PROCESS FOR THE DETOXIFICATION OF STEEL PLANT WASTES

Abstract: A technique for rendering toxic metals (chromium, lead, cadmium and arsenic) contained in steel plant furnace dust innocuous and suitable for burial with minimal adverse environmental impact. Pelletized iron oxide containing dust is introduced into a rotary hearth furnace under a reducing atmosphere in excess of 600°C. The higher iron oxides are reduced to FeO which in turn complexes with the toxic metals to form relatively benign products.

Description: TECHNICAL FIELD The instant invention relates to pollution control in general and, more particularly, to a technique for the economical and safe treatment and disposal of noxious steel plant dust. BACKGROUND ART The dust produced as a result of electric furnace steel making processes has been classified by the United States Environmental Protection Agency as "Hazardous Waste". Accordingly, this material must be manifested for transport and disposed only in a limited number of licensed hazardous waste disposal sites. This is costly, currently in excess of 100/ton. As the number of available sites diminishes, clearly the disposal costs will inexorably rise. Unfortunately, proposed alternatives are generally impractical. The world alloy steel business is based upon electric arc furnace melting, with the inevitable production of fume. To add insult to injury, the ingredient value of the fume is usually so low as to preclude economic recovery of materials entrained in the fume. Typical dust arising from the production of alloy steel has the following representative composition (in weight percent): Fe - 25.0-35.0 Ni - 0.5- 1.5 Cr - 0.5- 2.0 Mn - 2.0- 4.0 Zn - 4.0-10.0 Pb - 1.0- 5.0 Cd - 0.1- 1.0 Al₂O₃ - 0.5- 2.5 CaO - 3.0-12.0 SiO₂ - 3.0-15.0 MgO - 1.0- 5.0 Dust from the increasingly popular mini-mills is similar but usually contains even lower levels of nickel and chromium and higher zinc - up to 30% zinc. The hazardous nature of electric furnace oxide fume is caused by the generation of soluble oxides of Pb, Cd, As and Cr⁶⁺ formed at high temperatures above the steel bath and in the off-gas system of the electric arc furnace. After the dust is disposed in landfills, the soluble oxides find their way into the water table causing pollution. The Environmental Protection Agency (EPA) has specified a toxicity test using an accelerated leach with diluted acetic acid. Toxicity is then determined as milligrams of listed metals per liter of leachate. Current listed metals and their test limits are given below: Chromium - 5 mg/l Lead - 5 mg/l Cadmium - 1 mg/l Arsenic - 5 mg/l The potentially valuable elements in the dust such as nickel, chromium, zinc and iron are present at levels lower than those of the unimportant materials and cannot currently be recovered economically. In particular there are a number of techniques that may be used to recover selected components. For example, the SKF Plasmadust™ process is designed to recover zinc. However, it does not appear to be economically viable since high zinc dust generators are widely separated and the current processing and shipping costs of the recovered zinc vis-a-vis the current cost of zinc is not attractive. Another recovery alternative is taught by U.S. Patent 3,836,353. Iron and oxide impurities are recovered by the volatilization of zinc, lead and sulfur impurities and the subsequent formation of iron oxide containing pellets in a rotary hearth furnace. Iron oxide prices are similarly depressed. From the foregoing, it appears that a low cost process to render these listed wastes harmless and simply return them safely to the earth from whence they came and without the concern for element recovery is desirable. SUMMARY OF THE INVENTION Accordingly, there is provided an economical technique for the formation of stable complex compounds between the oxides of the toxic elements present in the flue dust and the lower oxides of iron (FeO). By forming these complexes, the toxic elements are rendered relatively innocuous and may be cheaply returned to the earth essentially in the form they were first removed. These insoluble compounds may be formed by heating the pelletized dust above 600°C under a reducing atmosphere in a rotary hearth furnace. According to the invention a process of detoxifying steel plant wastes containing iron oxides and toxic metals comprises the steps set out in claim 1. PREFERRED MODE FOR CARRYING OUT THE INVENTION The basis of the process is the formation of stable and insoluble complex compounds between the oxides of the toxic elements present in the dust and the lower (valence) oxide of iron (FeO). In an embodiment of the invention these compounds may be formed in alloy steel melting dust by heating the materials in a rotary hearth furnace above about 600°C under a reducing atmosphere preferably equivalent to about 50% CO and 50% CO₂ in order to form ferrous oxide (FeO) from the hematite (ferric oxide - Fe₂O₃) and magnetite (Fe₃O₄) generally present in the dust. Electric arc furnace dust removed from bag houses, electrostatic precipitators and the like may be pelletized by any method known to those in art. Analysis of the dust must be undertaken to determine whether sufficient quantities of carbon and iron are present. The carbon addition, if any, must match the zinc and toxic metal contents. Carbon may be added as coke breeze, coal dust, charcoal or any other suitable carbon source. Similarly, if the dust does not contain sufficient iron to form FeO, suitable iron sources such as mill scale, iron ore, etc. may be tapped. After the dust has been augmented, if necessary, with carbon and iron and pelletized, it is preferably introduced into a rotary hearth furnace ("RHF") at temperatures ranging between about 600°C-1100°C for about eight to twenty minutes. An RHF is a continuous reheating furnace generally having a circular inner wall circumscribed by a spaced outer wall. The void formed therebetween includes an annular rotating hearth. In order to retain the heat generated within the furnace, the walls are relatively low so as to enable the roof to be close to the hearth. Burners, instrumentation, temperature regulators, etc. are disposed within the furnace. Material, in this case the pellets, is usually loaded (dropped) onto the rotating hearth by a conveyor or chute. The depth of material on the hearth may be controlled although it is typical to limit the depth of the material to allow maximum heating and exposure to the predetermined furnace environment. Generally, after almost one complete rotation of the hearth the material is removed from the furnace by suitable means, such as a discharge screw. (See, for example, U.S. Patent No. 4,636,127.) Under the above-referenced preferred conditions, FeO rapidly forms from the hematite and magnetite and combines with the PbO, ZnO and Cr₂O₃ present in the pellets to form FeO·PbO, FeO·ZnO, 2FeO·Cr₂O₃ (ferrites and chromites respectively) and an FeAs spinel. The resultant iron complex products are stable and insoluble. The discharge product may be removed from the RHF, air cooled and disposed of in a landfill after the appropriate EPA delisting procedures have been followed. It should be appreciated that instead of being left with toxic materials or conducting numerous relatively expensive steps to recover economically dubious materials, the benign products of iron complexes are very similar to the original components first going into metal making process. For example, the resultant zinc ferrite is now nothing more than the franklinite that originally was used in the production of zinc. In essence, the instant process simply returns the bad actor metals to their originally occurring state as found in the earth. EXAMPLE Twenty tons (1.8 x 10⁴ kg) of alloy steel melt shop baghouse dust were obtained with the following composition (weight percent): C - 1.2 Fe - 31.5 S .27 Al₂O₃ - 1.0 SiO₂ - 10.7 CaO - 7.2 MgO - 7.4 Pb - 1.3 Cd - .04 Zn - 6.8 As - .2 The EPA leachate test showed the following composition: Cr - .2 mg/l Pb - 9 mg/l Cd - 13 mg/l As - 4 mg/l Two ten ton (9.1 x 10³ kg) tests were performed on the dust. Test 1 received a 5% coke breeze addition (4% carbon addition) and Test 2 received a 10% coke breeze addition (8% carbon addition). Coke breeze usually contains about 80% carbon and 20% ash. Pellets were made up and processed in the RHF for fifteen minutes at a temperature of 850°C. The furnace environment was maintained at 50% CO and 50% CO₂. Samples from both tests were treated under the EPA toxicity test with the following results (mg/l): Test 1 (4% C Added) Test 2 (8% C Added) Cr 2.3 0.04 Pb 7.7 0.2 Cd .2 0.06 As .1 0.05 Test 1 showed only a slight improvement in leach test results compared to the raw feed materials, whereas Test 2 gave results considerably below the toxicity limits. The reason was that Test 1 had insufficient carbon present to provide enough FeO for complete reaction with the toxic oxides. Zinc oxide appears to react preferentially with FeO so it appears that there was enough of the FeO present to satisfy the zinc ferrite formation in addition to reacting with the toxic components. Inasmuch as a critical feature of the instant process is the formation of the proper quantity of FeO, analysis should be undertaken to ensure that the dust mixture contains the proper stochiometric amount of carbon and iron to form the desired end product complexes. This calculation is, of course, a function of the quantity of heavy metals present and the inherent levels of iron and carbon in the dust and may be computed by methods known to those skilled in the art.

Claims: A method of detoxifying steel plant wastes containing iron oxides and toxic metals which comprises collecting the wastes in dust form, adjusting the quantities of carbon and iron in the dust in accordance with its analysis, solidifying the dust and exposing the solidified dust to a reducing environment and heat in excess of 600°C, so that a sufficient amount of FeO is generated from the solidified dust and reacts to form stable, insoluble complexes with the toxic metals therein, thereby generating a detoxified product. A method according to claim 1 wherein the dust is pelletized. A method according to claim 1 or claim 2 wherein the solidified dust is heated in a rotary hearth furnace. A method according to any preceding claim wherein the toxic metals include one or more of chromium, lead, cadmium and arsenic. A method according to any preceding claim wherein the dust also includes zinc and the amount of FeO generated is sufficient to react with the zinc as well as with the toxic metals present. A method according to any preceding claim wherein FeO is generated by reduction of Fe₂O₃ and Fe₃O₄ present in the solidified dust. A method according to any preceding claim wherein ferrites and chromites are generated. A method according to any preceding claim wherein additional carbon is added to the dust. A method according to any preceding claim wherein additional iron is added to the dust. A method according to any preceding claim wherein the process is conducted within a temperature range of about 600°C to 1100°C. A method according to any preceding claim wherein the heating and reducing process is conducted for about eight to twenty minutes. A method according to any preceding claim wherein iron-arsenic compounds are generated. A method according to any preceding claim wherein the reducing environment includes about 50% CO and about 50% CO₂. A method according to any preceding claim wherein the detoxified product is disposed of by introducing it into the ground.

Inventors: PARGETER, JOHN KENNETH
Applicants: THE INTERNATIONAL METALS RECLAMATION COMPANY INC.
Application year: 1988
Main classification: C22B7
IPC codes: B09B3, A62D101, C21B3, C22B7, C21B13, A62D3, B09B5