SINGLE-STEP CATALYTIC PROCESS FOR THE DIRECT CONVERSION OF POLYSACCHARIDES TO POLYHYDRIC ALCOHOLS

Abstract: Single-step process for the conversion of polysaccharides to polyhydric alcohols by hydrogenation at high pressure and tempera­ ture in the presence of a catalyst consisting of (i) a supported metal selected from ruthenium, copper, nickel, cobalt and their mixtures, said metal being highly dispersed on the support so as to be capable of adsorbing more than 0.58 molecules of CO per atom of metal, and (ii) a solid having acidic functions, which may or may not be identical to the support, said solid having sufficient acid functions so that the rate constant of hydrolysis of sucrose on the catalyst is greater than 70% of the rate constant of hydrogenation of glucose on the catalyst. The process gives substantially pure polyhydric alcohols in a single step.

Description: The invention relates to the production of substantially pure polyhydric alcohols. More particularly, this invention relates to a single-step process for the catalytic production of substantially pure polyhydric alcohols from polysaccharides. A particular aspect of the invention relates to the simultaneous hydrolysis and hydrogenation of polysaccharides, using an heterogeneous catalyst, to produce substantially pure hexitols. The term "carbohydrate" as used herein includes monosaccharides, polysaccharides, and mixtures of monosaccharides and/or polysaccharides. The term "polysaccharide" as used herein includes those saccharides containing more than one monosaccharide unit. This term thus includes disaccharides and oligosaccharides. The supported nickel catalyst supported on carbon, diatomaceous earth or kieselguhr, as described in U.S. Patents 3,538,019 and 3,670,035 (which is a division of U.S. Patent 3,538,019) have high activity for the conversion of both monosaccharides and polysaccharides including carbohydrate mixtures such as corn starch hydrolyzate, with high selectivity to sorbitol when either corn starch hydrolyzate or dextrose is used as the starting material. A disadvantage of the catalysts described in U.S. Patents 3,538,019 and 3,670,035 is that they cannot be regenerated; when reactivation is required, it is necessary to remove the active catalyst material from the support by chemical means and then to redeposit the catalyst metal on the support. Various other nickel catalysts for conversion of carbohydrates to polyhydric alcohols are cited in U.S. Patents 3,538,019 and 3,670,035. The conversion of carbohydrates to polyhydric alcohols using ruthenium on a solid carrier is known. U.S. Patent 2,868,847 discloses the use of ruthenium on an inert catalyst support such as carbon, alumina, silica, or kieselguhr as a catalyst for the catalytic hydrogenation of mono- and disaccharides, the latter being hydrolyzed and hydrogenated to hexitols. However, maltose, a disaccharide containing two glucose units, was more easily converted to maltitol, a C12 alcohol, according to the patent. The hydrogenation of aqueous solutions of carbohydrates over zerovalent groups VIII metals dispersed on alpha-alumina is disclosed in U.S. Patent 4,380,680. The hydrogenation of monosaccharides using a supported ruthenium, palladium, platinum, or nickel catalyst (activated carbon was used as the support in all experimental work) is discussed in an article by N.A. Vasyunina et al. "Catalytic Pro-perties of Ruthenium in Monosaccharides Hydrogenation Reaction" in Izvestiya Akademii Nauk SSR Khimicheskaya Serya 4:848-854 (1969). Ruthenium was found to have higher activity than the other three catalysts. A two stage process for hydrogen of ligneous and other plant material such as wood sawdust is disclosed in Izv. Akad. Nauk SSR, Otd. Khim. 8:1522-1523 (1960). The process consists of a first stage hydrolytic hydrogenation of polysaccharides in an acid medium, followed by a second stage hydrogenation of the lignin in an alkaline medium, using a ruthenium catalyst in both stages. In a specific embodiment, pine sawdust is treated using an aqueous phosphoric acid medium and a ruthenium-on-carbon catalyst. The first stage reaction product is filtered to separate the liquid medium from the crystals obtained from the first stage filtrate. Belgian Patent 837,201 and U.S. Patents 3,963,788 and 3;963,789 and 4,072,628 disclose a two-stage high-pressure process for the conversion of carbohydrates to polyhydric alcohols in the presence of a ruthenium-containing catalyst prepared by depositing RuCl3 on a support which is either a zeolite catalyst having a Si/Al molar ratio greater than 3 or a clay. The catalyst can be regenerated by contacting it with an aqueous solution of a mineral acid. All prior preparation procedures of Ru zeolites, as thought in US 2,609,399, US 3, 963, 789, BE 837, 201 and Bull. Soc.Chim. de France, Jul/Aug 1981, p.II-288 - II-292, Part II, Sabadie et al., consist in the impregnation of a zeolite with a Ru-salt" A process for the continuous preparation of polyhydric alcohols over lumps of catalyst, made of ruthenium supported on animal coal, was disclosed in U.S. Patent 4,520,211. However, a series of two consecutive reactors was necessary. Further, it was necessary to lower the pH of the aqueous carbohydrate solution down to about 2.5 to 4.5. However, the known procedures have serious disadvantages. First of all, the catalysts used therein cannot be regenerated. Also, they do not allow the preparation of polyhydric alcohols directly from polysaccharides, and they must therefore use expensive pure monosaccharides instead of the less expensive polysaccharides. Thus, although various catalytic processes for the conversion of carbohydrates to polyhydric alcohols are known in the art, none of them shows all desirable features, e.g. single-step process combining hydrolysis and hydrogenation, substantial purity of the products, no requirement for prior activation of the feedstocks. There is accordingly a need in the art for an improved process which would possess all these characteristics. An object of the invention is to provide a process for the production of substantially pure polyhydric alcohols. A further object of the invention is to provide a catalytic process for the conversion of polysaccharides to polyhydric alcohols, wherein the catalyst may be regenerated. Still another object of the invention is to provide a process for the production of polyhydric alcohols in one step directly from water-insoluble polysaccharides. According to the present invention, there is provided a single-step process for the production of a polyhydric alcohol from a polysaccharide by contacting said polysaccharide in an aqueous medium with hydrogen at elevated temperature and pressure in the presence of a catalyst consisting of (i) a supported metal selected from ruthenium, copper, nickel, cobalt and their mixtures and (ii) a solid having acidic functions, which solid may or may not be identical to the support, characterized in that (a) the metal is highly dispersed by ion exchange on the support so as to be capable of adsorbing more than 0.58 molecules of CO per atom of metal and (b) the solid has sufficient acid functions so that the rate constant of hydrolysis of sucrose on the catalyst is greater than 70% of the rate constant of hydrogenation of glucose on the catalyst. Conversion of polysaccharides to polyhydric alcohols involves hydrolysis of the polysaccharide and hydrogenation of the monosaccharide thus produced. Known processes have heretofore been limited to starting materials which are readily hydrolysable to monosaccharides; these previously known processes have further been limited to multi-step operation, wherein the hydrolysis and the hydrogenation are to be carried out in different steps. In contrast with the prior art, the present process is a single-step process, which may also be used to produce polyhydric alcohols from high molecular weight polysaccharides such as cellulose and insoluble starch. The process of the invention represents a significant improvement over known prior art (U.S. Patents 3,963,788, 3,963,789, 4,072,628 and 4,520,211 and Belgian Patent 837,201) since it is the first effective procedure that allows the one-step conversion of natural feedstocks in a reduced reaction time in the same conditions of conversion of monosaccharides. Another advantage of the invention is that the occurrence of by-products and the degradation of the catalyst are both negligible under the reaction conditions used. Further, no purification is required, whether before the reaction or after the reaction (except for the removal of the catalytic material, e.g. by a simple filtration). The importance of the process of the invention lies in the fact that polyhydric alcohols as D-glucitol and D-mannitol can be obtained easily and with high purity from cheap starting materials such as starch. Polysaccharides are hydrolyzed to their basic monosaccharide (or monosaccharides) whose aldehyde or ketone groups are then hydrogenated to hydroxyl groups to produce the corresponding polyhydric alcohol or alcohols. The nature of the products is known in the art and need not be further described. The catalyst is prepared by depositing a metal selected from ruthenium, copper, nickel, cobalt and their mixtures in finely divided form onto a suitable carrier material, using ion exchange. The Applicants have found that, in order to achieve the objects of the invention, it is essential that the metal present on the support be highly dispersed so as to be capable of adsorbing more than 0.58 molecules of CO per atom of metal. Chemisorption measurements are conventional in the art to evaluate the dispersion of metals on supported metal catalyst. CO chemisorption on supported metal catalyst, as herein construed, is measured by a flow method in a modified gas chromatograph provided with a thermal conductivity detector. The injector and detector temperatures are maintained at 523 K. The catalyst is contained in a metal microreactor of approximately 5 mm inner diameter and 30 mm length, which replaces the original column. The catalyst is held in place by means of quartz wool. Prior to a chemisorption measurement, the sample is first flushed at room temperature during 10 min. with helium. The gas is changed to hydrogen, first at room temperature during 10 min., then at a temperature increasing from 298 K to 423 K at a rate of 6K min-1 and maintained at 423 K during 14 minutes. Finally, the catalyst is treated in flowing helium at 423 K during 3 hours and the sample cooled to room temperature. Chemisorption measurements are made by injecting 1 ml pulses of 3% CO in He through 0.4 ml of catalyst sample at 298 K until CO is fully eluted. The volume of adsorbed gas is obtained by measuring the difference between the areas of the eluted and injected pulses. The flow rate used throughout the sample conditioning and the chemisorption determinations is of 27 ml min-1. Among the various known techniques for preparing supported metal catalyst, like impregnation, ion exchange or vapor deposition, the Applicants have found that ion exchange with amine complex salts allow to obtain highly dispersed supported metals, so as to be capable of adsorbing more than 0.58 molecule of CO per atom of metal. It has indeed been observed that the preparation method influences the catalytic properties, and that said properties are best evidenced by chemisorption measurements. As known in the art, the supported metal catalyst is obtained from the ion exchanged material by successively washing said material, drying it, and heating it under a flow of hydrogen at a temperature slowly increasing up to from 423 to 773 K, preferably not above 623 K. During this activation procedure, the amine complex salt is decomposed, and the metallic ions are reduced to the metal state. Once activated, the supported metal catalyst may be exposed to air without any loss of properties. The second component of the catalyst used in the process of the invention is a solid having sufficient acid functions so that the rate constant k1 of hydrolysis of sucrose on the catalyst is greater than 70% of the rate constant of hydrogenation k₂ of glucose on the catalyst. The rate constant k₁ of hydrolysis of sucrose, as herein construed, is determined in aqueous solution, at a temperature of 423 K, under a pressure of 1.79 MPa, under such conditions that the initial weight ratio of sucrose : acid solid is of 50, and when the sucrose concentration equals 30% of its initial value. The rate constant k₂ of hydrogenation of glucose, as herein construed, is determined in aqueous solution, at a temperature of 423 K, under a pressure of 1.79 MPa, under such conditions that the initial weight ratio of D-glucose : metal is 1000:1, and when the D-glucose concentration equals 30% of its initial value. Preferably, the rate constant k₁ of hydrolysis of sucrose on the catalyst should be greater than about 0.006 s⁻¹. If the support is different, there may be used as support suitable carrier materials which have no adverse effect on the hydrolysis reaction nor on the hydrogenation reaction, such as aluminium oxide, silica gel, zeolites, and molecular sieves. The weight ratio between the two components of the catalyst is not a very important parameter, as long as the ratio k₁ : k₂ is greater than 7:10. It is preferred to use approximately equal weights of supported metal and of solid having acid functions. The rate constants k₁ and k₂ may be determined on the separate components, providing that the ratio k₁/k₂ is corrected for the weight ratio of the components. If the support is the solid having acidic functions, the solid having acidic functions may be selected from silica-aluminas, silica-magnesia, silica-titania and acidic zeolites of natural or synthetic origin. Zeolites are ordinarily synthesized in the sodium form and other metallic ions or ammonium can be introduced into the zeolite by ion exchange, as is well known in the art. Zeolites in the hydrogen form can be obtained by decomposition of the ammonium form at high temperature, according to methods known in the art. The structure of zeolites is discussed extensively in D.L. Breck "Zeolite Molecular Sieves", published by John Wiley and Sons, New York, 1974. A comprehensive review of zeolite catalysts is contained in an article by J. Turkevitch, Catalysis Reviews, 1 , 1-35 (1967). The zeolites are crystalline aluminosilicates in which the aluminum, silicon, and oxygen atoms are arranged in a rigid three-dimensional network having internal cavities of molecular size and pores of uniform size which provide access to these cavities. The crystal network includes SiO₄ and AlO₄ tetrahedra; the negative charge on the latter is balanced by cations (e.g. metal ions, ammonium ions, or hydrogen ions). The crystal structure of zeolites has been discussed extensively in the literature and will not be discussed at length here. Whenever a zeolite is used as support, it should have intermediate pore sizes and a three-dimensional network of channels, in order to allow for the obtention of a high metal dispersion thereon. One category of zeolites having said properties is the faujasite-type of zeolites, which is preferred as support having acid functions. Faujasite type zeolites are characterized by a silica/alumina molar ratio of at least about 3, and effective pore size of at least about 8 nm in the hydrogen form, and a three-dimensional network of channels. Examples of catalyst of this type are Ultrastable Faujasite Y (hydrogen form), commerically available from W.C. Grace and Co, zeolite LZY-52 form available from Linde Division of Union Carbide Corporation, zeolite ZSM-3 described by Kokotailo and Ciric in Advances in Chemistry Series 101 (1971) p.108, and ZSM-20 disclosed in U.S. patent 3,972,983. Many other zeolites in the hydrogen form may be used as solid having acidic functions, such as HZSM-5, H-Beta or H Mordenite. They do not present the characteristics which would allow a high metal dispersion thereon, and they may thus not be used as suitable carrier for the deposited metal. As suitable polysaccharide starting material for the process of the invention, there may be cited the disaccharides such as sucrose, maltose, lactose and cellobiose, the oligosaccharides such as raffinose and the polysaccharides as insuline or starch, preferably corn starch, or degradation products of starch or cellulose. The present process uses an aqueous reaction medium. The initial polysaccharide concentration is usually of from 10 to 80 wt%, preferably of from 25 to 60 wt %. Suspensions may also be used when the starting material is not readily soluble. The amount of catalyst to be used in the process of the invention may vary over a wide range and will depend upon the particular catalyst, carbohydrate, temperature and pressure which are employed in the process. In general, catalyst concentrations range from 0.04 to 8.0 wt % of metal based on the initial weight of polysaccharide, preferably from 0.04 to 2.0 wt % when ruthenium is selected or from 0.2 to 8.0 wt % when copper, nickel or cobalt is selected. When ruthenium is used, the catalyst concentration should most preferably be of from 0.04 to 0.12 wt % for discaccharides and from 0.08 to 0.3 wt % for higher polysaccharides. The temperature and pressure used in the process of the invention may vary over wide ranges. The process may be carried out at temperatures from 348 to 523 K, preferably from 373 to 443 K for disaccharides and from 428 to 483 K for polysaccharides. The hydrogen pressure should be in excess to about 1 MPa to ensure adequate contact with the carbohydrate and to achieve rapid hydrogenation. The time of reaction will depend upon the specific starting material concentration, the specific catalyst used, pressure and temperature. Usually, the time of reaction is of about 30 to 180 minutes, some reactions are to be continued for longer periods of time to ensure complete hydrolysis and hydrogenation, in which case it is preferable to carry out the process at a temperature not exceeding about 433 K. The reactants may be added to the reaction chamber in any suitable manner or in any suitable order. It is preferred to add the catalyst to the aqeuous solution or suspension of the carbohydrate and then add the hydrogen under pressure and commence heating the mixture to the desired temperature. The reaction is carried out in any suitable type of apparatus which enables intimate contact of the reactants and control of the operating conditions and which is resistant to the high pressures involved. The process may be carried out in batch, semi-continuous, or continuous operation. Batch operation in a conventional autoclave gives excellent results. Upon completion of the reaction, the catalyst is removed by centrifugation, filtration or decantation, and the polyhydric alcohol may be separated from the filtrate by any suitable means, such as crystallization, solvent extraction or evaporation. The catalysts used in the process of the invention are highly resistant to deactivation, thereby allowing prolonged use of said catalyst without reactivation. It has been found that the catalyst used in the process of the invention may be used for the one-step batch conversion of starch in up to about ten consecutive hydrogenation runs before reactivation is required. For disaccharides this reactivation can be made even less frequently. Reactivation is made in a similar manner to activation; thus the catalyst are washed till carbohydrate-free, dried at room temperature, and heated under a flow of hydrogen at a temperature slowly increasing up to a value of from 423 to 773 K, preferably not above 623 K. The invention will now be described further by way of the following examples. Examples 1 to 5 a) Preparation of Ru on acid ultrastable Y Zeolite (HUSY) Zeolite NaY LZY-52, powder was obtained from Union Carbide Corporation. Ultrastabilization of zeolite NaY was done as follows. It was first exchanged with a 0.1 M aqueous solution of NH₄Cl in a 100-fold excess w.r.t. the cation exchange capacity (CEC). The (NH₄-Na)Y zeolite thus obtained was washed till Cl-free and found to be exchanged for 70% of the CEC. This material was then dried at 320 K and equilibrated in an atmosphere of 80% humidity (over a saturated NH₄Cl aqueous solution). This sample was calcinated for 12 hours in a furnace preheated at 723 K. This calcined (NH₄-Na)Y sample was then exchanged again with NH₄⁺ ions, dried, equilibrated in moisture and calcined a second time in a furnace now preheated at 1073 K. After a third NH₄⁺ exchange a sodium-free material is obtained which is denoted as HUSY. Ru-zeolite was prepared by ion exchange with Ru³⁺-hexamine. The ion exchange was carried out with 593.6 ml of a 0.05 M aqueous solution of Ru(NH₃)₆Cl₃ for 10 g of HUSY. The ion exchanged materials were washed till chloride free and dried at room temperature. Activation of the catalyst was performed by heating it at about 2 K/min. to about 673 K, under a flow of hydrogen. Thus the Ru-amine complex was decomposed and the Ru (III) reduced to the metal state. The catalyst contained 3% Ru with a Ru dispersion of 0.73 as measured by the molar ratio of adsorbed CO on Ru (according to the hereabove described method). The ratio k₁/k₂ (as hereabove defined) was of 0.91. b) Simultaneous hydrolysis and hydrogenation of corn starch 150 ml of an aqueous suspension of corn starch was loaded in a 600 ml Parr autoclave, and the catalyst, prepared as hereabove described, was added. After closing and purging the autoclave, it was heated under hydrogen pressure while stirring the mixture at 1000 rpm. After the necessary reaction time to complete the hydrogenation given in Table I, the reactor was cooled, the reaction mixture was filtered to remove the catalyst, and the filtrate was analyzed by gas-liquid chromatography. For high pressure liquid chromatography the filtrate was injected as such. For gas-liquid chromatography the samples were silanated with trimethylsilane. The separation of the trimethylsilylethers was done from 300 K to 478 K using a temperature programming of 3 K/min. The column was a 3 m packed column with 3 % OV-225 on Gaschrom Q. As internal standard the trimethylsilylderivative of phenyl-beta-D-glucopyranose was used. In liquid chromatography the "carbohydrate" column purchased from Chrompack was used, with water as solvent at a pressure of 7.2 MPa. In this case a calibration curve was determined for each component. The operating condition and the product composition are given in Table I. Example n o 1 2 3 4 5 Operating conditions Starch concentration (%) 25 10 10 50 30 Ru/Starch (g/g) 0.0018 0.0036 0.0012 0.0020 0.0018 Temperature (K) 453 453 403 453 453 H₂ pressure (MPa) 5.52 5.52 5.52 5.52 5.52 Duration (h) 0.58 0.6 41 1 1 Product composition (%) Total alditols 99 99.9 100 99.8 97 Total hexitols 97 92 96.5 97.8 94 D-glucitol 96 87 95.0 92 92 D-mannitol 1 5 1.5 5.8 2 Xylitol 2 7.9 3.5 2 3 The sum of total hexitols and xylitol equals necessarily the total amount of alditols, as the products are expressed in mole %. When the total alditol percentage does not equal 100%, it indicates the presence of traces of D-glucose. In Example 4, the catalyst used was the catalyst recovered by filtration in Example 2. In Example 5, the catalyst had been used for 17 successive batch processes. These examples show that the process of the invention may be performed many times before the catalyst eventually requires a regeneration step. The exact amounts of D-glucitol, D-mannitol and Xylitol depend mainly on the operating conditions. Xylitol is formed by hydrogenolysis of hexitols on the Ru metal. Isomerisation of D-glucitol in D-mannitol is sometimes observed depending upon the operating conditions but its isomerisation into L-iditol was not observed. Comparative example 1 . The procedure of Example 1 was repeated with the exceptions (i) that the concentration of starch was 30%, and (ii) that the Ru on ultrastable zeolite catalyst has been made as described in Belgian Patent 837,201 (CO/Ru = 0.49). After 1 hour of reaction, less than 20% alditols were obtained. Examples 6 and 7 Aqueous solutions of (+)-sucrose (Example 6) and (+)-lactose (Example 7) were loaded in a Parr autoclave where they were simultaneously hydrolysed and hydrogenated in the presence of a Ruzeolite catalyst prepared as hereabove described. The operating conditions and the product composition are given in Table II. Example n o 6 7 Operating conditions Disaccharide (+)- sucrose (+)- lactose Concentration (%) 40 30 Ru/Starch (g/g) 0.0006 0.0009 Temperature (K) 403 433 H₂ pressure (MPa) 5.52 5.52 Duration (h) 0.8 0.38 Product composition D-glucitol 72 50 D-mannitol 28 ? Galactitol - 50 These examples confirm that the process of the invention, although particularly adapted to the one-step conversion of higher polysaccharides such as starch, may also be used for disaccharides. Example 8 A 5% Ru/HUSY catalyst was prepared according to the procedure described in Example 1(a) by using 989.4 ml of an aqueous 0.005M solution of Ru(NH₃)₆ Cl₃ for 10 g of HUSY. A 30% aqueous solution of corn starch was loaded with the catalyst (with a Ru:starch weight ratio of 0.0018) in an autoclave and stirred at 1000 rpm. After 0.8 hour of reaction at a temperature of 453 K under an hydrogen pressure of 5.52 MPa, 99.5% of alditols were formed, of which 97% were D-glucitol and 2.5% xylitol. Examples 9 to 13 a) Preparation of the dual-component catalyst Ruthenium deposited on carbon in an amount of 5 wt % is available commerically from JOHNSON MATTHEY CHEMICALS. The rate constant k₂ of hydrogenation of glucose on this 5% Ru/C material was determined to be of 0.0083 s⁻¹ (under the hereabove described conditions). The 5% Ru/C component was mixed in a 1:1 weight ratio with the following acidic zeolites : examples 9 to 11 : HUSY prepared as in Example 1(a) example 12 : H-Mordenite (obtained from NORTON Co) example 13 : HZSM-5, prepared from ZSM-5 (U.S. Patent 3,702,886) by calcination at a temperature of 673 K during 24 hours, exchange in a boiling 0.5 N HCl aqueous solution during 0.5 hour, washing till chloride free and drying at 373 K. The rate constant k₁ of hydrolysis of sucrose (as hereabove defined) on these materials are mentioned in Table III. b) Simultaneous hydrolysis and hydrogenation of polysaccharides Aqueous solutions of polysaccharides were loaded with the catalyst in an autoclave and stirred at 1000 rpm. The operating conditions and the product composition are mentioned in Table III. Example n o 9 10 11 12 13 Acidic zeolite HUSY HUSY HUSY H-Morden. HZSM-5 k₁ (s⁻¹) 0.00752 0.00752 0.00752 0.00833 0.0141 Operating conditions Polysaccharide Corn Starch (+) sucrose (+) lactose Corn Starch Corn Starch k₁/k₂ 0.91 0.91 0.91 1.00 1.70 Concentration(%) 30 30 30 30 30 Ru/polysaccharide (g/g) 0.003 0.0005 0.0002 0.003 0.003 Temperature (K) 453 423 453 453 453 H₂ pressure (MPa) 1.79 1.79 1.79 1.79 1.79 Duration (h) 1.5 0.75 1.5 2.0 1.0 Product composition (%) Total alditol 100 100 100 100 100 Total hexitols 95 100 99.3 99.6 97.7 Total pentitols 5 0 0.7 0.4 2.3

Claims: Single-step process for the production of polyhydric alcohol from a polysaccharide by contacting said polysaccharide in an aqueous medium with hydrogen at elevated temperature and pressure in the presence of a catalyst consisting of (i) a supported metal selected from ruthenium, copper, nickel, cobalt and their mixtures, and (ii) a solid having acidic functions, which solid may or may not be identical to the support, characterized in that (a) the metal is highly dispersed by ion exchange on the support so as to be capable of adsorbing more than 0.58 molecules of CO per atom of metal and (b) the solid has sufficient acid functions so that the rate constant of hydrolysis of sucrose on the catalyst is greater than 70% of the rate constant of hydrogenation of glucose on the catalyst. Process according to Claim 1, wherein the supported metal is prepared using an amine complex salt which is then decomposed. Process according to either of Claims 1 and 2, wherein the supported metal is ruthenium. Process according to any one of Claims 1 to 3, wherein the support is selected from the group comprising silica-aluminas, silica-magnesia, silica-titania, acidic zeolites of natural or synthetic origin, aluminium oxide, silica gel, and molecular sieves. Process according to any one of Claims 1 to 4, wherein the support is identical to the solid having acidic functions, said solid being a synthetic acidic zeolite having intermediate pore sizes and a three-dimensional network of channels. Process according to any one of Claims 1 to 5, wherein the solid is acid ultrastable zeolite Y. Process according to any one of Claims 1 to 6, wherein the initial polysaccharide concentration is of from 10 to 80 wt %, preferably of from 25 to 60 wt %. Process according to any one of Claims 1 to 7, wherein the catalyst concentration is of from 0.04 to 8.0 wt % of metal, based on the initial weight of polysaccharide. Process according to any one of Claims 1 to 8, wherein the temperature is of from 348 to 523 K. Process according to any one of Claims 1 to 9, wherein the hydrogen pressure is in excess of about 1 MPa. Process according to any one of Claims 1 to 10, wherein the reaction time is of 30 to 180 minutes. Process according to any one of Claims 1 to 10, wherein the reaction time is of more than 180 minutes and the temperature does not exceed about 433 K. Process according to any one of Claims 1 to 12, wherein the polysaccharide is a disaccharide. Process according to any one of Claims 1 to 13, wherein the temperature is of from 373 to 443 K. Process according to any one of Claims 1 to 13, wherein the catalyst concentration is of from 0.04 to 0.12 wt % of metal, based on the initial weight of disaccharide. Process according to any one of Claims 1 to 12, wherein the polysaccharide is formed of more than 2 monosaccharide units. Process according to any one of Claims 1 to 12, wherein the polysaccharide is starch. Process according to either Claims 16 or 17, wherein the catalyst concentration is of from 0.08 to 0.3 wt % of metal, based on the initial weight of polysaccharide.

Inventors: HINNEKENS, HERVE, JACOBS, PIERRE, Hinnekens, Hervé
Applicants: FINA RESEARCH S.A.
Application year: 1988
Main classification: C07C31
IPC codes: C07C31, C07C29, B01J29, C07C67, C07C27