Silica extrudates

Abstract: The invention relates to a process for the preparation of a shapable dough which comprises mixing and kneading a particulate silica with water and with ammonia or an ammonia-releasing compound to obtain a mixture having a total solids content of from 25 to 60% by weight, the ammonia being present in an amount of from 0.5 to 20% by weight on the total solids content of the mixture, to a shapable dough obtained by this process, to the preparation of silica extrudates therefrom and to their use as catalyst carriers in hydrocarbon conversion or hydrocarbon synthesis reactions.

Description: The invention relates to the preparation of silica extrudates, to the preparation of a shapable dough for silica extrudates, to a shapable dough for silica extrudates and to the preparation of calcined silica extrudates and to their use. It is known that silica which is an interesting compound to be used as a carrier for catalysts, can not be extruded like other materials in conventional extrusion equipment to give reasonably strong products. In European patent application (publication) 167 324 is disclosed a method for the preparation of a silica extrudate whereby a particulate silica is mixed with water and an alkali metal compound to prepare a mixture which is extruded. However, the use of an alkali metal makes it necessary that the extruded silica must be soaked in a solution of ammonium nitrate and nitric acid to remove the alkali metal. Applicant has found that this process may be obviated by using ammonia or an ammonia-releasing compound in the preparation of a dough from which silica extrudates can be obtained. The invention therefore relates to a process for the preparation of a shapable dough which comprises mixing and kneading a particulate silica with water and with ammonia or an ammonia-releasing compound to obtain a mixture having a total solids content of from 25 to 45% by weight, the ammonia being present in an amount of from 0.5 to 20% by weight on the total solids content of the mixture. The invention further relates to a process for the preparation of silica extrudates which comprises mixing and kneading a particulate silica with water and with ammonia or an ammonia-releasing compound to obtain a mixture having a total solids content of from 25 to 45% by weight, the ammonia being present in an amount of from 0.5 to 20% by weight on the total solids content of the mixture and extruding the mixture. The invention further relates to a process for manufacturing calcined silica extrudates which comprises extruding a shapable dough into silica extrudates and drying and calcining the silica extrudates to a final temperature of between 300 °C and 1000 °C, and to calcined silica extrudates obtained by this process. The silica to be used in the process according to our invention is silica obtained by reacting a silicate, preferably sodium- or potassium silicate, with an acid. Preferred is the washed silica filter cake, the reaction product of waterglass and acid. The silica generally has an amorphous structure and gives no X-ray pattern. When silica gel is gradually heated to a higher temperature it loses water. Heating during longer times above 100 °C results that the water content decreases to about 5% by weight. The water content of the silica is determined by weight loss on ignition (LOI). A sample of the catalyst is weighed and then placed in a muffle furnace where it is heated at 1000 °C for 2 hours. After heating the sample is again weighed. The difference in weights represents the LOI or the amount of water present in the silica. When silica has been calcined, at e.g. 500 °C, it is less suitable for use in the extrusion process. However silica gels which have been spray dried are very suitable. Preferred is silica of about 98 to 99% purity, containing only very small percentages of iron, alumina etc. The total solids content of the mixture of silica, ammonia and water ranges from 25 to 45% by weight, preferably from 30 to 45% by weight and more preferably from 35 to 40% by weight, in order to obtain an extrudable mixture. The amount of ammonia ranges from 0.5 to 20% by weight, preferably from 2 to 15% by weight, more preferably from 3 to 10% by weight calculated on the total solids content. To improve the flux properties in the extruder the mixture may also comprise a polyelectrolyte, such as Nalco 7879 (obtained from Nalco). The mixture (with or without polyelectrolyte) can readily be extruded e.g. over the metal die-plate of the Bonnot-extruder. Cylindrical extrudates can be prepared, but other forms may be prepared as well, such as mentioned in US patent specification 4,028,227. It is possible to prepare silica with a surface area of more than 200 m 2 /g. Ammonia-releasing compounds other than NH 4 OH may be used as well. Ammonia-releasing compounds are compounds which by decomposing, e.g. under the influence of heat, give free NH 3 gas. It is possible prior to extrusion to admix titanium dioxide or zirconium dioxide to the composition. This is advantageous when the silica is used as carrier and the titanium and zirconium are the effective catalyst ingredients. The extruded silicas may be suitably used, for example, as carriers for catalysts, which are normally used in hydrocarbon conversion, like hydrodemetallization of heavy hydrocarbon oils, in hydrocarbon synthesis reactions, in the epoxidation of olefinically unsaturated compounds with organic hydroperoxides, in the hydrations of olefinically unsaturated compounds to produce the corresponding alkanols and in the purification of exhaust gases. EXAMPLE 1 A mixture was prepared having the following composition: silica (ex Crossfield) 525 g (LOI = 5%) aqueous ammonia (25% by weight of NH 3 ) 100 g water (demineralized) 625 g total 1250 g The mixture was prepared by adding the aqueous ammonia and water to the silica and the mixture was kneaded for 30 min. Then 50 g demineralized water was added to the mixture and the total mixture was further kneaded for 15 min. The total kneaded mixture was extruded. The obtained extrudates (diameter 1.5 mm) were dried at 120 °C for 2 h, broken to pieces of about 4 to 5 mm and calcined at 850 °C for 40 min. The silica extrudate had the following properties: BET surface area 116 m 2 /g mean pore diameter 28 nm pore volume 0.89 ml/g bulk crushing strength 1.01 MPa. EXAMPLE 2 A mixture was prepared having the following composition: silica (ex Crossfield) 525 g (LOI = 5%) aqueous ammonia (25% by weight of NH 3 ) 100 g water (demineralized) 625 g Nalco 7879 15 g total 1265 g The mixture was prepared by adding the aqueous ammonia and water to the silica and the mixture was kneaded for 25 min. Then 15 g of Nalco 7879 was added to the mixture and the total mixture was further kneaded for 5 min. The total kneaded mixture was extruded. The obtained extrudates (diameter 1.5 mm) were dried at 120 °C for 2 h, broken to pieces of about 4 to 5 mm and calcined at 850 °C for 40 min. The silica extrudate had the following properties: BET surface area 102 m 2 /g mean pore diameter 32 nm pore volume 0.94 ml/g bulk crushing strength 1.01 MPa. EXAMPLE 3 Examples 1 and 2 were repeated, with the exception that the calcination temperature was 500 °C and the time of calcination 2 h. The following results were obtained: without Nalco with Nalco BET surface area, m 2 /g 220 205 mean pore diameter, nm 25 27 pore volume, ml/g 1.00 1.13 bulk crushing strength, MPa 0.54 0.46 EXAMPLE 4 Using a composition as in Example 2, but with the double amount of ammonia, and carrying out the extrusion process with a Bonnot-extruder and drying and calcining the extrudate at 500 °C for 2 h and 850 °C for 40 min respectively gives the following properties to the two compositions: 500 °C/2 h 850 °C/40 min BET surface area 200 m 2 /g 66 m 2 /g mean pore diameter 24 nm 34 nm pore volume, ml/g 1.05 ml/g 0.79 ml/g bulk crushing strength 0.73 MPa 1.41 MPa EXAMPLE 5 A mixture was prepared having the following composition: silica (ex Crossfield) 556 g (LOI = 11.2%) titania gel 261 g aqueous ammonia (25% by weight of NH 3 ) 100 g water 399 g Nalco 7879 15 g total 1331 g The titania gel contained 45.5 g of solids. The mixture was prepared by adding the titania gel and 150 g of water to the silica and kneading the mixture for 5 min. Then aqueous ammonia and 249 g of water was added to the mixture and kneaded for 30 min. Nalco was added and the total mixture was kneaded for 10 min. The obtained kneaded mixture was extruded and the obtained extrudates (diameter 4 mm) dried for 2 h at 120 °C and broken to pieces of about 5 mm. Finally a part was calcined at 560 °C for 2 h and the remaining part was calcined at 850 °C for 30 min. The side crushing strength of the calcined silica extrudates was 109 N/cm and 217 N/cm respectively. The bulk crushing strength of the extrudates was 1.10 MPa. EXAMPLE 6 A mixture was prepared having the following composition: silica 2000 g aqueous ammonia (25% by weight of NH 3 ) 400 g Nalco 7879 19 g water (demineralized) 1352 g total 3771 g The silica has been obtained by grinding calcined silica spheres. The mixture was prepared by adding the aqueous ammonia and the water to the silica and kneading the obtained mixture for 30 min. 19 g of Nalco 7879 was added and the mixture then further kneaded for 5 min and extruded. The obtained extrudates (diameter 4 mm) were dried at 120 °C for 2 h and calcined at 850 °C for 1 h. The silica extrudate had the following properties: BET surface area 183 m 2 /g mean pore diameter 42 nm pore volume 0.84 ml/g bulk crushing strength 1.16 MPa

Claims: A process for the preparation of a shapable dough which comprises mixing and kneading a particulate silica with water and with ammonia or an ammonia-releasing compound to obtain a mixture, characterized in that the mixture has a total solids content of from 25 to 45% by weight, and that the ammonia is present in an amount of from 0.5 to 20 % by weight on the total solids content of the mixture. A process according to claim 1 wherein the silica is obtained by reacting a silicate with acid. A process according to claim 2 wherein silica filter cake is used. A process according to any one of the claims 1-3, wherein the total solids content is from 30 to 45% by weight, preferably 35 to 40% by weight. A process according to any one of the claims 1-4, wherein ammonia is present in an amount of from 3 to 10% by weight on the total solids content. A process according to any one of the claims 1-5, wherein a polyelectrolyte is admixed into the mixture. A process according to any one of the claims 1-6, wherein titanium dioxide or zirconium dioxide is admixed. A process for the preparation of silica extrudates from a shapable dough, which comprises mixing and kneading a particulate silica with water and with ammonia or an ammonia-releasing compound to obtain a mixture having a total solids content of from 25 to 45% by weight, the ammonia being present in an amount of from 0.5 to 20% by weight on the total solids content of the mixture and extruding the mixture. A process for manufacturing calcined silica extrudates which comprises drying and calcining the silica extrudates prepared by the process according to claim 8, to a final temperature of between 300 ° C and 1000 ° C.

Inventors: BOXHOORN GOSSE, DAAMEN JACOBUS THEODORUS, HUIZINGA TOM, MESTERS CAROLUS MATTHIAS ANNA, VELTHUIS OTTO MENTE, BOXHOORN, GOSSE, DAAMEN, JACOBUS THEODORUS, HUIZINGA, TOM, MESTERS, CAROLUS MATTHIAS ANNA MARIA, VELTHUIS, OTTO MENTE
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1988
Main classification: B01J21
IPC codes: C01B33, B01J21, B01J37