MOLDABLE THERMOPLASTIC POLYAMIDE COMPOSITION

Abstract: A composition is prepared by melt-kneading (A) 60-97 parts by wt of a polyamide (e.g. aliphatic polyamide 6, 6.6 or 12) and (B) 3-40 parts of an ethylene copolymer of (a) 40-90% by wt of an ethylene unit, (b) 5-60% by wt of an alkyl α,β-unsaturated C3-8 carboxylate unit (e.g. methyl methacrylate), and optionally other copolymerizable monomers; and 0.3-10% of maleic anhydride unit, the copolymer having a melt index of 1-100 g/10 mm; and then melt-kneading the composition with (c) 0-01-20 parts of a polyfunctional compound having at least 2 functional groups reactive to carboxyl, carboxylic acid anhydride or amino (e.g. amino, epoxy, dihydxyazolyl, carboxyl, carboxylic acid anhydride and hydroxyl), e.g. an aliphatic diamine or a polyamine; this effects partial crosslinking. Melt kneading can be performed in an extruder. The resultant resin composition can also contain other additives or reinforcements, and can be molded to make articles having good physical properties and appearance.

Description: This invention relates to a crosslinked thermoplastic resin composition which can be molded by injection, extrusion or the like molding method into sheets, films, etc. More particularly, it relates to a crosslinked thermoplastic resin composition comprising a polyamide resin, an ethylene copolymer containing an acid anhydride group, and a crosslinkable polyfunctional compound, which exhibits various physical properties in good balance, satisfactory appearance, and high softness. Polyamide resins are widely employed as engineering plastics because of their excellent properties in, for example, rigidity, abrasion resistance, chemical resistance, heat resistance, and electrical characteristics. However, they have disadvantages or room for improvement in impact resistance, molding stability, and the like, as having given rise to a bar to development of practical application. Various proposals have been made in an attempt of improving impact resistance of polyamide resins. One such proposal is addition of a modified ethylene copolymer containing an active group reactive to polyamide resins and having rubbery elasticity, as described in Japanese Patent Publications Nos. 4743/79 and 44108/80 and Japanese Patent Application (OPI) No. 23850/83 (the term "OPI" as used herein means an "unexamined published Japanese patent application"). The present inventors have proved that the above-described method achieves improvement of impact resistance relatively but still insufficiently and that the resulting molded articles are also unsatisfactory in a physical property balance among heat resistance, rigidity, and impact resistance. That is, it was found that the somewhat improved impact resistance and softness are cancelled out by other mechanical properties, such as rigidity, tensile strength, hardness and heat resistance, that are considerably poorer than those of the polyamide resin per se . Besides, the use of the resulting molded articles is often restricted due to their poor appearance, for example, coloring. Hence, it is important that a polymer to be compounded into polyamide resins should be selected from those of a modified ethylene copolymer type which would not involve these problems, and development of such a polymer has for long been demanded. One object of this invention is to provide a crosslinked thermoplastic resin composition mainly comprising a polyamide resin, which is excellent in impact resistance as well as mechanical properties, such as heat resistance and rigidity. As a result of extensive investigations on a resin composition effective for modification of a polyamide resin, we have now found that a composition having good balance among impact resistance, heat resistance and rigidity, excellent moldability and satisfactory appearance can be obtained by compounding an ethylene copolymer having a specific structure and a crosslinkable polyfunctional compound. The present invention relates to a thermoplastic resin composition obtained by melt-kneading (A) from more than 60 to 97 parts by weight of a polyamide resin and (B) from 3 to less than 40 parts by weight of an ethylene copolymer having a melt index of from 1 to 100 g/10 min. and comprising (a) from 40 to 90% by weight of an ethylene unit, (b) at least 5% by weight of an alkyl α,β-unsaturated carboxylate unit, and (c) from 0.3 to 10% by weight of a maleic anhydride unit, and then melt-kneading the resulting composition with (C) from 0.01 to 20 parts by weight, based on 100 parts by weight of components (A) and (B), of a polyfunctional compound having, per molecule, at least two functional groups selected from amino, epoxy, dihydroxazolyl, carboxyl, carboxylic acid anhydride and hydroxyl groups, so as to effect a partial crosslinking reaction. The polyamide resin which can be used as component (A) includes various kinds of polyamide obtained by ring-opening polymerization of a lactam having a ring with three or more members, polymerization of a polymerizable ω-amino acid, or polycondensation of a dibasic acid and a diamine, such as polymers of ε-caprolactam, aminocaproic acid, enantholactam, 7-aminoheptanoic acid, 11-aminoundecanoic acid, etc.; polymers obtained by polycondensation between a diamine, e.g., butanediamine, hexamethylenediamine, nonamethylenediamine, undecamethylenediamine, dodecamethylenediamine or m-xylenediamine, and a dicarboxylic acid, e.g., terephthalic acid, isophthalic acid, adipic acid, sebacic acid, dodecanedicarboxylic acid or glutaric acid; and copolymers of these monomer compounds. Specific examples of these polyamide resins are aliphatic polyamide resins, e.g., polyamide 4.6, polyamide 6, polyamide 6.6, polyamide 6.10, polyamide 11, polyamide 12 and polyamide 6.12; and aromatic polyamide resins, e.g., polyhexamethylenediamine terephthalamide, polyhexamethylene isophthalamide and an xylene-containing polyamide. Preferred of these are polyamide 6, polyamide 6.6, and polyamide 12. In addition, various copolymer nylon resins having melting points of from 80 to 200°C which are commercially available for use as hot-melt adhesives can also be utilized either individually or in combination with a polyamide resin having a melting point of 200°C or more. The ethylene copolymer as component (B) comprises (a) from 40 to 90% by weight, preferably from 65 to 90% by weight, of an ethylene unit, (b) at least 5% by weight, preferably from 10 to 35% by weight, of an alkyl α,β-unsaturated carboxylate unit, and (c) from 0.3 to 10% by weight, preferably from 1 to 5% by weight, of a maleic anhydride unit. The alkyl α,β-unsaturated carboxylate as monomer unit (b) are alkyl esters of unsaturated carboxylic acids having from 3 to 8 carbon atoms, e.g., acrylic or methacrylic acid. Specific examples of the monomer unit (b) include methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, t-butyl acrylate, isobutyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate and isobutyl methacrylate, with methyl acrylate, ethyl acrylate, n-butyl acrylate and methyl methacrylate being preferred. In so far as the desired properties of the resin composition should be retained, the ethylene copolymer (B) may further comprise other copolymerizable monomers, such as vinyl acetate or vinyl propionate. In the ethylene copolymer (B), if the content of the ethylene unit (a) is less than 40% by weight, the resulting polyamide composition suffers from great reduction in rigidity, and an ethylene content exceeding 90% by weight results in insufficient impact resistance. If the content of the alkyl α,β-unsaturated carboxylate unit (b) is less than 5% by weight, satisfactory impact resistance cannot be obtained. If it exceeds 60% by weight, rigidity greatly decreases. Further, if the content of the maleic anhydride unit (c) is less than 0.3% by weight, sufficient impact resistance cannot be obtained, and if it exceeds 10% by weight, the resulting composition does not exhibit satisfactory moldability. The ethylene copolymer (B) must have a melt index (JIS K6760) ranging from 1 to 100 g/10 min and preferably from 2 to 50 g/10 min. A melt index exceeding 100 g/10 min results in unfavorable mechanical properties. An ethylene copolymer having a melt index less than 1 g/10 min shows insufficient compatibility with the polyamide. The polyfunctional compound (C) containing the specified at least two functional groups having reactivity to a carboxyl group, a carboxylic acid anhydride group or an amino group per molecule has a intramolecular crosslinking reactivity to the ethylene copolymer (B) or polyamide resin (A). These polyfunctional compounds (C) are not particularly limited in molecular weight and embrace high molecular weight compounds. Specific examples of the compounds having two or more amino groups in the molecule thereof include aliphatic diamines, e.g., 1,6-hexamethylenediamine, trimethylhexamethylenediamine, 1,4-diaminobutane, 1,3-diaminopropane, ethylenediamine and polyether diamines; aliphatic diamine carbamates, e.g., hexamethylenediamine carbamate and ethylenediamine carbamate; aliphatic polyamines, e.g., diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, ethylaminoethylamine, methylaminopropylamine, 2-hydroxyethylaminopropylamine, aminoethylethanolamine, 1,2-bis(3-aminopropoxy)-2,2-dimethylpropane, 1,3,6-trisaminomethylhexane, iminobispropylamine, methyliminobispropylamine and bis(hexamethylene)triamine; alicyclic polyamines, e.g., methanediamine, N-aminoethylpiperazine, 1,3-diaminocyclohexane, isophorondiamine bis(4-amino-3-methylcyclohexyl methane, aliphatic polyamines having an aromatic ring, e.g., m-xylylenediamine and tetrachloro-p-xylylenediamine, aromatic amines, e.g., m-phenylenediamine, diaminodiphenyl ether, 4,4′-methylenedianiline, diaminodiphenylsulfone, benzidine, 4,4′-bis(p-toluidine), 4,4′-thiodianiline, o-phenylenediamine, dianisidine, methylenebis(o-chloroaniline), 2,4-toluenediamine, bis- (3,4-diaminophenyl)sulfone, diaminoditolylsulfone, 4-chloro-o-phenylenediamine, 4-methoxy-6-methyl-m-phenylenediamine and m-aminobenzylamine; polyamines containing silicon, e.g., 1,3-bis(γ-aminopropyl)-1,1,3,3-tetramethyldisiloxane, amine-modified silicone oils; amino-terminated butadiene-acrylonitrile copolymers; tertiary amine compounds, e.g. N,N,N′,N′-tetramethylhexamethylenediamine and N,N,N′,N″,N″-pentamethyldiethylenetriamine, ethylene copolymers comprising an ethylene unit and an N,N-dialkylaminoalkyl α,β-unsaturated carboxylate unit, e.g., an ethylene-N,N-dimethylaminoethyl methacrylate copolymer, ethylene copolymers comprising an ethylene unit and an N,N-dialkylaminoalkyl α,β-unsaturated carboxylic acid amide unit, e.g., an ethylene-N,N-dimethylaminopropylacrylamide copolymer, dihydrazide compounds, e.g., succinic acid dihydrazide, adipic acid dihydrazide, isophthalic acid dihydrazide and eicosanedicarboxylic acid dihydrazide, diaminomaleonitrile and melamine. The compounds having two or more epoxy groups per molecule are largely divided into olefin copolymers and epoxy resins. Specific examples of the olefin copolymers are copolymers of an olefin and diglycidyl methacrylate and/or diglycidyl acrylate. The olefin includes ethylene, propylene, butene-1, isobutylene, pentene-1, hexene-1, heptene-1, octene-1 and dodecene-1, with ethylene being preferred. The olefin copolymer may further contain an alkyl α,β-unsaturated carboxylate unit or a vinyl carboxylate unit as a comonomer. Examples of such a comonomer are alkyl esters of acrylic acid or methacrylic acid, (e.g., methyl acrylate, ethyl acrylate, n-butyl acrylate and methyl methacrylate,), vinyl acetate and vinyl propionate. The olefin copolymers further embrace glycidyl methacrylate-modified ethylene-propylene rubber and ethylene-methyl acrylate-glycidyl methacrylate copolymer rubber. The olefin copolymers can be prepared by any of random copolymerization, block copolymerization, and graft copolymerization. The glycidyl methacrylate unit and/or glycidyl acrylate unit in the olefin copolymer should be in the range of from 5 to 50% by weight. Otherwise, the effects to improve physical properties would be insufficient. The epoxy resin includes bisphenol A type epoxy resins, bisphenol F type epoxy resins, novolak type epoxy resins, alicyclic epoxy resins, glycidyl ester resins, glycidylamine resins, hydantoin type epoxy resins, and triglycidyl isocyanurate. The compounds containing two or more dihydroxazolyl groups per molecule include 2,2′-(1,3-phenylene)-bis(2-oxazoline) and a styrene-vinyloxazoline copolymer. The compounds containing two or more of carboxyl, carboxylic acid anhydride, or hydroxyl groups include terephthalic acid, isophthalic acid, adipic acid, sebacic acid, dodecanedicarboxylic acid, an ethylene-acrylic acid copolymer, trimellitic acid anhydride, pyromellitic acid anhydride, ethylene glycol bis(anhydrotrimellitate), an isobutylene-maleic anhydride copolymer, a styrene-maleic anhydride copolymer, trimethylolpropane, pentaerythritol, and a saponification product of an ethylene-vinyl acetate copolymer. The thermoplastic resin composition according to the present invention comprises from more than 60 to 97 parts by weight, preferably from 70 to 90 parts by weight, of the polyamide resin (A), and from 3 to less than 40 parts by weight, preferably from 10 to 30 parts by weight, of the ethylene copolymer (B). If the polyamide resin content is less than 60 parts by weight, rigidity and heat resistance of the resulting composition become insufficient, and if it exceeds 97 parts by weight, the composition has insufficient impact resistance. The amount of the polyfunctional compound (C) to be compounded should be determined depending on the reactivity of the functional groups thereof to a carboxyl, carboxylic acid anhydride or amino group from a range of from 0.01 to 20 parts by weight per 100 parts by weight of the total of the polyamide resin (A) and the ethylene copolymer (B). If it is less than 0.01 part by weight, the effects to improve mechanical properties, such as heat resistance and impact resistance would be insufficient. Amounts exceeding 20 parts by weight do not produce any further improving effects. The thermoplastic resin composition of the present invention can be prepared by first melt-kneading the components (A) and (B) and then adding the polyfunctional compound (C) to the resulting polymer blend, followed by melt-kneading to effect partial crosslinking reaction. It is considered that the component (C) added and melt-kneaded forms a polymer having satisfactory physical properties in a micro-dispersed state through moderate crosslinking reaction. It is generally accepted that improvement of heat deformation properties, in turn, tends to increase rigidity, which would lead to reduced impact resistance. However, the composition of this invention unexpectedly exhibits both improved heat resistance and improved impact resistance without suffering deterioration in other physical properties. In the production of the resin composition, the melt-kneading can be carried out by means of commonly employed kneading machines, such as single- or twin-screw extruders, a Banbury mixer, a roll, and various types of kneaders. The molten mixture of the components (A) and (B) obtained in, for example, an extruder may be once granulated, and the component (C) is then added thereto, followed by melt-kneading in an extruder. It is preferable, however, that the components (A) and (B) are melt-kneaded in a front zone of an extruder equipped with a side feeder to prepare a molten mixture and then the component (C) either in a solid or molten state is fed thereto from a side feed opening at a rear zone of the same extruder and melt-kneaded to obtain the resin composition. It is also preferable that the component (C) is previously melt-kneaded together with a resin inert thereto to prepare a master batch, which is appropriately added to a resin composition comprising the components (A) and (B) when necessary. In carrying out kneading, the resinous components, each in the form either of powder or pellet, are preferably dry-blended uniformly by the use of a mixing means, e.g., a tumbling mixer or a Henschel mixer. If desired, such dry-blending may be omitted, and each of the resinous components may be individually fed to a kneading machine. If desired, the resin composition according to the present invention may further comprise other optional components, such as pigments, dyes, reinforcements, fillers, thermal stabilizers, antioxidants, weathering agents, nucleating agents, lubricants, antistatics, flame retardants, plasticizers and other additives, and other polymers, as far as addition of these components does not impair moldability and physical properties of the resulting resin composition. In particular, addition of reinforcements or fillers, such as glass fibers having been subjected to various finishing treatments, carbon fibers, talc or calcium carbonate, produces a very useful resin composition having markedly improved rigidity and impact strength. The resin composition of the present invention can be molded by various molding methods, such as injection molding or extrusion molding. The present invention is now illustrated in greater detail with reference to Examples and Comparative Examples. In these examples, the parts and ratios are by weight. The resin compositions obtained in these examples and comparative examples were evaluated according to the following test methods. 1) Flexural Modulus: Measured in accordance with JIS K7203 (specimen thickness: 3.2 mm; measuring temperature: 23°C). 2) Izod Impact Strength: Measured in accordance with JIS K7110 (specimen thickness: 3.2 mm; measuring temperature: 23°C and -40°C; V-shaped notch). 3) Heat Deformation Temperature: Measured in accordance with JIS K7207 (specimen thickness: 3.2 mm; bending stress: 4.6 kgf/cm²). 4) Melt Index: Measured in accordance with JIS K6760 (190°C, 2160 g). The polyamide resins, ethylene copolymers and polyfunctional compounds used in the examples and comparative examples were as follows. A) Polyamide resin: (1) Polyamide 6.6 ("Maranyl® A 125" produced by Unitika Ltd.) (2). Polyamide 6 ("A 1030 BRL" produced by Unitika Ltd.) B) Ethylene Copolymer: (1) Copolymer (1) (E/EA/MAH = 66.8/32.0/1.2; MI: 7 g/10 min) (2) Copolymer (2) (E/EA/MAH = 71.9/25.0/3.1; MI: 33 g/10 min) (3) Copolymer (3) (E/MA/MAH = 70.2/27.8/2.0; MI: 15 g/10 min) (4) Copolymer (4) (E/MAH = 95.0/5.0; MI: 10 g/10 min) Abbreviations used here have the following meanings: E: Ethylene EA: Ethyl acrylate MA: Methyl acrylate MAH: Maleic anhydride MI: Melt index The above-described ethylene copolymers can be prepared by the processes described in French Patents 1,323,379 and 2,498,609. C) Polyfunctional Compound: (1) Bondfast® E [ethylene/glycidyl methacrylate copolymer (88/12) produced by Sumitomo Chemical Co., Ltd.; MI: 3 g/10 min)] (2) Acryft® CM 4008 [ethylene/methyl methacrylate copolymer (81/19) produced by Sumitomo Chemical Co., Ltd.; MI: 7 g/10 min)] (3) Platamid® H005 (copolyamide produced by Plate Bonn GmbH; specific gravity: 1.08; melting point: 115 to 125°C) (4) Siliconediamine X-22-161C (silicone oil having a primary amino group at both terminals of dimethylpolysiloxane, produced by Shin-etsu Chemical Ind., Co., Ltd.; amine equivalent: 1625) (5) E-DAM Copolymer [ethylene/dimethylaminoethyl methacrylate copolymer (72/28); MI: 100 g/10 min)] (6) Yukalon® EAA-510W [ethylene/acrylic acid copolymer (80/20) produced by Mitsubishi Petrochemical Co., Ltd.; MI: 300 g/10 min] (7) Saponified E-VA (saponification product of an ethylene/vinyl acetate copolymer (57/43); degree of saponification: 99%; MI: 35 g/10 min) (8) MB-1 (master batch prepared by melt-kneading 1 part of hexamethylenediamine carbamate and 99 parts of Acryft® CM4008 at 200°C in a 30 mm vented single-screw extruder) (9) MB-2 (master batch prepared by melt-kneading 1 part of hexamethylenediamine carbamate and 99 parts of Platamid® H005 at 170°C in a 30 mm vented single-screw extruder) (10) MB-3 (master batch prepared by melt-kneading 5 parts of 2,2′-(1,3-phenylene)-bis(2-oxazoline) and 95 parts of Acryft® CM4008 at 200°C in a 30 mm vented single-screw extruder) (11) MB-4 (master batch prepared by melt-kneading 2 parts of pyromellitic acid anhydride and 98 parts of an ethylene-propylene rubber ("E-120P" produced by Sumitomo Chemical Co., Ltd.) at 200°C in a 30 mm vented single-screw extruder) EXAMPLES 1 TO 13 AND COMPARATIVE EXAMPLE 13 A polyamide resin and an ethylene copolymer indicated in Table 1 below were melt-kneaded in a 30 mm vented single-screw extruder at a temperature of 270°C in the case of using polyamide 6.6 or at 240°C in the case of using polyamide 6. The resulting blend was mixed with a polyfunctional compound as shown in Table 1, and the mixture was melt-kneaded at a temperature as described above in the same extruder as described above to obtain a resin composition. Each of the resulting compositions was dried at 80°C for 12 hours and molded by means of a 10 oz. injection molding machine ("IS-150E-V Model" manufactured by Toshiba Corporation) at a temperature of 290°C in the case of using polyamide 6.6 or at 260°C in the case of using polyamide 6 and at a mold temperature of 70°C to prepare test specimens for physical property measurement. The test results obtained are shown in Table 1. COMPARATIVE EXAMPLES 1 AND 4 A polyamide resin, an ethylene copolymer, and a polyfunctional compound indicated in Table 1 were melt-kneaded through one step at 270°C by the use of a 30 mm vented single-screw extruder. The test results obtained are shown in Table 1. COMPARATIVE EXAMPLES 2, 3, 5 AND 8 A polyamide resin and an ethylene copolymer as shown in Table 1 were melt-kneaded by means of a 30 mm vented single-screw extruder at a temperature of 270°C in the case of using polyamide 6.6 or at 240°C in the case of using polyamide 6 to prepare a resin composition. The test results obtained are shown in Table 1. COMPARATIVE EXAMPLES 6 AND 9 A polyamide resin and a polyfunctional compound shown in Table 1 were melt-kneaded by using a 30 mm vented single-screw extruder at a temperature of 270°C in the case of using polyamide 6.6 or at 240°C in the case of using polyamide 6 to prepare a resin composition. The test results obtained are shown in Table 1. COMPARATIVE EXAMPLES 7 AND 10 Each of polyamide 6.6 and polyamide 6 was evaluated for physical properties. The results obtained are shown in Table 1. COMPARATIVE EXAMPLES 11 AND 12 A polyamide resin and an ethylene copolymer shown in Table 1 were melt kneaded in a 30 mm vented single-screw extruder at 270°C to obtain a resin blend. The resulting blend was mixed with Acryft® CM4008 of Platamid® H005, and the mixture was melt-kneaded at 270°C in the same extruder. The test results obtained are shown in Table 1. EXAMPLE 14 Polyamide 6.6 and Copolymer (1) were melt-kneaded at 270°C by the use of a 44 mm vented twin-screw extruder having a side feeder at the middle portion of the barrel. While these resinous components were melt-kneaded, a polyfunctional compound shown in Table 1 was fed from the side feed opening of the extruder at a constant rate and melt-kneaded to obtain a resin composition. The test results obtained are shown in Table 1. As described above, the thermoplastic resin composition in accordance with the present invention provides molded articles having a very good balance of various physical properties, such as mechanical and thermal properties, and satisfactory appearance. In particular, the fact that the addition of the polyfunctional compound achieves improvements on heat deformation properties and impact resistance without impairing other physical properties in an unpredictable result. The resin composition of the present invention can be molded easily into films, sheets or other molded articles by molding methods employed for general polyamide-based thermoplastic resin compositions, such as injection molding, extrusion molding, and the like, to provide resin products exhibiting a very good balance of physical properties, such as impact resistance, rigidity and heat resistance and uniform and smooth appearance.

Claims: 1. A thermoplastic resin composition obtained by: melt-kneading (A) from more than 60 to 97 parts by weight of a polyamide resin and (B) from 3 to less than 40 parts by weight of an ethylene copolymer having a melt index of from 1 to 100 g/10 min. and comprising (a) from 40 to 90% by weight of an ethylene unit, (b) at least 5% by weight of an alkyl α,β-unsaturated carboxylate unit, and (c) from 0.3 to 10% by weight of a maleic anhydride unit; and then melt-kneading the resulting composition with (C) from 0.01 to 20 parts by weight, based on 100 parts by weight of components (A) and (B), of a polyfunctional compound having, per molecule, at least two functional groups selected from amino, epoxy, dihydroxazolyl, carboxyl, carboxylic acid anhydride and hydroxyl groups, so as to effect a partial cross-linking reaction. 2. A thermoplastic resin composition as claimed in Claim 1, wherein said ethylene copolymer (B) comprises (a) from 65 to 90% by weight of an ethylene unit, (b) from 10 to 35% by weight of an alkyl α,β-unsaturated carboxylate unit, and (c) from 1 to 5% by weight of a maleic anhydride unit. 3. A thermoplastic resin composition as claimed in Claim 1 or 2, wherein said polyfunctional compound (C) is an aliphatic diamine carbamate. 4. A thermoplastic resin composition as claimed in Claim 1 or 2, wherein said polyfunctional compound (C) is an ethylene copolymer comprising an ethylene unit and an N,N-dialkylaminoalkyl α,β-unsaturated carboxylate unit or an ethylene copolymer comprising an ethylene unit and an N,N-dialkylaminoalkyl α,β-unsaturated carboxylic acid amide unit. 5. A thermoplastic resin composition as claimed in Claim 1 or 2, wherein said polyfunctional compound (C) is an ethylene copolymer comprising an ethylene unit and a glycidyl α,β-unsaturated carboxylate unit, an ethylene copolymer comprising an ethylene unit and an alkyl α,β-unsaturated carboxylate unit, or an ethylene copolymer comprising an ethylene unit, a glycidyl α,β-unsaturated carboxylate unit, and a vinyl carboxylate unit. 6. A thermoplastic resin composition as claimed in Claim 1 or 2, wherein said polyfunctional compound (C) is 2,2′-(1,3-phenylene)-bis(2-oxazoline). 7. A molded product made from a composition as claimed in any preceding claim.

Inventors: MASHITA, KENTARO, NAMBU, JINSHO, OHMAE, TADAYUKI, TOYOSHIMA, YOSHIKI
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1988
Main classification: C08L77
IPC codes: C08K5, C08L77