Synthesis of superconductors from xenotyme

Abstract: A superconductor of the type AM₂Cu₃O x , in which x is about 7 and M is an alkaline earth, is obtained by alkaline melting of xenotyme and melting of the product with an alkaline earth and copper oxide.

Description: Superconductive materials are those where the electric resistance falls to zero (10⁻²⁰ Ohm/cm) below a critical temperature, its amount depending on the material. The superconductivity is defined only within a critical surface (only figure), its axes being the temperature, the electrical current and the magnetic field. Thus, for a given working temperature there is a defined curve of critical current in function of the magnetic field generated and/or applied to the superconductor. The main practical superconductor materials are NbTi and Nb₃Sn. Their working temperature is only 4.2 K, which is the boiling temperature of liquid helium. This is the main limitation to large scale application of superconductivity. Superconductors are being used almost exclusively for winding or magnets. Manufactured from wires (NbTi and Nb₃Sn) or tapes (Nb₃Sn) with high critical current densities (3500 A/mm² to 5 Tesla for NbTi), they allow the winding of compact magnets for the production of high fields (up to 18 Tesla) in large volumes. The most popular superconductor magnets are the ones used for the formation of medical images by nuclear magnetic resonance (MRI) and for materials analysis by the same principle (NMR), the magnets for ore separation and research magnets for high fields. Among the latter are distinguished the magnets used in large particle accelerators (SSC, HERA, KEK, etc.). The superconductor magnets are included in the conceptual project of large machines, among them nuclear fusion reactors, energy generators for magneto-hydro-dynamics (MHD) and magnets for energy storage in space stations. Of course, some difficulties in the feasibility of these large machines transcend superconductivity. The oxide superconductors of high critical temperature were discovered in 1986. These are intermetallic compounds involving copper oxide and rare earth, with perovskite (mica) crystal structure. Their critical temperatures vary from 30 K to room temperature and their critical fields are above 60 Tesla. Therefore these materials are considered very promising and may come to replace with advantages the Nb₃Sn and NbTi in the manufacture of magnets and find other applications not feasible with liquid helium, such as transmission of electricity, for example. These materials are not yet on the market as wires, cables, films, tapes or sheets. The present invention relates to the synthesis of superconductors from xenotyme, which is an yttrium phosphate mineral common in Brazil, and which contains only those rare earth elements pertinent to the synthesis of the superconductors of interest here. The rare earth oxides represent 45 to 55% of the weight of the mineral. The preferred, but not exclusive destination of these superconductors is the winding of magnets, transmission and distribution of electricity, magnetic shielding, computer applications (hybrid superconductive semiconductors, Josephson joints, transistors, etc.), among other applications. The attached figure illustrates the critical surface relative to superconductivity, indicated by (A). The following is an example of the above exposure: 100 g of pulverized xenotyme (200 mesh) are melted at 1000°C with 1000g of a mixture of Na₂CO₃/K₂CO₃ in molar proportion of 1:1. The resulting solid is rinsed with 2 liters of a solution of 1:10 of Na₂CO₃, then treated with 200 ml of HC1 1M at 60°C and then filtered. The residue is discarded. The solution is treated with NH₄OH 3M until all rare earth is precipitated, an excess of NH₄OH is added to separate certain cations which form soluble complexes with NH₄ OH (Zn²⁺, Cu²⁺, Ni²⁺, etc.) which may be present. The precipitate is dissolved with HCl 3M and again precipitated with oxalic acid at a temperature between 50 and 60°C. the precipitate is rinsed with diluted oxalic acid and calcinated at 850°C. The mixture of oxides, of a mass between 45 and 55 g contains only the rare earth originally present in the 100 g of xenotyme. In order to obtain 100 g of superconductor, a mixture is prepared from 15g of rare earth oxides obtained as per above, 53 g of barium carbonate or other alkaline earth element and 32g of copper oxide. A heat treatment is performed for the reaction of the above components at 950°C during several hours. Then the calcinated material is ground and again heat treated during some hours at below 1000°C to allow for control by chemical calculation. Then the material is ground again to allow for its granulometric control.

Claims: A process for separating rare earths present in xenotyme comprising: alkaline melting xenotyme at 1000°C with a flux of a mixture of sodium carbonate and potassium carbonate with a molar ratio of 1:1; mixing the solid product with sodium carbonate solution; treating the product with hydrochloric acid and filtering; treating the filtrate with ammonia solution; dissolving the resulting precipitate in hydrochloric acid; treating the hydrochloric acid solution with oxalic acid at between 50°C and 60°C; and calcining the resulting precipitate at about 850°C. A process for preparing a superconductor of the type AM₂Cu₃O x in which x is about 7, A is a mixture of rare earths and M is an alkaline earth, comprising conducting a process according to claim 1, followed by: heating together the product of that process with an alkaline earth or alkaline earth compound and copper oxide at about 950°C; grinding the product; and heating the product at about 1000°C.

Inventors: CANEVAROLO SEBASTIAO VICENTE J, FILHO PEDRO IRIS PAULIN, FILIPINI CESAR AUGUSTO, SERRA OSWALDO ANTONIO, VELLEGO GENI, CANEVAROLO, SEBASTIAO VICENTE, JR., FILHO, PEDRO IRIS PAULIN, FILIPINI, CESAR AUGUSTO, SERRA, OSWALDO ANTONIO, VELLEGO, GENI
Applicants: FUNDACAO UNIVERSIDADE FEDERAL, PIRELLI CABOS S A, UNIV SAO PAULO, FUNDACAO UNIVERSIDADE FEDERAL DE SAO CARLOS, PIRELLI CABOS S/A, UNIVERSIDADE DE SAO PAULO
Application year: 1988
Main classification: C01F17
IPC codes: C01G3, C04B35, C01F17