FERROELECTRIC LIQUID CRYSTAL COMPOSITION

Abstract: A ferroelectric liquid crystal composition, which may be used in a light switching element, comprises a ferrorelectric liquid crystal composition comprising three liquid crystal components A, B and C, and containing from 10 to 70% by weight, based on the total of components A, B and C, of component A which comprises one or more compounds of the formulae: (in which R¹ and R² are the same or are different and each is a C₁-C₁₈ group), and (in which R³ and R⁴ are the same or are different, and each is a C₁-C₁₈ alkyl or C₁-C₁₈ alkoxy group); from 10 to 50% by weight, based on the total of components A, B and C, of component B which comprises one or more compounds of the formula: (in which R⁵ is a C₁-C₁₈ alkyl group, n is 0 or an integer from 1 to 10; and * indicates an asymmetric carbon atom); and from 10 to 40% by weight, based on the total of components A, B and C, of component C which comprises one or more compounds of the formuale: (in which R⁶ is a C₁-C₁₈ alkyl or C₁-C₁₈ alkoxy group and * represents an assymmetric carbon atom), and (in which R⁷ is a C₁-C₁₈ alkyl group or C₁-C₁₈ alkoxy group and * indicates an asymmetric carbon atom).

Description: This invention relates to ferroelectric liquid crystal materials. More particularly it relates to ferroelectric liquid crystal compositions comprising smectic liquid crystal compound(s) and optically active compound(s) and having high-speed response properties; and to a light switching element using such ferroelectric liquid materials. Liquid crystal compounds have been widely used for liquid crystal elements, but such liquid crystal display elements are of the TN display mode, and as liquid crystal materials, those belonging to the nematic phase have been used. Since the TN display mode is non-emissive, it has the advantages that it does not tire the eyes and its power consumption is small, but, on the other hand, it has drawbacks in that the response is slow and the display may not be visible depending on the angle of view. Thus, this display mode has recently been used, to make the best use of its characteristics, as a flat display, and in particular, high-speed response properties and a broad angle of view have been required. Various improvements in liquid crystal materials in response to such requirements have been attempted. However, as compared with other emissive displays such as electroluminescence display, plasma display, etc., the TN display mode is considerably inferior in response time and breadth of angle of view. In order to make the best use of the specific features of liquid crystal display elements such as non-emissive mode and lower power consumption and also to secure response properties matching those of emissive displays, the development of a novel liquid crystal display mode in place of the TN display mode is desirable. In one proposal, a display mode utilizing the light switching phenomenon of ferroelectric liquid crystals has been suggested by N.A. Clark et al [see Appl. Phys. Lett., Vol. 36, p. 899 (1980)]. The presence of ferroelectric liquid crystals has been announced by R.B. Meyer et al for the first time [see J. Phys. vol. 36, p. 69 (1975)], and the phases of the crystals include a chiral smectic C phase, chiral smectic I phase, a chiral smectic F phase, a chiral smectic G phase and a chiral smectic H phase (hereinafter simply referred to as Sc* phase, S p * phase, S F * phase, S G * phase and S H * phase, respectively). Various specific features are required for ferroelectric liquid crystal materials for use as practicable ferroelectric liquid crystal display elements, but at present, there is no single compound which satisfies all the specific features; hence it is necessary to use ferroelectric liquid crystal compositions obtained by mixing liquid crystal compounds with each other or with non-liquid-crystal compounds. Ferroelectric liquid crystal compositions are not limited to those consisting only of ferroelectric liquid crystal compounds, but it has been reported that using compound(s) or composition(s) each exhibiting achiral smectic C, F, G, H, I phase or the like phase (hereinafter simply referred to as Sc phase or the like) as base substance(s), at least one compound exhibiting ferroelectric liquid crystal phases is mixed with the above compound(s) of composition(s) to constitute a ferroelectric liquid crystal composition as a whole (see Japanese laid-open patent application No. Sho 61-195187/1986). Further, it has also been reported that using compound(s) or composition(s) each exhibiting or S c phase or the like as base substance(s), in admixture with at least one compound which is optically active but exhibits no ferroelectric liquid crystal phase a ferroelectric liquid crystal composition as a whole may be obtained [see Mol. Cryst. Liq. Cryst., 89 , 327 (1982)]. In brief, it is seen that when at least one optically active compound, irrespective of whether or not it exhibits a ferroelectric liquid crystal phase, is mixed with a base copound, it is possible to provide a ferroelectric liquid crystal composition. A smectic liquid mixture comprising the above-mentioned base substance exhibiting at least one achiral S c or the like and having at least one S c phase or the like will hereinafter referred to as a "smectic base mixture". As such smectic base mixture, liquid crystal mixtures exhibiting an S c phase within a broad temperature rance including room temperature are preferred in practice. As as a component of the smectic base mixture, compounds selected from among liquid crystal compounds of e.g. phenylbenzols, Schiff's bases, phenylpyrimidines, 5-alkyl-2-(4-alkoxyphenyl)-pyrimidines, etc. have been used. For example, laid-open Japanese patent application No. Sho 61-291679/1986 and PCT International publication No/ WO i86/06401 disclose a ferroelectric liquid crystal obtained by mixing a 5-alkyl-2-(4-alkoxyphenyl)-pyrimidine with an optically active compound, and the former publication discloses that the use of a ferroelectric smectic liquid crystal material using the above pyrimidine derivative as a smectic base mixture makes it possible to shorten the response time of light switching elements. Further the above former publication also discloses that a ferroelectric liquid crystal material consisting of a 5-alkyl-2-(4′-alkylbiphenylyl-4)-pyrimidine, the above 5-alkyl-2-(4-alkyloxyphenyl)pyrimidine and an optically active compound is also effective for improving response properties. However, as compared with liquid crystal displays of other modes such as an emissive display, a further improvement in the response properties is desirable. A further problem requiring solution, in addition to improvement in response properties, is to reduce the temperature-dependency of the response time. Current ferroelectric liquid crystal materials have a large temperature-dependence of the response time so that a cross-talk phenomenon often occurs due to environmental temperature change to markedly reduce the display quality of the display. Thus, a ferroelectric liquid crystal material having a small temperature-dependence of the response time together with high-speed response properties is desirable. It has now been found, in accordance with the present invention that when liquid crystal compounds are combined together as specified below, a ferroelectric liquid crystal composition having high-speed response properties and also a small temperature-dependency of the response time may be obtained. According to one embodiment of the invention there is provided a ferroelectric liquid crystal composition comprising three liquid crystal components A, B and C, and containing (i) from 10 to 70% by weight, based on the total of components A, B and C, of component A which comprises one or more compounds of the formulae: (in which R¹ and R² are the same or are different and each is a C₁-C₁₈ alkyl group), and (in which R³ and R⁴ are the same or are different, and each is a C₁-C₁₈ alkyl or C₁-C₁₈ alkoxy group); (ii) from 10 to 50% by weight, based on the total of components A, B and C, of component B which comprises one or more compounds of the formula: (in which R⁵ is a C₁-C₁₈ alkyl group, n is 0 or an integer from 1 to 10; and * indicates an asymmetric carbon atom); and (iii) from 10 to 40% by weight, based on the total of components A, B and C, of component C which comprises one or more compounds of the formulae: (in which R⁶ is a C₁-C₁₈ alkyl or C₁-C₁₈ alkoxy group and * represents an assymmetric carbon atom), and (in which R⁷ is a C₁-C₁₈ alkyl group or C₁-C₁₈ alkoxy group and * indicates an asymmetric carbon atom). The invention also provides a light switching element containing a liquid cyclal composition as defined above. Reference will be made, in the following description, to the accompanying drawings, in which: Fig. 1 is a graph illustrating the concentration dependencies of the response time of the respective mixture systems of a ferroelectric liquid crystal composition A of the present invention with a smectic base composition B, the proportions of A to B being varied; Fig. 2 is a graph illustrating the respective temperature dependencies of the response time of ferroelectric liquid crystal compositions C and D; and Fig. 3 is a graph illustrating the respective temperature dependencies of the response time of ferro electric liquid crystal compositions C and E. The compounds of the formulas (I) and (II) constituting the component (A) used in the invention are achiral compounds, but have an S c phase or the like and also have a very low viscosity; hence they are very useful as a smectic base mixture. The usefulness of the compounds has already been described by the present inventors in Japanese patent application laid-open No/ Sho 61-291679/1986, and the compounds are also very effective as a component of the ferroelectric liquid crystal composition aimed in the present invention. Similarly, the compound of the formula (III) constituting the component (B) is a halogen-containing heterocyclic compound previously applied for patent, the invention having been made by the present inventors (Japanese patent application No. Sho 61-10578/1986). The spontaneous polarization value of the compound is not so large, but the compound has Sc* phase within a very low temperature range; hence it is useful as a base liquid crystal compound for low temperatures. Further, as will be described later, it has been found by the present inventors for the first time that the compound also has an effect of reducing the temperature dependency of the response time of ferroelectric liquid crystal compositions. Similarly, the compounds of the formulas (IV) and (V) constituting the above component (C) are halogen-containing optically active liquid crystal compounds previously applied for patent, the invention having been made by the present inventors, and already laid open (Japanese patent application laid-open No. Sho 61-210056/1986) and has a very large spontaneous polarization value. Compounds having among the spontaneous polarization value (abbreviated to Ps), the viscosity (abbreviated to η) and the response time (abbreviated to τ) of ferroelectric liquid crystal materials, a relationship of wherein E represents an intensity of electric field impressed to a liquid crystal cell, and having a low viscosity and also a large spontaneous polarization value have been desired. The compounds of the formulas (IV) and (V) constituting the component (C) play such a role in the ferroelectric liquid crystal composition. Further, it has also been found by the present inventors that these compounds also have an effect of reducing the temperature dependency of the response time of ferroelectric liuqid crystal compositions. The present inventors have examined the respective proportions of the components A, B and C in which proportions a liquid crystal composition having aimed superior specific features is obtained by making the best use of the respective specific features of the components A, B and C. As a result, as described above, the proportion of the component A is in the range of 10 to 70% by weight, that of the component B is in the range of 10 to 50% by weight and that of the component C is in the range of 10 to 40% by weight. The present invention is based on a combination of the respective superior specific features of the liquid crystal compounds of the above formulas (I) to (V). The superior specific features of the respective liquid crystal components will be described below in more detail. The compounds of the formulas (I) and (II) constituting the liquid crystal component A are both achiral compounds, but the compound of the formula (I) has Sc phase within a low temperature region (e.g. Cr 28 Sc 47 S A 58 N 66 I so in the case of the formula (I) wherein R¹ = C₆H₁₃- and R² = C₈H₁₇-), whereas the compound of the formula (II) has Sc phase within a high temperature region (e.g. Cr 58 Sc 134 S A 144 N 157 I so in the case of the formula (II) wherein R³ = C₇H₁₅- and R⁴ = C₈H₁₇-). Thus, by combining the compound of the formula (I) with that of the formula (II), a smectic base mixture having Sc phase over from a low temperature region to a high temperature region is obtained. The superior specific features of the compound having this skeleton have already been described by the present inventors in Japanese patent application laid-open No. Sho 61-291679/1986, and since it has a very low viscosity, it also plays an important role as a smectic base mixture in the ferroelectric liquid crystal composition aimed in the present invention. Fig. 1 shows the concentration dependency of the response time of a mixture system of a ferroelectric liquid crystal composition A (phase transition points: ∼Sc* 55 S A 69 N* 76 I so ) composed of chiral smectic liquid crystal compounds with a smectic base composition B (phase transition points: Cr 4 Sc 65 S A 79 N 90 I so ) composed of achiral liquid crystal compounds. The measured temperature is 25°C, the intensity of electric field is 5V/µm and the proportions of the respective compositions are as follows: As seen from Fig. 1, as the composition B is added to the composition A, the response becomes faster, and the effectiveness of addition of the composition B is observed as far as 60% by weight in terms of the concentration of the composition B. However, beyond this concentration, the response time becomes slow; hence such higher concentrations are not practical. In view of the fact that the use object of the compounds of the component A consists in use as a smectic base compound, the concentration of the liquid crystal component A is preferred to be in the range of 70% by weight or less. The compound of the formula (III) constituting the liquid crystal component B is a chiral compound and its spontaneous polarization value is not so large, but the compound has Sc* phase within a very low temperature region (e.g. Cr 7 Sc* 31 S A 33 I so in the case of the formula (III) wherein R⁵ = C₆H₁₃- and n = 5); hence the component B also plays an important role as a liquid crystal base compound like the liquid crystal base component A in the ferroelectric liquid crystal composition aimed in the present invention. The compound having this skeleton is a compound previously applied for patent, the inventors of the application being the present inventors (Japanese patent application No. Sho 61-10578/1986). As a result of various examinations made later, a surprising effect of the compound has been found by the present inventors for the first time. Fig. 2 shows the respective temperature dependencies of the response time of the following ferroelectric liquid crystal compositions C and D: Composition C consists of the above-mentioned smectic base composition B and a chiral smectic liquid crystal compound A shown below (phase transition points of the C: ∼Sc* 62 Sc 74 N* 87 I so ). Composition D consists of the smectic base composition B, a chiral smectic liquid crystal compound A shown below and chiral smectic liquid crystal compounds B and C each of the formula (III) and shown below (phase transition points of the D: ∼Sc* 53 S A 70 N* 75 I so ). The intensity of electric field is 5V/µm and the respective proportions of the compositions C and D are as follows: As seen from Fig. 2, when the composition C is compared with the composition D, there is a tendency that the response times of the two compositions are to a similar extent within a temperature region of 20° to 40°C i.e. the vicinity of room temperature to higher temperatures, whereas the response time of the composition D is fater than that of the composition C within a lower temperature region of 0° to 20°C. The ratio of the response time at 0°C to that at 40°C is about 10 in the case of the composition C, while it is about 6.9 in the case of the composition D, that is, the temperature dependency of the composition C is very small. The difference between the composition C and the composition D consists only in that a moiety (40% by weight) of the smectic base composition B (80% by weight) in the composition C is replaced by the compound B and the compound C each of the formula (III) in the composition D. Thus, the fact that the temperature dependency of the response time of the composition D is better than that of the composition C is considered to be affected by the compound B and the compound C. Namely, it is seen that use of the compound of the formula (III) affords a small temperature-dependency of the response time. Since the component B compound has Sc* phase within a very low temperature region, the upper limit temperature of Sc* phase lowers when the compound is used too much (for example, comparison of the upper limit temperature of Sc* of composition C with that of composition D); hence such excess quantity is undesirable. Thus, the concentration range of the liquid crystal component B in the ferroelectric liquid crystal composition aimed in the present invention is preferably 50% by weight or less. The compounds of the formulas (IV) and (V) as the liquid crystal component C are chiral compounds previously applied for patent in Japan by the present applicants and already laid open (Japanese patent application laid-open No. Sho 61-210056/1986), which compounds exhibit Sc* phase within a high temperature region and also have a very large spontaneous polarization value (for example, in the case of a compound of the formula (IV) wherein R⁶ = C₈H₁₇0-, the phase transition points: Cr 52 Sc* 104 N* 109 I so , Ps: 132 nC/cm² (T - Tc = -30°C), and in the case of a compound of the formula (V) wherein R⁷ = C₇H₁₅0-, the phase transition points: Cr 69 Sc* 95 S A 106 I so , Ps: 93 nC/cm² (T - Tc = -30°C). Thus, the above compounds are important ones playing a role of developing high-speed response properties and also improving the upper limit temperature of Sc* phase of the composition in the ferroelectric liquid crystal composition aimed in the present invention. Further it has been found by the present inventors for the first time that these compounds have a surprising effect of reducing the temperature-dependency of the response time of ferroelectric liquid crystal compositions as in the case of the compound of the formula (III) as the liquid crystal component B. Fig. 3 shows a chart illustrating the respective temperature-dependencies of the response time in the above-mentioned ferroelectric liquid crystal composition C and a ferroelectric liquid crystal composition E (phase transition points: ∼Sc* 65 S A 74 N* 86 I so ) consisting of the above-mentioned smectic base composition B and a chiral smectic liquid crystal compound D which is a compound of the formula (IV). The intensity of the electric field if 5V/µm. The proportions of the composition E are as follows: Further, the spontaneous polarization value at 25°C of the composition C was 2 nC/cm² and that of the composition E was 5 nC/cm². As apparent from Fig. 3, the response time of the composition E is faster than that of the composition C and the temperature-dependency of the composition E is also less than that of the composition C (the ratio of the response times at 0°C and 40°C is about 10 in the case of the composition C and about 7.3 in the case of the composition E). The difference between the composition C and the composition E corresponds to the difference between the chiral smectic compound A and the chiral smectic compound D, and it has been found that by using the compound of the formula (IV), a ferroelectric liquid crystal composition having high-speed response properties and yet a small temperature-dependency of response time is obtained. Further, as apparent from Example 7 mentioned later, the compound of the formula (V) also has the same effectiveness as that of the compound of the formula (IV); hence it is anticipated that by using the compounds of the formula (IV) and the formula (V), a ferroelectric liquid crystal composition having a small temperature-dependency of response time may be obtained. Taking into account the respective concentration ranges of the liquid crystal component A and the liquid crystal component B, and also in view of the usefulness of the liquid crystal component C, the concentration range of the liquid crystal component C in the ferroelectric liquid crystal composition aimed in the present invention is preferred to be 40% by weight or less. The respective proportions of the liquid crystal components A, B and C in which proportions a ferroelectric liquid crystal composition having superior specific features, aimed in the present invention is obtained making the best use of the respective specific features of these components as described above are as follows: liquid crystal component A: 10 to 70% by weight, liquid crystal component B: 10 to 50% by weight, and liquid crystal component C: 10 to 40% by weight. Next, the foregoing will be described by way of examples. A ferroelectric liquid crystal composition F consisting of Sc compounds as the liquid crystal component A of the present invention and known chiral smectic liquid crystal compounds and having the following proportions was prepared: The phase transition points of this composition were as follows: The Ps at 25°C was 4.7 nC/cm², the tilt angle was 21° and the length of the helical pitch of Sc* phase was 5 µm. This liquid crystal composition F was filled in a cell of 2 µm thick provided with electrodes subjected to aligning treatment and a square wave of peak to peak (hereinafter abbreviated to V pp ) of 20V and 100 Hz was impressed to measure the response time. As a result, the time was 350 µ sec at 25°C. Further, the response time at 0°C and 40°C were 2m sec and 200 µ sec, respectively, and the ratio of the response times at 0°C and 40°C was 10. Further, a ferroelectric liquid crystal composition G consisting of Sc compounds as the liquid crystal component A and known chiral smectic liquid crystal compounds and having the following proportions was prepared: The phase transition points of this composition G were as follows: The Ps at 25°C was 5.9 nC/cm², the tilt angle was 24° and the length of the helical pitch of Sc* phase was 3 µm. This liquid crystal composition G was filled in the same cell as in the case of the composition F and the response time was measured to give 230 µ at 25°C. Further, the response times at 0°C and 40°C were 1.9 msec and 130 µ sec, respectively and the ratio of the response times at 0°C and 40°C was 14.6. On the other hand, a ferroelectric liquid crystal composition H comprising the liquid crystal components A, B and C of the present invention as shown below was prepared: The phase transition points of this composition H were as follows: The Ps at 25°C was 8 nC/cm², the tilt angle was 24° and the length of the helical pitch of Sc* phase was 3 µm. This liquid crystal composition H was filled in the same cell as in the case of the above composition F and the response time was measured to give 150 µsec at 25°C. Further, the response times at 0°C and 40°C were 600 µ sec and 80 µ sec, respectively, and the ratio of the response times at 0°C and 40°C was 7.5. As apparent from the foregoing, the ferroelectric liquid crystal composition comprising the liquid crystal components A, B and C of the present invention has far superior high-speed response properties and a small temperature-dependency of response time. Examples 1 to 11 The present invention will be described in more detail by way of Examples, but it should not be construed to be limited thereto. In addition, the spontaneous polarization value (Ps) was measured according to Sawyer-Tower method, and the helical pitch (P) was sought by using a cell of about 200 µm thick subjected to homogenous alignment and directly measuring the distance between dechiralization lines corresponding to the helical pitch under a polarizing microscope. The tilt angle (ϑ) was sought by impressing a sufficiently high electric field higher than the critical electric field to a cell subjected to homogeneous alignment to make the helical structure extinct, followed by inverting its polarity and observing the angle (corresponding to 2ϑ) at which the extinction position was transferred, under crossed nicols. The response time was sought by filling the respective compositions in a cell subjected to aligning treatment and having a distance between electrodes of 2 µm, impressing a square wave of V pp of 20V and 100Hz and observing the change in the intensity of transmitted light at that time. In addition, the compositions of Examples include those containing a chiral compound for extending the pitch of Sc* phase besides the above-mentioned respective components A, B and C, but such chiral compound does not damage the specific features of the ferroelectric liquid crystal composition aimed in the present invention; hence no problem is raised. Table 1 shows the component proportions of the ferroelectric liquid crystal compositions of the present invention in Examples 1 to 11 and Table 2 shows the values of their specific features. Further, the respective proportions in Table 1 are of percentage by weight.

Claims: A ferrorelectric liquid crystal composition comprising three liquid crystal components A, B and C, and containing (i) from 10 to 70% by weight, based on the total of components A, B and C, of component A which comprises one or more compounds of the formulae: (in which R¹ and R² are the same or are different and each is a C₁-C₁₈ alkyl group), and (in which R³ and R⁴ are the same or are different, and each is a C₁-C₁₈ alkyl or C₁-C₁₈ alkoxy group); (ii) from 10 to 50% by weight, based on the total of components A, B and C, of component B which comprises one or more compounds of the formula: (in which R⁵ is a C₁-C₁₈ alkyl group, n is 0 or an integer from 1 to 10; and * indicates an asymmetric carbon atom); and (iii) from 10 to 40% by weight, based on the total of components A, B and C, of component C which comprises one or more compounds of the formulae: (in which R⁶ is a C₁-C₁₈ alkyl or C₁-C₁₈ alkoxy group and * represents an assymmetric carbon atom), and (in which R⁷ is a C₁-C₁₈ alkyl group or C₁-C₁₈ alkoxy group and * indicates an asymmetric carbon atom). A light switching element containing a ferroelectric liquid crystal composition as claimed in claim 1.

Inventors: FURUKAWA, KENJI, ICHIHASHI, MITSUYOSHI, KIKUCHI, MAKOTO, TAKESHITA, FUSAYUKI, TERASHIMA, KANETSUGU
Applicants: CHISSO CORPORATION
Application year: 1988
Main classification: C09K19
IPC codes: C09K19, G02F1