METHOD FOR PREPARATION OF DIALKYL TELLURIUM AND DIALKYL SELENIUM

Abstract: A method for preparing tellurium and selenium dialkyls in a substantially pure state which comprises reacting the Group VI element or the Group IV halide thereof with a Group I metal alkyl within a solvent selected from C4-C10 aliphatic ether and which also may optionally contain liquid alkane, the product of which may be used directly or further purified for use in semiconductor technology such as cadmium mercury telluride infra-red detectors.

Description: Method for Preparation of Dialkyl Tellurium and ialkyl Selenium This invention relates to a method for the preparation of dialkyl of the Group VI metals tellurium and selenium. The metals Tellurium and Selenium are of importance in semi¬ conductor technology, for example in the preparation of the infra red detector material cadmium mercury telluride (CMT) and in light sensing switches respectively. It is well known that the presence of impurities in semi¬ conductor materials is extremely undesirable. It is therefore useful to be able to prepare semiconductor materials and chemical precursors used in their manufacture in a high degree of purity. An important series of such chemical precursors is the alkyls of the relevant semiconductor material, which can relatively easily be thermally dissociated to form an epitaxial layer of the material or a layer containing the material. Such alkyls have the additional advantage that they are otherwise relatively stable and may be purified further via the formation of adducts with for example lewis base adjuvants such as trialkyl or triaryl Group V compounds. The formation of various addjucts for semiconductor purifi¬ cation is described for example in GB 850955-A, together with a method for preparation of Group II metal alkyls. The preparation of other alkyls can present problems, and in particular the prep¬ aration of the Group VI alkyls such as those of tellurium and selenium in a pure state has until now presented great difficulty. At present methods for preparation of tellurium alkyls are known. Synthetic Communications 12(3), (1982), 163-165 describes a method for preparation of dialkyl ditellurium by reaction of the corresponding lithium alkyl and elemental tellurium in THF with atmospheric oxidation, tellurium dialkyl not being formed. Similarly J. Organometallic Chemistry 255, (1983), 61-70 describes the preparation of mixtures of tellurium dialkyls and ditellurium dialkyls by reaction of the corresponding Grignard reagent RMgCl with tellurium IV chloride. This reaction is believed to result in contamination of the product with RTeCl. The present invention seeks to overcome or alleviate the problems outlined above by providing a method for the preparation of dialkyls of tellurium and selenium in a substantially more pure state, or at least in a state that facilitates further purification. Other objects and advantages of the present invention will be apparent from the following description. According to the present invention a method for the preparation of dialkyl tellurium or dialkyl selenium comprises reacting either elemental tellurium or elemental selenium, or a tellurium IV or selenium IV halide with a Group I metal alkyl in a solvent which is or contains at least one C^-C-^Q aliphatic ether, and optionally also contains a liquid alkane. The reaction is preferably carried out under conditions which exclude atmospheric oxygen, for example under an inert atmosphere eg nitrogen. Oxidation by the atmosphere can result in impurities. A preferred temperature is below 20°C, especially -40 C to 0 C. Above room temperature impurities may be formed, such as neohexyl Group I metal alkyls. The method is suitable for the preparation of all dialkyls, but is especially suitable or the preparation of di- C, - C j , alkyls of tellurium and selenium, which may be straight chain, branched or tertiary alkyls, for example tellurium and selenium iimethyl, diethyl, άipropyl (n- and iso-) or butyl (n-, iso- and tert.-), especially tellurium dimethyl and li-tert.- " butyl. The Group I metal is preferably lithium, sodium or potassium, especially lithium. Preferred Group I metal alkyls are therefore MeLi and tert.-BuLi. Preferabl?/ the ether is a di- C 2 - Gc alkyl ether, especially a di-n-alkyl ether. The alkyl groups of the dialkyl or di-n-alkyl ether may be the same or different and a particularly preferred ether is diethyl ether. Whatever ether is/are used, it/they should preferably have a low " boiling, point. If an alkane is present it must be liquid at the reaction temp¬ erature, an--, suitable alkanes include n-pentane. When a halide of the Group VI element is used it is preferably the chloride, eg Te(lV)Gl,, or Se(l7)θή.. The reaction is preferably carried out using about stoichio- metric quantities of the reactants. Preferably the Group I metal alkyl is dissolved in the alkane, and this solution is added slowly to the element or halide suspended or dissolved in the ether. Following reaction the mixture may be stood at room temperature or refluxed if necessary to ensure completion. The solution of the dialkyl product may be separated from solid residues by filtration. Excess Group I alkyl may be destroyed by adding water. The tellurium or selenium dialkyl may then be isolated by evaporation of "the solvent followed by vacuum distillation. The method of the invention provides dialkyls of tellurium or selenium suitable for use in semiconductor formation, eg in epitaxial deposition. It may however be preferable in some cases to further purify the dialkyls by the known process of secondary adduct formation to produce an adduct with a lower dissociation temperature than that of the dialkyl itself at the pressure of secondary adduct dissociation. Other known further purification methods may be used. The Group VI dialkyls produced using the method of this invention also constitute a novel product, being in a generally purer form than h s been hithertoo available using known preparation processes. The invention will now be described by way o^ example only, (note: in this patent application the abbreviations Me = methyl, St = ethyl, Pr - propyl and Bu = butyl are used ). EXAMPLE 1 Synthesis of di-tert-butyl tellurium from elemental teliurini. ar.d t-3u i in Ξt„0 A solution of tert-butyllithium (450 cm 3 , 1.7 moles dm -3 ) in pentane was added dropwise to an ethereal suspension (300 cm 3 ) of elemental tellurium (90 g, 0.70 g atom) maintained at -40-0°C over a period of 5h. An exothermic reaction occurred and the reaction 5 mixture was stirred for lh after the complete addition, and was then refluxed for 2h. The deep yellow ether-pentane solution of di-tert- butyl tellurium was isolated from excess tellurium and the resulting lithium telluride by filtration. Water was added to destroy any excess tert-butyl lithium. The ether-pentane solution of di—tert- 0 butyl tellurium was separated, dried over anhydrous calcium chloride and, after filtration, diethyl ether and pentane were removed in vacuo. The resulting deep yellow oil was purified by vacuum distillation over calcium hydride. Overall yield = 49%. EXAMPLE 2 ^ Preparation of Di-tert-butyl tellurium from tetrachlorotell riu (IV) and t-3uli in St ϋ A solution of tert-butyllithium (830 cm 3 , 1.7 moles dm -3 ) in pentane was added dropwise to an ethereal solution of tellurium(IV) 0 chloride (100 g, 0.37 g moles) at 0°C over 6h. An exothermic reaction occurred and the reaction mixture was stirred for lh after the complete addition, and was then refluxed for 2h. The pale yellow ether-pentane solution of di-tert-butyl-tellurium was isolated from the resulting lithium chloride by filtration. Water c was added to destroy any excess tert-butyl-lithium. The ether pentane solution of di—tert-butyltellurium was separated, dried over anhydrous calcium chloride and after filtration, diethyl ether and pentane were removed in vacuo. The resulting deep yellow oil was purified by vacuum distillation over calcium hydride. Overall ~c yield = 62%. EXAMPLE 3 Synthesis of dimethyltelluride from elemental tellurium and methyl]ithium in Ξ gO• To a grey suspension of elemental tellurium (27.11 g, 0.2124 g atom) in diethyl ether (150 cm 3 ) maintained at temperature between -40-0°C was added a pentane solution of methyllithium (140 cm 3 , 1.5 moles dm 3 ) dropwise over a period of 2h. An exothermic reaction was found to occur. When the addition of methyllithium was complete the reaction mixture was brought to room temperature and was heated under a gentle reflux for a further 2h. The reaction product at this stage consisted of a red supernatant solution and a white amorphous residue. The red supernatant solution was isolated from the white residue by filtration and was then treated with distilled water (50 cm 3 ) to destroy any unreacted methyllithium. The ethereal solution was isolated from the aqueous layer dried over anhydrous calcium chloride, and after filtration, diethyl ether and pentane were removed by fractional distillation at 1 atmos. pressure under dry nitrogen. The dimethyltelluride was distilled at 1 atm (B.P. 83-84°C) and the resulting yellow oil was purified by vac urn distillation (overall yield = 85%).

Claims: CLAIMS 1. A method for the preparation of dialkyl tellurium or -ialkyl selenium characterised by reacting either elemental tellurium or elemental selenium, or a tellurium (IV) halide or selenium (IV) halide with a Group (l) metal alkyl in a solvent which is or contains at l3ast one ~ - ~ ~ - r\ aliphatic ether and optionally also contains a liquid alkane. 2. A methoi according to claim 1 characterised in that the dialkyl tellurium or selenium is a di- G 1 to C^ alkyl. 3- A method according to claim 2 characterised in that di-tert - butyl tellurium is prepared. - A method according' to claim 2 characterised in that dimethyl tellurium is prepared 5 A method according to claim 1 characteriseI in that the haliie of tellurium (IV) or selenium (IV) is the chloride. 6- A metho' 7 according to any one o^ the preceding claims charact¬ erised fn that the Group (i) metal iε lithium, potassium or sodium. 7- A metho according to claim 6 characterised in that the Group (i) metal iε lithium. 8. A method according to claim 6 characterised in that the Group (i) metal alkyl is lithium, sodium or potassium methyl, ethyl, propyl (n- or iso-) or butyl (τx- , iso- or tert.-). 9- A method according to claim 3 characterised in that the Group (i) metal alkyl is tert.-butyllithium or methyllithium. 10. A method according to claim 1 characterised in that the solvent iε a dialkyl ether. 11 A method according to claim 10 characterised in that the solvent is ;iethyl ether. 12 A method according to claim 1 characterise in that the reaction iε carried out under conditions which exclude atmospheric oxygen 1°- A rae ho" according to claim 1 characterised in that the reaction is carried out below 20 G. W . A. metho~ according to claim 13 characterised in that the reaction iε carried out at -4*0°C to 0°C. 15- A method according to claim 1 characterised in that di- tert-butyl tellurium is prepared by the reaction of t-BuLi with elemental tellurium at a temperature belcw 20°C in a solvent that contains diethyl ether. 16. A methc". according to claim 1 characterise3. in that di- tert-butyl tellurium iε prepared by the reaction of t-BuLi with tetrε.chlorotellurium (IV) at a temperature below 20°G in a solvent that contains diethyl ether. 17- A metho " according to claim 1 characterised in that di¬ methyl tellurium iε prepared by the reaction of methyllithium with elemental tellurium at a temperature below 20 C in a solvent that contains diethyl ether. 1*3. A dialkyl of tellurium or selenium when prepared by a proceεε according to any one of claims 1, 2, 5 , , 15, 16 or 17.

Inventors: COLE-HAMILTON DAVID JOHN, MULLIN JOHN BRIAN, SHENAI-KHATKHATE DEODATTA VINA, WEBB PAUL, COLE-HAMILTON, DAVID, JOHN, MULLIN, JOHN, BRIAN, SHENAI-KHATKHATE, DEODATTA, VINAYAK, WEBB, PAUL
Applicants: SECR DEFENCE BRIT, THE SECRETARY OF STATE FOR DEFENCE IN HER BRITANNI
Application year: 1988
Main classification: C07C163
IPC codes: C07C391, C07C395