Aromatic sulfideamide polymer and method for producing the same

Abstract: A class of amide group-containing aromatic dihalide compounds are sulfidized together with a class of aromatic dihalide compounds to provide a novel class of aromatic sulfideamide polymers increased in crystalline melting point (T m ). The polymers exhibit excellent resistance to high temperatures, resistance to solvents, flame-retardant properties and improved mechanical properties.

Description: This invention relates to a novel crystalline aromatic sulfideamide polymer and a process for production of the novel polymer. The polymers according to the invention have a chemical structure in which phenylene and alkylene groups are alternately bonded via an amide group and a thioether group. The polymers are useful as materials for producing articles exhibiting improved properties such as excellent resistance to high temperatures, flame-retardant properties, resistance to solvents, good mechanical properties, good fabricability, etc. Polyphenylene sulfide which is a polymeric compound comprising phenylene groups linked to each other via a thioether group is well known in the art. This polymer has such properties as good flame-retardancy, low moisture absorption, high dimensional stability, etc. However, since this type of polymer exhibits a relatively low heat distortion temperature (HDT) of 260°C (GF 40%; i.e. containing 40% glass fibers) and a crystalline melting point (T m ) of 281°C, its usefulness in applications where high resistance to heat is required is inevitably limited. Consequently there has been a demand in the art for the development of polyphenylene sulfide materials having further crystalline melting points. A polymer substance containing thioether, phenylene and amide groups in the macromolecular backbone, i.e. a polymer of aromatic polythioether amide, and a process for production thereof are described in JP-A-60-226528. This polymer substance presents some problems in practice because it has a rather low softening point, is soluble in organic solvents such as dimethyl sulfoxide of N-methyl-2-pyrrolidone and exhibits poor resistance to chemicals. Additionally the synthesis of thiol group-containing monomers to be used in the preparation of the polymer is so expensive that production of the polymer is not feasible from an economic point of view. It is also possible to synthesize a similar polymer from an amide group-containing aromatic dihalide compound and a sulfidizing agent. However, there are problems, such as that the resulting aromatic sulfideamide polymer itself has a too high melting point to be melt processed in the neat stage. The article (hereafter Daccord) by G. Daccord and B. Sillion, Die Makromolekulane Chemise , 1983, 184 , p.1861-1867, at page 1862 describes polymers 7a and 7b which are made from aliphatic dicarboxylic acids and aromatic amines which bear sulphide groups. The polymers of the present invention use cyclic nitrogen compounds in place of the aliphatic dicarboxylic acids of Daccord. These polymers have particularly advantageous thermal properties. An object of the present invention, therefore, is to provide a novel aromatic sulfideamide polymer substance comprising a commercially available, inexpensive aliphatic moiety in the repeating units and which is improved in terms of resistance to high temperatures, resistance to solvents and mechanical properties, and good fabricability. A further object of the present invention is to provide a process for production of such a novel polymer substance. According to one aspect of the present invention, there is provided a novel aromatic sulfideamide polymer which consists of from 1 to 99 mol% of repeating units represented by the following formula (I) : and from 99 to 1 mol% of repeating units represented by the formula (II): -[Ar³(R³) c -S]- (II) in these formulae Ar¹, Ar² and Ar³ which may be the same or different, each represent an aromatic ring; R¹, R² and R³, which may be the same or different, each represent an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group having 3 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, an acyl group having 2 to 20 carbon atoms or an arylalkyl group having 7 to 20 carbon atoms; a, b and c, which may be the same or different, each represent an integer of from 0 to 4; and R⁴ and R⁵, which may be the same or different, each represent an alkylene group having 1 to 20 carbon atoms, said polymer preferably having a logarithmic viscosity [η] of 0.02 to 2.00, as determined by measuring the relative viscosity of polymer dissolved in concentrated sulfuric acid at 30°C and at a polymer concentration of 0.5 g/100 ml or the relative viscosity of polymer dissolved in α-chloronaphthalene at 210°C and at a polymer concentration of 0.1 g/100 ml and computing the result in accordance with the equation: According to another aspect of the present invention, there is provided a process for production of an aromatic sulfideamide polymer compound or compounds, which comprises sulfidizing an amide group-containing dihalide compound or compounds having the following general formula (III) and an aromatic dihalide compound of the following formula (IV) with a sulfidizing agent in an organic polar solvent; X-Ar³(R³) c -Y (IV) in these formulae Ar¹, Ar² and Ar³, which may be the same or different, each represent an aromatic ring; R¹, R² and R³, which may be the same or different, each represent an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group having 3 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, an acyl group having 2 to 20 carbon atoms or an arylalkyl group having 7 to 20 carbon atoms; a, b and c, which may be the same or different, each represent an integer of from 0 to 4; R⁴ and R⁵, which may be the same or different, each represent an alkylene group having 1 to 20 carbon atoms; and X and Y, which may be the same or different, each represent a halogen; so as to form a polymer compound consisting of the following repeating unit (V): in these formulae Ar¹ through Ar³ , R¹ through R⁵ and a, b and c, are as defined above and the ratio of p/q ranges from 99/1 to 1/99. The accompanying Fig. 1 shows an IR spectrum (wave length: about 400 - 4000 cm⁻¹) of the polymer obtained in Example 1. The invention will now be described in more detail. Examples of groups Ar¹, Ar² and Ar³, in the aromatic dihalide compounds which may be used in the invention include: where Z represents -O-, -S-, -SO₂-, -CO-, -CH₂- or -C(CH3)₂-. The groups may be the same or different in one compound. Example of particularly preferred dihalide compounds (III) for use in the present invention include: It is preferred that the amide group-containing dihalide compounds contain bonds at the para positions, if it is mainly desired to improve the thermal resistance properties of the product polymers. On the other hand, if it is desired to improve the solubility and molding properties of the sulfideamide polymer products, the dihalide compounds may contain bonds at the meta positions and/or at the ortho positions, or may be branched. The amide group-containing dihalide compounds may be synthesized by the conventional amide linkage formation technique. A typical example of synthesis is a process in which a corresponding halogen-containing aromatic carbonyl chloride is reacted with a corresponding diamine. Examples of particularly preferred dihalide compounds (IV) which may be used in the invention include and mixtures thereof. Generally, the present process for production of aromatic sulfideamide polymers comprises sulfidizing the amide group-containing dihalide compound (III) and the aromatic dihalide compound (IV) with a sulfidizing agent in an organic polar solvent. In practice of the process, for example, the amide group-containing compound (III) and the other dihalide compound (IV) may be simultaneously sulfidized, or the amide group-containing compound (III) and the other dihalide compound (IV) may be separately sulfidized and then brought together into a reaction system where they are allowed to further react with each other, or the amide group-containing compound (III) may be first sulfidized in a reaction system and then the other dihalide compound (IV) being added together with an appropriate amount of additional sulfidizing agent to the system (or vice versa ) for further reaction. The organic polar solvents used in the process of the present invention are preferably aprotic and those which are stable in the presence of alkalis at elevated temperatures. Examples of the preferred solvents include N,N-dimethyl acetamide (DMA), N-ethyl-2-pyrrolidone, hexamethyl phosphoric triamide (HMPA), dimethyl sulfoxide (DMSO), N-methyl-2-pyrrolidone (NMP), and 1,3-dimethyl imidazolidinone. The sulfidizing agents which may be used in the process include alkali metal sulfides, combinations of hydrogen sulfide with alkali metal bases, and combinations of alkali metal hydrosulfides with alkali metal bases. The alkali metal sulfides and hydrosulfides may be used as hydrates (from 0.5 to 10 molar equivalents). The sulfidizing agents may be prepared in situ prior to introduction of the dihalide compounds of the general formulae (III) and (IV) into the reaction system. Of course, the sulfidizing agent may be prepared outside the reaction system and then introduced to the system. It is preferred that, before the sulfidizing agent is introduced for commencement of the polymerization in the reaction system, the content of water in the system should be reduced to a level of less than 2.5 molar equivalents per equivalent of the sulfidizing agent to be introduced. Among the available sulfidizing agents, sodium sulfide, sodium hydrosulfide in conjunction with sodium hydroxide, and hydrogen sulfide in conjunction with sodium hydroxide are preferred. In the polymerization, a phase transfer catalyst such as a crown-ether compound, phosphor salt or an ammonium salt compound and/or an assistant such as an alkali metal carboxylate may be used to effectively increase the molecular weight of the resulting polymer. The polymerization is effected at a temperature of about 150 - 300°C, preferably 180 - 280°C, for a period of about 0.5 - 24 hours, preferably 1 - 12 hours. The preferred molar ratio of the dihalide compounds (III) and the compound (IV) to the sulfidizing agent used in the present process ranges from 0.9:1.0 to 1.1:1.0. The quantity of solvent used in the process may be such that the reaction system will contain 7 - 50%, preferably 10 - 40%, by weight of the product polymer upon completion of the polymerization. The process preferably comprises the step of recovering the product polymer e.g. by conventional methods, such as vacuum distillation, flash-off, and re-precipitation with organic solvents or water. The isolated product polymer may be washed with any suitable organic solvent or water and then dried. Generally, the aromatic sulfideamide copolymers according to the present invention have a logarithmic viscosity in the range of 0.02 to 2.00, as measured at a concentration of 0.5 g/100 ml in concentrated sulfuric acid at a temperature of 30°C or at a concentration of 0.1 g/100 ml in α-chloronaphthalene at 210°C. Polymers having viscosities of 0.05 to 2.00 are preferred. The process preferably comprises a step of thermally treating the polymers in an oxidative atmosphere such as air or oxygen-enriched air so as to structurally modify the polymer and hence to improve its physical and chemical properties e.g. so that the polymer is advantageously chain-extended and/or cross-inked and/or branched. Where the polymers are molded or otherwise shaped, they may contain various filler materials. Examples of suitable filler materials include (a) fiber fillers, such as glass fibers, carbon fibers, boron fibers, aramid fibers, alumina fibers, etc. and (b) inorganic fillers, such as mica, talc, clay, graphite, carbon black, silica, asbestos, molybdenum disulfide, magnesium oxide, calcium oxide, etc. As shown in the following examples, the polymers described herein exhibit, on IR analysis, absorptions around 1090 cm⁻¹ (caused by thioether linkages), around 1640 cm⁻¹ (caused by carbonyl groups in amide linkages) and around 1540 cm⁻¹ (caused by amino groups in amide linkages). These IR data confirm that the polymers described herein have the structural repeating units (I) and (II). The invention is illustrated in detail by the following Examples. Since most of the polymers according to the invention are only soluble in some special solvents such as concentrated sulfuric acid or α-chloronaphthalene, and are only sparingly soluble or insoluble in common organic solvents, it is not readily possible to determine the average molecular weight of the present polymers by a conventional method. Hence, the logarithmic viscosity value [η] of a polymer is herein employed as a measure of the molecular weight of that polymer. The logarithmic viscosity value [η] is obtained by measuring the relative viscosity of the polymer dissolved in concentrated sulfuric acid at 30°C and at a polymer concentration of 0.5 g/100 ml or the relative viscosity of the polymer dissolved in α-chloronaphthalene at 210°C and at a polymer concentration of 0.1 g/100 ml and calculating the result in accordance with the equation: Example 1 . This is a comparative example. A 500 ml autoclave was charged with Na₂S·2.7H₂O (80 m moles) and N-methyl-2-pyrrolidone (NMP; 150 ml) and heated to a temperature of 200°C with stirring so as to dehydrate the mixture. By this dehydration, 2.19 g of water containing 3.95% of NMP was distilled off. After cooling the reaction system down to 100°C, a dichloride (60 mmoles) and (20 mmoles) were added together with an additional 50 ml of NMP. The system was shielded and heated to 250°C. At this temperature, the polymerization was allowed to proceed for 6 hours. At the end of the polymerization period, the system was cooled and methanol was added to precipitate out the product polymer. The mixture was filtered. The filter cake was repeatedly washed with warm water and filtered and then washed with methanol and dried to give a light gray powdery polymer product (21.3 g; corresponding to a yield of 90.8%). The infra-red absorption spectrum of the polymer showed absorptions at 1092 cm⁻¹ (thioether linkage) and 3400, 1622 and 1536 cm⁻¹ (amide linkage, respectively) (see Fig. 1). Results of the elemental analysis, thermal analysis and solubility test are listed below: Found (wt%): C 67.1, H 6.1, N 7.0, S 10.7 Theoretical (wt%): C 67.6, H 6.0, N 7.2, S 10.9 The polymer showed a decomposition temperature of 437°C but did not show a definite melting point. The polymer was soluble in concentrated sulfuric acid but was sparingly soluble in an NMP/LiCl (95/5 by weight) mixture. It had a logarithmic viscosity of 0.14 (0.5 g/100ml in H₂SO₄ at 30°C). Example 2 . This is a comparison example. A 500 ml autoclave was charged with Na₂S·2.7H₂O (58 mmoles) and N-methyl-2-pyrrolidone (NMP; 150 ml) and heated to a temperature of 200°C with stirring so as to dehydrate the mixture. By this dehydration 1.63 g of water containing 4.81% of NMP was distilled off. After cooling the reaction system down to 110°C, (60 mmoles) was added together with an additional 50 ml of NMP. The system was shielded and heated to 250°C. At this temperature, the polymerization was allowed to proceed for 2 hours. Similarly, a 1000 ml autoclave was charged with Na₂S·2.7H₂O (182 m moles) and N-methyl-2-pyrrolidone (NMP; 300 ml) and heated to 200°C with stirring so as to dehydrate the mixture. By this dehydration 5.34 g of water containing 3.76% of NMP was distilled off. Then the system was cooled down to 98°C and, then, (180 mmoles) was introduced together with the polymer slurry resulting from the first polymerization and an additional 100 ml of NMP into the polymerized slurry contained in the reactor. Then the reactor was again shielded and heated to 250 C. The mixture was allowed to react for a further 6 hours at this temperature. At the end of the period, the system was cooled and methanol was added to precipitate out the product polymer. The mixture was filtered. The filter cake was repeatedly washed with warm water and filtered and then washed with methanol and dried to give a light gray powdery polymer product (64.9 g; 92.3% yield). Results of the IR spectrometry, elemental analysis, thermal analysis, solubility test and logarithmic viscosity measurement are shown below: IR: 1090 cm⁻¹ (thioether linkage), 3390; 1620; and 1538 cm⁻¹ (amide linkage) Elemental analysis: Found (wt%): C 67.5, H 5.8, N 7.2, S 10.8 Theoretical (wt%): C 67.6, H 6.0, N 7.2, S 10.9 The decomposition temperature was 467°C, with no definite melting point. The polymer was soluble in concentrated sulfuric acid but sparingly soluble in NMP/LiCl (95/5 by weight). It had a logarithmic viscosity of 0.15 (0.5 g/100 ml in H₂SO₄ at 30°C). The polymer showed properties except for the decomposition temperature similar to those of the polymer produced in Example 1. It is believed that the significantly increased decomposition temperature of the polymer of Example 2 is due to its being a block copolymer. Example 3 Polymerization was performed as described in Example 1 except that the dihalide compounds were substituted by: Yield: 12.4 g (97.2%) IR: 1085 cm⁻¹ (thioether linkage), 1640 cm⁻¹ (carbonyl linkage) Elemental analysis: Found (wt%): C 66.6, H 4.5, N 4.1, S 20.1 Theoretical (wt%): C 66.7, H 4.3, N 4.3, S 19.7 The decomposition temperature was 427°C and the melting point was found around 268°C. The polymer was insoluble in an NMP/LiCl (95/5 by weight) mixture and slightly soluble in concentrated sulfuric acid. The logarithmic viscosity was 0.13 (0.1 g/100 ml in α-chloronaphthalene at 210°C). Example 4 The procedure of Example 1 was repeated except that the dihalide compouds were substituted by: Yield: 18.6 g (95.5%) IR: 1084 cm⁻¹ (thioether linkage), 1640 cm⁻¹ (carbonyl linkage) Elemental analysis: Found (wt%): C 67.3, H 5.0, N 7.6, S 10.9 Theoretical (wt%): C 67.5, H 4.9, N 7.5, S 11.4 The decomposition temperature was observed at 452°C and the melting point at 347°C. The logarithmic viscosity was 0.15 (0.1 g/100 ml in α-chloronaphthalene at 210°C). As above shown, although the simple aromatic sulfideamide polymers alone are not melt-processable, the corresponding copolymers containing a comonomer component such as a dihalobenzene may have such a reduced melting point that they are melt processable. Example 5 . This is a comparison example. The procedure of Example 1 was repeated except that the dihalide compounds were substituted by: Yield: 21.9 g (97.8%) IR: 1088 cm-¹ (thioether linkage), 3360; 1630; 1540 cm-¹ (amide linkage) The decomposition temperature was 465°C with no definite melting point observed. The polymer was soluble in concentrated sulfuric acid, but sparingly soluble in an NMP/LiCl (95/5 by weight) mixture. The polymer had a logarithmic viscosity of 0.16 (0.5 g/100 ml in H₂SO₄ at 30°C). From the above description, it will be appreciated that the present invention provides a novel class of aromatic sulfideamide copolymers which may be synthesized from readily commercially available materials by a simple procedure. It is expected that the novel copolymers will find use in a wide range of applications as engineering plastics because of their excellent heat resistance and processability properties and other useful properties. As can be observed from a comparison of the results quoted in the examples above the polymers of the invention (Examples 3 and 4) exhibit melting points of 268°C and 347°C respectively. None of the polymers of comparison Examples 1, 2 and 5 exhibit observable melting points which thus limits the way in which these polymers can be fabricated.

Claims: An aromatic sulfideamide polymer which consists of from 1 to 99 mol% of repeating units represented by the following formula (I): and from 99 to 1 mol% of repeating units represented by the formula (II): -[Ar³(R³) c -S]- (II) wherein Ar¹, Ar² and Ar³, which may be the same or different, each represent an aromatic ring; R¹, R² and R³, which may be the same or different, each represent an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group having 3 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, an acyl group having 2 to 20 carbon atoms or an arylalkyl group having 7 to 20 carbon atoms; a, b and c, which may be the same or different, each represent an integer of from 0 to 4; and R⁴ and R⁵, which may be the same or different, each represent an alkylene group having 1 to 20 carbon atoms. A polymer as claimed in Claim 1 in which the groups Ar¹, Ar² and Ar³ are each selected from where Z represents -O-, -S-, -SO₂-, -CO-, -CH₂- or -C(CH₃)₂-. A polymer as claimed in Claim 1 or Claim 2 which has a logarithmic viscosity [η] of 0.02 to 2.00, preferably 0.05 to 2.00, as determined by measuring the relative viscosity of the polymer dissolved in concentrated sulfuric acid at 30°C and at a polymer concentration of 0.5 g/100 ml or the relative viscosity of the polymer dissolved in α-chloronaphthalene at 210°C and at a polymer concentration of 0.1 g/100 ml and computing the result in accordance with the equation: A polymer as claimed in Claim 1, 2 or 3 which is cross-linked or chain extended or branched or any combination thereof by heating under an oxidative atmosphere. A process for production of an aromatic sulfideamide polymer, which comprises sulfidizing an amide group-containing dihalide compound or compounds having the following general formula (III) and an aromatic dihalide compound of the following formula (IV) with a sulfidizing agent in an organic polar solvent X-Ar³(R³) c -Y (IV) wherein Ar¹, Ar² and Ar³, which may be the same or different, each represent an aromatic ring; R¹, R² and R³, which may be the same or different, each represent an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group having 3 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, an acyl group having 2 to 20 carbon atoms or an arylalkyl group having 7 to 20 carbon atoms; a, b and c, which may be the same or different, each represent an integer of from 0 to 4; R⁴ and R⁵, which may be the same or different, each represent an alkylene group having 1 to 20 carbon atoms; and X and Y, which may be the same or different, each represent a halogen; so as to form a polymer consisting of the following repeating unit (V): wherein Ar¹ through Ar³, R¹, R², R³, R⁴ and R⁵ and a, b and c, are as defined above and the ratio of p/q ranges from 99/1 to 1/99. A process as claimed in Claim 5 in which groups Ar¹, Ar² and Ar³ are each selected from where Z represents -O-, -S-, -SO₂-, -CO-, -CH₂- or -C(CH₃)₂-. A process as claimed in Claim 5 or Claim 6 in which the amide group-containing dihalide compound (III) is selected from: and the mixtures thereof. A process as claimed in Claim 5, 6 or 7 in which the aromatic dihalide compound (IV) is selected from and mixtures thereof. A process as claimed in Claim 5, 6, 7 or 8 in which the amide group-containing compound (III) and the compound (IV) are simultaneously sulfidized. A process as claimed in any one of Claims 5 to 8 in which the aide group-containing compound (III) and the compound (IV) are separately sulfidized and then brought together into a reaction system where they are allowed to further react with each other. A process as claimed in any one of Claims 5 to 8 in which the amide group-containing compound (III) is first sulfidized in a reaction system and then the compound (IV) is added together with an appropriate amount of additional sulfidizing agent to the system, or vice versa , for further reaction. A process as claimed in any one of Claims 5 to 11 in which the organic solvent is aprotic. A process as claimed in Claim 12 in which the solvent is selected from N,N-dimethyl acetamide, N-ethyl-2-pyrrolidone, hexamethyl phosphoric triamide, dimethyl-sulfoxide, N-methyl-2-pyrrolidone, and 1,3-dimethyl imidazoline. A process as claimed in any one of Claims 5 to 13 in which the sulfidizing agent is selected from sodium sulfide, a combination of sodium hydrosulfide and sodium hydroxide, and a combination of hydrogen sulfide and sodium hydroxide. A composition comprising an aromatic sulfideamide polymer as claimed in any one of Claims 1 to 4 or produced by a process as claimed in any one of Claims 5 to 14 and one or more conventional additives.

Inventors: INOUE HIROSHI, KATO TOSHIKAZU, OGAWARA KENSUKE, TOMAGOU SATOSHI, INOUE, HIROSHI, KATO, TOSHIKAZU, OGAWARA, KENSUKE, TOMAGOU, SATOSHI
Applicants: TOSOH CORP, TOSOH CORPORATION
Application year: 1988
Main classification: C08G75
IPC codes: C08G75