Preform for, and method of forming hot fill container

Abstract: A blow molded container which is formed of a polyester resin which has formation and shape characteristics wherein it may be hot filled with a liquid at a temperature on the order of 180°-185°F. with a maximum volumetric shrinkage of no greater than 1 percent. The container is formed from a specially configurated injection molded preform which is initially stretched axially only on the order of 25 percent, after which the preform is inflated and blow molded within a blow mold to a configuration which resists vacuum collapse or paneling of the body.

Description: This invention relates to a preform for, and a method of forming, a hot fill plastics container , and more particularly a container which is blow molded of a polyester resin and for the most part is highly biaxially oriented, but has a non-oriented neck finish for receiving a closure. Such a container must receive a hot fill product with a minimum of shrinkage and distortion. In the past there have been developed wide mouth containers wherein the closure receiving portion or neck finish is highly biaxially oriented. Further, the neck finish may be subjected to thermal crystallization. Such a container and the method of forming the same is disclosed in US-A-4,618,515. This patent, in turn, is an improvement on an earlier US-A-4,496,064. It is now desired to form containers having a non-oriented injection molded neck finish which is relatively small in diameter and which container is particularly adapted for the packaging of liquids, which liquids must be placed into the container while hot to provide for adequate sterilization. One of the problems of forming a container with an injection molded neck finish is that immediately adjacent to the neck finish is a neck to body transition which normally has low biaxial orientation. This region tends to distort to a high degree when exposed to temperatures above 71°C (160°F). In the past this distortion problem has been solved by increasing the temperature resistance of PET through thermal crystallization since the degree of orientation is not adequate to yield sufficient strain crystallization to increase the temperature resistance of PET in this region. One of the features of this invention is to solve that problem. Another problem in the art is the tendency of the body of the container to shrink such that the overall shrinkage of the container is in excess of 1 percent which is the present desired maximum permissible shrinkage. JP-A-57-8123 discloses a preform for forming a blow moulded container having a neck to body transition between a neck finish and a body portion, the neck to body transition comprising a minimum cross-section region adjacent the neck finish and a portion flaring in increasing thickness from that region to the body portion and a method of making a blow moulded container from that preform. FR-A-2443915 discloses a method of blow moulding a biaxially oriented container by first axial stretching followed by blow moulding, and where the shoulder and bottom portions of the preform have a reduced wall thickness so they undergo preferential axial elongation. EP-A-0033745 discloses a hot fill polyester container having a succession of flat vertical surfaces and ridges wherein the surfaces curve inwardly to absorb any negative pressure in the bottle. The present invention provides a preform for forming a blow moulded hot fill container, the preform being formed of a polyester resin and including a neck finish portion, a neck to body transition, a body portion and a base portion, the neck finish portion including a flange immediately adjacent to the neck to body transition, the neck to body transition including a first portion adjacent to the flange, and a second portion adjacent to the first portion, characterised by the first portion flaring in increasing thickness between the second portion and the flange, the second portion defining a minimum cross-section region of the neck to body transition, which miminum cross-section has a thickness less than that of the body portion and being spaced from the flange, and a third portion between the second portion and the body portion, the third portion flaring in increasing thickness towards the body portion. The present invention further provides a method of forming a blow moulded hot fill container, the method comprising the steps of:- (a) providing a preform including a neck finish portion, a neck to body transition, the neck finish portion including a flange immediately adjacent to the neck to body transition, a body portion and a base portion, the neck to body transition having a portion thereof of minimum cross-section, the said portion having a thickness less than that of the body portion; characterised by (b) heating the neck to body transition, the body portion and the base portion to a blow moulding temperature; (c) placing the heated preform in a blow mould; (d) axially elongating the preform thereby causing preferential thinning of the minimum cross-section portion of the preform relative to the remainder of the neck to body transition, wherein during axial elongation the said portion is caused to neck down and assume a radially inwardly directed bowed configuration so as to undergo a greater stretching in the hoop direction during subsequent blow moulding; and (e) blow moulding the elongated preform to form the container. In accordance with the preferred embodiments of this invention, it has been found that through the application of specific process techniques, the shrinkage of the container, when hot filled with a liquid, will be no greater than 1 percent. Further, the paneled body may be so configurated wherein a conventional label may be wrappped around the body and be sufficiently supported by the body notwithstanding the provision of the vacuum panels. With the above and other objects in view that will hereinafter appear, the nature of the invention will be more clearly understood by reference to the following detailed description, the appended claims, and the several views illustrated in the accompanying drawings. Figure 1 is an elevational view with parts broken away of a preform formed in accordance with this invention. Figure 2 is a schematic sectional view showing the preform of Figure 1 initially being placed in a blow mold. Figure 3 is another schematic vertical sectional view similar to Figure 2 and shows a mechanical axial elongation of the preform. Figure 4 is yet another schematic vertical sectional view showing the previously axially elongated preform being blow molded to match the configuration of the blow mold. Figure 5 is an enlarged fragmentary sectional view of that portion of the preform identified in Figure 1. Figure 6 is an enlarged fragmentary vertical sectional view of that portion of the preform identified in Figure 1. Figure 7 is an enlarged fragmentary sectional view of the upper portion of the preform as shown in Figure 5 after the preform has been stretched in the manner shown in Figure 3. Figure 8 is an enlarged fragmentary sectional view of the lower part of the preform shown in Figure 6 after the axial elongation of the preform as shown in Figure 3. Figure 9 is an elevational view with parts broken away and shown in section of a container formed in accordance with this invention in the blow mold as shown in Figure 4 and having a label applied to the body thereof. Figure 10 is a horizontal sectional view taken generally along the line 10-10 of Figure 9 and shows further the details of the container and the associated label. This invention starts with a special preform 10 which is best illustrated in Figures 1 and 5-8. The preform 10 is injection molded of a polyester resin with particular reference being made to PET (polyethylene terephthalate). Basically speaking, the various portions of the preform 10 may be identified as including a base portion 12, a body portion 14, a neck finish portion 16 and a neck to body transition 18. Referring now to Figure 5, it will be seen that the upper part of the preform 10 is illustrated in detail. First of all, the illustrated neck finish portion 16 is in the form of a conventional neck finish which may include external threads 20 for receiving a closure, a locking bead 22 for engagement by a closure tamper indicating ring or band, and a lower flange 24. Immediately below the flange 24 is the neck to body transition 18. It starts with an internal thickening to define a seat 26 for receiving, for example, a blow nozzle in seated engagement. Immediately below the seat, the transition may include a cylindrical part 28. Below the cylindrical part 28, the transition 18 downwardly tapers in thickness externally as at 30 terminating in a further cylindrical part 32 of minimal cross section. Below the cylindrical part 32, the transition 18 flares both internally and externally as at 34 to join the greater thickness body portion 14. Referring now to Figure 6, it will be seen that the base portion begins at the lower end of the body 14 with a radius part 36 which joins a frustoconical part 38 to the body portion 14. The frustoconical part, in turn, carries a part spherical bottom 40 which tapers in thickness from the frustoconical part 38. It is to be understood that the preform 10 is formed by injection molding and when presented to the blow molding apparatus is at room temperature. A preform, in a normal blow molding operation, is heated by a series of quartz heaters which results in the heating of the outer surface of the preform to a higher temperature than the inner surface. On the other hand, radio frequency heating has been utilized with the result that the inner surface of the preform is heated to a higher temperature. Hybrid heating utilizing a combination of quartz heaters and radio frequency heaters has been utilized in the past to obtain a uniform temperature throughout the wall of the preform. Such a heating process is disclosed in US-A-4,407,651. More recently it has been found that if the average preform temperature is increased to 107°C (225°F), as compared to the permissible average temperature in the 93°-99°C (200°-210°F) range permissible with quartz heating and the 99°-104°C (210°-220°F) range permissible with radio frequency heating, shrinkage of a biaxially oriented PET container is reduced to 2 percent or less and by increasing the average temperature of the reheated preform at the time of stretch blowing to as high as 127°C (260°F), the container shrinkage is reduced to on the order of less than 1 percent. In accordance with this recent development in reheating of preforms, which is the subject of a pending U.S. application, the preform 10 will be reheated first utilizing a quartz oven or like quartz heater with this first reheating treatment resulting in the outside surface temperature of the preform rising to on the order of 116°C (240°F) while the inside surface of the preform is only slightly heated to a temperature on the order of 49°C (120°F) The temperature of the center of the body wall of the preform is only slightly greater than the inside surface temperature and is on the order of 60°C (140°F). The initial reheating time is on the order of 14.5 seconds. After the first quartz reheating, the reheating is discontinued and the preform is permitted to equilibrate for a period of time on the order of 5 seconds. The temperature of the outside surface of the preform body continues to increase to a temperature on the order of 121°C (250°F) and then begins to cool down to a temperature on the order of 110°C (230°F). At the same time, the temperature of the center of the preform body remains generally constant while the temperature of the inside surface of the preform body increases gradually to a temperature on the order of 57°C (135°F), the temperature of the inside surface of the preform body approaching that of the center of the preform body. Thereafter, it is preferred that further reheating of the preform be also by way of a quartz heater for a reheating period. The time of this further quartz reheating is on the order of 12.5 seconds and during this second period of quartz reheating, the temperature of the exterior surface of the preform body continues to rise above the temperature of the center of the preform body and the inside surface of the preform body. The exterior surface temperature rises to on the order of 177°C (350°F) while the inside surface temperature slowly gradually rises to a temperature on the order of 82°C (180°F) and the temperature at the center of the preform wall slowly rises at a slightly greater rate to a temperature on the order of 104°C (220°F). After the second quartz reheating, once again the temperature of the exterior surface of the preform body is much greater than that of the interior surface and the temperature at the center of the preform body has also gradually increased above that of the interior surface of the preform body. The preform body is immediately thereafter further reheated by way of radio frequency heating. While the temperature of the outside surface of the preform body rises only slightly during the radio frequency heating, the heating of the inside surface of the preform body very rapidly increases from the temperature generally on the order of 71°C (160°F) to a temperature slightly greater than 149°C (300°F). The time of radio frequency heating is on the order of 2 seconds. During this time there is only a minor increase in the temperature of the preform body at the center of the cross section thereof to a temperature on the order of 116°C (240°F). Thus the temperature of the center of the preform body cross section is the lowest and the temperatures of the inside surface and outside surface are greater. At this point, the application of external heat to the preform is stopped and the preform is directed into a blow mold, as will be discussed hereinafter, and blow molding steps are initiated with there being a total lapse of time on the order of 6 seconds. During these 6 seconds, there is a second equilibration of the preform. During the second temperature equilibration, the temperature of the outside surfaces of the preform body will rapidly decrease to a temperature on the order of, but below 138°C (280°F). At the same time, the temperature on the inside surface of the preform body will continue to increase and then taper off to a temperature on the order of 177°C (350°F). In a like manner, the temperature of the preform at the center of the body cross section will rise and then taper off at a temperature on the order of 127°C (260°F). It will thus be seen that the temperature at the center of the cross section of the preform body is still the lowest, but the temperature of the outside surface is only slightly greater. Inasmuch as crystallization is a factor of temperature and time and since the time during which surface crystallization may occur after reheating of the preform to its maximum temperature is reduced, the desired high reheat temperature may be obtained in accordance with this reheating method without the undesired surface crystallization. It is known to utilize a stretch rod to axially elongate a preform within a blow mold to assure the complete axial elongation of the preform. However, normally a similar rod is utilized solely for the purpose of maintaining the preform in a centered relationship with respect to the blow mold as the preform is inflated. However, in accordance with this invention, it is proposed to utilize the normal centering rod initially as a stretch rod, but prior to the introduction of a blowing gas into the preform. Thus, as is schematically shown in Figure 2, the preform 10, duly heated in the manner described above, is placed within an open split blow mold, generally identified by the numeral 42 in a conventional manner. After the blow mold 42 has been closed, as shown in Figure 3, instead of immediately beginning the inflation of the preform, the customary centering rod 44 is directed down into the preform 10 and engages the bottom part 40. The rod 44 is utilized to elongate the preform on the order of 25 percent, as is shown in Figure 3. The results of this elongation of the preform 10 are best shown in Figures 7 and 8. Since the reheating of the preform 10 stops on the order of 2mm below the flange 24, and since the preform is supported against axial movement within the blow mold by the flange 24, there is no deformation or elongation of the neck finish portion 16. On the other hand, since the central part of the neck to body transition 18 is of minimum cross section, it will be seen that there will be considerable elongation of the neck to body transition 18. This will occur primarily in the cylindrical part 32 but will also occur partially within the downwardly tapering portion 30 and the downwardly flaring portion 34. Further, and most particularly, it will be seen that when the transition 18 is axially elongated, it will also neck down so as to assume a radially inwardly directed bowed configuration thus in effect reducing the diameter of the central part of the transition 18. Because of the radially inwardly directed bowing of the transition 18, it will be seen that in the blow molding of the preform 10 within the blow mold 42 there will be a greater stretching of this portion of the preform in the hoop direction. With reference to Figure 8, it will be seen that since the base portion 12 of the preform 10 is also heated to a high temperature, when it is engaged by the stretch rod 44, its resistance to thinning will not be as great as that of the body 14 so that there will be an elongation of the base portion 12 as is best shown in Figure 8. This elongation will be primarily in the radially outer portion of the body part 40 and in the frustoconical part 38 with the result that there will be a newly formed body part 46 which is generally hemispherical together with a cylindrical part 48 in accordance with the diameter of the stretch rod 44. Finally there will be an upwardly flaring generally frustoconical part 50 which joins the cylindrical part 48 to the body 14 by way of a curved part 52. The preform 10, having been elongated on the order of 25 percent, is now ready for the introduction of a blow gas so that the preform 10 may be inflated in the customary manner to match the configuration of the blow mold 42. If desired, during the inflation of the stretched preform 10, the stretch rod 44 may be permitted to follow the axial elongation of the preform during inflation so as to make certain that the base portion 12 of the preform remains centered relative to the blow mold. The inflation of the preform 10 within the blow mold 42 results in the formation of a container in the form of a bottle generally identified by the numeral 54. It is to be understood that the shape of the container or bottle 54 is also critical in the hot fill shrinkage thereof. As will be apparent, the bottle 54 will have a neck finish which is identical with the original neck finish 16 of the preform 10 including the flange 24 and a portion of the preform immediately below the flange which was not heated, as previously described. This portion is generally in accordance with the previously described part 28 of the preform. The bottle 54 also includes a downwardly and outwardly sloping shoulder portion 56 which is formed from the previously stretched neck to body transition portion 18. The shoulder portion 56 in conventional container constructions is generally of a low orientation and is gradually formed during the inflation of the preform. However, inasmuch as the shoulder portion 56 is defined by that part of the preform which was very rapidly mechanically stretched followed by the inflation of the preform, the shoulder portion 56 has a high strain crystallization. In accordance with the design configuration of the illustrated bottle 54, the shoulder portion 56 is connected by a radius 58 to an upper body portion 60 which flares slightly outwardly and downwardly. The upper body portion 60 terminates in a radially inwardly directed rib 62 which, in turn, is connected to a generally cylindrical main body portion 64. The main body portion 64 includes upper and lower cylindrical bands 66, 68 with the body portion 64 between the bands 66, 68 including a plurality of radially inwardly recessed vacuum pressure panels 70. Each pressure panel 70, as is best shown in Figure 9, is of a vertically elongated rectangular configuration with rounded corners and is generally chordal in configuration. Each pressure panel 70 is reinforced against deformation by a plurality of transverse horizontally extending radially recessed ribs 72 which are also of an elongated rectangular outline, but the elongation being in the horizontal or circumferential direction. Adjacent pressure deformable vacuum panels 70 are separated by a vertically elongated land area 74. Each land area 74 extends between the bands 66, 68 and is reinforced by a vertically extending, radially inwardly directed rib 76. The bottle 54 also includes a base 78 which includes a ribbed recessed bottom 80 which is joined to the body 64 by a rounded base portion 82. The ribbed bottom, which is best shown in Figure 10, may include five circumferentially spaced, radiating downwardly directed ribs 84 which are defined by the base configuration of the blow mold 42. As is best shown in Figure 9, the bands 66, 68 are recessed radially inwardly a slight distance with respect to the lower part of the rib 62 and the rounded portion 82 of the base portion 78. This permits a conventional, low cost, full wrap label 86 to be applied to the body portion 64 in a protected position. As is dearly shown in Figure 10, the label 86 bridges the recessed pressure deformable vacuum panel 70 so as to give the bottle 54 the appearance of one wherein the body portion 64 is cylindrical. It is to be understood that due to the specific high temperature of the preform 10 which is possible in accordance with the heating procedure outlined above, and because of the specific stretch ratio of the blow bottle 54 with respect to the preform 10 in both the axial and hoop directions, the resultant bottle 54 has in the body portions thereof a 28-30 percent sidewall crystallization which is a stress induced crystallization as opposed to being a temperature induced crystallization. Further, because of the specific cross sectional configuration of the body portion 64 as well as the specific stress induced crystallization of the shoulder portion 56, when the bottle 54 is hot filled with a liquid at a temperature on the order of 82°-85°C (180°-185°F), the shrinkage of the bottle 54 by volume will be no greater than 1 percent, i.e. the volumetric shrinkage should be between 0 and 1 percent. Thus the bottle 54, when hot filled with a heated liquid, will maintain this configuration. Further, because the neck finish 16 is non-oriented, it will be subjected to heat deformation. However, because the neck finish 16 is injection molded and relatively thick, it will be able to withstand the momentary heating thereof to a relatively high temperature without deformation which will prevent the closing and sealing of the bottle 54 utilizing conventional closures, particularly screw threaded closures. It will also be noted that the recessed bottom or base portion 80 is of a relatively thick wall configuration and will resist deformation when the bottle 54 is filled with a heated liquid. Although only a preferred embodiment of the preform and of the method of forming the container have been specifically described and illustrated, it is to be understood that minor variations may be made in the invention without departing from the scope of the invention as defined by the appended claims.

Claims: A preform (10) for forming a blow moulded hot fill container, the preform (70) being formed of a polyester resin and including a neck finish portion (16), a neck to body transition (18), a body portion (14) and a base portion (12), the neck finish portion (16) including a flange (24) immediately adjacent to the neck to body transition (18), the neck to body transition (18) including a first portion (30) adjacent to the flange (24) and terminating in a second portion (32), the first portion (30) flaring in increasing thickness from the second portion (32) to the flange (24), the second portion (32) defining a minimum cross-section region of the neck to body transition (18), which miminum cross-section has a thickness less than that of the body portion (14) and being spaced from the flange (24), and a third portion (34) between the second portion (32) and the body portion (14), the third portion (34) flaring in increasing thickness to the body portion (14). A preform according to claim 1 wherein the first portion includes a substantially cylindrical portion (28) adjacent the flange and a flaring portion adjacent to the second portion (32). A preform according to claim 1 wherein the first portion includes an internal thickening adjacent the flange to define a seat (26) for receiving a blow nozzle. A preform according to claim 1 wherein the neck finish is non-oriented and is substantially free of heat crystallization. A preform according to any foregoing claim wherein the polyester is polyethylene terephthalate. A preform according to claim 1 wherein the flaring of the third portion (34) is both internal and external. A preform according to claim 1 wherein the minimum cross-section portion (32) is substantially cylindrical. A preform according to claim 4 wherein the flaring of the first portion (30) is external. A preform according to claim 1 wherein the first portion (30) flares in thickness by a greater amount per unit length of the preform (10) than the flaring of the third portion (34). A preform according to claim 1 wherein the base portion (12) includes a lowermost part-spherical part (40) and a frustoconical part (38) joining said part-spherical part (40) to said body portion (14). A preform according to claim 10 wherein the part-spherical part (40) tapers in thickness from the frustoconical part (38). A preform according to claim 11 wherein the base portion (12) further includes a radius part (36) which joins the frustoconical part (38) to the body portion (14). A method of forming a blow moulded hot fill container (54), the method comprising the steps of:- (a) providing a preform (10) including a neck finish portion (16), a neck to body transition (18), the neck finish portion (16) including a flange (24) immediately adjacent to the neck to body transition (18), a body portion (14) and a base portion (12). the neck to body transition (18) having a portion (32) thereof of minimum cross-section, the said portion (32) having a thickness less than that of the body portion (14), and the neck to body transition (18) flaring in thickness from said portion (32) to said body portion (14) ; (b) heating the neck to body transition (18), the body portion (14) and the base portion (12) to a blow moulding temperature; (c) placing the heated preform (10) in a blow mould (42); (d) axially elongating the preform (10) thereby causing preferential thinning of the minimum cross-section portion (32) of the preform (10),which is spaced from the flange (24), relative to the remainder of the neck to body transition (18), wherein during axial elongation the said portion (32) is caused to neck down and assume a radially inwardly directed bowed configuration so as to undergo a greater stretching in the hoop direction during subsequent blow moulding; and (e) blow moulding the elongated preform (10) to form the container (54). A method according to claim 13 wherein the preform includes a downwardly tapering first portion (30) decreasing in wall thickness toward the portion (32) of minimum cross-section, and wherein during axial elongation the first portion (30) also necks down and assumes a radially inwardly directed bowed configuration. A method according to claim 14 wherein the preform further includes a third portion below the minimum cross-section portion (32), the third portion (34) flaring in increasing thickness towards the body portion, and wherein during axial elongation the third portion (34) also necks down and assumes a radially inwardly directed bowed configuration. A method according to claim 13 wherein the said portion (32) of the neck to body transition (18) is a middle portion thereof which is spaced from the flange (24) and below portion (32) the neck to body transition (18) flares in increasing thickness to the body portion (14). A method according to claim 16 wherein the axial elongation and blow moulding steps (d) and (e) are carried out whereby the container (54) has a biaxially oriented relatively thin shoulder region (56) formed from the neck to body transition (18) adjacent to a relatively thick portion beneath the flange (24) of the neck finish portion (16) of the container (54). A method according to any one of claims 13 to 17 wherein after heating step (b) the neck to body transition (18) is substantially free of heat crystallisation. A method according to any one of claims 13 to 18 wherein in axial elongation step (d) the axial elongation is effected by a push rod (44) internally engaging the base portion (12) of the preform (10). A method according to any one of claims 13 to 19 wherein the axial elongation of the preform (10) prior to inflation is on the order of 25 percent. A method according to any one of claims 13 to 20 wherein in heating step (b) a portion of the neck to body transition (18) of the preform (10) which extends on the order of 2mm below the flange (24) is unheated. A method according to any one of claims 13 to 21 wherein the body portion (14) of the container (54) has a strain induced sidewall crystallisation of up to about 30 percent. A method according to any one of claims 13 to 22 wherein the container (54) has a volume shrinkage of no greater than 1% when hot filled with a liquid at a temperature of from 82 to 85°C (180 to 185°F). A method according to any one of claims 13 to 23 wherein the preform (10) is formed of polyester. A method according to claim 24 wherein the polyester is polyethylene terephthalate.

Inventors: COLLETTE WAYNE N, KIRSHNAKUMAR SUPPAYAN M, PICCIOLI DAVID P, COLLETTE, WAYNE N., KIRSHNAKUMAR, SUPPAYAN M., PICCIOLI, DAVID P.
Applicants: CONTINENTAL PET TECHNOLOGIES, CONTINENTAL PET TECHNOLOGIES, INC.
Application year: 1988
Main classification: B29C49
IPC codes: B65D1, B29C49, B29B11, B29K67, B29C55, B29L22