POLYMERIC COMPOSITION

Abstract: A polymeric composition comprising: an olefin polymer; a hydrogenated block copolymer comprising at least two polymeric block containing predominantly monoalkenyl aromatic hydrocarbon monomer units and at least one block containing predominantly hydrogenated, conjugated diolefin monomer units; and an LLDPE. The weight ratio of block copolymer to LLDPE in the polymeric composition will be within the range from 5:1 to 1:3. Shaped structures prepared with the polymeric composition will generally exhibit good clarity and good impact strength.

Description: This invention relates to a polymeric composition. More particularly, this invention relates to a polymeric composition comprising an olefin polymer and a selectively hydrogenated triblock copolymer. Olefin polymers and compositions comprising such polymers are, of course, well known in the prior art. Both the polymers and various compositions comprising such polymers are frequently used in molding applications to prepare molded articles as well as in the preparation of films, sheets, textile coatings and the like. Use of the various olefin polymers in many of these applications is, however, frequently restricted due to the poor impact resistance of the products thus produced. Use of the olefin polymers in many of these applications is also limited due to poor tensile strength, poor clarity in the various products produced and whitening or "blushing" of certain such products when subjected to stress or impact. Heretofore, several methods have been proposed for use in an effort to avoid one or more of these problems. For example, it has heretofore been proposed to incorporate a selectively hydrogenated triblock copolymer, having terminal polymeric blocks of a vinyl aromatic monomer and a central polymeric block prepared originally with a conjugated diolefin and subsequently hydrogenated, into a polymeric composition comprising one or more olefin polymers primarily for the purpose of improving impact resistance and to reduce whitening or "blushing" such as taught in U.S. Patent 3,299,174. The improved impact resistance is, however, apparently, achieved at the expense of losing other properties such as stiffness, particularly when polypropylene is the olefin polymer used. It has, therefore, been proposed to incorporate crystalline polyethylene into a polymeric composition comprising propylene and a hydrogenated block copolymer so as to achieve a better balance between stiffness and impact resistance as is taught in U.S. Patent 4,178,328. It is also known in the prior art to incorporate a relatively high polymerized styrene content linear or radial block copolymer comprising styrene polymeric blocks and butadiene polymeric blocks into a composition comprising crystalline polypropylene to produce resin products having a pearl-like pattern or luster and excellent impact strength and hinging properties as taught in U.S. Patent 4,499,238. It is further known in the prior art to add a copolymer of ethylene and vinyl acetate to a polymeric composition comprising a hydrogenated block copolymer of an aromatic vinyl compound and a conjugated diene and polypropylene to produce products having improved softness, transparency, high temperature strength and molding characteristics as taught in U.S. Patent 4,588,777. As is well known in the prior art, incorporation of a hydrogenated linear or radial block copolymer comprising two or more blocks containing predominantly aromatic hydrocarbon monomers and at least one polymeric block containing predominantly conjugated diolefin monomers into a polymeric composition comprising one or more olefin polymers will, indeed, solve several of the problems which have hampered the various products produced from olefin polymers. Polymeric compositions comprising an olefin polymer and a linear or radial block copolymer comprising at least two polymeric blocks containing predominantly monoalkenyl aromatic hydrocarbon monomer units and at least one polymeric block containing predominantly conjugated diolefin monomer units have not, however, been widely accepted commercially, apparently due to the relatively high cost of the block copolymer component. The need, then, for a polymeric composition comprising one or more olefin polymers, the products from which will be free from one or more of the aforementioned deficiencies, which polymeric composition can be produced at a lower cost is believed to be readily apparent. It is therefore an object of this invention to provide a polymeric composition comprising one or more olefin polymers, the products from which will exhibit good properties, and which can be produced at a lower cost than when a block copolymer comprising at least two polymer blocks of a monoalkenyl aromatic hydrocarbon and at least one polymer block prepared with a conjugated diolefin monomer, and subsequently hydrogenated, is used as the sole modifier in said composition. More particularly it is an object of this invention to provide a composition which can be molded into shaped articles having good impact resistance, and to provide such a polymeric composition which can be used to produce shaped articles having good tensile strength. It is yet another object of this invention to produce such a polymeric composition which can be used to manufacture shaped articles having a reduced tendency to whiten or "blush". It is still a further object of this invention to provide such a polymeric composition which can be produced at a lower cost than similar compositions which may be used to produce shaped articles having the same or nearly the same properties. It is an even further object of this invention to provide such a polymeric composition which can be used to produce shaped articles, generally, having good clarity. The foregoing and still other objects and advantages of the present invention will become apparent from the description set forth hereinafter and the examples included therein. As result of extensive research and experimentation it was surprisingly found, that the before-mentioned and other objects and advantages are accomplished with a polymeric composition comprising: an olefin polymer; a selectively hydrogenated block copolymer comprising at least two polymeric blocks containing predominantly polymerized monoalkenyl aromatic hydrocarbon monomer units and at least one polymeric block containing predominantly polymerized conjugated diolefin monomer units which are subsequently hydrogenated; and a linear low density polyethylene (LLDPE). As used herein in connection with block copolymer composition, the recitation "predominantly" is intended to mean that the recited monomer unit constitutes at least 85 wt% of the polymer block. The remaining monomer units may be any monomer copolymerizable with the specified monomer including the monomer or monomers contained in other polymeric blocks of the block copolymer. The olefin polymer will be the predominant polymeric component in the polymeric composition while the block copolymer and the LLDPE will be combined and used as a modifier at modifier concentrations. In general, shaped articles produced from the polymeric composition of this invention will exhibit good impact resistance, good tensile strength, good clarity and a reduced whitening or "blushing" tendency and will, generally, also exhibit good oxidation and thermal stability. As is well known in the prior art, "blushing" is the tendency of a shaped article to whiten in a stressed area when the article is subjected to stress, particularly impact or flexing stresses. In general, any of the olefin polymers known in the prior art to be useful in the preparation of shaped articles can be used in the polymeric composition of this invention. Suitable olefin polymers, then, include homopolymers of alpha olefins having from 2 to 10 carbon atoms per molecule, copolymers of such alpha olefins and copolymers of such alpha olefins and one or more other monomers copolymerizable therewith. Other monomers copolymerizable with such alpha olefins include, but are not necessarily limited to, vinyl esters such as vinyl acetate, acrylic and methacrylic acid esters such as methylacrylate and methylmethacrylate, ethylenically unsaturated carboxylic acids such as acrylic and methylacrylic acids. As is well known in the prior art, olefin polymers, particularly polymers of olefins containing 3 or more carbon atoms per molecule may exhibit atactic, syndiotactic and/or isotactic structures. In general, polymers containing any combination of these structures are useful in the polymeric composition of the present invention. The invention is, however, most effective when the olefin polymer exhibits a crystallinity of at least 35%. Olefin copolymers exhibiting this degree of crystallinity are, of course, well known in the prior art and such copolymers will exhibit significantly improved properties when used in the polymeric composition of this invention. The results realized with the modifier useful in the composition of this invention are even further improved when the olefin polymer comprises at least about 40% crystalline structure and such olefin polymers are, therefore, most preferred for use in the polymeric composition of this invention. Polymers of this type may be prepared with the methods summarized in U.S. Patent 3,299,174. In general, any of the selectively hydrogenated block copolymers comprising at least two polymeric blocks containing predominantly polymerized monoalkenyl aromatic hydrocarbon monomer units and at least one polymeric block containing predominantly polymerized conjugated diolefin monomer units, which are hydrogenated after incorporation into the polymer, known in the prior art may be used as a component in the polymer composition of this invention. According to specific embodiments the monoalkenyl aromatic hydrocarbon monomer may be selected from styrene, alpha methylstyrene, vinyl toluene, vinyl naphthalene and more preferably styrene, and the conjugated diolefin monomer may be selected from e.g. 1,3-butadiene, isoprene and the like, while 1,3-butadiene is preferred. Suitable hydrogenated block copolymers may be prepared by hydrogenating a block copolymer prepared in accordance with techniques well known in the prior art such as those described in U.S. Patent Nos. 3,231,635; 3,265,765; 3,322,856; 4,426,495 and 4,444,953. Particularly, block copolymers which may be hydrogenated to form the hydrogenated block copolymers useful in the polymeric composition of this invention will have one of the following general formulae: B x -(A-B) y -A z and [B x′ -(A-B) y′ -A z′ ] n -Z wherein A and B are as defined in the aforementioned U.S. Patent Nos. 3,231,635; 2,265,765; 3,322,856; 4,391,949 and 4,444,953; x and z are, independently, integers equal to 0 or 1; y is a whole number from 1 to 25; provided, however, that z + y ≧ 2 ; x' and z' are independently, integers ranging from 0 to 1; y' is a whole number from 1 to 25; n is a whole number from 2 to 30; and Z is coupling agent nucleus of a star-shaped or linear block copolymer. In general, each polymeric block A may have the same or a different weight average molecular weight within the range from 4,000 to 50,000 and each polymeric block B may have the same or a different weight average molecular weight within the range from 10,000 to 200,000. In a preferred embodiment, each polymeric block A will have approximately the same weight average molecular weight within the range from 5,000 to 10,000 and each polymeric block B will have approximately the same weight average molecular weight within the range from 25,000 to 100,000. In general, the block copolymers useful in the present invention may be hydrogenated using any of the methods known in the prior art being suitable for such hydrogenation. In general, the conditions used to hydrogenate the block copolymers useful in this invention will be selected to insure that at least 50%, preferably at least 80% and most preferably at least 95% of the ethylenic unsaturation remaining in the conjugated diolefin polymer blocks after preparation is saturated as a result of the hydrogenation. The hydrogenation conditions will also be selected so as to insure that less than 20%, preferably less than 10% and most preferably less than 5% of the aromatic unsaturation in the monoalkenyl aromatic hydrocarbon polymer blocks is hydrogenated. Suitable hydrogenation methods involve the use of a suitable catalyst comprising a Group VI or Group VIII metal atom. Suitable catalysts are described in U.K. Patent Specification No. 1,030,306, and in U.S. Patent No. 3,700,633. A particularly preferred method for selectively hydrogenating the block copolymers useful in this invention is the process described in the aforementioned U.S. Patent No. 3,700,633. In this process, selective hydrogenation is accomplished in the same solvent as is used to effect polymerization with a catalyst prepared by reacting an aluminum alkyl with a nickel or cobalt carboxylate or alkoxide. In general, hydrogenation is accomplished at a temperature within the range of from 25 °C to 175 °C at a hydrogen partial pressure below 345 bar (5,000 psig) and usually within the range from 17 bar (250 psig) to 103 bar (1,500 psig). In general, the use of lower temperatures and lower hydrogen partial pressures will reduce the amount of aromatic unsaturation that is hydrogenated. In general, any of the linear low density polyethylenes (LLDPE) known in the prior art to be useful as a modifer in a polymeric composition may be used as a modifier in the polymeric composition of this invention. Such LLDPE's are taught, for example, in U.S. Patent Nos. 4,430,476; 4,476,274; 4,495,323 and 4,560,727. Interestingly, it is within the scope of the teaching of each of these patents to use the LLDPE in combination with a copolymer comprising polymerized monoalkenyl aromatic hydrocarbon monomer units and polymerized conjugated diolefin monomer units. Moreover, the use of block copolymers comprising at least one polymeric block containing predominantly polymerized monoalkenyl aromatic hydrocarbon monomer units and at least one polymeric block containing predominantly polymerized conjugated diolefin monomeric units is specifically taught in three of these patents; viz., U.S. Patent Nos. 4,430,476; 4,495,323 and 4,560,727. The conjugated diolefin polymer block may be hydrogenated in the composition taught in U.S. Patent No. 4,430,476 and is hydrogenated in the composition taught in U.S. Patent No. 4,560,727. In general, the linear low density polyethylenes useful in the polymeric composition of the present invention will have melt indexes between 0.1 and 50 g/10 min as determined by ASTM D1238 (conditions FR-190/2.16) and a density within the range from 0.90 to 0.94 x10³ kg/m³ . The best balance as between impact resistance and clarity is, however, generally realized with LLDPE's having densities of less than 0.92 x10³ kg/m³. LLDPE's having densities within this range are, therefore, preferred. Moreover, the compositions are most readily prepared with LLDPE's having melt indexes above 10 g/10 min. LLDPE's having melt indexes above 10 g/10 min, as determined by ASTM D1238 (conditions FR-190/2.16) are, therefore, preferred. The LLDPE's useful in the polymeric composition of this invention will, generally, have crystalline melting points above 100 °C. As is well known, LLDPE is, actually, a random copolymer of ethylene and a minor amount, generally less than 20 mole%, preferably less than 15 mol% of an alpha-olefin having 3 to 15 carbon atoms, preferably 3 to 10 carbon atoms and most preferably 4 to 8 carbon atoms. The LLDPE's useful in the present invention may be prepared using any of the processes well known in the prior art such as those described in the book "Polyethylene" by Raff and Allison, Interscience Publishers (1956) and in Kirk-Othmer Encyclopedia of Science and Technology, Volume 14, pages 242-282 (2nd ed., 1967). The hydrogenated block copolymer and LLDPE will each be added to the polymeric composition at a concentration within the range from 2 to 15 parts, by weight, per 100 parts, by weight olefin polymer in the composition. Moreover, the weight ratio of hydrogenated block copolymer to LLDPE will be within the range from 5:1 to 1:3 and preferably will be within the range from 1:1.5 to 1.5:1. Most preferably, the weight ratio of hydrogenated block copolymer to LLDPE will be 1:1. In general, any of the techniques known in the prior art for blending polymeric components may be used to combine the polymeric components of the polymeric composition of this invention. Suitable blending techniques, then, include solution blending, solid state physical admixture, molten state admixture, extrusion admixture and roll milling. Of these, solution blending will, generally, produce the most uniform blend, however, mixing in the molten state with equipment such as a Banbury mixers, extruders or roll mills will be more convenient. In general, molten phase admixture will be accomplished at temperatures within the range from 140 °C to 270 °C but higher and lower temperatures may, in some cases at least, be operable. The polymer compositions of this invention may be used in any of the applications for which olefin polymers are known to be useful. Such uses include the production of molded objects, mechanical goods and extruded materials. The polymeric compositions of this invention may be used in injection molding operations, blow molding operations and compression molding operations. The polymeric compositions of this invention may also be extruded or coextruded to produce films, sheets, textile coatings, pipes, wire coatings and fibers. Depending upon the particular application or end use in which the polymeric composition of this invention is to be used, it may be compounded with other components known in the art including synthetic and natural reinforcing fillers such as carbon black, asbestos and fibers; pigments such at titanium dioxide, iron blue, cadmium pigments, chrome yellow, molybdate orange, ultramarine blue, molybdate red, zinc chromate, ultramarine green, various acid dyes, basic dyes, anthraquinones, Red Lake C, Red 23, benzidine yellow, benzidine orange and carbon blacks; various plasticizers; antiblocking agents; antioxidants; lubricants; flame retardants. In general, these materials, when used, will be used at effective concentrations well known in the prior art. Moreover, these materials may be added to the polymeric composition using techniques well known in the prior art. In a preferred embodiment of the present invention, a crystalline copolymer containing from 97 to 94 wt% polymerized propylene and from 6 to 3 wt% polymerized ethylene having a flow rate as determined using ASTM D1238 (conditions FR-230/2.16) within the range from 0.5 to 50 g/10 min. will be modified by combining it with from 2.5 to 10 parts, by weight, per 100 parts, by weight, of said copolymer of propylene and ethylene, of a hydrogenated block copolymer comprising 2 polystyrene blocks, each styrene block having a weight average molecular weight within the range from 5,000 to 10,000 and one polybutadiene block, which polybutadiene block will be hydrogenated after preparation, each polybutadiene block having a weight average molecular weight within the range from 25,000 to 100,000 and with from 2.5 to 10 parts, by weight, per 100 parts, by weight of said copolymer of propylene and ethylene, of an LLDPE having a melt index as determined by ASTM D1238 (conditions FR-190/2.16) greater than 10g/10 min. and a density less than 0.92 g/cc. In the preferred embodiment, the copolymer of propylene and ethylene will be at least 40% crystalline. In a preferred embodiment, preparation of the conjugated diolefin block will be controlled such that from 30 to 55 mol% of the conjugated diolefin monomer polymerizes via 1,2-addition and from 45 to 70 mole% of the conjugated diolefin polymerizes via 1,4-addition. In the preferred embodiment, the hydrogenation of the block copolymer will be accomplished such that at least 80% and most preferably at least 95% of the initial ethylenic unsaturation in the butadiene polymeric block is hydrogenated and such that less than 5% of the aromatic unsaturation in the styrene polymeric blocks is hydrogenated. In the preferred embodiment, the weight ratio of hydrogenated block copolymer to LLDPE will be within the range from 1:1.5 to 1.5:1 and in a most preferred embodiment, the weight ratio of hydrogenated block copolymer to LLDPE will be 1:1. In the preferred embodiment, the polymeric components will be combined in the molten state using suitable mixing equipment such as a Banbury mixer or a twin screw extruder at a temperature within the range from 175 °C to 250 °C. The invention will be illustrated by reference to the following examples. It will be appreciated, however, that the examples are presented solely for purposes of illustration and should not be construed as limiting the invention. Example 1 In this Example, five polymer compositions, three of which were within the scope of this invention, were prepared with three different propylene polymers and then shaped into disks 63.5 mm (2½ in.) in diameter and 3.2 mm (1/8 in.) thick using injection molding. Each of the polymeric compositions was prepared by blending the polymeric components in a twin screw extruder. The first three of these polymeric compositions contained 15 wt% of a modifier comprising equal weights of (1) a hydrogenated block copolymer comprising 2 blocks of polystyrene and a single block of hydrogenated polybutadiene and (2) an LLDPE having a density of 0.918 g/cc. Each of the polystyrene blocks of the block copolymer had a weight average molecular weight of 10,000 while the hydrogenated polybutadiene block had a weight average molecular weight of 47,000. The LLDPE had a melt index, as previously defined of about 1 g/10 min. The first of these three polymer compositions, which is hereinafter referred to as composition 1, was prepared with a propylene homopolymer having a flow rate as previously defined of 5 g/10 min.; the second of these compositions, hereinafter referred to as Composition 2, was prepared with a sequential impact copolymer comprising 91.5 wt% polymerized propylene and 8.5 wt% polymerized ethylene having a flow rate of 5 g/10 min.; and the third of these compositions, hereinafter referred to as Composition 3, was prepared with a random copolymer comprising 96% polymerized propylene and 4 wt% polymerized ethylene having a flow rate of 4 g/10 min. The fourth of the five compositions, which is hereinafter referred to as Composition 4, was prepared with a propylene copolymer identical to that used in Composition 3 and contained 15 wt% of a commercially available impact modifier which was a copolymer comprising 50 wt% of high density polyethylene and 50 wt% of EPDM. The fifth of the five compositions, which is hereinafter referred to as Composition 5, was prepared with a propylene copolymer identical to that used in Composition 3 and contained 15 wt% of a block copolymer identical to that used in Compositions 1-3. After preparation, the disks were then visually evaluated for clarity and tested for impact resistance using the Gardner Impact Test Procedure (without ring) at -10 °C. The disks were also visually evaluated for blushing after impact. The results obtained with each of the five compositions are summarized in the following Table: Composition Clarity Impact Strength, in N Blushing After Impact 1 Clear 216 Moderate 2 Cloudy >1798 Very severe 3 Clear 1025 Very slight 4 Cloudy 598 Severe 5 Clear 701 Very slight As will be apparent from the data summarized in the preceding Table, the impact resistance of the disk prepared with Composition 3, which contained the mixed modifier of this invention, was superior to that of the disks prepared with Compositions 4 and 5, which contained prior art impact modifiers, while the other tested properties, clarity and blush resistance were at least as good. As also will be apparent from the data summarized in the preceding Table, the effectiveness of the mixed modifier used in the composition of this invention varies with the particular olefin polymer used in the composition. For example, when the composition was prepared with a sequential impact copolymer, Composition 2, excellent impact resistance was realized but both clarity and blush resistance were generally lacking. The use of pigments could, however, offset the clarity deficiency thereby permitting use of this composition to manufacture shaped articles having good impact strength. The impact resistance of the disk prepared with composition 1 is, of course, low but the value actually realized is a significant improvement over the impact resistance exhibited by the polypropylene homopolymer alone. The balance of impact resistance and clarity appears, from the data summarized in the preceding Table, to be best when the olefin (polypropylene) polymer is a random copolymer containing a relatively minor amount (<10 wt%) of a polymerized comonomer, in this case ethylene. Example 2 In this Example, six polymeric compositions, three of which compositions are within the scope of this invention were prepared. All six polymeric compositions were prepared with a propylene random copolymer containing 96 wt% polymerized propylene and 4 wt% polymerized ethylene having a flow rate as previously defined of 10 g/10 min. The three compositions within the scope of this invention contained 12.5 wt% of combined hydrogenated block copolymer and LLDPE. The hydrogenated block copolymer actually used in these compositions had two polystyrene blocks, each with a molecular weight of 7,200 and a single hydrogenated polybutadiene block having a molecular weight of 34,000. Before hydrogenation, the polybutadiene had 38% 1,2-enchainment and 62% 1,4-enchainment. The LLDPE had a density of 0.917 and a melt index, as previously defined, of 25 g/10 min. The first of these compositions, hereinafter referred to as Composition 6, contained the hydrogenated block copolymer and LLDPE in a weight ratio of 3:1 (the composition contained 9.4 wt% of hydrogenated block copolymer and 3.1 wt% LLDPE). The second of these compositions, hereinafter referred to as Composition 7, contained the hydrogenated block copolymer and LLDPE in a weight ratio of 1:1 (the composition contained 6.25 wt% of each). The third of these compositions, hereinafter referred to as Composition 8, contained the hydrogenated block copolymer in a weight ratio of 1:3 (the composition contained 3.1 wt% hydrogenated block copolymer and 9.4 wt% LLDPE). The fourth of the six compositions, hereinafter referred to as Composition 9, contained 87.5 wt% of the propylene copolymer and 12.5 wt% of a hydrogenated block copolymer identical to that used in Compositions 6-8. The fifth of the six compositions, hereinafter referred to as Composition 10, contained 87.5 wt% of the propylene copolymer and 12.5 wt% of an LLDPE identical to that used in Compositions 6-8. The sixth of the six compositions, hereinafter referred to as Composition 11, was simply the propylene copolymer without an impact modifier of any kind. After preparation of the polymeric compositions, at least a portion of each was shaped into at least one plaque having a thickness of 0.15 cm (0.06 in.) and the plaques then tested for haze using ASTM procedure D-1003 and the Gardner Impact Strength was determined using the procedure summarized in Example 1. The results actually obtained with each composition are summarized in the following Table: Composition Haze Impact Strength, in N 6 34 1033 7 35 1618 8 46 539 9 47 1573 10 61 67 11 35 33 As will be apparent from the data summarized in the preceding Table, polymeric compositions comprising an olefin polymer, particularly a propylene polymer, produced shaped articles having good impact strengths when the polymeric composition also contained a hydrogenated block copolymer and LLDPE in a weight ratio within the range from 3:1 to 1:3 (Compositions 6-8) when compared to shaped articles prepared with the same olefin polymer from a composition containing only LLDPE as a modifier (Composition 10) or without a modifier (Composition 11). In fact, the composition containing a 50-50 blend of the hydrogenated block copolymer and LLDPE (Composition 7) resulted in an impact strength at least as good as that for a composition containing what was, heretofore, believed to be the best modifier (Composition 9) with better haze values. The raw materials cost for the blend is, of course, substantially lower than the cost of an equal amount of the hydrogenated block copolymer. Example 3 In this Example, eight polymeric compositions, all within the scope of this invention, were prepared. All eight were prepared with a propylene random copolymer identical to that used in the polymeric compositions prepared in Example 2. The first seven of these eight polymeric compositions were prepared with a selectively hydrogenated styrene-butadiene-styrene block copolymer identical to that used in Compositions 6-8 of Example 2. Each of these seven compositions was prepared with a different LLDPE. These seven compositions are hereinafter identified as Compositions 12-18. The eighth of these compositions was prepared with a selectively hydrogenated styrene-butadiene-styrene block copolymer identical to that used in Compositions 1-3 of Example 1. The eighth of these compositions was also prepared with a LLDPE identical to that used in Composition 18. The eight of these compositions is hereinafter referred to as Composition 19. Each of the eight compositions contained 85 wt% of the random copolymer, 7.5 wt% of the block copolymer and 7.5 wt% LLDPE. After preparation, at least a portion of each composition was shaped into at least one disk 63.5 mm (2½ in.) in diameter and 3.2 mm (1/8 in.) thick using injection molding techniques. After preparation, the disks were visually observed for clarity and ranked on a four point scale wherein 1 was assigned to those disks having the best clarity. The Gardner impact strength was also determined for each disk using the procedure summarized in Example 1. The results obtained with each composition as well as the density and melt index of the LLDPE used in composition are summarized in the following Table: Composition No. LLDPE density, kg/m³ LLDPE Ml, g/10 min Clarity Impact Strength, in N 12 0.918 x 10³ 3.2 1.5 >1798 13 0.926 12. 3 >1798 14 0.926 50. 3 >1798 15 0.934 5.8 4 >1798 16 0.918 1.0 1.5 >1798 17 0.924 20. 3 >1798 18 0.917 25. 1 >1798 19 0.917 25. 2 >1798 As will be apparent from the data summarized in the preceding Table, all of the modifiers tested significantly improved the impact strength of the shaped products. Best clarity, however, was obtained when the composition contained an LLDPE having a density less than 0.920 x10³ kg/m³ (cf. Compositions 12, 16, 18 and 19) and also when the LLDPE had a high melt index (cf. Composition 18). The somewhat poorer clarity obtained with composition 19 is attributed to the higher molecular weight of the block copolymer used, and particularly the molecular weight of the polystyrene blocks. While the present invention has been described and illustrated by reference to particular embodiments thereof, it will be appreciated by those of ordinary skill in the art that the same may lend itself to variations not necessarily described or illustrated herein.

Claims: Claims for the following Contracting States : BE, DE, FR, GB, IT, NL, SE A polymeric composition comprising: (a) 100 parts by weight of an olefin polymer, (b) 2 to 15 parts by weight of a selectively hydrogenated block copolymer comprising at least two polymeric blocks containing at least 85 wt% polymerized monoalkenyl aromatic hydrocarbon monomer units and at least one polymeric block containing at least 85 wt% polymerized, hydrogenated diolefin monomer units, and (c) 2 to 15 parts by weight of LLDPE, the weight ratio of hydrogenated block copolymer to LLDPE being within the range from 5:1 to 1:3. The polymeric composition of Claim 1 wherein said olefin polymer is a propylene polymer. The polymeric composition of Claim 2 wherein the propylene polymer is a random copolymer. The polymeric composition of Claim 3 wherein said copolymer is a copolymer of polymerized propylene and polymerized ethylene comprising from 3 to 6 wt% ethylene monomer units. The polymeric composition of Claim 1 wherein the weight ratio of block copolymer to LLDPE is within the range from 1:1.5 to 1.5:1. The polymeric composition of Claim 1 wherein said monoalkenyl aromatic hydrocarbon monomer unit is a styrene monomer unit and said conjugated diolefin monomer unit is a butadiene monomer unit. The polymeric composition of Claim 1 wherein said polymeric blocks containing at least 85 wt% monoalkenyl aromatic hydrocarbon monomer units have a weight average molecular weight within the range from 5,000 to 10,000 and said polymeric block containing at least 85 wt% hydrogenated diolefin monomeric units has a weight average molecular weight within the range from 25,000 to 100,000. The polymeric composition of Claim 7 wherein said LLDPE has a melt index above 10 g/10 min. and a density less than 0.92 x10³ kg/m³. The polymeric composition of Claim 6 wherein said olefin polymer is a random copolymer of polymerized propylene and polymerized ethylene containing less than 10 wt% polymerized ethylene and having a flow rate within the range from 0.5 to 50 g/10 min. The polymeric composition of Claim 9 wherein said copolymer is at least 40% crystalline. Claims for the following Contracting State : ES Process for the preparation of a polymeric composition comprising 100 parts by weight of an olefin polymer, 2 to 15 parts by weight of a selectively hydrogenated block copolymer comprising at least two polymeric blocks, containing at least 85 wt% of polymerized monoalkenyl aromatic hydrocarbon monomer units and at least one polymeric block containing at least 85 wt% of polymerized, hydrogenated diolefin monomer units and 2 to 15 parts by weight of LLDPE, the weight ratio of hydrogenated block copolymer to LLDPE being within the range from 5:1 to 1:3, by solution blending, solid state physical mixing, molten state admixture, extrusion admixture and roll milling. Process according to claim 1, characterized in that the components are blended by accomplishing molten phase admixture within the range from 140 °C to 270 °C. Process according to claims 1 and 2, characterized in that a propylene polymer is used. Process according to any one of the claims 1-3, characterized in that the propylene polymer is a random copolymer. Process according to any one of the claims 1-4, characterized in that a copolymer of polymerized propylene and polymerized ethylene comprising from 3 to 6 wt% ethylene monomer units is used. Process according to any one of the claims 1-5, characterized in that a block copolymer and LLDPE are used in a weight ratio within the range from 1:1.5 to 1.5:1. Process according to any one of the claims 1-6, characterized in that a block copolymer is used, wherein the monoalkenyl aromatic hydrocarbon monomer unit is a styrene monomer unit and the conjugated diolefin monomer unit is a butadiene monomer unit. Process according to any one of the claims 1-7, characterized in that a block copolymer is used wherein the polymeric blocks containing at least 85 wt% monoalkenyl aromatic hydrocarbon monomer units have a weight average molecular weight within the range from 5,000 to 10,000 and the polymeric blocks containing at least 85 wt% hydrogenated diolefinic monomeric units have a weight average molecular weight within the range from 25,000 to 100,000. Process according to any one of the claims 1-7, characterized in that LLDPE is applied having a melt index above 10 g/10 min. and a density less than 0.92 x10³ kg/m³. Process according to any one of the claims 1-9, characterized in that the used olefin polymer is a random copolymer of polymerized propylene and polymerized ethylene containing less than 10 wt% polymerized ethylene and having a flow rate within the range from 0.5 to 50 g/10 min. Process according to claim 10, characterized in that the copolymer is at least 40% crystalline.

Inventors: HANSEN, DAVID ROMME, HOLDEN, GEOFFREY
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1988
Main classification: C08L23
IPC codes: C08L53, C08L23