SELF REGULATING HEATER

Abstract: A self regulating heater comprises a non-­ conductive, magnetic core (20) having a coil (22) wound about it and providing pole pieces (26, 28) extending into contact or very near contact with a surrounding ferromagnetic member (36) which in turn may be surrounded by and in intimate contact with a non-magnetic low resistance member (30); the magnetic member having an effective Curie temperature at the temperature to be maintained.

Description: The present invention refers to a temperature self regulating heater according to the preamble of claim 1, employed as a tool for heating fusible and other types of heat activated bonding materials. In U.S. Patent No. 4,256,945 there is disclosed a first version of a soldering iron employing Curie temperature regulating concepts. An outer conical copper shell is lined with a ferromagnetic material, for instance, alloy 42 having a nominal mu of 400 and high electrical resistance, 75 x 10⁻⁶ ohm-cm. A copper rod is secured to the region of the apex of the cone and extends along the conic axis interiorly of the cone. When a high frequency, constant current is applied between the end of the rod remote from the conic's apex and the base of the cone, current flows primarily in the ferromagnetic material due to skin effect. When the device approaches Curie temperature, the ferromagnetic material becomes non-magnetic and the current flows primarily in the copper shell. Since the current is constant and the copper has substantially less electrical resistance than the ferromagnetic material, Joule heating is greatly reduced. In consequence the temperature is regulated near Curie temperature for the ferromagnetic material chosen. A modified form of heater designed to increase its impedance to better match the current source is disclosed in EP-A-0 180 301, on which is based the preamble of claim 1. Inductive coupling is employed to couple a constant current into a ferromagnetic layer surrounding and contacting a copper rod forming a rearward extension of the tip of a soldering iron. The coil employed to couple current into the magnetic material surrounds the material and an outer magnetic layer is disposed outside the coil to act as a magnetic shield and restrict spreading of the magnetic flux. Experiments were recently conducted to increase the efficiency of such an iron so that the heater can be made to operate efficiently at still higher power than permitted by the current design. The experiments determined that if the shank of the tip was cooled, under a heavy load, the heater responded immediately producing full power to bring the heater up to temperature as quickly as possible. When the tip itself was cooled under heavy load, the heater did not come up to full power and it took longer for the heater to achieve design temperature. Thus it was apparent that, particularly under heavy loads, the displacement of the heater from the tip of the iron had an adverse effect on the ability of the tip to maintain operating temperatures. According to the present invention there is provided a self-regulating electrical heater comprising, a hollow tubular member of ferromagnetic material or having a ferromagnetic material layer on its inner surface, the Curie temperature of which ferromagnetic material determines the self-regulation temperature of the heater, said tubular member containing an electrical coil wound directly on a core of high permeability low electrical conductivity material, with electrical connection means adapted to connect said coil to a substantially constant alternating current source, characterised in that said core is formed with pole portions that are shaped to contact or approach substantially into contact with said ferromagnetic material thereby to provide a low reluctance path between the core and said ferromagnetic material. In an embodiment such as a soldering iron, the heater energisation is by means of a coil and core located interiorly of the tip of the iron and which thus may be located quite close to the working surface while preserving the impedance matching available with inductive coupling. A non-conductive magnetic core material, such as compressed powdered iron or a ferrite, reduces losses in the core while maintaining a high flux density. The problem with placing the core and its associated coil interiorly of the heater is that the flux density of an inductor is far lower exteriorly of the core than in its interior. Thus the current flowing in the heater is relatively low under these circumstances and the heater efficiency is poor. This problem is overcome by using a core with shaped pole portions so as to focus the flux in the ferromagnetic material of the heater. The core may be "I" or "E" shaped, or the like, in axial section with the coil wound about its narrow portion or portions. The heater preferably has a hollow cylindrical interior in which the coil and core are located whereby the cross member of an I-shaped or the legs of an E-shaped core constitute poles concentrating the flux in the adjacent surrounding magnetic material. The magnetic material is preferably itself surrounded by copper or the like so as to provide a low electrical resistance, good heat conductive path for the heater. In consequence of this arrangement the heater is energised at a location quite close to and in some instances immediately interiorly of the working surface of the tool in which the heater is incorporated, increasing efficiency and its constant temperature attributes without sacrificing the impedance matching achieved with an inductive coupling circuit. In addition placement of the core and coil interiorly of the heater greatly decreases the problem of electromagnetically shielding the heater, that is, preventing radiation from the device and the development of circulating currents on the exterior of the heater. Arrangements according to the invention will now be described by way of example and with reference to the accompanying drawings, in which:- Figure 1 illustrates a prior art soldering iron cartridge; Figure 2 illustrates one embodiment of a soldering iron cartridge according to the present invention; Figure 3 is a heater structure according to the present invention employed independently of a soldering iron cartridge; and Figure 4 illustrates a tapered pole that may be employed with the core of the structure of the present invention. Referring now specifically to Figure 1 of the accompanying drawings there is illustrated a soldering iron of the prior art type as described in EP-A-0 180 301. A soldering iron is illustrated for purposes of example only. The concepts disclosed are applicable to any self regulating heater arrangement. The iron has a tip 2, preferably of copper, which has an extension or rod 4 extending rearwardly therefrom. The rod is surrounded by a layer 6 of magnetic material which in turn is surrounded by a multiturn coil 8 adapted to be energized by a high frequency constant current. A magnetic shield 10 surrounds the coil to limit spreading of the magnetic flux. The entire structure rearwardly of the tip 2 is surrounded by a non-magnetic steel tube 12. As previously indicated there are basically two problems with the design of Figure 1 when it is necessary to operate the device at very high wattage levels relative to the wattage for which the device is designed. The first problem is that in spite of the relatively large diameter of the rod 4, the heater is sufficiently removed from the tip 2 to materially affect the response of the heater to large changes in heavy loads. Reference is now made to Figure 2 of the accompanying drawings illustrating one embodiment of the present invention. A soldering iron comprises a truncated conical tip 14 preferably of copper and having a cylindrical recess 16 formed therein axially of the cone. The cylindrical recess 16 is lined with a ferromagnetic material 18 having a Curie temperature that defines the desired regulated temperature of the iron. A magnetic, essentially non-conductive bobbin or core 20 is inserted in the cylindrical channel 16 and has wound thereon a coil 22. The coil 22 is intended to be energized by a constant current source via leads 24. The core 20 is preferably made of a ferrite material because of its high permeability and high resistivity; the former to sustain large quantities of flux and the latter to reduce eddy current losses. Materials having small hysteresis loops are also preferred. The core 20 in this embodiment is I-shaped in axial section and thus has flanges 26 and 28 providing pole pieces of a diameter to preferably cause the circumference of the flanges to contact the inner bore of the magnetic material 18. At the worst the flanges should define a small air gap between their outer circumferences and the magnetic material; the gap being such as not to introduce a significant magnetic reluctance into the magnetic circuit. As to the ferrite material to be used such materials are available with permeabilities of 20 to 5000, a temperature range of 120° to 500°C. and which operate at frequencies from 180 KHz to 180 MHz. One such material is available from Fair-Rite Products, Product No. 9661103001, a ferric oxide, with other oxides. In one application the transformer structure comprised a two layer, 7 turn solenoid of 0.010" (0.25 mm) electromagnet wire wrapped around a ferrite bobbin to provide a 50 ohm resistance and a 20 ohm reactance. The bobbin used had an O.D. of 0.141 (3.58 mm) and an ID of 0.070 (1.78 mm). The system is matched to approximately 50 ohms resistance with an 85 pf capacitor in series with the coil. The heater comprised an 0.0007 inch (0.018 mm) layer of alloy 45 on an 0.005 (0.127 mm) layer of copper. The heater operated at an efficiency of 96.5% efficiency at 10 MHz and 92% at 13.56 MHz, the standard heater frequency of operation. Efficiency in this context is defined as the ratio of heat generated by the heater to the total electrical power supplied to the device. The mu of the material is approximately 125 and the resistivity is approximately 10⁸ ohm-cm. The Curie temperature of the ferrite should be above the Curie temperature of the heater material. The heater unit of Figure 2 may be employed independently of the tip 14; that is the ferrite core 20 and the coil 22 may be mounted on a rod, for instance, and inserted into a snug fitting sleeve of copper having an inner lining of ferromagnetic material whereby to heat the sleeve to solder it to a pipe or the like. Such is illustrated in Figure 3 where the core and coil are designated by the same reference numerals as in Figure 3. In this embodiment the sleeve to be soldered bears the reference numeral 30 and the element or pipe to which it is to be soldered has reference numeral 32. The sleeve 30 is, for instance, a copper tube 34 lined interiorly with a ferromagnetic material 36. The core 20 is snugly received in the sleeve 30 which is to be joined to tube 32. In a system such as Figure 3, the system may be readily adapted to fuse materials of different fusion temperatures. Various temperatures may be had by lining sleeves 30 with ferromagnetic materials of different Curie temperatures. Alloys 42 and 45 are often used each having a different Curie temperature. Many other materials may also be used to provide a wide range of temperature selections. This concept may be embodied into replaceable tip soldering irons. Referring now to Figure 4 of the accompanying drawings, there is illustrated a core having shaped pole pieces to focus the flux into the adjacent ferromagnetic material and thus reduce leakage flux. The tapering is designated by reference numeral 38. It should be noted that the dimensions of the tapered member must be large enough to prevent saturation of the pole piece which of course would increase rather than decrease leakage flux. The core 20 of Figures 2 and 3 and 4 may have many cross-sectional shapes such as a square, rectangle, etc. as opposed to cylindrical, depending upon the interior shape of the aperture into which it is to be fitted. Further the heater is not limited to a magnetic layer on a copper layer but may be a magnetic layer on a ferromagnetic layer of different Curie temperature. It has been stated that the core has a high resistivity so as to reduce core losses and thus produce little heating thereof. There may be instances where some core heating may be desired and thus a ferromagnetic core with some loss would be desirable. In such a case, the Curie temperature of such material should be above the Curie temperature of the ferromagnetic material of the heater. Thus two heat sources are supplied, one with a variable temperature and one with a more constant temperature. In such case the ranges of the cyclic temperature would be less. The term "constant current" as employed herein does not mean a current that cannot increase, but means a current that obeys the following formula where I is the load current. Specifically, in order to autoregulate, the power delivered to the load when the heater exceeds Curie temperature, must be less than the power delivered to the load below Curie temperature. If the current is held invariable, then the best autoregulating ratio is achieved short of controlling the power supply to reduce current. So long, however, as the current is controlled in accordance with the above formula, autoregulation is achieved. Thus, when large self regulating ratios are not required, constraints on the degree of current control may be relaxed thus reducing the cost of the power supply. The above equation is derived by analyzing the equation: P = [I²R] where P is power and I is the current in the load. Differentiating with respect to R dP dR = |I|² + 2R|I| dI dR to satisfy the requirements for self regulation dP/dR>0. Thus, which reduces to the above equation. It should be noted, however, that the more constant the current the better the self regulation.

Claims: A self-regulating electrical heater comprising, a hollow tubular member (18,34) of ferromagnetic material or having a ferromagnetic material layer (36) on its inner surface, the Curie temperature of which ferromagnetic material determines the self-regulation temperature of the heater, said tubular member containing an electrical coil (22) wound directly on a core (20) of high permeability low electrical conductivity material, with electrical connection means (24) adapted to connect said coil to a substantially constant alternating current source, characterised in that said core is formed with pole portions (26,28;38) that are shaped to contact or approach substantially into contact with said ferromagnetic material thereby to provide a low reluctance path between the core and said ferromagnetic material. A heater according to Claim 1, wherein said hollow tubular member is an electrically-conductive member with an inner lining of ferromagnetic material. A heater according to Claim 1 or Claim 2, wherein the material of said core has a higher electrical resistivity and Curie temperature than said ferromagnetic material. A heater according to any preceding claim, wherein the material of said core is also a ferromagnetic material. A heater according to any of the preceding Claims 1 to 3, wherein the material of said core is a ferrite having a resistivity of at least 10⁷ ohm-cm and a small BvH loop. A heater according to any of the preceding Claims 1 to 3, wherein the material of said core is a compressed powdered iron having a resistivity of at least 10⁷ ohm-cm and a small BvH loop. A heater according to any preceding claim, wherein the core is I-shaped or E-shaped in axial section, with the transverse limbs of the I or E constituting the pole portions that contact or substantially contact the surrounding ferromagnetic member or layer (18,36). A heater according to Claim 7, wherein said pole portions are tapered toward their tips.

Inventors: CARTER, JR. PHILIP S., COWELL, MARK J., LADD, KEVIN
Applicants: METCAL INC.
Application year: 1988
Main classification: B23K3
IPC codes: B23K3, H05B6