HIGH STRENGTH PIGMENTS FOR PRINTING INKS

Abstract: Organic pigments especially suitable in the manufacture of printing inks. The pigments are prepared with relatively high concentrations of resins or rosins which are reacted with controlled amounts of an aluminum salt to obtain aluminum resinates or aluminum rosinates. The resulting resinated pigmentary compositions are characterized by high strength, better transparency, good rheology without loss of coloristic properties.

Description: The present invention relates to a an improved method of preparing high strength organic pigments. More particularly, the invention pertains to making high strength organic pigments that are especially suitable for the manufacture of superiod printing inks. As set forth in U.S. Patent No. 4,102,704 (Fournier et al.), it is well known to incorporate modified or unmodified resins or rosins to improve the characteristics of pigmentary compositions intended for use in printing inks. In general, suitable additives include natural and synthetic resins. Rosin, often referred to as colophony, disproportioned rosin, hydrogenated rosin, and rosin derivatives are used for the present purposes. Such rosins have high compatibility with the binding agents employed in printing inks, have low softening points, as well as being soluble in an aqueous alkaline medium and substantially insoluble in an acidic medium. Organic pigments are generally resinated or rosinated during or after the conventional coupling procedure to achieve better dispersion of the pigmentary particles resulting in increased strength, transparency, and depth of mass tone for the pigments. The resin or rosin is normally precipitated as free acid or as a metal salt of calcium, barium or zirconium. In U.S. Patent No. 4,102,704, column 1, lines 26 through 35; French Patent No. 1,538,270 and Belgian Patent 660,978 are referred to for the foregoing teachings as well as the use of organic amines to react with the resin or rosin. Furthermore, the use of small quantities of wetting agents such as the oleic ester of triethanolamine is taught. The use of these additives are said to have the disadvantage of causing a loss in coloristic intensity. The disadvantages of the prior art procedures are said to be overcome in U.S. Patent No, 4,102,704 by incorporating modified or unmodified resin acids esterified with an amino alcohol in an acid aqueous solution containing the organic pigment. The esters are then precipitated by making the aqueous solution alkaline or by adding an acid which will form water insoluble salts. One of the features of the patented invention involves preparing the esters of the resin acids in a separate step. Somewhat more recently, Canadian Patent 1,170,802 proposes utilizing a high percentage of resin or rosin precipitated on the organic pigment as free acid to achieve high transparency and high tinctorial strength. However, when the manufacturing method of the Canadian Patent was utilized, for example with a C.I. Pigment Yellow-12, and in conjunction with a flushing treatment, the resulting flush has low viscosity and consequently needed more gelled vehicles to build up yield values for the ink so that it in turn would print better. US 4,327,017 describes a wide range of organic pigments which include an improving agent which may be an aluminium resinate, optionally formed in the presence of pigment. The suggested quantities of aluminium resinate in azo and polycyclic pigments compositions is relatively low, being no higher than 40% by weight. FR 1,246,922 relates to improvement of pigment compositions by the addition of metal resinates, including aluminium rosinate formed in the presence of the organic pigment. However, neither of these references realise the importance of the stoichiometric ratio of the aluminium to rosin in the pigment composition, in particular with respect to the rheology of the compositions. It would be advantageous therefore to have available a method for making pigmentary compositions that avoided such prior art problems or commercial problems as additional processing steps, loss of colour intensity, and undesirable viscosities when incorproated into ink. The product obtained by the practice of the method should lead to high strength, better transparency, and good rheological characteristics when used in printing inks. In accordance with the present invention it has now been found that a high strength organic pigment composition can be prepared by utilizing a high rosin content in a finished coupling and then precipitating the rosin as aluminum salts. When used in formulating printing inks high strength, better transparency and good rheology properties result. According to the present invention a new method for making a pigmentary composition comprising an azo, laked azo or phthalocyanine organic pigment and a dispersion enhancer selected from the group consisting of rosins, aluminium rosinates and mixtures thereof comprising contacting the pigment with rosin in an amount from 90 to 100% by weight of the organic pigment and with an aluminum salt in an amount effective to provide between 50% and 100% of the stoichiometric amount of aluminum theoretically needed for combination with all the rosin. In the preferred method the aluminum salt is contacted with the organic pigment prior to the rosin being contacted with the organic pigment. In another aspect of the invention there is provided a method for making rosinated pigmentary composition comprising the steps of: contacting an azo, laked azo or phthalocyanine organic pigment and a dispersion enhancer which is a rosin or mixture of rosins, said dispersion enhancer being present in an amount between about 90% and about 100% by weight of said organic pigment: contacting the resulting mixture with an amount of aluminum salt effective to form aluminum rosinate by combination of said rosin with said aluminum salt, where said aluminum salt is present in a concentration between 50% and 100% of the stoichiometric amount of the rosin. In yet another aspect of the invention there is provided a method for making a rosinated pigmentary composition comprising the steps of: a. contacting an organic pigment as outlined above with an aluminum salt to form a mixture; b. subsequently contacting said mixture with a dispersion enhancer selected from the group consisting of rosins and mixtures of rosin; the stoichiometric ratio of rosin to aluminum contributed by said aluminum salt being from about 2:1 to 1:1. The present invention also includes a new pigmentary composition comprising an organic pigment as outlined above, and a dispersion enhancer selected from the group consisting of rosins, aluminum rosinates and mixtures thereof, wherein 50% to 100% (by molar quantity) of said rosin is in the form of an aluminum rosinate, and in which the dispersion enhancer is present in an amount between about 90% and 100% by weight of the pigment. In general, the pigmentary compositions of the present invention comprise adding a solution of an aluminum salt to an alkaline slurry of a finished pigment coupling, and then adding an alkaline solution of the rosin. The pH is then made acidic and aluminum rosinate as well as unreacted rosin precipitate out and are separated from the solution and dried. The resulting granules or particles are suitable for use in the formulation of printing ink, which is another feature of the present invention. It is within the scope of the invention to initially add the alkaline solution of rosin to the alkaline slurry. However, it was unexpectedly found that the initial addition of the aluminum salt solution leads to superior rheology. The method of the invention is for use in the printing ink industry in which the pigments are azo pigments, laked azo pigments, and phthalocyanine pigments; the use of azo diarylide yellow pigments are especially preferred. The pigment slurry feed can either be dilute, i.e. 1-2% pigment, or concentrated, i.e. 2-15% pigment based on the weight of the slurry. The rosins employed may be any of those discussed above or mixtures thereof. The amount of rosin used ranges from 90 to 100% by weight based on the weight of the organic pigment. The use of about 100% by weight is preferred. The rosin is used in an alkaline aqueous solution such as a caustic soda solution. It should be understood, however, that other alkalies may be employed. Aluminum salts useful in the practice of the present invention include those which are water soluble such as aluminum sulfate, aluminum chloride, aluminum nitrate, etc. Preferred aluminum salts are aluminum sulfate and aluminum chloride. The amount of aluminum salt employed is an important feature of the invention. It has been found that the rheology of the organic pigment product may be changed to suit, for example, printing ink needs, by adjusting the amount of aluminum salt available for reaction with the rosin. More specifically, if a high excess of the theoretical or stoichiometric amount of aluminum necessary to react with the rosin is employed, the product has very poor rheology and poor gloss. Thus, the amount of aluminum salt employed is generally not more than about 100% of the stoichiometric amount necessary; preferred aluminum salt amounts range from 50 to 70% of the stoichiometric amount. In the present invention, a pigment suspension is heated to an elevated temperature, e.g. about 40 to 90°C, and the pH adjusted to the alkaline side, e.g. 9 to 11, preferably from 10.5 to 11.0, by using an alkaline solution of caustic soda, for example. Next, an aqueous solution of an aluminum salt is added to the pigment slurry, and this is followed by the addition of the rosin in the form of an alkaline solution, e.g. a 50% caustic soda solution. The pigment suspension is generally agitated during these addition steps. The pH of the slurry is then made acidic, the preferred pH being between 6.0 to 6.5. This change in pH can be accomplished by the addition of acids such as acetic acid, hydrochloric acid, or phosphoric acid. The aluminum rosinate as well as any free rosin precipitated out of solution, and the resulting slurry is filtered, the particles or granules washed to obtain a neutral pH, and then dried at a temperature ranging from about 45 to 60°C, preferably from 45 to 55°C. It is another aspect of the present invention to employ the novel pigmentary compositions in the manufacture of printing inks for commercial applications. Printing inks are conventionally made either by (1) using a flush base made out of pigment presscake in a high shear Sigma Blade mixer or (2) by dry grinding a dry pigment with suitable printing ink vehicles in a high shear machine such as a 3-roll mill. The resulting products are then cut back with suitable let down vehicles, solvents, etc. to meet the requirement of printing ink needs. In the flush process using a Sigma Blade machine, the pigment is preferably transferred into the oleophilic media, while the water which separates out is poured off. The product is washed to low conductivity, if necessary, and then dried to low moisture levels. The dried flush is cut back with suitable varnishes, solvents, etc. to meet appropriate printing ink needs. The present invention can be carried out in a dilute or concentrated pigment slurry, but can be advantageously done using a concentrated coupling and the resultant pigment slurry is flushed in a Sigma Blade mixer using resin solutions, which are known in the art as varnishes or flushing varnishes, alkyds and other solvents. The finished flush is then cut back with solvents, varnishes and other cut back vehicles to the consistency required of a printing ink or flush base. Such a procedure has the advantage over using regular presscake in flush because the pigmentary particles obtained are in an extremely fine state of dispersion, and achieve high tinctorial strength, much improved transparency, and better dispersion in the vehicle. The ink so prepared using the invention has up to 35% more tinctorial strength based on Yellow-12 content compared to a conventionally made product with little or no rosin and made under similar conditions. Alternatively, the pigment made according to the invention can be isolated in a filter press, washed salt free and the presscake flushed in a Sigma Blade mixer to obtain similar results. The pigment can also be washed salt free and dried in an air oven at 50-60°C, and the resultant dry pigment can be incorporated into printing ink vehicles using a high shear equipment such as a 3-roll mill or a high shear mixer. The invention will be more fully understood by reference to the following embodiments. Example 1 A pigment suspension containing 250 parts of C.I. Pigment Yellow-12 (Colour Index No. 21090) in a final coupling volume of 2900 parts (8.5% pigment concentration) was prepared by coupling at 12-14°C and at a final pH of 2.8-3.4. The finished coupling was then heated to 40-45°C. The pH of the pigment slurry was adjusted to 10-10.8, preferably 10.5-10.8, with caustic soda. A solution of a soluble aluminum salt containing 5.5 parts of aluminum, i.e. about 75% of the theoretical aluminum needed for the amount of rosin used, was added under agitation. Next 243 parts of a modified rosin (melting point 75-100°C) as a 20-25% solution in 70.7 parts of 50% caustic soda was added with agitation and the pH readjusted to 6.0-6.5 with dilute acetic acid. The above slurry when filtered, washed to neutral pH, dried in an oven at 50-60°C and tested against a non-resinated product using #1 Iso alkyd varnish (No. 1 Super Florite Aklyd supplied by Iovite Inc.) in the conventional Hoover Muller Test showed equal or 3-5% stronger color strength with much transparency and depth of mass tone. Thus, 1 gram of the new product containing 50.2% Yellow-12 pigment had equal or better strength to 1 gram of a regular Yellow-12 made without the rosin and aluminum salt. The pigment slurry obtained from above was flushed into a hydrocarbon resin varnish in magie oil (Magiesol 47 supplied by Magie Bros. Oil Company of Franklin Park, Illinois) using a high shear Sigma Blade mixer, washed to low conductivity with water and then dried under vacuum to low moisture. The product was then cut back with the varnish and solvents to a flush base. This product when tested against a conventionally prepared Yellow-12 slurry with no modifications, and subsequently flushed and converted to a flush base showed a strength advantage of 30-35%, based on Yellow-12 content, with good transparency and good rheology. Example 2 The procedure of Example 1 was repeated with the exception that the aluminum salt solution used contained 3.62 parts aluminum, i.e. about 50% of the theoretical aluminum required for the amount of rosin employed. The resulting product, when tested, showed a similar strength advantage and better rheological properties. Example 3 Following the procedure of Example 1, a series of runs were carried out with varying amounts of aluminum salt to demonstrate that greater than 100% stoichiometric amounts must be avoided to avoid undesirable product viscosities. Runs Rosin Based On Weight of Yellow-12 Al Salt Based On Stoichiometric Amount of Rosin Flush Viscosity A 100% 100% 544.4 B 100% 75% 285.5 C 100% 167% Too High To Measure The above data demonstrate that the practice of the present invention leads to unexpected and superior results without the necessity of additional processing steps or encountering viscosity and color intensity problems.

Claims: A method for making a pigmentary composition comprising an azo, laked azo or phthalocyanine organic pigment and a dispersion enhancer selected from the group consisting of rosins, aluminium rosinates and mixtures thereof, comprising contacting the pigment with rosin in an amount of from 90% to 100% by weight of the organic pigment and with an aluminum salt in an amount effective to provide between 50% and 100% of the stoichiometric amount of aluminum theoretically needed for combination with all the rosin. The method according to claim 1, wherein said aluminum salt is present in an amount effective to provide between 50% and 70% of the stoichiometric amount of aluminum theoretically needed to combine with all of the rosin. The method according to claim 1 or claim 2, wherein the aluminum salt is contacted with the organic pigment prior to the rosin being contacted with the organic pigment. The method according to claim 3, wherein the aluminum salt is added to an alkaline aqueous slurry of organic pigment prior to the addition of the rosin. A method according to any preceding claim in which the aluminum salt is a water-soluble inorganic salt, preferably selected from aluminum sulphate and aluminum chloride. A pigmentary composition comprising an azo, laked azo or phthalocyanine organic pigment, and a dispersion enhancer selected from the group consisting of rosins, aluminum rosinates and mixtures thereof, wherein the rosin is present in an amount between 90 and 100% by weight of the organic pigment and 50% to 100% (by molar quantity) of said rosin is in the form of an aluminum rosinate. A composition according to claim 6 in which 50% to 70% (by molar quantity) of said dispersion enhancer is an aluminum rosinate. Use of the product of a method according to any of claims 1 to 5 or of a composition according to either of claims 6 or 7 in the production of a printing ink.

Inventors: ANANTHARAMAN, K. R., SMOOT, WILMETH M., SOWARD, SUSAN T.
Applicants: SUN CHEMICAL CORPORATION
Application year: 1988
Main classification: C09B67
IPC codes: C09B67, C09F1, C09C3, C09D11