Curable organosiloxane compositions

Abstract: The tear strength of cured organosiloxane elastomers can be increased without adversely affecting other physical properties if the composition used to prepare the elastomer is curable by a platinum-catalyzed hydrosilation reaction and contains a mixture of two liquid diorganovinyl­ siloxy terminated polydiorganosiloxanes, one of which constitutes from 70 to 95 percent by weight of said mixture and contains vinyl or other ethylenically unsaturated hydrocarbon radicals only at the terminal positions. The second polydiorgansiloxane contains both terminal vinyl radicals and from 1 to 5 mole percent of vinyl radicals on non-terminal repeating units. .

Description: This invention relates to curable organosiloxane compositions. More particularly, this invention relates to organosiloxane compositions that can be transported by pumping and cured by a platinum-catalyzed hydroxilation reaction to form elastomers exhibiting superior physical properties, particularly tensile strength and tear strength, without sacrificing other desirable properties, such as hardness of the cured elastomer or processability of the curable composition. Curable organosiloxane compositions containing at least one polydiorganosiloxane with at least two silicon-bonded vinyl radicals, an organohydrogen siloxane or organic peroxide curing agent and a silica filler are well known in the art pertaining to silicone elastomers. It is also known to improve the physical properties, particularly tensile and tear strengths, of cured elastomers prepared from these curable compositions by using two or more vinyl-containing polydiorganosiloxanes of different molecular weights or a single vinyl-containing polydiorgano siloxane having a bimodal molecular weight distribution [U.S. Patent No. 4,162,243 to Lee et al]. An objective of this invention is to define a class of organosiloxane compositions that can be cured to yield elastomers exhibiting the combination of high tear and tensile strengths in addition to a durometer hardness value, measured on the shore A scale, of at least 45. A preferred class of the present compositions are "extrudable" as defined in the aforementioned Lee at al. U.S. Patent No. 4,162,243. Specifically, the compositions can be extruded at a rate of at least 20 grams per minute through a 3.175 millimeter-diameter orifice under a pressure of 620 kilopascals (kPa) at 25°C. The present inventor has discovered that the aforementioned objective can be achieved using a curable composition comprising a mixture of two liquid polydiorganosiloxanes, both of which have diorganovinylsiloxy terminal units. One of these is substantially free of non-terminal vinyl-substituted diorganosiloxane units and the second contains from 1 to 5 mole percent of these units. These compositions are cured using a platinum-catalyzed hydrosilation reaction. This invention provides a curable organosiloxane composition comprising the product obtained by mixing to homogeneity: a polymer component consisting of: A. from 70 to 95 weight percent, based on the total weight of (A) and (B), of a first liquid diorganovinylsiloxy terminated polydiorganosiloxane represented by the average general formula: ViR₂SiO(R'₂SiO) x SiR₂Vi where Vi represents a vinyl radical, R and R' are individually monovalent or substituted monovalent hydrocarbon radicals selected from methyl, ethyl, chloromethyl, 3-chloropropyl, 3,3,3-trifluoropropyl, cyclohexyl and phenyl, with the proviso that at least one of the R' radicals is methyl, and x represents a degree of polymerization equivalent to a viscosity of from 20 to 200 Pa·s at 25°C; B. from 5 to 30 weight percent, based on the total weight of (A) and (B), of a second liquid diorganovinylsiloxy terminated polydiorganosiloxane that is miscible with said first polydiorganosiloxane and exhibits a viscosity of from 0.1 to 200 Pa·s at 25°C, where from 1 to 5 percent of the non-terminal repeating units of said second diorganovinylsiloxy-terminated polydiorganosiloxane contain a vinyl radical; and C. an amount sufficient to cure said composition of an organohydrogensiloxane that is miscible with (A) and (B), and contains an average of more than two silicon-bonded hydrogen atoms per molecule, together with: D. a platinum hydrosilation catalyst in an amount equivalent to at least one part by weight of platinum per one million parts of curable composition; and E. from 10 to 60 weight percent, based on the weight of said composition, of a treated reinforcing silica filler, the treating agent being selected from liquid hydroxyl terminated polydiorganosiloxanes containing an average of from 2 to 20 repeating units per molecule and organosilicon compounds selected from hexaorganodisiloxanes and hexaorganodisilazanes that hydrolyze under the conditions used to treat the silica to form compounds with silicon-bonded hydroxyl groups. 1. The Vinyl-Containing Polydiorganosiloxanes The inventive features considered responsible for the unique combination of physical properties exhibited by elastomers prepared from the present curable composition are 1) the presence in the composition of two miscible diorganovinylsiloxy-terminated polydiorganosiloxanes the first of which, referred to hereinafter as ingredient A, contains vinyl or other ethylenically unsaturated radicals only at the terminal positions of the molecule and is present at a higher concentration than the second of the two diorganovinylsiloxy-terminated polydiorganosiloxanes, referred to hereinafter as ingredient B, and 2) the presence in ingredient B of vinyl radicals on from 1 to 5 mole percent of the non-terminal repeating units. Experimental data contained in the accompanying examples demonstrate that the physical properties of the cured elastomer are adversely affected when vinyl radicals are present in the non-terminal units of ingredient A or the concentration of non-terminal vinyl radicals in ingredient B is outside the present limits of from 1 to 5 mole percent of the non-terminal repeating units. Non-terminal ethylenically unsaturated radicals are essentially absent from ingredient A. In other words, the only ethylenically unsaturated hydrocarbon radicals present on the non-terminal silicon atoms of ingredient A result from impurities present in the reactants used to prepare ingredient A, or from undesired rearrangements occurring during preparation of this ingredient. Ingredient A is a liquid diorganovinylsiloxy-terminated polydiorganosiloxane represented by the average general formula: ViR₂SiO(R'₂SiO) x SiR₂Vi where Vi represents a vinyl radical, R and R' are individually monovalent hydrocarbon radicals or substituted monovalent hydrocarbon radicals selected from methyl, ethyl, chloromethyl, 3-chloropropyl, 3,3,3-trifluoropropyl, cyclohexyl and phenyl, with the proviso that at least one of the R' radicals is methyl, and x represents a degree of polymerization equivalent to a viscosity of from 20 to 200 Pa·s at 25°C. In preferred embodiments, the viscosity of ingredient A is from 40 to 70 Pa·s. The R and R' radicals bonded to the silicon atoms of ingredient A can be identical or different. Because ingredient A is a liquid at 25°C, at least one of the R' radicals on each of the non-terminal silicon atoms is methyl. The remaining R' radical can be methyl or ethyl; chloromethyl, 3-chloropropyl or 3,3,3-trifluoropropyl; cyclohexyl; or phenyl. Most preferably, any R and R' radicals other than methyl are phenyl or 3,3,3-trifluoropropyl, this preference being based on the availability of the intermediates used to prepare these polydiorganosiloxanes and the properties of cured elastomers prepared by curing compositions containing these polymers. Methods for preparing the liquid polydiorganosiloxanes used as ingredients A and B of the present compositions by hydrolysis and condensation of the corresponding halosilanes or cyclic polydiorganosiloxanes are sufficiently disclosed in the patent and other literature that a detailed description of preparative methods in this specification is not necessary. Ingredient B is a liquid diorganovinylsiloxy-terminated polydiorganosiloxane and can be represented by the average general formula ViR''₂SiO(R'''₂SiO) y (ViR'''SiO) z SiR''₂Vi In this formula, Vi represents a vinyl radical and R'' and R''' are selected from the same group of monovalent hydrocarbon radicals and substituted monovalent substituted hydrocarbon radicals as R and R'. Because ingredients A and B should be miscible with one another, the silicon-bonded hydrocarbon radicals present in these ingredients should be selected from the same class, e.g. methyl or ethyl. These hydrocarbon radicals are preferably identical. The degree of polymerization represented by the sum of y and z is equivalent to a viscosity of from 0.1 to 200 Pa·s, preferably from 0.1 to 20 Pa·s, and the ratio z/(y+z) is from 0.01 to 0.05, which specifies the requirement for this ingredient that from 1 to 5 mole percent of the non-terminal repeating units contain a vinyl radical. The degree of polymerization of Ingredient B is preferably less than the degree of polymerization of Ingredient A. Preferred embodiments of ingredient A and B include but are not limited to dimethylvinylsiloxy-terminated polydimethylsiloxanes, dimethylvinylsiloxy-terminated-polymethyl-3,3,3-trifluoropropylsiloxanes, dimethylvinylsiloxy-terminated-dimethylsiloxane/3,3,3-trifluoropropylmethylsiloxane copolymers and dimethylvinylsiloxy-terminated-dimethylsiloxane/methylphenylsiloxane copolymers. To achieve high tear strength without adversely affecting other physical properties of the cured elastomer ingredient B constitutes from 5 to 30 percent, preferably from 5 to 15 percent, of the combined weight of ingredients A and B. Compositions containing more than about 30 percent by weight of ingredient B yield elastomers with too high a degree of crosslinking, resulting in reduced values of elongation, tear strength and tensile strength. Less than about 5 percent by weight of ingredient B will not provide the desired high level of tear strength. 2. The Organohydrogensiloxane Curing Agent The organosiloxane compositions of this invention are cured by a platinum catalyzed hydrosilation reaction. The curing agent is an organohydrogensiloxane containing an average of more than two silicon-bonded hydrogen atoms per molecule. The organohydrogensiloxane contains from as few as four silicon atoms per molecule up to an average of 20 or more, and can have a viscosity of up to 10 Pa·s or higher at 25°C. The repeating units of this ingredient include but are not limited to HSiO 1.5 , R*HSiO and/or R*₂HSiO 0.5 in addition to one or more of monoorganosiloxy, diorganosiloxane, triorganosiloxy and SiO 4/2 units. In these formulae, R* represents a monovalent hydrocarbon or halocarbon radical as defined hereinabove for the R radical of ingredient A. Alternatively, the organohydrogensiloxane can be a cyclic compound containing diorganosiloxane and organohydrogensiloxane units or a compound of the formula Si(OSiR*₂H)₄. For those embodiments of the present composition wherein the hydrocarbon radicals of ingredients A and B, represented by R′, R′′ and R′′′, are methyl, R* is methyl and the curing agent is preferably a linear trimethylsiloxy terminated dimethylsiloxane/methylhydrogensiloxane copolymer containing an average of from 10 to about 50 repeating units per molecule, of which from 3 to 5 are methylhydrogensiloxane. The molar ratio of silicon-bonded hydrogen atoms to vinyl or other ethylenically unsaturated hydrocarbon radicals in compositions curable by a hydrosilation reaction determines the properties of the cured elastomer. The optimum ratio for the present curable compositions will be determined at least in part by the molecular weights of ingredients A and B, the type of curing agent and the concentration of any resinous organosiloxane copolymer described hereinafter. This optimum value can readily be determined by those skilled in the art with a minimum of experimentation, and is not part of this invention. For preferred compositions of this invention, the molar ratio of silicon-bonded hydrogen atoms to vinyl and other ethylenically unsaturated hydrocarbon radicals is between 1 and 2. 3. The Platinum Hydrosilation Catalyst and Optional Inhibitor Hydrosilation reactions are typically conducted in the presence of a catalyst that is a platinum group metal or a compound of such a metal. Platinum compounds such as hexachloroplatinic acid, and particularly complexes of these compounds with relatively low molecular weight vinyl-containing organosiloxane compounds are preferred catalysts because of their high activity and compatibility with the organosiloxane reactants. These complexes are described in U.S. Patent No. 3,419,593 that issued to David N. Willing on December 31, 1968. Complexes with low molecular weight organosiloxanes wherein the silicon-bonded hydrocarbon radicals are vinyl and either methyl or 3,3,3-trifluoropropyl are particularly preferred because of their ability to catalyze a rapid curing of the elastomer at temperatures of at least about 70°C. The platinum-containing catalyst can be present in an amount equivalent to as little as one part by weight of platinum per one million parts of curable composition. Catalyst concentrations equivalent to from 5 to 50 parts of platinum per million of curable composition are preferred to achieve a practical curing rate. Higher concentrations of platinum provide only marginal improvements in curing rate, and are therefore economically unattractive, particularly when the preferred catalysts are used. Mixtures of the aforementioned vinyl-containing reactants, curing agents and platinum-containing catalysts may begin to cure at ambient temperature. To obtain a longer working time or "pot life", the activity of the catalyst under ambient conditions can be retarded or suppressed by addition of a suitable inhibitor. Known platinum catalyst inhibitors include the acetylenic compounds disclosed in U.S. Patent No. 3,445,420, which issued on May 20, 1969 to Kookootsedes et al. Acetylenic alcohols such as 2-methyl-3-butyn-2-ol constitute a preferred class of inhibitors that will suppress the activity of a platinum-containing catalyst at 25°C. Compositions containing these catalysts typically require heating at temperatures of 70°C. or above to cure at a practical rate. If it desired to increase the pot life of a curable composition under ambient conditions, this can be accomplished using an olefinically substituted siloxane of the type described in U.S. Patent No. 3,989,667, which issued on November 2, 1976 to Lee and Marko. Cyclic methylvinylsiloxanes are preferred. Inhibitor concentrations as low as one mole of inhibitor per mole of platinum will in some instances impart satisfactory storage stability and cure rate. In other instances, inhibitor concentrations of up to 500 or more moles of inhibitor per mole of platinum are required. The optimum concentration for a given inhibitor in a given composition can readily be determined by routine experimentation and does not constitute part of this invention. 4. The Silica Filler To achieve the high levels of tear strength and other physical properties that characterize cured elastomers prepared using the compositions of this invention, the compositions must contain a reinforcing silica filler. The filler is treated with a silica treating agent to prevent a phenomenon referred to as "creping" or "crepe hardening" during processing of the curable composition. Any finely divided form of silica can be used as the reinforcing filler. Colloidal silicas are preferred because of their relatively high surface area, which is typically at least 50 square meters per gram. Fillers having surface areas of at least 300 square meters per gram are preferred for use in the present compositions. Colloidal silicas can be prepared by precipitation or a fume process. Both of these preferred types of silica are commercially available. The amount of finely divided silica used in the present compositions is at least in part determined by the physical properties desired in the cured elastomer. Liquid or pumpable polyorganosiloxane compositions typically contain from about 10 to about 60 percent by weight of silica, based on the weight of polydiorganosiloxane. This value is preferably from about 30 to about 50 percent. The silica treating agents are selected from liquid hydroxyl terminated polydiorganosiloxanes containing an average of from 2 to about 20 repeating units per molecule, and organosilicon compounds selected from hexaorganodisiloxanes and hexaorganodisilazanes that hydrolyze under the conditions used to treat the silica to form compounds with silicon-bonded hydroxyl groups. Preferably, at least a portion of the silicon-bonded hydrocarbon radicals present on the treating agent are identical to a majority of the hydrocarbon radicals present in ingredients A and B. A small amount of water can be added together with the silica treating agent(s) as a processing aid. It is believed that the treating agents function by reacting with silicon-bonded hydroxyl groups present on the surface of the silica particles to reduce interaction between these particles. 5. Optional Ingredients In addition to the vinyl-containing polydiorganosiloxanes, curing agent, catalyst and silica filler, the organosiloxane compositions of this invention can contain one or more additives that are conventionally present in curable compositions of this type. These materials are added to impart or enhance certain properties of the cured elastomer or facilitate processing of the curable composition. Typical additives include but are not limited to pigments, dyes, adhesion promoters, flame retardants, and heat and/or ultraviolet light stabilizers. 6. Preparation of Curable Compositions The silica filler can be treated in the presence of at least a portion of the other ingredients of the present compositions by blending these ingredients together until the filler is completely treated and uniformly dispersed throughout the composition to form a homogeneous material. The ingredients that are present during treatment of the silica typically include the treating agents and at least a portion of the polydiorganosiloxanes referred to herein as ingredients A and B. Because silica treatment is typically carried out at temperatures above ambient, the organohydrogensiloxane and platinum-containing catalyst are typically added after treatment of the silica has been completed. Irrespective of the type of mixer used, blending of the silica, filler treating agent(s), ingredients A and optionally, ingredient B is continued while the composition is heated at temperatures from about 100 to 250°C. under reduced pressure to remove volatile materials. The resultant product is the cooled prior to being blended with the organohydrogensiloxane (Ingredient C) and/or the platinum catalyst (Ingredient D), depending upon whether it is desired to prepare a one-part or two-part curable composition of this invention. The optional additives referred to hereinbefore can be added at this time or during blending of the silica with ingredient A. In-situ treatment of the silica can require anywhere from 15 minutes to 2 hours, depending upon the amount of material being processed, the viscosity of the material and the shear rate to which the material is subjected during processing. Alternatively, treatment of the silica can occur before the silica is blended with other ingredients of the present compositions. Methods for treating finely divided silica fillers prior to incorporating the silica into a polyorganosiloxane composition are known in the art. To ensure adequate blending of all ingredients the mixing equipment in which the present compositions are prepared should be capable of subjecting the composition to a high rate of shear. The advantage of using this type of a "high intensity" mixer to prepare silica filler polyorganosiloxane compositions is taught in U.S. Patent No. 3,960,804, which issued to Minuto on June 1, 1976. In accordance with the disclosure of this patent, the tip of the stirring device in the mixer is rotated at a speed of from 7.62 to 76.2 m/s (25 to 250 feet per second), which would generate considerable shearing forces. The exemplified compositions are blended in a Henschel high intensity mixer wherein the rotor was operated at a speed of 3800 revolutions per minute, equivalent to a rotor tip speed of 47.9 m/s (157 feet per second). Dough type mixers equipped with "sigma" shape blades, are not as efficient as mixers wherein the mixing surfaces are of a relatively flat "paddle" configuration. Examples of the paddle type mixers include the Henschel mixer disclosed in the aforementioned Minuto patent and certain mixers manufactured by Neulinger A.G. The blade is preferably rotated at a speed of at least 100 revolutions per minute. Curable compositions prepared using the present method typically exhibit viscosities of 0.5 up to 1000 Pa·s at 25°C. to facilitate blending and transfer of the compositions and minimize entrapment of air during mixing, a viscosity of less than 10 Pa·s at 25°C is preferred, particularly for extrudable compositions. 7. Fabrication and Curing of Shaped Articles The present curable compositions can be formed into shaped articles by press molding, injection molding, extrusion, or any of the other methods used to fabricate organosiloxane compositions. In the absence of one of the aforementioned catalyst inhibitors, the compositions will cure at ambient temperature over a period of several hours or days, or in several minutes when heated at temperatures of up to 250°C. Compositions containing one of these catalyst inhibitors are typically cured by heating them for several minutes at temperatures of from 50 to about 250°C. A preferred range is from 100 to 200°C. As discussed hereinbefore, cured elastomeric articles prepared using the curable compositions of this invention exhibit tear strengths above about 240 pounds per inch (42 kN/m) and tensile strengths above 9300 kPa without any adverse effect on the other desirable properties of the cured elastomer or the extrudability of the composition from which it is formed. This unique combination of properties make the elastomers desirable for a number of end use applications, including gaskets and other fabricated articles wherein at least a portion of the article is relatively thin and subjected to large amounts of stress. Articles of this type include diaphragms and bladders. The following example describes preferred curable compositions of this invention and the properties of elastomers prepared by curing these compositions. The example is intended to illustrate the present invention and should not be interpreted as limiting the invention as defined in the accompanying claims. Unless indicated to the contrary, all parts and percentages are by weight and all viscosities were measured at 25°C. EXAMPLE Curable organosiloxane compositions were prepared by blending to homogeniety in a dough type mixer the entire quantity of a fume silica having a nominal surface area of 250 m² per gram (ingredient E), two filler treating agents described hereinafter, water and an amount of a dimethylvinylsiloxy endblocked polydimethylsiloxane having a viscosity of about 50 Pa·s at 25°C. (ingredient A) equal to 1.3 times the weight of the filler. This mixture was heated for one hour by circulating steam through the jacket of the mixer while volatile materials were removed under reduced pressure. Following completion of the heating cycle, the remaining portion of ingredient A was added together with the entire amount of one of 4 different embodiments of ingredient B that are within the scope of this invention and 2 that are not. These embodiments are described hereinafter. These resultant compositions were then blended to homogeniety under ambient conditions. Two-part curable compositions were prepared by dividing this product into 2 equal parts. One of these parts was combined with 1) a trimethylsiloxy terminated polydiorganosiloxane having an average of five methylhydrogensiloxane units, three dimethylsiloxane units per molecule and containing from 0.7 to 0.8 weight percent of silicon-bonded hydrogen atoms as the curing agent (ingredient C) and 2) 0.05 parts of methylbutynol as a platinum catalyst inhibitor (ingredient F). The amount of ingredient C was equivalent to a molar ratio of silicon-bonded hydrogen atoms to vinyl radicals in the total curable composition of 1.8. The second part of the product from the silica treatment operation was combined with a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane that had been diluted with a liquid dimethylsiloxy terminated polydimethylsiloxane in an amount sufficient to achieve a platinum content of 0.7 weight percent (ingredient D), based on the weight of both parts of the curable composition. Four embodiments of ingredient B corresponding to the present invention were used in the compositions. Ingredient B1 was a dimethylvinylsiloxy terminated dimethylsiloxane/methylvinylsiloxane copolymer exhibiting a viscosity of 10 Pa·s and containing 1 mole percent of methylvinylsiloxane units. Ingredient B2 was a dimethylvinylsiloxy terminated dimethylsiloxane/methylvinylsiloxane copolymer exhibiting a viscosity of 10 Pa·s and containing 3 mole percent of methylvinylsiloxane units. Ingredient B3 was a dimethylvinylsiloxy terminated dimethylsiloxane/methylvinylsiloxane copolymer containing 5 mole percent of methylvinylsiloxy units and exhibiting a viscosity of 10 Pa·s. Ingredient B4 was a is a dimethylvinylsiloxy terminated dimethylsiloxane/methylvinylsiloxane copolymer exhibiting a viscosity of 0.3 Pa·s and containing 2 mole percent of methylvinylsiloxane units. For comparative purposes, a dimethylvinylsiloxy terminated polydimethylsiloxane containing no methylvinylsiloxane units and exhibiting a viscosity of 0.45 Pa·s (ingredient B5) and a liquid dimethylvinylsiloxy terminated dimethylsiloxane/methylvinylsiloxane copolymer exhibiting a viscosity of about 16 Pa·s containing 22 mole percent of methylvinylsiloxane units (ingredient B6) were used in place of an ingredient B of this invention containing from 1 to 5 mole percent of methylvinylsiloxane units. The combination of ingredient B5 with ingredient A provided a molecular weight distribution for vinyl-containing polydimethylsiloxanes that is within the range taught and claimed in U.S. Patent No. 4,162,243, issued to Lee et al. on July 24, 1979. The silica treating agents were (1) 1.0 part of a hydroxyl terminated diorganosiloxane copolymer wherein the repeating units consist essentially of dimethylsiloxane and methylvinylsiloxane units and the copolymer contains about 10 weight-percent of vinyl radical and about 16 weight percent of hydroxyl radicals; and (2) hexamethyldisilazane, used at a level of 8.9 parts in all but one of the formulations as specified in the following Table 1. The amount of water added to each of the compositions during treatment of the silica was 1.9 parts. Curable compositions were prepared by combining and mixing to homogeniety the two parts of each formulation. These compositions were cured in the form of sheets having a thickness of 1.9 mm. by placing the compositions in a hydraulic press and heating them for 5 minutes at a temperature of 150°C. Test samples were then cut from each of the sheets to determine the physical properties of the cured materials. The American Society of Testing and Materials (ASTM) test methods used to measure the various properties evaluated included ASTM-412 for tensile strength and elongation, ASTM-D625, Die B for tear strength and ASTM-D2240, Shore A scale for durometer hardness values. Table 1 summarizes the amounts of ingredients A, B, C and E present in each of the compositions evaluated. The physical properties of the cured compositions are summarized in Table 2. The data in Table 2 demonstrate that by using the curable compositions of this invention one is able to substantially improve the tear strength of cured elastomers relative to prior art elastomers prepared using extrudable organosiloxane compositions without adversely affecting other desirable properties of the cured elastomer such as tensile strength, hardness and elongation.

Claims: A curable organosiloxane composition comprising the product obtained by mixing to homogeneity: a polymer component consisting of: A. from 70 to 95 weight percent, based on the total weight of (A) and (B), of a first liquid diorganovinylsiloxy terminated polydiorganosiloxane represented by the average general formula: ViR₂SiO(R'₂SiO) x SiR₂Vi where Vi represents a vinyl radical, R and R' are individually monovalent or substituted monovalent hydrocarbon radicals selected from methyl, ethyl, chloromethyl, 3-chloropropyl, 3,3,3-trifluoropropyl, cyclohexyl and phenyl, with the proviso that at least one of the R' radicals is methyl, and x represents a degree of polymerization equivalent to a viscosity of from 20 to 200 Pa·s at 25°C; B. from 5 to 30 weight percent, based on the total weight of (A) and (B), of a second liquid diorganovinylsiloxy terminated polydiorganosiloxane that is miscible with said first polydiorganosiloxane and exhibits a viscosity of from 0.1 to 200 Pa.s at 25°C , where from 1 to 5 percent of the non-terminal repeating units of said second diorganovinylsiloxy-terminated polydiorganosiloxane contain a vinyl radical; C. an amount sufficient to cure said composition of an organohydrogensiloxane that is miscible with (A) and (B), and contains an average of more than two silicon-bonded hydrogen atoms per molecule, together with: D. a platinum hydrosilation catalyst in an amount equivalent to at least one part by weight of platinum per one million parts of curable composition; and E. from 10 to 60 weight percent, based on the weight of said composition, of a treated reinforcing silica filler, the treating agent being selected from liquid hydroxyl terminated polydiorganosiloxanes containing an average of from 2 to 20 repeating units per molecule and organosilicon compounds selected from hexaorganodisiloxanes and hexaorganodisilazanes that hydrolyze under the conditions used to treat the silica to form compounds with silicon-bonded hydroxyl groups. A composition according to Claim 1 where said second diorganovinylsiloxy terminated polydiorganosiloxane is represented by the average general formula: ViR''₂SiO(R'''₂SiO) y (R'''ViSiO) z SiR''₂Vi where Vi represents a vinyl radical, R'' and R''' are selected from the same group of monovalent hydrocarbon radicals and substituted monovalent substituted hydrocarbon radicals as R and R', the degree of polymerization represented by the sum of y and z is equivalent to a viscosity of from 0.1 to 200 Pa·s, and the ratio z/(y+z) is from 0.01 to 0.05.

Inventors: JENSEN JARY DAVID, JENSEN, JARY DAVID
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1988
Main classification: C08L83
IPC codes: C08L83, C08K5, C08K9, C08K3