METHOD FOR THE SERIES PRODUCTION OF CAPACITIVE PRESSURE SENSORS

Abstract: A method of batch producing capacitive pressure sensors is disclosed in which a sheet of two of a semiconductive material is provided with an insulating layer (4) on side thereof and a plurality of cavities (1) are formed in the semiconductive sheet by removing part of the insulating layer and part of the semiconductive sheet. Simultaneously with producing the cavities in the semiconductive sheet, at least one recess (12, 13) is provided, again by removing part of the insulating layer and part of the semiconductive sheet. The semiconductive sheet is then bonded to a non-conductive substrate (3) to form a composite sheet with the insulating layer (4) in contact with the substrate, the substrate being provided with a number of electrodes (5) corresponding to the number of cavities in the semiconductive sheet and arranged such that they are located within the cavities on bonding of the semiconductive sheet to the substrate, each electrode having an electrical feedthrough (6) extending therefrom and terminating at a point outside of the associated cavity but within an associated recess in the semiconductive sheet. The bonded composite sheet is patterned with a series of grid lines (8, 9) to delineate the plurality of pressure sensors and the semiconductive sheet is scored from the side opposite that provided with the insulating layer so as to break into each recess to reveal, at a stage in the method of production, the terminal end of each electrical feedthrough (6), and the bonded composite sheet is diced along the grid lines so as to separate the pressure sensors one from another.

Description: This invention relates to capacitive pressure sensors, that is pressure sensors which employ a diaphragm, the movement of which due to changes in pressure varies the capacitance of the sensor and thus provides an output representative of the applied pressure. Capacitive pressure sensors are well known and are employed in capacitance transducers, microphones, rupture discs, resonators, vibrators and like devices. Many of the applications for such capacitive pressure sensors require that the sensors be extremely small, for example of the order of 4 mm x 4 mm, and hence the sensors are difficult to handle and hence difficult to produce on a one-by-one basis. The object of the present invention is to provide a method of batch producing capacitive pressure sensors. According to one aspect of the present invention, there is provided a method of batch producing capacitive pressure sensors comprising the steps of:- a) providing an electrically insulating layer on one side of a sheet of a semiconductive material, b) forming an array of cavities in said sheet by removing at least part of the insulating layer, the remaining portions of the sheet acting as a diaphragm, the cavities being arranged in a plurality of rows and columns on the semiconductive sheet, c) forming at least one recess of a predetermined depth in the semiconductive sheet in association with each cavity by removing at least part of the insulating layer, d) bonding the semiconductive sheet to a non-conductive substrate to form a composite sheet with the insulating layer in contact with the substrate, the substrate being provided with electrodes for the cavities in the semiconductive sheet and arranged such that they are located within the cavities on bonding of the semiconductive sheet to the substrate, each electrode having an electrical feedthrough extending therefrom and terminating at a point outside the associated cavity, within the recess, e) providing delineation lines for the plurality of pressure sensors, f) cutting the semiconductive sheet from the side opposite that provided with the insulating layer to a depth, and at a position, so as to break into each recess to reveal, at a stage in the method, the terminal end of each electrical feedthrough, and g) dicing the composite sheet along the delineation lines so as to separate the pressure sensors one from another. Each recess may open to at least two sides of the associated sensor when the latter is finally formed, and the associated electrical feedthrough may terminate within the recess if an electrical lead is to be attached directly thereto once the terminal end is revealed. However, if a planarised electrical connection technique is to be used, each feedthrough extends beyond a part of the associated recess, this part with the related cut serving to insulate the main body of the semiconductive sheet from that portion in contact with the feedthrough and to which portion an electrical connection for the feedthrough is made. Although it is preferable to provide an insulating layer of a thickness such that the cavities can be formed by removing only a part of that layer, it may be necessary in some instances to remove also part of the adjacent semiconductive sheet. Removal of the insulating layer and, when necessary, the semiconductive sheet may be effected by etching and it will be appreciated that to involve a single etching step in relation to the insulating layer is simpler and less expensive than having to involve a second etching step in relation to the semiconductive sheet. Furthermore, the simple etching step in relation to the insulating layer can be achieved with a greater accuracy, namely ± 1%, compared with an accuracy of + 5% in relation to the etching of the semiconductive sheet. If the whole of the insulating layer is to be removed, an autostop etching technique can be employed by which the etching process will automatically terminate when the semiconductive sheet is reached. The cut may be arranged to delineate two corner regions of each sensor and may be at an angle of the order of 45° to the scribe lines. Alternatively, the cuts may be parallel to an edge of each sensor so as to delineate a strip at that edge of the sensor. The cutting step may be implemented prior to the dicing step, whereby the latter results in portions of the semiconductive sheet delineated by the cuts being removed to reveal the terminal end of each electrical feedthrough for subsequent connection to external electrical circuitry. However, these steps may be reversed so that dicing is effected first and then each individual sensor is cut to reveal the terminal end of the or each electrical feedthrough associated therewith. The shape of the cavities, as seen in plan view, may be circular although other shapes, such as rectangles or triangles, enables the packing density to be increased. Batch production may be further facilitated by employing a semiconductive sheet of a thickness greater than that ultimately required for the diaphragm of each sensor, thus making the semiconductive sheet more handleable, and then reducing the thickness of the semiconductive sheet to the required thickness prior to the dicing step. More specifically, the method may comprise the further step of removing part of said portion of the semiconductive sheet acting as a diaphragm from the side of the semiconductive sheet opposite to that which is bonded to the substrate so as to provide the diaphragm with a predetermined thickness appropriate to the required pressure range of the sensor. It will be appreciated that this further step provides a highly advantageous method of manufacturing capacitive pressure sensors of various ranges in as much as the basic fabrication of all of the sensors can be identical with one simple thickness-reducing step, such as by lapping, being used to trim the sensors to the required sensitivity. The parasitic capacitance of a capacitive pressure sensor can be minimised by maximising the thickness of the insulating layer on the semiconductive sheet but there is a trade off between maximising the thickness of the oxide layer and effective bonding of the conductive sheet. It is desirable to monitor the parasitic capacitance of the sensors during manufacture and in the batch production thereof in accordance with the present invention there may be included a further step of providing a dummy feedthrough for a predetermined selection of pressure sensors, each of which dummy feedthroughs is essentially identical to the feedthrough associated with the electrode of the corresponding sensor but electrically disconnected from the electrode. Assuming the insulating layer to be of uniform thickness, the variable capacitance of a sensor according to the applied pressure is given by subtracting the dummy capacitance from the actual capacitance. Thus the said selected sensor provided with dummy electrodes can be used as a quality control tool for the related batch of sensors. The cavity-forming step of the invention may comprise forming a peripheral recess around each cavity, the depth of the peripheral recess being varied to alter the pressure range of the sensor. The peripheral recess may be in the form of a trench, the recess aiding the bonding process, and producing a more linear capacitive/pressure response. The semiconductive sheet may be a doped p-type or n-type silicon but may be any other semiconductive material such as germanium, for example. The substrate or other member on which the electrode and one or more feedthroughs are provided for each sensor is preferably a glass having a coefficient of thermal expansion and Poissons's ratio well matched to the semiconductive material employed as well as a high volume resistivity. Using silicon as the semi-conductive material, a glass known as Corning 7070 or Schott 8248 has proved to be particularly advantageous in producing a pressure sensor with excellent thermal stability and low hysteresis. Capacitive pressure sensors in accordance with the present invention will now be described in greater detail by way of example, with reference to the accompanying drawings, in which:- Figure 1 is a cross-sectional view of one pressure sensor in accordance with the present invention, Figure 2 is a diagrammatic plan view of the batch production of the pressure sensor of Figure 1, Figure 3 is a detail, to a larger scale, of Figure 2, Figure 4 is a diagrammatic representation of steps in the batch production process of the present invention, Figures 5 to 8 illustrate various masks used in process of Figure 4. Figure 9 is a view similar to that of Figure 3 but showing an alternative sensor, and Figure 10 is a view similar to that of Figure 1 but showing a still further alternative embodiment. Referring first to Figure 1, a capacitive pressure sensor in accordance with the present invention is illustrated in cross-section and comprises a cavity 1 which is formed in a sheet 2 of semiconductive material, preferably silicon, by etching. The cavity is closed by bonding the semiconductive sheet 2 to a substrate 3 which is non-conductive and is conveniently in the form of a glass, the use of Corning 7070 or Schott 8248 glass being particularly advantageous. The semiconductive sheet 2 is provided with an electrically insulating layer or facing 4, preferably silicon dioxide or silicon nitride, prior to the formation of the cavity 1. The oxide layer 4 is disposed between the semiconductive sheet 2 and the substrate 3 when the two are bonded together to form a composite sheet. Prior to the bonding process, the substrate 3 is formed with a metallic pad 5 to which is connected an electrical feedthrough 6 which terminates exteriorly of the cavity 1. Batch production of the pressure sensor of Figure 1, in accordance with one aspect of the present invention, may be achieved by taking a sheet of semiconductive material, such as silicon, and forming therein a plurality of cavities 1 which are arranged in a plurality of rows and columns as illustrated in Figure 2. It will be seen from Figure 2 that the cavities 1 are circular in plan view and that the centres of adjacent cavities in a given row (or column) are offset with respect to one another, the locus of the centres of the cavities 1 in a given row taking the form of a sawtooth. The sheet of semiconductive material 2 is provided with the silicon dioxide or nitride layer 4 on the side thereof from which the cavities 1 are formed, the cavities being formed by etching through the oxide layer and into the semiconductive material. Each cavity 1 is surrounded by an annular peripheral recess or trench 1′. The depth of the trench can be varied so as to alter the pressure range of the associated sensor. Simultaneously with forming the cavities 1 and surrounding trenches 1′, there are formed (by etching) recesses at two corners 12, 13 of each sensor to a depth substantially each to the depth of the trenches 1′. A sheet of glass such as Corning 7070 or Schott 8248 is taken to provide the substrate 3 and the glass has deposited on one side thereof a series of circular electrodes 5, together with associated feedthroughs 6, these feedthroughs being those which are electrically connected to the respective electrodes 5. However, as seen in Figure 3, dummy feedthroughs 7 are also provided for a preselected number of sensors in a given batch, which dummy feedthroughs are substantially identical to the feedthroughs 6 but electrically disconnected from the electrodes 5. The electrodes 5 and feedthroughs 6 and 7 may be of a two-layer construction; a layer of NiCr (nickel chromium) in contact with the substrate 3 and a layer of Au (gold) in contact with the silicon oxide 4. The electrodes 5 are formed on the glass substrate 3 in a manner such that when the semiconductive sheet 2 is placed thereon, the electrodes 5 are disposed within the respective cavities 1 by way of being on the side of the cavity opposite the diaphragm D formed by the cut-away semiconductive material. The semiconductive sheet 2 and substrate 3 are then bonded together, preferably using the field assisted bonding technique which is sometimes referred to as anodic bonding or Mallory bonding or electrostatic bonding. The resulting bonding between the semiconductive sheet 2 and the substrate 3 via the dioxide layer 4, and between the metallic feedthroughs 6 and 7 and the dioxide layer 4 and substrate 3 producing a vacuum reference cavity 1 for each sensor. This enables the capacitance between the semi-conductive diaphragm D and the electrode 5 on the substrate to be used as an absolute pressure gauge. The substrate 3 and the dioxide layer 4 are deformed during the bonding step so as to bond these two components together to provide an hermetic seal, and the thermo-compression resulting from the field assisted bonding technique physically draws the dioxide layer 4 and substrate 3 into extremely close contact with the feedthroughs 6 and 7 to an extent such that the hermetic seal is maintained as discussed in greater detail in co-pending Patent Application No. (SPEZ4451). Before or after bonding the semiconductive sheet 2 to the substrate 3, the substrate is divided into a plurality of rectangles by a series of horizontal (as seen in Figure 2) grid lines 8 and a series of vertical (as seen in Figure 2) grid lines 9, these grid lines 8 and 9 thus being orthogonal to one another. Thus the grid lines 8 and 9 delineate the respective pressure sensors and once bonding of the semiconductive sheet 2 to the substrate 3 has been achieved, the semiconductive sheet 2 is cut along a series of lines 10 and a series of lines 11, with the lines 10 and 11 being orthogonal to one another but at an angle to the grid lines 8 and 9. Conveniently, this angle is of the order of 45°. The cuts along lines 10 and 11 are of a depth such that they break into the corner recesses 12 and 13 of each pressure sensor. The grid lines may be produced by etching or otherwise. Once the cuts 10 and 11 have been effected, the composite sheet of pressure sensors is now diced or divided along the grid lines 8 and 9 so as to produce individual pressure sensors. This operation also serves to remove the semiconductive layer from the corner regions 12 and 13 of each sensor to reveal the terminal ends of the feedthroughs 6 and 7. Thus the feedthroughs are exposed for electrical connection to wires or other electrical conductors. Thus electrical output signals can be taken from the feedthrough 6, which signals vary according to the flexure of the diaphragm D occasioned by applied pressure and which varies the capacitance of the sensor. Prior to the dicing step, the semi-conductive sheet 2 may be lapped, ground or otherwise reduced in thickness so as to provide the desired pressure range for the pressure sensors. For example, if a 600 micrometre semiconductive sheet 2 is employed, a 0-2,000 psi (1.4 10⁷ P) pressure sensor would be produced, whereas reducing the semiconductive sheet thickness to 150 micrometres produces a 0-30 psi (2.1·10⁵ P) sensor, these thicknesses referring in fact to the thickness of the actual diaphragm D of each sensor with a cavity diameter of substantially 4.8 mm. With a cavity diameter of 2mm, a 380 micrometre thick diaphragm would produce a 0-2000 psi (1.4 10⁷ P) sensor, and a 70 micrometre diaphragm would produce a 0-30 psi sensor. It will be appreciated that the same basic fabrication technique can be employed to produce a sheet of pressure sensors and then the sheet lapped, ground or otherwise reduced as regards the semiconductive layer to produce a required pressure range. A portion of the sheet could then be diced so as to produce individual pressure sensors of that range and then the remainder of the composite sheet reduced still further as regards the semiconductive layer to provide sensors of a different pressure range, and so on. Alternatively, whole composite sheets can be treated so as to give pressure sensors of the same pressure range. The cavities 1 formed in the semiconductive sheet 2 are preferably 2 micrometres deep and, as already stated, 4.8 mm in diameter. The trenches 1′ may be of a depth of the order of 25 micrometres, with the corner recesses 12, 13 of a similar depth. The overall dimension of each pressure sensor may be 8 mm x 8 mm and the grid lines 8 and 9 may be 200 micrometres in width to allow ready dicing of the composite sheet into individual pressure sensors. However, the sensors may be a quarter the size, i.e. 4 mm x 4 mm and in this case, the cavities may be 1 to 2 micrometres deep with the trenches '1' remaining of the order of 25 micrometers in depth. The use of dummy feedthroughs 7 for a number of sensors in a batch allows the parasitic capacitance of the pressure sensors of that batch to be monitored and thus provide a quality control tool. Figure 9 is similar to that of Figure 3 but shows an alternative embodiment in which the cuts to reveal the feedthroughs 6 are made parallel to one edge of the sensors so as to provide rectangular recesses 14 as opposed to the triangular recesses 12,13 of the embodiment of Figure 3. Figure 9 illustrates one of the sensors provided with an actual feedthrough 6 and a dummy feedthrough 7. In these sensors when no dummy feedthrough is provided, the feedthrough 6 could be positioned as indicated by broken lines in Figure 9. The attachment of electrical leads to the contact pads 15 provided at the ends of the feedthroughs 6 is by wire bonding, with the glass and semiconductor bonding pads being offset by the thickness of the semiconductor. However, this arrangement is unsuitable for the so-called "solder bump" attachment technique which requires a planar surface for the connections. It is possible to use existing semiconductor planarising techniques to produce bonding pads at the same surface on the semiconductive layer 2 as indicated at 16 and 17 in Figure 10 which shows such an arrangement prior to the bonding step. The pad 16 is associated only with the semiconductive layer 2, whereas the pad 17 is associated with the contact pad 15 on the end of the feedthrough 6, via the end or side portion 18 of the semiconductive layer 2 which is electrically insulated from the main body of that layer by a saw cut indicated at 19 in Figure 10. This saw cut 19 is made after the bonding process and a trench 21 is formed at the same line as the trech 1′ in order to prevent the cutting operation causing damage to the feedthrough 6. It will be noted that the portion 18 of the semiconductive layer 2 will be in electrical contact with the feedthrough pad 15 when the bonding process has been completed by virtue of the fact that this portion is devoid of any insulating layer 4. An even more specific example of batch producing capacitive sensors in accordance with the present invention is set out below. EXAMPLE Fabrication of Silicon Capacitive Pressure Sensors For the batch production of silicon capacitive pressure sensors, the basic components used were a silicon wafer 2 and a glass disc 3 of similar diameter. A typical process for preparing the silicon wafer is given hereinafter under the heading "Silicon Sheet Processing". If p-type silicon is used, items 3 to 8 thereof can be omitted. The glass components were machined into discs e.g. 75 mm diameter, 4 mm thick (in order to provide the required rigidity to the sensors as well as to accommodate high pressure devices and registration flats machined to match those aligned with the grid pattern on the silicon wafers. The glass discs were polished to a surface finish better than 25 nm RMS. The glass discs were then patterned with positive resist using the mask of Figure 8. It should be noted that this mask only has a dummy lead or feedthrough 7 on one out of four sensors for this quality control purpose referred to above. The glass discs were then coated sequentially with 10 nm of nichrome and 30 nm of gold using magnetron sputtering. The photoresist was then removed leaving the metalisation 5,6,7 as defined by the mask of Figure 8. The silicon and glass components were then bonded together using field assisted bonding. This operation was performed in a vacuum to ensure a 'zero' pressure reference cavity 1 in each pressure sensor and to ensure good sensor temperature stability. The samples were then heated to a temperature of 450°C and a voltage of 2 kV (silicon positive) applied across the components after they had been pressed together (oxide facing 4 against metallised glass 3). The voltage was applied for a period of 10 minutes. This produces an hermetic seal between the internal cavity 1 and the outside with the metal leads or feedthrough 6,7 connecting the two regions, the oxide facing 4 and the glass 3 having deformed around the edges of the feedthroughs to produce no leakage path, i.e. an hermetic seal. Having bonded the components, the next process step was to deposit aluminium contact pads (approx. 1 micrometre thick) onto the silicon back side of each of the individual sensors. This is achieved using magnetron sputtering, in conjunction with a suitably machined mask. If another metal (e.g. gold/antimony) is used instead of aluminium, stages 2 - 8 of the silicon processing can be omitted for n-type silicon. For forming devices of lower pressure ranges, the silicon is precision lapped, prior to this deposition process, to the required thickness. The next process step involved provision sawing. First diagonal cuts 10,11 were made into the silicon 2 following the diagonal registration flat on an 11.3 mm pitch. These cuts 10,11 stopped within 25 micrometres of the glass-silicon interface. The assembly was then diced along the registration lines 8,9 into individual sensor components. This process caused the removal of the recessed corners 12,13 of each silicon section 2, hence exposing the contact pads on the glass 3. The individual devices were then attached to headers, and gold leads wire bonded to the contact pads on the glass 3 and silicon 2. After attaching a can containing a pressure port, the sensors are ready for testing. It is essential that the silicon and glass preparation and the bonding of the two components are performed under clean conditions. Silicon Sheet Processing Material : 0.02 ohm-cm <111> Sb - doped 3′′ wafers. 1. RCA clean silicon wafers (Figure 4a) Back Side n+ Doping 2. Initial oxide : Grow 0.6 micrometres oxide in wet 0₂; T = 1100°C. 3. Spin resist on front. 4. Strip oxide from backs of wafers in 7:1 Buffered HF (BHF). 5. Strip resist in fuming nitric acid. 6. phosphorus deposition furnace (POCl₃): T = 1050°C; time = 30 m; dry N₂. 7. Strip oxide in 7:1 BHF (Figure 4b). Grow Facing Oxide 9. Grow thermal oxide. T = 1100°C; wet 0₂; time = 180 min; expected d ox = 0.6 micrometres (Figure 4c). 10. Measure oxide thickness, d ox , by Nanospec. interference method. Pattern Generation 11. Photolithography +ve resist using the mask of Figure 5. 12. Machine registration flats aligned with grid pattern (including diagonal) of mask of Figure 5. Wafers must then be thoroughly cleaned. 13. Photolithography +ve resist using the mask of Figure 6. 14. Etch oxide in 7:1 BHF; expected etch time = 12 min. (Figure 4d). 15. Strip resist in fuming nitric acid. 16. Deposit Si₃N₄; d Ni = 150 nm (Figure 4e). 17. Photolithography, +ve resist using the mask of Figure 7. 18. Dry etch Si₃N₄; d Ni = 150 nm; Overetch by 50%. 19. Strip resist in fuming nitric acid. Trench Etch 20. Silicon etch. Dip etch oxide in 20:1 BHF for 15 secs; then silicon etch in HF : HN0₃ : CH₃COOH for 2-3 mins. (Follows the mask of Figure 7). 21. Measure etch depth. Repeat step 18 for time calculated to give an etch depth of 25 micrometres for the trenches 1′ (Figure 4f). 22. Strip Si₃N₄ in orthophosphoric acid; T = 160°C; strip time = 90 mins. Silicon Etch 23. Dry etch Si in CCl₄ to a depth of 2 micrometres (follows the mask of Figure 6) to form the cavity 1 (Figure 4g). 24. Measure thickness d ox at several points to ensure uniformity. It will be seen that the present invention affords a method of batch producing capacitive pressure sensors which represents a significant advance in the art. A basic fabrication technique can be employed using semiconductive layers or sheets of a thickness which are readily handled and yet which can be reduced in the final stages of production to provide the required pressure range for a given sensor.

Claims: A method of batch producing capacitive pressure sensors comprising the steps of:- a) providing an electrically insulating layer (4) on one side of a sheet (2) of a semiconductive material, b) forming an array of cavities (1) in said sheet (2) by removing part of the insulating layer (4), the remaining portions of the sheet acting as a diaphragm, the cavities (1) being arranged in a plurality of rows and columns on the semiconductive sheet, c) forming at least one recess (12, 13; 14; 14, 21) of a predetermined depth in the semiconductive sheet in association with each cavity (1) by removing at least part of the insulating layer (4), d) bonding the semiconductive sheet to a non-conductive substrate (3) to form a composite sheet with the insulating layer (4) in contact with the substrate (3), the substrate being provided with electrodes (5) for the cavities (1) in the semiconductive sheet (2) and arranged such that they are located within the cavities (1) on bonding of the semiconductive sheet (2) to the substrate (3), each electrode (5) having an electrical feedthrough (6) extending therefrom and terminating at a point outside the associated cavity (1) within the recess (12, 13; 14; 14, 21), e) providing delineation lines (8,9) for the plurality of pressure sensors, f) cutting (10, 11; 19) the semiconductive sheet from the side opposite that provided with the insulating layer (4) to a depth, and at a position, so as to break into each recess (12, 13; 14; 14, 21) to reveal, at a stage in the method, the terminal end of each electrical feedthrough (6), and g) dicing the composite sheet along the delineation lines (8, 9) so as to separate the pressure sensors one from another. A method according to claim 1, wherein each recess (12, 13; 14) opens to at least two sides of the associated sensor, when the latter is finally formed, and the associated electrical feedthrough (6) terminates within the recess (12, 13; 14) and is subsequently revealed by removal of semiconductive material overlying the recess for the direct attachment thereto of an electrical connection. A method according to claim 1, wherein each electrical feedthrough (6) terminates within the recess (14) beyond the associated recess (21), the latter serving together with the related cut (19) to insulate the main body of the semiconductive sheet (2) from a portion (18) of semiconductive sheet in contact with the associated feedthrough (6) wherein said portion (18) is retained in the sensor produced and to which portion (18) an electrical connection (17) for the feedthrough (6) is made. A method according to any of claims 1 to 3, and comprising the further step of providing a peripheral recess (1') around each cavity. A method according to any of the preceding claims, wherein both the cavity-forming and recess-forming steps comprise removing part of the semiconductive sheet. A method according to any of the preceding claims, wherein the cuts (10, 11) are arranged to delineate two corner regions of each sensor. A method according to claim 6, wherein the cuts (10, 11) are at an angle of the order of 45° to the scribe lines (8, 9). A method according to claim 6 or 7, wherein the cuts (10, 11) each extend between two edges of the composite sheet, whereby a given cut can delineate corner regions (12, 13) on a plurality of sensors. A method according to any of claims 1 to 5, wherein the cuts are parallel to an edge of each sensor so as to delineate a strip at that edge of the sensor. A method according to claim 2, wherein the cutting step is implemented prior to the dicing step, whereby the latter results in portions of the semiconductive sheet (2) delineated by the cuts being removed to reveal the terminal end of each electrical feedthrough (6) for subsequent connection to external electrical circuitry. A method according to claim 2, wherein the dicing step is implemented prior to the cutting step, whereby each individual sensor is cut to reveal the terminal end of the or each electrical feedthrough (6) associated therewith. A method according to any of the preceding claims, wherein adjacent cavities (1) in a given row or column are offset one from the other. A method according to any of the preceding claims and further comprising the step of reducing the thickness of the semiconductive sheet (2) to a required thickness prior to the dicing step. A method according to any of the preceding claims and further comprising the step of forming in respect of each of a predetermined number of sensors in the batch a second electrically-conductive feedthrough (7) on the substrate substantially equal in surface area to the other feedthrough (6) for a given sensor and extending from the corresponding electrode, but not being electrically connected thereto. A method according to any of the preceding claims, wherein the or each electrical feedthrough (6) in each sensor is hermetically sealed between the insulating layer (4) and the substrate (3). A method according to any of the preceding claims and further comprising the step of removing part of said remaining portions of the semiconductive sheet (2) acting as diaphragms from the side of the semiconductive (2) sheet opposite to that which is bonded to the substrate so as to provide the diaphragms with a predetermined thickness appropriate to the required pressure range of the sensor. A method according to claim 16, wherein the step of removing part of said portion of the semiconductive sheet (2) is effected by lapping or grinding. A method according to any of the preceding claims, wherein the cavity-forming step comprises forming a peripheral recess (1') around each cavity, the depth of the peripheral recess (1') being varied to alter the pressure range of the sensor. A method according to any of the preceding claims, wherein the semiconductive sheet (2) is formed from doped silicon. A method according to any of the preceding claims, wherein the insulating layer (4) is silicon dioxide or silicon nitride. A method according to any of the preceding claims, wherein the substrate (3) is composed of Corning 7070 glass. A method according to any of claims 1 to 18, wherein the substrate (3) is composed of Schott 8248 glass.

Inventors: BLACKABY, DAVID EDWARD, CHEN, FRANK, ROGERS, TONY WILLIAM
Applicants: HAMILTON STANDARD CONTROLS, INC.
Application year: 1988
Main classification: G01L9
IPC codes: G01L9