MEDIUM REFRACTIVE INDEX GLASS SUITABLE FOR OPHTHALMIC APPLICATIONS

Abstract: This invention is related to glasses particularly useful in the fabrication of multifocal lenses for ophthalmic applications. The inventive glasses exhibit a refractive index between 1.599-1.602, an Abbe number between 40.5-41.5, a density between 2.64-2.66 g/cm³, a transmission of visible radiation at 400 nm through a thickness of 10 mm greater than 83%, a softening point between 670°-680°C, a birefringence upon sealing, measured as described, between -150 and +150 nm/cm, and consist essentially, expressed in terms of weight percent on the oxide basis, of: SiO₂ 52-57 K₂O 11.0-16.0 B₂O₃ 2.5-7.0 CaO 2-3.5 Al₂O₃ 0-1 ZrO₂ 1-1.5 Li₂O 0.3-0.8 TiO₂ 15.0-16.2 Na₂O 5.4-8.2 As₂O₃ 0.1-0.4 with the condition that M=69-72 where M= [760x%Li₂O+270x%Na₂O+170x%K₂O+185x%CaO+130x%TiO₂].

Description: The present invention is concerned with glasses for ophthalmic applications. More particularly, this invention is concerned with glasses which permit the fabrication of multifocal lenses by one of the processes currently utilized; that is to say, by soldering or "fusion" of one or more glasses to the principal glass, said "segment glasses" having a higher refractive index. This invention is related to the principal glass. This invention is designed to produce glasses having a refractive index (n d ) between about 1.599-1.602, an Abbe number (ν d ) of 40.5-41.5, a softening point or Littleton temperature of 670°-680°C, very low birefringence when sealed to existing segment glasses for "white" glasses with a refractive index of 1.523, a density of 2.64-2.66 g/cm³, very good transmission in the visible region of the radiation spectrum (transmission at a wavelength of 400 nm for a thickness of 10 mm greater than 83%), an absence of undesirable yellow coloration, excellent chemical durability and stability with respect to devitrification, and a viscosity at the highest temperature of devitrification (or "liquidus") equal to or greater than 300 Pa.s (3000 poises) so as to enable products to be produced using a continuous melting unit and formed using an automatic pressing process, which is indispensable for obtaining a cost of production that is low and compatible with the application. Summary of the Invention Glasses having a refractive index on the order of 1.600 have recently been developed for their use in low and average corrections, that is to say, in the region of lenses with a power of about +6 to -6 diopters. With respect to the current "white" glasses with a refractive index of 1.523, the present inventive glasses permit thinner lenses to be obtained and, in certain cases, appreciably lighter lenses (especially the highest corrections). For that it is indispensable that the density of the glass not be too high; it is especially preferable that it not be greater than 2.66 g/cm³. The increase in the index of refraction generally leads to a decrease in Abbe number or constringence (that is to say, an increase in the dispersion of the glass). If the dispersion is very high, the chromatic aberration then becomes significant and brings about the appearance of a colored fringe on the border of the lens which bothers the wearer of the lens. In order to alleviate this defect, the glass should have a constringence as high as possible. Thinness and lightness considerably improve the aesthetic appearance of the lenses and offer the wearer of eyeglasses better comfort. Because of the interest that has developed for this type of glass, it is necessary to be able to offer a series of products covering a range of applications as large as possible. One of these applications is the "double" correction (far and near vision) required by certain individuals, which can be effected through the help of lenses called "progressives" or through the help of fused bifocal lenses. The glasses of this invention apply more particularly to this second type of application. Obviously, they can also serve in the fabrication of all types of lenses, single vision, "progressives," and aspherics obtained by current polishing techniques. The glasses of the present invention exhibit another characteristic. That is, they can be fused to existing segment glasses and readily used with "white" glasses with a refractive index of 1.523. The advantages are evident as much as from a technical point of view as an economic point of view. The characteristics of two commercially marketed segment glasses which can be used with the glasses of the present invention are listed below: Glass A Glass B Refractive index (n d ) 1.681 1.750 Constringence (ν d ) 38.3 31.4 Density (g/cm³) 3.52 4.25 Softening point (T L )°C 665 660 Coefficient of thermal expansion (25°-300°C) x10⁻⁷/°C 90 89 The operation of fusing the segment glass to the principal glass is conducted at a temperature near the softening point of the latter and slightly higher than the softening point of the segment glass. Keeping in mind the softening points of the segment glasses given above, the principal glass should have a T L of at least 670°C. It is generally acknowledged that the seal between the two glasses should exhibit a birefringence between about -150 and +150 nm/cm and preferably between -50 and +50 nm/cm which requires quite close coefficients of thermal expansion. The measurement of the birefringence is more representative of the seal than that of the linear coefficient of thermal expansion. So that is the criterion that was observed in characterizing the principal glass. It should be noted, however, that the coefficient of thermal expansion of the inventive glasses between 25°-300°C is between 92-100x10⁻⁷/°C. Satisfying the criteria of the softening point temperature and birefringence of the seal, accompanied with other required conditions, was one of the critical difficulties to be resolved. According to the invention it has been found that glasses having the above-mentioned characteristics should have a composition located within the following restricted limits (expressed in terms of weight percent on the oxide basis as calculated from the batch): M is defined as the sum of the percentages of the principal modifying oxides weighted by their contribution to the birefringence of the seal; this contribution having been determined experimentally. Thus, if M is less than about 69, the glass is not sufficiently "expansible" (lack of modifiers) and the birefringence of the seal will be positive and greater than about 150. The situation is reversed in the case where M>72. The amount of SiO₂ will comprise between 52-57% by weight. This range is imposed by the choice of the other constituents of the glass whose contents limits are given below. B₂O₃ is an important constituent of the glass composition. Its principal advantages are a small contribution to the density of the glass associated with a reduction in the viscosity when it is added in substitution for SiO₂. The influence of B₂O₃ on the viscosity and, consequently, on the ease of production of the glass, also contributes to obtaining a glass exhibiting very little coloration. So the glass will contain at least 2.5% by weight. Beyond 7% B₂O₃, however, the amount of SiO₂ should be decreased in order to maintain the birefringence, which leads to an undesirable reduction in the softening point of the glass. Al₂O₃ increases the viscosity of the glass and improves its chemical durability, but, on the other hand, it rapidly makes worse the devitrification tendency of the glass. Substituted for SiO₂, it slightly decreases the T L . So, its content will not exceed about 1% by weight. Li₂O substituted for SiO₂ or B₂O₃ very strongly reduces the T L and raises the coefficient of thermal expansion, but it contributes to raising the refractive index without unfavorably altering the density of the glass. Its content will comprise between 0.3-0.8% by weight. For the other alkali metals used in the glass composition, the replacement of Na₂O with K₂O is favorable in raising the T L , but unfavorable in reducing the refractive index. The birefringence of the glass is adjusted by substituting the alkali metal oxides Na₂O and K₂O for glass formers SiO₂ and B₂O₃. For a negative birefringence (coefficient of thermal expansion too high) SiO₂ will be substituted for Na₂O, which is favorable in raising the T L . For a positive birefringence K₂O will be substituted for B₂O₃, the T L will remain essentially unchanged. For these various reasons the Na₂O content will comprise about 5.4-8.2% by weight and that of K₂O between 11.0-16.0% by weight. TiO₂ is the constituent which offers the best density-refractive index compromise. Used in a great amount, however, it decreases the transmission in the visible, facilitates devitrification, increases the density, and rapidly reduces the Abbe number. So its content will comprise between 15-16.2% by weight. ZrO₂ raises the refractive index and the density of the glass, but reduces the Abbe number less rapidly than TiO₂. This oxide improves the durability against alkaline agents and to satisfy that effect its content should be at least 1%. Nevertheless, it should not exceed 1.5% in order not to raise the density of the glass excessively. CaO is introduced in order to limit the content of TiO₂ and, consequently, to permit a very high Abbe number to be obtained. At least 2% must be present. Beyond 3.5%, however, the tendency toward devitrification significantly increases. Prior Art U. S. Patent No. 4,540,672 is directed to glasses suitable for optical and ophthalmic applications which exhibit densities less than 2.65 g/cm³, refractive indices between 1.595-1.607, Abbe numbers between 40-47, and which consist essentially, in weight percent, of: Whereas those broad ranges overlap the composition intervals of the present invention, with the exception of the Li₂O content, the physical properties exhibited by the glasses vary relatively widely and there is no requirement regarding the capability of the glasses to be sealed to existing segment glasses. Specifically, there was no requirement that the birefringence demonstrated at the seal be between ± 150 nm/cm and, preferably, between ± 50 nm/cm. To achieve that characteristic, the glasses of the present invention not only must have compositions within the very strictly delimited intervals, but also must comply with a M value between 69-72. No reference is made to a M value in the patent. U. S. Patent Nos. 2,523,265, 2,699,399, 2,901,365, and 4,438,211, Japanese Patent Publication 54-105,119, and Great Britain Patent Application No. 2,115,403 are also generally related to the present invention, but are not believed to be as relevant as Patent No. 4,540,672 supra. Description of Preferred Embodiments The invention is further illustrated through the non-limiting examples of Table I. The preferred example is No. 1. All the proportions of the components are given in weight percent on the oxide basis as calculated from the batch. Table 2 provides several examples of glasses which have compositions outside of the invention (the M parameter is outside the required limits). It can also be stated that, when M>72, the T L is generally lower than 670°C. Examples of a Glass Melt The glasses are prepared from customary batch materials (oxides, carbonates, hydrates, etc.). The batch materials chosen will preferably contain a minimum amount of Fe₂O₃ in order to obtain a glass as "white" as possible. After weighing, the batch materials are mixed together in accordance with current techniques. The mixture is then charged into a platinum crucible at a temperature of about 1250°C. When it is completely melted, the temperature of the melt is taken to about 1320°-1400°C and maintained there for 1-4 hours for homogenization and fining of the melt. The glass melt is then cooled to a temperature at which the viscosity thereof is appropriate for forming and poured into steel molds. The glass is then annealed at 500°C and cooled slowly at a rate of 60°C/hour to ambient temperature. The refractive index (n d ), the constringence (ν d ), the density (Den), the softening point in °C (T L ), the linear coefficient of thermal expansion over the range of 25°-300°C in 10⁻⁷°C⁻¹ (Exp), the transmission to visible radiation in % (Tran), the liquidus viscosity in Pa.s (poises) (Vis), and the liquidus temperature in °C (Liq) were measured utilizing conventional methods. In order to determine the birefringence (Bir), a seal was made with segment glass A, mentioned above, at 670°C for 30 minutes. The two contacting glass surfaces had previously been polished. After sealing, a 10 mm thick sample was cut perpendicularly to the plane of the join which is afterwards polished, and the birefringence then measured in the principal glass with the aid of a "Babinet Compensator"-type of apparatus. The birefringence is expressed in nm/cm. The chemical resistance [acid durability (Dur)] is determined through a test which consists of measuring the loss in weight of a polished sample immersed for three hours in a boiling aqueous solution containing 20% by volume HCl. The loss in weight is expressed in terms of mg/dm². 10 11 12 13 14 SiO₂ 54.2 53.25 52.95 54.7 54.95 B₂O₃ 4.9 4.35 5.05 5.9 5.05 Al₂O₃ 0.5 0.5 0.5 0.5 0.5 Li₂O 1.0 0.7 0.7 0.7 0.7 Na₂O 7.45 5.95 6.9 5.95 4.9 K₂O 12.2 14.6 13.85 12.2 13.85 CaO 3.1 3.8 3.15 3.8 3.15 ZrO₂ 1.0 1.3 1.3 1.3 1.3 TiO₂ 15.35 15.25 15.3 14.65 15.3 As₂O₃ 0.3 0.3 0.3 0.3 0.3 M 74.15 73.06 73.21 68.20 67.81 n d 1.6012 1.6002 1.6011 1.6007 1.6005 ν d 41.2 41.6 41.3 41.4 41.0 Den 2.66 2.66 2.66 2.65 2.65 T L 655 665 663 677 678 Exp 97.1 99.5 92.7 - Bir -360 -300 -280 +310 +385 Liq ≈923 ≈930 ≈912 ≈960 - The criticality of maintaining the value of M between 69-72 in order to insure the preparation of seals exhibiting low birefringence is immediately apparent from an examination of Table II. Examples 10, 11, 13, and 14 are compositions just slightly outside of those prescribed in the products of the present invention, and Example 12 comprises a composition wherein each individual component is within the ranges of the present inventive glasses. In each Example, however, the M value is outside of the composition interval found necessary to yield a seal demonstrating low birefringence. Consequently, Examples 10-14 would not be suitable glasses in the present invention. It might be observed that the composition of Example 10 is essentially within the composition ranges of Patent No. 4,450,672, supra.

Claims: A multifocal ophthalmic lens consisting of a principal glass and a segment glass fusion sealed to said principal glass, said principal glass being characterized by exhibiting a refractive index between 1.599-1.602, an abbe number between 40.5-41.5, a density between 2.64-2.66 g/cm³, a transmission of visible radiation at 400 nm through a thickness of 10 mm greater than 83%, a softening point between 670°-680°C, a linear coefficient of thermal expansion over the temperature range 25°-300°C of 92-100 x 10⁻⁷/°C, and a birefringence at the seal between said principal glass and said segment glass between -150 and +150 nm/cm, said principal glass consisting essentially, expressed in terms of weight percent on the oxide basis, of: A lens according to claim 1 characterised in the principal glass has viscosity at the liquidus temperature equal to or greater than 300 Pa.s. A lens according to claim 1 or claim 2 characterised in that the birefringence of the principal glass at the seal between that glass and the segment glass is between -50 and +50 nm/cm.

Inventors: BOUDOT, JEAN EMILE, MAZEAU, JEAN-PIERRE
Applicants: CORNING GLASS WORKS
Application year: 1988
Main classification: C03C3
IPC codes: C03C3