Vehicle component having improved friction material

Abstract: A vehicle component such as a transmission blocker ring (81) having an improved friction material (90) is provided. Friction material (90) comprises a composite of from about 25% to about 75% by weight of a flurocarbon polymer and from about 75% to about 25% by weight of substantially uniformly dispersed ceramic fiber and which is provided with controlled crystallinity by reason of having been cooled at a rate of less than about 20°C per minute after having been sintered at a predetermined sintering or annealing temperature and time for the friction material (90) .

Description: This invention relates generally to the manufacture of vehicle parts such as a twin shaft transmission including a component such as a blocker ring enabling synchronous gear changes having an improved friction material thereupon for enhancing frictional engagement therewith and more particularly to the friction material which is a composite of ceramic fibers and fluorocarbon polymer whose frictional engagement characteristics have been improved as a result of the fluorocarbon polymer having controlled crystallinity arising from the material having been cooled at a rate of less than about 20°C per minute and more preferably less than about 5°C per minute after having been sintered for a predetermined period of time at a temperature within a predetermined sintering temperature range for the polymer or having been heated at a temperature within a predetermined annealing temperature range for the polymer for a predetermined period of time that is less than the sintering temperature range. Composites of ceramic fiber and fluorocarbon polymer, particularly polytetrafluoroethylene (PTFE) polymer, are known and are highly advantageous for use as friction material due to high temperature and corrosion resistance, particularly to greases, oils and fuel, in conjunction with having the ability to maintain a substantially constant surface friction factor under widely varying conditions. An example of a friction facing material having purportedly superior dynamic fractional torque transmitting characteristics that comprises a composite of fluorocarbon polymer and carbon particulates, and which may optionally include ceramic fibers is described in US-A-4,593,802. Another example of a material believed to be a composite of ceramic fibers and polytetrafluoroethylene (PTFE) polymer is sold under the Trademark "Gylon" by the Garlock Company. As used herein, the term "ceramic fibers" includes fibers of silicon nitride, silicon carbide and alumina-silicate fibers well known to those skilled in the art of ceramic fibers as well as including mixtures thereof. As used herein the term "fluorocarbon polymer" means those fluorocarbon polymers whose crystallinity can be increased by controlling cooling rates from sintering or annealing temperatures and includes polytetrafluoroethylene (PTFE) polymer, fluorinated ethylenepropylene copolymer (FEP), and perfluoroalkoxy copolymer (PFA) of which PTFE, FEP and PFA are sold under the Trademark "Teflon" by the Dupont Company and (PTFE) under the Trademark "Halon" by Allied Corporation. Also known is the effect that cooling rate has upon crystallinity of PTFE polymer after the latter has been sintered at a temperature of from 340°C to 440°C for a prescribed period of time and after having been annealed at a temperature of from 306°C to 323°C for a prescribed period of time, as reported by P.E. Thomas et al of the Dupont Company in an article titled "Properties of Teflon Resins" beginning page 89 in the June, 1956 SPE Journal. Generally, the article describes a substantial increase in crystallinity ranging from about 44% when the PTFE is water or air quenched after sintering to as high as 80% where it is cooled at a rate of 2°C/minute after sintering. The article further describes that although flexural modulus can be increased as much as five fold and compressive stress as much as 50% by increasing its crystallinity, compressibility can be reduced by as much as 50% and percent recovery after compression as much as 70%. Thus, in view of the above, it would appear that increasing the crystallinity of PTFE would have a detrimental effect upon the ability of PTFE in conjunction with ceramic fibers to provide an effective frictional material involving repeated engagements where some degree of compression is involved due to its loss of resiliency and inability to recover completely or substantially completely from the compression. It has been surprisingly discovered that, contrary to the teaching relative loss in resiliency and inability to recover completely or substantially completely from compression, increasing the crystallinity of a fluorocarbon polymer such as PTFE by controlling the rate of cooling after a sintering or annealing operation actually enhances its effectiveness in conjunction with ceramic fibers as a frictional material particularly in vehicular applications. According to one aspect of the invention there is provided a method for the manufacture of a fluorocarbon polymer/ceramic fibre composite friction facing material of enhanced crystallinity, the method including the steps of sintering a composite comprising from 25 to 75% fluorocarbon polymer and from 75 to 25% ceramic fibres based on the weight of the polymer and fibre content of the composite, and thereafter cooling the composite, characterised in that following sintering the composite is cooled at a rate of less than 20°C per minute. According to another aspect of the invention there is provided also a method for the manufacture of a fluorocarbon polymer/ceramic fibre composite friction facing material of enhanced crystallinity, the method including the steps of annealing a composite comprising from 25 to 75% fluorocarbon polymer and from 75 to 25% ceramic fibres based on the weight of the polymer and fibre content of the composite, and thereafter cooling the composite, characterised in that following annealing the composite is cooled at a rate of less than 20°C per minute. DETAILED DESCRIPTION OF SOME PREFERRED EMBODIMENTS An example of a vehicular component upon which the friction material of the invention can be used to advantage is a blocking ring of a twin shaft transmission as shown by way of example only in the accompanying drawing which is a partial central cross-section of a vehicular twin shaft transmission, and which is described in greater detail in US-A-3,983,979. Referring to the drawing, the transmission includes a main shaft 23 which is drivingly coupled to the vehicle engine. Shaft 23 has external splines 44 which engage with splines 43 of clutch collar 42 such that it rotates with shaft 23 as well as being able to move axially relative shaft 23. A stop 46 is provided about the periphery of splines 46 to prevent clutch collar 42 from moving towards the viewer's right beyond a predetermined location. A coiled spring 47 is provided with a recess of clutch collar 42 such that it urges it axially toward the viewer's right. Clutch collar 42 is provided with external teeth 48 that are operative to engage internal teeth 50 of drive gear 71 and causes gear 71 to rotate in unison with shaft 23 when clutch collar is moved towards the viewer's right in response to movement of a shift fork (not shown). Gear 71 has external teeth 72 that meshingly engage with external teeth 83 of driven gear 85 which is splined to counter-shaft 82 by splines 84 and causes shaft 82 to rotate in an opposite direction to shaft 23 when gear 71 is rotating. It is desirable that gears 71 and 85 mesh smoothly with each other particularly under conditions of high load and/or when gear 71 is rotating at high speed relative gear 85. In order to insure that such is the case, a blocker ring 81 is included intermediate clutch collar 81 and gear 71. Blocker ring 81 is splined to teeth 48 of clutch collar 42 and is able to move axially relative thereto. Movement of blocker ring 81 axially towards the viewer's left is prevented by stop ring 60 in gear 71 as shown in the drawing. The right end of blocker ring 81 is supported in part by resilient ring 54. Blocker ring 81 has a conical annular surface 56 about its outer periphery that is operative to register with an internal annular conical surface on gear 71, as blocker ring 81 moves towards the viewer's right. It is preferably upon surface 56 that friction material 90 is provided that is operative to enhance frictional engagement between blocker ring 81 and surface 57 of gear 71 such that blocker ring 81 is operative to frictionally engage gear 71 and ring teeth 50 into synchronous rotation with teeth 48 of clutch collar 42 before they engage as described in greater detail in US-A-3,983,979. Because of high temperatures and exposure of transmission fluids, a friction material comprising a composite of ceramic fiber and fluorocarbon polymer is particularly well suited as friction material 90 on blocking ring 81. However, as previously described, it has been discovered that performance of the composite is even further enhanced by means of controllably increasing the crystallinity of the fluorocarbon polymer in spite of the known loss of resiliency and percent recovery after compression that such increase may cause. Friction material 90 is preferably in the form of a strip that is bonded to surface 56 by a suitable adhesive well known to those skilled in the art of bonding fluorocarbon polymers to metal substrates. The adhesive may be of an epoxy type and surface 56 may be etched by a suitable etching material prior to bonding frictional material thereto as is well known to those skilled in the art. Friction material 90 is a composite of from about 25% to about 75% and more preferably from about 40% to about 60% by weight fluorocarbon polymer to the total weight of the composite of which the balance comprises ceramic fibers such as silicon nitride or silicon carbide or alumina-silicate fibers or mixtures thereof dispersed substantially uniformly therein. Friction material 90 may include other additives compatible with both the fluorocarbon polymer and ceramic fibers provided the fluorocarbon polymer content remains within the ranges described and that such to not inhibit a controlled increase in crystallinity arising from controlling cooling rate from sintering or annealing temperature ranges as hereinafter described. Preferably, the fluorocarbon polymer is polytetrafluoroethylene (PTFE) polymer due to its superior high temperature and chemical resistance. Whereas a strip or sheet of ceramic fiber and FEP or PFA polymer composites may be made by heating such polymer to their respective melt points and thence pressing them into a mold or by mixing the ceramic fibers uniformly into their respective melts and then molding the respective sheets or strip or by molding the sheet and then cutting the strip from the sheet, PTFE teflon is more difficult to process and generally is required to be melt fused into the ceramic fiber or by pressing the FEP and ceramic fibers against each other with great force such as described in US-A-4,593,802. The thickness of the strip for use on blocker 81 is preferably 1.0 to 1.5 mm (about 0.04 inch to about 0.06 inch). It has been discovered that the performance of friction material 90 is greatly improved when the composite ceramic fiber - PTFE is cooled at a rate of less than about 20°C per minute and more preferably at a rate of less than about 5°C per minute and even more preferably at a rate of less than about 2°C per minute after the material has been sintered at a temperature within a prescribed sintering temperature range for a predetermined period of time or after having been annealed at a temperature within a predetermined annealing temperature range for a predetermined period of time. For PTFE polymer the sintering temperature range is preferably from about 340°C to about 445°C and the annealing temperature range is preferably from about 300°C to about 325°C with the time period for sintering being from about 1/2 hour to about 3 hours and that for annealing being from about 5 hours to about 20 hours. Such sintering or annealing followed by cooling at a rate of less than about 5°C per minute can be done prior to bonding the composite to a vehicular component such as blocking ring 81 or afterwards where such can be handled readily and the heat will not damage the component. Situations may exist, for example which friction material 90 has been sintered and water or air quenched prior to bonding to the component and thence annealed after bonding to the component followed by cooling at a rate of less than about 5°C per minute. By way of example, a composite of about 60% by weight PTFE and about 40% by weight ceramic fiber 1.27 mm (about 0.05 inch) thick exhibited a relative crystallinity of about 0.108 when measured by a differential scanning calorimeter (DSC) when air or water quenched after sintering versus a relative crystallinity of about 0.332 when cooled at a rate of less than about 5°C per minute which represents over a 300% increase in relative crystallinity. By way of further example, composites of about 60% by weight PTFE and ceramic fiber about 2.05 millimeters thick and having respective relative crystallinity values of 0.142 and 0.161 as measured by DSC where compared in a vibratory damping test using Dupont Dynamic analysis (DMA) test equipment. The results of the DMA test showed that the friction material having the .161 relative crystallinity, which is about 13.4% grater than the .142 friction material, exhibited a glass transition point at about 155.75°C versus one at about 149.80°C for the .142 material as well as about a 5% increase in elastic modulus as might be expected but also exhibited about a 10% decrease in ability to dampen the vibrations which is indicative of loss of resilience as previously described. When tested under actual operating conditions on a twin shaft transmission which involved repeated engagements and disengagements between blocker ring 90 and the driven gear 85 previously described, the friction material having the 0.107 relative crystallinity lasted over one million cycles whereas that having the 0.096 relative crystallinity lasted only about 300,000 cycles. Thus, it is clear that, although taught away from by the art, controlling cooling rate at less than 20°C per minute and more preferably less than about 5°C per minute from sintering or annealing temperatures for a composite of ceramic fiber and flurocarbon polymer can be of great advantage in providing improved frictional engagement characteristics for vehicular components such as twin shaft transmission blocker rings as well as any other vehicle part having a component that in one way or another case utilizes the improved frictional material described herein.

Claims: A method for the manufacture of a fluorocarbon polymer/ceramic fibre composite friction facing material of enhanced crystallinity, the method including the steps of sintering a composite comprising from 25 to 75% fluorocarbon polymer and from 75 to 25% ceramic fibres based on the weight of the polymer and fibre content of the composite, and thereafter cooling the composite, characterised in that following sintering the composite is cooled at a rate of less than 20°C per minute. A method for the manufacture of a fluorocarbon polymer/ceramic fibre composite friction facing material of enhanced crystallinity, the method including the steps of annealing a composite comprising from 25 to 75% fluorocarbon polymer and from 75 to 25% ceramic fibres based on the weight of the polymer and fibre content of the composite, and thereafter cooling the composite, characterised in that following annealing the composite is cooled at a rate of less than 20°C per minute. A method according to claim 1 or claim 2, wherein the composite comprises from 40 to 60% fluorocarbon polymer and from 60 to 40% ceramic fibres based on the weight of the polymer and fibre content of the composite. A method according to any one of claims 1 to 3, wherein the fluorocarbon polymer is selected from polytetrafluoroethylene, fluorinated ethylene/propylene copolymer and perfluoroalkoxy copolymer. A method according to claim 4, wherein the fluorocarbon polymer is polytetrafluoroethylene and wherein sintering is carried out at a temperature of 340 to 445°C for a period of 0.5 to 3 hours. A method according to claim 4, wherein the fluorocarbon polymer is polytetrafluoroethylene and wherein annealing is carried out at a temperature of 300 to 325°C for a period of 5 to 20 hours. A method according to any one of claims 1 to 6, wherein the composite is cooled at a rate of less than 5°C per minute. A method according to any one of claims 1 to 7, wherein the composite is cooled at a rate of less than 2°C per minute. A fluorocarbon polymer/ceramic fibre composite manufactured by a method according to any one of claims 1 to 8, in the form of a blocker ring for a vehicle twin shaft transmission.

Inventors: GENISE THOMAS ALAN, PUSATCIOGLU SELAMI YALCIN, GENISE, THOMAS ALAN, PUSATCIOGLU, SELAMI YALCIN
Applicants: EATON CORP, EATON CORPORATION
Application year: 1988
Main classification: F16D69
IPC codes: F16H63, C09K3, F16D13, F16D69