Peelable barrier film for vacuum skin packages and the like

Abstract: Disclosed is a film (1) for forming vacuum skin packages which comprises a coextruded, multi-layer composite forming web comprising a gas permeable film (2) and a gas impermeable film (3) which can be manually delaminated from each other, the gas permeable film having a plurality of layers including a heat sealable, polymeric layer, and a layer comprising a linear ethylene/alpha-olefin copolymer having a density of less than 0.915 g/cc, the gas impermeable film having a plurality of layers including a barrier layer of a hydrolyzed ethylene/vinyl-acetate or vinylidene chloride copolymer the barrier layer being immediately adjacent to and in contact with the linear ethylene/alpha-olefin copolymer so that when the layers are peeled apart the barrier layer will become a first surface layer and, an outer or second surface layer of polymeric material: the heat sealable layer of the permeable film seals to the surface of the package support member with a bond strength greater than the force required to delaminate the permeable layer from the impermeable layer so that the permeable layer can be peeled from the impermeable layer leaving the package covered with a permeable layer so that oxygen can penetrate to the packaged product.

Description: This invention relates generally to thermoformable barrier films and to vacuum skin packages which can be made therefrom. Particularly the present invention relates to multi-layer gas barrier films wherein the barrier layer or layers may be peeled and separated from the gas permeable layer or layers. Skin packaging can be classified as a vacuum forming process for thermoformable polymeric films. The product on a supporting member serves as the mold for the thermoformable film which is formed about the product by means of differential air pressure. However. the term "vacuum skin packaging" or VSP as it is referred to hereinafter, refers not to the fact that the thermoformable film is formed around the product by vacuum or differential air pressure but to the fact that the product is packaged under vacuum and the space containing the product is evacuated. Thus, there is a need for the film formed around the product and for the support member to be a barrier to oxygen, air, and other gases. In conventional skin packaging, a backing board which is porous or which is perforated so that a vacuum may be drawn directly through the backing board is employed. In vacuum skin packaging processes generally a vacuum chamber with an open top is used. The product on an impervious backing board is placed on a platform within the vacuum chamber. The top of the chamber is covered by a sheet of film which is clamped tightly against the chamber to form a vacuum tight closure. The chamber is evacuated while the film is heated to its forming and softening temperature. The platform is then raised to drive the product into the softened film and air pressure can be used above the film to force it tightly around the product. A process of this type is disclosed in French Patent No. 1,258,357 which issued to Alain G. Bresson on March 6, 1961. A variant of the process described in the Bresson patent is disclosed in French Patent No. 1,286,018 which issued on January 22, 1962 to LaRoach Freres Limited. In the the LaRoach Freres process, after the chamber has been evacuated and the product driven into the heat softened film, the vacuum is released and ambient air is permitted to enter the chamber so that the thermoplastic film molds more or less onto the product since there is a vacuum on the product side of the film and ambient air pressure on the other side of the film. Australian Patent No. 245,774 which issued to Colbros Proprietary Limited et al on July 16, 1967 discloses a vacuum skin packaging process in which an article to be packaged is inserted within the lower half of a vacuum chamber on a backing board, a thermoplastic film is placed over the open face of the lower half of the chamber, the chamber is closed and both halves and are brought to essentially the same state of vacuum, the film is heated and softened and then atmospheric air is introduced into the upper half of the chamber so that it alone forces the thermoplastic film down around the product and against the backing board. Another prior art version of vacuum skin packaging is disclosed in U. S. Patent No. 3,491,504, which issued to W. E. Young et al on January 27, 1970, heat softened film is physically moved down over a stationary product and, in connection with air pressure, the softened thermoplastic film is molded onto the product. In U. S. Patent No. RE.30,009, which was reissued on May 29, 1979 to Richard R. Perdue et al, a thermoformable or heat softenable film sheet is drawn by differential air pressure against the concave interior surface of the upper portion of a vacuum chamber, the film is then heated by surface contact, and then, after evacuation of the chamber, air pressure is used to blow the heat softened film down over the product and against the backing board. The resulting package comprises the product positioned on the backing board which is gas impervious and the product is held there by the thermoformable film which has been formed around the product in the exact shape of the product so that it appears to be a "skin." The thermoformable film, as stated previously, is also gas impervious and usually will consist of a number of layers each of which performs a specific function. The product contact and backing member contact layer will be a sealing or heat sealable layer, an interior layer will typically be a barrier layer which comprises a vinylidene chloride copolymer (PVDC) or a hydrolyzed ethylene/vinyl-acetate copolymer (EVOH), and the outer surface layer will be an abuse layer to protect the barrier layer from scratches, pin holes, or from moisture attack. Accordingly, one general object of the present invention is to provide an improved thermoformable film for use in vacuum skin packaging processes. In U. S. Patent No. 3,574,642 which issued on April 13, 1971 to Carl Frederick Weinke, a package for and a method of packaging meats is disclosed. The package includes an inner oxygen-permeable member which may be either gas flushed or evacuated and an outer oxygen-impermeable member which may also be gas flushed or evacuated. The package preserves the freshness of the meat until the meat is ready to be marketed to the consumer. For marketing, the outer wrapper is removed nd the inner package is displayed at the meat counter for the consumer. Being oxygen-permeable, the inner wrapper admits oxygen to the interior of the package causing the fresh meat product to change to a bright red color which the consumer associates with freshness. The inner pouch of the Weinke package may consist of polyethylene film and the outer pouches may be cellophane film with a coating of saran (vinylidene chloride copolymer or PVDC.) Another patent showing portions of fresh meat individually packaged in oxygen permeable plastic film and inserted into an outer container of impermeable film is U. S. Patent No. 3,681,092 which issued to Oliver R. Titchness et al on August 1, 1972. Another prior art package is described in U. S. Patent No. 3,713,849 which issued to Paul E. Grindrod et al on January 30, 1973. In the Grindrod et al patent a fresh meat package having an outer oxygen impermeable lamina which is readily and entirely peelable from an inner oxygen-permeable lamina is disclosed The package includes means for initiating the peeling separation along an edge of the package. The outer oxygen barrier maintains meats in well preserved condition in spite of the purplish color which has low consumer appeal. Shortly prior to display for sale to the consumer the outer lamina is removed by the retailer and the product develops a healthy bright red "bloom" due to the high rate of oxygen permeation through the inner remaining film package. The material disclosed in Grindrod et al is a laminate of PVC/Saran and EVA/Saran. (EVA designates ethylene/vinyl-acetate copolymer and PVC designates polyvinyl-chloride.) The EVA and PVC layers are the inner layers and at the periphery of the package they are sealed together but form a weak bond. The saran layers can be readily peeled from the respective EVA or PVC layers as saran does not form a strong bond between either. Gripping tabs are also provided. Yet another peelable package is shown in U. S. Patent No. 4,055,672 which issued on October 25, 1977 to Arthur Hirsch et al. In the Hirsch et al patent a semi-rigid tray of oxygen impermeable material is formed, a meat product placed therein, and then the tray is sealed around its upper periphery or flange area by a composite lid which has an inner layer of oxygen permeable material, an adhesive layer, and an outer layer of oxygen impermeable material. When the package is ready for retail display so that oxygen can reach the fresh meat packaged within the tray, the outer impermeable lid is peeled away so that the oxygen can penetrate through the remaining oxygen permeable portion of the lid. Accordingly, another object of the present invention is to provide a package with a strippable or peelable barrier layer which is an improvement over prior art packages. In a number of instances in order to preserve a meat product within an impermeable film, it is desirable to provide a modified atmosphere which may include inner gases such as nitrogen or the like or an atmosphere which has a mixture of gases such as oxygen and carbon dioxide to control the bacterial growth within a package. Typical packages are disclosed in U. S. Patent No. RE.27,872 which issued on January 8, 1974 to J. J. Estes; U. S. Patent No. 2,623,826 which issued on December 30, 1952 to Sanford R. Grinstead; U. S. Patent No. 3,360,382 was issued on December 26, 1967 to H. V. Miller; U. S. Patent No. 4,522,835 which issued on June 11, 1985 to Richard E. Woodriff; U. K. Patent No. 1,199,998 which was published July 22, 1970; Canadian Patent No. 890,766 which issued January 18, 1972 to Charles M. Davison et al; U. K. Patent No. 1,378,140 which was published December 18, 1974; and in U. K. Patent No. 1,186,978 which was published April 8, 1970. U. S. Patent No. 2,925,346 which issued February 16, 1960 discloses a process of packaging cured meat products and inhibiting color degradation by removing oxygen and back filling the container with a gaseous oxide of nitrogen. Accordingly, it is another object of the present invention to provide a vacuum skin package which is suitable for and can be used with modified atmospheres. In order to readily open packages where plastic film layers have been sealed together to close the package, various tear tabs and easy open mechanisms have been devised. One such easy-to-open, delaminating seal is disclosed in U. S. Patent No. 4,638,913 which issued on January 27, 1987 to Milton A. Howe, Jr. In this patent, two grippable film folds are provided and the folds when pulled apart will rupture one of the outer layers of the sealed together film and delaminate the film to its edge. In such a case, of course, the bond strength between the two sealed together films must be greater than the layer-to-layer bond of the film. Accordingly, it is still another object of the invention to provide a package which it is readily openable. In one aspect, the present invention is a forming web for vacuum skin packaging which web is separable into permeable and impermeable films comprising a coextruded, multi-layer film web comprising a gas permeable film and a gas impermeable film which can be manually delaminated from each other, said gas permeable film having a plurality of layers including a heat sealable, polymeric layer, and, a layer comprising a linear ethylene/alpha-olefin copolymer having a density of less than 0.915 x 10³ kg/m³ (0.915 g/cc.) and, said multi-layer gas impermeable film comprising a plurality of layers including a barrier layer comprising a hydrolyzed ethylene/vinyl-acetate copolymer (EVOH), or vinylidene chloride copolymer or terpolymer (PVDC), for instance EVOH, said barrier layer being immediately adjacent to and in contact with said linear ethylene/alpha-olefin copolymer so that when delamination occurs the barrier layer will become a first surface layer, and, an outer or second surface layer of polymeric material; and, said heat sealable layer being capable of sealing to a polymeric surface with a bond strength greater than the force required to delaminate said permeable film from said impermeable film. In another aspect, the multi-layer gas impermeable film of said web comprises a first surface or barrier layer comprising EVOH and at least two internal layers between the two surface layers, one of said layers being an adhesive layer and the other layer being a second barrier layer comprising EVOH, said adhesive layer being positioned between the two EVOH layers. In particular the gas impermeable film may comprise: (i) a first surface or barrier layer comprising EVOH; (ii) a second or internal barrier layer comprising EVOH; (iii) adhesive layers on each side of the second barrier layer; and (iv) an outer or second surface layer of high density polyethylene. A preferred film comprises: (a) a first EVOH layer; (b) an adhesive layer on each side of the EVOH layer; (c) a second EVOH layer; and (d) the first and second EVOH layers being positioned between two outer polymeric layers. Such a film preferably comprises a layer comprising ULDPE or VLDPE immediately adjacent the side of the second EVOH layer which is opposite to the side on which the first EVOH layer is positioned. In yet another aspect, the peelable film of the present invention requires that the bond strength between the heat sealable layer and the polymeric surface is greater than the force required to rupture or tear the multi-layer permeable film so that the permeable film which has the heat sealable layer will rupture in a predetermined fashion rather than delaminate or peel from the polymeric surface to which it has been bonded. In another aspect, the heat sealing layer is selected from the group consisting of linear ethylene/alpha-olefin copolymers having a density of less than 0.915 x 10³ kg/m³, for example less than 0.910 x 10³ kg/m³ (0.910 grams/cc), (VLDPE) and ethylene/vinyl-acetate copolymers (EVA) having a vinyl-acetate content in the range of from 4% to 12%. In one embodiment of the films of the invention the gas impermeable film has a thickness of 3.0 to 3.5 mils (0.076-0.089 mm) and the gas permeable film has a thickness of 1.5 to 3.0 mils (0.038-0.076 mm). In a further embodiment films of the invention comprise an adhesive layer which layer comprises a blend of an LDPE based adhesive and HDPE. In yet another aspect, the present invention relates to a method of making a peelable barrier film which comprises a multi-layer, heat sealable composite film for thermoforming around a product to be packaged in a vacuum skin packaging operation, which comprises coextruding a multi-layer film in accordance with the invention. In still another aspect, the present invention provides a vacuum skin package wherein the forming web is a film in accordance with the invention. In the drawings which are appended hereto and made a part of this disclosure: Figure 1 is a perspective view of one embodiment of a vacuum skin package which can be made using the film and process of the present invention; Figure 2 shows one embodiment of a tab arrangement for delaminating or peeling apart the two films comprising the composite peelable film of the present invention; Figure 3 shows the peeling process shown in Figure 2 underway after rupture of a portion of the permeable film has taken place; and, Figure 4 is a schematic cross section of the composite film of the present invention. As used herein, the following abbreviations and terms have the meanings defined below: EVA : EVA designates ethylene/vinyl-acetate copolymers. HDPE : HDPE designates high density polyethylene resins. Such resins are generally made by the low pressure process and have a density of greater than (0.940 x 10³ kg/m³) 0.940 g/cc. LLDPE : LLDPE means linear low density polyethylene which generally is understood to include that group of ethylene/alpha-olefin copolymers having limited side chain branching and which fall into a density range of 0.910-0.940 x 10³ kg/m³ (0.910 to 0.940 g/cc). Sometimes linear polyethylene in the density range from 0.926-0.940 x 10³ kg/m³ (0.926 to 0.940) is referred to as linear medium density polyethylene (LMDPE). Typical brand names are Dowlex from Dow Chemical Company, Ultzex and Neozex from Mitsui Petro Chemical Company, and Sclair from duPont. The alpha-olefin copolymers are typically butene-1, pentene-1, hexene-1, octene-1, etc. Dowlex, Ultzex, Neozex and Sclair are Trade Marks. VLDPE and ULDPE : Very low density polyethylene (VLDPE) and ultra-low density polyethylene (ULDPE) mean ethylene/alpha-olefin copolymers which have a specific gravity of less than about 0.915 and, more specifically, usually 0.912 or below and may be below 0.89. Typical VLDPE resins are those designated DFDA by Union Carbide and are believed to principally or usually have butene, or isobutene as a comonomer. The very low density polyethylenes as compared to LLDPE, usually have significantly higher copolymer content and distinctly different properties making them a distinct class of polymers. Typically, resins designated "ULDPE" resins come from Dow and are believed to have octene as the comonomer. There is a slight difference in properties which is thought to be attributable to the comonomer. As used herein the term "linear ethylene/alpha-olefin copolymer having a density of less than 0.915 x 10³ kg/m³ (0.915 g/cc) encompasses both VLDPE and ULDPE. (See "Plastics Technology Magazine" for September, 1984 at Page 113 where an article entitled, "INTRODUCING VERY LOW DENSITY PE" appears.) EVOH : EVOH means ethylene-vinyl alcohol, sometimes abbreviated "EVAL" or hydrolyzed ethylene/vinyl-acetate and sometimes abbreviated "HEVA." EVOH resins are noted for their very good gas barrier properties but tend to be quite moisture sensitive. Typical suppliers of resins are Evalca in the United States and Toya Seiken in Japan.. BARRIER or "Impermeable Material :" BARRIER, as used herein, means a gas barrier having an oxygen transmission rate, for example, of less than 40 milliliters of oxygen per square meter for 24 hours as set forth in the above mentioned USP 3,574,642 for packaging fresh raw meat. Oxygen permeation rates considerably less than 40 can be achieved but for the purposes of this invention a film having a permeation rate of less than 40 will be considered a BARRIER or impermeable film or material. PERMEABLE MATERIAL : An oxygen or gas permeable material will be one having an oxygen permeation rate in excess of about 2,000 milliliters of oxygen per square meter for 24 hours. Obviously it is desirable to have as high a permeation rate as possible if the object is to introduce oxygen to the product when the barrier film is peeled away. OPTICAL LAYER : As used herein, an optical layer of a multi-layer film designates a layer included to enhance the appearance characteristics or a film so that a product packaged in the film will have a better appearance. LDPE : LDPE designates branched chain polyethylene made by the high pressure process and will have a density below 0.940 x 10³ kg/m³ (0.940 g/cc) and, most often a density of 0.915 to 0.925 x 10³ kg/m³ (0.915 to 0.925 g/cc) as the 0.926 to 0.939 x 10³ kg/m³ (0.926 to 0.939 g/cc) range is often referred to as the medium density range. Turning now to the description of the invention reference is first made to Figure 1 where vacuum skin package 1 is shown. This package comprises a support member 3 which is a gas impermeable member preferably formed of polyvinyl chloride material (PVC) as a substrate material coated with a barrier material and a heat sealing material; or, it can be a material such as a polystyrene foam which also is coated with a barrier material and a heat sealing material. Typical heat sealing materials are branched low density polyethylene (LDPE), ionomers such as the Surlyn brand sold by duPont, and EVA copolymers. The support member 3 may be flat as shown or it may be formed in the shape of a tray. The product 4 positioned on the support member 3 will, in general, be a food product such as fresh red meat. Particularly, the prime cuts of beef, pork, and lamb would be the preferred food products. When these products are vacuum skin packaged or packaged in an atmosphere in the absence of oxygen the fresh meat will tend to turn a purplish color and remain that way as long it is chilled and kept out of contact with oxygen. The bright red "bloom" is restored when the meat makes contact with oxygen again. The thermoformable film 2 which covers the product 4 and is sealed around the perimeter of the product in a manner to assume the exact shape of the product and, thus, become a "skin" is a composite film and is shown in greater detail in Figure 4. In Figure 4, which is a schematic representation of the layers in film 2, the two films 6 and 7 which make up the composite 2 are shown bonded at interface 8. Film 2 is preferably coextruded and as shown eight layers are coextruded together. The two layers 15 and 16 which form the interface 8 are materials which do not readily adhere one to the other and form a relatively weak bond. PVDC or EVOH is used for layer 15 and LLDPE is preferably used for layer 16. When the barrier or gas impermeable film employs a layer of PVDC as the barrier layer usually only an abuse layer 11 need be added with a suitable internal adhesive layer. This abuse material can be nylon, high density polyethylene, EVA, polypropylene, or the like. In some instances it may be necessary to have an adhesive layer and the selection of a proper adhesive is well within the skill of those in the art. In a preferred embodiment, in order to achieve very good barrier properties, two layers of EVOH are employed. The first layer 15 is the interface layer with layer 16 and the second layer 13 of EVOH is disposed between two adhesive or tie layers 12 and 14. The adhesive layer 12 is adhered to an abuse layer 11. Since the EVOH layer 13 is an interior layer it is protected from moisture attack and will retain its low oxygen permeability. Thus, even if moisture were to penetrate the weak bond between layers 15 and 16 at interface 8 during storage under moist conditions and significantly degrade the barrier properties of layer 15, layer 13 would be protected and would maintain the excellent barrier properties of the composite film. The gas permeable film 7 comprises an interface layer 16 of ULDPE. The center or core layer 17 of the permeable film 7 is EVA having 18% to 28% VA or an alternate material is VLDPE. The specific best mode of the forming web for vacuum skin packaging and the like which is separable into permeable and impermeable films has as the permeable skin film or layer 7 a construction as follows: Wherein: Sealant = VLDPE from Union Carbide, or, EVA copolymer having 4% to 12% VA from duPont Core = VLDPE, or, EVA copolymer having 18% to 28% VA content Optical = ULDPE from Dox, resins 4002A or 4002B The impermeable or peelable barrier film has the following construction: Wherein: EVOH = ethylene/vinyl-alcohol from Evalca LDPE(tie) = Adhesive, preferably Bynel from duPont (Bynel is a Trade Mark) EVA = EVA copolymer having 18% VA HDPE = High density PE from USI Using the best mode web, retail shelf lives between 23 and 28 days have been achieved for T-bone stem cuts whereas with the single layer of EVOH only about a seven day shelf life can be expected. It has also been found that the interface of EVOH/ULDPE between the permeable and impermeable films provides the easiest delamination or peeling of the barrier or impermeable film. Furthermore, the LDPE based tie or adhesive provides the best combination of adhesion to the EVOH layers plus moisture protection of the EVOH. To make the composite film or web, a coextrusion process similar to that described in USP 4,287,151 to Esakov et al on September 1, 1981 may be employed. Suitable annular multi-layer dies must, of course, be used and these are well known in the art. In an alternate structure which has fewer layers, the impermeable film 6 will be three layers, e.g., layers 11, 12, and 13 thus eliminating layers 14 and 15. Layer 13 is the barrier layer and is EVOH containing 32% to 44% ethylene. Layer 12 would is a blend of EVA with a modified EVA which is modified to serve specifically as an adhesive. One of the EVA based Plexar resins from Chemplex Company is preferred. The abuse or outer layer is HDPE. The permeable film 7 comprises branched low density polyethylene (LDPE), the core layer is EVA having 18% to 29% VA and the sealing layer comprises EVA having 2% to 4% vinyl-acetate content. In this alternate embodiment, the low density polyethylene (LDPE) interface with the EVOH layer is a weak coextruded bond which can be readily peeled apart. While this alternate structure does not provide the same moisture protection for the EVOH layer, it is nonetheless adequate for many applications. Looking now at Figures 2 and 3 tab 5 has been laid across one edge of the vacuum skin package as can be seen by the dotted line in Figure 1 so that in forming of upper web 2, the composite film, around product 4, it does not adhere to the supporting web or film 3. This allows for a tab to form as can be seen in Figure 2 that can be gripped and moved upwardly by the fingers to a position shown in Figure 3. In this position it can be seen that the permeable film 7 has torn or ruptured rather than break loose or delaminate its bond with the support member 3. This leaves the film portion 7′ firmly adhered to the support member 3. This type of strong bond is formed between the VLDPE or EVA surface of the film 7 with the coated PVC of the support member. Surfaces such as LDPE, EVA, and ionomers adhere strongly to each other and their bond strength is greater than the internal cohesive strength of film 7. Also seen in Figure 3 is the beginning of the delamination of the permeable film 7 from the impermeable film 6. The already peeled apart portion 6′ has separated from the bonded portion 7′ so that the entire impermeable film 6 may be peeled from the permeable film 7 leaving the inner "skin" package comprising support member 3, peeled, permeable film 7′, and product 4. When product 4 is a fresh red meat product, it will, within half an hour to an hour, regain its bright red bloom and is then ready for display in a showcase.

Claims: A forming web for vacuum skin packaging which web is separable into permeable and impermeable films comprising: a coextruded, multi-layer composite film comprising a gas permeable film and a gas impermeable film which can be manually delaminated from each other; (1) the gas permeable film having a plurality of layers including; (a) a heat sealable, polymeric layer; and, (b) a layer comprising a linear ethylene/alpha-olefin in copolymer having a density of less than 0.915 x 10³ kg/m³ (0.915 gms/cm³) and, (2) the gas impermeable film comprising a plurality of layers including: (a) a barrier layer comprising a hydrolyzed ethylene vinyl acetate copolymer (EVOH) or vinylidene chloride copolymer or terpolymer (PVDC), the barrier layer being immediately adjacent to and in contact with the linear ethylene/alpha-olefin copolymer (1) (b) so that when delamination occurs the barrier layer will become a first surface layer; and, (b) an outer or second surface layer of polymeric material; the heat sealable layer being capable of sealing to a polymeric surface with a bond strength greater than the force required to delaminate the permeable film from the impermeable film. A web according to claim 1 wherein the gas impermeable film comprises a barrier layer comprising EVOH. A web according to claim 2 wherein the gas impermeable film comprises a first surface or barrier layer comprising EVOH and at least two internal layers between the two surface layers, one of the layers being an adhesive layer and the other layer being a second barrier layer comprising EVOH, the adhesive layer being positioned between the two EVOH layers. A film according to claim 3 further comprising a second adhesive layer in addition to the first adhesive layer, the adhesive layers being positioned on each side of the second barrier layer. A web according to claim 4 wherein the gas impermeable film comprises: (i) a first surface or barrier layer comprising EVOH; (ii) a second or internal barrier layer comprising EVOH; (iii) adhesive layers on each side of the second barrier layer; and (iv) an outer or second surface layer of high density polyethylene. A web according to claim 3, 4 or 5 wherein the layer of the gas permeable film immediately adjacent the gas impermeable film comprises ULDPE or VLDPE. A web according to any one of the preceding claims wherein the gas permeable film comprises a heat sealing layer comprising a linear ethylene/alpha-olefin copolymer having a density of less than 0.915 x 10³ kg/m³ (0.915 g/cc) or an ethylene/vinyl-acetate copolymer having a vinyl-acetate content from 4% to 12%. A web according to any one of the preceding claims wherein the gas impermeable film has a thickness of 3.0 to 3.5 mils (0.076-0.089 mm) and the gas permeable film has a thickness of 1.5 to 3.0 mils (0.038-0.076 mm). A web according to any one of the preceding claims which comprises an adhesive layer which layer comprises a blend of an LDPE based adhesive and HDPE. A web according to claim 1 comprising: (a) a sealant layer having a thickness of about 0.20 to 0.60 mils (0.005 - 0.015 mm) and comprising a VLDPE or ethylene/vinyl-acetate copolymer having a vinyl acetate content of 4% to 12% by weight, the sealant layer being one surface layer; (b) a core layer having a thickness of about 1.75 to 2.50 mils (0.044-0.064 mm) and comprising a VLDPE or ethylene/vinyl-acetate copolymer having a vinyl acetate content 18% to 28% by weight, the core layer being adjacent to the sealant layer; (c) an optical layer having a thickness of about 0.10 to 0.20 mils (0.0025-0.0051 mm) and comprising a ULDPE resin, the optical layer being adjacent the core layer; (d) a first EVOH layer having a thickness of about 0.20 mils (0.0051 mm) and being adjacent to the optical layer; (e) a first tie layer comprising a blend of about 40% by weight of an LDPE based adhesive with about 60% by weight of HDPE, the tie layer having a thickness of approximately 20 mils (0.51 mm) and being adjacent the first EVOH layer; (f) a second EVOH layer having a thickness of approximately 0.20 mil (0.0051 mm) and being adjacent the first tie layer; (g) a second tie layer having a thickness of approximately 0.20 mil (0.0051 mm) and comprising the same material as the first tie layer, the second tie layer being adjacent the second EVOH layer; (h) a layer comprising ethylene/vinyl-acetate copolymer (EVA) having a vinyl acetate content of approximately 18% by weight, said layer being adjacent the second tie layer and being approximately 1.5 mils (0.038 mm) in thickness; and (i) a layer comprising HDPE adjacent the EVA layer, said layer being approximately 0.20 mil (0.0051 mm) thick and being an outside layer. A vacuum skin package wherein the forming web is a web according to any one of the preceding claims. A method of making a web as claimed in any one of claims 1 to 11, which comprises coextruding the multi-layer composite film.

Inventors: KENT ALAN DAVIS, SOLOMON BEKELE, WALKER STOCKLEY, KENT, ALAN DAVIS, SOLOMON, BEKELE, WALKER STOCKLEY,
Applicants: GRACE W R & CO, W.R. GRACE & CO.-CONN.
Application year: 1988
Main classification: B32B27
IPC codes: B65D75, B32B7