Production of composite resins

Abstract: Composite resinous articles are manufactured by introducing a powdery, liquid crystal polymer into a resin matrix under controlled thermal conditions and molding or shaping the resulting mixture under selected thermal conditions. The product articles have increased mechanical properties and improved fabric­ ability.

Description: This invention relates to a method of blending polymers capable of forming anisotropic melts thereof (such a polymer will be referred to as "liquid crystal polymer" hereinafter) and a second polymeric material. In particular, the invention relates to such a method in which fibres of a liquid crystal polymer are formed in a certain regular arrangement in a matrix of a melt-processable resin upon molding or shaping whereby the matrix can be used to produce for example reinforced moldings, fibres, filaments, films, and sheets. Because of the rigid rod-like structure of their molecules, liquid crystal polymers generally exhibit relatively low viscosities in their molten state in comparison with ordinary thermoplastic resins and, when sheared, tend to orientate in the shearing direction to a high degree. Various types of liquid crystal polymers possessing high fluidity and orientation properties have been developed. It has been proposed to blend liquid crystal polymers with other melt-processable polymers so as to provide polymeric compositions which are improved in processability and mechanical properties by making use of the attributes of the special fluidity and orientation characteristics of liquid crystal polymers (see for example Japanese Patent Application Public Disclosure (KOKAI) Nos. 56-115357; 57-25354; 57-40550; 57-40551; 57-40555 and 57-51739). In all the above proposals, however, the liquid crystal polymers and the melt-processable polymeric materials are blended by employing the conventional melt-blending technique. Although it has been found that the blended products (at least in some limited ranges of blending ratio) will provide articles formed therefrom with improved mechanical properties as compared with cases where the respective polymeric components are employed alone, it is not intended to improve the mechanical properties of final products by means of higher order-structural control exercise in the blending of the liquid crystal polymer and the melt-processable polymer. Recently it has also been proposed to reinforce a matrix resin by orientation of a liquid crystal polymer material in acicular or fibre form in a matrix resin. This is known as the "in situ composite" technique and is described, for example, in Japanese Patent Application Public Disclosure (KOKAI) No. 62-116666; Polymer Engineering and Science 27 (1987), 410; Polymer Composite, 8 (1987), 158; and Polymer Engineering and Science 27 (1987), 653. This technique allows certain advantages to be achieved, such as the fact that the manufacturing process is simplified and that the manufacturing machine and other apparatus are worn by the filler to a reduced extent as compared with cases where the resins are reinforced by using conventional reinforcing materials such as glass fibre. Again in the "in situ composite" technique, the liquid crystal polymer and the matrix resin are subjected to melt-kneading. This technique is disclosed in EP-A-0217563. since the dispersibility of the liquid crystal polymer in the matrix resin is largely governed by the compatibility and relative proportions of the two polymeric components and by the extent of kneading, it is frequently observed that the shape or size of the fibres formed of the liquid crystal polymer in the matrix displays an extended distribution range. In other words, it is difficult to obtain a desired narrow range of shape or size of the liquid crystal fibres by employing the "in situ composite" technique. This wide distribution range of the shape or size of the liquid crystal polymer fibres in the matrix is not desirable in terms of achieving the intended improvement in the mechanical properties of the matrix resin in an efficient manner. If the liquid crystal polymer is dispersed in a very finely divided form in the matrix during the kneading step of the "in situ composite" technique, the surface energy of the fine particles is unduly increased so that the shearing deformation of the finely divided particles that is necessary for forming the fibres is prevented. On the other hand, if the liquid crystal polymer is dispersed in a coarse particulate form, the fibres will be formed with a large diameter or a sheetlike structure. Hence the fibres will have a decreased L/D ratio (or aspect ratio), which is not desirable in terms of improving the mechanical properties of final products. In view of the difficulties encountered in the conventional methods, one of the objects of the present invention is to provide a method for efficiently improving the mechanical properties of resinous moldings or shapings by uniformly dispersing in a matrix resin a liquid crystal polymer in a powder form within a certain particle size range so as to permit the dispersed liquid crystal polymer powder to form regularly arranged fibres in the matrix resin when subjected to a molding or shaping process. In order to solve the problems encountered in the conventional methods, we have studied how best to introduce the liquid crystal polymer into the matrix resin material. As a result of our studies, it has been found that mouldings or shapings having liquid crystal polymer fibres within a narrow diameter range dispersed in a matrix resin can be obtained by introducing a liquid crystal polymer in powder form within a certain particle size range into a melt-processable matrix; kneading the resulting mixture at a temperature at which the matrix resin will melt but at which the particles of the liquid crystal polymer will not be deformed so as to prepare a blend comprising particles of the liquid crystal polymer dispersed uniformly in the matrix resin; and molding or shaping the blend at a temperature within the range at which the liquid crystal polymer is capable of forming liquid crystals. Accordingly the present invention is directed to a resin mixture obtainable by a method comprising mixing a liquid crystal polymer material in powder form with a second melt processable polymer material which second polymer is processable at a temperature which is 5-150°C lower than the liquid crystal forming temperature or the lower limit of the liquid crystal forming temperature range of the liquid crystal polymer; the particle size of the liquid crystal polymer powder ranging from 10 to 1000 micrometres; the liquid crystal polymer material being present in a proportion of 1 to 80% by weight of the total weight of the liquid crystal polymer and the matrix polymer and kneading the resulting mixture at a temperature at the second polymer material will flow but at which the liquid crystal polymer will remain as discrete particles whereby the liquid crystal polymer powder is uniformly dispersed in a matrix of the second polymer; the ratio of the viscosity of the matrix polymer material measured at the temperature to be used in the molding or shaping step to the viscosity of the first polymer measured at the same temperature being in the range of from 0.5:1 to 100:1. The invention also extends to the use of the resin mixture of the invention for producing articles, characterised in that the mixture is subjected to a molding or shaping process at a temperature within the range at which the first polymer is capable of forming liquid crystals. The liquid crystal polymer materials which may be used in the present invention are thermoplastic resins exhibiting liquid crystal properties in the molten state and may be a polymer having a nematic or smectic or cholesteric structure. Examples of such liquid crystal polymers include aromatic polyesters as described, for example, in GB Patent No. 1,507,207; US Patent Nos. 3,778,410, 4,067,852, 4,083,829, 4,130,545 and 4,161,470; aromatic polyazomethines as described in US Patent No. 4,048,148; and other aromatic polyester-polycarbonates, aromatic polyimide-polyesters, or aromatic polyisocyanates. Although the melt-processable polymer used in the present invention may exhibit liquid crystal properties of its own, the primary object of the present invention is to improve the processability and mechanical properties of compositions based upon conventional melt-processable polymers. The melt-processable polymer material may be based on one or more thermoplastic polymers. Thus, examples of the melt-processable polymers which may be used in the invention include a polyolefin, an acrylic polymer, a polystyrene, a polyphenylene oxide, a polyamide, a polyphenylene sulphide, a polyester, a polysulphone, a polyether sulphone, a poly-ketone, a polyether ketone, a polyfluorolefin, a poly-oxymethylene, a thermoplastic cellulosic polymer, a microbially produced polymer (such as polyhydroxy-butyrate) or a mixture thereof. These thermoplastic materials may be used in combination with one or more thermosetting materials, provided that the resulting compositions are melt-processable. Examples of suitable thermosetting materials include injection moldable polyurethanes, silicone rubbers, phenolic resins and amino resins. The liquid crystal polymer may be an aromatic polyester, an aromatic polyazomethine, an aromatic polyester amide, an aromatic polyester-polycarbonate, an aromatic polyimide-polyester or an aromatic polyisocyanate or a mixture thereof. The liquid crystal polymer powder employed in the invention is dispersed in a matrix of the melt-processable resin in the molten state. The processing temperature of the matrix resin is 5° to 150°C lower than the liquid crystal forming temperature of the liquid crystal polymer to be used in combination with the matrix resin. If the matrix resin is processed at a temperature equal to or higher than the liquid crystal forming temperature of the liquid crystal polymer, uniform dispersion of the liquid crystal polymer particles may not be achieved in the matrix resin, because particles of the liquid crystal polymer are subject to deformation, particle size reduction, coalescence or the like under the influence of shearing force where particles of the liquid crystal polymer are dispersed in the molten matrix resin. However, for example in the case where the melt viscosity of the liquid crystal polymer is higher than that of the matrix resin to a degree sufficient to substantially protect the particles of the liquid crystal polymer from deformation when they are kneaded together, the kneading step may be carried out at a temperature higher than the liquid crystal forming temperature. The appropriate particle size of the liquid crystal polymer powder used in the invention ranges from 10 to 1,000 µm and preferably from 50 to 250 µm. Where the particle size is less than about 10µm, shearing deformation of the particles of the liquid crystal polymer may not occur or may only occur to a small extent in the matrix resin and the liquid crystal polymer will only be able to form fibres that are unevenly distributed in the matrix. On the other hand, if the particle size is greater than about 1,000 µm, the liquid crystal polymer will be rearranged in the matrix as fibres with an unduly large diameter or with a sheetlike structure. This means that the fibres of the liquid crystal polymer formed in the matrix show a low L/D ratio (or aspect ratio) which will not be effective in improving the mechanical properties of the products prepared from the blend. The proportion of liquid crystal polymer to be used in the present invention is from 1 to 80%, preferably from 5 to 70%, by weight on the basis of the total weight of the matrix resin and the liquid crystal polymer. If the liquid crystal polymer is employed in an amount of less than 1% by weight on the same basis, the mechanical properties of the final products would not be improved to any appreciable extent. If the liquid crystal polymer is employed in a proportion of greater than 80% by weight on the same basis, the fibres of liquid crystal formed in the matrix would tend to coalescence into sheet like structure resulting in a low reinforcement effect. The kneaded mixture comprising particles of the liquid crystal polymer dispersed uniformly in the matrix is then subjected to molding or shaping in a range of temperature within which the liquid crystal polymer is capable of forming liquid crystals. In regard to ensuring that the liquid crystal polymer is effectively formed into fibres in the matrix resin, the difference between the melt viscosity of the matrix resin and that of the liquid crystal polymer is an important parameter. Under the shearing stress that is applied during molding or shaping, if the apparent ratio of the viscosity of matrix resin to the viscosity of liquid crystal polymer is in the range of from about 0.5 to about 100, particles of the liquid crystal polymer may be deformed by the shearing stress and will be efficiently formed into fibres in a desirable state. If the apparent viscosity ratio is less than 0.5, the formation of fibres from the liquid crystal polymer in the matrix resin would not proceed efficiently. The liquid crystal forming temperature or range of the liquid crystal polymer at or within which the molding or shaping step is preferably effected according to the present invention may be easily determined by conventional means such as DSC (differential scanning calorimetry), X-ray diffraction, polarized microscope. Although the liquid crystal polymer will form an isotropic molten phase above the upper limit of the liquid crystal forming temperature, a temperature above the upper limit may be used in the molding or shaping step provided that the liquid crystal polymer is able to form liquid crystals after taking into account the shearing force used in that step, as well as being efficiently converted into fibres in the matrix. Generally, the liquid crystal polymers tend to display an emphasized or dramatic "shear thinning" effect as compared with ordinary thermoplastic resins. For this reason the liquid crystal polymers will show a significantly reduced melt viscosity and will be efficiently converted into fibres when a shearing rate of about 10² sec⁻¹ or more is employed in the molding or shaping step. In an embodiment of the present method for producing articles of composite resins, the liquid crystal polymer and the matrix resin are first kneaded, for example, in a conventional kneader and/or extruder, the kneaded mixture is pelletized, and the pellets are subjected to molding or shaping, for example, by an injection molding technique. In an alternative embodiment, the extrudate from the kneading step may be directly fed to the subsequent step, for example, a step of film-forming by the T-die method, or one of spinning by the melt spinning method. A matrix resin into which a liquid crystal polymer has been introduced in accordance with the present invention exhibits a significantly reduced melt viscosity in comparison with the viscosity of a matrix resin devoid of such a liquid crystal polymer. Thus the moldability of the matrix resin is improved. In addition, since the kneading of the liquid crystal polymer and the matrix resin is effected at a temperature below the liquid crystal forming temperature of the liquid crystal polymer, if a liquid crystal polymer powder within a predetermined range particle size is employed, it is possible to uniformly disperse this liquid crystal polymer of specified particle size in the matrix. Consequently, it is possible to form fibres of the liquid crystal polymer with a greater uniformity of diameter that are more uniformly dispersed in the matrix by molding or shaping the blend at a temperature at which the liquid crystal polymer is capable of forming liquid crystals. The uniform dispersion of the liquid crystal polymer in the matrix resin achieved by the present invention permits the liquid crystal polymer to be used in an increased proportion with increased benefits such as increased mechanical properties as compared with the case where both materials are blended by the conventional melt-blending technique. In this way, according to the present invention, composite moldings, films, sheets, fibres and the like are provided which offer improved ease of fabrication and mechanical properties by using a simple but readily controlled method. The invention will be described in more detail with reference to the following Examples and Comparative Examples. EXAMPLE 1 A polysulphone resin ("UDEL" P-1700; manufactured by Amoco Performance Products Industry; 90 parts by weight) and a wholly aromatic polyester (liquid crystal polymer) in powder form having a particle size range of from 150 to 250 µm (10 parts by weight) were mixed together. The mixture was kneaded in a "Laboplastomill" single screw extruder (manufactured by Toyo Seiki Mfg. Co.) and extruded through a die. The resulting continuous extrudate was taken off by a "Meltstrength" take-off machine so as to form a line of monofilament. The liquid crystal polymer used consisted of 60 mole % of 4-oxybenzoyl units, 15 mole % of terephthaloyl units, 5 mole % of isophthaloyl units and 20 mole % of 1,4-dioxydiphenylene units. The liquid crystal polymer exhibited a melting point of 336°C when measured by the DSC method. The melt viscosity was determined in a flow tester (manufactured by Shimazu Mfg. Co.) with a die having a capillary length of 2 mm and a diameter of 0.5 mm and was found to be 1,300 poises at a temperature of 340°C and at a shear rate of 10³ sec⁻¹. The polysulphone resin which was used had a melt viscosity of 5,600 poises when measured under the same conditions described. The kneading conditions employed in the extruder were a cylinder temperature of 300°C, a rotation speed of 5 rpm and a die temperature (or take-off temperature) of 340°C. The extruder die had a capillary length of 10 mm and a diameter of 2.1 mm. The extrudate was taken off at various speeds of 10, 50 and 100 m/min. The mechanical properties of the product filaments were determined using an "Autograph" testing apparatus (manufactured by Shimazu Mfg. Co.) with a sample having an aspect ratio of 100 and a strain rate of 10⁻³ sec⁻¹. Each of the values given is the average of measurements on seven filaments with the highest and lowest values being discarded. Each filament was conditioned at a relative humidity of 50% at 23°C for 24 hours before having its physical properties measured. EXAMPLE 2 The general procedure described in Example 1 was repeated except that a take-off temperature of 370°C was employed instead of one of 340°C. The ratio of the melt viscosity of the polysulphone (PSF) at 370°C to that of the liquid crystal polymer (LCP) at 370°C was 20 (at a shear rate of 1 x 10⁴ sec⁻¹). EXAMPLE 3 The general procedure described in Example 1 was repeated except that the particle size of the liquid crystal polymer powder ranged from 500 to 1000 µm. EXAMPLE 4 The general procedure described in Example 1 was repeated except that the polysulphone resin was used in a proportion of 70 parts by weight and the liquid crystal polymer was used in a proportion of 30 parts. EXAMPLE 5 The general procedure described in Example 1 was repeated except that the polysulphone resin was used in a proportion of 50 parts by weight and the liquid crystal polymer was used in a proportion of 50 parts. The mechanical properties of the monofilament products obtained in Examples 1 - 5 are shown in Table I. COMPARATIVE EXAMPLE 1 The general procedure described in Example 1 was repeated except that the profile of the cylinder temperature used in the kneader/extruder unit was set in such a fashion that the temperatures in the first, second and third zones of the cylinder were 340°C, 320°C and 300°C, respectively, and that the liquid crystal polymer was fed in a pellet form i.e. having a particle size well in excess of 1000 microns. COMPARATIVE EXAMPLE 2 The procedure of Comparative Example 1 was repeated except that 70 parts by weight of the polysulphone resin was combined with 30 parts by weight of pellets of the liquid crystal polymer in the kneader. COMPARATIVE EXAMPLE 3 The procedure of Comparative Example 1 was repeated except that 50 parts by weight of the polysulphone resin was combined with 50 parts by weight of pellets of the liquid crystal polymer in the kneader. COMPARATIVE EXAMPLE 4 The procedure of Comparative Example 1 was repeated except that the liquid crystal polymer was omitted and the polysulphone resin was used alone. COMPARATIVE EXAMPLE 5 The procedure described in Example 1 was repeated except that the take-off temperature was set at 300°C. The ratio of the melt viscosity of the polysulphone (PSF) resin at 300°C to the melt viscosity of the liquid crystal polymer (LCP) at 300°C was 0.2 (at a shear rate of 1 x 10⁴ sec⁻¹). The mechanical properties of the monofilament products obtained in Comparative Examples 1-5 are shown in Table II. COMPARATIVE EXAMPLE 6 The general procedure described in Example 1 was repeated except that the polysulphone resin was used in a proportion of 10 parts by weight and the liquid crystal polymer was used in a proportion of 90 parts. The resulting filament was heterogeneous and brittle and was not suitable to be subjected to the test for measuring mechanical properties. COMPARATIVE EXAMPLE 7 The general procedure of Example 1 was repeated except that the particle size of the liquid crystal polymer was 2000 µm. A significantly increased torque was required in the kneading operation. The resulting monofilament was heterogeneous.

Claims: A resin mixture obtainable by a method comprising mixing a liquid crystal polymer material in powder form with a second melt processable polymer material which second polymer is processable at a temperature which is 5-150°C lower than the liquid crystal forming temperature or the lower limit of the liquid crystal forming temperature range of the liquid crystal polymer; the particle size of the liquid crystal polymer powder ranging from 10 to 1000 micrometers; the liquid crystal polymer material being present in a proportion of 1 to 80% by weight of the total weight of the liquid crystal polymer and the matrix polymer; and kneading the resulting mixture at a temperature at which the second polymer material will flow but at which the liquid crystal polymer will remain as discrete particles whereby the liquid crystal polymer powder is uniformly dispersed in a matrix of the second polymer; the ratio of the viscosity of the matrix polymer material measured at the temperature to be used in the moulding or shaping step to the viscosity of the first polymer measured at the same temperature being in the range of from 0.5:1 to 100:1. A resin mixture as claimed in claim 1 characterised in that the liquid crystal polymer is nematic or smectic or cholesteric. A resin mixture as claimed in claim 1 or claim 2 characterised in that the liquid crystal polymer is an aromatic polyester, an aromatic polyazomethine, an aromatic polyester amide, an aromatic polyester-polycarbonate, an aromatic polyimide-polyester or an aromatic polyisocyanate or a mixture thereof. A resin mixture as claimed in claim 1, 2 or 3 characterised in that the melt-processable polymer material is based on one or more thermoplastic polymers. A resin mixture as claimed in claim 4 characterised in that the melt-processable polymer material is a polyolefin, an acrylic polymer, a polystyrene, a polyphenylene oxide, a polyamide, a polyphenylene sulphide, a polyester, a polysulphone, a polyether sulphone, a polyketone, a polyether ketone, a polyfluorolefin, a polyoxymethylene, a thermoplastic cellulosic polymer, a microbially produced polymer or a mixture thereof. A resin mixture as claimed in any one of claims 1 to 5 characterised in that the particle size of the liquid crystal polymer powder ranges from 50 to 250 micrometers. A resin mixture as claimed in any one of claims 1 to 6 characterised in that the liquid crystal polymer material is present in a proportion of 5 to 70%. The use of the resin mixture claimed in any one of claims 1 to 7 for producing articles, characterised in that the mixture is subjected to a moulding or shaping process at a temperature within the range at which the first polymer is capable of forming liquid crystals.

Inventors: ISHIKAWA TOMOHIRO, KAWAGUCHI HISATO, KONDO YOZO, TSURUTA AKEHARU, ISHIKAWA, TOMOHIRO, KAWAGUCHI, HISATO, KONDO, YOZO, TSURUTA, AKEHARU
Applicants: TOSOH CORP, TOSOH CORPORATION
Application year: 1988
Main classification: C08L101
IPC codes: C08J5, C08L81, C08J3, B29C67, C08L101