Optically anisotropic melt forming aromatic copolyesters based on t-butyl-4-hydroxybenzoic acid

Abstract: Novel copolyesters derived from (a) aromatic diols, (b) dicarboxylic acids and (c) aromatic hydroxycarboyxlic acids, in which the aromatic hydroxycarboyxlic acid component (c) comprises 15 to 60 mole % the copolyester and in which t-butyl-­ 4-hydroxybenzoic acid constitutes 25 to 100 mole % of the aromatic hydroxycarboxylic acid component (c), are disclosed. These copolyesters are anisotropic and fabricable in the melt. They generally can be processed using conventional thermoplastic shaping techniques at temperatures below 350 degrees C. into moldings, fibers and films which have outstanding mechanical properties.

Description: BACKGROUND OF THE INVENTION This invention relates to novel aromatic copolyesters that are optically anisotropic in the melt and that are derived from (a) a mixture of aromatic diols, (b) aromatic dicarboxylic acids, and (c) t-butyl-4-hydroxybenzoic acid. The key to this invention is the incorporation of t-butyl-4-hydroxybenzoic acid into the claimed copolyesters. These polymers range from glassy to semi-crystalline and are unexpectedly melt processable at temperatures generally at or below 350 degrees C. Optically anisotropic melt forming aromatic copolyesters based on various combinations of aromatic diols, aromatic dicarboxylic acids and aromatic hydroxycarboxylic acids are well known in the art. Due to the melt anisotropy of such aromatic copolyesters, shaped articles such as films and fibers made from them tend to have excellent mechanical properties. Unfortunately, the copolyesters also tend to have very high crystalline melting temperatures, a factor which makes it difficult to process them in conventional melt-processing equipment. The art is replete with attempts to improve the melt processability of anisotropic aromatic copolyesters (generally, by lowering crystalline melting temperatures) by altering one or more of the components in the polymer. For example, some have tried to achieve lower melting points by incorporating different substituents on the aromatic rings or by using some aromatic rings having chain extending linkages which are neither parallel nor coaxial. Numerous attempts have involved altering the aromatic hydroxycarboxylic acid component of the copolyester, as is the case in the present invention. US-A-4,447,593 to Funakoshi et al. discloses an aromatic polyester having melt anisotropy and an optional hydroxycarboxylic acid component which can be a mono-substituted p-hydroxybenzoic acid. The substituted p-hydroxybenzoic acid is preferably substituted by an alkyl group having 1 to 4 carbon atoms or by a halogen atom. The compound 3-t-butyl-4-hydroxybenzoic acid is included as an example of a suitable substituted p-hydroxybenzoic acid (column 5, lines 56-57, and Example 24 describes a polymer derived from (diphenylmethyl)hydroquinone, terephthalic acid, and 3-t-butyl-4-hydroxybenzoic acid). US-A-4,603,190 to Dicke et al. discloses thermotropic aromatic polyesters derived from (a) optionally substituted p-hydroxybenzoic acid, (b) isophthalic and optionally terephthalic acid, (c) hydroquinone and (d) certain polyaromatic diols. The preferred p-hydroxybenzoic acids are p-hydroxybenzoic acids substitued in the nucleus by C 1 -C 4 alkyl or alkoxy, C 6 -C 10 aryl or C 7 -C 12 alkaryl groups or halogen. There is no express disclosure of t-butyl-4-hydroxybenzoic acid, and it is indicated that unsubstituted p-hydroxybenzoic acid is the particularly preferred hydroxycarboxylic acid. US-A-4,600,764 and US-A-4,564,669 to Dicke et al. disclose similar thermotropic aromatic polyesters incorporating an optionally substituted p-hydroxybenzoic acid as described in US-A-4,603,190. US-A-4,536,561 to Schmidt et al. discloses thermotropic, wholly aromatic polyesters based on (a) p-hydroxybenzoic acid, (b) 3-chloro-4-hydroxybenzoic acid, (c) isophthalic acid, (d) hydroquinone and (e) certain polyaromatic diols. The p-hydroxybenzoic acid (a) may be substituted by C 1 -C 4 alkyl or alkoxy, C 6 -C 10 aryl or C 7 -C 12 alkaryl groups. As in the previously mentioned patents to Dicke et al., there is no express disclosure of t-butyl-4-hydroxybenzoic acid, and it is indicated that unsubstituted p-hydroxybenzoic acid is the particularly preferred hydroxycarboxylic acid. US-A-4,299,756 to Calundann discloses melt processable wholly aromatic polyesters derived from (I) 2- or 3-phenyl-4-hydroxybenzoic acid, (II) 4-hydroxybenzoic acid, (III) at least one dioxy aryl compound which can be either hydroquinone or certain polyaromatic diols, and (IV) at least one dicarboxyl aryl moiety such as terephthalic acid. The patent thus discloses the incorporation in a polyester of a 4-hydroxybenzoic acid substituted with a phenyl group; however, there is no mention of the use of a 4-hydroxybenzoic acid substituted with any other substituent, e.g., a t-butyl substituent. Despite the wealth of work which has been done in developing new optically anisotropic melt forming aromatic copolyesters, there still exists a need for such polymers which can be easily and economically processed. It is therefore an object of this invention to provide optically anisotropic melt forming copolyesters which possess a high degree of processability and outstanding mechanical properties. Another object of this invention is to produce optically anisotropic melt forming aromatic copolyesters which may be processed by thermoplastic shaping to produce moldings, fibers, and films which have a high strength and stiffness. Surprisingly, it has been found that the copolyesters described below have this desired combination of advantageous properties. SUMMARY OF THE INVENTION The novel copolyesters of this invention are derived from components consisting essentially of: I. an aromatic diol component consisting of 55 to 95 mole % of one or more diols of the formula where R is selected from the group consisting of H, C 1 -C 4 alkyl or alkoxy, C 6 -C 10 aryl or aryloxy, and halogen; and 5 to 45 mole % of one or more polyaromatic diols; II. a dicarboxylic acid component selected from "para"- or "meta"-oriented aromatic dicarboxylic acids and mixtures thereof, provided that any napthalene dicarboxylic acid comprises not greater than 60 mole % of the dicarboxylic acid component; and III. an aromatic hydroxycarboxylic acid component consisting of 25 to 100 mole % of a t-butyl-4-hydroxybenzoic acid and 0 to 75 mole % of 4-hydroxybenzoic acid, provided that when R=H, the aromatic hydroxycarboxylic acid component consists solely of a t-butyl-4-hydroxybenzoic acid; where said copolyester contains equal chemical equivalents of components I and II and contains 15 to 60 mole %, based on total moles of I plus II plus III, of component III. These novel copolyesters are advantageous because they are fabricable in the melt using conventional molding equipment and techniques, generally at temperatures below 350 degrees C. They are anisotropic in the melt which leads to their utility as engineering plastics where high mechanical properties (e.g., stiffness and strength) and moderate temperature resistance are needed. Surprisingly, tests indicate that the copolyesters of this invention have densities significantly lower than corresponding copolyesters not containing a t-butyl-4-hydroxybenzoic acid component. DETAILED DESCRIPTION OF THE INVENTION All of the components used to prepare the copolyesters of this invention are either available commercially or may be prepared by methods well known in the art. The t-butyl-4-hydroxybenzoic acids may be prepared using the Kolbe-Schmitt reaction whereby the appropriate t-butyl substituted phenol is reacted with carbon dioxide in accordance with known techniques. The major diol component (I) in the copolyester of this invention is unsubstituted or mono-substituted hydroquinone. The preferred such diols are unsubstituted hydroquinone, or hydroquinone mono-substituted with a methyl group, chlorine, a phenyl group or a t-butyl group, and the more preferred such diols are unsubstituted hydroquinone or hydroquinone mono-substituted with chlorine, a phenyl group or a t-butyl group. Preferably, the major diol component comprises 70 to 95% of the overall diol component in the copolyester, more preferably 75 to 90% of the overall diol component. The minor diol component (I) in the copolyester of this invention is a polyaromatic diol or mixture of said diols. The term "polyaromatic" as used in this application means that the diol has two or more aromatic ring structures at least two of which form part of the backbone of the copolyester of the invention. The aromatic rings may be fused (e.g., as in naphthalene), may be directly linked (e.g., as in diphenyl), or may be connected by other moieties (e.g., as in bisphenol-A, bisphenol-AF or diphenylsulfone). The preferred diols are compounds in which, in a realistic planar representation, the bonds joining the diolic oxygens to the rest of the molecule are either colinear or parallel to each other and are not in an ortho or a peri relationship (as would be the case, e.g., with 1,8-dihydroxynaphthalene). Examples of such diol moieties are as follows: The 3,4' derivatives of these diols may also be used. The aromatic rings in the diol may optionally be substituted with one or more substitutents, e.g., alkyl, halogen, or alkyloxy and others. The preferred minor diols are 4,4'-dihydroxydiphenyl (4,4'-biphenol), 2,2'-bis(4-hydroxyphenyl)propane (bisphenol-A), 3-hydroxy-4'-(4-hydroxyphenyl)benzophenone, 3,4' or 4,4'-dihydroxybenzophenone, 2,6- or 2,7-dihydroxy-naphthalene, 4,4'-dihydroxydiphenylsulfone, 4,4'-dihydroxydiphenylether, and 4,4'-dihydroxydiphenylsulfide. The most preferred minor diols are bisphenol-A and 4,4'-biphenol in an amount of 10 to 25 mole % of the aromatic diol component. The dicarboxylic acid component of the copolyester of this invention may be one or more acids selected from "para"- or "meta"-oriented aromatic dicarboxylic acids, provided that no more than 60 mole % of the dicarboxylic acid component comprises a naphthalene dicarboxylic acid. Examples of "para"-oriented aromatic dicarboxylic acids are terephthalic acid, 1,4-naphthalene dicarboxylic acid, 1,5-napththalene dicarboxylic acid, 2,6-naphthalene dicarboxylic acid, 4,4'-diphenyl dicarboxylic acid and 3,3'-diphenyl dicarboxylic acid. (The "para"-oriented dicarboxylic acids are those in which the two carboxyl groups bonded to the aromatic rings are not adjacent to each other or in a peri relationship but are arranged coaxially or parallelly in a realistic planar representation of the molecule.) Examples of "meta"-oriented dicarboxylic acids are isophthalic acid, 1,3-naphthalene dicarboxylic acid, 1,6-naphthalene dicarboxylic acid, 1,7-naphthalene dicarboxylic acid, 2,7-naphthalene dicarboxylic acid, and 3,4'-diphenyl dicarboxylic acid. (The "meta"-oriented dicarboxylic acids are those in which the two carboxyl groups bonded to the aromatic ring(s) are not adjacent to each other or in a peri relationship and are not arranged coaxially or parallelly in a realistic planar representation of the molecule.) Any of these aromatic dicarboxylic acids may optionally be substituted with one or more substituents such as alkyl, alkyloxy or halogen, to name a few. The preferred dicarboxylic acids are terephthalic acid and mixtures of terephthalic acid with less than 50 mole % of either isophthalic acid or 2,6-naphthalene dicarboxylic acid. The more preferred dicarboxylic acid is terephthalic acid. As previously indicated, a key to the copolyesters of this invention is the fact that they contain 15 to 60 mole %, based on total moles of copolyester, of an aromatic hydroxycarboxylic acid component (III) selected from t-butyl-4-hydroxybenzoic acid or mixtures of t-butyl-4-hydroxybenzoic acid with unsubstituted 4-hydroxybenzoic acid; however, when the major diol component of the copolyester is unsubstituted hydroquinone, the aromatic hydroxycarboxylic acid component (III) consists solely of a t-butyl-4-hydroxybenzoic acid. Preferably, the copolyesters contain 20 to 50 mole % and, more preferably 20 to 35 mole %, based on total moles of copolyester, of aromatic hydroxycarboxylic acid component (III). The t-butyl-4-hydroxybenzoic acid is preferably 3-t-butyl-4-hydroxybenzoic acid, but may also be 2-t-butyl-4-hydroxybenzoic acid or a mixture of the 3- and 2- isomers. Preferably, component III consists of at least 75% 3-t-butyl-4-hydroxybenzoic acid and, more preferably, component III consists solely of 3-t-butyl-4-hydroxybenzoic acid. The preferred copolyesters of this invention consist essentially of: I. Diol: 95-70 mole% of one or more diols selected from hydroquinone or hydroquinone mono-substituted with methyl, chlorine, phenyl or t-butyl; 5-30 mole % of one or more diols selected from 4,4'-biphenol; bisphenol-A; 3-hydroxy-4'-(4-hydroxyphenyl)benzophenone, 3,4' or 4,4'-dihydroxybenzophenone, 2,6- or 2,7-dihydroxynaphthalene, 4,4'-dihydroxydiphenylsulfone, 4,4'-dihydroxydiphenylether and 4,4'-dihydroxydiphenylsulfide. II. Dicarboxylic acid: terephthalic acid or mixtures of terephthalic acid and isophthalic acid or 2,6-naphthalene dicarboxylic acid, such mixtures containing greater than 50 mole % terephthalic acid. III.Hydroxycarboxylic acid: 20-50 mole %, based on moles of I + II + III, of aromatic hydroxycarboxylic acid selected from 3-t-butyl-4-hydroxybenzoic acid or mixtures of 3-t-butyl-4-hydroxybenzoic acid with up to 25 mole % 4-hydroxybenzoic acid; provided that when the major diol component is unsubstituted hydroquinone, the aromatic hydroxycarboxlyic acid consists solely of 3-t-butyl-4-hydroxybenzoic acid. The most preferred copolyesters of this invention, by virtue of the ease with which they can be made and processed, their density properties and the outstanding mechanical properties which they possess, consist essentially of: I. Diol: 90-75 mole % of unsubstituted hydroquinone or phenyl-, chloro- or t-butyl-substituted hydroquinone; 10-25 mole % 4,4'-biphenol or bisphenol-A. II. Diacid: Terephthalic acid. III. Hydroxy-acid: 20-35 mole%, based on moles I + II + III, of 3-t-butyl-4-hydroxybenzoic acid. The copolyesters of this invention may be prepared by conventional polymerization techniques such as described in US-A-4,118,372 and in the examples below, preferably under anhydrous conditions in an inert atmosphere. The copolyesters may be formed by a variety of ester-forming techniques from organic monomers possessing functional groups which upon condensation form the requisite recurring moieties. For example, the functional groups of the organic aromatic monomer compounds may be carboxylic acid groups, acyloxy groups, or acid halide groups. The organic monomer compounds may be allowed to react in the absence of a heat exchange fluid via a melt acidolysis procedure, in a suitable solvent via a solution procedure, or in a heat exchange medium via a slurry polymerization as described in US-A-4,067,852. The copolyesters of this invention are anisotropic in the molten state at temperatures below approximately 400 degrees C, a factor which should lead to high orientation, high strength, and high initial modulus of shaped articles made from these copolyesters. Optical anisotropy of the copolyester melts can be determined by examination of the materials with the use of an optical microscope. It is known that optically anisotropic materials cause plane polarized light to be rotated, whereas rotation of polarized light is zero for transmission through isotropic materials. Thus, optical anisotropy can be determined by placing a sample of the polymer on a heating stage of a microscope set with crossed polarizers and increasing the temperature beyond the polymer flow temperature. If the polymer is optically anisotropic in the melt, a bright static field will be observed at temperatures above the polymer flow temperature. These observations may be confirmed by the use of the Thermooptical Test (TOT) described in US-A-4,066,620 and US-A-4,118,372. Polymers which pass this test are considered to be optically anisotropic. The glass transition temperatures (Tg) of the copolyesters of this invention generally range from about 140-200 degrees C, preferably about 150-190 degrees C. The inherent viscosity of the copolyesters (measured as described below) is generally at least 0.5 dL/g, preferably 1.5 dL/g or greater. The copolyesters of this invention can be used in the form of shaped articles which can be prepared from the melt phase by extrusion, injection molding, compression molding or other convenient means. Such shaped articles include films, fibers, or mechanical parts. The copolyesters of this invention may also be used in the form of coatings. Using common coating techniques, coatings can be applied to wire, films, or fabrics. Composite structures can be prepared using known methods by combining the copolyesters of this invention with fibrous substrates or particulate fillers or by combining fibers of the copolyesters of this invention with resin materials. Fibrous substrates can include woven, nonwoven, tow, felt or undirectional continuous fibers. For many applications, such as various aerospace components, carbon fibers, and aramid fibers, which produce light and strong composites, are most preferred. Other fibers include, among others, glass, boron and asbestos fibers. Particulate fillers include carbon and graphite powders, mica, silica, clay and silicon carbide whiskers. The composite structures may optionally contain additives such as antioxidants, pigments, coupling agents for fillers, lubricants and anti-stick agents. The copolyesters of this invention, their properties, their preparation and use are further illustrated by the following examples. The following test procedures were used to measure properties of the copolyesters in the examples. Inherent viscosity (n inh ), a measure of molecular weight, was computed from n inh = (ln n rel )/C where n rel is the relative viscosity and C is solution concentration in grams of polymer per deciliter of solvent. Relative viscosity is the ratio of polymer solution flow time to solvent flow time in a capillary viscometer at 25 degrees C. The solvent mixture employed consisted of 50% by volume 1,2-dichloroethane and 50% by volume 4-chlorophenol. (Other solvents which could be used include pentafluorophenol, hexafluoroisopropanol or straight 4-chlorophenol.) The concentration was 0.5 g polymer per deciliter of solvent. Thermal characterization of the polymers by differential scanning calorimetry (DSC) was performed with the use of a Du Pont Model 1090 Thermal Analyzer, equipped with a Du Pont DSC cell. A known weight of polymer (usually 5 to 10 mg) was sealed in an aluminum DSC pan and maintained under nitrogen throughout the test. The sample was subjected to a heating cycle to remove the effects of prior thermal history. This cycle consisted of heating from room temperature to 360 to 420 degrees C at a rate of 25 degrees/minute, followed by holding the sample at the final temperature for 0 to 2 minutes. The sample was then cooled from the upper hold temperature to 30 to 40 degrees C at a rate of 30 degrees/minute and then maintained at 30 to 40 degrees C for two minutes. The sample was then subjected to a second heat-up cycle. This cycle consisted of heating the sample from the lower hold temperature to 360 to 420 degrees C at a rate of 25 degrees C/minute. The glass transition temperature (T g ) is defined as the midpoint of the change in heat flow from the curve of heat flow versus temperature. The crystalline melting temperature (T m ) is defined as the maximum of the characteristic melting endotherm. The T m is recorded from the first heat-up cycle, whereas T g is recorded from the second heat-up cycle. Flexural properties of injection molded samples were measured at room temperature with an Instron machine by using a cross-head speed of 0.127 cm (0.05 inch)/min and a span of 2.54 cm (1.0 inch). The modulus (Mod) reported is the initial Young's modulus in kPa (Kpsi) units derived from a stress-strain curve determined with the use of an Instron 1.27 cm (0.5 Inch) Extensometer. The strength (Str) is the strength at break in kPa (Kpsi) units and the elongation (El) is the elongation at break in percent. Flexural properties were measured for samples in the form of flexural bars with cross section of 0.16 cm x 1.27 cm (1/16 inch x 1/2 inch). The flexural properties reported in the examples represent average properties for at least five samples. The density of the polyesters of this invention was measured by using a density gradient technique according to ASTM D1505. Samples were used in the form of compression molded film with a thickness of about 0.02 cm - 0.0254 cm (0.008-0.010 inch). The density values reported in the examples represent the average properties for three samples. In the following examples, unless otherwise indicated, the copolyesters were injection molded using a Watson Stillman 28.35 g (one ounce) injection molding machine. The ram speed was about 157.5 cm (62 inch)/min., and the total cycle time was about 40 seconds. Specific barrel temperature and pressure conditions are presented in the examples. The following abbreviations are used in the examples: HQ = hydroquinone BP = 4,4'-biphenol TPA = terephthalic acid 1,4HBA = 4-hydroxybenzoic acid TBHBA = 3-t-butyl-4-hydroxybenzoic acid The copolyesters made in the examples were prepared in a kettle fitted with (1) a stainless steel stirrer extended through a pressure-tight resin bushing, (2) a nitrogen inlet, and (3) a short column leading to a water-cooled condenser with a receiver for collecting acetic acid by-product. An attachment for application of vacuum was also provided. An electrically heated Wood's metal bath mounted for vertical adjustment was used for heating. The reaction mixture was heated to increasing temperatures with stirring at atmospheric pressure under nitrogen purge until at least about 85% of the theoretical acetic acid had evolved. The vacuum was then applied and pressure gradually reduced from atmospheric to generally less than 133 Pa (1 mm of mercury). Heating under vacuum at less than 133 Pa (1 mm mercury) presssure was then continued until viscosity had increased to a level believed satisfactory for processing into useful articles. For example, this period could have been less than 30 minutes if the final material was to be melt-spun into fibers, or could have been as long as 2 hours if the final material was to be injection-molded into shaped articles. The polymer was removed from the resin kettle while hot, cooled to room temperature, and comminuted prior to processing. In the examples, the copolyesters were prepared from the diacetate of the aromatic diols and the mono-acetate of the aromatic hydroxycarboxylic acid. The acetate derivatives were either added directly to the resin kettle or were prepared in situ . The dicarboxylic acids were used as such rather than as esters or other derivatives. The monomer ingredients were added in substantially the same molar ratios as desired in the final polymer except that an excess (0.1 to 4%) of the hydroquinone component (major diol component, I) was used. Example 1 A polymer with the composition 26.7 mole % HQ 6.7 mole % BP 33.3 mole % TPA 33.3 mole % TBHBA was prepared by mixing the following in the polymerization vessel: 31.3 g HQ diacetate (0.161 mole including 0.5% excess) 7.4 g BP (0.040 mole) 33.2 g TPA (0.200 mole) 38.8 g TBHBA (0.200 mole) 30.3 g acetic anhydride (0.297 mole) The mixture was heated with continuous stirring in the polymerization vessel from approximately 145 degrees C to approximately 295 degrees C during 200 minutes at atmospheric pressure under nitrogen purge. The reaction mixture was then heated to about 330 degrees C during 30 minutes after which time approximately 85% of theoretical acetic acid had evolved and was removed from the vessel. During about 60 minutes, the pressure was reduced from atmospheric to less than 2 kPa (15 mm mercury). The heating was continued at 330 degrees C and the pressure was reduced further to below 60 Pa (0.45 mm mercury) during about 80 minutes. After cooling and solidification, 74.6 g (87% of theoretical) of polymer was recovered. The resultant polymer displayed a crystalline melting endotherm at 394 degrees C, as determined by differential scanning calorimetry. Inherent viscosity was 1.80 dL/g measured in 1,2-dichloroethane/4-chlorophenol (50/50, v/v). The polymer formed an optically anisotropic melt at its flow temperature of 318 degrees C up to at least 400 degrees C, as determined by optical microscopy (TOT). A tough opaque film could be pressed easily at 350 degrees C. The comminuted polymer was injection molded at 330 degrees C and 6.89 kPa (280 pounds/square inch) pressure into flexural bars. The flexural modulus, flexural strength, and elongation at break were measured to be 77.7 x 10 5 kPa (1127 Kpsi), 1.24 x 10 5 kPa (18.0 Kpsi) and 2.1% respectively. Examples 2 - 7 and Comparative Examples A - D Using the same general procedure as that outlined in Example 1, the copolyesters described in Tables la-d were prepared. Their properties are listed in Tables 2a-d and 3a-d. For purposes of comparison, information for the copolyester in Example 1 is included in these tables. The "TOT" described above was used to test the polymer melt for optical anisotropy (Opt. Anis. Melt, in Tables 2). Copolyester Composition (Amounts in mole percent) Ex. "R"-substituted hydroquinone R BP T 1,4HBA TBHBA 1 26.7 H 6.7 33.3 - 33.3 A 26.7 H 6.7 33.3 33.3 - Properties of Copolyesters Ex. Inherent Viscosity (dL/g) Density (g/cc) T g (°C) Mp(°C) Opt. Anis. Melt 1 1.80 1.2651 165 394 Yes A insoluble 1.4119 119 >>400 No Flexural Properties of Copolyesters Ex. Injection Temp (°C) Pressure (psi) Modulus (Kpsi) Strength (Kpsi) Elong @ Break(%) 1 330 280 1127 18.0 2.1 A Not measured; Could not be injection molded Copolyester Composition (Amounts in mole percent) Ex. "R"-substituted hydroquinone R BP T 1,4HBA TBHBA 2 32.0 t-butyl 8.0 40.0 - 20.0 3 26.7 " 6.7 33.3 16.65 16.65 4 26.7 " 6.7 33.3 - 33.3 B 32.0 t-butyl 8.0 40.0 20.0 - Properties of Copolyesters Ex. Inherent Viscosity (dL/g) Density (g/cc) T g (°C) Mp(°C) Opt. Anis. Melt 2 2.17 1.2339 181 None Yes 3 4.57 1.2505 180 None Yes 4 4.45 1.2244 178 None Yes B insoluble -- 186 371 Yes Flexural Properties of Copolyesters Ex. Injection Temp (°C) Pressure (psi) Modulus (Kpsi) Strength (Kpsi) Elong @ Break(%) 2 310 400 1640 27.3 2.0 3 300 250-300 2255 37.6 2.7 4 300 250-300 2205 36.8 2.2 B 350 600 2082 30.6 2.1 Copolyester Composition (Amounts in mole percent) Ex. "R"-substituted hydroquinone R BP T 1,4HBA TBHBA 5 26.7 phenyl 6.7 33.3 -- 33.3 C 26.7 phenyl 6.7 33.3 33.3 -- Properties of Copolyesters Ex. Inherent Viscosity (dL/g) Density (g/cc) T g (°C) Mp(°C) Opt. Anis. Melt 5 3.00 1.2542 155 None Yes C 4.65 1.3203 156 315 Yes Flexural Properties of Copolyesters Ex. Injection Temp (°C) Pressure (psi) Modulus (Kpsi) Strength (Kpsi) Elong @ Break(%) 5 310 280 2067 38.2 2.7 C 340 250-500 2775 36.5 2.1 Copolyester Composition (Amounts in mole percent) Ex. "R"-substituted hydroquinone R BP T 1,4HBA TBHBA 6 26.7 chlorine 6.7 33.3 16.65 16.65 7 26.7 " 6.7 33.3 - 33.3 D 26.7 chlorine 6.7 33.3 33.3 - Properties of Copolyesters Ex. Inherent Viscosity (dL/g) Density (g/cc) T g (°C) Mp(°C) Opt. Anis. Melt 6 4.75 1.3680 142 None Yes 7 4.16 1.3282 150 None Yes D insoluble 1.4099 110 276 Yes Flexural Properties of Copolyesters Ex. Injection Temp (°C) Pressure (psi) Modulus (Kpsi) Strength (Kpsi) Elong @ Break(%) 6 300 500 3046 35.5 2.1 7 310 400 2320 28.1 1.1 D 320 600-900 1448 14.8 1.4 The data presented in Tables 2a-d and 3a-d indicate that the substitution of a t-butyl group on the hydroxybenzoic acid component of these copolyester resins results in copolyesters with reduced levels of crystallinity and, therefore, improved processability. This effect is particularly prominent for the copolyester of Example 1. The related comparative compound, that of Comparative Example A, was highly crystalline, became solid and immobile during the polymerization, and could not be injection molded, whereas the copolyester of Example 1 was molded easily at 330 degrees C. The crystalline melting endotherm observed for resins derived from phenyl- or chlorohydroquinone (Comparative Examples C and D) was eliminated when the 3-t-butyl-4-hydroxybenzoic acid was used (Examples 5 and 7). All copolyesters in Examples 1-7 could be injection molded below 330 deg. C, most at 300-310 deg. C. While the resin of Comparative Example B (with 20 mole % 1,4HBA) was processed at 350 deg. C, the resin of Example 2 (with 20 mole % TBHBA) was molded easily at 310 deg. C. The copolyesters of Examples 1-7 had T g 's of 142-181 deg. C, were generally non-crystalline, and had flexural modulus/strength/elongation at break of 7.6-20.7 x 10 3 kPa (1.1-3.0 Kpsi)/124.1-262.0 x 10 3 kPa (18-38 Kpsi)/1.1-2.7 %. The incorporation of the 3-t-butyl-4-hydroxybenzoic acid was also found to dramatically lower the density of the copolyesters of Examples 1-7 relative to the comparative examples.

Claims: A copolyester capable of forming an optically anisotropic melt consisting essentially of: I. an aromatic diol component consisting of 55 to 95 mole % of one or more diols of the formula where R is selected from the group consisting of H, C 1 -C 4 alkyl or alkoxy, C 6 -C 10 aryl or aryloxy, and halogen; and 5 to 45 mole % of one or more polyaromatic diols; and II. a dicarboxylic acid component selected from a "para"- or "meta"-oriented aromatic dicarboxylic acid or mixtures of such acids, provided that no more than 60 mole % of the dicarboxylic acid component comprises a naphthalene dicarboxylic acid; characterized in that the copolyester consists in addition of III. an aromatic hydroxycarboxylic acid consisting of 25 to 100 mole % of t-butyl-4-hydroxybenzoic acid and 0 to 75 mole % of 4-hydroxybenzoic acid, provided that when R=H, the aromatic hydroxycarboxylic acid component consists solely of a t-butyl-4-hydroxybenzoic acid; where said copolyester contains equal chemical equivalents of components I and II and contains 15 to 60 mole %, based on total moles of I plus II plus III, of component III. A copolyester of Claim 1 in which the aromatic diol component comprises 5 to 30 mole% of one or more diols selected from 4,4'-biphenol, bisphenol-A, 3-hydroxy-4'-(4-hydroxyphenyl)benzophenone, 3,4' or 4,4'-dihydroxybenzophenone, 2,6- or 2,7-dihydroxy-naphthalene, 4,4-dihydroxydiphenylsulfone, 4,4'-dihydroxydiphenylether, and 4,4'-dihydroxydiphenylsulfide. A copolyester of Claim 2 in which the aromatic diol component comprises 10 to 25 mole% of 4,4'-biphenol or bisphenol-A or a mixture thereof. A copolyester of Claim 1 where the aromatic diol component comprises 70 to 95 mole% of one or more diols selected from the group consisting of unsubstituted hydroquinone and hydroquinone mono-substituted with a substituent selected from methyl, chlorine, phenyl and t-butyl. A copolyester of Claim 4 where the aromatic diol component comprises 75 to 90 mole% of one or more diols selected from unsubstituted hydroquinone and hydroquinone mono-substituted with a substitutent selected from phenyl, chlorine and t-butyl. A copolyester of Claim 1 where the dicarboxylic acid is selected from the group consisting of terephthalic acid, and mixtures of terephthalic acid with isophthalic acid or, 2,6-naphthalene dicarboxylic acid, provided that at least 50 mole % of the dicarboxylic acid component is terephthalic acid. A copolyester of Claim 6 where the dicarboxylic acid is terephthalic acid. A copolyester of Claim 1 in which the t-butyl-4-hydroxybenzoic acid is 3-t-butyl-4-hydroxybenzoic acid. A copolyester of Claim 1 which contains 20-50 mole % of said hydroxycarboxylic acid component and said hydroxycarboxylic acid component consists of 75 to 100 mole % of 3-t-butyl4-hydroxybenzoic acid and 0 to 25 mole % of 4-hydroxybenzoic acid. A copolyester of Claim 9 which contains 20-35 mole % of said hydroxycarboxylic acid component and said hydroxycarboxylic acid component is 3-t-butyl-4-hydroxybenzoic acid. A copolyester of Claim 1 wherein the aromatic diol component (I) consists essentially of 5 to 30 mole % of one or more diols selected from the group consisting of 4,4'-biphenol, bisphenol-A, 3-hydroxy-4'-(4-hydroxyphenyl)benzophenone, 3,4'- or 4,4'-dihydroxybenzophenone, 2,6- or 2,7-dihydroxy-naphthalene, 4,4-dihydroxydiphenylsulfone, 4,4'-dihydroxydiphenylether, and 4,4'-dihydroxydiphenylsulfide, and 95 to 70 mole % of one or more diols selected from the group consisting of unsubstituted hydroquinone and hydroquinone mono-substituted with a substitutent selected from methyl, chlorine, phenyl and t-butyl; the aromatic diacid component (II) is selected from the group consisting of terephthalic acid and mixtures of isophthalic acid or 2,6-naphthalene dicarboxylic acid with greater than 50 mole % terephthalic acid; the aromatic hydroxycarboxylic acid component (III) is selected from 3-t-butyl-4-hydroxybenzoic acid and mixtures of 3-t-butyl-4-hydroxybenzoic acid with up to 25 mole % 4-hydroxybenzoic acid; and the copolyester contains 20 to 50 mole %, based on total moles of I + II + III, of component III. A copolyester of Claim 1 wherein the aromatic diol component (I) is 75-90 mole % of one or more diols selected from unsubstituted hydroquinone or hydroquinone mono-substituted with a phenyl group, a t-butyl group, or chlorine, and is 10-25 mole % of one or more polyaromatic diols selected from 4,4-biphenol and bisphenol-A; the aromatic diacid component (II) is terephthalic acid; the aromatic hydroxycarboxylic acid component (III) is 3-t-butyl-4-hydroxybenzoic acid; and the copolyester contains 20 to 35 mole %, based on total moles of I + II + III, of component III. A shaped article obtained by extruding, compression molding or injection molding a copolyester of Claimsl, 11 or 12. A composite structure consisting essentially of (a) a copolyester of claims 1, 11 or 12 and (b) either a fibrous substrate or a particulate filler. A composite structure consisting essentially of (a) one or more resins and (b) fibers of a copolyester of Claims 1, 11 or 12. A copolyester of Claim 1 which has an inherent viscosity of at least 1.5 dL/g measured at 25 degrees C in a 50/50 by volume mixture of 1,2-dichloroethane and 4-chlorophenol and a concentration of 0.5 g polymer per deciliter of solvent. A process for preparing a copolyester of Claim 1 comprising contacting under reaction conditions the diacetates of the aromatic diols, the monoacetates of the hydroxyacids(s), and the dicarboxylic acid(s), the monomer ingredients being added in substantially the same molar ratios as desired in the final copolyester of Claim 1 except that an excess of 0.1 to 4 mole % of the hydroquinone component of the aromatic diol component I is used.

Inventors: CONNOLLY MARK STEPHEN, CONNOLLY, MARK STEPHEN
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1988
Main classification: C08G63
IPC codes: C08G63, C08J5