NON-AQUEOUS SECONDARY CELL

Abstract: A non-aqueous secondary cell is provided which is repeatedly chargeable and dischargeable. This cell comprises, as main components thereof, a negative electrode, a positive electrode, and a separator disposed between the positive electrode and negative electrode and impregnated with an electrolyte. The negative electrode has lithium or a lithium alloy as the active material. The positive electrode has as the active material a manganese oxide expressed by a chemical formula Li 1-X Mn₂O₄ wherein 1 ≧X≧ 0.

Description: Background of the Invention (1) Field of the Invention The present invention relates to a non-aqueous secondary cell in which lithium or lithium alloy is used as the active material for the negative electrode, and particularly to an improvement in the positive electrode. (2) Description of the Prior Art Molybdenum trioxide, vanadium pentoxide, titanium and niobic sulfide have been proposed as the active material for the positive electrode of this type of secondary cell, but these substances have not been to practical use to date. For the positive electrode of the non-aqueous primary cell, on the other hand, manganese dioxide and carbon fluoride are known to be typical examples of active material and are actually employed for the purpose. Manganese dioxide in particular has the advantages of being excellent in storage characteristics, abundant in the earth and inexpensive. As the crystal structure of manganese dioxide suited for the positive electrode, γ-β MnO₂ heat-treated at temperatures of 250-350°C has been proposed as in Japanese Patent Publication No. 49-25571. This γ-β MnO₂, however, is unsatisfactory in reversibility and has the problem of lowering charge and discharge characteristics. The reason will be explained with reference to Figs. 1a-1e of the accompanying drawings showing X-ray diffraction patterns. Fig. 1a shows a diffraction pattern prior to charging and discharging. Figs. 1b and 1c show diffraction patterns at a 10th discharge and charge, respectively. Compared with the pattern of Fig. 1a, it will be seen that the patterns of Figs. 1b and 1c show the angles of diffraction shifting to a lower side and the peaks becoming less sharp also after charging. These trends are more conspicuous and the peaks are almost leveled out in the patterns at a 100th discharge and charge shown in Figs. 1d and 1e, respectively. It may be deduced from the above that a repetition of charges and discharges results in widening of the bond length between manganese and oxygen and in loosening of the crystal structure of manganese dioxide. Consequently, the manganese dioxide has poor reversibility and charge and discharge characteristics. This applies also to β-MnO₂ heat-treated at temperatures of 350-430°C as disclosed in U.S. Patent 4,133,856. The active material for the positive electrode may comprise δ-manganese dioxide having a laminar structure or ∝-manganese dioxide having a structure including larger channels than γ - β and β-manganese dioxides. This is considered to improve the reversibility of the non-aqueous secondary cell since the spaces are then increased for doping and undoping lithium ions. δ- and α- manganese oxides contain potassium ions and ammonium ions in their structure. These ions elude into the electrolyte during the charging and discharging, thereby to greatly deteriorate the charge and discharge characteristics. An electrical energy storage cell according to the preamble of claim 1 is disclosed in EP-A-009 934. In this cell one of the electrodes comprises either LiMn₂O₄ or Mn₂O₄. In Mat. Res. Bull., volume 19, pages 179-187, 1984, M. M. Thackeray, et al, it is described that Li can be electrochemically removed from LiMn₂O₄ which is used as a starting material. Furthermore, this document shows the use of cathode electrode materials of spinel type and the formula Li 0.4 MnO₄. The object of the invention is to improved charge and discharge cycle characteristics of an non-aqueous secondary cell comprising a positive electrode having manganese oxide as the active material. This object is achieved by a repeatedly chargable and dischargable non-aqueous secondary cell having the features of claim 1; the further claims are related to methods of forming the cell. According to the invention Li 1-x Mn₂O₄ with x = 0.5 is employed as a starting material when the cell is prepared. Superiority of this material with respect to LiMn₂O₄ has been proved by experimental studies, and in particular it has been shown that the cells according to the invention have improved cell capacity for longer periods of time. The spinel type manganese oxide is prepared by mixing Mn₂O₃ and Li₂CO₃ and thereafter heat-treating a resulting mixture in the air. λ-manganese oxide is prepared by immersing a spinel type manganese oxide in acid. The manganese oxide having a crystal structure intermediate between a spinel type manganese oxide and λ-manganese oxide may be prepared by one of the following processes: immersing the spinel type manganese oxide in acid; immersing δ-MnO₂ or α-MnO₂ in LiOH solution, thereafter applying a microwave thereto until the LiOH solution evaporates, and heat-treating; and substituting lithium ions for dissimilar cations contained in a crystal structure of δ-MnO₂ or α-MnO₂ and thereafter heat-treating the manganese dioxide. As noted above, the present invention employs, as the active material for the positive electrode, the spinel type or λ-manganese oxide which has a three-dimensional channel structure and whose crystal structure is not easily collapsible and does not contain potassium ions or the like, or the manganese oxide having a crystal structure intermediate between these two types of manganese oxides. Through such measure the present invention provides a great improvement in the cycle characteristics of this type of cell, and the improvement is believed to have immense utility in industry. Brief Description of the Drawings The above and other objects, advantages and features of the invention will become apparent from the following description thereof taken in conjunction with the accompanying drawings, in which: - Figs. 1a-1e are views showing X-ray diffraction patterns where charges and discharges are repeated on a cell having a positive electrode formed of γ-β MnO₂, wherein Fig. 1a shows a diffraction pattern prior to charging and discharging, Figs. 1b and 1c show diffraction patterns at a 10th discharge and a subsequent charge, respectively, and Figs. 1d and 1e show diffraction patterns at a 100th discharge and a subsequent charge, respectively, Fig. 2 is a half section of a cell according to the present invention, Figs. 3 through 6 are views showing X-ray diffraction patterns of various types of manganese oxide used as the active material for the positive electrode of the cell according to the present invention, Fig. 7 is a view showing cycle characteristics of cells, and Figs. 8a-8g are views showing X-ray diffraction patterns where charges and discharges are repeated on a cell according to the present invention employing a spinel type manganese oxide as the active material for the positive electrode, wherein Fig. 8a shows a diffraction pattern prior to charging and discharging, Figs. 8b and 8c show diffraction patterns at a 10th discharge and a subsequent charge, respectively, Figs. 8d and 8e show diffraction patterns at a 100th discharge and a subsequent charge, respectively, and Figs. 8f and 8g show diffraction patterns at a 150th discharge and a subsequent charge, respectively. EXAMPLE 1 A first example will be described hereinafter with reference to a flat type non-aqueous secondary cell as shown in Fig. 2. The illustrated cell comprises positive and negative terminal cans 1 and 2 formed of stainless steel and separated from each other by an insulating packing 3 formed of polypropylene. Number 4 indicates a positive electrode constituting the gist of this invention, which is pressed upon a positive collector 5 secured to a bottom inside surface of the positive terminal can 1. Number 6 indicates a negative electrode pressed upon a negative collector 7 secured to a bottom inside surface of the negative terminal can 2. Number 8 indicates a separator comprising a porous membrane of polypropylene. This cell employs an electrolyte comprising lithium perchlorate dissolved in 1 M in an equal volume solvent mixture of propylene carbonate and dimethoxyethane. The positive and negative electrodes are prepared as follows: 100 grams of Mn₂O₃ and 23.4 grams of Li₂CO₃ are first mixed in a Mn-Li molar ratio of 2:1, and then heat-treated in the air at 650°C for six hours and at 850°C for fourteen hours. This heat treatment produces a spinal type manganese oxide (which is expressed by a chemical formula Li 1-X Mn₂O₄ wherein X=0). Fig. 3 shows an X-ray diffraction pattern of this sample. This X-ray diffraction pattern agrees with the LiMn₂O₄ data on ASTM Card No. 35-782, which confirms that the product resulting from the above process is a spinel type manganese oxide. The above heat treatment should preferably be carried out in an oxidizing atmosphere. Next, 90% by weight of this spinel type manganese oxide is mixed with 6% by weight of acetylene black acting as conductive agent and 4% by weight of fluoric resin powder acting as binder to produce a blend for forming the positive electrode. This blend is molded under a pressure of 5 tons/cm² into a shape having a 20mm diameter, and then heat-treated in a vacuum at 200 to 300°C, whereby the positive electrode is completed. This positive electrode has a theoretical capacity of 50mAH. The negative electrode, on the other hand, is prepared by punching a piece 20mm in diameter out of a lithium foil having a selected thickness. This negative electrode has a theoretical capacity of 200mAH. A cell 24.0mm in diameter and 3.0mm in height was formed by using the positive and negative electrodes as prepared above, together with a separator, an electrolyte, etc. This cell is hereinafter referred to as Cell A1. EXAMPLE 2 30 grams of the spinel type manganese oxide prepared through the process in EXAMPLE 1 was immersed in 4N sulfuric acid for 170 hours, and was thereafter rinsed in 2ℓ of pure water, whereby λ-manganese oxide (which is expressed by the chemical formula Li 1-x Mn₂O₄ wherein X=1) was prepared. A cell was formed as in EXAMPLE 1 except that the λ-manganese oxide was used as the active material for the positive electrode. This cell is hereinafter referred to as Cell A2. It was confirmed through an atomic absorption analysis that the above acid treatment had completely removed the lithium contained in the spinel type manganese oxide. Fig. 4 shows an X-ray diffraction pattern of the above λ-manganese oxide. This diffraction pattern is substantially the same as the diffraction pattern of the spinel type manganese oxide shown in Fig. 3. The diffraction pattern of Fig. 4 differs from that of Fig. 3 only in that a contraction of the lattice caused the peaks to shift in the direction of higher angles compared with the case of the spinel type manganese oxide. This indicates that the λ-manganese oxide retains the coordination between Mn and O continuing from the spinel type. EXAMPLE 3 The spinel type manganese oxide prepared through the process in EXAMPLE 1 was immersed in 0.5N sulfuric acid for 100 hours, whereby a manganese oxide having a crystal structure intermediate between the spinel type and λ-manganese oxide (which is expressed by the chemical formula Li 1-X Mn₂O₄ wherein X=0.5) was prepared. A cell was formed as in EXAMPLE 1 except that this manganese oxide having a crystal structure of the intermediate nature was used as the active material for the positive electrode. This cell embodying the present invention is hereinafter referred to as Cell A3. It was confirmed through the atomic absorption analysis that the above acid treatment had removed about half of the lithium contained in the spinel type manganese oxide. Fig. 5 shows an X-ray diffraction pattern of the manganese oxide having the intermediate crystal structure. This diffraction pattern is substantially the same as the diffraction pattern of the spinel type manganese oxide shown in Fig. 3. The diffraction pattern of Fig. 5 differs from that of Fig. 3 only in that a slight contraction of the lattice caused the peaks to shift to positions between those of the spinel type manganese oxide and λ-manganese oxide. This indicates that the manganese oxide having the crystal structure intermediate between the spinel type and λ-manganese oxide also retains the coordination between Mn and O continuing from the spinel type. EXAMPLE 4 δ-manganese oxide prepared by adding 1.5ℓ of 2N hydrochloric acid to 500mℓ of 1M potassium permanganate solution was immersed in 1M LiOH solution. Thereafter the product was exposed to a microwave of about 2.45GHz frequency until the LiOH solution evaporated. After repeating this process several times, the product was rinsed in pure water and then heat-treated in the air at temperatures of 200-450°C for 20 hours, whereby a manganese oxide having a crystal structure intermediate between the spinel type and λ-manganese oxide (which is expressed by the chemical formula Li 1-x Mn₂O₄ wherein 1>X>0) was prepared. A cell was formed as in EXAMPLE 1 except that this manganese oxide having a crystal structure of the intermediate nature was used as the active material for the positive electrode. This cell embodying the present invention is hereinafter referred to as Cell A4. Fig. 6 shows an X-ray diffraction pattern of this manganese oxide having the intermediate crystal structure. This diffraction pattern is substantially the same as the diffraction pattern of the spinel type manganese oxide shown in Fig. 3. The diffraction pattern of Fig. 6 differs from that of Fig. 3 only in that, as in EXAMPLE 3, a slight contraction of the rattice caused the peaks to shift to positions between those of the spinel type manganese oxide and λ-manganese oxide. This indicates that lithium is doped in the manganese oxide. COMPARATIVE EXAMPLE 1 γ - β manganese dioxide was prepared by heat treating I.C. No. 12 chemical manganese dioxide in the air at a temperature of 200-400°C. And a cell was formed as in EXAMPLE 1 except that this manganese dioxide was used as the active material for the positive electrode. This cell is hereinafter referred to as Comparative Cell B1. COMPARATIVE EXAMPLE 2 δ-manganese dioxide was heat-treated in the air at a temperature of 200-400°C for 20 hours without doping lithium. And a cell was formed as in EXAMPLE 1 except that this δ-manganese dioxide was used as the active material for the positive electrode. This cell is hereinafter referred to as Comparative Cell B2. COMPARATIVE EXAMPLE 3 α-manganese dioxide obtained by adding potassium permangate and potassium nitrate to a manganese sulfate solution was heat-treated in the air at a temperature of 200-400°C without doping lithium. And a cell was formed as in EXAMPLE 1 except that this α-manganese dioxide was used as the active material for the positive electrode. This cell is hereinafter referred to as Comparative Cell B3. Cycle characteristics of Cells A1-A4 and Comparative Cells B1-B3 were checked and the results are shown in Fig. 7. The testing conditions were such that the discharge was carried out in a current of 3mA for four hours, the charge in the current of 3mA, and the charge ending voltage was 4.0V. It will be seen from Fig. 7 that discharge ending voltage of Cell A3 according to the present invention drop to 2.0V only after 130-150 cycles of charge and discharge whereas Comparative Cell B1 has the discharge ending voltage dropping to 2.0V around the 100th cycle and Comparative Cells B2 and B3 have the discharge ending voltages dropping to 2.0V around the 30th cycle. This indicates that Cell A3 according to the present invention is far superior in cycle characteristics to Comparative Cells B1-B3. The reason for the improvement in the cycle characteristics will be explained with reference to Figs. 8a-8g. Compared with the a diffraction pattern prior to charging and discharging shown in Fig. 8a, diffraction patterns at a 10th charge shown in Figs. 8b and 8c indicate no weakening of the peaks and no shift of diffraction angles. This is true also of diffraction patterns at a 100th charge shown in Figs. 8d and 8e and diffraction patterns at a 150th charge shown in Figs. 8f and 8g. This demonstrates that, where the spinel type or λ-manganese oxide or a manganese oxide having a crystal structure of the intermediate nature is used as the active material for the positive electrode of a non-aqueous secondary cell, there occurs no collapse of the crystal structure with the charge and discharge cycles as encountered where γ-β or β-manganese dioxide is used as the active material for the positive electrode. Thus, the cells according to the present invention have improved reversibility and charge and discharge characteristics. It is considered that, while γ - β and β - manganese dioxides have a one-dimensional channel structure, the spinel type and λ-manganese oxides and the manganese oxide having a crystal structure of the intermediate nature have a three-dimensional channel structure which facilitates smooth doping and undoping of lithium ions at times of charging and discharging. Besides, unlike δ- and α-manganese dioxides, the spinel type and λ-manganese oxides and the manganese oxide having an intermediate crystal structure do not contain potassium ions or ammonium ions in their crystal structure, thereby to prevent deterioration of the charge and discharge characteristics. In EXAMPLE 3 the spinel type manganese oxide was immersed in 0.5N sulfuric acid for 100 hours, to prepare the manganese oxide having a crystal structure intermediate between the spinel type and λ-manganese oxide (which is expressed by the chemical formula Li 1-X Mn₂O₄ wherein X=0.5). By varying this acid treatment conditions, it is possible to prepare manganese oxides of the intermediate crystal structure containing lithium in various degrees of concentration (i.e. lithium-containing manganese oxides expressed by the chemical formula Li 1-X Mn₂O₄ wherein 1>X>0). Further, the manganese oxide having the intermediate crystal structure may be prepared by other methods, for example, by a method in which lithium ions are substituted for dissimilar cations contained in the crystal structure of δ -MnO₂ or α-MnO₂ which is followed by a heat treatment. In the foregoing embodiments, lithium is used as the active material for the negative electrode. However, a lithium alloy may be employed instead of lithium. Such lithium alloys include lithium-aluminum alloy, lithium-magnesium alloy and the like. In addition, the present invention is not limited to the secondary cell using the non-aqueous electrolyte. It will be apparent that the invention is applicable to a non-aqueous secondary cell using a solid electrolyte as well.

Claims: A repeatedly chargeable and dischargeable non-aqueous secondary cell comprising a non-aqueous electrolyte, a negative electrode (6) having lithium or a lithium alloy as active material, and a positive electrode (4) having manganese oxide expressed by the formula Li 1-x Mn₂O₄, as an active material characterized in that the value of x = 0,5 is selected when said cell is prepared, that said manganese oxide has a crystal structure intermediate between a spinel type manganese oxide and λ-manganese oxide in which the coordination between Mn and O is retained continuing from the spinel type manganese oxide, and that a separator (8) is disposed between said positive electrode and said negative electrode. A method of forming the cell of claim 1 , characterized by a first step of preparing said manganese oxide by immersing δ-Mno₂ or α-MnO₂ in LiOH solution, thereafter applying microwave thereto until said LiOH solution evaporates, and heat-treating, a second step of producing a positive electrode having said manganese oxide as an active material and a negative electrode having lithium or a lithium alloy as an active material, and a third step of assembling said positive electrode and said negative electrode with said separator impregnated with a non-aqueous electrolyte therebetween. A method for forming the cell of claim 1 , characterized by a first step of preparing said manganese oxide by substituting lithium ions for dissimilar cations contained in a crystal structure of δ-MnO₂ or α-MnO₂ and thereafter heat-treating the manganese dioxide, a second step of producing a positive electrode having said manganese oxide as an active material and a negative electrode having lithium or a lithium alloy as an active material, and a third step of assembling said positive electrode and said negative electrode with a separator impregnated with a non-aqueous electrolyte therebetween.

Inventors: FURUKAWA, NOBUHIRO, NOHMA, TOSHIYUKI, SAITO, TOSHIHIKO
Applicants: SANYO ELECTRIC CO., LTD.
Application year: 1988
Main classification: H01M4
IPC codes: H01M4, H01M10