PROCESS FOR PREPARING COMPOUND METAL OXIDES

Abstract: A process for preparing compound metal oxides, a superconductive compound oxides for instance, is disclosed. The process comprises preparing an aqueous solution containing a predetermined content ratio of chloride, nitrate or acetate of a rare earth metal, an alkaline earth metal and copper, slightly basifying the solution to form hydroxides of the rare earth metal and copper and then introducing carbon dioxide to form carbonate of the alkaline earth metal, collecting the thus formed mixed precipitate of hydroxides and carbonate and firing it.

Description: Field of the Invention This invention relates to a process for preparing compound metal oxides using specific chemical steps therefor. More specifically, this invention relates to a specific process for preparing compound metal oxides of specific compositions which are useful as superconductor materials, oxygen sensors, catalysts, etc. Especially, compound metal oxides of a rare earth metal, an alkaline earth metal and copper have recently drawn attention as superconductor materials which exhibit superconductivity at temperatures over 77K. Background of the Invention As methods for preparing compound metal oxides, there have been processes in which (1) Oxides, carbonates or oxalates of the respective component metals are physically mixed in the state of powder, the mixture is fired and pulverized; (2) Water-soluble salts such as nitrates of the respective components metals are dissolved in water to make a homogeneous solution, the metals are coprecipitated as insoluble oxalates by addition of oxalate ions, and the precipitate is collected and fired into a compound metal oxide. In process (1), powders are mixed and fired. Therefore, the reaction proceeds from the contact boundaries of the powder particles and there remain some unreacted portions. Thus the product often deviates in compositions from that intended. In process (2), the condition of precipitation differs from metal to metal, and, therefore, a precipitate containing a rare earth metal, an alkaline earth metal and copper, for instance, in the content ratio exactly the same as the content ratio in the solution is not always formed. Therefore, compound metal oxides of compositions different from that intended are inevitably formed. In process (2), a method in which precipitation of oxalate by addition of oxalate ions is caused at the pH of around 5 is preferably employed. Even in this method, however, sometimes compound metal oxides the composition of which deviates by several tens % from the intended composition are produced, and thus a compound metal oxide of the intended composition cannot be produced regularly and reproducibly. Jap. J. of Applied Physics, Vol. 26, pages L1159-L1160 (1987) refers to a method for preparing a Y-Ba-Cu-O superconductor by preparing an aqueous solution containing a predetermined content ratio of chlorides, nitrates or acetates ofa rare earth metal, copper and an alkaline earth metal, said content ratio corresponding to the composition of the desired compound metal oxide, basifying the solution to precipitate the hydroxides of these metals, collecting the precipitate and drying it, compacting the precipitate and calcinating it at a temperature of 400 to 950°C. The electric resistance of this product drops around 95 K and vanishes completely at 75 K. This invention relates to an improvement of the above-described conventional coprecipitation process. Disadvantages of conventional coprecipitation processes are diminished by the process as claimed in claim 1 or 2. Summary of the Invention This invention provides a process for preparing a compound metal oxide of a rare earth metal, an alkaline earth metal and copper of a specific composition comprising preparing an aqueous solution containing a predetermined content ratio of chloride, nitrate or acetate of a rare earth metal, an alkaline earth metal and copper, said content ratio corresponding to the composition of the object coumpound metal oxide, adjusting the pH of the solution to 6 - 9 to form a fine precipitate of hydroxides of the rare earth metal and copper at first, causing it to form a suspension and thereafter introducing carbon dioxide gas into the suspension to form a fine homogeneous coprecipitate of alkaline earth metal carbonate, rare earth metal hydroxide and copper hydroxide, and collecting the coprecipitate and firing it. Preferably, the introduction of carbon dioxide gas is carried out while the pH of the suspension is maintained at 6.5 - 7.5 and the temperature is kept at 0 - 20°C. Lower temperatures are preferred because finer particles are obtained. In the present invention, the term "rare earth metal" means Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu. In the present invention, the term "alkaline earth metal" means Be, Mg, Ca, Sr and Ba. The process of the present invention is carried out as follows. A mixed solution containing chloride, nitrate or acetate of a rare earth metal, an alkaline earth metal and copper in a predetermined content ratio is prepared, wherein the concentrations of the salts must be adjusted so that none of them deposit. After the salts are completely dissolved, the pH of the solution is adjusted to 6 - 9 so as to precipitate hydroxides of copper and the rare earth metal. The solution containing the precipitate is thoroughly stirred with the pH maintained, and carbon dioxide gas is blown into the suspension so that fine bubbles are formed. Thus a fine alkaline earth metal carbonate precipitate is formed. The adjustment of the pH is preferably effected with ammonia or an organic amine. At a pH of less than 6, precipitation of rare earth metal and copper hydroxides is insufficient. At a pH higher than 9, precipitation of copper hydroxides is again poor. The formed precipitate is collected and fired. Preferably firing is carried out as follow. The collected precipitate is compacted and the compact is calcined at a temperature of 400 - 900°C and roasted under an oxygen partial pressure of at least the same as that in air or higher. Thus the desired compound oxide is obtained. The point of the present invention does not reside in the step of firing but in the step of precipitation. By the process of the present invention, compound metal oxides the compositions of which are less deviated from the intended composition than the conventional process can be obtained. Specific Description of the Invention The process of the present invention and the use of the products thereof are explained by way of working examples. Example 1 5.651 g of Y₂O₃ (99.99 % purity) 19.754 g of BaCO₃ (99.9 % purity) and 11.943 g of CuO (99.9 % purity) were dissolved in 30 ml of concentrated nitric acid, and the solution was diluted to 1 liter. The solution was kept at 20°C, and the pH of the solution was adjusted to 7 with ammoniacal water so that the first step precipitation occurred. Then, 99.9 % pure carbon dioxide gas was blown into the suspension for 30 minutes at the rate of 500 mℓ/min. so that the second step precipitation occurred. During the bubbling of carbon dioxide gas, the pH of the suspension was maintained at 7, and the temperature was kept at 20°C. The precipitate was collected by suction filtration and dried in vacuo at 50°C for 15 hours. The obtained reaction product was calcined in an alumina boat at 900°C for 5 hours in air. The obtained powder was compacted into pellets and fired at 930°C for 10 hours. The fired pellets were cooled in the furnace at the rate of 100°C/hr. The product was analyzed by X-ray diffraction analysis and was identified to be YBa₂Cu₃O 7 - x perovskite type compound, wherein x is a small fraction which represents deviation from the stoichiometric relation but cannot be specified for the time being. Three 0.2 g samples were taken from the product and were chemically analyzed. The results are indicated in Table 1. (Molar Ratio) Sample No. Y Ba Cu 1 1.00₂ 2.00₁ 3 2 0.99₉ 2.00₀ 3 3 1.00₁ 1.99₉ 3 The product was also observed under a scanning electron microscope. The particle size was 0.1 - 0 2µm. The electric conductivity of the thus obtained pellets were measured while chilled with liquid nitrogen. The electric resistance sharply dropped from 96K and it became zero at 94K. Comparative Example 1 The same aqueous solution as used in Example 1 was prepared and the pH of the solution was adjusted to 5.5 to form a precipitate and thereafter barium carbonate by introduction of carbon dioxide. The obtained precipitate was calcined, and roasted into a compound metal oxide. However, precipitation of yttrium was poor and the Y:Ba:Cu ratio was 0.4:2:2, and the compound oxide did not exhibit superconductivity. Comparative Example 2 The same aqueous solution as used in Example 1 was prepared and the pH of the solution was adjusted to 9.5 to form a precipitate. Thereafter carbonate was formed by introduction of carbon dioxide. The obtained precipitate was calcined, and roasted into a compound metal oxide. However, copper did not precipitate and the composition of the resulting compound was Y:Ba:Cu=1. 0:2. 65:0. The compound did not exhibit superconductivity.

Claims: Process for preparing a compound metal oxide of a rare earth metal, copper and an alkaline earth metal comprising preparing an aqueous solution containing a predetermined content ratio of chlorides, nitrates or acetates of a rare earth metal, copper and an alkaline earth metal, said content ratio corresponding to the composition of the object compound metal oxide, basifying the solution to precipitate the hydroxides of these metals, collecting the precipitate and drying it, compacting the precipitate and calcinating it at a temperature of 400 to 950°C, characterized in that the solution of a rare earth metal, copper and an alkaline earth metal is first basified to a pH of 6-9 so as to precipitate hydroxides of the rare earth metal and copper and then carbon dioxide gas is introduced into the suspension so as to precipitate the alkaline earth metal as carbonate. Process according to claim 1, characterized in that the carbon dioxide is blown into the suspension containing the hydroxides of the rare earth metal and copper, the pH of the suspension is maintained at 6.5-7.5 and the temperature is kept at not higher than 20°C.

Inventors: HASEGAWA, NOZOMU, KIMURA, ETSUJI, NISHIYAMA, YUTAKA
Applicants: MITSUBISHI MATERIALS CORPORATION
Application year: 1988
Main classification: C01G3
IPC codes: H01L39, C01G3, C01G1, H01B12, C04B35