MICROFILLED DENTAL COMPOSITE AND METHOD FOR MAKING IT

Abstract: A microfilled dental composite containing from about 30% to about 60% filler. The filler being sub-micron hydrophobic silica particles of about 0.01 - 0.04 micrometers in diameter. The filler is dispersed in ethoxylated bisphenol A dimethacrylate resin containing suitable aliphatic dimethacrylate diluents up to about 40% by weight and curing agents effecting curing.

Description: This invention relates to a microfilled dental composite and to a method employing it. Background of the Invention Heretofore the fillers in dental composites have been composed of particles from 0.56 to 150 x 10⁻⁶ m (0.56 micron to 150 microns) in diameter. These relatively large particles have resulted in a rougher type of finish than many practitioners desired. Yet, although some manufacturers used a small amount of submicron filler particles, which are typically 2 to 4 x 10⁻⁸ m (0.02 to 0.04 micron) in diameter (to eliminate settling, for example), they have used them only up to about 5% by weight of the composite, and most of the particles remained relatively large. Recently, various manufacturers have placed on the market "microfilled" composites in which all of the filler was in the 2 to 4 x 10⁻⁸ m (0.02 to 0.04 micron) range, and a smoother finish was thereby obtained. However, when using these small particle fillers, only about 25% to 50% of the composite could be filler. When such a relatively small percentage of filler was added to the typical dental resin, the result was that physical properties, such as tensile strength and water sorption, were severely compromised. DE-A-2 462 271 discloses dental composites, in particular artifical teeth and parts for replacement of missing tooth parts, obtained from curable dental compositions which contain microfine inorganic fillers. The microfine inorganic filler is present in about 10 to 90% by wt. and only in particles having a size between about 5 to 700 µm. Preferably, at least 50% of the filler have a particle size in the range of 10 to 40µm. The filler may be silica and the curable resin was a Bis-GMA (a resin on the basis of Bisphenol A and glycidylmethacrylate). EP-A- 140 140 discloses a filled-resin composition useful for porcelain repair and as a dental composite as well as to a method for repairing porcelain or teeth. The composition comprises a methacrylate functional resin usable in dental composites, powdered filler-colorant therein, at least one photoinitiator for the resin in an amount sufficient to initiate polymerization and complete it in depth within about half a minute when exposed to a visible-light output of at least 5,000 foot candles and at least one accelerator-free peroxide curing agent for the resin in an effective amount for completing polymerization within about one-half hour of any portion of the resin not receiving sufficient light to effectuate complete cure before then. Summary of the Invention The present invention provides a microfilled dental composite containing from 15% to 55% filler, said filler being sub-micron hydrophobic silica particles of 1 to 4 x 10⁻⁸ m (0.01 - 0.04 micrometers) in diameter. The filler is dispersed in a resin, the main component of which is ethoxylated bisphenol A dimethacrylate, with suitable aliphatic dimethacrylate diluents up to about 40% by weight. Curing agents are added to effect a one-component light-cured restorative or a two-component self-cured material. A three-part curing system can be used to produce a two-component light-cured material with infinite cure, as in U.S. Patent 4,297,266, issued October 27, 1981 to Ibsen, et al. The resultant cured material exhibits the smooth finish of a microfilled restorative, but has physical properties in the same range as conventional "small particle" restorative. Examples The system is preferably a single, light-cured paste which is applied, shaped, etc. by the dentist, then cured by exposure to a special dental curing light. Example 1 A formulation system embodying this invention comprises the following illustrative ranges: Component Parts by Weight Ethoxylated bisphenol A dimethacrylate 67.75 - 36.00 Triethylene glycol dimethacrylate 11.00 - 16.94 Anti-oxidant (e.g., butyl hydroxy toluene) 0.002 - 0.02 Curing agent (e.g., 2,3-Bornanedione) 0.05 - 0.20 Cure accelerator (e.g., Ethyl-4-dimethylamino benzoate) 0.05 - 0.20 Sub-micron hydrophobic silica particles 15.00 - 55.00 The submicron hydrophobic silica may be Degussa's Aerosil R 972 which has a particle size range of 1 to 4 x 10⁻⁸ m (0.01 to 0.04 microns), with an average particle size of approximately 20 x 10⁻⁷ cm (0.02 micron). The basis for the manufacture of hydrophobic silica is a very pure form of silicon dioxide aerosol obtained by flame hydrolysis. Its particles vary in diameter between 1 to 4 x 10⁻⁵ m (10 and 40 µ). On each 100 sq. meters of surface area, it has about 0.5 millimol silanol groups; hence it is hydrophilic. On its surface, there is a one silanol group per 28-33 Å² (- Si - OH). Hence, with 200 square meters per gram specific surface area, there are about 6.2 x 10²⁰ silanol groups per gram, i.e., one millimol. This gives a figure of about 2000 silanol groups per particle. In a continuous process, some 75% of these silanol groups can be chemically reacted with dimethyl dichlorosilane, the resultant product having about 0.7 millimol of chemically combined methyl groups per 100 square meters of surface area. The silica when thus reacted becomes hydrophobic and behaves differently in organic liquids from the hydrophilic material. For this purpose, freshly obtained hydrophilic silica is separated from the bulk of the hydrochloric acid formed in the flame hydrolysis. Then, this silica, dimethyl dichlorosilane, and steam are pneumatically fed in parallel flow into a fluidized bed reactor heated to about 400°C by means of an inert gas such as nitrogen. Besides the chemical reaction of the chlorosilane with the silanol groups of the surface, the desorption of the hydrochloric acid resulting from the reaction takes place in the reactor in a continuous stream, so that there is an analytically assessable chlorine content of below 0.03%. The main quantity of hydrochloric acid is removed from the freshly manufactured SiO₂ and the material does not yet contain any absorbed water. Moreover, siloxane bridges still exist on the surface of the particles, these having formed at the high temperatures used in the process. These bridges break up in the presence of water vapor and chlorosilane in the reaction zone, whereupon the reaction can take place in the nascent state of the silanol group formation. Analytical data and moisture absorption data of hydrophobic silica are given in Tables 1 and 2 respectively. Analytical Data on Hydrophobic AEROSIL R 972 SiO₂ + (-CH₃) 99.8% Surface area (acc. to Brunauer, Emmet & Teller) 120 ± 30 m²/g Average particle size 20 x 10⁻⁷ cm Carbon 1.1 ± 0.2% pH value (4% dispersion methanol/water 1:1) 3.8 ± 0.2 Chlorine content 0.04 ± 0.01% Heavy metals 0.003% As 0.0001% Fe₂O₃ 0.003% Al₂O₃ 0.05% TiO₂ 0.03% Na₂O 0.01% Bulk density about 40-60 g/l Compacted volume about 10 ml/g Moisture Absorption in mg/100 m² Relative air humidity in % 20 40 60 80 Hydrophilic silica 1.3 4.0 10 30 Hydrophobic silica 0.3 0.4 0.9 1.5 . 2,3-Bornanedione and Ethyl-4-dimethyl amino benzoate are exciplex-forming photoinitiators. Other suitable photoinitiators include: 2,3-Bornanedione with ethyl-2-dimethyl amino benzoate Benzil with ethyl-4-dimethyl amino benzoate Benzil with ethyl-2-dimethyl amino benzoate 2-Isopropyl thioxanthone with ethyl-4-dimethyl amino benzoate 2-Isopropyl thioxanthone with ethyl-2-dimethyl amino benzoate Dibenzyl ketone with ethyl-4-dimethyl amino benzoate Dibenzyl ketone with ethyl-2-dimethyl amino benzoate 2-Hydroxy-2-methyl-1-phenyl-propan-1-one with ethyl-2-dimethyl amino benzoate 2-Hydroxy-2-methyl-1-phenyl-propan-1-one with ethyl-4-dimethyl amino benzoate Benzil dimethyl acetal with ethyl-4-dimethyl amino benzoate Benzil dimethyl acetal with ethyl-2-dimethyl amino benzoate Dimethoxy acetophenone with ethyl-4-dimethyl amino benzoate Dimethoxy acetophenone with ethyl-2-dimethyl amino benzoate Benzoin methyl ether with ethyl-4-dimethyl amino benzoate Benzoin methyl ether with ethyl-2-dimethyl amino benzoate . Example 2 A light-cured paste was made as follows: pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 2,3-Bornanedione 0.18 Ethyl-4-dimethyl amino benzoate 0.18 Sub-micron hydrophobic silica 50.00 This paste was compared with one excellent non-microfilled dental composite and with two competing microfilled composites. The test results are shown in Table 3. Tensile Strength kPa (psi) Cure Shrinkage (%) Thermal Expansion (ppm/°C) Water Sorption (mg/cm²) Water Stability An excellent nonmicrofilled dental composite 48,264 (7000) 0.50 17 0.45 Excellent The dental composite of this invention 42,155 (6114) 0.71 29 0.47 Excellent 1st competing microfilled composite (Silux) 26,821 (3890) 1.29 55 1.33 Poor 2nd competing microfilled composite (Durafil) 24,028 (3485) 1.16 62 1.05 Medium As these tests show, the tensile strength of the dental composite of this invention is substantially greater than that of the two competing microfilled composites and almost equal to that of an excellent non-microfilled composite. The cure shrinkage is lower than that of any of the microfilled composites. Thermal expansion is not much greater than that of the tested non-microfilled composites and much less than that of any of the microfilled composite. Water sorption is equal to that of the non-microfilled composite and very much less than that of the competing microfilled composites. Furthermore, color stability is excellent. Water sorption with the system is below 0.5 mg/cm², even with only 30% filler. It remains low throughout the filler range at every concentration tested up to 55% total filler. Example 3 Two pastes were prepared as followed: Paste A pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 Benzoyl Peroxide 1.50 Sub-micron hydrophobic silica 50.00 Paste B pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 2-hydroxy ethyl p-toluidine 4.25 Sub-micron hydrophobic silica 50.00 These pastes comprised a "self-cured" version of the present invention. When these two parts were mixed together, the material cured in 2-1/2 minutes and exhibited the following properties: Tensile strength 42,058 kPa (6100 psi) Water sorption 0.47 Thermal Expansion 29 ppm/°C . Example 4 Two pastes were prepared as followed: Paste A pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 Benzoyl Peroxide 0.55 Sub-micron hydrophobic silica 50.00 Paste B pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 2,3-Bornanedione 0.18 Ethyl-4-dimethyl amino benzoate 20.00 Sub-micron hydrophobic silica 50.00 . When these two parts were mixed together in equal portions, they did not react; however, when activated with a dental curing unit, the material hardened immediately to a depth of about 3-1/2 mm. The material was placed in the absence of light for one hour and again checked for depth of cure. Cure had extended to the depth of the sample, i.e., 12 mm. This example illustrates the use of the present invention in the form of a continuous cure two-part system. Example 5 A paste was prepared as followed: pbw Ethoxylated bisphenol A dimethacrylate 67.75 Triethylene glycol dimethacrylate 16.94 Butylated hydroxytoluene 0.02 2,3-Bornanedione 0.20 Ethyl-4-dimethyl amino benzoate 0.20 Sub-micron hydrophobic silica 15.00 . When exposed to a dental curing light for 30 seconds, the material cured to a depth of 5.35 mm, and had a tensile strength of 39,990 kPa (5800 psi). Example 6 A paste was prepared as followed: pbw Ethoxylated bisphenol A dimethacrylate 36.00 Triethylene glycol dimethacrylate 11.00 Butylated hydroxytoluene 0.002 2,3-Bornanedione 0.05 Ethyl-4-dimethyl amino benzoate 0.05 Sub-micron hydrophobic silica 55.00 . When exposed to a dental curing light for 30 seconds, the material cured to a depth of 4.85 mm, and had a tensile strength of 53,780 kPa (7800 psi).

Claims: A microfilled dental composite containing from 15% to 55% filler, said filler being sub-micron hydrophobic silica particles of 1 to 4 x 10⁻⁸ m (0.01-0.04 micrometers) in diameter, dispersed in ethoxylated bisphenol A dimethacrylate resin containing suitable aliphatic dimethacrylate diluents up to about 40% by weight and curing agents effecting curing. The composite of claim 1 including means for effecting a one-component light-cured material. The composite of claim 1 containing a two-component self-cured material. The composite of claim 1 having a three-part curing system to produce a two-component light-cured material with infinite cure. The composite of claim 1 in the form of a single, light-cured paste that is applied, and shaped and then cured by exposure to a dental curing visible light. A microfilled dental composite, comprising: Component Parts by Weight Ethoxylated bisphenol A dimethacrylate 67.75 - 36.00 Triethylene glycol dimethacrylate 11.00 - 16.94 Anti-oxidant (e.g., butyl hydroxy toluene) 0.002 - 0.02 Curing agent 0.05 - 0.20 Cure accelerator 0.05 - 0.20 Sub-micron hydrophobic silica particles 15.00 - 55.00 . The composite of claim 6 wherein the sub-micron hydrophobic silica has a particle range 1 to 4 x 10⁻⁸ m (0.01 to 0.04 microns), with an average particle size of approximately 20 x 10⁻⁷ cm (0.02 micron) and is based on hydrophylic very pure silicon dioxide aerosol obtained by flame hydrolysis, the particles of which vary in diameter between 1 to 4 x 10⁻⁵ m (10 and 40 µ) and having on each 100 sq. meters of surface area about 0.5 millimol silanol groups so that they are hydrophilic and have on their surface one silanol group per 28-33 Å² (- Si - OH) so that with 200 square meters per gram specific surface area, there are about 6.2 x 10²⁰ silanol groups per gram, i.e., one millimol and therefrom about 2000 silanol groups per particle. The composite of claim 6 wherein the curing agent is 2,3-bornanedione and ethyl-4-dimethyl amino benzoate. The composite of claim 6 wherein the curing agents and cure accelerators are chosen from the following pairs: 2,3-Bornanedione with ethyl-2-dimethyl amino benzoate Benzil with ethyl-4-dimethyl amino benzoate Benzil with ethyl-2-dimethyl amino benzoate 2-Isopropyl thioxanthone with ethyl-4-dimethyl amino benzoate 2-Isopropyl thioxanthone with ethyl-2-dimethyl amino benzoate Dibenzyl ketone with ethyl-4-dimethyl amino benzoate Dibenzyl ketone with ethyl-2-dimethyl amino benzoate 2-Hydroxy-2-methyl-1-phenyl-propan-1-one with ethyl-2-dimethyl amino benzoate 2-Hydroxy-2-methyl-1-phenyl-propan-1-one with ethyl-4-dimethyl amino benzoate Benzil dimethyl acetal with ethyl-4-dimethyl amino benzoate Benzil dimethyl acetal with ethyl-2-dimethyl amino benzoate Dimethoxy acetophenone with ethyl-4-dimethyl amino benzoate Dimethoxy acetophenone with ethyl-2-dimethyl amino benzoate Benzoin methyl ether with ethyl-4-dimethyl amino benzoate Benzoin methyl ether with ethyl-2-dimethyl amino benzoate . A dental composite consisting of: a light-cured paste as follows: pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 2,3-Bornanedione 0.18 Ethyl-4-dimethyl amino benzoate 0.18 Sub-micron hydrophobic silica 50.00 . A method for making a microfilled dental composite comprising the steps of: preparing a first paste of pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 Benzoyl Peroxide 1.50 Sub-micron hydrophobic silica 50.00 , preparing a second paste of pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 2-hydroxy ethyl p-toluidine 4.25 Sub-micron hydrophobic silica 50.00 , mixing said first and second pastes together, and curing the mixture within 2-1/2 minutes. A method for making a microfilled dental composite, comprising: preparing a first paste of pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 Benzoyl Peroxide 0.55 Sub-micron hydrophobic silica 50.00 , preparing a second paste of pbw Ethoxylated bisphenol A dimethacrylate 80.00 Triethylene glycol dimethacrylate 20.00 Butylated hydroxytoluene 0.0125 2,3-Bornanedione 0.18 Ethyl-4-dimethyl amino benzoate 20.00 Sub-micron hydrophobic silica 50.00 , mixing said first and second pastes together in equal portions, and activating the mixture with a dental curing unit. A method of making a microfilled dental composite comprising: preparing a paste as followed, pbw Ethoxylated bisphenol A dimethacrylate 67.75 Triethylene glycol dimethacrylate 16.94 Butylated hydroxytoluene 0.02 2,3-Bornanedione 0.20 Ethyl-4-dimethyl amino benzoate 0.20 Sub-micron hydrophobic silica 15.00 , and exposing said paste to a dental curing visible light for 30 seconds. A method for making a microfilled dental composite comprising: preparing a paste consisting of: and exposing said paste to a dental curing light for 30 seconds.

Inventors: GLACE, WILLIAM R., IBSEN, ROBERT L.
Applicants: DEN MAT CORPORATION
Application year: 1988
Main classification: A61K6
IPC codes: A61K6