SUPERCONDUCTIVE CERAMIC WIRE AND METHOD FOR MAKING SAME

Abstract: The present invention is related to a superconductive ceramic wire and a method for making same. According to the first aspect of the invention, there is provided a method for making a superconductive ceramic wire, the method comprising the steps of: (a) preparing a superconductive porous ceramics (2); (b) depositing lead (3) in the pores of the ceramics; (c) covering the lead-depositted ceramics with a metal (1); and (d) extending the metal-clad and lead-depositted ceramics. According to the second aspect of the invention, there is provided a superconductive ceramic wire which is obtained by: (a) preparing a superconductive porous ceramics (2); (b) depositing lead (3) in the pores of the ceramics; (c) covering the lead-depositted ceramics with a metal (1); and (d) extending the metal-clad lead-depositted ceramics.

Description: The present invention is related to a superconductive ceramic wire and a method for making same. It has been known that composite oxides, referred to as superconductive ceramics hereinafter, composed mainly of yttrium-including rare earth element (denoted hereinafter by R), an alkaline earth metal, copper and oxygen show a superconductivity at a temperature of 77°K which is higher than a boiling point of nitrogen. A conventional method for making the above-mentioned superconductive ceramics is as follows. First, powdery raw materials, that is, an R oxide (R₂O₃), a carbonate of an alkaline earth metal and copper oxide (CuO), average particle diameter being not larger than 10 um, are mixed at a molecular proportion of 0.5 : 2 : 3, respectively. Second, the mixed raw materials is heat-treated at a temperature between 850°C and 950°C for at least 24 hours in an oxygenous atmosphere to form a superconductive ceramic powder. In order to obtain a superconductive ceramic wire, thus obtained superconductive ceramic powder is sintered to make a sintered block therefrom, the block is charged in a silver or copper pipe, and a diameter thereof is reduced to be in the order of 5 mm by cold swaging, rolling or dieing. Another conventional method for diametrical reduction is to hot extrude the sintered ceramic block. A problem as to the above-mentioned conventional processing for obtaining a superconductive ceramic wire is that fissures and hollows are apt to be created in the superconductive material during the diametrical reduction because of the poor extensibility of the ceramics. As the fissures and hollows spoil superconductivity, namely the critical temperature and the critical electric current density Jc, of the material, diametrical reduction rate has to be kept lower than a certain level. A problem as to the superconductive ceramic wire obtained by a conventional method is that the diameter of the wire is not enough small and the material often has fissures and hollows which spoil the superconductivity. Therefore, electric resistance and critical electric current density which might be obtained in a massive superconductive ceramics is not obtained in the superconductive ceramic wires. An object of the method for making superconductive ceramic wire according to the first aspect of the present invention is, therefore, to provide a method for making a superconductive ceramic wire which enables a high diametrical reduction of the wire. Another object of the present invention is to provide a method by which creation of fissures and hollows in the wire is restrained. Further object of the invention is to provide a method for making a superconductive ceramic wire having superconductivity and high Jc. By virtue of the extensibility of lead depositted in the pores of the superconductive material, fissures and hollows are prevented from occurring. Even if they occur, they are filled with the lead. Second aspect of the present invention provides a superconductive ceramic wire having a small diameter. Another object of the second aspect is to provide a superconductive ceramic wire having little fissure and hollows therein. Further object thereof is to provide a superconductive ceramic wire having superconductivity at a boiling point of nitrogen and a high Jc. According to the first aspect of the present invention, there is provided a method for making a superconductive ceramic wire, the method comprising the steps of: (a) preparing a superconductive porous ceramics; (b) depositing lead in the pores of the ceramics; (c) covering the lead-deposited ceramics with a metal; and (d) extending the metal-clad and lead-depositted ceramics. According to the second aspect of the present invention, there is provided a superconductive ceramic wire which is obtained by: (a) preparing a superconductive porous ceramics; (b) depositing lead in the pores of the ceramics; (c) covering the lead-deposited ceramics with a metal; and (d) extending the metal-clad and lead-deposited ceramics. Figure 1 shows schematically a cross-section of a superconductive wire obtained according to the present invention. Figure 2 shows schematically a cross-section of a superconductive wire wherein the amount of lead depositted is insufficient. Figure 3 shows schematically a cross-section of a superconductive wire wherein an excessive amount of lead is depositted. Preferred embodiment of the present invention will now be explained. According to an embodiment of a method for making a superconductive ceramic wire, lead is laid in the pores of a superconductive porous ceramics essentially composed of an yttrium-including rare earth element, an alkaline earth metal, copper and oxygen. The lead deposited superconductive ceramics is covered by a metal sheath. Then, the metal-clad and lead deposited superconductive ceramics is extended. The lead deposited in the pores acts as a lubricator while the material is extended with the metal sheath. When fissures and hollows are formed in the superconductive material during the extension, the lead fills the defects to moderate their defective effects on the superconductivity. Thus a superconductive wire with little fissures and hollows is made. Lead has been used to fill the pores because lead has low hardness, substantial extensibility and deformability, consequently considerable workability and superconductivity though it appears as low a temperature as 9°K. Preferably, total amount of lead filling the hollow spaces in the ceramics is between 5% and 40% by volume of the porous superconductive ceramics. If the proportion is smaller than 5%, critical temperature becomes lower than 77°K because of substantial fissures and hollows existing between ceramic particles. If the proportion is higher than 40%, the critical temperature and the critical current density decreases because ceramic particles are out of contact to each other because of lead layers coming therebetween. Pores in the ceramic material are not easily filled with lead because the two materials are not affinitive to each other. By chemical-plating a copper or tin layer on the porous superconductive ceramics precedently, lead can be deposited thereon effectively. The chemical-plating also increases the bonding strength between the ceramics and metal sheath, consequently largely improving the extension rate and workability of the material. As explained above, method for making superconductive ceramic wire according to the first aspect of the present invention enables a high diametrical reduction in extending the wire. The method restrains a creation of fissures and hollows in the wire during the extension processing. It becomes possible to perform a extension at a extension rate higher than 80% while maintaining a superconductivity of the base material. Further, the method enables to provide a method for making a superconductive ceramic wire having superconductivity at a high temperature and having a high Jc. Superconductive ceramic wire according to the second aspect of the present invention has a small diameter and has little fissure and hollows therein. Further, the superconductive wire has superconductivity at a high temperature and a high Jc. Further, the copper sheath for retaining superconductive ceramics therein may be replaced by a silver sheath and the copper plating formed on the porous ceramics may be replaced by a tin plating. Examples A superconductive ceramic wire is made according to the first aspect of the present invention and characteristics of the wire is examined, as follows. Following raw materials, from (1) to (3), are prepared. (1) Yttrium oxide (Y₂O₃) in a powdery state having an average particle diameter of around 6 µm. (2) Barium carbonate (BaCO₃) in a powdery state having an average particle diameter of around 6 µm. (3) Copper oxide (CuO) in a powdery state having an average particle diameter of around 6 µm. Above raw materials are mixed at a following molecular ratio. Y₂O₃ : BaCO₃ : CuO = 0.5 : 2 : 3 Then, the mixture of the raw materials is heat treated at a temperature of 900°C, for 24 hours and in an atmosphere to obtain a superconductive ceramic material having a composition of YBa₂Cu₃O₇ and a perovskite structure. Next, thus obtained superconductive ceramic material is pulverized to a superconductive powder having an average particle diameter of 5 µm. The superconductive ceramic powder is mixed with a binder, paraffin or stearic acid for example, and formed in a cylindrical shape of 20 mm in diameter and 100 mm in length. The formed ceramic powder is heat-treated at a temperature of 930°C for 24 hours at an oxygenous atmosphere and a porous superconductive ceramic pellet is obtained. Copper is chemical-plated on the porous ceramic pellet in order to improve the affinity of the pellet to lead. More in detail, the ceramic pellet is surface treated by palladium to form a catalyst layer of palladium thereon. Then copper ion is deposited to form a layer of metal copper thereon. Thickness of the copper layer is about 1 µm. Moisture is dried out of the surface thereof. A tin layer may be formed by substituting the copper layer by tin. The copper clad ceramic pellet is soaked in pressurized molten lead and the molten lead is depositted in the pores formed in the pellet. The amount of lead deposited in the pellet is varied as shown in Table 1. Thus obtained ceramic pellet having a lead deposition formed thereto is sheathed in a copper tube of 23 mm in outer diameter, 20 mm in inner diameter and 200 mm in length. Finally, the pellet and the copper tube are rotary swaged and formed with a die so as to reduce its diameter to 1 mm. Thus, a superconductive ceramic wire is obtained. Diametrical reduction rate of the extension processing is 95.6%. Table 1 shows the critical temperature Tc(°K) and critical electrical current density at 77°K (A/cm²) of the ceramic wire. Figures 1, 2 and 3 show schematically a cross section of the ceramic wires Example No.4, 2 and 6, respectively. Superconductive ceramic particles 2 are in contact to each other but have openings also therebetween. Lead 3 is depositted in some of the openings. The ceramic particles 2 and the lead 3 are sheathed in a copper tube 1. As to the example No.4 shown in Figure 1 wherein the amount of depositted lead is 15% of the ceramic material, most of the outer openings are filled with the lead but the inner openings remain vacant. Table 1 shows that the Example No.4 has both a high critical temperature (91°K) and a high critical electric current density (4,700 A/cm²). The character is obtained when only the outer openings are filled with lead and the inner openings are left vacant as this example. As to the Example No.2 shown in Figure 2 wherein the amount of lead is 3% of the ceramic material by volume, some of the outer openings are filled with the lead but there remain vacant openings also at an outer side. Inner openings are vacant. In this example, the amount of lead is not enough and fissures and hollows generate and obstacle a path of electricity. As to the Example No.6 shown in Figure 3 wherein amount of lead is 50% of ceramic material by volume, virtually all the openings are filled with lead. Further in this example, lead layer comes between ceramic particles to increase resistance therebetween. The comparative study shows that good results are obtained when the amount of lead deposited in the superconductive ceramic pellet is between 5% and 40%, that is, examples No.3, 4 and 5. No. proportion of lead deposition by ceramic material (volume %) Critical temperature Tc (°K) Critical Electric Current Density Jc (A/cm²) at 77°K 1 0 - no superconductivity 2 3 93 1,600 3 5 91 4,700 4 15 90 4,600 5 40 92 2,600 6 50 90 700

Claims: A method for making a superconductive ceramic wire, the method comprising the steps of: (a) preparing a superconductive porous ceramics; (b) depositing lead in the pores of the ceramics; (c) covering the lead-deposited ceramics with a metal; and (d) extending the metal-clad and lead-deposited superconductive ceramics into a wire. A method for making a superconductive ceramic wire according to claim 1 which further comprises a step of making a layer of copper on the superconductive porous ceramics before depositing lead thereon. A method for making a superconductive ceramic wire according to claim 1 which further comprises a step of making a layer of tin on the superconductive porous ceramics before depositing lead thereon. A method for making a superconductive ceramic wire according to claim 1 wherein the porous ceramics is essentially composed of at least one yttrium-including rare earth element, at least one alkaline earth metal, copper and oxygen. A method for making a superconductive ceramic wire according to claim 4 wherein the superconductive porous ceramics is prepared by; (a) mixing powdery yttrium oxide (Y₂O₃), powdery barium carbonate (BaCO₃), powdery copper monoxide (CuO) at a molecular proportion of 0.5 : 2 : 3; (b) making a compound of having a composition of YBa₂Cu₃O₇ and a perovskite structure by heat-treating the powdery mixture; (c) pulverizing the compound; (d) mixing the pulverized compound with a binding material; and (e) heat-treating the mixture of powdery YBa₂Cu₃O₇ and the binding material. A method for making a superconductive ceramic wire according to claim 1 wherein lead is deposited by soaking the porous ceramics in molten lead. A method for making a superconductive ceramic wire according to claim 1 wherein the amount of lead deposited in the pores is between 5% and 40% by volume of the superconductive ceramics. A method for making a superconductive ceramic wire according to claim 1 wherein copper sheath is used for covering the lead deposited ceramics. A method for making a superconductive ceramic wire according to claim 1 wherein silver sheath is used for covering the lead depositted ceramics. A method for making a superconductive ceramic wire according to claim 2 wherein the copper layer is formed by chemical plating. A method for making a superconductive ceramic wire according to claim 3 wherein the tin layer is formed by chemical plating. A superconductive ceramic wire which is obtained by: (a) preparing a superconductive porous ceramics; (b) depositing lead in the pores of the ceramics; (c) covering the lead-deposited ceramics with a metal; and (d) extending the metal-clad and lead-deposited ceramics. A superconductive ceramic wire which is obtained by: (a) mixing powdery yttrium oxide (Y₂O₃), powdery barium carbonate (BaCO₃), powdery copper monoxide (CuO) at a molecular proportion of 0.5 : 2 : 3; (b) making a compound having a composition of YBa₂Cu₃O₇ and a perovskite structure by heat-treating the powdery mixture; (c) pulverizing the compound; (d) mixing the pulverized compound with a binding material; (e) heat-treating the mixture to obtain a superconductive porous ceramics; (f) making a layer of copper on the superconductive porous ceramics by chemical plating; (g) soaking the copper-clad porous ceramics in molten lead so that between 5% to 40% by volume of lead is deposited on the ceramics; (h) covering the lead-deposited ceramics with a copper sheath; and (g) extending the copper-clad and lead-deposited ceramics at a diametrical reduction rate higher than 80%.

Inventors: HAGINO, SADAAKI, TAKESHITA, TAKUO, YAMAGUCHI, TETSURO
Applicants: MITSUBISHI MATERIALS CORPORATION
Application year: 1988
Main classification: C04B35
IPC codes: H01B12, H01L39, H01B13, B28B1, C04B35