PROCESS FOR RECOVERING CHROMIC ANHYDRIDE FROM EXHAUSTED AQUEOUS CHROMIUM PLATING BATH SOLUTIONS WITH EXPLOITATION OF THE RECOVERED CHROMIUM

Abstract: The chromic anhydride contained in soluble form (chromic acid) in exhausted, polluted chromium plating baths is recovered by alkalizing the exhausted chromium plating liquid to a pH comprised between 3 and 7 at a temperature of 70 DEG C with a commercial sodium hydroxide solution, keeping the mass in reaction at this temperature for an hour and filtration separating the precipitate obtained. The filtered solution having a specific gravity of 1.25 kg/l, contains CrO3 (22 % in weight) which is then reduced with sulphur dioxide to obtain a solution containing basic chromium sulphate and sodium sulphate, suitable for use as a tanning bath; in this manner pollution is avoided and the waste chromium is exploited. The solution containing CrO3 can also be introduced into a hexavalent chromium salt production cycle.

Description: "PROCESS FOR RECOVERING CHROMIC ANHYDRIDE FROM EXHAUSTED AQUEOUS CHROMIUM PLATING BATH SOLUTIONS WITH EXPLOITATION OF THE RECOVERED CHROMIUM" The subject of the present invention is a process for recovering chromium anhydride contained in soluble form (chromic acid) m exhausted chromium plating baths polluted by the presence of various metallic ions, particularly iron, copper, zinc, alu i- 5. mum, nickel, cadmium, as well as by the appearance of tπvalent chromium, which forms during chromium plating. What is meant by exhausted solution is a chromium plating bath that can no longer be used for this purpose because it is polluted with metal ions (essentially iron, copper, zinc, 10. aluminium, nickel, cadmium) and by the appearance of tπvalent chronium. A typical examole of a so-called exhausted chromium plating bath has the following composition: CrO (total) = 35% (weight/weight) CrO (hexavalent) = 30% (weight/weight) CrO (trivalent) = 5% (weight/weight) Fe = 30 parts per 1000 parts of total CrO. Cu = 30 parts per 1000 parts of total CrO Zn = 5 parts per 1000 parts of total CrO Al = 1 part per 1000 parts of total CrO Ni = 0,1 parts per 1000 parts of total CrO 10. V = 0,05 parts per 1000 parts of total CrO. Cd = 0,2 parts per 1000 parts of total CrO Depending on the chromium plating processes from which the baths come, the following may also be present: Ca, Mg, Si, Na, SO , Cl . There may also be present chinonic organic substances whose 15. disruptive action may easily be stopped by adding mercaptoacetic acid to the chromium sulphate obtained (as described in Italian patent application No. 21807 A/82) . A known method is that of precipitating metallic hydrates contained in aqueous solutions, at controlled pH values, and 20. separating them on the basis of their relative separation factors, see Chemical Economy and Engineering Review; May 1975, vol. 7 No. 5 (No. 84) and references. Another known method is that of extracting chromic anhydride from aqueous solutions where it is found together with polluting 25. metallic ions, by means of ion exchange resins in solid or liquid form and with appropriate solvents (French patent application No. 2.179.649). Also known is the method (U.S. patent No. 4.045.340) consisting of precipitating the internal salt of hexavalent and trivalent chromium, known as chromium chromate, in the cycle of sodium bisulphate recovery from a chromium anhydride synthesis plant. 5 , Now it has surprisingly been discovered that at certain pH values it is possible to precipate simultaneously metallic ions (which pollute an exhausted chromium plating bath) and chromium chromate, which is, as mentioned earlier, an internal salt of hexavalent chromium and trivalent chromium, which are present in 1o. the bath. To be precise, it has been found in particular that the liquids separated by percolation from the chromium chromate precipitate, are suitable for use in a hexavalent chromium salt manufacturing process or to be transformed, by reduction of hexavalent and 15. trivalent chroumium with sulphur dioxide, into a basic chromium sulphate suitable for use in tanning hides, as will be described in greater detail further on, on the basis of illustrative examples . With this transformation, materials which, being toxic and 20. harmful, would cause serious ecological problems if they were released into the environment, are recovered in the form of products of considerable economic and commercial value, with a much reduced effect on the environmental preservation. In fact disposal problems are reduced to about 10% and the 25. process claimed herein therefore proves generally more economi- cal. During the studies leading to this discovery, basic chromium sulphate in a residual liquid from chromium plating baths polluted with Fe, Cu, Ni, Al, Zn, V and trivalent chromium was 5. at first transformed directly, reducing the chronium anhydride with sodium bisulphite. However it was noted that the resulting liquid, used as a tanning bath, gave unsatisfactory results for this operation; it was therefore deduced that a preliminary operation was needed to 10. purify the exhausted, polluted chromium plating bath. To this end a typical chromium plating bath as described above was titred at room temperature with NaOH and the relative curve (pH vs cc of N/10 NaOH used) was plotted (see Fig. 1) compared with the same titration (and relative curve) carried out on a 15. synthetically obtained solution, with only chromic anhydride dissolved in water, at the same concentration. An anomaly was observed in the titration curve between the pH values (experimental and theoretical) from 2 to 5,5. In fact in the chromium plating bath at pH 2 solid precipitation began and 20. the pH value subsequently rose more rapidly (up to a value of 5,5) in contrast with what happened in the synthetic solution. From pH 5,5 to 10 (which is the point at which bichromate is completely transformed to monochromate) behaviour was the same in both cases. The above is schematized in the attached graph (Fig. 1) , from which it can be noted that in both cases the following reaction takes place along line A: -2 A 2HCrO ->Cr 0 + H 0 4 2 7 2 5. whereas along B (synthetic solution) the previous reaction continues and along B (chromium plating bath) the hydrate precipitation reactions combine and predominantly the reaction: +3 HCrO + 2Cr + 50H chromium chromate precipitate CrO . Cr O + 3H O 3 2 3 2 10. which essentially determines the anomaly shown cy curve B compared with B. At a pH above 5,5 the following reaction along line C takes place in both cases: -2 - -2 Cr 0 + 2OH -7- 2CrO - H O 2 7 4 2 until completion (at pH 10) of the transformation to monochroma- 15. te. It was thus discovered that by alkalizing tne residual liquid from chromium plating baths, polluted with Fe, Cu, Ni, Al, Zn, V, Cd and Cr , with sodium hydroxide added m such an amount as to bring the pH value to between 3 and 7, all metallic 20. pollutants, present precipitate: surprisingly, by subsequently VI filterin and subjecting the filtrate (containing Cr ) to the action of SO , a liquid is obtained containing basic chromium sulphate and sodium sulphate, which has proved suitable, without further modification, for use in tanning baths with excellent 25. results. The operation described above was repeated several times, filtering the liquids brought to pH values between 3 and 7, and chromium sulphates suitable for hide tanning were always obtained, even though they presented different basicity values (ratio between SO linked to the chromium and chromium itself) according to the pH value selected for precipitation. 5. The separation factor pattern for iron, copper and trivalent chromium from hexavalent chromium was also examined at different pH values and the results are set out in Fig. 2 (in which the data are complete up to pH 5 for all elements) . In this figure it can be seen clearly that in the pH interval 10. from 3 to 7, an interval of special importance as we shall see later, for reasons discussed further on, the separation factors are such that their values do not subsequently interfere with hide tanning operations, as emerges clearly from the examples. At pH 3 the filtered liquids contain a solution of sodium 15. bichromate according to completion of the reaction: -2 2HCrO -jCr O ÷ H O (curve A m fig. 1) 4 2 7 2 y At pH 7 the filtered liquids contain hexavalent chromium, 50% of which is in the form of a bichromate and 50% in the form of a monochromate according to partial occurrence of the reaction: -2 - -2 20. Cr O + 20H → 2CrO + H O (curve C in fig. 1) 2 7 ^ 4 2 By reducing the hexavalent chromium in the liquids filtered at pH 3 the following is obtained: NaCr O + 3SO + H 0-) Na SO + 2 (CrOHSO ) 2 7 2 2 2 4 4 which is the so-called Schorlemmer 33,3% basicity basic chromium sulphate, which is used in certain types of hide tanning. By reducing the hexavalent chromium with SO in the liquids filtered at pH 7 the following is obtained: 0,5 Na Cr 0 + Na CrO + 3SO + 1,5 H 0- 1,5 Na SO 2 2 7 2 4 2 2 2 4 + 2 Cr(SO ) (OH) ] L 4 0, '5 1,5" The latter is the so-called 50,00% Schorlemmer oasicity basic chromium sulphate, which is used in certain other particular types of hide tanning. 10. Proceeding as described above at intermediate pH values (for example 5 - 6) intermediate basic chromium sulphates are obtained. The aim of the present invention is therefore to obtain from chromium plating residual materials which, according to present 15. laws, are classified as toxic and harmful, products of economic value, such as bichromates, chromates , chromium sulphates and derivatives thereof. In other words, n practice the process according to the present invention on the one hand solves the ecological problem of 20. preserving the environment from toxic substances and on the other hand offers the advantage of simultaneously exploiting what is at present a dangerous waste product. The process described can be modified, without altering its substance, with a preliminary operation to oxidize the trivalent chromium contained in exhausted chromium plating baths to hexavalent chromium, according to known methods. This operation reduces from about 10% to about 1% (in the case 5 , of the typical example shown for the composition of a chromium plating bath) the onus deriving from the need to dispose of solid waste, and the chromic anhydride obtained from the oxidation operation is recovered. EXAMPLE 1 1 o. Processing of exhausted chromium plating liquids according to a known process (chromium reduction without preliminary purifica¬ tion) To an exhausted liquid (10 kg) , from surface chromium plating operations, having the composition indicated in the description, 1 5. a 36% solution of sodium bisulphite was added, with no preliminary operation, until the hexavalent chromium had disappeared. The resulting liquid, whose physical appearance was similar to that indicated in example 2, had the following characteristics: 20. Cr O content = 12,2% (16,0% expressed in CrO,) 2 3 ' 3 Schorlemmer basicity= 34% Fe content = 480 mg per 100 g of liquid Cu content = 480 mg per 100 g of liquid Ni content = 1,6 mg per 100 g of liquid 25. Al content = 16 mg per 100 g of liquid Cd content = 25 mg per 100 g of liquid Zn content = 80 mg per 100 g of liquid V content = 0,8 mg per 100 g of liquid This material was used for a hide tanning test, as will be 5. described further on in example 7. EXAMPLE 2 Processing exhausted liquids according to the invention An exhausted liquid (10 kg) from surface chromium plating operations, having the composition indicated in the description, 10. was brought to pH 5, from an initial pH of 0,7, with a commercial sodium hydroxide solution, NaOH titre 45% (2,5 kg) . After the sodium hydroxide had been added, the temperature had risen to 70°C. The resulting mass was kept at 70°C for 1 h, in order to aid settling of the precipitated solid, and then 15. filtered to obtain: - a solid which, after drying at 110°C, weighed 1 kg, and - a liquid with a specific gravity of 1,25 kg/1 having a CrO concentration of 22% in weigth. The CrO recovered from the filtered liquid was equivalent to 20. 75% of that contained in the exhausted liquid. This liquid, purified and filtered, can be used for the synthesis of bichromate and monochromate. In the soecific case of the present example, it was subjected to the reducing action of SO , which was bubbled through the liquid until the hexavalent chromium had disappeared, and a solution of basic chromium and sodium sulphate having the following characteri¬ stics was obtained: 5. Cr 0 content "= 13,3% (17,5% expressed in CrO ) 2 3 ^ 3 Schorlemmer basicity= 35% Fe content = 1,6 mg per 100 g of liquid Cu content = 1,5 mg per 100 g of liquid Ni content = 0,7 mg per 100 g of liquid 10. Al content = 0,5 mg per 100 g of liquid Zn, V and Cd content= 0,1/0,2 mg per 100 g of liquid A hide tanning test was carried out with this material, as described in example 6. EXAMPLE 3 15. Processing exhausted chromium plating liquids according to a variant of the invention 10 kg of an exhausted chromium plating bath, having the composition indicated in the description, were brought to pH 7 (from an initial value of 0,7) with a commercial sodium 20. hydroxide solution, NaOH strength 45%; the amount of sodium hydroxide used was 4 kg. After the sodium hydroxide had been added the temperature had risen to 60°C. the resulting mass was kept under slow agitation for 1 h at this temperature, in order to aid settling of the precipitated solid then filtered to 25. obtain: - a solid which, after drying at 110°C to a constant weight, weighed 0,9 kg and - a liquid having a specific gravity of 1,4 kg/litre and a CrO. concentration of 21% in weight. The CrO separated from the liquid by filtration (compared with that contained in the exhausted liquid) was equivalent to 78%. This liquid could have been used for the synthesis of bichromate and/or monochromate, but, for closer comparison, t was subjected, as described in example 1 , to the action of SO until the hexavalent chromium had disappeared; a chromium sulphate and 10. sodium sulphate solution having the following characteristics was thus obtained: Cr O content = 12.2 (16% expressed in CrO ) 2 3 ' 3 Schorlemmer basιcιty= 50,5% Fe content = 1,0 mg per 100 g of liquid 15. Cu content = 0,6 mg per 100 g of liquid Ni content = 0,3 mg per 100 g of liquid Al content = 0,2 mg per 100 g of liquid Zn, V and Cd content= 0,1/0,2 mg per 100 g of liquid The material thus obtained was used to carry out a hide tanning 0 • test as described in example 8. EXAMPLE 4 Processing of exhausted liquids according to a further variant of the invention. An exhausted chromium plating bath having the following composi- tion was used: CrO (total) 18,5% (weight/weight) CrO Hexavalent 17,5% (weight/weight) 3 CrO Trivalent 1,0% (weight/weight) 3 5. Fe 50 parts per 1000 parts of total CrO Cu 30 parts per 1000 parts of total CrO Zn 5 parts, per 1000 parts of total CrO Al 1 part per 1000 parts of total CrO Ni 0,1 parts per 1000 parts of total CrO. 10. V traces and the following operations were performed: 100 kg of a bath having an initial pH of 0,5 were brought to pH 4 with a sodium hydroxide solution having NaOH titre 45% (15 kg) . After agitation for 1 h at 60°C it was filtered to obtain: 15. - 15 kg of wet solid (loss at 110°C = 50%) = 7,5 kg dry - 100 kg of liquid having the following composition: Hexavalent CrO = 15% (weight/weight) Trivalent CrO = absent Fe = 2 mg per 100 g of liquid 20. Cu = 2 mg per 100 g of liquid Zn = 0,2 mg per 100 g of liquid Al = 1 mg per 100 g of liquid Ni = 1 mg per 100 g of liquid V = traces 25. This liquid was concentrated by evaporating the water to a CrO concentration of 50% (weight/weight) and used to obtain both directly, by crystallization, sodium bichromate (Na CrO .2H 0) and , by addition of alkalis (sodium hydrate) and subsequent crystallization, sodium monochromate (Na CrO . 4H 0) . 2 4 2 EXAMPLE 5 Processing exhausted liquids according to a further variant of 5. the invention. To 10 kg of an exhausted chromium plating bath, having the composition indicated m the description, sodium persulphate was preliminarily added until the trivalent chromium had disap¬ peared. The bath was then treated as described in example 2. 10. A solid weighing 0,1 kg after drying at 110°C and a liquid wholly similar m its characteristics to that in example 2 were obtained. Th s liquid, thus purified and filtered, can be used for the synthesis of bichromate, monochromate and chromium sulphate, as 15. described m all preceding examples. The tanning operations, described in greater detail in the examples which follow, are carried out using: A) as laboratory apparatus: a 70 cm diameter drum with a rotation speed of 10 rpm. 20. B) as tannery apparatus: a 2500 cm diameter drum with a rotation speed of 8 rpm. C) as material for processing: light calf, kid or heavy cow skins ready for tanning pickled at pH 2,8, with a beamhouse weight of 30 kg for testing in the laboratory drum and 1500 kg for testing in the semi-industrial drum. In all the examples that follow all percentages refer to skins ready for tanning. 5. EXAMPLE 6 Tanning wi h 35 Sch basicity - Cr O titre 13,3 - conducted according to the present invention. After a successful test carried out in a laboratory drum, tanning was repeated in a semi-industrial drum. 10. 1500 kg of cow hides (each weighing 40-45 kg) were loaded into a drum with 100% water and 5% NaCl and after rotation for 10 minutes, 0,5% of concentrated H SO was added. he drum was then 2 4 kept in rotation for 30 minutes and the pH of the liquid when checked afterwards proved to be 3,6. 15. A further 0,25% of concentrated H SO was added and, after 2 4 rotation for 20 minutes, a sample of the liquid was removed and its pH proved to be 2,7, while the hide section had a pH of between 2,7 at the outside and 3 in the middle. The liquid was drained from the drum and 90% water and 9% basic 20. chromium sulphate solution, containing 13,3% of Cr O and having 35 Schorlemmer basicity, were added (the procedure for obtaining this solution was described in example 1) . After rotation for 10 minutes 1% of stuffing was added and the drum was kept rotating for 1 h. 0,5% of sodium formate was subsequently added. After rotation for 3 h the hide was checked for reaction and found to be 5. completely crossed by the chromium. The temperature of the path was 38 to 40°C. Basification was then begun by adding, in threee stages, NaHCO and precisely 0,3% at each stage, and rotating the drum for 20 minutes between the first and second addition. When all the 10. sodium bicarbonate had been added, the drum was kept in rotation the pH was checked after 1 h and found to be 4,2. The hides were then treated against mold so that they could be kept at length in wet blue and after the drum had been rotated for 1 h, the hides were removed and left m piles for 48 h 15. before pressing, splitting and shaving. Treated as described, the hides showed a uniform tanning colour and even gelling temperature (GT) . After the hides had been stored both the split and the gram were examined again and no abnormalities were found: they had remained of a uniform colour with good softness 20. and fullness characteristics. EXAMPLE 7 Tanning with 34 Sch basicity - 12,2% titre The 8/12 kg pickled hides of 3 French calves (beamhouse weight 30 kg) were placed in a laboratory tanning container (drum) and treated with 80% water, 2,6% Cr O from a solution of basic 2 3 chromium sulphate, having the following characteristics: basicity 34% Schorlemmer Fe content = 480 mg per 100 g of liquid 5. Cu content = 480 mg per 100 g of liquid Ni content — 1,6 mg per 100 g of liquid Al content = 16 mg per 100 g of liquid Zn content = 80 mg per 100 g of liquid V content = 0,8 mg per 100 g of liquid 10. After rotation for 2 h the chromium was found to have crossed the entire hide section. Three per cent of a 10% sodium carbonate solution was then added to the bath. Rotation was continued for 30 minutes, then a further 3% of 10% 15. sodium carbonate solution was added and rotation was continued for 30 minutes, after which a further 4% of 10% sodium carbonate solution was added; rotation was continued for 6 h. At the end of the six hours the pH of the solution was 3,8. The hides were unloaded from the drum, piled up for 48 h and then checked for 20. appearance before undergoing further processing. An abnormal clouring was immediately evident (dark green, tending to brown, with patches distributed over the whole surface) . The cause was put down to the impurities contained in the liquid, particularly to the presence of iron and copper which, as is known , are harmful to tanning operations . EXAMPLE 8 Tanning according to the invention with 50 Schorlemmer basicity and 12,2% Cr O 2 3 5. After delimmg, soaking and pickling, 1500 kg of cow hides were placed in a semi-industrial drum with 1,80% of the pickling bath solution in order to extablish a pH of 3,5. To this was added 7% of 12,2% Cr O solution with a basicity of 2 3 y 50 degrees Schorlemmer taken from the exhausted chromium plating 1 0. bath solution purified according to the method claimed in the present invention. The drum was kept in rotation for 30 minutes; stuffing was added m two stages and the drum was kept rotating for 2 h. A further 4% of 12,2% Cr 0 solution with 50° 2 3 Schorlemmer oasicity (from recovery of chromium plating baths) 15. was added and, after checking the pH of the bath, which proved to be 3,8, the hides were removed and left piled up for 48 h. The technital data confirmed a positive tanning result, with a good colour, regular penetration speed, absence of patches after 10 days of wet storage, even grain. The hides were subsequently 20. pressed, split and shaved to 1,2 mm, then neutralizing, dying and stuffing was carried out. The hides, subsequently pressed, were dried and perched. A good uniform colour, tne same degree of fullness and softness in all skins and good blowing strength were found.

Claims: C A I S 1. A process for recovering chromic anhydride from exhausted polluted chromium plating baths chacaterized in that alkali is added to the exhausted solution adjusting to a pH range between 3 and 7 and the mass is kept under reaction so 5. that the metallic pollutants are precipitated together with the chromium chromate; the precipitate obtained is separated from the solution containing hexavalent chromium by filtration. 2. A process accroding to claim 1, characterized in that before precipitation of all the metal pollutants in the pH range 10. between 3 and 7, the chromium is oxidized from the trivalent to the hexavalent state, using any of the known methods for this oxidation. 3. A process according to claim 1 or 2, characterized in that the solution containing hexavalent chromium is subjected to 15. the action of a reducer. 4. A process according to claim 3, characterized in that the reducer is sulphur dioxide which produces a solution of basic chromium sulphate and sodium sulphate. 5. A process according to any one of the preceding claims, characterized m that commercial sodium hydroxide is used as the alkali. - 6. A process according "to claim 1 or 2, characterized m that the solution containing hexavalent chromium is then used as basic material for the synthesis of hexavalent chromium salts. 7. A process according to any one of claims 3 to 5, characterized in that the solutions containing trivalent - chromium are used as hide tanning baths.

Inventors: BRUZZONE GIUSEPPE, GHELLI GIOVANNI, PERRONE DIEGO, BRUZZONE, GIUSEPPE, GHELLI, GIOVANNI, PERRONE, DIEGO
Applicants: STOPPANI LUIGI SPA, LUIGI STOPPANI S.P.A.
Application year: 1988
Main classification: C01G37
IPC codes: C01G37, C14C3