MECHANICAL PLASTING PROCESS

Abstract: This invention concerns a mechanical plating process comprising: shaving metal off from a pure metal or alloy block and plating an object to be plated with the shaved off metal by the use of at least a single metal brush, where­ in the metal block and the metal brush are in frictional contact with each other, and the object to be plated and the metal brush are concurrently in frictional contact with each other.

Description: The invention relates to a mechanical plating process, comprising shaving metal off from a pure metal or alloy block and plating an object to be plated with said shaved off metal by the use of at least a single metal brush, wherein said metal block and said metal brush are in frictional contact with each other, and said object to be plated and said metal brush are concurrently in frictional contact with each other. The plating process of the invention is applicable to various industrially produced goods that require corrosion resistance, heat-resistance, abrasion-resistance, solderability, platability or decorability. Among conventional plating processes employed for various materials or parts are electroplating, chemical plating, hot dipping or flame spraying; these processes are applied in their own ways according to circumstances in order to provide a thin metal coat on the surface of an object. Electroplating is made in aqueous solutions containing ions of metal to be plated with DC current being applied between the negative electrode, an object to be plated, and the positive electrode. Chemical plating does not need electricity; it is employed when insulating objects such as glass or plastic are to be plated. Hot dipping is made in molten metal by dipping an object to be plated in it. Flame spraying is made with molten metal being sprayed on an object to be plated with a jet of gas or compressed air. These processes have their own merits but drawbacks or problems at the same time. That is, in electroplating it is difficult to plate an alloy. Chemical plating is not suited to give a thick metal layer on an object, while it needs expensive chemicals. In hot dipping it is difficult to adjust the thickness of the metal layer on an object, while it is convenient to plate the inside of a pipe, for example, merely by dipping a pipe. Flame spraying tends to make an object porous; besides, metal particles are subject to oxidation. However, their greatest common problems of all are that the adhesion of plated metal at an object is not necessarily assured; apparatuses required for their processes are generally expensive; electroplating and chemical plating need to have a treatment process for their spent solutions to be discharged. In order to solve these problems, the present inventors already offered a proposal of mechanically plating an object with a pure metal or alloy brush being in frictional contact with the object. However, they found that the brush had problems in being subject to oxidation, too expensive for practical use, and readily falling out. Furthermore, a mechanical plating process of the type mentioned in the beginning is known from DE-C-430 016. This process which is schematically depicted in Fig. 1, is used for coating aluminum onto a metal surface. The process comprises shaving off aluminum particles from an aluminum block and transferring them to the metal surface by a metal brush, the metal brush being at all times in frictional contact with both the aluminum block and the metal substrate. However, the inventors of the present invention have found that the thickness of the aluminum coating provided by such process on the surface of a metal foil diminishes considerably along the length of this metal foil as shown in Figs. 3 to 6 by the curves with the white circles. It is an object of this invention to provide a mechanical plating process completely free from drawbacks in conventional electroplating, chemical plating, hot dipping, and flame spraying processes. It is another object of this invention to provide a mechanical plating process in which a metal brush is hardly oxidized, and hardly falls out and wherein the thickness of the metal coating on the object is uniform. According to a first aspect of the present invention these objects are accomplished by a mechanical plating process of the type mentioned in the beginning, which is characterized by conducting said mechanical plating process while removing small metal particles from said metal brush with a grinder or a cutting tool to remove metal particles remaining on the brush after the brush has brought the shaved off metal particles in contact with the object to be plated. According to a second aspect of the invention the above objects are achieved by a mechanical plating process of the type mentioned in the beginning, which is characterized by continuously conducting said mechanical plating process while moving said metal block in such a way as to always re-fresh the surface of said metal block. According to a third aspect of the invention the above objects are accomplished also by a mechanical plating process of the type mentioned in the beginning, which is characterized by continuously conducting said mechanical plating process while removing metal crust formed on said metal block by the contact of said metal block and said metal brush with a grinder or a cutting tool so as to re-fresh the surface of said metal block. A further development of the mechanical plating process according to the above second and third aspects is characterized by conducting said mechanical plating process while removing small metal particles from said metal brush with a grinder of a cutting tool to remove metal particles remaining on the brush after the brush has brought the shaved off metal particles in contact with the object to be plated. As a cross reference it is referred to EP-A-0 318 864 of Nippon Yakin Kogyo Co., Ltd. also disclosing a mechanical plating process of the above type however in the context of converting aluminum present in the surface layer to theta-alumina whiskers. Preferred embodiments of the invention and examples of the invention and for explaning the invention are now described with reference to the drawings, wherein: Fig. 1 is a schematic illustration of a conventional apparatus of the type disclosed in DE-C-430 016, which is improved according to Figs. 2(a) through 2(d) such that by these improved apparatuses the present invention can be practically embodied; Figs. 2(a) through 2(d) are schematic illustrations showing embodiments of this invention; Fig. 3 is a graph showing a change in the thickness of plated copper layer along the longitudinal direction of a foil in Example 2; Fig. 4 is a graph showing a change in the thickness of plated aluminum layer along the longitudinal direction of metal foil in Example 3; Fig. 5 is a graph showing a change in the thickness of plated aluminum layer along the longitudinal direction of metal foil in Example 4; and Fig. 6 is a graph showing a change in the thickness of plated copper layer along the longitudinal direction of metal foil in Example 5. In Figs. 3 through 6, the results of the examples of this invention and comparative examples are shown together in the same graph as solid and open circles for comparison respectively. In this invention, a metal block, an object to be plated, and a metal brush for use in plating can be combined variously with one another in practical use. But in principle, a metal block has to be softer than or as hard as a metal brush. For example, a metal block and a metal brush may be made of the same metal; also, an aluminium block and a copper brush can be combined, as well as a copper block and a steel brush. As for an object to be plated, many materials can be used for it with no limitation in particular. That is, Fe-42%Ni alloy, stainless steel and so forth can be used similarly. Because metal of a block clings to a brush, the oxidation of the brush can be prevented. Fig. 1 shows an apparatus of the type disclosed in DE-C-430 016. In the figure, 1 denotes a metal brush, 2 denotes a metal block, and 3 denotes an object to be plated. The surface of the object 3 is plated with metal of the block 2 by means of the metal brush 1 touching both the metal block 2 and the object 3, being rotated as fast as about 2400 rpm for example. In the figure, the metal block 2 is located above the object 3 to be plated with the metal brush 1 in between. But it is needless to say that the metal block 2 and the object 3 may be positioned elsewhere around the metal brush 1. Now with reference to Figs. 2(a) and (b), one embodiment of this invention will be described below in detail. This is a mechanical plating process comprising: shaving metal off from a pure metal or alloy block and plating an object to be plated with the shaved off metal by the use of at least a single metal brush, wherein the metal block and the metal brush are in frictional contact with each other, and the object to be plated and the metal brush are concurrently in frictional contact with each other. The mechanical plating process is conducted while removing small particles from the metal brush with a grinder or a cutting tool after the brush has brought the shaved off metal particles in contact with the object to be plated. Thereby the small metal particles still clinging to the metal brush are removed therefrom. In this mechanical plating process, the grinder or the cutting tool is disposed on the circumference of the metal brush between where the metal block comes into contact with the metal brush and where the object to be plated comes into contact with the metal brush. According to this process, since small metal particles of the metal block, shaved off from the metal block however not plated on the object but rather clinging to the metal brush, can be removed from the brush by the grinder or the cutting tool in contact with the metal brush, they are prevented from adhering to the metal block again so firmly as to form a hard crust thereon, so that now the metal block can be used continuously, and this makes it possible to conduct the mechanical plating process in a continuous manner. In this process, as far as their hardness is concerned, a metal block, a metal brush, and an object to be plated can be combined variously with one another in practical use. But in principle, the metal block has to be softer than or as hard as the metal brush. Moreover, the grinder or the cutting tool, for example, a bite, is enough if only they are so hard as to be able to shave the metal off from the metal brush; and as for the shape of the metal block, there is no limitation in particular if only the metal block has a face with which it can be in contact with the metal brush. Figs. 2(a) and (b) are a schematic illustration showing this process, in which 1 denotes a metal brush, 2 denotes a metal block, 3 denotes an object to be plated, 4 denotes a grinder (Fig. 2(a)) or an endless belt type abrasive tool (Fig. 2(b)), and 5 denotes a plated metal layer. The metal layer 5 can be formed on the object 3 with the metal brush 1, touching both the metal block 2 and the object 3, being rotated as fast as its circumferential speed attains about 2000 meters a minute, for example. Also, since the metal brush 1 and the grinder/the cutting tool 4 are in contact with each other in such a way as to remove small metal particles from the metal brush, the re-adhesion of the small metal particles to the metal block 2, which causes the formation of a hard tenacious crust on the metal block, is prevented completely; in consequence, a continuous mechanical plating can be conducted over many hours with the surface of the metal block being kept as fresh as ever; thus, there forms a metal layer very uniform in thickness on the object. According to another embodiment of this invention, the mechanical plating process can also be embodied in a continuous manner with the surface of the metal block being similarly kept fresh. When the metal block is crusted with metal, shaved off from itself but not plated on the object, the metal develops into such too hard a crust to be shaved off by the metal brush that metal to be plated on the object becomes more and more lessened, whereby not only does it take long time for plating but also the thickness of plated metal is to be irregular from portion to portion or decrease in progress of plating on the contrary. In order to eliminate these drawbacks and improve the irregularity or the decrease in the thickness of plated metal, the present inventors made intensive studies and found useful for that a mechanical plating process comprising shaving metal off from a pure metal or alloy block and plating an object to be plated with the shaved off metal by the use of at least a single metal brush, wherein the metal block and the metal brush are in frictional contact with each other, and the object to be plated and the metal brush are concurrently in frictional contact with each other, characterized by continuously conducting the mechanical plating process while moving the metal block in such a way as to always re-fresh the surface of the metal brush. In other words, this mechanical plating process is characterized in that the metal block is moved in such a way that it can always give the metal brush a fresh surface of itself. This mechanical plating process can be characterized in another way by continuously conducting it while removing metal crust formed on the metal block by the contact of the metal block and the metal brush with a grinder or a cutting tool so as to refresh the surface of the metal block Like this, according to this invention, metal to be plated on the object can be made uniform in thickness by moving the metal block or by removing metal crust on the metal block with a grinder or a cutting tool so that the surface of the metal block to come into contact with the metal brush can always be refreshed. Also, according to this invention, in order that these processes may be conducted more continuously, a grinder or a cutting tool can be brought into contact with metal brush in order to remove troublesome metal particles from the metal brush, which are not plated on the object clinging to the metal brush. As for the type of the grinder or the cutting tool, there is no limitation in particular if only they are able to shave the metal block or the metal brush. Moreover, as for the shape of the metal block, there is also no restriction in particular if only it has a face with which it can come into good contact with the metal brush. This invention will be described below in more detail with reference to the drawings. As shown in Figs. 2(c) and (d), 1 denotes a metal brush; 2 denotes a cylindrical metal bar (Fig. 2(c)) or metal foil (Fig. 2(d)); 3 denotes an object to be plated; 4 denotes a grinder (Fig. 2(c)) or an endless belt type abraser (Fig. 2(d)); and 5 denotes a plated metal layer. The metal layer 5 can be plated mechanically on the object 3 by means of the metal brush 1 in contact with the metal block 2 and the object 3 with the metal brush 1 being rotated as rapidly as its circumferential speed attains about 2000 meters a minute. Also, the metal block 2 can be refreshed continuously by bringing the grinder or the abraser 4 into contact with it. If plating should be conducted with the metal block being not moved or with the grinder/abraser being not in contact with the metal brush, metal particles, having not been plated on the object clinging to the metal brush, cling to the metal block again, and they form a hard, tenacious crust there, whereby not only does it take many hours for plating but also the thickness of plated metal layer would possibly decrease. However, when plating is conducted with the metal block being moved or with a hard metal crust forming on the metal block being removed as this invention teaches, the metal brush can always come into contact with the fresh surface of the metal block; in consequence, there is no afraid of the decrease or the wearing off of plated metal layer. Also, when the grinder or the cutting tool is brought into contact with the metal brush, metal particles having not been plated on the object clinging to the metal brush are removed from the metal brush, and they hardly form such a hard, tenacious crust that uniform plating can be conducted for hours continuously. This invention will be detailed more concretely with reference to the following examples; however, it is never to be construed to be limited by the examples. Example 1 Table 1 shows examples of a metal brush, a metal block, and an object to be plated in combinative use according to this invention. Table 2 shows their outstanding combinations, the plating condition (in terms of the rotation of the metal brush), and the thickness of plated metal layer resulting therefrom. As apparent from Table 2, each of the combinations gives a plated metal layer uniform in thickness. Having a strong adhesion to the object, the plated metal layer does not flake off readily. Metal block (Plating material) Metal brush Object to be plated Aluminium SUS 304 SUS 304 Hard steel wire SUS 430 Copper Fe-42%Ni alloy Copper SUS 304 SUS 304 Hard steel wire SUS 430 SUS 304 Fe-42%Ni alloy Solder Hard steel wire SUS 304 Brass Fe-42%Ni alloy Combination: Metal block + metal brush + object to be plated Rotation of brush Thickness of plated metal Al + Cu + SUS 304 2400 rpm 0.8 µm Cu + Hard steel wire + SUS 430 2700 0.7 Solder + Cu + Fe-42% Ni alloy 2100 1.0 Example 2 While a metal brush, 200 mm across by 100 mm long, planted with lots of 0.25 mm thick hard steel wires is being rotated at 2500 rpm, a copper block, 50 mm thick by 100 mm wide by 200 mm long, is pressed against the brush. Also, a length of SUS 304 stainless steel strip of the thickness 1.0 mm and the width 100 mm moving at the rate 2.0 m/minute is pressed against the brush. The thickness of plated copper layer along the longitudinal direction of the stainless steel strip is shown in Fig. 3, where solid circles indicate the result according to this invention (corresponding to Fig. 2(a)), obtained with the rotating hard steel brush being in contact with a grinder, and open circles indicate the result according to a comparative example, obtained with the rotating hard steel brush being not in contact with the grinder. Example 3 While a metal brush, 300 mm across by 500 mm long, planted with lots of 0.1 mm thick SUS 304 wires is being rotated at 2000 rpm, an aluminium block, 100 mm by 500 mm wide by 400 mm long, is pressed against the brush. Also, a length of Fe-42% Ni alloy strip of the thickness 2.0 mm and the width 500 mm moving at the rate 1.0 m/minute is pressed agaist the brush. The thickness of plated aluminium layer along the longitudinal direction of the alloy strip is shown in Fig.4, where solid circles indicate the result according to this invention (Corresponding to Fig. 2 (b)), obtained with the rotating SUS 304 brush being in contact with an endless belt type abraser, and open circles indicate the result according to a comparative example, obtained with the same brush being not in contact with the abraser. Example 4 While a metal brush, 250 mm across by 100 mm long, planted with lots of 0.2 mm thick hard steel wires is being rotated at 2500 rpm, a cylindrical aluminium bar, 100 mm across by 100 mm long, is pressed against the brush with its circumferential speed at 0.5 m/minute. Also, a length of SUS 304 stainless steel strip of the thickness 1.0 mm and the width 100 mm moving at the rate 1.0 m/minute is pressed against the brush. The thickness of plated aluminium layer along the longitudinal direction of the stainless steel strip is shown in Fig. 5, where solid circles indicate the result according to this invention (corresponding to Fig. 2(c)), obtained with the rotating aluminium bar being in contact with a grinder, and open circles indicate the result according to a comparative example, obtained with the aluminium bar being in contact with the grinder but not rotated. Example 5 While a metal brush, 300 mm across by 500 mm long, planted with lots of 0.1 mm thick SUS 304 stainless steel wires is being rotated at 2000 rpm, a length of copper strip, 2.0 mm thick by 500 mm wide, is pressed against the brush. Also, a length of Fe-42% Ni alloy strip of the thickness 1.5 mm and the width 500 mm is pressed against the brush. The thickness of plated copper layer along the longitudinal direction of the alloy strip is shown in Fig. 6, where solid circles indicate the result according to this invention (Corresponding to Fig. 2(d)), obtained with the copper belt, always in contact with an endless belt type abraser, being moved, and open circles indicate the result according to a comparative example, obtained with the copper belt, always in contact with the endless belt type abraser, being not moved. As seen from the above, the mechanical plating process of this invention is conducted with a metal block, a metal brush, and an object to be plated being in contact with one another with the metal brush in between; therefore, it does not need various tanks and expensive chemical solutions; thus, it is much cheaper than the conventional electroplating or the chemical plating process. Additionally, according to this invention, not only can there be formed a uniform metal layer strongly adhered to an object but also it is possible to eliminate problems in conventional mechanical plating process, such as the brush wire is subject to oxidation, expensive and easy to fall out. Moreover, with the mechanical plating process of this invention, a variety of pure metals or alloys can be plated firmly on top of other metals far cheaper than with conventional processes. Metals thus plated on show such a property of those fully adhered to substrate that there can be produced plated goods superior in platability, solderability, electroconductivity, corrosion resistance, heat resistance, abrasion resistance, and decorability.

Claims: A mechanical plating process, comprising shaving metal off from a pure metal or alloy block (2) and plating an object (3) to be plated with said shaved off metal by the use of at least a single metal brush (1), wherein said metal block (2) and said metal brush (1) are in frictional contact with each other, and said object (3) to be plated and said metal brush (1) are concurrently in frictional contact with each other, characterized by conducting said mechanical plating process while removing small metal particles from said metal brush (1) with a grinder (4) or a cutting tool (4) to remove metal particles remaining on the brush (1) after the brush (1) has brought the shaved off metal particles in contact with the object (3) to be plated. A mechanical plating process comprising shaving metal off from a pure metal or alloy block (2) and plating an object (3) to be plated with said shaved off metal by the use of at least a single metal brush (1), wherein said metal block (2) and said metal brush (1) are in frictional contact with each other, and said object (3) to be plated and said metal brush (1) are concurrently in frictional contact with each other, characterized by continuously conducting said mechanical plating process while moving said metal block (2) in such a way as to always re-fresh the surface of said metal block (2). A mechanical plating process comprising shaving metal off from a pure metal or alloy block (2) and plating an object (3) to be plated with said shaved off metal by the use of at least a single metal brush (1), wherein said metal block (2) and said metal brush (1) are in frictional contact with each other, and said object (3) to be plated and said metal brush (1) are concurrently in frictional contact with each other, characterized by continuously conducting said mechanical plating process while removing metal crust formed on said metal block (2) by the contact of said metal block (2) and said metal brush, with a grinder (4) or a cutting tool (4) so as to re-fresh the surface of said metal block (2). A mechanical plating process according to claim 2 or 3, characterized by conducting said mechanical plating process while removing small metal particles from said metal brush (1) with a grinder (4) or a cutting tool (4) to remove metal particles remaining on the brush (1) after the brush (1) has brought the shaved off metal particles in contact with the object (3) to be plated.

Inventors: IKEGAMI, YUJI, KAMIYA, TAKESHI, KOSHIBA, YOSHIKAZU, TACHINO, NOBORU
Applicants: NIPPON YAKIN KOGYO CO., LTD.
Application year: 1988
Main classification: C23C26
IPC codes: C23C26, B23K20, B23K35