CARBONACEOUS AND/OR SILICEOUS FILLER FOR RUBBER

Abstract: An additive for incorporation into a rubber product as filler or extender which is a carbonaceous and/or siliceous powder or fibrous material derived from plant or vegetable materials, such as bagasse or other waste materials. The additive is produced by processing the plant or vegetable material to form an ash material and thereafter treating the ash material to produce a carbonaceous and/or siliceous powder or fibrous material of required particle size. A rubber product containing the additive may also incorporate further components such as processing aids, coupling agents, etc.

Description: CARBONACEOUS AND/OR SILICEOUS FILLER FOR RUBBER This invention relates to an improved additive product and a process for its manufacture. The invention also relates to a further new product, of which the first mentioned product is a component, and, in turn, a process for its manufacture. The invention is extremely valuable in that it finds use for materials previously generally regarded as waste materials. More specifically the product of the invention is useful as an additive to, and component of, a new rubber product. Its purpose and considerable value in this respect will be elaborated hereafter. The expression "waste materials" includes within its ambit plant and vegetable materials. These, in turn, are defined as materials selected from bagasse (i.e. sugar cane residue), furfural residue, rice hulls, corn stalks, cane trash, coffee bean waste, peat moss, alcohol slop, olive pulp, sugar beet residue, sawdust and other wood wastes and coal and other similar organic materials. In most of the industries in which these materials are produced (as by-products in substantial quantities) , it has been a problem to find suitable uses for them. Such uses have included the manufacture of paper and building materials. However, as a matter of developing practice, a common use has been as a fuel. The present invention achieves a substantial step forward in the useful disposal of these materials. In one broad aspect, the invention is an additive product, for incorporation into a rubber product as a filler or extender therefor, the said additive product being a carbonaceous and/or siliceous powder or fibrous material of required particle size derived from one or more plant or vegetable materials as herein defined. More specifically the invention is an additive product, for incorporation into a rubber product as a filler or extender therefor, the said additive product being a carbonaceous and/or siliceous powder or fibrous material of required particle size derived from bagasse. Relatedly, in this aspect, the invention includes within its ambit these processes: - A process for manufacturing an additive product,for incorporation into a rubber product as a filler or extender therefor, comprising the steps of processing one or more plant or vegetable materials as herein defined to produce therefrom an ash material, and thereafter treating the ash material to produce a carbonaceous and/or siliceous powder or fibrous material of required particle size. - A process for manufacturing an additive product, for incorporation into a rubber product as a filler or extender therefor, comprising the steps of processing bagasse to produce therefrom ash material comprising furnace ash and fly ash, and treating the fly ash to produce a carbonaceous and/or siliceous powder or fibrous material of required particle size. In a further (and most important) aspect, the invention also provides a rubber product containing an additive functioning as a filler or extender therefor. The additive is derived from one or more plant or vegetable materials as herein defined, for example (and in particular) bagasse. The additive is a carbonaceous and/or siliceous powder or fibrous material which may be, but which is not necessarily, of fine particle size. The additive may further incorporate additional components such as processing aid(s) and/or coupling agent(s) . Additionally, in this aspect, the invention includes within its ambit a process of manufacturing the foregoing rubber product characterised in that there is incorporated into rubber the above additive. Other aspects and preferred features of the invention will appear hereafter. Where it is more convenient or appropriate to do so, the additive product of the invention will be simply designated by either of its functional names, namely "filler" and "extender". It is to be understood that the expressions are thus used interchangeably. The invention will now be detailedly described with reference to preferred performance features and specific examples. It will thus be appreciated that the ensuing description is merely intended to illustrate the invention and therefore should not be limitatively construed. As indicated the additive product of the invention can be derived from any suitable plant or vegetable material, in particular bagasse. Typically the product may be manufactured from bagasse in accordance with the following preferred procedure. The equipment used in carrying out this procedure is conventional. Bagasse (typical analysis sugar 3%, fibrous material 50%, water 47%) is fed to a sugar mill boiler where it burns to ash. The ash is made up of furnace as and fly ash. The fly ash, because it sometimes tends to be carried away in the gas stream before combustion is complete, can have a carbon content which is significantly higher than the furnace ash. As a first step, the fly ash is recovered. Recover is usually effected by dust collectors of the multi-cyclone type. Any fly ash which escapes this recovery step may be collected in secondary cleaning equipment, which may take the form of a wet scrubber (alternatively a bag filter or electrostatic precipitator may be employed) . In the case of a wet scrubber fine ash particles removed by the scrubber are directed in a slurry to a disposal pond from which they can be recovered for use. The recovered fly ash is then passed to a density separator which extracts heavy silica particles. Any oversize and unburned or partially burned bagasse particles are extracted by screening. With these contaminants removed, the remaining ash material is then classified, by classifying cyclones and/or air elutriation, and screened, in sequence as appropriate (but not necessarily in the order stated), to produce a first powder material, a second powder material, a first fibre material, and a further fibre material. The first powder material is a fine carbonaceous and/or siliceous powder, the particle size of which is up to 75 microns, for example 50-70 microns. The second powder material is larger in particle size (and thus able to be further ground as required) - but usually below about 350 microns. The first fibre material can be described as a medium carbonaceous fibre material, with particles up to 1000 microns in nominal size. The further fibre material is coarse and carbonaceous in nature (with a carbon content up to, for example, 85%). Further grinding of these materials, and screening, will produce the fine carbonaceous/siliceous powder as described. A typical additive product of the invention has a carbon content of (20-40)%. A typical siliceous material content is 50 to 60% with the balance made up of aluminium oxide (5 to 15%) - (the combined carbon/siliceous/alumina content preferably exceeding 85%) - and other chemically combined elements not incompatible with rubber. It is stressed however that these ranges can be widely varied in accordance with the end use of the rubber product. For example a powder of low carbon content would typically contain less than 10% carbon (e.g. 1-3%) and a high content (e.g. 60-65 to 75%) silica. Further, the additive product, which is typically a fine black powder when the carbon content is 20-40% as indicated above, may be of greyish hue when such carbon content is lower, and will be of more fibrous texture when fine particle size is not critical. It is odourless, substantially non-reactive (inert), has an extremely high melting point (in excess of 1000°C) and is substantially insoluble in water. As a specific (but merely) illustrative example an additive powder of the invention may be constituted as follows: carbon 29.5% Si0 2 53.2% A1 2 0 3 6.8% other chemically 10.5% combined rubber- compatible elements Turning now to the aforementioned important (rubber product) aspect of the invention, I have found, surpris¬ ingly, that the carbonaceous and/or siliceous powder of fine particle size as described above - and also carbonaceous and/or siliceous powders of larger (fibrous) particle size - possesses extremely valuable properties as a iller/extender for rubber compounds. This aspect of the invention will now be detailedly described. By way of preamble, rubber products or compounds (the expressions are used interchangeably) are conveniently grouped as general purpose non-oil resistant; general purpose oil-resistant and specialty elastomers. The first group includes, for example, natural, SBR (styrene/butadiene) , butyl and EPDM (ethylene propylene diene monomer) rubbers; the second includes (e.g.) nitrile, epichlorhydrin, chloroprene and urethane rubbers; the third includes (e.g.) silicone, polyacrylate rubbers and fluorocarbon rubbers. The use to which a product is to be put will naturally govern the category from which it is selected. For example, a rubber product intended for use as an oil seal will invariably be selected from the second group. In the manufacture of rubber compounds, it is a normal practice to add reinforcing fillers, such as carbon blacks, to enhance such properties as tensile strength and elongation. These properties are important for the dynamic physical properties of rubber compounds. Cost can also be reduced by adding additional quantities of reinforcing fillers. However, beyond a certain point, such addition can become counter-productive. A number of non-reinforcing fillers are also known in the art - such as soft clay, talc, and aluminium silicate. However the use of these fillers is usually limited to those rubber compounds not requiring high tensile strengths and elongation. Too much non-reinforcing filler is usually deleterious to these characteristics and also increases specific gravity. Hence their widespread use in high quality rubber compounding is severely restricted. The importance of fillers in the rubber industry, and the criteria to be taken into account when choosing a filler for a particular purpose, are well documented in the literature of the art. In this respect, attention is directed to an article entitled "The Needs and Requirements of Fillers for Mechanical Rubber Products" by Larry L. Yarnell, The Gates Rubber Company, Denver, Colorado, U.S., published in the Plastics and Rubber Institute's News and Views of December 1987. The properties of rubber fillers and rubber compounds containing them are also discussed at length by Eli M. Dannenberg, in an article entitled "Overview of Fillers Used in Rubber" published in the above periodical. Proceeding, my invention enables the loading (content) of non-rubber filler component, in a rubber compound, to be extended without reducing tensile strength to an unsatisfactory level. At the same time, satisfactory compression set and elongation are maintained. Apart from sustaining performance at a satisfactory level, substantial economic advantages can be gained (the overall cost of the rubber compound can be significantly reduced) . To express the above in somewhat more detail: - Addition of the powder set forth above to a rubber compound, as a non-reinforcing extender in conjunction with conventional reinforcing fillers, will reduce tensile strength - but to a level not lower than required by the standards of the art. In addition it will not reduce elongation or compression set in the same way that known non-reinforcing mineral fillers do when used as extenders. Functional capability (with particular regard to such characteristics as elongation and compression set) is thus maintained. - Incorporation of the inventive additive results in a significant increase in the proportion of non-rubber components in a rubber compound - with consequential reduction in the cost of the total materials used in a unit weight of such compound (whilst maintaining functional capability as stressed above) . - Unlike known mineral fillers which usually increase the plasticity of uncured rubbers, incorporation of the inventive additive makes no material difference to the plasticity of the rubber compound: this in turn means that processing problems are substantially avoided. - A rubber compound, in which the inventive additive is incorporated, has a specific gravity significantly lower than a comparable compound with (the majority of) known mineral fillers. The consequence of this is that the volume cost of the overall rubber material is kept down, with resultant cost advantages to the manufacturer. - Finally, unlike known fillers, the inventive additive is inert to (and does not interfere with) curing procedures to which the rubber compound is typically subjected. The inventive additive may be present in amounts selected in accordance with situational requirements. As these amounts can vary widely - depending upon the intended use of (and the properties required in) the rubber product - it would be unduly restrictive to place quantitive limitations thereon. Generally speaking, for a wide variety of rubbers, the additive can be present in the range 15 to 120 phr, for example 50 to 100 phr ("phr"is the standard abbreviation for "parts per hundred parts of rubber"). However, in testimony of what is stated immediately above, it is envisaged that in certain applications - specifically general purpose non-oil resistant EPDM rubbers - considerably higher amounts (e.g. up to 200-300 phr) could be incorporated. Taken in conjunction with a conventional filler already present (e.g. a carbon black reinforcing filler), the total amount of filler may well exceed (sometimes substantially) the amount of rubber. The conventional fillers (with wich. the inventive additive is usually to be associated) may be selected from any of the many fillers mentioned above. In addition, a rubber product of the invention may typically include further components as required. These components are selected from plasticizers, anti-oxidants, activators, processing aids, curatives, pigments (if required), anti-ozoneates, accelerators and the like. As indicated above, it is also a feature of this aspect of the invention for the additive product to be pre-treated or compounded with certain components, such as components facilitating dispersion into the rubber and coupling of a filler and rubber. These components include the aforementioned processing aids and coupling agents. The former may be exemplified by the compound known as Dispergator FL (trade name) - manufactured by Kittlitz Chemie GmbH and Co. KG. of Germany - and also by those mentioned heretofore. The coupling agents may be exemplified by the alkyl silanes, for example the compound known as Silanogran Si69GR (trade name) - manufactured as above. The processing aids may be incorporated in a preferred amount within the range 2 to 10% of powder or fibrous material (e.g. 3%). A typical amount of coupling agent is likewise in the preferred range 2 to 10% (e.g. 5%). This (rubber) aspect of the invention will now be further described with reference to the following specific Examples. Where these Examples incorporate conventional proprietary compositions which in the art are obtainable under, and normally identified by, trade names, each such composition is so identified - along with its respective function. In addition, where abbreviations are used (e.g. ASTM - designating American Society for Testing and Materials), such abbreviations are well known in the art. Example 1 A nitrile rubber product in accordance with the invention is constituted as follows: Components Amount NBR 32.50 polymer - 100.00 nitrile rubber N330 black (HAF) - 60.00 carbon black high- reinforcing filler Inventive additive 100.00 Dioctyl phthalate - 20.00 plasticizer Nocrack B (trade name) - 2.00 anti-oxidant Zinc oxide - activator 5.00 Stearic acid - activator 2.00 Sulfasan R (trade name) - 1.00 curative Mercapto benzothiazole 2.00 sulphenamide (MBTS) - curative Tetramethyl thiurea 2.50 disulphide (TMTD) - curative The product was prepared from the foregoing components in conventional fashion. The rate of incorporation into nitrile rubber of the inventive additive, on an open mill, in fact exceeded that of carbon black, thus reducing batch mixing time. The above rubber compound displays the following physical properties: Hardness, Shore A 80 Tensile strengh, psi 1090 Elongation, % 270 Specific gravity 1.383 Heat Aging: 70 hours at 125C. : ASTM D573 Hardness change, points +11 Tensile strength change, % +7 Elongation change, % -48 It is thus suitable for industrial products requiring oil and solvent resistance, but not a high degree of tensile strength. Such a product can be used in static applications such as some forms of oil seals, grommets, washers, bushes and dust covers. There are indeed many other general purpose static industrial applications for such a compound. Example 2 A series of tests, aimed at establishing the behavioural effects of various loadings of the inventive extender in a typical nitrile rubber compound were carried out. These tests served as a basis from which specific recipes for specific purposes could be selected. A B C D E (Control) NBR 32/50 100.00 100.00 .100.00 100.00 100.0 polymer - nitrile rubber N774 carbon 70.00 70.00 70.00 70.00 70.0 black - filler Inventive 25.00 50.00 75.00 100.0 Additive Corflex 880 5.00 5.00 5.00 5.00 5.0 (trade name) - processing aid Flectol flakes 2.00 2.00 2.00 2.00 2.0 (trade name) - antioxidant Polyethylene 1.00 1.00 1.00 1.00 1.0 AC (trade name) - mold flow and release agent Zinc oxide - 10.00 10.00 10.00 10.00 10. activator Stearic acid - ' 1.00 1.00 1.00 1.00 1.0 activator Sulphur MC 0.50 0.50 0.50 0.50 0.5 (trade name) - curative MBTS 3.00 3.00 3.00 3.00 3.0 (see Example 1 above) TMTD 2.00 2.00 2.00 2.00 2.0 (see Example 1 above) TOTAL 194.50 219.50 244.50 269.50 294.5 Test Results: 1. Mooney (1+4) 25 26 35 40 5 100C. 2. Physical Properties Hardness, IRHD 70 75 80 83 8 Tensile st'gth, 2620 2230 1760 1540 129 psi A B C D E (Control) Elongation, % 270 260 220 190 170 Specific gravity 1.253 1.305 1.357 1.393 1.439 3. Compression Set : 22 hours at lOOC. : ASTM D395 Method Compression 4 5 7 9 13 set, % 4. Heat Aging : 70 hours at 125C : ASTM D573 Hardness +9 - - +4 +3 change, pts Tensile +8 - - +2 +3 strength change, % Elong'n -22 - - -45 -41 change, % 5. Fluid Aging: 70 hours at 125C in ASTM #1 oil : ASTM D47 Hardness +7 - - +2 +3 change, pts Tensile +15 - -1 +8 strength change, % Elong'n -6 -26 -16 change, % Volume -5. ' 2 - - -3.6 -3.4 change, % 6. Fluid Aging: 70 hours at 125C in ASTM #3 oil : ASTM D47 Hardness -9 - - -11 -10 change, pts Tensile -6 - -3 -5 strength change, % Elong'n -13 -6 -11 change, % Volume +10.7 - - +9.8 +8.2 change, % Note: The tests for heat aging and fluid aging were not carried out for compounds B and C as a matter of economy in laboratory expenses, and were limited to the compounds D and E, to yield this particular data at the higher additive loadings. It was recognized that the heat aging and fluid aging tests could be repeated for each specific recipe for any particular purpose. The foregoing results show that the compounds B an C can be used for industrial rubber products requiring oil and solvent resistance, and a relatively high degree of tensile strength for a variety of dynamic industrial applications. When selecting the final recipe for such compounds, minor adjustments (as required) will be made to the plasticizer to achieve the required hardness. The results also indicate that compounds D and E containing 50 to 100 phr of additive (again with adjustment of the plasticizer as required to correct hardness) will be suitable for those industrial rubber products set forth in Example 1 above. Example 3 The following compound was formulated: Components Amount Krynac 34.50 - 100.00 nitrile rubber SRF (N774) carbon - 60.00 black - filler Inventive additive 40.00 Dioctyl phthalate - 7.00 plasticizer TE80 (trade name) - 1.00 processing aid Flectol Flakes (trade 2.00 name) - anti-oxidant Zinc oxide - activator 10.00 Stearic acid - activator 1.00 Sulphur MC (trade name) - 0.50 curative MBTS - as above 3.00 TMTD - as above 2.00 TOTAL 226.50 - 14 - This compound was tested against SAE (Society of Automotive Engineers Inc.) requirements - specifically SAE specification J120a in respect of rubber "O" rings for automotive sealing applications. The results are set forth below. Physical properties: Cured for 10 minutes at 175C. Measured SAE Results J120a Specification Hardness, Shore A 74 65-75 Tensile strength, psi 1710 1500 min Elongation, % 320 200-400 Modulus @ 100% 463 450 min. elongation Heat Aging, 70 hrs at 125C. Hardness change, points +7 +10 max. Tensile strength +8 -15 max. change, % Elongation change, % -44 -50 max. Compression Set : 70 hours at 125C Compression set ASTM 29 35 max. specimen, % Fluid Aging, 70 hrs at 150C. in ASTM #1 oil Hardness change, points +6 -5 to +8 Tensile strength, +7 -15 max. change % Elongation change, % -20 -40 max. Volume change, % -4.7 -5 to +5 Fluid Aging, 70 hrs at 150C. in ASTM #3 oil Hardness change, points -9 0 to -15 Tensile strength, -9 -30 max. change % Elongation change, % -15 -40 max. Volume change, % +10.6 +20 max. As can be seen, the physical properties of the compound conform in all respects with the requirements of. the SAE specification. The compound is thus eminently suitable for high quality automotive seals and "0" rings. Example 4 A series of test were carried out on rubber boot sole compounds as utilised by the armed forces (army specification 657B) . The purpose of these tests was (i) to initially determine the reinforcement afforded by specific amounts of a precipitated silica filler (ii) to then determine the extent to which a compound containing the precipitated silica filler could be extended by the inventive additive. In relation to (i), the compounds A to C below were formulated. The precipitated silica filler is identified by the trade name Ultrasil VN3. B Krynac 34.50 - 82 . 00 82 . 00 82 . 00 as above Austrapol BR1220 - 18. 00 18. 00 18.00 polybutadiene rubber Stearic acid - 1.00 1.00 1.00 as above. Permanax OD (trade name) - anti- 2.00 2.00 2.00 oxidant Ozone wax 110 2.80 2.80 2.80 anti-ozoneate Crodamide SR 1.80 1.80 1.80 anti-oxidant 16 - A B Zinc oxide - 3.00 3.00 3.00 as above Ultrasil VN3 20 . 00 30 . 00 45 . 00 as above Corflex 880 15.00 15.00 15.00 as above Pigments - optional MC sulphur 1.00 1.00 1.00 as above Mercapto benzo 0.55 0.55 0.55 thiazole (MBT) - curative MBTS - as above 1.45 1.45 1.45 Diphenyl guanadine 0.80 0.80 0.80 (DPG) - accelerator TMTD - as above 0.60 0.60 0.60 TOTAL 150.00 160.00 175.00 Physical properties: cured 10 mins at 180C, Hardness, IRHD 48 52 66 Tensile strength, 650 920 1330 psi Elongation, % 550 750 750 It is evident from the results for compounds A to that, as the loading of the precipitated silica is increased (from 20 to 45 phr), the rate of increase in hardness accelerates and the rate of increase in elongation decelerates. It can therefore be concluded that, if the precipitated silica loading were increased further, the hardness would increase dramatically and the elongation would decrease substantially. Such conditions would produce a hard brittle compound which would be quite unsuitable for the purpose indicated. Turning to (ii), compounds D to H were formulated by adding the inventive additive to compound C. The inventive additive in this Example is a low carbon powder of fine particle size manufactured from bagasse ash. The precipitated silica is as above. D E F G H Krynac 34.50 - 82.00 82.00 82.00 82.00 82. as above Austrapol BR1220 18.00 18.00 18.00 18.00 18. - as above Stearic acid - 1.00 1.00 1.00 1.00 1. as above Per anax OD - 2.00 2.00 2.00 2.00 2. as above Ozone wax 110 - 2.80 2.80 2.80 2.80 2. as above Crodamide SR - 1.80 1.80 1.80 1.80 1. as above Zinc oxide - 3.00 3.00 3.00 3.00 n 3. as above Ultrasil VN3 - 45.00 45.00 45.00 45.00 45. as above Inventive 15.00 30.00 45.00 60.00 75. Additive - as above Corflex 880 - 15.00 15.00 15.00 15.00 15.0 as above Pigments - as - - - - - above D E F G H MC sulphur - 1.00 1.00 1.00 1.00 1.00 as above MBT - as above 0.55 0.55 0.55 0.55 0.55 MBTS - as above 1.45 1.45 1.45 1.45 1.45 DPG - as above 0.80 0.80 0.80 0.80 0.80 TMTD - as above 0.60 0.60 0.60 0.60 0.60 TOTAL 190.00 205.00 220.00 235.00 250.00 Physical properties: cured 20 mins at 160C. Hardness, IRHD 54 62 72 73 77 Tensile strength, 1410 1200 1090 910 820 psi Elongation, % 720 700 680 680 660 Compound C cured for 20 mins at 160C. Hardness, IRHD 66 Tensile strength, 1360 psi Elongation, % 660 In contrast to the foregoing, the results obtained with compounds D to H - where the loading of the inventive additive was increased whilst maintaining the precipitated silica filler at 45 phr - indicate a reversal of the trend. The rate of increase in hardness is decelerated, whilst the rate of decrease in elongation is arrested. By further extending the compounds in this way, it is thus possible to increase the total filler loading from 45 phr to 105 phr while still making a compound of acceptable physical properties (for use in army footwear, industrial work boots and the like) . The economic and other advantages are obvious. In a supplementary test, further compounds were formulated wherein the low carbon/fine particle size inventive bagasse ash powder is substituted by (i) a high carbon/fine particle size bagasse ash powder, (ii) a low carbon/coarse bagasse ash powder. In both instances, similarly satisfactory results were obtained. In all of the foregoing tests, the incorporation of the inventive extender does not interfere with normal rubber curing procedures. This has been confirmed by standard rheographic testing procedures. In closing, it is reiterated that the foregoing description is, in the main, merely illustrative of the invention. As long as the basic criteria as broadly defined are observed, any non-critical matters, falling therewithin, can be varied as required. On the whole, however, it will be seen that, by the invention, a substantial contribution to the rubber industry has been achieved. Significant cost savings (e.g. of the order of 5-20% of the comparable cost of producing rubber compounds from rubber and traditional fillers) can be attained without deleterious effect on the required physical properties or performance specification of a wide variety of rubber compounds. It will also be appreciated that, by providing an efficacious usage of what was previously waste material, further economic and environment-enhancing contributions have been made.

Claims: THE CLAIMS 1. An additive product, for incorporation into a rubber product as a filler or extender therefor, the said additive product being a carbonaceous and/or siliceous powder or fibrous material of required particle size derived from one or more plant or vegetable materials as herein defined. 2. An additive product, for incorporation into a rubber product as a filler or extender therefor, the said additive product being a carbonaceous and/or siliceous powder or fibrous material of required particle size derived from bagasse. 3. An additive product as claimed in claim 1 or 2 which further incorporates one or more processing aids and/or coupling agents. 4. An additive product as claimed in any one of the preceding claims wherein the powder material is of fine particle size up to 75 microns. 5. An additive product as claimed in any one of the preceding claims wherein the carbonaceous content is within the range 20-40% and the siliceous content is within the range 50-60%. 6. An additive product as claimed in any one of claims 1 to 4 wherein the carbonaceous content is less than 10% and the siliceous content is above 60%. 7. An additive product as claimed in claim 1 or 2 and substantially as herein described. 8. A process for manufacturing an additive product, for incorporation into a rubber product as a filler or extender therefor, comprising the steps of processing one or more plant or vegetable materials as herein defined to produce therefrom an ash material, and thereafter treating the ash material to produce a carbonaceous and/or siliceous powder or fibrous material of required particle size. 9. A process for manufacturing an additive product, for incorporation into a rubber product as a filler or extender therefor, comprising the steps of processing bagasse to produce therefrom ash material comprising furnace ash and fly ash, and treating the fly ash to produce a carbonaceous and/or siliceous powder or fibrous material of required particle size. 10. A process as claimed in claim 8 or 9 which further comprises incorporating, into the additive product, one or more processing aids and/or coupling agents. 11. A process as claimed in any one of claims 8 to 10 wherein the powder material is of particle size up to 75 microns. 12. A process as claimed in any one of claims 8 to 11 wherein the carbonaceous content of the powder is within the range 20-40% and the siliceous content of the powder is within the range 50-60%. 13. A process as claimed in any one of claims 8 to 11 wherein the carbonaceous content is less than 10% and the siliceous content is above 60%. 14. A process as claimed in claim 6 or 7 and substantially as herein described. 15. A rubber product containing an additive product functioning as a filler or extender therefor, the additive product being a carbonaceous and/or siliceous powder or fibrous material of required particle size derived from one or more plant or vegetable materials as herein defined. 16. A rubber product containing an additive product functioning as a filler or extender therefor, the additive product being a carbonaceous and/or siliceous powder or fibrous material of required particle size derived from bagasse. 17. A rubber product as claimed in claim 15 or 16 which includes a carbon black and/or other known filler. 18. A rubber product as claimed in any one of claims 15 to 17 wherein the additive product further incorporates one or more processing aids and/or coupling agents. 19. A rubber product as claimed in any one of claims 15 to 18 wherein the content of additive product is in the range 15 to 120 phr. 20. A rubber product as claimed in any one of claims 15 to 19 which additionally includes one or more further filler components selected from plasticizers, anti-oxidants, activators, processing aids, curatives, pigments, anti-ozoneates and accelerators. 21. A rubber product as claimed in any one of claims 15 to 20 wherein the powder material of the additive product is of fine particle size up to 75 microns. 22. A rubber product as claimed in any one of claims 15 to 21 wherein the carbonaceous content of the additive product is within the range 20-40% and the siliceous content is within the range 50-60%. 23. A rubber product as claimed in any one of claims 15 to 21 wherein the carbonaceous content is less than 10% and the siliceous content is above 60%. 24. A rubber product as claimed in claim 15 or 16 substantially as herein described with reference to any of the foregoing examples thereof. 25. A process for manufacturing a rubber product characterised in that there is incorporated into rubber an additive product as claimed in any one of claims 1 to 7.

Inventors: KEOGH BOYD TERENCE, KEOGH, BOYD, TERENCE
Applicants: KEOGH BOYD TERENCE, KEOGH, BOYD, TERENCE
Application year: 1988
Main classification: C08K11
IPC codes: C08K3, C08K9, C08K11, C08L9, C08L21