FERROELECTRIC CERAMICS

Abstract: Ferroelectric ceramics represented by xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-­ qBi₂O₃-rX wherein x,y,z,m,n,p,q and r represent amounts by mole, respectively, with the proviso that x+y+z being 1, X is at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅, and Y₂O₃, and wherein x is from 0.25 to 0.50, Y is from 0.05 to 0.70, z is from 0.05 to 0.70, m is from 0 to 0.10, n is from 0 to 0.04, p is from 0 to 0.04, q is from 0 to 0.02 and r is from 0.005 to 0.02. The disclosed ferroelectric ceramics have increased relative dielectric constant and/or electromechanical coupling factor, and are suitable for use as actuators.

Description: FIELD OF THE INVENTION The present invention relates to ferroelectric ceramics of PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃ series. More particularly, it relates to ferroelectric ceramics of PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃ series having increased relative dielectric constant and/or electromechanical coupling factor. BACKGROUND OF THE INVENTION Piezoelectric materials comprising ferroelectric ceramics have heretofore been used in ceramic filters, mechanical filters, ultrasonic transducer and piezoelectric buzzers. When piezoelectric materials are used in such applications, resonance characteristics of the materials are utilized, and in this respect ferroelectric ceramics of PbTiO₃-PbZrO₃ series optionally having BaTiO₃, SrTiO₃ and/or CaTiO₃ added thereto have been generally used. Recently, to improved various characteristics of the ferroelectric ceramics of PbTiO₃-PbZrO₃ series, ternary piezoelectric ceramics represented by PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃ have also been proposed. On the other hand, use of piezoelectric in the non-resonance state, for example use of piezoelectric ceramics as an actuator, has also been studied. However, when a piezoelectric ceramic material is used in the non-resonance state, it is necessary to transform electric energy to mechanical energy which displaces the piezoelectric ceramics material itself. Accordingly, piezoelectric ceramics having a large piezoelectric strain constant d are required. Among the piezoelectric strain constant d, electromechanical coupling factor k and relative dielectric constant ε, of a piezoelectric ceramic material, there is a following relation: d ∝ k√ ε and therefore, in order that the material has a large piezoelectric strain constant d, it must have a large electromechanical coupling factor k and/or a large relative dielectric constant. It is known in the art that piezoelectric ceramics of PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃-SrTiO₃ series have a large relative dielectric constant and a large electromechanical coupling factor. OBJECT OF THE INVENTION An object of the invention is to provide novel ferroelectric ceramics of PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃ series which have further increased relative dielectric constant and/or electromechanical coupling factor and thus can be used as an actuator. SUMMARY OF THE INVENTION In has now been found that the relative dielectric constant and/or electromechanical coupling factor of piezoelectric ceramics of PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃-SrTiO₃ series optionally having added thereto SrTiO₃, SnO₂, ZnO or Bi₂O₃ can be further increased by incorporation of a specified amount of at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅, and Y₂O₃. Thus, ferroelectric ceramics according to the invention are represented by xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rX wherein x,y,z,m,n,p,q and r represent amounts by mole, respectively, with the proviso that x+y+z being 1, X is at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅, and Y₂O₃, x is from 0.25 to 0.50, y is from 0.05 to 0.70, z is from 0.05 to 0.70, m is from 0 to 0.10, n is from 0 to 0.04, p is from 0 to 0.04, q is from 0 to 0.02 and r is from 0.005 to 0.02. DETAILED DESCRIPTION OF THE INVENTION The ferroelectric ceramics according to the invention will now be described in detail. The ferroelectric ceramics according to the invention are represented by: xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rX wherein x,y,z,m,n,p,q and r represent amounts by mole, respectively, with the proviso that x+y+z being 1, X is at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅, and Y₂O₃, and wherein x is from 0.25 to 0.50, preferably from 0.30 to 0.45, y is from 0.05 to 0.70, preferably from 0.10 to 0.60, z is from 0.05 to 0.70, preferably from 0.10 to 0.60, m is from 0 to 0.10, preferably from 0.05 to 0.10, n is from 0 to 0.04, preferably from 0.01 to 0.02, p is from 0 to 0.04, preferably from 0.01 to 0.02, q is from 0 to 0.02, preferably from 0.01 to 0.02, and r is from 0.005 to 0.02, preferably from 0.008 to 0.02. As defined above, according to the invention, a specified amount of at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅ and Y₂O₃, is added to ferroelectric ceramics of xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃ series which optionally contain a specified amount of SrTiO₃, SnO₂, ZnO or Bi₂O₃. It has found that the piezoelectric strain constant, namely the relative dielectric constant and/or electromechanical coupling factor, of piezoelectric ceramics of PbTiO₃-PbZrO₃-Pb(Mg 1/3 Nb 2/3 )O₃ series optionally having added thereto SrTiO₃, SnO₂, ZnO or Bi₂O₃ can be remarkably increased by adding thereto from 0.005 to 0.02 mole, preferably from 0.008 to 0.02 mole of at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅, and Y₂O₃. With substantially less than 0.005 mole of Dy₂O₃, Ta₂O₅, and/or Y₂O₃, the relative dielectric constant of the product is not appreciably improved. Addition of an excess amount of Dy₂O₃, Ta₂O₅ or Y₂O₃, must be avoided: in fact, when the amount of Dy₂O₃, Ta₂O₅ and/or Y₂O₃ added exceeds 0.20 mole, the electromechanical coupling factor tends to be reduced instead. Further, ceramic compositions of the formula: xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rX wherein x is less than 0.25 or more than 0.50, y is less than 0.05 or more than 0.70, or z is less than 0.05 or more than 0.70,are not preferably, since they do not have appreciably increased relative dielectric constant and/or electromechanical coupling factor. Ceramic compositions of the above formula wherein m is more than 0.10 are also not preferably, since they have a reduced electromechanical coupling factor. Further, it has been found that as n exceeds 0.04, p exceeds 0.04 or q exceeds 0.02, both the relative dielectric constant and electromechanical coupling factor of the material tend to be reduced. The ferroelectric ceramics according to the invention are prepared by weighing suitable amounts of suitable starting compounds selected from; PbO(lead monoxide), ZrO₂(zirconium oxide), TiO₂(titanium oxide), MgCO₃(magnesium carbonate), Nb₂O₅(niobium oxide), SrCO₃(strontium carbonate), SnO₂(stannic oxide), ZnO(zinc oxide), Bi₂O₃(bismuth oxide), Dy₂O₃(dysprosium oxide), Ta₂O₅(tantalum oxide), and Y₂O₃(yttrium oxide), to provide a suitable starting mixture containing required metallic elements in required molar proportions depending upon the particular desired product, and calcining the mixture at a temperature from about 1000° to about 1300°C. More particularly, the ferroelectric ceramics according to the invention can be prepared by the following process. A suitable starting mixture containing required metallic elements in required molar proportions depending upon the particular desired product is pulverized in a ball mill and precalcined at a temperature of from about 900° to 1100°C. for a period of from 2 to 6 hours to provide a precalcined product. The precalcined product is again subjected to a ball mill treatment, admixed with a binder such as polyvinyl alcohol in an amount of from 1 to 20 % by weight based on the resulting admixture, dried e.g. by means of a spray drier, and press formed under a pressure of from 500 to 1500 kg/cm² and subjected to a further calcination in air at a temperature ranging from about 1000° to about 1300°C., using a crucible made of a refractory material such as MgO which is highly heat resistant and hardly absorb metallic elements such as Pb. During the further calcination, Pb is liable to be volatilized thereby frequently resulting in a product containing Pb in an amount less than that required. To avoid this, the further calcination is preferably carried out in a Pb rich atmosphere which can be established simply by placing particulate PbTiO₃ in the vicinity of the crucible. By the process as illustrated above the dense ferroelectric ceramics according to the invention can be prepared. EFFECT OF THE INVENTION The ferroelectric ceramics according to the invention which comprise a ferroelectric ceramic material of xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃ series (optionally containing a specified amount of SrTiO₃, SnO₂, ZnO or Bi₂O₃) having added thereto a specified amount of at least one oxide selected from the group consisting of Dy₂O₃, Ta₂O₅, and Y₂O₃., have an increased piezoelectric strain constant that is an increased electromechanical coupling coefficient and/or an increased relative dielectric constant, and therefore can be used as actuators. While the invention will be further described by the following examples, the invention is not restricted thereto. Example 1 Suitable amounts of PbO, ZrO₂, TiO₂, MgCO₃,Nb₂O₅, SrCO₃, SnO₂, ZnO, Bi₂O₃ and Dy₂O₃ were weighted to provide starting compounds capable of producing ferroelectric ceramics having compositions indicated in Table 1. Each compound was processed in a ball mill for a period of about 24 hours. The mixture was removed from the mill, dried, passed through a 250 µm (60 mesh) sieve, press formed under a pressure of 500 kg/cm² and precalcined at a temperature of 1000°C. The precalcined product was then passed through a 425 µm (40 mesh) sieve, and again ball milled for a period of 24 hours. The content of the mill was taken out, admixed with 2 % by weight of polyvinyl alcohol based on the weight of the resulting admixture, and dried by means of a spray drier to provide particles, which were then press formed under a pressure of about 1000kg/cm² to a disc having a diameter of 25 mm and a thickness of about 2 mm. The disc was placed in a crucible made of MgO. The crucible was covered with a well sealing lid, and particulate PbTiO₃ was placing in the vicinity of the crucible. The disc in the crucible was then calcined in air at temperatures of from 1210° to 1270°C. for a period of about 2 hours to provide a dense calcined disc having a density of not less than 7.7 g/cm³. The surfaces of the disc thus obtained were polished with particulate diamond having a diameter of 6 µm to provide a specimen, which was tested for various electric properties as described below. After the specimen thus obtained was coated with a silver paste on both surfaces and baked at a temperature of 750°C., it was polarized by application of an electric field of 40KV/cm at a temperature of about 100°C. and aged for 12 hours at a temperature of 50°C. On the so treated specimen the relative dielectric constant (ε) and the dielectric loss (tanδ) were measured at a frequency of 10 KHz, by means of an impedance analyzer. Separately, the resonance frequency (Fr) and the antiresonance frequency (Fa) of the disc specimen were measured. The radial electromechanical coupling factor (kp) of the specimen was determined from the following equation: wherein a is 0.395 and b is 0.574. Further, the piezoelectric constant (d₃₁) of the specimen was calculated from the following equation: wherein the Poisson's ratio (δ) and the elastic compliance (S₁₁ E ) were determined from the resonance characteristics of the specimen. Table 1 shows the relative dielectric constant (ε), dielectric loss (tanδ), radial electric mechanical coupling factor(kp) and piezoelectric constant (d₃₁) of the ferroelectric ceramics represented by xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rDy₂O₃ with various of values x,y,z,m,n,p,q and r indicated in the same table. Table 1 reveals that the relative dielectric constant (ε), dielectric loss (tanδ), radial electric mechanical coupling factor (kp) and piezoelectric constant (d₃₁) of the ferroelectric ceramics of xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃ series are enlarged by addition of Dy₂O₃. Example 2 Ferroelectric ceramics represented by xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rTa₂O₅ were prepared by the procedures described in Example 1 except that the indicated amounts of Ta₂O₅ were used instead of the Dy₂O₃, and tested for various electric properties as in Example 1. The results are shown in Table 2. Table 2 reveals that the relative dielectric constant (ε), dielectric loss (tanδ), radical electric mechanical coupling factor (kp) and piezoelectric constant (d₃₁) of the ferroelectric ceramics of xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃ series are enlarged by addition of Ta₂O₅. Example 3 Ferroelectric ceramics represented by xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rY₂O₃ were prepared by the procedures described in Example 1 except that the indicated amounts of Y₂O₃ were used instead of the Dy₂O₃, and tested for various electric properties as in Example 1. The results are shown in Table 3. Table 3 reveals that the relative dielectric constant (ε), dielectric loss (tanδ), radial electric mechanical coupling factor (kp) and piezoelectric constant (d₃₁) of ferroelectric ceramics of xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃ series are enlarged by addition of Y₂O₃.

Claims: A ferroelectric ceramic represented by the formula xPbTiO₃-yPbZrO₃-zPb(Mg 1/3 Nb 2/3 )O₃-mSrTiO₃-nSnO₂-pZnO-qBi₂O₃-rX, wherein x,y,z,m,n,p,q and r represent amounts by mole with the proviso that x+y+z is 1, X is at least one oxide selected from Dy₂O₃, Ta₂O₅, and Y₂O₃, x is from 0.25 to 0.50, y is from 0.05 to 0.70, z is from 0.05 to 0.70, m is from 0 to 0.10, n is from 0 to 0.04, p is from 0 to 0.04, q is from 0 to 0.02 and r is from 0.005 to 0.02. A ferroelectric ceramic according to claim 1 wherein x is from 0.30 to 0.45, y is from 0.10 to 0.60, z is from 0.10 to 0.60, m is from 0.05 to 0.10, n is from 0.01 to 0.02, p is from 0.01 to 0.02, q is from 0.01 to 0.02 and r is from 0.008 to 0.02. Use of a ferroelectric ceramic as claimed in claim 1 or 2 as an actuator.

Inventors: HIRAI, NOBUKI, OHNO, TAKAO, USHIDA, YOSHIHISA
Applicants: MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1988
Main classification: C04B35
IPC codes: C04B35, H01L41