PROCESS FOR PRODUCTION OF MINERAL DISPERSIONS

Abstract: Disclosed is an improved process for producing disper­ sions of vermiculite ore particles by intercalating organo-­ cation salts into the vermiculite structure under shearing conditions to delaminate the ore and reduce particle size in one step.

Description: This invention relates to a process for making aqueous dispersions of vermiculite particles. Vermiculite lamellae or platelets have a particle size typically less than 200 microns, preferably less than 50 microns, have a thickness dimension that is small compared to the other two dimensions, and have an "aspect ratio" (i.e., length or breadth divided by thickness) of at least 10, preferably at least 100 and more preferably at least 1,000, for example, 10,000. It is known that aqueous suspensions of swollen vermiculite ore particles can be prepared by substituting monovalent inorganic cations such as Li⁺ or Na⁺ for exchangeable cations in the ore (for example, Mg²⁺ cations), followed by a subsequent step of aqueous washing of the cation-exchanged ores to remove excess salt and swell the macroscopic ore particles. It is also known to subject the swollen ore particles in water to mechanical shearing action that delaminates the vermiculite structure and produces an aqueous dispersion of tiny particles or platelets of vermiculite known as vermiculite lamellae. Salts of lithium have been preferred in such known processes because Li⁺ cation-exchanged vermiculite ores will swell in the subsequent washing step sufficiently for a shearing action applied to the swollen ore particles to reduce the platelet dimensions to less than approximately 50 microns, thereby producing vermiculite lamellae of an appropriate size for the fabrication of films and coatings. Processes using these known techniques are disclosed for instance in U.S. Patent Nos. 3,325,340 and 4,608,303 and U.K. Patent No. 1,593,382. Because lithium salts are expensive, compared to sodium chloride for instance, the latter is more commonly used in the treatment of vermiculite particles, based on its low cost, availability and lack of environmental impact. Na⁺-exchanged ores, however, lack the swelling potential of Li⁺-exchanged ores, and the Na⁺ cations are conventionally replaced by an organo-cation, such as an organo-substituted ammonium cation, in a second exchange step that intercalates the organo-cations into the vermiculite structure. The second exchange step is followed by a second aqueous washing step to swell the vermiculite ore particles to an adequate degree, preferably to at least twice its original volume. They are then subjected to the shearing step to delaminate them and produce vermiculite lamellae of an appropriate size, which is generally preferred to be less than 50 microns. Such a process is disclosed in U.S. Patent No. 4,608,303 and in U.K. Patent No. 1,593,382. According to the latter patent, Na⁺-exchanged vermiculite ores are contacted with an aqueous solution of butylammonium chloride in the second exchange step. It is conventionally preferred, in such processes, to perform the second exchange step with an aqueous solution in which the concentration of the organo-cation is higher than that of the exchangeable ions in the Na⁺-exchanged vermiculite ore. Typically, molar ratios of 1:1 to 12:1 organo-cation to Na⁺-exchangeable ions in the ore are employed. In processes such as disclosed in U.S. 4,608,303 and U.K. 1,593,382, not only is the second swelling step performed on the organo-cation intercalated ore by aqueous washing prior to the shearing step crucial for the production of vermiculite lamellae of the desired size, but also the swelling of the ore is conventionally allowed to proceed to at least four times its original volume, and in some aspects, six times the ore's original volume before shearing. Since the washing and swelling step complicates the process of producing vermiculite lamellae, there is need for an improved way to produce useful suspensions of vermiculite lamellae that enables the organo-cation intercalated ore to be sheared without first subjecting it to a separate washing and swelling step. It would also be desirable to permit the concentration of the organo-cations to be less than that of exchangeable Na⁺ cations in the vermiculite ore. According to the invention, a process for making an aqueous dispersion of vermiculite ore particles that comprises the steps of contacting vermiculite ore with an aqueous alkali metal salt solution, washing the ore to produce an aqueous suspension of vermiculite ore particles intercalated with metal cations, and contacting the particles in aqueous suspension with an aqueous solution of an organo-substituted ammonium-cation, is characterized in that the suspension of vermiculite ore particles that have been intercalated with metal cations is subjected to a shearing action to delaminate the vermiculite ore particles simultaneously with the step of contacting the particles in aqueous suspension with an organo-substituted ammonium cation. Preferably according to the invention, the ratio of organo-substituted ammonium-cations in the aqueous solution of an organo-substituted ammonium-cation to the exchangeable alkali metal ions in the aqueous suspension of vermiculite ore particles that have been intercalated with metal cations is less than about 3.5:1 and greater than about 0.1:1. More preferably, the ratio is in the range between about 1:1 to about 0.2:1. In the first step of the process according to the invention, an aqueous suspension of vermiculite particles is prepared by contacting vermiculite ore particles with a concentrated salt solution, preferably a sodium salt solution, and gently agitating the mixture for a time sufficient to allow penetration of the salt solution into the structure of the vermiculite particles, thereby exchanging Na⁺ ions with exchangeable material within the vermiculite ore. The time may vary, depending on the size of the particles and the characteristics of the batch of vermiculite being treated, from about one hour to several days. The salt-treated vermiculite ore is then subjected to an aqueous washing until salt that has not penetrated the particle structure or the amount in excess of exchangeable ions in the ore has been removed. It is preferred to use a molar concentration of Na⁺ cations in the aqueous solution greater than that of the exchangeable ions in the vermiculite ore to insure an acceptable rate of exchange. Preferably, sodium chloride is the alkali metal salt used in the first step in the treatment of the vermiculite particles. The concentration of vermiculite ore in the suspension of vermiculite ore particles that have been intercalated with metal cations is preferably in the range from about 1% to about 70%, more preferably in the range from about 10% to about 30% by weight of vermiculite, based on the total suspension. The exchange reaction may be carried out at a variety of temperatures, typically at temperatures above ambient. It is preferable, however, to reflux the aqueous salt solution with the ore. Organo-cation salts known from prior art to exfoliate vermiculite can be used in this invention. For example, organo-cation salts that are useful in the practice of this invention include salts of ammonium, phosphonium and sulphonium cations. The organic group portion of these cations may be polymerizable or non-polymerizable, substituted or non-substituted, saturated or unsaturated, aliphatic chains, polyoxyethylene chains or aromatic or heterocyclic rings or any combination of two or more of these substituents. Examples of such organo-cations are n-butylammonium, isobutylammonium, propylammonium, iso-amylammonium, crotyltriethylammonium, allylammonium, methacryloxyethyltrimethylammonium, 3-acryloxyneopentyltrimethylammonium, 2-methacryloxyethyl-t-butylammonium, diallyammonium, diallyldimethylammonium, allyldimethylsulfonium, methacrylamidopropyltrimethylammonium, acrylamidopropyltrimethylammonium, butenyltrimethylammonium, vinylpyridinium ions such as N-methyl-2-vinylpyridinium, vinylbenzyldimethylsulfonium, vinylbenzyltrimethylammonium, 2,3-epoxypropyltrimethylammonium, triethylvinylphosphonium, tributylvinylphosphonium, alpha-ammonium-δ-butyrolactone, glycidyltrimethylammonium, 1-methyl-1-tert-butylaziridinium, and 1-ethyl-1,3,3-trimethyl azetidinum. Of the various organo-cation salts capable of exfoliating vermiculite, the most effective are salts of alkylammonium compounds having between 3 and 6 carbon atoms included in each alkyl group, especially those of allylammonium, n-butylammonium, iso-butylammonium, propylammonium and iso-amylammonium. Also effective are solutions of amino-acids, such as lysine or ornithine, in the cationic form. However, other chemical substances capable of exfoliating vermiculite may be employed as additives to the suspension of vermiculite ore particles from step (1), in place of, or as adjuvants to the organo-cation salt solutions, e.g., alkali metal chlorides such as lithium, or in combination with the aforementioned organo-cationic salts. The anions in the salts of lithium, sodium or organo-cationic salts are preferably inert anions commonly found in stable salts of these cations, for example, halide ions, and preferably chloride. While contacting the aqueous suspension of vermiculite ore particles from step (1) with the organo-cation solution in step (2), the vermiculite ore particles are delaminated by simultaneously subjecting the suspension of organo-cation exchanged ore particles to a shearing force such as a rotary paddle, cowles blade or by means of some other shearing devices known in the art. A colloid mill or similar type of shearing macerator may also be employed during this step of the invention, including a Waring blender or a macerator of the type similar to those used for domestic purposes. A shearing force may also be imparted by suitable vibratory treatment, for example, ultrasonic agitation of the suspension. Alternatively, delamination can be accomplished in a process involving two or more shearing steps, comprising an initial application of a low shearing action, followed by one or more applications of a higher shearing action. The object of the delamination step is to produce a dispersion of vermiculite lamellae or platelets having a particle size typically less than 200 microns, preferably less than 50 microns, and having one dimension much smaller than the other two. Preferably they have a thickness of less than about 0.5 microns, more preferably less than about 0.05 microns, and have an aspect ratio of at least 10, preferably at least 100, and more preferably at least 1,000, for example 10,000. The shearing operation should be applied for the minimum time necessary to achieve a dispersion containing particles of the aforesaid preferred dimensions. That means that a vigorous grinding action or shearing action that would ultimately reduce the vermiculite particles to approximately three-dimension equality is not desirable. The delamination of the vermiculite ore particles may be carried out at different temperatures, but usually at a temperature above the ambient temperature and preferably the delamination is carried out under reflux. Dispersions of vermiculite lamellae can be used, for example, to prepare strong, flexible heat resistant films and coatings by depositing the vermiculite lamellae on surfaces of various shapes and sizes and removing water from the vermiculite particles. Deposition of the vermiculite lamellae can be accomplished by any casting methods known in the art, or electrophoretic methods of depositing vermiculite lamellae from dispersions thereof to form films and coatings may also be employed. For example, films and coatings such as refractory-facing materials, fireproof packaging materials, thermal insulation materials, materials for gasket fabrication, and electrical insulating materials, may be used. The term "vermiculite" used herein refers to all materials known mineralogically or commercially as vermiculite, and minerals consisting wholly or largely of vermiculite including minerals of a mixed-layer type (phyllo-silicates) containing vermiculite layers as a constituent such as hydrobiotites and chlorite-vermiculites, and that can be delaminated in the same or similar manner as vermiculite. Vermiculite is the preferred layer-mineral, but other layer-minerals that may be used include montmorillonite, kaolinite, clays comprising sepiolite, and kaolinite, and other layer silicate minerals that can be delaminated by a process according to the invention to produce lamellae or plate-like particles. The following examples illustrate specific processes for the production of vermiculite suspensions according to the invention. Example I - Control A 20% by weight suspension of vermiculite ore is refluxed in a saturated sodium chloride solution for four hours, cooled to room temperature, and filtered. The filtrate is then washed with distilled water (by decantation), and air dried to a damp solid. The level of Na⁺ exchange capacity for various vermiculite ores is summarized in Table I. Na⁺ Exchange Capacity of Vermiculite Ore Ore Grade (ASTM Material Designation C-516) Milliequivalents Na⁺/100 grams 2 93 3 87 4 88 5 78 300 grams of the Na⁺ exchanged grade 4 vermiculite ore is heated to 80°C in 1.5 liters of 2M allylammonium chloride (ACC) (ACC/Na⁺ molar ratio of 11.4:1) for four hours using a paddle stirrer for agitation, cooled to room temperature, then washed with distilled water (by decantation), and then diluted to a 10% by weight solids suspension. The ore is permitted to swell to a sixfold increase in volume, then a shearing action is applied to the suspension for two hours using a commercial blender. The resulting dispersion of vermiculite ore particles is then sieved to remove particles greater than 53 microns in size (90% conversion to less than 53 microns in size). After the dispersion is diluted to 2 weight percent solids, a film is cast and the water evaporated to yield a sheet with a thickness of 3 mils (0.076mm), which exhibits a tensile strength of 1290 psi (8.7MPa), a modulus of 190 kpsi (1.28GPa), and an elongation of 3.3%. Example II To demonstrate that delamination is most effective at organo-cation/Na⁺ molar ratios between approximately 2:1 to approximately 0.2:1, the following experiments are performed. A 20 weight percent suspension of the grade 4 Na⁺ exchanged ore (see, Example I) is heated to 80°C in an aqueous solution of allylammonium chloride (ACC) for four hours using a paddle type stirrer, then cooled to room temperature. The organo-cation exchanged ore is then allowed to settle and volume of the ore determined. The expansion in ore volume is calculated as the volume the unwashed allylammonium exchanged ore occupies minus the volume the Na⁺ exchanged ore occupies divided by the volume of the Na⁺ exchanged ore. The change in organo-cation exchanged ore volume as the molar ratio of allylammonium chloride (ACC) in the aqueous solution to Na⁺ in the ore is varied from 12.5:1 to 0.1:1 is displayed in the following table. Volume Expansion Milliequivalents ACC/ Milliequivalents Na⁺ Volume Expansion (%) 12.5 0 6.3 29 3.1 98 1.6 260 0.8 340 0.4 340 0.2 15 0.1 0 Example III Example II is repeated using propylammonium chloride (PAC). The results are summarized in the following table: Volume Expansion Milliequivalents PAC/ Milliequivalents Na⁺ Volume Expansion (%) 12.5 0 6.3 0 3.1 70 1.6 490 0.8 350 0.4 400 Example IV To demonstrate that delamination of vermiculite ore pursuant to the instant invention is not restricted to ore size, the following experiments are performed. Example II is repeated except that the grade 4 Na⁺ exchanged vermiculite ore is replaced by grades 2, 3 or 5 Na⁺ exchanged ores and the molar ratio of allylammonium chloride to Na⁺ maintained at 0.7:1. All of the ores swell to at least threefold in volume. Example V The following example demonstrates the instant invention whereby an organo-cation/Na⁺ molar ratio within the preferred range is maintained and the separate steps of ore washing and swelling subsequent to organo-cation exchange is eliminated in preparation of dispersions of vermiculite lamellae. 100 grams of grade 4 Na⁺ exchanged vermiculite ore is suspended in 500 ml. of a 0.125 M aqueous solution of allylammonium chloride (ACC/Na⁺ molar ratio of 0.7:1). The dispersion is heated to 80°C for four hours while simultaneously applying a shearing action via a cowles blade at 2500 rpm. The dispersion is then cooled, diluted with distilled water and sieved to remove materials greater than 38 microns in size (70% conversion to less than 38 microns in size). The resulting dispersion is diluted to 2 weight percent solids and a film cast. Evaporation of the water produces a film 2 mils (0.058mm) thick with a tensile strength of 1570 psi (10.6MPa), a modulus of 300 kpsi (2.03GPa), and a elongation of 4.3%. Example VI This example further demonstrates the instant invention whereby the separate steps of washing and ore swelling are eliminated in the preparation of dispersions of vermiculite lamellae used to form films. Example V is repeated except that grade 4 Na⁺ exchanged vermiculite ore is replaced by grade 3 Na⁺ exchanged ore and the molar ratio of allylammonium chloride (ACC) to Na⁺ is varied from 0 to about 3.0:1. After sieving to remove particles larger than 38 microns in size, the resulting dispersions are diluted to 2 weight percent solids and respective films cast. Evaporation of water produces films having properties that are summarized in the following table: Effect of ACC/Na⁺ Mole Ratio On Film Properties ACC/Na⁺ Mole Ratio Particle Size Conversion to Less than 38 Microns (%) Tensile Strength (psi) Film Modulus (kpsi) Elongation (%) 0 46 708 580 0.2 0.2 67 1200 670 0.8 0.5 81 1560 560 1.8 0.7 81 1830 430 2.7 1.0 84 1400 260 5.7 1.5 78 1100 150 4.3 3.0 66 225 250 2.3 Example VII This example demonstrates that mechanical properties of films formed from dispersions of vermiculite lamellae can be improved by employing low shearing action to maximize platelet delamination, followed by shearing with a known device. Example V is repeated except that a paddle stirrer is used for 0 hours, one-half hour and 4 hours, respectively, before switching to the cowles blade. The data shows that mechanical properties of the film are improved compared to the use of the cowles blade alone. The results are summarized below: Paddle Stirrer (hrs.) Particle Size Conversion to Less than 38 Microns (%) Tensile Strength (psi) Film Modulus (kpsi) Elongation (%) 0 70 1570 300 4.3 0.5 71 2140 470 4.0 4.0 76 2610 400 4.5

Claims: A process for making an aqueous dispersion of vermiculite ore particles that comprises the steps of contacting vermiculite ore with an aqueous solution of an alkali metal salt, washing the ore to produce an aqueous suspension of vermiculite ore particles intercalated with metal cations, and contacting the particles in aqueous suspension with an aqueous solution of an organo-substituted ammonium-cation, is characterized in that the suspension of vermiculite ore particles that have been intercalated with metal cations is subjected to a shearing action to delaminate the vermiculite ore particles simultaneously with the step of contacting the particles in aqueous suspension with an organo-substituted ammonium cation. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 1, further characterized in that the ratio of organo substituted ammonium-cations to exchangeable alkali metal ions that have been intercalated with metal cations is less than about 3.5:1 and greater than about 0.1:1. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 2, further characterized in that the ratio of organo substituted ammonium-cations to exchangeable alkali metal ions that have been intercalated with metal cations is in the range between about 1:1 to about 0.2:1. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 1, 2, or 3, further characterized in that the shearing action is applied for a time necessary to achieve a dispersion containing particles having an aspect ratio of at least 10. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 4, further characterized in that the shearing action is applied for a time necessary to achieve a dispersion containing particles having an aspect ratio of at least 100. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 4, further characterized in that the shearing action is applied for a time necessary to achieve a dispersion containing particles having an aspect ratio of at least 1000. A process for making an aqueous dispersion of vermiculite ore particles as claimed in any of the preceding claims, further characterized in that the alkali metal salt solution is sodium. A process for making an aqueous dispersion of vermiculite ore particles as claimed in any of the preceding claims, further characterized in that the the source-compound of the organo-substituted ammonium cation contains an inert anion that will not decompose during delamination. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 8, further characterized in that the source-compound of the organo-substituted ammonium cation is a salt of alkylammonium compounds having between 3 and 6 carbon atoms in each alkyl group. A process for making an aqueous dispersion of vermiculite ore particles as claimed in claim 9, further characterized in that the ammonium cation is allylammonium, n-butylammonium, iso-butylammonium, propylammonium or iso-amylammonium. A process for making an aqueous dispersion of vermiculite ore particles as claimed in any of the preceding claims, further characterized in that the source-compound of the organo-substituted ammonium cation is allylammonium chloride. A process for making an aqueous dispersion of vermiculite ore particles as claimed in any of the preceding claims, further characterized in that the source-compound of the organo-substituted ammonium cation is propylammonium chloride. A process for making an aqueous dispersion of vermiculite ore particles as claimed in any of the preceding claims, further characterized in that the concentration of vermiculite ore particles in the aqueous suspension of vermiculite ore particles that have been intercalated with metal cations is in the range from about 1% to about 70%, by weight of vermiculite, based on the total suspension. A process for making an aqueous dispersion of vermiculite ore particles as claimed in any of the preceding claims, further characterized in that the concentration of vermiculite ore particles in the aqueous suspension is in the range from about 10% to about 30% by weight of vermiculite. A process for making an aqueous dispersion of vermiculite ore particles as claimed in in any of the preceding claims, further characterized in that an initial application of a low shearing action is followed by an application of a higher shearing action.

Inventors: NELSON, LAWRENCE LEE
Applicants: HERCULES INCORPORATED
Application year: 1988
Main classification: C04B14
IPC codes: C01B33, C04B14, C04B30