DEVICES AND APPARATUS FOR INJECTING GAS INTO HIGH TEMPERATURE LIQUIDS, E.G. MOLTEN METALS

Abstract: For injecting gas into a liquid, more particularly a molten metal, a nozzle body (24) is installed in the wall of a liquid-containment vessel, the body (24) having a nozzle passage (25) therethrough. Liquid and gas tightly fitted in a downstream end of the passage is a solid, gas porous plug (18) having capillary gas passages (20). Upstream of the plug (18) the passage has a gas-porous and liquid-impermeable cartridge (10) closely fitted therein which prevents liquid which may conceivably pass through the plug (18) from leaking out of the passage (25). The cartridge (10) has a gas impermeable metal sleeve (11) containing a particulate material (16) such as sand which is retained in the sleeve (11) by wads (14, 15) of fibrous material at the ends of the sleeve.

Description: "DEVICES AND APPARATUS FOR INJECTING GAS INTO HIGH TEMPERATURE LIQUIDS, E.G. MOLTEN METALS" The invention relates to devices and apparatus for injecting gas into high temperature liquids, e.g. molten metals*. It may often be necessary to introduce gas into molten metal in a container or vessel. Gas is injected, for instance into the bottom area of a vessel for diverse purposes, including rinsing; clearing the relatively cool bottom area of solid¬ ification products, to help remove them from the vicinity of the vessel bottom outlet where the vessel has such an outlet; equalising the temperature throughout the melt; and stirring to help disperse alloying additions uniformly in the melt. Usually an inert gas is used, e.g. argon. Reactive gases are sometimes substituted if the melt needs some particular chemical treatment such as deoxidising. Previous gas injection proposals have included the provision of a solid porous plug or brick in the refractory lining of the vessel, and of solid porous plugs in sliding gate teeming valves. Install¬ ations featuring porous plugs have the virtue of simplicity, but are potentially hazardous, inter alia because they may crack due to thermal shock when molten metal is introduced into the vessel. Failure of the plug can obviously have extremely dangerous consequences. Sliding gate valves adapted for gas injection are safer, but unless overly complicated they are not able to offer the possibility- of gas injection simultaneously with teeming. The present invention aims to overcome drawbacks associated with prior gas injection systems, and to provide safer and more cost effective equip- ment for use in gas injection. According to one aspect of the present invention, there is provided an injection cartridge, for use in injecting gas through the wall of a vessel into a high temperature liquid contained therein, the cartridge comprising an open-ended gas-impermeable sleeve blocked adjacent each of its opposite ends by a wad of fibrous refractory material and containing a filling of partic ¬ ulate refractory matter, the cartridge being permeable to gas flow from one end to the other and impermeable to liquid flow therethrough. Such cartridges are well able to cope with thermal shock and, in con¬ junction with further gas injection components, provide valuable measures of added safety to gas injection operations as will become apparent as the description proceeds. Gas injection apparatus according to the invention can comprise a cartridge as defined in the preceding paragraph, and a refractory gas-discharge block arranged in tandem therewith, the discharge block having one end interfitting with one end of the cartridge and being porous or foraminous to allow gas but not liquid to traverse the block. The gas discharge block can be made of porous refractory; alternatively, it can be made of substantially gas-impermeable refractory material pierced by one or more capillary passageways. According to another aspect of the invention, there is provided a gas injection nozzle, for in- stallation in the wall of a vessel and for use in injecting gas into a high temperature liquid, comprising a refractory nozzle body having a passage therein and a gas porous or foraminous end portion closing the passage at a discharge end of the body, and closely fitted in the passage is a porous gas injection cartridge comprising an open-ended, gas- impermeable sleeve having upstream and downstream ends, closed adjacent each end by a compressible wad of fibrous refractory material and containing a filling of particulate refractory matter, the cartridge being permeable to gas flow from the upstream to the downstream end and impermeable to liquid flow there¬ through. In the event of liquid, such as molten metal, traversing the passage-closing end portion e.g. after a failure of the latter, the cartridge can prevent a serious leakage of said liquid from the. passage. Gas inlet means for conveying gas from a supply to an upstream end of the cartridge can be arranged to urge the cartridge into sealing contact with the said end portion; the cartridge and end portion can be designed to interfit one with the other. Further according to the present invention, there is provided metal pouring apparatus comprising a container vessel for molten metal, an opening in or adjacent the bottom of the vessel and assoc¬ iated means operable to control teeming of molten metal through the opening, and means for injecting gas into molten metal in the vessel, the injecting means including a nozzle installed in a wall of the vessel in the vicinity of an separate from the said opening and the teeming control means, and ducting exteriorly of the vessel for conveying gas to a passage through the nozzle, the ducting including two abutting orificed refractory bodies, one of the refractory bodies being movable relative to the other to pl the orifices out of registry thereby to close ducting and prevent any molten metal entering nozzle passage from escaping from the vessel via the noz and ducting, and inside the passage there is me tightly fitted an injection cartridge compris an open-ended, gas-impermeable sleeve closed adjac each of its opposite ends by a compressible of fibrous refractory material and containing filling of particulate refractory matter, the ca ridge being permeable to flow of gas towards t vessel interior and impermeable to flow of molt metal therethrough. The invention also _ provides a method metal pouring employing apparatus as defined the last preceding paragraph, wherein gas is inject into the molten metal in the container through the gas injection means simultaneously with teemi the metal from the container via the teeming contr means. The gas injection means in this apparat can be located adjacent the vessel bottom in i side wall, but like the teeming control means wi usually be located in the vessel bottom. Inspection of the cartridge for eviden of metal leakage involves straightforward visual examination of the underside thereof, coupled possibl with inspection of the orificed body further therefro of both bodies. Traces of frozen metal on these members indicate the apparatus is in need of servicin and at this stage the refractory bodies will be manipulated to a duct-closing setting until the vessel has been emptied. Preferably the means to control teeming is a sliding gate valve, although it could be a stopper rod arrangement. Embodiments of the invention will now be described by way of example with reference to the accompanying drawings, in which: Fig. 1 is a cross-sectional view through a gas injection cartridge according to the invention, Fig. 2 is a cross-sectional view of a gas injection nozzle according to the invention, Fig. 3 is a cross-sectional view of the cartridge according to the invention in association with a gas-discharge block, Fig. 4 is a cross-sectional view through the bottom of a ladle or tundish funished with gas injection means according to the invention and with a sliding gate valve, Figs. 5, 6 and 7 show a preferred gas injection device according to the invention, and are respectively a cross-section therethrough, a bottom plan view and a fragmentary, part-sectional view taken on the line 7-7 of Fig. 6, and Fig. 8 is a cross-sectional view of a slightly- modified cartridge according to the invention, and shows its interfitting with associated upstream parts of a gas injection means. Fig. 1 of the accompanying drawings show a longitudinal section through a gas injectio cartridge according to the invention. The cartridg 10 is an essential element of gas injection arrange ments embodying the invention and will need t be replaced periodically. The illustrated cartridg 10 has a cylindrical gas-impermeable sleeve 11 e.g. made of metal, which is open at both its ends At one end, as shown, the sleeve has an inturne lip 12. The other end of the sleeve might als be inturned in some instances, although such i not the case for this preferred cartridge. Bot ends of the cartridge 10 are closed by wads 14 15 of " fibrous refractory material of felt-lik nature. The wads 14, 15 are tightly jammed int the respective ends of the sleeve and both ar compressible for reasons explained hereinafter. The wads 14, 15 can comprise KA0W00L (Registered Trade Mark) which is manufactured by Morganite Ceramic Fibres Limited. Retained between the wads 14, 15, the cartridge 10 has a filling 16 of part¬ iculate refractory matter. The particulate filling 16 and the wads 14, 15 are gas permeable so that when gas under pressure is fed to one end of the cartridge 10 (e.g. the end with the inturned lip 11), the gas will flow along the cartridge and exit from the other end. The particulate filling 16 can comprise a sand. The actual composition of the filling will be determined according to c the injection conditions e.g. the temperatures to which the cartridge 10 is likely to be subjected in service and the chemical reactivity of the gas to be injected. Where the cartridge is to be used in a ferrous environment, its filling 10 can comprise a granular refractory material, for example a blend of a sand and graphitic material. The filling can, therefore, comprise a blend such as is used in the steel industry as a well filler. While the cartridge 10 is gas permeable, 15 it is designed to be impermeable to liquid, i.e. molten metal. KA0W00L (RTM) is not the only commercially available material suitable for the wads 14, 15. Possible alternatives among many others include 20 REFRASIL (RTM) Batt BA-1M manufactured by Chemical and Insulating Company Limited of Darlington U.K. and FIBERFRAX (RTM) which is a mineral wool material marketed by Carborundum Limited in both woven and dense felt forms. In gas Injection apparatus according to the invention, the cartridge 10 may be arranged in tandem with a gas-discharge block of some kind. Fig. 2 shows one such gas-discharge block 18 fit atop the cartridge 10. The block 18 is a cylind in this instance slightly-tapered, made e.g. fr a pressed and fired refractory or from a moul 5 refractory castable. The block 18 can be made fr a refractory which is inherently porous or foramin to allow gas that has passed through the cartrid 10 to enter and traverse the block before exiti from a discharge face 19 thereof into the mel 10 As shown, however, the block is pierced from e to end by a capillary passage 20 or a plurali thereof to facilitate gas flow through the bloc The or each capillary passage 20 may be 1 mm less in diameter. The size should be sufficient 15 pass gas freely but insufficient to permit molt metal to traverse the block in significant amoun should gas flow cease. It will be observed that a rebate 21 encirc the block 18 at its end contacting the cartrid 20 10. The rebate 21 accepts an end portion of t cartridge sleeve 11 which pro ects above the fibro wad 15, thereby enabling the block 18 and cartrid 10 to interfit. Longitudinally, the rebate is longer than the distance by which the slee 25 11 projects above the wad 15- Like the cartridge 10, the block 18 is an expendable item. Ordinarily, when the vessel is emptied of melt, a skin of frozen metal will form on the discharge face 19, or the metal will enter and freeze in the capillary passages. In either event, subsequent injection through the block 18 will be impaired if not actually prevented, so the block will need replacing at frequent inter¬ vals. Of course, If the cartridge and block are used for injecting gases into some other liquids, less frequent replacement of these items may be appropriate. In use, the cartridge 10 and block 18 are mounted in a gas injection nozzle body installed in a seating in the refractory lining of the vessel. The arrangement of cartridge, block 18 and nozzle body 24 is illustrated in Fig. 3- The nozzle body has a generally cylindrical duct 25 therein to receive the cartridge 10 and block 18. The duct 25 tapers slightly, at least at a downstream end thereof, to match the slightly tapered block 18 and to enable a liquid-tight fit to be formed with the block. The nozzle body can be a pressed and fired refractory or a refractory concrete casting. Its external shape can be varied to suit the seating - 1 1 - in the vessel lining and hence need not be as shown. If desired, the block 18 could be eliminated. The duct 25 would then be blind, terminating intern¬ ally within the nozzle body 24. The end portion of the nozzle body 24 between the end of the duct and discharge face 26 of the nozzle body 24 would be made gas porous, e.g. by the provision of capillary passages. Generally speaking, such an adaptation is not preferred, particularly where the nozzle body 24 and cartridge 10 are employed for injecting gas into molten metals. The cost of replacing the nozzle body will usually be substantially higher than the cost of replacing the relatively small block 18. However, if the nozzle body were of a different and appreciably more compact design, it might be feasible for it to be made a dispensible item and enabling the separate block 18 to be elim¬ inated. The nozzle assembly shown in Fig. 3 will be utilised with a gas inlet means for conveying gas from a supply to the upstream end of the cartridge, i.e. end 28 thereof. The inlet means is adapted to urge the cartridge 10 inwardly into sealing contact with the block 18 or the said end portion of the nozzle body. Referring to Fig. 2, the pro- jecting end of the sleeve 11 is forced into the rebate 21 and wad 15 is compressed between the confronting end of the block 18 and the filling 16 inside the cartridge 10. At the same time, this end of the sleeve may be thrust into a liquid- tight and preferably also a gas-tight interference fit within the taper of the nozzle duct 25. When the cartridge 10 Is properly seated against the block 18 or the said end portion, any liquid such as molten metal which might penetrate as far as the cartridge 10 will be blocked by the latter from leaking outwardly from the duct 25. * The inlet means can take various forms which it will be within the capability of the ordin- arily skilled designer to devise. One such inlet means is shown in Fig. 4 to which reference is now made. Fig. 4 illustrates a vessel such as a ladle 110 furnished with gas injecting means according to this invention and with a separate teeming means. The vessel 111 has an opening 112 through which molten metal can be controllably teemed by operation of teeming control means 114. The teeming control means 114 is a sliding gate valve. Beside the valve 114 the vessel 111 has the gas injection means 115- Sliding gate valves, of which there are several basic types, are commercially available and well known in the art. The structure, mounting and operation of such valves therefore need not be described in detail here. The teeming control means could instead comprise a stopper rod arrangement which likewise is well known in the art. The -gas injection means 115 is shown in the bottom of vessel 111 but could be placed in a sidewall of the vessel adjacent the bottom and the teeming control means. The gas injection means 115 comprises a gas passage formed in a refractory gas-admitting nozzle block 24 cemented in a seating therefor in the insulating lining 118 of the vessel 111. The nozzle block 24 protrudes through a metal outer casing 119 of the vessel 111 and is supported in place by a spigot 120 and carrier plate 121. A solid, gas-porous discharge block 18 closes off the passage or duct of the nozzle block, and serves as a distributor into the melt of gas fed under pressure to the nozzle block 24. The passage or duct is, in this instance, provided in part by the nozzle block 24 and in part by a refractory insert ring 122 which is supported centrally of the nozzle block 24 by the spigot 122. A gas passage leading to the nozzle block 24, cartridge 10 and porous block 18 includes a duct provided by two orificed refractory bodies; the duct communicates with a gas feed pipe 124. Pipe 124 has a connection at one end for a usually flexible gas supply pipe (not shown). The pipe 124 terminates in a lower one of the two orificed bodies 126, 127. The duct formed by the two bodies 126, 127 is a continuation of the nozzle bore, and in this case the duct is co-linear with the bore. The upper orificed body 127 is fixedly mounted with its orifice in registry with the nozzle passage. The lower body 126 is mounted for to-and- fro lateral movement in contact with the underside of body 127- Moving the lower body 26 thus enables Its orifice to be brought into and out of registry with the orifice of the stationary upper body, the orifices being in registry for gas injection. The two bodies 126, 127 will be seen to form a plate valve which must be tight against leakage of molten metal when their orifices are fully out of registry. Biasing means, not shown, force the lower plate 126 firmly against the upper plate in order to obtain leak-tightness. Also, to assure leak-tightness, the insert ring 122 forms a recessed or stepped joint with the upper surface of the upper orificed body 127. Further, the assembly comprising bodies 126, 127 and insert ring 122 must be as gas tight as practical. The illustrated arrangement has been designed to facilitate the operation of changing the cartridge 10 and discharge block 18. The nozzle block 24 therefore has a downwardly and outwardly divergent duct matching the block 18 at least, as shown, at its uppermost end. Removal of the cartridge 10 and porous block 18 is through the bottom of the vessel 11 after dismounting the bodies 126 and 127. The nozzle block 24 can be a one-piece member but often more conveniently is an assembly of a plurality of components as shown. The lower end of insert ring component 122 forms a steppedjoint with the upper surface of the stationary orificed body 127, and this joint is cemented e.g. with a mastic to guard against escape of the gas from this joint. Manual, pneumatic or hydraulic means can be provided to displace the lower orificed body 126 laterally relative to the upper body 127- In normal operation, the orifices in the bodies 126, 127 will be in exact registry. Gas will be admitted to the nozzle block passage, the cartridge 10 and porous block 18 through the duct constituted by the aligned orifices, for distribution Into the melt after traversing the porous block. Gas admission will normally take place prior to teeming but in some pouring operations can be simul¬ taneous with teeming through the valve 14. If it is suspected that either the cartridge 10 or the porous block 18 (or a cement seal between it and the nozzle block 24 - if any) has become defective, occasioning a risk of leakage, lower orificed body 126 will be displaced laterally e.g. to the right as viewed in Fig. 1. This is to place the orifices of bodies 126, 127 out of registry, to interpose an imperforate portion of body 126 across the gas passage, and thereby ensure no molten metal can leak from the gas injection means 115. Periodic inspection of the cartridge 10 can be performed whenever the vessel 111 is empty. After removing the orificed bodies 126, 127 e.g. by swinging them downwardly away from a mounting plate 138 secured to the vessel casing 119, the - 17 - insert ring can be extracted followed by the cartridge 10. For maximum safety in use, the lower orificed body 126 will be moved to close the duct when gas c injection is finished. It will be appreciated that it is important to avoid gas leakages. Provided the cartridge 10 is firmly pressed against the porous discharge block 18, leakage of gas downwardly outside the 1 Q cartridge 10 will be substantially prevented. Gas could leak from the cement or mastic joint between the insert ring 122 and the stationary upper plate, or along the interface between the two plates. Springs, not shown, bias the plates 15 126, 127 upwardly against the insert ring 122, and in ideal circumstances can assure adequate gas tightness between these parts. However, manu¬ facturing tolerances can work against the achievement of gas tightness. The construction of the cartridge 2 Q 10, in particular its compressible wads 14, 15, and its telescoping interfitting with the discharge block 18 significantly contribute to the attainment of gas tightness. The arrangement provides enough give for the refractory parts to adjust one to 2 another for the springs to press them leak tightly together . In a modification, not shown, the lower nozzle insert ring component 122 is integral with the orificed upper body 127- Desirably the resulting integral body is encased in a metal jacket apart from its plane lower surface (which the lower body 26 contacts) and its uppermost surface. Advantageously, the lower body 126 is identical in shape to such an integral body and has the same size bore, so that the bodies are interchangeable. Obviously this simplifies manufacture and minimises cost as well as rationalises the user's stock requirements. In such a modification, the design should be such that the cartridge is adequately compressed long- itudinally when the springs, not shown, are holding the orificed bodies 126, 127 to their proper operating positions. In the modification, the porous discharge block 18 is once more mounted in the nozzle block 24 and is replaced when defective by pushing it out of the block 24 in a downward direction, after first dismounting the components below the discharge block 18. The discharge block 18 can be made of porous or foraminous refractory, i.e. one possessing numerous tiny passages meandering randomly through it. As shown, however, the block 18 is made from gas- impermeable refractory material, rendered foraminous and gas-conducting by being pierced by one or more narrow, capillary-type passageways 20. The passageway(s) 20 can be formed by small bore tubing of refractory material such as alumina. Such tubing is embedded in the body of the block 18 as the latter is pressed or cast. 0 The bore size can, for example, be 1 mm or less in diameter. Alternatively, the passageways can be formed by pressing or casting the refractory mass to form the block 18 around filaments of 1 mm diameter or less e.g. of nylon or some other 5 material which burns away when the pressing or casting is subjected to an elevated temperature, for instance during firing. The resulting bore size can again be 1 mm or less, e.g. 0.6 mm, or even larger than 1 mm provided metal can be prevented 0 from flowing through the passageway(s) . Still further, the block 18 can be formed by pressing or casting around a plurality of wires of 1 mm diameter or less, said wires being subsequently pulled from the formed block thereby creating 5 the passageways. In use of the apparatus according to the invention, metal may freeze in or on the block 18. Oxygen lancing may then enable the block 18 capable of passing gas. Such lancing may permit the ° block 18 to be reused after the vessel has been emptied, if the block is otherwise in a good and safe condition. In use of the preferred arrangement con¬ sisting of the cartridge and a nozzle discharge end portion or nozzle plug pierced by capillary passages, the cartridge beneficially provides an even flow of gas to the contiguous face of the end portion or plug, while the passages therein ensure the gas enters the liquid as fine, well directed and directionally stable jets. Desirably, an end portion or plug having capillary passages has a central recess in its face contiguous with the cartridge. The capillary passages open to the recess which serves as a small plenum and ensures there is a ready supply of gas to the passages. Such a plug is shown in Fig. 5; it is cemented into the discharge end of the nozzle passage^ Whilst Fig. 4 shows a practical gas in¬ jection means 115 in simplified form, a preferred gas Injection device is shown in Figs. 5 to 7- Features of the preferred device 215 will now be described. The nozzle body 24, plug 18 and cartridge 10 are assembled and located as before in the vessel lining 118. The means to convey gas to cartridge 10 in the passage of the nozzle body 24, and to shut off this passage, are mounted on the exterior of the vessel 111. An adaptor plate 216 is e.g. welded to the metal shell 119 of the vessel and an apertured mounting plate 218 is bolted thereto. An insert collar 219 is bolted in the aperture . of the mounting plate and serves to centre the refractory insert ring 122. A stationary refractory plate 220 is held in contact with the insert ring 122 by a metal retaining plate 222. As before, the refractory plate 220 and insert ring 122 form a stepped joint which is sealed by a suitable seal¬ ant. The retaining plate .222 is circular in plan, and in section resembles a shallow cup having an onwardly-projecting rim or flange 223- The refract- ory plate 220 is seated and suitably sealed in the hollow of the retaining plate 222. The rim 223 of the latter is clamped in facial contact with the underside of the mounting plate 218 by a set of bolts 224 passing through key-hole openings 225 in the rim 223- Thus clamped, the retaining plate 222 holds the refractory plate sealed with the insert ring 122. The refractory plate 220 has a plurality of passages 226 across its thickness, located cen- trally, for passing gas to the upstream end of the cartridge 10 in contact therewith. The retaining plate 222 has a recess in the upper surface of its hollow, the recess being located beneath the passages 226 in the refractory plate. Also, a bore extends through the retaining plate to the recess, which serves as a plenum for the passages 226 when gas is passed through the said bore to the recess. The bore has a lining or insert 228 made of thermally conductive material such as carbon or copper. The underside of the retaining plate is machined smooth and flat. Assembled to the underside of the retaining plate 222 is a slide frame and a metal slide block. The slide block 230 has a passage 231 which nor- mally registers with the bore insert 228 thereabove. The passage 231 leads to an inlet fitting 232 for a gas supply line (not shown). The slide block 230 Is shown in its normal operating position in Fig. 5. In this position, it will be recognised that gas supplied to inlet fitting 232 will flow into and up passage 231, up bore insert 228, through refractory plate 220 and thence to the cartridge 10 and plug 18 for entry to the vessel's contents. The slide frame 234 comprises a pair of spaced-apart parallel side plates 235, 236 and a bottom plate 238. The side plates 235, 236 are fastened to the underside of the retaining plate 222 and depend from it. The bottom plate 238 is bolted to the side plates. The frame 23^ snugly but slidably receives the slide block 230. This has its topside machined smooth and flat to coact with the similarly-finished underside of the re¬ taining plate. There are springs 240 acting between the slide block 230 and the frame bottom plate 2*38 to urge the block into gas-tight facial contact with the retaining plate 222. A push rod 242 is secured to the slide block 230, the push rod leading to a manual act¬ uator, a hydraulic actuator or the like, not shown. The push rod 242 is for displacing the block 230 (to the left as viewed in Fig. 5) suddenly to shut off the gas supply and e.g. to close the equipment - against leakage of melt in the very unlikely event of failure of the plug 18 and cartridge 10. When the block 230 is thus displaced, a thermally con¬ ductive disc 244 seated in its topside is placed across the bore insert 228. The disc may be made of carbon or copper. Should molten matter e.g. metal leak out of the vessel, by-passing the plug 18 and cartridge 10, then it will be arrested by the disc 244. The thermally conductive nature of the disc and bore insert 228 should sufficiently chill the leakage to cause it to freeze safely, and thereby prevent molten matter escaping completely from the equipment. The retaining plate 222 as well as the slide frame 23 and slide block 231 secured thereto are fastened to the mounting plate 218 by bolts 224, and when the device 215 is assembled, the cartridge 10 is compressed longitudinally in this instance. The refractory plate 220 is held firmly and gas tightly against the insert ring 122. Further, bolts 224 are tightened sufficiently to force the rim 223 of plate 222 gas tightly against the mounting plate 218. If desired sealing means such as a fibre seal (not shown) may be located n the interface between the rim 223 and the mounting plate 218. When it is necessary to service the gas injection means, e.g. to replace the plug 18 and/or the cartridge 10, the bolts 224 will be slackened sufficiently for the retaining plate 222 to be rotated through a small angle placing the enlarged ends of the key-hole openings 225 opposite the heads of the bolts 224. The retaining plate includ¬ ing components affixed to or supported thereby can then be detached, thus giving access to the nozzle passage. The slide frame 234 and slide block 230 can be disassembled as necessary for servicing, and the refractory plate 220 can be replaced if required. The weight and bulk of the retaining plate 222 and the components carried thereby can be con¬ siderable. To avoid the risk of this assembly being dropped inadvertently when it is rotated for release, the retaining plate 222 is desirably linked to the mounting plate 218 by a hinge means 248 secured to the latter. An arm 249 extends from the hinge 248 towards the underside of the frame bottom plate 238 and a swivel connection is formed between this plate and the arm by a spigot and socket 250 or another attachment. Further, a handle 252 is attached to the retaining plate 222. Thus, after slackening the bolts 224, the plate 222 is rotated by means of the handle 252 and, once the bolt heads align with the enlarged ends of the key-hole openings 225, the plate 222 is swung downwards on the arm 249 about the hinge 248. The latter for convenience has a dismountable pivot pin to permit the retaining plate 222 to be removed completely from the mounting plate 218. Reassembly of this gas injection device will in essence be the reverse of its disassembly and will be apparent from the foregoing description. The cartridge 10 of Figs. 1 to 5 can bene¬ ficially be modified, as can the upper orificed body 127 of Fig. 4 and the refractory plate 220 of Fig. 5, all in the interests of attaining a good, gas tight seal at the upstream end of the cartridge, to render minimal or eliminate loss of gas through leakage. Possible modifications are shown in Fig. 8. Cartridge 10' again comprises a sleeve 11' e.g. of metal filled with particulate refractory material 16', which is held in place by wads -14', 15' of compressible, fibrous refractory material located in the end regions of the cartridge. In this mod¬ ification, both the lower and upper wads 14', 15' are inset a short distance from the corresponding extreme ends of the sleeve 11'. Moreover, the sleeve 11' has no inturned lip at its lower end. As explained hereinbefore, the upper wad 15' is inset to ensure a gas-tight sealing between the cartridge 10' and end-closing means or block 18. The lower wad 14' is Inset for a like purpose, for creating a seal with the orificed body 127' or refractory plate 220'. The latter .body or plate is furnished with an upstanding protrusion 127A, 220A on its upper surface sized to fit closely into the bottom or upstream end of the sleeve 11', to press against the lower wad 14'. The distance by which the lower wad 14' is inset, and the height of the protrusion 127A, 220A are such as to ensure that when the in¬ jection apparatus is properly set up for injection, both wads 14', 15' are duly compressed to form eff¬ ective seals at the ends of the cartridge 10'. Thus, gas can be fed into and from the cartridge without fear of significant leakage of gas. As shown, body 127' or plate 220' is pierced by small bores, but it could have a single, larger bore such as shown in body 127 of Fig. 4. If desired, the end closing means or plug 18 and/or the body 127' or plate 220' can be recessed as shown by chain- dotted lines, t.o provide a plenum therein. Industrial Applicability The injection cartridge and apparatus with which the cartridge is used are applicable to the introduction of gases into molten metals contained in vessels such as ladles. The molten metals can be ferrous or non-ferrous, and gases can be intro¬ duced to achieve thermal and/or compositional uni¬ formity of the melt before it is poured from the ladle, or to change its chemical composition.

Claims: CLAIMS : 1. An injection cartridge, for use in in¬ jecting gas through the wall of a vessel into a high temperature liquid contained therein, the car- tridge (10) comprising an open-ended gas-impermeable sleeve (11) blocked adjacent each of its opposite ends by a compressible wad (14 or 15) of fibrous refractory material, and containing a filling (16) of particulate refractory matter, the cartridge being permeable to gas flow from one end to the other and impermeable to liquid flow therethrough. 2. A cartridge according to claim 1, wherein the sleeve (11) is a metal tube. 3. A cartridge according to claim 1 or claim 2, wherein the particulate filling (16) includes sand or sand and graphitic material. 4. A gas injection apparatus comprising a cartridge (10) according to any of claims 1 to 3 and a refractory gas-discharge block (18) arranged in tandem therewith, the discharge block (18) having one end interfitting (at 21) with one end of the cartridge and being porous or foraminous to allow gas but not liquid to traverse the block. 5- Apparatus according to claim 4, wherein the discharge block (18) is pierced by a plurality of capillary passages (20) for conveying gas through the block. 6. A gas injection nozzle, for installation in the wall of a vessel and for use in injecting gas into a high temperature liquid, comprising a refractory nozzle body (24) having a passage (25) therein and a gas porous or foraminous end portion (18) closing the passage at a discharge end (26) of the body, and closely fitted in the passage (25) is a porous gas injection cartridge (10) comprising an open-ended, gas-impermeable sleeve (11) having upstream and downstream ends, closed adjacent each end by a compressible wad (14 or 15) of fibrous refractory material and containing a filling (16) of particulate refractory matter, the cartridge being permeable to gas flow from the upstream to the downstream end and impermeable to liquid flow therethrough. 7. A nozzle according to claim 6, wherein the passage (25) extends wholly through the body (24) and the said end portion (18) is a plug element fitted liquid-tightly into a discharge end of the passage. 8. A nozzle according to claim 7, wherein the plug element (18) is an expendable item of the nozzle. 9. A nozzle according to claim 6, 7 or 8, wherein the said end portion (18) is rendered gas permeable by capillary passages (20) extending there¬ through. 10. A nozzle according to any of claims 6 to 9, wherein the sleeve (11) of the cartridge is a metal tube. 11. A nozzle according to any of claims 6 to 10, wherein the particulate filling of the car¬ tridge includes sand or sand and graphitic material. 12. A nozzle according to any of claims 6 to 11, wherein the end portion (18) is configured (at 21) to interfit with the downstream end of the .*» cartridge (10). 13- A nozzle according to any of claims 6 to 12, wherein the cartridge is an expendable item. 14. Gas injection apparatus comprising a nozzle (24) according to any of claims 6 to 13 and gas inlet means (126, 127) for conveying gas from a supply to the upstream end of the cartridge, the inlet means being adapted to urge the cartridge (10) into sealing contact with the said end portion (18), whereby In use any liquid which may permeate through the end portion is blocked from escaping via the passage by the liquid-impermeable cartridge. 15- Metal pouring apparatus comprising a container vessel (111) for molten metal, an opening (112) in or adjacent the bottom of the vessel and associated means (114) operable to control teeming of molten metal through the opening, and means (115) for injecting gas into molten metal in the vessel, the injecting means including a nozzle (24) installed in a wall (118) of the vessel in the vicinity of and separate from the said opening (112) and the teeming control means (114), and ducting exteriorly of the vessel for conveying gas to a passage through the nozzle, the ducting including two abutting ori¬ ficed refractory bodies (126, 127), one of the re- *. fractory bodies (e.g. 126) being movable relative to the other to place the orifices out of registry thereby to close the ducting and prevent any molten metal entering the nozzle passage (25) from escaping from the vessel via the nozzle and ducting, and inside the passage (25) there is melt-tightly fitted an injection cartridge (10) comprising an open-ended, gas-impermeable sleeve (11) closed adjacent each of its opposite ends by a compressible wad (14 or 15) of fibrous refractory material and containing a filling of particulate refractory matter (16), the cartridge being permeable to flow of gas towards the vessel interior and impermeable to flow of molten metal therethrough. 16. Gas injection apparatus for introducing gas into a container vessel for molten metal via an opening in or adjacent the bottom of the vessel, comprising a nozzle (24) for installation in the said opening of the vessel, the nozzle having a passage (25) with a gas permeable closing means (18) through which gas in use is passed to the melt, there being melt-tightly and gas-tightly fitted inside the passage an injection cartridge (10) com¬ prising an open-ended, gas-impermeable sleeve (11) blocked adjacent each of its opposite ends by a compressible wad (14 or 15) of fibrous refractory material and containing a filling (16) of particulate refractory matter, the cartridge (10) being permeable to flow of gas towards the vessel interior and im¬ permeable to flow of molten metal therethrough, and ducting in operative, gas-tight juxtaposition with the nozzle passage (25) and its cartridge (10) for conveying gas thereto from a supply, the ducting including a stationary e.g. metal body (222), a movable e.g. metal body (230) and means to bias the latter into gas-tight, slidable contact with the former, the bodies (222, 230) having orifices therein which, in a first position of the movable body (230) are registered for passing gas to the nozzle (24), and in a second position thereof are out of registry for closing the ducting, the station- ary body (222) having an insert sleeve (228) defining its orifice and the movable body (230) having an imperforate insert (244) positioned therein to reg¬ ister with the insert sleeve when the movable body is moved to the duct-closing position, the two in- serts (228, 244) being made of highly thermally conductive materials. 17. Apparatus according to claim 16, wherein the stationary body (222) has a refractory plate element (220) mounted thereto, the plate element being perforated to convey gas from the orifice of the stationary body to the nozzle passage (25), and there being sealing means between the plate element and nozzle (24) and between the former and the stationary body. 18. Apparatus according to claim 16 or claim 17, wherein the nozzle (24) has a porous or foram¬ inous closing means (18) at a gas discharge end thereof, and the cartridge (10) is compressed between the closing means (18) and the said bodies (222, 230). 19- Apparatus according to claim 18, wherein the closing means (18) is a solid plug fitted in a discharge end of the nozzle (24), the plug being formed from substantially gas-impermeable refractory material and being pierced by a capillary passageway (20), or a plurality thereof, for passing gas into the vessel. 20. Apparatus according to claim 18, wherein the foraminous closing means (18) is an integral part of the nozzle (24) and is pierced by a capillary passageway (20), or a plurality thereof, for passing gas into the vessel. 21. Apparatus according to any of claims 16 to 20, wherein the cartridge (10) has a metal tube forming said sleeve (11). 22. Apparatus according to any of claims 16 to 21, wherein the particulate filling includes sand, or sand and graphitic material. 23- Apparatus according to any of claims 15 to 22, wherein a portion (127A, 220A) of said ducting projects Into, and is a close fit in, an upstream end of the cartridge sleeve (11) the pro¬ jecting portion being perforated to convey gas into the sleeve and, in use, being pressed against a compressible wad (14, 14') of the cartridge (10). - 35 - 24. A method of metal pouring employing app¬ aratus as claimed in any of claims 15 to 23, wherein gas is injected into the molten metal in the vessel through the gas injection means (115) simultaneously with teeming the metal from the container via teeming control means (114) of the container.

Inventors: GELSTHORPE JOHN RICHARD, THROWER ANTHONY, GELSTHORPE, JOHN, RICHARD, THROWER, ANTHONY
Applicants: INJECTALL LTD, INJECTALL LIMITED
Application year: 1988
Main classification: C21C7
IPC codes: B22D1, C21C5, C21C7, C22B9, F27D3