Stabilized crystalline polymer composition

Abstract: The melting point and the apparent degree of crystallinity of a linear alternating polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon are stabilized against undue lowering during melt processing by inclusion within the polymer of an aluminium trialkoxide or hydrolysis product thereof.

Description: This invention relates to stabilized crystalline polymer compositions, notably of linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon. More particularly, the invention relates to polymers of improved melt processing stability during procedures which involve melting and subsequent solidification of the polymer. Polymers of carbon monoxide and olefin(s) have been known for a number of years. More recently, the class of linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon, e.g., ethylene or ethylene and propylene, has become of greater interest. A convenient general process for the production of these linear alternating polymers is illustrated by European Patent Applications Nos. 121,965 and 181,014. The process involves a catalyst composition formed from a Group VIII metal selected from palladium, cobalt or nickel, the anion of a non-hydrohalogenic acid having a pKa below 2 and a bidentate ligand of phosphorus, arsenic or antimony. The resulting polymers are relatively high molecular weight thermoplastic polymers having utility in the production of structural articles such as containers for food and drink and parts for the automotive industry. The polymers are characterized by relatively high melting points, frequently over 200 °C, depending upon the molecular weight and the chemical nature of the polymers. A melting point of this magnitude is of value in many applications, particularly when a shaped article is to be subjected to conditions of elevated temperature. However, when a polyketone polymer is subjected to the high temperatures required for melt processing, chemical changes can occur such as crosslinking, chain scission and formation of undesirable degradation products which can cause loss of attractive physical properties. These changes are particularly apparent in the melting point and the percentage of crystalline versus amorphous polymer as measured by differential scanning calorimetry (DSC). It is desirable that polyketone compositions should not undergo changes in physical properties during melt processing procedures. Stabilization of the percent crystallinity and melting point of the polymer is an indication of stabilization of other physical properties. It would be of advantage to provide polyketone compositions whose melting point is relatively constant throughout one or more melt processing operations. It would be of advantage to provide polyketone compositions whose percent crystallinity has been stabilized against loss during melting-solidification of the polymer composition. These objectives are met by incorporating aluminium alkoxides or derivatives thereof in the polyketone. Accordingly, the invention relates to a crystalline polymer composition stabilized against the loss of apparent crystallinity during melt processing, characterized in comprising a linear alternating polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon, and a stabilizing quantity of aluminium trialkoxide or aluminium containing hydrolysis product thereof. Such polyketone compositions exhibit stability of apparent crystallinity and relative stability of melting point through one or more melt processing operations which incorporate the melting and subsequent solidification of the polymer composition. The polymers which are employed in the compositions of the invention are the linear alternating polymers of carbon monoxide and at least one ethylenically unsaturated hydrocarbon which are often referred to as polyketones. Suitable ethylenically unsaturated hydrocarbons for use in the polymers have from 2 to 20 carbon atoms inclusive, preferably from 2 to 10 carbon atoms inclusive, which are aliphatic hydrocarbons such as ethylene as well as other alpha-olefins including propylene, butene-1, octene-1 and dodecene-1, or are arylaliphatic containing an aryl substituent on an otherwise aliphatic molecule, particularly an aryl substituent on a carbon atom of the ethylenic unsaturation. Illustrative of this latter class are styrene, p-methylstyrene, p-ethylstyrene and m-methylstyrene. Optionally functional groups are present in the hydrocarbon, so that copolymers of carbon monoxide and e.g. acrylate esters are included. Preferred polyketone polymers are copolymers of carbon monoxide and ethylene or terpolymers of carbon monoxide, ethylene and a second alpha-olefin, i.e., an alpha-olefin of 3 or more carbon atoms, particularly propylene. Of particular interest are those polymers of molecular weight from about 1,000 to about 200,000, particularly those of molecular weight from 10,000 to 50,000. The structure of the preferred polymer is that of a linear alternating polymer of carbon monoxide and unsaturated hydrocarbon, e.g., ethylene or ethylene and propylene. The polymer will contain substantially one carbon monoxide moiety for each moiety of unsaturated hydrocarbon. when terpolymers of carbon monoxide and ethylene and a second ethylenically unsaturated hydrocarbon are produced, there will be at least about 2 units incorporating a moiety of ethylene for each unit incorporating a moiety of the second hydrocarbon. Preferably there are 10 to 100 units incorporating a moiety of ethylene per unit incorporating a moiety of the second hydrocarbon. The polymer chain of the preferred class of polymers is thus represented by the formula [CO(CH₂-CH₂)] x [CO-(B)] y - wherein B is the moiety obtained by polymerization of the second alpha-olefin of 3 to 20 carbon atoms through the ethylenic unsaturation. The -CO(CH₂-CH₂) units and the -CO(B) units occur randomly throughout the polymer chain and the ratio of y:x is no more than 0.5. In the modification of the invention which employs copolymers of carbon monoxide and ethylene without the presence of a second hydrocarbon, the polymers are represented by the above formula wherein y=0. When y is other than 0, i.e., terpolymers are employed, ratios of y:x from 0.01 to 0.1 are preferred. The polymer chain will have end groups which depend upon the particular materials present during polymerization and how the polymer is processed during any subsequent purification. The precise nature of such end groups or "caps" is not critical, however, and the polymeric polyketones are fairly depicted by the description of the polymer chain. The compositions of the invention comprise an intimate mixture of the polyketone polymer and aluminium alkoxide or aluminium-containing hydrolysis product thereof. The precise form of the aluminium species present in the final composition is not known with certainty and may depend upon a number of factors including the degree of moisture in the polymer with which the aluminium trialkoxide is mixed, whether or not the composition has been exposed to moisture as by contact with a humid environment, the temperature to which the polymer composition has been raised and the number of times the composition has been thermally processed. It is known that the aluminium alkoxides are quite sensitive to moisture so that unless substantial precautions are taken to insure that the composition remains dry, the aluminium trialkoxide will hydrolyze, probably to species containing aluminium and hydroxyl moieties. At elevated temperatures, thermolysis of the aluminium trialkoxide may occur and this process is also considered to give species containing aluminium and hydroxyl moieties. Insofar as the aluminium species is likely the same regardless of whether hydrolysis or thermolysis takes place, despite different organic products, the term aluminium-containing hydrolysis product is employed to indicate the aluminium-containing species of either type of aluminium trialkoxide decomposition. However, when the stabilizer is provided in the form of an aluminium trialkoxide, whatever hydrolysis or thermolysis takes place is not considered to detract from the advantages of stabilization of the polymer. The aluminium trialkoxide employed as the source of the aluminium species incorporates three identical alkoxide moieties or alternatively contains two or three different alkoxide species and may have from 3 to 36 carbon atoms inclusive, preferably from 3 to 12. The alkoxide species are derived from primary, secondary or tertiary alcohols. A suitable aluminium alkoxide is therefore represented by the formula Al(OR)₃ wherein each R independently is alkyl of up to 12 carbon atoms, preferably up to 4, and is primary, secondary or tertiary alkyl. Illustrative of primary alkyl are methyl, ethyl, n-propyl, isobutyl, n-octyl, 2-ethyhexyl, n-dodecyl and n-decyl, while secondary alkyl substituents include isopropyl, sec.butyl 2,4-dimethyl-2-butyl and 2-ethyl-2-octyl. Tertiary alkyl radicals are illustrated by tert.butyl and tert.amyl. In general, secondary alkyl groups are preferred over either the primary or the tertiary alkyl groups and particularly preferred are those aluminium alkoxides incorporating three identical secondary alkoxide groups. Illustrative of such alkoxides are aluminium triisopropoxide, aluminium tri(sec.butoxide) and aluminium tri(sec.octoxide). Aluminium triisopropoxide is a particularly preferred species. The amount of aluminium alkoxide to be employed is a stabilizing quantity. Amounts from about 0.01% by weight to about 10% by weight based on the total composition are satisfactory with quantities from 0.05% by weight to 1% by weight on the same basis being preferred. The method of mixing the polymer and the aluminium alkoxide is not critical so long as an intimate mixture is obtained. In one modification, the aluminium alkoxide is dissolved in a suitable solvent as illustrated by hydrocarbons, e.g., benzene and toluene, lower alkanols such as methanol and ethanol or carbonylic solvents such as acetone or methyl ethyl ketone. The polymer in a particulate form is added and the solvent removed as by evaporation to provide the polymer composition as a residue. Best results are obtained if the composition is agitated during solvent removal by shaking or rotating of the container in which the composition is formed. In an alternate modification, the polymer in a finely divided form is mixed with an aluminium trialkoxide powder and the resulting mixture is passed through an extruder. Whatever the ultimate aluminium-containing species in the composition might be, the aluminium is preferably provided to the composition as the aluminium trialkoxide. The resulting compositions have an improved melt processability as evidenced by a relatively constant apparent crystallinity and relatively constant melting points and crystallization temperatures, as well as by relatively constant high heats of crystallization when subjected to melt processing operations of melting and solidification. Retention of an apparent crystallinity during melt processing indicates that the crystallinity of a polymer composition subsequent to processing is not significantly lower than the crystallinity prior to melt processing. Polymers which are not stabilized against loss of apparent crystallinity exhibit melting points, crystallization temperatures and heats of crystallization which decrease, in some cases substantially decrease, upon melt processing. This decrease of melting point and crystallization temperature, although possibly due to a number of factors, is a measure of the loss of apparent crystallinity with the magnitude of the temperature decrease being some measure of the loss of apparent crystallinity. A decrease in heat of crystallization upon melt processing is a more direct measure of loss of apparent crystallinity. This improvement in melt processability, as evidenced by stability of apparent crystallinity and relatively constant melting points, offers considerable advantages which are not to be found in unstabilized polymers. For example, a stabilized polymer composition may be converted into nibs by the use of an extruder. The nibs are then suitably injection molded to produce an article without substantial decrease in melting point of the polymeric composition. The compositions of the invention are particularly useful in this and other instances where melt processing to the desired product requires a series of melting and solidification cycles. While the compositions are usefully processed by conventional techniques which do not require melting and solidification of the polymer, the advantages of the compositions are most apparent when melt processing operations which do involve melting and solidification of the polymer are employed. The compositions of the invention stabilized against loss of apparent crystallinity may optionally contain other conventional additives which do not serve to unnecessarily reduce the melting point or apparent degree of crystallinity. Such additives include antioxidants, blowing agents and mold release agents which are added to the polymer by blending, milling or other conventional methods prior to, subsequent to or together with the aluminium alkoxide. The compositions of the invention are useful for the variety of applications of a premium thermoplastic. They are particularly useful in the production of articles which typically require one or more melting-solidification cycles in their production. Illustrative of such articles are containers for food and drink, shaped parts for the automobile industry, wires and cables and structural articles for construction applications. The invention is further illustrated by the following examples which should not be construed as limiting the invention. Procedure In the following examples, measurements of melting points and crystallization temperatures, or alternatively heats of melting and heats of fusion, were made by the use of a commercially available differential scanning calorimeter (DSC) which employs samples of polymer or polymer composition in sealed pan containers. The pan and contents are heated at a controlled rate, typically 20 °C/minute, until the sample has melted. The pan and contents are then cooled until the sample has solidified and then heated, past a second melting point, to 285 °C at which temperature the sample is maintained for 10 minutes. The pan and contents are then cooled until the sample has solidified a second time. The melting and crystallization temperatures are defined as the temperatures at which the heat flow reaches a maximum (for melting) or a minimum (for crystallization). Typically the melting point, Tm, will be higher than the crystallization temperature, Tc. Although a number of factors influence the melting point and crystallization temperature, these values are also influenced by the crystallinity of the polymer. In general, the smaller the difference between the first and second melting points, the greater the degree of retained crystallinity. The same relationship is generally true for the crystallization temperatures. It is also possible to determine through the use of the DSC the magnitude of the first and second heats of melting (H₁ and H₂) and the first and second heats of crystallization (C₁ and C₂) for the polymer without aluminium trialkoxide and also for the stabilized polymer composition. In general, the heats of crystallization for the stabilized composition will be higher than the corresponding values for the unstabilized polymer. The greater this difference is, the greater the degree of crystallinity which has been retained in the polymeric composition. Samples to be evaluated were prepared by several different procedures. In one method, aluminium triisopropoxide was deposited upon a linear alternating polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon by dissolving the alkoxide in toluene and adding polymer in particulate form. The toluene was then removed by evaporation on a rotary evaporator to leave a coating of aluminium triisopropoxide on the polymer particles. Samples produced in this manner are designated "A" in the examples which follow. The A samples were on occasion divided with one portion being kept under vacuum and the other portion maintained under 100% humidity for several days. These samples are designated AD and AW respectively. Other samples were prepared by powder blending. Aluminium triisopropoxide powder was shaken with the polymer in powdered form and the resulting mixture was extruded to produce nibs. Samples produced in this manner are termed "B" in the examples which follow. On occasion these B samples were divided with one portion maintained under vacuum and the other maintained under a relative humidity of 100% for several days. These samples are designated BD and BW respectively. Example 1 A linear alternating terpolymer of carbon monoxide, ethylene and propylene was produced employing a catalyst composition formed from palladium acetate, the anion of trifluoroacetic acid and 1,3-bis-(diphenylphosphino)propane. Samples of this polymer were evaluated in the DSC as a standard along with samples of stabilized composition produced by the above methods. The results are shown in Tables IA (where temperatures are given in °C) and IB (where heats are reported in cal/g ). Sample Preparation % Alkoxide in Sample TM1 TC1 TM2 TC2 Standard 0 232 167 224 155 AW 0.5 232 176 228 167 AD 0.5 231 178 226 170 BW 0.1 235 173 230 160 BD 0.1 234 175 226 162 BW 1.0 227 178 226 169 BD 1.0 232 178 227 169 Sample Preparation % Alkoxide in Sample H1 C1 H2 C2 Standard 0 ∼ 20 17.3 20.0 13.9 AW 0.5 21.9 19.7 21.3 17.0 AD 0.5 20.3 20.0 21.3 18.1 BW 0.1 19.3 18.2 19.1 15.4 BD 0.1 20.0 19.9 20.0 17.4 BW 1.0 20.0 19.6 20.3 17.7 BD 1.0 20.8 20.0 21.1 17.5 Example 2 Another linear alternating terpolymer of carbon monoxide, ethylene and propylene was produced employing a catalyst formed from palladium acetate, the anion of trifluoroacetic acid and 1,3-bis(diphenylphosphino)propane. Samples were prepared by the above procedures and evaluated, together with a standard, in the DSC. The results are shown in Tables IIA and IIB. Sample Preparation % Alkoxide in Sample TM1 TC1 TM2 TC2 Standard 0 230 159 214 142 AW 0.5 228 168 220 161 AD 0.5 232 171 227 163 Sample Preparation % Alkoxide in Sample H1 C1 H2 C2 Standard 0 ≈ 20 14.5 15.7 10.7 AW 0.5 18.4 17.7 20.4 15.6 AD 0.5 20.1 17.7 18.7 15.4 Example 3 A linear alternating copolymer of carbon monoxide and ethylene was produced employing a catalyst formed from palladium acetate, the anion of trifluoroacetic acid and 1,3-bis(diphenylphosphino)propane. A sample containing aluminium triisopropoxide was produced according to the BW procedure above and evaluated in the DSC against the copolymer as a standard. The results are shown in Tables IIIA and IIIB. Sample Preparation % Alkoxide in Sample TM1 TC1 TM2 TC2 Standard 0 254 196 248 179 BW 0.1 252 208 246 201 Sample Preparation % Alkoxide in Sample H1 C1 H2 C2 Standard 0 ∼ 20 25.8 28.6 20.8 BW 0.1 27.5 25.1 28.7 20.7 Although the retention of degree of crystallinity is not as great for the copolymer of this example as that for the terpolymers of the other examples, if larger percentages of aluminium triisopropoxide are added to the polymer, a greater degree of retention of crystallinity will be observed.

Claims: Crystalline polymer composition comprising a linear alternating polymer of carbon monoxide and at least one ethylenically unsaturated hydrocarbon, and an aluminium trialkoxide or aluminium-containing hydrolysis product thereof in an amount of from 0.01 to 10% by weight based on the total composition. A composition as claimed in claim 1 wherein the polymer is represented by the formula [CO-(CH₂-CH₂)] x [CO-(B))] y wherein B is the moiety of an alpha-olefin of 3 to 20 carbon atoms inclusive polymerized through the ethylenic unsaturation, and the ratio of y:x is no more than 0.5. A composition as claimed in claim 2 wherein the alpha-olefin of 3 to 20 carbon atoms inclusive is propylene. A composition as claimed in any of claims 1-3, wherein the aluminium trialkoxide is represented by the formula Al(OR)₃ wherein each R independently is alkyl of up to 12 carbon atoms. A composition as claimed in claim 4 wherein each R represents the same secondary alkoxide group of up to 4 carbon atoms. A composition as claimed in claim 5 wherein the aluminium trialkoxide is aluminium triisopropoxide.

Inventors: KEMP RICHARD ALAN, KLUTTZ ROBERT QUILLIN, RYAN ROBERT CHARLES, KEMP, RICHARD ALAN, KLUTTZ, ROBERT QUILLIN, RYAN, ROBERT CHARLES
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1988
Main classification: C08K5
IPC codes: C08K5, C08G67, C08L73