Mounting of optical fibers to integrated optical chips

Abstract: A fiber carrier (34) provides an effective coupling means between a cleaved facing surface of an optical fiber and a light port in a mounting surface (22) of an integrated optical device. Both the fiber carrier (34) and the integrated optical device (12) have an anisotropic thermal expansion property along the same known optic axis and both are substantially similar in magnitude to each other. The fiber carrier (34) is positioned with the integrated optical device (12) so that both the carrier optic axis is parallel to the device optic axis and so that an auxiliary surface (46) of the carrier is parallel to the device mounting surface (22). The optical fiber (40) is then bonded to the fiber carrier (34) so that the plane of the optical fiber cleaved facing surface lies in the plane of the carrier auxiliary surface. The carrier auxiliary surface (46) is finally bonded to the device mounting surface (22) so that the optical fiber cleaved facing surface is placed in registration with the light port in the device mounting surface.

Description: Technical Field This invention relates to the mounting optical fibers to integrated optic chips. Background Art The term "integrated optics" refers to a class of devices for guiding and controlling light in thin film layers or in narrow waveguide channels formed in a suitable dielectric material. The integrated optic (I/O) devices can be either of a single type including transducers, filters, modulators, memory elements, and others or of several functional applications combined ("integrated") onto a single device. Although several materials have been used for I/O device fabrication, one of the most widely used I/O device materials is lithium niobate. Lithium niobate is used primarily because of its optical and electro-optical properties. At room temperature, the atomic structure of lithium niobate belongs to the rhombohedral (trigonal) space group R3c and where the point group is 3m. This form of lithium niobate is stable up to the ferroelectric transition around 1200°C, where a transition to the nonpolar point group 3 m occurs. Crystallographers can measure parameters for lithium niobate as either a hexagonal or a rhombohedral unit cell. When measured as a rhombohedral unit cell, the atomic structure of lithium niobate exhibits an interaxial angle of approximately 56° and a unit cell axis length of approximately 5.5 angstroms. As a hexagonal unit cell, the atomic structure of lithium niobate has a unit cell axis length (a=b) of approximately 5.5 angstroms and a c axis length of approximately 13.8 angstroms. For purposes of this application the hexagonal unit cell shall be used to define the atomic structure of lithium niobate. Furthermore, lithium niobate is characterized by having large pyroelectric (i.e., spontaneous polarization of the crystal as a function of temperature), piezoelectric (i.e., induced polarization as a function of applied stress), photo-elastic (i.e., change in refractive index as a function of applied stress), and electro-optic (i.e., change in refractive index as a function of applied electric field) properties. It is also birefringent (i.e., linearly polarized electromagnetic waves will travel at two different velocities and along two perpendicular principal displacement directions) and exhibits a very strong bulk photovoltaic effect which also can produce a significant photo-refractive effect (i.e., change in refractive index as a function of the change in the optical intensity of the propagating light). See R. S. Weis and T. K. Gaylord: Appl. Phys. A37, P. 191-203 (1985). With all these optical and electro-optical properties, lithium niobate has found widespread application in laboratory and experimental systems. However, in order to make practical use of lithium niobate as an integrated optic device, numerous material problems still require solutions. One such problem is that lithium niobate devices still require a coupling device between themselves and optical fibers which functions over a wide range of environments (i.e., shock, vibration, and temperature). This inability to develop an environmentally stable coupling device stems from lithium niobate's strong anisotropic thermal expansion properties and from movement between the waveguide and the optical fiber. A strong anisotropic thermal expansion property means that the dimensional changes in the material associated with a temperature change differs in different directions in the crystal. Lithium niobate exhibits a thermal expansion property along the Z-axis (the Z-axis being defined as the axis about which the crystal exhibits three-fold rotation symmetry) in the range between 2 x 10⁻⁶/°C to 7.5 x 10⁻⁶/°C (Note: the variations being due to the various investigators' use of different materials, measurement techniques and over different temperature ranges), while the thermal expansion in the isotropic X or Y axes are in the range between 14 x 10⁻⁶/°C to 17 x 10⁻⁶/°C. Since in practical military applications where the integrated optic device must survive temperature fluctuations between -40°C to +80°C, the anisotropic thermal expansion property of both the integrated optic device and the coupling device must be substantially similar to maintain the bond between them. Movement between the optical fiber and the waveguide occurs primarily because of the environment in which the integrated optic device is used along with the anisotropic thermal expansion property of lithium niobate. In a gyroscope system, for example, the integrated optical device will have one degree of freedom which will sustain a substantial amount of the shock occurring along that axis while all three axes will undergo vibration. Since the light wavelength in many state of the art military applications is at the 850 nanometer range, the outside maximum allowable movement between the waveguide core with respect to the optical fiber core or vice versa is only 0.5 microns. Any movement beyond this narrow tolerance causes totally unacceptable distortion to the output signal. Despite these obstacles, several attempts at developing an environmentally stable coupling device for 850 nanometer optical fiber have been attempted. One such attempt used ion milled grooves in the lithium niobate device which permitted the rigid location of a chemically etched and polished optical fiber. This approach had alignment grooves which were defined by conventional photolithography and which were fabricated using ion milling in the same substrate as the waveguide. The coupling of the optical fiber to the waveguide was performed by inserting and bonding an etched portion of an optical fiber into the ion milled groove. Hence, the light emerging from the etched fiber went directly into the waveguide. See A. C. G. Nutt et al: Optics Letters, Vol. 9, No. 10, P. 463-465 (Oct. 1984). Although a good approach, this attempt had several shortcomings. First, the ion milling of the grooves in the waveguide and the etching of the optical fibers was a slow, expensive, and time consuming process requiring great precision which allowed for potential alignment problems between the waveguide and the optical fiber. Second, the etching of the fibers greatly reduces the polarization maintenance properties (i.e., stress zones) of the optical fibers which may exclude the use of birefringent optical fibers. Third, this approach was never actually demonstrated over a wide temperature range or for use with low loss connectors. Another attempt at providing a temperature stable coupling device was the use of silicon V-grooves. Optical fibers were prepared by epoxying single-mode fibers into V-grooves etched onto a silicon chip. A silicon chip cover was then mated with the silicon chip containing the etched V-grooves so that the optical fiber cores were precisely and periodically spaced along a straight line. After this assembly of the silicon chip, the end faces of the optical fibers were polished, butt coupled to a corresponding lithium niobate waveguide, aligned, and then attached using an optical adhesive. See E. J. Murphy et al: J. of Lightwave Tec., Vol. LT-3, No. 4, P. 795-798 (Aug. 1985). Although this approach allowed multiple optical fiber mountings to the waveguide, it also had problems. First, the silicon V-groove chip required very great accuracy and precision in the etching of the V-grooves in order to allow for the correct alignment of the optical fiber cores to the waveguide core. Second, the silicon V-groove chip is relatively large in physical size. Finally, the silicon V-grooved chip and the integrated optical device have different thermal expansion properties. Hence, at the silicon-lithium niobate interface, a substantial thermal mismatch exists which can result in thermal instabilities which could destroy the bond between optical fiber and the waveguide. It should be noted at this point that the coordinate system used to describe the physical tensor properties of lithium niobate is neither hexagonal nor rhombohedral but rather an X-Y-Z Cartesian coordinate system. Lithium niobate exhibits an anisotropic thermal expansion coefficient along an optic or C-axis and an isotropic thermal expansion coefficients along the other two axes. A light beam projected along the optic axis is exposed to the same refractive index regardless of the polarization of light and hence light propagating along this axis is said to be "symmetric". Accordingly, the optic axis which is usually assigned to the Z-axis can be easily determined. The sense of the Z-axis is the same as that of the optic axis. (I.e., upon compression the +Z face becomes negatively charged because of the piezoelectric effect.) As stated earlier in this background art section, lithium niobate has an atomic structure which can be described as a conventional hexagonal unit cell. According to the standard definition for a hexagonal unit cell, a hexagonal unit cell has three coplanar axes, called a H axes, 120° apart from each other and equal in magnitude to each other along with a fourth axis, called a C-axis or in the case of lithium niobate the optic axis, which is at right angles to the three a H axes. Also, the optic axis of lithium niobate lies in three mirror planes of symmetry about which any charge movement on one side of the plane is "mirrored" by movement on the other side. These three mirror planes of symmetry are also perpendicular to the a H axes. The X-axis is chosen to coincide with any of the a H axes and, since a right-handed cartesian coordinate system is used, the Y-axis lies in a plane of mirror symmetry. The sense of the Y-axis is determined in a manner similar to that described for the Z-axis. (I.e., upon compression, the +Y face becomes negatively charged because of the piezoelectric effect.) The sense of the X direction, however, cannot be determined in this way because the X-axis is perpendicular to a mirror plane. Any charge movement on one side of the plane is "mirrored" on the opposite side, hence, the X faces do not become charged. Typically, suppliers of lithium niobate crystals furnish pieces that are commonly in the form of thin slabs. These thin slabs may be designated X-cut, Y-cut, or Z-cut respectively, to the X, Y, or Z axes being normal to the broad face of the slab. A second letter is often added to the slab orientation indicating the direction of the propagation of light through a waveguide within the slab. Thus, an "X-cut, Y-propagation" describes a device having the X-axis normal to the broad face and the Y-axis in the direction in which light propagates within the waveguide. In an article "SIMPLE AND PRACTICAL TECHNIQUE FOR ATTACHING SINGLE-MODE FIBRES TO LITHIUM NIOBATE WAVEGUIDES", published in "ELECTRONICS LETTERS, November 8, 1984, page 974 to 976, K. H. Cameron, describes a fiber to waveguide joint, where the waveguide lies near the surface of a substrate material so that when a single-mode fiber is attached half of the fiber end protrudes above the top surface of the waveguide material. Since only half of the fiber end surface is fixed to the waveguide material, this kind of joint tends to be weakly bonded due to the limited fixing area. To improve such joint the article suggests attaching a small block of lithium niobate to the top surface of the substrate at the end of the waveguide. The block is positioned so that its polished face is aligned to the polished end of the waveguide and then is fixed in position at the substrate. The joint is subsequently made between the fiber and the combined block/substrate structure. Half of the fiber end overlaps the end of the waveguide substrate, and the other half of the fiber end overlaps the face of said attached block. Both the block as well as the substrate consist of lithium niobate. DE-A 22 37 444 describes a method for coupling optical components, in particular optical fibers and semiconductor lasers or photodiodes by bonding. The fiber is fixed to a first carrier, and the laser or diode is fixed to a second carrier, both carriers are positioned in relation to each other such that fiber is aligned with the laser or diode and thereafter both carriers are fixed together by bonding. Finally, any remaining gap between the end of the fiber on the one side and the laser or photodiode on the other side may be filled with a suitable transparent bonding agent. DE-A 22 37 444 does not deal with the problem of thermal expansion of the substrates and the fiber and less than ever about anisotropic thermal expansion. Disclosure of the Invention An object of the present invention is to provide an effective coupling device between lithium niobate devices and optical fibers for operation over a temperature range between -40°C to 80°C. Another object of the present invention is to provide an effective coupling device between lithium niobate devices and optical fibers which is more resistant to shock. Still another object of the present invention is to provide an effective coupling device between lithium niobate devices and optical fibers which is more resistant to vibration. The new integrated optic apparatus according to the invention is defined in claim 1, and a new method of joining an optical fiber to a light port of such I/O device is characterized in claim 6. Preferred details and embodiments of the invention are described in the dependent claims. According to the present invention, a fiber carrier provides an effective coupling means between a cleaved facing surface of an optical fiber and a light port in a mounting surface of an integrated optical device. Both the fiber carrier and the integrated optical device have an anisotropic thermal expansion property along the same known optic axis. Both the fiber carrier's and the integrated optical device's anisotropic thermal expansion property are also substantially similar in magnitude to each other. The fiber carrier is positioned with the integrated optical device so that both the carrier optic axis is parallel to the device optic axis and so that an auxiliary surface of the carrier is parallel to the device mounting surface. The optical fiber is then bonded to the fiber carrier so that the plane of the optical fiber cleaved facing surface lies in the plane of the carrier auxiliary surface. The carrier auxiliary surface is finally bonded to the I/O device mounting surface so that the optical fiber cleaved facing surface is placed in registration with the light port in the I/O device mounting surface. In further accord with the present invention, the mounting surface of the fiber carrier is aligned with the mounting surface of the I/O device such that the optic axis of the fiber carrier is the only one of the three orthogonal axes which is parallel to one of the three orthogonal axes of the I/O device. For example, both the auxiliary surface of the fiber carrier and the mounting surface of the I/O device are cleaved at an angle other than 90° with respect to the propagation of light to reduce the backreflection of light and any Fabry-Perot interferometer effects at the optical fiber-waveguide interface. The angle formed in the fiber carrier by cleaving is usually different from the angle formed in the I/O device by cleaving. However, in certain applications, both the angle in the fiber carrier and the angle in the I/O device can be the same. The present invention represents an advancement over prior devices which attempted to couple optical fibers to lithium niobate devices for several fundamental reasons. First, the integrated optic device and the fiber carrier are both formed from lithium niobate or other substantially similar materials which will reduce the thermal mismatch and hence stress on each because both now have substantially similar thermal expansion properties. Second, the present invention has been proved successful using optical fibers that are single mode at the 850 nanometer wavelength. According to the latest test results, optical fibers having a straight cleaved surface have a fiber-to-fiber throughput loss due to all causes of about -1db. This -1db loss mainly being due to a Fabry-Perot effect at the higher temperature ranges which would not be present in a best mode embodiment in which both the mounting surface of the substrate and the auxiliary surface of the carrier are cleaved at an angle other than 90°. Third, unlike the prior attempts at a coupling device, the present invention is simple to manufacture because it requires no critical tolerances or special manufacturing techniques. Hence, numerous lithium niobate fiber carriers can be easily, cheaply and quickly manufactured from a single lithium niobate wafer using only a cutting device. Fourth, the present invention allows for the active alignment and realignment of the optical fiber core to the waveguide port by projecting light through the fiber core - waveguide port interface and then manually realigning the fiber core to achieve maximum light throughput. This active alignment process is quite unlike the prior art which relied on special manufacturing techniques (i.e., etching and milling) with critical and narrow tolerances to achieve alignment between the fiber core and the waveguide port. Fifth, the fiber carrier of the present invention is a component having a very low mass and hence this device is more resistant to shock and vibration than any in the prior art. Finally, the present invention can be used with polarization maintaining fibers because nothing is done to the cladding of the optical fiber which could effect the stress zones or the elliptical inner core of these polarization maintaining fibers. It should be understood that although the invention has been disclosed in terms which closely follow the convention previously established in the art for describing crystalline axes, other conventions are of course possible. The invention should in no way be limited by the constraints of the nomenclature used herein. Similarly, although it is conventional in the art to provide I/O device substrates cut along axes chosen according to the conventional nomenclature, such I/O devices could be provided to cut along axes dictated by other systems of nomenclature. Thus, it will be understood that many different shapes and sizes of I/O devices can be utilized according to the present invention. It will also be understood that the orientation of the crystalline structure of the I/O device with respect to the outside shape provided is of little importance to the implementation of the present invention, properly understood. Each variation in shape of the I/O device can easily be matched by fabricating fiber carriers having the same axial alignment of their atomic structure as the I/O device when both the I/O device and the fiber carrier are mated together. These and other objects, features and advantages of the present invention will become more apparent in light of the following detailed description of a best mode embodiment thereof, as illustrated in the accompanying drawings. Brief Description of the Drawings Fig. 1 is a perspective illustration of one embodiment according to the present invention showing several fiber carriers mounted onto an I/O device; Fig. 2A is a top view illustration of a fiber carrier similar to the fiber carrier 34 of Fig. 1 except modified to eliminate back reflections; Fig. 2B is a side view illustration of a fiber carrier similar to the fiber carrier 34 of Fig. 1 except modified to eliminate back reflection; and Fig. 3 is a top view illustration of several fiber carriers mounted on an I/O device, according to the present invention. Best Mode For Carrying Out The Invention Fig. 1, which is not drawn to scale, illustrates several fiber carriers mounted onto an I/O device, according to the present invention. An I/O device 12 is bonded to a substrate 14. For illustrative purposes, an I/O device consisting of a simple "Y" shaped optical waveguide in LiNbO₃ is shown. The I/O device consists of a waveguide 16 formed within a crystal surface 18 which is spaced at a crystal thickness (t) from a crystal mating surface (not shown) and two device mounting surfaces 22 and 24 containing ports of the waveguide 16 (not shown). The waveguide can be formed by means well known in the art, such as, proton exchange or titanium indiffusion. The crystal mating surface is then bonded along a seam 26 to a mounting surface 28 of the substrate 14. The substrate 14 is chosen to have a material which has the same or a substantially similar anisotropic thermal expansion property aligned with the identical or similar axis of the I/O device 12. The I/O device 12 has a crystal thickness (t) of approximately 1.0 millimeter with the length and width selected for the particular application. The illustrated I/O device 12 is an "X-cut, Y-propagation" crystal, which by convention, means that the X-axis 30 of the chip in the Cartesian coordinate system 32 is normal to the crystal cut surface 18. Also by convention, the direction in which the waveguide lies is identified by a Cartesian coordinate axis parallel to it. Hence, the device is designated a "Y-propagation" which means the Y-axis lies parallel to the waveguide. The fiber carrier material is chosen having the same or a substantially similar anisotropic thermal expansion property along the same optic axis as that of the I/O device. After choosing the fiber carrier material, a wafer having the substantially similar thermal expansion properties (both anisotropic and isotropic) in the same axes of the same coordinate system as those of the I/O device is obtained. For example, if the I/O device chosen were a "Z-cut, Y-propagation" device, then the wafer obtained to made the fiber carriers would also have to be "Z-cut, Y-propagation". A mounting surface of the wafer is then securely bonded to a glass plate and the joined wafer-glass plate is mounted on a cutting device so that the wafer surface opposite the mounting surface, called the major surface, faces the cutting device. A cleaving cut, which allows for the eventual mating of the optical fiber to the fiber carrier, is made in a straight line along the major surface of the wafer. Numerous cleaving cuts are then made in straight regularly spaced lines along the major surface of the wafer. The spacing interval between these cleaving cuts on the wafer is dependent on the size and shape of the fiber carrier chosen while the shape and depth of these cleaving cuts correspond to the clad radius of the optical fiber. The blade in the cutting device is then replaced usually with a thicker model. Separating cuts, which subdivide and separate the individual fiber carriers, are then made both horizontally and vertically along regularly spaced intervals. Again, the spacing interval between the separating cuts are dependent upon the size and shape of the fiber carrier chosen while the depth of these separating cuts goes into but not through the glass plate. Finally, the bonding between the cut wafer and the glass plate is removed through the use of heat or a solvent which leaves the newly minted fiber carriers. In the embodiment of Fig. 1, therefore, each of the fiber carriers 34, 36, and 38 are "X-cut, Y-propagation" devices as designated in Fig. 1 by an X-axis 52 being a selected crystal axis and parallel to the X-axis 30 of the I/O device 12. Optical fibers 40, 42, and 44 respectively are then cleaved on one end to form a cleaved facing plane surface. Next, the optical fibers 40, 42, and 44 are respectively bonded onto the etched groove of each of the fiber carriers 34, 36, 38 such that the planes of the optical fiber cleaved facing surfaces lie roughly in the planes of carrier auxiliary surfaces 46, 48, and 50, respectively. The bonding material between the optical fiber and the fiber carrier may be, without limitation, a commercially available optical adhesive such as offered under the trade name Norland 61 or Norland 81. After the bonding of the optical fiber to the fiber carrier, the fiber carriers 34, 36, and 38 are mounted to the device mounting surfaces 22 and 24 respectively so that the optical fiber cleaved facing surfaces lie in registration with the waveguide ports. The carrier auxiliary surfaces 46, 48, and 50, have (by way of example and not limitation) a thin layer of UV sensitive optical adhesive on their surface which are then placed in contact with the waveguide ports in the device mounting surfaces 22 and 24 such as shown in Fig. 1. The registration may be done by conventional means of alignment. Or, a light signal of known intensity and power may be presented to the waveguide port in contact with the optical fiber while a detector mounted on the other waveguide port measures the output intensity/power. The fiber carrier device may then be aligned until the maximum output intensity/power is measured by the device. At that point, an ultraviolet light is projected onto the carrier auxiliary surface which bonds the carrier auxiliary surface to the device mounting surface which mounts the fiber carrier to the I/O device. Figs. 2A and 2B are top and side views of a carrier 34a similar to the carrier 34 of Fig. 1 except that both the carrier auxiliary surface and the device mounting surface are ground at an angle with respect to the horizontal and then polished to eliminate the backreflection of light at the optical fiber-waveguide interface. In the top view of Fig. 2A, the fiber carrier 34a and an optical fiber 40a have been ground at an angle theta ϑ. For the fiber carrier auxiliary surface an adequate angle for minimizing the reflected light back into the optical fiber has been found, through repeated testing, to be an approximately 10° cut along the auxiliary surface. The side view of the fiber carrier 34a in Fig. 2B clearly shows a carrier auxiliary surface 46a along with a fiber carrier cleaved surface 56. Fig. 3 shows a top view of an I/O device 12a having two mounting surfaces 22a and 24a and a waveguide 16a formed within a crystal surface 18a. Fiber carriers 34a, 36a, and 38a are manufactured and the optical fibers 40a, 42a, and 44a are aligned and mounted onto the mounting surface of the respective fiber carriers in the same manner as previously discussed. Furthermore, the auxiliary surfaces of the fiber carriers are cut and polished to form the previously discussed 10° angle. In Fig. 3, the I/O device mounting surfaces 22a, 24a are ground and polished to form angles β₁ and β₂ of approximately 15° to reduce and minimize the back reflection of light back into the waveguide. At this point, several important points are worth noting. First, although a Cartesian coordinate system has been used to define the atomic structure of the I/O device and the fiber carrier, the present invention should in no way be limited to the use of a Cartesian coordinate system to define the atomic structure. The use of a right-handed Cartesian coordinate system was for illustrative purposes and one skilled in the art will know of many other conventions to describe the crystalline structure of the fiber carrier and the I/O device. Second, although shown as a rectangular structure, the fiber carrier and the I/O device should not be limited to a particular shape. One skilled in the art would choose a particular shape for the fiber carrier or the I/O device dependent on the constraints and requirements of the specific application. So long as the I/O device and fiber carrier optic axes are parallel, the shape of the I/O device, the shape of the fiber carrier, and the orientation of their atomic structures with respect to those shapes are totally independent of the invention and are therefore application dependent. Finally, although described as a hexagonal unit cell in this application, the materials used should in no way be limited to the use of the hexagonal unit cell to define their crystalline structure. The use of the hexagonal unit cell in this application was for illustrative purposes only. One skilled in the art will know of many other unit cells to describe the crystalline structure of the materials described. For example, lithium niobate and similar materials can also be described as a rhombohedral unit cell or as a member of the perovskite family, specifically a deviated perovskite.

Claims: An integrated optic (I/O) apparatus comprising: a) an integrated optical (I/O) device (12) having a light port in a mounting surface (22, 24), said device being of a birefringent material having a device optic axis, and having anisotropic thermal expansion properties with a first device thermal expansion coefficient in the direction of the device optic axis and having a second device thermal expansion coefficient in a plane perpendicular to said device optic axis; b) an optical fiber (40, 42, 44) which has been cleaved at an end to form a cleaved facing surface (56) which lies in registration with said light port; c) a fiber carrier (34, 36, 38) supporting an end portion of said fiber and having an auxiliary surface (46, 48, 50) which is parallel to said I/O device mounting surface (22, 24) and is mounted thereto; in which d) said optical fiber (40, 42, 44) is bonded to said fiber carrier (34, 36, 38) such that the plane of said optical fiber cleaved facing surface (56) lies substantially in the plane of said carrier auxiliary surface (46, 48, 50); and e) said optical fiber (40, 42, 44) is bonded to said fiber carrier (34, 36, 38) along a longitudinal external portion of said fiber adjacent to said cleaved facing surface; characterized in that f) said fiber carrier (34, 36, 38) is of a material having a first axis, and having anisotropic thermal expansion properties with a first carrier thermal expansion coefficient in the direction of said carrier first axis, and having a second thermal expansion coefficient in a plane perpendicular to said carrier first axis; g) said carrier first axis is parallel to said device optic axis; and h) said first and second carrier thermal expansion coefficients are substantially similar in magnitude respectively to said first and second device thermal expansion coefficients. The apparatus of claim 1, characterized in that the optical fiber (40, 42, 44) is bonded onto an etched groove of the fiber carrier (34, 36, 38). The apparatus of claim 1 or 2, characterized in that the optical fiber cleaved facing surface (56) and the fiber carrier auxiliary surface (46, 48, 50) are inclined with respect to the optical axis of said optical fiber (40a, 42a, 44a) by a predetermined first angle (90-Θ) which is different from 90°. The apparatus of claim 3, characterized in that the I/O device mounting surface (22, 24a) is inclined with respect to the optical axis of said I/O device (12a) by a second angle (90°-β) which is different from 90°. The apparatus of claim 3 and 4, characterized in that the first angle is about 80° and the second angle is about 75°. A method of joining an optical fiber (40, 42, 44) to a light port in a mounting surface (22, 24) of an integrated optical (I/O) device (12), said device being of a birefringent material having an optic axis, and having anisotropic thermal expansion properties with a first device thermal expansion coefficient in the direction of the optic axis, and having a second device thermal expansion coefficient in a plane perpendicular to said optic axis, comprising the steps of: a) positioning a fiber carrier (34, 36, 38) such that an auxiliary surface (46, 48, 50) of said carrier is parallel to said device mounting surface (22, 24); b) providing an optical fiber (40, 42, 44) which has been cleaved at one end to form a cleaved facing surface (56), and bonding a longitudinal external portion of said optical fiber which is adjacent to said cleaved facing surface to said fiber carrier (34, 36, 38), so that the plane of said cleaved surface (56) substantially lies in the plane of said auxiliary surface (46, 48, 50); c) placing said cleaved facing surface (56) in registration with the light port; and d) bonding said carrier auxiliary surface (46, 48, 50) to the device mounting surface (22, 24); characterized in that the method further comprises e) selecting for said fiber carrier (34, 36, 38) a material having a first axis, and having anisotropic thermal expansion properties with a first carrier thermal expansion coefficient in the direction of its first axis, and with a second carrier thermal expansion coefficient in a plane perpendicular to said first axis; and f) selecting said carrier material such that said first and second carrier thermal expansion coefficients are substantially similar in magnitude respectively to said first and second device thermal expansion coefficients; and g) as part of said step of positioning further comprises the step of aligning said carrier first axis parallel to said device optic axis. The method of claim 6, wherein said step of placing further comprises the steps of: a) transmitting a light signal across the interface between the optical fiber (40, 42, 44) and the light port; b) detecting the magnitude of said light signal after transmission across said interface; and c) realigning the optical fiber with the light port to maximize said detected magnitude of said transmitted light signal. The method of claim 7, wherein said step of bonding comprises the step of ultraviolet bonding of said carrier auxiliary surface (46, 48, 50) to the device mounting surface (22, 24) when the magnitude of said transmitted light signal is maximized.

Inventors: BAILEY TIMOTHY JAMES, COURTNEY DANIEL PAUL, BAILEY, TIMOTHY JAMES, COURTNEY, DANIEL PAUL
Applicants: HONEYWELL INC, HONEYWELL INC.
Application year: 1988
Main classification: G02B6
IPC codes: G02B6