METHOD FOR MAKING MINERAL FILTRATION BEADS TO BE USED IN GEL ADSORPTION AND PERMEATION CHROMATOGRAPHY

Abstract: A mixture of silicon, zirconium, titanium and aluminum alkoxide is prehydrolyzed and dispersed into an aqueous phase in the form of droplets which gel and harden into porous glass beads by the addition of catalysts. The cross-section of the pores of the dried beads is normalized within relatively narrow statistical distribution ranges by infusing the pores with salts and heating the salt impregnated beads to 500-800°C for periods of time.

Description: The present invention relates to porous mineral beads of substantially uniform spherical shape which can be used in chromatographic separation and related techniques such as gel adsorption and permeation chromatography. These beads have a homogeneous metaloxane structure involving the oxides of metals silicon, zirconium, titanium and aluminum. It is well known that current organic porous filtrating materials usable in gel adsorption and permeation chromatography, for instance cross-linked dextrans (SEPHADEX), polyacrylamides, agarose, polyhydroxyacrylates, polystyrenes and others, cannot withstand relatively high filtration pressures because they tend to swell or shrink with consequent deterioration of the permeability parameters and loss of filtration efficiency (channelling). Now, for efficient chromatography separation as well as for the selective adsorption of biochemicals (enzymes, cells, hormones, lectins and others) low deformation materials are needed, preferably of spherical shape, to ensure homogeneous distribution and advantageously regenerable by thermal treatments. Consequently, mineral beads have been developed for this purpose, mainly silica beads with relatively well controlled size and porous structure. Such materials are, for instance, the filtering aids named in the trade as LICHROSORB (MERCK); TDK-Gel (TOYO SODA); SPHEROSIL (RHONE-POULENC) and Controlled Pore Glass (CPG by CORNING). These materials are generally manufactured by gelling-dispersive techniques starting from water-glass or colloïdal silica sols or by fusion of silicate batches. Methods also exist based on the prepolymerization of silicon alcoxides into liquid oligomers, pulverization or dispersion of said oligomers into droplets of controllable size and hardening of said droplets by hydrolytic gelation into porous SiO₂ beads. References on these methods are for instance: R. ENDELE et al., J of Chromatography 99 (1974), 377-393; USP 3,667.909 (THOMAS); KOHLSCHUTTER et al., Kolloid Zeitsch. & Zeitsch. für Polymere 243 (1971), 148-152; DE-A- 2 155 281 (MERCK). Although beads of porous silica presently on the market have merits, they are costly, sometimes lack homogeneity in shape (spherical), size and porosity and they are not stable in alkali (pH > 10). Therefore attempts have been made to provide porous composite minerals having improved stability in basic media. For instance, DE-A-2.317.455 discloses powders for packing chromatography columns consisting of porous microspheres (1-10 µm) with a thermally stable metal oxide such as Al₂O₃, ZrO₂, TiO₂, Fe₂O₃ or SnO₂ on the surface. DE-A-2.411.846 discloses the existence of Al₂O₃ microspheres obtained by agglomeration and firing of alumina particles resulting from the spray-dehydration of acidified aluminate solutions. On the other hand, porous SiO₂ or mixed metal oxides are well known which can be prepared, as already mentioned, by the technique called "sol-gel hydrolysis" which involves control-hydrolyzing metal alkoxides into corresponding hydroxylated compounds and subsequent self-condensation to metaloxane structures by dehydration and heat. For instance, JP-A-58-194.748 (SUWA SEIKOSHA) discloses the hydrolysis of metal alkoxy compounds by the sol-gel process and the conversion of the gelled products by heat into microporous structures. suitable for use as carrier for enzymes and others living materials. Other references in the field of porous glass for various purposes including filtration media and the manufacturing of optical glass are: JP-A-58-208.144; 58-213.655; 58-199.734; 58-199.733; 58-194.749 (all to SUWA SEIKOSHA); JP-A-56-169.121 (HITACHI); JP-A-57-190.645 (TOYOBO); JP-A-57-191.220 (HITACHI); H. MURAYAMA et al., Shikizai Kyokaishi 1973 , 46 (7), 439-44; B.E. YOLDAS, J. Am Ceram. Soc 1982 , 65 (8), 387-93; Ultrastruct. Process. Ceram., Glasses Compos. (Proc. Int. Conf.) 1983 60-69. D.R. WILEY, New-york; E. YASUDA et al., Sci. Sintering 1978 , 10 (2), 97-102; M.A. VICARINI et al., Bull. Soc. Chem. Fr. 1970 (10), 3884-7. Further references on filtration beads are outlined below. EP-A-65863 discloses a method of producing ceramic-forming metal hydroxide and oxide powders with variable and predeterminable sintering and densifying characteristics by hydrolyzing several samples of metal alkoxides using different amounts of water, calcining and sintering said hydrolyzed samples to produce samples of said metal oxide powder, and measuring the density of said samples of said metal oxide to obtain the relationship between said density and the water-alkoxide ratio. Then, after selecting the sintered density desired, hydrolyzing said alkoxide with the amount of water which corresponds to said desired sintered density to form said metal hydroxide, and drying said metal hydroxide it is possible to form said desired metal hydroxide powder; if an oxide powder is desired, heating said metal hydroxide powder to form said metal oxide powder can then be performed. WO-A-8303823 discloses a method for preparing a ceramic material comprising a metal oxide, said method including ball milling a metal oxide powder and sintering said metal oxide powder. The latter is obtained by hydrolyzing at least one alkoxide to form a slurry, drying the metal oxide powder in said slurry, granulating and calcining, and conducting said ball milling within a determined pH range that maximizes dispersion of metal oxide powder within the slurry. Kolloid Zeitschrift & Zeitschrift für Polymere 243 (1971), 148-152 discloses a method for making porous beads from silica. According to this method, a mother solution is prepared from silica ethoxide, diluted with N/100 hydrochloric acid and alcohol; then after a preliminary hydrolysis has taken place, the solution is heated to 120° to drive off volatiles and there is obtained a solution (of oligomers) in which 1 to 4 ethoxy groups per Si atom have been split. This solution is stable and reproducible. It was converted, immediately afterwards, into beads by adding it under violent strirring to an ethanol-water solution activated with N/10 HCl. After agitating several hours at 70°C, the beads were boiled with diluted HCl, thoroughly washed with water, predried in air and finally dried at 120°C. Depending on preparation parameters, a full range of beads of size from 10 µm to 1 mm were obtained. Typical bead properties (very briefly summarized) were: distribution of preferred size in classified fraction: 90%; structure density: 2.04 g/ml; porosity 0.373; specific area 682 m²/g (BET); volume of pores: 0.29 ml/g; average pore diameter 20 × 10⁻¹⁰m (Å); etc.... US-A-3922333 discloses the preparation of mullite powder by boiling a mixture of aluminum and silicon isopropoxides in isopropanol in the presence of ammonium hydroxide. The powder can be thereafter sintered by hot pressing into objects of near theoretical density usable as catalyst bases. US-A-3887692 discloses the preparation of spheroids of aluminum halo-hydroxides as an antiperspirant component. One useful dispersion technique, i.e. the discharging of very fine droplets of a basic aluminum halide solution into the vortex of an insolubilisation dispersant medium is detailed in this reference. EP-A-216730 (BATTELLE) discloses the preparation of porous mineral beads containing at least the oxides of Si and Zr and, optionally, oxides of other metals including aluminum and titanium. One technique of manufacturing these beads involves the initial preparation of metaloxane oligomer precursor solutions by the controlled prehydrolysis of metal alkoxides in acidified moistened alkanol solutions and elimination of volatiles by boiling under reduced pressure. Then the precursors (which are actually storage stable) are formed into droplets, for instance by dispersion into an aqueous non-compatible medium, or by air atomization, and the droplets are gelled into beads which are further hardened by pursuing hydrolysis and self-condensation under the influence of catalysts such as aqueous ammonia. Beads in the 5-500 µm range with a porosity of 100-600 m²/g (pores volumes 0.2 to 4 cm³/g) and pore cross-sectional sizes of about 2-500 nm were achievable by this technique. Document EP-A-216730 also discloses that the porosity of the filtration beads can be amplified by refluxing the beads with aqueous-alcoholic alkali. Although the porous mineral beads disclosed in EP-A216730 have a lot of merit, it was felt that further improvements could be brought thereto namely regarding pore cross-sectional radius distribution. Indeed, for most fine and sensitive affinity chromatography applications, using beads with a narrow pore cross-sectional size distribution is an important asset. After painstaking efforts, the present inventor uncovered a method capable of providing porous beads with much improved control of pore size distribution. This method is summarized in annexed claim 1. The proportion of Zr, Ti and Al compounds added to the silicon alkoxide are variable within wide limits, usually from 0.03 to 1.5 moles of the three Zr, Ti and Al together for 1 mole of Si. In this range, the proportion of one of the Zr, Ti or Al relative to the others can be the same or different. One preferred composition comprises (expressed in weight % of the oxides): SiO₂ 85; ZrO₂ 5; TiO₂ 5; Al₂O₃ 5. The alkoxides of silicon, zirconium, titanium and aluminum used in this method are generally the lower alkoxides and complex chelates used commonly in sol-gel technology. Among such compounds, the methoxides, ethoxides, propoxides, isopropoxides, butoxides (n, iso and tert) and other alkoxides (C₁ to C₈) can be recited, not excluding other higher alkoxides. The aluminum compounds are advantageously the bi-dentate chelate of Al-alkoxides, e.g. acetyl-acetonate or aceto-acetate of Al-dialkoxides, e.g. the di-sec.butoxide. Steps (a) and (b) of claim 1 are preferably carried out in a water-alkanol solution, i.e. a solution of water in one or more lower alcohols such as methanol, ethanol, propanol, isopropanol, butanol (n, iso, tert), and the like. The proportion of the water and the organic component in this medium is essentially variable and not critical since other parameters like acid concentration, temperature and time can be adjusted separately to provide a desired degree of prehydrolysis and self-condensation. In general, the prehydrolysis solution contains from about 0.05 to 1.5 moles of water per mole of silicon alkoxide. The acid used to acidify the solution is a mineral acid, preferably hydrochloric acid. As said before, depending upon the prehydrolysis conditions, i.e. time, temperature, concentration of water, amount of acid catalyst, the degree of prehydrolysis can be varied at will. The viscosity of the precursor solution (i.e. the solution of prehydrolysed oligomeric metaloxane) increases with increased extent of hydrolysis, for instance by increasing the water concentration, the heating temperature and the reaction time. It is generally assumed that the degree of prehydrolysis involved in precursor formation affects about 2 to 50 moles % of the originally mixed metal alkoxides. On the higher end of this range, the precursor may become very viscous or even solidify after substantially all volatile components (alcohol, water) have been removed by distillation. An inverse relation seems to exist between the amount of water used in the prehydrolysis step and the porosity of the beads manufactured from the prehydrolyzed material: the smaller the quantity of water used, (and the degree of prehydrolysis) the larger the volume of the pores. The precursors are stable and can be stored without gelling for an extended period. To be used in step (c) the precursor solution is diluted in a water-compatible solvent, e.g. one or more lower alcohols such as methanol, ethanol, propanol, butanol, amyl alcohol (and isomers thereof), and the like, and water soluble solvents like acetone,THF, dioxane, diols, glymes, etc...; this dilution also contains a non-water compatible solvent such as hydrophobic hydrocarbons like hexane, heptane, octane, benzene, toluene, xylene, etc... Cyclohexane is preferred. The proportions of precursor, water-compatible and hydrophobic solvents are chosen to achieve free flowability of the solution and favorable dispersability into droplets when added to a large volume of water in agitation. Preferably the dilution will contain about 1-2 parts (v/v) of diluting mixture for about 0.1 to 10 parts of the oligomeric precursor. However these limits are not critical and can be outstretched on both ends of the range. In step (c), the dilution of the precursor is dispersed in a large volume of water-ethanol mixture which can also contain additives which help controlling the conversion of the oligomers into small spherical droplets upon dispersion into water. These additives include ionic and non-ionic surfactants like polyoxyethylene glycol sorbitan-monolaurate, sodium-lauryl sulfate and the like. Preferred surfactants are the Tween® -like surfactants added to the water-alcohol dispersive mixture in about 0.1-1% by weight. The amount of alcohol (methanol, ethanol or isopropanol) in the alcohol-water dispersive mixture is from about 0.1 parts to 2 parts (v/v) of alcohol for 10 parts of water. The proportion (v/v) of the dilution of oligomeric precursor to the alkanol-water dispersive mixture into which it is added is in the range of 1: 100 to 1: 2, preferably 1: 5 to 1: 20. This addition is preferably performed dropwise at room temperature, the dispersive aqueous solution being stirred at from about 300 to 1000 rpm with non-turbulent agitation. When the oligomer dilution is added slowly this way, microdroplets of uniform size, 1-200 µm, preferably 10-100 µm diameter, will form and become gelled and hardened to corresponding porous glassy microsphere, either by raising the temperature of the dispersing medium to about 60-65° or by the addition of gelling catalysts. The preferred catalyst is diluted ammonia, i.e. (considering that ordinary commercial concentrated ammonia is 25%) ammonia solutions ranging from about 5 to 25% added in amounts, relative to the dispersion, of 1 part to 10 parts of ammonia solution for 20 parts of the dispersion. Generally the catalyst solution is added dropwise under agitation and after the addition is complete, agitation is pursued for one to several hours, after which the dispersion is allowed to stand and the porous glass spherical beads accumulate to the bottom of the dispersion container. For separating the beads from the dispersing phase and obtaining them in dry form, the first operation is decanting and washing, i.e. syphoning off the supernatant liquid which is normally cloudy because of the presence of unsettled sub-micronic particles, then adding a washing or rinsing liquid (usually an alcohol), allowing to decant again, and repeating once or more this purification stage. Then several drying routes are available: for instance the beads can be simply filtered and drained under suction; or the slurry of beads and washing liquid can be roto-evaporated (under reduced pressure and progressive heating) or the technique of hypercritical drying can be used. Hypercritical drying consists in effecting the drying under high pressure and temperature in an atmosphere of alcohol or CO₂ vapor. This is disclosed in detail in US-A-4,667,417. In the corresponding embodiment of the instant method, the liquid forming the slurry of beads before drying is progressively replaced by ethanol in a pressure vessel. Then the vessel is filled with an inert gas, e.g. N₂ or Ar, and the gas pressure is raised to a pressure of 50-100 bar at room temperature; subsequently, the temperature is raised to 200-350°C until the pressure exceeds the critical point, which means that the liquid in the bead pores is converted to the critical state (this occurs within the pores themselves with no pressure difference between the outside and the inside of the pores which strongly reduces the risks of bead fracture). This pressure may range for alcohol from about 180-250 bar. After standing a while under these conditions, the autoclave is depressurized slowly, i.e. at a rate of 1-50 bar/hr until it is 5 bar. Then the temperature is lowered to normal and the dry beads can be removed from the vessel. In a variant, CO₂ can be used in place of alcohol for hypercritical drying, in conformity with US-A-4,667,417. The volume of the pores of the beads dried according to the foregoing routes is generally above 1 cm³/g of material; in some cases, it may be as high as 4 cm³/g, this being particularly so for the beads that result from the processing of precursors which were prehydrolyzed with relatively little water (0.1 to 0.3 moles of H₂O per mole of Si(OET)₄; see Tables II and III in the Experimental section hereafter). However, the cross-sectional size of the pores is rather widely distributed. This may be appreciated from the annexed drawings in which: Fig 1 is a graph in which the cross-dimensional size of the pores (radii) expressed in angströms (X axis) is plotted against their relative occurrence given by the statistical pore distribution expressed in % (Y axis). Fig 2 is a graph similar to that of fig 1 but pertaining to the bead having been subjected to step (f), i.e. salt impregnation of the instant invention. It can be seen that the curves A, B, and C fig 1 (for details, see the Experimental part) which refer to three different kind of beads obtained after step (e) are not far from straight lines, which means that no particular size of pores is favored within the radii of about 150 to 3000 Å (15-300 nm). In order to narrow the pore size distribution, the beads resulting from step (e) are subjected to salt impregnation and heating according to step (f), then washed according to step (g). The salts used in step (g) are selected from halides and chalcogenides of metals of groups I, II and III of the Periodic Table; they preferably include NaCl, BACl₂, CaCl₂ and Al₂(SO₄)₃. Normally the beads are infused with aqueous solutions of these salts and then dried to remove the water at from about 90-150°C at ambient pressure or under vacuum. The concentration of said aqueous solutions may be between from about 5% to 30% by weight. Since the aim is to obtain beads with pores containing dry salts in a proportion ranging from about 20 to 95% by weight (expressed as weight of salt per weight of beads + salt), the amount of aqueous solutions used for infusion depends on the salt concentration in said solution, much of it relative to the beads being used if the concentration is low, and less of it if the concentration is high. In some cases two or more salts were used simultaneously (see Table IV thereafter). Usually, depending on intrinsic solubility of the salts in water, weight ratio of dried beads to salts used for impregnation range from about 0.05 to 4.5. Once the beads impregnated with the salts are fully dry, they are subjected to heating under air in a furnace, the rate of heating is about 1-10°C/min up to a temperature of about 600-800°C. Then the temperature is maintained for one or several hours (e.g. 1-6 hrs), knowing that long heating times increase the occurrence of pores in the 10-50 nm (100-500 A) range, and the whole is allowed to cool. Removal of the salts is effected by repeated washing with water, either at room temperature or at the boil until no salt is present in the pores. After salt removal, the beads are again dried in air at 100-200°C. Heating treatments to 750°C or more may result in a degree of pore collapsing due to glass densification unless some special treatments such as hydrothermal or oxidation with halogen or oxygen are applied. Fig 2 illustrates the effect of the salt heat treatment. Curve D represents the pore size distribution for a given kind of bead material and curve S5 represents the pore size distribution for the same material after 4 hrs at 750°C in the presence of more than 90% of salt. Obviously normalization of the pore size in the 50-60 nm (500-600 angstrom) range has occurred to a considerable extent. It is also interesting to note that the pores of a given size may not be distributed regularly in the bead body; actually, the larger pores are generally found in the beads near to their periphery, smaller pores being rather concentrated near the center. In addition to the carrying out of the various steps and modifications disclosed in connection with the method of the invention (see claim 1), the present beads can be subjected to additional treatment for improving their properties. For instance, they can be dehydroxylated by heating with chlorine/inert gases mixtures. Dehydroxylation may be important to decrease the tendency to pore collapsing at high temperature upon heating to promote crystallization to a glass-ceramic structure. Such structure is advantageous for use of the beads as chromatographic materials. Conditions for chlorine treatments are detailed in the experimental part. Other final treatments involve hydrothermal treatments, i.e. using water diluted mineral acid and bases under ambient conditions or moderate temperature and pressure conditions. Details about such further treatments are given in the experimental part which follows. Experimental Section (Examples) i) Preparation of oligomeric metaloxane precursors Silicon tetraethoxide (500 g, 2.4 moles) was dissolved in 136.3 g ETOH and 18.7 g of 0.1 HCl in ethanol (2.4 mmoles) and 8.64 g H₂O (0.5 moles) were successively added under stirring. Prehydrolysis of the silicon ethoxide was initiated by heating the solution (solution A) to 60°C for 1/2 hr after which it was cooled to about 0°C. A solution B was prepared by admixing successively under P₂O₅ dry nitrogen (glove box): 29.08 g (0.1 mole) of zirconium isopropoxide, 24.21 g (0.1 mole) of titanium tetraethoxide, 50.28 g of aluminum di-sec.butoxide-ethyl-acetoacetate, 20 g of ethanol and 20 g of isopropanol. The solution was heated to reflux for 15 min after which it was cooled to about 0°C and mixed with solution A. The overall solution A + B was heated progressively to 130° under a stream of nitrogen, whereby distillation occurred; water distilled off together with the volatile solvents to provide 552.7 g of prehydrolyzed oligomeric solution labeled PG3 (7). The above preparation was repeated using variable amounts of water for prehydrolysis. The products obtained are listed in the Table below (Table 1). Note that in all cases, the respective weight proportions of the metal components (expressed as their oxides SiO₂, ZrO₂, TiO₂ and Al₂O₃) were 85: 5: 5: 5. ii) Preparation of metaloxane beads by dispersing the precursor solution into insolubilizing media to form oligomer droplets which are subsequently gelled and hardened. A volume of 75 ml of precursor solution (PG3) was diluted with 56.3 mil of tert.amyl-alcohol (tam) and 18.8 ml of cyclo-hexane. This was slowly added dropwise at room temperature to an agitated solution (650-800 rpm) of 1300 g of water, 20 ml of Tween-20 (or 40) surfactant solution and 15 ml of ethanol which had been premixed beforehand for about 15 min. This addition resulted in the formation of a suspension of droplets (milky suspension) which was left under agitation for about 5-10 min to homogeneize. Then a diluted aqueous ammonia solution was added under stirring in 40 min to promote gelation of the droplets into beads and, afterwards, stirring was continued for 1-6 hours to complete bead hardening. Table II below shows the conditions under which this bead formation was brought about, i.e. the kind of precursor PG3 used (see Table I) and the quantity of ammonia (25% solution) and water added to effect gelation and hardening, the last column identifies by a code the hardened bead material obtained. The suspension of hardened beads was allowed to stand overnight and the supernatant liquid (cloudy) was syphoned off and replaced by ethanol. This decanting, syphoning and rinsing with ethanol was repeated twice. iii) Drying of the beads (hypercritical drying) After decanting the alcohol wash for the third time, the mass of beads was moistened with alcohol into a paste-like slurry. This slurry was placed in an autoclave which was filled with N₂ up to a pressure of 80-90 bar at 20°C. Then the autoclave was heated at a rate of 1.5°C/min up to 280°C (about 1-1.5 hrs) whereby the pressure rose to about 210-230 bar. After 1 hr standing under the above conditions, the autoclave was decompressed at 280°C at a rate between about 1-50 bar/hr until the residual pressure was 5 bar. Then it was allowed to cool to room temperature whereby the pressure was relieved. The beads obtained were substantially spherical with a diameter generally ranging from about 10 to 100 µm. Alternatively, the bead material was vacuum-dried in a rotavapor apparatus or drained on filter papers under suction. Table III summarizes the values of the pores volumes measured on some of the beads listed in Table II after hypercritical drying. The pores volumes were measured either with a Carlo ERBA porosimeter type AG/65 (mercury intrusion technique) from Carlo ERBA S.p.A., Milano, Italy, or by isopropanol infusion technique via a micropipette; the end point (occurrence of tacking) was however difficult to determine and required much experimentation and skill. Table III also gives pore volume values for some of the bead samples after being subjected to a post-drying heating period in air at 700-750°C. The values within brackets include the "dead" pore volume recorded initially in each measurement. The statistical distribution of the pore volumes for bead samples s01 (curve A), s01 after heat treatment (curve B) and s02 after heat treatment (curve C) is shown in fig 1. In fig 1 the "X" axis indicates the pore volumes on a logarithmic scale and the "Y" axis indicates the percent pore volume distribution. Therefore curves A, B and C correlate the relative proportion of pore volumes with a given range of values. It can be seen that the distribution is rather linear, i.e. there is practically no range of pore volumes which is favored at this stage. iv) Impregnation with salts and heat treatment. In these experiments, a given weight of beads was impregnated with an aqueous solution of salt of concentration 5-30% by weight and thereafter fully dried (90-150°C). Then the impregnated beads were placed in a horizontal tube-furnace (alumina boat) and heated in air (rate 1°C/min) up to a maximal temperature (680-800°C), left there for a period (2-4 h) and allowed to cool. Then the beads were washed repeatedly with water (boiling water or 20°C water) until all salts had been removed, after which the beads were dried again in air and the porosity measured. Table IV below summarizes some of the results. In some cases the beads were degassed at 150°C under vacuum; these are marked "dg". Table II successively indicates a "S" (salt) code number defining the experiment, the code for the beads used, the salt(s) used for impregnation and weight % and temperature of the heat treatment. Fig 2 shows on the same type of diagram as fig 1 the results of the salt impregnation heat treatment on the pores radius distribution. Curve D represents the case of the p02 beads before salt impregnation; curve S5 represents the S5 experiment reported in Table IV, i.e. the p02 beads subjected to 4 h of heating at 750° with 92,5% of salt. It can be seen that after the treatment about 50% of the pores are in the 25-80 nm (250-800) Å range. Curve S12 illustrates the results of experiment S12 in Table IV. Table V summarizes the pore size distribution in % for a given pore radius range, for a number of samples having undergone salt impregnation. The table also gives the corresponding pore volumes and the specific surface area of the beads From the above results, it can be seen that using high temperatures and prolonged heating in the salt impregnation treatment tends to bring the pore cross-sectional sizes in the 10-50 nm (100-500 Å) range. v) Hydrothermal treatments. In order to further decrease the affinity of the present beads toward biological molecules and reduce the adsorption capacity, lots were heated under nitrogen pressure for 2-6 hrs with moist alcohol optionally containing small amounts of reactive minerals such as HCl, NaOH or HF. The initial pressures ranged from about 15-150 bar, the heating temperatures from 120 to 250°C and the pressures at heating temperatures from about 40 to 250 bar. As an Example, beads v01 (9 g) were heated for 2 hours at 200°C with 150 ml of H₂O under 200 bar. After this treatment, the adsorption of blue dextran or human serum albumin (HSA) was less than 4%; the adsorption of phenol was zero. The adsorption capacity was also strongly reduced by NaOH treatment at room temperature. For instance v02 beads with pores normalized by treatment with NaCl at 700°C (see S32 in Table IV) had an adsorption capacity of 51% for HSA. This was reduced to 14% after treatment of the beads with 0.1N NaOH at room temperature. vi) Dehydroxylation by chlorine-argon mixture of hyper-critically dried beads. The samples were heated in tube-furnaces either in air or under a mixture of chlorine gas and argon according to the heating treatment programmes listed below (HT2, HT3, HT4). Table VI summarizes the results obtained from the dehydroxylation treatment in this Table, the pore volumes are reported as in Table III. It should be first noted that heating the present beads to temperatures of 800-1000° normally leads to a considerable degree of densification and pore plugging. The present chlorine treatment (terminated on one occasion by an oxidizing treatment; see HT4 last step) obviates this drawback. Instead, the beads will crystallize to same extent around 1000°C into a glass-ceramic material, the porosity not being substantially altered.

Claims: 1. A method for making porous mineral beads suitable for chromatographic separation techniques of substantially uniform spherical shape and controlled pore radius distribution and having a homogeneous metaloxane structure involving the oxides of the metals silicon, zirconium, titanium and aluminum, which comprises the steps of: a) dissolving an alkoxide of silicon in an acidified aqueous-organic solvent mixture and effecting a prehydrolysis of the silicon compound; b) adding thereto a solution of alkoxides of Zr, Ti and Al in a water-soluble organic solvent and subjecting the whole mixture to heat and distillation until substantially all volatiles components thereof have been removed, whereby a metaloxane precursor solution is obtained; c) diluting the precursor solution with a solution of a water compatible organic solvent and a water-insoluble hydro-carbon soluble in said compatible organic solvent and slurrying this dilution into droplets by adding it into an excess of an aqueous phase; d) converting said droplets into spherical gelled beads by heating to 40-65°C, or adding ammonia to the slurry, whereby hydrolysis is resumed with consequent formation of a gelled metaloxane structure; e) drying the gelled beads at room or higher temperatures, whereby highly porous dried beads are obtained with pore volumes greater than 1 cc g⁻¹; f) infusing into the pores of the dried beads an aqueous solution of a water-soluble mineral salt selected from halides and chalcogenides of metals of columns I, II and III of the Periodic Table and heating the impregnated beads at temperatures from 500 to 800°C. g) treating the beads with water to wash off the salts and isolating the washed beads. 2. The method of claim 1, in which the mole quantities of the Zr, Ti and Al components for one mole of silicon component, are in the range of 0.03 to 1.5 moles. 3. The method of claim 1, in which the alkoxides are lower alkoxides selected from methyl, ethyl, propyl, isopropyl and butyl alkoxides. 4. The method of claim 3, in which the Al compound is selected from aceto-acetate chelates of Al-di- (sec.alkoxides), and bidentate chelates of Al-di-(alkoxides). 5. The method of claim 1, in which the prehydrolysing aqueous organic solvent in step (a) is an aqueous lower alcohol solution acidified with hydrogen chloride. 6. The method of claim 5, in which the mole ratio of the water in the acidified aqueous alcohol solution to the total of the silicon alkoxide is 0.05 to 1.5. 7. The method of claim 1, in which the degree of prehydrolysis of the metal alkoxides achieved in step b) expressed in mole % is from 2 to 50. 8. The method of claim 1, in step c) of which 1 to 2 parts (v/v) of diluting mixture is used for 0.1 to 10 parts of the precursor solution. 9. The method of claim 8, in which the diluting mixture contains tert.amyl alcohol and other hydrophilic solvents, and organic hydrophobic solvents. 10. The method of claim 1, in step c) of which the aqueous phase is a water or a water solution of a lower alcohol containing surfactant agents like polyoxyethylene sorbitanmonolaurate and related compounds permitting the formation of perfectly spherical droplets. 11. The method of claim 10, in which the volume ratio of the diluted precursor to the aqueous phase is 1/5 to 1/20. 12. The method of claim 1, in which the volume ratio of the ammonia solution used in step d) and the diluted precursor is between 0 and 3. 13. The method of claim 1, in which step e) is effected under hypercritical drying conditions under pressures ranging from 100 to 250 bar. 14. The method of claim 1, in which step e) is effected under atmospheric pressure. 15. The method of claim 13, in which step e) is effected under an atmosphere of alcohol or CO₂. 16. The method of claim 13, in which the temperature in step e) is between 200 and 350°C. 17. The method of claim 16, in which, after maintaining the temperature and pressure for 0.5 to 2 hrs, the pressure is relieved at a rate of 1 to 50 bar/hr until it is 5 bar, after which the temperature is lowered to room temperature. 18. The method of claim 1, in which the concentration of the solution of salts used in step f) is between 5 and 30% by weight. 19. The method of claim 18, in which the salts used are selected from NaCl, BaCl₂, CaCl₂ and Al₂(SO₄)₃. 20. The method of claim 18, in which the impregnated porous beads are heated at the rate of 1-10°C/min in air. 21. The method of claim 18, in which, prior to impregnation, the beads are dried between 90 and 150°C under pressure ranging from 0.013-1.013 bar (10 to 760 Torr). 22. The method of claim 18, in which the weight ratio (I) of dried beads before impregnation to that of the salts, taken as in the dry state, is from 0.05 to 4.5. 23. The method of claim 22, in which beads having pores ranging from about 10-4,000 nm (100 to 40.000 Å) in random distribution are impregnated with aqueous NaCl, (I) being 0.082, then heated 4 hrs at 750°C, then cooled and washed with H₂O, whereby the porous structure now has about 60% of pores in the 35-50 nm (350-500 Å) range. 24. The method of claim 1, in which increasing heating time and temperature in step f) tends to increase the amount of pores in the 10-50 nm (100-500 Å) range. 25. The method of claim 1, in which the pore radii follow a radial distribution in the beads, the larger pores being near the periphery. 26. The method of claim 1, in which the average pore radii before salt impregnation is a function of prehydrolysis conditions pertaining to steps a) and b), the magnitude of pore size being inversely related to the amount of water added in step a). 27. The method of claim 1, whereby after step g) the dried products having defined pore radii are subjected to chlorine gas treatment at temperature in the range 500 to 1200°C to reduce the OH content at the surface of the pores. 28. The method of claim 1, whereby after step g) the dried products are subjected to aqueous hydrothermal treatment at pressures between 9.08-318 bar (10 and 350 atm) and at temperatures between 100 and 350°C to modify the OH content and metaloxane configuration at the pore surfaces. 29. The method of claims 1 and 27, whereby a final heating schedule (500 to 1200°C) is implemented for sufficient time to induce crystallization of the glass matrix, giving a glass-ceramic material, without significantly reducing the pore radius and the pore volume.

Inventors: GONZALEZ OLIVER, CARLOS
Applicants: BATTELLE MEMORIAL INSTITUTE
Application year: 1988
Main classification: B01J20
IPC codes: B01J20, G01N30, C01B33