VINYL CHLORIDE RESIN COMPOSITION FOR POWDER MOLDING AND METHOD FOR PRODUCING SAME

Abstract: A vinyl chloride resin composition for powder molding which is obtainable by a method comprising a first step in which from 40 to 120 parts by weight of plasticizer is blended with 100 parts by weight of granular vinyl chloride resin obtainable by suspension or bulk polymerisation; a second step in which from 0.5 to 40 parts by weight of at least one polymer or copolymer having an active hydrogen in the molecule [component (A)] and from 0.1 to 10 parts by weight of crosslinkable isocyanate compound [component (B)] are added and dry-blended; and a third step in which while the dry-blend system is cooling from a maximum temperature, finely powdered vinyl chloride resin obtainable by emulsion or micro-suspension polymerisation is added to coat the dry-blend.

Description: The present invention relates to a vinyl chloride resin composition for powder molding which is particularly useful for moulding cushiony covering materials for automobile interior parts such as crash pads, arm rests, head rests, console boxes, meter covers, door trims, pillars, etc., and to a method for producing the composition. In recent years, for such covering materials for automobile interior parts, those which are light in weight and of superior soft feel and which have embossed or stitched patterns giving a feeling of high quality are required. It is however difficult to meet this requirement by the use of the conventional vacuum-formed product of soft sheets consisting mainly of vinyl chloride resin and ABS resin. In order to answer this requirement, the powder molding method has attracted public attention. The feature of this powder molding method consists in that, by rotating or shaking an assembled unit of a mold kept at a temperature of 180°C or higher and a resin powder supply box, or injecting a resin powder into the mold, the resin powder is fused onto the inner surface of the mold, and the residual unfused powder is recovered automatically or forcedly into the box (Japanese Patent No. 132507/1983). For heating the mold used in this powder molding method, there are used a method with a gas furnace, a method with circulation of a heat medium oil or dipping into a heat medium oil, a high-frequency induction heating method, (Sumitomo Kagaku, No. 1985-I, pp. 84-91). The covering material produced by the powder molding method, like the conventional vacuum-formed products, is made into a final molded product by sticking a urethane foam to it by foaming in situ, and this urethane foam plays the role of a cushion. However, this product having a urethane foam stuck to it has the undesirable drawbacks that the amine compound used for urethane foaming markedly promotes color change of the covering material of vinyl chloride resin, and that urethane raw material is expensive. Further, it is on trial to produce the cushiony covering material by simultaneously and integrally molding the non-foam layer and foam layer by the powder molding method. This powder two-layer molding method is a method in which firstly a powder resin composition containing no foaming agent is fused onto a mold heated to a high temperature, secondly a powder resin composition containing a foaming agent is attached to the mold, and then the mold is kept at a temperature higher than the decomposition temperature of the foaming agent to produce a two-layer molded product, or when the mold cannot be kept at the temperature, the foaming agent is foamed by heating to produce the two-layer molded product. The fundamental principle of this method is known (Japanese Patent Publication No. 11510/1967). In this powder molding, the powder foamable resin composition should be of excellent powder flowability like the powder resin composition. In producing this powder foamable resin composition, there is used a known method of dry-blending a polyvinyl chloride resin with a plasticizer, stabilizer, foaming agent and other auxiliaries by means of a blender or high-speed rotating mixer equipped with a heating jacket. Also, in order to improve the powder flowability, it is well known to add a finely powdered polyvinyl chloride resin and a finely powdered inorganic powder (e.g. calcium carbonate, silica gel) at the cooling step after completion of the dry-blending (Rubber Digest, Vol. 14, No. 8, pp. 32-40; Polyvinyl Chloride-Its Chemistry and Industry II, pp. 367-370, 1968; and Japanese Patent Publication No. 1575/1962). Referring now to the foamable resin composition, it is hitherto known to give foamability to a polyvinyl chloride resin composition by blending a foaming agent (Japanese Patent No. 111337/1986). However, even foams produced with this composition are not always satisfactory in the shape recovery after compression, and also they are low in the percentage of closed cells. In order to solve this problem, blending a crosslinking component is known. For example, a foamable composition comprising a blend of vinyl chloride copolymer containing hydroxyl and carboxyl groups with a crosslinking agent is disclosed in Japanese Patent Publication Nos. 16498/1977, 44588/1977 and 20985/1979, Japanese Patent No. 18665/1978 and Japanese Patent Publication No. 27818/1983. Further, a vinyl chloride foamable composition containing a thermoplastic polyurethane and acrylic resin is disclosed, for example, in Japanses Patent Nos. 141729/1985 and 141730/1985. Further, examples of vinyl chloride foamable composition of which the thermoplastic polyurethane component is a reaction product of a bifunctional polyol with diisocyanate having a hydroxyl group at the terminals of the molecule are disclosed, for example, in Japanese Patent Nos. 18627/1981 and 168924/1982 and Japanese Patent Publication No. 20220/1987. However, these foamable compositions are only a dry-blended product, being too poor in powder flowability to be suitable for the powder molding method, although usable in extrusion molding, calender molding, press molding. An object of the present invention is to solve the foregoing problems of the prior art. The present invention provides a vinyl chloride resin composition for powder molding which contains no coarse agglomerate particles, has powder flowability suitable for powder molding. It can be foamed and its foamability (such as expansion ratio) is excellent and it produces a foam having flexibility and good shape recovery after compression, and a method for producing the same. In order to solve the foregoing requirements, the present inventors have extensively studied a method for producing the vinyl chloride resin composition for powder molding excellent in powder flowability and foamability without forming coarse agglomerate particles. As a result, the present inventors have found that the desired powdery resin composition excellent in powder flowability and foamability can be obtained without forming coarse agglomerate particles by carrying out dry-blending in the following manner : The first step is carried out in which a plasticizer is added to the vinyl chloride resin to allow the resin to absorb the plasticizer, and after the temperature of the mixture reaches a certain particular temperature, the second step is carried out in which at least one particular polymer having an active hydrogen in the molecule and a crosslinkable isocyanate compound are added. The present invention provides a vinyl chloride resin composition for powder molding characterized in that said composition is obtainable by a method of which the fundamental constitution is as follows : The first step is carried out in which from 40 to 120 parts by weight, preferably from 50 to 100 parts by weight, of a plasticizer is blended with 100 parts by weight of a granular vinyl chloride resin obtained by suspension polymerization or bulk polymerization, thereby to allow the resin to absorb the plasticizer, during which it is preferred to add a foaming agent and a stabilizer; the second step is carried out in which from 0.5 to 40 parts by weight, preferably from 1 to 20 parts by weight, of at least one polymer or copolymer having an active hydrogen in the molecule [component (A)] and from 0.1 to 10 parts by weight, preferably from 0.2 to 5 parts by weight, of a crosslinkable isocyanate compound [component (B)] are added and dry-blended, after the temperature has reached 90°C in the course of temperature increase; and while the temperature of the dry-blend system is in the course of cooling after it has reached a maximum temperature (preferably at a temperature lower than 50°C), the third step is carried out in which an amount (e.g. from 3 to 25, preferably from 5 to 20, parts by weight) of a finely powdered vinyl chloride resin obtained by emulsion polymerization or micro-suspension polymerization is added to coat the dry-blend. The compound used as the component (A) is preferably a vinyl chloride copolymer or acrylic polymer having an active hydrogen in the molecule. This copolymer or polymer may be used alone or in combination. When the vinyl chloride copolymer having an active hydrogen in the molecule is used as the component (A), the time of its addition in the second step is selected so that said addition is carried out after the temperature of the dry-blend system has reached 90°C, preferably 100°C in the course of temperature increase. When the acrylic polymer having an active hydrogen in the molecule is used as the component (A), the time of its addition in the second step is selected so that said addition is carried out after the temperature of the dry-blend system reaches 90°C, preferably 100°C in the course of temperature increase and before it falls to 100°C in the course of cooling. The addition of component (B) is carried out after the temperature of the dry-blend system has reached 90°C, preferably 100°C in the course of temperature increase. When the foregoing components are added at a temperature outside the scope of the temperature condition of the present invention, coarse agglomerate particles are easily formed and powder moldability becomes bad, which are not desirable. In the dry-blending process of the present invention, the rate of temperature increase from first to second step is for example 5-20°C/min, preferably 5-12°C/min. The subsequent rate of cooling for example is 5-25°C/min. Every component used in the present invention will be illustrated in detail. As examples of the vinyl chloride resin obtained by suspension polymerization or bulk polymerization, there are mentioned vinyl chloride polymers produced by suspension polymerization or bulk polymerization, copolymers of vinyl chloride with a monomer copolymerizable therewith (e.g. ethylene, propylene, vinyl acetate), graft copolymers of vinyl chloride with an ethylene/vinyl acetate copolymer and a mixture of two or more of these polymers. However, the vinyl chloride resin of the present invention is not limited to those described above. The average particle diameter of the granular vinyl chloride resin obtained by suspension polymerization or bulk polymerization is from 50 to 200 µm, preferably from 80 to 170 µm, more preferably from 100 to 150 µm. As examples of the vinyl chloride copolymer having an active hydrogen in the molecule, there are mentioned copolymers of a vinyl chloride monomer with a monomer having an active hydrogen in the molecule (e.g. a monomer having a hydroxyl, epoxy or carboxyl group) produced by the common suspension polymerization or emulsion polymerization or other known polymerization methods. Representative examples of the copolymer include vinyl chloride copolymer of a vinyl chloride monomer with 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, 3-chloro-2-hydroxypropyl methacrylate, 3-hydroxybutyl acrylate, ethyl-2-hydroxyethyl fumarate, 3-hydroxybutyl vinyl ether, glycidyl acrylate, glycidyl methacrylate, acrylic acid, methacrylic acid, monobutyl maleate and undecylenic acid. These copolymers can be used in an amount of from 0.5 to 25 parts by weight based on 100 parts by weight of the vinyl chloride resin. When the amount is less than 0.5 part by weight, the crosslinking effect is not developed while addition of an amount larger than 25 parts by weight is vain because the crosslinking effect does not change. As the acrylic polymer (A) used in the present invention, there are used elastic copolymers of alkyl acrylate, which is a main component, with a sub-component having an active group acting as a crosslinking point. For example, there are mentioned copolymers comprising as a main component one or more alkyl acrylates (e.g. ethyl acrylate, propyl, acrylate, butyl acrylate, 2-ethylhexyl acrylate) and as a sub-component allyl glycidyl ether, glycidyl acrylate, glycidyl methacrylate, hydroxyethyl acrylate, hydroxyethyl methacrylate and 2-chloroethyl vinyl ether, having an active group acting as a crosslinking point. Particularly, acrylic copolymers having an epoxy or hydroxyl group as an active group are preferably used. The acrylic copolymer can be used in an amount of from 0.5 to 25 parts by weight based on 100 parts by weight of the vinyl chloride resin. When the amount is less than 0.5 part by weight, the crosslinking effect is not developed at the time or molding of the foam, so that shape recovery is poor. The acrylic copolymer improves dispersibility by fusing it onto the surface of the vinyl chloride resin by applying heat. However, when an amount more than 25 parts by weight is added, the powdery composition becomes tacky to worsen the powder flowability. The component (A) may be a combination of the foregoing vinyl chloride copolymer and acrylic polymer having an active hydrogen in the molecule. In this case, the sum of both copolymers is from 0.5 to 40 parts by weight, preferably from 1 to 20 parts by weight. Instead of component (A) described above, saponified products of vinylester polymers or copolymers such as vinylacetate polymer or ethylene-vinylacetate copolymer can be used. As the crosslinkable isocyanate compound (B) used in the present invention, there are mentioned compounds having in the molecule two or more functional groups capable of reacting with the active hydrogen of the polymer (A), for example compounds having an isocyanate or blocked isocyanate group in the molecule. Representative examples of these compounds include : polyisocyanates such as tolylene diisocyanate, diphenylmethane diisocyanate, polymethylenepolyphenyl isocyanate; initial addition polymers of the foregoing polyisocyanates with an at least bifunctional active hydrogen-containing compound (e.g. trimethylolpropane, pentaerythritol, glycerin, polyethylene glycol, polytetramethylene glycol, polyethylene adipate), said polymers having an isocyanate group at the terminal of the molecule; and blocked isocyanates produced by blocking the isocyanate group of the foregoing polyisocyanates and initial addition polymers with phenol, diethyl malonate, acetoacetic acid esters, acetoxime, sodium hydrogensulfite or other masking agents. These crosslinkable isocyanate compounds are used in an amount of from 0.1 to 10 parts by weight, preferably from 0.2 to 5 parts by weight based on 100 parts by weight of the vinyl chloride resin. When the amount is less than 0.1 part by weight, the crosslinking effect is not sufficient, While addition of an amount larger than 10 parts by weight is vain because there is no corresponding increase in effect. In the dry-blending process, the polymer (A) having an active hydrogen in the molecule and the crosslinkable isocyanate compound (B) used in the present invention have to be added after the plasticizer is added to the vinyl chloride resin obtained by suspension polymerization or bulk polymerization, thereby to allow the resin to absorb the plasticizer and the temperature of the blend to reach 90°C, preferably 100°C in the course of temperature increase. When they are added before the temperature of the blend reaches 90°C in the course of temperature increase, absorption of the plasticizer by the vinyl chloride resin obtained by suspension polymerization or bulk polymerization is not sufficient; because of this, the polymer (A) having an active hydrogen in the molecule absorbs the plasticizer to become tacky, and the polymer particles cling to one another to grow into a large amount of coarse agglomerate particles, making it impossible to finally obtain a powder composition having good powder flowability. When such coarse agglomerate particles are present in the powder composition, good molded products cannot be obtained by powder molding; Consequently, such a powder composition has to be screened, for example through a 32-mesh wire net, to separate into a portion which passes through the wire net and a portion which is caught thereon, and the former fine particles are used for powder molding and the latter coarse agglomerate particles need to be discarded. When such coarse agglomerate particles are formed in large amounts, the amount of particles discarded also increases to decrease productivity, which is not desirable. Further, when the polymer having an active hydrogen in the molecule absorbs the plasticizer, the crosslinking effect when the foam is molded later is decreased, which is not desirable. The finely powdered vinyl chloride resin for coating used in the present invention includes vinyl chloride polymer and copolymers of vinyl chloride with a monomer copolymerizable therewith such as ethylene, propylene and vinyl acetate having an average unit particle diameter of from 0.1 to 10 µm produced by emulsion polymerization or micro-suspension polymerization. It is preferred that the finely powdered vinyl chloride resin for coating used in the present invention is added at a temperature lower than 50°C in the course of cooling of the dry-blend. By selecting such temperature conditions, a foamable powder molding composition of excellent powder flowability can be produced. The plasticizer used in the present invention includes phthalic acid esters such as diisodecyl phthalate, diisoundecyl phthalate and dialkyl phthalates having a C₉-C₁₁ alkyl group; and trimellitic acid esters such as trioctyl trimellitate, tri-2-ethylhexyl trimellitate, tridecyl trimellitate, trialkyl trimellitates having a C₇-C₉ or C₇-C₁₁ alkyl group. A small amount of an epoxy or polyester plasticizer may be used, but these plasticizers are not always used. As the foaming agent for the present invention, the common decomposable foaming agents can be used as need arises, without limitation thereto. For example, there are mentioned azodicarbonamide, p,p'-oxybisbenzenesulfonyl hydrazide, p-toluenesulfonyl hydrazide and benzenesulfonyl hydrazide. These compounds may be used alone or in a mixture of two or more of them. Particularly, azodicarbonamide is preferably used. In the present invention, a foaming assistant may be used. The foaming assistant includes inorganic zinc salts (e.g. zinc white, zinc nitrate), zinc/fatty acid soaps (e.g. zinc octoate, zinc stearate) and urea. These compounds may be used alone or in combination of two or more of them. The stabilizer which can be used in the present invention includes the compounds of a metal (e.g. zinc, barium, sodium, potassium, calcium, lithium, tin), for example the salts of a carboxylic acid with these metals. Particularly, composite stabilizers of these metallic compounds, for example carboxylic acid salts, and organic stabilizers such as epoxy compounds are mentioned. In the method for producing the composition of the present invention, fillers and pigments may be added if necessary in addition to the foregoing blending agents. The present invention as claimed will be illustrated more specifically with reference to the following examples: The above suspension-polymerized polyvinyl chloride resin was put in a supermixer and stirred with heating at a definite speed of rotation. When the resin temperature reached 80°C, the foregoing plasticizer, stabilizer and foaming agent were added and dry-blended. At a point when the temperature of the composition reached 120°C, the foregoing crosslinking components were added, and stirring was further continued. At a point when the temperature of the composition reached 125°C, cooling was started, and when the composition was cooled to 50°C, the foregoing finely powdered polyvinyl chloride resin was uniformly dispersed in the composition to obtain a powdery foamable resin composition having a good powder flowability. On screening the resulting composition through a 32-mesh wire net, it was found that the composition which passed through the wire net was 99.5 wt.% and coarse agglomerate particles caught on the wire net was 0.5 wt.%. Using the composition thus obtained, a foamed sheet was prepared by the following method, and the powder flowability of the powder composition and the foamability of the foamed sheet were evaluated according to the following item and method of evaluation. The results are shown in Table 1. A flat nickel mold was pre-heated for 5 minutes in a Geer oven kept at 280°C. The mold temperature at that time was 210°C. Immediately, the foregoing powdery vinyl chloride composition was sprinkled on this mold, and after about 10 seconds, the excess powder composition was removed. The mold was then put in a Geer oven kept at an atmospheric temperature of 240°C and re-heated for 1 minute to carry out foaming. After cooling, the molded product was taken out of the mold to obtain a foamed sheet. The powder composition and the foam were evaluated by the following methods. Item and method of evaluation: (1) Powder flowability 100 Milliliters of the composition was put in the funnel of the bulk specific gravity measuring apparatus described in JIS K 6721, and after the damper was pulled out of the funnel, a time which elapsed from the beginning of falling of the sample from the funnel until completion of the falling was measured in second. (2) Moldability In preparing the foam, the state of attachment of the powder composition to the mold was observed at a point when the composition was sprinkled on the heated mold and then removed therefrom. E (Excellent): Uniform attachment without unevenness in thickness. G (Good): Almost uniform attachment with some degree of unevenness in thickness. SG (Somewhat good): Somewhat nonuniform attachment with fairly unevenness in thickness. P (Poor): Non-uniform attachment with remarkable unevenness in thickness. (3) Expansion ratio Calculated from the following equation: (4) Percentage of closed cells The percentage of open cells was measured by means of Beckman's air-comparison pycnometer model 930, and the percentage of closed cells was calculated according to the following equation: (5) Shape recovery after compression The foam was completely pressed with a finger for 10 seconds, and the state of recovery after release of the pressure was judged macroscopically. E (Excellent): Immediate shape recovery after release of pressure without leaving traces. G (Good): Shape recoverly within 5 seconds with traces remaining. SG (Somewhat good): Shape recoverly within 10 seconds with traces remaining. P (Poor): No shape recovery even after 10 seconds with traces remaining. Examples 2 to 4 and Comparative examples 1 to 4 Using the same blending agents as used in Example 1, various powdery compositions were prepared in the same manner as in Example 1 except that there were changed the amount of each blending agent and the temperature at which the corsslinking component was added. Every powdery composition was screened through a 32-mesh wire net, and the amount of coarse agglomerate particles left on the wire net at that time was measured. The amount is shown in wt.% in Tables 1 and 2. Further, the powdery compositions and foamed sheets obtained in the same manner as in Example 1 were evaluated for the powder flowability and foamability, respectively. The results are shown in Tables 1 and 2. The above suspension-polymerized polyvinyl chloride resin was put in a supermixer and stirred with heating at a definite speed of rotation. When the resin temperature reached 80°C, the foregoing plasticizer, stabilizer and foaming agent were added and dry-blended. At a point when the temperature of the composition reached 120°C, the foregoing crosslinking components were added, and stirring was further continued. At a point when the temperature of the composition reached 125°C, cooling was started, and when the composition was cooled to 50°C, the foregoing finely powdered polyvinyl chloride resin was uniformly dispersed in the composition to obtain a powdery foamable resin composition having a good powder flowability. Using the composition thus obtained, a foamed sheet was prepared by the following method and evaluated. The results are shown in Table 3. A flat nickel mold was pre-heated for 5 minutes in a Geer oven kept at 280°C. The mold temperature at that time was about 210°C. Immediately, the foregoing powdery vinyl chloride composition was sprinkled on this mold, and after about 10 seconds, the excess powder composition was removed. The mold was then put in a Geer oven kept at an atmospheric temperature of 240°C and re-heated for 1 minute to carry out foaming. After cooling, the molded product was taken out of the mold to obtain a foamed sheet. Examples 6 to 12 and Comparative examples 5 to 8 Using the same crosslinking components as used in Example 5, various powdery compositions were prepared in the same manner as in Example 5 except that there were changed the amounts of the crosslinking components and the temperature at which the components were added. Foams were prepared and evaluated by the same method as in Example 5. The results are shown in Tables 3 and 4. The vinyl chloride copolymer having an active hydrogen in the molecule used in Examples and Comparative examples was a vinyl chloride/2-hydroxypropyl acrylate copolymer.

Claims: A vinyl chloride resin composition for powder molding which is obtainable by a method comprising a first step in which from 40 to 120 parts by weight of plasticizer is blended with 100 parts by weight of granular vinyl chloride resin obtainable by suspension or bulk polymerisation; a second step in which from 0.5 to 40 parts by weight of at least one polymer or copolymer having an active hydrogen in the molecule [component (A)] and from 0.1 to 10 parts by weight of crosslinkable isocyanate compound [component (B)] are added and dry-blended after the temperature of the blend has reached 90°C in the course of temperature increase; and a third step in which while the dry-blend system is cooling from a maximum temperature, finely powdered vinyl chloride resin obtainable by emulsion or micro-suspension polymerisation is added to coat the dry-blend; acrylic polymer when present as or in component (A) amounting to no more than 25 parts by weight. A method for producing a vinyl chloride resin composition for powder molding which comprises a first step in which from 40 to 120 parts by weight of plasticizer is blended with 100 parts by weight of granular vinyl chloride resin obtainable by suspension or bulk polymerisation; a second step in which from 0.5 to 40 parts by weight of at least one polymer or copolymer having an active hydrogen in the molecule [component (A)] and from 0.1 to 10 parts by weight of crosslinkable isocyanate compound [component (B)] are added and dry-blended after the temperature of the blend has reached 90°C in the course of temperature increase; and a third step in which, while the dry-blend system is cooling from a maximum temperature, finely powdered vinyl chloride resin obtainable by emulsion or micro-suspension polymerisation is added to coat the dry-blend; acrylic polymer when present as or in component (A) amounting to no more than 25 parts by weight. A method according to claim 2 wherein component (A) is selected from vinyl chloride copolymers and acrylic polymers. A method according to claim 3 wherein after the temperature of the system has reached 90°C in the course of temperature increase and before it falls to 100°C in the course of cooling, the second step is carried out in which acrylic copolymer having an active hydrogen in the molecule [component (A)] is blended with the system. A method according to any of claims 2 to 4 wherein the third step is carried out when the temperature of the dry-blend system has fallen to a temperature lower than 50°C. A method according to any of claims 2 to 5 wherein from 3 to 25 parts by weight of the finely powdered resin are added in the third step. A composition obtainable by the method of any of claims 2 to 6 including foaming agent.

Inventors: MATSUURA, ISAO, SHIDA, YUU, WAKATSUKI, AKIRA
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1988
Main classification: C08L27
IPC codes: C08J3, C08K5, C08L75, C08L27