Multilayered light receiving member

Abstract: A light receiving member for electrophotography made up of an aluminum support and a multilayered light receiving layer exhibiting photoconductivity formed on the aluminum support, wherein the multilayered light receiving layer consists of a lower layer in contact with the support and an upper layer, the lower layer being made of an inorganic material containing at least aluminum atom (Al), silicon atoms (Si) and hydrogen atoms (H), and having portion in which the aluminum atoms (Al), silicon atoms (Si), and hydrogen atoms (H) are unevenly distributed across the layer thickness, the upper layer being made of a non-single-crystal material composed of silicon atoms (Si) as the matrix and at least either of hydrogen atoms (H) or halogen atoms (X) and containing at least one of carbon atoms, nitrogen atoms (N) and oxygen atoms (O) in the layer region in adjacent with the lower layer. The light receiving member for electrophotography can overcome all of the foregoing problems and exibits extremely excellent electrical property, optical property, photoconductivity, durability, image property and circumstantial property of use.

Description: FIELD OF THE INVENTION This invention concerns a light receiving member sensitive to electromagnetic waves such as light (which herein means in a broader sense those lights such as ultraviolet rays, visible rays, infrared rays, X-rays, and γ-rays). More particularly, it relates to an improved light receiving member having a multilayered light receiving layer composed of a lower layer made of an inorganic material containing at least aluminum atoms, silicon atoms, and hydrogen atoms, and an upper layer made of non-single-crystal silicon material, which is suitable particularly for use in the case where coherent lights such as laser beams are applied. BACKGROUND OF THE INVENTION The light receiving member used for image formation has a light receiving layer made of a photoconductive material. This material is required to have characteristic properties such as high sensitivity, high S/N ratio (ratio of light current (Ip) to dark current Id)), absorption spectral characteristic matching the spectral characteristic of electromagnetic wave for irradiation, rapid optical response, appropriate dark resistance,and non-toxicity to the human body at the time of use. The non-toxicity at the time of use is an important requirement in the case of a light receiving member for electronic photography which is built into an electronic photographic apparatus used as an office machine. A photoconductive material attracting attention at present from the standpoint mentioned above is amorphous silicon (A-Si for short hereinafter). The application of A-Si to the light receiving member for electrophotography is disclosed in, for example, German Patent Laid-open Nos. 2746967 and 2855718. Fig. 2 is a schematic sectional view showing the layer structure of the conventional light receiving member for electrophotography. There are shown an aluminum support 201 and a photosensitive layer of A-Si 202 This type of light receiving member for electrophotography is usually produced by forming the photosensitive layer 202 of A-Si on the aluminum support 201 heated to 50 - 350°C, by deposition, hot CVD process, plasma CVD process, plasma CVD process or sputtering. Unfortunately, this light receiving member for electrophotography has a disadvantage that the sensitive layer 202 of A-Si is liable to crack or peel off during cooling subsequent to the film forming step, because the coefficient of thermal expansion of aluminum is nearly ten times as high as that of A-Si. To solve this problem, there was proposed a photosensitive body for electrophotography which is composed of an aluminum support, an inter mediate layer containing at least aluminum and a sensitive layer of A-Si (Japanese Patent Laid-open No. 28162/1984). The intermediate layer containing at least aluminum relieves the stress arising from the difference in the coefficient of thermal expansion between the aluminum support and the A-Si sensitive layer, thereby reducing the cracking and peeling of the A-Si sensitive layer. The the conventional light receiving member for electrophotography which has the light receiving layer made of A-Si has been improved in electrical, optical, and photoconductive characteristics (such as dark resistance, photosensitivity, and light responsivity), adaptability of use environment, stability with time, and durability. Nevertheless, it still has room for further improvement in its overall performance. For the improvement of image characteristics, several improvements has recently been made on the optical exposure unit, development unit, and transfer unit in the electrophotographic apparatus. This, in turn, has required the light receiving member for electrophotography to be improved further in image characteristics. With the improvement of images in resolving power, the users have begun to require further improvements such as the reduction of unevenness (so-called "coarse image") in the region where the image density delicately changes, and the reduction of image defects (so-called "dots") which appear in black or white spots, especially the reduction of very small "dots" which attracted no attention in the past. Another disadvantage of the conventional light receiving member for electrophotography is its low mechanical strength. When it comes into contact with foreign matters which have entered the electrophotographic apparatus, or when it comes into contact with the main body or tools while the electrophotographic apparatus is being serviced for maintenance, image defects occur or the A-Si film peel off on account to of the mechanical shocks and pressure. These aggravate the durability of the light receiving member for electrophotography. An additional disadvantage of the conventional light receiving member for electrophotography is that the A-Si film is liable to cracking and peeling on account of the stress which occurs because the A-Si film differs from the aluminum support in the coefficient of thermal expansion. This leads to lower yields in production. Under the circumstances mentioned above, it is desirable to solve the above-mentioned problems and to improve the light receiving member for electrophotography from the standpoint of its structure as well as the characteristic properties of the A-Si material per se. SUMMARY OF THE INVENTION The invention provides a light receiving member for electrophotography comprising an aluminum support and a multilayered light receiving layer exhibiting photoconductivity formed on said aluminum support; characterised in that said multilayered light receiving layer comprises a lower layer in contact with said aluminum support and an upper layer disposed on said lower layer; said lower layer comprising an inorganic material containing at least aluminum atoms, silicon atoms and hydrogen atoms; said lower layer having a portion in which said aluminum, silicon and hydrogen atoms are unevenly distributed across the layer thickness; said aluminum atoms being contained in said lower layer in an amount of 5 atomic % to 95 atomic % such that their content decreases across the layer thickness upward from the interface between said lower layer and said aluminum support, and wherein said content of said aluminum atoms is lower than 95 atomic % in the vicinity of the interface between said lower layer and said aluminum support and is higher than 5 atomic % in the vicinity of the interface between said lower layer and said upper layer; and said upper layer comprising a plurality of layer regions parallel to said interface each comprising a non-single crystal material composed of silicon atoms as the matrix and at least one kind of atoms selected from hydrogen atoms and halogen atoms, and wherein the layer region adjacent to said lower layer comprises at least one kind of atoms selected from carbon atoms, nitrogen atoms and oxygen atoms. DE-A-3412267 discloses a light receiving member having features of claim 1 but does not disclose a multilayered light receiving layer in which the lower layer has the structure set out above. The light receiving member for electrophotography in the present invention has the multilayered structure as mentioned above. Therefore, it is free from the above-mentioned disadvantages, and it exhibits outstanding electric characteristics, optical characteristics, photoconductive characteristics, durability, image characteristics, and adaptability to use environments. As mentioned above, the lower layer is made such that the aluminum atoms and silicon atoms, and especially the hydrogen atoms, are unevenly distributed across the layer thickness. This structure improves the injection of electric charge (photocarrier) across the aluminum support and the upper layer. In addition, this structure joins the constituent elements of the aluminum support to the constituent elements of the upper layer gradually in terms of composition and constitution. This leads to the improvement of image characteristics relating to coarse image and dots. Therefore, the light receiving member permits the stable reproduction of images of high quality with a sharp half tone and a high resolving power. The above-mentioned multilayered structure prevents the image defects and the peeling of the non-Si(H,X) film which occurs as the result of impactive mechanical pressure applied to the light receiving member for electrophotography. In addition, the multilayered structure relieves the stress arising from the difference between the aluminum support and the non-Si(H,X) film in the coefficient of thermal expansion and also prevents the occurrence of cracks and peeling in the non-Si(H,X) film. All this contributes to improved durability and increased yields in production. Particularly, since at least one of carbon atoms, nitrogen atoms and oxygen atoms are incorporated into the layer region of the upper layer in adjacent with the lower layer in this invention, the quality of the upper layer is improved to enhance the durability to the high voltage and the close bondability between the upper layer and the lower layer can further be improved, and image defects or the peeling of the Non-Si(H,X) film can be prevented, thereby contributing to the improvement of the durability. According to the present invention, the lower layer of the light receiving member may further contain atoms to control the image ("atoms (Mc)" for short hereinafter. The incorporation of atoms (Mc) to control the image quality improves the injection of electric charge (photocarrier) across the aluminum support and the upper layer and also improves the transferability of electric charge (photocarrier) in the lower layer. Thus the light receiving member permits the stable reproduction of images of high quality with a sharp half tone and a high resolving power. According to the present invention, the lower layer of the light receiving member may further contain atoms to control the durability ("atoms (CNOc) for short hereinafter). The incorporation of atoms (CNOc) greatly improves the resistance to impactive mechanical pressure applied to the light receiving member for electrophotography. In addition, it prevents the image defects and the peeling of the non-Si(H,X) film, relieves the stress arising from the difference between the aluminum support and the non-Si(H,X) film in the coefficient of thermal expansion, and prevents the occurrence of cracks and peeling in the non-Si(H,X) film. All this contributes to improved durability and increased yields in production. According to the present invention, the lower layer of the light receiving member may further contain halogen atom (X). The incorporation of halogen atom (X) compensates for the unbonded hands of silicon atom (Si) and aluminum atom (Al), thereby creating a stable state in terms of constitution and structure. This, coupled with the effect produced by the distribution of silicon atoms (Si), aluminum atoms (Al), and hydrogen atoms (H) mentioned above, greatly improves the image characteristics relating to coarse image and dots. According to the present invention, the lower layer of the light receiving member may further contain at least either of germanium atoms (Ge) or tin atoms (Sn). The incorporation of at least either of germanium atoms (Ge) or tin atoms (Sn) improves the injection of electric charge (photocarrier) across the aluminum support and the upper layer, the adhesion of the lower layer to the aluminum support, and the transferability of electric charge (photocarrier) in the lower layer. This leads to a distinct improvement in image characteristics and durability. According to the present invention, the lower layer of the light receiving member may further contain at least one kind of atoms selected from alkali metal atoms, alkaline earth metal atoms, and transition metal atoms, ("atoms (Me)" for short hereinafter). The incorporation of at least one kind of atoms selected from alkali metal atoms, alkaline earth metal atoms, and transition metal atoms permits more dispersion of the hydrogen atoms or halogen atoms contained in the lower layer (the reason for this is not yet fully elucidated) and also reduces the structure relaxation of the lower layer which occurs with lapse of time. This leads to reduced liability of cracking and peeling even after use for a long period of time. The incorporation of at least one kind of the above-mentioned metal atoms improves the injection of electric charge (photocarrier) across the aluminum support and the upper layer, the adhesion of the lower layer to the aluminum support, and the transferability of electric charge (photocarrier) in the lower layer. This leads to a distinct improvement in image characteristics and durability, which in turn leads to the stable production and quality. In the meantime, the above-mentioned Japanese Patent Laid-open No. 28162/1984 mentions the layer containing aluminum atoms and silicon atoms unevenly across the layer thickness and also mentions the layer containing hydrogen atoms. However, it does not mention how the layer contains hydrogen atoms. Therefore, it is distinctly different from the present invention. BRIEF DESCRIPTION OF THE INVENTION Fig. 1 is a schematic diagram illustrating the layer structure of the light receiving member for electrophotography. Fig.2 is a schematic diagram illutrating the layer structure of the conventional light receiving member for electrophotography. Fig. 3 to 8 are diagrams illustrating the distribution state of aluminum atoms (Al) contained in the lower layer, and also illustrating the distribution of atoms (Mc) to control image quality, and/or atoms (CNOc) to control durability, and/or halogen atoms (X), and/or germanium atoms (Ge), and/or tin atoms (Sn), and/or at least one kind of atoms selected from alkali metal atoms, alkaline earth metal atoms, and transition metal atoms, which are optionally contained in the lower layer. Figs. 9 to 16 are diagrams illustrating the distribution of silicon atoms (Si) and hydrogen atoms (H) contained in the lower layer, and also illustrating the distribution of atoms (Mc) to control image quality, and/or atoms (CNOc) to control durability, and/or halogen atoms (X), and/or germanium atoms (Ge), and/or tin atoms (Sn), and/or at least one kind of atoms selected from alkali metal atoms, alkaline earth metal atoms, and transition metal atoms, which are optionally contained in the lower layer. Figs. 17 to 36 are diagrams illustrating the distribution of atoms (M) to control conductivity, carbon atoms (C), and/or nitrogen atoms (N), and/or oxygen atoms (O), and/or germanium atoms (Ge), and/or tin atoms (Sn), and/or alkali metal atoms, and/or alkaline earth metal atoms, and/or transition metal atoms, which are contained in the upper layer. Fig. 37 is a schematic diagram illustrating an apparatus to form the light receiving layer of the light receiving member for electrophotography by RF glow discharge method according to the present invention. Fig. 38 is an enlarged sectional view of the aluminum support having a V-shape rugged surface which is used to form the light receiving member for electrophotography according to the present invention. Fig. 39 is an enlarged sectional view of the aluminum support having a dimpled surface on which is used to form the light receiving member for electrophotography according to the present invention. Fig. 40 is a schematic diagram of the depositing apparatus to form the light receiving layer of the light receiving member for electrophotography by microwave glow discharge method according to the present invention. Fig. 41 is a schematic diagram of the apparatus to form the light receiving layer of the light receiving member for electrophotography by microwave glow discharge method according to the present invention. Fig. 42 is a schematic diagram of the apparatus to form the light receiving layer of the light receiving member for electrophotography by RF sputtering method according to the present invention. Figs. 43 (a) to 43(d) show the distribution of the content of the atoms across the layer thickness in Example 349, Comparative Example 8, Example 356, and Example 357, respectively, of the present invention. DETAILED DESCRIPTION OF THE INVENTION The light receiving member for electrophotography pertaining to the present invention will be described in more detail with reference to the drawings. Fig. 1 is a schematic diagram showing a typical example of the layer structure suitable for the light receiving member for electrophotography pertaining to the present invention. The light receiving member 100 for electrophotography as shown in Fig. 1 comprises an aluminum support 101 for use in the light receiving member for electrophotography and, disposed thereon, a light receiving layer 102 having a layered structure comprising a lower layer 103 constituted with AlSiH and having a part in which the above-mentioned aluminum atoms and silicon atoms are unevenly distributed across the layer thickness and the upper layer 104 constituted with Non-Si(H,X) and containing at least one of carbon atoms, nitrogen atoms and oxygen atoms in the layer region in adjacent with the lower layer. The upper layer 104 has a free surface 105. Support The aluminum support 101 used in the present invention is made of an aluminum alloy. The aluminum alloy is not specifically limited in base aluminum and alloy components. The kind and composition of the components may be selected as desired. Therefore, the aluminum alloy used in the present invention may be selected from pure aluminum, Al-Cu alloy, Al-Mn alloy, Al-Mg alloy, Al-Mg-Si alloy, Al-Zn-Mg alloy, Al-Cu-Mg alloy (duralumin and super duralumin), Al-Cu-Si alloy (lautal), Al-Cu-Ni-Mg alloy (Y-alloy and RR alloy), and aluminum powder sintered body (SAP) which are standardized or registered as a malleable material, castable material, or die casting material in the Japanese Industrial Standards (JIS) , AA Standards, BS Standards, DIN Standards, and International Alloy Registration. The composition of the aluminum alloy used in the invention is exemplified in the following. The scope of the invention is not restricted to the examples. Pure aluminum conforming to JIS-1100 which is composed of less than 1.0 wt% of Si and Fe, 0.05 - 0.20 wt% of Cu, less than 0.05 wt% of Mn, less than 0.10 wt% of Zn, and more than 99.00 wt% of Al. Al-Cu-Mg alloy conforming to JIS-2017 which is composed of 0.05 - 0.20 wt% of Si, less than 0.7 wt% of Fe, 3.5 - 4.5 wt% of Cu, 0.40 - 1.0 wt% of Mn, 0.40 - 0.8 wt% of Mg, less than 0.25 wt% of Zn, and less than 0.10 wt% of Cr, with the remainder being Al. Al-Mn alloy conforming to JIS-3003 which is composed of less than 0.6 wt% of Si, less than 0.7 wt% of Fe, 0.05 - 0.20 wt% of Cu, 1.0 - 1.5 wt% of Mn, and less than 0.10 wt% of Zn, with the remainder being Al. Al-Si alloy conforming to JIS-4032 which is composed of 11.0 - 13.5 wt% of Si, less than 1.0 wt% of Fe, 0.50 - 1.3 wt% of Cu, 0.8 - 1.3 wt% of Mg, less than 0.25 wt% of Zn, less than 0.10 wt% of Cr, and 0.5 - 1.3 wt% of Ni, with the remainder being Al. Al-Mg alloy conforming to JIS-5086 which is composed of less than 0.40 wt% of Si, less than 0.50 wt% of Fe, less than 0.10 wt% of Cu, 0.20 - 0.7 wt% of Mn, 3.5 - 4.5 wt% of Mg, less than 0.25 wt% of Zn, 0.05 - 0.25 wt% of Cr, and less than 0.15 wt% of Ti, with the remainder being Al. An alloy composed of less than 0.50 wt% of Si, less than 0.25 wt% of Fe, 0.04 - 0.20 wt% of Cu, 0.01 - 1.0 wt% of Mn, 0.5 - 10 wt% of Mg, 0.03 - 0.25 wt% of Zn, 0.05 - 0.50 wt% of Cr, 0.05 - 0.20 wt% of Ti or Tr, and less than 1.0 cc of H₂ per 100 g of Al, with the remainder being Al. Al alloy composed of less than 0.12 wt% of Si, less than 0.15% of Fe, less than 0.30 wt% of Mn, 0.5 - 5.5 wt% of Mg, 0.01 - 1.0 wt% of Zn, less than 0.20 wt% of Cr, and 0.01 - 0.25 wt% of Zr, with the remainder being Al. Al-Mg-Si alloy conforming to JIS-6063 which is composed of 0.20 - 0.6 wt% of Si, less than 0.35 wt% of Fe, less than 0.10 wt% of Cu, less than 0.10 wt% of Mn, 0.45 - 0.9 wt% of MgO, less than 0.10 wt% of Zn, less than 0.10 wt% of Cr, and less than 0.10 wt% of Ti, with the remainder being Al. Al-Zn-Mg alloy conforming to JIS-7N01 which is composed of less than 0.30 wt% of Si, less than 0.35 wt% of Fe, less than 0.20 wt% of Cu, 0.20 - 0.7 wt% of Mn, 1.0 - 2.0 wt% of Mg, 4.0 - 5.0 wt% of Zn, less than 0.30 wt% of Cr, less than 0.20 wt% of Ti, less than 0.25 wt% of Zr, and less than 0.10 wt% of V, with the remainder being Al. In this invention, an aluminum alloy of proper composition should be selected in consideration of mechanical strength, corrosion resistance, workability, heat resistance, and dimensional accuracy which are required according to specific uses. For example, where precision working with mirror finish is required, an aluminum alloy containing magnesium and/or copper together is desirable because of its free-cutting performance. According to the present invention, the aluminum support 101 can be in the form of cylinder or flat endless belt with a smooth or irregular surface. The thickness of the support should be properly determined so that the light receiving member for electrophotography can be formed as desired. In the case where the light receiving member for electrophotography is required to be flexible, it can be made as thin as possible within limits not harmful to the performance of the support. Usually the thickness should be greater than 10 um for the convenience of production and handling and for the reason of mechanical strength. In the case where the image recording is accomplished by the aid of coherent light such as laser light, the aluminum support may be provided with an irregular surface to eliminate defective images caused by interference fringes. The irregular surface on the support may be produced by any known method disclosed in Japanese Patent Laid-open Nos. 168156/1985, 178457/1985, and 225854/1985. The support may also be provided with an irregular surface composed of a plurality of spherical dents in order to eliminate defective images caused by interference fringes which occur when coherent light such as laser light is used. In this case, the surface of the support has irregularities smaller than the resolving power required for the light receiving member for electrophotography, and the irregularities are composed of a plurality of dents. The irregularities composed of a plurality of spherical dents can be formed on the surface of the support according to the known method disclosed in Japanese Patent Laid-Open No. 231561/1986. Lower layer According to the present invention, the lower layer is made of an inorganic material which is composed of at least aluminum atoms (Al), silicon atoms (Si), and hydrogen atoms (H). It may further contain atoms (Mc) to control image quality, atoms (CNOc) to control durability, halogen atoms (X), germanium atoms (Ge), and/or tin atoms (Sn), and at least one kind of atoms (Me) selected from the group consisting of alkali metal atoms, and/or alkaline earth metal atoms, and transition metal atoms. The lower layer contains aluminum atoms (Al), silicon atoms, (Si), and hydrogen atoms (H) which are distributed evenly throughout the layer; but it has a part in which their distribution is uneven across the layer thickness. Their distribution should be uniform in a plane parallel to the surface of the support so that uniform characteristics are ensured in the same plane. According to a preferred embodiment, the lower layer contains aluminum atoms (Al), silicon atoms (Si), and hydrogen atoms (H) which are distributed evenly and continuously throughout the layer, with the aluminum atoms (Al) being distributed such that their concentration gradually decreases across the layer thickness toward the upper layer from the support, with the silicon atoms (Si) and hydrogen atoms (H) being distributed such that their concentration gradually increases across the layer thickness toward the upper layer from the support. This distribution of atoms makes the aluminum support and the lower layer compatible with each other and also makes the lower layer and the upper layer compatible with each other. In the light receiving member for electrophotography according to the present invention, it is desirable that the lower layer contains aluminum atoms (Al), silicon atoms (Si), and hydrogen atoms (H) which are specifically distributed across the layer thickness as mentioned above but are evenly distributed in the plane parallel to the surface of the support. The lower layer may further contain atoms (Mc) to control image quality, atoms (CNOc) to control durability, halogen atoms (X), germanium atoms (Ge), and/or tin atoms (Sn), and at least one kind of atoms (Me) selected from the group consisting of alkali metal atoms, alkaline earth metal atoms, and transition metal atoms, which are evenly distributed throughout the entire layer or unevenly distributed across the layer thickness in a specific part. In either case, their distribution should be uniform in a plane parallel to the surface of the support so that uniform characteristics are ensured in the same plane. Fig. 3 to 8 show the typical examples of the distribution of aluminum atoms (Al) and optionally added atoms in the lower layer of the light receiving member for electrophotography in the present invention. (The aluminum atoms (Al) and the optionally added atoms are collectively referred to as "atoms (AM)" hereinafter.) In Figs. 3 to 8, the abscissa represents the concentration (C) of atoms (AM) and the ordinate represents the thickness of the lower layer. (The aluminum atoms (Al) and the optionally added atoms may be the same or different in their distribution across the layer thickness.) The ordinate represents the thickness of the lower layer, with t B representing the position of the end (adjacent to the support) of the lower layer, with t T representing the position of the end (adjacent to the upper layer) of the lower layer. In other words, the lower layer containing atoms (AM) is formed from the t B side toward the t T side. Fig. 3 shows a first typical example of the distribution of atoms (AM) across layer thickness in the lower layer. The distribution shown in Fig. 3 is such that the concentration (C) of atoms (AM) remains constant at C₃₁ between position t B and position t₃₁ and linearly decreases from C₃₁ to C₃₂ between position t₃₁ and position t T . The distribution shown in Fig. 4 is such that the concentration (C) of atoms (AM) linearly decreases from C₄₁ to C₄₂ between position t B and position t T . The distribution shown in Fig. 5 is such that the concentration (C) of atoms (AM) gradually and continuously decreases from C₅₁ to C₅₂ between position t B and position t T . The distribution shown in Fig. 6 is such that the concentration (C) of atoms (AM) remains constant at C₆₁ between position t B and position t₆₁ and linearly decreases from C₆₂ to C₆₃ between t₆₁ and position t T . The distribution shown in Fig. 7 is such that the concentration (C) of atoms (AM) remains constant at C₇₁ between position t B and position t₇₁ and decreases gradually and continuously from C₇₂ to C₇₃ between position t₇₁ and position t T . THe distribution shown in Fig. 8 is such that the concentration (C) of atoms (AM) decreases gradually and continuously from C₈₁ to C₈₂ between position t B and position t T . The atoms (AM) in the lower layer are distributed across the layer thickness as shown in Figs. 3 to 8 with reference to several typical examples. In a preferred embodiment, the lower layer contains silicon atoms (Si) and hydrogen atoms (H) and atoms (AM) in a high concentration of C in the part adjacent to the support, and also contains atoms (AM) in a much lower concentration at the interface t T . In such a case, the distribution across the layer thickness should be made such that the maximum concentration C max of atoms (Al) is 10 atom% or above, preferably 30 atom% or above, and most desirably 50 atom% or above. According to the present invention, the amount of atoms (Al) in the lower layer should be properly established so that the object of the invention is effectively achieved. It is 5 - 95 atom%, preferably 10 - 90 atom%, and most desirably 20 - 80 atom%. Figs. 9 to 16 shows the typical examples of the distribution of silicon atoms (Si), hydrogen atoms (H), and the above-mentioned optional atoms contained across the layer thickness in the lower layer of the light receiving member for electrophotography in the present invention. In Figs. 9 to 16, the abscissa represents the concentration (C) of silicon atoms (Si), hydrogen atoms (H), and optionally contained atoms and the ordinate represents the thickness of the lower layer will be collectively referred to as "atoms (SHM)" hereinafter.) The silicon atoms (Si), hydrogen atoms (H), and optionally contained atoms may be the same or different in their distribution across the layer thickness. t B on the ordinate represents the end of the lower layer adjacent to the support and t T on the ordinate represents the end of the lower layer adjacent to the upper layer. In other words, the lower layer containing atoms (SHM) is formed from the t B side toward the t T side. Fig. 9 shows a first typical example of the distribution of atoms (SHM) across the layer thickness in the lower layer. The distribution shown in Fig. 9 is such that the concentration (C) of atoms (SHM) linearly increases from C₉₁ to C₉₂ between position t B and position t₉₁and remains constant at C₉₂ between position t₉₁ and position t T . The distribution shown in Fig. 10 is such that the concentration (C) of atoms (SHM) linearly increases from C₁₀₁ to C₁₀₂ between position t B and position t T . The distribution shown in Fig. 11 is such that the concentration (C) of atoms (SHM) gradually and continuously increase from C₁₁₁ to C₁₁₂ between position t B and position t T . The distribution shown in Fig. 12 is such that the concentration (C) of atoms (SHM) linearly increases from C₁₂₁ to C₁₂₂ between position t B and position t₁₂₁ and remains constant at C₁₂₃ between position t₁₂₁ and position t T . The distribution shown in Fig. 13 is such that the concentration (C) of atoms (SHM) gradually and continuously increases from C₁₃₁ to C₁₃₂ between position t B and position t₁₃₁ and remains constant at C₁₃₃ between position t₁₃₁ and position t T . The distribution shown in Fig. 14 is such that the concentration (C) of atoms (SHM) gradually and continuously increases from C₁₄₁ to C₁₄₂ between position t B and position t T . The distribution shown in Fig. 15 is such that the concentration (C) of atoms (SHM) gradually increases from substantially zero to C₁₅₁ between position t B and position t₁₅₁ and remains constant at C₁₅₂ between position t₁₅₁ and position t T . ("Substantially zero" means that the amount is lower than the detection limit. The same shall apply hereinafter.) The distribution shown in Fig. 16 is such that the concentration (C) of atoms (SHM) gradually increases from substantially zero to C₁₆₁ between position t B and position t T . The silicon atoms (Si) and hydrogen atoms (H) in the lower layer are distributed across the layer thickness as shown in Figs. 9 to 16 with reference to several typical examples. In a preferred embodiment, the lower layer contains aluminum atoms (Al) and silicon atoms (Si) and hydrogen atoms (H) in a low concentration of C in the part adjacent to the support, and also contains silicon atoms (Si) and hydrogen atoms (H) in a much higher concentration at the interface t T . In such a case, the distribution across the layer thickness should be made such that the maximum concentration C max of the total of silicon atoms (Si) and hydrogen atoms (H) is 10 atom% or above, preferably 30 atom% or above, and most desirably 50 atom% or above. According to the present invention, the amount of silicon atoms (Si) in the lower layer should be properly established so that the object of the invention is effectively achieved. It is 5 - 95 atom%, preferably 10 - 90 atom%, and most desirably 20 - 80 atom%. According to the present invention, the amount of hydrogen atoms (H) in the lower layer should be properly established so that the object of the invention is effectively achieved. It is 0.01 - 70 atom%, preferably 0.1 - 50 atom%, and most desirably 1 - 40 atom%. The above-mentioned atoms (Mc) optionally contained to control image quality are selected from atoms belonging to Group III of the periodic table, except for aluminum atoms (Al) ("Group III atoms" for short hereinafter), atoms belonging to Group V of the periodic table, except for nitrogen atoms (N) ("Group V atoms" for short hereinafter), and atoms belonging to Group VI of the periodic table, except for oxygen atoms (O) ("Group VI atoms" for short hereinafter). Examples of Group III atoms include B (boron), Ga (gallium), In (indium), and Tl (thallium), with B, Al and Ga being preferable. Examples of Group V atoms include P (phosphorus), As (arsenic), Sb (antimony) and Bi (bismuth), with P and As being preferable. Examples of Group VI atoms include S (sulfur), Se (selenium), Te (tellurium), and Po (polonium), with S and Se being preferable. According to the present invention, the lower layer may contain atoms (Mc) to control image quality, which are Group III atoms, Group V atoms, or Group VI atoms. The atoms (Mc) improve the injection of electric charge across the aluminum support and the upper layer and/or improve the transferability of electric charge in the lower layer. They also control conduction type and/or conductivity in the region of the lower layer which contains a less amount of aluminum atoms (Al). In the lower layer, the content of atoms (Mc) to control image quality should be 1 x 10⁻³ - 5 x 10⁴ atom-ppm, preferably 1 x 10⁻¹ - 5 x 10⁴ atom-ppm, and most desirably 1 x 10⁻² - 5 x 10³ atom-ppm. The above-mentioned atoms (NCOc) optionally contained to control image quality are selected from carbon atoms (C), nitrogen atoms (N), and oxygen atoms (O). When contained in the lower layer, carbon atoms (C), and/or nitrogen atoms (N), and/or oxygen atoms (O) as the atoms (CNOc) to control durability improve the injection of electric charge across the aluminum support and the upper layer and/or improve the transferability of electric charge in the lower layer and/or improve the adhesion of the lower layer to the aluminum support. They also control the width of the forbidden band in the region of the lower layer which contains a less amount of aluminum atoms (Al). In the lower layer, the content of atoms (NCOc) to control durability should be 1 x 10³ - 5 x 10⁵ atom-ppm, preferably 5 x 10¹ - 4 x 10⁵ atom-ppm, and most desirably 1 x 10² - 3 x 10³ atom-ppm. The above-mentioned halogen atoms (X) optionally contained in the lower layer are selected from fluorine atoms (F), chlorine atoms (Cl), bromine atoms (Br), and iodine atoms (I). When contained in the lower layer, fluorine atoms (F), and/or chlorine atoms (Cl), and/or bromine atoms (Br), and/or iodine atoms (I) as the halogen atoms (V) compensate for the unbonded hands of silicon atoms (Si) and aluminum atoms (Al) contained mainly in the lower layer and make the lower layer stable in terms of composition and structure, thereby improving the quality of the layer. The content of halogen atoms (X) in the lower layer should be properly established so that the object of the invention is effectively achieved. It is 1 - 4 x 10⁵ atom-ppm, preferably 10 - 3 x 10⁵ atom-ppm, and most desirably 1 x 10² - 2 x 10⁵ atom-ppm. According to the present invention, the lower layer may optionally contain germanium atoms (Ge) and/or tin atoms (Sn). They improve the injection of electric charge across the aluminum support and the upper layer and/or improve the transferability of electric charge in the lower layer and/or improve the adhesion of the lower layer to the aluminum support. They also narrow the width of the forbidden band in the region of the lower layer which contains a less amount of aluminum atoms (Al). These effects suppress interference which occurs when a light of long wavelength such as semiconductor laser is used as the light source for image exposure in the electrophotographic apparatus. The content of germanium atoms (Ge) and/or tin atoms (Sn) in the lower layer should be properly established so that the object of the invention is effectively achieved. It is 1 - 9 x 10⁵ atom-ppm, preferably 1 x 10² - 8 x 10⁵ atom-ppm, and most desirably 5 x 10² - 7 x 10⁵ atom-ppm. According to the present invention, the lower layer may optionally contain, as the alkali metal atoms and/or alkaline earth metal atoms and/or transition metal atoms, magnesium atoms (Mg) and/or copper atoms (Cu) and/or sodium atoms (Na) and/or yttrium atoms (Y) and/or manganese atoms (Mn) and/or zinc atoms (Zn). They disperse hydrogen atoms (H) and halogen atoms (X) uniformly in the lower layer and prevent the cohesion of hydrogen which is considered to cause cracking and peeling. They also improve the injection of electric charge across the aluminum support and the upper layer and/or improve the transferability of electric charge in the lower layer and/or improve the adhesion of the lower layer to the aluminum support. The content of the above-mentioned metals in the lower layer should be properly established so that the object of the invention is effectively achieved. It is 1 - 2 x 10⁵ atom-ppm, preferably 1 x 10² - 1 x 10⁵ atom-ppm, and most desirably 5 x 10² - 5 x 10⁴ atom-ppm. According to the present invention, the lower layer composed of AlSiH is formed by the vacuum deposition film forming method, as in the upper layer which will be mentioned later, under proper conditions for the desired characteristic properties. The thin film is formed by one of the following various methods. Glow discharge method (including ac current discharge CVD, e.g., low-frequency CVD, high-frequency CVD, and microwave CVD, and dc current CVD), ECR-CVD method, sputtering method, vacuum metallizing method, ion plating method, light CVD method, "HRCVD" method (explained below), "FOCVD" method (explained below). (According to HRCVD method, an active substance (A) formed by the decomposition of a raw material gas and the other active substance (B) formed from a substance reactive to the first active substance are caused to react with each other in a space where the film formation is accomplished. According to FOCVD method, a raw material gas and a halogen-derived gas capable of oxidizing said raw material gas are caused to react in a space where the film formation is accomplished.) A proper method should be selected according to the manufacturing conditions, the capital available, the production scale, and the characteristic properties required for the light receiving member for electrophotography. Preferable among these methods are glow discharge method, sputtering method, ion plating method, HRCVD method, and FOCVD method on account of their ability to control the production conditions and to introduce aluminum atoms (Al), silicon atoms (Si), and hydrogen atoms (H) with ease. These methods may be used in combination with one another in the same apparatus. The glow discharge method may be performed in the following manner to form the lower layer of AlSiH. The raw material gases are introduced into an evacuatable deposition chamber, and glow discharge is performed, with the gases being introduced at a desired pressure, so that a layer of AlSiH is formed as required on the surface of the support placed in the chamber. The raw material gases may contain a gas to supply aluminum atoms (Al), a gas to supply silicon atoms (Si), a gas to supply hydrogen atoms (H), an optional gas to supply atoms (Mc) to control image quality, an optional gas to supply atoms (CNOx) to control durability, an optional gas to supply halogen atoms (X), an optional gas to supply atoms (GSc), germanium atoms (Ge) and tin atoms (Sn), and an optional gas to supply atoms (Me) (at least one kind of alkali metal atoms, alkaline earth metal atoms, and transition metal atoms). The HRCVD may be performed in the following manner to form the lower layer of AlSiH. The raw material gases are introduced all together or individually into an evacuatable deposition chamber, and glow discharge is performed or the gases are heated, with the gases being introduced at a desired pressure, during which a first active substance (A) is formed and a second active substance (B) is introduced into the deposition chamber, so that a layer of AlSiH is formed as required on the surface of the support placed in the chamber. The raw material gases may contain a gas to supply aluminum atoms, (Al), a gas to supply silicon atoms (Si), an optional gas to supply atoms (Mc) to control image quality, an optional gas to supply atoms (CNOc) to control durability, an optional gas to supply halogen atoms (X), an optional gas to supply atoms (GSc) (germanium atoms (Ge) and tin atoms (Sn)), and an optional gas to supply atoms (Me) (at least one kind of alkali metal atoms, alkaline earth metal atoms, and transition metal atoms). A second active substance (B) is formed by introducing a gas to supply hydrogen into the activation chamber. Said first active substance (A) and said second active substance are individually introduced into the deposition chamber. The FOCVD method may be performed in the following manner to form the lower layer of AlSiH. The raw material gases are introduced into an evacuatable deposition chamber, and chemical reactions are performed, with the gases being introduced at a desired pressure, so that a layer of AlSiH is formed as required on the surface of the support placed in the chamber. The raw material gases may contain a gas to supply aluminum atoms (Al), a gas to supply silicon atoms (Si), a gas to supply hydrogen atoms (H), an optional gas to supply atoms (Mc) to control image quality, an optional gas to supply atoms (CNOc) to control durability, an optional gas to supply halogen atoms (X), an optional gas to supply atoms (GSc) (germanium atoms (Ge) and tin atoms (Sn)), and an optional gas to supply atoms (Me) (at least one kind of alkali metal atoms, alkaline earth metal atoms, and transition metal atoms). They may be introduced into the chamber altogether or individually, and a halogen (X) gas is introduced into the chamber separately from said raw materials gas, and these gases are subjected to chemical reaction in the deposition chamber. The sputtering method may be performed in the following manner to form the lower layer of AlSiH. The raw material gases are introduced into a sputtering deposition chamber, and a desired gas plasma environment is formed using an aluminum target and an Si target in an inert gas of Ar or He or an Ar- or He-containing gas. The raw material gases may contain a gas to supply hydrogen atoms (H), an optional gas to supply atoms (Mc) to control image quality, an optional gas to supply atoms (CNOc) to control durability, an optional gas to supply halogen atoms (X), an optional gas to supply atoms (GSc) (Germanium atoms (Ge) and tin atoms (Sn)), and an optional gas to supply atoms (Me) (at least one kind of alkali metal atoms, alkaline earth metal atoms, and transition metal atoms). If necessary, a gas to supply aluminum atoms (Al) and/or to supply silicon atoms (Si) are introduced into the sputtering chamber. The ion plating method may be performed in the same manner as the sputtering method, except that vapors of aluminum and silicon are passed through the gas plasma enviromnent. The vapors of aluminum and silicon are produced from aluminum and silicon polycrystal or single crystal placed in a boat which is heated by resistance or electron beams (EB method). According to the present invention, the lower layer contains aluminum atoms (Al), silicon atoms (Si), hydrogen atoms (H), optional atoms (Mc) to control image quality, optional atoms (CNOc) to control durability, optional halogen atoms (X), optional germanium atoms (Ge), optional tin atoms (En), optional alkali metal atoms, optional alkaline earth metal atoms, and optional transition metal atoms (collectively referred to as atoms (ASH) hereinafter), which are distributed in different concentrations across the layer thickness. The lower layer having such a depth profile can be formed by controlling the flow rate of the feed gas to supply atoms (ASH) according to the desired rate of change in concentration. The flow rate may be changed by operating the needle valve in the gas passage manually or by means of a motor, or it may be changed by any of customary means such as by properly adjusting the mass flow controller manually or by means of a programmable control apparatus. In the case where the sputtering method is used, the lower layer having such a depth profile can be formed, as in the glow discharge method, it can be achieved by controlling the flow rate of the gaseous raw material to supply atoms (ASH) according to the desired rate of change in concentration and introducing the gas into the deposition chamber. Alternatively, it is possible to use a sputtering target comprising a Al-Si mixture in which the mixing ratio of Al and Si is properly changed in the direction of layer thickness of the target. According to the present invention, the gas to supply Al includes, for example, AlCl₃, AlBr₃, AlI₃, Al(CH₃)₂Cl, Al(CH₃)₃, Al(OCH₃)₃, Al(C₂H₅)₃, Al(OC₂H₅)₃, Al(i-C₄H₉)₃, Al(i-C₃H₇)₃, Al(C₃H₇)₃ and (Al(OC₄H₉)₃. These gases to supply Al may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. According to the present invention, the gas to supply Si includes, for example, gaseous or gasifiable silicohydrides (silanes) such as Si₂, SiH₂H₆, Si₃H₈ and Si₄H₁₀. SiH₄ and Si₂H₆ are preferable from the standpoint of each of handling and the efficient supply of Si. These gases to supply Si may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. According to the present invention, the gas to supply H includes, for example, silicohydrides (silanes) such as SiH₄, Si₂H₆, Si₃H₈ and Si₄H₁₀. The amount of hydrogen atoms contained in the lower layer may be controlled by regulating the flow rate of the feed gas to supply hydrogen and/or regulating the temperature of the support and/or regulating the electric power for discharge. The lower layer may contain atoms (Mc) to control image quality, such as Group III atoms, Group V atoms and Group VI atoms. This is accomplished by introducing into the deposition chamber the raw materials to form the lower layer together with a raw material to introduce Group III atoms, a raw material to introduce Group V atoms, or a raw material to introduce Group VI atoms. The raw material to introduce Group III atoms, the raw material to introduce Group V atoms, or the raw material to introduce Group VI atoms may desirably be gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions. The raw material to introduce Group III atoms, especially boron atoms, include, for example, boron, hydrides such as B₂H₆, B₅H₉, B₅H₁₁, B₆H₁₀, B₆H₁₂ and B₆H₁₄, and boron halides such as BF₃, BCl₃ and BBr₃. Additional examples includes GaCl₃, Ga(CH₃)₃, InCl₃ and TiCl₃. The raw material to introduce Group V atoms, especially phosphorus atoms, include, for example, phosphorus hydrides such as PH₃, P₂H₄ and phosphorus halides such as PH₄I, PF₃, PF₅, PCl₃, PBr₃, PBr₅ and PI₃. Other examples effective to introduce Group V atoms include AsH₃, AsF₃, AsCl₃, AsBr₃, AsF₅, SbH₃, SbF₃, SbF₅, SbCl₃, SbCl₅, BiH₃, BiCl₃ and BiBr₃. The raw material to introduce Group VI atoms includes, for example, gaseous or gasifiable substances such as H₂, SF₄, SF₆, SO₂, SO₂F₂, COS, CS₂, CH₃SH, C₂H₅SH, C₄H₄S, (CH₃)₂S and S(C₂H₅)₂S. Other examples include gaseous of gasifiable substances such as SeH₂, SeF₆, (CH₃)₂)Se, (C₂H₅)₂Se. TeH₂, TeF₆, (CH₃)₂Te and (C₂H₅)₂Te. These raw materials to introduce atoms (Mc) to control image quality may be diluted with an inert gas such as H₂, He, Ar and Ne. According to the present invention, the lower layer may contain atoms (CNOc) to control durability, e.g., carbon atoms (C), nitrogen atom (N), and oxygen atoms (O). This is accomplished by introducing into the deposition chamber the raw materials to form the lower layer, together with a raw material to introduce carbon atoms (C), or a raw material to introduce nitrogen atoms (N), or a raw material to introduce oxygen atoms (O). Raw materials to introduce carbon atoms (C), nitrogen atoms (N), or oxygen atoms (O) may desirably be in the gaseous form at normal temperature and under normal pressure or may be readily gasifiable under the layer forming conditions. A raw material gas to introduce carbon atoms (C) includes those composed of C and H atoms such as saturated hydrocarbons having 1 to 4 carbon atoms, ethylene, series hydrocarbons having 2 to 4 carbon atoms and acetylene series hydrocarbons having 2 to 3 carbon atoms. Examples of the saturated hydrocarbons include specifically methane (CH₄), ethane (C₂H₆), propane (C₃H₈), n-butane (n-C₄H₁₀) and pentane (C₅H₁₂), Examples of the ethylene series hydrocarbons include ethylene (C₂H₄), propylene (C₃H₆), butene-1 (C₄H₈), butene-2 (C₄H₈), isobutylene (C₄H₈) and pentene (C₅H₁₀). Examples of acetylene series hydrocarbon include acetylene (C₂H₂), methylacetylene (C₃H₄) and butyne (C₄H₆). The raw material gas composed of Si, C, and H includes alkyl silicides such as Si(CH₃)₄ and Si(C₂H₅)₄. Additional examples include gases of halogenated hydrocarbons such as of CF₄, CCl₄ and CH₃CF₃, which introduce carbon atoms (C) as well as halogen atoms (X). Examples of the raw material gas to introduce nitrogen atoms (N) include nitrogen and gaseous or gasifiable nitrogen compounds (e.g., nitrides and azides) which are composed of nitrogen and hydrogen, such as ammonia (NH₃), hydrazine (H₂NNH₂), hydrogen azide (HN₃), and ammonium azide (NH₄N₃). Additional examples include halogenated nitrogen compounds such as nitrogen trifluoride (F₃N) and nitrogen tetrafluoride (F₄N₂), which can introduce nitrogen atoms as well as halogen atoms (X). Examples of the raw material gas to introduce oxygen atoms (O) include oxygen (O₂), ozone (O₃), nitrogen monoxide (NO), nitrogen dioxide (NO₂), trinitrogen tetraoxide (N₃O₄), dinitrogen pentaoxide (N₂O₅) and nitrogen trioxide (NO₃), as well as lower siloxanes such as disiloxane (H₃SiOSiH₃) and trisiloxane (H₃SiOSiH₂OSiH₃) which are composed of silicon atoms (Si), oxygen atoms (O) and hydrogen atoms (H). Examples of the gas to supply hydrogen atoms include halogen gases and gaseous or gasifiable halides, interhalogen compounds, and halogen-substituted silane derivatives. Additional examples include gaseous or gasifiable halogen-containing silicohydrides composed of silicon atoms and halogen atoms. The halogen compounds that can be suitably used in the present invention include halogen gases such as fluorine, chlorine, bromine and iodine; and interhalogen compounds such as BrF, ClF, ClF₃, BrF₅, BrF₃, IF₃, IF₇, ICl and IBr. Examples of the halogen-containing silicon compounds or halogen-substituted silane compounds, include specifically silane (SiH₄) and halogenated silicon such as Si₂F₆, SiCl₄ and SiBr₄. In the case where the halogen-containing silicon compounds is used to form the light receiving member for electrophotography by the glow discharge method or HRCVD method, it is possible to form the lower layer composed of AlSiH containing halogen atoms on the support without using a silicohydride gas to supply silicon atoms. In the case where the lower layer containing halogen atoms is formed by the glow discharge method of HRCVD method, a silicon halide gas is used as the gas to supply silicon atoms. The silicon halide gas may be mixed with hydrogen or a hydrogen-containing silicon compound gas to facilitate the introduction of hydrogen atoms at a desired level. The above-mentioned gases may be used individually or in combination with one another at a desired mixing ratio. The raw materials to form the lower layer which are used in addition to the above-mentioned halogen compounds or halogen-containing silicon compounds include gaseous or gasifiable hydrogen halides such as HF, HCl, HBr and HI; and halogen-substituted silicohydrides such as SiH₃F₂, SiH₂F₂, SiHF₃, SiH₂I₂, SiS₂Cl₂, SiHCl₃, SiH₂Br₂ and SiHBr₃. Among these substances, the hydrogen-containing halides are a preferred halogen-supply gas because they supply the lower layer with halogen atoms as well as hydrogen atoms which are very effective for the control of electric or photoelectric characteristics. The introduction of hydrogen atoms into the lower layer may also be accomplished in another method by inducing discharge in the deposition chamber containing a silicohydride such as SiH₄, Si₂H₆, Si₃H₈ and Si₄H₁₀ and a silicon compound to supply silicon atoms (Si). The amount of hydrogen atoms (H) and/or halogen atoms (X) to be introduced into the lower layer may be controlled by regulating the temperature of the support, the electric power for discharge, and the amount of raw materials for hydrogen atoms and halogen atoms to be introduced into the deposition chamber. The lower layer may contain germanium atoms (Ge) or tin atoms (Sn). This is accomplished by introducing into the deposition chamber the raw materials to form the lower layer together with a raw material to introduce germanium atoms (Ge) or tin atoms (Sn) in a gaseous form. The raw material to supply germanium atoms (Ge) or the raw material to supply tin atoms (Sn) may be gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions. The substance that can be used as a gas to supply germanium atoms (Ge) include gaseous or gasifiable germanium hydrides such as GeH₄, Ge₂H₆, Ge₃H₈ and Ge₄H₁₀. Among them, GeH₄, Ge₂H₆ and Ge₃H₈ are preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of germanium atoms (Ge). Other effective raw materials to form the lower layer include gaseous or gasifiable germanium hydride-halides such as GeHF₃, GeH₂F₂, GeH₃F, GeHCl₃, GeH₂Cl₂, GeH₃Cl, GeHBr₃, GeH₂Br₂. GeH₃Br, GeHI₃, GeH₂I₂ and GeH₃I and germanium halides such as GeF₄, GeCl₄, GeBr₄, GeI₄, GeF₂, GeCl₂, GeBr₂ and GeI₂. The substance that can be used as a gas to supply tin atoms (Sn) include gaseous or gasifiable tin hydrides such as SnH₄, Sn₂H₆, Sn₃H₈ and Sn₄H₁₀. Among them, SnH₄, Sn₂H₆ and Sn₃H₈ are preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of tin atoms (Sn). Other effective raw materials to form the lower layer include gaseous or gasifiable tin hydride-halides such as SnHF₃, SnH₂F₂, SnH₃F, SnHCl₃, SnH₂Cl₂, SnH₃Cl, SnHBr₃, SnH₂Br₂, SnH₃Br, SnHI₃, SnH₂I₂ and SnH₃I, and tin halides such as SnF₄, SnCl₄, SnBr₄, SnI₄, SnF₂, SnCl₂, SnBr₂ and SnI₂. The gas to supply GSc may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. The lower layer may contain magnesium atoms (Mg). This is accomplished by introducing into the deposition chamber the raw materials to form the lower layer together with a raw material to introduce magnesium atoms (Mg) in a gaseous form. The raw material to supply magnesium atoms (Mg) may be gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions. The substance that can be used as a gas to supply magnesium atoms (Mg) include organometallic compounds containing magnesium atoms (Mg). Bis(cyclopentadienyl)magnesium (II) complex salt (Mg(C₅H₅)₂) is preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of magnesium atoms (Mg). The gas to supply magnesium atoms (Mg) may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. The lower layer may contain copper atoms (Cu). This is accomplished by introducing into the deposition chamber the raw materials to form the lower layer together with a raw material to introduce copper atoms (Cu) in a gaseous form. The raw material to supply copper atoms(Cu) may be gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions. The substance that can be used as a gas to supply copper atoms (Cu) include organometallic compounds containing copper atoms (Cu). Copper (II) bisdimethylglyoximate Cu(C₄H₇N₂O₂)₂ is preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of Cu atoms. The gas to supply copper atoms (Cu) may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. The lower layer may contain sodium atoms (Na) or yttrium atoms (Y) or manganese atoms (Mn), zinc atoms (Zn), etc. This is accomplished by introducing into the deposition chamber the raw materials to form the lower layer together with a raw material to introduce sodium atoms (Na) or yttrium (Y) or manganese atoms (Mn) or zinc atoms (Zn). The raw material to supply sodium atoms (Na) or yttrium atoms (Y) or mangnaese atoms (Mn) or zinc atoms (Zn) may be gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions. The substance that can be used as a gas to supply sodium atoms (Na) includes sodium amine (NaNH₂) and organometallic compounds containing sodium atoms (Na). among them, sodium amine (NaNH₂) is preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of sodium atoms (Na). The substance that can be used as a gas to supply yttrium atoms (Y) includes organometallic compounds containing yttrium atoms (Y). Triisopropanol yttrium Y(Oi-C₃H₇)₃ is preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of yttrium atoms (Y). The substance that can be used as a gas to supply manganese atoms (Mn) includes organometallic compounds containing manganese atoms (Mn). Monomethylpentacarbonylmanganese Mn(CH₃)(CO)₅, is preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of sodium atoms (Na). The substance that can be used as a gas to supply zinc atoms (Zn) includes organometallic compounds containing zinc atoms (Zn). Diethyl zinc Zn(C₂H₅)₂ is preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of zinc atoms (Zn). The gas to supply sodium atoms (Na) or yttrium atoms (Y) or manganese atoms (Mn) or zinc atoms (Zn) may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. According to the present invention, the lower layer should have a thickness of 0.03 - 5 um, preferably, 0.01 - 1 um, and most desirable 0.05 - 0.5 um, from the standpoint of the desired electrophotographic characteristics and economic effects. According to the present invention, the lower layer has an interface region which is in contact with the aluminum support and contains less than 95% of the aluminum atoms contained in the aluminum support. If the interface region contains more than 95% of the aluminum atoms contained in the aluminum support, it merely functions as the support. The lower layer also has an interface which is in contact with the upper layer and contains more than 5% of the aluminum atoms contained in the lower layer. If the interface region contains less than 5% of the aluminum atoms contained in the lower layer, if merely functions as the upper layer. In order to form the lower layer of AlSiH which has the characteristic properties to achieve the object of the present invention, it is necessary to properly establish the gas pressure in the deposition chamber nd the temperature of the support. The gas pressure in the deposition chamber should be properly selected according to the desired layer. It is usually 1 x 10⁻⁵ - 10 Torr, preferably 1 x 10⁻⁴ - 3 Torr, and most desirably 1 x 10⁻⁴ - 1 Torr. The temperature (Ts) of the support should be properly selected according to the desired layer. It is usually 50 - 600°C, and preferably 100 - 400°C. In order to form the lower layer of AlSiH by the glow discharge method according to the present invention, it is necessary to properly establish the discharge electric power to be supplied to the deposition chamber according to the desired layer. It is usually 5 x 10⁻⁵ - 10 W/cm³, preferably 5 x 10⁻⁴ - 5 W/cm³ and most desirably 1 x 10⁻³ - 1 to 2 x 10⁻³ W/cm³. The gas pressure of the deposition chamber, the temperature of the support, and the discharge electric power to be supplied to the deposition chamber mentioned above should be established interdependently to that the lower layer having the desired characteristic properties can be formed. Upper layer The upper layer in this invention is composed of a Non-Si (H, X) and has desired photoconductivity. The upper layer of this invention contains, in at least the layer region adjacent with the lower layer, carbon atoms (C), and/or nitrogen atoms (N), and/or oxygen atoms (O), and optional atoms (M) to control conductivity but contains no substantial germanium atoms (Ge) and tin atoms (Sn). However, the upper layer may contain in other layer regions at least one of the atoms (M) to control the conductivity, carbon atoms (C), nitrogen atoms (N), oxygen atoms (O), germanium atoms (Ge) and tin atoms (Sn). Particularly, in the layer region of the upper layer near the free surface, at least one of carbon atoms (C), nitrogen atoms (N) and oxygen atoms (O) is preferably contained. The upper layer may contain in the layer region of the upper layer at least adjacent with the lower layer carbon atoms (C), and/or nitrogen atoms (N), and/or oxygen atoms (O) and optional atoms (M) to control the conductivity, which are distributed evenly throughout the layer region or distributed evenly throughout the layer region but may be contained uneven distribution across the layer thickness in a part. However, in either of the cases, their distribution should be uniform in a plane parallel to the surface of the support so that uniform characteristics are ensured in the same plane. In a case where the upper layer contains in other layer regions than the layer region at least in adjacent with the lower layer contains at least one of atoms (M) to control the conductivity, carbon atoms (C), nitrogen atoms (N), oxygen atoms (O), germanium atoms (Ge) and tin atoms (Sn), the atoms (M) to control the conductivity, carbon atoms (C), nitrogen atoms (N), oxygen atoms (O), germanium (Ge) , tin atoms (Sn) may be distributed uniformly in the layer region, or they may be contained in a portion uniformly distributed in the layer region but not unevenly distributed across the layer thickness. However, in either of the cases, their distribution should be uniform in a plane parallel to the surface of the support so that uniform characteristics are ensured in the same plane. According to the present invention, the upper layer may contain at least one of alkali metals, alkaline earth metal and transition metals. The atoms are incorporated in the entire layer region or a partial layer region of the upper layer, and they may be uniformly distributed throughout the region, or distributed evenly through the layer region but may contained unevenly distributed across the layer thickness. However, they should be incorporated uniformly in either of the cases in a plane parallel to the surface of the support so that uniform characteristics are ensured in the same plane. A layer region (hereinafter simply referred to as "layer region (M)") containing atoms (M) to control the conductivity (hereinafter simply referred to as "atoms (M)") and a layer region of the upper layer at least in adjacent with the lower layer (hereinafter simply referred to as "layer region (CNO B )") containing carbon atoms (C), and/or nitrogen atoms (N), and/or oxygen atoms (O) (hereinafter simply referred to as "atoms (CNO)") may be a substantially identical layer region or may have in common a portion at least on the side of the surface of the layer region (CNO B ), or may be contained within the layer region (CNO B ). Further, the layer region (hereinafter simply referred to as "layer region (GS)") containing germanium atoms (Ge) and/or tin atoms (Sn) (hereinafter simply referred to as "atoms (GS)") may contain a portion on the surface of the layer region (CNO B ). Further, the layer region containing atoms (CNO) other than the layer region (CNO B ) (hereinafter simply referred to as "layer region (CNO T )" and the layer region (CNO B ) and the layer region (CNO T ) being collectively referred as "layer region (CNO)"), the layer region (M), the layer region (GS) and the layer region (NYMZ) containing at least one of alkali metals, alkaline earth metals and transition metals may be substantially an identical layer region, may have in common at least a portion for the respective layer regions, or may have in common substantially the respective layer regions. Fig. 17 to 36 show the typical examples of the profile of atoms (M) across the layer thickness in the layer region (M), a typical example of the profile of atoms (CNO) in the layer region (CNO) across the layer thickness, a typical example of the profile of the atoms (GS) contained the layer region (GS) across the layer thickness, and a typical example of the profile of alkali metal atoms, alkaline earth metal atoms or transition metal atoms contained in the layer region incorporating at least one of alkali metal atoms, alkaline earth metal atoms and transition metal atoms across the layer thickness in the upper layer of the light receiving member for use in electrophotography in this invention (hereinafter the layer regions are collectively referred to as "layer region (Y)" and these atoms are collectively referred to as "atoms (Y)"). Accordingly, Fig. 17 to 36 show the typical examples of the profiles of the atoms (Y) contained in the layer region (Y) across the layer thickness, in which one layer region (Y) is contained in the upper layer in a case where the layer region (M), layer region (CNO), layer region (GS), a layer region containing at least one of alkali metal, alkaline earth metal and transition metal are substantially the identical layer region, or a plurality of the layer regions (Y) are contained in the upper layer if they are not substantially identical layer region. In Figs. 17 to 36, the abscissa represents the distribution concentration C of the atoms (Y) and ordinate represents the thickness of the layer region (Y), while t B represents the position of the end of the layer region (Y) on the side of the lower layer and t T represents the position of the end of the layer region (Y) on the side of the free surface. That is, the layer region (Y) containing the atoms (Y) is formed from the side t B to the side t T . Fig. 17 shows a first typical example of the profile of atoms (Y) contained in the layer region (Y) across the layer thickness. In the example shown in Fig. 17, the atoms (Y) contained is distributed such that the concentration increases gradually and continuously from C₁₇₁ to C₁₇₂ from the position t B to the position t T . In the example shown in Fig. 18, the atoms (Y) contained is distributed such that the concentration C linearly increases from C₁₈₁ to C₁₈₂ from the position t B to the position t₁₈₁ and takes a constant value of C₁₈₃ from the position t₁₈₁ to the position t T . In the example shown in Fig. 19, the atoms (Y) contained is distributed such that the concentration C takes a constant value of C₁₉₁ from the position t B to the position t₁₉₁, gradually and continuously increases from C₁₉₁ to C₁₉₂ from the position t₁₉₁ to the position t₁₉₂ and then takes a constant value of concentration t₁₉₃ from the position t₁₉₂ to the position t T . In the example shown in Fig. 20, the atoms (Y) contained is distributed such that the concentration C takes a constant value of C₂₀₁ from the position t B to the position t₂₀₁, takes a constant value C₂₀₂ from the position t₂₀₁ to the position t₂₀₂ and takes a constant value C₂₀₃ from the position t₂₀₂ to the position t T . In the example shown in Fig. 21, the atoms (Y) contained is distributed such that the concentration C takes a constant value of the C₂₁₁ from the position t B to the position t T . In the example shown in Fig. 22, the atoms (Y) contained is distributed such that the concentration C takes a constant value C₂₂₁ from the position t B to the position t₂₂₁, decreases gradually and continuously from C₂₂₂ to C₂₂₃ from the position t₂₂₁ to the position t T . In the example shown in Fig. 23, the atoms (Y) contained is distributed such that the concentration C gradually and continuously decreases from C₂₃₁ to the C₂₃₂ from the the position t B to the position t T . In the example shown in Fig. 24 the atoms (Y) contained is distributed such that the distribution C takes a constant value C₂₄₁ from the position t B to the position t₂₄₁, gradually and continuously decreases from the C₄₄₂ to the concentration substantialy equal to zero from the position t₂₄₁, to the position t T (substantially zero means here and hereinafter the concentration lower than the detectable limit). In the example shown in Fig. 25, the atoms (Y) contained is distributed such that the concentration C gradually and continuously decreases from C₂₅₁ to substantially equal to zero from the position t B to the position t T . In the example shown in Fig. 26, the atoms (Y) contained is distributed such that the concentration C remains constant at C₂₆₁ from the position t B to the position t₂₆₂, lineary decreases to C₂₆₂ from the position t₂₆₁ to the position t T and remains at C₂₆₂ at the position t T . In the example shown in Fig. 27, the atoms (Y) contained is distributed such that the concentration C linearly decreases from C₂₇₁ to substantially equal to zero from the position t B to the position t T . In the example shown in Fig. 28, the atoms (Y) contained is distributed such that the concentration C remaining constant at C₂₈₁ from the position t B to the position t₂₈₁ and linearly decreases from C₂₈₁ to C₂₈₂ from the position t₂₈₂ to the position t T . In the example shown in Fig. 29, the atoms (Y) contained is distributed such that the concentration C gradually and continuously decreases from C₂₉₁ to C₂₉₂ from the position t B to the position t T . In the example shown in Fig. 30, the atoms (Y) contained is distributed such that the concentration C remains at a constant value C₃₀₁ from the position t B to the position t₃₀₁, linearly decreases from C₃₀₂ to C₃₀₃ from the position t₃₀₁ to the position t T . In the example shown in Fig. 31, the atoms (Y) contained is distributed such that the concentration C gradually and continuously increases from C₃₁₁ to C₃₁₂ from the position t B to the position t₃₁₁ and remains at a constant value C₃₁₃ from the position t₃₁₁ to the position t T . In the example shown in Fig. 32, the atoms (Y) contained is distributed such that the concentration C gradually and continuously increases from C₃₂₁ to C₃₂₂ from the position t B to the position t T . In the example shown in Fig. 33. the atoms (Y) contained is distributed such that the concentration C gradually and continuously increases from substantially zero to C₃₃₁ from the position t B to the position t₃₃₁ and remains constant at C₃₃₂ between position t₃₃₁ and position t T . In the example shown in Fig. 34, the atoms (Y) contained is distributed such that the concentration C gradually and continuously increases from substantially zero to C₃₄₁ from the position t B to the position t T . In the example shown in Fig. 35, the atoms (Y) contained is distributed such that the concentration C linearly increases from C₃₅₁ to C₃₅₂ from the position t B to the position t₃₅₁, and remains constant at C₃₅₂ from the position t₃₅₁ to the position t T . In the example shown in Fig. 36, the atoms (Y) contained is distributed such that the concentration C linearly increases from C₃₆₁ to C₃₆₂ from the position t B to the position t T . The atoms (M) to control the conductivity can include so-called impurities in the field of the semiconductor, and those used in this invention include atoms belonging to the group III of the periodical table giving p type conduction (hereinafter simply referred to as "group III atoms"), or atoms belonging to the group V of the periodical table except for nitrogen atoms (N) giving n-type conduction (hereinafter simply referred to as "group V atoms") and atoms belonging to the group VI of the periodical table except oxygen atoms (O) (hereinafter simply referred to as "group VI atoms"). Examples of the group III atoms can include B (boron), Al (aluminum), Ga (gallium), In (indium), Tl (thallium), etc., B, Al, Ga being particularly preferred. Examples of the group V atoms can include, specifically, P (phosphorus), As (arsenic), Sb (antimony), Bi (bismuth), P, As being particularly preferred. Examples of the group VI atoms can include, specifically, S (sulfur), Se (selenium), Te (tellurium) and Po (polonium), S and Se being particularly preferred. Incorporation of group III atoms, group V atoms or group VI atoms as the atoms (M) to control the conductivity into the layer region (M) in the present invention, can provide the effect, mainly, of controlling the conduction type and/or conductivity, and/or the effect of improving the charge injection between the layer region (M) and the layer region of the upper region other the layer region (M). In the layer region (M), the content of atoms (M) to control the conductivity is preferably 1 x 10⁻³ - 5 x 10⁴ atom-ppm, more preferably, 1 x 10⁻² - 1 x 10⁴ atom-ppm and, most preferably, 1 x 10⁻¹ - 5 x 10³ atom-ppm. Particularly, in a case where the layer region (M) contains carbon atoms (C), and/or nitrogen atoms (N), and/or oxygen atoms (O) described later by 1 x 10³ atom-ppm, the layer region (M) contains atoms (M) to control the conductivity preferably from 1 x 10⁻³ - 1 x 10³ atom-ppm and, in a case if the content of the carbon atoms (C) and/or nitrogen atom (N) and/or oxygen atom (O) is in excess of 1 x 10³ atom-ppm, the content of the atoms (M) to control the conductivity is preferably 1 x 10⁻¹ - 5 x 10⁴ atom-ppm. According to this invention, incorporation of the carbon atoms (C) and/or nitrogen atoms (N) and/or oxygen atoms (O) in the layer region (CNO) can mainly obtain an effect of increasing the dark resistance and/or hardness, and/or improving the control for the spectral sensitivity and/or enhancing the close bondability between the layer region (CNO) and the layer region of the upper layer other than the layer region (CNO). The content of carbon atoms (C), and/or nitrogen atoms (N) and/or oxygen atoms (O) in the layer region (CNO) is preferably 1 - 9 x 10⁵ atom-ppm, more preferably, 1 x 10¹ - 5 x 10⁵ atom-ppm and most preferably, 1 x 10² - 3 x 10⁵ atom-ppm. In addition, if it is intended to increase the dark resistance and/or the hardness, the content is preferably 1 x 10³ - 9 x 10⁵ atom-ppm and, preferably, it is 1 x 10² - 5 x 10⁵ atom-ppm in a case where the spectral sensitivity is intended to be controlled. In this invention, the spectral sensitivity can be controlled mainly and, particularly, sensitivity to the light of longer wave length can be improved in the case of using light of longer wavelength such as of a semiconductor laser by incorporating germanium atoms (Ge) and/or tin atoms (Sn) to the layer region (GS). The content of germanium atoms (Ge) and/or tin atoms (Sn) contained in the layer region is preferably 1 - 9.5 x 10⁵ atom-ppm, more preferably, 1 x 10² - 8 x 10⁵ atom-ppm and, most suitably, 5 x 10² - 7 x 10⁵ atom-ppm. In addition, hydrogen atoms (H) and/or halogen atoms (X) contained in the upper layer in this invention can compensate the unbonded bands of silicon atoms (Si), thereby improving the quality of the layer. The content of hydrogen atoms (H) or the sum of the hydrogen atoms (H) and halogen atoms (X) in the upper layer is suitably 1 x 10³ - 7 x 10⁵ atom-ppm, while the content of halogen atoms (X) is preferably 1 - 4 x 10⁵ atom-ppm. Particularly, in a case where the content of the carbon atoms (C), and/or nitrogen atoms (N) and/or oxygen atoms (O) in the upper layer is less than 3 x 10⁵ atom-ppm, the content of hydrogen atoms (H) or the sum of hydrogen atoms (H) and halogen atoms (X) is desirably 1 x 10³ - 4 x 10⁵ atom-ppm. Furthermore, in a case where the upper layer is composed of poly-Si(H,X), the content of hydrogen atoms (H) or the sum of hydrogen atoms (H) and halogen atoms (X) in the upper layer is preferably 1 x 10³ - 2 x 10⁵ atom-ppm and in a case where the upper layer is composed of A-Si(H,X), it is preferably 1 x 10⁴ - 7 x 10⁵ atom-ppm. In this invention, the content of at least one of alkali metal, alkaline earth metal and transition metal in the upper layer is preferably 1 x 10⁻³ - 1 x 10⁴ atom-ppm, more preferably, 1 x 10⁻² - 1 x 10³ atom-ppm and most suitably 5 x 10⁻² - 5 x 10² atom-ppm. In this invention, the upper layer composed of Non-Si(H,X) can be prepared by the same vacuum deposition film formation as that for the lower layer described above, and glow discharge, sputtering, ion plating, HRCVD process, FOCVD process are particularly preferred. These methods may be used in combination in one identical device system. For instance, the glow discharge method may be performed in the following manner to form the upper layer composed of Non-Si(H,X). The raw material gases are introduced into an evacuatable deposition chamber and glow discharge is performed with the gases being introduced at a desired pressure, so that a layer of Non-Si(H,X) is formed as required on the surface of the support situated at a predetermined position and previously formed with a predetermined lower layer. The raw material gases may contain a gas to supply silicon atoms (Si), a gas to supply hydrogen atoms (H), and/or a gas to supply halogen atoms (X), an optional gas to supply atoms (M) to control the conductivity, and/or a gas to supply carbon atoms (C) , and/or a gas to supply nitrogen atoms (N), and/or a gas to supply oxygen atoms (O) , and/or a gas to supply germanium atoms (Ge), and/or a gas to supply tin atoms (Sn) and/or a gas to supply at least one of alkali metal, alkaline earth metal and transition metal. The HRCVD process may be performed in the following manner to form the upper layer composed of Non-Si(H,X). The raw material gases are introduced individually or altogether into an evacuatable deposition chamber, and glow discharge performed or the gases are heated with the gases being introduced at a desired pressure, during which active substance (A) is formed and another active substance (B) is introduced into the deposition chamber, so that a layer of Non-Si(H,X) is formed as required on the surface of the support situated at a predetermined position and formed with a predetermined lower layer thereon in the deposition chamber. The raw material gases may contain a gas to supply silicon atoms (Si), a gas to supply halogen atoms (X), an optional gas to control conductivity (M), and/or a gas to supply carbon atoms (C), and/or a gas to supply nitrogen atoms (N), and/or a gas to supply oxygen atoms (O), and/or a gas to supply germanium atoms (Ge), and/or a gas to supply tin atoms (Sn) and/or a gas to supply at least one of alkali metal, alkaline earth metal and transition metal. Another active substance (B) is formed by introducing a gas to supply hydrogen activation space. The active substance (A) and another active substance (B) may individually be introduced into the deposition chamber. The FOCVD process may be performed in the following manner to form the upper layer of Non-Si(H,X). The raw material gases are introduced into an evacuatable deposition chamber individually or altogether as required under a desired gas pressure. The raw material gases may contain a gas to supply silicon atoms (Si), a gas to supply hydrogen atoms (H), an optional gas to supply atoms (M) to control conductivity, and/or a gas to supply carbon atoms (C), and/or a gas to supply nitrogen atoms (N), and/or a gas to supply oxygen atoms (O), and/or a gas to supply germanium atoms (Ge), and/or a gas to supply tin atoms (Sn) and/or a gas to supply at least one of alkali metal, alkaline earth metal and transition metals. They may be introduced into the deposition chamber individually or altogether as required. A halogen (X) gas is introduced into the deposition chamber separately from the raw material gases described above and these gases subjected to chemical reactions in the deposition chamber. The sputtering method or the ion plating method may performed in the following manner to form the upper layer composed of the Non-Si(H,X), basically, by the known method as described for example, in Japanese Patent Laid-Open No. Sho 61-59342. According to this invention, the upper layer is formed while controlling the profile of the concentration C of atoms (M) to control the conductivity, carbon atoms (C), nitrogen atoms (N), oxygen atoms (O), germanium atoms (Ge), tin atoms (Sn) and at least one of alkali metal atoms, alkaline earth metal atoms and transition metal atoms (simply referred to collectively as "atoms (Z)") across the layer thickness to obtain a layer having a desired depth profile across the layer thickness. This can be achieved, in the case of glow discharge, HRCVD and FOCVD, by properly controlling the gas flow rate of a gas to supply atoms (Z) the concentration of which is to be varied in accordance with a desired rate of change in the concentration and then introducing the gas into the deposition chamber. The flow rate may be changed by operating a needle valve disposed in the gas passage manually or by means of a customary means such as an external driving motor. Alternatively, the flow rate setting to a mass flow controller for the control of the gas flow rate is properly changed by an adequate means manually or using a programmable control device. The gas to supply Si atoms used in this invention can include gaseous or gasifiable silicon hydrides (silanes) such as SiH₄, Si₂H₆, Si₃H₈ and Si₄H₁₀. SiH₄ and Si₂H₆ are preferable from the standpoint of ease of handling and the efficient supply of Si. These gases to supply Si may be diluted with an inert gas such as H₂, He, Ar and Ne if necessary. According to the present invention, the gas to supply halogen includes various halogen compounds, for example, gaseous and gasifiable halogen compounds, for example, halogen gases, halides, interhalogen compounds and halogen-substituted silane derivatives. Additional examples in this invention can include, gaseous or gasifiable halogen atom (X)-containing silicon hydride compounds composed of silicon atoms (Si) and halogen atoms (X). Halogen compounds that can be suitably used in this invention can include halogen gases such as of fluorine, chlorine, bromine and iodine; and interhalogen compounds such as BrF, ClF, ClF₃, BrF₅, BrF₃, IF₃, IF₇ ICl and IBr. Examples of the halogen atoms (X)-containing silicon compounds, or halogen atom (X)-substituted silane derivatives can include, specifically, silicon halides such as SiF₄, Si₂F₆, SiCl₄ and SiBr₄. In the case where the halogen-containing silicon compound is used to form the light receiving member for use in electrophotography according to this invention by the glow discharge or HRCVD method, it is possible to form the upper layer composed of Non-Si(H,X) containing halogen atoms (X) on a desired lower layer without using a silicohydride gas to supply Si atoms. In the case where the upper layer containing halogen atoms (X) is formed according to the glow discharge or HRCVD method, a silicon halide gas is used as the gas to supply silicon atoms to form the upper layer on a desired support. The silicon halide gas may further be mixed with hydrogen gas or a hydrogen atom (H)-containing silicon compound gas to facilitate the introduction of hydrogen atoms (H) at a desired level. The above-mentioned gases may be used individually or in combination with one another at a desired mixing ratio. In this invention, the above-mentioned halogen compounds or halogen atom (X)-containing silicon compounds are used as effective material as the gas to supply halogen atoms, but gaseous or gasifiable hydrogen halides such as HF, HCl, HBr and HI; and halogen-substituted silicohydrides such as SiH₃F, SiH₂F₂, SiHF₃, SiH₂I₁, SiH₂Cl₂, SiHCl₃, SiH₂Br₂ and SiBr₃ can also be used. Among them, hydrogen atom (H)-containing halides can be used as preferably halogen supply gases in this invention upon forming the upper layer, because they supply the upper layer with halogen atoms (X), as well as hydrogen atoms (H) which are very effective for the control of electric or photoelectric characteristics. The introduction of hydrogen atoms (H) into the upper layer may also be accomplished in another method by inducing discharge in the deposition chamber containing H₂ or silicoharide such as SiH₄, Si₂H₆, Si₃H₈ and Si₄H₁₀ and a silicon compound to supply silicon atoms (Si). The amount of hydrogen atoms (H) and/or halogen atoms (X) to be introduced into the upper layer may be controlled by regulating the temperature of the support, the amount of raw materials for hydrogen atoms and halogen atoms to be introduced into the deposition chamber and/or the electric power for discharge. The upper layer may contain atoms (M) to control the conductivity, for example, group III atoms, group V atoms or group VI atoms. This is accomplished by introducing into the deposition chamber the raw materials to form the upper layer together with a raw materials to supply group III atoms, raw materials to supply group V atoms or raw material to supply group VI atoms. The raw material to supply group III atoms, the raw material to supply group V atoms, or the raw material to supply group VI atoms may be gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions are desirably used. The raw material to supply the group III atoms can include specifically boron hydrides such as B₂H₆. B₄H₁₀, B₄H₉, B₅H₁₁, B₆H₁₀, B₆H₁₂ and B₆H₁₄ or boron harides such as BF₃, BCl₃ and BBr₃ for the material to supply boron atoms. Additional examples are AlCl₃, GaCl₃, Ga(CH₃)₃, InCl₃ and TlCl₃. The raw material to supply group V atoms that can be used effectively in this present invention can include, phosphorus hydride such as PH₃, P₂H₄, etc. phosphorus halide such as PH₄I, PF₃, PF₅, PCl₃, PCl₅, PBr₃, PBr₅ and PI₃ as the material to supply phosphorus atoms. Additional examples as effective raw materials to supply group V atoms can also include AsH₃, AsF₃, AsCl₃, AsBr₃, AsF₅, SbH₃, SbF₃, sbF₅, SbCl₃, SbCl₅, BiH₃, BiCl₃, BiBr₃. Raw materials to supply groups VI atoms can include those gaseous or gasifiable materials such as hydrogen sulfide (H₂S), SF₄, SV₆, SO₂, SO₂F₂, COS, CS₂, CH₃SH, C₂H₅SH, C₄H₄S, (CH₃)₂S, (C₂H₅)₂S, etc. Additional example can include, those gaseous or gasifiable materials such as SeH₂, SeF₆, (CH₃)₂Se, (C₂H₅)₂Se, TeH₂, TeF₆, (CH₃)₂Te, (C₂H₅)₂Te. The raw material for supplying atoms (M) to control the conductivity may be diluted with an inert gas such as H₂, He, Ar and Ne if necessary. The upper layer may contain carbon atoms (C), nitrogen atoms (N) or oxygen atoms (O). This accomplished by introducing into the chamber the raw material to supply carbon atoms (C), the raw material to supply nitrogen atoms (N) or raw material to supply oxygen atoms (O) in a gaseous form together with other raw materials for forming the upper layer. The raw material to supply carbon atoms (C), the raw material to supply nitrogen atoms (N) or the raw material to supply oxygen atoms (O) are desirably gaseous at normal temperature and under normal pressure or gasifiable under the layer forming conditions. A raw material that can effectively be used as the starting gas to supply carbon atoms (C) can include those hydrocarbons having C and H as constituent atoms, for example, saturated hydrocarbons having 1 to 4 carbon atoms, ethylene series hydrocarbons having 2 to 4 carbon atoms and acetylene series hydrocarbon atoms 2 to 3 carbon atoms. Examples of the saturated hydrocarbons include methane (CH₄), ethane (C₂H₅), propane (C₃H₈), n-butane (n-C₄H₁₀), pentane (C₅H₁₂). Examples of ethylene series hydrocarbons include ethylene (C₂H₄), propylene (C₃H₆), butene-1 (C₄H₈), butene-2 (C₄H₈), isobutylene (C₄H₈) and pentene (C₅H₁₀). Examples of acetylene series hydrocarbon can include, acetylene (C₂H₂), methylacetylene (C₃H₄) and butine (C₄H₆). Additional example can include halogenated hydrocarbon gases such as CF₄, CCl₄ and CH₃CF₃ with a view point that halogen atom (X) can be introduced in addition to hydrocarbons (C). Examples of the raw materials gas to introduce nitrogen atoms (N) can include those having N as constituent atoms, or N and H as constituent atoms, for example, gaseous or gasifiable nitrogen, or nitrogen compounds such as nitrides and azides, for example, nitrogen (N₂), ammonia (NH₃), hydrazine (H₂NNH₂), hydrogen azide (HN₃) and ammonium azide (NH₄N₃). Additional examples can include halogenated nitrogen compounds such as nitrogen trifluoride (F₃N) and nitrogen tetrafluoride (F₄N₂), etc. which can introduce nitrogen atoms as well as halogen atoms (X). Examples of the raw material gas to introduce oxygen atoms (O) can include oxygen (O₂), ozone (O₃), nitrogen monoxide (NO), nitrogen dioxide (NO₂), dinitrogen oxide (N₂O), dinitrogen trioxide (N₂O₃), trinitrogen tetraoxide (N₃O₄), dinitrogen pentaoxide (N₂O₅) and nitrogen trioxide (NO₃), as well as lower siloxanes having silicon atoms (Si), oxygen atoms (O) and hydrogen atoms (H) as constituent atoms, for example, disiloxane (H₃SiOSiH₃) and trisiloxane (H₃SiOSiH₂OSiH₃). The upper layer may be introduced with germanium (Ge) or tin atoms (Sn). This is accomplished by introducing, into the deposition chamber, the raw material to supply germanium (Ge) or the raw material to supply tin atoms (Sn) into the deposition chamber together with other raw materials to form the upper layer in a gaseous form. The raw material to supply germanium (Ge) or the raw material to supply tin atoms (Sn) may desirably be gaseous at normal temperature and normal pressure or gasifiable under the layer forming conditions. The material that can be used as a gas to supply germanium atoms (Ge) can include, gaseous or gasifiable germanium hydrides such as GeH₄, Ge₂H₆, Ge₃H₈ and Ge₄H₁₀. and GeH₄, Ge₂H₆ and Ge₃H₈ being preferable from the standpoint of easy handling at the time of layer forming and the efficient supply of germanium atoms (Ge). Additional examples of the raw material for effectively forming the upper layer can include those gaseous or gasifiable materials such as germanium hydride-halides, for example, GeHF₃, GeH₂F₂, GeH₃F, GeHCl₃, GeH₂Cl₂, GeH₃Cl, GeHBr₃, GeH₂Br₂. GeH₃Br, GeHI₃, GeH₂I₂ and GeH₃I, as well as germanium halides such as GeF₄, GeCl₄, GeBr₄, GeI₄, GeF₂, GeCl₂, GeBr₂ and GeI₂. The material that can be used as a gas to supply tin atoms (Sn) can include gaseous or gasifiable tin hydrides such as SnH₄, Sn₂H₆, Sn₃H₈ and Sn₄H₁₀ and SnH₄, Sn₂H₆ and Sn₃H₈ being preferred from the standpoint of easy handling at the time of layer forming and the efficient supply of tin atoms (Sn). Additional examples of the starting material for effectively forming the upper layer can include gaseous or gasifiable tin halide-hydrides such as SnHF₃, SnH₂F₂, SnH₃F, SnHCl₃, SnH₂Cl₂, SnH₃Cl, SnHBr₃, SnH₂Br₂, SnH₃Br, SnHI₃, SnH₂I₂ and SnH₃I, as well as tin halides such as SnF₄, SnCl₄, SnBr₄, SnI₄, SnF₂, SnCl₂, SnBr₂ and SnI₂. The lower layer may contain magnesium atoms (Mg). This accomplished by introducing, into the deposition chamber, the raw materials for supplying magnesium atoms (Mg) to form the upper layer together with other raw materials for forming the upper layer in a gaseous form. The raw material to supply magnesium atoms (Mg) may be gaseous at normal temperature and a normal pressure or gasifiable under the layer forming conditions. The substance that can be used as a gas to supply magnesium atoms (Mg) can include organometallic compounds containing magnesium atoms (Mg). Bis(cyclopentadienyl)magnesium (II) complex salt (Mg(C₅₆)₂) is preferable from the stand point of easy handling at the time of layer form an the effective supply of magnesium atoms (Mg). The gas to supply magnesium atoms (Mg) may be diluted with an inert gas such as H₂, He, Ar and Ne if necessary. The upper layer may contain copper atoms (Cu). This is accomplished by introducing, into the deposition chamber, the raw material to supply copper atoms (Cu) for forming the upper layer together with other raw materials for forming the upper layer in a gaseous form. The raw material to supply copper atoms (Cu) may be gaseous at normal temperature and normal pressure and gasifiable under the layer forming condition. The material that can be used as a gas to supply copper atoms (Cu) can include organometallic compounds containing copper atoms (Cu). Copper (II)bisdimethylglyoximate CU(C₄N₂O₂)₂ is preferred from the stand point of easy handling at the time of layer forming and efficient supply of magnesium atoms (Mg). The gas to supply copper atoms (Cu) may be diluted with an inert gas such as H₂. He, Ar and Ne, if necessary. The upper layer may contain sodium atoms (Na), yttrium atoms (Y), manganese atoms (Mn) or zinc atoms (Zn). This is accomplished by introducing, into the deposition chamber, raw material to supply sodium atoms (Na), the raw material to supply yttrium atoms (Y), the raw material to supply manganese atoms (Mn) or the raw materials to supply zinc atoms (Zn) for forming the upper layer together with other raw materials for forming the upper layer in a gaseous form. The raw material to supply sodium atoms (Na), the raw material to supply yttrium atoms (Y), the raw material to supply manganese atoms (Mn) or the raw material to supply zinc atoms (Zn) may be gaseous at normal temperature and normal pressure or gasifiable at least under the layer forming conditions. The material that can be effectively used as a gas to supply sodium atoms (Na) can include sodium amine (NaNH₂) and organometallic compounds containing sodium atoms (Na). Among them, sodium amine (NaNH₂) is preferred from the standpoint of easy handling at the time of layer forming and the efficient supply of sodium atoms (Na). The material that can be effectively used as a gas to supply yttrium atoms (Y) can include organometallic compounds containing ytrrium atoms (Y). Triisopropanol yttrium Y(Oi-C₃H₇)₃ is preferred from the standpoint of easy handling at the time of layer forming and the effective supply of yttrium atoms (Y). The material can be effectively used as a gas to supply manganese atoms (Mn) can include organometallic compounds containing manganese atoms (Mn). Monomethylpentacarbonyl manganese Mn(CH₃)(CO)₅ is preferred from the standpoint of easy handling at the time of layer forming and the efficient supply of manganese atoms (Mn). The material that can be effectively used as a gas to supply zinc atoms (Zn) can include organometallic compounds containing Zinc atoms (Zn). Diethyl zinc Zn(C₂H₅)₂ is preferred from the standpoint of easy handling at the time of layer forming and the efficient supply of zinc atoms (Zn). The gas to supply sodium atoms (Na), yttrium atoms (Y), manganese atoms (Mn) or zinc atoms (Zn) may be diluted with an inert gas such as H₂, He, Ar and Ne, if necessary. In the present invention, the layer thickness of the upper layer is 1 - 130 um, preferably, 3 - 100 um and, most suitably, 5 - 60 um from the standpoint of the desired electrophotographic characteristics and economical effect. In order to form the upper layer composed of Non-Si(H,X) which has the characteristics to achieve the object of this invention, it is necessary to properly establish the gas pressure in the deposition chamber and the temperature of the support. The gas pressure in the deposition chamber should properly be selected according to the design of the layer. It is usually 1 x 10⁻⁵ - 10 Torr, preferably, 1 x 10⁻⁴ - 3 Torr and, most suitably, 1 x 10⁻⁴ - 1 Torr. In the case of selecting A-Si(H, X) as the Non-Si(H,X) for the upper layer, the temperature (Ts) of the support should properly be selected according to the desired design for the layer and it is usually 50 - 400°C, preferably, 100 - 300°C. In a case where poly-Si(H,X) is selected as the Non-Si(H,X) for the upper layer, there are various methods for forming the layer including, for example, the following methods. In one method, the temperature of the support is set to a high temperature, specifically, to 400 - 600°C and a film is deposited on the support by means of the plasma CVD process. In another method, an amorphous layer is formed at first to the surface of the support. That is, a film is formed on a support heated to a temperature of about 250°C by a plasma CVD process and the amorphous layer is annealed into a polycrystalline layer. The annealing is conducted by heating the support to 400 - 600°C about for 5 - 30 min, or applying laser beams for about 5 - 30 min. Upon forming the upper layer composed of Non-Si(H,X) by the glow discharge method according to this invention, it is necessary to properly select the discharge electric power to be supplied to the deposition chamber according to the design of the layer. It is usually 5 x 10⁻⁵ - 10 W/cm³, preferably, 5 x 10⁻⁵ - 5 W/cm³ and, most suitably, 1 x 10⁻³ - 2 x 10⁻¹ W/cm³. The gas pressure of the deposition chamber, the temperature of the support and the discharge electric power to be supplied to the deposition chamber mentioned above should be set interdependently so that the upper layer having the desired characteristic properties can be formed. EFFECT OF THE INVENTION The light receiving member for use in electrophotography according to this invention, having the specific layer structure as described above, can overcome all of the problems in the conventional light receiving members for use in electrophotography constituted with A-Si and it can exhibit particularly excellent electrical properties, optical properties, photoconductive properties, image properties, durability and characteristics in the circumstance of use. Particularly, since the lower layer contains aluminum atoms (Al), silicon atoms (Si) and, particularly, hydrogen atoms (H) across the layer thickness in an unevenly distributed state according to the present invention, injection of charges (photocarriers) across the aluminum support and the upper layer can be improved and, moreover, since the texture and continuity for the constituent elements between the aluminum support and the upper layer is improved, image properties such as coarse image or dots can be improved thereby enabling to stably reproduce high quality images with clear half-tone and high resolving power. In addition, it is possible to prevent image defects or peeling of Non-Si(H,X) films due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, thereby improving the durability and, further, stresses resulted from the difference in the heat expansion coefficients between aluminum support and Non-Si(H,X) film to prevent cracking or peeling in the No-Si(H,X) film to thereby enhance the yield of the productivity. Incorporation of at least one of carbon atoms, nitrogen atoms and oxygen atoms into the layer region of the upper layer in adjecent with the lower layer can further improve the close bondability between the upper layer and the lower layer, to prevent the occurrence of image defects and peeling of the Non-Si(H,X) films thereby improving the durability. Further, since atoms (Mc) to control the image quality are contained in the lower layer in addition to aluminum atoms (Al), silicon atoms (Si) and hydrogen atoms (H), the injection of photocarriers across the aluminum support and the upper layer is further improved and the transferability of the photocarriers in the lower layer is improved. Accordingly, image characteristics such as coarse image can be improved to stably reproduce a high quality image with clear half-tone and high resolving power. Furthermore, since halogen atoms co-existent in the lower layer can compensate the unbonded bands of silicon atoms aluminum atoms, etc. to attain more stable state in view of the texture and structure according to the present invention, remarkable improvement can be obtained in view of the image characteristics such as coarse image or dots coupled with the foregoing effect due to the distribution of the silicon atoms, aluminum atoms and hydrogen atoms. Since at least one of germanium atoms (Ge) and tin atoms (Sn) are contained in the lower layer according to this invention, the injection of the photocarriers across the aluminum support and the upper layer, close bondability and the transferability of the photocarriers in the lower layer can remarkably be improved to thereby provide remarkable improvement in the image characteristics or durability. Particularly, since at lest one of alkali metal atoms, alkaline earth metal atoms and transition metal atoms are contained in the upper layer according to the present invention, an outstanding feature can be obtained that the hydrogen atoms and halogen atoms contained in the lower layer can be dispersed more effectively to prevent layer peeling resulted from the cohesion of hydrogen atoms and/or halogen atoms during long time use. Furthermore, since the injection of photocarriers and the close bondability across the aluminum support and the upper layer, and the transferability of photocarriers in the lower layer can be improved remarkably as described above, significant improvement can be obtained in the image property and the durability to result in improvement to the stable production and the stability for the quality. PREFERRED EMBODIMENT OF THE THE INVENTION This invention will be described more specifically referring to examples but the invention is no way limited only thereto. Example 1 A light receiving member for use in electrophotography according to this invention was formed by radio frequency (hereinafter simply referred to as "RF") glow discharge decomposition. Fig. 37 shows an apparatus for producing the light receiving member for use in electrophotography by the RF glow discharge decomposition, comprising a raw material gas supply device 1020 and a deposition device 1000. In the figure, raw material gases for forming the respective layers in this invention were tightly sealed in gas cylinders 1071, 1072, 1073, 1074, 1075, 1076 and 1077, and a tightly sealed vessel 1078, in which the cylinder 1071 was for SiH₄ gas (99.99 % purity), the cylinder 1072 was for H₂ gas (99.9999 %), the cylinder 1073 was for CH₄ gas (99.999 % purity), cylinder 1074 was for PH₃ gas diluted with H₂ gas (99.999 % purity, hereinafter simply referred to as "PH₃/H₂"), the cylinder 1075 was for B₂H₆ gas diluted with H₂ gas (99.999 % purity, hereinafter simply referred to as "B₂H₆/H₂"), the cylinder 1076 was for NO gas (99.9 % purity), the cylinder 1077 was for He gas (99.999 % purity), and the vessel 1078 was tightly sealed charged with AlCl₃ (99.99 % purity). In the figure, a cylindrical aluminum support 1005 had an outer diameter of 108 mm and a mirror-finished surface. After confirming that valves 1051 - 1057 for the gas cylinders 1071 - 1077, flow-in valves 1031 - 1037 and a leak valve 1015 for the deposition chamber 1001 were closed and flow-out valves 1041 - 1047 and an auxiliary valve 1018 were opened, a main valve 1016 was at first opened to evacuate the deposition chamber 1001 and gas pipeways by a vacuum pump not illustrated. Then, when the indication of a vacuum meter 1017 showed about 1 x 10⁻³ Torr, the auxiliary valve 1018, the flow-out valves 1041 - 1047 were closed. Then, the valves 1051 - 1057 were opened to introduce SiH₄ from the gas cylinder 1071, H₂ gas from the gas cylinder 1072, CH₄ gas from the gas cylinder 1073, PH₃/H₂ gas from the gas cylinder 1074, B₂H₆/H₂ gas from the gas cylinder 1075, NO gas from the gas cylinder 1076 and He gas from the gas cylinder 1077, and the pressures for the respective gases were adjusted to 2 kg/cm² by pressure controllers 1061 - 1067. Then, the flow-in valves 1031 - 1037 were gradually opened to introduce the respective gases in mass flow controllers 1021 - 1027. In this case, since the He gas from the gas cylinder 1077 was passed through the tightly sealed vessel 1078 charged with AlCl₃, the AlCl₃ gas diluted with the He gas (hereinafter simply referred to as "AlCl₃/He") was introduced to the mass flow controller 1027. The temperature of the cylindrical aluminum support 1005 disposed in the deposition chamber 1001 was heated to 250°C by a heater 1014. After completing the preparation for the film formation as described above, each of the lower and upper layers was formed on the cylindrical aluminum support 1005. The lower layer was formed by gradually opening the flow-out valves 1041, 1042 and 1047, and the auxiliary valve 1018 thereby introducing the SiH₄ gas, H₂ gas and AlCl₃/He gas through the gas discharge aperture 1009 of a gas introduction pipe 1018 to the inside of the deposition chamber 1001. In this case, the gas flow rates were controlled by the respective mass flow controllers 1021, 1022 and 1027 such that the gas flow rates were set to 50 SCCM for SiH₄, 10 SCCM for H₂ gas, and 120 SCCM for AlCl₃/He. The pressure in the deposition chamber was controlled to 0.4 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced to the inside of the deposition chamber 1001 by way of an RF matching box 1012 while setting the power of a RF power source (not illustrated) to 5 mW/cm³, to cause RF glow discharge, thereby starting the formation of the lower layer on the aluminum support. The mass flow controllers 1021, 1022 and 1027 were adjusted during formation of the lower layer such that the SiH₄ gas flow remains at a constant rate of 50 SCCM, the H₂ gas flow rate is increased at a constant ratio from 10 SCCM to 200 SCCM and the AlCl₃/He gas flow rate is decreased at a constant ratio from 120 SCCM to 40 SCCM. Then, when the lower layer of 0.05 um thickness was formed, the RF glow discharge was stopped and the entrance of the gas to the inside of the deposition chamber 1001 is interrupted by closing the flow-out valves 1041, 1042 and 1047 and the auxiliary valve 1018, to complete the formation of the lower layer. Then, for forming the first layer region of the upper layer, the flow-out valves 1041, 1042 and 1046, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas, H₂ gas and NO gas through the gas discharge aperture 1009 of the gas introduction pipe 1008 into the deposition chamber 1001. In this case, respective mass flow controllers 1021, 1022 and 1026 were adjusted so that the SiH₄ gas flow rate was 100 SCCM, H₂ gas flow rate was 100 SCCM and NO gas flow rate was 30 SCCM. The pressure in the deposition chamber 1001 was controlled to 0.35 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced into the deposition chamber 1001 through a radio frequency matching box 1012 while setting the power of a RF power source (not illustrated) to 10 mW/cm³, to cause RF glow discharge and start the formation of the first layer region of the upper layer over the lower layer. Then, when the first layer region of the upper layer with 3 um thickness was formed, the RF glow discharge was stopped and the flow of the gas into the deposition chamber 1001 was interrupted by closing the flow-out valves 1041, 1042 and 1046, and the auxiliary valve 1018, thereby completing the formation of the first layer region of the upper layer. Then, for forming the second layer region of the upper layer, the flow-out valves 1041 and 1042, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas and Hy gas through the gas discharge aperture 1009 of the gas introduction pipe 1008 into the deposition chamber 1001. In this case, respective mass flow controllers 1021 and 1022 were adjusted so that the SiH₄ gas flow rate was 300 SCCM and H₂ flow rate was 300 SCCM. The pressure in the deposition chamber 1001 was controlled to 0.5 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced into the deposition chamber 1001 through the radio frequency matching box 1012 while setting the power of the RF power source (not illustrated) to 15 mW/cm³, to cause the RF glow discharge and start the formation of the second layer region on the first layer region of the upper layer. Then, when the second layer region of the upper layer with 20 um thickness was formed, the RF glow discharge was stopped and the flow of the gas into the deposition chamber 1001 was interrupted by closing the flow-out valves 1041 and 1042, and the auxiliary valve 1018, thereby completing the formation of the second layer region of the upper layer. Then, for forming the third layer region of the upper layer, the flow-out valves 1041 and 1043, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas and CH₄ gas through the gas discharge aperture 1009 of the gas introduction pipe 1008 into the deposition chamber 1001. In this case, respective mass flow controllers 1021 and 1023 were adjusted so that the SiH₄ gas flow rate was 50 SCCM and CH₄ flow rate was 500 SCCM. The pressure in the deposition chamber 1001 was controlled to 0.4 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced into the deposition chamber 1001 through the radio frequency matching box 1012 while setting the power of the RF power source (not illustrated) to 10 mW/cm³, to cause the RF glow discharge and start the formation of the third layer region on the second layer region of the upper layer. Then, when the third layer region of the upper layer with 0.5 um thickness was formed, the RF glow discharge was stopped and the flow of the gas into the deposition chamber 1001 was interrupted by closing the flow-out valves 1041 and 1043, and the auxiliary valve 1018, thereby completing the formation of the third layer region of the upper layer. The conditions for preparing the light receiving member for use in electrophotography described above are shown in Table 1. It will be apparent that all of the flow-out valves other than those required for forming the respective layers were completely closed and, for avoiding the respective gases from remaining in the deposition chamber 1001 and in the pipeways from the flow-out valves 1041 - 1047 to the deposition chamber 1001, the flow-out valves 1041 - 1047 were closed, the auxiliary valve 1018 was opened and, further, the main valve was fully opened thereby evacuating the inside of the system once to a high vacuum degree as required. Further, for forming the layer uniformly during this layer formation, the cylindrical aluminum support 1005 was rotated at a desired speed by a driving device not illustrated. Comparative Example 1 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 1 except for not using H₂ gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electrophotography are shown in Table 2. The light receiving members for use in electrophotography thus prepared in Example 1 and Comparative Example 1 were set respectively to an electrophotographic apparatus, i.e., a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 1 was less than 3/4 of that of the light receiving member for use in electrophotography in Comparative Example 1. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 1 was less than 2/3 for that of the light receiving member for use in electrophotography in Comparative Example 1, and the light receiving member for use in electrophotography of Example 1 was excellent over the light receiving member for use in Electrophotography of Comparative Example 1 in view of the visual observation. In addition, for comparing the occurrence of image defects and the peeling of the light receiving layer due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, when stainless steel balls of 3.5 mm diameter were fallen freely from the vertical height of 30 cm above the surface of the light receiving member for use in electrophotography and abutted against the surface of the light receiving member for use in electrophotography, to thereby measure the frequency of occurrence for cracks in the light receiving layer, it was found that the rate of occurrence in the light receiving member for use in electrophotography of Example 1 was less than 3/5 for that in the light receiving member for use in electrophotography of Comparative Example 1. As has been described above, the light receiving member for use in electrophotography of Example 1 was superior to the light receiving member for use in electrophotography of Comparative Example 1. Example 2 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 except for changing the way of varying the AlCl₃/He gas flow rate in the lower layer, under the preparation conditions shown in Table 3 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 3 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 except for not using the CH₄ gas in the upper layer of Example 1, under the preparation conditions shown in Table 4 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 4 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 except for replacing the PH₃/H₂ gas cylinder with a He gas (99.9999 % purity) cylinder and, further, using SiF₄ gas and N₂ gas from cylinder not illustrated in Example 1, under the preparation conditions shown in Table 5 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 5 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 except for replacing the B₂H₆/H₂ gas cylinder with an Ar gas (99.9999 % purity) cylinder and, further replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 1, under the preparation conditions shown in Table 6 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 6 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using PH₃/H₂ gas and C₂H₆ gas in the upper layer, under the preparation conditions shown in Table 7 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 1. Example 7 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 8 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 1. Example 8 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using N₂ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 9 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 1. Example 9 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 except for replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 1, under the preparation conditions shown in Table 10 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 10 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by replacing the NO gas cylinder with a N₂ gas cylinder in Example 1, under the preparation conditions shown in Table 11 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 11 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 1, under the preparation conditions shown in Table 12 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 12 A light receiving member for use in electrophotography was prepared in the same manner as in Example 6 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 13 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 6. Example 13 A light receiving member for use in electrophotography was prepared in the same manner as in Example 9 by further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 14 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 9. Example 14 A light receiving member for use in electrophotography was prepared in the same manner as in Example 11 by further using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 15 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 11. Example 15 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using GeH₄ from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 16 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 1. Example 16 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by changing the outer diameter of the cylindrical aluminum support to 80 mm in Example 1, under the preparation conditions shown in Table 17 and, when evaluated in the same manner as in Example 1, except for using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 17 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 1, under the preparation conditions shown in Table 18 and, when evaluated in the same manner as in Example 1, except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 18 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 1, under the preparation conditions shown in Table 19 and, when evaluated in the same manner as in Example 1, except for using an electrophotographic apparatus, i.e., a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 19 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 1, under the preparation conditions shown in Table 20, and evaluated in the same manner as in Example 1 except for using an electrophotographic apparatus, manufactured for experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 20 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 16 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 16 and further machined into a cross sectional shape of : a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 16, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 16. Example 21 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 16 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of : c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 16, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 16. Example 22 A light receiving member for use in electrophotography having an upper layer comprising poly-Si(H, X) was prepared in the same manner as in Example 9 by using a cylindrical aluminum support heated to a temperature of 500°C, under the preparation conditions as shown in Table 21 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 9. Example 23 A light receiving member for use in electrophotography according to this invention was formed by microwave (hereinafter simply referred to as "uW") glow discharge decomposition. A production apparatus for the light receiving member for use in photography by the uW glow discharge decomposition shown in Figure 41 was used, in which a decomposition device 1100 for use in the uW glow discharge decomposition shown in Figure 40 was used instead of the deposition device 1000 in the production apparatus of RF glow discharge decomposition shown in Fig. 37, and it was connected with a raw material gas supply device 1020. In the figure, a cylindrical aluminum support 1107 had 108 mm of outer diameter and mirror-finished surface. At first, in the same manner as in Example 1, the inside of the deposition chamber 1101 and the gas pipeways was evacuated such that the pressure in the deposition chamber 1101 was 5 x 10⁻⁶ Torr. Then, in the same manner as in Example 1, the respective gases were introduced in the mass flow controllers 1021 - 1027. In this case, however, a SiF₄ gas cylinder was used in place of the N₂ gas cylinder. Further, the cylindrical aluminum support 1107 disposed in the deposition chamber 1101 was heated to a temperature of 250°C by a heater not illustrated. After the preparation for the film formation was thus completed, each of the lower and the upper layers was formed on the cylindrical aluminum support 1107. The lower layer was formed by gradually opening the flow-out valves 1041, 1042 and 1047 and the auxiliary valve 1018, thereby flowing the SiH₄ gas, H₂ gas and AlCl₃/He gas through the gas discharge aperture not illustrated of the gas introduction pipe 1110 into a plasma generation region 1109. In this case, the gas flow rate was controlled by each of the mass flow controllers 1021, 1022 and 1027 such that SiH₄ gas flow rate was 150 SCCM, H₂ gas flow rate was 20 SCCM and AlCl₃ gas flow rate was 400 SCCM. The pressure in the deposition chamber 1101 was set to 0.6 mTorr by adjusting the opening of the main valve not illustrated while observing the vacuum meter not illustrated. Then, uW power was introduced by way of a wave guide portion 1103 and a dielectric window 1102 into a plasma generation region 1109 by setting the power for a uW power source not illustrated to 0.5 W/cm³, to cause uW glow discharge and start the formation of the lower layer on the cylindrical aluminum support 1107. The mass flow controllers 1021, 1022 and 1027 were controlled such that the SiH₄ gas flow rate remained at a constant rate of 150 SCCM, the H₂ gas flow rate was increased at a constant ratio from 20 SCCM to 500 SCCM, the AlCl₃/He gas flow rate was reduced at a constant ratio from 400 SCCM to 80 SCCM for the 0.01 um on the support side, while reduced at a constant ratio from 80 SCCM to 50 SCCM for 0.01 um on the side of the upper layer during formation of the lower layer. When the lower layer of 0.02 um thickness was formed, the uW glow discharge was stopped, the flow-out valves 1041, 1042, 1047 and the auxiliary valve 1018 were closed to interrupt the flow of the gas into the plasma generation region 1109 thereby completing the formation of the lower layer. Then, for forming the first layer region of the upper layer, the flow-out valves 1041, 1042, 1044, 1045 and 1046, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas, H₂ gas and SIF₄ gas, B₂H₆/H₂ and NO gas through the gas discharge aperture not illustrated of the gas introduction pipe 1110 into the plasma generation space 1109. In this case, respective mass flow controllers 1021, 1022, 1024, 1025 and 1026 were adjusted so that the SiH₄ gas flow rate was 3500 SCCM, H₂ gas flow rate was 350 SCCM, SiF₄ gas flow rate was 20 SCCM, B₂H₆/H₂ gas flow rate was 600 ppm to the SiH₄ gas flow rate and NO gas flow rate was 13 SCCM. The pressure in the deposition chamber 1101 was controlled to 0.5 mTorr. Then, RF power was introduced into the plasma generation chamber 1109 while setting the power of RF power source (not illustrated) to 0.5 mW/cm³, to cause uW glow discharge and start the formation of the first layer region of the upper layer over the lower layer. Then, the first layer region of 3 um thickness of the upper layer was formed. Then, for forming the second layer region of the upper layer, the flow-out valves 1041, 1042 and 1044, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas, H₂ gas and SiF₄ gas through the gas discharge aperture not illustrated of the gas introduction pipe 1110 into the plasma generation space 1109. In this case, respective mass flow controllers 1021, 1022 and 1024 were adjusted so that the SiH₄ gas flow rate was 700 SCCM, H₂ gas flow rate was 500 SCCM and SiF₄ gas flow rate was 30 SCCM. The pressure in the deposition chamber 1101 was controlled to 0.5 mTorr. Then, the power of a uW power source (not illustrated) was set to 0.5 mW/cm³, to cause uW glow discharge in the plasma generation region 1109 and form the second layer region with 20 um thickness of the upper layer on the first layer region of the upper layer. Then, for forming the third layer region of the upper layer, the flow-out valves 1041 and 1043 and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas and CH₄ gas through the gas discharge aperture not illustrated of the gas introduction pipe 1110 into the plasma generation space 1109. In this case, respective mass flow controllers 1021 and 1023 were adjusted so that the SiH₄ gas flow rate was 150 SCCM and CH₄ gas flow rate was 500 SCCM. The pressure in the deposition chamber 1101 was controlled to 0.3 mTorr. Then, the power of a uW power source (not illustrated) was set to 0.5 mW/cm³, to cause uW glow discharge in the plasma generation region 1109 and and the third layer region with 0.5 um thickness of the upper layer was formed on the second layer region of the upper layer. The conditions for preparing the light receiving member for use in electrophotography described above are shown in Table 22. When the the light receiving member for use in electrophotography was evaluated in the same manner in Example 1, improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 24 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 1, under the preparation conditions shown in Table 23 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 25 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by replacing the No gas cylinder with a N₂ gas cylinder in Example 1, under the preparation conditions shown in Table 24 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 26 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 1, under the preparation conditions shown in Table 25 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 27 A light receiving member for use in electrophotography was prepared in the same manner as in Example 6 by further using SiF₄ from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 26 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 6. Example 28 A light receiving member for use in electrophotography was prepared in the same manner as in Example 9 by further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 27 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 9. Example 29 A light receiving member for use in electrophotography was prepared in the same manner as in Example 11 by further using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 28 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 11. Example 30 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by replacing the PH₃/H₂ gas cylinder with a He gas (99.999 % purity) cylinder and further using N₂ gas from not illustrated cylinder in the Example 1, under the preparation conditions shown in Table 29 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 31 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using PH₃/H₂ gas, C₂H₂ gas and SiF₄ gas in the upper layer, under the preparation conditions shown in Table 30 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 32 A light receiving member for use in electrophotography was prepared in the same manner as in Example 6 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 31 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 6. Example 33 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using B₂H₆/H₂ and C₂H₂ gas in the upper layer, under the preparation conditions shown in Table 32 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 34 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using PH₃/H₂ gas and C₂H₂ gas in the upper layer, under the preparation conditions shown in Table 33 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 35 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using PH₃/H₂ and C₂H₂ gas, SiF₄ gas and H₂S gas in the upper layer, under the preparation conditions shown in Table 34 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 1. Example 36 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using B₂H₆ gas upon forming the lower layer in Example 1, under the preparation conditions as shown in Table 35. Comparative Example 2 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 36 except for not using B₂H₆/H₂ gas and H₂ gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electrophotography are shown in Table 36. The light receiving members for use in electrophotography thus prepared in Example 36 and Comparative Example 2 were set respectively to an electrophotographic apparatus, i.e., a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 24 was less than 3/4 of that of the light receiving member for use in electrophotography in Comparative Example 2. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 36 was less than 1/2 for that of the light receiving member for use in electrophotography in Comparative Example 2, and the light receiving member for use in electrophotography of Example 1 was excellent over the light receiving member for use in Electrophotography of Comparative Example in view of the visual observation. Example 37 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 except for changing the way of varying the AlCl₃/He gas flow rate in the lower layer, under the preparation conditions shown in Table 37 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 38 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 except for not using the CH₄ gas in the upper layer of Example 36, under the preparation conditions shown in Table 38 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 39 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 except for replacing the PH₃/H₂ gas cylinder with a He gas (99.9999 % purity) cylinder and, further, using SiF₄ gas and N₂ gas from cylinder not illustrated, under the preparation conditions shown in Table 39 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 40 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 except for replacing the B₂H₆/H₂ gas cylinder with an Ar gas (99.9999 % purity) cylinder and, further replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder, under the preparation conditions shown in Table 40 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 41 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using PH₃/H₂ gas and C₂H₂ gas in the upper layer, under the preparation conditions shown in Table 41 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 36. Example 42 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 42, and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 36. Example 43 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using N₂ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 43 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 36. Example 44 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 except for replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 36, under the preparation conditions shown in Table 44 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 45 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by replacing the NO gas cylinder with a N₂ gas cylinder in Example 36, under the preparation conditions shown in Table 45 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 46 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 36, under the preparation conditions shown in Table 46 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 47 A light receiving member for use in electrophotography was prepared in the same manner as in Example 41 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 47 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 41. Example 48 A light receiving member for use in electrophotography was prepared in the same manner as in Example 44 by further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 48 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 44. Example 49 A light receiving member for use in electrophotography was prepared in the same manner as in Example 46 by further using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 49 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 46. Example 50 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using GeH₄ from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 50 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 36. Example 51 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by changing the outer diameter of the cylindrical aluminum support to 80 mm in Example 36, under the preparation conditions shown in Table 51 and, when evaluated in the same manner as in Example 36, except for using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 52 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 36, under the preparation conditions shown in Table 52 and, when evaluated in the same manner as in Example 36, except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 53 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 36, under the preparation conditions shown in Table 53 and, when evaluated in the same manner as in Example 36, except for using an electrophotographic apparatus, i.e., a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 54 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 36, under the preparation conditions shown in Table 54, and evaluated in the same manner as in Example 36, except for using an electrophotographic apparatus, manufactured for experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 55 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 51 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 51 and further machined into a cross sectional shape of : a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 51, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 51. Examples 56, 57 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 51 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of : c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 56, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 51. Example 58 A light receiving member for use in electrophotography was prepared by microwave glow discharge decomposition in the same manner as in Example 23 by further using B₂H₆ gas upon forming the lower layer in Example 23, under the preparation conditions shown in Table 56. When the light receiving member for use in electrophotography was evaluated in the same manner as in Example 36, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 59 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 36, under the preparation conditions shown in Table 57 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 60 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by replacing the No gas cylinder with a N₂ gas cylinder in Example 36, under the preparation conditions shown in Table 58 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 61 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 36, under the preparation conditions shown in Table 59 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 62 A light receiving member for use in electrophotography was prepared in the same manner as in Example 41 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 60 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 41. Example 63 A light receiving member for use in electrophotography was prepared in the same manner as in Example 44 by further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 61 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 44. Example 64 A light receiving member for use in electrophotography was prepared in the same manner as in Example 46 by further using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 62 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 46. Example 65 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by replacing the PH₃/H₂ gas cylinder with a He gas (99.999 % purity) cylinder and further using N₂ gas from a not illustrated cylinder in the Example 36, under the preparation conditions shown in Table 63 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 66 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using gas, C₂H₂ gas and SiF₄ gas in the upper layer, under the preparation conditions shown in Table 64 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 67 A light receiving member for use in electrophotography was prepared in the same manner as in Example 41 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 65 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 41. Example 68 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using B₂H₆/H₂ and C₂H₂ gas in the upper layer, under the preparation conditions shown in Table 66 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 69 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using PH₃/H₂ gas and C₂H₂ gas in the upper layer, under the preparation conditions shown in Table 67 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 70 A light receiving member for use in electrophotography was prepared in the same manner as in Example 36 by further using PH₃/H₂ and C₂H₂ gas, SiF₄ gas and H₂S gas in the upper layer, under the preparation conditions shown in Table 68 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 36. Example 71 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using NO gas upon forming the lower layer in Example 1, under the preparation conditions as shown in Table 69. Comparative Example 3 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 71 except for not using H₂ gas and NO gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electrophotography are shown in Table 70. The light receiving members for use in electrophotography thus prepared in Example 36 and Comparative Example 2 were set respectively to an electrophotographic apparatus, i.e., a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 71 was less than 3/4 of that of the light receiving member for use in electrophotography in Comparative Example 3. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 71 was less than 1/2 for that of the light receiving member for use in electrophotography in Comparative Example 3. and the light receiving member for use in electrophotography of Example 71 was excellent over the light receiving member for use in Electrophotography of Comparative Example 3 in view of the visual observation. In addition, for comparing the occurrence of image defects and the peeling of the light receiving layer due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, when stainless steel balls of 3.5 mm diameter were fallen freely from the vertical height of 30 cm above the surface of the light receiving member for use in electrophotography and abutted against the surface of the light receiving member for use in electrophotography, to thereby measure the frequency of occurrence for cracks in to the light receiving layer, it was found that the rate of occurrence in the light receiving member for use in electrophotography of Example 71 was less than 2/5 for that in the light receiving member for use in electrophotography of Comparative Example 3. As has been described above, the light receiving member for use in electrophotography of Example 71 was superior to the light receiving member for use in electrophotography of Comparative Example 3. Example 72 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 except for changing the way of varying the AlCl₃/He gas flow rate in the lower layer and using B₂H₆ gas in the upper layer, under the preparation conditions shown in Table 71 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 73 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 except for not using the CH₄ gas in the upper layer of Example 71, under the preparation conditions shown in Table 72 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 74 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the PH₃/H₂ gas cylinder with the He gas (99.9999 % purity) cylinder and, further, using SiF₄ gas and N₂ gas from cylinders not illustrated in Example 71, under the preparation conditions shown in Table 73 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 75 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the B₂H₆/H₂ gas cylinder with an Ar gas (99.9999 % purity) cylinder and replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 71, under the preparation conditions shown in Table 74 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 76 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by further using pH₃/H₂ gas and C₂H₆ gas in the upper layer, under the preparation conditions shown in Table 75 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 71. Example 77 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 76 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 71. Example 78 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by further using N₂ gas and H₂S gas from a not illustrated cylinder in the Example 71, under the preparation conditions shown in Table 77, and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 1. Example 79 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 71, under the preparation conditions shown in Table 78 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 80 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the NO gas cylinder with a N₂ gas cylinder and, further using the H₂S gas from cylinder not illustrated in Example 71, under the preparation conditions shown in Table 79 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 81 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 71, under the preparation conditions shown in Table 80 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 82 A light receiving member for use in electrophotography was prepared in the same manner as in Example 76 by further using SiF₄ gas from a not illustrated cylinder and replacing C₂H₂ gas cylinder with CH₄ gas cylinder in the upper layer, under the preparation conditions shown in Table 82 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 79. Example 83 A light receiving member for use in electrophotography was prepared in the same manner as in Example 79 by using Si₂F₄ gas from a not illustrated cylinder and further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 82 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 79. Example 84 A light receiving member for use in electrophotography was prepared in the same manner as in Example 81 by further using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 83 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 81. Example 85 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by further using GeH₄ from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 84 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 71. Example 86 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by changing the outer diameter of the cylindrical aluminum support to 8o mm in Example 71, under the preparation conditions shown in Table 85 and, when evaluated in the same manner as in Example 71, except for using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 87 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 71, under the preparation conditions shown in Table 86 and, when evaluated in the same manner as in Example 71, except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 88 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 71, under the preparation conditions shown in Table 87 and, when evaluated in the same manner as in Example 71, except for using an electrophotographic apparatus, i.e., a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 89 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 71, under the preparation conditions shown in Table 88 evaluated in the same manner as in Example 71, except for using an electrophotographic apparatus, manufactured for experimental use, satisfactory improve was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 90 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 86 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 86 and further machined into a cross sectional shape of : a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 86, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 86. Example 91 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 86 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 86, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 86. Example 92 A light receiving member for use in electrophotography having an upper layer comprising poly-Si(H, X) was prepared in the same manner as in Example 79 by using a cylindrical aluminum support heated to a temperature of 500°C, the preparation conditions as shown in Table 89 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 79. Example 93 A light receiving member for use in electrophotography was prepared by microwave glow discharge decomposition in the same manner as in Example 23 by further using NO gas and B₂H₆ gas upon forming the lower layer in Example 23, under the preparation conditions shown in Table 90. When the light receiving member for use in electrophotography was evaluated in the same manner as in Example 71, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 94 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 71, under the preparation conditions shown in Table 91 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 95 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the No gas cylinder with a N₂ gas cylinder in Example 71, under the preparation conditions shown in Table 92 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 96 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 71, under the preparation conditions shown in Table 93 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 97 A light receiving member for use in electrophotography was prepared in the same manner as in Example 76 by further using SiF₄ from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 94 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 76. Example 98 A light receiving member for use in electrophotography was prepared in the same manner as in Example 79 by replacing SiH₄ gas cylinder with Si₂H₆ gas cylinder and further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 95 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 79. Example 99 A light receiving member for use in electrophotography was prepared in the same manner as in Example 81 by further using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 96 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 81. Example 100 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by replacing the PH₃/H₂ gas cylinder with a He gas (99.999 % purity) cylinder and further using N₂ gas from a not illustrated cylinder in the Example 71, under the preparation conditions shown in Table 97 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 101 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by further using C₂H₂ gas and SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 98 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 11. Example 102 A light receiving member for use in electrophotography was prepared in the same manner as in Example 101 by further using SiF₄ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 99 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 101. Example 103 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106 by using B₂H₆/H₂ and further using C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 100 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 104 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by using PH₃/H₂ and further using C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 101 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 105 A light receiving member for use in electrophotography was prepared in the same manner as in Example 71 by using C₂H₂ gas, SiF₄ gas and H₂ S gas from a not illustrated cylinder, under the preparation conditions shown in Table 102 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 106 A light receiving member for use in electrophotography was prepared in the same manner as in Example 79 by using C₂H₂ gas and SiF₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 103 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 79. Example 107 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 104, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 108 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 105 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 109 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 106 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 110 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 107 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 111 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 108 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 112 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 109 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 113 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 110 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 114 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 111 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 115 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106 by further using PH₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 112 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 116 A light receiving member for use in electrophotography was prepared in the same manner as in Example 115, under the preparation conditions shown in Table 113 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 115. Example 117 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106 by further using H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 114 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 118 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 114 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 119 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 116 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 120 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106 by further using NH₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 117 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 121 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106 by further using N₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 118 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 122 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 119 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 123 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 120 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 124 A light receiving member for use in electrophotography was prepared in the same manner as in Example 115, under the preparation conditions shown in Table 121 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 115. Example 125 A light receiving member for use in electrophotography was prepared in the same manner as in Example 106, under the preparation conditions shown in Table 122 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 106. Example 126 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using SiF₄ gas and NO gas upon forming the lower layer in Example 1, under the preparation conditions shown in Table 123. Comparative Example 4 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 126 except for not using SiF₄ gas, NO gas and H₂ gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electro photography are shown in Table 124. The light receiving members for use in electrophotography thus prepared in Example 126 and Comparative Example 4 were set respectively to an electrophotographic apparatus, i.e., a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 71 was less than half of that of the light receiving member for use in electrophotography in Comparative Example 3. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 126 was less than 1/2 for that of the light receiving member for use in electrophotography in Comparative Example 4, and the light receiving member for use in electrophotography of Example 126 was excellent over the light receiving member for use in Electrophotography of Comparative Example 4 in view of the visual observation. In addition, for comparing the occurrence of image defects and the peeling of the light receiving layer due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, when stainless steel balls of 3.5 mm diameter were fallen freely from the vertical height of 30 cm above the surface of the light receiving member for use in electrophotography and abutted against the surface of the light receiving member for use in electrophotography, to thereby measure the frequency of occurrence for cracks in the light receiving layer, it was found that the rate of occurrence in the light receiving member for use in electrophotography of Example 126 was less than 2/5 for that in the light receiving member for use in electrophotography of Comparative Example 4. As has been described above, the light receiving member for use in electrophotography of Example 126 was superior to the light receiving member for use in electrophotography of Comparative Example 4. Example 127 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by not using the NO gas and changing the way of varying the AlCl₃/He gas flow rate in the lower layer of Example 126, under the preparation conditions shown in Table 125 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 128 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by not using the CH₄ gas in Example 126, under the preparation conditions shown in Table 126 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 129 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using He gas (99.9999 % purity) from a not illustrated cylinder in Example 126, under the preparation conditions shown in Table 127 and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 130 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by replacing the B₂H₆/H₂ gas with diluted H₂ gas (99.999 % purity, hereinafter simply referred to as PH₃/H₂) cylinder, replacing the NO gas cylinder with NH₃ gas (99.999 % purity) cylinder in Example 126, under the preparation conditions shown in Table 128 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 131 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using C₂H₂ gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 129 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 126. Example 132 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using PH₃/H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 130 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 126. Example 133 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using N₂ gas, H₂S and PH₃/H₂ gas from a not illustrated cylinder in the Example 126, under the preparation conditions shown in Table 131 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 126. Example 134 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 126, under the preparation conditions shown in Table 132 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 135 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by replacing the B₂H₆/H₂ gas cylinder with H₂-diluted BF₃ gas (99.999 % purity, hereinafter simply referred to as PH₃/H₂) cylinder, replacing the NO gas cylinder with a N₂ gas (99.999 % purity) cylinder and using H₂S gas from a not illustrated cylinder in Example 126, under the preparation conditions shown in Table 133 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 136 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 126, under the preparation conditions shown in Table 134, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 137 A light receiving member for use in electrophotography was prepared in the same manner as in Example 131 by further using the hydrogen gas-diluted PF₅ gas (99.999 % purity, hereinafter simply referred to as PF₃/H₂) from a not illustrated cylinder and PH₃/H₂ gas, replating the G₂H₂ gas cylinder with CH₄ gas cylinder, under the preparation conditions shown in Table 135 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 131. Example 138 A light receiving member for use in electrophotography was prepared in the same manner as in Example 136 by using a not illustrated Si₂F₆ gas cylinder, under the preparation conditions shown in Table 136 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 134. Example 139 A light receiving member for use in electrophotography was prepared in the same manner as in Example 136 by further using PH₃/H₂ gas and Si₂F₄ gas, under the preparation conditions shown in Table 137 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 136. Example 140 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using GeH₄ from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 138 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 126. Example 141 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by changing the outer diameter of the cylindrical aluminum support to 8o mm in Example 126, under the preparation conditions shown in Table 139 and, when evaluated in the same manner as in Example 126, except tor using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 142 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 126, under the preparation conditions shown in Table 140 and, when evaluated in the same manner as in Example 126, except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 143 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 126, under the preparation conditions shown in Table 141 and, when evaluated in the same manner as in Example 126, except for using an electrophotographic apparatus, i.e., a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 144 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 126, under the preparation conditions shown in Table 142, and evaluated in the same manner as in Example 126, except for using an electrophotographic apparatus, manufactured for experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 145 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 141 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 141 and further machined into a cross sectional shape of : a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 141, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 141. Example 146 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 141 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of : c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 141, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 141. Example 147 A light receiving member for use in electrophotography having an upper layer comprising poly-Si(H, X) was prepared in the same manner as in Example 134 by using a cylindrical aluminum support heated to a temperature of 500°C, under the preparation conditions as shown in Table 143 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 134. Example 148 A light receiving member for use in electrophotography was prepared by microwave glow discharge decomposition in the same manner as in Example 23 by further using SiF₄ gas, No gas and B₂H₆ gas in Example 23, under the same preparation conditions as shown in Table 144. When the light receiving member for use in electrophotography was evaluated in the same manner as in Example 126. satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 149 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 126, under the preparation conditions shown in Table 145 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 150 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by replacing the NO gas cylinder with a N₂ gas cylinder in Example 126, under the preparation conditions shown in Table 146 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 151 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by using PF₅ gas and Si₂F₆ gas from a not illustrated cylinder and replacing NO gas cylinder with a NH₃ gas cylinder in Example 126, under the preparation conditions shown in Table 147 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 152 A light receiving member for use in electrophotography was prepared in the same manner as in Example 131 by further using PF₅/H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 148 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 131. Example 153 A light receiving member for use in electrophotography was prepared in the same manner as in Example 134, under the preparation conditions shown in Table 149 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 134. Example 154 A light receiving member for use in electrophotography was prepared in the same manner as in Example 136 by further using PH₃/H₂ gas, under the preparation conditions shown in Table 150 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 136. Example 155 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using the He gas (99.999 % purity) from a not illustrated cylinder in the Example 126, under the preparation conditions shown in Table 151 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 156 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using C₂H₂ gas and PH₃/H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 151 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 157 A light receiving member for use in electrophotography was prepared in the same manner as in Example 131 by further using PH₃/H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 153 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 131. Example 158 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 154 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 159 A light receiving member for use in electrophotography was prepared in the same manner as in Example 158 by further using C₂H₂ gas and PH₃/H₂ from a not illustrated cylinder, under the preparation conditions shown in Table 155 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 158. Example 160 A light receiving member for use in electrophotography was prepared in the same manner as in Example 126 by further using C₂H₂ gas, PF₃/H₂ gas and H₂S gas from a not was prepared in the same manner as in Example 126 by further using C₂H₂ gas, PF₃/H₂ gas and H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 156 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 126. Example 161 A light receiving member for use in electrophotography was prepared in the same manner as in Example 134 by further using C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 134 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 134. Example 162 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 158, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 163 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 159. and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 164 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161 by using BF₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 160, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 165 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 161 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 166 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 162 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 167 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 163 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 168 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 164 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 169 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 165 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 170 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161 by further using PH₃ gas and Si₂F₆ gas from a not illustrated cylinder, under the preparation conditions shown in Table 166 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 171 A light receiving member for use in electrophotography was prepared in the same manner as in Example 170, under the preparation conditions shown in Table 167 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 170. Example 172 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161 by further using H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 168 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 173 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 169 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 174 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 170 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 175 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161 by further using NH₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 171 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 176 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161 by further using N₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 172 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 177 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 173 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 178 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 174 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 179 A light receiving member for use in electrophotography was prepared in the same manner as in Example 170, under the preparation conditions shown in Table 175 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 170. Example 180 A light receiving member for use in electrophotography was prepared in the same manner as in Example 161, under the preparation conditions shown in Table 176 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 161. Example 181 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 by further using GeH₄ gas upon forming the lower layer in Example 1, under the same preparation conditions as shown in Table 177. Comparative Example 5 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 181 except for not using GeH₄ gas and H₂ gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electrophotography are shown in Table 178. The light receiving members for use in electrophotography thus prepared in Example 181 and Comparative Example 5 were set respectively to an electrophotographic apparatus, i.e. , a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 181 was less than 2/5 of that of the light receiving member for use in electrophotography in Comparative Example 5. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 181 was less than 1/3 for that of the light receiving member for use in electrophotography in Comparative Example 5. and the light receiving member for use in electrophotography of Example 181 was excellent over the light receiving member for use in Electrophotography of Comparative Example 5 in view of the visual observation. In addition, for comparing the occurrence of image defects and the peeling of the light receiving layer due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, when stainless steel balls of 3.5 mm diameter were fallen freely from the vertical height of 30 cm above the surface of the light receiving member for use in electrophotography and abutted against the surface of the light receiving member for use in electrophotography, to thereby measure the frequency that cracks occurred to the light receiving layer, it was found that the rate of occurrence in the light receiving member for use in electrophotography of Example 181 was less than 1/3 for that in the light receiving member for use in electrophotography of Comparative Example 5. When the lower layer of the light receiving member for use in electrophotography of Example 181 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. As has been described above, the light receiving member for use in electrophotography of Example 181 was superior to the light receiving member for use in electrophotography of Comparative Example 5. Example 182 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by changing the way of varying the AlCl₃/He gas flow rate in the lower layer, under the preparation conditions shown in Table 179, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 183 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 not using the CH₄ gas in the upper layer of Example 181, under the preparation conditions shown in Table 180, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 184 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using He gas (99.9999 % purity) and N₂ gas from a not illustrated cylinder in Example 181, under the preparation conditions shown in Table 181, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 185 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by replacing the B₂H₆/H₂ gas cylinder with hydrogen-diluted PH₃ gas (99.999 % purity, hereinafter simply referred to as PH₃/H₂) cylinder, replacing the NO gas cylinder with NH₃ gas (99.999 % purity) cylinder in Example 181, under the preparation conditions shown in Table 182, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 186 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using C₂H₂ gas from a not illustrated cylinder in Example 181, under the preparation conditions shown in Table 183 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 181. Example 187 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using PH₃/H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 184 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 181. Example 188 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using N₂ gas, H₂S (99.9 % purity) and PH₃/H₂ gas from a not illustrated cylinder in Example 181, under the preparation conditions shown in Table 185, and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 181. Example 189 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by replacing the GeH₄ gas cylinder with GeF₄ gas (99.999 % purity), and replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder in Example 181, under the preparation conditions shown in Table 186 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 190 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by replacing the B₂H₆/H₂ gas cylinder with H₂-diluted BF₃ gas (99.999 % purity, hereinafter simply referred to as BF₃/H₂) cylinder and replacing the NO gas cylinder with N₂ gas and also using H₂S gas from a not illustrated cylinder in Example 181, under the preparation conditions shown in Table 187, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 191 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder in Example 181, under the preparation conditions shown in Table 188, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 192 A light receiving member for use in electrophotography was prepared in the same manner as in Example 186 by replacing the PF₅ gas diluted with hydrogen (99.999 % purity, hereinafter simply referred to as PH₃/H₂) from a not illustrated cylinder and further using B₂H₆/H₂ gas, under the preparation conditions shown in Table 189, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 186. Example 193 A light receiving member for use in electrophotography was prepared in the same manner as in Example 189 by using Si₂H₆ (99.99 % purity), Si₂F₆ (99199 % purity) gas, under the preparation conditions shown in Table 190. and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 189. Example 194 A light receiving member for use in electrophotography was prepared in the same manner as in Example 191 by further using PF₅/H₂ gas and Si₂F₆ gas, under the preparation conditions shown in Table 191 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 191. Example 195 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using GeH₄ gas in the upper layer, under the preparation conditions shown in Table 192 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 181. Example 196 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by changing the outer diameter of the cylindrical aluminum support to 80 mm in Example 181, under the preparation conditions shown in Table 193 and, when evaluated in the same manner as in Example 181, except for using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 197 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 181, under the preparation conditions shown in Table 194 and, when evaluated in the same manner as in Example 181, except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 198 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 181, under the preparation conditions shown in Table 195 and, when evaluated in the same manner as in Example 181, except for using an electrophotographic apparatus, i.e. , a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 199 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 181, under the preparation conditions shown in Table 196, and evaluated in the same manner as in Example 181, except for using an electrophotographic apparatus, manufactured for experimental use and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 200 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 196 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 196 and further machined into a cross sectional shape of a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 196, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 196. Example 201 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 196 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of : c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 196, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 196. Example 202 A light receiving member for use in electrophotography in the same manner as in Example 189 having an upper layer comprising poly-Si(H, X) was prepared by using a cylindrical aluminum support heated to a temperature of 500°C, under the preparation conditions as shown in Table 197 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 189. Example 203 A light receiving member for use in electrophotography was prepared by microwave glow discharge decomposition in the same manner as in Example 23 by further using GeH₄ gas, B₂H₆ gas and NO gas upon forming the lower layer in Example 23, under the same preparation conditions as shown in Table 198. When the light receiving member for use in electrophotography was evaluated in the same manner as in Example 181. satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 204 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder, and replacing GeH₄ gas cylinder with a GeF₄ gas cylinder and further using Si₂F₆ gas in Example 181, under the preparation conditions shown in Table 199 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 205 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181, under the preparation conditions shown in Table 200 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 206 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by using SnH₄ gas (99.99 % purity), PF₅ gas and Si₂F₆ gas from a not illustrated cylinder and replacing NO gas cylinder with a NH₃ gas cylinder in Example 181, under the preparation conditions shown in Table 201 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 207 A light receiving member for use in electrophotography was prepared in the same manner as in Example 186 by further using PF₅/H₂ gas and SiF₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 202 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 186. Example 208 A light receiving member for use in electrophotography was prepared in the same manner as in Example 189, under the preparation conditions shown in Table 203 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 189. Example 200 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using PH₃/H₂ gas, under the preparation conditions shown in Table 204 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 210 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using He gas and N₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 205 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 211 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using C₂H₂ gas, SiF₄ gas and PH₃/H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 206 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 212 A light receiving member for use in electrophotography was prepared in the same manner as in Example 211 by further using PH₃/H₂ gas and SiF₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 207 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 211. Example 213 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 208 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 214 A light receiving member for use in electrophotography was prepared in the same manner as in Example 213 by further using C₂H₂ gas, PH₃/H₂ and SnH₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 209 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 213. Example 215 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using C₂H₂ gas, PF₃/H₂ gas, H₂ S gas and SiF₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 210 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 216 A light receiving member for use in electrophotography was prepared in the same manner as in Example 189 by further using C₂H₂ gas and SiF₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 211 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 189. Example 217 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216 by using SnH₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 212, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 218 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 213 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 219 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216 by using BF₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 214, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 220 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 215 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 221 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 216 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 222 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 217 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 223 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 218 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 224 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 219 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 225 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216 by further using PH₃ gas and Si₂F₆ gas from a not illustrated cylinder, under the preparation conditions shown in Table 220 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 226 A light receiving member for use in electrophotography was prepared in the same manner as in Example 225, under the preparation conditions shown in Table 221 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 225. Example 227 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216 by further using H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 222 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 228 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 223 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 229 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 224 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 230 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216 by further using NH₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 225 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 231 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216 by further using N₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 226 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 232 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 227 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 233 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 228 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 234 A light receiving member for use in electrophotography was prepared in the same manner as in Example 225, under the preparation conditions shown in Table 229 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 225. Example 235 A light receiving member for use in electrophotography was prepared in the same manner as in Example 216, under the preparation conditions shown in Table 230 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 216. Example 236 The light receiving member for use in electrophotography according to this invention was formed by radio frequency (hereinafter simply referred to as "RF") glow discharge decomposition. Fig. 37 shows an apparatus for producing the light receiving member for use in electrophotography by the RF glow discharge decomposition, comprising a raw material gas supply device 1020 and a deposition device 1000. In the figure, raw material gases for forming the respective layers in this invention were tightly sealed in gas cylinders 1071, 1072, 1073, 1074, 1075, 1076, 1077 and 1079, and tightly sealed vessels 1078 and 1080 in which the cylinder 1071 was for SiH₄ gas (99.99 % purity), the cylinder 1072 was for H₂ gas (99.9999 %), the cylinder 1073 was for CH₄ gas (99.999 % purity), the cylinder 1074 was for GeH₄ gas (99.999 %), the cylinder 1075 was for PH₃ gas diluted with H₂ gas (99.999 % purity, hereinafter simply referred to as "PH₃/H₂"), the cylinder 1076 was for NO gas (99.9 % purity) , the cylinders 1077 and 1079 were for He gas (99.999 % purity), the tightly sealed vessel 178 was charged with AlCl₃ (99.999 % purity) and the tightly sealed vessel 178 was charged with Mg(C₅H₅)₃ (99.999 % purity). In the figure, a cylindrical aluminum support 1005 had an outer diameter of 108 mm and a mirror-finished surface. After confirming that valves 1051 - 1058 for the gas cylinders 1071 - 1077 and 1079, flow-in valves 1031 - 1038 and a leak valve 1015 for the deposition chamber 1001 were closed and flow-out valves 1041 - 1048 and an auxiliary valve 1018 were opened, a main valve 1016 was at first opened to evacuate the deposition chamber 1001 and gas pipeways by a vacuum pump not illustrated. Then, when the indication of a vacuum meter 1017 showed about 1 x 10⁻³ Torr, the auxiliary valve 1018, the flow-out valves 1041 - 1048 were closed. Then, the valves 1051 - 1058 were opened to introduce SiH₄ from the gas cylinder 1071, H₂ gas from the gas cylinder 1072, CH₄ gas from the gas cylinder 1073, GeH₄ gas from the gas cylinder 1074, B₂H₅/H₂ gas from the gas cylinder 1075, NO gas from the gas cylinder 1076 and He gas from the gas cylinders 1077 and 1079. and the pressures for the respective gases were adjusted to 2 kg/cm² by pressure controllers 1061 - 1068. Then, the flow-in valves 1031 - 1038 were gradually opened to introduce the respective gases in mass flow controllers 1021 - 1028. In this case, since the He gas from the gas cylinder 1077 was passed through the tightly sealed vessel 1078 charged with AlCl₃, the AlCl₃ gas diluted with the He gas (hereinafter simply referred to as "AlCl₃/He") was introduced to the mass flow controller 1027 and since the He gas from the gas cylinder 1079 was passed through the tightly sealed vessel 1080 charged with Mg(C₅H₅)₂, the Mg(C₅H₅)₃ gas diluted with the He gas (hereinafter simply referred to as "Mg(C₅H₅)₂/He") was introduced to the mass flow controller 1028. The temperature of the cylindrical aluminum support 1005 disposed in the deposition chamber 1001 was heated to 250°C by a heater 1014. After completing the preparation for the film formation as described above, each of the lower and upper layers was formed on the cylindrical aluminum support 1005. The lower layer was formed by gradually opening the flow-out valves 1041, 1042, 1047 and 1048, and the auxiliary valve 1018 thereby introducing the SiH₄ gas, H₂ gas, AlCl₃/He gas and Mg(C₅H₅) gas through the gas discharge aperture 1009 of a gas introduction pipe 1008 to the inside of the deposition chamber 1001. In this case, the gas flow rates were controlled by the respective mass flow controllers 1021, 1022, 1027 and 1028 such that the gas flow rates were set to 50 SCCM for SiH₄, 10 SCCM for H₂ gas, 120 SCCM for AlCl₃/He and 10 SCCM for Mg(C₅H₅)₂. The pressure in the deposition chamber 1101 was controlled to 0.4 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced to the inside of the deposition chamber 1001 by way of an RF matching box 1012 while setting the power of RF power source (not illustrated) to 5 mW/cm³, to cause RF glow discharge, thereby starting the formation of the lower layer on the aluminum support. The mass flow controllers 1021, 1022, 1027 and 1028 were adjusted during formation of the lower layer such that the SiH₄ gas flow remains at a constant rate of 50 SCCM the H₂ gas flow rate was increased at a constant ratio from 10 SCCM to 200 SCCM, the AlCl₃/He gas flow rate was decreased at a constant ratio from 120 SCCM to 40 SCCM and Mg(C₅H₅)₂/He gas flow remains at a constant rate of 10 SCCM. Then, when the lower layer of 0.05 um thickness was formed, the RF glow discharge was stopped and the entrance of the gas to the inside of the deposition chamber 1001 is interrupted by closing the flow-out valves 1041, 1042, 1047 and 1048, and the auxiliary valve 1018, to complete the formation of the lower layer. Then, for forming the first layer region of the upper layer, the flow-out valves 1041, 1042 and 1046, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas, H₂ gas and NO gas through the gas discharge aperture 1009 of the gas introduction pipe 1008 into the deposition chamber 1001. In this case, respective mass flow controllers 1021, 1022 and 1026 were adjusted so that the SiH₄ gas flow rate was 100 SCCM, H₂ gas flow rate was 100 SCCM and NO gas flow rate was 30 SCCM. The pressure in the deposition chamber 1001 was controlled to 0.35 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced into the deposition chamber 1001 through a radio frequency matching box 1012 while setting the power of RF power source (not illustrated) to 10 mW/cm³, to cause RF glow discharge and start the formation of the first layer region of the upper layer over the lower layer. Then, when the first layer region of the upper layer with 3 um thickness was formed, the RF glow discharge was stopped and the flow of the gas into the deposition chamber 1001 was interrupted by closing the flow-out valves 1041, 1042 and 1046, and the auxiliary valve 1018, thereby completing the formation of the first layer region of the upper layer. Then, for forming the second layer region of the upper layer, the flow-out valves 1041 and 1042, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas and H₂ gas through the gas discharge aperture 1009 of the gas introduction pipe 1008 into the deposition chamber 1001. In this case, respective mass flow controllers 1021 and 1022 were adjusted so that the SiH₄ gas flow rate was 300 SCCM and H₂ flow rate was 300 SCCM. The pressure in the deposition chamber 1001 was controlled to 0.5 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced into the deposition chamber 1001 through the radio frequency matching box 1012 while setting the power of the RF power source (not illustrated) to 15 mW/cm³, to cause the RF glow discharge and start the formation of the second layer region on the first layer region of the upper layer. Then, when the second layer region of the upper layer with 20 um thickness was formed, the RF glow discharge was stopped and the flow of the gas into the deposition chamber 1001 was interrupted by closing the flow-out valves 1041 and 1042, and the auxiliary valve 1018, thereby completing the formation of the second layer region of the upper layer. Then, for forming the third layer region of the upper layer, the flow-out valves 1041 and 1043, and the auxiliary valve 1018 were gradually opened to flow SiH₄ gas and CH₄ gas through the gas discharge aperture 1009 of the gas introduction pipe 1008 into the deposition chamber 1001. In this case, respective mass flow controllers 1021 and 1023 were adjusted so that the SiH₄ gas flow rate was 50 SCCM and CH₄ flow rate was 500 SCCM. The pressure in the deposition chamber 1001 was controlled to 0.4 Torr by adjusting the opening of the main valve 1016 while observing the vacuum meter 1017. Then, RF power was introduced into the deposition chamber 1001 through the radio frequency matching box 1012 while setting the power of RF power source (not illustrated) to 10 mN/cm³, to cause the RF glow discharge and start the formation of the third layer region on the second layer region of the upper layer. Then, when the third layer region of the upper layer with 0.5 um thickness was formed, the RF glow discharge was stopped and the flow of the gas into the deposition chamber 1001 was interrupted by closing the flow-out valves 1041 and 1043, and the auxiliary valve 1018, thereby completing the formation of the third layer region of the upper layer. The conditions for preparing the light receiving member for use in electrophotography described above are shown in Table 231. It will be apparent that all of the flow-out valves other than those required for forming respective layers were completely closed and, for avoiding the respective gases from remaining in the deposition chamber 1001 and in the pipeways from the flow-out valves 1041 - 1048 to the deposition chamber 1001, the flow-out valves 1041 - 1048 were closed, the auxiliary valve 1018 was opened and, further, the main valve was fully opened thereby evacuating the inside of the system once to a high vacuum degree as required. Further, for forming the layer uniformly during this layer formation, the cylindrical aluminum support 1005 was rotated at a desired speed by a driving device not illustrated. Comparative Example 6 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 236 except for not using H₂ gas and Mg(C₅H₅)₂/H₂ gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electrophotography are shown in Table 232. The light receiving members for use in electrophotography thus prepared in Example 236 and Comparative Example 6 were set respectively to an electrophotographic apparatus, i.e., a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 236 was less than 1/3 of that of the light receiving member for use in electrophotography in Comparative Example 6. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 236 was less than 1/4 for that of the light receiving member for use in electrophotography in Comparative Example 6 and the light receiving member for use in electrophotography of Example 236 was excellent over the light receiving member for use in Electrophotography of Comparative Example 6 in view of the visual observation. In addition, for comparing the occurrence of image defects and the peeling of the light receiving layer due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, when stainless steel balls of 3.5 mm diameter were fallen freely from the vertical height of 30 cm above the surface of the light receiving member for use in electrophotography and abutted against the surface of the light receiving member for use in electrophotography, to thereby measure the frequency that cracks occurred to the light receiving layer, it was found that the rate of occurrence in the light receiving member for use in electrophotography of Example 236 was less than 1/4 for that in the light receiving member for use in electrophotography of Comparative Example 6. When the lower layer of the light receiving member for use in electrophotography of Example 236 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. As has been described above, the light receiving member for use in electrophotography of Example 236 was superior to the light receiving member for use in electrophotography of Comparative Example 6. Example 237 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by changing the way of varying the AlCl₃/He gas flow rate in the lower layer, under the preparation conditions shown in Table 233 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 238 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by not using the CH₄ gas in the upper layer of Example 236, under the preparation conditions shown in Table 234 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 239 A light receiving member for use in electrophotography was prepared in the same manner as in Example 181 by further using not illustrated SiF₄ gas (99.9999 % purity), not illustrated He gas (99.999 % purity) and not illustrated N₂ gas in Example 236, under the preparation conditions shown in Table 235 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 240 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by replacing GeH₄ gas cylinder with Ar gas (99.9999 % purity) cylinder, replacing NO gas cylinder with NH₃ gas (99.999 % purity) cylinder, replacing B₂H₆/H₂ gas cylindr with H₂-diluted PH₃ gas (99.999 % purity, hereinafter simply referred to as "PH₃/H₂ gas") purity, hereinafter simply referred to as PH₃/H₂) cylinder, replacing the NO gas cylinder with NH₃ gas (99.999 % purity) cylinder in Example 236, under the preparation conditions shown in Table 236 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 241 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas, not illustrated PH₃/H₂ gas, not illustrated C₂H₂ gas and not illustrated SiF₄ gas, under the preparation conditions shown in Table 237 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 236. Example 242 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by replacing GeH₄ gas cylinder with SiF₄ gas (99.999 % purity) cylinder, and further using NO gas, not illustrated PH₃/H₂ gas, B₂H₆/H₂ gas and Si/F₄ gas, under the preparation conditions shown in Table 238 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 236. Example 243 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas, not illustrated H₂S (99.9 % purity), not illustrated PH₃/H₂ gas and not illustrated N₂ gas, under the preparation conditions shown in Table 239, and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 181. Example 244 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 replacing the CH₄ gas cylinder with C₂H₂ gas (99.999 % purity) cylinder in Example 236, under the preparation conditions shown in Table 240 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 245 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by replacing the B₂H₆/H₂ gas cylinder with BF₃ gas diluted H₂ (99.999 % purity, hereinafter simply referred to as BF₃/H₂) cylinder, and replacing the NO gas cylinder with N₂ gas and using H₂S gas from a not illustrated cylinder in Example 236, under the preparation conditions shown in Table 241, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 181. Example 246 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by replacing the NO gas cylinder with a NH₃ gas (99.999 % purity) cylinder, replacing B₂H₆/H₂ gas cylinder with PH₃/H₂ gas cylinder in Example 236, under the preparation conditions shown in Table 242, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 247 A light receiving member for use in electrophotography was prepared in the same manner as in Example 241 by further using H₂-diluted PF₅ gas from a not illustrated cylinder (99.999 % purity, hereinafter simply referred to as "PF₅/H₂ gas"), SiF₄ gas and B₂H₆/H₂ gas, under the preparation conditions shown in Table 243, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 241. Example 248 A light receiving member for use in electrophotography was prepared in the same manner as in Example 244 by further using Si₂H₆ (99.99 % purity), Si₂F₆ (99199 % purity) gas and PH₃/H₃ gas, under the preparation conditions shown in Table 244, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 244. Example 249 A light receiving member for use in electrophotography was prepared in the same manner as in Example 246 by further using B₂H₆/H₂ gas from a not illustrated cylinder, PH₅/H₂ gas and Si₂F₆ gas, under the preparation conditions shown in Table 245 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 246. Example 250 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas and GeH₄ gas in the upper layer, under the preparation conditions shown in Table 246 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 236. Example 251 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by changing the outer diameter of the cylindrical aluminum support to 80 mm in Example 247, under the preparation conditions shown in Table 193 and, when evaluated in the same manner as in Example 236, except for using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 252 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 236, under the preparation conditions shown in Table 248 and, when evaluated in the same manner as in Example 236 except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 253 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 236, under the preparation conditions shown in Table 249 and, when evaluated in the same manner as in Example 236, except for using an electrophotographic apparatus, i.e., a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 254 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 236, under the preparation conditions shown in Table 250, and evaluated in the same manner as in Example 236, except for using an electrophotographic apparatus, manufactured for experimental use and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 255 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 251 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 251 and further machined into a cross sectional shape of : a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 251, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 251. Example 256 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 251 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of : c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 251, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 251. Example 257 A light receiving member for use in electrophotography having an upper layer comprising poly-Si(H, X) was prepared in the same manner as in Example 244 by using a cylindrical aluminum support heated to a temperature of 500°C, under the preparation conditions as shown in Table 251 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 244. Example 258 A light receiving member for use in electrophotography was prepared by microwave glow discharge decomposition in the same manner as in Example 23 by further using SiF₄ gas, NO gas, Mg(C₅H₅)₂/He gas and B₂H₆ gas upon forming the lower layer in Example 23, under the same preparation conditions as shown in Table 252. When the light receiving member for use in electrophotography was evaluated in the same manner as in Example 236. satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. When the lower layer of the light receiving member for use in electrophotography of Example 258 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. Example 259 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by replacing the CH₄ gas cylinder with a C₂H₂ gas (99.9999 % purity) cylinder, and further using B₂H₆/H₂ gas Si₂F₆ gas in Example 236, under the preparation conditions shown in Table 253 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 260 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas, N₂ gas, under the preparation conditions shown in Table 254 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 261 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by using SnH₄ gas (99.99% purity) from a not illustrated cylinder, PF₅/H₂ gas, Si₂/f₆ gas and replacing NO gas cylinder with NH₃ gas (99.999 %, purity) cylinder in Example 236, under the preparation conditions shown in Table 255 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 262 A light receiving member for use in electrophotography was prepared in the same manner as in Example 241 by replacing N₂ gas cylinder with SiF₄ gas and further using PF₅H₂ gas from a not illustrated cylinder, SiF₄ gas in Example 236, under the preparation conditions shown in Table 256 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 241. Example 263 A light receiving member for use in electrophotography was prepared in the same manner as in Example 244 by further using Si₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 257 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 244. Example 264 A light receiving member for use in electrophotography was prepared in the same manner as in Example 246 by further using B₂H₆/H₂ gas in the upper layer, under the preparation conditions shown in Table 258 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 246. Example 265 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas and He gas from a not illustrated cylinder, under the preparation conditions shown in Table 259 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 266 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas, SiF₄ gas from a not illustrated cylinder, C₂H₂ gas and PH₃/H₂, under the preparation conditions shown in Table 266 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 267 A light receiving member for use in electrophotography was prepared in the same manner as in Example 241, under the preparation conditions shown in Table 261 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 241. Example 268 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using B₂H₆/H₂ gas, C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 262 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 269 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using C₂H₂ gas from a not illustrated cylinder, PH₃/H₂ gas, under the preparation conditions shown in Table 262 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 270 A light receiving member for use in electrophotography was prepared in the same manner as in Example 236 by further using GeH₄ gas, H₂S gas from a not illustrated cylinder, PH₃/H₂ gas, C₂H₂ gas and SiF₄, under the preparation conditions shown in Table 264 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 271 A light receiving member for use in electrophotography was prepared in the same manner as in Example 244 by further using SiH₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 265 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 244. Example 272 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 266 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 273 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 267 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 274 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271 by further using BF₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 268 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 275 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 269 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 276 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 270 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 277 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 271 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 278 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 272 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 279 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 273 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 280 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271 by further using PH₃ gas from a not illustrated cylinder and Si₂F₆ gas, under preparation conditions shown in Table 274 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 281 A light receiving member for use in electrophotography was prepared in the same manner as in Example 280, under the preparation conditions shown in Table 275 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 280. Example 282 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271 by using H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 276 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 283 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 277 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 284 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 278 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 285 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271 by using NH₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 279 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 286 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271 by using N₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 280 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 287 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 281 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 288 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 282 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 271. Example 289 A light receiving member for use in electrophotography was prepared in the same manner as in Example 280, under the preparation conditions shown in Table 283 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 280 Example 290 A light receiving member for use in electrophotography was prepared in the same manner as in Example 271, under the preparation conditions shown in Table 284 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 71. Example 291 A lower layer of a light receiving member for use in electrophotography according to this invention was formed by RF sputtering method and the upper layer thereof was formed RF glow discharge decomposition. Fig. 42 shows an apparatus for producing the light receiving member for use in electrophotography by the RF sputtering, comprising a raw material gas supply device 1500 and a deposition device 1501. In the figure, a target 1045 is composed of Si, Al and Mg as the raw material for forming the lower layer, in which the mixing ratio for the atoms is varied such that a desired profile is obtained across the thickness for each of the atoms. In the figure, raw material gases for forming the lower layer in this invention were tightly sealed in gas cylinders 1408, 1409 and 1410, in which the cylinder 1408 was for SiH₄ gas (99.99 % purity), the cylinder 1409 was for H₂ gas (99.9999 %) and the cylinder 1076 was for Ar gas (99.9999 % purity). In the figure, a cylindrical aluminum support 1402 has an outer diameter of 108 mm and a mirror-finished surface. At first, in the same manner as in Example 1, the inside of the deposition chamber 1401 and gas pipeways was evacuated till the pressure of the deposition chamber 1401 was reduced to 1 x 10⁻⁶ Torr. Then, in the same manner as in Example 1, the respective gases were introduced into the mass flow controllers 1412 - 1414. The temperature of the cylindrical aluminum support 1402 disposed in the deposition chamber 1401 was heated to 250°C by a heater not illustrated. After completing the preparation for the film formation as described above, the lower layer was formed on the cylindrical aluminum support 1402. The lower layer was formed by gradually opening the flow-out valves 1420, 1421 and 1422, and the auxiliary valve 1432 thereby introducing the SiH₄ gas, H₂ gas and Ar gas to the inside of the deposition chamber 1401. In this case, the gas flow rates were controlled by the respective mass flow controllers 1412, 1413 and 1414 such that the gas flow rates were set to 50 SCCM for SiH₄, 10 SCCM for H₂ gas, and 200 SCCM for Ar gas. The pressure in the deposition chamber 1401 was controlled to 0.01 Torr by adjusting the opening of the main valve 1407 while observing the vacuum meter 1435. Then, RF power was introduced between the target 1405 and the aluminum support 1402 by way of an RF matching box 1433 while setting the power of an RF power source (not illustrated) to 1 mW/cm³, thereby starting the formation of the lower layer on the cylindrical aluminum support. The mass flow controllers 1412, 1413 and 1414 were adjusted during formation of the lower layer such that the SiH₄ gas flow remained at a constant rate of 50 SCCM, the H₂ gas flow rate was increased at a constant ratio from 5 SCCM to 100 SCCM and the Ar gas flow rate remained at a constant ratio of 204 SCCM. Then, when the lower layer of 0.05 um thickness was formed, the RF glow discharge was stopped and the entrance of the gas to the inside of the deposition chamber 1401 was interrupted by closing the flow-out valves 1420, 1421 and 1423 and the auxiliary valve 1432, to complete the formation of the lower layer. The cylindrical aluminum support 1402 was rotated at a desired speed by a driving device not illustrated during formation of the lower layer for making the layer formation uniform. Then, a light receiving member for use in electrophotography was prepared in the same manner as in Example 265 under the preparation conditions shown in Table 285 by using the device illustrated in Fig. 37 upon forming the upper layer. When the same evaluation was applied, satisfactory improvement was obtained to dots, coarse image and layer peeling in the same manner as in Example 265. When the lower layer of the light receiving member for use in electrophotography of Example 291 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. Example 292 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 under the preparation conditions shown in Table 286 by further using Cu(C₄H₇N₂O₂)₂/He gas upon forming the lower layer in Example 1. Comparative Example 7 A light receiving member for use in electrophotography was prepared under the same preparation conditions as those in Example 292 except for not using H₂ gas and Cu(C₄H₇N₂O₂)₂/He gas upon forming the lower layer. The conditions for preparing the light receiving member for use in electrophotography are shown in Table 287. The light receiving members for use in electrophotography thus prepared in Example 292 and Comparative Example 7 were set respectively to an electrophotographic apparatus, i.e., a copying machine NP-7550 manufactured by Canon Inc. and modified for experimental use and, when several electrophotographic properties were checked under various conditions, it was found that both of them had outstanding characteristics with voltage withstanding property in that no image defects were formed even if a high voltage was applied to the light receiving member for use in electrophotography by highly intensive corona discharge or frictional discharge by means of a cleaning agent. Then, when the number of dots as the image characteristics were compared, it was found that the number of dots, particularly, the number of dots with less than 0.1 mm diameter of the light receiving member for use in electrophotography of Example 292 was less than 1/4 of that of the light receiving member for use in electrophotography in Comparative Example 7. In addition, for comparing the "coarse image", when the image density was measured for circular regions each of 0.05 mm diameter assumed as one unit at 100 points and the scattering in the image density was evaluated, it was found that the scattering in the light receiving member for use in electrophotography of Example 292 was less than 1/5 for that of the light receiving member for use in electrophotography in Comparative Example 7 and the light receiving member for use in electrophotography of Example 292 was excellent over the light receiving member for use in Electrophotography of Comparative Example 7 in view of the visual observation. In addition, for comparing the occurrence of image defects and the peeling of the light receiving layer due to impactive mechanical pressure applied for a relatively short period of time to the light receiving member for use in electrophotography, when stainless steel balls of 3.5 mm diameter were fallen freely from the vertical height of 30 cm above the surface of the light receiving member for use in electrophotography and abutted against the surface of the light receiving member for use in electrophotography, to thereby measure the frequency that cracks occurred to the light receiving layer, it was found that the rate of occurrence in the light receiving member for use in electrophotography of Example 292 was less than 1/5 for that in the light receiving member for use in electrophotography of Comparative Example 7. When the lower layer of the light receiving member for use in electrophotography of Example 292 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. As has been described above, the light receiving member for use in electrophotography of Example 292 was superior to the light receiving member for use in electrophotography of Comparative Example 6. Example 293 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using B₂H₆/H₂ gas and NO gas and changing the way of varying the AlCl₃/He gas flow rate in the lower layer, under the preparation conditions shown in Table 288, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 294 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using Mg(C₅H₅) gas diluted with He gas (hereinafter simply referred to as "Mg(C₅H₅)₂/He") from a not illustrated sealed vessel and GeH₄ gas in the lower layer, and He gas from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 289 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 295 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by further using Mg(C₅H₅)₂/He gas from a not illustrated sealed vessel, CH₄ gas, B₂H₆/H₂ gas, NO gas, SiF₄ gas (99.999 % purity) from a not illustrated cylinder, N₂ gas from a not illustrated cylinder and He gas, under the preparation conditions shown in Table 290 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 296 A light receiving member for use in electrophotography was prepared in the same manner as in Example 291 by replacing H₂ gas cylinder with Ar gas cylinder (99.9999 % purity), CH₄ gas cylinder with NH₃ gas cylinder (99.999 % purity), and further using SiV₄ gas in the upper layer, under the preparation conditions shown in Table 291 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 297 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using CH₄ gas and B₂H₆/H₂ gas in the lower layer, and PH₃/H₂ gas (99.999 % purity) from a not illustrated cylinder in the upper layer, under the preparation conditions shown in Table 292, and when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 298 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing NO gas cylinder with SiF₄ gas cylinder in the lower layer, and further using PH₃/H₂ from a not illustrated cylinder in the upper layer in Example 292, under the preparation conditions shown in Table 293 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 292. Example 299 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using Mg(C₅H₅)₂/He gas from a not illustrated sealed vessel in the lower layer, and PH₃/H₂ gas from a not illustrated cylinder and N₂ gas in the upper layer, under the preparation conditions shown in Table 294 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 292. Example 300 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by further using CH₄ gas and B₂H₆/H₂ gas in the lower layer, and replacing CH₄ gas cylinder with C₂H₂ gas (99.9999 % purity) cylinder in the upper layer, under the preparation conditions shown in Table 295 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 292. Example 301 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using Mg(C₅H₅)₂/He gas from a not illustrated sealed vessel, replacing B₂H₆ gas cylinder with PH₃/H₂ gas cylinder and further using SiF₄ gas from a not illustrated cylinder, under the preparation conditions shown in Table 296 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 292. Example 302 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing CH₄ gas cylinder with NH₃ gas (99.999 % purity) cylinder in Example 292, and using NH₃ gas in the upper layer, under the preparation conditions shown in Table 297, and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 292. Example 303 A light receiving member for use in electrophotography was prepared in the same manner as in Example 297 by using CH₄ gas in the lower layer, and further using SiF₄ gas in the upper layer, under the preparation conditions shown in Table 298 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 297. Example 304 A light receiving member for use in electrophotography was prepared in the same manner as in Example 300 by replacing CH₄ gas with C₂H₂ gas, using PH₃/H₂ gas from a not illustrated cylinder in the lower layer, and further using Si₂F₆ gas (99.99 % purity) cylinder from a not illustrated cylinder and Si₂F₆ gas (99.99 a% purity) in the upper layer, under the preparation conditions shown in Table 299 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 300. Example 305 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using Si₂F₆ gas, PH₃ gas and NH₃ gas from a not illustrated cylinder, under the preparation conditions shown in Table 300, and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 306 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292, under the preparation conditions shown in Table 301 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 307 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by changing the outer diameter of the cylindrical aluminum support to 80 mm in Example 292, under the preparation conditions shown in Table 302 and, when evaluated in the same manner as in Example 292, except for using an electrophotographic apparatus, i.e., a copying machine NP-9030 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 308 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by changing the outer diameter of the cylindrical aluminum support to 60 mm in Example 292, under the preparation conditions shown in Table 303 and, when evaluated in the same manner as in Example 292, except for using an electrophotographic apparatus, i.e., a copying machine NP-150Z manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 309 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by changing the outer diameter of the cylindrical aluminum support to 30 mm in Example 294, under the preparation conditions shown in Table 304 and, when evaluated in the same manner as in Example 236, except for using an electrophotographic apparatus, i.e., a copying machine FC-5 manufactured by Canon Inc. and modified for the experimental use, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 310 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by changing the outer diameter of the cylindrical aluminum support to 15 mm in Example 292, under the preparation conditions shown in Table 305, and evaluated in the same manner as in Example 292, except for using an electrophotographic apparatus, manufactured for experimental use and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 311 A light sensitive member for use in electrophotography was prepared, under the same preparation conditions as those in Example 307 by using a cylindrical aluminum support applied with mirror-finishing fabrication in Example 307 and further machined into a cross sectional shape of : a = 25 um, b = 0.8 um as shown in Fig. 38 by a diamond point tool and, when evaluated in the same manner as in Example 207, satisfactory improvement was obtained to, the dots, coarse image and peeling in the same manner as in Example 307. Example 312 A light receiving member for use in electrophotography was prepared, under the same preparation conditions as those in Example 307 using a cylindrical aluminum support applied with mirror-finish fabrication and subsequently applied with a so-called surface dimpling of causing a number of hit pits to the surface of the cylindrical aluminum support by the exposure to a plurality of dropping bearing balls to form into a cross sectional shape of : c = 50 um and d = 1 um as shown in Figure 39 and, when evaluated in the same manner as in Example 307, satisfactory improvement was be obtained for the dots, coarse image and peeling in the same as in Example 307. Example 313 A light receiving member for use in electrophotography having an upper layer comprising poly-Si(H, X) was prepared in the same manner as in Example 300 by replacing CH₄ gas with C₂h₂ gas and using a cylindrical aluminum support heated to a temperature of 500°C, under the preparation conditions as shown in Table 306 and, when evaluated in the same manner, satisfactory improvement was obtained to dots, coarse image and peeling in the same manner as in Example 300. Example 314 A light receiving member for use in electrophotography was prepared by microwave glow discharge decomposition in the same manner as in Example 23 by further using Cu(C₄H₂N₂O₂)He gas, SiF₄ gas, NO gas and B₂H₆ gas upon forming the lower layer in Example 23, under the same preparation conditions as shown in Table 307. When the light receiving member for use in electrophotography was evaluated in the same manner as in Example 292, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. When the lower layer of the light receiving member for use in electrophotography of Example 314 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. Example 315 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing the CH₄ gas cylinder with a C₂H₂ gas cylinder in Example 292, under the preparation conditions shown in Table 308 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 316 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing B₂H₆/H₂ gas cylinder with PF₃/H₂ gas cylinder in Example 292, using CH₄ gas in lower layer, and using SiF₄ gas in the entire layer, under the preparation condition shown in Table 309 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 317 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing CH₄ gas cylinder with NH₃ gas cylinder, using SnH₄ from a not illustrated cylinder, Mg(C₅H₅)₂/He gas from a not illustrated sealed vessel in Example 292, under the preparation conditions shown in Table 310 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 318 A light receiving member for use in electrophotography was prepared in the same manner as in Example 297 by replacing B₂H₆/H₂ N₂ gas cylinder with PF₃/H₂ gas cylinder, and using SiF₄ gas, under the preparation conditions shown in Table 311 and, when evaluated in the same manner, satis factory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 241. Example 319 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing CH₄ gas cylinder with C₂H₂ gas cylinder, and further using Si₂H₆ gas in the upper layer, under the preparation conditions shown in Table 312 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 320 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing CH₄ gas cylinder with C₂H₂ gas cylinder in Example 292, and further using PH₃/H₂ gas from a nor illustrated gas cylinder in the upper layer, under the preparation conditions shown in Table 313 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 321 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by further using NO gas, B₂H₆/H₂ gas, Mg(C₅H₅)₂/He gas in the lower layer, and replacing H₂ gas with not illustrated He gas in the upper layer in Example 292, under the preparation conditions shown in Table 314 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 322 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by using SiF₄ gas, CH₄ gas, B₂H₆/H₂ gas, NO gas, AlCl₃/He gas, Cu(C₄H₇N₂O₂)₂/He gas in the entire layer, and using PH₃/H₂ gas in the upper layer, under the preparation conditions shown in Table 315 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 323 A light receiving member for use in electrophotography was prepared in the same manner as in Example 322, under the preparation conditions shown in Table 316 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 322. Example 324 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by further using C₂H₂ gas, under the preparation conditions shown in Table 317 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 325 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by replacing C₄ gas cylinder with C₂H₂ 2 gas cylinder, B₂H₆/H₂ gas cylinder with PH₃/H₂ gas cylinder in Example 292, under the preparation conditions shown in Table 318 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 326 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292 by further using H₂ S gas (99.999 % purity) from a not illustrated cylinder, under the preparation conditions shown in Table 319 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 327 A light receiving member for use in electrophotography was prepared in the same manner as in Example 322 by further using C₂H₂ gas from a not illustrated cylinder, under the preparation conditions shown in Table 320 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 322. Example 328 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 321 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 329 A light receiving member for use in electrophotography was prepared in the same manner as in Example 322 by further using Mg(C₅H₅)₂/He gas from a not illustrated sealed vessel, under the preparation conditions shown in Table 322 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 322. Example 330 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 324 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327 Example 331 A light receiving member for use in electrophotography was prepared in the same manner as in Example 329, under the preparation conditions shown in Table 324 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 329. Example 332 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 325 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 333 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 326 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 334 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 327 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 335 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 328 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 336 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327 by further using H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 329 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 236. Example 337 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 330 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 338 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327 by further using H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 327 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 339 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 332 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 340 A light receiving member for use in electrophotography was prepared in the same manner as in Example 329, under the preparation conditions shown in Table 333 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 329. Example 341 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327 by further using NH₃ tas and H₂S gas from a not illustrated cylinder, under the preparation conditions shown in Table 327 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 342 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 335 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 343 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 336 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 344 A light receiving member for use in electrophotography was prepared in the same manner as in Example 329, under the preparation conditions shown in Table 337 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 329. Example 345 A light receiving member for use in electrophotography was prepared in the same manner as in Example 329 by further using Mg(C₅H₅)₂/He gas, under the preparation conditions shown in Table 338 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 329. Example 346 A light receiving member for use in electrophotography was prepared in the same manner as in Example 327, under the preparation conditions shown in Table 339 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 327. Example 347 A light receiving member for use in electrophotography was prepared in the same manner as in Example 292, under the preparation conditions shown in Table 340 and, when evaluated in the same manner, satisfactory improvement was obtained to the dots, coarse image and peeling in the same manner as in Example 292. Example 348 The lower layer was formed under the preparation conditions shown in Table 341 in the same manner as in Example 292 except for using a target composed of Si, Al, Cu instead of Si, Al, Mg upon forming the lower layer in Example 291. Then, a light receiving member for use in electrophotography was prepared in the same manner as in Example 292 under the preparing conditions shown in aTable 341 by using the device shown in Fig. 37 for forming the upper layer. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 292. When the lower layer of the light receiving member for use in electrophotography of Example 348 was analyzed by using SIMS, it was found that the content of silicon atoms, hydrogen atoms and aluminum atoms in the direction of the film thickness was varied as desired. Example 349 A light receiving member for use in electrophotography was prepared in the same manner as in Example 1 under the preparation conditions shown in Table 225 by further using NaNH₂/He gas upon forming the lower oayer in Example 1. Comparative Example 8 A light receiving member for use in electrophotography was prepared under the same conditions in Example 349 except for not using H₂ gas upon forming the lower layer. The orifice for the content of atoms across the layer thickness near the lower layer of the light receiving member for use in electrophotography in Example 349 and Comparative Example 8 thus prepared was analyzed by using SIMS (secondary ion mass analyzing device, manufactured by Kameka : IMS-3F). The results are shown in Figure 43(a), (b) . In Fig. 43, the abscissa represents the measured time corresponding to the position across the layer thickness, and the ordinate represents the content for each of the atoms by relative values. Fig. 4(a) shows the profile for the content of atoms across the layer thickness in Example 349 in which aluminum atoms were distributed more on the side of the support, while silicon atoms, hydrogen atoms are distributed more on the side of the upper layer. Fig. 4(b) shows the profile for the content of atoms across the layer thickness in Comparative Example 8 in which aluminum atoms are distributed more on the side of the support, silicon atoms were distributed more on the side of the upper layer and hydrogen atoms were distributed uniformly. Then, the light receiving members for use photography thus prepared in Example 349 and Comparative Example 8 were set respectively to electrophotographic apparatus, that is, a copying machine NP-7550 manufactured by Cannon Inc. and modified for experimental use and several electrophotographic properties were checked under various conditions. The light receiving member for use in electrophotography was rotated for 1000 turns while using a magnet roller as a cleaning roller, coating positive toners on the magnet roller while keeping all of the charging devices not operated. Then, a black original was prepared by an ordinary electrophotographic process and as a result of measuring the number of dots generated, it was found that the light receiving member for use in electrophotography of Example 349 showed the number of dots less than 1/3 for that of the light receiving member for use in electrophotography in Comparative Example 8. In addition, the light receiving member for use in electrophotography was rotated by 20 turns in a state where coagulated paper dusts were placed on the grits of a separation charger to cause abnormal discharge. Then, after removing the paper dusts, images were prepared by using a black original and, as a result of measuring the number of dots, it was found that the number of dots in the light receiving member for use in electrophotography of Example 349 was less than 2/3 for that of the light receiving member for use in electrophotography in Comparative Example 8. Further, a roll made of high density polyethylene having about 32 mm⊘ diameter and 5 mm thickness was urged to the light receiving member for use in electrophotography under the pressure of 2 kg and then the light receiving member for use in electrophotography was rotated for 500,000 turns. Then, as a result of comparing the number of peeling visually in the light receiving layer, it was found that the number of peeling for the light receiving member for use in Example 349 was less than 1/2 for that of the light receiving member for use in electrophotography in Comparative Example 8. As has been described above, the light receiving member for use in electrophotography in Example 349 was superior from overall point of view to the light receiving member for use in electrophotography in Comparative Example 8. Example 350 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 342 except for changing the gas flow rate of Al(CH₃)₃/He to the value shown in Table 343. Comparative Example 9 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 342 except for changing the gas flow rate of Al(CH₃)₃/He to the value shown in Table 343. A roll made of high density polyethylene was urged to the light receiving members for use in electrophotography thus prepared in Example 350 and Comparative Example 9 in the same manner as in Example 349 and the number of layer peeling was compared. The result is shown in Table 343 assuming the number of layer peeling to 1 in the layer of the light receiving member for use in electrophotography of Example 349. Further, the content of aluminum atoms near the upper portion of the lower layer was analyzed by using SIMS. The result is shown in Table 343. As shown by the result in Table 343, the number of layer peeling was low and satisfactory result was obtained in the region where the content of the aluminum atoms near the upper portion of the lower layer is greater than 20 atom%. Example 351 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 342 except for changing the temperature for the support at a constant rate from 350°C to 250°C and using Y(Oi-C₃H₇)₃ instead of NaNH₂ during formation of the lower layer. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 349. Example 352 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 342 except for changing RF power at a constant rate from 50 mW/cm³ to 5 mW/cm³ and using Mn(CH₃)(CO)₅ instead of NaNH₂ during formation of the lower layer. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 349. Example 353 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 344 except for using Zn(C₂H₅)₂ instead of NaNH₂ and, further, adding the raw material gas shown in Table 342. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 349. Example 354 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 342 except for changing the outer diameter of the cylinderical aluminum support to 30 mm and changing the gas flow rate and RF power shown in Table 342 to 1/3 respectively. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 349. Example 355 A light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in Table 345. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 349. Example 356 A light receiving member for use in electrophotography was prepared by the microwave glow discharge decomposition in the same manner as in Example 23 under the preparing conditions shown in Table 346 by further using SiF₄ gas and NaNH₂/He gas upon forming the lower layer in Example 23. When the same evaluation as in Example 349 was conducted for the light receiving member for use in electrophotography, satisfactory improvement was obtained to dots and layer peeling in the same manner as in Example 349. The profile for the content of atoms across the layer thickness near the lower layer was analyzed by using SIMS in the same manner as in Example 349 and the result is shown in Fig. 43(c). It was found that aluminum atoms, silicon atoms and hydrogen atoms are distributed in the same manner as in Example 349. Example 357 The lower layer was formed under the preparing conditions shown in Table 347 in the same manner as in Example 291 except for using a target composed of Si, Al, Mn instead of a target composed of Si, Al, Mg upon forming the lower layer in Example 291. Then, a light receiving member for use in electrophotography was prepared in the same manner as in Example 349 under the preparing conditions shown in 342 by using the device shown in Fig. 37 for forming the upper layer. When the evaluation was conducted in the same manner, satisfactory improvement to dots and layer peeling was obtained in the same manner as in Example 349. The profile for the content of atoms across the layer thickness near the lower layer was analyzed by using SIMS in the manner as in Example 349 and the results is shown in Fig. 43(d). It was found that aluminum atoms, silicon atoms and hydrogen atoms were distributed in the same manner as in Example 349. In the following Tables 1 to 346, the mark "*" means increase of a flow rate at constant proportion; the mark "**" means decrease of a flow rate at constant proportion; the term "S-side" means substrate side; the term "UL-side" means upper layer side; the term "LL-side" means lower layer side; the term "U.1st LR-side" means 1st layer region side of the upper layer; the term "U.2nd LR-side" means 2nd layer region side of the upper layer; the term "U.3rd LR-side" means 3rd layer region side of the upper layer; the term "U.4th LR-side" means 4th layer region side of the upper layer; and the term "FS-side" means free surface side of the upper layer.

Claims: A light receiving member for electrophotography comprising an aluminum support and a multilayered light receiving layer exhibiting photoconductivity formed on said aluminum support; wherein said multilayered light receiving layer comprises a lower layer in contact with said aluminum support and an upper layer disposed on said lower layer; said lower layer comprising an inorganic material containing at least aluminum atoms, silicon atoms and hydrogen atoms; said lower layer having a portion in which said aluminum, silicon and hydrogen atoms are unevenly distributed across the layer thickness; said aluminum atoms being contained in said lower layer in an amount of 5 atomic % to 95 atomic % such that their content decreases across the layer thickness upward from the interface between said lower layer and said aluminum support, and wherein said content of said aluminum atoms is lower than 95 atomic % in the vicinity of the interface between said lower layer and said aluminum support and is higher than 5 atomic % in the vicinity of the interface between said lower layer and said upper layer; and said upper layer comprising a plurality of layer regions parallel to said interface each comprising a non-single crystal material composed of silicon atoms as the matrix and at least one kind of atoms selected from hydrogen atoms and halogen atoms, and wherein the layer region adjacent to said lower layer comprises at least one kind of atoms selected from carbon atoms, nitrogen atoms and oxygen atoms. A light receiving member according to claim 1, wherein the lower layer further contains atoms of an element capable of contributing to the control of image quality. A light receiving member according to claim 2, wherein the image quality controlling element is selected from the group III elements of the periodic table except for aluminum. A light receiving member according to claim 2, wherein the image quality controlling element is selected from the group V elements of the periodic table except for nitrogen. A light receiving member according to claim 2, wherein the image quality controlling element is selected from the group VI elements of the periodic table except for oxygen. A light receiving member according to any one of claims 1 to 5, wherein the lower layer further contains atoms of an element capable of contributing to the control of durability. A light receiving member according to claim 6, wherein the durability controlling element is selected from carbon, nitrogen and oxygen. A light receiving member according to any one of claims 1 to 7, wherein the lower layer further contains halogen atoms. A light receiving member according to any one of claims 1 to 8, wherein the lower layer further contains at least one kind of atoms selected from germanium atoms and tin atoms. A light receiving member according to any one of claims 1 to 9, wherein the lower layer further contains at least one kind of atoms selected from alkali metal atoms, alkaline earth metal atoms and transition metal atoms. A light receiving member according to claim 10, wherein the alkaline earth metal is magnesium. A light receiving member according to claim 10, wherein the transition metal is copper. An electrophotographic process comprising: (a) applying an electric field to a light receiving member according to any preceding claim; and (b) applying electromagnetic waves to said light receiving member so as to form an electrostatic image.

Inventors: AOIKE TATSUYUKI CANON DAI-ICHI, KARIYA TOSHIMITSU CANON DAI-IC, NIINO HIROAKI CANON DAI-ICHI N, SANO MASAFUMI CANON DAI-ICHI N, YOSHINO TAKEHITO CANON DAI-ICH, AOIKE, TATSUYUKI CANON DAI-ICHI NAGAHAMA-RYO, KARIYA, TOSHIMITSU CANON DAI-ICHI NAGAHAMA-RYO, NIINO, HIROAKI CANON DAI-ICHI NAGAHAMA-RYO, SANO, MASAFUMI CANON DAI-ICHI NAGAHAMA-RYO, YOSHINO, TAKEHITO CANON DAI-ICHI NAGAHAMA-RYO
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1988
Main classification: G03G5
IPC codes: G03G5