Semiconductive resin composition

Abstract: A semiconductive resin composition comprising 100 parts by weight of a polymer component comprising an ethylene-based copolymer, an ethylene-propylene rubber, and a low molecular weight polyethylene having an average molecular weight of 1,000 to 4,000, and 40 parts by weight or more of electroconductive carbon black.

Description: FIELD OF THE INVENTION This invention relates to a semiconductive resin composition suitable for forming internal- or external-semiconductive layers of high voltage power cables having polyethylene or crosslinked polyethylene as insulator, and, especially, to a semiconductive resin composition which can provide improved water tree resistance. BACKGROUND OF THE INVENTION High voltage power cables using polyethylene or crosslinked polyethylene as an insulator are provided with an internal semiconductive layer surrounding the outer periphery of the conductor and an external semiconductive layer surrounding the outer periphery of the insulator. Internal semiconductive layers relax heterogeneous electrical stress attributed to irregularities in the twisted wires in conductors, and also increase the adhesion between the conductor and the insulator. External semiconductive layers homogenize the electrical stress on the insulator surface. Generally, for forming the semiconductive layers, an ethylene-based copolymer used as a base polymer, such as an ethylene-vinyl acetate copolymer and ethylene-ethyl acrylate copolymer, mixed with conductive carbon black, is used. When the conductive carbon black is not sufficiently dispersed in the base polymer, coarse grains are formed by coagulation of the carbon black particles. When the grains are formed in the interface between the insulator and the semiconductor layers, water tree deterioration initiates from these grains. JP-A-59-8216 discloses a method of improving the water tree resistance by blending ethylene-propylene rubber with an ethylene-based copolymer, to prevent the formation of grains. (The term "JP-A" as used herein means an "unexamined published Japanese patent application".) According to this method, a large shearing stress is generated at the time of dispersing the conductive carbon in the polymer by using kneaders such as a Banbury mixer so that the grains are finely divided to become harmless. The above composition is, however, so viscous that a commonly used manufacturing method for high voltage cables, i.e., the common extruding method, cannot be applied. In the common extruding method, the semiconductive layer and the insulator layer are simultaneously extruded on the outer surface of the conductor using a common crosshead. This method avoids a disconformity between the semiconductor and the insulating layers. Since the common crosshead is used for both the layers, the extruding temperature of the semiconductive layer is restricted to be the same as that of the insulator layer or lower. When a crosslinked polyethylene insulator is used, the temperature is limited to 130°C or less. In the case of the above composition comprising an ethylene-based copolymer blended with an ethylene-propylene rubber, the viscosity is extremely high so that the extrusion becomes very difficult. SUMMARY OF THE INVENTION The present invention was made to solve the above problems. Therefore it is an object of the present invention to provide a semiconductive resin composition having an excellent extrusion workability which suppresses water tree formation. A semiconductive resin composition according to the present invention comprises: (a) 100 parts by weight of a polymer component comprising an ethylene-based copolymer selected from the group consisting of ethylene-vinyl acetate copolymers, ethylene-ethyl acrylate copolymers and ethylene-methyl methacrylate copolymers, an ethylene-propylene rubber, and a low molecular weight polyethylene having an average molecular weight of 1,000 to 4,000, and (b) 40 parts by weight or more of electroconductive carbon black. DETAILED DESCRIPTION OF THE INVENTION The ethylene-based copolymers used in the present invention are selected from ethylene-vinyl acetate copolymers, ethylene-ethyl acrylate copolymers and ethylene-methyl methacrylate copolymers. Either ethylene-propylene copolymers or ethylene-propylene-unconjugated diene terpolymers are useful as ethylene-propylene rubbers. A chief feature of the present invention resides in that a low molecular weight polyethylene having an average molecular weight between 1,000 and 4,000 is blended as a third component in addition to an ethylene-based copolymer and an ethylene-propylene rubber. By this, the viscosity is lowered to enable a common extrusion while maintaining the water tree resistance. The low molecular weight polyethylene to be used is a waxy material having a softening point between 100 and 130°C. Waxy materials such as paraffin wax or microcrystalline wax having softening or melting points lower than the above temperature range melt in the initial steps of kneading with carbon black, so that no high shearing stress can be obtained. Therefore, though viscosity is lowered, the grains are not reduced and the water tree resistance cannot be maintained. A low molecular weight propylene, which has a high softening point, does not melt at the common extrusion temperature and generates sufficiently high shearing stress to greatly reduce the amount of the grains, but the extrusion operation becomes impossible due to the high viscosity. Further, stearic acid amides or zinc stearates having softening or melting points between 100 and 130°C, but with low molecular weights, are prone to move to the surface of the semiconductor layer. Also, they act as external lubricants between the processing machine and the material to avoid the sticking. Therefore, they are unsuitable for lowering the viscosity. Preferably, the composition comprises 40 to 90 wt% ethylene-based copolymer, 5 to 30 wt% ethylene-propylene rubber, and 5 to 30 wt% low molecular weight polyethylene. When the ethylene-propylene rubber content is too low, the grain formation and water trees are not effectively suppressed, whereas too high a content makes the common extrusion unoperable due to the increased viscosity. The content of the low molecular weight polyethylene varies depending on the content of the ethylene-propylene rubber. Too low a content is insufficient to effectively lower the viscosity, and too high a content fails to suppress the grain formation. Carbon blacks used in the present invention include those of common types used as a conductivity imparting agent, such as furnace black, acetylene black, and Ketjen black. These can be used alone or in combinations of two or more thereof. Most effective among them in decreasing the grain formation is the furnace carbon black with an arithmetic mean particle size of 25 to 40 mµ, an iodine adsorption of 40 to 60 mg/g and a DBP oil absorption (by JIS A method) of 120 to 150 mℓ/100g. The arithmetic mean particle size is that obtained by electron microscopic observation. Particles smaller than 25 mµ increase the viscosity so that the extrusion workability is decreased, and particles having a particle size exceeding 40 mµ tend to give insufficient conductivity. In addition, a composition with an iodine adsorption of less than 40 mg/g is deficient in conductivity, whereas one exceeding 60 mg/g is deteriorated in extrusion workability due to a too high viscosity. The DBP oil absorption is measured by the JIS A method. When it is lower than 120 mℓ/100 g, the conductivity obtained is not high enough and a value higher than 150 mℓ/100 g increases the viscosity of the composition and adversely affects the extrusion workability. Acetylene black may be used together with the above furnace black so far as the viscosity of the composition is not considerably increased. The addition of the conductive carbon black should be 40 parts by weight or higher per 100 parts by weight of the polymer component. If the addition is lower than this lower limit, the conductivity obtained is not high enough. Lubricants, antioxidants, and inhibitors against metallic damage and deterioration may be added to the composition of the present invention. Preferable lubricants are those acting as external lubricants which prevent adhesion of the composition to the processing machine. Examples of such lubricants are aliphatic alcohols, esters of fatty acids, metal salts of fatty acids, and fatty acid amides. They can be used independently or in combinations of two or more. Examples of antioxidants include thiobisphenols, alkylidenebisphenols, alkylphenols, hydroxybenzyl compounds, aminophenols, hydroxyphenyl propionates, sec-aromatic amines, thioethers, phosphites and phosphonites. They may be used independently or in combinations of two or more thereof. The composition of the present invention may be crosslinkable or noncrosslinkable. In the case of the former, generally used as the crosslinking agents are organic peroxides. Examples of such agents include dialkyl peroxides, such as dicumyl peroxides, 1,3-bis(tertbutylperoxyisopropyl)benzene, 2,2-dimethyl-2,5-di(tertbutylperoxy)hexine-3. The present invention is now illustrated in greater detail with reference to Examples and Comparative Examples. In these examples, all percents and parts are by weight unless otherwise indicated. EXAMPLES The components were kneaded with a Banbury mixer to give the compositions of Examples 1 to 13 and Comparative Examples 1 to 8 shown below. Each composition thus obtained was fed to an extruder to form internal and external semiconductive layers together with a polyethylene insulator on a copper twisted wire conductor having a cross sectional area of 150 mm² by extrusion coating using a common head. The thickness of the layers was 1 mm each for the internal and the external semiconductive layers and 4 mm for the polyethylene insulator layer. The extrusion temperature for both the internal and external semiconductive layers was 120°C. After extrusion, crosslinking was effected by heating to give crosslinked polyethylene insulated power cables. The insulating layer was prepared by mixing 100 parts of a low density polyethylene(with a density of 0.920 g/cm³ and a melt index of 1.0 g/10 min.) with 2.5 parts of dicumyl peroxide as the crosslinking agent and 0.25 parts of 4,4'-thio-bis(3-methyl-6-tert-butylphenol) as the anti-oxidant. EXAMPLE 1 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 90 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 5 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 5 parts 4,4'-Thio-bis(3-methyl-6-tert-butyl-phenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 2 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 5 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 3 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 75 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 15 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 4 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 60 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 20 parts Low molecular weight polyethylene (average molecular weight of 2,000; softening point of 107°C) 20 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 5 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 40 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 30 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 30 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 6 Ethylene-ethyl acrylate copolymer (containing 17% of ethyl acrylate; with melt index of 18) 80 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 4,000; softening point of 126°C) 10 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 7 Ethylene-ethyl acrylate copolymer (containing 17% of ethyl acrylate; with melt index of 18) 60 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 20 parts Low molecular weight polyethylene (average molecular weight of 4,000; softening point of 126°C) 20 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts EXAMPLE 8 EXAMPLE 9 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 5 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Furnace carbon black (with arithmetic mean particle size of 30 mµ; iodine adsorption of 53 mg/g; DBP oil absorption of 133 mℓ/100 g) 75 parts EXAMPLE 10 EXAMPLE 11 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 5 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Furnace carbon black (with arithmetic mean particle size of 22 mµ; iodine adsorption of 104 mg/g; DBP oil absorption of 129 mℓ/100 g) 75 parts EXAMPLE 12 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 5 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Furnace carbon black (with arithmetic mean particle size of 43 mµ; iodine adsorption of 44 mg/g; DBP oil absorption of 115 mℓ/100 g) 75 parts EXAMPLE 13 COMPARATIVE EXAMPLE 1 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 100 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 2 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 15 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-buty-peroxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 3 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 5,000; softening point of 111°C) 5 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 4 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 80 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Paraffin wax (melting point of 66°C) 10 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 5 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 80 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Microcrystalline Wax (melting point of 90°C) 10 parts 4,4'-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 6 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 88 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Zinc stearate (melting point of 120°C) 10 parts 4,4′-Thio-bis(3-methyl-6-tert-butyl-phenol) 2 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 7 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 80 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (softening point of 145°C) 10 parts 4,4′-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 65 parts COMPARATIVE EXAMPLE 8 Ethylene-vinyl acetate copolymer (containing 14% of vinyl acetate; with melt index of 15) 85 parts Ethylene-propylene rubber (with Mooney viscosity of ML₁+₄=40) 10 parts Low molecular weight polyethylene (average molecular weight of 1,500; softening point of 105°C) 5 parts 4,4′-Thio-bis(3-methyl-6-tert-butylphenol) 0.5 parts 1,3-Bis(tert-butylperoxyisopropyl)benzene 0.5 parts Acetylene black 35 parts The compositions given above and the cables prepared by using them were evaluated and the results are given in Table 1 below. Evaluations were made according to the following. Extrusion workability: the state of the cable at extrusion was observed, i.e., it was decided whether common extrusion was applicable or not. Grain (particle generation): a compound kneaded with a Banbury mixer was extruded into a 1 mm thick and 30 mm wide tape using an extruder with a barrel diameter of 30 mm, and the surface of the tape was visually observed. Water tree: water was poured into the conductor of the cable and the cable was immersed in water while applying an alternating voltage 15 kV at 50 Hz between the conductor and the water electrode, at 90°C for 18 months. The insulator was then spiral-cut, boiled in an aqueous Methylene Blue solution, and the interfaces between the insulator and the internal semiconductor layer and between the insulator and the external semiconductor layer were subjected to microscopic observation to investigate whether water trees were formed or not. Volume resistivity: measurements following the AEIC-CS5-82 method were performed on the outside semiconductive layer. Extrusion workability particles (piece/200 cm²) Water tree Volume resistivity (Ω·cm) Examples of the Invention 1 good 2 nil 6×10¹ 2 good 2 nil 9×10¹ 3 good 2 nil 3×10² 4 good 1 nil 4×10² 5 good 3 nil 9×10² 6 good 2 nil 8×10¹ 7 good 2 nil 4×10² 8 good 2 nil 7×10¹ 9 good 4 nil 1×10² 10 good 5 nil 5×10² 11 good 7 nil 1×10³ 12 good 7 nil 5×10³ 13 good 6 nil 3×10³ Comparative Examples 1 good 25 Observed 2×10¹ 2 unextrudable 2 Unmeasurable Unmeasurable 3 unextrudable 4 Unmeasurable Unmeasurable 4 good 22 Observed 8×10¹ 5 good 21 Observed 9×10¹ 6 unextrudable 5 Unmeasurable Unmeasurable 7 unextrudable 3 Unmeasurable Unmeasurable 8 good 21 Observed 10⁶ < Samples 1 to 13 of the present invention were readily manufactured by the common extrusion, showed extremely low tendency to form grains, were completely free from water trees and had a low volume resistivity. Comparative Example 1 using only an ethylene-vinyl acetate copolymer as the base polymer formed a large amount of grains and water trees. Comparative Example 2 was the case where an ethylene-vinyl acetate copolymer and an ethylene-propylene rubber were used as the base polymer. In this case, the viscosity was too high that the common extrusion was impossible. Comparative Examples 3 to 7 were the cases where waxy substances beyond the scope of the present invention were used. Therefore, the common extrusion was impossible in some cases, and grains and water trees were formed in other cases. In Comparative Example 8 the amount of carbon black was below the specified value, and the volume resistivity was too high for a semiconductive layer.

Claims: A semiconductive resin composition comprising: (a) 100 parts by weight of a polymer component comprising an ethylene-based copolymer selected from the group consisting of ethylene-vinyl acetate copolymers, ethylene-ethyl acrylate copolymers and ethylene-methyl methacrylate copolymers, an ethylene-propylene rubber, and a low molecular weight polyethylene having an average molecular weight of 1,000 to 4,000, and (b) 40 parts by weight or more of electroconductive carbon black. A semiconductive resin composition as in claim 1, wherein the polymer component comprises 40 to 90 wt% ethylene-based copolymer, 30 to 5 wt% ethylene-propylene rubber, and 30 to 5 wt% low molecular weight polyethylene having a average molecular weight of 1,000 to 4,000. A semiconductive resin composition as in claim 1, wherein the conductive carbon black is at least one member selected from furnace carbon black and acetylene black. A semiconductive resin composition as in claim 3, wherein the furnace carbon black has an arithmetic mean particle size of 25 to 40 mµ, an iodine adsorption of 40 to 60 mg/g, and a DBP oil absorption (measured by JIS A method) of 120 to 150 mℓ/100 g. A semiconductive resin composition as in claim 1, wherein the composition further comprises an antioxidant. A semiconductive resin composition as in claim 5, wherein the antioxidant is 4,4'-thio-bis(3-methyl-6-tert-butylphenol). A semiconductive resin composition as in claim 1, wherein the composition further comprises a crosslinking agent. A semiconductive resin composition as in claim 7, wherein the crosslinking agent is 1,3-bis(tert-butylperoxyisopropyl)benzene.

Inventors: HANAWA KATSUTOSHI, MARUMO MORITADA, SHIINA TOSHIO, SHIMAZAKI YUKIO, WATANABE KIYOSHI, YAGYU HIDEKI, HANAWA, KATSUTOSHI, MARUMO, MORITADA, SHIINA, TOSHIO, SHIMAZAKI, YUKIO, WATANABE, KIYOSHI, YAGYU, HIDEKI
Applicants: HITACHI CABLE, HITACHI CABLE, LTD.
Application year: 1988
Main classification: H01B1
IPC codes: C08L23, H01B1, C08K3