PROCESS FOR THE PRODUCTION OF IRON OXIDE HAVING HIGH REACTIVITY AND HIGH SPECIFIC SURFACE

Abstract: The present invention refers to a process for the obtention of iron oxide having high reactivity and high specific surface, utilized, mainly, as hydrogen sulphide absorber in oil drilling muds, which is obtained from calcination and reduction of natural and/or synthetic iron oxides and presents specific surface superior to 100.000 cm<2>/g. The process, object of the present invention, comprises the steps of calcination of natural iron oxides, with granulometry inferior to 3.0 mm, at temperatures in the range of 400 to 1000 DEG C, reduction of the calcined oxide with a gaseous composition composed of 15 to 40 % of CO (carbon monoxide), 5 to 20 % of CO2 (carbon dioxide), 1 to 30 % of H2 (hydrogen) and 10 to 70 % of N2 (nitrogen), followed by cooling, in a reducing or neutral atmosphere, at temperatures lower than 140 DEG C.

Description: . 4 - Descriptive Report of the Patent of Invention: "PROCESS FOR THE PRODUCTION OF IRON OXIDE HAVING HIGH REACTIVITY AND HIGH SPECIFIC SURFACE". The present invention refers to a process for the production of iron oxide having high reactivity and high specific surface, from natural and/or synthetic iron oxides having low reactivity and low specific surface. The iron oxide having high reactivity and high specific surface obtained by the process of the present invention is specially adequate to be utilized as an H2S absorber (hydrosulphuric gas), found in drilling muds of oil and natural gas wells. During the drilling operations of oil or gas wells, emanations of H2S occurs very frequently. This gas, acts upon the equipment employed during the drilling process, causing serious problems of corrosion and, due to its toxicity, serious problems to the health of the workers who work in the well drilling zones. Due to these reasons, the removal and elimination of this gas are very important. At present, a few natural or synthetic products have been employed in the elimination of H2S; however, some of them do not eliminate the gas efficiently while others that reach higher efficiency levels have a high production cost that render them economically unfeasible for such a utilization. Recently, an imported synthetic product has been employed as an H2S absorber. It is denominated Ironite Sponge, and it is described in the patent documents GB 1,471,607, of 28/06/74 and BR 7701035 of 17/02/77. These documents describe an iron oxide and a process for the elimination of hydrogen sulphide (H2S) from drilling mud oil and gas wells, employing the referred iron oxide which is porous (Ironite sponge) and prepared by iron oxidation, for example, iron filings, containing carbon, at a temperature in the range of 204°C to 232°C, in such a way as to form Fe3U4 with spongy porosity. Following this, Fe3θ4 formed is submitted to deagglomeration by crushing, to neutralization with hydroxide or ammonium solution, to echanical agitation, with subsequent separation and removal of the non-reacted fraction, removal of the excess water and drying at 204°C. The iron oxide thus obtained presents a surface area of up to 16 times more than that of the magnetic one. The process of preparation of ironite sponge mentioned above employs as raw-material, the iron-filing and utilizes complementary steps of physical and chemical treatments, which render it economically unfeasible, due to excess of operational units involved in it. Apart from this, the iron oxide produced does not present satisfactory characteristics for a good removal of H2S from oil drilling muds. Documents BR 8305404 of 30/09/83 and GB 2147284 of 28/09/84, describe a process for the obtention of high surface area magnetite, which consists in separating the magnetic fraction of a mixture of iron oxides, with a determined granulometry, obtained by pirite roasting the referred magnetic fraction being a magnetite concentrate which is employed to absorb hydrogen sulphide (H2S) evolved from oil drilling wells. This process which employs pyrite roasting and magnetic separation, is technically and economically inadequate for its employment in drilling wells. One other British document GB 1435219 of 14/12/ 73,, describes improvements in or relating to the production of non-magnetic iron oxide, having a relatively high specific gravity and obtained from iron ore, such as limonite and goethite having a relatively low specific gravity. The process comprises the steps of calcining said iron-containing ore under oxidizing conditions with a residence time, sufficient to maintain the ore at a temperature between 1700°F (926°C) and 2200°F (1204°C) for at least 20 minutes; cooling the calcined ore and separating the desired iron-oxide containing material. The iron oxide thus obtained presents specific gravity of at least 4,2 and may be employed for oil drilling , as an H2S absorber. As it may be observed, the conditions of this process are oxidizing and utilizes a high temperature range that requires a higher _. δ- energy consumption, despite the fact that iron oxide produced is not magnetic. With the aim to solve the technical and economical inconveniences existent in the production of the so-called "ironite sponge", the process for the production of iron oxide having high reactivity and high specific surface was developed, object of the present invention, which utilizes natural and/or synthetic iron oxides as raw-material having low reactivity and low specific surface. The iron oxide presents characteristics which are much superior to those presently employed as H2S absorbers, in oil or gas drilling muds. Due to its extremely low production cost, the iron oxide thus produced substitutes, with great efficiency, technically and economically, the products utilized up to now. The present process, consists in calcining under appropriate temperature of 400 to 1000°C, natural iron oxides, hydrated or not, such as limonite (2Fe2θ3.3H2θ), goethite (Fe2θ3.3H2θ) and hematite (Fe2θ3) or synthetic iron oxides, such as hematite, or its mixtures in any proportion and after or during calcining,reducing with a reducing gaseous composition, in such a way that oxide be preferentially reduced to Fe2θ4. The gaseous composition utilized consists of CO: 15% to 4%, C0 2 : 5% to 20%, H 2 : 1% to 30% and N 2 : 10% to 70%. Having goethite as basis, with the calcining, the Fe2θ3.3H2θ turns into spongy anhydrous Fe2θ3. Following this, during reduction, the Fe2U3 sponge formed previously increases its volume considerably, attaining specific surface superior to 10 m 2 /g. This material is highly reactive, being, therefore, an excellent H2S absorber in oil drilling muds and may also be utilized as a weighting agent. A synthetic iron oxide having low reactivity and low specific surface which may be employed as raw material in the present process, is the hematite obtained in the HC1 operations (hydrochloric acid) by pyrolysis of iron chlorides. This hematite is the solid residue of the pyrolysis and due to its characteristics and qualities, it - k - is usually utilized in the production of ferrite or in the pigment industry. However, when submitted to reduction by the present process, this hematite turns into magnetic, with a small-sized grain, greater porosity and high specific surface. The process is carried out by the introduction, in a rotating oven or fluid bed, of the natural and/or synthetic iron oxides, having an initial granulometry inferior to 3,00mm, where they are submitted to calcination at temperatures in the range of 400 to 1000°C, followed by reduction with a gaseous composition composed of CO: 15% to 40%, C0 2 : 5% to 20% H 2 : ' % to 30% and N 2 : 10% to 7% at adequate temperatures. The calcination and reduction steps may be carried out simultaneously or in sequence. After these steps (calcination and reduction), the iron oxide produced is cooled at a temperature lower than 140°C, in a reducing or neutral atmosphere and after this comminuted to a granulometry inferior to 200 mesh (0,074 mm). Several assays have been carried out utilizing the present invention, with natural and synthetic iron oxides, which are described below by way of illustrative examples, which, however, must not be understood as limiting parameters of the invention: Example I Utilized iron oxides: Hematite 50% + goethite 50% Initial granulometry: < 2,00 mm (lower than 2,00 mm) Calcination temperature: 750°C Calcination time: 60 minutes Reduction temperature: 550°C Reduction time: 60 minutes Gaseous mixture composition for reduction: CO = 25% C0 2 = 5% H 2 = 6% N 2 = 64% Final granulometry : ^ 200 mesh ( l ower than 0 , 074 mm ) Initial speci fic surface : 1000 cm 2 /g Final specific surface : > 100.000 cmVg (higher than 100.000 cmVg) - - Exa ple I I Utilized iron oxide: goethite - 100% initial granulometry: < 2,0 mm (lower than 2,0 mm) Calcination temperature: 600°C Calcination time: 60 minutes Reduction temperature: 600°C Reduction time: 60 minutes Gaseous mixture composition for reduction: CO = 23% C0 2 = 6% H 2 = 8% N 2 = 63% Final granul ometry : <£ 200 mesh ( lower than 0 , 074 mm ) Initial speci fic sur face : 1200 cm Vg Final speci fic surface : > 250.000 cm 2 /g (higher than 250.000 cm 2 /g) Example III Utilized iron oxides: Goethite 50% + limonite 50% Initial granulometry:< 1 ,0 mm (lower than 1,0 mm) Calcination temperature: 700°C Calcination time: 60 minutes Reduction temperature: 550°C Reduction time: 60 minutes Gaseous mixture composition for reduction Final granulometry: * 200 mesh (lower than 0,074 mm) Initial specific surface: 1800 cm 2 /g Final specific surface:> 400.000 cmVg (greater than 400.000 cmVg) As it may be observed by the examples above, the iron oxide produced by the present example, presents a high final specific surface (> 100.000 cm 2 /g), which is characteristic of an excellent product to be utilized, as an H2S absorber as well as a weighting agent. With samples of iron oxides obtained by the process, the below-mentioned chemical tests were carried out, specially employed to evaluate the quality of the spongy iron oxide: . Kinetic and Reactivity Test: it measures the drop of sulphide concentration present in the reaction medium, in 15 minute-intervals. . Sulphide Consumption Test: it is carried out aiming at evaluating the occurrence of the sample's active centers. . H2S Consumption Test: it is carried out aiming at evaluating the surface area which is chemically active in the presente of H2S. It must be pointed out that in the kinetic test, a sample is approved if, in the 15 minutes interval, the drop in the initial sulphide concentration is superior to 50% and, at the end of 60 minutes of the test, the sulphide concentration is equal to zero. The table below shows the comparative result of 3 (three) samples of iron oxide obtained by the process of the invention, denominated CVRD (Companhia Vale do Rio Doce) and a sample of the product denominated "Ironite Sponge". SAMPLE DROP IN THE INITIAL CONCENTRATION As it may be observed, the reactivity of the samples CVRD-1, 2 and 3 is much higher than that of the Ironite Sponge sample, and because of this, the CVRD product is much superior in quality when compared with the product of the prior art. The sulphide consumption tests for the samples CVRD-1, and 3 presented the following results: samples 0,19, 016 and 0,19 g S = /g, respectively. These results are considered excellent, having in view that the specification of this test is that the sample presents a result equal or superior to the sample 0,09g S = /g. The H2S consumption test establishes Lhat the tested samples present a result superior to the sample 0,9 H2S/g. In the samples CVRD-1, 2 and 3, the result presented was of sample 1,4, 1,6 and 1,4 H 2 S/g, respectively. With the adoption of the present invention for the production of iron oxide having high reactivity and high specific surface, new perspectives lie ahead for the utilization of natural and synthetic iron oxides as basic raw-material for the prodution of a hydrogen sulphide-absorbing agent. As the product obtained technical characteristics which are much superior to those presently existent on the market and considering that its production process permits a great cost reduction, it makes the invention competitive and with an enormous application potential.

Claims: CLAIMS 1 - PROCESS FOR THE PRODUCTION OF IRON OXIDE HAVING HIGH REACTIVITY AND HIGH SPECIFIC SURFACE, which comprises the steps of calcination, reduction and cooling, characterized by the fact that it comprises the calcination of natural and/or synthetic iron oxides, with granulometry inferior to 3,0 mm, at temperatures in the range of 400 to 1000°C, reduction of the referred calcined oxide with a gaseous composition composed of 15 to 40% of CO (carbon monoxide), 5 to 20% of CO2 (carbon dioxide), 1 to 30% of H2 (hydrogen) and 10 to 70% of N2 (nitrogen), followed by cooling, in reducing or neutral atmosphere, at temperatures lower than 140°C. 2 - PROCESS, according to claim 1, characterized by the fact that natural and/or synthetic oxides like limonite (2Fe2θ3-3H2θ) ; or goethite (Fe2θ3.3H2θ) or hematite (Fe2U3) or any of its mixtures are in variable proportions. 3 - PROCESS, according to claim 1, characterized by the fact that the steps of calcination and reduction are carried out simultaneosly or in sequence. 4 - PROCESS, according to claim 1, characterized by the fact that the spongy iron oxide obtained has a specific surface superior to 100.000 cm 2 /g. 5 - PROCESS, according to claim 1, characterized by the fact that the spongy iron oxide obtained is submitted to comminution up to a granulometry inferior to 200 mesh (0,074 mm) .

Inventors: JARDIM PAIX O JOSE MARCIO, JARDIM PAIXO, JOSE, MARCIO
Applicants: VALE DO RIO DOCE CO, COMPANHIA VALE DO RIO DOCE
Application year: 1988
Main classification: C01G49
IPC codes: C01G49, C09K8