A process for making a self-aligned thin film transistor

Abstract: A process for making a self-aligned thin film transistor, comprising the steps of: (a) providing a gate which comprises a glass substrate (1), a transparent electrode (2) on top thereof, and a metal electrode (3) on top of said transparent electrode, (b) forming a stack by depositing over said gate a triple layer structure consisting of gate dielectric material (4), active material (5) and a top passivating dielectric (6), (c) coating the top of said triple layer with a dual-­ tone photoresist (7), (d) exposing said photoresist from the top through a mask having transparent areas, opaque areas and areas transparent to selective wavelengths, using broad band UV light, (e) developing the photoresist by treatment with a solvent, (f) etching the stack with a liquid etchant through to the glass substrate, (g) exposing the photoresist from the bottom through the glass substrate using near UV light, (h) developing the photoresist with a solvent, and (i) etching off the top passivating layer of the stack.

Description: The present invention is concerned with a process for making a self-aligned thin film transistor, according to claim 1. U.S.-A- 4,599,246 shows a process for producing a thin film transistor array. The process requires three masking steps instead of the conventional seven. The process is not self-aligning and does not involve the use of a dual-tone resist. An article by Kodama et al in IEEE Electron Device Letters, Vol. EDL-3, #7, July 1982, page 187, shows a self-aligning process for thin film transistors. The process of this publication does not involve the use of a dual-tone resist. DE -A- 3337315 discloses the concept of a dual-tone resist. The publication, however, is entirely silent in regard to a process for making a thin film transistor and does not describe a self-aligning process. The present invention provides a process for making a self-aligned thin film transistor, said process comprising the steps of: (a) providing a glass substrate, (b) providing a gate which comprises a transparent electrode on top of an area of the glass substrate, and a metal electrode on top of said transparent electrode, (c) forming a stack by depositing over the gate and surrounding substrate a triple layer structure consisting of gate dielectric material, active material and a top passivating dielectric, (d) coating the top of said triple layer with a dual-tone photoresist, (e) exposing said dual-tone photoresist from the top through a mask having transparent areas, opaque areas and areas transparent to selective wavelengths, using broad band UV light, (f) developing the photoresist by treatment with a solvent, such that an exposed cross-linked resist area remains on the triple layer stack forming the external border of the transistor, and an exposed central part of said photoresist limited by said border part remains above the metal electrode, (g) etching the areas of the stack not covered by photoresist with a liquid etchant through to the glass substrate, (h) exposing the photoresist from the bottom through the glass substrate using near-UV light, the metal electrode acting as a mask, (i) developing the photoresist with a solvent such that the exposed cross-linked resist remains and unexposed resist remains only directly above the metal electrode used as a mask, and (j) etching off the areas of the top passivating layer of the stack not covered by photoresist. The process of present invention has the advantages of requiring only three mask exposures and of reducing the number of required steps. Furthermore, the most critical alignment is achieved automatically regardless of small changes in the size of the glass from step-to-step, for example. Both these advantages serve to lower cost by improving yield and by reducing the number of alignment tools. How the invention can be carried out will now be described by way of example, with reference to the accompanying diagrammatic drawings, in which Fig. 1 to Fig. 7 represent cross-sections, not to scale, of a transistor device during the steps of its manufacture by a process embodying the present invention. Fig. 1 shows a starting material in the form of a gate which comprises a glass substrate (1), a transparent electrode (2), and a metal electrode (3). In the first step of the process embodying the present invention, a stack is formed by coating the gate and the surrounding substrate with a triple layer. As is shown in Fig. 2, this triple layer consists of a gate dielectric material (4), active metal (5) and top passivation dielectric (6). This stack is next coated with a dual-tone photoresist which is shown in Fig. 3 as (7). In the next step of the process, the dual-tone photoresist (7) is exposed from the top through a mask having three types of areas: (a) opaque areas, (b) areas transparent to selected wavelengths and (c) transparent areas. The exposure is done from the top using broad band UV light, and following the exposure, development takes place using a solvent. This results in the structure shown in Fig. 4 where the side portions of the original dual-tone photoresist have been completely removed. Another portion remains as exposed cross-linked resist (8) and still another portion remains as unexposed resist (9). The areas of the stack not covered by photoresist are next etched with a liquid etchant through to the glass substrate thereby producing the structure shown in Fig. 5. The structure of Fig. 5 is then exposed from the bottom through the glass substrate using near UV light and developed with a solvent to produce the structure shown in Fig. 6. It will be noticed that Fig. 6 differs from Fig. 5 in that the unexposed resist (9) has been removed except for that area above the metal electrode. Finally, the areas of the stack not covered by photoresist are subjected to an etching step to remove the top passivating layer, thereby producing the finished thin film transistor structure shown in Fig. 7. In summary, according to the process of the present invention, a self-aligned thin film transistor is produced by the steps of (a) providing a glass substrate, (b) providing a gate which comprises a transparent electrode on top of an area of the glass substrate, and a metal electrode on top of said transparent electrode, (c) forming a stack by depositing over the gate and surrounding substrate a triple layer structure consisting of gate dielectric material, active material and a top passivating dielectric, (d) coating the top of said triple layer with a dual-tone photoresist, (e) exposing said dual-tone photoresist from the top through a mask having transparent areas, opaque areas and areas transparent to selective wavelengths, using broad band UV light, (f) developing the photoresist by treatment with a solvent, such that an exposed cross-linked resist area remains on the triple layer stack forming the external border of the transistor, and an exposed central part of said photoresist limited by said border part remains above the metal electrode, (g) etching the areas of the stack not covered by photoresist with a liquid etchant through to the glass substrate, (h) exposing the photoresist from the bottom through the glass substrate using near-UV light, the metal electrode acting as a mask, (i) developing the photoresist with a solvent such that the exposed cross-linked resist remains and unexposed resist remains only directly above the metal electrode used as a mask, and (j) etching off the areas of the top passivating layer of the stack not covered by photoresist. This process results in having the active layer in a geometry which is registered or self aligned to the underlying metal, and since the metal is registered to the edge of the transparent portion of the gate, the contact has a controlled overlay (e.g. 3um) with respect to the gate electrode. It is a particular advantage of the present invention that it allows control of this overlap of the gate electrode. The concept of a dual-tone resist has already been reported in the art. The expression "dual-tone resist" is used here in its ordinary meaning to refer to a resist composition having a matrix resin and at least two photoactive additives, one of which causes acceleration of dissolution upon radiation and one of which causes deceleration of dissolution upon radiation. For the purposes of the present invention, one such dual-tone resist composition which is preferred comprises a matrix resin which is a phenol-formaldehyde resin. Another suitable matrix resin is poly (p-hydroxystyrene) Useful accelerating photoadditives include diazoquinones, such as 4- or 5-sulfonate esters of 1-oxo-2-diazonapthoquinone sulfonic acids. The preferred photoactive additives that decelerate resist dissolution upon activation are mono-or bis-aryl azides including diazidodiphenyl sulfones, bis-(azidobenzylidene) cyclohexanones and azidochalcones. In a preferred variation of the present invention, the compositions employed are made sensitive to various wavelengths of UV light. For example, the additive that brings about acceleration of resist dissolution upon activation can be diazonaphthoquinone sulfonate esters that absorb at wavelengths up to 400-450 nanometers. The decelerating additive can be mono- or bis-azides that do not absorb at wavelengths above 320 nanometers. The mask can be fabricated on a quartz substrate that transmits all wavelengths above 200 nanometers. The opaque mask elements can be chromium that is opaque to all activating wavelengths. The optical filter elements can be films of a common positive diazonaphthoquinone-novolac photoresist such as those commonly used in microcircuit fabrication, which transmit above 350 nanometers and are opaque below 350 nanometers at thicknesses greater than 3 microns. As examples of other preferred materials for use in the process of the present invention, the following may be mentioned. The developing solvent can be an aqueous alkaline solution of an alkali hydroxide, such as sodium hydroxide. The transparent electrode is conveniently made of indium tin oxide and the metal electrode of molybdenum. Silicon nitride serves as a good material for the gate dielectric material, with amorphous silicon as the active metal, and silicon nitride as the passivation dielectric material. A useful etchant for the passivation layer is phosphoric acid. A useful etchant for the indium tin oxide and molybdenum is a mixture of nitric and hydrochloric acids.

Claims: A process for making a self-aligned thin film transistor, comprising the steps of: (a) providing a glass substrate (1), (b) providing a gate which comprises a transparent electrode (2) on top of an area of the glass substrate (1), and a metal electrode (3) on top of said transparent electrode, (c) forming a stack by depositing over the gate and surrounding substrate a triple layer structure consisting of gate dielectric material (4), active material (5) and a top passivating dielectric (6), (d) coating the top of said triple layer with a dual-tone photoresist (7), (e) exposing said dual-tone photoresist (7) from the top through a mask having transparent areas, opaque areas and areas transparent to selective wavelengths, using broad band UV light, (f) developing the photoresist by treatment with a solvent, such that an exposed cross-linked resist area (8) remains on the triple layer stack forming the external border of the transistor, and an exposed central part (9) of said photoresist limited by said border part (8) remains above the metal electrode, (g) etching the areas of the stack not covered by photoresist with a liquid etchant through to the glass substrate, (h) exposing the photoresist from the bottom through the glass substrate using near-UV light, the metal electrode (3) acting as a mask, (i) developing the photoresist with a solvent such that the exposed cross-linked resist (8) remains and unexposed resist (9) remains only directly above the metal electrode (3) used as a mask, and (j) etching off the areas of the top passivating layer of the stack not covered by photoresist. A process as claimed in claim 1, wherein the dual-tone photoresist comprises a phenol-formaldehyde-type matrix resin, an accelerating photoactive additive which is a diazoquinone, and a decelerating photoactive additive which is a mono- or bis-aryl azide. A process as claimed in claim 1, wherein the mask is a chromium-on-quartz photomask having certain transparent areas which transmit mid-UV light and other transparent areas which transmit only near-UV light.

Inventors: HINSBERG WILLIAM DINAN III, HOWARD WEBSTER EUGENE, WILLSON CARLTON GRANT, HINSBERG, WILLIAM DINAN III, HOWARD, WEBSTER EUGENE, WILLSON, CARLTON GRANT
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1988
Main classification: H01L21
IPC codes: H01L29, H01L21, H01L27