COATED ABRASIVE GRAINS AND A MANUFACTURING METHOD THEREFOR

Abstract: Coated abrasive grains and a manufacturing method for them are disclosed. The abrasive grains are coated using an immersion method with a coating comprising at least one substance selected from carbides, borides, and nitrides of a metal, comprising: preparing an immersion bath comprising a molten salt bath containing said metal; and immersing abrasive grains to be treated in said immersion bath for a suitable length of time.

Description: This invention relates to a manufacturing method in which a molten salt bath is employed, and in which abrasive grains are coated with a layer of a metal compound such as at least one substance selected from metallic carbides, metallic borides, and metallic nitrides. Abrasive grains such as diamond abrasive grains and hard BN abrasive grains are referred to as ultrahard abrasive grains and are widely used as starting materials for abrasive articles or as abrasives. In particular, abrasive grains comprising natural or synthetic diamonds are bonded together with a binder in the form of a metal, a synthetic resin, or a vitreous inorganic material to form abrasive articles, such as grinding wheels. These abrasive articles have a wide range of uses including the grinding of carbide tools and hard materials such as ceramics, ferrite, and glass, and the cutting of stones and concrete. As a result of the spectacular development of ceramics in recent years, diamond wheels and hard BN wheels, which enable high-precision grinding of ceramics, have been used in large quantities. However, presently-used abrasive grains have the following problems. For example, in the case of resin-bonded wheels or metal-bonded wheels which have diamond abrasive grains as their main component, in order to increase the bond strength between the abrasive grains and the resin or metal which serves as a binder, the surfaces of the abrasive grains are coated with a metal such as nickel. This metal coating is said to have the effect of preventing the deterioration of the resin due to heat which is generated along the edges of the abrasive grains during use of a grinding wheel. However, the metal coating has the problem that it causes the clogging of the wheel. On the other hand, vitrified-bonded wheels which also have diamond abrasive grains as their main component use a ceramic as a binder. As these wheels are manufactured by firing at high temperatures, the bonding strength between the abrasive grains and the binder is high due to a solid phase reaction. However, during the high-temperature firing, the diamond abrasive grains undergo thermal corrosion, and as a result manufacture is difficult. Japanese Published Unexamined Patent Application No. 55-162499 (1980) disclosed a method of coating the surface of diamond abrasive grains with Ti(C,N,O) by chemical vapor deposition in order to prevent oxidation of the abrasive grains during manufacture of wheels, improve the adhesion to coatings, and prevent the clogging of the wheel during grinding. However, the adhesion of a coating formed by this method is said to be inadequate. Thus, as the advantages of coated abrasive grains have been recognized, various methods have been proposed for improving the properties thereof. However, as all of these methods employ CVD or other vapor phase deposition processes, they are unsuitable for mass production, and they require large and expensive equipment in order to be carried out. The following U.S. patents are issued regarding coated diamond abrasive grains of the prior art: U.S. Patents 3,465,416; 3,520,667; 3,617,346; 3,650,714; 3,826,630; 3,924,031; 3,929,432; 4,063,907; 4,220,455; 4,417,906; and 4,606,738. Accordingly, in order to take advantage of the above-described excellent properties of coated abrasive grains, there is a need for a method which can easily and greatly improve the adhesion to coatings of coated abrasive grains and which at the same time is inexpensive. Therefore, an object of the present invention is to provide a method for the manufacture of ultrahard coated abrasive grains, the abrasive grains having superior oxidation resistance, wear resistance, and adhesion to coatings. Another object of the present invention is to provide a method for the manufacture of ultrahard coated abrasive grains having the above properties which is less expensive and more suitable for mass production than CVD. In Japanese Published Unexamined Patent Application No. 62-27577 (1987), one of the present inventors proposed a method for forming a hard coating on the surface of a metal using a molten chloride bath. It was found that this method greatly increases both the hardness of the surface of the metal and the wear resistance. As a result of subsequent research, it was found that this method is applicable not only to metals but to nonmetals as well. Particularly in the case of nonmetals, this method not only improves hardness, but the adhesion of the coating to the surface is remarkably increased. This is because it employs a molten salt bath, and a portion of the surface to be treated is roughened. Upon further investigation concerning the application of an immersion method for accomplishing the above objective, it was found that coating the surface of abrasive grains produces remarkable effects, and the present invention was completed. The term "immersion method" here refers to a method in which abrasive grains are immersed in a molten salt bath to form a surface coating. The present invention provides a manufacturing method for coated abrasive grains coated with a layer of metal compound which method comprises preparing a molten salt bath containing said metal and immersing the abrasive grains to be treated in said immersion bath to provide a coating on the grains of the carbide, boride or nitride of said metal. The coated grains of the present invention can be used without further treatment, or if necessary, they may be subjected to after-treatment by further coating, such as by plating, of a metallic compound, a metal, or an alloy. In preferred embodiments of the present invention, the abrasive grains are diamond abrasive grains or hard BN grains. When forming a metallic carbide coating, and particularly when the abrasive grains are hard BN abrasive grains, it is preferable to use hard BN abrasive grains on which carbon was previously deposited by vapor deposition. Furthermore, when a thick metallic carbide coating is desired, diamond abrasive grains previously coated with a carbon coating by carbon vapor deposition or other method can be used. The carbon in the surface layer of the abrasive grains reacts with the metal in the immersion bath to form a carbide coating. Alternatively, if uncoated hard BN abrasive grains are immersed, B is substituted by a metal in the immersion bath by a substitution reaction, and the resulting coating comprises a nitride of the metal coming from the immersion bath. The molten salt bath preferably comprises at least one substance selected from chlorides of an alkali metal and chlorides of an alkali earth metal. In a further preferred embodiment, the molten salt bath is a fluoride-containing chloride bath. The fluoride may comprise at least one substance selected from fluorides of an alkali metal and fluorides of an alkali earth metal. In accordance with a different mode of the invention, the molten salt bath may be a fluoride-containing molten bromide bath, a fluoride-containing molten iodide bath, or a fluoride-containing molten fluoride bath, and the immersion bath may be prepared by adding one or more of oxides of a metal, and halides of a metal, a metal in elemental form, and alloys thereof to the molten salt bath. In this case, the fluoride, the bromide, or the iodide is preferably a fluoride, a bromide, or an iodide of an alkali metal or an alkali earth metal. In a preferred embodiment, the immersion bath is prepared by adding an oxide and/or halide of a metal together with a metal in elemental form or an alloy thereof to the molten salt bath. When the immersion treatment is performed with different types of metals, it can be performed two or more times. In accordance with yet another mode of the invention, a manufacturing method for abrasive grains coated with a boron compound is provided in which an immersion bath is prepared by adding at least one of an oxide of boron, a boron alloy, and a boron-containing carbide (B₄C), preferably an oxide of boron and a boron alloy (or boron carbide) to a fluoride-containing molten halide bath, and uncoated abrasive grains or abrasive grains previously coated with a substance selected from Ti, Cr, V, W, Mo, Zr, Hf, Nb, Ta, Ni, and alloys or compounds thereof are immersed in the immersion bath for a suitable length of time. Coated abrasive grains of the present invention may of course be used instead of the above-described metal-coated abrasive grains. The "coating" of abrasive grains with a metal (a metal in elemental form, a metal alloy, or a metal compound) does not necessarily refer to completely enveloping the abrasive grains in the metal or to plating it with the metal. It is necessary only that the metal be applied to at least the surface to be treated. Many different methods can be employed for applying the metal, including electroplating, electroless plating, cladding, physical vapor deposition (sputtering, etc.), and chemical vapor deposition (vapor plating, etc.). There is no restriction on the shape of the abrasive grains. Figure 1 is a graph showing the oxidation resistance of conventional uncoated diamond abrasive grains; Figure 2 is a graph showing the oxidation resistance of coated diamond abrasive grains in accordance with this invention; Figures 3a and 3b are photomicrographs (x45) showing the surface condition of diamond abrasive grains coated with TiC and of peeled material, respectively, after a peeling test; Figures 4a and 4b are photomicrographs (x45) showing the surface condition of uncoated diamond abrasive grains and of peeled material, respectively, after a peeling test; Figure 5 is an electron microscope photograph (x1500) of the surface of a piece of the coated abrasive grains shown in Figure 3; and Figure 6 is a photograph (x3000) taken with an X-ray microanalyzer showing the distribution of elemental Ti in the same coated abrasive grains. The present invention will be explained more particularly. A molten chloride bath, which is a representative example of a molten salt bath which constitutes the immersion bath employed in the present invention, generally comprises KCl-BaCl₂ to which a fluoride such as NaF is added. Other examples of chlorides which can be employed for the molten chloride bath are NaCl, LiCl, and CaCl₂, and other examples of fluorides are NaF, KF, LiF, CaF₂, and BaF₂ . Preferably, the bath comprises a chloride of an alkali metal, a chloride of an alkali earth metal, and a fluoride of an alkali metal. The exact proportions of the components will be readily apparent to those skilled in the art from the foregoing explanation. However, with a KCl-BaCl₂-NaF bath, the proportions are generally 5 - 95 mole % of KCl, 5 - 95 mole % of BaCl₂, and 5 - 50 mole % of NaF. If the proportion of the fluoride is greater than 50 mole %, not only does the bath temperature become too high, but also corrosion becomes a problem. Alternatively, a bromide, an iodide, or a fluoride can be used in place of the chloride in the molten salt bath. As in the case in which a chloride is employed, the bromide, the iodide, or the fluoride is preferably selected from bromides, iodides, or fluorides of an alkali metal or an alkali earth metal. There is no particular restriction on the type of metal which is added to the molten bath. However, as one of the purposes of the present invention is to increase the adhesion of a coating to the abrasive grains being treated, hard metals which have in the past been thought hard to form into coatings are preferred, some examples of which are Si, Cr, V, B, W, Mo, Ti, Zr, Hf, Nb, Ta, and other members of groups IVa, Va, and VIa of the periodic table. It is advantageous that a portion of the metal which is added to the molten salt bath be in the form of a compound (typically an oxide), since metallic compounds are easy to obtain and convenient to handle. It is also advantageous that another portion of the metal be in the form of a metal powder. The metal powder may be in elemental form or in the form of an alloy, such as a ferroalloy. When sodium fluoride is used as the fluoride, the NaF and the oxides react in the molten salt bath containing potassium and/or sodium, and potassium and/or sodium metal fluorides are formed partially. These substances are formed by reactions such as TiO₂ → NaK₂TiF₆, Cr₂O₃ → NaCrF₃, V₂O₅ → Na₃VF₆, B₂O₃ → KBF₄, and WO₃ → K₃WF₆. The resulting substances then react on the surfaces of the abrasive grains and respectively become Ti-C (TiC), Cr-C (Cr₇C₃, Cr₃C₂, Cr₂₃C₆) , V-C (V₂C, V₄C₃ , V₈C₇, VC 0.88 ), B-C, W-C, and the like. At this time, the metal in elemental or alloyed form is thought to act as a reducing agent for the metal which was added to the bath in the form of a metallic oxide. There is no restriction on the amount of the metal to be added in elemental or alloyed form, but it is adequate if an oxide of such a metal constitutes 2 weight % of the immersion bath. If the amount of the metal is too small, a coating of sufficient thickness can not be obtained, and under usual conditions the lower limit is about 1 weight %. On the other hand, if the amount of metal is too large, the thickness of the resulting carbide coating becomes nonuniform. Under usual conditions, the upper limit is about 7 weight %. Preferably, the amount of metal is 5 - 7 weight %. The metal may be added to the molten salt bath in the form of a halide. When such a metallic halide is used, the molten salt bath may contain up to 40 weight % of the metallic halide. If the amount of metallic halide exceeds this level, the corrosion of equipment becomes a problem, and a health problem is created by the generation of large amounts of halogen gas. When a metal which is added to the molten salt bath is in the form of an oxide, a reducing agent for the oxide is also added to the bath. Examples of reducing agents are substances having a greater affinity for oxygen than the metal, e.g., chromium or group Va elements, such as Mn, Al, Ca, Si, Ti, and Zr, as well as alloys thereof such as Fe-Mn, Fe-Al, Fe-Ti, Fe-Zr, Fe-Si, Ca-Si, and Ca-Si-Mn. The reducing agent may constitute 2 - 20 weight % of the treatment bath. If less than 2 weight % is added, an adequate reducing effect is not obtained, and if more than 20 weight % is added, the formation of carbides is obstructed. Preferably, the proportion of the reducing agent is 5 - 15 weight %. The immersion time and temperature for the immersion method of the present invention vary in accordance with the type of metal compound which is to be formed, but in general it is sufficient to perform immersion at 700 - 1000°C for from one to several hours. The ultrahard abrasive grains which are employed in the present invention are preferably diamond abrasive grains, hard BN abrasive grains, or a mixture thereof. There is no particular restriction on the type of diamond abrasive grains which are employed, and abrasive grains of either natural or synthetic diamonds may be used. There is no particular limitation on grain size, but when the diamond or hard BN abrasive grains are to be made into a grinding wheel using a suitable binder, in general it is preferable that the grain sizes be approximately 106 - 90 µm (140 - 170 mesh ASTM) or 300 - 250 µm (50 - 60 mesh ASTM). Prior to immersion, it is not necessary to perform any preliminary treatment of the diamond abrasive grains or the hard BN abrasive grains. However, if degreasing or similar treatment is performed, the adhesion of the coating to be formed on the grains can be further increased. As explained earlier, the formation of a coating by immersion in accordance with the present invention can also be performed on abrasive grains which have been previously coated with a suitable metal by CVD, vacuum sputtering, or other method. However, the previously-applied coating is not restricted to a coating of a metal, and it can be a coating of a metallic compound in accordance with the present invention. Namely, by treating the surface of the abrasive grains which were coated with a metallic compound, e.g., a metallic carbide in the above manner by second time using the same type of molten salt bath, the metal in the coating which is already formed on the surface of the abrasive grains combines with another metal in the bath, and a second coating is formed. In this case, the metal in the bath which combines with the metal in the coating is preferably B, which is present in the bath in the form of an oxide such as B₂O₃. As a result, the second coating is a metallic boride coating. Namely, an oxide of boron (such as boron oxide) reacts in the fluoride-containing molten salt bath (e.g., B₂O₃→ KBF₄). The resulting compound reacts with a metal (such as Ti) in the first coating to form a substance MB₂ or MB (such as TiB₂ or TiB), wherein M stands for a metal. As a result of this treatment, the oxidation resistance of the abrasive grains is further improved. Next, the present invention will be described more particularly on the basis of the following examples. In the examples, unless otherwise indicated, % refers to % by weight. Example 1 42.2 mole % of KCl, 20.2 mole % of BaCl₂, and 37.6 mole % of NaF were placed in a porcelain crucible and then melted by heating. Next, prescribed quantities of metallic oxides and alloy powders (ferroalloys) were added and the mixture was thoroughly stirred to obtain an immersion bath. 2g of diamond abrasive grains having a grain size of 300 - 250 µm (50 - 60 mesh ASTM) (tradename "MBS" manufactured by General Electric) were immersed in this immersion bath at 850°C for 2 hours. The average coating thickness was 1.8 µm. The types and quantities of metallic oxides and alloys used in this example as well as the composition of the resulting coating are shown in Table 1. The immersion of the abrasive grains was performed using a stainless steel wire mesh bucket. The resulting coated abrasive grains were placed together with 14 sintered carbide balls having a diameter of 4.6 mm into a tempered hard glass bottle (16.5mm in diameter, 30 ml). The glass bottle was rotated at 150 rpm for 15 minutes, after which the coating adhesion was evaluated by comparing the weight of coating which had peeled off to the initial weight. The results are shown in Table 1. Figure 1 and Figure 2 are graphs which show the DTA (differential thermal analysis) curve and the TGA (thermogravimetric analysis) curve for uncoated diamond abrasive grains (Figure 1) and for abrasive grains which were coated in the above manner with a carbide of chromium (Test No. 2, Figure 2). If the curves of Figure 2 for coated abrasive grains of the present invention are compared with the curves of Figure 1 for a conventional example, it can be seen that the temperature which shows the peak of heat flow increased from 904°C to 1018.9°C, and the temperature at which oxidation loss occurred also increased. It is therefore clear that the oxidation resistance of the abrasive grains of the present invention is far superior to that of the conventional example. Figures 3a and 3b are photomicrographs (X45) showing the state of the surface coating and of peeled material from diamond abrasive grains coated with a TiC coating (formed in a manner similar to that used for Test No. 1) after the completion of the above-described peeling test. There was substantially no peeling of the coating, and the only reduction in the size of the grains was due to chipping. The coated abrasive grains of Figures 3a, 3b were prepared by immersion at 900°C for 3 hours, and the thickness of the TiC coating was 5 µm. Similarly, Figures 4a and 4b are photomicrographs (X45) showing the state of the surface coating and of peeled material after the completion of a peeling test of diamond abrasive grains which were not coated with a coating in accordance with the present invention. It can be seen that the abrasive grains of Figures 4a, 4b underwent a greater reduction in size than did the abrasive grains of Figures 3a, 3b, demonstrating that the coating of the present invention is effective not only for preventing peeling but also for preventing chipping. Figure 5 is an electron microscope photograph (X1500) of the surface of a piece of the coated abrasive grains of Figure 3a. It clearly shows that the TiC coating is adhered to the surface of the abrasive grains. Figure 6 is a photograph (X3000) which was produced by an X-ray microanalyzer and which shows the distribution of elemental Ti in the same coated abrasive grain. It can be seen that Ti is adequately dispersed among the diamond abrasive grains. Coated diamond abrasive grains produced by the method of the present invention which were obtained in the above-described manner were used as a starting material powder for the manufacture of a metal-bonded diamond whetstone. It was found to have a working life of roughly three times that of a metal-bonded diamond whetstone made from conventional uncoated diamond abrasive grains. Example 2 The coated diamond abrasive grains of Example 1 were coated with a second layer in the form of boride coating using the method of the present invention. Namely, B₂O₃ and boron in elemental form were added to the above-described molten salt bath to prepare an immersion bath, and then the procedure of Example 1 was followed. The same peeling resistance test as for Example 1 was performed on the resulting abrasive grains. The compositions of the resulting coatings and the test results are shown in Table 2. Immersion was carried out at 850°C for one hour. Each of the coating thicknesses shown in Table 2 is the total of the first layer (the carbide coating) and the second layer (the boride coating). Example 3 In this example, diamond abrasive grains were employed which had been previously coated with a metallic layer (2 µm thick) of Ti, Cr, V, W, or Mo using chemical vapor deposition. The previously-coated grains were then coated with a boride coating in the same manner as in Example 2. The compositions of the coatings and the peeling characteristics of the resulting coated abrasive grains are shown in Table 3. Immersion was performed at 950°C for 2 hours. Example 4 In this example, a metallic layer (approximately 2µm thick) of Ti, Cr, V, or Mo was formed by chemical vapor deposition on hard BN abrasive grains (trade name "BZN-550" manufactured by General Electric) having a grain size of 50 - 60 mesh. Next, a boride coating was formed atop the grains in the same manner as in Example 2. The compositions of the coatings and the peeling characteristics of the resulting coated abrasive grains are shown in Table 4. Immersion was performed at 950°C for 2 hours. Example 5 In this example, SiC abrasive grains (420 - 350 µm) were coated with a carbide coating in the manner of Example 1. The immersion bath temperature was maintained at 950°C, and the SiC abrasive grains were reacted therein for 2 hours. As in Example 1, the immersion bath contained a metallic oxide and an alloy. However, in this example the substitution reaction SiC → MeC (Me: metal) took place, and a carbide coating was formed. The types of metallic oxides and alloys employed in the immersion bath are shown in Table 5. The table also shows the coating thickness and the amount of peeling (%) of the coating. Example 6 In this example, a nitride coating was applied to C-BN abrasive grains (210 - 177 µm) in the manner of Example 1. Reaction was performed at 950°C for 2 hours. As when forming a carbide coating, the immersion bath contained a metallic oxide and an alloy. The substitution reaction BN → MeN (Me: metal) took place, and a nitride coating was formed. The composition of the coating and its characteristics are shown in Table 6. Example 7 In this example, first a nitride coating was formed on BN abrasive grains (210 - 177 µm) in the manner of Example 6, and then a boride layer was formed atop the nitride coating in the manner of Example 2. Immersion was performed at 950°C for one hour. The results for this example are shown in Table 7. Example 8 In this example, a bromide bath was employed. The bath composition was 37.6 mole % of NaF, 31.2 mole % of NaBr, and 31.2 mole % of KBr. MBS abrasive grains 300 - 250 µm (50 - 60 mesh ASTM) were immersed in the bath at 950°C for 2 hours. The results are shown in Table 8. Example 9 In this example, an immersion bath was employed which had a composition of 37.6 mole % of NaF, 31.2 mole % of NaI, and 31.2 mole % of KI. A metallic oxide, a metallic halide, a metal in elemental form, or an alloy was added to the bath, and various coatings were formed on MBS abrasive grains (50 - 60 mesh) in a manner like that employed in Example 1. Immersion was carried out at 950°C for 2 hours. The results are shown in Table 9. Example 10 In this example, an immersion bath was employed which had a composition of 37.6 mole % of NaF and 62.4 mole % of KF. A metallic oxide, a metal in elemental form, or an alloy was added to the bath, and various coatings were formed on MBS abrasive grains 300 - 250 µm (50 - 60 mesa ASTM) in a manner like that employed in Example 1. Immersion was carried out at 950°C for 2 hours. The results are shown in Table 10. In this manner, according to the present invention, by merely performing simple immersion treatment using a molten salt bath which is easy to handle, a surface coating which has excellent adhesion and oxidation resistance not exhibited by conventional coatings is obtained. Therefore, the present invention greatly contributes to the advancement of industry. (EXAMPLE 1) Test No. Metallic Oxide Alloy Coating Composition Coating Thickness (µm) Amount of Peeling (%) 1 TiO₂ Fe-Ti Ti-C 2.0 0.5 2 Cr₂O₃ Fe-Cr Cr-C 1.8 0.4 3 V₂O₅ Fe-V V-C 1.8 0.3 4 WO₃ Fe-W W-C 1.9 0.4 5 MoO₃ Fe-Mo Mo-C 1.8 0.5 6 Ta₂O₅ Fe-Ta Ta-C 1.5 0.3 7 ZrO₂ Fe-Zr Zr-C 1.4 0.2 8 Nb₂O₅ Fe-Nb Nb-C 1.8 0.3 9 SiO₂ Si Si-C 0.8 0.3 10 B₂O₃ B B-C 0.5 0.4 NOTE: The thickness of the coating was determined on the surface of a piece of the peeled grains by means of an electron microscope. (EXAMPLE 2) Test No. First Layer Composition Second Layer Composition Total Thickness of Coatings (µm) Amount of Peeling (%) 11 Ti-C Ti-B single layer or Ti-B, B-C composite 2.1 0.6 12 Cr-C Cr-B single layer or Cr-B, B-C composite 1.8 0.5 13 V-C V-B single layer or V-B, B-C composite 1.9 0.4 14 W-C W-B single layer or W-B, B-C composite 1.7 0.5 15 Mo-C Mo-B single layer or Mo-B, B-C composite 1.7 0.5 16 Ta-C Ta-B single layer or Ta-B, B-C composite 1.4 0.4 17 Zr-C Zr-B single layer or Zr-B, B-C composite 1.3 0.4 18 Nb-C Nb-B single layer or Nb-B, B-C composite 1.7 0.5 NOTE: The second layer was very thin (0.1∼0.2 µm). A total thickness smaller than the starting layer seems to be caused by experimental errors. (EXAMPLE 3) Test No. First Layer Composition Second Layer Composition Total Thickness of Coatings (µm) Amount of Peeling (%) 19 Ti Ti-B 1.9 3.0 20 Cr Cr-B 1.7 2.8 21 V V-B 1.6 2.6 22 W W-B 1.8 3.2 23 Mo Mo-B 1.6 3.5 (EXAMPLE 4) Test No. First Layer Composition Second Layer Composition Total Thickness of Coatings (µm) Amount of Peeling (%) 24 Ti Ti-B 1.8 3.1 25 Cr Cr-B 1.7 2.6 26 V V-B 1.5 2.7 27 W W-B 1.8 3.3 28 Mo Mo-B 1.6 3.7 (EXAMPLE 5) Test No. Metallic Oxide Alloy Coating Composition Coating Thickness (µm) Amount of Peeling (%) 29 TiO₂ Fe-Ti Ti-C single layer or Ti-C,Ti-Si composite 23.0 1.0 30 Cr₂O₃ Fe-Cr Cr-C single layer or Cr-C,Cr-Si composite 25.0 0.9 31 V₂O₅ Fe-V V-C single layer or V-C,V-Si composite 5.5 0.6 32 WO₃ Fe-W W-C single layer or W-C,W-Si composite 5.6 0.7 33 MoO₃ Fe-Mo Mo-C single layer or Mo-C,Mo-Si composite 5.3 1.0 34 Ta₂O₅ Fe-Ta Ta-C single layer or Ta-C,Ta-Si composite 4.5 0.6 35 ZrO₂ Fe-Zr Zr-C single layer or Zr-C,Zr-Si composite 4.4 0.5 36 Nb₂O₅ Fe-Nb Nb-C single layer or Nb-C,Nb-Si composite 5.6 0.5 (EXAMPLE 6) Test No. Metallic Oxide Alloy Coating Composition Coating Thickness (µm) Amount of Peeling (%) 37 TiO₂ Fe-Ti Ti-N single layer or Ti-N,Ti-B composite 9.2 1.2 38 Cr₂O₃ Fe-Cr Cr-N single layer or Cr-N,Cr-B composite 10.0 1.0 39 V₂O₅ Fe-V V-N single layer or V-N,V-B composite 4.5 0.8 40 WO₃ Fe-W W-N single layer or W-N,W-B composite 4.0 0.5 41 MoO₃ Fe-Mo Mo-N single layer or Mo-N,Mo-B composite 4.0 0.5 42 Ta₂O₅ Fe-Ta Ta-N single layer or Ta-N,Ta-B composite 4.5 0.4 43 ZrO₂ Fe-Zr Zr-N single layer or Zr-N,Zr-B composite 4.3 0.3 44 Nb₂O₅ Fe-Nb Nb-N single layer or Nb-N,Nb-B composite 4.5 1.0 (EXAMPLE 7) Test No. First Layer Composition Second Layer Composition Total Thickness of Coatings (µm) Amount of Peeling (%) 45 Ti-N single layer or Ti-N,Ti-B composite Ti-B single layer or Ti-B,B-N composite 9.2 1.3 46 Cr-N single layer or Cr-N,Cr-B composite Cr-B single layer or Cr-B,B-N composite 9.9 1.2 47 V-N single layer or V-N,V-B composite V-B single layer or V-B,B-N composite 4.6 1.0 48 W-N single layer or W-N,W-B composite W-B single layer or W-B,B-N composite 3.9 0.7 49 Mo-N single layer or Mo-N,Mo-B composite Mo-B single layer or Mo-B,B-N composite 4.0 0.6 50 Ta-N single layer or Ta-N,Ta-B composite Ta-B single layer or Ta-B,B-N composite 4.4 0.5 51 Zr-N single layer or Zr-N,Zr-B composite Zr-B single layer or Zr-B,B-N composite 4.3 0.5 52 Nb-N single layer or Nb-N,Nb-B composite Nb-B single layer or Nb-B,B-N composite 4.4 1.2 NOTE: The second layer was very thin (0.1 ∼0.2 µm). A total thickness smaller than the starting layer seems to be caused by experimental errors. (EXAMPLE 8) Test No. Additive to Immersion Bath Coating Composition Coating Thickness (µm) Amount of Peeling (%) 53 Ti Ti-C 6.2 1.1 54 Fe-Ti Ti-C 6.1 1.0 55 V₂O₅, Aℓ V-C 3.0 0.7 56 K₂TiF₆, Fe-Ti TiC 6.3 1.1 57 Fe-Cr Cr-C 5.3 0.9 58 Fe-V V-C 5.4 0.4 59 Fe-W W-C 5.3 0.8 60 Fe-Mo Mo-C 5.2 0.9 61 ZrO₂, Fe-Zr Zr-C 4.0 0.4 62 Nb₂O₅, Fe-Nb Nb-C 5.3 0.4 NOTE: It is thought that the surface of commonly-used metals and alloys is slightly oxidized, and technically, these substances are not pure metals. (EXAMPLE 9) Test No. Additive to Immersion Bath Coating Composition Coating Thickness (µm) Amount of Peeling (%) 63 Ti Ti-C 6.1 1.0 64 V₂O₅, Aℓ V-C 3.0 0.7 65 K₂TiF₆, Fe-Ti Ti-C 5.4 1.0 66 Fe -Cr Cr-C 5.2 0.9 67 Fe -V V-C 5.3 0.5 68 ZrO₂, Fe-Zr Zr-C 4.0 0.5 69 Nb₂O₅, Fe-Nb Nb-C 5.1 0.4 (EXAMPLE 10) Test No. Additive to Immersion Bath Coating Composition Coating Thickness (µm) Amount of Peeling (%) 70 Ti Ti-C 10.1 1.5 71 V₂O₅, Aℓ V-C 4.5 0.9 72 Fe-Cr Cr-C 8.9 1.2 73 Fe-V V-C 8.1 1.3 74 ZrO₂, Fe-Zr Zr-C 6.3 0.6 75 Nb₂O₅, Fe-Nb Nb-C 7.8 0.7 76 TiCℓ₃ Ti-C 2.7 0.8

Claims: A method for producing coated abrasive grains coated with a layer of a metal compound in which the method comprises: preparing a molten salt bath containing said metal; and immersing the abrasive grains to be treated in said immersion bath to provide a coating on the grains of the carbide, boride or nitride of said metal. A method as claimed in claim 1, wherein said abrasive grains which are to be coated are diamond abrasive grains or hard BN abrasive grains. A method as claimed in claim 1 or claim 2, wherein said molten salt bath is a fluoride-containing molten chloride bath, and said bath is prepared by adding at least one substance selected from oxides of said metal, halides of said metal, said metal in elemental form and alloys of said metal to said molten salt bath. A method as claimed in claim 3, wherein said molten salt bath is a fluoride-containing molten bromide bath, a fluoride-containing molten iodide bath, or a fluoride-containing fluoride bath. A method as claimed in any one of claims 1 to 4, wherein said bath is prepared by adding an oxide of boron and either a boron-containing alloy or a boron-containing carbide to said molten salt bath, and uncoated abrasive grains or abrasive grains which have been previously coated with a metal selected from Ti, Cr, V, W, Mo, Zr, Hf, Hb, Ta, Ni, and alloys or metallic compounds thereof are immersed in said bath to provide the coating of a boride of said metal on said abrasive grains. A method as claimed in any one of claims 1 to 4 wherein the abrasive grains are diamond abrasive grains and they are first provided with a coating of carbon prior to immersing the grains in the immersion bath whereupon the said metal and the carbon react to provide a coating of a carbide of said metal on said abrasive grains. A method as claimed in any one of claims 1 to 4, wherein the metal is provided in the immersion bath by adding an oxide of metal and also an alloy of the metal so that the hard abrasive grains are provided with a coating comprising the carbide of said metal. A method as claimed in claim 7, wherein the resulting coated abrasive grains are provided with a boride coating by forming a second immersion bath by adding boron oxide and boron in elemental metal form to a molten salt bath and then immersing the abrasive grains therein to provide a boride coating. A method as claimed in any of claims of 1 to 4, wherein the abrasive grains contain nitrogen and a metallic oxide and an alloy is added to the said immersion bath so that when the abrasive grains are immersed therein a coating of metal nitride is produced on the surface of the said abrasive grains. A method as claimed in any one of the preceding claims wherein the said metal is Ti, Cr, V, W, Mo, Ta, Zr, Nb, Si or B. A method of producing a grinding wheel or other abrasive tool characterised in that said wheel or tool is formed by bonding coated abrasive grains produced by the method claimed in any one of the preceding claims. The use of a grinding wheel or other abrasive tool produced by the method as claimed in claim 11 to grind or otherwise shape a ceramic material.

Inventors: AOKI, SATOSHI, FUKUTA, YOICHI, HISADA, EIICHI, OKI, TAKEO
Applicants: NORITAKE CO., LIMITED, OKI, TAKEO
Application year: 1988
Main classification: B24D3
IPC codes: C04B41, C09K3, C23C8, C23C28