METHOD FOR MAUFACTURING A SINTERED BODY WITH HIGH DENSITY

Abstract: A method is provided for manufacturing a sintered body comprising the steps of: heating a membrane of an inorganic polysilazane in liquid formed on the surface of a porous body to oxidize a surface portion of the layer into an oxide layer and still pyrolyzing the remaining of the inorganic polysilazane, the inorganic polysilazane being given by the formula of (-SiH₂NH-)n where n represents degree of polymerization; softening the oxide layer to make it impermeable; and sintering the porous body with the oxide layer having impermeability at high pressure and at high temperature n of degree of polymerization ranges 6 to 25. The layer is of 0.5 to 2.0mm in thickness.

Description: The present invention relates to a method for manufacturing a sintered body with high density from ceramic porous body, and more particularly to a method of forming a layer on the surface of porous body. HIP process is well known wherein, firstly, metallic or ceramic powders are formed into a compact of a predetermined shape, and the compact is presintered into a presintered body: and then, to the compact or the presintered body a gaseous medium of high temperature and high pressure such as argon and nitrogen is applied, thereby the compact or the presintered body being sintered into a sintered body with high density. In this HIP process, such a porous body as the compact or the presintered body is put into a pressure vessel to which high temperature and high pressure is applicable, and is isostatically pressed by means of letting a gaseous medium of 600 to 2,500°C and 500 to 3,000 atm. Thus, the porous body is increased in density. However, owing to this HIP method using a high pressure gas as a medium applying pressure, it is required to take a measure of preventing the gas from penetrating into the pores of the porous body. As such a measure, the following are known: (a) a method wherein density of a presintered body is increased to 93% or more of true density, and more preferably to 95% or more and a presintered body itself is transformed into an impermeable one against gas; and (b) a method wherein a compact or a presintered body is arranged in a sealed capsule impermeable against gas, and a gas medium of high temperature and high pressure is applied thereto, thereby the density being increased. This method is applicable to an ordinary compact which has a density of 40 to 75% of true density and is inevitably permeable, or a presintered body which has a density less than 93% of true density. In method (b), sometimes a porous body is arranged in a capsule prepared in advance and then the capsule is sealed. But, this way is hard to apply to a porous body having a complicated shape and the application of this way is limited to a porous body of a simple shape. In addition, sometimes in method (b), a powder layer is formed on the surface of the porous body, and is heated and softened to have the powder layer transformed into a tightly sealed capsule. When this way is adopted, the restriction arising from the shape of the porous body is small, this way of doing is particularly useful, for a porous body having a complicated shape. A prior art is disclosed in a Japanese Examined Patent Publication (KOKOKU) No. 35870/84 wherein: (a) on the surface of a preformed body of silicon nitride powders an inner porous layer of a first material and an outer porous layer of a second material are formed; (b) heat treatment is applied to the extent of a temperature which is high enough to allow the outer porous layer to be transformed into one impermeable against a pressure medium, but at which the inner porous layer still maintains its porous property; (c) heat treatment is further applied up to a temperature high enough to transform the inner porous layer into one impermeable against a pressure medium; (d) to the preformed body having had the mentioned heat treatments through the inner porous layer and the outer porous layer, isostatic pressing is applied; and (e) the first material constituting the inner porous layer is a powder of high-melting glass, a powder capable of forming a high-melting glass, or a powder of high-melting metal, the second material constituting the outer porous layer is a powder of low-melting glass, or a powder capable of forming low-melting glass. Another prior art is also disclosed in a Japanese Patent Unexamined Publication (KOKAI) No. 116178/84 wherein a ceramic porous body is covered with seal material composed of porous high silicate glass or nitride thereof and is sintered at high temperature and at high isostatic pressure to produce a sintered ceramic body with high density. Further another prior art is disclosed in a West German Patent No. 3403917. In this specification, powder layers, on the surface of a porous body, composed of two layers, i.e. an inner layer and an outer layer. The inner layer is of substance not containing a sintering-promoting additive, and the outer layer is of substance containing a sintering-promoting additive. Consequently, the outer layer has characteristic of transforming into an impermeable layer. The inner layer, as a separated layer hard to sinter, has characteristic of making it easy to take away the impermeable layer which has been formed. This method, however, has a problem in reliability in formation of a layer, since a preformed porous body is coated with slurry which is made by means of dispersing powders into a solvent. That is to say, since powders are usually cohered if they are used simply and directly in producing slurry, big pores of 30 to 40 microns are brought about in the formed powder layers. Owing to these pores remaining in impermeable layers, formation of the impermeable layers are impaired. Therefore, breaking powders is indispensable. In addition, if selection of a solvent is not appropriate, owing to powders precipitating, formation of layers having uniform density and thickness is impaired. Furthermore, shrinkage occurs during drying process after the coating and cracking is easy to occur. If, in order to lessen the shrinkage, powder concentration in slurry is increased, adhesion to the porous body is insufficient. Resultantly, the layers get easy not only to exfoliate but also to lack uniformity in thickness. To avoid the shrinkage and cracking, addition of organic binder is effective, but defect is apt to occur when the organic binder is pyrolyzed. Owing to these various reasons, it has been difficult to form layers reliable enough to maintain impermeability against high pressure. It is an object of the present invention to provide formation of layer reliable enough to maintain impermeability against high pressure. To attain the object, in accordance with the present invention, a method is provided for manufacturing a sintered body with high density comprising the steps of: heating a layer of a liquid inorganic polysilazane of formula (-SiH₂NH-) n , where n (the degree of polymerization) falls in the range 6-25, formed on the surface of a porous body to oxidize a surface portion of the layer into an oxide layer, pyrolyzing the remainder of the inorganic polysilazane, softening the oxide layer to make the oxide layer impermeable; and sintering the porous body with the impermeable oxide layer at high pressure and at high temperature. Furthermore, in accordance with the present invention, a method is provided for manufacturing a sintered body with high density comprising the steps of: heating a layer of a slurry composed of a ceramic powder and a liquid inorganic polysilazane of formula (-SiH₂NH-) n , where n (the degree of polymerization) falls in the range 6-25, formed on the surface of a porous body to oxidize a surface portion of the layer into an oxide layer, pyrolyzing the remainder of the inorganic polysilazane, softening the oxide layer to make the oxide layer impermeable; and sintering the porous body with the impermeable oxide layer at high pressure and at high temperature. The object and other objects and advantages of the present invention will become more apparent in the detailed description to follow, taken in conjunction with the appended drawings. Fig. 1 is a graphic representation showing relation between treatment time and temperatere, and relation between treatment time and pressure in regard with Example-I; and Fig. 2 a graphic representation showing relation between treatment time and temperature, and relation between treatment time and pressure in regard with Exmaple-2. Preferred Embodiment-1 An inorganic polysilazane given by the formula of (-SiH₂NH-) n where n represents degree of polymerization is prepared by using dihalosilane given by the formula of SiH₂X₂, which is composed of at least one of SiH₂Cl₂, SiH₂Br₂ and SiH₂I₂. The combination of more than one of the three are mixed. The dihalosilane and ammonia are reacted in a non-reactive solution, at -70 to 150°C to be synthesized into the inorganic polysilazane. As such solution, benzen, methyl chloride, diethyl ether and the like can be used. For example, when dichlorosilane SiH₂Cl₂ is used, the reaction is given by the following formula. H₂SiCl₂ + 3NH₃ → H₂SiNH + 2NH₄Cl n H₂SiNH → (-SiH₂NH-) n n showing degree of polymerization of the inorganic polysilazane is of key importance. n ranges 6 to 25. If n is 5 or less, the inorganic polysilazane become a very fluid liquid and penetrates into a porous body after the coating. This results in making formation of a layer difficult. If n is 26 or more, the inorganic polysilazane is of high viscosity, and cannot be used for coating. The inorganic polysilazane within the preferable range is liquid and easy to form a uniform layer. In the present invention, a metallic porous body to be formed can be any of metal or metallic group composite material requiring the temperature of 1,300 to 2,200°C to be sintered. For example, molybdenum, tungsten, molybdenum alloy, and tungsten alloy can be used. WC-Co ultra-hard alloy, and TiC-Ni and TiN-Ni cermets also are available. For a preformed ceramic body, any of ceramics can be used so long as it requires the temperature of 1,300 to 2,200°C to be sintered. Oxides of elements belonging to II,III and IV groups, carbides, nitrides and borides are preferable. For example, silicon nitride, silicon carbide, titanium boride, titanium carbide and titanium nitride can be mentioned. As methods of molding porous bodies, those publicly known, i.e. die pressing, rubber pressing, extrusion, and injection molding are available. Porous bodies formed by these methods have density of 40 to 75% of true density. Post-treatment can be practiced by means of coating porous bodies obtained by these methods with liquid inorganic polysilazane (-SiH₂NH-) n . A presintered body can be a porous body which a metallic or ceramic compact is tranformed into by means of hot press method, pressureless sintering method, gas pressure sintering method to be increased in density, a porous body of reaction sintering silicon nitride, a porous body of reaction sintering silicon carbide or the like. The method of the present invention works effectively when the density of the porous body is less than 93% of true density. This is because HIP treatment can be applied without use of the method of the present invention if the density is 93% or more of true density. But, of course, the method of the present invention can be applied even to a porous body having a density of 93% or more. In the present invention, a porous body is coated with inorganic polysilazane on the surface of the porous body. As a method of coating, any of dipping, spraying and brushing can be used. The coating thickness ranges 0.05 to 2.0mm. If the thickness is less than 0.05mm, owing to the dispersion of thickness, there is possibility of impairing the impermeability of the layer. If over 2.0mm, owing to the porous body being bound, deformation of the porous body sometimes occurs, A liquid inorganic polysilazane layer thus coated requires 3 to 5 days to be solidified when it is left at ordinary temperature, but heating accelerates the solidification. If the heating temperature is over 50°C, pyrolysis accompanying loss in weight begins. The loss in weight almost finishes at 450°C. This pyrolysis is presumed to react in accordance with the formula given below. 4H₂SiNH → Si₃N₄ + Si + 6H₂ The heating temperature preferably ranges 450 to 1,400°C. If the temperature is lower than 450°C, the pyrolysis of the inorganic polysilazane is not completed. Contrarily, if the temperature is over 1,400°C, in spite of completion of the pyrolysis, owing to softening or melting of the inorganic polysilazane, area where the inorganic polysilazane is brought into contact with gas is reduced, and the oxidation to follow is reduced. Resultantly, Si remains, and melt or evaporation of Si causes pores. The caking and the pyrolysis by heating proceed in the gaseous atmosphere of any one of air, nitrogen, argon and ammonia. If the coking and the pyrolysis are performed in the air, oxidation of metallic silicon as the reaction product and oxidation of the inorganic polysilazane simultaneously proceed. The oxidation of the inorganic polysilazane is performed mainly by moisture in the air, and proceeds partially by work of oxygen. The oxidation of the inorganic polysilazane by the moisture is performed by the formulas given below, SiO₂ and SiH₂O being produced. H₂SiNH + 2H₂O → SiO₂ + 2H₂ + NH₃ H₂SiNH + H₂O → SiH₂O + NH₃ The oxidation converts Si₃N₄ hard to become dense into SiO₂ easy to become dense. Thanks to this conversion, impermeable layer having no pores can be formed. When the heating is carried out in the atmosphere of nitrogen gas, Si₃N₄ is produced. Subsequently, Si₃N₄ is brought into contact with oxygen or water, and then, SiO₂ and SiH₂O are produced. SiH₂O is converted by heating at high temperature into SiO₂. When the heating is carried out in the atmosphere of argon gas, Si₃N₄ is produced as in the case of the nitrogen gas atmosphere. By contact with oxygen or water, SiO₂ and SiH₂O are produced as well. In the ammonium atmosphere, Si₃N₄ is produced, and SiO₂ and SiH₂O are obtained similarly. To accelerate the oxidation, spraying steam on a porous body or placing the porous body in the humidified atmosphere can be adopted. Furthermore, oxidation at 50°C or less can proceed in advance of pyrolysis. The surface of the coated layer had better be wholly transformed at least into oxide. Oxide layer of the porous body which is pyrolized through heating and oxidized are softened to get impermeable. This process is carried out by keeping the porous body at 1,300 to 1,800°C. If the temperature is less than 1,300°C, it takes long to make dense. This is far from commercial production. In addition, the porous body is easy enough to be softened at 1,800°C to be increased in density, and raising the temperature more than 1,800°C is useless from commercial view point. Thus, the porous body comes to be in the state of being ready to be given by HIP treatment. The temperature and pressure at the time of the HIP treatment is to be determined, depending upon quality of the porous body. However, when the state of impermeable layer is taken into consideration, the preferable temperature is 1,300 to 1,800°C. If the temperature is less than 1,300°C, the viscosity of the impermeable layer fails to follow suitably the shrinkage of the porous body. If over 1,800°C, the impermeable layer is melted away. Preferred Embodiment-2 In Preferred Embodiment 1, liquid inorganic polysilazane is solely used in forming a layer on the surface of the porous body, but the material used in forming the layer of the present invention is not necessarily limited to the liquid inorganic polysilazane. A further method is provided to use slurry composed of liquid inorganic polysilazane mixed with ceramic or glass to the extent that the liquid inorganic polysilazane is kept in liquid state instead of the liquid inorganic polysilazane only. The material to be mixed with liquid inorganic polysilazane can be at least one selected from the group consisting of TiN powder, AlN powder, Si₃N₄ powder, SiC powder, TiD powder, B₂O₃ powder, Al₂O₃ powder, MgO powder, Y₂O₃ powder and CeO powder. The material mentioned is preferable so as to enable controlling softening point and viscosity of produced layer. In addition, a layer can also be prepared by a method, wherein two different kinds of slurry are prepared, and then, firstly, one kind of slurry is coated on the surface of a porous body and dried, and secondly, the other kind of slurry is coated on the surface of the dried porous body and dried. Example-1 Powders having a blend ratio of 96wt.% Si₃N₄ and 4wt.% Y₂O₃ were mixed in liquid methanol by means of ball mill for 24 hours, dried and screened through a 100 mesh sieve to remove coase grains therefrom. Thus, material powders to be formed into were prepared. The material powders were put into a metallic mold and formed into a compact of 60mm × 10mm × 12mm by an axis press forming at 300 kg/cm². Then, the compact was put into a thin rubber pouch, and subsequently formed by rubber press at 3t/cm² The bulk density of 10 porous bodies was 49% of true density. In the meantime, 30 vol.% methyl chloride was disolved into 70 vol.% H₂SiCl₂ in a 300 ml flask to form a solution, and NH₃ was blown in onto the solution continuously and reacted for 2 hours in thermostatic chamber of -10°C. The solvent was volatiled through pressure reduction to be removed. Thus, colorless liquid inorganic polysilazane was obtained. This inorganic polysilazane was spread on the whole surface of the porous bodies by means of brushing to form about 0.5mm layers of the inorganic polysilazane in thickness. Subsequently, to oxidize surface portions of the layers and pyrolyze the remaining inorganic polysilazane, the porous bodies with the layers (were heated upto 500°C at a rate of 3°C/min in a hot blast dryer as air was circulated and were kept at 500°C for an hour. Then, the porous bodies were kept as they were naturally cooled. 10 porous bodies thus obtained were charged into HIP equipment, and HIP treatment was applied to them. Fig. 1 graphically represents relation between processing time and temperature and relation between processing time and pressure. (a) To heat the 10 porous bodies upto 1000°C as a pressure is reduced. (b) To keep them at 1,000°C for 3 hours (finally the degree of vacuum becomes 0.1mm Torr). (c) To heat them upto 1,700°C as nitrogen gas of 1 atm. in term of gauge pressure is being supplied. (d) To keep them at 1,700°C for an hour. (e) To heat them upto 1,750°C as nitrogen gas of 120 atm. is being supplied. (f) To keep them at 1750°C and at 2000 atm. (g) To leave them to cool naturally. After the natural cooling, 10 samples of the sintered body obtained were sandblasted to take away the surface impermeable layers all the 10 samples made progress in increasing in density. The density has proved to attain 99.4 ± 0.2% of theoretical density. Example-2 0.02 to 0.04 micron tungsten ultra fine powders in size were put into a metallic mold and were formed by one axis press at 300 kg/cm² into a compact of 60mm × 10mm × 8mm. The compact was put into a thin rubber pouch, and subsequently formed by rubber press at 5t/cm². The bulk density of 10 poruos bodies was 57% of true density. Inorganic polysilazane prepared in the same method as in Example-1 was spread on the whole surface of the porous bodies by means of brushing to form about 0.5mm layers of the inorganic polysilazane in thickness. Subsequently, to oxidize surface portions of the layers and pyrolyze the remaining inorganic polysilazane, the porous bodies with the layers were heated upto 500°C at a rate of 3°C/min. in a hot blast dryer as air was circulated, and were kept at 500°C for an hour. Then, the porous bodies were left as they were naturally cooled. 10 porous bodies thus obtained were charged into a vacuum sintering apparatus. Firstly in the apparatus, the pressure was reduced to 10⁻⁴ Torr at ordinary temperature by means of vacuum suction, and the temperature was raised to 1,000°C by heating as the vacuum was being maintained, 1,000°C being kept for 5 hours. Subsequently, the temperature was raised to 1700°C, and was kept for an hour. Then, the 10 porous bodies were left as they were naturally cooled. Samples covered with glass were obtained. These samples were charged into HIP equipment, and HIP treatment was applied to them. Fig. 2 graphically represents relation between processing time and temperature and relation between processing time and pressure. (a) To heat the porous bodies up to 1,700°C as 1 atm. argon gas is being blown in. (b) To keep them at 1,700°C for an hour. (c) To heat them up to 1,800°C as 120 atm. argon gas is being supplied. (d) To keep them at 1,800°C and at 1,000 atm. (e) To leave them to cool naturally. After the natural cooling, 10 samples were sandblasted. All the 10 samples made progress in increasing in density. The density has proved to attain the theoretical density. Example-3 15wt.% of inorganic polysilazane prepared in the same method as in the case of Example-1 was dissolved in 50wt.% of tetrahydrofuran to prepare a solution. With this solution, 35wt.% of 0.25 micron silicon carbide powder on average size was mixed to prepare slurry A. Next, 15wt.% of in organic polysilazane was dissolved in 50wt.% of tetrahydrofurane to form a solution. With this solution, 35wt.% of 1.5 micron glass powders on average size consisting of 80.4wt.% SiO₂, 12.0wt.% B₂O₃, 4.0wt.% Na₂O; 0.4wt.% K₂O and 0.3wt.% CaO to prepare slurry B. Slurry A was spread by means of brushing on the whole surface of a porous body of silicon nitride produced in the same process as in the case of Example-1, and dried in a hot drier. Furthermore, slurry B was spread on the spread slurry A by brushing and dried on the hot drier. Thus, a 0.5mm layer composed of slurry A and slurry B in thickness was obtained. Subsequently, in order to oxidize a surface portion of the layer, and pyrolyze the remaining of the inorganic polysilazane, the porous body with the layer was heated up to 500°C at a rate of 3°C/min. in a hot blast drier as air was circulated, and kept at 500°C for an hour. An then, the porous body was left to natural cooling. 10 porous bodies thus obtained, were put into HIP equipment and HIP treatment was applied thereto. The HIP treatment was carried out on the same terms and conditions with those of Example-1. After natural cooling, the 10 samples were sandblasted to remove the surface impermeable layers. All the samples made progress in increasing in density. The density was 99.4 ± 0.2% of the theoretical density. Control 10 compacts of silicon nitride were prepared in the same steps as in the case of Example-1. In the meantime, 20wt.% of glass powders having composition of 96.7wt.% SiO₂, 2.9wt.% B₂O₂ and 0.4wt.% Al₂O₃ was mixed with 80wt.% isopropyl alcohol to form a mixture. The mixture was dispersed by means of a supersonic wave device to be transformed into slurry. Said compacts were dipped into the slurry, and then were dried at 200°C in a hot blast drier for an hour. Thus, porous bodies with glass powders adhered thereto were obtained. HIP treatment was applied to the porous bodies in the same steps taken as in the case of Example 1. 6 of the 10 porous bodies did not make progress in increasing in density. In these 6 porous bodies, there were voids between each of sintered bodies and each of glass layers thereof to be found. The other 4 porous bodies made progress in density, but the glass layers each stuck so firmly to the respective sintered bodies that it was difficult to remove the glass layers perfectly from the sintered bodies by sandblasting. Resultantly, exact measurement of the density thereof was unable to be done. But, the density reached 99% of the theoretical density.

Claims: A method for manufacturing a high density sintered body comprising the steps of: heating a layer of a liquid inorganic polysilazane of formula (-SiH₂NH-) n , where n (the degree of polymerization) falls in the range 6-25, formed on the surface of a porous body to oxidize a surface portion of the layer into an oxide layer, pyrolyzing the remainder of the inorganic polysilazane, softening the oxide layer to make the oxide layer impermeable; and sintering the porous body with the impermeable oxide layer at high pressure and at high temperature. A method according to claim 1, wherein the porous body is a metallic porous body or a ceramic body. A method according to claim 2, further comprising the step of pre-sintering the porous body. A method according to any preceding claim, further comprising the step of synthesising the inorganic polysilazane by reacting a dihalosilane of formula SiH₂X₂ and ammonia in a non-reactive solvent; wherein X represents at least one element of Cl, Br and I. A method according to any preceding claim characterized in that the layer of the liquid inorganic polysilazane formed on the porous body is in the form of a membrane having a thickness of 0.5 to 2.0mm. A method according to any preceding claim characterized in that the step of heating the layer of the inorganic polysilazane is carried out at 450 to 1,400°C in a gaseous atmosphere. A method according to claim 6, characterized in that the gaseous atmosphere comprises air, nitrogen, argon or ammonia. A method according to claim 7, characterized in that the gaseous atmosphere further comprises moisture. A method according to any preceding claim characterized in that the step of making the oxide layer impermeable includes maintaining the oxide layer at 1,300 to 1,800°C to increase the density of the oxide layer. A method according to any preceding claim characterized in that the step of sintering the porous body at high pressure and high temperature includes applying hot isostatic press to the porous body at 1,300 to 2,200°C to sinter the porous body. A method for manufacturing a high density sintered body comprising the steps of: heating a layer of a slurry composed of a ceramic powder and a liquid inorganic polysilazane of formula (-SiH₂NH-) n , where n (the degree of polymerization) falls in the range 6-25, formed on the surface of a porous body to oxidize a surface portion of the layer into an oxide layer, pyrolyzing the remainder of the inorganic polysilazane, softening the oxide layer to make the oxide layer impermeable; and sintering the porous body with the impermeable oxide layer at high pressure and at high temperature. A method according to claim 11, characterized in that the slurry layer formed on the porous body is in the form of a membrane having a thickness of 0.5 to 2.0 mm. A method according to claim 11 or claim 12 characterized in that the step of heating the layer of the slurry includes heating at 450 to 1,400°C in a gaseous atmosphere. A method according to claim 13, characterized in that the gaseous atmosphere comprises air, nitrogen, argon or ammonia. A method according to claim 14, characterized in that the gaseous atmosphere further comprises moisture. A method according to any one of claims 11 to 15, characterized in that the step of making the oxide layer impermeable includes maintaining the oxide layer at 1,300 to 1,800°C to increase the density of the oxide layer. A method according to any one of claims 11 to 16, characterized in that the step of sintering the porous body includes applying hot isostatic press to the porous body at 1,300 to 2,200°C to sinter the porous body. A method according to any one of claims 11 to 17, characterized in that the layer of slurry is formed by coating a first layer of slurry on the surface of the porous body, drying the first slurry layer, coating a second layer of slurry on the surface of the porous body coated with the first layer of dried slurry, and drying the second slurry layer.

Inventors: NISHIO, HIRAOKI C/O PATENT & LICENSE AND, Nishio, Hiraoki c/o Patent &amp; License and
Applicants: NIPPON KOKAN KABUSHIKI KAISHA
Application year: 1988
Main classification: C04B41
IPC codes: C04B35, B22F3