A latent looped yarn, a fabric made of the same, and a method for manufacturing the latent looped yarn

Abstract: A latent looped yarn having fine loops therein before a weaving operation provides a potential for large loops therein, which large loops are revealed in a fabric, after the yarn has been woven therein at least as warp yarns, by heat treatment. The latent looped yarn is produced by an eddy current treatment and can be utilized to give a fabric having a spunlike handling and high yarn density.

Description: The present invention relates to a looped yarn which is produced in such a way that a running yarn is led into a texturing zone where it is subjected to an eddy current produced by a pressurized fluid to form opened loops and closed loops on a surface of the yarn. In more detail, the present invention relates to a latent looped yarn and a method for manufacturing it, in which opened loops and closed loops are previously provided on the yarn and the latent loops are revealed after the latent looped yarn is woven into a fabric, and a method for manufacturing such a fabric. The present invention also relates to a high density fabric made of latent looped yarn and having a spunlike touch (hereinafter referred to as a "spunlike" fabric). Various processes for producing bulky yarn are known in which the bulkiness is obtained by shrinking yarns containing filaments having different shrinkage properties along their length and/or shrinkage properties different from one another. US-A-3273328 described a process for producing a bulky yarn in which a crimped multifilament yarn component is stabilised against stretching by a multifilament yarn component in which the filaments are straight. The respective components are interlaced by an air jet either before or after crimping of one component. The crimped component may be provided by filaments having thermal shrinkage properties different from those of the straight component and capable of differential shrinkage during a crimping operation subsequent to interlacing. GB-A-1590207 described the preparation of a bulky yarn suitable for knitted fabrics. A drawn yarn having a single multifilament yarn component or a mixed drawn yarn having two different multifilament yarn components each having different thermal shrinkage properties is passed over a random heat-treatment pin, then to a fluid interlacing device and then over a tension control roller which provides a tension of the yarn at the heated pin lower than the thermal shrinkage stress of the yarn, thus loosening individual filaments and providing a contact time with the pin short enough to enable the heat from the pin not to be uniformly conducted to every part of the yarn. This produces filaments having thermal shrinkage values differing along the length of each filament and from one filament to another at any given cross section of the yarn. It also provides randomly arranged loosened arch portions. After the interlacing the filaments, they are supplied under an overfeed condition of at least 10% to an air jet texturing device where fluid turbulent flow causes randomly twisted portions which on release of the yarn form loops. GB-A-2048329 discloses a bulkable filamentary yarn having filaments which are essentially straight but have a series of interlaced portions along their length. The filamentary group between each pair of interlaced portions exhibits mixed, differential boil-off shrinkage characteristics both among the filaments and within each of the filaments. The yarn is obtained by feeding a yarn through a jet of turbulent fluid at a constant overfeed ratio to provide the yarn with intermittent interlaced portions between arch like, i.e. opened, looped portions, while avoiding the formation of closed loops. The resulting yarn is heat treated under a tension insufficient to remove the loops by stretching. The heat treatment causes the loops to shrink freely and provides them with an enhanced heat treatment as compared with the straight portions thus enhancing the difference in boil off shrinkage between the looped and straight portions. DE-A-1804525 described the preparation of a bulky yarn in which two multifilament yarn components of low and high shrinkage respectively are interlaced by air jet entangling. The yarn component of high shrinkage is overfed to the air jet zone which provides the yarn with arcs, the yarn component of highest shrinkage having the larger arcs. The material is then shrunk by heating and then false twist crimped. Thus various looped yarns in which many fine opened loops and closed loops are provided on each respective component filament of a multifilament yarn are known and have proved useful, since such a looped yarn has the characteristics of giving a fabric a voluminous feeling and a certain stiffness. But many operational problems arise when using such looped yarns in a weaving process to make a fabric; for example, the yarn is hooked at an abrasive contacting portion of a guide or tensor to create an abnormal tension on the yarn. This causes yarn breakage, or the element thereof is destroyed. There are many kinds of blown looped yarns in which a plurality of fine opened loops and closed loops are provided on each respective component filament of a multifilament yarn, for making a spunlike fabric utilizing multifilament yarns, and there have been many proposals for making such a yarn, since a fabric having a voluminous feeling and a certain stiffness can be produced from such yarns. These kinds of yarn inherently have a significant drawback such that, when a high tension exceeding a level of tension required is applied to the yarn, the loops are eliminated and thus the voluminous characteristic given to the yarn is lost. In addition, the voluminous characteristic disappears because the opened loops and closed loops thereof are formed on the surface of the yarn only by an entanglement among the component filaments. Fabrics are known which have a spunlike quality and which have a high density. Such a fabric is suitable for a coat or an outer garment for sports, which especially requires, in particular, waterproofing or wind breaking characteristics. Thus, as a fabric for such a purpose, JP-A-57-117647 proposes a high density fabric utilizing conjugated synthetic multifilament yarns having component filaments which are divisible and separable, while JP-A-59-204941 and JP-A-60-394385 describe fabrics having a water proofness, moisture permeability, and water repellency, which are produced by a process in which, firstly, a high density fabric is woven utilizing a mixed multifilament yarn comprising a multifilament yarn as a high shrinkage component and a multifilament yarn consisting of ultra fine filaments as a low shrinkage component, and a water repellent treatment is then applied to the fabric. These fabrics are provided with such water-proofness and moisture permeability by limiting the spaces between each filament to the order of microns, by arranging the filaments in such a way that the number of filaments per unit area of the high density fabric is set to an extreme upper limit. Accordingly, in the construction of such a fabric, the density of the filaments is increased by arranging the filaments as parallel to each other as possible. This fabric has a greasy feeling inherent in the ultra fine synthetic filaments, and has a drawback such that this fabric does not have a good natural unevenness, compared with the fabric made of spun yarns, from the visual point of view. Japanese Patent Publication 61-40778 discloses a method for manufacturing a napped fabric utilizing an interlaced and mixed multifilament yarn having a two-layer configuration in which a filament yarn having a high shrinkage ratio is used as a core yarn and ultra fine fibers entangled around the core yarn are used as a sheath yarn. A fabric woven or knitted with the yarn receives a napping treatment. Generally speaking, a looped yarn as mentioned above is used in most cases as a weft yarn when producing a spunlike fabric with the looped yarn, this being because of the problems mentioned above which arise especially when using looped yarns as warp yarns. But, if a high density fabric is to be produced utilizing multifilament yarns, it is not sufficient to use such a looped yarn only as a weft yarn thereof; such a looped yarn should be also used as a warp yarn. Nevertheless, when such a looped yarn is used as warp yarn of a fabric, other drawbacks arise; for example, the warp yarn density must be extremely coarse, because of the entanglement of the looped yarns with each other on a loom, which causes a problem of a lowered shedding ability during weaving, as well as the operational problems described above. To solve these problems, many attempts, such as attenuating the denier of filaments of a sheath yarn, have been made, but these require the use of several kinds of supplemental devices for taking up the looped yarn from a yarn package. But even when such a supplemental device is used, the warp yarn density is limited, and thus a fabric having high warp yarn density cannot be obtained. Furthermore, conventionally, in order to achieve a satisfactory take up of a yarn from a yarn package, or a satisfactory freedom of yarn passage through a weaving or knitting station or through a station arranged before or after such a weaving or knitting process at which a processing step (such as yarn or fabric treating process) takes place, it is necessary, in th warp yarn of the fabric, either to eliminate the loops entirely or to provide only a low density of loops and no loops of large size by ensuring that the difference in yarn length between the respective component filaments of the yarn is extremely small. Accordingly, a fabric having a satisfactory feel and surface touch cannot be obtained. Thus, at present a looped yarn cannot be used as a warp yarn for making a fabric having a relatively high yarn density. As is well known in this field, the number of loops and their size in a conventional looped yarn are seldom changed or are slightly increased, even if such a looped yarn is subjected to a hot water treatment with a subsequent free tension, and if such a looped yarn were used as a warp yarn, it would be impossible to obtain a fabric having a high yarn density and good spunlike feeling. Therefore, to make a spunlike fabric having a high yarn density, a looped yarn which can be used as a warp yarn must be realized. An object of the present invention is to overcome the technical drawbacks described above and to provide a new type of latent looped yarn which can also be used as a warp yarn of a high density fabric, and to provide a method for manufacturing it. In more detail, the present invention is intended to provide a latent looped yarn which can improve the yarn taking-up operation from a yarn package (difficulties arising here being one of the drawbacks associated with conventional looped yarns as described above), enabling unwinding of a yarn from the yarn package at a high yarn speed and, simultaneously, improving the conditions in a weaving process or other yarn treating process or fabric treating process arranged before or after the weaving process. The latent looped yarn can also be used as a warp yarn to enable a fabric to be made that has a high density weave construction, and further, can be used to make a spunlike fabric having a superior feeling and surface touch in the final product without applying to it a special treatment, such as a napping treatment. Further, an object of the invention is to provide a spunlike fabric having a high density utilizing such a latent looped yarn, and a method for manufacturing it. According to a first aspect the present invention provides a method for manufacturing a looped composite yarn in which at least first and second synthetic multifilament yarns are simultaneously fed to a texturing zone in which an eddy current flows, thereby producing a composite multifilament yarn having opened and closed loops on a surface thereof, and thereafter said composite multifilament yarn is stretched thereby eliminating or refining (i.e. reducing the size of) said opened and closed loops, the said first synthetic multifilament yarn having a shrinkage ratio in hot water higher than that of the said second synthetic multifilament yarn. According to a second aspect, the invention provides a high density fabric comprising: (a) warp yarns comprising a mixed composite multifilament yarn having opened loops and closed loops on a surface thereof according to claim 1 wherein the cover factor (CF) of the warp yarns, given by the equation CF = n √d , where n is the yarn density (ends/inch) and d is the yarn denier, or by the equation CF = 7.62 n SI √ tex , where n SI is the yarn density (ends/cm), is more than 1100; and (b) weft yarns. Such a fabric may be a mixed fabric comprising: (a) warp yarns or weft yarns comprising mixed composite multifilament yarns capable of shrinkage, having opened and closed loops on a surface thereof and comprising at least one synthetic multifilament yarn according to claim 1 and (b) weft yarns or warp yarns comprising spun yarns; wherein the total cover factor, as defined above, of the said warp and weft yarns is from 2000 to 3500. According to a third aspect, the invention provides a method of manufacturing a woven fabric having a spunlike feeling and resembling a fabric made of super high length cotton fibers, in which said fabric is woven with mixed composite multifilament yarns made of synthetic multifilament yarn components and having a total denier of less than 10 tex (90d) and said composite yarn consists of a filament "a" having a shrinkage ratio in hot water of more than 12% and a denier of a component filament thereof is more than 0.17 tex (1.5d) and total denier thereof is less than 6.67 tex (60d) and a filament "b" having a shrinkage ratio in hot water of less than 10% and a denier of a component filament thereof is less than 0.11 tex (1.0d) and total denier thereof is less than 6.67 tex (60d), and said composite yarn is further characterized by having, prior to shrinkage, more than 300 ends/m of the loop A, more than 50 ends/m of the loop B, and less than 10 ends/m of the loop C, each of said loop A, loop B, and loop C being defined hereunder, and after wearing a shrinking treatment is applied to said fabric to cause a differential shrinkage between said filament "a" and filament "b" which results in projecting opened loops and closed loops of said filament "b" on the surface of said fabric, wherein each of said loop A, loop B and loop C is defined in such a manner than when each loop is measured under a condition of a yarn speed of 50 m/min and a yarn running tension of 0.1 g/d (0.0108 cN/tex), by using a photo-electric type fluff measuring device by which the number of loops of a yarn running therethrough is counted, a loop projecting more than 0.15 mm from a yarn surface is defined as a loop A, a loop projecting more than 0.35 mm from the yarn surface is defined as a loop B, and a loop projecting more than 0.6 mm from a yarn surface is defined as a loop C. According to a fourth aspect, the invention provides a looped composite yarn having opened and closed loops on a surface thereof, which looped composite yarn comprises at least one synthetic multifilament yarn component having a high shrinkage ratio and at least one synthetic multifilament yarn component having a low shrinkage ratio, the shrinkage ratio in hot water of the filaments of the synthetic multifilament yarn component having a high shrinkage ratio being more than 10% and the difference in shrinkage ratio in hot water between that of the said filaments of the synthetic multifilament yarn component having a high shrinkage ratio and that of the said filaments of the synthetic multifilament yarn component having a low shrinkage ratio being more than 5%, whereby the said looped composite yarn is such that the total number of opened and closed loops thereof can be increased by thermally treating the yarn while free of tension, each said loop being classified as a loop in class A, B or C in terms of its projection height, the number of loops projecting above a given height being measured at a yarn speed of 50m/min and a yarn running tension of 0.1g/d (0.0108 cN/tex), loops in class A being loops which project more than 0.15mm from the yarn surface, loops in class B being loops which project more than 0.35 mm from the yarn surface, and loops in class C being loops which project more than 0.6mm from the yarn surface, the looped composite yarn having on the said surface thereof, before the said thermal treatment, more than 300 ends/m of loops in class A, more than 50 ends/m of loops in class B, and less than 10 ends/m of loops in class C, the number of loops, measured after a thermal treatment with hot water at 98°C for 10 minutes under a tension free condition and with subsequent drying, being such that at least the number of loops in class B is more than 1.5 times that of said looped yarn before heat treatment, and the number of loops in class C is more than 50 ends/m. Embodiments of the invention will now be described with reference to the accompanying drawings in which: Figure 1 is a schematic representation of one embodiment of a process for producing a latent looped yarn of the present invention; Figure 2 is a graph indicating the results obtained in Examples 1 and 2 of method embodying the invention as described below; Figure 3 is a cross sectional view of a filament having a flat shape in cross section, as used in a high density fabric embodying the present invention; Figure 4 shows looped yarn produced by an eddy current treatment with compressed air, as obtained in Example 5; Figure 5 shows latent looped yarn embodying the present invention obtained by stretching the looped yarn shown in Figure 4; Figure 6 shows bulked looped yarn obtained by heat-treating the looped yarn shown in Figure 4 with hot water at 98°C under tension free conditions; and, Figure 7 shows looped yarn embodying the present invention after developing latent loops on the surface thereof by heat-treatment the latent looped yarn shown in Figure 5 with hot water at 98°C under tension free conditions. To attain the above-mentioned objects of the present invention, use is made of a latent looped yarn which is a mixed composite multifilament yarn comprising at least two synthetic multifilament yarn components each having a different thermal shrinkage and having fine, i.e. small, opened loops and fine closed loops on a surface thereof. On thermally treating the composite multifilament yarn in boiling water, the total number of the closed and opened loops in the yarn and their size can be increased compared with those present in the multifilament yarn before heat treatment. Hereinafter, a "closed" loop means a loop in which the root portion is closed as shown by X in Figure 5, and an "opened" loop means a loop in which the root portion is opened, as shown by Y in Figure 5. Further, in a yarn in accordance with the present invention, the looped yarn is characterized in that, in accordance with a classification of the loops A,B,C, as defined hereunder, the total number of both the opened loops and closed loops provided on the surface of the latent looped yarn before receiving a heat treatment such as, for example, a hot water treatment under free tension, with the yarn in, for example, hank form, is such that there are more than 300 ends/m of loops A, more than 50 ends/m of loops B and less than 10 ends/m of loops C. When classifying the loops, their projection height and number are measured on a yarn running at a speed of 50m/min and a yarn running tension of 0.1 g/d (0.098 cN/tex), by using a photo-electric type fluff measuring device (for example, a fluff counter sold by TORAY Industries Inc. under the name of "TORAY FRAY COUNTER") which counts the number of loops of a yarn running therethrough. A loop projecting more than 0.15 mm from the yarn surface is defined as a loop A, a loop projecting more than 0.35 mm from the yarn surface is defined as a loop B, and a loop projecting more than 0.6 mm from the yarn surface is defined as a loop C. Further, the latent looped yarn is characterized in that a strong loop revealing force is retained inside the yarn in this condition. Note, preferably the looped yarn has a loop revealing force in which the number of loops B is increased by more than 1.5 times that of the yarn and the number of loops C is increased to more than 50 ends/m after the yarn is subjected to thermal treatment with hot water at 98°C for ten minutes under a shrink free condition and then dried. A latent looped yarn embodying the present invention will be now explained in more detail. The latent looped yarn embodying the present invention is a composite yarn which comprises basically a multifilament yarn component having a high shrinkage ratio and a multifilament yarn component having a low shrinkage ratio, and both multifilament yarn components may be arranged in a side by side configuration so as to be parallel to each other along the yarn axis, or may be arranged in a sheath and core configuration, in the latent looped yarn. In the latter case, the multifilament yarn component having a high shrinkage ratio is preferably arranged in a core portion of the latent looped yarn and the multifilament yarn component having a low shrinkage ratio of normal shrinkage ratio is preferably arranged in a sheath portion thereof. In the present invention, the latent looped yarn may be made by interlacing the multifilament yarn components with each other. The number and size of the fine opened loops and closed loops provided on the surface of the latent looped yarn of the present invention is small, and the voluminosity of the yarn is relatively small, as shown in Figure 5. A feature of a yarn in accordance with the present invention is that the number of opened loops and closed loops projecting more than 0.6 mm from the surface of the looped yarn, i.e., loops C, is less than 10 ends/m, which is remarkably small and can be considered negligible. In other words, in a condition (as shown in Figure 4) just after the yarn has been textured as a mixed composite multifilament yarn by an eddy current of pressurized air in the texturing zone, the latent looped yarn does not have an outer surface configuration resembling that of a bulky yarn. However, when this latent looped yarn is treated with heat in hot water at 98°C under free tension for 10 minutes, the latent looped yarn, per se, is caused to shrink by the shrinkage of the multifilament yarn components having a high shrinkage ratio and a low shrinkage ratio, as shown in Figure 7. As the multifilament yarn component having a high shrinkage ratio and the multifilament yarn component having a low shrinkage ratio are interlaced with each other, and as already known, the shrinkage of each component filament of a multifilament yarn component having a low shrinkage ratio is less than that of each component filament of a multifilament yarn component having a high shrinkage ratio, when such a latent looped yarn, per se, is shrunk, each component filament of the multifilament yarn component having a low shrinkage ratio is projected from the surface of the yarn to form opened loops and closed loops by the shrinkage of the multifilament yarn component having a high shrinkage ratio, which reduces the latent looped yarn into a looped yarn having revealed loops thereon and having a voluminous nature. The looped yarn having opened loops and closed loops revealed by the heat treatment has a remarkably increased voluminosity in which the number of loops B projected more than 0.35 mm from a yarn surface is increased by more than 1.5 times that of the composite yarn before heat treatment, and the number of loops C projected more than 0.6 mm from a yarn surface is increased to more than 50 ends/m after the composite yarn is subjected to a thermal treatment with hot water at 98°C for ten minutes under a shrink free condition, and dried. As described above, the latent looped yarn of the present invention has the latent opened loops and closed loops therein when it is produced, and the number of loops C projecting from the surface of the yarn is extremely small. Accordingly, the bulkiness, per se, of this yarn is very low, and the surface of the yarn is comparatively smooth, as shown in Figure 5. Therefore, the yarn running friction thereof on a device provided for this process is very small. Especially when this yarn is used as a warp yarn on a fabric, the running ability of the yarn in the head and the reed is excellent, and there is no possibility of an entanglement of the loops of adjacent warps with each other, or an incomplete shedding at a loom. Therefore, this yarn can be used as a warp of the fabric. Further, when a dyeing and finishing treatment is applied to the fabric after the weaving process, a high density and high bulk fabric can be obtained by subjecting the fabric to a heat treatment (utilizing dry heat, wet heat or steam heat, for example) at a high temperature in a tension free condition alone, or accompanied by a dyeing treatment, causing the latent opened loops and closed loops of the latent looped yarn to be revealed. To attain another object according to the present invention of manufacturing the latent looped yarn, at least two synthetic multifilament yarns each having a different shrinkage ratio are simultaneously fed into an eddy current zone to make the opened loops and closed loops on the surface of the yarn, and thereafter, the yarn is stretched to eliminate or refine the loops. In the process mentioned above, the shrinkage ratio in hot water of the multifilament yarn having a high shrinkage ratio may be more than 10%, and the difference in the shrinkage ratio in hot water between the multifilament yarn having a high shrinkage ratio and the multifilament yarn having a low shrinkage ratio may be more than 5%. Further, a component filament of the multifilament yarn having a low shrinkage ratio may have a denier of 0.05 - 2.5d (0.0055 - 0.28 tex), preferably 0.05 - 1.3 denier (0.0055 - 0.14 tex), and a component filament of the multifilament yarn having a high shrinkage ratio may have a denier of 0.1 - 15 denier (0.011 - 1.67 tex), preferably 0.3 - 15 denier (0.033 - 1.67 tex) and more preferably 1 - 15 denier (0.11 - 1.67 tex). A preferred embodiment of the process for making a latent looped yarn of the present invention will be now explained with reference to Figure 1, as an example. Figure 1 is a schematic representation of one embodiment of the process for making a latent looped yarn of the present invention. As shown in Figure 1, a high shrinkage multifilament yarn 2 unwinding from a package 1 is supplied to a texturing device 4 at which an eddy current zone is formed by compressed air, through feed rollers 3. At the same time, a low shrinkage multifilament yarn 6 unwinding from a package 5 is fed to the same texturing device 4 through feed roller 7. These multifilaments 2 and 6 are simultaneously fed to the texturing device 4 through suitable yarn guides 8 and 9. Note, in this process, the multifilament yarn 6 can be fed directly to the texturing device 4. After the multifilament yarns 2 and 6 have passed through the texturing device 4, which provides an eddy current of compressed air, they are wound onto a package 14 as a looped yarn 10, through a first take up roller 11, a second take up roller 12, and a winding device 13. During this process, the looped yarn thus produced is stretched between the take up rollers 11 and 12. This stretching operation is used to eliminate the large opened loops and closed loops of the looped yarn, and preferably is controlled so that it does not affect the development of the opened loops and closed loops during the heat treatment. Namely, if the stretch is too weak the large opened loops and closed loops are not properly eliminated and when the stretch is too strong, the fine opened loops and closed loops of the looped yarn formed by the eddy current zone are almost completely extinguished. Preferably, the elimination of the loops is carried out in such a way that the fine loops cannot be seen on the surface of the yarn by the naked eye but only by utilizing a microscope or a magnifying glass. The latent looped yarn of the present invention is preferably produced under the following conditions. Namely, in the process embodying the present invention, a multifilament yarn having a shrinkage ratio in hot water of more than 10% and having a filament denier of 0.1 - 15d (0.011 - 1.67 tex), preferably 0.3 - 15d (0.033 - 1.67 tex) and more preferably 1 - 15d (0.11 - 1.67 tex) is used as a high shrinkage yarn, and a multifilament having a shrinkage in hot water such that the difference in the shrinkage between the multifilament yarn having a high shrinkage ratio and that of the multifilament yarn having a low shrinkage ratio is more than 5% and having a filament denier of 0.05 - 2.5d (0.0055 - 0.28 tex) preferably 0.05 - 1.3d (0.0055 - 0.14 tex), is used as a low shrinkage yarn. These yarns are supplied to the texturing device 4 which provides the eddy current zone with compressed air (in which a feed volume of the compressed air is 80 - 120 ml/min), from the respective feed rollers, at a different overfeed ratio, and after the yarn is withdrawn from the texturing device, the looped yarns, which have been subjected to an interlacing and mixing treatment, are taken up by the same take up roller. The overfeed ratio used in a method in accordance with the present invention is based on the following equation, F(%) = (V₁ - V₂ )/V₂ x 100 wherein, V₁ represents the surface speed of the feed roller and V₂ represents the surface speed of the take up roller. Note that the overfeed ratio is defined only when the F value obtained from the equation is positive (+). In a method embodying the present invention, the overfeed ratio λ of the high shrinkage multifilament yarn is set at around 2 - 15% and the overfeed ratio β of the low shrinkage multifilament is set at around 5 - 30%. Further, more preferably, in the present invention the yarn withdrawn from the first take up roller is taken up by the second take up roller under a continuous stretching condition at an underfeed ratio of 0.4 λ - 0.8 λ to the overfeed ratio λ of the high shrinkage yarn. In a method embodying the present invention, a multifilament yarn having a filament denier of 0.1 - 15d (0.011 - 1.67 tex) is used as the high shrinkage yarn of the latent looped yarn. In other words, when the filament denier is less than 1d (0.11 tex), a desired yarn shrinkage cannot generally be obtained after the heat treatment, because the shrinkage of the filaments is small and shrinkage ratio of the yarn is substantially reduced. However, even when a filament having a denier of less than 1.0d (0.11 tex) is used, a sufficient yarn shrinkage can be obtained when the content thereof is more than 40 weight % of the yarn. When the filament denier is more than 15d (1.67 tex), the fabric obtained has a coarse feeling and experiences deteriorated handling because the yarn, per se, is very hard. Preferably, the shrinkage of the high shrinkage multifilament yarn is large, even though the use of a yarn having a large shrinkage causes other problems in that such a yarn has an inherent instability in its size which varies with lapse of time, and thus the quality of a product made with this yarn may not be stable. Accordingly, preferably a multifilament yarn having a shrinkage ratio of from 10 to 30% is used. On the other hand, a multifilament yarn having a filament denier of 0.05 - 1.3d (0.0055 - 0.14 tex) is preferably used as the low shrinkage multifilament yarn. Note that a multifilament having a filament denier of less than 0.05d (0.0055 tex) may be used, but when the denier becomes very small, the yarn handling will become difficult because of the development of fluffs, and when the filament denier thereof exceeds 1.3d (0.14 tex), it is difficult for the fine loops to be revealed and a fabric obtained from such a yarn will have a coarse handling. Note that the shrinkage of the low shrinkage multifilament is preferably as low as possible, but since special yarns generally have problems of yarn texturing ability and dyeing, preferably a multifilament yarn having a normal shrinkage (a shrinkage ratio ΔS of around 7.5%) is used. Namely, the difference between the shrinkage ratio of the high shrinkage multifilament yarn and the shrinkage ratio of the low shrinkage multifilament must be at least 5%, because the development of the opened loops and closed loops of the latent looped yarn depends completely upon such a difference in the shrinkage ratios. When making the latent looped yarn of the present invention, the overfeed ratio λ of the high shrinkage multifilament yarn is preferably 2 - 15% and the overfeed ratio β of the low shrinkage multifilament is preferably 5 - 30%, and further, the difference between the overfeed ratios β - λ is preferably 3 - 15%. These conditions are most suitable for forming the fine opened loops and closed loops in the eddy current zone with compressed air. The latent looped yarn obtained by a method embodying the present invention is a mixed composite yarn made of synthetic multifilament yarns each having a different shrinkage and having fine opened loops and closed loops on the surface thereof and the number and the size thereof can be increased by heat treatment under a free tension or shrink free condition. Namely, the yarn of the present invention must not have an outer configuration resembling that of a bulky yarn at the stage in which the yarn is textured as a mixed composite multifilament yarn by entanglement just after passing through the eddy current zone. However, as described above, when the latent looped yarn is treated by a thermal treatment with hot water at 98°C for ten minutes under a shrink free condition and dried, many opened loops and closed loops are projected and revealed on the surface of the yarn. EXAMPLES By using the yarn manufacturing method represented by Figure 1, a latent looped yarn was produced under conditions in which the overfeed ratio λ of a high shrinkage multifilament yarn and the overfeed ratio β of a low shrinkage multifilament were set at 9% and 15%, respectively, and a "TASLAN" type nozzle was used as a texturing device 4 with an air feed volume of 90 Nl/min, and further, the underfeed ratio between the first take up roller and the second take up roller was set at 5.4% (i.e., 0.6λ). The combinations of the high shrinkage multifilament yarn and the law shrinkage multifilament yarn used are as shown below: Example 1 High shrinkage yarn: Polyester multifilament 50D (5.55 tex) - 24F (having a high shrinkage ratio of ΔS = 20%) Low shrinkage yarn: Polyester multifilament 50D (5.55 tex) - 72F (having a normal shrinkage of ΔS = 7.5%) Example 2 High shrinkage yarn: Polyester multifilament 30D (3.33 tex) - 12F (having a high shrinkage ratio of ΔS = 20%) Low shrinkage yarn: Polyester multifilament 30D (3.33 tex) - 48F (having a normal shrinkage of ΔS = 7.5%) Comparative Example High shrinkage yarn: Polyester multifilament 30D (3.33 tex) - 12F (having a normal shrinkage of ΔS = 7.5%) Low shrinkage yarn: Polyester multifilament 30D (3.33 tex) - 48F (having a normal shrinkage of ΔS = 7.5%) The yarn shrinkage of the latent looped yarn thus obtained, and the characteristics of the loops before and after the treatment are disclosed in Table 1. Example 1 Example 2 Comparative Example Yarn shrinkage (%) 17.8 18.4 7.1 Before heat treatment loop A 447 332 332 loop B 125 72 68 loop C 1 1 1 After heat treatment loop A 438 416 363 loop B 390 330 115 loop C 168 88 11 Before stretching treatment loop A 345 340 loop B 101 96 loop C 13 12 In Table 1, the yarn indicated as "before the heat treatment" is the latent looped yarn of the invention, per se, and the yarn indicated as "after the heat treatment" is the looped yarn obtained from the latent looped yarn in such a way that the latent looped yarn was wound 100 times on a reel having a reel length of 1 m to make a short hank and then the short hank was immersed in hot water at 98°C for 10 minutes under a shrink free condition, and thereafter, dried. Further, the yarn indicated as "before the stretching treatment" is a yarn produced by winding up the latent looped yarn withdrawn from the first take up roller, without a stretching operation. Figure 2 is a graph indicating the results of the data shown in the Table 1. The characteristics of the loops of the Examples were measured by the following method. Namely, the yarn to be measured was passed through a photo-electric type fluff measuring device (for example, a "TORAY FRAY COUNTER") at a yarn running speed of 50 m/min and a yarn running tension of 0.1 g/d (0.0108 cN/tex) to count the number of loops on the yarn, and this counted number was indicated as a value per meter based upon the measured data obtained in 20 seconds (n = 5). On the other hand, for the measurement of the yarn after the treatment, the sample for measurement was produced in such a way that after the short hank was dried by air, it was mounted on a reel by hand, while ensuring that no tension was given to the yarn, and thereafter, was wound on a bobbin by slowly rotating the reel. As apparent from Figure 2 and Table 1, the number of loops C on the latent looped yarn in the Example of this invention is comparatively small, and although in the yarn before the stretching treatment, a small number of loops C can be seen, these loops C are completely eliminated to produce a condition wherein no loops exist on the yarn. In the methods of Examples 1 and 2, numbers of loops in classes B and C of the yarn after treatment are increased reasonably as compared with the numbers of such loops before treatment. However, conversely, the increase in the loops B and C in the Comparative Example is much smaller. By comparing the results of Example 2 with that of the Comparative Example, it can be seen that in Example 2 the number of loops B after the treatment is steeply increased to nearly 5-fold that of the number of loops B before the treatment, and the number of loops C after the treatment is also steeply increased up to 88 ends/m. However, in the Comparative Example, the increase in the number of loops B after the treatment is only 1.5 times that of the number before the treatment, which is regarded as small, and the number of loops C after the treatment is 11 ends/m, so that heating causes no increase in the number of loops C. Although the variations of the characteristics of the loop both before and after the stretching treatment were also considered, there were no significant differences therebetween, and thus only the data relating to the yarn after the stretching treatment are indicated. If the number of loops B after the heat treatment is not increased more than 1.5 times that of the number before the treatment, and the number of loops C is not more than 50 ends/m, the thus obtained looped yarn is not preferred because it has a very low bulkiness and a coarse touch feeling. It can be seen that the characteristics of the loops of the looped yarn depend upon the shrinkage ratio of the latent looped yarn and the difference between the shrinkage ratio of the high shrinkage yarn and the low shrinkage yarn. Namely, in the Comparative Example, there is no difference in the shrinkage ratio of the two yarns, and accordingly, the variation of the characteristics of the loops before and after the treatment is very small, and there is little difference between the loops on the yarn formed in the eddy current zone and those on the yarn after the heat treatment. In comparison, the characteristics of the loops of the yarn already treated by the heat treatment obtained in the Examples can be remarkably increased, because the shrinkage difference between the high shrinkage yarn and the low shrinkage yarn is large, and further, the high shrinkage yarn has a large shrinkage ratio, and these factors have a synergistic effect on the yarn. Example 3 In the process represented by Figure 1, a polyester multifilament yarn, 75D (8.33 tex) - 36F, having a shrinkage ratio in hot water of 15%, and consisting of 18 ends of filaments having a shrinkage ratio in hot water of 20% as high shrinkage components and 18 ends of filaments having a shrinkage ratio in hot water of 8% as low shrinkage components, was used as a core yarn, and a polyester multifilament yarn, 75D (8.33 tex) - 96F, having a shrinkage ratio in hot water of 8% was used as a sheath yarn, and these yarns were supplied to a texturing zone provided with a "TASLAN" nozzle at an overfeed ratio of the core yarn of +9% and an overfeed ratio of the sheath yarn of +20%, and were treated by a texturizing treatment under a high pressure of 8.0 kg/cm². Subsequently, the thus treated yarn was wound up on a package, while being stretched between the first take up roller and the second take up roller, at an underfeed ratio of -6.5%. The yarn characteristics thus obtained are as follows. Shrinkage ratio of the yarn 14. 2% Number of loops at the initial stage of the texturing process LOOP A 428 ends/m LOOP B 360 ends/m LOOP C 15 ends/m Number of loops after the eliminating treatment LOOP A 317 ends/m LOOP B 78 ends/m LOOP C 3 ends/m Number of loops after the recovery treatment LOOP A 395 ends/m LOOP B 320 ends/m LOOP C 45 ends/m The data of the number of loops after the recovery treatment is a conversion data in which the raw data thereof is modified by the shrinkage element. Also, in the data of the number of loops after the recovery treatment, the number of loops C is higher than that of the same loop measured at the initial stage of the texturing process. This is because a loosened or sagged portion of the filament created by the yarn shrinkage is counted in addition to the recovered loops. Example 4 In the process presented by Figure 1, a polyester multifilament yarn, 75D (8.33 tex) - 36F, having a shrinkage ratio in hot water of 20% was used as a core yarn and a polyester multifilament yarn, 75D (8.33 tex) - 96F, having a shrinkage ratio in hot water of 10% was used as a sheath yarn, and these yarns were supplied to texturing zone provided with a "TASLAN" nozzle at an overfeed ratio of the core yarn of +12% and an overfeed ratio of the sheath yarn of +20%, and were treated by a texturizing treatment under a high pressure of 6.0 kg/cm². Subsequently, the thus treated yarn was wound up on a package while being stretched between the first take up roller and the second take up roller, at an under-feed ratio of -3.0%. The yarn characteristics thus obtained are as follows. Shrinkage ratio of the yarn 10.4% Number of loops at the initial stage of the texturing process LOOP A 620 ends/m LOOP B 430 ends/m LOOP C 165 ends/m Number of loops after the eliminating treatment LOOP A 546 ends/m LOOP B 175 ends/m LOOP C 4 ends/m Number of loops after the recovery treatment LOOP A 573 ends/m LOOP B 397 ends/m LOOP C 182 ends/m Bulkiness of the yarn (cm³/g) At the initial stage of the texturing process 17.5 After the eliminating treatment 4.51 After the recovery treatment 19.49 Increment of the bulkiness (%) 432 The measurement of the bulkiness was carried out by using the method defined in Japanese Industrial Standard (JIS) L 1059C. The latent looped yarn obtained in this invention has a greatly improved yarn unwinding characteristic from a yarn package and has a superior yarn unwinding characteristic at a high yarn speed. In this invention, an extremely wide range of thermoplastic synthetic filaments can be used regardless of any restrictions on the filament denier or cross sectional shape of a component yarn of the sheath yarn, for example. Furthermore, when the latent looped yarn of this invention is used as a warp yarn of the fabric, the running ability of the yarn in the head and the reed is excellent and there is no possibility of entanglement of the loops of adjacent warps with each other, or an incomplete shedding at a loom. Consequently, a fabric having a high yarn density can be produced when such a looped yarn is used as a warp yarn. Furthermore, in this invention, a relaxed heat treatment can be applied to the fabric after the weaving process without tension and all of the latent looped yarn can perform the recovery motion to regain the loop shape formed at the initial stage of the texturing process. Therefore, a remarkable fabric having various kinds of feeling or surface touch can be obtained depending upon the method and condition of the relaxed heat treatment. Further, the latent looped yarn of this invention is a mixed composite multifilament yarn having opened loops and closed loops projecting from the surface thereof, and although the number of large sized loops classified into group C is very small, it has a superior characteristic such that, when subjected to a heat treatment, the number of large sized loops classified as loops B and C can be remarkably increased, and therefore, the weaving operation can be performed with a high efficiency. Furthermore, in this invention, the fabric obtained can possess a soft handling because a fabric having a high density can be made through the shrinkage operation by the heat treatment carried out after the weaving operation, whereby a large number of the opened loops and closed loops can be revealed on the surface of the fabric. In a conventional looped yarn, it has been necessary to provide as many opened and closed loops as possible on the surface thereof in order to obtain a fabric having good feeling and handling effects after dyeing and finishing treatments. However, when a yarn having many opened and closed loops is used as a warp yarn, the weaving operation has many problems, as mentioned above. Accordingly, in the conventional manner of using such a looped yarn as a warp yarn, the yarn density must be reduced or the number of opened and closed loops must be reduced, to maintain the weaving efficiency at the mass production level. However, this reduction in the numbers of opened and closed loops causes deterioration of the feeling or surface touch of the fabric. For a conventional looped yarn, the weaving efficiency of a looped yarn having a minimum loop level at which a fabric having a good spunlike handling is obtained, is such that the loom stopping counts indicated per 24 hours per loom was 24.1 counts/24 hr loom, as indicated in Table 2, and this is a bad result compared with the standard level of 10 counts/24 hr loom required for mass production. The fabrics obtained under such poor operating conditions have no value for final products, and accordingly, such fabrics have not been commercially available. In contrast to this, the latent looped yarn of this invention can have a remarkable effect on the weaving ability, such that the loop stopping count is as low as 4.3 counts/24 hr loom as shown in Table 2. In this invention, the number of opened loops and closed loops can be adjusted to any desired level merely by changing the difference in the shrinkage ratio of the core yarn and the sheath yarn, the shrinkage ratio of the core yarn and the overfed ratio of both the core yarn and the sheath yarn. Accordingly, in this invention, many superior functions and effects such a widening of the capability of designing fabrics, can be obtained. warp yarn 70D (7.77 tex) - 48F Conventional looped yarn 70D (7.77tex) - 60F Latent looped yarn Loop characteristic loop A (ends/m) 460 524 loop B ( " ) 170 126 loop C ( " ) 15 3 Weaving ability loom stopping count (count/24 hr loom) 24.1 4.3 Weaving conditions Weaving construction Plain Weaving density (warp x weft) 132 x 93 loom · revolution number WJL NISSAN LW-41 Type 400 rpm Weft yarn 70D (7.77 tex) - 60F latent loop yarn Next, spunlike fabrics having a high yarn density produced by using the latent looped yarn of this invention mainly as warp yarns are described as follows. As described above, the method of manufacturing a fabric having a spunlike handling, utilizing a looped yarn consisting of multifilament yarns having many opened loops and closed loops on the surface thereof formed by, for example, the "TASLAN" process, is already known. But such a conventional yarn can be used only as a weft yarn of the fabric, and there is a strict limitation on the use of such a yarn as warp yarns of the fabric, because of difficult yarn handling and poor yarn passing ability in the weaving process. In this invention, by using the latent looped yarn, all of the drawbacks mentioned above can be overcome and a high density fabric having a soft and spunlike feeling, wherein a mixed composite multifilament yarn having opened loops and closed loops is used as the warp yarns, can be obtained. According to the invention, the spunlike fabric utilizing a latent looped yarn is a high density fabric construction, in which a mixed composite multifilament yarn consisting of synthetic multifilament yarn components having opened loops and closed loops on a surface thereof, is used at least as the warp yarns of the fabric, and the cover factor of the warp yarns of the fabric is more than 1100. In this fabric, preferably the latent looped yarn used as a warp yarn is a mixed composite multifilament yarn comprising at least two multifilament yarn components each having a different shrinkage factor. The fabric of this invention will be now described more detail. By using a latent looped yarn consisting of synthetic multifilament yarn components having opened loops and closed loops, as the warp yarns, the opened loops and closed loops exist in a mixed state on the surface of the fabric, and such loops provided on the surface of the fabric give the fabric a soft handling touch which is the same as that of the fluff of a spun yarn, and simultaneously, an unevenness feeling like a fabric made of a spun yarn, because the arrangements of the multifilament yarns consisting of both the warp yarns and the weft yarns are not orderly, from a visual point of view. Note that the smaller the denier of a component filament, the better the spun like feeling of the fabric. Further, in a fabric embodying this invention, the fabric must be reduced to a fabric having a high density, to provide a soft and spunlike feeling and handling of the fabric, by the opened loops and closed loops existing in a mixed state on the surface of the fabric utilizing the latent looped yarn, and for giving the fabric a suitable stiffness and avoiding the problems of a fastening effect caused by the loops or dust accumulation. Therefore, in the fabric of this invention, the yarn density of the warp yarn must be set in such a way that the cover factor of the mixed composite multifilament yarn having opened loops and closed loops used as warp yarns in the fabric already treated by a dyeing and finishing treatment is more than 1100, and preferably less than 1600. Generally speaking, if the cover factor of the warp yarn is more than 1100, as mentioned above, when a weaving operation is carried out by using such a mixed composite multifilament yarn having opened loops and closed loops, such loops provided on each adjacent warp are entangled with each other by repeated mutual contact therebetween caused by the shedding operation of the loom, and thus problems such as an incomplete shedding or picking will arise, and therefore, a fabric having a good quality can not be produced at a mass production level. In this invention, contrary to the conventional looped yarn, the latent looped yarn is used to improve the yarn passage ability in the weaving process, and thus a fabric having a relatively high yarn density, compared with a fabric made of the conventional looped yarn, can be woven, and further, this fabric can be reduced to a fabric having a higher yarn density by shrinking by a heat treatment under a shrink free condition, such as a relaxed treatment in the dyeing and finishing treatment. Namely, in this invention, a high density fabric can be produced even when a mixed composite multifilament yarn having opened loops and closed loops thereon is used as the warp yarns. The fabric of this invention has finer surface characteristics as compared with a fabric made of the conventional looped yarn produced by a eddy current treatment, because the loops which are potentialized in the yarn are revealed in the fabric by a loop developing treatment, and thus the number of loops revealed on the cross point of the warp and weft yarn is very small. As already known, the feel or handling of a fabric mainly depends upon the effect of a warp yarn in a general fabric having a normal weaving construction, although when the latent looped yarn which is the same yarn as used for the warp yarn is used for the weft yarn, a high yarn density fabric utilizing the looped yarn as both the warp and weft yarns can be obtained, and the handling thereof and a spunlike and soft feeling of the surface thereof is far superior to that of a fabric made of the looped yarn produced by the eddy current treatment and used as the weft yarns. Moreover, as the weft yarn used in a fabric embodying the present invention, the mixed composite multifilament yarn comprises at least two synthetic multifilament yarn components each having a different shrinkage ratio and having a total shrinkage ratio in hot water of more than 10%, or a yarn having a low shrinkage ratio in hot water but having a shrinkage ratio in dry heat of more than 10%, or even a mixed spun yarn comprising staple fibers each having a different shrinkage ratio, can be used. As the low shrinkage component of the mixed composite multifilament yarn or spun yarn, fibers or filaments having a smaller single fiber denier than that of the fiber used in the high shrinkage component are preferably used, to obtain a fabric having a soft feeling and spun like outer configuration and to prevent a fastening effect and dust accumulation. Note, that the latent looped yarn of the construction described above can be applied to a fabric having such a high yarn density. The most preferable yarn construction of the latent looped yarn of this invention in such that the multifilament yarn component having a high shrinkage ratio is preferably arranged in a core portion of the latent looped yarn and the multifilament yarn component having a low shrinkage ratio or normal shrinkage ratio is preferably arranged in a sheath portion thereof, although the yarn construction of this invention is not restricted to this construction. The manufacturing method for obtaining the latent looped yarn explained above can be also applied to the method for making a fabric having a high density as described above. As described above, the latent looped yarn of this invention has latent opened loops and closed loops therein when produced and the number of loops C projecting from the surface of the yarn is extremely small. Accordingly, the bulkness of this yarn, per se, is very low and the surface of the yarn is comparatively smooth, and therefore, its yarn running friction in a device provided in this process is very small. Especially, when this yarn is used as a warp yarn of a fabric, the running ability of the yarn in the heald and the reed is excellent, and there is no possibility of an entanglement of the loops of adjacent warps, or an incomplete shedding at a loom. Therefore, this yarn can be used as a warp of the fabric. Further, when a dyeing and finishing treatment is applied to the fabric after the weaving process, a high density and high bulky fabric can be obtained by treating the fabric with a heat treatment (utilizing dry heat, wet heat or steam heat, for example) at a high temperature in a tension free condition alone, or accompanied by a dying treatment, causing the latent opened loops and closed loops of the latent looped yarn to be revealed. Example 5 In the process represented by Figure 1, a bright polyester multifilament yarn, 50D (5.55 tex) - 24F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 20% was used as a component yarn, preferably as a core yarn, and a bright polyester multifilament yarn, 50D - 72F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 7. 5% was used as a component yarn, preferably as a sheath yarn, and these yarns were supplied to a texturing zone provided with a eddy current nozzle at an overfeed ratio of the core yarn of +9% and an overfeed ratio of the sheath yarn of +15% and treated by a texturizing treatment at an air feed volume of 90 N l/min. Subsequently, the thus treated yarn was wound up on a package while being stretched between the first take up roller and the second take up roller, at an under-feed ratio of -5.4%. The yarn characteristics thus obtained are as follows. Total yarn denier 106 D (11.78 tex) Shrinkage ratio of the yarn 17.8% Number of loops before the heat treatment LOOP A 447 ends/m LOOP B 125 ends/m LOOP C 1 ends/m Number of loops after the heat treatment LOOP A 438 ends/m LOOP B 390 ends/m LOOP C 168 ends/m Thereafter, the thus obtained latent looped yarn was used as warp and weft yarns to make a plain weave fabric, utilizing a water jet loom with a warp yarn density of 85 ends/inch (33.5 ends/cm) (the cover factor of the warp yarn was 850) and a weft yarn density of 78 ends/inch (30.7 ends/cm). The grey fabric was then given the following sequence of treatments; a relaxed treatment, an intermediate setting treatment, an alkali weight loss treatment (5%), a dyeing treatment, and a finishing treatment, and a high density fabric having a warp yarn density of 117 ends/inch (46.1 ends/cm) (the cover factor of the warp yarn was 1170) and a weft yarn density of 100 ends/inch (39.4 ends/cm) was obtained. In terms of yarn density (ends/inch), n, and yarn denier, d, the cover factor (CF) is given by the equation CF = n √d. In terms of yarn density (ends/cm), n SI , and yarn tex, the cover factor (CF) is given by the equation CF = (2.54 /9)n SI √ tex = 7.62N SI √ tex . The thus obtained fabric had opened loops and closed loops existing in a mixed state on the surface of the fabric, and had a superior soft touch and spunlike feeling similar to a fabric made of a spun yarn, because the surface of the fabric embodying the invention was covered with fine and micronized loops, and further, the fabric had a good stiffness because it had a high yarn density. Example 6 In the process represented by Figure 1, a bright polyester multifilament yarn, 30D (3.33 tex) - 12F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 20% was used as a component yarn, preferably as a core yarn, and a bright polyester multifilament yarn, 30D (3.33 tex) - 48F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 7.5% was used as a component yarn, preferably as a sheath yarn, and these yarns were supplied to a texturing zone provided with an eddy current nozzle at an overfeed ratio of the core yarn of +9% and an overfeed ratio of the sheath yarn of +15%, and were treated by a texturizing treatment with an air feed volume of 90 N l/min. Subsequently, the thus treated yarn was wound up on a package while being stretched between the first take up roller and the second take up roller, at an underfeed ratio of -5.4%. The yarn characteristics thus obtained are as follows. Total yarn denier 63 D (7.0 tex) Shrinkage ratio of the yarn 18.4% Number of loops before the heat treatment LOOP A 332 ends/m LOOP B 72 ends/m LOOP C 1 end/m Number of loops after the heat treatment LOOP A 416 ends/m LOOP B 330 ends/m LOOP C 88 ends/m Thereafter, the thus obtained latent looped yarn was used as the warp and weft yarns to make a plane fabric, utilizing a water jet loom, with a warp yarn density of 142 ends/inch (55.9 ends/cm) (the cover factor of the warp yarn was 1100) and a weft yarn density of 110 ends/inch. The grey fabric was then treated by the following sequence of treatments; a relaxed treatment, an intermediate setting treatment, an alkali weight loss treatment (5%), a dyeing treatment, and a finishing treatment, and a high density fabric having a warp yarn density of 177 ends/inch (69.7 ends/cm (the cover factor of the warp yarn was 1370) and a weft yarn density of 135 ends/inch (53 ends/cm), was obtained. The thus obtained fabric had opened loops and closed loops existing in a mixed state on the surface of the fabric, and had a superior soft touch and spunlike feeling similar to a fabric made of the spun yarn, because the surface of the fabric of this invention was covered with fine and micronized loops, and further, the fabric of this invention had a good stiffness because this fabric had a high yarn density. The fabric embodying the invention has a high density, although having a stiffness based upon the bulkiness of the yarn, and simultaneously, has an improved water proof characteristic, and therefore, when a water repellent finish is applied to the fabric after the dyeing treatment, the fabric is suitable for use in sports products, especially ski wear products. When the high density fabric embodying the invention having a spunlike feeling is further developed, another spunlike fabric having a high density, which is suitable for a coat or an outer garment for sports wear, which requires, in particular, waterproofing or wind breaking characteristics, can be obtained. By making a fabric embodying the invention as explained below, the technical problems described above with particular reference to JP-A-57-117647 can be overcome and a spunlike high density fabric, having not only waterproofness and moisture permeability but also a spunlike feeling and an outdoor look, can be provided. The fabric mentioned above has a construction in which the latent looped yarn described above is used as a warp yarn and a synthetic multifilament yarn, each component filament of which having a flat cross sectional shape, is used as a weft yarn and the total cover factor of the warp yarn and the weft yarn is from 1800 to 3500. In a high density fabric embodying the invention, as a looped yarn for the warp yarn, the latent looped yarn is used and the latent looped yarn is preferably a composite yarn having a sheath-core type yarn configuration, wherein in the synthetic multifilament yarn used as the core portion of the composite yarn a single component filament thereof has a relatively large denier, and in the synthetic multifilament yarn used as the sheath portion of the composite yarn a single component filament thereof has a relatively small denier. Note that in a fabric of the invention, the yarn construction is not restricted to a sheath-core type composite yarn. Generally speaking, the stiffness of a high density fabric is high and its handling is coarse because movement of the yarns relative to each other, inside the high density fabric, is restricted. Accordingly, preferably an ultra fine multifilament yarn having a component filament denier of 0.05 - 1.3d (0.0055 - 0.14 tex) is used as the yarn component for the sheath portion of the composite yarn, and further, preferably a multifilament yarn having a component filament denier of 0.1 - 15d (0.011 - 1.67 tex), is used as the yarn component for the core portion thereof, so that voluminosity and resilience can be given to the fabric. Both the yarn construction and the yarn making method mentioned above can be applied to the yarn construction of the latent looped yarn and the manufacturing method thereof in this embodiment. On the other hand, a flat ratio of the filaments having a flat cross sectional shape consisting of the synthetic multifilament, used as a weft yarn in this embodiment, is preferably 2.0 - 6.0. When the flat ratio is less than 2.0, the waterproofness or wind breakability, which is provided mainly by the flatness of the filament, will be small, but on the other hand, when the flat ratio is more that 6.0, the luster of the fabric will be increased and the spunlike feeling or outer configuration thereof caused by the warp yarn will be reduced. Accordingly, a preferred flat ratio is from 2.0 to 6.0. The flat ratio of this embodiment is represented by "b/a", wherein "a" and "b" are the thickness and lateral dimensions respectively of the cross sectional shape as shown in Figure 3. As the multifilament having a flat cross sectional shape is naturally accurately arranged in a certain direction in the fabric, the space provided between the adjacent yarns can be reduced and made extremely narrow, enabling an increase in the waterproofness and moisture permeability of the fabric. In a fabric woven using a hundred percent of multifilament yarns having a flat cross sectional shape, problems arise in that the fabric has a smooth feeling and strong luster caused by the light reflected at the surface of the fabric. However, these problems can be overcome using a fabric embodying the invention because of the resistance of the closed loops and opened loop on the surface of the fabric, which causes a reduction in smoothness and luster. Further, when a multifilament having a flat cross sectional shape is used in a weaving process, the filaments are preferably not subjected to a heat treatment such as a false twisting process, and post twisting is avoided as much as possible, in order to actuate the shrinkage characteristic of the filaments. Namely, even when such a yarn is used as a warp yarn, the post twisting number should be less than about 300 turns/m. As the method for obtaining a composite yarn having a high shrinkage multifilament yarn component and a low shrinkage multifilament yarn component for providing the latent looped yarn embodying the invention, a direct spinning and drawing method, a filament mixing method in which the high shrinkage component multifilament yarns and the low shrinkage component multifilament yarns are respectively spun previously and then mixed, or a filament mixing method in which two high shrinkage component multifilament yarns are spun and then one of the yarns is treated with heat utilizing a hot plate to make a low shrinkage multifilament yarn which thereafter is mixed with the high shrinkage multifilament yarn not subjected to the heat treatment, can be used. An example of a high density fabric mentioned above will be now explained. Example 7 In the process represented by Fig 1, a bright polyester multifilament yarn, 30D (3.33 tex) - 12F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 20% was used as a component yarn, preferably as a core portion, and a bright polyester multifilament yarn, 30D (3.33 tex) - 48F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 8% was used as a component yarn, preferably as a sheath portion, and these yarns were supplied to a texturing zone provided with an eddy current nozzle at an over feed ratio of the core side yarn of +9% and an overfeed ratio of the sheath side yarn of +15% and treated by a texturizing treatment having an air feed volume of 90 N l/min at a feed ratio of the first to the second take up roller of -5.4%. The thus obtained looped yarn had a total yarn denier of 63D (6.7 tex) and shrinkage ratio in hot water of 18.4%, and the number of loops before the heat treatment was such that the loops A were 332 ends/m, the loops B were 72 ends/m, and the loops C were 1 end/m, while the number thereof after the heat treatment, i.e., a shrinkage treatment in hot water under a shrink free condition, was such that the loops A were 416 ends/m, the loops B were 330 ends/m, and the loops C were 88 ends/m, and these latent looped yarns were used as the warp yarns. Further, a bright polyester multifilament, 50D (5.55 tex) - 24F, each component filament of which had a flat cross sectional shape and a flat ratio of 4.5 and which had a total shrinkage in hot water of 15.7%, comprised a multifilament yarn, 25D (2.77 tex) - 12F, having a shrinkage ratio in hot water of 16.5% and a multifilament yarn, 25D (2.77 tex) - 12F, having a shrinkage ratio in hot water of 10.3%, and spun by a direct spinning and drawing method, was used as the weft yarns. Then a fabric having a warp yarn density of 114 ends/inch (44 ends/cm), and a weft yarn density of 120 ends/inch (47 ends/cm), and had a total cover factor, i.e. a sum of the cover factors of the warp and weft,of 1730, was woven. The method for measuring the cover factor as described above is also applied to this embodiment. Thereafter, the thus obtained fabric was dyed in a conventional relaxing and dyeing process and then finished by a finishing process with a water repellent agent. The thus treated final fabric had a warp yarn density of 156 ends/inch (61 ends/cm) and a waft yarn density of 146 ends/inch (57 ends/cm), and had a total cover factor, i.e. sum of the cover factors of the warp and weft yarns, of 2240. Moreover, the fabric had various functionally useful features, namely a waterproof pressure of 560 mm, a water repellency of 90 points, and a moisture permeability of 8200 g/cm²/24 Hr, and this was a superior fabric having a high density and spunlike feeling both in handling and external configuration which cannot be obtained in a fabric made of a conventional textured yarn such as "TASLAN". In the example above, the latent looped yarn embodying the invention is mainly used as the warp yarns. However, a latent looped yarn of this invention need not be used only as the warp yarns but can be also used as both the weft yarn and the warp yarn, or as the weft yarn alone. Next, by a method of producing a fabric embodying the invention, a spunlike high density fabric having a softer feeling than that of the fabric obtained in the example immediately above was obtained. This fabric has the following fabric construction. Namely, a mixed fabric having a high density, in which mixed composite multifilament yarns consisting of at least a synthetic multifilament yarn component capable of shrinking and having fine opened loops and closed loops on a surface thereof, were used as warp yarns and spun yarns were used as weft yarns or warp yarns, and was further characterized in that a total cover factor of the warp yarns and the weft yarns thereof was from 2000 to 3500. In this embodiment, a fabric having a high yarn density, which heretofore could not be produced by utilizing spun yarns, can be obtained, and further, a fabric having a good handling never seen heretofore and a spunlike external configuration caused by the fluffs of the spun yarns and the opened loops and the closed loops of the multifilament yarn components, which are joined together, was obtained. In this embodiment, the latent looped yarns may be used as a warp yarn or a weft yarn or as both. The yarn construction and the method for producing it, as mentioned above, can be applied to this embodiment. But, as the latent looped yarn used in this embodiment, the preferred yarn construction is the same construction of the latent looped yarn used as a warp yarn explained in the previous embodiment. In this embodiment, when the latent looped yarn is used as a warp yarn and the spun yarn is used as a weft yarn, a fabric having an extremely high yarn density, which can not be realized by using the conventional looped yarn, can be produced, because the latent looped yarn has a straight configuration which is not recognized as a looped yarn at a glance, and is completely different from the looped yarn obtained by a conventional eddy current treatment. Accordingly, in this embodiment, the fabric may be woven with as high a warp yarn density as possible, and with the spun yarns as a weft yarn at a normal or higher density, and then thus woven the fabric is shrunk in the warp direction by a shrinking treatment carried out in a later process, such as a dyeing process, to make the fabric into a fabric having a high weft yarn density, and simultaneously, to make a fabric having a high density and superior spun like effect both in feeling and external configuration without losing the handling effect of the spun yarns. The latent looped yarn may be used with post twisting. As the spun yarn, a spun yarn made of natural fibers such as cotton, wool, linen or silk, or made of the synthetic fibers such as polyester, nylon or acrylic, or a mixed spun yarn consisting of at least two kinds of fiber selected from any of those mentioned above, can be used. However, in consideration of the count number of the spun yarn, a fine yarn count such as more than 30S (less than 19.68 tex) in a cotton count system is desirable, in order to obtain a thin fabric. Moreover, in this embodiment, the spun yarn is preferably used as a single yarn. In the case of a high density fabric in which the spun yarns are used as warp yarns, by using the latent looped fabric having a shrinkage ratio in hot water of more than 10%, preferably more than 15%, and having closed and opened loops, as the weft yarns, the fabric can be woven with a comparatively coarser yarn density than the desired yarn density by calculating the increment of the density caused by the shrinkage of the weft yarn. When the fabric is treated thereafter in the dyeing process, to bulk up the fabric, the fabric can be reduced to a fabric having a further high yarn density by attaining a bulkiness and high density thereof, and simultaneously, increasing the picking density of the weft yarn. Example 8 As a warn yarn, a single polyester 100% spun yarn having cotton count of 60S (9.84 tex) is used, and as a weft yarn, a latent looped yarn made by the process described hereunder is used. Namely, in the process represented by Figuue 1, a bright polyester multifilament yarn, 30D (3.33 tex) - 12F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 20% is used as a component yarn, preferably as a core portion, and a bright polyester multifilament yarn, 30D (3.33 tex) - 48F, having a circular cross sectional shape and having a shrinkage ratio in hot water of 7.5% is used as a component yarn, preferably as a sheath portion, and these yarns are supplied to a texturing zone provided with an eddy current nozzle at an overfeed ratio of the core side yarn of +9% and an overfeed ratio of the sheath side yarn of +15% and are treated by a texturizing treatment having an air feed volume of 90 N l/min at a feed ratio of the first to the second taking up roller of -5.4%. The thus obtained looped yarn has a total yarn denier of 63D (7.0 tex) and a shrinkage ratio in hot water of 18.4% and the number of loops before the heat treatment is such that the loops A are 332 ends/m, the loops B are 72 ends/m, and the loop C is 1 end/m, and the number thereof after the heat treatment, i.e., a shrinkage treatment in hot water under a shrink free condition, is such that the loops A are 416 ends/m, the loops B are 330 ends/m, and the loops C are 88 ends/m. Then a plain weave fabric was woven with the warp yarn and the weft yarn mentioned above, utilizing a rapier loom, and thereafter, the gray fabric thus obtained was treated by a usual conventional relaxing operation and dyeing operation utilizing a jet dying machine. The fabric thus obtained was finished with a water repellent treatment, and a calendering treatment on the back surface of the fabric, after being treated with a setting treatment for finishing, and the thus finished final product had improved functions due to an increase of the warp yarn density and a desirable finishing effect having an excellent feeling and external configuration which cannot be obtained by the conventional method, as indicated below. Further, the weaving ability of the fabric was excellent and problem-free. In the comparative embodiment described below, the fabric was woven with 100% single cotton spun yarns having a cotton count of 80S (combed cotton yarn) (7.38 tex). Example Comparative Example Warp yarn density x weft yarn density of the gray fabric (ends/inch) 114 x 110 146 x 131 [Ends/cm] [49x43] [57x52] (Cover factor) (1920) (2257) Warp yarn density x weft yarn density of the fabric after dyeing 152 x 120 157 x 135 (Cover factor) (2350) (23280) Water proof pressure (mm) 430 210 Moisture permeability (g/cm²/24 hr) 8450 8810 Example 9 In this Example, a plain weave fabric was woven utilizing the latent looped yarn used as a weft yarn in Example 8 as a warp yarn, and 100% of single cotton spun yarns having a cotton count of 80S (combed cotton yarn) (7.38 tex) as a weft yarn, by a rapier loom. Then the thus obtained fabric was treated by a dyeing process in which a relaxing treatment, an intermediate setting treatment, a dyeing and finishing treatment, a water repellent treatment, and a calendering treatment on the back side of the fabric were applied to the fabric, in this order. The thus obtained fabric had a similar feeling and external configuration as the fabric made of 100% spun yarns, and superior functions, as described hereunder. Warp yarn density x weft yarn density of the gray fabric 176 ends/in x 95 ends/in (69 ends/cm x 35 ends/cm) (Cover factor) (2168) Warp yarn density x weft yarn density of the fabric after dyeing 183 ends/in x 118 ends/in (72 ends/cm x 46 ends/cm) (Cover factor) (2410) Water proof pressure (mm) 410 Moisture permeability (g/cm²/24 hr) 8600 The cover factor used in this embodiment is obtained by the following equation. Cover factor = [warp yarn density (ends/inch) + weft yarn density (ends/inch)] x√d wherein, d is the multifilament yarn denier, and when a spun yarn is used, the cotton count number S is converted into denier d by the equation: 5315/cotton count number. As a spun like fabric, a fabric made of a high quality cotton, especially made of a spun yarn having a cotton count number of more than 60S (less than 9.84 tex), the yarn of which consists of cotton fibers having a super high staple length, is required, and thus many attempts to make a fabric having a similar handling to that of a fabric utilizing synthetic fibers have been made. The handling or feel thereof reached a high level, due to improvements in the spinning technology and the yarn texturizing technology, especially in the attenuation of a filament denier to an ultra fine denier, or producing an alternating twisted false twisted yarn and a sheath core type false twisted composite yarn or the like. Nevertheless, the fluff feeling caused by cotton fibers, from the visual point of view, could not be realized in such a manner heretofore. To attain such an object, a fabric made of a looped yarn produced by an eddy current treatment has been proposed and developed, although it is difficult for this fabric, even when having a fluff feeling of cotton fibers caused by the surface effect of the loops, to be given a special bulkiness caused by the cotton having a super high fiber length, a smooth surface touch, and a stiffness caused by the high yarn density. But when the latent looped yarn of this invention is used in the fabric, then such a fabric having a special feeling of cotton having a super high fiber length, in addition to a smooth surface touch, a fluff feeling, and a stiffness caused by the high yarn density, can be obtained. Such a fabric can be produced in the manner described below. A fabric having a spun like feeling resembling a fabric made of super high length cotton fibers is produced by a method in which the fabric is woven with mixed composite multifilament yarns having a total denier of less than 90d (9.99 tex), wherein the composite yarn consists of a multifilament yarn component of filaments "a" having a shrinkage ratio in hot water of more than 12%, a component filament denier of more than 1.5d (0.17 tex), and a total denier of the multifilament yarn component less than 60d (6.67 tex), and a multifilament yarn components of filaments "b" having a shrinkage ratio in hot water of less than 10%, a component filament denier of less than 1.0d (0.11 tex), and a total denier of the multifilament yarn component less than 60d (6.67 tex), and the composite yarn is further characterized by having more than 300 ends/m of loops in a class A, more than 50 ends/m of loops in a class B, and less than 10 ends/m of loops in a class C, each of classes A, B, and C being defined below, and thereafter a shrinking treatment is applied to the fabric to cause a differential shrinkage between the filaments "a" and filaments "b", which results in a projection of opened and closed loops of the filaments "b" on the surface of the fabric, wherein measurement and counting of the loops for assignment of the loops into the relevant classes A, B and C is carried out by the method previously described. As the mixed composite yarn used in this embodiment, a latent looped yarn of a construction previously described can be used, and its manufacturing method is also the same as that described above. The multifilament yarn material used in this embodiment may be any kind of synthetic material, but is especially a polyester. A multifilament yarn component having a high shrinkage ratio and a multifilament yarn component having a low shrinkage ratio may be arranged in the form of a sheath core type configuration in the latent looped yarn or arranged in a side by side configuration therein. Further, in this embodiment, the latent looped yarn can be used as the warp yarn or as both the warp and the weft yarns. When the latent looped yarn is used only as the warp yarn, the cover factor of the warp yarn in a gray fabric is preferably more than 800, more preferably, more than 1100. When the latent looped yarn is used as both the warp and the weft yarns, the total cover factor, i.e. the sum of the cover factors of the warp yarn and the weft yarn in the gray fabric, is 1500 - 2700, more preferably 1800 - 2500. Desirably, the warp yarn of this embodiment is twisted more than 300 T/m, in order to obtain a handling and external configuration closer to the spun like feeling provided by the fibers having a super high length. The embodiment described above will be now explained in more detail. To develop the fluff feeling of the fibers having a super high length, the use of the latent looped yarn embodying the invention is suitable, and to obtain a smooth surface touch resembling that of fibers having a super high length, it is effective to use a composite multifilament having a total denier of less than 90D (9.99 tex), more preferably less than 70D (7.77 tex), comprising component filaments used as a sheath yarn having a denier of less than 1.0d (0.11 tex), preferably less than 0.7d (0.077 tex). The fibers having a super high length, as used in this embodiment, are, for example, Egyptian cotton or Sea Island cotton, having a comparatively high fiber length, and a spun yarn made of such cotton fibers may have a cotton yarn count of more than 60S (less than 9.84 tex), more preferably more than 80S (less than 7.38 tex), and a thickness of 10 µ - 14 µ. According to investigation by the inventors into a polyester composite yarn having opened loops and closed loops on the surface thereof caused by the eddy current treatment, when the single filament denier was more than 10 µ, i.e., its thickness was more than 1d (0.11 tex), the yarn was stiff and the effect of the fabric obtained by the yarn was not good. On the other hand, when a single filament denier is less than 1d, a fabric having smooth surface touch can be obtained, and especially, when the denier thereof is less than 0.7d (0.077 tex) (less than 8.5 µ), an excellent effect can be obtained. This is considered to be because, when using a cotton fiber, the fluffs thereof are projected alone from the surface of the spun yarn, one by one, and on the other hand, in the polyester composite yarn, the fluffs consist of loops and thus the stiffness thereof is double that of each filament. Next, in order to obtain a fabric made of a spun yarn comprising fibers having a super high length, stiffness, and a high density, the fabric must be woven at least with a high warp yarn density, even though it is difficult to so weave a fabric with a conventional composite looped yarn produced by a conventional eddy current treatment because the loops of the warp yarns hinder the shedding operation. Therefore, in this embodiment, a process is adopted whereby, during the weaving, the loops of the warp yarn are kept small, i.e., in a latent condition, and thereafter, in the dyeing and finishing process after the weaving process, the yarn is shrunk to develop the loops on the surface of the fabric and, simultaneously, to reduce the fabric to one having a high density. Next, an Example of the embodiment described above will be explained. Example 10 In the process represented by Figure 1, a polyester multifilament yarn, 20D (2.22 tex) - 8F, having a shrinkage ratio in hot water of 20% is used as a core yarn and a polyester multifilament yarn, 20D (2.22 tex) - 48F, having a shrinkage ratio in hot water of 8% is used as a sheath yarn, and these yarns are supplied to a texturing zone provided with an eddy current nozzle at an overfeed ratio of the core yarn of +9% and an overfeed ratio of the sheath yarn of +15%, and are treated by a texturizing treatment having an air feed volume of 90 N l/min. Subsequently, the thus treated yarn is wound up on a package while being stretched between the first take up roller and the second take up roller, at an under-feed ratio of -5.4%. The yarn characteristics thus obtained are shown hereunder. Total yarn denier 43 D (4.77 tex) Shrinkage ratio of the yarn 19.2% Number of loops before the heat treatment LOOP A 330 ends/m LOOP B 71 ends/m LOOP C 1 end/m Number of the loops after the heat treatment LOOP A 441 ends/m LOOP B 328 ends/m LOOP C 86 ends/m Thereafter, the thus obtained latent looped yarns were used as the warp and weft yarns to make a plain weave fabric with a warp yarn density of 180 ends/inch (70 ends/cm) and a weft yarn density of 130 ends/inch (51 ends/cm), and then the resulting grey fabric was treated by a relaxing treatment at 98°C and a dyeing treatment at 130°C. Accordingly, a high density fabric having a warp yarn density of 225 ends/inch (88 ends/cm) and a weft yarn density of 156 ends/inch (61 ends/cm), and having fine loops developed on the surface thereof, and further, having a smooth surface touch and bulkiness similar to those obtained by cotton fibers having a super high fiber length, and a stiffness caused by the high density, was obtained.

Claims: A looped composite yarn having opened and closed loops on a surface thereof, which looped composite yarn comprises at least one synthetic multifilament yarn component having a high shrinkage ratio and at least one synthetic multifilament yarn component having a low shrinkage ratio the shrinkage ratio in hot water of the filaments of the synthetic multifilament yarn component having a high shrinkage ratio being more than 10% and the difference in shrinkage ratio in hot water between that of the said filaments of the synthetic multifilament yarn component having a high shrinkage ratio and that of the said filaments of the synthetic multifilament yarn component having a low shrinkage ratio being more than 5%, whereby the said looped composite yarn is such that the total number and size of opened and closed loops thereof can be increased by thermally treating the yarn while free of tension, each said loop being classified as a loop in class A, B or C in terms of its projection height, the number of loops projecting above a given height being measured at a yarn speed of 50m/min and a yarn running tension of 0.1g/d (0.0108 cN/tex) loops in class A being loops which project more than 0.15mm from the yarn surface, loops in class B being loops which project more than 0.35 mm from the yarn surface, and loops in class C being loops which project more than 0.6mm from the yarn surface, the looped composite yarn having on the said surface thereof, before the said thermal treatment, more than 300 ends/m of loops in class A, more than 50 ends/m of loops in class B, and less than 10 ends/m of loops in class C, the number of loops, measured after a thermal treatment with hot water at 98°C for 10 minutes under a tension free condition and with subsequent drying, being such that at least the number of loops in class B is more than 1.5 times that of said looped yarn before heat treatment, and the number of loops in class C is more than 50 ends/m. A looped composite yarn according to claim 1, which has been subjected to thermal treatment with hot water at 98°C for 10 minutes under a tension free condition and subsequently dried. A looped composite yarn according to claim 1 or claim 2, wherein a filament of the multifilament yarn component having a high shrinkage ratio has a denier 0.1 - 15 denier (0.11 - 16.6 dtex) and a filament of the multifilament yarn component having a low shrinkage ratio has a denier of 0.05 - 1.3 denier (0.055 - 1,44 dtex). A looped composite yarn according to any one of claims 1 to 3, which has a shrinkage ratio in hot water of at least 10%. A method for manufacturing a looped composite yarn in which at least first and second synthetic multifilament yarns are simultaneously fed to a texturing zone in which an eddy current flows, thereby producing a composite multifilament yarn having opened and closed loops on a surface thereof, and thereafter said composite multifilament yarn is stretched thereby eliminating or reducing the size of said opened and closed loops, the said first synthetic multifilament yarn having a shrinkage ratio in hot water higher than that of the said second synthetic multifilament yarn. A method according to claim 5, wherein the first synthetic multifilament yarn has a shrinkage ratio in hot water of more than 10% and the difference between the respective shrinkage ratios in hot water of the first and second synthetic multifilament yarns is more than 5%. A method according to claim 5 or claim 6, wherein a filament of the second synthetic multifilament yarn has a denier of 0.05 - 1.3 denier (0.055 - 14.4 dtex). A method according to any one of claims 5 to 7, wherein a component filament of the first synthetic multifilament yarn has a denier of 0.1 - 15 denier (0.11 - 16.6 dtex). A method according to claim 7 or 8, wherein a component filament of the second synthetic multifilament yarn has a denier of 0.05 - 1.3 denier (0.055 - 14.4 dtex) and a component filament of the first synthetic multifilament yarn has a denier of 0.1 - 15 denier (0.11 - 16.6 dtex). A method according to any one of claims 5 to 9, wherein the first and second multifilament yarns are overfed to the texturing zone and are each overfed at a respective overfeed ratio different from the other. A method according to claim 10, wherein the second multifilament yarn of low shrinkage ratio is fed to the texturing zone at an overfeed ratio higher than the overfeed ratio at which the first multifilament yarn of high shrinkage is fed. A method according to claim 11, wherein, in the texturing zone the first and second synthetic multifilament yarns are each treated with compressed air providing the eddy current, wherein the first and second synthetic multifilament yarns are simultaneously fed into the texturing zone at an overfeed ratio λ, for the first multifilament yarn of 2 - 15% and at a overfeed ratio β for the second multifilament yarn of 5 - 30%, and wherein the composite multifilament yarn thus treated is continuously stretched at an underfeed ratio of 0.4 λ - 0.8 λ, and thereafter, is wound up on a yarn package. A high density fabric comprising: (a) warp yarns comprising a mixed composite multifilament yarn having opened loops and closed loops on a surface thereof according to claim 1, wherein the cover factor (CF) of the warp yarns, given by the equation CF = n √d , where n is the yarn density (ends/inch) and d is the yarn denier, or by the equation CF = 7.62 n SI √ tex , where n SI is the yarn density (ends/cm), is more than 1100; and (b) weft yarns. A high density fabric according to claim 13, wherein the said mixed composite multifilament yarn comprises at least first and second synthetic multifilament yarn components, the first synthetic multifilament yarn component having a shrinkage ratio in hot water higher than that of the second multifilament yarn component. A high density fabric according to claim 14, wherein a filament of the second synthetic multifilament yarn component has a denier of from 0.05 to 1.3d (0.055 to 14.4 dtex) and a filament of the first synthetic multifilament yarn component has a denier of from 0.1 to 15d (0.11 to 16.6 dtex). A high density fabric according to claim 15, wherein the first synthetic multifilament yarn component has a shrinkage ratio in hot water of more than 10% and the difference between the respective shrinkage ratios in hot water of the first and second multifilament yarn components is more than 5%. A high density fabric according to any one of claims 13 to 16 which has been subjected to heat treatment and wherein, when the number of loops projecting above a given height is measured at a yarn speed of 50 m/min and a yarn running tension of 0.1 g/d (0.0108 cN/tex), the composite multifilament yarn is found to have a number of loops C projecting more than 0.6 mm from a surface of the said yarn of at least 50 ends/cm. A high density fabric according to any one of claims 13 to 17, having weft yarns of a synthetic multifilament yarn, each component filament of which has a flat cross sectional shape, and having a total cover factor, as defined in claim 13, of warp yarns and weft yarns of from 1800 to 3500, whereby the fabric has a spunlike feeling. A high density fabric according to claim 18, wherein the composite multifilament yarn has a shrinkage ratio in hot water of more than 10%. A high density fabric according to claim 18 or claim 19, wherein the flat ratio, being the ratio of lateral to width dimension, of each component filament of the synthetic multifilament yarn and having the flat cross sectional shape is from 2.0 to 6.0. A high density fabric according to any one of claims 18 to 20, wherein the synthetic multifilament yarn, each component filament of which has a flat cross sectional shape, has a total shrinkage ratio in hot water of from 8 to 27, and wherein from 30 to 70 weight percent of said component filaments have a shrinkage ratio in hot water of from 7 to 30% and from 70 to 30 weight percent of said component filaments have a shrinkage ratio in hot water of from 1 to 15%. A mixed fabric having a high density comprising (a) warp yarns or weft yarns comprising mixed composite multifilament yarns capable of shrinkage, having opened loops and closed loops on a surface thereof and comprising at least one synthetic multifilament yarn; according to claim 1 and (b) weft yarns or warp yarns comprising spun yarns; wherein the total cover factor, as defined in claim 13, of the said warp yarns and weft yarns thereof is from 2000 to 3500. A mixed fabric according to claim 22, wherein the said composite multifilament yarn has a shrinkage ratio in hot water of more than 10%. A mixed fabric according to claim 22 or claim 23, wherein the said mixed composite multifilament yarn comprises at least first and second synthetic multifilament yarns each having a respective different shrinkage ratio in hot water. A mixed fabric according to claim 24, wherein the shrinkage ratio in hot water of the said first synthetic multifilament yarn component is higher than the shrinkage ratio of the said second multifilament yarn component, the shrinkage ratio in hot water of the said first synthetic multifilament yarn component is more than 10% and the difference between the respective shrinkage ratios in hot water of the said first and second multifilament yarn components is more than 5%. A mixed fabric according to claim 24 or claim 25, wherein a component filament of one of the multifilament yarn components has a denier of from 0.1 to 2.5d (0.011 to 0.28 tex) and a component filament of another of the multifilament yarn components has a denier of from 0.3 to 15d (0.033 to 1.67 tex). A mixed fabric according to any one of claims 22 to 26, which has been subjected to heat treatment and wherein when the number of loops projecting above a given height is measured at a yarn speed of 50 m/min and a yarn running tension of 0.1 g/d (0.9 g/tex), the composite multifilament yarn is found to have a number of loops C projecting more than 0.6 mm from a surface of the said yarn of at least 50 ends/cm. A mixed fabric according to any one of claims 22 to 27, wherein said spun yarn has a cotton count of more than 30S (less than 19.68 tex). A method of manufacturing a woven fabric having a spunlike feeling and resembling a fabric made of super high length cotton fibers, in which said fabric is woven with mixed composite multifilament yarns made of synthetic multifilament yarn components and having a total denier of less than 10 tex (90d) and said composite yarn consists of a filament "a" having a shrinkage ratio in hot water of more than 12% and a denier of a component filament thereof is more than 0.17 tex (1.5d) and total denier thereof is less than 6.67 tex (60d) and a filament "b" having a shrinkage ratio in hot water of less than 10% and a denier of a component filament thereof is less than 0.11 tex (1.0d) and total denier thereof is less than 6.67 tex (60d), and said composite yarn is further characterized by having, prior to shrinkage, more than 300 ends/m of the loop A, more than 50 ends/m of the loop B, and less than 10 ends/m of the loop C, each of said loop A, loop B, and loop C being defined hereunder, and after weaving a shrinking treatment is applied to said fabric to cause a differential shrinkage between said filament "a" and filament "b" which results in projecting opened loops and closed loops of said filament "b" on the surface of said fabric, wherein each of said loop A, loop B and loop C is defined in such a manner than when each loop is measured under a condition of a yarn speed of 50 m/min and a yarn running tension of 0.1 g/d (0.0108 cN/tex), by using a photo-electric type fluff measuring device by which the number of loops of a yarn running therethrough is counted, a loop projecting more than 0.15 mm from a yarn surface is defined as a loop A, a loop projecting more than 0.35 mm from the yarn surface is defined as a loop B, and a loop projecting more than 0.6 mm from a yarn surface is defined as a loop C.

Inventors: MASUZAKI SATORU, MIURA TOSHIAKI, NABESHIMA KEITAROU, SHIOJIMA MINORU, MASUZAKI, SATORU, MIURA, TOSHIAKI, NABESHIMA, KEITAROU, SHIOJIMA, MINORU
Applicants: TORAY INDUSTRIES, TORAY TEXTILE INC, TORAY INDUSTRIES, INC., TORAY TEXTILE, INC.
Application year: 1988
Main classification: D02G1
IPC codes: D02G1, D03D15