NOVEL STOVING LACQUERS AND THEIR USE

Abstract: Stoving lacquers which are especially useful in "coil coating" and provide a finish on a reflective substrate (1) simulating that of a metallic lacquer comprise a stovable coloured film-forming binder (2) composition having colourless transparent particles (3) dispersed therein.

Description: This invention relates to stoving lacquers especially useful in so called "coil coating". So called "metallic lacquers" provide a characteristic finish which is widely used for coating mainly metallic articles such as for example claddings for buildings, slatted blinds, and motor vehicle panels. The characteristic optical effect is caused by variations in light reflection and intensity which vary with the angle of observation and over the lacquer surface. In the known metallic lacquers the visual effect is produced by the presence of metallic pigments in the form of minute metallic flakes embedded in a clear and usually coloured binder. In place of the metallic flakes it is also possible to use mica flakes provided with a titanium dioxide deposit. Such metallic lacquers are expensive and not always very stable, either to light or in their resistance to acid and alkalis. Moreover, they are liable to go cloudy on application and may need to be provided with additional protective layers. The present invention provides a stoving lacquer which when applied to a reflective surface and stoved, gives an optical effect similar to that of a metallic lacquer, while avoiding at least some of the disadvantages of the latter. A reflective substrate in accordance with the present invention is provided with a stoved lacquer layer formed from a stoving lacquer which comprises a stovable transparent film-forming binder composition having dispersed therein transparent thermoplastic particles having particle sizes in the range of 2 to 50 micrometers, with a maximum diameter up to 1.2 x (thickness of the stoved layer) in cases where the particles flow appreciably during the stoving operation, and up to substantially the thickness of the stoved lacquer layer in cases where the particles do not substantially flow during the stoving operation, the said binder composition and the said particles being such that one is substantially colourless and the other is coloured with transparent pigment, and that in the stoved lacquer layer, the particles remain as a separate phase and do not substantially protrude from the surface of the stoved lacquer layer, the particle sizes being such that the stoved layer contains both coloured and substantially colourless, transparent zones through the thickness of the said layer and colourless transparent zones extending partly through the said layer, so that the layer has an uneven colour intensity. When such a stoving lacquer is applied to the reflective surface of a stoving heat resistant substrate and stoved, minute "windows" are formed in the stoved lacquer layer, through which the reflective surface to which the lacquer has been applied may be seen. It is not necessary that such windows shall necessarily extend completely through the thickness of the layer provided that the "window" is sufficiently transparent to permit substantial reflection of light from the reflective surface of the substrate. The "windows" are randomly distributed throughout the stoved lacquer layer and are more or less irregular in outline so that the reflectiveness of the stoved layer is strongly dependent upon the position and angle of view. In addition to the selection of the binder to meet the essential requirement that the particles remain as a phase separate from the binder after stoving, the material, size and volume of the particles as well as the stoving conditions and the consequent extent of particle-flow and particle-agglomeration should be chosen and balanced to achieve the required optical effect. In this respect the extent of the flow or the agglomeration or of both may be zero. In the accompanying drawings Figure 1 shows in cross-section a diagrammatic representation of a stoved layer produced from a stoving lacquer in accordance with the present invention. The reflective substrate 1 carries the stoved binder layer 2 in which are minute "windows" formed of the transparent particles 3. Figure 2 shows an alternative type of layer in which the substrate 1 carries the stoved binder layer 2 in which the transparent particles 3 have fused to form a network of fused particles shaped separate strips. The film-forming binder composition used in the stoving lacquers may be of known kind provided that it is transparent and preferably coloured. Suitable such composition may be based on polyurethanes, polyesters or polyacrylates which can be cured by heating. While the binder composition is preferably thermo-setting, i.e. is cured during the stoving operation, it is also possible to use stovable binder compositions based on thermoplastic resins which have adequate durability and hardness for the envisaged end use. Suitable compositions may be based on cross-linkable polyesters, which may be combined with thermosettable aminoplast resins based on for example benzoguanamine or melamine. Other suitable compositions may be based on cross-linkable blocked polyurethane resins which may be combined with thermoplastic resins such as cellulose acetate butyrate. Thermoplastic stovable compositions may be based on, for example, polyvinyl chloride or another vinyl copolymer, which may be hardened by the inclusion of a thermosetting resin such as an epoxy resin or a melamine-based resin. The binder composition, may, if desired, include a plasticiser to ensure adequate flexibility of the stoved layer and/or a flow additive to facilitate formation of a coating of even thickness. The usual stabilizers, against ultra-violet light, may be included. Stovable film-forming binder compositions normally contain a solvent which is evaporated during the stoving operation. The solids content is usually 40 to 80% by weight, expressed as the weight percentage of total solids (not including the transparent particles mentioned above) based on the total weight of the binder composition. The metallic effect produced by the stoving lacquers of the present invention depends in part on providing a colour contrast between the transparent film forming binder and the transparent particles. This is normally achieved by using colourless transparent particles and including transparent pigments in the binder composition. Such pigments are known in the art and include for example yellow, red and black forms of iron oxide pigment and lamp black. Other transparent pigments including organic pigments may be used, the choice depending upon the desired colour and the required degree of durability, especially light fastness. The transparent particles included in the stoving lacquers of the invention must not dissolve in or react with the film forming binder composition. Thermoplastic particles are normally preferred. They may be made from, for example, polyvinylidenedifluoride, polyvinylfluoride, polytetrafluoroethylene, a polyamide, especially nylon 10, nylon 11 or nylon 12, or polypropylene. The transparent particles have particle sizes of 2 to 50 micrometers, preferably 10 to 20 micrometres. They are preferably included in the novel stoving lacquers in a proportion of 3 to 30% by weight based on the film-forming binder composition (total wet lacquer) or 5 - 70% by weight based on the stoved layer produced from the lacquer. The preferred proportions, in the case of particles less than 10 micrometres in size, are 5 - 10% by weight based on the wet stoving lacquer and 10 to 20% by weight on the stoved layer produced therefrom. In the case of transparent particles having a particle size greater than 10 micrometres, the preferred proportions are 10 to 25% by weight based on the wet stoving lacquer and 20 to 50% by weight based on the stoved layer obtained therefrom. Particularly attractive visual effects are obtained using colourless transparent polyamide particles having a particle size of about 5 micrometres, which are present in the stoving lacquers in a proportion of 5 to 10% by weight of the total wet lacquer. The layer formed from the stoving lacquer in accordance with the present invention may have the usual thickness for a layer obtained from a stoving lacquer, e.g. 2 to 50 micrometres, preferably 4 to 40 micrometres. The maximum size (diameter) of the transparent particles is up to 20% greater than the expected thickness of the stoved lacquer layer in those cases where the particles flow appreciably during the stoving operation. In this situation, the flow of the particles during the stoving ensures that there is no substantial protrusion of the particles above the surface of the stoved layer and a smooth surface is obtained which is essential for a satisfactory optical appearance of the stoved layer. If the transparent particles flow at the stoving temperature, they may have a diameter substantially smaller than the expected thickness of the stoved layer. In some embodiments of the invention, the materials and stoving conditions are chosen so that the particles normally agglomerate and form larger particles. With some combinations of particles and binder, a net work of fused particles or a multitude of irregularly shaped separate strips, which are an initial stage in the net work forming process, can be formed, and this produces an excellent optical effect. This type of layer is shown diagrammatically in the accompanying Figure 2. In some cases, for example with a large volume of very fine particles, a continuous layer of molten particles may be deliberately or accidentally formed, either directly between the substrate and the binder or over the binder. Such layer, if sufficiently thin and transparent and of appropriate colour intensity, can still give acceptable results if special effects are required, but it reduces reflection intensity. Too high a proportion of the particles will always prevent the desired optical effects being obtained. If the transparent particles do not substantially flow during the stoving operation, the particles have a size which is the same as, or only slightly less than, the thickness of the stoved lacquer layer. In such a case it is also desirable to ensure that the shape of the individual particles is such as to facilitate the formation of the desired windows. More particularly highly irregular shapes should be avoided. The new stoving lacquers are especially suitable for application to reflective and particularly metallic surfaces, e.g. of aluminium. The binder composition is formulated to have satisfactory adhesion to the substrate. In place of metallic surfaces, it is also possible to use other reflective surfaces including especially surfaces of transparent plastics materials which have been metallised on the reverse side. The stoving operation may be carried out at temperatures up to 300°C, e.g 100 to 300°C for times from, e.g., 15 seconds to 30 minutes, depending on the temperature used. In the following Examples, the lacquer is a stoving lacquer for use in so called "coil" coating. In this process, a layer of lacquer is applied by means of a coating roller to one or both sides of an aluminium strip which is supplied from a roll, after which the strip is passed continuously through a muffle furnace, where the strip is heated to a temperature (measured as the temperature of the metal) of which the maximum value is given in each Example. The residence time in the furnace is about 30 seconds. During the heating the solvent present in the binder composition evaporates after which the strip is cooled and wound up again as a roll. During the rolling up, the lacquer layer is already dry and cured. If desired more than one lacquering station may be used, e.g. to apply a special primer or special finish to the strip. EXAMPLE I BRASS-COLOURED LACQUER Component Type Component Material Proportion by Weight Transparent polyester L818 (60% in S150) 62.0 Resin benzoguanamine resin 15.0 hexamethoxymelamine 4.6 Solvent diacetone-alcohol 20.0 Solvesso 100 15.0 Catalyst paratoluene-sulphonic-acid 0.5 Transparent Pigment yellow iron oxide (micronised) 1.8 Transparent Particles polyamide-12 (max. particle diameter 10µm) 14.0 This lacquer is suitable for stoving at 225 o C for 60 seconds. The base material can be aluminium, e.g. alu-strip, or other material with a normal, glossy or highly reflective surface. Alternative materials are laminated materials having a metal or metallized surface layer. The same effect can be obtained if the surface to be coated has a metallic appearance and the surface does not have to consist of metal. EXAMPLE II The base material can be aluminium, e.g. alu-strip, or other material with a normal, glossy or highly reflective surface. Alternative materials are laminated materials having a metal or metallized surface layer. The same effect can be obtained if the surface to be coated has a metallic appearance and the surface does not have to consist of metal. EXAMPLE III BRONZE - COLOURED LACQUER Component Type Component Material Proportion by Weight Transparent Resin a)vinylchloride/vinylpropionate copolymer (Lutofan 210, BASF) 50% in ethylacetate 50.0 b)epoxy resin (Epikote 828, Shell) 15.0 c)55% melamine resin (Luwilpal 030, BASF) 2.0 Plasticizer ethylhexylphthalate (Palatinol AH, BASF) 2.8 Solvent Solvesso 100 15.0 Butyl-acetate 24.0 ethyleneglycol-diacetate 10.0 Transparent Pigment yellow iron oxide 0.8 black iron oxide 0.4 Clear Particles polyamide 12, max. particle size 20 µm 20.0 This lacquer is suitable for stoving at 245 o C for 60 seconds. The base material can be aluminium e.g. alu-strip, or other material with a normal, glossy or highly reflective surface. Alternative materials are laminated materials having a metal or metallized surface layer. The same effect can be obtained if the surface to be coated has a metallic appearance and the surface does not have to consist of metal.

Claims: A reflective substrate provided with a stoved lacquer layer formed from a stovable, transparent film-forming binder composition having dispersed therein transparent thermoplastic particles having particle sizes in the range of 2 to 50 micrometers, with a maximum diameter up to 1.2 x (thickness of the stoved layer) in cases where the particles flow appreciably during the stoving operation, and up to substantially the thickness of the stoved lacquer layer in cases where the particles do not substantially flow during the stoving operation, the said binder composition and the said particles being such that one is substantially colourless and the other is coloured with transparent pigment, and that in the stoved lacquer layer, the particles remain as a separate phase and do not substantially protrude from the surface of the stoved lacquer layer, the particle sizes being such that the stoved layer contains both coloured and substantially colourless, transparent zones through the thickness of the said layer and colourless transparent zones extending partly through the said layer, so that the layer has an uneven colour intensity. A reflective substrate provided with a stoved lacquer layer according to claim 1 in which the said transparent particles have a particle size less than 10 micrometers and are present in a proportion of 5 to 10 % by weight based on the wet stoving lacquer. A reflective substrate provided with a stoved lacquer layer according to claim 1 in which the said transparent particles have a particle size greater than 10 micrometers and are present in a proportion of 10 to 25% based on the wet stoving lacquer. A reflective substrate provided with a stoved lacquer layer according to claim 3 in which the said transparent particles have a particle size in the range 10 to 20 micrometers. A reflective substrate provided with a stoved lacquer layer according to any of claims 1 to 4 in which the said transparent particles are polyamide particles, preferably nylon-11 or nylon-12 particles. A reflective substrate provided with a stoved lacquer layer according to any one of claims 1 to 5 in which the said binder composition in the wet stoving lacquer contains 40 to 80% solids not including the said transparent particles. A reflective substrate provided with a stoved lacquer layer according to any one of claims 1 to 6 in which the transparent particles are colourless. A reflective substrate provided with a stoved lacquer layer according to any one of claims 1 to 7 in which the transparent pigment is red or black iron oxide and/or lamp black. A reflective substrate provided with a stoved lacquer layer according to any one of claims 1 to 8 in which the transparent particles have a softening temperature such that they flow at the stoving temperature of the said binder composition. A reflective substrate provided with a stoved lacquer layer in which the substrate is the surface of a metal, preferably aluminium, and the particles of the stoved lacquer layer are polyamide particles, preferably of nylon-12.

Inventors: DE JONG, HENDRIKUS
Applicants: HUNTER DOUGLAS INDUSTRIES B.V.
Application year: 1988
Main classification: C09D5
IPC codes: C09D5, C09D177