Superconductor structure

Abstract: A superconductive structure comprising a crystalline coating (12) applied to a substrate (11) and a crystalline superconducting film (13) epitaxially deposited on said crystalline coating (12). Especially CaF₂ crystals and ZrO₂ crystals with a CaF₂ crystal structure show good lattice matching with semiconductor substrate materials such as Si, GaAs, etc., as well as with superconducting materials comprising copper oxide. The crystalline coating (12) may be made of a material having a perovskite structure, such as BaTiO₃, when the superconducting coating (13) is made of a material having a perovskite structure.

Description: BACKGROUND OF THE INVENTION This invention relates to a superconductor, and more particularly to a compound thin film superconductor. Recently, it was proposed that the materials of Y-Ba-Cu-O system are the superconductors of higher temperature [M.K. Wu et al, Physical Review Letters Vol. 58, No. 9, 908-910 (1987)]. More recently, materials of Bi-Sr-Ca-Cu-O system becoming electrically superconducting above 100 K were found, and materials of Tl-Ba-Ca-Cu-O system exhibiting zero electrical resistance at still higher temperature were successively found. The details of the superconductivity mechanism of these high Tc superconducting oxides are not clear, but there are possibilities that the transition temperature of these materials may become higher than the room temperature. Superior performances to the conventional binary compounds as the electrical superconductor are expected. These high Tc superconducting oxides, however, can only be made, at the current technology, through the step of sintering. Therefore, these materials are only available in the forms of ceramic powders or ceramic blocks. For bringing materials of this kind into practical use, it is strongly desired that the materials are shaped in thin films or wires. At the current technology, tested specimens are poor in reproducibility and reliability. It is generally considered that good superconductive film and/wires of these materials are very hardly supplied. Superconductor structures of the YBaCuO-type, for example, are known from "Proceedings of Symposium S, Extended Abstracts, High Temperature Superconductors, April 23-24, 1987, pages 169-171." These supercontuctors comprise an Al 2 O 3 substrate, a buffer layer disposed on the substrate and a superconductor layer laminated on the buffer layer. For the buffer layer, ZrO 2 is preferred. The superconductors having the aforementioned compositional structure, however, are not satisfactory at all unless the influence of the substrate material is sufficiently considered. EP 0 300 499, published on January 25, 1989, discloses a composite superconductor layer comprising a single crystal substrate, a metal buffer film provided thereon, and an oxide film deposited on the metal buffer film. EP 0 292 959, which was published on November 30, 1988, teaches a superconducting member comprising a base material, a first film including at least a single ceramic layer formed on said base material and a second film containing an oxide superconductor formed on said first film. The base material is prepared by stainless steel. The object underlying the invention is to improve the performance of a superconductor structure. The above object is achieved by superconductor structures according to the claims. The superconductor structure according to this invention is markedly featured by the fact that the superconductor is formed in the shape of thin film on a substrate which is provided with a crystalline coating. Namely, regarding the film formation, when the superconductor materials once decomposed into extremely fine particles of atomic state are directly deposited on a non-crystalline or amorphous substrate, it is often difficult to obtain superconductor films of good quality. On a substrate covered with a crystal-line coating, however, a crystalline superconductor film of good quality is allowed to epitaxially deposit. Therefore, a superconductor of very high performances can be realized according to the invention. BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a cross-section of a superconductor structure according to an embodiment of the invenion. DESCRIPTION OF THE PREFERRED EMBODIMENTS Now, detailed description on the preferred embodiments of the invention will be made along with the accompanying drawing. In Fig. 1, a superconductor coating 13 is formed for example by sputtering on a calcium fluoride crystalline coating 12 which is formed in a film on a surface of a single crystal substrate 11 of for example silicon. Here, the substrate 11 is aimed to support the superconductor coating 13 which exhibits the superconductivity. This coating 13 is formed usually at a high temperature of 700°C. When a superconductor material film was deposited directly on a substrate 11 without the crystalline coating 12, for example silicon atoms of the substrate 11 diffused into the superconductor coating. The electrical resistivity became extremely large and the superconducting properties were lost. When a calcium fluoride thin film 12 was inserted between the silicon substrate 11 and the superconductor coating, oriented good quality superconductor film 13 was made. The present inventors have confirmed that as the material of the crystalline coating 12 of Fig. 1, crystais of CaF 2 type crystal structure such as barium fluoride BaF 2 , strontium fluoride SrF 2 , as well as calcium fluoride CaF 2 are effective. Further, it was confirmed that zirconia ZrO 2 having the CaF 2 type crystal structure is effective and that zirconia compounds such as stabilized zirconias in which zirconia is stabilized by oxides of rare earth elements such as Y 2 O 3 , Sm 2 O 3 , Gd 2 O 3 , La 2 O 3 , Nd 2 O 3 , etc. and MgO, CaO, and TiO 2 are effected. The superconductor coating employed in this invention is made of a crystal of perovskite crystal structure. It was confirmed that titanate type crystals such as BaTiO 3 , SrTiO 3 , CaTiO 3 , etc.. perovskite type oxides such as niobates of elements K, Na and Ag, tantalates of elements K, Na and Ag, or GdTiO 3 , etc., both having the perovskite crystal structure are effective. Further, the present inventors have found that as the substrate 11 of Fig. 1, semiconductor single crystal bodies of germanium Ge, galium arsenide GaAs, gallium phosphide GaP, and zinc sulfide ZnS, are effective as well as silicon Si. Namely, it was found that for forming a highly crystailine superconductor coating 13 on a surface of a single crystal semiconductor substrate 11, it is only necessary to form a film of a high Tc superconductor oxide on a substrate having a crystalline coating of the CaF 2 type or perovskite type crystal structure. The superconductor a-b-Cu-O system used in this invention is not yet clearly determined its crystal structure nor its chemical composition formula, but is also called oxygen-defect perovskite. The present inventors have confirmed that the superconducting phenomena are observed when the molar ratio of the elements in the film is in the range of 0.5 ≦ a + b Cu ≦ 2.5 . even when there are some differences in the critical temperature. In sputtering deposition, sintered a-b-Cu-O ceramics is used as the target. When the substrate temperature is 700°C, there was observed a tendency that Cu is short in the deposited film when comparing the compositions of the target and the deposited film. The present inventors have confirmed that Cu may be contained in the target about 50% in excess to obtain good results. Therefore, the optimum composition of the target was found to lie in 0.3 ≦ a + b Cu ≦ 1.7 . Here, the target for use in the sputtering deposition may also be in the form of granular or powder sintered bodies as well as in the form of plate ceramics or cylinder ceramics. EXAMPLE 1 Using (100) oriented silicon single crystal as the substrate 11, calcium fluoride coating 12 was deposited on the substrate 11 by vacuum deposition. Here, the substrate 11 was kept at a temperature in the range of 500 - 600°C, and the coating was grown to a thickness of 0.1 µm. The obtained film was (100)-oriented, single crystal, calcium fluoride electrical insulator. A coating 13 was deposited on this calcium fluoride coating 12 by rf planar magnetron sputtering of a sintered ErBa 2 Cu 4.5 O 8 target. Here, the atmosphere was Ar gas at a pressure of 0.5 Pa, the sputtering power was 150 W, the sputtering time was 2 hours, the thickness of the coating was 0.5 µm, and the substrate temperature was 700°C. The obtained coating [0.5 µm (H) x 1 mm (W) x 1 mm (L)] was a (002)-oriented crystalline film which has a room temperature resistance of 30 Ω and a superconductivity transition temperature of 90 K. The lattice constant of calcium fluoride is 5.8 Å with a face-centered cubic structure. The atom-to-atom (i.e. corner atom to face center atom) distance is 3.8 Å, which meets the lattice of the Er-Ba-Ca-O system superconductors, and is considered to allow production of a good crystalline superconductor body. EXAMPLE 2 Using (100)-oriented single crystal silicon wafer as the substrate 11, a stabilized zirconia coating 12 was deposited by vacuum deposition. Here, the substrate was kept at a temperature in the range of 500 - 600°C, and the coating was grown to a thickness of 0.1 µm. The obtained film was a (100)-oriented, stabilized zirconia single crystal, electrical insulator. A coating 13 was deposited on this stabilized zirconia coating 12 by rf planar magnetron sputtering of a sintered ErBa 2 Cu 4.5 O 8 target. Here, the pressure of Ar gas was 0.5 Pa, the sputtering power was 150 W, the sputtering time was 2 hours, the thickness of the coating was 0.5 µm, and the substrate temperature was 700°C. The obtained coating [0.5 µm (H) x 1 mm (W) x 1 mm (L)] was a crystalline film of (002) orientation, and had a room temperature resistance of 30 Ω and a su- perconductivity transition temperature of 90 K. Here, the lattice constant of the stabilized zirconia is about 5.05 - 5.3 Å with a fluorite type face-centered cubic crystal structure. The atom-to-atom (i.e. corner atom to face-center atom) distance is about 3.6 Å, which is very slightly smaller than the lattice constant of the Er-Ba-Cu-O system superconductor, hence has an effect of inducing strain in the Er-Ba Cu-O system su- perconductor, and is considered to allow production of good crystalline superconductor. EXAMPLE 3 Calciuin titanate CaTiO 3 coating 12 was deposited by sputtering on a substrated 11 of (100)-oriented silicon single crystal wafer. Here, the substrate temperature was held in a temperature range of 500 - 600°C, and the deposition was done to a film thickness of 0.1 µm. The obtained film was an electrical insulator of calcium titanate single crystal. A coating 13 was deposited on this calcium titanate coating by rf planar magnetron sputtering of a ErBa 2 Cu 4.5 O 8 target. Here, the Ar gas pressure was 0.5 Pa, the sputtering power was 150 W, the sputtering time was 2 hours, the thickness of the film was 0.5 µm, and the substrate temperature was 700°C. The obtained coating [0.5 µm (H = height) x 1 mm (L = length) x 1 mm (W = width)] was a crystalline film which had a room temperature resistance of 30 Ω and a superconductivity transition temperature of 90 K. Calcium titanate has a lattice constant of 3.8 Å. It is considered that this lattice constant: meets the lattice constant of the Er-Ba-Cu-O system superconductor and produced a good crystalline superconductor. Regarding this kind of superconductor a-b-Cu-O, details of the changes in the superconductivity by the changes in the constituent elements a and b are not clear. Description has been made on examples which employ Er as the element a. The intrinsic nature of the present invention, however, does not change when the element a is one of Sc, La, and Lanthanide elements (atomic number 57 - 71), although the superconductivity transition temperature may change. Also, the intrinsic nature of the present invention does not change when the element b is changed in the group consisting of group IIa elements of the periodic table, such as Sr, Ca, Ba, etc. The superconductor structure according to this invention is largely featured in the structure that the superconductor body, is formed in the shape of a film on an insulator-coated semiconductor substrate. The film is formed through the steps of decomposing the superconductor material into extremely fine particles of atomic state and then depositing them on a substrate. Thus, the produced superconductor body inherently has a more uniform composition compared to the conventional sintered bodies. Therefore, superconductor bodies of very high precision can be realized according to the present invention. Also, it is possible to integrate, in a semiconductor device, superconductor bodies of good quality in crystalline state, for example, being separated by electric insulator films. Examples are described with (100)-oriented silicon single crystal substrate and a crystalline coating of calcium fluoride, stabilized zirconia, or calcium titanate. Appropriate materials are not limited to these. In case of calcium fluoride, other crystal orientations of silicons eg. (111) surface, are also effective. On a (111) oriented silicon surface, a (111) oriented calcium fluoride coating was formed. Using gallium phosphide or zinc sulfide, mostly coincident results to those of silicon case were obtained. This is considered to be due to almost the coincident lattice constant for silicon and gallium phosphide. Similarly, in case when gallium arsenide or germanium is used as the substrate, for example a (111)-plane calcium fluoride film was obtained on a (111)-plane germanium substrate, and an oriented superconductor body was obtained on this calcium fluoride film. Here, however, since the lattice constant of a germanium or gallium arsenide is larger than that of calcium fluoride, strain is generated in the calcium fluoride film. The present inventors have confirmed that for removing such strain and realizing a stable film coating, it is effective to use strontium fluoride for the crystalline coating, or a mixture compound of strontium fluoride and calcium fluoride, for example Ca 0.44 Sr 0.56 F 2 for the crystalline coating. The present inventors have also confirmed that when indium phosphide or cadmium sulfide is used as the substrate, it is especially effective to use strontium fluoride or a mixed compound of strontium fluoride and barium fluoride as the crystalline coating. In the case of stabilized zirconia, example of using (100)-oriented silicon single crystal as the substrate is described. Other crystal orientations of silicon, e.g. (111) plane, are also effective as the substrate. In case of a (111) siilicon plane, a (111) plane zirconia coating was formed thereon. When gallium phosphide or zinc sulfide semiconductor was used as the substrate, mostly coincident results to the silicon substrate case were obtained. This is considered to be ascribed to the substantially coincident lattice constant of silicon and gallium phosphide. In case of us-ing gallium arsenide or germanium, for example when a (111) plane germanium was used as the substrate, a (111) plane zirconia coating was obtained and an oriented superconductor film was obtained on this zirconia coating. Here, however, since the lattice constant of germanium or gallium arsenide is considerably larger than that of zirconia, excessive strain is generated in the zirconia coating, The present invention have confirmed that for dissolving such strain and realizing a stable coating, it is effective to use a mixed compound of CaO and zirconia as the crystalline coating. Also, the present inventors have confirmed that it is particularly effective to use a mixed compound of CaO and MgO for stabilizing zirconia crystalline coating. In the case of calcium titanate, an example of using a (100) silicon single crystal, as the substrate, is described. Other crystal planes of silicon, such as (111) plane, were also effective. When gallium phosphide or zinc sulfide was used as the substrate, mostly coincident results to the silicon substrate case were obtained. This is considered to be ascribed to the substantially coincident lattice constant of silicon and gallium phosphide. Similarly, when gallium arsenide or germanium is used, crystalline calcium titanate was obtained, and an oriented superconductor film was obtained on this calcium titanate coating. However, the lattice constant in the <110> direction of calcium titanate is different from the lattice constant in the <100> direction of germanium or gallium arsenide, strain is generated in the coating. The present inventors have confirmed that for dissolving such strain and realizing a stable coating, it is effective to use strontium titanate or a mixed compound of strontium titanate and calcium titanate for the crystalline coating. The present inventors have also confirmed that when indium phosphide or cadmium sulfide is used as the substrate, it is particularly effective to use strontium titanate or a mixed compound of strontium titanate and barium titanate as the crystalline coating. The present inventors have confirmed that the above facts are based on the degree of lattice matching between the substrate and the crystalline coating. As has been described above, it becomes possible to form dense and good quality superconductor films according to this invention. It is possible to integrate the superconductor structure with semiconductor devices of Si, GaAs, CdS, etc., by using this invention. The superconductor structure according to this invention can be practically incorporated in various superconductor devices such as Josephson device. Particularly, there is a possibility that the transition temperature of the compound superconductor materials of this kind may become or exceed the room temperature. Then, the field of application becomes very broad. The industrial value of this invention is high.

Claims: A superconductor structure comprising: a single crystal substrate (11); a crystalline non-metallic coating (12) formed on said substrate, and an oxide superconductor coating (13) made of an oxide containing element a, element b and Cu and formed on said crystalline coating (12) wherein the atomic ratio of the elements satisfies 0.5 ≤ a + b Cu ≤ 2.5, and a is at least one species selected form the group consisting of Sc, Y and Lanthanide elements (atomic number 57 - 71), and b is at least one species selected from the group consisting of group IIa elements of the periodic table, characterized in that said substrate (11) is made of crystals of Si, GaP, or ZnS and said crystalline coating (12) is made of CaF 2 , bTiO 3 where b is an least one species selected from the group consisting of group IIa elements of the periodic table, a stabilized compound of ZrO 2 stabilized by at least one of rare earth metal oxides such as Y 2 O 3 , Sm 2 O 3 , Gd 2 O 3 , La 2 O 3 , and Nd 2 O 3 , or a stabilized compound of ZrO 2 stabilized by at least one selected form the group consisting of MgO, CaO and TiO 2 . A superconductor structure comprising: a single crystal substrate (11); a crystalline non-metallic coating (12) formed on said substrate; and an oxide superconductor coating (13) made of an oxide containing element a, element b and Cu and formed on said crystalline coating (12) wherein the atomic ratio of the elements satisfies 0.5 ≤ a + b Cu ≤ 2.5 , and a is at least one species selected from the group consisting of Sc, Y and Lanthanide elements (atomic number 57 - 71), and b is at least one species selected from the group consisting of group IIa elements of the periodic table, characterized in that said substrate (11) is made of single crystals of Ge or GaAs and said crystalline coating (12) is made of SrF 2 , a mixture of strontium fluoride and calcium fluoride, strontium titanate, a mixed compound of strontium titanate and calcium titanate, a stabilized compound of ZrO 2 stabilized by CaO or a stabilized compound of ZrO 2 stabilized by a mixed compound of CaO and MgO, or said substrate (11) is made of indium phosphide or cadnium sulfide and said crystalline coating is made of strontium titanate, a mixed compound of strontium titanate and basium titanate, strontium fluoride or a mixed compound of strontium fluoride and basium fluoride. A superconductor structure according to claim 1, wherein said superconductor coating (13) is a copper oxide high-temperature superconductor coating.

Inventors: ADACHI HIDEAKI, HIGASHINO HIDETAKA, HIRAO TAKASHI, KAMADA TAKESHI, SETSUNE KENTARO, WASA KIYOTAKA, YAMAZAKI OSAMU, ADACHI, HIDEAKI, HIGASHINO, HIDETAKA, HIRAO, TAKASHI, KAMADA, TAKESHI, SETSUNE, KENTARO, WASA, KIYOTAKA, YAMAZAKI, OSAMU
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1988
Main classification: H01L39
IPC codes: H01L39