METHOD OF TRANSPORTING RAPIDLY QUENCHED RIBBON AND APPARATUS THEREFOR

Abstract: A method and an apparatus for transporting a rapidly quenched ribbon (3) from a cooling roll (1) to a winding reel (21, 22 or 33) by a pinch roll (8) are disclosed. The pinch roll (8) comprises a brush roll (9) and a solid roll (10) for transporting the ribbon (3) such as to maintain an adequate tension in the ribbon without any transversal displacement and breakdown of ribbon. The tension is controlled within a range of 2∼8 kgf by adjusting at least one of an amount of pressing of the brush roll (9) against the solid roll (10), a pressing force on the brush roll (9) and a ratio between circumferential speeds of the pinch roll (8) and the cooling roll (1).

Description: The invention relates to a method and an apparatus for transporting a rapidly quenched ribbon from a cooling roll to a winding reel. The rapidly quenched ribbon such as an amorphous ribbon is produced by continuously and rapidly quenching molten metal on the surface of a cooling roll rotating at a high speed. Particularly, an amorphous ribbon having a thickness of about 30 µm is produced by rotating the cooling roll at such a high circumferential speed as in a range of 20∼40 meter/sec. Accordingly, there has been required a special means for transporting the rapidly quenched ribbon produced at such a high speed from the surface of the cooling roll to a reel. Japanese Patent Application Laid-Open Publication No. 59-43,772 discloses an ejector type transporting means in the form of a duct having a cavity of a flat rectangular section for blowing out air as a carrier fluid at high speed. The high speed carrier fluid generates a reduced pressure within the duct lower than the atmosphere to suck the atmospheric fluid into the duct and thereby guiding the rapidly quenched ribbon from the surface of the cooling roll into the duct and transporting it to the reel by the carrier fluid. The ejector type transporting means mentioned above can stably peel the ribbon from the surface of the roll and subsequently transport by the carrier fluid if the atmospheric fluid is not disturbed. The ejector type transporting means has however disadvantages that the suction force by means of an ejector is limited and if the ribbon is clogged in the duct or the ribbon peeling point on the surface of the cooling roll is unstably displaced up and down, the ribbon is broken at the inlet side of the duct. Japanese Patent Application Laid-open Publication Nos. 56-12,257 and 59-138,572 disclose means for transporting the rapidly quenched ribbon comprising two brush rolls adapted to apply a tension to the ribbon by sliding resistance. There is however disadvantages that since the rotating speed of the brush rolls is more than 30 meter/sec, the progress of the ribbon is unstable and the ribbon is easily transversely displaced owing to a difference of tension so that it is difficult to continuously transporting the ribbon from the surface of the cooling roll. Furthermore, in order to apply an adequate tension, it is necessary to apply a large screw down or pressing force to the upper and lower brush rolls and results in a tendency of a breakdown of the ribbon. Japanese Utility Model Application Laid-open Publication No. 61-167,248 discloses a ribbon transporting apparatus comprising a pinch roll including upper and lower solid rolls, an air nozzle and a guide conveyor. This transporting apparatus has however no training device and is not adapted to pass the ribbon at high speed. Furthermore, a plurality of tension applicator are sequentially arranged in the outlet side of the cooling roll and resulted in a large tension at the initial winding so that the ribbon is necessarily to break between the cooling roll and the pinch rolls. Japanese Patent Application Laid-open Publication No. 59-57,864 and Japanese Patent Application Publication No. 60-48,431 disclose means comprising dancer rolls for winding the ribbon. This winding means has however a drawback such that in order to improve the shape of the wound ribbon rolls it is necessary to apply a large tension, but the cooling roll is directly affected by such a large tension to render the casting unstable. Furthermore, Japanese Patent Application Publication No. 59-34,467 discloses an approximate magnet reel, but it has a drawback such that since the reel is adjacent to the cooling roll, a measurement and control system cannot be easily arrangement so that it is difficult to stably produce the ribbon for an industrialization. An inwardly blowing reel disclosed in Japanese Patent Application Laid-open Publication No. 57-3,901 is also difficult to continuously feed the ribbon from the cooling roll. EP-A-0 021 049 discloses a method and an apparatus for the inline string-up, in automatic fashion, of a rapidly advancing filament, particularly a glassy alloy strip, from a high speed continuous casting operation onto a rotating winding wheel. According to this prior art, the leading segment of the advancing filament is passed into the nip of two counterrotating brush rollers having a peripheral velocity exceeding that of the advancing filament to produce a sliding frictional tensioning of the filament. The two brush rollers and the engaged filament are then moved over the rotating winding wheel to lay a segment of the advancing filament onto the rotating winding surface. A cut-and-grip device associated with the winder is then actuated to cut the filament at the winding surface and to secure the filament onto the winder, whereupon winding of the advancing filament proceeds. JP-A-58 22 244 discloses a rotatably mounted brush roll for guiding an article on the lower end of a frame adjustably arranged against a wind-up roll and a belt conveyor. Further a nozzle forming a fluid jetting means is attached. In the early winding stage of the article to be wound a fluid is jetted from the fluid jetting means between the belt and the article and the free end of the article is floated upward. The free end is automatically guided onto the outer peripheral surface of the wind-up roll by the guiding means and is closely contacted with said surface. Although this prior art document discloses the combination of a brush roll and a solid roll, the brush roll is arranged for urging a leading end of the article to the winding-up solid roll in order to initially wind the leading end of the article to be wound on the solid roll rather than tensioning the article. Once the end of the article wound on the wind-up roll, the tension of the belt shaped article is controlled by the wind-up roll only. This means that the brush roll simply serves to catch the leading end during initial winding, but is not adjustably pressed against the solid wind-up roll so that the brush roll does not control the tension of the article. It is an object of the present invention to provide a method and an apparatus for transporting a rapidly quenched ribbon which is continuously produced on the surface of a cooling roll rotating at high speed, to a winding reel in a stable condition under an adequate tension without transversal displacement of the ribbon. According to the present invention, in a method of transporting a rapidly quenched ribbon from a cooling roll to a winding reel, use is made of a pinch roll comprising a brush roll and a solid roll for transporting the ribbon such as to maintain an adequate tension in the ribbon. In a preferable embodiment of the present invention, the tension applied to the ribbon is controlled by adjusting at least one of an amount of pressing of the brush roll against the solid roll, a pressing force on the brush roll and a ratio between circumferential speeds of the pinch roll and the cooling roll. The tension to be applied is preferably controlled within a range of 2∼8 kg. An apparatus for transporting a rapidly quenched ribbon according to the invention comprises a pinch roll comprising of a brush roll and a solid roll arranged between a cooling roll and a winding reel. The brush roll comprises a roll shaft and a brush composed of metal wires spirally wound around the roll shaft in the form of double helical. The solid roll is preferably shaped in the form of a crown roll. In a preferable embodiment of the invention, the apparatus for transporting a ribbon comprises an inlet duct hood, a pinch roll comprising a brush roll and a solid roll included in a housing hood which is detachably connected to the inlet duct hood, a suction blower arranged at the outlet side of the pinch roll in an outlet hood connected to the housing hood and a truck carrying the hood including the pinch roll and the suction blower. The truck is movable from a position adjacent to the cooling roll beyond the winding reel. Further object and advantages of the present invention will become apparent as the following description of illustrative embodiments proceeds with reference to the drawings, in which: Fig. 1 is a side elevation of the transporting apparatus according to the invention in partly section; Fig. 2 is a front elevation of the pinch roll according to the invention; Fig. 3 is an enlarged sectional view of the brush roll; Fig. 4 is a schematic view illustrating an arrangement of the transporting apparatuses for transporting a ribbon from a reel to another reels; Fig. 5 is a schematic side view illustrating an embodiment of the transporting apparatus provided with means for measuring the pressing force and the tension applied to the ribbon; Fig. 6 is a schematic side view illustrating another embodiment for transporting a ribbon from a cooling roll to a winding reel; Figs. 7 and 8 is a schematic side view similar to Fig. 6 illustrating an operation of the transporting apparatus; Fig. 9 is a diagram showing a correlation between the tension applied to the ribbon and the amount of pressing of the brush roll against the solid roll; Fig. 10 is a diagram showing a correlation between the tension applied to the ribbon and the pressing force of the pinch roll; Fig. 11 is a diagram showing a correlation between the tension applied to the ribbon and the ratio of circumferential speeds of the pinch roll and the cooling roll; Fig. 12 is a diagram showing a relation between the tension applied to the ribbon and rates of rotation of the pinch roll; Fig. 13 is a diagram showing variations of the tension applied to the ribbon by changing an electric current supplied to a motor driving the pinch roll; and Figs. 14∼16 are diagrams showing variations of the tension applied to the ribbon during transporting. The present invention will be more fully described with reference to the accompanying drawings. Referring to Fig. 1 illustrating an embodiment of the apparatus for transporting a rapidly quenched ribbon according to the present invention, the numeral 1 designates a cooling roll adapted for rapidly quenching molten metal from a pouring nozzle 2 to produce a rapidly quenched ribbon 3 which is peeled from the surface of the cooling roll 1 by means of an air jet of an air knife 4. The transporting apparatus 5 includes an inlet duct hood 6a having a suction inlet 7 directing in the tangential direction with respect to the outer periphery of the cooling roll for providing a passage for transporting the ribbon. Within a housing hood 6b, there is provided with a pinch roll 8 which comprises a lower brush roll 9 and an upper solid roll 10 and a suction blower 11 arranged at the outlet side of the pinch roll 8 in an outlet duct hood 6c. The hood 6b and 6c including the pinch roll 8 and the suction blower 11 is mounted on a truck 12 which is movable on rails 13 which is extended from a position adjacent to the cooling roll 1 towards a winding reel. The brush roll 9 has a brush 14 composed of a belt of metal wires such as stainless steel fibers spirally wound around a roll shaft 15 in the form of a single helical or double helical (Fig. 2). The roll shaft 15 is rotatably supported at the opposite ends by means of bearings 17 each of which is operated up and down by a pneumatic or hydraulic pressing cylinder 17. The roll shaft 15 is also connected to a motor 18 by means of a pulley coupling 19 as shown in Fig. 2. Preferably, in order to prevent the ribbon from transversely displacing, the roll shaft 15 is provided with the brush 14 wound in the form of double helical consisting of clockwise and anticlockwise half portions at the opposite sides of the center and the solid roll 10 is shaped by a radial crown having a larger diameter at the center portion than that at the opposite ends of the roll barrel or a tapered crown so that the pressing force by the brush roll 9 becomes large at the central portion in the width direction of the ribbon to force it to pass in the center of the roll without any transverse displacement. The brush roll 9 is pressed against the solid roll 10 by means of a pneumatic or hydraulic pressing cylinder 17 to apply a tension to the ribbon 3 by a sliding resistance between the brush roll 9 and the solid roll 10. Thus, the tension of the ribbon can be controlled by at least one of a pressing force of the pinch roll 8, an amount of pressing of the brush roll 9 against the solid roll 10 and a ratio between circumferential speeds of the pinch roll 8 and the cooling roll 1. The amount of pressing of the brush roll against the solid roll is defined by a distance between axes of the brush roll 9 and the solid roll 10 when the brush roll 9 is pressed against the solid roll and a distance between axes of both rolls when the brush 14 of the brush roll initially contacts the surface of the solid roll 10 is prescribed as zero. The material of the brush 14 may be selectively used form various material according to the material and other properties of the ribbon to be transported without limiting to the material mentioned above. The shape of the solid roll 10 and the kind of helical winding of the brush 14 may be selectively determined according to a transporting speed and an amount of the transversal displacement. The brush roll 9 may be positioned above the solid roll 10 so that the pinch roll 8 comprises an upper brush roll and a lower solid roll, if necessary. Fig. 4 illustrates an arrangement of the transporting apparatuses 5 as shown in Figs. 1 and 2 for transporting the rapidly quenched ribbon from a reel 20 to other reels 21 and 22. In this arrangement, the ribbon 3 is rewound from a reel 20 by means of a first transporting apparatus 5-1 and is checked by means of a defect detector 23. After checking, the ribbon 3 is transported by a second transporting apparatus 5-2 to a shear 24. When the defect detector 23 detects a defect in the ribbon 3 to provide an output signal to a controller 25, the shear 24 and a movable guide 26 are actuated by their actuators in response to signals from the controller to cut the defective ribbon and reject it into a scrap box 27. The ribbon having no defect is directed to a third or fourth transporting apparatuses 5-3 or 5-4 by the movable guide 26 and is then wound on the real 21 or 22. During the transportation mentioned above, the ribbon can be transported under an adequate tension by the transporting apparatus 5-1∼5-4 without any transversal displacement. Fig. 5 illustrates an embodiment of the transporting an apparatus provided with a load cell 30 on an arm 31 supporting the brush roll 9 for measuring the pressing force of the pressing cylinder and a tension meter 32 for measuring the tension applied to the ribbon 3. Figs. 6∼8 illustrate another arrangement for transporting the rapidly quenched ribbon 3 from the cooling roll 1 to winding reels 35 and 36 of a revolving wheel 33. Referring Fig. 6, a ribbon 3 rapidly quenched on the surface of the cooling roll 1 is peeled by air jet from the air knife 4 and sucked into the inlet duct hood 6a by suction force of the suction blower 11. In the housing hood 6b, the ribbon 3 passes between the brush roll 9 and the solid roll 10 of the pinch roll 8 and an irregular front end portion of the ribbon 3 is removed by sucking action of the blower 11. The brush roll 9 is pressed against the ribbon 3 on the solid roll 10 by the pressing cylinder to apply a predetermined tension of 2∼8 kg to the ribbon such as to stabilize the pass line of the ribbon. In this stage, the ribbon is continuously reeled from the cooling roll 1 and regularly guided by means of a deflector roll 34. The truck 12 carrying the pinch roll 8 is then moved towards the revolving wheel 33 to maintain a tension within a range of 2∼8 kg applied to the ribbon. It is preferable to maintain a relation of V₁>V₂»V₃ between a circumferential speed V₁ of the pinch roll 8, a transporting speed V₂ and a moving speed V₃ of the truck 12. Referring Fig. 7 which illustrates a condition just before the ribbon is wound on winding reels 35 and 36 of the revolving wheel 33 after the truck 12 has passed beyond the revolving wheel 33, the ribbon 3 is contacted with a dancer roll 37, deflector rolls 38 and 39, a tension separator 40 and deflector rolls 41 and 42 to prepare for winding the ribbon on the reels 35 and 36. Subsequently, a revolving wheel 33 including the reels 35 and 36 is revolved to approach the first winding reel 35 to the ribbon 3. Thus, the ribbon 3 is transported from pinch roll 8 to the winding reel 35 by a cutting machine 45 which comprises a deflector roll 42, a pressing roll 43 and a knife 44. Further referring Fig. 8, the ribbon 3 is cut by means of a knife 44 to separate from the ribbon portion held by the pinch roll 8 of the transporting apparatus and simultaneously the pressing roll 43 presses the cut end of the ribbon against the reel 35 which can continuously take up the ribbon. The winding speed of the reel 35 is preferably controlled to provide an adequate tension by detecting and adjusting the position of the dancer roll 37. The tension separator 40 operates to separate the tension of the ribbon such as to maintain a necessary high tension between the separator 40 and the winding reel 35 while a low tension between the separator 40 and the cooling roll 1. It is important to maintain the ribbon to be transported under a tension within a range of 2∼8 kg in order to stabilize the transportation of the ribbon because under a lower tension than 2 kg the ribbon slacks to occur a transversal displacement in the duct hood before or at the pinch roll, thereby striking the ribbon against the inner side wall of the duct hood or moving the ribbon out the pinch roll and the ribbon is broken. Furthermore, under such a low tension, a peeling point at which the ribbon is peeled from the surface of the cooling roll is displaced and the ribbon is largely flapped up and down when the thickness of the ribbon is varied to cause the pass line unstable, so that the ribbon is broken before the pinch roll. While under a higher tension than 8 kgf the ribbon may break at the pinch roll owing to defects such as a crack and pit in the ribbon or an abrupt variation of the tension by increasing of a coefficient of friction between the brush roll and the solid roll or by winding to the rolls. When the ribbon is initially passed to the pinch roll, an adequate tension is applied to the ribbon by controlling the amount of pressing of the brush roll, the pressing force of the pressing cylinder and the ratio between circumferential speeds of the pinch roll and the cooling roll. When the tension applied to the ribbon is varied out the adequate range owing to a variation of peeling point on the cooling roll, a variation of thickness of the ribbon, a transversal displacement of the ribbon and the like during transporting the ribbon, the tension must be controlled by adjusting at least one of the amount of pressing of the brush roll, the pressing force of the pressing cylinder and the ratio between the circumferential speeds of the pinch roll and the cooling roll. A series of test were carried out to determine a relationship between the tension applied to the ribbon and the amount of pressing of the brush roll, the pressing force of the pressing cylinder and the ratio between the circumferential speeds of the pinch roll and the cooling roll. In the tests, the transporting apparatus as shown in Fig.5 was used and a rapidly quenched ribbon having a width of 100 mm and a thickness of 30 µm was initially passed between the brush roll and the solid roll. The results of the tests are shown in Figs. 9∼11. Fig. 9 is a diagram showing various relation between the amount of pressing of the brush roll and the tension applied to the ribbon when the ribbon was initially passed between the brush rolls having an outer diameter of 200∼350 mm and a solid roll under a condition of the ratio between the circumferential speeds of the pinch roll and the cooling roll of 1.0. It will be seen from the diagram shown in Fig. 9 that there is a correlation between the amount of pressing of the brush roll and the tension applied to the ribbon and it is possible to apply a tension within the range of 2∼8 kg to the ribbon by control the amount of pressing of the brush roll to keep it within a range. The proper range of the amount of pressing of the brush roll is however different according to the material and the diameter of the metal wire of the brush so that it is necessary to adjust the range in corresponding to the selected brush roll. Generally the pressing or screw down force corresponds to the mount of pressing of the roll when the pinch roll comprises a pair of conventional solid roll. However, the pinch roll according to the present invention comprises a brush roll and a solid roll so that the amount of pressing of the brush roll does not correspond to the pressing force owing to the material and diameter of metal wires, the used duration and the loading condition of the brush roll. Accordingly, the tension applied to the ribbon is effectively controlled by adjusting the pressing force by the pressing cylinder as shown in Fig. 10 which shows a correlation between the tension applied to the ribbon and the pressing force of the pressing cylinder as a result from a series of tests. In the tests, a brush roll having brushes of stainless steel fibers of 0.1 mm diameter was used and the ratio between the circumferential speeds of the pinch roll and the cooling roll was 1.0. Additionally another brush rolls rather than the stainless steel fiber brush roll are tested under the same condition. It is seen from results of these tests that the tension applied to the ribbon is advantageously maintained in the range of 2∼8 kg by adjusting the pressing force within a range of 10∼100 kg under a condition that a ratio between the circumferential speeds of the pinch roll and the cooling roll is 0.1. Fig. 11 shows the correlation between the tension applied to the ribbon and the ratio of the circumferential speeds of the pinch roll and the cooling roll when a brush roll having a brush of brass alloy wires (0.2 mm) is pressed against a solid roll by an amount of pressing of 1 mm. It is seen from the Fig. 1 that when the ratio is lower than 1.0, the tension becomes lower than 2 kg to slack the ribbon and when the ratio is higher than 1.3, the tension becomes higher than 8 kg to break the ribbon. Additionally, another brush rolls are tested under the same condition. It is seen from results of these tests that the tension applied to the ribbon is advantageously maintained in the range of 2∼8 kg by adjusting the ratio within in the range of 1.0∼1.3 when the amount of pressing is 1 mm. Figs. 12 and 13 show diagrams showing variation of tensions applied to a ribbon having a width of 100 mm and a thickness of 30 µm by changing rates of rotation of the driving motor connected to the brush roll and current supplied to the driving motor. It can be seen from these Figs. 12 and 13 that there is no correlation between the circumferential speed of the brush roll and the tension and also between the current and the tension which is largely varied. Example 1 An apparatus as shown in Fig. 5 was used to transport a rapidly quenched ribbon of Fe-Si-B amorphous alloy to a winding reel at a circumferential speed of 33 m/sec of a solid roll and a brush roll as described below. The amount of pressing of brush roll, the pressing force and the ratio of circumferential speeds at the initial pass were changed as shown in Table 1 and the tension, amount of transversal displacement and stability of the ribbon were measured. The results of these measurement are shown in Table 1 together with results of comparative tests carried by using pinch rolls comprising a pair of brush rolls and a pair of solid rolls, respectively. (1) Solid roll (crown roll) Diameter of roll : 201 mm at center 200 mm at opposite ends Length of roll barrel : 250 m Material of roll : S45C (2) Brush roll Diameter of roll : 200 mm Length of roll barrel : 250 mm Diameter of roll shaft : 50 mm Material of roll shaft : S45C Diameter of brush wire : 0.1 mm Material of brush wire : stainless steel fiber Type of brush : Double helical windings of clock wise and anticlockwise half portions separated at the center of the roll such as to center the ribbon in the passing direction. Example 2 An apparatus as shown in Fig. 5 was used to transport a rapidly quenched ribbon of Fe-Si-B amorphous alloy to a winding reel. The ribbon was initially passed through the pinch roll as described below under a tension of 4 kg. After two seconds, the tension was varied and then the amount of pressing was adjusted to stabilized the tension as shown in Fig. 14. The initial pass conditions of the amount of pressing of 0.5 mm, pressing force of 20 kg and the ratio of circumferential speed of 1.2 was used. (1) Solid roll (flat roll) Diameter of roll : 80 mm Length of roll barrel : 170 mm Material of roll : S45C (2) Brush roll Diameter of roll : 80 mm Length of roll barrel : 170 mm Diameter of roll shaft : 25 mm Material of roll shaft : S45C Diameter of brush wire : 0.2 mm Material of brush wire : stainless steel fiber Type of brush : Closely spirally wound around the roll shaft by clockwise or anticlockwise winding Comparative Example 1 A pinch roll comprising a pair of solid rolls as described below was used. A rapidly quenched ribbon of Fe-Si-B amorphous alloy was guided to the pinch roll. When the ribbon was bit by the pinch roll, a variation of tension as shown in Fig. 15 generates and after several seconds the ribbon was broken. Accordingly, the ribbon could not be transported to a winding reel. (1) Solid roll (upper crown roll) Diameter of roll : 83 mm at center, 80 mm at opposite ends Length of roll barrel : 70 mm Material of roll : S45C (2) Solid roll (lower flat roll) Diameter of roll : 80 mm Length of roll barrel : 70 mm Material of roll : S45C Comparative Example 2 A pinch roll comprising a pair of brush rolls as described below was used in place of the pinch roll comprising the brush roll and the solid roll in the transporting apparatus as shown in Fig. 5. A rapidly quenched ribbon of Fe-Si-B amorphous was guided to the pinch roll. When the ribbon was bit by and initially passed through the pinch roll, the ribbon slacked and transversally displaced. After short run, the ribbon was broken and could not be transported to a winding reel. When the ratio between the circumferential speeds of the pinch roll (brush rolls) and the cooling roll was decreased to 0.9 and the ribbon slacked, the rate of rotation of the pinch roll was controlled to increase the ratio to 1.0 or more and the pressing force was set to 20 kg or more, but the slack of the ribbon could not be removed and the break of the ribbon could not be prevented. Brush roll (both the upper and lower rolls) Diameter of roll : 80 mm Length of roll barrel : 170 mm Diameter of roll shaft : 25 mm Material of roll shaft : S45C Diameter of brush wire : 0.2 mm Material of brush wire : stainless steel fiber Type of brush : closely spirally wounded around roll shaft Comparative Example 3 A pinch roll comprising a solid roll and a brush roll as shown in Fig. 5 was used in the transporting apparatus to transport a rapidly quenched ribbon of Fe-Si-B amorphous to a winding reel. Under a condition of a pressing force of 100 kg and a ratio between circumferential speeds of 1.3, the ribbon was bit and then initially passed through the pinch roll to apply a tension of 8 kg to the ribbon. After two seconds, the ribbon was transported to the winding reel. As a result, the ribbon peel point was displaced on the cooling roll and the pressing force increased up to 150 kg to break the ribbon before the pressing force can be decreased. Accordingly, the ribbon could not be wound on the winding reel.

Claims: A method of transporting a rapidly quenched ribbon (3) from a cooling roll (1) to a winding reel (21, 22 or 33) by a pinch roll, characterized in that said pinch roll (8) comprises a brush roll (9) and a solid roll (10) for transporting the ribbon (3) such as to maintain an adequate tension in the ribbon (3). A method claimed in claim 1, characterized in that the tension applied to the ribbon (3) is controlled by adjusting at least one of an amount of pressing of the brush roll (9) against the solid roll (10), a pressing force on the brush roll and a ratio between circumferential speeds of the pinch roll (8) and the cooling roll (1). An apparatus for transporting a rapidly quenched ribbon by a pinch roll characterized in that the pinch roll (8) comprises a brush roll and a solid roll (10) arranged between a cooling roll (1) and a winding reel (21, 22 or 33). An apparatus claimed in claim 3, characterized in that the brush roll (9) comprises a roll shaft (15) and a brush (14) composed of metal wires spirally wound around the roll shaft in the form of double helical. An apparatus claimed in claim 4, characterized in that the solid roll (10) is shaped in the form of a crown roll. An apparatus for transporting a rapidly quenched ribbon to a winding reel, characterized by an inlet duct hood (6a), a pinch roll (8) comprising a brush roll (9) and a solid roll (10) included in a housing hood (6a) which is detachably connected to the inlet duct hood, a suction blower (11) arranged at the outlet side of the pinch roll (8) in an outlet hood (6c) connected to the housing hood (6b) and a truck (12) carrying the hoods including the pinch roll (8) and the suction blower (11). An apparatus claimed in claim 6, characterized in that the truck (12) is guided to move from a position adjacent to the cooling roll (1) beyond the winding reel.

Inventors: HIRAMATSU, TERUO C/O TECHNICAL RESEARCH DIVISION, MORITO, NOBUYUKI C/O TECHNICAL RESEARCH DIVISION, SHIBUYA, KIYOSHI C/O TECHNICAL RESEARCH DIVISION, YOKUMOTO, MASAO C/O TECHNICAL RESEARCH DIVISION
Applicants: KAWASAKI STEEL CORPORATION
Application year: 1988
Main classification: B22D11
IPC codes: B22D11, B21C47