SEMICONDUCTOR LASER DEVICES

Abstract: A semiconductor laser device comprises a p-­ type semiconductor substrate (11) and a multi-layered crystal structure with an active layer (14) for laser-­ oscillating operation, the multi-layered crystal structure being disposed on the substrate (11) and having a striped channel region (100) through which current is supplied to the active layer and a light-absorbing region positioned outside of the channeled region by which a difference between the amount of light to be absorbed inside of the channeled region and the amount of light to be absorbed outside of the channeled region is created, which causes a difference in the effective refractive index of the active layer, resulting in an optical waveguide in the active layer, wherein the light-­ absorbing region is constituted by an n-type semiconductor substance, but a portion of the n-type semiconductor substance positioned in the vicinity of at least one of both facets is replaced by a p-type semiconductor substance (31, 111).

Description: BACKGROUND OF THE INVENTION 1. Field of the invention: This invention relates to a semiconductor laser device with a structure by which the rise of the temperature of the facets that is caused by the light absorption of the facets can be prevented, thereby attaining stabilized laser oscillation for a long period of time even at high output power. 2. Description of the prior art: Semiconductor laser devices that can oscillate coherent light have been used as light sources in optical disc apparatuses, optical communication systems, etc. As optical disc apparatuses, there have been add-on-memory type optical disc apparatuses that achieve writing operation and erasable memory type optical disc apparatuses that achieve erasable operation. Semiconductor laser devices that are used as light sources in these optical disc apparatuses are required to produce optical output power as high as 20-40 mW. For this purpose, in recent years, high output power semiconductor laser devices have been put into practice. The high output power semiconductor laser devices are disadvantageous in that the light-emitting facet thereof tends to deteriorate. It has been reported that high output power semiconductor laser devices oscillating laser light at high output power deteriorate in inverse proportion to the fourth power of the optical output in the cases where semiconductor laser devices with the same structure are examined. Figure 6 shows a conventional VSIS (V-channeled substrate inner stripe) semiconductor laser device (see "Applied Physics Letters", Vol.40, No.5, March 1982, pages 372-374), which is produced as follows: On a p-GaAs substrate 11, an n-GaAs current blocking layer 12 is formed. Then, a V-channel with a width W1 is formed on the current blocking layer 12 in such a manner that the V-channel reaches the substrate 11 through the current blocking layer 12. On the current blocking layer 12 including the V-channel, a p-GaAlAs cladding layer 13, a GaAs or GaAlAs active layer 14, an n-GaAlAs cladding layer 15, and an n-GaAs cap layer 16 are successively formed. Current for laser oscillation is confined by the n-GaAs current blocking layer 12 and only flows into the channel with a width W1. Laser light that is produced in the active layer 14 is absorbed by the n-GaAs current blocking layer 12 that is positioned outside of the V-channel, so that a difference arises in the effective refractive index between the portion of the active layer 14 corresponding to the V-channel and the other portions of the active layer 14 corresponding to the outside of the V-channel, resulting in an optical waveguide in the active layer 14. Thus, laser oscillation can be attained in a stabilized fundamental transverse mode. The said waveguiding structure functions as a loss-waveguide structure. This VSIS laser device is disadvantageous in that although it can attain laser oscillation in a stabilized fundamental transverse mode at a low output power level, it cannot continue to oscillate laser light for a long period of time at a high output power level with extreme reliability. The reasons why the above-mentioned laser device deteriorates at a high output power level are based on the deterioration of the shoulders of the V-channel in the vicinity of the facets, which is caused by heat generation of the n-GaAs current blocking layer 12 corresponding to the shoulder portions of the V-channel that absorbs light that leaks from the optical waveguide. The diffusion length of the minority carrier within the n-GaAs current blocking layer 12 is short, so that the carrier that is produced by the light absorption achieves a non-radiative recombination in the vicinity of the shoulder portions of the V-channel, resulting in the generation of heat. SUMMARY OF THE INVENTION The semiconductor laser device of this invention, which overcomes the above-discussed and numerous other disadvantages and deficiencies of the prior art, comprises a p-type semiconductor substrate and a multi-layered crystal structure with an active layer for laser-oscillating operation and cladding layers, the said multi-layered crystal structure being disposed on said substrate and having a striped channel region through which current is supplied to said active layer, an optical waveguide comprised by the portions of the active layer and the cladding layers located in the channel region, and a light-absorbing region positioned outside of said channel region, wherein said light-absorbing region is constituted, in the vicinity of at least one of both facets by a p-type semiconductor substance, and elsewhere by an n-type semiconductor substance. In a preferred embodiment, a portion which may be the entire portion of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance. In another preferred embodiment, an upper portion of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance and a lower portion thereof remains. In a further preferred embodiment, a portion with a limited width of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance. In another preferred embodiment, an upper portion with a limited width of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance and the lower portion thereof remains. Thus, the invention described herein makes possible the objective of providing a loss-waveguide semiconductor laser device in which portions of an n-type light-absorbing area that constitutes a waveguide are made of a p-type semiconductor substance in the vicinity of the facets, so that the rise of the temperature of the facets that is caused by the light absorption can be prevented and the deterioration of the facets can be suppressed even at high output power operation, thereby attaining laser oscillation with extreme reliability even at a high output power level. BRIEF DESCRIPTION OF THE DRAWINGS This invention may be better understood and its numerous objects and advantages will become apparent to those skilled in the art by reference to the accompanying drawings as follows: Figure 1 is a perspective view showing the decomposition of a semiconductor laser device of this invention. Figures 2A to 2C are schematic diagrams showing a production process of the semicondcutor laser device shown in Figure 1. Figure 3 is a perspective view showing the decomposition of another semiconductor laser device of this invention. Figure 4 is a perspective view showing the decomposition of another semiconductor laser device of this invention. Figures 5A to 5D are schematic diagrams showing a production process of the semiconductor laser device shown in Figure 4. Figure 6 is a perspective view showing a conventional VSIS semiconductor laser device. DESCRIPTION OF THE PREFERRED EMBODIMENTS This invention provides a semiconductor laser device in which the portions of a light-absorbing area in the vicinity of the facets are made of a p-type semiconductor substance in which the diffusion length of the minority carrier is long, so that the rise of the temperature of the facets that is caused by the light absorption can be prevented and the deterioration of the facets can be suppressed even at high output power operation, thereby attaining laser oscillation with extreme reliability even at a high output power level. Example 1 Figure 1 shows a VSIS semiconductor laser device of this invention, which is produced as follows: As shown in Figure 2A, on a p-GaAs substrate 11, a current blocking layer (that constitutes a light-absorbing region) 12 with a thickness of 0.7 µm is formed by liquid phase epitaxy. As shown in Figure 2B, the portions of the n-GaAs current blocking layer 12 in the vicinity of the facets are removed over a length of 10 µm each in the oscillation direction by an etching technique by the use of an SiO₂ film 41 as a masking means. Then, as shown in Figure 2C, by the organic metal thermal decomposition method a p-GaAs layer 31 with a thickness of 0.7 µm is selectively formed on the exposed portions of the p-GaAs substrate 11 from which the n-GaAs current blocking layer 12 has been removed. The SiO₂ film 41 is then removed. The p-GaAs layer 31 is flush with the remaining n-GaAs layer 12 because both layers 31 and 12 are formed with the same thickness on the substrate 11. Then, a V-channel 100 with a width of 4 µm and a depth of 1 µm is formed into a stripe such that it reaches the p-GaAs substrate 11 through the n-GaAs current blocking layer 12, resulting in a current path. Then, on the n-GaAs current blocking layer 12 and on p-GaAs layer 31 including the V-channel 100, a p-Al 0.42 Ga 0.58 As cladding layer 13 with a thickness of 0.15 µm at the outside of the V-channel 100, a p- or n-Al 0.14 Ga 0.86 As active layer 14 with a thickness of 0.08 µm, an n-Al 0.42 Ga 0.58 As cladding layer 15 with a thickness of 0.8 µm, and an n-GaAs contact layer 16 with a thickness of 1.5 µm are successively formed by liquid phase epitaxy in the same way as the growth method for use in conventional VSIS semiconductor laser devices. According to liquid phase epitaxy, the p-Al 0.42 Ga 0.58 As cladding layer 13 is formed on the n-GaAs current blocking layer 12 including the V-channel 100 so that the top surface thereof becomes flat, and accordingly the Al 0.14 Ga 0.86 As active layer 14 that is formed on the said flat cladding layer 13 becomes flat and uniform over the entire surface thereof. Thereafter, a p-side electrode 21 and an n-side electrode 22 are formed on the bottom face of the substrate 11 and the top surface of the contact layer 16, respectively, followed by cleaving the wafer, resulting in a semiconductor laser device with a Fabry-Pérot resonator for laser oscillation. The transverse mode that is attained by this semiconductor laser device is stabilized because light that leaks from the optical waveguide of the active layer 14 is absorbed by both the n-GaAs layer 12 and the p-GaAs layer 31 without the heat generation of the facets. The reasons therefor are as follows: In the vicinity of the facets that receive light with a high optical intensity, the p-GaAs layer 31 attains the absorption of light. Although electron-holes pairs are generated in the vicinity of the shoulder portions of the V-channel, because the relaxation time of the minority carrier (i.e., electrons) of the p-GaAs layer 31 is relatively long, the electrons do not relax in the vicinity of the shoulder portions of the V-channel but they move to a place that is far from the said shoulder portions and relax therein, which causes the generation of heat. Thus, the heat generation does not arise in the shoulder portions of the V-channel, but it arises over the whole light-absorbing area including the n-GaAs layer and the p-GaAs layer, so that the rise of the temperature of local portions of the light-absorbing area can be suppressed. Therefore, the deterioration of the facets based on the heat generation of the shoulder portions of the V-channel does not occur in the semiconductor laser device of this invention, and the said semiconductor laser device can attain laser oscillation with extreme reliability even at high output power operation. When the light-emitting facet was coated with a substance with a reflectivity of 4% and the other facet was coated with a substance with a reflectivity of 97%, the facets of the semiconductor laser devie were not deteriorated even at high output power operation, 100 mW. Example 2 Figure 3 shows another VSIS semiconductor laser device of this invention, which is produced in the same way as that of Example 1, except that the portions of the n-GaAs current blocking layer 12 in the vicinity of the facets are not completely removed, but the upper portions only thereof are removed and the lower portions thereof remain. The p-GaAs layer 31 is formed on the remaining portions of the n-GaAs current blocking layer 12 in the vicinity of the facets. In this way, the shoulder portions of the V-channel 100 in the vicinity of the facets are constituted by the p-GaAs layer 31, so that the heat generation of local areas of the light-absorbing layers 12 and 31 can be suppressed for the same reasons as mentioned above. Moreover, current is confined by the n-GaAs layer 12 that underlies the p-GaAs layer 31 even in the vicinity of the facets, so that the threshold current of this semiconductor laser device is less than that of the semiconductor laser device of Example 1. When the light-emitting facet was coated with a substance with a reflectivity of 4% and the other facet was coated with a substance with a reflectivity of 97%, these facets of this semiconductor laser device did not deteriorate even at high output power operation, 100 mW. Example 3 Figure 4 shows another VSIS semiconductor laser device of this invention, in which the p-GaAs layer 31 with a width of W2 (W2 > W1) is disposed instead of the n-GaAs current blocking layer 12 in the vicinity of the facets. The portions with a width W2 of the current path in the vicinity of the facets are defined by the n-GaAs current blocking layer 12 that is positioned outside of the p-GaAs layer 31, and the threshold current of this semiconductor laser device is less than that of the semiconductor laser device of Example 1. When the value of W2 was set to be 10 µm and the light-emitting facet and the other facet were coated with substances with reflectivities of 4% and 97%, respectively, these facets of this semiconductor laser device did not deteriorate even at high output power operation, 100 mW. The semiconductor laser device shown in Figure 4 can be produced by a process shown in Figure 5: As shown in Figure 5A, mesa portions 111 with a length of 10 µm in the oscillation direction and a height of 1.0 µm are formed on the portions of a p-GaAs substrate 11 in the vicinity of the facets by photolithography and an etching technique. Then, as shown in Figure 5B, on the p-GaAs substrate 11 with the mesa portions 111, an n-GaAs layer 12 with a thickness of 2.0 µm at the outside of the mesa portions 111 is formed by liquid phase epitaxy. As mentioned in Example 1, by the use of liquid phase epitaxy as a crystal growth technique, the n-GaAs layer 12 becomes flat over the entire surface thereof. Thereafter, the wafer is etched so that the thickness of the n-GaAs layer 12 becomes 0.7 µm at the outside of the mesa portions 111, and as shown in Figure 5C, the top surface of each of the mesa portions 111 is exposed to the outside. Then, as shown in Figure 5D, a V-channel 100 with a width of 4 µm and a depth of 1 µm is formed into a stripe from one facet to the other facet so that it reaches the p-GaAs substrate 11 via the n-GaAs layer 12. Then, a p-AlGaAs cladding layer 13, a p- or n-AlGaAs active layer 14, a p-AlGaAs cladding layer 15, and an n-GaAs contact layer 16 are formed on both the n-GaAs layer 12 and the p-GaAs mesa portions 111 including the V-channel 100 in the same way as mentioned in Example 1, resulting in a semiconductor laser device shown in Figure 4. Example 4 Another VSIS semiconductor laser device of this invention is obtainable in which the structure of the laser device of Figure 4 is incorporated into the structure of the laser device of Figure 3. The lower portions of the p-GaAs layer 31 in the vicinity of the facets shown in Figure 4 are replaced by the n-GaAs layer over the width of W2. Thus, the n-GaAs layer underlies the p-GaAs layer over the width of W2 in the vicinity of the facets, whereby the same effect as mentioned above can be attained. Although the above-mentioned examples disclose device structures that a p-GaAs layer is disposed on both facet sides, the p-GaAs layer can be disposed on the light-emitting facet side alone. This invention is also applicable to optical waveguide structures other than those described herein. Moreover, although the above-mentioned examples disclose only liquid phase epitaxy as a crystal growth technique, molecular beam epitaxy, metal organic-chemical vapor deposition, the thermal decomposition method, vapor phase epitaxy, and so on can be used.

Claims: A semiconductor laser device comprising a p-type semiconductor substrate (11) and a multi-layered crystal structure (12-16) with an active layer (14) for laser-oscillating operation and cladding layers (13, 15), the said multi-layered crystal structure (12-16) being disposed on said substrate (11) and having a striped channel region (100) through which current is supplied to said active layer (14), an optical waveguide comprised by the portions of the active layer (14) and the cladding layers (13, 15) located in the channel region (100), and a light-absorbing region, positioned outside of said channel region (100), wherein said light-absorbing region is constituted, in the vicinity of at least one of both facets by a p-type semiconductor substance (31, 111), and elsewhere by an n-type semiconductor substance. A semiconductor laser device according to claim 1, wherein a portion of said n-type semiconductor substance originally positioned in the vicinity of said at least one facet has been replaced by said p-type semiconductor substance (31). A semiconductor laser device according to claim 2 wherein the replaced portion of said n-type semiconductor substance is the entire portion. A semiconductor laser device according to claim 1, wherein an upper portion of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance (31) and a lower portion thereof remains. A semiconductor laser device according to claim 1, wherein a portion with a limited width of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance (31). A semiconductor laser device according to claim 1, wherein an upper portion with a limited width of said n-type semiconductor substance that is positioned in the vicinity of at least one facet is replaced by said p-type semiconductor substance (31) and a lower portion thereof remains.

Inventors: HAYASHI, HIROSHI, KANEIWA, SHINJI, KAWANISHI, HIDENORI, MORIMOTO, TAIJI, YAMAGUCHI, MASAHIRO
Applicants: SHARP KABUSHIKI KAISHA
Application year: 1988
Main classification: H01S3
IPC codes: H01S5