Novel piperidyl-triazine derivatives and their use as polymer stabilizers

Abstract: New compounds of formula (I): [in which: R¹ is hydrogen, alkyl, alkoxyalkyl, carboxylic acyl or phenylalkyl, or an optionally substituted tetramethylpiperidyl group; R² is hydrogen, alkyl, carboxylic acyl or phenylalkyl group; R³ is alkylene optionally interrupted by at least one oxygen atom; X is oxygen or -NR⁵- (in which R⁵ is hydrogen or alkyl); Y is -OCO-, -COO-, -CONH- or -OCONH-; n is 2 to 4; and, when n is 2, Z is alkylene optionally interrupted by at least one oxygen, sulfur or aryl, cycloalkyl or heterocyclic group, or, when n is 3, Z is alkanetriyl in which a carbon is optionally replaced by nitrogen or, when n is 4, Z is alkanetetrayl optionally interrupted by at least one oxygen atom] and acid addition salts thereof are valuable polymer stabilizers. The compounds may be prepared by reacting an active compound corresponding to the portion of the compound of formula (I) shown above in brackets.

Description: The present invention relates to novel piperidyl-triazine derivatives which are useful as stabilizers for synthetic polymers. In recent years, a number of triazine derivatives have been proposed for use as polymer stabilizers, for example as disclosed in U.S. Patent specifications No. 4 108 829, No. 4 433 145, No. 4 400 505 and No. 4 461 861 and in Japanese Patent Application Kokai (i.e. as laid open to public inspection) No. 176 662/86. Of these, the closest prior art is believed to be Japanese Application Kokai No. 176 662/86, which discloses, inter alia , the compound 1,3-bis〈3-{2,4-bis[ N -butyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-ylamino}propoxy〉-2,2-dimethylpropane and proposes its use as a polymer stabilizer. In broad, general terms, the chemical structure of these prior art compounds, including that one specifically mentioned above, insofar as they are relevant to the compounds of the present invention, may be described as having a piperidylaminotriazinyl group attached via , for example, an amino group to an alkylene group, which itself may optionally be interrupted by certain specific atoms or groups. In the case of the prior art compounds, the alkylene group is interrupted by certain specific atoms or groups, such as an oxygen or sulphur atom or an amino group. We have now surprisingly discovered piperidyl-triazine derivatives in which the alkylene group is interrupted by a group of formula -COO-, which is unusual in this type of compound. These compounds have a very low volatility, and indeed, do not even volatilize to any great extent when the polymer containing them is heated. Moreover, they result in little blooming and additionally are excellent polymer stabilizers against heat and light. The only compounds of this type that we have been able to discover having an alkylene group interrupted by groups similar to those in the present invention are disclosed in Japanese Patent Application Kokai No. 63570/87 and in United Kingdom Patent No. 2 136 805. Although these prior compounds are disclosed for use as polymer stabilizers, they differ from the compounds of the present invention in that they have a piperidylamino group attached directly to the alkylene group and lack the triazine group of the present invention. The compounds of the present invention have been found to be significantly more effective polymer stabilizers than these prior compounds. EP 61659 also discloses compounds which have a piperidyl-triazine structure. These compounds have an alkylene group which is interrupted by a group of formula -OCO- or -OCONH-, and are useful as plastics stabilisers. The novel piperidyl-triazine derivatives of the present invention can be represented by the following formula (I): in which: R¹ represents a methyl group or an ethyl group; and Z represents a -(CH₂)₆- group or a -CH₂-CH₂-O-CH₂-CH₂- group; and acid addition salts therof. The invention further provides a polymer, preferably a synthetic polymer, composition comprising a polymer stabilized against the effects of light and heat by the incorporation of a polymer stabilizer, in which the polymer stabilizer comprises at least one compound of formula (I) and/or acid addition salts thereof. The invention also provides processes for preparing the compounds of the present invention, which processes are described in more detail hereafter. The compounds of the present invention have several basic nitrogen atoms in their molecular structure and can thus form acid addition salts, which are also included within the scope of this invention. There is no particular restriction on the nature of the acid used to form such acid addition salts provided that it does not inhibit stabilization of the high polymer or does not do so to an unacceptable degree. Examples of such acids include: inorganic acids, such as sulphuric acid, hydrochloric acid or phosphoric acid; carboxylic acids such as formic acid, acetic acid, valeric acid, stearic acid, oxalic acid, adipic acid, sebacic acid, maleic acid, benzoic acid, p -t-butylbenzoic acid, 3,5-di-t- butyl-4-hydroxybenzoic acid, salicylic acid or terephthalic acid; sulphonic acids such as methanesulphonic acid or benzenesulphonic acid; and phosphonic acids such as phenylphosphonic acid. The following two compounds are the most preferred: 105. Hexane-1,6-diol bis( N -(2,4-bis[ N -methyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)glycinate}; and 114. Diethylene glycol bis{ N -(2,4-bis[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)glycinate}; and acid addition salts thereof. In general terms, the compounds of the present invention can be prepared by reacting a compound of formula (VIII): in which: R¹ is as defined above; and R⁷ represents a C₁ - C₄ alkyl group; with a compound of formula (X): (Y'')₂-Z (X) (in which: Y'' represents a hydroxy group; and Z is defined above; and, if required, converting the resulting compound to an acid addition salt thereof or converting a salt to the free base. In more detail, the compounds of the present invention can be prepared by the sequence of reactions shown in Reaction Scheme A: In the formulae shown above, R¹, R⁷, Y'' and Z are as defined above; and Q represents a halogen atom, such as a chlorine, bromine or iodine atom, preferably a chlorine atom. In Step A1 of Method A a compound of formula (XIII) is prepared by reacting a compound of formula (XI) with a compound of formula (XII) under catalytic reduction conditions. There is no particular restriction on the nature of the catalyst to be employed in the reaction, and any catalyst capable of being used in conventional catalytic reduction reactions can equally be used here. Preferred examples of such catalysts include palladium-on-carbon, palladium black, platinum oxide and Raney nickel, of which platinum oxide is particularly preferred. The reaction is preferably effected in the presence of a solvent, the nature of which is not critical to the reaction, provided that it does not interfere with the reaction. Examples of suitable solvents include water or an alcohol, such as methanol, ethanol or propanol. The reaction is effected in an atmosphere of hydrogen, and the hydrogen pressure to be used in the reaction is usually at least atmospheric pressure, e.g. from atmospheric pressure to 10 atmospheres. The reaction may be carried out over a wide range of temperatures, and the precise temperature chosen is not particularly critical to the reaction. In general, we prefer that the reaction should be carried out at a temperature in the range of from room temperature to 100°C. The time required for the reaction may vary widely, depending on the nature of the starting materials and the catalyst as well as upon the reaction temperature, but a period of from 30 minutes to 5 hours will usually suffice. The compound of formula (XII) can be used in the form of a salt, and there is no substantial restriction on the nature of the salt to be employed. Examples of such salts include: salts with mineral acids, such as hydrochloric acid, nitric acid or sulphuric acid; salts with carboxylic acids, such as acetic acid, trifluoroacetic acid, adipic acid or benzoic acid; salts with sulphonic acids, such as methanesulphonic acid or p -toluenesulphonic acid; and salts with phosphonic acids, such as phenylphosphonic acid. In Step A2 and Step A3 of Method A, compounds of formulae (XV) and (VIII) are prepared, respectively, by reacting the compound of formula (XIII) with the compound of formula (XIV), and by reacting the compound of formula (XV) with the compound of formula (XVI). These reactions are preferably conducted sequentially and take place under essentially the same conditions. If desired, they may be carried out without intermediate isolation of the compound of formula (XV). A compound of formula (XV) in which each group represented by R¹ in the two piperidyl groups is different can be prepared by reacting the compound of formula (XIV) first with about an equimolar amount of a first compound of formula (XIII), and then with about an equimolar amount of another compound of formula (XIII). The reactions are preferably carried out in the presence of a solvent, the nature of which is not critical, provided that it does not interfere with the reactions. Examples of suitable solvents include: water; ketones, such as acetone or methyl ethyl ketone; ethers, such as diethyl ether, tetrahydrofuran or dioxane; aromatic hydrocarbons, such as benzene, toluene or xylene; saturated hydrocarbons, such as heptane, octane, isooctane, cyclohexane or ethylcyclohexane; and mixtures of any one or more of the above organic solvents with water. We particularly prefer to use a mixture of water and acetone. The reactions may be carried out over a wide range of temperatures, and the precise temperature chosen is not particularly critical to the reactions. In general, we prefer that the reactions should be carried out at a temperature in the range of from 0 to 200°C, more preferably from room temperature to 150°C. The time required for the reactions may vary widely, depending on the nature of the starting materials as well as upon the reaction temperature, but a period of from 30 minutes to 30 hours will usually suffice for each of the reactions. The reactions are preferably effected in the presence of an acid binding agent. Any compound capable of binding to the hydrohalic acid HQ produced in the reaction and effectively removing the acid from participation in the reaction may be employed, provided that it does not otherwise interfere with the reaction. Examples of such acid binding agents include: inorganic bases, especially alkali metal hydroxides and carbonates, such as sodium hydroxide, potassium hydroxide, sodium carbonate or potassium carbonate; and organic bases, such as triethylamine, pyridine, N , N -dimethylaniline or 1,8-diazabicyclo[4.3.0]undeca-7-ene (DBU). Of these, we prefer sodium hydroxide, potassium hydroxide, sodium carbonate or potassium carbonate. In Step A4 of Method A, a compound of formula (I) is prepared by reacting a compound of formula (VIII) with a compound of formula (X) in a suitable ratio in an inert solvent. The reaction is preferably conducted in an inert solvent and in the presence of a base. Although the reaction temperature is not critical and the reaction will take place over a wide range of temperatures, we normally prefer to carry out the reaction at an elevated temperature, usually at a reaction temperature of from 80 to 150°C. The time required for the reaction may vary widely, depending on the nature of the starting materials as well as upon the reaction temperature, but a period of from 30 minutes to 5 hours will usually suffice. In general, we prefer that the reaction should be carried out whilst distilling off the lower alcohol formed in the course of the reaction. A compound of formula (I) in which each group of formula: is different can be prepared by reacting the compound of formula (X) stepwise first with about an equimolar amount of a first compound of formula (VIII), then with about an equimolar amount of a second compound of formula (VIII), and so on. There is no particular restriction on the nature of the base to be employed, provided that it has no adverse effect on the reaction or on the reagents. Examples of suitable bases include: alkali metal compounds, especially alkoxides, hydroxides and amides, such as sodium methoxide, sodium ethoxide, potassium t-butoxide, sodium hydroxide, potassium hydroxide or lithium amide; and titanate compounds, such as tetraisopropyl or tetrabutyl titanate. Of these, we prefer sodium ethoxide, potassium hydroxide and the titanate compounds. The nature of the solvent employed is not critical, provided that it does not interfere with the reaction. Examples of suitable solvents include: hydrocarbons, which may be aliphatic, aromatic or alicyclic, such as benzene, toluene, xylene, heptane, octane, isooctane, cyclohexane or ethylcyclohexane. After completion of the reaction, the desired product in each step can be collected from the reaction mixture by conventional means. For example, the desired product can be obtained by the following procedures: when insolubles are present in the reaction mixture, filtering off such insolubles; or, when the reaction mixture is acidic or basic, neutralizing the reaction mixture; adding water thereto; extracting the resulting mixture with a water-immiscible organic solvent; drying the extract thus obtained; and then distilling the solvent from the extract. The desired compound thus obtained may be further purified, if necessary, by means of such conventional means as the various chromatography techniques, e.g. column chromatography or preparative thin layer chromatography, or other means, such as distillation or recrystallisation. An alternative method of preparing the compound of formula (VIII), which may then be used to prepare the compounds of the present invention, is illustrated in Reaction Scheme B: In the above formulae, Q, R¹ and R⁷ are as defined above. In Step B1, the compound of formula (XVII) is prepared by reacting the compound of formula (XIV) with the compound of formula (XVI). In Step B2 the compound of formula (VIII) is prepared by reacting the compound of formula (XVII) with the compound of formula (XIII). These steps are equivalent to Steps A2 and A3 of Reaction Scheme A, and may be effected using the same reaction conditions. The piperidyl-triazine derivatives and acid addition salts thereof of the present invention have excellent compatibility with polymers, less volatility or blooming liability than many conventional polymer stabilizers, as well as excellent light and heat stabilizing ability. Accordingly they can be employed for stabilizing a wide variety of synthetic high polymer compounds. Examples of synthetic high polymer compounds which can be stabilized by the compounds of the present invention include: Olefin and Diene polymers Homopolymers of olefins or dienes, for example, polyethylene (which can be low density, linear-chain low density, high density or crosslinked), polypropylene, polyisobutylene, polybutene-1, polymethylbutene-1, polymethylpentene-1, polyisoprene or polybutadiene. Mixtures of two or more of the homopolymers mentioned above, for example, mixtures of polypropylene with polyethylene, with polybutene-1 or with polyisobutylene. Copolymers of olefins with other olefins and/or with dienes, for example, ethylene/propylene copolymers, propylene/butene-1 copolymers, propylene/isobutene copolymers, ethylene/butene-1 copolymers, and also terpolymers of ethylene with propylene and a diene (e.g. hexadiene, dicyclopentadiene or ethylidenenorbornene). Styrene polymers Polystyrene, and copolymers of styrene or α-methylstyrene with other ethylenically unsaturated compounds [for example, styrene-maleic anhydride copolymer, styrene-butadiene copolymer, styrene-acrylonitrile copolymer, styreneacrylonitrile-methyl methacrylate copolymer, styrene-acrylonitrile-acrylate copolymers, styrene-acrylonitrile copolymer modified with an acrylate polymer in order to give a high impact strength or styrene polymer modified with an EPDM (ethylene-propylene-diene polymer) in order to give a high impact strength]. Graft copolymers of styrene, for example, styrene on polybutadiene, styrene and acrylonitrile on polybutadiene and mixtures thereof with the above copolymers, such as those known as acrylonitrile-butadiene-styrene or ABS polymers. Halogen-containing polymers Especially vinyl and vinylidene polymers, such as polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polychloroprene, chlorinated rubbers, chlorinated vinyl-vinylidene chloride copolymer, chlorinated polyethylene, vinyl chloride-vinylidene chloride copolymer, vinyl chloride-ethylene copolymer, vinyl chloride-vinyl acetate copolymer and vinylidene chloride-vinyl acetate copolymer. Polymers which are derived from α,β-unsaturated acids and their derivatives Polyacrylates, polymethacrylates, polyacrylamides and polyacrylonitrile. Polymers which are derived from unsaturated alcohols and amines or their acyl derivatives or acetals Polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate, polyallyl melamine and copolymers of the monomers forming these polymers with other vinyl compounds, such as ethylene-vinyl acetate copolymers. Epoxy polymers Homopolymers and copolymers of epoxides, such as polyethylene oxide and their copolymers with bis-glycidyl ethers. Polyacetals, polyalkylene oxides and polyphenylene oxides Polyoxymethylene, oxymethylene-ethylene oxide copolymer, polyoxyethylene, polypropylene oxide, polyisobutylene oxide and polyphenylene oxide. Polyurethanes and polyureas Polycarbonates Polysulphones Polyamides and copolyamides Polyamides and copolyamides which are derived from diamines and aliphatic or aromatic dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, such as Nylon 6, Nylon 6/6, Nylon 6/10, Nylon 11 and Nylon 12. Polyesters Polyesters which are derived from dicarboxylic acids and dialcohols and/or from hydroxycarboxylic acids or the corresponding lactones, such as polyethylene terephthalate, polybutylene terephthalate and polycyclohexane-1,4-dimethyleneterephthalate. Crosslinked polymers Crosslinked polymers which are derived from (a) an aldehyde and from (b) a phenol, urea or melamine, such as phenol-formaldehyde resins, urea-formaldehyde resins and melamine-formaldehyde resins, and diallylphthalate resins. Alkyd resins Glycerol/phthalic acid resins and their mixtures with melamine-formaldehyde resins. Unsaturated polyester resins Derived from copolymers of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and a vinyl compound as the crosslinking agent and also halogenated products thereof modified to have flame retardancy. The amount of the compound of the invention employed as a stabilizer will depend upon various factors, for example the nature and properties of the polymer, the intended use of the polymer composition and whether or not there are any other stabilizers present. In general, however, the stabilizers of the present invention will be added to the polymers in an amount of from 0.01 to 5% by weight, based on the weight of the polymer. However, the most effective amount of stabilizer depends upon the nature of the polymer and specifically: For olefin, diene and styrene polymers, we prefer to use from 0.01 to 2.0% by weight of stabilizer, based on the polymer, more preferably from 0.02 to 1.0% by weight. For polymers derived from vinyl chloride or vinylidene chloride, we prefer to use from 0.01 to 1.0% by weight of stabilizer, based on the weight of the polymer, more preferably from 0.02 to 0.5% by weight. For polyurethanes and polyamides, we prefer to use from 0.01 to 5.0% by weight of stabilizer, based on the weight of polymer, more preferably from 0.02 to 2.0% by weight. If desired, two or more of the compounds of the invention may be used together as stabilizers and, if desired, other stabilizers may be used in combination with one or more of the stabilizers of the invention. The stabilizers of the invention can easily be mixed, employing conventional techniques, into the polymer or prepolymer at any suitable stage prior to preparation of shaped articles or other products from the polymer compositions. For example, the stabilizers may be mixed into the polymer in the molten condition or as dry pulverized materials or a suspension or emulsion of the stabilizer or stabilizers may be mixed with a solution, suspension or emulsion of the polymer. It is possible to incorporate other additives commonly employed in polymer technology into the stabilized polymer compositions of the invention. Examples of such additives include: Phenolic antioxidants: 2,6-di-t-butyl- p -cresol; stearyl 3-(4-hydroxy-3,5-di-t-butylphenyl)propionate; distearyl (4-hydroxy-3-methyl-5-t-butylbenzyl)malonate; 2,2'-methylenebis(4-methyl-6-t-butylphenol); 4,4'-methylenebis(2,6-di-t-butylphenol); 2,2'-methylenebis[6-(1-methylcyclohexyl)- p -cresol]; bis[3,3-bis(4-hydroxy-3-t-butylphenyl)butyric acid]glycol ester; 4,4'-butylidenebis(6-t-butyl- m -cresol); 1,1,3-tris(2-methyl-4-hydroxy-5-t-butyl-phenyl)butane; 1,3,5-tris(3,5-di-t-butyl-4-hydroxy-benzyl)-2,4,6-trimethylbenzene; 3,9-bis[1,1-dimethyl-2-(3,5-di-t-butyl-4-hydroxyphenyl)ethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane; tetrakis[methylene-3-(3,5-di-t-butyl-4-hydroxyphenyl)-propionate]methane; 1,3,5-tris(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate and 1,3,5-tris[3,5-di-t-butyl-4-hydroxyphenyl)propionyloxyethyl]-isocyanurate; bis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyl]oxamide. Phosphite series stabilizers: tris(2,4-di-t-butylphenyl) phosphite, triphenyl phosphite; tris(nonylphenyl) phosphite; distearylpentaerythritol diphosphite; 4,4-butylidenebis(3-methyl-6-t-butylphenyl-di-tridecyl) phosphite; bis(2,4-di-t-butylphenyl)-pentaerythritol diphosphite. Ultraviolet absorbers: 2-hydroxy-4-methoxybenzophenone; 2-hydroxy-4-octoxybenzophenone; 2,4-dihydroxybenzophenone; 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole; 2-(2'hydroxy-3',5'-di-t-butylphenyl)-5-chlorobenzotriazole; 2-(2'-hydroxy-5'-methylphenyl)benzotriazole; 2-(2'hydroxy-3',5'-di-t-amylphenyl)benzotriazole; phenyl salicylate; 2,4-di-t-butylphenyl-3,5-di-t-butyl-4-hydroxybenzoate. Nickel series stabilizers: Ni-monoethyl-3,5-di-t-butyl-4-hydroxybenzylphosphonate; butylamine-Ni-2,2'-thiobis(4-t-octylphenolate) complex; Ni-dibutyl-dithiocarbamate; Ni-3,5-di-t-butyl-4-hydroxybenzoate, Metal salts of higher fatty acids: calcium, magnesium, barium, zinc, cadmium, lead or nickel stearate, and calcium, magnesium, cadmium, barium or zinc laurate. In addition to the above additives, heavy metal deactivators, nucleating agents, organic tin compounds, plasticizers, epoxy compounds, pigments, fillers, foaming agents, antistatic agents, lubricants, processing aids, etc. can also be used. Polymers stabilized in this way can be employed in very many different forms, for example as films, fibers, tapes, compression-molding compositions, coating compositions or paints. The invention is further illustrated by the following Preparations and Examples, in which all parts and percentages are by weight, unless otherwise specified. EXAMPLE 1 (A Reference Example) Bis {2-(2,4-bis[N-ethyl-N-(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)oxyethyl} succinate 1.60 g of 2,4-bis-[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-6-(2-hydroxyethoxy)-1,3,5-triazine [prepared as described in Preparation 3(B)] and 0.22 g of dimethyl succinate were dissolved in 20 ml of toluene, and a catalytic amount of tetraisopropyl titanate was added to the resulting solution. The resulting mixture was first agitated at 100 to 105°C for 3 hours whilst the methanol generated was removed by distillation, and then the temperature was elevated to 130°C to remove the toluene. When this removal was complete, a mixture of ethyl acetate and water was added to the residue, and then the mixture was shaken. The ethyl acetate layer was then separated, dried and concentrated by evaporation under reduced pressure, and the resulting residue was purified by silica gel column chromatography (using a 10 : 3 : 1 by volume mixture of diethyl ether, ethanol and triethylamine as eluent), to obtain 920 mg of the title compound as crystals melting at 85°C. EXAMPLES 2 AND 3 The procedure described in Example 1 was repeated but replacing the 2,4-bis-[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-6-(2-hydroxyethylamino)-1,3,5-triazine and dimethyl succinate by other appropriate starting materials, to obtain the following compounds: Example 2 Diethylene glycol bis{ N -(2,4-bis[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)-glycinate} (Compound No. 114), melting at 113°C Example 3 Hexane-1,6-diol bis{ N -(2,4-bis[ N -methyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)-glycinate} (Compound No. 105), melting at 175 to 177°C PREPARATION 1 1(A) 2,2,6,6-Tetramethyl-4-butylaminopiperidine 155 g of 2,2,6,6-tetramethyl-4-piperidone and 80.0 g of butylamine were dissolved in 300 ml of methanol, and then 2.0 g of platinum oxide were added to the resulting solution, after which the solution was shaken under a pressure of 3 atmospheres of hydrogen in a medium-pressure hydrogenation apparatus at room temperature for 5 hours. At the end of this time, the platinum catalyst was filtered off, and the solvent was removed from the filtrate by distillation under reduced pressure, after which the residue was further purified by distillation under reduced pressure, to yield 201.5 g of the title compound as an oil boiling at 100 to 101°C/5 mmHg (667 Pa). Preparation 1(B) and 1(C) A procedure similar to that described in Preparation 1(A) was repeated, except that the corresponding piperidone and amino compounds were employed in place of 2,2,6,6-tetramethyl-4-piperidone and butylamine. 1(B) 2,2,6,6-Tetramethyl-4-ethylaminopiperidine, boiling at 80 to 83°C/5 mmHg (667 Pa); 1(C) 2,2,6,6-Tetramethyl-4-methylaminopiperidine, boiling at 68 to 70°C/3.5 mmHg (467/Pa). PREPARATION 2 2(A) 2-Chloro-4,6-bis[N-(2,2,6,6-tetramethyl-4-piperidyl)butylamino]-1,3,5-triazine A solution of 43.6 g of 2,2,6,6-tetramethyl-4-butylaminopiperidine dissolved in 100 ml of dioxane was added dropwise to a solution of 18.4 g of cyanuric chloride dissolved in 200 ml of dioxane, whilst stirring at 20 to 25°C. The resulting mixture was thereafter stirred at the same temperature for 2 hours, and then for a further 2 hours at 60 to 70°C. At the end of this time, the dioxane was distilled off under reduced pressure. The residue was mixed with a 10 % w/v aqueous solution of potassium carbonate and extracted with ethyl acetate. The extract was dried over potassium carbonate, and then the ethyl acetate was removed by distillation under reduced pressure, to obtain an oil. This oil was purified by silica gel column chromatography (using a 20 : 1 : 1 by volume mixture of ethyl acetate, ethanol and triethylamine as eluent) to yield 52.5 g of the title compound melting at 40 to 42°C. Preparation 2(B) and 2(C) A procedure similar to that described in Preparation 2(A) was repeated, except that the corresponding piperidine derivative was employed in place of 2,2,6,6-tetramethyl-4-butylaminopiperidine, to give the following compounds: 2(B) 2-Chloro-4,6-bis[ N -(2,2,6,6-tetramethy-4-piperidyl)ethylamino]-1,3,5-triazine, melting at 126 to 127°C; 2(C) 2-Chloro-4,6-bis[ n -(2,2,6,6-tetramethyl-4-piperidyl)methylamino]-1,3,5-triazine, melting at 179 to 188°C. PREPARATION 3 3(A) 2,4-Bis[N-ethyl-N-(2,2,6,6-tetramethyl-4-piperidyl)amino]-6-(2-hydroxyethylamino)-1,3,5-triazine 12.0 g of 2-chloro-4,6-bis[ N -(2,2,6,6-tetramethyl-4-piperidyl)ethylamino]-1,3,5-triazine [obtained as described in Preparation 2(B)], 2.3 g of ethanolamine and 2.0 g of potassium carbonate in 50 ml of dioxane, were heated under reflux for 5 hours. At the end of this time, the dioxane was removed by distillation under reduced pressure, and a mixture of ethyl acetate and water was added thereto, after which the mixture was shaken. The ethyl acetate layer was separated, dried and concentrated by evaporation under reduced pressure, and the resulting residue was recrystallized from ethyl acetate to yield 11.6 g of the title compound as crystals melting at 184 to 185°C. Preparation 3(B) A procedure similar to that described in Preparation 3(A) was repeated, except that the corresponding chlorotriazine compound and corresponding amino compound or alcohol compound were employed, to give the following compounds: 3(B) 2,4-Bis[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-6-(2-hydroxyethoxy)-1,3,5-triazine, melting at 192 to 193°C; PREPARATION 4 4(A) Ethyl N-(2,4-dichloro-1,3,5-triazin-6-yl)-glycinate 36.9 g of cyanuric chloride, 27.9 g of ethyl glycinate hydrochloride and 33.6 g of sodium bicarbonate were heated under reflux in 200 ml of dioxane for 30 minutes. At the end of this time, the dioxane was removed by distillation under reduced pressure, and a mixture of ethyl acetate and water was added to the resulting residue, after which the mixture was shaken. The ethyl acetate layer was separated, dried and concentrated by evaporation under reduced pressure, and the resulting residue was recrystallized from a mixture of hexane and ethyl acetate, to yield 45.0 g of the title compound as crystals melting at 82 to 87°C. 4(B) Ethyl N-[2,4-bis(N-butyl-N-(2,2,6,6-tetramethyl-4-piperidyl)amino)-1,3,5-triazin-6-yl]glycinate 2.36 g of ethyl N -(2,4-dichloro-1,3,5-triazin-6-yl)-glycinate [obtained as described in Preparation 4(A)], 4.19 g of 2,2,6,6-tetramethyl-4-(butylamino)piperidine [obtained as described in Preparation 1(A)] and 2.77 g of sodium bicarbonate were heated under reflux in 20 ml of xylene for 29 hours. At the end of this time, the xylene was removed by distillation under reduced pressure, and a mixture of methylene chloride and water was added to the resulting residue, after which the mixture was shaken. The methylene chloride layer was separated, dried and concentrated by evaporation under reduced pressure, and the resulting residue was purified by silica gel column chromatography (using a 20 : 10 : 1 : 1 by volume mixture of hexane, diethyl ether, ethanol and triethylamine as eluent), to yield 5.46 g of the title compound melting at 40°C. Preparations 4(C) and 4(D) A procedure similar to that described in Preparation 4(B) was repeated, except that the appropriate starting materials were employed, to obtain the following: 4(C) Ethyl N -[2,4-bis( N -methyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino)-1,3,5-triazin-6-yl]glycinate, melting at 133 to 136°C, using 2,2,6,6-tetramethyl-4-(methylamino)piperidine in place of 2,2,6,6-tetramethyl-4-(butylamino) piperidine; 4(D) Ethyl N -[2,4-bis( N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino)-1,3,5-triazin-6-yl]glycinate, melting at 125 to 129°C, using 2,2,6,6-tetramethyl-4-(ethylamino)piperidine in place of 2,2,6,6-tetramethyl-4-(butylamino)piperidine. EXAMPLE 4 100 parts of unstabilized polypropylene powder (melt flow rate = 10 to 15), 0.3 part of stearyl 3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate (an antioxidant) and 0.25 part of one of the stabilizers of this invention were kneaded together in a Brabender Plasti-Corder at 200°C for 10 minutes to obtain a homogeneous composition. The resulting mass was pressed into a sheet having a thickness of 2 to 3 mm using a laboratory press. Portions of this sheet were pressed by a hydraulic press at 260°C for 6 minutes, and immediately thereafter it was introduced into cold water to obtain a sheet having a thickness of 0.5 mm. The same procedures were followed to form a film having a thickness of 0.1 mm from the 0.5 mm thick sheet, and the resulting film was cut into test pieces having dimensions of 50 mm x 120 mm. The test pieces were exposed to light in a sunshine carbon weather meter at a black panel temperature of 63 ± 3°C. The exposed test specimens were subjected to periodic tensile tests, and the "deterioration time" was obtained by determining the time when the elongation of each specimen droped to 50 % of its initial value. The test results are shown as the ratio between the deterioration time of the stabilizer of this invention and that of a control specimen to which the stabilizer of this invention had not been added. These results are summarized in the following Table 2, in which the compounds are identified by the numbers hereinbefore assigned to them. The 2 prior art compounds also tested are: A: ethylene glycol bis[ N -methyl- N -(1,2,2,6,6-pentamethyl-4-piperidyl)aminoacetate]; and B: 1,6-bis{[ N -methyl- N -(1,2,2,6,6-pentamethyl-4-piperidyl)amino]acetatamido}hexane. Compound No. Light resistance (ratio) 105 7.0 114 7.0 A 4.7 B 5.3 Control (no stabilizer) 1.0 EXAMPLE 5 Test pieces of dimensions 10 mm x 100 mm were prepared from the 0.5 mm thick polypropylene sheet obtained as described in Example 4. They were kept in an oven at 150°C and regularly observed. The number of days before the test pieces became white through brittleness was noted and is reported in Table 3. Compound No. Days to brittleness 105 77 114 55 A 9 B 13 Control (no stabilizer) 5

Claims: Claims for the following Contracting States : GB, FR, DE, IT, CH, BE, NL, LU, SE, AT, GR Compounds of formula (I): in which: R¹ represents a methyl group or an ethyl group; and Z represents a -(CH₂)₆- group or a -CH₂-CH₂-0-CH₂-CH₂- group; and acid addition salts thereof. Hexane-1,6-diol bis{ N -(2,4-bis[ N -methyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)glycinate} and acid addition salts thereof. Diethylene glycol bis{ N -(2,4-bis[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)glycinate} and acid addition salts thereof. A polymer composition comprising a polymer stabilized against the effects of light and heat by the incorporation of a polymer stabilizer, in which the polymer stabilizer comprises at least one compound according to any one of the preceding Claims. A composition according to Claim 4, in which said polymer is a synthetic polymer. A composition according to Claim 4, in which said polymer is at least one polymer selected from olefin and diene polymers, styrene polymers, halogen-containing polymers, polymers which are derived from α,β-unsaturated acids and their derivatives, polymers which are derived from unsaturated alcohols and amines or their acyl derivatives or acetals, epoxy polymers, polyacetals, polyalkylene oxides and polyphenylene oxides, polyurethanes and polyureas, polycarbonates, polysulfones, polyamides and copolyamides, polyesters, crosslinked polymers, alkyd resins and unsaturated polyester resins. A process for preparing a compound according to any one of Claims 1 to 3, which comprises reacting a compound of formula (VIII): in which: R¹ is as defined in claim 1; and R⁷ represents a C₁ - C₄ alkyl group; with a compound of formula (X): (Y'')₂-Z (X) (in which: Y'' represents a hydroxy group; and Z is as defined in Claim 1); and, if required, converting the resulting compound to an acid addition salt thereof or converting a salt to the free base. Claims for the following Contracting State : ES A process for the preparation of a compound of formula (I): in which: R¹ represents a methyl group or an ethyl group; and Z represents a -(CH₂)₆- group or a -CH₂-CH₂-0-CH₂-CH₂- group; and acid addition salts thereof; which process comprises reacting a compound of formula (VIII): in which: R¹ is as defined above; and R⁷ represents a C₁ - C₄ alkyl group; with a compound of formula (X): (Y'')₂-Z (X) (in which: Y'' represents a hydroxy group; and Z is as defined above); and, if required, converting the resulting compound to an acid addition salt thereof or converting a salt to the free base. A process according to Claim 1, in which the starting materials and reaction conditions are so chosen as to produce hexane-1,6-diol bis{ N -(2,4-bis[ N -methyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)glycinate) and acid addition salts thereof. A process according to Claim 1, in which the starting materials and reaction conditions are so chosen as to produce diethylene glycol bis{ N -(2,4-bis[ N -ethyl- N -(2,2,6,6-tetramethyl-4-piperidyl)amino]-1,3,5-triazin-6-yl)glycinate} and acid addition salts thereof. A process for preparing a polymer composition stabilised against the effects of light and heat by incorporating a polymer stabiliser into a polymer, in which the polymer stabiliser comprises at least one compound of formula (I) or a salt thereof, as defined in any one of the preceding claims. A process according to Claim 4, in which the polymer is a synthetic polymer. A process according to Claim 4, in which said polymer is at least one polymer selected from olefin and diene polymers, styrene polymers, halogen-containing polymers, polymers which are derived from α,β-unsaturated acids and their derivatives, polymers which are derived from unsaturated alcohols and amines or their acyl derivatives or acetals, epoxy polymers, polyacetals, polyalkylene oxides and polyphenylene oxides, polyurethanes and polyureas, polycarbonates, polysulfones, polyamides and copolyamides, polyesters, crosslinked polymers, alkyd resins and unsaturated polyester resins.

Inventors: NAITO SATORU C O SANKYO COMPAN, OSAWA HISAYU C O SANKYO COMPAN, TODA TOSHIMASA C O SANKYO COMP, YAMAZAKI TAKAAKI C O SANKYO CO, NAITO, SATORU C/O SANKYO COMPANY LIMITED, OSAWA, HISAYU C/O SANKYO COMPANY LIMITED, TODA, TOSHIMASA C/O SANKYO COMPANY LIMITED, YAMAZAKI, TAKAAKI C/O SANKYO COMPANY LIMITED
Applicants: SANKYO CO, SANKYO COMPANY LIMITED
Application year: 1988
Main classification: C07D401
IPC codes: C08K5, C07D401