TONER FOR DEVELOPING ELECTROSTATICALLY CHARGED IMAGE

Abstract: This improved toner for developing electrostatically charged images is composed of associated secondary particles contg. prim. particles of an acidic or basic polar gp.-contg. polymer, colourant particles, and an optional charge controlling agent. The secondary particles form a membrane and their points of contact are pref. partially fused. The toner is produced in the following process, (1) the colourant and charge controlling agent are added to the polymer emulsion. (2) the emulsion is then heated with stirring at 20-45 deg.C for 1-3 hrs. (3) the temp. is then raised for 1-3 hrs. to a point higher than the glass transition point, but less than 65 deg.C higher (4) the produced associated particles are then filtered in stages, (5) the particles are then dried. The toner can also contain a carrier such as iron pieces, glass pieces, etc. Typically, the glass transition point of the basic polymer used for producing the toner is 90-100 deg.C (pref. 30-100 deg.C best 10-60 deg.C).

Description: This invention relates to a toner for developing an electrostatically charged image in electrophotography, electrostatic recording, electrostatic printing, etc., and a developer containing it. Toners generally used widely heretofore are produced by dry-blending a styrene/acrylate-type copolymer powder obtained by suspension polymerization with a coloring agent such as carbon black and optionally a charge controlling agent and/or a magnetic material, melt-kneading the mixture by an extruder or the like, and then pulverizing and classifying the kneaded mixture (see Japanese Laid-Open Patent Publication No. 23354/1976). With the conventional toners obtained by the above melt-kneading/pulverizing method, controlling of the particle diameter of the toners is limited, and it is substantially difficult to produce toners having an average particle diameter of not more than 10 µm, especially not more than 8 µm , above all not more than 5 µm , in good yields. Moreover, it is difficult to avoid the defect that developers prepared from the toners have a low resolution and poor chargeability and fogging occurs. It has also been proposed to produce a toner by copolymerizing monomers in the presence of a coloring agent. The product, however, still has the defect that it has insufficient chargeability and fogging occurs. US-A-4 789 617 discloses toners which are particles composed of a polymer and a colorant in which particles of a monomer composition dispersed in an aqueous medium are polymerized. These are not associated particles of secondary particles comprising primary particles of a polymer having a particle diameter of 0.05 to 0.5 µm and particles of a coloring agent (cf. column 11, lines 14 to 16). According to US-A-4 789 617 a cyclized rubber or a polar polymer may be added in an amount of 0.5 to 50 wt. parts based on 100 wt. parts of the polymeric monomer. In the working examples, however, the polymer from the polymeric monomer per se is a homopolymer of styrene or a copolymer of styrene and 2-ethylhexylacrylate and is not a polymer having an acidic or basic polar group. Moreover, the working examples disclose the use of a cyclized rubber but not the use of a polar polymer. Further, the use of this cyclized rubber makes it an object that the cyclized polymer of a relatively large molecular weight thus gathered at the particle surfaces envelops a large amount of the low-softening polymer inside thereof to provide the toner with excellent anti-blocking characteristics (cf. column 9, lines 27 to 33). JP-A-59 62869 discloses a toner which is obtained by adding a monomer to the seed particle produced in accordance with the melt emulsion method and then polymerizing said monomer. Its Examples 1 to 3 merely disclose a paraffin wax and an ethylene vinyl acetate copolymer as seed particles and (i) a monomer composition of styrene and diethylaminomethacrylate or (ii) a monomer composition of styrene, n-butylmethacrylate and diethylaminomethacrylate as said monomers, respectively. It is an object of this invention to greatly eliminate the above defects of toners heretofore used widely, and to provide a toner at a lower price than the conventional toners by using a novel process for production. The toner for developing an electrostatically charged image in accordance with this invention is a toner for developing an electrostatically charged image, composed of associated particles of secondary particles comprising primary particles of a polymer having an acidic or basic polar group (to be referred to as the "polymer having a polar group"), preferably a polymer having an acidic polar group, and particles of a coloring agent and optionally a charge controlling agent. The invention provides a toner for developing an electrostatically charged image, composed of associated particles having an average particle diameter of 3 to 25 µm of secondary particles having an average particle diameter of 0.5 to 5 µm comprising: a) primary particles of a polymer having an acidic or basic polar group, said primary particles having an average particle diameter of 0.05 to 0.5 µm; b) particles of a coloring agent having an average particle diameter of 0.01 to 0.5 µm; and optionally c) particles of a charge controlling agent said toner particles being obtainable by a process comprising adding the coloring agent and optionally a charge controlling agent to an emulsion of the polymer obtained by emulsion polymerization, heating the mixture with stirring, then heating the mixture with stirring at a temperature from the glass transition temperature of the polymer to a temperature higher than the glass transition temperature, filtering the resulting associated particles optionally, and then drying the associated particles. Figure 1 is an electron micrograph showing the structure of secondary particles during the production of the toner of this invention. Figure 2 is a scanning electron micrograph (magnification 1,000X) showing the structure of the associated particles during the production of the toner of the invention. Figure 3 is an electron micrograph showing the structure of the toner particles of the invention consisting of associated particles in which the contacting portions among the secondary particles are at least partly melt-adhered by film formation. The primary particles of the polymer having a polar group as used in this invention are particles of a thermoplastic polymer having an average particle diameter of 0.05 to 0.5 µm , preferably 0.1 to 0.3 µm , and are obtained by an emulsion polymerization method. The secondary particles constituting the associated particles which are the toner of the invention are particles resulting from aggregation of primary particles of the coloring agent having an average particle diameter of 0.01 to 0.5, preferably 0.03 to 0.1 µm , and the primary particles of the polymer having a polar group by bonding forces such as forces of an ionic bonding, a hydrogen bonding, a metal coordination bonding and a weak-acid weak base bonding, or Van der Waals force. The secondary particles have an average particle diameter of 0.5 to 5 µm , preferably 1 to 4 µm . Figure 1 is a scanning electron micrograph (magnification 1,000X) showing one example of secondary particles formed in the toner producing process in the present invention. The associated particles are irregularly-shaped particles formed by aggregation of the secondary particles. The associated particles have an average particle diameter of generally 3 to 25 µm , preferably 5 to 15 µm , most preferably 5 to 13 µm. In the invention, there are used associated particles in which the contacting portions among the secondary particles constituting the associated particles are at least partly, preferably mostly, melt-adhered by film formation. Figure 3 is a scanning electron micrograph (magnification 1000X) of associated particles of this invention in which at least a part of the contacting portions among the secondary particles are melt-adhered by film formation. The associated particles which are the toner of this invention contains 20 to 99.9 % by weight, preferably 30 to 98 % by weight, most preferably 40 to 95 % by weight, of the polymer having a polar group and 80 to 0.1 % by weight, preferably 70 to 2 % by weight, most preferably 60 to 5 % by weight, of the coloring agent, based on the total weight of the polymer having a polar group and the coloring agent. Preferred examples of the polymer having a polar group used in this invention include copolymers of styrenes, alkyl (meth)acrylates, and comonomers having an acidic or basic polar group (to be referred to as the "comonomers having a polar group"). Preferred examples of the copolymers are those containing (a) 90 to 20 % by weight, preferably 80 to 30 % by weight, based on the total weight of (a) and (b), of styrenes, (b) 10 to 80 % by weight, preferably 20 to 70 % by weight, based on the total weight of (a) and (b), of alkyl (meth)acrylates, and (c) 0.05 to 30 parts by weight, preferably 1 to 20 parts by weight, per 100 parts of (a) and (b) combined, of comonomers having a polar group. The copolymers may optionally contain polymerizable comonomers other than the monomers (a), (b) and (c) in proportions which do not impair the performance of the toner of the invention. Examples of the styrenes (a) include styrene, o-methylstyrene, m-methylstyrene, p-methylstyrene, alphamethylstyrene, p-ethylstyrene, 2,4-dimethylstyrene, p-n-butylstyrene, p-tert-butylstyrene, p-n-hexylstyrene, p-n-octylstyrene, p-n-nonylstyrene, p-n-decylstyrene, p-n-dodecylstyrene, p-methoxystyrene, p-phenylstyrene, p-chlorostyrene, 3,4-dichlorostyrene and p-chloromethylstyrene. Styrene is especially preferred. Examples of the alkyl (meth)acrylates (b) include methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, propyl acrylate, n-octyl acrylate, dodecyl acrylate, lauryl acrylate, 2-ethylhexyl acrylate, stearyl acrylate, 2-chloroethyl acrylate, methyl alpha-chloroacrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, n-octyl methacrylate, dodecyl methacrylate, lauryl methacrylate, 2-ethylhexyl methacrylate and stearyl methacrylate. Among them, esters of (meth)acrylic acid with aliphatic alcohols having 1 to 12 carbon atoms, preferably 3 to 8 carbon atoms, especially preferably 4 carbon atoms, are used preferably. The monomers (c) having acidic polar groups may be, for example, (i) alpha,beta-ethylenically unsaturated compounds having a carboxyl group (-COOH) and (ii) alpha,beta-ethylenically unsaturated compounds having a sulfone group (-SO 3 H). Examples of the alpha,beta-ethylenically unsaturated compounds having the -COOH group are acrylic acid, methacrylic acid, fumaric acid, maleic acid, itaconic acid, cinnamic acid, monobutyl maleate, monooctyl maleate, and metal salts, such as Na or Zn salts, of these acids. Examples of the alpha,beta-ethylenically unsaturated compounds having the -SO 3 H group are sulfonated styrene, its sodium salt, allylsulfosuccinic acid, octyl allylsulfosuccinate and its sodium salt. Examples of the comonomers (c) having a basic polar group are (i) (meth)acrylic acid esters of aliphatic alcohols having an amine group or a quaternary ammonium group and 1 to 12 carbon atoms, preferably 2 to 8 carbon atoms, especially preferably 2 carbon atoms, (ii) (meth)acrylamide, and (meth)acrylamide optionally mono- or di-substituted by an aikyl group having 1 to 18 carbon atoms on N, (iii) vinyl compounds substituted by a heterocyclic group containing N as a ring member, and (iv) N,N-diallyl-alkylamines and quaternary ammonium salts thereof. Of these, the (meth)acrylic acid esters of aliphatic alcohols having an amine group or a quaternary ammonium group (i) are preferred as the comonomers having a basic group. Examples of the (meth)acrylic acid esters of aliphatic alcohols having an amine group or a quaternary ammonium group (i) are dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, quaternary ammonium salts of the above four compounds, 3-dimethylaminophenyl acrylate, and 2-hydroxy-3-methacryloxypropyl trimethyl ammonium salt. Examples of (meth)acrylamide or (meth)acrylamide optionally mono- or di-substituted by an alkyl group on N (ii) include acrylamide, N-butylacrylamide, N,N-dibutylacrylamide, piperidylacrylamide, methacrylamide, N-butylmethacrylamide, N,N-dimethylacrylamide and N-octadecylacrylamide. Examples of the vinyl compounds substituted by a heterocyclic group containing N as a ring member (iii) are vinylpyridine, vinylpyrrolidone, vinyl-N-methylpyridinium chloride and vinyl-N-ethylpyridinium chloride. Examples of the N,N-diallylalkylamines (iv) are N,N-diallylmethyl ammonium chloride and N,N-diallylethyl ammonium chloride. The polymers having an acidic or basic polar group used in this invention are produced by an emulsion polymerization method. Surface-active agents that can be used in emulsion polymerization may be, for example, anionic surface-active agents, nonionic surface-active agents, protective colloids and cationic surface-active agents. Examples of the anionic surface-active agents and the nonionic surface-active agents include a wide range of anionic surface-active agents, for example fatty acid salts such as sodium oleate and potassium oleate, alkylsulfuric acid ester salts such as sodium lauryl sulfate and ammonium lauryl sulfate, alkylarylsulfonic acid salts such as sodium alkylbenzenesulfonates and sodium alkylnapthalenesulfonates, dialkylsulfosuccinic acid salts, alkylphosphoric acid salts, and nonionic anionic surface-active agents resulting from addition of polyoxyalkylenes such as polyoxyethylene to these compounds; and a wide range of nonionic surface-active agents, for example polyoxyalkylene alkyl ethers such as polyoxyethylene lauryl ether and polyoxyethylene stearyl ether, polyoxyalkylene alkylphenol ethers such as polyoxyethylene octylphenol ether and polyoxyethylene nonylphenol ether, sorbitan fatty acid esters such as sorbitan monolaurate, sorbitan monostearate and sorbitan trioleate, polyoxyalkylene fatty acid esters such as polyoxyethylene monolaurate and polyoxyethylene monostearate, and glycerin fatty acid esters such as oleyl monoglyceride and stearyl monoglyceride. They may be used either singly or in combination. The amount of the surface-active agent used may be properly selected, and may be, for example, 0.05 to 10 % by weight, preferably about 0.05 to 7 % by weight, particularly 0.03 to 5 % by weight, based on the total weight of the monomers used. Examples of the protective colloids used include partially saponified polyvinyl alcohol, completely saponified polyvinyl alcohol, modified polyvinyl alcohol, cellulose derivatives and salts thereof such as hydroxyethyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose salts, and natural polysaccharides such as guar gum. They may be used either singly or in combination. The amount of the protective colloid used may be properly selected, and may be, for example, 0 to 10 % by weight, preferably 0.05 to 5 % by weight, especially preferably 0.05 to 2 % by weight, based on the total weight of the monomers used. Examples of the cationic surface-active agents include alkylamine salts such as laurylamine acetate, quaternary ammonium salts such as lauryl trimethyl ammonium chloride and alkylbenzyl methyl ammonium chloride, and polyoxyethylalkylamines. Examples of amphoteric surface-active agents are alkylbetains such as laurylbetain. The amount of the cationic surface-active agent or the amphoteric surface-active agent may also properly selected, and may be, for example, 0 to 10 % by weight, preferably 0.05 to 5 % by weight, especially preferably 0.05 to 2 % by weight, based on the total weight of the monomers used. If the surface-active agent is used in an amount exceeding the preferred range, the resulting toner tends to have inferior moisture resistance. If it is too small, running property (stability of images in producing many copies) tends to be reduced. Examples of catalysts used in aqueous emulsion copolymerization include persulfates such as sodium persulfate, potassium persulfate and ammonium persulfate, organic peroxides such as tertiary butyl hydroperoxide, cumene hydroperoxide and p-menthane hydroperoxide, and hydrogen peroxide. They may be used either singly or in combination. The amount of the catalyst may be properly selected, and may be, for example, about 0.05 to about 1 % by weight, preferably about 0.1 to about 0.7 % by weight, particularly about 0.1 to about 0.5 % by weight. If desired, a reducing agent may be used jointly in the aqueous emulsion polymerization. Examples of the reducing agent are reducing organic compounds such as ascorbic acid, tartaric acid, citric acid and glucose, sodium thiosulfate, sodium sulfite, sodium bisulfite, and sodium meta-bisulfite. The amount of the reducing agent used may be properly selected, and is, for example, about 0.05 to about 1 % by weight, based on the total weight of the monomers used. In carrying out the aqueous emulsion copolymerization reaction, all the amount of a predetermined surface-active agent may be added to the reaction system. It is also possible to add part of the surface-active agent to the reaction system, start the reaction and add the remainder during the reaction either continuously or portionwise at intervals, and this procedure is preferred. The monomers and as desired, other modifying comonomers may be added at a time, portionwise, or continuously. To control the reaction, it is preferred to add them continuously. In addition to the surface-active agents and catalysts described above, a pH adjusting agent, a polymerization degree adjusting agent, a defoamer, etc. may properly be added during the emulsion polymerization. The polymer having a polar group used in this invention has a glass transition temperature of -90 to 100 °C, preferably -30 to 80 °C, most preferably -10 to 60 °C, and a gellation degree, in terms of the amount of an insoluble portion on Soxhlet extraction under acetone reflux, of 0.0 to 99.9 % by weight, preferably 1 to 30 % by weight. If its glass transition is too high beyond 100 °C, the resulting toner undesirably tends to have reduced low-temperature fixability. If it is too lower below -90 °C, the flowability of the toner particles undesirably tends to be deteriorated. On the other hand, if its gellation degree is too high beyond 50 % by weight, the low-temperature fixability of the resulting toner undesirably tends to be reduced. The term "coloring agent" used in this specification means a coloring additive which gives to the developer a color necessary as a developer for an electrostatically charged image. Accordingly, if additives which imparts properties (e.g., magnetism or charge controlling propery) other than those of the coloring agent to the developer, for example, charge controlling agents such as a magnetic material (e.g., magnetite) or a nigrosine dye impart the desired coloring property to the developer, these additives are also included within the "coloring agent". Inorganic pigments, organic pigments and organic dyes, preferably the inorganic pigments or organic pigments may be used as the coloring agent in accordance with this invention. The inorganic pigments preferably include (a) metallic powder-type pigments, (b) metal oxide-type pigments, (c) carbon-type pigments, (d) sulfide-type pigments, (e) chromate salt-type pigments, and (f) ferrocyanide salt-type pigments. Examples of the metal powder-type pigments (a) are zinc, iron and copper powders. Examples of the metal oxide-type pigments (b) are magnetite, ferrite, red iron oxide, titanium oxide, zinc flower, silica, chromium oxide, ultramarine, cobalt blue, Cerulean blue, mineral violet, and trilead tetroxide. Examples of the carbon-type pigments (c) are carbon black, thermatomic carbon, lamp black and furnace black. Examples of the sulfide-type pigments (d) are zinc sulfide, cadmium red, selenium red, mercury sulfide and cadmium yellow. Examples of the chromate-type pigments (e) are molybdenum red, barium yellow, strontium yellow and chrome yellow. Milori Blue is an example of the ferrocyanide compound-type pigments (f). Examples of the organic pigments are shown below. (a) Azoic pigments Hansa Yellow G, benzidine yellow, benzidine orange, permanent red 4R, pyrazolone red, Lithol Red, brilliant scarlet G and Bon Maroon Light. (b) Acid dye-type pigments and basic dye-type pigments Products obtained by precipitating such dyes as orange II, acid orange R, eoxine, quinoline yellow, tartrazine yellow, acid green, peacock blue and alkali blue with precipitating agents, and products obtained by precipitating such dyes as Rhodamine, magenta, malachite green, methyl violet and victoria blue with tannic acid, tartar emetic, PTA, PMA, PTMA, etc. (c) Mordant dye-type pigments Metal salts of hydroxyanthraquinones, and alizarin murder lake. (d) Phthalocyanine pigments Phthalocyanine blue and copper phthalocyanine sulfonate (e) Quinacridone-type pigments and dioxane-type pigments Quinacridone red, quinacridone violet and carbazoledioxazine violet. (f) Others Organic fluorescent pigments and aniline black. Nigrosine dyes and aniline dyes are used as the organic dyes mentioned above. As stated above, the toner of this invention, as required, may contain a charge controlling agent or a magnetic material, for example. Examples of the charge controlling agent are those for dealing with positive charges, for example electron-donating dyes of the nigrosine type, metal salts of naphthenic acid, metal salts of higher fatty acids, alkoxylated amines, quaternary ammonium salts, alkylamides, chelates, pigments and fluorine treatment activating agents, and those for dealing with negative charges, for example electron accepting organic complexes, chlorinated paraffin, chlorinated polyesters, polyesters having an excess of acid groups, and a sulfonylamine of copper phthalocyanine. For the purpose of improving fixability, the toner of the invention may contain additives. Examples of the fixability improving additives include olefinic resins (such as low-molecular-weight polyethylene, low-molecular-weight polypropylene, polyethylene oxide and polytetrafluoroethylene), epoxy resins, polyester resins, styrene/butadiene copolymer (monomer ratio 5-30:95-70), olefin copolymers (such as ethylene/acrylic acid copolymer, ethylene/acrylate ester copolymers, ethylene methacrylic acid copolymer, ethylene methacrylate ester copolymers, ethylene/vinyl chloride copolymer, ethylene/vinyl acetate copolymer, and ionomer resins), polyvinyl pyrrolidone, methyl vinyl ether/maleic anhydride copolymer, maleic acid-modified phenolic resins and phenol-modified terpene resins. The olefinic resins are preferred. These resins are used preferably as an aqueous emul-sion. As required, the toner of this invention may be used together with additives such as a fluidizing agent. Fine powders of hydrophobic silica, titanium dioxide and aluminum oxide may be cited as examples of the fluidizing agent. The fluidizing agent may be used in an amount of 0.01 to 5 parts by weight, preferably 0.1 to 1 part by weight, per 100 parts by weight of the toner. For the purpose of improving moisture resistance, the toner of this invention may be surface-treated with a silane coupling agent and a titanium coupling agent. These coupling agents may be used singly or in combination of two or more. A preferred process for producing the toner of this invention will be described below. A required amount of the coloring agent powder and optionally the charge controlling agent are mixed with an emulsion of the polymer having an acidic or basic polar group obtained by emulsion polymerization to disperse them finely. When the mixture is further stirred for 0.5 to 4 hours, preferably 1 to 3 hours, primary particles of the polymer having a polar group and the coloring agent particles gradually aggregated and grow to secondary particles having an average particle diameter of 0.5 to 5 µm as shown in the photograph of Figure 1. When the resulting dispersion is further stirred for 0.5 to 3 hours, preferably 1 to 2 hours, the secondary particles further aggregate and grow to associated particles having an average particle diameter of 5 to 25 µm as shown in the photograph of Figure 2. According to process of producing the toner of this invention, when the resulting dispersion is further stirred for 1 to 3 hours at the glass transition temperature of the polymer having a polar group to a temperature 65 °C higher than the glass transition temperature, associated particles in which the contacting portions among the secondary particles are at least partly melt-adhered by film formation, as shown in the photograph of Figure 3. Since the secondary particles are melt-adhered to each other by film formation, these associated particles do not substantially undergo disintegration during storage, transportation and production of a developer, and are especially suitable as a developer for electrostatically charged images. A developer is prepared by mixing the toner of this invention with a carrier such as iron and glass beads. When the toner itself already contains ferrite as the coloring agent, the ferrite also acts as a carrier. In this case, the resulting developer may be used directly. An iron powder having negative triboelectric charging property as a result of coating with a resin, preferably a fluorine-type resin is particularly suitable as the carrier. The toner of this invention has a relatively narrow particle size distribution and a relatively small average particle diameter. Hence, when it is formed into a developing agent for electrostatically charged images, it exhibits excellent effects in that its resolution is much improved over conventional products, its chargeability is excellent, and there is hardly any occurrence of fogging. Furthermore, the process for producing it is simplified as compared with the prior art because it does not require pulverization and classification and does not necessarily require coagulating agents such as magnesium sulfate. Furtheremore, since the yield of the required toner particles is high, the process has excellent economy. The following examples illustrate the present invention specifically. Unless otherwise specified, all amounts are expressed by weight. EXAMPLE 1 Preparation of a polymer containing an acid polar group Styrene monomer (ST) 60 parts Butyl acrylate (BA) 40 parts Acrylic acid (AA) 8 parts A mixture of the above monomers was added to a mixture of the following ingredients. Water 100 parts Nonionic emulsifier (Emulgen 950) 1 part Anionic emulsifier (Neogen R) 1.5 parts Potassium persulfate 0.5 part The resulting mixture was stirred at 70 °C for 8 hours to obtain an emulsion of a resin having an acid polar group. The solids concentration of the emulsion was 50 %. Preparation of a toner (1) Emulsion of a resin containing an acid polar group 120 parts Magnetite 40 parts Nigrosine dye (Bontron N-04) 5 parts Carbon black (Dia Black #100) 5 parts Water 380 parts A mixture of the above ingredients was maintained at about 30 °C for 2 hours while it was dispersed and stirred by means of a slusher. It was then heated to 70 °C with stirring and maintained at this temperature for 3 hours. In the meantime, microscopic observation led to the determination that a complex of resin particles and magnetite particles grew to a size of about 10 µm. The mixture was cooled, and the resulting liquid dispersion was subjected to Buchner filtration, washed with water, and dried in vacuum at 50 °C for 10 hours. To 100 parts by weight of the toner was added 0.5 part by weight of silica (Aerosil R972 manufactured by Japan Aerosil Co., Ltd.) as a fluidizing agent, and they were mixed to form a test developer. The polymer used in this toner had a Tg of 45 °C, a gellation degree of 5 % and a softening point of 148 °C. The toner had an average particle diameter of 12 µm. The developer was charged into a commercial copying machine (NP-270Z produced by Canon Co., Ltd.), and copying was carried out. Copied images having a high density and reduced fog were obtained. The results are shown in Table 2. EXAMPLES 2-7 The monomer compositions shown in Table 1 were used, and subjected to the same operation as in Example 1. The results are shown in Table 2. The abbreviations used in Table 1 have the following meanings. MAA: methacrylic acid MBM: monobutyl maleate BQA: 2-hydroxypropyl-N,N,N-trimethyl ammonium chloride acrylate DMAA: dimethylaminoethyl acrylate LMA: lauryl methacrylate VP: vinylpyridine DMPC: N,N-diallylmethyl ammonium chloride EXAMPLE 8 An emulsion of a resin containing an acid polar group was prepared as in Example 1, and a toner was prepared by the following operation. Preparation of a toner (2) Emulsion of a resin containing an acid polar group 184 parts Chrome dye (Bontron E-81) 1 part Carbon black (Regal 330R) 7 parts Water 307 parts A mixture of the above ingredients were worked up in the same way as in Example 1 to prepare a test toner. The polymer had a Tg of 43 °C, a gellation degree of 590 and a softening point of 147 °C. The toner had an average particle diameter of 10.5 µm. The toner was charged into a commercial copying machine (Leodry BD-4140 made by Toshiba Co., Ltd.), and copying was carried out. Copied images having a high density and reduced fog were obtained. The results are shown in Table 2. EXAMPLES 9-11 The same operation as in Example 8 was repeated using the monomer compositions shown in Table 1. The results are shown in Table 2. EXAMPLE 12 When during the reaction of forming the associated particles in Example 1, the toner-forming composition was heated to 60 °C and maintained at this temperature for 2 hours instead of maintaining it at 70 °C for 3 hours, the growth of particles was controlled, and a toner having an average particle diameter of 5 µm was obtained in a yield of 60 %. When a copying test was carried out using this toner, images having a very good resolution, a high density and reduced fog were obtained. COMPARATIVE EXAMPLE 1 When an emulsion of a resin obtained by polymerization using the resin monomer composition shown in Example 1 but without adding AA (a monomer having an acid polar group) as shown in Table 1, the associated particles did not grow, and a test toner could not be obtained. COMPARATIVE EXAMPLE 2 The resin emulsion obtained in Example 1 was dried by a spray dryer (Mobile Minor made by Ashizawa Niroatomizer) under the following conditions. Inlet temperature: 120 °C Outlet temperature: 90 °C Feed rate: 1.5 liters/min. Atomizer: operated at 3 x 10 4 rpm. Sixty parts of the resulting resin, 40 parts of magnetite, 5 parts of a nigrosine dye (Bontron N-04) and 5 parts of carbon black (Dia Black #100) were melt-kneaded and pulverized to give a toner having an average particle diameter of 5 µm. The yield at this time was 35 %. To 100 parts by weight of the resulting toner, 0.5 part by weight of silica (R-972 produced by Japan Aerosil Co., Ltd.), and they were mixed to form a test developer. This developer had very poor flowability. When this developer was subjected to the same copying test as in Example 1, images having much fogging were obtained. COMPARATIVE EXAMPLE 3 A resin having the composition shown in Table 1 was obtained by the same operation as in Comparative Example 2. The resin was compounded as in Comparative Example 2 and melt-kneaded and pulverized to give a toner having an average particle diameter of 12.0 µm in a yield of 55 %. The same copying test was carried out using the resulting toner. The results are shown in Table 2. Method of evaluating the resolution of a copied image The test pattern AR-4 of Data Quest Co., Ltd. was copied. The number of lines per mm in the copied test pattern was determined by visual observation, and made a rating of resolution. By this evaluating method, with the resin composition shown in Table 1, at least 6.3 lines can be determined to be a good resolution, and not more than 3.6 lines, a poor resolution. Method of evaluating fogging of a copied image Using a reflectometer (CM-53P made by Murakami Color Laboratory Co., Ltd.), the reflectance of white paper before copying and the reflectance of the non-character portion of the paper after copying were compared at a light angle of 45°. The ratio of the reflectance is defined as a fog density (%). A fog density of not more than 0.7 can be determined to be good, and a fog density of at least 1.0, to be poor. Average particle diameter of the toner ( µm ) Resolution (lines) Fog density (%) Example 1 12.0 8.0 0.4 2 11.5 8.0 0.4 3 13.0 6.3 0.3 4 9.5 8.0 0.5 5 12.5 7.1 0.4 6 12.5 6.3 0.3 7 10.5 6.3 0.4 8 10.5 7.1 0.4 9 11.0 6.3 0.3 10 9.0 7.1 0.5 11 9.5 7.1 0.5 12 5.0 25 0.6 Comp. Example 1 - - 2 5.0 4.5 3.2 3 12.0 3.6 1.5 EXAMPLE 13 Preparation of a polymer having an acid polar group Styrene monomer (AT) 75 parts Butyl acrylate (BA) 35 parts Acrylic acid (AA) 3 parts A mixture of the above monomer was added to a mixture of the following ingredients. Water 100 parts Nonionic emulsifier (Emulgen 950) 1 part Anionic emulsifier (Neogen R) 0.1 part Potassium persulfate 0.5 part The resulting mixture was polymerized at 70 °C for 8 hours with stirring to give an emulsion of a resin having an acid polar group with a solids content of 50 %. Preparation of a toner (1) Emulsion of the resin having an acid polar group 120 parts Magnetite 40 parts Nigrosine dye (Bontron N-04) 5 parts Carbon black (Dia Black #100) 5 parts Water 380 parts Wax emulsion (HYTEC E-4B) (effective component 40 %) 20 parts A mixture of the above ingredients was maintained at about 30 °C for 2 hours while dispersed and stirred by a slusher. Observation under a scanning electron microscope during this time showed that the primary particles had a size of 0.3 µm , and the primary particles of the coloring agent had a size of 0.04 to 0.08 µm , and the aggregated secondary particles had a size of about 2 µm. Thereafter, the mixture was maintained at 70 °C for 3 hours with stirring. Microscopic observation during this time led to the determination that a complex of the resin particles and the magnetite particles grew to a size of about 10 µm. The mixture was cooled, and the resulting liquid dispersion was subjected to Buchner filtration, washed with water, and dried in vacuum at 50 °C for 10 hours. Five parts of a 10 % ethanol solution of a silane coupling agent (A-143 produced by Nippon Unicar Co.) was sprayed onto 100 parts of the resulting particles, and surface coupling was effected at 40 °C for 50 hours to form a test toner. The polymer used in the toner had a Tg of 55 °C, a gellation degree of 15 % and a softening point of 135 °C. The toner had an average particle diameter of 13 µm. The developer was charged into a commercial copying machine (NP-270Z made by Canon Co., Ltd.), and copying was carried out. Copied images having a high density and reduced fog (fog density 0.0) were obtained. The fixability of this toner was tested by the following method, and the fixation ratio was as good as 95 %. The moisture resistance of the toner in an environment kept at room temperature and 85 % humidity was tested by the following method. The fog density was as low as 0.1 %, and good results were obtained. The chargeability of this toner was excellent, and the distribution of the amount of charge was very narrow. Evaluation of fixability The test pattern AR-4 of Data Quest Co., Ltd. was copied, and the solid portion was rubbed with a sanded rubber eraser through 5 reciprocations. The ratio of the reflectance of the solid portion after rubbing and that before rubbing was determined by a reflectometer, and defined as the fixation ratio. The reflectometer was CM-53P made by Murakami Color Laboratory Co., Ltd. Evaluation of moisture resistance The test was carried out after the copying test in an environment kept at room temperature and 85 % for 3 days. The fog density of the non-character portion of the test pattern was measured by using the above reflectometer. The reflectance of white paper before copying and that of the non-character portion after copying were compared, and the ratio of the reflectances was defined as a fog density.

Claims: Toner particles for developing an electrostatically charged image consisting of associated particles having an average particle diameter of 3 to 25 µm of secondary particles having an average particle diameter of 0.5 to 5 µm, the contacting portions of which are at least partly melt-adhered by film formation comprising: a) primary particles of a polymer having an acidic or basic polar group, said primary particles having an average particle diameter of 0.05 to 0.5 µm; b) particles of a coloring agent having an average particle diameter of 0.01 to 0.5 µm; and optionally c) particles of a charge controlling agent said toner particles being obtainable by a process comprising adding the coloring agent and optionally a charge controlling agent to an emulsion of the polymer obtainable by emulsion polymerization, heating the mixture at 20 to 45°C for 1 to 3 hours with stirring, then heating the mixture with stirring at a temperature from the glass transition temperature of the polymer to a temperature 65°C higher than the glass transition temperature for 1 to 3 hours, filtering the resulting associated particles optionally, and then drying the associated particles. A developer for developing an electrostatically charged image comprising the toner particles of claim 1 and carrier particles.

Inventors: HASEGAWA YUKINOBU, MARUYAMA MASATOSHI, MURAI KOICHI, SHIMOMURA HIROYOSHI, TANGE TOYOKICHI, HASEGAWA, YUKINOBU, MARUYAMA, MASATOSHI, MURAI, KOICHI, SHIMOMURA, HIROYOSHI, TANGE, TOYOKICHI
Applicants: NIPPON CARBIDE KOGYO KK, NIPPON CARBIDE KOGYO KABUSHIKI KAISHA
Application year: 1988
Main classification: G03G9
IPC codes: G03G9