METHOD FOR PRODUCING OF CONCRETE WITH VARIABLE DENSITY

Abstract: The invention concerns a method for producing a concrete with variable density, particularly within the range 800-2000 kg/m<3>, by mixing a conventional concrete mass with a porousity agent, consisting of water, cement and a foaming agent. The finished concrete is including a large number of smaller pores. The strength of the concrete can, if desired, be kept high, e.g. at least 12 MPa, at the density 1600 kg/m<3>.

Description: METHOD FOR PRODUCING OF CONCRETE WITH VARIABLE DENSITY The present invention concerns a method for pro¬ ducing concrete with variable density, particularly with- in the range of 800-2000 kg/m 3 , where also the compres¬ sion strength can be kept high, e.g. more than 12 MPa at a density of 1600 kg/m 3 . It has proved to be that production of concrete mass preferably is made at stationary concrete stations and that the concrete mass is moulded in situ in moulds to transportable units or is transported to the building place in a liquid shape to be moulded and hardened in moulds. The advantages are several. Among others can be mentioned: 1. A stationary equipment can be made more technically complete. 2. The capacity can be made bigger for a stationary plant. 3. The access to laboratory equipment for testing of used materials and the finished product makes the concrete to be produced with a higher accuracy. 4. The working place does not need to be saddled with concrete mixer, stores of cement and ballast and so on. Therefore most industrial countries on the whole have complete concrete stations for delivery of concrete mass to the working places. The concrete with the greatest range of appli¬ cation to day concists of a mixture of cement, ballast and water and often some additives for changing of the consistence and so on. The ballast is constituted by sand, gravel and stone and the density of the stabilized concrete normally is about 2300 kg/m 3 . The strength re¬ quirements can vary. The test method for the compression strength has been standardized and is carried out in the way that a cube is moulded with a side of 150 mm with certain requirements of side-parallelism and angel-accu¬ racy. After hardening of the cube at a room temperature of 20°C a varying number of days, in most cases 8 and 28 days, the cube will be tested by pressing between flat surfaces and the highest load is registrated before the cube starts cracking. A value of the compression strength around 60 MPa can be achieved under certain circumstan¬ ces, but maximum values of about 40 MPa are most common. For structures with lower requirements the con¬ crete price can be cheapened particularly by increasing the rate of weight between participating water and cement in the concrete mass, the so called water cement factor. This is used to be indicated vet. More and more demands have been raised for the density to be varied among others to get light struc¬ tures, and not only by increasing the volume of the structures. The whole range of densities, from the pre¬ sent of about 2400 kg/m 3 at conventional ballast materi¬ al, and lower is interesting, and as very interesting a density of 1600 kg/m 3 seems to be at present. However compression strength of at least 12 MPa will be achieved at this density with god reproducing. This lowering of the density has proved to be difficult to obtain even without setting requirements of compression strength of at least 12 MPa with acceptable reproducing. This will preferably be valid in the density range of 2000-800 kg/m 3 . Blowing air into the liquid concrete mass to get air porousities in the concrete occurs, making the con¬ crete less affected by frost, among others in bridges and outdoor-balconies. Injection of air also is made to lower the density. However the compression strength will be dramatically lowered and the porousities are so irregu ¬ larly spread that already at a density of 2000 kg/m 3 the method is debatable. Also mixing with lighter ballast to lower the density is tested, but in this case no better results will be reached before a practical limit for the compres¬ sion strength will be reached. However it has been proved that a concrete with closed porousities, so called porous concrete with densi¬ ties below 500 kg/m 3 , can be achieved by adding a foaming agent, of trademarks present on the market, to water and after that adding a certain amount of cement. This porous concrete must be produced at the moulding place. Certain¬ ly it becomes low coefficients of thermal conductivity, which sometimes can be an advantage, but the value for compression strength hardly ever exceeds 1,5 MPa. In or- der to raise the density of the porous concrete more than 500 kg/m 3 a certain amount of ballast has been added, but this will settle already at 700 kg/m 3 and an unacceptable quality of the concrete will be obtained. The range of densities between 800 and 2000 kg/m 3 thus have been difficult to achieve industrially. Cement mixers intended for parts of this range certainly are present on the market, but they have shown many draw- -backs. The producing of the concrete mass is made in connection with the moulding place. Usually a mixture of cement, water and ballast first is produced in the ma¬ chine. Separately water and foaming agent are mixed up. After that this foam mixture are brought into an outlet pipe from the mixer. These two mixtures are jumbled care¬ fully and as soon as possible brought to the moulds. The method is complicated and an interruption, unforeseen or not, will make considerable extra job. Practically it also has shown that it hardly will be possible to reach a compression strength of 12 MPa and certainly not with an acceptable repeatability at e.g. a density of 1600 kg/m 3 , that density which to day is very coveted. This among others depending on that the water cement ratio (vet) is raised at adding of the mixture of water and foaming agent. Compensation of this by a low vet-factor in the first produced cement mixture does not work why this will be so viscous that the process is not possible to carry out. Surprisingly it has proved to be that a concrete with very good strength caracteristics also in the range 800-2000 kg/m 3 can be produced by adding a porousity agent made of water, cement and a foaming agent, to e.g. a conventionally produced liquid concrete mass, mixed up by cement, ballast and water, e.g. in a stationary con¬ crete station, and have these to mix well together. After moulding and hardening a concrete will be obtained inclu¬ ding small porousities and variable density depending of the mixing conditions. High values of compression strength also are obtained, probably depending on that the pores formed in the concrete are very small, mainly below 3 mm, and very equally distributed, and that the water cement ratio (vet) can be kept low as well in the concrete mass as in the porousity agent. The repeatabi- lity also has proved to be very high when standardizing the routines at the producing. The concrete mass neces¬ sary for the moulding can be calculated and produced complete on the concrete station if desirable, if the distance to the moulding place is not to large. Otherwise the standard concrete mass produced at the concrete sta¬ tion can be transported to the working place, mixed to¬ gether with the porousity agent and moulded. Mixing to¬ gether the standard concrete mass and the porousity agent is a simple operation. Tests show that the mixing of the porousity agent shall be made quickly. The producing of the porousity agent is carried out separately, as men¬ tioned above, in a simple, eventually transportable, mixer. The invention will be closer described in the enclosed claims and in the example below, where different concretes are produced with different density and diffe¬ rent routines. Data and results from the tests have been declarated in the table enclosed. Compression strength has been determined according to the Swedish standard SS 13 11 11 - 13 where cubes of 150 x 150 mm have been moul¬ ded and tested at a concrete station accepted by the Swedish authorities. Compression according to SS 13 11 12, 5.1 and 5.2 has been excluded in order not to disturb the distribution of the pores in the material. Also storing in water according to 5.6 in the same stan¬ dard has been excluded by the same reasons. Determination of density has been made on the same place according to SS 13 72 34. EXAMPLE 1. Specimen no 1-2. A normal concrete mass was produced in a labo¬ ratory scale in a simple mixer, aiming for a density of about 2200 kg/m 3 and a compression strength after 28 days hardening of about 0 MPa. The concrete mass was produced with vet = 0,45. Besides a smaller amount of porousity agent was produced. This was also made in a smaller mixer and was made in that way that water and a foaming agent of the trademark CELLEX was mixed with a smaller amount of chemicals for stabilization of the foam. After that cement powder was added during stirring so that vet = 48 was obtained. To 6 litre of the concrete mass 0,6 litre porousity agent was added during stirring. Test cubes was moulded from the concrete mass as well as from the latter mixture with the porousity agent jumbled. The cubes where tested at an accepted concrete station as well concerning the compression strength as density (after 8 and 28 days). The result showed that, within this coveted range of density, a concrete with a god compression strength was obtained already after 8 days hardening, which was further improved after 28 days hardening. The surfaces of fracture showed that small pours, none over 3 mm exten¬ sion could be seen, were equally distributed over the surface of fracture. EXAMPLE 2. Specimen no 3-4. The purpose was also here to get a concrete with a density of 1600 kg/m 3 . The base concrete mass however was produced in a conventional concrete mixer often used on the working places in order to produce smaller amounts of concrete mass. The porousity agent was added directly into the mixer during the rotation of the mixing container. At specimen 3 a delay in time more than 1 minute was made for the adding while at specimen 4 the porousity agent was added without delay. The same good result as in example 1 was obtained for specimen 4, i.e. when the porousity agent was mixed in quickly, but some inferior result was obtained for specimen 3 with a de¬ layed mixing. EXAMPLE 3. Specimen no 5-9. A series of test were carried out mainly on the same way as specimen 4 above, but in that case the mixing rates between the start concrete mass and the porousity agent was varied. As can be seen from the result a fi¬ nished concrete was obtained in the hard-mastered range of density between 2000 and 800 kg/m 3 with very god va- lues of compression strength which however naturally was lowered with lowering values of density. TABLE

Claims: CLAIMS 1. A method for producing a concrete with vari¬ able density, which at the density 1200 kg/m 3 has a com¬ pression strength of at least 3 > 5 MPa and after that a linear increasing to at least 19 MPa at 2000 kg/m 3 , c h a r a c t e r i z e d in mixing a concrete mass mainly concisting of cement, water and a porousity agent mainly concisting of cement, water and a foaming agent, and that the mixed mass after that is moulded in a con- ventional manner. 2. A method for producing a concrete according to the preceding claim, c h a r a c t e r i z e d in that the finished concrete becomes closed pores with a size which, with few exeptions, are below 3 mm.

Inventors: JOHANSSON INGEMAR, SVEDMAN KJELL, JOHANSSON, INGEMAR, SVEDMAN, KJELL
Applicants: DANES VERKSTAEDER AB
Application year: 1988
Main classification: C04B38
IPC codes: C04B38