Flame retardant electrical insulating composition having antifungal action

Abstract: A flame retardant electrical insulating composition having an antifungal action comprises 100 parts by weight of a polyolefin, 50 - 300 parts by weight of a metal hydroxide, and at least 0.2 parts by weight of an amine compound. Also, a flame retardant electrical insulating composition having an antifungal action comprises 100 parts by weight of an ethylene-vinyl acetate copolymer with a vinyl acetate content of at least 20 wt% or an ethylene-ethyl acrylate copolymer with an ethyl acrylate content of at least 20 wt%, 50 - 300 parts by weight of a metal hydroxide, at least 0.2 parts by weight of an amine compound, and at least 0.5 parts by weight of a hydroxyl group containing lubricant.

Description: The present invention relates to a flame retardant electrical insulating composition that will not evolve toxic gases as it burns. More particularly, the present invention relates to a flame retardant electrical insulating composition that can inhibit the generation of fungi even when it is used as an insulation or sheath material for electric wires or cables. High-rise buildings, power stations, various industrial plants, vehicles and ships are constantly exposed to fire hazards. With respect to the wire harnesses installed in these structures, the need has recently arisen to use electric wires and cables that employ insulation or sheath materials that are highly resistant to flames and which will not evolve halide gases, as they burn, which are harmful to humans and capable of causing corrosion of surrounding instruments. U.S. Patent 4,067,847 describes a flame retardant (self-extinguishing) resin composition prepared by incorporating a metal hydroxide such as magnesium hydroxide, and preferably additional carbon black, into a polyolefin such as polyethylene, polypropylene or a propylene-ethylene copolymer. The metal hydroxide used releases the water of crystallization by heat of combustion, which accelerates the endothermic reaction, to thereby render the resin resistant to flames. By using this flame retardant resin composition as an insulation or sheath material, electric wires or cables having low smoking properties and evolving no toxic gaseous components can be realized. The composition disclosed in US-A-4,067,847 holds much promise for applications where high flame resistance is required. applications where high flame resistance is required. On the other hand, electric wires and cables are often laid in poorly ventilated areas such as cable tunnels or ducts or are buried under the ground . It has recently become apparent that materials containing polyolefins and metal hydroxides as basic components easily suffer from the generation of fungi. The exact mechanism of the generation of fungi has not been fully elucidated but in consideration of the fact that the generation of fungi is negligible when polyolefins are used alone, it can be supposed that the absorption of water or moisture or the surface unevenness caused by the addition of metal hydroxides relates to implantation of fungi. There is another problem that is peculiar to those flame retardant electric wires and cables which are especially intended for use in vehicles and ships. It has recently been required to provide them not only with fungus resistance but also with oil resistance comparable to that of neoprene rubber and chlorosulfonated polyethylene in order to ensure satisfactory field performance. Accordingly, it is the object of the present invention to provide a flame retardant electrical insulating composition which has a superior antifungal action, evolves no harmful halide gases and exhibits high oil resistance. This object of the present invention is attained by a flame retardant electrical insulating composition which comprises 100 parts by weight of an ethylene-vinyl acetate copolymer with a vinyl content of at least 20 wt % or an ethylene-ethyl acrylate copolymer with an ethyl acrylate content of at least 20 wt %, 50 - 300 parts by weight of a metal hydroxide, at least 0.2 parts by weight of an amine compound and at least 0.5 parts by weight of a hydroxyl group containing lubricant. If the content of vinyl acetate or ethyl acrylate in the copolymer is increased, the extruding processability of the resin is greatly reduced on account of sticking during processing such as roll mixing or twin-screw mixing. In order to avoid this problem, a hydroxyl group containing lubricant is used. The metal hydroxides that are suitable for use in the present invention have an average particle size of 0.1 - 30 µm, preferably 0.5 - 15 µm. If a metal hydroxide to be used has been surface-treated with a suitable compound such as a fatty acid, a metal salt of a fatty acid, a silane compound or a titanate compound, it will be dispersed in the copolymer sufficiently uniformly to produce a composition that has an improved processability in such operations as extrusion molding. Specific examples of such metal hydroxides include aluminum hydroxide, magnesium hydroxide, basic magnesium carbonate, calcium hydroxide or hydrotalcite. The amount of the metal hydroxide to be incorporated must be in the range of 50 - 300 parts by weight per 100 parts by weight of the polyolefin. If this amount is less than 50 parts by weight, the desired flame resistance will not be imparted. If this amount exceeds 300 parts by weight, reduction in extruding processability and mechanical strength will result. The amine compound to be used in the present invention is a compound having at least one hydrogen atom in ammonia (NH₃) replaced by a hydrocarbon group R. There are three kinds of amines, i.e. RNH₂, R₂NH and R₃N. The present inventors have confirmed by experimentation that improved antifungal action can be imparted by the addition of this amine compound. Other compounds such as phenolic compounds are little effective in imparting the desired antifungal action. Specific examples of the amine compound that can be used in the present invention include: phenyl-β-naphthylamine; bis(phenyl-isopropylidene)-4,4' - diphenylamine; N,N'-diphenyl-p-phenylenediamine; N-isopropyl-N'-phenyl-p-phenylenediamine; a polymer of 2,2,4-trimethyl-1,2-dihydroquinoline; 2,5-di-tert-butylhydroquinone; 2-mercaptobenzimidazole; and 2 - mercaptomethyl-benzimidazole. The amount of the amine compound to be incorporated must be at least 0.2 parts by weight per 100 parts by weight of the polyolefin. If this amount is less than 0.2 parts by weight, the desired antifungal action will not be attained. While there is no particular upper limit for this content, about 20 parts by weight can be given as a guide figure. In addition to the essential ingredients described above, the composition of the present invention may optionally contain carbon black, antioxidants, softening agents, dispersants and lubricants other than the hydroxyl group containing lubricant. Carbon black has the ability to provide further improved flame resistance by accelerating carbonization during combustion. Carbon black is preferably added in an amount of at least 0.5 parts by weight per 100 parts by weight of the polyolefin. As already mentioned, a hydroxyl group containing lubricant is contained in the composition of the invention. Specific examples of such hydroxyl group containing lubricants are hydroxyl group containing fatty acids or metal salts thereof typified by such compounds as hydroxystearic acid, ricinoleic acid, abarium hydroxystearate, calcium hydroxystearate, calcium hydroxylaurate, lithium hydroxystearate, barium ricinoleate and calcium ricinoleate. The hydroxyl group containing lubricant is added in an amount of at least 0.5 parts by weight per 100 parts by weight of the copolymer. The resin composition of the present invention may or may not be crosslinked. If it is crosslinked, organic peroxides typified by dicumyl peroxide and 3- bis(tert-butylperoxyisopropyl)benzene can advantageously be used as curing agents. Such curing agents may be used in combination with curing assistants such as sulfur, ethylene dimethacrylate, diallyl phthalate and p-quinone dioxime. Crosslinking of the composition can also be accomplished by irradiation with electron beams and, in such cases, reactive monomers such as trimethylol propane trimellitate and triallyl isocyanurate are generally added as curing assistants. The following examples are provided for the purpose of further illustrating the present invention EXAMPLES 1-4, COMPARATIVE EXAMPLE 1 AND REFERENCE EXAMPLES 1 AND 2 The ingredients listed in the recipes shown under Examples 1-4, Comparative Example 1 and Reference Examples 1 and 2 were kneaded with 15.24 cm (6-in) rolls at 100°C, to thereby prepare compounds. Polyethylene was extrusion-coated in a thickness of 1 mm over copper wires (o.d., 3 mm) and crosslinked to form insulated conductors. Three of such insulated conductors were stranded together into a core, which was extrusion-coated with each of the compounds in a thickness of 2 mm using a 40-mm extruder ( L/D = 25 ). The compound coatings were crosslinked by holding them in steam (1471kPa (15 kg/cm²)) for 3 minutes, to produce electric cables. In another run, the compounds prepared from the components shown under Examples 1 - 4, Comparative Example 1, and Reference Examples 1 and 2 were, after preforming at 100°C, press-cured at 180°C for 10 minutes, to form sheets. The results of evaluations conducted on the respective samples for their roll processability, flame resistance, tensile characteristics, oil resistance and antifungal action are summarized in Table 1. The criteria for the evaluations were as follows. Roll processability: The rolled compound was cut twice, that is, 3 and 5 minutes after the start of roll-mixing, to check for the occurrence of sticking to the rolls. Flame resistance: Eight electric cables arranged vertically were subjected to a tray flame test described in IEEE Standard 383 and those which did not burn out entirely were rated "acceptable". Tensile characteristics: The core was drawn out of each electric cable, and the remaining coat was abraded to a thickness of 1 mm, died out with JIS dumbbell No. 3, left to stand in a thermostatic room for 1 day at 20°C, and then subjected to a tensile test by stretching it at a speed of 500 mm/min with a Schopper tensile tester. Oil resistance: The core was drawn out of each electric cable, and the remaining coat was immersed in an insulating oil (ASTM #2 oil) far 18 hours at 120°C in accordance with the standards of chloroprene rubber for electric appliances, removed from the oil, left to stand in a thermostatic room for 1 day at 20°C, and then subjected to a tensile test. Fungus resistance: A sheet was cut into a square test piece (50 x 50 mm) and fungi were cultivated for 2 weeks on this test piece in accordance with a wet method of JIS Z 2911 for textiles. The results of observation of the growth of fungi were evaluated by the following criteria: (A), no growth of fungi; (B), the growth of fungi covered no more than a third of the area of the test piece; and (C), the growth of fungi covered more than a third of the area of the test piece. EXAMPLE 1 Ethylene-vinyl acetate copolymer (vinyl acetate content, 40 wt%; melt index = 2.0 at 190°C) 100 parts by weight Magnesium hydroxide (treated with oleic acid; average particle size, 1 µm) 100 parts by weight Dicumyl peroxide 3 parts by weight 2-Mercaptobenzimidazole 2 parts by weight FEF Carbon black 5 parts by weight Hydroxystearic acid 1 part by weight COMPARATIVE EXAMPLE 1 Ethylene-vinyl acetate copolymer (vinyl acetate content, 40 wt%; melt index = 2.0 at 190°C) 100 parts by weight Magnesium hydroxide (treated with oleic acid; average particle size, 1 µm) 100 parts by weight Dicumyl peroxide 3 parts by weight 4,4'-Thio-bis(6-tert-butyl-4-methylphenol) 2 parts by weight FEF Carbon black 5 parts by weight Hydroxystearic acid 1 part by weight REFERENCE EXAMPLE 1 Ethylene-vinyl acetate copolymer (vinyl acetate content, 15 wt%; melt index = 0.8 at 190°C) 100 parts by weight Magnesium hydroxide (treated with oleic acid; average particle size, 1 µm) 100 parts by weight Dicumyl peroxide 3 parts by weight 2-Mercaptobenzimidazole 2 parts by weight FEF Carbon black 5 parts by weight Hydroxystearic acid 1 part by weight REFERENCE EXAMPLE 2 Ethylene-vinyl acetate copolymer (vinyl acetate content, 40 wt%; melt index = 2.0 at 190°C) 100 parts by weight Magnesium hydroxide (treated with oleic acid; average particle size, 1 µm) 100 parts by weight Dicumyl peroxide 3 parts by weight 2-Mercaptobenzimidazole 2 parts by weight FEF Carbon black 5 parts by weight Stearic acid 2 parts by weight EXAMPLE 2 Ethylene-vinyl acetate copolymer (vinyl acetate content, 45 wt%; melt index = 2.0 at 190°C) 100 parts by weight Aluminum hydroxide (treated with stearic acid; average particle size, 1 µm) 150 parts by weight Dicumyl peroxide 3 parts by weight 2-Mercaptobenzimidazole 2 parts by weight FEF Carbon black 5 parts by weight Calcium hydroxystearate 2 parts by weight EXAMPLE 3 Ethylene-ethyl acrylate copolymer (ethyl acrylate content, 25 wt%; melt index = 5.0 at 190°C) 100 parts by weight Magnesium hydroxide (treated with oleic acid; average particle size, 1 µm) 110 parts by weight Dicumyl peroxide 3 parts by weight 2-Mercaptobenzimidazole 2 parts by weight FEF Carbon black 5 parts by weight Lithium hydroxystearate 3 parts by weight EXAMPLE 4 Ethylene-ethyl acrylate copolymer (ethyl acrylate content, 30 wt%; melt index = 5.0 at 190°C) 100 parts by weight Magnesium hydroxide (treated with oleic acid; average particle size, 1 µm) 120 parts by weight Dicumyl peroxide 3 parts by weight 2-Mercaptobenzimidazole 2 parts by weight FEF Carbon black 10 parts by weight Calcium hydroxystearate 2 parts by weight The samples prepared in Examples 1 - 4 according to the present invention were satisfactory with respect to roll processability, tensile characteristics, oil resistance, flame resistance and antifungal action. The sample prepared in Comparative Example 1 employed a phenolic compound instead of an amine compound and was unable to inhibit the growth of fungi. The sample prepared in Reference Example 1 employed an ethylene-vinyl acetate copolymer with a vinyl acetate content of no more than 20 wt%; the oil resistance of this sample was apparently low. The sample prepared in Reference Example 2 used a lubricant containing no hydroxyl group and was poor in roll processability.

Claims: A flame retardant electrical insulating composition having an antifungal action, which comprises 100 parts by weight of an ethylene-vinyl acetate copolymer with a vinyl acetate content of at least 20 wt% or an ethylene-ethyl acrylate copolymer with an ethyl acrylate content of at least 20 wt%, 50 - 300 parts by weight of a metal hydroxide, at least 0.2 parts by weight of an amine compound and at least 0.5 parts by weight of a hydroxyl group containing lubricant. The flame retardant electrical insulating composition of claim 1, wherein the hydroxyl group containing lubricant is hydroxystearic acid. The flame retardant electrical insulating composition of claim 1, wherein the hydroxyl group containing lubricant is calcium hydroxystearate. The flame retardant electrical insulating composition of claim 1, wherein the hydroxyl group containing lubricant is lithium hydroxystearate. The flame retardant electrical insulating composition of claim 1 which further contains at least 0.5 parts by weight of carbon black. The flame retardant electrical insulating composition of claim 1, wherein the metal hydroxide is aluminum hydroxide. The flame retardant electrical insulating composition of claim 1, wherein the metal hydroxide is magnesium hydroxide. The flame retardant electrical insulating composition of claim 1, wherein the amine compound is N,N-'diphenyl-p-phenylenediamine. The flame retardant electrical insulating composition of claim 1, wherein the amine compound is a polymer of 2,2,4-trimethyl-1,2-dihydroquinoline. The flame retardant electrical insulating composition of claim 1, wherein the amine compound is 2-mercaptobenzimidazole. The flame retardant electrical insulating composition of claim 1, wherein the amine compound is 2,5-di-tert-butylhydroquinone.

Inventors: HORI AKIHIRO, SORIMACHI MASAMI, TSUKADA HIROAKI, YAMAMOTO YASUAKI, HORI, AKIHIRO, SORIMACHI, MASAMI, TSUKADA,HIROAKI, YAMAMOTO, YASUAKI
Applicants: HITACHI CABLE, HITACHI CABLE, LTD.
Application year: 1988
Main classification: C08L23
IPC codes: C08K5, C08K3, H01B3