SYNTHESIS OF ULTRA-HARD ABRASIVE PARTICLES

Abstract: Friable abrasive particles, particularly diamond particles, are produced by causing suitable material, such as a chloride salt, to be occluded in the particles during their manufacture and then removing some of this material, for example, by leaching.

Description: BACKGROUND OF THE INVENTION This invention relates to the synthesis of diamond particles. Diamonds have been synthesized commercially for several decades and the technology is now very well developed. Diamond synthesis involves subjecting a source of non-diamond carbon, particularly graphite, to temperature and pressure conditions in the diamond stable region of the carbon phase diagram in the presence of a diamond solvent (also known as a catalyst). The conditions for diamond synthesis can be tailored to produce diamonds of a particular shape, size and character. SUMMARY OF THE INVENTION According to the present invention, there is provided a method of producing friable diamond particles including the steps of subjecting a reaction mass to temperature and pressure conditions suitable for producing the particles, the reaction mass comprising a source material for producing the diamond particles, a diamond solvent and a non-metallic material capable of being occluded in the ultra-hard abrasive particles so produced and being removed therefrom, recovering the diamond particles from the reaction mass, and removing at least some of the occluded material from the diamond particles. DETAILED DESCRIPTION OF THE INVENTION In the method of the invention for the production of friable diamond particles the source material will be non-diamond carbon, particularly graphite, and the temperature and pressure conditions applied will be in the diamond stable region of the carbon phase diagram. The synthesis will take place in the presence of a diamond solvent. Thus, the reaction mass will contain a diamond solvent. Diamond solvents are usually a Group VIII metal or alloy containing such a metal. Diamond solvents and the temperature and pressure conditions used for diamond synthesis are well known in the art and are described, for example, in United States Patents Nos. 2,947,609 and 2,947,610. The preferred diamond synthesis conditions are temperatures in the range 1450°C to 1600°C and pressures in the range 45 to 70 kilobars. The occluded material is preferably a suitable salt such as a chloride. The preferred chloride is sodium chloride. The recovery technique usually involves treating the reaction mass with a hot acid solution. This acid solution will dissolve away the diamond solvent and will also be suitable for leaching out the occluded material, particularly when that material is a chloride salt. The occluded material typically constitutes up to 30% by weight of the reaction mass. The occluded material will be removed from the surface of the diamond particle leaving crevices and holes which assist in creating the friability in the particles. Some of the occluded material will remain trapped in closed pores in the diamond particle. The reaction mass will be placed in the reaction zone of a conventional high temperature/high pressure apparatus and then raised to the necessary elevated temperature and pressure conditions. Such apparatus is described, for example, in United States patent No. 2,941,248. In an example of the invention, a mixture of a powdered nickel/manganese alloy (76/24), graphite and sodium chloride was placed in a reaction capsule of a conventional high temperature/high pressure apparatus. The ratio of the alloy to graphite was 2: 1 on a weight basis. The sodium chloride was present in an amount of 5% by weight expressed as a percentage of the alloy and graphite. The reaction capsule was placed in a conventional high temperature/high pressure apparatus and subjected to a pressure of 60-65 kilobars and a temperature of about 1500°C. These conditions were maintained for a period of 16 minutes. The temperature and pressure conditions were allowed to return to ambient and the reaction capsule removed from the apparatus. The capsule was then placed in a body of a hot acid solution which dissolved the metal leaving a mass of fine diamond particles. It was found that the sodium chloride became occluded in the diamond particles during manufacture and that the sodium chloride in the open pores was leached from the particles by the acid solution leaving crevices and holes in the surfaces of the particles. These crevices and holes assisted in creating the friable nature of the particles. Small amounts of sodium chloride remained in closed pores in the particles. In further examples, diamond particles were produced using the same method and apparatus described above except that the sodium chloride content was varied. Diamond particles were produced using a 0,5, 2, 2,5, and 10% by weight sodium chloride based on the alloy and graphite. In each case, friable diamond particles were produced with crevices and holes in the surfaces thereof and some sodium chloride was left in closed pores. The friable nature of the diamond particles made according to the invention renders them particularly suitable for use in grinding wheels, such as resin bonded grinding wheels. A grinding wheel consists of a hub around which is located a working portion. The working portion consists of discrete abrasive particles uniformly distributed through a bonding matrix. In the case of a resin bonded grinding wheel the bonding matrix is a resin. Friable diamond particles produced as described above and using a reaction mass containing 5% by weight of sodium chloride were incorporated into a number of resin bonded grinding wheels. A second set of resin bonded grinding wheels was produced except that the diamond particles used were standard RD (resin bond) friable diamond particles. Two of the wheels in each set contained diamond particles in the range 88 to 105 microns, and two of the wheels in each set contained diamond particles containing 125 to 149 microns in size. The grinding ratio of each wheel was determined. The grinding ratio is the ratio of the amount of workpiece removed to the amount of grinding wheel removed. The higher the grinding ratio the better the grinding wheel and hence the more effective the diamond particle in the wheel. In all instances, the diamond particles produced by the method of the invention out-performed the standard RD friable diamond particles. The results obtained are set out in the Table below. The grinding ratios of the wheels containing the particles produced by the invention are expressed as a percentage of the corresponding grinding wheel using conventional RD friable diamond particles. It will be seen from the above that in all examples, whether the grinding conditions were wet or dry, grinding wheels containing the diamond particles produced by the method of the invention had a higher grinding ratio to those using conventional RD friable diamond particles and hence out-performed these wheels.

Claims: 1. A method of producing friable diamond particles including the steps of subjecting a reaction mass to temperature and pressure conditions suitable for producing the particles, the reaction mass comprising a source material for producing the diamond particles, a diamond solvent and a non-metallic material capable of being occluded in the diamond particles so produced and being removed therefrom, recovering the diamond particles from the reaction mass, and removing at least some of the occluded material from the diamond particles. 2. A method according to claim 1 wherein the reaction mass comprises a mixture of the source material, the diamond solvent and the material capable of being occluded in the diamond particles. 3. A method according to claim 1 or claim 2 wherein the material capable of being occluded in the diamond particles is a chloride salt. 4. A method according to claim 3 wherein the chloride salt is sodium chloride. 5. A method according to any one of the preceding claims wherein the material capable of being occluded in the diamond particles is present in the reaction mass in an amount of up to 30% by weight of the mass. 6. A method according to any one of the preceding claims wherein at least some of the occluded material is removed from the diamond particles by leaching. 7. A method according to any one of the preceding claims wherein the source material is graphite.

Inventors: FISH, MICHAEL LESTER
Applicants: DE BEERS INDUSTRIAL DIAMOND DIVISION (PROPRIETARY) LIMITED
Application year: 1988
Main classification: B01J3
IPC codes: B01J3, C09K3