ION EXCHANGER BASED ON CROSS-LINKED GLUCOMANNAN

Abstract: A novel ion-exchanger, particularly for ion-exchange chromatography, is obtained by introducing radicals of one or more ion-exchangeable groups into cross-linked glucomannan beads, by chemical treatment.

Description: Background of the Invention 1. Field of the Invention The present invention relates to a novel ion exchanger of spherical beads based on cross-linked konjakmannan, a type of glucomannan, and, more specifically, to an ion exchanger superior in the compressive strength permitting to use under high hydrodynamic shear stress, for general ion-exchange purposes and, in particular, for ion-exchange chromatography. 2. Description of the Prior Art As typical ion exchangers for ion-exchange chromatography, there are found in the market today DEAE-Sephadex A-50 (DEAE is an abridgement of diethylaminoethyl and is used below throughout the Specification), DEAE-Sepharose CL-6B, CM-Sephadex C-50 (CM is an abridgement of carboxymethyl) and CM-Sepharose CL-6B, all trademarks, of the firm Pharmacia Fine Chemicals. They are produced each under the use of a natural high molecular weight substance as the starting material and are used for separating high molecular weight substances, such as, proteins, polysaccharides, nucleic acids, membrane components and so on. These prior art ion exchangers have a disadvantage that each bead of the ion exchanger becomes, due to lower compressive strength, deformed upon ion exchange operation at high flow velocity whereby a considerable reduction in the separation efficiency is caused. A further increase in the flow velocity may cause a steep rise of the pressure loss in the exchanger column and may result even in a blockade of the column. In the case of using an ion exchanger for the separation of, such as, proteins, polysaccharides, nucleic acids, membrane components and other high molecular weight substances, it is necessary in general to provide for the subsequent adsoption step, namely ion exchange step, by removing all the substances combined by ionic bond. In general, it is conventional to remove contaminants, such as lipids and proteins, by washing with approx. 0.1 M aqueous NaOH, followed by a complete removal of the residual alkali by washing with distilled water or a buffer or salt solution. This procedure is long and laborious, compared to the ionic adsorption procedure, and constitutes a principal cause of the extended operation cycle comprising the steps of ionic adsorption, desorption (elution), water wash and regeneration. In practice, it is preferred to reduce the length of the washing and regeneration steps, rather than of the adsorption step. For this purpose, beads of ion-exchanger having higher compressive strength and permitting a high liquid flow rate are required. Japanese Laid-Open Patent Application No. 236839/1987 discloses the use of glucomannan beads, which have a cross-linked structure and exhibit a degree of swelling in the range from 1.5 to 15 (in terms of number of ml of wet gel bed per g of dry gel), an exclusion limit molecular weight of 100 to 10⁸ and an average bead size of 1 to 500 µm, in gel filtration and gel chromatography. The glucomannan beads do not, however, have ion-exchange capacity and, therefore, cannot be used for ion-exchange chromatography. CA-A-0960652 discloses ion-exchangers in bead form. The ion-exchange material is a polysaccharide such as starch or xylan, and it is stated that xylan can be replaced by glucomannan isolated from Douglas fir. Summary of the Invention An ion-exchanger according to the present invention comprises beads of cross-linked konjakmannan having radicals of one or more ion-exchangeable groups, and wherein the cross-linked konjakmannan has an exclusion limit molecular weight of 10⁵ to 10⁸. Description of the Invention The ion-exchangeable group in the ion-exchanger according to the present invention may be any known in the art for that purpose. Examples are diethylaminoethyl (DEAE), carboxymethyl (CM), sulfomethyl, primary to tertiary aminoethyls, quaternary ethylammonium, sulfopropyl and phosphate. The introduction of the ion-exchangeable group can be effected by conventional technique. For example, cross-linked konjakmannan beads are first soaked in a solution of an alkali and are then reacted with a reagent having a terminal halogen atom, forming a combined radical of an ion-exchangeable group. The reagent is, for example, 2-chlorotriethylamine hydrochloride, chloroacetic acid, a salt of chloromethanesulfonic acid, or phosphoryl chloride. The alkali is, for example, sodium hydroxide or potassium hydroxide. The ion-exchange capacity of the ion-exchanger according to the present invention is preferably 0.1 to 5 meq. per gram of dry beads. The cross-linked konjakmannan beads preferably have a degree of swelling of 1.5 to 15, more preferably 2 to 8, and an average bead diameter in the range from 5 to 500 µm. Konjakmannan is commercially-available. It is obtained from the plant Amorphonhalus konjak . The cross-linked konjakmannan beads are obtained from the konjakmannan by reaction with a cross-linking agent. The degree of swelling and the exclusion limit molecular weight of the spherical beads of cross-linked konjakmannan are preferably adjusted so that they exhibit a porous macrostructure. It is possible, alternatively or concurrently, to incorporate regulation of the degree of cross-linking, to control the degree of swelling and the exclusion limit molecular weight. The cross-linked konjakmannan beads can be obtained by dissolving an esterified product of konjakmannan alone or together with a diluent in a solvent, suspending the resulting solution in an aqueous medium (the solvent has a boiling point lower than the aqueous medium and is immiscible or only poorly miscible with this aqueous medium), to form liquid droplets of the esterified konjakmannan, evaporating off the solvent contained in the liquid droplets, saponifying the resulting spherical beads of the esterified konjakmannan, and reacting the saponified beads with a cross-linking agent. The spherical beads of cross-linked konjakmannan according to the present invention can be prepared, in more practical detail, as follows: A commercially-available konjakmannan may be used as such, as the starting material, or a refined product treated by dissolving a commercial product once in water and precipitating the konjakmannan from this aqueous solution by addition of a non-solvent such as ethyl alcohol or methyl alcohol. The konjakmannan is then swollen with a solvent such as formamide or dimethylformamide. An acid is added, to esterify the konjakmannan, using an esterification catalyst such as pyridine. The acid may be organic or inorganic, examples being acetic acid, acetic anhydride, propionic acid, butyric acid and nitric acid; one or more acids can be used, in order to obtain a mixed ester. When using an acid having free carboxyl group, water is formed upon reaction with the konjakmannan, which may cause the molecular chain of the konjakmannan to break down, so that it is preferred to provide a means for dewatering. In contrast thereto, an acid anhydride, such as acetic anhydride, does not form water of reaction, and is therefore advantageous. The esterification renders the konjakmannan insoluble in water, and gives suspended particles of konjakmannan. It is desirable to esterify most, preferably more than 85%, especially more than 90%, of the OH groups in the konjakmannan. The thus esterified konjakmannan is then purified using, for example, acetone. If the degree of esterification is less than 85%, the solubility of the konjakmannan in acetone is reduced, so that the degree of recovery is reduced. The esterified konjakmannan is thereafter precipitated by contacting it with water, and is then dried. The konjakmannan ester thus obtained is dissolved, alone or together with a diluent, in a solvent. The solvent should have a boiling point lower than the aqueous suspension medium, as will be explained below, and be immiscible or poorly miscible with the aqueous medium. The solvent is, for example, a chlorinated hydrocarbon such as dichloromethane, chloroform, carbon tetrachloride or trichloroethylene, or a mixture thereof. The concentration of the solution of konjakmannan ester prepared as above should be such that spherical beads will be formed after it is introduced into an aqueous medium, and the beads should possess sufficient strength, e.g. for use in ion-exchange chromotography, after the solvent has been removed by evaporation. The concentration is preferably 0.2 to 20%, more preferably from 0.5 to 5%, and most preferably from 0.5 to 2%, by weight. If the concentration of the konjakmannan ester is less than 0.2% by weight, a fine floc-like precipitate, but no beads will be formed. If it exceeds 20% by weight, the particle size is too large, and the particles exhibit a non-porous surface, which makes it impossible to employ the packed material in chromatography. In preparing the solution of the konjakmannan ester, it is possible to dissolve the ester alone in a solvent, but it is preferred to employ a diluent, for facilitating the adjustment of the degree of swelling and the exclusion limit molecular weight. Use and removal of a diluent leaves voids or pores, i.e. a porous macrostructure in the beads. The diluent should have a boiling point higher than that of the solvent, and should not dissolve the konjakmannan ester: examples include tetrahydronaphthalene, decahydronaphthalene, ethylbenzene, diethylbenzene, methyl dodecanoate, methyl caprinate, toluene, hexyl alcohol, heptyl alcohol and octyl alcohol. When the konjakmannan is swollen preliminarily with formamide, tetrahydronaphthalene and decahydronaphthalene are preferably chosen as the diluent. The amount of the diluent to be added may be chosen in accordance with the contemplated degree of swelling and with the desired exclusion limit molecular weight. For example, for preparing a gel product having a degree of swelling of 3 and an exclusion limit molecular weight of over 10⁶, the amount of diluent may be, as a rough measure, in the range of 100-1000%, preferably from 100 to 500%, based on the weight of the glucomannan ester employed. The starting solution containing the konjakmannan ester is prepared as described above. The solution is then introduced into an aqueous medium, in order to form spherical liquid droplets of the solution suspended in the aqueous medium, as the precursor of the beads of konjakmannan ester. The aqueous medium may be water or an aqueous solution containing a hydrophilic protective colloid such as partially-hydrolysed polyvinyl acetate, polyvinyl alcohol, carboxymethylcellulose, ethylcellulose, methylcellulose, soluble starch or gelatine. The use of partially-hydrolysed polyvinyl acetate and polyvinyl alcohol as the protective colloid is preferred, since they dissolve quite well in water even at lower temperature and, in addition, reveal the ability for dispersing particles and an effect of increasing the viscocity more easily as compared with other ones. The protective colloid may preferably be employed in a form of an aqueous solution of a concentration of 0.1 - 10 % by weight, preferably 0.3 - 5 % by weight. A concentration of protective colloid lower than 0.1 % by weight tends to form konjakmannan particles having excessively large particle size and concentrations outside the range of from 0.1 to 10 % by weight tend to produce konjakmannan particles of not spherical form. The aqueous medium may preferably be used at least in the same volume and preferably in an amount of 2 - 20 times of the volume of the konjakmannan ester solution. The starting process solution is introduced into the aqueous medium all at once, followed by agitation to disperse to form a suspension or, it may be introduced into the aqueous medium held in an agitated state all at once or dropwise to form a suspension. The intensity of agitation is so regulated, that the average bead size of the final product will be from 1 to 500 µm. Upon introduction of the starting solution into the aqueous medium, the konjakmannan ester will be dispersed and suspended finely in the aqueous medium, since esterified konjakmannan is insoluble in water. Here, evaporation of the solvent starts concurrently with the formation of beads. In this manner, spherical beads of konjakmannan ester from which the solvent has substantially be evaporated off will finally be obtained. For the temperature for evaporating off the organic solvent in the liquid droplets, a temperature above the freezing point of the aqueous medium and below the boiling point of the organic solvent is employed. Here, a temperature which is lower than the boiling point of the organic solvent, in particular by 1 - 15°C, is preferred, in order to keep the spherical form of the bead in a better manner and to facilitate the evaporation of the organic solvent. During the process step for evaporating off the organic solvent from the liquid droplets, the aqueous medium is held under agitation so as to maintain the spherical form of the liquid droplet. After the organic solvent contained in the liquid droplets has been evaporated off, spherical beads are left behind. The beads are formed in a gelled state and contain internally the diluent within a pumice-like porous matrix and can hold their shape of beads after they have been taken out of the aqueous medium. The diluent contained in the beads of konjakmannan ester is removed partly in this process step and will be removed completely in the subsequent process step of saponification. The spherical beads of konjakmannan ester are then subjected to a saponification after they have been taken out of the aqueous medium. The saponification is effected for restoring the water soluble nature by re-conversion into free konjakmannan. Here, substantially all the esterified konjakmannan is saponified. It is necessary to employ a saponification bath which permits to effect saponification without causing any harmful effect to the spherical form of the konjakmannan ester beads which have restored their water-solubility after the re-conversion into free konjakmannan. As the saponification bath, for instance, an alcohol solution of alkali hydroxide, such as a methanol solution of sodium hydroxide or potassium hydroxide, an aqueous solution of alkali hydroxide, such as an aqueous solution of sodium or potassium hydroxide dissolved in an aqueous solution of salts such as sodium sulfate etc., may be used. One concrete manner of effecting the saponification consists in that spherical beads of a konjakmannan ester are soaked in an amount of methanol, which may amount to 5 - 10 times of the weight of the beads in accordance with each particular requirement, for 0.1 - 2 hours. The thus soaked beads are then introduced into a saponification bath of a mixture, which consists of an alcohol, such as, methanol etc., and of an aqueous solution of sodium hydroxide in a weight ratio of [alcohol] : [aqueous solution] of [9 ∼7] : [1 ∼3] and has a concentration of 0.1 - 5 N NaOH, in such an amount that the ratio of [konjakmannan] : [NaOH] is 1 : [0.5∼10] on the weight basis, and the mixture is agitated at room temperature for 10 - 24 hours to effect the saponification. Here, the sodium hydroxide solution may be incorporated by adding it dropwise so as to reach finally said range. If the concentration of NaOH of the bath is lower than 0.1 N, the saponification does not proceed sufficiently and, on the other hand, if it exceeds 5 N, cracks may occur in the beads. If the content of the alcohol is outside of the above mentioned range, undesirable phenomena, such as, elution or leakage of the saponified konjakmannan and abnormal progress of saponification and so on, may appear. During this saponification step, the konjakmannan ester in the beads is saponified and the diluent contained in the beads will be extracted into the alcohol, leaving behind many voids or pores inside the bead to form a porous macrostructure. One concrete manner of effecting the saponification with an aqueous alkali solution consists in that the spherical beads of konjakmannan ester are introduced into an aqueous solution prepared by dissolving sodium hydroxide or potassium hydroxide in an aqueous solution of sodium sulfate and the mixture is agitated for 24 hours at room temperature. The concentration of the alkali hydroxide in this aqueous solution is 10 - 15 % by weight and the amount of the alkali hydroxide may not be less than 50 %, based on the amount of the konjakmannan ester. The amount of sodium sulfate employed may be in the range of 20 to 30 %, based on the total weight of aqueous solution. Among the concrete manners of saponification described above, the use of alcohol/aq. NaOH mixture may be more preferable from the reasons that it realizes simultaneous elution or removal of the residual diluent and so on. The thus obtained beads of konjakmannan which have restored their water-solubility by the saponification are then contacted with a cross linking agent. The cross linking agent will penetrate into the inside of the spherical bead of konjakmannan to realize cross linking of the konjakmannan molecules with each other. For the cross linking agent, bifunctional compounds, such as, epichlorohydrin, diepoxybutane, tolylene diisocyanate, hexamethylene diisocyanate and so on, can be employed. The cross linking agent is employed in a form of a solution in an organic solvent. As the organic solvent for the cross linking agent, there may be employed kerosene or liquid paraffin or a mixture of them (for example, in a volume ratio of 7 : 3) with addition of a surface active agent (a non-ionic surfactant, such as, sorbitan fatty acid ester) in an amount of 1 - 2 % by weight. Another example of the solvent for the cross linking agent consists of a mixture of acetone with dimethyl sulfoxide (with a volume ratio of, for example, 6 : 4). The concentration of the solution of cross linking agent may be at least 0.01 mole per liter of the cross linking solution and preferably in the range from 0.01 to 15 moles per liter of the cross linking solution. The cross linking of konjakmannan in the spherical beads is attained by introducing 1 - 5 parts by weight of the konjakmannan beads into 100 parts by weight of the solution of cross linking agent and agitating the mixture at a temperature of about 60 °C for 24 - 36 hours. The thus cross-linked spherical beads of konjakmannan are then filtered off and rinsed with acetone and washed then using a neutral surfactant, followed by water wash. If the amount of the cross-linking agent used is below the given value, the stability under pressure is reduced. The ion-exchanger according to the present invention is based on beads of cross-linked konjakmannan, into which radicals of one or more of ion-exchangeable groups have been introduced by a chemical treatment thereof. It is therefore insoluble in water, in aqueous alkali and in aqueous acid, and is physically robust. Its degree of swelling is preferably 1.5 to 15, more preferably 2 to 8, so that is has good water-retaining ability, which renders it suitable for use for general ion-exchange purposes. If the degree of swelling is less than 1.5, the beads may not be employed practically for an ion-exchanger due to the decrease in the water-retaining ability. If the degree of swelling exceeds 15, the compressive strength of the beads is reduced to an undesirable extent. The exclusion limit molecular weight of the ion-exchanger according to the present invention is from 10⁵ to 10⁸. Products having such a high exclusion limit molecular weight have considerably higher compressive strength than other gel products. The novel products are useful for the separation of materials such as proteins. The "exclusion limit molecular weight" means that particles having molecular weights higher than this limitation will not penetrate through the micropores of the packing material. This is represented, in practice, in terms of the molecular weight determined by a procedure in which a series of aqueous solutions of a certain high molecular weight substance, such as, dextran, polyethylene glycol etc., of varying known molecular weights are passed through a column charged with a packing material to be tested, in order to observe each eluted amount using a differential refractometer, spectrophotometer or so on and the data observed are plotted on a graph with respect to the molecular weight of the substance observed and reading the molecular weight value at the break of the curve. The ion exchanger based on beads of cross-linked konjakmannan according to the present invention are especially suitable for use for the packing material for ion-exchange chromatography, while other uses for universal ion exchange purposes are also permissible. Using the ion exchanger according to the present invention in ion exchange chromatography, a marked increase in the separation efficiency in separating various biological substances can be attained, since it permits a remarkably high flow rate of the liquid containing such biological substances, which conventional ion exchangers have not ever permitted. In a separation of physiologically active substances or the like, it is required to effect treatment operations within a period of time as short as possible, since there may occur an activity depression of the substances during the separation procedures due to possible existence of instability of the substances included. Here, a high flow rate of the liquid to be subjected to the ion-exchange chromatography will save such a problem and reveals an inventive feature of the ion exchanger according to the present invention. Preferred Embodiments of the Invention In the following, the present invention will be described by way of Examples. Example 1 (1) Production of Cross-linked Glucomannan (konjakmannan) Beads 40 g of konjakmannan powder were dissolved in 4 ℓ of deionized water at 60 - 70 °C with agitation. This solution was dropped in small portions into 6 ℓ of ethanol to cause deposition of the glucomannan (konjakmannan), which was filtered out and dried in air and then under vacuum at 20 °C. 30 g of this dried glucomannan (konjakmannan) were introduced into 1 ℓ of formamide and stored for two days to cause it to swell. Thereto were then added 300 mℓ of pyridine and 300 mℓ of acetic anhydride to cause reaction with the swollen glucomannan (konjakmannan). The reaction was conducted at 50 °C for 5 days. The reaction mixture was then poured into 7 ℓ of water with agitation. The precipitate formed was separated by filtration and was washed with water. The precipitate was then dried in air and then under vacuum. 3 g of this dried product were dissolved in 300 mℓ of chloroform containing 10.5 mℓ of decahydronaphthalene. This solution was then dropped into 3ℓ of 2 % aqueous solution of a by 90 % saponified polyvinylalcohol with agitation and, by continuing an adequate agitation, liquid droplets of the chloroform solution having an average particle size of 44 - 105 µm were formed. By cooling this suspension gradually over 24 hours, solidified particles were obtained, which were separated by filtration and washed with water. This particulate product was then introduced into a solution composed of 270 mℓ of methanol and 30 mℓ of 10 N NaOH and saponification was effected by maintaining the mixture for 24 hours with agitation. The so saponified beads were then separated by filtration and were introduced into a cross linking bath prepared by dissolving 35 g of epichlorohydrin in 300 mℓ of a 1 : 1 mixture of acetone and dimethyl sulfoxide and the cross linking reaction was conducted at 60°C for 24 hours. (2) Introduction of Ion Exchangeable Group into the Beads In a 300 mℓ three-necked flask immersed in an ice bath, there were charged 5 g (dry weight) of cross-linked glucomannan (konjakmannan) beads and thereto were added 40 mℓ of 4 N aqueous solution of sodium hydroxide to soak the beads under agitation for 1 hour. Thereto were then added 10 mℓ of aqueous solution of 2-chloro-triethylamine hydrochloride whose concentration had been adjusted to 3 g/mℓ. The resulting mixture was heated to 80 - 83 °C and the reaction was conducted for 1 hour. After 1 hour, the three-necked flask was immersed again in the ice bath to cool the reaction mixture, whereupon the beads were filtered on a filter cloth with aspiration. The beads were washed with about 5,000 mℓ of deionized water. There was obtained an ion exchanger of cross-linked glucomannan (konjakmannan) beads into which bonded radicals of diethylaminoethyl had been introduced. The total ion-exchange capacity was determined by sampling a portion of the so obtained beads and subjecting it to a neutralization titration and was found to be 0.95 meq. per g of dry beads. The cross-linked glucomannan (konjakmannan) beads having therein bonded radicals of DEAE-group obtained as above and stored under soaking in water were packed in a stainless steel column having a length of 300 mm and an inner diameter of 5 mm. Using this packed column, experiments were carried out as to the relationship between the flow rate of liquid passing through the column and the resulting pressure loss (Δp) by observing the flow rate and the liquid inlet pressure by flowing the liquid using a high pressure feed pump. The observed values are plotted on a graph as shown in Fig. 1. As comparison examples, similar experiments were carried out using two commercial products, namely DEAE-Sephadex A-50 (trademark) and DEAE-Sepharose CL-6B (trademark) of the firm Pharmacia Fine Chemicals. The results are also plotted in the graph of Fig. 1 for the sake of comparison with those of the beads according to the present invention. From the graph of Fig. 1, it is seen that the compressive strength of the DEAE-glucomannan (konjakmannan) ion exchanger of the present invention is considerably higher than that of the beads of DEAE-Sephadex A-50 and of DEAE-Sepharose CL-6B, since there holds a linear relationship between the flow rate and the pressure loss Δp even at higher flow rates without causing any steep rise of pressure. Example 2 In a 50 mℓ three-necked flask, 2 g (dry weight) of the cross-linked glucomannan (konjakmannan) beads obtained in the above (1) of Example 1 were soaked in 20 mℓ of 10 N aqueous solution of sodium hydroxide. While cooling the flask by immersing it in a constant temperature bath filled with ice water, the reaction mixture in the flask was kept agitated mildly for 1 hour using a stirrer. Thereto was added subsequently an aqueous solution of monochloroacetic acid (8 g of monochloroacetic acid + 16 mℓ of ultra-high purity water) and the temperature of the contents of the flask was elevated up to 70 °C. After 1 hour from the arrival at 70 °C, the reaction mixture was filtered by a glass filter and the beads thus separated were washed with ultra-high purity water sufficiently. The ion exchange capacity of the so washed beads was determined after they had been subjected to a conditioning in a usual way. The capacity was found to be 2.3 meq. per g of dry beads. Example 3 Using a glass column having an inner diameter of 5 mm and a length of 100 mm packed with a DEAE-glucomannan ion exchanger having introduced therein bonded radicals of ion-exchangeable group prepared so as to have a total ion-exchange capacity of 0.15 meq. per mℓ of gel, an adsorption-elution experiment was carried out for human albumin and for haemoglobin. The concentration of these substances in the liquid to be passed through the column was settled each at 4 mg/mℓ and the amount of charge thereof was adjusted at 5 µℓ. For ion adsorption, a buffer solution of 0.02 M tris(hydroxymethyl)-aminomethane (pH = 8.02) was passed through the column at a flow rate of 0.5 mℓ/min. For elution, a buffer solution of 0.5 M NaCl/0.02 M tris(hydroxymethyl)-aminomethane (pH = 8.02) was passed through the column at a flow rate of 0.5 m ℓ/min. The elution time for each substance was found to be: 10.4 min. for human albumin 10.2 min. for haemoglobin The flow rate of the solution was varied both for human albumin and for haemoglobin in the range from 0.5 m ℓ/min. to 5 mℓ/min. and the column was re-used in the subsequent experiment after regeneration of the beads and water wash thereof. In the experiment using the conventional commercial product (DEAE-Sepharose), it was practically impossible to flow the solution at flow rates above 2 mℓ/min.

Claims: An ion-exchanger comprising beads of cross-linked konjakmannan having radicals of one or more ion-exchangeable groups, and wherein the cross-linked konjakmannan has an exclusion limit molecular weight of 10⁵ to 10⁸. An ion-exchanger according to claim 1, which has an ion-exchange capacity of 0.1 to 5 meq. per g of dry beads. An ion-exchanger according to claim 1 or claim 2, wherein the ion-exchangeable group or groups are selected from carboxymethyl, sulfomethyl, primary, secondary, tertiary or quaternary aminoethyl, sulfopropyl and phosphate. An ion-exchanger according to any preceding claim, wherein the beads of cross-linked konjakmannan have a degree of swelling of 1.5 to 15 and an average bead diameter of 5 to 500 µm. An ion-exchanger according to claim 4, wherein the beads of cross-linked konjakmannan have a degree of swelling of 2 to 8. An ion-exchanger according to any preceding claim, as obtained by the steps of processing esterified konjakmannan into beads, subjecting the beads to saponification and cross-linking, and introducing the radicals by chemical treatment. An ion-exchanger according to claim 6, wherein more than 85% of the hydroxyl groups in the konjakmannan are esterified. A process for preparing an ion-exchanger according to any preceding claim, which comprises conducting the steps defined in claim 6 or claim 7. An ion-exchange column comprising an ion-exchanger according to any of claims 1 to 7. An ion-exchange process, which comprises contacting a liquid containing ions with an ion-exchanger according to any of claims 1 to 7.

Inventors: JOKO, ISAO, MORITA, HIROSHI, MOTOZATO, YOSHIAKI, TOMODA, TAKASHI, YAMAGUCHI, MASATO
Applicants: KURITA WATER INDUSTRIES LTD., MOTOZATO, YOSHIAKI
Application year: 1988
Main classification: B01J39
IPC codes: C08L5, B01J39, G01N30, B01J20, B01J41