NOVEL COPOLYMER AND WATER- AND OIL-REPELLENT COMPRISING THE SAME

Abstract: A fluorine-containing copolymer comprising (a) 40 to 90 % by weight of repeating units deri­ ved from a polymerizable compound having a C₄-C₂₀ perfluoro­ alkyl group, (b) 5 to 50 % by weight of repeating units derived from at least one unsaturated ester selected from the group consisting of stearyl acrylate and stearyl methacrylate, (c) 5 to 50 % by weight of repeating units derived from at least one monomer selected from the group consisting of alkyl acrylate and alkyl methacrylate having 2 to 8 car­ bon atoms in the alkyl group, which is useful as an active component of a water- and oil-repellent.

Description: The present invention relates to a novel copolymer having a perfluoroalkyl group and a water- and oil-repellent comprising the same. More particularly, it relates to a novel copolymer which can impart good water- and oil-repellency and anti-slipping property to fabrics, and a water-and oil-repellent which has good durability against domestic washing and dry cleaning and stability when it is used in combination with other additives and impart slipping resistance to fabrics. DESCRIPTION OF THE RELATED ART A water- and oil-repellent comprising a polymer of a polymerizable compound having a perfluoroalkyl group has been known for many years. There have been proposed several copolymers of the polymerizable compound having a fluoroalkyl group with at least one of other copolymerizable compound such as alkyl acrylate, maleic anhydride, chloroprene, butadiene, methyl vinyl ketone and styrene to be used as water- and oil-repellents in various commercial fields and/or to impart some other properties to the water- and oil-repellent. To improve the water repellency and durability against domestic washing and dry cleaning of the water- and oil-repellent, it is proposed to use, as a water- and oil-repellent, a copolymer of the polymerizable compound having the perfluoroalkyl group with acrylate or methacrylate having a hydroxyl group (cf. Japanese Patent Publication No. 3798/1975). Further, some copolymers of the polymerizable compound having the perfluoroalkyl group with polymerizable compounds having various functional groups are used to improve the water repellency and durability of the water- and oil-repellent. Particularly, a copolymer comprising the polymerizable compound having the perfluoroalkyl group, stearyl acrylate or methacrylate and 2-hydroxy-3-chloropropyl acrylate or methacrylate is known to have excellent water- and oil-repellency and durability (cf. Japanese Patent Publication No. 8068/1985). EP-A-0157138 discloses graft polymerising an unsaturated perfluoroalkyl monomer onto an aqueous acrylic dispersion graft base. Examples taken from this document include the use of stearyl methacrylate as a further graft monomer component. As higher and more versatile properties are required for the water- and oil-repellent, it is necessary to further increase quality of the water- and oil-repellent. For example, the water- and oil-repellents comprising the above conventional copolymers do not have sufficient durability and stability when used together with other additives such as a finishing agent. In addition, fabric treated with the conventional water- and oil-repellents tend to cause slippage of yarns. One object of the present invention is to provide a novel fluorine-containing copolymer which can be used as a high quality water- and oil-repellent. Another object of the present invention is to provide a water- and oil-repellent which can impart improved water- and oil-repellency and anti-slippage property to a treated fabric. Further object of the present invention is to provide a water- and oil-repellent which can impart good water- and oil-repellency, resistance to washing and dry cleaning and anti-slippage property to a treated fabric and has good stability when used together with other additives. These and other objects are achieved by a fluorine-containing copolymer comprising (a) 40 to 90 % by weight of repeating units derived from a polymerizable compound having a C₄-C₂₀ perfluoroalkyl group, (b) 5 to 50 % by weight of repeating units derived from at least one unsaturated ester selected from the group consisting of stearyl acrylate and stearyl methacrylate, (c) 5 to 50 % by weight of repeating units derived from at least one monomer selected from the group consisting of alkyl acrylate and alkyl methacrylate having 2 to 8 carbon atoms in the alkyl group and a water- and oil-repellent comprising said copolymer. Optionally, the copolymer of the present invention may comprise (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom, (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group or (f) repeating units derived from glycidyl acrylate or methacrylate. DETAILED DESCRIPTION OF THE INVENTION Specific examples of the polymerizable compound constituting the repeating unit (a) are following acrylate and methacrylate: wherein R f is a C₄-C₂₀ perfluoroalkyl group, R¹ is a hydrogen atom or a C₁-C₁₀ alkyl group, R² is a C₁-C₁₀ alkylene group, R³ is a hydrogen atom or a methyl group, R⁴ is a C₁-C₁₇ alkyl group, n is a number of 1 to 10, and m is a number of 0 to 10. The content of the repeating units (a) in the copolymer is from 40 to 90 % by weight, preferably from 50 to 90 % by weight. When this content is less than 40 % by weight, the copolymer has insufficient water- and oil-repellency. The content of the repeating units (b) in the copolymer is from 5 to 50 % by weight. When this content is less than 5 % by weight, the copolymer has insufficient water repellency. Preferably, the copolymer contains 15 to 35 % by weight of the repeating units (b). Although the repeating units (b) increase waterand oil-repellency of the copolymer, they tend to impart undesired slipping property to the yarns in the fabric and to deteriorate stability when used together with isopropanol in a treatment step. To overcome such defects, the repeating units (c) are used according to the present invention. The content of the repeating units (c) is from 5 to 50 % by weight. When this content is less than 5 % by weight, the copolymer cannot sufficiently impart the antislipping property and resistance to isopropanol to the treated material. Preferably, the content of the repeating units (c) is from 5 to 25 % by weight. Specific examples of the alkyl acrylate and alkyl methacrylate having 2 to 8 carbon atoms in the alkyl group are ethyl acrylate and methacrylate, isopropyl acrylate and methacrylate, n-butyl acrylate and methacrylate, isobutyl acrylate and methacrylate, cyclohexyl acrylate and methacrylate, and 2-ethylhexyl acrylate and methacrylate. The monomer or monomers constituting each of the repeating units (a), (b) and (c) may be used as a single compound or as a mixture of two or more compounds. Optionally, the copolymer may comprise repeating units derived from other monomer. Examples of such other monomer are N-methylolacrylamide, N-methylolmethacrylamide, aziridinyl acrylate and methacrylate, diacetoneacrylamide, diacetonemethacrylamide, methyloled diacetoneacrylamide, methyloled diacetonemethacrylamide, 2-hydroxy-3-chloropropyl acrylate and methacrylate, hydroxy-(C₂-C₄)-alkyl acrylate and methacrylate, monoethyleneglycol monoacrylate and monomethacrylate, polyethylene glycol monoacrylate and monomethacrylate (degree of polymerization of polyethylene glycol being from 2 to 40), ethylene, vinyl acetate, vinyl fluoride, vinyl chloride, acrylamide, methacrylamide, styrene, α-methylstyrene, p-methylstyrene, C₁-C₂₀-alkyl acrylate and methacrylate, benzyl acrylate and methacrylate, vinyl C₁-C₂₀-alkyl ether, halogenated vinyl C₁-C₂₀-alkyl ether, vinyl C₁-C₂₀-alkyl ketone, maleic anhydride, butadiene, isoprene, chloroprene, and mixtures thereof. The content of the repeating units of other monomer is not more than 15 % by weight. Among the optionally copolymerized monomers, (d) an acrylate or methacrylate having at least one nitrogen atom and (e) an acrylate and methacrylate having at least one hydroxyl group are useful to increase water- and oil-repellency and durability of the water- and oil-repellent, since the nitrogen atom or the hydroxyl group of the monomer (d) or (e) may increase adhesion of the copolymer to the material such as fabrics by ionic bonding force. Among these two kinds of monomers, the monomer (d) is more preferred. The content of the monomers (d) and (e) is respectively from 0.1 to 5 % by weight. When the content is more than 5 % by weight, the dispersion stability is deteriorated. As the monomer (d), N-methylolacrylamide or N-methylolmethacrylamide is preferred, while aziridinyl acrylate and methacrylate, diacetoneacrylamide, diacetonemethacrylamide, methyloled diacetoneacrylamide and methyloled diacetylmethacrylamide can be used. As the monomer (e), 2-hydroxy-3-chloropropyl acrylate or methacrylate is preferred, while hydroxy-(C₂-C₅)-alkyl acrylate and methacrylate (e.g. 2-hydroxypropyl acrylate and methacrylate) and monoethylene glycol monoacrylate and monomethacrylate (degree of polymerization of polyethylene glycol being from 2 to 40) can be used. When the copolymer further comprises (f) repeating units derived from glycidyl acrylate or methacrylate in addition to the essential repeating units (a), (b) and (c), the water- and oil-repellent comprising said copolymer has excellent durability, since the repeating units (f) form covalent bonds between the treated material and the copolymer and cure the copolymer three dimensionally. The content of the repeating units (f) in the copolymer is from 0.1 to 5 % by weight, preferably from 2 to 5 % by weight. When the content is more than 5 % by weight, the dispersion stability is deteriorated, while when it is less than 0.1 % by weight, the durability of the water- and oil-repellent is not effectively improved. Further, the water- and oil-repellent comprising the copolymer consisting of the repeating units (a), (b), (c) and (d) or (f) or the repeating units (a), (b), (c), (d), (e) and (f) has much improved durability. The copolymer of the present invention may be prepared by copolymerizing the above described monomers by a per se conventional method such as bulk polymerization, solution polymerization, suspension polymerization, emulsion polymerization, radiation polymerization, and photopolymerization. For example, the monomer mixture is emulsified in water in the presence of a surfactant and copolymerized with stirring. In the reaction system, a polymerization initiator such as an azo compound or a peroxide may be added. As the surfactant, any of anionic, cationic or nonionic surfactants may be used. Among them, a mixture of at least one cationic surfactant and at least one nonionic surfactant is preferred. From the copolymer, the water- and oil-repellent can be formulated in any of suitable application forms such as an emulsion, a solution or an aerosol. The water- and oil-repellent may contain other polymer in addition to the copolymer of the present invention. Further, the water- and oil-repellent may contain other water-repellent or oil-repellent and suitable additives such as an insecticide, a flame-retardant, an anti-static agent, a dye stabilizer, a crease resisting agent, and a perfume. Any material can be treated with the water- and oil-repellent of the present invention. Examples of such material are fibers, yarns, fabrics, glass, paper, wood, leathers, furs, asbestos, bricks, cement, metals or metal oxides, ceramics, plastics, coated surfaces, and plasters. Among them, fibers of polyester, cotton, polyamide, acryl, silk, wool and their textile blends and their fabrics are preferably treated by the water- and oil-repellent of the present invention. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be illustrated by following Examples, in which the water- and oil-repellency were measured as follows: The water repellency is expressed by the water repellency No. of Table 1 determined by the spray method according to JIS (Japanese Industrial Standards) L-1092, and the oil repellency is expressed by the oil repellency No. of Table 2 determined by dropping several drops of a test solvent on a surface of the cloth treated with the water- and oil-repellent and observing whether the drops are held on the surface more than 3 minutes or not. The "+" or "-" mark suffixed to the water or oil repellency No. in the following Tables represent that the result is slightly better or worse than said water or oil repellency No. Resistance to washing is expressed by the water-and oil-repellency Nos. which are determined after washing a cloth treated with the water- and oil-repellent at 40°C in water containing 2 g/liter of a detergent (Zabu-koso, manufacture by Kao) with a bath ratio of 1:30 by weight (cloth: washing liquid) for 15 minutes by using a domestic washing machine followed by rinsing the cloth for 15 minutes, dehydrating it for 15 minutes and air drying at 110°C for 3 minutes. Resistance to dry cleaning is expressed by the water- and oil-repellency Nos. which are determined by washing a cloth treated with the water- and oil-repellent at 30°C in tetrachloroethylene by using a Launder-O-meter followed by drying at room temperature and then measuring the water- and oil-repellency. IPA (isopropyl alcohol) resistance is determined by diluting the water- and oil-repellent with a diluent shown in Table 3 and expressed by the maximum number at which no precipitation is formed. Resistance to slippage is determined according to ASTM D 1336-64 (1970) by means of a fabric shift tester. A prescribed sized piece of fabric to be tested is clamped at opposite sides and placed between a pair of grippers, the upper one of which is loaded with a load of 2 kg with fixing the bottom one of which. After twice reciprocating the upper gripper with a prescribed traveling distance, the fabric shift, namely the largest distance between the adjacent yarns is measured by means of a microscope. Resistance to slippage is expressed in terms of so measured fabric shift (mm). When the fabric shift of the cloth treated with the water- and oil-repellent is smaller than that of the untreated cloth, resistance to slippage is good. In Example, the fabric shift of the untreated cloth was 1.0 mm. Examples 1-20 and Comparative Examples 1-3 In a 500 ml flask, predetermined amounts of the monomers shown in Table 4 (the total amount of the monomers being 100 g) were charged, and then deoxygenated water (160 g), acetone (50 g), n-laurylmercaptan (0.2 g), an emulsifier (9 g) of the formula: in which n is 20 on the average (HS-220, trade name of Nippon Fat and Oil) and a compound (3.4 g) of the formula: were added and stirred at 60°C for one hour under a nitrogen stream. Thereafter, a solution of azobisisobutylamidine hydrochloride (1 g) in water (10 g) was added and stirred at 60°C for 3 hours under a nitrogen stream to copolymerize the monomers. The conversion in the polymerization reaction was more than 99 % according to gas chromatography. From this conversion, it was confirmed that the weight ratio of the repeating units in the copolymer substantially corresponded to that of the monomers charged. The obtained emulsion contained 30 % by weight of the nonvolatile components. The IPA resistance of the emulsion was measured. The result is shown in Table 4. The emulsion was diluted with water to a non-volatile content of 12 %. In the diluted liquid, a polyester fabric for measurement of water- and oil-repellency or a nylon fabric for measurement of slippage was dipped, squeezed by rolls, predried at 80°C for 3 minutes and heated at 150°C for 3 minutes. The treated polyester fabric was tested on its water- and oil-repellency and then its washing and dry cleaning resistance, and the treated nylon fabric was tested on slippage. The results are shown in Table 4.

Claims: A fluorine-containing copolymer comprising (a) 40 to 90 % by weight of repeating units derived from a polymerizable compound having a C₄-C₂₀ perfluoroalkyl group, (b) 5 to 50 % by weight of repeating units derived from at least one unsaturated ester selected from the group consisting of stearyl acrylate and stearyl methacrylate, (c) 5 to 50 % by weight of repeating units derived from at least one monomer selected from the group consisting of alkyl acrylate and alkyl methacrylate having 2 to 8 carbon atoms in the alkyl group. The fluorine-containing copolymer according to claim 1, which further comprises 0.1 to 5 % by weight of (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom or (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group or (f) repeating units derived from glycidyl acrylate or methacrylate. The fluorine-containing copolymer according to claim 1, which further comprises 0.1 to 5 % by weight of (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom, and 0.1 to 5 % by weight of (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group or (f) repeating units derived from glycidyl acrylate or methacrylate. The fluorine-containing copolymer according to claim 1, which further comprises 0.1 to 5 % by weigh of (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group and 0.1 to 5 % by weight of (f) repeating units derived from glycidyl acrylate or methacrylate. The fluorine-containing copolymer according to claim 1, which further comprises 0.1 to 5 % by weight of (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom, 0.1 to 5 % by weight of (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group and 0.1 to 5 % by weight of (f) repeating units derived from glycidyl acrylate or methacrylate. A water- and oil-repellent comprising a fluorine-containing copolymer which comprises (a) 40 to 90 % by weight of repeating units derived from a polymerizable compound having a C₄-C₂₀ perfluoroalkyl group, (b) 5 to 50 % by weight of repeating units derived from at least one unsaturated ester selected from the group consisting of stearyl acrylate and stearyl methacrylate, (c) 5 to 50 % by weight of repeating units derived from at least one monomer selected from the group consisting of alkyl acrylate and alkyl methacrylate having 2 to 8 carbon atoms in the alkyl group. The water- and oil-repellent according to claim 6, wherein the copolymer further comprises 0.1 to 5 % by weight of (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom or (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group or (f) repeating units derived from glycidyl acrylate or methacrylate. The water- and oil-repellent according to claim 6, wherein the copolymer further comprises 0.1 to 5 % by weight of (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom, and 0.1 to 5 % by weight of (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group or (f) repeating units derived from glycidyl acrylate or methacrylate. The water- and oil-repellent according to claim 6, wherein the copolymer further comprises 0.1 to 5 % by weigh of (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group and 0.1 to 5 % by weight of (f) repeating units derived from glycidyl acrylate or methacrylate. The water- and oil-repellent according to claim 6, wherein the copolymer further comprises 0.1 to 5 % by weight of (d) repeating units derived from an acrylate or methacrylate having at least one nitrogen atom, 0.1 to 5 % by weight of (e) repeating units derived from an acrylate and methacrylate having at least one hydroxyl group and 0.1 to 5 % by weight of (f) repeating units derived from glycidyl acrylate or methacrylate.

Inventors: AMIMOTO, YOSHIO, ENOMOTO, TAKASHI, HAYASHI, KAZUNORI, SHINJO, MASAYOSHI
Applicants: DAIKIN INDUSTRIES, LIMITED
Application year: 1988
Main classification: C08F220
IPC codes: C08F220, D06M15