Non-staining and slightly-staining antiozonants

Abstract: There is disclosed compounds having, within their structural formulae, a trivalent moiety: >N- - which exhibit anitozonant activity when added to rubber compositions at antiozonant effective levels and which exhibit synergistic antiozonant activity when used with conventional antiozonants in rubber compositions. There is also disclosed novel compounds which can be used as antiozonants.

Description: Field of the Invention This invention relates to compounds having, within their structural formulae, a trivalent moiety: It relates to compounds which exhibit antiozonant activity when added to rubber compositions at antiozonant effective levels. It also relates to compounds which exhibit synergistic antiozonant activity when used with conventional antiozonants in rubber compositions. It also relates to novel compounds which can be used as antiozonants. Background Art Essentially all types of rubber, both natural and synthetic, and particularly rubbers formed from dienes are known to be susceptible to deterioration resulting from prolonged exposure to ozone. A great deal of effort has been expended by those engaged in the field of polymer technology to develop various antiozonants that will effectively inhibit the adverse effects of ozone on polymeric compositions. The more commercially available antiozonants for rubber and rubber goods are the several derivatives of para-phenylenediamine. These derivatives generally suffer from one or more of the following limitations: limited solubility in rubber; low but significant volatility and water solubility; reactivity toward other species such as dioxygen; staining and discoloration. One approach to decreasing the water solubility and volatility of these derivatives of para-phenylenediamine has been to increase their molecular weight. As a class, the para-phenylenediamine derivatives are very active antiozonants but their usefulness is greatly limited by their severe staining and discoloring nature. Thus considerable effort has been expended in the search for non-staining, non-discoloring antiozonants. Many materials have been investigated for this purpose including lactams, phosphites, phosphines, thioureas, thiosemicarbazides and substituted olefins but all have significant drawbacks and limitations. The lactams which are reported to have excellent dynamic ozone protection are very scorchy. Phosphites and phosphines react readily with peroxide and sulfur curatives and so are not useful in conventionally cured goods. Of the thioureas and thiosemicarbazides the most studied are the trisubstituted derivatives especially tributyl thiourea. Chemical literature teaches that the most active materials of either class are the trisubstituted derivatives. However, like the lactams, these materials are quite scorchy and thus have found little, if any, commercial use. A substituted olefin is marked by Bayer as a non-discoloring antiozonant but it is only recommended for use in ozone-resistant rubbers such as polychloroprene. In addition to the above-mentioned materials a recent patent claims antiozonant activity for cyanoalkyl esters of dithiocarbamic acids. This invention discloses a new class of antiozonants which are stable toward dioxygen. Their protective reactivity is specifically directed toward ozone which greatly increases their persistence in rubber. In addition, their molecular weights can be adjusted to improve volatility and water extractability characteristics. An additional benefit of these new antiozonants is that they are largely non-discoloring and non-staining. Thus, they can be used in rubber goods heretofore unable to be protected from the degradative effects of ozone, e.g. white sidewalls on tires, shoe soles, boots and rubbers, and gaskets which come in contact with painted surfaces. Other species in the class have the benefit of being less staining and less discoloring than the para-phenylenediamine derivatives commercially available. Disclosure of the Invention In accordance with the practice of the present invention, there is disclosed a rubber composition comprising a non-halogenated rubber susceptible to ozone degradation and from 2.5 to 10 phr of a compound represented by the following structural formula: wherein G is >N-R³; wherein R¹, R², R³ are independently selected from the group consisting of: (a) alkyl radicals having 1 to 25 carbon atoms, wherein said alkyl may be substituted by an amino group, (b) cycloalkyl radicals having 3 to 25 carbon atoms, wherein said cycloalkyl may be substituted by an amino group, (c) aryl radicals having 6 to 25 carbon atoms; and (d) radicals selected from the group consisting of those radicals represented by the following structural formulae: wherein R¹⁷, R¹⁸, R¹⁹ and R²⁰ are independently selected from the group consisting of hydrogen; substituted and unsubstituted alkyl radicals having 1 to 25 carbon atoms; and substituted and unsubstituted aryl radicals having 6 to 25 carbon atoms; n is an integer of 1 to 6; wherein R³ can also be hydrogen; wherein when a radical from member (a) or (b) is substituted with an amino group, the alpha atom of the radical is free of amino groups. There is also further disclosed a composition of matter represented by the following structural formula: wherein G is >N-R⁴³; wherein R⁴¹, R⁴², R⁴³ are independently selected from the group consisting of (a) alkyl radicals having 1 to 25 carbon atoms, wherein said alkyl may be substituted by an amino group, (b) cycloalkyl radicals having 3 to 25 carbon atoms, wherein said cycloalkyl may be substituted by an amino group, (c) aryl radicals having 6 to 25 carbon atoms, and (d) radicals selected from the group consisting of those radicals represented by the following structural formulae: wherein R⁵⁷, R⁵⁸, R⁵⁹ and R⁶⁰ are independently selected from the group consisting of hydrogen, alkyl radicals having 1 to 25 carbon atoms and aryl radicals having 6 to 25 carbon atoms; n is an integer of 1 to 6; wherein when a radical from members (a) or (b) is substituted with an amino group, the alpha atom of the radical is free of amino groups; wherein at least one of R⁴¹, R⁴² and R⁴³ is selected from the radicals of member (d). Compounds conforming to structural formulae I and XI can be prepared as follows: Preparation of a 1,3-disubstituted thiourea Two moles of a primary amine are added to a one-liter, three-neck flask fitted with a mechanical stirrer, addition funnel and a condenser. Next, is added 250 milliliters of a solvent, such as isopropanol. Then 1.1 moles of carbon disulfide are added with stirring, at a rate such that the reflux level is kept to the lower quarter of the condenser. When the addition of the carbon disulfide is complete, the mixture is refluxed with stirring until hydrogen sulfide evolution ceases. The product can be recovered by cooling the mixture and filtering off the product or by distilling out the solvent. General procedure for preparation of tetrahydro-(S)-triaz inethiones One mole of a 1,3-disubstituted thiourea and two moles of formalin are combined in a two liter flask with 250 mL solvent such as toluene and heated with stirring to 50 to 60°C. More solvent may be needed depending on the thiourea. After 0 to 6 hours, one mole of a primary amine is added and heating is continued overnight. If analysis shows poor conversion of the thiourea, additional formalin and amine are added in a 2 to 1 ratio and the reaction continued. The product may be recovered by appropriate conventional methods such as crystallization and filtration or distillation of the solvent. It may be purified further by such methods as distillation, extraction or chromatography. The following compounds are representative of the novel composition of matter of the present invention: tetrahydro-1,3-di-(4-isopropoxyphenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-di-(4-isopropoxyphenyl)-5-t-octyl-(S)-triazine thione; tetrahydro-1,3-di-(4-anilinophenyl)-5-t-octyl-(S)-triazine thione; tetrahydro-1,3-di-(4-anilinophenyl)-5-hexadecyl-(S)-triaz ine thione; tetrahydro-1,3-di-(4-o-toluidinophenyl)-5-hexadecyl-(S)-triazine thione; tetrahydro-1,3-bis-(4-diethylaminophenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-bis-(4-diethylaminophenyl)-5-t-octyl-(S)-triazine thione; tetrahydro-1,3-bis-[4-(1,3-dimethylbutylamino)-phenyl]-5-octyl-(S)-triazine thione; tetrahydro-1,3-bis-[4-(1,3-dimethylbutylamino)-phenyl]-5-isopropyl-(S)-triazine thione; tetrahydro-1,3-di-(4-dodecylmercaptomethylphenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-di-(4-dodecylmercaptomethylphenyl)-5-cyclohexyl-(S)-triazine thione; tetrahydro-1,3-di-(4-isopropylaminophenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-di-(4-isopropylaminophenyl)-5-t-octyl-(S)-triazine thione; In addition to those compounds immediately above, the following compounds can be used in the rubber compositions of the present invention: tetrahydro-1,3,5-tributyl-(S)-triazine thione; tetrahydro-1,3-diethyl-5-cyclohexyl-(S)-triazine thione; tetrahydro-1,3,5-tricyclohexyl-(S)-triazine thione; tetrahydro-1,3,5-tribenzyl-(S)-triazine thione; tetrahydro-1,3-diphenyl-5-butyl-(S)-triazine thione; tetrahydro-1,3-dibutyl-(S)-triazine thione; Preferred compounds are the following: tetrahydro-1,3-di-(4-isopropoxyphenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-di-(4-isopropoxyphenyl)-5-t-octyl-(S)-triazine thione; tetrahydro-1,3-di-(4-anilinophenyl)-5-t-octyl-(S)-triazine thione; tetrahydro-1,3-bis-(4-diethylaminophenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-bis-(4-diethylaminophenyl)-5-t-octyl-(S)-triazine thione; tetrahydro-1,3-bis-[4-(1,3-dimethylbutylamino)phenyl]-5-octyl-(S)-triazine thione; tetrahydro-1,3-bis-[4-(1,3-dimethylbutylamino)phenyl]-5-isopropyl-(S)-triazine thione; tetrahydro-1,3-di-(4-isopropylaminophenyl)-5-butyl-(S)-triazine thione; tetrahydro-1,3-di-(4-isopropylaminophenyl)-5-t-octyl-(S)-triazine thione; EXAMPLE 1 Preparation of tetrahydro-5-(t)-butyl-1,3-di-n-butyl-(S)-triazinethione Formalin (40.5g; 37%; 0.50mol) and 1,3-dibutyl thiourea (47.1g; 0.25 mol) were combined in a 500 mL Erlenmeyer flask and heated to approximately 50°C. Sufficient isopropanol was added to yield a homogeneous solution which was heated for 6 hours after which t-butyl amine (18.3g; 0.25 mol) was added. Additional isopropanol was required to maintain homogeneity. After stirring at reflux overnight, the isopropanol was stripped off on a rotary evaporator. The residue was diluted with 200 mL of 75/25, v/v, ether/hexane solution, washed with dilute acetic acid, water and saturated NaHCO₃. After drying with K₂CO₃, the solvent was removed on a rotary evaporator to give 67.2g (94% yield) light yellow oil which was approximately 85% pure as analyzed by NMR. The major impurity appeared to be dibutyl thiourea. EXAMPLE 2 Preparation of tetrahydro-5-cyclohexyl-1,3-di-n-butyl-(S) -triazinethione Formalin (40.5g; 37%; 0.50mol) and 1,3-dibutyl thiourea (47.1g; 0.25 mol) were heated together in a 250 mL Erlenmeyer flask at 50-60°C for 1 hour. Cyclohexyl amine (24.8g; 0.25 mol) was added and heating continued overnight. Analysis of the crude product by NMR showed 50% reaction so an additional 30g (0.21 mol) formalin and 18.2g (0.18 mol) cyclohexyl amine was added and heating continued for an additional 6 hours. The reaction product was recovered by separating the aqueous layer, extracting it with two 100 mL portions of 75/25, v/v, ether/hexane solution and washing the combined organic layers with dilute acetic acid, water and saturated NaHCO₃. After drying the organic solution with K₂CO₃, the solvent was removed on the rotary evaporator. NMR analysis indicated a conversion of 75%. This mixture was combined with 10g (0.12 mol) formalin and sufficient isopropanol to yield a homogeneous solution and allowed to sit at room temperature over the weekend. Cyclohexyl amine (7g; 0.07 mol) was added and the mixture refluxed for 7 hours, then the reaction product was recovered as above to yield 75.1g (97% yield) amber oil approximately 95% pure analyzed by NMR. EXAMPLE 3 Preparation of tetrahydro-5-cyclohexyl-1,3-diethyl-(S)-tr iazinethione Formalin (1344g; 37%; 16.4 mol), 1,3-diethyl thiourea (983g; 7.4 mol) and NaOH (3g; 0.075 mol) were combined in a 5L-3-neck flask with 1L isopropanol and allowed to stand overnight. Cyclohexylamine (894g; 9.0 mol) was added with stirring over 3 hours. The reaction was then heated to reflux overnight. An additional 400g (4.9 mol) formalin was added, the mixture heated for 8 hours and 250g (2.5 mol) cyclohexyl amine added. After refluxing overnight, the aqueous layer was drawn off and the isopropanol distilled to a pot temperature of 110°C. The residue was diluted 1:1 v/v, with 50/50, v/v, toluene/hexane solution, extracted with 10% HCl till the wash was acidic, then with water and saturated NaHCO₃ solution. After drying with K₂CO₃ the solution was cooled to collect the product. Additional material was collected by concentration of the mother liquors to give 940g (50% yield) of a white solid, mp. 73-75°C. An additional 410g was recovered from the mother liquors after stripping on a rotary evaporator by continuous extraction with hexane. EXAMPLE 4 Preparation of 1,3-di-(4-anilinophenyl)-triourea Para-aminodiphenylamine (1917g;10.4 mol) was weighed into a 12 L, 3-neck flask and 5 L isopropanol added. Carbon disulfide (476g; 6.25 mol) was added with stirring over the course of 2 hours. The mixture was then heated to reflux for 7 hours, the evolved H₂S being trapped in a NaOH solution. After cooling, the product was filtered off, washed with isopropanol and air dried. Yield 1872g (88%) of a grey solid, mp 164-71°C. EXAMPLE 5 Preparation of tetrahydro-1,3-di-(4-anilinophenyl)-5-butyl-(S)-triazine thione The 1,3-di-(4-anilinophenyl)-thiourea, from Example 4, (41g; 0.10 mol) was dissolved in 100 mL THF and formalin (16.8g; 0.21 mol) added. This mixture was refluxed 0.5 hours after which butyl amine (7.7g; 0.105 mol) made up to 25 mL in THF was added in one portion. Heating was continued for 22 hours after which the reaction was cooled and the crystalline product collected, to yield 29.8g (59%) of white crystals, mp 202.5-204°C. EXAMPLE 6 Preparation of tetrahydro-1,3-di-(4-anilinophenyl)-5-(t)-octyl-(S)-triazine thione The 1,3-di-(4-anilinophenyl)-thiourea, from Example 4, (205g; 0.50 mol), formalin (86g, 37%; 1.05 mol) and t-octyl amine (68g; 0.52 mol) were combined in a 1L-1-neck flask with 300 mL acetonitrile. The mixture was heated at reflux for 10 hours, then the solvent stripped on a rotary evaporator. On mixing the residual oil with toluene, a white solid immediately formed which was filtered off and dried, to yield 253g (90%); mp 154-156°C. The corresponding 5-tallowamine, mp 65-120°C, 5-cocoamine, mp 151-154°C and 5-Jeffamine™ M-360 derivatives were prepared in a similar fashion. The rubbers which can be used in the compositions of this invention are those in the general class of non-halogenated diene polymers, for instance the following: natural rubber, also known as polyisoprene, and synthetic polymers which are polymers prepared from a single monomer (homopolymer) or a mixture of two or more copolymerizable monomers (copolymers) wherein the monomers are combined in a random distribution or block form. Representative of the synthetic polymers are polybutadiene, polyisoprene, polyethylbutadiene, polydimethylbutadiene, polypentadiene, polydicyclopentadiene, polyhexadiene, polypiperylene, polyacrylonitrile, copolymers of diene monomers with olefin, cycloolefin or vinyl monomers such as styrene-butadiene copolymers, styrene-isoprene copolymers, acrylonitrile-butadiene copolymers, ethylene-propylene-diene copolymers, isobutene-isoprene copolymers and the like. When the compounds of the present invention are used in the rubber compositions of this invention either singly or in combinations, the total level to be effective as antiozonants is from 2.5 to 10 parts by weight, preferably 3.0 to 7.0 parts by weight based on 100 parts by weight of the rubber polymer (hereinafter, phr). Greater or lesser amounts can be used, however, depending upon the severity of the conditions to which the rubber composition will be submitted. When the compounds of the present invention are used in rubber compositions to enhance known antiozonants, they can be used at a level of at least 0.1 phr, preferably at least 0.5 phr. It should be readily apparent to those skilled in the art of rubber compounding that some of the compounds used in some of the embodiments of this invention have been used in rubber compositions as vulcanization accelerators, particularly for halogenated dienes such as polychloroprene. It is believed that analogs of the compounds of the present invention having a hydrogen attached to the nitrogen adjacent to the thiocarbonyl group would also function as accelerators and thus destroy functionality as an antiozonant. Furthermore it is believed that the presence of some substituents e.g. a nitrogen atom on a carbon atom alpha to the thiocarbonyl group would decompose at vulcanization temperatures to form a vulcanization accelerator. The following examples are intended to illustrate, not to limit, the practice of the present invention. EXAMPLE 7 Preparation of N-(1,3-dimethylbutyl)-p-phenylenediamine In a 1L, 3-neck flask were combined p-aminoacetanilide (100g;0.67 mol), methyl isobutyl ketone (350g;3.5 mol) and Amberlyst® 15 resin (5g). The flask was heated with stirring overnight, collecting 11mL water (92% of theory) in a Dean-Stark trap. The catalyst resin was filtered off and the excess ketone removed on a rotary evaporator to yield 154g of the intermediate Schiff base. This material was dissolved in 200 mL methanol and transferred to a 600 mL beaker. To it was added a solution of 25g (0.66 mol) of NaBH₄ in 100 mL of 0.5 M aqueous NaOH in small portions. When the addition was complete, the mixture was heated at 50°C for 2 hours. The solution was then cooled, carefully made strongly acidic with 15% HCl and refluxed for 2 hours. After cooling, the solution was made basic with careful addition of solid Na₂CO₃ and extracted with ether. The organic solution was dried with K₂CO₃ and the ether removed on the rotary evaporator to yield 128g (99%) of the desired amine. EXAMPLE 8 Preparation of tetrahydro-1,3-bis-[4-(1,3-dimethyl-butylamino)-phenyl]-5-octyl-(S)- triazinethione A 1L, 3-neck flask was charged with 250g (1.30 mol) of N-(1,3-dimethylbutyl)-p-phenylenediamine and 300 mL of acetonitrile. While stirring, carbon disulfide (53g; 0.70 mol) was added dropwise. When addition was complete, the mixture was heated until H₂S evolution was complete. It was then cooled and formalin (120g; 1.5 mol) and n-octyl amine (86g; 0.66 mol) were added. The mixture was refluxed overnight. The solvent was removed on a rotary evaporator and the residual, syrupy material taken up in methanol. Prolonged cooling in the freezer yielded 112g (30%) of the product, mp 143-6°C. EXAMPLE 9 Tetrahydro-1,3,5-tributyl-(S)-triazine thione (1,3,5 TBTT) and tetrahydro-5-cyclohexyl-1,3-diethyl-(S)-triazine thione (5-Ch-1,3DETT) were each added at 4.0 parts and 6.0 parts per 100 parts, all by weight, (hereinafter, phr) to a 50/50 blend of a natural rubber (NR) and a polybutadiene (PBD) according to the formulation as shown in Table I to prepare a rubber composition according to the present invention for comparison versus a control composition containing no antiozonant (AOZ). Material phr NR-SMR#5 50.00 PBD-BUDENE™ 1207 50.00 Carbon Black 55.00 Oil 10.00 Fillers 7.00 Antioxidant - Wingstay™ 29 2.00 Curatives 3.15 Antiozonant as specified The stocks were cured at 150°C for the times shown in Table II. Stress/strain properties were tested according to ASTM method D-412 on the original samples and on samples which had been exposed to 50 parts per hundred million (pphm), ozone at 40°C for 8h and 24h. Percent tensile retention and percent 100% Modulus retention on the exposed samples were used as a measure of antiozonant effectiveness as shown in Table II. Sample phr Cure Time, Min % Tensile Retention % 100% Modulus Retention 8h 24h 8h 24h No AOZ - 12 55 43 83 72 1,3,5TBTT 4 5 60 64 93 82 1,3,5TBTT 6 5 61 65 95 99 5-Ch-1,3DETT 4 7.5 60 56 95 81 5-Ch-1,3DETT 6 7.5 77 76 106 95 EXAMPLE 10 The same two materials from Example 9 were each added at 3.0 phr and 5.0 phr to a styrene-butadiene copolymer (SBR) composition as shown in Table III. Material phr SBR 1502 100.00 Carbon Black 50.00 Fillers 7.00 Oil 5.00 Antioxidant - Wingstay™ 29 1.00 Curatives 3.00 Antiozonant as specified The stocks were cured at 150°C for the times shown in Table IV. Stress/strain properties were run identically to Example 9. Results are shown in Table IV. Sample phr Cure Time, Min % Tensile Retention % 100% Modulus Retention 8h 24h 8h 24h No AOZ - 20 54 78 96 90 1,3,5TBTT 3 20 98 72 104 102 1,3,5TBTT 5 15 89 92 137 100 5-Ch-1,3DETT 3 17 102 75 97 86 5-Ch-1,3DETT 5 15 86 73 106 113 EXAMPLE 11 Tetrahydro-1,3-bis-[4-(1,3-dimethylbutyl-amino)-phenyl]-5-octyl-(S)-triazine thione (1,3DBA5OTT) and tetrahydro-1,3-di-(4-anilinophenyl)-5-t-octyl-(S)-triazine thione (DAP5OTT) were each added at a level of 3.0 phr to a synthetic polyisoprene (IR) according to the formulation shown in Table V, to prepare a rubber composition of the present invention along with a control stock containing no antiozonant. Material phr IR, NATSYN™ 2200 100.00 HAF Carbon Black 35.00 Oil 5.00 Fillers 5.00 Curatives 3.45 Antiozonant as specified Sheets (2mm thick) from each stock were cured @ 150°C for the times shown in Table VI after which specimens were prepared and used to run the ICI Annulus Ozone Test as described in a Technical Information Bulletin issued 1.3.71 by Application Research and Technical Service Department, Dyestuffs Division, Imperial Chemical Industries Limited, based upon a paper by Amsden, C.S., Transactions of the Institution of the Rubber Industry, Vol. 13, No. 3, June 1966. The results shown in Table VI are the threshold elongations below which cracking did not occur on specimens exposed to 50 pphm ozone at 40°C for the time periods listed in Table VI. Sample Cure Time, Min Threshold Elongation,% at Exposure Time 2h 4h 6h No AOZ 12 20 0 0 1,3DBA5OTT 9 30 30 30 DAP5OTT 10 25 25 25 EXAMPLE 12 Tetrahydro-1,3,5-tributyl-(S)-triazine thione (1,3,5TBTT) and commercially available N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylene diamine (WS300) were each used alone and in various combinations with each other in an SBR formulation as shown in Table VII. Specimens were prepared for the ICI Annulus Ozone Test as described in Example 11. The various levels used and the threshold elongations after 8 hr exposure to 50 pphm ozone are listed in Table VIII. Material ph SBR 1502 100.00 Fillers 72.00 Oil 5.00 Curatives 3.25 Antiozonant as specified WS300,phr 0 1 2 1,3,5TBTT,phr Threshold Elongation, % 0 10 30 35 2 13 25 100 4 17 100 100 The results are an indication of the synergy which occurs between a compound of the present invention and a commercially available para-phenylenediamine antiozonant. EXAMPLE 13 Tetrahydro-1,3,5-tributyl-(S)-triazine thione (1,3,5-TBTT), tetrahydro-5-cyclohexyl-1,3-diethyl-(S)-triazine thione (5-Ch-1,3-DETT), N-N-(oxydiethylene)-phenylethane thioamide (N,N-ODPET) and N,N-(oxydiethylene)-4-methylpentanethioamide (N,N-ODMPT) were added at the level specified to an acrylonitrile-butadiene copolymer (NBR) composition as shown in Table IX. Material phr Chemigum N-615B 100.00 FEF Black 50.00 Curatives 6.90 Antiozonant as specified The stocks were cured at 150°C for the times shown in Table X. Results are shown in Table X. Sample phr Cure Time Min % Tensile Retention % 100% Modulus Retention 8h 24h 8h 24h No AOz - 20 69 57 92 84 1,3,5-TBTT 5.32 23 90 78 112 82 5-Ch-1,3-DETT 5.00 26 83 73 96 91 N,N-ODPET 4.13 16 88 83 103 94 N,N-ODMPT 3.75 22 82 81 102 92 EXAMPLE 14 Tetrahydro-1,3-di-(4-toluidinophenyl)-5-butyl-(S)-triazinethione (1,3DTP5BTT), tetrahydro-1,3-bis-(4-dimethylaminophenyl)-5-butyl-(S)-triazinethione (1,3DMA5BTT), tetrahydro-1,3-bis-(4-(1,3-dimethyl-amino)-phenyl)-5-octyl-(S)-triazinethione (1,3DBA5OTT), tetrahydro-1,3-di-(4-anilinophenyl)-5-tert-octyl-(S)-tria zinethione (1,3DAP5TOTT), and tetrahydro-1,3-bis-(4-diethylaminophenyl)-5-hexadecyl-(S)-triazinethione (1,3DEA5HTT) were added at the level specified to a styrene-butadiene copolymer (SBR) composition as shown in Table XI. Material phr SBR 1502 100.00 Fillers 72.00 Oil 5.00 Curatives 3.25 Antiozonant as specified The stocks were cured at 150°C for the times shown in Table XII. Stress/strain properties were run identically to Example 9. Results are shown in Table XII. Sample phr Cure Time Min % Tensile Retention % 100% Modulus Retention 8h 24h 8h 24h No AOz - 38 44 36 80 68 1,3DTP5BTT 6.0 24 85 61 91 64 1,3DMA5BTT 4.6 18 130 94 90 91 1,3DBA5OTT 3.0 14 - 58 - 92 1,3DAP5TTOT 3.0 14 - 48 - 72 1,3DEA5HTT 3.3 13 - 61 - 91 Industrial Applicability The compounds of the present invention have utility as antiozonants in rubber compositions to protect the compositions from the degradative effects of ozone. The rubber compositions of the present invention have utility in articles such as tires, belts, hoses and other rubber goods particularly where those articles may be exposed to the degradative effects of ozone. A particularly beneficial property is the non-staining characteristic of those rubber compositions containing structures wherein the radicals are selected from groups free of para-phenylenediamine moieties. However, even those compositions containing structures having para-phenylenediamine, while they may not be as non-staining as some of the other embodiments of the invention, are lighter colored than the conventional para-phenylenediamines such as Wingstay™ 300 and may migrate to a much lesser degree. These would have applicability to light colored rubber compositions such as white sidewalls, shoe products, floor mats and the like.

Claims: A rubber composition comprising a non-halogenated rubber susceptible to ozone degradation and a compound characterized by the following structural formula: wherein G is >N-R³; wherein R¹, R² and R³ are independently selected from the group consisting of (a) alkyl radicals having 1 to 25 carbon atoms, wherein said alkyl may be substituted by an amino group, (b) cycloalkyl radicals having 3 to 25 carbon atoms, wherein said cycloalkyl may be substituted by an amino group, (c) aryl radicals having 6 to 25 carbon atoms; and (d) radicals selected from the group consisting of those radicals represented by the following structural formulae: wherein R¹⁷, R¹⁸, R¹⁹ and R²⁰ are independently selected from the group consisting of hydrogen; alkyl radicals having 1 to 25 carbon atoms; and aryl radicals having 6 to 25 carbon atoms; n is an integer of 1 to 6; wherein R³ can also be hydrogen; wherein if the radical from group (a) or (b) is substituted with an amino group, the alpha atom of the radical is free of amino groups. A rubber composition according to claim 1 comprising a non-halogenated rubber and from 2.5 to 10 phr of a compound characterized by formula (I) as defined in claim 1. A composition of matter characterized by the following structural formula: wherein G is >N-R⁴³; wherein R⁴¹, R⁴², R⁴³ are independently selected from the group consisting of (a) alkyl radicals having 1 to 25 carbon atoms, wherein said alkyl may be substituted by an amino group, (b) cycloalkyl radicals having 3 to 25 carbon atoms, wherein said cycloalkyl may be substituted by an amino group, (c) aryl radicals having 6 to 25 carbon atoms, and (d) radicals selected from the group consisting of those radicals represented by the following structural formulae: wherein R⁵⁷, R⁵⁸, R⁵⁹ and R⁶⁰ are independently selected from the group consisting of hydrogen; alkyl radicals having 1 to 25 carbon atoms; and aryl radicals having 6 to 25 carbon atoms; n is an integer of 1 to 6; wherein when a radical from member (a) or (b) is substituted with an amino group, the alpha atom of the radical is free of amino groups; wherein at least one of R⁴¹, R⁴² and R⁴³ is selected from the radicals of member (d); The rubber composition of Claim 1 having therein from 2.5 to 10 phr tetrahydro-5-(t)-butyl-1,3-di-n-butyl-(S)-triazinethione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr tetrahydro-5-cyclohexyl-1,3-di-n-butyl-(S)-triazine thione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr of tetrahydro-5-cyclohexyl-1,3-diethyl-(S)-triazine thione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr of tetrahydro-1,3-di-(4-anilinophenyl)-5-butyl-(S)-triazine thione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr of tetrahydro-1,3-di-(4-anilinophenyl)-5-(t)-octyl-(S)-triazine thione The rubber composition of Claim 1 having therein from 2.5 to 10 phr of 1,3-di-(4-isopropylaminophenyl)-5-butyl-(S)-triazine thione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr of 1,3-di-(4-isopropylaminophenyl)-5-t-octyl-(S)-triazine thione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr of tetrahydro-1,3,5-tributyl-(S)-triazine thione. The rubber composition of Claim 1 having therein from 2.5 to 10 phr of tetrahydro-1,3-bis[4-(1,3-dimethylbutylamino)-phenyl]-5-octyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is tetrahydro-5-(t)-butyl-1,3-di-n-butyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is tetrahydro-5-cyclohexyl-1,3-di-n-butyl-(S)-tetrahydro-5-cyclohexyl-1,3-di-n-butyl-(S)triazine thione. The rubber composition of Claim 2 wherein said compound is tetrahydro-5-cyclohexyl-1,3-diethyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is tetrahydro-1,3-di-(4-anilinophenyl)-5-butyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is tetrahydro-1,3-di-(4-anilinophenyl)-5-t-octyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is 1,3-di-(4-isopropylaminophenyl)-5-butyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is 1,3-di-(4-isopropylaminophenyl)-5-t-octyl-(S)-triazine thione. The rubber composition of Claim 2 wherein said compound is tetrahydro-1,3,5-tributyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-bis-[4-(1,3-dimethylbutyl-amino)-phenyl]-5-octyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-bis-(4-diethylamino-phenyl)-5-butyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-bis-(4-diethylamino-phenyl)-5-t-octyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-di-(4-anilinopheny)-5-hexadecyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-di-(4-anilinophenyl)-5-t-octyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-di-(4-isopropylamino-phenyl)-5-butyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-di-(4-isopropylamino-phenyl)-5-t-octyl-(S)-triazine thione. The composition of matter of Claim 3 wherein said compound is tetrahydro-1,3-bis-[4-(1.3-dimethyl-butylamino)phenyl]-5-octyl-(S)-triazine thione.

Inventors: GILLICK JAMES GREGORY, KUCZKOWSKI JOSEPH ANDREW, ROLLICK KEVIN LOUIS, GILLICK, JAMES GREGORY, KUCZKOWSKI, JOSEPH ANDREW, ROLLICK, KEVIN LOUIS
Applicants: GOODYEAR TIRE & RUBBER, THE GOODYEAR TIRE & RUBBER COMPANY
Application year: 1988
Main classification: C08L21
IPC codes: C08K5, C07D277, C07D251, C07D273, C08L21