AMINOARYLSULFONIC ACID-PHENOL-FORMALDEHYDE CONDENSATE AND CONCRETE ADMIXTURE COMPRISING THE SAME

Abstract: Aminoarylsulfonic acid-phenol-formaldehyde condensate prepared by polymerizing 20 to 70 parts by weight of a compound of the general formula: R¹SO₃H (I) wherein R¹ is (wherein R is hydrogen or lower alkyl) or or its salt, 10 to 50 parts by weight of a compound of the general formula: wherein R² is hydrogen, lower alkyl, lower alkoxy, hydroxy or carboxy, or its salt, and l0 to 40 parts by weight of formaldehyde, a concrete admixture comprising such condensate for incorporation in fresh cementing composition, and for incorporation in fresh concrete, and a method for preparing cementing composition and for preparing concrete.

Description: The present invention relates to aminoarylsulfonic acid-phenole-formaldehyde condensate (hereinafter referred to as ASPFC), the use thereof as an additive for cementing compositions and concrete admixtures, the process for preparing the same and the concrete admixture comprising the same for incorporation in cementing compositions, for example, in concrete, mortar, cement paste and the like. The concrete admixture which comprises ASPFC mentioned below improves consistency of fresh cementing composition, and further restrains the change of the fluidity such as slump loss with the passage of time. More definitely, when the concrete admixture of this invention is added to the cementing composition, the slump of the cementing composition can be increased without adding water and the cementing composition can be transported without slump loss for a long period of time, and further this concrete admixture facilitates flow rates of fresh cementing composition when the fresh cementing composition is pumped to a desired location during cementing operation. Up to now, although various kinds of concrete admixture are known in the art, they are insufficient in improvement of consistency of fresh cementing composition and in restraining of the change of the fluidity such as slump loss with the passage of time. For example, EP-A-0 099 954 discloses liquifiers for hydraulic binders prepared by the condensation reaction of aromatic sulfonic acid amines, polyamines and formaldehyde. It is therefore an object of the present invention to provide a composition suitable as a concrete admixture which does not possess the disadvantages of the compositions known in the art and to provide a process for the production thereof. The inventors of the present invention have conducted the research work to find out more preferable concrete admixture which possesses improved characteristics in consistency and restraining of the change of fluidity such as slump loss with the passage of time, and have completed the present invention. The object of the present invention is solved by the provision of an aminoarylsulfonic acid-phenol-formaldehyde condensate prepared by polymerizing 20 to 70 parts by weight of 4-aminobenzenesulfonic acid, 10 to 50 parts by weight of phenol and 10 to 40 parts by weight of formaldehyde. Furthermore, the present invention is directed to a process for preparing the aminoarylsulfonic acid-phenol-formaldehyde condensate which comprises polymerizing 20 to 70 parts by weight of 4-aminobenzenesulfonic acid, 10 to 50 parts by weight of phenol and 10 to 40 parts by weight of formaldehyde, and to the use of an aminoarylsulfonic acid-phenol-formaldehyde condensate prepared by polymerizing 20 to 70 parts by weight of a compound of the general formula: R¹SO₃H (I) wherein R¹ is (wherein R¹a is hydrogen or (C₁-C₆)alkyl) or or its salt, 10 to 50 parts by weight of a compound of the general formula: wherein R² is hydrogen, (C₁-C₆) alkyl, (C₁-C₆) alkoxy, hydroxy or carboxy, or its salt, and 10 to 40 parts by weight of formaldehyde as additive for cementing compositions and concrete admixture and to the concrete admixture for incorporation in fresh concrete having good fluidity, which comprises the aforementioned aminoarylsulfonic acid-phenol-formaldehyde condensate. The present invention is additionally directed to use of the aminoarylsulfonic acid-phenol-formaldehyde condensate wherein the condensate is prepared by polymerizing 20 to 70 parts by weight of 4-aminobenzenesulfonic acid, 10 to 50 parts by weight of phenol and 10 to 40 parts by weight of formaldehyde as additive for cementing compositions and concrete admixture, and to the concrete admixture for incorporation in fresh concrete having good fluidity comprising the same, and to the methods for preparing the aforementioned cementing compositions and concrete admixtures. Since ASPFC of the present invention reduces apparently the viscosity of fresh cementing composition to which it is added, it is possible to reduce the unit water content of fresh cementing composition which results in greater compressive strength in the hardened concrete as obtained. In the above and subsequent descriptions of the present specification, the various definitions which the present invention intends to include within the scope thereof are explained in detail as follows. The term "lower" is used to intend a group having 1 to 6 carbon atom(s), unless otherwise provided. Suitable "lower alkyl" may include straight or branched one, having 1 to 6 carbon atom(s), such as methyl, ethyl, propyl, isopropyl, butyl, t-butyl, pentyl and hexyl. Suitable "lower alkoxy" may include straight or branched one such as methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, pentyloxy, isopentyloxy and hexyloxy. ASPFC can be prepared by polymerizing 20 to 70 parts by weight of a compound (I), 10 to 50 parts by weight of a compound (II) and 10 to 40 parts by weight of formaldehyde in an aqueous condition under warming or heating. Now, in order to show the utility of ASPFC of the present invention, the test data of the representative ASPFCs on mortar and concrete are shown in the following. Test 1 Mortar slump test (1) Test Method Consistency was measured by mortar slump test at 20°C, and slump of the mortars containing the test compounds was compared with that of the reference mortar (non-additive). Materials and the mortar composition utilized in the test were 700 g of ordinary Portland cement specified in JIS R 5210, 1960 g of river sand (specific gravity: 2.63, fineness modulus: 2.66) and 339.5 ml of water or an aqueous solution containing 2.8 g of the test compound. The mortars were made by mechanical mixing of ingredients according to the standard method in JIS R 5201. Mortar slump was determined in accordance with JIS A 1101 by using a slump cone of half size of the standard mold (with base 100 mm in diameter, top 50 mm in diameter and the height 150 mm). Air content of the test mortar was measured by gravimetric method. After initial measurement of the slump and air content, the mortar was recovered into the mixing bowl, allowed to stand for 60 minutes and then remixed by using mixing spoon in the bowl. The slump and air content was measured again, as described above. (2) Test Results The test results are given in Table 1. Test compounds (Example Nos.) Slump (cm) Air content (%) 0 min. 60 min. 0 min. 60 min. 1 9.6 8.5 2.7 2.2 2 10.2 7.4 2.2 1.8 3 9.3 7.4 4.1 3.1 4 10.7 7.9 2.8 1.1 5 9.3 6.3 2.4 2.1 6 8.2 5.5 2.5 1.6 7 9.9 6.9 2.2 2.1 8 8.5 5.6 3.0 2.3 9 10.6 8.8 1.5 1.6 10 8.8 6.3 2.4 1.9 11 10.6 8.5 2.2 1.7 12 10.2 7.8 1.6 1.1 13 11.0 8.9 2.1 1.3 14 9.7 6.8 2.3 1.7 15 10.6 10.8 1.8 1.0 16 11.2 9.9 1.5 1.0 17 11.3 10.2 1.0 0.8 18 10.7 10.8 2.0 1.0 19 11.4 8.5 1.6 2.0 20 9.9 9.1 3.5 2.3 21 9.4 9.7 3.2 2.0 22 11.0 10.8 2.2 1.4 23 11.4 9.7 1.1 0.9 24 10.3 7.9 0.7 0.9 25 10.3 7.4 0.5 0.7 26 11.6 8.8 1.2 1.5 27 10.9 6.9 1.5 2.9 28 8.3 4.8 3.5 2.7 29 8.7 5.1 10.9 6.1 30 9.7 6.2 4.0 2.8 31 11.7 10.5 1.9 1.6 32 12.6 11.6 0.3 0.1 33 12.0 10.6 1.2 1.0 34 9.7 7.7 2.9 1.9 35 10.2 8.0 2.0 1.2 36 11.8 9.2 0.2 0.6 37 6.8 3.0 3.8 3.1 38 7.4 5.4 2.0 2.6 39 7.2 3.2 4.0 3.0 Reference (non-additive) 3.5 - 2.7 - Test 2 Concrete test (1) Test Method Consistency of the concrete containing test compounds were compared with that of the plain concrete (non-additive), and slump loss (the time-dependent change of fluidity) of the concrete was compared with that of the reference concrete adjusted to the same initial slump by increasing unit water content. The method utilized in the test was the basic procedure described in the Japan Industrial Standard (JIS) A 6204 for chemical admixtures for concrete. Materials utilized in the test were as follows: Cement: a mixture of ordinary Portland cements specified in JIS R 5210 from three different manufacturers. Fine aggregate: river sand specific gravity: 2.64 fineness modulus: 2.75 Coarse aggregate: crushed stone specific gravity: 2.67 fineness modulus: 6.70 Mix proportions of concrete are shown in Table 2. The concrete was prepared by mixing cement, aggregates and water or water containing a test compound in a forced mixing type mixer for 1.5 minutes on a scale of 30 liters, and was allowed to stand in a mixing plate. Initial slump and the time-dependent change of slump (at every 30 minutes intervals to 1.5 hours) were measured after remixing in the mixing plate. (2) Test Results The results are given in Table 3. As clear from the test results as stated above, ASPFC of the present invention improves consistency of cementing composition (cf. high initial slump) and restrains the slump loss with the passage of time in concrete as compared with the reference. It might be clear from the test results shown in Table 3 that ASPFC much reduced unit water content without air-entraining. Concrete having good fluidity can be prepared by admixing ASPFC (0.01 to 1.0% of cement, preferably 0.1 to 0.6% of cement) with the ordinary concrete. Said ordinary concrete may include cement (5-25%), coarse aggregate (30-60%), fine aggregate (20-50%), water (4-10%), and air entraining agent (0-1% of cement) and/or water-reducing agent (0-1% of cement). Mortar having good fluidity can be prepared by admixing ASPFC (0.01 to 1.0% of cement, preferably 0.1 to 0.6% of cement) with the ordinary mortar. Said ordinary mortar may include cement (15-45 %), water (5-30%), sand (35-75%), and air entraining agent (0-1% of cement) and/or water-reducing agent (0-1% of cement). Cement paste having good fluidity can also be prepared by admixing ASPFC (0.01 to 1.0% of cement, preferably 0.1 to 0.6% of cement) with the ordinary cement paste. Said ordinary cement paste may include cement (20-80%) and water (80-20%). As the cement, there may be mentioned cement currently on the market, such as ordinary portland cement, high-early-strength cement, moderate heat cement, blast-furnace slag cement and fly ash cement, with fly ash, granulated slag powder, siliceous admixtures and the like. The following Examples are given for the purpose of illustrating the preparation of ASPFC of the present invention. Example 1 To a mixture of 4-aminobenzenesulfonic acid (8.66 g) and phenol (4.70 g) in water (30 ml) was added 20% aqueous sodium hydroxide (10.20 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. A weight of the solution was adjusted to 56.00 g with water and then heated. To the solution was added 37% aqueous formaldehyde (8.10 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing. The solution was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (3.26 g) and condensed at 40°C to afford an aqueous solution of the condensate (49.40 g). Ratio (4-aminobenzenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.49 Viscosity of the aqueous solution of the condensate: 8.9 (cP at 25°C, 30%) Molecular weight: Mw: 1976, Mn: 833 Examples 2 to 14 was conducted in a similar manner to that of Example 1. Example 15 To a mixture of 4-aminobenzenesulfonic acid (594.8 g) and phenol (323.2 g) in water (2000.0 ml) was added 20% aqueous sodium hydroxide (704.0 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 3850.0 g with water and then heated. To the solution was added 37% aqueous formaldehyde (557.4 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (252.5 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (4659.9 g). Ratio (4-aminobenzenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.49 Molecular weight: Mw: 4336, Mn: 943 Examples 16 to 23 was conducted in a similar manner to that of Example 15. Example 24 To a mixture of 4-aminobenzenesulfonic acid (17.32 g) and pyrocatechol (11.01 g) in water (60 ml) was added 20% aqueous sodium hydroxide (21.12 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 119.20 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing. Further, 37% aqueous formaldehyde (8.12 g) was added thereto under refluxing and stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (7.72 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (151.30 g). Ratio (4-aminobenzenesulfonic acid:pyrocatechol:formaldehyde): 1:1:3 Ratio (starting monomers:water): 1:2.45 Viscosity of the aqueous solution of the condensate: 36.3 (cP at 25°C, 30%) Molecular weight: Mw: 5832 Example 25 To a mixture of 4-aminobenzenesulfonic acid (34.64 g) and hydroquinone (22.02 g) in water (122 ml) was added 20% aqueous sodium hydroxide (40.92 g) and the mixture was stirred at 50°C. The resulting solution was adjusted to pH 8.03 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 238.40 g with water and then heated. To the solution was added 37% aqueous formaldehyde (32.46 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (25.04 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (295.90 g). Ratio (4-aminobenzenesulfonic acid:hydroquinone:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.52 Viscosity of the aqueous solution of the condensate: 23.9 (cP at 25°C, 30%) Molecular weight: Mw: 4895 Example 26 To a mixture of 3-aminobenzenesulfonic acid (17.32 g) and phenol (9.41 g) in water (55 ml) was added 20% aqueous sodium hydroxide (20.41 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 112.10 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 9.25 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (5.14 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (133.50 g). Ratio (3-aminobenzenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.49 Molecular weight: Mw: 4891, Mn: 1091 Example 27 To a mixture of 2-aminobenzenesulfonic acid (17.32 g) and phenol (9.41 g) in water (54 ml) was added 20% aqueous sodium hydroxide (20.39 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 112.10 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 9.25 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (5.26 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (133.60 g). Ratio (2-aminobenzenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.49 Molecular weight: Mw: 5078, Mn: 1180 Example 28 To a mixture of 2-aminobenzenesulfonic acid (17.32 g) and m-cresol (10.83 g) in water (63 ml) was added 20% aqueous sodium hydroxide (20.30 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 118.30 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (3.08 g) and refluxed for 1 hour (2nd step) to afford an aqueous solution of the condensate (137.60 g). Ratio (2-aminobenzenesulfonic acid:m-cresol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.52 Viscosity of the aqueous solution of the condensate: 82.8 (cP at 25°C, 30%) Example 29 To a mixture of 2-amino-5-methylbenzenesulfonic acid (18.72 g) and phenol (9.41 g) in water (61 ml) was added 20% aqueous sodium hydroxide (20.00 g) and the mixture was stirred at 50°C. The resulting solution was adjusted to pH 7.92 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 118.30 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (8.40 g) and refluxed for 1 hour (2nd step) to afford an aqueous solution of the condensate (142.90 g). Ratio (2-amino-5-methylbenzenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.53 Viscosity of the aqueous solution of the condensate: 13.8 (cP at 25°C, 30%) Molecular weight: Mw: 11870 Example 30 To a mixture of 4-amino-1-naphthalenesulfonic acid (22.33 g) and phenol (9.41 g) in water (73 ml) was added 20% aqueous sodium hydroxide (19.90 g) and the resulting solution was adjusted to pH 8.1 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 134.20 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (11.50 g) and refluxed for 1 hour (2nd step) to afford an aqueous solution of the condensate (162.10 g). Ratio (4-amino-1-naphthalenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.61 Molecular weight: Mw: 2175 Example 31 To a mixture of 4-aminobenzenesulfonic acid (303.1 g) and phenol (164.7 g) in water (115 ml) was added 20% aqueous sodium hydroxide (357.0 g) and the mixture was stirred at 70°C. The resulting solution was adjusted to pH 7.65 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 990.7 g with water and then heated. To the solution was added 37% aqueous formaldehyde (284.0 g) under refluxing and the reaction mixture was stirred for 2 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (184.4 g) and refluxed for 1 hour (2nd step) to afford an aqueous solution of the condensate (1459.1 g). Ratio (4-aminobenzenesulfonic acid:phenol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:0.98 Molecular weight: Mw: 3572, Mn: 918 Examples 32 to 35 was conducted in a similar manner to that of Example 31. Example 36 To a mixture of 4-aminobenzenesulfonic acid (17.32 g) and m-cresol (10.80 g) in water (173.2 ml) was added 20% aqueous sodium hydroxide (20.45 g) and the mixture was stirred at 85°C. The resulting solution was adjusted to pH 7.42 with 0.1N aqueous sodium hydroxide and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (2.87 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (240.90 g). Ratio (4-aminobenzenesulfonic acid:m-cresol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:5.23 Viscosity of the aqueous solution of the condensate: 8.8 (cP at 25°C, 30%) Molecular weight: Mw: 8981, Mn: 858 Example 37 To a mixture of 3-aminobenzenesulfonic acid (17.32 g) and salicylic acid (13.80 g) in water (52 ml) was added 20% aqueous sodium hydroxide (40.60 g) and the resulting solution was adjusted to pH 8.20 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 131.30 g with water and then heated. To the solution was added 37% aqueous formaldehyde (16.23 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.2 with 20% aqueous sodium hydroxide (1.03 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (148.60 g). Ratio (3-aminobenzenesulfonic acid:salicylic acid:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.26 Viscosity of the aqueous solution of the condensate: 4.1 (cP at 25°C, 21.5%) Molecular weight: Mw: 1110, Mn: 562 Example 38 To a mixture of 4-aminobenzenesulfonic acid (8.65 g) and guaiacol (6.20 g) in water (117.3 ml) was added 20% aqueous sodium hydroxide (10.24 g) and the mixture was stirred at 80°C. The resulting solution was adjusted to pH 7.51 with 0.1N aqueous sodium hydroxide and then heated. To the solution was added 37% aqueous formaldehyde (8.12 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide (9.39 g) and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate (93.30 g). Ratio (4-aminobenzenesulfonic acid:guaiacol:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:6.56 Viscosity of the aqueous solution of the condensate: 9.3 (cP at 25°C, 30%) Molecular weight: Mw: 1215, Mn: 432 Example 39 To a mixture of 4-aminobenzenesulfonic acid (8.65 g) and salicylic acid (6.91 g) in water (24 ml) was added 20% aqueous sodium hydroxide (20.12 g) and the mixture was stirred at 75°C. The resulting solution was adjusted to pH 7.58 with 0.1N aqueous sodium hydroxide. The weight of the solution was adjusted to 73.80 g with water and then heated. To the solution was added 37% aqueous formaldehyde (8.12 g) under refluxing and the reaction mixture was stirred for 7.5 hours under refluxing (1st step). The mixture was cooled to room temperature, adjusted to pH 11.0 with 20% aqueous sodium hydroxide and refluxed for 3 hours (2nd step) to afford an aqueous solution of the condensate. Ratio (4-aminobenzenesulfonic acid:salicylic acid:formaldehyde): 1:1:2 Ratio (starting monomers:water): 1:2.27 Viscosity of the aqueous solution of the condensate: 5.7 (cP at 25°C, 30%) Molecular weight: Mw: 1464, Mn: 552

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, IT, LI, NL, SE Aminoarylsulfonic acid-phenol-formaldehyde condensate prepared by polymerizing 20 to 70 parts by weight of 4-aminobenzenesulfonic acid, 10 to 50 parts by weight of phenol and 10 to 40 parts by weight of formaldehyde. Process for preparing aminoarylsulfonic acid-phenol-formaldehyde condensate which comprises polymerizing 20 to 70 parts by weight of 4-aminobenzenesulfonic acid, 10 to 50 parts by weight of phenol and 10 to 40 parts by weight of formaldehyde. Use as additive for cementing compositions and concrete admixtures of aminoarylsulfonic acid-phenol-formaldehyde condensate prepared by polymerizing 20 to 70 parts by weight of a compound of the general formula: R¹SO₃H (I) wherein R¹ is (wherein R¹a is hydrogen or C₁-C₆ alkyl) or or its salt, 10 to 50 parts by weight of a compound of the general formula: wherein R² is hydrogen, C₁-C₆ alkyl,C₁-C₆ alkoxy, hydroxy or carboxy, or its salt, and 10 to 40 parts by weight of formaldehyde. Use of the aminoarylsulfonic acid-phenol-formaldehyde condensate according to claim 3 wherein the condensate is prepared according to claim 2. Concrete admixture for incorporation in fresh concrete having good fluidity, which comprises aminoarylsulfonic acid-phenol-formaldehyde condensate prepared as set out in claim 3. The concrete admixture for incorporation in fresh concrete having good fluidity according to claim 5 wherein the aminoarylsulfonic acid-phenol-formaldehyde condensate is prepared according to claim 2. A method for preparing cementing composition or concrete admixtures having good fluidity which comprises admixing with the ordinary cementing composition or concrete admixtures an aminoarylsulfonic acid-phenol-formaldehyde condensate prepared as set out in claim 3. The method according to claim 7 wherein the aminoarylsulfonic acid-phenol-formaldehyde condensate is prepared according to claim 2. Claims for the following Contracting State : ES Process for preparing aminoarylsulfonic acid-phenol-formaldehyde condensate which comprises polymerizing 20 to 70 parts by weight of 4-aminobenzenesulfonic acid, 10 to 50 parts by weight of phenol and 10 to 40 parts by weight of formaldehyde. A method for preparing cementing composition or concrete admixtures having good fluidity which comprises admixing an aminoarylsulfonic acid-phenol-formaldehyde condensate prepared by polymerizing 20 to 70 parts by weight of a compound of the general formula: R¹SO₃H (I) wherein R¹ is (wherein R¹a is hydrogen or C₁-C₆ alkyl) or or its salt, 10 to 50 parts by weight of a compound of the general formula: wherein R² is hydrogen, (C₁-C₆) alkyl, (C₁-C₆) alkoxy, hydroxy or carboxy, or its salt, and 10 to 40 parts by weight of formaldehyde with the ordinary cementing composition or concrete admixtures. The method according to claim 2 wherein the aminoarylsulfonic acid-phenol-formaldehyde condensate is prepared according to claim 1.

Inventors: ADACHI, TOSHIKAZU, FURUHASHI, TAKAHIRO, KAWADA, KAZUSHIGE, TAHARA, SUSUMU, TAKAHASHI, YUJI, TAKEUCHI, TORU, TERAJI, TSUTOMU
Applicants: FUJISAWA PHARMACEUTICAL CO., LTD.
Application year: 1988
Main classification: C08G14
IPC codes: C04B24, C08G14