METHOD OF IMPROVING THE RESISTANCE TO SUNLIGHT, AND FORMED ARTICLES

Abstract: The resistance to discolouring of formed articles from polymer mixtures which comprise a polyphe­ nylene ether and at least a second polymer can be improved by treating the surface of the formed articles with a solvent. The solvent is chosen so that the polyphenylene ether does dissolve therein, but the second polymer does not dissolve therein.

Description: The invention relates to a method of improving the resistance to sunlight of articles formed by injection molding from polymer mixtures which comprise a polyphenylene ether and at least one or more of the following: a polyamide, a polyolefin, a polyalkylene terephtalate, a polyetherimide, a polyacetal as a second polymer. The invention also relates to the articles thus obtained. It is generally known that articles formed from polymer mixtures which comprise a polyphenylene ether discolour when exposed to sunlight. This discoloration also occurs in articles formed from polymer mixtures which, in addition to a polyphenylene ether, comprise a second polymer. In practice various measures are used to solve this problem. It has been suggested to incorporate stabilisers in the polymer mixture. This measure results in an improvement of the resistance to sunlight. Sometimes the formed articles are provided with a lacquer layer which provides protection. The invention provides a further solution to the above mentioned problem. The method according to the invention is characterised in that the surface of the formed article is treated with a solvent for a sufficiently long period of time to remove at least a part of the polyphenylene ether, the solvent being chosen to be so that the second polymer does not dissolve therein. EP-A-267 382 describes the analysis of polyphenylene ether - polyester or polyamid blends, by extracting the unreacted polyphenylene ether with a suitable solvent and analysing the residue. For extractive analysis one uses small divided particles to ensure complete extraction. It has been found that articles having a considerably improved resistance to sunlight can be obtained by means of the method described hereinbefore. The articles which are treated according to the method of the invention have been manufactured entirely or partly from polymer mixtures. They are manufactured by injection moulding from the polymer mixture. The polymer mixture from which the articles have been manufactured comprises at least a polyphenylene ether and a second polymer. The second polymer is generally chosen to be so that it satisfies the following two conditions: a. it must have a resistance to sunlight better than that of polyphenylene ethers, and b. it must be possible to find a solvent or solvents in which the second polymer is less readily soluble than the polyphenylene ether. Various polymer mixtures are known which comprise a polyphenylene ether. In the method according to the invention especially the polymer mixtures known per se are suitable which, in addition to a polyphenylene ether, comprise a polyamide, a polyolefin, a polyalkylene terephthalate, for example, polybutylene terephthalate and polyethylene terephthalate, a polyether imide, a polyacetal and/or a polyolefin. These polymer mixtures generally comprise 1-80% by weight, preferably 1-70% by weight, of polyphenylene ether and 99-20% by weight, preferably 99-30% by weight, of a second polymer. Even more preferably, the content of the second polymer is chosen between the limits mentioned hereinbefore so that the second polymer in the polymer mixture forms the continuous phase in which the polyphenylene ether is dispersed. The way in which the method according to the invention is performed is not critical: for example, the formed article may be immersed for some time in the solvent chosen. It is also possible to spray solvent on the surface of the formed article. The solvent may be a mixture of one or more organic liquids. It is only of importance that the polyphenylene ether dissolves in the solvent better than the second polymer. Examples of solvents used in the treatment of articles formed from polymer mixtures which comprise a polyphenylene ether are aromatic hydrocarbons, for example, benzene, toluene, xylene, petrol, halogenated especially chlorinated hydrocarbons, for example, methylene chloride, chloroform and trichloroethylene. The article which are treated according to the method of the invention have been manufactured from polymer mixtures which comprise a polyphenylene ether. Polyphenylene ethers are compounds known per se . For this purpose, reference may be made to numerous patent publications. A survey of suitable polyphenylene ethers is described, for example, in WO 87/00540. Polymer mixtures which, in addition to a polyphenylene ether, comprise a second polymer and which are suitable for the manufacture of articles which can be treated according to the method of the invention are known per se . By way of example, reference may be made to WO 87/00540 in which polymer mixtures are described which comprise a polyamide as the second polymer; to WO 87/00850 in which polymer mixtures are described which comprise a polyester as the second polymer; to US-4,431,779 in which polymer mixtures are described which comprise a polyether imide as the second polymer, and to EP-A-133487 in which polymer mixtures are described which comprise a polyolefin as the second polymer. The articles may also be manufactured from polymer mixtures which comprise more than two polymers. Examples of such polymer mixtures are polymer mixtures which comprise a polyphenylene ether, one or more of the polymers mentioned hereinbefore, and polymers or copolymers derived from vinylaromatic monomers. Such polymer mixtures are described, for example, in EP-A-0046040, EP-A-0221341 and EP-A-0222129. The invention will now be described in greater detail with reference to the ensuing specific example. EXAMPLE I A polymer mixture was prepared from 49 parts by weight of polyphenylene ether (a poly (2,6-dimethyl-l,4-phenylene) ether with an intrinsic viscosity measured in CHCl₃ at 25°C of 46 dl/g), 41 parts by weight of polyamide 6.6 having a number-averaged molecular weight M of 20,000 and a viscosity index measured according to ISO R307 (0.5 g of polyamide dissolved in 100 g of 90% formic acid at 25°C) of 135 ml/g and a moisture content of approximately 0.20% by weight, 10 parts by weight of a non-hydrogenated styrene-butadiene-styrene block copolymer, 0.7 parts by weight of citric acid-1-hydrate, and 4.4 parts by weight of pigments (of which 4.0 parts by weight of TiO₂). The said constituents were processed in a double-blade extruder to form a polymer mixture in pellet form. A large plate (thickness approximately 3 mm) was manufactured from the resulting polymer mixture by injection moulding. Two small samples were sawn from the plate. The first sample (sample A) was immersed for 6 minutes in a 50/50 mixture of toluene/isooctane ("fuel C"). The second sample (sample B) was not treated. Both samples were exposed on one side (in the Netherlands) to natural sunlight behind a glass plate for 30 months. After termination of the test period, the yellowness index and the discolouring according to CIELAB (DIN 6174) of both samples were determined. The discolouring (delta E ab* ) was determined in comparison with the colour of the side of the same sample not exposed to sunlight. The found and calculated values are recorded hereinafter: Sample Yellowness index Delta E ab* A. unexposed side 20.9 exposed side 35.6 9.9 B. unexposed side 20.2 exposed side 53.0 22.5 It may be seen from the results obtained that the discolouring of the treated sample is less than that of the non-treated sample. In particular, as appears from the yellowness index, less yellowing occurs. EXAMPLE II In the same manner as described in example I, two samples C and D were manufactured from a polymer mixture consisting of 36 parts by weight of the same polyphenylene ether, 0.7 parts by weight of citric acid-1-hydrate, 19 parts by weight of high-impact polystyrene, 8 parts by weight of the same styrene-butadiene-styrene block copolymer, 37 parts by weight of the same polyamide-6,6 and 4.4 parts by weight of pigments (of which 4.0 parts by weight of TiO₂). The samples C and D were treated and exposed to light in the same manner as described in Example I. The results obtained were as follows. Sample Yellowness index Delta E ab* C. unexposed side 17.5 exposed side 25.0 4.8 D. unexposed side 17.4 exposed side 40.8 15.4 In this case also the method according to the invention resulted in an improvement of the colourfastness.

Claims: A method of improving the resistance to sunlight of articles formed by injection molding from polymer mixtures which comprise a polyphenylene ether and at least one or more of the following: a polyamide, a polyolefin, a polyalkylene terephtalate, a polyetherimide, a polyacetal as a second polymer, characterised in that the surface of the formed article is treated for a sufficiently long period of time with a solvent so as to remove at least a part of the polyphenylene ether, the solvent being chosen so that the second polymer does not dissolve therein. A method according to claim 1 wherein the polymer mixture comprises as a second polymer one or more of the following polymers: a polyolefin, a polyetherimide, a polyacetal. A method as claimed in Claim 1 of treating articles formed from polymer mixtures which comprise a polyphenylene ether and a polyamide, characterised in that the formed article is treated with a chlorinated hydrocarbon. Formed articles having an improved resistance to sunlight obtained by using the method as claimed in claims 1-3.

Inventors: VAN DE MEER, ROELOF GENERAL ELECTRIC PLASTICS B.V.
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1988
Main classification: C08J7
IPC codes: C08J7