, characterized in that said expanded clay granulometry has the following general distribution (w/w): 2% from 4 to 2 mm; 60% from 2 to 0,5 mm; 20% from 0,5 to 0,2 mm; 10% from 0,2 to 0,1; 8% below than 0,1 mm. A composition according to claim 1 characterized in that the ice melting additive is selected from: alcohols; calcium acetate; magnesium acetate; calcium/magnesium acetate; calcium, sodium or magnesium chloride; glycerine; glycols or polyglycols; anionic, cationic or non-ionic surface tension agents. A composition according to one of claims 1 to 4, characterized in that said additive comprises at least an anti-acid limiter selected from amines and their salts; polyamines and their salts, oxyethylated amines, ammonium quaternary salts, and amphoterics. A composition according to claims 1 to 4, characterized in that said expanded clay is soaked with 5 - 50 % by weight of pure liquid ice melting additive or with an aqueous solution thereof. A composition according to claims 1 to 6, characterized in that said melting additive is dissolved in water in a proportion varying between 5 and 50% of the water weight. A composition according to claim 6, characterized in that said melting additive is dissolved in water in a ratio within the range from 5 to 30%, of the water weight. A composition according to claim 5, characterized in that said anti-acid limiters are added to the melting additive in the proportion from 0.5 to 10% and preferably from 1.5 to 2.5% by weight of the melting additive. A composition according to any previous claim, further comprising up to 20% (w/w) of heavy inert materials.

Inventors: CANZANI, ALBERTO
Applicants: CANZANI, ALBERTO
Application year: 1988
Main classification: C09K3
IPC codes: C09K3