HYDROLYZED MEMBRANE AND PROCESS FOR ITS PRODUCTION

Abstract: A hydrolyzed membrane capable of selectively permeat­ ing water, which contains as a major component a material capable of producing carboxyl groups by hydrolysis, with part of said material having carboxyl groups formed by hydrolysis, and which may be coated with a hydrophilic polymer. The membrane may be widely used as a membrane capable of se­ lectively permeating water, such as a reverse osmosis mem­ brane or a membrane for dehumidifying air as well as a mem­ brane for selective permeation of water according to pervapor­ ation or vapor permeation. ABSTRACT A selectively water-permeable hydrolyzed membrane characterized in that it is mainly made of a material which can generate a carboxyl group by hydrolysis and that a part of the material is hydrolyzed to have carboxyl groups, which may be further coated with a hydrophilic polymer. The above membrane is useful as a selectively water-permeable membrane and is widely appliable not only to pervaporation and vapor permeation, but also to reverse osmosis, dehumidification of air and so on.

Description: The present invention relates to a selectively water-permeable membrane which is not only useful in pervaporation or vapor permeation, but also appliable to a wide field including reverse osmosis and dehumidification of air. The membrane may have any form arbitrarily selected depending upon the use. For example, it may be a flat membrane, a hollow yarn or fiber membrane or a tubular membrane. Reverse osmosis methods have been put to practical use as methods of concentrating a low-concentration aqueous solution of an organic substance with a memberane. However, these reverse osmosis methods necessitate the application of a pressure higher than the osmotic pressure of a separation solution to a separative membrane, so that the methods cannot be applied to a high-concentration aqueous solution owing to its high osmotic pressure. Thus, the solution separable by the reverse osmosis methods is limited in concentration. Meanwhile, pervaporation and vapor permeation have been noted as a new separating method free from influence of osmotic pressure. Pervaporation is a method characterized in that a substance to be separated is made to permeate a membrane in a gaseous state by feeding a separation solution to the primary side of the membrane, while reducing the pressure of the secondary side thereof or passing a carrier gas through the secondary side. On the other hand, vapor permeation is different from the pervaporation in that a vapor mixture is fed to the primary side. The membrane-permeating substance can be recovered by condensing the permeating vapor under cooling. With respect to pervaporation, many studies have been made. For example, US-A-3,750,735 and US-A-4,067,805 disclose the separation of an organic substance from water with a polymer having an active anionic group, while US-A-2,953,502 and US-A-3,035,060 disclose the separation of ethanol from water with a cellulose acetate or polyvinyl alcohol membrane. Further, JP-A-109,204/1984 discloses a cellulose acetate membrane and a polyvinyl alcohol membrane, while JP-A-55,305/1984 discloses a crosslinked polyethyleneimine membrane. However, these membranes disclosed in the references are too poor in separation performance, particularly in permeation rate, to be put to practical use. Meanwhile, JP-A-129,104/1985 discloses a membrane prepared from an anionic polysaccharide or a polysaccharide derivative as a membrane excellent in separation performance. However, this membrane has inherent unavoidable problems resulting from the nature of a natural high-molecular weight compound, for example, depolymerization with acid or alkali or decomposition with bacteria, so that the endurance and chemical resistance of the membrane fall short of expectations. Generally, a hydrophobic separative membrane has disadvantages in that the surface thereof is hardly wettable and readily dries and that it tends to cause adsorption or clogging frequently. Therefore, for the purpose of overcoming these disadvantages, it has been attempted to impart a hydrophilic nature to such a membrane by various methods. For example, a method of adding a polyhydric alcohol such as polyethylene glycol or glycerin to a hydrophobic separative membrane has been generally adopted. However, the membrane thus improved in hydrophilic nature is disadvantageous in that the additives contained in the membrane are dissolved out into a filtrate in service. Further, JP- -16187/1981 discloses a method which comprises applying a water-soluble polymer to a hydrophobic separative membrane by dipping and insolubilizing the applied water-soluble polymer by irradiation with electron beams, crystallization through heating or chemical reaction with formaldehyde or glyoxal to thereby impart a hydrophilic nature to the membrane. However, this method is disadvantageous in that it necessitates complicated operation so that it is unsuitable for practical use and that defects are often generated. Furthermore, JP-A-35862/1983 discloses a method for imparting a hydrophilic nature to a hydrophobic porous filter membrane which comprises etching a polysulfone filter membrane in an atmosphere of vacuum electric discharge by sputtering. However, this method is disadvantageous in that the resulting porous filter membrane exhibits remarkably lowered mechanical strengths. It is therefore the object of the present invention to prepare a separative membrane having selective permeability to water which exhibits sufficient endurance and excellent permeation rate and separation factor by hydrolysis, which is a simple chemical treatment, without the formation or a thin film such as coating. According to the present invention this object is attained with a selectively water-permeable membrane obtainable by partially hydrolyzing a polyacrylonitrile based membrane thereby forming an anionic polymer having carboxylic groups and reacting said anionic polymer with a cationic polymer to obtain a polyion complex. The present invention further relates to a process for producing a selectively water-permeable membrane comprising hydrolyzing a polyacrylonitrile based membrane to form an anionic polymer having carboxylic groups and reacting said anionic polymer with a cationic polymer to obtain a polyion complex. The term "permeation rate" used in this specification refers to the amount of a mixture permeating a membrane per unit area of the membrane and unit time and is shown by kg/m²·h, while the term "separation factor (α)" refers to the ratio of the ratio of water to organic substance with respect to a permeation gas to that with respect to a feed solution or vapor, i.e., In this equation, X and Y are the contents of water and organic substance in the two systems respectively, and p and f stand for "permeation" and "feed", respectively. The membrane material may be as a blend or copolymer thereof with other material. Further, it is a matter of course that the use of the membrane material in a crosslinked state is preferable from the standpoint of the form retention of a membrane. Particular examples of the material include polyacrylonitril and a polymer of the acidester type and the acidamide type. Hydrolysis of the membrane formed from such a material can be representatively carried out by dipping the membrane in an acid or alkaline solution. Particularly, a dipping process using a solution of an alkali such as potassium hydroxide, sodium hydroxide or barium hydroxide is preferable from the standpoint of the balance between the hydrolysis rate and the form retention. Although the degree of hydrolysis varies depending upon the kind of the material or the state thereof (i.e., blend, copolymer, crosslinked or uncrosslinked), it can be suitably adjusted by selecting the kind of the acid or alkali to be used, concentration or treatment time. The complete hydrolysis of the material is unfavorable, because it tends to convert the material into a water-soluble gel in many cases, though there is difference depending upon the kind of the material used. On the contrary, when the degree of hydrolysis is too low, the separating function of the resulting membrane will be unfavorably low. Alternatively, it is possible to bring only the surface of the membrane into contact with a treatment solution to thereby carry out the hydrolysis. The reaction route of hydrolysis of polyacrylonitrile with an alkaline solution is presumably as follows: Accordingly, the hyrolysis treatment may be arbitrarily discontinued during the turning of the color of a membrane from brown into transparence. A suitably hydrolyzed membrane as prepared above contains carboxyl groups of free acid form or various metal or amine salt forms depending upon the treatment solution used and can be used even as such as a selectively water-permeable membrane. However, it is in accordance with the present invention, in order to enhance the performance of the membrane and the stability thereof the membrane is reacted with a cationic polymer to form a polyion complex. Particular examples of the cationic polymer include polyethyleneimine, polyallylamine, polyvinylpyridine and ionene polymers containing quarternary ammonium salt groups in their main chain. Further the formation of a polyion complex can be easily attained only by dipping a hydrolyzed membrane as described above in a solution of a cationic polymer. Furthermore, a hydrolyzed membrane as prepared above is easily improved further in performance by applying a hydrophilic polymer to the surface thereof by coating. Hence, in accordance with the present invention a composite membrane can be prepared by applying a hydrophilic synthetic polymer to the partially hydrolyzed polyacrylonitrile based membrane to thereby enhance the hydrophilicity of the base membrane. Representative examples of the hydrophilic synthetic polymer include polyacrylic acid and polyvinyl alcohol. When the coating solution is an anionic polymer such as polyacrylic acid, the performance of the membrane or the safety are enhanced when the anionic polymer is reacted with the cationic polymer to form a polyion complex. In this case he formation of the polyion complex is easily attained merely by dipping the hydrolyzed membrane coated with anionic polymer in a solution of the cationic polymer. When a base membrane having an anionic group such as a carboxyl group is used, it is apparent that the cationic polymer can be easily applied to such a base membrane prior to the application of the anionic polymer owing to the interaction between the ions. According to the present invention, an excellent separative membrane having selective permeability to water can be obtained by dipping a commercially available reverse osmosis membrane, ultrafiltration membrane of a ultra-micro filtration membrane as such in an aqueous solution of an acid or an alkali for a specified time to thereby hydrolyze the membrane, without employing any coating step which necessitates advanced technique. Further, the membrane thus prepared can be easily coated with a hydrophilic polymer by virtue of the improved compatibility of the surface of the membrane with a hydrophilic polymer. According to the present invention, a lot of materials can be treated at once with conventional equipment, which is very advantageous in production cost. The selectively water-permeable hydrolyzed membrane according to the present invention exhibits particularly excellent selective permeability for water in pervaporation and can be used not only in the dehydration of various solutions containing organic substances but also in a wide range of uses including vapor permeation, dialysis, reverse osmosis and dehumidification of air by utilizing its characteristics. Fig. 1 is a graph showing the relationship between the membrane performance and the alkali concentration or dipping time in the treatment at 80°C. Fig. 2 is a graph showing the relationship between the membrane performance and the temperature of alkali solution or dipping time in the treatment with 1N-NaOH. The present invention will now be described in more detail by referring to the following Examples. Example 1 A commercially available reverse osmosis membrane made of polyacrylonitrile was dipped in a 1N aqueous solution of NaOH at 80°C for 13 min to carry out the hydrolysis of the membrane. The excessive alkali was rinsed out of the membrane with water. The resulting membrane was dipped in an aqueous solution of a polycation of an ionene type PCA-107 having a structure which will be described below overnight to form a polyion complex. The resulting membrane was examined for selective permeability to water by pervaporation (feed solution: 95 weight-% aqueous ethanol, 70°C) The permeation rate was 0.81kg/m²·h and the separation factor was 850. Comparative Example 1 The reverse osmosis membrane of Example 1 was examined as such (without being hydrolized) for selective permeability to water under the same conditions as those of Example 1. The permeation rate was 4.0kg/m²·h and the separation factor was 2.8. Although the membrane exhibited a high permeation rate, it hardly exhibited selective permeability to water. Comparative Example 2 The reverse osmosis membrane of Example 1 was dipped in a 1N aqueous solution of NaOH at 80°C for 60 min to carry out the hydrolysis. The polyacrylonitrile of the membrane was excessively hydrolyzed into polysodium acrylate, so that the membrane gelled to lose its form. Example 2 A dope prepared by dissolving commercially available polyacrylonitrile in N,N-dimethylformamide at a weight ratio of 1:9 was cast on a polyester woven textile in a casting thickness of 250µm and immediately dipped in water to carry out the solidification. Thus, a flat membrane of polyacrylonitrile was obtained. This membrane was dipped in a 1N aqueous solution of NaOH at 80°C for 24 min to carry out the hydrolysis. The excessive alkali was rinsed out of the hydrolyzed membrane with water. The resulting membrane was dipped in an aqueous solution of a polycation of an ionene type, PCA-107, overnight to form a polyion complex. The membrane was examined for selective permeability to water under the same conditions as those of Example 1. The permeation rate was 0.94kg/m²·h and the separation factor was 1480. Comparative Example 3 The flat polyacrylonitrile membrane prepared in Example 2 was examined as such (without being hydrolyzed) for selective permeability to water. The membrane hardly exhibited any separating function for a water/ethanol mixture. Example 3 A commercially available flat polyacrylonitrile ultrafiltration membrane (polyacrylonitrile content: about 70%) was dipped in a 1N aqueous solution of NaOH at 78 to 85°C for 30 min to carry out the hydrolysis. The excessive alkali was rinsed out of the hydrolyzed membrane with water. The hydrolyzed membrane was dipped in an aqueous solution of a polycation of an ionene type, PCA-107, overnight to form a polyion complex. The resulting membrane was examined for selective permeability to water under the same conditions as those of Example 1. The permeation rate was 1.0kg/m².h and the separation factor was 540. Comparative Example 4 The flat membrane as used in Example 3 was examined as such (without being hydrolyzed) for selective permeability to water under the same conditions as those of Example 1. The membrane hardly exhibited any separating function or a water/ethanol mixture. Comparative Example 5 The flat membrane as used in Example 3 was dipped in a 1N aqueous solution of NaOH at 78 to 85°C for 60 min to carry out the hydrolysis. The polyacrylonitrile membrane was excessively hydrolyzed into polysodium acrylate, so that the membrane gelled to lose its form. Example 4 A flat membrane as used in Example 3 was dipped in a 0.1N aqueous solution of Ba(OH)₂ at 78 to 85°C for 150 min to carry out the hydrolysis. The excessive alkali was rinsed out of the hydrolyzed membrane with water. The resulting membrane was dipped in an aqueous solution of a polycation of an ionene type, PCA-107, overnight to form a polyion complex. The resulting membrane was examined for selective permeability of water under the same conditions as those of Example 1. The permeation rate was 0.7kg/m²·h and the separation factor was 190. Example 5 Five minimodules having a surface area of about 70cm² were produced by the use of a hollow yarn (inside diameter/outside diameter=1.0/1.5mm) made of a polyacrylonitrile-base polymer (content: about 90%). 1N-NaOH was passed through the inside of the yarn of the module at 80°C for 15 min to hydrolyze the inside surface of the yarn slightly. Then, a 0.5% aqueous solution of a polyacrylic acid having a molecular weight of 4,000,000 was passed through the inside of the yarn for 10 s, followed by drying with hot air at 50°C. A 2% aqueous solution of a polycation of an ionen type, PCA-107, was passed through the inside of the resulting yarn to form a polyion complex, followed by air drying. In order to prevent the generation of defective areas, the above procedure from the application of polyacrylic acid to the formation of a polyion complex was repeated twice. The resulting module was examined for selective permeability to water (evaluation solution: 95% by weight ethanol, 60°C) by pervaporation. Each of the five modules exhibited a high separation factor exceeding 800. In such an evaluation method, the smaller the defective area such as unevenly coated area, the higher the separation factor. Accordingly, the membrane is estimated to be nearly uniformly coated. Comparative Example 6 The same procedure as that described in Example 5 was repeated except that the polyacrylonitrile hollow yarn was used as such as a base membrane without being hydrolyzed. Three of the five resulting modules each exhibited a separation factor exceeding 800. Example 6 In a similar manner to that described in Example 5, a polyacrylonitrile hollow yarn was hydrolyzed and converted into a polyion complex by passing a 2% aqueous solution of a polycation of an ionen type, PCA-107, therethrough except that the hollow yarn was not coated with polyacrylic acid. The resulting membrane was examined for performance in a similar manner to that of Example 1. The separation factor was about 3 and the permeation rate was 10kg/m²·h or above. Comparative Example 7 The same procedure as that described in Example 6 was repeated except that the yarn was not hydrolyzed. The resulting membrane was examined for performance in a similar manner to that of Example 5. It exhibited a separation factor of about 1 and no selective permeability of water. Example 7 A hollow yarn having an inside diameter of 1mm and an outside diameter of 1.5mm was produced by the use of a polyacrylonitrile-base polymer (polyacrylonitrile/vinyl acetate=9/1) by dry-wet spinning. This yarn had pores having a size of 0.3µm on the outside surface and those having a size of several tens of nm (hundreds of Å) on the inside surface. The hollow fiber exhibited a permeation rate of pure water of about 8ℓ/min·m² 10⁵ Pa · (atm) and a rejection rate for bovine serum albumin of about 10%. The membrane was dipped in a 1N aqueous solution of NaOH to hydrolyze a part of the membrane. The excessive alkali was rinsed out of the membrane with water. The resulting membrane was dipped in an aqueous solution of a polycation of an ionene type, PCA-107, overnight to form a polyion complex. The hydrolysis of the membrane was carried out at a constant dipping temperature, while varying the concentration of the NaOH solution and dipping time. The resulting membrane was examined for selective permeability of water by pervaporation (feeding a 95% by weight aqueous ethanol of 60°C into the inside of the membrane, while evacuating the outside thereof). The results are shown in Fig. 1. Separately, the hydrolysis was carried out with an aqueous solution of NaOH having a constant concentration, while varying the dipping temperature and dipping time. The resulting membrane was examined for selective permeability of water. The results are shown in Fig. 2. As shown in these figures, the permeation rate lowered with the lapse of the dipping time while the separation factor temporarily increased to reach a peak and then lowered independent of the concentration of the aqueous solution of NaOH or the dipping temperature. The lower the concentration or temperature of the alkali solution, the longer the time which elapsed until the separation factor reached a peak and the more moderate the change in the separation factor or the permeation rate, i.e., the easier the control of the performance of a membrane. Further, among the hollow yarns shown in the figures, the best-performance one exhibited a permeation rate of 0.6 to 0.7kg/m²·h and a separation factor of 2,000 to 3,000.

Claims: A selectively water-permeable membrane obtainable by partially hydrolyzing a polyacrylonitrile based membrane thereby forming an anionic polymer having carboxylic groups and reacting said anionic polymer with a cationic polymer to obtain a polyion complex. The membrane of claim 1 wherein the cationic polymer is selected from the group consisting of polyethyleneimine, polyallylamine, polyvinylpyridine and an ionene polymer containing quaternary ammonium groups in its main chain. The membrane of claim 1 further comprising a hydrophilic polymer. The membrane of claim 3 wherein the hydrophilic polymer is poylacrylic acid or polyvinyl alcohol. A process for producing a selectively water-permeable membrane comprising hydrolyzing a polyacrylonitrile based membrane to form an anionic polymer having carboxylic groups and reacting said anionic polymer with a cationic polymer to obtain a polyion complex. The process according to claim 5 further comprising applying a hydrophilic polymer on said membrane. The process of claim 5 or 6 wherein hydrolysis is conducted by dipping said polyacrylonitrile based membrane in an alkaline solution. Use of a membrane of any of claims 1 to 4 for pervaporation or vapor permeation.

Inventors: KARAKANE HIROKI, MAEDA YASUSHI, TSUYUMOTO MICHIO, KARAKANE, HIROKI, MAEDA, YASUSHI, TSUYUMOTO, MICHIO
Applicants: JAPAN REPRESENTED BY MINISTRY, JAPAN REPRESENTED BY MINISTRY OF INTERNATIONAL TRADE AND INDUSTRY DIRECTOR-GENERAL, BASIC INDUSTRIES BUREAU
Application year: 1988
Main classification: B01D61
IPC codes: B01D69, B01D67, B01D71