Glazing units

Abstract: A double glazing unit (1) comprising an outer pane (2) of body coloured heat absorbing glass and an inner pane (3) of annealed glass with a coating (4) including a silver layer having a thickness in the range 15 nm to 40 nm on its face turned towards the outer pane.

Description: The invention relates to solar control coatings on glass and, in particular, to double glazing units incorporating highly reflecting solar control coatings of silver metal. The term 'solar control' is used to refer to coatings used on glass to reduce the amount of solar heat which enters buildings through the windows in order to avoid overheating within the building and/or reduce the load on air-conditioning plant cooling the building. A wide range of solar control coatings of different composition and thickness, to give a range of colours and performance, is commercially available. Typically, solar control coatings function by reflecting a proportion of solar heat incident upon them. They also cause the coated glass to absorb an increased proportion of the incident solar heat, and much of that absorbed solar heat is re-radiated towards the outside. Even glasses with coatings which are generally considered as highly reflecting, for example REFLECTAFLOAT (trade mark) glass from Pilkington Glass Limited, depend heavily for their performance on the absorption of solar heat. As a result of such solar heat absorption, the coated glasses become hot in use and it is frequently necessary to toughen the coated glass in order to avoid breakage through overheating. It would be desirable to have a coated solar control glass which could be widely used without the need for toughening. This is particularly important for coated glasses which are not toughenable i.e. coated glasses which lose their useful properties on toughening. To produce such glasses in coated form, it is necessary to toughen the glass and then coat it. This is an expensive procedure, since in practice it involves coating relatively small pieces of toughened glass, rather than large stock sizes which can be cut up for use later. Moreover, as indicated above, different coatings are required depending on the appearance and properties required in the product. It would be desirable to have a coated solar control glass which could be used to provide glazings with a range of reflection colours. UK patent specification 1,152,691 describes the use of heat reflecting metal or metal oxide coatings to protect body coloured heat absorbing glasses from overheating, with the consequent risk of fracture, due to solar heating. To protect the heat absorbing glass, the coating is disposed between the glass and the sun. In one example, a pane of heat absorbing grey glass is used as the inner pane of a double glazing unit, with a gold coating on the surface of the pane facing the airspace of the unit. The outer pane may be of clear float or of 'slightly coloured' glass. UK patent specification 2,174,412A describes a double glazing unit incorporating two coatings. One of the coatings is a low emissivity coating comprising doped tin oxide and/or doped indium oxide, and the other coating is a heat reflecting metal oxide coating comprising at least 30% tin and at least 30% titanium calculated as weight per cent of the respective dioxide in the coating. The coatings may be on the same or different panes, and one of the panes may be of body coloured glass. Example 3 describes a double glazing unit having an outer pane of bronze float glass with the heat reflecting metal oxide coating on its outer face (i.e. away from the airspace), and an inner pane with the low emissivity coating on its outer face (i.e. towards the air space). US-A-4,069,630 describes a double glazing unit having a low emissivity tin oxide containing coating on the inner face (i.e. towards the airspace) of the outer pane. To mask the iridescent colour of the coating, the outer pane is of coloured heat absorbing glass. UK-A-1 364 712 describes a double glazing unit with a light and heat-reflecting coating on the inner face of the outer pane and a transparent conductive heating coating on the outer face of the inner pane (i.e. both coatings towards the airspace). The light and heat-reflecting layer may be of metallic copper, nickel, gold, titanium dioxide or another low emissivity coating, chosen to have sufficient transmission for visible light to avoid perceptible darkening within a building. The transparent conductive coating is generally tin oxide but may also be e.g. copper, gold or silver. The light transmission of a pane remains virtually unchanged if coated with a tin oxide layer. A suitable replacement metallic layer also having minimal effect on the light transmission would need to be very thin. The outer pane may be clear or coloured. GB-A-2068442 describes a thermal control multiple glazing assembly. The assembly is reversible to provide year-round adaptability, specifically using a pair of stub axles mounted on the glass frame so that the assembly rotates about a horizontal axis. One of the panes of the assembly has a higher energy absorptivity in respect of solar radiation than the other pane. To one side only of the more absorbent pane, at least one pane face which faces another pane of the assembly bears a light transmitting coating of a material (preferably doped tin oxide) selected to reduce the emissivity of the coated face in respect of infra-red radiation. The low emissivity coating is preferably located on a face of the more absorbent pane. US-A-4610115 is generally concerned with a curtainwall system incorporating architectural panels comprising a pair of spaced transparent substrates, at least one of the panels having vision and spandrel, i.e. opaque, areas. The aim of the invention is to provide an architectural panel in which the line between the vision and spandrel areas is obfuscated. To achieve this a reflective coating, which is preferably a metal oxide coating, is used on one of the faces of the panel, one of the faces of the outer pane being preferred in order to achieve the best obfuscation. EP-A-233003 discloses a bent and/or toughened silver coated glass having high light transmission and low emissivity. The specification is concerned with maintaining the low emissivity of the silver coating during subsequent bending and/or toughening by the deposition of layers of additional, different metals over the silver layer. We have now found that a range of high performance double glazing units of varying colour and performance can be produced, based on glass with a solar control coating of standard composition, and without the need to toughen the coated glass. According to the present invention there is provided a double glazing unit comprising an outer pane of toughened or partly toughened body coloured heat absorbing glass and an inner pane of annealed glass with a coating including a silver layer having a thickness in the range 15 nm to 40 nm on its face turned towards the outer pane. The expression "body coloured heat absorbing glass" is used, with reference to the present invention, to refer to glasses which contain heat absorbing metal oxides which colour the glass and which glasses have, when in the form of a pane 6 mm thick, a solar heat absorption of at least 40%. Examples of such glasses are ANTISUN Bronze glass, ANTISUN Green glass and ANTISUN Grey glass (ANTISUN is a trade mark of Pilkington plc; ANTISUN glasses are available from Pilkington Glass Limited). Preferably the outer pane is of 6 mm thick body coloured heat absorbing glass having a solar heat absorption in the range 45% to 55%. The outer pane will be toughened or partly toughened (for example, "heat strengthened" glass as defined in United States Federal Specification DD-G-1403D) to enable it to withstand the temperatures reached in service without fracturing. The coated inner pane may be a pane of coated clear float glass having a light transmission higher than its total solar heat transmission. The thickness of the silver layer in the coating on the inner pane is preferably in the range 20 nm to 30 nm. The coating on the inner pane preferably comprises a silver layer sandwiched between two anti-reflection layers. The anti-reflection layers may be of metal oxide, for example tin oxide, indium tin oxide, titanium oxide or zinc oxide, and will usually have a thickness in the range 10 nm to 80 nm especially 20 nm to 60 nm. A double glazing unit according to the invention is illustrated, in cross section, in the accompanying drawings. A double glazing unit 1 comprises an outer pane 2 of body coloured heat absorbing glass, an inner pane 3 of annealed glass with a coating 4 including a silver layer having a thickness in the range 15 nm to 40 nm on its face turned towards the outer pane. The panes are held in opposed spaced relationship by a spacing and sealing system 6. The invention is further illustrated, but not limited, by the following Examples. Throughout the specification and claims, including the Examples, the following terms have the meanings given below: "Light transmission" and "Light reflection" mean respectively the light transmission and light reflection with respect to the C.I.E. Illuminant C expressed in percent. The procedures for calculating these from the spectral transmission and reflection of the glass are well known and given in the standard colour text-books, e.g. W.D. Wright - The Measurement of Colour, Hilger & Watts, London 1964. "Solar heat absorption" means the percentage of solar radiation absorbed, where the solar radiation spectral distribution is that defined by P. Moon for air mass 2 (Journal of the Franklin Institute, 1940, volume 230, page 583) "Solar heat reflection" means the percentage of solar radiation reflected, where the solar radiation spectral distribution is that defined by P.Moon for air mass 2 (Journal of the Franklin Institute, 1940, volume 230, page 583.) "Direct solar heat transmission" means the percentage of solar radiation directly transmitted, where the spectral energy distribution of the solar radiation is taken as that defined by P. Moon for air mass 2. (Journal of the Franklin Institute, 1940, volumë 230, page 583). "Total solar heat transmission" is equal to the direct solar heat transmission plus the percentage of solar radiation which is absorbed and then re-radiated/convected to the inside. Example 1 A double glazing unit as shown in the drawings has an outer pane 2 of thermally toughened ANTISUN bronze glass, 6 mm thick. ANTISUN bronze glass is a bronze body coloured glass available from Pilkington Glass Limited having, when in the form of a pane 6 mm thick, a solar heat absorption of 49%. The inner pane 3 is a 6 mm pane of clear float glass with a coating 4 comprising a layer of silver 23 nm thick sandwiched between anti-reflection tin oxide layers each 60 nm thick to give a coating with a substantially neutral reflection colour. The coating was deposited by a magnetically enhanced sputtering process, using a thin layer of aluminium over the silver, as described in UK patent GB2,129,831B. The coated pane had a light transmission of 49%, a solar heat absorption of 10%,a solar heat reflection of 60% and a direct solar heat transmission of 30%, all measured with the coating towards the incident radiation. It is the suprisingly high solar heat reflection and very low solar heat absorption of the silver coatings used in the present invention which enables the products of the invention to be used without toughening of the inner pane. From the outside, the double glazing unit appears bronze in reflected light and bronze in transmitted light. From the inside, the double glazing unit appears silver in reflected light and bronze in transmitted light. The unit has the following optical properties (referring to solar radiation incident on the outer pane): Light transmission 25% Light reflection 15% Direct solar heat transmission 14% Total solar heat transmission 24% Example 2 A double glazing unit is constructed as described in Example 1 using a 6 mm pane of thermally toughened ANTISUN Grey glass (available from Pilkington Glass Limited) for the outer pane 2 in place of the ANTISUN Bronze glass used in Example 1. From the outside, the unit appears grey in reflected light and grey/bronze in transmitted light. From the inside, the double glazing unit appears silver in reflected light and grey/bronze in transmitted light. The unit has the following optical properties (referring to solar radiation incident on the outer pane.) Light transmission 21% Light reflection 12% Direct solar heat transmission 13% Total solar heat transmission 23% Example 3 A double glazing unit is constructed as described in Example 1 using a 6 mm pane of thermally toughened "ANTISUN Green" glass (available from Pilkington Glass Limited) for the outer pane 2 in place of the ANTISUN Bronze glass used in Example 1. From the outside the unit appears green in reflected light and yellow/green in transmitted light. From the inside the unit appears silver in reflected light and yellow/green in transmitted light. The unit has the following optical properties (referring to solar radiation incident on the outer pane): Light transmission 36% Light reflection 28% Direct solar heat transmission 14% Total solar heat transmission 24% Example 4 A double glazing unit is constructed as described in Example 1 using a 6 mm pane of thermally toughened ANTISUN Blue glass (available from Pilkington Glass Limited) for the outer pane 2 in place of the ANTISUN Bronze glass used in Example 1. From the outside, the unit appears blue in reflected light and blue/green in transmitted light. From the inside, the unit appears silver in reflected light and blue/green in transmitted light. The unit has the following optical properties (referring to solar radiation incident on the outer pane): Light transmission 27% Light reflection 17% Direct solar heat transmission 14% Total solar heat transmission 24% Thus it will be seen that the invention provides, using a single coating, a range of high performance solar control double glazing units of different colours. Moreover, because the outer pane is of body coloured heat absorbing glass, and the coating has a very high solar heat reflection and a low emissivity, the coated glass does not become hot in service and it is unnecessary to toughen it. The silver layer on the glass has a low electrical resistance and, if desired, may be used either for electromagnetic screening (as described in our UK patent application No. 8802401 filed 3rd February, 1988) or as a heating film. When used for electromagnetic screening, the coating may be provided with a continuous electroconductive bus bar at or adjacent the periphery thereof in electrical contact with the silver layer for connection to earth. If the coating is to be used for heating, it will usually be provided with a pair of separate bus bars each adjacent an opposite edge of the coating in electrical contact with the silver layer for connection to a source of electricity. However, it is not envisaged that the coatings will usually be used for heating and they will generally be free from a pair of bus bars as described above.

Claims: A double glazing unit comprising an outer pane of toughened or partly toughened body coloured heat absorbing glass and an inner pane of annealed glass with a coating including a silver layer having a thickness in the range 15 nm to 40 nm on its face turned towards the outer pane. A double glazing unit according to claim 1, comprising an outer pane of 6 mm thick body coloured heat absorbing glass having a solar heat absorption in the range 45% to 55%. A double glazing unit according to any of the preceding claims wherein the coated pane is of clear float glass and has a light transmission higher than its total solar heat transmission. A double glazing unit according to any of the preceding claims wherein the thickness of silver layer in the coating on the inner pane is in the range 20 nm to 30 nm. A double glazing unit according to any of the preceding claims wherein the coating on the inner pane comprises a silver layer sandwiched between two anti-reflection layers.

Inventors: GOODALL DAVID RAYMOND, GOODALL, DAVID RAYMOND
Applicants: PILKINGTON PLC
Application year: 1988
Main classification: E06B3
IPC codes: C03C27, E06B3, C03C17, H05K9