CATALYST CARRIERS AND A PROCESS FOR PRODUCING THE SAME

Abstract: A catalyst carrier comprise a substrate made of a material selected from a stainless steel and a nickel base alloy both at least containing 0.2 to 0.8 wt% of Ti and 0.01 to 0.5 wt% of C, and an alumina thin layer firmly bonded onto the surface of the substrate by Aℓ-O-Ti-C bonds, said catalyst carrier being shaped in the form of a porous body having gas permeability in at least one direction. The alumina thin layer may be firmly bonded by Aℓ-O-Ti-C bonds to the surface of the substrate having an aluminum-iron alloy layer or an aluminum-nickel alloy layer. The alumina thin layer is formed by heat treating alumina coated onto the surface of substrate at 600 to 1,000°C for not less than 10 minutes. Instead of the coating with alumina, aluminum may be plated onto the surface of the substrate for this purpose.

Description: The present invention relates to catalyst carriers made of a metallic material (hereinafter referred to as "metallic catalyst carriers") to be used for purification catalysts to purify combustion waste gases exhausted from automobiles and factories. The invention also relates to a process for producing such catalyst carriers. JP-A-56-96,726 discloses a technique using, as metallic catalyst carriers, a foil made of an aluminum-containing ferrite type stainless steel in which alumina whiskers are formed on surfaces of the foil through heat treatment. According to this technique, a stainless steel which can withstand high temperatures is used, and the alumina whiskers are present on its surface. Therefore, when γ-Aℓ₂O₃ or the like is carried on such a catalyst carrier as a wash coat, the alumina whiskers function as wedges. Thus, the wash coat layer made of γ-Aℓ₂O₃ or the like can firmly be adhered to the metallic catalyst carrier. However, since the ferrite type stainless steel as the substrate contains not less than 3% by weight of aluminum, its plastic deformability is extremely poor. Thus, it takes many steps to obtain a foil of the stainless steel of this kind. It is an object of the present invention to diminish the above-mentioned problems, and to provide catalyst carriers in which a metal substrate and an alumina thin layer are firmly bonded and which have good plastic deformability. It is a further object of the present invention to provide a process for producing such catalyst carriers. According to a first aspect, the present invention provides a catalyst carrier as set out in claim 1. Processes for producing catalyst carriers according to the present invention are set out in claims 6 and 9. In the process of claim 6, the substrate may be converted into the porous body before or after the steps of forming the alumina coating and heat treating. In the catalyst carrier of claim 1, since Ti and C are present in the nickel base alloy as the substrate in the respectively specified amounts, the tough Aℓ-O-Ti-C bonds can be formed at the interface through the reaction between the alumina thin layer provided on the surface of the substrate and TiC (titanium carbide) precipitated in the metal by the heat treatment. Consequently, the alumina thin layer can firmly be bonded to the carrier substrate by the chemical bonds. Further, the alumina thin layer which has equal or more excellent performance as compared with the alumina whiskers is formed by heat treating the alumina thin layer without the addition of a certain amount of Aℓ into the substrate for producing the alumina whiskers unlike the prior art. Thus, the plastic deformability is kept undeteriorated. In one process of the present invention, Ti and C are present in the nickel base alloy as the substrate in the respectively specific amounts, and the aluminum plated onto the surface of the substrate is oxidized by heat treatment in air. Thereby, an alumina thin layer is formed on the substrate through the aluminum-nickel alloy layer, and reacts with TiC (titanium carbide) precipitated in the metal, so that the tough Aℓ-O-Ti-C bonds are formed at the interface. Thus, the firm bonding between the metal substrate and the alumina thin layer can be obtained by the chemical bonding. Further, the chemically bonded alumina thin layer which has equal or more excellent performance as compared with the alumina whiskers is formed by heat treating the plated aluminum layer formed on the substrate without the addition of a certain amount of Aℓ into the substrate for producing the alumina whiskers unlike the prior art. Thus, the plastic deformability is kept undeteriorated. Furthermore, when the substrate is plated with aluminum, a pretreatment such as coarsening of the surface of the substrate to be plated is unnecessary unlike the alumina coating. Accordingly, the production process can be simplified. In addition, since the plated aluminum layer is heat treated, the aluminum-nickel alloy layer is produced between the plated aluminum layer and the substrate made of the Ni base alloy owing to the diffusion of aluminum into the substrate. Consequently, the alumina thin layer is firmly bonded to the surface of the substrate by the Aℓ-O-Ti-C bonds. For a better understanding of the invention, reference is made to the attached drawings, wherein: Figs. 1 through 4 are flow charts explaining examples of a first process for producing the catalyst carriers according to the present invention; Fig. 5 is a flow chart illustrating an example of a second process for producing the catalyst carriers according to the present invention; Figs. 6 through 9 are schematic perspective views of embodiments of the catalyst carriers according to the present invention; and Figs. 10 and 11 are schematic sectional views of parts of catalyst carriers according to the present invention. First, numerical limitations made in the present invention will be explained below. The reasons for limiting the addition amounts of Ti and C are as follows: If the content of Ti is less than 0.2 wt% or if that of C is less than 0.01 wt%, as is clear from Experiments mentioned later, the alumina thin layer is peeled. Thus, the respectively lower limits are imposed upon the contents of Ti and C. This peeling is considered to be caused because sufficient Aℓ-O-Ti-C bonds are not formed due to smaller addition amounts of Ti and C. In contrast, if the content of C exceeds 0.5 wt%, carbon precipitates in the form of graphite at the interface between the metal substrate and the alumina film layer. Consequently, the alumina film layer becomes brittle, and is likely to be peeled. Furthermore, if the content of Ti exceeds 0.8 wt%, the thickness of a TiC bonding layer increases due to repeated heat treatment. When the thickness of this layer becomes greater, the alumina thin layer is also likely to be peeled due to excessive hardness of bonding phase. For the above reasons, Ti is limited to 0.2 to 0.8 wt%, while C is to 0.01 to 0.5 wt%. The reason why the heat treatment is preferably limited to a range from 600 to 1,000°C and not less than 10 minutes in the case of the first aspect of the present invention is as follows: If the temperature is less than 600°C, sufficient bonding strengthmay not be obtained between the metal substrate and the alumina thin layer. On the other hand, if it is more than 1,000°C, the alumina thin layer is likely to be peeled because of rapid formation of the Aℓ-O-Ti-C bonds. If the heat treating time is less than 10 minutes, the Aℓ-O-Ti-C bonds are not sufficiently formed and improvement of the bonding strength is not recognized. Therefore, the heat treating conditions are limited to the temperature range from 600 to 1,000°C and not less than 10 minutes. The above discussion on the limitations of the heat treating conditions is similarly applicable to the second aspect of the present invention. That is, if the temperature is less than 600°C, it takes a very long time to form the Aℓ-O-Ti-C bonds, and sufficient bonding strength at interface cannot be obtained. Thus, less than 600°C is impractical. On the other hand, if the temperature is more than 1,000°C, the alumina thin layer is likely to be peeled because of rapid formation of the aluminum-nickel alloy layer. If the heat treating time is less than 10 minutes, the Aℓ-O-Ti-C bonds are not sufficiently formed and improvement of the bonding strength is not recognized. Therefore, the heat treating conditions are limited to the temperature range from 600 to 1,000°C and the heating time of not less than 10 minutes. In the present invention as set out in claim 6, the thickness of the alumina thin layer is preferably in a range from 0.1 to 5.0 µm for the following reasons. That is, as is seen from the experiments mentioned later, if the thickness of the alumina thin layer is more than 5.0 µm, the layer is likely to be peeled due to influence of the difference in thermal expansion, while if it is less than 0.1 µm, no sufficient thickness of the alumina thin layer can be obtained. Consequently, the alumina thin layer does not function as a primary coat for attaching the wash coat onto the substrate. In the case of the present invention as set out in claim 9, the thickness of the plated aluminum layer is preferably in a range from 1 to 10 µm for the following reasons. That is, as is seen from the experiments mentioned later, if the thickness of the plated aluminum layer exceeds 10 µm, the alumina thin layer is likely to be peeled due to influence of the difference of thermal expansion. On the other hand, it is very difficult to control the thickness of plated aluminum layer when thickness is less than 1 µm. Next, preferred examples of the respective constituent features of the present invention will be explained in more detail. Unless otherwise referred to the following discussion will be applicable to all processes of the present invention. (1) Substrate: a) As the shape of the substrate in the present invention as set out in claim 6, those given in Table 1 are preferably used. In the invention as set out in claim 9, the first row (Strip sheet) in Table 1 is preferably employed. b) Composition range of the Ni base alloy (Units are all "%" by weight): It is preferable that the Ni base alloy is composed of indispensable ingredients and additive elements given in the following Table 2. Among the Ni base alloys, the following ones having compositions shown in Table 3 are recited as preferred. (2) Shape of the porous body: As given in the following Table 4, preferred shapes of the porous bodies for the substrates are present in the present invention as set out in claim 6. In the case of the present invention as set out in claim 9, the first row ("Strip") is preferably employed. Substrate Shape of porous body Strip A porous body is shaped by corrugating a thin strip of 0.03 to 0.50 mm in thickness and shaping it to form numerous through holes in an axial direction. A porous body is shaped by preliminarily embossing, perforating, or finely corrugating a thin strip of 0.03 to 0.50 mm in thickness, further corrugating and shaping it to form numerous through holes in an axial direction. Pipe A porous body is shaped by bundling pipe-like substrates (0.03-0.50 mm thickness and 0.5-5.0 mm in diameter). Wire A gas permeable porous body is formed from a metallic knit in which metal wires of 0.03-0.50 mm in diameter are knitted as fibers. A gas permeable porous body is formed by twisting metal wires of 0.030-0.50 mm in diameter. (3) Alumina thin layer: The alumina thin layer is mainly composed of not less than 60 wt% of alumina, and as is clear from the experiments mentioned later, the thickness thereof is preferably in a range from 0.1 to 5.0 µm. The alumina thin layer may be formed by coating an alumina slurry onto the substrate by dipping or spraying it with an alumina colloidal solution, an aluminum alkoxide solution, or an alumina suspension liquid, drying the coated substrate at 150 to 400°C for not less than 30 minutes, and then heat treating the dried substrate at 600 to 1,000°C for not less than 10 minutes as specified above. (4) Aℓ-O-Ti-C bonding layer: After the specified heat treatment, the Aℓ-O-Ti-C bonding layer having a thickness of not more than 0.5 µm is present at the interface between the metal substrate and the alumina film. This is because Ti atoms in the metal substrate are diffused into a surface layer by heating to form TiC, Ti atoms in the metal substrate are bonded to O atoms in the alumina to form the Aℓ-O-Ti-C bond, and the firm chemical bonding is formed. (5) Plated aluminum layer: The plated aluminum layer is mainly composed of not less than 80 wt% of aluminum. As is clear from the experiments mentioned later, its thickness is in a range from 1 to 10 µm. The plated aluminum layer may be formed by a conventional technique such as a hot dipping in a molten aluminum bath. Now, the present invention as set out in claim 6 will be explained in more detail. As mentioned above, the Aℓ-O-Ti-C bonds in the present invention may be obtained by coating the surface of the substrate having the specified composition and made of the nickel base alloy at least containing 0.2 to 0.8 wt% of Ti and 0.01 to 0.5 wt% of C with alumina, and heat treating the thus coated substrate at 600 to 1,000°C for not less than 10 minutes. The following four processes are advantageously employed for practically producing products. Figs. 1 through 4 are flow charts showing examples of the production process for producing the catalyst carriers according to the first aspect of the present invention. In the flow chart of Fig. 1, a corrugated honeycomb carrier is produced from a metal strip. First, the metal strip having a given composition is prepared. The metal strip may be produced by using a conventional technique such as cold rolling. Next, the metal strip is converted to a corrugated foil. The corrugated foil is piled upon a flat metal strip, which is then coiled to form a honeycomb substrate. The thus obtained honeycomb substrate is coated with alumina under desired conditions, which is heat treated under the above-mentioned conditions to form an Aℓ-O-Ti-C bonding at an interface between the metal substrate and the alumina film layer. Thereby, a honeycomb catalyst carrier having gas permeability in at least one direction is obtained. The flow chart of Fig. 2 shows a modification of the process in Fig. 1 for producing the catalyst carrier from a metal strip. In Fig. 2, after the metal strip is similarly prepared, the strip is subjected first to coating with alumina and then to the above-mentioned heat treatment, thereby forming an Aℓ-O-Ti-C bonding. Next, the thus treated strip is converted to a corrugated foil, and a honeycomb catalyst carrier having gas permeability in at least one direction is obtained as a honeycomb substrate in the same manner as in Fig. 1. In this process, the alumina coating step is simplified and the productivity is improved as compared with the process illustrated in the flow chart of Fig. 1. Fig. 6 illustrates the above production process, and Fig. 10 schematically shows a side portions of the foils encircled in Fig. 6. In Fig. 6, A and A' denote the flat and corrugated foils, respectively. In Fig. 10, reference numerals 1, 2 and 3 denote nickel base alloy, an alumina thin layer, and an Aℓ-O-Ti-C bonding, respectively. The flow chart of Fig. 3 illustrates a process for producing a honeycomb catalyst carrier from pipe-like substrates. First, the pipe-like substrates having a given composition are prepared. The pipe-like substrates may be produced by using a conventional technique. Next, the entire inner and outer surfaces of each of the pipe-like substrates are coated with alumina, and the pipe is heated under specific conditions to form an Aℓ-O-Ti-C bonding at the interface between the pipe-like substrate and the alumina film layer. Finally, a honeycomb catalyst carrier having gas permeability in at least one direction is obtained by bundling the heat treated pipe-like substrates together. With respect to this process, a modified process may be employed. That is, pipe-like substrates are first bundled together, coated with alumina, and then heat treated under given conditions, thereby obtaining a honeycomb catalyst carrier. Fig. 7 illustrates such a honeycomb catalyst carrier. This catalyst carrier also has the layer structure as shown in Fig. 10 with respect to the constituting pipes. The flow chart of Fig. 4 illustrates a process for producing a porous body having a given configuration from wire substrates. First, the wire substrates having a given composition are prepared. The wire substrates may be produced by a conventional technique. Then, the wire substrates are knitted to form a knitted substrate, or they are twisted to form a combined wire substrate. The knitted substrate or the combined wire substrate is formed in a given shape. Thus, a catalyst carrier having gas permeability in at least one direction is obtained in the form of a porous body in the same manner as in the aforementioned processes. Figs. 8 and 9 illustrate such honeycomb catalyst carriers. The wire substrates of the honeycomb catalyst carriers also have the layer structure as shown in Fig. 10. In the following, with respect to the bonding between the substrate and the alumina thin layer in the the present invention as set out in claim 6, actual examples will be explained. Experiments In order to prepare metal strip for substrates, an ingot was prepared by melting a Ni base alloy formulated at a given composition shown in Tables 5 in a vacuum melting furnace. The obtained ingot having the given composition was subjected to hot rolling, and then repeatedly to cold rolling and annealing, thereby obtaining a metal strip of about 0.5 mm in thickness. The metal strip was cut into square test substrates having 100 mm long sides as test pieces. Then, an alumina film was coated onto each of the test substrates in the following procedures. First, a coating solution was prepared by dissolving aluminum isopropoxide into hot water (not less than 75°C) and adjusting the resulting solution to weakly acidic with nitric acid. Then, the metal substrate was preliminarily treated in a mixed acid solution containing 10% of nitric acid and 2% of fluoric acid for 10 minutes, and then washed with water. The preliminarily treated metal substrate was dipped into the above-prepared coating solution for effecting the coating. With respect to all the test substrates, the thickness of the coat was adjusted to 3 µm by controlling the pulling speed and the number of dipping times. Finally, the coated metal substrate was dried in an electric furnace by heating it at a heating rate of 2.5°C/min, and then by maintaining it at 350°C for 30 minutes. Thereafter, the substrates on which the alumina film layer was coated were heat treated. In the heat treatment, Aℓ-O-Ti-C bonds were formed by heating the substrates at 900°C in the electric furnace for 15 minutes, thereby obtaining test pieces. In order to evaluate characteristics, the thus obtained test pieces were subjected to thermal shock tests through cooling and heating by using a device for putting them into the electric furnace at 900°C in air and extracting them therefrom. The test cycling was 500 cycles between 900°C for 15 minutes in air and room temperature for 45 minutes. The surface state of the test pieces was observed by naked eyes. With respect to the catalyst carriers using the Ni base alloy, results are given in Table 5, respectively. It is seen from Table 5 that the test substrates satisfying the composition ranges of Ti and C in the present invention exhibited completely no abnormality in the thermal shock tests, while the alumina thin layers were partially peeled in case of those not satisfying the composition ranges of Ti and C in the present invention. Then, with respect to substrates made of the Ni base alloy satisfying the composition ranges in the present invention respectively, thermal shock tests were similarly conducted while the thickness of the alumina film layer was varied. Results are shown in Table 6. It is seen from the results in Table 6 that the thickness is preferably not more than 5.0 µm. Furthermore, substrates made of the Ni base alloy satisfying the composition ranges in the present invention among the above-mentioned ones were heated in a temperature range of 500 to 1,000°C for various time periods, and were subjected to lattice-cut tests according to JIS K 5400. Then, their adhesion states were checked. In the tests, the thickness of the alumina coating layer was adjusted to 3 µm for all the substrates. Results are shown in Table 7. As is clear from the foregoing explanation, according to the catalyst carrier of the invention and the production process therefor set out in claim 6, since the specified amounts of Ti and C are contained in the metal substrate, chemically strong Aℓ-O-Ti-C bonding is formed between the metal substrate and the alumina thin layer. Thus, the alumina thin layer can firmly be bonded to the substrate. Further, an alumina thin layer having equal or higher strength as compared with the alumina whiskers is produced by heating and oxidizing the alumina coating layer without the addition of Aℓ in the substrate for producing the aluminum whiskers. Therefore, the catalyst carrier, which has gas permeability in at least one given direction and which is useful to purify a variety of combustion waste gases, can be obtained without deteriorating the plastic deformability. Next, the process of the present invention as set out in claim 9 will be explained in more detail. As mentioned above, the Aℓ-O-Ti-C bonds in the present invention will be obtained by plating the surface of the substrate having the specified composition and made of the nickel base alloy at least containing 0.2 wt% to 0.8 wt% of Ti and 0.01 to 0.5 wt% of C with aluminum, and heat treating the thus coated substrate at 600 to 1,000°C for 10 minutes so that the plated aluminum is oxidized to form alumina and that the Aℓ-O-Ti-C bonds are formed through the aluminum-nickel alloy layer. However, the following process is advantageously employed for practically producing products. Fig. 5 shows a flow chart of an example of the process for producing the catalyst carriers according to the second aspect of the present invention. In the flow chart of Fig. 5, a corrugated honeycomb carrier is produced from a metal strip. First, the metal strip having a given composition is prepared. The metal strip may be produced by using a conventional technique such as rolling. Next, the surface of the thus obtained metal strip is plated with aluminum in a given thickness, and the plated substrate is cold rolled to obtain a metal foil. The obtained metal foil is converted to a corrugated foil, and piled upon a flat metal foil, which is then coiled to obtain a honeycomb substrate as shown in Fig. 7. The honeycomb substrate is heated under given conditions, so that the plated aluminum layer is converted to an alumina thin layer and aluminum-nickel alloy layer, and that the Aℓ-O-Ti-C bonding is formed at the interface between the metal substrate and the alumina thin layer. Thereby, a honeycomb catalyst carrier which contains an aluminum-nickel alloy layer and which has gas permeability in at least one direction is obtained. Fig. 12 schematically illustrates a side portion of the foil in which reference numerals 1, 2, 3 and 4 denote nickel base alloy, an alumina thin layer, an Aℓ-O-Ti-C bonding, and an aluminum-nickel alloy layer, respectively. In the following, with respect to the bonding between the substrate and the alumina thin layer, actual examples will be explained. Experiments In order to prepare a metal strip for substrates, an ingot was prepared by melting a Ni base alloy formulated at a given composition shown in Table 5 in a vacuums melting furnace. The obtained ingot having the given composition was subjected to hot rolling, and then repeatedly to cold rolling and annealing, thereby obtaining a metal strip of about 1 mm in thickness. The metal strip was cut into test substrates of 100 x 500 mm. Then, each of the test substrates was plated with aluminum in the following procedures. First, aluminum alloy containing 8 wt% of Si was prepared for hot dipping in a molten aluminum bath. Then, the metal substrate was preliminarily cleaned with a mixed acid solution containing 10 wt% of nitric acid and 2 wt% of fluoric acid for about 10 minutes, and washed with water. The preliminarily cleaned metal substrate was dipped into the molten aluminum bath above prepared, and an amount of aluminum attached was adjusted by gas wiping. The thickness of the plated layer was further adjusted by rolling the hot-dipped substrate. The substrate was cut into square test substrates having 100 mm long sides. The thickness of the plated layer was 5 µm for all the test substrates. Thereafter, the test substrate on which the plated aluminum layer was formed was heat treated. The heat treatment was carried out by heating the plated test substrate in an electric furnace at 800°C for 30 minutes in air. The characteristics of the test substrates were evaluated by the heat cycling test in the same manner as in the experiments for the present invention as set out in claim 6. Obtained results were the same as those given in Table 5. It is seen from table 5 that the test substrates satisfying the composition ranges of Ti and C in the present invention exhibited completely no abnormality in the thermal shock tests, while the alumina thin layer was partially peeled in case of the test substrates not satisfying the composition ranges of the present invention. Then, among the above test pieces, those made of the Ni base alloy satisfying the composition ranges in the present invention were subjected to thermal shock tests, while the thickness of the alumina thin layer was varied. Results obtained are shown in Table 8. It is seen from the results in Table 8 that the thickness of the plated aluminum layer is preferably not less than 10 µm. Furthermore, substrates made of the Ni base alloy satisfying the composition ranges in the present invention among the above-mentioned runs were treated at temperatures of 500 to 1,000°C for various time periods, and their sectional faces were observed through a microscope to examine the heat treating conditions. At that time, the thickness of the plated aluminum layer was 5 µm for all the test substrates. Results are shown in Table 9. As is seen from the results in Table 9, it is necessary that the heat treating conditions required for completing the alloying are 600 to 1,000°C and not less than 10 minutes. As is clear from the foregoing explanation, according to the catalyst carrier of the invention and the producing process thereof as set out in claim 9, since the specified amounts of Ti and C are contained in the metal substrate, chemically strong Aℓ-O-Ti-C bonding is formed between the metal substrate and the alumina thin layer. Thus, the alumina thin layer can firmly be bonded to the substrate. Further, the alumina thin layer having equal or higher strength is produced by heat treating the plated aluminum layer without the addition of a certain amount of Aℓ into the substrate unlike the prior art to produce the alumina whiskers. Therefore, the catalyst carrier, which has gas permeability in at least one given direction and which is useful to purify a variety of combustion waste gases, can be obtained by simple steps without deteriorating the plastic deformability.

Claims: A catalyst carrier comprising a substrate made of a nickel base alloy, said alloy containing at least 0.2 to 0.8 wt% of Ti and 0.01 to 0.5 wt% of C, and an alumina thin layer firmly bonded onto a surface of the substrate by Al-O-Ti-C bonds either directly to the nickel alloy or to an aluminium-nickel alloy layer formed at the surface of the nickel alloy said catalyst carrier being shaped in the form of a porous body having gas permeability in at least one direction. A catalyst carrier according to claim 1, wherein a thickness of the alumina thin layer is in a range from 0.1 to 5.0µm. A catalyst carrier according to claim 1 or 2, wherein the Ni base alloy consists of 0.2 to 0.8 wt% of Ti, 0.01 to 0.5 wt% of C, 20 to 65 wt% of Cr+Fe+Mo in a total amount, 0 to 10 wt% of Mn, 0 to 5 wt% of Si, 0 to 5 wt% of V, 0 to 5 wt% of Co, 0 to 3 wt% of Al, 0 to 3 wt% of Cu, 0 to 3 wt% of Be, 0 to 1 wt% of Zr, 0 to 3 wt% of Y, 0 to 3 wt% of Ce, and the balance being Ni and unavoidable impurities. A catalyst carrier according to claim 1 or 2, wherein the Ni base alloy is one selected from the group consisting of: a) a Ni base alloy consisting of 0.4 to 0.7 wt% of Ti, 15 to 23 wt% of Cr, not more than 1.00 wt% of Si, not more than 1.50 wt% of Al, 0.015 to 0.15 st% of C, 8 to 15 wt% of Fe, not more than 1.00 wt% of Mn, and the balance being Ni and unavoidable impurities ; b) a Ni base alloy consisting of 0.4 to 0.7 wt% of Ti, 48 to 62 wt% of Cr, not more than 1.00 wt% of Mn, 0.015 to 0.15 wt% of C, not more than 1.00 wt% of Si, 9.0 to 13.0 wt% of Fe, and the balance being Ni and unavoidable impurities ; c) a Ni base alloy consisting of 0.4 to 0.7 wt% of Ti, not more than 1.00 wt% of Cr, not more than 1.00 wt% of Mn, 26 to 30 wt% of Mo, 0.015 to 0.15 wt% of C, not more than 1.00 wt% of Si, 3.0 to 6.0 wt% of Fe, and the balance being Ni and unavoidable impurities ; d) a Ni base alloy consisting of 0.4 to 0.7 wt% of Ti, 14.5 to 16.5 wt% of Cr, not more than 1.00 wt% of Mn, not more than 2.5 wt% of Co, 0.015 to 0.15 wt% of C, not more than 1.00 wt% of Si, 4.0 to 7.0 of Fe, 15 to 18 wt% of Mo, and the balance being Ni and unavoidable impurities ; e) a Ni base alloy consisting of 0.4 to 0.7 wt% of Ti, 0.015 to 0.15 wt% of C, and the balance being Ni and unavoidable impurities. A catalyst carrier according to any one of claims 1 to 4, wherein the porous body is in the form of a corrugated roll, a bundle of pipes, or twisted wire. A process for producing a catalyst carrier comprising: a) preparing a nickel base alloy substrate, each containing at least 0.2 to 0.8 wt% of the Ti and 0.01 to 0.5 wt% of C; b) forming an alumina coating on the substrate; c) heat treating the coated substrate at 600 to 1000°C for not less than 10 minutes to form an alumina thin layer bonded to the surface of the substrate by Al-O-Ti-C bonds either directly to the nickel alloy or to an aluminium-nickel alloy layer formed at the surface of the substrate; and d) converting either the substrate from (a) or the heat treated substrate from (c) into a porous body having gas permeability in at least one direction. A process according to claim 6 in which the substrate is prepared in the form of a metal strip which is corrugated in stage (d). A process according to clam 6 in which the substrate is prepared in the form of a bundle of pipes or twisted or knitted wire. A process for producing a catalyst carrier, comprising the steps of: a) preparing a metal strip of a nickel base alloy containing at least 0.2 to 0.8 wt% of Ti and 0.01 to 0.5 wt% of C, b) plating a surface of the metal strip with aluminium; c) cold rolling the plated metal strip, d) converting the cold rolled metal strip to a corrugated porous body having gas permeability in at least one direction; and e) forming an alumina thin layer firmly bonded by Al-O-Ti-C bonds onto the surface of the porous body made of the metal strip containing an aluminium-nickel alloy by heat treating the porous body at 600 to 1000°C for not less than 10 minutes.

Inventors: SHIBATA, MOTONOBU
Applicants: SHIBATA, MOTONOBU
Application year: 1988
Main classification: B01J37
IPC codes: B01J37, B01J23, F01N3, B01D53, B01J35, B01J32