Method of forming a fine pattern

Abstract: A photoresist is coated on a substrate to form a planar surface, thus to form recessed portions corresponding to a mask of a pattern to be formed in the photoresist layer having planar surface. SiO₂ etc. are deposited into the recessed portions to prepare a mask, thus to form a fine pattern by anisotropic etching. As a result, by films remaining below the recessed portions formed in the photoresist layer having planar surface, a fine pattern is formed.

Description: This invention relates to a method of forming a fine pattern, and more particularly though not exclusively a method of forming a fine pattern of less than submicron order in a manufacturing of a VLSI (Very Large Scale Integrated Circuit). Photoresists have been conventionally used for forming a pattern in manufacturing of LSI. Among two types of photoresists, a positive resist having resolution superior to that of a negative resist is generally used for forming a fine pattern of less than submicron order. However, with such a positive resist, it is ordinary that fine space pattern or opening pattern inferior to the resolution is only formed. In addition, as a result of the fact that light having a short wavelength is used for exposure in the formation of pattern of submicron order in recent years, the depth of a focus becomes shallow, resulting in difficulty in coping with such a circumstance that there is any offset on a substrate. Reference is made to Patent Abstracts of Japan, vol. 10, No. 217, (E-423)(2273) July 29, 1986 and JP-A-6154629, which discloses a method of forming a fine pattern, comprising a step of coating a first photoresist on the surface of an Si substrate; a step of forming raised and recessed portions defining a predetermined fine pattern in the top surface of said first photoresist so that said recessed portions are exposed to the outside; a step of depositing an SiO 2 second film of material over said first photoresist and said recessed portions, said SiO 2 film having an etch rate different from that of said photoresist; and a step of removing exposed portions of said first photoresist by anisotropic etching with said material of said SiO 2 film deposited within said recessed portions acting as a mask. BRIEF DESCRIPTION OF THE DRAWINGS The invention will now be described, by way of example, with reference to the accompanying drawings, in which: Figs 1 and 2 are schematic cross sectional views for explaining a conventional method of forming a fine pattern, respectively; Fig. 3 is an explanatory view of a multi-layer resist process conventionally used in the formation of a fine pattern; Fig. 4 contains process diagrams showing a method of forming a fine pattern, such method being outside the scope of the appended claims but included to provide background information; and Figs. 5 and 6 are process diagrams of two preferred ways of putting the invention into effect for forming a fine pattern. A conventional method of forming a pattern using a photoresist will be described with reference to Figs. 1 and 2. In the case of depositing a photoresist, e.g., having a resolution of 1 µm on a substrate 1, thereafter to form a pattern using a mask pattern of line/space having a width of 1 µm, there is a tendency that photoresists 42 having been subjected to patterning on lines become narrow, whereas spaces 43 become broad as shown in Fig. 1, so that it is practically difficult to form a pattern of line/space having a width of 1 µm. Even in the case of forming a pattern of contact holes of 1 µm in dimension in a manner similar to the above, because the side surfaces of respective photoresist 42 having been subjected to patterning have a regular taper or inclination in the vicinity of the limit resolution of the pattern, it is also impossible to open contact holes of 1 µm using such photoresists. Further, since, e.g., a polysilicon layer or a silicon oxide film is ordinarily formed on the substrate 1 and there is an offset of about 1 µm in the film 44 to be subjected to patterning, there occurs a difference in the film thickness of photoresist in coating photoresist. Thus, the film thickness of the photoresist becomes uneven because of such an offset, so that it is difficult to obtain an optimum condition for exposure and development of the entirety of photoresist. Namely, an optimum condition for exposure and development at the portion which is thick in the thickness of the photoresist is different from that at the portion which is thin therein. At the portion which is thin in film thickness, exposure and development become excessive by any means. Accordingly, spaces or contact holes are to become large. Especially, as a result of the fact that times of submicron order have come and exposure has been carried out using light having a short wavelength, the depth of a focus becomes equal to the order of 1.0 or 0.5 µm, resulting in the tendency that the exposure condition changes to much degree accordingly. The space 46 at the portion which is thin in the film thickness of the photoresist 45 having been subjected to patterning in this way becomes larger than the space 47 at the portion which is thick in the film thickness thereof. In opening contact holes in a portion which is thick in the film thickness of the photoresist, even in the case that such contact holes could be opened, residues appear on the bottom portions of the opened contact holes since they may not be sufficiently subjected to cleaning at the time of development because of large aspect ratio, resulting in the possibility that the opening yield is lowered. As just described above, in the conventional method of forming a fine pattern, there were problems that it is impossible to form a tine pattern of photoresist with a limit resolution of photoresist or less than that, and that a pattern of photoresist formed becomes uneven in dimensions because of unevenness of the film thickness of photoresist resulting from an offset on a substrate, On the other hand, for a method of forming a fine pattern, there has been conventionally known a method called a multi-layer resist process or stacked resist process. This method requires, as shown in Fig. 3 process steps of 1 ○ coating of first interlayer resist (Fig. 3 (a)), 2 ○ spin-on glass coating (Fig. 3(b)), 3 ○ coating of a second layer resist (Fig. 3 (c), 4 ○ patterning by exposure/development (Fig. 3 (d)), 5 ○ patterning of a glass layer by RIE (Fig. 3 (e)), 6 ○ resist etching by O 2 RIE (Fig. 3(f)) and 7 ○ etching of underlying layer with the spin-on glass and the second interlayer resist being as a mask. Another method of forming a fine pattern (not in accordance with this invention) will now be described with reference to Fig. 4. On a substrate 1, a film 2 of a conductive film, such as, for example, a polysilicon film or an aluminum film is formed. The film 2 subjected to patterning in accordance with a wiring pattern includes an offset on the surface thereof. A photoresist 3 is sufficiently thickly coated on the film 2 to thereby eliminate the offset so that the photoresist 3 surface becomes planar. Since the photoresist 3 surface subject to exposure is thus planarized, there is no possibility that focus undesirably deviates from a normal position, with the result that the stepper (stepping projection aligner) can exhibit the maximum performance. The thickness of the photoresist 3 was about 2 µm (Fig. 4(a)). Then, by using a mask having positive/negative surfaces opposite to those of a mask conventionally used, a pattern having a width of 1 µm is transferred onto the photoresist 3. At this time, the condition for exposure and development is set such that a photoresist having a film thickness of substantially 0.5 µm is subjected to exposure and development to form recessed portions 4 at the top surface of the photoresist 3 and having a width of 1 µm and a depth of substantially 0.5 µm in the layer formed by the photoresist 3. At this time, photoresist 3 sides defining respective recessed portions 4 have a gentle regular taper or inclination (Fig. 4 (b)). The provision of such regular tapers is convenient in that the film is prevented from being brought into a perforated state at the time of formation of the film. In the case of forming a pattern having a width of 1 µm, when each recessed portion 4 has a width of 1.2 µm and each portion between adjacent recessed portions 4 has a width of 0.8 µm, exposure is easily conducted, and the width of the wiring portion formed below each recessed portion at the subsequent process step becomes equal to 1.2 µm, so that the wiring width is allowed to be broad in comparison with the pitch (2 µm), thus permitting a large current to flow, Using LPD (Liquid Phase Deposition) method (see Japanese Laid-Open Patent Publication No. 57-196744), an SiO 2 film (glass layer) 5 is deposited on the photoresist 3. This deposition method is to immerse a substrate into an immersion liquid of hydrofluoric acid (H 2 SiF 6 ) supersaturated with SiO 2 , and is characterized in that the film thickness is entirely uniform. In accordance with this method, since deposition is enabled at a temperature nearly equal to a room temperature, there is no possibility that photoresist is damaged even if SiO 2 , film is deposited on photoresist. In this method, SiO 2 film 5 having a film thickness of about 0.7 µm was deposited to completely fill therewith recessed portions 4 having a width of 1 µm in the layer formed by the photoresist 3 (Fig. 4(c)). Then, etch back is applied to the entire surface of the SiO 2 film 5, thus allowing SiO 2 film 6 to remain only within the recessed portions 4 formed in the photoresist layer 3 (Fig. 4(d)). At this time, diluted fluoric acid was used for etch back in the first embodiment. In addition, etching may be conducted using an activated species of fluoric gas obtained from CF 4 /O 2 plasma, or etching may be conducted by RIE (Plasma Etching) method using CHF 3 /O 2 as its main component. With the SiO 2 films 6 remaining within the recessed portions 4 being as a mask, by RIE method using an etching gas containing O 2 as its major component, anisotropic etching of the photoresist 3 is carried out, thus allowing photoresists 7 to remain below the SiO 2 films 6. Thus, a photoresist pattern is formed by these remaining photoresists 7 (Fig. 4(e)). Thereafter, although not shown, with the SiO 2 films 6 and the remaining photoresists 7 being as a mask, the underlying film 2 is subjected to etching to implement patterning of the film 2. By this patterning, a fine wiring pattern of film 2 of a conductive film, such as, for example, a polysilicon film or an aluminum film having an offset is formed. As just described above, in accordance with the method disclosed, a pattern having a limit resolution of photoresist can be provided also in a photoresist formed on a foundation or underlying layer having an offset, and particularly the space pattern can be formed so that it is finer than resolution. A method of forming a fine pattern according to a first embodiment of this invention will be described with reference to Fig. 5. On a substrate 1, a film 8 of a conductive film, such as, for example, a polysilicon film or an aluminum film similar to that in the first embodiment is formed. In the case of the above-mentioned method described with reference to Fig. 4, film 2 is subjected to patterning into wiring lines having a width of 1 µm. In contrast, the first embodiment is concerned with the case that film 8 is subjected to patterning into wiring lines having a variety of different widths. After a photoresist 9 is thickly coated on the film 8, recessed portions 10, 11 and 12 exposed to the outside, and having a depth of approximately 0.5 µm and a diversity of widths are formed in the layer formed by the photoresist 9. The pattern side surfaces of the photoresist 9 defining these recessed portions 10, 11 and 12 have a gentle regular taper or inclination (Fig. 5(a)). Using LPD method, a silicon film 13 having a film thickness of about 1 µm is deposited on the photoresist 9. However, even if SiO 2 film 13 is thickly deposited in this way, it is not completely filled within the recessed portion 12 having a width of 2 µm or more, so that a recessed portion 14 exposed to the outside remains in the SiO 2 film 13 (Fig, 5(b)). A photoresist 15 is then coated on the SiO 2 film 13 by spin-coating method to fill the recessed portion 14 in the SiO 2 film 13 therewith, thus allowing the photoresist 15 surface to be planar (Fig. 2(c)). By RIE method using an etching gas containing C 2 F 6 /CHF 3 /O 2 as its major component, etching of the photoresist 15 and the SiO 2 film 13 is carried out. At this time, the etching condition is set so that etch rates for the photoresist 15 and the SiO 2 film 13 are nearly equal to each other. By etch back under this condition, SiO 2 films 16, 17 and 18 are caused to remain only within recessed portions 10, 11 and 12 in the photoresist 9, respectively, (Fig. 5(d)). With the SiO 2 films 16, 17 and 18 respectively remaining within the recessed portions 10, 11 and 12 being as a mask, anisotropic etching of the photoresist 9 is carried out by RIE method using an etching gas containing O 2 as its major component, thus allowing photoresists 19 to remain below the SiO 2 films 16, 17 and 18. By these remaining photoresists 19, a photoresist pattern is formed (Fig.5 (e)). Thereafter, although not shown, with the SiO 2 films 16, 17 and 18, and the remaining photoresists 19 being as a mask, the underlying film 8 is subjected to etching to carry out patterning of the film 8. Thus, wiring lines having various widths comprised of the film 8 of a conductive film, such as, for example, a polysilicon film or an aluminum film are formed. As just described above, in accordance with the method of forming a fine pattern using photoresist of the first embodiment, a line pattern having various widths can be obtained and the space pattern is formed so that it is finer than resolution. Then, a method of forming a fine pattern according to a second embodiment of this invention will be described with reference to Fig. 6. On a substrate 1, a film 20 of an insulating film, such as, for example, a silicon oxide film is formed. In the case of the above-mentioned method according to Fig. 4 and first embodiment according to Fig. 5, films 2 and 8 formed as a conductive film, such as, for example, a polysilicon film or an aluminum film are subjected to patterning. Differently from this, the second embodiment is concerned with the case that fine holes such as contact holes are Opened in a film of an insulating film. After a photoresist 21 having a film thickness of about 1.5 µm is first coated on the film 20, exposure and development processing is applied to predetermined sites or portions to remove them so that recessed portions 22 having a depth of 1 µm are formed, thus leaving projecting portions 23 only at sites corresponding to openings (Fig. Using LPD method, a SiO 2 film 24 having a film thickness of 0.3 µm is deposited on photoresists 22 including projecting portions 23 (Fig. 3(b)). Further, a photoresist 25 is coated on the SiO 2 film 24, thus allowing the photoresist 25 surface to be planar. To realize this, by RIE method using an etching gas containing C 2 F 6 /CHF 3 /O 2 as its major component, etching of the photoresist 25 and the SiO 2 film 24 is carried out. At this time, the etching condition is set so that etch rates for photoresist 25 and SiO 2 film 24 are nearly equal to each other. By etch back under this condition, SiO 2 film 24 on the top of each projecting portion 23 is removed, thus allowing the SiO 2 films 26 of the remainder to remain as they are (Fig. 6 (c)). Then, with the remaining SiO 2 films 26 being as a mask, by RIE method using an etching gas containing O 2 as its major component, anisotropic etching of the photoresist 22 is carried out. At this time, photoresists 25 on SiO 2 films 26 are removed by etching. However, since SiO 2 films 26 are little subjected to etching, only photoresists 22 of the projecting portions 23 corresponding to openings are removed by etching, so that photoresists 27 remain below the SiO 2 films 26, respectively (Fig. 6(d)). By these remaining photoresists 27, a photoresist pattern is formed. Thereafter, although not shown, with the photoresists 27 being as a mask, the film 20 is subjected to etching. Thus, fine contact holes are formed in the film 20 of an insulating film such as a silicon oxide film. As just described above, in accordance with the method of forming a fine pattern using photoresist of the second embodiment, it is possible to form contact holes finer than a limit resolution of photoresist. Meanwhile, when exposure is conducted using electron beam in forming an uneven pattern on the surface of photoresist thickly coated in the above-described first and second embodiments, the photoresist has little influence of back scattering from the substrate at the time of exposure because it is thick, resulting in no need of back scattering correction having been implemented. Thus, writing is simplified to much extent. In the case of electron beam, such an effect may be obtained by using a condition where an acceleration voltage at the time of writing is set to a small value, thus to expose only the outermost layer portion having a depth of 0.3 to 0.5 µm of the surface of the photoresist thickly coated. In the case of exposure using light, the photoresist pattern may be collapsed by reflected light from the substrate, and particularly in the case that a film subjected to etching with such a photoresist being as a mask is an aluminum film, pattern collapse may conspicuously appear to such an extent that it is called "inversed mustache", or the side surfaces of the photoresist may become notched by interference light, giving rise to a cause of unevenness in dimensions. However, because of the fact that the film thickness of the photoresist is thick, and that only the outermost layer portion of the photoresist is subjected to exposure and development in the above-described first to third embodiments, such a phenomenon does not occur in any degree. In addition, because there is no need that the depth of recessed portions formed in the resist layer is not so deep, times for exposure and development are reduced. Especially, the exposure time by stepper is reduced, resulting in greatly improved producibility. While pattern transfer to the photoresist is conducted by using light or electron beam in the above-mentioned first and second embodiments, the same effect may be obtained by focused ion beam or X-ray. Furthermore, a method of depositing SiO 2 film onto the photoresist having been subjected to pattern transfer is not limited to LPD method employed in the above-mentioned first and second embodiments, such as deposition may be conducted by using other means for depositing film at a low temperature, e.g., non-electrolytic plating method, sputtering method, bias sputtering method, etc. Also in connection with the film to be deposited, as long as a material has a different etch rate and can be used as a mask in etching photoresist or organic film by RIE method using an etching gas containing O 2 as its major component, such a film to be deposited is not limited to SiO 2 film, but may be metal film or silicide film. In addition, while positive resist is used for photoresist in the above-mentioned first and second embodiments, this invention as defined by the appended claims can be applicable to negative resist. As stated above, in accordance with this invention as defined by the appended claims, the advantages are achieved that a fine pattern of less than limit resolution of resist can be formed, and the number of process steps can be reduced as compared to the conventional multi-layer resist process.

Claims: A method of forming a fine pattern, comprising: a first step of forming a first film (8;20) on a substrate (1); a second step of coating a first photoresist (9;21) on the surface of said first film (8;20); a third step of forming raised and recessed portions (10-12;23,22) defining a predetermined fine pattern in the top surface of said first photoresist(9;21) so that said recessed portions (10-12;22) are exposed to the outside; a fourth step of depositing a second film (13;24) of a material on said first photoresist (9;21) and said recessed portions (22), the second film having a non-planarised exposed surface; a fifth step of coating a second photoresist (15;25) on said second film (13;24), whereby the second photoresist has a planar exposed surface; a sixth step of etching back said second photoresist (15;25) and said second film (13;24) above the level of the raised portions (23) in the top surface of the first photoresist (9;21) to expose the raised portions, the etching rates for the second photoresist and the material of the second film being nearly equal; and a seventh step of removing exposed portions of said first photoresist (9;21) by anisotropic etching having an etching rate for the material of the second film which is different from that for the first photoresist so that said material of said second film (16-18;26) deposited within said recessed portions (10-12;22) acts as a mask. A method of forming a fine pattern as in claim 1, wherein there is an eighth step of removing said first film (8;20) with said material of said second film (16-18;26) deposited within said recessed portions (10-12;22) acting as a mask. A method of forming a fine pattern as in claim 1 or 2, wherein said first film is an insulating film (20). A method of forming a fine pattern as in any preceding claim, wherein said second step is to sufficiently thickly coat said first photoresist (9;21) so that the surface of said first photoresist (9;21) becomes planar. A method of forming a fine pattern as in claim 3 or claim 4 as appended to claim 3, wherein said first photoresist (21) coated on the surface of said first film (20) has a film thickness of about 1.5µm, said recessed portions (22) have a depth of 1µm, and said second film (24) has a thickness of 0.3 µm. A method according to any preceding claim, wherein said raised portions (23) are such as to provide holes finer than a limit resolution of said first photoresist (21) after said seventh step has been completed. A method according to any preceding claim, wherein the side walls of each recessed portion (10-12;22) are outwardly inclined from the bottom thereof.

Inventors: OKUMA KATSUYA, WATANABE TOHRU, OKUMA, KATSUYA, WATANABE, TOHRU
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1988
Main classification: H01L21
IPC codes: H01L21