IMPACT RESISTANT POLYETHYLENE TEREPHTALATE/POLYCARBONATE BLENDS

Abstract: High impact strength blends based on polyethylene terephthalate resin, aromatic polycarbonate resin and styrene-acrylonitrile grafted copolymers of EPDM.

Description: This invention relates to an improved high impact composition comprising a blend of recycled or reclaimed polyethylene terephthalate resin, polycarbonate resin and a grafted EPDM copolymer composition. BACKGROUND OF THE INVENTION Products designed around thermoplastic polyester resins are in great demand because of the tremendous versatility of these resins and their inherent properties. The term thermoplastic polyester refers to high molecular weight polyester and copolyesters of glycols and dibasic acids such as terephthalic or isophthalic acid. These are described for example in U.S. Patents 2,465,319 and 3,047,539. Because of its rapid crystallization rate, polybutylene terephthalate (PBT) has been preferred for injection molded articles while polyethylene terephthalate (PET), with its very slow crystallization rate, has largely been used in packaging. Nucleating agents have been used to increase the crystallization rate, and post molding heat treatment (annealing) can be used to crystallize molded articles made of PET. The crystallized PET tends to higher tensile strength, stiffness, and heat resistance compared to uncrystallized PET. Nucleating agents and/or annealing are generally not required to crystallize molded PBT articles. In order to improve the overall property spectrum of PET, the resin has often been blended with numerous other resins. Specific additives are also incorporated to increase the general level of the impact strength of the PET containing blends as well as the consistency of the impact property in a molded article. Illustrative of the specific additives or impact modifiers that have been proposed to be used with thermoplastic polyester resins are the family of modifiers comprising polyalkyl acrylates, methacrylates, and/or ethacrylates (Brinkmann et al; U.S. Patent 3,591,659) typical of which is Acryloid KM-330, a polyacrylate resin sold by Rohm & Haas Co. Certain rubber resin graft copolymers have also been proposed to effect impact resistance of polyester resins. In U.S. Patent No. 3,919,353 (Castelnuovo et al) EPDM grafted with common ethylenically unsaturated monomers is disclosed to be an effective impact modifier. Polybutadiene is taught to be the preferred elastomer. All of the examples use polybutadiene grafted with styrene-methyl methacrylates and the elastomer is crosslinked. One of the resin blends preferred for its overall balance of molded properties is that comprising polyesters and polycarbonate (PC) resins. It should be noted that the impact strength at room temperature of most polycarbonates is relatively high. For example, the Notched Izod Impact at Room Temperature (NIRT)(ft-1b/in.) of numerous commercial polycarbonates such as LEXAN 103 (trade mark of General Electric) is often in the range of from about 16 to 20 ft-lb/in (800 to 1000 Jm⁻¹. However, to obtain maximum chemical resistance of polyester/polycarbonate blends, it is desirable to keep the polycarbonate content low. Furthermore, polycarbonate resin is susceptible to mechanical stress cracking which can be exacerbated by exposure to unfavourable environments such as the presence of solvents or solvent vapors. This tendency to stress crack provides an additional reason to utilize as little polycarbonate resin as possible in these polyester blends. When adding impact modifiers to polyethylene terephthalate/polycarbonate blends, susceptibility to the effects of ester interchange on the final blend properties must also be taken into account. Blends produced under high shear conditions may have unpredictable properties due to reaction (ester interchange) between the polyester and polycarbonate components. The ester interchange reaction can be minimised, of course, by the use of inhibitors and/or by lowering the shear level. Various blends based on polyester resin, polycarbonate resin and graft copolymer rubber-resin materials have heretofore been proposed (eg US Patent Nos 3591659, 3919353, 4022748, 4034013, 4034016, 4044073, 4096202, 4260690 and 4280949). US Patent No 4257937 teaches the impact modification of polyester/polycarbonate blends via a polyacrylate resin such as Acryoid KM-330 and 7709-XP (trademarks of Rohm & Haas Co.) U.S. Patent No. 4,172,859 (Epstein) discloses blends of polyesters, polycarbonate and an impact modifier which can comprise various monomers, combinations of which can include EPDM. U.S. Patent No. 4,493,921 represents another step in the continuing effort to improve the level of performance of polyester-type resin/polycarbonate-type blends via the addition to polybutylene terephthalate (PBT)/PC blends of an impact modifier comprising an ethylene-propylene-non-conjugated diene (EPDM) rubber spine grafted with either a styrene/acrylonitrile monomer mixture, a styrene/methyl methacrylate monomer mixture or a methyl methacrylate monomer mixture. EP-A- 0 135 677 discloses resin compositions comprising PBT or PET and EPDM graft impact modifiers. One of the art recognized difficulties realized in the impact-modification polyester art is the unpredictability of the modifier effect, i.e., a modifier that enhances the properties of one polyester such as polybutylene terephthalate (PBT) or a PBT resin blend, may have little property modification in a different polyester or polyester blend. For example, certain polyacrylate modifiers such as Acryloid KM-330, while capable of significantly improving the impact properties of a PBT/PC resin blend, will have much less effect on a PET/PC blend. SUMMARY OF THE INVENTION A graft copolymer rubber resin material has been found that significantly enhances on a broad spectrum the physical properties of recycled or reclaimed polyethylene terephthalate/polycarbonate resin blends. In accordance with this invention rubbery spine polymer of a certain EPDM having grafted thereon styrene-acrylonitrile monomeric material based on comparisons with similarly structured materials, has been found to unexpectedly increase the impact properties of PET/PC blends. DETAILED DESCRIPTION OF THE INVENTION The present invention is based on a blend of a) recycled or reclaimed polyethylene terephthalate resin, b) polycarbonate resin and c) graft copolymer composition comprising EPDM-type rubber grafted with styrene-acrylonitrile monomers. These blends have high impact properties even at low polycarbonate levels. Preparations of polyethylene terephthalates are well known in the art and a basic description is described, for example, in U.S. Patent Nos. 2,465,319 and 2,471,023. Polycarbonate resins can be made by known processes and they are available commercially from many sources, e.g., General Electric Co., Pittsfield, MA, U.S.A. under the trademark LEXAN. In general, any of the aromatic polycarbonates described in U.S. Patent No. 4,034,016; 4,257,937 and/or 4,280,949 can be used, especially those including units derived from bisphenol-A. The graft copolymer material (c) constituting the third component of the invention is based on a graft copolymer of resin-forming monomeric material on a rubbery unsaturated spine polymer of ethylene-propylene-non-conjugated diene (EPDM). The preferred non-conjugated diene is ethylidene norbornene. The grafted monomeric resin comprises the monomers styrene (which also includes substituted styrenes) and acrylonitrile. The styrene:acrylonitrile monomer ratios are in the range of from 90:10 to 40:60; preferably from 90:10 to 50:50; and most preferably from 80:20 to 60:40. It will be understood that in practice the product of the graft copolymerization process is actually a mixture of true graft of resin on rubber along with a certain amount of separate, ungrafted resin (that is, the grafting efficiency is not 100 percent; see U.S. Pat. No. 4,202,948, Peascoe.) The graft copolymer of the present invention is an ethylene-propylene-non-conjugated diene terpolymer upon which is grafted a "graft resin". The method by which the graft copolymer is formed, that is, the method by which the styrene-acrylonitrile graft resin is grafted onto the ethylene-propylene-non-conjugated diene terpolymer is set forth in detail in U.S. Patents 3,489,821; 3,489,822; and 3,642,950. It is The graft copolymers of the present invention include a graft resin constituency, that is a styrene-acrylonitrile concentration, comprising between about 5 percent and 75 percent by weight, based on a total weight of the graft copolymer. More preferably, the graft resin comprises between about 30 percent and 70 percent by weight, based on the total weight of the graft copolymer. Most preferably, the graft resin comprises between about 40 percent and 60 percent by weight, based on the total weight of the graft copolymer. The terpolymer of the present invention to which the graft resin is attached is characterised by a weight ratio of ethylene to propylene in the range of between about 50:50 and 75:25. Further, the ethylene-propylene-non-conjugated diene terpolymer, so-called "rubber" portion of the graft copolymer, possesses an intrinsic viscosity, as measured in tetralin at 135°C, in the range of between about 1.5 and 2.6. The Mooney Viscosity (ML-4 at 275°F(125°C) of the rubber portion is in the range between about 30 to 100. Typically, the ungrafted rubber is defined by an Iodine number in the range of between about 4 and 30. Generally, the proportion of the three polymeric ingredients may vary, as indicated in the following table, wherein the amounts are expressed in parts by weight per 100 parts of blend: Parts by Weight Broad Preferred More Preferred (a) recycled Polyester resin 20 or more 20 or more 40 or more (b) Polycarbonate resin 20-60 20-50 20-40 (c) Graft copolymer 20-50 20-40 20-30 The total amount of the polycarbonate resin and the graft copolymer should be greater than 40% by weight of the PET/PC/graft copolymer blend. Preferred compositions tend to include a major proportion of the polyester resin component (a) which combines good moldability and good properties at elevated temperature, along with sufficient polycarbonate resin (b) and graft copolymer (c) to provide high notched impact strength. Although it is possible to use modifier (c) levels above about 30%, such an increase would tend to decrease hardness, tensile strength and stiffness. Blends containing 40% (or more) of polycarbonate (b) are capable of providing satisfactory results. To prepare the blends of the invention, the PET resin component (a), the polycarbonate resin component (b), and the graft copolymer composition (c) are mixed together at elevated temperature in conventional plastics mixing equipment, such as a twin screw extruder-mixer. If desired, any two of the components may be mixed together first, followed by mixing in of the third component. One desirable mixing procedure is a two-step compounding process involving first working the graft copolymer compositions (c) without the other ingredients (a) and (b), under shearing and fluxing conditions, for example in a twin screw extruder-mixer. This disperses the EPDM within the resin contained in the graft copolymer composition to form an "inverted" composition in which the EPDM rubber is a discontinuous phase. The second step involves fluxing the inverted graft component (c) with the PET component (a) and the polycarbonate component (b) under lower shear conditions, for example in a single screw extruder. In commercial practice these two steps can be combined in one extrusion operation, using an extruder having a first and second feedport; a section of the extruder downstream of the first feedport can be used to shear (invert) the graft copolymer (c) and a section downstream of the second feedport can be used to mix the graft with the other ingredients (a) and (b). The inverted graft composition (a) may also be pelletized and tumble blended with PET (a) and polycarbonate (b) pellets to form a physical mixture which can be fed into an injection molding machine or an extruder. In this case the plasticissing screw of the injection or extrusion machine can perform the second stage of the mixing during fabrication. As indicated, the invention is based on the discovery that three-component blends of recycled polyethylene terephthalate (PET) with polycarbonate (PC) and ethylene-propylene-ethylidene norbornene (EPDM) grafted with styrene-acrylonitrile resin have unexpectedly high impact strength as well as a broad spectrum of other highly desirable physical and chemical properties. The following examples will serve to illustrate and delineate the practice of the inventions in more detail. Comparative Examples 1-6 The following examples illustrate the impact results realised via the use of the polyacrylate impact modifier Acryloid KM-330 (a trade mark of Rohm and Haas) in polyethylene terephthalate/polycarbonate and polybutylene terephthalate/polycarbonate blends. The blends listed in Table 1 are prepared by fluxing the Acryloid KM-330 with PET (KODAPAK 7352; trade mark EASTMAN CHEMICALS) or PBT (VALOX 310; trade mark of General Electric Co.); and polycarbonate resin (reaction product of bis-phenol with phosgene (LEXAN 141; a trade mark of General Electric Co.) in a 1" (25mm) single-screw extruder equipped with strand die and pelletizer. Specimens for mechanical property testing are cut from 1/8 inch (3.2 mm) injection molded plaques. In Table 1 (and the remaining Tables) the amounts of each comonent are express in parts by weight; PET stands for the polethylene terephthalate; PBT stands for the polybutylene terephthalate; PC stands for the polycarbonate resin: NIRT stans for Notched Izod Impact Strength at room temperature (reported in Joules per metre of notch). NIRT (annealed) means Notched Izod Impact Strength at room temperature determined after annealing the specimen for 2 hours at 150°C in a circulating air oven. The annealing process causes the PET to crystallize and will tend to increase tensile and stiffness of the blend. The PBT blends are crystallized as molded. Comparative Examples 1 2 3 4 5 6 Acryloid KM-330 10 20 30 10 20 30 PET 70 60 50 PBT 70 60 50 PC 20 20 20 20 20 20 NIRT (As molded) 164 1124 943 80 795 624 NIRT (annealed) -- -- -- 53 107 117 The above comparative examples show that although a given polyacrylate additive may perform satisfactorily as an impact modifier for certain polyester/polycargbonate blends, specifically PBT/PC blends, one cannot predict that the additive will affect the impact properties of another polyester, albeit a homologous one, in a similar manner. Comparative Examples 7-14 Three graft copolymers, designated A, B and C in TABLE II below, are prepared by the slurry technique described in US Patent No 4202948 (Peascoe) using an ethylene-propylene-ethylidene norbornene EPDM terpolymer rubber (E/P ratio 60/40; Mooney viscosity 68 ML-4 @ 275°F (125°C); iodine number 20) as the spine rubber. The resin forming monomers in each graft are indicated in TABLE II, which gives the composition of the resin portion of the graft copolymers. The overall resin/EPDM ratio in the graft copolymer is 50/50 in each case. Resin Ratio A Styrene/Acrylonitrile 72/28 B Styrene/Methyl Methacrylate 50/50 C Methyl Methacrylate 100 The blends listed in TABLE III are prepared by first fluxing the graft copolymers (A, B or C) in a 53 mm Werner and Pfliederer twin-screw extruder equipped with a strand die and pelletizer. The pelletized grafts are then fluxed with PBT (VALOX 310; a trade mark of General Electric Co.) and polycarbonate resin (reaction product of bisphenol A with phosgene; LEXAN 103 (trade mark of General Electric)) in a one-inch (2.5 cm) single-screw extruder to make the blend shwon in TABLE III. Specimens for mechanical property testing are cut from 1/8 inch (3.2 mm) injection molded plaques. (See our US Patent No 4493921). Comparative Examples 7 8 9 10 11 12 13 14 B 20 10 30 20 C 20 A 20 30 20 PBT 60 60 60 70 50 50 40 40 PC 20 20 20 20 20 20 40 40 NIRT 950 801 955 139 1024 1010 975 865 The above comparative examples show that in PBT/PC blends, incorporation of graft copolymers comprising ethylene-propylene-non-conjugated diene rubbery spine having grafted thereon either styrene-acrylonitrile resin methyl methacrylate resin or styrene-methylmethacrylate resin, results in similar, ie, equivalent enhancement of impact strength properties provided at least 20% of the modifier is present. Examples 1-6 Graft copolymer F is prepared by the slurry technique described in US Patent No 4202948 (Peascoe). The graft copolymer F used an ethylene-propylene-ethylidene-norbornene EPDM terpolymer rubber (E/P ratio 60/40; Mooney viscosity 68 ML-4 at 257°F (125°C), iodine number 20) as the spine rubber. The resin of graft coplymer F is a styrene-acrylonitrile resin with a ratio of 72/28. The weight ratio of EPDM to resin is 50:50. The blends listed in TABLE IV are prepared by first fluxing the graft copolymer in a 53 mm Werner and Pfleiderer twin-screw extruder equipped with a strnad die and pelletizer. The pelletized graft is then fluxed with PET (KODAPAK 7352; a trade mark of Eastman Chemicals) and polycarbonate resin (reaction product of bis-phenol A with phosgene (LEXAN 141; a trade mark of General Electric Co.) in a one-inch (25 mm) single-screw extruder to make the blends. Specimens for mechanical property testing are cut from 1/8 inch (3.2 mm) injection molded plaques. The following examples illustrate the totally unexpected additional increase in Notched Izod impact values, especially at low temperatures, realized by utilizing the specific graft copolymers of this invention in blends of polycarbonate with reclaimed or recycled polyethylene terephthalate resin, i.e., resin that had had a processing history that included a molding step or cycle over similar blends containing virgin or not previously molded PET resin. Virgin PET is a polyethylene terephthalate copolymer made by Eastman Chemicals (KODAPAK 7352) having an inherent viscosity (in phenol/tetrachloroethane (60/40)) of 0.70. Reclaim PET is recycled polyethylene terephthalate resin primarily from ground beverage bottles having an inherent viscosity (in phenol/tetrachloroethane (60/40)) of 0.68 obtained from NYCONN Industries. The above data illustrates that the utilization of the graft copolymers of this invention is able to realize Notched Izod impact properties in scrap or reclaimed PET/PC blends that equal and oftimes exceed the values acheived via the use of previously unmolded PET resin in the blends: the effect being especially noticeable at low temperatures. The foregoing examples may be repeated using other aromatic polycarbonate resins; polyethylene terephthalate resins; or ethylene-propylene-non-conjugated diene terpolymers grafted as set forth above.

Claims: A thermoplastic polyester blend characterised in comprising: a) 20 or more parts of reclaimed or recycled polyethylene terephthalate resin; b) 20-60 parts polycarbonate resin;and c) 20-50 parts graft copolymer of styrene-acrylonitrile resin on an ethylene-propylene-non- conjugated diene rubber spine having an ethylene propylene weight ratio of 50:50 to 75:25,a Mooney viscosity at 125°C of 30 to 100 and an intrinsic viscosity as measured in tetralin at 135°C in the range of 1,5 to 2,6 ;said styrene acrylonitrile resin being present in an amount of 5 to 75% by weight of the graft copolymer; and wherein the proportions of (a),(b) and (c) are expressed in parts by weight per 100 parts of (a),(b) and (c), and the combined parts by weight of (b) and (c) is greater than 40. A blend according to Claim 1 wherein the conjugated diene of the ethylene-propylene-non-conjucated diene rubber spine in the graft copolymer of styrene-acrylonitrile resin is ethylidene norbornene. A blend according to Claim 1 wherein the graft copolymer is an inverted composition in which the rubber is the discontinuous phase. A blend as claimed in Claim 1 wherein the proportions of (a), (b) and (c) are: (a) 20 or more (b) 20-50 (c) 20-40 A blend as claimed in Claim 1 wherein the proportions of (a), (b) and (c) are: (a) 20 or more (b) 20-40 (c) 20-30 A method of making a blend of (a) 20 or more parts polyethylene terephthalate resin; (b) 20-60 parts polycarbonate resin; and (c) 20-50 parts graft copolymer of styrene-acrylonitrile resin on an ethylene-propylene-ethylidene norbornene rubber spine, said styrene-acrylonitrile resin being present in an amount of about 30-70% weight of the graft copolymer, and wherein the proportions of (a), (b) and (c) are expressed in parts by weight per 100 parts of (a), (b) and (c), and the combined parts by weights of (b) and (c) is greater than 40; said method comprising: working the graft copolymer (c) under shearing and fluxing conditions to disperse the rubber portion of the graft within the resinous portion thereof, thus forming an inverted composition in which the rubber portion is a discontinuous phase, and thereafter blending the resulting inverted graft with components (a) and (b), A method of making a blend as claimed in Claim 7 wherein the proportions of (a), (b) and (c) are as follows: (a) 20 or more (b) 20-50 (c) 20-40 A method as claimed in claims 6 or 7 ,wherein said polyethylene terephthalate resin is recycled or reclaimed from ground beverage bottles. A method as claimed in claims 6 to 8 comprising the further steps of molding to form an article and annealing the article.

Inventors: WEFER, JOHN MICHAEL
Applicants: UNIROYAL CHEMICAL COMPANY, INC.
Application year: 1988
Main classification: C08L67
IPC codes: C08L51, C08L69, C08L67