Production of multicolor display

Abstract: The first embodiment of the present invention is a process for producing a multicolor display comprising the following steps (a) a transfer panel which has thereon electroconductive layers insulated with each other is immersed in an electrodeposition bath, in which a voltage is applied to one or more of said electroconductive layers to be colored with a same color to form the color layer thereon, (b) said step (a) is repeated with the other colors to form a multicolor layer, and (c) said multicolor layer is transferred onto a transparent substrate. The second embodiment of the present invention is an improved process of the first embodiment, wherein both the multicolor layer and the electroconductive layer are transferred onto the transparent substrate.

Description: Field of the Invention The present invention relates to a multicolor display. More particularly, it relates to a multicolor filter having a multicolor layer formed by electrodeposition. Background of the Invention A multicolor display is employed as a display for a liquid crystal color television and the like. It generally is composed of a transparent substrate and a color layer thereon. Recently, in a process for producing a multicolor display, electrodeposition has become noteworthy. Japanese Kokai Publication JP-A-59 114 572 discloses a process for producing a multicolor display wherein, as shown in Fig. 3, a transparent electrode 2 is patterned on a glass substrate 4 (see Fig.3 (a)) which is then immersed in an electrodeposition bath while a voltage is applied to a portion of the transparent electrode 2 to be colored with, for example, red to form a red color layer 3 (see Fig.3 (b)), then green and blue color layers 3 were formed on each portion of the electrode 2 by passing electricity (see Fig.3 (c) and (d)). In the apparatus produced by the process mentioned above, the transparent electrode is employed not only for electrodepositing a color layer, but also for driving liquid crystal. However, since the color layer electrodeposited on the electrode is insulating, a high driving voltage for liquid crystal is needed. In order to reduce the driving voltage, an additional transparent layer which is for driving liquid crystal is formed on the color layer (see Fig.3 (e)). The formation of the additional electrode is time and cost consuming because it makes the process complicated and requires a further patterning process. Also, since an transparent electrode generally has a light transmittance of 80 to 85 %, two transparent electrodes reduces the light transmittance of the display, thus deteriorating properties of the multicolor display. Another process without using electrodeposition has also been proposed which includes screen printing, photolithography and the like. Screen printing has a limit in miniaturization of pattern and accuracy of printing declines to result in a discrepancy of a pattern. Photolithography makes possible miniaturization of pattern, but protection against dyeing is necessary in order not to carry out double dyeing. It makes the process complicated. Summary of the Invention The present invention provides a process for producing a multicolor filter for a multicolor display comprising the following steps; (a) a transfer panel, which has thereon electroconductive layers insulated with each other, is immersed in an electrodeposition bath, in which a voltage is applied to one or more of said electroconductive layers to be colored with a first same color to form a first color layer on the one or more of said electroconductive layers, (b) said step (a) is repeated with the other colors to form a multicolor layer, (c) a transparent substrate is contacted with said multicolor layer, (d) said multicolor layer is transferred onto said transparent substrate, and (e) a transparent electrode is formed on the multicolor layer. Brief Explanation of the Drawings Fig.1 is a process drawing showing a first embodiment of the process of the present invention. Fig.2 is a process drawing showing a second embodiment of the process of the present invention. Fig.3 is a process drawing indicating the process of Japanese Kokai Publication JP-A-59 114 572. Detailed Description of the Invention An electroconductive layer 2 is formed on a transfer panel 1 which is made from glass or plastics, as shown in Fig.1 (a). The electroconductive layer 2 is formed from an electroconductive metal, such as copper, silver and the like, or a transparent electroconductive material, such as tin oxide, indium and the like. The electroconductive layer 2 is formed by spray coating, sputtering and the like and patterned by chemical etching, dry etching and the like. The patterned electroconductive layer 2 is generally separated to two or more portions, each of which is electrically insulated with others and colored with the same color. On the transfer panel 1 having the patterned electroconductive layer 2, as shown in Fig.1 (b) to (d), a multicolor layer is formed by electrodeposition. For example, assuming that three colors, i.e. red, green and blue are formed, the transfer panel is immersed in a red electrodeposition bath and electrodeposited only in a patterned portion to be colored with red to from a red electrodeposited coating thereon, which is shown in Fig.1 (b). The panel 1 is rinsed and dried, and then electrodeposited with green in a similar manner mentioned above to form a red and green electrodeposited coating, as shown in Fig.1 (c). This is the same in Fig.1 (d). The synthetic polymer resin employed as a film-forming component in the electrodeposition baths mentioned above can be cationic or anionic, including those known to the skilled in the art, for example acrylic resins, epoxy resins, urethane resins, polybutadiene resins, polyamide resins, carboxyl group-containing polybutadienes, carboxyl group-containing alkyd resins and the like. Detailed informations of the electrodeposition bath and the others are described in Japanese Patent Application Ser. No. 46321/1987 to the present inventors and Japanese Kokai Publication 114592/1984. The electrodepositable coating composition can be either heat curable or photocurable. Next, as is shown in Fig.1 (e), a transparent substrate 4 is contacted with the multicolor layer 3 formed on the transfer panel 1 and the multicolor layer 3, as shown in Fig.1 (f), is transferred onto the transparent substrate 4. Consequently, the transfer panel 1 having the patterned electroconductive layer 2 remains, which can be again used for a transfer panel of Fig.1 (a). This is the first embodiment, according to which the transfer panel 1, if patterned, can be repeatedly used to enhance productive efficiency. The transference may be carried out using a rubber coated roller, while the transparent substrate 4 is contacted with the multicolor layer 2. If the electrodepositable coating composition is photocurable, the transfer panel 1 is taken off after it is exposed to ultraviolet light. Generally, cure can be done with 200 mJ/cm² at room temperature in air. If it is required to obtain a high fastness of the multicolor layer, intensity of radiation may increase. Also, if the coating composition is heat curable, cure may be conducted by heating before or after the transfer panel 1 is taken off. A transparent electrode is then formed on the multicolor layer on the transparent substrate 4 by vapor deposition, sputtering and the like to form a multicolor display of the present invention. The second embodiment of the present invention is very similar to the first embodiment mentioned above. The steps shown in Fig.2 (b) to (e) are corresponding to the steps shown in Fig.1 (a) to (d) and therefore an explanation of these steps are omitted. It, however, is required that the electroconductive layer 2 be transparent, i.e. tin oxide, indium and the like, because the electrode 2 is transferred onto the transparent substrate 4 together with the multicolor layer 3. In the step of Fig.2 (a), a release layer 5 may be formed on the transfer panel 1 in order to promote a transferring of both the electroconductive layer 2 and the multicolor layer 3. If transference is smoothly conducted without the release layer 5, it is not necessary. An example of the release layer 5 is a silicone thin film and the like. After the steps of Fig.2 (b) to (e), the multicolor layer 2 and the transparent electroconductive layer 2 are transferred onto the transparent substrate, as shown in Fig.2 (f). The transference can be conducted as mentioned in the first embodiment (Fig.1). After taking off the transfer panel1, as shown in Fig.2 (g), there remain a multicolor display not having an electrode between the multicolor layer 3 and the transparent substrate 4 and the transfer panel. Accordingly, the multicolor display of the second embodiment of the present invention only has one electrode. The remaining transfer panel of the step of Fig.2 (g) can be used in the step Fig.2 (a). Examples The present invention is further illustrated by the following examples which are not to be construed as limiting the present invention to their details. Example 1 An organic polymer binder having a weight average molecular weight of about 70,000 was obtained by reacting N,N-diethylaminoethyl methacrylate, styrene, ethylacrylate and a 1/1 molar ratio reaction product of p-hydroxybenzoic acid and glycidyl acrylate in a molar ratio of 3 : 2 : 4 : 1. A cationic photocurable resin composition was prepared by mixing 80 parts by weight of the organic polymer binder obtained above, 0.5 parts by weight of 2,2-dimethoxy-2-phenyl acetophenone and 14.5 parts by weight of trimethylolpropane triacrylate, which was diluted with ethylene glycol monobutyl ether to a volatile content of 80 %. The obtained solution was neutralized with 0.5 equivalent of acetic acid and adjusted with deionized water to a volatile content of 10 % to form an electrodepositable resin composition. The obtained resin composition was mixed with a pigment in a following formulation to obtain three color cationic electrodeposition baths. (1) Patterning step An indium oxide transparent electroconductive layer was formed on a polyester transfer panel and patterned by etching to a stripe form to form a transparent electrode. (2) Electrodepositing step In the transparent electrode, a portion to be colored with red was selected and connected to a cathode of a power source. The transfer panel was immersed in the red electrodeposition bath mentioned above and a potential difference of 50 V was applied for 2 minutes. The electrodeposited panel was taken out of the electrodeposition bath and rinsed with water, while the electrodeposited resin turns to be water-insoluble so as not to wash out. After rinsing, the panel was dried to form a transparent red polymer film thereon. This process was repeated with blue and green. (3) Transferring step A transparent glass substrate was contacted with the multicolor layer of the transfer panel and the multicolor layer was transferred onto the glass substrate by using a rubber coating roller. The polyester transfer panel was the removed therefrom. (4) Curing step The multicolor layer was cured by exposing to a high pressure mercury lamp to obtain a film thickness of 2.0 micrometer. Example 2 Preparation of a cationic acrylic resin A reaction vessel equipped with a stirrer, a condenser, a dropping funnel and a thermometer was charged with 40 parts by weight of isopropyl alcohol, 2 parts by weight of azobisisobutylonitrile and heated to reflux. On starting reflux, a mixture of 30 parts by weight of glycidyl methacrylate, 5 parts by weight of hydroxyethyl metehacrylate, 30 parts by weight of styrene, 35 parts by weight of 2-ethylhexyl acrylate and 2 parts by weight of azobisisobutylonitrile was added over two hours and allowed to react for three hours under refluxing to obtain a colorless and transparent copolymer solution. Next, 5.3 parts by weight of di-n-propylamine and 84 parts by weight of isopropyl alcohol were added and further reacted for three hours at a refluxing temperature. The obtained resin solution had a nonvolatile content of 65 % and a viscosity of 48 poise at 25 °C. Then, 154 parts by weight of the resin solution was mixed with 27 parts by weight of a 10 % acetic acid solution to obtain a cationic acrylic resin varnish. Preparation of cationic electrodeposition baths Three cationic electrodeposition baths were prepared as follows: (1) Patterning step Patterning process was conducted as generally described in Example 1. (2) Electrodepositing step Electrodeposition was carried out as generally described in Example 1 with the exception that a voltage of 40 V was applied for 3 minutes. (3) Transferring step Transferring process was conducted as generally described in Example 1. (4) Curing step The multicolor layer was cured by heating at 175 °C for 30 minutes to obtain a film thickness of 1.7 micrometer. Example 3 Preparation of an anionic acryl-melamine resin A reaction vessel equipped with a stirrer, a condenser, a dropping funnel and a thermometer was charged with 40 parts by weight of ethylene glycol monomethyl ether and 2 parts by weight of azobisisobutylonitrile and heated to reflux. On starting reflux, a mixture of 25 parts by weight of acrylic acid and 2 parts by weight of azobisisobutylonitrle was added over two hours and then allowed to reflux for two hours to obtain a resin solution having a nonvolatile content of 72 % and a viscosity of 18 poise at 25 °C. Next, 60 parts by weight of the obtained resin solution was mixed with 20 parts by weight of butylized melamine resin and 2 parts by weight of triethylamine to form an anionic acryl-melamine resin varnish. Preparation of anionic electrodeposition baths Three cationic electrodeposition baths were prepared as follows: An anionic electrodeposition process was carried out as generally described in Example 1. The obtained multicolor layer having a thickness of 1.7 micrometer. Example 4 The same process was carried out as generally described in Example 1 with the exception that a transfer panel having a release layer of silicone was employed. Transferring of both the multicolor layer and the electroconductive layer was smoothly carried out and the obtained multicolor layer has a thickness of 1.0 micrometer. Example 5 Three cationic electrodeposition baths were prepared as follows: (1) Patterning step Patterning process was conducted as generally described in Example 4. (2) Electrodepositing step Electrodeposition was carried out as generally described in Example 4 with the exception that a voltage of 40 V was applied for 3 minutes. (3) Transferring step Transferring process was conducted as generally described in Example 4. (4) Curing step The multicolor layer was cured by heating at 175 °C for 30 minutes to obtain a film thickness of 1.7 micrometer. Example 6 An anionic electrodeposition process was carried out as generally described in Example 5 with the exception that an acryl-melamine resin obtained in Example 3 was employed as an anionic electrodeposition resin instead of the cationic acrylic resin of Example 5 to form an aqueous solution having a resin solid content of 8 % by weight. The result was the same as Example 2.

Claims: A process of producing a multicolor filter for a multicolor display comprising the following steps: a) a transfer panel (1), which has thereon electroconductive layers (2) insulated from each other, is immersed in an electrodeposition bath, in which a voltage is applied to one or more of said electroconductive layers to be colored with a first same color to form a first color layer (3) on the one or more of said electroconductive layers, b) said step a) is repeated with the other colors to form a multicolor layer, c) a transparent substrate (4) is contacted with said multicolor layer, d) said multicolor layer is transferred onto said transparent substrate (4), and e) a transparent electrode is formed on the multicolor layer. The process according to Claim 1 wherein a release layer is formed between the transfer panel and the electroconductive layers. The process according to Claim 1 wherein said electroconductive layers are transparent.

Inventors: ISHIKAWA KATSUKIYO - SAYAMAKIT, MATSUMURA AKIRA, NOZAKI YASUO, ISHIKAWA, KATSUKIYO 2-40, SAYAMAKITADAI, MATSUMURA, AKIRA, NOZAKI, YASUO
Applicants: NIPPON PAINT CO LTD, NIPPON PAINT CO., LTD.
Application year: 1988
Main classification: G02F1
IPC codes: G02F1, G09F9, C25D13