SURFACE MODIFIED OPTICAL LENS AND METHOD OF SURFACE MODIFICATION

Abstract: An optical lens of an acrylic polymer having an outermost surface modified in molecular structure to possess a desired characteristic. The modified surface includes a select chemical group, having the desired characteristic, bound by silane groups to reactive carboxyl groups on polymer chains of the acrylic polymer at the outermost surface of the lens. The surface is modified by a surface activating hydrolysis reaction chemically linking active carboxyl groups on polymer chains at the outermost surface of the acrylic polymer and then modifying the activated outermost surface by reacting a reagent including a select chemical group having the desired lens surface characteristic with the active carboxyl groups to bond the select chemical group to and modify the molecular structure of the outermost surface of the lens body. The desired characteristics imparted by the select chemical groups may include biological inertness, low glare and soil resistance, UV absorbance, and cytotoxic and anti-bacterial properties.

Description: SURFACE MODIFIED OPTICAL LENS AND METHOD OF SURFACE MODIFICATION BACKGROUND OF INVENTION The present invention relates to improvements in artificial optical lenses such as contact lenses, intraocular lenses and intracorneal implants, and, more particularly to such optical lenses having an outermost surface modified in molecular structure to provide medically desirable lens surface properties such as improved biological inertness, soil resistance, glare reduction, ultraviolet light absorption and selective cytotoxic and bactericidal properties. There is a recognized need in the field of artificial optical lenses for lenses having surfaces which are characterized by properties of biological inertness. In addition, it is desired that such surfaces be soil resistant, glare free, capable of absorbing ultra violet light and possess cytotoxic and bactericidal properties. Accordingly, in my recently issued United States Patent 4,655,770, the stated primary objective is to provide an improved biological implant material particularly for use as an intraocular lens wherein the material is designed to substantially minimize or eliminate inflammatory reactions with surrounding tissue or cells. More particularly, in my prior patent, I detail a method of passivating or modifying the surface of a transparent polymeric material forming an intraocular lens by chemically bonding a layer of a relatively inert fluorocarbon to the outer surface of the polymeric material. Preferably, the polymeric material is polymethyl methacrylate (PMMA) . In the bonding process, the PMMA is first treated with an oxidizing agent to produce a high concentration of hydroxyl groups at the surface of the PMMA. The hydroxyl groups bond the fluorocarbon to the PMMA creating the desired inert surface minimizing or eliminating inflammatory reactions with surrounding tissue or cells. Recently, I have discovered a surface activating hydrolysis reaction which when applied to an acrylic polymer forms high concentrations of active carboxyl groups at the outermost surface of the acrylic polymer. I have further found the carboxyl groups formed by the hydrolysis reaction to be reactive with perfluoro groups as well as various other chemical groups which are not reactive with hydroxyl groups but which possess particularly desirable chemical characteristics in association with optical lenses. In particular, when applied to optical lens bodies of acrylic polymers, my new surface modification process produces a lens body modified in molecular structure to possess desired characteristics of improved biological inertness, soil resistance, and glare reduction, or ultra violet light absorption or cytotoxic or anti-bacterial properties. SUMMARY OF INVENTION Generally speaking, in my present invention, a lens body of an acrylic polymer is characterized by an outermost surface modified in molecular structure to possess a desired characteristic, such as biologic al inertness, low glare, soil resistance, UV absorbance, and cytotoxic and anti¬ bacterial properties. The modified surface includes a select chemical group, having the desired characteristic, bound by silane groups to reactive carboxyl groups on polymer chains of the acrylic polymer at the outermost surface of the lens body. Such modification is accomplished by reacting a reagent including the select chemical group with reactive carboxyl groups on polymer chains at the outermost surface of the acrylic polymer to bond the select chemical group to and modify the molecular structure of the surface of the lens. Usually, the reactive carboxyl groups are formed by an activation step wherein a surface activating hydrolysis reaction occurs at the outermost surface of the acrylic polymer lens body to generate a high concentration of active carboxyl groups on polymer chains at the outermost surface of the lens body. The activation step is followed by a surface modifying step wherein the activated outermost surface of the lens body is reacted with a reagent including the select chemical group having the desired lens surface characteristic. In practice, some acrylic polymers naturally possess a high concentration of carboxyl groups at their outermost surface. For such acrylic polymers, my surface modification process may only include the surface modifying reaction step or, if it is desired to enhance the naturally occurring surface concentration of the carboxyl groups, may include both the activating and surface modifying steps. BRIEF DESCRIPTION OF DRAWINGS Figure 1 is a flow diagram, in block form, depicting fields of application of the process of my invention to acrylics of various types and the desired characteristics imparted to the outermost surfaces of optical lenses of such acrylics. Figure 2a is a flow diagram, in block form, of the surface activation step in the process of my invention. Figure 2b depicts a chemical reaction in accordance with the activation step of Figure 2a. Figure 3a is a flow diagram, in block form, of a surface modifying step in the process of my invention for producing an outermost surface on an acrylic polymer lens body having the characteristic of biological inertness, low glare, and soil resistance. Figure 3b depicts chemical reactions in accordance with the surface modifying step of Figure 3a with the last reaction including a diagrammatic illustration of the surface formed on the lens body. Figure 4 depicts a chemical reaction of a silane reagent and perf luoroalkyl carboxylic acid according to Figure 3a illustrating three reaction products formed thereby, each of which is employed in the surface modifying reaction. Figure 5a is a flow diagram, in block form, of a surface modifying step in the process of my invention for producing an outermost surface on an acrylic polymer lens body having the characteristic of cytotoxicity. Figure 5b depicts a chemical reaction in accordance with the surface modifying step of Figure 5a. Figure 5c is a diagrammatic representation of the chemical reaction of Figure 5b illustrating the bonding of the select chemical group Penicillin-N to the outermost surface of an optical lens body. Figure .5d depicts the chemical formula of polymyxin-B which may be utilized in the reaction of Figure 5b in place of Penicillin-N when it is desired to produce a lens surface having anti- bacteriological characteristics. Figure 6a is a flow diagram, in block form, of a surface modifying step in the process of my invention for producing an outermost surface on an acrylic polymer lens body having a ultra violet light absorbing characteristic. Figure 6b depicts the chemical reaction in accordance with the surface modifying step of Figure 6a. DETAILED DESCRIPTION OF INVENTION As previously stated, my present invention provides an optical lens having a lens body of an acrylic polymer. The outermost surface of the lens body is modified in molecular structure to possess a desired characteristic such as biological inertness, low glare, soil resistance, UV absorbance or cytotoxic or anti-bacterial properties. The modified surface includes a select chemical group for imparting the desired characteristic to the surface of the lens body. The select chemical group is bound by silane groups to reactive carboxyl groups on polymer chains of the acrylic polymer at the outermost surface of the lens body. The modification of the outermost surface of the lens body is accomplished by reacting a reagent including the select chemical group with reactive carboxyl groups on polymer chains at the outermost surface of the acrylic polymer to bind the select chemical group to and modify the molecular structure of the surface of the lens body. Usually, the reactive carboxyl groups are formed by an activation step wherein a surface activating hydrolysis reaction occurs at the outermost surface of the acrylic polymer to generate a high concentration of reactive carboxyl groups on polymer chains at the outermost surface of the lens body. The activation step is followed by a surface modifying step wherein the activated outermost surface of the lens body is reacted with a reagent including the select chemical group. Figure 1 depicts in block form the field of application of the process of my invention to acrylics of various types and the desired characteristics imparted to the outermost surface of optical lenses of such acrylics. More specifically, the surface modification process of my invention is applicable to any acrylic polymer or copolymer except those which are constituted of an acrylic or methacrylic acid in concentrations in excess of 50%. As depicted in Figure 1, the acrylic polymers to which my activation process is applicable include (1) thermoplastics which are o glassy at 50 C and below including poly methyl methacrylate (PMMA) , polysulfones and polycarbonates, (2) thermosets such as hydrogels, crosslinked hard acrylics and epoxy which are o glassy at 50 C and below and (3) thermosets o elastomeric at 50 C and above such as soft acrylics, polyacrylamides, polyacrylic acids and cellulose. For each type of acrylic polymer, the surface activation step produces an outermost surface on the lens body having a high concentration of reactive carboxyl groups. As previously stated, the surface activation step involves a surface activating hydrolysis reaction as depicted in Figures 2a and 2b. As there illustrated, the acrylic polymer lens body is immersed in a surface activating reagent to subject the outermost surface of the acrylic polymer to hydrolysis and the formation of a high concentration of reactive carboxyl groups on polymer chains at the outermost surface of the lens body. Following the immersion process, the lens body is removed from the reagent, washed and heated in an oven for several hours. In the chemical reaction depicted in Figure 2b, the acryl ic polymer i s reacted with a tetraalkylammonium hydroxide at room temperature for about 60 minutes. Preferably, the reagent comprises a highly concentrated (e.g. 35%) aqueous solution of tetramethylammonium hydroxide. The o lens body is immersed in such a reagent at 50 C for about 60. minutes. After immersion, the lens is withdrawn from the solution, washed deionized or distilled water and then heated and dried at about o 60 C in a convection oven with circulating air for 4 hours. The process of immersion hydrolyzes the ester groups on the surface of the acrylic polymer and forms an ammonium salt as shown in Figure 2b. The heating and drying process drives off ammonia and leaves the surface with a high concentration of free and reactive carboxylic acid (carboxyl groups). In such an activation step, carboxyl groups are formed on the polymer chains at the surface of the acrylic polymer without causing chain scission or allowing permeation of the activating reagent into the bulk of the acrylic polymer. This results from the activation reaction being conducted under mild conditions and for a short period of time. As also depicted in the diagram of Figure 1, some acrylic polymers naturally possess a high concentration of carboxyl groups on their surface. Such polymers are included in each of the three types of acrylic polymers to which the surface modification of my invention applies. For such polymers, the concentration of carboxyl groups may be sufficient naturally to proceed directly to the surface modifying step of the process of my invention. However, it may be desired to further enhance the concentration of carboxyl groups. In that event, the surface activating step is applied as depicted in Figure 1 to produce a polymer with an even higher concentration of carboxyl groups on the outermost surface of the acrylic polymer lens body. Having achieved surface activation either by the hydrolysis reaction or by use of a polymer having a sufficiently high naturally occurring concentration of carboxyl groups on its outermost surface, the lens body is ready for the surface modifying step of my invention. Generally speaking, the surface modifying step is accomplished by reacting a reagent including a select chemical group with the reactive carboxyl groups on the polymer chains of the outermost surface of the acrylic polymer to bond the select chemical group to and modify the molecular structure of the surface of the lens. Usually in the surface activating step, the acrylic surface activated to bear a high concentration of carboxyl groups is reacted with a silane reagent to complete the " surface modification process. A typical reagent for the surface modifying step comprises a molecule incorporating a reactive silane group and a group whose presence is desired on the acrylic surface. Hence, the typical reagent may have a formula R -X-R , where R is a silane group, R is 1 2 1 2 a group whose presence is desired on the surface, and X is a joining group, which may or may not be needed. Silanes are versatile reagents since they may be derivatized to incorporate many different R groups. Reagents 2 bearing silane end groups and different R groups 2 may be readily synthesized from commercially available silane (R A) and appropriate reagents 1 bearing R groups (R B) . However, it should be 2 2 noted that silane reagents do not react with carboxyl groups efficiently unless they are reacted with water to convert the alkoxy silane groups to silanol immediately prior to use. Thus, the surface modifying reagent is maintained as the alkoxy derivative until just before use. Then, the silanol groups, formed by the addition of water, are reactive to the surface (COOH groups) and to themselves. In particular, the silanol groups react with carboxyl groups on the activated acrylic surface to form silyl esters. Table 1 below lists various silane reagents R A, reagents bearing appropriate R groups (R B) 1 2 2 and the surface thicknesses and properties associated with the outermost surfaces of acrylic polymer optical lenses formed by the surface modifying step incorporating such R A and R B 1 2 reagents. For the R A reagents, the trialkoxy 1 aminosilane reagent may be depicted by the formula; (θMe) 3 Si CH^ NH CH^ H^ the trialkoxy silane reagent may be depicted the the formula; the chlorosilane reagent may be depicted by the formula; CiSi(CH_) cH 2 CH,C 6 H 5 and may be Z6076 available from Union Carbide; and the trialkoxyacryloxy silane reagent may be depicted by the formula: CH £ =C(CH^COθ(CH 2 ) 3 Sϊ(OCH^ For the R B r eagent s , th e pe rf luo roalkyl 2 derivatives may be depicted by the formula: COOH (CF ? ) Y CF WHERE X = 2-12 the cytotoxic polypeptides may be penicillin-N depicted by the formula; or polymyxin-B as illustrated in Figure 4; and where the benzophenone is a 2 hydroxy-4 (ethoxy acryloxy) derivative, and benzotriazole is a 2- hydroxy 5-ethoxyacryloxy derivative represented generally by the formulas: BENZOPHENONE ou OOCCH = at BENZOTR.AZOLE As depicted in Figure 1 and Table 1, the surface modifying step will result in a lens body having a biological inertness when the select chemical group is in a relatively thin layer and will possess the characteristics of biological inertness, reduced glare and soil resistance when the surface layer is relatively thick. In such instances, the select chemical group may be a fluorocarbon such as a perfluoro derivative defined by the foregoing formula COOH(CF ) CF . 2 x 3 Alternatively, the select chemical group may be an alkyl group (CH ) CH where x = 2 to 12, a siloxane 2 3 group (SiOR) and R is a methyl, ethyl or alkyl 3 (CH ) CH group where X = 1 to 8, or where the 2 3 select chemical group is a cyclohexyl group C H 6 11 Figures 3a and 3b depict the chemical reaction for the surface modifying step when the select chemical group is a perfluoro group. Reagents for the alkyl, siloxyl and cyclohexyl groups are well known in the art and may be utilized in the manner illustrated by the flow diagram of Figure 3a to produce the modified surface of the acrylic polymer lens having the characteristics of biological inertness, glare reduction and soil resistance associated with the perfluoro group as hereinafter described. More specifically, and by way of example, a surface modifying reagent particularly useful with the perfluoro group may be prepared by reaction of n-aminoethyl aminopropyl trimethoxy silane, commercially available as Z-6020 from Dow Corning Corporation, with perf luorodecanoic acid in anhydrous methanol under reflux in an atmosphere of nitrogen gas for 24 hours. The concentration of Z- -2 6020 should be in the range of 5 x 10 moles per -4 liter to 1 x 10 moles per liter and preferably 1 -3 x 10 moles per liter. Such a concentration yields a surface modified layer of a thickness of 50 to 100 angstroms. For thicker layers., higher concentrations are needed. The molar concentration of the perf luorodecanoic acid may be either equal to that, of the z-6020 or may be an integral multiple thereof. Preferably, it is the same as Z- 6020. As illustrated in Figure 4, the reaction product may be an amide. In fact, three different modes of .attachment between the two reagents are possible, an amide, a siloxane, and a secondary amide. Each contributes to the biological inertness of the surface and each enters into the surface modification reaction. When the reaction is complete, the reaction product may be cooled, transferred to a flask, and stored in a sealed bottle for up to 24 hours. At any time prior to use of the reagent in immersion of the surface activated lens body as depicted in Figure 3a, the efficacy of the solution may be tested using a glass test plate. In such a procedure, the first step is to prepare a batch of glass slides by dipping them in a 20% by weight aqueous solution of sodium hydroxide for 10 minutes then rinsing them thoroughly with distilled or deionized water. The second step is to dip one end of one or more of the glass slides into the surface modifying reagent for a minimum of 30 seconds. The third step is to wash the treated glass slide in methanol and dry in an oven for 10 minutes. Finally, the contact angle on the treated portion of the glass slide is measured with a water drop in a goniometer. The solution is good and suitable o for use if the contact angle exceeds 78 . After completion of the reaction of the silane reagent with the perfluorodecanoic acid, or after the efficacy of the resulting solution is determined, the surface activated lens body may be placed in a Teflon holder and immersed in the surface modifying reagent. As illustrated in Figure 3a, and for the purposes previously described, deionized water is added to the solution at a concentration of 1 volume percent of the surface modifying reagent. The lens body is immersed in the surface modifying reagent for 16 hours under reflux. The lens body is subsequently withdrawn from the surface modifying reagent, washed several times in dry anhydrous methanol for approximately 30 seconds per wash and then dried in o an oven at 60 C for about 4 hours. In practice, the results of such a process were tested by measurement of contact angle on a goniometer using 0.1 ml drops of deionized water. Contact angles measured on a batch of 30 intraocular lenses made o of PMMA ranged from 98 to 106 , with a mean of o 100 . As previously stated, for the concentration ranges referred to above, the surface modified layer produced by the process reactions of Figures 3a and 3b have a thickness of between 50 and 100 angstroms. In many cases, and particularly in the cases of select chemical groups producing biological inertness, the properties exhibited by the modified surface depend on the thickness of the modified layer. The thickness of the surface modified layer developed by a silane reagent is controlled by adjusting the concentrations of the surface modifying reagent and the period of the immersion reaction. Since the silane reagent has a multiple (3) silanol groups per molecule of reagent, two silanol groups are left on each reagent molecule subsequent to its reaction with the reactive carboxyl groups at the outermost surface of the lens body. The anchored silane molecule may react with a free silane molecule in solution to form a siloxane bond. The free silane molecule is thus anchored on a first bound silane molecule and serves to build up multiple layers of silane derivatives each bearing a perfluorononyl group as shown in Figure 3b. Reaction of the bound silane molecule with free silane molecules in solution compete in its reaction with a bound neighbor, hence substantial build up of the odif ied layer is achieved only at high concentrations of free saline reagent in solution. When the free salines are depleted, the bound salines react with each other exhausting all the silanol groups and forming siloxane bonds. This o reaction may take elevated temperatures (60 C) and considerable time (4 hours). The siloxane bonds serve to crosslink the surface modified layer, increasing its density, reducing its hydrophilicity and increasing its hardness. Thus, surface modifications reactions carried out using high concentrations of free silanes produce a thick surface modification layer which is uncrosslinked, soft and hydrophilic except at its uppermost layers while the use of dilute solutions of the surface modifying reagent produce a thin crosslinked hard layer. Preferably, to produce a surface modification which is characterized by biological inertness and resistance to soiling, it has been found that the thickness of the surface modification layer should be in a range from 2000 to 6000 angstroms. In that range of thickness, it has been found that substantial glare reduction occurs. In particular, it is known that the refractive index of an acrylic with long chains of perfluoroalkyl substitutions is lower than that of acrylics such as PMMA. Hence, if the surface modified layer is built up to a thickness ranging from 2000 to 6000 angstroms, the lower refractive index of the surface will reduce the reflectivity of the surface. The surface reflectivity reaches a minimum and is no more than 0.5%, when the refractive index of the surface layer is the geometric mean of the refractive index of the acrylic polymer forming the lens body and that of the surrounding medium. Since the refractive index of the acrylic polymer such as PMMA is 1.493, and that of the ocular medium in which the optical lens is placed is about 1.36, the desired refractive index of the surface layer is 1.423. Refractive index may be achieved by bonding perf luoroalkane chains having a refractive index ranging from 1.40 to 1.42. Such a reduction of surface reflection leads to reduced glare from the surface of the optical lens. Studies suggest that glare from conventional PMMA lenses with a 6 mm optic may be -reduced by more than 50% by using an optimal thickness of 6000 angstroms of a perf luoroalkyl layer formed by the method of my invention. As previously stated, one of the desired characteristics associated with the surface modified acrylic polymer optical lens of my invention, is cytotoxicity or anti-bacterial properties. Figure 5a illustrates, in block form. the surface modifying step for producing such a surface modification of an acrylic polymer lens body. Figures 5b and 5c depict the chemical reaction and the manner in which the select chemical group is bound to the outermost surface of the acrylic polymer lens body according to the chemical reaction of Figure 5b. More specifically, for the physical characteristic of cytotoxicity, cytotoxic polypeptides may be utilized as the select chemical group. For example, as depicted in Figures 5b and 5c, a barium salt of 9-penicillin (Penicillin-N) is dissolved in anhydrous methanol at a concentration -4 -3 ranging from 1 x 10 moles per liter to 1 x 10 moles per liter. A trialkoxy silane is dissolved in anhydrous methanol at the same concentration. Equal volumes of the two solutions are mixed together and warmed in a water bath at o approximately 40 C for 1 hour in the absence of moisture or air. At the end of 1 hour, the reaction is completed and, if desired, the surface modifying reagent (R ) may be stored for several 6 hours in the absence or air or moisture. To ready the surface modifying solution it is hydrated with 1% distilled water (0.026 moles per liter) just before use. The surface activated acrylic polymer lens body is then immersed in the 6 solution for 30 minutes at 25 C for surface modification and attachment of the select chemical group to occur. A layer of about 5000 to 1000 angstroms thickness having the structure represented as R in Figure 5c is permanently bound 7 to the surface by the foregoing method. The foregoing procedure is generally applicable to all polypeptides including polymyxin- B as illustrated in Figure 5d. Polymyxin-B is a mixture of polymyxins B and B . Poly yxin B is 1 2 1 C H N 0 , where R = (+) -6- Methyloctanoyl; X = 56 96 16 13 Phenylalanine; Y = Leucine; and Z = L-DAB. Polymyxin B is C H N 0 , where R = 6- 2 55 96 16 13 Methyheptanoyl ; X = Phenylalanine; Y = Leucine; and Z = L-DAB. In the case of Penicillin-N, the resulting outermost surface of the lens body is cytotoxic and prevents bacterial growth and hence prevents ophthalmitis. In the case of polymyxin-B, the surface exhibits an anti-bacterial property principally effective against gram-negative bacteria. As previously stated, one of the desired characteristics of the outermost surface of an acrylic polymer optical lens, is that it be UV light absorbing. The surface modifying step of my invention for producing such a surface is depicted in Figures 6a and 6b. As represented, this is a two step process. First, an appropriate silane reagent is mixed with methanol. Distilled water is added to the solution readying it to receive the surface activated acrylic polymer lens body preferably at room temperature for approximately 4 hours. Separately, an appropriate UV absorber is mixed with an inert solvent and a polymerization initiator and the surface activated lens body is removed from the solution of the silane reagent and immersed in the UV absorber solution for o polymerization at about 60 C for 6 hours. The resulting lens is washed and then dried. • More particularly, in the first step, the silane reagent is preferably a trialkoxyacryloxy derivative. It is mixed with methanol such that the resulting solution has a concentration of the -2 silane reagent of approximately 2 x 10 moles per liter. As previously stated, the solution is hydrated with distilled water (a 1% solution) prior to use. The reaction of the surface activated acrylic polymer lens body with the silane solution is at room temperature for 4 hours. This results in a layer of acryloxy silane groups being bonded to the outer surface of the activated acrylic polymer lens body. The thickness of the layer is in a range of 1000 to 5000 angstroms with 2000 angstroms being optimum. Such a range has been found to be optimum for UV absorption and for minimal light scatter. The acryloxy silane group bearing surface formed by the first step is ready for the second step which involves the polymerization of an acryloxy derivative of the UV absorber with surface bound acryloxysilane groups. The UV absorber chromophore may be a -benzophenone or benzotriazole. The polyme ization reaction involving the UV absorber is carried out in a hexane solution. For example, a 0.1 mole per liter solution may be prepared by dissolving 3 grams of the UV absorber derivative 2-hydroxy 4-ethoxyacryloxy benzophenone in 1 liter of n-hexane. 100 mg of a free radical initiator such as USP-245 available commercially from Union Carbide Corporation is added to the solution. The optical lens body is immersed in the , solution which is then deareated. The solution is o maintained at about 60 Q ± or s hours. The resulting layer of acryloxy groups at the surface of the lens body is copoly erized with the acryloxy derivative of the UV absorber as shown in Figure 6b. Use of a lower polymerization temperature, a higher catalyst concentration and a longer reaction time will lead to prolongation of the surface polymerization reaction and a thicker layer of polymerized UV absorber derivative, if desired. After the polymerization reaction is completed the lens body is thoroughly washed in cold methanol to remove any polymeric UV absorber formed in solution, but precipitated on the surface of the lens body. The lens body is subsequently dried in a vacuum oven and its absorption spectrum is recorded. For example, a 7000 angstrom layer will have an optical density of 3.5 at 360 nm and will have an absorption of 90% of UV light at 380 nm. Other types of UV absorber derivatives may be attached in a similar fashion among them acryloxy derivatives of 2-hydroxyphenyl benzotriazole. From the foregoing, it should be appreciated that my present invention provides a lens body of an acrylic polymer characterized by an outermost surface modified in molecular structure to possess desired characteristics such as biological inertness, low glare, soil resistance, UV absorbance and cytotoxic and anti-bacterial properties. While specific examples of chemical reactions and formulations for producing such characteristics have been described in detail, the present invention is not limited to such. Rather, the invention is to be limited of scope only by the terms of the following claims.

Claims: ______!__£ 1. An optical lens comprising: a lens body of an acrylic polymer; and an outermost surface of the lens body including a select chemical group having a desired lens surface characteristic bound by silane groups to reactive carboxyl groups on polymer chains of the acrylic polymer at the outermost surface of the lens body. 2. The optical lens of Claim 1, wherein the select chemical group is a UV absorber. 3. The optical lens of Claim 2, wherein the UV absorber is a benzophenone or a benzotriazole. the silane groups are acryloxysilane groups formed by reacting a silane reagent with the carboxyl groups, and the UV absorber is bound to the acryloxysilane groups by polymerization of an acryloxy derivative of the UV absorber with surface boundacryloxy silane groups. 4. The optical lens of Claim 2, wherein the silane reagent is a trialkoxy acryloxy silane. 5. The optical lens of Claim 4, wherein the outermost surface of the lens body has a thickness between 5000 and 10,000 angstroms. 6. The optical lens of Claim 1, wherein the select group is a perfluoro, alkyl, siloxane or cyclohexyl group. 7. The optical lens of Claim 6, wherein the select chemical group is a perfluoro group and the outermost surface has a thickness between 50 and 100 angstroms to provide a biologically inert surface for the lens body. 8. The optical lens of Claim 6, wherein the select chemical group is a perfluoro group and the outermost surface has a thickness between 2000 and 6000 angstroms to provide a biologically inert, low glare and soil resistant surface for the lens body. 9. The optical lens of Claim 1, wherein the select chemical group is a cytotoxic polypeptide. 10. The optical lens of Claim 9, wherein the polypeptide is penicillin-N or polymyxin-B. 11. A method of modifying the outermost surface of an acrylic polymer optical lens body to have selected and desired surface characteristics, comprising: (1) activating the outermost surface of the lens body by a surface activating hydrolysis reaction to chemically link active carboxyl groups- on polymer chains of the acrylic polymer at the outermost surface of the lens body; and (2) modifying the activated outermost surface of the lens body by reacting a reagent including a select chemical group having the desired lens surface characteristic with the active carboxyl groups to bond the select chemical group to and modify the molecular structure of the surface of the lens body. 12. The method of Claim 11, wherein in step (1) the active carboxyl groups are linked to the polymer chains by reacting the acrylic polymer at the outermost surface of the lens body with a concentrated aqueous solution of a 3 tetramethylammonium hydroxide then washing and heating the lens body to drive off ammonia. 13. The method of Claim 12, wherein in step (2) the reagent further includes reactive silane groups for linking the select chemical group to the active carboxyl groups. 14. The method of Claim 13, wherein in step (2) the select chemical group is a perfluoro, alkyl, siloxane or cyclohexyl group. - 15. The method of Claim 14, wherein in step (2) the select chemical group is the perfluoro group and wherein the reagent is a perfluoroalkyl reagent mixed with a silane reagent and methanol, the lens body is immersed in the reagent, washed and dried to produce a fluoroalkyl layer the thickness of which is controlled by the concentration of the silane reagent to be between 50 and 100 angstroms to provide a biologically inert surface for the lens body or to be between 2000 and 6000 angstroms to provide a biologically inert, low glare and soil resistant surface for the lens body. 16. The method of Claim 15, wherein the silane reagent is a trialkoxy aminosilane reagent. 17. The method of Claim 13, wherein in step (2) the select chemical group is a cytotoxic polypeptide and the reagent is a mixture of a silane reagent and methanol, the reagent is hy rated with water and the lens body immersed in the reagent. 18. The method of Claim 17, wherein the polypeptide is penicillin-N or polymyxin-B. 19. The method of Claim 18, wherein the silane reagent is a t r i al ko xy s ilane or a chlorosilane. 20. The method of Claim 11, wherein step (2) comprises immersing the lens body in a aqueous mixture of a trialkoxy acryloxysilane reagent and methanol and polymerizing an acrylic derivative of a UV absorber with acryloxysilane groups bound to the surface of the lens body. 21. A method of modifying the outermost surface of an acrylic polymer optical lens body to have a select and desired surface characteristic, comprising: reacting a reagent including a select chemical group having the desired lens surface characteristic with active carboxyl groups on polymer chains at an outermost surface of the acrylic to bond the select chemical group to and modify the molecular structure of the surface of the lens body. 22. The method of Claim 21, wherein the reagent further includes reactive silane groups for linking the select chemical group to the active carboxyl groups. 23. The method of Claim 22, wherein the select chemical group is a perfluoro, alkyl, siloxane or cyclohexyl group. 24. The method of Claim 23, wherein the select chemical group is the perfluoro group and wherein the reagent is a perf luoroalkyl reagent mixed with a silane reagent and methanol, and wherein the method further includes controlling the concentration of the silane reagent to control the thickness of the modified surface to be between 50 and 100 angstroms to provide a biologically inert surface for the lens body or to be between 2000 and 6000 angstroms to provide a biologically inert, low glare and soil resistant surface for the lens body. 25. The method of Claim 22, wherein the select chemical group is a cytotoxic polypeptide and the reagent is a mixture of a silane reagent and methanol. 26. A method of modifying the outermost surface on an acrylic polymer optical lens body to have selected and desired ultra violet light absorbing characteristics, comprising: immersing the lens body in an aqueous mixture of trialkoxyacryloxy silane reagent and methanol and polymerizing an acryloxy derivative of a UV absorber with acryloxysilane groups bound to the surface of the lens body. 27. A method of activating the surface of an acrylic polymer lens body comprising reacting the acrylic polymer surface of the lens body with a concentrated a q u eous solution of a tetramethylammonium hydroxide, washing and then heating the lens body to drive off ammonia leaving active carboxyl groups linked to a polymer chain at the outermost surface of the acrylic polymer. 28. An optical lens comprising: a lens body of an acrylic polymer; and a surface of the lens body modified in molecular structure to possess a desired characteristic by reacting a reagent including a select chemical group having the desired lens surface characteristic with active carboxyl groups on polymer chains at an outermost surface of the acrylic to bond the select chemical group to and modify the molecular structure of the surface of the lens. 29. The optical lens of Claim 28, wherein the bonding of the select chemical group to the surface of the lens is furthered by a polymerization reaction. 30. The optical lens of Claim 28, wherein the reagent further includes reactive silane groups for linking the select chemical group to the active carboxyl groups. 31. The optical lens of Claim 30, wherein the select chemical group is a perfluoro, alkyl, siloxane or cyclohexyl group. 32. The optical lens of Claim 31, wherein the select chemical group is a perfluoro group and the modified surface has a thickness between 50 and 100 angstroms to provide a biologically inert surface for the lens body. 33. The optical lens of Claim 31, wherein the select chemical group is a perfluoro group and the modified surface has a thickness of between 2000 and 6000 angstroms to provide a biologically inert, low glare and anti-soil surface for the lens body. 34. The optical lens of Claim 30, wherein the select chemical group is a cytotoxic polypeptide. 35. The optical lens of Claim 34, wherein the polypeptide is penicillin-N or polymyxin-B. 36. The optical lens of Claim 28, wherein the active carboxyl groups are formed by a surface activating hydrolysis reaction. 37. The optical lens of Claim 36, wherein the active carboxyl groups are linked to the polymer chains at the outermost surface of the acrylic by reacting the acrylic polymer surface of the lens body with a con-centrated aqueous solution of tetraalkylammonium hydroxide then washing and heating the lens body to drive off ammonia. 38. The optical lens of Claim 36, wherein the reagent further includes reactive silane groups for linking the select chemical group to the active carboxyl groups. 39. The optical lens of Claim 38, wherein the select chemical group is a perfluoro, alkyl, siloxane or cyclohexyl group. 40. The optical lens of Claim 38, wherein the select chemical group is a cytotoxic polypeptide. 41. The optical lens of Claim 37, wherein the reagent further includes reactive silane groups for linking the select chemical group to the active carboxyl groups. 42. The optical lens of Claim 41, wherein the select chemical group is a perfluoro, alkyl, siloxane or cyclohexyl group. 43. The optical lens of Claim 42, wherein the select chemical group is a perfluoro group and the modified surface has a thickness between 50 and 100 angstroms to provide a biologically inert surface for the lens body. 44. The optical lens of Claim 42, wherein the select chemical group is s perfluoro group and the modified surface has a thickness between 2000 and 6000 angstroms to provide a biologically inert, low glare and soil resistant surface for the lens body. 45. The optical lens of Claim 41, wherein the select chemical group is a cytotoxic polypeptide. 46. The optical lens of Claim 45, wherein the polypeptide is penicillin-N or polymyxin-B.

Inventors: GUPTA AMITAVA, GUPTA, AMITAVA
Applicants: IOPTEX RESEARCH INC, IOPTEX RESEARCH, INC.
Application year: 1988
Main classification: C08F8
IPC codes: B29D11, C08F8, C08J7, G02B1, G02C7