Use of a copolymer alpha olefin alkenylsilane for bonding two layers or for coating an article

Abstract: The present invention relates to the use of a polyolefin resin composition comprising a random copolymer of an alkenylsilane compound and an α-olefin compound as a material for adhesion or a coating material.

Description: The present invention relates to the use of a polyolefin resin composition comprising a random copolymer of an alkenylsilane and an α-olefin as a material for adhering two layers of an article. The composition is particularly advantageous for adhering a metal and a polyolefin or adhering a polymer containing polar groups and a polyolefin. The present invention also relates to the use of the polyolefin resin composition material as an easy coating material. Description of the Related Art It is known to employ a multi-layer structure comprising a polyolefin layered between polymers containing polar groups, such as a saponified ethylene-vinyl acetate copolymer (such as EVAL), nylon or polyester in order to obtain the beneficial properties imparted by a polyolefin, as well as the beneficial properties imparted by polymers containing polar groups, such as gas barrier properties, which cannot be achieved through the use of a polyolefin alone. It is also known to employ a multi-layer structure comprising a polyolefin and a metal such as iron or aluminum. However, due to incompatibility between a polyolefin and polymers containing polar groups, and bad drapeability between a polyolefin and a metal, the materials cannot be directly adhered. Thus, when such multi-layer structures are employed, an adhesive resin is inserted between the polyolefin and the polymers containing polar groups, or between the polyolefin and the metal. A composition comprising a graft polymer of polyolefin and anhydrous maleic acid has been used as an adhesive resin in such multi-layer structures. A polyolefin is useful in various applications including exterior paint. However, a polyolefin has poor coating properties and thus, if used alone, easily peels. Thus, a composition comprising a graft polymer of polyolefin and anhydrous maleic acid is widely employed as an adhesive resin to adhere a polyolefin to the surface of a molded component or to treat the surface of a molded component by plasma. Plasma treatment requires a complicated method and special equipment is required. It is desirable to develop a resin composition which will improve the coating properties of a polyolefin upon being mixed therewith. A graft polymer of anhydrous maleic acid and polyolefin improves the adhesiveness between a polyolefin and a polymer containing a polar group to a certain extent. However, when the graft copolymer is used to adhere a saponified ethylene-vinyl acetate copolymer and a polyolefin or a metal, poor adhesive properties result. Further, when used to adhere a polyolefin with a metal, there is a problem of corrosion of the metal. Thus, it has been desired to produce a resin which shows better adhesiveness. As set forth in a co-pending application entitled "α-Olefin Block Copolymers and Processes for Preparing the Same", filed in the United States Patent and Trademark Office on November 16, 1988, (EP-A 317 280) Applicants discovered that an α-olefin block copolymer comprising an alkenylsilane and an α-olefin is useful as a material for adhesion. A random copolymer of an alkenylsilane and an α-olefin polymerized in the presence of a transition metal compound and an organic compound is disclosed in US-A- 3,223,686. More particularly, US-A-3,223,686 discloses copolymerizing allylsilane with ethylene to obtain amorphous linear copolymers resembling a non-vulcanized elastomer. US-A-3,644,306 discloses that such a copolymer can be used to obtain a crosslinkable material. The polymers disclosed in US-A-3,644,306 are ethylene-propylene-alkenylsilane terpolymers resembling vulcanized rubbers and fibres, and are useful for producing materials and articles possessing elastic properties. However, it has not been previously known that these copolymers are useful as a material for adhesion and for easy coating materials. A crosslinkable copolymer of ethylene and a silane is taught in GB-A-1,415,194; crosslinking is by exposure to water in the presence of a siloxane condensation catalyst. The copolymer has alkoxy or alkoxyalkoxy radicals in the molecule and its production is said to avoid the formation of corrosive hydrohalic acids. EP-A-0,193,317 teaches a silane crosslinkable copolymer composition prepared by radically polymerizing a monomeric mixture consisting of ethylene and an ethylenically-unsaturated silane compound having a hydrolyzable organic group. The composition is said to avoid condensation reactions in an extruder, so that the resulting product has improved surface smoothness and appearance. EP-A-0,240,638 discloses copolymers containing olefinic chlorosilane and olefinic halide functional groups. The copolymers are said to be useful in fibreglass and rubber compositions, and for the formation of graft and block polymers. The copolymers can be crosslinked to yield useful lube oil additives. The present invention is concerned with the provision and use of a polyolefin resin composition as a material for adhesion or coating comprising a random copolymer of an alkenylsilane and an α-olefin. The resin composition can provide a material for easy coating, a molded article of which is easily surface coated and which is obtainable, for example, by thermoforming the random copolymer. The composition serves as an adhesion material or an easy coating material which has superior adherability and coating strength when applied between a metal and a polyolefin compound, or between a polymer containing polar groups and a polyolefin. One aspect of the invention lies in the use, as an adhesive of a polyolefin resin composition containing a random copolymer of an α-olefin and an alkenylsilane represented by the formula (I) H₂C = CH - (CH₂) n - SiH m R (3-m) wherein n is 0 or an integer of from 1 to 12, R is selected from the group consisting of a methyl and a phenyl radical, and m is an integer of from 1 to 3, when making an article by bonding a first layer to a second layer of the article, said first layer being formed of a polyolefin and said second layer consisting of a metal or a polymer containing polar groups. Another aspect of the invention is a process of making a shaped article, comprising the steps of (a) shaping the article from a polyolefin resin composition containing a random copolymer of an α-olefin and an alkenylsilane represented by the formula (I). H₂C = CH - (CH₂) n - SiH m R (3-m) wherein n is 0 or an integer of from 1 to 12, R is selected from the group consisting of a methyl and a phenyl radical, and m is an integer of from 1 to 3, and (b) coating the article with a metal or a polymer containing polar groups. Additional features and advantages of the invention will be set forth in the description that follows, or may be learned by practice of the invention. To achieve the objects and in accordance with the purpose of the invention, as embodied and broadly described herein, the invention concerns the use of a polyolefin resin composition comprising a random copolymer of an alkenylsilane and an α-olefin. The random copolymer has been found excellent in adhesive and coating properties as well as in rigidity, and therefore is of great industrial value. Reference will now be made to the preferred embodiments of the invention. The alkenylsilane compounds useful in the practice of the invention have the formula (I): H₂C = CH - (CH₂) n - SiH m R (3-m) wherein n is 0 or an integer from 1 to 12, R is selected from the group consisting of a methyl and a phenyl radical, and m is an integer of from 1 to 3. Exemplary suitable alkenylsilanes for use in the invention include vinylsilane, allylsilane, butenylsilane and pentenylsilane. Compounds formed by substituting a hydrocarbon residue such as a methyl or a phenyl group for one or two hydrogen atoms of the Si-H groups, or substituting a halogen residue for one, two or three hydrogen atoms of the Si-H groups, in each molecule of the alkenylsilane compound can also be employed. Preferably, the α-olefin used in the random copolymer is a C₂-C₁₂ olefin, more preferably, a C₂-C₈ olefin such as ethylene, propylene, butene-1, pentene-1, hexene-1, 2-methylpentene-1, octene-1 and a mixture of two or more of these compounds. The random copolymer is obtained by polymerizing an alkenylsilane and an α-olefin, preferably in the presence of a catalyst. Suitable catalysts useful in preparing the random copolymer include a catalyst system composed of a transition metal compound and an organometal compound. Exemplary suitable catalysts are also described in U.S. Patent No. 3,223,686. The transition metal compound is preferably a titanium halide or a vanadium halide. The organometal compound is preferably an organoaluminum compound. Exemplary suitable catalyst systems include a combination of a transition metal catalyst obtained by reducing titanium tetrachloride with metallic aluminum, hydrogen or an organoaluminum compound; those obtained by modifying the titanium trichloride with an electron donor and an organoaluminum compound optionally including an electron donor compound such as oxygen-containing compounds; a combination of a vanadium halide or oxy-vanadium halide and an organicaluminum compound; a combination of a transition metal catalyst obtained by carrying a titanium halide, a vanadium halide or oxy-vanadium halide on a carrier such as magnesium halide or on a carrier by treating with an electron donor and an organicaluminum compound optionally including an electron donor compound such as oxygen-containing compounds; a combination of a transition metal catalyst obtained by dissolving the reaction product of magnesium halide and an alcohol in a hydrocarbon solvent, and thereafter treating by a precipitant such as titanium tetrachloride to insolubilize the hydrocarbon solvent. Further, the titanium tetrachloride may be treated by an electron donor compound such as an ester or ether and thereafter treated by a titanium halide and an organoaluminum compound that optionally includes an electron donor compound such as an oxygen-containing compound. Exemplary suitable catalyst systems are disclosed in Zieglar-Natta Catalysts and Polymerization by John Boor, Jr. (Academic Press), Journal of Macromolecular Science Reviews in Macromolecular Chemistry and Physics, C24(3) 355-385 (1984), ibid. (25(1) 578-597 (1985)). Preferably, the electron donor contains oxygen containing compounds such as ethers, esters, orthoethers, and alkoxy-silicon compounds. Further, alcohols, aldehydes and water may be used as the electron donor. The organoaluminum compound is preferably selected from the group consisting of a trialkylaluminum, a dialkylaluminum halide, an alkylaluminum sesquihalide and an alkylaluminum dihalide. Preferably, the alkyl groups of these compounds are selected from the group consisting of methyl, ethyl, propyl, butyl and hexyl groups, and the halide groups are selected from the group consisting of chlorine, bromine and iodine. Polymerization of the alkenylsilane and α-olefin is generally carried out by a solvent process in which an inert solvent is used. However, bulk polymerization or vapor-phase polymerization processes are also suitable. Polymerization of the random copolymer may be carried out by well-known processes and conditions for polymerizing α-olefins. Generally, polymerization is conducted at a temperature of from about 0°C to about 200°C, preferably from about 25°C to about 150°C, under a pressure of from about atmospheric pressure to about 150 kg/cm² (14.7 mPa), preferably from atmospheric pressure to about 100 kg/cm² (9.8 mPa). Preferably, the alkenylsilane is present in the random copolymer used in the processes of the invention in an amount of from 1 wt. ppm to 30 wt. % when the copolymer is used as an adhesive material. If present in an amount greater than 30 wt. %, the alkenylsilane causes a decrease in catalyst activity. Preferably, when used as a material for easy coating, the alkenylsilane is present in an amount of from 10 wt. ppm to 30 wt. %. No particular limitation is placed on the molecular weight of the copolymer and hence the molecular weight may be determined in accordance with the purpose of use. When the random copolymer is to be used as a blend with other polyolefins, a desired molecular weight of the copolymer can be achieved by adjusting its intrinsic viscosity measured at 135°C in a tetralin solution to not exceed 10, preferably from about 0.1 to about 5 dl/g. For commercial purposes, it is more economical to adjust the content of the alkenylsilane to above 1 wt. ppm for an adhesive material and above 10 wt. ppm for an easy coating material by blending the random copolymer which contains a relatively high concentration of alkenylsilane and a polyolefin which contains no alkenylsilane. Any polyolefin which does not contain an alkenylsilane can be employed. There is no particular limitation on the molecular weights of the polyolefin employed. Further, a random or block copolymer of olefins can be blended with the alkenylsilane - olefin random copolymer to produce a material for adhesion or easy coating. Polyolefins suitable for use include homopolymers, random or block copolymers and copolymers with a small amount of α-olefin of higher carbon in number. The polyolefins are obtained by any conventional polymerization process carried out in the presence of a conventional polymerization catalyst. Polyolefins commercially obtained on the market are also suitable for use in the invention. Various additives such as an anti-oxidizing agent and an ultraviolet light absorber can be added to the polyolefin resin composition if necessary to achieve a desired property. Further, optionally a catalytic addition which activates the Si-H bond can be used in combination with the additives to improve the adhesive properties and the easy coating properties. Suitable addition compounds include an organic acid or its salt, an organic base, an alkoxide compound of an alkali metal or an alkali earth metal, a hydroxy compound, an oxide, a noble metal such as palladium or platinum. However, it is not necessary to use these catalytic additives. The mixing ratio of the random copolymer which contains an alkenylsilane and the polyolefin which does not contain an alkenylsilane depends on the amount of alkenylsilane present in the random copolymer. Preferably, the amount of alkenylsilane present in the composition is from about 1 weight ppm to about 1 weight % for adhesion materials, and from about 10 weight ppm to 1 weight percent for easy coating materials. The random copolymer may be blended with an additive such as a stabilizer. There is no particular limitation on the procedure employed for mixing the copolymer with other polyolefins and/or additives. A conventional procedure such as premixing the mixture in a Henschel mixer homogeneously and melt-blending the resultant mixture in an extruder followed by granulation is sufficient. Mixing and melting may be carried out simultaneously by brabender or after melting, according to the desired end use, the mixture may be molded to form a sheet or film. Specifically, the polyolefin resin composition may be employed as an adhesive for a polyolefin and a polar group-containing polymer, for example, polyamide, polyester, polyether or ethylenevinyl alcohol copolymer, or a metal, for example, aluminum, steel sheet, soft iron sheet or galvanized iron sheet. The polyolefin resin composition comprising a random copolymer of an alkenysilane an α-olefin may be used as a material for adhesion in a manner such that it is held between the layers of a polyolefin and a polar group-containing polymer to bind both layers by hot melt or extrusion amination. The layer may also be in the shape of a bottle. It is also possible to use the random copolymer layer as an adhesive composition on a structure composed of a polyolefin or metal layer. The random copolymer may also be utilized as a material for easy coating. When being used as a material for easy coating, the random copolymer is first formed into a desired shape and then coated. No particular restrictions are imposed on the coating to be used for this purpose. For example, urethane coatings, acrylic coatings and the like may be used. The invention will further be clarified by the following examples, which are intended to be purely exemplary of the invention. Example 1: (a) Preparation of the polymerization catalyst An oscillating mill equipped with four grinding pots which contained 9 kg of steel balls having a diameter of 12 mm and an inner volume of 4 liters were employed. In each pot, 300 g of magnesium chloride, 60 ml of tetraethoxysilane and 45 ml of α,α,α-trichlorotoluene were added and ground for 40 hours in an atmosphere of nitrogen. The ground mixture thus obtained (300 g) was charged in a 5 liter flask. 1.5 liters of titanium tetrachloride and 1.5 liters of toluene were added to the ground mixture, followed by stirring at 100°C for 30 minutes. The supernatant was removed. An additional 1.5 liters of titanium tetrachloride and 1.5 liters of toluene were added to the solid portion obtained, followed by stirring at 100°C for 30 minutes. The resultant supernatant was removed and the solid portion was washed repeatedly with n-hexane, thereby obtaining a transition metal catalyst slurry. A part of the slurry was taken out as a sample and its titanium content was analyzed. It was found to be 1.9 weight percent. (b) Random Copolymerization of Vinylsilane and Propylene To a pressure-tight glass autoclave having an inner volume of 200 ml the following were added: 40 ml of toluene, 20 mg of the above-described transition metal catalyst, 0.128 ml of diethylaluminum chloride, 0.06 ml of p-toluic acid methyl ester and 0.20 ml of triethylaluminum in an atmosphere of nitrogen. To the resultant mixture 2.0 g of vinylsilane were charged, then propylene was charged up to a pressure of 5 kg/cm² (0˙5 mPa), followed by polymerization at 70°C for 2 hours. After the polymerization reaction, the polymer containing slurry was filtrated and then dried. 43 g of random copolymer powder were obtained. The intrinsic viscosity (hereinafter abbreviated as η) of the powder was 1.45 dl/g measured at 135°C in a tetralin solution. The melting point and crystallizing temperatures were measured at maximum peak temperatures by raising or decreasing the temperature at a rate of 10°C/min. by means of a differential-thermal analysis instrument. The melting point was 156°C and the crystallizing temperature was 118°C. The amount of polymerized vinylsilane in the random copolymer was calculated by analyzing silicon and was found to be 1.6 weight percent. (c) Preparation of Ethylene Propylene Copolymer Propylene and 2.5 weight percent of ethylene were polymerized in the same manner as above. The ethylene-propylene random copolymer had an η of 1.60 dl/g; a rate of extraction residue of 91.5 percent (determined by extracting the powder by boiling n-heptene in a Soxhlet's extractor (hereinafter abbreviated as I.I.) which was given in terms of the weight percentage of the powder after the extraction to the powder before the extraction); and a melting point of 154°C. (d) Preparation of the Composition 200 g of ethylene-propylene random copolymer were mixed with 10 g of propylene-vinylsilane random copolymer, 0.2 g of phenol type stabilizers and 0.3 g of calcium stearate. The resulting mixture was granulated to prepare a composition for adhesive materials. (e) Adhesion Test To determine the strength of adhesion between a sheet of EVAL (Kuraray Co., Ltd., EP-F, ethylene-vinyl alcohol copolymer) having a thickness of 0.2 mm and a sheet of propylene-ethylene copolymer (obtained in section (c) above), a multi-layer structure having the following three layers was formed: sheet of ethylene-vinyl alcohol copolymer; sheet of propylene-vinylsilane random copolymer; sheet of propylene-ethylene copolymer. The sheet of propylene-vinylsilane random copolymer had a thickness of 0.1 mm. The sheets were pressed at 220°C and 4 g/cm² for 3 minutes. The peel strength of the multi-layered structure was not less than 2 kg/cm. The peel strength was the T-type peel strength and was measured for a specimen having a width of 2.5 cm at 23°C and a pulling rate of 100 mm/min, by using the Instron tensile testing machine. (f) Comparison For comparative purposes, the adhesion test was carried out on a multi-layer structure in which a sheet having the composition set forth in (d), above but which did not contain any propylene-vinylsilane random copolymer, was inserted between a sheet of EVAL and a sheet of ethylene-propylene copolymer. The sheets were peeled autogeneously and the peel strength could not be measured. Example 2: A polyethylene having an η of 1.75 dl/g was obtained according to the procedure of Example 1(b) except that vinylsilane was not used and ethylene was used instead of propylene. A sheet of the composition was inserted as an adhesive layer between a sheet of polyethylene having a thickness of 0.2 mm and a sheet of EVAL having a thickness of 0.2 mm. The peel strength was not less than 2.0 kg/cm. For comparison, an adhesion test was carried out using a sheet of the composition which did not contain vinylsilane propylene random copolymer, inserted between a sheet of polyethylene and a sheet of EVAL. The sheets peeled autogeneously and the peel strength could not be measured. Example 3: Example 1 was repeated except allylsilane was used instead of vinylsilane to produce an alkenyl-α-olefin random copolymer having a melting point of 152°C, an η of 1.28 dl/g, and an allylsilane content of 2.1 weight percent. The peel strength was not less than 2 kg/cm. Example 4: Random copolymerization of ethylene and vinylsilane was carried out as follows: (a) Preparation of Random Copolymer of Vinylsilane and Ethylene To a pressure-tight glass autoclave having an inner volume of 200 ml the following were added: 40 ml of toluene, 50 mg of the transition metal catalyst obtained in Example 1(a), 0.128 ml of diethylaluminum chloride, 0.06 ml of p-toluic acid methyl ester and 0.20 ml of triethylaluminum in an atmosphere of nitrogen. To the resultant mixture the following were charged: 4.0 g of vinylsilane hydrogen up to a pressure of 0.2 kg/cm² (19.6 kPa), ethylene up to a pressure of 1 kg/cm² (98 kPa). Polymerization was then carried out at 70°C for 2 hours. After the polymerization reaction, the polymer containing slurry was removed and subjected to filtration and then dried. 63 g of random copolymer powder were obtained. The η was 1.81 dl/g, the melting point was 126°C and the crystallizing temperature was 104°C. The amount of polymerized vinylsilane in the random copolymer was calculated by analyzing silicon and was found to be 1.3 weight percent. (b) Preparation of Polyethylene A polyethylene having an η of 1.88 dl/g was obtained by a homopolymerization process. (c) Preparation of the Composition To 200 g of polyethylene powder were added 10 g of the ethylene-vinylsilane random copolymer, 0.2 g of phenol type stabilizers and 0.3 g of calcium stearate. The resulting mixture was granulated to prepare a composition for adhesive materials. (d) Adhesion Test The peel strength test was carried out in the same manner as in Example 2 and the peel strength of the sheets was not less than 2 kg/cm. (e) Comparison For comparison, the adhesion test was carried out in the same manner as above except a sheet of the composition which did not contain an ethylene-allylsilane copolymer was employed as the middle sheet in the multi-layer structure. The sheets peeled autogeneously and the peel strength could not be measured. Example 5: A resin composition was prepared by mixing and granulating 10 g of the ethylene-vinylsilane random copolymer obtained in Example 4(a), 200 g of the ethylene propylene copolymer obtained in Example 1(c), and the same amounts of additives as in Example 4(c). This composition was used as an adhesion layer between a sheet of propylene ethylene copolymer obtained in Example 1(c) and a sheet of EVAL. The adhesion test was carried out in the same manner as in Example 1(e). The peel strength was not less than 2 kg/cm. Example 6: The random copolymerization was carried out in the same manner as in Example 4(a) except that allylsilane was used instead of vinylsilane. The random copolymer of ethylene-allylsilane, which contained 1.81 weight percent of allylsilane, having a melting point of 123°C and an η of 1.31 dl/g, was obtained. The composition was prepared by mixing the ethylene allylsilane random copolymer, polyethylene and additives as in Example 4(c). The peel strength was measured in the same manner as in Example 4(d) and was found to be not less than 2 kg/cm. Example 7: 2 parts by weight of the propylene vinylsilane random copolymer obtained in Example 1(b), 97 parts by weight of polypropylene (η was 1.65 dl/g. I.I. was 97.1%), 0.2 parts by weight of phenol type stabilizers, and 0.3 parts by weight calcium stearate were mixed in a Henschel mixer for 5 minutes, followed by granulation by a 20 mm ⊘ extruder at 220°C. The pellets obtained were compression molded at 220°C and a pressure of 100 kg/cm² (9˙8 mPa) to form a 200 µm sheet. To determine the strength of adhesion between the sheet and aluminum, aluminum plates 10 µm thick degreased with acetone were employed in the order of aluminum plate-sheet-aluminum plate to form a multi-layer structure. The resulting formation was pressed at 230°C under 10 kg/cm² (0˙98 mPa) for 10 minutes and then cooled with water to form a laminated plate. The peel strength was 1.8 kg/cm. Comparison The test was repeated in the same manner except that the middle sheet did not contain a random copolymer of vinylsilane and propylene. The laminated plate peeled autogeneously and the peel strength could not be measured. Example 8: Example 7 was repeated except the random copolymer of propylene and allylsilane obtained in Example 3 was used in place of the vinylsilane propylene copolymer. The peel strength was 1.6 kg/cm. Example 9: Example 7 was repeated except a galvanized iron sheet (JIS-J-3302) was used instead of an aluminum plate. The peel strength was 1.1 kg/cm. Comparison The test was repeated in the same manner except that a composition that did not contain a random copolymer of vinylsilane and propylene was used to form the middle sheet. The laminated sheets peeled autogeneously and the peel stremgth could not be measured. Example 10: Example 7 was repeated except that a soft iron sheet was used in place of the aluminum plate, and the sheet obtained in Example 8 was used. The peel strength was 1.7 kg/cm. Comparison The test was repeated except a composition that did not contain a random copolymer of vinylsilane and propylene was used for the middle sheet. The laminated sheets peeled autogeneously and the peel strength could not be measured. Example 11: 10 g of the propylene-vinylsilane random copolymer obtained in Example 1(b), 200 g of polyethylene obtained by polymerizing ethylene using the catalyst obtained in Example 1(a), 0.2 g of phenol type stabilizers and 0.3 g of calcium stearate were mixed and then granulated to prepare a composition for easy coating materials. Strength of Coating Test To determine the strength of coating, the composition was further compression-molded at 220°C and 40 kg/cm² (3˙9 mPa) to obtain a sheet having a thickness of 1 mm. Specimens of the sheet were separately coated with two kinds of coatings (Olestar 2182: product of Mitsui Toatsu Chemicals, Inc.) as a urethane coating and Unirock (product of Rock Paint, Inc.) as an acrylic coating by brush. The specimens were baked and dried in an air oven at 60°C for 30 minutes. The strength of adhesion of the coated film was measured for the specimens applied with the coatings accordng to the procedure of JIS K-5400 (the cross hatch test). The number of cross-cut residual coated films were respectively as excellent as 100 out of 100. For comparison, the test was repeated except a composition that did not contain a random copolymer of propylene and vinylsilane was used for the composition for easy coating materials. The number of cross-cut residual coated films were respectively 5 and 10. Example 12: The random copolymerization was carried out in the same manner in Example 4(a) except that allylsilane was used instead of vinylsilane and the amount of hydrogen charged was 0.1 kg/cm² (9˙8 kPa) instead of 0.2 kg/cm² (19˙6 kPa). Thus, the random copolymer of ethylene and allylsilane which contained 1.7 weight percent allylsilane, having a melting point of 126°C and an intrinsic viscosity of 1.48 dl/g was obtained. The random copolymer and an ethylene-butene-1 copolymer and additives were mixed to prepare a composition. The strength of coating was repeated in the same manner as in Example 11. The number of cross-cut residual coated films were both as excellent as 100 out of 100. For comparison, the test was repeated except a composition not containing a random copolymer of ethylene and allylsilane was used as the composition for easy coating. The number of cross-cut residual coated films were respectively 5 and 10 out of 100. Example 13: The composition obtained in Example 4 was used as the composition for easy coating. The test was carried out in the same manner as in Example 11. The number of cross-cut residual coated films were respectively as excellent as 100 out of 100. For comparison, the strength of the coating test was repeated except a composition that did not contain a random copolymer of ethylene and allylsilane was used as the easy coating material. The number of cross-cut residual coated films were respectively 5 and 10. Example 14: The random copolymer of ethylene and allylsilane obtained in Example 12 (containing 1.7 weight percent of allylsilane, having a melting point of 126°C and an η of 1.48 dl/g), polypropylene (Mitsui Noblen JHH-G, Mitsui Toatsu Chemicals, Inc.) and additives were mixed to prepare a composition. The strength of coating test was repeated in the same manner as in Example 11. The number of cross-cut residual coated films were both 100 out of 100. For comparison, the test was repeated except a random copolymer of ethylene and allylsilane was used as the easy coating material. The number of cross-cut residual coated films were respectively 5 and 5. Example 15: The test was repeated in the same manner as in Example 14 except that 5 g, rather than 10 g, of random copolymer of the ethylene-allylsilane compound were employed. The number of cross-cut residual coated films were respectively 85 and 90. Example 16: The strength of coating test was repeated in the same manner as in Example 15 except that 0.1 g of lithium ethoxide was added to the composition. The number of cross-cut residual coated films were both 100. For comparison, the test was repeated except that a composition that did not contain a random copolymer of ethylene and allylsilane was used as the easy coating material. The number of cross-cut residual coated films were both 5. Example 17: Polypropylene (η was 1.65 dl/g and I.I. was 97.1%) was obtained according to the same manner as in Example 1(b) except that vinylsilane was not added. 200 g of polypropylene, 10 g of the random copolymer of propylene and vinylsilane obtained in Example 1(b), 0.2 g of phenol type stabilizers and 0.3 g of calcium stearates were mixed and granulated to prepare a composition for easy coating. The strength of coating test was repeated in the same manner as in Example 11. The number of cross-cut residual coated films were both 100. For comparison, the strength of coating test was repeated except that a composition that did not contain a random copolymer of ethylene and vinylsilane was used as an easy coating material. The number of cross-cut residual coated films were 5 and 10. Example 18: The strength of coating test was repeated in the same manner as in Example 17 except that 5 g, rather than 10 g, of a random copolymer of propylene-allylsilane compound were employed. The number of cross-cut residual coated films were respectively 90 and 95. Example 19: The composition obtained in Example 18 was molded to a sheet. The sheet was subjected to a treatment in ethanol at 40°C for one hour. The test was then repeated in the same manner as in Example 11. The number of cross-cut residual coated films were both 100. Thus, by treating multi-layer structures containing the composition of the invention with alcohol, the adhesive and coating properties of the structure are improved.

Claims: Use, as an adhesive of a polyolefin resin composition containing a random copolymer of an α-olefin and an alkenylsilane represented by the formula (I) H₂C = CH - (CH₂) n - SiH m R (3 - m) wherein n is 0 or an integer of from 1 to 12, R is selected from the group consisting of a methyl and a phenyl radical, and m is an integer of from 1 to 3, when making an article by bonding a first layer to a second layer of the article, said first layer being formed of a polyolefin and said second layer consisting of a metal or a polymer containing polar groups. A process of making a shaped article, comprising the steps of (a) shaping the article from a polyolefin resin composition containing a random copolymer of an α-olefin and an alkenylsilane represented by the formula (I). H₂C = CH - (CH₂) n - SiH m R (3-m) wherein n is 0 or an integer of from 1 to 12, R is selected from the group consisting of a methyl and a phenyl radical, and m is an integer of from 1 to 3, and (b) coating the article with a metal or a polymer containing polar groups. The use/process of claim 1 or claim 2, wherein said alkenylsilane is present in an amount of from 1 weight ppm to 30 weight percent of the random copolymer. The use/process of claim 3, wherein the weight percent is from 10 weight ppm to 30 weight percent of the random copolymer. The use/process of any of claims 1 to 4, wherein said alkenylsilane is selected from the group consisting of vinylsilane, allylsilane, butenylsilane and pentenylsilane. The use/process of any of claims 1 to 5, wherein said α-olefin is a C₂ - C₁₂ olefin. The use/process of claim 6 wherein said α-olefin is selected from the group consisting of ethylene, propylene, butene-1, pentene-1, hexene-1, 2-methylpentene-1, octene-1 and a mixture of at least two of said compounds. The use/process of any of claims 1 to 7, wherein said random copolymer is blended with at least one polyolefin. The use/process of claim 8, wherein said random copolymer is blended with at least one homopolymer or copolymer of an α-olefin. The use/process of claim 8, wherein the olefin is a random or a block copolymer. The use/process of claim 8, wherein the weight percent of alkenylsilane is from 1 weight ppm to 1 weight percent. The use/process of any preceding claim, wherein said random copolymer has an intrinsic viscosity measured at 135° C in a tetralin solution of from 0.1 dl/g to 10 dl/g, e.g. 0.1 to 5 dl/g. The use/process of any preceding claim, wherein said polyolefin resin composition contains an additive such as an anti-oxidizing agent or an ultraviolet light absorber. The use/process of claim 3, wherein said polyolefin resin composition contains an additive and a catalytic compound that activates the Si-H bond.

Inventors: ASANUMA TADASHI, OHNAKA JUNKO, TOKURA YOSHIKO, YAMAMOTO KAZUHIKO, ASANUMA, TADASHI, OHNAKA, JUNKO, TOKURA, YOSHIKO, YAMAMOTO, KAZUHIKO
Applicants: MITSUI TOATSU CHEMICALS, MITSUI TOATSU CHEMICALS, INC.
Application year: 1988
Main classification: C08F230
IPC codes: C09J143, C09D143, C08F297, C08F210, C09D153, C08F230, C09J153