PROCESS FOR ELECTROLESS PLATING A METAL ON NON-CONDUCTIVE MATERIALS

Abstract: The present invention discloses a process for electroless plating a metal on the surface of almost all the common non-­ conductive material substrates by brushing or spraying compo­ site chemical solutions onto said surface. When practising the present invention, metal can be quickly deposited on the surface and firmly bound with the substrate. In addition, the composite chemical solutions used in the invention can be pre­ pared from the raw chemicals which is nontoxic and does not cause pollution in environment.

Description: Background of the invention The present invention relates to a process for electroless plating a metal on non-conductive materials, and more particularly, it relates to a process of depositing metal layer on surfaces of various non-conductive materials such as plastics, glass, ceramic body, wood, stone, plaster body, cement article and articles made of bamboo etc. by electroless brushing or spraying chemical compositions onto said surface to bring about chemical reaction. This invention also relates to the products obtained by the above said process. Processes for depositing metals on conductive materials by bath electro-plating or by brush electro-plating have been widely used for a long time. And it is also well-known to deposite a metal on the surfaces of non-conductive material substrate by treating the surface to provide surface conductibility, then depositing metals on the conductive surface of said non-conductive material by bath electro-plating or brush-electroplating (US Patents 4481081, 4165394). Surfaces of some non-conductive nonmetal materials such as ceramics, plastics etc. are first subjected to etching, then treated with a linking agent capable of providing sites for stannous ion adsorption on said surface by immersion or dipping, primed with aqueous solution containing stannous and copper ions by immersion or dipping, following by immersion or dipping treated with a reducing agent capable of reducing the valence state of the copper ions, and finally electrolessly plated to deposite metal layer on said surface. This process is also well-known (US Patent 3993848). However, up to now all the existing processes for depositing metals on non-conductive material substrates cannot be carried out without plating bath, that is to say, the substrate to be plated must be immersed or dipped in pretreatment solution and plating solution. Therefore, the application of said processes is restricted by many factors. First, the dimension of the substrate to be plated must be within a certain range since it is impossible to provide very large plating baths in practice, then, the kinds of platable materials are restricted, since a porous material would absorb a large amount of plating solution resulting in greater expenses. And further, such processes are not suitable for plating only a portion of the surface of material. Through investigation on the matter of electroless plating for years, the present inventor has found that metal can be deposited on the surfaces of various non-conductive material substrates only by brushing or spraying certain composite pretreatment solutions that are a sensitization solution and activation solution, and a certain composite electroless plating solution without the necessity of immersing said substrate in bath solution. The process according to the present invention does not require the immersing or dipping step existing in the prior art processes, and it has advantages of simplicity in apparatus and flexibility in process, by which a metal can be deposited on the surfaces of various non-conductive materials, either on the entire surfaces or on a portion of a surface, without any restriction of the dimension and surface state of the substrate to be plated. Using the process of this invention, a metal can be deposited quickly and bound firmly on the surface of the substrate, with low assumption of pretreating and plating solutions. There is no restriction of the temperature at which the process is caried out. Further, no CN group is present in the composite solutions used in the present invention, and all the composite solutions are prepared from the substances which are non-toxic and cause no pollution to the environment. One object of the present invention is to provide a process for electroless plating a metal on the surface of a non-conductive material substrate which can withstand acidic corrosion and exhibits surface nonpolarity or weak polarity by brushing or spraying composite chemical solutions onto said surface comprising the steps of (1) roughening said surface of the non-conductive material substrate to be plated as pretreatment by means of a method including mechanical grinding or contacting with a chemical solution or contacting with an organic solvent and the combination thereof; (2) brushing or spraying the composite solution having the following compositions onto the roughened surface to sensitize said surface, SnCl₂ 50 - 350 g/l 36% HCl 50 - 150 g/l aqueous solution containing 0.001 - 1 wt.% alkyl sulfonate and 20 - 25 wt.% HCl 10 - 100 g/l optionally aqueous solution containing 70 - 80 wt.% propanetriol 5 - 10 drops/l water balance (3) brushing or spraying a solution containing positive ions of a metal having catalytic activity onto the sensitized surface to activate the surface; (4) brushing or spraying a solution containing copper ions of 12 - 50 g/l, a conventional reducing agent and a complexing agent onto the activated surface until a desired thickness of copper layer is deposited on the surface. Another object of the present invention is to provide a method for depositing a metal on the surfaces of non-conductive material substrates which can withstand acidic corrosion and exhibits either a surface polarity or a surface affinity for water. The process procedure of depositing metal on this kind of materials is substantially the same as that of depositing metal on the surface of materials having nonpolarity or weak polarity with identical apparatus and tools. The difference between the two is in that different treatment solutions are respectively used. The feature of the latter case is that the composite sensitization solution contains a certain amount of alcohol and indicator which can combine with the ions acting as sensitization agent to form a complex compound, for example, thymol blue or the like. It is preferred that the process comprises a step of electro-brush-plating a metal on the copper plated surface. It is further preferred that the process comprises a step of washing the sensitized surface with deionized water between steps (2) and (3). It is also preferred that the solution used in step (2) as the alkyl sulfonate contains a straight-chain alkyl-sulfonate having 8 - 20 carbon atoms in a concentration in the range of 0.01 - 0.1 g/l based on the sensitization solutions. It means that the object of the present invention is a process for electroless plating a metal on the surface of a non-conductive material substrate which can withstand acidic corrosion and exhibits a surface polarity or a surface affinity for water by brushing or spraying composite chemical solutions onto said surface, comprising the steps of (1) roughening said surface of the non-conductive material substrate to be plated as pretreatment by means of method including mechanical grinding or contacting with a chemical solution or contacting with an organic solvent and the combination thereof; (2) brushing or spraying a composite solution having the following compositions on the roughened surface to sensitize the surface: SnCl₂ 25 - 175 g/l 36% HCl 35 - 110 g/l alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol 50 - 100 g/l aqueous solution containing 70 - 80 wt.% propanetriol 3 - 5 drops/l water balance (3) brushing or spraying a solution containing positive ions of a metal having catalytic activity onto the sensitized surface to activate the surface; (4) brushing or spraying a solution containing copper ions of 12 - 50 g/l, a conventional reducing agent and a complexing agent onto the activated surface until a desired thickness of copper layer being deposited on the surface. According to the special features of the invention the process further comprises a step of electro-brush-plating a metal on the copper plated surface. It is preferred that the process comprises a step of washing the sensitized surface with deionized water between steps (2) and (3). Still another object of the invention is to provide a process for electroless plating a metal on the surface of a non-conductive material substrate which can withstand alkaline corrosion or exhibits alkaline properties by brushing or spraying composite chemical solutions onto said surface, comprises the steps of (1) roughening said surface of the non-conductive material substrate to be plated as pretreatment by means of method including mechanical grinding or contacting with a chemical solution or contacting with an organic solvent and the combination thereof; (2) brushing or spraying a composite solution having the following compositions onto the roughened surface to sensitize the surface: SnCl₂ 50 - 100 g/l NaOH 100 - 150 g/l Sodium-potassium tartrate 120 - 170 g/l alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol 50 - 100 g/l water balance (3) brushing or spraying a solution containing positive ions of a metal having catalytic activity onto the sensitized surface to activate the surface; (4) brushing or spraying a solution containing copper ions of 12 - 50 g/l, a conventional reducing agent and a complexing agent onto the activated surface until a desired thickness of copper layer being deposited on the surface. According to a preferred embodiment the process comprises a step of electro-brush-plating a metal on the copper plated surface. It is further preferred that the process comprises a step of washing the sensitized surface with deionized water between steps (2) and (3). The process procedure, apparatus and tools used for depositing metal on the surfaces of this kind of materials are substantially the same as that of the above two cases. The composite sensitization solution contains a certain amount of strong alkaline, alcohol and an indicator agent which can combine with the ions acting as sensitization agent to form a complex compound. The processes of the present invention can be used in a very wide range, by which a metal layer can be deposited on various non-conductive materials only by brushing or spraying different composite chemical agent solutions dependent on the kind of material to be plated. After depositing a metal layer on the material, the surface of the material becomes conductive, so a further metal layer can be deposited by any conventional brush electro-plating or bath electro-plating, and of course, any methods of metal surface treatment can be used for further processing the metal surface formed according to the present invention. The present invention provides composite sensitization solutions used in depositing metal on various different materials according to the present invention. 1. A composite sensitization solution suitable for the materials including the acid-resistant non-conductive material and organic materials having non-polarity surface or weak polarity surface is provided. The solution contains a high concentration of metal ions acting as sensitization agent, which metal ions are apt to be oxidized by positive ions of a metal having catalytic activity but can hardly be oxidized by air. Stannous ion is an example of such ions. The concentration of stannous ion is in the range of 15,6-219,1 g/l. A large amount of acid is to be added into this composite sensitization solution and a small amount of indicator may also be added, such as thymol blue. The characteristics of this solution is that it contains a low concentration of negative ion surfactant. It is better to use a straight chain alkylsulfonate, preferably having 8-20 carbon atoms, as surfactant. The concentration of the surfactant should be very low, generally it is in the range of 0.0001 g/l-0.1 g/l, and not beyond 1 g/l. The binding strength between the deposited metal layer and the substrate will be lowered if the concentration of the surfactant is too high while too low a concentration of the surfactant will cause misdeposition and lower the deposition rate during brush plating. Practice shown, it is better to prepare beforehand an aqueous solution comprising an alkylsulfonate of 0.001-1 g/l and hydrochloric acid of 20-25% by weight to be used as the surfactant component during preparing composite sensitization solution. This composite sensitization solution may contain a little amount of propanetriol and has the following basic composition: SnCl₂ 50-350 g/l 36% hydrochloric acid 50-150 g/l aqueous solution containing 0.001 - 1 wt.% alkyl sulfonate and 20 - 25 wt.% HCl 10 - 100 g/l aqueous solution containing 70 - 80 wt.% propanetriol 5 - 10 drops/l balance water. 2. A composite sensitization solution suitable for non-conductive materials which can withstand acidic corrosion and exhibits either a surface polarity or surface affinity for water contains the same metallic ions as that in the above first solution, only the concentration thereof is a little bit lower. And, in this solution the acid content is less than that in the first solution. The characteristics of this sensitization solution is that it contains a certain amount of alcohol, most commonly ethanol, and an indicator capable of complexing with the ions acting as sensitization agent. Said indicator will change in colour during brush plating to indicate the result of the deposition of the catalytic metal and thus making the deposition uniform and perfect. Ethanol is volatile, so, the concentration of this solution will increase during the sensitization step. This composite sensitization solution may also contain propanetriol. Generally, the materials suitable to be treated with this sensitization solution are easily wetted by water, therefore, it is unnecessary to add surfactant thereinto. It should be noted that the ethanol content in this solution should be adjusted according to the specific substrate material. The compositions of this solution are: SnCl₂ 25-175 g/l 36% hydrochloric acid 35-110 g/l alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol 50-100 g/l aqueous solution containing 70 - 80 wt.% propanetriol 3-5 drops/l balance water. 3. A composite sensitization solution suitable for the materials which can withstand strong alkaline corrosion or exhibits alkaline properties contains the same metallic ions as that in the above first and second solutions. But, this solution contains a large amount of strong alkaline and in which the metallic ions are completely dissolved. The characteristics of this solution is that it contains a large amount of tartrate, and its concentration is in the range of 120-270 g/l. And a certain amount of alcohol, ethanol is the most common one, can be added into this solution, the indicator capable of complexing with the metallic ions acting as sensitization agent can also be added. The compositions of this solution are: SnCl₂ 50-100 g/l NaOH 100-150 g/l Sodium-potassium tartrate 120-170 g/l alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol 50-100 g/l balance water The composite sensitization solutions provided by the present invention are nontoxic and cause no pollution to the environment; and the raw chemicals are relatively inexpensive and easy to be obtained. The preparation of the solutions is quite simple and easy to handle. Therefore, such solutions can be used extensively under various conditions. When practising the process of the present invention, the apparatus are very simple, the process has flexibility and the rate of depositing metal is very quick; a metal can be deposited on almost any common non-conductive materials by selecting a proper composite sensitization solution depending on the surface properties of the substrate materials to be plated. The terminology "the material can withstand acidic corrosion" refers to the material basically does not react with acid, and if the surface of this material is treated with acidic solution, there will be no unfavourable effects on the properties and the shape of the material itself. The representative examples of this kind of materials are various plastics, various glass, organic glass, enameled ceramics, grinites, silicate stone, bamboo and some kinds of wood, etc. "The materials having surface nonpolarity or weak polarity" includes almost all kinds of common organic materials. Representative examples of these materials are various resins or plastics such as epoxide resin, phenolplast, polyethylene, polysulfones, polyvinyl chloride, aminoplastics, some A.B.S. plastics, polytetrafluorethylene, polyaldehyde, etc. "The materials exhibiting a surface polarity or a surface affinity for water" refer to the materials having microporous surface or being apt to be wetted by water. Examples of this kind of materials are plainly sintered ceramics, clay articles, gypsum articles, wood and bamboo, etc., and some kinds of A.B.S. plastics. "The materials which can withstand alkaline corrosion or exhibits alkaline properties" refer to the materials which do not react with alkaline or the materials which cannot be treated with an acidic solution due to its reaction with acid. Examples of this kind of materials are carbonate-containing materials, such as marble, limestone, cement article; granite stone, silicate stone, wood fruit, bamboo, rattens. In the roughening step of the present invention, either mechanical roughening, chemical agent roughening or solvent roughening may be selected based on the specific substrate material to be plated. Of course, all these three roughening methods can be used simultaneously, or no roughening step is required for some specific materials. The mechanical roughening may be any mechanical roughening process, such as grinding, sand blasting, abrasion with emery cloth, etc. Roughening solvent should be chosen according to the specific substrate to be plated. For example, for the substrate of organic glass acetone may be chosen as the roughening solvent, and for polyethylene plastics cyclohexanone may be chosen, etc. The roughening chemical solution may be a mixture of a strong acid and oxidizing agent or a hydrofluoric acid containing solution, for example, an aqueous solution comprising 10-30 g/l CrO₃ and 125-250 g/l H₂SO₄, an aqueous solution comprising 75-125 g/l H₂SO₄, 43-127 g/l HF and 30-65 g/l CrO₃. The composite sensitization solution used in the present invention has been discussed hereinbefore in detail. In the practice of the present invention the sensitization solution should be chosen according to the specific material substrate to be plated. For example, an alkaline sensitization solution is required for marble and the solution containing a negative ion surfactant is required for a nonpolarity plastics. Some substrate materials can be treated with different kinds of composite sensitization solutions, for example, some compact wood can be sensitized with either an acidic sensitization solution or an alkaline solution. For the substrate materials of high water absorption, a pretreatment should be carried out before the sensitization step in order to block up the water-absorbing holes. A conventional process for filling holes can be applied, such as point coating, plastics spraying, etc. In some cases, the sensitized surface should be rinsed with deionized water to wash away the surplus sensitizing solution and to promote the absorption of the ions used as activating agent. The activation treatment is to brush or spray the composite solution containing the ions of a metal having catalytic activity on the sensitized surface, thus making the ions reduced to metal particles by the reducing ions adsorbed on the surface during sensitization step, and the metal particles are firmly adsorbed on the surface. The catalytic metal particles adsorbed on the surface are the nucleating centres during electroless brush-plating. Therefore, the activation should be carried out uniformly and thoroughly. In the process of the present invention, the composite activating solution may further contain a negative ion surfactant, propanetriol, ethanol or NH₄OH besides the ions used as the activating agent. The common ions are Ag⁺ and Pd⁺⁺. For the solution containing Ag⁺, a certain amount of NH₄OH must be added, and propanetriol, ethanol or a negative ion surfactant may also be added according to the specific condition. The concentration of Ag⁺ in the solution in general is rather high. For the Pd⁺⁺-containing solution, a certain amount of hydrochloric acid must be added, and a negative ion surfactant and/or a certain amount of ethanol may also be added according to the specific condition. The concentration of Pd⁺⁺ is in the range of 1-5 g/l. The composite activating solution containing a negative ion surfactant is suitable for the materials exhibiting surface nonpolarity or weak polarity, particularly, for an organic material having nonpolarity surface. The addition of the surfactant in low concentration can improve the deposition effect significantly. For the substrate materials easy to react with acid, the activating solution containing Ag⁺ must be used. In some cases, the activated surface may be washed with water and reduced with a conventional reducing agent before the step of electroless brush-plating. After the above-mentioned steps, the electroless brush-plating is carried out, i.e. continuously applying the chemical brush-plating solution onto the activated surface by means of brushing or spraying to deposite a metal, preferably copper, on the surface. As the metal ions are converted into metal by the reducing agent in the solution, a layer of the deposited metal is gradually formed and firmly bound on the surface to be plated. The electroless brush-plating solution is also a composite solution, which may contain a conventional reducing agent, complexing agent and buffer agent besides the ions of the metal to be deposited. The concentration of the composite solution is rather higher as compared with that in prior art electroless bath-plating, and in the case of depositing copper, the copper ion concentration is in the range of 12-50 g/l, preferably 20-50 g/l. The conventional stabilizing agent capable of decreasing the rate of metal deposition should not exist in the composite solution. After the step of electroless brush-plating, a layer of metal has deposited on the surface of the substrate, thus making the surface conductive. Therefore, the conductive substrate surface can be treated subsequently with any technique suitable for the conductive materials to achieve the final purpose. The most suitable subsequent treatment is the brush electro-plating, which requires no immersing bath and will not be restricted by the geometrical shape and dimension of the substrate. Of course, some substrates may also subsequently be treated by bath electro-plating according to the requirement Besides the advantages as set forth, the following benefits are also present in the process of the invention. The composite solution having been applied onto the substrate surface are continuously stirred by brushing, thus accelerating the diffusion rate of the ion particles in the solution so that all the chemical reaction rate, the absorption rate and the depositing rate are accelerated. The concentrations of the metal ions in the solutions are rather high so that high absorption rate and depositing rate can be achieved. This invention will be explained in more detail by the following examples. Example 1 Preparation of the composite sensitization solution suitable for the materials capable of withstanding acid corrosion and having weak polarity or nonpolarity surface. 150 g SnCl₂ was placed into a beaker of 1000 ml, then a concentrated hydrochloric acid of 120 ml and the mixing agent of an aqueous solution containing 0.001 - 1 wt.% sulfonate and 20 - 25 wt.% HCl of 60 ml were slowly added into the same beaker with stirring until the SnCl₂ was dissolved thoroughly. Subsequently, five drops of the mixing agent, an aqueous solution containing 70 - 80 wt.% propanetriol were added into the solution, then the solution was slowly diluted to the volume of 1l with deonized water under stirring. Put it into a brown glass bottle, ready for use. Example 2 Preparation of the sensitization solution suitable for the materials capable of withstanding acid corrosion and having surface polarity or affinity for water. 75 g SnCl₂ was placed into a beaker of 1000 ml, a concentrated hydrochloric acid of 85 ml was also added thereto with stirring until complete dissolution of SnCl₂. The obtained solution was slowly diluted with deionized water to the volume of 800 ml under stirring, then the mixing agent, an alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol, of 50 ml and five drops of the mixing agent, an aqueous solution containing 70 - 80 wt.% propanetriol, were added, then stirring again, diluted with deionized water to the volume of 1 l. The solution was kept in a brown bottle ready for use. Example 3 Preparation of the sensitization solution suitable for the materials capable of withstanding strong alkaline corrosion or exhibiting alkaline properties. A definite amount of SnCl₂ was dissolved in a definite amount of water to prepare a solution A. A definite amount of potassium-sodium tartrate was dissolved in water, then a definite amount of NaOH was added, stirring until completely dissolved, thus a solution B was prepared. The solution A was mixed with the solution B, then a definite amount of mixing agent, an alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95 % alcohol, was added under stirring, then diluted to a definite number. Example 4 The compositions and preparation of the composite activation solutions. Activation solution (I) Compositions AgNO₃ 10-35 g/l mixing agent solution comprising 50 wt.% ethanol 10-15 wt.% NH₄OH and water 15-80 ml/l mixing agent solution comprising 50 wt.% ethanol, 0.01-1 wt.% alkylsulfonate and water 10-20 ml/l Water balance Preparation 15 g AgNO₃ was placed into a beaker of 1000 ml, 500 ml deionized water was added, under stirring then 25-40 ml mixing agent, a solution comprising 50 wt.% ethanol, 10-15 wt.% NH₄OH and water, was added until complete dissolution of the produced precipitate, 10 ml mixing agent, solution comprising 50 wt.% ethanol, 0.01-1 wt.% alkylsulfonate and water, was then added thereto. The solution is stirred and diluted into a volume of 1 l, and kept in a brown bottle. Activation solution (II) Compositions AgNO₃ 5-15 g/l mixing agent solution comprising 50 wt.% ethanol 10-15 wt.% NH₄OH and water 10-90 ml/l aqueous solution containing 70-80 wt.% propanetriol 1-3 drops/l Water balance Preparation 10 g AgNO₃ was placed into a beaker of 1000 ml, 10-15 ml mixing agent, a solution comprising 50 wt.% ethanol, 10-15 wt.% NH₄OH and water 10-90 ml/l, was added under stirring until complete dissolution of the produced precipitate. Then three drops of mixing agent, aqueous solution containing 70-80 wt.% propanetriol, were added and the solution was diluted with deionized water into one litre, stirred and kept in a brown bottle. Example 5 Electroless plating copper solutions Compositions of solution (I) CuSO₄ 30- 90 g/l potassium-sodium tartrate 95-230 g/l NaOH 40-120 g/l 36% HCHO aqueous solution 80-250 g/l TCA agent 120-180 g/l E.D.T.A. 8- 20 g/l Water balance. Here, the term "TCA agent" referring to the mixing aqueous solution comprising 12-15% by weight, Na₂CO₃ 10-12% by weight (C₂H₅O)₃N and deionized water. Compositions of solution (II) CuSO₄ 30- 80 g/l (C₂H₅O)₃N 70-200 g/l Na₂CO₃ 10- 60 g/l NaOH 40-180 g/l 36% HCHO aqueous solution 80-250 g/l Water balance. Compositions of solution (III) CuSO₄ 30-100 g/l propanetriol 40-120 g/l Na₂CO₃ 10- 50 g/l 36% HCHO aqueous solution 100-250 g/l water balance. Example 6 Plating copper on the surface of a polychloroethylene board having a thickness of 3 mm, the steps were as follows: 1. The surface of the board was rubbed crosswise with emery paper to reduce the roughening traces, then rinsing away the rubbing sludges. 2. The rubbed surface of the board was treated with an aqueous solution containing 20 g CrO₃/l and 200 g/l H₂SO₄ by brushing the solution thereto for 3-5 min. The speed of brushing was 1-3 m/min., then rinsing away the solution on the board with water. 3. Sensitization - the roughened surface was treated with the composite sensitization solution prepared in Example 1 to sensitize the surface by careful brushing, the brushing speed being 1-3 m/min. 4. The sensitized surface was washed with deionized water. 5. Activation - the activation solution (I) prepared in Example 4 was brushed on the sensitized surface with the brushing speed of 1-3 m/min to activate the surface to be plated. 6. The activated surface was rinsed with an aqueous HCHO solution. 7. Electroless brush-plating. The electroless plating copper solution (I) shown in Example 5 was used. The brush was first dipped in the solution, then brushing the solution onto the activated surface continuously, the copper ions in the solution were reduced into metal copper and deposited on the surface, gradually forming a copper layer. During the brushing the speed of the relative motion of the brush to the substrate surface was 4-8 m/min. 8. Wash the plated copper surface with water. Example 7 Copper was plated on a phenolplast board of 2 mm thickness by the treating the same steps as that of Example 6 with the exception that the composite sensitization solution of Example 2 was used in sensitization step. The copper plated polychloroethylene board and phenolplast board were tested as samples. Testing items: 1. Immersing the samples into hot water at 50°C and 100°C respectively for half an hour, then taking it out and putting it into cold water at 15°C at once for sudden cooling. 2. The samples treated in item 1 were bent with a bending R of 5 cm. The testing results: 1. No scaling or peeling of the copper coating from the substrate of the two samples was found after the treating of item 1. 2. No scaling or peeling of the copper coating from the substrate of the two samples was found during bending and after bending. Example 8 Plating copper on the surface of a ceramic body without enamel. In this example the operating steps of the sensitization and hereinafter were the same as that mentioned in Example 7 with the roughening step as described below. Alumina sands of 60-100 mesh were blasted onto the body surface by an air pressure of 2-3 kg/cm² to roughen the surface; then the roughened body was immersed in water until it was not absorbing water further; subsequently, taking it out of water and drying in air for 30-120 minutes to remove the water on surface. Then the sensitization step and the following steps according to Example 7 were carried out. Example 9 Plating copper on the surface of a red pin wooden block In this example the operating steps were the same as that of Example 7 with the exception that the sensitization solution was prepared in Example 3. Finally, copper was deposited on the block. Example 10 Plating copper on marble surface In this example the operation was the same as that of Example 7 with the exception that the sensitization solution prepared in Example 3 and the activation solution (II) were used; finally, a copper layer was bound on the marble surface. Example 11 Comparison In this example three samples were produced, and the operation was the same as that of Example 6 with the exception that different sensitization solutions (1), (2) and (3) prepared according to Example 1 but containing respectively different concentrations of an aqueous solution containing 70 - 80 wt.% propanetriol, in which the concentrations of the sodium alkylsulfonate were 0.8%-0.03%, and 0.00% respectively, were used. As a result, the binding strength between the plated copper layer and the polychloroethylene substrate were different. Sample The concentration of sodium alkylsulfonate result 1 0.8% poor binding 2 0.03% firmly binding 3 0.00% apt to miss plating After reading the specification, it should be understood that various changes and modifications of the preferred embodiments described herein will be apparent to those skilled in the art.

Claims: A process for electroless plating a metal on the surface of a non-conductive material substrate which can withstand acidic corrosion and exhibits surface nonpolarity or weak polarity by brushing or spraying composite chemical solutions onto said surface comprising the steps of (1) roughening said surface of the non-conductive material substrate to be plated as pretreatment by means of a method including mechanical grinding or contacting with a chemical solution or contacting with an organic solvent and the combination thereof; (2) brushing or spraying the composite solution having the following compositions onto the roughened surface to sensitize said surface, SnCl₂ 50 - 350 g/l 36% HCl 50 - 150 g/l aqueous solution containing 0.001 - 1 wt.% alkyl sulfonate and 20 - 25 wt.% HCl 10 - 100 g/l optionally aqueous solution containing 70 - 80 wt.% propanetriol 5 - 10 drops/l water balance (3) brusing or spraying a solution containing positive ions of a metal having catalytic activity onto the sensitized surface to activate the surface; (4) brushing or spraying a solution containing copper ions of 12 - 50 g/l, a conventional reducing agent and a complexing agent onto the activated surface until a desired thickness of copper layer is deposited on the surface. A process according to Claim 1, further comprising a step of electro-brush-plating a metal on the copper plated surface. A process according to Claim 1, further comprising a step of washing the sensitized surface with deionized water between steps (2) and (3). A process according to Claim 1, wherein the solution used in step (2) as the alkyl sulfonate contains a straight-chain alkyl-sulfonate having 8 - 20 carbon atoms in a concentration in the range of 0.01 - 0.1 g/l based on the sensitization solutions. A process for electroless plating a metal on the surface of a non-conductive material substrate which can withstand acidic corrosion and exhibits a surface polarity or a surface affinity for water by brushing or spraying composite chemical solutions onto said surface, comprising the steps of (1) roughening said surface of the non-conductive material substrate to be plated as pretreatment by means of method including mechanical grinding or contacting with a chemical solution or contacting with an organic solvent and the combination thereof; (2) brushing or spraying a composite solution having the following compositions on the roughened surface to sensitize the surface: SnCl₂ 25 - 175 g/l 36% HCl 35 - 110 g/l alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol 50 - 100 g/l aqueous solution containing 70 - 80 wt.% propanetriol 3 - 5 drops/l water balance (3) brushing or spraying a solution containing positive ions of a metal having catalytic activity onto the sensitized surface to activate the surface; (4) brushing or spraying a solution containing copper ions of 12 - 50 g/l, a conventional reducing agent and a complexing agent onto the activated surface until a desired thickness of copper layer being deposited on the surface. A process according to Claim 5, further comprising a step of electro-brush-plating a metal on the copper plated surface. A process according to Claim 5, further comprising a step of washing the sensitized surface with deionized water between steps (2) and (3). A process for electroless plating a metal on the surface of a non-conductive material substrate which can-withstand alkaline corrosion or exhibits alkaline properties by brushing or spraying composite chemical solutions onto said surface, comprising the steps of (1) roughening said surface of the non-conductive material substrate to be plated as pretreatment by means of method including mechanical grinding or contacting with a chemical solution or contacting with an organic solvent and the combination thereof; (2) brushing or spraying a composite solution having the following compositions onto the roughened surface to sensitize the surface: SnCl₂ 50 - 100 g/l NaOH 100 - 150 g/l Sodium-potassium tartrate 120 - 170 g/l alcohol solution containing 0.01 - 1 wt.% thymol blue indicator and 95% alcohol 50 - 100 g/l water balance (3) brushing or spraying a solution containing positive ions of a metal having catalytic activity onto the sensitized surface to activate the surface; (4) brushing or spraying a solution containing copper ions of 12 - 50 g/l, a conventional reducing agent and a complexing agent onto the activated surface until a desired thickness of copper layer being deposited on the surface. A process according to Claim 8, further comprising a step of electro-brush-plating a metal on the copper plated surface. A process according to Claim 8, further comprising a step of washing the sensitized surface with deionized water between steps (2) and (3).

Inventors: CHUANMING ZHENG, RONGSHENG HAN, SHAOXIAN ZHANG
Applicants: ARMOUR FORCE ENGINEERING INSTITUTE OF THE CHINESE PEOPLE'S LIBERATION ARMY
Application year: 1988
Main classification: C23C18
IPC codes: C23C18, H05K3