REINFORCED POLYMER SHEET

Abstract: A process for producing a fibre reinforced polymer sheet by paper-making technology starting from an aqueous dispersion of thermoplastic polymer particles and fibres having a minimum length of 2.0 mm, characterized in that the polymer is an alternating copolymer of an olefinically unsaturated compound and carbon monoxide with a weight average molecular weight of at least 2000 and the fibres are used in an amount of from 5 to 450 pbw per 100 pbw of polymer.

Description: This invention is concerned with a process for producing reinforced polymer sheet by paper-making technology, starting from an aqueous dispersion of a particulate thermoplastic polymer and reinforcing fibres having a minimum length of 2 mm. It is known to produce fibre reinforced polymer articles of manufacture by various methods, e.g. melt-extrusion of a fibre-containing polymer composition to form sheet, film, slabs, tubes, piping, profiles etc., calendering of similar compositions to form sheet or film, injection-moulding, blow-moulding and compression-moulding of similar compositions to form moulded objects, particularly those having a reduced wall-thickness, e.g. cups, bottles and other containers. Such techniques present no particular problems provided staple fibres of relatively short length, i.e. having a length of less than 2 mm, are employed. With longer fibres very few of the above techniques are to date practised on a truly commercial scale since there are very restricted possibilities for achieving the desired degree of homogeneity in the mixture of fibre and polymer at the moment the very moulding or shaping is about to be effected. Since the reinforcing effect is a function of fibre length, there exists a general incentive to employ longer fibres, e.g. having a length of at least 5 mm. It has been proposed to solve the problem related to the processing of long reinforcing fibres in thermoplastics by a completely different technology which is a paper-making process based upon using a thermoplastic polymer in particulate form e.g. a powder or granules, ground down to a very small particle size, as binder for the fibres. Thus, a paper is produced when the fibres are cellulose fibres, or a paper-like material or synthetic paper can be produced from metal fibres, glass fibres, carbon fibres, nylon fibres, polyaramid fibres, etc. The commercial development of this different technology basically hinges around the use of olefin polymers, e.g. polyethylene, polypropylene or polybutene as the binding polymer. (c.f. EP-A 69650, EP-A 100726, EP-A 180863 and FR-A 2530274). The binding performance of such polyolefins is however rather poor, most likely due to their outspoken hydrophobic properties. Because of this it is necessary to use various surfactants, detergents or flocculating agents in order to improve wettability performance. These auxiliary agents may even have to be employed at different stages of the paper-making process, which significantly complicates the technology. There is thus a need to find a simplified process. Unexpectedly, the Applicants have found that another thermoplastic polymer has a very attractive wettability and that there is no strict need to employ the auxiliary agents referred to hereinabove. This polymer is an alternating copolymer of carbon monoxide and an olefinically unsaturated compound, provided its weight average molecular weight is at least 2000, preferably at least 6000. Therefore, the present invention is concerned with a process for producing a fibre reinforced polymer sheet by paper-making technology starting from an aqueous dispersion of a particulate thermoplastic polymer having a weight average molecular weight of at least 2000 and fibres having a minimum length of 2.0 mm which fibres are used in an amount of from 5 to 450 pbw per 100 pbw of polymer, characterized in that the polymer is an alternating copolymer of carbon monoxide and an olefinically unsaturated compound and in that the process is carried out in the absence of a surfactant, a detergent or a flocculating agent. The fibres are preferably employed in an amount of from 20 to 200 pbw per 100 pbw of copolymer. The particle size of the copolymer should be such that adequate handling of the product in the machinery is obtained. Both the presence of particles which are too small or too large for this purpose is to be avoided. Preferred particle sizes are of from 0.01 to 0.75 mm, best of all selected in the range of from 0.05 to 0.3 mm. Preferred fibre lengths are at least 4.5 mm. Alternating copolymers of olefinically unsaturated compounds and carbon monoxide are known per se. They can be produced with a catalytic copolymerization process disclosed for example in EP-A 121965, and EP-A 181014. The term "copolymer" as used in this specification includes terpolymers of an olefinically unsaturated compound, e.g. ethylene carbon monoxide and another olefinically unsaturated compound such as styrene, norbornene, propylene, butene-1, decene, vinylacetate, etc. The term "alternating" as used herein defines those copolymers having the general formula in which units -A- are derived from the olefinically unsaturated compound, e.g. -CH₂-CH₂-in a copolymer of ethylene and carbon monoxide. In a terpolymer some of the units -A- are replaced by a unit of another olefinically unsaturated compound. Such substitution effects a lowering of the melting point of the carbon monoxide copolymer, preferred terpolymers are those of ethylene, propylene and carbon monoxide having a melting point in the range of from 215 to 240 °C. Preferred copolymers are copolymers of ethylene and carbon monoxide. The implementation of the process of this invention presents no problems to those skilled in the art. A homogeneous dispersion in water of reinforcing fibres and polymer particles is brought on the filtering equipment of a paper-making machine, the water is drained-off, thus yielding after drying at elevated temperature a self-supporting sheet of reinforced polymer. For further processing several of these sheets can be stacked together and compression moulded at a temperature around or above the melting point of the polymer. Compression-moulding can also be carried out with stacked sheets that have been united to form one coherent sheet of increased thickness in a previous forming operation, e.g. calendering, in which use may be made of adhesive films or coatings on the various layers of sheets. The reinforced copolymer compositions of this invention may further comprise various additives such as fillers, colourants, plasticizers, thermostabilizers or antioxidants. Other polymeric constituents may be incorporated as well, for example polyethylene or polypropylene and it is also possible to use hybrids as reinforcing fibres. The invention is illustrated herein with Examples which are not intended to restrict the scope of the working conditions for practising the process of the invention. EXAMPLES A powder of an ethylene/propylene/carbon monoxide terpolymer, with a crystalline melting point of 221 °C and an intrinsic viscosity of 1.01 dl.g⁻¹ (determined in m-cresol at 85 °C), was stirred to a dense suspension in demineralized water not containing any surfactant or flocculant. Then various fibres were added as indicated in the Table below, all fibres had a length of 6 mm. The fibres were defibrillated by continuous, vigorous stirring of the suspension having a solids content of 1 g.l⁻¹. Then, the suspension was poured onto a filter, water was drained off. The resulting, self-supporting sheet was positioned between two layers of filter paper, and rolled with a heavy roller to absorb most of the water in the wet sheet. Final drying was effected by drying overnight at ambient temperature and in a vacuum oven under N₂ at 50 °C for 3 hours. Each single sheet was compression-moulded in a hot press using 1 mm thick metal supports. Four compression-moulded sheets were stacked, preheated in an oven at 110 °C and once more compression-moulded at 235 °C to obtain a test-sheet with a thickness of 0.7 to 1.0 mm. For reference purpose single sheets of terpolymer were produced by compression-moulding of terpolymer powder at the same temperature. Four sheets so obtained were then stacked and compression-moulded at 235 °C to obtain a test-sheet with a thickness of 0.7 to 1.0 mm. In the Table the reported amounts of fibre are pbw per 100 pbw of terpolymer. All moulded samples of reinforced polymer showed a homogeneous distribution of fibrillated fibres in the polymer matrix.

Claims: A process for producing a fibre reinforced polymer sheet by paper-making technology starting from an aqueous dispersion of a particulate thermoplastic polymer having a weight average molecular weight of at least 2000 and fibres having a minimum length of 2.0 mm which fibres are used in an amount of from 5 to 450 pbw per 100 pbw of polymer, characterized in that the polymer is an alternating copolymer of carbon monoxide and an olefinically unsaturated compound and in that the process is carried out in the absence of a surfactant, a detergent or a flocculating agent. A process as claimed in claim 1, wherein the molecular weight of the copolymer is at least 6000. A process as claimed in claim 1 or 2, wherein the fibres are used in an amount of from 20 to 200 pbw per 100 pbw of polymer. A process as claimed in any one of claims 1 to 3 wherein the particle size of the copolymer is selected within the range of from 0.01 to 0.75 mm. A process as claimed in claim 4, wherein the particle size of the copolymer is selected within the range of 0.05 to 0.30 mm. A process as claimed in any one of claims 1 to 5 wherein the copolymer is a terpolymer of ethylene, carbon monoxide and propylene. A process as claimed in claim 6, in which a terpolymer having a melting point of from 215 to 240 °C is employed. A process as claimed in any one of claims 1 to 5, in which the copolymer is a copolymer of ethylene and carbon monoxide.

Inventors: GILLEMANS, JOHANNES CAROLUS MARIA, VAN BREEN, ADRIAAN WOUTER
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1988
Main classification: C08K7
IPC codes: C08J3, D21H13, C08K7, C08J5, D21H21, B32B17, D21H17, B29C41, C08L73