Organopolysiloxane elastomers having improved electrical properties and insulators coated therewith

Abstract: Organopolysiloxanes having improved electrical properties, which comprises mixing an organopolysiloxane having reactive groups with an amine-containing organosilicon compound, which is capable of crosslinking with the organo­ polysiloxane and a treated aluminum trihydrate and thereafter exposing the resultant composition to atmospheric moisture. The resultant composition may be dispersed in an organic solvent and applied to electrical insulators.

Description: The present invention relates to organopolysiloxane elastomers having improved electrical properties and more particularly to organopolysiloxane compositions which may be applied to electrical insulators to provide improved arc resistance. Background of the Invention Various compositions have been described heretofore having improved electrical properties. For example, U. S. Patent No. 3,965,065 to Elliott describes a method for preparing a composition having improved electrical properties which comprises heating a mixture containing aluminum hydrate and an organopolysiloxane which is convertible to an elastomeric solid to a temperature above 100°C for at least thirty (30) minutes. Niemi describes a method for preparing improved high voltage insulators in U. S. Patent No. 4,476,155 in which a composition containing the product obtained by mixing a hydroxyl endblocked polydimethylsiloxane with aluminum hydroxide and a ketoxime functional silane, is applied to the outer surface of an insulator. Penneck discloses high voltage insulating materials in U. S. Patent No. 4,001,128 in which the insulating materials contain organic synthetic polymeric materials and an anti-tracking filler system containing at least 20 percent by weight of alumina trihydrate and at least one percent by weight based on the weight of the polymer and filler system of a chemically treated silica filler. Penneck discloses tracking resistant insulating materials in U. S. Patent No. 4,189,392, in which the insulating materials contain a polymeric material and an anti-tracking filler and a fluorine substituted compound which is a hydrophobic, non-ionic compound having a fluorine-substituted aliphatic carbon chain linked to a group having an affinity for the polymeric material and/or the anti-tracking filler. It is an object of the present invention to provide an organopolysiloxane elastomer having improved adhesion. Another object of the present invention is to provide an organopolysiloxane having an improved contact angle. Still another object of the present invention is to provide an organopolysiloxane having an accelerated cure rate. Still another object of the present invention is to provide an organopolysiloxane elastomer having improved arc resistance. Still another object of the present invention is to provide an organopolysiloxane elastomer which exhibits improved resistance to leakage of electrical current. Still another object of the present invention is to provide a composition which may be applied to the outer surface of insulators to reduce electrical leakage. A further object of the present invention is to provide coated insulators having a longer useful life. A still further object of the present invention is to provide coated insulators which are resistant to arcing. Summary of the Invention The foregoing objects and others which are apparent from the following description are accomplished in accordance with this invention, generally speaking, by providing a composition comprising an organopolysiloxane containing reactive groups, an amine crosslinking agent which is capable of crosslinking with the organopolysiloxane and aluminum trihydrate, which has been treated to impart hydrophobic properties thereto. The resultant composition may be applied to the outer surface of electrical insulators and crosslinked in the presence of atmospheric moisture. Description of the Invention The organopolysiloxanes employed herein are organopolysiloxanes having terminal hydroxyl groups. These organopolysiloxanes are well known and have been employed heretofore in room temperature vulcanizable (RTV) compositions. The preferred diorganopolysiloxanes, which have terminal hydroxyl groups, may be represented by the formula where each R is a monovalent hydrocarbon radical or a substituted monovalent hydrocarbon radical, x has an average value of from 0.99 to 1.01, y has an average value of from 1.99 to 2.01, x + y is equal to 3, n is a number of at least 3 and preferably at least 50. The hydroxyl groups linked to the silicon atoms of the organopolysiloxane can be replaced in part or entirely by other reactive groups such as hydrogen atoms, halogen atoms, alkoxy groups, aryloxy radicals and radicals of the formula R'NH-, where R' is a cycloalkyl radical of from 5 to 12 carbon atoms. The siloxane polymers are essentially linear, hence they are predominately, i.e., at least 90 mole percent are R₂SiO units. However, siloxane units, other than the disiloxane (R₂SiO) units may be present in an amount up to about 5 mol percent and more preferably below about 2 mol percent. Generally, siloxane units such as RSiO 3/2 units, R₃SiO ½ units and/or SiO 4/2 units, where R is the same as above can be present mostly as impurities. In the above formula, each R can be a monovalent hydrocarbon radical of up to 18 carbon atoms. Examples of radicals represented by R include alkyl radicals such as the methyl, ethyl, n-propyl, isopropyl, dodecyl and octadecyl radicals; alkenyl radicals such as vinyl, allyl, hexenyl and octadecenyl radicals; cycloalkyl radicals such as the cyclobutyl, cyclopentyl, cyclohexyl and cyclodecyl radicals; cycloalkenyl radicals such as the cyclobutenyl, cyclopentenyl, cyclohexenyl and cyclodecenyl radicals; aryl radicals such as phenyl, xenyl, naphthyl and the phenanthryl radicals; aralkyl radicals such as the benzyl, B-phenylethyl and B-phenylpropyl radicals and alkaryl radicals such as the tolyl, xylyl and ethylphenyl radicals. Substituted hydrocarbon radicals represented by R include halogen hydrocarbon radicals such as o-, m- and p-chlorophenyl and bromophenyl radicals, α,α,α-trifluorotolyl, 3,3,3-trifluoropropyl, chloro-, fluoro- and bromo-derivatives of the various hydrocarbon radicals set forth above as well as cyanoalkyl radicals such as B-cyanoethyl, cyanopropyl, cyano-n-butyl, cyano-n-propyl and omega-cyanooctadecyl radicals. Preferably, the radicals represented by R have less than 8 carbon atoms and more preferably R represents methyl, ethyl, propyl, vinyl, phenyl, and 3,3,3-trifluoropropyl radicals. Of course, as is usually the case, the R radicals on a single silicon atom can be the same or different and various units in the siloxane chain can be the same or different homopolymers, e.g., dimethylsiloxane units, copolymers of, for example, dimethylsiloxane and methylvinylsiloxane units, or phenylmethylsiloxane units and mixtures thereof. The siloxane polymers employed can vary from relatively mobile fluids (viscosity 50 mPa.s at 25°C) to gum-like materials having viscosities in the range of 10⁶ mPa.s at 25°C. This can be seen from the value of n in the general formula above, where n is at least 3 and is preferably at least 50, but can have a value as high as 2,000,000. The preferred siloxane polymers are those having viscosities in the range of from 200 to 200,000 mPa.s at 25°C. These siloxanes are known and have been described in, for example, U. S. Patents Nos. 3,294,732; 3,127,363; 3,105,061 and others. The room temperature vulcanizable organopolysiloxane compositions are prepared by mixing under anhydrous conditions organopolysiloxanes containing reactive groups, preferably hydroxyl groups, with an amine-substituted silicon compound capable of reacting with the organopolysiloxane reactive groups and having an average of at least two -NR 1 / 2 groups bonded to a silicon atom per molecule, where R¹ is a monovalent hydrocarbon radical which preferably has up to 18 carbon atoms or hydrogen, and more preferably at least one R¹ is hydrogen. Amine-substituted silicon compounds which may be employed as crosslinking agents are aminosilanes of the formula R² 4-z Si(NR 1 / 2) z where R¹ is the same as above and R² is a monovalent radical, preferably a monovalent hydrocarbon radical, having from 1 to 18 carbon atoms, and z has an average value of at least 2 and more preferably from 2 to 4 per molecule and partial hydrolyzates thereof. The aminosilanes which are employed as crosslinking agents preferably may contain an average of 3 or 4 amino substituents per silicon atom and 0 or 1 alkyl, or aryl, or alkaryl or aralkyl radicals per silicon atom. In general, the trifunctional aminosilanes may be represented by the formula R²Si(NR 1 / 2)₃ and the tetra-functional silanes by the formula Si(NR 1 / 2)₄, where R¹ and R² are the same as above. Specific examples of monovalent hydrocarbon radicals represented by R¹ are alkyl radicals, such as the methyl, ethyl, propyl or octadecyl radicals, aryl radicals, such as the phenyl or anthracyl or a cycloalkyl radical such as the cyclohexyl radical or an aralkyl radical such as the benzyl or phenylethyl radical or an alkaryl radical such as the tolyl or xylyl radicals. Examples of monovalent hydrocarbon radicals represented by R² are an alkyl, aryl, cycloalkyl, alkaryl or aralkyl radicals. The specific examples recited for the R¹ radicals also apply to the R² radicals, when R¹ is a monovalent hydrocarbon radical. Only one type of aminosilane need be employed; however, mixtures of aminosilanes may also be employed as crosslinking agents. Other amino-substituted silicon compounds which may be employed as cross-linking agents are aminosiloxanes having the general formulas and aminosilylalkanes having the general formula where R, R¹ and R² are the same as above, R³ is a saturated or unsaturated divalent hydrocarbon radical having up to 10 carbon atoms, m is a number of from 0 to 50, v is a number of from 0 to 3, w is a number of from 0 to 3 and the sum of v + w is equal to at least 3. Divalent saturated hydrocarbon radicals represented by R³ above are methylene, ethylene, propylene, butylene, hexylene, octylene and decylene radicals. Divalent unsaturated hydrocarbon radicals represented by R³ are ethenylene, propenylene, butenylene, hexenylene, octenylene and decenylene radicals. An example of a divalent cyclic hydrocarbon radical is the phenylene radical. The aminosilanes and aminosiloxanes and aminosilylalkanes employed as crosslinking agents are described, for example, in U. S. Patents Nos. 3,408,325 to Hittmair et al; 3,464,951 to Hittmair et al; 3,452,964 to Creamer; 3,644,434 to Hittmair et al; and 3,816,164 to Pepe et al, all of which are incorporated herein by reference. Other amine-substituted silicon compounds which may be employed as cross-linking agents in the compositions of this invention may be represented by the formula where R² and z are the same as above, R⁴ which may be the same or different represent monovalent hydrocarbon radicals having from 1 to 18 carbon atoms, preferably from 1 to 10 carbon atoms, and more preferably from 1 to 4 carbon atoms. Preferably, R⁴ is an alkyl radical, such as the methyl, ethyl, propyl, isopropyl, butyl, octyl, decyl and octadecyl radicals. Other radicals represented by R⁴ are aryl radicals such as the phenyl radical, alkaryl radicals such as the tolyl and ethylphenyl radicals and aralkyl radicals such as the benzyl and the B-phenylethyl radicals. Examples of crosslinking agents represented by the above formula are silanes of the formula CH₃Si[NHCH(CH₃)C₂H₅]₃ and silazanes of the general formula where R¹, R² are the same as above and g is 0 or a number having a value of at least 1 and preferably less than about 100. Other silicon compounds which can be used as crosslinking agents are aminosiloxanes of the formula R 2 / 3SiO(SiR₂O) m Si[NHCH(R⁴)₂]₃ where R, R², R⁴ and m are the same as above. These crosslinking agents may be prepared, for example, by reacting halosilanes with a sec-butylamine. These secondary butylamine crosslinking agents and their method of preparation are described in U. S. Patent No. 3,923,736 to Nitzsche et al, which is incorporated herein by reference. The silicon valences of the amine substituted silicon compounds which are not satisfied by the -NCH(R⁴)₂ groups are preferably satisfied by monovalent hydrocarbon radicals, cyanoalkyl radicals, Si-bonded hydroxyl groups and/or siloxane oxygen atoms. The amine-substituted organosilicon compounds are employed in amounts which will provide at least one gram equivalent silicon atom of the amih, substituted organosilicon compound per gram equivalent of reactive groups on the organopolysiloxane. Generally from about 0.2 to 40 parts by weight of amine substituted organosilicon compound is added for each 100 parts by weight of the organopolysiloxane containing reactive groups. In addition to the organopolysiloxane polymer and amine-substituted organosilicon compound, the composition also contains aluminum trihydrate, which has been treated to impart hydrophobic properties thereto. Preferably, the aluminum trihydrate has a specific surface area in the range of from about 1 to 20 m²/g and more preferably from about 2 to 15 m²/g. The average particle size ranges from about 2 to 10 µm and more preferably from about 2 to 5 µm. Preferably, about 97 percent of the aluminum trihydrate has a particle size of less than about 10 µm. Generally, the aluminum trihydrate is present in an amount of from about 40 to 75 percent by weight and more preferably from about 50 to 70 percent by weight based on the weight of the organopolysiloxane polymer and the aluminum trihydrate. Organosilicon compounds which may be employed to treat the aluminum trihydrate are those having the general formula (R₃Si) a Z or R a' SiZ' 4-a' wherein R which may be the same or different represents monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals having up to 18 carbon atoms, Z and Z' represent halogen, hydrogen or a radical of the formula -OH, -OR⁴, NX₂, -NR⁴X, -ONR⁴, or -OOCR⁴ and when a is 2, then Z may also represent -O- or -NX-; R⁴ is a monovalent hydrocarbon radical having up to 18 carbon atoms and more preferably R⁴ is an alkyl radical having from 1 to 4 carbon atoms; X is hydrogen or has the same meaning as R⁴, a is 1 or 2 and a' is 1, 2 or 3. Other organosilicon compounds which may be employed are octamethycyclotetrasiloxane and/or dimethylpolysiloxanes having from 2 to 12 siloxane units per molecule in which the dimethylpolysiloxanes have an Si-bonded hydroxyl group in each of their terminal units. The monovalent and halogenated monovalent hydrocarbon radicals represented by R in the organosilicon compounds may be the same as the R radicals linked to the diorganopolysiloxanes. Suitable monovalent hydrocarbon radicals having from 1 to 18 carbon atoms are alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals, alkaryl radicals, aralkyl radicals and halogenated derivatives thereof. Examples of halogen atoms represented by Z and Z' are chlorine, bromine and iodine, with chlorine being the preferred example, since it is readily available. Preferred examples of hydrocarbon radicals represented by R⁴ are the methyl, ethyl, propyl and butyl radicals. Additional examples of hydrocarbon radicals represented by R⁴ are described in the following examples of organosilicon compounds which impart hydrophobic properties to aluminum trihydrate. Suitable examples of organosilicon compounds which may be employed to impart hydrophobic properties to aluminum trihydrate are hexamethyldisilazane, vinyltriethoxysilane, vinyltrimethoxysilane, trimethylethoxysilane, trimethylaminosilane, trimethylchlorosilane, dimethyldiethoxysilane, trimethylsilylisopropylamine, trimethylsilylethylamine, phenyldimethylsilylpropylamine, vinyldimethylsilylbutylamine, diethylaminoxytrimethylsilane, diethylaminoxyphenyldimethylsilane, hexamethyldisiloxane, 1,3-divinyltetramethyldisiloxane, 1,3-diphenyltetramethyldisilazane, dimethyldichlorosilane, dimethyldimethoxysilane, diphenyldiethoxysilane, vinylmethyldimethoxysilane, and methyltriethoxysilane. It is preferred that the organosilicon compound used to treat the aluminum trihydrate be a vinyltrialkoxysilane having 1 to 2 carbon atoms per alkoxy group because they do not release any by-products which may have a detrimental effect on the dispersions of this invention. Mixtures of various organosilicon compounds may also be employed in the treatment of aluminum trihydrate to impart hydrophobic properties thereto. The amount of organosilicon compounds used in the surface treatment of the aluminum trihydrate is from about 0.1 to 10 percent by weight based on the weight of the aluminum trihydrate. The aluminum trihydrate can be reacted with the organosilicon compounds by any conventional technique known in the art for reacting inorganic substances which are solid at room temperature. Also, it is possible to react the aluminum trihydrate with hydrophobic imparting organosilicon compounds which evaporate at room temperature at 760mm Hg (abs.), in a sealed container, such as, for example, a polyethylene bag, for a period of time under ambient conditions. In addition, the aluminum trihydrate can be mixed in a mechanical mixing device with a liquid hydrophobic imparting organosilicon compound or in a fluidized bed, and if desired, in the presence of a stream of inert gas. The reaction of the aluminum trihydrate with the organosilicon compound can be accelerated by using catalysts such as ammonia or amines at the rate of from about 0.3 to 3 percent by weight based on the weight of the aluminum trihydrate. The compositions of this invention should be prepared by mixing the various ingredients in an atmosphere which is substantially free of water. In addition to the organopolysiloxane polymer, the amine-substituted organosilicon compound and the treated aluminum trihydrate, the compositions of this invention may also contain additives such as compression-set additives, pigments, soluble dyes, aromatics (essential oils), oxidation inhibitors, heat stabilizers, flame retardants and light stabilizers, plasticizers and softeners such as trimethylsiloxy endblocked dimethylpolysiloxane fluids, reinforcing fillers and non-reinforcing fillers. Examples of reinforcing fillers and non-reinforcing fillers are quartz, diatomaceous earth, calcium silicate, zirconium silicate, so-called "molecular sieves", metal oxide powders, such as titania, alumina, iron oxide, zinc oxide and calcium carbonate. Fibrous fillers, for example, asbestos, glass fibers or organic fibers can also be used. The fillers can advantageously be treated by known methods to include organosiloxy or alkoxy groups on their surface. Mixtures of different fillers may be added to the compositions of this invention. The amount of filler may vary over a broad range, preferably from 0 to 90 percent by weight, based on the total weight of the organopolysiloxane and filler; however, the amount of filler should not be so great as to degrade the arc resistance or current leakage supression of the elastomeric coating. Other additives which may be employed in the compositions of this invention are condensation catalysts such as those disclosed in, for example, U. S. Patents Nos. 2,843,555; 2,127,363; and 3,082,527. Examples of suitable condensation catalysts are metallic salts and organometallic salts of carboxylic acids, such as lead octoate, dibutyltin dilaurate and dibutyltin salts of aliphatic carboxylic acids which are branched in the alpha-position to the carboxyl groups and have from 9 to 11 carbon atoms, amines, such as 3-ethoxypropylamine-1, and silanes which have at least one amine group bonded via carbon to silicon and at least one monovalent hydrocarbon radical or a hydrocarbon radical substituted by an amine group and/or alkoxy group, and bonded via oxygen to silicon in each molecule. Silanes of the latter, which not only act as condensation catalysts but as adhesion promoters for improving the adhesion of the elastomers to the substrates, are N-beta-(aminoethyl)-gamma-aminopropyltrimethoxysilane or a compound of the formula CH₃Si[O(CH₂)₂NH₂]₂(CH₂)₃O(CH₂)₂NH₂ . If condensation catalysts are used, they are generally employed in amounts of from 0.01 to 5 percent by weight and more preferably from about 0.05 to 1 percent by weight, based on the total weight of the composition. When adhesion promoters are employed in the compositions, the amount may range from about 0.2 to about 2 percent by weight, based on the weight of the organopolysiloxane and aluminum trihydrate. The compositions of this invention are prepared by mixing the treated aluminum trihydrate with the organopolysiloxane containing reactive groups. The amine-substituted organosilicon crosslinking agent and catalyst, if used, is then added to the mixture under anhydrous conditions. The compositions of this invention may be stored for long periods of time under anhydrous conditions without deletrious effects and then crosslinked by merely exposing them to atmospheric moisture at room temperature. The compositions of the present invention are especially useful for coating high voltage apparatus where it is essential that a component be insulated from the surrounding elements. High voltage insulators, preferably ceramic or plastic insulators, may be coated with the compositions of the invention by conventional methods, such as spraying, dipping or brushing. Generally, the composition are dispersed in a non-reactive solvent for ease of application. Examples of non-reactive solvents which may be employed are hydrogen solvents such as toluene, xylene, naphtha and chlorinated hydrocarbon solvents such as chlorothene. Preferred solvents are chlorinated hydrocarbon solvents, especially chlorothene and V.M.&P naphtha. By dispersing the position in a solvent, the viscosity can be reduced so that it can be applied to the insulator surface by spraying, dipping or brushing. The amount of non-reactive solvent is not critical and may range up to about 80 percent by weight, based on the weight of the composition. The coatings of this invention may be crosslinked by exposing the coating to atmospheric moisture. Crosslinking may be accelerated by applying heat or by adding water in addition to that contained in the atmosphere or by the addition of carbon dioxide. The coating preferably ranges from about 0.2 to about 2 mm in thickness. A coating thickness above about 2 mm may be applied to the insulators, if desired. It has been found that a thicker coating may be more resistant to arcing than thinner coatings, such as those having a thickness of less than about 0.2 mm. An advantage of the present invention is that a coated insulator can be manufactured in place. Insulators such as ceramic suspension insulators, strings, ceramic post insulators, composite suspension insulators, filled-resin post insulators and cable terminations can be coated in the field by applying the compositions of this invention on the surfaces of the insulators and thereafter exposing the coated surface to atmospheric moisture to crosslink the same. The resultant coating forms a hydrophobic arc-resistant surface. Also, insulators may be sprayed on line and the line re-energerized while the coating dries and cures in the presence of atmospheric moisture. These compositions are useful in a number of applications where it is necessary to resist erosion and/or control current leakage, and are especially useful in electrical components exposed to voltages above 1 kV. The compositions may be used in electrical power transmission and distribution systems, as for example, insulator materials for high voltage components, as insulators for cable terminations, fuse covers, transformer covered and as insulation coatings. Surprisingly, it was found that the use of aluminum trihydrate treated with a hydrophobic agent provided an elastomer having an improved contact angle. It has been shown heretofore that there is a close correlation between the hydrophobic nature of the surface as measured by contact angle with water and the electrical performance of the elastomer. In the following examples all parts are by weight unless otherwise specified. Example 1 To a mixer containing 100 parts of a hydroxyl-terminated dimethylpolysiloxane having a viscosity of 20,000 mPa.s at 25°C are added 150 parts of treated aluminum trihydrate (available from Solem Industries, Inc. as SP-632) and mixed for about 20 minutes under a nitrogen atmosphere. Then about 82 parts of chlorothene are added to the mixture and mixed for about 10 minutes to form a dispersion. About 10 parts of methyltris-(cyclohexylamino)silane and 0.8 parts of gamma-aminopropyltrimethoxysilane are then added to the dispersion and mixed for about 20 minutes under a nitrogen atmosphere. The resultant dispersion is molded to form test specimens and exposed to atmospheric moisture for 7 days. The skin-over time is 6 minutes and the tack-free time is 11 minutes. The physical properties are determined after curing for 7 days in atmospheric moisture. Physical Properties Durometer, Shore A 55 Tensile strength 2,069 MPa (300 psi) Elongation percent 125 Tear 5.26 N/mm ( 30 ppi) The arc resistance of a cured sample is determined in accordance with ASTM D-495-73. Arc resistance to failure > 420 seconds Contact angle measurement. The contact angle is measured by the sessile drop technique in which drops of water about 2 mm in diameter are applied from a syringe to the surface of the sample after it has cured for 7 days. The contact angle is measured about 30 seconds after applying the water using a telescope fitted with a goniometer eyepiece. Contact angle of the cured sample is 103°. Comparison Example The procedure of Example 1 is repeated, except that 150 parts of an untreated aluminum trihydrate (available from Solem Industries, Inc. as SB-632) is substituted for the treated aluminum trihydrate. The resultant mixture is formed into test specimens and exposed to atmospheric moisture. The skin-over time is 11 minutes and the tack-free time is 18 minutes. After curing for 7 days in atmospheric moisture, the physical properties are determined. Physical Properties Durometer, Shore A 50 Tensile strength 1,655 MPa (240 psi) Elongation, percent 150 Tear 5.26 N/mm ( 30 ppi) The contact angle, which is measured in accordance with the procedure described in Example 1, is 90°. Example 2 The procedure of Example 1 is repeated, except that 67 parts of treated aluminum trihydrate is substituted for 150 parts of treated aluminum trihydrate. The resultant composition exhibited good arc resistance. Example 3 The procedure of Example 1 is repeated, except that 300 parts of treated aluminum trihydrate is substituted for 150 parts of treated aluminum trihydrate. The arc resistance of the resultant composition before failure is greater than 420 seconds. Example 4 The solvent dispersion prepared in accordance with the procedure of Example 1 is applied to the surface of a ceramic insulator as a uniform coating about 1 mm in thickness and cured by exposure to atmospheric moisture. The resultant coating provides a hydrophobic and arc resistant surface which shows excellent adhesion to the insulator surface. Example 5 The procedure of Example 1 is repeated, except that 10 parts of each of the following crosslinking agents are substituted for 10 parts of methyltris(cyclohexylamino)silane in the above composition: Methyltris(ethylamino)silane, methyltris(phenylamino)silane, methyltris(n-heptylamino)silane, phenyltris(3,5,5-trimethylcyclohexylamino)silane, methyltris(sec-butylamino)silane, tetrakis(n-butylamino)silane, phenyltris(dimethylamino)silane, hexyltris(n-butylamino)silane, ethyltris(methylhexylamino)silane, vinyltris(phenylamino)silane and a mixture containing 30 percent by weight dimethylbis(cyclohexylamino)silane and 70 percent by weight of vinyltris(n-propylamino)silane, based on the weight of the mixture of crosslinking agents. The resultant compositions cured at room temperature to form elastomers having excellent arc resistant properties.

Claims: A room temperature vulcanizable composition which is stable in the absence of moisture, but when exposed to atmospheric moisture crosslinks to form an elastomer having improved electrical properties obtainable by a process comprising the steps of 1) treating an aluminum trihydrate with 0.1 to 10 per cent by weight based on the weight of aluminium trihydrate of an organosilicon compound selected from the group consisting of a) organosilicon compounds having the general formula (R₃Si) a Z or R a' SiZ' 4-a' wherein R which may be the same or different represents monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals having up to 18 carbon atoms, Z and Z' represent halogen, hydrogen or a radical of the formula -OH, -OR⁴, NX₂, -NR⁴X, -ONR⁴ or -OOCR⁴ and when a is 2, then Z may also represent -O- or -NX-; R⁴ is a monovalent hydrocarbon radical having up to 18 carbon atoms; X is hydrogen or has the same meaning as R⁴, a is 1 or 2 and a' is 1, 2 or 3, b) octamethylcyclotetrasiloxane and c) dimethylpolysiloxanes having from 2 to 12 siloxane units per molecule in which the dimethylpolysiloxanes have a Si-bonded hydroxyl group in each of their terminal units, 2) mixing 60 to 25 per cent by weight of an organopolysiloxane containing terminal reactive groups selected from the group consisting of hydroxyl groups, hydrogen atoms, halogen atoms, alkoxy groups, acryloxy radicals and radicals of the formula R'NH-, where R' is a cycloalkyl radical of from 5 to 12 carbon atoms with 40 to 75 percent by weight of the treated aluminum trihydrate based on the weight of the organopolysiloxane and the aluminum trihydrate and 3) adding to the mixture obtained in step 2 an organosilicon crosslinking agent capable of reacting with the organopolysiloxane reactive groups and having an average of at least two -NR 1 / 2 groups per molecule linked to silicon, where R¹ is selected from the group consisting of a monovalent hydrocarbon radical having up to 18 carbon atoms and hydrogen. A method for coating an electrical insulator having improved electrical properties, which comprises coating an insulator with a composition as claimed in claim 1 dispersed in a non-reactive solvent and thereafter exposing the coated insulator to atmospheric moisture. The composition of claim 1 or the method of claim 2, wherein the organopolysiloxane containing reactive groups is a hydroxyl-terminated organopolysiloxane. The composition of claim 1 or the method of claim 2, wherein the organosilicon crosslinking agent is selected from the group consisting of an aminosilane of the formula where R¹ is selected from the group consisting of a monovalent hydrocarbon radical having from 1 to 18 carbon atoms and hydrogen, R² is a monovalent hydrocarbon radical having from 1 to 18 carbon atoms and z has an average value of from 2 to 4 and partial hydrolyzates thereof. The composition of claim 1 or the method of claim 2, wherein the organosilicon crosslinking agent is present in an amount of at least one gram equivalent of silicon atom of the amine substituted organosilicon compound per gram equivalent of reactive groups on the organopolysiloxane. The composition or method of claim 4, wherein the aminosilane is methyltris-(cyclohexylamino)silane. The composition of claim 1 or the method of claim 2, wherein the treated aluminum trihydrate has an average particle size of from 2 to 10 µm. The composition of claim 1 or the method of claim 2, wherein the composition is dispersed in a non-reactive organic solvent, preferably a chlorinated hydrocarbon solvent. The composition of claim 1 or the method of claim 2, wherein the composition contains an adhesion promoter. The coated insulator obtainable from the method of any of the claims 2 to 9.

Inventors: ADKINS JAMES R, ADKINS, JAMES R.
Applicants: WACKER CHEMIE GMBH, WACKER-CHEMIE GMBH
Application year: 1988
Main classification: C08K9
IPC codes: C08K9, C09D5, C08L83, H01B3, C08K13, C09D183, C08K5