BITUMINOUS COMPOSITION

Abstract: Bituminous composition comprising a bitumen, an elastomeric, optionally hydrogenated, block copolymer containing at least two monoalkenyl arene blocks A and at least one conjugated diene block B which composition further comprises a polymer of a monovinylaromatic hydrocarbon of which polymer the number average molecular weight is the range of 1/4 to 2 times the number average molecular weight of the polymeric blocks A.

Description: The present invention relates to a bituminous composition especially suitable for roofing coatings, comprising bitumen and an elastomeric block copolymer or hydrogenated block copolymer of a monovinylaromatic hydrocarbon and a conjugated diene. Such compositions are known to have excellent elasticity, flexibility and adhesion properties, which render them especially suitable for use in roofing coatings. However, their resistance to flow is not always wholly satisfactory. US-A-4,585,816 discloses a method for the preparation of a blend of asphalt with a block copolymer of AB(BA)n configuration where n is an integer from 1 to 10, A is predominantly an alkenyl aromatic polymer and B is an elastomeric polymer. The document further discloses the addition of other components to the blend such as polymers and oligomers of ethylene, styrene and alpha-methylstyrene, hydrogenated poly(alpha-methylstyrene) oligomers and copolymers of alpha-methylstyrene and styrene. In accordance with the present invention, there is provided a bituminous composition comprising a bitumen, an elastomeric, optionally hydrogenated, block copolymer containing at least two mono alkenyl arene blocks A and at least one conjugated diene block B, and a homopolymer of a monovinylaromatic hydrocarbon, characterised in that the homopolymer of a monovinylaromatic hydrocarbon has a number average molecular weight in the range of 1/4 to 2 times the number average molecular weight of the polymeric blocks A. The bitumen used can be selected from any bitumen from natural or pyrogenous origin. Preferably, the bitumen is derived from a mineral oil. Suitable bitumen components derived from a mineral oil include a long residue, a short residue, a thermally cracked residue, precipitation bitumen or the blown product of each of the mentioned components. Propane or butane bitumen or blown propane or butane bitumen is very suitable, while mixtures of bitumen components can also be used. Also mixtures of bitumens and extender oils can be employed as bitumen component. Preferred bitumen components employed in the composition according to the invention include those having a penetration of at most 450 dmm at 25°C, and preferably in the range from 50 to 250dmm at 25°C. This property is determined according to ASTM-D5. Suitable mono alkenyl arene compounds to be used in blocks A of the elastomeric block copolymer include isopropenyl naphthalene, alpha-methyl styrene, vinyl toluene, vinyl xylene(s) and other styrene derivatives having one or more C 1-6 alkyl substituents. Styrene is particularly preferred. The polymeric blocks A in the elastomeric, optionally hydrogenated, block copolymer preferably have number average molecular weights of 5,000 to 50,000, more preferably from 10,000 to 35,000. Suitable conjugated dienes to be employed as block B of the elastomeric block copolymer includes dienes with 4 to 8 carbon atoms per monomer, in particular isoprene and butadiene. It is preferred that the proportion of the polymeric blocks A in the block copolymer lies in the range of 10 to 60%w, more preferably from 20 to 50%w. Higher proportions of monovinylaromatic hydrocarbons in the block copolymer can give rise to compatibility problems with the bitumen. These compatibility problems may manifest themselves as the formation of very viscous compositions that are difficult to handle, or in compositions from which the polymer of the monovinyl aromatic hydrocarbon separates into a discrete phase. Therefore, it is very surprising that in the present invention the addition of a polymer of a monovinylaromatic hydrocarbon does not involve any compatibility problem and that it even improves the flow resistance and storage stability. The polydiene block (or blocks) B has (have) preferably a number average molecular weight of 15,000 to 350,000, more preferably from 25,000 to 150,000. Suitable elastomeric block copolymers include linear, branched and star-shaped (radial) block copolymers. The polymeric blocks A preferably form the terminal blocks of the copolymer. Suitable linear copolymers can thus be represented by the formula A-B-(-B-A) n , in which n preferably ranges from 1 to 20, preferably 1 to 5, and suitable branched or star-shaped copolymer can be represented by the formula A-B-(-B-A) m in which m preferably is from 2 to 20. Any of these copolymers may optionally contain coupling agent residues included during their preparation. Extremely useful block copolymers are linear block copolymers having the configuration A-B-A, i.e. n is 1, and star-shaped block copolymers of configuration A-B-(B-A) m in which m is 2 - 8. The preparation of the block copolymer is known in the art. In British patent specification No. 1,538,266 a number of methods are described. For the preparation of star-shaped copolymers use can be made of suitable coupling agents such as diesters, like adipates, phosphites or silicon-compounds or a nucleus prepared by oligomerization of di- or tri-vinyl benzene. Other coupling agents can be selected from polyepoxides, such as epoxidized linseed oil, polyisocyanates, e.g. benzo-1,2,4-triisocyanate, polyketones e.g. hexane-1,3,6-trione, polyanhydrides or polyhalides. Especially when oligomers of di- or trivinyl benzene are used as coupling agents, the resulting star-shaped copolymer can have a large number of polymeric arms, e.g. 7-20 arms. The hydrogenation of the block copolymer, if desired, may be carried out as described in the above British patent specification. The monomer used in the preparation of the homopolymer of the monovinylaromatic hydrocarbon can be selected from the same monomers as used in the blocks A of the block copolymer. Suitable monomers include isopropenyl naphthalene, alpha-methyl styrene, vinyl toluene, vinyl xylene(s) and other styrene derivatives containing one or more C 1-6 alkyl substituents. Styrene is particularly preferred. Preferably, the number average molecular weight of the monovinylaromatic hydrocarbon homopolymer is 3,000 to 50,000, more preferably 5,000 to 40,000. As noted above, the molecular weight of this polymer should be from 0.25 to 2 times the molecular weight of the polymeric blocks A. Advantageously, the molecular weight is chosen such that the number average molecular weight of the homopolymer is from 0.4 to 1.5 times the molecular weight of the polymeric blocks A. In a practically very suitable situation the molecular weight of the homopolymer and the polymeric blocks A are about the same. The monovinylaromatic hydrocarbon homopolymer can be prepared by free-radical, anionic, cationic or coordination catalysis. Free-radical and cationic mechanisms yield polymers with a high degree of the random placement of the aromatic group relative to the backbone, i.e. these polymers are classified as amorphous. Polymers obtained by anionic mechanisms are usually amorphous, though under special conditions isotactic polymers can be prepared. Polymers prepared by coordination catalysis comprise mixtures of amorphous and isotactic polymers. Another known suitable polymerization technique is emulsion polymerization, as those skilled in the art will appreciate. The monovinylaromatic hydrocarbon homopolymer can also advantageously be produced simultaneously with the elastomeric block copolymer. The first step of this process involves contacting a mono vinyl arene and an initiator to form living polymers A. Suitable initiators include alkyllithium compounds. In the next step less than the stoichiometric amount of terminating agent required to kill all radicals is added to the reaction mixture. Typical terminating agents are water or alcohols. This results in the formation of polymers of monovinyl aromatic hydrocarbon with some living polymer blocks remaining in the reaction mixture. The living polymer blocks are then contacted with a conjugated diene. The then resulting living two-block intermediates can then be coupled to yield linear or branched or star-shaped copolymers, depending on the coupling agent used. The composition according to the present invention can conveniently be prepared by mixing the bitumen, the elastomeric block copolymer and the homopolymer of a monovinylaromatic hydrocarbon. The composition obtained is believed to differ from a composition obtained by reacting a bituminous material with monovinylaromatic hydrocarbon and the elastomeric block copolymer. In the latter case the monovinylaromatic hydrocarbon reacts with unsaturated bonds in the elastomeric copolymer and components of the bituminous material, resulting in the cross-linking of the bituminous material with the elastomeric block copolymer. The resulting composition, therefore, does not contain a discrete block copolymer and a discrete homopolymer of the monovinylaromatic hydrocarbon. The amounts of the elastomeric block copolymer and the homopolymer of a monovinylaromatic hydrocarbon in the composition according to the present invention can vary within wide ranges. Preferably the composition contains from 1 to 20%w of the elastomeric block copolymer and from 0.25 to 15%w of the homopolymer of the monovinylaromatic hydrocarbon, all weight percentages being based on the total weight of the bitumen, the elastomeric block copolymer and the homopolymer of the monovinylaromatic hydrocarbon. The composition according to the present invention can be used in road asphalt, pipe coatings, mastics and the like. When the composition is used in road asphalt, the amount of the polymers will normally be 1-10 %w, in pipe coatings, 5-15%w, in mastics, 5-15 %w, and in roofing coatings, 4-20 %w, based on the total of bitumen and the two polymers. The composition is particularly suitable for roofing coatings, and the invention, therefore, also includes the use of such a composition as a roofing coating. When used as a roofing coating, the composition is suitably employed in combination with a reinforcement. This reinforcement may comprise woven or unwoven fabrics or chopped fibres, preferably comprised of glass or polyester. The composition may further contain fillers, extenders, pigments or plasticizers. The composition of the present invention is suitable heated and applied to the fibres. Hence it is possible to prepare preformed membranes of the composition with a reinforcement. However, membranes consisting of the composition, i.e. without reinforcements, can also be prepared. Either type of membrane can be used as protective coating by applying the membranes onto a surface using heat and/or an adhesive, which adhesive can be relatively soft bitumen, or by other means known to those skilled in the art. The present composition can also be taken up in an emulsion, the emulsion can be sprayed onto the surface to be coated and after breaking of the emulsion a coating remains. The invention will further be illustrated by means of the following Examples. EXAMPLES In the experiments of the Examples two bitumens I and II were used each with a penetration of 200dmm at 25°C, bitumen I being a Venezuelan bitumen and bitumen II being a Middle East bitumen. As elastomeric block copolymer a star-shaped polymer of styrene (A) and butadiene (B) was used, the polymer having an average number of 3.5 arms of structure A-B, in which the blocks A have a number average molecular weight of 21,000 and in which the styrene content is 30 %w. The polystyrene used was prepared by anionic polymerisation unless otherwise indicated. Polystyrene with different molecular weights were employed. The properties tested included the softening point (T R&B ) of the mixtures (ASTM D36), the viscosity of the mixtures (ASTM D2171) and a resistance to flow and a cold bend test in accordance with German standard DIN 52123. According to this standard the mixture must pass a cold bend test at -15°C and a flow resistance test at 100°C. The procedure of this standard was modified for the mixtures by recording the highest temperatures at which they passed the flow resistance test. The temperature intervals between the flow resistance tests were 5°C. For some mixtures the storage stability was determined as follows. A can of 10 cm height was filled with the mixtures under nitrogen, the can was sealed, stored at 160°C for 5 days; then the can was sawed into halves, yielding a top fraction and a bottom fraction. The softening points of both fractions were determined, the value of the bottom fraction was deducted from that of the top fraction and the difference was recorded. The smaller the difference, the better was the storage stability. EXAMPLE 1 Mixtures were prepared of bitumen I (B-I) the elastomeric block copolymer (EBC) and polystyrene (PS) with a number average molecular weight of 15,000. The amounts of the components, and the properties of the mixtures are indicated in Table I. From the Table it is apparent that the addition of the polystyrene with the low molecular weight yields improved flow properties and improved storage stability. EXAMPLE 2 To show the effect of the molecular weight of the polystyrene, mixtures with the bitumens I and II, and with polystyrene having different molecular weights were prepared. Composition of the mixture and their properties are represented in Table II.

Claims: Claims for the following Contracting States : AT, BE, CH, DE, FR, GB, GR, IT, LI, LU, NL, SE Bituminous composition comprising a bitumen, an elastomeric, optionally hydrogenated, block copolymer containing at least two monoalkenyl arene blocks A and at least one conjugated diene block B, and a homopolymer of a monovinylaromatic hydrocarbon, characterised in that the homopolymer of a monovinylaromatic hydrocarbon has a number average molecular weight in the range of 1/4 to 2 times the number average molecular weight of the polymeric blocks A. Composition according to claim 1, wherein the monoalkenyl arene of polymeric blocks A is styrene, and the conjugated diene block B is isoprene or butadiene. Composition according to claim 1 or 2, wherein the polymeric blocks A have a number average molecular weight of 5,000 to 50,000, and the proportion of polymeric blocks A in the block copolymer is in the range of 10 to 60 %w. Composition according to any one of claims 1-3, wherein the block copolymer is a linear block copolymer having the configuration A-B-A, or a star-shaped block copolymer of configuration A-B-(-B-A) m , in which m is 2 - 8. Composition according to any one of claims 1-4, wherein the homopolymer of a monovinylaromatic hydrocarbon is polystyrene. Composition according to any one of claims 1-5, wherein the number average molecular weight of the homopolymer of a monovinylaromatic hydrocarbon is from 3,000 to 50,000. Composition according to any one of claims 1-6, wherein the amount of the elastomeric block copolymer is from 1 to 20%w and the amount of the homopolymer of a monovinylaromatic hydrocarbon is from 0.25 to 15%w, the weight percentages being based on the total weight of the bitumen, the elastomeric block copolymer and the homopolymer of a monovinylaromatic hydrocarbon. Composition according to any one of claims 1-7, wherein the bitumen has a penetration of at most 450dmm at 25°C determined according to ASTM-D5. Use as a roofing coating of a composition according to any of claims 1-8. Claims for the following Contracting State : ES A process for the preparation of a bituminous composition which comprises mixing a bitumen, with an elastomeric, optionally hydrogenated, block copolymer containing at least two monoalkenyl arene blocks A and at least one conjugated diene block B, and a homopolymer of a monovinylaromatic hydrocarbon, characterised in that the homopolymer of a monovinylaromatic hydrocarbon has a number average molecular weight in the range of 1/4 to 2 times the number average molecular weight of the polymeric blocks A. A process according to claim 1, wherein the monoalkenyl arene of polymeric blocks A is styrene, and the conjugated diene block B is isoprene or butadiene. A process according to claim 1 or 2, wherein the polymeric blocks A have a number average molecular weight of 5,000 to 50,000, and the proportion of polymeric blocks A in the block copolymer is in the range of 10 to 60 %w. A process according to any one of claims 1-3, wherein the block copolymer is a linear block copolymer having the configuration A-B-A, or a star-shaped block copolymer of configuration A-B-(-B-A) m , in which m is 2 - 8. A process according to any one of claims 1-4, wherein the homopolymer of a monovinylaromatic hydrocarbon is polystyrene. A process according to any one of claims 1-5, wherein the number average molecular weight of the homopolymer of a monovinylaromatic hydrocarbon is from 3,000 to 50,000. A process according to any one of claims 1-6, wherein the amount of the elastomeric block copolymer is from 1 to 20%w and the amount of the homopolymer of a monovinylaromatic hydrocarbon is from 0.25 to 15%w, the weight percentages being based on the total weight of the bitumen, the elastomeric block copolymer and the homopolymer of a monovinylaromatic hydrocarbon. A process according to any one of claims 1-7, wherein the bitumen has a penetration of at most 450dmm at 25°C determined according to ASTM-D5. Use as a roofing coating of a composition prepared by a process as claimed in any one of claims 1-8.

Inventors: BROUWER, HENDRIK JAN, BULL, ANTHONY LEONARD, VONK, WILLEM CORNELIS
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1988
Main classification: C08L95
IPC codes: C08L95, C08F297, C08L53