Dehydrogenation catalyst

Abstract: This invention relates to an improved dehydrogenation catalyst, useful in converting alkylaromatics to alkenylaromatics, e.g. ethylbenzene to styrene, which contains lower amounts of iron and relatively larger amounts of cerium and potassium than those known to the art.

Description: This invention relates to improved catalysts for the dehydrogenation of hydrocarbons to corresponding more-unsaturated hydrocarbons, more particularly, to the production of vinyl aromatic hydrocarbons from alkyl aromatic hydrocarbons and to the production of olefins from the corresponding more saturated aliphatic hydrocarbons. The vinyl benzenes and butadienes play a particularly important role in the preparation of synthetic rubbers, plastics and resins. The polymerization of styrene, for example, with various comonomers such as butadiene to produce synthetic rubbers is well known as is the polymerization of styrene to produce polystyrene resins. Styrene and butadiene are typically produced from ethylbenzene and butylene, respectively, by dehydrogenation over solid catalysts in the presence of steam and at temperatures ranging from 500°C to 800°C. The class of catalysts found to be the most effective for this process contains a predominant amount of iron oxide, promoted by potassium carbonate, and stabilized by chromium oxide. Any improvement which results in either increasing the selectivity (moles of desired product produced per mole of reactant reacted) or the conversion (moles of reactant reacted per mole of starting material) without lowering the other is economically attractive since the result is that the yield (moles of desired product produced per mole of reactant) of the product has been increased. An increase of only a few tenths of a percent in the selectivity can result in a substantial savings of starting materials while an increase in conversion can substantially reduce capital expenditure and energy consumption. The prior art catalysts used in the dehydrogenation of alkyl aromatics to alkenyl aromatics, for example, ethylbenzene to styrene as previously discussed, are widely known. Early dehydrogenation patents describe the use of cerium oxide as the major active ingredient. Thus, for example, U.S. 1,985,844 discloses the use of cerium oxide precipitated on broken pieces of clay to dehydrogenate ethylbenzene below atmospheric pressure. U.S. 2,036,410 discloses the use of cerium oxide promoted with oxides of tungsten, uranium, and molybdenum. Various catalysts, the dehydrogenation conditions and other operating data are disclosed by Pitzer in U.S. 2,866,790 relating to the use of catalyst composition including potassium carbonate, chromium oxide, and iron oxide. Other catalysts and procedures are also shown by Gutzeit, U.S. 2,408,140; Eggertsen, et al, U.S. 2,414,585: Hills, et al, U.S. 3,360,579; U.S. 3,364,277; and U.S. 4,098,723. Belgium Patent 811,145 discloses the use of cerium in promoted iron oxide dehydrogenation catalysts. Belgium Patent No. 811,552, based on the principal patent above, discloses the use of cerium and molybdenum in potassium promoted iron oxide dehydrogenation catalysts. In these two patents iron oxide is 50 to 80 percent by weight, preferably 55 to 65 percent by weight. Cerium oxide is 0.5 to 10 percent by weight, most preferably 4 to 6 percent by weight. Potassium carbonate is present in a concentration of from 1 to 40 percent by weight. O'Hara, in U.S. 3,904 552, discloses the use of cerium and molybdenum in alkali promoted iron oxide dehydrogenation catalysts. The iron oxide is employed in the catalyst at 30 to 90 percent by weight, more preferably 55 to 90 percent by weight. O'Hara's preferred alkali metal compound is potassium carbonate and is employed in amounts in the range of 1.0 to 40 percent, preferably 5 to 25 percent by weight. Cerium oxide is employed in the range of from 0.5 to 10 percent by weight, most preferably 4 to 6 percent by weight. The use of cerium oxide in alkali promoted dehydrogenation catalysts with iron oxide percentages as low as 20 percent by weight has been disclosed. Thus, Macfarlane, in U.S. 3,223,743, teaches that it is very difficult to obtain a catalyst which has both high selectivity and high activity since, as one increases, the other usually decreases. To overcome this he teaches the use of two layers of catalyst, the first layer with high selectivity (lower activity) and a second layer with high activity (lower selectivity). The first layer with high selectivity and lower activity may contain 20 to 80 percent by weight iron and 0.5 to 5 percent by weight cerium oxide. Riesser, in U.S. 4,144,197, discloses the use of vanadium to improve the selectivity of a potassium promoted dehydrogenation catalyst containing 20 to 95 percent by weight ferric oxide and 0.01 to 50 percent by weight cerium oxide. Data in this patent is consistent with the teaching of Macfarlane with respect to vanadium addition since, by increasing the amount of vanadium, the selectivity of the catalyst is increased at the sacrifice of activity. Another patent disclosing the use of cerium as a promoter in iron oxide based catalysts is U.S. 4,467,046. The advantage of having a promoted dehydrogenation catalyst containing both cerium and potassium in high concentrations together with low concentrations of iron as related to the known art has not previously been recognized. Thus, catalysts containing more than 10 percent by weight cerium as cerium oxide and more than 40 percent by weight potassium as potassium carbonate and less than 30 percent iron as iron oxide have not been disclosed. It has now been discovered that a highly active and highly selective dehydrogenation catalyst which contains high concentrations of both cerium and potassium compounds and small amounts of iron, but without vanadium, can be achieved using only a single catalyst layer. The catalytic components are optionally promoted with molybdenum and/or chromium compounds. From these components unitary structures are made. i.e. pellets or extrudates, by adding hydraulic cement and other binders. The catalyst pellets are then calcined before use in a dehydrogenation process. An improved dehydrogenation catalyst useful in converting alkylaromatics to alkenylaromatics. e.g. ethylbenzene to styrene, has been discovered which contains a unique combination of relatively low amounts of iron and large amounts of cerium and potassium. Such catalysts give excellent conversions and selectivities. Catalysts in accordance with this invention contain less than 0.01 wt% of vanadium calculated as V 2 O 5 5 to 28 percent iron as Fe 2 O 3 , 40 to 60 percent potassium as K 2 CO 3 , and 10 to 60 percent cerium as Ce 2 O 3 as catalytic components together with a binder with the proviso that the weights of the components add up to 100%. Agents, such as graphite and cellulose, can also be added to improve the porosity. These, however, burn out during the calcination process. Cerium as used in the catalyst compositions of the present invention can be added to the catalyst in the form of cerium oxide or in the form of other cerium compounds which decompose upon calcination to form cerium oxide, as for example, cerium carbonate, cerium nitrate and cerium hydroxide. The catalyst compositions of the present invention contain, by weight, from 5 to 28 percent iron as Fe 2 O 3 , preferably from 15 to 28 percent, from 40 to 60 percent potassium as K 2 CO 3 , preferably from 45 to 55 percent and from 10 to 60 percent cerium as Ce 2 O 3 , preferably from 12 percent to 30 percent, with the proviso that the weights of the components add up to 100%, based on the total of the finished calcined catalyst. The dehydrogenation catalyst compositions of the present invention contain iron as an essential catalytic component. Many forms of iron oxide are used in preparing dehydrogenation catalysts. While various forms of iron oxide can be employed in the compositions of the present invention, the preferred form employed in the catalytic compositions of the present invention is red iron oxide or a mixture of red iron oxide (Fe 2 O 3 ) and yellow iron oxide (Fe 2 O 3 ·H 2 O). When the mixture of oxides is employed, 30 percent to 70 percent of the total moles of iron oxide is added as yellow iron oxide. The amount preferred is 40 to 60 molar percent of the yellow oxide and the most preferred is 50 molar percent. Particularly suited are pigment grade red and yellow iron oxides. The catalyst compositions of the invention contain from 5 percent to 28 percent by weight, preferably from 15 percent to 28 percent, of iron calculated as Fe 2 O 3 . The dehydrogenation catalyst compositions of the present invention also contain as a catalyst promoter, one or more potassium compounds. The potassium promoter material can be added to the catalyst in various forms. For example, it may be added as the oxide, or as other compounds which are convertible, at least in part, under calcination conditions, to the oxide. For example, the hydroxides, carbonates and bicarbonates are suitable. The potassium compound is preferably present in the catalyst as potassium carbonate or as a mixture thereof with potassium oxide. The present catalyst compositions comprise from 40 percent to 60 percent by weight, and preferably from 45 percent to 55 percent by weight, of potassium promoter compound, calculated as potassium carbonate. Other known catalyst additives can be included in the catalysts of the invention, but are not essential. Thus, an optional component of the catalyst composition of the invention is a chromium compound which serves as a stabilizer for the active catalytic components. Chromium compounds have, in fact, typically been added to alkali-promoted iron oxide catalysts to extend their life. Chromium, as used in the compositions of this invention, can be added to the catalyst in the form of a chromium oxide or in the form of chromium compounds which decompose upon calcination to chromium oxides, as for example, chromium nitrates, hydroxides and acetates. If potassium chromates are used, such materials can, of course, also contribute to the requisite concentration of potassium essentially present in the dehydrogenation catalyst compositions as hereinbefore discussed. Catalyst compositions herein optionally contain up to 5 percent by weight, preferably (when employed) from 1 percent to 3 percent, of a chromium compound, calculated as Cr 2 O 3. A second optional component, used to improve the selectivity of the catalyst, is molybdenum which can be added as its oxide or as a molybdate. The molybdenum component is present (when employed) in an amount up to 2.5 percent by weight, preferably 0.2 to 1.5 percent molybdenum, calculated as MoO 3 . The physical strength, activity and selectivity of the catalyst compositions of the present invention can be improved by adding certain binding agents. Binding agents can include, for example, calcium aluminate or Portland cement. These cements can be added individually or in combination. The catalyst should contain from 3 percent to 20 percent by weight hydraulic cement, preferably from 5 percent to 15 percent. Calcium sulfate which can also be added to the composition serves to supplement the binder component. The density of the catalyst composition herein can likewise be modified by the addition of various filler substances, for example, combustible materials such as graphite and methyl cellulose. Such materials can be added to the compositions during preparation but are burned out after the catalyst pellets have been formed during the calcining step. These porosity promoting aids can also facilitate extrusion of catalyst pellets. These fillers generally comprise up to 10 percent by weight of the catalyst composition, preferably from 2 to 8 percent. The catalyst compositions of the present invention generally are prepared by admixing the essential and desired optional components heretofore described and by drying and calcining the resulting mixture. Calcination temperatures can range from 500°C to 800°C, preferably from 550°C to 750°C. The catalyst compositions of the present invention can be prepared in various ways known to the art. One method comprises ballmilling together a mixture of the desired compounds, adding a small amount of water, and extruding the composite to produce small pellets, which are then dried and calcined. Another method is mixing the components together with water, drying them to form a powder and tabletizing. Another procedure involves mixing the components together with an excess of water, partially drying, and then subsequently extruding, drying and calcining the resulting pellets. The catalysts of the present invention are especially effective in promoting the dehydrogenation of ethylbenzene to produce styrene. Such a dehydrogenation reaction is usually carried out at reaction temperatures of from 500°C to 700°C. However, higher or lower temperatures may be used as are known to the art. The use of sub-atmospheric, atmospheric, or superatmospheric pressures are suitable. However, since it is preferred to operate at as low a pressure as is feasible, atmospheric or subatmospheric pressure is preferred. The process of the invention preferably is carried out as a continuous operation. It is preferred to utilize a fixed bed which may consist of a single stage or a series of stages of the same catalyst in one or several reactors. With the use of the catalyst of this invention, it is desirable to add steam to the hydrocarbon reactant feed to aid in the removal of carbonaceous residues from the catalyst. Steam to hydrocarbon weight ratios of from 0.8:1 to 5:1 are desirable depending on the compound being dehydrogenated. Best results are obtained with steam to hydrocarbon ratios above 1:1. The contact time of the reactant-containing gas with the catalyst is usually expressed in terms of liquid-hourly-space velocity (LHSV), which is defined as the volume of liquid hydrocarbon reactant per volume of catalyst per hour. The LHSV of the organic reactants, eg. ethylbenzene, according to this invention may vary from 0.3 to 10 and is preferably adjusted within this range to effect the degree of conversion desired for the particular feed in question. The catalysts of the present invention and their use will be further described by the following illustrative examples. It should be noted that advantages resulting from increases in selectivity of only a few tenths of a percent and/or increases in activity of a few degrees of temperature are extremely significant in a commercial process which may produce many hundreds of thousand pounds of product per day. Example 1. A catalyst according to the invention was prepared by mixing 22.0g red Fe 2 O 3 , 198.4 g cerium oxide, 4.0g CaSO 4 ·2H 2 O, 162.6g K 2 CO 3 , 20.4g Portland cement, 4.1g methyl cellulose and 39.4g graphite with enough water to make a wet paste. The mixture was dried at 150°C, ground to a powder, and pressed into 3/16-inch (4.8 mm) tablets. The tablets were calcined at 600°C for 1 1 / 2 hours and then at 750°C for 1 / 2 hour. Example 2. A catalyst was prepared according to the procedure of Example 1 except that the ratio of iron to cerium, was increased. Thus, 66.1g Fe 2 O 3 , 154.3g cerium oxide, 4.0g CaSO 4 ·2H 2 O, 162.6g K 2 CO 3 , 20.4g Portland cement, 4.1 g methyl cellulose and 39.4 graphite were used. Example 3. A catalyst according to the invention, using a mixture of iron oxides, was prepared, by dry blending 238.1g cerium carbonate [Ce 2 (CO 3 ) 3 ·5H 2 O], 120g calcium aluminate cement (trade name LUMNITE manufactured by Lehigh Cement Co.), 50g graphite, 10g methyl cellulose, 12.7 gypsum (CaSO 4 ·2H 2 O), 90.9g yellow iron oxide (Fe 2 O 3 ·H 2 O which drys to 80g Fe 2 O 3 ) having a surface area below 20m 2 /gm and an average particle size of less than 2 microns, and 80g red iron oxide (Fe 2 O 3 ) having a surface area of 5m 2 /gm and an average particle size of 1 micron. Potassium carbonate, 500g, was dissolved in 500g water and mulled with the dry-blended ingredients. After drying the mixture to a moisture content of 10 percent, it was pelleted, 1/8" pellets (3.2 mm). The pellets were dried at 150°C for 1 / 2 hour, then calcined at 600°C for 2 to 3 hours. The weight percentage compositions of the finished calcined catalysts of Examples 1-3 are given in Table I, the balance of the total catalyst composition being the cementitious binder. Catalyst of Example Wt. % Component Fe 2 O 3 Ce 2 O 3 K 2 CO 3 , 1 5.4 48.8 40.0 2 16.3 37.9 40.0 3 17.0 16.0 53.2 The catalysts prepared in Examples 1-3 were tested for activity and selectivity by using them in the dehydrogenation of ethylbenzene to styrene by loading the catalyst into one of two fixed bed reactors having a volume of 70 and 100 cc, respectively, and passing a preheated mixture of steam and ethylbenzene at a weight ratio of 1.0:1 or 1.5:1 into the catalyst bed, which was maintained at the temperature required to obtain the desired conversion (∼50 percent) of ethylbenzene. The reactor pressure was maintained at essentially atmospheric. The liquid hourly space velocity (LHSV) of ethylbenzene was kept at 1.0. The effluent crude product was analyzed, the activity and selectivity to styrene were calculated and the results are shown in Table II. Catalyst of Example Temp. °C Conversion Selectivity S/O LHSV 1 597 50.0 96.5 1.06 1 2 594 51.2 96.7 1.50 1 3 591 49.9 96.8 1.52 1 Example 4. Another catalyst of the invention was prepared by dry-blending 130 g red iron oxide, 148 g yellow iron oxide, 158.7 g Ce 2 (CO 3 ) 3 ·5H 2 O (63 percent cerium oxide), 120 g calcium aluminate cement (LUMNITE), 12.7 g CaSO 4 ·2H 2 O, 50 g amorphous graphite, 10 g of methyl cellulose and 450 g K 2 CO 3 . Enough water was added to these components so as to provide 10 percent moisture. The mixture was then mulled and pelleted (5/32")and the pellets were calcined at a temperature of from 550 to 650°C for two and one half hours in flowing air. The weight percentages of this catalyst, as shown in Table III, were calculated by expressing the yellow iron oxide as Fe 2 O 3 , the cerium carbonate as Ce 2 O 3 , and the CaSO 4 ·2H 2 O as CaSO 4 . The red iron oxide, K 2 CO 3 , and the cement were considered to remain unchanged while the graphite and methyl cellulose were considered to be burned out during the calcination step. The catalyst was tested for activity and selectivity in the reaction for dehydrogenating ethylbenzene to styrene by placing 70 ml of the above catalyst pellets in a fixed bed reactor and passing a preheated mixture of steam and ethylbenzene at a weight ratio of 1.5:1 through the bed which was maintained at a temperature to give the desired conversion of ethylbenzene, this temperature being dependendent upon the activity of the particular catalyst. The LHSV was 1.0 and the pressure was maintained at atmospheric. The results are shown in Table III. Examples 5-14. Other catalysts were prepared in the manner of Example 4. The cement employed was the calcium aluminate used in Example 3. Graphite and methyl cellulose were added in the same weight percentages, i.e. 5 percent and 1 percent, respectively, and the compositions were calculated and expressed as in Example 4. Pellets having the same diameter were extruded and calcined at the same temperature as in Example 4. The compositions and results of use are shown in Table III. The activity of each catalyst is indicated by the temperature required to obtain 58 percent conversion of ethylbenzene. The selectivity is the percentage of converted product which is styrene. Component Example No. (Weight Percent) 4 5 6 7 8 9 10 11 12 13 14 Fe 2 O 3 27.6 9.6 17.0 16.6 16.5 17.0 17.0 22.2 22.3 27.6 25.8 K 2 CO 3 47.9 47.8 47.8 46.8 46.4 58.4 53.1 47.9 47.8 47.9 44.6 Ce 2 O 3 10.5 21.2 15.9 15.6 15.5 10.6 15.9 12.8 15.9 10.6 11.9 Cement 12.8 18.0 18.0 17.7 17.5 12.7 12.7 12.8 12.7 12.8 11.9 CaSO 4 1.1 3.2 1.1 3.1 3.1 1.1 1.1 3.2 1.1 1.1 1.6 MoO 3 0.0 0.2 0.2 0.2 1.0 0.2 0.2 1.1 0.2 0.2 1.0 Cr 2 O 3 3.2 T(°C) at 58% conv. 605 598 605 598 600 608 602 598 597 602 595 % Selectivity 95.8 95.5 96.0 96.3 95.7 96.2 95.9 95.8 96.1 95.9 95.8 Comparative Example A preferred catalyst of the prior art (Example 1, U.S. Patent 3,904,552) was prepared by the same procedure used to produce catalysts of the present invention. The following components were thoroughly mixed with water to a suitable consistency for extrusion. Components Parts by Weight Fe 2 O 3 600 K 2 CO 3 210 Portland Cement 115 MoO 3 25 Ce 2 (CO 3 ) 3 ·5H 2 O 79.4 The paste was extruded to form pellets having 5/32 to inch (4 mm) diameter. The pellets were calcined in air at 550 to 650°C for three hours (ramped temperature). The components added were equivalent to 60 percent Fe 2 O 3 , 21 percent K 2 CO 3 , 11.5 percent Portland cement, 2.5 percent MoO 3 , and 5.0 percent Ce 2 O 3 . A temperature of 601°C was required to give 50 percent ethylbenzene conversion at a steam/oil ratio of 1.5 and an LHSV of 1.0. A selectivity to styrene of 95.7 percent was achieved under these conditions. By comparison catalysts of the present invention (average of Examples 4-14, inclusive) produced a conversion of 58 percent at the same temperature with no loss in selectivity.

Claims: A dehydrogenation catalyst composition containing less than 0.01 wt% of vanadium calculated as V 2 O 5 which comprises as catalyst components cerium as Ce 2 O 3 , potassium as K 2 CO 3 and iron as Fe 2 O 3 in amounts of from 10 to 60 percent from 40 to 60 percent and from 5 to 28 percent, respectively, with the proviso that the weights of the components add up to 100%, all by weight in the finished catalyst. A composition as claimed in Claim 1 wherein the amounts of cerium, potassium and iron are from 12 to 30 percent, 45 to 55 percent and 15 to 28 percent, respectively. A composition as claimed in Claim 1 or 2, wherein a cement binder is additionally present. A composition as claimed in Claim 3 wherein the cement binder is Portland cement or a calcium aluminate cement. A composition as claimed in Claim 3 or 4 wherein a portion of the cement binder is replaced by CaSO 4 . A composition as claimed in Claims 3-5 wherein the amount of cement binder is 3-20 wt.% of the total of the composition. A composition as claimed in Claims 1-6 therein the catalyst contains chromium or molybdenum promoters or a mixture thereof. A composition as claimed in Claim 7 wherein the chromium promoter is present in an amount of up to 5 percent, calculated as Cr 2 O 3 . A composition as claimed in Claim 7 or 8 wherein the molybdenum is present in an amount of up to 2.5 percent, calculated as MoO 3 . In a process for dehydrogenating an alkylaromatic compound in which said compound is heated together with steam in the presence of an iron-containing catalyst, the improvement which comprises employing a catalyst according to claims 1-9. A process as claimed in Claim 10 wherein the catalyst contains cerium, potassium and iron in amounts of from 12 to 30 percent, 45 to 55 percent and 5 to 28 percent, respectively. A process as claimed in Claim 10 or 11 wherein the catalyst also contains promoting amounts of molybdenum, chromium or mixtures thereof. A process as claimed in Claims 10-12 wherein the catalyst also contains a binder.

Inventors: SHERROD FRED ALLEN, SMITH RAY ALLEN, SHERROD, FRED ALLEN, SMITH, RAY ALLEN
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1988
Main classification: B01J23
IPC codes: C07C1, B01J23, C07C67, C07B35, C07B61, B01J27, C07C11, C07C5, C07B31, C07C15