PROCESS FOR THE ALKYLATION OF PHENOLS

Abstract: A process for the alkylation of phenols comprises reacting a phenol with a vinyl-aromatic hydrocarbon in the presence of an acidic catalyst and of a solvent.

Description: The present invention relates to a process for the aralkylation of phenols. More particularly, this invention relates to a process for the aralkylation of phenols with a high yield and selectivity to a mono-aralkylated product. The alkylation of phenols with olefins in the presence of acidic catalysts is a per se known process, although not widely used on a commercial scale owing to its low reaction yields. For example, U.S. patent nos. US-A-2,832,808 and 2,722,556 disclose the alkylation of phenols with olefins in the presence of such acidic catalysts as sulphuric acid or phosphoric acid. However, according to these processes, very low yields of mono-alkylated product, even lower than 50%, or selectivities to di-alkylated products higher than 90% are obtained. US-A-2,714,120 discloses the aralkylation of phenolic compounds by reaction with a vinyl aromatic hydrocarbon in the presence of a small amount of a hydrocarbon sulfonic acid or of aqueous sulphuric acid of a concentration from 25 to 50% H₂SO₄ by weight as condensation catalyst. Again, yield of monoalkylated product and selectivity are low, the reaction product consisting generally of a mixture of individual phenols aralkylated to various degrees. In Japanese patent application nos. JP-A-58/140,035 and 59/112,935, the above mentioned drawback purports to be partially overcome; in fact, these Japanese patent applications disclose the preparation of mono-alkyl-substituted hydroquinone by reaction of hydroquinone with vinyl-aromatic hydrocarbons, to obtain reaction yields of the order of 90-93%. However, these processes are not free from drawbacks, in that the alkylation, in order to achieve such highly satisfactory outcome, must be carried out either by using the same reaction product as the solvent, or by causing the reaction to take place in the presence of a poly-substituted hydroquinone. U.S. patent no. US-A-4,661,645 discloses the synthesis of (1-phenyl-ethyl)-hydroquinone from styrene and hydroquinone in the presence of a Lewis acid and in homogeneous phase, with an alkyl ether being used as the homogenising solvent. In this case, too, the reaction product contains large amounts of di(phenyl-ethyl)hydroquinone, which may be higher than 30% by weight relative to the mixture of mono- and di-substituted products. It has now been discovered (in accordance with the present invention) that the drawbacks of the prior art can be overcome by a process for the aralkylation of phenols wherein the reaction takes place in heterogeneous phase. The present invention provides a process for the aralkylation of phenols, comprising reacting a phenol with a vinyl-aromatic hydrocarbon in the presence of an organic solvent and of a catalyst comprising or consisting essentially of an inorganic acid diluted in water. Examples of phenols which may be used in the process of the present invention are hydroquinone, resorcinol, pyrocatechol, pyrogallol, benzophenol, cresols, p-octyl-phenol, di-hydroxy-diphenyl, alpha-naphthol and beta-naphthol. A particularly preferred reactant is hydroquinone. The vinyl-aromatic hydrocarbon is preferably selected from those of the formula: wherein: Ar represents an aryl group containing from 6 to 18 carbon atoms, and R₁,R₂ and R₃, which may be the same as or different from one another, are selected from hydrogen and alkyl radicals having from 1 to 10 carbon atoms. Examples of reactants of formula (I) are styrene, alpha-methyl-styrene, alpha-ethyl-styrene, p-methyl-styrene, p-isopropyl-styrene, p-methyl-alpha-methyl-styrene, beta-methyl-styrene and vinyl-naphthalene. A particularly preferred reactant is styrene. According to a preferred form of practical embodiment of the present invention, the phenol is employed in a slight molar excess with respect to the aromatic hydrocarbon. Molar ratios of phenol/vinyl-aromatic hydrocarbon within the range of from 1.5 to 1, more preferably within the range of from 1.3 to 1, are those preferably used to the greatest advantage. The aralkylation reaction is suitably carried out in a solvent having a boiling temperature compatible with the reaction temperature and a good solubility for both the reactants and the end products. Suitable solvents are the aromatic hydrocarbons, such as toluene, xylene or a mixture of xylenes. The solvent may be used in any weight ratio relative to the phenol; however, weight ratios of solvent/phenol within the range of from 0.5 to 5, more preferably within the range of from 1 to 2, are preferred. Any inorganic acid can be used as the catalyst of the aralkylation process according to the present invention, although ortho-phosphoric acid, pyro-phosphoric acid, and sulphuric acid, diluted in water at 60-90%, more preferably at 70-80% by weight of the acid, are preferred. The catalyst is preferably used in molar ratios relative to the phenol that are within the range of from 0.5 to 6, more preferably from 1 to 3. The aralkylation reaction is suitably carried out under room pressure and preferably at a temperature within the range of from 90° to 120°C, more preferably from 110° to 115°C. At the end of the aralkylation reaction the organic phase constituted by the solvent and by the raw reaction product is decanted off from the catalytic system, and the solvent is then evaporated off. According to the process of the present invention, a yield of mono-aralkylated product higher than 95% and a selectivity with respect to di-aralkylated product lower than 5% may be obtained, with a purity referred to mono-and di-aralkylated products higher than 99.9%. In a particuarly preferred embodiment of the invention, the phenol is hydroquinone and the vinyl-aromatic hydrocarbon is styrene. The reaction product directly obtained by means of the process of the invention may be used for the production of polymers, in particular of thermotropic liquid-crystalline polyesters. In the aralkylation of hydroquinone, the process according to the present invention is particularly interesting in that it makes it possible for the raw reaction product to be used for producing polymers, in particular for producing thermotropic liquid-crystalline aromatic polyesters, without further purification which would have a considerable effect on both the yield and the costs. In fact, mono-aralkylated hydroquinone is a glass-like, non-crystallizable solid which can only be purified by distillation, during which the product is subject to thermal breakdown due to the required operating conditions, e.g. at temperatures higher than 180°C and operating pressures lower than 1 mbar. The invention will be further described with reference to the following illustrative Examples. Example 1 To a glass reactor of 250 ml capacity fitted with a stirrer, thermometer, reflux condenser, dripping funnel, and external heating bath, 26.4 g (0.24 mol) of hydroquinone, 50 ml of xylene, and 110 g of H₃PO₄ as an aqueous solution at 75% by weight, were charged. The reaction mixture was heated to 113°C and styrene was added in an amount of 20.8 g (0.2 mol). After a 3-hour stirring at 115°-116°C, the two phases were allowed to separate; the solution of H₃PO₄ was removed; and the xylenic solution was washed with NaHCO₃, using an aqueous solution at 5% by weight, and water. After evaporating xylene, 41.4 g of a uniform glass-like product was obtained, with a gas-chromatographic titer of 96% of (1-phenyl-ethyl)-hydroquinone and 3.9% of di(phenyl-ethyl)hydroquinone, equivalent to a molar yield of (1-phenylethyl)hydroquinone/styrene of 95.9%. Examples 2-8 The process was repeated as described in Example 1, but with such amounts, and under such operating conditions, and with such results as are reported below in Table 1:

Claims: A process for the aralkylation of phenols, to produce a monoaralkylated product, characterized by comprising reacting in a heterogeneous phase, a phenol with a vinyl-aromatic hydrocarbon in the presence of an organic solvent immiscible with water and of a catalyst comprising or consisting essentially of an inorganic acid selected from the class consisting of orthophosphoric acid, pyrophosphoric acid and sulphuric acid in water solution at 60 to 90% by weight of the acid. A process as claimed in claim 1, characterized in that the phenol is selected from hydroquinone, resorcinol, pyrocatechol, pyrogallol, benzophenol, cresols, p-octyl-phenol, di-hydroxy-diphenyl, alpha-naphthol and beta-naphthol. A process as claimed in claim 1 or 2, characterized in that vinyl-aromatic hydrocarbon is selected from those of formula: wherein: Ar represents an aryl group containing from 6 to 18 carbon atoms, and R₁, R₂ and R₃, which may be the same as or different from one another, are selected from hydrogen and alkyl radicals having from 1 to 10 carbon atoms. A process as claimed in claim 3, characterized in that the vinyl-aromatic hydrocarbon is selected from styrene, alpha-methyl-styrene, alpha-ethyl-styrene, p-methyl-styrene, p-isopropyl-styrene, p-methyl-alpha-methyl-styrene, beta-methyl-styrene and vinyl-naphthalene. A process as claimed in any of claims 1 to 4, characterized in that molar ratio of phenol/vinyl-aromatic hydrocarbon is from 1.5 to 1, preferably from 1.3 to 1. A process as claimed in any of claims 1 to 5, characterized in that the solvent is an aromatic solvent such as toluene or xylene or a mixture of xylenes. A process as claimed in any of claims 1 to 6, characterized in that weight ratio of the solvent to the phenol is from 0.5 to 5, preferably from 1 to 2. A process as claimed in any of claims 1 to 7, characterized in that the catalyst is ortho-phosphoric acid, pyrophosphoric acid or sulphuric acid diluted in water at 70-80% by weight of the acid. A process as claimed in any of claims 1 to 8, characterized in that the molar ratio of the catalyst to the phenol is from 0.5 to 6, preferably from 1 to 3. A process as claimed in any of claims 1 to 9, characterized in that the reaction temperature is from 90° to 120°C, preferably from 110° to 115°C. A process as claimed in any of claims 1 to 10, characterized in that the phenol is hydroquinone and the vinyl-aromatic hydrocarbon is styrene.

Inventors: CHAPOY, LAWRENCE L., SOGLI, LORIS, UNGARELLI, RAFFAELE
Applicants: MONTEDISON S.P.A.
Application year: 1988
Main classification: C07C37
IPC codes: C07C39, C07B61, C07C37, C07C27, C07C67, B01J27