Thermoplastic resin composition and method for preparing the same

Abstract: There is here provided a thermoplastic resin composi­ tion containing (I) 99 to 1% by weight of a polypropylene, (II) 1 to 99% by weight of at least one kind of resin selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a poly­ phenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer and an ABS resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I) + (II), of a multi-­ phase structure thermoplastic resin which is composed of 5 to 95% by weight of a polyolefin and 95 to 5% by weight of a vinyl polymer or copolymer obtained from at least one kind of vinyl monomer, either of both the components being in the state of a dispersion phase having a particle diameter of 0.001 to 10 µm. A method for preparing the above-mentioned thermoplastic resin composition is also provided here.

Description: BACKGROUND OF THE INVENTION (1) Field of the Invention The present invention relates to a thermoplastic resin composition having excellent chemical resistance, moldability, impact resistance, heat resistance, coating properties, mechanical properties and appearance of molded articles made therefrom, and a method for preparing the same. The composition of the present case can be widely utilized as a material for electrical and electronic parts, machine parts, automobile parts and the like. (2) Description of the Prior Art The so-called engineering plastics such as aromatic polyester resins, polycarbonate resins, polyamide resins and polyphenylene ether resins have excellent mechanical properties, heat resistance, stiffness and impact resistance. Furthermore, ABS resins and polypropylenes are widely used for various molded articles because of having excellent chemical resistance, moldability and the like, and because of being inexpensive. In recent years, with regard to not only the engineering plastics but also the ABS resins and polypropylenes, new additional functions are demanded, and various attempts have been made. One of them is a composition comprising a combination of plural plastics, and this composition has features of the respective plastics and is known as a polymer alloy. For example, combinations of engineering plastics such as an aromatic polyester resin/a polyphenylene ether resin and a polycarbonate resin/an ABS resin are known from relatively long ago, but examples of polymer alloys of polypropylenes and the engineering plastics are extremely limited. If a material can be provided with mechanical properties, heat resistance, stiffness, impact resistance and coating properties and the like, maintaining moldability and chemical resistance as well as inexpensiveness which are characteristics of the polypropylene, such a material will be industrially useful. However, the polypropylene and each of such plastics as mentioned above are difficult to mutually mix, and therefore merely by melting and mixing these materials, the polymer alloy cannot be obtained. In Japanese Patent Unexamined Publication Nos. 61-62542 and 61-64741, examples are disclosed in which polyamide resins are blended with a polypropylene, and in Japanese Patent Unexamined Publication Nos. 61-60744 and 61-60746, examples are disclosed in which aromatic polyester resins are blended with a polypropylene. In these examples, acid anhydride-modified polypropylenes and epoxy group-containing ethylene copolymers are used to facilitate the mixing of these resins. In this case, the compatibility of the two resins with each other is higher than when they are simply mixed, but there are drawbacks such as the increase in melting viscosity. EP-A-206 644 relates to a block copolymer A, which is obtained by copolymerizing a (meth)acrylic acid ester monomer with a peroxy carbonate and has peroxy groups pendant to its main polymer chain and segments of (co)polymer B, which is different from copolymer A in the monomer composition and does not contain peroxy groups. This polymer is said to be useful for modifying resins and the like. However, no mention is made in this reference about a possible use of said copolymer as an agent for improving the compatibility. In addition, with regard to resins other than the polyamide resins and aromatic polyesters, any examples of improved compatibility have not been present. SUMMARY OF THE INVENTION The inventors of the present application have intensively researched to solve the above-mentioned problems, and as a result, they have found that when a specific multi-phase structure thermoplastic resin is used, the compatibility of a polypropylene with an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or the like can be improved, so that a thermoplastic resin composition can be obtained which retains excellent moldability and chemical resistance of the polypropylene and which additionally has good heat resistance, mechanical properties, stiffness, impact resistance and coating properties. That is, the first aspect of the present invention is directed to a thermoplastic resin composition containing (I) 99 to 1% by weight of a polypropylene, (II) 1 to 99% by weight of at least one kind of resin selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer in an amount of 0 to 95% by weight of the polyphenylene ether resin and an ABS resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I) + (II), of a multi-phase structure thermoplastic resin which is a graft copolymer composed of 5 to 95% by weight of a polyolefin and 95 to 5% by weight of a vinyl polymer or copolymer obtained from at least one kind of vinyl monomer, either of the graft copolymer components being in the state of a dispersion phase having a particle diameter of 0.001 to 10 µm, and wherein the vinyl polymer or copolymer in the multi-phase structure thermoplastic resin has an average polymerization degree of 5 to 10 000. The second aspect of the present invention is directed to a method for preparing a thermoplastic resin composition which comprises the step of melting and mixing 99 to 1% by weight of a polypropylene (I) and 1 to 99% by weight of at least one kind of resin (II) selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer in an amount of 0 to 95% by weight of the polyphenylene ether resin and an ABS resin, with 1 to 100% by weight of a graft polymerization precursor (A) which is obtained by first adding at least one kind of vinyl monomer, at least one kind of radical polymerizable or copolymerizable organic peroxide and a radical polymerization initiator to an aqueous suspension of a polyolefin, then heating the suspension under such conditions that the decomposition of the radical polymerization initiator does not occur substantially, in order to impregnate the polyolefin with the vinyl monomer, the radical polymerizable or copolymerizable organic peroxide and the radical polymerization initiator, and raising the temperature of this aqueous suspension, when the degree of the impregnation has reached 50% by weight of the original total weight of the vinyl monomer, peroxide and initiator, in order to copolymerize the vinyl monomer with the radical polymerizable or copolymerizable organic peroxide in the polyolefin, 0 to 99% by weight of the polyolefin (B), and 0 to 99% by weight of a vinyl polymer or copolymer (C) obtained by polymerizing at least one kind of vinyl monomer, wherein said vinyl polymer or copolymer has an average polymerization degree of 5 to 10,000. or alternatively melting and mixing the components (A), (B) and (C) previously at a temperature in the range of 150 to 350°C in order to form a multi-phase structure thermoplastic resin (III), and then melting and mixing the resin (III) with the resins (I) and (II). BRIEF DESCRIPTION OF THE PHOTOGRAPHS Photograph No. 1 is the electron microscope photograph (10,000 magnifications) of the multi-phase structure thermoplastic resin prepared in Preparation Example 1 in which spherical styrene polymer particles having a diameter of 0.3 to 0.7 µm are dispersed in a matrix comprising a polypropylene homopolymer (PP). This photograph is indicated with "PP-g-PSt: multi-phase structure thermoplastic resin". Photograph No. 2 is the electron microscope photograph (5,000 magnifications) of the multi-phase structure thermoplastic resin prepared in Preparation Example 3 in which spherical styrene polymer particles having a diameter of 0.1 to 0.3 µm are dispersed in a matrix comprising ethylene-glycidyl methacrylate (E-GMA). This photograph is indicated with "E-GMA-g-PSt: multi-phase structure thermoplastic resin". Photograph No. 3 is the electron microscope photograph (1,000 magnifications) of a blend composition (Reference Example 1) which is prepared by first blending the polypropylene homopolymer (PP) used in Preparation Example 1 with 30% by weight of polystyrene (PSt) and then mixing them under melting. This photograph is indicated with "PP/PSt: blend composition". DETAILED DESCRIPTION OF THE INVENTION A polypropylene (I) used in the present invention is a crystallizable polypropylene, and examples of the polypropylene include, in addition to the homopolymer of propylene, block and random copolymers of propylene and α-olefins such as ethylene and butene-1. An aromatic polyester used in the present invention is a polyester having an aromatic ring on a chain unit thereof, and it is a polymer or copolymer obtained by subjecting, to condensation reaction, an aromatic/dicarboxylic acid (or its ester-forming derivative) and a diol (or its ester-forming derivative) as main components. Examples of the aromatic dicarboxylic acid mentioned above include terephthalic acid, isophthalic acid, phthalic acid, 2,6-naphthalenedicarboxylic acid, 1,5-naphthalenedicarboxylic acid, bis(p-carboxyphenyl)methane, anthracenedicarboxylic acid, 4,4'-diphenyldicarboxylic acid, 4,4'-diphenyl ether dicarboxylic acid, 1,2-bis(phenoxy)ethane-4,4'-dicarboxylic acid, and ester-forming derivatives thereof. Examples of the above-mentioned diol component include aliphatic diols having 2 to 10 carbon atoms, i.e., ethylene glycol, propylene glycol, 1,4-butanediol, neopentyl glycol, 1,5-pentanediol, 1,6-hexanediol, decamethylene glycol and cyclohexanediol; long-chain glycols each having a molecular weight of 400 to 6,000, i.e., polyethylene glycol, poly(1,3-propylene glycol) and polytetramethylene glycol; and mixtures thereof. Typical and preferable examples of the thermoplastic aromatic polyester resin used in the present invention include polyethylene terephthalate, polypropylene terephthalate, polybutylene terephthalate, polyhexamethylene terephthalate, polyethylene-2,6-naphthalate and polyethylene-1,2-bis(phenoxy)ethane-4,4'-dicarboxylate. Of these examples, polyethylene terephthalate and polybutylene terephthalate are more preferable. The intrinsic viscosity of the thermoplastic aromatic polyester resin is preferably in the range of 0.4 to 4.0 dl/g at 25±0.1°C at a concentration of 0.32 g in 100 milliliters of trifluoric acid (25)/methylene chloride (75). When the intrinsic viscosity is less than 0.4 dl/g, the thermoplastic aromatic polyester resin cannot exert mechanical strength sufficiently. Inversely, when it is in excess of 4.0 dl/g, the flowability of the resin deteriorates, which leads to the decline of the surface gloss on molded articles thereof. The polycarbonate resin used in the present invention include 4,4-dioxyallylalkane polycarbonates typified by a polycarbonate of 4,4-dihydroxydiphenyl-2,2-propane (generally called bisphenol A), but above all, 4,4-dihydroxydiphenyl-2,2-propane polycarbonate having a number average molecular weight of 15,000 to 80,000 is preferable. This polycarbonate may be prepared by an optional method. For example, 4,4-dihydroxydiphenyl-2,2-propane polycarbonate may be prepared by blowing phosgene in 4,4-dihydroxydiphenyl-2,2-propane as a dioxine compound in the presence of an aqueous caustic alkali solution and a solvent, or alternatively by carrying out ester interchange between 4,4-dihydroxydiphenyl-2,2-propane and a diester carbonate in the presence of a catalyst. The polyphenylene ether resin used in the present invention is a polymer obtained by oxidizing and polymerizing a phenolic compound represented by the general formula wherein each of R₁, R₂, R₃, R₄ and R₅ is selected from the group consisting of a hydrogen atom, a halogen atom, a hydrocarbon group or a substituted hydrocarbon group, and at least one of them is a hydrogen atom, with oxygen or an oxygen-containing gas in the presence of a coupling catalyst. Typical examples of R₁, R₂, R₃, R₄ and R₅ in the above-mentioned general formula include hydrogen, chlorine, fluorine, iodine, bromine, methyl, ethyl, propyl, butyl, chloroethyl, hydroxyethyl, phenylethyl, benzyl, hydroxymethyl, carboxyethyl, methoxycarbonylethyl, cyanoethyl, phenyl, chlorophenyl, methylphenyl, dimethylphenyl and ethylphenyl. Typical examples of the phenolic compounds having the above-mentioned general formula include phenol, o-, m- and p-cresols, 2,6-, 2,5-, 2,4- and 3,5-dimethylphenols, 2-methyl-6-phenylphenol, 2,6-diphenylphenol, 2,6-dimethylphenol, 2-methyl-6-ethylphenol, and 2,3,5-, 2,3,6- and 2,4,6-trimethylphenols. These phenolic compounds may be used in a combination of two or more thereof. Other examples of the phenolic compound used in the present invention include copolymers of the phenolic compounds having the above general formula with divalent phenols such as bisphenol A, tetrabromobisphenol A, resorcin and hydroquinone. Examples of the styrene polymer used in the present invention include homopolymers such as polystyrene, poly(α-methylstyrene) and poly(p-methylstyrene), polystyrenes modified with butadiene rubber, styrene-butadiene copolymer, ethylene-propylene copolymer and ethylene-propylene-diene copolymer, styrene-maleic anhydride copolymer, styrene-acrylonitrile copolymer, styrene-acrylonitrile-butadiene copolymer and styrene-methylmethacrylate copolymer. The styrene copolymer is used in an amount of 0 to 95% by weight with respect to the polyphenylene ether resin. Examples of a polyamide resin used in the present invention include aliphatic polyamide resins such as 6-nylon, 6,6-nylon, 6,10-nylon, 6,12-nylon, 11-nylon, 12-nylon and 4,6-nylon; aromatic polyamide resins such as polyhexamethylenediamine terephthalamide, polyhexamethylenediamine isophthalamide and xylene group-containing polyamide; modified compounds of these polyamides; and mixtures thereof. The particularly preferable polyamides are 6-nylon and 6,6-nylon. The ABS resin used in the present invention is a grafted copolymer (a) obtained by polymerizing, in the presence of a conjugated diene rubber, two or more compounds selected from the group consisting of vinyl cyanide compounds, aromatic vinyl compounds and alkyl ester compounds of unsaturated carboxylic acids. If desired, the ABS resin may contain a copolymer (b) obtained by polymerizing two or more compounds selected from the group consisting of vinyl cyanide compounds, aromatic vinyl compounds and alkyl ester compounds of unsaturated carboxylic acids. The composition ratio between the conjugated diene rubber and the above-mentioned compound in the grafted copolymer (a) is not particularly limited, but the preferable composition ratio is 5 to 80% by weight of the conjugated diene rubber and 95 to 80% by weight of the above-mentioned compound. Furthermore, the composition ratio among the respective compounds mentioned above is preferably 0 to 30% by weight of the vinyl cyanide compound, 30 to 80% by weight of the aromatic vinyl compound and 0 to 70% by weight of the alkyl ester compound of an unsaturated carboxylic acid. With regard to the particle diameter of the conjugated diene rubber, it is not particularly limited, but preferably it is in the range of 0.05 to 1 µm. In the case of the copolymer (b), the preferable composition ratio of the respective compounds is 0 to 30% by weight of the vinyl cyanide compound, 50 to 90% by weight of the aromatic vinyl compound and 0 to 40% by weight of the alkyl ester of an unsaturated carboxylic acid. The intrinsic viscosity [30°C, dimethylformamide (DMF)] of the copolymer (b) is not particularly limited, either, but it is preferably in the range of 0.25 to 1.0. Examples of the conjugated diene rubber include polybutadienes, butadiene-styrene copolymers and butadiene-acrylonitrile copolymers. Moreover, examples of the vinyl cyanide compound include acrylonitrile and methacrylonitrile, examples of the aromatic vinyl compound include styrene, α-methylstyrene, vinyltoluene, dimethylstyrene and chlorostyrene; and exampies of the alkyl ester compound of an unsaturated carboxylic acid include methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate and hydroxyethyl acrylate. The ABS resin may be prepared in accordance with, for example, an emulsion polymerization process, a suspension polymerization process, a solution polymerization process, a mass polymerization process or an emulsion-suspension polymerization process. The multi-phase structure thermoplastic resin (III) used in the present invention is a polyolefin or a vinyl polymer or copolymer matrix in which another vinyl polymer or copolymer or polyolefin is uniformly dispersed in a spherical form. The polyolefin mentioned above is at least one selected from the group consisting of a propylene polymer and/or an epoxy group-containing ethylene copolymer, an ethylene-unsaturated carboxylic acid or its alkyl ester copolymer, or its metallic salt, and an ethylene-vinyl ester copolymer. The propylene polymer is different from the above-mentioned polypropylene (I), and examples of the propylene polymer include the homopolymer of propylene, block and random copolymers of propylene and, for example, α-olefins such as ethylene and butene-1, ethylene-propylene copolymer rubber, and ethylene propylene-diene copolymer rubber. In particular, when the aromatic polyester and polyamide are used, it is preferred that not only the propylene polymer but also the ethylene copolymer is employed as the additional polyolefin, because the compatibility of the polyolefins with the aromatic polyester and polyamide can be remarkably improved. Above all, the epoxy group-containing ethylene copolymer reacts with the aromatic polyester and polyamide, and therefore its effect is surprising. The polymer dispersed in the multi-phase structure thermoplastic resin has a particle diameter of 0.001 to 10 µm, preferably 0.01 to 5 µm. When the particle diameter of the dispersed polymer is less than 0.001 µm or is more than 10 µm, the compatibility of the polypropylene (I) with the resin (II), for example, the above-mentioned aromatic polyester is bad, with the result that impact resistance deteriorates. The vinyl polymer or copolymer in the multi-phase thermoplastic resin (III) used in the present invention has a number average polymerization degree of 5 to 10,000, preferably 10 to 5,000. When the number average polymerization degree is less than 5, impact resistance of the thermoplastic resin composition regarding the present invention can be improved, but heat resistance deteriorates unpreferably. Inversely, when it is in excess of 10,000, melting viscosity is high, moldability deteriorates, and surface gloss falls off unpreferably. The multi-phase thermoplastic resin (III) used in the present invention comprises 5 to 95% by weight, preferably 20 to 90% by weight, of the polyolefin. Therefore, the content of the vinyl polymer or copolymer is 95 to 5% by weight, preferably 80 to 10% by weight. When the polyolefin is less than 5% by weight, its compatible effect with the polypropylen is not exerted sufficiently, and when it is more than 95% by weight, heat resistance and dimensional stability of the thermoplastic resin regarding the present invention are impaired unpreferably. The polyolefin in the multi-phase structure thermoplastic resin used in the present invention is at least one selected from the group consisting of an epoxy group-containing copolymer, an ethylene-unsaturated carboxylic acid or its alkyl ester copolymer, or its metallic salt, and an ethylene-vinyl ester copolymer. This ethylene copolymer can be preferably prepared by a high-pressure radical polymerization. The epoxy group-containing ethylene copolymer mentioned above is a copolymer of ethylene and an unsaturated glycidyl group-containing monomer, a three-dimensional copolymer of an olefin, an unsaturated glycidyl group-containing monomer and another unsaturated monomer, or a terpolymer. The preferable epoxy group-containing ethylene copolymer is composed of 60 to 99.5% by weight of ethylene, 0.5 to 40% by weight of a glycidyl group-containing monomer and 0 to 39.5% by weight of the other unsaturated monomer. Examples of the unsaturated glycidyl group-containing monomer include glycidyl acrylate, glycidyl methacrylate, itaconic acid monoglycidyl ester, butenetricarboxylic acid monoglycidyl ester, butenetricarboxylic acid diglycidyl ester, butenetricarboxylic acid triglycidyl ester, vinyl glycidyl ethers and glycidyl esters of maleic acid, crotonic acid and fumaric acid, allyl glycidyl ether, glycidyloxy ethylvinyl ether, glycidyl ethers such as styrene p-glycidyl ether, and p-glycidyl styrene. The particularly preferable ones are glycidyl methacrylate and allyl glycidyl ether. Other examples of the unsaturated monomers include olefins, vinyl esters, α,β-ethylenic unsaturated carboxylic acids and their derivatives. Typical examples of such unsaturated monomers include olefins such as propylene, butene-1, hexene-1, decene-1, octene-1 and styrene, vinyl esters such as vinyl acetate, vinyl propionate and vinyl benzoate, acrylic acid, methacrylic acid, esters such as methyl, ethyl, propyl, butyl, 2-ethylhexyl, cyclohexyl, dodecyl and octadecyl acrylates and methacrylates, maleic acid, maleic anhydride, itaconic acid, fumaric acid, maleic monoesters and diesters, vinyl ethers such as vinyl chloride, vinyl methyl ether and viny ethyl ether, and acrylic amide compounds. Particularly, acrylic and methacrylic esters are preferable. Typical examples of the epoxy group-containing ethylene copolymer include ethylene-glycidyl methacrylate copolymer; ethylene-vinyl acetate-glycidyl methacrylate copolymer; ethylene-ethyl acrylate-glycidyl methacrylate copolymer; ethylene-carbon monoxide-glycidyl methacrylate copolymer; ethylene-glycidyl acrylate copolymer; and ethylene-vinyl acetate-glycidyl acrylate copolymer. Above all, ethylene-glycidyl methacrylate copolymer, ethylene-ethyl acrylate-glycidyl methacrylate copolymer and ethylene-vinyl acetate-glycidyl methacrylate copolymer are preferred. These epoxy group-containing olefin copolymers can be used in a mixture thereof. Additional examples of the epoxy group-containing ethylene copolymer of the present invention include modified compounds prepared by the addition reaction of the above-mentioned unsaturated glycidyl group-containing monomers to conventional olefin homopolymers and copolymers. Examples of the above-mentioned ethylene polymer include low-density, medium-density and high-density polyethylenes, ethylene-propylene copolymer, ethylene-butene-1 copolymer, ethylene-hexene-1 copolymer, ethylene-4-methylpentene-1 copolymer, copolymers with other α-olefins mainly comprising ethylene such as ethylene-octene-1 copolymer, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, copolymers of ethylene and methyl, ethyl, propyl, isopropyl and butyl acrylate and methacrylate, ethylene-maleic acid copolymer, ethylene-propylene copolymer rubber, ethylene-propylene-diene-copolymer rubber, etylene-vinyl acetate-vinyl chloride copolymer, mixtures thereof, and mixtures of these compounds with other kinds of synthesized resins and rubbers. Examples of an unsaturated carboxylic acid as well as its alkyl ester and vinyl ester monomers for the ethylene-unsaturated carboxylic acid or its alkyl ester copolymer, or its metallic salt, and the ethylene-vinyl ester copolymer include unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic acid, fumaric acid, maleic anhydride and itaconic anhydride; unsaturated alkyl carboxylate monomers such as methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, isopropyl acrylate, isopropyl methacrylate, n-butyl acrylate, n-butyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, lauryl acrylate, lauryl methacrylate, stearyl acrylate, stearyl methacrylate, monomethyl maleate, monoethyl maleate, diethyl maleate and monomethyl fumarate; and vinyl ester monomers such as vinyl propionate, vinyl acetate, vinyl caproate, vinyl caprylate, vinyl laurate, vinyl stearate and vinyl trifluoroacetate. Of these compounds, ethyl acrylate and vinyl acetate are particularly preferable. The above-mentioned monomers can be used in the form of a mixture thereof. Furthermore, in the ethylene polymer used in the present invention, an ion-crosslinked ethylene copolymer ionomer is also included, and the ion-crosslinked ethylene copolymer may be prepared by reacting a metallic compound having a valence of 1 to 3 in the groups I, II, III, IV-A and VI of the periodic table with a modified copolymer obtained by the addition polymerization of the above-mentioned unsaturated carboxylic acid such as acrylic acid, maleic acid or maleic anhydride to a low-density, medium-density or high-density polyethylene or ethylene-α-olefin copolymer, or with the above-mentioned modified copolymer obtained by random or addition polymerization. Preferable examples of the metallic compound include borates, acetates, oxides, hydroxides, methoxides, ethoxides, carbonates and bicarbonates. Examples of the metallic ion include Na⁺, K⁺, Ca⁺⁺, Mg⁺⁺, Zn⁺⁺, Ba⁺⁺, Fe⁺⁺, Fe⁺⁺⁺, Co⁺⁺, Ni⁺⁺ and Al⁺⁺⁺. Of these ions, Na⁺, Mg⁺⁺ and Zn⁺⁺ are particularly preferable. These metallic compounds may be used in a combination of two or more thereof, if necessary. The ethylene copolymer may be prepared by a high-pressure radical polymerization, e.g., by simultaneously or stepwise contacting and polymerizing a monomer mixture of 60 to 99.5% by weight of the above-mentioned ethylene, 0.5 to 40% by weight of one or more unsaturated glycidyl group-containing monomer, and 0 to 39.5% by weight of at least one other unsaturated monomer, or a monomer mixture of 50 to 99.5% by weight of ethylene, 50 to 0.5% by weight of at least one monomer selected from the group consisting of an unsaturated carboxylic acid, its alkyl ester and/or a vinyl ester and 0 to 49.5% by weight of another unsaturated monomer in the presence of 0.0001 to 1% by weight of a radical polymerization initiator based on the total weight of all the monomers at a polymerization pressure of 500 to 4,000 kg/cm², preferably 1,000 to 3,500 kg/cm², at a reaction temperature of 50 to 400°C, preferably 100 to 350°C, using a chain transfer agent and, if necessary, some auxiliary agents in an autoclave or tubular reactor. Examples of the above-mentioned radical polymerization initiator include usual initiators such as peroxides, hydroperoxides, azo-compounds, amine oxide compounds and oxygen. Examples of the chain transfer agent include hydrogen, propylene, butene-1, saturated aliphatic hydrocarbons having 1 to 20 carbon atoms such as methane, ethane, propane, butane, isobutane, n-hexane, n-heptane and cycloparaffins; halogen-substituted hydrocarbons such as chloroform and carbon tetrachloride; saturated aliphatic alcohols such as methanol, ethanol, propanol and isopropanol; saturated aliphatic carbonyl compounds having 1 to 20 or more carbon atoms such as carbon dioxide, acetone and methyl ethyl ketone; and aromatic compounds such as toluene, diethylbenzene and xylene. Typical examples of the vinyl polymer and copolymer in the multi-phase structure thermoplastic resin (III) used in the present invention include polymers and copolymers prepared by polymerizing one or more of vinyl monomers such as vinyl aromatic monomers, for example, styrene, nucleus-substituted styrenes such as methylstyrene, dimethylstyrene, ethylstyrene, isopropylstyrene and chlorostyrene, and α-substituted styrene such as α-methylstyrene and α-ethylstyrene; acrylate and methacrylate monomers, for example, alkyl esters having 1 to 7 carbon atoms of acrylic acid or methacrylic acid such as methyl, ethyl, propyl, isopropyl and butyl acrylate and methacrylate; acrylonitrile and methacrylonitrile monomers; vinyl ester monomers such as vinyl acetate and vinyl propionate; acrylamide and methacrylamide monomers; and monoesters and diesters of maleic anhydride and maleic acid. Above all, the vinyl polymer and copolymer containing 50% by weight or more of a vinyl aromatic monomer are particularly preferable. Preferable monomers are those selected from the group consisting of vinyl aromatic monomers, acrylate and methacrylate monomers, acrylonitrile and methacrylonitrile monomers, and vinyl ester monomers. As a grafting technique used to prepare the multi-phase structure thermoplastic resin regarding the present invention, there may be employed a well known process such as a chain transfer process and an ionizing radiation process, but the following process is most preferable, because grafting efficiency is high, secondary cohesion due to heat does not occur, and therefore performance can be exerted effectively. Now, a method for preparing the thermoplastic resin composition of the present invention will be described in detail. That is, water is suspended in 100 parts by weight of a polyolefin. Afterward, 5 to 400 parts by weight of at least one vinyl monomer is added to the suspension, and in the mixture, a solution is poured in which there are dissolved 0.1 to 10 parts by weight, based on 100 parts by weight of the vinyl monomer, of one or a mixture of radical polymerizable or copolymerizable organic peroxides represented by the undermentioned general formula (a) or (b) and 0.01 to 5 parts by weight, based on 100 parts by weight of the total of the vinyl monomer and the radical polymerizable or copolymerizable organic peroxide, of a radical polymerization initiator in which a decomposition temperature to obtain a half-life period of 10 hours is from 40 to 90°C. The mixture is then heated under conditions that the decomposition of the radical polymerization initiator does not occur substantially, in order to impregnate the polyolefin with the vinyl monomer, the radical polymerizable or copolymerizable organic peroxide and the radical polymerization initiator. When the impregnation ratio has reached 50% by weight or more of the original total weight of the monomer, peroxide and initiator, the temperature of this aqueous suspension is raised to copolymerize the vinyl monomer with the radical polymerizable or copolymerizable organic peroxide in the polyolefin, thereby obtaining a graft polymerization precursor (A). This graft polymerization precursor (A) also is the multi-phase structure thermoplastic resin. Therefore, in order to obtain the thermoplastic resin composition of the present invention, this graft polymerization precursor may be directly mixed under melting with at least one resin (II) selected from the group consisting of a polypropylene, an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin alone or a mixture of the polyphenylene ether resin and a styrene polymer in an amount of 0 to 95% by weight of the polyphenylene ether resin, and an ABS resin, but in the best case, the multi-phase thermoplastic resin (III) obtained by kneading the graft polymerization precursor is mixed with a polypropylene and the resin (II). The above-mentioned radical polymerizable or copolymerizable organic peroxides are compounds represented by the general formulae (a) and (b): wherein R₁ is a hydrogen atom or an alkyl group having 1 or 2 carbon atoms, each of R₂ and R₇ is a hydrogen atom or a methyl group, R₆ is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, each of R₃, R₄, R₈ and R₉ is an alkyl group having 1 to 4 carbon atoms, each of R₅ and R₁₀ is an alkyl group having 1 to 12 carbon atoms, a phenyl group, an alkyl-substituted phenyl group or a cycloalkyl group having 3 to 12 carbon atoms, m is 1 or 2, and n is 0, 1 or 2. Typical examples of the radical polymerizable or copolymerizable organic peroxides represented by the general formula (a) include t-butylperoxyacryloyloxyethyl carbonate, t-amylperoxyacryloyloxyethyl carbonate, t-hexylperoxyacryloyloxyethyl carbonate, 1,1,3,3-tetramethylbutylperoxyacryloyloxyethyl carbonate, cumylperoxyacryloyloxyethyl carbonate, p-isopropylperoxyacryloyloxyethyl carbonate, t-butylperoxymethacryloyloxyethyl carbonate, t-amylperoxymethacryloyloxyethyl carbonate, 1,1,3,3-tetramethylbutylperoxymethacryloyloxyethyl carbonate, cumylperoxymethacryloyloxyethyl carbonate, p-isopropylperoxymethacryloyloxyethyl carbonate, t-butylperoxyacryloyloxyethoxyethyl carbonate, t-amylperoxyacryloyloxyethoxyethyl carbonate, t-hexylperoxyacryloyloxyethoxyethyl carbonate, 1,1,3,3-tetramethylbutylperoxyacryloyloxyethoxyethyl carbonate, cumylperoxyacryloyloxyethoxyethyl carbonate, p-isopropylperoxyacryloyloxyethoxyethyl carbonate, t-butylperoxymethacryloyloxyethoxyethyl carbonate, t-amylperoxymethacryloyloxyethoxyethyl carbonate, t-hexylperoxymethacryloyloxyethoxyethyl carbonate, 1,1,3,3-tetramethylbutylperoxymethacryloyloxyethoxyethyl carbonate, cumylperoxymethacryloyloxyethoxyethyl carbonate, p-isopropylperoxymethacryloyloxyethoxyethyl carbonate, t-butylperoxyacryloyloxyisopropyl carbonate, t-amylperoxymacryloyloxyisopropyl carbonate, t-hexylperoxyacryloyloxyisopropyl carbonate, 1,1,3,3-tetramethylbutylperoxyacryloyloxyisopropyl carbonate, cumylperoxyacryloyloxyisopropyl carbonate, p-isopropylperoxyacryloyloxyisopropyl carbonate, t-butylperoxymethacryloyloxyisopropyl carbonate, t-amylperoxymethacryloyloxyisopropyl carbonate, t-hexylperoxymethacryloyloxyisopropyl carbonate, 1,1,3,3-tetramethylbutylperoxymethacryloyloxyisopropyl carbonate, cumylperoxymethacryloyloxyisopropyl carbonate, p-isopropylperoxymethacryloyloxyisopropyl carbonate. Typical examples of the compounds represented by the general formula (b) include t-butylperoxyallyl carbonate, t-amylperoxyallyl carbonate, t-hexylperoxyallyl carbonate, 1,1,3,3-tetramethylbutylperoxyallyl carbonate, p-menthaneperoxyallyl carbonate, cumylperoxyallyl carbonate, t-butylperoxymethallyl carbonate, t-amylperoxymethallyl carbonate, t-hexylperoxymethallyl carbonate, 1,1,3,3-tetramethylbutylperoxymethallyl carbonate, p-menthaneperoxymethallyl carbonate, cumylperoxymethallyl carbonate, t-butylperoxyallyloxyethyl carbonate, t-amylperoxyallyloxyethyl carbonate, t-butylperoxymethallyloxyethyl carbonate, t-amylperoxymethallyloxyethyl carbonate, t-hexylperoxymethallyloxyethyl carbonate, t-butylperoxyallyloxyisopropyl carbonate, t-amylperoxyallyloxyisopropyl carbonate, t-hexylperoxyallyloxyisopropyl carbonate, t-butylperoxymethallyloxyisopropyl carbonate, t-hexylperoxymethallyloxyisopropyl carbonate. Of these compounds, preferable ones are t-butylperoxyacryloyloxyethyl carbonate, t-butylperoxymethacryloyloxyethyl carbonate, t-butylperoxyallyl carbonate and t-butylperoxymethallyl carbonate. In the present invention, amounts of the above-mentioned resins (I) and (II) depend upon the purpose of the composition of the present invention. That is, when it is aimed that features of the polypropylene (I) are retained and poor stiffness, heat resistance and dimensional stability which are drawbacks of the polypropylene (I) are improved, there are required 50 to 99% by weight, preferably 60 to 95% by weight, of the polypropylene. When the polypropylene is less than 50% by weight, excellent moldability and chemical resistance which are features of the polypropylene are impaired. When it is in excess of 99% by weight, the improvement effect of stiffness, heat resistance and dimensional stability which is one of the purposes of the present invention is not obtained. On the other hand, if it is intended that physical properties are improved by the polypropylene, maintaining features of the resin (II), the content of the resin (II) is suitably from 50 to 99% by weight. That is, if it is aimed that low notched impact strength which is the drawback of the aromatic polyester resin is improved, maintaining features thereof, it is necessary that the content of the aromatic polyester resin is from 50 to 99% by weight, preferably from 60 to 95% by weight. When the content of the aromatic polyester resin is less than 50% by weight, stiffness and dimensional stability which are features of the aromatic polyester resin are impaired. If it is aimed that chemical resistance and moldability are improved, retaining features of the polycarbonate, there are required 50 to 99% by weight, preferably 60 to 95% by weight, of the polycarbonate. When the amount of the polycarbonate is less than 50% by weight, excellent impact resistance and stiffness which are the features of the polycarbonate is impaired, and when it is in excess of 99% by weight, the improvement effect of chemical resistance and moldability which is one of the purposes of the present invention is not obtained. If it is aimed that features of the polyphenylene ether are retained and the poor moldability and chemical resistance which are drawbacks of the polyphenylene ether are improved, there are required 50 to 99% by weight, preferably 60 to 95% by weight, of the polyphenylene ether. When the amount of the polyphenylene ether is less than 50% by weight, heat resistance and dimensional stability of the polyphenylene ether are impaired, and when it is in excess of 99% by weight, the improvement effect of moldability and chemical resistance which is one of the purposes of the present invention is not obtained. When it is aimed that poor hygroscopicity and dimensional stability of the polyamide resin are improved, retaining features thereof, 50 to 99% by weight, preferably 60 to 95% by weight of the polyamide resin are necessary. When the polyamide resin is less than 50% by weight, the features of the polyamide resin are impaired, and when it is in excess of 99% by weight, the improvement effect of hygroscopicity and dimensional stability thereof which is one of the purposes of the present invention cannot be expected. If it is intended that chemical resistance of the ABS resin is improved, retaining features thereof, 50 to 99% by weight, preferably 60 to 95% by weight of the ABS resin are necessary. When the content of the ABS resin is less than 50% by weight, the features of the ABS resin are impaired, and when it is in excess of 99% by weight, the improvement effect of the chemical resistance cannot be expected. In the present invention, the multi-phase structure thermoplastic resin is used in an amount of 0.1 to 100 parts by weight, preferably 1 to 50 parts by weight, based on 100 parts by weight of the total weight of the resins (I) + (II). When the amount of the multi-phase structure thermoplastic resin is less than 0.1 part by weight, any compatibility effect is not present, impact strength deteriorates, and delamination occurs on molded articles, with the result that the appearance of the articles is degraded. When it is in excess of 100 parts by weight, stiffness and heat resistance of the composition of the present invention deteriorate unpreferably. In the present invention, the inorganic filler (IV) can be used in an amount of 1 to 150 parts by weight based on 100 parts of the components (I) + (II) + (III). The inorganic filler may be used in granular, lamellar, scaly, needle, spherical, balloon and fibrous forms, and examples of these inorganic fillers include granular fillers such as calcium sulfate, calcium silicate, clay, diatomaceous earth, talc, alumina, siliceous sand, glass powder, iron oxide, metallic powder, graphite, silicon carbide, silicon nitride, silica, boron nitride, aluminum nitride and carbon black; lamellar and scaly fillers such as mica, glass plate, sericite, pyrophyllite, metallic foil, for example, aluminum flake, and graphite; balloon fillers such as Shirasu balloon, metallic balloon, glass balloon and pumice; and mineral fibers such as glass fiber, carbon fiber, graphite fiber, whisker, metallic fiber, silicon carbide fiber, asbestos and wollastonite. When the content of the filler is in excess of 150 parts by weight, the impact strength of molded articles deteriorates unpreferably. Inversely, when it is less than 1 part by weight, any modification effect cannot be exerted. The surface of the inorganic filler is preferably treated by the use of stearic acid, oleic acid, palmitic acid or a metallic salt thereof, paraffin wax, polyethylene wax or a modified material thereof, an organic silane, an organic borane or an organic titanate. Furthermore, in the present invention, the thermoplastic resin composition can be brought into a flame resistant state by blending therewith a flame retardant (V) in an amount of 5 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I) + (II) + (III). As the flame retardants, there can be used organic flame retardants of halogen series and phosphorus series, and inorganic flame retardants. The halogen series flame retardants include brominated and chlorinated paraffins such as tetrabromobisphenol (TBA), hexabromobenzene, decabromodiphenyl ether, tetrabromoethane (TBE), tetrabromobutane (TBB) and hexabromocyclodecane (HBCD), chlorine series flame retardants such as chlorinated paraffin, chlorinated polyphenyl, chlorinated polyethylene, chlorinated diphenyl, perchloropentacyclodecane and chlorinated naphthalene, usual halogen series flame retardants such as halogenated diphenyl sulfides, halogenated polystyrenes such as brominated polystyrene, brominated poly-α-methylstyrene and derivatives thereof, halogenated polycarbonates such as brominated polycarbonates, halogenated polyesters such as polyalkylene tetrabromoterephthalate and brominated terephthalic acid series polyesters, halogenated epoxy compounds such as halogenated bisphenol series epoxy resins, halogenated polyphenylene oxide compounds such as poly(dibromophenylene oxide), and high-molecular type halogen-containing polymers such as cyanuric acid ester compounds of halogenated bisphenols. Of these flame retardants, oligomers and polymers of the aromatic halides are particularly preferred. In addition, phosphorus series flame retardants include phosphates and halogenated phosphates such as tricresyl phosphate, tri(β-chloroethyl) phosphate, tri(dibromopropyl) phosphate and 2,3-dibromopropyl-2,3-chloropropyl phosphate, phosphonic acid compounds and phosphonic acid derivatives. Examples of other flame retardants include guanidine compounds such as guanidine nitride. The above-mentioned organic flame retardants may be used alone or as a mixture of two or more thereof. The organic flame retardant is used in an amount of 5 to 50 parts by weight, preferably 7 to 40 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I) + (II) + (III). When the content of the flame retardant is less than 5 parts by weight, a flame-resistive effect is poor, and when it is more than 50 parts by weight, the flame-resistive effect is not improved any more and cost rises unpreferably. These organic flame retardants, particularly halogen series flame retardants can exert a synergistic effect, when used together with a flame-resistive auxiliary. Examples of the flame-resistive auxiliary include antiomony halides such as antimony trioxide, antimony pentaoxide, antimony trichloride and antimony pentaoxide, and antimony compounds such as antimony trisulfide, antimony pentasulfide, sodium antimonate, antimony tartrate and metallic antimony. In addition, examples of the inorganic flame retardants used in the present invention include aluminum hydroxide, magnesium hydroxide, zirconium hydroxide, basic magnesium carbonate, dolonite, hydrotalcite, calcium hydroxide, barium hydroxide, hydrate of stannous hydroxide, hydrates of inorganic metallic compounds of borax and the like, zinc borate, zinc metaborate, barium metaborate, zinc carbonate, magnesium-calcium carbonate, calcium carbonate, barium carbonate, magnesium oxide, molybdenum oxide, zirconium oxide, stannous oxide and red phosphorus. These inorganic flame retardants may be used alone or as a mixture of two or more thereof. Of these flame retardants, hydrates of metallic compounds of aluminum hydroxide, magnesium hydroxide, zirconium hydroxide, basic magnesium carbonate, dolonite, hydrotalcite are particularly preferable. Above all, aluminum hydroxide and magnesium hydroxide are effective as the flame retardants and are economically advantageous. The particle diameter of the inorganic flame retardant depends upon its kind, but in the cases of aluminum hydroxide and magnesium hydroxide, the average particle diameter is 20 µm or less, preferably 10 µm or less. The inorganic flame retardant is used in an amount of 30 to 150 parts by weight, preferably 40 to 120 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I) + (II) + (III). When the content of the inorganic flame retardant is less than 30 parts by weight, a flame-resistive effect is poor in its single use, and thus it is necessary to add the organic flame retardant thereto. Inversely, when it is more than 150 parts by weight, impact strength and mechanical strength deteriorate. In the present invention, the above-mentioned inorganic filler and flame retardant may be employed simultaneously, whereby the content of the flame retardant can be decreased, and other characteristics can be acquired additionally. In the preparation of the thermoplastic composition of the present invention, melting and mixing are carried out at a temperature of 150 to 350°C, preferably 180 to 320°C. When the above temperature is less than 150°C, the melting is insufficient, melting viscosity is high, the mixing is poor, and the resin tends to peel off in a layer state unpreferably. Inversely when it is in excess of 350°C, decomposition and gelation of the resin take place inconveniently. In melting and mixing, there may be used a usual kneader such as a Banbury mixer, a pressure kneader, a kneading extruder, a biaxial extruder and mixing rolls. In the present invention, the following materials can be additionally used, in so far as they do not deviate from the gist of the present invention. Examples of such materials include resins such as polyolefin resins, polyvinyl chloride resin, polyvinylidene chloride resin, polyphenylene sulfide resin, polysulfone resin; rubbers such as a natural rubber and a synthetic rubber; and additives such as an antioxidant, an ultraviolet inhibitor, a lubricant, a dispersant, a foaming agent, a crosslinking agent and a colorant. Now, the present invention will be described in detail in reference to examples. Preparation Example 1 (Preparation of Multi-phase Structure Thermoplastic Resin IIIa) In a 5-liter stainless steel autoclave were placed 2,500 g of pure water, and 2.5 g of polyvinyl alcohol were further dissolved therein as a suspending agent. In the solution were placed 700 g of a polypropylene (trade name Nisseki Polypro J130G; made by Nippon Petrochemicals Co., Ltd.), followed by stirring to suspend the polypropylene therein. Separately, in 300 g of styrene as a vinyl monomer were dissolved 1.5 g of benzoylperoxide as a radical polymerization initiator (trade name Nyper-B; made by Nippon Oils & Fats Co., Ltd.) and 6 g of t-butylperoxymethacryloyloxyethyl carbonate as a radical polymerizable or copolymerizable organic peroxide, and the resulting solution was then placed in the above-mentioned autoclave, followed by stirring. Afterward, the autoclave was heated up to a temperature of 60 to 65°C, and stirring was then continued for 2 hours, so that the polypropylene was impregnated with the vinyl monomer containing the radical polymerization initiator and the radical polymerizable or copolymerizable organic peroxide. After it had been confirmed that the total amount of the impregnated vinyl monomer, radical polymerizable or copolymerizable organic peroxide and radical polymerization initiator was 50% by weight or more of the original total weight thereof, the temperature of the mixture was raised up to a level of 80 to 85°C, and this temperature was then maintained for 7 hours to complete polymerization, followed by water washing and drying, thereby obtaining a graft polymerization precursor IIIa'. Next, this graft polymerization precursor was extruded at 240°C by a plastomill monoaxial extruder (Toyo Seiki Seisaku-sho Ltd.) to perform graft reaction, whereby a multi-phase structure thermoplastic resin IIIa was obtained. This multi-phase structure thermoplastic resin (PP-g-PSt) was then observed by a scanning type electron microscope (trade name JEOL JSM T300; made by JEOL, Ltd.), and it was found that it was a multi-phase structure thermoplastic resin in which spherical resin particles each having a diameter of 0.3 to 0.4 µm were uniformly dispersed, as shown in Photograph No. 1. In this case, the graft efficiency of the styrene polymer was 77.1% by weight. Preparation Example 2 (Preparation of Multi-phase Structure Thermoplastic Resin IIIb) The same procedure as in Preparation Example 1 was repeated with the exception that 300 g of styrene as the monomer was replaced with 210 g of styrene and 90 g of acrylonitrile as monomers was used, thereby preparing a graft polymerization precursor IIIb'. According to the iodometry process, the active oxygen amount of this precursor was 0.13% by weight. Furthermore, when this precursor was extracted with xylene by the use of a Soxhlet extractor, any xylene-insoluble substance was not present. This precursor was then kneaded at 180°C at 50 rpm for 10 minutes by the use of a plastomill monoaxial extruder as in Preparation Example 1 in order to perform graft reaction. A copolymer which had not been grafted was then extracted from the resulting reaction product with ethyl acetate by the Soxhlet extractor, and the graft efficiency was measured. The graft efficiency of the styrene-acrylonitrile copolymer was 51% by weight. Moreover, extraction was then made with xylene, it was found that the amount of insoluble substances was 12.6% by weight. Preparation Example 3 (Preparation of Multi-phase Structure Thermoplastic Resin IIIc) The procedure of Preparation Example 1 was repeated with the exception that the polypropylene (trade name Nisseki Polypro J130G; made by Nippon Petrochemicals Co., Ltd.) was replaced with an ethylene-glycidyl methacrylate copolymer (content of glycidyl methacrylate = 15% by weight) (trade name Rexpearl J-3700; Nippon Petrochemicals Co., Ltd.) as an epoxy group-containing ethylene copolymer, in order to obtain a graft polymerization precursor IIIc'. A styrene polymer was then extracted from this graft polymerization precursor with ethyl acetate, and according to GPC, the number average polymerization degree of the styrene polymer was 900. Next, this graft polymerization precursor was extruded at 200°C as in Preparation Example 1, to perform graft reaction, whereby a multi-phase structure thermoplastic resin IIIc was obtained. This multi-phase structure thermoplastic resin (EGMA-g-PSt) was then observed, and it was found that it had a multi-phase structure in which spherical resin particles each having a diameter of 0.3 to 0.4 µm were uniformly dispersed, as shown in Photograph No. 2. In this case, the graft efficiency of the styrene polymer was 49.0% by weight. Preparation Example 4 (Preparation of Multi-phase Structure Thermoplastic Resin IIId) The same procedure as in Preparation Example 1 was repeated with the exception that the ethylene-glycidyl methacrylate copolymer as the epoxy group-containing ethylene copolymer was replaced with an ethylene-ethyl acrylate copolymer (content of ethyl acrylate = 20% by weight) (trade name Rexlon EEA A-4200; made by Nippon Petrochemicals Co., Ltd.), in order to obtain a multi-phase structure thermoplastic resin IIId. In this case, the number average polymerization degree of the styrene polymer was 900, and the average grain diameter was from 0.3 to 0.4 µm. Reference Example 1 (Preparation of Blend) In a 5-liter reaction tank equipped with a cooling pipe and a thermometer were placed 3 kg of water in which 6 g of a partially saponified polyvinyl alcohol were dissolved, and it was then stirred and heated up to 80°C. Styrene in which 5 g of benzoyl peroxide were dissolved was added thereto, and polymerizaion was performed for 7 hours. After the polymerization, the resulting polymer was filtered, washed and dried to obtain 950 g of polystyrene. The latter was then mixed with a polypropylene homopolymer (trade name Nisseki Polypro J130G; made by Nippon Petrochemicals Co., Ltd.) under melting. The mixing ratio of polypropylene:polystyrene was 70 parts by weight:30 parts by weight. This melting/mixing process was carried out at 230°C at a screw revolution speed of 100 rpm by the use of an extruder having a screw diameter of 20 mm and L/D = 24 (trade name Labo Plastomill; made by Toyo Seiki Seisaku-sho Ltd.). The resulting composition was observed through an electron microscope, and the results are shown in Photograph No. 3. In this photograph, particles of the polystyrene are not observed, and fine fibrous peeled layers are seen, which indicates that mixing is not made sufficiently. Examples 1 to 8 A polypropylene homopolymer (trade name Nisseki Polypro J130G; made by Nippon Petrochemicals Co., Ltd.) of MFR 4.0, polybutylene terephthalate (which is represented with PBT in tables given hereinafter) having an intrinsic viscosity of 3.5 dl/g as an aromatic polyester, and multi-phase structure thermoplastic resins IIIa, IIIc and IIId were mixed in ratios shown in Table 1. The melting/mixing process was carried out by feeding the respective materials into a one-directional twin-screw extruder (made by Plastic Engineering Institute) and then mixing them under melting in a cylinder thereof. The mixed resin was then formed into granules, and the latter were then dried at 150°C for 3 hours, followed by injection molding in order to prepare specimens. Sizes of the specimens and standard tests were as follows: Specimens for notched izod impact strength 13 x 65 x 6 mm (JIS K7110) Specimens for heat distortion temperature 13 x 130 x 6 mm (JIS K7207) Specimens for flexural strength 10 x 130 x 4 mm (JIS K7203) State of Delamination: The state of delamination was ranked as follows by visually observing the state of the brokn surface of each molded article. O : Delamination was not present at all. ▵ : Delamination was slightly present. X : Delamination was perceptibly present. Example 1 2 3 4 5 6 7 8 Polypropylene (wt%) 90 80 70 70 40 30 30 10 PBT (wt%) 10 20 30 30 60 70 70 90 Multi-Phase Structure Themoplastic Resin IIIa 10 10 10 10 10 5 5 5 Multi-Phase Structure Themoplastic Resin IIIc 5 5 8 - 15 - 15 20 Multi-Phase Structure Themoplastic Resin IIId - - - 10 - 20 - - Notched Izod Impact Strength (kg·cm/cm) 8 10 14 12 18 20 23 21 Heat Distortion Temperature (°C) (18.6 kg/cm²) 68 70 69 70 67 70 70 69 Flexural Strength (kg/cm²) 420 450 490 470 620 650 630 680 State of Delamination O O O O O O O O Examples 9 to 15 The same procedure as in the above-mentioned examples was repeated with the exception that the multi-phase structure thermoplastic resin (IIIa) and (IIIc) were replaced with graft polymerization precursors (IIIa′), (IIIc′) and (IIId′) obtained in Preparation Examples 1, 3 and 4, and the results are set forth in Table 2. Examples 16 to 24 In these examples, a glass fiber as an inorganic filler was blended in which an average fiber length was 5.0 mm and a fiber diameter was 10 µm. The results are set forth in Table 3. Examples 25 to 30 The same procedure as in Examples 16 and 22 was repeated with the exception that flame retardants and auxiliaries were used, in order to prepare combustion specimens of the dimension 6.35 mm x 12.7 mm x 127 mm (1/4" x 1/2" x 5") having compositions shown in Table 4, and vertical flame tests were then carried out in accordance with UL-94 standard. Comparative Examples 1 to 5 The procedure of the above-mentioned examples was repeated with the exception that the blends obtained in Reference Example 2, the ethylene-glycidyl methacrylate copolymer used in Preparation Example 3 and a modified polypropylene (amount of added maleic acid = 0.15% by weight) were employed. The results are set forth in Table 5. Comp. Example 1 2 3 4 5 Polypropylene (wt%) 40 40 40 40 40 PBT (wt%) 60 60 60 60 60 Blend 10 - - - - Ethylene-Glycidyl Methacrylate Copolymer - 5 10 - 10 Modified Polypropylene - - - 25 25 Notched Izod Impact strength (kg·cm/cm) 2 5 7 6 8 Heat Distortion Temperature (°C) (18.6 kg/cm²) 49 58 56 54 53 Flexural Strength (kg/cm²) 500 620 500 510 480 State of Delamination X X X X O Examples 31 to 36 The procedure of Example 1 was repeated with the exception that the polybutylene terephthalate and multi-phase structure thermoplastic resin (IIIa) used therein were replaced with a polycarbonate resin having a number average molecular weight of 62,000 and the multi-phase structure thermoplastic resin (IIIb) obtained in Preparation Example 2, and melting/mixing was made in ratios shown in Table 6. Chemical resistance was then evaluated by immersing each specimen into methanol at 75°C for 30 days, then drying it at room temperature, measuring the deterioration ratio of tensile strength, and observing the appearance of the specimen. O : The specimen was not changed. X : Cracks and dissolution took place on the surface of the specimen. Example 31 32 33 34 35 36 Polypropylene (wt%) 25 25 50 50 80 80 Polycarbonate (wt%) 75 75 50 50 20 20 Multi-phase Structure Thermoplastic Resin (IIIb) 10 20 10 20 10 20 Notched Izod Impact Strength (kg·cm/cm) 72 80 62 65 45 51 Heat Distortion Temperature (°C) (18.6 kg/cm²) 127 125 120 117 120 120 Chemical Resistance Appearance O O O O O O Deterioration Ratio of Tensile Strength (%) 10 8 5 5 3 2 Examples 37 to 40 The procedure of the above-mentioned examples was repeated with the exception that the multi-phase structure thermoplastic resin (IIIb) used therein was replaced with a graft polymerization precursor (IIIb′). The results are set forth in Table 7. Functional effects in these cases are similar to those in cases of the grafted multi-phase structure thermoplastic resins. Example 37 38 39 40 Polypropylene (wt%) 25 25 50 80 Polycarbonate (wt%) 75 75 50 20 Graft Polymerization Precursor (IIIb') 10 20 20 20 Notched Izod Impact Strength (kg·cm/cm) 70 83 63 55 Heat Distortion Temperature (°C) (18.6 kg/cm²) 130 127 115 123 Chemical Resistance Appearance O O O O Deterioration Ratio of Tensile Strength (%) 11 10 6 3 Examples 41 to 44 In the above-mentioned examples, a glass fiber having an average fiber length of 3.0 mm and a diameter of 10 µm was additionally blended. The results are set forth in Table 8. Example 41 42 43 44 Polypropylene (wt%) 25 25 50 80 Polycarbonate (wt%) 75 75 50 20 Multi-phase Structure Thermoplastic Resin (IIIb) 15 25 20 20 Glass Fiber 30 30 30 30 Notched Izod Impact Strength (kg·cm/cm) 95 88 80 59 Heat Distortion Temperature (°C) (18.6 kg/cm²) 145 140 137 125 Examples 45 to 52 The procedure of Example 1 was repeated with the exception that the polybutylene terephthalate was replaced with 6,6-nylon (trade mame Amilan CM3001-N; made by Toray Industries, Inc.), and melting/mixing was made in ratios shown in Table 9. Afterward, physical properties were measured. Hygroscopicity was evaluated by immersing each specimen into water at 23°C for 24 hours, then allowing it to stand at 23°C at a relative humidity of 65%, and making a caluculation on the basis of a weight increment ratio. Furthermore, coating adhesive properties were evaluated by coating each specimen with an acrylic coating material, applying a cellophane adhesive tape on the surface of the coating material, tearing away it therefrom, and observing the state of the surface. O : The coating film was not delaminated at all. ▵ : The coating film was partially delaminated. X : The coating film was substantially all delaminated. Example 45 46 47 48 49 50 51 52 Polypropylene (wt%) 80 80 60 60 50 30 30 20 6,6-Nylon (wt%) 20 20 40 40 50 70 70 80 Multi-phase Structure Thermoplastic Resin (IIIa) 10 5 10 10 10 5 5 5 Multi-phase Structure Thermoplastic Resin (IIIc) 10 15 10 - 10 15 - 20 Multi-phase Structure Thermoplastic Resin (IIId) - - - 10 - - 15 - Notched Izod Impact Strength (kg·cm/cm) 18 16 19 17 20 20 22 25 Heat Distortion Temperature (°C) (18.6 kg/cm²) 70 70 75 77 80 83 81 90 Coating Adhesive Properties O O O O O O O O Hygroscopicity (%) 2.5 2.5 4.0 3.8 4.5 6.2 6.6 6.5 Examples 53 to 58 In the above-mentioned examples, a glass fiber having an average fiber length of 7.0 mm and a diameter of 10 µm was additionally blended. The results are set forth in Table 10. Example 53 54 55 56 57 58 Polypropylene (wt%) 80 60 60 50 30 20 6,6-Nylon (wt%) 20 40 40 50 70 80 Multi-phase Structure Thermoplastic Resin (IIIa) 10 10 10 10 5 5 Multi-phase Structure Thermoplastic Resin (IIIc) 10 10 - 10 - 20 Multi-phase Structure Thermoplastic Resin (IIId) - - 10 - 15 - Glass Fiber 35 35 35 35 35 35 Notched Izod Impact Strength (kg·cm/cm) 50 47 42 44 42 40 Heat Distortion Temperature (°C) (18.6 kg/cm²) 128 135 143 140 155 165 Examples 59 to 65 In examples 59 to 65 the components used in example 53 (examples 59, 60, 62, 63 and 65) and example 55 (examples 61 and 64) were additionally blended with the same flame-retardents and auxiliaries as used in example 25 (examples 59 to 62 and 64) and example 30 (examples 63 and 65), respectively, and a flame-test was then carried out. The procedure of the test was the same as in example 25. The results are set forth in table 11. Example 59 60 61 62 63 64 65 Polypropylene (wt%) 80 80 80 80 80 20 20 6,6-Nylon (wt%) 20 20 20 20 20 80 80 Multi-phase Structure Thermoplastic Resin (IIIa) 10 10 10 10 10 5 5 Multi-phase Structure Thermoplastic Resin (IIIc) 10 10 - 10 10 - 20 Multi-phase Structure Thermoplastic Resin (IIId) - - 10 - - 20 - Glass Fiber 35 35 35 35 35 35 35 Brominated Polystyrene 5 10 10 25 - 20 - Magnesium Hydroxide - - - - 100 - 100 Antimony Trioxide 2 5 5 10 - 10 - UL-94 Flame Properties V-0 V-0 V-0 V-0 V-2 V-0 V-2 Comparative Examples 6 to 11 The procedure of Example 43 was repeated with the exception that the multi-phase structure thermoplastic resin was replaced with a blend and a modified polypropylene, as in Comparative Examples 1 to 5. The results are set forth in Table 12. Comp. Example 6 7 8 9 10 11 Polypropylene (wt%) 80 80 80 50 40 30 6,6-Nylon (wt%) 20 20 20 50 60 70 Blend - 10 - - - - Modified Polypropylene - - 25 20 20 20 Notched Izod Impact Strength (kg·cm/cm) 5 6 12 14 15 20 Heat Distortion Temperature (°C) (18.6 kg/cm²) 60 62 67 77 77 79 Coating Adhesive Properties X X ▵ O O O Hygroscopicity (%) 3.0 3.1 2.7 4.8 5.3 6.6 Examples 66 to 73 The procedure of Example 1 was repeated with the exception that the polybutylene terephthalate was replaced with poly-2,6-dimethyl-1,4-phenylene ether (which is represented by PPE in tables), a modified PPE (trade name Nolyl 534J; made by Engineering Plastics Co., Ltd.) and the multi-phase structure thermoplastic resin (IIIa) obtained in Preparation Example 1. The results are set forth in Table 13. Chemical resistance was evaluated by immersing each specimen into gasoline for 1.5 hours, and then observing its appearance. O : The specimen was not changed at all. ▵ : The specimen was partially dissolved on its surface. X : The specimen was remarkably dissolved on its surface. Example 66 67 68 69 70 71 72 73 Polypropylene (wt%) 30 30 50 50 80 80 30 80 PPE (wt%) 70 70 50 50 20 20 - - Modified PPE (wt%) - - - - - - 70 20 Multi-phase Structure Thermoplastic Resin (IIIa) 10 20 10 20 10 20 20 20 Notched Izod Impact Strength (kg·cm/cm) 22 32 25 30 15 20 28 18 Heat Distortion Temperature (°C) (18.6 kg/cm²) 127 125 120 117 120 120 129 122 Chemical Resistance O O O O O O O O Examples 74 to 80 The procedure of the above-mentioned examples was repeated with the exception that the multi-phase structure thermoplastic resin used therein was replaced with a graft polymerization precursor, and physical properties were then measured. The results are set forth in Table 14. Example 74 75 76 77 78 79 80 Polypropylene (wt%) 30 30 50 20 20 30 20 PPE (wt%) 70 70 50 80 80 70 - Modified PPE (wt%) - - - - - - 80 Graft Polymerization Precursor (IIIa') 10 20 20 10 20 20 20 Notched Izod Impact Strength (kg·cm/cm) 20 33 45 55 61 26 58 Heat Distortion Temperature (°C) (18.6 kg/cm²) 130 127 115 113 110 130 114 Chemical Resistance O O O O O O O Examples 81 to 87 In the above-mentioned examples, a glass fiber having an average fiber length of 5.0 mm and a diameter of 10 µm was additionally blended. The results are set forth in Table 15. Example 81 82 83 84 85 86 87 Polypropylene (wt%) 25 25 25 50 80 25 80 PPE (wt%) 75 75 75 50 20 - - Modified PPE (wt%) - - - - - 75 20 Multi-phase Structure Thermoplastic Resin (IIIa) 15 25 - 20 20 20 20 Graft Polymerization Precursor (IIIa') - - 25 - - - - Glass Fiber 30 30 30 30 30 30 30 Notched Izod Impact Strength (kg·cm/cm) 42 50 52 45 35 39 28 Heat Distortion Temperature (°C) (18.6 kg/cm²) 147 140 135 137 125 135 129 Comparative Examples 12 to 18 The procedure of the above-mentined examples was repeated with the exception that the blend obtained in Reference Example 1, ethylene-glycidyl methacrylate copolymer and a modified polypropylene (which was obtained by the addition reaction of 0.1% by weight of maleic anhydride to a polypropylene). The results are set forth in Table 16. Comp. Example 12 13 14 15 16 17 18 Polypropylene (wt%) 30 30 50 50 75 30 30 PPE (wt%) 70 70 50 50 25 70 70 Blend - - - - - 15 - Ethylene-Glycidyl Methacrylate Copolymer 10 15 - - - - - Modified Polypropylene - - - - - - 15 Notched Izod Impact Strength (kg·cm/cm) 9 5 11 7 4 2 4 Heat Distortion Temperature (°C) (18.6 kg/cm²) 117 110 95 98 91 88 91 Chemical Resistance ▵ X ▵-X X ▵-X X ▵-X Examples 88 to 95 A polypropylene homopolymer (trade name Nisseki Polypro J130G; made by Nippon Petrochemicals Co., Ltd.) of MFR 4.0, an ABS resin of Table 17 and the multi-phase structure thermoplastic resin (IIIb) obtained in Preparation Example 2 were mixed under melting in a ratio shown in Table 18. The procedure of the melting/mixing process and the measurement manner of mechanical properties were the same as in Example 1. Coating adhesive properties were evaluated by coating each specimen with an acrylic coating material, applying a cellophane adhesive tape on the surface of the coating material, tearing away it therefrom, and observing the state of the surface. The coating adhesive properties were ranked as follows: O : The coating film was not delaminated at all. ▵ : The coating film was partially delaminated. X : The coating film was substantially all delaminated. Furthermore, chemical resistance was evaluated by immersing each specimen into acetone for 1 hour, then drying it at room temperature, measuring the deterioration ratio of tensile strength, and observing the appearance of the specimen. O : The specimen was not changed at all. ▵ : The specimen was partially dissolved on its surface. X : The specimen was remarkably dissolved on its surface. Composition Sample ABS Resin [1] ABS Resin [2] Acrylonitrile (wt%) 20 25 Styrene (wt%) 55 15 α-Methylstyrene (wt) 0 40 Polybutadiene (wt%) 25 20 Intrinsic Viscosity 0.60 0.65 Example 88 89 90 91 92 93 94 95 Polypropylene (wt%) 25 25 25 50 50 50 80 80 ABS Resin [1] (wt %) 75 75 - 50 50 - 20 - ABS Resin [2] (wt %) - - 75 - - 50 - 20 Multi-phase Structure Thermoplastic Resin (IIIb) 20 10 20 20 10 20 20 20 Notched Izod Impact Strength (kg·cm/cm) 35 27 26 23 20 20 20 17 Heat Distortion Temperature (°C) (18.6 kg/cm²) 75 78 75 73 73 75 81 80 Coating Adhesive Properties O O O O O O O O Chemical Resistance Appearance O O O O O O O O Deterioration Ratio of Tensile Strength (%) 7 8 7 5 5 5 3 2 Examples 96 to 102 The procedure of the above-mentioned examples was repeated with the exception that the grafted multi-phase structure thermoplastic resin was replaced with the graft polymerization precursor obtained in Preparation Example 2, and that a glass fiber having an average fiber length of 5.0 mm and a diameter of 10 µm was additionally blended. The results are set forth in Table 19. Example 96 97 98 99 100 101 102 Polypropylene (wt%) 25 50 50 80 80 80 25 ABS Resin [1] (wt%) 75 50 - 20 - - 75 ABS Resin [2] (wt%) - - 50 - 20 20 - Multi-phase Structure Thermoplastic Resin (IIIb) - - - 20 20 - 20 Graft Polymerization Precursor (IIIb') 20 20 20 - - 20 - Glass Fiber - - - 20 20 20 20 Notched Izod Impact Strength (kg·cm/cm) 24 22 19 17 15 17 18 Heat Distortion Temperature (°C) (18.6 kg/cm²) 74 74 73 110 108 110 100 Coating Adhesive Properties O O O O O O O Chemical Resistance Appearance O O O O O O O Deterioration Ratio of Tensile Strength (%) 9 6 5 3 3 2 2 Examples 103 to 110 In Examples 100, 101 and 103, the same flame retardants and auxiliaries as used in Example 25 were additionally used, and a flame test was then carried out. The procedure of the test was the same as in Example 25. The results are set forth in Table 20. Example 103 104 105 106 107 108 109 110 Polypropylene (wt%) 80 80 80 80 80 25 25 25 ABS Resin [1] (wt%) 20 20 20 - - 75 75 75 ABS Resin [2] (wt%) - - - 20 20 - - - Multi-phase Structure Thermoplastic Resin (IIIb) 20 20 20 20 20 20 20 20 Glass Fiber 30 30 30 30 30 30 30 30 Brominated Polystyrene - 10 25 10 25 - - 10 Magnesium Hydroxide 100 - - - - 50 100 - Antimony Trioxide - 7 10 7 10 - - 10 UL-94 Flame Properties V-2 V-0 V-0 V-0 V-0 V-2 V-1 V-0 Comparative Examples 19 to 25 The procedure of Examples 88 to 90 was repeated with the exception that the multi-phase structure thermoplastic resin used therein was replaced with the blend obtained in Reference Example 1 and ethylene-vinyl acetate copolymer (content of vinyl acetate = 30% by weight). The results are set forth in Table 21. Comp. Example 19 20 21 22 23 24 25 Polypropylene (wt%) - - 25 25 25 25 25 ABS Resin [1] (wt%) 100 - 75 - 75 75 - ABS Resin [2] (wt%) - 100 - 75 - - 75 Blend - - - - - 20 20 Ethylene-Vinyl Acetate Copolymer - - 15 15 - - - Notched Izod Impact Strength (kg·cm/cm) 18 19 10 11 5 5 6 Heat Distortion Temperature (°C) (18.6 kg/cm²) 81 82 73 75 77 78 77 Coating Adhesive Properties O O Δ Δ Δ X X Chemical Resistance Appearance X X Δ Δ X X X Deterioration Ratio of Tensile Strength (%) 75 69 43 50 77 85 80 The thermoplastic resin composition of the present invention effectively has different features of raw material resins, and it is excellent in moldability, chemical resistance, impact resistance, heat resistance, coating properties, mechanical properties and appearance of molded articles made therefrom. Degrees of impact strength, heat resistance and mechanical properties can be regulated by suitably selecting a ratio of resins and a multi-phase structure thermoplastic resin which are mixed with one another, and therefore the present invention can meet a variety of demands. As is apparent from the foregoing, the thermoplastic resin composition of the present invention can be widely utilized as materials for, e.g., automobile parts, electrical and electronic machine parts, and other industrial parts.

Claims: A thermoplastic resin composition containing (I) 99 to 1% by weight of a polypropylene, (II) 1 to 99% by weight of at least one kind of resin selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer in an amount of 0 to 95% by weight of the polyphenylene ether resin and an ABS resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I) + (II), of a multi-phase structure thermoplastic resin which is a graft copolymer composed of 5 to 95% by weight of a polyolefin and 95 to 5% by weight of a vinyl polymer or copolymer obtained from at least one kind of vinyl monomer, either of the graft copolymer components being in the state of a dispersion phase having a particle diameter of 0.001 to 10 µm, and wherein the vinyl polymer or copolymer in the multi-phase structure thermoplastic resin has an average polymerization degree of 5 to 10,000. A thermoplastic resin composition according to Claim 1 wherein the polyolefin in the multi-phase structure thermoplastic resin is at least one selected from the group consisting of a propylene polymer and/or an epoxy group-containing ethylene copolymer, an ethylen-unsaturated carboxylic acid or its alkyl ester copolymer, or its metallic salt, and an ethylene-vinyl ester copolymer. A thermoplastic resin composition according to Claim 1 or 2, wherein the multi-phase structure thermoplastic resin (III) is a grafted compound prepared by melting and mixing the mixture which comprises 1 to 100% by weight of a graft polymerization precursor (A) obtained by copolymerizing at least one vinyl monomer with at least one of radical polymerizable or copolymerizable organic peroxides represented by the following general formulae (a) and (b) wherein R₁ is a hydrogen atom or an alkyl group having 1 or 2 carbon atoms, each of R₂ and R₇ is a hydrogen atom or a methyl group, R₆ is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, each of R₃, R₄, R₈ and R₉ is an alkyl group having 1 to 4 carbon atoms, each of R₅ and R₁₀ is an alkyl group having 1 to 12 carbon atoms, a phenyl group, an alkyl-substituted phenyl group or a cycloalkyl group having 3 to 12 carbon atoms, m is 1 or 2, and n is 0, 1 or 2, in particles of a polyolefin, 0 to 99% by weight of a polyolefin (B), and 0 to 99% by weight of a vinyl polymer or copolymer (C) obtained by polymerizing or copolymerizing at least one vinyl monomer. A thermoplastic resin composition according to any of the Claims 1 to 3, wherein the vinyl monomer is at least one vinyl monomer selected from the group consisting of vinyl aromatic monomers, acrylate and methacrylate monomers, acrylonitrile and methacrylonitrile monomers, and vinyl ester monomers. A thermoplastic resin composition according to any of the Claims 1 to 4, wherein the polyolefin is a copolymer composed of 60 to 99.5% by weight of ethylene, 40 to 0.5% by weight of glycidyl acrylate or methacrylate, and 0 to 39.5% by weight of another unsaturated monomer. A thermoplastic resin composition according to any of the Claims 1 to 4, wherein the polyolefin is a copolymer or its metallic salt which comprises 50 to 99.5% by weight of ethylene, 50 to 0.5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids, their alkyl esters and vinyl esters, and 0 to 49.5% by weight of another unsaturated monomer. A thermoplastic resin composition according to any of the Claims 1 to 6, wherein the vinyl polymer or copolymer exhibits a content of a vinyl aromatic monomer of 50% by weight or more. A thermoplastic resin composition according to any of the Claims 1 to 7, wherein an inorganic filler (IV) is additionally blended in an amount of 1 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I) + (II) + (III). A thermoplastic resin composition according to any of the Claims 1 to 8, wherein a flame retardant (V) is additionally blended in an amount of 5 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I) + (II) + (III). A method for preparing a thermoplastic resin composition which comprises the step of melting and mixing 99 to 1% by weight of a polypropylene (I) and 1 to 99% by weight of at least one kind of resin (II) selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer in an amount of 0 to 95% by weight of the polyphenylene ether resin and an ABS resin, with 1 to 100% by weight of a graft polymerization precursor (A) which is obtained by first adding at least one kind of vinyl monomer, at least one kind of radical polymerizable or copolymerizable organic peroxide and a radical polymerization initiator to an aqueous suspension of a polyolefin, then heating the suspension under such conditions that the decomposition of the radical polymerization initiator does not occur substantially, in order to impregnate the polyolefin with the vinyl monomer, the radical polymerizable or copolymerizable organic peroxide and the radical polymerization initiator, and raising the temperature of this aqueous suspension, when the degree of the impregnation has reached 50% by weight of the original total weight of the vinyl monomer, peroxide and initiator, in order to copolymerize the vinyl monomer with the radical polymerizable or copolymerizable organic peroxide in the polyolefin, 0 to 99% by weight of the polyolefin (B), and 0 to 99% by weight of a vinyl polymer or copolymer (C) obtained by polymerizing at least one kind of vinyl monomer, wherein said vinyl polymer or copolymer has an average polymerization degree of 5 to 10,000, or alternatively melting and mixing the components (A), (B) and (C) previously at a temperature in the range of 150 to 350°C in order to form a multi-phase structure thermoplastic resin (III), and then melting and mixing the resin (III) with the propylene (I) and at least one kind of resin (II) selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer and an ABS resin. A method for preparing a thermoplastic resin composition according to Claim 10 wherein the radical polymerizable or copolymerizable organic peroxide is one or a mixture of two or more of peroxycarbonate compounds represented by the following general formulae (a) and (b) wherein R₁ is a hydrogen atom or an alkyl group having 1 or 2 carbon atoms, each of R₂ and R₇ is a hydrogen atom or a methyl group, R₆ is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, each of R₃, R₄, R₈ and R₉ is an alkyl group having 1 to 4 carbon atoms, each of R₅ and R₁₀ is an alkyl group having 1 to 12 carbon atoms, a phenyl group, an alkyl-substituted phenyl group or a cycloalkyl group having 3 to 12 carbon atoms, m is 1 or 2, and n is 0, 1 or 2. A method according to claim 10 or 11, wherein a thermoplastic resin composition accordig to any one of the Claims 2, 3 or 5 to 10 is prepared. The use of a thermoplastic resin composition according to any of the Claims 1 to 9 for producing shaped parts.

Inventors: MAKI YOSHINORI, NISHIMURA SADAHIRO, ORIKASA YUICHI, SAKAZUME SUEHIRO, MAKI, YOSHINORI, NISHIMURA, SADAHIRO, ORIKASA, YUICHI, SAKAZUME, SUEHIRO
Applicants: NIPPON OILS & FATS CO LTD, NIPPON PETROCHEMICALS CO LTD, NIPPON OIL AND FATS COMPANY, LIMITED, NIPPON PETROCHEMICALS COMPANY, LIMITED
Application year: 1988
Main classification: C08L23
IPC codes: C08L55, C08F4, C08L101, C08L23, C08L69, C08L25, C08L77, C08L51, C08L67, C08K7, C08L71