Manufacture of polyurethane foam

Abstract: Flexible polyurethane foam based on methylene diphenyl isocyanates and isocyanate-reactive compounds selected from polyols and polyamines, for which the ratio of the density expressed in kg/m³ to the compression hardness at 40% compression, expressed in kPa, has a value of at least 20. Such foams may be obtained through a process which comprises reacting methylene diphenyl isocyanates with one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 and from 0 to 5 parts by weight of water per 100 parts of polyols and/or polyamine, optionally together with additives conventional in the art, and optionally together with blowing agents other than water, whereas the isocyanate index ranges from 10 to 60.

Description: This invention relates to a process for manufacturing flexible foam products comprising urethane and or urea linkages. More particularly the invention relates to a process for manufacturing such foam products in a one shot method which uses methylene diphenyl isocyanate (MDI) based isocyanates. The manufacture of flexible polyurethane foam is a well known process. Its chemistry and technology have been reviewed in reference bocks such as the "Polyurethane Chemistry and Technology" by H. Saunders and K. C. Frisch, the "Polyurethane Handbook" by G. Oertel and the "Flexible Polyurethane Foams and Chemistry and Technology" by G. Woods. The techniques described there are abundantly exploited industrially to produce flexible polyurethane foams for application in furniture, bedding, automotive, etc. Flexible polyurethane foams are generally produced by reacting polyols and polyisocyanates in the presence of water as carbon dioxide generator (isocyanate hydrolysis reaction). Halocarbon, such as chlorofluorocarbons (CFC), are often used as auxiliary blowing agents to supplement the blowing action of water. Tolylene-di-isocyanate (TDI) based isocyanates have long been applied as the preferred polyisocyanate. More recently however methylene-diphenyl-isocyanates (MDI) have also found application in the manufacture of flexible polyurethane foams. A reported advantage for the use of MDI over TDI is their lower vapour pressure which results in a safer use, from industrial hygiene point of view. One limitation however of MDI-based systems has been considered to lie in their rather narrow range of commercially achievable properties, in particular in respect of density and hardness and also in their inability to produce low hardness (soft) foams without using auxiliary blowing agents beside or instead of water. Reference is made in this respect to publications by R. Volland (Journal of cellular plastics Nov.-Dec. 84. p. 416), by M.H. Courtney (proceedings of 30th SPI annual polyurethane technical and marketing meeting - p. 244) and R.C. Allen (proceedings of 30th annual SPI polyurethane technical and marketing meeting-p.256). As there is a growing opposition to the use of CFC blowing agents this is clearly a serious drawback for MDI-based polyurethane flexible foams. French Patent Application 2181987 discloses the preparation of soft and stable foams from polyesters having an hydroxyl value of 70-135 and a polyisocyanate at an index of 60-90 using water as a blowing agent. The Journal of Cellular Plastics Vol. 20, No. 4, July/Aug 1984, pages 285-290 discloses that the hardness of an MDI based foam is decreased when the index is decreased and that compression set is deteriorating very fast when lowering the index from 80 to 70. US 4239856 discloses a method for preparing highly resilient flexible foams based on MDI and polyether polyols having an equivalent weight of 1250-3500 in the presence of water at an index of 102. It has now been found surprisingly however that it is possible to produce foams based on MDI with a much broader range of properties, by performing the foaming process under the conditions defined hereinafter. Accordingly the invention provides a process for manufacturing flexible polyurethane foams based on methylene diphenyl isocyanates and isocyanate-reactive compounds, which comprises reacting methylene diphenyl isocyanates with one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000-3000 and from 0 to 5 parts by weight of water per 100 parts of polyols and/or polyamine, optionally together with additives conventional in the art, and optionally together with blowing agents other than water, whereas the isocyanate index ranges from 10 to 60 with the proviso that an amount of 5 parts by weight per 100 parts of polyols and/or polyamines for the preparation of cold-cure, moulded polyurethane foam in a closed mould is excluded. According to an embodiment of the invention there is also provided a process for manufacturing flexible polyurethane foams based on methylene diphenyl isocyanates and isocyanate-reactive compounds, in the presence of less than 1% by weight based on the total formulation of halocarbon blowing agents, which comprises reacting methylene diphenyl isocyanates with water and one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000-3000, optionally together with additives conventional in the art, whereas the isocyanate index ranges from 10 to below 60 and the weight ratio of the isocyanate-reactive compounds to water is at least 20 with the proviso that an amount of 5 parts by weight per 100 parts of polyols and/or polyamines for the preparation of cold-cure, moulded polyurethane foam in a closed mould is excluded. In accordance with a certain trend in the art, the expression "polyurethane foam" as used herein generally refers to cellular products as obtained by reacting polyisocyanates with isocyanate-reactive hydrogen containing compounds, in the presence of foaming agents, and in particular includes cellular products obtained with water as reactive foaming agent (involving a reaction of water with isocyanate groups yielding urea linkages and carbon dioxide). The expressions "isocyanate-reactive hydrogen containing compounds" or "isocyanate-reactive compounds" as used herein are furthermore intended to include polyols as well as polyamines. The expression "polyurethane foam" is thus intended also to include products which comprise urethane linkages together with urea linkages and even products which essentially comprise urea linkages with few or no urethane linkages. The expression "flexible polyurethane foam" as used herein refers to cellular products which exhibit substantial shape recovery after deformation. The expressions "methylene diphenyl isocyanates" and "MDI" as used herein refers to polyisocyanate compositions comprising compounds selected from diphenylmethane diisocyanate isomers, polyphenyl polymethylene polyisocyanates and derivatives thereof bearing at least two isocyanate groups and containing carbodiimide groups, uretonimine groups, isocyanurate groups, urethane groups, allophanate groups, urea groups or biuret groups. Methylenediphenyl isocyanates as thus defined are obtainable by condensing aniline with formaldehyde, followed by phosgenation, which process yields what is called crude MDI, by fractionation of said crude MDI, which process yields pure MDI and polymeric MDI, and by autocondensation of crude, pure or polymeric MDI, or reaction of excess of crude, pure or polymeric MDI with polyols or polyamines, which processes yield modified MDI, containing respectively carbodiimide, uretonimine, isocyanurate, allophanate or biuret groups and urethane or urea groups. Thus the expression methylene diphenyl isocyanates as used herein is intended to encompass isocyanate bearing compounds sometimes referred to in the art as quasi-prepolymers or semi-prepolymers based on MDI, which in fact correspond to the modified MDI containing urethane and/or urea groups as defined above. The amount of halocarbon blowing agents more specifically is less than 0,5% by weight of halocarbon blowing agent based on the total formulation. The expression "additives conventional in the art" as used herein refers to such optional or desirable ingredients as known in the art of flexible polyurethane foams, as more in particular reported in chapter 2 of the reference book "Flexible Polyurethane Foams" by George Woods, edited by Applied Science Publishers. Thus the expression additives conventional in the art is in particular intended to include catalysts, chain-extending agents, cross-linking agents, curing agents, blowing agents, surfactants, fillers, fibrous reinforcements and flame retardants. The expressions "isocyanate index" and "NCO-index" as used herein refer to the ratio of -NCO groups over reactive hydrogen atoms present in a polyurethane formulation, given as a percentage : NCO-index = [NCO] [active hydrogen] x 100 In other words the NCO-index expresses the percentage of isocyanate actually used in a formulation with respect to the amount of isocyanate theoretically required for reacting with the amount of isocyanate reactive hydrogen used in a formulation. The expression "active hydrogen atoms" as used herein for the purpose of calculating the isocyanate index refers to the total of hydroxyl and amine hydrogen atoms present in the reactive compositions in the form of polyols, polyamines and/or water; this means that for the purpose of calculating the isocyanate index one hydroxyl group is considered to comprise one reactive hydrogen, one primary amine group is considered to comprise two reactive hydrogens and one water molecule is considered to comprise two active hydrogens. It should be observed that the isocyanate index as used herein is considered from the point of view of the actual foaming process involving the MDI ingredient, the polyol and/or polyamine ingredient and the water, regarded as a one shot system. Any isocyanate groups consumed in a preliminary step to produce modified MDI (including such MDI-derivatives referred to in the art as quasi- or semi-prepolymers) or any active hydrogens reacted with isocyanate to produce modified polyols or polyamines, are not taken into account in the calculation of the isocyanate index. Only the free isocyanate groups and the free active hydrogens (including those of the water) present at the actual foaming process are taken into account. The expression "one shot" method, process or system as used herein therefore refer to "such processes where the MDI ingredient, the polyol and polyamine ingredient and the water are reacted with each other, excluding the so called prepolymer method in which MDI ingredients are pre-reacted with all polyol and polyamine ingredients, whereas the obtained product, possibly with additional MDI, is finally foamed with the water, but including so called semi- or quasi-prepolymer systems where some polyol and/or polyamine has been incorporated into the MDI ingredient. The expressions "foam density" and "density" as used herein when referring to flexible polyurethane foams, relate, for the purpose of clear definition, to the density as would be measured on a foam sample obtained by foaming under free rise conditions, as opposed to foaming under vacuum or in a closed mould. The process of the invention is however not limited to such free rise conditions and in particular the process can for example be used for slabstock manufacture as well as for molding and vacuum foaming. Methylene diphenyl isocyanates which can be employed in accordance with the invention include for example : (a) diphenylmethane-4,4'-diisocyanate and mixtures thereof with other isomers of of diphenylmethane diisocyanate; (b) methylene bridged polyphenylpolyisocyanates prepared by phosgenation of mixtures of polyamines obtained by the condensation of aniline and formaldehyde and known in the art as "crude" or "polymeric MDI"; (c) polymers and oligomers obtained by reacting diphenylmethane diisocyanates or "crude MDI" with an isocyanate reactive compound, such as for example a monomeric glycol or polyol (or mixtures thereof) or a hydroxyl-ended polyester or polyether; such polymers and oligomers known in the art as "MDI prepolymers"; and (d) modified diphenylmethane diisocyanates or "crude MDI" in which a proportion of the isocyanate groups are converted into other functional groups such as carbodiimide, isocyanurate, uretonimine or allophanate groups, or in which a proportion of the isocyanate groups are reacted with an isocyanate-reactive compound. The NCO-functionality of the used methylene diphenyl isocyanates preferably ranges from 1.9 to 2.9 and most preferably from 2 to 2.5. Mixtures of MDI variants may also be used if desired. Isocyanate reactive hydrogen containing compounds for use in accordance with the invention are selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000 to 3000. Suitable polyols which can be employed include for example those polyether and polyester polyols which have an average hydroxyl functionality from 2 to 4, and preferably from 2 to 3, and an average hydroxyl equivalent weight of from 1000 to 3000 and most preferably from 1000 to 2500. Further polyols which may be employed include for example polythioethers, polyacetals, polycarbonates and polyesteramides comprising from 2 to 4, and preferably from 2 to 3 hydroxyl groups. Suitable polyamines which can be employed include for example those polyether polyamines which have an average amine functionality from 2 to 4, and preferably from 2 to 3, and an average amine equivalent weight from 1000 to 3000 and most preferably from 1000 to 2500. Suitable polyether polyols which can be employed include those which are prepared by reacting one or more alkylene oxides or substituted alkylene oxides with one or more active hydrogen containing initiators compounds. Suitable such oxides include for example ethylene oxide, propylene oxide, tetrahydrofuran, butylene oxides, styrene oxide, epichlorhydrin and epibromhydrin. Suitable initiator compounds include, for example, water ethylene glycol, propylene glycol, butane diol, hexane diol, glycerol, trimethylol propane, pentaerythritol, hexanetriol, hydroquinone, resorcinol, catechol, bisphenols, novolac resins, phosphoric acid. Further suitable initiators include, for example, ammonia, ethylenediamine, diaminopropanes, diaminobutanes, diaminopentanes, diaminohexanes, ethanolamine, aminoethylethanolamine, aniline, 2,4-toluenediamine, 2,6-toluenediamine, 2,4-diamino-diphenylmethane, 4,4-diaminodiphenylmethane, 1,3-phenylenediamine, 1,4-phenylenediamine, naphthylene-1,5-diamine, 4,4'-di(methylamino)-diphenylmethane, 1-methyl-2-methylamino-4-aminobenzene, 1,3-diethyl-2,4-diaminobenzene, 2,4-diaminomesitylene, 1-methyl-3,5-diethyl-2,4-diaminobenzene, 1-methyl-3,5-diethyl-2,6-diaminobenzene, 1,3,5-triethyl-2,6-diaminobenzene and 3,5,3',5'-tetraethyl-4,4'-diaminodiphenylmethane. Suitable polyester polyols which can be employed include, for example, those prepared by reacting one or more polycarboxylic acids or anhydrides or esters thereof with one or more polyhydric alcohols. The polycarboxylic acids may be aliphatic, cycloaliphatic, aromatic and/or heterocyclic and may be substituted (e.g. with halogen) and/or unsaturated. Examples of carboxylic acids of this kind include glutaric acid, succinic acid, adipic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, isophthalic acid, trimellitic acid, tetrahydrophthalic acid, hexahydrophthalic acid, tetrachlorophthalic acid, maleic acid, fumaric acid, dimeric and trimeric fatty acids, which may be in admixture with monomeric fatty acids, terephthalic acid and the like. Examples of suitable polyhydric alcohols include ethylene glycol; 1,2-propylene glycol; 1,3-propylene glycol; butylene glycols; 1,6-hexane diol; 1,8-octane diol; neopentyl glycol; cyclohexane dimethanol (1,4-bis-hydroxymethyl cyclohexane); 2-methyl-1,3-propane diol; glycerol; trimethylol propane; 1,2,6-hexane triol; 1,2,4-butane triol; trimethylol ethane; pentaerythritol; quinitol; diethylene glycol; triethylene glycol; tetraethylene glycol; polyethylene glycol; dipropylene glycol; polypropylene glycols; dibutylene glycol; or polybutylene glycols. It is also possible to use polyesters of lactones such as caprolactone; or hydroxy carboxylic acids such as hydroxy caproic acid. Suitable polyether polyamines which can be employed include those which are prepared by amination of polyether polyols of the type described above. For use in accordance with the invention it is not necessary that the amination of the polyols be complete. Partially aminated polyether polyols of the type disclosed above can also be employed. Other suitable polyol compositions which can be used include for example polyhydroxyl derivatives which contain high molecular polyaddition or polycondensation polymers in dispersed or soluble state. Such polyhydroxyl derivatives can for example be obtained by carrying out a polyaddition reaction (for instance between polyisocyanates and amino-functional compounds) or a polycondensation reaction (for instance between formaldehyde and phenols and/or amines) in situ in such polyols as already disclosed above. Suitable are also polyhydroxyl derivative modified by vinyl-polymerization, such as for example obtained by polymerizing styrene and acrylonitrile in the presence of polyether polyols or polycarbonate polyols. In the process according to the invention the isocyanate index as defined above should range from 10 to 60 and preferably from 20 to below 60. According to one embodiment of the invention this specific range of isocyanate index is associated with the use of halocarbon blowing agents to provide polyurethane foams with particular properties. According to another embodiment of the invention the above specific range of isocyanate index is associated with the use of water, in various ranges of water to polyol and polyamine proportions. Thus an isocyanate index ranging from 10 to 60, preferably from 20 to 60, may be used together with a proportion of 0.5 to 5 % by weight of water with respect to the polyols and polyamines. Alternatively an isocyanate index ranging from 10 to 60, preferably from 20 to 60 may be used together with less than 0.5 % of water with respect to the polyols and polyamines. The present invention further also covers polyurethane systems suitable for performing the process of the invention. The expression "system" as used herein refers to a set of individual components which are produced and/or marketed with the obvious purpose to be suitable for use in combination with each other to perform a specific process or to achieve specific performances. Thus, the invention covers a reactive system for the manufacture of flexible polyurethane foams involving an isocyanate composition based on methylene diphenyl isocyanates and an isocyanate reactive composition comprising one or more polyols and/or polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000-3000 and from 0 to 5 parts by weight of water per 100 parts of polyol and polyamine, optionally together with additives conventional in the art and/or with blowing agents other than water, said isocyanate composition and isocyanate reactive composition being provided in proportions to give an isocyanate index ranging from 10 to 60 with the proviso that an amount of 5 parts by weight per 100 parts of polyols and/or polyamines for the preparation of cold-cure, moulded polyurethane foam in a closed mould is excluded. The manufacture of flexible foams in accordance with the present invention may be performed using techniques well known in the art and abundantly commented in the reference books referred to more above. Thus the process can be performed in conventional ways as free rise method or as moulding method, and may be used to manufacture moulded foams as well as slabstock, either by a continuous or by a discontinuous process. The invention is illustrated but not limited by the following examples. In these examples the following hand mix procedure has been followed. The isocyanate-reactive compound, the water and additives were premixed for 15 seconds at 1500 RPM. The isocyanate was then added, with a further 5 second mixing at 2000 RPM. The mixtures were poured in 5 liter polyethylene buckets. The foam was allowed to cure for 24 hours. Pads of 10 x 10 x 5 cm were then cut from the center of the bun for physical testing. In the formulations listed herebelow the following references are used to designate the various components : I-R designates the isocyanate reactive compound(s) according to the definition given above C designates catalyst component(s) C-L designates cross-linker component(s) S designates stabiliser component(s) and ISO designates the isocyanate component(s). Example 1 I-R Daltocel T-3275 (from ICI) 100 pbw S Tegostab B 4113 (from Goldschmidt) 0.3 pbw C Dabco 33LV (from Air Products) 0.7 pbw C Dimethylaminopropylamine 0.35 pbw C Dimethylethanolamine 0.40 pbw Water 3.0 pbw ISO Suprasec VM 28 (from ICI) 34.0 pbw The isocyanate index was 50. The cured foam had a density of 62 kg/m 3 . The compression hardness at 40 % compression (CV40), as measured according to the method described in ISO 3386 had a value of 0.95 kPa. Example 2 I-R Daltorez RL (from ICI) 100 pbw C Dabco 33LV (from Air Products) 0.2 pbw C Niax A1 (from Union Carbide) 0.1 pbw C Stannous Octoate 0.2 pbw S Tegostab 2370 (from Goldschmidt) 1.0 pbw Water 5.0 pbw ISO 50/50 mixture of Suprasec DNR and Uropol DP 980 (from ICI) 49 pbw The isocyanate index was 53. The cured foam had a density of 75 kg/m 3 . The compression hardness at 40 % compression (CV40) as measured according to the method described in ISO 3386 had a value of 2.7 kPa. Uropol DP 980 is a polyester modified MDI with a -NCO functionality of 2.

Claims: Process for manufacturing flexible polyurethane foams based on methylene diphenyl isocyanates and isocyanate-reactive compounds, which comprises reacting methylene diphenyl isocyanates with one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000-3000 and from 0 to 5 parts by weight of water per 100 parts of polyols and/or polyamine, optionally together with additives conventional in the art, and optionally together with blowing agents other than water, wherein the isocyanate index ranges from 10 to 60 with the proviso that an amount of 5 parts by weight per 100 parts of polyols and/or polyamines for the preparation of cold-cure, moulded polyurethane foam in a closed mould is excluded. Process for manufacturing flexible polyurethane foams based on methylene diphenyl isocyanates and isocyanate-reactive compounds, in the presence of less than 1% by weight based on the total formulation of halocarbon blowing agents, which comprises reacting methylene diphenyl isocyanates with water and one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000-3000, optionally together with additives conventional in the art, wherein the isocyanate index ranges from 10 to below 60 and the weight ratio of the isocyanate-reactive compounds to water is at least 20 with the proviso that an amount of 5 parts by weight per 100 parts of polyols and/or polyamines for the preparation of cold-cure, moulded polyurethane foam in a closed mould is excluded. Process according to claim 2 characterised in that the weight ratio of the isocyanate-reactive compounds to water ranges from 20 to 200. Process according to any one of the preceding claims, characterised in that one or more isocyanate-reactive compounds are selected from polyether polyols, polyester polyols and polyether polyamines. Reactive system consisting of a set of individual components for the manufacture of flexible polyurethane foams involving an isocyanate composition based on methylene diphenyl isocyanates and an isocyanate-reactive composition comprising one or more polyether polyols and/or polyamines with a functionality of 2-4 and an average equivalent weight ranging from 1000-3000 and from 0 to 5 parts by weight of water per 100 parts of polyol and polyamine, optionally together with additives conventional in the art and/or with blowing agents other than water, said isocyanate composition and isocyanate-reactive compositon being provided in proportions to give an isocyanate index ranging from 10 to 60 with the proviso that an amount of 5 parts by weight per 100 parts of polyols and/or polyamines for the preparation of cold-cure, moulded polyurethane foam in a closed mould is excluded.

Inventors: MULLER LOUIS, PHAM TU, MULLER, LOUIS, PHAM, TU
Applicants: ICI PLC, IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1988
Main classification: C08G18
IPC codes: C08G18