A curable composition

Abstract: A curable composition comprises 100 parts by weight of an oxyalkylene polymer having at least one silicon-containing group which has a hydroxyl or hydrolyzable group attached to silicon atom and which is crosslinkable by forming a siloxane linkage and from 0.1 to less than 10 parts by weight of a liquid diene polymer.

Description: The present invention relates to a composition curable by moisture at room temperature yielding a rubbery cured substance. More particularly, the invention relates to a curable composition comprising an oxyalkylene polymer having a silicon-containing group which has a hydroxyl or hydrolyzable group attached to silicon atom (hereinafter referred to as a reactive silicon functional group) and which is crosslinkable by forming a siloxane linkage. Oxyalkylene polymers having at least one reactive group in the molecule are well known. The polymers are curable at room temperature yielding a rubbery substance and are used as a sealant and the like. Of these polymers, polyoxypropylene having terminal methoxysilyl groups has already been industrially produced (trade name: MS Polymer of Kanegafuchi Chemical Industry Co., Ltd.). The cured oxyalkylene polymers having a reactive silicon functional group are rubbery substances preferably free of surface tack, and this property is especially important where the polymers are used as a sealant. This is because dust or dirt is apt to adhere to the surface where the surface is tacky. The drawback of the oxyalkylene polymers having a reactive silicon group, however, is that these polymers can produce cured substances having a tacky surface. EP-A-0 108 946 discloses a curing composition which is said to be useful e.g. as a pressure sensitive adhesive or a sealant and which has good initial tackiness and heat resistance. The curing composition contains as effective components, (A) a polyether having in one molecule at least one functional group selected from a reactive silicon-containing group and an olefin group and (B) at least one specific vinyl polymer such as a homopolymer or copolymer with or without reactive silicon-containing groups in the side chain or an acrylate and/or methacrylate polymer with reactive silicon-containing groups in the polymer ends. JP-A-59 25 828 discloses a composition which is said to have improved adhesiveness after curing and is obtainable by blending polybutadiene or a copolymer consisting essentially of butadiene with a specific polyether polymer. EP-A-0 242 903 discloses a tackifier composition comprising, as essential components, (a) 100 parts by weight of polyether having at least one reactive silicon group and (b) from 10 to 140 parts by weight of a phenolic hydroxyl group containing cyclopentadiene resin. After a diligent study to ease the problem of tacky surface (to reduce the tack) of oxyalkylene polymers, the present inventors have achieved the objective of the present invention by admixing the polymer with a liquid 1,2-polybutadiene. The present invention relates, therefore to a curable composttion comprising 100 parts (by weight and the same hereinafter) of an oxyalkylene polymer having at least one silicon-containing group which has a hydroxyl or hydrolyzable group attached to the silicon atom and which is crosslinkable by forming a siloxane linkage and from 0.1 to 8 parts of a liquid 1,2 polybutadiene. An oxyalkylene polymer having at least one reactive silicon functional group in its molecule [this polymer is hereinafter referred to as oxyalkylene polymer (A)] is used in the present invention, and examples of oxyalkylene polymer (A) are proposed in US-A-3,971,751, 3,979,384, and 4,323,488, and JP-B-45-36319, JP-B-46-12154 and JP-B-49-32673, as well as in JP-A-50-156599, JP-A-51-73561, JP-A-54-6096, JP-A-55-82123, JP-A-55-123620, JP-A-55-125121, JP-A-55-131022, JP-A-55-135135 and JP-A-55-137129. (The terms "JP-A" and "JP-B" as used herein mean an "unexamined published Japanese patent application" and an "examined Japanese patent publication", respectively.) The molecular chain of the oxyalkylene polymer (A) preferably has a recurring unit that is represented by the general formula: -R¹-O- where R¹ is a divalent hydrocarbon group having 1 to 8 carbon atoms, preferably hydrocarbon groups having 3 or 4 carbon atoms. It is preferable that the sum of the recurring units: -R¹-O- oxyalkylene polymer (A) exceeds 50 wt%, specifically 70 wt% of said polymer. Specific examples of R¹ include: The molecular chain of the oxyalkylene polymer (A) may be composed of recurring units of a single type or two or more different types. A particularly preferred example of R¹ is The reactive silicon functional groups in oxyalkylene polymer (A) that are capable of crosslinking by forming siloxane bonds, are well-known in the art and are characterized by their ability to crosslink even at room temperature. Typical examples of such reactive silicon functional groups are represented by the general formula (I): where R² is a substituted or unsubstituted monovalent organic group having 1 to 20 carbon atoms which may be the same or different; X is a hydroxyl or hydrolyzable group and, in the case where two or more X groups are present, they may be the same or different; a is 0, or an integer of 1 or 2; b is 0, or an integer of 1, 2 or 3, with the proviso that (the sum of a and b)≧1 and preferably 1≦(the sum of a and b)≦4 ; and m is 0 or an integer of 1 to 18 or 19, however, not all of the m units are necessarily the same and a is not necessarily the same throughout the m units. Reactive silicon functional groups which are preferred for such reasons as economy are represented by the general formula (II) where R², X and b are the same as defined above. Specific examples of the hydroxyzable group X in the general formula (I) include a halogen atom, a hydrogen atom, a hydroxyl group, an alkoxy group, an acyloxy group, a ketoximate group, an amino group, an amido group, an acid amide group, an aminooxy group, a mercapto group and an alkenyloxy group. Among these examples, alkoxy groups such as methoxy and ethoxy are preferred since they will undergo mild hydrolysis. Specific examples of R² in the general formula (I) include alkyl groups having 1 to 20 carbon atoms such as methyl and ethyl; cycloalkyl groups having 3 to 20 carbon atoms such as cyclohexyl; aryl groups having 6 to 20 carbon atoms such as phenyl; and aralkyl groups having 7 to 20 carbon atoms such as benzyl. In formula (I) or (II) R² may be a triorganosiloxy group represented by the following general formula: (R′)₃SiO- where R′ is a substituted or unsubstituted monovalent organic group, preferably hydrocarbon groups having 1 to 20 carbon atoms, such as methyl group or phenyl group, provided that the three R′ are not necessarily the same. A particularly preferred example of R² in formula (I) or (II) is methyl. In order to ensure satisfactory curability, the oxyalkylene polymer (A) preferably contains at least 1, more preferably at least 1.1, and most preferably 1.5 to 4 reactive silicon functional groups on average. Such reactive silicon functional groups are preferably present at terminals of the molecular chain of the oxyalkylene polymer (A). The oxyalkylene polymer (A) has a number average molecular weight which preferably ranges from 500 to 30,000, more preferably from 3,000 to 15,000. Oxyalkylene polymers (A) may be used either alone or in combination. The oxyalkylene polymer (A) may be prepared by performing an addition reaction between a hydrosilyl compound having a structural formula with a hydrogen atom attached to the group represented by the general formula (I) and an oxyalkylene polymer having an olefin group represented by the general formula (III) (where R³ is a hydrogen atom or a substituted or unsubstituted monovalent organic group having 1 to 20 carbon atoms; R⁴ is a divalent organic group having 1 to 20 carbon atoms; and c is 0 or 1) in the presence of a catalyst, such as a platinum compound, made from a transition metal of group VIII. Other methods for preparing the oxyalkylene polymer (A) are described below: (1) reacting a hydroxyl-terminated polyoxyalkylene with a polyisocyanate compound such as toluene diisocyanate to form an isocyanate-terminated alkylene oxide polymer, and subsequently reacting the terminal isocyanate group with a W group in a silicon compound represented by general formula (IV): where W is an active hydrogen containing group selected from among a hydroxyl group, a carboxyl group, a mercapto group and an amino group (primary or secondary); and b, R², R⁴ and X are each the same as defined above; (2) performing an addition reaction between an olefin group in an olefin-containing polyoxyalkylene represented by formula (III) and a mercapto group in a silicon compound of formula (IV) where W is a mercapto group; and (3) reacting a hydroxyl group in a hydroxyl terminated polyoxyalkylene with a compound represented by general formula (V): where R², R⁴, X and b are each the same as defined above. It should, however, be noted that the oxyalkylene polymer (A) may be prepared by other methods. In the preparation of oxyalkylene polymer (A) a part or all of the X groups in the reactive silicon functional group may be converted to other hydrolyzable groups or a hydroxyl group. If X group is a halogen atom or hydrogen atom, it is preferably converted to an alkoxy, acyloxy, aminooxy, alkenyloxy, hydroxyl group, or some other groups. In the general formula (III), R³ is a hydrogen atom or a substituted. or unsubstituted monovalent organic group of 1 to 20 carbon atoms, and is preferably a hydrogen atom or a hydrocarbon group, with the former being particularly preferred. In formula (III), R⁴ is a divalent organic group having 1 to 20 carbon atoms, and is preferably -R⁵-, -R⁵OR⁵-, (where R⁵ is a hydrocarbon group having 1 to 10 carbon atoms), with methylene group being particularly preferred. The olefin containing alkylene oxide polymer may be prepared by various methods such as a method in which olefin groups are introduced to hydroxylterminated polyoxyalkylene by using ether, ester, urethane or carbonate linkage disclosed in JP-A-54-6097, and a method in which epoxy compound such as ethylene oxide or propylene oxide is polymerized with an olefin-containing epoxy compound such as allyl glycidyl ether producing an alkylene oxide polymer having an olefin-group in side chain. In the present invention, a liquid 1,2-polybutadiene is used to ease the problem that tack is apt to remain when an oxyalkylene polymer is cured. The liquid 1,2-polybutadiene contributes to the reduction of the remaining tack of the composition of the present invention, because a cured substance is formed by an oxidative crosslinking of the 1,2-polybutadiene by the action of air. Of the diene polymers, as compared with 1,4-polydiene, 1,2-polydiene has an advantage in that it does not cause phase separation during storage because of its better compatibility with an oxyalkylene polymer and that it contributes to a better weathering resistance without discoloration of the cured substance. The use ratio of a liquid 1,2-polybutadiene is, based on 100 parts of the oxyalkylene polymer (A) from 1 to 8 parts. Where the liquid 1,2-polybutadiene is used in amount of less than 0.1 part, the reduction of remaining tack that is the objective of using the liquid 1,2-polybutadiene is insufficient, whereas an amount of, in excess of 8 parts impairs tensile properties or weathering resistance, etc. of the cured substance. As for the manufacturing method of the present composition which comprises the oxyalkylene polymer (A) and a liquid 1,2-polybutadiene, there is no specific limitation. One of the examples is a mere addition of a liquid 1,2-polybutadiene to the oxyalkylene polymer (A). In this case, it is only required to obtain a uniform dispersion and dissolution of the two by adjusting conditions such as heating, stirring and the like depending on the properties of the liquid 1,2-polybutadiene. However, perfect transparency of the product is not necessary, because the objective is sufficiently achieved only if a uniform dispersion is obtained even though the product is nontransparent. Dispersion improving agents such as surface active agents may be used as such necessity arises. The other method of manufacturing the composition of the present invention is to admix a predetermined amount of a liquid 1,2-polybutadiene at the time of end use of the composition. For example, where the composition is used as a two-component sealant, the oxyalkylene polymer (A), liquid 1,2-polybutadiene, and, as a necessity, a curing catalyst are admixed at the time of application. Examples of curing catalysts which may be employed include titanates such as tetrabutyl titanate and tetrapropyl titanate; organo-tin compounds such as dibutyl tin dilaurate, dibutyl tin maleate, dibutyl tin diacetate, tin octylate and tin naphthenate; lead octylate; amine compounds such as butylamine, acylamine, dibutylamine, monoethanolamine, diethanolamine, triethanolamine, diethylenetriamine, triethylenetetramine, oleylamine, octylamine, cyclohexylamine, benzylamine, diethylaminopropylamine, xylylenediamine, triethylenediamine, guanidine, diphenylguanidine, 2,4,6-tris(dimethylaminomethyl)phenol, morpholine, N-methylmorpholine and 1,8-diazabicyclo(5,4,0)undecene-7(DBU) or salts thereof with carboxylic acid; lower molecular weight polyamide resins obtainable from excessive amounts of polyamines and polybasic acids; reaction products from excessive amounts of polyamines and epoxy compounds; amino group bearing silane coupling agents - i.e., known silanol condensation catalysts such as γ-aminopropyltrimethoxysilane, N-(β-aminoethyl)aminopropylmethyldimethoxysilane. These may be used alone or in combination. There may be added to the composition of the present invention an additive for improving tensile property, a reinforcing or non-reinforcing filler, a plasticizer, an adhesion promoter, an antisagging agent, a coloring material, an antioxidant, a flame retardant. Examples of the additives for improvement of tensile property include various silane coupling agents such as compounds which contribute to the reduction of the hardness and thereby to the elongation of the cured substance - i.e., a silicon compound having one silanol group in the molecule or a silicon compound capable of producing after hydrolysis a compound having one silanol group in the molecule, and which contributes to the increase of the hardness of the cured substance - i.e., a silicon compound having no less than three silanol groups in the molecule or a silicon compound capable of producing after hydrolysis a compound having no less than three silanol groups in the molecule. Other compounds usable as additive are functional group-bearing dialkoxysilanes such as dimethyldimethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, N-(β-aminoethyl)aminopropylmethyldimethoxysilane, γ-mercaptopropylmethyldimethoxysilane and the like, functional group-bearing diisopropenoxysilanes such as dimethyldiisopropenoxysilane, γ-glycidoxypropylmethyldiisopropenoxysilane, silicon varnishes and polysiloxanes, etc. Examples of the compounds which increase elongation while reducing hardness of cured substances include those disclosed in JP-A-61-34066, such as: Examples of the additives to increase the hardness of the cured substances include methyltrimethoxysilane, n-propyltrimethoxysilane, methyltriisopropenoxysilane, γ-glycidoxypropyltrimethoxysilane, vinyltrimethoxysilane, γ-aminopropyltrimethoxysilane and γ-mercaptopropyltrimethoxysilane, although the additives are not limited to those enumerated. Examples of the fillers are ordinary ones which include light and heavy calcium carbonates; calcium carbonates whose surface has been treated with such materials as fatty acids, resinous acids, cationic surface active agents, anionic surface active agents and the like; magnesium carbonate; talc; titanium dioxide; barium sulfate; alumina; powders of metals such as aluminium, zinc, iron; bentonite; kaoline clay; fumed silica; quartz powder; white carbon; carbon black; asbestos; and glass fiber. Sealants of excellent transparency can be obtained by use of transparent fillers such as fumed silica in particular. The above filler may be used alone or in combination. Examples of plasticizers which are used for adjustment of properties of the composition or the curred product of the composition include phthalates such as dibutylphthalate, diheptylphthalate, di(2-ethylhexyl)phthalate, butylbenzylphthalate and butylphthalylbutylglycolate; esters of dibasic non-aromatic acids such as dioctyladipate and dioctylsebacate; esters of polyalkylene glycols such as diethyleneglycol dibenzoate and triethyleneglycol dibenzoate; phosphates such as tricresyl phosphate and tributylphosphate; chlorinated paraffins; and hydrocarbon oils such as alkyldiphenyl and partially hydrogenated terphenyl. These may be used alone or in combination, but they are not essential. They may be incorporated at the time when the polymers are produced. Since the oxyalkylene polymer (A) itself has excellent adhesion to glass, other ceramics, and metals, and may be bonded to a further wide range of materials where primers are used, the addition of adhesion promoters is not essential. However, bond strength to other various substrates can be enhanced by use of, as an adhesion promoter, one or two or more of epoxy resins, phenolic resins, silane coupling agents already described as additives, alkyltitanates and aromatic polyisocyanates. Examples of antisagging agents include derivatives of hydrogenated castor oil, metallic soaps such as calcium stearate, aluminum stearate and barium stearate, although these are unnecessary depending on the purpose of use of the composition and fillers to be incorporated therein. Usable as the coloring materials are ordinary inorganic pigments, organic pigments, dyes. Usable as antioxidants are ordinary antioxidants and ultraviolet absorbers. For such purpose as improving workability or reducing the viscosity of the composition of the present invention, solvents may be incorporated, which include aromatic hydrocarbon solvents such as toluene and xylene; esters such as ethyl acetate, butyl acetate, amyl acetate and cellosolve acetate; and ketones such as methylethyl ketone, methylisobutyl ketone and diisobutyl ketone. Where the compound of the present invention is used, for example, as a sealant, the sealant may be prepared either as a one-component sealant wherein all the ingredients have been previously incorporated and kept in an air-tight container so that the composition cures after application by absorbing moisture from the air or as a two-component type which comprises a hardener component wherein ingredients such as curing catalysts, fillers, plasticizers and water have been admixed in advance so that said hardener component is mixed with the polymer component before application. In the case of a one-component type sealant, since all the ingredients are previously admixed, it is preferable that water-containing ingredients undergo pretreatment by water removal-drying before incorporation or by the water removal preformed in the stage of mixing-kneading by, for example, employing a vacuum. In the case of two-component type sealant, since curing catalysts are not admixed with the base component comprising the oxyalkylene polymer (A), the presence of some amount of water hardly causes gelation of the composition. However, for long time storage stability, it is preferable to carry out water removal drying of the ingredients. Suitable methods of water removing-drying for solid materials are heating and those for liquid materials are application of vacuum or use of chemicals such as synthetic zeolite, active alumina and silica gel. Otherwise, a small amount of an isocyanate compound is incorporated so that water is removed as a reaction product between the isocyanate compound and water. In addition to such water removing and drying methods, storage stability is further increased by incorporation of lower alcohols such as methanol and ethanol and of alkoxysilanes such as n-propyltrimethoxysilane, vinylmethyldimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, γ-mercaptopropylmethyldiethoxysilane and γ-glycidoxypropyltrimethoxysilane. The curable compositions obtainable in the above-mentioned manner are usable as adhesives, paints, sealants, water repellents, spraying materials, mold materials, casting rubbery materials, etc. Particularly useful is the application as a sealant. Illustrating the present invention in embodiments are the following examples and comparative examples. EXAMPLES 1 TO 8 AND COMPARATIVE EXAMPLE 1 100 g of a propylene oxide polymer having on average two methyldimethoxysilyl (-Si(CH₃)(OCH₃)₂) groups per one molecule and an average molecular weight of 9,600 was admixed with liquid 1,2-polybutadienes and the sensitizer (Irgacure-651) in amounts as shown in Table 1, then the mixture was further admixed with 150 g of a hard calcium carbonate (trade name "CCR" of Shiraishi Industry, Co., Ltd.), 65 g of dioctylphthalate, 1 g of an antioxidant based on a hindered phenolic compound (trade name "Nocrack NS-6 of Ohuchi Shinkoh Kagaku Co., Ltd.), 3 g of tin (II) octylate and 1 g of laurylamine. After sufficient mixing by 3-pass milling on a small roller for paint, the mixture was made into sheets of 3 mm in thickness. After cure at 23°C and 50% RH, the sheets were exposed outdoors (at an inclination of 45°C facing south) to observe the degree of dust collection. The remaining tack was evaluated by touch of finger on the surface of two series of samples of one day cure and 7-day cure each. The results of the Examples are shown in Table 1 together with the results of Comparative Example 1 where no liquid 1,2-polybutadiene was incorporated. In Table 1 NISSO PB B-1000 is a liquid 1,2-polybutadiene of a number average molecular weight of 1,050, NISSO®PB B-3000 is a liquid 1,2-polybutadiene of a number average molecular weight of 3,000, NISSO PB G-1000 is a liquid 1,2-polybutadiene of a number average molecular weight of 1,350 having hydroxyl groups at both ends, and NISSO®PB TE-2000 is a liquid 1,2-polybutadiene having ends modified with acrylic groups (all of which are manufactured by Nippon Soda Co., Ltd.). In Table 1, ratings of dust collection denote: A: Dust scarcely adheres, B: Dust slightly adheres, and C: Dust adheres; while ratings by touch of remaining tack denote: A: No tack at all, B: Slight tack, C: Tacky, and D: Very tacky. The results in Table 1 indicate that the incorporation of liquid 1,2-polybutadienes improve the properties with respect to dust collection and remaining tack. EXAMPLES 9 TO 16 AND COMPARATIVE EXAMPLE 2 The procedure of Examples 1 to 8 were repeated except that first 100 g of a mixture of a propylene oxide polymer having on average 2.7 dimethoxysilyl (Si(CH₃) (OCH₃)₂) groups per one molecule and an average molecular weight of 10,000 and 3 g of an additive, C₆H₅OSi(CH₃)₃, which decreases hardness and thereby increases elongation, was stirred for 2 hours at 80°C and then there were added to 100 g of said mixture liquid 1,2-polybutadienes and the sensitizer in amount as shown in Table 2. The results are shown in Table 2. The results in Table 2 indicate that the same improvements as in Examples 1 to 8 are still obtained despite incorporation of C₆H₅OSi(CH₃)₃.

Claims: A curable sealant composition comprising 100 parts by weight of an oxyalkylene polymer having at least one silicon-containing group which has a hydroxyl or hydrolyzable group attached to a silicon atom and which is crosslinkable by forming a siloxane linkage, and from 0.1 to 8 parts by weight of a liquid 1,2 polybutadiene. The composition of claim 1 wherein the oxyalkylene polymer has a main chain consisting essentially of a recurring unit represented by the formula: -R¹-O- where R¹ is a divalent hydrocarbon group having 1 to 8 carbon atoms. The composition of claim 1 wherein the silicon-containing group is represented by the general formula(I) wherein R² is a substituted or unsubstituted monovalent organic group having 1 to 20 carbon atoms, and in case two or more R² groups are present, they may be the same or different; X is a hydroxyl or hydrolyzable group, and in case two or more X groups are present, they may be the same or different; a is 0, 1 or 2; b is 0, 1, 2 or 3, with the proviso that (the sum or a and b )≧1 and that a is not necessarily the same throughout m units of the formula and m is 0 or an integer of 1 to 19 inclusive. A composition of claim 3 wherein X is selected from the group consisting of a hydrogen atom, a halogen atom, a hydroxyl group, an alkoxy group, an acyloxy group, a ketoximate group, an amino group, an amido group, an acid amide group, an aminooxy group, a mercapto group and an alkenyloxy group; and wherein, when two or more X groups are present, they may be the same or different. The composition of claim 3 wherein X of the general formula (I) is an alkoxy group. The composition of claim 3 wherein X in the general formula (I) is a methoxy group.

Inventors: HIROSE TOSHIFUMI, ISAYAMA KATSUHIKO, HIROSE, TOSHIFUMI, ISAYAMA, KATSUHIKO
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1988
Main classification: C08L71
IPC codes: C08L71