Process for preparing N-substituted amine

Abstract: An N-substituted amine is produced by reacting an alcohol or aldehyde with ammonia, a primary amine or a secondary amine in the presence of a catalyst comprising (1) copper, (2) a metal selected from chromium, manganese, iron, cobalt, nickel and zinc, (3) a metal of the platinum VIII group and (4) a metal selected from aluminium, tungsten and molybdenum.

Description: The present invention relates to a process for preparing an N-substituted amine which comprises reacting an alcohol or an aldehyde with ammonia or a primary or secondary amine. The amine prepared according to the present invention is a material important from the industrial viewpoint as intermediates of a rust preventive, a surfactant, a germicide, a dyeing assistant and a fiber softener, etc. It is known in the art that an alcohol or an aldehyde is reacted with ammonia or a primary or secondary amine to give the corresponding amine. However, it was difficult to selectively prepare a particular amine through a reaction of an alcohol or the like with an amine or the like. Examples of the process for preparing an amine from an alcohol and an amine include those disclosed in Japanese Patent Laid-Open Nos. 19604/1977 (a copper chromite catalyst and a cobalt catalyst) and 59602/1978 (copper/molybdenum and copper/tungsten catalysts), U.S. Patent No. 3 223 734 (Raney nickel catalyst and copper chromite catalysts), West German Patent Laid-Open No. 1,493,781 (a supported cobalt catalyst), Japanese Patent Publication No. 55704/1982 (a copper/nickel catalyst), etc. However, these catalysts are insufficient in both the catalytic activity and the selectivity and should be used in a large amount, which brings about a low yield of the intended amine. In order to solve these problems, processes described in Japanese Patent Laid-Open Nos. 15865/1986, 149646/1987, 149647/1987, and 149648/1987 have been developed. In these processes, a copper/nickel/group VIII platinum metal element catalyst is used to prepare an intended amine in a high yield. That is, in these processes, an intended amine is prepared in a high yield through the addition of a small amount of the group VIII platinum metal element to a conventional copper/nickel catalyst having insufficient activity and selectivity for the purpose of improving the activity and selectivity. However, the process in which the reaction is conducted in the presence of this catalyst is not always satisfactory from the viewpoint of the durability of the catalyst. Specifically, although this process is superior in the activity and the selectivity to other general processes and brings about little or no lowering in the activity of the catalyst even after recovery and reuse of tens of times, the selectivity is lowered. Therefore, with the consideration of the preparation of an N-substituted amine on a commercial scale, a further improvement in the durability is desired from the viewpoint of the yield and quality of the formed N-substituted amine. However, N-substituted amines which have been prepared in the presence of these catalysts bring about the deterioration of hue when converted into a quaternary ammonium salt (tetraalkylammonium salt, trialkylbenzylammonium salt, etc.), which unfavorably causes remarkable deterioration of performance in applications such as surfactants. DE-A-3641666 discloses the use of a catalyst comprising copper, nickel and a group VIII metal to produce secondary amines by reacting an alcohol or aldehyde with a primary amine. The invention provides a process for preparing an N-substituted amine, which comprises the step of reacting an alcohol or an aldehyde with ammonia, a primary amine or a secondary amine at 150 to 250°C at a pressure of the atmospheric pressure to 100 atm gauge (101.325 to 10132.5 KPa), while water formed in the reaction is being removed out, in the presence of a catalyst comprising as active components: (1) copper; (2) a metal selected from the group consisting of chromium, manganese, iron, cobalt, nickel and zinc; (3) a metal of the platinum VIII group; and (4) a metal selected from the group consisting of aluminum, tungsten and molybdenum. It is preferable that a molar ratio of the component (1) to (2) ranges from 10/90 to 99/1, preferably 1/9 to 9/1 or 50/50 to 99/1, a molar ratio of the component (3) to the sum total of (1) and (2) ranges from 0.001 to 0.1 and a molar ratio of the component (2) to (4) ranges from 1/0.01 to 1/1. The addition of aluminium, tungsten or molybdenum as a fourth active component to a copper/fourth period transition metal element/group VIII platinum metal element catalyst brings about an improvement in the durability of the catalyst while substantially maintaining the activity and the selectivity. In this case, chromium, manganese, iron, cobalt, nickel and zinc were useful as the fourth period transition metal element while platinum, palladium, ruthenium and rhodium were useful as the group VIII platinum metal element. Consequently, the addition of aluminium, tungsten or molybdenum as the fourth active component to the copper/fourth period transition metal element/group VIII platinum metal element catalyst enabled the development of a high performance amination catalyst not only having activity and selectivity equal to those of the copper/fourth period transition metal element/group VIII platinum metal element catalyst and durability far superior to that of the copper/fourth period transition metal element/group VIII platinum metal element catalyst. The fourth period transition metal elements particularly suitable for the reaction according to the present invention are chromium, manganese, iron, cobalt, nickel, and zinc. The platinum group elements particularly suitable for the reaction according to the present invention are platinum, palladium, ruthenium, and rhodium. Further, the fourth component particularly useful for the reaction according to the present invention includes aluminum, tungsten, and molybdenum. A molar ratio of the fourth period transition metal element to the fourth component is preferably 1/0.01 to 1/1, more preferably 1/0.05 to 1/1. Although the catalyst metal composition should contain four components, ie. copper, a fourth transition metal element, a platinum group element, and a fourth component, the catalyst suitable for the present invention may have various forms. Specifically, in the present invention, only when the four components, ie. copper, a fourth period transition metal element, a platinum group element, and a fourth component are present in the reaction system as the catalyst composition, an effect can be attained through interaction among the four components. Therefore, this four component composition has a substantial function as a catalyst, and in the reaction the catalytic activity is not developed until each metallic component is reduced in a hydrogen atmosphere. For this reason, in the present invention, there is no limitation with respect to the form of the metals before the reduction and the state of the system after the completion of the reduction as far as the reduction in a hydrogen atmosphere according to the method described in the present specification brings about interaction among copper, the fourth period transition metal element, the platinum group element, and the fourth component. Therefore, the metals suitable for the process of the present invention may have any of the following forms as far as the four metal components indispensable to the present invention bring about interaction thereamong through reduction in a hydrogen atmosphere: 1) a form of a metal, an oxide or a hydroxide thereof and a mixture thereof which can be dispersed in a reaction medium; 2) a form of either a mixture of copper, a fourth period transition metal element, a platinum group element and a fourth component respectively supported on suitable carriers, or three components, i.e., copper, a fourth period transition metal element, a platinum group element, and a fourth component, homogeneously supported on a single carrier which can be dispersed in a reaction medium; 3) a form of an aliphatic carboxylic acid salt of these metals, a complex of these metals stabilized by a suitable ligand or the like which is converted into a metallic colloid in a reaction medium to form a homogeneous system; and 4) a mixture of a form described in the above items 1) and 2) which is dispersed in a reaction medium with a form described in the above item 3) which forms a homogeneous system in a reaction system, or a form which is in a dispersed state before hydrogen reduction but becomes homogeneous after hydrogen reduction. With respect to the form of the catalyst used in the process of the present invention, it is preferred from the viewpoint of the stabilization of the catalyst metal, i.e., immobilization of the active surface, and resistance to a catalyst poison that the above-described four metal components are homogeneously supported on a suitable carrier. When the four metal components according to the present invention, i.e., copper, a fourth period transition metal element, a platinum group element, and a fourth component, are to be supported on a carrier, suitable carriers are those commonly employed as catalyst carriers, e.g., alumina, silica/alumina, diatomaceous earth, silica, active carbon, and natural and artificial zeolite. Although the amount of the catalyst metal supported on a carrier may be arbitrarily determined, it is generally preferably 5 to 70%. Further, these four metal components may be supported on a carrier by various methods. In this case, the form of the raw metals of the catalyst may be an oxide, a hydroxide, or various salts of copper, a fourth period transition metal element, and a platinum group element. Examples of the form of the raw metals include chlorides, sulfates, nitrates, acetates, aliphatic carboxylates of copper, a fourth period transition metal element, a platinum group element, and a fourth component, or complexes of these metals, e.g., acetylacetone complexes and dimethylglyoxime complexes of copper, a fourth period transition metal element, a platinum group element, and a fourth component. Further, with respect to the platinum group element, carbonyl complexes, amine complexes, phosphine complexes, etc. may also be employed. The preparation of a catalyst through supporting of the metal components on a carrier by making use of these raw metal materials may be conducted by any of conventional known processes, e.g., a process which comprises adding a carrier to a solution of suitable salts of copper, a fourth period transition metal element, a platinum group element, and a fourth component, to sufficiently impregnate the carrier with the solution and drying and baking the impregnated carrier (impregnation process), a process which comprises conducting either a step of sufficiently mixing a carrier with an aqueous solution of suitable salts of copper, a fourth period transition metal element and a platinum group element and then adding an aqueous alkaline solution, such as an aqueous sodium carbonate or sodium hydroxide solution or aqueous ammonia, to the mixture to precipitate the metal salts on the carrier, or a step or simultaneously adding an aqueous solution of suitable salts of copper, a fourth period transition metal element and a platinum group element and an aqueous alkaline solution, such as an aqueous sodium carbonate or sodium hydroxide solution or aqueous ammonia, to a water slurry of a carrier in such a manner that the pH value of the slurry remains constant (e.g., a constant pH value of 7) to precipitate the metal salts on the carrier, drying and baking the metal salts supported on the carrier to prepare a copper/fourth period transition metal element/platinum group element catalyst, placing the resulting ternary catalyst in an aqueous solution of an alkali metal salt or an alkaline earth metal salt to impregnate the catalyst with the aqueous solution, and drying and baking the impregnated catalyst (a combination of the coprecipitation process with the impregnation process), and a process which comprises conducting an ion exchange with hydrogen or a metal contained in zeolite (ion exchange process). In the case of the coprecipitation process, the carrier is sufficiently washed with water after deposition of the metals, dried at about 100°C, and baked at 300 to 700°C to prepare a catalyst. An other effective process comprises supporting only copper or only copper and a fourth period transition metal element on a carrier through the above-described processes and adding, prior to the reaction, a supported platinum group element or fourth/component, or an aliphatic carboxylate or a complex thereof to form a composite comprising a combination of copper with the fourth period transition metal element, the platinum group element and the fourth component in a reaction medium in a hydrogen atmosphere. With respect to the form of the catalyst, it is more preferable that the four components be homogeneously supported on the same carrier. The four components, i.e., copper, a fourth period transition metal element, a platinum group element, and a fourth component, are indispensable to the present invention. The alcohol or aldehyde which is a starting material used in the present invention is a straight-chain or branched saturated or unsaturated aliphatic alcohol or aldehyde having 8 to 36 carbon atoms. Examples of the alcohol include octyl alcohol, lauryl alcohol, myristyl alcohol, stearyl alcohol, behenyl alcohol, oleyl alcohol, and a mixture thereof, a Ziegler alcohol prepared by the Ziegler process, an oxo alcohol prepared by the oxo process, and alcohols having a branched chain such as Guerbet alcohol. Examples of the aldehyde include lauraldehyde, oxo aldehyde, and aldehydes corresponding to the above-described alcohols. Further, various polyhydric alcohols may also be used, and examples thereof include 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,9-nonanediol, diethylene glycol, and triethylene glycol. Examples of other alcohol include aromatic alcohols, such as benzyl alcohol and phenethyl alcohol, polyoxy ether alcohols, such as adduct of an aliphatic alcohol with ethylene oxide or propylene oxide, and amino alcohols, such as ethanolamine and diethanolamine. The alcohol or aldehyde is particularly preferably an aliphatic alcohol or aldehyde selected from among saturated and unsaturated straight-chain and branched aliphatic alcohols and aldehydes having 8 to 36 carbon atoms and aliphatic glycols having 2 to 12 carbon atoms. The amine which is reacted with these alcohols or aldehydes may be a gaseous or liquid one, and examples thereof include aliphatic amines, e.g., primary amines such as monomethylamine, ethylamine and dodecylamine, and secondary amines such as dimethylamine, diethylamine and didodecylamine. In the present invention, it is necessary to remove water formed during a reaction of an alcohol or an aldehyde with an amine from the reaction system. When the formed water is not removed from the reaction system, no sufficient catalytic performance according to the present invention can be attained. That is, the catalytic activity and selectivity are lowered, so that it becomes difficult to easily prepare an N-substituted amine in a high yield. For example, when the reaction is conducted by making use of dimethylamine as the amine without removing the formed water, not only the amount of by-products, such as monoalkylmethylamine, which are difficult to separate through mere distillation is increased but also a high-boiling material, such as condensate of an aldehyde, is formed in a large amount, which brings about a lowering in the yield of the intended N-substituted amine. Water may be intermittently or continuously removed during the reaction as far as the formed water is properly removed so as not to remain in the reaction system for a long period of time. It is preferred to continuously remove water each time it is formed. More specifically, it is a common practice to introduce a suitable amount of hydrogen gas into the reaction system to distill the formed water and the excess amine (in the case of use of a gaseous amine) together with the hydrogen gas. In this method, it is also possible to reuse the hydrogen gas through condensation and separation of the formed water in a condenser. Further, a suitable solvent may be added to the reaction system, followed by distillation and removal of the formed water in the form of an azeotrope with the solvent. In the process of the present invention, although a catalyst which has separately been reduced with a hydrogen gas may be employed, a catalyst before reduction is placed in a reactor together with the starting material of the reaction, i.e., an alcohol or an aldehyde, followed by elevation of the temperature to the reaction temperature while introducing a hydrogen gas, thereby conducting reduction. That is, the copper/fourth period transition metal element/platinum group element catalyst according to the present invention has also a significant feature that since the reduction temperature is low, the reduction can be conducted in the step of elevating the temperature to the reaction temperature. The preferred embodiments of the process of the present invention will now be briefly described. A reaction vessel equipped with a tube for introducing hydrogen and an amine and a condenser and a separator for condensing and separating water formed during the reaction, the excess amine and oleaginous matter distilled off is charged with a starting material, i.e., an alcohol or an aldehyde, and a catalyst. The amount of the catalyst may be arbitrary. Since, however, the catalyst of the present invention has high activity, it is usually employed in an amount as small as 0.1 to 2 % by weight based on the feed alcohol or aldehyde. The system is purged with a nitrogen gas, and the temperature is then raised while introducing hydrogen. The reaction is usually conducted at a temperature of 150 to 250°c. However, the reaction temperature may be one outside the above-described range depending upon the kind of the reaction. The catalyst is converted into a reduced, active state during the elevation of the temperature. When the temperature reaches a predetermined value, ammonia or an amine is introduced to initiate the reaction. The amine may be gaseous or liquid. Further, the amine may be introduced into the system in a continuous or intermittent manner or at a time (in the case of a liquid amine). During the reaction, the formed water is discharged outside the reaction system together with gaseous substances (excess gaseous amine in the case of the use of hydrogen and a gaseous amine) and passed through the condenser and separator to separate the water from the oleaginous matter. The analysis of the gaseous substances (excess gaseous amine in the case of the use of hydrogen and a gaseous amine) has revealed that these gaseous substances are substantially free from by-products (e.g., hydrocarbon and amine by-product formed by disproportionation of the starting amine), i.e., has proved that the catalyst of the present invention has high selectivity. Therefore, it was found that these gaseous substances can be reused without any special step of purification. After the completion of the reaction, the reaction mixture itself is subjected to distillation or filtration to separate the reactant from the catalyst. The N-substituted amine obtained by the filtration can be distilled into a very pure form. Examples Example 1 and Comparative Example 1 A copper/fourth period transition metal element/platinum group element/fourh component quaternary catalyst supported on synthetic zeolite was prepared as follows. A 1-ℓ flask was charged with synthetic zeolite, and an aqueous solution prepared by dissolving copper nitrate, nickel nitrate, palladium chloride, and aluminum nitrate in water in a copper : nickel : palladium : aluminum molar ratio of 4 : 1 : 0.05 : 0.05 was then added thereto, followed by elevation of the temperature while stirring. An aqueous 10% Na₂CO₃ solution was gradually dropwise added thereto at 90°C. The mixture was aged for 1 hr, and the resultant precipitates were collected by filtration, washed with water, dried at 80°C for 10 hr, and baked at 400°C for 3 hr. The amount of the resultant metallic oxide supported on the carrier was 50%. Then, a reaction of an alcohol with dimethylamine was conducted in the presence of the above-prepared catalyst. In Comparative Examples, the reaction was conducted in the presence of a copper/nickel/palladium catalyst prepared in the same manner as that described above. A 1-ℓ flask equipped with a condenser and a separator for separating the formed water was charged with 600 g of lauryl alcohol and 1.5 g (0.25% by weight based on the starting alcohol) of the above-described catalyst. The system was purged with nitrogen while stirring, followed by initiation of the elevation of the temperature. When the temperature reached 100°C, a hydrogen gas was blown into the system through a flowmeter at a flow rate of 10 ℓ/hr, and the temperature was raised to 200°C. At this temperature, a mixed gas comprising dimethylamine and hydrogen was blown into the reaction system at a flow rate of 40 ℓ/hr, and the reaction was monitored by measurement of an amine value and gas chromatography. The results of the reactions including those of the reactions conducted in the presence of a catalyst after recovery of ten times and a catalyst after recovery of twenty times are shown in Table 1. It was found from the results that as with the Cu/Ni/platinum group element (Pd) ternary catalyst system (Comparative Example 1), the Cu/fourth period transition metal element (Ni)/platinum group element (Pd)/fourth component (Aℓ) quaternary catalyst system according to the present invention exhibited high activity and selectivity and a remarkable improvement in the durability. Examples 2 to 4 With respect to a catalyst comprising copper, a fourth period transition metal element, a platinum group element, and a fourth component, the activity in a reaction of stearyl alcohol with monomethylamine was determined by using Cr as the fourth period transition metal element and Ru as the platinum group element and varying the kind of the fourth component among Aℓ, W, and Mo in the catalyst. These quaternary catalysts were prepared by the impregnation process. The results of reactions conducted in the presence of catalysts after recovery of ten times are shown in Table 2. It was found from the results that when distearylmonomethyl tertiary amine was prepared through a reaction of stearyl alcohol with monomethylamine, the Cu/Cr/Ru/fourth component catalysts wherein Aℓ, W, or Mo is used as the fourth component exhibited a high activity and selectivity and remarkably improved in durability. Examples 5 to 7 With respect to a catalyst comprising copper, a fourth period transition metal element, a platinum group element, and a fourth component, the activity in a reaction of dodecyl alcohol with ammonia was determined by using Zn as the fourth period transition metal element and Pt as the platinum group element and varying the kind of the fourth component among Aℓ, W, and Mo in the catalyst. These quaternary catalysts were prepared in the same manner as that of Example 2. The results of reactions conducted in the presence of catalysts after recovery of ten times are shown in Table 3. It was found from the results that when tridodecylamine was prepared through a reaction of dodecyl alcohol with ammonia, the Cu/Zn/Pt/fourth component catalysts wherein Aℓ, W, or Mo was used as the fourth component exhibited a high activity and selectivity and improved in durability. Examples 8 A reaction of lauryl alcohol with ammonia was conducted in the presence of a Cu/Co/Pd/fourth component (Aℓ) catalyst. In this reaction, ammonia was blown into the system at a feed rate of 30 ℓ/hr. The reaction was monitored by measurement of an amine value and gas chromatography. The results of reactions conducted after recovery of ten times are shown in Table 4. It was found from the results that the use of the Cu/Co/Pd/fourth component (Aℓ) catalyst in a reaction of lauryl alcohol with ammonia enabled the preparation of a secondary amine with a high durability. Example 9 A reaction of lauryl alcohol with stearylamine was conducted in the presence of a Cu/Mn/Ru fourth component (W) catalyst. In this reaction, the stearylamine was introduced at a time in a liquid state into the reaction system. The reaction was monitored by measurement of an amine value and gas chromatography. The results of reactions conducted after recovery of ten times are shown in Table 5. It was found from the results that the present catalyst system enabled the reaction to proceed with very high activity and selectivity and the corresponding amine to be prepared with a high durability. Examples 10 to 13 The effect of the catalyst of the present invention was examined with respect to reactions of various alcohols or aldehydes with dimethylamine to prepare the corresponding tertiary amines. The catalysts used were prepared by the impregnation process. The results of reactions conducted after recovery of ten times are shown in Table 6. It was found from the above results that the catalyst of the present invention enabled a tertiary amine to be prepared with very high activity and high selectivity and high durability even when a branched alcohol, a polyhydric alcohol (glycol), or an aldehyde was used as the starting material and reacted with a secondary amine. In general, the use of such a branched alcohol, a polyhydric alcohol, or an aldehyde as the starting material brings about an increase in the possibilities of causing side reactions such as decomposition or condensation of these substances. However, it was substantiated that the catalyst having a composition according to the present invention was an excellent catalyst capable of solving these problems. Examples 14 A reaction of lauryl alcohol with stearylamine was conducted in the presence of a Cu/Fe/Pd/fourth component (Mo) catalyst. In this reaction, stearylamine was introduced at a time in a liquid state into the reaction system. The reaction was monitored by measurement of an amine value and gas chromatography. The reaction pressure was 50 atm (gauge). The results of reactions conducted after recovery of ten times are shown in Table 7. It was found from the results that the present catalyst system enabled the preparation of an amine through a reaction of lauryl alcohol with stearylamine with a high activity and a high selectivity. Example 15 Behenyl alcohol and stearylamine, red at a molar ratio of 1/1, were reacted with each other in the presence of 2 percent by weight, based on the alcohol, of a catalyst of Cu, Mn, Rh and Mo, having a molar ratio of 95,5/0.05/0.5 and an amount of support of 40 percent by weight, at 200°c. The stearylamine was introduced at a time in the form of liquid into the reaction system and the reaction procedure was followed with an amine value and gas chromatographic analysis. The used catalyst had been used 10 times before. Results are shown in Table 8. It is found that a corresponding amine can be produced with a high reactivity, a long durability and a high selectivity from a long chain alcohol and a long chain amine, with the catalyst of the invention. example 15 catalyst Cu/Mn/Rh/Mo reaction time (hour) 5 composition of product mixture (weight percent) unreacted alcohol 3.0 N-stearyl-behenylamine 81.0 others 16.0

Claims: A process for preparing an N-substituted amine, which comprises the step of reacting an alcohol or an aldehyde with ammonia, a primary amine or a secondary amine at a temperature from 150 to 250°C and at a pressure from 101.325 KPa to 10132.5 KPa (atmospheric pressure to 100 atm gauge), with removal of water formed in the reaction, in the presence of a catalyst comprising as active components (1) copper; (2) a metal selected from chromium, manganese, iron, cobalt, nickel and zinc; (3) a metal of the platinum VIII group; and (4) a metal selected from aluminium, tungsten and molybdenum. A process as claimed in Claim 1, in which the molar ratio of the component (1) to (2) ranges from 10/90 to 99/1, the molar ratio of the component (3) to the sum total of (1) and (2) ranges from 0.001 to 0.1 and the molar ratio of the component (2) and (4) ranges from 1/0.01 to 1/1.

Inventors: ABE HIROSHI, AIKAWA JUN, OKABE KAZUHIKO, SOTOYA KOHSHIRO, ABE, HIROSHI, AIKAWA, JUN, OKABE, KAZUHIKO, SOTOYA, KOHSHIRO
Applicants: KAO CORP, KAO CORPORATION
Application year: 1988
Main classification: C07C209
IPC codes: B01J23, C07C209