Process for the production of thin stretched films from polyolefins of ultrahigh molecular weight

Abstract: The invention relates to a process for the production of thin stretched films with thickness between 0.1 and 20 µm from polyolefins of ultrahigh molecular weight by dissolving the polyolefin in a solvent, shaping the solution at a temperature above the solution tem­ perature of the polyolefin to a tape, cooling the tape to a tem­ perature below the solution temperature to obtain gelation and stretching the gelled tape. In this process the gelled tape is ini­ tially subjected to a preliminary orientation in one direction, under solvent removal, and is then stretched in a direction essentially per­ pendicular to the direction of preliminary orientation, at elevated temperature, followed by final stretching to obtain the finished thin films. This process makes possible the production of films which are free from pores, that is to say transparant and which posses high Young's moduli, high tensile strengths and favourable values for elongation at break.

Description: The invention relates to a process for the production of thin stretched films from polyolefins of ultrahigh molecular weight, which possess high tensile strengths, high Young's moduli and excellent values for elongation at break. In EP-A-0,163,424 thin films made from polyethylene of ultrahigh molecular weight and a process for their production are described. This process consists of dissolving polyethylene of ultrahigh molecular weight in a solvent, shaping the solution into a tape, cooling the tape to a temperature below the gelation temperature, a gelled tape being formed, partly removing the solvent from the gelled tape, the gelled tape being fixed in the longitudinal and transverse directions, heating the gelled tape and stretching biaxially in the usual manner. Since the thin films obtained in this manner exhibit pores and therefore are cloudy, they are subjected to a compression process at a temperature below the melting point of the polyethylene, a press or calender being used. This compression treatment is not able however to remove all pores and represents a measure which makes a continuous production of film on an industrial scale more expensive. The object of the invention is to provide a process for the production of thin stretched films from polyolefins in the implementation of which this compression stage is eliminated, films being obtained which are essentially free from pores and hence transparent and which compared with the previously known films have improved tensile strengths, Young's moduli and values for elongation at break. This object is achieved by the process according to the invention. The process according to the invention for the production of thin stretched films from polyolefins of ultrahigh molecular weight by dissolving the polyolefin in a solvent, shaping the solution into a tape at a temperature above the solution temperature of the polyolefin, cooling the tape to a temperature below the solution temperature to achieve gelation and stretching the gelled tape is characterized in that the gelled tape is first subjected to a preliminary orientation in one direction under solvent removal, and then is stretched in a direction essentially perpendicular to the direction of preliminary orientation, at elevated temperature, which is succeeded by a final stretching. By means of this process it is surprisingly possible to produce stretched thin polyolefin films which are free from pores. Apart from this, the films produced by the process according to the invention possess higher tensile strengths of more than 0.5 GPa, higher Young's moduli of more than 5 GPa and better values for elongation at break of less than 60% compared with the known films. For final thickness of 0.1 to 20 µm their thickness distribution amounts to less than 10%. Moreover, they are completely transparent, that is to say macroscopically non porous. The invention is based on the surprising observation that by a preliminary orientation of the gelled tape in one direction, with solvent removal, and subsequent stretching at an elevated temperature in a direction which is essentially perpendicular to the direction of preliminary orientation, the formation of pores caused by the elimination of solvent from the gelled tape is suppressed and better physical properties of the finished stretched films are achieved than in the case of the known films. This preliminary orientation can be carried out in such a way that the gelled tape during solvent removal, for example by evaporation, is allowed to shrink more in one direction than in the direction essentially perpendicular thereto, whereby a preliminary orientation of the polyolefin molecules occurs in the direction in which it is allowed to shrink less. Another possibility consists in carrying out the preliminary orientation in such a way that the gelled tape is stretched more in one direction than in the direction essentially perpendicular thereto in order to achieve the preliminary orientation in one direction. A third possibility consists in stretching the gelled tape only in one direction. Combinations of these three preferred measures can also be applied to carry out the preliminary orientation of the gelled tape in one direction. Expediently, the preliminary orientation of the gelled tape is carried out in the machine direction in which case in a continuous procedure, which the present invention allows, the gelled tape is stretched by suitably arranged stretching rolls in the machine direction, a stretching of lesser magnitude than in the machine direction also being carried out, if desired, by clamps which grip the sides of the tape. In an expedient manner, the preliminary orientation of the gelled tape is carried out in one direction with a stretch ratio of 1.1 to 20, in particular 1.1 to 5. The solvent removal from the gelled tape during the preliminary orientation is preferably achieved by drying that is to say evaporation of the solvent, in particular at room temperature. However, other measures for solvent removal are also possible, using more readily volatile solvents for the polyolefin solvent, and it is also possible to remove the solvent mechanically, for example by squeezing. The stretching of the gelled tape in the direction essentially perpendicular to the direction of preliminary orientation can be achieved preferably at a temperature which lies between 30°C below the melting point and the melting point of the polyolefin. This stretching is expediently carried out with a minimum stretch ratio of 1.5, while the maximum stretch ratio is preferably 10 to 15. The speed with which this stretching in the direction essentially perpendicular to the direction of preliminary orientation is carried out is expediently 1% per second to 1,000% per second. Before the final stretching, stiffened sections are preferably produced at the edges of the gelled tape which allow in particular ultrahigh final stretching without formation of noticeable curls caused by the locally gripping pulling clamps of the stretching apparatus. These stiffened sections can be produced in a manner whereby the gelled tape, if it is free from solvent, is heated at its lateral edges to a temperature which lies between 10°C below the crystalline melting point and below the decomposition temperature of the polymer or, if the gel tape still contains solvent, it is heated to a temperature above the solution temperature and below the decomposition temperature of the polymer (compare also EP-A-300540). The final stretching can be carried out in one direction, but preferably biaxially, the stretching in this case being able to be carried out simultaneously or sequentially and stretch ratios between 3 and 25 expediently being maintained. It has further proved expedient to subject the film produced, after the final stretching, to an annealing treatment, which preferably is carried out at a temperature between room temperature and the melting point of the polyolefin. By this annealing process a possible delamination of the films, which can be observed in all highly stretched polyolefin films, is inhibited. The polyolefin films produced by the process according to the invention are used in particular as magnetic recording media, as capacitor foils, as wire coatings, as components of composite materials, as insulation films, as implantation materials etc. The polyolefins used to carry out the process according to the invention are preferably polyethylenes, in particular linear polyethylenes, which can contain relatively small quantities, preferably at most 5 mol%, of one or more other alkenes which are copolymerizable therewith, such as propylene, butylene, pentene, hexene, 4-methylpentene, octene, etc. Preferably the polyethylene contains 1 to 10, in particular 2 to 6, methyl or ehtyl groups per 1000 carbon atoms. The process can however be carried out with the use of other polyolefins such as propylene homo- and copolymers. Furthermore, the polyolefins used can also contain small amounts of one or more other polymers, in particular alkene-1 polymers. The polyolefins used to carry out the process according to the invention possess an ultrahigh molecular weight, that is to say a weight-average molecular weight of at least 4 x 10⁵ g/mol, it being possible to use polyolefins with molecular weights up to 6 x 10⁶ g/mol and above. The polyolefins used can contain known additives such as fillers, stabilizers against degradation by ultraviolet radiation or ozone, flame inhibitors, crystallizing agents, calcium stearate, agents to improve abrasion resistance, antiblocking agents, etc. Suitable solvents for the ultrahigh molecular polyolefins used to carry out the process according to the invention are the halogenated and non-halogenated hydrocarbons known for this purpose, in particular aliphatic, cycloaliphatic and aromatic hydrocarbons with boiling points of at least 100°C, such as paraffins, toluene, xylenes, tetralin, decalin, C₉- to C₁₂- alkanes or petroleum fractions. It is also possible to use solvents which are solid at room temperature but which are liquid at the solution temperature, such as paraffin waxes. The polyolefin is dissolved in these hydrocarbons expediently in quantities between 1 and 80% by weight, in particular 10 and 50% by weight. Preferably the solution occurs at a temperature between 100 and 220°C, decalin being used as the particularly preferred solvent. The solution temperature depends of course on the particular polyolefin used, the solvent used, the quantity to be dissolved and the apparatus used to carry out the dissolving. Expediently the dissolving occurs in an extruder, in particular in a twin screw extruder, to which a suspension of the polyolefin to be dissolved in the particular solvent is introduced, one or more static mixers preferably being connected downstream of the extruder. The residence time in the extruder lies expediently between 1 and 25 minutes, in particular between 3 and 15 minutes. With the aid of the kneading action in the extruder and in the static mixers optionally connected downstream, the polyolefin goes into solution. The solution is extruded through a shaping die, which preferably has a width between 60 mm and 700 mm and a height between 100 µm and 10 mm producing a tape which is rapidly cooled to a temperature below the solution temperature of the polyolefin, with formation of a gel. The cooling can be carried out by immersion in a cooling bath, by blowing with a cooling gas or by using cooling rolls. When a cooling bath is used, water is preferably used as the cooling medium but the solvent which was used to dissolve the polyolefin can also be used as the cooling medium. Preferably, the temperature of the cooling bath is between 5 and 40°C. The gelled tape obtained is then subjected to a preliminary orientation in one direction, preferably in the machine direction, with solvent removal, in the manner described above, it being possible to remove 20 to 100% of the solvent from the gelled tape during this preliminary orientation. After the preliminary orientation in one direction, as the first measure essential to the invention, there follows the second measure essential to the invention of stretching in a direction which is essentially perpendicular to the direction of preliminary orientaton, at an elevated temperature, which expediently lies between the melting point of the particular polyolefin and 30°C below this melting point. The lateral edges of the gelled tape on which the pulling clamps of the stretching apparatus engage, are then expediently subjected to a stiffening treatment, preferably by heating to a temperature which, if the gelled tape is free of solvent, lies between 10°C below the crystalline melting point and below the decomposition temperature of the polyolefin, and if the gelled tape still contains solvent, lies above the solution temperature and below the decomposition temperature of the polyolefin. By this heating, a re-renewed entangling of the polymer molecules and hence a stiffening of the lateral edges occurs, so that final stretching with ultrahigh stretch ratios is possible, without significant formation of curls, which may tear, at the gripping points of the pulling clamps. The stiffened sections can also be produced by application of a strenghtening layer, for example made from a polymer such as a polyethylene of low density (LLDPE). More precise details of this stiffening treatment are obtainable from European patent application EP-A 300540. The tape treated in this way is then, in order to obtain the finished thin films with final thicknesses between 0.1 and 20 µm, subjected to final stretching which is carried out monoaxially, but preferably biaxially, it being possible for the biaxial stretching to be carried out in the particular directions sequentially or simultaneously. The annealing of the finished films in order to suppress a possible tendency to delamination in the plane of the film can be carried out in the same way according to the process in EP-A-301621. The continuous process according to the invention can be carried out with the employment of known apparatus for the production of polyethylene films by the gel process. These apparatus must merely be modified by a heating facility, for example a heating chamber, in which at elevated temperature the stretching of the gelled tape which has been preliminary orientated in one direction is carried out in a direction essentially perpendicular thereto. The examples which follow illustrate the invention. Example 1 This example describes a discontinuous manner of operating the process according to the invention. A linear polyethylene with an average molecular weight of 1.5 x 10⁶ g/mol (Hostalen GUR 412 R ) is dissolved in a concentration of 15% by weight in decalin in a twin screw extruder at a temperature of 190°C and with a residence time in the extruder of 8 minutes, and extruded through a shaping die with an orifice of 250 x 4 mm. The tape obtained is cooled in water at a temperature of 15°C, whereupon a piece with dimensions of 200 x 200 mm is cut from the tape. This piece is tensioned in an elastic tensioning apparatus, this tensioning apparatus allowing a shrinkage at a temperature of 50°C in an oven of 10% in the machine direction and 35% in the transverse direction. The gelled tape thus given a preliminary orientation in the machine direction is then stretched at a speed of 10% per second in the transverse direction for 3 seconds at a temperature of 130°C followed by a simultaneous biaxial stretching with a stretch ratio of 8 x 8. Then the film obtained is annealed at 100°C for 5 minutes under tension. The film obtained possesses a Young's modulus of 8.5 GPa, a tensile strength of 0.8 GPa, an elongation at break of 23% (in each case measured according to ASTM D-882 with a distance between the clamps of 100 mm and a clamp speed of 100 mm per minute), and a thickness of 2.7 µm. Example 2 (Comparative example) A linear polyethylene with an average molecular weight of 1.5 x 10⁶ g/mol (Hostalen GUR 412®) is dissolved in a concentration of 15% by weight in decalin under the conditions described in Example 1 in a twin screw extruder, and the solution is shaped with a shaping die of dimensions 250 x 5 mm to form a tape which is then quenched in the way described in Example 1. After quenching the gelled tape possesses a width of 220 mm and is led through an oven in which clamps located at the sides allow a shrinkage from 220 to 160 mm. The speed of the tape is 20 cm per minute in the oven and 18.5 cm per minute from the oven because of the shrinkage which has occured there, which amounts to 5% in the machine direction and 28% in the transverse direction. The tape thus given a preliminary orientation in the machine direction is simultaneously stretched in both directions at a speed of 10% per second at a temperature of 130°C. Even before a stretch ratio of 2 is reached the film is split in the lengthwise direction. This example therefore shows the importance of the stretching according to the invention in the direction perpendicular to the direction of preliminary orientation. Example 3 (comparative example) Example 2 is repeated with the exception that in this case a stretching in a direction perpendicular to the direction of preliminary orientation is carried out at 130°C with a stretch ratio of 1.3. During the simultaneous stretching in both directions which follows, the film likewise splits in the lengthwise direction because of the fact that the stretch ratio in the direction perpendicular to the direction if preliminary orientation is only 1.3 and hence under the lower limit of 1.5. Example 4 The procedure in Example 2 is repeated, a stretching perpendicular to the direction of preliminary orientation of the gelled tape being carried out at 137°C with a ratio of 5. After simultaneous stretching in the machine direction and in the transverse direction with a stretch ratio of 6 x 6 at 130°C a tape is obtained with a Young's modulus of 6 GPa, a tensile strength of 0.4 GPa, an elongation at break of 51%, and a thickness of 2.4 µm. Example 5 The procedure described in Example 2 is repeated, the stretching perpendicular to the direction of preliminary orientation of the gelled tape being carried out at a temperature of 137°C in a stretch ratio of 8. Subsequently, sequential stretching is carried out firstly in the machine direction with a stretch ratio of 4 and then in the machine direction with a stretch ratio of 4 and then in the transverse direction with a stretch ratio of 3 at a temperture of 137°C. The tape obtained possesses a Young's modulus in the machine direction of 6.3 GPa (transverse direciton 5.5. GPa), a tensile strength in the machine direction of 0.6 GPa (transverse direction 0.6 GPa), an elongation at break in the machine direction of 25% (transverse direction 31%), and a thickness of 4.5 µm. Example 6 A linear polyethylene with a weight-average molecular weight of 1.5 x 106 g/mol (Hostalen GUR 412®) is dissolved in a concentration of 15% by weight in decalin and quenched according to the method described in Example 1. The gelled tape obtained has a width of 220 mm and is led through an oven in which, by means of clamps applied at the sides, a sideways stretching and a shrinkage in the machine direction occur. The speed at which the tape enters the oven is 20 cm per minute and its exit speed from the oven is 13 cm per minute. In the oven the tape is stretched by the laterally placed clamps from its original width of 220 mm to a width of 310 mm. Accordingly, the tape is stretched in the machine direction with a stretch ratio of 0.65 and in the transverse direction with a stretch ratio of 1.4. This gelled tape, given a preliminary orientation in the transverse direction, is then stretched in the machine direction at a speed of 10% per second at 137°C with a stretch ratio of 6.5 and then is stretched at 134°C in the machine direction and in the transverse direction at 10% per second with a stretch ratio of 5 x 3. The tape obtained possesses a Young's modulus of 9 GPa, in the transverse direction (machine direction 6 GPa), a tensile strength of 0.7 GPa in the transverse direction (0.7 GPa in the machine direction), an elongation at break of 20% in the transverse direction (28% in the machine direction), and a thickness of 3.4 µm. Example 7 The procedure described in Example 2 is repeated. The tape thus obtained is allowed to shrink in the oven for 20% in the machine direction and 35% in the transverse direction. Subsequently, the gelled tape, given a preliminary orientation, is stretched in the transverse direction with a stretch ratio of 2 and then is stretched at 137°C in the machine direction and in the transverse direction at a speed of 20 mm per second with a stretch ratio of 8 x 8. The total stretch ratio of the tape is 66.6. The tape obtained possesses a Young's modulus in the machine direction of 8.0 GPa (transverse direction 7.5 GPa), a tensile strength in the machine direction of 0.8 GPa (transverse direction 0.7 GPa), an elongation at break in the machine direction of 23% (transverse direction 25%) and a thickness of 4.5 µm. Example 8 (Comparative example) Example 2 is repeated but the tape is not submitted to a preliminary orientation. The tape is stretched with a stretch ratio in both the transverse direction and the machine direction of 8 at 137°C. The total stretch ratio of the tape is 8 x 8 = 64. The tape obtained possesses a Young's modulus in the machine direction of 4.5 GPa (transverse direction 4.3 GPa), a tensile strength of 0.3 GPa in the machine direction and 0.4 GPa in the transverse direction, an elongation at break of 30% in the machine direction (transverse direction 35%) and a thickness of 6 µm.

Claims: Process for the production of thin stretched films from polyolefins of ultrahigh molecular weight by dissolving the polyolefin in a solvent, shaping the solution into a tape at a temperature above the solution temperature of the polyolefin, cooling the tape to a temperature below the solution temperature to achieve gelation and stretching the gelled tape, characterized in that the gelled tape is first subjected to a preliminary orientation in one direction under solvent removal, and then is stretched in a direction essentially perpendicular to the direction of preliminary orientation, at elevated temperature, which is succeeded by a final stretching. Process according to Claim 1, characterized in that the preliminary orientation is carried out in such a way that the gelled tape during solvent removal is allowed to shrink more in one direction than in the direction essentially perpendicular thereto. Process according to Claim 1, characterized in that the preliminary orientation is carried out in such a way that the gelled tape is stretched more in one direction than in the direction essentially perpendicular thereto. Process according to Claim 1, characterized in that the preliminary orientation is carried out in such a way that the gelled tape is stretched only in one direction. Process according to one of Claims 1 to 4, characterized in that the preliminary orientation of the gelled tape is carried out in the machine direction. Process according to one of Claims 1 to 5, characterized in that the preliminary orientation of the gelled tape is carried out in one direction with a stretch ratio in the direction of preliminary orientation of 1.1 to 20, in particular of 1.1 to 5. Process according to one of Claims 1 to 6, characterized in that the solvent removal from the gelled tape is carried out by drying, in particular at room temperature up to 50°C. Process according to one of Claims 1 to 7, characterized in that the stretching of the gelled tape in the direction essentially perpendicular to the direction of preliminary orientation is carried out at a temperature which lies between the melting point of the polyolefin and 30°C below this melting point. Process according to Claim 8, characterized in that the stretching is carried out with a minimum stretch ratio 1.5. Process according to one of Claims 8 to 9, characterized in that the stretching is carried out at a speed of 1% per second to 1000% per second. Process according to one of Claims 1 to 10, characterized in that the lateral edges of the gelled tape are treated to produce stiffened sections. Process according to one of Claims 1 to 11, characterized in that the final stretching is carried out in one direction or in both directions simultaneously or sequentially with a stretch ratio between 3 and 25. Process according to one of Claims 1 to 12, characterized in that after the final stretching an annealing treatment of the film obtained is carried out. Process according to Claim 13, characterized in that the annealing treatment is carried out at a temperature from room temperature to the melting point of the polyolefin. Use of the films produced according to Claims 1 to 13 as magnetic recording media, capacitor foils, wire coatings or components of composite materials.

Inventors: PLUYTER PIETER BOUDEWIJN, PONTENAGEL WILLIBRORDUS MARIE, VAN UNEN LAMBERT HENRI THEODOO, PLUYTER, PIETER BOUDEWIJN, PONTENAGEL, WILLIBRORDUS MARIE GERTRUD FRANCISCUS, VAN UNEN, LAMBERT HENRI THEODOOR
Applicants: DSM NV, DSM N.V.
Application year: 1988
Main classification: C08J5
IPC codes: B29K23, B29L7, C08J5, H01G13, B29C55