Polyimide film

Abstract: Disclosed is a film of polyimide having repeating units of formula (1) and a birefringence (Δn) of at least 0.13: wherein R¹ is an aromatic group having a valency of 4, at carbon atoms constituting the aromatic ring, and R² is an aromatic group having a valency of 2, at carbon atoms constituting the aromatic ring. This polyimide film exhibits good thermal dimensional stability.

Description: The present invention relates to a polyimide resin, widely known as a heat resistant resin, and more particularly, to a polyimide film having improved thermal dimensional stability. It is known that polyimide resins exhibit excellent properties such as a high resistance to heat and chemicals, as well as having good electrical and mechanical characteristics. A polyimide film formed of a polyimide resin synthesized from 4,4'-diaminodiphenyl ether and pyromellitic dianhydride has been used in a wide variety of applications, such as is described in, for example, Japanese Patent Publication (Kokoku) No. 36-10999. Polyimide film, which exhibits excellent mechanical characteristics, such as in relation to elongation, has a high coefficient of expansion and thus poor thermal dimensional stability. In recent times, there has been a sharp increase in demand, especially on the part of the electronic and electrical industries, for a polyimide film having excellent dimensional stability and mechanical characteristics. This is because such a film would be extremely useful for printed circuit boards requiring fine processing, as well as in other fields, such as high density magnetic recording. For this reason, various studies are currently being made in an attempt to develop a polyimide film having excellent dimensional stability. For example, the use of rigid molecules such as paraphenylenediamine, dimethyl benzidine, and pyromellitic dianhydride for improving thermal dimensional stability is exemplified in Japanese Patent Disclosures (Kokai) Nos. 61-264028; 61-241325; 61-181828; 61-158025; and 58-185624. However, all of the resultant polyimide films leave room for further improvement with respect to their mechanical strength (particularly, elongation) and their resistance to heat and chemicals. The object of the present invention is to provide a polyimide film of excellent characteristics, including high thermal dimensional stability and high mechanical strength, particularly with regard to elongation. As a result of extensive research carried out with the aim of solving the problems described above, the present inventors have found that a film of a polyimide consisting of repeating units of formula (1) and repeating units of formula (2): wherein R¹ is derived from pyromellitic acid, and wherein the birefringences (Δ n) of said film is at least 0.13, and the molar ratio of the repeating unit of formula (2) to the repeating unit of formula (1) is in the range 1 : 99 to 90 : 10. The way in which to measure the birefringence (Δn) is described in, for example, "Shin Jikken Kagaku Koza, Vol. 19 (Maruzen Ltd.)" and "Seni-Kobunshi Sokutei-ho no Gijutsu (Asakura Shoten)". To be brief, a sample is cut into a wedge shape. Interference fringes can be seen if the sample is subjected to polarizing microscopic observation using sodium light. The birefringence (Δn) of the sample, in which n represents the number of interference fringes, is determined as follows: Δn = (n x λ)/d where, λ is the wavelength (589 nm) of the sodium light, and d is the sample width (nm). A film of polyimide having a birefringence (Δn) of at least 0.13 exhibits good thermal dimensional stability. The thermal dimensional stability of the film is much improved if the birefringence value is 0.17 or greater, and preferably, 0.18 or more. If the birefringence is less than 0.13, the polyimide film exhibits a high coefficient of linear expansion, which results in poor thermal dimensional stability. The polyimide forming the film of the present invention has repeating units represented by formula (2) in combination with repeating units of formula (1): In formulas (1) and (2), R¹ is derived from pyromellitic acid. The molar ratio of the repeating units of formula (2) to the repeating units of formula (1) falls within the range of between 1:99 and 90:10. If the molar ratio is greater than 90:10, the effect this has on increasing the birefringence (Δn) is relatively small. In manufacturing the polyimide film of the present invention, the polyimide is prepared first from a polyamic acid solution which is a precursor to the polyimide. The polyamic acid solution can be prepared by a known method. Specifically, the polyamic acid solution can be prepared by polymerizing substantially equimolar amounts of pyromellitic anhydride and p-phenylene diamine and diamino diphenyl ether as a diamine component in an organic polar solvent. Because it comes to a polyamic acid solution having two different repeating units, it is possible to employ any copolymerization method. Further, it is possible to mix different polyamic acid solutions. The polyimide can be prepared from the polyamic acid solution by way of a chemical method in which a dehydrating agent in an amount exceeding the stoichiometric amount and, as required, a catalytic amount of a tertially amine, etc, are added to the polyamic acid solution for achieving the desired dehydration. Alternatively, the ring-closing to provide the desired polyimide can be performed thermally without using a dehydrating agent. The chemical method is far superior to the thermal method for providing the desired polyimide having a birefringence (Δn) of at least 0.13, though the reason for this is as yet unknown. For manufacturing a polyimide film, the polyamic acid solution is cast or coated on a support, to form a film. The film is dried at 150°C or less for 1 to 30 minutes to obtain a self-supporting film. After it is peeled off the support, the film is fixed to a stationary frame and gradually heated to 100 to 500°C, so as to thermally or chemically perform dehydration and ring-closing to provide the required polyimide film. Alternatively, the polyamic acid solution cast or coated on a support may be gradually heated to about 100 to 500°C for thermally or chemically performing the dehydration and ring-closing on the support. In order to obtain a polyimide film having a birefringence of at least 0.13, however, it is preferable to peel off the self-supporting film, as in the former method, though again, the reason for this is unknown. When chemical dehydration is employed in the former method, the required polyimide film can be obtained very easily. Substances suitable as the dehydrating agent used in the method of chemical dehydration and ring-closing can include, for example, a fatty acid anhydride and an aromatic acid anhydride, while those suitable as the catalyst can include, for example, an aliphatic tertiary amine such as triethyl amine, an aromatic tertiary amine such as dimethylaniline, and a heterocyclic tertiary amine such as pyridine, picoline, or isoquinoline. Examples The present invention can be more fully understood when taken in conjunction with the Examples which follow, though it should be understood that the present invention is not restricted to these Examples. The linear expansion coefficient, in each case, was measured under the condition of 5°C/min, using a TMA-10 (trademark of a thermophysical tester manufactured by Seiko Electronics Inc.), and is given by the average value within the range of between 100°C and 200°C. Comparative Example 1 26.78 g of paraphenylenediamine was placed in a 500-mℓ four-neck flask, and 245.00 g of N,N-dimethyl acetoamide was added thereto to dissolve the paraphenylenediamine. In addition, 18.22 g of 3,3' ,4,4'-biphenyltetracarboxlic acid anhydride in a solid state was placed in a 100-mℓ eggplant type flask and then added to the paraphenylenediamine solution. The 3,3',4,4'-biphenyltetracarboxylic acid dianhydride remaining attached to the inner surface of the eggplant type flask was dissolved in 10.00 g of N,N-dimethyl acetoamide, and the resultant solution was poured into the four-neck flask. The mixture was kept stirred for 3 hours to obtain 15% by weight of a polyamic acid solution. In the above reactions, dry nitrogen gas was used to treat the 3,3',4,4'-biphenyltetracarboxlic acid dianhydride and to fill the reaction system. The polyamic acid solution thus prepared was cast and coated on a glass plate and dried at 100°C for 10 minutes, to form a film. The polyamic acid film was then peeled off from the glass plate and fixed to a stationary frame. Thereafter, the film was heated at 100°C for about 30 minutes, at about 200°C for about 60 minutes and, finally, at about 300°C for about 60 minutes, so as to perform dehydration and ring-closing and, thus, to obtain a polyimide film about 25 microns thick. Table 1 shows the properties of the polyimide film obtained. Comparative Example 2 Acetic anhydride and isoquinoline were added to a polyamic acid solution prepared as in Comparative Example 1, in amounts of 4 moles and 0.5 mole, respectively, relative to 1 mole of the amide bond of the polyamic acid solution. The mixture was well stirred and then cast and coated on a glass plate, after which it was heated at about 100°C for about 10 minutes, at about 250°C for about 10 minutes and, finally, at about 350°C for about 5 minutes. After the heating, the coating was peeled off from the glass plate so as to obtain a polyimide film about 25 microns thick. Table 1 shows the properties of the polyimide film obtained. Comparative Example 3 A polyamic acid solution was prepared as in Comparative Example 1, except that 21.54 g of 4,4'-diaminodiphenyl ether and 23.46 g of pyromellitic anhydride were used. Added to the solution were 4 moles of acetic anhydride and 0.5 mole of isoquinoline relative to 1 mole of the amide bond of the polyamic acid. The mixture was well stirred and, then, cast and coated on a glass plate, after which the coating was dried at about 100°C for about 10 minutes. After the drying, the polyamic acid film was peeled off from the glass plate and fixed to a stationary frame. In this condition, the film was heated at about 250°C for about 10 minutes and, then, at about 350°C for about 5 minutes, so as to obtain a polyimide film about 25 microns thick. Table 1 shows the properties of the polyimide film obtained. Examples 1-4 Polyimide films each about 25 microns thick were prepared as in Comparative Example 3, except that the molar ratio of 4,4'-diaminodiphenyl ether to paraphenylene diamine was changed and an equimolar amount of pyromellitic anhydride was used together therewith. Table 1 shows the properties of the polyimide films obtained. As is apparent from Table 1, the polyimide film exhibits a small linear expansion coefficient if its birefringence (Δn) is 0.13 or greater.

Claims: A film of a polyimide consisting of repeating units of formula (1) and repeating units of formula (2): wherein R¹ is derived from pyromellitic acid, and wherein the birefringences (Δ n) of said film is at least 0.13, and the molar ratio of the repeating unit of formula (2) to the repeating unit of formula (1) is in the range 1 : 99 to 90 : 10.

Inventors: AKAHORI KIYOKAZU, KAWAI HIDEKI, NAGANO HIROSAKU, AKAHORI, KIYOKAZU,, KAWAI, HIDEKI, NAGANO, HIROSAKU,
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI CHEMICAL INDUSTRY CO., LTD.
Application year: 1988
Main classification: C08G73
IPC codes: C08G73, C08J5