PURPLE DIAMOND AND METHOD OF PRODUCING THE SAME

Abstract: A purple diamond characterized in that the absorption coefficient of the Ib type nitrogen at 500 nm is 0.2 - 2 cm⁻¹, the absorption coefficient of the N-V center at an absorption peak of 570 nm is 0.3 - 10 cm⁻¹, and the absorption coefficients of the GR1 center, H2 center, H3 center and H4 center are less than 0.2 cm⁻¹ in the visible region. A method of producing a purple diamond characterized by using an Ib type artificial synthetic diamond crystal wherein the Ib type nitrogen content in the crystal is within the range of 8 x 10¹⁷ - 1.4 x 10¹⁹ atoms/cm³, subjecting the diamonds crystal to an electron beam irradiation by 5 x 10¹⁶ - 2 x 10¹⁸ electrons/cm² at 2 - 4 MeV, and annealing it in a vacuum of less than 10⁻² Torr at a temperature of 800 - 1100°C for more than 25 hours.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a purple diamond suitable, for example, for ornamental purposes and a method of producing the same. Description of the Background To obtain a colored diamond, it has been usual practice to irradiate a natural diamond with an electron beam and then anneal the same under a vacuum atmosphere, so as to form a color center. A color center is formed when a nitrogen atom in a crystal and a lattice defect formed by the irradiation of an electron beam are combined with each other by the action of annealing. Further, a lattice defect alone is also effective in forming a colored diamond. Further, the type of the color center is determined by the manner in which nitrogen atoms aggregate together. The relation between color centers and colors is shown in Table 1. For the methods of forming the color centers listed in Table 1 and their characteristics, refer to "Optical absorption and luminescence in diamonds," Reports on Progress Physics, John Walker, Vol. 42, 1979. Further, the true colors exhibited by colored diamonds are the colors indicated in Table 1 superposed on the intrinsic colors of natural rough diamonds. The intrinsic colors of natural rough diamonds are classified as shown in Table 2. As is obvious from Table 2 and Table 1, those rough stones are colored effectively by making a color center indicated in Table 1 in type IIa or Ia diamonds which are transparent colorless or light yellow. These rough stones either do not have nitrogen at all or have 1 or 2 pairs of nitrogen atoms. Thus, it follows that coloration is effective for only two colors which follow: (1) Bluish green (based on the GR1 center formed solely by electron beam irradiation) (2) Yellow (based on the H3 and H4 centers formed by electron beam irradiation and annealing). The EP-A-0 275 063 discloses a light emitting element basing on an artificial diamond with color centers giving the diamond a yellow color. Particularly an increased number of H3 color centers is capable to improve the laser efficiency of the light emitting element. From the above observation, we have concluded that a diamond which exhibits purple developed by the N-V center can hardly be produced from natural rough stones and that a purple diamond which induces a transparent sensation in the mind and whose color is brilliant cannot be produced from natural rough stones. Further, since the Ib type rough stone containing isolated type nitrogen alone for production of the N-V center is present in as low as 0.2 % of natural rough stones, it is very difficult to obtain such rough stone itself. Thus, we conceived the idea of using an Ib type artificial synthetic diamond which contains 100 % isolated nitrogen. In addition, a method of producing the N-V center by electron beam irradiation and annealing is described in A.T. Collins, Journal of Physics C, Solid State Physics, 16 (pp. 2177-2181, 1983). However, to put a colored diamond to ornamental use, it should induce a transparent sensation in the mind and its color should be brilliant, a problem which has not been solved. SUMMARY OF THE INVENTION An object of the present invention is to provide a purple diamond which induces a transparent sensation in the mind and whose color is brilliant and a method of mass-producing the same. A purple diamond according to the present invention is characterized in that the absorption coefficient of the Ib type nitrogen at 500 nm is 0.2 - 2 cm⁻¹, the absorption coefficient of the N-V center at an absorption peak of 570 nm is 0.3 - 10 cm⁻¹, and the absorption coefficients of the GR1 center, H2 center, H3 center and H4 center are less than 0.2 cm⁻¹ in the visible region. A method of producing a purple diamond according to the invention used an Ib type artificial synthetic diamond crystal wherein the Ib type nitrogen content is within the range of 8 x 10¹⁷ - 1.4 x 10¹⁹ atoms/cm³. And it is characterized by subjecting said diamond crystal to an electron beam irradiation of 5 x 10¹⁶ - 2 x 10¹⁸ electrons/cm² at 2 - 4 MeV, followed by annealing in a vacuum of less than 1.3 Pa (10⁻² Torr) at a temperature of 800 - 1100°C for more than 25 hours. Our Purple Diamond The transparent sensation depends on the absorption coefficient of the N-V center and on the absorption coefficient of the Ib type nitrogen, and to induce a transparent sensation in the mind, it is important that this value has to be within said range. On the other hand, in order to ensure the color brilliance of the diamonds, it is important that the absorption coefficients of the other color centers have to be less than 0.2 cm⁻¹ in the visible region in addition to the restriction as to the absorption coefficients of said N-V center and Ib type nitrogen. (A) On absorption Coefficient of N-V Center: In the N-V center absorption occurs from 500 nm to 640 nm, the peak value being 570 nm. Therefore, the center color of absorption is yellow. As a result of this absorption, the crystals exhibit a complementary color, purple. This absorption plays an important role in determining the color of a purple diamond according to the invention. The transparent sensation is an important factor in ornamental use. This correlates to absorption coefficient such that the transparent sensation is lost when the absorption coefficient exceeds 10 cm⁻¹. On the other hand, for an absorption coefficient of less than 0.3 cm⁻¹, the purple disappears, giving place to the yellow which is the intrinsic color of the rough stone. (B) On Absorption Coefficient of Type Ib Nitrogen: In the case of type Ib nitrogen, the absorption occurs at 550 nm. As a wavelength decreases, the absorption coefficient increases and becomes almost equal to the infinity at 400 nm. The range in which absorption increases lies above 500 nm, where blue, indigo and purple colors are absorbed, with the crystals exhibiting a complementary color, yellow. If this yellow is light, it mixes with purple, exhibiting a clear purple color, inducing a transparent sensation in the mind. This effect will not take place if the absorption coefficient at 500 nm is less than 0.2 cm⁻¹. If it exceeds 2 cm⁻¹, the yellow is too dark for the crystals to induce a transparent sensation in the mind and predominates over purple; purple is not longer exhibited. (C) On Absorption Coefficient Associated with Other Types of Absorption: When other types of absorption (by the GR1 center, H2 center, H3 center and H4 center) take place in the visible region, the purple becomes turbid, decreasing the brilliant sensation. To maintain the brilliant sensation, it is important that the absorption coefficient be less than 0.2 cm⁻¹. Absorption peaks representative of other types of absorption taking place in the visible region include those from the GR1 center where absorption appears at 550 - 740 nm and the H2 center where absorption appears at 650 - 990 nm. Since these centers absorb colors which lie around red, excessively high absorption coefficients would cause green, which is a complementary color, to mix with purple, decreasing the brilliant sensation. On Production Method (A) Use of Ib type artificial synthetic diamonds: In the case of natural diamonds, since various forms of nitrogen atoms are contained, annealing will provide a plurality of type of color centers. Therefore, it is very difficult to prepare a rough stone which contains the N-V center alone by using a natural diamond. Ib type artificial synthetic diamonds contain 100 % isolated type nitrogen atoms. For this reason, if an artificial synthetic diamond is used, a rough stone which contains the N-V center alone can be easily produced. In this case, a diamond synthesized by the temperature gradient method contains a less amount of bulk-like inclusions than does a diamond synthesized by the film growth method, resulting in large-sized crystals, a fact which is desirable. (B) On Nitrogen Content: The factor which is most closely correlated to the absorption coefficient of the N-V center and to the absorption coefficient of the Ib type nitrogen is the nitrogen content. If the content is less than 8 x 10¹⁷ atoms/cm³, the absorption coefficient of the N-V center at 570 nm will be 0.2 cm⁻¹ or the absorption coefficient of the Ib type nitrogen at 500 nm will be less than 0.3 cm⁻¹. Further, if the content exceeds 1.4 x 10¹⁹ atoms/cm³, the absorption coefficient of the N-V center will exceed 2 cm⁻¹ or the absorption coefficient of the Ib type nitrogen will exceed 10 cm⁻¹. (C) On Electron Beam Irradiation: Uniform formation of lattice defects by electron beam irradiation is essential for uniform production of the N-V center throughout the crystals. Under the condition of irradiation with less than 5 x 10¹⁶ electrons/cm² at 2 MeV, the lattice defect concentration will be decreased in some of the crystal. Further, above 4 MeV, there will be a possibility of the inclusions being irradiated. With an irradiation dose which exceeds 2 x 10¹⁸ electrons/cm², the defect concentration will be too high, raising a problem that the GR1 center cannot be removed or that the H2 center begins to form. In this case, there will be a high degree of absorption in the visible region due to other than the N-V center and Ib type nitrogen. (D) On Annealing: More than 25 hours of annealing satisfactorily eliminates the GR1 center produced by electron beam irradiation and ensures satisfactory combination between the Ib type nitrogen and lattice defects. With less than 25 hours of annealing, however, said effects cannot be attained to the fullest extent. Further, with a vacuum which exceeds 1.3 Pa (10⁻² Torr), graphitization of diamond surface will occur. If the annealing temperature is less than 800°C, the GR1 center cannot be fully removed, while if it exceeds 1100°C, the N-V center begins to be destroyed and the purple is lightened. According to the invention, a purple diamond which induces a transparent sensation in the mind and whose color is brilliant can be obtained. Furthermore, according to a method of producing a purple diamond, since a purple diamond is obtained by the process characteristic of the invention by using an artificial synthetic diamond, it is easy to procure the necessary rough stone and hence purple diamonds can be mass-produced. Examples Example 1 Seven Ib type artificial synthetic diamonds (whose nitrogen content was 4 x 10¹⁷ to 4 x 10¹⁹ atoms/cm³) synthesized by the temperature gradient method were subjected to electron beam irradiation using 1 x 10¹⁶ to 2 x 10¹⁹ electrons/cm² at 3 MeV. Subsequently, they were subjected to 30 hours of annealing in a vacuum of 0.13 Pa (10⁻³ Torr) at 900°C. The diamonds obtained were tested for the absorption coefficient of the N-V center, Ib type nitrogen, GR1 and H2 centers by using an ultraviolet visible spectroscope. Further, said samples were brilliant-cut into 0.5 - 0.6 carat/piece. To evaluate them as to their ornamental use, 100 randomly selected women aged 18 - 65 were requested to observe said sample and information on the following subjects was gathered through this questionnaire. The result is shown in Table 3. (Subjects to be asked in the questionnaire) (1) Does it induce a transparent sensation in the mind? (2) Is the color brilliant? (3) Does it have an ornamental value? In addition, the result of the questionnaire shown in Table 3 indicates the number of persons who answered "Yes". Example 2 Three Ib type synthetic diamonds (whose nitrogen content was 2 x 10¹⁸ atoms/cm³) synthesized by the temperature gradient method were subjected to electron beam irradiation using 2 x 10¹⁸ to 1 x 10¹⁹ electrons/cm² at 3 MeV. Subsequently, they were subjected to 10 - 40 hours of annealing in a vacuum of 0.013 Pa (10⁻⁴ Torr) at 1100°C. The samples obtained were tested for the absorption coefficient of the N-V center, Ib type nitrogen, GR1 center and H2 center by using an ultraviolet visible spectroscope. Further, said samples were brilliant-cut into 0.8 - 1.2 carats/piece. To evaluate them as to their ornamental use, a questionnaire was conducted in the same manner as in Example 1, and the result is shown in Table 4. Sample No. 1 2 3 Ultraviolet visible spectroscopic analysis (cm⁻¹) N-V center absorption coefficient (cm⁻¹) 0.7 0.6 0.7 Ib type nitrogen absorption coefficient (cm⁻¹) 0.3 0.3 0.3 Other-center absorption coefficient (cm⁻¹) Approximately 0 0.3 3.5 Electron beam irradiation dose (electrons/cm²) 2x10¹⁸ 2x10¹⁸ 1x10¹⁹ Annealing time (hours) 25 10 40 Result of questionnaire Transparent sensation (persons) 100 98 0 Color brilliantness (persons) 100 55 5 Ornamental value (persons) 100 45 0 Example Control Control In addition, the result of the questionnaire shown in Table 4 indicates the number of persons who answered "Yes".

Claims: Purple diamond having absorption coefficients of 0.2 - 2 cm⁻¹ of the 1b type nitrogen at 500 nm; 0.3 - 10 cm⁻¹ of the NV-center at 570 nm characterized by an absorption coefficient of less than 0.2 cm⁻¹ of the GR1-, H2-, H3- and H4-centers in the visible region. Method for producing a purple diamond using a 1b type artificial synthetic diamond crystal with a 1b type nitrogen content of the crystal in the range of 8 x 10¹⁷ - 1.4 x 10¹⁹ atoms/cm³, whereby the crystal is subjected to an electron beam irradiation of 5 x 10¹⁶ - 2 x 10¹⁸ electrons/cm² at 2 - 4 MeV and to an annealing procedure at a temperature of 800 - 1100°C, characterized in that the annealing procedure is held in a vacuum of less than 1.3 Pa (10⁻² Torr) for more than 25 hours.

Inventors: KAZUWO, TSUJI, SHUICHI, SATOH, Kazuwo, Tsuji, c/o Sumitomo Electric Ind.Ltd., Shuichi, Satoh, c/o Sumitomo Electric Ind.Ltd.
Applicants: SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1988
Main classification: C30B33
IPC codes: C30B33, C01B31, B28D5