COLORED MICACEOUS PIGMENTS

Abstract: Dispersed insoluble colored pigments are coated on the surface of mica and oxide-coated mica pigments by deposition in a precipitate of a polyvalent cation and ana anionic polymeric substance. The re­ sulting combination pigments have more than one color, depending on the angle of viewing.

Description: BACKGROUND OF THE INVENTION This invention deals with colored nacreous pigments and with processes for producing these pigments. Nacreous pigments produce pearl-like, metallic, and iridescent effects. A widely used type comprises muscovite mica platelets coated with a metallic oxide, such as titanium dioxide. A relatively thin titanium dioxide coating produces a pearl-like or silvery luster. Mica platelets with thicker coatings produce color, even though the components are colorless, through the phenomenon of light interference; they are known as interference pigments. The color called the reflection color, is seen most effectively by specular or mirror-like reflection, where the angle of reflection equals the angle of incidence. The reflection color is a function of optical thickness, i.e. the geometrical thickness times the refractive index, of the coating. Optical thickness of about 80 nm to about 140 nm produce reflections which may be called white, silvery or pearly; optical thickness of about 190 nm or more produce colored reflections. Combination pigments are more complex. The oxide-coated mica pigment is further coated with an absorption pigment or dye, so-called because it absorbs some portion of the visible spectrum. If the absorption colorant has the same hue as the reflection color of the oxide-mica pigment, that color is intensified and is seen over a wide range of angles; if it has a different hue, the reflection color or a color close to it is seen at the specular angle, whereas the hue of the absorption pigment is seen at other angles. In some cases, transition colors may be seen between the extremes. Thus a single pigment has more than one color. The absorption colorant coat should be uniform and should adhere firmly to the oxide-coated mica particles. In known combination pigments, the desired results are achieved by depositing the colorant or a precursor on the pigment platelets from aqueous solution. For example, U.S. 4,309,480 teaches that iron blue (ferric ferrocyanide) may be precipitated onto TiO₂-coated mica by the reaction of ferric chloride and potassium ferrocyanide in aqueous solution. Aluminum hydroxide may be precipitated after the iron blue or simultaneously with it, but it is not required for the formation of the iron blue coating. U.S. 3,951,679 shows that an Fe(II) phosphate layer may be precipitated onto mica pigments from aqueous solution and then converted in place of ferrous ferrocyanide by reaction with ferrocyanide solution, followed by oxidation in place to ferric ferrocyanide. U.S. 4,084,983 describes the formation of colored lakes on mica pigments by first depositing aluminum hydroxide on the surface from soluble reactants and the reacting with a dye in solution. Many colored pigments of very desirable properties cannot be formed from a water-soluble reactant or reactants. In the present invention, such insoluble pigment particles are dispersed in water and then deposited on the surface of the mica platelets to form continuous, adherent, and smooth colored coatings, creating a new class of combination pigments. It is an object of the present invention to make combination pigments containing absorption pigments which are not soluble in water and which cannot be formed in place from a water-soluble reactant or reactants. Examples are pigments like the phthalocyanines, quinacridones, perylenes, dioxazines, and carbon black. Although insoluble in water, these pigments can be dispersed in water. They have high color intensity, lightfastness and bleed resistance, properties which make the resulting combination pigments suitable for automotive finishes as well as for general use in paints and in plastics incorporation. They are also useful in cosmetics when cosmetically acceptable components are employed. SUMMARY OF THE INVENTION In the present invention, an aqueous dispersion of the coloured pigment containing an anionic polymeric substance, such as albumin or xanthan gum, is added to a suspension of the mica or oxide-coated mica pigment. The hydrous oxide of a polyvalent metal, for example chromium(III) or aluminum(III), is then produced by the simultaneous addition of a solution of the metal salt and of a basic solution. The dispersed pigment particles and the polymer deposit with the hydrous oxide of the polyvalent metal to form a smooth, adherent, uniform coating on the mica platelets. While not wishing to be limited to theory, it is likely that the polymer reacts with the polyvalent metal to form a complex hydrous oxide. The resulting combination pigments exhibit brilliant colour and colour play, the specific colours depending on the reflection colour of the original oxide-mica pigment and the colour of the deposited pigment. In accordance with one aspect of the present invention, therefore, there is provided a coloured micaceous pigment comprising micaceous platelets, each platelet being coated with a layer which comprises a polyvalent metal cation, an anionic polymer and a coloured pigment, characterised in that said micaceous pigment is made by combining an aqueous suspension of said micaceous platelets with an aqueous suspension of a water-insoluble coloured pigment which contains said anionic polymer, combining the resulting suspension with an aqueous solution of said polyvalent metal cation, adjusting the pH of the suspension thereby to cause precipitation of a hydroxide or hydrous oxide of said polyvalent metal cation and thereby to effect deposition of said hydrous oxide or hydroxide, the anionic polymer and said coloured pigment onto the platelets, and thereafter recovering the resulting coloured micaceous pigments. DETAILED DISCUSSION Coated mica pigments are now well known and widely used to produce pearlescent, metallic, and iridescent effects. Colourless oxides, such as TiO₂ and ZrO₂, are described as coatings for mica in U.S. 3,087,828. Coloured oxides, such as Fe₂O₃, Cr₂O₃, etc., appear in U.S. 3,087,829. Interference pigments of a colourless oxide coated on mica are of particular interest, because the colour is derived entirely from the interference effect. They make possible combination pigments with the widest range of colours: any described reflection colour is obtainable by controlling the thickness of the oxide coating, and absorption pigments of any desired colour are available for overcoating. For example, a blue-reflecting TiO₂-coated mica overcoated with a red absorption colourant appears blue at the specular angle and primarily red at other angles. If the oxide coating consists of or includes a coloured oxide, the pigment itself already has a reflection colour and an absorption colour; the latter modifies the colour of the absorption pigment overcoating. In some cases, the absorption colourant can shift the hue of the reflection colour to some extent. This factor is taken into account in deciding on the thickness of the oxide coating to be deposited on the mica. In order to utilize an insoluble absorption pigment successfully in combination pigments, the insoluble pigment must be very highly dispersed. A convenient starting point is the dry pigment or preferably an aqueous presscake of the pigment. After dilution with water or other liquid, such as alcohol, dispersion is achieved by any one of the usual techniques, such as milling, high shear mixing, or application of ultrasonic energy. The desired degree of dispersion is similar to that conventionally used in paint and coating formulations. It is preferred to add the anionic polymer prior to or during the dispersion step in order to assist the dispersion process. The polymer-absorption pigment dispersion is combined with a suspension of mica or oxide-coated mica. The pH of the resulting suspension should be in the range suitable for precipitation of the desired polyvalent cation hydroxide or hydrous oxide, generally between about pH 1 and 11, and most frequently between about pH 2 and 8. A solution of soluble salt of the polyvalent cation is then added to the suspension simultaneously with a quantity of a basic material soluble in the solution sufficient to maintain the pH in the desired precipitation range. The absorption pigment is deposited on the platelets to form a smooth, uniform, colored coating. The suspension can then be filtered, and the filter cake washed with water and dried, for example, at 120° C to produce an easily dispersible powder of the combination pigment. The anionic polymer is a necessary component in this procedure. Without it, the absorption pigment particles are likely to agglomerate during the polyvalent cation addition and do not deposit on the substrate. The procedure is effective on mica as well as oxide-coated mica and oxide-coated mica. The coatings may be of TiO₂, ZrO₂, SnO₂, ZnO, Fe₂O₃, Cr₂O₃, V₂O₅, and the hydrous form thereof. The oxide may be present in various crystalline forms, for example TiO₂ can be anatase or rutile. Combinations of oxides of two or more metals may be used. The colorless oxides allow the greatest freedom in choice of absorption colorant; the color of the colored oxides influences the choice of absorption colorant because the final absorption color is determined by the mixture of the two colors. The oxide coating typically has an optical thickness from about 80 to about 600 nm. The mica platelets are from about 3 to about 100 um in their longest direction, and from about 0.1 to 1 um in thickness. Suitable types of mica for the micaceous pigments of the invention are muscovite, phlogopite, biotite, and synthetic micas. Muscovite is the preferred natural mica because its own light color does not adversely affect the color of the absorption pigment. Absorption pigments which are water insoluble, transparent (i.e. substantially non-light scattering) and which cannot be formed in situ from a water soluble reactant(s) but which may be highly dispersed in water or water-alcohol containing anionic polymer are suitable for the invention. These include, for example, carbon black and organic pigments in the following groups: azo compounds, anthraquinones, perinones, perylenes, quinacridones, thioindigos, dioxazines, and phthalocyanines and their metal complexes. The pigments, depending on their color intensity, are used in concentration range of about 0.01% to about 30% based on the weight of mica pigment, preferably 0.1% to 10%. The useful polymers are those which are capable of precipitating with polyvalent cations at the appropriate pH values. Thus, the polymers are usually anionic, or, like proteins, have both anionic and cationic groups. Useful polymers include albumin gelatin, polyacrylamides, polyacrylic acids, polystyrene sulfonates, polyvinyl phosphonates, sodium carboxymethyl cellulose and polysaccharides such as xanthan gum, alginates, and carageenin. The polymer content is from about 0.01% to about 20%, preferably from 0.05 to 10%, based on the weight of the mica pigment. Any polyvalent cation which will form a precipitate with the polymer under given pH conditions can be used. Such polyvalent cations are employed in the form of a solution of a soluble salt. Thus, the cation can be, for example, one or more of Al(III), Cr(III), Zn(II), Mg(II), Ti(IV), Zr(IV), Fe(II), Fe(III), and Sn(IV). Suitable anions include chloride, nitrate, sulfate, and the like. The quantity of polyvalent metal ion is from about 0.01% to about 20%, preferably about 0.05% to about 10%, of the weight of the mica pigment. The preferred pH range for deposition depends on the particular cation being employed. For Al and Cr(III), it is about 4.0 to 8.0. For Zn(IV), it is about 1.0 to 4.0. The metal salt solution is usually acidic, and the pH of the suspension is maintained at the desired range by addition of a soluble base, such as sodium hydroxide, potassium hydroxide, or ammonia solution. Where the desired pH of precipitation is lower than that of the salt solution, a soluble acid, such as HCl, is added as required. The effect in each case is to deposit on the mica pigment platelets a complex of metal hydroxide or hydrous oxide and polymer which carries the particles of the absorption pigment with it, to produce a combination pigment with a smooth, adherent colored film on the platelets. After the deposition, the film can be fixed by washing and drying the combination pigment. The use of chromium as the polyvalent cation for the coating of a rutile-coated mica is of particular interest, inasmuch as chromium hydroxide imparts high resistance to weatherability stress to such pigments, as disclosed in U.S. 4,134,776. The products are suitable for exterior use in such applications as automotive finishes, roof tiles, outdoor furniture, and the like. The combination pigments of this invention have advantages over multicolor effects obtained by incorporating the mica pigment and absorption pigment separately in a paint or lacquer vehicle. No dispersion step is required for the absorption pigment, since it is already dispersed for maximum effectiveness on the mica pigment surface. The oil absorption requirement of the combination pigment is less than that of the sum of the separate pigments. The tendency of absorption pigment particles to flocculate is eliminated or greatly reduced when the particles are bound to the micaceous platelets. Also, the paint formulator has the convenience of working with fewer components because a two-color effect is achieved by a single pigment. Colors may be adjusted if desired by mixing combination pigments. In general, it is preferred to mix pigments of the same or similar reflection color, since reflection colors mix additively and color intensity is reduced when very different reflection colors are mixed. The absorption pigment components mix subtractively, and the usual pigment blending procedures are followed. The new combination pigments may be used in all the usual applications for nacreous pigments: in paints and other coatings, incorporated in plastics, and in cosmetics when the components are acceptable for this use. Furthermore, the specific colors of the combination pigment may be modified, if desired, by the addition of other absorption colorants to the formulation in the conventional way. The preparation of the combination pigments are best illustrated by the following non-limiting examples: EXAMPLE 1 Quinacridone red on blue-reflecting anatase-coated mica. An aqueous presscake of quinacridone red (Sunfast Red 19, Sum Chemical Co., 23.7% pigment) was diluted to 0.50% pigment with water. To 250 g of this suspension was added 0.1 g xanthan gum (Kelzan, a microbiolal polysaccharide containing glucuronic acid, Kelco Division). Ultrasonic energy was applied by means of a Sonifier® Model 350 (Branson Sonic Power Co.) for 30 minutes to disperse the pigment. The mica containing pigment substrate was 50 g of blue-reflecting TiO₂-coated muscovite mica (most platelets about 5-50 um long, average thickness about 0.5 um, 46% TiO₂), suspendend by stirring in 400 g of water. The pH value of the suspension was 9.0, and was adjusted to 6.0 with 0.1N HC1. This suspension was combined with quinacridone red dispersion; there was no significant pH change. A solution of 2.64 g. CrCl₃.6H₂O in 165 g water was added at a uniform rate in 100 minutes while maintaining the pH at 6.0 with 3.5% (by weight) NaOH. Examination of the resulting suspension by optical microscope at 1000x magnification showed that all the red pigment was deposited on the micaceous platelets to form a smooth, uniform red coating. The suspension was filtered, and the filter cake was washed with water. The filtrate and washings were clear and colorless. The filter cake was dried at 120° C for 1 hour. Incorporated at 3% by weight in a paint vehicle of the following composition: Acrylic resin thermosetting, 50% Nv 51.78 Melamine, 60% NV 16.83 Solvent, xylene 30.29 100.00 the combination pigment yielded a two-color paint which, coated on a surface, had a blue highlight on a red background. EXAMPLE 2 Phthalocyanine blue on pearl-reflecting rutile-coated mica. An aqueous presscake of phthalocyanlne blue (Sunfast Blue 15:3, Sun Chemical Co., 34.6% pigment) was diluted to 0.50% pigment with water. To 250 g of this suspension was added 0.1 g albumin. Dispersion was achieved as in Example 1. The pigment substrate was 50 g of pearl-reflecting TiO₂-coated mica pigment (dimensions as in Example 1; composition 73.8% mica, 26% TiO₂, 0.8% SnO₂) suspended by stirring in 400 g of water. This pigment has a white-pearl of silvery appearance. The pH value of the suspension was 9.0, and was adjusted to 6.0 with 0.1N HCl. This suspension was combined with the phthalocyanine blue dispersion. A solution of 0.80 g CrCl₃.6H₂O in 50 g water was added at a uniform rate in 30 minutes while maintaining the pH at 6.0 with 3.5% (by weight) NaOH solution. The suspension was filtered, and the filter cake was washed with water. The filtrate and washings were clear and colorless. The filter cake was dried at 120° C for 1 hour. The resulting combination pigment, used in the paint of Example 1, produced a silvery highlight on a blue background. EXAMPLE 3 Phthalocyanine blue on bronze-reflecting FE₂O₃-coated mica. Phthalocyanine blue was dispersed by the technique of Example 1, except that gelatin was used as the polymer in place of xanthan. The substrate was a bronze-reflecting Fe₂O₃-coated mica (32% Fe₂O₃) which itself had a yellow absorption color. The polyvalent cation solution was 2.5 g AlCl₃.6H₂O in 50 g water. The pH was kept constant at 5.5 during the addition of the aluminum solution by the simultaneous addition of 3% NH₃ solution. The combination pigment had a bronze highlight on a green background, the latter resulting from the color blending of the yellow Fe₂O₃ with phthalocyanine blue. EXAMPLES 4-9 The procedure of Example 1 was followed in Examples 4-9, with the various absorption pigments, polymers, substrates, polyvalent cations and precipitation pH values noted in the following table. EXAMPLES 10-11 The effect of the combination pigment can be illustrated by its use in an automotive paint. A suitably primed curved metal panel was sprayed with a light gray automotive paint base coat. The paint of Example 2 was sprayed over it. The panel had a silver highlight on a blue background. The panel exhibited excellent light and moisture stability. The pigment of Example 9 was formulated in a similar manner and sprayed over a white base coat. A clear automotive topcoat was then applied. The finish had a gold highlight on a blue background. In automotive two-coat and three-coat systems, the combination pigment may be used in the bottom coat, middle coat, or top coat. Other uses will be evident to those skilled in the art.

Claims: A coloured micaceous pigment comprising micaceous platelets, each platelet being coated with a layer which comprises a polyvalent metal cation, an anionic polymer and a coloured pigment, characterised in that said micaceous pigment is made by combining an aqueous suspension of said micaceous platelets with an aqueous suspension of a water-insoluble coloured pigment which contains said anionic polymer, combining the resulting suspension with an aqueous solution of said polyvalent metal cation, adjusting the pH of the suspension thereby to cause or allow precipitation of a hydroxide or hydrous oxide of said polyvalent metal cation and thereby to effect deposition of said hydrous oxide or hydroxide, the anionic polymer and said coloured pigment onto the platelets, and thereafter recovering the resulting coloured micaceous pigments. A pigment as claimed in claim 1, characterised in that said metal cation is selected from aluminium, chromium, titanium, zinc, magnesium, zirconium, iron and tin cations. A pigment as claimed in claim 1 or claim 2, characterised in that said cation is a chromium cation. A pigment as claimed in claim 1 or claim 2, characterised in that said cation is an aluminium cation. A pigment as claimed in any preceding claim, characterised in that said mica platelets are coated with an oxide. A pigment as claimed in any preceding claim, characterised in that said mica platelets are coated with a titanium (IV) oxide. A pigment as claimed in any of claims 1 to 5, characterised in that said mica platelets are coated with an iron (III) oxide. A pigment as claimed in any preceding claim, characterised in that said anionic polymer is selected from albumin, gelatin, polyacrylic acid, alginate and polysaccharide. A pigment as claimed in any preceding claim, characterised in that said water-insoluble colour is selected from phthalocyanine, quinacridone, dioxazine and carbon black. A paint comprising a paint vehicle and a coloured micaceous pigment as claimed in any preceding claim. A method of preparing a coloured micaceous pigment, which method comprises the steps of:- combining an aqueous suspension of micaceous platelets with an aqueous suspension of a water-insoluble coloured pigment containing an anionic polymer; combining the resulting suspension with an aqueous acidic solution of a polyvalent metal cation which forms a precipitate with said anionic polymer at a given pH and a quantity of a pH adjustment agent to provide said given pH; and thereafter recovering the resulting coloured micaceous pigment. A method as claimed in claim 11, characterised in that said pH adjustment agent is a base. A method as claimed in claim 11 or claim 12, characterised in that said pH adjustment agent is sodium hydroxide. A method as claimed in any of claims 11 to 13, characterised in that said cation is selected from aluminium, chronium, titanium, zinc, magnesium, zirconium, iron and tin, further characterised in that said platelets are mica or mica coated with an oxide platelets. A method as claimed in any of claims 11 to 14, characterised in that said ionic polymer is selected from albumin, gelatin, pelyacrylic acid, alginate and polysaccharide, and further characterised in that said water-insoluble colour is selected from phthalocyanine, quinacridone, dioxazine and carbon black. A method as claimed in any of claims 11 to 15 characterised in that said cation is an aluminium or chromium cation, said platelets are mica platelets or mica platelets coated with titanium oxide or ferric oxide, and said given pH is about 4 to about 8. A method as claimed in any of claims 12 to 16, characterised in that said base and acid solution are simultaneously added to said resulting suspension. A method as claimed in any of claims 11 to 17, characterised in that the quantities of colour material, anionic polymer and polyvalent cation employed are given as follows: Coloured Material: 0.01% - 30% Anionic Polymer: 0.01% - 20% Cation: 0.01% - 20% wherein the percentages are based on the weight of said platelets.

Inventors: ARMANINI, LOUIS
Applicants: THE MEARL CORPORATION
Application year: 1988
Main classification: C09C1
IPC codes: A61K8, C09B67, C09B63, C09C1, A61Q1, C09D7