GAS SEPARATION MEMBRANES FROM BISPHENOL AF POLYCARBONATES AND POLYESTERCARBONATES

Abstract: The invention relates to a gas separation membrane comprising a thin discriminating layer of bisphenol AF polycarbonate or polyestercarbonate. The invention further relates to a method of separating gases comprising (a) contacting a feed gas mixture under pressure with one side of a semi-permeable membrane comprising a thin discriminating layer of polycarbonate or polyestercarbonate, wherein the diphenolic residue in the polymer backbone is based on bisphenol AF; (b) maintaining a pressure differential across the membrane under conditions such that a component of the feed gas selectively permeates through the membrane from the high pressure side to the low pressure side of the membrane; (c) removing the permeated gas which is enriched in the faster permeating component from the low pressure side of the membrane; and (d) removing the nonpermeated gas which is depleted in the faster permeating component from the high pressure side of the membrane.

Description: This invention relates to semi-permeable membranes substantially derived from bisphenol AF polycarbonates and polyestercarbonates. This invention further relates to the use of these membranes to separate gases. The use of membranes to separate gases is well known in the art. Membranes have been used to recover or isolate a variety of gases, including hydrogen, helium, oxygen, nitrogen, carbon dioxide, methane, and light hydrocarbons. Particular applications of interest include the separation of carbon dioxide from light hydrocarbons or other crude oil components as part of the tertiary oil recovery process. In other embodiments, nitrogen or helium is separated from natural gas. Other applications include the recovery of an enriched oxygen stream from air for use in enhanced combustion processes. Alternately, an enriched nitrogen stream may be obtained from air for use as an inert atmosphere over flammable fluids or for food storage. Such membrane separations are based on the relative permeability of two or more gaseous components through the membrane. To separate a gas mixture into two portions, one richer and one leaner in at least one component, the mixture is brought into contact with one side of a semi-permeable membrane through which at least one of the gaseous components selectively permeates. A gaseous component which selectively permeates through the membrane passes through the membrane more rapidly than the other component(s) of the mixture. The gas mixture is thereby separated into a stream which is enriched in the selectively permeating component(s) and a stream which is depleted in the selectively permeating component(s). The stream which is depleted in the selectively permeating component(s) is enriched in the relatively nonpermeating component(s). A relatively nonpermeating component permeates more slowly through the membrane than the other component(s). An appropriate membrane material is chosen for the mixture so that some degree of separation of the gas mixture can be achieved. Membranes for gas separation have been fabricated from a wide variety of polymeric materials, including cellulose triacetate; polyolefins such as polyethylene, polypropylene, and poly-4-methylpentene-1; and polysulfone. An ideal gas separation membrane is characterized by the ability to operate under high temperature and/or pressure while possessing a high separation factor (selectivity) and high gas permeability. The problem is finding membrane materials which possess all the desired characteristics. Polymers possessing high separation factors generally have low gas permeabilities, while those polymers possessing high gas permeabilities generally have low separation factors. In the past, a choice between a high separation factor and a high gas permeability has been unavoidably necessary. For instance, EP-A- 244 126 is directed to a membrane and its application for separating oxygen from a mixture of gases containing oxygen and nitrogen, the membrane comprising a polyestercarbonate of the formula wherein A is R¹ is separately in each instance -CO-, -SO₂ -, -O-, a single direct bond, a C₁₋₆ divalent hydrocarbon radical, C₁₋₆ divalent fluorocarbon radical, or an inertly substituted C₁₋₆ divalent hydrocarbon radical. These polyestercarbonate membranes have high selectivity or separation factor, e.g. O₂ /N₂ separation factor of 6.5 or above. However, the gas permeability is rather low, e.g. about 1 barrer. See the table of data on the last page of the description. Furthermore, some of the membrane materials previously used have suffered from the disadvantage of poor performance under high operating temperatures and pressures. A membrane which possesses high selectivity, high gas permeability, and ability to operate under extreme conditions of temperature and pressure is needed. The invention relates to a gas separation membrane comprising a thin discriminating layer of polycarbonate or polyestercarbonate, and a diphenolic residue in the polymer backbone based on a bisphenol , wherein the gas separation membrane functions as a semi-permeable membrane capable of separating at least one gas from a gas mixture, characterized in that the membrane comprises a thin discriminating layer of polycarbonate of the formula: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine; R¹ is independently at each occurrence a divalent unsubstituted or halo-substituted C₁₋₂₀ hydrocarbon; x is a positive real number of 0.05 to 1.0, y is a positive real number of 0 to 0.95, with the proviso that the ratio of ester to carbonate groups is between 50 to 0 percent; and n is a positive real number from 20 or greater. The invention further relates to a method of separating gases comprising (a) contacting a feed gas mixture under pressure with one side of a semi-permeable membrane comprising a thin discriminating layer of polycarbonate or polyestercarbonate, and the diphenolic residue in the polymer backbone is based on a bisphenol; (b) maintaining a pressure differential across the membrane under conditions such that a component of the feed gas selectively permeates through the membrane from the high pressure side to the low pressure side of the membrane; (c) removing the permeated gas which is enriched in the faster permeating component from the low pressure side of the membrane; and (d) removing the nonpermeated gas which is depleted in the faster permeating component from the high pressure side of the membrane. According to the method of the invention the membrane comprises a thin discriminating layer of polyestercarbonate of the formula: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine, R¹ is independently at each occurrence a divalent unsubstituted or halo-substituted C₁₋₂₀ hydrocarbon; x is a positive real number of 0.05 to 1.0, y is a positive real number of 0 to of 0.95, with the proviso that the ratio of ester to carbonate groups is 50 to 0 percent; and n is a positive real number of 20 or greater. The membranes of this invention possess high selectivities for oxygen/nitrogen separation and carbon dioxide/methane separation. The membranes of this invention also possess good mechanical properties so as to enable operation of the membranes at high temperatures and pressures. The gas separation membranes of this invention are prepared from polycarbonates or polyestercarbonates, wherein the diphenolic residue in the polymer backbone is based on bisphenol AF. Polyestercarbonates contain both ester and carbonate linkages as functional groups in the polymer backbone. The polyestercarbonates of this invention are randomized copolymers, in which the ester and carbonate functional groups occur in a random arrangement along the polymer backbone. The polycarbonates or polyestercarbonates used in the invention preferably correspond to Formula 1: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine; R¹ is independently at each occurrence divalent unsubstituted or halo-substituted C₁₋₂₀ hydrocarbon; x is a positive real number of 0.05 to 1.0, y is a positive real number of 0 to of 0.95, with the proviso that the ratio of ester to carbonate groups is 50 to 0 percent; and n is a positive real number of 20 or greater. In Formula 1, R¹ is preferably a divalent unsubstituted or halo-substituted C₁₋₁₈ aliphatic, a divalent unsubstituted or halo-substituted C₅₋₂₀ cycloaliphatic, or a divalent unsubstituted or halo-substituted C₆₋₂₀ aromatic. More preferably, R¹ is described by Formulas 2-5: wherein: R³ is independently in each occurrence a halogen, an unsubstituted or halo-substituted C₁₋₄ alkyl, or phenyl; and m is independently in each occurrence a positive integer from 0 to 4. R⁴ is a C₁₋₆ divalent unsubstituted or halo-substituted alkyl. Most preferably, R¹ is described by Formula 3: In Formula 1, x is preferably 0.67 to 1.0, more preferably 0.75 to 1.0. y is preferably 0 to 0.33, more preferably 0 to 0.25. The ratio of ester to carbonate groups in the polyestercarbonates is preferably 50 to 0 percent, more preferably 40 to 0 percent. n preferably is 20 or greater, more preferably 50 or greater. The polycarbonates and polyestercarbonates useful in this invention are prepared from bisphenol AF, that is 1,1,1,3,3,3-hexafluoro-2,2-bis-(4-hydroxyphenyl)propane, or its substituted derivatives, which correspond to Formula 7: wherein R is independently in each occurrence hydrogen, chlorine or fluorine. The manufacture of bisphenol AF and its derivatives is known in the art. See U.S. Patents 4,358,624 and 4,649,207. The polycarbonates useful in this invention may be prepared by any process known in the art which results in polycarbonates with suitable membrane formation properties. For example, polycarbonates may be produced by the reaction of phosgene and the appropriate bisphenol in the presence of an HCl acceptor such as pyridine. Polycarbonates may also be prepared by a transesterification reaction between the appropriate bisphenol and a carbonate ester such as diphenyl carbonate. See Kirk-Othmer Encyclopedia of Chemical Technology , 3rd edition, John Wiley & Sons, New York, 1982, Vol. 18, pp. 479-494 and Ferdinand Rodriguez, Principles of Polymer Systems , 2nd edition, Hemisphere Publishing Corporation, McGraw-Hill Book Company, 1982, pp. 433-436. The polyestercarbonates useful in this invention may be prepared by reacting the appropriate bisphenol with a difunctional ester forming agent in the presence of phosgene. Preferred ester forming agents are dicarboxylic acids or dicarboxylic acid halides such as C₁₋₂₀ hydrocarbons substituted with two carboxylic acid or carboxylic acid halide moieties. More preferred dicarboxylic acids or dicarboxylic acid halides include C₁₋₂₀ aliphatic dicarboxylic acids, C₁₋₂₀ aliphatic dicarboxylic acid halides, C₅₋₂₀ cycloaliphatic carboxylic acids, C₅₋₂₀ cycloaliphatic carboxylic acid halides, C₆₋₂₀ aromatic carboxylic acids and C₆₋₂₀ aromatic carboxylic acid halides. The most preferred class of ester forming agents is the dicarboxylic acid halides. Preferred dicarboxylic acid halides include those corresponding to Formulas 8-11: wherein X is a halogen and R³ and m are as previously defined. Preferred dicarboxylic acid halides useful in this invention include 1,4-cyclohexane dicarboxylic acid chloride, 1,4-cyclohexane dicarboxylic acid bromide, 1,3-cyclohexane dicarboxylic acid chloride, or 1,3-cyclohexane dicarboxylic acid bromide, terephthaloyl chloride, terephthaloyl bromide, isophthaloyl chloride, isophthaloyl bromide, 2,6-naphthylene dicarboxylic acid chloride, or 2,6-naphthylene dicarboxylic acid bromide. The more preferred class of dicarboxylic acid halides is the dicarboxylic acid chlorides. Preferred acid chlorides are terephthaloyl chloride, isophthaloyl chloride, 1,4-cyclohexane dicarboxylic acid chloride, and 2,6-naphthylene dicarboxylic acid chloride. The most preferred dicarboxylic acid chlorides are terephthaloyl chloride, isophthaloyl chloride, or mixtures thereof. In a preferred embodiment in which a mixture of terephthaloyl chloride and isophthaloyl chloride is used as the ester forming agent, the ratio of terephthaloyl chloride to isophthaloyl chloride may be 100:0 to 0:100, preferably 80:20 to 20:80. Generally a chain stopping agent is added to the reaction mixture to control molecular weight and viscosity. The molecular weight of the polymers useful in this invention is preferably greater than 7,500, more preferably greater than 10,500. The inherent viscosity of the polymers useful in this invention is preferably 0.2 to 1.5, more preferably 0.25 to 0.80. The polyestercarbonates of this invention may be prepared by techniques known in the art. The solution process is one preferred process for the manufacture of the polyestercarbonates which are the subject of this invention. In the solution process, the bisphenol in a chlorinated solvent in the presence of a tertiary amine acid acceptor is contacted with a dicarboxylic acid or acid chloride in the presence of phosgene with agitation. See U.S. Patent 3,028,365; 4,194,038; and 4,310,652. See also P. W. Morgan, Condensation Polymers: By Interfacial and Solution Methods , Interscience, 1965, pages 325-393. In another preferred process for preparing polyestercarbonates, the interfacial process, an aqueous bisphenolate solution with a pH of at least 8 is mixed with phosgene and an organic solution of an acid halide which solution is immiscible with the aqueous bisphenolate solution. Said components are agitated for a sufficient time at a temperature so as to react the phosgene and the acid halide with the bisphenolate to form an amorphous polymer. The aqueous phase containing the amorphous polymer is separated from the organic phase. The organic phase is then washed with an aqueous liquid. An amorphous, melt-processable polyestercarbonate polymer is recovered from the washed organic phase. The organic phase may be based upon any conventional organic solvent for the product polymer. A preferred group of solvents includes chlorinated aliphatic C₁₋₄ hydrocarbons such as methylene chloride, dichloromethane, chloroform, carbon tetrachloride, dichloroethane, trichloroethane, trichloroethylene, tetrachloroethylene, and mixtures thereof. Another preferred group of solvents includes chlorinated and non-halogenated aromatic hydrocarbons such as toluene, chlorobenzene, dichlorobenzene, and mixtures thereof. Preferred solvents are the chloromethanes, especially dichloromethane. The bisphenols useful in this invention are converted to bisphenolates by dissolving the bisphenol in water with an inorganic base, especially in an aqueous alkali metal or alkaline earth metal hydroxide, preferably an alkali metal hydroxide, and more preferably sodium hydroxide. Further descriptions of the interfacial processes can be found in U.S. Patents 3,169,121; 3,030,331; 3,028,364; 4,137,128; 4,156,069; 3,207,814; 4,255,556; and 4,311,822. See also P. W. Morgan, supra. The ratio of acid halide to phosgene generally controls the relative ratio of ester to carbonate units, with a higher ratio of acid halides resulting in a higher ester content and a lower ratio of acid halides resulting in a lower ester content. Generally, the molar ratio of phosgene to acid halide or carboxylic acid is 0.02:1 to 20:1. The membranes of this invention may be homogenous, composite, or asymmetric membranes. Preferably, the membranes of this invention are asymmetric or composite. In addition, the membranes may be shaped in the form of flat sheets, hollow fibers, or hollow tubes. Homogeneous membranes are prepared by forming a thin discriminating layer which is dense and free of voids and pores. Such membranes generally have the same structure and composition throughout the membrane. In one preferred embodiment, the polycarbonate and polyestercarbonates of this invention are dissolved in a water-miscible solvent, for example, dimethylformamide or dimethylacetamide. Additional solvents suitable for forming membranes include chlorinated hydrocarbons such as methylene chloride, chloroform, trichloroethane, trichloroethylene, tetrachloroethylene, and the like. The configuration into which the membrane is to be formed determines the membrane solution composition. To form a flat sheet membrane, a solution with 10 to 20 weight percent of polymer is preferred, with 15 to 20 weight percent of polymer being more preferred. To form a hollow fiber membrane, a solution with 30 to 80 weight percent polymer is preferred, with 50 to 80 weight percent of polymer being more preferred. The polymer solution should be homogeneous and possess sufficient viscosity to allow casting of the solution onto a flat surface. The casting surface is such that the finished membrane may thereafter be readily separated. One way of carrying out this operation is by casting the polymer solution onto a support surface which may be dissolved away from the finished membrane following drying and curing. Alternately, the membrane may be cast onto a support having a low surface energy, such as silicone coated glass, or a surface to which the membrane will not adhere, such as mercury. Casting is performed by pouring the solution onto the appropriate surface and drawing down the polymer solution using an appropriate tool to form a solution layer of the appropriate thickness. Thereafter, the cast solution is exposed to drying or curing conditions. Such conditions are used to remove the solvent, thereby leaving a thin discriminating layer of polymer which is homogeneous, The solution may be dried by exposing the solution to a vacuum, exposing the solution to elevated temperatures, allowing the solvent to evaporate from the solution over time, or a combination thereof. Generally, it is preferable to expose the cast solution to elevated temperatures. Any temperature at which the solvent evaporates in a reasonable period of time and below the glass transition temperature is suitable, preferably less than 100 degrees Celsius, more preferably less than 80 degrees Celsius. In one preferred embodiment, such exposure is done under vacuum at elevated temperature. This drying is performed over a period sufficient to remove the solvent, preferably between 24 to 48 hours. Homogeneous polycarbonate and polyestercarbonate membranes may alternately be formed by the melt extrusion process. The polymers may be extruded and drawn down into films using conventional extrusion equipment. Typically, the polymers of this invention may be extruded at temperatures of 220 to 300°C. In a composite membrane, the thin discriminating layer of the membrane is supported on a porous substructure or substrate, The porous substrate generally does not greatly impede the transport of components through the membrane. To prepare a composite membrane, a homogeneous, thin discriminating layer can be formed and thereafter adhered to a porous support after formation. Alternatively, the porous support can be the surface upon which the membrane is cast or laminated. In one embodiment, the composite membrane is prepared by casting or laminating a forming solution as a uniform coating on the porous support which forms the support layer for the finished membrane. Penetration of the polymer into pores of the porous support layer is operable so long as the desired thickness of the semi-permeable membrane is not exceeded. In one embodiment, the support layer may be a metal or polymeric plate with a plurality of holes drilled into it. However, such a drill plate is not advantageous because it can significantly reduce the effective surface area of the membrane. In a preferred embodiment, the porous support layer is a very porous polymer membrane. Illustrative of such polymeric support layers are porous cellulose ester and microporous polysulfone membranes. Such membranes are commercially available under the tradenames MILLIPORE, PELLICON, and DIAFLOW. Where such support membranes are thin or highly deformable, a screen or other support frame may also be necessary to adequately support the semi-permeable membrane. In one especially preferred embodiment, the polymeric support layer is in the form of a hollow fiber of a microporous polymer such as cellulose ester or polysulfone. The hollow fiber itself provides adequate support for the thin discriminating layer coated on the inside or the outside of the hollow fiber. After the thin discriminating layer is coated onto the porous support, the composite membrane is exposed to conditions for removal of the solvent so as to form the dense skin. Such conditions are similar to those hereinbefore described for the formation of homogenous membranes. To form an asymmetric membrane, a solution is cast as hereinbefore described, and thereafter the cast solution is partially cured to remove a portion of the solvent. Thereafter, one or both surfaces of the partially dried membrane is contacted with a quench liquid such as water so as to form a thin discriminating layer on one or both sides of the membrane, under conditions such that the solvent away from the dense layer communicates to the dense layer forming pores in the remainder of the membrane, thereby forming an asymmetric membrane. Such porous layer is present to provide support for the thin discriminating layer without impeding the transport of the fluid containing the components to be separated by the semi-permeable, thin discriminating layer. The partial curing step is performed in a manner similar to the curing step described with respect to the formation of homogeneous membranes. Hollow fiber membranes can be formed by spinning fibers from an appropriate solution of the polycarbonate or polyestercarbonate in a water-miscible solvent or by melt extrusion. Such spinning processes are well known to those skilled in the art, and the formation of homogeneous, asymmetric, or composite membranes requires the adaptation of the hereinbefore described procedures to the hollow fiber membrane form. Such adaptations are well within the skill of the art. The membranes used in the invention are relatively thin. The thickness of such homogeneous membranes is preferably greater than 5 µm and less than 500 µm. More preferably, the membrane thickness for a homogeneous membrane is between 10 to 300 µm. In the case of composite or asymmetric membranes, the active discriminating layer thickness is preferably between 0.05 and 10 µm, more preferably between 0.05 and 5 µm. The membranes are fabricated into flat sheet, spiral, tubular, or hollow fiber devices by methods described in the art. The membranes are sealingly mounted in a pressure vessel in such a manner that the membrane separates the vessel into two fluid regions wherein fluid flow between the two regions is accomplished by fluid permeating through the membrane. For examples of conventional membrane device designs and fabrication methods see U.S. Patents 3,228,876; 3,433,008; 3,455,460; 3,475,331; 3,526,001; 3,538,553; 3,690,465; 3,702,658; 3,755,034; 3,801,401; 3,872,014; 3,966,616; 4,045,851; 4,061,574; 4,080,296; 4,083,780; 4,220,535; 4,235,723; 4,265,763; 4,430,219; 4,352,092; 4,337,139; and 4,315,819. The membranes are used to isolate or recover gases from gas mixtures, The feed gas mixture may contain gases such as hydrogen, helium, oxygen, nitrogen, carbon dioxide, methane, light hydrocarbons, and the like. One side of the membrane is contacted with a feed gas mixture under pressure, while a pressure differential is maintained across the membrane. At least one of the components in any given gas mixture selectively permeates through the membrane more rapidly than the other components. A stream is obtained on the low pressure side of the membrane which is enriched in the faster permeating components. The permeated gas is removed from the low pressure (downstream) side of the membrane. A stream depleted in the faster permeating gas is withdrawn from the high pressure (upstream) side of the membrane. The separation process should be carried out at pressures which do not adversely affect the membrane. In the case where oxygen is separated from nitrogen, the pressure differential across the membrane is preferably 69-2412 Pa gauge (10 to 350 psig), more preferably between 345-1723 Pa gauge (50 and 250 psig). In the case where carbon dioxide is separated from methane, the pressure differential across the membrane is preferably between 345-6895 Pa gauge (50 and 1000 psig), more preferably between 345-3448 Pa gauge (50 and 500 psig). The separation process should be carried out at temperatures which do not adversely affect membrane integrity. Under continuous operation, the operating temperature is preferably 0 to 100 degrees Celsius, more preferably 0 to 50 degrees Celsius. Gas permeability is defined as A standard permeability measurement unit is the barrer, which is abbreviated hereinafter as The reduced flux is defined as (permeability)/(membrane thickness). A standard reduced flux unit is hereinafter abbreviated as The separation factor (selectivity) is defined as the ratio of the permeability of the faster permeating gas to the permeability of the slower permeating gas. In the embodiment where oxygen is separated from nitrogen, the membrane preferably has a separation factor for oxygen/nitrogen at about 25 degrees Celsius of 3.5 or greater, more preferably 4.0 or greater. The permeability of oxygen at 25 degrees Celsius is preferably 2.0 Barrers or greater, more preferably of 2.5 Barrers or greater. The reduced flux of oxygen at about 25 degrees Celsius is preferably more preferably In the embodiment where carbon dioxide is separated from methane, the membrane preferably has a separation factor for carbon dioxide/methane at about 25 degrees Celsius of at least 16, more preferably of at least 21. The permeability of carbon dioxide at about 25 degrees Celsius is at least 9 Barrers, more preferably at least 12 Barrers. The reduced flux of carbon dioxide at about 25 degrees Celsius is preferably more preferably The following examples are included to illustrate the invention and are not intended to limit the scope of the invention or claims. Example 1 - Bisphenol AF Based Polycarbonate Polymerization A three neck, 2.0 liter round bottom flask, equipped with a thermometer, stirrer, and glass funnel, is charged with 1.2 liters of methylene chloride, 185.6 grams (0.55 moles) of 1,1,1,3,3,3-hexafluoro-2,2-bis-(4-hydroxy phenyl)propane (bisphenol AF), and 116.8 cc (1.44 moles) of pyridine. The resultant clear, pale pink solution is stirred under a nitrogen atmosphere for 10 minutes. Moderate stirring is continued while a total of 68 grams (0.69 moles) of phosgene is bubbled into the solution over a period of 41 minutes. The creamy, pale yellow solution is then scavenged with methanol, neutralized with dilute hydrochloric acid, and washed a second time with dilute hydrochloric acid. The colorless, slightly hazy solution is clarified by passing it through an MSC resin bed, further diluted with methylene chloride, and precipitated in 4 volumes of n-heptane. The precipitated polymer is dried under vacuum at 80 degrees Celsius for 48 hours. The resultant polymer has an inherent viscosity of 0.67 dL/g at 25 degrees Celsius in methylene chloride. Film Preparation and Testing 2 grams of dried polymer are dissolved in 18 grams of methylene chloride to form a casting solution. The casting solution is passed through a fritted glass filter onto a clean glass plate and drawn down with a casting blade. The film is covered until dry, removed from the glass plate, and annealed under vacuum at 80 degrees Celsius for 48 hours. From the cast film, a small disc is cut to provide a sample for gas permeability evaluation. The mean thickness and standard deviation are determined and the sample is placed in a gas permeation test cell of a fixed volume-variable pressure gas permeability test apparatus. Both sides of the membrane are evacuated overnight. One side of the membrane is then pressurized with oxygen at 150 kPaG and the downstream pressure increase is monitored with a pressure transducer and recorded on a single-pen recorder. Gas permeability coefficients and standard deviation are calculated from the slope of the time-pressure curve. The same procedure is followed for each of the following gases: nitrogen, methane, helium, and carbon dioxide. The results are listed in Tables IA, IB, and II. Example 2 - Bisphenol AF Based Polyestercarbonate The polymerization step is similar to that of Example 1, except that 50 percent of the phosgene (0.345 moles) is replaced with an 80:20 mixture of terephthaloyl chloride:isophthaloyl chloride. A film is prepared in a manner similar to that described in Example 1 and gas permeabilities are determined for oxygen, nitrogen, methane, helium, and carbon dioxide. Results are listed in Tables IA, IB, and II. Example 3 - Bisphenol A Based Polycarbonate This Example does not illustrate the invention but is meant to compare the gas separation performance of bisphenol AF polycarbonates with that of bisphenol A polycarbonates. The procedure of Example 1 is used except that bisphenol A is used in place of the 1,1,1,3,3,3-hexafluoro-2,2-bis(4-hydroxy phenyl)propane (bisphenol AF). The results of gas permeability measurements for oxygen, nitrogen, methane, and carbon dioxide are listed in Tables IA, IB, and II. Example 4 - Bisphenol A Based Polyestercarbonate This Example does not illustrate the invention but is meant to compare the gas separation performance of bisphenol AF polyestercarbonates with that of bisphenol A polyestercarbonates. The procedure of Example 2 is used except that bisphenol A is used in place of the 1,1,1,3,3,3-hexafluoro-2,2-bis(4-hydroxyphenyl)propane (bisphenol AF). The results of gas permeability measurements for oxygen and nitrogen are listed in Tables IA, IB, and II. GAS PERMEABILITIES Example Membrane Thickness cm x 10⁻³ (mils) Oxygen Nitrogen Methane Carbon Dioxide Helium 1 5.33 (2.10) 3.37 0.69 0.51 14.2 31.9 2 4.88 (1.92) 3.96 0.95 0.77 17.7 31.4 3 13.06 (5.14) 1.06 0.20 0.23 5.54 -- 4 5.18 (2.04) 1.16 0.26 - - - Reduced flux values in units of SEPARATION FACTORS Example O₂/N₂ CO₂/CH₄ He/CH₄ 1 4.9 27.8 62.3 2 4.2 23.0 41.0 3 5.3 24.1 - 4 4.6 - -

Claims: A gas separation membrane comprising a thin discriminating layer of polycarbonate or polyestercarbonate, and a diphenolic residue in the polymer backbone based on a bisphenol , wherein the gas separation membrane functions as a semi-permeable membrane capable of separating at least one gas from a gas mixture, characterized in that the membrane comprises a thin discriminating layer of polycarbonate of the formula: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine; R¹ is independently at each occurrence a divalent unsubstituted or halo-substituted C₁₋₂₀ hydrocarbon; x is a positive real number of 0.05 to 1.0, y is a positive real number of 0 to 0.95, with the proviso that the ratio of ester to carbonate groups is between 50 to 0 percent; and n is a positive real number from 20 or greater. The membrane of Claim 1, wherein R¹ is wherein: R³ is independently in each occurrence a halogen, an unsubstituted or halo-substituted C₁₋₄ alkyl, or phenyl; m is independently in each occurrence a positive integer from 0 to 4; and R⁴ is a C₁₋₆ divalent unsubstituted or halo-substituted alkyl. The membrane of Claim 2, wherein the polyestercarbonate is derived from bisphenol AF and terephthaloyl chloride, isophthaloyl chloride or a mixture of terephthaloyl chloride and isophthaloyl chloride. The membrane of Claim 1, wherein the membrane comprises a thin discriminating layer of polycarbonate of the formula: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine; n is a positive real number of 20 or greater. The membrane of Claims 1, 2, 3 or 4, wherein the separation factor for oxygen/nitrogen is 3.5 or greater at 25 degrees Celsius. The membrane of Claims 1, 2, 3 or 4, wherein the separation factor for carbon dioxide/methane is 16 or greater at 25 degrees Celsius. The membrane of Claims 1, 2, 3 or 4, wherein R is fluorine. A method of separating gases comprising (a) contacting a feed gas mixture under pressure with one side of a semi-permeable membrane comprising a thin discriminating layer of polycarbonate or polyestercarbonate and a diphenolic residue in the polymer backbone as defined in claim 1; (b) maintaining a pressure differential across the membrane such that a component of the feed gas selectively permeates through the membrane from the high pressure side of the membrane; (c) removing the permeated gas which is enriched in the faster permeating component from the low pressure side of the membrane; and d) removing the nonpermeated gas which is depleted in the faster permeating component from the high pressure side of the membrane characterized in that the membrane comprises a thin discriminating layer of polyestercarbonate of the formula: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine; R¹ is independently at each occurrence a divalent unsubstituted or halo-substituted C₁₋₂₀ hydrocarbon; x is a positive real number of 0.05 to 1.0, y is a positive real number of 0 to of 0.95, with the proviso that the ratio of ester to carbonate groups is 50 to 0 percent; and n is a positive real number of 20 or greater. The method of Claim 8, wherein R¹ is wherein: R³ is independently at each occurrence halogen, unsubstituted or halo-substituted C₁₋₄ alkyl, or phenyl; m is independently at each occurrence a positive integer from 0 to 4; and R⁴ is a C₁₋₆ divalent unsubstituted or halosubstituted alkyl. The method of Claim 8, wherein the polyestercarbonate is derived from bisphenol AF and terephthaloyl chloride, isophthaloyl chloride, or a mixture of terephthaloyl chloride and isophthaloyl chloride. The method of Claim 8, wherein the membrane is comprised of a thin discriminating layer of polycarbonate corresponding to the formula: wherein: R is independently at each occurrence hydrogen, chlorine or fluorine; and n is a positive real number of 20 or greater. The method of Claim 8 or 11 wherein R is fluorine. The method of Claims 8 or 11 wherein the feed gas mixture contains at least one gaseous component of hydrogen, helium, oxygen, or light hydrocarbons. The method of Claim 13, wherein the separation factor for oxygen/nitrogen is 3.5 or greater. The method of Claim 13, wherein the separation factor for carbon dioxide/methane is 16 or greater.

Inventors: JEANES, THOMAS O.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1988
Main classification: B01D71
IPC codes: D01F6, B01D71, D01D5, C08G64, C08G63