CRYSTALLIZATION METHOD EMPLOYING MICROWAVE RADIATION

Abstract: A crystallization process employing microwave energy is described. The process is especially useful in the manufacture of porous crystaline materials, e.g., zeolites.

Description: This invention relates to a method of crystallizing materials from aqueous crystallization media. Zeolite materials, both natural and synthetic, have been demonstrated in the past to have catalytic properties for various types of hydrocarbon conversion. Certain zeolitic materials are ordered, porous crystalline metallosilicates having a definite crystalline structure as determined by X-ray diffraction within which there are a number of smaller cavities which may be interconnected by a number of still smaller channels or pores. These cavities and pores are uniform in size within a specific zeolite material. Since the dimensions of these pores are such as to accept for adsorption molecules of certain dimensions while rejecting those of large dimensions, these materials have come to be known as "molecular sieves" and are utilized in a variety of ways to take advantage of these properties. Such molecular sieves, both natural and synthetic, include a wide variety of positive ion-containing crystalline metallosilicates. For example, in the case of aluminosilicates, these materials can be described as a rigid three-dimensional framework of SiO₄ and AlO₄ tetrahedra which are cross-linked by the sharing of oxygen atoms whereby the ratio of the total aluminum and silicon atoms to oxygen atoms is 1:2. The electrovalence of the tetrahedra containing aluminum is balanced by the inclusion in the crystal of a cation, for example an alkali metal or an alkaline earth metal cation. This can be expressed wherein the ratio of aluminum to the number of various cations, such as Ca/2, Sr/2, Na, K or Li, is equal to unity. One type of cation may be exchanged either entirely or partially with another type of cation utilizing ion exchange techniques in a conventional manner. By means of such cation exchange, it has been possible to vary the properties of a given aluminosilicate or other metallosilicate zeolite by suitable selection of the cation. The spaces between the tetrahedra are occupied by molecules of water prior to dehydration. Prior art techniques have resulted in the formation of a great variety of synthetic porous, crystalline metallosilicate zeolites. The zeolites have come to be designated by letter or other convenient symbols, as illustrated by zeolite A (U.S. Patent No. 2,882,243), zeolite L (U.S. Patent No. 3,130,006), zeolite X (U.S. Patent No. 2,882,244), zeolite Y (U.S. Patent No. 3,130,007), zeolite ZK-5 (U.S. Patent No. 3,247,195), zeolite beta, (U.S. Patent No. 3,308,069), zeolite ZK-4 (U.S. Patent No. 3,314,752), zeolite ZSM-4 (Great Britain Patent No. 1,117,568), zeolite ZSM-5 (U.S. Patent No. 3,702,886, now U.S. Patent No. Re. 29,948), zeolite ZSM-11 (U.S. Patent No. 3,709,979), zeolite ZSM-12 (U.S. Patent No. 3,832,449), zeolite ZSM-20 (U.S. Patent No. 3,972,983), zeolite ZSM-22, zeolite ZSM-23 (U.S. Patent No. 4,076,842), zeolite ZSM-34, zeolite ZSM-35 (U.S. Patent No. 4,016,245), zeolite ZSM-39 (U.S. Patent No.4,259,306), zeolite ZSM-21 (U.S. Patent No. 4,046,859), ZSM-48 (U.S. Patent No. 4,375,573), ZSM-51 (U.S. Patent No. 4,568,654), zeolite EU-1 (European Patent Application 0 042 226), zeolite EU-2 (UK Patent Application GB 2077709 A), zeolite EU-4 (European Patent Application 0 063 436), and zeolites NU-6(1) and NU- 6(2) (U.S. Patent No. 4,397,825), merely to name a few. Zeolites containing a framework element other than, or in addition to, aluminum, e.g., boron, iron, titanium, zirconium, geranium, gallium, etc., are known from, inter alia , U.S. Patent Nos. 3,328,119; 3,329,480; 3,329,481; 4,414,423 and 4,417,088. Synthetic zeolites are generally prepared by providing an aqueous solution of the desired oxides and other required components of the crystallization reaction medium and thereafter crystallizing the zeolite under heat and pressure. The present invention provides a method for producing a porous crystalline zeolite comprising the steps of :- a) providing a crystallization medium comprising a crystallizable material and a heat transfer agent sympathetic to microwave energy; and, b) subjecting the crystallization medium to microwave energy to crystallize the crystallizable material and produce the required zeolite. The term "crystallizable material" as used herein shall be understood to include a crystallizable material which is initially present in the crystallization medium as well as the precursors, or formative components, of the crystallizable material. In the case of the latter, subjecting the crystallization medium to microwave energy in accordance with this invention supplies the thermal energy required to drive the reaction and effect crystallization. A general advantage of the foregoing crystallization method lies in its ability to provide relatively small crystals at higher rates of productivity compared to known hydrothermal crystallization procedures. Such crystals typically exhibit greater catalytic activity since their relatively small size permits faster diffusion of reactant(s) into, and product(s) out of, the catalyst. While the rate of nucleation is not greatly influenced by temperature, crystal growth is fairly temperature-sensitive so that when conventional hydrothermal processes are utilized in obtaining relatively small crystals, it is necessary to reduce the temperature and concomitantly, increase the time, required to effect crystallization. Longer crystallization periods not only reduce productivity, they increase the risk that the desired crystalline material will become contaminated with undesirable crystalline material. The unexpectedly rapid crystallization rates which are made possible by the method of the present invention permit one to obtain smaller crystals within a shorter period than is possible with conventional hydrothermal crystallization techniques and with less risk of contamination than with the latter procedures. In the case of synthetic zeolites, the foregoing method has surprisingly been found to provide the desired zeolites but with altered morphologies compared to those of the same zeolites prepared by known hydrothermal crystallization methods. The method of the present invention is useful for the crystallization of all manner of porous crystalline zeolites such as the porous crystalline metallophosphate materials and the porous crystalline metallosilicate zeolites in particular. Essentially any medium from which a crystalline zeolite can be formed is suitable for practicing the invention. The heat transfer agent sympathetic to microwave energy, which is an essential constituent of he crystallization medium herein, can be water or an organic compound, e.g., a liquid hydrocarbon, an alkylene glycol such as ethylene glycol, etc. Materials which absorb microwave energy do so by vibrating at the same frequency as the microwave. For the purposes of this disclosure, a heat transfer agent is considered to be sympathetic to microwave energy if it absorbs microwave energy. In contrast, if the heat transfer agent reflects or is transparent to microwave energy, it is not considered to be sympathetic to microwave energy. One type of non-aqueous crystallization medium which is suitable herein is that disclosed in U.S. Patent No. 3,503,900. According to this patent, a zeolitic molecular sieve is crystallized from a crystallization medium containing a hydrocarbon oil as the heat-transfer medium. Suitability of a particular material for use as a heat transfer agent in the method of this invention can be readily determined by simple and routine testing. For illustration purposes, the crystallization method herein will be more fully described in connection with the preparation of two zeolites, i.e., the sodium form of zeolite A (NaA), a small pore zeolite useful as an adsorbent, detergent builder, etc., and zeolite ZSM-5, a medium pore zeolite having application as a catalyst for a wide variety of chemical conversion processes including hydrocracking, hydrofinishing, hydroewaxing, oligomerization, isomerization, disproportionation, alkylation, reforming, etc. In making zeolite NaA, representative reactants are silica gel, silicic acid or sodium silicate as a source of silica. Alumina may be obtained from activated alumina, gamma alumina, alpha alumina, alumina trihydrate, or sodium aluminate. Sodium hydroxide may supply the sodium ion and in addition assist in controlling the pH. Preferably the reactants are water soluble. A solution of the reactants in the proper proportions is placed in a container, suitably of glass or other material which does not significantly interfere with the passage of microwave radiation. The container is preferably closed to prevent loss of water and the reactants are subjected to microwave heating for the required time. A convenient and preferred procedure for preparing the reactant mixture is to make an aqueous solution containing the sodium aluminate and hydroxide and add this, preferably with agitation, to an aqueous solution of sodium silicate. The system is stirred until homogeneous or until any gel which forms is broken into a nearly homogeneous or until any gel which forms is broken into a nearly homogeneous mix. After this mixing, agitation may be stopped as it is unnecessary to agitate the reacting mass during the formation and crystallization of the zeolite, however, mixing during formation and crystallization has not been found to be detrimental. The initial mixing of ingredients is conveniently done at room temperature but this is not essential. A crystallization temperature of about 100°C is particularly advantageous in this process. However, satisfactory results can be obtained with the temperature of the reaction as high as about 150°C, the pressure being atmospheric or at least that corresponding to the vapor pressure of water in equilibrium with the mixture at the higher temperature. After the reaction period, the NaA crystals are recovered, e.g., by filtration, washed and dried. Zeolite ZSM-5 can be suitably prepared by preparing a solution containing a tetraalkylammonium compound, e.g. tetrapropylammonium bromide, a Group IA or IIA oxide, e.g., sodium oxide, an oxide of a Group IIIB, an oxide of Group IVB, and a heat transfer agent which is sympathetic to microwave radiation such as water and/or an organic compound such as ethylene glycol and having a composition, in terms of mole ratios of oxides, falling within the following ranges: Broad Preferred Particularly Preferred OH⁻ / YO₂ 0.07-10.0 0.1-0.8 0.2- 0.75 R₄N⁺/(R₄N⁺+Na⁺) 0.2 - 0.95 0.3-0.9 0.4-0.9 H₂O/OH⁻ 10 - 300 10-300 10-300 YO₂/W₂O₃ 20 - infinity 20-3000 40- 200 wherein R is the tetraalkyl group, W is the Group IIIB compound, and Y is the Group IVB compound and maintaining the mixture until crystals of the zeolite are formed. Thereafter, the crystals are separated from the liquid and recovered. Typical reaction conditions consist of heating the foregoing reaction mixture to a temperature of from 75°C to 175°C for a period of time of from one hour to 60 days. A more preferred temperature range is from 100 to 175° C with the amount of time at a temperature in such a range being from six hours to 8 days. The digestion of the gel particles is carried out until crystals form. The solid product is separated from the reaction medium, as by cooling the whole to room temperature, filtering, and water washing. The foregoing product is dried, e.g., at 110°C (230°F), for from 8 to 24 hours. Of course, milder conditions may be employed if desired, e.g., room temperature under vacuum. ZSM-5 is preferably formed as an aluminosilicate. The composition can be prepared utilizing materials which supply the appropriate oxide. Such compositions include for an aluminosilicate, sodium aluminate, alumina, aluminum sulfate, sodium silicate, silica hydrosol, silica gel, silicic acid, sodium hydroxide or other Group IA or IIA hydroxides, and tetraalkylammonium compounds, e.g. tetrapropylammonium bromide. In addition to tetrapropylammonium compounds, tetramethyl, tetraethyl or tetrabutyl ammonium compounds can similarly be employed. Glycols such as ethylene glycol are also useful for this purpose. It will be understood that each component utilized in the reaction mixture for preparing a member of the ZSM-5 family can be supplied by one or more initial reactants and they can be mixed together in any order. For example, sodium oxide can be supplied by an aqueous solution of sodium hydroxide, or by an aqueous solution of sodium silicate: tetrapropylammonium cation can be supplied by the hydroxide. The reaction mixture can be prepared either batchwise or continuously. Crystal sized and crystallization time of the crystalline metal organosilicate composition will vary with the nature of the reaction mixture employed, the intensity of the microwave energy, its duration and other factors as will be apparent to those skilled in this art. The as-synthesized ZSM-5 can have the original components thereof replaced by a wide variety of others according to the techniques well known in the art. Typical replacing components would include hydrogen, ammonium, alkyl ammonium and aryl ammonium and metals, other than metals of Group IIIA, including mixtures of the same. The hydrogen form may be prepared, for example, by substitution of original sodium with ammonium. The composition is then calcined at a temperature of, say, 538°C (1000°F) causing evolution of ammonia and retention of hydrogen in the composition. Of the replacing metals, preference is accorded to metals of Groups II, IV and VIII of the Periodic Table. ZSM-5 crystals are then preferably washed with water and dried at a temperature ranging from 66°C to 316°C (150°F to 600°F) and thereafter calcined in air or other inert gas at temperatures ranging from 260°C to 816°C (500°F to 1500°F) for periods of time ranging from 1 to 48 hours or more. The ZSM-5 crystals can be composited with other materials, e.g., alumina, silica, silica-alumina, silica-zirconia, etc. as is known. Microwave heating is employed in the crystallization method of this invention not only to direct the crystallization mechanism but also to increase the rate of crystallization. The useful frequency range of microwave energy herein contemplates electromagentic radiation at about 600 to about 50,000 MHZ; preferably about 900 to about 30,000; more preferably about 900 to about 3600 MHZ; most preferably about 915 to about 2450 MHZ. In order to be suitably exposed to the microwave energy, the crystallization medium must be contained within a vessel fabricated from a material which absorbs little or none of the microwave energy, e.g., the polytetrafluoroethylenes, quartz, ceramic, polypropylene, the polyethylene, some polyesters, alumina, beryllia, some silicones, some phenolics, and polyphenylene oxide. Other materials moderately low in absorption of microwave energy and which are therefore useful herein are: cured epoxies, alkyds, polyester, urethanes, glass, polyamides, polyimides, some phenolics, some melamines, and polycarbonates. Both meandering wave guides and resonating cavities can be used as means for exposing the crystallization medium to be heated to microwave radiation. The meandering wave guide system has the disadvantage of requiring a relatively shallow bed depth. This limitation is caused by the nature of the propagation of the electromagnetic radiation and the necessity for confining it within a hollow wave guide. In order to best utilize the electromagnetic radiation for heating, it is necessary to pass the crystallization medium to be heated through the center of the meandering wave guide since at the top and bottom of the wave guide the electric field is at its maximum while at its sides it as its minimum. A shallow bed depth requires a relatively narrow opening in the wave guide; hence, there is no danger of radiation leakage out of the wave guide. As the bed depth increases, the height of the opening increases up into the zone of high field intensity allowing radiation leakage and resulting in lower overall heating efficiency. Accordingly, the preferred crystallization method utilizes a resonating cavity device since the bed depth is not so limited. While the duration of exposure to the selected level of microwave energy can vary widely, and in any event will depend upon the composition of the crystallization medium, the configuration of the equipment and other apparent factors, periods of from about 30 minutes to about 24 hours or more are entirely suitable in most cases. The following examples are further illustrative of the hydrothermal crystallization method of this invention. The microwave radiation source used in the examples is an industrial size microwave system (CEM Corporation Models MDS- 81) having a selectable power output of 0-600 watts and microwave radiation of 2450 MHZ. EXAMPLE 1 This example illustrates the preparation of zeolite NaA by the microwave heating method herein and compares the resulting crystals with NaA crystals obtained by a conventional hydrothermal crystallization process. 100 Grams of NaAlO₂ and 34 grams of NaOH were dissolved in 520 g of water. Fifty-six grams of Hi-Sil (trade-mark), a precipitated silica, available from PPG industries was added to the solution. The mixture was aged at ambient temperature for 2 hours then crystallized under microwave radiation in a closed glass jar with a capillary vent. At 50% power, zeolite NaA started to crystallize in as little as 5 minutes. It completely crystallizes in about 12 minutes at a temperature of 100°C (as shown in Table II following Example 2). A similar crystallization medium took 2 hours to crystallize under conventional hydrothermal crystallization conditions in a steam box. The product from the microwave crystallization was 85% crystalline, had a SiO₂/Al₂O₃ of 2.28 and Na/Al of 1.03. Scanning electron micrographs showed zeolite NaA resulting from the microwave crystallization to have more rounded edges than zeolite NaA prepared in the conventional manner, a property preferred in detergent builder applications. EXAMPLE 2 This example illustrates the preparation of zeolite ZSM- 5 by the process of the invention comparing the zeolite with ZSM-5 obtained by conventional hydrothermal crystallization procedures. A crystallization reaction mixture was prepared by dissolving 12 g of NaOH, 30 g of tetrapropylammonium bromide in 250 g of water, then adding 575 g of Cab-O-Grip-II (trade mark) colloidal silica and 20 g of ZSM-5 seeds. A 200 g portion of the mixture was crystallized under microwave radiation in a glass jar with a capillary vent. At 300 W, 2450 MHZ power, the sample almost completely crystallized within 100 minutes. A similar preparation took six hours to crystallize using conventional crystallization procedures (as shown in Table II on following page.) EXAMPLE 3 A mixture of 76 parts (by weight) water, 1 part sodium chloride, 23 parts Hi-Sil (trade mark) and 3 parts ZSM-5 seeds was combined with a mixture of 20 parts water, 2 parts aluminum sulfate, 6 parts 50% sodium hydroxide solution, and 11 parts tetrapropylammonium bromide. This combined mixture was then split into two equal parts. One part was loaded into a polytetrafluoroethylene bottle and placed into a hot water bath (90°) for six days. The other half of the synthesis mixture was loaded into an identical bottle and placed in the microwave unit. The microwave unit was programmed to maintain a solution temperature of approximately 90°C for six days. After the six days both samples were washed, filtered, and dried. X-ray analyses indicated that ZSM-5 was synthesized in both examples and the chemical analyses and scanning electron micrographs indicated that both preparations were the same. Table III reports the results. Crystallization of Zeolite ZSM-5 Microwave Crystallization Hydrothermal Crystallization Silica/Alumina Ratio 68 62 Na, wt. % 3.1 2.1 N, wt. % .63 .51 C, wt. % 7.9 5.9 Adsorption, wt. % Cyclohexane 3.9 4.8 n-Hexane 9.0 9.8 EXAMPLE 4 A mixture of 1 part (by weight) aluminum sulfate, 3 parts sulfuric acid, and 27 parts water was combined with a mixture of 28 parts sodium silicate solution (28.5% SiO₂), 7 parts water, 2 parts ZSM-5 seeds, and 50 parts ethylene glycol. The combined mixture was loaded into a polytetrafluoroethylene bottle and placed into a microwave oven. The microwave unit was programmed to maintain a solution temperature of approximately 95°C for 72 hours. After 72 hours, the sample was washed, filtered, and dried. X-ray analysis indicated that ZSM-5 was synthesized. EXAMPLE 5 ZSM-5 crystallization was attempted using the same formula as described in Example 4 except that all of the water was replaced by equal amounts of ethylene glycol. The only remaining source of water in the mixture was present in the sodium silicate solution. The synthesis mixture was processed as described in Example 4. After 72 hours the sample was washed, filtered, and dried. The X-ray analysis indicated that ZSM-5 was synthesized. EXAMPLE 6 A mixture of 1 part (by weight) aluminum sulfate and 27 parts water was combined with a mixture of 14 parts HiSil (trade mark) (an amorphous silica), 3 parts 50% sodium hydroxide solution, 27 parts water, 4 parts ZSM-5 seeds, and 76 parts ethylene glycol. This combined mixture was loaded into a polytetrafluoroethylene bottle and processed as described in Example 4. After 72 hours the X-ray analysis indicated that ZSM-5 was synthesized.

Claims: A method for producing a porous crystalline zeolite comprising the steps of: a) providing a crystallization medium comprising a crystallizable material and a heat transfer agent which absorbs microwave energy; and b) subjecting the crystallization medium to microwave energy to crystallize the crystallizable material and produce the required zeolite. A method according to claim 1 wherein the heat transfer agent comprises water. A method according to claim 1 or 2 wherein the heat transfer agent comprises an organic material. A method according to any preceding claim wherein the porous crystalline zeolite comprises at least one of zeolites A, L, X, Y, ZK-4, ZK-5, ZSM-4, ZSM-5, ZSM-11, ZSM-12, ZSM-20, ZSM-22, ZSM-23, ZSM-34, ZSM-35, ZSM-48, and ZSM-51. A method according to any preceding claim wherein the zeolite comprises a crystalline framework structure containing aluminum. A method according to any preceding claim wherein the frequency range of microwave energy is from 600 to 50,000 MHZ. A method according to claim 6 wherein the frequency range of microwave energy is from 900 to 3600 MHZ.

Inventors: CHU, POCHEN, DWYER, FRANCIS GERARD, VARTULI, JAMES CLARKE
Applicants: MOBIL OIL CORPORATION
Application year: 1988
Main classification: C01B33
IPC codes: C01B37, C01B39