Sintered body having high corrosion resistance containing ZrB2.

Abstract: A sintered body containing ZrB₂ is obtained by sintering a starting powder material containing not less than 50 % by weight of a starting powder mixture consisting essentially of Cr₃C₂ and a boride represented by the formula (XB₂) n wherein n represents an integer of 1 or 2 and when n is 1, X represents a zirconium atom and when n is 2, X represents a zirconium atom and a titanium atom, respectively and B represents a boron atom. The weight ratio of the Cr₃C₂ : the boride is 50 to 0.5 : 50 to 99.5.

Description: BACKGROUND OF THE INVENTION: This invention relates to a sintered body having a high corrosion resistance and containing ZrB₂. The sintered bodies containing ZrB₂ have been studied and investigated for a long time and a number of patent aplications have been made on this subject. However, the known sintered bodies have not been found extensively commercially useful. For obtaining a sintered body containing ZrB₂, it is known to add silicates such as MoSi₂ or ZrSi₂, carbides such as SiC, B₄C or WC, nitrides such as TaN, BN, AlN or HfN, oxides such as ZrO₂ and metal powders as a sintering aid or additional components to ZrB₂ and to sinter the resulting mixture. For obtaining a sintered body containing ZrB₂ and TiB₂, metal powders and tungsten carbide base super hard alloyes may be used as a sintering aid, as disclosed in Japanese Laid-open Patent Publication No. 44768/1986. However, when the silicates such as MoSi₂ or ZrSi₂ or metal powders are used as the sintering aids, the resulting hard alloy is inferior in strength, corrosion resistance and anti-oxidation due to its tendency towards melting and decomposition under elevated temperatures. Although nitrides in general are superior in hardness and strength, these lack in anti-oxidation properties, corrosion resistance and thermal shock resistance. ZrO₂, mentioned herein as the oxide, is not satisfactory in anti-oxidation properties, while it is also poor in strength when used under elevated temperatures and under an oxidizing atmosphere due to transition from the tetragonal to the monoclinical system or vice versa. SiC, B₄C or WC, used as the carbides, apparently are insufficient in oxidation resistance. These sintering aids have several deficiencies, as discussed hereinabove, and cannot be practically employed in a form taking advantage of the strong points of ZrB₂ and TiB₂. SUMMARY OF THE INVENTION: It is a principal object of the present invention to provide a sintered body having a high corrosion resistance. It is another object of the present invention to provide a sintered body having superior corrosion resistance and anti-oxidation properties while exhibiting a high melting point, superior hardness and electrical conductivity without detracting from the properties of ZrB₂. It is a further object of the present invention to provide a sintered body having high strength and superior thermal shock resistance. These and other objects of the present invention will become apparent from the following description of the invention. In accordance with the present invention a sintered body having high corrosion resistance and containing ZrB₂ obtained by sintering a starting powder material containing not less than 50 % by weight of a starting powder mixture consisting essentially of Cr₃C₂ and ZrB₂ or a starting powder mixture consisting essentially of Cr₃C₂, ZrB₂ and TiB₂ is characterized in that the weight ratio of Cr₃C₂ : ZrB₂ or a mixture of ZrB₂ and TiB₂ is 50 to 0.5 : 50 to 99.5. DESCRIPTION OF THE INVENTION: The present invention will be explained in detail hereinbelow. It is an important feature of the present invention to combine a boride or borides consisting essentially of ZrB₂ or of ZrB₂ and TiB₂ with Cr₃C₂, whereby success has been achieved in overcoming the deficiencies of the prior art. That is, both ZrB₂ and Cr₃C₂, that are used for preparing a sintered body of the present invention, have been known to have superior corrosion-resistant properties. Since the ZrB₂ itself may be sintered only with extreme difficulties, a variety of sintering aids have been employed without, however, allowing to exhibit the properties inherent in ZrB₂ satisfactorily. In addition, Cr₃C₂ in effect cannot be solely employed practically since it yields a sintered body which is brittle although it has rather high sintering properties. According to the present invention, the aforementioned deficiencies can be compensated for each other by the combined use of ZrB₂ and Cr₃C₂ as a starting powder mixture. According to the present invention the sintered body is obtained by sintering a starting powder material containing a starting powder mixture. The starting powder mixture consists essentially of Cr₃C₂ and ZrB₂ or a mixture of ZrB₂ and TiB₂. The weight ratio of Cr₃C₂ : ZrB₂ or a mixture of ZrB₂ and TiB₂ is in the ranges of 50 to 0.5 : 50 to 99.5. With the weight ratio of Cr₃C₂ less than 0.5, the effects of the Cr₃C₂ as the sintering aid are practically nil, leading to loss of high corrosion resistance. With the weight ratio of Cr₃C₂ in excess of 50, the properties of the boride are impaired. According to the present invention, the aforementioned boride and Cr₃C₂ promote the sintering each other to exhibit the excellent and unexpected results. According to the present invention, the Cr₃C₂ and the aforementioned boride are employed in weight ratio amounts that will together make up 100. That is, when the boride is ZrB₂, there is employed a starting powder mixture consisting essentially of 0.5 to 50 ratio by weight of Cr₃C₂ and 99.5 to 50 ratio by weight of ZrB₂. When the boride is composed of ZrB₂ and TiB₂, it is preferred that the above mixture be composed essentially of 50 to 0.5 ratio by weight of Cr₃C₂, 5 to 94.5 ratio by weight of ZrB₂ and 94.5 to 5 ratio by weight of TiB₂, with the Cr₃C₂, ZrB₂ and TiB₂ together making up 100 ratio by weight in total. With the ZrB₂ less than 5 ratio by weight, the properties inherent in ZrB₂, such as high melting point, high hardness or high corrosion resistance, are not exhibited. With the TiB₂ less than 5 ratio by weight, the properties of high strength naturally expected from the addition of TiB₂ are not exhibited. In the context of the present invention, the starting powder mixture "consisting essentially" of Cr₃C₂ and boride means that the Cr₃C₂ need not necessarily be of 100 % purity. The Cr₃C₂ may thus include Cr₇C₃ and Cr₄C, as an example. Also it is preferred that ZrB₂, TiB₂ and Cr₃C₂ each be of a purity of not less than 99 % and have a mean particle size of not more than 10 µm and desirably not larger than 1 µm. In the present invention, the starting powder mixture consisting essentially of the Cr₃C₂ and the boride is contained in an amount of not less than 50 % by weight, based on the total weight of the starting powder material. According to the present invention, the starting powder material may contain 100 % by weight of the starting powder mixture, that is, Cr₃C₂-ZrB₂ powders or Cr₃C₂-ZrB₂-TiB₂ powders. Or alternatively, the starting powder material may contain up to 50 % by weight of one or more of additional starting powders. These additional starting powders may be selected from the group consisting of not more than 40 % by weight of BN, not more than 25 % by weight of AlN, not more than 25 % by weight of B₄C, not more than 15 % by weight of SiC, not more than 15 % by weight of TiC, based on the total weight of the starting powder material, and mixtures thereof. As stated hereinabove, the additional starting powders are employed in an amount of less than 50 % by weight based on the total weight of the starting powder material, so that, when 40 % by weight of BN is employed, for example, 5 % by weight of each of AlN and B₄C, for example, may be employed simultaneously. The additional starting powders may be employed within the range of the aforementioned upper limit for producing the desired properties. BN is employed for improving the thermal impact resistance of the sintered body. For preventing the strength from decreasing, it is employed in the range of not more than 40 % by weight and preferably in the range between 5 and 20 % by weight. AlN, on the other hand, is employed for promoting the sintering. Since the anti-oxidation properties and heat resistance of the sintered body are lowered with excessive amounts of AlN, it is employed in an amount of not more than 25 % by weight and preferably in the range of from 5 to 20 % by weight. B₄C is employed for improving hardness of the sintered body. Since the anti-oxidation properties and heat resistance are lowered with excessive amounts of B₄C, it is employed in an amount of not more than 25 % by weight and preferably in the range of from 5 to 20 % by weight. SiC is effective as the sintering aid and for improving hardness and anti-oxidation properties of the sintered body. Since the corrosion resistance and the thermal shock resistance of the sintered body are lowered with excessive amounts of SiC, it is employed in an amount of not more than 15 % by weight and preferably in the range of from 5 to 10 % by weight. TiC is effective as the sintering aid and for improving the hardness of the sintered body. Since the anti-oxidation properties of the sintered body are considerably lowered with excessive amounts of TiC, it is employed in an amount of not more than 15 % by weight and preferably in the range of from 5 to 15 % by weight. It is preferred that the BN, AlN, B₄C, SiC and TiC employed as the additional starting powders be each of a purity of not lower than 99 % and have a mean particle size of not more than 10 µm. In preparing the starting powder material, the respective starting powders may be pulverized and subsequently mixed or, alternatively, the starting powders may be mixed and pulverized simultaneously. Any of the wet and dry methods may be employed for pulverizing the powders. In sintering, the starting powder material may be subjected to press molding or CIP (Cold isostatic pressing) molding in vacuum or under a neutral or reducing atmosphere of argon, helium or nitrogen, followed by sintering at pressureless conditions. The sintering temperature and the sintering time may be in the range of from 1400 to 2200°C and in the range of 30 minutes to six hours, respectively, and are suitably selected in dependence upon the composition and the particle size of the starting powder material. The HIP (Hot isostatic pressing) method or the hot pressing method may also be employed for molding. In addition to the above powders, whiskers and/or fibers, such as A₂O₃, SiO₂, MgO, SiC, B₄C or Si₃N₄, may be added to the starting powder material of the present invention for further improving the physical properties, such as the impact resistance or thermal shock resistance or fracture toughness of the sintered body. The corrosion-resistant sintered body of the present invention has high melting point, hardness, conduct electricity and are superior in corrosion resistance and anti-oxidation properties, without impairing the properties of borides, so that it can be used for applications such as electrodes, mechanical parts, heating elements or corrosion resistant components. For example, it can be used for level sensors, protective tubes for iron and steel making or electrodes used under elevated temperatures, such as gas arc welders, jigs for glass melting, such as crucibles or mold materials, extrusion dies for metal forming, or jigs such as nozzles or weirs, adapted for quenching and coagulating methods for the preparation of amorphous alloys. Example 1 Powders of ZrB₂ having a purity of not less than 99 % (mean particle size: 3.33 µm) and the powders of Cr₃C₂ (mean particle size: 4.74 µm) were ball-milled and molded by the CIP method for three minutes under a molding pressure of 2.7 tonnes/cm². The molded products were sintered under vacuum atmosphere 0.0133 kPa (10 ⁻¹ mmHg) at 1900°C for 180 minutes for Example Run Nos. 2 to 10 and at 1500°C for 360 minutes for Comparative Example Run Nos. 11 and 12. The physical properties of the sintered bodies, as measured by the following methods, are shown in Table 1. (1) The thermal shock resistance was measured by a quenching strength measurement method. A flexural strength testing piece of 3 X 4 X 40 mm in size was used and heated to a prescribed temperature in an eletrical oven. After the test piece was maintained at this temperature for one hour, it was quenched by being lowered into a water bath of 0°C installed below the oven, and the flexural strength of the test piece was measured by three point bending test. The temperature difference ΔT between the heating temperature when the strength of the test piece was lowered and the water temperature of 0°C was determined. (2) The corrosion resistance was determined from the amount of corrosion of a test piece of 3 X 4 X 40 mm in size which was immersed in a bath of molten ss-41 steel at 1600°C for one hour under an argon atmosphere. In the Table, the marks ○, ▵ and X stand for no corrosion, some corrosion and considerable corrosion, respectively. (3) The anti-oxidation properties were determined from the weight of the oxide after heat treatment at 1200°C for 100 hours in atmosphere. (4) Hv in the Table stands for Vickers hardness. Run No. Composition (Wt. Part) Relative Density (%) Flexural Strength (kg/mm²) Thermal Shock Resistance ΔT(°C) Corrosion Resistance ZrB₂ Cr₃C₂ 1 100 0 57.3 3 - - 2 99.5 0.5 68.2 20 250 ○ 3 97 3 80.7 25 300 ○ 4 95 5 91.8 33 350 ○ 5 90 10 97.3 36 400 ○ 6 85 15 97.1 37 450 ○ 7 80 20 96.7 35 400 ○ 8 70 30 95.3 33 450 ○ 9 60 40 93.9 27 350 ○ 10 50 50 91.8 25 400 ○ 11 30 70 88.5 12 200 ▵ 12 20 80 95.2 18 200 ▵ Referring to Table 1, the sintered product consisting only of ZrB₂ exhibits poor sintering properties and lower strength. On the other hand, the sintered body consisting only of Cr₃C₂ exhibits high sintering density but low strength (See Table 3, Run No. 4 hereinbelow). Addition of 0.5 to 50 % by weight of Cr₃C₂ to ZrB₂ gives a sintered body having high sintering density and strength with superior thermal shock resistance and corrosion resistance. The more the contents of ZrB₂ in the composition, the higher is the preferred sintering temperature. Conversely, the more the contents of Cr₃C₂ in the composition, the lower the preferred sintering temperature. Example 2 Similarly to the preceding Example 1, powders of ZrB₂ and Cr₃C₂ and powders of BN, AlN, B₄C, SiC and TiC each having the purity of not less than 99 %, were ball-milled and molded by the CIP method for three minutes at a molding pressure of 2.7 tonnes/cm². Each of the molded products was sintered in vacuum. The physical properties of the sintered products are shown in Table 2. The amounts of the additional powders, that is, BN, AlN, B₄C, SiC and TiC, are indicated by percent by weight based on the total weight of the starting powder material, the balance containing 90 parts by weight of ZrB₂ and 10 parts by weight of Cr₃C₂. The mean particle size of each of BN, B₄C, SiC and TiC is 5 to 10 µm. It is seen from Table 2 that thermal shock resistance is markedly increased by the addition of BN and sintering properties are increased by the addition of AlN. It is also seen that hardness is mrakedly increased by the addition of B₄C and both sintering density and hardness are improved by the addition of both SiC and TiC. Example 3 Powders of ZrB₂ and TiB₂ each having a purity of not less than 99 % (mean particle size: 3 to 4 µm) and powders of Cr₃C₂ (mean particle size: 4 to 5 µm) were ball-milled and molded by the CIP method for three minutes at a molding pressure of 2.7 tonnes/cm². The molded products were sintered under a vacuum atmosphere at 1600°C for 180 minutes for the Comparative Example Run No.4 and at 1900°C for 180 minutes for the other Runs, and the physical properties of the sintered products were measured in accordance with the Example 1. The results are shown in Table 3. Run No. Composition (Wt. Part) Relative Density (%) Flexural Strength (MPa) Thermal Shock Resistance ΔT(°C) Corrosion Resistance ZrB₂ TiB₂ Cr₃C₂ Comp. Ex. 1 100 - - 57.3 30 200 ▵ 2 - 100 - 86.7 150 250 ▵ 3 50 50 - 76.5 70 200 ▵ 4 - - 100 96.6 10< - - Ex. 5 80 10 10 97.0 335 400 ○ 6 50 40 10 91.1 300 350 ○ 7 10 80 10 92.1 350 400 ○ 8 79.5 20 0.5 89.1 270 250 ○ 9 75 20 5 96.5 330 300 ○ 10 70 10 20 95.8 320 400 ○ 11 60 10 30 90.4 310 400 ○ 12 40 10 50 90.2 295 350 ○ It is seen from Table 3 that the present Example Run Nos. 5 to 12 are superior in corrosion resistance, thermal shock resistance, strength and density as compared to the Comparative Run Nos. 1 to 4. Example 4 Powders of ZrB₂, TiB₂ and Cr₃C₂ of the Example 3 Run No.5 and the respective separate powders of BN, AlN, B₄C, SiC and TiC each having a purity of not less than 99 % (mean particle size: 4 to 5 µm) were metered out each in a prescribed amount and mixed manually in a mortar. The resulting mixtures were molded by the CIP method (2.7 tonnes/cm², 3 min.) and sintered in vacuum at 1900°C for 180 minutes. The physical properties of the mixtures are shown in Table 4. The amounts of the additional starting powders BN, AlN, B₄C, SiC and TiC are expressed in terms of percent by weight based on the total weight of the starting powder material. In Table 4, the anti-oxidation properties were determined from the weight of the oxide produced when the samples were heat-treated at 1200°C for 12 hours under an oxidizing atmosphere. In the Table, ○, ▵ and X stand for oxides not increased, oxides increased slightly and oxides increased markedly or oxides pulverized, respectively. It is seen from Table 4 that the thermal shock resistance is increased markedly by the addition of BN while the hardness is also markedly increased by the addition of SiC and TiC. It is also seen that the strength, hardness and the thermal shock resistance become more balanced and that the excellent corrosion resistance is realized in all of the sintered products.

Claims: A sintered body having high corrosion resistance and containing ZrB₂ obtained by sintering a starting powder material containing not less than 50 % by weight of a starting powder mixture consisting essentially of Cr₃C₂ and ZrB₂ or a starting powder mixture consisting essentially of Cr₃C₂, ZrB₂ and TiB₂ characterized in that the weight ratio of Cr₃C₂ : ZrB₂ or a mixture of ZrB₂ and TiB₂ is 50 to 0.5 : 50 to 99.5. The sintered body according to claim 1 wherein said starting powder material contains 100 % by weight of said starting powder mixture. The sintered body according to claim 1 wherein said starting powder material contains less than 50 % by weight, in addition to said starting powder mixture, of additional starting powders selected from the group consisting of not more than 40 % by weight of BN, not more than 25 % by weight of AlN, not more than 25 % by weight of B₄C, not more than 15 % by weight SiC, not more than 15 % by weight of TiC and mixtures thereof. The sintered body according to claim 1 wherein said starting powder mixture consists essentially of Cr₃C₂, ZrB₂ and TiB₂, the weight ratio of the Cr₃C₂ : ZrB₂ : TiB₂ being 50 to 0.5 : 5 to 94.5 : 94.5 to 5 and the Cr₃C₂, ZrB₂ and TiB₂ together making up 100. The sintered body according to claim 1 wherein said Cr₃C₂ and the boride each have a purity of not less than 99 % and a mean particle size prior to sintering of not more than 10 µm. The sintered body acccording to claim 3 wherein said additional starting powders each have a purity of not less than 99 % and a mean particle size prior to sintering of not more than 10 µm. The sintered body according to claim 1 obtained by sintering said starting powder material at pressure less conditions under an atmosphere selected from the group consisting of vacuum, argon, helium and nitrogen. The sintered body according to claim 7 wherein said sintering is effected at 1400 to 2200°C for 30 minutes to 6 hours.

Inventors: IMAMURA YASUO, ISOZAKI KEI, MATSUNAGA HIROTSUGU, IMAMURA, YASUO, ISOZAKI, KEI, MATSUNAGA, HIROTSUGU
Applicants: DENKI KAGAKU KOGYO KK, DENKI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1988
Main classification: C04B35
IPC codes: C04B35